Structural and photoluminescence properties of silicon nanowires extracted by means of a centrifugation process from plasma torch synthesized silicon nanopowder.

PubMed

Le Borgne, Vincent; Agati, Marta; Boninelli, Simona; Castrucci, Paola; De Crescenzi, Maurizio; Dolbec, Richard; El Khakani, My Ali

2017-07-14

We report on a method for the extraction of silicon nanowires (SiNWs) from the by-product of a plasma torch based spheroidization process of silicon. This by-product is a nanopowder which consists of a mixture of SiNWs and silicon particles. By optimizing a centrifugation based process, we were able to extract substantial amounts of highly pure Si nanomaterials (mainly SiNWs and Si nanospheres (SiNSs)). While the purified SiNWs were found to have typical outer diameters in the 10-15 nm range and lengths of up to several μm, the SiNSs have external diameters in the 10-100 nm range. Interestingly, the SiNWs are found to have a thinner Si core (2-5 nm diam.) and an outer silicon oxide shell (with a typical thickness of ∼5-10 nm). High resolution transmission electron microscopy (HRTEM) observations revealed that many SiNWs have a continuous cylindrical core, whereas others feature a discontinuous core consisting of a chain of Si nanocrystals forming a sort of 'chaplet-like' structures. These plasma-torch-produced SiNWs are highly pure with no trace of any metal catalyst, suggesting that they mostly form through SiO-catalyzed growth scheme rather than from metal-catalyzed path. The extracted Si nanostructures are shown to exhibit a strong photoluminescence (PL) which is found to blue-shift from 950 to 680 nm as the core size of the Si nanostructures decreases from ∼5 to ∼3 nm. This near IR-visible PL is shown to originate from quantum confinement (QC) in Si nanostructures. Consistently, the sizes of the Si nanocrystals directly determined from HRTEM images corroborate well with those expected by QC theory.

Structural and photoluminescence properties of silicon nanowires extracted by means of a centrifugation process from plasma torch synthesized silicon nanopowder

NASA Astrophysics Data System (ADS)

Le Borgne, Vincent; Agati, Marta; Boninelli, Simona; Castrucci, Paola; De Crescenzi, Maurizio; Dolbec, Richard; El Khakani, My Ali

2017-07-01

We report on a method for the extraction of silicon nanowires (SiNWs) from the by-product of a plasma torch based spheroidization process of silicon. This by-product is a nanopowder which consists of a mixture of SiNWs and silicon particles. By optimizing a centrifugation based process, we were able to extract substantial amounts of highly pure Si nanomaterials (mainly SiNWs and Si nanospheres (SiNSs)). While the purified SiNWs were found to have typical outer diameters in the 10-15 nm range and lengths of up to several μm, the SiNSs have external diameters in the 10-100 nm range. Interestingly, the SiNWs are found to have a thinner Si core (2-5 nm diam.) and an outer silicon oxide shell (with a typical thickness of ˜5-10 nm). High resolution transmission electron microscopy (HRTEM) observations revealed that many SiNWs have a continuous cylindrical core, whereas others feature a discontinuous core consisting of a chain of Si nanocrystals forming a sort of ‘chaplet-like’ structures. These plasma-torch-produced SiNWs are highly pure with no trace of any metal catalyst, suggesting that they mostly form through SiO-catalyzed growth scheme rather than from metal-catalyzed path. The extracted Si nanostructures are shown to exhibit a strong photoluminescence (PL) which is found to blue-shift from 950 to 680 nm as the core size of the Si nanostructures decreases from ˜5 to ˜3 nm. This near IR-visible PL is shown to originate from quantum confinement (QC) in Si nanostructures. Consistently, the sizes of the Si nanocrystals directly determined from HRTEM images corroborate well with those expected by QC theory.

The effect of different temperature profiles upon the length and crystallinity of vertically-aligned multi-walled carbon nanotubes.

PubMed

Yun, Jongju; Lee, Cheesung; Zheng, Qing; Baik, Seunghyun

2012-08-01

We synthesized vertically-aligned multi-walled carbon nanotubes with an inner diameter of 1.6-7.5 nm and stack height of 80-28600 microm by chemical vapor deposition. The effects of synthesis conditions such as substrate position in the tube furnace, maximum temperature, temperature increasing rate and synthesis duration on the structure of nanotubes were investigated. It was found that slightly faster temperature increase rate resulted in significantly longer length, larger diameter and more defects of nanotubes. Structural parameters such as inner, outer diameters, wall thickness and defects were investigated using transmission electron microscopy and Raman spectroscopy.

Facile Fabrication of Uniform Polyaniline Nanotubes with Tubular Aluminosilicates as Templates

PubMed Central

2008-01-01

The uniform polyaniline (PANI) nanotubes, with inner diameter, outer diameter, and tubular thickness of 40, 60, and 10 nm, respectively, were prepared successfully by using natural tubular aluminosilicates as templates. The halloysite nanotubes were coated with PANI via the in situ chemical oxidation polymerization. Then the templates were etched with HCl/HF solution. The PANI nanotubes were characterized using FTIR, X-ray diffraction, and transmission electron microscopy. The conductivity of the PANI nanotubes was found to be 1.752 × 10−5(Ω·cm)−1.

Facile Fabrication of Uniform Polyaniline Nanotubes with Tubular Aluminosilicates as Templates

NASA Astrophysics Data System (ADS)

Zhang, Long; Liu, Peng

2008-08-01

The uniform polyaniline (PANI) nanotubes, with inner diameter, outer diameter, and tubular thickness of 40, 60, and 10 nm, respectively, were prepared successfully by using natural tubular aluminosilicates as templates. The halloysite nanotubes were coated with PANI via the in situ chemical oxidation polymerization. Then the templates were etched with HCl/HF solution. The PANI nanotubes were characterized using FTIR, X-ray diffraction, and transmission electron microscopy. The conductivity of the PANI nanotubes was found to be 1.752 × 10-5 (Ω·cm)-1.

Positive contact, self retaining bearing seals

DOEpatents

Johnson, Bruce H.; Larsen, Lawrence E.; Welch, Edmund F.

1992-05-05

An ultra-low friction bearing including an inner race, an outer race, bearing elements engaged between the inner and outer races and a seal between the inner and outer races is disclosed. The seal includes first and second sealing washers. The first washer has an outer diameter greater than an inner diameter of the outer race and an inner diameter greater than the outer diameter of the inner race. The second washer has an inner diameter less than the outer diameter of the inner race and an outer diameter less than the inner diameter of the outer race. The first washer slidably engages the outer race, the second washer slidably engages the inner race and the washers overlap and slidably engage one another. One of the washers snap fits into its respective inner or outer race while the other washer engages a stepped surface of the other of the inner and outer races. The grooved and stepped surface are offset from one another in a longitudinal direction of the races such that the washers are conically loaded thus providing a seal between the inner and outer races sufficient to prevent lubricant and contaminating particles from passing therethrough. The washers are made from a non-metallic semi-flexible low-modulus material.

Fine tuning of nanopipettes using atomic layer deposition for single molecule sensing.

PubMed

Sze, Jasmine Y Y; Kumar, Shailabh; Ivanov, Aleksandar P; Oh, Sang-Hyun; Edel, Joshua B

2015-07-21

Nanopipettes are an attractive single-molecule tool for identification and characterisation of nucleic acids and proteins in solutions. They enable label-free analysis and reveal individual molecular properties, which are generally masked by ensemble averaging. Having control over the pore dimensions is vital to ensure that the dimensions of the molecules being probed match those of the pore for optimization of the signal to noise. Although nanopipettes are simple and easy to fabricate, challenges exist, especially when compared to more conventional solid-state analogues. For example, a sub-20 nm pore diameter can be difficult to fabricate and the batch-to-batch reproducibility is often poor. To improve on this limitation, atomic layer deposition (ALD) is used to deposit ultrathin layers of alumina (Al2O3) on the surface of the quartz nanopipettes enabling sub-nm tuning of the pore dimensions. Here, Al2O3 with a thickness of 8, 14 and 17 nm was deposited onto pipettes with a starting pore diameter of 75 ± 5 nm whilst a second batch had 5 and 8 nm Al2O3 deposited with a starting pore diameter of 25 ± 3 nm respectively. This highly conformal process coats both the inner and outer surfaces of pipettes and resulted in the fabrication of pore diameters as low as 7.5 nm. We show that Al2O3 modified pores do not interfere with the sensing ability of the nanopipettes and can be used for high signal-to-noise DNA detection. ALD provides a quick and efficient (batch processing) for fine-tuning nanopipettes for a broad range of applications including the detection of small biomolecules like RNA, aptamers and DNA-protein interactions at the single molecule level.

Visual and functional demonstration of growing Bax-induced pores in mitochondrial outer membranes

PubMed Central

Gillies, Laura A; Du, Han; Peters, Bjoern; Knudson, C. Michael; Newmeyer, Donald D.; Kuwana, Tomomi

2015-01-01

Bax induces mitochondrial outer membrane permeabilization (MOMP), a critical step in apoptosis in which proteins are released into the cytoplasm. To resolve aspects of the mechanism, we used cryo-electron microscopy (cryo-EM) to visualize Bax-induced pores in purified mitochondrial outer membranes (MOMs). We observed solitary pores that exhibited negative curvature at their edges. Over time, the pores grew to ∼100–160 nm in diameter after 60–90 min, with some pores measuring more than 300 nm. We confirmed these results using flow cytometry, which we used to monitor the release of fluorescent dextrans from isolated MOM vesicles. The dextran molecules were released gradually, in a manner constrained by pore size. However, the release rates were consistent over a range of dextran sizes (10–500 kDa). We concluded that the pores were not static but widened dramatically to release molecules of different sizes. Taken together, the data from cryo-EM and flow cytometry argue that Bax promotes MOMP by inducing the formation of large, growing pores through a mechanism involving membrane-curvature stress. PMID:25411335

Proteomic characterization of the outer membrane vesicle of the halophilic marine bacterium Novosphingobium pentaromativorans US6-1.

PubMed

Yun, Sung Ho; Lee, Sang-Yeop; Choi, Chi-Won; Lee, Hayoung; Ro, Hyun-Joo; Jun, Sangmi; Kwon, Yong Min; Kwon, Kae Kyoung; Kim, Sang-Jin; Kim, Gun-Hwa; Kim, Seung Il

2017-01-01

Novosphingobium pentaromativorans US6-1 is a Gram-negative halophilic marine bacterium able to utilize several polycyclic aromatic hydrocarbons such as phenanthrene, pyrene, and benzo[a]pyrene. In this study, using transmission electron microscopy, we confirmed that N. pentaromativorans US6-1 produces outer membrane vesicles (OMVs). N. pentaromativorans OMVs (hereafter OMV Novo ) are spherical in shape, and the average diameter of OMV Novo is 25-70 nm. Proteomic analysis revealed that outer membrane proteins and periplasmic proteins of N. pentaromativorans are the major protein components of OMV Novo . Comparative proteomic analysis with the membrane-associated protein fraction and correlation analysis demonstrated that the outer membrane proteins of OMV Novo originated from the membrane- associated protein fraction. To the best of our knowledge, this study is the first to characterize OMV purified from halophilic marine bacteria.

Composite microparticles of halloysite clay nanotubes bound by calcium carbonate.

PubMed

Jin, Yi; Yendluri, Raghuvara; Chen, Bin; Wang, Jingbo; Lvov, Yuri

2016-03-15

Natural halloysite clay nanotubes with 15 nm inner and 75 nm outer diameters have been used as vehicles for sustained release of drugs in composite hollow microparticles "glued" with CaCO3. We used a layer-by layer assembly accomplished alginate binding with Ca(2+) followed by CO2 bubbling to prepare the composite microspheres of CaCO3 and polyelectrolytes (PE) modified halloysite nanotubes (HNTs-PE2/CaCO3) with the diameter of about 5-10 μm. These microparticles have empty spherical structure and abundant pore distributions with maxima at 2.5, 3.9, 6.0 and 13.3 nm, and higher surface area of 82.3 m(2) g(-1) as characterized by SEM and BET test. We loaded drugs in these micro-nano carriers of tight piles of halloysite nanotube with end clogged with CaCO3. The sustained release of Nifedipine drug from HNTs-PE2/CaCO3 composite microspheres was slower than for pristine halloysite nanotubes. Copyright © 2015 Elsevier Inc. All rights reserved.

Nanocomposites Derived From a Low-Color Aromatic Polyimide (CP2) and Amine-Functionalized Vapor-Grown Carbon Nanofibers: In Situ Polymerization and Characterization (Preprint)

DTIC Science & Technology

2007-01-01

small metal catalyst (e.g., ferrocene, Fe (CO)5, etc.). They have an outer diameter of 60-200 nm, a hollow core of 30-90 nm, and length on the order...diffractions (WAXS) of compression-molded samples were recorded with a Rigaku RU-200 diffractometer using Ni-filtered Cu KR radiation (40 kV, 100 mA, λ...attributable to the sp3 C-H and sp2 C-H defects as methane is used as the major component in the feedstock for its production . Based on hydrogen

Gas turbine structural mounting arrangement between combustion gas duct annular chamber and turbine vane carrier

DOEpatents

Wiebe, David J.; Charron, Richard C.; Morrison, Jay A.

2016-10-18

A gas turbine engine ducting arrangement (10), including: an annular chamber (14) configured to receive a plurality of discrete flows of combustion gases originating in respective can combustors and to deliver the discrete flows to a turbine inlet annulus, wherein the annular chamber includes an inner diameter (52) and an outer diameter (60); an outer diameter mounting arrangement (34) configured to permit relative radial movement and to prevent relative axial and circumferential movement between the outer diameter and a turbine vane carrier (20); and an inner diameter mounting arrangement (36) including a bracket (64) secured to the turbine vane carrier, wherein the bracket is configured to permit the inner diameter to move radially with the outer diameter and prevent axial deflection of the inner diameter with respect to the outer diameter.

Small cell foams containing a modified dense star polymer or dendrimer as a nucleating agent

DOEpatents

Hedstrand, David M.; Tomalia, Donald A.

1995-01-01

A small cell foam having a modified dense star polymer or dendrimer is described. This modified dense star polymer or dendrimer has a highly branched interior of one monomeric composition and an exterior structure of a different monomeric composition capable of providing a hydrophobic outer shell and a particle diameter of from about 5 to about 1,000 nm with a matrix polymer.

Small cell foams containing a modified dense star polymer or dendrimer as a nucleating agent

DOEpatents

Hedstrand, D.M.; Tomalia, D.A.

1995-02-28

A small cell foam having a modified dense star polymer or dendrimer is described. This modified dense star polymer or dendrimer has a highly branched interior of one monomeric composition and an exterior structure of a different monomeric composition capable of providing a hydrophobic outer shell and a particle diameter of from about 5 to about 1,000 nm with a matrix polymer.

Large size self-assembled quantum rings: quantum size effect and modulation on the surface diffusion.

PubMed

Tong, Cunzhu; Yoon, Soon Fatt; Wang, Lijun

2012-09-24

We demonstrate experimentally the submicron size self-assembled (SA) GaAs quantum rings (QRs) by quantum size effect (QSE). An ultrathin In0.1 Ga0.9As layer with different thickness is deposited on the GaAs to modulate the surface nucleus diffusion barrier, and then the SA QRs are grown. It is found that the density of QRs is affected significantly by the thickness of inserted In0.1 Ga0.9As, and the diffusion barrier modulation reflects mainly on the first five monolayer . The physical mechanism behind is discussed. The further analysis shows that about 160 meV decrease in diffusion barrier can be achieved, which allows the SA QRs with density of as low as one QR per 6 μm2. Finally, the QRs with diameters of 438 nm and outer diameters of 736 nm are fabricated using QSE.

Direct Synthesis of Carbon Nanotubes at Low Temperature by the Reaction of CCl4 and Ferrocene

NASA Astrophysics Data System (ADS)

Luo, Wei; Tang, Yan; He, Mingsheng; Ouyang, Degang; Ding, Cuijiao; Han, Bin; Zhu, Shanhe; Li, Minghui

Islands-like amorphous carbon nanotubes (a-CNTs) and multi-wall carbon nanotubes (MWCNTs) have been synthesized by the reaction of CCl4 and ferrocene without or with Co/N alloy as growth catalyst at 160 and 350 ºC, respectively. The as-obtained products are characterized by FESEM, TEM, HRTEM, Raman spectroscopy, and nitrogen adsorption-desorption analysis. The results show that a-CNTs have an outer diameter around 450 nm and a length of up to 5 μm, whereas MWCNTs are 20 nm in diameter and 1.5 μm in length. The specific surface area of a-CNTs and MWCNTs are determined to be 1092 and 364 m2×g-1, respectively. Dichlorocarbene and cyclopentadienyl groups are proved to be the reaction intermediates by GC-MS measurements. A possible growth mechanism of the a-CNTs and MWCNTs has been proposed.

One-dimensional arrangement of nanoparticles utilizing the V-groove and cage shaped proteins

NASA Astrophysics Data System (ADS)

Ban, Takahiko; Uenuma, Mutsunori; Migita, Shinji; Okamoto, Naofumi; Ishikawa, Yasuaki; Uraoka, Yukiharu; Yamashita, Ichiro; Yamamoto, Shin-ichi

2017-06-01

The one-dimensional arrangement of nanoparticles (NPs) was performed using a V-groove and ferritins as spherical shell proteins. The V-groove was synthesized by lithography and anisotropic etching of a Si substrate. Ferritin has an outer diameter of 12 nm and an inner diameter of 6 nm, and various inorganic substances can be formed into the cavity. In this study, iron oxide, cobalt oxide, and indium oxide cores were used. The surface potential of ferritin can be changed by genetic modification. Particularly, by using Fer8-K98E, NPs could be arranged one-dimensionally onto the bottom of the V-groove. In addition, we succeeded in selectively forming a one-dimensional array of one layer, two layers, and three layers by changing the protein concentration. This experiment is expected to be applicable to various one-dimensional devices.

Electrolytic Generation of Nano-Scale Carbon Phases with Framework Structures in Molten Salts on Metal Cathodes

NASA Astrophysics Data System (ADS)

Novoselova, Inessa A.; Oliinyk, Nikolai F.; Voronina, Anastasiya B.; Volkov, Sergei V.

2008-08-01

An electrochemical study of mechanisms of electrodeposition of carbon solid phases from halide melts (Na,K|Cl; Na,K,Cs|Cl), saturated with carbon dioxide under an excessive pressure of up to 1.5 MPa, has been carried out in the temperature range 550 - 850 °C by cyclic voltammetry. It has been found that the cathode process occurs in three steps at sweep rates of less than 0.1 Vs-1, and its electrochemical-chemical-electrochemical (ECE) mechanism is suggested. It has furthermore been found that cathodic deposits contain nano-sized carbon particles of different forms and structure: blocks of amorphous carbon, crystalline graphite, carbon nanotubes (CNT), and nanofibres. The outer diameter of the tubes is 5 - 250 nm, and the internal diameter is 2 - 140 nm. A correlation between the product structure and yield against electrolysis conditions and regimes has been established.

High-Q Hybrid Plasmon-Photon Modes in a Bottle Resonator Realized with a Silver-Coated Glass Fiber with a Varying Diameter

NASA Astrophysics Data System (ADS)

Rottler, Andreas; Harland, Malte; Bröll, Markus; Klingbeil, Matthias; Ehlermann, Jens; Mendach, Stefan

2013-12-01

We experimentally demonstrate that hybrid plasmon-photon modes exist in a silver-coated glass bottle resonator. The bottle resonator is realized in a glass fiber with a smoothly varying diameter, which is subsequently coated with a rhodamine 800-dye doped acryl-glass layer and a 30 nm thick silver layer. We show by means of photoluminescence experiments supported by electromagnetic simulations that the rhodamine 800 photoluminescence excites hybrid plasmon-photon modes in such a bottle resonator, which provide a plasmon-type field enhancement at the outer silver surface and exhibit quality factors as high as 1000.

The truth about laser fiber diameters.

PubMed

Kronenberg, Peter; Traxer, Olivier

2014-12-01

To measure the various diameters of laser fibers from various manufacturers and compare them with the advertised diameter. Fourteen different unused laser fibers from 6 leading manufacturers with advertised diameters of 200, 270, 272, 273, 365, and 400 μm were measured by light microscopy. The outer diameter (including the fiber coating, cladding, and core), cladding diameter (including the cladding and the fiber core), and core diameter were measured. Industry representatives of the manufacturers were interviewed about the diameter of their fibers. For all fibers, the outer and cladding diameters differed significantly from the advertised diameter (P <.00001). The outer diameter, which is of most practical relevance for urologists, exhibited a median increase of 87.3% (range, 50.7%-116.7%). The outer, cladding, and core diameters of fibers with equivalent advertised diameters differed by up to 180, 100, and 78 μm, respectively. Some 200-μm fibers had larger outer diameters than the 270- to 273-μm fibers. All packaging material and all laser fibers lacked clear and precise fiber diameter information labels. Of 12 representatives interviewed, 8, 3, and 1 considered the advertised diameter to be the outer, the cladding, and the core diameter, respectively. Representatives within the same company frequently gave different answers. This study suggests that, at present, there is a lack of uniformity between laser fiber manufacturers, and most of the information conveyed to urologists regarding laser fiber diameter may be incorrect. Because fibers larger than the advertised laser fibers are known to influence key interventional parameters, this misinformation can have surgical repercussions. Copyright © 2014 Elsevier Inc. All rights reserved.

Comparison of 980-nm and 1070-nm in endovenous laser treatment (EVLT)

NASA Astrophysics Data System (ADS)

Topaloglu, Nermin; Tabakoglu, Ozgur; Ergenoglu, Mehmet U.; Gülsoy, Murat

2009-07-01

The use of endovenous laser treatment for varicose veins has been increasing in recent years. It is a safer technique than surgical vein stripping. Its complications (e.g. bruising, pain) are less than the complications of surgical vein stripping. But best parameters such as optimum wavelength, power, and application duration are still under investigation to clarify uncertainties about this technique. To prevent its complications and improve its clinical outcomes, the exact mechanism of it has to be known. The aim of this study is to investigate the effect of different laser wavelengths on endovenous laser therapy. In this study 980-nm diode laser and 1070-nm fiber laser were used. Human veins were irradiated with 980-nm and 1070-nm lasers at 8 W and 10 W to find the optimal power and wavelength. After laser application, remarkable shrinkage was observed. Inner and outer diameters of the veins also narrowed for both of the laser types. 10 W of 980-nm laser application led to better shrinkage results.

Nanoscale Hollow Spheres: Microemulsion-Based Synthesis, Structural Characterization and Container-Type Functionality

PubMed Central

Gröger, Henriette; Kind, Christian; Leidinger, Peter; Roming, Marcus; Feldmann, Claus

2010-01-01

A wide variety of nanoscale hollow spheres can be obtained via a microemulsion approach. This includes oxides (e.g., ZnO, TiO2, SnO2, AlO(OH), La(OH)3), sulfides (e.g., Cu2S, CuS) as well as elemental metals (e.g., Ag, Au). All hollow spheres are realized with outer diameters of 10−60 nm, an inner cavity size of 2−30 nm and a wall thickness of 2−15 nm. The microemulsion approach allows modification of the composition of the hollow spheres, fine-tuning their diameter and encapsulation of various ingredients inside the resulting “nanocontainers”. This review summarizes the experimental conditions of synthesis and compares them to other methods of preparing hollow spheres. Moreover, the structural characterization and selected properties of the as-prepared hollow spheres are discussed. The latter is especially focused on container-functionalities with the encapsulation of inorganic salts (e.g., KSCN, K2S2O8, KF), biomolecules/bioactive molecules (e.g., phenylalanine, quercetin, nicotinic acid) and fluorescent dyes (e.g., rhodamine, riboflavin) as representative examples. PMID:28883333

Evaluation of rheological behavior of 10W40 lubricant containing hybrid nano-material by measuring dynamic viscosity

NASA Astrophysics Data System (ADS)

Ahmadi Nadooshan, Afshin; Hemmat Esfe, Mohammad; Afrand, Masoud

2017-08-01

In the present paper, the dynamic viscosity of 10W40 lubricant containing hybrid nano-materials has been examined. Hybrid nano-materials were composed of 90% of silica (SiO2) with 20-30 nm mean particle size and 10% of multi-walled carbon nanotubes (MWCNTs) with inner diameter of 2-6 nm and outer diameter of 5-20 nm. Nano-lubricant samples were prepared by two-step method with solid volume fractions of 0.05%, 0.1%, 0.25%, 0.5%, 0.75% and 1%. Dynamic viscosity of the samples was measured at temperatures between 5 and 55 °C and at shear rates of 666.5 s-1 up to 11,997 s-1. Experimental results indicated that the nano-lubricant had non-Newtonian behavior at all temperatures, while 10w40 oil was non-Newtonian only at high temperatures. With the use of the curve fitting technique of experimental data, power law and consistency indexes were obtained; furthermore, these coefficients were assessed by shear stress and viscosity diagram.

Carbon nanopipettes and microtubes for electrochemical sensing and microfluidics

NASA Astrophysics Data System (ADS)

Mani, Radhika C.; Bhimarasetti, Gopinath; Lowe, Randall; Sunkara, Mahendra K.

2004-12-01

We present the synthesis of two novel morphologies for carbon tubular structures: Nanopipettes and Micropipes. The synthesis procedures for both these structures are both unique and different from each other and the conventional methods used for carbon nanotubes. Carbon nanopipettes, open at both ends, are made up of a central nanotube (~10-20 nm) surrounded by helical sheets of graphite. Thus nanopipettes have an outer conical structure, with a base size of about a micron, that narrows down to about 10-20 nm at the tip. Due to their unique morphology, the outer walls of the nanopipettes continuously expose edge planes of graphite, giving a very stable and reversible electrochemical response for detecting neurological compounds such as dopamine. The synthesis of carbon nanopipettes is based on high temperature nucleation and growth of carbon nanotubes under conditions of hydrogen etching during growth. Carbon micropipes, on the other hand, are tubular structures whose internal diameters range from a few nanometers to a few microns with a constant wall thickness of 10-20 nm. In addition to tuning the internal diameters, the conical angles of these structures could also be changed during synthesis. Due to their larger inner diameters and thin walls, both the straight and conical micro-tubular structures are suitable for microfluidic devices such as throttle valves, micro-reactors, and distribution channels. The synthesis of carbon micro-tubular structures is based on the wetting behavior of gallium with carbon during growth. The contact angle between gallium and the carbon wall determines the conical angle of the structure. By varying the contact angle, one can alter the conical angles from 400 to -150, and synthesize straight tubes using different N2/O2 dosing compositions. An 'n-step' dosing sequence at various stages of growth resulted in 'n-staged' morphologies for carbon micro-tubular structures such as funnels, tube-on-cone, Y-junctions and dumbbells.

Spin-glass-like freezing of inner and outer surface layers in hollow γ-Fe 2O 3 nanoparticles

DOE PAGES

Khurshid, Hafsa; Lampen-Kelley, Paula; Iglesias, Òscar; ...

2015-10-27

Disorder among surface spins largely dominates the magnetic response of ultrafine magnetic particle systems. In this work, we examine time-dependent magnetization in high-quality, monodisperse hollow maghemite nanoparticles (NPs) with a 14.8±0.5 nm outer diameter and enhanced surface-to-volume ratio. The nanoparticle ensemble exhibits spin-glass-like signatures in dc magnetic aging and memory protocols and ac magnetic susceptibility. The dynamics of the system slow near 50 K, and becomes frozen on experimental time scales below 20 K. Remanence curves indicate the development of magnetic irreversibility concurrent with the freezing of the spin dynamics. A strong exchange-bias effect and its training behavior point tomore » highly frustrated surface spins that rearrange much more slowly than interior spins with bulk coordination. Monte Carlo simulations of a hollow particle reproducing the experimental morphology corroborate strongly disordered surface layers with complex energy landscapes that underlie both glass-like dynamics and magnetic irreversibility. Calculated hysteresis loops reveal that magnetic behavior is not identical at the inner and outer surfaces, with spins at the outer surface layer of the 15 nm hollow particles exhibiting a higher degree of frustration. Lastly, our combined experimental and simulated results shed light on the origin of spin-glass-like phenomena and the important role played by the surface spins in magnetic hollow nanostructures.« less

Spin-glass-like freezing of inner and outer surface layers in hollow γ-Fe2O3 nanoparticles

PubMed Central

Khurshid, Hafsa; Lampen-Kelley, Paula; Iglesias, Òscar; Alonso, Javier; Phan, Manh-Huong; Sun, Cheng-Jun; Saboungi, Marie-Louise; Srikanth, Hariharan

2015-01-01

Disorder among surface spins is a dominant factor in the magnetic response of magnetic nanoparticle systems. In this work, we examine time-dependent magnetization in high-quality, monodisperse hollow maghemite nanoparticles (NPs) with a 14.8 ± 0.5 nm outer diameter and enhanced surface-to-volume ratio. The nanoparticle ensemble exhibits spin-glass-like signatures in dc magnetic aging and memory protocols and ac magnetic susceptibility. The dynamics of the system slow near 50 K, and become frozen on experimental time scales below 20 K. Remanence curves indicate the development of magnetic irreversibility concurrent with the freezing of the spin dynamics. A strong exchange-bias effect and its training behavior point to highly frustrated surface spins that rearrange much more slowly than interior spins. Monte Carlo simulations of a hollow particle corroborate strongly disordered surface layers with complex energy landscapes that underlie both glass-like dynamics and magnetic irreversibility. Calculated hysteresis loops reveal that magnetic behavior is not identical at the inner and outer surfaces, with spins at the outer surface layer of the 15 nm hollow particles exhibiting a higher degree of frustration. Our combined experimental and simulated results shed light on the origin of spin-glass-like phenomena and the important role played by the surface spins in magnetic hollow nanostructures. PMID:26503506

Size-dependent melting modes and behaviors of Ag nanoparticles: a molecular dynamics study

NASA Astrophysics Data System (ADS)

Liang, Tianshou; Zhou, Dejian; Wu, Zhaohua; Shi, Pengpeng

2017-12-01

The size-dependent melting behaviors and mechanisms of Ag nanoparticles (NPs) with diameters of 3.5-16 nm were investigated by molecular dynamics (MD). Two distinct melting modes, non-premelting and premelting with transition ranges of about 7-8 nm, for Ag NPs were demonstrated via the evolution of distribution and transition of atomic physical states during annealing. The small Ag NPs (3.5-7 nm) melt abruptly without a stable liquid shell before the melting point, which is characterized as non-premelting. A solid-solid crystal transformation is conducted through the migration of adatoms on the surface of Ag NPs with diameters of 3.5-6 nm before the initial melting, which is mainly responsible for slightly increasing the melting point of Ag NPs. On the other hand, surface premelting of Ag NPs with diameters of 8-16 nm propagates from the outer shell to the inner core with initial anisotropy and late isotropy as the temperature increases, and the close-packed facets {111} melt by a side-consumed way which is responsible for facets {111} melting in advance relative to the crystallographic plane {111}. Once a stable liquid shell is formed, its size-independent minimum thickness is obtained, and a three-layer structure of atomic physical states is set up. Lastly, the theory of point defect-pair (vacancy-interstitial) severing as the mechanism of formation and movement of the solid-liquid interface was also confirmed. Our study provides a basic understanding and theoretical guidance for the research, production and application of Ag NPs.

Molecular characterization of outer membrane vesicles released from Acinetobacter radioresistens and their potential roles in pathogenesis.

PubMed

Fulsundar, Shweta; Kulkarni, Heramb M; Jagannadham, Medicharla V; Nair, Rashmi; Keerthi, Sravani; Sant, Pooja; Pardesi, Karishma; Bellare, Jayesh; Chopade, Balu Ananda

2015-01-01

Acinetobacter radioresistens is an important member of genus Acinetobacter from a clinical point of view. In the present study, we report that a clinical isolate of A. radioresistens releases outer membrane vesicles (OMVs) under in vitro growth conditions. OMVs were released in distinctive size ranges with diameters from 10 to 150 nm as measured by the dynamic light scattering (DLS) technique. Additionally, proteins associated with or present into OMVs were identified using LC-ESI-MS/MS. A total of 71 proteins derived from cytosolic, cell membrane, periplasmic space, outer membrane (OM), extracellular and undetermined locations were found in OMVs. The initial characterization of the OMV proteome revealed a correlation of some proteins to biofilm, quorum sensing, oxidative stress tolerance, and cytotoxicity functions. Thus, the OMVs of A. radioresistens are suggested to play a role in biofilm augmentation and virulence possibly by inducing apoptosis. Copyright © 2015 Elsevier Ltd. All rights reserved.

Ultra-Compact Multitip Scanning Probe Microscope with an Outer Diameter of 50 mm

NASA Astrophysics Data System (ADS)

Cherepanov, Vasily; Zubkov, Evgeny; Junker, Hubertus; Korte, Stefan; Blab, Marcus; Coenen, Peter; Voigtländer, Bert

We present a multitip scanning tunneling microscope (STM) where four independent STM units are integrated on a diameter of 50 mm. The coarse positioning of the tips is done under the control of an optical microscope or an SEM in vacuum. The heart of this STM is a new type of piezoelectric coarse approach called Koala Drive which can have a diameter greater than 2.5 mm and a length smaller than 10 mm. Alternating movements of springs move a central tube which holds the STM tip or AFM sensor. This new operating principle provides a smooth travel sequence and avoids shaking which is intrinsically present for nanopositioners based on inertial motion with saw tooth driving signals. Inserting the Koala Drive in a piezo tube for xyz-scanning integrates a complete STM inside a 4 mm outer diameter piezo tube of <10 mm length. The use of the Koala Drive makes the scanning probe microscopy design ultra-compact and accordingly leads to a high mechanical stability. The drive is UHV, low temperature, and magnetic field compatible. The compactness of the Koala Drive allows building a four-tip STM as small as a single-tip STM with a drift of <0.2 nm/min and lowest resonance frequencies of 2.5 (xy) and 5.5 kHz (z). We present examples of the performance of the multitip STM designed using the Koala Drive.

Highly Monodisperse Microporous Polymeric and Carbonaceous Nanospheres with Multifunctional Properties

PubMed Central

Ouyang, Yi; Shi, Huimin; Fu, Ruowen; Wu, Dingcai

2013-01-01

Fabrication of monodisperse porous polymeric nanospheres with diameters below 500 nm remains a great challenge, due to serious crosslinking between neighboring nanospheres during pore-making process. Here we show how a versatile hypercrosslinking strategy can be used to prepare monodisperse microporous polystyrene nanospheres (MMPNSs) with diameters as low as ca. 190 nm. In our approach, an unreactive crosslinked PS outer skin as protective layer can be in-situ formed at the very beginning of hypercrosslinking treatment to minimize the undesired inter-sphere crosslinking. The as-prepared MMPNSs with a well-developed microporous network demonstrate unusual multifunctional properties, including remarkable colloidal stability in aqueous solution, good adsorption-release property for drug, and large adsorption capacity toward organic vapors. Surprisingly, MMPNSs can be directly transformed into high-surface-area monodisperse carbon nanospheres with good colloidal stability via a facile hydrothermal-assisted carbonization procedure. These findings provide a new benchmark for fabricating well-defined porous nanospheres with great promise for various applications. PMID:23478487

Structure of Immune Stimulating Complex Matrices and Immune Stimulating Complexes in Suspension Determined by Small-Angle X-Ray Scattering

PubMed Central

Pedersen, Jan Skov; Oliveira, Cristiano L.P.; Hübschmann, Henriette Baun; Arleth, Lise; Manniche, Søren; Kirkby, Nicolai; Nielsen, Hanne Mørck

2012-01-01

Immune stimulating complex (ISCOM) particles consisting of a mixture of Quil-A, cholesterol, and phospholipids were structurally characterized by small-angle x-ray scattering (SAXS). The ISCOM particles are perforated vesicles of very well-defined structures. We developed and implemented a novel (to our knowledge) modeling method based on Monte Carlo simulation integrations to describe the SAXS data. This approach is similar to the traditional modeling of SAXS data, in which a structure is assumed, the scattering intensity is calculated, and structural parameters are optimized by weighted least-squares methods when the model scattering intensity is fitted to the experimental data. SAXS data from plain ISCOM matrix particles in aqueous suspension, as well as those from complete ISCOMs (i.e., with an antigen (tetanus toxoid) incorporated) can be modeled as a polydisperse distribution of perforated bilayer vesicles with icosahedral, football, or tennis ball structures. The dominating structure is the tennis ball structure, with an outer diameter of 40 nm and with 20 holes 5–6 nm in diameter. The lipid bilayer membrane is 4.6 nm thick, with a low-electron-density, 2.0-nm-thick hydrocarbon core. Surprisingly, in the ISCOMs, the tetanus toxoid is located just below the membrane inside the particles. PMID:22677391

In situ SEM Observation of Column-like and Foam-like CNT Array Nanoindentation

DTIC Science & Technology

2011-03-02

frompyrolization of iron(II) phthalocyanine , producing vertically aligned CNTs with a nominal outer diameter of 50 nm.11,12 The array was indented using a 40 40 μm...www.acsami.org In situ SEM Observation of Column-like and Foam-like CNT Array Nanoindentation Matthew R. Maschmann,†,‡Qiuhong Zhang,†,§ Robert Wheeler...multiple length scales. Their behavior is expected to rely heavily on the properties of individual constituent CNTs , interactions and load distribution

MEDULLARY THICK ASCENDING LIMB BUFFER VASOCONSTRICTION OF RENAL OUTER-MEDULLARY VASA RECTA IN SALT-RESISTANT BUT NOT SALT-SENSITIVE RATS

PubMed Central

O’Connor, Paul M.; Cowley, Allen W.

2013-01-01

We have previously demonstrated that paracrine signaling occurs between medullary thick ascending limb (mTAL) and the contractile pericytes of outer-medullary vasa recta (VR) termed ‘tubular-vascular cross talk’. The aim of the current study was to determine whether tubular-vascular cross talk has a functional effect on vasoconstrictor responses to angiotensin II, and to determine whether this is altered in the Dahl salt-sensitive (SS) rat. Studies were performed on salt-resistant consomic SS.13BN and SS rats using a novel outer medullary tissue strip preparation in which freshly isolated VR within VR bundles were perfused either alone or in combination with nearby mTAL. In VR from SS.13BN rats, angiotensin II (1μM) increased VR bundle intracellular Ca2+ concentration ([Ca2+]VR) 19±9nM (n=8) and reduced focal diameter in perfused VR by (−20±7%;n=5). In the presence of nearby mTAL however, [Ca2+]VR (−9±8nM; n=8) and VR diameter (−1±4%, n=7) in SS.13BN rats was unchanged by angiotensin II. In contrast, in Dahl SS rats, angiotensin II resulted in rapid and sustained increase in [Ca2+]VR (89±48 n=7;50±24% n=8) and a reduction in VR diameter of (−17±7;n=7 and −11±4%;n=5) in both isolated VR and VR with nearby mTAL, respectively. In VR with mTAL from SS13BN rats, inhibiton of purinergic receptors resulted in an increase in [Ca2+]VR, indicating purinergic signaling buffers vasoconstriction. Importantly, our in vitro data were able to predict medullary blood flow responses to angiotensin II in SS and SS.13BN rats in vivo. We conclude that paracrine signaling from mTAL buffers angiotensin II vasoconstriction in Dahl salt-resistant SS.13BN rats but not SS rats. PMID:22926950

The ultrastructure of rabbit sclera after scleral crosslinking with riboflavin and blue light of different intensities.

PubMed

Karl, Anett; Makarov, Felix N; Koch, Christian; Körber, Nicole; Schuldt, Carsten; Krüger, Martin; Reichenbach, Andreas; Wiedemann, Peter; Bringmann, Andreas; Iseli, Hans Peter; Francke, Mike

2016-08-01

We aimed to determine the ultrastructural changes of collagen fibrils and cells in the rabbit sclera after scleral crosslinking using riboflavin and blue light of different intensities. Scleral crosslinking is known to increase scleral stiffness and may inhibit the axial elongation of progressive myopic eyes. The equatorial parts of the sclera of one eye of six adult albino rabbits were treated with topical riboflavin solution (0.5 %) followed by irradiation with blue light (200, 400, 650 mW/cm(2)) for 20 min. After 3 weeks, the ultrastructure of scleral cells and the abundance of small- (10-100 nm) and large-diameter (>100 nm) collagen fibrils in fibril bundles of different scleral layers were examined with electron microscopy. In the scleral stroma of control eyes, the thickness of collagen fibrils showed a bimodal distribution. The abundance of small-diameter collagen fibrils decreased from the inner towards the outer sclera, while the amount of large-diameter fibrils and the scleral collagen content did not differ between different stroma layers. Treatment with riboflavin and blue light at 200 mW/cm(2) did not induce ultrastructural changes of cells and collagen fibrils in the scleral stroma. Treatment with blue light of higher intensities induced scleral cell activation in a scleral layer-dependent manner. In addition, outer scleral layers contained phagocytes that engulfed collagen fibrils and erythrocytes. Blue light of the highest intensity induced a reduction of the scleral collagen content, a decreased abundance of large-diameter collagen fibrils, and an increased amount of small-diameter fibrils in the whole scleral stroma. The data indicate that in rabbits, scleral crosslinking with riboflavin and blue light of 200 mW/cm(2) for 20 min is relatively safe and does not induce ultrastructural alterations of scleral cells and of the collagen composition of the scleral stroma. Irradiation with blue light of intensities between 200 and 400 mW/cm(2) induces scleral cell activation, which may contribute to scleral scarring and stiffening. Higher intensities cause scleritis.

Bulk nucleation and growth of inorganic nanowires and nanotubes

NASA Astrophysics Data System (ADS)

Sharma, Shashank

The nanometer scale materials such as nanowires and nanotubes will be of particular interest as building blocks for designing novel sensors, catalysts, electronic, optical, and optoelectronic devices. However, in order to realize these applications, bulk amounts of nanowires and nanotubes need to be synthesized with precise control over the nanostructure characteristics. In addition, the structure-property relationships for one-dimensional structures are expected to be different than their bulk when their diameters are less than a characteristic Bohr exciton radius. This fundamental curiosity also necessitates bulk synthesis of nanostructures. The current bulk nanowire synthesis methods utilize either nanometer scale porous molds or nanometer scale transition metal clusters to template one-dimensional growth. All these techniques have inherent limitations in terms of control over the nanowire diameter distribution, composition, the growth direction, and the ability to generate abrupt interfaces within individual nanowires. In this dissertation, a new concept for bulk nucleation and growth of one-dimensional nanostructures is proposed and demonstrated for a variety of inorganic material systems. In this technique, multiple nanowires nucleate and grow from pools of low-melting metal melts when exposed to an activated gas phase containing the necessary precursors. This concept, hereby termed Low Melting Metals and Activated Gas phase (LMAG) mediated method, is specifically demonstrated for the synthesis of, (a) silicon nanowires grown using molten gallium and silane precursors; (b) silicon compound nanowires using solution of molten gallium and appropriate gas phase precursors, and (c) metal-oxide nanostructures grown using direct reaction of the respective metal melts and oxygen precursors. Nanowires resulted from the same molten gallium pool at high densities (>1011/cm2) and with narrow diameter distribution. The silicon nanowires synthesized using the LMAG technique were single crystalline, defect free, and contained a non uniform, extremely thin oxide sheath (<1.5 nm). The nanowire diameter could be varied from 3 to 100 nm, with lengths up to hundreds of microns. Unique tubular and paintbrush-like morphologies were obtained in gallium oxide (Ga2O3) nanostructures. Small gallium droplets (<100 nm size) allowed Ga2O3 nanowire growth parallel to the substrate, followed by 2-dimensional nanoweb formation. These experiments using small gallium droplets resulted in the growth of crystalline Ga2O3 nanotubes with outer diameters as small as 5 nm and inner diameters as small as 2.5 nm.

Ultrathin Wall (1 nm) and Superlong Pt Nanotubes with Enhanced Oxygen Reduction Reaction Performance.

PubMed

Tao, Lu; Yu, Dan; Zhou, Junshuang; Lu, Xiong; Yang, Yunxia; Gao, Faming

2018-05-01

The synthesis of Pt nanotubes catalysts remains a substantial challenge, especially for those with both sub-nanometer wall thickness and micrometer-scale length characteristics. Combining techniques of insulin fibril template with Pd nanowire template, numerous Pt nanotubes with diameter of 5.5 nm, tube-length of several micrometers, and ultrathin wall thickness of 1 nm are assembled. These tubular catalysts with both open ends deliver electrochemical active surface area (ECSA) of 91.43 m 2 g pt -1 which results from multiple Pt atoms exposed on the inner and outer surfaces that doubled Pt atoms can participate in catalytic reactions, further with enhanced electrocatalytic performance for oxygen reduction reaction (ORR). The ultrafine Pt nanotubes represent a class of hollow nanostructure with increased Pt-utilization and large ECSA, which is regarded as a type of cost-effective catalysts for ORR. © 2018 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Miniature near-infrared dual-axes confocal microscope utilizing a two-dimensional microelectromechanical systems scanner

PubMed Central

Liu, Jonathan T. C.; Mandella, Michael J.; Ra, Hyejun; Wong, Larry K.; Solgaard, Olav; Kino, Gordon S.; Piyawattanametha, Wibool; Contag, Christopher H.; Wang, Thomas D.

2007-01-01

The first, to our knowledge, miniature dual-axes confocal microscope has been developed, with an outer diameter of 10 mm, for subsurface imaging of biological tissues with 5–7 μm resolution. Depth-resolved en face images are obtained at 30 frames per second, with a field of view of 800 × 100 μm, by employing a two-dimensional scanning microelectromechanical systems mirror. Reflectance and fluorescence images are obtained with a laser source at 785 nm, demonstrating the ability to perform real-time optical biopsy. PMID:17215937

Infrared laser thermal fusion of blood vessels: preliminary ex vivo tissue studies.

PubMed

Cilip, Christopher M; Rosenbury, Sarah B; Giglio, Nicholas; Hutchens, Thomas C; Schweinsberger, Gino R; Kerr, Duane; Latimer, Cassandra; Nau, William H; Fried, Nathaniel M

2013-05-01

Suture ligation of blood vessels during surgery can be time-consuming and skill-intensive. Energy-based, electrosurgical, and ultrasonic devices have recently replaced the use of sutures and mechanical clips (which leave foreign objects in the body) for many surgical procedures, providing rapid hemostasis during surgery. However, these devices have the potential to create an undesirably large collateral zone of thermal damage and tissue necrosis. We explore an alternative energy-based technology, infrared lasers, for rapid and precise thermal coagulation and fusion of the blood vessel walls. Seven near-infrared lasers (808, 980, 1075, 1470, 1550, 1850 to 1880, and 1908 nm) were tested during preliminary tissue studies. Studies were performed using fresh porcine renal vessels, ex vivo, with native diameters of 1 to 6 mm, and vessel walls flattened to a total thickness of 0.4 mm. A linear beam profile was applied normal to the vessel for narrow, full-width thermal coagulation. The laser irradiation time was 5 s. Vessel burst pressure measurements were used to determine seal strength. The 1470 nm laser wavelength demonstrated the capability of sealing a wide range of blood vessels from 1 to 6 mm diameter with burst strengths of 578 ± 154, 530 ± 171, and 426 ± 174  mmHg for small, medium, and large vessel diameters, respectively. Lateral thermal coagulation zones (including the seal) measured 1.0 ± 0.4  mm on vessels sealed at this wavelength. Other laser wavelengths (1550, 1850 to 1880, and 1908 nm) were also capable of sealing vessels, but were limited by lower vessel seal pressures, excessive charring, and/or limited power output preventing treatment of large vessels (>4  mm outer diameter).

The Opportunistic Pathogen Vibrio vulnificus Produces Outer Membrane Vesicles in a Spatially Distinct Manner Related to Capsular Polysaccharide

PubMed Central

Hampton, Cheri M.; Guerrero-Ferreira, Ricardo C.; Storms, Rachel E.; Taylor, Jeannette V.; Yi, Hong; Gulig, Paul A.; Wright, Elizabeth R.

2017-01-01

Vibrio vulnificus, a bacterial species that inhabits brackish waters, is an opportunistic pathogen of humans. V. vulnificus infections can cause acute gastroenteritis, invasive septicemia, tissue necrosis, and potentially death. Virulence factors associated with V. vulnificus include the capsular polysaccharide (CPS), lipopolysaccharide, flagellum, pili, and outer membrane vesicles (OMVs). The aims of this study were to characterize the morphology of V. vulnificus cells and the formation and arrangement of OMVs using cryo-electron microscopy (cryo-EM). cryo-EM and cryo-electron tomography imaging of V. vulnificus strains grown in liquid cultures revealed the presence of OMVs (diameters of ∼45 nm for wild-type, ∼30 nm for the unencapsulated mutant, and ∼50 nm for the non-motile mutant) in log-phase growth. Production of OMVs in the stationary growth phase was limited and irregular. The spacing of the OMVs around the wild-type cells was in regular, concentric rings. In wild-type cells and a non-motile mutant, the spacing between the cell envelope and the first ring of OMVs was ∼200 nm; this spacing was maintained between subsequent OMV layers. The size, arrangement, and spacing of OMVs in an unencapsulated mutant was irregular and indicated that the polysaccharide chains of the capsule regulate aspects of OMV production and order. Together, our results revealed the distinctive organization of V. vulnificus OMVs that is affected by expression of the CPS. PMID:29163452

Laser-induced retinal damage thresholds for annular retinal beam profiles

NASA Astrophysics Data System (ADS)

Kennedy, Paul K.; Zuclich, Joseph A.; Lund, David J.; Edsall, Peter R.; Till, Stephen; Stuck, Bruce E.; Hollins, Richard C.

2004-07-01

The dependence of retinal damage thresholds on laser spot size, for annular retinal beam profiles, was measured in vivo for 3 μs, 590 nm pulses from a flashlamp-pumped dye laser. Minimum Visible Lesion (MVL)ED50 thresholds in rhesus were measured for annular retinal beam profiles covering 5, 10, and 20 mrad of visual field; which correspond to outer beam diameters of roughly 70, 160, and 300 μm, respectively, on the primate retina. Annular beam profiles at the retinal plane were achieved using a telescopic imaging system, with the focal properties of the eye represented as an equivalent thin lens, and all annular beam profiles had a 37% central obscuration. As a check on experimental data, theoretical MVL-ED50 thresholds for annular beam exposures were calculated using the Thompson-Gerstman granular model of laser-induced thermal damage to the retina. Threshold calculations were performed for the three experimental beam diameters and for an intermediate case with an outer beam diameter of 230 μm. Results indicate that the threshold vs. spot size trends, for annular beams, are similar to the trends for top hat beams determined in a previous study; i.e., the threshold dose varies with the retinal image area for larger image sizes. The model correctly predicts the threshold vs. spot size trends seen in the biological data, for both annular and top hat retinal beam profiles.

Hydrazine-Assisted Formation of Indium Phosphide (InP)-Based Nanowires and Core-Shell Composites

PubMed Central

Patzke, Greta R.; Kontic, Roman; Shiolashvili, Zeinab; Makhatadze, Nino; Jishiashvili, David

2012-01-01

Indium phosphide nanowires (InP NWs) are accessible at 440 °C from a novel vapor phase deposition approach from crystalline InP sources in hydrazine atmospheres containing 3 mol % H2O. Uniform zinc blende (ZB) InP NWs with diameters around 20 nm and lengths up to several tens of micrometers are preferably deposited on Si substrates. InP particle sizes further increase with the deposition temperature. The straightforward protocol was extended on the one-step formation of new core-shell InP–Ga NWs from mixed InP/Ga source materials. Composite nanocables with diameters below 20 nm and shells of amorphous gallium oxide are obtained at low deposition temperatures around 350 °C. Furthermore, InP/Zn sources afford InP NWs with amorphous Zn/P/O-coatings at slightly higher temperatures (400 °C) from analogous setups. At 450 °C, the smooth outer layer of InP-Zn NWs is transformed into bead-shaped coatings. The novel combinations of the key semiconductor InP with isotropic insulator shell materials open up interesting application perspectives in nanoelectronics. PMID:28809296

Hydrazine-Assisted Formation of Indium Phosphide (InP)-Based Nanowires and Core-Shell Composites.

PubMed

Patzke, Greta R; Kontic, Roman; Shiolashvili, Zeinab; Makhatadze, Nino; Jishiashvili, David

2012-12-27

Indium phosphide nanowires (InP NWs) are accessible at 440 °C from a novel vapor phase deposition approach from crystalline InP sources in hydrazine atmospheres containing 3 mol % H₂O. Uniform zinc blende (ZB) InP NWs with diameters around 20 nm and lengths up to several tens of micrometers are preferably deposited on Si substrates. InP particle sizes further increase with the deposition temperature. The straightforward protocol was extended on the one-step formation of new core-shell InP-Ga NWs from mixed InP/Ga source materials. Composite nanocables with diameters below 20 nm and shells of amorphous gallium oxide are obtained at low deposition temperatures around 350 °C. Furthermore, InP/Zn sources afford InP NWs with amorphous Zn/P/O-coatings at slightly higher temperatures (400 °C) from analogous setups. At 450 °C, the smooth outer layer of InP-Zn NWs is transformed into bead-shaped coatings. The novel combinations of the key semiconductor InP with isotropic insulator shell materials open up interesting application perspectives in nanoelectronics.

Analysis of Effluent Gases During the CCVD Growth of Multi Wall Carbon Nanotubes from Acetylene

NASA Technical Reports Server (NTRS)

Schmitt, T. C.; Biris, A. S.; Miller, D. W.; Biris, A. R.; Lupu, D.; Trigwell, S.; Rahman, Z. U.

2005-01-01

Catalytic chemical vapor deposition was used to grow multi-walled carbon nanotubes on a Fe:Co:CaCO3 catalyst from acetylene. The influent and effluent gases were analyzed by gas chromatography and mass spectrometry at different time intervals during the nanotubes growth process in order to better understand and optimize the overall reaction. A large number of byproducts were identified and it was found that the number and the level for some of the carbon byproducts significantly increased over time. The CaCO3 catalytic support thermally decomposed into CaO and CO2 resulting in a mixture of two catalysts for growing the nanotubes, which were found to have outer diameters belonging to two main groups 8 to 35 nm and 40 to 60 nm, respectively.

Absolute measurements of large mirrors

NASA Astrophysics Data System (ADS)

Su, Peng

The ability to produce mirrors for large astronomical telescopes is limited by the accuracy of the systems used to test the surfaces of such mirrors. Typically the mirror surfaces are measured by comparing their actual shapes to a precision master, which may be created using combinations of mirrors, lenses, and holograms. The work presented here develops several optical testing techniques that do not rely on a large or expensive precision, master reference surface. In a sense these techniques provide absolute optical testing. The Giant Magellan Telescope (GMT) has been designed with a 350 m 2 collecting area provided by a 25 m diameter primary mirror made out from seven circular independent mirror segments. These segments create an equivalent f/0.7 paraboloidal primary mirror consisting of a central segment and six outer segments. Each of the outer segments is 8.4 m in diameter and has an off-axis aspheric shape departing 14.5 mm from the best-fitting sphere. Much of the work in this dissertation is motivated by the need to measure the surfaces or such large mirrors accurately, without relying on a large or expensive precision reference surface. One method for absolute testing describing in this dissertation uses multiple measurements relative to a reference surface that is located in different positions with respect to the test surface of interest. The test measurements are performed with an algorithm that is based on the maximum likelihood (ML) method. Some methodologies for measuring large flat surfaces in the 2 m diameter range and for measuring the GMT primary mirror segments were specifically developed. For example, the optical figure of a 1.6-m flat mirror was determined to 2 nm rms accuracy using multiple 1-meter sub-aperture measurements. The optical figure of the reference surface used in the 1-meter sub-aperture measurements was also determined to the 2 nm level. The optical test methodology for a 1.7-m off axis parabola was evaluated by moving several times the mirror under test in relation to the test system. The result was a separation of errors in the optical test system to those errors from the mirror under test. This method proved to be accurate to 12nm rms. Another absolute measurement technique discussed in this dissertation utilizes the property of a paraboloidal surface of reflecting rays parallel to its optical axis, to its focal point. We have developed a scanning pentaprism technique that exploits this geometry to measure off-axis paraboloidal mirrors such as the GMT segments. This technique was demonstrated on a 1.7 m diameter prototype and proved to have a precision of about 50 nm rms.

Rapid sealing of porcine renal blood vessels, ex vivo, using a high power, 1470-nm laser, and laparoscopic prototype

NASA Astrophysics Data System (ADS)

Hardy, Luke A.; Hutchens, Thomas C.; Larson, Eric R.; Gonzalez, David A.; Chang, Chun-Hung; Nau, William H.; Fried, Nathaniel M.

2017-05-01

Energy-based, radiofrequency (RF) and ultrasonic (US) devices currently provide rapid sealing of blood vessels during laparoscopic procedures. We are exploring infrared lasers as an alternate energy modality for vessel sealing, capable of generating less collateral thermal damage. Previous studies demonstrated feasibility of sealing vessels in an in vivo porcine model using a 1470-nm laser. However, the initial prototype was designed for testing in open surgery and featured tissue clasping and light delivery mechanisms incompatible with laparoscopic surgery. In this study, a laparoscopic prototype similar to devices currently in surgical use was developed, and performance tests were conducted on porcine renal blood vessels, ex vivo. The 5-mm outer-diameter laparoscopic prototype featured a traditional Maryland jaw configuration that enables tissue manipulation and blunt dissection. Laser energy was delivered through a 550-μm-core-diameter optical fiber with side-delivery from the lower jaw and beam dimensions of 18-mm length×1.2-mm width. The 1470-nm diode laser delivered 68 W with 3-s activation time, consistent with vessel seal times associated with RF and US-based devices. A total of 69 fresh porcine renal vessels with mean diameter of 3.3±1.7 mm were tested, ex vivo. Vessels smaller than 5-mm diameter were consistently sealed (48/51) with burst pressures greater than malignant hypertension blood pressure (180 mmHg), averaging 1038±474 mmHg. Vessels larger than 5 mm were not consistently sealed (6/18), yielding burst pressures of only 174±221 mmHg. Seal width, thermal damage zone, and thermal spread averaged 1.7±0.8, 3.4±0.7, and 1.0±0.4 mm, respectively. Results demonstrated that the 5-mm optical laparoscopic prototype consistently sealed vessels less than 5-mm diameter with low thermal spread. Further in vivo studies are planned to test the performance across a variety of vessels and tissues.

Morphing hull implementation for unmanned underwater vehicles

NASA Astrophysics Data System (ADS)

Miller, Timothy F.; Gandhi, Farhan; Rufino, Russell J.

2013-11-01

There has been much interest and work in the area of morphing aircraft since the 1980s. Morphing could also potentially benefit unmanned underwater vehicles (UUVs). The current paper envisions a UUV with an interior pressure hull and a variable diameter outer flexible hull with fuel stored in the annulus between, and presents a mechanism to realize diameter change of the outer hull. The outer hull diameter of UUVs designed for very long endurance/range could be progressively reduced as fuel was consumed, thereby reducing drag and further increasing endurance and range capability. Diameter morphing could also be advantageous for compact storage of UUVs. A prototype is fabricated to represent an axial section of such a morphing diameter UUV. Diameter change is achieved using eight morphing trusses arranged equidistant around the circumference of the representative interior rigid hull. Each morphing truss has a lower rail (attached to the rigid hull) and an upper rail with V-linkages between, at either ends of the rail. Horizontal motion of the feet of the V-linkages (sliding in the lower rail) results in vertical motion of the upper rail which in turn produces diameter change of the outer hull. For the prototype built and tested, a 63% increase in outer diameter from 12.75″ to 20.75″ was achieved. The introduction of a stretched latex representative flexible skin around the outer rails increased actuation force requirement and led to a propensity for the wheel-in-track sliders in the morphing truss to bind. It is anticipated that this could be overcome with higher precision manufacturing. In addition to symmetric actuation of the morphing trusses resulting in diameter change, the paper also shows that with asymmetric actuation the hull cross-section shape can be changed (for example, from a circular section for underwater operation to a V-section for surface operations).

Targeting mitochondria in cancer cells using gold nanoparticle-enhanced radiotherapy: A Monte Carlo study

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kirkby, Charles, E-mail: charles.kirkby@albertahealthservices.ca; Ghasroddashti, Esmaeel; Department of Physics and Astronomy, University of Calgary, Calgary, Alberta T2N 1N4

2015-02-15

Purpose: Radiation damage to mitochondria has been shown to alter cellular processes and even lead to apoptosis. Gold nanoparticles (AuNPs) may be used to enhance these effects in scenarios where they collect on the outer membranes of mitochondria. A Monte Carlo (MC) approach is used to estimate mitochondrial dose enhancement under a variety of conditions. Methods: The PENELOPE MC code was used to generate dose distributions resulting from photons striking a 13 nm diameter AuNP with various thicknesses of water-equivalent coatings. Similar dose distributions were generated with the AuNP replaced by water so as to estimate the gain in dosemore » on a microscopic scale due to the presence of AuNPs within an irradiated volume. Models of mitochondria with AuNPs affixed to their outer membrane were then generated—considering variation in mitochondrial size and shape, number of affixed AuNPs, and AuNP coating thickness—and exposed (in a dose calculation sense) to source spectra ranging from 6 MV to 90 kVp. Subsequently dose enhancement ratios (DERs), or the dose with the AuNPs present to that for no AuNPs, for the entire mitochondrion and its components were tallied under these scenarios. Results: For a representative case of a 1000 nm diameter mitochondrion affixed with 565 AuNPs, each with a 13 nm thick coating, the mean DER over the whole organelle ranged from roughly 1.1 to 1.6 for the kilovoltage sources, but was generally less than 1.01 for the megavoltage sources. The outer membrane DERs remained less than 1.01 for the megavoltage sources, but rose to 2.3 for 90 kVp. The voxel maximum DER values were as high as 8.2 for the 90 kVp source and increased further when the particles clustered together. The DER exhibited dependence on the mitochondrion dimensions, number of AuNPs, and the AuNP coating thickness. Conclusions: Substantial dose enhancement directly to the mitochondria can be achieved under the conditions modeled. If the mitochondrion dose can be directly enhanced, as these simulations show, this work suggests the potential for both a tool to study the role of mitochondria in cellular response to radiation and a novel avenue for radiation therapy in that the mitochondria may be targeted, rather than the nuclear DNA.« less

Distinct constrictive processes, separated in time and space, divide caulobacter inner and outer membranes.

PubMed

Judd, Ellen M; Comolli, Luis R; Chen, Joseph C; Downing, Kenneth H; Moerner, W E; McAdams, Harley H

2005-10-01

Cryoelectron microscope tomography (cryoEM) and a fluorescence loss in photobleaching (FLIP) assay were used to characterize progression of the terminal stages of Caulobacter crescentus cell division. Tomographic cryoEM images of the cell division site show separate constrictive processes closing first the inner membrane (IM) and then the outer membrane (OM) in a manner distinctly different from that of septum-forming bacteria. FLIP experiments had previously shown cytoplasmic compartmentalization (when cytoplasmic proteins can no longer diffuse between the two nascent progeny cell compartments) occurring 18 min before daughter cell separation in a 135-min cell cycle so the two constrictive processes are separated in both time and space. In the very latest stages of both IM and OM constriction, short membrane tether structures are observed. The smallest observed pre-fission tethers were 60 nm in diameter for both the inner and outer membranes. Here, we also used FLIP experiments to show that both membrane-bound and periplasmic fluorescent proteins diffuse freely through the FtsZ ring during most of the constriction procession.

Joint small-angle X-ray and neutron scattering data analysis of asymmetric lipid vesicles

DOE Office of Scientific and Technical Information (OSTI.GOV)

Eicher, Barbara; Heberle, Frederick A.; Marquardt, Drew T.

