Novel design of highly [110]-oriented barium titanate nanorod array and its application in nanocomposite capacitors.

PubMed

Yao, Lingmin; Pan, Zhongbin; Zhai, Jiwei; Chen, Haydn H D

2017-03-23

Nanocomposites in capacitors combining highly aligned one dimension ferroelectric nanowires with polymer would be more desirable for achieving higher energy density. However, the synthesis of the well-isolated ferroelectric oxide nanorod arrays with a high orientation has been rather scant, especially using glass-made substrates. In this study, a novel design that is capable of fabricating a highly [110]-oriented BaTiO 3 (BT) nanorod array was proposed first, using a three-step hydrothermal reaction on glass-made substrates. The details for controlling the dispersion of the nanorod array, the orientation and the aspect ratio are also discussed. It is found that the alkaline treatment of the TiO 2 (TO) nanorod array, rather than the completing transformation into sodium titanate, favors the transformation of the TO into the BT nanorod array, as well as protecting the glass-made substrate. The dispersity of the nanorod array can be controlled by the introduction of a glycol ether-deionized water mixed solvent and soluble salts. Moreover, the orientation of the nanorod arrays could be tuned by the ionic strength of the solution. This novel BT nanorod array was used as a filler in a nanocomposite capacitor, demonstrating that a large energy density (11.82 J cm -3 ) can be achieved even at a low applied electric field (3200 kV cm -1 ), which opens us a new application in nanocomposite capacitors.

Vertically aligned diamond-graphite hybrid nanorod arrays with superior field electron emission properties

NASA Astrophysics Data System (ADS)

Ramaneti, R.; Sankaran, K. J.; Korneychuk, S.; Yeh, C. J.; Degutis, G.; Leou, K. C.; Verbeeck, J.; Van Bael, M. K.; Lin, I. N.; Haenen, K.

2017-06-01

A "patterned-seeding technique" in combination with a "nanodiamond masked reactive ion etching process" is demonstrated for fabricating vertically aligned diamond-graphite hybrid (DGH) nanorod arrays. The DGH nanorod arrays possess superior field electron emission (FEE) behavior with a low turn-on field, long lifetime stability, and large field enhancement factor. Such an enhanced FEE is attributed to the nanocomposite nature of the DGH nanorods, which contain sp2-graphitic phases in the boundaries of nano-sized diamond grains. The simplicity in the nanorod fabrication process renders the DGH nanorods of greater potential for the applications as cathodes in field emission displays and microplasma display devices.

The use of silver nanorod array based surface enhanced Raman scattering sensor for food safety applications

USDA-ARS?s Scientific Manuscript database

For the advancement of preventive strategies, it is critical to develop rapid and sensitive detection methods with nanotechnology for food safety applications. This article reports the recent development on the use of aligned silver nanorod (AgNR) arrays prepared by oblique angle deposition, as surf...

Photodeposition of Ag2S on TiO2 nanorod arrays for quantum dot-sensitized solar cells

PubMed Central

2013-01-01

Ag2S quantum dots were deposited on the surface of TiO2 nanorod arrays by a two-step photodeposition. The prepared TiO2 nanorod arrays as well as the Ag2S deposited electrodes were characterized by X-ray diffraction, scanning electron microscope, and transmission electron microscope, suggesting a large coverage of Ag2S quantum dots on the ordered TiO2 nanorod arrays. UV–vis absorption spectra of Ag2S deposited electrodes show a broad absorption range of the visible light. The quantum dot-sensitized solar cells (QDSSCs) based on these electrodes were fabricated, and the photoelectrochemical properties were examined. A high photocurrent density of 10.25 mA/cm2 with a conversion efficiency of 0.98% at AM 1.5 solar light of 100 mW/cm2 was obtained with an optimal photodeposition time. The performance of the QDSSC at different incident light intensities was also investigated. The results display a better performance at a lower incident light level with a conversion efficiency of 1.25% at 47 mW/cm2. PMID:23286551

Multi-angle ZnO microstructures grown on Ag nanorods array for plasmon-enhanced near-UV-blue light emitter

NASA Astrophysics Data System (ADS)

Pal, Anil Kumar; Bharathi Mohan, D.

2017-10-01

Metal enhanced ultraviolet light emission has been explored in ZnO/Ag hybrid structures prepared by hydrothermal growth of multi-angled ZnO nanorods on slanted Ag nanorods array fabricated by the thermal evaporation technique. Slanted Ag nanorods are realized to be the stacking of non-spherical Ag nanoparticles, resulting in asymmetric surface plasmon resonance spectra. The surface roughness of Ag nanorod array films significantly influences the growth mechanism of ZnO nanorods, leading to the formation of multi-angled ZnO microflowers. ZnO/Ag hybrid structures facilitate the interfacial charge transfer from Ag to ZnO with the realization of negative shift in binding energy of Ag 3d orbitals by ˜0.8 eV. These high quality ZnO nanorods in ZnO/Ag hybrid nanostructures exhibit strong ultraviolet emission in the 383-396 nm region without broad deep level emission, which can be explained by a suitable band diagram. The metal enhanced photoluminescence is witnessed mainly due to interfacial charge transfer with its dependence on surface roughness of bottom layer Ag nanorods, number density of ZnO nanorods and diversity in the interfacial area between Ag and ZnO nanorods. The existence of strong ultraviolet light with minor blue light emission and appearance of CIE shade in strong violet-blue region by ZnO/Ag hybrid structures depict exciting possibilities towards near UV-blue light emitting devices.

Multi-angle ZnO microstructures grown on Ag nanorods array for plasmon-enhanced near-UV-blue light emitter.

PubMed

Pal, Anil Kumar; Mohan, D Bharathi

2017-10-13

Metal enhanced ultraviolet light emission has been explored in ZnO/Ag hybrid structures prepared by hydrothermal growth of multi-angled ZnO nanorods on slanted Ag nanorods array fabricated by the thermal evaporation technique. Slanted Ag nanorods are realized to be the stacking of non-spherical Ag nanoparticles, resulting in asymmetric surface plasmon resonance spectra. The surface roughness of Ag nanorod array films significantly influences the growth mechanism of ZnO nanorods, leading to the formation of multi-angled ZnO microflowers. ZnO/Ag hybrid structures facilitate the interfacial charge transfer from Ag to ZnO with the realization of negative shift in binding energy of Ag 3d orbitals by ∼0.8 eV. These high quality ZnO nanorods in ZnO/Ag hybrid nanostructures exhibit strong ultraviolet emission in the 383-396 nm region without broad deep level emission, which can be explained by a suitable band diagram. The metal enhanced photoluminescence is witnessed mainly due to interfacial charge transfer with its dependence on surface roughness of bottom layer Ag nanorods, number density of ZnO nanorods and diversity in the interfacial area between Ag and ZnO nanorods. The existence of strong ultraviolet light with minor blue light emission and appearance of CIE shade in strong violet-blue region by ZnO/Ag hybrid structures depict exciting possibilities towards near UV-blue light emitting devices.

Optimization of processing parameters on the controlled growth of ZnO nanorod arrays for the performance improvement of solid-state dye-sensitized solar cells

DOE Office of Scientific and Technical Information (OSTI.GOV)

Lee, Yi-Mu, E-mail: ymlee@nuu.edu.t; Yang, Hsi-Wen

2011-03-15

High-transparency and high quality ZnO nanorod arrays were grown on the ITO substrates by a two-step chemical bath deposition (CBD) method. The effects of processing parameters including reaction temperature (25-95 {sup o}C) and solution concentration (0.01-0.1 M) on the crystal growth, alignment, optical and electrical properties were systematically investigated. It has been found that these process parameters are critical for the growth, orientation and aspect ratio of the nanorod arrays, showing different structural and optical properties. Experimental results reveal that the hexagonal ZnO nanorod arrays prepared under reaction temperature of 95 {sup o}C and solution concentration of 0.03 M possessmore » highest aspect ratio of {approx}21, and show the well-aligned orientation and optimum optical properties. Moreover the ZnO nanorod arrays based heterojunction electrodes and the solid-state dye-sensitized solar cells (SS-DSSCs) were fabricated with an improved optoelectrical performance. -- Graphical abstract: The ZnO nanorod arrays demonstrate well-alignment, high aspect ratio (L/D{approx}21) and excellent optical transmittance by low-temperature chemical bath deposition (CBD). Display Omitted Research highlights: > Investigate the processing parameters of CBD on the growth of ZnO nanorod arrays. > Optimization of CBD process parameters: 0.03 M solution concentration and reaction temperature of 95 {sup o}C. > The prepared ZnO samples possess well-alignment and high aspect ratio (L/D{approx}21). > An n-ZnO/p-NiO heterojunction: great rectifying behavior and low leakage current. > SS-DSSC has J{sub SC} of 0.31 mA/cm{sup 2} and V{sub OC} of 590 mV, and an improved {eta} of 0.059%.« less

Room temperature synthesis and optical properties of small diameter (5 nm) ZnO nanorod arrays.

PubMed

Cho, Seungho; Jang, Ji-Wook; Lee, Jae Sung; Lee, Kun-Hong

2010-10-01

We report a simple wet-chemical synthesis of ∼5 nm diameter ZnO nanorod arrays at room temperature (20 °C) and normal atmospheric pressure (1 atm) and their optical properties. They were single crystalline in nature, and grew in the [001] direction. These small diameter ZnO nanorod arrays can also be synthesized at 0 °C. Control experiments were also conducted. On the basis of the results, we propose a mechanism for the spontaneous growth of the small diameter ZnO structures. The optical properties of the 5 nm diameter ZnO nanorod arrays synthesized using this method were probed by UV-Visible diffuse reflectance spectroscopy. A clear blue-shift, relative to the absorption band from 50 nm diameter ZnO nanorod arrays, was attributed to the quantum confinement effects caused by the small nanocrystal size in the 5 nm diameter ZnO nanorods.

Copper nanorod array assisted silicon waveguide polarization beam splitter

PubMed Central

Kim, Sangsik; Qi, Minghao

2014-01-01

We present the design of a three-dimensional (3D) polarization beam splitter (PBS) with a copper nanorod array placed between two silicon waveguides. The localized surface plasmon resonance (LSPR) of a metal nanorod array selectively cross-couples transverse electric (TE) mode to the coupler waveguide, while transverse magnetic (TM) mode passes through the original input waveguide without coupling. An ultra-compact and broadband PBS compared to all-dielectric devices is achieved with the LSPR. The output ports of waveguides are designed to support either TM or TE mode only to enhance the extinction ratios. Compared to silver, copper is fully compatible with complementary metal-oxide-semiconductor (CMOS) technology. PMID:24787839

Copper nanorod array assisted silicon waveguide polarization beam splitter.

PubMed

Kim, Sangsik; Qi, Minghao

2014-04-21

We present the design of a three-dimensional (3D) polarization beam splitter (PBS) with a copper nanorod array placed between two silicon waveguides. The localized surface plasmon resonance (LSPR) of a metal nanorod array selectively cross-couples transverse electric (TE) mode to the coupler waveguide, while transverse magnetic (TM) mode passes through the original input waveguide without coupling. An ultra-compact and broadband PBS compared to all-dielectric devices is achieved with the LSPR. The output ports of waveguides are designed to support either TM or TE mode only to enhance the extinction ratios. Compared to silver, copper is fully compatible with complementary metal-oxide-semiconductor (CMOS) technology.

Tuning the surface morphology of aluminium doped zinc oxide thin films by arrayed nanorods through chemical growth process

NASA Astrophysics Data System (ADS)

Devasia, Sebin; Anila, E. I.

2018-04-01

Here we report the growth and characterization of chemically grown aluminium doped zinc oxide nanorods on seed layers. The seed layers were prepared by chemical spray pyrolysis which acted as the growth centers. The growth duration of nanorods were varied from 3h to 12h in steps of 3h. Further, investigations on their structural, morphological, electrical and optical properties. The SEM images confirmed the hexagonal shaped nanorod arrays grown on the seed layers. Later, the x-ray diffraction measurements revealed the pure zinc oxide phase of the samples. Photoluminescence and photoconductivity studies were carried out to analyze the potential of its optoelectronic properties.

CdS nanorods/organic hybrid LED array and the piezo-phototronic effect of the device for pressure mapping.

PubMed

Bao, Rongrong; Wang, Chunfeng; Dong, Lin; Shen, Changyu; Zhao, Kun; Pan, Caofeng

2016-04-21

As widely applied in light-emitting diodes and optical devices, CdS has attracted the attention of many researchers due to its nonlinear properties and piezo-electronic effect. Here, we demonstrate a LED array composed of PSS and CdS nanorods and research the piezo-photonic effect of the array device. The emission intensity of the device depends on the electron-hole recombination at the interface of the p-n junction which can be adjusted using the piezo-phototronic effect and can be used to map the pressure applied on the surface of the device with spatial resolution as high as 1.5 μm. A flexible LED device array has been prepared using a CdS nanorod array on a Au/Cr/kapton substrate. This device may be used in the field of strain mapping using its high pressure spatial-resolution and flexibility.

Plasmon enhanced fluorescence studies from aligned gold nanorod arrays modified with SiO{sub 2} spacer layers

DOE Office of Scientific and Technical Information (OSTI.GOV)

Damm, Signe; Fedele, Stefano; Rice, James H., E-mail: james.rice@ucd.ie

Here, we demonstrate that quasi self-standing Au nanorod arrays prepared with plasma polymerisation deposited SiO{sub 2} dielectric spacers support surface enhanced fluorescence (SEF) while maintaining high signal reproducibility. We show that it is possible to find a balance between enhanced radiative and non-radiative decay rates at which the fluorescent intensity is maximized. The SEF signal optimised with a 30 nm spacer layer thickness showed a 3.5-fold enhancement with a signal variance of <15% thereby keeping the integrity of the nanorod array. We also demonstrate the decreased importance of obtaining resonance conditions when localized surface plasmon resonance is positioned within the spectralmore » region of Au interband transitions. Procedures for further increasing the SEF enhancement factor are also discussed.« less

HKUST-1 Membranes Anchored on Porous Substrate by Hetero MIL-110 Nanorod Array Seeds.

PubMed

Mao, Yiyin; Cao, Wei; Li, Junwei; Sun, Luwei; Peng, Xinsheng

2013-09-02

Great anchors and seeds: Hetero-seeding growth processes and anchored nanorod arrays were successfully utilized in the synthesis of HKUST-1 membranes. These arrays were firmly anchored on porous substrates by using a MIL-110 nanorod array as both the anchor and seed. The resulting HKUST-1 membranes demonstrated good separation factors for binary gases exceeding the Knudson selectivity. Copyright © 2013 WILEY‐VCH Verlag GmbH & Co. KGaA, Weinheim.

Enhancing absorption in coated semiconductor nanowire/nanorod core-shell arrays using active host matrices

NASA Astrophysics Data System (ADS)

Jule, Leta; Dejene, Francis; Roro, Kittessa

2016-12-01

In the present work, we investigated theoretically and experimentally the interaction of radiation field phenomena interacting with arrays of nanowire/nanorod core-shell embedded in active host matrices. The optical properties of composites are explored including the case when the absorption of propagating wave by dissipative component is completely compensated by amplification in active (lasing) medium. On the basis of more elaborated modeling approach and extended effective medium theory, the effective polarizability and the refractive index of electromagnetic mode dispersion of the core-shell nanowire arrays are derived. ZnS(shell)-coated by sulphidation process on ZnO(shell) nanorod arrays grown on (100) silicon substrate by chemical bath deposition (CBD) has been used for theoretical comparison. Compared with the bare ZnO nanorods, ZnS-coated core/shell nanorods exhibit a strongly reduced ultraviolet (UV) emission and a dramatically enhanced deep level (DL) emission. Obviously, the UV and DL emission peaks are attributed to the emissions of ZnO nanorods within ZnO/ZnS core/shell nanorods. The reduction of UV emission after ZnS coating seems to agree with the charge separation mechanism of type-II band alignment that holes transfer from the core to shell, which would quench the UV emission to a certain extent. Our theoretical calculations and numerical simulation demonstrate that the use of active host (amplifying) medium to compensate absorption at metallic inclusions. Moreover the core-shell nanorod/nanowire arrays create the opportunity for broad band absorption and light harvesting applications.

ZnO/Er2O3 core-shell nanorod arrays: Synthesis, properties and growth mechanism

NASA Astrophysics Data System (ADS)

Yang, Jun; Wang, Yongqian; Jiang, Tingting; Li, Yinchang; Yang, Xiande

2015-01-01

In this study, we demonstrated large-scale ZnO/Er2O3 core-shell nanorod arrays, which were successfully synthesized by a facile and simple electrodeposition method. The effect of varying the amount of Er2O3 in the range from 0.2 g to 1.0 g on morphology of ZnO nanorod arrays has been thoroughly investigated. The results indicate that the growth pattern of all the ZnO/Er2O3 shell-core nanorod arrays were along c-axis and perpendicular to the substrate as before, even more vertical. Photoluminescence measurement was carried out and the PL peaks at 382 nm, 438 nm and 462 nm were observed, which are considered to be due to free excitons and donor-bound excitons, respectively. The ZnO/Er2O3 core-shell nanorods exhibited improved optical property, which can be attributed to the enhanced donor density by the covered Er2O3. Finally, a possible growth mechanism of the ZnO nanostructures is discussed. The electrochemical deposition of ZnO/Er2O3 core-shell nanorod arrays including two stages, namely nucleation and growth process.

An amorphous FeMoS4 nanorod array toward efficient hydrogen evolution electrocatalysis under neutral conditions.

PubMed

Ren, Xiang; Wang, Weiyi; Ge, Ruixiang; Hao, Shuai; Qu, Fengli; Du, Gu; Asiri, Abdullah M; Wei, Qin; Chen, Liang; Sun, Xuping

2017-08-08

It is highly attractive to develop efficient hydrogen-evolving electrocatalysts under neutral conditions. In this communication, we report an amorphous FeMoS 4 nanorod array on carbon cloth (FeMoS 4 NRA/CC) prepared by hydrothermal treatment of an FeOOH nanorod array on carbon cloth (FeOOH NRA/CC) in (NH 4 ) 2 MoS 4 solution. As a 3D electrode for hydrogen evolution electrocatalysis, this FeMoS 4 NRA/CC demonstrates superior catalytic activity and strong long-term electrochemical durability in 1.0 M phosphate buffered saline (pH: 7). It needs an overpotential of 204 mV to drive a geometrical current density of 10 mA cm -2 , which is 450 mV less than that for FeOOH NRA/CC. Density functional theory calculations suggest that FeMoS 4 has a more favourable hydrogen adsorption free energy than FeOOH.

Effect of growth time on Ti-doped ZnO nanorods prepared by low-temperature chemical bath deposition

NASA Astrophysics Data System (ADS)

Bidier, Shaker A.; Hashim, M. R.; Al-Diabat, Ahmad M.; Bououdina, M.

2017-04-01

Ti-doped ZnO nanorod arrays were grown onto Si substrate using chemical bath deposition (CBD) method at 93 °C. To investigate the effect of time deposition on the morphological, and structural properties, four Ti-doped ZnO samples were prepared at various deposition periods of time (2, 3.5, 5, and 6.5 h). FESEM images displayed high-quality and uniform nanorods with a mean length strongly dependent upon deposition time; i.e. it increases for prolonged growth time. Additionally, EFTEM images reveal a strong erosion on the lateral side for the sample prepared for 6.5 h as compared to 5 h. This might be attributed to the dissolution reaction of ZnO with for prolonged growth time. XRD analysis confirms the formation of a hexagonal wurtzite-type structure for all samples with a preferred growth orientation along the c-axis direction. The (100) peak intensity was enhanced and then quenched, which might be the result of an erosion on the lateral side of nanorods as seen in EFTEM. This study confirms the important role of growth time on the morphological features of Ti-doped ZnO nanorods prepared using CBD. Increase the growth time causes an erosion in lateral side -(100) direction XRD- and enhances the axial direction -(002), XRD.

Microwave Synthesized ZnO Nanorod Arrays for UV Sensors: A Seed Layer Annealing Temperature Study.

PubMed

Pimentel, Ana; Ferreira, Sofia Henriques; Nunes, Daniela; Calmeiro, Tomas; Martins, Rodrigo; Fortunato, Elvira

2016-04-20

The present work reports the influence of zinc oxide (ZnO) seed layer annealing temperature on structural, optical and electrical properties of ZnO nanorod arrays, synthesized by hydrothermal method assisted by microwave radiation, to be used as UV sensors. The ZnO seed layer was produced using the spin-coating method and several annealing temperatures, ranging from 100 to 500 °C, have been tested. X-ray diffraction (XRD), scanning electron microscopy (SEM), atomic force microscopy (AFM) and spectrophotometry measurements have been used to investigate the structure, morphology, and optical properties variations of the produced ZnO nanorod arrays regarding the seed layer annealing temperatures employed. After the growth of ZnO nanorod arrays, the whole structure was tested as UV sensors, showing an increase in the sensitivity with the increase of seed layer annealing temperature. The UV sensor response of ZnO nanorod arrays produced with the seed layer annealed temperature of 500 °C was 50 times superior to the ones produced with a seed layer annealed at 100 °C.

Microwave Synthesized ZnO Nanorod Arrays for UV Sensors: A Seed Layer Annealing Temperature Study

PubMed Central

Pimentel, Ana; Ferreira, Sofia Henriques; Nunes, Daniela; Calmeiro, Tomas; Martins, Rodrigo; Fortunato, Elvira

2016-01-01

The present work reports the influence of zinc oxide (ZnO) seed layer annealing temperature on structural, optical and electrical properties of ZnO nanorod arrays, synthesized by hydrothermal method assisted by microwave radiation, to be used as UV sensors. The ZnO seed layer was produced using the spin-coating method and several annealing temperatures, ranging from 100 to 500 °C, have been tested. X-ray diffraction (XRD), scanning electron microscopy (SEM), atomic force microscopy (AFM) and spectrophotometry measurements have been used to investigate the structure, morphology, and optical properties variations of the produced ZnO nanorod arrays regarding the seed layer annealing temperatures employed. After the growth of ZnO nanorod arrays, the whole structure was tested as UV sensors, showing an increase in the sensitivity with the increase of seed layer annealing temperature. The UV sensor response of ZnO nanorod arrays produced with the seed layer annealed temperature of 500 °C was 50 times superior to the ones produced with a seed layer annealed at 100 °C. PMID:28773423

Short-length and high-density TiO2 nanorod arrays for the efficient charge separation interface in perovskite solar cells

NASA Astrophysics Data System (ADS)

Xiao, Guannan; Shi, Chengwu; Zhang, Zhengguo; Li, Nannan; Li, Long

2017-05-01

The TiO2 nanorod arrays with the length of 70 nm, the diameter of 20 nm, and the areal density of 1000 μm-2 were firstly prepared by the hydrothermal method using the aqueous grown solution of 38 mM titanium isopropoxide and 6 M hydrochloric acid at 170 °C for 60 min. Over-500 nm-thickness CH3NH3PbI3-xBrx absorber layers were successfully obtained by sequential deposition routes using 1.7 M PbI2·DMSO complex precursor solution and 0.465 M isopropanol solution of the methylammonium halide mixture with the molar ratio of CH3NH3I/CH3NH3Br=85/15. The perovskite solar cells based on the TiO2 nanorod array and 560 nm-thickness CH3NH3PbI3-xBrx absorber layer exhibited the best photoelectric conversion efficiency (PCE) of 15.93%, while the corresponding planar perovskite solar cells without the TiO2 nanorod array and with 530 nm-thickness CH3NH3PbI3-xBrx absorber layer gave the best PCE of 12.82% at the relative humidity of 50-54%.

Highly Transparent and UV-Resistant Superhydrophobic SiO2-Coated ZnO Nanorod Arrays

PubMed Central

2015-01-01

Highly transparent and UV-resistant superhydrophobic arrays of SiO2-coated ZnO nanorods are prepared in a sequence of low-temperature (<150 °C) steps on both glass and thin sheets of PET (2 × 2 in.2), and the superhydrophobic nanocomposite is shown to have minimal impact on solar cell device performance under AM1.5G illumination. Flexible plastics can serve as front cell and backing materials in the manufacture of flexible displays and solar cells. PMID:24495100

Ag nanoparticles-decorated ZnO nanorod array on a mechanical flexible substrate with enhanced optical and antimicrobial properties

NASA Astrophysics Data System (ADS)

Chen, Yi; Tse, Wai Hei; Chen, Longyan; Zhang, Jin

2015-03-01

Heteronanostructured zinc oxide nanorod (ZnO NR) array are vertically grown on polydimethylsiloxane (PDMS) through a hydrothermal method followed by an in situ deposition of silver nanoparticles (Ag NPs) through a photoreduction process. The Ag-ZnO heterostructured nanorods on PDMS are measured with an average diameter of 160 nm and an average length of 2 μm. ZnO NRs measured by high-resolution transmission electron microscope (HRTEM) shows highly crystalline with a lattice fringe of 0.255 nm, which corresponds to the (0002) planes in ZnO crystal lattice. The average diameter of the Ag NPs in situ deposited on the ZnO NRs is estimated at 22 ± 2 nm. As compared to the bare ZnO NRs, the heterostructured Ag-ZnO nanorod array shows enhanced ultraviolet (UV) absorption at 440 nm, and significant emission in the visible region (λem = 542 nm). In addition, the antimicrobial efficiency of Ag-ZnO heterostructured nanorod array shows obvious improvement as compared to bare ZnO nanorod array. The cytotoxicity of ZnO nanorod array with and without Ag NPs was studied by using 3 T3 mouse fibroblast cell line. No significant toxic effect is imposed on the cells.

Ag nanoparticles-decorated ZnO nanorod array on a mechanical flexible substrate with enhanced optical and antimicrobial properties.

PubMed

Chen, Yi; Tse, Wai Hei; Chen, Longyan; Zhang, Jin

2015-01-01

Heteronanostructured zinc oxide nanorod (ZnO NR) array are vertically grown on polydimethylsiloxane (PDMS) through a hydrothermal method followed by an in situ deposition of silver nanoparticles (Ag NPs) through a photoreduction process. The Ag-ZnO heterostructured nanorods on PDMS are measured with an average diameter of 160 nm and an average length of 2 μm. ZnO NRs measured by high-resolution transmission electron microscope (HRTEM) shows highly crystalline with a lattice fringe of 0.255 nm, which corresponds to the (0002) planes in ZnO crystal lattice. The average diameter of the Ag NPs in situ deposited on the ZnO NRs is estimated at 22 ± 2 nm. As compared to the bare ZnO NRs, the heterostructured Ag-ZnO nanorod array shows enhanced ultraviolet (UV) absorption at 440 nm, and significant emission in the visible region (λem = 542 nm). In addition, the antimicrobial efficiency of Ag-ZnO heterostructured nanorod array shows obvious improvement as compared to bare ZnO nanorod array. The cytotoxicity of ZnO nanorod array with and without Ag NPs was studied by using 3 T3 mouse fibroblast cell line. No significant toxic effect is imposed on the cells.

Controlled growth of standing Ag nanorod arrays on bare Si substrate using glancing angle deposition for self-cleaning applications

NASA Astrophysics Data System (ADS)

Singh, Dhruv P.; Singh, J. P.

2014-03-01

A facile approach to manipulate the hydrophobicity of surface by controlled growth of standing Ag nanorod arrays is presented. Instead of following the complicated conventional method of the template-assisted growth, the morphology or particularly average diameter and number density (nanorods cm-2) of nanorods were controlled on bare Si substrate by simply varying the deposition rate during glancing angle deposition. The contact angle measurements showed that the evolution of Ag nanorods reduces the surface energy and makes an increment in the apparent water contact angle compared to the plain Ag thin film. The contact angle was found to increase for the Ag nanorod samples grown at lower deposition rates. Interestingly, the morphology of the nanorod arrays grown at very low deposition rate (1.2 Å sec-1) results in a self-cleaning superhydrophobic surface of contact angle about 157° and a small roll-off angle about 5°. The observed improvement in hydrophobicity with change in the morphology of nanorod arrays is explained as the effect of reduction in solid fraction within the framework of Cassie-Baxter model. These self-cleaning Ag nanorod arrays could have a significant impact in wide range of applications such as anti-icing coatings, sensors and solar panels.

Preparation of thin hexagonal highly-ordered anodic aluminum oxide (AAO) template onto silicon substrate and growth ZnO nanorod arrays by electrodeposition

NASA Astrophysics Data System (ADS)

Chahrour, Khaled M.; Ahmed, Naser M.; Hashim, M. R.; Elfadill, Nezar G.; Qaeed, M. A.; Bououdina, M.

2014-12-01

In this study, anodic aluminum oxide (AAO) templates of Aluminum thin films onto Ti-coated silicon substrates were prepared for growth of nanostructure materials. Hexagonally highly ordered thin AAO templates were fabricated under controllable conditions by using a two-step anodization. The obtained thin AAO templates were approximately 70 nm in pore diameter and 250 nm in length with 110 nm interpore distances within an area of 3 cm2. The difference between first and second anodization was investigated in details by in situ monitoring of current-time curve. A bottom barrier layer of the AAO templates was removed during dropping the voltage in the last period of the anodization process followed by a wet etching using phosphoric acid (5 wt%) for several minutes at ambient temperature. As an application, Zn nanorod arrays embedded in anodic alumina (AAO) template were fabricated by electrodeposition. Oxygen was used to oxidize the electrodeposited Zn nanorods in the AAO template at 700 °C. The morphology, structure and photoluminescence properties of ZnO/AAO assembly were analyzed using Field-emission scanning electron microscope (FESEM), Energy dispersive X-ray spectroscopy (EDX), Atomic force microscope (AFM), X-ray diffraction (XRD) and photoluminescence (PL).

Synthesis and characterization of beta-Ga2O3 nanorod array clumps by chemical vapor deposition.

PubMed

Shi, Feng; Wei, Xiaofeng

2012-11-01

beta-Ga2O3 nanorod array clumps were successfully synthesized on Si (111) substrates by chemical vapor deposition. The composition, microstructure, morphology, and light-emitting property of these clumps were characterized by X-ray diffraction, Fourier transform infrared spectrophotometry, X-ray photoelectron spectroscopy, scanning electron microscopy, high-resolution transmission electron microscopy, Raman spectroscopy, and photoluminescence. The results demonstrate that the sample synthesized at 1050 degrees C for 15 min was composed of monoclinic beta-Ga2O3 nanorod array clumps, where each single nanorod was about 300 nm in diameter with some nano-droplets on its tip. These results reveal that the growth mechanism agrees with the vapor-liquid-solid (VLS) process. The photoluminescence spectrum shows that the Ga2O3 nanorods have a blue emission at 438 nm, which may be attributed to defects, such as oxygen vacancies and gallium-oxygen vacancy pairs. Defect-energy aggregation confinement growth theory was proposed to explain the growth mechanism of Ga2O3 nanorod array clumps collaborated with the VLS mechanism.

Plasmonic nanorod arrays of a two-segment dimer and a coaxial cable with 1 nm gap for large field confinement and enhancement

NASA Astrophysics Data System (ADS)

Cheng, Zi-Qiang; Nan, Fan; Yang, Da-Jie; Zhong, Yu-Ting; Ma, Liang; Hao, Zhong-Hua; Zhou, Li; Wang, Qu-Quan

2015-01-01

Seeking plasmonic nanostructures with large field confinement and enhancement is significant for photonic and electronic nanodevices with high sensitivity, reproducibility, and tunability. Here, we report the synthesis of plasmonic arrays composed of two-segment dimer nanorods and coaxial cable nanorods with ~1 nm gap insulated by a self-assembled Raman molecule monolayer. The gap-induced plasmon coupling generates an intense field in the gap region of the dimer junction and the cable interlayer. As a result, the longitudinal plasmon resonance of nanorod arrays with high tunability is obviously enhanced. Most interestingly, the field enhancement of dimer nanorod arrays can be tuned by the length ratio L1/L2 of the two segments, and the maximal enhancement appears at L1/L2 = 1. In that case, the two-photon luminescence (TPL) of dimer nanorod arrays and the Raman intensity in the dimer junction is enhanced by 27 and 30 times, respectively, under resonant excitation. In the same way, the Raman intensity in the gap region is enhanced 16 times for the coaxial cable nanorod arrays. The plasmonic nanorod arrays synthesized by the facile method, having tunable plasmon properties and large field enhancement, indicate an attractive pathway to the photonic nanodevices.Seeking plasmonic nanostructures with large field confinement and enhancement is significant for photonic and electronic nanodevices with high sensitivity, reproducibility, and tunability. Here, we report the synthesis of plasmonic arrays composed of two-segment dimer nanorods and coaxial cable nanorods with ~1 nm gap insulated by a self-assembled Raman molecule monolayer. The gap-induced plasmon coupling generates an intense field in the gap region of the dimer junction and the cable interlayer. As a result, the longitudinal plasmon resonance of nanorod arrays with high tunability is obviously enhanced. Most interestingly, the field enhancement of dimer nanorod arrays can be tuned by the length ratio L1/L2 of

Fast light-induced reversible wettability of a zinc oxide nanorod array coated with a thin gold layer

NASA Astrophysics Data System (ADS)

Wei, Yuefan; Du, Hejun; Kong, Junhua; Tran, Van-Thai; Koh, Jia Kai; Zhao, Chenyang; He, Chaobin

2017-11-01

Zinc oxide (ZnO) has gained much attention recently due to its excellent physical and chemical properties, and has been extensively studied in energy harvesting applications such as photovoltaic and piezoelectric devices. In recent years, its reversible wettability has also attracted increasing interest. The wettability of ZnO nanostructures with various morphologies has been studied. However, to the best of our knowledge, there is still a lack of investigations on further modifications on ZnO to provide more benefits than pristine ZnO. Comprehensive studies on the reversible wettability are still needed. In this study, a ZnO nanorod array was prepared via a hydrothermal process and subsequently coated with thin gold layers with varied thickness. The morphologies and structures, optical properties and wettability were investigated. It is revealed that the ZnO-Au system possesses recoverable wettability upon switching between visible-ultraviolet light and a dark environment, which is verified by the contact angle change. The introduction of the thin gold layer to the ZnO nanorod array effectively increases the recovery rate of the wettability. The improvements are attributed to the hierarchical structures, which are formed by depositing thin gold layers onto the ZnO nanorod array, the visible light sensitivity due to the plasmonic effect of the deposited gold, as well as the fast charge-induced surface status change upon light illumination or dark storage. The improvement is beneficial to applications in environmental purification, energy harvesting, micro-lenses, and smart devices.

Facile construction of vertically aligned EuS-ZnO hybrid core shell nanorod arrays for visible light driven photocatalytic properties

DOE Office of Scientific and Technical Information (OSTI.GOV)

Ranjith, K. S.; Kumar, D. Ranjith; Kumar, R. T. Rajendra, E-mail: rtrkumar@buc.edu.in

2015-06-24

We demonstrated the development of coupled semiconductor in the form of hybrid heterostructures for significant advancement in catalytic functional materials. In this article, we report the preparation of vertically aligned core shell ZnO-EuS nanorod photocatalyst arrays by a simple chemical solution process followed by sulfudation process. The XRD pattern confirmed formation of the hexagonal wurtzite structure of ZnO and cubic nature of the EuS. Cross sectional FESEM images show vertical rod array structure, and the size of the nanorods ranges from 80 to 120 nm. UV-Vis DRS spectra showed that the optical absorption of ZnO was significantly enhanced to the visiblemore » region by modification with EuS surfaces. TEM study confirmed that the surface of ZnO was drastically improved by the modification with EuS nanoparticle. The catalytic activity of EuS−ZnO core shell nanorod arrays were evaluated by the photodegradation of Methylene Blue (MB) dye under visible irradiation. The results revealed that the photocatalytic activity of EuS−ZnO was much higher than that of ZnO under natural sunlight. EuS−ZnO was found to be stable and reusable without appreciable loss of catalytic activity up to four consecutive cycles.« less

Novel Gas Sensor Based on ZnO Nanorod Circular Arrays for C2H5OH Gas Detection.

PubMed

Jianjiao, Zhang; Hongyan, Yue; Erjun, Guo; Shaolin, Zhang; Liping, Wang; Chunyu, Zhang; Xin, Gao; Jing, Chang; Hong, Zhang

2015-03-01

Novel side-heating gas sensor based on ZnO nanorod circular arrays was firstly fabricated by hydrothermal treatment assisted with a kind of simple dip-coating technique. The structure and morphologies of ZnO nanorods were characterized by X-ray diffraction (XRD), Scanning Electron Microscope (SEM), respectively. XRD result indicates that the obtained ZnO nanorods have good crystalline with the hexagonal wurtzite structure. SEM result indicates that ZnO nanorod arrays are vertically growth on the surface of ceramic tube of side-heating sensor with controlled diameter and length, narrow size distribution and high orientation. The gas sensing properties of ZnO nanorod circular arrays are also evaluated. Comparative to the sensor based on scattered ZnO nanorods responding to 25 ppm H2, CO, C6H5CH3 and C2H5OH gas, respectively, the sensing values of high orientation gas sensor are generally increased by 5%. This novel sensor has good application promising for the fabrication of cost effective and high performance gas sensors.

Large-area zinc oxide nanorod arrays templated by nanoimprint lithography: control of morphologies and optical properties

NASA Astrophysics Data System (ADS)

Zhang, Chen; Huang, Xiaohu; Liu, Hongfei; Chua, Soo Jin; Ross, Caroline A.

2016-12-01

Vertically aligned, highly ordered, large area arrays of nanostructures are important building blocks for multifunctional devices. Here, ZnO nanorod arrays are selectively synthesized on Si substrates by a solution method within patterns created by nanoimprint lithography. The growth modes of two dimensional nucleation-driven wedding cakes and screw dislocation-driven spirals are inferred to determine the top end morphologies of the nanorods. Sub-bandgap photoluminescence of the nanorods is greatly enhanced by the manipulation of the hydrogen donors via a post-growth thermal treatment. Lasing behavior is facilitated in the nanorods with faceted top ends formed from wedding cakes growth mode. This work demonstrates the control of morphologies of oxide nanostructures in a large scale and the optimization of the optical performance.

Combination of short-length TiO2 nanorod arrays and compact PbS quantum-dot thin films for efficient solid-state quantum-dot-sensitized solar cells

NASA Astrophysics Data System (ADS)

Zhang, Zhengguo; Shi, Chengwu; Chen, Junjun; Xiao, Guannan; Li, Long

2017-07-01

Considering the balance of the hole diffusion length and the loading quantity of quantum-dots, the rutile TiO2 nanorod array with the length of 600 nm, the diameter of 20 nm, and the areal density of 500 μm-2 is successfully prepared by the hydrothermal method using the aqueous grown solution of 38 mM titanium isopropoxide and 6 M hydrochloric acid at 170 °C for 105 min. The compact PbS quantum-dot thin film on the TiO2 nanorod array is firstly obtained by the spin-coating-assisted successive ionic layer absorption and reaction with using 1,2-ethanedithiol (EDT). The result reveals that the strong interaction between lead and EDT is very important to control the crystallite size of PbS quantum-dots and obtain the compact PbS quantum-dot thin film on the TiO2 nanorod array. The all solid-state sensitized solar cell with the combination of the short-length, high-density TiO2 nanorod array and the compact PbS quantum-dot thin film achieves the photoelectric conversion efficiency of 4.10%, along with an open-circuit voltage of 0.52 V, a short-circuit photocurrent density of 13.56 mA cm-2 and a fill factor of 0.58.

Fe 2O 3–TiO 2 core–shell nanorod arrays for visible light photocatalytic applications

DOE PAGES

Yao, Kun; Basnet, Pradip; Sessions, Henry; ...

2015-11-11

By using the glancing angle deposition technique and post-deposition annealing, Fe 2O 3–TiO 2 core-shell nanorod arrays with specific crystalline states can be designed and fabricated. The Fe 2O 3–TiO 2 core-shell samples annealed at temperatures greater than 450°C formed α-Fe 2O 3 and anatase TiO 2, and showed higher catalytic efficiency for the degradation of methylene blue (MB) under visible light illumination when compared with pure anatase TiO 2 or α-Fe 2O 3 nanorod arrays. Solar conversion of carbon dioxide and water vapor in the presence of Fe 2O 3–TiO 2 core-shell nanorod arrays was also investigated. Carbon monoxide,more » hydrogen, methane, and methanol along with other hydrocarbons were produced after only several hours’ exposure under ambient sunlight. It was determined that the core-shell structure showed greater efficiency for solar CO 2 conversion than the pure TiO 2 nanorod arrays.« less

Plasmonic nanorod arrays of a two-segment dimer and a coaxial cable with 1 nm gap for large field confinement and enhancement.

PubMed

Cheng, Zi-Qiang; Nan, Fan; Yang, Da-Jie; Zhong, Yu-Ting; Ma, Liang; Hao, Zhong-Hua; Zhou, Li; Wang, Qu-Quan

2015-01-28

Seeking plasmonic nanostructures with large field confinement and enhancement is significant for photonic and electronic nanodevices with high sensitivity, reproducibility, and tunability. Here, we report the synthesis of plasmonic arrays composed of two-segment dimer nanorods and coaxial cable nanorods with ∼1 nm gap insulated by a self-assembled Raman molecule monolayer. The gap-induced plasmon coupling generates an intense field in the gap region of the dimer junction and the cable interlayer. As a result, the longitudinal plasmon resonance of nanorod arrays with high tunability is obviously enhanced. Most interestingly, the field enhancement of dimer nanorod arrays can be tuned by the length ratio L1/L2 of the two segments, and the maximal enhancement appears at L1/L2 = 1. In that case, the two-photon luminescence (TPL) of dimer nanorod arrays and the Raman intensity in the dimer junction is enhanced by 27 and 30 times, respectively, under resonant excitation. In the same way, the Raman intensity in the gap region is enhanced 16 times for the coaxial cable nanorod arrays. The plasmonic nanorod arrays synthesized by the facile method, having tunable plasmon properties and large field enhancement, indicate an attractive pathway to the photonic nanodevices.

Electrodeposition of ZnO nanorod arrays on ZnO substrate with tunable orientation and optical properties.

PubMed

Jehl, Z; Rousset, J; Donsanti, F; Renou, G; Naghavi, N; Lincot, D

2010-10-01

The electrodeposition of ZnO nanorods on ZnO:Al films with different orientations is reported. The influence of the total charge exchanged during electrodeposition on the nanorod's geometry (length, diameter, aspect ratio and surface density) and the optical transmission properties of the nanorod arrays is studied on a [0001]-oriented ZnO:Al substrate. The nanorods are highly vertically oriented along the c axis, following the lattice matching with the substrate. The growth on a [1010] and [1120] ZnO:Al-oriented substrate with c axis parallel to the substrate leads to a systematic deviation angle of 55 degrees from the perpendicular direction. This finding has been explained by the occurrence of a minority orientation with the [1011] planes parallel to the surface, with a preferential growth on corresponding [0001] termination. Substrate crystalline orientation is thereby found to be a major parameter in finely tuning the orientation of the nanorod array. This new approach allows us to optimize the light scattering properties of the films.

Cobalt selenide hollow nanorods array with exceptionally high electrocatalytic activity for high-efficiency quasi-solid-state dye-sensitized solar cells

NASA Astrophysics Data System (ADS)

Jin, Zhitong; Zhang, Meirong; Wang, Min; Feng, Chuanqi; Wang, Zhong-Sheng

2018-02-01

In quasi-solid-state dye-sensitized solar cells (QSDSSCs), electron transport through a random network of catalyst in the counter electrode (CE) and electrolyte diffusion therein are limited by the grain boundaries of catalyst particles, thus diminishing the electrocatalytic performance of CE and the corresponding photovoltaic performance of QSDSSCs. We demonstrate herein an ordered Co0.85Se hollow nanorods array film as the Pt-free CE of QSDSSCs. The Co0.85Se hollow nanorods array displays excellent electrocatalytic activity for the reduction of I3- in the quasi-solid-state electrolyte with extremely low charge transfer resistance at the CE/electrolyte interface, and the diffusion of redox species within the Co0.85Se hollow nanorods array CE is pretty fast. The QSDSSC device with the Co0.85Se hollow nanorods array CE produces much higher photovoltaic conversion efficiency (8.35%) than that (4.94%) with the Co0.85Se randomly packed nanorods CE, against the control device with the Pt CE (7.75%). Moreover, the QSDSSC device based on the Co0.85Se hollow nanorods array CE presents good long-term stability with only 4% drop of power conversion efficiency after 1086 h one-sun soaking.

Electroluminescence of ordered ZnO nanorod array/p-GaN light-emitting diodes with graphene current spreading layer

PubMed Central

2014-01-01

Ordered ZnO nanorod array/p-GaN heterojunction light-emitting diodes (LEDs) have been fabricated by introducing graphene as the current spreading layer, which exhibit improved electroluminescence performance by comparison to the LED using a conventional structure (indium-tin-oxide as the current spreading layer). In addition, by adjusting the diameter of ZnO nanorod array in use, the light emission of the ZnO nanorod array/p-GaN heterojunction LEDs was enhanced further. This work has great potential applications in solid-state lighting, high performance optoelectronic devices, and so on. PACS 78.60.Fi; 85.60.Jb; 78.67.Lt; 81.10.Dn PMID:25489284

Electroluminescence of ordered ZnO nanorod array/p-GaN light-emitting diodes with graphene current spreading layer.

PubMed

Dong, Jing-Jing; Hao, Hui-Ying; Xing, Jie; Fan, Zhen-Jun; Zhang, Zi-Li

2014-01-01

Ordered ZnO nanorod array/p-GaN heterojunction light-emitting diodes (LEDs) have been fabricated by introducing graphene as the current spreading layer, which exhibit improved electroluminescence performance by comparison to the LED using a conventional structure (indium-tin-oxide as the current spreading layer). In addition, by adjusting the diameter of ZnO nanorod array in use, the light emission of the ZnO nanorod array/p-GaN heterojunction LEDs was enhanced further. This work has great potential applications in solid-state lighting, high performance optoelectronic devices, and so on. 78.60.Fi; 85.60.Jb; 78.67.Lt; 81.10.Dn.

A high efficiency microreactor with Pt/ZnO nanorod arrays on the inner wall for photodegradation of phenol.

PubMed

Zhang, Quan; Zhang, Qinghong; Wang, Hongzhi; Li, Yaogang

2013-06-15

A high efficiency microreactor with Pt coated ZnO (Pt/ZnO) nanorod arrays on the inner wall was successfully fabricated by pumping a Pt sol into the microchannel containing preformed ZnO nanorod arrays. Phenol was selected as a persistent organic pollutant to evaluate the photocatalytic performance of the microreactors. The microreactor which was coated by Pt sol for 5 min showed the best photocatalytic performance compared with other Pt/ZnO nanorod array-modified microreactors. The presence of Pt nanoparticles on the surfaces of ZnO nanorods promoted the separation of photoinduced electron-hole pairs and thus enhanced the photocatalytic activity. In addition, the recyclable property of the microcreator was investigated. It was found that the microreactor displayed higher durability during the continuous photocatalytic process. Copyright © 2013 Elsevier B.V. All rights reserved.

Separating light absorption layer from channel in ZnO vertical nanorod arrays based photodetectors for high-performance image sensors

NASA Astrophysics Data System (ADS)

Ma, Yang; Wu, Congjun; Xu, Zhihao; Wang, Fei; Wang, Min

2018-05-01

Photoconductor arrays with both high responsivity and large ON/OFF ratios are of great importance for the application of image sensors. Herein, a ZnO vertical nanorod array based photoconductor with a light absorption layer separated from the device channel has been designed, in which the photo-generated carriers along the axial ZnO nanorods drive to the external electrodes through nanorod-nanorod junctions in the dense layer at the bottom. This design allows us to enhance the photocurrent with unchanged dark current by increasing the ratio between the ZnO nanorod length and the thickness of the dense layer to achieve both high responsivity and large ON/OFF ratios. As a result, the as-fabricated devices possess a high responsivity of 1.3 × 105 A/W, a high ON/OFF ratio of 790, a high detectivity of 1.3 × 1013 Jones, and a low detectable light intensity of 1 μW/cm2. More importantly, the developed approach enables the integration of ZnO vertical nanorod array based photodetectors as image sensors with uniform device-to-device performance.

Chemical growth of ZnO nanorod arrays on textured nanoparticle nanoribbons and its second-harmonic generation performance

NASA Astrophysics Data System (ADS)

Gui, Zhou; Wang, Xian; Liu, Jian; Yan, Shanshan; Ding, Yanyan; Wang, Zhengzhou; Hu, Yuan

2006-07-01

On the basis of the highly oriented ZnO nanoparticle nanoribbons as the growth seed layer (GSL) and solution growth technique, we have synthesized vertical ZnO nanorod arrays with high density over a large area and multi-teeth brush nanostructure, respectively, according to the density degree of the arrangement of nanoparticle nanoribbons GSL on the glass substrate. This controllable and convenient technique opens the possibility of creating nanostructured film for industrial fabrication and may represent a facile way to get similar structures of other compounds by using highly oriented GSL to promote the vertical arrays growth. The growth mechanism of the formation of the ordered nanorod arrays is also discussed. The second-order nonlinear optical coefficient d31 of the vertical ZnO nanorod arrays measured by the Maker fringes technique is 11.3 times as large as that of d36 KH 2PO 4 (KDP).

Fabrication of needle-like ZnO nanorods arrays by a low-temperature seed-layer growth approach in solution

NASA Astrophysics Data System (ADS)

Zhang, Haimin; Quan, Xie; Chen, Shuo; Zhao, Huimin

2007-11-01

Uniform, large-scale, and well-aligned needle-like ZnO nanorods with good photoluminescence and photocatalysis properties on Zn substrates, have been successfully fabricated using a simple low-temperature seed-layer growth approach in solution (50 °C). The formation of ZnO seed-layer by the anodic oxidation technique (AOT) plays an important role in the subsequent growth of highly oriented ZnO nanorods arrays. Temperature also proved to be a significant factor in the growth of ZnO nanorods and had a great effect on their optical properties. X-ray diffraction (XRD) analysis, selected-area electron diffraction (SAED) pattern and high-resolution TEM (HRTEM) indicated that the needle-like ZnO nanorods were single crystal in nature and that they had grown up preferentially along the [0001] direction. The well-aligned ZnO nanorods arrays on Zn substrates exhibited strong UV emission at around 380 nm at room temperature. To investigate their potential as photocatalysts, degradation of pentachlorophenol (PCP) in aqueous solution was carried out using photocatalytic processes, with comparison to direct photolysis. After 1 h, the degradation efficiencies of PCP by direct photolysis and photocatalytic processes achieved 57% and 76% under given experimental conditions, respectively. This improved degradation efficiency of PCP illustrates that ZnO nanorods arrays on Zn substrates have good photocatalytic activity. This simple low-temperature seed-layer growth approach in solution resulted in the development of an effective and low-cost fabrication process for high-quality ZnO nanorods arrays with good optical and photocatalytic properties that can be applicable in many fields such as photocatalysis, photovoltaic cells, luminescent sensors, and photoconductive sensors.

Biological sensing and control of emission dynamics of quantum dot bioconjugates using arrays of long metallic nanorods.

PubMed

Sadeghi, Seyed M; Gutha, Rithvik R; Wing, Waylin J; Sharp, Christina; Capps, Lucas; Mao, Chuanbin

2017-01-01

We study biological sensing using plasmonic and photonic-plasmonic resonances of arrays of ultralong metallic nanorods and analyze the impact of these resonances on emission dynamics of quantum dot bioconjugates. We demonstrate that the LSPRs and plasmonic lattice modes of such array can be used to detect a single self-assembled monolayer of alkanethiol at the visible (550 nm) and near infrared (770 nm) range with well resolved shifts. We study adsorption of streptavidin-quantum dot conjugates to this monolayer, demonstrating that formation of nearly two dimensional arrays of quantum dots with limited emission blinking can lead to extra well-defined wavelength shifts in these modes. Using spectrally-resolved lifetime measurements we study the emission dynamics of such quantum dot bioconjugates within their monodispersed size distribution. We show that, despite their close vicinity to the nanorods, the rate of energy transfer from these quantum dots to nanorods is rather weak, while the plasmon field enhancement can be strong. Our results reveal that the nanorods present a strongly wavelength or size-dependent non-radiative decay channel to the quantum dot bioconjugates.

Understanding charge transfer dynamics in QDs-TiO2 nanorod array photoanodes for solar fuel generation

NASA Astrophysics Data System (ADS)

Li, Jiangtian; McClure, Joshua P.; Fu, Richard; Jiang, Rongzhong; Chu, Deryn

2018-01-01

Harvesting light to drive water splitting for hydrogen generation is an attractive approach to satisfy the urgent energy demands. The design and fabrication of photoelectrode materials that are able to harvest sunlight is an important scientific undertaking. In this study, a two-quantum-dot (QD) layer is developed to decorate one-dimensional TiO2 nanorod arrays, which are subsequently utilized as photoanodes to harvest the wide-spectrum sunlight for water splitting. The QD-coated TiO2 nanorod arrays extend the light absorption range from the UV into the visible region yielding increased solar-to-hydrogen efficiencies. Transient photocurrent decay measurements demonstrate that the multi-layer CdSe-CdS QDs deposited onto the TiO2 nanorod arrays result in a stepwise band alignment that not only improves the hole extraction but also facilitates electron injection from the QDs to TiO2 rods. Moreover, the multi-heterojunction photoanode introduces interfacial states that act as recombination centers to trap the photogenerated electrons.

Electrochemical growth of controlled tip shapes of ZnO nanorod arrays on silicon substrate and enhanced photoluminescence emission from nanopyramid arrays compared with flat-head nanorods

NASA Astrophysics Data System (ADS)

Alimanesh, Mahmoud; Hassan, Z.; Zainal, Norzaini

2017-10-01

Zinc oxide (ZnO) nanorod arrays (NRAs) with different morphologies such as; perfect hexagon flat-head, pyramidal, compact pencil, nail-shaped, and high-compact ZnO nanorod thin films, were successfully grown on silicon substrates. These NRAs were formed on substrates using a simple low-temperature electrochemical method without adding any catalyst or template via the precursors of zinc nitrate hexahydrate [Zn(NO3)2·6H2O] and hexamethylenetetramine [HMT; C6H12N4] with an equal molar concentration of 0.025 mol/l. The morphologies of the ZnO nanorods (NRs) could be controlled and transformed successfully in to other morphologies by changing the growth conditions, such as; growth temperature and applied current density. Detailed structural investigations reveal that the synthesized various NRs are single crystalline with wurtzite hexagonal phase and preferentially grow along the c-axis direction. The room temperature photoluminescence spectra show that each spectrum consists of an ultraviolet (UV) band and a relative broad visible light emission and infrared emission peak. The enhanced light emission intensity at UV peak (∼375 nm) is observed significantly from ZnO nanopyramid (NP) arrays because of the conical shape of NP. The photoluminescence intensity of the UV peak from the NPs is found to be 1.5-17 times larger than those from the other various NRs.

Self-assembled vertically aligned Au nanorod arrays for surface-enhanced Raman scattering (SERS) detection of Cannabinol

NASA Astrophysics Data System (ADS)

Milliken, Sarah; Fraser, Jeff; Poirier, Shawn; Hulse, John; Tay, Li-Lin

2018-05-01

Self-assembled multi-layered vertically aligned gold nanorod (AuNR) arrays have been fabricated by a simple preparation process that requires a balance between the particle concentration and the ionic strength of the solvent. An experimentally determined critical AuNR concentration of 2.0 nM and 50 mM NaCl produces well-ordered vertically aligned hexagonally close-packed AuNR arrays. We demonstrate surface treatment via UV Ozone cleaning of such samples to allow introduction of analyte molecules (benzenethiol and cannabinol) for effective surface enhanced Raman scattering detection. This is the first demonstration of the SERS analysis of cannabinol. This approach demonstrates a cost-effective, high-yield and simple fabrication route to SERS sensors with application in the screening for the cannabinoids.

Hydrophilicity Reinforced Adhesion of Anodic Alumina Oxide Template Films to Conducting Substrates for Facile Fabrication of Highly Ordered Nanorod Arrays.

PubMed

Wang, Chuanju; Wang, Guiqiang; Yang, Rui; Sun, Xiangyu; Ma, Hui; Sun, Shuqing

2017-01-17

Arrays of ordered nanorods are of special interest in many fields. However, it remains challenging to obtain such arrays on conducting substrates in a facile manner. In this article, we report the fabrication of highly ordered and vertically standing nanorod arrays of both metals and semiconductors on Au films and indium tin oxide glass substrates without an additional layering. In this approach, following the simple hydrophilic treatment of an anodic aluminum oxide (AAO) membrane and conducting substrates, the AAO membrane was transferred onto the modified substrates with excellent adhesion. Subsequently, nanorod arrays of various materials were electrodeposited on the conducting substrates directly. This method avoids any expensive and tedious lithographic and ion milling process, which provides a simple yet robust route to the fabrication of arrays of 1D materials with high aspect ratio on conducting substrates, which shall pave the way for many practical applications in a range of fields.

Self-assembled vertically aligned Au nanorod arrays for surface-enhanced Raman scattering (SERS) detection of Cannabinol.

PubMed

Milliken, Sarah; Fraser, Jeff; Poirier, Shawn; Hulse, John; Tay, Li-Lin

2018-05-05

Self-assembled multi-layered vertically aligned gold nanorod (AuNR) arrays have been fabricated by a simple preparation process that requires a balance between the particle concentration and the ionic strength of the solvent. An experimentally determined critical AuNR concentration of 2.0nM and 50mM NaCl produces well-ordered vertically aligned hexagonally close-packed AuNR arrays. We demonstrate surface treatment via UV Ozone cleaning of such samples to allow introduction of analyte molecules (benzenethiol and cannabinol) for effective surface enhanced Raman scattering detection. This is the first demonstration of the SERS analysis of cannabinol. This approach demonstrates a cost-effective, high-yield and simple fabrication route to SERS sensors with application in the screening for the cannabinoids. Copyright © 2018. Published by Elsevier B.V.

Defects in ZnO nanorods prepared by a hydrothermal method.

PubMed

Tam, K H; Cheung, C K; Leung, Y H; Djurisić, A B; Ling, C C; Beling, C D; Fung, S; Kwok, W M; Chan, W K; Phillips, D L; Ding, L; Ge, W K

2006-10-26

ZnO nanorod arrays were fabricated using a hydrothermal method. The nanorods were studied by scanning electron microscopy, photoluminescence (PL), time-resolved PL, X-ray photoelectron spectroscopy, and positron annihilation spectroscopy before and after annealing in different environments and at different temperatures. Annealing atmosphere and temperature had significant effects on the PL spectrum, while in all cases the positron diffusion length and PL decay times were increased. We found that, while the defect emission can be significantly reduced by annealing at 200 degrees C, the rods still have large defect concentrations as confirmed by their low positron diffusion length and short PL decay time constants.

Preparation and Electrochemical Performance of Li4Mn5O12 Nanorods using β-MnO2 Nanorods as Precursor

NASA Astrophysics Data System (ADS)

Zhao, Yan; Wang, Li; Mu, Yanlin; Zhang, Chongwei; Zhu, Fan; Liu, Mengjiao; Lai, Qiongyu; Bi, Jian; Gao, Daojiang

2018-03-01

Li4Mn5O12 nanorods were successfully prepared by using β-MnO2 nanorod precursors as self-templates. The obtained Li4Mn5O12 nanorods were approximately 0.8-1.5 μm in length and 0.15 μm in width, and were employed as electrode materials and applied in supercapacitors. The results show that Li4Mn5O12 nanorods can deliver 211 F g-1 within the potential range of 0-1.4 V at a scan rate of 5 mV s-1 in 1 mol L-1 Li2SO4 solution, which presents a good electrochemical performance.

Aligned copper nanorod arrays for highly efficient generation of intense ultra-broadband THz pulses.

PubMed

Mondal, S; Wei, Q; Ding, W J; Hafez, H A; Fareed, M A; Laramée, A; Ropagnol, X; Zhang, G; Sun, S; Sheng, Z M; Zhang, J; Ozaki, T

2017-01-10

We demonstrate an intense broadband terahertz (THz) source based on the interaction of relativistic-intensity femtosecond lasers with aligned copper nanorod array targets. For copper nanorod targets with a length of 5 μm, a maximum 13.8 times enhancement in the THz pulse energy (in ≤20 THz spectral range) is measured as compared to that with a thick plane copper target under the same laser conditions. A further increase in the nanorod length leads to a decrease in the THz pulse energy at medium frequencies (≤20 THz) and increase of the electromagnetic pulse energy in the high-frequency range (from 20-200 THz). For the latter, we measure a maximum energy enhancement of 28 times for the nanorod targets with a length of 60 μm. Particle-in-cell simulations reveal that THz pulses are mostly generated by coherent transition radiation of laser produced hot electrons, which are efficiently enhanced with the use of nanorod targets. Good agreement is found between the simulation and experimental results.

Aligned copper nanorod arrays for highly efficient generation of intense ultra-broadband THz pulses

PubMed Central

Mondal, S.; Wei, Q.; Ding, W. J.; Hafez, H. A.; Fareed, M. A.; Laramée, A.; Ropagnol, X.; Zhang, G.; Sun, S.; Sheng, Z. M.; Zhang, J.; Ozaki, T.

2017-01-01

We demonstrate an intense broadband terahertz (THz) source based on the interaction of relativistic-intensity femtosecond lasers with aligned copper nanorod array targets. For copper nanorod targets with a length of 5 μm, a maximum 13.8 times enhancement in the THz pulse energy (in ≤20 THz spectral range) is measured as compared to that with a thick plane copper target under the same laser conditions. A further increase in the nanorod length leads to a decrease in the THz pulse energy at medium frequencies (≤20 THz) and increase of the electromagnetic pulse energy in the high-frequency range (from 20–200 THz). For the latter, we measure a maximum energy enhancement of 28 times for the nanorod targets with a length of 60 μm. Particle-in-cell simulations reveal that THz pulses are mostly generated by coherent transition radiation of laser produced hot electrons, which are efficiently enhanced with the use of nanorod targets. Good agreement is found between the simulation and experimental results. PMID:28071764

Aligned copper nanorod arrays for highly efficient generation of intense ultra-broadband THz pulses

NASA Astrophysics Data System (ADS)

Mondal, S.; Wei, Q.; Ding, W. J.; Hafez, H. A.; Fareed, M. A.; Laramée, A.; Ropagnol, X.; Zhang, G.; Sun, S.; Sheng, Z. M.; Zhang, J.; Ozaki, T.

2017-01-01

We demonstrate an intense broadband terahertz (THz) source based on the interaction of relativistic-intensity femtosecond lasers with aligned copper nanorod array targets. For copper nanorod targets with a length of 5 μm, a maximum 13.8 times enhancement in the THz pulse energy (in ≤20 THz spectral range) is measured as compared to that with a thick plane copper target under the same laser conditions. A further increase in the nanorod length leads to a decrease in the THz pulse energy at medium frequencies (≤20 THz) and increase of the electromagnetic pulse energy in the high-frequency range (from 20-200 THz). For the latter, we measure a maximum energy enhancement of 28 times for the nanorod targets with a length of 60 μm. Particle-in-cell simulations reveal that THz pulses are mostly generated by coherent transition radiation of laser produced hot electrons, which are efficiently enhanced with the use of nanorod targets. Good agreement is found between the simulation and experimental results.

Low temperature preparation of Ag-doped ZnO nanowire arrays for sensor and light-emitting diode applications

NASA Astrophysics Data System (ADS)

Lupan, O.; Viana, B.; Cretu, V.; Postica, V.; Adelung, R.; Pauporté, T.

2016-02-01

Transition metal doped-oxide semiconductor nanostructures are important to achieve enhanced and new properties for advanced applications. We describe the low temperature preparation of ZnO:Ag nanowire/nanorod (NW/NR) arrays by electrodeposition at 90 °C. The NWs have been characterized by SEM, EDX, transmittance and photoluminescence (PL) measurements. The integration of Ag in the crystal is shown. Single nanowire/nanorod of ZnO:Ag was integrated in a nanosensor structure leading to new and enhanced properties. The ultraviolet (UV) response of the nanosensor was investigated at room temperature. Experimental results indicate that ZnO:Ag (0.75 μM) nanosensor possesses faster response/recovery time and better response to UV light than those reported in literature. The sensor structure has been also shown to give a fast response for the hydrogen detection with improved performances compared to pristine ZnO NWs. ZnO:Ag nanowire/nanorod arrays electrochemically grown on p-type GaN single crystal layer is also shown to act as light emitter in LED structures. The emission wavelength is red-shifted compared to pristine ZnO NW array. At low Ag concentration a single UV-blue emission is found whereas at higher concentration of dopant the emission is broadened and extends up to the red wavelength range. Our study indicates that high quality ZnO:Ag NW/NR prepared at low temperature by electrodeposition can serve as building nanomaterials for new sensors and light emitting diodes (LEDs) structures with low-power consumption.