2017-02-28

Low- and high-resolution models describing the internal transbilayer structure of asymmetric lipid vesicles have been developed. These models can be used for the joint analysis of small-angle neutron and X-ray scattering data. The models describe the underlying scattering length density/electron density profiles either in terms of slabs or through the so-called scattering density profile, previously applied to symmetric lipid vesicles. Both models yield structural details of asymmetric membranes, such as the individual area per lipid, and the hydrocarbon thickness of the inner and outer bilayer leaflets. The scattering density profile model, however, comes at a cost of increased computational effortmore » but results in greater structural resolution, showing a slightly lower packing of lipids in the outer bilayer leaflet of ~120 nm diameter palmitoyloleoyl phosphatidylcholine (POPC) vesicles, compared to the inner leaflet. Here, analysis of asymmetric dipalmitoyl phosphatidylcholine/POPC vesicles did not reveal evidence of transbilayer coupling between the inner and outer leaflets at 323 K, i.e.above the melting transition temperature of the two lipids.« less

Electric current distribution of a multiwall carbon nanotube

DOE Office of Scientific and Technical Information (OSTI.GOV)

Chen, Li-Ying; Chang, Chia-Seng, E-mail: jasonc@phys.sinica.edu.tw; Institute of Physics, Academia Sinica, Taipei 11529, Taiwan

2016-07-15

The electric current distribution in a multiwall carbon nanotube (MWCNT) was studied by in situ measuring the electric potential along an individual MWCNT in the ultra-high vacuum transmission electron microscope (TEM). The current induced voltage drop along each section of a side-bonded MWCNT was measured by a potentiometric probe in TEM. We have quantitatively derived that the current on the outermost shell depends on the applied current and the shell diameter. More proportion of the total electronic carriers hop into the inner shells when the applied current is increased. The larger a MWCNT’s diameter is, the easier the electronic carriersmore » can hop into the inner shells. We observed that, for an 8 nm MWCNT with 10 μA current applied, 99% of the total current was distributed on the outer two shells.« less

Physical characterization of neurocatheter performance in a brain phantom gelatin with nanoscale porosity: steady-state and oscillatory flows

NASA Astrophysics Data System (ADS)

Bauman, M. A.; Gillies, G. T.; Raghavan, R.; Brady, M. L.; Pedain, C.

2004-01-01

An agarose gelatin having nanoscale transport properties similar to those of in vivo mammalian brain was employed as a surrogate for living brain tissue in the evaluation of infusion therapy protocols and neurocatheters to be used in the treatment of brain tumours. The catheters under study were a polyimide tube of 950 µm outer diameter (OD) and 750 µm inner diameter (ID), and a silicone tube of 2.5 mm OD and 1.25 mm ID. From the pressure profiles that were measured during infusions of a solution of Bromphenol Blue dye into this gel, we infer that forces on the order of 0.1 fN were driving the solute molecules through the {\\approx } 200 nm intramatrix voids in the gel at rates of {\\approx } 10\

Premixed direct injection nozzle for highly reactive fuels

DOEpatents

Ziminsky, Willy Steve; Johnson, Thomas Edward; Lacy, Benjamin Paul; York, William David; Uhm, Jong Ho; Zuo, Baifang

2013-09-24

A fuel/air mixing tube for use in a fuel/air mixing tube bundle is provided. The fuel/air mixing tube includes an outer tube wall extending axially along a tube axis between an inlet end and an exit end, the outer tube wall having a thickness extending between an inner tube surface having a inner diameter and an outer tube surface having an outer tube diameter. The tube further includes at least one fuel injection hole having a fuel injection hole diameter extending through the outer tube wall, the fuel injection hole having an injection angle relative to the tube axis. The invention provides good fuel air mixing with low combustion generated NOx and low flow pressure loss translating to a high gas turbine efficiency, that is durable, and resistant to flame holding and flash back.

Facile Synthesis of Uniform Virus-like Mesoporous Silica Nanoparticles for Enhanced Cellular Internalization

PubMed Central

2017-01-01

The low-efficiency cellular uptake property of current nanoparticles greatly restricts their application in the biomedical field. Herein, we demonstrate that novel virus-like mesoporous silica nanoparticles can easily be synthesized, showing greatly superior cellular uptake property. The unique virus-like mesoporous silica nanoparticles with a spiky tubular rough surface have been successfully synthesized via a novel single-micelle epitaxial growth approach in a low-concentration-surfactant oil/water biphase system. The virus-like nanoparticles’ rough surface morphology results mainly from the mesoporous silica nanotubes spontaneously grown via an epitaxial growth process. The obtained nanoparticles show uniform particle size and excellent monodispersity. The structural parameters of the nanoparticles can be well tuned with controllable core diameter (∼60–160 nm), tubular length (∼6–70 nm), and outer diameter (∼6–10 nm). Thanks to the biomimetic morphology, the virus-like nanoparticles show greatly superior cellular uptake property (invading living cells in large quantities within few minutes, <5 min), unique internalization pathways, and extended blood circulation duration (t1/2 = 2.16 h), which is much longer than that of conventional mesoporous silica nanoparticles (0.45 h). Furthermore, our epitaxial growth strategy can be applied to fabricate various virus-like mesoporous core–shell structures, paving the way toward designed synthesis of virus-like nanocomposites for biomedicine applications. PMID:28852697

Biological effects of carbon nanotubes generated in forest wildfire ecosystems rich in resinous trees on native plants

PubMed Central

Dasgupta-Schubert, Nabanita; Borjas-García, Salomón; Tiwari, DK; Paraguay-Delgado, Francisco; Jiménez-Sandoval, Sergio; Alonso-Nuñez, Gabriel; Gómez-Romero, Mariela; Lindig-Cisneros, Roberto; Reyes De la Cruz, Homero

2017-01-01

Carbon nanotubes (CNTs) have a broad range of applications and are generally considered human-engineered nanomaterials. However, carbon nanostructures have been found in ice cores and oil wells, suggesting that nature may provide appropriate conditions for CNT synthesis. During forest wildfires, materials such as turpentine and conifer tissues containing iron under high temperatures may create chemical conditions favorable for CNT generation, similar to those in synthetic methods. Here, we show evidence of naturally occurring multiwalled carbon nanotubes (MWCNTs) produced from Pinus oocarpa and Pinus pseudostrobus, following a forest wildfire. The MWCNTs showed an average of 10 walls, with internal diameters of ∼2.5 nm and outer diameters of ∼14.5 nm. To verify whether MWCNT generation during forest wildfires has a biological effect on some characteristic plant species of these ecosystems, germination and development of seedlings were conducted. Results show that the utilization of comparable synthetic MWCNTs increased seed germination rates and the development of Lupinus elegans and Eysenhardtia polystachya, two plants species found in the burned forest ecosystem. The finding provides evidence that supports the generation and possible ecological functions of MWCNTs in nature. PMID:28828256

Biological effects of carbon nanotubes generated in forest wildfire ecosystems rich in resinous trees on native plants.

PubMed

Lara-Romero, Javier; Campos-García, Jesús; Dasgupta-Schubert, Nabanita; Borjas-García, Salomón; Tiwari, D K; Paraguay-Delgado, Francisco; Jiménez-Sandoval, Sergio; Alonso-Nuñez, Gabriel; Gómez-Romero, Mariela; Lindig-Cisneros, Roberto; Reyes De la Cruz, Homero; Villegas, Javier A

2017-01-01

Carbon nanotubes (CNTs) have a broad range of applications and are generally considered human-engineered nanomaterials. However, carbon nanostructures have been found in ice cores and oil wells, suggesting that nature may provide appropriate conditions for CNT synthesis. During forest wildfires, materials such as turpentine and conifer tissues containing iron under high temperatures may create chemical conditions favorable for CNT generation, similar to those in synthetic methods. Here, we show evidence of naturally occurring multiwalled carbon nanotubes (MWCNTs) produced from Pinus oocarpa and Pinus pseudostrobus, following a forest wildfire. The MWCNTs showed an average of 10 walls, with internal diameters of ∼2.5 nm and outer diameters of ∼14.5 nm. To verify whether MWCNT generation during forest wildfires has a biological effect on some characteristic plant species of these ecosystems, germination and development of seedlings were conducted. Results show that the utilization of comparable synthetic MWCNTs increased seed germination rates and the development of Lupinus elegans and Eysenhardtia polystachya , two plants species found in the burned forest ecosystem. The finding provides evidence that supports the generation and possible ecological functions of MWCNTs in nature.

Nanoparticle-stabilized liposomes for pH-responsive gastric drug delivery.

PubMed

Thamphiwatana, Soracha; Fu, Victoria; Zhu, Jingying; Lu, Diannan; Gao, Weiwei; Zhang, Liangfang

2013-10-01

We report a novel pH-responsive gold nanoparticle-stabilized liposome system for gastric antimicrobial delivery. By adsorbing small chitosan-modified gold nanoparticles (diameter ~10 nm) onto the outer surface of negatively charged phospholipid liposomes (diameter ~75 nm), we show that at gastric pH the liposomes have excellent stability with limited fusion ability and negligible cargo releases. However, when the stabilized liposomes are present in an environment with neutral pH, the gold stabilizers detach from the liposomes, resulting in free liposomes that can actively fuse with bacterial membranes. Using Helicobacter pylori as a model bacterium and doxycycline as a model antibiotic, we demonstrate such pH-responsive fusion activity and drug release profile of the nanoparticle-stabilized liposomes. Particularly, at neutral pH the gold nanoparticles detach, and thus the doxycycline-loaded liposomes rapidly fuse with bacteria and cause superior bactericidal efficacy as compared to the free doxycycline counterpart. Our results suggest that the reported liposome system holds a substantial potential for gastric drug delivery; it remains inactive (stable) in the stomach lumen but actively interacts with bacteria once it reaches the mucus layer of the stomach where the bacteria may reside.

SIMS depth profiling of working environment nanoparticles

NASA Astrophysics Data System (ADS)

Konarski, P.; Iwanejko, I.; Mierzejewska, A.

2003-01-01

Morphology of working environment nanoparticles was analyzed using sample rotation technique in secondary ion mass spectrometry (SIMS). The particles were collected with nine-stage vacuum impactor during gas tungsten arc welding (GTAW) process of stainless steel and shielded metal arc welding (SMAW) of mild steel. Ion erosion of 300-400 nm diameter nanoparticles attached to indium substrate was performed with 2 keV, 100 μm diameter, Ar + ion beam at 45° ion incidence and 1 rpm sample rotation. The results show that both types of particles have core-shell morphology. A layer of fluorine, chlorine and carbon containing compounds covers stainless steel welding fume particles. The cores of these particles are enriched in iron, manganese and chromium. Outer shell of mild steel welding fume particles is enriched in carbon, potassium, chlorine and fluorine, while the deeper layers of these nanoparticles are richer in main steel components.

Transparent Nanotubular TiO₂ Photoanodes Grown Directly on FTO Substrates.

PubMed

Paušová, Šárka; Kment, Štěpán; Zlámal, Martin; Baudys, Michal; Hubička, Zdeněk; Krýsa, Josef

2017-05-10

This work describes the preparation of transparent TiO₂ nanotube (TNT) arrays on fluorine-doped tin oxide (FTO) substrates. An optimized electrolyte composition (0.2 mol dm -3 NH₄F and 4 mol dm -3 H₂O in ethylene glycol) was used for the anodization of Ti films with different thicknesses (from 100 to 1300 nm) sputtered on the FTO glass substrates. For Ti thicknesses 600 nm and higher, anodization resulted in the formation of TNT arrays with an outer nanotube diameter around 180 nm and a wall thickness around 45 nm, while for anodized Ti thicknesses of 100 nm, the produced nanotubes were not well defined. The transmittance in the visible region (λ = 500 nm) varied from 90% for the thinnest TNT array to 65% for the thickest TNT array. For the fabrication of transparent TNT arrays by anodization, the optimal Ti thickness on FTO was around 1000 nm. Such fabricated TNT arrays with a length of 2500 nm exhibit stable photocurrent densities in aqueous electrolytes (~300 µA cm -2 at potential 0.5 V vs. Ag/AgCl). The stability of the photocurrent response and a sufficient transparency (≥65%) enables the use of transparent TNT arrays in photoelectrochemical applications when the illumination from the support/semiconductor interface is a necessary condition and the transmitted light can be used for another purpose (photocathode or photochemical reaction in the electrolyte).

Specific Internalisation of Gold Nanoparticles into Engineered Porous Protein Cages via Affinity Binding

PubMed Central

Peng, Tao; Free, Paul; Fernig, David G.; Lim, Sierin; Tomczak, Nikodem

2016-01-01

Porous protein cages are supramolecular protein self-assemblies presenting pores that allow the access of surrounding molecules and ions into their core in order to store and transport them in biological environments. Protein cages’ pores are attractive channels for the internalisation of inorganic nanoparticles and an alternative for the preparation of hybrid bioinspired nanoparticles. However, strategies based on nanoparticle transport through the pores are largely unexplored, due to the difficulty of tailoring nanoparticles that have diameters commensurate with the pores size and simultaneously displaying specific affinity to the cages’ core and low non-specific binding to the cages’ outer surface. We evaluated the specific internalisation of single small gold nanoparticles, 3.9 nm in diameter, into porous protein cages via affinity binding. The E2 protein cage derived from the Geobacillus stearothermophilus presents 12 pores, 6 nm in diameter, and an empty core of 13 nm in diameter. We engineered the E2 protein by site-directed mutagenesis with oligohistidine sequences exposing them into the cage’s core. Dynamic light scattering and electron microscopy analysis show that the structures of E2 protein cages mutated with bis- or penta-histidine sequences are well conserved. The surface of the gold nanoparticles was passivated with a self-assembled monolayer made of a mixture of short peptidols and thiolated alkane ethylene glycol ligands. Such monolayers are found to provide thin coatings preventing non-specific binding to proteins. Further functionalisation of the peptide coated gold nanoparticles with Ni2+ nitrilotriacetic moieties enabled the specific binding to oligohistidine tagged cages. The internalisation via affinity binding was evaluated by electron microscopy analysis. From the various mutations tested, only the penta-histidine mutated E2 protein cage showed repeatable and stable internalisation. The present work overcomes the limitations of currently available approaches and provides a new route to design tailored and well-controlled hybrid nanoparticles. PMID:27622533

Implementation of focal zooming on the Nike KrF laser

NASA Astrophysics Data System (ADS)

Kehne, D. M.; Karasik, M.; Aglitsky, Y.; Smyth, Z.; Terrell, S.; Weaver, J. L.; Chan, Y.; Lehmberg, R. H.; Obenschain, S. P.

2013-01-01

In direct drive inertial confinement laser fusion, a pellet containing D-T fuel is imploded by ablation arising from absorption of laser energy at its outer surface. For optimal coupling, the focal spot of the laser would continuously decrease to match the reduction in the pellet's diameter, thereby minimizing wasted energy. A krypton-fluoride laser (λ = 248 nm) that incorporates beam smoothing by induced spatial incoherence has the ability to produce a high quality focal profile whose diameter varies with time, a property known as focal zooming. A two-stage focal zoom has been demonstrated on the Nike laser at the Naval Research Laboratory. In the experiment, a 4.4 ns laser pulse was created in which the on-target focal spot diameter was 1.3 mm (full width at half maximum) for the first 2.4 ns and 0.28 mm for the final 2 ns. These two diameters appear in time-integrated focal plane equivalent images taken at several locations in the amplification chain. Eight of the zoomed output beams were overlapped on a 60 μm thick planar polystyrene target. Time resolved images of self-emission from the rear of the target show the separate shocks launched by the two corresponding laser focal diameters.

Implementation of focal zooming on the Nike KrF laser.

PubMed

Kehne, D M; Karasik, M; Aglitsky, Y; Smyth, Z; Terrell, S; Weaver, J L; Chan, Y; Lehmberg, R H; Obenschain, S P

2013-01-01

In direct drive inertial confinement laser fusion, a pellet containing D-T fuel is imploded by ablation arising from absorption of laser energy at its outer surface. For optimal coupling, the focal spot of the laser would continuously decrease to match the reduction in the pellet's diameter, thereby minimizing wasted energy. A krypton-fluoride laser (λ = 248 nm) that incorporates beam smoothing by induced spatial incoherence has the ability to produce a high quality focal profile whose diameter varies with time, a property known as focal zooming. A two-stage focal zoom has been demonstrated on the Nike laser at the Naval Research Laboratory. In the experiment, a 4.4 ns laser pulse was created in which the on-target focal spot diameter was 1.3 mm (full width at half maximum) for the first 2.4 ns and 0.28 mm for the final 2 ns. These two diameters appear in time-integrated focal plane equivalent images taken at several locations in the amplification chain. Eight of the zoomed output beams were overlapped on a 60 μm thick planar polystyrene target. Time resolved images of self-emission from the rear of the target show the separate shocks launched by the two corresponding laser focal diameters.

Super-achromatic microprobe for ultrahigh-resolution endoscopic OCT imaging at 800 nm (Conference Presentation)

NASA Astrophysics Data System (ADS)

Yuan, Wu; Alemohammad, Milad; Yu, Xiaoyun; Yu, Shaoyong; Li, Xingde

2016-03-01

In this paper, we report a super-achromatic microprobe made with fiber-optic ball lens to enable ultrahigh-resolution endoscopic OCT imaging. An axial resolution of ~2.4 µm (in air) can be achieved with a 7-fs Ti:Sapphire laser. The microprobe has minimal astigmatism which affords a high transverse resolution of ~5.6 µm. The miniaturized microprobe has an outer diameter of ~520 µm including the encasing metal guard and can be used to image small luminal organs. The performance of the ultrahigh-resolution OCT microprobe was demonstrated by imaging rat esophagus, guinea pig esophagus, and mouse rectum in vivo.

Synthesis of NiO nanotubes for use as negative electrodes in lithium ion batteries

NASA Astrophysics Data System (ADS)

Needham, S. A.; Wang, G. X.; Liu, H. K.

Nickel oxide (NiO) nanotubes have been produced for the first time via a template processing method. The synthesis involved a two step chemical reaction in which nickel hydroxide (Ni(OH) 2) nanotubes were firstly formed within the walls of an anodic aluminium oxide (AAO) template. The template was then dissolved away using concentrated NaOH, and the freed nanotubes were converted to NiO by heat treatment in air at 350 °C. Individual nanotubes measured 60 μm in length with a 200 nm outer diameter and a wall thickness of 20-30 nm. The NiO nanotube powder was used in Li-ion cells for assessment of the lithium storage ability. Preliminary testing indicates that the cells demonstrate controlled and sustainable lithium diffusion after the formation of an SEI. Reversible capacities in the 300 mAh g -1 range were typical.

Preparation of α-Fe2O3 nanotubes via electrospinning and research on their catalytic properties

NASA Astrophysics Data System (ADS)

Shao, Hao; Zhang, Xuebin; Chen, Fanyan; Liu, Shasha; Ji, Yi; Zhu, Yajun; Feng, Yi

2012-09-01

In this paper, smooth α-Fe2O3 nanotubes have been successfully synthesized by electrospinning of ferric nitrate-polyvinyl alcohol solution followed by calcination in air. The morphologies and structures of the samples were characterized by transmission electron microscopy, scanning electron microscopy and X-ray diffraction. The catalytic properties were studied by differential thermal analysis and thermogravimetric analysis. The results indicated that the as-prepared α-Fe2O3 nanotubes showed a continuous morphology and an extremely high degree of crystallization. The average inner and outer diameters of the obtained α-Fe2O3 nanotubes were about 60 nm and 100 nm, respectively. The obtained α-Fe2O3 nanotubes were able to lower the temperature of the high-temperature thermal decomposition of ammonium perchlorate, while they had little effect on the crystallographic phase transformation and the low-temperature thermal decomposition.

Fabrication of Nanopipette Arrays for Biosensing

NASA Technical Reports Server (NTRS)

Meyyappan, Meyya (Inventor)

2015-01-01

Method for providing a nanopipette array for biosensing applications. A thin substrate of anodizable metal ("AN-metal," such as Al, Mg, Zn, Ti, Ta and/or Nb) is anodized at temperature T=20-200.degree. C., chemical bath pH=4-6 and electrical potential 1-300 Volts, to produce an array of anodized nanopipette channels, having diameters 10-50 nm, with oxidized channel surfaces of thickness 5-20 nm. A portion of exposed non-oxidized AN-metal between adjacent nanopipette channels, of length 1-5 .mu.m, is etched away, exposing inner and outer surfaces of a nanopipette channel. A probe molecule, is deposited on one or both surfaces to provide biosensing capability for K(.gtoreq.1) target molecules. Target molecule presence, in an above-threshold concentration, in a fluid passed through or adjacent to a nanopipette channel, produces characteristic detection signals associated with the probe molecule site.

The fabrication and electrochemical properties of electrospun nanofibers of a multiwalled carbon nanotube grafted by chitosan

NASA Astrophysics Data System (ADS)

Feng, Wei; Wu, Zigang; Li, Yu; Feng, Yiyu; Yuan, Xiaoyan

2008-03-01

Multiwalled carbon nanotubes (MWCNTs) were grafted by chitosan (CS); the product could disperse well in poly(vinyl alcohol) (PVA) aqueous solution with 2% (v/v) acetic acid solution. Because this product has potential in several biological fields, it was electrospun so as to enlarge the surface area. Raman spectra indicated that the electrospinning process did not severely alter the electron hybridization of carbon atoms within the nanotube framework. Moreover and interestingly, these nanofibers showed a novel sheath-core structure; the outer and inner diameters of these sheath-core nanofibers were about 200 nm and 100 nm, respectively. These nanofibers' electrochemical properties were characterized by detection of hydrogen peroxide and voltammetric responses of potassium ferricyanide. The electrospun fibers' web displayed faster electron transfer kinetics and better electrochemical properties than its cast film, which justified further applications in biological areas.

Fabrication and room temperature operation of semiconductor nano-ring lasers using a general applicable membrane transfer method

NASA Astrophysics Data System (ADS)

Fan, Fan; Yu, Yueyang; Amiri, Seyed Ebrahim Hashemi; Quandt, David; Bimberg, Dieter; Ning, C. Z.

2017-04-01

Semiconductor nanolasers are potentially important for many applications. Their design and fabrication are still in the early stage of research and face many challenges. In this paper, we demonstrate a generally applicable membrane transfer method to release and transfer a strain-balanced InGaAs quantum-well nanomembrane of 260 nm in thickness onto various substrates with a high yield. As an initial device demonstration, nano-ring lasers of 1.5 μm in outer diameter and 500 nm in radial thickness are fabricated on MgF2 substrates. Room temperature single mode operation is achieved under optical pumping with a cavity volume of only 0.43λ03 (λ0 in vacuum). Our nano-membrane based approach represents an advantageous alternative to other design and fabrication approaches and could lead to integration of nanolasers on silicon substrates or with metallic cavity.

Appendiceal outer diameter as an indicator for differentiating appendiceal mucocele from appendicitis.

PubMed

Lien, Wan-Ching; Huang, Shih-Pei; Chi, Chun-Lin; Liu, Kao-Lang; Lin, Ming-Tsan; Lai, Ting-I; Liu, Yueh-Ping; Wang, Hsiu-Po

2006-11-01

Patients with appendiceal mucocele (AM) commonly present with features indicative of acute appendicitis. In emergency departments, accurate preoperative diagnosis is crucial to prompt appropriate treatment. This study investigates the clinical and sonographic characteristics of AM, which may prove useful in preoperatively differentiating AM from appendicitis. This case-control study compares the clinical and sonographic findings of 16 histologically confirmed AM with sex- and age-matched control subjects (n = 64) with appendicitis by a 1:4 ratio. Conditional logistic regression was applied to estimate the odds ratio (OR) and 95% confidence intervals (CI) of clinical and sonographic parameters associated with AM. Univariate analysis demonstrated that the larger appendiceal outer diameter by sonography was positively correlated with diagnosis of AM (OR, 2.31; 95% CI, 1.42-3.72) and right lower quadrant abdominal pain was negatively correlated (OR, 0.38; 95% CI, 0.17-0.82). However, multiple regression analysis suggested that only outer diameter remained significant (OR, 2.21; 95% CI, 1.36-3.59) after adjusting for age, sex, and right lower quadrant pain. An outer diameter of 15 mm or more was predictive of AM diagnosis, with a sensitivity of 83% and specificity of 92%. When the threshold is set at 15 mm, appendiceal outer diameter by sonography is a useful preoperative measurement for differentiating between AM and acute appendicitis.

Micropipette as Coulter counter for submicron particles

NASA Astrophysics Data System (ADS)

Rudzevich, Yauheni; Ordonez, Tony; Evans, Grant; Chow, Lee

2011-03-01

Coulter counter based on micropipette has been around for several decades. Typical commercial Coulter counter has a pore size of 20 μ m, and is designed to detect micron-size blood cells. In recent years, there are a lot of interests in using nanometer pore size Coulter counter to detect single molecule and to sequence DNA. Here we describe a simple nanoparticle counter based on pulled micropipettes with a diameter of 50 -- 500 nm. Borosilicate micropipettes with an initial outer diameter of 1.00 mm and inner diameter of 0.5 mm are used. After pulling, the micropipettes are fire polished and ultrasound cleaned. Chlorinated Ag/AgCl electrodes and 0.1 M of KCl solution are used. The ionic currents are measured using an Axopatch 200B amplifier in the voltage-clamp mode. Several types and sizes of nanoparticles are measured, including plain silica and polystyrene nanospheres. The results will be discussed in terms of pH values of the solution and concentrations of the nanoparticles. Financial support from National Science Foundation (NSF-0901361) is acknowledged.

Amorphous and crystalline TiO2 nanotube arrays for enhanced Li-ion intercalation properties.

PubMed

Guan, Dongsheng; Cai, Chuan; Wang, Ying

2011-04-01

We have employed a simple process of anodizing Ti foils to prepare TiO2 nanotube arrays which show enhanced electrochemical properties for applications as Li-ion battery electrode materials. The lengths and pore diameters of TiO2 nanotubes can be finely tuned by varying voltage, electrolyte composition, or anodization time. The as-prepared nanotubes are amorphous and can be converted into anatase nanotubes with heat treatment at 480 degrees C. Rutile crystallites emerge in the anatase nanotube when the annealing temperature is increased to 580 degrees C, resulting in TiO2 nanotubes of mixed phases. The morphological features of nanotubes remain unchanged after annealing. Li-ion insertion performance has been studied for amorphous and crystalline TiO2 nanotube arrays. Amorphous nanotubes with a length of 3.0 microm and an outer diameter of 125 nm deliver a capacity of 91.2 microA h cm(-2) at a current density of 400 microA cm(-2), while those with a length of 25 microm and an outer diameter of 158 nm display a capacity of 533 microA h cm-2. When the 3-microm long nanotubes become crystalline, they deliver lower capacities: the anatase nanotubes and nanotubes of mixed phases show capacities of 53.8 microA h cm-2 and 63.1 microA h cm(-2), respectively at the same current density. The amorphous nanotubes show excellent capacity retention ability over 50 cycles. The cycled nanotubes show little change in morphology compared to the nanotubes before electrochemical cycling. All the TiO2 nanotubes demonstrate higher capacities than amorphous TiO2 compact layer reported in literature. The amorphous TiO2 nanotubes with a length of 1.9 microm exhibit a capacity five times higher than that of TiO2 compact layer even when the nanotube array is cycled at a current density 80 times higher than that for the compact layer. These results suggest that anodic TiO2 nanotube arrays are promising electrode materials for rechargeable Li-ion batteries.

Ethanol Gas Detection Using a Yolk-Shell (Core-Shell) α-Fe2O3 Nanospheres as Sensing Material.

PubMed

Wang, LiLi; Lou, Zheng; Deng, Jianan; Zhang, Rui; Zhang, Tong

2015-06-17

Three-dimensional (3D) nanostructures of α-Fe2O3 materials, including both hollow sphere-shaped and yolk-shell (core-shell)-shaped, have been successfully synthesized via an environmentally friendly hydrothermal approach. By expertly adjusting the reaction time, the solid, hollow, and yolk-shell shaped α-Fe2O3 can be selectively synthesized. Yolk-shell α-Fe2O3 nanospheres display outer diameters of 350 nm, and the interstitial hollow spaces layer is intimately sandwiched between the inner and outer shell of α-Fe2O3 nanostructures. The possible growth mechanism of the yolk-shell nanostructure is proposed. The results showed that the well-defined bilayer interface effectively enhanced the sensing performance of the α-Fe2O3 nanostructures (i.e., yolk-shell α-Fe2O3@α-Fe2O3), owing predominantly to the unique nanostructure, thus facilitated the transport rate and augmented the adsorption quantity of the target gas molecule under gas detection.

Assembly of flammutoxin, a cytolytic protein from the edible mushroom Flammulina velutipes, into a pore-forming ring-shaped oligomer on the target cell.

PubMed

Tomita, T; Ishikawa, D; Noguchi, T; Katayama, E; Hashimoto, Y

1998-07-01

Flammutoxin has been previously isolated as a cardiotoxic and cytolytic polypeptide of 22 or 32 kDa from the fruiting bodies of the edible mushroom Flammulina velutipes. In the present study, we purified flammutoxin as a single haemolytic protein of 31 kDa and studied the mode of its cytolytic action. (1) Flammutoxin caused efflux of potassium ions from human erythrocytes and swelling of the cells before haemolysis. (2) Flammutoxin did not lyse human erythrocytes in the presence of non-electrolytes with hydrodynamic diameters of >5.0 nm, although it caused leakage of potassium ions and swelling of the cells under the same conditions. (3) Experiments including solubilization of cell-bound toxin with 2% (w/v) SDS at 20 degrees C and subsequent Western immunoblots showed that flammutoxin formed a band corresponding to 180 kDa under the conditions where it lysed erythrocytes. (4) Electron microscopy of flammutoxin-treated human erythrocytes revealed the presence of a ring-shaped structure with outer and inner diameters of 10 and 5 nm, respectively, on the cells. (5) A ring-shaped toxin oligomer of the same dimensions was solubilized from the toxin-treated human erythrocytes with 2% (w/v) SDS at 20 degrees C and isolated by a sucrose-gradient ultracentrifugation. These data indicated that flammutoxin assembles into a ring-shaped oligomer possessing a hydrophilic pore of 4-5 nm on target cells.

Physicochemical characterization of artificial nanoerythrosomes derived from erythrocyte ghost membranes.

PubMed

Deák, Róbert; Mihály, Judith; Szigyártó, Imola Cs; Wacha, András; Lelkes, Gábor; Bóta, Attila

2015-11-01

Colloidal stabile nanoerythrosomes with 200 nm average diameter were formed from hemoglobin-free erythrocyte ghost membrane via sonication and membrane extrusion. The incorporation of extra lipid (1,2-dipalmitoyl-sn-glycero-3-phosphocholine, DPPC), added to the sonicated ghosts, caused significant changes in the thermotropic character of the original membranes. As a result of the increased DPPC ratio the chain melting of the hydrated DPPC system and the characteristic small angle X-ray scattering (SAXS) of the lipid bilayers appeared. Significant morphological changes were followed by transmission electron microscopy combined with freeze fracture method (FF-TEM). After the ultrasonic treatment the large entities of erythrocyte ghosts transformed into nearly spherical nanoerythrosomes with diameters between 100 and 300 nm and at the same time a great number of 10-30 nm large membrane proteins or protein clusters were dispersed in the aqueous medium. The infrared spectroscopy (FT-IR) pointed out, that the sonication did not cause changes in the secondary structures of the membrane proteins under our preparation conditions. About fivefold of extra lipid--compared to the lipid content of the original membrane--caused homogeneous dispersion of nanoerythrosomes however the shape of the vesicles was not uniform. After the addition of about tenfold of DPPC, monoform and monodisperse nanoerythrosomes became typical. The outer surfaces of these roughly spherical objects were frequently polygonal, consisting of a net of pentagons and hexagons. Copyright © 2015 Elsevier B.V. All rights reserved.

High speed photoacoustic imaging with fast OPO laser at 1.7 μm (Conference Presentation)

NASA Astrophysics Data System (ADS)

Piao, Zhonglie; Teng, Ma; Li, Jiawen; Qu, Yueqiao; Yu, Mingyue; Shung, K. Kirk; Zhou, Qifa; Kim, Chang-Seok; Chen, Zhongping

2016-03-01

Acute cardiovascular events are mostly due to a blood clot or thrombus induced by the sudden rupture of vulnerable atherosclerotic plaques within coronary artery walls. Based on the high optical absorption contrast of the lipid rich plaques within the vessel wall, intravascular photoacoustic (IVPA) imaging at 1.7 μm spectral band has shown promising capabilities for detecting of lipid composition, but the translation of the technology for in vivo application is limited by the slow imaging speed. In this work, we will present a high speed integrated IVPA/US imaging system with a 500 Hz optical parametric oscillator laser at 1725 nm (5 nm linewidth). A miniature catheter with 1.0 mm outer diameter was designed with a polished 200 μm multimode fiber and an ultrasound transducer with 45 MHz center frequency. Two optical illumination methods by gradient-index (GRIN) lens and ball lens are introduced and compared for higher spatial resolution. At 1725 nm, atherosclerotic rabbit abdominal aorta was imaged at two frame per second, which is more than one order of magnitude faster than previous reported IVPA imaging. Furthermore, by wide tuning range of the laser wavelength from 1680 nm to 1770 nm, spectroscopic photoacoustic analysis of lipid-mimicking phantom and an human atherosclerotic artery was performed ex vivo.

Anisotropic metal growth on phospholipid nanodiscs via lipid bilayer expansion

PubMed Central

Oertel, Jana; Keller, Adrian; Prinz, Julia; Schreiber, Benjamin; Hübner, René; Kerbusch, Jochen; Bald, Ilko; Fahmy, Karim

2016-01-01

Self-assembling biomolecules provide attractive templates for the preparation of metallic nanostructures. However, the intuitive transfer of the “outer shape” of the assembled macromolecules to the final metallic particle depends on the intermolecular forces among the biomolecules which compete with interactions between template molecules and the metal during metallization. The shape of the bio-template may thus be more dynamic than generally assumed. Here, we have studied the metallization of phospholipid nanodiscs which are discoidal particles of ~10 nm diameter containing a lipid bilayer ~5 nm thick. Using negatively charged lipids, electrostatic adsorption of amine-coated Au nanoparticles was achieved and followed by electroless gold deposition. Whereas Au nanoparticle adsorption preserves the shape of the bio-template, metallization proceeds via invasion of Au into the hydrophobic core of the nanodisc. Thereby, the lipidic phase induces a lateral growth that increases the diameter but not the original thickness of the template. Infrared spectroscopy reveals lipid expansion and suggests the existence of internal gaps in the metallized nanodiscs, which is confirmed by surface-enhanced Raman scattering from the encapsulated lipids. Interference of metallic growth with non-covalent interactions can thus become itself a shape-determining factor in the metallization of particularly soft and structurally anisotropic biomaterials. PMID:27216789

Phytotoxicity of carbon nanotubes in soybean as determined by interactions with micronutrients

NASA Astrophysics Data System (ADS)

Zaytseva, Olga; Wang, Zhengrui; Neumann, Günter

2017-02-01

Carbon nanomaterials released into the environment exert extremely variable effects on living organisms. In this study, we used soybean ( Glycine max) to investigate early responses to seed exposure to multi-walled carbon nanotubes (MWCNTs, outer diameter 20-70 nm, inner diameter 5-10 nm, length of >2 μm). Soybean seeds were imbibed with deionised water (control) or MWCNT suspension (1000 mg L-1) and were analysed for MWCNT contamination using light microscopy. The seedlings vitality status was evaluated by staining with triphenyltetrazolium chloride and measurement of oxidative stress indicators in the root tissue. Micronutrient (Zn, Mn, Cu) availability in different seedling organs was assessed and the effects of antioxidants, and micronutrient supplementation was investigated. Oxidative stress induction by MWCNTs was detectable in radicle tips, coincided with MWCNTs accumulation and was reverted by external application of proline as antioxidant and micronutrients (Zn, Cu, Mn) as cofactors for various enzymes involved in oxidative stress defence. Accordingly, SOD activity increased after Zn supplementation. During germination, the MWCNT treatments reduced Zn translocation from the cotyledons to the seedling and MWCNTs exhibited adsorption potential for Zn and Cu, which may be involved in internal micronutrients immobilisation. This study demonstrates for the first time that MWCNT phytotoxicity is linked with oxidative stress-related disturbances of micronutrient homeostasis.

Investigation of star polymer nanoshells for use in diagnostic imaging and photothermal cancer therapy applications

NASA Astrophysics Data System (ADS)

Gomez, Lizabeth

Gold nanoshells can be designed to possess high light scattering and strong absorption of near-infrared light. Thus, they have the potential to be used in biological applications as contrast agents for diagnostic imaging as well as for thermal ablation of tumor cells in future cancer treatments. In this study, gold nanoshells with dye-loaded star polymer cores were investigated. Uniform near-infrared gold nanoshells with 100 nm diameters were successfully generated using different batches of star polymer templates and were characterized by UV-visible spectroscopy and scanning electron microscopy. The star polymers used were block copolymer structures with a hydrophobic polystyrene (PS) core and a hydrophilic poly(N,N-dimethylaminoethylmethracrylate) (DMAEMA) outer shell. Within this work, a general procedure was established in order to achieve a desired gold nanoshell size regardless of the star polymer batch used, since the synthesis process conditions can cause star polymers to vary in size as well in the number and length of amino-functionalized arms. Control of the gold nanoshell diameter was optimized after an in-depth analysis of the synthesis parameters that affected the formation and final size of the dye-loaded star polymer gold nanoshells. The main parameters examined were pH of the gold seeds used to nucleate the templates and the ratio of star polymer to gold hydroxide used during the growth of the outer gold shell.

Investigation and characterization of ZnO single crystal microtubes

DOE Office of Scientific and Technical Information (OSTI.GOV)

Al-Naser, Qusay A.H.; Zhou, Jian, E-mail: jianzhou@whut.edu.cn; Liu, Guizhen

2016-04-15

Morphological, structural, and optical characterization of microwave synthesized ZnO single crystal microtubes were investigated in this work. The structure and morphology of the ZnO microtubes are characterized using X-ray diffraction (XRD), single crystal diffraction (SCD), field emission scanning electron microscopy (FESEM), energy dispersive X-ray spectroscopy (EDX), and transmission electron microscopy (TEM). The results reveal that the as-synthesized ZnO microtube has a highly regular hexagonal cross section and smooth surfaces with an average length of 650–700 μm, an average outer diameter of 50 μm and wall thickness of 1–3 μm, possessing a single crystal wurtzite hexagonal structure. Optical properties of ZnOmore » single crystal microtubes were investigated by photoluminescence (PL) and ultraviolet-visible (UV-vis) absorption techniques. Room-temperature PL spectrum of the microtube reveal a strong UV emission peak at around 375.89 nm and broad and a weak visible emission with a main peak identified at 577 nm, which was assigned to the nearest band-edge emission and the deep-level emission, respectively. The band gap energy of ZnO microtube was found to be 3.27 eV. - Highlights: • ZnO microtube length of 650–700 μm, diameter of 50 μm, wall thickness of 1–3 μm • ZnO microtube possesses a single crystal wurtzite hexagonal structure. • The crystal system is hexahedral oriented along a-axis with indices of (100). • A strong and sharp UV emission at 375.89 nm (3.29 eV) • One prominent absorption band around 378.88 nm (3.27 eV)« less

Purification of 1.9-nm-diameter semiconducting single-wall carbon nanotubes by temperature-controlled gel-column chromatography and its application to thin-film transistor devices

NASA Astrophysics Data System (ADS)

Thendie, Boanerges; Omachi, Haruka; Hirotani, Jun; Ohno, Yutaka; Miyata, Yasumitsu; Shinohara, Hisanori

2017-06-01

Large-diameter semiconductor single-wall carbon nanotubes (s-SWCNTs) have superior mobility and conductivity to small-diameter s-SWCNTs. However, the purification of s-SWCNTs with diameters larger than 1.6 nm by gel filtration has been difficult owing to the low selectivity of the conventional purification method in these large-diameter regions. We report a combination of temperature-controlled gel filtration and the gradient elution technique that we developed to enrich a high-purity s-SWCNT with a diameter as large as 1.9 nm. The thin-film transistor (TFT) device using the 1.9-nm-diameter SWCNT shows an average channel mobility of 23.7 cm2 V-1 s-1, which is much higher than those of conventional SWCNT-TFTs with smaller-diameters of 1.5 and 1.4 nm.

Formation of Annular Protofibrillar Assembly by Cysteine Tripeptide: Unraveling the Interactions with NMR, FTIR, and Molecular Dynamics.

PubMed

Banerji, Biswadip; Chatterjee, Moumita; Pal, Uttam; Maiti, Nakul C

2017-07-06

Both hydrogen-bonding and hydrophobic interactions play a significant role in molecular assembly, including self-assembly of proteins and peptides. In this study, we report the formation of annular protofibrillar structure (diameter ∼500 nm) made of a newly synthesized s-benzyl-protected cysteine tripeptide, which was primarily stabilized by hydrogen-bonding and hydrophobic interactions. Atomic force microscopy and field emission scanning electron microscopy analyses found small oligomers (diameter ∼60 nm) to bigger annular (outer diameter ∼300 nm; inner diameter, 100 nm) and protofibrillar structures after 1-2 days of incubation. Rotating-frame Overhauser spectroscopic (ROESY) analysis revealed the presence of several nonbonded proton-proton interactions among the residues, such as amide protons with methylene group, aromatic protons with tertiary butyl group, and methylene protons with tertiary butyl group. These added significant stability to bring the peptides closer to form a well-ordered assembled structure. Hydrogen-deuterium exchange NMR measurement further suggested that two individual amide protons among the three amide groups were strongly engaged with the adjacent tripeptide via H-bond interaction. However, the remaining amide proton was found to be exposed to solvent and remained noninteracting with other tripeptide molecules. In addition to chemical shift values, a significant change in amide bond vibrations of the tripeptide was found due to the formation of the self-assembled structure. The amide I mode of vibrations involving two amide linkages appeared at 1641 and 1695 cm -1 in the solid state. However, in the assembled state, the stretching band at 1695 cm -1 became broad and slightly shifted to ∼1689 cm -1 . On the contrary, the band at 1641 cm -1 shifted to 1659 cm -1 and indicated that the -C═O bond associated with this vibration became stronger in the assembled state. These changes in Fourier transform infrared spectroscopy frequency clearly indicated changes in the amide backbone conformation and the associated hydrogen-bonding pattern due to the formation of the assembled structure. In addition to hydrogen bonding, molecular dynamics simulation indicated that the number of π-π interactions also increased with increasing number of tripeptides participated in the self-assembly process. Combined results envisaged a cross β-sheet assembly unit consisting of four intermolecular hydrogen bonds. Such noncovalent peptide assemblies glued by hydrogen-bonding and other weak forces may be useful in developing nanocapsule and related materials.

A centerless grinding unit used for precisely processing ferrules of optical fiber connector

NASA Astrophysics Data System (ADS)

Wu, Yongbo; Kondo, Takahiro; Kato, Masana

2005-02-01

This paper describes the development of a centerless grinding unit used for precisely processing ferrules, a key component of optical fiber connectors. In conventional processing procedure, the outer diameter of a ferrule is ground by employing a special machine tool, i.e., centerless grinder. However, in the case of processing small amount of ferrules, introducing a centerless grinder leads to high processing cost. Therefore, in order to take measures against this problem, the present authors propose a new centerless grinding technique where a compact centerless grinding unit, which is composed of an ultrasonic elliptic-vibration shoe, a workrest blade, and their respective holders, is installed on a popular surface grinder to perform the centerless grinding operations for outer diameter machining of ferrules. In this work, a unit is designed and constructed, and is installed on a surface grinder equipped with a diamond grinding wheel. Then, the performance of the unit is examined experimentally followed by grinding tests of ferrule"s outer diameter. As a result, the roundness of the ferrule"s outer diameter improved from the original value of around 3μm to the final value of around 0.5 μm, confirming the validity of the new technique.

Core break-off mechanism

NASA Technical Reports Server (NTRS)

Myrick, Thomas M. (Inventor)

2003-01-01

A mechanism for breaking off and retaining a core sample of a drill drilled into a ground substrate has an outer drill tube and an inner core break-off tube sleeved inside the drill tube. The break-off tube breaks off and retains the core sample by a varying geometric relationship of inner and outer diameters with the drill tube. The inside diameter (ID) of the drill tube is offset by a given amount with respect to its outer diameter (OD). Similarly, the outside diameter (OD) of the break-off tube is offset by the same amount with respect to its inner diameter (ID). When the break-off tube and drill tube are in one rotational alignment, the two offsets cancel each other such that the drill can operate the two tubes together in alignment with the drill axis. When the tubes are rotated 180 degrees to another positional alignment, the two offsets add together causing the core sample in the break-off tube to be displaced from the drill axis and applying shear forces to break off the core sample.

Room temperature synthesis and optical properties of small diameter (5 nm) ZnO nanorod arrays.

PubMed

Cho, Seungho; Jang, Ji-Wook; Lee, Jae Sung; Lee, Kun-Hong

2010-10-01

We report a simple wet-chemical synthesis of ∼5 nm diameter ZnO nanorod arrays at room temperature (20 °C) and normal atmospheric pressure (1 atm) and their optical properties. They were single crystalline in nature, and grew in the [001] direction. These small diameter ZnO nanorod arrays can also be synthesized at 0 °C. Control experiments were also conducted. On the basis of the results, we propose a mechanism for the spontaneous growth of the small diameter ZnO structures. The optical properties of the 5 nm diameter ZnO nanorod arrays synthesized using this method were probed by UV-Visible diffuse reflectance spectroscopy. A clear blue-shift, relative to the absorption band from 50 nm diameter ZnO nanorod arrays, was attributed to the quantum confinement effects caused by the small nanocrystal size in the 5 nm diameter ZnO nanorods.

Dual functional nisin-multi-walled carbon nanotubes coated filters for bacterial capture and inactivation.

PubMed

Dong, Xiuli; Yang, Liju

2015-01-01

Removal of pathogens from water is one way to prevent waterborne illness. In this paper, we developed dual functional carbon nanotube (CNT) modified filters for bacterial capture and inactivation, utilizing multi-walled CNTs (MWCNTs) to coat on commercially available filters and making use of the exceptional adsorption property of CNTs to adsorb a natural antimicrobial peptide-nisin on it. Two types of MWCNTs with different outer layer diameters were used (MWCNTs1: <8 nm in diameter; MWCNTs2: 10-20 nm in diameter). The thickness of MWCNT layers, surface morphology, and surface hydrophobicity of both types of MWCNT coated filters were characterized. The MWCNT coating on filters significantly increased the surface hydrophobicity. The absorption of nisin and the capture of bacterial pathogens were correlated with increased surface hydrophobicity. The MWCNTs1 and MWCNTs2 filters with 1.5 mg MWCNTs loading captured 2.44 and 3.88 log of cells, respectively, from aqueous solutions containing a total of ~10(6) CFU/mL cells. Nisin deposit at the amount of 0.5 mg on the surfaces of MWCNT filters significantly reduced the viability of captured B. anthracis cells by 95.71-97.19 %, and inhibited the metabolic activities of the captured cells by approximately 98.3 %. The results demonstrated that the MWCNT-nisin filters achieved dual functions in bacterial pathogen capture and inhibition in one single filtration step, which is potentially applicable in removing undesired microorganisms from water sources and inhibiting captured Gram positive bacteria activities.

Application of thermospray flame furnace atomic absorption spectrometry for investigation of silver nanoparticles.

PubMed

Sirirat, Natnicha; Tetbuntad, Kornrawee; Siripinyanond, Atitaya

2017-03-01

Thermospray flame furnace atomic absorption spectrometry (TS-FF-AAS) was applied to investigate the time-dependent absorption peak profile of various forms of silver. The thermospray flame furnace was set up with a 10-cm-long nickel tube with six holes, each 2.0 mm in diameter, to allow the flame to enter, and this nickel tube acted as a furnace. A sample of 300 μL was introduced into this furnace by use of water as a carrier at a flow rate of 0.5 mL min -1 through the ceramic capillary (0.5-mm inner diameter and 2.0-mm outer diameter), which was inserted into the front hole of the nickel tube. The system was applied to examine atomization behaviors of silver nanoparticles (AgNPs) with particle sizes ranging from 10 to 100 nm. The atomization rate of AgNPs was faster than that of the dissolved silver ion. With increased amount of silver, the decay time observed from the time-dependent absorption peak profile was shortened in the case of dissolved silver ion, but it was increased in the case of AgNPs. With the particle size ranging from 10 to 100 nm, the detection sensitivity was indirectly proportional to the particle size, suggesting that TS-FF-AAS may offer insights into the particle size of AgNPs provided that the concentration of the silver is known. To obtain quantitative information on AgNPs, acid dissolution of the particles was performed before TS-FF-AAS analysis, and recoveries of 80-110% were obtained.

Study of the effect of varying core diameter, shell thickness and strain velocity on the tensile properties of single crystals of Cu-Ag core-shell nanowire using molecular dynamics simulations

NASA Astrophysics Data System (ADS)

Sarkar, Jit; Das, D. K.

2018-01-01

Core-shell type nanostructures show exceptional properties due to their unique structure having a central solid core of one type and an outer thin shell of another type which draw immense attention among researchers. In this study, molecular dynamics simulations are carried out on single crystals of copper-silver core-shell nanowires having wire diameter ranging from 9 to 30 nm with varying core diameter, shell thickness, and strain velocity. The tensile properties like yield strength, ultimate tensile strength, and Young's modulus are studied and correlated by varying one parameter at a time and keeping the other two parameters constant. The results obtained for a fixed wire size and different strain velocities were extrapolated to calculate the tensile properties like yield strength and Young's modulus at standard strain rate of 1 mm/min. The results show ultra-high tensile properties of copper-silver core-shell nanowires, several times than that of bulk copper and silver. These copper-silver core-shell nanowires can be used as a reinforcing agent in bulk metal matrix for developing ultra-high strength nanocomposites.

Optical properties of carbon nanotubes

NASA Astrophysics Data System (ADS)

Chen, Gugang

This thesis addresses the optical properties of novel carbon filamentary nanomaterials: single-walled carbon nanotubes (SWNTs), double-walled carbon nanotubes (DWNTs), and SWNTs with interior C60 molecules ("peapods"). Optical reflectance spectra of bundled SWNTs are discussed in terms of their electronic energy band structure. An Effective Medium Model for a composite material was found to provide a reasonable description of the spectra. Furthermore, we have learned from optical absorption studies of DWNTs and C60-peapods that the host tube and the encapsulant interact weakly; small shifts in interband absorption structure were observed. Resonant Raman scattering studies on SWNTs synthesized via the HiPCO process show that the "zone-folding" approximation for phonons and electrons works reasonably well, even for small diameter (d < 1 nm) tubes. The energy of optical transitions between van Hove singularities in the electronic density of states computed from the "zone-folding" model (with gamma0 = 2.9 eV) agree well with the resonant conditions for Raman scattering. Small diameter tubes were found to exhibit additional sharp Raman bands in the frequency range 500-1200 cm-1 with an, as yet, undetermined origin. The Raman spectrum of a DWNT was found to be well described by a superposition of the Raman spectra expected for inner and outer tubes, i.e., no charge transfer occurs and the weak van der Waals (vdW) interaction between tubes does not have significant impact on the phonons. A ˜7 cm-1 downshift of the small diameter, inner-tube tangential mode frequency was observed, however, but attributed to a tube wall curvature effect, rather than the vdW interaction. Finally, we studied the chemical doping of DWNTs, where the dopant (Br anions) is chemically bound to the outside of the outer tube. The doped DWNT system is a model for a cylindrical molecular capacitor. We found experimentally that 90% of the positive charge resides on the outer tube, so that most of electric field on the inner tube is screened, i.e., we have observed a molecular Faraday cage effect. A self-consistent theoretical model in the tight-binding approximation with a classical electrostatic energy term is in good agreement with our experimental results.

Facile synthesis of ultrahigh-surface-area hollow carbon nanospheres for enhanced adsorption and energy storage

PubMed Central

Xu, Fei; Tang, Zhiwei; Huang, Siqi; Chen, Luyi; Liang, Yeru; Mai, Weicong; Zhong, Hui; Fu, Ruowen; Wu, Dingcai

2015-01-01

Exceptionally large surface area and well-defined nanostructure are both critical in the field of nanoporous carbons for challenging energy and environmental issues. The pursuit of ultrahigh surface area while maintaining definite nanostructure remains a formidable challenge because extensive creation of pores will undoubtedly give rise to the damage of nanostructures, especially below 100 nm. Here we report that high surface area of up to 3,022 m2 g−1 can be achieved for hollow carbon nanospheres with an outer diameter of 69 nm by a simple carbonization procedure with carefully selected carbon precursors and carbonization conditions. The tailor-made pore structure of hollow carbon nanospheres enables target-oriented applications, as exemplified by their enhanced adsorption capability towards organic vapours, and electrochemical performances as electrodes for supercapacitors and sulphur host materials for lithium–sulphur batteries. The facile approach may open the doors for preparation of highly porous carbons with desired nanostructure for numerous applications. PMID:26072734

SiO2/ZnO Composite Hollow Sub-Micron Fibers: Fabrication from Facile Single Capillary Electrospinning and Their Photoluminescence Properties.

PubMed

Song, Guanying; Li, Zhenjiang; Li, Kaihua; Zhang, Lina; Meng, Alan

2017-02-24

In this work, SiO2/ZnO composite hollow sub-micron fibers were fabricated by a facile single capillary electrospinning technique followed by calcination, using tetraethyl orthosilicate (TEOS), polyvinylpyrrolidone (PVP) and ZnO nanoparticles as raw materials. The characterization results of the scanning electron microscopy (SEM), transmission electron microscopy (TEM), X-ray diffraction (XRD) and Fourier transform infrared spectroscopy (FT-IR) spectra indicated that the asprepared composite hollow fibers consisted of amorphous SiO2 and hexagonal wurtzite ZnO. The products revealed uniform tubular structure with outer diameters of 400-500 nm and wall thickness of 50-60 nm. The gases generated and the directional escaped mechanism was proposed to illustrate the formation of SiO2/ZnO composite hollow sub-micron fibers. Furthermore, a broad blue emission band was observed in the photoluminescence (PL) of SiO2/ZnO composite hollow sub-micron fibers, exhibiting great potential applications as blue light-emitting candidate materials.

The Tom Core Complex

PubMed Central

Ahting, Uwe; Thun, Clemens; Hegerl, Reiner; Typke, Dieter; Nargang, Frank E.; Neupert, Walter; Nussberger, Stephan

1999-01-01

Translocation of nuclear-encoded preproteins across the outer membrane of mitochondria is mediated by the multicomponent transmembrane TOM complex. We have isolated the TOM core complex of Neurospora crassa by removing the receptors Tom70 and Tom20 from the isolated TOM holo complex by treatment with the detergent dodecyl maltoside. It consists of Tom40, Tom22, and the small Tom components, Tom6 and Tom7. This core complex was also purified directly from mitochondria after solubilization with dodecyl maltoside. The TOM core complex has the characteristics of the general insertion pore; it contains high-conductance channels and binds preprotein in a targeting sequence-dependent manner. It forms a double ring structure that, in contrast to the holo complex, lacks the third density seen in the latter particles. Three-dimensional reconstruction by electron tomography exhibits two open pores traversing the complex with a diameter of ∼2.1 nm and a height of ∼7 nm. Tom40 is the key structural element of the TOM core complex. PMID:10579717

Self-Assembly of Porphyrin J-Aggregates

NASA Astrophysics Data System (ADS)

Snitka, Valentinas; Rackaitis, Mindaugas; Navickaite, Gintare

2006-03-01

The porphyrin nanotubes were built by ionic self-assembly of two oppositely charged porphyrins in aqueous solution. The porphyrins in the acid aqueous solution self-assemble into J-aggregates, wheels or other structures. The electrostatic forces between these porphyrin blocks contribute to the formation of porphyrin aggregates in the form of nanotubes, enhance the structural stability of these nanostructures. The nanotubes were composed mixing aqueous solutions of the two porphyrins - anionic Meso-tetra(4- sulfonatophrnyl)porhine dihydrochloride (TPPS4) and cationic Meso-tetra(4-pyridyl)porphine (T4MPyP). The porphyrin nanotubes obtained are hollow structures with the length of 300 nm and diameter 50 nm. Photocatalytic porphyrins are used to reduce metal complexes from aqueous solution and to control the deposition of Au from AuHCl4 and Au nanoparticles colloid solutions onto porphyrin nanotubes. Porphyrin nanotubes are shown to reduce metal complexes and deposit the metal selectively onto the inner or outer surface of the tubes, leading to nanotube-metal composite structures.

Multi-level multi-thermal-electron FDTD simulation of plasmonic interaction with semiconducting gain media: applications to plasmonic amplifiers and nano-lasers.

PubMed

Chen, X; Bhola, B; Huang, Y; Ho, S T

2010-08-02

Interactions between a semiconducting gain medium and confined plasmon-polaritons are studied using a multilevel multi-thermal-electron finite-difference time-domain (MLMTE-FDTD) simulator. We investigated the amplification of wave propagating in a plasmonic metal-semiconductor-metal (MSM) waveguide filled with semiconductor gain medium and obtained the conditions required to achieve net optical gain. The MSM gain waveguide is used to form a plasmonic semiconductor nano-ring laser(PSNRL) with an effective mode volume of 0.0071 microm3, which is about an order of magnitude smaller than the smallest demonstrated integrated photonic crystal based laser cavities. The simulation shows a lasing threshold current density of 1kA/cm2 for a 300 nm outer diameter ring cavity with 80 nm-wide ring. This current density can be realistically achieved in typical III-V semiconductor, which shows the experimental feasibility of the proposed PSNRL structure.

Polymer micromold and fabrication process

DOEpatents

Lee, A.P.; Northrup, M.A.; Ahre, P.E.; Dupuy, P.C.

1997-08-19

A mold assembly is disclosed with micro-sized features in which the hollow portion thereof is fabricated from a sacrificial mandrel which is surface treated and then coated to form an outer shell. The sacrificial mandrel is then selectively etched away leaving the outer shell as the final product. The sacrificial mandrel is fabricated by a precision lathe, for example, so that when removed by etching the inner or hollow area has diameters as small as 10`s of micros ({micro}m). Varying the inside diameter contours of the mold can be accomplished with specified ramping slopes formed on the outer surface of the sacrificial mandrel, with the inside or hollow section being, for example, 275 {micro}m in length up to 150 {micro}m in diameter within a 6 mm outside diameter (o.d.) mold assembly. The mold assembly itself can serve as a micronozzle or microneedle, and plastic parts, such as microballoons for angioplasty, polymer microparts, and microactuators, etc., may be formed within the mold assembly. 6 figs.

Polymer micromold and fabrication process

DOEpatents

Lee, Abraham P.; Northrup, M. Allen; Ahre, Paul E.; Dupuy, Peter C.

1997-01-01

A mold assembly with micro-sized features in which the hollow portion thereof is fabricated from a sacrificial mandrel which is surface treated and then coated to form an outer shell. The sacrificial mandrel is then selectively etched away leaving the outer shell as the final product. The sacrificial mandrel is fabricated by a precision lathe, for example, so that when removed by etching the inner or hollow area has diameters as small as 10's of micros (.mu.m). Varying the inside diameter contours of the mold can be accomplished with specified ramping slopes formed on the outer surface of the sacrificial mandrel, with the inside or hollow section being, for example, 275 .mu.m in length up to 150 .mu.m in diameter within a 6 mm outside diameter (o.d.) mold assembly. The mold assembly itself can serve as a micronozzle or microneedle, and plastic parts, such as microballoons for angioplasty, polymer microparts, and microactuators, etc., may be formed within the mold assembly.

Electromagnetic characteristics of eccentric figure-eight coils for transcranial magnetic stimulation: A numerical study

NASA Astrophysics Data System (ADS)

Kato, Takuya; Sekino, Masaki; Matsuzaki, Taiga; Nishikawa, Atsushi; Saitoh, Youichi; Ohsaki, Hiroyuki

2012-04-01

Repetitive transcranial magnetic stimulation (rTMS) is effective for treatment of several neurological and psychiatric diseases. We proposed an eccentric figure-eight coil, which induces strong eddy currents in the target brain tissue. In this study, numerical analyses were carried out to obtain magnetic field distribution of the eccentric figure-eight coil and eddy current in the brain. The analyses were performed with various coil design parameters, such as the outer and inner diameters and number of turns, to investigate the influence of these parameters on the coil characteristics. Increases in the inner diameter, outer diameter, and number of turns caused increases in the maximum eddy current densities. Coil inductance, working voltage, and heat generation also became higher with the increases in these design parameters. In order to develop a compact stimulator system for use at home, we need to obtain strong eddy current density, keeping the working voltage as low as possible. Our results show that it is effective to enlarge the outer diameter.

Quantitative evaluation of lipid concentration in atherosclerotic plaque phantom by near-infrared multispectral angioscope at wavelengths around 1200 nm

NASA Astrophysics Data System (ADS)

Matsui, Daichi; Ishii, Katsunori; Awazu, Kunio

2015-07-01

Atherosclerosis is a primary cause of critical ischemic diseases like heart infarction or stroke. A method that can provide detailed information about the stability of atherosclerotic plaques is required. We focused on spectroscopic techniques that could evaluate the chemical composition of lipid in plaques. A novel angioscope using multispectral imaging at wavelengths around 1200 nm for quantitative evaluation of atherosclerotic plaques was developed. The angioscope consists of a halogen lamp, an indium gallium arsenide (InGaAs) camera, 3 optical band pass filters transmitting wavelengths of 1150, 1200, and 1300 nm, an image fiber having 0.7 mm outer diameter, and an irradiation fiber which consists of 7 multimode fibers. Atherosclerotic plaque phantoms with 100, 60, 20 vol.% of lipid were prepared and measured by the multispectral angioscope. The acquired datasets were processed by spectral angle mapper (SAM) method. As a result, simulated plaque areas in atherosclerotic plaque phantoms that could not be detected by an angioscopic visible image could be clearly enhanced. In addition, quantitative evaluation of atherosclerotic plaque phantoms based on the lipid volume fractions was performed up to 20 vol.%. These results show the potential of a multispectral angioscope at wavelengths around 1200 nm for quantitative evaluation of the stability of atherosclerotic plaques.

Free-Standing Zone Plate Optimized for He II 30.4 nm Solar Irradiance Measurements Having High Accuracy and Stability in Space

NASA Astrophysics Data System (ADS)

Seely, J. F.; McMullin, D. R.; Vest, R.; Sakdinawat, A.; Chang, C.; Jones, A. R.; Bremer, J.

2015-12-01

A zone plate was designed to record the He II 30.4 nm solar irradiance, was fabricated using electron beam lithography, and was absolutely calibrated using the NIST SURF synchrotron. The zone plate has an open support grid identical to those used to successfully launch transmission gratings in previous solar radiometers and is otherwise free-standing with no support membrane that would absorb EUV radiation. The measured efficiency of 3.0 ± 0.1% at 30.4 nm is consistent with detailed modeling of the efficiency and accounting for the geometrical transmittance of the support grid. The binary nature of the zone plate, consisting of opaque gold bars and open spaces with no support membrane, results in excellent long-term stability in space against contamination, radiation damage, and other effects that could alter the efficiency and instrument throughput. The zone plate's focusing property enables the rejection of out-of-band radiation by small apertures and high signal to background values that are superior to previous radiometers. The 4 mm outer diameter of the zone plate and the 25 mm focal length for 30.4 nm radiation enable a compact instrument that is attractive for small CubeSats and other space flight missions where resources are extremely limited.

The effect of cup outer sizes on the contact mechanics and cement fixation of cemented total hip replacements.

PubMed

Hua, Xijin; Li, Junyan; Wang, Ling; Wilcox, Ruth; Fisher, John; Jin, Zhongmin

2015-10-01

One important loosening mechanism of the cemented total hip arthroplasty is the mechanical overload at the bone-cement interface and consequent failure of the cement fixation. Clinical studies have revealed that the outer diameter of the acetabular component is a key factor in influencing aseptic loosening of the hip arthroplasty. The aim of the present study was to investigate the influence of the cup outer diameter on the contact mechanics and cement fixation of a cemented total hip replacement (THR) with different wear penetration depths and under different cup inclination angles using finite element (FE) method. A three-dimensional FE model was developed based on a typical Charnley hip prosthesis. Two acetabular cup designs with outer diameters of 40 and 43 mm were modelled and the effect of cup outer diameter, penetration depth and cup inclination angle on the contact mechanics and cement fixation stresses in the cemented THR were studied. The results showed that for all penetration depths and cup inclination angles considered, the contact mechanics in terms of peak von Mises stress in the acetabular cup and peak contact pressure at the bearing surface for the two cup designs were similar (within 5%). However, the peak von Mises stress, the peak maximum principal stress and peak shear stress in the cement mantle at the bone-cement interface for the 43 mm diameter cup design were predicted to be lower compared to those for the 40 mm diameter cup design. The differences were predicted to be 15-19%, 15-22% and 18-20% respectively for different cup penetration depths and inclination angles, which compares to the clinical difference of aseptic loosening incidence of about 20% between the two cup designs. Copyright © 2015 IPEM. Published by Elsevier Ltd. All rights reserved.

Flammutoxin, a cytolysin from the edible mushroom Flammulina velutipes, forms two different types of voltage-gated channels in lipid bilayer membranes.

PubMed

Tadjibaeva, G; Sabirov, R; Tomita, T

2000-08-25

Flammutoxin, a 31-kDa cardiotoxic and cytolytic protein from the edible mushroom Flammulina velutipes, has been shown to assemble into a pore-forming annular oligomer with outer and inner diameters of 10 and 5 nm on the target cells [Tomita et al., Biochem. J. 333 (1998) 129-137]. Here we studied electrophysiological properties of flammutoxin channels using planar lipid bilayer technique, and found that flammutoxin formed two types of moderately cation-selective, voltage-gated channels with smaller and larger current amplitudes (1-4.5 pA and 20-30 pA, respectively, at 20 mV) in the lipid bilayers composed of phospholipid and cholesterol. The larger-conductance single channel showed the properties of a wide water-filled pore such as a linear relationship between channel conductance and salt concentration of the bathing solution. The functional diameter of the larger-conductance channel was estimated to be 4-5 nm by measuring the current conductance in the presence of polyethylene glycols of various sizes. In contrast, the smaller-conductance single channels showed a non-linear current to voltage curve and a saturating conductance to increasing salt concentration. These results suggest that the larger-conductance channel of flammutoxin corresponds to the hemolytic pore complex, while the smaller-conductance channel may reflect the intermediate state(s) of the assembling toxin.

Carbon nanotubes shynthesis in fluidized bed reactor equipped with a cyclone

NASA Astrophysics Data System (ADS)

Setyopratomo, P.; Sudibandriyo, M.; Wulan, P. P. D. K.

2018-03-01

This work aimed to observe the performance of a fluidized bed reactor which was equipped with a cyclone in the synthesis of carbon nanotubes (CNT) by chemical vapor deposition. Liquefied petroleum gas with a constant volumetric flow rate of 1940 cm3/minutes was fed to the reactor as a carbon source, while a combination of metal components of Fe-Co-Mo supported on MgO was used as catalyst. The CNT synthesis was carried out at a reaction temperature which was maintained at around 800 – 850 °C for 1 hour. The CNT yield was decreased sharply when the catalyst feed was increased. The carbon efficiency is directly proportional to the mass of catalyst fed. It was found from the experiment that the mass of as-grown CNT increased in proportion to the increase of the catalyst mass fed. A sharp increase of the mass percentage of carbon nanotubes entrainment happened when the catalyst feed was raised from 3 to 7 grams. Agglomerates of carbon nanotubes have been formed. The agglomerates composed of mutually entangled carbon nanotubes which have an outer diameter range 8 – 14 nm and an inner diameter range 4 – 10 nm, which confirmed that the multi-walled carbon nanotubes were formed in this synthesis. It was found that the mesopores dominate the pore structure of the CNT product and contribute more than 90 % of the total pore volume.

Fiber optic muzzle brake tip for reducing fiber burnback and stone retropulsion during thulium fiber laser lithotripsy.

PubMed

Hutchens, Thomas C; Gonzalez, David A; Irby, Pierce B; Fried, Nathaniel M

2017-01-01

The experimental thulium fiber laser (TFL) is being explored as an alternative to the current clinical gold standard Holmium:YAG laser for lithotripsy. The near single-mode TFL beam allows coupling of higher power into smaller optical fibers than the multimode Holmium laser beam profile, without proximal fiber tip degradation. A smaller fiber is desirable because it provides more space in the ureteroscope working channel for increased saline irrigation rates and allows maximum ureteroscope deflection. However, distal fiber tip burnback increases as fiber diameter decreases. Previous studies utilizing hollow steel sheaths around recessed distal fiber tips reduced fiber burnback but increased stone retropulsion. A “fiber muzzle brake” was tested for reducing both fiber burnback and stone retropulsion by manipulating vapor bubble expansion. TFL lithotripsy studies were performed at 1908 nm, 35 mJ, 500 ?? ? s , and 300 Hz using a 100 - ? m -core fiber. The optimal stainless steel muzzle brake tip tested consisted of a 1-cm-long, 560 - ? m -outer-diameter, 360 - ? m -inner-diameter tube with a 275 - ? m -diameter through hole located 250 ?? ? m from the distal end. The fiber tip was recessed a distance of 500 ?? ? m . Stone phantom retropulsion, fiber tip burnback, and calcium oxalate stone ablation studies were performed ex vivo. Small stones with a mass of 40 ± 4 ?? mg and 4-mm-diameter were ablated over a 1.5-mm sieve in 25 ± 4 ?? s

Rapid-quench axially staged combustor

DOEpatents

Feitelberg, Alan S.; Schmidt, Mark Christopher; Goebel, Steven George

1999-01-01

A combustor cooperating with a compressor in driving a gas turbine includes a cylindrical outer combustor casing. A combustion liner, having an upstream rich section, a quench section and a downstream lean section, is disposed within the outer combustor casing defining a combustion chamber having at least a core quench region and an outer quench region. A first plurality of quench holes are disposed within the liner at the quench section having a first diameter to provide cooling jet penetration to the core region of the quench section of the combustion chamber. A second plurality of quench holes are disposed within the liner at the quench section having a second diameter to provide cooling jet penetration to the outer region of the quench section of the combustion chamber. In an alternative embodiment, the combustion chamber quench section further includes at least one middle region and at least a third plurality of quench holes disposed within the liner at the quench section having a third diameter to provide cooling jet penetration to at least one middle region of the quench section of the combustion chamber.

Nanoparticle-Based Delivery of Anaplasma marginale Membrane Proteins; VirB9-1 and VirB10 Produced in the Pichia pastoris Expression System.

PubMed

Zhang, Bing; Cavallaro, Antonio S; Mody, Karishma T; Zhang, Jun; Deringer, James R; Brown, Wendy C; Mahony, Timothy J; Yu, Chengzhong; Mitter, Neena

2016-11-05

Bovine anaplasmosis or cattle-tick fever is a tick-borne haemolytic disease caused by the rickettsial haemoparasite Anaplasma marginale in tropical and subtropical areas of the world. While difficult to express, the proteins VirB9-1 and VirB10 are immunogenic components of the outer membrane type IV secretion system that have been identified as candidate antigens for vaccines targeting of A. marginale . Soluble VirB9-1 and VirB10 were successfully expressed using Pichia pastoris . When formulated with the self-adjuvanting silica vesicles, SV-100 (diameter: 50 nm, and pore entrance size: 6 nm), 200 µg of VirB9-1 and VirB10 were adsorbed per milligram of nanoparticle. The VirB9-1 and VirB10, SV-100 formulations were shown to induce higher antibody responses in mice compared to the QuilA formulations. Moreover, intracellular staining of selected cytokines demonstrated that both VirB9-1 and VirB10 formulations induced cell-mediated immune responses in mice. Importantly, the SV-100 VirB9-1 and VirB10 complexes were shown to specifically stimulate bovine T-cell linages derived from calves immunised with A. marginale outer membrane fractions, suggesting formulations will be useful for bovine immunisation and protection studies. Overall this study demonstrates the potential of self-adjuvanting silica vesicle formulations to address current deficiencies in vaccine delivery applications.

Systems and methods for determining strength of cylindrical structures by internal pressure loading

DOEpatents

DeTeresa, Steven John; Groves, Scott Eric; Sanchez, Roberto Joseph; Andrade, William Andrew

2015-08-04

In one embodiment, an apparatus, includes: a mandrel; an expansion cylinder, comprising: opposite first and second ends; an inner circumferential surface extending between the ends and characterized by an inner diameter, the inner circumferential surface defining a hollow cavity; an outer circumferential surface extending between the ends and characterized by an outer diameter that is greater than the inner diameter; and a plurality of slots extending from the inner circumferential surface to the outer circumferential surface and latitudinally oriented between the ends; and one or more base plates configured to engage one of the ends of the expansion cylinder. In another embodiment, a method includes: arranging an expansion cylinder inside a test cylinder; arranging a mandrel inside the expansion cylinder; applying a force to the mandrel for exerting a radial force on the expansion cylinder; and detecting one or more indicia of structural failure of the test cylinder.

Method and apparatus for wind turbine air gap control

DOEpatents

Grant, James Jonathan; Bagepalli, Bharat Sampathkumaran; Jansen, Patrick Lee; DiMascio, Paul Stephen; Gadre, Aniruddha Dattatraya; Qu, Ronghai

2007-02-20

Methods and apparatus for assembling a wind turbine generator are provided. The wind turbine generator includes a core and a plurality of stator windings circumferentially spaced about a generator longitudinal axis, a rotor rotatable about the generator longitudinal axis wherein the rotor includes a plurality of magnetic elements coupled to a radially outer periphery of the rotor such that an airgap is defined between the stator windings and the magnetic elements and the plurality of magnetic elements including a radially inner periphery having a first diameter. The wind turbine generator also includes a bearing including a first member in rotatable engagement with a radially inner second member, the first member including a radially outer periphery, a diameter of the radially outer periphery of the first member being substantially equal to the first diameter, the rotor coupled to the stator through the bearing such that a substantially uniform airgap is maintained.

A novel strategy to directly fabricate flexible hollow nanofibers with tunable luminescence-electricity-magnetism trifunctionality using one-pot electrospinning.

PubMed

Liu, Yawen; Ma, Qianli; Dong, Xiangting; Yu, Wensheng; Wang, Jinxian; Liu, Guixia

2015-09-21

Novel photoluminescent-electrical-magnetic trifunctional flexible Eu(BA)3phen/PANI/Fe3O4/PVP (BA = benzoic acid, phen = phenanthroline, PANI = polyaniline, PVP = polyvinylpyrrolidone) hollow nanofibers were fabricated by a one-pot electrospinning technique using a specially designed coaxial spinneret for the first time. Very different from the traditional preparation process of hollow fibers via coaxial electrospinning, which needs to firstly fabricate the coaxial fibers and followed by removing the core through high-temperature calcination or solvent extraction, in our current study, no core spinning solution is used to directly fabricate hollow nanofibers. The morphology and properties of the obtained hollow nanofibers were characterized in detail using X-ray diffractometry, scanning electron microscopy, transmission electron microscopy, fluorescence spectroscopy, Fourier-transform infrared spectroscopy, a 4-point probe resistivity measurement system and vibrating sample magnetometry. The Eu(BA)3phen/PANI/Fe3O4/PVP hollow nanofibers, with outer diameters of ca. 305 nm and inner diameters of about 140 nm, exhibit excellent photoluminescence performance, electrical conductivity and magnetic properties. Fluorescence emission peaks of Eu(3+) are observed in the Eu(BA)3phen/PANI/Fe3O4/PVP hollow nanofibers and assigned to the (5)D0→(7)F0 (580 nm), (5)D0→(7)F1 (592 nm) and (5)D0→(7)F2 (616 nm) energy level transitions of Eu(3+) ions, and the (5)D0→(7)F2 hypersensitive transition at 616 nm is the predominant emission peak. The electrical conductivity of the hollow nanofibers reaches up to the order of 10(-3) S cm(-1). The luminescent intensity, electrical conductivity and magnetic properties of the hollow nanofibers can be tuned by adding various amounts of Eu(BA)3phen, PANI and Fe3O4 nanoparticles. The new-type photoluminescent-electrical-magnetic trifunctional flexible hollow nanofibers hold potential for a variety of applications, including electromagnetic interference shielding, microwave absorption, molecular electronics and biomedicine. The design conception and synthetic strategy developed in this study are of universal significance to construct other multifunctional hollow one-dimensional nanomaterials.

[Ultrastructure and cytochemistry of the pellicle and apical complexes of the kinete of Babesia bigemina and Babesia ovis in the hemolymph and oavry of the tick].

PubMed

Weber, G

1980-02-01

The term kinete is used in this paper for the cigar-shaped, motile development stages (VERMICULE") OF Babesia occurring intra- and extracellularly in hemolymph and overy (including oocytes) of vectors, hard ticks (Ixodoidea). The structure of, and cytochemical activities of hydrolases (acid phosphatase, nonspecific esterase) in the pellicle and the apical complex was studied at the fine-structural level in kinetes of Babesia bigemina Smith & Kilborne, in hemolympho of female Boophilus microplus Canestrini. The cytochemistry of acid hydrolases was studied also in kinetes of Babesia ovis (Babès) Starcovici, in hemolymph and ovary of Rhipicephalus bursa Canestrini & Fanzago. The pellicle of the B. bigemina kinetes is composted of 3 membranes (pellicular complex): an outer membrane, approximately 8 nm thick (the plasmalemma) and 2 innder ones, each approximately nm thick, lying closely together. The outer membrane appears to be covered by a structureless coat, 3 nm thick. The space between the inner double membrane and the plasmalemma is 7.5 nm. The whole pellicular complex is 30 nm in diameter. The 2 inner pellicular membranes appear to be derived from the endoplasmic reticulum (ER) for the following reasons: (a) a layer of hydrolase-active material is enclosed by these membranes; (b) in the spheroid parasite stages which transform from kinetes inside hemocytes, the inner double membrane is apparently replaced by an ER cisterna; (c) the thickness of each of the inner pellicular membranes is approximately the same as that of the ER membrane. There are circular openings in the pellicular double membrane with average diameters of 100 nm; despite some similarity to micropores, they have a specific structure. The term Intrapellikularfenster (IPF) (intrapellicular windows) or pseudomicropores is proposed for these pellicular differentiations. The margin of an IPF is formed by the 2 inner membranes folding into each other; cytoplasmic, electron-dense material is accumulated alongside this edge. Unlike that of micropores, the plasmalemma of the IPF is not invaginated. The IPF appears as a single, dark ring in tangential sections. At times, rhoptry-like bodies are associated with the openings. The function of the IPF is not known. An intrapellicular opening similar to the IPF, although wider, is present at the apex of the parasite. Its margin coincides with the inners edge of the apical ring. Typical subpellicular microtubuli were not observed in the Babesia kinetes. The apical complex of the B. bigemina kinetes consists of an Apikalschirm (apical umbrella), a crown of microtubuli beneath it, and rhoptries: micronemes are also present in large numbers. The Apikalschirm is located beneath the pellicle of the apical pole of the parasite. It is a wheel-like structure composed of spokes radiating from a wide, hub=like central ring (apical ring). It should be stressed that the apical ring is not identical with the polar ring described as an integral part of the pellicular complex in other Apicomplexa...

Sample-morphology effects on x-ray photoelectron peak intensities. III. Simulated spectra of model core–shell nanoparticles

DOE Office of Scientific and Technical Information (OSTI.GOV)

Powell, Cedric J., E-mail: cedric.powell@nist.gov; Chudzicki, Maksymilian; Werner, Wolfgang S. M.

2015-09-15

The National Institute of Standards and Technology database for the simulation of electron spectra for surface analysis has been used to simulate Cu 2p photoelectron spectra for four types of spherical copper–gold nanoparticles (NPs). These simulations were made to extend the work of Tougaard [J. Vac. Sci. Technol. A 14, 1415 (1996)] and of Powell et al. [J. Vac. Sci. Technol. A 31, 021402 (2013)] who performed similar simulations for four types of planar copper–gold films. The Cu 2p spectra for the NPs were compared and contrasted with analogous results for the planar films and the effects of elastic scatteringmore » were investigated. The new simulations were made for a monolayer of three types of Cu/Au core–shell NPs on a Si substrate: (1) an Au shell of variable thickness on a Cu core with diameters of 0.5, 1.0, 2.0, 5.0, and 10.0 nm; (2) a Cu shell of variable thickness on an Au core with diameters of 0.5, 1.0, 2.0, 5.0, and 10.0 nm; and (3) an Au shell of variable thickness on a 1 nm Cu shell on an Au core with diameters of 0.5, 1.0, 2.0, 5.0, and 10.0 nm. For these three morphologies, the outer-shell thickness was varied until the Cu 2p{sub 3/2} peak intensity was the same (within 2%) as that found in our previous work with planar Cu/Au morphologies. The authors also performed similar simulations for a monolayer of spherical NPs consisting of a CuAu{sub x} alloy (also on a Si substrate) with diameters of 0.5, 1.0, 2.0, 5.0, and 10.0 nm. In the latter simulations, the relative Au concentration (x) was varied to give the same Cu 2p{sub 3/2} peak intensity (within 2%) as that found previously. For each morphology, the authors performed simulations with elastic scattering switched on and off. The authors found that elastic-scattering effects were generally strong for the Cu-core/Au-shell and weak for the Au-core/Cu-shell NPs; intermediate elastic-scattering effects were found for the Au-core/Cu-shell/Au-shell NPs. The shell thicknesses required to give the selected Cu 2p{sub 3/2} peak intensity for the three types of core–shell NPs were less than the corresponding film thicknesses of planar samples since Cu 2p photoelectrons can be detected from the sides and, for the smaller NPs, bottoms of the NPs. Elastic-scattering effects were also observed on the Au atomic fractions found for the CuAu{sub x} NP alloys with different diameters.« less

The Physics of Ultrabroadband Frequency Comb Generation and Optimized Combs for Measurements in Fundamental Physics

DTIC Science & Technology

2016-07-02

beams Superresolution machining Threshold effect of ablation means that structure diameter is less than the beam diameter fs pulses at 800 nm yield 200...Approved for public release: distribution unlimited. Applications of Bessel beams Superresolution machining Threshold effect of ablation means that... Superresolution machining Threshold effect of ablation means that structure diameter is less than the beam diameter fs pulses at 800 nm yield 200 nm

Detrimental impact of silica nanoparticles on the nanomechanical properties of Escherichia coli, studied by AFM.

PubMed

Mathelié-Guinlet, Marion; Grauby-Heywang, Christine; Martin, Axel; Février, Hugo; Moroté, Fabien; Vilquin, Alexandre; Béven, Laure; Delville, Marie-Hélène; Cohen-Bouhacina, Touria

2018-05-29

Despite great innovative and technological promises, nanoparticles (NPs) can ultimately exert an antibacterial activity by affecting the cell envelope integrity. This envelope, by conferring the cell its rigidity and protection, is intimately related to the mechanical behavior of the bacterial surface. Depending on their size, surface chemistry, shape, NPs can induce damages to the cell morphology and structure among others, and are therefore expected to alter the overall mechanical properties of bacteria. Although Atomic Force Microscopy (AFM) stands as a powerful tool to study biological systems, with high resolution and in near physiological environment, it has rarely been applied to investigate at the same time both morphological and mechanical degradations of bacteria upon NPs treatment. Consequently, this study aims at quantifying the impact of the silica NPs (SiO 2 -NPs) on the mechanical properties of E. coli cells after their exposure, and relating it to their toxic activity under a critical diameter. Cell elasticity was calculated by fitting the force curves with the Hertz model, and was correlated with the morphological study. SiO 2 -NPs of 100 nm diameter did not trigger any significant change in the Young modulus of E. coli, in agreement with the bacterial intact morphology and membrane structure. On the opposite, the 4 nm diameter SiO 2 -NPs did induce a significant decrease in E. coli Young modulus, mainly associated with the disorganization of lipopolysaccharides in the outer membrane and the permeation of the underlying peptidoglycan layer. The subsequent toxic behavior of these NPs is finally confirmed by the presence of membrane residues, due to cell lysis, exhibiting typical adhesion features. Copyright © 2018 Elsevier Inc. All rights reserved.

Detonation re-initiation in a concentric tube arrangement for C_2H_2/O_2/Ar mixtures

NASA Astrophysics Data System (ADS)

Wu, Y.; Lee, J. H. S.; Weng, C.

2017-05-01

Re-initiation of detonation in a concentric tube arrangement where a detonation exiting from a small diameter inner tube to a large diameter outer tube has been investigated. The outer tube diameter D is 50.8 mm and inner tube diameters d are 38, 25.4, and 12.7 mm giving diameter ratios D/d=1.34, 2, and 4. Stoichiometric C_2H_2-O_2 mixtures with argon dilution of 0, 25, 50, and 70% are used in the present study. Velocity measurements are made using photodiodes, and smoked foils downstream of the exit of the inner tube are also used to record the re-initiation process. Upon exit from the inner tube, the detonation suffers an abrupt decrease in velocity and at critical conditions, the velocity downstream of the exit is of the order of 50% of the Chapman-Jouguet velocity. It is found that re-initiation generally occurs within 10 tube diameters downstream of the exit. If re-initiation is not successful, the detonation continues to propagate at a low velocity for distances of the order of 30 tube diameters without any indication of flame acceleration of deflagration-to-detonation transition (DDT). Thus, the re-initiation process is clearly defined and distinct from the usual DDT in a smooth tube. The critical d/λ value ratio in the concentric tube is significantly lower than the usual unconfined case of d/λ =13 where λ is the detonation cell size. Thus, it is a result of re-initiation at the Mach stem of the reflected shock from the wall of the outer concentric tube. If re-initiation is not successful upon the first reflection, then subsequent multiple reflections at the tube axis and wall of the outer tube can also result in re-initiation. However, this is only observed for undiluted mixtures. For high-argon-diluted mixtures, re-initiation only occurs at the Mach stem of the first reflection.

Growing Aligned Carbon Nanotubes for Interconnections in ICs

NASA Technical Reports Server (NTRS)

Li, Jun; Ye, Qi; Cassell, Alan; Ng, Hou Tee; Stevens, Ramsey; Han, Jie; Meyyappan, M.

2005-01-01

A process for growing multiwalled carbon nanotubes anchored at specified locations and aligned along specified directions has been invented. Typically, one would grow a number of the nanotubes oriented perpendicularly to a silicon integrated-circuit (IC) substrate, starting from (and anchored on) patterned catalytic spots on the substrate. Such arrays of perpendicular carbon nanotubes could be used as electrical interconnections between levels of multilevel ICs. The process (see Figure 1) begins with the formation of a layer, a few hundred nanometers thick, of a compatible electrically insulating material (e.g., SiO(x) or Si(y)N(z) on the silicon substrate. A patterned film of a suitable electrical conductor (Al, Mo, Cr, Ti, Ta, Pt, Ir, or doped Si), having a thickness between 1 nm and 2 m, is deposited on the insulating layer to form the IC conductor pattern. Next, a catalytic material (usually, Ni, Fe, or Co) is deposited to a thickness between 1 and 30 nm on the spots from which it is desired to grow carbon nanotubes. The carbon nanotubes are grown by plasma-enhanced chemical vapor deposition (PECVD). Unlike the matted and tangled carbon nanotubes grown by thermal CVD, the carbon nanotubes grown by PECVD are perpendicular and freestanding because an electric field perpendicular to the substrate is used in PECVD. Next, the free space between the carbon nanotubes is filled with SiO2 by means of CVD from tetraethylorthosilicate (TEOS), thereby forming an array of carbon nanotubes embedded in SiO2. Chemical mechanical polishing (CMP) is then performed to remove excess SiO2 and form a flat-top surface in which the outer ends of the carbon nanotubes are exposed. Optionally, depending on the application, metal lines to connect selected ends of carbon nanotubes may be deposited on the top surface. The top part of Figure 2 is a scanning electron micrograph (SEM) of carbon nanotubes grown, as described above, on catalytic spots of about 100 nm diameter patterned by electron-beam lithography. These and other nanotubes were found to have lengths ranging from 2 to 10 m and diameters ranging from 30 to 200 nm, the exact values of length depending on growth times and conditions and the exact values of diameter depending on the diameters and thicknesses of the catalyst spots. The bottom part of Figure 2 is an SEM of an embedded array of carbon nanotubes after CMP.

Dependence of light transmission through human skin on incident beam diameter at different wavelengths

NASA Astrophysics Data System (ADS)

Zhao, ZhongQuan; Fairchild, Paul W.

1998-05-01

For many skin treatments with light, it is important to have deep photon penetration into the skin. Because of absorption and scattering of photons by skin tissue, both the color and the diameter of the incident beam affect the penetration depth of photons. In this study, the dependence of light transmission through human skin tissues (ear lobs and between the fingers) has been measured in-vivo at six wavelengths (532 nm, 632 nm, 675 nm, 810 nm, 911 nm, and 1064 nm). The same measurement was also made on pig skin in-vitro for comparison. It was observed that (1) the photons at 1064 nm penetrate deeper than the other colors studied for a given incident beam diameter; and (2) the transmittance at a particular wavelength increases asymptotically with incident beam diameter. For some skin tissues, the transmittance flattens at about 8 mm for 532 nm photons and approaches saturation at about 12 mm for all other colors. The results on pig skin is similar.

Multi-scale Structural and Tensile Mechanical Response of Annulus Fibrosus to Osmotic Loading

PubMed Central

Han, Woojin M.; Nerurkar, Nandan L.; Smith, Lachlan J.; Jacobs, Nathan T.; Mauck, Robert L.; Elliott, Dawn M.

2012-01-01

This study investigates differential multi-scale structure and function relationships of the outer and inner annulus fibrosus (AF) to osmotic swelling in different buffer solutions by quantifying tensile mechanics, GAG content, water content and tissue swelling, and collagen fibril ultrastructure. In the outer AF, the tensile modulus decreased by over 70% with 0.15M PBS treatment but was unchanged with 2M PBS treatment. Moreover, the modulus loss following 0.15M PBS treatment was reversed when followed by 2M PBS treatment, potentially from increased interfibrillar and interlamellar shearing associated with fibril swelling. In contrast, the inner AF tensile modulus was unchanged by 0.15M PBS treatment and increased following 2M treatment. Transmission electron microscopy revealed that the mean collagen fibril diameters of the untreated outer and inner AF were 87.8 ± 27.9 and 71.0 ± 26.9 nm, respectively. In the outer AF, collagen fibril swelling was observed with both 0.15M and 2M PBS treatments, but inherently low GAG content remained unchanged. In the inner AF, 2M PBS treatment caused fibril swelling and GAG loss, suggesting that GAG plays a role in maintaining the structure of collagen fibrils leading to modulation of the native tissue mechanical properties. These results demonstrate important regional variations in structure and composition, and their influence on the heterogeneous mechanics of the AF. Moreover, because the composition and structure is altered as a consequence of progressive disc degeneration, quantification of these interactions is critical for study of the AF pathogenesis of degeneration and tissue engineering. PMID:22314837

Femtosecond-laser inscribed double-cladding waveguides in Nd:YAG crystal: a promising prototype for integrated lasers.

PubMed

Liu, Hongliang; Chen, Feng; Vázquez de Aldana, Javier R; Jaque, D

2013-09-01

We report on the design and implementation of a prototype of optical waveguides fabricated in Nd:YAG crystals by using femtosecond-laser irradiation. In this prototype, two concentric tubular structures with nearly circular cross sections of different diameters have been inscribed in the Nd:YAG crystals, generating double-cladding waveguides. Under 808 nm optical pumping, waveguide lasers have been realized in the double-cladding structures. Compared with single-cladding waveguides, the concentric tubular structures, benefiting from the large pump area of the outermost cladding, possess both superior laser performance and nearly single-mode beam profile in the inner cladding. Double-cladding waveguides of the same size were fabricated and coated by a thin optical film, and a maximum output power of 384 mW and a slope efficiency of 46.1% were obtained. Since the large diameters of the outer claddings are comparable with those of the optical fibers, this prototype paves a way to construct an integrated single-mode laser system with a direct fiber-waveguide configuration.

Integrated microfluidic flowmeter based on a micro-FBG inscribed in Co²⁺-doped optical fiber.

PubMed

Liu, Zhengyong; Tse, Ming-Leung Vincent; Zhang, A Ping; Tam, Hwa-Yaw

2014-10-15

A novel microfluidic flowmeter integrated with microfiber Bragg grating (µFBG) is presented. Two glass capillaries and a short length of high-light-absorption Co²⁺-doped optical fiber were stacked inside a larger outer capillary tube. The stack was then drawn into a tapered device. Two microchannels with the diameter of ~50  μm were formed inside the capillaries for flowing of microfluidics. An FBG was inscribed in the tapered Co²⁺-doped fiber with waist diameter of ~70  μm, and acts as a flow-rate sensor. A pump laser with wavelength of 1480 nm was utilized to locally heat the µFBG, rendering the µFBG as miniature "hot-wire" flowmeter. The flow rate of the liquid in the microchannels is determined by the induced wavelength shift of the µFBG. The experimental results achieve a minimum detectable change of ~16  nL/s in flow rate, which is very promising in the use as part of biochips.

Evaluation of Carburized and Ground Face Gears

NASA Technical Reports Server (NTRS)

Lewicki, David G.; Handschuh, Robert F.; Heath, Gregory F.; Sheth, Vijay

1999-01-01

Experimental durability tests were performed on carburized and ground AIS19310 steel face gears. The tests were in support of a Defense Advanced Research Projects Agency (DARPA) Technology Reinvestment Program (TRP) to enhance face-gear technology. The tests were conducted in the NASA Glenn spiral-bevel-gear/face-gear test facility. Tests were run at 2300 rpm face gear speed and at loads of 64, 76, 88, 100, and 112-percent of the design torque of 377 N-m (3340 in-lb). The carburized and ground face gears demonstrated the required durability when run for ten-million cycles at each of the applied loads. Proper installation was critical for the successful operation of the spur pinions and face gears. A large amount of backlash produced tooth contact patterns that approached the inner-diameter edge of the face-gear tooth. Low backlash produced tooth contact patterns that approached the outer-diameter edge of the face-gear tooth. Measured backlashes in the range of 0.178 to 0.254 mm (0.007 to 0.010 in) produced acceptable tooth contact patterns.

Antibiofilm surface functionalization of catheters by magnesium fluoride nanoparticles

PubMed Central

Lellouche, Jonathan; Friedman, Alexandra; Lahmi, Roxanne; Gedanken, Aharon; Banin, Ehud

2012-01-01

The ability of bacteria to colonize catheters is a major cause of infection. In the current study, catheters were surface-modified with MgF2 nanoparticles (NPs) using a sonochemical synthesis protocol described previously. The one-step synthesis and coating procedure yielded a homogenous MgF2 NP layer on both the inside and outside of the catheter, as analyzed by high resolution scanning electron microscopy and energy dispersive spectroscopy. The coating thickness varied from approximately 750 nm to 1000 nm on the inner walls and from approximately 450 nm to approximately 580 nm for the outer wall. The coating consisted of spherical MgF2 NPs with an average diameter of approximately 25 nm. These MgF2 NP-modified catheters were investigated for their ability to restrict bacterial biofilm formation. Two bacterial strains most commonly associated with catheter infections, Escherichia coli and Staphylococcus aureus, were cultured in tryptic soy broth, artificial urine and human plasma on the modified catheters. The MgF2 NP-coated catheters were able to significantly reduce bacterial colonization for a period of 1 week compared to the uncoated control. Finally, the potential cytotoxicity of MgF2 NPs was also evaluated using human and mammalian cell lines and no significant reduction in the mitochondrial metabolism was observed. Taken together, our results indicate that the surface modification of catheters with MgF2 NPs can be effective in preventing bacterial colonization and can provide catheters with long-lasting self-sterilizing properties. PMID:22419866

High speed intravascular photoacoustic imaging of atherosclerotic arteries (Conference Presentation)

NASA Astrophysics Data System (ADS)

Piao, Zhonglie; Ma, Teng; Qu, Yueqiao; Li, Jiawen; Yu, Mingyue; He, Youmin; Shung, K. Kirk; Zhou, Qifa; Kim, Chang-Seok; Chen, Zhongping

2016-02-01

Cardiovascular disease is the leading cause of death in the industrialized nations. Accurate quantification of both the morphology and composition of lipid-rich vulnerable atherosclerotic plaque are essential for early detection and optimal treatment in clinics. In previous works, intravascular photoacoustic (IVPA) imaging for detection of lipid-rich plaque within coronary artery walls has been demonstrated in ex vivo, but the imaging speed is still limited. In order to increase the imaging speed, a high repetition rate laser is needed. In this work, we present a high speed integrated IVPA/US imaging system with a 500 Hz optical parametric oscillator laser at 1725 nm. A miniature catheter with 1.0 mm outer diameter was designed with a 200 μm multimode fiber and an ultrasound transducer with 45 MHz center frequency. The fiber was polished at 38 degree and enclosed in a glass capillary for total internal reflection. An optical/electrical rotary junction and pull-back mechanism was applied for rotating and linearly scanning the catheter to obtain three-dimensional imaging. Atherosclerotic rabbit abdominal aorta was imaged as two frame/second at 1725 nm. Furthermore, by wide tuning range of the laser wavelength from 1680 nm to 1770 nm, spectroscopic photoacoustic analysis of lipid-mimicking phantom and an human atherosclerotic artery was performed ex vivo. The results demonstrated that the developed IVPA/US imaging system is capable for high speed intravascular imaging for plaque detection.

Controlling magnetic and electric dipole modes in hollow silicon nanocylinders.

PubMed

van de Haar, Marie Anne; van de Groep, Jorik; Brenny, Benjamin J M; Polman, Albert

2016-02-08

We propose a dielectric nanoresonator geometry consisting of hollow dielectric nanocylinders which support geometrical resonances. We fabricate such hollow Si particles with an outer diameter of 108-251 nm on a Si substrate, and determine their resonant modes with cathodo-luminescence (CL) spectroscopy and optical dark-field (DF) scattering measurements. The scattering behavior is numerically investigated in a systematic fashion as a function of wavelength and particle geometry. We find that the additional design parameter as a result of the introduction of a center gap can be used to control the relative spectral spacing of the resonant modes, which will enable additional control over the angular radiation pattern of the scatterers. Furthermore, the gap offers direct access to the enhanced magnetic dipole modal field in the center of the particle.

VNIR Multispectral Observations of Rocks at Spirit of St. Louis Crater and Marathon Valley on Th Rim of Endeavour Crater Made by the Opportunity Rover Pancam

NASA Technical Reports Server (NTRS)

Farrand, W. H.; Johnson, J. R.; Bell, J. F., III; Mittlefehldt, D.W.

2016-01-01

The Mars Exploration Rover Opportunity has been exploring the western rim of the 22 km diameter Endeavour crater since August, 2011. Recently, Opportunity has reached a break in the Endeavour rim that the rover team has named Mara-thon Valley. This is the site where orbital observations from the MRO CRISM imaging spectrometer indicated the presence of iron smectites. On the outer western portion of Marathon Valley, Opportunity explored the crater-form feature dubbed Spirit of St. Louis (SoSL) crater. This presentation describes the 430 to 1009 nm (VNIR) reflectance, measured by the rover's Pancam, of rock units present both at Spirit of St. Louis and within Marathon Valley.

Tunable Porosities and Shapes of Fullerene-Like Spheres

PubMed Central

Dielmann, Fabian; Fleischmann, Matthias; Heindl, Claudia; Peresypkina, Eugenia V; Virovets, Alexander V; Gschwind, Ruth M; Scheer, Manfred

2015-01-01

The formation of reversible switchable nanostructures monitored by solution and solid-state methods is still a challenge in supramolecular chemistry. By a comprehensive solid state and solution study we demonstrate the potential of the fivefold symmetrical building block of pentaphosphaferrocene in combination with CuI halides to switch between spheres of different porosity and shape. With increasing amount of CuX, the structures of the formed supramolecules change from incomplete to complete spherically shaped fullerene-like assemblies possessing an Ih-C80 topology at one side and to a tetrahedral-structured aggregate at the other. In the solid state, the formed nano-sized aggregates reach an outer diameter of 3.14 and 3.56 nm, respectively. This feature is used to reversibly encapsulate and release guest molecules in solution. PMID:25759976

Identification of endogenous fluorophores in the photoreceptors using autofluorescence spectroscopy

NASA Astrophysics Data System (ADS)

Zhao, Lingling; Qu, Junle; Niu, Hanben

2007-11-01

In this paper, we present our investigation on the identification of endogenous fluorophores in photoreceptors using autofluorescence spectroscopy, which is performed with an inverted laser scanning confocal microscope equipped with an Argon ion laser and a GreNe laser. In our experiments, individual cones and rods are clearly resolved even in freshly prepared retina samples, without slicing or labeling. The experiment results show that autofluorescence spectrum of the photoreceptors has three peaks approximately at 525nm, 585nm and 665nm. Furthermore, the brightest autofluorescence originates from the photoreceptor outer segments. We can, therefore, come to a conclusion that the peaks at 525nm, 585nm are corresponding to FAD and A2-PE, respectively, which are distributed in the photoreceptor outer segments.

Experimental tests of the effect of rotor diameter ratio and blade number to the cross-flow wind turbine performance

NASA Astrophysics Data System (ADS)

Susanto, Sandi; Tjahjana, Dominicus Danardono Dwi Prija; Santoso, Budi

2018-02-01

Cross-flow wind turbine is one of the alternative energy harvester for low wind speeds area. Several factors that influence the power coefficient of cross-flow wind turbine are the diameter ratio of blades and the number of blades. The aim of this study is to find out the influence of the number of blades and the diameter ratio on the performance of cross-flow wind turbine and to find out the best configuration between number of blades and diameter ratio of the turbine. The experimental test were conducted under several variation including diameter ratio between outer and inner diameter of the turbine and number of blades. The variation of turbine diameter ratio between inner and outer diameter consisted of 0.58, 0.63, 0.68 and 0.73 while the variations of the number of blades used was 16, 20 and 24. The experimental test were conducted under certain wind speed which are 3m/s until 4 m/s. The result showed that the configurations between 0.68 diameter ratio and 20 blade numbers is the best configurations that has power coefficient of 0.049 and moment coefficient of 0.185.

In Vivo Magnetic Stimulation of Rat Sciatic Nerve With Centimeter- and Millimeter-Scale Solenoid Coils.

PubMed

Kagan, Zachary B; RamRakhyani, Anil Kumar; Lazzi, Gianluca; Normann, Richard A; Warren, David J

2016-11-01

Previous reports of magnetic stimulation of the peripheral nervous system (PNS) used various coil geometries, all with outer diameters larger than 35 mm, and stimulation energies in the 50 J range to evoke neural excitation. Recent reports of central nervous system (CNS) activation used sub-mm-scale solenoid coils with mJ energy levels. The goal of this study was to translate the lower energy levels from the CNS to the PNS via using smaller coils placed in closer proximity to the neural tissue. Such a performance improvement would advance the state of the art of magnetic stimulation and provide a path towards new neuroprosthetic devices. Primarily, we investigated the range of coil outer diameters from 25 mm down to 5 mm to better understand the dependence of coil diameter on energy required for PNS activation. Nine cm- and mm-scale copper solenoid coils, with various resistances, inductances, inner and outer diameters, and heights were compared by quantizing neuromuscular responses to magnetic stimulation via capacitive discharge excitation of rat sciatic nerves in vivo. Additionally, the effects of stimulus duration and coil position were investigated. As opposed to prior work, this study compares a subset of stimulation parameters in an intact nerve preparation, and shows that magnetic stimulation with coils that abut the nerve is a reliable, effective method of neuromuscular stimulation. Although we observed different energies required for neuromuscular activation depending on the coil and excitation parameters used, for the experimental configuration, devices, and stimulus waveform shapes presented in this manuscript, no systematic dependence of PNS activation on coil diameter was found, even for the mm-scale coils investigated herein. However, there was a clear relationship between discharge circuit capacitance and energy required to evoke a neuromuscular response. Coils approximately 12 mm in outer diameter and larger consistently evoked responses, whereas coils 5 mm in outer diameter did not. Furthermore, we observed meaningful neuromuscular excitation when stimulating with energies as low as 20 J. Although this is an improvement over prior work, it is still orders of magnitude greater than the energy required for conventional electrical stimulation, suggesting that these devices are presently not suitable for use in an application requiring continued pulsed stimulation. Nevertheless, these devices are suitable for basic research and as clinical tools that infrequently stimulate, such as in diagnostic applications.

Influence of depressed-index outer ring on evanescent tunneling loss in tapered double-cladding fibers.

PubMed

Chen, Nan-Kuang; Hsu, Kuei-Chu; Liaw, Shien-Kuei; Lai, Yinchieh; Chi, Sien

2008-08-01

A tapered fiber with a depressed-index outer ring is fabricated and dispersion engineered to generate a widely tunable (1250-1650 nm) fundamental-mode leakage loss with a high cutoff slope (-1.2 dB/nm) and a high attenuation for stop band (>50 dB) by modification of both waveguide and material dispersions. The higher cutoff slope is achieved with a larger cross angle between the two refractive index dispersion curves of the tapered fiber and surrounding optical liquids through the use of depressed-index outer ring structures in double-cladding fibers.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Lamoureux, R; Sinclair, L; Mench, A

Purpose: To introduce and investigate effective diameter ratios as a new patient metric for use in computed tomography protocol selection as a supplement to patient-specific size parameter data. Methods: The metrics of outer effective diameter and inner effective diameter were measured for 7 post-mortem subjects scanned with a standardized chest/abdomen/pelvis (CAP) protocol on a 320-slice MDCT scanner. The outer effective diameter was calculated by obtaining the anterior/posterior and lateral dimensions of the imaged anatomy at the middle of the scan range using Effective Diameter= SQRT(AP height*Lat Width). The inner effective diameter was calculated with the same equation using the APmore » and Lat dimensions of the anatomy excluding the adipose tissue. The ratio of outer to inner effective diameter was calculated for each subject. A relationship to BMI, weight, and CTDI conversion coefficients was investigated. Results: For the largest subject with BMI of 43.85 kg/m2 and weight of 255 lbs the diameter ratio was calculated as 1.33. For the second largest subject with BMI of 33.5 kg/m2 and weight of 192.4 lbs the diameter ratio was measured as 1.43, indicating a larger percentage of adipose tissue in the second largest subject’s anatomical composition. For the smallest subject at BMI of 17.4 kg/m2 and weight of 86 lbs a similar tissue composition was indicated as a subject with BMI of 24.2 kg/m2 and weight of 136 lbs as they had the same diameter ratios of 1.11. Conclusion: The diameter ratio proves to contain information about anatomical composition that the BMI and weight alone do not. The utility of this metric is still being examined but could prove useful for determining MDCT techniques and for giving a more in depth detail of the composition of a patient’s body habitus.« less

Breakdown of Shape Memory Effect in Bent Cu-Al-Ni Nanopillars: When Twin Boundaries Become Stacking Faults.

PubMed

Liu, Lifeng; Ding, Xiangdong; Sun, Jun; Li, Suzhi; Salje, Ekhard K H

2016-01-13

Bent Cu-Al-Ni nanopillars (diameters 90-750 nm) show a shape memory effect, SME, for diameters D > 300 nm. The SME and the associated twinning are located in a small deformed section of the nanopillar. Thick nanopillars (D > 300 nm) transform to austenite under heating, including the deformed region. Thin nanopillars (D < 130 nm) do not twin but generate highly disordered sequences of stacking faults in the deformed region. No SME occurs and heating converts only the undeformed regions into austenite. The defect-rich, deformed region remains in the martensite phase even after prolonged heating in the stability field of austenite. A complex mixture of twins and stacking faults was found for diameters 130 nm < D < 300 nm. The size effect of the SME in Cu-Al-Ni nanopillars consists of an approximately linear reduction of the SME between 300 and 130 nm when the SME completely vanishes for smaller diameters.

Niobium oxide nanocolumns formed via anodic alumina with modulated pore diameters

NASA Astrophysics Data System (ADS)

Pligovka, A.; Zakhlebayeva, A.; Lazavenka, A.

2018-03-01

Niobium oxide nanocolumns with modulated diameters were formed for the first time. An Al/Nb bilayer specimen was prepared by successive sputter-deposition of 300 nm niobium layer and 1200 nm aluminum layer onto silicon wafer. Regular anodic alumina matrix with modulated pore diameters was formed by sequential anodization of initial specimen in tartaric acid at 180 V, and in oxalic acid at 37 V. Further potentiodynamic reanodization of the specimen up to 400 V causes the simultaneous growth of 440 nm continuous niobium oxide layer beneath the alumina film and two types of an array of oxide nanocolumns (thick – with 100 nm width and 630 nm high and thin – with 25 nm width and 170 nm high), which are the filling of the alumina pores. The morphology of the formed anodic niobium oxide nanocolumns with modulated diameters was determined by field emission scanning electron microscopy. The formed nanostructures can be used for perspective devices of nano- and optoelectronics such as photonic crystals.

Preparation of novel stable antibacterial nanoparticles using hydroxyethylcellulose and application in paper.

PubMed

Wei, Dafu; Chen, Yan; Zhang, Youwei

2016-01-20

Taking advantage of the self-assembly between the components, novel stable antibacterial nanoparticles were efficiently fabricated via a facile one-step co-polymerization of acrylic acid (AA) and N,N'-methylenebisacrylamide (MBA) on a mixed aqueous solution of poly(hexamethylene guanidine hydrochloride) (PHMG) and hydroxyethylcellulose (HEC). The z-average hydrodynamic diameters of the nanoparticles ranged from 220 nm to 450 nm. The inner layer of the nanoparticles is composed of water-insoluble interpolymer complexes of PHMG and PAA networks, while the outer layer is composed of PHMG and HEC. The nanoparticles are stabilized by electrostatic interactions, hydrogen bonding interactions, and the chemical bonds. The nanoparticle solution remained stable in a wide pH range of 2.0-12.0 and at salt concentrations below 0.25 mol/L. The nanoparticles were incorporated into handsheets using a dipping treatment. The resulted handsheets exhibited excellent antimicrobial activities even after multiple water washing treatments. The nanoparticles are promising in fabricating paper, water-based coatings and textiles with permanent antibacterial activity. Copyright © 2015 Elsevier Ltd. All rights reserved.

A facile construction strategy of stable lipid nanoparticles for drug delivery using a hydrogel-thickened microemulsion system

NASA Astrophysics Data System (ADS)

Chen, Huabing; Xiao, Ling; Du, Danrong; Mou, Dongsheng; Xu, Huibi; Yang, Xiangliang

2010-01-01

We report a novel facile method for preparing stable nanoparticles with inner spherical solid spheres and an outer hydrogel matrix using a hot O/W hydrogel-thickened microemulsion with spontaneous stability. The nanoparticles with average diameters of about 30.0 nm and 100.0 nm were constructed by cooling the hot hydrogel-thickened microemulsion at different temperatures, respectively. We explained the application of these nanoparticles by actualizing the cutaneous delivery of drug-loaded nanoparticles. The in vitro skin permeation studies showed that the nanoparticles could significantly reduce the penetration of model drugs through skin and resulted in their dermal uptakes in skin. The sol-gel process of TEOS was furthermore used in the template of HTM to regulate the particle size of nanoparticles. The coating of silica on the surface of nanoparticles could regulate the penetration of drug into skin from dermal delivery to transdermal delivery. This strategy provides a facile method to produce nanoparticles with long-term stability and ease of manufacture, which might have a promising application in drug delivery.

Comparison of epidermal/dermal damage between the long-pulsed 1064 nm Nd:YAG and 755 nm alexandrite lasers under relatively high fluence conditions: quantitative and histological assessments.

PubMed

Lee, Ju Hwan; Park, So Ra; Jo, Jeong Ho; Park, Sung Yun; Seo, Young Kwon; Kim, Sung Min

2014-07-01

The purpose of this study was to compare degrees of epidermal/dermal tissue damage quantitatively and histologically after laser irradiation, to find ideal treatment conditions with relatively high fluence for skin rejuvenation. A number of recent studies have evaluated the clinical efficacy and safety of therapeutic lasers under relatively low fluence conditions. We transmitted the long-pulsed 1064 nm Nd:YAG and 755 nm Alexandrite lasers into pig skin according to different fluences and spot diameters, and estimated epidermal/dermal temperatures. Pig skin specimens were stained with hematoxylin and eosin for histological assessments. The fluence conditions comprised 26, 30, and 36 J/cm2, and the spot diameter conditions were 5, 8, and 10 mm. Pulse duration was 30 ms for all experiments. Both lasers produced reliable thermal damage on the dermis without any serious epidermal injuries, under relatively high fluence conditions. The 1064 nm laser provided more active fibrous formations than the 755 nm laser, while higher risks for tissue damages simultaneously occurred. The ideal treatment conditions for skin rejuvenation were 8 mm diameter with 30 J/cm2 and 10 mm diameter with 26 J/cm2 for the 1064 nm laser, and 8 mm diameter with 36 J/cm2 and 10 mm diameter with 26 J/cm2 for the 755 nm laser.

Interaction of the Full-length Bax Protein with Biomimetic Mitochondrial Liposomes: A Small-Angle Neutron Scattering and Fluorescence Study

DOE Office of Scientific and Technical Information (OSTI.GOV)

Satsoura, D; Kucerka, Norbert; Shivakumar, S

2012-01-01

In response to apoptotic stimuli, the pro-apoptotic protein Bax inserts in the outer mitochondrial membrane, resulting in the formation of pores and the release of several mitochondrial components, and sealing the cell's fate. To study the binding of Bax to membranes, we used an in vitro system consisting of 50 nm diameter liposomes prepared with a lipid composition mimicking that of mitochondrial membranes in which recombinant purified full-length Bax was inserted via activation with purified tBid. We detected the association of the protein with the membrane using fluorescence fluctuation methods, and found that it could well be described by anmore » equilibrium between soluble and membrane-bound Bax and that at a high protein-toliposome ratio the binding seemed to saturate at about 15 Bax proteins per 50 nm diameter liposome. We then obtained structural data for samples in this saturated binding regime using small-angle neutron scattering under different contrast matching conditions. Utilizing a simple model to fit the neutron data, we observed that a significant amount of the protein mass protrudes above the membrane, in contrast to the conjecture that all of the membrane-associated Bax states are umbrella-like. Upon protein binding, we also observed a thinning of the lipid bilayer accompanied by an increase in liposome radius, an effect reminiscent of the action of antimicrobial peptides on membranes.« less

A hybrid chip based on aerodynamics and electrostatics for the size-dependent classification of ultrafine and nano particles.

PubMed

Kim, Yong-Ho; Park, Dongho; Hwang, Jungho; Kim, Yong-Jun

2009-09-21

Conventional virtual impactors experience a large pressure drop when they classify particles according to size, in particular ultrafine particles smaller than 100 nm in diameter. Therefore, most virtual impactors have been used to classify particles larger than 100 nm. Their cut-off diameters are also fixed by the geometry of their flow channels. In the proposed virtual impactor, particles smaller than 100 nm are accelerated by applying DC potentials to an integrated electrode pair. By the electrical acceleration, the large pressure drop could be significantly decreased and new cut-off diameters smaller than 100 nm could be successfully added. The geometric cut-off diameter (GCD) of the proposed virtual impactor was designed to be 1.0 microm. Performances including the GCD and wall loss were examined by classifying dioctyl sebacate of 100 to 600 nm in size and carbon particles of 0.6 to 10 microm in size. The GCD was measured to be 0.95 microm, and the wall loss was highest at 1.1 microm. To add new cut-off diameters, monodisperse NaCl particles ranging from 15 to 70 nm were classified using the proposed virtual impactor with applying a DC potential of 0.25 to 3.0 kV. In this range of the potential, the new cut-off diameters ranging from 15 to 35 nm was added.

Material with core-shell structure

DOEpatents

Luhrs, Claudia [Rio Rancho, NM; Richard, Monique N [Ann Arbor, MI; Dehne, Aaron [Maumee, OH; Phillips, Jonathan [Rio Rancho, NM; Stamm, Kimber L [Ann Arbor, MI; Fanson, Paul T [Brighton, MI

2011-11-15

Disclosed is a material having a composite particle, the composite particle including an outer shell and a core. The core is made from a lithium alloying material and the outer shell has an inner volume that is greater in size than the core of the lithium alloying material. In some instances, the outer mean diameter of the outer shell is less than 500 nanometers and the core occupies between 5 and 99% of the inner volume. In addition, the outer shell can have an average wall thickness of less than 100 nanometers.

Performance of an adjustable, threaded inertance tube

NASA Astrophysics Data System (ADS)

Zhou, W. J.; Pfotenhauer, J. M.; Nellis, G. F.; Liu, S. Y.

2015-12-01

The performance of the Stirling type pulse tube cryocooler depends strongly on the design of the inertance tube. The phase angle produced by the inertance tube is very sensitive to its diameter and length. Recent developments are reported here regarding an adjustable inertance device that can be adjusted in real time. The inertance passage is formed by the root of a concentric cylindrical threaded device. The depth of the threads installed on the outer screw varies. In this device, the outer screw can be rotated four and half turns. At the zero turn position the length of the passage is 1.74 m and the hydraulic diameter is 7 mm. By rotating the outer screw, the inner threaded rod engages with additional, larger depth threads. Therefore, at its upper limit of rotation, the inertance passage includes both the original 1.74 m length with 7mm hydraulic diameter plus an additional 1.86 m length with a 10 mm hydraulic diameter. A phase shift change of 24° has been experimentally measured by changing the position of outer screw while operating the device at a frequency of 60 Hz. This phase angle shift is less than the theoretically predicted value due to the presence of a relatively large leak through the thread clearance. Therefore, the distributed component model of the inertance tube was modified to account for the leak path causing the data to agree with the model. Further, the application of vacuum grease to the threads causes the performance of the device to improve substantially.

Excellent Field Emission Properties of Short Conical Carbon Nanotubes Prepared by Microwave Plasma Enhanced CVD Process

PubMed Central

2008-01-01

Randomly oriented short and low density conical carbon nanotubes (CNTs) were prepared on Si substrates by tubular microwave plasma enhanced chemical vapor deposition process at relatively low temperature (350–550 °C) by judiciously controlling the microwave power and growth time in C2H2 + NH3gas composition and Fe catalyst. Both length as well as density of the CNTs increased with increasing microwave power. CNTs consisted of regular conical compartments stacked in such a way that their outer diameter remained constant. Majority of the nanotubes had a sharp conical tip (5–20 nm) while its other side was either open or had a cone/pear-shaped catalyst particle. The CNTs were highly crystalline and had many open edges on the outer surface, particularly near the joints of the two compartments. These films showed excellent field emission characteristics. The best emission was observed for a medium density film with the lowest turn-on and threshold fields of 1.0 and 2.10 V/μm, respectively. It is suggested that not only CNT tip but open edges on the body also act as active emission sites in the randomly oriented geometry of such periodic structures.

Herpes simplex virus glycoproteins gB and gH function in fusion between the virion envelope and the outer nuclear membrane.

PubMed

Farnsworth, Aaron; Wisner, Todd W; Webb, Michael; Roller, Richard; Cohen, Gary; Eisenberg, Roselyn; Johnson, David C

2007-06-12

Herpesviruses must traverse the nuclear envelope to gain access to the cytoplasm and, ultimately, to exit cells. It is believed that herpesvirus nucleocapsids enter the perinuclear space by budding through the inner nuclear membrane (NM). To reach the cytoplasm these enveloped particles must fuse with the outer NM and the unenveloped capsids then acquire a second envelope in the trans-Golgi network. Little is known about the process by which herpesviruses virions fuse with the outer NM. Here we show that a herpes simplex virus (HSV) mutant lacking both the two putative fusion glycoproteins gB and gH failed to cross the nuclear envelope. Enveloped virions accumulated in the perinuclear space or in membrane vesicles that bulged into the nucleoplasm (herniations). By contrast, mutants lacking just gB or gH showed only minor or no defects in nuclear egress. We concluded that either HSV gB or gH can promote fusion between the virion envelope and the outer NM. It is noteworthy that fusion associated with HSV entry requires the cooperative action of both gB and gH, suggesting that the two types of fusion (egress versus entry) are dissimilar processes.

Dependence of Capillary Properties of Contemporary Clinker Bricks on Their Microstructure

NASA Astrophysics Data System (ADS)

Wesołowska, Maria; Kaczmarek, Anna

2017-10-01

Contemporary clinker bricks are applied for outer layers of walls built from other materials and walls which should have high durability and aesthetic qualities. The intended effect depends not only on the mortar applied but also on clinker properties. Traditional macroscopic tests do not allow to predict clinker behaviour in contact with mortars and external environment. The basic information for this issue is open porosity of material. It defines the material ability to absorb liquids: rain water (through the face wall surface) and grout from mortar (through base surface). The main capillary flow goes on in pores with diameters from 300 to 3000nm. It is possible to define pore distribution and their size using the Mercury Intrusion Porosimetry method. The aim of these research is evaluation of clinker brick capillary properties (initial water absorption and capillary rate) and analysis of differences in microstructure of the face and base wall of a product. Detailed results allowed to show pore distribution in function of their diameters and definition of pore amount responsible for capillary flow. Based on relation between volume function differential and pore diameter, a differential distribution curve was obtained which helped to determine the dominant diameters. The results obtained let us state that face wall of bricks was characterized with the lowest material density and open porosity. In this layer (most burnt) part of pores could be closed by locally appearing liquid phase during brick burning. Thus density is lower comparing to other part of the product.

Lunar impact basins revealed by Gravity Recovery and Interior Laboratory measurements

PubMed Central

Neumann, Gregory A.; Zuber, Maria T.; Wieczorek, Mark A.; Head, James W.; Baker, David M. H.; Solomon, Sean C.; Smith, David E.; Lemoine, Frank G.; Mazarico, Erwan; Sabaka, Terence J.; Goossens, Sander J.; Melosh, H. Jay; Phillips, Roger J.; Asmar, Sami W.; Konopliv, Alexander S.; Williams, James G.; Sori, Michael M.; Soderblom, Jason M.; Miljković, Katarina; Andrews-Hanna, Jeffrey C.; Nimmo, Francis; Kiefer, Walter S.

2015-01-01

Observations from the Gravity Recovery and Interior Laboratory (GRAIL) mission indicate a marked change in the gravitational signature of lunar impact structures at the morphological transition, with increasing diameter, from complex craters to peak-ring basins. At crater diameters larger than ~200 km, a central positive Bouguer anomaly is seen within the innermost peak ring, and an annular negative Bouguer anomaly extends outward from this ring to the outer topographic rim crest. These observations demonstrate that basin-forming impacts remove crustal materials from within the peak ring and thicken the crust between the peak ring and the outer rim crest. A correlation between the diameter of the central Bouguer gravity high and the outer topographic ring diameter for well-preserved basins enables the identification and characterization of basins for which topographic signatures have been obscured by superposed cratering and volcanism. The GRAIL inventory of lunar basins improves upon earlier lists that differed in their totals by more than a factor of 2. The size-frequency distributions of basins on the nearside and farside hemispheres of the Moon differ substantially; the nearside hosts more basins larger than 350 km in diameter, whereas the farside has more smaller basins. Hemispherical differences in target properties, including temperature and porosity, are likely to have contributed to these different distributions. Better understanding of the factors that control basin size will help to constrain models of the original impactor population. PMID:26601317

Lunar impact basins revealed by Gravity Recovery and Interior Laboratory measurements.

PubMed

Neumann, Gregory A; Zuber, Maria T; Wieczorek, Mark A; Head, James W; Baker, David M H; Solomon, Sean C; Smith, David E; Lemoine, Frank G; Mazarico, Erwan; Sabaka, Terence J; Goossens, Sander J; Melosh, H Jay; Phillips, Roger J; Asmar, Sami W; Konopliv, Alexander S; Williams, James G; Sori, Michael M; Soderblom, Jason M; Miljković, Katarina; Andrews-Hanna, Jeffrey C; Nimmo, Francis; Kiefer, Walter S

2015-10-01

Observations from the Gravity Recovery and Interior Laboratory (GRAIL) mission indicate a marked change in the gravitational signature of lunar impact structures at the morphological transition, with increasing diameter, from complex craters to peak-ring basins. At crater diameters larger than ~200 km, a central positive Bouguer anomaly is seen within the innermost peak ring, and an annular negative Bouguer anomaly extends outward from this ring to the outer topographic rim crest. These observations demonstrate that basin-forming impacts remove crustal materials from within the peak ring and thicken the crust between the peak ring and the outer rim crest. A correlation between the diameter of the central Bouguer gravity high and the outer topographic ring diameter for well-preserved basins enables the identification and characterization of basins for which topographic signatures have been obscured by superposed cratering and volcanism. The GRAIL inventory of lunar basins improves upon earlier lists that differed in their totals by more than a factor of 2. The size-frequency distributions of basins on the nearside and farside hemispheres of the Moon differ substantially; the nearside hosts more basins larger than 350 km in diameter, whereas the farside has more smaller basins. Hemispherical differences in target properties, including temperature and porosity, are likely to have contributed to these different distributions. Better understanding of the factors that control basin size will help to constrain models of the original impactor population.

Comparison of Epidermal/Dermal Damage Between the Long-Pulsed 1064 nm Nd:YAG and 755 nm Alexandrite Lasers Under Relatively High Fluence Conditions: Quantitative and Histological Assessments

PubMed Central

Lee, Ju Hwan; Park, So Ra; Jo, Jeong Ho; Park, Sung Yun; Seo, Young Kwon

2014-01-01

Abstract Objective: The purpose of this study was to compare degrees of epidermal/dermal tissue damage quantitatively and histologically after laser irradiation, to find ideal treatment conditions with relatively high fluence for skin rejuvenation. Background data: A number of recent studies have evaluated the clinical efficacy and safety of therapeutic lasers under relatively low fluence conditions. Methods: We transmitted the long-pulsed 1064 nm Nd:YAG and 755 nm Alexandrite lasers into pig skin according to different fluences and spot diameters, and estimated epidermal/dermal temperatures. Pig skin specimens were stained with hematoxylin and eosin for histological assessments. The fluence conditions comprised 26, 30, and 36 J/cm2, and the spot diameter conditions were 5, 8, and 10 mm. Pulse duration was 30 ms for all experiments. Results: Both lasers produced reliable thermal damage on the dermis without any serious epidermal injuries, under relatively high fluence conditions. The 1064 nm laser provided more active fibrous formations than the 755 nm laser, while higher risks for tissue damages simultaneously occurred. Conclusions: The ideal treatment conditions for skin rejuvenation were 8 mm diameter with 30 J/cm2 and 10 mm diameter with 26 J/cm2 for the 1064 nm laser, and 8 mm diameter with 36 J/cm2 and 10 mm diameter with 26 J/cm2 for the 755 nm laser. PMID:24992273

DOE Office of Scientific and Technical Information (OSTI.GOV)

Raghuwanshi, Vikram Singh; Garusinghe, Uthpala Manavi; Ilavsky, Jan

Controlling nanoparticles (NPs) aggregation in cellulose/NPs composites allows to optimise NPs driven properties and their applications. Polyelectrolytes are used to control NPs aggregation and their retention within the fibrous matrix. Here in this study, we aim at evaluating how a polyelectrolyte (Cationic Polyacrylamide; CPAM, molecular weight: 13 MDa, charge: 50%, Radius of gyration: 30–36 nm) adsorbs and re-conforms onto the surface of silica(SiO 2) NPs differing in diameter (8, 22 and 74 nm) and to investigate the respective NPs aggregation in cellulose matrices. SEM shows the local area distribution of NPs in composites. Ultra-SAXS (USAXS) allows to evaluate the averagemore » NPs size distribution and the inter-particle interactions at length scale ranging from 1 to 1000 nm. USAXS data analysis reveals that CPAM covers multiple NPs of the smaller diameter (8 nm), presumably with a single chain to form large size NPs aggregates. As the NPs diameter is increased to 22 nm, CPAM re-conforms over NP surface forming a large shell of thickness 5.5 nm. For the composites with NPs of diameter 74 nm, the CPAM chain re-conforms further onto NP surface and the surrounding shell thickness decreases to 2.2 nm. Lastly, structure factor analysis reveals higher structural ordering for NPs as increases their diameter, which is caused by different conformations adopted by CPAM onto NPs surface.« less

Effect of nanoparticles size and polyelectrolyte on nanoparticles aggregation in a cellulose fibrous matrix

DOE PAGES

Raghuwanshi, Vikram Singh; Garusinghe, Uthpala Manavi; Ilavsky, Jan; ...