UV-enhanced CO sensing using Ga 2O 3-based nanorod arrays at elevated temperature

DOE Office of Scientific and Technical Information (OSTI.GOV)

Lin, Hui-Jan; Gao, Haiyong; Gao, Pu-Xian

Monitoring and control of gaseous combustion process are critically important in advanced energy systems such as power plants, gas turbines, and automotive engines. However, very limited gas sensing solutions are available in the market for such application due to the inherent high temperature of combustion gaseous atmosphere. In this study, we fabricated and demonstrated high-performance metal oxide based nanorod array sensors assisted with ultra-violet (UV) illumination for in situ and real-time high-temperature gas detection. Without UV-illumination, it was found surface decoration of either 5 nm LSFO or 1 nm Pt nanoparticles can enhance the sensitivity over CO at 500 °Cmore » by an order of magnitude. Under the 254 nm UV illumination, CO gas-sensing performance of Ga 2O 3-based nanorod array sensors was further enhanced with the sensitivity boosted by 125 %, and the response time reduced by 30 % for La 0.8Sr 0.2FeO 3(LSFO)-decorated sample. The UV-enhanced detecting of CO might be due to the increased population of photo-induced electron-hole pairs. While for LSFO-decorated nanorod array sensor under UV illumination, the enhancement is through a combination of sensitizing effect and photocurrent effect.« less

UV-enhanced CO sensing using Ga 2O 3-based nanorod arrays at elevated temperature

DOE PAGES

Lin, Hui-Jan; Gao, Haiyong; Gao, Pu-Xian

2017-01-23

Monitoring and control of gaseous combustion process are critically important in advanced energy systems such as power plants, gas turbines, and automotive engines. However, very limited gas sensing solutions are available in the market for such application due to the inherent high temperature of combustion gaseous atmosphere. In this study, we fabricated and demonstrated high-performance metal oxide based nanorod array sensors assisted with ultra-violet (UV) illumination for in situ and real-time high-temperature gas detection. Without UV-illumination, it was found surface decoration of either 5 nm LSFO or 1 nm Pt nanoparticles can enhance the sensitivity over CO at 500 °Cmore » by an order of magnitude. Under the 254 nm UV illumination, CO gas-sensing performance of Ga 2O 3-based nanorod array sensors was further enhanced with the sensitivity boosted by 125 %, and the response time reduced by 30 % for La 0.8Sr 0.2FeO 3(LSFO)-decorated sample. The UV-enhanced detecting of CO might be due to the increased population of photo-induced electron-hole pairs. While for LSFO-decorated nanorod array sensor under UV illumination, the enhancement is through a combination of sensitizing effect and photocurrent effect.« less

UV-enhanced CO sensing using Ga2O3-based nanorod arrays at elevated temperature

NASA Astrophysics Data System (ADS)

Lin, Hui-Jan; Gao, Haiyong; Gao, Pu-Xian

2017-01-01

Monitoring and control of the gaseous combustion process are critically important in advanced energy systems such as power plants, gas turbines, and automotive engines. However, very limited gas sensing solutions are available in the market for such applications due to the inherent high temperature of the combustion gaseous atmosphere. In this study, we fabricated and demonstrated high-performance metal oxide based nanorod array sensors assisted with ultra-violet (UV) illumination for in situ and real-time high-temperature gas detection. Without UV-illumination, it was found that surface decoration of either 5 nm LSFO or 1 nm Pt nanoparticles can enhance the sensitivity over CO at 500 °C by an order of magnitude. Under the 254 nm UV illumination, the CO gas-sensing performance of Ga2O3-based nanorod array sensors was further enhanced with the sensitivity boosted by 125% and the response time reduced by 30% for the La0.8Sr0.2FeO3(LSFO)-decorated sample. The UV-enhanced detection of CO might be due to the increased population of photo-induced electron-hole pairs, whereas for LSFO-decorated nanorod array sensor under UV illumination, the enhancement is through a combination of the sensitizing effect and photocurrent effect.

Synthesis of Various Metal/TiO2 Core/shell Nanorod Arrays

NASA Astrophysics Data System (ADS)

Zhu, Wei; Wang, Guan-zhong; Hong, Xun; Shen, Xiao-shuang

2011-02-01

We present a general approach to fabricate metal/TiO2 core/shell nanorod structures by two-step electrodeposition. Firstly, TiO2 nanotubes with uniform wall thickness are prepared in anodic aluminum oxide (AAO) membranes by electrodeposition. The wall thickness of the nanotubes could be easily controlled by modulating the deposition time, and their outer diameter and length are only limited by the channel diameter and the thickness of the AAO membranes, respectively. The nanotubes' tops prepared by this method are open, while the bottoms are connected directly with the Au film at the back of the AAO membranes. Secondly, Pd, Cu, and Fe elements are filled into the TiO2 nanotubes to form core/shell structures. The core/shell nanorods prepared by this two-step process are high density and free-standing, and their length is dependent on the deposition time.

TiO2 nanocrystals decorated Z-schemed core-shell CdS-CdO nanorod arrays as high efficiency anodes for photoelectrochemical hydrogen generation.

PubMed

Li, Chia-Hsun; Hsu, Chan-Wei; Lu, Shih-Yuan

2018-07-01

TiO 2 nanocrystals decorated core-shell CdS-CdO nanorod arrays, TiO 2 @CdO/CdS NR, were fabricated as high efficiency anodes for photoelctrochemical hydrogen generation. The novel sandwich heterostructure was constructed from first growth of CdS nanorod arrays on a fluorine doped tin oxide (FTO) substrate with a hydrothermal process, followed by in situ generation of CdO thin films of single digit nanometers from the CdS nanorod surfaces through thermal oxidation, and final decoration of TiO 2 nanocrystals of 10-20 nm via a successive ionic layer absorption and reaction process. The core-shell CdS-CdO heterostructure possesses a Z-scheme band structure to enhance interfacial charge transfer, facilitating effective charge separation to suppress electron-hole recombination within CdS for much improved current density generation. The final decoration of TiO 2 nanocrystals passivates surface defects and trap states of CdO, further suppressing surface charge recombination for even higher photovoltaic conversion efficiencies. The photoelectrochemical performances of the plain CdS nanorod array were significantly improved with the formation of the sandwich heterostructure, achieving a photo current density of 3.2 mA/cm 2 at 1.23 V (vs. RHE), a 141% improvement over the plain CdS nanorod array and a 32% improvement over the CdO/CdS nanorod array. Copyright © 2018 Elsevier Inc. All rights reserved.

Density-controlled, solution-based growth of ZnO nanorod arrays via layer-by-layer polymer thin films for enhanced field emission

NASA Astrophysics Data System (ADS)

Weintraub, Benjamin; Chang, Sehoon; Singamaneni, Srikanth; Han, Won Hee; Choi, Young Jin; Bae, Joonho; Kirkham, Melanie; Tsukruk, Vladimir V.; Deng, Yulin

2008-10-01

A simple, scalable, and cost-effective technique for controlling the growth density of ZnO nanorod arrays based on a layer-by-layer polyelectrolyte polymer film is demonstrated. The ZnO nanorods were synthesized using a low temperature (T = 90 °C), solution-based method. The density-control technique utilizes a polymer thin film pre-coated on the substrate to control the mass transport of the reactant to the substrate. The density-controlled arrays were investigated as potential field emission candidates. The field emission results revealed that an emitter density of 7 nanorods µm-2 and a tapered nanorod morphology generated a high field enhancement factor of 5884. This novel technique shows promise for applications in flat panel display technology.

Electropolymerization of Uniform Polyaniline Nanorod Arrays on Conducting Oxides as Counter Electrodes in Dye-Sensitized Solar Cells.

PubMed

He, Ziming; Liu, Jing; Khoo, Si Yun; Tan, Timothy Thatt Yang

2016-01-01

Conventional techniques for the synthesis of oriented polyaniline (PANI) nanostructures are often complex or time consuming. Through an innovative reduced graphene oxide (rGO) modified FTO and a low-potential electropolymerization strategy, the rapid and template-free growth of a highly ordered PANI nanorod array on the FTO substrate is realized. The highly ordered nanostructure of the PANI array leads to a high electrocatalytic activity and chemical stability. The importance of the polymerization potential and rGO surface modification to achieve this nanostructure is revealed. Compared to platinum, the PANI nanorod array exhibits an enhanced performance and stability as counter electrodes in dye-sensitized solar cells, with a 17.6 % enhancement in power conversion efficiency. © 2016 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Vertically aligned p-type single-crystalline GaN nanorod arrays on n-type Si for heterojunction photovoltaic cells.

PubMed

Tang, Y B; Chen, Z H; Song, H S; Lee, C S; Cong, H T; Cheng, H M; Zhang, W J; Bello, I; Lee, S T

2008-12-01

Vertically aligned Mg-doped GaN nanorods have been epitaxially grown on n-type Si substrate to form a heterostructure for fabricating p-n heterojunction photovoltaic cells. The p-type GaN nanorod/n-Si heterojunction cell shows a well-defined rectifying behavior with a rectification ratio larger than 10(4) in dark. The cell has a high short-circuit photocurrent density of 7.6 mAlcm2 and energy conversion efficiency of 2.73% under AM 1.5G illumination at 100 mW/cm2. Moreover, the nanorod array may be used as an antireflection coating for solar cell applications to effectively reduce light loss due to reflection. This study provides an experimental demonstration for integrating one-dimensional nanostructure arrays with the substrate to directly fabricate heterojunction photovoltaic cells.

Vertically aligned ZnO nanorod core-polypyrrole conducting polymer sheath and nanotube arrays for electrochemical supercapacitor energy storage

PubMed Central

2014-01-01

Nanocomposite electrodes having three-dimensional (3-D) nanoscale architecture comprising of vertically aligned ZnO nanorod array core-polypyrrole (PPy) conducting polymer sheath and the vertical PPy nanotube arrays have been investigated for supercapacitor energy storage. The electrodes in the ZnO nanorod core-PPy sheath structure are formed by preferential nucleation and deposition of PPy layer over hydrothermally synthesized vertical ZnO nanorod array by controlled pulsed current electropolymerization of pyrrole monomer under surfactant action. The vertical PPy nanotube arrays of different tube diameter are created by selective etching of the ZnO nanorod core in ammonia solution for different periods. Cyclic voltammetry studies show high areal-specific capacitance approximately 240 mF.cm-2 for open pore and approximately 180 mF.cm-2 for narrow 30-to-36-nm diameter PPy nanotube arrays attributed to intensive faradic processes arising from enhanced access of electrolyte ions through nanotube interior and exterior. Impedance spectroscopy studies show that capacitive response extends over larger frequency domain in electrodes with PPy nanotube structure. Simulation of Nyquist plots by electrical equivalent circuit modeling establishes that 3-D nanostructure is better represented by constant phase element which accounts for the inhomogeneous electrochemical redox processes. Charge-discharge studies at different current densities establish that kinetics of the redox process in PPy nanotube electrode is due to the limitation on electron transport rather than the diffusive process of electrolyte ions. The PPy nanotube electrodes show deep discharge capability with high coulomb efficiency and long-term charge-discharge cyclic studies show nondegrading performance of the specific areal capacitance tested for 5,000 cycles. PMID:25246867

The alcohol-sensing behaviour of SnO2 nanorods prepared by a facile solid state reaction

NASA Astrophysics Data System (ADS)

Gao, F.; Ren, X. P.; Wan, W. J.; Zhao, Y. P.; Li, Y. H.; Zhao, H. Y.

2017-02-01

SnO2 nanorods with the range of 12-85 nm in diameter were fabricated by a facile solid state reaction in the medium of NaCl-KCl mixture at room temperature and calcined at 600, 680, 760 and 840 oC, respectively. The XRD, TEM and XPS were employed to characterize the structure and morphology of the SnO2 nanorods. The influence of the calcination temperature on the gas sensing behaviour of the SnO2 nanorods with different diameter was investigated. The result showed that all the sensors had good response to alcohol. The response of the gracile nanorods prepared at a low calcined temperature demonstrated significantly better than the thick nanorods prepared at a high calcined temperature. The mechanism was attributed to the nonstoichiometric ratio of Sn/O and larger surface area of the gracile nanorods to enhance the oxygen surface adsorption.

Hydrothermal synthesis of highly crystalline ZnO nanorod arrays: Dependence of morphology and alignment on growth conditions

DOE Office of Scientific and Technical Information (OSTI.GOV)

Azzez, Shrook A., E-mail: shurouq44@yahoo.com; Hassan, Z.; Alimanesh, M.

Highly oriented zinc oxide nanorod were successfully grown on seeded p-type silicon substrate by hydrothermal methode. The morphology and the crystallinty of ZnO c-axis (002) arrays were systematically studied using field emission scanning electron microscopy (FESEM) and X-ray diffraction (XRD) methods. The effect of seed layer pre-annealing on nanorods properties was explained according to the nucleation site of ZnO nanoparticles on silicon substrate. In addition, the variation of the equal molarity of zinc nitrate hexahydrate and hexamine concentrations in the reaction vessel play a crucial role related to the ZnO nanorods.

A patterned ZnO nanorod array/gas sensor fabricated by mechanoelectrospinning-assisted selective growth.

PubMed

Wang, Xiaomei; Sun, Fazhe; Huang, Yongan; Duan, Yongqing; Yin, Zhouping

2015-02-21

Micropatterned ZnO nanorod arrays were fabricated by the mechanoelectrospinning-assisted direct-writing process and the hydrothermal growth process, and utilized as gas sensors that exhibited excellent Ohmic behavior and sensitivity response to oxidizing gas NO2 at low concentrations (1-100 ppm).

Preparation and Photoacoustic Analysis of Cellular Vehicles Containing Gold Nanorods.

PubMed

Cavigli, Lucia; Tatini, Francesca; Borri, Claudia; Ratto, Fulvio; Centi, Sonia; Cini, Alberto; Lelli, Beatrice; Matteini, Paolo; Pini, Roberto

2016-05-02

Gold nanorods are attractive for a range of biomedical applications, such as the photothermal ablation and the photoacoustic imaging of cancer, thanks to their intense optical absorbance in the near-infrared window, low cytotoxicity and potential to home into tumors. However, their delivery to tumors still remains an issue. An innovative approach consists of the exploitation of the tropism of tumor-associated macrophages that may be loaded with gold nanorods in vitro. Here, we describe the preparation and the photoacoustic inspection of cellular vehicles containing gold nanorods. PEGylated gold nanorods are modified with quaternary ammonium compounds, in order to achieve a cationic profile. On contact with murine macrophages in ordinary Petri dishes, these particles are found to undergo massive uptake into endocytic vesicles. Then these cells are embedded in biopolymeric hydrogels, which are used to verify that the stability of photoacoustic conversion of the particles is retained in their inclusion into cellular vehicles. We are confident that these results may provide new inspiration for the development of novel strategies to deliver plasmonic particles to tumors.

Flexible asymmetric supercapacitors based upon Co9S8 nanorod//Co3O4@RuO2 nanosheet arrays on carbon cloth.

PubMed

Xu, Jing; Wang, Qiufan; Wang, Xiaowei; Xiang, Qingyi; Liang, Bo; Chen, Di; Shen, Guozhen

2013-06-25

We have successfully fabricated flexible asymmetric supercapacitors (ASCs) based on acicular Co9S8 nanorod arrays as positive materials and Co3O4@RuO2 nanosheet arrays as negative materials on woven carbon fabrics. Co9S8 nanorod arrays were synthesized by a hydrothermal sulfuration treatment of acicular Co3O4 nanorod arrays, while the RuO2 was directly deposited on the Co3O4 nanorod arrays. Carbon cloth was selected as both the substrate and the current collector for its good conductivity, high flexibility, good physical strength, and lightweight architecture. Both aqueous KOH solutions and polyvinyl alcohol (PVA)/KOH were employed as electrolyte for electrochemical measurements. The as-fabricated ASCs can be cycled reversibly in the range of 0-1.6 V and exhibit superior electrochemical performance with an energy density of 1.21 mWh/cm(3) at a power density of 13.29 W/cm(3) in aqueous electrolyte and an energy density of 1.44 mWh/cm(3) at the power density of 0.89 W/cm(3) in solid-state electrolyte, which are almost 10-fold higher than those reported in early ASC work. Moreover, they present excellent cycling performance at multirate currents and large currents after thousands of cycles. The high-performance nanostructured ASCs have significant potential applications in portable electronics and electrical vehicles.

Plasmon-enhanced Electrically Light-emitting from ZnO Nanorod Arrays/p-GaN Heterostructure Devices

PubMed Central

Lu, Junfeng; Shi, Zengliang; Wang, Yueyue; Lin, Yi; Zhu, Qiuxiang; Tian, Zhengshan; Dai, Jun; Wang, Shufeng; Xu, Chunxiang

2016-01-01

Effective and bright light-emitting-diodes (LEDs) have attracted broad interests in fundamental research and industrial application, especially on short wavelength LEDs. In this paper, a well aligned ZnO nanorod arrays grown on the p-GaN substrate to form a heterostructured light-emitting diode and Al nanoparticles (NPs) were decorated to improve the electroluminescence performance. More than 30-folds enhancement of the electroluminescence intensity was obtained compared with the device without Al NPs decoration. The investigation on the stable and transient photoluminescence spectraof the ZnO nanorod arrays before and after Al NPs decoration demonstrated that the metal surface plasmon resonance coupling with excitons of ZnO leads to the enhancement of the internal quantum efficiency (IQE). Our results provide aneffective approach to design novel optoelectronic devices such as light-emitting diodes and plasmonic nanolasers. PMID:27181337

Plasmon-enhanced Electrically Light-emitting from ZnO Nanorod Arrays/p-GaN Heterostructure Devices.

PubMed

Lu, Junfeng; Shi, Zengliang; Wang, Yueyue; Lin, Yi; Zhu, Qiuxiang; Tian, Zhengshan; Dai, Jun; Wang, Shufeng; Xu, Chunxiang

2016-05-16

Effective and bright light-emitting-diodes (LEDs) have attracted broad interests in fundamental research and industrial application, especially on short wavelength LEDs. In this paper, a well aligned ZnO nanorod arrays grown on the p-GaN substrate to form a heterostructured light-emitting diode and Al nanoparticles (NPs) were decorated to improve the electroluminescence performance. More than 30-folds enhancement of the electroluminescence intensity was obtained compared with the device without Al NPs decoration. The investigation on the stable and transient photoluminescence spectraof the ZnO nanorod arrays before and after Al NPs decoration demonstrated that the metal surface plasmon resonance coupling with excitons of ZnO leads to the enhancement of the internal quantum efficiency (IQE). Our results provide aneffective approach to design novel optoelectronic devices such as light-emitting diodes and plasmonic nanolasers.

ZnO/perovskite core–shell nanorod array based monolithic catalysts with enhanced propane oxidation and material utilization efficiency at low temperature

DOE PAGES

Wang, Sibo; Ren, Zheng; Song, Wenqiao; ...

2015-04-24

Here, a hydrothermal strategy combined with colloidal deposition synthesis was successfully used to grow ZnO/perovskite (LaBO 3, B=Mn, Co, Ni) core-shell nanorod arrays within three dimensional (3-D) honeycomb cordierite substrates. A facile sonication assisted colloidal wash coating process is able to coat a uniformly dispersed perovskite nanoparticles onto the large scale ZnO nanorod arrays rooted on the channel surfaces of the 3D cordierite substrate achieved by hydrothermal synthesis. Compared to traditional wash-coated perovskite catalysts, an enhanced catalytic performance was observed for propane oxidation with 25°C lower light-off temperature than wash-coated perovskite catalyst of similar LaMnO 3 loading (4.3mg). Temperature programmedmore » reduction and desorption under H 2 and O 2 atmosphere, respectively, were used to study the reducibility and oxygen activity of these core-shell nanorod arrays based monolithic catalysts, revealing a catalytic activity sequence of LaCoO 3>LaMnO 3>La 2NiO 4 at the initial stage of catalytic reaction. The good dispersion and size control in La-based perovskite nanoparticles and their interfaces to ZnO nanorod arrays support may contribute to the enhancement of catalytic performance. Lastly, this work may provide a new type of Pt-group metals (PGM) free catalysts with improved catalytic performance for hydrocarbon oxidations at low temperatures.« less

Pt-Ni/WC Alloy Nanorods Arrays as ORR Catalyst for PEM Fuel Cells

DOE Office of Scientific and Technical Information (OSTI.GOV)

Begum, Mahbuba; Yurukcu, Mesut; Yurtsever, Fatma

Polymer electrolyte membrane fuel cells (PEMFCs) among the other types of fuel cell technology are attractive power sources, especially for electric vehicle applications. While significant progress and plausible prospects of PEMFCs have been achieved, there are still some challenges related to the performance, durability, and cost that need to be overcome to make them economically viable for widespread commercialization. Our strategy is to develop thin films of high-active and stable catalyst coated on vertically aligned nanorod arrays of conductive and stable support. In this work, we fabricated tungsten carbide (WC) nanorods as support and coated them with a platinum-nickel (Pt-Ni)more » alloy shell denoted as Pt-Ni/WC catalysts. The Pt- Ni/WC nanorods were deposited on glassy carbon disks as well as on silicon substrates for evaluation of their electrocatalytic oxygen reduction reaction (ORR) activity and physical properties. Cyclic voltammetry experiments using rotating disk electrode were performed in perchloric acid (0.1 M HClO4) electrolyte at room temperature to characterize the ORR activity and stability of Pt-Ni/WC nanorods catalysts. Scanning electron microscopy and X-ray diffraction techniques were utilized to study the morphology and crystallographic properties, respectively.« less

Optimized emission in nanorod arrays through quasi-aperiodic inverse design.

PubMed

Anderson, P Duke; Povinelli, Michelle L

2015-06-01

We investigate a new class of quasi-aperiodic nanorod structures for the enhancement of incoherent light emission. We identify one optimized structure using an inverse design algorithm and the finite-difference time-domain method. We carry out emission calculations on both the optimized structure as well as a simple periodic array. The optimized structure achieves nearly perfect light extraction while maintaining a high spontaneous emission rate. Overall, the optimized structure can achieve a 20%-42% increase in external quantum efficiency relative to a simple periodic design, depending on material quality.

Electromagnetic enhancement of ordered silver nanorod arrays evaluated by discrete dipole approximation.

PubMed

Wei, Guoke; Wang, Jinliang; Chen, Yu

2015-01-01

The enhancement factor (EF) of surface-enhanced Raman scattering (SERS) from two-dimensional (2D) hexagonal silver nanorod (AgNR) arrays were investigated in terms of electromagnetic (EM) mechanism by using the discrete dipole approximation (DDA) method. The dependence of EF on several parameters, i.e., structure, length, excitation wavelength, incident angle and polarization, and gap size has been investigated. "Hotspots" were found distributed in the gaps between adjacent nanorods. Simulations of AgNR arrays of different lengths revealed that increasing the rod length from 374 to 937 nm (aspect ratio from 2.0 to 5.0) generated more "hotspots" but not necessarily increased EF under both 514 and 532 nm excitation. A narrow lateral gap (in the incident plane) was found to result in strong EF, while the dependence of EF on the diagonal gap (out of the incident plane) showed an oscillating behavior. The EF of the array was highly dependent on the angle and polarization of the incident light. The structure of AgNR and the excitation wavelength were also found to affect the EF. The EF of random arrays was stronger than that of an ordered one with the same average gap of 21 nm, which could be explained by the exponential dependence of EF on the lateral gap size. Our results also suggested that absorption rather than extinction or scattering could be a good indicator of EM enhancement. It is expected that the understanding of the dependence of local field enhancement on the structure of the nanoarrays and incident excitations will shine light on the optimal design of efficient SERS substrates and improved performance.

III-nitride core–shell nanorod array on quartz substrates

PubMed Central

Bae, Si-Young; Min, Jung-Wook; Hwang, Hyeong-Yong; Lekhal, Kaddour; Lee, Ho-Jun; Jho, Young-Dahl; Lee, Dong-Seon; Lee, Yong-Tak; Ikarashi, Nobuyuki; Honda, Yoshio; Amano, Hiroshi

2017-01-01

We report the fabrication of near-vertically elongated GaN nanorods on quartz substrates. To control the preferred orientation and length of individual GaN nanorods, we combined molecular beam epitaxy (MBE) with pulsed-mode metal–organic chemical vapor deposition (MOCVD). The MBE-grown buffer layer was composed of GaN nanograins exhibiting an ordered surface and preferred orientation along the surface normal direction. Position-controlled growth of the GaN nanorods was achieved by selective-area growth using MOCVD. Simultaneously, the GaN nanorods were elongated by the pulsed-mode growth. The microstructural and optical properties of both GaN nanorods and InGaN/GaN core–shell nanorods were then investigated. The nanorods were highly crystalline and the core–shell structures exhibited optical emission properties, indicating the feasibility of fabricating III-nitride nano-optoelectronic devices on amorphous substrates. PMID:28345641

High-performance optical projection controllable ZnO nanorod arrays for microweighing sensors.

PubMed

Wang, Hongbo; Jiang, Shulan; Zhang, Lei; Yu, Bingjun; Chen, Duoli; Yang, Weiqing; Qian, Linmao

2018-03-08

Optical microweighing sensors are an essential component of micro-force measurements in physical, chemical, and biological detection fields, although, their limited detection range (less than 15°) severely hinders their wide application. Such a limitation is mainly attributed to the essential restrictions of traditional light reflection and optical waveguide modes. Here, we report a high-performance optical microweighing sensor based on the synergistic effects of both a new optical projection mode and a ZnO nanorod array sensor. Ascribed to the unique configuration design of this sensing method, this optical microweighing sensor has a wide detection range (more than 80°) and a high sensitivity of 90 nA deg -1 , which is much larger than that of conventional microcantilever-based optical microweighing sensors. Furthermore, the location of the UV light source can be adjusted within a few millimeters, meaning that the microweighing sensor does not need repetitive optical calibration. More importantly, for low height and small incident angles of the UV light source, we can obtain highly sensitive microweighing properties on account of the highly sensitive ZnO nanorod array-based UV sensor. Therefore, this kind of large detection range, non-contact, and non-destructive microweighing sensor has potential applications in air quality monitoring and chemical and biological detection.

Large enhancement of X-ray excited luminescence in Ga-doped ZnO nanorod arrays by hydrogen annealing

NASA Astrophysics Data System (ADS)

Li, Qianli; Liu, Xiaoliln; Gu, Mu; Li, Fengrui; Zhang, Juannan; Wu, Qiang; Huang, Shiming; Liu, Si

2018-03-01

Highly c-axis oriented and densely packed ZnO:Ga nanorod arrays were fabricated on ZnO-seeded substrates by hydrothermal method, and the effect of hydrogen annealing on their morphology, structure and luminescence properties was investigated in detail. Under ultraviolet or X-ray excitation, an intense ultraviolet luminescence appeared in the hydrogen-annealed samples owing to the formation of a shallow hydrogen donor state, which can sharply activate the reconbination radiation. The luminescence intensity increased with the annealing temperature, and then decreased at a higher temperature due to the dissociation of the hydrogen ion. The optimum concentration and time of hydrogen annealing were acquired simultaneously. It is expected that the ZnO:Ga nanorod array is a promising candidate for application in ultrafast and high-spatial-resolution X-ray imaging detector.

Preparation, characterization and electroluminescence studies of ZnO nanorods for optoelectronic device applications

DOE Office of Scientific and Technical Information (OSTI.GOV)

Singh, Anju, E-mail: singh-nk24@yahoo.com; Vishwakarma, H. L., E-mail: horilal5@yahoo.com

2015-07-31

In this work, ZnO nanorods were achieved by a simple chemical precipitation method in the presence of capping agent Poly Vinyl Pyrrolidone (PVP) at room temperature. X-Ray Diffraction (XRD) result indicates that the synthesized undoped ZnO nanorods have wurtzite hexagonal structure without any impurities. It has been seen that the growth orientation of the prepared ZnO nanorods were (101). XRD analysis revealed that the nanorods having the crystallite size 49 nm. The Scanning Electron Microscopy (SEM) image confirmed the size and shape of these nanorods. The diameter of nanorods has been found that 1.52 µm to 1.61 µm and the lengthmore » of about 4.89 µm. It has also been found that at room temperature Ultra Violet Visible (UV-VIS) absorption band is around 355 nm (blue shifted as compared to bulk). Electroluminescence (EL) studies show that emission of light is possible at very small threshold voltage and increases rapidly with increasing applied voltage. It is seen that smaller ZnO nanoparticles give higher electroluminescence brightness starting at lower threshold voltage. The brightness is also affected by increasing the frequency of AC signal.« less

Facile green in situ synthesis of Mg/CuO core/shell nanoenergetic arrays with a superior heat-release property and long-term storage stability.

PubMed

Zhou, Xiang; Xu, Daguo; Zhang, Qiaobao; Lu, Jian; Zhang, Kaili

2013-08-14

We report a facile green method for the in situ synthesis of Mg/CuO core/shell nanoenergetic arrays on silicon, with Mg nanorods as the core and CuO as the shell. Mg nanorods are first prepared by glancing angle deposition. CuO is then deposited around the Mg nanorods by reactive magnetron sputtering to realize the core/shell structure. Various characterization techniques are used to investigate the prepared Mg/CuO core/shell nanoenergetic arrays, including scanning electron microscopy, transmission electron microscopy, X-ray energy dispersive spectroscopy, X-ray diffraction, and thermal analysis. Uniform mixing and intimate contact between the Mg nanorods and CuO are confirmed from both visual inspection of the morphological images and analyses of the heat-release curves. The nanoenergetic arrays exhibit a low-onset reaction temperature (∼300 °C) and high heat of reaction (∼3400 J/g). Most importantly, the nanoenergetic arrays possess long-term storage stability resulting from the stable CuO shell. This study provides a potential general strategy for the synthesis of various Mg nanorod-based stable nanoenergetic arrays.

Low temperature grown ZnO@TiO{sub 2} core shell nanorod arrays for dye sensitized solar cell application

DOE Office of Scientific and Technical Information (OSTI.GOV)

Goh, Gregory Kia Liang; Le, Hong Quang, E-mail: lehq@imre.a-star.edu.sg; Huang, Tang Jiao

High aspect ratio ZnO nanorod arrays were synthesized on fluorine-doped tin oxide glasses via a low temperature solution method. By adjusting the growth condition and adding polyethylenimine, ZnO nanorod arrays with tunable length were successfully achieved. The ZnO@TiO{sub 2} core shells structures were realized by a fast growth method of immersion into a (NH{sub 4}){sub 2}·TiF{sub 6} solution. Transmission electron microscopy, X-ray Diffraction and energy dispersive X-ray measurements all confirmed the existence of a titania shell uniformly covering the ZnO nanorod's surface. Results of solar cell testing showed that addition of a TiO{sub 2} shell to the ZnO nanorod significantlymore » increased short circuit current (from 4.2 to 5.2 mA/cm{sup 2}), open circuit voltage (from 0.6 V to 0.8 V) and fill factor (from 42.8% to 73.02%). The overall cell efficiency jumped from 1.1% for bare ZnO nanorod to 3.03% for a ZnO@TiO{sub 2} core shell structured solar cell with a 18–22 nm shell thickness, a nearly threefold increase. - Graphical abstract: The synthesis process of coating TiO{sub 2} shell onto ZnO nanorod core is shown schematically. A thin, uniform, and conformal shell had been grown on the surface of the ZnO core after immersing in the (NH{sub 4}){sub 2}·TiF{sub 6} solution for 5–15 min. - Highlights: • ZnO@TiO{sub 2} core shell nanorod has been grown on FTO substrate using low temperature solution method. • TEM, XRD, EDX results confirmed the existing of titana shell, uniformly covered rod's surface. • TiO{sub 2} shell suppressed recombination, demonstrated significant enhancement in cell's efficiency. • Core shell DSSC's efficiency achieved as high as 3.03%, 3 times higher than that of ZnO nanorods.« less

Self-Supported CoP Nanorod Arrays Grafted on Stainless Steel as an Advanced Integrated Anode for Stable and Long-Life Lithium-Ion Batteries.

PubMed

Xu, Xijun; Liu, Jun; Hu, Renzong; Liu, Jiangwen; Ouyang, Liuzhang; Zhu, Min

2017-04-19

To alleviate the capacity degradation of anode materials for Li-ion batteries, caused by serious volume expansion and particle aggregation, intensive attention has been devoted to the rational design and fabrication of novel anode architectures. Herein, self-supported CoP nanorod arrays have been facilely synthesized using hydrothemally deposited Co(CO 3 ) 0.5 (OH)⋅0.11 H 2 O nanorod arrays as the precursor, through a gas-phase phosphidation method. As the anode for Li-ion batteries, such 3D interconnected CoP nanorod arrays show an initial discharge capacity of 1067 mAh g -1 and a high reversible charge capacity of 737 mAh g -1 at 0.4 Ag -1 . After 400 cycles, their specific capacity can reach 510 mAh g -1 ; even after 900 cycles, they can still deliver a specific capacity of 390 mAh g -1 . CoP//LiCoO 2 full-cells also exhibit a high reversible capacity of 400 mAh g -1 after 50 cycles. These unique 3D interconnected CoP nanorod arrays also show ultrastable cycling performance over 500 cycles when used as the anode in a Na-ion battery. © 2017 Wiley-VCH Verlag GmbH & Co. KGaA, Weinheim.

Pr3+ doped biphasic TiO2 (rutile-brookite) nanorod arrays grown on activated carbon fibers: Hydrothermal synthesis and photocatalytic properties

NASA Astrophysics Data System (ADS)

Li, Min; Zhang, Xiaomei; Liu, Ying; Yang, Yi

2018-05-01

Praseodymium-doped biphasic TiO2 (rutile-brookite) nanorod arrays (Pr-TiO2 NRAs) were successfully prepared via a two-step hydrothermal reaction on activated carbon fibers (ACFs) which pre-coated with TiO2 nanoparticles at first step. The bicrystalline arrays grown on ACFs are primarily constructed by the well-aligned TiO2 nanorods growing along [0 0 1] direction, which were indicated by the results of SEM and XRD. The nanorods are uniform in diameter and length with about 250 nm and 2.5 μm. The composite photocatalyst with high specific surface area and well-aligned nanostructure are beneficial to enhance the adsorption capacity and even help to suppress electron-hole recombination effectively, which consequently revealed much better (2 times) catalytic performance than that of commercially available P25 TiO2 on methylene blue(MB) photodegradation. In addition, the existence of praseodymium in TiO2 gives rise to shift of absorption edge towards long wavelength, which was indicated by the results of UV-vis DRS. Photodegradation results reveal that Pr-doping significantly improves the activity of TiO2, which was 20% higher than that of undoped TiO2 NRAs for the photodegradation of MB in aqueous medium under visible light irradiation. Meanwhile, the doped amount of Pr had a tiny influence on the photocatalytic performance of the composites. In our experiment, 3% Pr-doped molar concentration was proven to be the relatively optimal dopant concentration for the doping of TiO2 NRAs. Moreover, the photocatalyst grown on ACFs substrates is favorable to reuse and photodegradation rate kept on 76% even after 4 times of reuse.

Hierarchical nanorods constructed by Mn2Mo3O8@reduced graphene oxide nanosheet arrays with enhanced lithium storage properties

NASA Astrophysics Data System (ADS)

Zhang, Lifeng; Shen, Kechao; He, Wenjie; Liu, Yi; Yin, Lixiong; Guo, Shouwu

2018-10-01

3D hierarchical nanorods of Mn2Mo3O8@reduced graphene oxide (rGO) nanohybrid assembled with nanosheet arrays have been fabricated via a facile solvothermal process combined with subsequent anneal. It is identified that the annealing temperature and the input amount of graphene oxide (GO) are critical to form such unique Mn2Mo3O8@rGO nanostructure, whose hierarchical nanorods (ca. 470 nm of diameter) are constructed by vertical nanosheet arrays (30 ± 5 nm average thickness for individual nanosheet). As an anode material for lithium ion batteries, the hierarchical Mn2Mo3O8@rGO electrode delivers superior capability and rate properties to the compared nanostructure synthesized at different annealing temperature. The enhanced electrochemical performance is attributed to the rational combination of 3D nanorods and 2D nanosheets, which is beneficial to the fast penetration of electrolytes and thus provide more reactive facets, shorten the diffusion paths of Li+ and facilitate the electron conduction.

Role of Ag2S coupling on enhancing the visible-light-induced catalytic property of TiO2 nanorod arrays

NASA Astrophysics Data System (ADS)

Li, Zhengcao; Xiong, Shan; Wang, Guojing; Xie, Zheng; Zhang, Zhengjun

2016-01-01

In order to obtain a better photocatalytic performance under visible light, Ag2S-coupled TiO2 nanorod arrays (NRAs) were prepared through the electron beam deposition with glancing angle deposition (GLAD) technique, annealing in air, followed by the successive ionic layer absorption and reaction (SILAR) method. The properties of the photoelectrochemical and photocatalytic degradation of methyl orange (MO) were thus conducted. The presence of Ag2S on TiO2 NRAs was observed to have a significant improvement on the response to visible light. It’s resulted from that Ag2S coupling can improve the short circuit photocurrent density and enhance the photocatalytic activity remarkably.

Role of Ag2S coupling on enhancing the visible-light-induced catalytic property of TiO2 nanorod arrays

PubMed Central

Li, Zhengcao; Xiong, Shan; Wang, Guojing; Xie, Zheng; Zhang, Zhengjun

2016-01-01

In order to obtain a better photocatalytic performance under visible light, Ag2S-coupled TiO2 nanorod arrays (NRAs) were prepared through the electron beam deposition with glancing angle deposition (GLAD) technique, annealing in air, followed by the successive ionic layer absorption and reaction (SILAR) method. The properties of the photoelectrochemical and photocatalytic degradation of methyl orange (MO) were thus conducted. The presence of Ag2S on TiO2 NRAs was observed to have a significant improvement on the response to visible light. It’s resulted from that Ag2S coupling can improve the short circuit photocurrent density and enhance the photocatalytic activity remarkably. PMID:26790759

Bias-polarity-dependent UV/visible transferable electroluminescence from ZnO nanorod array LED with graphene oxide electrode supporting layer

NASA Astrophysics Data System (ADS)

Liu, Weizhen; Wang, Wei; Xu, Haiyang; Li, Xinghua; Yang, Liu; Ma, Jiangang; Liu, Yichun

2015-09-01

A simple top electrode preparation process, employing continuous graphene oxide films as electrode supporting layers, was adopted to fabricate a ZnO nanorod array/p-GaN heterojunction LED. The achieved LED demonstrated different electroluminescence behaviors under forward and reverse biases: a yellow-red emission band was observed under forward bias, whereas a blue-UV emission peak was obtained under reverse bias. Electroluminescence spectra under different currents and temperatures, as well as heterojunction energy-band alignments, reveal that the yellow-red emission under forward bias originates from recombinations related to heterointerface defects, whereas the blue-UV electroluminescence under reverse bias is ascribed to transitions from near-band-edge and Mg-acceptor levels in p-GaN.

Directed self-assembly of nanorod networks: bringing the top down to the bottom up.

PubMed

Einsle, Joshua F; Scheunert, Gunther; Murphy, Antony; McPhillips, John; Zayats, Anatoly V; Pollard, Robert; Bowman, Robert M

2012-12-21

Self-assembled electrodeposited nanorod materials have been shown to offer an exciting landscape for a wide array of research ranging from nanophotonics through to biosensing and magnetics. However, until now, the scope for site-specific preparation of the nanorods on wafers has been limited to local area definition. Further there is little or no lateral control of nanorod height. In this work we present a scalable method for controlling the growth of the nanorods in the vertical direction as well as their lateral position. A focused ion beam pre-patterns the Au cathode layer prior to the creation of the anodized aluminium oxide (AAO) template on top. When the pre-patterning is of the same dimension as the pore spacing of the AAO template, lines of single nanorods are successfully grown. Further, for sub-200 nm wide features, a relationship between the nanorod height and distance from the non-patterned cathode can be seen to follow a quadratic growth rate obeying Faraday's law of electrodeposition. This facilitates lateral control of nanorod height combined with localized growth of the nanorods.

Large-scale fabrication of polymer/Ag core-shell nanorod array as flexible SERS substrate by combining direct nanoimprint and electroless deposition

NASA Astrophysics Data System (ADS)

Liu, Sisi; Xu, Zhimou; Sun, Tangyou; Zhao, Wenning; Wu, Xinghui; Ma, Zhichao; Xu, Haifeng; He, Jian; Chen, Cunhua

2014-06-01

We demonstrate a highly sensitive surface-enhanced Raman scattering (SERS) substrate, which consists of Ag nanoparticles (NPs) assembled on the surface of a nanopatterned polymer film. The fabrication route of a polymer/Ag core-shell nanorod (PACSN) array employed a direct nanoimprint technique to create a high-resolution polymer nanorod array. The obtained nanopatterned polymer film was subjected to electroless deposition to form a sea-cucumber-like Ag shell over the surface of the polymer nanorod. The morphology and structures of PACSNs were analyzed by using scanning electron microscopy and X-ray diffraction. The as-synthesized PACSNs exhibited a remarkable SERS activity and Raman signal reproducibility to rhodamine 6G, and a concentration down to 10-12 M can be identified. The effect of electroless deposition time of Ag NPs onto the polymer nanorod surface was investigated. It was found that the electroless deposition time played an important role in SERS activity. Our results revealed that the combination of direct nanoimprint and electroless deposition provided a convenient and cost-effective way for large-scale fabrication of reliable SERS substrates without the requirement of expensive instruments.

Highly exothermic and superhydrophobic Mg/fluorocarbon core/shell nanoenergetic arrays.

PubMed

Zhou, Xiang; Xu, Daguo; Yang, Guangcheng; Zhang, Qiaobao; Shen, Jinpeng; Lu, Jian; Zhang, Kaili

2014-07-09

Mg/fluorocarbon core/shell nanoenergetic arrays are prepared onto silicon substrate, with Mg nanorods as the core and fluorocarbon as the shell. Mg nanorods are deposited by the glancing angle deposition technique, and the fluorocarbon layer is then prepared as a shell to encase the Mg nanorods by the magnetron sputtering deposition process. Scanning electron microscopy and transmission electron microscopy show the core/shell structure of the Mg/fluorocarbon arrays. X-ray energy-dispersive spectroscopy, X-ray diffraction, and Fourier transform infrared spectroscopy are used to characterize the structural composition of the Mg/fluorocarbon. It is found that the as-prepared fluorocarbon layer consists of shorter molecular chains compared to that of bulk polytetrafluoroethylene, which is proven beneficial to the low onset reaction temperature of Mg/fluorocarbon. Water contact angle test demonstrates the superhydrophobicity of the Mg/fluorocarbon arrays, and a static contact angle as high as 162° is achieved. Thermal analysis shows that the Mg/fluorocarbon material exhibits a very low onset reaction temperature of about 270 °C as well as an ultrahigh heat of reaction approaching 9 kJ/g. A preliminary combustion test reveals rapid combustion wave propagation, and a convective mechanism is adopted to explain the combustion behaviors.

Effect of growth time to the properties of Al-doped ZnO nanorod arrays

NASA Astrophysics Data System (ADS)

Ismail, A. S.; Mamat, M. H.; Malek, M. F.; Saidi, S. A.; Yusoff, M. M.; Mohamed, R.; Sin, N. D. Md; Suriani, A. B.; Rusop, M.

2018-05-01

Aluminum (Al)-doped zinc oxide (ZnO) nanorod array films were successfully deposited at different growth time on zinc oxide (ZnO) seed layer coated glass substrate using sol-gel immersion method. The morphology images of the films showed that the thicknesses of the films were increased parallel with the increment of growth period. The surface topology of the films displayed an increment of roughness as the growth period increased. Optical properties of the samples exposed that the percentage of transmittances reduced at higher growth time. Besides, the Urbach energy of the films slightly increased as the immersion time increased. The current-voltage (I-V) measurement indicated that the resistance increased as the immersion time increased owing to the appearance of intrinsic layer on top of the nanorods.

The Effect of Eu Doping on Microstructure, Morphology and Methanal-Sensing Performance of Highly Ordered SnO2 Nanorods Array

PubMed Central

Zhao, Yanping; Li, Yuehua; Ren, Xingping; Gao, Fan; Zhao, Heyun

2017-01-01

Layered Eu-doped SnO2 ordered nanoarrays constructed by nanorods with 10 nm diameters and several hundred nanometers length were synthesized by a substrate-free hydrothermal route using alcohol and water mixed solvent of sodium stannate and sodium hydroxide at 200 °C. The Eu dopant acted as a crystal growth inhibitor to prevent the SnO2 nanorods growth up, resulting in tenuous SnO2 nanorods ordered arrays. The X-ray diffraction (XRD) revealed the tetragonal rutile-type structure with a systematic average size reduction and unit cell volume tumescence, while enhancing the residual strain as the Eu-doped content increases. The surface defects that were caused by the incorporation of Eu ions within the surface oxide matrix were observed by high-resolution transmission electron microscope (HRTEM). The results of the response properties of sensors based on the different levels of Eu-doped SnO2 layered nanoarrays demonstrated that the 0.5 at % Eu-doped SnO2 layered nanorods arrays exhibited an excellent sensing response to methanal at 278 °C. The reasons of the enhanced sensing performance were discussed from the complicated defect surface structure, the large specific surface area, and the excellent catalytic properties of Eu dopant. PMID:29168796

Synthesis and Self-Assembly of fcc Phase FePt Nanorods

DOE Office of Scientific and Technical Information (OSTI.GOV)

Chen, Min; Pica, Timothy; Jiang, Ying-Bing

2007-05-01

In this paper, we report a synthesis of FePt nanorods by confining decomposition of Fe(CO) 5 and reduction of Pt(caca) 2 in surfactant reverse cylindrical micelles. The controlled nucleation and growth kinetics in confined environment allows easy control over Fe/Pt composition, nanorod uniformity, and nanorod aspect ratio. The FePt nanorods tend to self-assemble into ordered arrays along three-dimensions. Directed assembly under external magnetic field leads to two-dimensional ordered arrays, parallel to the substrate magnetic field. We expect that with optimized external magnetic fields, we should be able to assemble these nanorods into orientated one or two-dimensional arrays, providing a uniformmore » anisotropic magnetic platform for varied applications in enhanced data storage, magneto-electron transport, etc.« less

Semiconductor@metal-organic framework core-shell heterostructures: a case of ZnO@ZIF-8 nanorods with selective photoelectrochemical response.

PubMed

Zhan, Wen-wen; Kuang, Qin; Zhou, Jian-zhang; Kong, Xiang-jian; Xie, Zhao-xiong; Zheng, Lan-sun

2013-02-06

Metal-organic frameworks (MOFs) and related material classes are attracting considerable attention for their applications in gas storage/separation as well as catalysis. In contrast, research concerning potential uses in electronic devices (such as sensors) is in its infancy, which might be due to a great challenge in the fabrication of MOFs and semiconductor composites with well-designed structures. In this paper, we proposed a simple self-template strategy to fabricate metal oxide semiconductor@MOF core-shell heterostructures, and successfully obtained freestanding ZnO@ZIF-8 nanorods as well as vertically standing arrays (including nanorod arrays and nanotube arrays). In this synthetic process, ZnO nanorods not only act as the template but also provide Zn(2+) ions for the formation of ZIF-8. In addition, we have demonstrated that solvent composition and reaction temperature are two crucial factors for successfully fabricating well-defined ZnO@ZIF-8 heterostructures. As we expect, the as-prepared ZnO@ZIF-8 nanorod arrays display distinct photoelectrochemical response to hole scavengers with different molecule sizes (e.g., H(2)O(2) and ascorbic acid) owing to the limitation of the aperture of the ZIF-8 shell. Excitingly, such ZnO@ZIF-8 nanorod arrays were successfully applied to the detection of H(2)O(2) in the presence of serous buffer solution. Therefore, it is reasonable to believe that the semiconductor@MOFs heterostructure potentially has promising applications in many electronic devices including sensors.

Growing vertical ZnO nanorod arrays within graphite: efficient isolation of large size and high quality single-layer graphene.

PubMed

Ding, Ling; E, Yifeng; Fan, Louzhen; Yang, Shihe

2013-07-18

We report a unique strategy for efficiently exfoliating large size and high quality single-layer graphene directly from graphite into DMF dispersions by growing ZnO nanorod arrays between the graphene layers in graphite.

In situ formation of a ZnO/ZnSe nanonail array as a photoelectrode for enhanced photoelectrochemical water oxidation performance

NASA Astrophysics Data System (ADS)

Wang, Liyang; Tian, Guohui; Chen, Yajie; Xiao, Yuting; Fu, Honggang

2016-04-01

In this study, a ZnO/ZnSe nanonail array was prepared via a two-step sequential hydrothermal synthetic route. In this synthetic process, the ZnO nanorod array was first grown on a fluorine-doped tin oxide (FTO) substrate using a seed-mediated growth approach via the hydrothermal process. Then, the ZnO nanonail array was obtained via in situ growth of ZnSe nano caps onto the ZnO nanorod array via a hydrothermal process in the presence of a Se source. The surface morphology and amount of ZnSe grown on the surface of the ZnO nanorods can be regulated by varying the reaction time and reactant concentration. Compared with pure ZnO nanorods, this unique nanonail array heterostructure exhibits enhanced visible light absorption. The transient photocurrent condition, in combination with steady-state and time-resolved photoluminescence spectroscopy, reveals that the ZnO/ZnSe nanonail array electrode has the highest charge separation rate, highest electron injection efficiency, and highest chemical stability. The photocurrent density of the ZnO/ZnSe nanonail array heterostructure reaches 1.01 mA cm-2 at an applied potential of 0.1 V (vs. Ag/AgCl), which is much higher than that of the ZnO/ZnSe nanorod array (0.71 mA cm-2), the pristine ZnO nanorod array (0.39 mA cm-2), and the ZnSe electrode (0.21 mA cm-2), indicating its significant visible light driven activities for photoelectrochemical water oxidation. This unique morphology of nail-capped nanorods might be important for providing better insight into the correlation between heterostructure and photoelectrochemical activity.In this study, a ZnO/ZnSe nanonail array was prepared via a two-step sequential hydrothermal synthetic route. In this synthetic process, the ZnO nanorod array was first grown on a fluorine-doped tin oxide (FTO) substrate using a seed-mediated growth approach via the hydrothermal process. Then, the ZnO nanonail array was obtained via in situ growth of ZnSe nano caps onto the ZnO nanorod array via a

Significant enhancement of yellow-green light emission of ZnO nanorod arrays using Ag island films

NASA Astrophysics Data System (ADS)

Lin, Chin-An; Tsai, Dung-Sheng; Chen, Cheng-Ying; He-Hau, Jr.

2011-03-01

Surface plasmon (SP) mediated emission from ZnO nanorod arrays (NRAs)/Ag/Si structures has been investigated. The ratio of visible emission to UV emission can be increased by over 30 times via coupling with SP without deterioration of the crystal quality. The fact that the effect of SP crucially depends on the size of Ag island films provides the feasibility to significantly enhance the yellow-green emission of the ZnO nanostructures without sacrificing the crystallinity of ZnO.Surface plasmon (SP) mediated emission from ZnO nanorod arrays (NRAs)/Ag/Si structures has been investigated. The ratio of visible emission to UV emission can be increased by over 30 times via coupling with SP without deterioration of the crystal quality. The fact that the effect of SP crucially depends on the size of Ag island films provides the feasibility to significantly enhance the yellow-green emission of the ZnO nanostructures without sacrificing the crystallinity of ZnO. Electronic supplementary information (ESI) available. See DOI: 10.1039/c0nr00732c

Quick and Selective Dual Mode Detection of H2S Gas by Mobile App Employing Silver Nanorods Array.

PubMed

Gahlaut, Shashank Kumar; Yadav, Kavita; Sharan, Chandrashekhar; Singh, Jitendra Pratap

2017-12-19

Hydrogen sulfide (H 2 S) is a hazardous gas, which not only harms living beings but also poses a significant risk to damage materials placed in culture and art museums, due to its corrosive nature. We demonstrate a novel approach for selective rapid detection of H 2 S gas using silver nanorods (AgNRs) arrays on glass substrates at ambient conditions. The arrays were prepared by glancing angle deposition method. The colorimetric and water wetting properties of as-fabricated arrays were found to be highly sensitive toward the sulfurization, in the presence of H 2 S gas with a minimal concentration in ppm range. The performance of AgNRs as H 2 S gas sensor is investigated by its sensing ability of 5 ppm of gas with an exposure time of only 30 s. We have developed an android-based mobile app to monitor real-time colorimetric detection of H 2 S. The wettability detection has been carried out by a mobile camera. A comparative analysis for different gases reveals the highest sensitivity and selectivity of the array AgNRs toward H 2 S. The rapid detection has also been demonstrated for H 2 S emission from aged wool fabric. Thus, high sensing ability of AgNRs toward H 2 S gas may have potential applications in health monitoring and art conservation.

Interspace modification of titania-nanorod arrays for efficient mesoscopic perovskite solar cells

NASA Astrophysics Data System (ADS)

Chen, Peng; Jin, Zhixin; Wang, Yinglin; Wang, Meiqi; Chen, Shixin; Zhang, Yang; Wang, Lingling; Zhang, Xintong; Liu, Yichun

2017-04-01

Morphology of electron transport layers (ETLs) has an important influence on the device architecture and electronic processes of mesostructured solar cells. In this work, we thoroughly investigated the effect of the interspace of TiO2 nanorod (NR) arrays on the photovoltaic performance of the perovskite solar cells (PSCs). Along with the interspace in TiO2-NR arrays increasing, the thickness as well as the crystal size of perovskite capping layer are reduced accordingly, and the filling of perovskite in the channel becomes incomplete. Electrochemical impedance spectroscopy measurements reveal that this variation of perovskite absorber layer, induced by interspace of TiO2 NR arrays, causes the change of charge recombination process at the TiO2/perovskite interface, suggesting that a balance between capping layer and the perovskite filling is critical to obtain high charge collection efficiency of PSCs. A power conversion efficiency of 10.3% could be achieved through careful optimization of interspace in TiO2-NR arrays. Our research will shed light on the morphology control of ETLs with 1D structure for heterojunction solar cells fabricated by solution-deposited method.

Enhanced solar photoelectrochemical conversion efficiency of the hydrothermally-deposited TiO2 nanorod arrays: Effects of the light trapping and optimum charge transfer

NASA Astrophysics Data System (ADS)

An, Gil Woo; Mahadik, Mahadeo A.; Chae, Weon-Sik; Kim, Hyun Gyu; Cho, Min; Jang, Jum Suk

2018-05-01

The vertically aligned TiO2 nanorod arrays (NRA) with manipulated aspect ratio were hydrothermally synthesized by changing the amount of the titanium (Ti) precursor in the initial growth solution. FE-SEM images show the optimum morphology, density and aspect ratio of the well-aligned TB-1.2 NRs on the surface of the FTO substrate. The UV-vis-absorption measurements revealed that a sample prepared at TB-1.2 can provide an increased light trapping effect. PEC analyses demonstrated that the TiO2 nanorods deposited at TB-1.2 of Titanium butoxide show a relatively high PEC conversion efficiency (3.5 times) compared with the TB-0.8 prepared TiO2 at a 1.0 V versus RHE. The higher PEC performance is believed to be the result of an enhancement of the optimum aspect ratio, light trapping, an efficient charge separation, and the high carrier transport in the vertically aligned TiO2 NRs. Further, the PEC based organic dye degradation experiments showed 77% and 94% removal of Orange II and methylene blue respectively. Additionally, 109 μmol h-1 cm-2 hydrogen generations were attributed using optimized vertically aligned TiO2 NRA's. Thus, the appropriate morphology manipulated the TiO2 NRAs are useful for solar conversion applications.

Fabrication and Characterization of Vertically Aligned ZnO Nanorod Arrays via Inverted Monolayer Colloidal Crystals Mask

NASA Astrophysics Data System (ADS)

Chen, Cheng; Ding, Taotao; Qi, Zhiqiang; Zhang, Wei; Zhang, Jun; Xu, Juan; Chen, Jingwen; Dai, Jiangnan; Chen, Changqing

2018-04-01

The periodically ordered ZnO nanorod (NR) arrays have been successfully synthesized via a hydrothermal approach on the silicon substrates by templating of the TiO2 ring deriving from the polystyrene (PS) nanosphere monolayer colloidal crystals (MCC). With the inverted MCC mask, sol-gel-derived ZnO seeds could serve as the periodic nucleation positions for the site-specific growth of ZnO NRs. The large-scale patterned arrays of single ZnO NR with good side-orientation can be readily produced. According to the experimental results, the as-integrated ZnO NR arrays showed an excellent crystal quality and optical property, very suitable for optoelectronic applications such as stimulated emitters and ZnO photonic crystal devices.

Ultra-thin layer chromatography and surface enhanced Raman spectroscopy on silver nanorod array substrates prepared by oblique angle deposition

NASA Astrophysics Data System (ADS)

Chen, Jing; Abell, Justin; Huang, Yao-wen; Zhao, Yiping

2012-06-01

We demonstrate the potential use of silver nanorod (AgNR) array substrates for on-chip separation and detection of chemical mixtures by ultra-thin layer chromatography (UTLC) and surface enhanced Raman spectroscopy (SERS). The capability of the AgNR substrates to separate different compounds in a mixture was explored using a mixture of the food colorant Brilliant Blue FCF and lactic acid, and the mixtures of Methylene Violet and BSA at various concentrations. After the UTLC process, spatially-resolved SERS spectra were collected along the mobile phase development direction and the intensities of specific SERS peaks from each component were used to generate chromatograms. The AgNR substrates demonstrate the capability of separating Brilliant Blue from lactic acid, as well as revealing the SERS signal of Methylene Violet from the massive BSA background after a simple UTLC step. This technique may have significant practical implications in actual detection of small molecules from complex food or clinical backgrounds.

Photocatalytic properties of h-WO3 nanoparticles obtained by annealing and h-WO3 nanorods prepared by hydrothermal method

NASA Astrophysics Data System (ADS)

Boyadjiev, Stefan I.; Nagy-Kovács, Teodóra; Lukács, István; Szilágyi, Imre M.

2016-03-01

In the present study, two different methods for preparing hexagonal WO3 (h-WO3) photocatalysts were used - controlled thermal decomposition and hydrothermal synthesis. WO3 nanoparticles with hexagonal structure were obtained by annealing (NH4)xWO3-y at 500 °C in air. WO3 nanorods were prepared by a hydrothermal method using sodium tungstate Na2WO4, HCl, (COOH)2 and NaSO4 precursors at 200 °C. The formation, morphology, structure and composition of the as-prepared nanoparticles and nanorods were studied by powder X-ray diffraction (XRD), transmission electron microscopy (TEM), and scanning electron microscopy combined with energy-dispersive X-ray spectroscopy (SEM-EDX). The photocatalytic activity of the h-WO3 nanoparticles and nanorods was studied by decomposing methyl orange in aqueous solution under UV light irradiation.

Facile fabrication and configuration design of Co3O4 porous acicular nanorod arrays on Ni foam for supercapacitors.

PubMed

Jiang, Tongtong; Yang, Siyu; Bai, Zhiman; Dai, Peng; Yu, Xinxin; Wu, Mingzai; Hu, Haibo

2018-08-03

The configuration of electrode materials is of great significance to the performance of supercapacitors (SCs) because of its direct effects on specific surface area and electron transfer path. Given this, herein, a series of Co 3 O 4 hierarchical configurations composed of porous acicular nanorods are designedly synthesized on Ni foam with in-site self-organization method depending on the addition of NH 4 F. In the absence of NH 4 F, Co 3 O 4 nanorods self-assemble into porous urchin-like structure (PULS), while the introduction of NH 4 F can induce the vertical growth of Co 3 O 4 acicular nanorods, forming porous acicular nanorod arrays (PANRAs). By simply tuning the concentration of NH 4 F, the Co 3 O 4 PANRAs with different specific surface area can be obtained. As expected, Co 3 O 4 PANRAs electrode for SCs (using 1 mmol of NH 4 F) exhibits high specific capacitance (1486 F g -1 at 1 A g -1 ) and excellent cycling stability (98.8% retention after 5000 continuous charge-discharge cycles), which are better than those of Co 3 O 4 PULS electrode (658.2 F g -1 at 1 A g -1 , 90.4%). Corresponding solid-state symmetric SC achieves a high energy density of 48.63 Wh kg -1 at power density of 600 W kg -1 . Such superior performance is attributed to fast charge transfer kinetics, facile electron transport and ions diffusion rate resulting from porous array structure, indicating the importance of configuration design of electrode materials for high performance SCs.

Solvothermal preparation of phthalocyanine nanorod/rGO composites and their application to visible-light-responsive photocatalysts

NASA Astrophysics Data System (ADS)

Zhang, Shuai; Lu, Yongting; Zhang, Fan; Qu, Jie; Lin, Bencai; Yuan, Ningyi; Fang, Bijun; Ding, Jian-Ning

2016-09-01

Phthalocyanine (Pc) nanorod/reduced graphene oxide (rGO) composites were prepared by a simple solvothermal method, in which Pc nanosheet and graphene oxide (GO) suspensions were mixed in methanol. As characterized by scanning electron microscopy, transmission electron microscopy, and selected area electron diffraction, Pc nanorods with an amorphous structure and an average diameter of 250nm are partially covered by rGO sheets. In the photodegradation experiments, all the composites with different rGO content show enhanced photocatalytic activity for Rhodamine B decomposition under visible-light compared to pure Pc nanorods or rGO sheets. The enhanced photocatalytic activity shall be ascribed to the large surface area offered by rGO and the charge-transfer from Pc to rGO as indicated by the photoluminescence measurement, in which fluorescence intensity of the composites is much weaker than that of Pc nanorods.

All-silicon nanorod-based Dammann gratings.

PubMed

Li, Zile; Zheng, Guoxing; He, Ping'An; Li, Song; Deng, Qiling; Zhao, Jiangnan; Ai, Yong

2015-09-15

Established diffractive optical elements (DOEs), such as Dammann gratings, whose phase profile is controlled by etching different depths into a transparent dielectric substrate, suffer from a contradiction between the complexity of fabrication procedures and the performance of such gratings. In this Letter, we combine the concept of geometric phase and phase modulation in depth, and prove by theoretical analysis and numerical simulation that nanorod arrays etched on a silicon substrate have a characteristic of strong polarization conversion between two circularly polarized states and can act as a highly efficient half-wave plate. More importantly, only by changing the orientation angles of each nanorod can the arrays control the phase of a circularly polarized light, cell by cell. With the above principle, we report the realization of nanorod-based Dammann gratings reaching diffraction efficiencies of 50%-52% in the C-band fiber telecommunications window (1530-1565 nm). In this design, uniform 4×4 spot arrays with an extending angle of 59°×59° can be obtained in the far field. Because of these advantages of the single-step fabrication procedure, accurate phase controlling, and strong polarization conversion, nanorod-based Dammann gratings could be utilized for various practical applications in a range of fields.