2017-09-18

Controlling nanoparticles (NPs) aggregation in cellulose/NPs composites allows to optimise NPs driven properties and their applications. Polyelectrolytes are used to control NPs aggregation and their retention within the fibrous matrix. Here in this study, we aim at evaluating how a polyelectrolyte (Cationic Polyacrylamide; CPAM, molecular weight: 13 MDa, charge: 50%, Radius of gyration: 30–36 nm) adsorbs and re-conforms onto the surface of silica(SiO 2) NPs differing in diameter (8, 22 and 74 nm) and to investigate the respective NPs aggregation in cellulose matrices. SEM shows the local area distribution of NPs in composites. Ultra-SAXS (USAXS) allows to evaluate the averagemore » NPs size distribution and the inter-particle interactions at length scale ranging from 1 to 1000 nm. USAXS data analysis reveals that CPAM covers multiple NPs of the smaller diameter (8 nm), presumably with a single chain to form large size NPs aggregates. As the NPs diameter is increased to 22 nm, CPAM re-conforms over NP surface forming a large shell of thickness 5.5 nm. For the composites with NPs of diameter 74 nm, the CPAM chain re-conforms further onto NP surface and the surrounding shell thickness decreases to 2.2 nm. Lastly, structure factor analysis reveals higher structural ordering for NPs as increases their diameter, which is caused by different conformations adopted by CPAM onto NPs surface.« less

Effect of aging on the microstructure, hardness and chemical composition of dentin.

PubMed

Montoya, C; Arango-Santander, S; Peláez-Vargas, A; Arola, D; Ossa, E A

2015-12-01

Understanding the effects of biological aging on human tissues has been a topic of extensive research. With the increase in healthy seniors and quality of life that topic is becoming increasingly important. In this investigation the effects of aging on the microstructure, chemical composition and hardness of human coronal dentin was studied from a comparison of teeth within "young" and "old" age groups. The microstructure of dentin within three regions (i.e., inner, middle and outer) was analyzed using electron and optical microscopy. The mineral-to-collagen ratio in these three regions was estimated using Raman spectroscopy and the hardness was evaluated using microindentation. Results showed that there were significant differences in tubule density, tubule diameter and peritubular cuff diameter with depth. Although there was no difference in tubule density and diameter of the tubules between the age groups, there was a significant difference in the occlusion ratio. A significant increase in hardness between young and old patients was found for middle and outer dentin. An increase in mineral-to-collagen ratio from inner to outer dentin was also found for both groups. In old patients, an increase in mineral content was found in outer coronal dentin as a consequence of tubule occlusion. An increase in occlusion ratio, hardness, and mineral content was found in the dentin of adult patients with age. This increase is most evident in the outer coronal dentin. Copyright © 2015 Elsevier Ltd. All rights reserved.

Pipe support for use in a nuclear system

DOEpatents

Pollono, Louis P.; Mello, Raymond M.

1977-01-01

A pipe support for high temperature, thin-walled vertical piping runs used in a nuclear system. A cylindrical pipe transition member, having the same inside diameter as the thin-walled piping, replaces a portion of the piping where support is desired. The outside diameter of the pipe transition member varies axially along its vertical dimension. For a section of the axial length adjacent the upper and lower terminations of the pipe transition member, the outside diameter is the same as the outside diameter of the thin-walled piping to which it is affixed. Intermediate of the termination sections, the outside diameter increases from the top of the member to the bottom. Adjacent the lower termination section, the diameter abruptly becomes the same as the piping. Thus, the cylindrical transition member is formed to have a generally triangular shaped cross-section along the axial dimension. Load-bearing insulation is installed next to the periphery of the member and is kept in place by an outer ring clamp. The outer ring clamp is connected to pipe hangers, which provide the desired support for the vertical thin-walled piping runs.

Synthesis of brushite particles in reverse microemulsions of the biosurfactant surfactin.

PubMed

Maity, Jyoti Prakash; Lin, Tz-Jiun; Cheng, Henry Pai-Heng; Chen, Chien-Yen; Reddy, A Satyanarayana; Atla, Shashi B; Chang, Young-Fo; Chen, Hau-Ren; Chen, Chien-Cheng

2011-01-01

In this study the "green chemistry" use of the biosurfactant surfactin for the synthesis of calcium phosphate using the reverse microemulsion technique was demonstrated. Calcium phosphates are bioactive materials that are a major constituent of human teeth and bone tissue. A reverse microemulsion technique with surfactin was used to produce nanocrystalline brushite particles. Structural diversity (analyzed by SEM and TEM) resulted from different water to surfactin ratios (W/S; 250, 500, 1000 and 40,000). The particle sizes were found to be in the 16-200 nm range. Morphological variety was observed in the as-synthesized microemulsions, which consisted of nanospheres (~16 nm in diameter) and needle-like (8-14 nm in diameter and 80-100 nm in length) noncalcinated particles. However, the calcinated products included nanospheres (50-200 nm in diameter), oval (~300 nm in diameter) and nanorod (200-400 nm in length) particles. FTIR and XRD analysis confirmed the formation of brushite nanoparticles in the as-synthesized products, while calcium pyrophosphate was produced after calcination. These results indicate that the reverse microemulsion technique using surfactin is a green process suitable for the synthesis of nanoparticles.

Influence of the impact energy on the pattern of blood drip stains

NASA Astrophysics Data System (ADS)

Smith, F. R.; Nicloux, C.; Brutin, D.

2018-01-01

The maximum spreading diameter of complex fluid droplets has been extensively studied and explained by numerous physical models. This research focuses therefore on a different aspect, the bulging outer rim observed after evaporation on the final dried pattern of blood droplets. A correlation is found between the inner diameter, the maximum outer diameter, and the impact speed. This shows how the drying mechanism of a blood drip stain is influenced by the impact energy, which induces a larger spreading diameter and thus a different redistribution of red blood cells inside the droplet. An empirical relation is established between the final dried pattern of a passive bloodstain and its impact speed, yielding a possible forensic application. Indeed, being able to relate accurately the energy of the drop with its final pattern would give a clue to investigators, as currently no such simple and accurate tool exists.

Fabrication of 10nm diameter carbon nanopores

DOE Office of Scientific and Technical Information (OSTI.GOV)

Radenovic, Aleksandra; Trepagnier, Eliane; Csencsits, Roseann

2008-09-25

The addition of carbon to samples, during imaging, presents a barrier to accurate TEM analysis, the controlled deposition of hydrocarbons by a focused electron beam can be a useful technique for local nanometer-scale sculpting of material. Here we use hydrocarbon deposition to form nanopores from larger focused ion beam (FIB) holes in silicon nitride membranes. Using this method, we close 100-200nm diameter holes to diameters of 10nm and below, with deposition rates of 0.6nm per minute. I-V characteristics of electrolytic flow through these nanopores agree quantitatively with a one dimensional model at all examined salt concentrations.

Method for hot press forming articles

DOEpatents

Baker, Robert R.; Hartsock, Dale L.

1982-01-01

This disclosure relates to an improved method for achieving the best bond strength and for minimizing distortion and cracking of hot pressed articles. In particular, in a method for hot press forming both an outer facing circumferential surface of and an inner portion of a hub, and of bonding that so-formed outer facing circumferential surface to an inner facing circumferential surface of a pre-formed ring thereby to form an article, the following improvement is made. Normally, in this method, the outside ring is restrained by a restraining sleeve of ring-shaped cross-section having an inside diameter. A die member, used to hot press form the hub, is so-formed as to have an outside diameter sized to engage the inside diameter of the restraining sleeve in a manner permitting relative movement therebetween. The improved method is one in which several pairs of matched restraining sleeve and die member are formed with each matched pair having a predetermined diameter. The predetermined diameter of each matched pair is different from another matched pair by stepped increments. The largest inside diameter of a restraining sleeve is equal to the diameter of the outer facing circumferential surface of the hub. Each pair of the matched restraining sleeve and die member is used to form an article in which an inside hub is bonded to an outside ring. The several samples so-formed are evaluated to determine which sample has the best bond formed between the hub and the ring with the least or no cracking or distortion in the ring portion of the article. Thereafter, the matched restraining sleeve and die member which form the article having the best bonding characteristics and least distortion cracking is then used for repeated formations of articles.

Control of optical bandgap energy and optical absorption coefficient by geometric parameters in sub-10 nm silicon-nanodisc array structure

NASA Astrophysics Data System (ADS)

Fairuz Budiman, Mohd; Hu, Weiguo; Igarashi, Makoto; Tsukamoto, Rikako; Isoda, Taiga; Itoh, Kohei M.; Yamashita, Ichiro; Murayama, Akihiro; Okada, Yoshitaka; Samukawa, Seiji

2012-02-01

A sub-10 nm, high-density, periodic silicon-nanodisc (Si-ND) array has been fabricated using a new top-down process, which involves a 2D array bio-template etching mask made of Listeria-Dps with a 4.5 nm diameter iron oxide core and damage-free neutral-beam etching (Si-ND diameter: 6.4 nm). An Si-ND array with an SiO2 matrix demonstrated more controllable optical bandgap energy due to the fine tunability of the Si-ND thickness and diameter. Unlike the case of shrinking Si-ND thickness, the case of shrinking Si-ND diameter simultaneously increased the optical absorption coefficient and the optical bandgap energy. The optical absorption coefficient became higher due to the decrease in the center-to-center distance of NDs to enhance wavefunction coupling. This means that our 6 nm diameter Si-ND structure can satisfy the strict requirements of optical bandgap energy control and high absorption coefficient for achieving realistic Si quantum dot solar cells.

Controlling diameter distribution of catalyst nanoparticles in arc discharge.

PubMed

Li, Jian; Volotskova, Olga; Shashurin, Alexey; Keidar, Michael

2011-11-01

It is demonstrated that the diameter distribution of catalyst nanoparticles in arc discharge can be controlled by a magnetic field. The magnetic field affects the arc shape, shortens the diffusing time of the catalyst nanoparticles through the nucleation zone, and consequentially reduces the average diameters of nanoparticles. The average diameter is reduced from about 7.5 nm without magnetic field to about 5 nm is the case of a magnetic field. Decrease of the catalyst nanoparticle diameter with magnetic field correlates well with decrease in the single-wall carbon nanotube and their bundles diameters.

76 FR 36398 - Airworthiness Directives; BAE SYSTEMS (OPERATIONS) LIMITED Model BAe 146 and Avro 146-RJ Airplanes

Federal Register 2010, 2011, 2012, 2013, 2014

2011-06-22

..., during any inspection required by paragraphs (g) and (h) of this AD, the chromium plating on the outer... chromium plating on the outer diameter of any pin, before further flight, replace the pin with a...

Manufacturing and advanced characterization of sub-25nm diameter CD-AFM probes with sub-10nm tip edges radius

NASA Astrophysics Data System (ADS)

Foucher, Johann; Filippov, Pavel; Penzkofer, Christian; Irmer, Bernd; Schmidt, Sebastian W.

2013-04-01

Atomic force microscopy (AFM) is increasingly used in the semiconductor industry as a versatile monitoring tool for highly critical lithography and etching process steps. Applications range from the inspection of the surface roughness of new materials, over accurate depth measurements to the determination of critical dimension structures. The aim to address the rapidly growing demands on measurement uncertainty and throughput more and more shifts the focus of attention to the AFM tip, which represents the crucial link between AFM tool and the sample to be monitored. Consequently, in order to reach the AFM tool's full potential, the performance of the AFM tip has to be considered as a determining parameter. Currently available AFM tips made from silicon are generally limited by their diameter, radius, and sharpness, considerably restricting the AFM measurement capabilities on sub-30nm spaces. In addition to that, there's lack of adequate characterization structures to accurately characterize sub-25nm tip diameters. Here, we present and discuss a recently introduced AFM tip design (T-shape like design) with precise tip diameters down to 15nm and tip radii down to 5nm fabricated from amorphous, high density diamond-like carbon (HDC/DLC) using electron beam induced processing (EBIP). In addition to that advanced design, we propose a new characterizer structure, which allows for accurate characterization and design control of sub-25nm tip diameters and sub-10nm tip edges radii. We demonstrate the potential advantages of combining a small tip shape design, i.e. tip diameter and tip edge radius, and an advanced tip characterizer for the semiconductor industry by the measurement of advanced lithography patterns.

Use of a Novel Two Color PALM Method to Examine Structural Properties of Drp1 Helical Rings during Mammalian Mitochondrial Fission In Situ

NASA Astrophysics Data System (ADS)

Rosenbloom, Alyssa Blair

In this thesis, we accomplish two goals: 1) we develop a novel two color photoactivatable light microscopy (PALM) method for imaging in mammalian cells and 2) we explore our original biological question and discern the structural properties of the Drp1 helical ring during fission. We established that mitochondrial membranes can be distinguished with the available photoactivatable fluorescent protein mEos2. However, we were not able to use any of the published photoactivatable and photoswitchable green fluorescent proteins, predominantly because of an inability to identify individual fluorescent events due to rapidity of the photoswitiching. Based on published crystal structures, we created novel Dronpa variants with increasing steric hindrance around the chromophore, likely partially inhibiting the isomerization. We replaced Val157 with isoleucine, leucine, or phenyalanine. DronpaV157F showed no fluorescence and was discarded. DronpaV157I and DronpaV157L showed photoswitchable green fluorescence, with individual fluorescent events that were more easily discerned. DronpaV157L in particular had bright fluorescent events that were well separated when imaged in mammalian cells at 20 Hz. We named this new variant rsKame. Using PALM we successfully imaged rsKame expressed and localized to the mammalian mitochondrial inner membrane. With the novel photoswitchable fluorescent protein, rsKame, available, we returned to the development of a novel two color PALM method. We chose PAmCherry1 as the partner for rsKame since PAmCherry1 has distinct and well separated excitation/emission spectra from rsKame and is not activated by low 405 nm laser power density. We first imaged rsKame with 405 nm activation at (0.61 mW/mm2) and 488 nm activation/excitation (5.87 W/mm 2) to completion. We then imaged PAmCherry1 with increasing 405 nm activation (0.6-6.0 W/mm2) and 561 nm excitation (22 W/mm 2). With the novel PALM imaging method, we labeled the inner and outer mitochondrial membranes with large populations of membrane bound rsKame and PAmCherry1 in HeLa and EpH4 cells. We were able to observe and clearly differentiate the two mitochondrial membrane structures and their various morphologies in situ. With the functional two-color PALM method, we returned to our original investigation of the Drp1 fission ring in situ. In fixed HeLa cells, we continued to label the outer membrane with PAmCherry1 and fused rsKame to the N-terminus of Drp1, separated by a linker. The resultant PALM images allowed for the observation of two previously observed and one hitherto unseen distinct Drp1 morphologies: Constrict, Terminal, and Split. The Constrict morphology was defined as the Drp1 structures that clearly encircle the mitochondrial tubule at various stages of membrane constriction. The Terminal morphology was defined as the Drp1 structures found at the termini of mitochondria, presumably post membrane scission. The Split morphology is a novel morphology and was defined as two Drp1 foci flanking the mitochondrial tubule but not completely encircling it. Quantification of the diameter and length of the Drp1 helical ring structures showed that the mean length of the Drp1 helical rings was consistent between all three morphologies, though a slight decrease was observed for the Terminal morphology, likely due to degradation. We observed a decrease of approximately 40 nm between the Constrict and Terminal mean diameters, consistent with a dynamic change in the Drp1 ring size due to membrane constriction towards membrane scission during mitochondrial fission. The Split morphology had a wide distribution of diameters and warrants further study. (Abstract shortened by UMI.)

Double-ended metal halide arc discharge lamp with electrically isolated containment shroud

NASA Technical Reports Server (NTRS)

Muzeroll, Martin M. (Inventor)

1994-01-01

A double-ended arc discharge lamp includes a sealed, light-transmissive outer jacket, a light-transmissive shroud mounted within the outer jacket and directly supported by the outer jacket, and an arc discharge tube mounted within the shroud. The arc tube is typically a metal halide arc discharge tube. In a preferred embodiment, the shroud includes an outwardly flared portion at each end. The outwardly flared portions space the shroud from the outer jacket and support the shroud within the outer jacket. The outwardly flared portions of the shroud can be affixed to the outer jacket by fusing. The outer jacket can be provided with inwardly extending dimples for locating the shroud with respect to the outer jacket. In another embodiment, the outer jacket includes reduced diameter portions near each end which are attached to the shroud.

Ethylene Gas Sensing Properties of Tin Oxide Nanowires Synthesized via CVD Method

NASA Astrophysics Data System (ADS)

Akhir, Maisara A. M.; Mohamed, Khairudin; Rezan, Sheikh A.; Arafat, M. M.; Haseeb, A. S. M. A.; Uda, M. N. A.; Nuradibah, M. A.

2018-03-01

This paper studies ethylene gas sensing performance of tin oxide (SnO2) nanowires (NWs) as sensing material synthesized using chemical vapor deposition (CVD) technique. The effect of NWs diameter on ethylene gas sensing characteristics were investigated. SnO2 NWs with diameter of ∼40 and ∼240 nm were deposited onto the alumina substrate with printed gold electrodes and tested for sensing characteristic toward ethylene gas. From the finding, the smallest diameter of NWs (42 nm) exhibit fast response and recovery time and higher sensitivity compared to largest diameter of NWs (∼240 nm). Both sensor show good reversibility features for ethylene gas sensor.

Retinal Arterioles in Hypo-, Normo-, and Hypertensive Subjects Measured Using Adaptive Optics.

PubMed

Hillard, Jacob G; Gast, Thomas J; Chui, Toco Y P; Sapir, Dan; Burns, Stephen A

2016-08-01

Small artery and arteriolar walls thicken due to elevated blood pressure. Vascular wall thickness show a correlation with hypertensive subject history and risk for stroke and cardiovascular events. The inner and outer diameter of retinal arterioles from less than 10 to over 150 μm were measured using a multiply scattered light adaptive optics scanning laser ophthalmoscope (AOSLO). These measurements were made on three populations, one with habitual blood pressures less than 100/70 mm Hg, one with normal blood pressures without medication, and one with managed essential hypertension. The wall to lumen ratio was largest for the smallest arterioles for all three populations. Data from the hypotensive group had a linear relationship between outer and inner diameters ( r 2 = 0.99) suggesting a similar wall structure in individuals prior to elevated blood pressures. Hypertensive subjects fell below the 95% confidence limits for the hypotensive relationship and had larger wall to lumen ratios and the normotensive group results fell between the other two groups. High-resolution retinal imaging of subjects with essential hypertension showed a significant decrease in vessel inner diameter for a given outer diameter, and increases in wall to lumen ratio and wall cross-sectional areas over the entire range of vessel diameters and suggests that correcting for vessel size may improve the ability to identify significant vascular changes. High-resolution imaging allows precise measurement of vasculature and by comparing results across risk populations may allow improved identification of individuals undergoing hypertensive arterial wall remodeling.

Optimization of electrospun TSF nanofiber alignment and diameter to promote growth and migration of mesenchymal stem cells

NASA Astrophysics Data System (ADS)

Qu, Jing; Zhou, Dandan; Xu, Xiaojing; Zhang, Feng; He, Lihong; Ye, Rong; Zhu, Ziyu; Zuo, Baoqi; Zhang, Huanxiang

2012-11-01

Silk fibroin scaffolds are a naturally derived biocompatible matrix with the potential for reconstructive surgical applications. In this study, tussah silk fibroin (TSF) nanofiber with different diameters (400 nm, 800 nm and 1200 nm) and alignment (random and aligned) were prepared by electrospinning, then the growth and migration of mesenchymal stem cells (MSCs) on these materials were further evaluated. CD90 immunofluorescence staining showed that fiber alignment exhibited a strong influence on the morphology of MSCs, indicating that the alignment of the scaffolds could determine the distribution of cells. Moreover, smaller diameter and aligned TSF scaffolds are more favorable to the growth of MSCs as compared with 800 nm and 1200 nm random TSF scaffolds. In addition, the increased migration speed and efficiency of MSCs induced by three-D TSF were verified, highlighting the guiding roles of TSF to the migrated MSCs. More importantly, 400 nm aligned TSF scaffolds dramatically improved cell migratory speed and further induced the most efficient migration of MSCs as compared with larger diameter TSF scaffolds. In conclusion, the data demonstrate that smaller diameter and aligned electrospun TSF represent valuable scaffolds for supporting and promoting MSCs growth and migration, thus raising the possibility of manipulating TSF scaffolds to enhance homing and therapeutic potential of MSCs in cellular therapy.

Fiber-Based 589 nm Laser for Sodium Guide Star

DTIC Science & Technology

2006-02-01

are combined in a 980/1060 nm WDM coupler and free-space launched through an isolator designed for 1060 nm into a 23 m long Yb doped fiber. This fiber...lenses. The final-stage amplifier comprised a 23 m long YDF with a core diameter of 8 lam and a D-shaped inner cladding of 400 jtm diameter. It was...resolution). (b) High resolution spectrum of the 1178 nm output beam at 534 m W output power, linewidth (FWHM) - 0. 6 nm (0.05 nm resolution). The

Synthesis of Brushite Particles in Reverse Microemulsions of the Biosurfactant Surfactin

PubMed Central

Maity, Jyoti Prakash; Lin, Tz-Jiun; Cheng, Henry Pai-Heng; Chen, Chien-Yen; Reddy, A. Satyanarayana; Atla, Shashi B.; Chang, Young-Fo; Chen, Hau-Ren; Chen, Chien-Cheng

2011-01-01

In this study the “green chemistry” use of the biosurfactant surfactin for the synthesis of calcium phosphate using the reverse microemulsion technique was demonstrated. Calcium phosphates are bioactive materials that are a major constituent of human teeth and bone tissue. A reverse microemulsion technique with surfactin was used to produce nanocrystalline brushite particles. Structural diversity (analyzed by SEM and TEM) resulted from different water to surfactin ratios (W/S; 250, 500, 1000 and 40,000). The particle sizes were found to be in the 16–200 nm range. Morphological variety was observed in the as-synthesized microemulsions, which consisted of nanospheres (~16 nm in diameter) and needle-like (8–14 nm in diameter and 80–100 nm in length) noncalcinated particles. However, the calcinated products included nanospheres (50–200 nm in diameter), oval (~300 nm in diameter) and nanorod (200–400 nm in length) particles. FTIR and XRD analysis confirmed the formation of brushite nanoparticles in the as-synthesized products, while calcium pyrophosphate was produced after calcination. These results indicate that the reverse microemulsion technique using surfactin is a green process suitable for the synthesis of nanoparticles. PMID:21747709

A Piezoelectric Micromotor with a Stator of φ=1.6 mm and l=4 mm Using Bulk PZT

NASA Astrophysics Data System (ADS)

Cagatay, Serra; Koc, Burhanettin; Moses, Paul; Uchino, Kenji

2004-04-01

The smallest discrete piezoelectric ultrasonic motor using bulk ceramics was developed. We are proposing basically a two-part motor: stator and rotor. The stator of the present motor consists of a hollow metal brass tube with outer diameter of 1.6 mm, inner diameter of 0.8 mm and length of only 4 mm with 2 PZT plates bonded onto it. Owing to the asymmetrical stator surface, two degenerated orthogonal bending modes were slightly split, resulting in a wobbling motion. Thus, the motor can be driven by a single driving source. The rotor is a spring, which is basically different from previous designs, pressed at both ends to the stator by a pair of ferrules. Consequently, the length of the whole motor assembly was reduced significantly; a final motor length of only 5 mm was obtained. The working frequency under zero load was approximately 227-233 kHz. Although the size is small, relatively high power was obtained under an optimized load condition: torque of 0.06 mNm, maximum power of 3.2 mW with a speed of 118 rad/s, and maximum efficiency of 11% under 48 Vrms at 221 kHz.

Diameter Control and Photoluminescence of ZnO Nanorods from Trialkylamines

DOE PAGES

Andelman, Tamar; Gong, Yinyan; Neumark, Gertrude; ...

2007-01-01

A novel solution method to control the diameter of ZnO nanorods is reported. Small diameter (2-3 nm) nanorods were synthesized from trihexylamine, and large diameter (50–80 nm) nanorods were synthesized by increasing the alkyl chain length to tridodecylamine. The defect (green) emission of the photoluminescence (PL) spectra of the nanorods varies with diameter, and can thus be controlled by the diameter control. The small ZnO nanorods have strong green emission, while the large diameter nanorods exhibit a remarkably suppressed green band. We show that this observation supports surface oxygen vacancies as the defect that gives rise to the green emission.

Whispering Gallery Optical Resonator Spectroscopic Probe and Method

NASA Technical Reports Server (NTRS)

Anderson, Mark S. (Inventor)

2014-01-01

Disclosed herein is a spectroscopic probe comprising at least one whispering gallery mode optical resonator disposed on a support, the whispering gallery mode optical resonator comprising a continuous outer surface having a cross section comprising a first diameter and a second diameter, wherein the first diameter is greater than the second diameter. A method of measuring a Raman spectrum and an Infra-red spectrum of an analyte using the spectroscopic probe is also disclosed.

Generation of the Submicron Soft X-Ray Beam Using a Fresnel Zone Plate

NASA Astrophysics Data System (ADS)

Nishikino, M.; Kawazome, H.; Tanaka, M.; Kishimoto, M.; Hasegawa, N.; Ochi, Y.; Kawachi, T.; Sukegawa, K.; Yamatani, H.; Nagashima, K.; Kato, Y.

We have developed a fully coherent x-ray laser at 13.9 nm and the application research has been started. The generation of submicron x-ray beam is important for the application of high intensity x-ray beam, such as the non-linear optics, the material science, and the biology. The submicron x-ray bee am is generated by the soft x-ray laser with using a Fresnel zone plate. The spot diameter is estimated about 680 nm (290 nm at FWHM) by the theoretical calculation. In this experiment, the diameter of the x-ray beam is measured by the knife-edge scan. The diameter and the intensity are estimated 730 nm (310 nm at FWHM) and 3x1011 W/cm2, respectively.

[Research on NEDC ultrafine particle emission characters of a port fuel injection gasoline car].

PubMed

Hu, Zhi-Yuan; Li, Jin; Tan, Pi-Qiang; Lou, Di-Ming

2012-12-01

A Santana gasoline car with multi-port fuel injection (PFI) system was used as the research prototype and an engine exhaust particle sizer (EEPS) was employed to investigate the exhaust ultrafine particle number and size distribution characters of the tested vehicle in new European driving cycle (NEDC). The tested results showed that the vehicle's nuclear particle number, accumulation particle number, as well as the total particle number emission increased when the car drove in accelerated passage, and the vehicle's particle number emission was high during the first 40 seconds after test started and when the speed was over 90 km x h(-1) in extra urban driving cycle (EUDC) in NEDC. The ultrafine particle distribution of the whole NEDC showed a single peak logarithmic distribution, with diameters of the peak particle number emission ranging from 10 nm to 30 nm, and the geometric mean diameter was 24 nm. The ultrafine particle distribution of the urban driving cycle named by the economic commission for Europe (ECE) e. g. ECE I, ECE II - IV, the extra urban driving cycle e. g. EUDC, and the idling, constant speed, acceleration, deceleration operation conditions of NEDC all showed a single peak logarithmic distribution, also with particle diameters of the peak particle number emission ranging from 10 nm to 30 nm, and the geometric mean diameters of different driving cycle and different driving mode were from 14 nm to 42 nm. Therefore, the ultrafine particle emissions of the tested PFI gasoline car were mainly consisted of nuclear mode particles with a diameter of less than 50 nm.

Research Update: Synthesis of sub-15-nm diameter silver nanowires through a water-based hydrothermal method: Fabrication of low-haze 2D conductive films

NASA Astrophysics Data System (ADS)

Jang, Hae-Won; Kim, Yong-Hoe; Lee, Ki-Wook; Kim, Yoon-Mi; Kim, Jin-Yeol

2017-08-01

We synthesized ultra-thin Ag nanowire (Ag NWs) with sub-15 nm diameters and aspect ratios of 1000 through a water-based high-pressure hydrothermal method in the presence of a tetrabutylammonium dichlorobromide organic salt and glucose reducing agent. In the crystal growth stage, the diameter of the NWs could be controlled by adjusting the pressure, and 15-nm diameter wires were obtained at a pressure of 190 psi. These 2D conductive Ag NW network films showed an excellent optical performance with low haze value of ≤1.0% and 94.5% transmittance at a low sheet resistance of 20 Ω/sq.

Reduced Net Erosion of High-Z PFC Materials in DIII-D Divertor

NASA Astrophysics Data System (ADS)

Rudakov, D. L.; Stangeby, P. C.; Elder, J. D.; Wampler, W. R.; Buchenauer, D. A.; Watkins, J. G.; Brooks, J. N.; Hassanein, A.; Sizyuk, T.; Briesemeister, A. R.; McLean, A. G.; Chrobak, C. P.; Guo, H. Y.; Leonard, A. W.; Wong, C. P. C.

2014-10-01

DiMES samples featuring 1 cm and 1 mm diameter W films deposited on a Si substrate were exposed in DIII-D near the attached outer strike point of LSN L-mode discharges. The measured net and gross erosion rates of W, determined from post-mortem ion beam analysis (IBA) of 1 cm and 1 mm samples, were 0.14 and 0.48 nm/s, respectively, giving net/gross erosion ratio of 0.29. REDEP/WBC modeling of this experiment yielded a very close ratio of 0.33. Projection of the modeling results to ITER shows very low net erosion of W. In another experiment Mo-coated samples were exposed with 13CH4 gas injected ~2 cm upstream of DiMES. Reduction of Mo erosion was evidenced in - situ by the suppression of MoI line radiation. Post-mortem IBA showed that the net erosion of Mo was below the measurement resolution of 0.5 nm, corresponding to a rate of <=0.07 nm/s. Compared to the previously measured erosion rates, this constitutes a reduction of more than 10X. Work supported in part the by US DOE under DE-FG02-07ER54917, DE-AC04-94AL85000, DE-AC05-00OR22725, DE-AC52-07NA27344 & DE-FC02-04ER54698.

Programmed Nanoparticle-Loaded Nanoparticles for Deep-Penetrating 3D Cancer Therapy.

PubMed

Kim, Jinhwan; Jo, Changshin; Lim, Won-Gwang; Jung, Sungjin; Lee, Yeong Mi; Lim, Jun; Lee, Haeshin; Lee, Jinwoo; Kim, Won Jong

2018-05-18

Tumors are 3D, composed of cellular agglomerations and blood vessels. Therapies involving nanoparticles utilize specific accumulations due to the leaky vascular structures. However, systemically injected nanoparticles are mostly uptaken by cells located on the surfaces of cancer tissues, lacking deep penetration into the core cancer regions. Herein, an unprecedented strategy, described as injecting "nanoparticle-loaded nanoparticles" to address the long-lasting problem is reported for effective surface-to-core drug delivery in entire 3D tumors. The "nanoparticle-loaded nanoparticle" is a silica nanoparticle (≈150 nm) with well-developed, interconnected channels (diameter of ≈30 nm), in which small gold nanoparticles (AuNPs) (≈15 nm) with programmable DNA are located. The nanoparticle (AuNPs)-loaded nanoparticles (silica): (1) can accumulate in tumors through leaky vascular structures by protecting the inner therapeutic AuNPs during blood circulation, and then (2) allow diffusion of the AuNPs for penetration into the entire surface-to-core tumor tissues, and finally (3) release a drug triggered by cancer-characteristic pH gradients. The hierarchical "nanoparticle-loaded nanoparticle" can be a rational design for cancer therapies because the outer large nanoparticles are effective in blood circulation and in protection of the therapeutic nanoparticles inside, allowing the loaded small nanoparticles to penetrate deeply into 3D tumors with anticancer drugs. © 2018 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Maskless nano-implant of 20 keV Ga+ in bulk Si(1 0 0) substrates

NASA Astrophysics Data System (ADS)

Milazzo, R. G.; D'Arrigo, G.; Mio, A. M.; Rimini, E.; Spinella, C.; Peto, L.; Nadzeyka, A.; Bauerdick, S.

2014-12-01

Multidirectional SPEG (Solid Phase Epitaxial Growth) of silicon has been investigated in micro and nanoamorphous structures generated on a crystalline substrate by a nano-sized ion beam, Gaussian shaped and with a standard deviation of about 5 nm. The 20 keV Ga+ ions were implanted at a fluence of 5 × 1014 ions cm-2 in a bulk Si(1 0 0) single crystal. Two structures were used for the implants: circular regions of 100 nm and 1 μm diameters respectively and straight lines 10 nm in width and few microns in length along (1 0 0) or (1 1 0) directions. The lateral spread of ions has been taken into account in the damage estimation. Transmission Electron Microscopy indicates that the structures are made of an amorphous core surrounded by a defective and filamentary shell. The recovery of the damaged outer regions promptly occurs during the early stages of the thermal treatment at 500-600 °C for all the structures. By prolonging annealing time, re-crystallization of the amorphous cores is achieved too by the movement of the underneath crystal-amorphous interface. The re-growth is almost defects free when the contribution of the crystalline seed below the structures is present, defective and twin mediated if it misses as in the thinnest regions of the specimen.

Wire-in-tube structure fabricated by single capillary electrospinning via nanoscale Kirkendall effect: the case of nickel-zinc ferrite.

PubMed

Fu, Jiecai; Zhang, Junli; Peng, Yong; Zhao, Changhui; He, Yongmin; Zhang, Zhenxing; Pan, Xiaojun; Mellors, Nigel J; Xie, Erqing

2013-12-21

Wire-in-tube structures have previously been prepared using an electrospinning method by means of tuning hydrolysis/alcoholysis of a precursor solution. Nickel-zinc ferrite (Ni0.5Zn0.5Fe2O4) nanowire-in-nanotubes have been prepared as a demonstration. The detailed nanoscale characterization, formation process and magnetic properties of Ni0.5Zn0.5Fe2O4 nanowire-in-nanotubes has been studied comprehensively. The average diameters of the outer tubes and inner wires of Ni0.5Zn0.5Fe2O4 nanowire-in-nanotubes are around 120 nm and 42 nm, respectively. Each fully calcined individual nanowire-in-nanotube, either the outer-tube or the inner-wire, is composed of Ni0.5Zn0.5Fe2O4 monocrystallites stacked along the longitudinal direction with random orientation. The process of calcining electrospun polymer composite nanofibres can be viewed as a morphologically template nucleation and precursor diffusion process. This allows the nitrates precursor to diffuse toward the surface of the nanofibres while the oxides (decomposed from hydroxides and nitrates) products diffuse to the core region of the nanofibres; the amorphous nanofibres transforming thereby into crystalline nanowire-in-nanotubes. In addition, the magnetic properties of the Ni0.5Zn0.5Fe2O4 nanowire-in-nanotubes were also examined. It is believed that this nanowire-in-nanotube (sometimes called core-shell) structure, with its uniform size and well-controlled orientation of the long nanowire-in-nanotubes, is particularly attractive for use in the field of nano-fluidic devices and nano-energy harvesting devices.

A multifunctional role of trialkylbenzenes for the preparation of aqueous colloidal mesostructured/mesoporous silica nanoparticles with controlled pore size, particle diameter, and morphology

NASA Astrophysics Data System (ADS)

Yamada, Hironori; Ujiie, Hiroto; Urata, Chihiro; Yamamoto, Eisuke; Yamauchi, Yusuke; Kuroda, Kazuyuki

2015-11-01

Both the pore size and particle diameter of aqueous colloidal mesostructured/mesoporous silica nanoparticles (CMSS/CMPS) derived from tetrapropoxysilane were effectively and easily controlled by the addition of trialkylbenzenes (TAB). Aqueous highly dispersed CMPS with large pores were successfully obtained through removal of surfactants and TAB by a dialysis process. The pore size (from 4 nm to 8 nm) and particle diameter (from 50 nm to 380 nm) were more effectively enlarged by the addition of 1,3,5-triisopropylbenzene (TIPB) than 1,3,5-trimethylbenzene (TMB), and the enlargement did not cause the variation of the mesostructure and particle morphology. The larger molecular size and higher hydrophobicity of TIPB than TMB induce the incorporation of TIPB into micelles without the structural change. When TMB was used as TAB, the pore size of CMSS was also enlarged while the mesostructure and particle morphology were varied. Interestingly, when tetramethoxysilane and TIPB were used, CMSS with a very small particle diameter (20 nm) with concave surfaces and large mesopores were obtained, which may strongly be related to the initial nucleation of CMSS. A judicious choice of TAB and Si sources is quite important to control the mesostructure, size of mesopores, particle diameter, and morphology.Both the pore size and particle diameter of aqueous colloidal mesostructured/mesoporous silica nanoparticles (CMSS/CMPS) derived from tetrapropoxysilane were effectively and easily controlled by the addition of trialkylbenzenes (TAB). Aqueous highly dispersed CMPS with large pores were successfully obtained through removal of surfactants and TAB by a dialysis process. The pore size (from 4 nm to 8 nm) and particle diameter (from 50 nm to 380 nm) were more effectively enlarged by the addition of 1,3,5-triisopropylbenzene (TIPB) than 1,3,5-trimethylbenzene (TMB), and the enlargement did not cause the variation of the mesostructure and particle morphology. The larger molecular size and higher hydrophobicity of TIPB than TMB induce the incorporation of TIPB into micelles without the structural change. When TMB was used as TAB, the pore size of CMSS was also enlarged while the mesostructure and particle morphology were varied. Interestingly, when tetramethoxysilane and TIPB were used, CMSS with a very small particle diameter (20 nm) with concave surfaces and large mesopores were obtained, which may strongly be related to the initial nucleation of CMSS. A judicious choice of TAB and Si sources is quite important to control the mesostructure, size of mesopores, particle diameter, and morphology. Electronic supplementary information (ESI) available. See DOI: 10.1039/c5nr04465k

Diameter control of single-walled carbon nanotube forests from 1.3–3.0 nm by arc plasma deposition

PubMed Central

Chen, Guohai; Seki, Yasuaki; Kimura, Hiroe; Sakurai, Shunsuke; Yumura, Motoo; Hata, Kenji; Futaba, Don N.

2014-01-01

We present a method to both precisely and continuously control the average diameter of single-walled carbon nanotubes in a forest ranging from 1.3 to 3.0 nm with ~1 Å resolution. The diameter control of the forest was achieved through tuning of the catalyst state (size, density, and composition) using arc plasma deposition of nanoparticles. This 1.7 nm control range and 1 Å precision exceed the highest reports to date. PMID:24448201

Novel Hollow Fiber Air Filters for the Removal of Ultrafine Particles in PM2.5 with Repetitive Usage Capability.

PubMed

Li, Manqing; Feng, Yingnan; Wang, Kaiyu; Yong, Wai Fen; Yu, Liya; Chung, Tai-Shung

2017-09-05

Severe air pollution has become a global concern, and there is a pressing need to develop effective and efficient air filters for removing airborne particulate matters (PMs). In this work, a highly permeable poly(ether sulfone) (PES) based hollow fiber membrane was developed via a one-step dry-jet wet spinning. For the first time, a hollow fiber membrane was used in removing the ultrafine particles (PMs with aerodynamic equivalent diameters of less than 100 nm) in PM 2.5 . The novel air filter was designed to possess the synergistic advantages of porous filters and fibrous filters with a sievelike outer surface and a fibrouslike porous substrate. A filtration efficiency of higher than 99.995% could be easily achieved when the self-support hollow fiber was challenged with less than 300 nm particulates. Without losses of the structural advantages, we have demonstrated that the permeation properties of the hollow fiber membrane can be facilely tailored via manipulation of the dope and bore fluid formulations. Various cleaning strategies were explored to regenerate the membrane performance after fouling. Both water rinse and backwash showed effectiveness to restore the membrane permeance for repetitive usage.

Bio-Inspired Hierarchical Nanofibrous Fe3O4-TiO2-Carbon Composite as a High-Performance Anode Material for Lithium-Ion Batteries.

PubMed

Li, Shun; Wang, Mengya; Luo, Yan; Huang, Jianguo

2016-07-13

A bioinspired hierarchical nanofibrous Fe3O4-TiO2-carbon composite was fabricated by employing natural cellulose substance (e.g., filter paper) as both the scaffold and the carbon source and showed improved electrochemical performances when it is employed as an anode material for lithium-ion batteries. FeOOH nanoparticles were first grown uniformly onto the surface of the titania thin-layer precoated cellulose nanofibers, and thereafter, the as-prepared FeOOH-TiO2-cellulose composite was calcined and carbonized in argon atmosphere at 500 °C for 6 h to produce the Fe3O4-TiO2-carbon composite. The resultant composite possesses a hierarchical structure that was faithfully inherited from the initial cellulose substance, which was composed of titania-coated carbon fibers with corncob-like shaped Fe3O4 nanoparticles immobilized on the surfaces. The diameter of the composite nanofiber is ca. 100-200 nm, and the diameter of the Fe3O4 nanoparticle is about 30 nm, which is coated with an ultrathin carbon layer with a thickness about 3 nm. This composite displayed superior lithium-ion storage performance. It showed a first-cycle discharge capacity of 1340 mAh/g, delivering a stable reversible capacity of ca. 525 mAh/g after 100 charge-discharge cycles at a current density of 100 mA/g, and the efficiency is as high as ca. 95% of the theoretical value. This is much higher than those of the commercial Fe3O4 powder (160 mAh/g) and the Fe3O4-carbon counter material (310 mAh/g). It was demonstrated that the thin titania precoating layer (thickness ca. 3-5 nm) is necessary for the high content loading of the Fe3O4 nanoparticles onto the carbon nanofibers. Owing to the unique three-dimensional porous network structure of the carbon-fiber scaffold, together with the ultrathin outer carbon-coating layer, the composite showed significantly improved cycling stability and rate capability.

Isolation of >1 nm Diameter Single-Wall Carbon Nanotube Species Using Aqueous Two-Phase Extraction.

PubMed

Fagan, Jeffrey A; Hároz, Erik H; Ihly, Rachelle; Gui, Hui; Blackburn, Jeffrey L; Simpson, Jeffrey R; Lam, Stephanie; Hight Walker, Angela R; Doorn, Stephen K; Zheng, Ming

2015-05-26

In this contribution we demonstrate the effective separation of single-wall carbon nanotube (SWCNT) species with diameters larger than 1 nm through multistage aqueous two-phase extraction (ATPE), including isolation at the near-monochiral species level up to at least the diameter range of SWCNTs synthesized by electric arc synthesis (1.3-1.6 nm). We also demonstrate that refined species are readily obtained from both the metallic and semiconducting subpopulations of SWCNTs and that this methodology is effective for multiple SWCNT raw materials. Using these data, we report an empirical function for the necessary surfactant concentrations in the ATPE method for separating different SWCNTs into either the lower or upper phase as a function of SWCNT diameter. This empirical correlation enables predictive separation design and identifies a subset of SWCNTs that behave unusually as compared to other species. These results not only dramatically increase the range of SWCNT diameters to which species selective separation can be achieved but also demonstrate that aqueous two-phase separations can be designed across experimentally accessible ranges of surfactant concentrations to controllably separate SWCNT populations of very small (∼0.62 nm) to very large diameters (>1.7 nm). Together, the results reported here indicate that total separation of all SWCNT species is likely feasible by the ATPE method, especially given future development of multistage automated extraction techniques.

Thermophilic Ferritin: Versatile Nanohost

NASA Astrophysics Data System (ADS)

Pulsipher, Katherine W.

Thermophilic ferritin from Archaeoglobus fulgidus (AfFtn) is a 24meric, hollow, cage-like protein, whose native function is the oxidation, mineralization, and storage of iron. Unique among ferritins, its self-assembly is dependent on high ionic strength, reflecting the deep sea thermal vent environment where A. fulgidus is found. This ionic strength dependence can be used to encapsulate charged cargo within the AfFtn cavity. Its subunits self-assemble into tetrahedral symmetry, resulting in four, large (4.5 nm), triangular pores, not found in other ferritins. Due to its size (12 nm outer diameter, 8 nm inner diameter), self-assembly properties, and potential for both genetic and chemical modification, AfFtn is an ideal nanocontainer for a variety of cargo, including inorganic nanoparticles and proteins. We have sought to better understand the self-assembly of AfFtn and its encapsulation of various cargo. Guided by computational analysis and through mutagenesis, we have investigated the role of electrostatics along the AfFtn trimeric interface in self-assembly. We have developed a series of single point mutants with increasingly favorable cage assembly. One specific mutation, E65R, has a dramatic effect on AfFtn, almost entirely preventing disassembly and enhancing thermal stability by 14°C. By using a novel graphene-based microelectrode, we have determined that AfFtn maintains its quaternary structure upon encapsulation of a gold nanoparticle, developing a new tool for investigating protein-nanomaterial interactions. We have also shown that AfFtn can be used to template seeded gold nanoparticle growth and have explored two often neglected factors in ferritin-nanoparticle templating: the charge of the gold salt used, and the size of the protein pores. Our results demonstrate that the open, porous structure of AfFtn allows more efficient particle growth than typical closed-pore ferritins. Finally, we have expanded the cargo uptake of AfFtn beyond nanoparticles to include proteins, encapsulating supercharged GFP. The AfFtn-cargo complexes developed here have application in catalysis, nanomaterials synthesis, and targeted delivery.

Metal tube reducer is inexpensive and simple to operate

NASA Technical Reports Server (NTRS)

Mayfield, R. M.

1967-01-01

Low-cost metal tube reducer accepts tubing up to 1 inch outer diameter and can reduce this diameter to less than 1/2 inch with controlled wall thickness. This device can reduce all of the tube without waste. It produces extremely good surface finishes.

Ferromagnetic signal in nanosized Ag particles.

PubMed

Jo, Younghun; Jung, Myung-Hwa; Kyum, Myung-Chul; Lee, Sung-Ik

2007-11-01

A new technique using an inductively coupled plasma reactor equipped with a liquid-nitrogen cooling system was developed to prepare Ag nanoparticles. The magnetic signal from these Ag particles with diameters of 4 nm showed, surprisingly, a signal with combined ferromagnetic and diamagnetic components, in contrast to the signal with only one diamagnetic component from bulk Ag. The same technique was used to prepare the Ag/Cu nanoparticles, which are Ag nanoparticles coated with a Cu layer. Compared to the Ag nanoparticles, these showed a greatly enhanced superparamagnetic signal in addition to the same value of the ferromagnetism. The comparison between the Ag and the Ag/Cu nanoparticles indicated that the ferromagnetic components are a common feature of Ag nanoparticles while the greatly enhanced paramagnetic component of Ag/Cu, which dominates over the background diamagnetic component from the Ag core, is from the outer Cu shell.

Switching fields and their distributions in rounded-rectangle [Co/Pd]8 nanodots and nanorings with identical configuration

NASA Astrophysics Data System (ADS)

Ren, Y.; Wang, Y.; He, X. D.; Adeyeye, A. O.

2018-04-01

We present two different types of magnetization reversal behaviors for the identically-configured Co/Pd multilayers with rounded-rectangular nanodots and nanorings for various edge-to-edge distances (s), by using focused magneto-optic Kerr measurements and magnetic force microscopy measurements. For the nanodots with a fixed outer diameter of d = 580 nm, the switching field Hsw and switching field distribution (SFD) are almost invariant with respect to s. However, the Hsw and SFD for the nanodot arrays could be easily modulated by varying d, which is ascribed to the size effect. In contrast, the Hsw and SFD are strongly dependent on s for the nanorings. Compared to the strongly coupled magnetic moments of the closely-packed nanorings, the magnetostatic interaction among nanodots is negligible, which should be responsible for the observed different magnetization reversal behaviors.

New Particle Formation in the Tropical UTLS Near Costa Rica: Contrast January and February with June and August

NASA Astrophysics Data System (ADS)

Wilson, J. C.; Saad, M. S.; Axisa, D.

2017-12-01

Aerosol size distributions were measured in the 4 nm to 1000 nm diameter range from the NASA WB-57 aircraft based in Costa Rica from 2004 through 2007. The measurements were made with the Nuclei Mode Aerosol Size Spectrometer (NMASS) and the Focused Cavity Aerosol Spectrometer (FCAS). The NMASS consists of 5 condensation particle counters (CPCs) each operated with a different supersaturation of the working fluid (FC-43). Therefore each CPC has a different lower size cut off. The size cutoffs are near 4nm 8nm, 16 nm, 32nm and 50nm in diameter. The FCAS is an optical particle counter that detects and sizes particles in the 100 to 1000 nm diameter range. By considering counting statistics, it is possible to identify those time intervals during which the counts in the 4 nm channel exceeded the counts in the 8 nm channel. Thus it is possible to clearly identify when there are particles in the 4 to 8 nm diameter range present in the size distribution. These particles have a short lifetime due to coagulation and their presence is taken to be evidence of recent new particle formation (NPF). The measurements made in January-February are contrasted with measurements made in June and August and differences are seen in the frequency with which NPF occurred. We examine the roles of air mass origin as determined by back trajectories, pre-existing aerosol surface area, atmospheric motions and trace gas concentrations in contributing to this difference.

Interruption of Hydrogen Bonding Networks of Water in Carbon Nanotubes Due to Strong Hydration Shell Formation.

PubMed

Oya, Yoshifumi; Hata, Kenji; Ohba, Tomonori

2017-10-24

We present the structures of NaCl aqueous solution in carbon nanotubes with diameters of 1, 2, and 3 nm based on an analysis performed using X-ray diffraction and canonical ensemble Monte Carlo simulations. Anomalously longer nearest-neighbor distances were observed in the electrolyte for the 1-nm-diameter carbon nanotubes; in contrast, in the 2 and 3 nm carbon nanotubes, the nearest-neighbor distances were shorter than those in the bulk electrolyte. We also observed similar properties for water in carbon nanotubes, which was expected because the main component of the electrolyte was water. However, the nearest-neighbor distances of the electrolyte were longer than those of water in all of the carbon nanotubes; the difference was especially pronounced in the 2-nm-diameter carbon nanotubes. Thus, small numbers of ions affected the entire structure of the electrolyte in the nanopores of the carbon nanotubes. The formation of strong hydration shells between ions and water molecules considerably interrupted the hydrogen bonding between water molecules in the nanopores of the carbon nanotubes. The hydration shell had a diameter of approximately 1 nm, and hydration shells were thus adopted for the nanopores of the 2-nm-diameter carbon nanotubes, providing an explanation for the large difference in the nearest-neighbor distances between the electrolyte and water in these nanopores.

Evaluation of the Lower Punctum Parameters and Morphology Using Spectral Domain Anterior Segment Optical Coherence Tomography

PubMed Central

Allam, Riham S. H. M.; Ahmed, Rania A.

2015-01-01

Purpose. To study features of the lower punctum in normal subjects using spectral domain anterior segment optical coherence tomography (SD AS-OCT). Methods. Observational cross-sectional study that included 147 punctae (76 subjects). Punctae were evaluated clinically for appearance, position, and size. AS-OCT was used to evaluate the punctal shape, contents, and junction with the vertical canaliculus. Inner and outer diameters as well as depth were measured. Results. 24 males and 52 females (mean age 44 ± 14.35 y) were included. Lower punctum was perceived by OCT to be an area with an outer diameter (mean 412.16 ± 163 μm), inner diameter (mean 233.67 ± 138.73 μm), and depth (mean 251.7 ± 126.58 μm). The OCT measured outer punctum diameter was significantly less than that measured clinically (P: 0.000). Seven major shapes were identified. The junction with the vertical canaliculus was detectable in 44%. Fluid was detected in 34%, one of which had an air bubble; however, 63% of punctae showed no contents and 4% had debris. Conclusions. AS-OCT can be a useful tool in understanding the anatomy of the punctum and distal lacrimal system as well as tear drainage physiology. Measuring the punctum size may play a role in plugs fitting. PMID:26090219

Theory of nanotube faraday cage

NASA Astrophysics Data System (ADS)

Roxana Margine, Elena; Nisoli, Cristiano; Kolmogorov, Aleksey; Crespi, Vincent H.

2003-03-01

Charge transfer between dopants and double-wall carbon nanotubes is examined theoretically. We model the system as a triple cylindrical capacitor with the dopants forming a shell around the outer wall of the nanotube. The total energy of the system contains three terms: the band structure energies of the inner and outer tube, calculated in a tight-binding model with rigid bands, and the electrostatic energy of the tri-layer distribution. Even for metallic inner and outer tube walls, wherein the diameter dependence of the bandgap does not favor the outer wall, nearly all of the dopant charge resides on the outer layer, a nanometer-scale Faraday cage. The calculated charge distribution is in agreement with recent experimental measurements.

Self-organized formation of GaSb/GaAs quantum rings.

PubMed

Timm, R; Eisele, H; Lenz, A; Ivanova, L; Balakrishnan, G; Huffaker, D L; Dähne, M

2008-12-19

Ring-shaped GaSb/GaAs quantum dots, grown by molecular beam epitaxy, were studied using cross-sectional scanning tunneling microscopy. These quantum rings have an outer shape of a truncated pyramid with baselengths around 15 nm and heights of about 2 nm but are characterized by a clear central opening extending over about 40% of the outer baselength. They form spontaneously during the growth and subsequent continuous capping of GaSb/GaAs quantum dots due to the large strain and substantial As-for-Sb exchange reactions leading to strong Sb segregation.

Exposure assessment of nano-sized and respirable particles at different workplaces

NASA Astrophysics Data System (ADS)

Tsai, Chuen-Jinn; Huang, Cheng-Yu; Chen, Sheng-Chieh; Ho, Chi-En; Huang, Cheng-Hsiung; Chen, Chun-Wan; Chang, Cheng-Ping; Tsai, Su-Jung; Ellenbecker, Michael J.

2011-09-01

In this study, nanoparticle (NP, diameter < 100 nm) and respirable particles measurements were conducted at three different nanopowder workplaces, including the mixing area of a nano-SiO2-epoxy molding compound plant (primary diameter: 15 nm), bagging areas of a nano-carbon black (nano-CB) (primary diameter: 32 nm) and a nano-CaCO3 (primary diameter: 94 nm) manufacturing plant. Chemical analysis of respirable particle mass (RPM) and NPs was performed to quantify the content of manufactured nanoparticles in the collected samples. Nanopowder products obtained from the plants were used in the laboratory dustiness testing using a rotating drum tester to obtain particle mass and number distributions. The obtained laboratory data were then used to elucidate the field data. Both field and laboratory data showed that NP number and mass concentrations of manufactured materials were close to the background level. Number concentration was elevated only for particles with the electrical mobility diameter >100 nm during bagging or feeding processes, unless there were combustion-related incidental sources existed. Large fraction of nanomaterials was found in the RPM due to agglomeration of nanomaterials or attachment of nanomaterials to the larger particles. From this study, it is concluded that RPM concentration measurements are necessary for the exposure assessment of nanoparticles in workplaces.

White light supercontinuum generation in a Y-shaped microstructured tapered fiber pumped at 1064 nm.

PubMed

Cascante-Vindas, J; Díez, A; Cruz, J L; Andrés, M V

2010-07-05

We report the generation of supercontinuum in a Ge-doped Y-shape tapered fiber pumped at 1064 nm in the ns pump regime. The taper was designed to have long taper transitions and a taper waist with a core diameter of 0.9 mum. The large air-filling fraction and diameter of the air-hole microstructure reduces the confinement loss at long wavelengths so, enabling the extension of the spectrum to longer wavelengths. Along the taper transition the zero-dispersion wavelength decreases as the diameter of the taper becomes smaller. The spectral components generated along the taper transition pump the taper waist, enhancing the generation of short wavelengths. A flat spectrum spanning from 420 nm to 1850 nm is reported.

High-speed, bi-directional dual-core fiber transmission system for high-density, short-reach optical interconnects

NASA Astrophysics Data System (ADS)

Geng, Ying; Li, Shenping; Li, Ming-Jun; Sutton, Clifford G.; McCollum, Robert L.; McClure, Randy L.; Koklyushkin, Alexander V.; Matthews, Karen I.; Luther, James P.; Butler, Douglas L.

2015-03-01

A complete single mode dual-core fiber system for short-reach optical interconnects is fabricated and tested for high-speed data transmission. It includes dual-core fibers capable of bi-directional data transmission, dual-core simplex LC connectors, and fan-outs. The transmission system offers simplified bi-directional traffic engineering with integrated bidirectional transceivers and compact system design, utilizing simplex dual-core LC connectors that use half the space while increasing the bandwidth density by a factor of two. The fiber has two cores that are compatible with single mode fiber and conforms to the industry standard outer diameter of 125 μm. This reduces operational complexity by reducing the size and number of fibers, cables and connectors. Measured OTDR loss for both cores was 0.34 dB/km at 1310 nm and 0.19 dB/km at 1550 nm. Crosstalk for a piece of 5.8 km long dual-core fiber was measured to be below -75 dB at 1310 nm, and below -40 dB at 1550 nm. Both free-space optics fan-outs and tapered-fiber-coupler based MCF fan-outs were evaluated for the transmission system. Error-free and penalty-free 25 Gb/s bi-directional transmission performance was demonstrated for three different fiber lengths, 200 m, 2 km and 10 km, using the complete all-fiber-based system including connectors and fan-outs. This single mode, dual-core fiber transmission system adds complementary value to systems where additional increases in bandwidth density can come from wavelength division multiplexing and multiple bits per symbol.

Selective-area growth of GaN nanocolumns on Si(111) substrates for application to nanocolumn emitters with systematic analysis of dislocation filtering effect of nanocolumns

NASA Astrophysics Data System (ADS)

Kishino, Katsumi; Ishizawa, Shunsuke

2015-06-01

The growth of highly uniform arrays of GaN nanocolumns with diameters from 122 to 430 nm on Si (111) substrates was demonstrated. The employment of GaN film templates with flat surfaces (root mean square surface roughness of 0.84 nm), which were obtained using an AlN/GaN superlattice (SL) buffer on Si, contributed to the high-quality selective-area growth of nanocolumns using a thin Ti mask of 5 nm thickness by rf-plasma-assisted molecular beam epitaxy. Although the GaN template included a large number of dislocations (dislocation density ˜1011 cm-2), the dislocation filtering effect of nanocolumns was enhanced with decreasing nanocolumn diameters (D). Systematic transmission electron microscopy (TEM) observation enabled us to explain the dependence of the dislocation propagation behavior in nanocolumns on the nanocolumn diameter for the first time. Plan-view TEM analysis was performed for nanocolumns with D = 120-324 nm by slicing the nanocolumns horizontally at a height of ˜300 nm above their bottoms and dislocation propagation through the nanocolumns was analyzed by the cross-sectional TEM observation of nanocolumns with D ˜ 200 nm. It was clarified that dislocations were effectively filtered in the bottom 300 nm region of the nanocolumns, the dislocation density of the nanocolumns decreased with decreasing D, and for narrow nanocolumns with D < 200 nm, dislocation-free crystals were obtained in the upper part of the nanocolumns. The dramatic improvement in the emission properties of GaN nanocolumns observed with decreasing diameter is discussed in relation to the decreased dislocation density. The laser action of InGaN/GaN-based nanocolumn arrays with a nanocolumn diameter of 170 nm and a period of 200 nm on Si under optical excitation was obtained with an emission wavelength of 407 nm. We also fabricated red-emitting InGaN-based nanocolumn light-emitting diodes on Si that operated at a wavelength of 652 nm, demonstrating vertical conduction through the AlN/GaN SL buffer to the Si substrate.

The Three-Dimensional Distribution of αA-Crystalline in Rat Lenses and Its Possible Relation to Transparency

PubMed Central

Zampighi, Guido A.; Zampighi, Lorenzo; Lanzavecchia, Salvatore

2011-01-01

Lens transparency depends on the accumulation of massive quantities (600–800 mg/ml) of twelve primary crystallines and two truncated crystallines in highly elongated “fiber” cells. Despite numerous studies, major unanswered questions are how this heterogeneous group of proteins becomes organized to bestow the lens with its unique optical properties and how it changes during cataract formation. Using novel methods based on conical tomography and labeling with antibody/gold conjugates, we have profiled the 3D-distribution of the αA-crystalline in rat lenses at ∼2 nm resolutions and three-dimensions. Analysis of tomograms calculated from lenses labeled with anti-αA-crystalline and gold particles (∼3 nm and ∼7 nm diameter) revealed geometric patterns shaped as lines, isosceles triangles and polyhedrons. A Gaussian distribution centered at ∼7.5 nm fitted the distances between the ∼3 nm diameter gold conjugates. A Gaussian distribution centered at ∼14 nm fitted the Euclidian distances between the smaller and the larger gold particles and another Gaussian at 21–24 nm the distances between the larger particles. Independent of their diameters, tethers of 14–17 nm in length connected files of gold particles to thin filaments or clusters to ∼15 nm diameter “beads.” We used the information gathered from tomograms of labeled lenses to determine the distribution of the αA-crystalline in unlabeled lenses. We found that αA-crystalline monomers spaced ∼7 nm or αA-crystalline dimers spaced ∼15 nm center-to-center apart decorated thin filaments of the lens cytoskeleton. It thus seems likely that lost or gain of long-range order determines the 3D-structure of the fiber cell and possible also cataract formation. PMID:21909355

Fabrication of sub-micrometer-sized jingle bell-shaped hollow spheres from multilayered core-shell particles.

PubMed

Gu, Shunchao; Kondo, Tomohiro; Mine, Eiichi; Nagao, Daisuke; Kobayashi, Yoshio; Konno, Mikio

2004-11-01

Jingle bell-shaped hollow spheres were fabricated starting from multilayered particles composed of a silica core, a polystyrene inner shell, and a titania outer shell. Composite particles of silica core-polystyrene shell, synthesized by coating a 339-nm-sized silica core with a polystyrene shell of thickness 238 nm in emulsion polymerization, were used as core particles for a succeeding titania-coating. A sol-gel method was employed to form the titania outer shell with a thickness of 37 nm. The inner polystyrene shell in the multilayered particles was removed by immersing them in tetrahydrofuran. These successive procedures could produce jingle bell-shaped hollow spheres that contained a silica core in the titania shell.

Atomic layer deposition as pore diameter adjustment tool for nanoporous aluminum oxide injection molding masks.

PubMed

Miikkulainen, Ville; Rasilainen, Tiina; Puukilainen, Esa; Suvanto, Mika; Pakkanen, Tapani A

2008-05-06

The wetting properties of polypropylene (PP) surfaces were modified by adjusting the dimensions of the surface nanostructure. The nanostructures were generated by injection molding with nanoporous anodized aluminum oxide (AAO) as the mold insert. Atomic layer deposition (ALD) of molybdenum nitride film was used to control the pore diameters of the AAO inserts. The original 50-nm pore diameter of AAO was adjusted by depositing films of thickness 5, 10, and 15 nm on AAO. Bis(tert-butylimido)-bis(dimethylamido)molybdenum and ammonia were used as precursors in deposition. The resulting pore diameters in the nitride-coated AAO inserts were 40, 30, and 20 nm, respectively. Injection molding of PP was conducted with the coated inserts, as well as with the non-coated insert. Besides the pore diameter, the injection mold temperature was varied with temperatures of 50, 70, and 90 degrees C tested. Water contact angles of PP casts were measured and compared with theoretical contact angles calculated from Wenzel and Cassie-Baxter theories. The highest contact angle, 140 degrees , was observed for PP molded with the AAO mold insert with 30-nm pore diameter. The Cassie-Baxter theory showed better fit than the Wenzel theory to the experimental values. With the optimal AAO mask, the nanofeatures in the molded PP pieces were 100 nm high. In explanation of this finding, it is suggested that some sticking and stretching of the nanofeatures occurs during the molding. Increase in the mold temperature increased the contact angle.

Flow-field characteristics of high-temperature annular buoyant jets and their development laws influenced by ventilation system.

PubMed

Wang, Yi; Huang, Yanqiu; Liu, Jiaping; Wang, Hai; Liu, Qiuhan

2013-01-01

The flow-field characteristics of high-temperature annular buoyant jets as well as the development laws influenced by ventilation system were studied using numerical methods to eliminate the pollutants effectively in this paper. The development laws of high-temperature annular buoyant jets were analyzed and compared with previous studies, including radial velocity distribution, axial velocity and temperature decay, reattachment position, cross-section diameter, volumetric flow rate, and velocity field characteristics with different pressures at the exhaust hood inlet. The results showed that when the ratio of outer diameter to inner diameter of the annulus was smaller than 5/2, the flow-field characteristics had significant difference compared to circular buoyant jets with the same outer diameter. For similar diameter ratios, reattachment in this paper occurred further downstream in contrast to previous study. Besides, the development laws of volumetric flow rate and cross-section diameter were given with different initial parameters. In addition, through analyzing air distribution characteristics under the coupling effect of high-temperature annular buoyant jets and ventilation system, it could be found that the position where maximum axial velocity occurred was changing gradually when the pressure at the exhaust hood inlet changed from 0 Pa to -5 Pa.

Flow-Field Characteristics of High-Temperature Annular Buoyant Jets and Their Development Laws Influenced by Ventilation System

PubMed Central

Liu, Jiaping; Wang, Hai; Liu, Qiuhan

2013-01-01

The flow-field characteristics of high-temperature annular buoyant jets as well as the development laws influenced by ventilation system were studied using numerical methods to eliminate the pollutants effectively in this paper. The development laws of high-temperature annular buoyant jets were analyzed and compared with previous studies, including radial velocity distribution, axial velocity and temperature decay, reattachment position, cross-section diameter, volumetric flow rate, and velocity field characteristics with different pressures at the exhaust hood inlet. The results showed that when the ratio of outer diameter to inner diameter of the annulus was smaller than 5/2, the flow-field characteristics had significant difference compared to circular buoyant jets with the same outer diameter. For similar diameter ratios, reattachment in this paper occurred further downstream in contrast to previous study. Besides, the development laws of volumetric flow rate and cross-section diameter were given with different initial parameters. In addition, through analyzing air distribution characteristics under the coupling effect of high-temperature annular buoyant jets and ventilation system, it could be found that the position where maximum axial velocity occurred was changing gradually when the pressure at the exhaust hood inlet changed from 0 Pa to −5 Pa. PMID:24000278

High-aspect-ratio and highly ordered 15-nm porous alumina templates.

PubMed

Martín, Jaime; Manzano, Cristina V; Caballero-Calero, Olga; Martín-González, Marisol

2013-01-01

Ordered anodic aluminum oxide (AAO) templates with pores <15 nm in diameter and an aspect ratio (length-to-diameter ratio) above 3 × 10(3) have been fabricated using a nonlithographic approach; specifically, by anodizing aluminum in an ethylene-glycol-containing sulfuric acid electrolyte. The pores are the smallest in diameter reported for a self-ordered AAO without pore aspect-ratio limitations and good ordering, which opens up the possibility of obtaining nanowire arrays in the quantum confinement regime that is of interest for efficient thermoelectric generators. The effect of the ethylene glycol addition on both the pore diameter and the ordering is evaluated and discussed. Moreover, 15-nm-diameter Bi(2)Te(3) and poly(3-hexyl thiophene) (P3HT) nanowires have been prepared using these AAO templates. As known, Bi(2)Te(3) is currently the most efficient thermoelectric bulk material for room-temperature operations and, according with theory, its Seebeck coefficient should be increased when it is confined to nanowires with diameters close to 10 nm. On the other hand, P3HT is one of the main candidates for integrating organic photovoltaic and thermoelectric devices, and its properties are also proposed to increase when it is confined to nanoscale structures, mainly due to molecular orientation effects.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wang, Bochong; Kubota, Hitoshi, E-mail: hit-kubota@aist.go.jp; Yakushiji, Kay

The dependence on diameter of the emission power in MgO-based nano-pillar spin torque oscillators (STOs) was systematically investigated. A maximum emission power of over 2.5 μW was obtained around 300 nm in diameter, which is the largest reported to date among the out-of-plane precession STOs. By analyzing physical quantities, precession cone angle of the free-layer magnetization was evaluated. In the diameter range below 300 nm, the increase in power was mainly due to the increase of the injected current. The power decrease above 300 nm is possibly attributed to the decrease in the averaged precession cone angle, suggesting spatial phase difference of magnetization precession.more » This study provides the method for estimating the optimum STO diameter, which is of great importance in practical use.« less

Fresnel Lens Characterization for Potential Use in an Unpiloted Atmospheric Vehicle DIAL Receiver System

NASA Technical Reports Server (NTRS)

Fastig, Shlomo; Deoung, Russell J.

1998-01-01

Acrylic plastic Fresnel lenses are very light and can have large diameters. Such lenses could be used in lidar telescope receivers if the focal spot is not too large or distorted. This research effort characterizes the focal spot diameter produced by a Fresnel lens with a diameter of 30.5 cm (12 in.). It was found that the focal spot diameter varied from 1.2 mm at 750 nm to 1.6 mm at 910 nm. The focal spot was irregular and not easily described by a Gaussian profile.

Spontaneous and controlled-diameter synthesis of single-walled and few-walled carbon nanotubes

NASA Astrophysics Data System (ADS)

Inoue, Shuhei; Lojindarat, Supanat; Kawamoto, Takahiro; Matsumura, Yukihiko; Charinpanitkul, Tawatchai

2018-05-01

In this study, we explored the spontaneous and controlled-diameter growth of carbon nanotubes. We evaluated the effects of catalyst density, reduction time, and a number of catalyst coating on the substrate (for multi-walled carbon nanotubes) on the diameter of single-walled carbon nanotubes and the number of layers in few-walled carbon nanotubes. Increasing the catalyst density and reduction time increased the diameters of the carbon nanotubes, with the average diameter increasing from 1.05 nm to 1.86 nm for single-walled carbon nanotubes. Finally, we succeeded in synthesizing a significant double-walled carbon nanotube population of 24%.

Gold Nanoparticles of Diameter 13 nm Induce Apoptosis in Rabbit Articular Chondrocytes

NASA Astrophysics Data System (ADS)

Huang, Hao; Quan, Ying-yao; Wang, Xiao-ping; Chen, Tong-sheng

2016-05-01

Gold nanoparticles (AuNPs) have been widely used in biomedical science including antiarthritic agents, drug loading, and photothermal therapy. In this report, we studied the effects of AuNPs with diameters of 3, 13, and 45 nm, respectively, on rabbit articular chondrocytes. AuNPs were capped with citrate and their diameter and zeta potential were measured by dynamic light scattering (DLS). Cell viability was evaluated by Cell Counting Kit-8 (CCK-8) assay after the rabbit articular chondrocytes were pre-incubated with 3, 13, and 45 nm AuNPs, respectively, for 24 h. Flow cytometry (FCM) analysis with annexin V/propidium iodide (PI) double staining and fluorescence imaging with Hoechst 33258 staining were used to determine the fashion of AuNPs-induced chondrocyte death. Further, 13 nm AuNPs (2 nM) significantly induced chondrocyte death accompanying apoptotic characteristics including mitochondrial damage, externalization of phosphatidylserine and nuclear concentration. However, 3 nm AuNPs (2 nM) and 45 nm (0.02 nM) AuNPs did not induce cytotoxicity in chondrocytes. Although 13 nm AuNPs (2 nM) increased the intracellular reactive oxygen species (ROS) level, pretreatment with Nacetyl cysteine (NAC), a ROS scavenger, did not prevent the cytotoxicity induced by 13 nm AuNPs, indicating that 13 nm AuNPs (2 nM) induced ROS-independent apoptosis in chondrocytes. These results demonstrate the size-dependent cytotoxicity of AuNPs in chondrocytes, which must be seriously considered when using AuNPs for treatment of osteoarthritis (OA).

Giant Syncytia and Virus-Like Particles in Ovarian Carcinoma Cells Isolated from Ascites Fluid

PubMed Central

Rakowicz-Szulczynska, Eva M.; McIntosh, David G.; Smith, McClure L.

1999-01-01

Ovarian cancer cells were isolated from ascites fluid of 30 different patients diagnosed with cystadenocarcinoma of ovaries. Large colonies of malignant ASC cells were observed during the first week of cell growth in vitro. Colony formation was followed by fusion of cells and formation of large multinucleated and highly vacuolated syncytia. In contrast, cells isolated from the ascites fluid produced by patients with benign mucinous cystadenoma of ovaries did not form syncytia. Nonmalignant Brenner tumor cells, isolated from the ascites fluid, also did not form syncytia. Syncytia, but not the nonmalignant tumor cells, were immunofluorescence stained with an anti-human immunodeficiency virus type 1 (HIV-1) gp120 monoclonal antibody (MAb) and MAb RAK-BrI. Both MAbs recognized cancer-associated antigens RAK (for Rakowicz markers) p120, p42, and p25. Exposure of ASC cells to either the anti-HIV-1 gp120 MAb or MAb RAK-BrI inhibited syncytium formation. PCR with HIV-1 Env-derived primers revealed DNA sequences with over 90% homology to HIV-1 gp41 in syncytia and in ovarian cancer cells but not in normal ovary cells. Electron microscopic analysis revealed viral particles, hexagonal in shape (90 nm in diameter), with a dense central core surrounded by an inner translucent capsid and dense outer shell with projections. Negative staining detected membrane-covered particles (100 to 110 nm in diameter) in the cell culture medium. Incubation of normal breast cells with viral particles resulted in drastic morphological changes and syncytium formation by the transformed breast cells. The cytopathic effects of the identified virus resembled those of spumaviruses, which, in addition to their epitopic and genetic homology to HIV-1, might suggest a common phylogeny. PMID:9874674

Giant syncytia and virus-like particles in ovarian carcinoma cells isolated from ascites fluid.

PubMed

Rakowicz-Szulczynska, E M; McIntosh, D G; Smith, M L

1999-01-01

Ovarian cancer cells were isolated from ascites fluid of 30 different patients diagnosed with cystadenocarcinoma of ovaries. Large colonies of malignant ASC cells were observed during the first week of cell growth in vitro. Colony formation was followed by fusion of cells and formation of large multinucleated and highly vacuolated syncytia. In contrast, cells isolated from the ascites fluid produced by patients with benign mucinous cystadenoma of ovaries did not form syncytia. Nonmalignant Brenner tumor cells, isolated from the ascites fluid, also did not form syncytia. Syncytia, but not the nonmalignant tumor cells, were immunofluorescence stained with an anti-human immunodeficiency virus type 1 (HIV-1) gp120 monoclonal antibody (MAb) and MAb RAK-BrI. Both MAbs recognized cancer-associated antigens RAK (for Rakowicz markers) p120, p42, and p25. Exposure of ASC cells to either the anti-HIV-1 gp120 MAb or MAb RAK-BrI inhibited syncytium formation. PCR with HIV-1 Env-derived primers revealed DNA sequences with over 90% homology to HIV-1 gp41 in syncytia and in ovarian cancer cells but not in normal ovary cells. Electron microscopic analysis revealed viral particles, hexagonal in shape (90 nm in diameter), with a dense central core surrounded by an inner translucent capsid and dense outer shell with projections. Negative staining detected membrane-covered particles (100 to 110 nm in diameter) in the cell culture medium. Incubation of normal breast cells with viral particles resulted in drastic morphological changes and syncytium formation by the transformed breast cells. The cytopathic effects of the identified virus resembled those of spumaviruses, which, in addition to their epitopic and genetic homology to HIV-1, might suggest a common phylogeny.

Photonic crystal fiber monitors for intracellular ice formation

NASA Astrophysics Data System (ADS)

Battinelli, Emily; Reimlinger, Mark; Wynne, Rosalind

2012-04-01

An all-silica steering wheel photonic crystal fiber (SW-PCF) device with real-time analysis for cellular temperature sensing is presented. Results are provided for water-filled SW-PCF fibers experiencing cooling down near -40°C. Cellular temperature sensors with fast response times are of interest particularly to the study of cryopreservation, which has been influential in applications such as tissue preservation, food quality control, genetic engineering, as well as drug discovery and in- vitro toxin testing. Results of this investigation are relevant to detection of intracellular ice formation (IIF) and better understanding cell freezing at very low temperatures. IIF detection is determined as a function of absorption occurring within the core of the SW-PCF. The SW-PCF has a 3.3μm core diameter, 125μm outer diameter and steering wheel-like air hole pattern with triangular symmetry, with a 20μm radius. One end of a 0.6m length of the SW-PCF is placed between two thermoelectric coolers, filled with ~0.1μL water. This end is butt coupled to a 0.5m length of single mode fiber (SMF), the distal end of the fiber is then inserted into an optical spectrum analyzer. A near-IR light source is guided through the fiber, such that the absorption of the material in the core can be measured. Spectral characteristics demonstrated by the optical absorption of the water sample were present near the 1300-1700nm window region with strongest peaks at 1350, 1410 and 1460nm, further shifting of the absorption peaks is possible at cryogenic temperatures making this device suitable for IIF monitoring applications.

Conformation of chromatin oligomers. A new argument for a change with the hexanucleosome.

PubMed

Marion, C; Bezot, P; Hesse-Bezot, C; Roux, B; Bernengo, J C

1981-11-01

Quasielastic laser light scattering measurements have been made on chromatin oligomers to obtain information on the transition in their electrooptical properties, previously observed for the hexameric structures [Marion, C. and Roux, B. (1978) Nucleic Acids Res. 5, 4431-4449]. Translational diffusion coefficients were determined for mononucleosomes to octanucleosomes containing histone H1 over a range of ionic strength. At high ionic strength, oligomers show a linear dependence of the logarithm of diffusion coefficient upon the logarithm of number of nucleosomes. At low ionic strength a change occurs between hexamer and heptamer. Our results agree well with the recent sedimentation data of Osipova et al. [Eur. J. Biochem. (1980) 113, 183-188] and of Butler and Thomas [J. Mol. Biol. (1980) 140, 505-529] showing a change in stability with hexamer. Various models for the arrangements of nucleosomes in the superstructure of chromatin are discussed. All calculations clearly indicate a conformational change with the hexanucleosome and the results suggest that, at low ionic strength, the chromatin adopts a loosely helical structure of 28-nm diameter and 22-nm pitch. These results are also consistent with a discontinuity every sixth nucleosome, corresponding to a turn of the helix. This discontinuity may explain the recent electric dichroism data of Lee et al. [Biochemistry (1981) 20, 1438-1445]. The hexanucleosome structure which we have previously suggested, with the faces of nucleosomes arranged radially to the helical axis has been recently confirmed by Mc Ghee et al. [Cell (1980) 22, 87-96]. With an increase of ionic strength, the helix becomes more regular and compact with a slightly reduced outer diameter and a decreased pitch, the dimensions resembling those proposed for solenoid models.

Sodium chloride-catalyzed oxidation of multiwalled carbon nanotubes for environmental benefit.

PubMed

Endo, Morinobu; Takeuchi, Kenji; Tajiri, Takeyuki; Park, Ki Chul; Wang, Feng; Kim, Yoong-Ahm; Hayashi, Takuya; Terrones, Mauricio; Dresselhaus, Mildred S

2006-06-22

A sodium chloride (NaCl) catalyst (0.1 w/w %) lowers the oxidation temperature of graphitized multiwalled carbon nanotubes: MWCNT-20 (diameter: 20-70 nm) and MWCNT-80 (diameter: 80-150 nm). The analysis of the reaction kinetics indicates that the oxidation of MWCNT-20 and MWCNT-80 mixed with no NaCl exhibits single reaction processes with activation energies of E(a) = 159 and 152 kJ mol(-1), respectively. The oxidation reaction in the presence of NaCl is shown to consist of two different reaction processes, that is, a first reaction and a second reaction process. The first reaction process is dominant at a low temperature of around 600 degrees C, while the second reaction process becomes more dominant than the first one in a higher temperature region. The activation energies of the first reaction processes (MWCNT-20: E(a1) = 35.7 kJ mol(-1); MWCNT-80: E(a1) = 43.5 kJ mol(-1)) are much smaller than those of the second reaction processes (MWCNT-20: E(a2) = 170 kJ mol(-1); MWCNT-80: E(a2) = 171 kJ mol(-1)). The comparison of the kinetic parameters and the results of the spectroscopic and microscopic analyses imply that the lowering of the oxidation temperature in the presence of NaCl results from the introduction of disorder into the graphitized MWCNTs (during the first reaction process), thus increasing the facility of the oxidation reaction of the disorder-induced nanotubes (in the second reaction process). It is found that the larger nanopits and cracks on the outer graphitic layers are caused by the catalytic effect of NaCl. Therefore, the NaCl-mixed samples showed more rapid and stronger oxidation compared with that of the nonmixed samples at the same residual quantity.

Endocytic pathways involved in PLGA nanoparticle uptake by grapevine cells and role of cell wall and membrane in size selection.

PubMed

Palocci, Cleofe; Valletta, Alessio; Chronopoulou, Laura; Donati, Livia; Bramosanti, Marco; Brasili, Elisa; Baldan, Barbara; Pasqua, Gabriella

2017-12-01

PLGA NPs' cell uptake involves different endocytic pathways. Clathrin-independent endocytosis is the main internalization route. The cell wall plays a more prominent role than the plasma membrane in NPs' size selection. In the last years, many studies on absorption and cell uptake of nanoparticles by plants have been conducted, but the understanding of the internalization mechanisms is still largely unknown. In this study, polydispersed and monodispersed poly(lactic-co-glycolic) acid nanoparticles (PLGA NPs) were synthesized, and a strategy combining the use of transmission electron microscopy (TEM), confocal analysis, fluorescently labeled PLGA NPs, a probe for endocytic vesicles (FM4-64), and endocytosis inhibitors (i.e., wortmannin, ikarugamycin, and salicylic acid) was employed to shed light on PLGA NP cell uptake in grapevine cultured cells and to assess the role of the cell wall and plasma membrane in size selection of PLGA NPs. The ability of PLGA NPs to cross the cell wall and membrane was confirmed by TEM and fluorescence microscopy. A strong adhesion of PLGA NPs to the outer side of the cell wall was observed, presumably due to electrostatic interactions. Confocal microscopy and treatment with endocytosis inhibitors suggested the involvement of both clathrin-dependent and clathrin-independent endocytosis in cell uptake of PLGA NPs and the latter appeared to be the main internalization pathway. Experiments on grapevine protoplasts revealed that the cell wall plays a more prominent role than the plasma membrane in size selection of PLGA NPs. While the cell wall prevents the uptake of PLGA NPs with diameters over 50 nm, the plasma membrane can be crossed by PLGA NPs with a diameter of 500-600 nm.

Infrared glass fiber cables for CO laser medical applications

NASA Astrophysics Data System (ADS)

Arai, Tsunenori; Mizuno, Kyoichi; Sensaki, Koji; Kikuchi, Makoto; Watanabe, Tamishige; Utsumi, Atsushi; Takeuchi, Kiyoshi; Akai, Yoshiro

1993-05-01

We developed the medical fiber cables which were designed for CO laser therapy, i.e., angioplasty and endoscopic therapy. As-S chalcogenide glass fibers were used for CO laser delivery. A 230 micrometers core-diameter fiber was used for the angioplasty laser cable. The outer diameter of this cable was 600 micrometers . The total length and insertion length of the angioplasty laser cable were 2.5 m and 1.0 m, respectively. Typically, 2.0 W of fiber output was used in the animal experiment in vivo for the ablation of the model plaque which consisted of human atheromatous aorta wall. The transmission of the angioplasty laser cable was approximately 35%, because the reflection loss occurred at both ends of the fiber and window. Meanwhile, the core diameter of the energy delivery fiber for the endoscopic therapy was 450 micrometers . The outer diameter of this cable was 1.7 mm. Approximately 4.5 W of fiber output was used for clinical treatment of pneumothorax through a pneumoscope. Both types of the cables had the ultra-thin thermocouples for temperature monitoring at the tip of the cables. This temperature monitoring was extremely useful to prevent the thermal destruction of the fiber tip. Moreover, the As-S glass fibers were completely sealed by the CaF2 windows and outer tubes. Therefore, these cables were considered to have sufficient safety properties for medical applications. These laser cables were successfully used for the in vivo animal experiments and/or actual clinical therapies.

A new technique for the diagnosis of acute appendicitis: abdominal CT with compression to the right lower quadrant.

PubMed

Kılınçer, Abidin; Akpınar, Erhan; Erbil, Bülent; Ünal, Emre; Karaosmanoğlu, Ali Devrim; Kaynaroğlu, Volkan; Akata, Deniz; Özmen, Mustafa

2017-08-01

To determine the diagnostic accuracy of abdominal CT with compression to the right lower quadrant (RLQ) in adults with acute appendicitis. 168 patients (age range, 18-78 years) were included who underwent contrast-enhanced CT for suspected appendicitis performed either using compression to the RLQ (n = 71) or a standard protocol (n = 97). Outer diameter of the appendix, appendiceal wall thickening, luminal content and associated findings were evaluated in each patient. Kruskal-Wallis, Fisher's and Pearson's chi-squared tests were used for statistical analysis. There was no significant difference in the mean outer diameter (MOD) between compression CT scans (10.6 ± 1.9 mm) and standard protocol (11.2 ± 2.3 mm) in patients with acute appendicitis (P = 1). MOD was significantly lower in the compression group (5.2 ± 0.8 mm) compared to the standard protocol (6.5 ± 1.1 mm) (P < 0.01) in patients without appendicitis. A cut-off value of 6.75 mm for the outer diameter of the appendix was found to be 100% sensitive in the diagnosis of acute appendicitis for both groups. The specificity was higher for compression CT technique (67.7 vs. 94.9%). Normal appendix diameter was significantly smaller in the compression-CT group compared to standard-CT group, increasing diagnostic accuracy of abdominal compression CT. • Normal appendix diameter is significantly smaller in compression CT. • Compression could force contrast material to flow through the appendiceal lumen. • Compression CT may be a CT counterpart of graded compression US.

Nanohole and dot patterning processes on quartz substrate by R-θ electron beam lithography and nanoimprinting

NASA Astrophysics Data System (ADS)

Watanabe, Tsuyoshi; Taniguchi, Kazutake; Suzuki, Kouta; Iyama, Hiromasa; Kishimoto, Shuji; Sato, Takashi; Kobayashi, Hideo

2016-06-01

Fine hole and dot patterns with bit pitches (bp’s) of less than 40 nm were fabricated in the circular band area of a quartz substrate by R-θ electron beam lithography (EBL), reactive ion etching (RIE), and nanoimprinting. These patterning processes were studied to obtain minimum pitch sizes of hole and dot patterns without pattern collapse. The patterning on the circular band was aimed to apply these patterning processes to future high-density bit-patterned media (BPM) for hard disk drive (HDD) and permanent memory for the long life archiving of digital data. In hole patterning, a minimum-22-nm-bp and 8.2-nm-diameter pattern (1.3 Tbit/in.2) was obtained on a quartz substrate by optimizing the R-θ EBL and RIE processes. Dot patterns were replicated on another quartz substrate by nanoimprinting using a hole-patterned quartz substrate as a master mold followed by RIE. In dot patterning, a minimum-30-nm-bp and 18.5-nm-diameter pattern (0.7 Tbit/in.2) was obtained by introducing new descum conditions. It was observed that the minimum bp of successful patterning increased as the fabrication process proceeded, i.e., from 20 nm bp in the first EBL process to 30 nm bp in the last quartz dot patterning process. From the measured diameters of the patterns, it was revealed that pattern collapse was apt to occur when the value of average diameter plus 3 sigma of diameter was close to the bp. It was suggested that multiple fabrication processes caused the degradation of pattern quality; therefore, hole patterning is more suitable than dot patterning for future applications owing to the lower quality degradation by its simple fabrication process.

Polyhedral protein cages encase synaptic vesicles and participate in their attachment to the active zone.

PubMed

Zampighi, G A; Fisher, R S

1997-08-01

In an effort to elucidate the interactions between synaptic vesicles and the membrane of the active zone, we have investigated the structure of interneuronal asymmetric synapses in the neocortex of adult rats using thin-sectioning, freeze-fracture, and negative staining electron microscopy. We identified three subtypes of spherical synaptic vesicles. Type I were agranular vesicles of 47.5 +/- 3.8 nm (mean SD, n = 24) in diameter usually seen aggregated in clusters in the presynaptic bouton. Type II synaptic vesicles were composed of a approximately 45-nm-diameter lipid bilayer sphere encased in a cage 77 +/- 4.6 nm (mean SD, n = 42) in diameter. The cage was composed of open-faced pentamers 20-22 nm/side arranged as a regular polyhedron. Type II caged vesicles were found in clusters at the boutons, adhered to the active zone, and were also present in axons. Type III synaptic vesicles appeared as electron-dense spheres 60-75 nm in diameter abutted to the membrane of the active zone. Clathrin-coated vesicles and pits of 116.6 +/- 9 nm (mean SD, n = 14) in diameter were also present in both the pre- and postsynaptic sides. Freeze-fracture showed that some intrinsic membrane proteins in the active zone were arranged as pentamers exhibiting the same dimension of those forming cages (approximately 22 nm/side). From these data, we concluded that: (a) the presynaptic bouton contains a heterogeneous population of "caged" and "plain" synaptic vesicles and (b) type II synaptic vesicles bind to receptors in the active zone. Therefore, current models of transmitter release should take into account the substantial heterogeneity of the vesicle population and the binding of vesicular cages to the membrane of the active zone.

Herpesvirus gB-induced fusion between the virion envelope and outer nuclear membrane during virus egress is regulated by the viral US3 kinase.

PubMed

Wisner, Todd W; Wright, Catherine C; Kato, Akihisa; Kawaguchi, Yasushi; Mou, Fan; Baines, Joel D; Roller, Richard J; Johnson, David C

2009-04-01

Herpesvirus capsids collect along the inner surface of the nuclear envelope and bud into the perinuclear space. Enveloped virions then fuse with the outer nuclear membrane (NM). We previously showed that herpes simplex virus (HSV) glycoproteins gB and gH act in a redundant fashion to promote fusion between the virion envelope and the outer NM. HSV mutants lacking both gB and gH accumulate enveloped virions in herniations, vesicles that bulge into the nucleoplasm. Earlier studies had shown that HSV mutants lacking the viral serine/threonine kinase US3 also accumulate herniations. Here, we demonstrate that HSV gB is phosphorylated in a US3-dependent manner in HSV-infected cells, especially in a crude nuclear fraction. Moreover, US3 directly phosphorylated the gB cytoplasmic (CT) domain in in vitro assays. Deletion of gB in the context of a US3-null virus did not add substantially to defects in nuclear egress. The majority of the US3-dependent phosphorylation of gB involved the CT domain and amino acid T887, a residue present in a motif similar to that recognized by US3 in other proteins. HSV recombinants lacking gH and expressing either gB substitution mutation T887A or a gB truncated at residue 886 displayed substantial defects in nuclear egress. We concluded that phosphorylation of the gB CT domain is important for gB-mediated fusion with the outer NM. This suggested a model in which the US3 kinase is incorporated into the tegument layer (between the capsid and envelope) in HSV virions present in the perinuclear space. By this packaging, US3 might be brought close to the gB CT tail, leading to phosphorylation and triggering fusion between the virion envelope and the outer NM.

Nanowire sensors and arrays for chemical/biomolecule detection

NASA Technical Reports Server (NTRS)

Yun, Minhee; Lee, Choonsup; Vasquez, Richard P.; Ramanathan, K.; Bangar, M. A.; Chen, W.; Mulchandan, A.; Myung, N. V.

2005-01-01

We report electrochemical growth of single nanowire based sensors using e-beam patterned electrolyte channels, potentially enabling the controlled fabrication of individually addressable high density arrays. The electrodeposition technique results in nanowires with controlled dimensions, positions, alignments, and chemical compositions. Using this technique, we have fabricated single palladium nanowires with diameters ranging between 75 nm and 300 nm and conducting polymer nanowires (polypyrrole and polyaniline) with diameters between 100 nm and 200 nm. Using these single nanowires, we have successfully demonstrated gas sensing with Pd nanowires and pH sensing with polypirrole nanowires.

Role of Plasma Temperature and Residence Time in Stagnation Plasma Synthesis of c-BN Nanopowders

DTIC Science & Technology

2013-01-01

outer diameter of 15mm. A center injection 19 nozzle of 1.4mm diameter is implemented for precursor introduction. Plasma and sheath gas ... Gas Phase Synthesis of Nanoparticles..................................................... 5 2.2 Cubic Boron Nitride Synthesis...11 2.2.4 Effects of gas composition ............................................................................................ 11

46 CFR 169.563 - Firehose.

Code of Federal Regulations, 2012 CFR

2012-10-01

... or equivalent of not over 11/2 inch diameter or garden hose of not less than 5/8 inch nominal inside diameter. If garden hose is used, it must be of a good commercial grade constructed of an inner rubber tube, plies of braided cotton reinforcement and an outer rubber cover, or of equivalent material, and must be...

46 CFR 169.563 - Firehose.

Code of Federal Regulations, 2014 CFR

2014-10-01

... or equivalent of not over 11/2 inch diameter or garden hose of not less than 5/8 inch nominal inside diameter. If garden hose is used, it must be of a good commercial grade constructed of an inner rubber tube, plies of braided cotton reinforcement and an outer rubber cover, or of equivalent material, and must be...

46 CFR 169.563 - Firehose.

Code of Federal Regulations, 2013 CFR

2013-10-01

... or equivalent of not over 11/2 inch diameter or garden hose of not less than 5/8 inch nominal inside diameter. If garden hose is used, it must be of a good commercial grade constructed of an inner rubber tube, plies of braided cotton reinforcement and an outer rubber cover, or of equivalent material, and must be...

Extrusion of metal oxide superconducting wire, tube or ribbon

DOEpatents

Dusek, Joseph T.

1993-10-05

A process for extruding a superconducting metal oxide composition YBa.sub.2 Cu.sub.3 O.sub.7-x provides a wire (tube or ribbon) having a cohesive mass and a degree of flexibility together with enhanced electrical properties. Wire diameters in the range of 6-85 mils have been produced with smaller wires on the order of 10 mils in diameter exhibiting enhanced flexibility for forming braided, or multistrand, configurations for greater current carrying capacity. The composition for extrusion contains a polymeric binder to provide a cohesive mass to bind the particles together during the extrusion process with the binder subsequently removed at lower temperatures during sintering. The composition for extrusion further includes a deflocculent, an organic plasticizer and a solvent which also are subsequently removed during sintering. Electrically conductive tubing with an inner diameter of 52 mil and an outer diameter of 87-355 mil has also been produced. Flat ribbons have been produced in the range of 10-125 mil thick by 100-500 mil wide. The superconducting wire, tube or ribbon may include an outer ceramic insulating sheath co-extruded with the wire, tubing or ribbon.

Extrusion of metal oxide superconducting wire, tube or ribbon

DOEpatents

Dusek, Joseph T.

1993-01-01

A process for extruding a superconducting metal oxide composition YBa.sub.2 Cu.sub.3 O.sub.7-x provides a wire (tube or ribbon) having a cohesive mass and a degree of flexibility together with enhanced electrical properties. Wire diameters in the range of 6-85 mils have been produced with smaller wires on the order of 10 mils in diameter exhibiting enhanced flexibility for forming braided, or multistrand, configurations for greater current carrying capacity. The composition for extrusion contains a polymeric binder to provide a cohesive mass to bind the particles together during the extrusion process with the binder subsequently removed at lower temperatures during sintering. The composition for extrusion further includes a deflocculent, an organic plasticizer and a solvent which also are subsequently removed during sintering. Electrically conductive tubing with an inner diameter of 52 mil and an outer diameter of 87-355 mil has also been produced. Flat ribbons have been produced in the range of 10-125 mil thick by 100-500 mil wide. The superconducting wire, tube or ribbon may include an outer ceramic insulating sheath co-extruded with the wire, tubing or ribbon.

Low-temperature synthesis of single-walled carbon nanotubes with a narrow diameter distribution using size-classified catalyst nanoparticles

NASA Astrophysics Data System (ADS)

Kondo, Daiyu; Sato, Shintaro; Awano, Yuji

2006-05-01

Single-walled carbon nanotubes (SWNTs) with a narrow diameter distribution have been synthesized by hot-filament chemical vapor deposition using acetylene at 590 °C. Iron nanoparticles with diameters of 1.6, 2.0, 2.5, 5.0 and 10 nm (standard deviation: ≈10%) obtained with a differential mobility analyzer were used as a catalyst without any supporting materials on a substrate. SWNTs were obtained from 2.0 nm or smaller particles. The ratio of G band to D band in Raman spectra was as high as 35 without purification, indicating that high-quality SWNTs were synthesized. The SWNT diameters correlated with the particle diameters, demonstrating diameter-controlled SWNT growth.

50 CFR 216.254 - Mitigation.

Code of Federal Regulations, 2010 CFR

2010-10-01

... safety for marine mammals with a radius of no less than 5 nm (9.3 km) for single bombs and 10 nm (18.5 km) for double bombs and a buffer zone from the outer edge of the safety zone with a radius of at least 2.5 nm (4.6 km) for single bombs and 5 nm (18.5 km) for double bombs. (b) Prior to a JASSM or SDB...

Gallium ion-assisted room temperature synthesis of small-diameter ZnO nanorods.

PubMed

Cho, Seungho; Kim, Semi; Lee, Kun-Hong

2011-09-15

We report a method for synthesizing small-diameter ZnO nanorods at room temperature (20 °C), under normal atmospheric pressure (1 atm), and using a relatively short reaction time (1 h) by adding gallium salts to the reaction solution. The ZnO nanorods were, on average, 92 nm in length and 9 nm in diameter and were single crystalline in nature. Quantitative analyses revealed that gallium atoms were not incorporated into the synthesized nanocrystals. On the basis of the experimental results, we propose a mechanism for the formation of small-diameter ZnO nanorods in the presence of gallium ions. The optical properties were probed by UV-Vis diffuse reflectance spectroscopy. The absorption band of the small-diameter ZnO nanorods was blue-shifted relative to the absorption band of the ~230 nm diameter ZnO nanorods (control samples). Control experiments demonstrated that the absence of metal ion-containing precipitants (except ZnO) at room temperature is essential, and that the ZnO nanorod diameter distributions were narrow for the stirred reaction solution and broad when prepared without stirring. Copyright © 2011 Elsevier Inc. All rights reserved.

Rotational Splittings of Acoustic Modes in an Experimental Model of a Planetary Core

NASA Astrophysics Data System (ADS)

Adams, M. M.; Stone, D.; Lathrop, D. P.

2014-12-01

Planetary zonal flows can be probed in principle using the tools of helioseismology. We explore this technique using laboratory experiments where the measurement of zonal flows is also of geophysical relevance. The experiments are carried out in a device with a geometry similar to that of Earth's core. It consists of a 60 cm diameter outer spherical shell concentric with a 20 cm diameter inner sphere. Air between the inner sphere and outer shell is used as the working fluid. A turbulent shear flow is driven in the air by independently rotating the inner sphere and outer shell. Acoustic modes are excited in the vessel with a speaker, and microphones are used to measure the rotational splittings of these modes. The radial profile of azimuthal velocities is inferred from these splittings, in an approach analogous to that used in helioseismology to determine solar velocity profiles. By varying the inner and outer rotation rates, different turbulent states can be investigated. Comparison is made to previous experimental investigations of turbulent spherical Couette flow. These experiments also serve as a test of this diagnostic, which may be used in the future in liquid sodium experiments, providing information on zonal flows in hydromagnetic experiments.

Aerosol Inlet Characterization Experiment Report

DOE Office of Scientific and Technical Information (OSTI.GOV)

Bullard, Robert L.; Kuang, Chongai; Uin, Janek

2017-05-01

The U.S. Department of Energy (DOE) Atmospheric Radiation Measurement (ARM) Climate Research Facility Aerosol Observation System inlet stack was characterized for particle penetration efficiency from 10 nm to 20 μm in diameter using duplicate scanning mobility particle sizers (10 nm-450 nm), ultra-high-sensitivity aerosol spectrometers (60 nm-μm), and aerodynamic particle sizers (0.5 μm-20 μm). Results show good model-measurement agreement and unit transmission efficiency of aerosols from 10 nm to 4 μm in diameter. Large uncertainties in the measured transmission efficiency exist above 4 μm due to low ambient aerosol signal in that size range.

A multimodal spectroscopy system for real-time disease diagnosis

NASA Astrophysics Data System (ADS)

Šćepanović, Obrad R.; Volynskaya, Zoya; Kong, Chae-Ryon; Galindo, Luis H.; Dasari, Ramachandra R.; Feld, Michael S.

2009-04-01

The combination of reflectance, fluorescence, and Raman spectroscopy—termed multimodal spectroscopy (MMS)—provides complementary and depth-sensitive information about tissue composition. As such, MMS is a promising tool for disease diagnosis, particularly in atherosclerosis and breast cancer. We have developed an integrated MMS instrument and optical fiber spectral probe for simultaneous collection of all three modalities in a clinical setting. The MMS instrument multiplexes three excitation sources, a xenon flash lamp (370-740 nm), a nitrogen laser (337 nm), and a diode laser (830 nm), through the MMS probe to excite tissue and collect the spectra. The spectra are recorded on two spectrograph/charge-coupled device modules, one optimized for visible wavelengths (reflectance and fluorescence) and the other for the near-infrared (Raman), and processed to provide diagnostic parameters. We also describe the design and calibration of a unitary MMS optical fiber probe 2 mm in outer diameter, containing a single appropriately filtered excitation fiber and a ring of 15 collection fibers, with separate groups of appropriately filtered fibers for efficiently collecting reflectance, fluorescence, and Raman spectra from the same tissue location. A probe with this excitation/collection geometry has not been used previously to collect reflectance and fluorescence spectra, and thus physical tissue models ("phantoms") are used to characterize the probe's spectroscopic response. This calibration provides probe-specific modeling parameters that enable accurate extraction of spectral parameters. This clinical MMS system has been used recently to analyze artery and breast tissue in vivo and ex vivo.

Hydrocode Simulations of the Chesapeake Bay Impact

NASA Technical Reports Server (NTRS)

Collins, G. S.; Melosh, H. J.

2004-01-01

The Chesapeake Bay Impact Crater (CBIC) formed about 35 million years ago (late Eocene), in a shallow marine environment (400-600 m water depth). The crater is complex and developed in a multi-layer, rheologically-variable target that comprised 400-1000 meters of soft, water-saturated sediments overlying crystalline basement. Seismic reflection data illustrates that the Chesapeake Bay crater morphology - often described as an "inverted sombrero" - is similar to other marine-target impact craters. It consists of a approx. 1 - 1.5-km deep, highly disturbed central crater, surrounded by a shallower, less deformed basin. The inner crater has a diameter of approx. 40 km; the edge of the outer basin extends to 85-km diameter. The morphological divide between the inner and outer crater is termed the inner ring or peak ring. Little is known about the nature of the inner ring. Seismic reflection data show that the underlying basement is modestly uplifted; however, it is unclear whether the pristine surface expression of the inner ring was elevated above the floor of the outer crater.

The effects of nanostructures on the mechanical and tribological properties of TiO2 nanotubes

NASA Astrophysics Data System (ADS)

Yoon, Yeoungchin; Park, Jeongwon

2018-04-01

TiO2 nanotubes were prepared by anodization on Ti substrates with a diameter variation of 30-100 nm, and the structure of the nanotubes were studied using x-ray diffraction and Raman spectroscopy, which confirmed the structure changes from the anatase phase to the rutile phase of TiO2 at a diameter below 50 nm. The tribological behaviors of TiO2 nanotubes were investigated with different diameters. The effectiveness of the rutile phase and the diameter size enhanced the frictional performance of TiO2 nanotubes.

Micromachined cascade virtual impactor with a flow rate distributor for wide range airborne particle classification

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kim, Yong-Ho; Maeng, Jwa-Young; Park, Dongho

2007-07-23

This letter reports a module for airborne particle classification, which consists of a micromachined three-stage virtual impactor for classifying airborne particles according to their size and a flow rate distributor for supplying the required flow rate to the virtual impactor. Dioctyl sebacate particles, 100-600 nm in diameter, and carbon particles, 0.6-10 {mu}m in diameter, were used for particle classification. The collection efficiency and cutoff diameter were examined. The measured cutoff diameters of the first, second, and third stages were 135 nm, 1.9 {mu}m, and 4.8 {mu}m, respectively.

The effects of nanostructures on the mechanical and tribological properties of TiO2 nanotubes.

PubMed

Yoon, Yeoungchin; Park, Jeongwon

2018-04-20

TiO 2 nanotubes were prepared by anodization on Ti substrates with a diameter variation of 30-100 nm, and the structure of the nanotubes were studied using x-ray diffraction and Raman spectroscopy, which confirmed the structure changes from the anatase phase to the rutile phase of TiO 2 at a diameter below 50 nm. The tribological behaviors of TiO 2 nanotubes were investigated with different diameters. The effectiveness of the rutile phase and the diameter size enhanced the frictional performance of TiO 2 nanotubes.

Strong focusing effect of 660 nm laser by microsized tapered glass tubes with different diameters

NASA Astrophysics Data System (ADS)

Lin, Chongnan; Luo, Xujia; Zhu, Xiaoyang; Zhu, Li; Wang, Hongcheng; Zhang, Ao; Xu, Runyu; Qu, Zheng; Chen, Ximeng; Zhang, Weiyi; Shao, Jianxiong

2017-09-01

A laser with a wavelength of 660 nm was focused by microsized tapered glass tubes with different diameters of the exit. By using the 3-μm optical fiber and micrometer displacement stages, we measured the light intensity distribution around the focal spot, the focal distance, and the transmission coefficient of the light transmitted through these tubes. The focusing effect for the glass tubes with smaller outlet diameters of the exit was found to be much stronger than those with larger diameters of the exit. Furthermore, the dependence of the size and distance and the maximum intensity of the focal spot on the tubes' diameter of exit are obtained.

30-W Yb3+-pulsed fiber laser with wavelength tuning

NASA Astrophysics Data System (ADS)

Davydov, B. L.; Krylov, A. A.

2007-12-01

We have investigated various pulsed operation regimes of a diode-pumped Yb3+-doped fiber laser with both an acoustooptic filter and a shutter inside the resonator. To imbed the polarization-sensitive acoustooptic-tunable spectral filter into the polarization-nonmaintaining resonator, based on an “isotropic” single-mode fiber without “polarization’ losses, we have used a CaCO3 single-crystal nondispersive thermostable polarization splitter. Stable smooth bell-shaped laser pulses were obtained in the Q-switch generation regime across the entire wavelength tuning band. Their duration depended on the resonator travel time and their repetition rate was determined exclusively by the outer high-frequency generator controlling the acoustooptic shutter. A pulsed laser radiation tuning bandwidth of more than 20-nm at a repetition rate band of 10-100 kHz was observed in the amplification band of the Yb3+-doped fiber. A stable average power of 30 W of the pulsed 70-ns 100-kHz laser radiation in a near Gaussian beam was reached by means of the two-stage amplifier based on Yb3+-doped fibers with an enlarged mode field diameter (14 μm). The amplifier was pumped by λ = 975 nm CW multimode laser diodes with a maximum average power of 42 W.

Effects of sintering temperature on the pyrochlore phase in PZT nanotubes and their transformation to the perovskite phase by coating with PbO multilayers.

PubMed

Han, Jin Kyu; Choi, Yong Chan; Jeon, Do Hyen; Lee, Min Ku; Bu, Sang Don

2014-11-01

We report the phase evolution of Pb(Zr0.52Ti0.48)O3 nanotubes (PZT-NTs), from the pyrochlore to perovskite phase, with an outer diameter of about 420 nm and a wall thickness of about 10 nm. The PZT-NTs were fabricated in pores of porous anodic alumina membrane (PAM) using a spin coating of PZT sol-gel solution and subsequent annealing at 500-700 degrees C in oxygen gas. The pyrochlore phase was found to be formed at 500 degrees C, and also found not to be transformed into the perovskite phase, even though annealing was performed at higher temperatures to 700 degrees C. Elementary distribution analysis of PZT-NTs embedded in PAM reveal that Pb diffusion from nanotubes into pore walls of PAM is one of the main reasons. By employing firstly an additional PbO coating on the pyrochlore nanotubes and then subsequent annealing at 700 degrees C, we have successfully achieved an almost pure perovskite phase in nanotubes. These results suggest that PbO acts as a Pb-compensation agent in the Pb- deficient PZT-NTs. Moreover, our method can be used in the synthesis of all metal-oxide materials, including volatile elements.

Mechanical Properties of Nanoscopic Lipid Domains

DOE PAGES

Nickels, Jonathan D.; Cheng, Xiaolin; Mostofian, Barmak; ...

2015-09-28

We found that the lipid raft hypothesis presents insight into how the cell membrane organizes proteins and lipids to accomplish its many vital functions. Yet basic questions remain about the physical mechanisms that lead to the formation, stability, and size of lipid rafts. Thus, much interest has been generated in the study of systems that contain similar lateral heterogeneities, or domains. In the current work we present an experimental approach that is capable of isolating the bending moduli of lipid domains. This is accomplished using neutron scattering and its unique sensitivity to the isotopes of hydrogen. Combining contrast matching approachesmore » with inelastic neutron scattering, we isolate the bending modulus of ~13 nm diameter domains residing in 60 nm unilamellar vesicles, whose lipid composition mimics the mammalian plasma membrane outer leaflet. Importantly, the bending modulus of the nanoscopic domains differs from the modulus of the continuous phase surrounding them. Moreover, from additional structural measurements and all-atom simulations, we also determine that nanoscopic domains are in-register across the bilayer leaflets. Taken together, these results inform a number of theoretical models of domain/raft formation and highlight the fact that mismatches in bending modulus must be accounted for when explaining the emergence of lateral heterogeneities in lipid systems and biological membranes.« less

Deposition of silver nanoparticles on multiwalled carbon nanotubes by chemical reduction process and their antimicrobial effects

NASA Astrophysics Data System (ADS)

Haider, Adawiya J.; Thamir, Amin D.; Ahmed, Duha S.; Mohammad, M. R.

2016-07-01

In this paper, the functionalization of raw-MWCNTs involves oxidation reaction using concentrated acid mixture of HNO3:H2SO4 (1:3), via ultrasonic bath (170 W, 50 kHz) to obtain functional groups. Then Ag nanoparticles are decorated the outside over the surface of functionalized MWCNTs using a chemical reduction process resulting in the formation of(Ag/ MWCNTs) hybrid material. The results showed that outer diameter functionalized F-MWCNTs andAg nanoparticles size was about (11-80) nm and (10 to 25) nm, respectively using TEM and HRTEM. The crystallographic structure of MWCNTs using X-ray diffraction (XRD) analysis proved diffraction peaks at 38.1°, 44.3°, 64.7° and 77.4° degrees namely, Ag (111), Ag (200), Ag (220), and Ag (311) of the face-centered cubic lattice of Ag, respectively, excepting the peak at 2θ =25.6°, which correspond to the (0 0 2) reflection of the MWNTs are corresponding to Ag/MWNTs. The antimicrobial activities of Ag/MWCNTs hybrid using plate count method showed that decreasing a large number of bacteria colonies of E. coli and S. aureu with increasing the hybrid concentrations after incubation for 24h in shaker incubator with percentage of inhibition approaching 100%.

Superhydrophilic nanopillar-structured quartz surfaces for the prevention of biofilm formation in optical devices

NASA Astrophysics Data System (ADS)

Han, Soo; Ji, Seungmuk; Abdullah, Abdullah; Kim, Duckil; Lim, Hyuneui; Lee, Donghyun

2018-01-01

Bacterial biofilm formation on optical devices such as contact lenses, optical glasses, endoscopic devices, and microscopic slides and lenses are major concerns in the field of medicine and biomedical engineering. To solve these problems, here we present the first report of superhydrophilic transparent nanopillar-structured surfaces with bactericidal properties. To construct bactericidal surfaces, we imitated a topological mechanism found in nature in which nanopillar-structured surfaces cause a mechanical disruption of the outer cell membranes of bacteria, resulting in bacterial cell death. We used nanosphere lithography to fabricate nanopillars with various sharpnesses and heights on a quartz substrate. Water contact angle and light reflectance measurements revealed superhydrophilic, antifogging and antireflective properties, which are important for use in optical devices. To determine bactericidal efficiency, the fabricated surfaces were incubated and tested against two Gram-negative bacteria associated with biofilm formation and various diseases in humans, Pseudomonas aeruginosa and Escherichia coli. The highest bactericidal activity was achieved with nanopillars that measured 300 nm in height and 10 nm in apex diameter. Quartz substrates patterned with such nanopillars killed ∼38,000 P. aeruginosa and ∼27,000 E. coli cells cm-2 min-1, respectively. Thus, the newly designed nanopillar-structured bactericidal surfaces are suitable for use in the development of superhydrophilic and transparent optical devices.

Halloysite Nanocapsules Containing Thyme Essential Oil: Preparation, Characterization, and Application in Packaging Materials.

PubMed

Jang, Si-Hoon; Jang, So-Ri; Lee, Gyeong-Min; Ryu, Jee-Hoon; Park, Su-Il; Park, No-Hyung

2017-09-01

Halloysite nanotubes (HNTs), which are natural nanomaterials, have a hollow tubular structure with about 15 nm inner and 50 nm outer diameters. Because of their tubular shape, HNTs loaded with various materials have been investigated as functional nanocapsules. In this study, thyme essential oil (TO) was encapsulated successfully in HNTs using vacuum pulling methods, followed by end-capping or a layer-by-layer surface coating process for complete encapsulation. Nanocapsules loaded with TO were mixed with flexographic ink and coated on a paper for applications as food packaging materials. Scanning electron microscopy and transmission electron microscopy were used to characterize the morphology of the nanocapsules and to confirm the TO loading of the nanocapsules. Fourier transform infrared spectroscopy and thermogravimetric analyses analysis were used to complement the structural information. In addition, the controlled release of TO from the nanocapsules showed sustained release properties over a period of many days. The results reveal that the release properties of TO in these nanocapsules could be controlled by surface modifications such as end-capping and/or surface coating of bare nanocapsules. The packaging paper with TO-loaded HNT capsules was effective in eliminating against Escherichia coli during the first 5 d and showed strong antibacterial activity for about 10 d. © 2017 Institute of Food Technologists®.

Probing plasmon resonances of individual aluminum nanoparticles

NASA Astrophysics Data System (ADS)

Wei, Zhongxia; Mao, Peng; Cao, Lu; Song, Fengqi

2018-01-01

The plasmon resonances of individual aluminum nanoparticles are investigated by electron energy-loss spectroscopy (EELS) in scanning transmission electron microscope (STEM). Surface plasmon mode and bulk plasmon mode of Al nanoparticles are clearly characterized in the EEL spectra. Discrete dipole approximation (DDA) calculations show that as the particle diameter increases from 20 nm to 100 nm, the plasmon resonance shifts to lower energy and higher mode of surface plasmon arises when the diameter reaches 60 nm and larger.

The Fate of Polyol-Made ZnO and CdS Nanoparticles in Seine River Water (Paris, France).

PubMed

da Rocha, Alice; Sivry, Yann; Gelabert, Alexandre; Beji, Zyed; Benedetti, Marc F; Menguy, Nicolas; Brayner, Roberta

2015-05-01

This study aims to characterize nanoparticles with different compositions and structures as well as seeing their evolutions over time in a natural environment such as Seine river water (Paris, France). Face centered cubic (fcc) and hexagonal (hcp) CdS as well as hexagonal (hcp) ZnO nanoparticles were synthesized by the Polyol method. CdS nanoparticles (i) cfc structure: are agglomerated, present 100 nm length with heterogeneous diameter and 10 m2 g(-1) specific surface area (S(g)) from Brunauer Emett and Teller (BET) measurements; (ii) hcp structure: 20 nm and S(g) = 67 m2 g(-1). ZnO hcp nanoparticles presents 50 nm length and 15 nm diameter and S(g) = 54 m2 g(-1). These results are in agreement with X-ray diffraction (XRD), and small angle X-ray scattering (SAXs). After 48 h interaction with Seine river water, cryo-TEM analysis showed that ZnO nanoparticles form spherical agglomerates with 300 nm diameter; CdS nanoparticles (fcc) are agglomerated presenting large diameters (> 500 nm); and CdS nanoparticles (hcp) are not agglomerated and present the same characteristics of the starting material. After 168h of contact with Seine river water, CdS (fcc) presents only 14% of dissolution, CdS (hcp) presents both 60% dissolution and 30% reprecipitation in a cadmium carbonate form and finally almost 90% of ZnO nanoparticles are dissolved.

Controlled manipulation of flexible carbon nanotubes through shape-dependent pushing by atomic force microscopy.

PubMed

Yang, Seung-Cheol; Qian, Xiaoping

2013-09-17

A systematic approach to manipulating flexible carbon nanotubes (CNTs) has been developed on the basis of atomic force microscope (AFM) based pushing. Pushing CNTs enables efficient transport and precise location of individual CNTs. A key issue for pushing CNTs is preventing defective distortion in repetitive bending and unbending deformation. The approach presented here controls lateral movement of an AFM tip to bend CNTs without permanent distortion. The approach investigates possible defects caused by tensile strain of the outer tube under uniform bending and radial distortion by kinking. Using the continuum beam model and experimental bending tests, dependency of maximum bending strain on the length of bent CNTs and radial distortion on bending angles at a bent point have been demonstrated. Individual CNTs are manipulated by limiting the length of bent CNTs and the bending angle. In our approach, multiwalled CNTs with 5-15 nm diameter subjected to bending deformation produce no outer tube breakage under uniform bending and reversible radial deformation with bending angles less than 110°. The lateral tip movement is determined by a simple geometric model that relies on the shape of multiwalled CNTs. The model effectively controls deforming CNT length and bending angle for given CNT shape. Experimental results demonstrate successful manipulation of randomly dispersed CNTs without visual defects. This approach to pushing can be extended to develop a wide range of CNT based nanodevice applications.

Fiber optic muzzle brake tip for reducing fiber burnback and stone retropulsion during thulium fiber laser lithotripsy

NASA Astrophysics Data System (ADS)

Hutchens, Thomas C.; Gonzalez, David A.; Irby, Pierce B.; Fried, Nathaniel M.

2017-01-01

The experimental thulium fiber laser (TFL) is being explored as an alternative to the current clinical gold standard Holmium:YAG laser for lithotripsy. The near single-mode TFL beam allows coupling of higher power into smaller optical fibers than the multimode Holmium laser beam profile, without proximal fiber tip degradation. A smaller fiber is desirable because it provides more space in the ureteroscope working channel for increased saline irrigation rates and allows maximum ureteroscope deflection. However, distal fiber tip burnback increases as fiber diameter decreases. Previous studies utilizing hollow steel sheaths around recessed distal fiber tips reduced fiber burnback but increased stone retropulsion. A "fiber muzzle brake" was tested for reducing both fiber burnback and stone retropulsion by manipulating vapor bubble expansion. TFL lithotripsy studies were performed at 1908 nm, 35 mJ, 500 μs, and 300 Hz using a 100-μm-core fiber. The optimal stainless steel muzzle brake tip tested consisted of a 1-cm-long, 560-μm-outer-diameter, 360-μm-inner-diameter tube with a 275-μm-diameter through hole located 250 μm from the distal end. The fiber tip was recessed a distance of 500 μm. Stone phantom retropulsion, fiber tip burnback, and calcium oxalate stone ablation studies were performed ex vivo. Small stones with a mass of 40±4 mg and 4-mm-diameter were ablated over a 1.5-mm sieve in 25±4 s (n=10) without visible distal fiber tip burnback. Reduction in stone phantom retropulsion distance by 50% and 85% was observed when using muzzle brake tips versus 100-μm-core bare fibers and hollow steel tip fibers, respectively. The muzzle brake fiber tip simultaneously provided efficient stone ablation, reduced stone retropulsion, and minimal fiber degradation during TFL lithotripsy.

Factors affecting diurnal stem contraction in young Douglas-fir

Treesearch

Warren D. Devine; Constance Harrington

2011-01-01

Diurnal fluctuation in a tree's stem diameter is a function of daily growth and of the tree's water balance, as water is temporarily stored in the relatively elastic outer cambial and phloem tissues. On a very productive site in southwestern Washington, U.S.A we used recording dendrometers to monitor stem diameter fluctuations of Douglas-fir at plantation...

Formation of small gold clusters in solution by laser excitation of interband transition

NASA Astrophysics Data System (ADS)

Mafuné, Fumitaka; Kondow, Tamotsu

2003-04-01

Gold nanoparticles with ˜10 nm in average diameter were prepared by laser ablation of a gold metal plate in an aqueous solution of sodium dodecyl sulfate (SDS) and were fragmented by excitation of an interband transition of gold nanoparticles under irradiation of an intense 355-nm pulsed laser. Fragmentation dynamics was investigated by comparing the fragmentation by excitation of a surface plasmon band of gold nanoparticles by a 532-nm laser. It is found that gold nanoparticles with 1.5-nm average diameter are produced together with small gold clusters by properly optimizing the surfactant concentration.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kishino, Katsumi, E-mail: kishino@sophia.ac.jp; Sophia Nanotechnology Research Center, Sophia University, 7-1 Kioi-cho, Chiyoda-ku, Tokyo 102-8554; Ishizawa, Shunsuke

Bottom-up grown structurally graded InGaN-based nanocolumn photonic crystals, in which nanocolumns were arranged in triangular lattice and the nanocolumn diameter changed one-dimensionally from 93 to 213 nm with a fixed lattice constant of 250 nm, were fabricated. The spatial distribution of the diameter resulted in random-laser-like operation under optical excitation. A broad multi-wavelength lasing spectrum with more than 10 peaks was obtained with a full width at half maximum of 27 nm at 505 nm wavelength as well as lowering of the polarization degree, which is expected to be suitable for speckle contrast reduction in laser projection display applications.

Formation of hexagonal boron nitride nanoscrolls induced by inclusion and exclusion of self-assembling molecules in solution process

NASA Astrophysics Data System (ADS)

Hwang, Da Young; Suh, Dong Hack

2014-05-01

Unlike nanoscrolls of 2D graphene, those of 2D h-BN have not been demonstrated, except for only a few experimental reports. Nanoscrolls of h-BN with high yields and reproducibility are first synthesized by a simple solution process. Inner-tube diameters of BNSs including LCAs, N-(2-aminoethyl)-3α-hydroxy-5β-cholan-24-amide, a bile acid derivative and self-assembling material, can be controlled by adjusting the diameter of the LCA fiber which is grown by self-assembly. TEM and SEM images show that BNSs have a tube-like morphology and the inner-tube diameter of BNSs can be controlled in the range from 20 to 60 nm for a smaller diameter, up to 300 nm for a larger diameter by LCA fiber growth inside the BNSs. Finally, open cylindrical BNSs with hollow cores were obtained by dissolving LCAs inside BNSs.Unlike nanoscrolls of 2D graphene, those of 2D h-BN have not been demonstrated, except for only a few experimental reports. Nanoscrolls of h-BN with high yields and reproducibility are first synthesized by a simple solution process. Inner-tube diameters of BNSs including LCAs, N-(2-aminoethyl)-3α-hydroxy-5β-cholan-24-amide, a bile acid derivative and self-assembling material, can be controlled by adjusting the diameter of the LCA fiber which is grown by self-assembly. TEM and SEM images show that BNSs have a tube-like morphology and the inner-tube diameter of BNSs can be controlled in the range from 20 to 60 nm for a smaller diameter, up to 300 nm for a larger diameter by LCA fiber growth inside the BNSs. Finally, open cylindrical BNSs with hollow cores were obtained by dissolving LCAs inside BNSs. Electronic supplementary information (ESI) available. See DOI: 10.1039/c4nr00897a

Electrospray ionization from nanopipette emitters with tip diameters of less than 100 nm.

PubMed

Yuill, Elizabeth M; Sa, Niya; Ray, Steven J; Hieftje, Gary M; Baker, Lane A

2013-09-17

Work presented here demonstrates application of nanopipettes pulled to orifice diameters of less than 100 nm as electrospray ionization emitters for mass spectrometry. Mass spectrometric analysis of a series of peptides and proteins electrosprayed from pulled-quartz capillary nanopipette emitters with internal diameters ranging from 37 to 70 nm is detailed. Overall, the use of nanopipette emitters causes a shift toward the production of ions of higher charge states and leads to a reduction in width of charge-state distribution as compared to typical nanospray conditions. Further, nanopipettes show improved S/N and the same signal precision as typical nanospray, despite the much smaller dimensions. As characterized by SEM images acquired before and after spray, nanopipettes are shown to be robust under conditions employed. Analytical calculations and numerical simulations are used to calculate the electric field at the emitter tip, which can be significant for the small diameter tips used.

Determination of detonation parameters for liquid High Explosives

NASA Astrophysics Data System (ADS)

Mochalova, Valentina; Utkin, Alexander

2011-06-01

The experimental investigation of detonation parameters and reaction zone structure in liquid HE (bis-(2-fluoro-2,2-dinitroethyl)formal (FEFO), tetranitromethane (TNM), nitromethane (NM)) was conducted. Detonation front in TNM and NM was stable while the instability of detonation in FEFO was observed. Von Neumann spike was recorded for these HE and its parameters were determined. The different methods for C-J point determination were used for each HE. For FEFO reaction time τ was found from experiments with different charge diameters (τ is approximately equal to 300 ns); for TNM - at fixed diameter and different lengths of charges (τ ~ 200 ns); for NM - at fixed diameter and length of charges, but detonation initiation was carried out by different explosive charges (τ ~ 50 ns). It was found that in TNM the detonation velocity depends on charge diameter. Maximum value of reaction rate in investigated liquid HE was observed after shock jump and induction time was not recorded.

Determination of detonation parameters for liquid high explosives

NASA Astrophysics Data System (ADS)

Mochalova, Valentina; Utkin, Alexander

2012-03-01

The experimental investigation of detonation parameters and reaction zone structure in liquid HE (bis-(2-fluoro-2,2-dinitroethyl)formal (FEFO), tetranitromethane (TNM), nitromethane (NM)) was conducted by means of laser interferometer VISAR. Detonation front in TNM and NM was stable while the instability of detonation in FEFO was observed. The parameters of Von Neumann spike were determined for these HE. The different methods for C-J point determination were used for each HE. For FEFO reaction time t was found from experiments with different charge diameters (τ is approximately equal to 300 ns); for TNM - at fixed diameter and different lengths of charges (τ ≈ 200 ns); for NM - at fixed diameter and length of charges, but detonation initiation was carried out by different explosive charges (τ ≈ 50 ns). It was found that in TNM the detonation velocity depends on charge diameter. Maximum value of reaction rate in investigated liquid HE was observed after shock jump.

Cr-Si Schottky nano-diodes utilizing anodic aluminum oxide templates.

PubMed

Kwon, Namyong; Kim, Kyohyeok; Heo, Jinhee; Chung, Ilsub

2014-04-01

We have fabricated Cr nanodot Schottky diodes utilizing AAO templates formed on n-Si substrates. The diameters of the diodes were 75.0, 57.6, and 35.8 nm. Cr nanodot Schottky diodes with smaller diameters yield higher current densities than those with larger diameters due to an enhanced tunnel current contribution, which is attributed to a reduction in the barrier thickness. The diameters of Cr nanodots smaller than the Debye length (156 nm) play an important role in the reduction of barrier thickness. Also, we have fabricated Cr-Si nanorod Schottky diodes with three different lengths (130, 220, and 330 nm) by dry etching of n-Si substrate. Cr-Si nanorod Schottky diodes with longer nanorods yield higher reverse current than those with shorter nanorods due to the enhanced electric field, which is attributed to a high aspect ratio of Si nanorod.

Fabrication and electrical characterization of sub-micron diameter through-silicon via for heterogeneous three-dimensional integrated circuits

NASA Astrophysics Data System (ADS)

Abbaspour, R.; Brown, D. K.; Bakir, M. S.

2017-02-01

This paper presents the fabrication and electrical characterization of high aspect-ratio (AR) sub-micron diameter through silicon vias (TSVs) for densely interconnected three-dimensional (3D) stacked integrated circuits (ICs). The fabricated TSV technology features an AR of 16:1 with 680 nm diameter copper (Cu) core and 920 nm overall diameter. To address the challenges in scaling TSVs, scallop-free low roughness nano-Bosch silicon etching and direct Cu electroplating on a titanium-nitride (TiN) diffusion barrier layer have been developed as key enabling modules. The electrical resistance of the sub-micron TSVs is measured to be on average 1.2 Ω, and the Cu resistivity is extracted to be approximately 2.95 µΩ cm. Furthermore, the maximum achievable current-carrying capacity (CCC) of the scaled TSVs is characterized to be approximately 360 µA for the 680 nm Cu core.

In-line rotating capacitive torque sensor

DOEpatents

Kronberg, James W.

1991-01-01

A method and apparatus for measuring torques developed along a rotating mechanical assembly comprising a rotating inner portion and a stationary outer portion. The rotating portion has an electrically-conductive flexing section fitted between two coaxial shafts in a configuration which varies radially in accordance with applied torque. The stationary portion comprises a plurality of conductive plates forming a surface concentric with and having a diameter slightly larger than the diameter of the rotating portion. The capacitance between the outer, nonrotating and inner, rotating portion varies with changes in the radial configuration of the rotating portion. Signal output varies approximately linearly with torque for small torques, nonlinearly for larger torques. The sensor is preferably surrounded by a conductive shell to minimize electrical interference from external sources.

Retinal photoreceptors and visual pigments in Boa constrictor imperator.