Ti nanorod arrays with a medium density significantly promote osteogenesis and osteointegration

PubMed Central

Ning, Chengyun; Wang, Shuangying; Zhu, Ye; Zhong, Meiling; Lin, Xi; Zhang, Yu; Tan, Guoxin; Li, Mei; Yin, Zhaoyi; Yu, Peng; Wang, Xiaolan; Li, Ying; He, Tianrui; Chen, Wei; Wang, Yingjun; Mao, Chuanbin

2016-01-01

Ti implants are good candidates in bone repair. However, how to promote bone formation on their surface and their consequent perfect integration with the surrounding tissue is still a challenge. To overcome such challenge, we propose to form Ti nanorods on their surface to promote the new bone formation around the implants. Here Ti nanorod arrays (TNrs) with different densities were produced on pure Ti surfaces using an anodizing method. The influence of TNr density on the protein adsorption as well as on the adhesion, proliferation, and osteogenic differentiation of MC3T3-E1 pre-osteoblastic cells were assessed. The TNrs were also implanted into the bone defects in rabbits to test their application in promoting bone formation and osteointegration at the implant-bone interface. TNrs with the medium density were found to show the best capability in promoting the protein adsorption from surrounding medium, which in turn efficiently enhanced osteogenic differentiation in vitro and osteointegration in vivo. Our work suggests that growing TNrs with a medium density on the surface of traditional Ti implants is an efficient and facile method for promoting bone formation and osteointegration in bone repair. PMID:26743328

Ti nanorod arrays with a medium density significantly promote osteogenesis and osteointegration

NASA Astrophysics Data System (ADS)

Ning, Chengyun; Wang, Shuangying; Zhu, Ye; Zhong, Meiling; Lin, Xi; Zhang, Yu; Tan, Guoxin; Li, Mei; Yin, Zhaoyi; Yu, Peng; Wang, Xiaolan; Li, Ying; He, Tianrui; Chen, Wei; Wang, Yingjun; Mao, Chuanbin

2016-01-01

Ti implants are good candidates in bone repair. However, how to promote bone formation on their surface and their consequent perfect integration with the surrounding tissue is still a challenge. To overcome such challenge, we propose to form Ti nanorods on their surface to promote the new bone formation around the implants. Here Ti nanorod arrays (TNrs) with different densities were produced on pure Ti surfaces using an anodizing method. The influence of TNr density on the protein adsorption as well as on the adhesion, proliferation, and osteogenic differentiation of MC3T3-E1 pre-osteoblastic cells were assessed. The TNrs were also implanted into the bone defects in rabbits to test their application in promoting bone formation and osteointegration at the implant-bone interface. TNrs with the medium density were found to show the best capability in promoting the protein adsorption from surrounding medium, which in turn efficiently enhanced osteogenic differentiation in vitro and osteointegration in vivo. Our work suggests that growing TNrs with a medium density on the surface of traditional Ti implants is an efficient and facile method for promoting bone formation and osteointegration in bone repair.

Localized surface plasmon resonance properties of Ag nanorod arrays on graphene-coated Au substrate

NASA Astrophysics Data System (ADS)

Mu, Haiwei; Lv, Jingwei; Liu, Chao; Sun, Tao; Chu, Paul K.; Zhang, Jingping

2017-11-01

Localized surface plasmon resonance (LSPR) on silver nanorod (SNR) arrays deposited on a graphene-coated Au substrate is investigated by the discrete dipole approximation (DDA) method. The resonance peaks in the extinction spectra of the SNR/graphene/Au structure show significantly different profiles as SNR height, and refractive index of the surrounding medium are varied gradually. Numerical simulation reveals that the shifts in the resonance peaks arise from hybridization of multiple plasmon modes as a result of coupling between the SNR arrays and graphene-coated Au substrate. Moreover, the LSPR modes blue-shifts from 800 nm to 700 nm when the thickness of the graphene layer in the metal nanoparticle (NP) - graphene hybrid nanostructure increases from 1 nm to 5 nm, which attribute to charge transfer between the graphene layer and SNR arrays. The results provide insights into metal NP-graphene hybrid nanostructures which have potential applications in plasmonics.

Color tunable light-emitting diodes based on p+-Si/p-CuAlO2/n-ZnO nanorod array heterojunctions

NASA Astrophysics Data System (ADS)

Ling, Bo; Zhao, Jun Liang; Sun, Xiao Wei; Tan, Swee Tiam; Kyaw, Aung Ko Ko; Divayana, Yoga; Dong, Zhi Li

2010-07-01

Wide-range color tuning from red to blue was achieved in phosphor-free p+-Si/p-CuAlO2/n-ZnO nanorod light-emitting diodes at room temperature. CuAlO2 films were deposited on p+-Si substrates by sputtering followed by annealing. ZnO nanorods were further grown on the annealed p+-Si/p-CuAlO2 substrates by vapor phase transport. The color of the p-CuAlO2/n-ZnO nanorod array heterojunction electroluminescence depended on the annealing temperature of the CuAlO2 film. With the increase of the annealing temperature from 900 to 1050 °C, the emission showed a blueshift under the same forward bias. The origin of the blueshift is related to the amount of Cu concentration diffused into ZnO.

Optical and photoelectrochemical performance study based on n-ZnO nanorod arrays/p-CuAlO2 laminar films/Ni heterojunction

NASA Astrophysics Data System (ADS)

Ding, Juan; Yang, Haibin; Deng, Weiwen

2014-06-01

A novel ZnO nanorod arrays (NRs)/CuAlO2 laminar films heterojunction nanostructure was grown on the substrate of Ni plates using sol-gel synthesis for laminar films and subsequent hydrothermal reaction for nanorod arrays. The surface morphology, structure, optical and photoelectrochemical behaviors of this heterojunction were considered. Two significant absorption peaks of UV-vis spectra and a favorable forward current to reverse current ratio at applied voltage of -0.7 V to +2 V were observed in this heterojunction. Furthermore, the photoelectrochemical property was indicated that the highest photocurrent of 0.67 mA/cm2 was obtained under AM 1.5 illumination (vs Ag/AgCl). This heterojunction will play an important role in the optoelectronic fields and can be extended to other binary or ternary oxide compositions for optoelectronic applications.

Heterostructured TiO2/NiTiO3 Nanorod Arrays for Inorganic Sensitized Solar Cells with Significantly Enhanced Photovoltaic Performance and Stability.

PubMed

Li, Yue-Ying; Wang, Jian-Gan; Sun, Huan-Huan; Wei, Bingqing

2018-04-11

Organic dyes used in the conventional dye-sensitized solar cells (DSSCs) suffer from poor light stability and high cost. In this work, we demonstrate a new inorganic sensitized solar cell based on ordered one-dimensional semiconductor nanorod arrays of TiO 2 /NiTiO 3 (NTO) heterostructures prepared via a facile two-step hydrothermal approach. The semiconductor heterostructure arrays are highly desirable and promising for DSSCs because of their direct charge transport capability and slow charge recombination rate. The low-cost NTO inorganic semiconductor possesses an appropriate band gap that matches well with TiO 2 , which behaves like a "dye" to enable efficient light harvesting and fast electron-hole separation. The solar cells constructed by the ordered TiO 2 /NTO heterostructure photoanodes show a significantly improved power conversion efficiency, high fill factor, and more promising, outstanding life stability. The present work will open up an avenue to design heterostructured inorganics for high-performance solar cells.

Scalable continuous flow synthesis of ZnO nanorod arrays in 3-D ceramic honeycomb substrates for low-temperature desulfurization

DOE PAGES

Wang, Sibo; Wu, Yunchao; Miao, Ran; ...

2017-07-26

Scalable and cost-effective synthesis and assembly of technologically important nanostructures in three-dimensional (3D) substrates hold keys to bridge the demonstrated nanotechnologies in academia with industrially relevant scalable manufacturing. In this paper, using ZnO nanorod arrays as an example, a hydrothermal-based continuous flow synthesis (CFS) method is successfully used to integrate the nano-arrays in multi-channeled monolithic cordierite. Compared to the batch process, CFS enhances the average growth rate of nano-arrays by 125%, with the average length increasing from 2 μm to 4.5 μm within the same growth time of 4 hours. The precursor utilization efficiency of CFS is enhanced by 9more » times compared to that of batch process by preserving the majority of precursors in recyclable solution. Computational fluid dynamic simulation suggests a steady-state solution flow and mass transport inside the channels of honeycomb substrates, giving rise to steady and consecutive growth of ZnO nano-arrays with an average length of 10 μm in 12 h. The monolithic ZnO nano-array-integrated cordierite obtained through CFS shows enhanced low-temperature (200 °C) desulfurization capacity and recyclability in comparison to ZnO powder wash-coated cordierite. This can be attributed to exposed ZnO {101¯0} planes, better dispersion and stronger interactions between sorbent and reactant in the ZnO nanorod arrays, as well as the sintering-resistance of nano-array configurations during sulfidation–regeneration cycles. Finally, with the demonstrated scalable synthesis and desulfurization performance of ZnO nano-arrays, a promising, industrially relevant integration strategy is provided to fabricate metal oxide nano-array-based monolithic devices for various environmental and energy applications.« less

Scalable continuous flow synthesis of ZnO nanorod arrays in 3-D ceramic honeycomb substrates for low-temperature desulfurization

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wang, Sibo; Wu, Yunchao; Miao, Ran

Scalable and cost-effective synthesis and assembly of technologically important nanostructures in three-dimensional (3D) substrates hold keys to bridge the demonstrated nanotechnologies in academia with industrially relevant scalable manufacturing. In this paper, using ZnO nanorod arrays as an example, a hydrothermal-based continuous flow synthesis (CFS) method is successfully used to integrate the nano-arrays in multi-channeled monolithic cordierite. Compared to the batch process, CFS enhances the average growth rate of nano-arrays by 125%, with the average length increasing from 2 μm to 4.5 μm within the same growth time of 4 hours. The precursor utilization efficiency of CFS is enhanced by 9more » times compared to that of batch process by preserving the majority of precursors in recyclable solution. Computational fluid dynamic simulation suggests a steady-state solution flow and mass transport inside the channels of honeycomb substrates, giving rise to steady and consecutive growth of ZnO nano-arrays with an average length of 10 μm in 12 h. The monolithic ZnO nano-array-integrated cordierite obtained through CFS shows enhanced low-temperature (200 °C) desulfurization capacity and recyclability in comparison to ZnO powder wash-coated cordierite. This can be attributed to exposed ZnO {101¯0} planes, better dispersion and stronger interactions between sorbent and reactant in the ZnO nanorod arrays, as well as the sintering-resistance of nano-array configurations during sulfidation–regeneration cycles. Finally, with the demonstrated scalable synthesis and desulfurization performance of ZnO nano-arrays, a promising, industrially relevant integration strategy is provided to fabricate metal oxide nano-array-based monolithic devices for various environmental and energy applications.« less

Morphology-controllable of Sn doped ZnO nanorods prepared by spray pyrolysis for transparent electrode application

NASA Astrophysics Data System (ADS)

Hameed, M. Shahul; Princice, J. Joseph; Babu, N. Ramesh; Zahirullah, S. Syed; Deshmukh, Sampat G.; Arunachalam, A.

2018-05-01

Transparent conductive Sn doped ZnO nanorods have been deposited at various doping level by spray pyrolysis technique on glass substrate. The structural, surface morphological and optical properties of these films have been investigated with the help of X-ray diffraction (XRD), scanning electron microscope (SEM), atomic force microscope (AFM) and UV-Vis spectrophotometer respectively. XRD patterns revealed a successful high quality growth of single crystal ZnO nanorods with hexagonal wurtzite structure having (002) preferred orientation. The scanning electron microscope (SEM) image of the prepared films exposed the uniform distribution of Sn doped ZnO nanorod shaped grains. All these films were highly transparent in the visible region with average transmittance of 90%.

A comprehensive biosensor integrated with a ZnO nanorod FET array for selective detection of glucose, cholesterol and urea.

PubMed

Ahmad, Rafiq; Tripathy, Nirmalya; Park, Jin-Ho; Hahn, Yoon-Bong

2015-08-04

We report a novel straightforward approach for simultaneous and highly-selective detection of multi-analytes (i.e. glucose, cholesterol and urea) using an integrated field-effect transistor (i-FET) array biosensor without any interference in each sensor response. Compared to analytically-measured data, performance of the ZnO nanorod based i-FET array biosensor is found to be highly reliable for rapid detection of multi-analytes in mice blood, and serum and blood samples of diabetic dogs.

Controlled growth of c-axis oriented ZnO nanorod array films by electrodeposition method and characterization.

PubMed

Arslan, Andaç; Hür, Evrim; Ilican, Saliha; Caglar, Yasemin; Caglar, Mujdat

2014-07-15

ZnO nanorod array films were deposited from aqueous solution containing different concentrations (1×10(-2) M and 5×10(-3) M) Zn(NO3)2⋅6H2O and C6H12N4 and at different electrodeposition times (i.e., 15 min, 30 min, 60 min, 120 min and 180 min) using chronoamperometry method on p-Si substrate. Surface morphology and crystal structural properties of ZnO films were investigated by XRD and FESEM to select ZnO films which have optimum properties. The highest TC(hkl) value was observed in (002) plane for the film, which is deposited at 1×10(-2) M and 120 min. It is also observed that the highly oriented nanorods in this film are denser. Additionally, the conductivity type was determined by using Mott-Schottky which is electrochemical impedance spectroscopy method (EIS). On the other hand, to investigate the utility of obtained ZnO on p-Si (p-Si/n-ZnO) as supercapacitor electrode active material, the electrochemical storage properties of p-Si/ZnO was studied by electrochemical impedance spectroscopy and repeating chronopotentiometry methods. It is suggested from electrochemical tests results that p-Si/ZnO is a promising electrode materials for supercapacitor applications that required low voltage (<10 V). Rectifiying behavior was observed from the I-V characteristic of nanorod array n-ZnO/p-Si heterojunction diode. The n value, Io and the ϕb were found to be 5.48, 1.93×10(-8) A and 0.75 eV, respectively. Copyright © 2014 Elsevier B.V. All rights reserved.

Transient Negative Optical Nonlinearity of Indium Oxide Nanorod Arrays in the Full-Visible Range

DOE PAGES

Guo, Peijun; Chang, Robert P. H.; Schaller, Richard D.

2017-06-09

Dynamic control of the optical response of materials at visible wavelengths is key to future metamaterials and photonic integrated circuits. Here we demonstrate large amplitude, negative optical nonlinearity (Δ n from -0.05 to -0.09) of indium oxide nanorod arrays in the full-visible range. We experimentally quantify and theoretically calculate the optical nonlinearity, which arises from the modifications of interband optical transitions. Furthermore, the approach towards negative optical nonlinearity can be generalized to other transparent semiconductors and opens door to reconfigurable, sub-wavelength optical components.

Multifunctional transparent ZnO nanorod films.

PubMed

Kwak, Geunjae; Jung, Sungmook; Yong, Kijung

2011-03-18

Transparent ZnO nanorod (NR) films that exhibit extreme wetting states (either superhydrophilicity or superhydrophobicity through surface chemical modification), high transmittance, UV protection and antireflection have been prepared via the facile ammonia hydrothermal method. The periodic 1D ZnO NR arrays showed extreme wetting states as well as antireflection properties due to their unique surface structure and prevented the UVA region from penetrating the substrate due to the unique material property of ZnO. Because of the simple, time-efficient and low temperature preparation process, ZnO NR films with useful functionalities are promising for fabrication of highly light transmissive, antireflective, UV protective, antifogging and self-cleaning optical materials to be used for optical devices and photovoltaic energy devices.

One-step solvothermal deposition of ZnO nanorod arrays on a wood surface for robust superamphiphobic performance and superior ultraviolet resistance

PubMed Central

Yao, Qiufang; Wang, Chao; Fan, Bitao; Wang, Hanwei; Sun, Qingfeng; Jin, Chunde; Zhang, Hong

2016-01-01

In the present paper, uniformly large-scale wurtzite-structured ZnO nanorod arrays (ZNAs) were deposited onto a wood surface through a one-step solvothermal method. The as-prepared samples were characterized by X-ray diffraction (XRD), field-emission scanning electron microscopy (FE-SEM), transmission electron microscopy (TEM), Fourier transform infrared spectroscopy (FTIR), thermogravimetry (TG), and differential thermal analysis (DTA). ZNAs with a diameter of approximately 85 nm and a length of approximately 1.5 μm were chemically bonded onto the wood surface through hydrogen bonds. The superamphiphobic performance and ultraviolet resistance were measured and evaluated by water or oil contact angles (WCA or OCA) and roll-off angles, sand abrasion tests and an artificially accelerated ageing test. The results show that the ZNA-treated wood demonstrates a robust superamphiphobic performance under mechanical impact, corrosive liquids, intermittent and transpositional temperatures, and water spray. Additionally, the as-prepared wood sample shows superior ultraviolet resistance. PMID:27775091

One-step solvothermal deposition of ZnO nanorod arrays on a wood surface for robust superamphiphobic performance and superior ultraviolet resistance

NASA Astrophysics Data System (ADS)

Yao, Qiufang; Wang, Chao; Fan, Bitao; Wang, Hanwei; Sun, Qingfeng; Jin, Chunde; Zhang, Hong

2016-10-01

In the present paper, uniformly large-scale wurtzite-structured ZnO nanorod arrays (ZNAs) were deposited onto a wood surface through a one-step solvothermal method. The as-prepared samples were characterized by X-ray diffraction (XRD), field-emission scanning electron microscopy (FE-SEM), transmission electron microscopy (TEM), Fourier transform infrared spectroscopy (FTIR), thermogravimetry (TG), and differential thermal analysis (DTA). ZNAs with a diameter of approximately 85 nm and a length of approximately 1.5 μm were chemically bonded onto the wood surface through hydrogen bonds. The superamphiphobic performance and ultraviolet resistance were measured and evaluated by water or oil contact angles (WCA or OCA) and roll-off angles, sand abrasion tests and an artificially accelerated ageing test. The results show that the ZNA-treated wood demonstrates a robust superamphiphobic performance under mechanical impact, corrosive liquids, intermittent and transpositional temperatures, and water spray. Additionally, the as-prepared wood sample shows superior ultraviolet resistance.

Facile preparation of MnO2 nanorods and evaluation of their supercapacitive characteristics

NASA Astrophysics Data System (ADS)

Aghazadeh, Mustafa; Asadi, Maryam; Maragheh, Mohammad Ghannadi; Ganjali, Mohammad Reza; Norouzi, Parviz; Faridbod, Farnoush

2016-02-01

The first time pulsed base (OH-) electrogeneration to the cathodic electrodeposition of MnO2 in nitrate bath was applied and MnO2 nanorods were obtained. The deposition experiments were performed under a pulse current mode with typical on-times and off-times (ton = 10 ms and toff = 50 ms) and a peak current density of 2 mA cm-2 (Ia = 2 mA cm-2). The structural characterization with XRD and FTIR revealed that the prepared MnO2 is composed of both α and γ phases. Morphological evaluations through SEM and TEM revealed that the prepared MnO2 contains nanorods of relative uniform structures (with an average diameter of 50 nm). The electrochemical measurements through cyclic voltammetry and charge-discharge techniques revealed that the prepared MnO2 nanostructures reveal an excellent capacitive behavior with specific capacitance values of 242, 167 and 98 F g-1 under the applied current densities of 2, 5 and 10 A g-1, respectively. Also, excellent long-term cycling stabilities of 94.8%, 89.1%, and 76.5% were observed after 1000 charge-discharge cycles at the current densities of 2, 5 and 10 A g-1.

Facile synthesis and photocatalytic activity of ZnO/zinc titanate core-shell nanorod arrays

NASA Astrophysics Data System (ADS)

He, Ding-Chao; Fu, Qiu-Ming; Ma, Zhi-Bin; Zhao, Hong-Yang; Tu, Ya-Fang; Tian, Yu; Zhou, Di; Zheng, Guang; Lu, Hong-Bing

2018-02-01

ZnO/zinc titanate core-shell nanorod arrays (CSNRs) were successfully prepared via a simple synthesis process by combining hydrothermal synthesis and liquid phase deposition (LPD). The surface morphologies, crystalline characteristics, optical properties and surface electronic states of the ZnO/zinc titanate CSNRs were characterized by scanning electron microscope, transmission electron microscope, x-ray diffractometer, x-ray photoelectron spectroscopy, PL and ultraviolet (UV)-visible absorption spectra. By controlling the reaction time of LPD, the shell thickness could vary with the reaction time. Furthermore, the impacts of the reaction time and post-annealing temperature on the crystalline structure and chemical composition of the CSNRs were also investigated. The studies of photocatalytic activity under UV light irradiation revealed that the ZnO/zinc titanate CSNRs annealed at 700 °C with 30 min deposition exhibited the best photocatalytic activity and good stability for degradation of methylene blue. It had been found that the effective separation of photogenerated electron-hole pairs in the CSNRs led to the enhanced photocatalytic activity. Moreover, the ZnO/zinc titanate CSNRs grown on quartz glass substrate could be easily recycled for reuse with almost unchanged photocatalytic activity.

TiO2 Nanorods Preparation from Titanyl Sulphate Produced by Dissolution of Ilmenite

NASA Astrophysics Data System (ADS)

Wahyuningsih, S.; Rinawati, L.; Munifa, R. M. I.; Ramelan, A. H.; Sulistyono, Eko

2017-02-01

One-dimensional titanium oxides (TiO2) nanorods have substantial applications in photocatalytic, nanoelectronic, and photoelectrochemical solar cells. These applications require large quantities of materials and a production technique suitable for future industry fabrication. We demonstrate here a new method of TiO2 nanorods production from ilmenite sands (FeTiO3). In this process, the roasted ilmenite sand was separated from the iron content and dissolved in the sulphuric acid solution. Separation process of TiO2 from ilmenite has been carried out by roasting, leaching and precipitation processes. The roasting process was conducted by the addition of Na2S at a temperature of 800°C that had been deomposed ilmenite into hematite (Fe2O3), anatase TiO2, rutile TiO2, Na2SO4, NaFeS2 and NaFeO2. Separation TiO2 from titanyl sulfate (TiOSO4) after leaching in H2SO4 solution was conducted by hydrolysis-condensation step and complexation step of Fe2+ content. KCNS solution was used as a complexing agent. The xerogel synthesized TiO2 then was prepared to 1-D nanostructure of TiO2 nanorods by hydrothermal process under alkaline condition. By the two-step method, we finally gain the 1D nanorods TiO2 extracted from ilmenite sand. The characterization using the Scanning Electron Microscopy (SEM) and Transmission Electron Microscopy (TEM) obtained the nanorod morphology at a diameter about 9.6 nm.

Fabrication of Vertically Aligned Carbon Nanotube or Zinc Oxide Nanorod Arrays for Optical Diffraction Gratings.

PubMed

Kim, Jeong; Kim, Sun Il; Cho, Seong-Ho; Hwang, Sungwoo; Lee, Young Hee; Hur, Jaehyun

2015-11-01

We report on new fabrication methods for a transparent, hierarchical, and patterned electrode comprised of either carbon nanotubes or zinc oxide nanorods. Vertically aligned carbon nanotubes or zinc oxide nanorod arrays were fabricated by either chemical vapor deposition or hydrothermal growth, in combination with photolithography. A transparent conductive graphene layer or zinc oxide seed layer was employed as the transparent electrode. On the patterned surface defined using photoresist, the vertically grown carbon nanotubes or zinc oxides could produce a concentrated electric field under applied DC voltage. This periodic electric field was used to align liquid crystal molecules in localized areas within the optical cell, effectively modulating the refractive index. Depending on the material and morphology of these patterned electrodes, the diffraction efficiency presented different behavior. From this study, we established the relationship between the hierarchical structure of the different electrodes and their efficiency for modulating the refractive index. We believe that this study will pave a new path for future optoelectronic applications.

Flexible piezoelectric nanogenerators based on a transferred ZnO nanorod/Si micro-pillar array

NASA Astrophysics Data System (ADS)

Baek, Seong-Ho; Park, Il-Kyu

2017-03-01

Flexible piezoelectric nanogenerators (PNGs) based on a composite of ZnO nanorods (NRs) and an array of Si micro-pillars (MPs) are demonstrated by a transfer process. The flexible composite structure was fabricated by hydrothermal growth of ZnO NRs on an electrochemically etched Si MP array with various lengths followed by mechanically delaminating the Si MP arrays from the Si substrate after embedding them in a polydimethylsiloxane matrix. Because the Si MP arrays act as a supporter to connect the ZnO NRs electrically and mechanically, verified by capacitance measurement, the output voltage from the flexible PNGs increased systematically with the increased density ZnO NRs depending on the length of the Si MPs. The flexible PNGs showed 3.2 times higher output voltage with a small change in current with increasing Si MP length from 5 to 20 μm. The enhancement of the output voltage is due to the increased number of series-connected ZnO NRs and the beneficial effect of a ZnO NR/Si MP heterojunction on reducing free charge screening effects. The flexible PNGs can be attached on fingers as a wearable electrical power source or motion sensor.

Ultrasensitive sliver nanorods array SERS sensor for mercury ions.

PubMed

Song, Chunyuan; Yang, Boyue; Zhu, Yu; Yang, Yanjun; Wang, Lianhui

2017-01-15

With years of outrageous mercury emissions, there is an urgent need to develop convenient and sensitive methods for detecting mercury ions in response to increasingly serious mercury pollution in water. In the present work, a portable, ultrasensitive SERS sensor is proposed and utilized for detecting trace mercury ions in water. The SERS sensor is prepared on an excellent sliver nanorods array SERS substrate by immobilizing T-component oligonucleotide probes labeled with dye on the 3'-end and -SH on the 5'-end. The SERS sensor responses to the specific chemical bonding between thymine and mercury ions, which causes the previous flexible single strand of oligonucleotide probe changing into rigid and upright double chain structure. Such change in the structure drives the dyes far away from the excellent SERS substrate and results in a SERS signal attenuation of the dye. Therefore, by monitoring the decay of SERS signal of the dye, mercury ions in water can be detected qualitatively and quantitatively. The experimental results indicate that the proposed optimal SERS sensor owns a linear response with wide detecting range from 1pM to 1μM, and a detection limit of 0.16pM is obtained. In addition, the SERS sensor demonstrates good specificity for Hg 2+ , which can accurately identify trace mercury ions from a mixture of ten kinds of other ions. The SERS sensor has been further executed to analyze the trace mercury ions in tap water and lake water respectively, and good recovery rates are obtained for sensing both kinds of water. With its high selectivity and good portability, the ultrasensitive SERS sensor is expected to be a promising candidate for discriminating mercury ions in the fields of environmental monitoring and food safety. Copyright © 2016 Elsevier B.V. All rights reserved.

Low temperature growth of ZnO nanorods array via solution-immersion on TiO2 seed layer

NASA Astrophysics Data System (ADS)

Asib, N. A. M.; Aadila, A.; Afaah, A. N.; Rusop, M.; Khusaimi, Z.

2018-05-01

In this work, TiO2:ZNR thin films were successfully fabricated on glass substrates at low temperatures of 75 to 90°C. The substrates were coated with titanium dioxide (TiO2) using sol-gel spin coating, which act as seed layer to grow zinc oxide nanorods (ZNR) by solution-immersion method. At 90 and 95° C, ZNR with hexagonal tip are well dispersed without any aggregation and exhibit more uniform nanorods array as observed using FESEM. The diffraction peak intensity of the (0 0 2)-plane increased as the temperature increased, indicating improved orientation in the c-axis direction of the ZNR as detected in XRD patterns. From UV-Vis absorbance spectra, it was found that the samples has higher absorption properties at middle range of immersion temperatures; 80, 85 and 90°C.

Preparation of ZnO nanorods on conductive PET-ITO-Ag fibers

NASA Astrophysics Data System (ADS)

Li, Yiwen; Ji, Shuai; Chen, Yuanyu; Zhang, Hong; Gong, Yumei; Guo, Jing

2016-12-01

We studied the vertical ZnO nanorods grown on conductive conventional polyethylene terephthalate (PET) fibers which are prepared by electroless silver depositing on tin-doped indium oxide (ITO) coated PET fibers through an efficient and low-cost green approach. The PET fibers were firstly functionalized with a layer of ITO gel synthesized through a sol-gel process at rather low temperature, simply by immersing the fibers into ITO sol for several minutes followed by gelation at 120 °C. Once the ITO gel layer surface was activated by SnCl2, a continuous, uniform, and compact layer of silver was carried out on the surface of the PET-ITO fibers through electroless plating operation at room temperature. The as-prepared PET-ITO-Ag fibers had good electrical conductivity, with surface resistivity as low as 0.23 mΩ cm. The overall procedure is simple, efficient, nontoxic, and controllable. The conductive PET-ITO-Ag fiber was used successfully as a flexible basal material to plant vertical ZnO nanorods through controlling the seeding and growth processes. The morphology of the PET-ITO, PET-ITO-Ag, and PET-ITO-Ag-ZnO fibers were observed by scanning electron microscopy (SEM) and transmission electron microscopy (TEM). Undergone the whole process, although the tensile strength of the fiber decreased slightly, they may still exert their applications in flexible electronic such as photovoltaic and piezoelectric devices.

Flower-like ZnO nanorod arrays grown on HF-etched Si (111): constraining relation between ZnO seed layer and Si (111)

NASA Astrophysics Data System (ADS)

Brahma, Sanjaya; Liu, C.-W.; Huang, R.-J.; Chang, S.-J.; Lo, K.-Y.

2015-11-01

We demonstrate the formation of self-assembled homogenous flower-like ZnO nanorods over a ZnO seed layer deposited on a HF-etched Si (111) substrate. The typical flower-like morphology of ZnO nanorod arrays is ascribed to the formation of the island-like seed layer which is deposited by the drop method followed by annealing at 300 °C. The island-like ZnO seed layer consists of larger ZnO grains, and is built by constraining of the Si (111) surface due to pattern matching. Pattern matching of Si with ZnO determines the shape and size of the seed layer and this controls the final morphology of ZnO nanorods to be either flower like or vertically aligned. The high quality of the island-like ZnO seed layer enhances the diameter and length of ZnO nanorods. Besides, while the amorphous layer formed during the annealing process would influence the strained ZnO grain, that subsequent amorphous layer will not block the constraining between the ZnO grain and the substrate.

Evolution of the composition, structure, and piezoelectric performance of (K1-xNax)NbO3 nanorod arrays with hydrothermal reaction time

NASA Astrophysics Data System (ADS)

Jin, Wenchao; Wang, Zhao; Li, Meng; He, Yahua; Hu, Xiaokang; Li, Luying; Gao, Yihua; Hu, Yongming; Gu, Haoshuang; Wang, Xiaolin

2018-04-01

Lead-free (K,Na)NbO3 (KNN) nanorod arrays were synthesized with the assistance of a Nb: SrTiO3 single-crystal substrate through the hydrothermal process. The evolutions of the morphology, composition, and structure of the as-synthesized KNN nanorods with the increase in reaction time were investigated. The results confirmed that the increase in reaction time up to 3 h led to the increase in the length and aspect ratio of the well-aligned KNN nanorods. All samples have K-rich orthorhombic crystal structures, while the diffraction peaks shifted towards a higher degree. The peak shifts should be attributed to the increase in the Na content in the KNN lattice, which could decrease the lattice parameters owing to the small ionic radius of Na+ than that of K+. Moreover, the increase in reaction time also resulted in the suppression of oxygen vacancies on the surface of the KNN nanorods. These evolutions of the composition and crystal structure, as well as the decrease in the defect content, lead to great enhancement of the nanorod's piezoelectric response, as their d33 value was increased from 19 to 64 pm/V. These results demonstrated the significant impact of reaction time on the hydrothermal growth of high-performance lead-free KNN one-dimensional nanomaterials.

High optical switching speed and flexible electrochromic display based on WO3 nanoparticles with ZnO nanorod arrays' supported electrode

NASA Astrophysics Data System (ADS)

Wang, Mingjun; Fang, Guojia; Yuan, Longyan; Huang, Huihui; Sun, Zhenhua; Liu, Nishuang; Xia, Shanhong; Zhao, Xingzhong

2009-05-01

The electrochromic (EC) property of WO3 nanoparticles grown on vertically self-aligned ZnO nanorods (ZNRs) is reported. An electrochromic character display based on WO3 nanoparticle-modified ZnO nanorod arrays on a flexible substrate has been fabricated and demonstrated. The ZNRs were first synthesized on ZnO-seed-coated In2O3:Sn (ITO) glass (1 cm2 cell) and polyethylene terephthalate (PET) (4 cm2 cell) substrates by a low temperature hydrothermal method, and then amorphous WO3 nanoparticles were grown directly on the surface of the ZNRs by the pulsed laser deposition (PLD) method. The ZNR-based EC device shows high transparence, good electrochromic stability and fast switching speed (4.2 and 4 s for coloration and bleaching, respectively, for a 1 cm2 cell). The good performance of the ZNR electrode-based EC display can be attributed to the large surface area, high crystallinity and good electron transport properties of the ZNR arrays. Its high contrast, fast switching, good memory and flexible characteristics indicate it is a promising candidate for flexible electrochromic displays or electronic paper.

Influence of substrates and rutile seed layers on the assembly of hydrothermally grown rutile TiO2 nanorod arrays

NASA Astrophysics Data System (ADS)

Kalb, Julian; Dorman, James A.; Folger, Alena; Gerigk, Melanie; Knittel, Vanessa; Plüisch, Claudia S.; Trepka, Bastian; Lehr, Daniela; Chua, Emily; Goodge, Berit H.; Wittemann, Alexander; Scheu, Christina; Polarz, Sebastian; Schmidt-Mende, Lukas

2018-07-01

Rutile TiO2 nanorod arrays (NRAs) are applicable in various prospective technologies. Hydrothermal methods present a simple technique to fabricate such NRAs. In this report, we present the fabrication of seed layers for the hydrothermal growth of rutile TiO2 nanorods via sputter deposition, electron-beam evaporation, and sol-gel method and study the influence of each on the growth behavior. To satisfy the requirements of numerous applications, p-type silicon, platinum, levitating carbon membranes, a template made of polystyrene spheres, and commercial fluorine tin oxide (FTO) were employed as substrates. We document the structural properties of the TiO2 seed layers and describe the relationship between the characteristics of the seed crystals, the growth evolution, and the appearance of as-grown nanorods. Various growth stages of rutile TiO2 nanorods are compared depending on whether they are grown on polycrystalline TiO2 or FTO seed layers. In both cases, a homogenous TiO2 bottom layer is formed at the seed layer/substrate interface, which is essential for electronic applications such as hybrid solar cells. Detached NRAs illustrate the effect of rutile FTO and TiO2 on the porosity of this bottom layer. Further details about the formation process of this layer are obtained from the growth on confined seed layers fabricated by electron-beam lithography.

Hierarchical core-shell structure of ZnO nanorod@NiO/MoO₂ composite nanosheet arrays for high-performance supercapacitors.

PubMed

Hou, Sucheng; Zhang, Guanhua; Zeng, Wei; Zhu, Jian; Gong, Feilong; Li, Feng; Duan, Huigao

2014-08-27

A hierarchical core-shell structure of ZnO nanorod@NiO/MoO2 composite nanosheet arrays on nickel foam substrate for high-performance supercapacitors was constructed by a two-step solution-based method involving two hydrothermal processes followed by a calcination treatment. Compared to one composed of pure NiO/MoO2 composite nanosheets, the hierarchical core-shell structure electrode displays better pseudocapacitive behaviors in 2 M KOH, including high areal specific capacitance values of 1.18 F cm(-2) at 5 mA cm(-2) and 0.6 F cm(-2) at 30 mA cm(-2) as well as relatively good rate capability at high current densities. Furthermore, it also shows remarkable cycle stability, remaining at 91.7% of the initial value even after 4000 cycles at a current density of 10 mA cm(-2). The enhanced pseudocapacitive behaviors are mainly due to the unique hierarchical core-shell structure and the synergistic effect of combining ZnO nanorod arrays and NiO/MoO2 composite nanosheets. This novel hierarchical core-shell structure shows promise for use in next-generation supercapacitors.

High-performance electrochemical glucose sensing enabled by Cu(TCNQ) nanorod array

NASA Astrophysics Data System (ADS)

Wu, Xiufeng; Lu, Wenbo

2018-04-01

It is highly attractive to construct stable enzyme-free glucose sensors based on three-dimensional direct electrochemical detection of glucose. In this paper, a copper 7,7,8,8-tetracyanoquinodimethane (Cu(TCNQ)) nanorod array on Cu foam (Cu(TCNQ) NA/CF) is proposed as an efficient catalyst for electrochemical glucose oxidation in alkaline conditions. When Cu(TCNQ) NA/CF was used as the enzyme-free sensory of glucose, the sensor showed a response time within 3 s, a wide linear detection in the range 0.001-10.0 mM, the minimum limit of detection was as low as 10 nM (S/N = 3), and it had a high sensitivity of 26 987 μA mM-1 cm-2. Moreover, this sensor also possesses long-term stability, high selectivity, reproducibility, and actual applications for fresh human serum sample analysis is also successfully accepted.

Effect of bath temperature on surface morphology and photocatalytic activity of ZnO nanorods

DOE Office of Scientific and Technical Information (OSTI.GOV)

Sriharan, N.; Senthil, T. S., E-mail: tssenthi@gmail.com; Muthukumarasamy, N.

2016-05-06

ZnO nanorods were prepared by using simple hydrothermal method using four different bath temperatures. All the prepared ZnO nanorods are annealed at 450°C and are characterized by using various techniques such as X-ray diffraction, UV spectra and scanning electron microscopy. Photocatalytic activity of the prepared ZnO nanorods is analyzed. A novel photocatalytic reactor designed with ZnO nanorods prepared at 90°C shows enhanced catalytic efficiency. The role of light irradiation time, bath temperature and surface morphology of the ZnO nanorods on the performance of photocatalytic reaction is analyzed.

Significantly Enhanced Energy Density in Nanocomposite Capacitors Combining the TiO2 Nanorod Array with Poly(vinylidene fluoride).

PubMed

Yao, Lingmin; Pan, Zhongbin; Liu, Shaohui; Zhai, Jiwei; Chen, Haydn H D

2016-10-05

A novel inorganic/polymer nanocomposite, using 1-dimensional TiO 2 nanorod array as fillers (TNA) and poly(vinylidene fluoride) (PVDF) as matrix, has been successfully synthesized for the first time. A carefully designed process sequence includes several steps with the initial epitaxial growth of highly oriented TNA on the fluorine-doped tin oxide (FTO) conductive glass. Subsequently, PVDF is embedded into the nanorods by the spin-coating method followed by annealing and quenching processes. This novel structure with dispersive fillers demonstrates a successful compromise between the electric displacement and breakdown strength, resulting in a dramatic increase in the electric polarization which leads to a significant improvement on the energy density and discharge efficiency. The nanocomposites with various height ratios of fillers between the TNA and total film thickness were investigated by us. The results show that nanocomposite with 18% height ratio fillers obtains maximum increase in the energy density (10.62 J cm -3 ) at a lower applied electric field of 340 MV m -1 , and it also illustrates a higher efficiency (>85%) under the electric field less than 100 MV m -1 . Even when the electric field reached 340 MV m -1 , the efficiency of nanocomposites can still maintained at ∼70%. This energy density exceeds most of the previously reported TiO 2 -based nanocomposite values at such a breakdown strength, which provides another promising design for the next generation of dielectric nanocomposite material, by using the highly oriented nanorod array as fillers for the higher energy density capacitors. Additionally, the finite element simulation has been employed to analyze the distribution of electric fields and electric flux density to explore the inherent mechanism of the higher performance of the TNA/PVDF nanocomposites.

Growth of Well-Aligned ZnO Nanorod Arrays and Their Application for Photovoltaic Devices

NASA Astrophysics Data System (ADS)

Yuan, Zhaolin; Yao, Juncai

2017-11-01

We have fabricated well-aligned ZnO nanorod arrays (ZNRAs) on indium tin oxide-coated glass substrates by a facile chemical bath deposition method. We used field-emission scanning electron microscope, x-ray diffraction and UV-Vis absorption spectroscopy to study the morphology, crystalline structure and optical absorption of the fabricated ZNRAs, respectively. The results showed that ZnO nanorods stood almost perpendicularly on the substrate, were about 30-50 nm in diameter and 800-900 nm in length, and were wurtzite-structured (hexagonal) ZnO. In addition, well-aligned ZNRAs exhibited a weak absorption in the visible region and had an optical band gap value of 3.28 eV. Furthermore, a hybrid ZNRAs/polymer photovoltaic device was made, under 1 sun AM 1.5 illumination (light intensity, ˜100 mW/cm2), and the device showed an open circuit voltage ( V oc) of 0.32 V, a short circuit current density ( J sc) of 7.67 mA/cm2, and a fill factor ( FF) of 0.37, yielding an overall power conversion efficiency of 0.91%. Also, the exciton dissociation and transportation processes of charge carriers in the device under illumination were explained according to its current density-voltage ( J- V) curve and the energy level diagram.

Perovskite nanoparticle-sensitized Ga 2O 3 nanorod arrays for CO detection at high temperature

DOE PAGES

Lin, Hui -Jan; Baltrus, John P.; Gao, Haiyong; ...

2016-04-04

Here, noble metal nanoparticles are extensively used for sensitizing metal oxide chemical sensors through the catalytic spillover mechanism. However, due to earth-scarcity and high cost of noble metals, finding replacements presents a great economic benefit. Besides, high temperature and harsh environment sensor applications demand material stability under conditions approaching thermal and chemical stability limits of noble metals. In this study, we employed thermally stable perovskite-type La 0.8Sr 0.2FeO 3 (LSFO) nanoparticle surface decoration on Ga 2O 3 nanorod array gas sensors and discovered an order of magnitude enhanced sensitivity to carbon monoxide at 500 °C. The LSFO nanoparticle catalysts wasmore » of comparable performance to that achieved by Pt nanoparticles, with a much lower weight loading than Pt. Detailed electron microscopy and X-ray photoelectron spectroscopy studies suggested the LSFO nanoparticle sensitization effect is attributed to a spillover-like effect associated with the gas-LSFO-Ga 2O 3 triple-interfaces that spread the negatively charged surface oxygen ions from LSFO nanoparticles surfaces over to β-Ga 2O 3 nanorod surfaces with faster surface CO oxidation reactions.« less

Perovskite Nanoparticle-Sensitized Ga2O3 Nanorod Arrays for CO Detection at High Temperature.

PubMed

Lin, Hui-Jan; Baltrus, John P; Gao, Haiyong; Ding, Yong; Nam, Chang-Yong; Ohodnicki, Paul; Gao, Pu-Xian

2016-04-13

Noble metal nanoparticles are extensively used for sensitizing metal oxide chemical sensors through the catalytic spillover mechanism. However, due to earth-scarcity and high cost of noble metals, finding replacements presents a great economic benefit. Besides, high temperature and harsh environment sensor applications demand material stability under conditions approaching thermal and chemical stability limits of noble metals. In this study, we employed thermally stable perovskite-type La(0.8)Sr(0.2)FeO3 (LSFO) nanoparticle surface decoration on Ga2O3 nanorod array gas sensors and discovered an order of magnitude enhanced sensitivity to carbon monoxide at 500 °C. The LSFO nanoparticle catalysts was of comparable performance to that achieved by Pt nanoparticles, with a much lower weight loading than Pt. Detailed electron microscopy and X-ray photoelectron spectroscopy studies suggested the LSFO nanoparticle sensitization effect is attributed to a spillover-like effect associated with the gas-LSFO-Ga2O3 triple-interfaces that spread the negatively charged surface oxygen ions from LSFO nanoparticles surfaces over to β-Ga2O3 nanorod surfaces with faster surface CO oxidation reactions.

Cu-doped ZnO nanorod arrays: the effects of copper precursor and concentration

PubMed Central

2014-01-01

Cu-doped ZnO nanorods have been grown at 90°C for 90 min onto a quartz substrate pre-coated with a ZnO seed layer using a hydrothermal method. The influence of copper (Cu) precursor and concentration on the structural, morphological, and optical properties of ZnO nanorods was investigated. X-ray diffraction analysis revealed that the nanorods grown are highly crystalline with a hexagonal wurtzite crystal structure grown along the c-axis. The lattice strain is found to be compressive for all samples, where a minimum compressive strain of −0.114% was obtained when 1 at.% Cu was added from Cu(NO3)2. Scanning electron microscopy was used to investigate morphologies and the diameters of the grown nanorods. The morphological properties of the Cu-doped ZnO nanorods were influenced significantly by the presence of Cu impurities. Near-band edge (NBE) and a broad blue-green emission bands at around 378 and 545 nm, respectively, were observed in the photoluminescence spectra for all samples. The transmittance characteristics showed a slight increase in the visible range, where the total transmittance increased from approximately 80% for the nanorods doped with Cu(CH3COO)2 to approximately 90% for the nanorods that were doped with Cu(NO3)2. PMID:24855460

Highly reproducible and sensitive silver nanorod array for the rapid detection of Allura Red in candy

NASA Astrophysics Data System (ADS)

Yao, Yue; Wang, Wen; Tian, Kangzhen; Ingram, Whitney Marvella; Cheng, Jie; Qu, Lulu; Li, Haitao; Han, Caiqin

2018-04-01

Allura Red (AR) is a highly stable synthetic red azo dye, which is widely used in the food industry to dye food and increase its attraction to consumers. However, the excessive consumption of AR can result in adverse health effects to humans. Therefore, a highly reproducible silver nanorod (AgNR) array was developed for surface enhanced Raman scattering (SERS) detection of AR in candy. The relative standard deviation (RSD) of AgNR substrate obtained from the same batch and different batches were 5.7% and 11.0%, respectively, demonstrating the high reproducibility. Using these highly reproducible AgNR arrays as the SERS substrates, AR was detected successfully, and its characteristic peaks were assigned by the density function theory (DFT) calculation. The limit of detection (LOD) of AR was determined to be 0.05 mg/L with a wide linear range of 0.8-100 mg/L. Furthermore, the AgNR SERS arrays can detect AR directly in different candy samples within 3 min without any complicated pretreatment. These results suggest the AgNR array can be used for rapid and qualitative SERS detection of AR, holding a great promise for expanding SERS application in food safety control field.

Enhanced photoelectrochemical properties of TiO2 nanorod arrays decorated with CdS nanoparticles

PubMed Central

Xie, Zheng; Liu, Xiangxuan; Wang, Weipeng; Liu, Can; Li, Zhengcao; Zhang, Zhengjun

2014-01-01

TiO2 nanorod arrays (TiO2 NRAs) sensitized with CdS nanoparticles were fabricated via successive ion layer adsorption and reaction (SILAR), and TiO2 NRAs were obtained by oxidizing Ti NRAs obtained through oblique angle deposition. The TiO2 NRAs decorated with CdS nanoparticles exhibited excellent photoelectrochemical and photocatalytic properties under visible light, and the one decorated with 20 SILAR cycles CdS nanoparticles shows the best performance. This can be attributed to the enhanced separation of electrons and holes by forming heterojunctions of CdS nanoparticles and TiO2 NRAs. This provides a promising way to fabricate the material for solar energy conversion and wastewater degradation. PMID:27877718

Orientation-Controllable ZnO Nanorod Array Using Imprinting Method for Maximum Light Utilization in Dye-Sensitized Solar Cells.

PubMed

Jeong, Huisu; Song, Hui; Lee, Ryeri; Pak, Yusin; Kumaresan, Yogeenth; Lee, Heon; Jung, Gun Young

2015-12-01

We present a holey titanium dioxide (TiO2) film combined with a periodically aligned ZnO nanorod layer (ZNL) for maximum light utilization in dye-sensitized solar cells (DSCs). Both the holey TiO2 film and the ZNL were simultaneously fabricated by imprint technique with a mold having vertically aligned ZnO nanorod (NR) array, which was transferred to the TiO2 film after imprinting. The orientation of the transferred ZNL such as laid, tilted, and standing ZnO NRs was dependent on the pitch and height of the ZnO NRs of the mold. The photoanode composed of the holey TiO2 film with the ZNL synergistically utilized the sunlight due to enhanced light scattering and absorption. The best power conversion efficiency of 8.5 % was achieved from the DSC with the standing ZNL, which represented a 33 % improvement compared to the reference cell with a planar TiO2.

Photoelectrocatalytic activity of a hydrothermally grown branched Zno nanorod-array electrode for paracetamol degradation.

PubMed

Lin, Chin Jung; Liao, Shu-Jun; Kao, Li-Cheng; Liou, Sofia Ya Hsuan

2015-06-30

Hierarchical branched ZnO nanorod (B-ZnR) arrays as an electrode for efficient photoelectrocatalytic degradation of paracetamol were grown on fluorine-doped tin oxide substrates using a solution route. The morphologic and structural studies show the ZnO trunks are single-crystalline hexagonal wurtzite ZnO with a [0001] growth direction and are densely covered by c-axis-oriented ZnO branches. The obvious enhancement in photocurrent response of the B-ZnR electrode was obtained than that in the ZnO nanoparticle (ZnO NP) electrode. For the photoelectrocatalytic degradation of paracetamol in 20 h, the conversion fraction of the drug increased from 32% over ZnO NP electrode to 62% over B-ZnR arrays with about 3-fold increase in initial reaction rate. The light intensity-dependent photoelectrocatalytic experiment indicated that the superior performance over the B-ZnR electrode was mainly ascribed to the increased specific surface area without significantly sacrificing the charge transport and pollutant diffusion efficiencies. Two aromatic intermediate compounds were observed and eventually converted into harmless carboxylic acids and ammonia. Hierarchical tree-like ZnO arrays can be considered effective alternatives to improve photoelectro degradation rates without the need for expensive additives. Copyright © 2015 Elsevier B.V. All rights reserved.

Near-infrared photoluminescence biosensing platform with gold nanorods-over-gallium arsenide nanohorn array.

PubMed

Zhang, Yiming; Jiang, Tao; Tang, Longhua

2017-11-15

The near-infrared (NIR) optical detection of biomolecules with high sensitivity and reliability have been expected, however, it is still a challenge. In this work, we present a gold nanorods (AuNRs)-over-gallium arsenide nanohorn-like array (GaAs NHA) system that can be used for the ultrasensitive and specific NIR photoluminescence (PL) detection of DNA and proteins. The fabrication of GaAs NHA involved the technique of colloidal lithography and inductively coupled plasma dry etching, yielding large-area and well-defined nanostructural array, and exhibiting an improved PL emission compared to the planar GaAs substrate. Importantly, we found that the DNA-bridged AuNRs attachment on NHA could further improve the PL intensity from GaAs, and thereby provide the basis for the NIR optical sensing of biological analytes. We demonstrated that DNA and thrombin could be sensitively and specifically detected, with the detection limit of 1 pM for target DNA and 10 pM for thrombin. Such ultrasensitive NIR optical platform can extend to the detection of other biomarkers and is promising for clinical diagnostics. Copyright © 2017 Elsevier B.V. All rights reserved.

Polyethylene glycol assisted growth of Sn-doped ZnO nanorod arrays prepared via sol-gel immersion method

NASA Astrophysics Data System (ADS)

Ismail, A. S.; Mamat, M. H.; Malek, M. F.; Saidi, S. A.; Yusoff, M. M.; Mohamed, R.; Sin, N. D. Md; Suriani, A. B.; Rusop, M.

2018-05-01

Tin-doped zinc oxide (SZO) nanorod films at different concentrations of polyethylene glycol (PEG) were successfully deposited on zinc oxide (ZnO) seeded layer catalyst using sol-gel immersion method. The morphology of the samples were characterized using field emission scanning electron microscopy (FESEM), optical properties using UV-Vis spectrophotometer and electrical properties using I-V measurement system. The current-voltage (I-V) characteristics displayed that 5 wt % sample produced the highest conductivity.

Strong light coupling effect for a glancing-deposited silver nanorod array in the Kretschmann configuration

PubMed Central

2014-01-01

In this work, three slanted silver nanorod arrays (NRAs) with different thicknesses are fabricated using the glancing angle deposition method. Each silver NRA in the Kretschmann configuration is arranged to form a prism/NRA/air system. Attenuated total reflection occurs over the visible wavelengths and wide incident angles of both s- and p-polarization states. The extinctance is inversely proportional to the thickness of the Ag NRA. The thinnest NRA, with a thickness of 169 nm, exhibits strong extinctance of more than 80% over the visible wavelengths. The associated forward scatterings from the three NRAs are measured and compared under illumination with a laser beam with a wavelength of 632.8 nm. PMID:25352769

Superior environment resistance of quartz crystal microbalance with anatase TiO2/ZnO nanorod composite films

NASA Astrophysics Data System (ADS)

Qiang, Wei; Wei, Li; Shaodan, Wang; Yu, Bai

2015-08-01

The precise measurement of quartz crystal microbalance (QCM) in the detection and weighing of organic gas molecules is achieved due to excellent superhydrophobicity of a deposited film composite. Photocatalysis is utilized as a method for the self-cleaning of organic molecules on the QCM for extended long-term stability in the precision of the instrument. In this paper, ZnO nanorod array is prepared via in situ methods on the QCM coated with Au film via hydrothermal process. Subsequently, a TiO2/ZnO composite film is synthesized by surface modification with TiO2 via sol-gel methods. Results show the anatase TiO2/ZnO nanorod composite film with a sharp, pencil-like structure exhibiting excellent superhydrophobicity (water contact angle of 155°), non-sticking water properties, and an autonomous cleaning property under UV irradiation. The anatase TiO2/ZnO nanorod composite film facilitates the precise measurement and extended lifetime of the QCM for the detection of organic gas molecules.

Electrical Measurements on Iridium Dioxide Nanorods

NASA Astrophysics Data System (ADS)

Lin, Y. H.; Lee, T. C.; Lin, J. J.; Chang, H. M.; Huang, Y. S.

2006-09-01

Iridium dioxide (IrO2) nanorods have been prepared by metal-organic chemical vapor deposition method. Applying the standard electron-beam lithography technique, a single nanorod with a diameter of 110 nm is contacted by three Cr/Au fingers from above. The resistance measurements on this nanorod have been performed between 10 and 300 K, using different probe configurations. We observe that the resistivity ρ of the nanorod has a value ⩽ 120 μΩ cm at 300 K. On the other hand, the temperature dependence of the contact resistance R obeys the law logR ∝ T-1/2 below 100 K. The conduction process through the contact is ascribed to the transport of electrons via hopping in granular metals accidentally formed at the contact region.

PDMS-based triboelectric and transparent nanogenerators with ZnO nanorod arrays.

PubMed

Ko, Yeong Hwan; Nagaraju, Goli; Lee, Soo Hyun; Yu, Jae Su

2014-05-14

Vertically-grown ZnO nanorod arrays (NRAs) on indium tin oxide (ITO)-coated polyethylene terephthalate (PET), as a top electrode of nanogenerators, were investigated for the antireflective property as well as an efficient contact surface in bare polydimethysiloxane (PDMS)-based triboelectric nanogenerators. Compared to conventional ITO-coated PET (i.e., ITO/PET), the ZnO NRAs considerably suppressed the reflectance from 20 to 9.7% at wavelengths of 300-1100 nm, creating a highly transparent top electrode, as demonstrated by theoretical analysis. Also, the interval time between the peaks of generated output voltage under external pushing forces was significantly decreased from 1.84 to 0.19 s because the reduced contact area of the PDMS by discrete surfaces of the ZnO NRAs on ITO/PET causes a rapid sequence for triboelectric charge generation process including rubbing and separating. Therefore, the use of this top electrode enabled to operate the transparent PDMS-based triboelectric nanogenerator at high frequency of external pushing force. Under different external forces of 0.3-10 kgf, the output voltage and current were also characterized.

Growth of high-density ZnO nanorods on wood with enhanced photostability, flame retardancy and water repellency

NASA Astrophysics Data System (ADS)

Kong, Lizhuo; Tu, Kunkun; Guan, Hao; Wang, Xiaoqing

2017-06-01

Zinc oxide (ZnO) nanorod arrays were successfully assembled on the wood surface in situ via a two-step process consisting of formation of ZnO seeds and subsequent crystal growth under hydrothermal conditions at a low temperature. The morphology and crystalline structure of the formed ZnO nanorods were studied by field-emission scanning electron microscopy (FE-SEM) and X-ray diffraction (XRD). Highly dense and uniform arrays of ZnO nanorods with well-defined hexagonal facets were generated on the wood surface by tuning the concentration of the ZnO growth solution during the hydrothermal treatment. Accelerated weathering tests indicated that the assembled ZnO nanorod arrays were highly protective against UV radiation and greatly enhanced the photostability of the coated wood. Meanwhile, the ZnO nanorod-coated wood can withstand continuous exposure to flame with only minor smoldering in contrast with the pristine wood catching fire easily and burning rapidly. Moreover, when further modified with low-surface-energy stearic acid, the ZnO nanorod decorated wood surface can be transformed into a superhydrophobic surface, with a water contact angle (CA) of ∼154°. Such ZnO nanorod-modified woods with enhanced photostability, flame retardancy and water repellency offer an interesting alternative to conventional wood preservation strategies, highlighting their potential applications in some novel wood products.

T-Nb2O5 quantum dots prepared by electrodeposition for fast Li ion intercalation/deintercalation

NASA Astrophysics Data System (ADS)

Zhao, Guangyu; Ye, Chen; Zhang, Li; Li, Changle; Sun, Kening

2017-05-01

T-Nb2O5 quantum dots were electrodeposited on Ti nanorod arrays to prepare Ti@T-Nb2O5 core-shell array electrodes. The particle size of T-Nb2O5 could be manipulated by adjusting the depositing current density, and quantum dots several nanometers in size could be obtained at a deposition current of 6 mA cm-2. Benefiting from the ultra-small particle size of T-Nb2O5 and the array structure, Ti@T-Nb2O5 nanorod arrays exhibited good rate capability and durability when used as self-supported Li ion battery anodes. The arrays possessed capacities of 350 and 70 mAh g-1 at rate currents of 0.06 and 30 A g-1, respectively. Furthermore, the electrodes maintained 500 cycles without obvious decay at a high rate current of 30 A g-1.

Three-dimensional architecture hybrid perovskite solar cells using CdS nanorod arrays as an electron transport layer

NASA Astrophysics Data System (ADS)

Song, Zihang; Tong, Guoqing; Li, Huan; Li, Guopeng; Ma, Shuai; Yu, Shimeng; Liu, Qian; Jiang, Yang

2018-01-01

Three-dimensional (3D) architecture perovskite solar cells (PSCs) using CdS nanorod (NR) arrays as an electron transport layer were designed and prepared layer-by-layer via a physical-chemical vapor deposition (P-CVD) process. The CdS NRs not only provided a scaffold to the perovskite film, but also increased the interfacial contact between the perovskite film and electron transport layer. As an optimized result, a high power conversion efficiency of 12.46% with a short-circuit current density of 19.88 mA cm-2, an open-circuit voltage of 1.01 V and a fill factor of 62.06% was obtained after 12 h growth of CdS NRs. It was four times the efficiency of contrast planar structure with a similar thickness. The P-CVD method assisted in achieving flat and voidless CH3NH3PbI3-x Cl x perovskite film and binding the CdS NRs and perovskite film together. The different density of CdS NRs had obvious effects on light transmittance of 350-550 nm, the interfacial area and the difficulty of combining layers. Moreover, the efficient 1D transport paths for electrons and multiple absorption of light, which are generated in 3D architecture, were beneficial to realize a decent power conversion efficiency.

Fabrication of nickel hydroxide electrodes with open-ended hexagonal nanotube arrays for high capacitance supercapacitors.

PubMed

Wu, Mao-Sung; Huang, Kuo-Chih

2011-11-28

A nickel hydroxide electrode with open-ended hexagonal nanotube arrays, prepared by hydrolysis of nickel chloride in the presence of hexagonal ZnO nanorods, shows a very high capacitance of 1328 F g(-1) at a discharge current density of 1 A g(-1) due to the significantly improved ion transport.

Aqueous chemical growth of free standing vertical ZnO nanoprisms, nanorods and nanodiskettes with improved texture co-efficient and tunable size uniformity

NASA Astrophysics Data System (ADS)

Ram, S. D. Gopal; Ravi, G.; Athimoolam, A.; Mahalingam, T.; Kulandainathan, M. Anbu

2011-12-01

Tuning the morphology, size and aspect ratio of free standing ZnO nanostructured arrays by a simple hydrothermal method is reported. Pre-coated ZnO seed layers of two different thicknesses (≈350 nm or 550 nm) were used as substrates to grow ZnO nanostructures for the study. Various parameters such as chemical ambience, pH of the solution, strength of the Zn2+ atoms and thickness of seed bed are varied to analyze their effects on the resultant ZnO nanostructures. Vertically oriented hexagonal nanorods, multi-angular nanorods, hexagonal diskette and popcorn-like nanostructures are obtained by altering the experimental parameters. All the produced nanostructures were analysed by X-ray powder diffraction analysis and found to be grown in the (002) orientation of wurtzite ZnO. The texture co-efficient of ZnO layer was improved by combining a thick seed layer with higher cationic strength. Surface morphological studies reveal various nanostructures such as nanorods, diskettes and popcorn-like structures based on various preparation conditions. The optical property of the closest packed nanorods array was recorded by UV-VIS spectrometry, and the band gap value simulated from the results reflect the near characteristic band gap of ZnO. The surface roughness profile taken from the Atomic Force Microscopy reveals a roughness of less than 320 nm.

Fabrication and photovoltaic properties of ZnO nanorods/perovskite solar cells

DOE Office of Scientific and Technical Information (OSTI.GOV)

Shirahata, Yasuhiro; Tanaike, Kohei; Akiyama, Tsuyoshi

2016-02-01

ZnO nanorods/perovskite solar cells with different lengths of ZnO nanorods were fabricated. The ZnO nanorods were prepared by chemical bath deposition and directly confirmed to be hexagon-shaped nanorods. The lengths of the ZnO nanorads were controlled by deposition condition of ZnO seed layer. Photovoltaic properties of the ZnO nanorods/CH{sub 3}NH{sub 3}PbI{sub 3} solar cells were investigated by measuring current density-voltage characteristics and incident photon to current conversion efficiency. The highest conversion efficiency was obtained in ZnO nanorods/CH{sub 3}NH{sub 3}PbI{sub 3} with the longest ZnO nanorods.

Enhanced polarization of (11-22) semi-polar InGaN nanorod array structure

NASA Astrophysics Data System (ADS)

Athanasiou, M.; Smith, R. M.; Hou, Y.; Zhang, Y.; Gong, Y.; Wang, T.

2015-10-01

By means of a cost effective nanosphere lithography technique, an InGaN/GaN multiple quantum well structure grown on (11-22) semipolar GaN has been fabricated into two dimensional nanorod arrays which form a photonic crystal (PhC) structure. Such a PhC structure demonstrates not only significantly increased emission intensity, but also an enhanced polarization ratio of the emission. This is due to an effective inhibition of the emission in slab modes and then redistribution to the vertical direction, thus minimizing the light scattering processes that lead to randomizing of the optical polarization. The PhC structure is designed based on a standard finite-difference-time-domain simulation, and then optically confirmed by detailed time-resolved photoluminescence measurements. The results presented pave the way for the fabrication of semipolar InGaN/GaN based emitters with both high efficiency and highly polarized emission.

Gold nanoparticle-embedded silk protein-ZnO nanorod hybrids for flexible bio-photonic devices

NASA Astrophysics Data System (ADS)

Gogurla, Narendar; Kundu, Subhas C.; Ray, Samit K.

2017-04-01

Silk protein has been used as a biopolymer substrate for flexible photonic devices. Here, we demonstrate ZnO nanorod array hybrid photodetectors on Au nanoparticle-embedded silk protein for flexible optoelectronics. Hybrid samples exhibit optical absorption at the band edge of ZnO as well as plasmonic energy due to Au nanoparticles, making them attractive for selective UV and visible wavelength detection. The device prepared on Au-silk protein shows a much lower dark current and a higher photo to dark-current ratio of ∼105 as compared to the control sample without Au nanoparticles. The hybrid device also exhibits a higher specific detectivity due to higher responsivity arising from the photo-generated hole trapping by Au nanoparticles. Sharp pulses in the transient photocurrent have been observed in devices prepared on glass and Au-silk protein substrates due to the light induced pyroelectric effect of ZnO, enabling the demonstration of self-powered photodetectors at zero bias. Flexible hybrid detectors have been demonstrated on Au-silk/polyethylene terephthalate substrates, exhibiting characteristics similar to those fabricated on rigid glass substrates. A study of the performance of photodetectors with different bending angles indicates very good mechanical stability of silk protein based flexible devices. This novel concept of ZnO nanorod array photodetectors on a natural silk protein platform provides an opportunity to realize integrated flexible and self-powered bio-photonic devices for medical applications in near future.

Omnidirectional anti-reflection properties of vertically align SiO2 nanorod films prepared by electron beam evaporation with glancing angle deposition

NASA Astrophysics Data System (ADS)

Prachachet, R.; Samransuksamer, B.; Horprathum, M.; Eiamchai, P.; Limwichean, S.; Chananonnawathorn, C.; Lertvanithphol, T.; Muthitamongkol, P.; Boonruang, S.; Buranasiri, P.

2018-03-01

Omnidirectional anti-reflection coating nanostructure film have attracted enormous attention for the developments of the optical coating, lenses, light emitting diode, display and photovoltaic. However, fabricated of the omnidirectional antireflection nanostructure film on glass substrate in large area was a challenge topic. In the past two decades, the invention of glancing angle deposition technique as a growth of well-controlled two and three-dimensional morphologies has gained significant attention because of it is simple, fast, cost-effective and high mass production capability. In this present work, the omnidirectional anti-reflection nanostructure coating namely silicon dioxide (SiO2) nanorods has been investigated for optimized high transparent layer at all light incident angle. The SiO2 nanorod films of an optimally low refractive index have been fabricated by electron beam evaporation with the glancing angle deposition technique. The morphological of the prepared sampled were characterized by field-emission scanning electron microscope (FE-SEM) and high-resolution transmission electron microscope (HRTEM). The optical transmission and omnidirectional property of the SiO2 nanorod films were investigated by UV-Vis-NIR spectrophotometer. The measurement were performed at normal incident angle and a full spectral range of 200 - 2000 nm. The angle dependent transmission measure were investigated by rotating the specimen, with incidence angle defined relative to the surface normal of the prepared samples. The morphological characterization results showed that when the glancing angle deposition technique was applied, the vertically align SiO2 nanorods with partially isolated columnar structure can be constructed due to the enhanced shadowing and limited addtom diffusion effect. The average transmission of the vertically align SiO2 nanorods were higher than the glass substrate reference sample over the visible wavelength range at all incident angle due to the

Field gradients can control the alignment of nanorods.

PubMed

Ooi, Chinchun; Yellen, Benjamin B

2008-08-19

This work is motivated by the unexpected experimental observation that field gradients can control the alignment of nonmagnetic nanorods immersed inside magnetic fluids. In the presence of local field gradients, nanorods were observed to align perpendicular to the external field at low field strengths, but parallel to the external field at high field strengths. The switching behavior results from the competition between a preference to align with the external field (orientational potential energy) and preference to move into regions of minimum magnetic field (positional potential energy). A theoretical model is developed to explain this experimental behavior by investigating the statistics of nanorod alignment as a function of both the external uniform magnetic field strength and the local magnetic field variation above a periodic array of micromagnets. Computational phase diagrams are developed which indicate that the relative population of nanorods in parallel and perpendicular states can be adjusted through several control parameters. However, an energy barrier to rotation was discovered to influence the rate kinetics and restrict the utility of this assembly technique to nanorods which are slightly shorter than the micromagnet length. Experimental results concerning the orientation of nanorods inside magnetic fluid are also presented and shown to be in strong agreement with the theoretical work.

Large-scale fabrication of single crystalline tin nanowire arrays

NASA Astrophysics Data System (ADS)

Luo, Bin; Yang, Dachi; Liang, Minghui; Zhi, Linjie

2010-09-01

Large-scale single crystalline tin nanowire arrays with preferred lattice orientation along the [100] direction were fabricated in porous anodic aluminium oxide (AAO) membranes by the electrodeposition method using copper nanorod as a second electrode.Large-scale single crystalline tin nanowire arrays with preferred lattice orientation along the [100] direction were fabricated in porous anodic aluminium oxide (AAO) membranes by the electrodeposition method using copper nanorod as a second electrode. Electronic supplementary information (ESI) available: Experimental details and the information for single crystalline copper nanorods. See DOI: 10.1039/c0nr00206b

Growth of aragonite calcium carbonate nanorods in the biomimetic anodic aluminum oxide template

NASA Astrophysics Data System (ADS)

Lee, Inho; Han, Haksoo; Lee, Sang-Yup

2010-04-01

In this study, a biomimetic template was prepared and applied for growing calcium carbonate (CaCO 3) nanorods whose shape and polymorphism were controlled. A biomimetic template was prepared by adsorbing catalytic dipeptides into the pores of an anodic aluminum oxide (AAO) membrane. Using this peptide-adsorbed template, mineralization and aggregation of CaCO 3 was carried out to form large nanorods in the pores. The nanorods were aragonite and had a structure similar to nanoneedle assembly. This aragonite nanorod formation was driven by both the AAO template and catalytic function of dipeptides. The AAO membrane pores promoted generation of aragonite polymorph and guided nanorod formation by guiding the nanorod growth. The catalytic dipeptides promoted the aggregation and further dehydration of calcium species to form large nanorods. Functions of the AAO template and catalytic dipeptides were verified through several control experiments. This biomimetic approach makes possible the production of functional inorganic materials with controlled shapes and crystalline structures.

Templated synthesis of metal nanorods in silica nanotubes

DOE Office of Scientific and Technical Information (OSTI.GOV)

Yin, Yadong; Gao, Chuanbo

A method of preparing a metal nanorod. The method includes seeding a metal nanoparticle within the lumen of a nanotube, and growing a metal nanorod from the seeded metal nanoparticle to form a metal nanorod-nanotube composite. In some cases, the nanotube includes metal binding ligands attached to the inner surface. Growing of the metal nanorod includes incubating the seeded nanotube in a solution that includes: a metal source for the metal in the metal nanorod, the metal source including an ion of the metal; a coordinating ligand that forms a stable complex with the metal ion; a reducing agent formore » reducing the metal ion, and a capping agent that stabilizes atomic monomers of the metal. Compositions derived from the method are also provided.« less

Influence of Zr doping on structure and morphology of TiO2 nanorods prepared using hydrothermal method

NASA Astrophysics Data System (ADS)

Muslimin, Masliana; Jumali, Mohammad Hafizuddin; Tee, Tan Sin; Beng, Lee Hock; Hui, Tan Chun; Chin, Yap Chi

2018-04-01

The aim of this work is to investigate the effect of Zr doping on TiO2 nanostructure. TiO2 nanorods thin films with different Zr-doping concentrations (6 × 10-3 M, 13 × 10-3 M and 25 × 10-3 M) were successfully prepared using a simple hydrothermal method. The structural and morphological properties of the samples were evaluated using XRD and FESEM respectively. The XRD results revealed that the TiO2 in all samples stabilized as rutile phase. The FESEM micrographs confirmed that TiO2 exist as square like nanorods with blunt tips. Although the crystallographic nature remains unchanged, the introduction of Zr has altered the surface density, structure and morphology of TiO2 which subsequently will have significant effect on its properties.

Hydroxyapatite nanorods: soft-template synthesis, characterization and preliminary in vitro tests.

PubMed

Nguyen, Nga Kim; Leoni, Matteo; Maniglio, Devid; Migliaresi, Claudio

2013-07-01

Synthetic hydroxyapatite nanorods are excellent candidates for bone tissue engineering applications. In this study, hydroxyapatite nanorods resembling bone minerals were produced by using soft-template method with cetyltrimethylammonium bromide. Composite hydroxyapatite/poly(D, L)lactic acid films were prepared to evaluate the prepared hydroxyapatite nanorods in terms of cell affinity. Preliminary in vitro experiments showed that aspect ratio and film surface roughness play a vital role in controlling adhesion and proliferation of human osteoblast cell line MG 63. The hydroxyapatite nanorods with aspect ratios in the range of 5.94-7 were found to possess distinctive properties, with the corresponding hydroxyapatite/poly(D, L)lactic acid films promoting cellular confluence and a fast formation of collagen fibers as early as after 7 days of culture.

Fabrication of TiN nanorods by electrospinning and their electrochemical properties

NASA Astrophysics Data System (ADS)

Sun, Dongfei; Lang, Junwei; Yan, Xingbin; Hu, Litian; Xue, Qunji

2011-05-01

TiN nanorods were synthesized using electrospinning technique followed by thermolysis in different atmospheres. A dimethyl formamide-ethanol solution of poly-(vinyl pyrrolidone) and Ti (IV)-isopropoxide was used as the electrospinning precursor solution and as-spun nanofibers were calcined at 500 °C in air to generate TiO 2 nanofibers. Subsequently, a conversion from TiO 2 nanofibers to TiN nanorods was employed by the nitridation treatment at 600˜1400 °C in ammonia atmosphere. A typical characteristic of the final products was that the pristine nanofibers were cut into nanorods. The conversion from TiO 2 to TiN was realized when the nitridation temperature was above 800 °C. As-prepared nanorods were composed of TiN nano-crystallites and the average crystallite size gradually increased with the increase of the nitridation temperature. Electrochemical properties of TiN nanorods showed strong dependence on the nitridation temperature. The maximum value of the specific capacitance was obtained from the TiN nanorods prepared at 800 °C.

Enhanced photoelectrochemical property of ZnO nanorods array synthesized on reduced graphene oxide for self-powered biosensing application.

PubMed

Kang, Zhuo; Gu, Yousong; Yan, Xiaoqin; Bai, Zhiming; Liu, Yichong; Liu, Shuo; Zhang, Xiaohui; Zhang, Zheng; Zhang, Xueji; Zhang, Yue

2015-02-15

We have realized the direct synthesis of ZnO nanorods (ZnO NRs) array on reduced graphene layer (rGO), and demonstrated the enhanced photoelectrochemical (PEC) property of the rGO/ZnO based photoanode under UV irradiation compared with the pristine ZnO NRs array. The introduction of the rGO layer resulted in a favorable energy band structure for electron migration, which finally led to the efficient photoinduced charge separation. Such nanostructure was subsequently employed for self-powered PEC biosensing of glutathione in the condition of 0 V bias, with a linear range from 10 to 200 µM, a detection limit of 2.17 µM, as well as excellent selectivity, reproducibility and stability. The results indicated the rGO/ZnO nanostructure is a competitive candidate in the PEC biosensing field. Copyright © 2014 Elsevier B.V. All rights reserved.

Gigahertz acoustic vibrations of elastically anisotropic Indium–tin-oxide nanorod arrays [Gigahertz modulation of the full visible spectrum via acoustic vibrations of elastically anisotropic Indium-tin-oxide nanorod arrays

DOE PAGES

Guo, Peijun; Schaller, Richard D.; Ocola, Leonidas E.; ...

2016-08-15

Active control of light is important for photonic integrated circuits, optical switches,. and telecommunications. Coupling light with acoustic vibrations in nanoscale optical resonators offers optical modulation capabilities with high bandwidth and Small footprint Instead of using noble metals, here we introduce indium tin-oxide nanorod arrays (ITO-NRAs) as the operating media;and demonstrate optical modulation covering the visible spectral range (from 360 to 700 nm), with similar to 20 GHz bandwidth through the excitation of coherent acoustic vibrations in ITO-NRAs. This broadband modulation results from the collective optical diffraction by the dielectric ITO-NRAs, and a high differential transmission modulation up to 10%more » is achieved through efficient near-infrared, on-plasmon-resonance pumping. By combining the frequency signatures Of the vibrational modes with finite-element simulations, we,further determine the anisotropic elastic constants for single-crystalline ITO, which are not known-for the bulk phase. Furthermore, this technique to determine elastic constants using Coherent acoustic vibrations of uniform nanostructures can be generalized to the study of other inorganic materials.« less

Gigahertz acoustic vibrations of elastically anisotropic Indium–tin-oxide nanorod arrays [Gigahertz modulation of the full visible spectrum via acoustic vibrations of elastically anisotropic Indium-tin-oxide nanorod arrays

DOE Office of Scientific and Technical Information (OSTI.GOV)

Guo, Peijun; Schaller, Richard D.; Ocola, Leonidas E.

Active control of light is important for photonic integrated circuits, optical switches,. and telecommunications. Coupling light with acoustic vibrations in nanoscale optical resonators offers optical modulation capabilities with high bandwidth and Small footprint Instead of using noble metals, here we introduce indium tin-oxide nanorod arrays (ITO-NRAs) as the operating media;and demonstrate optical modulation covering the visible spectral range (from 360 to 700 nm), with similar to 20 GHz bandwidth through the excitation of coherent acoustic vibrations in ITO-NRAs. This broadband modulation results from the collective optical diffraction by the dielectric ITO-NRAs, and a high differential transmission modulation up to 10%more » is achieved through efficient near-infrared, on-plasmon-resonance pumping. By combining the frequency signatures Of the vibrational modes with finite-element simulations, we,further determine the anisotropic elastic constants for single-crystalline ITO, which are not known-for the bulk phase. Furthermore, this technique to determine elastic constants using Coherent acoustic vibrations of uniform nanostructures can be generalized to the study of other inorganic materials.« less

Graded core/shell semiconductor nanorods and nanorod barcodes

DOEpatents

Alivisatos, A. Paul; Scher, Erik C.; Manna, Liberato

2010-12-14

Graded core/shell semiconductor nanorods and shaped nanorods are disclosed comprising Group II-VI, Group III-V and Group IV semiconductors and methods of making the same. Also disclosed are nanorod barcodes using core/shell nanorods where the core is a semiconductor or metal material, and with or without a shell. Methods of labeling analytes using the nanorod barcodes are also disclosed.

Graded core/shell semiconductor nanorods and nanorod barcodes

DOEpatents

Alivisatos, A. Paul; Scher, Erik C.; Manna, Liberato

2013-03-26

Graded core/shell semiconductor nanorods and shapped nanorods are disclosed comprising Group II-VI, Group III-V and Group IV semiconductors and methods of making the same. Also disclosed are nanorod barcodes using core/shell nanorods where the core is a semiconductor or metal material, and with or without a shell. Methods of labeling analytes using the nanorod barcodes are also disclosed.

A TiO2/FeMnP Core/Shell Nanorod Array Photoanode for Efficient Photoelectrochemical Oxygen Evolution.

PubMed

Schipper, Desmond E; Zhao, Zhenhuan; Leitner, Andrew P; Xie, Lixin; Qin, Fan; Alam, Md Kamrul; Chen, Shuo; Wang, Dezhi; Ren, Zhifeng; Wang, Zhiming; Bao, Jiming; Whitmire, Kenton H

2017-04-25

A variety of catalysts have recently been developed for electrocatalytic oxygen evolution, but very few of them can be readily integrated with semiconducting light absorbers for photoelectrochemical or photocatalytic water splitting. Here, we demonstrate an efficient core/shell photoanode with a highly active oxygen evolution electrocatalyst shell (FeMnP) and semiconductor core (rutile TiO 2 ) for photoelectrochemical oxygen evolution reaction. Metal-organic chemical vapor deposition from a single-source precursor was used to ensure good contact between the FeMnP and the TiO 2 . The TiO 2 /FeMnP core/shell photoanode reaches the theoretical photocurrent density for rutile TiO 2 of 1.8 mA cm -2 at 1.23 V vs reversible hydrogen electrode under simulated 100 mW cm -2 (1 sun) irradiation. The dramatic enhancement is a result of the synergistic effects of the high oxygen evolution reaction activity of FeMnP (delivering an overpotential of 300 mV with a Tafel slope of 65 mV dec -1 in 1 M KOH) and the conductive interlayer between the surface active sites and semiconductor core which boosts the interfacial charge transfer and photocarrier collection. The facile fabrication of the TiO 2 /FeMnP core/shell nanorod array photoanode offers a compelling strategy for preparing highly efficient photoelectrochemical solar energy conversion devices.

Binder-free ZnO@ZnSnO3 quantum dots core-shell nanorod array anodes for lithium-ion batteries

NASA Astrophysics Data System (ADS)

Tan, Hsiang; Cho, Hsun-Wei; Wu, Jih-Jen

2018-06-01

In this work, ZnSnO3 quantum dots (QDs), instead of commonly used conductive carbon, are grown on the ZnO nanorod (NR) array to construct the binder-free ZnO@ZnSnO3 QDs core-shell NR array electrode on carbon cloth for lithium-ion battery. The ZnO@ZnSnO3 QDs core-shell NR array electrode exhibits excellent lithium storage performance with an improved cycling performance and superior rate capability compared to the ZnO NR array electrode. At a current density of 200 mAg-1, 15.8% capacity loss is acquired in the ZnO@ZnSnO3 QDs core-shell NR array electrode after 110 cycles with capacity retention of 1073 mAhg-1. Significant increases in reversible capacities from 340 to 545 mAhg-1 and from 95 to 390 mAhg-1 at current densities of 1000 and 2000 mAg-1, respectively, are achieved as the ZnO NR arrays are coated with the ZnSnO3 QD shells. The remarkably improved electrochemical performances result from that the configuration of binder-free ZnO@ZnSnO3 QDs core-shell NR array electrode not only facilitates the charge transfer through the solid electrolyte interface and the electronic/ionic conduction boundary as well as lithium ion diffusion but also effectively accommodates the volume change during repeated charge/discharge processes.

Tuning of defects in ZnO nanorod arrays used in bulk heterojunction solar cells

PubMed Central

2012-01-01

With particular focus on bulk heterojunction solar cells incorporating ZnO nanorods, we study how different annealing environments (air or Zn environment) and temperatures impact on the photoluminescence response. Our work gives new insight into the complex defect landscape in ZnO, and it also shows how the different defect types can be manipulated. We have determined the emission wavelengths for the two main defects which make up the visible band, the oxygen vacancy emission wavelength at approximately 530 nm and the zinc vacancy emission wavelength at approximately 630 nm. The precise nature of the defect landscape in the bulk of the nanorods is found to be unimportant to photovoltaic cell performance although the surface structure is more critical. Annealing of the nanorods is optimum at 300°C as this is a sufficiently high temperature to decompose Zn(OH)2 formed at the surface of the nanorods during electrodeposition and sufficiently low to prevent ITO degradation. PMID:23186280

ZnO nanorods for electronic and photonic device applications

NASA Astrophysics Data System (ADS)

Yi, Gyu-Chul; Yoo, Jinkyoung; Park, Won Il; Jung, Sug Woo; An, Sung Jin; Kim, H. J.; Kim, D. W.

2005-11-01

We report on catalyst-free growth of ZnO nanorods and their nano-scale electrical and optical device applications. Catalyst-free metalorganic vapor-phase epitaxy (MOVPE) enables fabrication of size-controlled high purity ZnO single crystal nanorods. Various high quality nanorod heterostructures and quantum structures based on ZnO nanorods were also prepared using the MOVPE method and characterized using scanning electron microscopy, transmission electron microscopy, and optical spectroscopy. From the photoluminescence spectra of ZnO/Zn 0.8Mg 0.2O nanorod multi-quantum-well structures, in particular, we observed a systematic blue-shift in their PL peak position due to quantum confinement effect of carriers in nanorod quantum structures. For ZnO/ZnMgO coaxial nanorod heterostructures, photoluminescence intensity was significantly increased presumably due to surface passivation and carrier confinement. In addition to the growth and characterizations of ZnO nanorods and their quantum structures, we fabricated nanoscale electronic devices based on ZnO nanorods. We report on fabrication and device characteristics of metal-oxidesemiconductor field effect transistors (MOSFETs), Schottky diodes, and metal-semiconductor field effect transistors (MESFETs) as examples of the nanodevices. In addition, electroluminescent devices were fabricated using vertically aligned ZnO nanorods grown p-type GaN substrates, exhibiting strong visible electroluminescence.

Removal of Carmine from Aqueous Solution by Carbonated Hydroxyapatite Nanorods

PubMed Central

Liu, Guanxiong; Xue, Caibao; Zhu, Peizhi

2017-01-01

In this study, carbonated hydroxyapatite (CHA) nanorods were prepared by a novel hydrothermal method. The crystallinity and chemical structure of synthesized CHA nanorods was characterized by transmission electron microscopy (TEM), X-ray diffraction (XRD), Raman spectroscopy and X-ray photoelectron spectroscopy (XPS), respectively. Carmine was selected as representative organic dyes to study the adsorption capacities of CHA nanorods. Mechanistic studies of carmine adsorption by CHA nanorods show that the adsorption processes both follow the pseudo-second-order kinetic model and fit the Langmuir isotherm model well. The CHA nanorods exhibited a high adsorption capacity of 85.51 mg/g for carmine at room-temperature. The experimental results prove that CHA nanorods can be promising absorbents for removing organic dye pollutants in wastewater from paper and textile plants. PMID:28587250

MIL-68 (In) nano-rods for the removal of Congo red dye from aqueous solution.

PubMed

Jin, Li-Na; Qian, Xin-Ye; Wang, Jian-Guo; Aslan, Hüsnü; Dong, Mingdong

2015-09-01

MIL-68 (In) nano-rods were prepared by a facile solvothermal synthesis using NaOAc as modulator agent at 100°C for 30 min. The BET test showed that the specific surface area and pore volume of MIL-68 (In) nanorods were 1252 m(2) g(-1) and 0.80 cm(3) g(-1), respectively. The as-prepared MIL-68 (In) nanorods showed excellent adsorption capacity and rapid adsorption rate for removal of Congo red (CR) dye from water. The maximum adsorption capacity of MIL-68 (In) nanorods toward CR reached 1204 mg g(-1), much higher than MIL-68 (In) microrods and most of the previously reported adsorbents. The adsorption process of CR by MIL-68 (In) nano-rods was investigated and found to be obeying the Langmuir adsorption model in addition to pseudo-second-order rate equation. Moreover, the MIL-68 (In) nanorods showed an acceptable reusability after regeneration with ethanol. All information gives an indication that the as-prepared MIL-68 (In) nanorods show their potential as the adsorbent for highly efficient removal of CR in wastewater. Copyright © 2015 Elsevier Inc. All rights reserved.

Construction of porous CuCo2S4 nanorod arrays via anion exchange for high-performance asymmetric supercapacitor.

PubMed

Cheng, Siyi; Shi, Tielin; Chen, Chen; Zhong, Yan; Huang, Yuanyuan; Tao, Xiangxu; Li, Junjie; Liao, Guanglan; Tang, Zirong

2017-07-27

To push the energy density limit of supercapacitors, proper pseudocapacitive materials with favorable nanostructures are urgently pursued. Ternary transition metal sulfides are promising electrode materials due to the better conductivity and higher electrochemical activity in comparison to the single element sulfides and transition metal oxides. In this work, we have successfully synthesized porous CuCo 2 S 4 nanorod array (NRAs) on carbon textile through a stepwise hydrothermal method, including the growth of the Cu-Co precursor nanowire arrays and subsequent conversion into CuCo 2 S 4 NRAs via anion exchange reaction. The CuCo 2 S 4 NRAs electrode exhibits a greatly enhanced specific capacitance and an outstanding cycling stability. Moreover, an asymmetric supercapacitor using the CuCo 2 S 4 NRAs as positive electrode and activated carbon as negative electrode delivers a high energy density of 56.96 W h kg -1 . Such superior performance demonstrate that the CuCo 2 S 4 NRAs are promising materials for future energy storage applications.

Hydrothermal synthesis of CdS nanorods anchored on α-Fe2O3 nanotube arrays with enhanced visible-light-driven photocatalytic properties.

PubMed

Lei, Rui; Ni, Hongwei; Chen, Rongsheng; Gu, Huazhi; Zhang, Bowei; Zhan, Weiting

2018-03-15

As an n-type semiconductor with an excellent physicochemical properties, iron oxide (Fe 2 O 3 ) has been extensively used in the fields of environmental pollution control and solar energy conversion. However, the high recombination rate of the photoinduced electron-hole pairs and poor charge mobility for Fe 2 O 3 nanomaterial generally result in low photocatalytic efficiency. Herein, an uniform CdS nanorods grown directly on one-dimensional α-Fe 2 O 3 nanotube arrays (NTAs) are successfully synthesized by a facile hydrothermal method and the constructed heterojunction can be a kind of efficient and recyclable photocatalysts. Successful deposition of CdS nanorods onto the α-Fe 2 O 3 NTAs is verified by field emission scanning electron microscopy(FESEM), X-ray diffraction (XRD) and transmission electron microscopy (TEM) with energy dispersive X-ray spectroscopy (EDS). UV-Vis diffuse reflectance spectroscopy indicates that α-Fe 2 O 3 /CdS NTAs possess the intense visible light absorption and also display a red-shift of the band-edge compared with the pure α-Fe 2 O 3 NTAs. The as-obtained α-Fe 2 O 3 /CdS NTAs display excellent photocatalytic activity for decomposition of methylene blue (MB), methyl orange (MO), and phenol under visible light illumination. Among all the tested photocatalysts, the film synthesized for 3h with good stability exhibits the best photocatalytic properties and produces the highest photocurrent of 1.43 mA/cm 2 at 0.8 V vs. Ag/AgCl electrode, owing to its well formed heterojunction structure, effective electron-hole pair separation and direct electron transfer pathway along the CdS nanorods and α-Fe 2 O 3 NTAs. Besides, the photogenerated holes (h + ) and superoxide radicals (O 2 - ) play dominant roles in the photocatalytic process. On the basis of the photocatalytic results and energy band diagram, the photocatalytic process mechanism is proposed. Considering the easy preparation and excellent performance, α-Fe 2 O 3 /CdS NTAs could

Assembling Ordered Nanorod Superstructures and Their Application as Microcavity Lasers

NASA Astrophysics Data System (ADS)

Liu, Pai; Singh, Shalini; Guo, Yina; Wang, Jian-Jun; Xu, Hongxing; Silien, Christophe; Liu, Ning; Ryan, Kevin M.

2017-03-01

Herein we report the formation of multi-layered arrays of vertically aligned and close packed semiconductor nanorods in perfect registry at a substrate using electric field assisted assembly. The collective properties of these CdSexS1-x nanorod emitters are harnessed by demonstrating a relatively low amplified spontaneous emission (ASE) threshold and a high net optical gain at medium pump intensity. The importance of order in the system is highlighted where a lower ASE threshold is observed compared to disordered samples.

Improvement of the electrochemical properties via poly(3,4-ethylenedioxythiophene) oriented micro/nanorods

NASA Astrophysics Data System (ADS)

Li, Yu; Wang, Bichen; Chen, Huimin; Feng, Wei

Arrays of oriented poly(3,4-ethylenedioxythiophene) (PEDOT) micro/nanorods are synthesized by electrochemical galvanostatic method at the current density of 1 mA cm -2 in the cetyltrimethylammonium bromide (CTAB) aqueous solution whose pH value is 1. The CTAB is used both as the surfactant and the supporting salt in the electrolyte solution. The electrochemical properties of PEDOT films are characterized by cyclic voltammetry and galvanostatic charge/discharge techniques, which indicate that the arrays of oriented PEDOT micro/nanorods can be applied as the electrode materials of supercapacitors. In addition, the cycling performance of PEDOT micro/nanorods is much better than that of traditional PEDOT particles. The effects of the concentration of CTAB, the current density, and pH value of electrolyte solutions on the morphologies and electrochemical properties of PEDOT films are investigated. The mechanism of different morphologies formation is discussed in this study as well.

Role of nanorods insertion layer in ZnO-based electrochemical metallization memory cell

NASA Astrophysics Data System (ADS)

Mangasa Simanjuntak, Firman; Singh, Pragya; Chandrasekaran, Sridhar; Juanda Lumbantoruan, Franky; Yang, Chih-Chieh; Huang, Chu-Jie; Lin, Chun-Chieh; Tseng, Tseung-Yuen

2017-12-01

An engineering nanorod array in a ZnO-based electrochemical metallization device for nonvolatile memory applications was investigated. A hydrothermally synthesized nanorod layer was inserted into a Cu/ZnO/ITO device structure. Another device was fabricated without nanorods for comparison, and this device demonstrated a diode-like behavior with no switching behavior at a low current compliance (CC). The switching became clear only when the CC was increased to 75 mA. The insertion of a nanorods layer induced switching characteristics at a low operation current and improve the endurance and retention performances. The morphology of the nanorods may control the switching characteristics. A forming-free electrochemical metallization memory device having long switching cycles (>104 cycles) with a sufficient memory window (103 times) for data storage application, good switching stability and sufficient retention was successfully fabricated by adjusting the morphology and defect concentration of the inserted nanorod layer. The nanorod layer not only contributed to inducing resistive switching characteristics but also acted as both a switching layer and a cation diffusion control layer.

Using carbon nanotubes-gold nanocomposites to quench energy from pinnate titanium dioxide nanorods array for signal-on photoelectrochemical aptasensing.

PubMed

Deng, Wenping; Shen, Lei; Wang, Xiu; Yang, Chunlei; Yu, Jinghua; Yan, Mei; Song, Xianrang

2016-08-15

On the basis of the absorption and emission spectra overlap, an enhanced resonance energy transfer caused by excition-plasmon resonance between carbon nanotubes-gold nanoparticles (CNTs-Au) and pinnate titanium dioxide nanorods array (P-TiO2 NA) was obtained. Three-dimensional single crystalline P-TiO2 were prepared successfully on fluorine-doped tin oxide conducting glass (FTO glass), and its optical absorption properties and photoelectrochemical (PEC) properties were investigated. With the synergy of CNTs-Au as energy acceptor, it resulted in the enhancement of energy transfer between excited P-TiO2 NA and CNTs-Au. Upon the novel sandwichlike structure formed via DNA hybridization, the exciton produced in P-TiO2 NA was annihilated and a damped photocurrent was obtained. With the use of carcinoembryonic antigen (CEA) as a model which bonded to its specific aptamer and destroyed the sandwichlike structure, the energy transfer efficiency was lowered, leading to PEC response augment. Thus a signal-on PEC aptasensor was constructed. Under the optimal conditions, the PEC aptasensor for CEA determination exhibited a linear range from 0.001 to 2.5ngmL(-1) with a detection limit of 0.39pgmL(-1) and was satisfactory for clinical sample detection. Furthermore, the proposed aptasensor shows satisfying performance, such as easy preparation, rapid detection and so on. Moreover, since different aptamer can specifically bind to different target molecules, the designed strategy has an expansive application for the construction of versatile PEC platforms. Copyright © 2016 Elsevier B.V. All rights reserved.

Effect of annealing temperature on the photoluminescence and scintillation properties of ZnO nanorods

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kurudirek, Sinem V.; Menkara, H.; Klein, Benjamin D. B.

2018-01-01

The effect of the annealing to enhance the photoluminescence (PL) and scintillation properties, as determined by pulse height distribution of alpha particle irradiation, has been investigated for solution grown ZnO nanorods For this investigation the ZnO nanorod arrays were grown on glass for 22 h at 95 ◦ C as a substrate using a solution based hydrothermal technique. The samples were first annealed for different times (30, 60, 90 and 120 min) at 300 ◦ C and then at different temperatures (100 ◦ C–600 ◦ C) in order to determine the optimum annealing time and temperature, respectively. Before annealing, themore » ZnO nanorod arrays showed a broad yellow–orange visible and near-band gap UV emission peaks. After annealing in a forming gas atmosphere, the intensity of the sub-band gap PL was significantly reduced and the near-band gap PL emission intensity correspondingly increased (especially at temperatures higher than 100 ◦ C). Based on the ratio of the peak intensity ratio before and after annealing, it was concluded that samples at 350 ◦ C for 90 min resulted in the best near-band gap PL emission. Similarly, the analysis of the pulse height spectrum resulting from alpha particles revealed that ZnO nanorod arrays similarly annealed at 350 ◦ C for 90 min exhibited the highest scintillation response.« less

Shedding Light on the Formation of Gold Nanorods

NASA Astrophysics Data System (ADS)

Lopez, Orlando; Hudry, Damien; Nykypanchuk, Dmytro

A significant interest in the study and synthesis of one-dimensional materials such as nanorods or nanowires is sparked by their potential application in electronics, photonics and biodetection. However, the synthesis of these low dimensional materials is not always reliable due to kinetic effects in symmetry breaking and high sensitivity to impurities. In this work we discuss the synthesis of gold nanorods and new ways to achieve symmetry breaking during the growth from seed solution, hence maximizing the yield of nanorods. We discuss the mechanism involved in symmetry breaking and general strategies to improve the nanorod morphology and synthetic yield. This work can serve as a starting point to design reproducible synthetic strategies for preparing high quality gold nanorods. This project was supported by the U.S. Department of Energy, Office of Science, under the Science Undergraduate Laboratory Internships Program and used resources of the C.F.N., which is a U.S. DOE Facility, at B.N.L., Contract No. DE-SC0012704.

Selective formation of GaN-based nanorod heterostructures on soda-lime glass substrates by a local heating method.

PubMed

Hong, Young Joon; Kim, Yong-Jin; Jeon, Jong-Myeong; Kim, Miyoung; Choi, Jun Hee; Baik, Chan Wook; Kim, Sun Il; Park, Sung Soo; Kim, Jong Min; Yi, Gyu-Chul

2011-05-20

We report on the fabrication of high-quality GaN on soda-lime glass substrates, heretofore precluded by both the intolerance of soda-lime glass to the high temperatures required for III-nitride growth and the lack of an epitaxial relationship with amorphous glass. The difficulties were circumvented by heteroepitaxial coating of GaN on ZnO nanorods via a local microheating method. Metal-organic chemical vapor deposition of ZnO nanorods and GaN layers using the microheater arrays produced high-quality GaN/ZnO coaxial nanorod heterostructures at only the desired regions on the soda-lime glass substrates. High-resolution transmission electron microscopy examination of the coaxial nanorod heterostructures indicated the formation of an abrupt, semicoherent interface. Photoluminescence and cathodoluminescence spectroscopy was also applied to confirm the high optical quality of the coaxial nanorod heterostructures. Mg-doped GaN/ZnO coaxial nanorod heterostructure arrays, whose GaN shell layers were grown with various different magnesocene flow rates, were further investigated by using photoluminescence spectroscopy for the p-type doping characteristics. The suggested method for fabrication of III-nitrides on glass substrates signifies potentials for low-cost and large-size optoelectronic device applications.

Controllable electrodeposition of ZnO nanorod arrays on flexible stainless steel mesh substrate for photocatalytic degradation of Rhodamine B

NASA Astrophysics Data System (ADS)

Lu, Hui; Zhang, Mei; Guo, Min

2014-10-01

Well-aligned single-crystalline ZnO nanorod arrays (ZNRAs) were prepared on flexible stainless steel mesh (SSM) substrate in large-scale by using a direct electrodeposition method. The effects of electrochemical parameters, such as applied potential, applied nucleation potential time, substrate pretreatment, electrodeposition duration and times, on the orientation, morphology and density of ZNRAs were systematically studied by X-ray diffraction (XRD), scanning electron microscopy (SEM), high-resolution transmission electron microscopy (HRTEM) and the selected area electron diffraction (SAED). The results showed that ZNRAs on SSM substrate with [0 0 1] preferred orientation and well crystallization were obtained by controlling the applied potential in the range of -0.9 to -1.1 V. The density of ZNRAs could be increased obviously by applying a nucleation potential (-1.3 V for more than 10 s before deposition) or by means of substrate pretreatment (the SSM immersed in zinc acetate colloid for more than 10 min before deposition), meanwhile, the deposited ZNRAs also had small average diameter (<46 ± 4 nm), narrow size distribution and good orientation. In addition, it was also found that the average diameter of ZNRAs could be increased from 89 to 201 ± 5 nm by extending the electrodeposition duration from 1800 to 7200 s, and the length of rods was from 0.8 to 2.2 ± 0.1 μm when the times of the electrodeposition from one to six times. Furthermore, the band gap energy (Eg) of as-prepared ZNTAs was not closely related to the electrodeposition times (only changed from 3.30 to 3.32 eV). The ZNRAs prepared with more electrodeposition times showed enhanced photocatalytic performance under the UV-lamp for degradation of Rhodamine B. The degradation efficiency of ZNRAs improved from 89.4% to 98.3% with the deposition times from one to six times.

Constructing MnO{sub 2}/single crystalline ZnO nanorod hybrids with enhanced photocatalytic and antibacterial activity

DOE Office of Scientific and Technical Information (OSTI.GOV)

Yu, Weiwei; Liu, Tiangui, E-mail: tianguiliu@gmail.com; Cao, Shiyi

In order to improve the photocatalytic and antibacterial activity of ZnO nanorods, ZnO nanorods decorated with MnO{sub 2} nanoparticles (MnO{sub 2}/ZnO nanorod hybrids) were prepared by using microwave assisted coprecipitation method under the influence of hydrogen peroxide, and the structure, photocatalytic activity and antibacterial property of the products were studied. Experimental results indicated that MnO{sub 2} nanoparticles are decorated on the surface of single crystalline ZnO nanorods. Moreover, the resultant MnO{sub 2}/ZnO nanorod hybrids have been proven to possess good photocatalytic and antibacterial activity, which their degradated efficiency for Rhodamin B (RhB) is twice as the pure ZnO nanorods. Enhancementmore » for photocatalytic and antibacterial activity is mainly attributed to the low band gap energy and excellent electrochemical properties of MnO{sub 2} nanoparticles. - Graphical abstract: The MnO{sub 2}/single crystalline ZnO nanorods hybrids, which MnO{sub 2} nanoparticles are loaded on the surface of ZnO nanorods, were prepared by the step-by-step precipitation method under the assistance of ammonia and hydrogen peroxide. Display Omitted - Highlights: • MnO{sub 2}/ZnO nanorod hybrids were prepared by the step-by-step assembly method. • Single crystalline ZnO nanorods can be decorated by MnO{sub 2} nanoparticles. • MnO{sub 2}/ZnO nanorod hybrids possess good photocatalytic and antibacterial activity. • MnO{sub 2} can improve the photocatalytic activity of ZnO nanorods under visible light.« less

Synthesis and photoelectrochemical properties of a novel CuO/ZnO nanorod photocathode for solar hydrogen generation

NASA Astrophysics Data System (ADS)

Shaislamov, Ulugbek; Lee, Heon-Ju

2016-10-01

Here, we present a facile synthesis method and photoelectrochemical characterizations of a p-type CuO-nanorod array photoelectrode with ZnO nanorod branches. Vertically-aligned CuO nanorods were synthesized by using direct oxidation of metallic Cu nanorods grown on a Cu substrate by using a facile template-assisted electrodeposition method. The formed CuONR/ZnONB hierarchically-structured photoelectrode exhibited remarkable photoelectrodechemical performance and outstanding stability compared to the CuO NR photoelectrode without ZnO NR branches. Morphological, optical and electrochemical characterizations were carried out in order to examine the effects of ZnO nanorod branches on the stability and the overall electrochemical performance of the electrode.

Metal molybdate nanorods as non-precious electrocatalysts for the oxygen reduction

NASA Astrophysics Data System (ADS)

Wu, Tian; Zhang, Lieyu

2015-12-01

Development of non-precious electrocatalysts with applicable electrocatalytic activity towards the oxygen reduction reaction (ORR) is important to fulfill broad-based and large-scale applications of metal/air batteries and fuel cells. Herein, nickel and cobalt molybdates with uniform nanorod morphology are synthesized using a facile one-pot hydrothermal method. The ORR activity of the prepared metal molybdate nanorods in alkaline media are investigated by using cyclic voltammetry (CV), linear sweep voltammetry (LSV) and chronoamperomety in rotating disk electrode (RDE) techniques. The present study suggests that the prepared metal molybdate nanorods exhibit applicable electrocatalytic activities towards the ORR in alkaline media, promising the applications as non-precious cathode in fuel cells and metal-air batteries.

Preparation of arrays of long carbon nanotubes using catalyst structure

DOEpatents

Zhu, Yuntian T.; Arendt, Paul; Li, Qingwen; Zhang, Xiefie

2016-03-22

A structure for preparing an substantially aligned array of carbon nanotubes include a substrate having a first side and a second side, a buffer layer on the first side of the substrate, a catalyst on the buffer layer, and a plurality of channels through the structure for allowing a gaseous carbon source to enter the substrate at the second side and flow through the structure to the catalyst. After preparing the array, a fiber of carbon nanotubes may be spun from the array. Prior to spinning, the array can be immersed in a polymer solution. After spinning, the polymer can be cured.

Preparation, characterization, and nonlinear optical properties of hybridized graphene @ gold nanorods nanocomposites

NASA Astrophysics Data System (ADS)

Guo, Jia; Ning, Tingyin; Han, Yanshun; Sheng, Yingqiang; Li, Chonghui; Zhao, Xiaofei; Lu, Zhengyi; Man, Baoyuan; Jiao, Yang; Jiang, Shouzhen

2018-03-01

The methods of chemical vapor deposition (CVD) and seed-mediated growth were used to obtain graphene and gold nanorods (GNRs), respectively. We fabricate graphene @ gold nanorods (G@GNRs) nanocomposites by successively using dropping and transferring methods Through SEM, Raman spectra and TEM analysis, the number of graphene layers is 6-7. The diameter of gold nanorods (GNRs) is about 10 nm and the average aspect ratio is 6.5. In addition, we systematically investigate their nonlinear optical responses by using open-aperture Z-scan technique. In contrast with graphene and GNRs, the G@GNRs nanocomposites exhibit excellent nonlinear optical response with a modulation depth of about 51% and a saturable intensity of about 6.23 GW/cm2. The results suggest that the G@GNRs nanocomposites could potentially be used as an optical modulator in pulsed laser generation.

Concerted growth and ordering of cobalt nanorod arrays as revealed by tandem in situ SAXS-XAS studies

DOE PAGES

Cormary, Benoit; Li, Tao; Liakakos, Nikos; ...

2016-06-14

The molecular and ensemble dynamics for the growth of hierarchical supercrystals of cobalt nanorods have been studied by in situ tandem X-ray Absorption Spectroscopy – Small Angle X-ray Scattering (XAS - SAXS). The super-crystals were obtained by reducing a Co(II) precursor under H 2 in the presence of a long chain amine and a long chain carboxylic acid. Complementary time-dependent ex situ TEM studies were also performed. The experimental data provide critical insights into the nanorod growth mechanism, and unequivocal evidence for a concerted growth-organization process. Nanorod formation involves cobalt nucleation, a fast atom by atom anisotropic growth and amore » slower oriented attach-ment process that continues well after cobalt reduction is complete. As a result, smectic-like ordering of the nanorods appears very early in the process, as soon as nanoparticle elongation appears, and nanorod growth takes place inside organized super-lattices, which can be regarded as mesocrystals.« less

Ultrasensitive hydrogen sensor based on Pt-decorated WO₃ nanorods prepared by glancing-angle dc magnetron sputtering.

PubMed

Horprathum, M; Srichaiyaperk, T; Samransuksamer, B; Wisitsoraat, A; Eiamchai, P; Limwichean, S; Chananonnawathorn, C; Aiempanakit, K; Nuntawong, N; Patthanasettakul, V; Oros, C; Porntheeraphat, S; Songsiriritthigul, P; Nakajima, H; Tuantranont, A; Chindaudom, P

2014-12-24

In this work, we report an ultrasensitive hydrogen (H2) sensor based on tungsten trioxide (WO3) nanorods decorated with platinum (Pt) nanoparticles. WO3 nanorods were fabricated by dc magnetron sputtering with a glancing angle deposition (GLAD) technique, and decorations of Pt nanoparticles were performed by normal dc sputtering on WO3 nanorods with varying deposition time from 2.5 to 15 s. Crystal structures, morphologies, and chemical information on Pt-decorated WO3 nanorods were characterized by grazing-incident X-ray diffraction, field-emission scanning electron microscopy, energy-dispersive X-ray spectroscopy, and photoelectron spectroscopy, respectively. The effect of the Pt nanoparticles on the H2-sensing performance of WO3 nanorods was investigated over a low concentration range of 150-3000 ppm of H2 at 150-350 °C working temperatures. The results showed that the H2 response greatly increased with increasing Pt-deposition time up to 10 s but then substantially deteriorated as the deposition time increased further. The optimally decorated Pt-WO3 nanorod sensor exhibited an ultrahigh H2 response from 1530 and 214,000 to 150 and 3000 ppm of H2, respectively, at 200 °C. The outstanding gas-sensing properties may be attributed to the excellent dispersion of fine Pt nanoparticles on WO3 nanorods having a very large effective surface area, leading to highly effective spillover of molecular hydrogen through Pt nanoparticles onto the WO3 nanorod surface.

Hierarchical composites of sulfonated graphene-supported vertically aligned polyaniline nanorods for high-performance supercapacitors

NASA Astrophysics Data System (ADS)

Ma, Biao; Zhou, Xiao; Bao, Hua; Li, Xingwei; Wang, Gengchao

2012-10-01

Hierarchical composites of sulfonated graphene-supported vertically aligned polyaniline nanorods (sGNS/PANI) are successfully synthesized via interfacial polymerization of aniline monomers in the presence of sulfonated graphene nanosheets (sGNS). The FE-SEM images indicate that the morphologies of sGNS/PANI composites can be controlled by adjusting the concentration of aniline monomers. FTIR and Raman spectra reveal that aligned PANI nanorod arrays for sGNS/PANI exhibit higher degree of conjugation compared with pristine PANI nanorods. The hierarchical composite based on the two-electrode cell possesses higher specific capacitance (497 F g-1 at 0.2 A g-1), better rate capability and cycling stability (5.7% capacitance loss after 2000 cycles) than those of pristine PANI nanorods.

[Theragnostic approaches using gold nanorods and near infrared light].

PubMed

Niidome, Takuro; Shiotani, Atsushi; Akiyama, Yasuyuki; Ohga, Akira; Nose, Keisuke; Pissuwan, Dakrong; Niidome, Yasuro

2010-12-01

Gold nanoparticles have unique optical properties such as surface-plasmon and photothermal effects. Such properties have resulted in gold nanoparticles having several clinical applications. Gold nanorods (which are rod-shaped gold nanoparticles) show a surface plasmon band in the near-infrared region. They have therefore been proposed as contrast agents for bioimaging, or as heating devices for photothermal therapy. Polyethylene glycol-modified gold nanorods systemically administrated into mice can be detected with integrating sphere, and the stability of the gold nanorods in blood flow evaluated. After intravenous injection of gold nanorods followed by near-infrared laser irradiation, significant tumor damage triggered by the photothermal effect was observed. To deliver gold nanorods to the target tissue, thermosensitive polymer gel-coated gold nanorods were prepared. After intravenous injection of the gel-modified gold nanorods and irradiation of the tumor, a larger amount of gold was detected in the irradiated tumor than in the non-irradiated tumor. This effect is due to the hydrophobic interaction between the cellular membrane or the extracellular matrix and the gel surfaces induced by the photothermal effect. Furthermore, the photothermal effect enhanced the permeability of the stratum corneum of the skin. As a result of treatment of the skin with ovalbumin and gold nanorods followed by near-infrared light irradiation, a significant amount of protein was detected in the skin. The gold nanorods therefore showed several functions as a photothermal nanodevice for bioimaging, thermal therapy, and a drug delivery system.

Comparison of photovoltaic properties of TiO2 electrodes prepared with nanoparticles and nanorods.

PubMed

Nam, Sang-Hun; Ju, Dong-Woo; Boo, Jin-Hyo

2014-12-01

In this report, single crystalline rutile TiO2 nanoparticles and nanorods were synthesized via the hydrothermal method using titanium tetra-isopropoxide as a precursor then, these were coated on top of a fluorine-doped tin oxide (FTO) substrate by using a doctor blade and direct deposition, respectively. Consequently, TiO2 nanorods-based dye-sensitized solar cells (DSSC) exhibit a J(sc) of 3.37 mA/cm2, a V(oc) of 0.82 V and fill factor of 60.1% with an overall conversion efficiency of 1.66%. This result shows an increase of around 38% for current density and 35% for conversion efficiency. Also, with respect to the impedance data, TiO2 nanorods-based DSSCs had smaller semicircles than did the nanoparticles-based DSSCs. These results demonstrate that the nanorod structure can have fast electron transport and reduced charge recombination.

Design and construction of hierarchical TiO2 nanorod arrays by combining layer-by-layer and hydrothermal crystallization techniques for electrochromic application

NASA Astrophysics Data System (ADS)

Chen, Yongbo; Li, Xiaomin; Bi, Zhijie; He, Xiaoli; Li, Guanjie; Xu, Xiaoke; Gao, Xiangdong

2018-05-01

The hierarchical TiO2 (H-TiO2) nanorod arrays (NRAs) composed of single-crystalline nanorods and nanocrystals were finely designed and successfully constructed for electrochromic (EC) application. By combining layer-by-layer (LBL) method and hydrothermal crystallization technique, the superfine nanocrystals (5-7 nm), which can provide abundant active sites and facilitate ion insertion/extraction during EC reactions, were uniformly and conformally assembled on the surface of single-crystalline TiO2 (SC-TiO2) NRAs. The as-formed H-TiO2 NRAs integrate the advantages of one-dimensional NRAs with fast kinetics and superfine nanocrystals with high ion capacity, showing highly enhanced EC performance. Large optical contrast (40.3%), shorter coloring/bleaching time (22/4 s), high coloration efficiency (11.2 cm2 C-1), and excellent cycling stability can be achieved in H-TiO2 NRAs, superior to the pristine SC-TiO2 NRAs and nanocrystalline TiO2 films. This work provides a feasible and well-designed strategy to explore high-performance materials for EC application.

Enhancement of Perovskite Solar Cells Efficiency using N-Doped TiO2 Nanorod Arrays as Electron Transfer Layer.

PubMed

Zhang, Zhen-Long; Li, Jun-Feng; Wang, Xiao-Li; Qin, Jian-Qiang; Shi, Wen-Jia; Liu, Yue-Feng; Gao, Hui-Ping; Mao, Yan-Li

2017-12-01

In this paper, N-doped TiO 2 (N-TiO 2 ) nanorod arrays were synthesized with hydrothermal method, and perovskite solar cells were fabricated using them as electron transfer layer. The solar cell performance was optimized by changing the N doping contents. The power conversion efficiency of solar cells based on N-TiO 2 with the N doping content of 1% (N/Ti, atomic ratio) has been achieved 11.1%, which was 14.7% higher than that of solar cells based on un-doped TiO 2 . To get an insight into the improvement, some investigations were performed. The structure was examined with X-ray powder diffraction (XRD), and morphology was examined by scanning electron microscopy (SEM). Energy dispersive spectrometer (EDS) and Tauc plot spectra indicated the incorporation of N in TiO 2 nanorods. Absorption spectra showed higher absorption of visible light for N-TiO 2 than un-doped TiO 2 . The N doping reduced the energy band gap from 3.03 to 2.74 eV. The photoluminescence (PL) and time-resolved photoluminescence (TRPL) spectra displayed the faster electron transfer from perovskite layer to N-TiO 2 than to un-doped TiO 2 . Electrochemical impedance spectroscopy (EIS) showed the smaller resistance of device based on N-TiO 2 than that on un-doped TiO 2 .

Single-layer graphene/titanium oxide cubic nanorods array/FTO heterojunction for sensitive ultraviolet light detection

NASA Astrophysics Data System (ADS)

Liang, Feng-Xia; Wang, Jiu-Zhen; Wang, Yi; Lin, Yi; Liang, Lin; Gao, Yang; Luo, Lin-Bao

2017-12-01

In this study, we report on the fabrication of a sensitive ultraviolet photodetector (UVPD) by simply transferring single-layer graphene (SLG) on rutile titanium oxide cubic nanorod (TiO2NRs) array. The cubic TiO2NRs array with strong light trapping effect was grown on fluorine-doped tin oxide (FTO) glass through a hydrothermal approach. The as-assembled UVPD was very sensitive to UV light illumination, but virtually blind to white light illumination. The responsivity and specific detectivity were estimated to be 52.1 A/W and 4.3 × 1012 Jones, respectively. What is more, in order to optimize device performance of UVPD, a wet-chemistry treatment was then employed to reduce the high concentration of defects in TiO2NRs during hydrothermal growth. It was found that the UVPD after treatment showed obvious decrease in sensitivity, but the response speed (rise time: 80 ms, fall time: 160 ms) and specific detectivity were substantially increased. It is also found that the speicific detectivity was imporoved by six-fold to 3.2 × 1013 Jones, which was the best result in comparison with previously reported TiO2 nanostructures or thin film based UVPDs. This totality of this study shows that the present SLG/TiO2NR/FTO UVPD may find potential application in future optoelectronic devices and systems.

Halide perovskite solar cells using monocrystalline TiO2 nanorod arrays as electron transport layers: impact of nanorod morphology

NASA Astrophysics Data System (ADS)

Thakur, Ujwal Kumar; Askar, Abdelrahman M.; Kisslinger, Ryan; Wiltshire, Benjamin D.; Kar, Piyush; Shankar, Karthik

2017-07-01

This is the first report of a 17.6% champion efficiency solar cell architecture comprising monocrystalline TiO2 nanorods (TNRs) coupled with perovskite, and formed using facile solution processing without non-routine surface conditioning. Vertically oriented TNR ensembles are desirable as electron transporting layers (ETLs) in halide perovskite solar cells (HPSCs) because of potential advantages such as vectorial electron percolation pathways to balance the longer hole diffusion lengths in certain halide perovskite semiconductors, ease of incorporating nanophotonic enhancements, and optimization between a high contact surface area for charge transfer (good) versus high interfacial recombination (bad). These advantages arise from the tunable morphology of hydrothermally grown rutile TNRs, which is a strong function of the growth conditions. Fluorescence lifetime imaging microscopy of the HPSCs demonstrated a stronger quenching of the perovskite PL when using TNRs as compared to mesoporous/compact TiO2 thin films. Due to increased interfacial contact area between the ETL and perovskite with easier pore filling, charge separation efficiency is dramatically enhanced. Additionally, solid-state impedance spectroscopy results strongly suggested the suppression of interfacial charge recombination between TNRs and perovskite layer, compared to other ETLs. The optimal ETL morphology in this study was found to consist of an array of TNRs ∼300 nm in length and ∼40 nm in width. This work highlights the potential of TNR ETLs to achieve high performance solution-processed HPSCs.

Miniaturized pH Sensors Based on Zinc Oxide Nanotubes/Nanorods

PubMed Central

Fulati, Alimujiang; Ali, Syed M.Usman; Riaz, Muhammad; Amin, Gul; Nur, Omer; Willander, Magnus

2009-01-01

ZnO nanotubes and nanorods grown on gold thin film were used to create pH sensor devices. The developed ZnO nanotube and nanorod pH sensors display good reproducibility, repeatability and long-term stability and exhibit a pH-dependent electrochemical potential difference versus an Ag/AgCl reference electrode over a large dynamic pH range. We found the ZnO nanotubes provide sensitivity as high as twice that of the ZnO nanorods, which can be ascribed to the fact that small dimensional ZnO nanotubes have a higher level of surface and subsurface oxygen vacancies and provide a larger effective surface area with higher surface-to-volume ratio as compared to ZnO nanorods, thus affording the ZnO nanotube pH sensor a higher sensitivity. Experimental results indicate ZnO nanotubes can be used in pH sensor applications with improved performance. Moreover, the ZnO nanotube arrays may find potential application as a novel material for measurements of intracellular biochemical species within single living cells. PMID:22291545

Hydrogen effects on the electroluminescence of n-ZnO nanorod/p-GaN film heterojunction light-emitting diodes.

PubMed

Fang, Fang; Zhao, Dongxu; Li, Binghui; Zhang, Zhenzhong; Shen, Dezhen

2010-07-07

Through a facile low-temperature solution process, vertically n-type ZnO nanorod arrays were grown on a GaN film to form a n-ZnO nanorod/p-GaN film heterojunction. A study of the electroluminescence (EL) characteristics of the heterojunction in air and in air with 2000 ppm hydrogen revealed the sensitivity of such a device to the surrounding atmosphere. The additional hydrogen shallow donors increased the effective electron concentration in ZnO nanorods and the EL recombination zone changed from the ZnO nanorods to the GaN film, which can be identified visually from the color change.

Subwavelength dielectric nanorod chains for energy transfer in the visible range.

PubMed

Li, Dongdong; Zhang, Jingjing; Yan, Changchun; Xu, Zhengji; Zhang, Dao Hua

2017-10-15

We report a new type of energy transfer device, formed by a dielectric nanorod array embedded in a silver slab. Such dielectric chain structures allow surface plasmon wave guiding with large propagation length and highly suppressed crosstalk between adjacent transmission channels. The simulation results show that our proposed design can be used to enhance the energy transfer along the waveguide-like dielectric nanorod chains via coupled plasmons, where the energy spreading is effectively suppressed, and superior imaging properties in terms of resolution and energy transfer distance can be achieved.

Solution-processed all-oxide bulk heterojunction solar cells based on CuO nanaorod array and TiO2 nanocrystals.

PubMed

Wu, Fan; Qiao, Qiquan; Bahrami, Behzad; Chen, Ke; Pathak, Rajesh; Tong, Yanhua; Li, Xiaoyi; Zhang, Tiansheng; Jian, Ronghua

2018-05-25

We present a method to synthesize CuO nanorod array/TiO 2 nanocrystals bulk heterojunction (BHJ) on fluorine-tin-oxide (FTO) glass, in which single-crystalline p-type semiconductor of the CuO nanorod array is grown on the FTO glass by hydrothermal reaction and the n-type semiconductor of the TiO 2 precursor is filled into the CuO nanorods to form well-organized nano-interpenetrating BHJ after air annealing. The interface charge transfer in CuO nanorod array/TiO 2 heterojunction is studied by Kelvin probe force microscopy (KPFM). KPFM results demonstrate that the CuO nanorod array/TiO 2 heterojunction can realize the transfer of photo-generated electrons from the CuO nanorod array to TiO 2 . In this work, a solar cell with the structure FTO/CuO nanoarray/TiO 2 /Al is successfully fabricated, which exhibits an open-circuit voltage (V oc ) of 0.20 V and short-circuit current density (J sc ) of 0.026 mA cm -2 under AM 1.5 illumination. KPFM studies indicate that the very low performance is caused by an undesirable interface charge transfer. The interfacial surface potential (SP) shows that the electron concentration in the CuO nanorod array changes considerably after illumination due to increased photo-generated electrons, but the change in the electron concentration in TiO 2 is much less than in CuO, which indicates that the injection efficiency of the photo-generated electrons from CuO to TiO 2 is not satisfactory, resulting in an undesirable J sc in the solar cell. The interface photovoltage from the KPFM measurement shows that the low V oc results from the small interfacial SP difference between CuO and TiO 2 because the low injected electron concentration cannot raise the Fermi level significantly in TiO 2 . This conclusion agrees with the measured work function results under illumination. Hence, improvement of the interfacial electron injection is primary for the CuO nanorod array/TiO 2 heterojunction solar cells.

Solution-processed all-oxide bulk heterojunction solar cells based on CuO nanaorod array and TiO2 nanocrystals

NASA Astrophysics Data System (ADS)

Wu, Fan; Qiao, Qiquan; Bahrami, Behzad; Chen, Ke; Pathak, Rajesh; Tong, Yanhua; Li, Xiaoyi; Zhang, Tiansheng; Jian, Ronghua

2018-05-01

We present a method to synthesize CuO nanorod array/TiO2 nanocrystals bulk heterojunction (BHJ) on fluorine-tin-oxide (FTO) glass, in which single-crystalline p-type semiconductor of the CuO nanorod array is grown on the FTO glass by hydrothermal reaction and the n-type semiconductor of the TiO2 precursor is filled into the CuO nanorods to form well-organized nano-interpenetrating BHJ after air annealing. The interface charge transfer in CuO nanorod array/TiO2 heterojunction is studied by Kelvin probe force microscopy (KPFM). KPFM results demonstrate that the CuO nanorod array/TiO2 heterojunction can realize the transfer of photo-generated electrons from the CuO nanorod array to TiO2. In this work, a solar cell with the structure FTO/CuO nanoarray/TiO2/Al is successfully fabricated, which exhibits an open-circuit voltage (V oc) of 0.20 V and short-circuit current density (J sc) of 0.026 mA cm‑2 under AM 1.5 illumination. KPFM studies indicate that the very low performance is caused by an undesirable interface charge transfer. The interfacial surface potential (SP) shows that the electron concentration in the CuO nanorod array changes considerably after illumination due to increased photo-generated electrons, but the change in the electron concentration in TiO2 is much less than in CuO, which indicates that the injection efficiency of the photo-generated electrons from CuO to TiO2 is not satisfactory, resulting in an undesirable J sc in the solar cell. The interface photovoltage from the KPFM measurement shows that the low V oc results from the small interfacial SP difference between CuO and TiO2 because the low injected electron concentration cannot raise the Fermi level significantly in TiO2. This conclusion agrees with the measured work function results under illumination. Hence, improvement of the interfacial electron injection is primary for the CuO nanorod array/TiO2 heterojunction solar cells.

3D highly oriented nanoparticulate and microparticulate array ofmetal oxide materials

DOE Office of Scientific and Technical Information (OSTI.GOV)

Vayssieres, Lionel; Guo, Jinghua; Nordgren, Joseph

2006-09-15

Advanced nano and micro particulate thin films of 3d transition and post-transition metal oxides consisting of nanorods and microrods with parallel and perpendicular orientation with respect to the substrate normal, have been successfully grown onto various substrates by heteronucleation, without template and/or surfactant, from the aqueous condensation of solution of metal salts or metal complexes (aqueous chemical growth). Three-dimensional arrays of iron oxide nanorods and zinc oxide nanorods with parallel and perpendicular orientation are presented as well as the oxygen K-edge polarization dependent x-ray absorption spectroscopy (XAS) study of anisotropic perpendicularly oriented microrod array of ZnO performed at synchrotron radiationmore » source facility.« less

Hierarchical Fe₃O₄@Fe₂O₃ Core-Shell Nanorod Arrays as High-Performance Anodes for Asymmetric Supercapacitors.

PubMed

Tang, Xiao; Jia, Ruyue; Zhai, Teng; Xia, Hui

2015-12-16

Anode materials with relatively low capacitance remain a great challenge for asymmetric supercapacitors (ASCs) to pursue high energy density. Hematite (α-Fe2O3) has attracted intensive attention as anode material for ASCs, because of its suitable reversible redox reactions in a negative potential window (from 0 V to -1 V vs Ag/AgCl), high theoretical capacitance, rich abundance, and nontoxic features. Nevertheless, the Fe2O3 electrode cannot deliver large volumetric capacitance at a high rate, because of its poor electrical conductivity (∼10(-14) S/cm), resulting in low power density and low energy density. In this work, a hierarchical heterostructure comprising Fe3O4@Fe2O3 core-shell nanorod arrays (NRAs) is presented and investigated as the negative electrode for ASCs. Consequently, the Fe3O4@Fe2O3 electrode exhibits superior supercapacitive performance, compared to the bare Fe2O3 and Fe3O4 NRAs electrodes, demonstrating large volumetric capacitance (up to 1206 F/cm(3) with a mass loading of 1.25 mg/cm(2)), as well as good rate capability and cycling stability. The hybrid electrode design is also adopted to prepare Fe3O4@MnO2 core-shell NRAs as the positive electrode for ASCs. Significantly, the as-assembled 2 V ASC device delivered a high energy density of 0.83 mWh/cm(3) at a power density of 15.6 mW/cm(3). This work constitutes the first demonstration of Fe3O4 as the conductive supports for Fe2O3 to address the concerns about its poor electronic and ionic transport.

Confinement and Ordering of Au Nanorods in Polymer Films

NASA Astrophysics Data System (ADS)

Hore, Michael J. A.; Mills, Eric; Liu, Yu; Composto, Russell J.

2009-03-01

Ordered arrays of gold nanorods (Au NRs) possess interesting optical properties that might be utilized in future devices. Au NRs functionalized with a poly(ethylene glycol)-thiol brush are incorporated into homopolymer or block copolymer (BCP) films. NR distribution and orientational correlations are studied as a function of nanorod concentration and spacial confinement via Rutherford backscattering spectrometry (RBS) and transmission electron microscopy, respectively. In particular, differences in the degree of nanorod ordering are presented for PMMA homopolymer films (d ˜ 45 nm) versus PS-b-PMMA BCP films (L/2 ˜ 40 nm), where higher ordering is seen in the case of BCP films. At moderate volume fractions of NRs, φ = 1% to 10%, the degree of ordering is moderate, and increases with increasing φ . However, coexistence between regions of higher ordering and isotropic orientations is observed. In addition to the planar confinement considered above, orientation of Au NRs confined to cylindrical P2VP domains is studied in PS-b-P2VP BCP films.

Structural characterization of hydrothermally synthesized MnO2 nanorods

NASA Astrophysics Data System (ADS)

A'yuni, D. Q.; Alkian, I.; Sya'diyah, F. K.; Kadarisman; Darari, A.; Gunawan, V.; Subagio, A.

2017-11-01

We prepared the hydrothermal method to synthesize MnO2 nanorods with controlled structure. KMnO4 and HCl with the various molar ratio (1:2,1:6,1:8) reacted at 160°C for three hours to form MnO2 nanorods. The study found that changing the molar ratio can control the structure and morphology of MnO2. The result revealed that MnO2 formed in nanorod microstructures with different crystallographic structure and phase composition of each molar ratio. The diffraction peaks observed at 2θ values of 28.9°, 37.8°, 40.9°, 49.7° and 60.5° respectively indexed to (110), (101), (200), (411) and (521) plane reflections of a tetragonal phase of β-MnO2 and α-MnO2. The characterization of the morphology showed that the diameters of nanorod microstructures of MnO2 ranging from 30 to 145 nm with length ranging from 0.5 to 3 μm. These MnO2 nanorods product would be potentially used in energy storage devices.

Ag-nanoparticles-decorated NiO-nanoflakes grafted Ni-nanorod arrays stuck out of porous AAO as effective SERS substrates.