PubMed

Sillman, A J; Johnson, J L; Loew, E R

2001-09-01

The photoreceptors of Boa constrictor, a boid snake of the subfamily Boinae, were examined with scanning electron microscopy and microspectrophotometry. The retina of B. constrictor is duplex but highly dominated by rods, cones comprising 11% of the photoreceptor population. The rather tightly packed rods have relatively long outer segments with proximal ends that are somewhat tapered. There are two morphologically distinct, single cones. The most common cone by far has a large inner segment and a relatively stout outer segment. The second cone, seen only infrequently, has a substantially smaller inner segment and a finer outer segment. The visual pigments of B. constrictor are virtually identical to those of the pythonine boid, Python regius. Three different visual pigments are present, all based on vitamin A(1.) The visual pigment of the rods has a wavelength of peak absorbance (lambda(max)) at 495 +/- 2 nm. The visual pigment of the more common, large cone has a lambda(max) at 549 +/- 1 nm. The small, rare cone contains a visual pigment with lambda(max) at 357 +/- 2 nm, providing the snake with sensitivity in the ultraviolet. We suggest that B. constrictor might employ UV sensitivity to locate conspecifics and/or to improve hunting efficiency. The data indicate that wavelength discrimination above 430 nm would not be possible without some input from the rods. Copyright 2001 Wiley-Liss, Inc.

Low-temperature synthesis and characterization of helical carbon fibers by one-step chemical vapour deposition

NASA Astrophysics Data System (ADS)

Jin, Yongzhong; Chen, Jian; Fu, Qingshan; Li, Binghong; Zhang, Huazhi; Gong, Yong

2015-01-01

Helical carbon fibers (HCNFs) were synthesized by one-step chemical vapour deposition using cupric tartrate as a catalyst at temperature below 500 °C. The bound rubber of natural rubber (NR)/HCNFs were also prepared in this study. The results of thermogravimetry-differential scanning calorimetry (TG/DSC) for cupric tartrate nanoparticles show that the transformation of C4H4CuO6 → Cu reaction occurs at ∼250-310 °C. The characterization of scanning electron microscopy (SEM), transmission electron microscope (TEM), X-ray diffraction (XRD) and Raman spectrum for the synthesized products confirms that the synthesis of HCNFs is highly temperature-dependent. The straight fibers with the fiber diameter of 100-400 nm are obtained at 280 °C and HCNFs can be synthesized at higher temperature, with the coil diameter of 0.5-1 μm and fiber diameter of 100-200 nm at 380 °C, and the coil diameter of ∼100 nm and fiber diameter of ∼80 nm at 480 °C. The maximum of the bound-rubber content (37%) can be obtained with the addition of 100 wt.% HCNFs in NR, which indicates that the coiled configuration of HCNFs makes a noticeable contribution to the reinforcement of NR/CB system.

Superparamagnetic properties of carbon nanotubes filled with NiFe{sub 2}O{sub 4} nanoparticles

DOE Office of Scientific and Technical Information (OSTI.GOV)

Stojak Repa, K.; Israel, D.; Phan, M. H., E-mail: phanm@usf.edu, E-mail: sharihar@usf.edu

2015-05-07

Multi walled carbon nanotubes (MWCNTs) were successfully synthesized using custom-made 80 nm pore-size alumina templates, and were uniformly filled with nickel ferrite (NFO) nanoparticles of 7.4 ± 1.7 nm diameter using a novel magnetically assisted capillary action method. X-ray diffraction confirmed the inverse spinel phase for the synthesized NFO. Transmission electron microscopy confirms spherical NFO nanoparticles with an average diameter of 7.4 nm inside MWCNTs. Magnetometry indicates that both NFO and NFO-filled MWCNTs present a blocking temperature around 52 K, with similar superparamagnetic-like behavior, and weak dipolar interactions, giving rise to a super-spin-glass-like behavior at low temperatures. These properties along with the uniformity of sub-100 nm structuresmore » and the possibility of tunable magnetic response in variable diameter carbon nanotubes make them ideal for advanced biomedical and microwave applications.« less

A fast integrated mobility spectrometer for rapid measurement of sub-micrometer aerosol size distribution, Part II: Experimental characterization

DOE PAGES

Wang, Jian; Pikridas, Michael; Pinterich, Tamara; ...

2017-06-08

A Fast Integrated Mobility Spectrometer (FIMS) with a wide dynamic size range has been developed for rapid aerosol size distribution measurements. The design and model evaluation of the FIMS are presented in the preceding paper (Paper I), and this paper focuses on the experimental characterization of the FIMS. Monodisperse aerosol with diameter ranging from 8 to 600 nm was generated using Differential Mobility Analyzer (DMA), and was measured by the FIMS in parallel with a Condensation Particle Counter (CPC). The mean particle diameter measured by the FIMS is in good agreement with the DMA centroid diameter. Comparison of the particlemore » concentrations measured by the FIMS and CPC indicates the FIMS detection efficiency is essentially 100% for particles with diameters of 8 nm or larger. For particles smaller than 20 nm or larger than 200 nm, FIMS transfer function and resolution can be well represented by the calculated ones based on simulated particle trajectories in the FIMS. For particles between 20 and 200 nm, the FIMS transfer function is boarder than the calculated, likely due to non-ideality of the electric field, including edge effects near the end of the electrode, which are not represented by the 2-D electric field used to simulate particle trajectories.« less

A fast integrated mobility spectrometer for rapid measurement of sub-micrometer aerosol size distribution, Part II: Experimental characterization

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wang, Jian; Pikridas, Michael; Pinterich, Tamara

A Fast Integrated Mobility Spectrometer (FIMS) with a wide dynamic size range has been developed for rapid aerosol size distribution measurements. The design and model evaluation of the FIMS are presented in the preceding paper (Paper I), and this paper focuses on the experimental characterization of the FIMS. Monodisperse aerosol with diameter ranging from 8 to 600 nm was generated using Differential Mobility Analyzer (DMA), and was measured by the FIMS in parallel with a Condensation Particle Counter (CPC). The mean particle diameter measured by the FIMS is in good agreement with the DMA centroid diameter. Comparison of the particlemore » concentrations measured by the FIMS and CPC indicates the FIMS detection efficiency is essentially 100% for particles with diameters of 8 nm or larger. For particles smaller than 20 nm or larger than 200 nm, FIMS transfer function and resolution can be well represented by the calculated ones based on simulated particle trajectories in the FIMS. For particles between 20 and 200 nm, the FIMS transfer function is boarder than the calculated, likely due to non-ideality of the electric field, including edge effects near the end of the electrode, which are not represented by the 2-D electric field used to simulate particle trajectories.« less

Characteristic of nanoparticles generated from different nano-powders by using different dispersion methods

NASA Astrophysics Data System (ADS)

Tsai, Chuen-Jinn; Lin, Guan-Yu; Liu, Chun-Nan; He, Chi-En; Chen, Chun-Wan

2012-03-01

A standard rotating drum with a modified sampling train (RD), a vortex shaker (VS), and a SSPD (small-scale powder disperser) were used to investigate the emission characteristics of nano-powders, including nano-titanium dioxide (nano-TiO2, primary diameter: 21 nm), nano-zinc oxide (nano-ZnO, primary diameter: 30-50 nm), and nano-silicon dioxide (nano-SiO2, primary diameter: 10-30 nm). A TSI SMPS (scanning mobility particle sizer), a TSI APS (aerodynamic particle sizer), and a MSP MOUDI (micro-orifice uniform deposit impactor) were used to measure the number and mass distributions of generated particles. Significant differences in specific number and mass concentration or distributions were found among different methods and nano-powders with the most specific number and mass concentration and the smallest particles being generated by the most energetic SSPD, followed by VS and RD. Near uni-modal number or mass distributions were observed for the SSPD while bi-modal number or mass distributions existed for nano-powders except nano-SiO2 which also exhibited bimodal mass distributions. The 30-min average results showed that the mass median aerodynamic diameter (MMAD) and number median diameter (NMD) of the SSPD ranged 1.1-2.1 μm and 166-261 nm, respectively, for all three nano-powders, which were smaller than those of the VS (MMAD: 3.3-6.0 μm and NMD: 156-462 nm), and the RD (MMAD: 5.2-11.2 μm and NMD: 198-479 nm). For nano-particles (electric mobility diameter < 100 nm), specific mass concentrations were nearly negligible for all three nano-powders and test methods. Specific number concentrations of nano-particles were low for the RD tester but were elevated when more energetic VS and SSPD testers were used. The quantitative size and concentration data obtained in this study is useful to elucidate the field emission and personal exposure data in the future provided that particle loss in the generation system is carefully assessed.

Impact of osmotic pressure and gelling in the generation of highly stable single core water-in-oil-in-water (W/O/W) nano multiple emulsions of aspirin assisted by two-stage ultrasonic cavitational emulsification.

PubMed

Tang, Siah Ying; Sivakumar, Manickam; Nashiru, Billa

2013-02-01

The present investigation focuses in investigating the effect of osmotic pressure, gelling on the mean droplet diameter, polydispersity index, droplet size stability of the developed novel Aspirin containing water-in-oil-in-water (W/O/W) nano multiple emulsion. The aspirin-loaded nano multiple emulsion formulation was successfully generated using two-stage ultrasonic cavitational emulsification which had been reported in author's previous study. The osmotic behavior of ultrasonically prepared nano multiple emulsions were also examined with different glucose concentrations both in the inner and outer aqueous phases. In addition, introducing gelatin into the formulation also observed to play an important role in preventing the interdroplet coalescence via the formation of interfacial rigid film. Detailed studies were also made on the possible mechanisms of water migration under osmotic gradient which primarily caused by the permeation of glucose. Besides, the experimental results have shown that the interfacial tension between the two immiscible phases decreases with varying the composition of organic phase. Although the W/O/W emulsion prepared with the inner/outer glucose weight ratio of 1-0.5% (w/w) showed an excellent droplet stability, the formulation containing 0.5% (w/w) glucose in the inner aqueous phase appeared to be the most stable with minimum change in the mean droplet size upon one-week storage period. Based on the optimization, nano multiple emulsion droplets with the mean droplet diameter of around 400 nm were produced using 1.25% (w/w) Span 80 and 0.5% Cremophore EL. Overall, our investigation makes a pathway in proving that the use of ultrasound cavitation is an efficient yet promising approach in the generation of stable and uniform nano multiple emulsions and could be used in the encapsulation of various active pharmaceutical ingredients in the near future. Copyright © 2012 Elsevier B.V. All rights reserved.

Synthesis of Vertically-Aligned Carbon Nanotubes from Langmuir-Blodgett Films Deposited Fe Nanoparticles on Al2O3/Al/SiO2/Si Substrate.

PubMed

Takagiwa, Shota; Kanasugi, Osamu; Nakamura, Kentaro; Kushida, Masahito

2016-04-01

In order to apply vertically-aligned carbon nanotubes (VA-CNTs) to a new Pt supporting material of polymer electrolyte fuel cell (PEFC), number density and outer diameter of CNTs must be controlled independently. So, we employed Langmuir-Blodgett (LB) technique for depositing CNT growth catalysts. A Fe nanoparticle (NP) was used as a CNT growth catalyst. In this study, we tried to thicken VA-CNT carpet height and inhibit thermal aggregation of Fe NPs by using Al2O3/Al/SiO2/Si substrate. Fe NP LB films were deposited on three typed of substrates, SiO2/Si, as-deposited Al2O3/Al/SiO2/Si and annealed Al2O3/Al/SiO2/Si at 923 K in Ar atmosphere of 16 Pa. It is known that Al2O3/Al catalyzes hydrocarbon reforming, inhibits thermal aggregation of CNT growth catalysts and reduces CNT growth catalysts. It was found that annealed Al2O3/Al/SiO2/Si exerted three effects more strongly than as-deposited Al2O3/Al/SiO2/Si. VA-CNTs were synthesized from Fe NPs-C16 LB films by thermal chemical vapor deposition (CVD) method. As a result, at the distance between two nearest CNTs 28 nm or less, VA-CNT carpet height on annealed Al2O3/Al/SiO2/Si was about twice and ten times thicker than that on SiO2/Si and that on as-deposited Al2O3/Al/SiO2/Si, respectively. Moreover, distribution of CNT outer diameter on annealed Al2O3/Al/SiO2/Si was inhibited compared to that on SiO2/Si. These results suggest that since thermal aggregation of Fe NPs is inhibited, catalyst activity increases and distribution of Fe NP size is inhibited.

Estimating surface hardening profile of blank for obtaining high drawing ratio in deep drawing process using FE analysis

NASA Astrophysics Data System (ADS)

Tan, C. J.; Aslian, A.; Honarvar, B.; Puborlaksono, J.; Yau, Y. H.; Chong, W. T.

2015-12-01

We constructed an FE axisymmetric model to simulate the effect of partially hardened blanks on increasing the limiting drawing ratio (LDR) of cylindrical cups. We partitioned an arc-shaped hard layer into the cross section of a DP590 blank. We assumed the mechanical property of the layer is equivalent to either DP980 or DP780. We verified the accuracy of the model by comparing the calculated LDR for DP590 with the one reported in the literature. The LDR for the partially hardened blank increased from 2.11 to 2.50 with a 1 mm depth of DP980 ring-shaped hard layer on the top surface of the blank. The position of the layer changed with drawing ratios. We proposed equations for estimating the inner and outer diameters of the layer, and tested its accuracy in the simulation. Although the outer diameters fitted in well with the estimated line, the inner diameters are slightly less than the estimated ones.

Response of Gd 2 Ti 2 O 7 and La 2 Ti 2 O 7 to swift-heavy ion irradiation and annealing

DOE Office of Scientific and Technical Information (OSTI.GOV)

Park, Sulgiye; Lang, Maik; Tracy, Cameron L.

2015-07-01

Swift heavy ion (2 GeV 181Ta) irradiation-induced amorphization and temperature-induced recrystallization of cubic pyrochlore Gd2Ti2O7 (Fd3¯m) are compared with the response of a compositionally-similar material with a monoclinic-layered perovskite-type structure, La2Ti2O7 (P21). The averaged electronic energy loss, dE/dx, was 37 keV/nm and 35 keV/nm in Gd2Ti2O7 and La2Ti2O7, respectively. Systematic analysis of the structural modifications was completed using transmission electron microscopy, synchrotron X-ray diffraction, Raman spectroscopy, and small-angle X-ray scattering. Increasing ion-induced amorphization with increasing ion fluence was evident in the X-ray diffraction patterns of both compositions by a reduction in the intensity of the diffraction maxima concurrent with themore » growth in intensity of a broad diffuse scattering halo. Transmission electron microscopy analysis showed complete amorphization within ion tracks (diameter: ~10 nm) for the perovskite-type material; whereas a concentric, core–shell morphology was evident in the ion tracks of the pyrochlore, with an outer shell of disordered yet still crystalline material with the fluorite structure surrounding an amorphous track core (diameter: ~9 nm). The radiation response of both titanate oxides with the same stoichiometry can be understood in terms of differences in their structures and compositions. While the radiation damage susceptibility of pyrochlore A2B2O7 materials decreases as a function of the cation radius ratio rA/rB, the current study correlates this behavior with the stability field of monoclinic structures, where rLa/rTi > rGd/rTi. Isochronal annealing experiments of the irradiated materials showed complete recrystallization of La2Ti2O7 at 775 °C and of Gd2Ti2O7 at 850 °C. The annealing behavior is discussed in terms of enhanced damage recovery in La2Ti2O7, compared to the pyrochlore compounds Gd2Ti2O7. The difference in the recrystallization behavior may be related to structural constraints, i.e., reconstructing a low symmetry versus a high symmetry phase.« less

Ultrafast studies of gold, nickel, and palladium nanorods

NASA Astrophysics Data System (ADS)

Sando, Gerald M.; Berry, Alan D.; Owrutsky, Jeffrey C.

2007-08-01

Steady state and ultrafast transient absorption studies have been carried out for gold, nickel, and palladium high aspect ratio nanorods. For each metal, nanorods were fabricated by electrochemical deposition into ˜6μm thick polycarbonate templates. Two nominal pore diameters(10 and 30nm, resulting in nanorod diameters of about 40 and 60nm, respectively) were used, yielding nanorods with high aspect ratios (>25). Static spectra of nanorods of all three metals reveal both a longitudinal surface plasmon resonance (SPRL) band in the mid-infrared as well as a transverse band in the visible for the gold and larger diameter nickel and palladium nanorods. The appearance of SPRL bands in the infrared for high aspect ratio metal nanorods and the trends in their maxima for the different aspect ratios and metals are consistent with calculations based on the Gans theory. For the gold and nickel samples, time resolved studies were performed with a subpicosecond resolution using 400nm excitation and a wide range of probe wavelengths from the visible to the mid-IR as well as for infrared excitation (near 2000cm-1) probed at 800nm. The dynamics observed for nanorods of both metals and both diameters include transients due to electron-phonon coupling and impulsively excited coherent acoustic breathing mode oscillations, which are similar to those previously reported for spherical and smaller rod-shaped gold nanoparticles. The dynamics we observe are the same within the experimental uncertainty for 400nm and infrared (5μm) excitation probed at 800nm. The transient absorption using 400nm excitation and 800nm probe pulses of the palladium nanorods also reveal coherent acoustic oscillations. The results demonstrate that the dynamics for high aspect ratio metal nanorods are similar to those for smaller nanoparticles.

Enhancement of Combustion and Flame Stabilization Using Transient Non-Equilibrium Plasma

DTIC Science & Technology

2007-03-31

cathode spot D = diameter of MGA device D= diffusivity of i’h species d = diameter of arc dcoected= diametrically corrected diameter of arc d.rwwd... cathode and anode, stabilization (4) respectively (Fig. 1). A wire was attached to the cathode , which was separated from the outer anode by 2 mm at the...smallest gap (point (1) in Fig. 1). The wire spiraled progressively closer to the cathode , where it was attached at the largest gap between the two

Facile Fabrication of Ordered Anodized Aluminum Oxide Membranes with Controlled Pore Size by Improved Hard Anodization.

PubMed

Fan, Jiangxia; Zhu, Xinxin; Wang, Kunzhou; Chen, Xiaoyuan; Wang, Xinqing; Yan, Minhao; Ren, Yong

2018-05-01

We have fabricated highly ordered anodized aluminum oxide (AAO) membranes with different diameter through improved hard anodization (HA) at high temperature. This process can generate thick AAO membranes (30 μm) in a short anodizing time with high growth rate 20-60 μm h-1 which is much faster than that in traditional mild two-step anodization. We enlarged the AAO pore diameter by adjusting the voltage rise rate at the same time, which has a great influence on current density and temperature. The AAO pore diameter varies from 60-110 nm to 160-190 nm. The pore diameter (Dp) of the AAO prepared by this improved process is much larger than that prepared by HA (40-60 nm) when H2C2O4 as electrolyte. It can expand potential use of the AAO membranes such as for the template-based synthesis of nanowires or nanotubes with modulated diameters and also for practical separation technology. We also has used the AAO with different diameters prepared by this improved HA to fabricate Co nanowires and γ-Fe2O3 superparamagnetic nanorods.

Physicochemical characterization of titanium dioxide pigments using various techniques for size determination and asymmetric flow field flow fractionation hyphenated with inductively coupled plasma mass spectrometry.

PubMed

Helsper, Johannes P F G; Peters, Ruud J B; van Bemmel, Margaretha E M; Rivera, Zahira E Herrera; Wagner, Stephan; von der Kammer, Frank; Tromp, Peter C; Hofmann, Thilo; Weigel, Stefan

2016-09-01

Seven commercial titanium dioxide pigments and two other well-defined TiO2 materials (TiMs) were physicochemically characterised using asymmetric flow field flow fractionation (aF4) for separation, various techniques to determine size distribution and inductively coupled plasma mass spectrometry (ICPMS) for chemical characterization. The aF4-ICPMS conditions were optimised and validated for linearity, limit of detection, recovery, repeatability and reproducibility, all indicating good performance. Multi-element detection with aF4-ICPMS showed that some commercial pigments contained zirconium co-eluting with titanium in aF4. The other two TiMs, NM103 and NM104, contained aluminium as integral part of the titanium peak eluting in aF4. The materials were characterised using various size determination techniques: retention time in aF4, aF4 hyphenated with multi-angle laser light spectrometry (MALS), single particle ICPMS (spICPMS), scanning electron microscopy (SEM) and particle tracking analysis (PTA). PTA appeared inappropriate. For the other techniques, size distribution patterns were quite similar, i.e. high polydispersity with diameters from 20 to >700 nm, a modal peak between 200 and 500 nm and a shoulder at 600 nm. Number-based size distribution techniques as spICPMS and SEM showed smaller modal diameters than aF4-UV, from which mass-based diameters are calculated. With aF4-MALS calculated, light-scattering-based "diameters of gyration" (Øg) are similar to hydrodynamic diameters (Øh) from aF4-UV analyses and diameters observed with SEM, but much larger than with spICPMS. A Øg/Øh ratio of about 1 indicates that the TiMs are oblate spheres or fractal aggregates. SEM observations confirm the latter structure. The rationale for differences in modal peak diameter is discussed.

Nanofiber alignment of a small diameter elastic electrospun scaffold

NASA Astrophysics Data System (ADS)

Patel, Jignesh

Cardiovascular disease is the leading cause of death in western countries with coronary heart disease making up 50% of these deaths. As a treatment option, tissue engineered grafts have great potential. Elastic scaffolds that mimic arterial extracellular matrix (ECM) may hold the key to creating viable vascular grafts. Electrospinning is a widely used scaffold fabrication technique to engineer tubular scaffolds. In this study, we investigated how the collector rotation speed altered the nanofiber alignment which may improve mechanical characteristics making the scaffold more suitable for arterial grafts. The scaffold was fabricated from a blend of PCL/Elastin. 2D Fast Fourier Transform (FFT) image processing tool and MatLab were used to quantitatively analyze nanofiber orientation at different collector speeds (13500 to 15500 rpm). Both Image J and MatLab showed graphical peaks indicating predominant fiber orientation angles. A collector speed of 15000 rpm was found to produce the best nanofiber alignment with narrow peaks at 90 and 270 degrees, and a relative amplitude of 200. This indicates a narrow distribution of circumferentially aligned nanofibers. Collector speeds below and above 15000 rpm caused a decrease in fiber alignment with a broader orientation distribution. Uniformity of fiber diameter was also measured. Of 600 measures from the 15000 rpm scaffolds, the fiber diameter range from 500 nm to 899 nm was most prevalent. This diameter range was slightly larger than native ECM which ranges from 50 nm to 500 nm. The second most prevalent diameter range had an average of 404 nm which is within the diameter range of collagen. This study concluded that with proper electrospinning technique and collector speed, it is possible to fabricate highly aligned small diameter elastic scaffolds. Image J 2D FFT results confirmed MatLab findings for the analyses of circumferentially aligned nanofibers. In addition, MatLab analyses simplified the FFT orientation data providing an accurate, user friendly orientation measurement tool.

Quantum-interference transport through surface layers of indium-doped ZnO nanowires

NASA Astrophysics Data System (ADS)

Chiu, Shao-Pin; Lu, Jia Grace; Lin, Juhn-Jong

2013-06-01

We have fabricated indium-doped ZnO (IZO) nanowires (NWs) and carried out four-probe electrical-transport measurements on two individual NWs with geometric diameters of ≈70 and ≈90 nm in a wide temperature T interval of 1-70 K. The NWs reveal overall charge conduction behavior characteristic of disordered metals. In addition to the T dependence of resistance R, we have measured the magnetoresistance (MR) in magnetic fields applied either perpendicular or parallel to the NW axis. Our R(T) and MR data in different T intervals are consistent with the theoretical predictions of the one- (1D), two- (2D) or three-dimensional (3D) weak-localization (WL) and the electron-electron interaction (EEI) effects. In particular, a few dimensionality crossovers in the two effects are observed. These crossover phenomena are consistent with the model of a ‘core-shell-like structure’ in individual IZO NWs, where an outer shell of thickness t (≃15-17 nm) is responsible for the quantum-interference transport. In the WL effect, as the electron dephasing length Lφ gradually decreases with increasing T from the lowest measurement temperatures, a 1D-to-2D dimensionality crossover takes place around a characteristic temperature where Lφ approximately equals d, an effective NW diameter which is slightly smaller than the geometric diameter. As T further increases, a 2D-to-3D dimensionality crossover occurs around another characteristic temperature where Lφ approximately equals t (

Quantum-interference transport through surface layers of indium-doped ZnO nanowires.

PubMed

Chiu, Shao-Pin; Lu, Jia Grace; Lin, Juhn-Jong

2013-06-21

We have fabricated indium-doped ZnO (IZO) nanowires (NWs) and carried out four-probe electrical-transport measurements on two individual NWs with geometric diameters of ≈70 and ≈90 nm in a wide temperature T interval of 1-70 K. The NWs reveal overall charge conduction behavior characteristic of disordered metals. In addition to the T dependence of resistance R, we have measured the magnetoresistance (MR) in magnetic fields applied either perpendicular or parallel to the NW axis. Our R(T) and MR data in different T intervals are consistent with the theoretical predictions of the one- (1D), two- (2D) or three-dimensional (3D) weak-localization (WL) and the electron-electron interaction (EEI) effects. In particular, a few dimensionality crossovers in the two effects are observed. These crossover phenomena are consistent with the model of a 'core-shell-like structure' in individual IZO NWs, where an outer shell of thickness t (~15-17 nm) is responsible for the quantum-interference transport. In the WL effect, as the electron dephasing length Lφ gradually decreases with increasing T from the lowest measurement temperatures, a 1D-to-2D dimensionality crossover takes place around a characteristic temperature where Lφ approximately equals d, an effective NW diameter which is slightly smaller than the geometric diameter. As T further increases, a 2D-to-3D dimensionality crossover occurs around another characteristic temperature where Lφ approximately equals t (

Effect of AOT Microemulsion Composition on the Hydrodynamic Diameter and Electrophoretic Mobility of Titanium Oxide Nanoparticles

NASA Astrophysics Data System (ADS)

Shaparenko, N. O.; Beketova, D. I.; Demidova, M. G.; Bulavchenko, A. I.

2018-05-01

The hydrodynamic diameter and electrophoretic mobility of titania nanoparticles in AOT microemulsions are studied depending on their water content (from 0 to 1.5 vol %), chloroform content in n-decane-chloroform mixture (from 0 to 30 vol %) and temperature (from 0 to 60°C). Considerable changes in diameter (from 20 to 400 nm) are detected upon adding water to the microemulsion. The electrophoretic mobility grows by 2-3 times upon adding chloroform, or as the temperature falls. The observed features allow us to halve the time of electrophoretic concentration for 140 nm TiO2 nanoparticles, and to concentrate 14 nm nanoparticles that do not exhibit electrophoretic mobility in the absence of chloroform.

Design trade-off between spatial resolution and power consumption in CMOS biosensor circuit based on millimeter-wave LC oscillator array

NASA Astrophysics Data System (ADS)

Matsunaga, Maya; Kobayashi, Atsuki; Nakazato, Kazuo; Niitsu, Kiichi

2018-03-01

In this paper, we describe a trade-off between spatial resolution and power consumption in an LC oscillator-based CMOS biosensor, which can detect biomolecules by observing the resonance frequency shift due to changes in the complex permittivity of the biomolecules. The optimal operating frequency and improvement in the image resolution of the sensor output require a reduction in the size of the inductor. However, it is necessary to increase the transconductance of the cross-coupling transistor to achieve the oscillation condition, although the power consumption increases. We confirmed the trade-off between the spatial resolution and the power consumption of this sensor using SPICE simulation. A test chip was fabricated using a 65 nm CMOS process, and the transition in the peak frequency and the power consumption were measured. When the outer diameter of the inductor was 46 µm, the power consumption was 31.2 mW, which matched well with the simulation results.

Chitosan-Gated Magnetic-Responsive Nanocarrier for Dual-Modal Optical Imaging, Switchable Drug Release, and Synergistic Therapy

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wang, Hui; Mu, Qingxin; Revia, Richard

In this study, we present a multifunctional yet structurally simple nanocarrier that has a high drug loading capacity, releases drug in response to onset of an AC magnetic field, and can serve as a long-term imaging contrast agent and effectively kills cancer cells by synergistic action. This nanocarrier (HMMC-NC) has a spherical shell structure with a center cavity of 80 nm in diameter. The shell is comprised of two layers: an inner layer of magnetite that exhibits superparamagnetism and an outer layer of mesoporous carbon embedded with carbon dots that exhibit photoluminescence property. Thus in addition to being a drugmore » carrier, HMMC-NC is also a contrast agent for bioimaging. The switchable drug release is enabled by the chitosan molecules attached on the nanocarrier as the switching material which turns on or off the drug release in response to the application or withdrawal of an AC magnetic field.« less

Optical fiber LPG biosensor integrated microfluidic chip for ultrasensitive glucose detection

PubMed Central

Yin, Ming-jie; Huang, Bobo; Gao, Shaorui; Zhang, A. Ping; Ye, Xuesong

2016-01-01

An optical fiber sensor integrated microfluidic chip is presented for ultrasensitive detection of glucose. A long-period grating (LPG) inscribed in a small-diameter single-mode fiber (SDSMF) is employed as an optical refractive-index (RI) sensor. With the layer-by-layer (LbL) self-assembly technique, poly (ethylenimine) (PEI) and poly (acrylic acid) (PAA) multilayer film is deposited on the SDSMF-LPG sensor for both supporting and signal enhancement, and then a glucose oxidase (GOD) layer is immobilized on the outer layer for glucose sensing. A microfluidic chip for glucose detection is fabricated after embedding the SDSMF-LPG biosensor into the microchannel of the chip. Experimental results reveal that the SDSMF-LPG biosensor based on such a hybrid sensing film can ultrasensitively detect glucose concentration as low as 1 nM. After integration into the microfluidic chip, the detection range of the sensor is extended from 2 µM to 10 µM, and the response time is remarkablely shortened from 6 minutes to 70 seconds. PMID:27231643

Self-assembly of (perfluoroalkyl)alkanes on a substrate surface from solutions in supercritical carbon dioxide.

PubMed

Gallyamov, Marat O; Mourran, Ahmed; Tartsch, Bernd; Vinokur, Rostislav A; Nikitin, Lev N; Khokhlov, Alexei R; Schaumburg, Kjeld; Möller, Martin

2006-06-14

Toroidal self-assembled structures of perfluorododecylnonadecane and perfluorotetradecyloctadecane have been deposited on mica and highly oriented pyrolytic graphite surfaces by exposure of the substrates to solutions of the (pefluoroalkyl)alkanes in supercritical carbon dioxide. Scanning force microscopy (SFM) images have displayed a high degree of regularity of these self-assembled nanoobjects regarding size, shape, and packing in a monolayer. Analysis of SFM images allowed us to estimate that each toroidal domain has an outer diameter of about 50 nm and consists of several thousands of molecules. We propose a simple model explaining the clustering of the molecules to objects with a finite size. The model based on the close-packing principles predicts formation of toroids, whose size is determined by the molecular geometry. Here, we consider the amphiphilic nature of the (perfluoroalkyl)alkane molecules in combination with incommensurable packing parameters of the alkyl- and the perfluoralkyl-segments to be a key factor for such a self-assembly.

Zonal Flow Velocimetry in Spherical Couette Flow using Acoustic Modes

NASA Astrophysics Data System (ADS)

Adams, Matthew M.; Mautino, Anthony R.; Stone, Douglas R.; Triana, Santiago A.; Lekic, Vedran; Lathrop, Daniel P.

2015-11-01

We present studies of spherical Couette flows using the technique of acoustic mode Doppler velocimetry. This technique uses rotational splittings of acoustic modes to infer the azimuthal velocity profile of a rotating flow, and is of special interest in experiments where direct flow visualization is impractical. The primary experimental system consists of a 60 cm diameter outer spherical shell concentric with a 20 cm diameter sphere, with air or nitrogen gas serving as the working fluid. The geometry of the system approximates that of the Earth's core, making these studies geophysically relevant. A turbulent shear flow is established in the system by rotating the inner sphere and outer shell at different rates. Acoustic modes of the fluid volume are excited using a speaker and measured via microphones, allowingdetermination of rotational splittings. Preliminary results comparing observed splittings with those predicted by theory are presented. While the majority of these studies were performed in the 60 cm diameter device using nitrogen gas, some work has also been done looking at acoustic modes in the 3 m diameter liquid sodium spherical Couette experiment. Prospects for measuring zonal velocity profiles in a wide variety of experiments are discussed.

Shaft/shaft-seal interface characteristics of a multiple disk centrifugal blood pump.

PubMed

Manning, K B; Miller, G E

1999-06-01

A multiple disk centrifugal pump (MDCP) is under investigation as a potential left ventricular assist device. As is the case with most shaft driven pumps, leakage problems around the shaft/shaft seal interface are of major interest. If leakage were to occur during or after implantation, potential events such as blood loss, clotting, blood damage, and/or infections might result in adverse effects for the patient. Because these effects could be quite disastrous, potential shaft and shaft seal materials have been investigated to determine the most appropriate course to limit these effects. Teflon and nylon shaft seals were analyzed as potential candidates along with a stainless steel shaft and a Melonite coated shaft. The materials and shafts were evaluated under various time durations (15, 30, 45, and 60 min), motor speeds (800, 1,000, 1,200, and 1,400 rpm), and outer diameters (1/2 and 3/4 inches). The motor speed and geometrical configurations were typical for the MDCP under normal physiologic conditions. An air and water study was conducted to analyze the inner diameter wear, the inner temperature values, and the outer temperature values. Statistical comparisons were computed for the shaft seal materials, the shafts, and the outer diameters along with the inner and outer temperatures. The conclusions made from the results indicate that both the tested shaft seal materials and shaft materials are not ideal candidates to be used for the MDCP. Teflon experienced a significant amount of wear in air and water studies. Nylon did experience little wear, but heat generation was an evident problem. A water study on nylon was not conducted because of its molecular structure.

Adsorption of lead on multi-walled carbon nanotubes with different outer diameters and oxygen contents: kinetics, isotherms and thermodynamics.

PubMed

Yu, Fei; Wu, Yanqing; Ma, Jie; Zhang, Chi

2013-01-01

The effects of different outer diameters and surface oxygen contents on the adsorption of heavy metals onto six types of multi-walled carbon nanotubes (MWCNTs) were investigated in an aqueous solution and lead was chosen as a model metal ion. The results indicated that the percentage removal and adsorption capacity of lead remarkably increased with decreasing outer diameter due to larger specific surface area (SSA). The SSA-normalized maximum adsorption capacity (qmSSA) and SSA-normalized adsorption coefficient (Kd/SSA) were strongly positively correlated with surface oxygen content, implying that lead adsorption onto MWCNTs significantly increases with the rise of oxygen content and decreases with decreasing SSA. The calculated thermodynamic parameters indicated that adsorption of lead on MWCNTs was endothermic and spontaneous. When the oxygen content of MWCNTs increased from 2.0% to 5.9%, the standard free energy (deltaG0) became more negative, which implied that the oxygenated functional groups increased the adsorption affinity of MWCNTs for lead. Through calculation of enthalpy (deltaH0), deltaG0 and free energy of adsorption (Ea), lead adsorption onto MWCNTs was recognized as a chemisorption process. The chemical interaction between lead and the phenolic groups of MWCNTs could be one of the main adsorption mechanisms due to highly positive correlations between the phenolic groups and Kd/SSA or qm/SSA.

Inverse opal photonic crystals with photonic band gaps in the visible and near-infrared

NASA Astrophysics Data System (ADS)

Jarvis, Brandon C.; Gilleland, Cody L.; Renfro, Tim; Gutierrez, Jose; Parikh, Kunjal; Glosser, R.; Landon, Preston B.

2005-08-01

Colloidal silica spheres with 200nm, 250nm, and 290nm diameters were self-assembled with single crystal crystallites 4-5mm wide and 10-15mm long. Larger spheres with diameters between 1000-2300nm were self-assembled with single crystal crystallites up to 1.5mm wide and 2mm long. The silica opals self-assembled vertically along the [100] direction of the face centered cubic lattice resulting in self-templated opals. Inverse opal photonic crystals with a partial band gap possessing a maximum in the near infrared at 3.8μm were constructed from opal templates composed of 2300nm diameter spheres with chalcogenide Ge33As12Se55 (AMTIR-1), a transparent glass in the near infrared with high refractive index. Inverse gold and gold/ polypropylene composite photonic crystals were fabricated from synthetic opal templates composed of 200-290nm silica spheres. The reflectance spectra and electrical conductance of the resulting structures is presented. Gold was infiltrated into opal templates as gold chloride and heat converted to metallic gold. Opals partially infiltrated with gold were co-infiltrated with polypropylene plastic for mechanical support prior to removal of the silica template with hydrofluoric acid.

ZnO and TiO2 particles: a study on nanosafety and photoprotection

NASA Astrophysics Data System (ADS)

Popov, Alexey; Zhao, Xin; Zvyagin, Andrei; Lademann, Jürgen; Roberts, Michael; Sanchez, Washington; Priezzhev, Alexander; Myllylä, Risto

2010-04-01

Nanoparticles of titanium dioxide (TiO2) and zinc oxide (ZnO) are used in sunscreens as protective compounds against UV radiation. We investigate these particles from the viewpoint of nanosafety (penetration into skin in vivo, production of free radicals when UV-irradiated) as well as UV protection. We show that: a) even after multiple applications, the particles remain within stratum corneum (uppermost skin layer); b) the optimal sizes are 62 nm and 45 nm, respectively for TiO2 and ZnO particles for 310-nm light and, correspondingly, 122 and 140 nm - for 400-nm radiation; c) in general, small particles (25 nm in diameter) are more photoactive than the larger ones (400 nm in diameter); however, on the background if porcine skin in vitro this difference is not seen and is substantially surpassed by skin contribution into production of free radicals.

Controllable Fabrication of Non-Close-Packed Colloidal Nanoparticle Arrays by Ion Beam Etching

NASA Astrophysics Data System (ADS)

Yang, Jie; Zhang, Mingling; Lan, Xu; Weng, Xiaokang; Shu, Qijiang; Wang, Rongfei; Qiu, Feng; Wang, Chong; Yang, Yu

2018-06-01

Polystyrene (PS) nanoparticle films with non-close-packed arrays were prepared by using ion beam etching technology. The effects of etching time, beam current, and voltage on the size reduction of PS particles were well investigated. A slow etching rate, about 9.2 nm/min, is obtained for the nanospheres with the diameter of 100 nm. The rate does not maintain constant with increasing the etching time. This may result from the thermal energy accumulated gradually in a long-time bombardment of ion beam. The etching rate increases nonlinearly with the increase of beam current, while it increases firstly then reach its saturation with the increase of beam voltage. The diameter of PS nanoparticles can be controlled in the range from 34 to 88 nm. Based on the non-close-packed arrays of PS nanoparticles, the ordered silicon (Si) nanopillars with their average diameter of 54 nm are fabricated by employing metal-assisted chemical etching technique. Our results pave an effective way to fabricate the ordered nanostructures with the size less than 100 nm.

Improvement of optical damage in specialty fiber at 266 nm wavelength

NASA Astrophysics Data System (ADS)

Tobisch, T.; Ohlmeyer, H.; Zimmermann, H.; Prein, S.; Kirchhof, J.; Unger, S.; Belz, M.; Klein, K.-F.

2014-02-01

Improved multimode UV-fibers with core diameters ranging from 70 to 600 μm diameter have been manufactured based on novel preform modifications and fiber processing techniques. Only E'-centers at 214 nm and NBOHC at 260 nm are generated in these fibers. A new generation of inexpensive laser-systems have entered the market and generated a multitude of new and attractive applications in the bio-life science, chemical and material processing field. However, for example pulsed 355 nm Nd:YAG lasers generate significant UV-damages in commercially available fibers. For lower wavelengths, no results on suitable multi-mode or low-mode fibers with high UV resistance at 266 nm wavelength (pulsed 4th harmonic Nd:YAG laser) have been published. In this report, double-clad fibers with 70 μm or 100 μm core diameter and a large claddingto- core ratio will be recommended. Laser-induced UV-damages will be compared between these new fiber type and traditional UV fibers with similar core sizes. Finally, experimental results will be cross compared against broadband cw deuterium lamp damage standards.

Formation of Size- and Position-Controlled Nanometer Size Pt Dots on GaAs and InP Substrates by Pulsed Electrochemical Deposition

NASA Astrophysics Data System (ADS)

Sato, Taketomo; Kaneshiro, Chinami; HiroshiOkada, HiroshiOkada; Hasegawa, Hideki

1999-04-01

Attempts were made to form regular arrays of size- andposition-controlled Pt-dots on GaAs and InP by combining an insitu electrochemical process with the electron beam (EB)lithography. This utilizes the precipitation of Pt nano-particles atthe initial stage of electrodeposition. First, electrochemicalconditions were optimized in the mode of self-assembled dot arrayformation on unpatterned substrates. Minimum in-plane dot diameters of22 nm and 26 nm on GaAs and InP, respectively, were obtained underthe optimal pulsed mode. Then, Pt dots were selectively formed onpatterned substrates with open circular windows formed by EBlithography, thereby realizing dot-position control. The Pt dot wasfound to have been deposited at the center of each open window, andthe in-plane diameter of the dot could be controlled by the number,width and period of the pulse-waveform applied to substrates. Aminimum diameter of 20 nm was realized in windows with a diameter of100 nm, using a single pulse. Current-voltage (I-V)measurements using an atomic force microscopy (AFM) system with aconductive probe indicated that each Pt dot/n-GaAs contact possessed ahigh Schottky barrier height of about 1 eV.

Achieving sub-50 nm controlled diameter of aperiodic Si nanowire arrays by ultrasonic catalyst removal for photonic applications

NASA Astrophysics Data System (ADS)

Chaliyawala, Harsh A.; Purohit, Zeel; Khanna, Sakshum; Ray, Abhijit; Pati, Ranjan K.; Mukhopadhyay, Indrajit

2018-05-01

We report an alternative approach to fabricate the vertically aligned aperiodic Si nanowire arrays by controlling the diameter of the Ag nanoparticles and tuneable ultrasonic removal. The process begins by sputtering the Ag thin film (t=5 nm) on the Si/SiO2 substrates. Followed by Ag thin film, annealed for various temperature (T=300°C, 400°C, 500°C and 600°C) to selectively achieve a high density, well-spaced and diameter controlled Ag nanoparticles (AgNPs) on the Si/SiO2 substrates. The sacrificial layer of AgNPs size indicates the controlled diameter of the Si nanowire arrays. Image J analysis for various annealed samples gives an indication of the high density, uniformity and equal distribution of closely packed AgNPs. Furthermore, the AgNPs covered with Au/Pd mesh (5 nm) as a template, was removed by ultrasonication in the etchant solution for several times in different intervals of preparation. The conventional and facile metal assisted electroless etching approach was finally employed to fabricate the vertically aperiodic sub-50 nm SiNWAs, can be applicable to various nanoscale opto-electronic applications.

Apparatus for focusing flowing gas streams

DOEpatents

Nogar, N.S.; Keller, R.A.

1985-05-20

Apparatus for focusing gas streams. The principle of hydrodynamic focusing is applied to flowing gas streams in order to provide sample concentration for improved photon and sample utilization in resonance ionization mass spectrometric analysis. In a concentric nozzle system, gas samples introduced from the inner nozzle into the converging section of the outer nozzle are focused to streams 50-250-..mu..m in diameter. In some cases diameters of approximately 100-..mu..m are maintained over distances of several centimeters downstream from the exit orifice of the outer nozzle. The sheath gas employed has been observed to further provide a protective covering around the flowing gas sample, thereby isolating the flowing gas sample from possible unwanted reactions with nearby surfaces. A single nozzle variation of the apparatus for achieving hydrodynamic focusing of gas samples is also described.

Fabrication of Controllable Pore and Particle Size of Mesoporous Silica Nanoparticles via a Liquid-phase Synthesis Method and Its Absorption Characteristics

NASA Astrophysics Data System (ADS)

Nandiyanto, Asep Bayu Dani; Iskandar, Ferry; Okuyama, Kikuo

2011-12-01

Monodisperse spherical mesoporous silica nanoparticles were successfully synthesized using a liquid-phase synthesis method. The result showed particles with controllable pore size from several to tens nanometers with outer diameter of several tens nanometers. The ability in the control of pore size and outer diameter was altered by adjusting the precursor solution ratios. In addition, we have conducted the adsorption ability of the prepared particles. The result showed that large organic molecules were well-absorbed to the prepared silica porous particles, in which this result was not obtained when using commercial dense silica particle and/or hollow silica particle. With this result, the prepared mesoporous silica particles may be used efficiently in various applications, such as sensors, pharmaceuticals, environmentally sensitive pursuits, etc.

In-line rotating capacitive torque sensor

DOEpatents

Kronberg, J.W.

1991-09-10

Disclosed are a method and apparatus for measuring torques developed along a rotating mechanical assembly comprising a rotating inner portion and a stationary outer portion. The rotating portion has an electrically-conductive flexing section fitted between two coaxial shafts in a configuration which varies radially in accordance with applied torque. The stationary portion comprises a plurality of conductive plates forming a surface concentric with and having a diameter slightly larger than the diameter of the rotating portion. The capacitance between the outer, nonrotating and inner, rotating portion varies with changes in the radial configuration of the rotating portion. Signal output varies approximately linearly with torque for small torques, nonlinearly for larger torques. The sensor is preferably surrounded by a conductive shell to minimize electrical interference from external sources. 18 figures.

Angle-resolved reflection spectroscopy of high-quality PMMA opal crystal

NASA Astrophysics Data System (ADS)

Nemtsev, Ivan V.; Tambasov, Igor A.; Ivanenko, Alexander A.; Zyryanov, Victor Ya.

2018-02-01

PMMA opal crystal was prepared by a simple hybrid method, which includes sedimentation, meniscus formation and evaporation. We investigated three surfaces of this crystal by angle-resolved reflective light spectroscopy and SEM study. The angle-resolved reflective measurements were carried out in the 400-1100 nm range. We have determined the high-quality ordered surface of the crystal region. Narrow particle size distribution of the surface has been revealed. The average particle diameter obtained with SEM was nearly 361 nm. The most interesting result was that reflectivity of the surface turned out up to 98% at normal light incidence. Using a fit of dependences of the maximum reflectivity wavelength from an angle based on the Bragg-Snell law, the wavelength of maximum 0° reflectivity, the particle diameter and the fill factor have been determined. For the best surface maximum reflectivity wavelength of a 0° angle was estimated to be 869 nm. The particle diameter and fill factor were calculated as 372 nm and 0.8715, respectively. The diameter obtained by fitting is in excellent agreement with the particle diameter obtained with SEM. The reflectivity maximum is assumed to increase significantly when increasing the fill factor. We believe that using our simple approach to manufacture PMMA opal crystals will significantly increase the fabrication of high-quality photonic crystal templates and thin films.

Effect of diameter of metal nanowires on pool boiling heat transfer with FC-72

NASA Astrophysics Data System (ADS)

Kumar G., Udaya; S., Suresh; M. R., Thansekhar; Babu P., Dinesh

2017-11-01

Effect of varying diameter of metal nanowires on pool boiling heat transfer performance is presented in this study. Copper nanowires (CuNWs) of four different diameters (∼35 nm, ∼70 nm, ∼130 nm and ∼200 nm) were grown directly on copper specimen using template-based electrodeposition technique. Both critical heat flux (CHF) and boiling heat transfer coefficient (h) were found to be improved in surfaces with nanowires as compared to the bare copper surface. Moreover, both the parameters were found to increase with increasing diameter of the nanowires. The percentage increases observed in CHF for the samples with nanowires were 38.37%, 40.16%, 48.48% and 45.57% whereas the percentage increase in the heat transfer coefficient were 86.36%, 95.45%, 184.1% and 131.82% respectively as compared to the bare copper surface. Important reasons believed for this enhancement were improvement in micron scale cavity density and cavity size which arises as a result of the coagulation and grouping of nanowires during the drying process. In addition to this, superhydrophilic nature, capillary effect, and enhanced bubble dynamics parameters (bubble frequency, bubble departure diameter, and nucleation site density) were found to be the concurring mechanisms responsible for this enhancement in heat transfer performance. Qualitative bubble dynamics analysis was done for the surfaces involved and the visual observations are provided to support the results presented and discussed.

Self-assembled clusters of spheres related to spherical codes.

PubMed

Phillips, Carolyn L; Jankowski, Eric; Marval, Michelle; Glotzer, Sharon C

2012-10-01

We consider the thermodynamically driven self-assembly of spheres onto the surface of a central sphere. This assembly process forms self-limiting, or terminal, anisotropic clusters (N-clusters) with well-defined structures. We use Brownian dynamics to model the assembly of N-clusters varying in size from two to twelve outer spheres and free energy calculations to predict the expected cluster sizes and shapes as a function of temperature and inner particle diameter. We show that the arrangements of outer spheres at finite temperatures are related to spherical codes, an ideal mathematical sequence of points corresponding to the densest possible sphere packings. We demonstrate that temperature and the ratio of the diameters of the inner and outer spheres dictate cluster morphology. We present a surprising result for the equilibrium structure of a 5-cluster, for which the square pyramid arrangement is preferred over a more symmetric structure. We show this result using Brownian dynamics, a Monte Carlo simulation, and a free energy approximation. Our results suggest a promising way to assemble anisotropic building blocks from constituent colloidal spheres.

Superconductivity of a Sn film controlled by an array of Co nanowires

NASA Astrophysics Data System (ADS)

Wei, Zhiyuan; Ye, Zuxin; Rathnayaka, Daya; Lyuksyutov, Igor; Wu, Wenhao; Naugle, Donald

2012-02-01

Superconducting properties of a hybrid structure composed of ferromagnetic Co nanowire arrays and a superconducting Sn film have been investigated. Ordered Co nanowires arrays with 60 nm, 150 nm and 200 nm diameter were electroplated into the pores of self organized anodic aluminum oxide (AAO) membranes. Hysteretic dependence of the Sn film superconducting properties on applied magnetic field and critical current enhancement at moderate fields has been observed. This behavior strongly depends on the ratio of the Sn film thickness to the Co nanowire diameter.

Superconductivity of a Sn film controlled by an array of Co nanowires

NASA Astrophysics Data System (ADS)

Wei, Z.; Ye, Z.; Rathnayaka, K. D. D.; Lyuksyutov, I. F.; Wu, W.; Naugle, D. G.

2012-09-01

Superconducting properties of a hybrid structure composed of ferromagnetic Co nanowire arrays and a superconducting Sn film have been investigated. Ordered Co nanowires arrays with 60 nm, 150 nm and 200 nm diameter were electroplated into the pores of self organized Anodic Aluminum Oxide (AAO) membranes. Hysteretic dependence of the Sn film superconducting properties on applied magnetic field and critical current enhancement at moderate fields has been observed. This behavior strongly depends on the ratio of the Sn film thickness to the Co nanowire diameter.

Amorphous iron–chromium oxide nanoparticles with long-term stability

DOE Office of Scientific and Technical Information (OSTI.GOV)

Iacob, Mihail; Institute of Chemistry of ASM, Academiei str. 3, Chisinau 2028, Republic of Moldova; Cazacu, Maria, E-mail: mcazacu@icmpp.ro

2015-05-15

Highlights: • Fe–Cr oxide nanoparticles with pre-established metals ratio were obtained. • The amorphous state and its long-term stability were highlighted by X-ray diffraction. • The average diameter of dried nanoparticles was 3.5 nm, as was estimated by TEM, AFM. • In hexane dispersion, nanoparticles with diameter in the range 2.33–4.85 nm were found. • Superparamagnetic state of NPs co-exists with diamagnetism of the organic layer. - Abstract: Iron–chromium nanoparticles (NPs) were obtained through the thermal decomposition of μ{sub 3}-oxo heterotrinuclear (FeCr{sub 2}O) acetate in the presence of sunflower oil and dodecylamine (DA) as surfactants. The average diameter of themore » NPs was 3.5 nm, as estimated on the basis of transmission electron microscopy and atomic force microscopy images. Both techniques revealed the formation of roughly approximated spheres with some irregularities and agglomerations in larger spherical assemblies of 50–100 nm. In hexane, NPs with diameters in the 2.33–4.85 nm range are individually dispersed, as emphasized by dynamic light scattering measurements. The amorphous nature of the product was emphasized by X-ray powder diffraction. The study of the magnetic properties shows the presence of superparamagnetic state of iron–chromium oxide NPs and the diamagnetic contribution from DA layer forming a shell of NPs.« less

Controlling energy transfer between multiple dopants within a single nanoparticle

PubMed Central

DiMaio, Jeffrey R.; Sabatier, Clément; Kokuoz, Baris; Ballato, John

2008-01-01

Complex core-shell architectures are implemented within LaF3 nanoparticles to allow for a tailored degree of energy transfer (ET) between different rare earth dopants. By constraining specific dopants to individual shells, their relative distance to one another can be carefully controlled. Core-shell LaF3 nanoparticles doped with Tb3+ and Eu3+ and consisting of up to four layers were synthesized with an outer diameter of ≈10 nm. It is found that by varying the thicknesses of an undoped layer between a Tb3+-doped layer and a Eu3+-doped layer, the degree of ET can be engineered to allow for zero, partial, or total ET from a donor ion to an acceptor ion. More specifically, the ratio of the intensities of the 541-nm Tb3+ and 590 nm Eu3+ peaks was tailored from <0.2 to ≈2.4 without changing the overall composition of the particles but only by changing the internal structure. Further, the emission spectrum of a blend of singly doped nanoparticles is shown to be equivalent to the spectra of co-doped particles when a core-shell configuration that restricts ET is used. Beyond simply controlling ET, which can be limiting when designing materials for optical applications, this approach can be used to obtain truly engineered spectral features from nanoparticles and composites made from them. Further, it allows for a single excitation source to yield multiple discrete emissions from numerous lanthanide dopants that heretofore would have been quenched in a more conventional active optical material. PMID:18250307

Analysis of Eddy Current Capabilities for the Detection of Outer Diameter Stress Corrosion Cracking in Small Bore Metallic Structures

NASA Technical Reports Server (NTRS)

Wincheski, Buzz; Williams, Phillip; Simpson, John

2007-01-01

The use of eddy current techniques for the detection of outer diameter damage in tubing and many complex aerospace structures often requires the use of an inner diameter probe due to a lack of access to the outside of the part. In small bore structures the probe size and orientation are constrained by the inner diameter of the part, complicating the optimization of the inspection technique. Detection of flaws through a significant remaining wall thickness becomes limited not only by the standard depth of penetration, but also geometrical aspects of the probe. Recently, an orthogonal eddy current probe was developed for detection of such flaws in Space Shuttle Primary Reaction Control System (PRCS) Thrusters. In this case, the detection of deeply buried stress corrosion cracking by an inner diameter eddy current probe was sought. Probe optimization was performed based upon the limiting spatial dimensions, flaw orientation, and required detection sensitivity. Analysis of the probe/flaw interaction was performed through the use of finite and boundary element modeling techniques. Experimental data for the flaw detection capabilities, including a probability of detection study, will be presented along with the simulation data. The results of this work have led to the successful deployment of an inspection system for the detection of stress corrosion cracking in Space Shuttle Primary Reaction Control System (PRCS) Thrusters.

Tungsten migration in Alcator C-Mod: sputtering and melting

NASA Astrophysics Data System (ADS)

Wright, G. M.; Barnard, H.; Lipschultz, B.; Whyte, D. G.

2010-11-01

A row of bulk tungsten (W) tiles were installed near the typical outer strike-point location in the Alcator C-Mod divertor in 2007. In the 2009/2010 campaign, one of the W tiles mechanically failed resulting in significant W melting at that location. Post-campaign PIXE surface analysis has been used to observe tungsten (W) deposition and migration patterns in the divertor for the typical operations (sputtering only) and operation with melted components. For sputtering conditions, W deposition of up to 20 nm equivalent thickness is observed at various divertor surfaces indicating prompt re-deposition at the outer divertor, neutral and ion transport through the private-flux region and ion transport in the scrape off layer. For melting conditions, W deposition of up to 400 nm equivalent thickness is observed at some locations at the outer divertor. However, the toroidal distribution of W on the outer divertor is strongly non-uniform. There is no W deposition measured on the inner wall limiter. These results indicate that impurity migration is affected by the erosion mechanism and source, with the migration from melting being less predictable and uniform than from the sputtering case. Supported by USDoE award DE-SC00-02060.

Diameter dependent thermoelectric properties of individual SnTe nanowires

DOE PAGES

Xu, E. Z.; Li, Z.; Martinez, J. A.; ...

2015-01-15

The lead-free compound tin telluride (SnTe) has recently been suggested to be a promising thermoelectric material. In this work, we report on the first thermoelectric study of individual single-crystalline SnTe nanowires with different diameters ranging from ~ 218 to ~ 913 nm. Measurements of thermopower S, electrical conductivity σ and thermal conductivity κ were carried out on the same nanowires over a temperature range of 25 - 300 K. While the electrical conductivity does not show a strong diameter dependence, the thermopower increases by a factor of two when the nanowire diameter is decreased from ~ 913 nm to ~more » 218 nm. The thermal conductivity of the measured NWs is lower than that of the bulk SnTe, which may arise from the enhanced phonon - surface boundary scattering and phonon-defect scattering. Lastly, temperature dependent figure of merit ZT was determined for individual nanowires and the achieved maximum value at room temperature is about three times higher than that in bulk samples of comparable carrier density.« less

Combination of small size and carboxyl functionalisation causes cytotoxicity of short carbon nanotubes

PubMed Central

Fröhlich, Eleonore; Meindl, Claudia; Höfler, Anita; Leitinger, Gerd; Roblegg, Eva

2012-01-01

The use of carbon nanotubes (CNTs) could improve medical diagnosis and treatment provided they show no adverse effects in the organism. In this study, short CNTs with different diameters with and without carboxyl surface functionalisation were assessed. After physicochemical characterisation, cytotoxicity in phagocytic and non-phagocytic cells was determined. The role of oxidative stress was evaluated according to the intracellular glutathione levels and protection by N-acetyl cysteine (NAC). In addition to this, the mode of cell death was also investigated. CNTs <8 nm acted more cytotoxic than CNTs ≥20 nm and carboxylated CNTs more than pristine CNTs. Protection by NAC was maximal for large diameter pristine CNTs and minimal for small diameter carboxylated CNTs. Thin (<8 nm) CNTs acted mainly by disruption of membrane integrity and CNTs with larger diameter induced mainly apoptotic changes. It is concluded that cytotoxicity of small carboxylated CNTs occurs by necrosis and cannot be prevented by antioxidants. PMID:22963691

Magnetic vortices in nanocaps induced by curvature

NASA Astrophysics Data System (ADS)

Abdelgawad, Ahmed M.; Nambiar, Nikhil; Bapna, Mukund; Chen, Hao; Majetich, Sara A.

2018-05-01

Magnetic nanoparticles with room temperature remanent magnetic vortices stabilized by their curvature are very intriguing due to their potential use in biomedicine. In the present study, we investigate room temperature magnetic chirality in 100 nm diameter permalloy spherical caps with 10 nm and 30 nm thicknesses. Micromagnetic OOMMF simulations predict the equilibrium spin structure for these caps to form a vortex state. We fabricate the permalloy caps by sputtering permalloy on both close-packed and sparse arrays of polystyrene nanoparticles. Magnetic force microscopy scans show a clear signature of a vortex state in close-packed caps of both 10 nm and 30 nm thicknesses. Alternating gradient magnetometry measurements of the caps are consistent with a remnant vortex state in 30 nm thick caps and a transition to an onion state followed by a vortex state in 10 nm thick caps. Out-of-plane measurements supported by micromagnetic simulations shows that an out-of-plane field can stabilize a vortex state down to a diameter of 15 nm.

Process for the manufacture of seamless metal-clad fiber-reinforced organic matrix composite structures

NASA Technical Reports Server (NTRS)

Bluck, Raymond M. (Inventor); Bush, Harold G. (Inventor); Johnson, Robert R. (Inventor)

1991-01-01

A process for producing seamless metal-clad composite structures includes providing a hollow, metallic inner member and an outer sleeve to surround the inner member and define an inner space therebetween. A plurality of continuous reinforcing fibers is attached to the distal end of the outside diameter of the inner member, and the inner member is then introduced, distal end first, into one end of the outer sleeve. The inner member is then moved, distal end first, into the outer sleeve until the inner member is completely enveloped by the outer sleeve. A liquid matrix material is then injected into the space containing the reinforcing fibers between the inner member and the outer sleeve. Next a pressurized heat transfer medium is passed through the inner member to cure the liquid matrix material. Finally, the wall thickness of both the inner member and the outer sleeve are reduced to desired dimensions by chemical etching, which adjusts the thermal expansion coefficient of the metal-clad composite structure to a desired value.

Magneto-plasmonic Au-Coated Co nanoparticles synthesized via hot-injection method

NASA Astrophysics Data System (ADS)

Souza, João B., Jr.; Varanda, Laudemir C.

2018-02-01

A synthetic procedure is described for the obtaining of superparamagnetic Co nanoparticles (NPs) via hot-injection method in the presence of sodium borohydride. The Co NPs obtained have an average diameter of 5.3 nm and saturation magnetization of 115 emu g-1. A modified Langevin equation is fitted to the magnetization curves using a log-normal distribution for the particle diameter and an effective field to account for dipolar interactions. The calculated magnetic diameter of the Co NPs is 0.6 nm smaller than TEM-derived values, implying a magnetic dead layer of 0.3 nm. The magnetic core is coated with Au to prevent oxidation, resulting in water-stable magneto-plasmonic Co/Au core/shell NPs with saturation of 71.6 emu g-1. The coating adds a localized surface plasmon resonance property with absorbance in the so-called ‘therapeutic window’ (690-900 nm), suitable for biomedical applications. It is suggested that these multifunctional NPs are distinguished as a potential platform for applied and fundamental research.

Broadband visible light source based on AllnGaN light emitting diodes

DOEpatents

Crawford, Mary H.; Nelson, Jeffrey S.

2003-12-16

A visible light source device is described based on a light emitting diode and a nanocluster-based film. The light emitting diode utilizes a semiconductor quantum well structure between n-type and p-type semiconductor materials on the top surface a substrate such as sapphire. The nanocluster-based film is deposited on the bottom surface of the substrate and can be derived from a solution of MoS.sub.2, MoSe.sub.2, WS.sub.2, and WSe.sub.2 particles of size greater than approximately 2 nm in diameter and less than approximately 15 nm in diameter, having an absorption wavelength greater than approximately 300 nm and less than approximately 650 nm.

Potential health effects of fume particles on the crew of spacecrafts

NASA Technical Reports Server (NTRS)

Ferin, Juraj; Oberdorster, Gunter

1992-01-01

The effect of the size of polymer (e.g., Teflon) particles in fumes inhaled by spacecraft personnel on the condition of the lung tissue and on the recovery of the exposed subjects was investigated in rats receiving a single intrapulmonary instillation, or repeated inhalation exposures to either TiO2 particles with primary particle diameter 20 nm, or TiO2 particles with primary particle diameter 250 nm. It was found that rats exposed to 20-nm-diam particles showed a dramatically higher toxicity and slower recovery compared to the group exposed to the 250-nm-diam particles, due to a larger extent of penetration of the interstitium of the lung by the finer particles.

Cenosphere formation from heavy fuel oil: a numerical analysis accounting for the balance between porous shells and internal pressure

NASA Astrophysics Data System (ADS)

Reddy, Vanteru M.; Rahman, Mustafa M.; Gandi, Appala N.; Elbaz, Ayman M.; Schrecengost, Robert A.; Roberts, William L.

2016-01-01

Heavy fuel oil (HFO) as a fuel in industrial and power generation plants ensures the availability of energy at economy. Coke and cenosphere emissions from HFO combustion need to be controlled by particulate control equipment such as electrostatic precipitators, and collection effectiveness is impacted by the properties of these particulates. The cenosphere formation is a function of HFO composition, which varies depending on the source of the HFO. Numerical modelling of the cenosphere formation mechanism presented in this paper is an economical method of characterising cenosphere formation potential for HFO in comparison to experimental analysis of individual HFO samples, leading to better control and collection. In the present work, a novel numerical model is developed for understanding the global cenosphere formation mechanism. The critical diameter of the cenosphere is modelled based on the balance between two pressures developed in an HFO droplet. First is the pressure (Prpf) developed at the interface of the liquid surface and the inner surface of the accumulated coke due to the flow restriction of volatile components from the interior of the droplet. Second is the pressure due to the outer shell strength (PrC) gained from van der Walls energy of the coke layers and surface energy. In this present study it is considered that when PrC ≥ Prpf the outer shell starts to harden. The internal motion in the shell layer ceases and the outer diameter (DSOut) of the shell is then fixed. The entire process of cenosphere formation in this study is analysed in three phases: regression, shell formation and hardening, and post shell hardening. Variations in pressures during shell formation are analysed. Shell (cenosphere) dimensions are evaluated at the completion of droplet evaporation. The rate of fuel evaporation, rate of coke formation and coke accumulation are analysed. The model predicts shell outer diameters of 650, 860 and 1040 µm, and inner diameters are 360, 410 and 430 µm respectively, for 700, 900 and 1100 µm HFO droplets. The present numerical model is validated with experimental results available from the literature. Total variation between computational and experimental results is in the range of 3-7%.

Evanescent wave DNA-aptamer biosensor based on long period gratings for the specific recognition of E. coli outer membrane proteins.

PubMed

Queirós, R B; Gouveia, C; Fernandes, J R A; Jorge, P A S

2014-12-15

An evanescent wave fiber optic sensor for detection of Escherichia coli (E. coli) outer membranes proteins (EcOMPs) using long period gratings (LPGs) as a refractometric platform is presented. The sensing probes were attained by the functionalization of LPGs inscribed in single mode fiber using two different methods of immobilization; electrostatic assembly and covalent binding. The resulting label-free configuration enabled the specific recognition of EcOMPs in water by monitoring the resonance wavelength shift due to refractive index changes induced by binding events. The sensors displayed linear responses in the range of 0.1 nM to 10 nM EcOMPs with sensitivities of -0.1563±0.005 nm decade(-1) [EcOMP, M] (electrostatic method) and -0.1597±0.004 nm decade(-1) [EcOMP, M] (covalent method). The devices could be regenerated (under low pH conditions) with a deviation less than 0.1% for at least three subsequent detection events. The sensors were also applied to spiked environmental water samples. Copyright © 2014 Elsevier B.V. All rights reserved.

Diameter modulation of vertically aligned single-walled carbon nanotubes.

PubMed

Xiang, Rong; Einarsson, Erik; Murakami, Yoichi; Shiomi, Junichiro; Chiashi, Shohei; Tang, Zikang; Maruyama, Shigeo

2012-08-28

We demonstrate wide-range diameter modulation of vertically aligned single-walled carbon nanotubes (SWNTs) using a wet chemistry prepared catalyst. In order to ensure compatibility to electronic applications, the current minimum mean diameter of 2 nm for vertically aligned SWNTs is challenged. The mean diameter is decreased to about 1.4 nm by reducing Co catalyst concentrations to 1/100 or by increasing Mo catalyst concentrations by five times. We also propose a novel spectral analysis method that allows one to distinguish absorbance contributions from the upper, middle, and lower parts of a nanotube array. We use this method to quantitatively characterize the slight diameter change observed along the array height. On the basis of further investigation of the array and catalyst particles, we conclude that catalyst aggregation-rather than Ostwald ripening-dominates the growth of metal particles.

Synthesis of subnanometer-diameter vertically aligned single-walled carbon nanotubes with copper-anchored cobalt catalysts

NASA Astrophysics Data System (ADS)

Cui, Kehang; Kumamoto, Akihito; Xiang, Rong; An, Hua; Wang, Benjamin; Inoue, Taiki; Chiashi, Shohei; Ikuhara, Yuichi; Maruyama, Shigeo

2016-01-01

We synthesize vertically aligned single-walled carbon nanotubes (VA-SWNTs) with subnanometer diameters on quartz (and SiO2/Si) substrates by alcohol CVD using Cu-anchored Co catalysts. The uniform VA-SWNTs with a nanotube diameter of 1 nm are synthesized at a CVD temperature of 800 °C and have a thickness of several tens of μm. The diameter of SWNTs was reduced to 0.75 nm at 650 °C with the G/D ratio maintained above 24. Scanning transmission electron microscopy energy-dispersive X-ray spectroscopy (EDS-STEM) and high angle annular dark field (HAADF-STEM) imaging of the Co/Cu bimetallic catalyst system showed that Co catalysts were captured and anchored by adjacent Cu nanoparticles, and thus were prevented from coalescing into a larger size, which contributed to the small diameter of SWNTs. The correlation between the catalyst size and the SWNT diameter was experimentally clarified. The subnanometer-diameter and high-quality SWNTs are expected to pave the way to replace silicon for next-generation optoelectronic and photovoltaic devices.We synthesize vertically aligned single-walled carbon nanotubes (VA-SWNTs) with subnanometer diameters on quartz (and SiO2/Si) substrates by alcohol CVD using Cu-anchored Co catalysts. The uniform VA-SWNTs with a nanotube diameter of 1 nm are synthesized at a CVD temperature of 800 °C and have a thickness of several tens of μm. The diameter of SWNTs was reduced to 0.75 nm at 650 °C with the G/D ratio maintained above 24. Scanning transmission electron microscopy energy-dispersive X-ray spectroscopy (EDS-STEM) and high angle annular dark field (HAADF-STEM) imaging of the Co/Cu bimetallic catalyst system showed that Co catalysts were captured and anchored by adjacent Cu nanoparticles, and thus were prevented from coalescing into a larger size, which contributed to the small diameter of SWNTs. The correlation between the catalyst size and the SWNT diameter was experimentally clarified. The subnanometer-diameter and high-quality SWNTs are expected to pave the way to replace silicon for next-generation optoelectronic and photovoltaic devices. Electronic supplementary information (ESI) available: Comparison between the Co monometallic catalyst system and the Co/Mo bimetallic catalyst system, the effect of CVD temperature on the G/D ratio, the effect of ethanol partial pressure on the morphology, diameter and quality of SWNT films, and Raman spectra of the Si/SiO2 substrate. See DOI: 10.1039/c5nr06007a

A water-based fast integrated mobility spectrometer (WFIMS) with enhanced dynamic size range

DOE Office of Scientific and Technical Information (OSTI.GOV)

Pinterich, Tamara; Spielman, Steven R.; Hering, Susanne

We developed a water-based fast integrated mobility spectrometer (WFIMS) with enhanced dynamic size range. The WFIMS builds on two established technologies: the fast integrated mobility spectrometer and laminar flow water-based condensation methodology. Inside WFIMS, particles of differing electrical mobility are separated in a drift tube and subsequently enlarged through water condensation. Particle size and concentration are measured via digital imaging at a frame rate of 10 Hz. When we measure particles of different mobilities simultaneously, the WFIMS resolves particle diameters ranging from 8 to 580 nm within 1 s or less. The performance of WFIMS was characterized with differential mobilitymore » analyzer (DMA) classified (NH 4) 2SO 2 particles with diameters ranging from 8 to 265 nm. The mean particle diameters measured by WFIMS were found to be in excellent agreement with DMA centroid diameters. Furthermore, detection efficiency of WFIMS was characterized using a condensation particle counter as a reference and is nearly 100% for particles with diameter greater than 8 nm. In general, measured and simulated WFIMS mobility resolutions are in good agreement. But, some deviations are observed at low particle mobilities, likely due to the non-idealities of the WFIMS electric field.« less

A water-based fast integrated mobility spectrometer (WFIMS) with enhanced dynamic size range

DOE PAGES

Pinterich, Tamara; Spielman, Steven R.; Hering, Susanne; ...

2017-06-08

We developed a water-based fast integrated mobility spectrometer (WFIMS) with enhanced dynamic size range. The WFIMS builds on two established technologies: the fast integrated mobility spectrometer and laminar flow water-based condensation methodology. Inside WFIMS, particles of differing electrical mobility are separated in a drift tube and subsequently enlarged through water condensation. Particle size and concentration are measured via digital imaging at a frame rate of 10 Hz. When we measure particles of different mobilities simultaneously, the WFIMS resolves particle diameters ranging from 8 to 580 nm within 1 s or less. The performance of WFIMS was characterized with differential mobilitymore » analyzer (DMA) classified (NH 4) 2SO 2 particles with diameters ranging from 8 to 265 nm. The mean particle diameters measured by WFIMS were found to be in excellent agreement with DMA centroid diameters. Furthermore, detection efficiency of WFIMS was characterized using a condensation particle counter as a reference and is nearly 100% for particles with diameter greater than 8 nm. In general, measured and simulated WFIMS mobility resolutions are in good agreement. But, some deviations are observed at low particle mobilities, likely due to the non-idealities of the WFIMS electric field.« less

Diameter-dependent optical constants of gold mesoparticles electrodeposited on aluminum films containing copper.

PubMed

Brevnov, Dmitri A; Bungay, Corey

2005-08-04

Electrodeposition of gold mesoparticles on anodized and chemically etched aluminum/copper films deposited on silicon wafers proceeds by instantaneous nucleation and with no diffusion limitations. Both of these phenomena favor the formation of relatively monodispersed gold particles. Under the reported electrodeposition conditions, the relative standard deviation of the particle diameter is 25%. The particle coverage is 7 x 10(8) particles cm(-2). The mean particle diameter varies as a function of electrodeposition time in the range of 40-80 nm. Optical constants of gold mesoparticles are resolved by spectroscopic ellipsometry. A two-layer optical model is constructed to determine both extinction coefficients and refractive indexes of gold mesoparticles as a function of the mean particle diameter. The absorption peak, associated with surface plasmons, is modeled with two Lorentz oscillators. Absorption peak maximums shift from 610 to 675 nm as the mean particle diameter increases from 42 to 74 nm. Electrodeposition of gold particles on technologically relevant substrates, such as aluminum/copper films, is expected to increase the utility of gold particles and facilitate their incorporation in nanostructured materials and a variety of electronic and optical devices.

Translocation of 40 nm diameter nanowires through the intestinal epithelium of Daphnia magna

PubMed Central

Mattsson, Karin; Adolfsson, Karl; Ekvall, Mikael T.; Borgström, Magnus T.; Linse, Sara; Hansson, Lars-Anders; Cedervall, Tommy; Prinz, Christelle N.

2016-01-01

Abstract Nanowires (NWs) have unique electrical and optical properties of value for many applications including lighting, sensing, and energy harnessing. Consumer products containing NWs increase the risk of NWs being released in the environment, especially into aquatic ecosystems through sewage systems. Daphnia magna is a common, cosmopolitan freshwater organism sensitive to toxicity tests and represents a likely entry point for nanoparticles into food webs of aquatic ecosystems. Here we have evaluated the effect of NW diameter on the gut penetrance of NWs in Daphnia magna. The animals were exposed to NWs of two diameters (40 and 80 nm) and similar length (3.6 and 3.8 μm, respectively) suspended in water. In order to locate the NWs in Daphnia, the NWs were designed to comprise one inherently fluorescent segment of gallium indium phosphide (GaInP) flanked by a gallium phosphide (GaP) segment. Daphnia mortality was assessed directly after 24 h of exposure and 7 days after exposure. Translocation of NWs across the intestinal epithelium was investigated using confocal fluorescence microscopy directly after 24 h of exposure and was observed in 89% of Daphnia exposed to 40 nm NWs and in 11% of Daphnia exposed to 80 nm NWs. A high degree of fragmentation was observed for NWs of both diameters after ingestion by the Daphnia, although 40 nm NWs were fragmented to a greater extent, which could possibly facilitate translocation across the intestinal epithelium. Our results show that the feeding behavior of animals may enhance the ability of NWs to penetrate biological barriers and that penetrance is governed by the NW diameter. PMID:27181920

Quantitative characterization of gold nanoparticles by field-flow fractionation coupled online with light scattering detection and inductively coupled plasma mass spectrometry.

PubMed

Schmidt, Bjørn; Loeschner, Katrin; Hadrup, Niels; Mortensen, Alicja; Sloth, Jens J; Koch, Christian Bender; Larsen, Erik H

2011-04-01

An analytical platform coupling asymmetric flow field-flow fractionation (AF(4)) with multiangle light scattering (MALS), dynamic light scattering (DLS), and inductively coupled plasma mass spectrometry (ICPMS) was established and used for separation and quantitative determination of size and mass concentration of nanoparticles (NPs) in aqueous suspension. Mixtures of three polystyrene (PS) NPs between 20 and 100 nm in diameter and mixtures of three gold (Au) NPs between 10 and 60 nm in diameter were separated by AF(4). The geometric diameters of the separated PS NPs and the hydrodynamic diameters of the Au and PS NPs were determined online by MALS and DLS, respectively. The three separated Au NPs were quantified by ICPMS and recovered at 50-95% of the injected masses, which ranged between approximately 8-80 ng of each nanoparticle size. Au NPs adhering to the membrane in the separation channel was found to be a major cause for incomplete recoveries. The lower limit of detection (LOD) ranged between 0.02 ng Au and 0.4 ng Au, with increasing LOD by increasing nanoparticle diameter. The analytical platform was applied to characterization of Au NPs in livers of rats, which were dosed with 10 nm, 60 nm, or a mixture of 10 and 60 nm nanoparticles by intravenous injection. The homogenized livers were solubilized in tetramethylammonium hydroxide (TMAH), and the recovery of Au NPs from the livers amounted to 86-123% of their total Au content. In spite of successful stabilization with bovine serum albumin even in alkaline medium, separation of the Au NPs by AF(4) was not possible due to association with undissolved remains of the alkali-treated liver tissues as demonstrated by electron microscopy images.

Hierarchically assembled Au microspheres and sea urchin-like architectures: formation mechanism and SERS study

NASA Astrophysics Data System (ADS)

Wang, Xiansong; Yang, Da-Peng; Huang, Peng; Li, Min; Li, Chao; Chen, Di; Cui, Daxiang

2012-11-01

The hierarchically assembled Au microspheres/sea urchin-like structures have been synthesized in aqueous solution at room temperature with and without proteins (bovine serum albumin, BSA) as mediators. The average diameter of an individual Au microsphere is 300-600 nm, which is composed of some compact nanoparticles with an average diameter of about 15 nm. Meanwhile, the sea urchin-like Au architecture exhibits an average diameter of 600-800 nm, which is made up of some nanopricks with an average length of 100-200 nm. These products are characterized by means of scanning electron microscopy (SEM), X-ray diffraction (XRD) and transmission electronic microscopy (TEM). It is found that the BSA and ascorbic acid (AA) have great effects on the morphology of the resulting products. Two different growth mechanisms are proposed. The study on surface enhanced Raman scattering (SERS) activities is also carried out between Au microspheres and Au sea urchin-like architectures. It is found that Au urchin-like architectures possess much higher SERS activity than the Au microspheres. Our work may shed light on the design and synthesis of hierarchically self-assembled 3D micro/nano-architectures for SERS, catalysis and biosensors.The hierarchically assembled Au microspheres/sea urchin-like structures have been synthesized in aqueous solution at room temperature with and without proteins (bovine serum albumin, BSA) as mediators. The average diameter of an individual Au microsphere is 300-600 nm, which is composed of some compact nanoparticles with an average diameter of about 15 nm. Meanwhile, the sea urchin-like Au architecture exhibits an average diameter of 600-800 nm, which is made up of some nanopricks with an average length of 100-200 nm. These products are characterized by means of scanning electron microscopy (SEM), X-ray diffraction (XRD) and transmission electronic microscopy (TEM). It is found that the BSA and ascorbic acid (AA) have great effects on the morphology of the resulting products. Two different growth mechanisms are proposed. The study on surface enhanced Raman scattering (SERS) activities is also carried out between Au microspheres and Au sea urchin-like architectures. It is found that Au urchin-like architectures possess much higher SERS activity than the Au microspheres. Our work may shed light on the design and synthesis of hierarchically self-assembled 3D micro/nano-architectures for SERS, catalysis and biosensors. Electronic supplementary information (ESI) available. See DOI: 10.1039/c2nr32405a

Optimizing heterosurface adsorbent synthesis for liquid chromatography

NASA Astrophysics Data System (ADS)

Bogoslovskii, S. Yu.; Serdan, A. A.

2016-03-01

The structural and geometric parameters of a silica matrix (SM) for the synthesis of heterosurface adsorbents (HAs) are optimized. Modification is performed by shielding the external surfaces of alkyl-modified silica (AS) using human serum albumin and its subsequent crosslinking. The structural and geometric characteristics of the SM, AS, and HA are measured via low-temperature nitrogen adsorption. It is found that the structural characteristics of AS pores with diameters D < 6 nm do not change during HA synthesis, while the volume of pores with diameters of 6 nm < D < 9 nm shrinks slightly due to the adsorption of albumin in the pore orifices. It is established that the volume of pores with diameters D > 9 nm reduces significantly due to adsorption of albumin. It is concluded that silica gel with a maximum pore size distribution close to 5 nm and a minimal proportion of pores with D > 9 nm is optimal for HA synthesis; this allows us to achieve the greatest similarity between the chromatographic retention parameters for HA and AS. The suitability of the synthesized adsorbents for analyzing drugs in biological fluids through direct sample injection is confirmed by chromatography. It was found that the percentage of the protein fraction detected at the outlet of the chromatographic column is 98%.

Pulmonary inflammation induced by bacteria-free outer membrane vesicles from Pseudomonas aeruginosa.

PubMed

Park, Kyong-Su; Lee, Jaewook; Jang, Su Chul; Kim, Sae Rom; Jang, Myoung Ho; Lötvall, Jan; Kim, Yoon-Keun; Gho, Yong Song

2013-10-01

Pseudomonas aeruginosa is often involved in lung diseases such as cystic fibrosis. These bacteria can release outer membrane vesicles (OMVs), which are bilayered proteolipids with diameters of approximately 20 to 250 nm. In vitro, these OMVs activate macrophages and airway epithelial cells. The aim of this study was to determine whether OMVs from P. aeruginosa can induce pulmonary inflammation in vivo and to elucidate the mechanisms involved. Bacteria-free OMVs were isolated from P. aeruginosa cultures. Wild-type, Toll-like receptor (TLR)2 and TLR4 knockout mice were exposed to OMVs by the airway, and inflammation in the lung was assessed using differential counts, histology, and quantification of chemokines and cytokines. The involvement of the TLR2 and TLR4 pathways was studied in human cells using transfection. OMVs given to the mouse lung caused dose- and time-dependent pulmonary cellular inflammation. Furthermore, OMVs increased concentrations of several chemokines and cytokines in the mouse lungs and mouse alveolar macrophages. The inflammatory responses to OMVs were comparable to those of live bacteria and were only partly regulated by the TLR2 and TLR4 pathways, according to studies in knockout mice. This study shows that OMVs from P. aeruginosa cause pulmonary inflammation without live bacteria in vivo. This effect is only partly controlled by TLR2 and TLR4. The role of OMVs in clinical disease warrants further studies because targeting of OMVs in addition to live bacteria may add clinical benefit compared with treating with antibiotics alone.

Lipid detection by intravascular photoacoustic imaging with flexible catheter at 20 fps (Conference Presentation)

NASA Astrophysics Data System (ADS)

Wu, Min; Daeichin, Verya; Springeling, Geert; van der Steen, Antonius F. W.; van Soest, Gijs

2016-02-01

Intravascular Photoacoustic (IVPA) imaging is a promising new technology to assess lipid content of coronary atherosclerotic plaque, an important determinant of the risk associated with the plaque triggering a heart attack. Clinical translation of IVPA imaging requires real-time image acquisition, which has been a technological challenge. In this work, we demonstrate a high-speed, dual-wavelength IVPA imaging system at 1.7 µm wavelength, operating with a flexible catheter of 1.2 mm outer diameter (including outer sheath). The catheter was custom designed and fabricated, and used a 40 MHz transducer for intravascular ultrasound (IVUS) and IVPA imaging. The optical excitation is provided by a dual OPO system, pumped by CW diode-pumped Q-switched Nd:YAG lasers, with a repetition rate of 5 kHz. Each OPO can be tuned to a custom wavelength between 1690 and 1750 nm; two wavelengths only are needed to discriminate between plaque lipids and adipose tissue. The pulse energy is about 80 µJ. We tested the imaging performance of the presented system in a polyvinyl-alcohol (PVA) vessel mimicking phantom and human coronary arteries ex vivo. IVPA identified lipid deposits inside atherosclerotic plaque, while IVUS showed tissue structure. We demonstrated IVPA imaging at a speed of 20 frames per second, with 250 A-scans per frame. This is significantly faster than previous IVPA imaging systems, and will enable the translation of IVPA imaging into clinical practice.

Deposition of silver nanoparticles on multiwalled carbon nanotubes by chemical reduction process and their antimicrobial effects

DOE Office of Scientific and Technical Information (OSTI.GOV)

Haider, Adawiya J., E-mail: adawiyahaider@yahoo.com; Thamir, Amin D.; Ahmed, Duha S.

In this paper, the functionalization of raw-MWCNTs involves oxidation reaction using concentrated acid mixture of HNO{sub 3}:H{sub 2}SO{sub 4} (1:3), via ultrasonic bath (170 W, 50 kHz) to obtain functional groups. Then Ag nanoparticles are decorated the outside over the surface of functionalized MWCNTs using a chemical reduction process resulting in the formation of(Ag/ MWCNTs) hybrid material. The results showed that outer diameter functionalized F-MWCNTs andAg nanoparticles size was about (11-80) nm and (10 to 25) nm, respectively using TEM and HRTEM. The crystallographic structure of MWCNTs using X-ray diffraction (XRD) analysis proved diffraction peaks at 38.1°, 44.3°, 64.7° andmore » 77.4° degrees namely, Ag (111), Ag (200), Ag (220), and Ag (311) of the face-centered cubic lattice of Ag, respectively, excepting the peak at 2θ =25.6°, which correspond to the (0 0 2) reflection of the MWNTs are corresponding to Ag/MWNTs. The antimicrobial activities of Ag/MWCNTs hybrid using plate count method showed that decreasing a large number of bacteria colonies of E. coli and S. aureu with increasing the hybrid concentrations after incubation for 24 h in shaker incubator with percentage of inhibition approaching 100%.« less

Sutureless closure of scleral wounds in animal models by the use of laser welded biocompatible patches

NASA Astrophysics Data System (ADS)

Rossi, Francesca; Matteini, Paolo; Menabuoni, Luca; Lenzetti, Ivo; Pini, Roberto

2011-03-01

The common procedures used to seal the scleral or conjunctival injuries are based on the traditional suturing techniques, that may induce foreign body reaction during the follow up, with subsequent inflammation and distress for the patient. In this work we present an experimental study on the laser welding of biocompatible patches onto ocular tissues, for the closure of surgical or trauma wounds. The study was performed ex vivo in animal models (porcine eyes). A penetrating perforation of the ocular tissue was performed with a surgical knife. The wound walls were approximated, and a biocompatible patch was put onto the outer surface of the tissue, in order to completely cover the wound as a plaster. The patches were prepared with a biocompatible and biodegradable polymer, showing high mechanical strength, good elasticity, high permeability for vapour and gases and rather low biodegradation. During preparation, Indocyanine Green (ICG) was included in the biopolymeric matrix, so that the films presented high absorption at 810 nm. Effective adhesion of the membranes to the ocular tissues was obtained by using diode laser light emitted from an 810 nm diode laser and delivered by means of a 300 μm core diameter optical fiber, to produce spots of local film/tissue adhesion, due to the photothermal effect at the interface. The result is an immediate closure of the wound, thus reducing post-operative complications due to inflammation.

Efficient active waveguiding properties of Mo6 nano-cluster-doped polymer nanotubes

NASA Astrophysics Data System (ADS)

Bigeon, J.; Huby, N.; Amela-Cortes, M.; Molard, Y.; Garreau, A.; Cordier, S.; Bêche, B.; Duvail, J.-L.

2016-06-01

We investigate 1D nanostructures based on a Mo6@SU8 hybrid nanocomposite in which photoluminescent Mo6 clusters are embedded in the photosensitive SU8 resist. Tens of micrometers long Mo6@SU8-based tubular nanostructures were fabricated by the wetting template method, enabling the control of the inner and outer diameter to about 190 nm and 240 nm respectively, as supported by structural and optical characterizations. The image plane optical study of these nanotubes under optical pumping highlights the efficient waveguiding phenomenon of the red luminescence emitted by the clusters. Moreover, the wave vector distribution in the Fourier plane determined by leakage radiation microscopy gives additional features of the emission and waveguiding. First, the anisotropic red luminescence of the whole system can be attributed to the guided mode along the nanotube. Then, a low-loss propagation behavior is evidenced in the Mo6@SU8-based nanotubes. This result contrasts with the weaker waveguiding signature in the case of UV210-based nanotubes embedding PFO (poly(9,9-di-n-octylfluorenyl-2,7-diyl)). It is attributed to the strong reabsorption phenomenon, owing to overlapping between absorption and emission bands in the semi-conducting conjugated polymer PFO. These results make this Mo6@SU8 original class of nanocomposite a promising candidate as nanosources for submicronic photonic integration.

Efficient active waveguiding properties of Mo6 nano-cluster-doped polymer nanotubes.

PubMed

Bigeon, J; Huby, N; Amela-Cortes, M; Molard, Y; Garreau, A; Cordier, S; Bêche, B; Duvail, J-L

2016-06-24

We investigate 1D nanostructures based on a Mo6@SU8 hybrid nanocomposite in which photoluminescent Mo6 clusters are embedded in the photosensitive SU8 resist. Tens of micrometers long Mo6@SU8-based tubular nanostructures were fabricated by the wetting template method, enabling the control of the inner and outer diameter to about 190 nm and 240 nm respectively, as supported by structural and optical characterizations. The image plane optical study of these nanotubes under optical pumping highlights the efficient waveguiding phenomenon of the red luminescence emitted by the clusters. Moreover, the wave vector distribution in the Fourier plane determined by leakage radiation microscopy gives additional features of the emission and waveguiding. First, the anisotropic red luminescence of the whole system can be attributed to the guided mode along the nanotube. Then, a low-loss propagation behavior is evidenced in the Mo6@SU8-based nanotubes. This result contrasts with the weaker waveguiding signature in the case of UV210-based nanotubes embedding PFO (poly(9,9-di-n-octylfluorenyl-2,7-diyl)). It is attributed to the strong reabsorption phenomenon, owing to overlapping between absorption and emission bands in the semi-conducting conjugated polymer PFO. These results make this Mo6@SU8 original class of nanocomposite a promising candidate as nanosources for submicronic photonic integration.

Physicochemical modifications and applications of carbon nano-onions for electrochemical energy storage

NASA Astrophysics Data System (ADS)

Borgohain, Rituraj

Carbon nano-onions (CNOs), concentrically multilayered fullerenes, are prepared by several different methods. We are studying the properties of two specific CNOs: A-CNOs and N-CNOs. A-CNOs are synthesized by underwater arc discharge, and N-CNOs are synthesized by high-temperature graphitization of commercial nanodiamond. In this study the synthesis of A-CNOs are optimized by designing an arc discharge aparatus to control the arc plasma. Moreover other synthesis parameters such as arc power, duty cycles, temperature, graphitic and metal impurities are controlled for optimum production of A-CNOs. Also, a very efficient purification method is developed to screen out A-CNOs from carboneseous and metal impurities. In general, A-CNOs are larger than N-CNOs (ca. 30 nm vs. 7 nm diameter). The high surface area, appropriate mesoporosity, high thermal stability and high electrical conductivity of CNOs make them a promising material for various applications. These hydrophobic materials are functionalized with organic groups on their outer layers to study their surface chemistry and to decorate with metal oxide nanoparticles. Both CNOs and CNO nanocomposites are investigated for application in electrochemical capacitors (ECs). The influences of pH, concentration and additives on the performance of the composites are studied. Electrochemical measurements demonstrate high specific capacitance and high cycling stability with high energy and power density of the composite materials in aqueous electrolyte. Key words: Carbon Nano-onions, Arc discharge, Purification, Functionalization, Supercapacitor.

Formation of self-ordered porous anodized alumina template for growing tungsten trioxide nanowires

NASA Astrophysics Data System (ADS)

Hussain, Tajamal; Shah, Asma Tufail; Shehzad, Khurram; Mujahid, Adnan; Farooqi, Zahoor Hussain; Raza, Muhammad Hamid; Ahmed, Mirza Nadeem; Nisa, Zaib Un

2015-12-01

Uniform porous anodized aluminum oxide (AAO) membrane has been synthesized by two-step anodization for fabricating tungsten trioxide (WO3) nanowires. Under assayed conditions, uniform porous structure of alumina (Al2O3) membrane with long range ordered hexagonal arrangements of nanopores was achieved. The self-assembled template possesses pores of internal diameter of 50 nm and interpore distance ( d int) of 80 nm with a thickness of about 80 µm, i.e., used for fabrication of nanostructures. WO3 nanowires have been fabricated by simple electroless deposition method inside Al2O3 nanopores. SEM images show tungsten trioxide nanowire with internal diameter of about 50 nm, similar to porous diameter of AAO template. XRD results showed that nanowires exist in cubic crystalline state with minor proportion of monoclinic phase.

Pentatwinned Cu Nanowires with Ultrathin Diameters below 20 nm and Their Use as Templates for the Synthesis of Au-Based Nanotubes

DOE PAGES

Luo, Ming; Zhou, Ming; Rosa da Silva, Robson; ...

2017-01-24

Here, we report a one-pot method for the facile synthesis of Cu nanowires in high purity, together with ultrathin diameters well below 20 nm. Selected area electron diffraction and high-resolution transmission electron microscopy studies confirm that the Cu nanowires are grown along the <110> direction to give pentatwinned, one-dimensional nanostructures, enclosed by five {100} facets on the side surface. A systematic study further indicates that it is critical to conduct the synthesis under an argon atmosphere in order to improve the purity and uniformity of the nanowires while keeping their diameters thinner than 20 nm. Finally, we demonstrate the usemore » of these nanowires as sacrificial templates for the synthesis of Au-based nanotubes through a galvanic replacement process.« less

Pentatwinned Cu Nanowires with Ultrathin Diameters below 20 nm and Their Use as Templates for the Synthesis of Au-Based Nanotubes

DOE Office of Scientific and Technical Information (OSTI.GOV)

Luo, Ming; Zhou, Ming; Rosa da Silva, Robson

Here, we report a one-pot method for the facile synthesis of Cu nanowires in high purity, together with ultrathin diameters well below 20 nm. Selected area electron diffraction and high-resolution transmission electron microscopy studies confirm that the Cu nanowires are grown along the <110> direction to give pentatwinned, one-dimensional nanostructures, enclosed by five {100} facets on the side surface. A systematic study further indicates that it is critical to conduct the synthesis under an argon atmosphere in order to improve the purity and uniformity of the nanowires while keeping their diameters thinner than 20 nm. Finally, we demonstrate the usemore » of these nanowires as sacrificial templates for the synthesis of Au-based nanotubes through a galvanic replacement process.« less

High-gradient compact linear accelerator

DOEpatents

Carder, B.M.

1998-05-26

A high-gradient linear accelerator comprises a solid-state stack in a vacuum of five sets of disc-shaped Blumlein modules each having a center hole through which particles are sequentially accelerated. Each Blumlein module is a sandwich of two outer conductive plates that bracket an inner conductive plate positioned between two dielectric plates with different thicknesses and dielectric constants. A third dielectric core in the shape of a hollow cylinder forms a casing down the series of center holes, and it has a dielectric constant different that the two dielectric plates that sandwich the inner conductive plate. In operation, all the inner conductive plates are charged to the same DC potential relative to the outer conductive plates. Next, all the inner conductive plates are simultaneously shorted to the outer conductive plates at the outer diameters. The signal short will propagate to the inner diameters at two different rates in each Blumlein module. A faster wave propagates quicker to the third dielectric core across the dielectric plates with the closer spacing and lower dielectric constant. When the faster wave reaches the inner extents of the outer and inner conductive plates, it reflects back outward and reverses the field in that segment of the dielectric core. All the field segments in the dielectric core are then in unipolar agreement until the slower wave finally propagates to the third dielectric core across the dielectric plates with the wider spacing and higher dielectric constant. During such unipolar agreement, particles in the core are accelerated with gradients that exceed twenty megavolts per meter. 10 figs.

High-gradient compact linear accelerator

DOEpatents

Carder, Bruce M.

1998-01-01

A high-gradient linear accelerator comprises a solid-state stack in a vacuum of five sets of disc-shaped Blumlein modules each having a center hole through which particles are sequentially accelerated. Each Blumlein module is a sandwich of two outer conductive plates that bracket an inner conductive plate positioned between two dielectric plates with different thicknesses and dielectric constants. A third dielectric core in the shape of a hollow cylinder forms a casing down the series of center holes, and it has a dielectric constant different that the two dielectric plates that sandwich the inner conductive plate. In operation, all the inner conductive plates are charged to the same DC potential relative to the outer conductive plates. Next, all the inner conductive plates are simultaneously shorted to the outer conductive plates at the outer diameters. The signal short will propagate to the inner diameters at two different rates in each Blumlein module. A faster wave propagates quicker to the third dielectric core across the dielectric plates with the closer spacing and lower dielectric constant. When the faster wave reaches the inner extents of the outer and inner conductive plates, it reflects back outward and reverses the field in that segment of the dielectric core. All the field segments in the dielectric core are then in unipolar agreement until the slower wave finally propagates to the third dielectric core across the dielectric plates with the wider spacing and higher dielectric constant. During such unipolar agreement, particles in the core are accelerated with gradients that exceed twenty megavolts per meter.

Atomic force microscopy investigation of the giant mimivirus

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kuznetsov, Yuri G.; Xiao Chuan; Sun Siyang

2010-08-15

Mimivirus was investigated by atomic force microscopy in its native state following serial degradation by lysozyme and bromelain. The 750-nm diameter virus is coated with a forest of glycosylated protein fibers of lengths about 140 nm with diameters 1.4 nm. Fibers are capped with distinctive ellipsoidal protein heads of estimated Mr = 25 kDa. The surface fibers are attached to the particle through a layer of protein covering the capsid, which is in turn composed of the major capsid protein (MCP). The latter is organized as an open network of hexagonal rings with central depressions separated by 14 nm. Themore » virion exhibits an elaborate apparatus at a unique vertex, visible as a star shaped depression on native particles, but on defibered virions as five arms of 50 nm width and 250 nm length rising above the capsid by 20 nm. The apparatus is integrated into the capsid and not applied atop the icosahedral lattice. Prior to DNA release, the arms of the star disengage from the virion and it opens by folding back five adjacent triangular faces. A membrane sac containing the DNA emerges from the capsid in preparation for fusion with a membrane of the host cell. Also observed from disrupted virions were masses of distinctive fibers of diameter about 1 nm, and having a 7-nm periodicity. These are probably contained within the capsid along with the DNA bearing sac. The fibers were occasionally observed associated with toroidal protein clusters interpreted as processive enzymes modifying the fibers.« less

The transverse diameter of the chest on routine radiographs reliably estimates gestational age and weight in premature infants.

PubMed

Dietz, Kelly R; Zhang, Lei; Seidel, Frank G

2015-08-01

Prior to digital radiography it was possible for a radiologist to easily estimate the size of a patient on an analog film. Because variable magnification may be applied at the time of processing an image, it is now more difficult to visually estimate an infant's size on the monitor. Since gestational age and weight significantly impact the differential diagnosis of neonatal diseases and determine the expected size of kidneys or appearance of the brain by MRI or US, this information is useful to a pediatric radiologist. Although this information may be present in the electronic medical record, it is frequently not readily available to the pediatric radiologist at the time of image interpretation. To determine if there was a correlation between gestational age and weight of a premature infant with their transverse chest diameter (rib to rib) on admission chest radiographs. This retrospective study was approved by the institutional review board, which waived informed consent. The maximum transverse chest diameter outer rib to outer rib was measured on admission portable chest radiographs of 464 patients admitted to the neonatal intensive care unit (NICU) during the 2010 calendar year. Regression analysis was used to investigate the association between chest diameter and gestational age/birth weight. Quadratic term of chest diameter was used in the regression model. Chest diameter was statistically significantly associated with both gestational age (P < 0.0001) and birth weight (P < 0.0001). An infant's gestational age and birth weight can be reliably estimated by comparing a simple measurement of the transverse chest diameter on digital chest radiograph with the tables and graphs in our study.

Endobronchial Photoacoustic Microscopy for Staging of Lung Cancer

DTIC Science & Technology

2016-08-01

acoustic lens: (1) Three hairs were buried at different depths within the background phantom with 4mm distance between each hair . The advantage of this...and carried out tests to demonstrate this advantage using human hair as micro-scale targets (Figure 4). The targets were buried in a background with...the signal from the hair targets. The 30MHz transducer has outer diameter 11mm, and was equipped with corresponding lens whose apertures fit its outer

Directional microwave applicator and methods

NASA Technical Reports Server (NTRS)

Fink, Patrick W. (Inventor); Lin, Greg Y. (Inventor); Chu, Andrew W. (Inventor); Dobbins, Justin A. (Inventor); Arndt, G. Dickey (Inventor); Ngo, Phong H. (Inventor)

2008-01-01

A miniature microwave antenna is disclosed which may be utilized for biomedical applications such as, for example, radiation induced hyperthermia through catheter systems. One feature of the antenna is that it possesses azimuthal directionality despite its small size. This directionality permits targeting of certain tissues while limiting thermal exposure of adjacent tissue. One embodiment has an outer diameter of about 0.095'' (2.4 mm) but the design permits for smaller diameters.

Method for forming a thermocouple

DOEpatents

Metz, Hugh J.

1979-01-01

A method is provided for producing a fast response, insulated junction thermocouple having a uniform diameter outer sheath in the region of the measuring junction. One step is added to the usual thermocouple fabrication process that consists in expanding the thermocouple sheath following the insulation removal step. This makes it possible to swage the sheath back to the original diameter and compact the insulation to the desired high density in the final fabrication step.

Recent Combined Effects Explosives Technology

DTIC Science & Technology

2010-07-01

flow velocities are relative to the detonation velocity, D. Using the Jones-Wilkens-Lee-Baker [ JWLB (ref. 7)] thermo- dynamic equation of state...cylinder test modeling using identical JWLB equations of state for TNT and LX-14. The JWLB equations of state were parameterized using JAGUAR...thermochemical equation of state modeling (ref. 11). Table 1 presents the TNT and LX-14 JWLB parameters. The 1.2 in. outer diameter, 1 in. inner diameter

A video-angiometer for simultaneous and continuous measurement of inner and outer vessel diameters. Technical report.

PubMed

Assmann, R; Henrich, H

1978-09-29

A system is described for continuously measuring vessel diameters. It bases on the evaluation of video signal differences of a video camera which are induced by light intensity differences (grey levels) caused by the vascular wall structures. The system is electronically linear, automatically measuring and in addition eyeball controlled by the human sensor: the inaccuracy does not exceed the 5% level.

Accommodating Thickness in Origami-Based Deployable Arrays

NASA Technical Reports Server (NTRS)

Zirbel, Shannon A.; Magleby, Spencer P.; Howell, Larry L.; Lang, Robert J.; Thomson, Mark W.; Sigel, Deborah A.; Walkemeyer, Phillip E.; Trease, Brian P.

2013-01-01

The purpose of this work is to create deployment systems with a large ratio of stowed-to-deployed diameter. Deployment from a compact form to a final flat state can be achieved through origami-inspired folding of panels. There are many models capable of this motion when folded in a material with negligible thickness; however, when the application requires the folding of thick, rigid panels, attention must be paid to the effect of material thickness not only on the final folded state, but also during the folding motion (i.e., the panels must not be required to flex to attain the final folded form). The objective is to develop new methods for deployment from a compact folded form to a large circular array (or other final form). This paper describes a mathematical model for modifying the pattern to accommodate material thickness in the context of the design, modeling, and testing of a deployable system inspired by an origami six-sided flasher model. The model is demonstrated in hardware as a 1/20th scale prototype of a deployable solar array for space applications. The resulting prototype has a ratio of stowed-to-deployed diameter of 9.2 (or 1.25 m deployed outer diameter to 0.136 m stowed outer diameter).

[Gradient-index (GRIN) endoscopic examinations from the inner structures of the optic nerve meninges].

PubMed

Sens, Frank Michael; Killer, Hanspeter Esriel; Meyer, Peter

2003-03-01

Due to the excellent image quality and the small outer diameter of the GRIN-(gradient index) endoscope tips we were able to examine the subdural and the subarachnoidal space of the optic nerve meninges by endoscopy. This examination was performed to obtain more information about the inner structure of the optic nerve meninges. In this post-mortem study 7 optic nerves were examined from the chiasm to the globe by GRIN endoscopy (Volpi, Schlieren, Switzerland), with an outer diameter of 0.89 mm, integrated optic of 0.5 mm diameter and an integrated fluid channel of 0.2 mm diameter. In all cases the endoscopic examination of the optic nerve meninges was technically easy to perform. It was possible to study the inner surface of the nerve sheaths and the nerve sheath spaces in close-up. We found horizontal and vertical cords on the inner surface of the dura mater, which could tighten by movements of the optic nerve. With a gradient-index (GRIN) endoscope we obtained new information about the inner structure of the optic nerve meninges. New theories about the changes of the optic nerve meninges during movements of the optic nerve may evolve from this study. Further studies with this new method should be encouraged.

Composite drill pipe and method for forming same

DOEpatents

Leslie, James C; Leslie, II, James C; Heard, James; Truong, Liem; Josephson, Marvin

2014-04-15

Metal inner and outer fittings configured, the inner fitting configured proximally with an external flange and projecting distally to form a cylindrical barrel and stepped down-in-diameter to form an abutment shoulder and then projecting further distally to form a radially inwardly angled and distally extending tapered inner sleeve. An outer sleeve defining a torque tube is configured with a cylindrical collar to fit over the barrel and is formed to be stepped up in diameter in alignment with the first abutment shoulder to then project distally forming a radially outwardly tapered and distally extending bonding surface to cooperate with the inner sleeve to cooperate with the inner sleeve in forming a annular diverging bonding cavity to receive the extremity of a composite pipe to abut against the abutment shoulders and to be bonded to the respective bonding surfaces by a bond.

Surface expression of the Chicxulub crater

PubMed

Pope, K O; Ocampo, A C; Kinsland, G L; Smith, R

1996-06-01

Analyses of geomorphic, soil, and topographic data from the northern Yucatan Peninsula, Mexico, confirm that the buried Chicxulub impact crater has a distinct surface expression and that carbonate sedimentation throughout the Cenozoic has been influenced by the crater. Late Tertiary sedimentation was mostly restricted to the region within the buried crater, and a semicircular moat existed until at least Pliocene time. The topographic expression of the crater is a series of features concentric with the crater. The most prominent is an approximately 83-km-radius trough or moat containing sinkholes (the Cenote ring). Early Tertiary surfaces rise abruptly outside the moat and form a stepped topography with an outer trough and ridge crest at radii of approximately 103 and approximately 129 km, respectively. Two discontinuous troughs lie within the moat at radii of approximately 41 and approximately 62 km. The low ridge between the inner troughs corresponds to the buried peak ring. The moat corresponds to the outer edge of the crater floor demarcated by a major ring fault. The outer trough and the approximately 62-km-radius inner trough also mark buried ring faults. The ridge crest corresponds to the topographic rim of the crater as modified by postimpact processes. These interpretations support previous findings that the principal impact basin has a diameter of approximately 180 km, but concentric, low-relief slumping extends well beyond this diameter and the eroded crater rim may extend to a diameter of approximately 260 km.

The Relationship Between Surface Curvature and Abdominal Aortic Aneurysm Wall Stress.

PubMed

de Galarreta, Sergio Ruiz; Cazón, Aitor; Antón, Raúl; Finol, Ender A

2017-08-01

The maximum diameter (MD) criterion is the most important factor when predicting risk of rupture of abdominal aortic aneurysms (AAAs). An elevated wall stress has also been linked to a high risk of aneurysm rupture, yet is an uncommon clinical practice to compute AAA wall stress. The purpose of this study is to assess whether other characteristics of the AAA geometry are statistically correlated with wall stress. Using in-house segmentation and meshing algorithms, 30 patient-specific AAA models were generated for finite element analysis (FEA). These models were subsequently used to estimate wall stress and maximum diameter and to evaluate the spatial distributions of wall thickness, cross-sectional diameter, mean curvature, and Gaussian curvature. Data analysis consisted of statistical correlations of the aforementioned geometry metrics with wall stress for the 30 AAA inner and outer wall surfaces. In addition, a linear regression analysis was performed with all the AAA wall surfaces to quantify the relationship of the geometric indices with wall stress. These analyses indicated that while all the geometry metrics have statistically significant correlations with wall stress, the local mean curvature (LMC) exhibits the highest average Pearson's correlation coefficient for both inner and outer wall surfaces. The linear regression analysis revealed coefficients of determination for the outer and inner wall surfaces of 0.712 and 0.516, respectively, with LMC having the largest effect on the linear regression equation with wall stress. This work underscores the importance of evaluating AAA mean wall curvature as a potential surrogate for wall stress.

Investigation of H2S separation from H2S/CH4 mixtures using functionalized and non-functionalized vertically aligned carbon nanotube membranes

NASA Astrophysics Data System (ADS)

Gilani, Neda; Towfighi, Jafar; Rashidi, Alimorad; Mohammadi, Toraj; Omidkhah, Mohammad Reza; Sadeghian, Ahmad

2013-04-01

Separation of H2S from binary mixtures of H2S/CH4 using vertically aligned carbon nanotube membranes fabricated in anodic aluminum oxide (AAO) template was studied experimentally. Carbon nanotubes (CNTs) were grown in five AAO templates with different pore diameters using chemical vapor deposition, and CNT/AAO membranes with tubular carbon nanotube structure and open caps were selected for separation of H2S. For this, two tubular CNT/AAO membranes were fabricated with the CNT inner diameters of 23 and 8 nm. It was found that permeability and selectivity of the membrane with inner diameter of 23 nm for CNT were independent of upstream feed pressure and H2S feed concentration unlike that of CNT having an inner diameter of 8 nm. Selectivity of these membranes for separation of H2S was obtained in the ranges of 1.36-1.58 and 2.11-2.86, for CNTs with internal diameters of 23 and 8 nm, respectively. In order to enhance the separation of H2S from H2S/CH4 mixtures, dodecylamine was used to functionalize the CNT/AAO membrane with higher selectivity. The results showed that for amido-functionalized membrane, both upstream feed pressure and H2S partial pressure in the feed significantly increased H2S permeability, and selectivity for H2S being in the range of 3.0-5.57 respectively.

High-Resolution, Large-Area, Nano Imprint Lithography

DTIC Science & Technology

2009-08-27

oxides as the seed layers can provide implication as the general synthetic route for the spontaneous growth of metal - silicide nanowires in large...nano-island array preparation , we have successfully fabricated patterned magnetic recording media as described in Fig. 2. About ~30 nm diameter Si...that we fabricated at UCSD with 5-50 nm diameter magnetic islands was used, since a large- area, hard disk size preparation was necessary, and since a

Fatigue resistance, electrochemical corrosion and biological response of Ti-15Mo with surface modified by amorphous TiO2 nanotubes layer.

PubMed

Campanelli, Leonardo C; Oliveira, Nilson T C; da Silva, Paulo Sergio C P; Bolfarini, Claudemiro; Palmieri, Annalisa; Cura, Francesca; Carinci, Francesco; Motheo, Artur J

2018-03-04

The objective of this work was a systemic evaluation of the anodizing treatment in a β-type Ti-15Mo alloy to grow a TiO 2 nanostructured layer for osseointegration improvement. The technical viability of the surface modification was assessed based on the resistance to mechanical fatigue, electrochemical corrosion, and biological response. By using an organic solution of NH 4 F in ethylene glycol, a well-organized array of 90 nm diameter nanotubes was obtained with a potential of 40 V for 6 h, while undefined nanotubes of 25 nm diameter were formed with a potential of 20 V for 1 h. Nevertheless, the production of the 90 nm diameter nanotubes was followed by micrometer pits that significantly reduced the fatigue performance. The undefined nanotubes of 25 nm diameter, besides the greater cell viability and improved osteoblastic cell differentiation in comparison to the as-polished surface, were not deleterious to the fatigue and corrosion properties. This result strengthens the necessity of an overall evaluation of the anodizing treatment, particularly the fatigue resistance, before suggesting it for the design of implants. © 2018 Wiley Periodicals, Inc. J Biomed Mater Res Part B: Appl Biomater, 2018. © 2018 Wiley Periodicals, Inc.

Common path endoscopic probes for optical coherence tomography (Conference Presentation)

NASA Astrophysics Data System (ADS)

Singh, Kanwarpal; Gardecki, Joseph A.; Tearney, Guillermo J.

2017-02-01

Background: Dispersion imbalance and polarization mismatch between the reference and sample arm signals can lead to image quality degradation in optical coherence tomography (OCT). One approach to reduce these image artifacts is to employ a common-path geometry in fiber-based probes. In this work, we report an 800 um diameter all-fiber common-path monolithic probe for coronary artery imaging where the reference signal is generated using an inline fiber partial reflector. Methods: Our common-path probe was designed for swept-source based Fourier domain OCT at 1310 nm wavelength. A face of a coreless fiber was coated with gold and spliced to a standard SMF-28 single mode fiber creating an inline partial reflector, which acted as a reference surface. The other face of the coreless fiber was shaped into a ball lens for focusing. The optical elements were assembled within a 560 µm diameter drive shaft, which was attached to a rotary junction. The drive shaft was placed inside a transparent sheath having an outer diameter of 800 µm. Results: With a source input power of 30mW, the inline common-path probe achieved a sensitivity of 104 dB. Images of human finger skin showed the characteristic layers of skin as well as features such as sweat ducts. Images of coronary arteries ex vivo obtained with this probe enabled visualization of the characteristic architectural morphology of the normal artery wall and known features of atherosclerotic plaque. Conclusion: In this work, we have demonstrated a common path OCT probe for cardiovascular imaging. The probe is easy to fabricate, will reduce system complexity and overall cost. We believe that this design will be helpful in endoscopic applications that require high resolution and a compact form factor.

Intravital Förster resonance energy transfer imaging reveals elevated [Ca2+]i and enhanced sympathetic tone in femoral arteries of angiotensin II-infused hypertensive biosensor mice

PubMed Central

Wang, Youhua; Chen, Ling; Wier, W Gil; Zhang, Jin

2013-01-01

Artery narrowing in hypertension can only result from structural remodelling of the artery, or increased smooth muscle contraction. The latter may occur with, or without, increases in [Ca2+]i. Here, we sought to measure, in living hypertensive mice, possible changes in artery dimensions and/or [Ca2+]i, and to determine some of the mechanisms involved. Ca2+/calmodulin biosensor (Förster resonance energy transfer-based) mice were made hypertensive by s.c. infusion of angiotensin II (Ang II, 400 ng kg−1 min−1, 2–3 weeks). Intravital fluorescence microscopy was used to determine [Ca2+]i and outer diameter of surgically exposed, intact femoral artery (FA) of anaesthetized mice. Active contractile FA ‘tone’ was calculated from the basal-state diameter and the passive (i.e. Ca2+-free) diameter (PD). Compared to saline control, FAs of Ang II-infused mice had (1) ∼21% higher active tone and (2) ∼78 nm higher smooth muscle [Ca2+]i, but (3) the same PDs. The local Ang II receptor (AT1R) blocker losartan had negligible effect on tone or [Ca2+]i in control FAs, but reduced the basal tone by ∼9% in Ang II FAs. Both i.v. hexamethonium and locally applied prazosin abolished the difference in FA tone and [Ca2+]i, suggesting a dominant role of sympathetic nerve activity (SNA). Changes in diameter and [Ca2+]i in response to locally applied phenylephrine, Ang II, arginine vasopressin, elevated [K+]o and acetylcholine were not altered. In summary, FAs of living Ang II hypertensive mice have higher [Ca2+]i, and are more constricted, due, primarily, to elevated SNA and some increased arterial AT1R activation. Evidence of altered artery reactivity or remodeling was not found. PMID:23981717

Intravital Förster resonance energy transfer imaging reveals elevated [Ca2+]i and enhanced sympathetic tone in femoral arteries of angiotensin II-infused hypertensive biosensor mice.

PubMed

Wang, Youhua; Chen, Ling; Wier, W Gil; Zhang, Jin

2013-11-01

Artery narrowing in hypertension can only result from structural remodelling of the artery, or increased smooth muscle contraction. The latter may occur with, or without, increases in [Ca(2+)]i. Here, we sought to measure, in living hypertensive mice, possible changes in artery dimensions and/or [Ca(2+)]i, and to determine some of the mechanisms involved. Ca(2+)/calmodulin biosensor (Förster resonance energy transfer-based) mice were made hypertensive by s.c. infusion of angiotensin II (Ang II, 400 ng kg(-1) min(-1), 2-3 weeks). Intravital fluorescence microscopy was used to determine [Ca(2+)]i and outer diameter of surgically exposed, intact femoral artery (FA) of anaesthetized mice. Active contractile FA 'tone' was calculated from the basal-state diameter and the passive (i.e. Ca(2+)-free) diameter (PD). Compared to saline control, FAs of Ang II-infused mice had (1) ∼21% higher active tone and (2) ∼78 nm higher smooth muscle [Ca(2+)]i, but (3) the same PDs. The local Ang II receptor (AT1R) blocker losartan had negligible effect on tone or [Ca(2+)]i in control FAs, but reduced the basal tone by ∼9% in Ang II FAs. Both i.v. hexamethonium and locally applied prazosin abolished the difference in FA tone and [Ca(2+)]i, suggesting a dominant role of sympathetic nerve activity (SNA). Changes in diameter and [Ca(2+)]i in response to locally applied phenylephrine, Ang II, arginine vasopressin, elevated [K(+)]o and acetylcholine were not altered. In summary, FAs of living Ang II hypertensive mice have higher [Ca(2+)]i, and are more constricted, due, primarily, to elevated SNA and some increased arterial AT1R activation. Evidence of altered artery reactivity or remodeling was not found.

Characterization and corrosion behavior of F6NM stainless steel treated in high temperature water

NASA Astrophysics Data System (ADS)

Li, Zheng-yang; Cai, Zhen-bing; Yang, Wen-jin; Shen, Xiao-yao; Xue, Guo-hong; Zhu, Min-hao

2018-03-01

F6NM martensitic stainless steel was exposed to 350 °C water condition for 500, 1500, and 2500 h to simulate pressurized water reactor (PWR) condition. The characterization and corrosion behavior of the oxide film were investigated. Results indicate that the exposed steel surface formed a double-layer oxide film. The outer oxide film is Fe-rich and contains two type oxide particles. However, the inner oxide film is Cr-rich, and two oxide films, whose thicknesses increase with increasing exposure time. The oxide film reduces the corrosion behavior because the outer oxide film has many crack and pores. Finally, the mechanism and factors affecting the formation of the oxide film were investigated.

Effect of Shock Precompression on the Critical Diameter of Liquid Explosives

NASA Astrophysics Data System (ADS)

Petel, Oren E.; Higgins, Andrew J.; Yoshinaka, Akio C.; Zhang, Fan

2006-07-01

The critical diameter of both ambient and shock-precompressed liquid nitromethane confined in PVC tubing are measured experimentally. The experiment was conducted for both amine sensitized and neat NM. In the precompression experiments, the explosive is compressed by a strong shock wave generated by a donor explosive and reflected from a high impedance anvil prior to being detonated by a secondary event. The pressures reached in the test sections prior to detonation propagation was approximately 7 and 8 GPa for amine sensitized and neat NM respectively. The results demonstrated a 30% - 65% decrease in the critical diameter for the shock-compressed explosives. This critical diameter decrease is observed despite a significant decrease in the predicted Von Neumann temperature of the detonation in the precompressed explosive. The results are discussed in the context of theoretical predictions based on thermal ignition theory and previous critical diameter measurements.

Formation of hexagonal boron nitride nanoscrolls induced by inclusion and exclusion of self-assembling molecules in solution process.

PubMed

Hwang, Da Young; Suh, Dong Hack

2014-06-07

Unlike nanoscrolls of 2D graphene, those of 2D h-BN have not been demonstrated, except for only a few experimental reports. Nanoscrolls of h-BN with high yields and reproducibility are first synthesized by a simple solution process. Inner-tube diameters of BNSs including LCAs, N-(2-aminoethyl)-3α-hydroxy-5β-cholan-24-amide, a bile acid derivative and self-assembling material, can be controlled by adjusting the diameter of the LCA fiber which is grown by self-assembly. TEM and SEM images show that BNSs have a tube-like morphology and the inner-tube diameter of BNSs can be controlled in the range from 20 to 60 nm for a smaller diameter, up to 300 nm for a larger diameter by LCA fiber growth inside the BNSs. Finally, open cylindrical BNSs with hollow cores were obtained by dissolving LCAs inside BNSs.

Directed Growth of Carbon Nanotubes Across Gaps

NASA Technical Reports Server (NTRS)

Delzeit, Lance; Meyyapan, Meyya

2008-01-01

An experiment has shown that when single-walled carbon nanotubes (SWNTs) are grown by chemical vapor deposition in the presence of an electric field of suitable strength, the nanotubes become aligned along the electric field. In an important class of contemplated applications, one would exploit this finding in fabricating nanotube transistors; one would grow SWNTs across gaps between electrodes that would serve, subsequently, as source and drain contacts during operation of the transistors. In preparation for the experiment, a multilayer catalyst comprising a 20-nmthick underlayer of iridium (platinum group), a 1-nm-thick middle layer of iron, and a 0.2-nm-thick outer layer of molybdenum was ion-beam sputtered onto a quartz substrate. A 25 micrometers-diameter iron wire was used as a shadow mask during the sputtering to create a 25 micrometers gap in the catalyst. Then electrical leads were connected to the catalyst areas separated by the gap so that these catalyst areas would also serve as electrodes. The substrate as thus prepared was placed in a growth chamber that consisted of a quartz tube of 1-in. (2.54-cm) diameter enclosed in a furnace. SWNTs of acceptably high quantity and quality were grown in 10 minutes with methane at atmospheric pressure flowing through the chamber at a rate of 1,000 standard cubic centimeters per minute at a temperature of 900 C. To prevent oxidation of the SWNTs, the chamber was purged with 99.999-percent pure argon before and after growth, and the chamber was cooled to less than 300 C before opening it to the atmosphere after growth. When no voltage was applied across the gap, the SWNTs grew in random directions extending out from the edges of the catalyst at the gap. When a potential of 10 V was applied between the catalyst/electrode areas to create an electric field across the gap, the SWNTs grew across the gap, as shown in the figure.

Electrospun Poly(lactic acid-co-glycolic acid) Scaffolds for Skin Tissue Engineering

PubMed Central

Kumbar, Sangamesh G.; Nukavarapu, Syam Prasad; James, Roshan; Nair, Lakshmi S.; Laurencin, Cato T.

2008-01-01

Electrospun fiber matrices composed of scaffolds of varying fiber diameters were investigated for potential application of severe skin loss. Few systematic studies have been performed to examine the effect of varying fiber diameter electrospun fiber matrices for skin regeneration. The present study reports the fabrication of poly[lactic acid-co-glycolic acid] (PLAGA) matrices with fiber diameters of 150–225, 200–300, 250–467, 500–900, 600–1200, 2500–3000 and 3250–6000 nm via electrospinning. All fiber matrices found to have a tensile modulus from 39.23 ± 8.15 to 79.21 ± 13.71 MPa which falls in the range for normal human skin. Further, the porous fiber matrices have porosity between 38–60 % and average pore diameters between 10–14µm. We evaluated the efficacy of these biodegradable fiber matrices as skin substitutes by seeding them with human skin fibroblasts (hSF). Human skin fibroblasts acquired a well spread morphology and showed significant progressive growth on fiber matrices in the 350–1100 nm diameter range. Collagen type III gene expression was significantly up-regulated in hSF seeded on matrices with fiber diameters in the range of 350–1100 nm. Based on the need, the proposed fiber skin substitutes can be successfully fabricated and optimized for skin fibroblast attachment and growth. PMID:18639927

Study on effect of the surface variation of colloidal silica abrasive during chemical mechanical polishing of sapphire

NASA Astrophysics Data System (ADS)

Bun-Athuek, Natthaphon; Yoshimoto, Yutaka; Sakai, Koya; Khajornrungruang, Panart; Suzuki, Keisuke

2017-07-01

The surface and diameter size variations of colloidal silica particles during the chemical mechanical polishing (CMP) of sapphire substrates were investigated using different particle diameters of 20 and 55 nm. Dynamic light scattering (DLS) results show that the silica particles became larger after CMP under both conditions. The increase in particle size in the slurry was proportional to the material removal amount (MRA) as a function of the removed volume of sapphire substrates by CMP and affected the material removal rate (MRR). Transmission electron microscopy (TEM) images revealed an increase in the size of the fine particles and a change in their surface shape in the slurry. The colloidal silica was coated with the material removed from the substrate during CMP. In this case, the increase in the size of 55 nm diameter particles is larger than that of 20 nm diameter particles. X-ray fluorescence spectrometry (XRF) results indicate that the aluminum element from polished sapphire substrates adhered to the surfaces of silica particles. Therefore, MRR decreases with increasing of polishing time owing to the degradation of particles in the slurry.

Synthesis of subnanometer-diameter vertically aligned single-walled carbon nanotubes with copper-anchored cobalt catalysts.

PubMed

Cui, Kehang; Kumamoto, Akihito; Xiang, Rong; An, Hua; Wang, Benjamin; Inoue, Taiki; Chiashi, Shohei; Ikuhara, Yuichi; Maruyama, Shigeo

2016-01-21

We synthesize vertically aligned single-walled carbon nanotubes (VA-SWNTs) with subnanometer diameters on quartz (and SiO2/Si) substrates by alcohol CVD using Cu-anchored Co catalysts. The uniform VA-SWNTs with a nanotube diameter of 1 nm are synthesized at a CVD temperature of 800 °C and have a thickness of several tens of μm. The diameter of SWNTs was reduced to 0.75 nm at 650 °C with the G/D ratio maintained above 24. Scanning transmission electron microscopy energy-dispersive X-ray spectroscopy (EDS-STEM) and high angle annular dark field (HAADF-STEM) imaging of the Co/Cu bimetallic catalyst system showed that Co catalysts were captured and anchored by adjacent Cu nanoparticles, and thus were prevented from coalescing into a larger size, which contributed to the small diameter of SWNTs. The correlation between the catalyst size and the SWNT diameter was experimentally clarified. The subnanometer-diameter and high-quality SWNTs are expected to pave the way to replace silicon for next-generation optoelectronic and photovoltaic devices.

Characteristics of nanolite crystallization in volcanic pyroclasts

NASA Astrophysics Data System (ADS)

Mujin, M.; Nakamura, M.; Miyake, A.

2017-12-01

Crystal nucleation and initial growth in silicate melt may control the number density and later stage growth of crystals, such as twinning and morphology, and are therefore fundamental but still poorly understood processes in magma crystallization. Petrographic and experimental studies on groundmass microlites shed light on their importance for understanding eruption dynamics, but most studies did not focus on nanometer scale crystals. Recently, we reported "nanolites (30 nm-1 µm in width)" and "ultrananolites (< 30 nm in diameter)", which are nanoscale crystals with extremely high number density, in the interstices of microlites in pyroclasts. In this presentation, we summarize their mineralogical and petrological characteristics in pyroclasts of the 2011 eruption of Shinmoedake (Kirishima volcano group)1. By covering a wide size-range of crystals (down to 1 nm in diameter) based on scanning electron microscopy with tungsten filament (W-SEM), field emission (FE)-SEM, and transmission electron microscopy (TEM), we found a clear size gap (hiatus) in the size distribution and presence of minimum crystal size. In a dense juvenile fragment, crystals were absent or their number densities were too low to measure the sizes of pyroxene with a diameter of < 20 nm and a width of 30-100 nm, plagioclase with a width of < 100 nm, and Fe-Ti oxide with a diameter of 2-10 nm and a width of 20-100 nm. In pumice clasts, crystals smaller than 100 nm were not found. These observations show that nucleation of nanoscale crystals almost paused (froze) in the late stage of crystallization, possibly due to a decrease in undercooling, increase in interfacial free energy, and decrease in diffusivity in a dehydrated melt, whereas crystal growth was mostly continuous. Ultrananolites were found in pyroxene and Fe-Ti oxide; notably, these were spherical, whereas nanolites and microlites were rectangular. The observed ultrananolite-sized particles might partly include "subcritical clusters", which are particles smaller than the critical nucleation size assumed in the transient nucleation models. References 1) Mujin and Nakamura, 2014, Geology, v.42, p.611-614, and Mujin et al, in revision, Am. Min.