PubMed

Zhou, Qitao; Meng, Guowen; Huang, Qing; Zhu, Chuhong; Tang, Haibin; Qian, Yiwu; Chen, Bin; Chen, Bensong

2014-02-28

NiO-nanoflakes (NiO-NFs) grafted Ni-nanorod (Ni-NR) arrays stuck out of the porous anodic aluminum oxide (AAO) template are achieved by a combinatorial process of AAO-confined electrodeposition of Ni-NRs, selectively etching part of the AAO template to expose the Ni-NRs, wet-etching the exposed Ni-NRs in ammonia to obtain Ni(OH)2-NFs grafted onto the cone-shaped Ni-NRs, and annealing to transform Ni(OH)2-NFs in situ into NiO-NFs. By top-view sputtering, Ag-nanoparticles (Ag-NPs) are decorated on each NiO-NFs grafted Ni-NR (denoted as NiO-NFs@Ni-NR). The resultant Ag-NPs-decorated NiO-NFs@Ni-NR (denoted as Ag-NPs@NiO-NFs@Ni-NR) arrays exhibit not only strong surface-enhanced Raman scattering (SERS) activity but also reproducible SERS-signals over the whole array. It is demonstrated that the strong SERS-activity is mainly ascribed to the high density of sub-10 nm gaps (hot spots) between the neighboring Ag-NPs, the semiconducting NiO-NFs induced chemical enhancement effect, and the lightning rod effect of the cone-shaped Ni-NRs. The three-level hierarchical nanostructure arrays stuck out of the AAO template can be utilized to probe polychlorinated biphenyls (PCBs, a kind of global environmental hazard) with a concentration as low as 5 × 10(-6) M, showing promising potential in SERS-based rapid detection of organic environmental pollutants.

Effect of Sn doping on structural, mechanical, optical and electrical properties of ZnO nanoarrays prepared by sol-gel and hydrothermal process

NASA Astrophysics Data System (ADS)

Agarwal, Manish Baboo; Sharma, Akash; Malaidurai, M.; Thangavel, R.

2018-05-01

Undoped and Sn doped Zinc oxide nanorods were prepared by two step process: initially growth of seed layers by sol-gel spin coating technique and then zinc oxide nanorods by hydrothermal process using the precursors zinc nitrate hexahydrate, hexamine and tin chloride. The effects on the electrical, optical, mechanical and structural properties for various Sn concentrations were studied. The crystalline phase determination from X-ray diffraction (XRD) confirms that Sn doped ZnO nanorods have hexagonal wurtzite structure. The variations of stress and strain with different doping concentration of Sn in ZnO nanorods were studied. The doping effect on electrical properties and optical bandgap is estimated by current voltage characteristics and absorbance spectra respectively. The surface morphology was studied with field emission scanning electron microscope (FESEM), which shows that the formation of hexagonal nanorods arrays with increasing Sn concentration. The calculated value of Young's modulus of elasticity (Y) for all the samples remains same. These results can be used in optoelectronic devices.

Effect of an Electrochemically Oxidized ZnO Seed Layer on ZnO Nanorods Grown by using Electrodeposition

NASA Astrophysics Data System (ADS)

Jeon, Woosung; Leem, Jae-Young

2018-05-01

ZnO nanorods were prepared on a Si substrate with and without a ZnO seed layer formed by electro-oxidation to investigate the effect of the seed layer on their growth. The ZnO nanorods grown on the ZnO seed layer had top surfaces that were flat whereas those grown without it had rough top surfaces, as observed in field-emission scanning electron microscopy images. In the Xray diffraction analysis, all ZnO nanorods showed preferential orientation with the (002) plane. In the case of ZnO nanorods prepared with a ZnO seed layer, the residual stress decreased, and the full width at half maximum of the ZnO (002) plane peak decreased. The photoluminescence spectra show a strong and narrow near-band-edge emission peak and high near-band-edge emission to deep-level emission peak ratio for the ZnO nanorods prepared with the seed layer. With respect to the photoresponse properties, the ZnO nanorods grown with the ZnO seed layer showed higher responsivity and faster rise/decay curves than those grown without it. Thus, the ZnO seed layer formed by electro-oxidation improves the structural, optical, and photoresponse properties of the ZnO nanorods formed on it. This method could serve as a new route for improving the properties of optoelectronic devices.

Effect of intrinsic zinc oxide coating on the properties of Al-doped zinc oxide nanorod arrays

NASA Astrophysics Data System (ADS)

Saidi, S. A.; Mamat, M. H.; Ismail, A. S.; Malek, M. F.; Yusoff, M. M.; Sin, N. D. Md.; Zoolfakar, A. S.; Khusaimi, Z.; Rusop, M.

2018-05-01

The aim of this study was to explore the influence of intrinsic zinc oxide (ZnO) coating fabricated by a simple immersion method. X-ray powder diffraction (XRD) analysis indicated that the Al-doped ZnO nanorod arrays films had a hexagonal wurtzite structure, similar to that of an intrinsic ZnO coating. Structural properties of the samples were characterised using field emission scanning electron microscopy (FESEM; JEOL JSM-7600F) and optical properties using X-ray diffraction (XRD). The XRD results showed that all films were crystallized under hexagonal wurtzite structure and presented a preferential orientation along the c-axis (002) was obtained. The XRD results showed that the intrinsic ZnO coating material had a strong orientation, whereas the ZnO was randomly oriented. Overall these results indicate that intrinsic ZnO coating are pontetial for the creation of functional materials such as barrier protection, optoelectronic devices, humidity sensor and ultraviolet photoconductive sensor.

Nonenzymetic glucose sensing using carbon functionalized carbon doped ZnO nanorod arrays

NASA Astrophysics Data System (ADS)

Chakraborty, Pinak; Majumder, Tanmoy; Dhar, Saurab; Mondal, Suvra Prakash

2018-04-01

Fabrication of highly sensitive, long stability and low cost glucose sensors are attractive for biomedical applications and food industries. Most of the commercial glucose sensors are based on enzymatic detection which suffers from problems underlying in enzyme activities. Development of high sensitive, enzyme free sensors is a great challenge for next generation glucose sensing applications. In our study Zinc oxide nanorod sensing electrodes have been grown using low cost hydrothermal route and their nonenzymatic glucose sensing properties have been demonstrated with carbon functionalized, carbon doped ZnO nanorods (C-ZnO NRs) in neutral medium (0.1M PBS, pH 7.4) using cyclic voltammetry and amperometry measurements. The C-ZnO NRs electrodes demonstrated glucose sensitivity˜ 13.66 µAmM-1cm-2 in the concentration range 0.7 - 14 mM.

Size tunable gold nanorods evenly distributed in the channels of mesoporous silica.

PubMed

Li, Zhi; Kübel, Christian; Pârvulescu, Vasile I; Richards, Ryan

2008-06-01

Uniformly distributed gold nanorods in mesoporous silica were synthesized in situ by performing a seed-mediated growth process in the channels of SBA-15 which functions as a hard-template to confine the diameter of gold nanorods. By changing the amount of gold precursor, gold nanorods were prepared with a fixed diameter (6-7 nm) and tunable aspect ratios from 3 to 30. Transmission electron microscope and electron tomography were utilized to visualize the gold nanorods supported on one piece of SBA-15 segment and showed a fairly uniform 3-dimensional distribution of gold nanorods within the SBA-15 channels. The longitudinal plasmon resonances of the gold nanorods/SBA-15 composites analyzed by diffuse reflectance UV-vis spectra were found to be tunable depending on the length of gold nanorods. No significant decrease in surface area and/or pore size of the composite was found after growth, indicating the growth process did not disrupt the open mesoporous structure of SBA-15. The combination of the tunable size of the nanorods and their 3-dimensional distribution within the open supporting matrix makes the gold nanorods/SBA-15 composites interesting candidates to systematically study the influence of the aspect ratio of gold nanorods on their properties and potential applications, i.e., catalyst, optical polarizer, and ultrasensitive medical imaging technique.

Spectroscopic characterization of zinc oxide nanorods synthesized by solid-state reaction

NASA Astrophysics Data System (ADS)

Prasad, Virendra; D'Souza, Charlene; Yadav, Deepti; Shaikh, A. J.; Vigneshwaran, Nadanathangam

2006-09-01

Well-crystallized zinc oxide nanorods have been fabricated by single step solid-state reaction using zinc acetate and sodium hydroxide, at room temperature. The sodium lauryl sulfate (SLS) stabilized zinc oxide nanorods were characterized by using X-ray diffraction, Fourier transform infrared spectroscopy, transmission electron microscopy and photoluminescence spectroscopy. The X-ray diffraction revealed the wurtzite structure of zinc oxide. The size estimation by XRD and TEM confirmed that the ZnO nanorods are made of single crystals. The growth of zinc oxide crystals into rod shape was found to be closely related to its hexagonal nature. The mass ratio of SLS:ZnO in the nanorods was found to be 1:10 based on the thermogravimetric analysis. Blue shift of photoluminescence emission was noticed in the ZnO nanorods when compared to that of ZnO bulk. FT-IR analysis confirmed the binding of SLS with ZnO nanorods. Apart from ease of preparation, this method has the advantage of eco-friendliness since the solvent and other harmful chemicals were eliminated in the synthesis protocol.

ZnO nanorods/AZO photoanode for perovskite solar cells fabricated in ambient air

NASA Astrophysics Data System (ADS)

La Ferrara, Vera; De Maria, Antonella; Rametta, Gabriella; Della Noce, Marco; Vittoria Mercaldo, Lucia; Borriello, Carmela; Bruno, Annalisa; Delli Veneri, Paola

2017-08-01

ZnO nanorods are a good candidate for replacing standard photoanodes, such as TiO2, in perovskite solar cells and in principle superseding the high performances already obtained. This is possible because ZnO nanorods have a fast electron transport rate due to their large surface area. An array of ZnO nanorods is grown by chemical bath deposition starting from Al-doped ZnO (AZO) used both as a seed layer and as an efficient transparent anode in the visible spectral range. In particular, in this work we fabricate methylammonium lead iodide (CH3NH3PbI3) perovskite solar cells using glass/AZO/ZnO nanorods/perovskite/Spiro-OMeTAD/Au as the architecture. The growth of ZnO nanorods has been optimized by varying the precursor concentrations, growth time and solution temperature. All the fabrication process and photovoltaic characterizations have been carried out in ambient air and the devices have not been encapsulated. Power conversion efficiency as high as 7.0% has been obtained with a good stability over 20 d. This is the highest reported value to the best of our knowledge and it is a promising result for the development of perovskite solar cells based on ZnO nanorods and AZO.

Highly antireflective AlGaN/GaN ultraviolet photodetectors using ZnO nanorod arrays on inverted pyramidal surfaces

NASA Astrophysics Data System (ADS)

So, Hongyun; Lim, Jongwoo; Suria, Ateeq J.; Senesky, Debbie G.

2017-07-01

Highly antireflective heterostructured aluminum gallium nitride (AlGaN)/GaN ultraviolet (UV) photodetectors were demonstrated using a combination of inverted pyramidal surfaces and zinc oxide nanorod arrays (i.e., antireflective surface modification) to enhance the optical sensitivity. The microfabricated hierarchical surfaces significantly reduced the average surface reflectance to less than 0.3% in the UV region and less than 1% in the visible light region, allowing near-perfect absorption of incident light regardless of the angle of incidence (5-80°). As a result, the photodetectors fabricated on highly antireflective AlGaN/GaN surfaces showed higher sensitivity and responsivity over a broad range of incidence angles compared to photodetectors on planar AlGaN/GaN surfaces, supporting the use of a hierarchically modified sensing surface for omnidirectional UV monitoring with higher sensitivity.

Zinc oxide nanorod clusters deposited seaweed cellulose sheet for antimicrobial activity.

PubMed

Bhutiya, Priyank L; Mahajan, Mayur S; Abdul Rasheed, M; Pandey, Manoj; Zaheer Hasan, S; Misra, Nirendra

2018-06-01

Seaweed cellulose was isolated from green seaweed Ulva fasciata using a common bleaching agent. Sheet containing porous mesh was prepared from the extracted seaweed crystalline cellulose along with zinc oxide (ZnO) nanorod clusters grown over the sheet by single step hydrothermal method. Seaweed cellulose and zinc oxide nanorod clusters deposited seaweed cellulose sheet was characterized by FT-IR, XRD, TGA, and SEM-EDX. Morphology showed that the diameter of zinc oxide nanorods were around 70nm. Zinc oxide nanorod clusters deposited on seaweed cellulose sheet gave remarkable antibacterial activity towards gram-positive (Staphylococcus aureus, Bacillus ceresus, Streptococcus thermophilis) and gram-negative (Escherichia coli, Pseudomonas aeruginous) microbes. Such deposited sheet has potential applications in pharmaceutical, biomedical, food packaging, water treatment and biotechnological industries. Copyright © 2018 Elsevier B.V. All rights reserved.

High performance devices enabled by epitaxial, preferentially oriented, nanodots and/or nanorods

DOEpatents

Goyal, Amit [Knoxville, TN

2011-10-11

Novel articles and methods to fabricate same with self-assembled nanodots and/or nanorods of a single or multicomponent material within another single or multicomponent material for use in electrical, electronic, magnetic, electromagnetic, superconducting and electrooptical devices is disclosed. Self-assembled nanodots and/or nanorods are ordered arrays wherein ordering occurs due to strain minimization during growth of the materials. A simple method to accomplish this when depositing in-situ films is also disclosed. Device applications of resulting materials are in areas of superconductivity, photovoltaics, ferroelectrics, magnetoresistance, high density storage, solid state lighting, non-volatile memory, photoluminescence, thermoelectrics and in quantum dot lasers.

Nanoscale characterization of GaN/InGaN multiple quantum wells on GaN nanorods by photoluminescence spectroscopy

NASA Astrophysics Data System (ADS)

Chen, Weijian; Wen, Xiaoming; Latzel, Michael; Yang, Jianfeng; Huang, Shujuan; Shrestha, Santosh; Patterson, Robert; Christiansen, Silke; Conibeer, Gavin

2017-02-01

GaN/InGaN multiple quantum wells (MQW) and GaN nanorods have been widely studied as a candidate material for high-performance light emitting diodes. In this study, GaN/InGaN MQW on top of GaN nanorods are characterized in nanoscale using confocal microscopy associated with photoluminescence spectroscopy, including steady-state PL, timeresolved PL and fluorescence lifetime imaging (FLIM). Nanorods are fabricated by etching planar GaN/InGaN MQWs on top of a GaN layer on a c-plane sapphire substrate. Photoluminescence efficiency from the GaN/InGaN nanorods is evidently higher than that of the planar structure, indicating the emission improvement. Time-resolved photoluminescence (TRPL) prove that surface defects on GaN nanorod sidewalls have a strong influence on the luminescence property of the GaN/InGaN MWQs. Such surface defects can be eliminated by proper surface passivation. Moreover, densely packed nanorod array and sparsely standing nanorods have been studied for better understanding the individual property and collective effects from adjacent nanorods. The combination of the optical characterization techniques guides optoelectronic materials and device fabrication.

Growth of High-Density Zinc Oxide Nanorods on Porous Silicon by Thermal Evaporation

PubMed Central

Rusli, Nurul Izni; Tanikawa, Masahiro; Mahmood, Mohamad Rusop; Yasui, Kanji; Hashim, Abdul Manaf

2012-01-01

The formation of high-density zinc oxide (ZnO) nanorods on porous silicon (PS) substrates at growth temperatures of 600–1000 °C by a simple thermal evaporation of zinc (Zn) powder in the presence of oxygen (O2) gas was systematically investigated. The high-density growth of ZnO nanorods with (0002) orientation over a large area was attributed to the rough surface of PS, which provides appropriate planes to promote deposition of Zn or ZnOx seeds as nucleation sites for the subsequent growth of ZnO nanorods. The geometrical morphologies of ZnO nanorods are determined by the ZnOx seed structures, i.e., cluster or layer structures. The flower-like hexagonal-faceted ZnO nanorods grown at 600 °C seem to be generated from the sparsely distributed ZnOx nanoclusters. Vertically aligned hexagonal-faceted ZnO nanorods grown at 800 °C may be inferred from the formation of dense arrays of ZnOx clusters. The formation of disordered ZnO nanorods formed at 1000 °C may due to the formation of a ZnOx seed layer. The growth mechanism involved has been described by a combination of self-catalyzed vapor-liquid-solid (VLS) and vapor-solid (VS) mechanism. The results suggest that for a more precise study on the growth of ZnO nanostructures involving the introduction of seeds, the initial seed structures must be taken into account given their significant effects.

Freestanding polyaniline nanorods grown on graphene for highly capacitive energy storage

NASA Astrophysics Data System (ADS)

Li, Zijiong; Qin, Zhen; Yang, Baocheng; Guo, Jian; Wang, Haiyan; Zhang, Weiyang; Lv, Xiaowei; Stack, Alison

2015-02-01

Freestanding polyaniline (PANI) nanorods grown in situ on microwave-expanded graphene oxide (MEGO) sheets were prepared through a facile solution method. The morphological characterization indicates that large quantity of free-standing PANI nanorods with average diameter of 50 nm were uniformly deposited onto the double sides of the MEGO nanosheets to form a sandwich structure. The hybrid of PANI/MEGO (GPANI) exhibit high specific surface area and high electrical conductivity, compared with pristine PANI nanorods. When evaluated as electrodes for supercapacitors, the GPANI demonstrate high specific capacitance of 628 F g-1 at a current density of 1.1 A g-1, high-rate performance, and excellent cycle stability compared to individual component. Such excellent electrochemical performance should be attributed to the combined double-layer capacitance and pseudo -capacitance mechanisms from the MEGO sheets and PANI nanorods.

Hydrothermal Growth of Vertically Aligned ZnO Nanorods Using a Biocomposite Seed Layer of ZnO Nanoparticles.

PubMed

Ibupoto, Zafar Hussain; Khun, Kimleang; Eriksson, Martin; AlSalhi, Mohammad; Atif, Muhammad; Ansari, Anees; Willander, Magnus

2013-08-19

Well aligned ZnO nanorods have been prepared by a low temperature aqueous chemical growth method, using a biocomposite seed layer of ZnO nanoparticles prepared in starch and cellulose bio polymers. The effect of different concentrations of biocomposite seed layer on the alignment of ZnO nanorods has been investigated. ZnO nanorods grown on a gold-coated glass substrate have been characterized by X-ray diffraction (XRD) and field emission scanning electron microscopy (FESEM) techniques. These techniques have shown that the ZnO nanorods are well aligned and perpendicular to the substrate, and grown with a high density and uniformity on the substrate. Moreover, ZnO nanorods can be grown with an orientation along the c -axis of the substrate and exhibit a wurtzite crystal structure with a dominant (002) peak in an XRD spectrum and possessed a high crystal quality. A photoluminescence (PL) spectroscopy study of the ZnO nanorods has revealed a conventional near band edge ultraviolet emission, along with emission in the visible part of the electromagnetic spectrum due to defect emission. This study provides an alternative method for the fabrication of well aligned ZnO nanorods. This method can be helpful in improving the performance of devices where alignment plays a significant role.

Hydrothermal Growth of Vertically Aligned ZnO Nanorods Using a Biocomposite Seed Layer of ZnO Nanoparticles

PubMed Central

Ibupoto, Zafar Hussain; Khun, Kimleang; Eriksson, Martin; AlSalhi, Mohammad; Atif, Muhammad; Ansari, Anees; Willander, Magnus

2013-01-01

Well aligned ZnO nanorods have been prepared by a low temperature aqueous chemical growth method, using a biocomposite seed layer of ZnO nanoparticles prepared in starch and cellulose bio polymers. The effect of different concentrations of biocomposite seed layer on the alignment of ZnO nanorods has been investigated. ZnO nanorods grown on a gold-coated glass substrate have been characterized by X-ray diffraction (XRD) and field emission scanning electron microscopy (FESEM) techniques. These techniques have shown that the ZnO nanorods are well aligned and perpendicular to the substrate, and grown with a high density and uniformity on the substrate. Moreover, ZnO nanorods can be grown with an orientation along the c-axis of the substrate and exhibit a wurtzite crystal structure with a dominant (002) peak in an XRD spectrum and possessed a high crystal quality. A photoluminescence (PL) spectroscopy study of the ZnO nanorods has revealed a conventional near band edge ultraviolet emission, along with emission in the visible part of the electromagnetic spectrum due to defect emission. This study provides an alternative method for the fabrication of well aligned ZnO nanorods. This method can be helpful in improving the performance of devices where alignment plays a significant role. PMID:28811454

Controllable synthesis of ZnxCd1-xS@ZnO core-shell nanorods with enhanced photocatalytic activity.

PubMed

Xie, Shilei; Lu, Xihong; Zhai, Teng; Gan, Jiayong; Li, Wei; Xu, Ming; Yu, Minghao; Zhang, Yuan-Ming; Tong, Yexiang

2012-07-17

We report the synthesis of Zn(x)Cd(1-x)S@ZnO nanorod arrays via a facile two-step process and the implementation of these core-shell nanorods as an environmental friendly and recyclable photocatalyst for methyl orange degradation. The band gap of Zn(x)Cd(1-x)S@ZnO core-shell nanorods can be readily tunable by adjusting the ratio of Zn/Cd during the synthesis. These Zn(x)Cd(1-x)S@ZnO core-shell nanorods exhibit a high photocatalytic activity and good stability in the degradation of the methyl orange. Moreover, these films grown on FTO substrates make the collection and recycle of the photocatalyst easier. These findings may open new opportunities for the design of effective, stable, and easy-recyclable photocatalytic materials.

Hierarchical Branched Vanadium Oxide Nanorod@Si Nanowire Architecture for High Performance Supercapacitors.

PubMed

Li, Zhaodong; Wang, Fei; Wang, Xudong

2017-01-01

Vanadium oxide (VO x ) nanorods are uniformly synthesized on dense Si nanowire arrays. This 3D hierarchical nanoarchitecture offers a novel high-performance supercapacitor electrode design with significantly improved specific capacitance and high-rate capability. © 2016 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

AuNPs Hybrid Black ZnO Nanorods Made by a Sol-Gel Method for Highly Sensitive Humidity Sensing.

PubMed

Zhang, Hongyan; Zhang, Min; Lin, Cunchong; Zhang, Jun

2018-01-13

A highly sensitive self-powered humidity sensor has been realized from AuNPs hybrid black zinc oxide (ZnO) nanorods prepared through a sol-gel method. XRD pattern reveals that both ZnO and ZnO/AuNPs exhibit a wurtzite structure. ZnO/AuNPs nanorods grow in a vertical alignment, which possesses high uniformity and forms dense arrays with a smaller diameter than that of ZnO nanoparticles. All ZnO/AuNPs and pure black ZnO show lower band gap energy than the typically reported 3.34 eV of pure ZnO. Furthermore, the band gap of ZnO/AuNPs nanocomposites is effectively influenced by the amount of AuNPs. The humidity sensing tests clearly prove that all the ZnO/AuNPs humidity sensors exhibit much higher response than that of ZnO sensors, and the sensitivity of such ZnO/AuNPs nanorods (6 mL AuNPs) display a change three orders higher than that of pure ZnO with relative humidity (RH) ranging from 11% to 95% at room temperature. The response and recovery time of the ZnO/AuNPs are 5.6 s and 32.4 s, respectively. This study of the construction of semiconductor/noble metal sensors provides a rational way to control the morphology of semiconductor nanomaterials and to design a humidity sensor with high performance.

Enhanced Structural and Luminescent Properties of Carbon-Assisted ZnO Nanorod Arrays on (100) Si Substrate

NASA Astrophysics Data System (ADS)

Yoon, Im Taek; Cho, Hak Dong; Lee, Sejoon; Roshchupkin, Dmitry V.

2018-02-01

We have fabricated as-grown ZnO nanorods (NRs) and carbon-assisted NR arrays on semi-insulating (100)-oriented Si substrates. We compared the structural and luminescent properties of them. High-resolution transmission microscopy, field emission scanning electron microscopy, x-ray diffraction and energy-dispersive x-ray revealed that the as-grown ZnO NRs and carbon-assisted ZnO NRs were single crystals with a hexagonal wurtzite structure, and grew with a c-axis orientation perpendicular to the Si substrate. These measurements show that the carbon-assisted ZnO NRs were better synthesized vertically on an Si substrate compared to the as-grown ZnO NRs. Photoluminescence measurements showed that luminescence intensity of the carbon-assisted ZnO NRs was enhanced compared to the as-grown ZnO NRs. The enhanced luminescence intensity of the carbon-assisted ZnO demonstrates the possible improvement in the performance of photovoltaic nanodevices based on ZnO-like materials. This method can be applied to the fabrication of well-aligned ZnO NRs used widely in optoelectronic devices.

The photoluminescence, drug delivery and imaging properties of multifunctional Eu3+/Gd3+ dual-doped hydroxyapatite nanorods.

PubMed

Chen, Feng; Huang, Peng; Zhu, Ying-Jie; Wu, Jin; Zhang, Chun-Lei; Cui, Da-Xiang

2011-12-01

The design and synthesis of multifunctional systems with high biocompatibility are very significant for the future of clinical applications. Herein, we report a microwave-assisted rapid synthesis of multifunctional Eu(3+)/Gd(3+) dual-doped hydroxyapatite (HAp) nanorods, and the photoluminescence (PL), drug delivery and in vivo imaging of as-prepared Eu(3+)/Gd(3+) doped HAp nanorods. The photoluminescent and magnetic multifunctions of HAp nanorods are realized by the dual-doping with Eu(3+) and Gd(3+). The PL intensity of doped HAp nanorods can be adjusted by varying Eu(3+) and Gd(3+) concentrations. The magnetization of doped HAp nanorods increases with the concentration of doped Gd(3+). The as-prepared Eu(3+)/Gd(3+)-doped HAp nanorods exhibit inappreciable toxicity to the cells in vitro. More importantly, the Eu(3+)/Gd(3+)-doped HAp nanorods show a high drug adsorption capacity and sustained drug release using ibuprofen as a model drug, and the drug release is governed by a diffusion process. Furthermore, the noninvasive visualization of nude mice with subcutaneous injection indicates that the Eu(3+)/Gd(3+)-doped HAp nanorods with the photoluminescent function are suitable for in vivo imaging. In vitro and in vivo imaging tests indicate that Eu(3+)/Gd(3+)-doped HAp nanorods have a potential in applications such as a multiple-model imaging agent for magnetic resonance (MR) imaging, photoluminescence imaging and computed tomography (CT) imaging. The Eu(3+)/Gd(3+) dual-doped HAp nanorods are promising for applications in the biomedical fields such as multifunctional drug delivery systems with imaging guidance. Copyright © 2011 Elsevier Ltd. All rights reserved.

Magnetic-plasmonic multilayered nanorods

NASA Astrophysics Data System (ADS)

Thumthan, Orathai

Multilayered nanorods which consist of alternating magnetic layers separated by Au layers combine two distinctive properties, magnetic properties and surface plasmonic resonance (SPR) properties into one nano-entity. Their magnetic properties are tunable by changing the layer thickness, varying from single domain to superparamagnetic state. Superparamagnetic is a key requirement for magnetic nanoparticles for bioapplications. Superparamagnetic nanoparticles exhibit high magnetic moments at low applied magnetic field while retain no magnetic moments when magnetic field is removed preventing them from aggregation due to magnetic attraction. Au layers in the nanorods provide anchorage sites for functional group attachment. Also, Au nanodisks exhibit SPR properties. The SPR peak can be tuned from 540 nm to 820 nm by controlling the thickness of magnetic segments while keeping Au thickness constant. In this research, there are three types of multilayered nanorod have been fabricated: Au/NiFe nanorods, Au/Fe nanorods, and Au/Co nanorods. These magnetic nanorods were fabricated by templated electrodeposition into the channels in Anodic Aluminum Oxide (AAO) membrane. The setup for AAO fabrication was developed as a part of this research. Our fabricated AAO membrane has channels with a diameter ranging from 40nm to 80 nm and a thickness of 10um to 12um. Magnetic properties of nanorods such as saturation field, saturation moment, coercivity and remanence are able to manipulate through their shape anisotropy. The magnetization will be easier in long axis rather than short axis of particle. In addition, Au nanodisks in the nanorod structure are not only serving as anchorage sites for functional groups but also provide SPR properties. Under irradiation of light Au nanodisks strongly absorb light at SPR frequency which ranging from 540 nm to 820 nm by controlling the thickness of magnetic segments while keeping Au thickness constant. The SPR tunability of nanorods in near

High Stability Induced by the TiN/Ti Interlayer in Three-Dimensional Si/Ge Nanorod Arrays as Anode in Micro Lithium Ion Battery.

PubMed

Yue, Chuang; Yu, Yingjian; Wu, Zhenguo; Sun, Shibo; He, Xu; Li, Juntao; Zhao, Libo; Wu, Suntao; Li, Jing; Kang, Junyong; Lin, Liwei

2016-03-01

Three-dimensional (3D) Si/Ge-based micro/nano batteries are promising lab-on-chip power supply sources because of the good process compatibility with integrated circuits and Micro/Nano-Electro-Mechanical System technologies. In this work, the effective interlayer of TiN/Ti thin films were introduced to coat around the 3D Si nanorod (NR) arrays before the amorphous Ge layer deposition as anode in micro/nano lithium ion batteries, thus the superior cycling stability was realized by reason for the restriction of Si activation in this unique 3D matchlike Si/TiN/Ti/Ge NR array electrode. Moreover, the volume expansion properties after the repeated lithium-ion insertion/extraction were experimentally investigated to evidence the superior stability of this unique multilayered Si composite electrode. The demonstration of this wafer-scale, cost-effective, and Si-compatible fabrication for anodes in Li-ion micro/nano batteries provides new routes to configurate more efficient 3D energy storage systems for micro/nano smart semiconductor devices.

Effect of the polymeric coating thickness on the photocurrent performance of titanium dioxide nanorod arrays-polyaniline composite-based UV photosensor

NASA Astrophysics Data System (ADS)

Yusoff, M. M.; Mamat, M. H.; Malek, M. F.; Othman, , N.; Ismail, A. S.; Saidi, S. A.; Mohamed, R.; Suriani, A. B.; Khusaimi, Z.; Rusop, M.

2018-05-01

Titanium dioxide (TiO2) nanorod arrays (TNAs) were synthesized and deposited on fluorine tin oxide (FTO)-coated glass substrate using a one-step immersion method in a glass container. The effect of the polymeric coating thickness of p-type polyaniline (PANI) on the n-type TNAs was investigated in the p-n heterojunction photodiode (PD) for the application of ultraviolet (UV) photosensor. The fabricated photosensor demonstrated an increased photocurrent under UV irradiation in correlation with the thickness layer of PANI. The measured UV response showed the highest photocurrent of 0.014 µA at 1.0 V of reverse bias with low dark current under the UV radiation (365 nm, 750 µW/cm2). The thickness of the PANI film improved the photocurrent of the fabricated TNAs/PANI composite-based UV photosensor.

Mn-doping-induced photocatalytic activity enhancement of ZnO nanorods prepared on glass substrates

NASA Astrophysics Data System (ADS)

Putri, Nur Ajrina; Fauzia, Vivi; Iwan, S.; Roza, Liszulfah; Umar, Akrajas Ali; Budi, Setia

2018-05-01

Mn-doped ZnO nanorods were synthesized on glass substrates via a two-steps process of ultrasonic spray pyrolysis and hydrothermal methods with four different concentrations Mn-doping (0, 1, 3, and 7 mol%). Introduction of Mn into ZnO is known could enhance the photocatalytic activity owing to the increase in the defect sites that effectively suppress the recombination of free electrons and holes. In this study, results show that Mn-doping has effectively modified the nucleations and crystal growth of ZnO, as evidenced by the increasing in the diameter, height, and the number of nanorods per unit area, besides slightly reduced the band gap and increased the oxygen vacancy concentrations in the ZnO lattice. This condition has successfully multiplied the photocatalytic performance of the ZnO nanorods in the degradation of methylene blue (MB) compared to the undoped-ZnO sample where in the typical process the MB can be degraded approximately 77% within only 35 min under a UV light irradiation.

Gold Nanorod Linking to Control Plasmonic Properties in Solution and Polymer Nanocomposites

PubMed Central

2015-01-01

A novel, solution-based method is presented to prepare bifunctional gold nanorods (B-NRs), assemble B-NRs end-to-end in various solvents, and disperse linked B-NRs in a polymer matrix. The B-NRs have poly(ethylene glycol) grafted along its long axis and cysteine adsorbed to its ends. By controlling cysteine coverage, bifunctional ligands or polymer can be end-grafted to the AuNRs. Here, two dithiol ligands (C6DT and C9DT) are used to link the B-NRs in organic solvents. With increasing incubation time, the nanorod chain length increases linearly as the longitudinal surface plasmon resonance shifts toward lower adsorption wavelengths (i.e., red shift). Analogous to step-growth polymerization, the polydispersity in chain length also increases. Upon adding poly(ethylene glycol) or poly(methyl methacrylate) to chloroform solution with linked B-NR, the nanorod chains are shown to retain end-to-end linking upon spin-casting into PEO or PMMA films. Using quartz crystal microbalance with dissipation (QCM-D), the mechanism of nanorod linking is investigated on planar gold surfaces. At submonolayer coverage of cysteine, C6DT molecules can insert between cysteines and reach an areal density of 3.4 molecules per nm2. To mimic the linking of Au NRs, this planar surface is exposed to cysteine-coated Au nanoparticles, which graft at 7 NPs per μm2. This solution-based method to prepare, assemble, and disperse Au nanorods is applicable to other nanorod systems (e.g., CdSe) and presents a new strategy to assemble anisotropic particles in organic solvents and polymer coatings. PMID:24483622

Gold nanorod linking to control plasmonic properties in solution and polymer nanocomposites.

PubMed

Ferrier, Robert C; Lee, Hyun-Su; Hore, Michael J A; Caporizzo, Matthew; Eckmann, David M; Composto, Russell J

2014-02-25

A novel, solution-based method is presented to prepare bifunctional gold nanorods (B-NRs), assemble B-NRs end-to-end in various solvents, and disperse linked B-NRs in a polymer matrix. The B-NRs have poly(ethylene glycol) grafted along its long axis and cysteine adsorbed to its ends. By controlling cysteine coverage, bifunctional ligands or polymer can be end-grafted to the AuNRs. Here, two dithiol ligands (C6DT and C9DT) are used to link the B-NRs in organic solvents. With increasing incubation time, the nanorod chain length increases linearly as the longitudinal surface plasmon resonance shifts toward lower adsorption wavelengths (i.e., red shift). Analogous to step-growth polymerization, the polydispersity in chain length also increases. Upon adding poly(ethylene glycol) or poly(methyl methacrylate) to chloroform solution with linked B-NR, the nanorod chains are shown to retain end-to-end linking upon spin-casting into PEO or PMMA films. Using quartz crystal microbalance with dissipation (QCM-D), the mechanism of nanorod linking is investigated on planar gold surfaces. At submonolayer coverage of cysteine, C6DT molecules can insert between cysteines and reach an areal density of 3.4 molecules per nm(2). To mimic the linking of Au NRs, this planar surface is exposed to cysteine-coated Au nanoparticles, which graft at 7 NPs per μm(2). This solution-based method to prepare, assemble, and disperse Au nanorods is applicable to other nanorod systems (e.g., CdSe) and presents a new strategy to assemble anisotropic particles in organic solvents and polymer coatings.

High performance superconducting devices enabled by three dimensionally ordered nanodots and/or nanorods

DOEpatents

Goyal, Amit

2013-09-17

Novel articles and methods to fabricate same with self-assembled nanodots and/or nanorods of a single or multicomponent material within another single or multicomponent material for use in electrical, electronic, magnetic, electromagnetic and electrooptical devices is disclosed. Self-assembled nanodots and/or nanorods are ordered arrays wherein ordering occurs due to strain minimization during growth of the materials. A simple method to accomplish this when depositing in-situ films is also disclosed. Device applications of resulting materials are in areas of superconductivity, photovoltaics, ferroelectrics, magnetoresistance, high density storage, solid state lighting, non-volatile memory, photoluminescence, thermoelectrics and in quantum dot lasers.

One-dimensional α-MoO3 nanorods for high energy density pseudocapacitor

NASA Astrophysics Data System (ADS)

Dutta, Shibsankar; Pal, Shreyasi; De, Sukanta

2018-04-01

Ultralong α-MoO3 nanorods having length of 500 nm to 1 µm and uniform width of around ˜50 nm have been synthesized by a simple one step hydrothermal route using a molybdenum organic salt precursor. An evaluation of the electrochemical properties of the nanorods was done by cyclic voltammetry (CV), and galvanometric charging- discharging (GCD) test. Because of the high active sites and rapid ion diffusion and electron transport of the electrodes using as prepared nanorods reveals energy density of 65 Wh/kg at a power density of 940 W/ kg and a maximum specific capacitance of 474 F/g. It also shows excellent cycling stability.

Hydrothermal Synthesis and Photocatalytic Property of β-Ga2O3 Nanorods

NASA Astrophysics Data System (ADS)

Reddy, L. Sivananda; Ko, Yeong Hwan; Yu, Jae Su

2015-09-01

Gallium oxide (Ga2O3) nanorods were facilely prepared by a simple hydrothermal synthesis, and their morphology and photocatalytic property were studied. The gallium oxide hydroxide (GaOOH) nanorods were formed in aqueous growth solution containing gallium nitrate and ammonium hydroxide at 95 °C of growth temperature. Through the calcination treatment at 500 and 1000 °C for 3 h, the GaOOH nanorods were converted into single crystalline α-Ga2O3 and β-Ga2O3 phases. From X-ray diffraction analysis, it could be confirmed that a high crystalline quality of β-Ga2O3 nanorods was achieved by calcinating at 1000 °C. The thermal behavior of the Ga2O3 nanorods was also investigated by differential thermal analysis, and their vibrational bands were identified by Fourier transform infrared spectroscopy. In order to examine the photocatalytic activity of samples, the photodegradation of Rhodamine B solution was observed under UV light irradiation. As a result, the α-Ga2O3 and β-Ga2O3 nanorods exhibited high photodegeneration efficiencies of 62 and 79 %, respectively, for 180 min of UV irradiation time.

Gallium ion-assisted room temperature synthesis of small-diameter ZnO nanorods.

PubMed

Cho, Seungho; Kim, Semi; Lee, Kun-Hong

2011-09-15

We report a method for synthesizing small-diameter ZnO nanorods at room temperature (20 °C), under normal atmospheric pressure (1 atm), and using a relatively short reaction time (1 h) by adding gallium salts to the reaction solution. The ZnO nanorods were, on average, 92 nm in length and 9 nm in diameter and were single crystalline in nature. Quantitative analyses revealed that gallium atoms were not incorporated into the synthesized nanocrystals. On the basis of the experimental results, we propose a mechanism for the formation of small-diameter ZnO nanorods in the presence of gallium ions. The optical properties were probed by UV-Vis diffuse reflectance spectroscopy. The absorption band of the small-diameter ZnO nanorods was blue-shifted relative to the absorption band of the ~230 nm diameter ZnO nanorods (control samples). Control experiments demonstrated that the absence of metal ion-containing precipitants (except ZnO) at room temperature is essential, and that the ZnO nanorod diameter distributions were narrow for the stirred reaction solution and broad when prepared without stirring. Copyright © 2011 Elsevier Inc. All rights reserved.

Hydrothermal Synthesis and Photocatalytic Property of β-Ga2O3 Nanorods.

PubMed

Reddy, L Sivananda; Ko, Yeong Hwan; Yu, Jae Su

2015-12-01

Gallium oxide (Ga2O3) nanorods were facilely prepared by a simple hydrothermal synthesis, and their morphology and photocatalytic property were studied. The gallium oxide hydroxide (GaOOH) nanorods were formed in aqueous growth solution containing gallium nitrate and ammonium hydroxide at 95 °C of growth temperature. Through the calcination treatment at 500 and 1000 °C for 3 h, the GaOOH nanorods were converted into single crystalline α-Ga2O3 and β-Ga2O3 phases. From X-ray diffraction analysis, it could be confirmed that a high crystalline quality of β-Ga2O3 nanorods was achieved by calcinating at 1000 °C. The thermal behavior of the Ga2O3 nanorods was also investigated by differential thermal analysis, and their vibrational bands were identified by Fourier transform infrared spectroscopy. In order to examine the photocatalytic activity of samples, the photodegradation of Rhodamine B solution was observed under UV light irradiation. As a result, the α-Ga2O3 and β-Ga2O3 nanorods exhibited high photodegeneration efficiencies of 62 and 79 %, respectively, for 180 min of UV irradiation time.

Vertically aligned TiO2 nanorods-woven carbon fiber for reinforcement of both mechanical and anti-wear properties in resin composite

NASA Astrophysics Data System (ADS)

Fei, Jie; Zhang, Chao; Luo, Dan; Cui, Yali; Li, Hejun; Lu, Zhaoqing; Huang, Jianfeng

2018-03-01

A series of TiO2 nanorods were successfully grown on woven carbon fiber by hydrothermal method to reinforce the resin composite. The TiO2 nanorods improved the mechanical interlocking among woven carbon fibers and resin matrix, resulting in better fibers/resin interfacial bonding. Compared with desized-woven carbon fiber, the uniform TiO2 nanorods array resulted in an improvement of 84.3% and 73.9% in the tensile and flexural strength of the composite. However, the disorderly TiO2 nanorods on woven carbon fiber leaded to an insignificant promotion of the mechanical strength. The enhanced performance of well-proportioned TiO2 nanorods-woven carbon fiber was also reflected in the nearly 56% decrease of wear rate, comparing to traditional woven carbon fiber reinforced composite.

Integrated titer plate-injector head for microdrop array preparation, storage and transfer

DOEpatents

Swierkowski, Stefan P.

2000-01-01

An integrated titer plate-injector head for preparing and storing two-dimensional (2-D) arrays of microdrops and for ejecting part or all of the microdrops and inserting same precisely into 2-D arrays of deposition sites with micrometer precision. The titer plate-injector head includes integrated precision formed nozzles with appropriate hydrophobic surface features and evaporative constraints. A reusable pressure head with a pressure equalizing feature is added to the titer plate to perform simultaneous precision sample ejection. The titer plate-injector head may be utilized in various applications including capillary electrophoresis, chemical flow injection analysis, microsample array preparation, etc.

Synthesis and characterization of mixed monolayer protected gold nanorods and their Raman activities

DOE Office of Scientific and Technical Information (OSTI.GOV)

Mlambo, Mbuso; Nanotechnology Innovation Centre, Advanced Materials Division, Mintek, Private Bag X3015, Randburg 2125; Mdluli, Phumlani S.

2013-10-15

Graphical abstract: Gold nanorods surface functionalization. - Highlights: • Mixed monolayer protected gold nanorods. • Surface enhanced Raman spectroscopy. • HS-(CH{sub 2}){sub 11}-NHCO-coumarin as a Raman active compound. - Abstract: The cetyltrimethylammonium bromide (CTAB) gold nanorods (AuNRs) were prepared by seed-mediated route followed by the addition of a Raman active compound (HS-(CH{sub 2}){sub 11}-NHCO-coumarin) on the gold nanorods surfaces. Different stoichiometric mixtures of HS-(CH{sub 2}){sub 11}-NHCO-coumarin and HS-PEG-(CH{sub 2}){sub 11}COOH were evaluated for their Raman activities. The lowest stoichiometric ratio HS-(CH{sub 2}){sub 11}-NHCO-coumarin adsorbed on gold nanorods surface was detected and enhanced by Raman spectroscopy. The produced mixed monolayer protectedmore » gold nanorods were characterized by UV-vis spectrometer for optical properties, transmission electron microscope (TEM) for structural properties (shape and aspect ratio) and their zeta potentials (charges) were obtained from ZetaSizer to determine the stability of the produced mixed monolayer protected gold nanorods. The Raman results showed a surface enhanced Raman scattering (SERS) enhancement at the lowest stoichiometric ratio of 1% HS-(CH{sub 2}){sub 11}-NHCO-coumarin compared to high ratio of 50% HS-(CH{sub 2}){sub 11}-NHCO-coumarin on the surface of gold nanorods.« less

Eradication of Multi-drug Resistant Bacteria by Ni Doped ZnO Nanorods: Structural, Raman and optical characteristics

NASA Astrophysics Data System (ADS)

Jan, Tariq; Iqbal, Javed; Ismail, Muhammad; Mansoor, Qaisar; Mahmood, Arshad; Ahmad, Amaar

2014-07-01

In this paper, ZnO nanorods doped with varying amounts of Ni have been prepared by chemical co-precipitation technique. Structural investigations provide the evidence that Ni is successfully doped into ZnO host matrix without having any secondary phases. Scanning electron microscopy (SEM) images reveal the formation of rodlike structure of undoped ZnO with average length and diameter of 1 μm and 80 nm, respectively. Raman spectroscopy results show that the E1LO phonons mode band shifts to the higher values with Ni doping, which is attributed to large amount of crystal defects. Ni doping is also found to greatly influence the optical properties of ZnO nanorods. The influence of Ni doping on antibacterial characteristics of ZnO nanorods have been studied by measuring the growth curves of Escherichia coli (E. coli), Methicillin-resistant Staphylococcus aureus (S. aureus) and Pseudomonas aeruginosa (P. aeruginosa) bacteria in the presence of prepared nanorods. ZnO nanorods antibacterial potency is found to increase remarkably with Ni doping against S. aureus and P. aeruginosa microbials, which might possibly be due to the increase in reactive oxygen species (ROS) generation. Interestingly, it is observed that Ni doped ZnO nanorods completely eradicates these multi-drug resistant bacteria.

Ultrasensitive Characterization of Mechanical Oscillations and Plasmon Energy Shift in Gold Nanorods.

PubMed

Soavi, Giancarlo; Tempra, Iacopo; Pantano, Maria F; Cattoni, Andrea; Collin, Stéphane; Biagioni, Paolo; Pugno, Nicola M; Cerullo, Giulio

2016-02-23

Mechanical vibrational resonances in metal nanoparticles are intensively studied because they provide insight into nanoscale elasticity and for their potential application to ultrasensitive mass detection. In this paper, we use broadband femtosecond pump-probe spectroscopy to study the longitudinal acoustic phonons of arrays of gold nanorods with different aspect ratios, fabricated by electron beam lithography with very high size uniformity. We follow in real time the impulsively excited extensional oscillations of the nanorods by measuring the transient shift of the localized surface plasmon band. Broadband and high-sensitivity detection of the time-dependent extinction spectra enables one to develop a model that quantitatively describes the periodic variation of the plasmon extinction coefficient starting from the steady-state spectrum with only one additional free parameter. This model allows us to retrieve the time-dependent elongation of the nanorods with an ultrahigh sensitivity and to measure oscillation amplitudes of just a few picometers and plasmon energy shifts on the order of 10(-2) meV.

Nested seaweed cellulose fiber deposited with cuprous oxide nanorods for antimicrobial activity.

PubMed

Bhutiya, Priyank L; Misra, Nirendra; Abdul Rasheed, M; Zaheer Hasan, S

2018-05-30

Bird's nest type architectural network of cellulosic nanofibers was extracted, with nearly 34% yield, from green filamentous seaweed Chaetomorpha antennina using mild bleaching agent. Nanorods of cuprous oxide (Cu 2 O) were grown over the porous sheet, prepared from the seaweed cellulose, by one step hydrothermal method. The seaweed cellulose and Cu 2 O nanorods deposited seaweed cellulose sheets, were characterized by XRD, SEM-EDX, FT-IR, TGA and tensile test. XRD revealed that seaweed cellulose acted as reducing agent, reducing CuO to Cu 2 O. Morphology showed that the average diameter of seaweed cellulose and deposited Cu 2 O nanorods were 30 nm and 90 nm, respectively. Cuprous oxide nanorods deposited seaweed cellulose sheet gave very good antibacterial activity towards gram-positive (Staphylococcus aureus, Streptococcus thermophilis) and gram-negative (Pseudomonas aeruginous, Escherichia coli) microbes. The Cu 2 O nanorods deposited seaweed cellulose sheet can be viewed to have great potential in biomedical, packaging, biotechnological, textile, water treatment and pharmaceutical applications. Copyright © 2018 Elsevier B.V. All rights reserved.

Synthesis of CdS nanorods in soft template under gamma-irradiation.

PubMed

Zhao, Bing; Wang, Yanli; Zhang, Haijiao; Jiao, Zheng; Wang, Haobo; Ding, Guoji; Wu, Minghong

2009-02-01

CdS nano material which has a band gap of 2.42 eV at room temperature is a typical II-VII semiconductor having many commercial or potential applications, e.g., light-emitting diodes, solar cell and optoelectronic devices. In this paper, we use a new strategy to synthesize CdS nanorods. CdS nanorods were prepared in soft template under gamma-irradiation though the reaction of cadmium sulphide and thiacetamide (TAA). The formation process and characters of CdS nanorods was investigated in detail by transmission electron microscopy (TEM), electron diffraction (ED) pattern, X-ray powder diffraction (XRD), ultraviolet spectrophotometer (UV) and photoluminescence spectrophotometer (PL). In the experiment we proposed that the irradiation of gamma-ray accelerated the formation of S(2-) under acidic condition (pH = 3) and vinyl acetate (VAc) monomer formed pre-organized nano polymer tubules which were used as both templates and nanoreacters for the growth of CdS nanorods. In this process, we have obtained the CdS polycrystal nanorods with PVAc nano tubules and CdS single-crystal nanorods. The result of X-ray powder diffraction confirms that the crystal type of CdS nanorods is cubic F-43 m (216). The results from transmission electron microscopy and electron diffraction show that the concentrations of reactants and the dose rate of gamma-ray are key to produce appropriate CdS nanorods. Relatively low concentrations (Cd2+: 0.008-0.02 mol/L, Cd2+ : S(2-) = 1 : 2) of reactants and long time (1-2 d) of irradiation in low dose rate (6-14 Gy/min) are propitious to form CdS single-crystal nanorods with small diameter (less than 100 nm) and well length (2-5 microm). UV and PL characterizations show the sample have well optical properties.

Compact hematite buffer layer as a promoter of nanorod photoanode performances

NASA Astrophysics Data System (ADS)

Milan, R.; Cattarin, S.; Comisso, N.; Baratto, C.; Kaunisto, K.; Tkachenko, N. V.; Concina, I.

2016-10-01

The effect of a thin α-Fe2O3 compact buffer layer (BL) on the photoelectrochemical performances of a bare α-Fe2O3 nanorods photoanode is investigated. The BL is prepared through a simple spray deposition onto a fluorine-doped tin oxide (FTO) conducting glass substrate before the growth of a α-Fe2O3 nanorods via a hydrothermal process. Insertion of the hematite BL between the FTO and the nanorods markedly enhances the generated photocurrent, by limiting undesired losses of photogenerated charges at the FTO||electrolyte interface. The proposed approach warrants a marked improvement of material performances, with no additional thermal treatment and no use/dispersion of rare or toxic species, in agreement with the principles of green chemistry.

Chemical synthesis of CdS onto TiO2 nanorods for quantum dot sensitized solar cells

NASA Astrophysics Data System (ADS)

Pawar, Sachin A.; Patil, Dipali S.; Lokhande, Abhishek C.; Gang, Myeng Gil; Shin, Jae Cheol; Patil, Pramod S.; Kim, Jin Hyeok

2016-08-01

A quantum dot sensitized solar cell (QDSSC) is fabricated using hydrothermally grown TiO2 nanorods and successive ionic layer adsorption and reaction (SILAR) deposited CdS. Surface morphology of the TiO2 films coated with different SILAR cycles of CdS is examined by Scanning Electron Microscopy which revealed aggregated CdS QDs coverage grow on increasing onto the TiO2 nanorods with respect to cycle number. Under AM 1.5G illumination, we found the TiO2/CdS QDSSC photoelectrode shows a power conversion efficiency of 1.75%, in an aqueous polysulfide electrolyte with short-circuit photocurrent density of 4.04 mA/cm2 which is higher than that of a bare TiO2 nanorods array.

A self-powered nano-photodetector based on PFH/ZnO nanorods organic/inorganic heterojunction

NASA Astrophysics Data System (ADS)

Li, Xiaoyun; Liu, Wei; Li, Peigang; Song, Jia; An, Yuehua; Shen, Jingqin; Wang, Shunli; Guo, Daoyou

2018-03-01

PFH/ZnO nanorods heterojunctions were fabricated by spin-coating p-type Poly (9,9-dihexylfluorene) (PFH) on n-type vertically aligned ZnO nanorod arrays grown by a facile hydrothermal method on indium tin oxide (ITO) transparent conductive glass. A typical p-n junction behavior was observed in the fabricated heterojunction. The current of heterojunction increases and decreases dramatically by switching the illumination on and off at zero bias, showing potential self-powered photodetector applications. The heterojunction were capable of generating negative current when illuminated under an appropriate wavelength. The photoresponse properties of the heterojunction can be tuned by the applied bias. In vacuum, the rectifying behavior disappeared, and show only simple semiconductor behavior. Band structure of the heterojunction was schematic drawn and explain the mechanism of the properties of PFH/ZnO nanorods heterojunctions.

ZnO nanorod array/CuAlO2 nanofiber heterojunction on Ni substrate: synthesis and photoelectrochemical properties.

PubMed

Ding, Juan; Sui, Yongming; Fu, Wuyou; Yang, Haibin; Zhao, Bo; Li, Minghui

2011-07-22

A novel ZnO nanorod array (NR)/CuAlO(2) nanofiber (NF) heterojunction nanostructure was grown on a substrate of Ni plates using sol-gel synthesis for the NFs and hydrothermal reaction for the NRs. Compared with a traditional ZnO/CuAlO(2) laminar film nanostructure, the photocurrent of this fibrous network heterojunction is significantly increased. A significant blue-shift of the absorption edge and a favorable forward current to reverse current ratio at applied voltages of -2 to +2 V were observed in this heterojunction with the increase of Zn(2+) ion concentration in the hydrothermal reaction. Furthermore, the photoelectrochemical properties were investigated and the highest photocurrent of 3.1 mA cm(-2) was obtained under AM 1.5 illumination with 100 mW cm(-2) light intensity at 0.71 V (versus Ag/AgCl). This novel 3D fibrous network nanostructure plays an important role in the optoelectronic field and can be extended to other binary or ternary oxide compositions for various applications.

ZnO nanorod array/CuAlO2 nanofiber heterojunction on Ni substrate: synthesis and photoelectrochemical properties

NASA Astrophysics Data System (ADS)

Ding, Juan; Sui, Yongming; Fu, Wuyou; Yang, Haibin; Zhao, Bo; Li, Minghui

2011-07-01

A novel ZnO nanorod array (NR)/CuAlO2 nanofiber (NF) heterojunction nanostructure was grown on a substrate of Ni plates using sol-gel synthesis for the NFs and hydrothermal reaction for the NRs. Compared with a traditional ZnO/CuAlO2 laminar film nanostructure, the photocurrent of this fibrous network heterojunction is significantly increased. A significant blue-shift of the absorption edge and a favorable forward current to reverse current ratio at applied voltages of - 2 to + 2 V were observed in this heterojunction with the increase of Zn2 + ion concentration in the hydrothermal reaction. Furthermore, the photoelectrochemical properties were investigated and the highest photocurrent of 3.1 mA cm - 2 was obtained under AM 1.5 illumination with 100 mW cm - 2 light intensity at 0.71 V (versus Ag/AgCl). This novel 3D fibrous network nanostructure plays an important role in the optoelectronic field and can be extended to other binary or ternary oxide compositions for various applications.

Conformal Coating of a Phase Change Material on Ordered Plasmonic Nanorod Arrays for Broadband All-Optical Switching.

PubMed

Guo, Peijun; Weimer, Matthew S; Emery, Jonathan D; Diroll, Benjamin T; Chen, Xinqi; Hock, Adam S; Chang, Robert P H; Martinson, Alex B F; Schaller, Richard D

2017-01-24

Actively tunable optical transmission through artificial metamaterials holds great promise for next-generation nanophotonic devices and metasurfaces. Plasmonic nanostructures and phase change materials have been extensively studied to this end due to their respective strong interactions with light and tunable dielectric constants under external stimuli. Seamlessly integrating plasmonic components with phase change materials, as demonstrated in the present work, can facilitate phase change by plasmonically enabled light confinement and meanwhile make use of the high sensitivity of plasmon resonances to the variation of dielectric constant associated with the phase change. The hybrid platform here is composed of plasmonic indium-tin-oxide nanorod arrays (ITO-NRAs) conformally coated with an ultrathin layer of a prototypical phase change material, vanadium dioxide (VO 2 ), which enables all-optical modulation of the infrared as well as the visible spectral ranges. The interplay between the intrinsic plasmonic nonlinearity of ITO-NRAs and the phase transition induced permittivity change of VO 2 gives rise to spectral and temporal responses that cannot be achieved with individual material components alone.

Synthesis of p-type nickel oxide nanosheets on n-type titanium dioxide nanorod arrays for p-n heterojunction-based UV photosensor

NASA Astrophysics Data System (ADS)

Yusoff, M. M.; Mamat, M. H.; Malek, M. F.; Abdullah, M. A. R.; Ismail, A. S.; Saidi, S. A.; Mohamed, R.; Suriani, A. B.; Khusaimi, Z.; Rusop, M.

2018-05-01

Titanium dioxide (TiO2) nanorod arrays (TNAs) were synthesized and deposited on fluorine tin oxide (FTO)-coated glass substrate using a novel and facile immersion method in a glass container. The synthesis and deposition of p-type nickel oxide (NiO) nanosheets (NS) on the n-type TNAs was investigated in the p-n heterojunction photodiode (PD) for the application of ultraviolet (UV) photosensor. The fabricated TNAs/NiO NS based UV photosensor exhibited a highly increased photocurrent of 4.3 µA under UV radiation (365 nm, 750 µW/cm2) at 1.0 V reverse bias. In this study, the fabricated TNAs/NiO NS p-n heterojunction based photodiode showed potential applications for UV photosensor based on the stable photo-generated current attained under UV radiation.

Surfactant mediated hydrothermal synthesis, characterization and luminescent properties of GdPO{sub 4}: Ce{sup 3+}/Tb{sup 3+} @ GdPO{sub 4} core shell nanorods

DOE Office of Scientific and Technical Information (OSTI.GOV)

Khajuria, Heena; Ladol, Jigmet; Khajuria, Sonika

Highlights: • Core shell nanorods were synthesised by surfactant assisted hydrothermal method. • Morphology of core shell nanorods resembles those of core nanorods indicating coating of shell on cores. • More uniform and non-aggregated core shell nanorods were prepared in presence of surfactants. • Surfactant assisted prepared core shell nanorods show intense emission as compared to uncoated core nanorods. - Abstract: Core shell GdPO{sub 4}: Ce{sup 3+}/Tb{sup 3+} @ GdPO{sub 4} nanorods were synthesized via hydrothermal route in the presence of different surfactants [cetyltrimethyl ammonium bromide (CTAB) and Sodium dodecyl sulphate (SDS)]. The nanorods were characterized by powder X-ray diffractionmore » (PXRD), fourier transform infrared spectroscopy (FTIR), field emission scanning electron microscopy (FE-SEM), transmission electron microscopy (TEM), energy dispersive spectroscopy (EDS) and photoluminescence (PL) studies. The X-ray diffraction results indicate good crystallinity and effective doping in core and core shell nanorods. SEM and TEM micrographs show that all of the as prepared gadolinium phosphate products have rod like shape. The compositional analysis of GdPO{sub 4}: Ce{sup 3+}/Tb{sup 3+} core was done by EDS. The emission intensity of the GdPO{sub 4}: Ce{sup 3+}/Tb{sup 3+} @ GdPO{sub 4} core shell increased significantly with respect to those of GdPO{sub 4}: Ce{sup 3+}/Tb{sup 3+} core nanorods. The effect of surfactant on the uniformity, thickness and luminescence of the core shell nanorods was investigated.« less

AuNPs Hybrid Black ZnO Nanorods Made by a Sol-Gel Method for Highly Sensitive Humidity Sensing

PubMed Central

Zhang, Min; Lin, Cunchong; Zhang, Jun

2018-01-01

A highly sensitive self-powered humidity sensor has been realized from AuNPs hybrid black zinc oxide (ZnO) nanorods prepared through a sol-gel method. XRD pattern reveals that both ZnO and ZnO/AuNPs exhibit a wurtzite structure. ZnO/AuNPs nanorods grow in a vertical alignment, which possesses high uniformity and forms dense arrays with a smaller diameter than that of ZnO nanoparticles. All ZnO/AuNPs and pure black ZnO show lower band gap energy than the typically reported 3.34 eV of pure ZnO. Furthermore, the band gap of ZnO/AuNPs nanocomposites is effectively influenced by the amount of AuNPs. The humidity sensing tests clearly prove that all the ZnO/AuNPs humidity sensors exhibit much higher response than that of ZnO sensors, and the sensitivity of such ZnO/AuNPs nanorods (6 mL AuNPs) display a change three orders higher than that of pure ZnO with relative humidity (RH) ranging from 11% to 95% at room temperature. The response and recovery time of the ZnO/AuNPs are 5.6 s and 32.4 s, respectively. This study of the construction of semiconductor/noble metal sensors provides a rational way to control the morphology of semiconductor nanomaterials and to design a humidity sensor with high performance. PMID:29342860

Efficient PbS/CdS co-sensitized solar cells based on TiO2 nanorod arrays

PubMed Central

2013-01-01

Narrow bandgap PbS nanoparticles, which may expand the light absorption range to the near-infrared region, were deposited on TiO2 nanorod arrays by successive ionic layer adsorption and reaction method to make a photoanode for quantum dot-sensitized solar cells (QDSCs). The thicknesses of PbS nanoparticles were optimized to enhance the photovoltaic performance of PbS QDSCs. A uniform CdS layer was directly coated on previously grown PbS-TiO2 photoanode to protect the PbS from the chemical attack of polysulfide electrolytes. A remarkable short-circuit photocurrent density (approximately 10.4 mA/cm2) for PbS/CdS co-sensitized solar cell was recorded while the photocurrent density of only PbS-sensitized solar cells was lower than 3 mA/cm2. The power conversion efficiency of the PbS/CdS co-sensitized solar cell reached 1.3%, which was beyond the arithmetic addition of the efficiencies of single constituents (PbS and CdS). These results indicate that the synergistic combination of PbS with CdS may provide a stable and effective sensitizer for practical solar cell applications. PMID:23394609

Facet control of gold nanorods

DOE PAGES

Zhang, Qingfeng; Han, Lili; Jing, Hao; ...

2016-01-21

While great success has been achieved in fine-tuning the aspect ratios and thereby the plasmon resonances of cylindrical Au nanorods, facet control with atomic level precision on the highly curved nanorod surfaces has long been a significantly more challenging task. The intrinsic structural complexity and lack of precise facet control of the nanorod surfaces remain the major obstacles for the atomic-level elucidation of the structure–property relationships that underpin the intriguing catalytic performance of Au nanorods. Here we demonstrate that the facets of single-crystalline Au nanorods can be precisely tailored using cuprous ions and cetyltrimethylammonium bromide as a unique pair ofmore » surface capping competitors to guide the particle geometry evolution during nanorod overgrowth. By deliberately maneuvering the competition between cuprous ions and cetyltrimethylammonium bromide, we have been able to create, in a highly controllable and selective manner, an entire family of nanorod-derived anisotropic multifaceted geometries whose surfaces are enclosed by specific types of well-defined high-index and low-index facets. This facet-controlled nanorod overgrowth approach also allows us to fine-tune the particle aspect ratios while well-preserving all the characteristic facets and geometric features of the faceted Au nanorods. Furthermore, taking full advantage of the combined structural and plasmonic tunability, we have further studied the facet-dependent heterogeneous catalysis on well-faceted Au nanorods using surface-enhanced Raman spectroscopy as an ultrasensitive spectroscopic tool with unique time-resolving and molecular finger-printing capabilities.« less

Tunable photovoltaic performance of preferentially oriented rutile TiO₂ nanorod photoanodes based dye sensitized solar cells with quasi-state electrolyte.

PubMed

T C, Sabari Girisun; C, Jeganathan; N, Pavithra; Anandan, Sambandam

2017-12-20

Photoanodes made of highly oriented TiO2 nanorod arrays with different aspect ratios were synthesized via one-step hydrothermal technique. Preferentially oriented single crystalline rutile TiO2 was confirmed by the single peak in XRD pattern (2θ=63o, (0 0 2)). FESEM image evidence the growth of an array of nanorods having different geometry with respect to reaction time and solution refreshment rate. The length, diameter and aspect ratio of the nanorods increased with reaction time as 4 hours (1.98 μm, 121 nm, 15.32), 8 hours (4 μm, 185 nm, 22.70), 12 hours (5.6 μm, 242 nm, 27.24) and 16 hours (8 μm, 254 nm, 38.02) respectively. Unlike conventional Dye-Sensitized Solar Cell (DSSC) with a liquid electrolyte, DSSC were fabricated here using 1D rutile TiO2 nanorods based photoanodes, N719 dye and quasi-state electrolyte. The charge transport properties were investigated from current-voltage curves and fitted using one-diode model. Interestingly photovoltaic performance of DSSCs increased exponentially with the length of the nanorod and is attributed to the higher surface to volume ratio, more dye anchoring, and channelized electron transport. Higher photovoltaic performance (Jsc=5.99 mA/cm2, Voc=750 mV, η=3.08%) was observed with photoanodes (16 hours) made of densely packed longest TiO2 nanorods (8 µm, 254 nm). © 2017 IOP Publishing Ltd.

Fast photocatalytic degradation of sulforhodamine B using ZnO:Cu nanorods

NASA Astrophysics Data System (ADS)

Raji, R.; Gopchandran, K. G.

2018-02-01

In this work, ZnO:Cu nanorods with tunable Cu content were successfully synthesized via co-precipitation method and investigations were made on the use of these nanorods as photocatalyst by observing the photodegradation of a representative dye pollutant of sulforhodamine B (SRB) under sunlight. The X-ray diffraction analysis and high resolution transmission electron microscopy showed that ZnO:Cu nanorods possess wurtzite phase with preferential growth along (101) plane. The formation of additional defect levels in these nanorods on doping with Cu and its dependence on the concentration of Cu were studied using photoluminescence and X-ray photoelectron spectroscopy. ZnO:Cu nanorods results in faster degradation of dye as compared to the undoped ZnO and is found that Cu doping enhances the photodegradation activity significantly and is highly sensitive to Cu doping level. The fast photocatalytic degradation is attributed to the fact that Cu ions promote the interfacial charge transfer and favors the effective charge separation of photogenerated electrons and holes generated during sunlight irradiation, increasing the rate of production of reactive oxygen species needed for the degradation of the dye. The chemical oxygen demand analysis of the dye solution after sunlight irradiation indicates that rate of mineralization is slower than the decoloration. The possible mechanism for degradation of dye under sunlight irradiation is described with a schematic. Additionally, the photostability of the ZnO:Cu nanorods was also tested through three repetitive cycles. This work suggest that the prepared ZnO:Cu nanorods are suitable for cost-effective water purification.

Embedded vertically aligned cadmium telluride nanorod arrays grown by one-step electrodeposition for enhanced energy conversion efficiency in three-dimensional nanostructured solar cells.

PubMed

Wang, Jun; Liu, Shurong; Mu, Yannan; Liu, Li; A, Runa; Yang, Jiandong; Zhu, Guijie; Meng, Xianwei; Fu, Wuyou; Yang, Haibin

2017-11-01

Vertically aligned CdTe nanorods (NRs) arrays are successfully grown by a simple one-step and template-free electrodeposition method, and then embedded in the CdS window layer to form a novel three-dimensional (3D) heterostructure on flexible substrates. The parameters of electrodeposition such as deposition potential and pH of the solution are varied to analyze their important role in the formation of high quality CdTe NRs arrays. The photovoltaic conversion efficiency of the solar cell based on the 3D heterojunction structure is studied in detail. In comparison with the standard planar heterojunction solar cell, the 3D heterojunction solar cell exhibits better photovoltaic performance, which can be attributed to its enhanced optical absorption ability, increased heterojunction area and improved charge carrier transport. The better photoelectric property of the 3D heterojunction solar cell suggests great application potential in thin film solar cells, and the simple electrodeposition process represents a promising technique for large-scale fabrication of other nanostructured solar energy conversion devices. Copyright © 2017 Elsevier Inc. All rights reserved.

Effects of nanorod structure and conformation of fatty acid self-assembled layers on superhydrophobicity of zinc oxide surface.

PubMed

Badre, Chantal; Dubot, P; Lincot, Daniel; Pauporte, Thierry; Turmine, Mireille

2007-12-15

Superhydrophobic surfaces have been prepared from nanostructured zinc oxide layers by a treatment with fatty acid molecules. The layers are electrochemically deposited from an oxygenated aqueous zinc chloride solution. The effects of the layer's structure, from a dense film to that of a nanorod array, as well as that of the properties of the fatty acid molecules based on C18 chains are described. A contact angle (CA) as high as 167 degrees is obtained with the nanorod structure and the linear saturated molecule (stearic acid). Lower values are found with molecules having an unsaturated bond on C9, in particular with a cis conformation (140 degrees ). These results, supplemented by infrared spectroscopy, indicate an enhancement of the sensitivity to the properties of the fatty acid molecules (conformation, flexibility, saturated or not) when moving from the flat surface to the nanostructured surface. This is attributed to a specific influence of the structure of the tops of the rods and lateral wall properties on the adsorption and organization of the molecules. CA measurements show a very good stability of the surface in time if stored in an environment protected from UV radiations.

Synthesis of NiMn-LDH Nanosheet@Ni3S2 Nanorod Hybrid Structures for Supercapacitor Electrode Materials with Ultrahigh Specific Capacitance.

PubMed

Yu, Shuai; Zhang, Yingxi; Lou, Gaobo; Wu, Yatao; Zhu, Xinqiang; Chen, Hao; Shen, Zhehong; Fu, Shenyuan; Bao, Binfu; Wu, Limin

2018-03-27

One of the key challenges for pseudocapacitive electrode materials with highly effective capacitance output and future practical applications is how to rationally construct hierarchical and ordered hybrid nanoarchitecture through the simple process. Herein, we design and synthesize a novel NiMn-layered double hydroxide nanosheet@Ni 3 S 2 nanorod hybrid array supported on porous nickel foam via a one-pot hydrothermal method. Benefited from the ultrathin and rough nature, the well-defined porous structure of the hybrid array, as well as the synergetic effect between NiMn-layered double hydroxide nanosheets and Ni 3 S 2 nanorods, the as-fabricated hybrid array-based electrode exhibits an ultrahigh specific capacitance of 2703 F g -1 at 3 A g -1 . Moreover, the asymmetric supercapacitor with this hybrid array as a positive electrode and wood-derived activated carbon as a negative electrode demonstrates high energy density (57 Wh Kg -1 at 738 W Kg -1 ) and very good electrochemical cycling stability.

Preparation and characterization of nanorod-like TiO2 and ZnO films used for charge-transport buffer layers in P3HT based organic solar cells

NASA Astrophysics Data System (ADS)

Thao, Tran Thi; Long, Dang Dinh; Truong, Vo-Van; Dinh, Nguyen Nang

2016-08-01

With the aim of findingout the appropriate buffer layers for organic solar cells (OSC), TiO2 and ZnO on ITO/glass were prepared as nanorod-like thin films. The TiO2 films were crystallyzed in the anatase phase and the ZnO films, in the wurtzite structure. The nanorods in both the fims have a similar size of 15 to 20 nm in diameter and 30 to 50 nm in length. The nanorods have an orientation nearly perpendicular to the ITO-substrate surface. From UV-Vis data the bandgap of the TiO2 and ZnO films were determined tobe 3.26 eV and 3.42 eV, respectively. The laminar organic solar cells with added TiO2 and ZnO, namely ITO/TiO2/P3HT:PCBM/LiF/Al (TBD) and ITO/ZnO/P3HT:PCBM/LiF/Al (ZBD)were made for characterization of the energy conversion performance. As a result, comparing to TiO2,the nanorod-likeZnO filmwas found to be a much better buffer layer that made the fill factor improve from a value of 0.60 for TBD to 0.82 for ZBD, and consequently thePCE was enhanced from 0.84 for TBD to 1.17% for ZBD.

Biofunctionalization of aqueous dispersed, alumina membrane-templated polymer nanorods for use in enzymatic chemiluminescence assays.

PubMed

Mark, Sonny S; Stolper, Samuel I; Baratti, Carla; Park, Jason Y; Kricka, Larry J

2008-09-01

The noncovalent immobilization of alkaline phosphatase (ALP) onto aqueous dispersed nylon 6 nanorods ( approximately 310 nm mean diameter; approximately 6 microm mean length) prepared by anodic aluminum oxide (AAO) membrane templating was studied. Using multi-stacked layer-by-layer (LBL) assembly with the cationic quaternary ammonium polymer Sapphire II , the amount of ALP enzyme loaded onto the polymer nanostructures was found to be 115+/-7 microg mg(-1) nanorod. The biofunctionalized nanorods were also characterized for their chemiluminescent activity with the dioxetane substrate, CSPD . The results indicate that the kinetic parameters, K(m) and V(max), for the catalytic activity of the nanostructure-bound ALP enzyme are different from those of soluble ('free') ALP. While the K(m) value was measured to be 156 microM for free ALP, the apparent K(m) value determined for the LBL-immobilized ALP is approximately 20% lower (122 microM). Furthermore, despite the relatively high enzyme loading capacity of the nanorods, the specific activity of the bound ALP enzyme was found to be almost nine times lower than that measured for free ALP. Finally, additional experiments revealed that the catalytic activities of both free ALP and nanorod-conjugated ALP are affected similarly by changes in pH, with optimal performance levels occurring under conditions of pH 9.5. To the best of our knowledge, this study represents the first report examining the preparation of aqueous dispersed, AAO-templated polymer nanorods for potential application as enzyme scaffolds in chemiluminescent-based assay systems.

Very low-refractive-index optical thin films consisting of an array of SiO2 nanorods

NASA Astrophysics Data System (ADS)

Xi, J.-Q.; Kim, Jong Kyu; Schubert, E. F.; Ye, Dexian; Lu, T.-M.; Lin, Shawn-Yu; Juneja, Jasbir S.

2006-03-01

The refractive-index contrast in dielectric multilayer structures, optical resonators, and photonic crystals is an important figure of merit that creates a strong demand for high-quality thin films with a low refractive index. A SiO2 nanorod layer with low refractive index of n=1.08, to our knowledge the lowest ever reported in thin-film materials, is grown by oblique-angle electron-beam deposition of SiO2. A single-pair distributed Bragg reflector employing a SiO2 nanorod layer is demonstrated to have enhanced reflectivity, showing the great potential of low-refractive-index films for applications in photonic structures and devices.

Facile formation of Ag{sub 2}WO{sub 4}/AgX (X = Cl, Br, I) hybrid nanorods with enhanced visible-light-driven photoelectrochemical properties

DOE Office of Scientific and Technical Information (OSTI.GOV)

Li, Jingjing; Yu, Caiyun; Zheng, Changcheng

2015-01-15

Highlights: • Ag{sub 2}WO{sub 4}/AgX hybrid nanorods were prepared by a facile in-situ anion exchange reaction. • Ag{sub 2}WO{sub 4} nanorods and different X{sup −} ions were reacted in water at room temperature. • The hybrids possess significantly enhanced photoelectrochemical properties. • Ag{sub 2}WO{sub 4}/AgBr hybrids exhibit the highest photocatalytic activity among three samples. • The active species tests were also investigated to confirm photocatalytic mechanism. - Abstract: In this work, we demonstrated a general strategy for the preparation of a series of uniform Ag{sub 2}WO{sub 4}/AgX (X = Cl, Br, I) hybrid nanorods by a facile in-situ anion exchangemore » reaction occurring at room temperature between pregrown Ag{sub 2}WO{sub 4} nanorods and different X{sup −} ions in water. Compared with Ag{sub 2}WO{sub 4} nanorods, further investigation has revealed that the as-prepared hybrid nanorods possess significantly enhanced photocurrent response and photocatalytic activity in degrading methyl orange (MO) under visible-light irradiation. In particular, the Ag{sub 2}WO{sub 4}/AgBr hybrid nanorods exhibit the highest photocatalytic activity among the three kinds of samples. The active species tests indicate that superoxide anion radicals and photogenerated holes are responsible for the enhanced photocatalytic performance.« less

Manipulation of surface morphology of flower-like Ag/ZnO nanorods to enhance photocatalytic performance

NASA Astrophysics Data System (ADS)

U-thaipan, Kasira; Tedsree, Karaked

2018-06-01

The surface morphology of flower-like Ag/ZnO nanorod can be manipulated by adopting different synthetic routes and also loading different levels of Ag in order to alter their surface structures to achieve the maximum photocatalytic efficiency. In a single-step preparation method Ag/ZnO was prepared by heating directly a mixture of Zn2+ and Ag+ precursors in an aqueous NaOH-ethylene glycol solution, while in the two-step preparation method an intermediate of flower-shaped ZnO nanorod was obtained by a hydrothermal process before depositing Ag particles on the ZnO surfaces by chemical reduction. The structure, morphology and optical properties of the synthesized samples were characterized using TEM, SEM, XRD, DRS and PL techniques. The sample prepared by single-step method are characterized with agglomeration of Ag atoms as clusters on the surface of ZnO, whereas in the sample prepared by two-step method Ag atoms are found uniformly dispersed and deposited as discrete Ag nanoparticles on the surface of ZnO. A significant enhancement in the adsorption of visible light was evident for Ag/ZnO samples prepared by two-step method especially with low Ag content (0.5 mol%). The flower-like Ag/ZnO nanorod prepared with 0.5 mol% Ag by two-step process was found to be the most efficient photocatalyst for the degradation of phenol, which can decompose 90% of phenol within 120 min.

Effect of Cobalt Concentration and Oxygen Vacancy on Magnetism of Co Doped ZnO Nanorods.

PubMed

Li, Congli; Che, Ping; Sun, Changyan; Li, Wenjun

2016-03-01

Zn(1-x)Co(x)O (x = 0-0.07) single-crystalline nanorods were prepared by a modified microemulsion route. The crystalline structure, morphology, optical, and hysteresis loop at low and room temperature of as-prepared materials were characterized by XRD, TEM, PL spectra, and magnetic measurement respectively. The nanorods are 80-250 nm in diameter and about 3 μm in length. X-ray diffraction data, TEM images confirm that the materials synthesized in optimal conditions are ZnO:Co single crystalline solid solution without any impurities related to Co. The PL spectra show that the ferromagnetic samples exhibit strong Zn interstitials and oxygen vacancy emission indicating defects may stabilize ferromagnetic order in the obtained diluted magnetic semiconductors. Magnetic measurements show that the Zn(1-x)Co(x)O nanorods exist obvious ferromagnetic characteristics with T(c) above 300 K. M(s) and coercivities first increase and then decrease with dopant concentration increasing, reaching the highest for 3% doping level. The structural and magnetic properties of these samples support the hypothesis that the FM of DMS nanorods is due to a defect mediated mechanism instead of cobalt nanoclusters and carrier mediated.

Aligned hierarchical Ag/ZnO nano-heterostructure arrays via electrohydrodynamic nanowire template for enhanced gas-sensing properties.

PubMed

Yin, Zhouping; Wang, Xiaomei; Sun, Fazhe; Tong, Xiaohu; Zhu, Chen; Lv, Qiying; Ye, Dong; Wang, Shuai; Luo, Wei; Huang, YongAn

2017-09-22

Gas sensing performance can be improved significantly by the increase in both the effective gas exposure area and the surface reactivitiy of ZnO nanorods. Here, we propose aligned hierarchical Ag/ZnO nano-heterostructure arrays (h-Ag/ZnO-NAs) via electrohydrodynamic nanowire template, together with a subsequent hydrothermal synthesis and photoreduction reaction. The h-Ag/ZnO-NAs scatter at top for higher specific surface areas with the air, simultaneously contact at root for the electrical conduction. Besides, the ZnO nanorods are uniformly coated with dispersed Ag nanoparticles, resulting in a tremendous enhancement of the surface reactivity. Compared with pure ZnO, such h-Ag/ZnO-NAs exhibit lower electrical resistance and faster responses. Moreover, they demonstrate enhanced NO 2 gas sensing properties. Self-assembly via electrohydrodynamic nanowire template paves a new way for the preparation of high performance gas sensors.

Effect of thermal implying during ageing process of nanorods growth on the properties of zinc oxide nanorod arrays

DOE Office of Scientific and Technical Information (OSTI.GOV)

Ismail, A. S., E-mail: kyrin-samaxi@yahoo.com; Mamat, M. H., E-mail: mhmamat@salam.uitm.edu.my; Rusop, M., E-mail: rusop@salam.uitm.my

Undoped and Sn-doped Zinc oxide (ZnO) nanostructures have been fabricated using a simple sol-gel immersion method at 95°C of growth temperature. Thermal sourced by hot plate stirrer was supplied to the solution during ageing process of nanorods growth. The results showed significant decrement in the quality of layer produced after the immersion process where the conductivity and porosity of the samples reduced significantly due to the thermal appliance. The structural properties of the samples have been characterized using field emission scanning electron microscopy (FESEM) electrical properties has been characterized using current voltage (I-V) measurement.

The effect of cation doping on the morphology, optical and structural properties of highly oriented wurtzite ZnO-nanorod arrays grown by a hydrothermal method

NASA Astrophysics Data System (ADS)

Hassanpour, A.; Guo, P.; Shen, S.; Bianucci, P.

2017-10-01

Undoped and C-doped (C: Mg2+, Ni2+, Mn2+, Co2+, Cu2+, Cr3+) ZnO nanorods were synthesized by a hydrothermal method at temperatures as low as 60 °C. The effect of doping on the morphology of the ZnO nanorods was visualized by taking their cross section and top SEM images. The results show that the size of nanorods was increased in both height and diameter by cation doping. The crystallinity change of the ZnO nanorods due to each doping element was thoroughly investigated by an x-ray diffraction (XRD). The XRD patterns show that the wurtzite crystal structure of ZnO nanorods was maintained after cation addition. The optical Raman-active modes of undoped and cation-doped nanorods were measured with a micro-Raman setup at room temperature. The surface chemistry of samples was investigated by x-ray photoelectron spectroscopy and energy-dispersive x-ray spectroscopy. Finally, the effect of each cation dopant on band-gap shift of the ZnO nanorods was investigated by a photoluminescence setup at room temperature. Although the amount of dopants (Mg2+, Ni2+, and Co2+) was smaller than the amount of Mn2+, Cu2+, and Cr3+ in the nanorods, their effect on the band structure of the ZnO nanorods was profound. The highest band-gap shift was achieved for a Co-doped sample, and the best crystal orientation was for Mn-doped ZnO nanorods. Our results can be used as a comprehensive reference for engineering of the morphological, structural and optical properties of cation-doped ZnO nanorods by using a low-temperature synthesis as an economical mass-production approach.

Tunable laser interference lithography preparation of plasmonic nanoparticle arrays tailored for SERS.

PubMed

Gisbert Quilis, Nestor; Lequeux, Médéric; Venugopalan, Priyamvada; Khan, Imran; Knoll, Wolfgang; Boujday, Souhir; Lamy de la Chapelle, Marc; Dostalek, Jakub

2018-05-23

The facile preparation of arrays of plasmonic nanoparticles over a square centimeter surface area is reported. The developed method relies on tailored laser interference lithography (LIL) that is combined with dry etching and it offers means for the rapid fabrication of periodic arrays of metallic nanostructures with well controlled morphology. Adjusting the parameters of the LIL process allows for the preparation of arrays of nanoparticles with a diameter below hundred nanometers independently of their lattice spacing. Gold nanoparticle arrays were precisely engineered to support localized surface plasmon resonance (LSPR) with different damping at desired wavelengths in the visible and near infrared part of the spectrum. The applicability of these substrates for surface enhanced Raman scattering is demonstrated where cost-effective, uniform and reproducible substrates are of paramount importance. The role of deviations in the spectral position and the width of the LSPR band affected by slight variations of plasmonic nanostructures is discussed.

Facile synthesis and luminescent properties of TiO{sub 2}:Eu{sup 3+} nanorods and spindle-shaped nanoparticles from titanate nanotubes precursors

DOE Office of Scientific and Technical Information (OSTI.GOV)

Li, Hongbo; Sheng, Ye; Zhao, Huan

2012-12-15

Graphical abstract: This picture illustration for the formation process of TiO{sub 2}:Eu{sup 3+} nanorods and spindle-shaped nanoparticles. Display Omitted Highlights: ► TiO{sub 2}:Eu{sup 3+} nanorods and spindle-shaped nanoparticles were prepared. ► The nanotubes could transform to nanorods and spindle-shaped nanoparticles. ► The luminescence properties are dependent on the increases of the bandgap. -- Abstract: TiO{sub 2}:Eu{sup 3+} nanorods and spindle-shaped nanoparticles have been successfully prepared through simple calcination and hydrothermal process respectively using titanate as the precursors. On the basis of X-ray diffraction results, the as-obtained precursors are titanate (H{sub 2}Ti{sub 2}O{sub 5}·H{sub 2}O), while nanorods and spindle-shaped nanoparticles aremore » pure anatase phase of TiO{sub 2}. TEM and SEM images show that the as-formed precursor could be transformed from nanotubes into nanorods and spindle-shaped nanoparticles by the calcination and hydrothermal process respectively. Under UV light excitation, both the TiO{sub 2}:Eu{sup 3+} nanorods and spindle-shaped nanoparticles exhibit the strong red emission. In addition, the luminescence intensity of TiO{sub 2}:Eu{sup 3+} nanorods is higher than that of TiO{sub 2}:Eu{sup 3+} spindle-shaped nanoparticles due to the increases of the bandgap of the TiO{sub 2} nanorods.« less

Large-scale fabrication of single crystalline tin nanowire arrays.

PubMed

Luo, Bin; Yang, Dachi; Liang, Minghui; Zhi, Linjie

2010-09-01

Large-scale single crystalline tin nanowire arrays with preferred lattice orientation along the [100] direction were fabricated in porous anodic aluminium oxide (AAO) membranes by the electrodeposition method using copper nanorod as a second electrode.

High performance electrical, magnetic, electromagnetic and electrooptical devices enabled by three dimensionally ordered nanodots and nanorods

DOEpatents

Goyal, Amit , Kang; Sukill, [Knoxville, TN

2012-02-21

Novel articles and methods to fabricate same with self-assembled nanodots and/or nanorods of a single or multicomponent material within another single or multicomponent material for use in electrical, electronic, magnetic, electromagnetic and electrooptical devices is disclosed. Self-assembled nanodots and/or nanorods are ordered arrays wherein ordering occurs due to strain minimization during growth of the materials. A simple method to accomplish this when depositing in-situ films is also disclosed. Device applications of resulting materials are in areas of superconductivity, photovoltaics, ferroelectrics, magnetoresistance, high density storage, solid state lighting, non-volatile memory, photoluminescence, thermoelectrics and in quantum dot lasers.

Optoacoustic detection of viral antigens using targeted gold nanorods

NASA Astrophysics Data System (ADS)

Maswadi, Saher; Woodward, Lee; Glickman, Randolph D.; Barsalou, Norman

2009-02-01

We are detecting antigens (Ag), isolated from infectious organisms, utilizing laser optoacoustic spectroscopy and antibody-coupled gold nanorod (NR) contrast agents specifically targeted to the antigen of interest. We have detected, in clinical ocular samples, both Herpes Simplex Virus Type 1 and 2 (HSV-1 and HSV-2) . A monoclonal antibody (Ab) specific to both HSV-1 and HSV-2 was conjugated to gold nanorods to produce a targeted contrast agent with a strong optoacoustic signal. Elutions obtained from patient corneal swabs were adsorbed in standard plastic micro-wells. An immunoaffinity reaction was then performed with the functionalized gold nanorods, and the results were probed with an OPO laser, emitting wavelengths at the peak absorptions of the nanorods. Positive optoacoustic responses were obtained from samples containing authentic (microbiologically confirmed) HSV-1 and HSV-2. To obtain an estimate of the sensitivity of the technique, serial dilutions from 1 mg/ml to 1 pg/ml of a C. trachomatis surface Ag were prepared, and were probed with a monoclonal Ab, specific to the C. trachomatis surface Ag, conjugated to gold nanorods. An optoacoustic response was obtained, proportional to the concentration of antigen, and with a limit of detection of about 5 pg/ml. The optoacoustic signals generated from micro-wells containing albumin or saline were similar to those from blank wells. The potential benefit of this method is identify viral agents more rapidly than with existing techniques. In addition, the sensitivity of the assay is comparable or superior to existing colorimetric- or fluorometric-linked immunoaffinity assays.

Hexagonal nanorods of tungsten trioxide: Synthesis, structure, electrochemical properties and activity as supporting material in electrocatalysis

NASA Astrophysics Data System (ADS)

Salmaoui, Samiha; Sediri, Faouzi; Gharbi, Néji; Perruchot, Christian; Aeiyach, Salah; Rutkowska, Iwona A.; Kulesza, Pawel J.; Jouini, Mohamed

2011-07-01

Tungsten trioxide, unhydrated with hexagonal structure (h-WO 3), has been prepared by hydrothermal method at a temperature of 180 °C in acidified sodium tungstate solution. Thus prepared h-WO 3 has been characterized by X-ray diffraction (XRD) method and using electrochemical techniques. The morphology has been examined by scanning and transmission electron microscopies (SEM and TEM) and it is consistent with existence of nanorods of 50-70 nm diameter and up to 5 μm length. Cyclic voltammetric characterization of thin films of h-WO 3 nanorods has revealed reversible redox behaviour with charge-discharge cycling corresponding to the reversible lithium intercalation/deintercalation into the crystal lattice of the h-WO 3 nanorods. In propylene carbonate containing LiClO 4, two successive redox processes of hexagonal WO 3 nanorods are observed at the scan rate of 50 mV/s. Such behaviour shall be attributed to the presence of at least two W atoms of different surroundings in the lattice structure of h-WO 3 nanorods. On the other hand, in aqueous LiClO 4 solution, only one redox process is observed at the scan rate of 10 mV/s. The above observations can be explained in terms of differences in the diffusion of ions inside two types of channel cavities existing in the structure of the h-WO 3 nanorods. Moreover, the material can be applied as active support for the catalytic bi-metallic Pt-Ru nanoparticles during electrooxidation of ethanol in acid medium (0.5 mol dm -3 H 2SO 4).

Reactive tunnel junctions in electrically driven plasmonic nanorod metamaterials

NASA Astrophysics Data System (ADS)

Wang, Pan; Krasavin, Alexey V.; Nasir, Mazhar E.; Dickson, Wayne; Zayats, Anatoly V.

2018-02-01

Non-equilibrium hot carriers formed near the interfaces of semiconductors or metals play a crucial role in chemical catalysis and optoelectronic processes. In addition to optical illumination, an efficient way to generate hot carriers is by excitation with tunnelling electrons. Here, we show that the generation of hot electrons makes the nanoscale tunnel junctions highly reactive and facilitates strongly confined chemical reactions that can, in turn, modulate the tunnelling processes. We designed a device containing an array of electrically driven plasmonic nanorods with up to 1011 tunnel junctions per square centimetre, which demonstrates hot-electron activation of oxidation and reduction reactions in the junctions, induced by the presence of O2 and H2 molecules, respectively. The kinetics of the reactions can be monitored in situ following the radiative decay of tunnelling-induced surface plasmons. This electrically driven plasmonic nanorod metamaterial platform can be useful for the development of nanoscale chemical and optoelectronic devices based on electron tunnelling.

Enhanced photobactericidal activity of ZnO nanorods modified by meso-tetrakis(4-sulfonatophenyl)porphyrin under visible LED lamp irradiation.

PubMed

Rahimi, Rahmatollah; Shokraiyan, Javad; Rabbani, Mahboubeh; Fayyaz, Fatemeh

2015-01-01

In this study, zinc oxide (ZnO) nanorods have been synthesized using a simple template-free precipitation technique and deposited on glass substrate. The meso-tetrakis(4-sulfonatophenyl)porphyrin (TPPS) has been synthesized and then immobilized on the surface of ZnO nanorods to prepare an organic/inorganic composite. The samples were characterized by various techniques such as X-ray diffraction, diffuse reflectance spectra, Fourier transform-infrared spectroscopy and scanning electron microscopy. In addition, the photobactericidal activity of TPPS/ZnO composite, TPPS and ZnO nanorods was tested against the pathogenic bacterium of Escherichia coli under visible LED lamp irradiation. The results indicate that the photobactericidal activity of TPPS-loaded ZnO nanorods was better than TPPS or ZnO nanorods, separately.

Surface polyPEGylation of Eu3+ doped luminescent hydroxyapatite nanorods through the combination of ligand exchange and metal free surface initiated atom transfer radical polymerization

NASA Astrophysics Data System (ADS)

Zeng, Guangjian; Liu, Meiying; Heng, Chunning; Huang, Qiang; Mao, Liucheng; Huang, Hongye; Hui, Junfeng; Deng, Fengjie; Zhang, Xiaoyong; Wei, Yen

2017-03-01

The Eu3+ doped luminescent hydroxyapatite (HAp) nanorods with uniform size and morphology can be synthesized by hydrothermal route. However, these HAp nanorods are coated by hydrophobic oleylamine, which makes them difficult to be dispersed in aqueous solution and impede their biomedical applications. In this work, Eu3+ doped luminescent polymers functionalized HAp nanorods were prepared through the combination of ligand exchange reaction and metal free surface initiated atom transfer radical polymerization (ATRP) method. In this procedure, the amino group functionalized HAp nanorods were first prepared by ligand exchange reaction using adenosine monophosphate (AMP) as ligand. Then the Br-containing initiators (HAp-Br) were introduced onto the surface of HAp-AMP nanorods through the amidation reaction. Finally, polymers functionalized HAp nanorods were prepared by metal free ATRP method using poly(ethylene glycol) methacrylate (PEGMA) as monomer and 10-phenylphenothiazine (PTH) as organic photocatalyst. The properties of these obtained HAp nanocomposites (HAP-polyPEGMA nanorods) were characterized by means of transmission electron microscopy, Fourier transformed infrared spectroscopy, X-ray photoelectron spectroscopy and thermogravimetric analysis in detail. The cell imaging of these HAP-polyPEGMA nanorods was examined using laser scanning confocal microscope to evaluate their biomedical applications. We demonstrated for the first time that hydrophobic luminescent HAp nanorods can be functionalized with polyPEGMA through the combination of ligand exchange reaction and metal free surface initiated ATRP. As compared with the traditional ATRP, the metal free ATRP can overcome the toxic and fluorescence quenching effects of metal catalysts such as copper ions. More importantly, the strategy described in this work should also be utilized for fabrications of many other luminescent polymer nanocomposites due to its good monomer adoptability.

Highly piezoelectric BaTiO3 nanorod bundle arrays using epitaxially grown TiO2 nanomaterials.

PubMed

Jang, Seon-Min; Yang, Su Chul

2018-06-08

Low-dimensional piezoelectric nanostructures such as nanoparticles, nanotubes, nanowires, nanoribbons and nanosheets have been developed for potential applications as energy harvesters, tunable sensors, functional transducers and low-power actuators. In this study, lead-free BaTiO 3 nanorod bundle arrays (NBA) with highly piezoelectric properties were successfully synthesized on fluorine-doped tin oxide (FTO) substrate via a two-step process consisting of TiO 2 epitaxial growth and BaTiO 3 conversion. Through the TiO 2 epitaxial growth on FTO substrate, (001) oriented TiO 2 nanostructures formed vertically-aligned NBA with a bundle diameter of 80 nm and an aspect ratio of six. In particular, chemical etching of the TiO 2 NBA was conducted to enlarge the surface area for effective Ba 2+ ion diffusion during the perovskite conversion process from TiO 2 to BaTiO 3 . The final structure of perovskite BaTiO 3 NBA was found to exhibit a feasible piezoelectric response of 3.56 nm with a clear phase change of 180° from the single BaTiO 3 bundle, by point piezoelectric forced microscopy (PFM) analysis. Consequently, highly piezoelectric NBA could be a promising nanostructure for various nanoscale electronic devices.

Highly piezoelectric BaTiO3 nanorod bundle arrays using epitaxially grown TiO2 nanomaterials

NASA Astrophysics Data System (ADS)

Jang, Seon-Min; Yang, Su Chul

2018-06-01

Low-dimensional piezoelectric nanostructures such as nanoparticles, nanotubes, nanowires, nanoribbons and nanosheets have been developed for potential applications as energy harvesters, tunable sensors, functional transducers and low-power actuators. In this study, lead-free BaTiO 3 nanorod bundle arrays (NBA) with highly piezoelectric properties were successfully synthesized on fluorine-doped tin oxide (FTO) substrate via a two-step process consisting of TiO2 epitaxial growth and BaTiO3 conversion. Through the TiO2 epitaxial growth on FTO substrate, (001) oriented TiO2 nanostructures formed vertically-aligned NBA with a bundle diameter of 80 nm and an aspect ratio of six. In particular, chemical etching of the TiO2 NBA was conducted to enlarge the surface area for effective Ba2+ ion diffusion during the perovskite conversion process from TiO2 to BaTiO3. The final structure of perovskite BaTiO3 NBA was found to exhibit a feasible piezoelectric response of 3.56 nm with a clear phase change of 180° from the single BaTiO3 bundle, by point piezoelectric forced microscopy (PFM) analysis. Consequently, highly piezoelectric NBA could be a promising nanostructure for various nanoscale electronic devices.

Chemically stable Au nanorods as probes for sensitive surface enhanced scattering (SERS) analysis of blue BIC ballpoint pens

NASA Astrophysics Data System (ADS)

Alyami, Abeer; Saviello, Daniela; McAuliffe, Micheal A. P.; Cucciniello, Raffaele; Mirabile, Antonio; Proto, Antonio; Lewis, Liam; Iacopino, Daniela

2017-08-01

Au nanorods were used as an alternative to commonly used Ag nanoparticles as Surface Enhanced Raman Scattering (SERS) probes for identification of dye composition of blue BIC ballpoint pens. When used in combination with Thin Layer Chromatography (TLC), Au nanorod colloids allowed identification of the major dye components of the BIC pen ink, otherwise not identifiable by normal Raman spectroscopy. Thanks to their enhanced chemical stability compared to Ag colloids, Au nanorods provided stable and reproducible SERS signals and allowed easy identification of phthalocyanine and triarylene dyes in the pen ink mixture. These findings were supported by FTIR and MALDI analyses, also performed on the pen ink. Furthermore, the self-assembly of Au nanorods into large area ordered superstructures allowed identification of BIC pen traces. SERS spectra of good intensity and high reproducibility were obtained using Au nanorod vertical arrays, due to the high density of hot spots and morphological reproducibility of these superstructures. These results open the way to the employment of SERS for fast screening analysis and for quantitative analysis of pens and faded pens which are relevant for the fields of forensic and art conservation sciences.

A study of transition from n- to p-type based on hexagonal WO3 nanorods sensor

NASA Astrophysics Data System (ADS)

Wu, Ya-Qiao; Hu, Ming; Wei, Xiao-Ying

2014-04-01

Hexagonal WO3 nanorods are fabricated by a facile hydrothermal process at 180 °C using sodium tungstate and sodium chloride as starting materials. The morphology, structure, and composition of the prepared nanorods are studied by scanning electron microscopy, X-ray diffraction spectroscopy, and energy dispersive spectroscopy. It is found that the agglomeration of the nanorods is strongly dependent on the PH value of the reaction solution. Uniform and isolated WO3 nanorods with diameters ranging from 100 nm-150 nm and lengths up to several micrometers are obtained at PH = 2.5 and the nanorods are identified as being hexagonal in phase structure. The sensing characteristics of the WO3 nanorod sensor are obtained by measuring the dynamic response to NO2 with concentrations in the range 0.5 ppm-5 ppm and at working temperatures in the range 25 °C-250 °C. The obtained WO3 nanorods sensors are found to exhibit opposite sensing behaviors, depending on the working temperature. When being exposed to oxidizing NO2 gas, the WO3 nanorod sensor behaves as an n-type semiconductor as expected when the working temperature is higher than 50 °C, whereas, it behaves as a p-type semiconductor below 50 °C. The origin of the n- to p-type transition is correlated with the formation of an inversion layer at the surface of the WO3 nanorod at room temperature. This finding is useful for making new room temperature NO2 sensors based on hexagonal WO3 nanorods.

Praseodymium hydroxide and oxide nanorods and Au/Pr6O11 nanorod catalysts for CO oxidation.

PubMed

Huang, P X; Wu, F; Zhu, B L; Li, G R; Wang, Y L; Gao, X P; Zhu, H Y; Yan, T Y; Huang, W P; Zhang, S M; Song, D Y

2006-02-02

Praseodymium hydroxide nanorods were synthesized by a two-step approach: First, metallic praseodymium was used to form praseodymium chloride, which reacted subsequently with KOH solution to produce praseodymium hydroxide. In the second step the hydroxide was treated with a concentrated alkaline solution at 180 degrees C for 45 h, yielding nanorods as shown by the scanning and transmission electron microscopy images. The results of X-ray diffraction and energy-dispersive X-ray spectroscopy experiments indicate that these nanorods are pure praseodymium hydroxide with a hexagonal structure, which can be converted into praseodymium oxide (Pr6O11) nanorods of a face-centered cubic structure after calcination at 600 degrees C for 2 h in air. Gold was loaded on the praseodymium oxide nanorods using HAuCl4 as the gold source, and NaBH4 was used to reduce the gold species to metallic nanoparticles with sizes of 8-12 nm on the nanorod surface. These Au/Pr6O11 nanorods exhibit superior catalytic activity for CO oxidation.

Hydrothermally derived nanoporous titanium dioxide nanorods/nanoparticles and their influence in dye-sensitized solar cell as a photoanode

NASA Astrophysics Data System (ADS)

Rajamanickam, Govindaraj; Narendhiran, Santhosh; Muthu, Senthil Pandian; Mukhopadhyay, Sumita; Perumalsamy, Ramasamy

2017-12-01

Titanium dioxide is a promising wide band gap semiconducting material for dye-sensitized solar cell. The poor electron transport properties still remain a challenge with conventional nanoparticles. Here, we synthesized TiO2 nanorods/nanoparticles by hydrothermal method to improve the charge transport properties. The structural and morphological information of the prepared nanorods/nanoparticles was analysed with X-ray diffraction and electron microscopy analysis, respectively. A high power conversion efficiency of 7.7% is achieved with nanorods/nanoparticles employed device under 100 mW/cm2. From the electrochemical impedance analysis, superior electron transport properties have been found for synthesized TiO2 nanorods/nanoparticles employed device than commercial P25 nanoparticles based device.

1D structure of Y2O3:Eu nanorods: controllable synthesis, growth mechanisms and luminescence properties.

PubMed

Wang, Qin; Guo, Jing; Jia, Wenjing; Liul, Baocang; Liu, Yongxin; Xu, Guangran; Liu, Yang; Hu, Wenting; Zhang, Jun

2014-05-01

Y2O3O:Eu nanorods were successfully synthesized by a facile and effective hydrothermal method in the presence of P123 (EO106PO70EO106) as the surfactant followed by a subsequent heat treatment process. The scanning electron microscopy (SEM) and transmission electron microscopy (TEM) images indicate that the as-prepared samples consist of nanorods with diameters ranging from 80 nm to 100 nm and grow along the (100) direction. The growth mechanism of the as-obtained Y2O3:Eu nanorods was proposed on the basis of pH-dependent experiments. It is found that the pH is a crucial factor in determining the phase, morphology and luminescence properties of Y2O3:Eu nanorods. The luminescent spectra of Y2O3:Eu nanorods show the strong characteristic dominant emission of the Eu3+ ions at 613 nm.

Gold nanorod vaccine for respiratory syncytial virus

NASA Astrophysics Data System (ADS)

Stone, John W.; Thornburg, Natalie J.; Blum, David L.; Kuhn, Sam J.; Wright, David W.; Crowe, James E., Jr.

2013-07-01

Respiratory syncytial virus (RSV) is a major cause of pneumonia and wheezing in infants and the elderly, but to date there is no licensed vaccine. We developed a gold nanorod construct that displayed the major protective antigen of the virus, the fusion protein (F). Nanorods conjugated to RSV F were formulated as a candidate vaccine preparation by covalent attachment of viral protein using a layer-by-layer approach. In vitro studies using ELISA, electron microscopy and circular dichroism revealed that conformation-dependent epitopes were maintained during conjugation, and transmission electron microscopy studies showed that a dispersed population of particles could be achieved. Human dendritic cells treated with the vaccine induced immune responses in primary human T cells. These results suggest that this vaccine approach may be a potent method for immunizing against viruses such as RSV with surface glycoproteins that are targets for the human immune response.

Hexagonal pencil-like CdS nanorods: Facile synthesis and enhanced visible light photocatalytic performance

NASA Astrophysics Data System (ADS)

An, Liang; Wang, Guanghui; Zhao, Lei; Zhou, Yong; Gao, Fang; Cheng, Yang

2015-07-01

In the present study, hexagonal pencil-like CdS nanorods have been successfully synthesized through a typical facile and economical one-step hydrothermal method without using any surfactant or template. The product was characterized by X-ray powder diffraction (XRD), field-emission scanning electron microscopy (FE-SEM) and energy dispersive analysis of X-ray (EDX). The results revealed that the prepared CdS photocatalyst consisted of a large quantity of straight and smooth solid hexagonal nanorods and a few nanoparticles. The photocatalytic activities of CdS nanorods and commercial CdS powders were investigated by the photodegradation of Orange II (OII) in aqueous solution under visible light, and the CdS nanorods presented the highest photocatalytic activity. Its photocatalytic efficiency enhancement was attributed to the improved transmission of photogenerated electron-hole pairs in the CdS nanostructures. The present findings may provide a facile approach to synthesize high efficient CdS photocatalysts.

Effect of Temperature and Growth Time on Vertically Aligned ZnO Nanorods by Simplified Hydrothermal Technique for Photoelectrochemical Cells.

PubMed

Mohd Fudzi, Laimy; Zainal, Zulkarnain; Lim, Hong Ngee; Chang, Sook-Keng; Holi, Araa Mebdir; Sarif Mohd Ali, Mahanim

2018-04-29

Despite its large band gap, ZnO has wide applicability in many fields ranging from gas sensors to solar cells. ZnO was chosen over other materials because of its large exciton binding energy (60 meV) and its stability to high-energy radiation. In this study, ZnO nanorods were deposited on ITO glass via a simple dip coating followed by a hydrothermal growth. The morphological, structural and compositional characteristics of the prepared films were analyzed using X-ray diffractometry (XRD), field emission scanning electron microscopy (FESEM), and ultraviolet-visible spectroscopy (UV-Vis). Photoelectrochemical conversion efficiencies were evaluated via photocurrent measurements under calibrated halogen lamp illumination. Thin film prepared at 120 °C for 4 h of hydrothermal treatment possessed a hexagonal wurtzite structure with the crystallite size of 19.2 nm. The average diameter of the ZnO nanorods was 37.7 nm and the thickness was found to be 2680.2 nm. According to FESEM images, as the hydrothermal growth temperature increases, the nanorod diameter become smaller. Moreover, the thickness of the nanorods increase with the growth time. Therefore, the sample prepared at 120 °C for 4 h displayed an impressive photoresponse by achieving high current density of 0.1944 mA/cm².

High quality boron carbon nitride/ZnO-nanorods p-n heterojunctions based on magnetron sputtered boron carbon nitride films

DOE Office of Scientific and Technical Information (OSTI.GOV)

Qian, J. C.; Department of Engineering Physics, Polytechnique Montréal, Montreal, Quebec H3A 3A7; Jha, S. K., E-mail: skylec@gmail.com, E-mail: apwjzh@cityu.edu.hk

2014-11-10

Boron carbon nitride (BCN) films were synthesized on Si (100) and fused silica substrates by radio-frequency magnetron sputtering from a B{sub 4}C target in an Ar/N{sub 2} gas mixture. The BCN films were amorphous, and they exhibited an optical band gap of ∼1.0 eV and p-type conductivity. The BCN films were over-coated with ZnO nanorod arrays using hydrothermal synthesis to form BCN/ZnO-nanorods p-n heterojunctions, exhibiting a rectification ratio of 1500 at bias voltages of ±5 V.

MnO2 Nanorods Intercalating Graphene Oxide/Polyaniline Ternary Composites for Robust High-Performance Supercapacitors

NASA Astrophysics Data System (ADS)

Han, Guangqiang; Liu, Yun; Zhang, Lingling; Kan, Erjun; Zhang, Shaopeng; Tang, Jian; Tang, Weihua

2014-04-01

New ternary composites of MnO2 nanorods, polyaniline (PANI) and graphene oxide (GO) have been prepared by a two-step process. The 100 nm-long MnO2 nanorods with a diameter ~20 nm are conformably coated with PANI layers and fastened between GO layers. The MnO2 nanorods incorporated ternary composites electrode exhibits significantly increased specific capacitance than PANI/GO binary composite in supercapacitors. The ternary composite with 70% MnO2 exhibits a highest specific capacitance reaching 512 F/g and outstanding cycling performance, with ~97% capacitance retained over 5000 cycles. The ternary composite approach offers an effective solution to enhance the device performance of metal-oxide based supercapacitors for long cycling applications.

Selective Detection of NO2 Using Cr-Doped CuO Nanorods

PubMed Central

Kim, Kang-Min; Jeong, Hyun-Mook; Kim, Hae-Ryong; Choi, Kwon-Il; Kim, Hyo-Joong; Lee, Jong-Heun

2012-01-01

CuO nanosheets, Cr-doped CuO nanosheets, and Cr-doped CuO nanorods were prepared by heating a slurry containing Cu-hydroxide/Cr-hydroxide. Their responses to 100 ppm NO2, C2H5OH, NH3, trimethylamine, C3H8, and CO were measured. For 2.2 at% Cr-doped CuO nanorods, the response (Ra/Rg, Ra: resistance in air, Rg: resistance in gas) to 100 ppm NO2 was 134.2 at 250 °C, which was significantly higher than that of pure CuO nano-sheets (Ra/Rg = 7.5) and 0.76 at% Cr-doped CuO nanosheets (Ra/Rg = 19.9). In addition, the sensitivity for NO2 was also markedly enhanced by Cr doping. Highly sensitive and selective detection of NO2 in 2.2 at% Cr-doped CuO nanorods is explained in relation to Cr-doping induced changes in donor density, morphology, and catalytic effects. PMID:22969384

Synthesis and characterization of silicon nanorod on n-type porous silicon.

PubMed

Behzad, Kasra; Mat Yunus, Wan Mahmood; Bahrami, Afarin; Kharazmi, Alireza; Soltani, Nayereh

2016-03-20

This work reports a new method for growing semiconductor nanorods on a porous silicon substrate. After preparation of n-type porous silicon samples, a thin layer of gold was deposited on them. Gold deposited samples were annealed at different temperatures. The structural, thermal, and optical properties of the samples were studied using a field emission scanning electron microscope (FESEM), photoacoustic spectroscopy, and photoluminescence spectroscopy, respectively. FESEM analysis revealed that silicon nanorods of different sizes grew on the annealed samples. Thermal behavior of the samples was studied using photoacoustic spectroscopy. Photoluminescence spectroscopy showed that the emission peaks were degraded by gold deposition and attenuated for all samples by annealing.

Changing the thickness of two layers: i-ZnO nanorods, p-Cu2O and its influence on the carriers transport mechanism of the p-Cu2O/i-ZnO nanorods/n-IGZO heterojunction.

PubMed

Ke, Nguyen Huu; Trinh, Le Thi Tuyet; Phung, Pham Kim; Loan, Phan Thi Kieu; Tuan, Dao Anh; Truong, Nguyen Huu; Tran, Cao Vinh; Hung, Le Vu Tuan

2016-01-01

In this study, two layers: i-ZnO nanorods and p-Cu2O were fabricated by electrochemical deposition. The fabricating process was the initial formation of ZnO nanorods layer on the n-IGZO thin film which was prepared by sputtering method, then a p-Cu2O layer was deposited on top of rods to form the p-Cu2O/i-ZnO nanorods/n-ZnO heterojunction. The XRD, SEM, UV-VIS, I-V characteristics methods were used to define structure, optical and electrical properties of these heterojunction layers. The fabricating conditions and thickness of the Cu2O layers significantly affected to the formation, microstructure, electrical and optical properties of the junction. The length of i-ZnO nanorods layer in the structure of the heterojunction has strongly affected to the carriers transport mechanism and performance of this heterojunction.

Adsorption study of a macro-RAFT agent onto SiO2-coated Gd2O3:Eu3+ nanorods: Requirements and limitations

NASA Astrophysics Data System (ADS)

Zou, Hua; Melro, Liliana; de Camargo Chaparro, Thaissa; de Souza Filho, Isnaldi Rodrigues; Ananias, Duarte; Bourgeat-Lami, Elodie; dos Santos, Amilton Martins; Barros-Timmons, Ana

2017-02-01

The use of a macromolecular RAFT (macro-RAFT) agent to encapsulate anisotropic nano-objects via emulsion polymerization is an emerging route to prepare polymer/inorganic colloidal nanocomposites. However, a number of requirements have to be fulfilled. This work aims at highlighting the effects of the preparative procedure and dispersion method on the amount of macro-RAFT agent adsorbed onto SiO2-coated Gd2O3:Eu3+ nanorods. The adsorption of macro-RAFT agent was studied using the depletion method with UV-vis spectrophotometry. Measurements were performed at a fixed concentration of nanorods and varying concentrations of the macro-RAFT agent in aqueous dispersion at room temperature. The adsorption isotherms showed that for the same initial macro-RAFT agent concentration, the highest adsorption capacity of the macro-RAFT agent on nanorods was usually achieved for non-calcined thin SiO2-coated nanorods under mild bath sonication.

Magnetic anisotropy of nickel nanorods and the mechanical torque in an elastic environment

NASA Astrophysics Data System (ADS)

Schopphoven, C.; Tschöpe, A.

2018-03-01

Nickel nanorods with average length L=340~nm and diameter D=20~nm were prepared by the anodic aluminum oxide (AAO)-template method, processed to a colloidal dispersion and embedded in a gelatine hydrogel matrix at low volume fraction φ ≤slant 10-4 . The large aspect ratio of these single-domain particles gives rise to a high magnetic shape anisotropy in combination with a significant anisotropic optical polarizability. The magnetic anisotropy enables exertion of a torque on nanorods without contact by applying a homogeneous magnetic field. In response, the nanorods rotate by an angle which is determined by the balance between the magnetic torque and the mechanical counter torque, caused by the elastic deformation of the surrounding matrix. This rotation was experimentally detected using optical transmission of linearly polarized light. We used the combination of magnetization and torque-driven rotation measurements to evaluate an adapted Stoner-Wohlfarth model of the orientation- and field-dependent magnetic torque on Ni nanorods in an elastic environment as base for optimization of torque-driven magnetic actuators.

Size effect of ZnO nanorods on physicochemical properties of plasticized starch composites.

PubMed

Guz, L; Famá, L; Candal, R; Goyanes, S

2017-02-10

This work demonstrates that the size of ZnO nanorods (ZnONR) with similar aspect ratio determines several physicochemical and microbiological properties of thermoplastic starch composites (TPS/ZnONR) at a given concentration of ZnONRs. A combination of sol-gel and hydrothermal methods was developed to synthesize ZnONR with different sizes but similar aspect ratios. Starch composites containing 1wt.% of ZnONR were prepared by casting. Composites with smaller size nanorods (ZnONR-S) showed more efficiency in shielding UVA radiation and had a higher solubility and water vapor permeability than those with larger nanorods (ZnONR-L). Mechanical properties, biodegradability and antibacterial activity were also influenced by the size of the ZnONR. X-ray diffraction analysis showed that composites with ZnONR-S maintained the typical B-V type starch structure, intensifying the V-type starch structure peaks, while composite with ZnONR-L induced the formation of an amorphous structure, preventing starch retrogradation during storage. Properties affected by nanorods size are fundamental in determining composite applications. Copyright © 2016 Elsevier Ltd. All rights reserved.

ZnO nanorod arrays and direct wire bonding on GaN surfaces for rapid fabrication of antireflective, high-temperature ultraviolet sensors

NASA Astrophysics Data System (ADS)

So, Hongyun; Senesky, Debbie G.

2016-11-01

Rapid, cost-effective, and simple fabrication/packaging of microscale gallium nitride (GaN) ultraviolet (UV) sensors are demonstrated using zinc oxide nanorod arrays (ZnO NRAs) as an antireflective layer and direct bonding of aluminum wires to the GaN surface. The presence of the ZnO NRAs on the GaN surface significantly reduced the reflectance to less than 1% in the UV and 4% in the visible light region. As a result, the devices fabricated with ZnO NRAs and mechanically stable aluminum bonding wires (pull strength of 3-5 gf) showed higher sensitivity (136.3% at room temperature and 148.2% increase at 250 °C) when compared with devices with bare (uncoated) GaN surfaces. In addition, the devices demonstrated reliable operation at high temperatures up to 300 °C, supporting the feasibility of simple and cost-effective UV sensors operating with higher sensitivity in high-temperature conditions, such as in combustion, downhole, and space exploration applications.

Photoresponsive surface molecularly imprinted polymer on ZnO nanorods for uric acid detection in physiological fluids.

PubMed

Tang, Qian; Li, Zai-Yong; Wei, Yu-Bo; Yang, Xia; Liu, Lan-Tao; Gong, Cheng-Bin; Ma, Xue-Bing; Lam, Michael Hon-Wah; Chow, Cheuk-Fai

2016-09-01

A photoresponsive surface molecularly imprinted polymer for uric acid in physiological fluids was fabricated through a facile and effective method using bio-safe and biocompatible ZnO nanorods as a support. The strategy was carried out by introducing double bonds on the surface of the ZnO nanorods with 3-methacryloxypropyltrimethoxysilane. The surface molecularly imprinted polymer on ZnO nanorods was then prepared by surface polymerization using uric acid as template, water-soluble 5-[(4-(methacryloyloxy)phenyl)diazenyl]isophthalic acid as functional monomer, and triethanolamine trimethacryl ester as cross-linker. The surface molecularly imprinted polymer on ZnO nanorods showed good photoresponsive properties, high recognition ability, and fast binding kinetics toward uric acid, with a dissociation constant of 3.22×10(-5)M in aqueous NaH2PO4 buffer at pH=7.0 and a maximal adsorption capacity of 1.45μmolg(-1). Upon alternate irradiation at 365 and 440nm, the surface molecularly imprinted polymer on ZnO nanorods can quantitatively uptake and release uric acid. Copyright © 2016 Elsevier B.V. All rights reserved.

Hydrothermal route to VO2 (B) nanorods: controlled synthesis and characterization

NASA Astrophysics Data System (ADS)

Song, Shaokun; Huang, Qiwei; Zhu, Wanting

2017-10-01

One-dimensional vanadium dioxides have attracted intensive attention owing to their distinctive structure and novel applications in catalysis, high energy lithium-ion batteries, chemical sensors/actuators and electrochemical devices etc. In this paper, large-scale VO2 (B) nanorods have been successfully synthesized via a versatile and environment friendly hydrothermal strategy using V2O5 as vanadium source and carbohydrates/alcohols as reductant. The obtained samples are characterized by XRD, FT-IR, TEM, and XPS techniques to investigate the effects of chemical parameters such as reductants, temperature, and time of synthesis on the structure and morphology of products. Results show that pure B phase VO2 with homogeneous nanorod-like morphology can be prepared easily at 180 °C for 3 days with glycerol as reluctant. Typically, the nanorod-like products are 0.5-1 μm long and 50 nm width. Furthermore, it is also confirmed that the products are consisted of VO2, corresponding to the B phase. More importantly, this novel approach is efficient, free of any harmful solvents and surfactants. Therefore, this efficient, green, and cost-saving route will have great potential in the large-scale fabrication of 1D VO2 (B) nanorods from the economic and environmental point of view.

Enhanced room temperature gas sensing of aligned Mn3O4 nanorod assemblies functionalized by aluminum anodic membranes.

PubMed

John, Neetha; Thomas, Paulose; Divya, K V; Abraham, K E

2018-08-17

The study includes a conductometric chemical sensor design using aligned Mn 3 O 4 nanorods. Nanostructuring is an emerging field of prominence due to its capacity to introduce unprecedented properties in materials with potential applications. A hydrothermally prepared in situ Mn 3 O 4 sample appears with an urchin rod-like morphology, which changes to a spherical shape upon annealing. An aluminum anodic membrane/template (AAO) is used for the growth of the nanorods and also as a medium to support the sensor. The aligned Mn 3 O 4 nanorods are formed in the pores of the AAO by vacuum infiltration approach, which is later on annealed. The gold electrical contacts are deposited on the top or bottom ends of the Mn 3 O 4 -embedded AAO to ensure conductometric sensing along the length of the Mn 3 O 4 nanorods. In comparison to the Mn 3 O 4 film-based sensor, the Mn 3 O 4 nanorods in the AAO template have enhanced sensitivity for detecting ethanol and acetone vapor at room temperature. The novel property observed is a result of the large surface area and number of oxygen vacancies of the uniformly aligned and parallel assemblies of the nanorods. The sensor exhibits the lowest response time at 4 s for ethanol and 2 s for acetone at room temperature with a concentration of 50 ppm. The response time is 7 and 5 s, respectively, for 25 ppm. The maximum sensitivities of the sensor at room temperature for ethanol and acetone gases are 67% and 68%, respectively, for 50 ppm concentration. The growth mechanism of the aligned nanorods formed in the AAO template is well established through FESEM analysis. The XPS and HRTEM study give additional evidence for the presence of oxidation states and structure of the prepared nanostructures, respectively.

Collective alignment of nanorods in thin Newtonian films

NASA Astrophysics Data System (ADS)

Gu, Yu; Burtovyy, Ruslan; Townsend, James; Owens, Jeffery; Luzinov, Igor; Kornev, Konstantin

2013-11-01

We provide a complete analytical description of the alignment kinetics of magnetic nanorods in magnetic field. Nickel nanorods were formed by template electrochemical deposition in alumina membranes from a dispersion in a water-glycerol mixture. To ensure uniformity of the dispersion, the surface of the nickel nanorods was covered with polyvinylpyrrolidone (PVP). A 40-70 nm coating prevented aggregation of nanoroda. These modifications allowed us to control alignment of the nanorods in a magnetic field and test the proposed theory. An orientational distribution function of nanorods was introduced. We demonstrated that the 0.04% volume fraction of nanorods in the glycerol-water mixture behaves as a system of non-interacting particles. However, the kinetics of alignment of a nanorod assembly does not follow the predictions of the single-nanorod theory. The distribution function theory explains the kinetics of alignment of a nanorod assembly and shows the significance of the initial distribution of nanorods in the film. It can be used to develop an experimental protocol for controlled ordering of magnetic nanorods in thin films. This work was supported by the Air Force Office of Scientific Research, Grant numbers FA9550-12-1-0459 and FA8650-09-D-507 5900.

Synthesis of ZnO nanorods and observation of resistive switching memory in ZnO based polymer nanocomposites

NASA Astrophysics Data System (ADS)

Nair, Manjula G.; Malakar, Meenakshi; Mohapatra, Saumya R.; Chowdhury, Avijit

2018-05-01

This research reports the observation of bipolar resistive switching memory in ZnO nanorod based polymer nanocomposites. We synthesized ZnO nanorods by wet-chemical method and characterized them using XRD, UV-VIS spectroscopy and SEM. The synthesized materials have hexagonal ZnO phase with grain size of 24 nm and having strong orientation along (101) direction as observed from XRD. The SEM micrograph confirms the formation of ZnO nanorods with diameter in the range of 10 to 20 nm and length of the order of 1 µm. From optical absorption spectra the band gap is estimated to be 2.42 eV. ZnO nanorods were dispersed in PVDF-HFP polymer matrix to prepare the nanocomposite. This nanocomposite was used as active layer in the devices having sandwich structure of ITO/PVDF-HFP+ZnO nanorods/Al. Bipolar non-volatile memory was observed with ON-OFF resistance ratio of the order of 103 and with a wide voltage window of 2.3V. The switching mechanism could be due to the trapping and de-trapping of electrons by the ZnO nanorods in the nanocomposite during ON and OFF states respectively.

Reduced graphene oxide-induced recrystallization of NiS nanorods to nanosheets and the improved Na-storage properties.

PubMed

Pan, Qin; Xie, Jian; Zhu, Tiejun; Cao, Gaoshao; Zhao, Xinbing; Zhang, Shichao

2014-04-07

Preparation of two-dimensional (2D) graphene-like materials is currently an emerging field in materials science since the discovery of single-atom-thick graphene prepared by mechanical cleavage. In this work, we proposed a new method to prepare 2D NiS, where reduced graphene oxide (rGO) was found to induce the recrystallization of NiS from nanorods to nanosheets in a hydrothermal process. The process and mechanism of recrystallization have been clarified by various characterization techniques, including scanning electron microscopy (SEM), transmission electron microscopy (TEM), energy dispersive X-ray spectroscopy (EDS) mapping, and X-ray photoelectron spectroscopy (XPS). The characterization of ex situ NiS/rGO products by SEM and EDS mapping indicates that the recrystallization of NiS from nanorods to nanosheets is realized actually through an exfoliation process, while the characterization of in situ NiS/rGO products by SEM, TEM, and EDS mapping reveals the exfoliation process. The XPS result demonstrates that hydrothermally assisted chemical bonding occurs between NiS and rGO, which induces the exfoliation of NiS nanorods into nanosheets. The obtained NiS/rGO composite shows promising Na-storage properties.

Microstructure evolution of zinc oxide films derived from dip-coating sol-gel technique: formation of nanorods through orientation attachment.

PubMed

Huang, Nan; Sun, Chao; Zhu, Mingwei; Zhang, Bin; Gong, Jun; Jiang, Xin

2011-07-01

ZnO:Al thin films with Al incorporation of 0-20 at.% were deposited through the sol-gel technique. Such a film undergoes a significant microstructure development, from columnar to granular structures and then nanorod arrays with increasing Al content. The important role of Al incorporation level in the microstructure evolution was determined using scanning electron microscopy, x-ray photoelectron spectroscopy and transmission electron microscopy. At low Al level, the transition from columnar to granular grains can be attributed to the coarsening barrier resulting from the introduction of Al into the matrix. However, oriented structures of ZnO nanorod arrays are formed at a high Al level. TEM investigation reveals that a nanorod with smooth morphology at the top and rough morphology at the bottom has a single-crystalline wurtzite structure, which is the aggregation of nanoparticles of a few nanometers in size formed through the orientation attachment mechanism followed by epitaxial growth on the aggregated particles. Finally, the physical properties of the ZnO films with different degrees of Al concentration are discussed. Such detailed microstructure studies may aid the understanding of the doping effect process on the growth of a film, which is essential to altering its physical or chemical properties.

MnO2 Nanorods Intercalating Graphene Oxide/Polyaniline Ternary Composites for Robust High-Performance Supercapacitors

PubMed Central

Han, Guangqiang; Liu, Yun; Zhang, Lingling; Kan, Erjun; Zhang, Shaopeng; Tang, Jian; Tang, Weihua

2014-01-01

New ternary composites of MnO2 nanorods, polyaniline (PANI) and graphene oxide (GO) have been prepared by a two-step process. The 100 nm-long MnO2 nanorods with a diameter ~20 nm are conformably coated with PANI layers and fastened between GO layers. The MnO2 nanorods incorporated ternary composites electrode exhibits significantly increased specific capacitance than PANI/GO binary composite in supercapacitors. The ternary composite with 70% MnO2 exhibits a highest specific capacitance reaching 512 F/g and outstanding cycling performance, with ~97% capacitance retained over 5000 cycles. The ternary composite approach offers an effective solution to enhance the device performance of metal-oxide based supercapacitors for long cycling applications. PMID:24769835

Low-temperature growth of aligned ZnO nanorods: effect of annealing gases on the structural and optical properties.

PubMed

Umar, Ahmad; Hahn, Yoon-Bong; Al-Hajry, A; Abaker, M

2014-06-01

Aligned ZnO nanorods were grown on ZnO/Si substrate via simple aqueous solution process at low-temperature of - 65 degrees C by using zinc nitrate and hexamethylenetetramine (HMTA). The detailed morphological and structural properties measured by FESEM, XRD, EDS and TEM confirmed that the as-grown nanorods are vertically aligned, well-crystalline possessing wurtzite hexagonal phase and grown along the [0001] direction. The room-temperature photoluminescence spectrum of the grown nanorods exhibited a strong and broad green emission and small ultraviolet emission. The as-prepared ZnO nanorods were post-annealed in nitrogen (N2) and oxygen (O2) environments and further characterized in terms of their morphological, structural and optical properties. After annealing the nanorods exhibit well-crystallinity and wurtzite hexagonal phase. Moreover, by annealing the PL spectra show the enhancement in the UV emission and suppression in the green emission. The presented results demonstrate that simply by post-annealing process, the optical properties of ZnO nanostructures can be controlled.

ZnO:Ag nanorods as efficient photocatalysts: Sunlight driven photocatalytic degradation of sulforhodamine B

NASA Astrophysics Data System (ADS)

Raji, R.; K. S., Sibi; K. G., Gopchandran

2018-01-01

Visible light responsive highly photocatalytic ZnO:Ag nanorods with varying Ag concentration were synthesized via co-precipitation method. X-ray diffraction analysis and high resolution transmission electron microscopy investigations confirmed the hexagonal wurtzite phase for these ZnO:Ag nanorods with preferential growth along the (101) plane. Raman shift and luminescence measurements indicated that the incorporation of Ag influences the lattice vibrational modes; there by causing distortion in lattice, inducing silent vibrational modes and emission behavior by quenching of both the band edge and visible emissions respectively. The photocatalytic performance of these nanorods as catalysts was tested by observing the photodegradation of a representative dye pollutant, viz., sulforhodamine B under sunlight irradiation. Photocatalytic performance was evaluated by determining the rate of reaction kinetics, photodegradation efficiency and mineralization efficiency. A high rate constant of 0.552 min-1, chemical oxygen demand value of 5.8 ppm and a mineralization efficiency of 94% were obtained when ZnO: Ag nanorods with an Ag content of 1.5 at.% were used as catalysts. The observed increase in photocatalytic efficiency with Ag content in ZnO:Ag nanorods is attributed to the electron scavenging action of silver, Schottky barrier between the Ag and ZnO interface and the better utilization of sunlight due to enhanced absorption due to plasmons in the visible region. BET analysis indicated that silver doping causes effective surface area of nanorods to increase, which in turn increases the photocatalytic efficiency. The possible mechanism for degradation of dye under sunlight irradiation is described with a schematic and the photostability of the ZnO:Ag nanorods were also tested through five repetitive cycles. This work suggests that the prepared ZnO:Ag nanorods are excellent reusable photocatalysts for the degradation of toxic organic waste in water, which causes severe

Semiconductor gas sensor based on tin oxide nanorods prepared by plasma-enhanced chemical vapor deposition with postplasma treatment

DOE Office of Scientific and Technical Information (OSTI.GOV)

Huang Hui; Tan, O.K.; Lee, Y.C.

2005-10-17

SnO{sub 2} thin films were deposited by radio-frequency inductively coupled plasma-enhanced chemical vapor deposition. Postplasma treatments were used to modify the microstructure of the as-deposited SnO{sub 2} thin films. Uniform nanorods with dimension of null-set 7x100 nm were observed in the plasma-treated films. After plasma treatments, the optimal operating temperature of the plasma-treated SnO{sub 2} thin films decreased by 80 deg. C, while the gas sensitivity increased eightfold. The enhanced gas sensing properties of the plasma-treated SnO{sub 2} thin film were believed to result from the large surface-to-volume ratio of the nanorods' tiny grain size in the scale comparable tomore » the space-charge length and its unique microstructure of SnO{sub 2} nanorods rooted in SnO{sub 2} thin films.« less

Plasma treatment of p-GaN/n-ZnO nanorod light-emitting diodes

NASA Astrophysics Data System (ADS)

Leung, Yu Hang; Ng, Alan M. C.; Djurišic, Aleksandra B.; Chan, Wai Kin; Fong, Patrick W. K.; Lui, Hsien Fai; Surya, Charles

2014-03-01

Zinc oxide (ZnO) is a material of great interest for short-wavelength optoelectronic applications due to its wide band gap (3.37 eV) and high exciton binding energy (60 meV). Due to the difficulty in stable p-type doping of ZnO, other p-type materials such as gallium nitride (GaN) have been used to form heterojunctions with ZnO. p-GaN/n-ZnO heterojunction devices, in particular light-emitting diodes (LED) have been extensively studied. There was a huge variety of electronic properties and emission colors on the reported devices. It is due to the different energy alignment at the interface caused by different properties of the GaN layer and ZnO counterpart in the junction. Attempts have been made on modifying the heterojunction by various methods, such as introducing a dielectric interlayer and post-growth surface treatment, and changing the growth methods of ZnO. In this study, heterojunction LED devices with p-GaN and ZnO nanorods array are demonstrated. The ZnO nanorods were grown by a solution method. The ZnO nanorods were exposed to different kinds of plasma treatments (such as nitrogen and oxygen) after the growth. It was found that the treatment could cause significant change on the optical properties of the ZnO nanorods, as well as the electronic properties and light emissions of the resultant LED devices.

GaN based nanorods for solid state lighting

NASA Astrophysics Data System (ADS)

Li, Shunfeng; Waag, Andreas

2012-04-01

In recent years, GaN nanorods are emerging as a very promising novel route toward devices for nano-optoelectronics and nano-photonics. In particular, core-shell light emitting devices are thought to be a breakthrough development in solid state lighting, nanorod based LEDs have many potential advantages as compared to their 2 D thin film counterparts. In this paper, we review the recent developments of GaN nanorod growth, characterization, and related device applications based on GaN nanorods. The initial work on GaN nanorod growth focused on catalyst-assisted and catalyst-free statistical growth. The growth condition and growth mechanisms were extensively investigated and discussed. Doping of GaN nanorods, especially p-doping, was found to significantly influence the morphology of GaN nanorods. The large surface of 3 D GaN nanorods induces new optical and electrical properties, which normally can be neglected in layered structures. Recently, more controlled selective area growth of GaN nanorods was realized using patterned substrates both by metalorganic chemical vapor deposition (MOCVD) and by molecular beam epitaxy (MBE). Advanced structures, for example, photonic crystals and DBRs are meanwhile integrated in GaN nanorod structures. Based on the work of growth and characterization of GaN nanorods, GaN nanoLEDs were reported by several groups with different growth and processing methods. Core/shell nanoLED structures were also demonstrated, which could be potentially useful for future high efficient LED structures. In this paper, we will discuss recent developments in GaN nanorod technology, focusing on the potential advantages, but also discussing problems and open questions, which may impose obstacles during the future development of a GaN nanorod based LED technology.

Solid state green synthesis and catalytic activity of CuO nanorods in thermal decomposition of potassium periodate

NASA Astrophysics Data System (ADS)

Patel, Vinay Kumar; Bhattacharya, Shantanu

2017-09-01

The present study reports a facile solid state green synthesis process using the leaf extracts of Hibiscus rosa-sinensis to synthesize CuO nanorods with average diameters of 15-20 nm and lengths up to 100 nm. The as-synthesized CuO nanorods were characterized by x-ray diffraction, Fourier transform infrared spectroscopy, transmission electron microscopy and selected area electron diffraction. The formation mechanism of CuO nanorods has been explained by involving the individual role of amide I (amino groups) and carboxylate groups under excess hydroxyl ions released from NaOH. The catalytic activity of CuO nanorods in thermal decomposition of potassium periodate microparticles (µ-KIO4) microparticles was studied by thermo gravimetric analysis measurement. The original size (~100 µm) of commercially procured potassium periodate was reduced to microscale length scale to about one-tenth by PEG200 assisted emulsion process. The CuO nanorods prepared by solid state green route were found to catalyze the thermal decomposition of µ-KIO4 with a reduction of 18 °C in the final thermal decomposition temperature of potassium periodate.

Highly sensitive and simple SERS substrate based on photochemically generated carbon nanotubes-gold nanorods hybrids.

PubMed

Caires, A J; Vaz, R P; Fantini, C; Ladeira, L O

2015-10-01

We report a simple and easy formation of hybrids between multi-wall carbon nanotubes and gold nanorods by one-pot in situ photochemical synthesis. Measurements of surface-enhanced Raman scattering (SERS) through the effect "coffee ring" in visible and near infrared (NIR) show high sensitivity with detection of nanomolar concentrations of aromatic dyes. The formation of nanocomposites between carbon nanotubes and gold nanorods without chemical binders simplifies the preparation. Photochemical synthesis is an advance over the techniques previously published. Copyright © 2015 Elsevier Inc. All rights reserved.

Synthesis of highly efficient antibacterial agent Ag doped ZnO nanorods: Structural, Raman and optical properties

DOE Office of Scientific and Technical Information (OSTI.GOV)

Jan, Tariq; Iqbal, Javed, E-mail: javed.saggu@iiu.edu.pk; Ismail, Muhammad

Here, synthesis, structural, morphological, Raman, optical properties and antibacterial activity of undoped and Ag doped ZnO nanorods by chemical co-precipitation technique have been reported. Structural analysis has revealed that Ag doping cannot deteriorate the structure of ZnO and wurtzite phase is maintained. Lattice constants are found to be decreased with the Ag doping. Fourier transform infrared and Raman spectroscopy also confirm the X-ray diffraction results. Scanning electron microscopy results have demonstrated the formation of ZnO nanorods with average diameter and length of 96 nm and 700 nm, respectively. Raman spectroscopy results suggest that the Ag doping enhances the number of defects inmore » ZnO crystal. It has been found from optical study that Ag doping results in positional shift of band edge absorption peak. This is attributed to the successful incorporation of Ag dopant into ZnO host matrix. The antibacterial activity of prepared nanorods has been determined by two different methods and compared to that of undoped ZnO nanorods. Ag doped ZnO nanorods exhibit excellent antibacterial activity as compared to that of undoped ZnO nanorods. This excellent antibacterial activity may be attributed to the presence of oxygen vacancies and Zn{sup 2+} interstitial defects. Our preliminary findings suggest that Ag doped ZnO nanorods can be used externally to control the spreading of infections related with tested bacterial strains.« less

1D-TlInSe2: Band Structure, Dielectric Function and Nanorods

NASA Astrophysics Data System (ADS)

Mamedov, Nazim; Wakita, Kazuki; Akita, Seiji; Nakayama, Yoshikazu

2005-01-01

Linear combination of atomic orbitals (LCAO) analysis of the electronic band states has been completed for one-dimensional (1D) TlInSe2 having rod-like ground state shape of bulky crystal. The total scenario of the occurrence of the band states from the atomic states has been established. According to this scenario, in dipole approximation the optical transitions at band gap (point T of Brillouin zone) are either entirely forbidden or allowed for T2-T10 transitions in e\\perpc configuration provided that either initial or terminate state has T2 symmetry and both are Se-like. As a whole, the obtained results on the electronic spectrum, including dielectric function, are applicable to all obtained 1D-TlInSe2 nanorods which were as thin as 30--50 nm in cross-section, and apparently preserved tetragonal crystal structure of bulky material. The thermal instabilities developing already in bulky samples of 1D-TlInSe2 are considered to be an ultimate source of the nanoparticles emerging in plenty during nanorods preparation. The nanoplates of a chemically similar but 2D material, TlInS2, are demonstrated for comparison to show the absence of nanoparticles in that case. A possibility of nanoparticle preparation using laser excited coherent phonon trains in the nanorods of 1D-TlInSe2 is figured out.

The Synthesis and Characterization of Cerium Carbonate Hydroxide Nanorods as an Anode for Lithium-Ion Batteries

NASA Astrophysics Data System (ADS)

Zhou, Yining; Liu, Hefen; Liu, Jianqiang; Liu, Haowen

2018-03-01

Nanorods cerium carbonate hydroxide, CeCO3OH, was synthesized through a low-temperature reaction route. The data of x-ray diffraction and scanning electron microscopy revealed that the as-prepared samples were CeCO3OH nanorods. The diameters of the nanorods were in the range of 50-100 nm, and the lengths were around 300-500 nm. As an anode of a lithium ion battery, the charge-discharge capacity, cyclability and lithium-ion diffusion kinetics of CeCO3OH nanorods were investigated. The calculated lithium ion diffusion coefficient was 1.36 × 10-19 cm2 s-1. The initial discharge capacity was about 621.6 mA h g-1 at 0.2 mA cm-2 in 0.05-2.5 V. After 100 cycles, the discharge capacity stabilized at about 362 mA h g-1 and the Coulombic efficiency was nearly 98%, indicating the potential application in anodes of lithium-ion batteries.

Side-detecting optical fiber coated with Zn(OH)2 nanorods for ultraviolet sensing applications

NASA Astrophysics Data System (ADS)

Azad, S.; Parvizi, R.; Sadeghi, E.

2017-09-01

This paper presents an improved coupling efficiency and side detecting of UV radiation induced by light scattering and luminescent features of Zn(OH)2 nanorods coated multimode optical fibers. Uniform and high density Zn(OH)2 nanorods were grown hydrothermally on the core of chemically etched multimode optical fibers. The prepared samples were characterized through x-ray diffraction patterns, scanning electron microscopy and photoluminescence spectroscopy. The detecting technique was based on the intensity modulation of the side coupled light through the Zn(OH)2 nanorods. A simple and cost-effective UV radiation detecting setup has been designed. Experimentally estimated coupling efficiency of the proposed setup was obtained near 11%. The proposed device exhibited stable and reversible responses with a fast rising and decaying time of about 1.4 s and 0.85 s, respectively.

Large-scale synthesis of water-soluble luminescent hydroxyapatite nanorods for security printing.

PubMed

Chen, Xiaohu; Jin, Xiaoying; Tan, Junjun; Li, Wei; Chen, Minfang; Yao, Lan; Yang, Haitao

2016-04-15

Luminescent hydroxyapatite nanoparticles, which have excellent biocompatibility, excellent photostability, and strong fluorescence, have received increasing attention as bioprobes in cell imaging. However, they are also excellent candidates for use in ink-jet security printing. Successful products for related applications usually require highly crystalline, mono-dispersible hydroxyapatite nanorods with good colloidal stability and high fluorescence in aqueous media. These requirements are hard to simultaneously satisfy using most synthetic methods. In this paper, we report a simple and versatile hydrothermal method that incorporates the use of sodium citrate to prepare water-dispersible Eu(3+)-doped hydroxyapatite nanorods. The hydroxyapatite nanorods obtained using this method are highly crystalline rod-shaped particles with an average length of 50-80 nm and an average diameter of 15-30 nm. Dispersions of these hydroxyapatite nanorods, which are transparent with a slightly milky color under natural light and a bright red color when excited with 241 nm UV light, display zeta potentials of -35 mV and hydrodynamic diameters of 120 nm. These dispersions remain colloidally stable for a few months. Dispersions with these properties could be easily applied to security printing for confidential information storage and anti-counterfeiting technologies. Copyright © 2016 Elsevier Inc. All rights reserved.

Influence of Sn ion doping on the photocatalytic performance of V2O5 nanorods prepared by hydrothermal method

NASA Astrophysics Data System (ADS)

Rajeshwari, S.; Santhosh Kumar, J.; Rajendrakumar, R. T.; Ponpandian, N.; Thangadurai, P.

2018-02-01

Pure and different concentrations of Sn4+ doped V2O5 (Sn:V2O5) nanorods were synthesized by hydrothermal method. The Sn:V2O5 nanorods obtained were orthorhombic in structure. No secondary phase was observed up to 10% of Sn doping, but beyond that, there evolved a secondary phase of SnO2. Microstructural analysis revealed the morphology of V2O5 as nanorods and platelets like structure. Presence of V, O and Sn elements in the samples was confirmed by energy dispersive spectroscopy. The V2O5 nanorods have shown a strong absorption in the visible region and the band gap energy was obtained to be varying from 2.21 to 2.26 eV as a function of Sn ion doping. Photocatalytic studies on methylene blue (MB) under visible light irradiation showed that the 3% Sn:V2O5 had effectively degraded MB up to a maximum degradation of 96% and further increase in Sn content had decreased the photodegradation due to higher recombination rate of photogenerated electrons. The mechanism of photodegradation was completely understood and the OH· radicals have played a dominant role in the photodegradation of the organic dyes.

Preparation of zeolite nanorods by corona discharge plasma for degradation of phenazopyridine by heterogeneous sono-Fenton-like process.

PubMed

Khataee, Alireza; Rad, Tannaz Sadeghi; Vahid, Behrouz; Khorram, Sirous

2016-11-01

The plasma-modified clinoptilolite (PMC) nanorods were prepared from natural clinoptilolite (NC) utilizing environmentally-friendly corona discharge plasma. The PMC and NC were characterized by XRD, FT-IR, SEM, EDX, XPS and BET, which confirmed the nanocatalyst formation. The catalytic performance of the PMC in the heterogeneous sono-Fenton-like process was greater than the NC for treatment of phenazopyridine (PhP). The desired amounts were obtained for experimental parameters including initial pH (5), PMC dosage (2g/L), K2S2O8 concentration (2mmol/L), ultrasonic power (300W) and PhP concentration (10mg/L). Reactive oxygen species scavengers decreased the removal efficiency of the PhP. The treatment process followed pseudo-first order kinetic and seven degradation intermediates were identified by the GC-MS technique. Copyright © 2016 Elsevier B.V. All rights reserved.

Novel hybrid light-emitting devices based on MAPbBr3 nanoplatelets:PVK nanocomposites and zinc oxide nanorod arrays

NASA Astrophysics Data System (ADS)

Wang, Szu-Ping; Chang, Chun-Kai; Yang, Sheng-Hsiung; Chang, Che-Yu; Chao, Yu-Chiang

2018-01-01

In this research, we demonstrate inverted perovskite light-emitting devices (PeLEDs) based on zinc oxide nanorod arrays (ZnO NAs) as the electron transport layer and methylammonium lead bromide nanoplatelets (MAPbBr3 NPLs) as the emissive material for the first time. The polyethyleneimine ethoxylated (PEIE) was inserted between the ZnO NAs and the MAPbBr3 NPLs layer to reduce the energy barrier and improve the electron injection efficiency. Besides, different weight ratios of poly(N-vinylcarbazole) (PVK) were blended with MAPbBr3 NPLs to make evenly dispersed nanocomposite films, thereby enhancing the performance of devices. Meanwhile, the photoluminescence of MAPbBr3 NPLs:PVK nanocomposite film was increased due to reduced self-quenching and prolonged carrier lifetime. Inverted PeLEDs with the configuration of ITO/PEIE-modified ZnO NAs/MAPbBr3 NPLs:PVK/TFB/Au were fabricated and evaluated, using TFB as the hole transport layer. The current density of the devices containing PVK matrix was significantly suppressed compared to those without PVK. Herein, the best device revealed a max brightness of 495 cd m-2 and a low turn-on voltage of 3.1 V that shows potential use in light-emitting applications.

Effect of Surface and Defect Chemistry on the Photocatalytic Properties of Intentionally Defect-Rich ZnO Nanorod Arrays.

PubMed

Kegel, Jan; Zubialevich, Vitaly Z; Schmidt, Michael; Povey, Ian M; Pemble, Martyn E

2018-05-30

Due to the abundance of intrinsic defects in zinc oxide (ZnO), the material properties are often governed by same. Knowledge of the defect chemistry has proven to be highly important, especially in terms of the photocatalytic degradation of pollutants. Given the fact that defect-free materials or structures exhibiting only one type of defect are extremely difficult to produce, it is necessary to evaluate what influence various defects may have when present together in the material. In this study, intentionally defect-rich ZnO nanorod (NR) arrays are grown using a simple low-temperature solution-based growth technique. Upon changing the defect chemistry using rapid thermal annealing (RTA) the material properties are carefully assessed and correlated to the resulting photocatalytic properties. Special focus is put on the investigation of these properties for samples showing strong orange photoluminescence (PL). It is shown that intense orange emitting NR arrays exhibit improved dye-degradation rates under UV-light irradiation. Furthermore, strong dye-adsorption has been observed for some samples. This behavior is found to stem from a graphitic surface structure (e.g., shell) formed during RTA in vacuum. Since orange-luminescent samples also exhibit an enhancement of the dye adsorption a possible interplay and synergy of these two defects is elucidated. Additionally, evidence is presented suggesting that in annealed ZnO NRs structural defects may be responsible for the often observed PL emission at 3.31 eV. However, a clear correlation with the photocatalytic properties could not be established for these defects. Building on the specific findings presented here, this study also presents some more general guidelines which, it is suggested, should be employed when assessing the photocatalytic properties of defect-rich ZnO.

Control of ZnO Nanorod Defects to Enhance Carrier Transportation in p-Cu₂O/i-ZnO Nanorods/n-IGZO Heterojunction.

PubMed

Ke, Nguyen Huu; Trinh, Le Thi Tuyet; Mung, Nguyen Thi; Loan, Phan Thi Kieu; Tuan, Dao Anh; Truong, Nguyen Huu; Tran, Cao Vinh; Hung, Le Vu Tuan

2017-01-01

The p-Cu₂O/i-ZnO nanorods/n-IGZO heterojunctions were fabricated by electrochemical and sputtering method. ZnO nanorods were grown on conductive indium gallium zinc oxide (IGZO) thin film and then p-Cu₂O layer was deposited on ZnO nanorods to form the heterojunction. ZnO nanorods play an important role in carrier transport mechanisms and performance of the junction. The changing of defects in ZnO nanorods by annealing samples in air and vacuum have studied. The XRD, photoluminescence (PL) spectroscopy, and FTIR were used to study about structure, and defects in ZnO nanorods. The SEM, i–V characteristics methods were also used to define structure, electrical properties of the heterojunctions layers. The results show that the defects in ZnO nanorods affected remarkably on performance of heterojunctions of solar cells.

Preparation and regulating cell adhesion of anion-exchangeable layered double hydroxide micropatterned arrays.

PubMed

Yao, Feng; Hu, Hao; Xu, Sailong; Huo, Ruijie; Zhao, Zhiping; Zhang, Fazhi; Xu, Fujian

2015-02-25

We describe a reliable preparation of MgAl-layered double hydroxide (MgAl-LDH) micropatterned arrays on gold substrate by combining SO3(-)-terminated self-assembly monolayer and photolithography. The synthesis route is readily extended to prepare LDH arrays on the SO3(-)-terminated polymer-bonded glass substrate amenable for cell imaging. The anion-exchangeable MgAl-LDH micropattern can act both as bioadhesive region for selective cell adhesion and as nanocarrier for drug molecules to regulate cell behaviors. Quantitative analysis of cell adhesion shows that selective HepG2 cell adhesion and spreading are promoted by the micropatterned MgAl-LDH, and also suppressed by methotrexate drug released from the LDH interlayer galleries.

Self-propelled micromotors based on Au-mesoporous silica nanorods

NASA Astrophysics Data System (ADS)

Wang, Ying-Shuai; Xia, Hong; Lv, Chao; Wang, Lei; Dong, Wen-Fei; Feng, Jing; Sun, Hong-Bo

2015-07-01

Here, a chemical powered micromotor from the assembly of Au-SiO2 nanorods is presented. This new micromotor can be propelled efficiently by hydrogen bubbles generated from a hydrolysis reaction of aqueous NaBH4 and KBH4 and by oxygen bubbles produced by decomposition of H2O2. The monodisperse Au nanoparticles in mesoporous silica particles could catalyze the decomposition of two different kinds of fuels and produce bubbles. High speeds of 80 μm s-1 and recycles of more than 30 times are achieved in both NaBH4 and H2O2 media. Locomotion and rolling forms of movement were found. The locomotion forms can be obtained in a larger proportion by patterning the Au-SiO2 nanorods and a PDMS membrane. These micromotors that use multiple fuel sources to power them offer a broader scope of preparation and show considerable promise for diverse applications of nanomotors in different chemical environments.Here, a chemical powered micromotor from the assembly of Au-SiO2 nanorods is presented. This new micromotor can be propelled efficiently by hydrogen bubbles generated from a hydrolysis reaction of aqueous NaBH4 and KBH4 and by oxygen bubbles produced by decomposition of H2O2. The monodisperse Au nanoparticles in mesoporous silica particles could catalyze the decomposition of two different kinds of fuels and produce bubbles. High speeds of 80 μm s-1 and recycles of more than 30 times are achieved in both NaBH4 and H2O2 media. Locomotion and rolling forms of movement were found. The locomotion forms can be obtained in a larger proportion by patterning the Au-SiO2 nanorods and a PDMS membrane. These micromotors that use multiple fuel sources to power them offer a broader scope of preparation and show considerable promise for diverse applications of nanomotors in different chemical environments. Electronic supplementary information (ESI) available: More electronic microscopy graphs, UV-Vis spectra and N2 adsorption isotherms. See DOI: 10.1039/c5nr02545a

Enzymatic glucose detection using ZnO nanorods on the gate region of AlGaN /GaN high electron mobility transistors

NASA Astrophysics Data System (ADS)

Kang, B. S.; Wang, H. T.; Ren, F.; Pearton, S. J.; Morey, T. E.; Dennis, D. M.; Johnson, J. W.; Rajagopal, P.; Roberts, J. C.; Piner, E. L.; Linthicum, K. J.

2007-12-01

ZnO nanorod-gated AlGaN /GaN high electron mobility transistors (HEMTs) are demonstrated for the detection of glucose. A ZnO nanorod array was selectively grown on the gate area using low temperature hydrothermal decomposition to immobilize glucose oxidase (GOx). The one-dimensional ZnO nanorods provide a large effective surface area with high surface-to-volume ratio and provide a favorable environment for the immobilization of GOx. The AlGaN /GaN HEMT drain-source current showed a rapid response of less than 5s when target glucose in a buffer with a pH value of 7.4 was added to the GOx immobilized on the ZnO nanorod surface. We could detect a wide range of concentrations from 0.5nMto125μM. The sensor exhibited a linear range from 0.5nMto14.5μM and an experiment limit of detection of 0.5nM. This demonstrates the possibility of using AlGaN /GaN HEMTs for noninvasive exhaled breath condensate based glucose detection of diabetic application.

Applications, Surface Modification and Functionalization of Nickel Nanorods

PubMed Central

Schrittwieser, Stefan; Reichinger, Daniela; Schotter, Joerg

2017-01-01

The growing number of nanoparticle applications in science and industry is leading to increasingly complex nanostructures that fulfill certain tasks in a specific environment. Nickel nanorods already possess promising properties due to their magnetic behavior and their elongated shape. The relevance of this kind of nanorod in a complex measurement setting can be further improved by suitable surface modification and functionalization procedures, so that customized nanostructures for a specific application become available. In this review, we focus on nickel nanorods that are synthesized by electrodeposition into porous templates, as this is the most common type of nickel nanorod fabrication method. Moreover, it is a facile synthesis approach that can be easily established in a laboratory environment. Firstly, we will discuss possible applications of nickel nanorods ranging from data storage to catalysis, biosensing and cancer treatment. Secondly, we will focus on nickel nanorod surface modification strategies, which represent a crucial step for the successful application of nanorods in all medical and biological settings. Here, the immobilization of antibodies or peptides onto the nanorod surface adds another functionality in order to yield highly promising nanostructures. PMID:29283415

Optoacoustic response of gold nanorods in soft phantoms using high-power diode laser assemblies at 870 and 905 nm.

PubMed

Leggio, L; Gawali, S; Gallego, D; Rodríguez, S; Sánchez, M; Carpintero, G; Lamela, H

2017-03-01

In the present paper we show the optoacoustic (OA) response of two solutions of gold nanorods dispersed in distilled water (0.8 mg/ml) and hosted in tissue-like phantoms by using small arrays of HPDLs at 870 and 905 nm as excitation sources. The HPDLs are coupled to a 7-to-1 optical fiber bundle with output diameter of 675 μm. Each solution of gold nanorods exhibits an absorption peak close to the operating wavelength, i.e. ~860 nm and ~900 nm, respectively, to optimize the generation of OA signals. The phantoms are made of agar, intralipid and hemoglobin to simulate a soft biological tissue with reduced properties of scattering. Three 3-mm diameter tubes done in the phantoms at different depths (0.9 cm, 1.8 cm, and 2.7 cm) have been filled with gold nanorods. In this way, OA signals with appreciable SNR are generated at different depths in the phantoms. The high OA response exhibited by gold nanorods suggests their application in OA spectroscopy as exogenous contrast agents to detect and monitor emerging diseases like metastasis and arteriosclerotic plaques.

TiO2 nanorods/PMMA copolymer-based nanocomposites: highly homogeneous linear and nonlinear optical material

NASA Astrophysics Data System (ADS)

Sciancalepore, C.; Cassano, T.; Curri, M. L.; Mecerreyes, D.; Valentini, A.; Agostiano, A.; Tommasi, R.; Striccoli, M.

2008-05-01

Original nanocomposites have been obtained by direct incorporation of pre-synthesized oleic acid capped TiO2 nanorods into properly functionalized poly(methyl methacrylate) copolymers, carrying carboxylic acid groups on the repeating polymer unit. The presence of carboxylic groups on the alkyl chain of the host functionalized copolymer allows an highly homogeneous dispersion of the nanorods in the organic matrix. The prepared TiO2/PMMA-co-MA nanocomposites show high optical transparency in the visible region, even at high TiO2 nanorod content, and tunable linear refractive index depending on the nanoparticle concentration. Finally measurements of nonlinear optical properties of TiO2 polymer nanocomposites demonstrate a negligible two-photon absorption and a negative value of nonlinear refractive index, highlighting the potential of the nanocomposite for efficient optical devices operating in the visible region.

Synthesis of mesoporous β-Ga2O3 nanorods using PEG as template: preparation, characterization and photocatalytic properties.

PubMed

Zhao, Weirong; Yang, Yong; Hao, Rui; Liu, Feifei; Wang, Yan; Tan, Min; Tang, Jing; Ren, Daqing; Zhao, Dongye

2011-09-15

Mesoporous wide bandgap semiconductors offer high photocatalytic oxidation and mineralization activities. In this study, mesoporous β-Ga(2)O(3) diamond nanorods with 200-300 nm in diameter and 1.0-1.2 μm in length were synthesized via a urea-based hydrothermal method using polyethylene glycol (PEG) as template agent. The UV photocatalytic oxidation activity of β-Ga(2)O(3) for gaseous toluene was evaluated, and 7 kinds of intermediates were monitored online by a proton transfer reaction mass spectrometry. Photoluminescence spectra manifested that the dosage and molecular weight of PEG are crucial for formation of vacancies and photocatalytic oxidation activities. A PEG-assisted hydrothermal formation mechanism of mesoporous β-Ga(2)O(3) diamond nanorods was proposed. Based on the health risk influence index (η) of the intermediates, the calculated health risks revealed that the β-Ga(2)O(3) nanorods with a η value of 9.6 are much safer than TiO(2) (η = 17.6). Copyright © 2011 Elsevier B.V. All rights reserved.

Assessment of Anisotropic Semiconductor Nanorod and Nanoplatelet Heterostructures with Polarized Emission for Liquid Crystal Display Technology.

PubMed

Cunningham, Patrick D; Souza, João B; Fedin, Igor; She, Chunxing; Lee, Byeongdu; Talapin, Dmitri V

2016-06-28

Semiconductor nanorods can emit linear-polarized light at efficiencies over 80%. Polarization of light in these systems, confirmed through single-rod spectroscopy, can be explained on the basis of the anisotropy of the transition dipole moment and dielectric confinement effects. Here we report emission polarization in macroscopic semiconductor-polymer composite films containing CdSe/CdS nanorods and colloidal CdSe nanoplatelets. Anisotropic nanocrystals dispersed in polymer films of poly butyl-co-isobutyl methacrylate (PBiBMA) can be stretched mechanically in order to obtain unidirectionally aligned arrays. A high degree of alignment, corresponding to an orientation factor of 0.87, was achieved and large areas demonstrated polarized emission, with the contrast ratio I∥/I⊥ = 5.6, making these films viable candidates for use in liquid crystal display (LCD) devices. To some surprise, we observed significant optical anisotropy and emission polarization for 2D CdSe nanoplatelets with the electronic structure of quantum wells. The aligned nanorod arrays serve as optical funnels, absorbing unpolarized light and re-emitting light from deep-green to red with quantum efficiencies over 90% and high degree of linear polarization. Our results conclusively demonstrate the benefits of anisotropic nanostructures for LCD backlighting. The polymer films with aligned CdSe/CdS dot-in-rod and rod-in-rod nanostructures show more than 2-fold enhancement of brightness compared to the emitter layers with randomly oriented nanostructures. This effect can be explained as the combination of linearly polarized luminescence and directional emission from individual nanostructures.

Nanostructured ZnO films with various morphologies prepared by ultrasonic spray pyrolysis and its growing process

NASA Astrophysics Data System (ADS)

Ma, H. L.; Liu, Z. W.; Zeng, D. C.; Zhong, M. L.; Yu, H. Y.; Mikmekova, E.

2013-10-01

Nanostructured ZnO films were prepared by the ultrasonic spray pyrolysis method using Zn(CH3COO)2·2H2O as a precursor. The effects of substrate temperature (Ts) on the morphology and properties were systematically studied. As the Ts increased from 430 °C to 610 °C, the morphology of the film transforms from closed packed nanosheets to dense nanocrystalline film and then to hexagonal nanorod array. The dense film formed at a temperature of 550 °C has the lowest electric resistivity and highest carrier concentration. The optical transmittance for all prepared samples was higher than 90%. The photoluminescence (PL) properties varied with the Ts due to the internal defect difference. The growth mechanism of ZnO film involves island growth and diffusion, which was evident by observing the samples prepared at various times.

Fabrication of Well-Aligned ZnO Nanorods Using a Composite Seed Layer of ZnO Nanoparticles and Chitosan Polymer.

PubMed

Khun, Kimleang; Ibupoto, Zafar Hussain; AlSalhi, Mohamad S; Atif, Muhammad; Ansari, Anees A; Willander, Magnus

2013-09-30

In this study, by taking the advantage of both inorganic ZnO nanoparticles and the organic material chitosan as a composite seed layer, we have fabricated well-aligned ZnO nanorods on a gold-coated glass substrate using the hydrothermal growth method. The ZnO nanoparticles were characterized by the Raman spectroscopic techniques, which showed the nanocrystalline phase of the ZnO nanoparticles. Different composites of ZnO nanoparticles and chitosan were prepared and used as a seed layer for the fabrication of well-aligned ZnO nanorods. Field emission scanning electron microscopy, energy dispersive X-ray, high-resolution transmission electron microscopy, X-ray diffraction, and infrared reflection absorption spectroscopic techniques were utilized for the structural characterization of the ZnO nanoparticles/chitosan seed layer-coated ZnO nanorods on a gold-coated glass substrate. This study has shown that the ZnO nanorods are well-aligned, uniform, and dense, exhibit the wurtzite hexagonal structure, and are perpendicularly oriented to the substrate. Moreover, the ZnO nanorods are only composed of Zn and O atoms. An optical study was also carried out for the ZnO nanoparticles/chitosan seed layer-coated ZnO nanorods, and the obtained results have shown that the fabricated ZnO nanorods exhibit good crystal quality. This study has provided a cheap fabrication method for the controlled morphology and good alignment of ZnO nanorods, which is of high demand for enhancing the working performance of optoelectronic devices.

Fabrication of Well-Aligned ZnO Nanorods Using a Composite Seed Layer of ZnO Nanoparticles and Chitosan Polymer

PubMed Central

Khun, Kimleang; Ibupoto, Zafar Hussain; AlSalhi, Mohamad S.; Atif, Muhammad; Ansari, Anees A.; Willander, Magnus

2013-01-01

In this study, by taking the advantage of both inorganic ZnO nanoparticles and the organic material chitosan as a composite seed layer, we have fabricated well-aligned ZnO nanorods on a gold-coated glass substrate using the hydrothermal growth method. The ZnO nanoparticles were characterized by the Raman spectroscopic techniques, which showed the nanocrystalline phase of the ZnO nanoparticles. Different composites of ZnO nanoparticles and chitosan were prepared and used as a seed layer for the fabrication of well-aligned ZnO nanorods. Field emission scanning electron microscopy, energy dispersive X-ray, high-resolution transmission electron microscopy, X-ray diffraction, and infrared reflection absorption spectroscopic techniques were utilized for the structural characterization of the ZnO nanoparticles/chitosan seed layer-coated ZnO nanorods on a gold-coated glass substrate. This study has shown that the ZnO nanorods are well-aligned, uniform, and dense, exhibit the wurtzite hexagonal structure, and are perpendicularly oriented to the substrate. Moreover, the ZnO nanorods are only composed of Zn and O atoms. An optical study was also carried out for the ZnO nanoparticles/chitosan seed layer-coated ZnO nanorods, and the obtained results have shown that the fabricated ZnO nanorods exhibit good crystal quality. This study has provided a cheap fabrication method for the controlled morphology and good alignment of ZnO nanorods, which is of high demand for enhancing the working performance of optoelectronic devices. PMID:28788336

Hydrothermal Synthesis of Hydroxyapatite Nanorods for Rapid Formation of Bone-Like Mineralization

NASA Astrophysics Data System (ADS)

Hoai, Tran Thanh; Nga, Nguyen Kim; Giang, Luu Truong; Huy, Tran Quang; Tuan, Phan Nguyen Minh; Binh, Bui Thi Thanh

2017-08-01

Hydroxyapatite (HAp) is an excellent biomaterial for bone repair and regeneration. The biological functions of HAp particles, such as biomineralization, cell adhesion, and cell proliferation, can be enhanced when their size is reduced to the nanoscale. In this work, HAp nanoparticles were synthesized by the hydrothermal technique with addition of cetyltrimethylammonium bromide (CTAB). These particles were also characterized, and their size controlled by modifying the CTAB concentration and hydrothermal duration. The results show that most HAp nanoparticles were rod-like in shape, exhibiting the most uniform and smallest size (mean diameter and length of 39 nm and 125 nm, respectively) at optimal conditions of 0.64 g CTAB and hydrothermal duration of 12 h. Moreover, good biomineralization capability of the HAp nanorods was confirmed through in vitro tests in simulated body fluid. A bone-like mineral layer of synthesized HAp nanorods formed rapidly after 7 days. This study shows that highly bioactive HAp nanorods can be easily prepared by the hydrothermal method, being a potential nanomaterial for bone regeneration.

Chelator free gallium-68 radiolabelling of silica coated iron oxide nanorods via surface interactions

NASA Astrophysics Data System (ADS)

Burke, Benjamin P.; Baghdadi, Neazar; Kownacka, Alicja E.; Nigam, Shubhanchi; Clemente, Gonçalo S.; Al-Yassiry, Mustafa M.; Domarkas, Juozas; Lorch, Mark; Pickles, Martin; Gibbs, Peter; Tripier, Raphaël; Cawthorne, Christopher; Archibald, Stephen J.

2015-09-01

The commercial availability of combined magnetic resonance imaging (MRI)/positron emission tomography (PET) scanners for clinical use has increased demand for easily prepared agents which offer signal or contrast in both modalities. Herein we describe a new class of silica coated iron-oxide nanorods (NRs) coated with polyethylene glycol (PEG) and/or a tetraazamacrocyclic chelator (DO3A). Studies of the coated NRs validate their composition and confirm their properties as in vivo T2 MRI contrast agents. Radiolabelling studies with the positron emitting radioisotope gallium-68 (t1/2 = 68 min) demonstrate that, in the presence of the silica coating, the macrocyclic chelator was not required for preparation of highly stable radiometal-NR constructs. In vivo PET-CT and MR imaging studies show the expected high liver uptake of gallium-68 radiolabelled nanorods with no significant release of gallium-68 metal ions, validating our innovation to provide a novel simple method for labelling of iron oxide NRs with a radiometal in the absence of a chelating unit that can be used for high sensitivity liver imaging.The commercial availability of combined magnetic resonance imaging (MRI)/positron emission tomography (PET) scanners for clinical use has increased demand for easily prepared agents which offer signal or contrast in both modalities. Herein we describe a new class of silica coated iron-oxide nanorods (NRs) coated with polyethylene glycol (PEG) and/or a tetraazamacrocyclic chelator (DO3A). Studies of the coated NRs validate their composition and confirm their properties as in vivo T2 MRI contrast agents. Radiolabelling studies with the positron emitting radioisotope gallium-68 (t1/2 = 68 min) demonstrate that, in the presence of the silica coating, the macrocyclic chelator was not required for preparation of highly stable radiometal-NR constructs. In vivo PET-CT and MR imaging studies show the expected high liver uptake of gallium-68 radiolabelled nanorods with no

Preparation of Pt Ag alloy nanoisland/graphene hybrid composites and its high stability and catalytic activity in methanol electro-oxidation

PubMed Central

2011-01-01

In this article, PtAg alloy nanoislands/graphene hybrid composites were prepared based on the self-organization of Au@PtAg nanorods on graphene sheets. Graphite oxides (GO) were prepared and separated to individual sheets using Hummer's method. Graphene nano-sheets were prepared by chemical reduction with hydrazine. The prepared PtAg alloy nanomaterial and the hybrid composites with graphene were characterized by SEM, TEM, and zeta potential measurements. It is confirmed that the prepared Au@PtAg alloy nanorods/graphene hybrid composites own good catalytic function for methanol electro-oxidation by cyclic voltammograms measurements, and exhibited higher catalytic activity and more stability than pure Au@Pt nanorods and Au@AgPt alloy nanorods. In conclusion, the prepared PtAg alloy nanoislands/graphene hybrid composites own high stability and catalytic activity in methanol electro-oxidation, so that it is one kind of high-performance catalyst, and has great potential in applications such as methanol fuel cells in near future. PMID:21982417

Solid-State Dewetting of Gold Aggregates/Islands on TiO2 Nanorod Structures Grown by Oblique Angle Deposition.

PubMed

Liu, Shizhao; Plawsky, Joel L

2017-12-12

A composite film made of a stable gold nanoparticle (NP) array with well-controlled separation and size atop a TiO 2 nanorod film was fabricated via the oblique angle deposition (OAD) technique. The fabrication of the NP array is based on controlled, Rayleigh-instability-induced, solid-state dewetting of as-deposited gold aggregates on the TiO 2 nanorods. It was found that the initial spacing between as-deposited gold aggregates along the vapor flux direction should be greater than the TiO 2 interrod spacing created by 80° OAD to control dewetting and produce NP arrays. A numerical investigation of the process was conducted using a phase-field modeling approach. Simulation results showed that coalescence between neighboring gold aggregates is likely to have caused the uncontrolled dewetting in the 80° deposition, and this could be circumvented if the initial spacing between gold aggregates is larger than a critical value s min . We also found that TiO 2 nanorod tips affect dewetting dynamics differently than planar TiO 2 . The topology of the tips can induce contact line pinning and an increase in the contact angle along the vapor flux direction to the supported gold aggregates. These two effects are beneficial for the fabrication of monodisperse NPs based on Rayleigh-instability-governed self-assembly of materials, as they help to circumvent the undesired coalescence and facilitate the instability growth on the supported material. The findings uncover the application potential of OAD as a new method to fabricate structured films as template substrates to mediate dewetting. The reported composite films would have uses in optical coatings and photocatalytic systems, taking advantage of their ability to combine plasmonic nanostructures within a nanostructured dielectric film.

Composite silicon nanostructure arrays fabricated on optical fibre by chemical etching of multicrystal silicon film.

PubMed

Zuo, Zewen; Zhu, Kai; Ning, Lixin; Cui, Guanglei; Qu, Jun; Huang, Wanxia; Shi, Yi; Liu, Hong

2015-04-17

Integrating nanostructures onto optical fibers presents a promising strategy for developing new-fashioned devices and extending the scope of nanodevices' applications. Here we report the first fabrication of a composite silicon nanostructure on an optical fiber. Through direct chemical etching using an H2O2/HF solution, multicrystal silicon films with columnar microstructures are etched into a vertically aligned, inverted-cone-like nanorod array embedded in a nanocone array. A faster dissolution rate of the silicon at the void-rich boundary regions between the columns is found to be responsible for the separation of the columns, and thus the formation of the nanostructure array. The morphology of the nanorods primarily depends on the microstructure of the columns in the film. Through controlling the microstructure of the as-grown film and the etching parameters, the structural control of the nanostructure is promising. This fabrication method can be extended to a larger length scale, and it even allows roll-to-roll processing.

Optoacoustic sensing of ocular bacterial antigen using targeted gold nanorods

NASA Astrophysics Data System (ADS)

Maswadi, Saher; Page, Leland; Woodward, Lee; Glickman, Randolph D.; Barsalou, Norman

2008-02-01

Bacterial contamination can be detected using a minimally invasive optical method, based on laser-induced optoacoustic spectroscopy, to probe for specific antigens associated with a specific infectious agent. As a model system, we have used a surface antigen (Ag), isolated from Chlamydia trachomatis, and a complementary antibody (Ab). A preparation of 0.2 mg/ml of monoclonal Ab specific to the C. trachomatis surface Ag was conjugated to gold nanorods using standard commercial reagents, in order to produce a targeted contrast agent with a strong optoacoustic signal. The C. trachomatis Ag was absorbed in standard plastic microwells, and the binding of the complementary Ab-nanorod conjugate was tested in an immunoaffinity assay. Optoacoustic signals were elicited from the bound nanorods, using an optical parametric oscillator (OPO) laser system as the optical pump. The wavelength tuneability of the OPO optimized the spectroscopic measurement by exciting the nanorods at their optical absorption maxima. Optoacoustic responses were measured in the microwells using a probe beam deflection technique. Immunoaffinity assays were performed on several dilutions of purified C. trachomatis antigen ranging from 50 μg/ml to 1 pg/ml, in order to determine the detection limit for the optoacoustic-based assay. Only when the antigen was present, and the complementary Ab-NR reagent was introduced into the microwell, was an enhanced optoacoustic signal obtained, which indicated specific binding of the Ab-NR complex. The limit of detection with the current system design is between 1 and 5 pg/ml of bacterial Ag.

In vitro and in vivo studies on laser-activated gold nanorods for applications in photothermal therapies

NASA Astrophysics Data System (ADS)

Pini, Roberto; Ratto, Fulvio; Matteini, Paolo; Centi, Sonia; Rossi, Francesca

2010-04-01

We review our experimental studies on near infrared laser-activated gold nanoparticles in the direct welding of connective tissues. In particular, we discuss the use of gold nanorods excited by diode laser radiation at 810 nm to mediate functional photothermal effects and weld eye's lens capsules and arteries. The preparation of biopolymeric matrices including gold nanorods is described as well, together with preliminary tests for their application in the closure of wounds in vessels and tendons. Finally we mention future perspectives on the use of these nanoparticles for applications in the therapy of cancer.

Facile and Eco-Friendly Synthesis of Finger-Like Co3O4 Nanorods for Electrochemical Energy Storage

PubMed Central

Sun, Shijiao; Zhao, Xiangyu; Yang, Meng; Ma, Liqun; Shen, Xiaodong

2015-01-01

Co3O4 nanorods were prepared by a facile hydrothermal method. Eco-friendly deionized water rather than organic solvent was used as the hydrothermal media. The as-prepared Co3O4 nanorods are composed of many nanoparticles of 30–50 nm in diameter, forming a finger-like morphology. The Co3O4 electrode shows a specific capacitance of 265 F g−1 at 2 mV s−1 in a supercapacitor and delivers an initial specific discharge capacity as high as 1171 mAh g−1 at a current density of 50 mA g−1 in a lithium ion battery. Excellent cycling stability and electrochemical reversibility of the Co3O4 electrode were also obtained. PMID:28347124

An Explanation for Bends of 1-Dimensional Nanorods

NASA Astrophysics Data System (ADS)

Mukaida, Masashi; Ichinose, Ataru; Mele, Paolo; Mtsumoto, Kaname; Horii, Shigeru; Yoshida, Yutaka

Growth of artificial pinning centers (APCs) in YBa2Cu3O7-J (YBCO) films are discussed. The APCs used in this research are BaZrO3 and BaSnO3 nanorods which are reported by Mele et al. TEM images show these nanorods graduallybend accordinglywith approachingtoasurfaceof films. This featureshowedagrowth patternlikeafirework. Weexplainthe featureofthe nanorodsas follows;Atanearlygrowth stage, filmsgrowinalayerbylayergrowth mode. The surface of the films is flat and very smooth. After the early growth stage, the film surface gradually becomes rough, indicating the film grows in a Stranski-Krastanov growth mode. This roughness was caused by a spiral growth of films with manysteps. At the step of YBCO films, nanorod materials such as BaZrO3 are supplied from one direction. Then, the center of nanorods sifts to the same direction of the step flow. Then, the nanorods bend to the edge of the grains in the films. As a grain in spiral growth had a convex surface, nanorods bent to the direction perpendicular to the grain surface. Finally, nanorods in rough grains form firework structures.

Preparation and characterization of bionanocomposite film based on tapioca starch/bovine gelatin/nanorod zinc oxide.

PubMed

Marvizadeh, Mohammad Mehdi; Oladzadabbasabadi, Nazila; Mohammadi Nafchi, Abdorreza; Jokar, Maryam

2017-06-01

To exploring a nano-packaging materials for using as coating or edible films, tapioca starch/gelatin/nanorod ZnO (ZnON) bionanocomposites were prepared via solution casting technique. The effects of nanofiller addition on the mechanical, physicochemical, and crystalline structures, as well as the barrier properties of bionanocomposite films were investigated. X-ray diffraction analysis showed that the bionanocomposite film incorporated with ZnON at a concentration of 3.5% w/w exhibited high intensity peaks compared with control samples. Results of UV-vis spectra analysis showed that incorporation of ZnON into the films can absorb the whole UV light. Tensile strength of the films was increased from 14 to 18MPa whereas elongation at breaks decreased from 18 to 8 percent and oxygen permeability decreased from 151.03 to 91.52cm 3 μm/(m 2 -day) by incorporation of 3.5% ZnON into biopolymer matrix. In summary combined starch/gelatin films supported by ZnON showed better properties compared to starch or gelatin alone. Thus, the bionanocomposite films can be used in food, medicine, and pharmaceutical packaging. Copyright © 2017 Elsevier B.V. All rights reserved.

Direct Low-Temperature Growth of Single-Crystalline Anatase TiO2 Nanorod Arrays on Transparent Conducting Oxide Substrates for Use in PbS Quantum-Dot Solar Cells.

PubMed

Chung, Hyun Suk; Han, Gill Sang; Park, So Yeon; Shin, Hee-Won; Ahn, Tae Kyu; Jeong, Sohee; Cho, In Sun; Jung, Hyun Suk

2015-05-20

We report on the direct growth of anatase TiO2 nanorod arrays (A-NRs) on transparent conducting oxide (TCO) substrates that can be directly applied to various photovoltaic devices via a seed layer mediated epitaxial growth using a facile low-temperature hydrothermal method. We found that the crystallinity of the seed layer and the addition of an amine functional group play crucial roles in the A-NR growth process. The A-NRs exhibit a pure anatase phase with a high crystallinity and preferred growth orientation in the [001] direction. Importantly, for depleted heterojunction solar cells (TiO2/PbS), the A-NRs improve both electron transport and injection properties, thereby largely increasing the short-circuit current density and doubling their efficiency compared to TiO2 nanoparticle-based solar cells.

Anisotropic growth and formation mechanism investigation of 1D ZnO nanorods in spin-coating sol-gel process.

PubMed

Song, Yijian; Zheng, Maojun; Ma, Li; Shen, Wenzhong

2010-01-01

ZnO nanorods are fabricated on glass substrate by spin-coating sol-gel process using non-basic aged solution and annealing. Sample solutions reserved in room temperature for different time (one day, one month, two months and four months) are prepared for the experiment. The morphology study indicates that the aging time has direct influence on the final products. This is verified by the Transmission Electron Microscopy and Photon Correlation Spectroscopy study. Small crystalline nanoparticles would gradually nucleate and aggregate in the sol during the aging process. They act as nucleation site for the secondary crystal growth into nanorods during anneal. Both the size of crystalline particles in the sol and the size of nanorods will grow bigger as the aging time increases. The products' structure and optical property are further studied by X-ray diffraction spectroscopy, Photoluminescence and Raman spectroscopy. This work also helps to further clarify the formation mechanism of ZnO nanorods by solution-based method.

Highly Sensitive and Reproducible SERS Sensor for Biological pH Detection Based on a Uniform Gold Nanorod Array Platform.

PubMed

Bi, Liyan; Wang, Yunqing; Yang, Ying; Li, Yuling; Mo, Shanshan; Zheng, Qingyin; Chen, Lingxin

2018-05-09

Conventional research on surface-enhanced Raman scattering (SERS)-based pH sensors often depends on nanoparticle aggregation, whereas the variability in nanoparticle aggregation gives rise to poor repeatability in the SERS signal. Herein, we fabricated a gold nanorod array platform via an efficient evaporative self-assembly method. The platform exhibits great SERS sensitivity with an enhancement factor of 5.6 × 10 7 and maintains excellent recyclability and reproducibility with relative standard deviation (RSD) values of less than 8%. On the basis of the platform, we developed a highly sensitive bovine serum albumin (BSA)-coated 4-mercaptopyridine (4-MPy)-linked (BMP) SERS-based pH sensor to report pH ranging from pH 3.0 to pH 8.0. The intensity ratio variation of 1004 and 1096 cm -1 in 4-MPy showed excellent pH sensitivity, which decreased as the surrounding pH increased. Furthermore, this BMP SERS-based pH sensor was employed to measure the pH value in C57BL/6 mouse blood. We have demonstrated that the pH sensor has great advantages such as good stability, reliability, and accuracy, which could be extended for the design of point-of-care devices.

A general approach for MFe2O4 (M = Zn, Co, Ni) nanorods and their high performance as anode materials for lithium ion batteries

NASA Astrophysics Data System (ADS)

Wang, Nana; Xu, Huayun; Chen, Liang; Gu, Xin; Yang, Jian; Qian, Yitai

2014-02-01

MFe2O4 (M = Zn, Co, Ni) nanorods are synthesized by a template-engaged reaction, with β-FeOOH nanorods as precursors which are prepared by a hydrothermal method. The final products are characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), and high-resolution transmission electron microscopy (HRTEM). The electrochemical properties of the MFe2O4 (M = Zn, Co, Ni) nanorods are tested as the anode materials for lithium ion batteries. The reversible capacities of 800, 625 and 520 mAh g-1 are obtained for CoFe2O4, ZnFe2O4 and NiFe2O4, respectively, at the high current density of 1000 mA g-1 even after 300 cycles. The superior lithium-storage performances of MFe2O4 (M = Zn, Co, Ni) nanorods can be attributed to the one-dimensional (1D) nanostructure, which can shorten the diffusion paths of lithium ions and relax the strain generated during electrochemical cycling. These results indicate that this method is an effective, simple and general way to prepare good electrochemical properties of 1D spinel Fe-based binary transition metal oxides. In addition, the impact of different reaction temperatures on the electrochemical properties of MFe2O4 nanorods is also investigated.

Solvothermal transformation of a calcium oleate precursor into large-sized highly ordered arrays of ultralong hydroxyapatite microtubes.

PubMed

Lu, Bing-Qiang; Zhu, Ying-Jie; Chen, Feng; Qi, Chao; Zhao, Xin-Yu; Zhao, Jing

2014-06-02

Hydroxyapatite (HAP), a well-known member of the calcium phosphate family, is the major inorganic component of bones and teeth in vertebrates. The highly ordered arrays of HAP structures are of great significance for hard tissue repair and for understanding the formation mechanisms of bones and teeth. However, the synthesis of highly ordered HAP structure arrays remains a great challenge. In this work, inspired by the ordered structure of tooth enamel, we have successfully synthesized three-dimensional bulk materials with large sizes (millimeter scale) that are made of highly ordered arrays of ultralong HAP microtubes (HOAUHMs) by solvothermal transformation of calcium oleate precursor. The core-shell-structured oblate sphere consists of a core that is composed of HAP nanorods and a shell that consists of highly ordered HAP microtube arrays. The prepared HOAUHMs are large: 6.0 mm in diameter and up to 1.4 mm in thickness. With increasing solvothermal reaction time, the HOAUHMs grow larger; the microtubes become more uniform and more ordered. This work provides a new synthetic method for synthesizing highly ordered arrays of uniform HAP ultralong microtubes that are promising for biomedical applications. © 2014 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Scalable Nanostructured Carbon Electrode Arrays for Enhanced Dopamine Detection.

PubMed

Demuru, Silvia; Nela, Luca; Marchack, Nathan; Holmes, Steven J; Farmer, Damon B; Tulevski, George S; Lin, Qinghuang; Deligianni, Hariklia

2018-04-27

Dopamine is a neurotransmitter that modulates arousal and motivation in humans and animals. It plays a central role in the brain "reward" system. Its dysregulation is involved in several debilitating disorders such as addiction, depression, Parkinson's disease, and schizophrenia. Dopamine neurotransmission and its reuptake in extracellular space takes place with millisecond temporal and nanometer spatial resolution. Novel nanoscale electrodes are needed with superior sensitivity and improved spatial resolution to gain an improved understanding of dopamine dysregulation. We report on a scalable fabrication of dopamine neurochemical probes of a nanostructured glassy carbon that is smaller than any existing dopamine sensor and arrays of more than 6000 nanorod probes. We also report on the electrochemical dopamine sensing of the glassy carbon nanorod electrode. Compared with a carbon fiber, the nanostructured glassy carbon nanorods provide about 2× higher sensitivity per unit area for dopamine sensing and more than 5× higher signal per unit area at low concentration of dopamine, with comparable LOD and time response. These glassy carbon nanorods were fabricated by pyrolysis of a lithographically defined polymeric nanostructure with an industry standard semiconductor fabrication infrastructure. The scalable fabrication strategy offers the potential to integrate these nanoscale carbon rods with an integrated circuit control system and with other complementary metal oxide semiconductor (CMOS) compatible sensors.

Ultrafast studies of gold, nickel, and palladium nanorods

NASA Astrophysics Data System (ADS)

Sando, Gerald M.; Berry, Alan D.; Owrutsky, Jeffrey C.

2007-08-01

Steady state and ultrafast transient absorption studies have been carried out for gold, nickel, and palladium high aspect ratio nanorods. For each metal, nanorods were fabricated by electrochemical deposition into ˜6μm thick polycarbonate templates. Two nominal pore diameters(10 and 30nm, resulting in nanorod diameters of about 40 and 60nm, respectively) were used, yielding nanorods with high aspect ratios (>25). Static spectra of nanorods of all three metals reveal both a longitudinal surface plasmon resonance (SPRL) band in the mid-infrared as well as a transverse band in the visible for the gold and larger diameter nickel and palladium nanorods. The appearance of SPRL bands in the infrared for high aspect ratio metal nanorods and the trends in their maxima for the different aspect ratios and metals are consistent with calculations based on the Gans theory. For the gold and nickel samples, time resolved studies were performed with a subpicosecond resolution using 400nm excitation and a wide range of probe wavelengths from the visible to the mid-IR as well as for infrared excitation (near 2000cm-1) probed at 800nm. The dynamics observed for nanorods of both metals and both diameters include transients due to electron-phonon coupling and impulsively excited coherent acoustic breathing mode oscillations, which are similar to those previously reported for spherical and smaller rod-shaped gold nanoparticles. The dynamics we observe are the same within the experimental uncertainty for 400nm and infrared (5μm) excitation probed at 800nm. The transient absorption using 400nm excitation and 800nm probe pulses of the palladium nanorods also reveal coherent acoustic oscillations. The results demonstrate that the dynamics for high aspect ratio metal nanorods are similar to those for smaller nanoparticles.

Self-propelled micromotors based on Au-mesoporous silica nanorods.

PubMed

Wang, Ying-Shuai; Xia, Hong; Lv, Chao; Wang, Lei; Dong, Wen-Fei; Feng, Jing; Sun, Hong-Bo

2015-07-28

Here, a chemical powered micromotor from the assembly of Au-SiO2 nanorods is presented. This new micromotor can be propelled efficiently by hydrogen bubbles generated from a hydrolysis reaction of aqueous NaBH4 and KBH4 and by oxygen bubbles produced by decomposition of H2O2. The monodisperse Au nanoparticles in mesoporous silica particles could catalyze the decomposition of two different kinds of fuels and produce bubbles. High speeds of 80 μm s(-1) and recycles of more than 30 times are achieved in both NaBH4 and H2O2 media. Locomotion and rolling forms of movement were found. The locomotion forms can be obtained in a larger proportion by patterning the Au-SiO2 nanorods and a PDMS membrane. These micromotors that use multiple fuel sources to power them offer a broader scope of preparation and show considerable promise for diverse applications of nanomotors in different chemical environments.

Molten salt-directed synthesis method for LiMn2O4 nanorods as a cathode material for a lithium-ion battery with superior cyclability

NASA Astrophysics Data System (ADS)

Kebede, Mesfin A.; Ozoemena, Kenneth I.

2017-02-01

A molten salt synthesis technique has been used to prepare nanorods of Mn2O3 and single-crystal LiMn2O4 nanorods cathode material with superior capacity retention. The molten salt-directed synthesis involved the use of NaCl as the eutectic melt. The as-synthesized LiMn2O4 nanorods cathode material showed superior electrochemical performance compared to the LiMn2O4 sample obtained via the solid state method. The as-synthesized LiMn2O4 nanorods maintained more than 95% of the initial discharge capacity of 107 mA h g-1 over 100 cycles at a rate of 0.1 C, whereas the LiMn2O4 sample synthesized using the solid state reaction method maintained 88% of the initial discharge capacity of 98 mA h g-1 over 100 cycles at a rate of 0.1 C. Compared to the literature, the molten salt-directed method for the preparation of high-performance LiMn2O4 is simpler and less expensive, with greater potential for industrial scale-up.

Efficient Carrier Multiplication in Colloidal Silicon Nanorods

DOE PAGES

Stolle, Carl Jackson; Lu, Xiaotang; Yu, Yixuan; ...

2017-08-01

In this study, auger recombination lifetimes, absorption cross sections, and the quantum yields of carrier multiplication (CM), or multiexciton generation (MEG), were determined for solvent-dispersed silicon (Si) nanorods using transient absorption spectroscopy (TAS). Nanorods with an average diameter of 7.5 nm and aspect ratios of 6.1, 19.3, and 33.2 were examined. Colloidal Si nanocrystals of similar diameters were also studied for comparison. The nanocrystals and nanorods were passivated with organic ligands by hydrosilylation to prevent surface oxidation and limit the effects of surface trapping of photoexcited carriers. All samples used in the study exhibited relatively efficient photoluminescence. The Auger lifetimesmore » increased with nanorod length, and the nanorods exhibited higher CM quantum yield and efficiency than the nanocrystals with a similar band gap energy E g. Beyond a critical length, the CM quantum yield decreases. Finally, nanorods with the aspect ratio of 19.3 had the highest CM quantum yield of 1.6 ± 0.2 at 2.9E g, which corresponded to a multiexciton yield that was twice as high as observed for the spherical nanocrystals.« less

One-pot synthesis of magnetite nanorods/graphene composites and its catalytic activity toward electrochemical detection of dopamine.

PubMed

Salamon, J; Sathishkumar, Y; Ramachandran, K; Lee, Yang Soo; Yoo, Dong Jin; Kim, Ae Rhan; Gnana Kumar, G

2015-02-15

Magnetite (Fe3O4) nanorods anchored over reduced graphene oxide (rGO) were synthesized through a one-pot synthesis method, where the reduction of GO and in-situ generation of Fe3O4 nanorods occurred concurrently. The average head and tail diameter of Fe3O4 nanorods anchored over the rGO matrix are found to be 32 and 11 nm, respectively, and morphology, structure and diameter of bare Fe3O4 nanorods were not altered even after the composite formation with rGO. The increased structural disorders and decrement in the sp(2) domains stimulated the high electrical conductivity and extended catalytic active sites for the prepared rGO/Fe3O4 nanocomposite. The constructed rGO/Fe3O4/GCE sensor exhibited excellent electrocatalytic activity toward the electrooxidation of dopamine (DA) with a quick response time of 6s, a wide linear range between 0.01 and 100.55 µM, high sensitivity of 3.15 µA µM(-1) cm(-2) and a lower detection limit of 7 nM. Furthermore, the fabricated sensor exhibited a practical applicability in the quantification of DA in urine samples with an excellent recovery rate. The excellent electroanalytical performances and straight-forward, surfactant and template free preparation method construct the rGO/Fe3O4 composite as an extremely promising material for the diagnosis of DA related diseases in biomedical applications. Copyright © 2014 Elsevier B.V. All rights reserved.

Growth process and anticancer properties of gold nanorods.

PubMed

Zhang, Junyan; Wang, Mian; Webster, Thomas J

2017-09-01

Gold nanoparticles have been of great interest because of their unique optical properties, facile synthesis and conjugation. Among various shapes of gold nanoparticles, gold nanorods have been widely studied. They can be conjugated with different molecules for biomedical applications, such as tumor imaging and therapy. However, few researchers have studied the antitumor properties of bare gold nanorods. In this study, unfunctionalized gold nanorods were synthesized and tested on breast tumor cells. Results showed that the aspect ratio of gold nanorods could be easily influenced by both reaction time and the amount of silver nitrate in the growth solution. A new growth process is proposed here based on the UV-Vis spectra and TEM images of gold nanorods at different reaction times. More importantly, cell studies showed that within a certain concentration range, the gold nanorods can selectively kill tumor cells while having limited or little influence on healthy mammalian (dermal fibroblast) cells. Thus, this study shows promise for the use of bare gold nanorods for further study alone or in combination with photothermal treatment. © 2017 Wiley Periodicals, Inc. J Biomed Mater Res Part A: 105A: 2616-2621, 2017. © 2017 Wiley Periodicals, Inc.

Highly crystalline zinc incorporated hydroxyapatite nanorods' synthesis, characterization, thermal, biocompatibility, and antibacterial study

NASA Astrophysics Data System (ADS)

Udhayakumar, Gayathri; Muthukumarasamy, N.; Velauthapillai, Dhayalan; Santhosh, Shanthi Bhupathi

2017-10-01

Highly crystalline zinc incorporated hydroxyapatite (Zn-HAp) nanorods have been synthesized using microwave irradiation method. To improve bioactivity and crystallinity of pure HAp, zinc was incorporated into it. As-synthesized samples were characterized by Fourier transform-infrared spectroscopy (FT-IR), X-ray diffraction, field-emission scanning electron microscopy (FESEM), energy dispersive X-ray analysis (EDAX), high-resolution transmission electron microscopy (HRTEM), and the thermal and crystallinity behavior of Zn-HAp nanoparticle were studied by thermogravimetry (TGA) and differential scanning calorimetry (DSC). Antibacterial activity of the as-synthesized nanorods was evaluated against two prokaryotic strains ( Escherichia coli and Staphylococcus aureus). The FT-IR studies show the presence of hydroxide and phosphate functional groups. HRTEM and FESEM images showed highly crystalline rod-shaped nanoparticles with the diameter of about 50-60 nm. EDAX revealed the presence of Ca, Zn, P, and O in the prepared samples. The crystallinity and thermal stability were further confirmed by TGA-DSC analysis. The biocompatibility evaluation results promoted that the Zn-HAp nanorods are biologically active apatites and potentially promising bone-substitute biomaterials for orthopaedic application.

Control of size and aspect ratio in hydroquinone-based synthesis of gold nanorods

NASA Astrophysics Data System (ADS)

Morasso, Carlo; Picciolini, Silvia; Schiumarini, Domitilla; Mehn, Dora; Ojea-Jiménez, Isaac; Zanchetta, Giuliano; Vanna, Renzo; Bedoni, Marzia; Prosperi, Davide; Gramatica, Furio

2015-08-01

In this article, we describe how it is possible to tune the size and the aspect ratio of gold nanorods obtained using a highly efficient protocol based on the use of hydroquinone as a reducing agent by varying the amounts of CTAB and silver ions present in the "seed-growth" solution. Our approach not only allows us to prepare nanorods with a four times increased Au3+ reduction yield, when compared with the commonly used protocol based on ascorbic acid, but also allows a remarkable reduction of 50-60 % of the amount of CTAB needed. In fact, according to our findings, the concentration of CTAB present in the seed-growth solution do not linearly influence the final aspect ratio of the obtained nanorods, and an optimal concentration range between 30 and 50 mM has been identified as the one that is able to generate particles with more elongated shapes. On the optimized protocol, the effect of the concentration of Ag+ ions in the seed-growth solution and the stability of the obtained particles has also been investigated.

Simulation of spectral properties of bundlelike gold nanorods

NASA Astrophysics Data System (ADS)

Ozaki, Ryotaro; Nagao, Yoshiki; Kadowaki, Kazunori; Kuwahara, Yutaka

2016-03-01

Metal nanoparticles have become increasingly important in fields such as electronics, photonics, and biotechnology. In particular, anisotropic gold nanoparticles, such as gold nanorods, exhibit unique properties owing to their anisotropy. Optical properties of isolated gold nanorods and dimers of gold nanorods have been investigated from both experimental and theoretical points of view. We have reported a method for three-dimensional assembly of anisotropic gold nanoparticles by two-phase transfer in which the morphologies of the assemblies can be controlled by the aspect ratio of nanorods. In this study, we numerically calculate extinction spectra to investigate the plasmonic properties of bundlelike assemblies by the finite-element method. Their plasmonic properties depend on not only the three orthogonal directions but also the alignment of the nanorod assembly.

SILAR controlled CdSe nanoparticles sensitized ZnO nanorods photoanode for solar cell application: Electrolyte effect.

PubMed

Nikam, Pratibha R; Baviskar, Prashant K; Majumder, Sutripto; Sali, Jaydeep V; Sankapal, Babasaheb R

2018-08-15

Controlled growth of different sizes of cadmium selenide (CdSe) nanoparticles over well aligned ZnO nanorods have been performed using successive ionic layer adsorption and reaction (SILAR) technique at room temperature (27 °C) in order to form nano heterostructure solar cells. Deposition of compact layer of zinc oxide (ZnO) by SILAR technique on fluorine doped tin oxide (FTO) coated glass substrate followed by growth of vertically aligned ZnO nanorods array using chemical bath deposition (CBD) at low temperature (<100 °C). Different characterization techniques viz. X-ray diffractometer, UV-Vis spectrophotometer, field emission scanning electron microscopy, transmission electron microscopy and X-ray photoelectron spectroscopy have been used to know the structural, optical, morphological and compositional properties of synthesized nano heterostructure. The photovoltaic performance of the cells with variation in SILAR cycles for CdSe and with use of different electrolytes have been recorded as J-V characteristics and the maximum conversion efficiency of 0.63% have been attained with ferro/ferri cyanide electrolyte for 12 cycles CdSe coating over 1-D ZnO nanorods. Copyright © 2018 Elsevier Inc. All rights reserved.

A gradient field defeats the inherent repulsion between magnetic nanorods

PubMed Central

Gu, Yu; Burtovyy, Ruslan; Custer, John; Luzinov, Igor; Kornev, Konstantin G.

2014-01-01

When controlling the assembly of magnetic nanorods and chains of magnetic nanoparticles, it is extremely challenging to bring them together side by side while keeping a desired spacing between their axes. We show that this challenge can be successfully resolved by using a non-uniform magnetic field that defeats an inherent repulsion between nanorods. Nickel nanorods were suspended in a viscous film and a non-uniform field was used to control their placement. The in-plane movement of nanorods was tracked with a high-speed camera and a detailed image analysis was conducted to quantitatively characterize the behaviour of the nanorods. The analysis focused on the behaviour of a pair of neighbour nanorods, and a corresponding dynamic model was formulated and investigated. The complex two-dimensional dynamics of a nanorod pair was analysed analytically and numerically, and a phase portrait was constructed. Using this phase portrait, we classified the nanorod behaviour and revealed the experimental conditions in which nanorods could be placed side by side. Dependence of the distance between a pair of neighbour nanorods on physical parameters was analysed. With the aid of the proposed theory, one can build different lattices and control their spacing by applying different field gradients. PMID:26064550

Effects of Chromium Dopant on Ultraviolet Photoresponsivity of ZnO Nanorods

NASA Astrophysics Data System (ADS)

Mokhtari, S.; Safa, S.; Khayatian, A.; Azimirad, R.

2017-07-01

Structural and optical properties of bare ZnO nanorods, ZnO-encapsulated ZnO nanorods, and Cr-doped ZnO-encapsulated ZnO nanorods have been investigated. Encapsulated ZnO nanorods were grown using a simple two-stage method in which ZnO nanorods were first grown on a glass substrate directly from a hydrothermal bath, then encapsulated with a thin layer of Cr-doped ZnO by dip coating. Comparative study of x-ray diffraction patterns showed that Cr was successfully incorporated into the shell layer of ZnO nanorods. Moreover, energy-dispersive x-ray spectroscopy confirmed presence of Cr in this sample. It was observed that the thickness of the shell layer around the core of the ZnO nanorods was at least about 20 nm. Transmission electron microscopy of bare ZnO nanorods revealed single-crystalline structure. Based on optical results, both the encapsulation process and addition of Cr dopant decreased the optical bandgap of the samples. Indeed, the optical bandgap values of Cr-doped ZnO-encapsulated ZnO nanorods, ZnO-encapsulated ZnO nanorods, and bare ZnO nanorods were 2.89 eV, 3.15 eV, and 3.34 eV, respectively. The ultraviolet (UV) parameters demonstrated that incorporation of Cr dopant into the shell layer of ZnO nanorods considerably facilitated formation and transportation of photogenerated carriers, optimizing their performance as a practical UV detector. As a result, the photocurrent of the Cr-doped ZnO-encapsulated ZnO nanorods was the highest (0.6 mA), compared with ZnO-encapsulated ZnO nanorods and bare ZnO nanorods (0.21 mA and 0.06 mA, respectively).

Optical characterization of CdS nanorods capped with starch

NASA Astrophysics Data System (ADS)

Roy, J. S.; Pal Majumder, T.; Schick, C.

2015-05-01

Well crystalline uniform CdS nanorods were grown by changing the concentration of maize starch. The highly polymeric (branched) structure of starch enhances the growth of CdS nanorods. The average diameter of the nanorods is 20-25 nm while length is of 500-600 nm as verified from SEM and XRD observations. The optical band gaps of the CdS nanorods are varying from 2.66 eV to 2.52 eV depending on concentration of maize starch. The photoluminescence (PL) emission bands are shifted from 526 nm to 529 nm with concentration of maize starch. We have also observed the enhanced PL intensity in CdS nanorods capped with starch. The Fourier transform infrared (FTIR) spectroscopy shows the significant effect of starch on CdS nanorods.

High Lithium Insertion Voltage Single-Crystal H2 Ti12 O25 Nanorods as a High-Capacity and High-Rate Lithium-Ion Battery Anode Material.

PubMed

Guo, Qiang; Chen, Li; Shan, Zizhao; Lee, Wee Siang Vincent; Xiao, Wen; Liu, Zhifang; Liang, Jingjing; Yang, Gaoli; Xue, Junmin

2018-01-10

H 2 Ti 12 O 25 holds great promise as a high-voltage anode material for advanced lithium-ion battery applications. To enhance its electrochemical performance, control of the crystal orientation and morphology is an effective way to cope with slow Li + -ion diffusion inside H 2 Ti 12 O 25 with severe anisotropy. In this report, Na 2 Ti 6 O 13 nanorods, prepared from Na 2 CO 3 and anatase TiO 2 in molten NaCl medium, were used as a precursor in the synthesis of long single-crystal H 2 Ti 12 O 25 nanorods with reactive facets. The as-prepared H 2 Ti 12 O 25 nanorods with a diameter of 100-200 nm showed higher charge (extraction) specific capacity and better rate performance than previously reported systems. The reversible capacity of H 2 Ti 12 O 25 was 219.8 mAh g -1 at 1C after 100 cycles, 172.1 mAh g -1 at 10C, and 144.4 mAh g -1 at 20C after 200 cycles; these values are higher than those of H 2 Ti 12 O 25 prepared by the conventional soft-chemical method. Moreover, the as-prepared H 2 Ti 12 O 25 nanorods exhibited superior cycle stability with more than 94 % retention of capacity with nearly 100 % coulombic efficiency after 100 cycles at 1C. On the basis of the above results, long single-crystal H 2 Ti 12 O 25 nanorods synthesized in molten NaCl with outstanding electrochemical characteristics hold a significant amount of promise for hybrid electric vehicles and energy-storage systems. © 2018 Wiley-VCH Verlag GmbH & Co. KGaA, Weinheim.

Synthesis of gold nanorods with a longitudinal surface plasmon resonance peak of around 1250 nm

NASA Astrophysics Data System (ADS)

Nguyen, Thi Nhat Hang; Le Trinh Nguyen, Thi; Thanh Tuyen Luong, Thi; Thang Nguyen, Canh Minh; Nguyen, Thi Phuong Phong

2016-03-01

We prepared gold nanorods and joined them to chemicals such as tetrachloauric (III) acid trihydrate, silver nitrate, hydroquinone, hexadecyltrimethylammonium bromide, sodium hydroxide and sodium borohydride using the seed-mediated method. The combination of hydroquinone, with or without salicylic acid, influences the size of the gold nanorods, and this is demonstrated by the results of TEM images, UV-vis spectra and the value of the longitudinal surface plasmon resonance peak with respect to the UV-vis spectra. By changing the Ag+ ion and hydroquinone concentration and the combination of hydroquinone and salicylic acid, the size of the gold nanorods can be controlled and this is manifested by longitudinal surface plasmon resonance peaks forming between 875 and 1278 nm. In particular, sample E2 achieved a longitudinal surface plasmon peak at 1273 nm and an aspect ratio of more than 10 by modifying the hydroquinone to 2.5 mM and salicylic acid to 0.5 mM concentration in the growth solution.

Biotin-streptavidin-induced aggregation of gold nanorods: tuning rod-rod orientation.

PubMed

Gole, Anand; Murphy, Catherine J

2005-11-08

We report herein biotin-streptavidin-mediated aggregation studies of long gold nanorods. We have previously demonstrated end-to-end linkages of gold nanorods driven by the biotin-streptavidin interaction (Caswell et al. J. Am. Chem. Soc. 2003, 125, 13914). In that report, the specific binding of biotin disulfide to the gold nanorod edges was achieved due to the preferred binding of thiol molecules to the Au[111] surface (gold nanorod ends) as opposed to the gold nanorod side faces. This led to the end-end linkage of gold nanorods upon subsequent addition of streptavidin. In this report we demonstrate a simple procedure to biotinylate the entire gold nanorod surface and subsequently form a 3-D assembly by addition of streptavidin. Gold nanorods were synthesized by the three-step seeding protocol documented in our previous articles. The surface of gold nanorods was further modified by a layer of a weak polyelectrolyte, poly(acrylic acid), PAA. A biotin molecule which has an amine group at one end (biotin-PEO-amine) was anchored to the carboxylic acid group of the polyelectrolyte using the well-known carbodiimide chemistry. This process biotinylates the entire gold nanorod surface. Addition of streptavidin further leads to aggregation of gold nanorods. A closer look at the aggregates reveals a preferential side-to-side assembly of gold nanorods. The gold nanorods were characterized at each stage by UV-vis spectroscopy, light scattering, and transmission electron microscopy (TEM) measurements.

Diameter Control and Photoluminescence of ZnO Nanorods from Trialkylamines

DOE PAGES

Andelman, Tamar; Gong, Yinyan; Neumark, Gertrude; ...

2007-01-01

A novel solution method to control the diameter of ZnO nanorods is reported. Small diameter (2-3 nm) nanorods were synthesized from trihexylamine, and large diameter (50–80 nm) nanorods were synthesized by increasing the alkyl chain length to tridodecylamine. The defect (green) emission of the photoluminescence (PL) spectra of the nanorods varies with diameter, and can thus be controlled by the diameter control. The small ZnO nanorods have strong green emission, while the large diameter nanorods exhibit a remarkably suppressed green band. We show that this observation supports surface oxygen vacancies as the defect that gives rise to the green emission.

Alignment of gold nanorods by angular photothermal depletion

DOE Office of Scientific and Technical Information (OSTI.GOV)

Taylor, Adam B.; Chow, Timothy T. Y.; Chon, James W. M., E-mail: jchon@swin.edu.au

2014-02-24

In this paper, we demonstrate that a high degree of alignment can be imposed upon randomly oriented gold nanorod films by angular photothermal depletion with linearly polarized laser irradiation. The photothermal reshaping of gold nanorods is observed to follow quadratic melting model rather than the threshold melting model, which distorts the angular and spectral hole created on 2D distribution map of nanorods to be an open crater shape. We have accounted these observations to the alignment procedures and demonstrated good agreement between experiment and simulations. The use of multiple laser depletion wavelengths allowed alignment criteria over a large range ofmore » aspect ratios, achieving 80% of the rods in the target angular range. We extend the technique to demonstrate post-alignment in a multilayer of randomly oriented gold nanorod films, with arbitrary control of alignment shown across the layers. Photothermal angular depletion alignment of gold nanorods is a simple, promising post-alignment method for creating future 3D or multilayer plasmonic nanorod based devices and structures.« less

Formation and electrical transport properties of pentacene nanorod crystal.

PubMed

Akai-Kasaya, M; Ohmori, C; Kawanishi, T; Nashiki, M; Saito, A; Aono, M; Kuwahara, Y

2010-09-10

The monophasic formation of an uncharted pentacene crystal, the pentacene nanorod, has been investigated. The restricted formation of the pentacene nanorod on a bare mica surface reveals a peculiar surface catalytic crystal growth mode of the pentacene. We demonstrated the charge transport measurements through a single pentacene nanorod and analyzed the data using a periodic hopping conduction model. The results revealed that the pentacene nanorod has a periodic conductive node within their one-dimensional crystal.

Scalable Direct Writing of Lanthanide-Doped KMnF3 Perovskite Nanowires into Aligned Arrays with Polarized Up-Conversion Emission.

PubMed

Shi, Shuo; Sun, Ling-Dong; Xue, Ying-Xian; Dong, Hao; Wu, Ke; Guo, Shi-Chen; Wu, Bo-Tao; Yan, Chun-Hua

2018-05-09

The use of one-dimensional nano- and microstructured semiconductor and lanthanide materials is attractive for polarized-light-emission studies. Up-conversion emission from single-nanorod or anisotropic nanoparticles with a degree of polarization has also been discussed. However, microscale arrays of nanoparticles, especially well-aligned one-dimensional nanostructures as well as their up-conversion polarization characterization, have not been investigated yet. Herein, we present a novel and facile paradigm for preparing highly aligned arrays of lanthanide-doped KMnF 3 (KMnF 3 :Ln) perovskite nanowires, which are good candidates for polarized up-conversion emission studies. These perovskite nanowires, with a width of 10 nm and length of a few micrometers, are formed through the oriented attachment of KMnF 3 :Ln nanocubes along the [001] direction. By the employment of KMnF 3 :Ln nanowire gel as nanoink, a direct-writing method is developed to obtain diverse types of aligned patterns from the nanoscale to the wafer scale. Up-conversion emissions from the highly aligned nanowire arrays are polarized along the array direction with a polarization degree up to 60%. Taking advantage of microscopic nanowire arrays, these polarized up-conversion emissions should offer potential applications in light or information transportation.

YBa2Cu3O x superconducting nanorods

NASA Astrophysics Data System (ADS)

Rieken, William; Bhargava, Atit; Horie, Rie; Akimitsu, Jun; Daimon, Hiroshi

2018-02-01

Herein, we report the synthesis of YBa2Cu3O x superconducting nanorods performed by solution chemistry. Initially, a mixture of fine-grained coprecipitated powder was obtained and subsequently converted to YBa2Cu3O x nanorods by heating to 1223 K in oxygen for 12 h. The nanorods are superconducting without the need for any further sintering or oxygenation, thereby providing an avenue for direct application to substrates at room temperature or direct use as formed nanorods. A critical superconducting transition temperature T c of about 92 K was achieved at a critical magnetic field of 10 Oe.

Tunable infrared hyperbolic metamaterials with periodic indium-tin-oxide nanorods

DOE PAGES

Guo, Peijun; Chang, Robert P. H.; Schaller, Richard D.

2017-07-10

Hyperbolic metamaterials (HMMs) are artificially engineered optical media that have been used for light confinement, excited state decay rate engineering, and subwavelength imaging, due to their highly anisotropic permittivity and with it the capability of supporting high- k modes. HMMs in the infrared range can be conceived for additional applications such as free space communication, thermal engineering, and molecular sensing. Here, we demonstrate infrared HMMs comprised of periodic indium-tin-oxide nanorod arrays (ITO-NRAs). We show that the ITO-NRA based HMMs exhibit a stationary epsilon-near-pole resonance in the near-infrared regime that is insensitive to the filling ratio, and a highly tunable epsilon-near-zeromore » resonance in the mid-infrared range depending on the array periodicity. Experimental results are supported by finite-element simulations, in which the ITO-NRAs are treated both explicitly and as an effective hyperbolic media. Lastly, our work presents a low-loss HMM platform with favorable spectral tunability in the infrared range.« less

Growth process for gallium nitride porous nanorods

DOEpatents

Wildeson, Isaac Harshman; Sands, Timothy David

2015-03-24

A GaN nanorod and formation method. Formation includes providing a substrate having a GaN film, depositing SiN.sub.x on the GaN film, etching a growth opening through the SiN.sub.x and into the GaN film, growing a GaN nanorod through the growth opening, the nanorod having a nanopore running substantially through its centerline. Focused ion beam etching can be used. The growing can be done using organometallic vapor phase epitaxy. The nanopore diameter can be controlled using the growth opening diameter or the growing step duration. The GaN nanorods can be removed from the substrate. The SiN.sub.x layer can be removed after the growing step. A SiO.sub.x template can be formed on the GaN film and the GaN can be grown to cover the SiO.sub.x template before depositing SiN.sub.x on the GaN film. The SiO.sub.x template can be removed after growing the nanorods.

CdO nanorods and Cd(OH)2/Ag core/satellite nanorods: Rapid and efficient sonochemical synthesis, characterization and their magnetic properties.

PubMed

Abbas, Mohamed; Tawfik, Wael; Chen, Jiangang

2018-01-01

We have designed an efficient and direct sonochemical method for the facile synthesis of Cd(OH) 2 , CdO, and Cd(OH) 2 /Ag core/satellite nanorods. A Cd(OH) 2 nanorod was synthesized with a one-pot, environmentally-friendly aqueous sonochemical reaction, followed by calcination at 500°C to produce CdO nanorods. Thirty minutes of re-ultrasonicated CdO nanorods in the presence of the Ag precursor was sufficient for phase transformation from the cubic structure of CdO to the monoclinic crystalline structure of Cd(OH) 2 , accompanied by deposition of Ag nanodots on the surface to form Cd(OH) 2 /Ag core/satellite nanorods. X-ray diffraction, transmission electron microscopy, high-resolution transmission electron microscopy, energy-dispersive spectroscopy, N 2 Brunauer-Emmett-Teller adsorption-desorption, and Fourier-transform infrared spectroscopy measurements confirmed the successful formation of the various phases and the unique morphology of the nanorods/satellites. We also measured the magnetic properties using a vibrating sample magnetometer at room temperature, and the produced nanorods showed weak unsaturated ferromagnetic properties with a magnetic moment values of 0.105 and 0.076emu/g for CdO and Cd(OH) 2 /Ag NRs, respectively. In conclusion, our one-pot, cost-effective, sonochemical approach holds promise for the synthesis of various oxides and core/satellite nanoparticles. Copyright © 2017 Elsevier B.V. All rights reserved.

A potentiometric biosensor for the detection of notch 3 using functionalized ZnO nanorods.

PubMed

Ibupoto, Z H; Khun, K; Liu, X; Willander, M

2014-09-01

The notch signalling plays a vital and radical role for the activity of cellular proliferation, differentiation and apoptosis. In this study, for the first time a particular biosensor is developed for the detection of notch 3. ZnO nanorods were fabricated on the gold coated glass substrate by hydrothermal method and afterwards were decorated with the gold nanoparticles by electrodepositing technique. Scanning electron microscopy (SEM) has shown the perpendicular to the substrate growth pattern of ZnO nanorods. X-ray diffraction (XRD) studies showed the c-axis oriented growth direction with wurtzite crystal structure of ZnO nanorods. X-ray Photoelectron Spectroscopy (XPS) and energy dispersive X-ray (EDX) techniques have shown the presence of Zn, O and Au atoms in the prepared functional material. Furthermore, the anti-notch 3 was physically adsorbed on the gold nanoparticles functionalized ZnO nanorods. The developed potentiometric immunosensor has shown response to the wide range of notch 3 molecules. The detected range included 1.00 x 10(-5)-1.50 x 10(0 ) μg/mL with a sensitivity of 23.15 ± 0.31 mV/decade. The analytical parameters including reproducibility, stability, and selectivity were also investigated and the observed results indicate the acceptable performance of the notch 3 biosensor. Moreover, the proposed notch 3 biosensor exhibited a fast response time of 10 s.

Co3O4 nanorod-supported Pt with enhanced performance for catalytic HCHO oxidation at room temperature

NASA Astrophysics Data System (ADS)

Yan, Zhaoxiong; Xu, Zhihua; Cheng, Bei; Jiang, Chuanjia

2017-05-01

Formaldehyde (HCHO) removal from air at room (ambient) temperature by effective catalysts is of significance for improving indoor air quality, and catalysts with high efficiency and good recyclability are highly desirable. In this study, platinum (Pt) supported on nanorod-shaped Co3O4 (Pt/Co3O4) was prepared by calcination of microwave-assisted synthesized Co3O4 precursor followed by NaBH4-reduction of Pt precursor. The as-prepared Co3O4 exhibited a morphology of nanorods with lengths of 400-700 nm and diameters of approximately 40-50 nm, which were self-assembled by nanoparticles. The Pt/Co3O4 catalyst exhibited a superior catalytic performance for HCHO oxidation at room temperature compared to Pt supported on commercial Co3O4 (Pt/Co3O4-c) and Pt supported on commercial TiO2 (Pt/TiO2), which is mainly due to the high oxygen mobility resulting from its distinct nanorod morphology, strong metal-support interaction between Pt and Co3O4, and the intrinsic redox nature of the Co3O4 support. This study provides new insights into the fabrication of high-performance catalysts for indoor air purification.

Layered-metal-hydroxide nanosheet arrays with controlled nanostructures to assist direct electronic communication at biointerfaces.

PubMed

An, Zhe; Lu, Shan; Zhao, Liwei; He, Jing

2011-10-18

In this work, ordered vertical arrays of layered double hydroxide (LDH) nanosheets have been developed to achieve electron transfer (eT) at biointerfaces in electrochemical devices. It is found that tailoring the gap size of LDH nanosheet arrays could significantly promote the eT rate. This research has successfully extended nanomaterials for efficient modifications of electrode surfaces from nanoparticles, nanowires, nanorods, and nanotubes to nanosheets. © 2011 American Chemical Society

Nanorod-Based Fast-Response Pressure-Sensitive Paints

NASA Technical Reports Server (NTRS)

Bencic, Timothy; VanderWal, Randall

2007-01-01

A proposed program of research and development would be devoted to exploitation of nanomaterials in pressuresensitive paints (PSPs), which are used on wind-tunnel models for mapping surface pressures associated with flow fields. Heretofore, some success has been achieved in measuring steady-state pressures by use of PSPs, but success in measuring temporally varying pressures has been elusive because of the inherent slowness of the optical responses of these materials. A PSP contains a dye that luminesces in a suitable wavelength range in response to photoexcitation in a shorter wavelength range. The luminescence is quenched by oxygen at a rate proportional to the partial pressure of oxygen and thus proportional to the pressure of air. As a result, the intensity of luminescence varies inversely with the pressure of air. The major problem in developing a PSP that could be easily applied to a wind-tunnel model and could be useful for measuring rapidly varying pressure is to provide very high gas diffusivity for rapid, easy transport of oxygen to and from active dye molecules. Most PSPs include polymer-base binders, which limit the penetration of oxygen to dye molecules, thereby reducing responses to pressure fluctuations. The proposed incorporation of nanomaterials (somewhat more specifically, nanorods) would result in paints having nanostructured surfaces that, relative to conventional PSP surfaces, would afford easier and more nearly complete access of oxygen molecules to dye molecules. One measure of greater access is effective surface area: For a typical PSP as proposed applied to a given solid surface, the nanometer-scale structural features would result in an exposed surface area more than 100 times that of a conventional PSP, and the mass of proposed PSP needed to cover the surface would be less than tenth of the mass of the conventional PSP. One aspect of the proposed development would be to synthesize nanorods of Si/SiO2, in both tangle-mat and regular- array

Enhancement of transdermal protein delivery by photothermal effect of gold nanorods coated on polysaccharide-based hydrogel.

PubMed

Haine, Aung Thu; Koga, Yuki; Hashimoto, Yuta; Higashi, Taishi; Motoyama, Keiichi; Arima, Hidetoshi; Niidome, Takuro

2017-10-01

Transdermal protein delivery is a useful and attractive method for protein therapy and dermal vaccination. However, this delivery method is restricted by the low permeability of the stratum corneum. The purpose of this study was to develop a transdermal delivery system for enhancement of protein permeability into the skin. First, we prepared a transparent gel patch made of polysaccharides with gold nanorods on the gel surface and fluorescein isothiocyanate-modified ovalbumin (FITC-OVA) inside. Next, the gel patch was placed on mouse skin to allow contact with the coated gold nanorods, and irradiated by a continuous-wave laser. The laser irradiation heated the gold nanorods and the skin temperature increased to 43°C, resulting in enhanced translocation of FITC-OVA into the skin. These results confirmed the capability of the transdermal protein delivery system to perforate the stratum corneum and thus facilitate the passage of proteins across the skin. Copyright © 2017 Elsevier B.V. All rights reserved.

Preparation of Janus Particles and Alternating Current Electrokinetic Measurements with a Rapidly Fabricated Indium Tin Oxide Electrode Array.

PubMed

Chen, Yu-Liang; Jiang, Hong-Ren

2017-06-23

This article provides a simple method to prepare partially or fully coated metallic particles and to perform the rapid fabrication of electrode arrays, which can facilitate electrical experiments in microfluidic devices. Janus particles are asymmetric particles that contain two different surface properties on their two sides. To prepare Janus particles, a monolayer of silica particles is prepared by a drying process. Gold (Au) is deposited on one side of each particle using a sputtering device. The fully coated metallic particles are completed after the second coating process. To analyze the electrical surface properties of Janus particles, alternating current (AC) electrokinetic measurements, such as dielectrophoresis (DEP) and electrorotation (EROT)- which require specifically designed electrode arrays in the experimental device- are performed. However, traditional methods to fabricate electrode arrays, such as the photolithographic technique, require a series of complicated procedures. Here, we introduce a flexible method to fabricate a designed electrode array. An indium tin oxide (ITO) glass is patterned by a fiber laser marking machine (1,064 nm, 20 W, 90 to 120 ns pulse-width, and 20 to 80 kHz pulse repetition frequency) to create a four-phase electrode array. To generate the four-phase electric field, the electrodes are connected to a 2-channel function generator and to two invertors. The phase shift between the adjacent electrodes is set at either 90° (for EROT) or 180° (for DEP). Representative results of AC electrokinetic measurements with a four-phase ITO electrode array are presented.

Polyacrylonitrile block copolymers for the preparation of a thin carbon coating around TiO2 nanorods for advanced lithium-ion batteries.

PubMed

Oschmann, Bernd; Bresser, Dominic; Tahir, Muhammad Nawaz; Fischer, Karl; Tremel, Wolfgang; Passerini, Stefano; Zentel, Rudolf

2013-11-01

Herein, a new method for the realization of a thin and homogenous carbonaceous particle coating, made by carbonizing RAFT polymerization derived block copolymers anchored on anatase TiO2 nanorods, is presented. These block copolymers consist of a short anchor block (based on dopamine) and a long, easily graphitizable block of polyacrylonitrile. The grafting of such block copolymers to TiO2 nanorods creates a polymer shell, which can be visualized by atomic force microscopy (AFM). Thermal treatment at 700 °C converts the polyacrylonitrile block to partially graphitic structures (as determined by Raman spectroscopy), establishing a thin carbon coating (as determined by transmission electron microscopy, TEM, analysis). The carbon-coated TiO2 nanorods show improved electrochemical performance in terms of achievable specific capacity and, particularly, long-term cycling stability by reducing the average capacity fading per cycle from 0.252 mAh g(-1) to only 0.075 mAh g(-1) . © 2013 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Surface engineering on CeO2 nanorods by chemical redox etching and their enhanced catalytic activity for CO oxidation

NASA Astrophysics Data System (ADS)

Gao, Wei; Zhang, Zhiyun; Li, Jing; Ma, Yuanyuan; Qu, Yongquan

2015-07-01

Controllable surface properties of nanocerias are desired for various catalytic processes. There is a lack of efficient approaches to adjust the surface properties of ceria to date. Herein, a redox chemical etching method was developed to controllably engineer the surface properties of ceria nanorods. Ascorbic acid and hydrogen peroxide were used to perform the redox chemical etching process, resulting in a rough surface and/or pores on the surface of ceria nanorods. Increasing the etching cycles induced a steady increase of the specific surface area, oxygen vacancies and surface Ce3+ fractions. As a result, the etched nanorods delivered enhanced catalytic activity for CO oxidation, compared to the non-etched ceria nanorods. Our method provides a novel and facile approach to continuously adjust the surface properties of ceria for practical applications.Controllable surface properties of nanocerias are desired for various catalytic processes. There is a lack of efficient approaches to adjust the surface properties of ceria to date. Herein, a redox chemical etching method was developed to controllably engineer the surface properties of ceria nanorods. Ascorbic acid and hydrogen peroxide were used to perform the redox chemical etching process, resulting in a rough surface and/or pores on the surface of ceria nanorods. Increasing the etching cycles induced a steady increase of the specific surface area, oxygen vacancies and surface Ce3+ fractions. As a result, the etched nanorods delivered enhanced catalytic activity for CO oxidation, compared to the non-etched ceria nanorods. Our method provides a novel and facile approach to continuously adjust the surface properties of ceria for practical applications. Electronic supplementary information (ESI) available: Diameter distributions of as-prepared and etched samples, optical images, specific catalytic data of CO oxidation and comparison of CO oxidation. See DOI: 10.1039/c5nr01846c

Alq3 nanorods: promising building blocks for optical devices.

PubMed

Chen, Wei; Peng, Qing; Li, Yadong

2008-07-17

Monodisperse Alq3 nanorods with hexagonal-prism-like morphology are produced via a facile, emulsion based synthesis route. The photoluminescence of individual nanorods differs from the bulk material. These nanorods are promising building blocks for novel optical devices. Copyright © 2008 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

A theory of growing crystalline nanorods - Mode I

NASA Astrophysics Data System (ADS)

Du, Feng; Huang, Hanchen

2018-08-01

Nanorods grow in two possible modes during physical vapor deposition (PVD). In mode I, monolayer surface steps dictate the diameter of nanorods. In mode II, multiple-layer surface steps dictate the diameter, which is the smallest possible under physical vapor deposition [5,10]. This paper reports closed-form theories of terrace lengths and nanorod diameter during the growth in mode I, as a function of deposition conditions. The accompanying lattice kinetic Monte Carlo simulations verify these theories. This study reveals that (1) quasi-steady growth exists for each set of nanorod growth conditions, and (2) the characteristic length scales, including terrace lengths and nanorod diameter at the quasi-steady state, depend on the deposition conditions - deposition rate F, substrate temperature T, and incidence angle θ - only as a function of l2D/tan θ, with l2 D = 2(v2 D/Fcosθ) 1/3 as a diffusion-limited length scale and v2D as the atomic diffusion jump rate over monolayer surface steps.

A selective potentiometric copper (II) ion sensor based on the functionalized ZnO nanorods.

PubMed

Khun, K; Ibupoto, Z H; Liu, X; Nur, O; Willander, M; Danielsson, B

2014-09-01

In this work, ZnO nanorods were hydrothermally grown on the gold-coated glass substrate and characterized by field emission scanning electron microscopy (FESEM) and X-ray diffraction (XRD) techniques. The ZnO nanorods were functionalized by two different approaches and performance of the sensor electrode was monitored. Fourier transform infrared spectroscopy (FTIR) was carried out for the confirmation of interaction between the ionophore molecules and ZnO nanorods. In addition to this, the surface of the electrode was characterized by X-ray photoelectron spectroscopy (XPS) showing the chemical and electronic state of the ionophore and ZnO nanorod components. The ionophore solution was prepared in the stabilizer, poly vinyl chloride (PVC) and additives, and then functionalized on the ZnO nanorods that have shown the Nernstian response with the slope of 31 mV/decade. However, the Cu2+ ion sensor was fabricated only by immobilizing the selective copper ion ionophore membrane without the use of PVC, plasticizers, additives and stabilizers and the sensor electrode showed a linear potentiometric response with a slope of 56.4 mV/decade within a large dynamic concentration range (from 1.0 x 10(-6) to 1.0 x 10(-1) M) of copper (II) nitrate solutions. The sensor showed excellent repeatability and reproducibility with response time of less than 10 s. The negligible response to potentially interfering metal ions such as calcium (Ca2+), magnesium (Mg2+), potassium (K+), iron (Fe3+), zinc (Zn2+), and sodium (Na+) allows this sensor to be used in biological studies. It may also be used as an indicator electrode in the potentiometric titration.

Diamond-Like Carbon Nanorods and Fabrication Thereof

NASA Technical Reports Server (NTRS)

Varshney, Deepak (Inventor); Makarov, Vladimir (Inventor); Morell, Gerardo (Inventor); Saxena, Puja (Inventor); Weiner, Brad (Inventor)

2017-01-01

Novel sp. (sup 3) rich diamond-like carbon (DLC) nanorod films were fabricated by hot filament chemical vapor deposition technique. The results are indicative of a bottom-up self-assembly synthesis process, which results in a hierarchical structure that consists of microscale papillae comprising numerous nanorods. The papillae have diameters ranging from 2 to 4 microns and the nanorods have diameters in the 35-45 nanometer range. A growth mechanism based on the vapor liquid-solid mechanism is proposed that accounts for the morphological aspects in the micro- and nano-scales.

Frabicating hydroxyapatite nanorods using a biomacromolecule template

NASA Astrophysics Data System (ADS)

Zhu, Aiping; Lu, Yan; Si, Yunfeng; Dai, Sheng

2011-02-01

Rod-like hydroxyapatite (HAp) nanoparticles with various aspect ratios are synthesized by means of low-temperature hydrothermal method in the presence of a N-[(2-hydroxy-3-trimethylammonium) propyl]chitosan chloride (HTCC) template. The synthesized HAps were examined by X-ray diffraction (XRD), Fourier transform infrared spectrophotometer (FTIR) and transmission electron microscopy (TEM) techniques. The results reveal that HAps are rod-like monocrystals, where the size and morphology can be tailored by varying synthesis conditions, such as pH, hydrothermal synthesis temperature and the ratio of PO43- to the quaternary ammonium in HTCC. The mechanism of HTCC template on HAp nanorod preparation is analyzed.

Functionalized Gold Nanorods for Tumor Imaging and Targeted Therapy

PubMed Central

Gui, Chen; Cui, Da-xiang

2012-01-01

Gold nanorods, as an emerging noble metal nanomaterial with unique properties, have become the new exciting focus of theoretical and experimental studies in the past few years. The structure and function of gold nanorods, especially their biocompatibility, optical property, and photothermal effects, have been attracting more and more attention. Gold nanorods exhibit great potential in applications such as tumor molecular imaging and photothermal therapy. In this article, we review some of the main advances made over the past few years in the application of gold nanorods in surface functionalization, molecular imaging, and photothermal therapy. We also explore other prospective applications and discuss the corresponding concepts, issues, approaches, and challenges, with the aim of stimulating broader interest in gold nanorod-based nanotechnology and improving its practical application. PMID:23691482

Exciton emission from bare and hybrid plasmonic GaN nanorods

NASA Astrophysics Data System (ADS)

Mohammadi, Fatemesadat; Kunert, Gerd; Hommel, Detlef; Ge, Jingxuan; Duscher, Gerd; Schmitzer, Heidrun; Wagner, Hans Peter

We study the exciton emission of hybrid gold nanoparticle/Alq3 (aluminiumquinoline)/wurtzite GaN nanorods. GaN nanorods of 1.5 μm length and 250 nm diameter were grown by plasma assisted MBE. Hybrid GaN nanorods were synthesized by organic molecular beam deposition. Temperature and power dependent time integrated (TI) and time resolved (TR) photoluminescence (PL) measurements were performed on bare and hybrid structures. Bare nanorods show donor (D0,X) and acceptor bound (A0,X) exciton emission at 3.473 eV and at 3.463 eV, respectively. TR-PL trace modeling reveal lifetimes of 240 ps and 1.4 ns for the (D0,X) and (A0,X) transition. 10 nm gold coated GaN nanorods show a significant PL quenching and (D0,X) lifetime shortening which is tentatively attributed to impact ionization of (D0,X) due to hot electron injection from the gold nanoparticles. This is supported by electron energy loss spectroscopy that shows a redshift of a midgap state transition indicating a reduction of a preexisting band-bending at the nanorod surface due to positive charging of the gold nanoparticles. Inserting a nominally 5 nm thick Alq3 spacer between the nanorod and the gold reduces the PL quenching and lifetime shortening. Plasmonic nanorods with a 30 nm thick Alq3 spacer reveal lifetimes which are nearly identical to uncoated GaN nanorods.

Self-assembly of Nano-rods in Photosensitive Phase Separation

NASA Astrophysics Data System (ADS)

Liu, Ya; Kuksenok, Olga; Maresov, Egor; Balazs, Anna

2012-02-01

Computer simulations reveal how photo-induced chemical reactions in polymeric mixtures can be exploited to create long-range order in materials whose features range from the sub-micron to the nanoscale. The process is initiated by shining a spatially uniform light on a photosensitive AB binary blend, which thereby undergoes both a reversible chemical reaction and phase separation. When a well-collimated, higher intensity light is rastered over the sample, the system forms defect-free, spatially periodic structures. We now build on this approach by introducing nanorods that have a preferential affinity for one the phases in a binary mixture. By rastering over the sample with the higher intensity light, we can create ordered arrays of rods within periodically ordered materials in essentially one processing step.

Cryptomelane-type manganese oxide (KMn8O16) nanorods cathode materials synthesized by a rheological phase for lithium ion batteries

NASA Astrophysics Data System (ADS)

Zheng, Hao; Wang, Ting; Zhao, Rongfei; Chen, Jinsong; Li, Lin

2018-01-01

Cryotolerance-type manganese oxide (KMn8O16) nanorods were prepared for the first time by a rheological phase reaction method. The KMn8O16 samples were characterized by X-ray diffraction, scanning electron microscopy, the effects of different annealed temperatures on the morphologies and electrochemical properties of the final products were systematically investigated. The result that the annealed samples exhibit the superior electrochemical performances compared to the unannealed sample. The KMn8O16 nanorods annealed at 400 °C show the highest reversible discharge capacity (147.9 mAh/g even after 80 cycles) at current density of 50 mA/g and the best cycling stability. These results indicate that the KMn8O16 nanorods could be a promising cathode material for lithium ion batteries.

Photothermal ablation cancer therapy using homogeneous CsxWO3 nanorods with broad near-infra-red absorption

NASA Astrophysics Data System (ADS)

Guo, Chongshen; Yin, Shu; Yu, Haijun; Liu, Shaoqin; Dong, Qiang; Goto, Takehiro; Zhang, Zhiwen; Li, Yaping; Sato, Tsugio

2013-06-01

Recently, photothermal ablation therapy (PTA) employing near-infrared radiation (NIR) has been extensively investigated as an emerging modality for cancer management. However, the clinical translation of this promising approach is limited by the lack of PTA agents with broad NIR absorption, low cost and high photothermal conversion efficiency. Herein, we have developed PEGylated homogeneous CsxWO3 nanorods (a mean size ~69.3 nm × 12.8 nm) with broad photo-absorption (780-2500 nm) as a novel NIR absorbent for PTA treatment of human cancer. The prepared CsxWO3 nanocrystals displayed strong near-infrared optical absorption with a high molar extinction coefficient (e.g. 4.8 × 1010 M-1 cm-1 at 980 nm), thus generated significant amounts of heat upon excitation with near-infrared light. The PTA study in two human carcinoma cell lines (i.e. A549 lung cancer cells and HeLa ovarian cancer cells) demonstrated that CsxWO3 nanorods can efficiently cause cell death via hyperthermia induced lysosome destruction, cytoskeleton protein degradation, DNA damage and thereafter cellular necrosis or apoptosis. Our study also confirmed the migration of healthy cells migrated from unirradiated areas to dead cell cycle, which is essential for tissue reconstruction and wound healing after photodestruction of tumor tissue. The prompted results reported in the current study imply the promising potential of CsxWO3 nanorods for application in PTA cancer therapy.Recently, photothermal ablation therapy (PTA) employing near-infrared radiation (NIR) has been extensively investigated as an emerging modality for cancer management. However, the clinical translation of this promising approach is limited by the lack of PTA agents with broad NIR absorption, low cost and high photothermal conversion efficiency. Herein, we have developed PEGylated homogeneous CsxWO3 nanorods (a mean size ~69.3 nm × 12.8 nm) with broad photo-absorption (780-2500 nm) as a novel NIR absorbent for PTA treatment of human

Structural and Optical Properties of Core-Shell TiO2/CdS Prepared by Chemical Bath Deposition

NASA Astrophysics Data System (ADS)

Al-Jawad, Selma M. H.

2017-10-01

Titanium dioxide (TiO2) nanorod arrays (NRAs) sensitized with cadmium sulfide (CdS) nanoparticles (NPs) were deposited by chemical bath deposition (CBD). TiO2 NRAs were also obtained by using the same method on glass substrates coated with fluorine-doped tin oxide (FTO). The structure of the FTO/TiO2/CdS core-shell was characterized by x-ray diffraction (XRD), atomic force microscopy, scanning electron microscopy, ultraviolet-visible (UV-Vis) absorption spectroscopy, photoluminescence, and photoelectrocatalysis of FTO/TiO2 and FTO/TiO2/CdS. The FTO/TiO2 conformed to anatase and rutile phase structures for different pH values and also with annealing. XRD patterns of the FTO/TiO2/CdS sample exhibited two peaks corresponding to hexagonal (100) and (101) for CdS. Scanning electron micrographs showed nanorod structures for the TiO2 thin films deposited at a pH value equal 0.7. Optical results showed the CdS deposited on nanorod TiO2 exhibited increased absorption ability in the visible light, indicating an increased photocatalytic activity for TiO2/CdS core-shell nanorods in the visible light. When illuminated with a UV-Vis light source, the TiO2/CdS core-shell films displayed high responses. A composite exists between the TiO2 nanostructure and CdS NPs because the film absorbs the incident light located in both the visible and UV-Vis regions. A higher response to UV-Vis light was attained with the use of TiO2 NRAs/CdS NPs films prepared by CBD. This approach offers a technique for fabricating photoelectrodes.

Nanorod Mobility within Entangled Wormlike Micelle Solutions

DOE Office of Scientific and Technical Information (OSTI.GOV)

Lee, Jonghun; Grein-Iankovski, Aline; Narayanan, Suresh

In the semi-dilute regime, wormlike micelles form an isotropic entangled microstructure that is similar to that of an entangled polymer solution with a characteristic, nanometer-scale entanglement mesh size. We report a combined x-ray photon correlation spectroscopy (XPCS) and rheology study to investigate the translational dynamics of gold nanorods in semi-dilute solutions of entangled wormlike micelles formed by the surfactant cetylpyridinium chloride (CPyCl) and the counter-ion sodium salicylate (NaSal). The CPyCl concentration is varied to tune the entanglement mesh size over a range that spans from approximately equal to the nanorod diameter to larger than the nanorod length. The NaSal concentrationmore » is varied along with the CPyCl concentration so that the solutions have the maximum viscosity for given CPyCl concentration. On short time scales the nanorods are localized on a length scale matching that expected from the high-frequency elastic modulus of the solutions as long as the mesh size is smaller than the rod length. On longer time scales, the nanorods undergo free diffusion. At the highest CPyCl concentrations, the nanorod diffusivity approaches the value expected based on the macroscopic viscosity of the solutions, but it increases with decreasing CPyCl concentration more rapidly than expected from the macroscopic viscosity. A recent model by Cai et al. [Cai, L.-H.; Panyukov, S.; Rubinstein, M. Macromolecules 2015, 48, 847-862.] for nanoparticle “hopping” diffusion in entangled polymer solutions accounts quantitatively for this enhanced diffusivity.« less

Nanorod Mobility within Entangled Wormlike Micelle Solutions

DOE PAGES

Lee, Jonghun; Grein-Iankovski, Aline; Narayanan, Suresh; ...

2016-12-20

In the semi-dilute regime, wormlike micelles form an isotropic entangled microstructure that is similar to that of an entangled polymer solution with a characteristic, nanometer-scale entanglement mesh size. We report a combined x-ray photon correlation spectroscopy (XPCS) and rheology study to investigate the translational dynamics of gold nanorods in semi-dilute solutions of entangled wormlike micelles formed by the surfactant cetylpyridinium chloride (CPyCl) and the counter-ion sodium salicylate (NaSal). The CPyCl concentration is varied to tune the entanglement mesh size over a range that spans from approximately equal to the nanorod diameter to larger than the nanorod length. The NaSal concentrationmore » is varied along with the CPyCl concentration so that the solutions have the maximum viscosity for given CPyCl concentration. On short time scales the nanorods are localized on a length scale matching that expected from the high-frequency elastic modulus of the solutions as long as the mesh size is smaller than the rod length. On longer time scales, the nanorods undergo free diffusion. At the highest CPyCl concentrations, the nanorod diffusivity approaches the value expected based on the macroscopic viscosity of the solutions, but it increases with decreasing CPyCl concentration more rapidly than expected from the macroscopic viscosity. A recent model by Cai et al. [Cai, L.-H.; Panyukov, S.; Rubinstein, M. Macromolecules 2015, 48, 847-862.] for nanoparticle “hopping” diffusion in entangled polymer solutions accounts quantitatively for this enhanced diffusivity.« less

Facile synthesis of hybrid nanorods with the Sb2Se3/AgSbSe2 heterojunction structure for high performance photodetectors.

PubMed

Chen, Shuo; Qiao, Xvsheng; Wang, Fengxia; Luo, Qun; Zhang, Xianghua; Wan, Xia; Xu, Yang; Fan, Xianping

2016-01-28

An effective colloidal process involving the hot-injection method is developed to synthesize uniform single-crystalline Sb2Se3 nanorods in high yields. The photoconductive characteristics of the as-synthesized Sb2Se3 nanorods are investigated by developing a film-based photodetector and this device displays a remarkable response to visible light with an "ON/OFF" ratio as high as 50 (with an incident light density of 12.05 mW cm(-2)), short response/recovery times and long-term durability. To overcome the challenge of the intrinsic low electrical conductivity of Sb2Se3, hybrid nanorods with the Sb2Se3/AgSbSe2 heterojunction structure having a type-II band alignment are firstly prepared. The electric current of the photodetector based on the Sb2Se3/AgSbSe2 hybrid nanorod film has been significantly increased both in the dark and under light illumination. The responsivity of the photodetector based on the Sb2Se3/AgSbSe2 hybrid nanorod film is about 4.2 times as much as that of the photodetector based on the Sb2Se3 nanorod film. This improvement can be considered as an important step to promote Sb2Se3 based semiconductors for applications in high performance photodetectors.

Nanocrystalline CeO2-δ coated β-MnO2 nanorods with enhanced oxygen transfer property

NASA Astrophysics Data System (ADS)

Huang, Xiubing; Zhao, Guixia; Chang, Yueqi; Wang, Ge; Irvine, John T. S.

2018-05-01

In this research, β-MnO2 nanorods were synthesized by a hydrothermal method, followed by a facile precipitation method to obtain nanocrystalline CeO2-δ coated β-MnO2 nanorods. The as-prepared samples were characterized by XRD, HRTEM, FESEM, XPS and in-situ high-temperature XRD. The HRTEM results show that well dispersed CeO2-δ nanocrystals sized about 5 nm were coated on the surface of β-MnO2 nanorods. The oxygen storage and transfer property of as-synthesized materials were evaluated using TGA under various atmospheres (air, pure N2, and 5%H2/95%Ar). The TGA results indicate that CeO2-δ modification could favour the reduction of Mn4+ to Mn3+ and/or Mn2+ at lower temperature as compared with pure β-MnO2 nanorods and the physically mixed CeO2-δ-β-MnO2 under low oxygen partial pressure conditions (i.e., pure N2, 5%H2/95%Ar). Specifically, CeO2-δ@β-MnO2 sample can exhibit 7.5 wt% weight loss between 100 and 400 °C under flowing N2 and 11.4 wt% weight loss between 100 and 350 °C under flowing 5%H2/95%Ar. During the reduction process under pure N2 or 5%H2/95%Ar condition, the oxygen ions in β-MnO2 nanorods are expected to be released to the surroundings in the form of O2 or H2O with the coated CeO2-δ nanocrystals acting as mediator as inferred from the synergistic effect between the well-interacted CeO2-δ nanocrystals and β-MnO2 nanorods.

Violet-blue LEDs based on p-GaN/n-ZnO nanorods and their stability.

PubMed

Jha, Shrawan; Qian, Jin-Cheng; Kutsay, Oleksandr; Kovac, Jaroslav; Luan, Chun-Yan; Zapien, Juan Antonio; Zhang, Wenjun; Lee, Shuit-Tong; Bello, Igor

2011-06-17

In this paper, we report a fabrication, characterization and stability study of p-GaN/n-ZnO nanorod heterojunction light-emitting devices (LEDs). The LEDs were assembled from arrays of n-ZnO vertical nanorods epitaxially grown on p-GaN. LEDs showed bright electroluminescence in blue (440 nm), although weaker violet (372 nm) and green-yellow (550 nm) spectral components were also observed. The device characteristics are generally stable and reproducible. The LEDs have a low turn-on voltage (∼5 V). The electroluminescence (EL) is intense enough to be noticed by the naked eye, at an injection current as low as ∼ 40 µA (2.1 × 10(-2) A cm(-2) at 7 V bias). Analysis of the materials, electrical and EL investigations point to the role of a high quality of p-n nano-heterojunction which facilitates a large rectification ratio (320) and a stable reverse current of 2.8 µA (1.4 × 10(-3) A cm(-2) at 5 V). Stability of EL characteristics was investigated in detail. EL intensity showed systematic degradation over a short duration when the LED was bias-stressed at 30 V. At smaller bias (<20 V) LEDs tend to show a stable and repeatable EL characteristic. Thus a simple low temperature solution growth method was successfully exploited to realize nanorod/film heterojunction LED devices with predictable characteristics.

One-step in situ synthesis of graphene–TiO{sub 2} nanorod hybrid composites with enhanced photocatalytic activity

DOE Office of Scientific and Technical Information (OSTI.GOV)

Sun, Mingxuan, E-mail: mingxuansun@sues.edu.cn; Li, Weibin; Sun, Shanfu

2015-01-15

Chemically bonded graphene/TiO{sub 2} nanorod hybrid composites with superior dispersity were synthesized by a one-step in situ hydrothermal method using graphene oxide (GO) and TiO{sub 2} (P25) as the starting materials. The as-prepared samples were characterized by XRD, XPS, TEM, FE-SEM, EDX, Raman, N{sub 2} adsorption, and UV–vis DRS techniques. Enhanced light absorption and a red shift of absorption edge were observed for the composites in the ultraviolet–visible diffuse reflectance spectroscopy (UV–vis DRS). Their effective photocatalytic activity was evaluated by the photodegradation of methylene blue under visible light irradiation. An enhancement of photocatalytic performance was observed over graphene/TiO{sub 2} nanorodmore » hybrid composite photocatalysts, as 3.7 times larger than that of pristine TiO{sub 2} nanorods. This work demonstrated that the synthesis of TiO{sub 2} nanorods and simultaneous conversion of GO to graphene “without using reducing agents” had shown to be a rapid, direct and clean approach to fabricate chemically bonded graphene/TiO{sub 2} nanorod hybrid composites with enhanced photocatalytic performance.« less

ZnO Nano-Rod Devices for Intradermal Delivery and Immunization.

PubMed

Nayak, Tapas R; Wang, Hao; Pant, Aakansha; Zheng, Minrui; Junginger, Hans; Goh, Wei Jiang; Lee, Choon Keong; Zou, Shui; Alonso, Sylvie; Czarny, Bertrand; Storm, Gert; Sow, Chorng Haur; Lee, Chengkuo; Pastorin, Giorgia

2017-06-15

Intradermal delivery of antigens for vaccination is a very attractive approach since the skin provides a rich network of antigen presenting cells, which aid in stimulating an immune response. Numerous intradermal techniques have been developed to enhance penetration across the skin. However, these methods are invasive and/or affect the skin integrity. Hence, our group has devised zinc oxide (ZnO) nano-rods for non-destructive drug delivery. Chemical vapour deposition was used to fabricate aligned nano-rods on ZnO pre-coated silicon chips. The nano-rods' length and diameter were found to depend on the temperature, time, quality of sputtered silicon chips, etc. Vertically aligned ZnO nano-rods with lengths of 30-35 µm and diameters of 200-300 nm were selected for in vitro human skin permeation studies using Franz cells with Albumin-fluorescein isothiocyanate (FITC) absorbed on the nano-rods. Fluorescence and confocal studies on the skin samples showed FITC penetration through the skin along the channels formed by the nano-rods. Bradford protein assay on the collected fluid samples indicated a significant quantity of Albumin-FITC in the first 12 h. Low antibody titres were observed with immunisation on Balb/c mice with ovalbumin (OVA) antigen coated on the nano-rod chips. Nonetheless, due to the reduced dimensions of the nano-rods, our device offers the additional advantage of excluding the simultaneous entrance of microbial pathogens. Taken together, these results showed that ZnO nano-rods hold the potential for a safe, non-invasive, and painless intradermal drug delivery.

Geometric and compositional factors on critical current density in YBa2Cu3O7‑δ films containing nanorods

NASA Astrophysics Data System (ADS)

Horide, Tomoya; Nagao, Sho; Izutsu, Ryosuke; Ishimaru, Manabu; Kita, Ryusuke; Matsumoto, Kaname

2018-06-01

Critical current density (J c) was investigated in YBa2Cu3O7‑δ films containing nanorods prepared with various nanorod materials, with variation of nanorod content, substrate temperature, and oxidization condition. Three types of compositional situation were realized: films containing strain induced oxygen vacancies; fully oxidized films containing cation compositional deviation; and oxygen deficient films. Normalized J c‑B behavior was determined via the matching field, which is a geometric factor, regardless of the compositional details. A J c‑critical temperature (T c) relation depending on distribution and fraction of compositional deviation (cation compositional deviation and strain induced oxygen vacancies) was found: the J c values decreased with decreasing T c due to the effect of T c on nanorod pinning strength in the fully oxidized films; J c decreased with decreasing oxygen pressure in the film cooling process after film deposition in spite of T c remaining almost the same, due to reduction of the effective area for current flow in the oxygen deficient films. Thus, a J c landscape based on geometric and compositional factors was obtained. The study highlights the importance of the J c‑T c analysis in the understanding of J c in YBa2Cu3O7‑δ films containing nanorods.

Maximizing omnidirectional light harvesting in metal oxide hyperbranched array architectures

NASA Astrophysics Data System (ADS)

Wu, Wu-Qiang; Feng, Hao-Lin; Rao, Hua-Shang; Xu, Yang-Fan; Kuang, Dai-Bin; Su, Cheng-Yong

2014-05-01

The scrupulous design of nanoarchitectures and smart hybridization of specific active materials are closely related to the overall photovoltaic performance of an anode electrode. Here we present a solution-based strategy for the fabrication of well-aligned metal oxide-based nanowire-nanosheet-nanorod hyperbranched arrays on transparent conducting oxide substrates. For these hyperbranched arrays, we observe a twofold increment in dye adsorption and enhanced light trapping and scattering capability compared with the pristine titanium dioxide nanowires, and thus a power conversion efficiency of 9.09% is achieved. Our growth approach presents a strategy to broaden the photoresponse and maximize the light-harvesting efficiency of arrays architectures, and may lead to applications for energy conversion and storage, catalysis, water splitting and gas sensing.

Maximizing omnidirectional light harvesting in metal oxide hyperbranched array architectures.

PubMed

Wu, Wu-Qiang; Feng, Hao-Lin; Rao, Hua-Shang; Xu, Yang-Fan; Kuang, Dai-Bin; Su, Cheng-Yong

2014-05-29

The scrupulous design of nanoarchitectures and smart hybridization of specific active materials are closely related to the overall photovoltaic performance of an anode electrode. Here we present a solution-based strategy for the fabrication of well-aligned metal oxide-based nanowire-nanosheet-nanorod hyperbranched arrays on transparent conducting oxide substrates. For these hyperbranched arrays, we observe a twofold increment in dye adsorption and enhanced light trapping and scattering capability compared with the pristine titanium dioxide nanowires, and thus a power conversion efficiency of 9.09% is achieved. Our growth approach presents a strategy to broaden the photoresponse and maximize the light-harvesting efficiency of arrays architectures, and may lead to applications for energy conversion and storage, catalysis, water splitting and gas sensing.

Facile growth of barium oxide nanorods: structural and optical properties.

PubMed

Ahmad, Naushad; Wahab, Rizwan; Alam, Manawwer

2014-07-01

This paper reports a large-scale synthesis of barium oxide nanorods (BaO-NRs) by simple solution method at a very low-temperature of - 60 degrees C. The as-grown BaO-NRs were characterized in terms of their morphological, structural, compositional, optical and thermal properties. The morphological characterizations of as-synthesized nanorods were done by scanning electron microscopy (SEM) which confirmed that the synthesized products are rod shaped and grown in high density. The nanorods exhibits smooth and clean surfaces throughout their lengths. The crystalline property of the material was analyzed with X-ray diffraction pattern (XRD). The compositional and thermal properties of synthesized nanorods were observed via Fourier transform infrared (FTIR) spectroscopy and thermogravimetric analysis which confirmed that the synthesized nanorods are pure BaO and showed good thermal stability. The nanorods exhibited good optical properties as was confirmed from the room-temperature UV-vis spectroscopy. Finally, a plausible mechanism for the formation of BaO-NRs is also discussed in this paper.

Hydrodynamic fabrication of structurally gradient ZnO nanorods.

PubMed

Kim, Hyung Min; Youn, Jae Ryoun; Song, Young Seok

2016-02-26

We studied a new approach where structurally gradient nanostructures were fabricated by means of hydrodynamics. Zinc oxide (ZnO) nanorods were synthesized in a drag-driven rotational flow in a controlled manner. The structural characteristics of nanorods such as orientation and diameter were determined by momentum and mass transfer at the substrate surface. The nucleation of ZnO was induced by shear stress which plays a key role in determining the orientation of ZnO nanorods. The nucleation and growth of such nanostructures were modeled theoretically and analyzed numerically to understand the underlying physics of the fabrication of nanostructures controlled by hydrodynamics. The findings demonstrated that the precise control of momentum and mass transfer enabled the formation of ZnO nanorods with a structural gradient in diameter and orientation.

Vibrations of single-crystal gold nanorods and nanowires

NASA Astrophysics Data System (ADS)

Saviot, L.

2018-04-01

The vibrations of gold nanowires and nanorods are investigated numerically in the framework of continuum elasticity using the Rayleigh-Ritz variational method. Special attention is paid to identify the vibrations relevant in Raman scattering experiments. A comprehensive description of the vibrations of nanorods is proposed by determining their symmetry, comparing with standing waves in the corresponding nanowires, and estimating their Raman intensity. The role of experimentally relevant parameters such as the anisotropic cubic lattice structure, the presence of faceted lateral surfaces, and the shape of the ends of the nanorods is evaluated. Elastic anisotropy is shown to play a significant role contrarily to the presence of facets. Localized vibrations are found for nanorods with flat ends. Their evolution as the shape of the ends is changed to half-spheres is discussed.

Soluble Molecularly Imprinted Nanorods for Homogeneous Molecular Recognition

NASA Astrophysics Data System (ADS)

Liang, Rongning; Wang, Tiantian; Zhang, Huan; Yao, Ruiqing; Qin, Wei

2018-03-01

Nowadays, it is still difficult for molecularly imprinted polymer (MIPs) to achieve homogeneous recognition since they cannot be easily dissolved in organic or aqueous phase. To address this issue, soluble molecularly imprinted nanorods have been synthesized by using soluble polyaniline doped with a functionalized organic protonic acid as the polymer matrix. By employing 1-naphthoic acid as a model, the proposed imprinted nanorods exhibit an excellent solubility and good homogeneous recognition ability. The imprinting factor for the soluble imprinted nanoroads is 6.8. The equilibrium dissociation constant and the apparent maximum number of the proposed imprinted nanorods are 248.5 μM and 22.1 μmol/g, respectively. We believe that such imprinted nanorods may provide an appealing substitute for natural receptors in homogeneous recognition related fields.

Enhancement of UV photodetector properties of ZnO nanorods/PEDOT:PSS Schottky junction by NGQD sensitization along with conductivity improvement of PEDOT:PSS by DMSO additive