Saturn's outer magnetosphere

NASA Technical Reports Server (NTRS)

Schardt, A. W.; Behannon, K. W.; Carbary, J. F.; Eviatar, A.; Lepping, R. P.; Siscoe, G. L.

1983-01-01

Similarities between the Saturnian and terrestrial outer magnetosphere are examined. Saturn, like Earth, has a fully developed magnetic tail, 80 to 100 RS in diameter. One major difference between the two outer magnetospheres is the hydrogen and nitrogen torus produced by Titan. This plasma is, in general, convected in the corotation direction at nearly the rigid corotation speed. Energies of magnetospheric particles extend to above 500 keV. In contrast, interplanetary protons and ions above 2 MeV have free access to the outer magnetosphere to distances well below the Stormer cutoff. This access presumably occurs through the magnetotail. In addition to the H+, H2+, and H3+ ions primarily of local origin, energetic He, C, N, and O ions are found with solar composition. Their flux can be substantially enhanced over that of interplanetary ions at energies of 0.2 to 0.4 MeV/nuc.

Superficial Macromolecular Arrays on the Cell Wall of Spirillum putridiconchylium

PubMed Central

Beveridge, T. J.; Murray, R. G. E.

1974-01-01

Electron microscopy of the cell envelope of Spirillum putridiconchylium, using negatively stained, thin-sectioned, and replicated freeze-etched preparations, showed two superficial wall layers forming a complex macromolecular pattern on the external surface. The outer structured layer was a linear array of particles overlying an inner tetragonal array of larger subunits. They were associated in a very regular fashion, and the complex was bonded to the outer, pitted surface of the lipopolysaccharide tripartite layer of the cell wall. The relationship of the components of the two structured layers was resolved with the aid of optical diffraction, combined with image filtering and reconstruction and linear and rotary integration techniques. The outer structural layer consisted of spherical 1.5-nm units set in double lines determined by the size and arrangement of 6- by 3-nm inner structural layer subunits, which bore one outer structural layer unit on each outer corner. The total effect of this arrangement was a double-ridged linear structure that was evident in surface replicas and negatively stained fragments of the whole wall. The packing of these units was not square but skewed by 2° off the perpendicular so that the “unit array” described by optical diffraction and linear integration appeared to be a deformed tetragon. The verity of the model was checked by using a photographically reduced image to produce an optical diffraction pattern for comparison with that of the actual layers. The correspondence was nearly perfect. Images PMID:4137219

S-Layer Architectures: Extending the Morphogenetic Potential of S-Layer Protein Self Assembly

DTIC Science & Technology

2012-07-11

virus  capsids  (typically  30  to  100nm  in   diameter)  or  hollow  (apo) ferritin  (12  nm  in  diameter)  S...R., Sleytr, U.B., Pum, D. J. Biol. Chem. 2011, 286, 27416-27424 30. Sára,  M.   Trends  Microbiol.  2001,  9,  47-­‐49.   31. Sára

Development of magnetic bearing system for a new third-generation blood pump.

PubMed

Lee, Jung Joo; Ahn, Chi Bum; Choi, Jaesoon; Park, Jun Woo; Song, Seung-Joon; Sun, Kyung

2011-11-01

A magnetic bearing system is a crucial component in a third-generation blood pump, particularly when we consider aspects such as system durability and blood compatibility. Many factors such as efficiency, occupying volume, hemodynamic stability in the flow path, mechanical stability, and stiffness need to be considered for the use of a magnetic bearing system in a third-generation blood pump, and a number of studies have been conducted to develop novel magnetic bearing design for better handling of these factors. In this study, we developed and evaluated a new magnetic bearing system having a motor for a new third-generation blood pump. This magnetic bearing system consists of a magnetic levitation compartment and a brushless direct current (BLDC) motor compartment. The active-control degree of freedom is one; this control is used for controlling the levitation in the axial direction. The levitation in the radial direction has a passive magnetic levitation structure. In order to improve the system efficiency, we separated the magnetic circuit for axial levitation by using a magnetic circuit for motor drive. Each magnetic circuit in the bearing system was designed to have a minimum gap by placing mechanical parts, such as the impeller blades, outside the circuit. A custom-designed noncontact gap sensor was used for minimizing the system volume. We fabricated an experimental prototype of the proposed magnetic bearing system and evaluated its performance by a control system using the Matlab xPC Target system. The noncontact gap sensor was an eddy current gap sensor with an outer diameter of 2.38 mm, thickness of 0.88 mm, and resolution of 5 µm. The BLDC motor compartment was designed to have an outer diameter of 20 mm, length of 28.75 mm, and power of 4.5 W. It exhibited a torque of 8.6 mNm at 5000 rpm. The entire bearing system, including the motor and the sensor, had an outer diameter of 22 mm and a length of 97 mm. The prototype exhibited sufficient levitation performance in the stop state and the rotation state with a gap of 0.2 mm between the rotor and the stator. The system had a steady position error of 0.01 µm in the stop state and a position error of 0.02 µm at a rotational speed of 5000 rpm; the current consumption rates were 0.15 A and 0.17 A in the stop state and the rotation state, respectively. In summary, we developed and evaluated a unique magnetic bearing system with an integrated motor. We believe that our design will be an important basis for the further development of the design of an entire third-generation blood pump system. © 2011, Copyright the Authors. Artificial Organs © 2011, International Center for Artificial Organs and Transplantation and Wiley Periodicals, Inc.

Novel Iron-oxide Catalyzed CNT Formation on Semiconductor Silicon Nanowire

PubMed Central

Adam, Tijjani; U, Hashim

2014-01-01

An aqueous ferric nitrate nonahydrate (Fe(NO3)3.9H2O) and magnesium oxide (MgO) were mixed and deposited on silicon nanowires (SiNWs), the carbon nanotubes (CNTs) formed by the concentration of Fe3O4/MgO catalysts with the mole ratio set at 0.15:9.85 and 600°C had diameter between 15.23 to 90nm with high-density distribution of CNT while those with the mole ratio set at 0.45:9.55 and 730°C had diameter of 100 to 230nm. The UV/Vis/NIR and FT-IR spectroscopes clearly confirmed the presence of the silicon-CNTs hybrid structure. UV/Vis/NIR, FT-IR spectra and FESEM images confirmed the silicon-CNT structure exists with diameters ranging between 15-230nm. Thus, the study demonstrated cost effective method of silicon-CNT composite nanowire formation via Iron-oxide Catalyze synthesis. PMID:25237290

Fabrication and transport property of artificial structure of CNTs using SPM nano-manipulation

NASA Astrophysics Data System (ADS)

Maejima, K.; Kida, M.; Yaguchi, Y.; Sudo, K.; Kawamura, T.; Morimoto, T.; Aoki, N.; Ochiai, Y.

2007-04-01

We have established a novel manipulation technique using a glass-micro capillary under a high-resolution CCD microscope so far. Two isolated multi-wall carbon nanotubes (MWNTs) are settled to form a well-aligned cross structure. Recently, we have tried to develop a fine manipulation system using a scanning probe microscope with a silicon cantilever. Therefore, thinner high-quality MWNTs (˜10 nm in diameter) can be utilized in this system. At the junction, we have observed weak localization and Fano-like-effect, zero bias anomaly whose traces were visible even at room temperature with thick MWNTs (˜100 nm in diameter). On the other hand, with thinner high-quality MWNTs (˜10 nm in diameter), we have observed also anomalous I-V characteristic and Altshuler-Aronov-Spivak-like magneto-oscillations at low temperature in the nano-space transport.

Silicon crystallization in nanodot arrays organized by block copolymer lithography

NASA Astrophysics Data System (ADS)

Perego, Michele; Andreozzi, Andrea; Seguini, Gabriele; Schamm-Chardon, Sylvie; Castro, Celia; BenAssayag, Gerard

2014-12-01

Asymmetric polystyrene- b-polymethylmethacrylate (PS- b-PMMA) block copolymers are used to fabricate nanoporous PS templates with different pore diameter depending on the specific substrate neutralization protocol. The resulting polymeric templates are used as masks for the subsequent deposition of a thin ( h = 5 nm) amorphous Si layer by electron beam evaporation. After removal of the polymeric film and of the silicon excess, well-defined hexagonally packed amorphous Si nanodots are formed on the substrate. Their average diameter ( d < 20 nm), density (1.2 × 1011 cm-2), and lateral distribution closely mimic the original nanoporous template. Upon capping with SiO2 and high temperature annealing (1050 °C, N2), each amorphous Si nanodot rearranges in agglomerates of Si nanocrystals ( d < 4 nm). The average diameter and shape of these Si nanocrystals strongly depend on the size of the initial Si nanodot.

Fast detection of humidity with a subwavelength-diameter fiber taper coated with gelatin film.

PubMed

Zhang, Lei; Gu, Fuxing; Lou, Jingyi; Yin, Xuefeng; Tong, Limin

2008-08-18

A subwavelength-diameter tapered optical fiber coated with gelatin layer for fast relative humidity (RH) sensing is reported. The sensing element is composed of a 680-nm-diameter fiber taper coated with a 80-nm-thickness 8-mm-length gelatin layer, and is operated at a wavelength of 1550 nm. When exposed to moisture, the change in refractive index of the gelatin layer changes the mode field of the guided mode of the coated fiber, and converts a portion of power from guided mode to radiation mode, resulting in RH-dependent loss for optical sensing. The sensor is operated within a wide humidity range (9-94% RH) with high sensitivity and good reversibility. Measured response time is about 70 ms, which is one or two orders of magnitude faster than other types of RH sensors relying on conventional optical fibers or films.

Increase of reliability of contact networks of electric transport, due to increase of strength of the joint unit of pipes of different diameters

NASA Astrophysics Data System (ADS)

Sabitov, L. S.; Kashapov, N. F.; Gilmanshin, I. R.; Gatiyatov, I. Z.; Kuznetsov, I. L.

2017-09-01

The feature of the stress state of the supports of the contact networks is the presence of a joint of pipes of different diameters, the ultimate state of which is determined, as a rule, the strength of the weld. The proposed unit allows to increase the reliability and strength of the connection and also exclude the presence of a weld bead on the outer surface of the pipe of smaller diameter in the place of its attachment to the upper end of the support ring.

Interactions and reversal-field memory in complex magnetic nanowire arrays

NASA Astrophysics Data System (ADS)

Rotaru, Aurelian; Lim, Jin-Hee; Lenormand, Denny; Diaconu, Andrei; Wiley, John. B.; Postolache, Petronel; Stancu, Alexandru; Spinu, Leonard

2011-10-01

Interactions and magnetization reversal of Ni nanowire arrays have been investigated by the first-order reversal curve (FORC) method. Several series of samples with controlled spatial distribution were considered including simple wires of different lengths and diameters (70 and 110 nm) and complex wires with a single modulated diameter along their length. Subtle features of magnetic interactions are revealed through a quantitative analysis of the local interaction field profile distributions obtained from the FORC method. In addition, the FORC analysis indicates that the nanowire systems with a mean diameter of 70 nm appear to be organized in symmetric clusters indicative of a reversal-field memory effect.

Correlation between size distribution and luminescence properties of spool-shaped InAs quantum dots

NASA Astrophysics Data System (ADS)

Xie, H.; Prioli, R.; Torelly, G.; Liu, H.; Fischer, A. M.; Jakomin, R.; Mourão, R.; Kawabata, R.; Pires, M. P.; Souza, P. L.; Ponce, F. A.

2017-05-01

InAs QDs embedded in an AlGaAs matrix have been produced by MOVPE with a partial capping and annealing technique to achieve controllable QD energy levels that could be useful for solar cell applications. The resulted spool-shaped QDs are around 5 nm in height and have a log-normal diameter distribution, which is observed by TEM to range from 5 to 15 nm. Two photoluminescence peaks associated with QD emission are attributed to the ground and the first excited states transitions. The luminescence peak width is correlated with the distribution of QD diameters through the diameter dependent QD energy levels.

Measuring Air Leaks into the Vacuum Space of Large Liquid Hydrogen Tanks

NASA Technical Reports Server (NTRS)

Youngquist, Robert; Starr, Stanley; Nurge, Mark

2012-01-01

Large cryogenic liquid hydrogen tanks are composed of inner and outer shells. The outer shell is exposed to the ambient environment while the inner shell holds the liquid hydrogen. The region between these two shells is evacuated and typically filled with a powderlike insulation to minimize radiative coupling between the two shells. A technique was developed for detecting the presence of an air leak from the outside environment into this evacuated region. These tanks are roughly 70 ft (approx. equal 21 m) in diameter (outer shell) and the inner shell is roughly 62 ft (approx. equal 19 m) in diameter, so the evacuated region is about 4 ft (approx. equal 1 m) wide. A small leak's primary effect is to increase the boil-off of the tank. It was preferable to install a more accurate fill level sensor than to implement a boil-off meter. The fill level sensor would be composed of an accurate pair of pressure transducers that would essentially weigh the remaining liquid hydrogen. This upgrade, allowing boil-off data to be obtained weekly instead of over several months, is ongoing, and will then provide a relatively rapid indication of the presence of a leak.

Repair Types, Procedures - Part 2

DTIC Science & Technology

2010-05-01

completely severed or severely damaged fuel lines, cut away the damaged section and use a piece of fuel- resistant rubber hose with an inner diameter...equal to the existing fuel line outer diameter to replace the damaged section. Ensure the repair hose extends far enough on each side of the damage to...accommodate two hose clamps, oriented 180° from one another. Flare the ends of the existing fuel line to improve the seal and prevent leakage

Static Gas-Charging Plug

NASA Technical Reports Server (NTRS)

Indoe, William

2012-01-01

A gas-charging plug can be easily analyzed for random vibration. The design features two steeped O-rings in a radial configuration at two different diameters, with a 0.050-in. (.1.3-mm) diameter through-hole between the two O-rings. In the charging state, the top O-ring is engaged and sealing. The bottom O-ring outer diameter is not squeezed, and allows air to flow by it into the tank. The inner diameter is stretched to plug the gland diameter, and is restrained by the O-ring groove. The charging port bushing provides mechanical stop to restrain the plug during gas charge removal. It also prevents the plug from becoming a projectile when removing gas charge from the accumulator. The plug can easily be verified after installation to ensure leakage requirements are met.

Polymer nanoimprinting using an anodized aluminum mold for structural coloration

NASA Astrophysics Data System (ADS)

Kikuchi, Tatsuya; Nishinaga, Osamu; Natsui, Shungo; Suzuki, Ryosuke O.

2015-06-01

Polymer nanoimprinting of submicrometer-scale dimple arrays with structural coloration was demonstrated. Highly ordered aluminum dimple arrays measuring 530-670 nm in diameter were formed on an aluminum substrate via etidronic acid anodizing at 210-270 V and subsequent anodic oxide dissolution. The nanostructured aluminum surface led to bright structural coloration with a rainbow spectrum, and the reflected wavelength strongly depends on the angle of the specimen and the period of the dimple array. The reflection peak shifts gradually with the dimple diameter toward longer wavelength, reaching 800 nm in wavelength at 670 nm in diameter. The shape of the aluminum dimple arrays were successfully transferred to a mercapto-ester ultra-violet curable polymer via self-assembled monolayer coating and polymer replications using a nanoimprinting technique. The nanostructured polymer surfaces with positively and negatively shaped dimple arrays also exhibited structural coloration based on the periodic nanostructure, and reflected light mostly in the visible region, 400-800 nm. This nanostructuring with structural coloration can be easily realized by simple techniques such as anodizing, SAM coating, and nanoimprinting.

Multiple double cross-section transmission electron microscope sample preparation of specific sub-10 nm diameter Si nanowire devices.

PubMed

Gignac, Lynne M; Mittal, Surbhi; Bangsaruntip, Sarunya; Cohen, Guy M; Sleight, Jeffrey W

2011-12-01

The ability to prepare multiple cross-section transmission electron microscope (XTEM) samples from one XTEM sample of specific sub-10 nm features was demonstrated. Sub-10 nm diameter Si nanowire (NW) devices were initially cross-sectioned using a dual-beam focused ion beam system in a direction running parallel to the device channel. From this XTEM sample, both low- and high-resolution transmission electron microscope (TEM) images were obtained from six separate, specific site Si NW devices. The XTEM sample was then re-sectioned in four separate locations in a direction perpendicular to the device channel: 90° from the original XTEM sample direction. Three of the four XTEM samples were successfully sectioned in the gate region of the device. From these three samples, low- and high-resolution TEM images of the Si NW were taken and measurements of the NW diameters were obtained. This technique demonstrated the ability to obtain high-resolution TEM images in directions 90° from one another of multiple, specific sub-10 nm features that were spaced 1.1 μm apart.

Microstructure, Chemistry, and Origin of Grain Rims on ilmenite from the Lunar Soil Finest Fraction

NASA Technical Reports Server (NTRS)

Christoffersen, Roy; Keller, Lindsay P.; McKay, David S.

1996-01-01

Analytical transmission electron microscope (TEM) observations reveal that ilmenite grains sampled from the sub-10 micron size fraction of Apollo 11 (10084) and Apollo 16 (61221, 67701) soils have rims 10-300 nm thick that are chemically and microstructurally distinct from the host ilmenite. The rims have a thin outer sublayer 10-50 nm thick that contains the ilmenite-incompatible elements Si, Al, Ca and S. This overlies a relatively thicker (50-250 nm) inner sublayer of nanocrystalline Ti-oxide precipitates in a matrix of single-crystal ilmenite that is structurally continuous with the underlying host grain. Microstructural information, as well as data from x-ray spectrometry (EDS) and electron energy loss spectrometry (EELS) analysis of the inner sublayer, suggest that both the inner and outer sublayer assemblages are reduced and that the inner layer is depleted in Fe relative to the underlying ilmenite. The chemistry of the outer sublayer suggests that it is a surface deposit of sputtered or impact-vaporized components from the bulk lunar soil. The inner sublayer is part of the original host grain that has been physically and chemically processed, but not amorphized, by solar ion irradiation and possibly some subsolidus heating. The fact that the deposited outer sublayer is consistently much thinner than the radiation-altered inner sublayer indicates that only a minor fraction of the total rim volume is a product of vapor or sputter deposition. This finding is in contrast to recent descriptions of thick deposited layers on one-third of regolith silicate grains and indicates that ilmenite and silicate rims as a group are different in the fraction of deposited material that they contain.

Vortex Mask: Making 80nm contacts with a twist!

NASA Astrophysics Data System (ADS)

Levenson, Marc D.; Dai, Grace; Ebihara, Takeaki

2002-12-01

An optical vortex has a phase that spirals like a corkscrew. Since any nonzero optical amplitude must have a well-defined phase, the axis of a vortex (where the phase is undefined) is always dark. Printed in negative resist, lowest order vortices would produce contact holes with 0.20.6 can be produced using a chromeless phase-edge mask composed of rectangles with phases of 0°, 90°, 180° and 270°. EMF and Kirchhoff-approximation simulations reveal that the image quality of the dark spots is excellent, and predict a process window with 15% exposure latitude and 400nm DOF for 80nm diameter spots on pitches >=250nm at σ=0.15. EMF simulations predict that the 0-270° phase step will not be excessively dark if the quartz wall is vertical. Chrome spots at the centers can control the diameters which otherwise are set by the parameters of the imaging system and exposure dose. Unwanted vortices can be erased from the image by exposing with a second, more conventional, trim mask. This method would be superior to the other ways of producing sub-wavelength vias, but successful implementation requires the development of appropriate negative-tone resist processes.

Gold Nanohole Array with Sub-1 nm Roughness by Annealing for Sensitivity Enhancement of Extraordinary Optical Transmission Biosensor

NASA Astrophysics Data System (ADS)

Zhang, Jian; Irannejad, Mehrdad; Yavuz, Mustafa; Cui, Bo

2015-05-01

Nanofabrication technology plays an important role in the performance of surface plasmonic devices such as extraordinary optical transmission (EOT) sensor. In this work, a double liftoff process was developed to fabricate a series of nanohole arrays of a hole diameter between 150 and 235 nm and a period of 500 nm in a 100-nm-thick gold film on a silica substrate. To improve the surface quality of the gold film, thermal annealing was conducted, by which an ultra-smooth gold film with root-mean-square (RMS) roughness of sub-1 nm was achieved, accompanied with a hole diameter shrinkage. The surface sensitivity of the nanohole arrays was measured using a monolayer of 16-mercaptohexadecanoic acid (16-MHA) molecule, and the surface sensitivity was increased by 2.5 to 3 times upon annealing the extraordinary optical transmission (EOT) sensor.

Replication of the nano-scale mold fabricated with focused ion beam

NASA Astrophysics Data System (ADS)

Gao, J. X.; Chan-Park, M. B.; Xie, D. Z.; Ngoi, Bryan K. A.

2004-12-01

Silicon mold fabricated with Focused Ion Beam lithography (FIB) was used to make silicone elastomer molds. The silicon mold is composed of lattice of holes which the diameter and depth are about 200 nm and 60 nm, respectively. The silicone elastomer material was then used to replicate slavery mold. Our study show the replication process with the elastomer mold had been performed successfully and the diameter of humps on the elastomer mold is near to that of holes on the master mold. But the height of humps in the elastomer mold is only 42 nm and it is different from the depth of holes in the master mold.

The second species of Gromia (Protista) from the deep sea: its natural history and association with the Pakistan margin oxygen minimum zone.

PubMed

Gooday, Andrew J; Bowser, Samuel S

2005-06-01

We describe a gromiid protist Gromia pyriformis sp. nov., from bathyal depths on the Pakistan margin (NE Arabian Sea), an area characterised by a well-developed Oxygen Minimum Zone (OMZ). The new species is smaller (length usually <1 mm) than the only other described deep-sea gromiid species (Gromia sphaerica) or the well-known coastal species Gromia oviformis. Its identification as a gromiid is based on the test-wall ultrastructure. This includes (i) an outer wall (165-300 nm thick) limited by an electron-opaque layer and perforated by pore structures which typically extend through its entire thickness, and (ii) inner "honeycomb membrane" structures which form a discontinuous sheet (18-20 nm thick) lying parallel to the outer wall. An outermost glycocalyx (approximately 75 nm thick), not observed in other gromiid species, is also present and imparts a finely granular appearance to the outer test surface, as seen by Scanning Electron Microscopy (SEM). Numerous rod-shaped prokaryotes are attached to the exterior of the glycocalyx. Gromia pyriformis sp. nov. typically occurs above the sediment-water interface, attached to the large arborescent foraminiferan Pelosina sp. It is confined to a very narrow bathymetric zone (approximately 1000 m water depth) in the lower portion of the OMZ, where bottom-water oxygen concentrations are approximately 0.2 ml l(-1).

Mid-section of a can-annular gas turbine engine with a cooling system for the transition

DOEpatents

Wiebe, David J.; Rodriguez, Jose L.

2015-12-08

A cooling system is provided for a transition (420) of a gas turbine engine (410). The cooling system includes a cowling (460) configured to receive an air flow (111) from an outlet of a compressor section of the gas turbine engine (410). The cowling (460) is positioned adjacent to a region of the transition (420) to cool the transition region upon circulation of the air flow within the cowling (460). The cooling system further includes a manifold (121) to directly couple the air flow (111) from the compressor section outlet to an inlet (462) of the cowling (460). The cowling (460) is configured to circulate the air flow (111) within an interior space (426) of the cowling (460) that extends radially outward from an inner diameter (423) of the cowling to an outer diameter (424) of the cowling at an outer surface.

A new quadrature annular resonator for 3 T MRI based on artificial-dielectrics.

PubMed

Mikhailovskaya, Anna A; Shchelokova, Alena V; Dobrykh, Dmitry A; Sushkov, Ivan V; Slobozhanyuk, Alexey P; Webb, Andrew

2018-06-01

Dielectric resonators have previously been constructed for ultra-high frequency magnetic resonance imaging and microscopy. However, it is challenging to design these dielectric resonators at clinical field strengths due to their intrinsically large dimensions, especially when using materials with moderate permittivity. Here we propose and characterize a novel approach using artificial-dielectrics which reduces substantially the required outer diameter of the resonator. For a resonator designed to operate in a 3 Tesla scanner using water as the dielectric, a reduction in outer diameter of 37% was achieved. When used in an inductively-coupled wireless mode, the sensitivity of the artificial-dielectric resonator was measured to be slightly higher than that of a standard dielectric resonator operating in its degenerate circularly-polarized hybrid electromagnetic modes (HEM 11 ). This study demonstrates the first application of an artificial-dielectric approach to MR volume coil design. Copyright © 2018 Elsevier Inc. All rights reserved.

Method to produce large, uniform hollow spherical shells

DOEpatents

Hendricks, C.D.

1983-09-26

The invention is a method to produce large uniform hollow spherical shells by (1) forming uniform size drops of heat decomposable or vaporizable material, (2) evaporating the drops to form dried particles, (3) coating the dried particles with a layer of shell forming material and (4) heating the composite particles to melt the outer layer and to decompose or vaporize the inner particle to form an expanding inner gas bubble. The expanding gas bubble forms the molten outer layer into a shell of relatively large diameter. By cycling the temperature and pressure on the molten shell, nonuniformities in wall thickness can be reduced. The method of the invention is utilized to produce large uniform spherical shells, in the millimeter to centimeter diameter size range, from a variety of materials and of high quality, including sphericity, concentricity and surface smoothness, for use as laser fusion or other inertial confinement fusion targets as well as other applications.

Development of a miniature double-pass cylindrical mirror electron energy analyzer (DPCMA), and its application to Auger photoelectron coincidence spectroscopy (APECS)

NASA Astrophysics Data System (ADS)

Kobayashi, Eiichi; Seo, Junya; Nambu, Akira; Mase, Kazuhiko

2007-09-01

We have developed a miniature double-pass cylindrical mirror electron energy analyzer (DPCMA) with an outer diameter of 26 mm. The DPCMA consists of a shield for the electric field, inner and outer cylinders, two pinholes with a diameter of 2.0 mm, and an electron multiplier. By assembling the DPCMA in a coaxially symmetric mirror electron energy analyzer (ASMA) coaxially and confocally we developed an analyzer for Auger photoelectron coincidence spectroscopy (APECS). The performance was estimated by measuring the Si-LVV-Auger Si-1s-photoelectron coincidence spectra of clean Si(1 1 1). The electron-energy resolution of the DPCMA was estimated to be E/Δ E = 20. This value is better than that of the miniature single-pass CMA ( E/Δ E = 12) that was used in the previous APECS analyzer.

A new quadrature annular resonator for 3 T MRI based on artificial-dielectrics

NASA Astrophysics Data System (ADS)

Mikhailovskaya, Anna A.; Shchelokova, Alena V.; Dobrykh, Dmitry A.; Sushkov, Ivan V.; Slobozhanyuk, Alexey P.; Webb, Andrew

2018-06-01

Dielectric resonators have previously been constructed for ultra-high frequency magnetic resonance imaging and microscopy. However, it is challenging to design these dielectric resonators at clinical field strengths due to their intrinsically large dimensions, especially when using materials with moderate permittivity. Here we propose and characterize a novel approach using artificial-dielectrics which reduces substantially the required outer diameter of the resonator. For a resonator designed to operate in a 3 Tesla scanner using water as the dielectric, a reduction in outer diameter of 37% was achieved. When used in an inductively-coupled wireless mode, the sensitivity of the artificial-dielectric resonator was measured to be slightly higher than that of a standard dielectric resonator operating in its degenerate circularly-polarized hybrid electromagnetic modes (HEM11). This study demonstrates the first application of an artificial-dielectric approach to MR volume coil design.

Metal halide arc discharge lamp having short arc length

NASA Technical Reports Server (NTRS)

Muzeroll, Martin E. (Inventor)

1994-01-01

A metal halide arc discharge lamp includes a sealed light-transmissive outer jacket, a light-transmissive shroud located within the outer jacket and an arc tube assembly located within the shroud. The arc tube assembly includes an arc tube, electrodes mounted within the arc tube and a fill material for supporting an arc discharge. The electrodes have a spacing such that an electric field in a range of about 60 to 95 volts per centimeter is established between the electrodes. The diameter of the arc tube and the spacing of the electrodes are selected to provide an arc having an arc diameter to arc length ratio in a range of about 1.6 to 1.8. The fill material includes mercury, sodium iodide, scandium tri-iodide and a rare gas, and may include lithium iodide. The lamp exhibits a high color rendering index, high lumen output and high color temperature.

Low-pressure water-cooled inductively coupled plasma torch

DOEpatents

Seliskar, C.J.; Warner, D.K.

1984-02-16

An inductively coupled plasma torch is provided which comprises an inner tube, including a sample injection port to which the sample to be tested is supplied and comprising an enlarged central portion in which the plasma flame is confined; an outer tube surrounding the inner tube and containing water therein for cooling the inner tube, the outer tube including a water inlet port to which water is supplied and a water outlet port spaced from the water inlet port and from which water is removed after flowing through the outer tube; and an rf induction coil for inducing the plasma in the gas passing into the tube through the sample injection port. The sample injection port comprises a capillary tube including a reduced diameter orifice, projecting into the lower end of the inner tube. The water inlet is located at the lower end of the outer tube and the rf heating coil is disposed around the outer tube above and adjacent to the water inlet.

Low-pressure water-cooled inductively coupled plasma torch

DOEpatents

Seliskar, Carl J.; Warner, David K.

1988-12-27

An inductively coupled plasma torch is provided which comprises an inner tube, including a sample injection port to which the sample to be tested is supplied and comprising an enlarged central portion in which the plasma flame is confined; an outer tube surrounding the inner tube and containing water therein for cooling the inner tube, the outer tube including a water inlet port to which water is supplied and a water outlet port spaced from the water inlet port and from which water is removed after flowing through the outer tube; and an r.f. induction coil for inducing the plasma in the gas passing into the tube through the sample injection port. The sample injection port comprises a capillary tube including a reduced diameter orifice, projecting into the lower end of the inner tube. The water inlet is located at the lower end of the outer tube and the r.f. heating coil is disposed around the outer tube above and adjacent to the water inlet.

Spontaneous formation of nanometer scale tubular vesicles in aqueous mixtures of lipid and block copolymer amphiphiles.

PubMed

Lim, Seng Koon; Wong, Andrew S W; de Hoog, Hans-Peter M; Rangamani, Padmini; Parikh, Atul N; Nallani, Madhavan; Sandin, Sara; Liedberg, Bo

2017-02-08

Many common amphiphiles self-assemble in water to produce heterogeneous populations of discrete and symmetric but polydisperse and multilamellar vesicles isolating the encapsulated aqueous core from the surrounding bulk. But when mixtures of amphiphiles of vastly different elastic properties co-assemble, their non-uniform molecular organization can stabilize lower symmetries and produce novel shapes. Here, using high resolution electron cryomicroscopy and tomography, we identify the spontaneous formation of a membrane morphology consisting of unilamellar tubular vesicles in dilute aqueous solutions of binary mixtures of two different amphiphiles of vastly different origins. Our results show that aqueous phase mixtures of a fluid-phase phospholipid and an amphiphilic block copolymer spontaneously assume a bimodal polymorphic character in a composition dependent manner: over a broad range of compositions (15-85 mol% polymer component), a tubular morphology co-exists with spherical vesicles. Strikingly, in the vicinity of equimolar compositions, an exclusively tubular morphology (L t ; diameter, ∼15 nm; length, >1 μm; core, ∼2.0 nm; wall, ∼5-6 nm) emerges in an apparent steady state. Theory suggests that the spontaneous stabilization of cylindrical vesicles, unaided by extraneous forces, requires a significant spontaneous bilayer curvature, which in turn necessitates a strongly asymmetric membrane composition. We confirm that such dramatic compositional asymmetry is indeed produced spontaneously in aqueous mixtures of a lipid and polymer through two independent biochemical assays - (1) reduction in the quenching of fluorophore-labeled lipids and (2) inhibition in the activity of externally added lipid-hydrolyzing phospholipase A2, resulting in a significant enrichment of the polymer component in the outer leaflet. Taken together, these results illustrate the coupling of the membrane shape with local composition through spontaneous curvature generation under conditions of asymmetric distribution of mixtures of disparate amphiphiles.

Influence of surface roughness on the oxidation behavior of a Ni-4.0Cr-5.7Al single crystal superalloy

NASA Astrophysics Data System (ADS)

Pei, Haiqing; Wen, Zhixun; Li, Zhenwei; Zhang, Yamin; Yue, Zhufeng

2018-05-01

The high-temperature oxidation dynamics and mechanisms of a Ni-based single crystal superalloy with four kinds of surface roughnesses were investigated by virtue of XRD, OM, SEM and EDS at 1000 °C. In the initial oxidation stage, outer (Ni, Co)O was mainly produced on the surfaces of the samples with Ra = 90 nm and 19 nm. Correspondingly, outer Cr2O3 and transient θ-Al2O3 were mainly formed on the surfaces with Ra = 509 nm and 182 nm. After 180 min oxidation, the values of instantaneous parabolic mass gain coefficients (kp) of the samples with all surface roughnesses were gradually consistent with the data of the growth parabolic coefficient of α-Al2O3. The oxidation mechanisms of Ni-based superalloy with different surface roughnesses were discussed by a model. The external diffusion flux of Al (DAl) increases with the increases of surface roughness. Thus, the required Al concentration decreases with the increases of surface roughness when the selective oxidation of Al occurrs to form a protective single α-Al2O3 film.

Supercontinuum generation from 437 to 2850 nm in a tapered fluorotellurite microstructured fiber

NASA Astrophysics Data System (ADS)

Wang, F.; Jia, Z. X.; Yao, C. F.; Wang, S. B.; Hu, M. L.; Wu, C. F.; Ohishi, Y.; Qin, W. P.; Qin, G. S.

2016-12-01

We demonstrated supercontinuum (SC) generation in a tapered fluorotellurite microstructured fiber (MF) with a sub-micrometer core diameter. Fluorotellurite MFs based on TeO2-BaF2-Y2O3 glasses were fabricated by using a rod-in-tube method and a tapered fluorotellurite MF with a minimum core diameter of ~0.65 µm was prepared by employing a tapering system. A 1560 nm femtosecond fiber laser was used as the pumping source. With increasing the peak power of the launched pump laser to ~11 kW, SC light expanding from 437 to 2850 nm was generated in the tapered fluorotellurite MF. In addition, relatively strong blue-shifted dispersive wave at ~489 nm was also observed from the tapered fluorotellurite MF.

Characterization of Nanofibrillated Cellulose Produced by Different Methods from Cabbage Outer Leaves.

PubMed

Khukutapan, Donnapa; Chiewchan, Naphaporn; Devahastin, Sakamon

2018-06-01

The potential use of cabbage outer leaves as a starting material for the production of nanofibrillated cellulose (NFC) was investigated. Chemical-free pretreatment methods, namely, autoclaving, ultrasonication (US), and high-shear homogenization (HS), were applied to remove noncellulosic components from cabbage cell walls prior to defibrillation, which was conducted by subjecting a pretreated sample to HS and then high-pressure homogenization. The sample undergone autoclaving at 130 °C for 2 hr was noted to contain a significantly higher cellulose content (36.5% dry mass) compared with the fresh leaves (12.48% dry mass). This led to an increase in the crystallinity index (CI) of the autoclaved cabbages from 30.8% to 50.7%. Further increase in the cellulose content (47.0% to 49.2% dry mass) was observed when subjecting the autoclaved sample to either US at 37 kHz for 1 hr, HS at 3800 × g for 15 min or HS followed by US at the aforementioned conditions. After pretreatment and defibrilllation, a suspension of NFC with the diameters of 4 to 50 nm was obtained, with the CI of 59.1% to 66.7%. Such a suspension exhibited a gel-like behavior with tan δ in the range of 0.12 to 0.13; the suspension exhibited a similar behavior to that prepared by the conventional chemical pretreatment method. NFC could be produced from cabbage outer leaves, which are an abundantly available by-product of a vegetable processing plant, via the combined hydrothermal and mechanical pretreatment without the use of any chemicals. This chemical-free preparation process is highly desirable as it leaves no residues in the product and causes no chemical waste that needs to be treated. Cabbage-based NFC also exhibits similar characteristics to that prepared via a chemically treated route. © 2018 Institute of Food Technologists®.

Transition of carbon nanostructures in heptane diffusion flames

NASA Astrophysics Data System (ADS)

Hu, Wei-Chieh; Hou, Shuhn-Shyurng; Lin, Ta-Hui

2017-02-01

The flame synthesis has high potential in industrial production of carbon nanostructure (CNS). Unfortunately, the complexity of combustion chemistry leads to less controlling of synthesized products. In order to improve the understanding of the relation between flames and CNSs synthesized within, experiments were conducted through heptane flames in a stagnation-point liquid-pool system. The operating parameters for the synthesis include oxygen supply, sampling position, and sampling time. Two kinds of nanostructures were observed, carbon nanotube (CNT) and carbon nano-onion (CNO). CNTs were synthesized in a weaker flame near extinction. CNOs were synthesized in a more sooty flame. The average diameter of CNTs formed at oxygen concentration of 15% was in the range of 20-30 nm. For oxygen concentration of 17%, the average diameter of CNTs ranged from 24 to 27 nm, while that of CNOs was around 28 nm. For oxygen concentration of 19%, the average diameter of CNOs produced at the sampling position 0.5 mm below the flame front was about 57 nm, while the average diameters of CNOs formed at the sampling positions 1-2.5 mm below the flame front were in the range of 20-25 nm. A transition from CNT to CNO was observed by variation of sampling position in a flame. We found that the morphology of CNS is directly affected by the presence of soot layer due to the carbonaceous environment and the growth mechanisms of CNT and CNO. The sampling time can alter the yield of CNSs depending on the temperature of sampling position, but the morphology of products is not affected.

Self-assembled nanotubes from single fluorescent amino acid

NASA Astrophysics Data System (ADS)

Babar, Dipak Gorakh; Sarkar, Sabyasachi

2017-04-01

Self-assembly of biomolecules has gained increasing attention as it generates various supramolecular structural assemblies having potential applications principally in biomedical sciences. Here, we show that amino acid like tryptophan or tyrosine readily aggregates as nanotubes via a simple self-assembly process. These were characterized by FTIR, scanning electron microscopy, and by fluorescence microscopy. Nanotubes prepared from tryptophan are having 200 nm inner diameter and those from tyrosine are having the same around 50 nm diameter.

Silicon Based Colloidal Quantum Dot and Nanotube Lasers

DTIC Science & Technology

2013-03-01

carrier density is theoretically and experimentally derived to be inversely proportional to the diameter; (b) demonstration of InGaN/ GaN light emitting...diodes and GaN single nanowire photonic crystal laser on silicon characterized by a lasing transition at λ=371.3 nm with a linewidth of 0.55 nm. The...derived to be inversely proportional to the diameter; (b) demonstration of InGaN/ GaN light emitting diodes and GaN single nanowire photonic crystal

Size resolved Internally Mixed Black Carbon and the Absorption Enhancement in the Indo-Gangetic Plain due to internally mixed BC

NASA Astrophysics Data System (ADS)

Tripathi, S. N.; Thamban, N.

2017-12-01

Indo-Gangetic Plain (IGP) is one of the most populated and polluted regions in northern India. Even though IGP is a well-known "absorbing aerosol hotspot", information of BC mixing state in IGP is mostly unknown. Our calculation on size resolved mixing state in IGP shown that the mixing state of BC changes with the core diameter of BC. The majority of BC particle were thickly coated ( 80%) at lower diameter (75-125 nm) and the externally mixed BC fraction was gradually increased at higher core diameter of BC (125-250 nm). The mean fraction of "thickly coated BC" particles (fTCBC) was found to be 61.6% for a BC core diameter of 70 to 450 nm, indicating that a large fraction of BC particles was internally mixed in IGP. The fTCBC increased after sunrise with a peak at about noontime, indicating that the formation of secondary organic aerosol under active photochemistry can enhance organic coating on a core of black carbon. A positive correlation between the fTCBC and the mass absorption cross-section at 781nm (MAC781) was also observed (r=0.58). Our results identify that the observed fTCBC in IGP could amplify the MAC781 approximately by a factor of 1.8, which may catalyze the positive radiative forcing.

Spin Polarization and Quantum Spins in Au Nanoparticles

PubMed Central

Li, Chi-Yen; Karna, Sunil K.; Wang, Chin-Wei; Li, Wen-Hsien

2013-01-01

The present study focuses on investigating the magnetic properties and the critical particle size for developing sizable spontaneous magnetic moment of bare Au nanoparticles. Seven sets of bare Au nanoparticle assemblies, with diameters from 3.5 to 17.5 nm, were fabricated with the gas condensation method. Line profiles of the X-ray diffraction peaks were used to determine the mean particle diameters and size distributions of the nanoparticle assemblies. The magnetization curves M(Ha) reveal Langevin field profiles. Magnetic hysteresis was clearly revealed in the low field regime even at 300 K. Contributions to the magnetization from different size particles in the nanoparticle assemblies were considered when analyzing the M(Ha) curves. The results show that the maximum particle moment will appear in 2.4 nm Au particles. A similar result of the maximum saturation magnetization appearing in 2.3 nm Au particles is also concluded through analysis of the dependency of the saturation magnetization MP on particle size. The MP(d) curve departs significantly from the 1/d dependence, but can be described by a log-normal function. Magnetization can be barely detected for Au particles larger than 27 nm. Magnetic field induced Zeeman magnetization from the quantum confined Kubo gap opening appears in Au nanoparticles smaller than 9.5 nm in diameter. PMID:23989607

Conductive atomic force microscopy measurements of nanopillar magnetic tunnel junctions

NASA Astrophysics Data System (ADS)

Evarts, E. R.; Hogg, C.; Bain, J. A.; Majetich, S. A.

2009-03-01

Magnetic tunnel junctions have been studied extensively for their magnetoresistance and potential uses in magnetic logic and data storage devices, but little is known about how their performance will scale with size. Here we examined the electronic behavior of 12 nm diameter magnetic tunnel junctions fabricated by a novel nanomasking process. Scanning electron microscopy images indicated feature diameter of 12 nm, and atomic force microscopy showed a height of 5 nm suggesting that unmasked regions have been milled on average to the oxide barrier layer, and areas should have the remnants of the free layer exposed with no remaining nanoparticle. Electrical contact was made to individual nanopillars using a doped-diamond-coated atomic force microscopy probe with a 40 nm radius of curvature at the tip. Off pillar we observed a resistance of 8.1 x 10^5 φ, while on pillar we found a resistance of 2.85 x 10^6 φ. Based on the RA product for this film, 120 φ-μm^2, a 12 nm diameter cylinder with perfect contact would have a resistance of 1.06 x 10^6 φ. The larger experimental value is consistent with a smaller contact area due to damaging the pillar during the ion milling process. The magnetoresistance characteristics of these magnetic tunnel junctions will be discussed.

Effect of sintering temperature of Ce3+-doped Lu3Al5O12 phosphors on light emission and properties of crystal structure for white-light-emitting diodes

NASA Astrophysics Data System (ADS)

Koizumi, Hiroshi; Watabe, Junya; Sugiyama, Shin; Hirabayashi, Hideaki; Homma, Tetsuya

2018-06-01

The effect of the sintering temperature of Ce3+-doped Lu3Al5O12 (Ce-LuAG) phosphors on the emission and properties of the crystal structure was studied. A cathodoluminescence peak at 317 nm, which was assigned to lattice defects, was exhibited in addition to emission peaks at 508 and 540 nm for the Ce-LuAG phosphors. The intensities of the 317 nm emission peak for the phosphors with mean particle diameters of 5.0 and 10.0 µm formed at a low sintering temperature of 1430 °C were higher than those for the phosphors with mean particle diameters of 18.0 and 20.5 µm formed at a high sintering temperature of 1550 °C. In contrast, the electroluminescence spectra for fabricated white-light-emitting diodes (LEDs) using the phosphors revealed that the intensity of the peak at 540 nm was strong for the mean particle diameters of 18.0 and 20.5 µm. The intensity of the 540 nm peak, which is attributed to the 4f→5d transition of the Ce3+ activator, showed a dependence on the sintering temperature. The relationship between the optical properties and the lattice defects is discussed.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Joseph Berkmans, A.; Jagannatham, M.; Priyanka, S.

Highlights: • Polymer wastes are converted into ultrafine and nano carbon tubes and spheres. • Simple process with a minimal processing time. • It is a catalyst free and solvent free approach. • This process forms branched ultrafine carbon tubules with nano channels. - Abstract: Upcycling polymer wastes into useful, and valuable carbon based materials, is a challenging process. We report a novel catalyst-free and solvent-free technique for the formation of nano channeled ultrafine carbon tubes (NCUFCTs) and multiwalled carbon nanotubes (MWCNTs) from polyethylene terephthalate (PET) wastes, using rotating cathode arc discharge technique. The soot obtain from the anode containsmore » ultrafine and nano-sized solid carbon spheres (SCS) with a mean diameter of 221 nm and 100 nm, respectively, formed at the lower temperature region of the anode where the temperature is approximately 1700 °C. The carbon spheres are converted into long “Y” type branched and non-branched NCUFCTs and MWCNTs at higher temperature regions where the temperature is approximately 2600 °C, with mean diameters of 364 nm and 95 nm, respectively. Soot deposited on the cathode is composed of MWCNTs with a mean diameter of 20 nm and other nanoparticles. The tubular structures present in the anode are longer, bent and often coiled with lesser graphitization compared to the nanotubes in the soot on the cathode.« less

Synthesis of tubular nanostructures from wheat bran albumins during proteolysis with V8 protease in the presence of calcium ions.

PubMed

Chaquilla-Quilca, G; Balandrán-Quintana, R R; Azamar-Barrios, J A; Ramos-Clamont Montfort, G; Mendoza-Wilson, A M; Mercado-Ruiz, J N; Madera-Santana, T J; López-Franco, Y L; Luna-Valdez, J G

2016-06-01

There are very few reports on the self-assembly of peptides derived from proteins of agro industrial byproducts origin. Although it has been claimed that purity is a determining factor in peptide self-assembly, whether proteins extracted using water along with other components also form self-assembled structures is not known. The results of this work prove that albumins from wheat bran, a byproduct obtained from the milling industry, can form tubular nanostructures during their hydrolysis with the V8 protease in the presence of Ca(2+). Electron microscopy of the hydrolysate revealed that under specific conditions, long filaments are formed, which are nanotubes of several microns in length, with inner and outer diameters of 100 and 200 nm, respectively. The infrared analysis of the hydrolysate identified (-)OOC-Ca(2+) interactions and changes in beta sheet content in response to variations in protein/V8/Ca(2+) molar ratios. A model that explains the probable mechanism of the observed self-assembly is discussed. Copyright © 2016 Elsevier Ltd. All rights reserved.

Studies on cryogenic Xe capillary jet target for laser-produced plasma EUV-light source

NASA Astrophysics Data System (ADS)

Inoue, T.; Nica, P. E.; Kaku, K.; Shimoura, A.; Amano, S.; Miyamoto, S.; Mochizuki, T.

2006-03-01

In this paper, characterizations of a cryogenic Xe capillary jet target for a laser-produced plasma extreme ultraviolet (EUV) light source are reported. The capillary jet target is a candidate of fast-supplying targets for mitigating debris generation and target consumption in a vacuum chamber without reducing the EUV conversion efficiency. Xe capillary jets (jet velocity ~ 0.4 m/s) were generated in vacuum by using annular nozzles chilled to ~ 170 K at a Xe backing pressure of ~ 0.7 MPa. Forming mechanisms of the capillary jet targets were studied by using numerical calculations. Furthermore, laser-produced plasma EUV generation was performed by irradiating a Nd:YAG laser (1064 nm, ~ 0.5 J, 10 ns, 120 μmφ, ~ 4×10 11 W/cm2) on a Xe capillary jet target (outer / inner diameter = 100 / 70 μmφ). The angular distribution of EUV generation was approximately uniform around the Xe capillary jet target, and the peak kinetic energy of the fast-ions was evaluated to be ~ 2 keV.

Tunable porosities and shapes of fullerene-like spheres.

PubMed

Dielmann, Fabian; Fleischmann, Matthias; Heindl, Claudia; Peresypkina, Eugenia V; Virovets, Alexander V; Gschwind, Ruth M; Scheer, Manfred

2015-04-13

The formation of reversible switchable nanostructures monitored by solution and solid-state methods is still a challenge in supramolecular chemistry. By a comprehensive solid state and solution study we demonstrate the potential of the fivefold symmetrical building block of pentaphosphaferrocene in combination with Cu(I) halides to switch between spheres of different porosity and shape. With increasing amount of CuX, the structures of the formed supramolecules change from incomplete to complete spherically shaped fullerene-like assemblies possessing an Ih -C80 topology at one side and to a tetrahedral-structured aggregate at the other. In the solid state, the formed nano-sized aggregates reach an outer diameter of 3.14 and 3.56 nm, respectively. This feature is used to reversibly encapsulate and release guest molecules in solution. © 2015 The Authors. Published by Wiley-VCH Verlag GmbH & Co. KGaA. This is an open access article under the terms of the Creative Commons Attribution Non-Commercial License, which permits use, distribution and reproduction in any medium, provided the original work is properly cited and is not used for commercial purposes.

Extracellular Vesicles Present in Human Ovarian Tumor Microenvironments Induce a Phosphatidylserine Dependent Arrest in the T Cell Signaling Cascade

PubMed Central

Kelleher, Raymond J.; Balu-Iyer, Sathy; Loyall, Jenni; Sacca, Anthony J.; Shenoy, Gautam N.; Peng, Peng; Iyer, Vandana; Fathallah, Anas M.; Berenson, Charles S.; Wallace, Paul K.; Tario, Joseph; Odunsi, Kunle; Bankert, Richard B.

2015-01-01

The identification of immunosuppressive factors within human tumor microenvironments, and the ability to block these factors, would be expected to enhance patients’ anti-tumor immune responses. We previously established that an unidentified factor, or factors, present in ovarian tumor ascites fluids reversibly inhibited the activation of T cells by arresting the T cell signaling cascade. Ultracentrifugation of the tumor ascites fluid has now revealed a pellet that contains small extracellular vesicles (EV) with an average diameter of 80nm. The T cell arrest was determined to be causally linked to phosphatidylserine (PS) that is present on the outer leaflet of the vesicle bilayer, as a depletion of PS expressing EV or a blockade of PS with anti-PS antibody significantly inhibits the vesicle induced signaling arrest. The inhibitory EV were also isolated from solid tumor tissues. The presence of immune suppressive vesicles in the microenvironments of ovarian tumors and our ability to block their inhibition of T cell function represent a potential therapeutic target for patients with ovarian cancer. PMID:26112921

High-resolution electron microscopic evidence for the filamentous structure of the cyst wall in Giardia muris and Giardia duodenalis.

PubMed

Erlandsen, S L; Bemrick, W J; Pawley, J

1989-10-01

High-resolution morphological studies of the cyst wall of Giardia spp. were performed using low-voltage scanning electron microscopy (LVSEM) and transmission electron microscopy (TEM). The cyst wall was composed of membranous and filamentous layers. The membranous layer consisted of an inner and an outer cyst membrane separated by a thin layer of cytoplasm. The filamentous layer contained individual filaments that ranged from 7 to 20 nm in diameter when measured by LVSEM, formed a dense meshwork with branches or interconnections, and were occasionally arranged on the surface in whorled patterns. Cysts of Giardia muris from mice, Giardia duodenalis from dogs, pigs, voles, beavers, muskrats, and humans, and Giardia psittaci from a bird (parakeet), possessed an essentially identical wall composed of filaments. Inducement of excystation in viable Giardia cysts produced a dramatic increase in the interfilament spacing over an entire cyst, but none was observed in heat-killed or chemically fixed control cysts. These results demonstrated that the cyst wall of Giardia spp. was composed of a complex arrangement of filaments, presumably formed during the process of encystment.

Crystal Initiation Structures in Developing Enamel: Possible Implications for Caries Dissolution of Enamel Crystals

PubMed Central

Robinson, Colin; Connell, Simon D.

2017-01-01

Investigations of developing enamel crystals using Atomic and Chemical Force Microscopy (AFM, CFM) have revealed a subunit structure. Subunits were seen in height images as collinear swellings about 30 nM in diameter on crystal surfaces. In friction mode they were visible as positive regions. These were similar in size (30–50 nM) to collinear spherical structures, presumably mineral matrix complexes, seen in developing enamel using a freeze fracturing/freeze etching procedure. More detailed AFM studies on mature enamel suggested that the 30–50 nM structures were composed of smaller units, ~10–15 nM in diameter. These were clustered in hexagonal or perhaps a spiral arrangement. It was suggested that these could be the imprints of initiation sites for mineral precipitation. The investigation aimed at examining original freeze etched images at high resolution to see if the smaller subunits observed using AFM in mature enamel were also present in developing enamel i.e., before loss of the organic matrix. The method used was freeze etching. Briefly samples of developing rat enamel were rapidly frozen, fractured under vacuum, and ice sublimed from the fractured surface. The fractured surface was shadowed with platinum or gold and the metal replica subjected to high resolution TEM. For AFM studies high-resolution tapping mode imaging of human mature enamel sections was performed in air under ambient conditions at a point midway between the cusp and the cervical margin. Both AFM and freeze etch studies showed structures 30–50 nM in diameter. AFM indicated that these may be clusters of somewhat smaller structures ~10–15 nM maybe hexagonally or spirally arranged. High resolution freeze etching images of very early enamel showed ~30–50 nM spherical structures in a disordered arrangement. No smaller units at 10–15 nM were clearly seen. However, when linear arrangements of 30–50 nM units were visible the picture was more complex but also smaller units including ~10–15 nM units could be observed. Conclusions: Structures ~10–15 nM in diameter were detected in developing enamel. While the appearance was complex, these were most evident when the 30–5 nM structures were in linear arrays. Formation of linear arrays of subunits may be associated with the development of mineral initiation sites and attendant processing of matrix proteins. PMID:28670283

Arrays of size and distance controlled platinum nanoparticles fabricated by a colloidal method

NASA Astrophysics Data System (ADS)

Manzke, Achim; Vogel, Nicolas; Weiss, Clemens K.; Ziener, Ulrich; Plettl, Alfred; Landfester, Katharina; Ziemann, Paul

2011-06-01

Based on emulsion polymerization in the presence of a Pt complex, polystyrene (PS) particles were prepared exhibiting a well defined average diameter with narrow size-distribution. Furthermore, the colloids contain a controlled concentration of the Pt precursor complex. Optimized coating of Si substrates with such colloids leads to extended areas of hexagonally ordered close-packed PS particles. Subsequent application of plasma etching and annealing steps allows complete removal of the PS carriers and in parallel nucleation and growth of Pt nanoparticles (NPs) which are located at the original center of the PS colloids. In this way, hexagonally arranged spherical Pt NPs are obtained with controlled size and interparticle distances demonstrating variability and precision with so far unknown parameter scalability. This control is demonstrated by the fabrication of Pt NP arrays at a fixed particle distance of 185 nm while systematically varying the diameters between 8 and 15 nm. Further progress could be achieved by seeded emulsion polymerization. Here, Pt loaded PS colloids of 130 nm were used as seeds for a subsequent additional emulsion polymerization, systematically enlarging the diameter of the PS particles. Applying the plasma and annealing steps as above, in this way hexagonally ordered arrays of 9 nm Pt NPs could be obtained at distances up to 260 nm. To demonstrate their stability, such Pt particles were used as etching masks during reactive ion etching thereby transferring their hexagonal pattern into the Si substrate resulting in corresponding arrays of nanopillars.Based on emulsion polymerization in the presence of a Pt complex, polystyrene (PS) particles were prepared exhibiting a well defined average diameter with narrow size-distribution. Furthermore, the colloids contain a controlled concentration of the Pt precursor complex. Optimized coating of Si substrates with such colloids leads to extended areas of hexagonally ordered close-packed PS particles. Subsequent application of plasma etching and annealing steps allows complete removal of the PS carriers and in parallel nucleation and growth of Pt nanoparticles (NPs) which are located at the original center of the PS colloids. In this way, hexagonally arranged spherical Pt NPs are obtained with controlled size and interparticle distances demonstrating variability and precision with so far unknown parameter scalability. This control is demonstrated by the fabrication of Pt NP arrays at a fixed particle distance of 185 nm while systematically varying the diameters between 8 and 15 nm. Further progress could be achieved by seeded emulsion polymerization. Here, Pt loaded PS colloids of 130 nm were used as seeds for a subsequent additional emulsion polymerization, systematically enlarging the diameter of the PS particles. Applying the plasma and annealing steps as above, in this way hexagonally ordered arrays of 9 nm Pt NPs could be obtained at distances up to 260 nm. To demonstrate their stability, such Pt particles were used as etching masks during reactive ion etching thereby transferring their hexagonal pattern into the Si substrate resulting in corresponding arrays of nanopillars. Electronic supplementary information (ESI) available: Detailed description of the experimental part (S1-S4) platinum concentration inside the polymer particles synthesized by a seeded polymerization from the same seed particles measured by ICP-OES (Fig. S1 and S5); SEM image of Pt complex containing PS particles after oxygen plasma treatment (Fig. S2 and S6); effect of hydrofluoric acid treatment on silicon oxide elevation under Pt NPs (Fig. S3 and S6); SEM images demonstrating the variability of Pt NP distance while keeping the diameter constant (Fig. S4 and S8); results of experimental determination of Pt content by ICP-OES (Tables S1 and S9); diameter of the particles at different fabrication states (Tables S2 and S10). See DOI: 10.1039/c1nr10169b

The human, primate and rabbit ultraviolet action spectra

NASA Technical Reports Server (NTRS)

Pitts, D. G.; Gibbons, W. D.

1972-01-01

A 5000 watt xenon-mercury high pressure lamp was used to produce a continuous ultraviolet spectrum. Human and animal exposures were made to establish the photokeratitis threshold and abiotic action spectrum. The lower limit of the abiotic action spectrum was 220 nm while the upper limit was 310 nm. The radiant exposure threshold at 270 nm was 0.005 watts/sq cm for the rabbit, 0.004 watts/sq cm for the primate, and 0.004 watts/ sq cm for the human. The rabbit curve was bi-peaked with minimums at 220 nm, 240 nm and 270 nm. The primate curve was tri-peaked with minimums at 220 nm, 240 nm and 270 nm. The human data showed a rather shallow curve with a minimum at 270 nm. Formulas and calculations are given to predict minimum exposure times for ocular damage to man in outer space, to establish valid safety criteria, and to establish protective design criteria.

Ryanodine receptors regulate arterial diameter and wall [Ca2+] in cerebral arteries of rat via Ca2+-dependent K+ channels

PubMed Central

Knot, Harm J; Standen, Nicholas B; Nelson, Mark T

1998-01-01

The effects of inhibitors of ryanodine-sensitive calcium release (RyR) channels in the sarcoplasmic reticulum (SR) and Ca2+-dependent potassium (KCa) channels on the membrane potential, intracellular [Ca2+], and diameters of small pressurized (60 mmHg) cerebral arteries (100–200 μm) were studied using digital fluorescence video imaging of arterial diameter and wall [Ca2+], combined with microelectrode measurements of arterial membrane potential. Ryanodine (10 μm), an inhibitor of RyR channels, depolarized by 9 mV, increased intracellular [Ca2+] by 46 nm and constricted pressurized (to 60 mmHg) arteries with myogenic tone by 44 μm (∼22 %). Iberiotoxin (100 nm), a blocker of KCa channels, under the same conditions, depolarized the arteries by 10 mV, increased arterial wall calcium by 51 nm, and constricted by 37 μm (∼19 %). The effects of ryanodine and iberiotoxin were not additive and were blocked by inhibitors of voltage-dependent Ca2+ channels. Caffeine (10 mm), an activator of RyR channels, transiently increased arterial wall [Ca2+] by 136 ± 9 nm in control arteries and by 158 ± 12 nm in the presence of iberiotoxin. Caffeine was relatively ineffective in the presence of ryanodine, increasing [calcium] by 18 ± 5 nm. In the presence of blockers of voltage-dependent Ca2+ channels (nimodipine, diltiazem), ryanodine and inhibitors of the SR calcium ATPase (thapsigargin, cyclopiazonic acid) were without effect on arterial wall [Ca2+] and diameter. These results suggest that local Ca2+ release originating from RyR channels (Ca2+ sparks) in the SR of arterial smooth muscle regulates myogenic tone in cerebral arteries solely through activation of KCa channels, which regulate membrane potential through tonic hyperpolarization, thus limiting Ca2+ entry through L-type voltage-dependent Ca2+ channels. KCa channels therefore act as a negative feedback control element regulating arterial diameter through a reduction in global intracellular free [Ca2+]. PMID:9490841

Preparation, characterization and in vitro antimicrobial activity of liposomal ceftazidime and cefepime against Pseudomonas aeruginosa strains

PubMed Central

Torres, Ieda Maria Sapateiro; Bento, Etiene Barbosa; Almeida, Larissa da Cunha; de Sá, Luisa Zaiden Carvalho Martins; Lima, Eliana Martins

2012-01-01

Pseudomonas aeruginosa is an opportunistic microorganism with the ability to respond to a wide variety of environmental changes, exhibiting a high intrinsic resistance to a number of antimicrobial agents. This low susceptibility to antimicrobial substances is primarily due to the low permeability of its outer membrane, efflux mechanisms and the synthesis of enzymes that promote the degradation of these drugs. Cephalosporins, particularty ceftazidime and cefepime are effective against P. aeruginosa, however, its increasing resistance has limited the usage of these antibiotics. Encapsulating antimicrobial drugs into unilamellar liposomes is an approach that has been investigated in order to overcome microorganism resistance. In this study, antimicrobial activity of liposomal ceftazidime and cefepime against P. aeruginosa ATCC 27853 and P. aeruginosa SPM-1 was compared to that of the free drugs. Liposomal characterization included diameter, encapsulation efficiency and stability. Minimum Inhibitory Concentration (MIC) was determined for free and liposomal forms of both drugs. Minimum Bactericidal Concentration (MBC) was determined at concentrations 1, 2 and 4 times MIC. Average diameter of liposomes was 131.88 nm and encapsulation efficiency for cefepime and ceftazidime were 2.29% end 5.77%, respectively. Improved stability was obtained when liposome formulations were prepared with a 50% molar ratio for cholesterol in relation to the phospholipid. MIC for liposomal antibiotics for both drugs were 50% lower than that of the free drug, demonstrating that liposomal drug delivery systems may contribute to increase the antibacterial activity of these drugs. PMID:24031917

Spectral shaping of an all-fiber torsional acousto-optic tunable filter.

PubMed

Ko, Jeakwon; Lee, Kwang Jo; Kim, Byoung Yoon

2014-12-20

Spectral shaping of an all-fiber torsional acousto-optic (AO) tunable filter is studied. The technique is based on the axial modulation of AO coupling strength along a highly birefringent optical fiber, which is achieved by tailoring the outer diameter of the fiber along its propagation axis. Two kinds of filter spectral shaping schemes-Gaussian apodization and matched filtering with triple resonance peaks-are proposed and numerically investigated under realistic experimental conditions: at the 50-cm-long AO interaction length of the fiber and at half of the original fiber diameter as the minimum thickness of the tailored fiber section. The results show that the highest peak of sidelobe spectra in filter transmission is suppressed from 11.64% to 0.54% via Gaussian modulation of the AO coupling coefficient (κ). Matched filtering with triple resonance peaks operating with a single radio frequency signal is also achieved by cosine modulation of κ, of which the modulation period determines the spectral distance between two satellite peaks located in both wings of the main resonance peak. The splitting of two satellite peaks in the filter spectra reaches 48.2 nm while the modulation period varies from 7.7 to 50 cm. The overall peak power of two satellite resonances is calculated to be 22% of the main resonance power. The results confirm the validity and practicality of our approach, and we predict robust and stable operation of the designed all-fiber torsional AO filters.

Common path ball lens probe for optical coherence tomography (Conference Presentation)

NASA Astrophysics Data System (ADS)

Singh, Kanwarpal; Yamada, Daisuke; Tearney, Guillermo J.

2016-02-01

Background: Common path probes are highly desirable for optical coherence tomography (OCT) as they reduce system complexity and cost. In this work we report an all-fiber common path side viewing monolithic probe for coronary artery imaging. Methods: Our common path probe was designed for spectrometer based Fourier domain OCT at 1310 nm wavelength. Light from the fiber expands in the coreless fiber region and then focussed by the ball lens. Reflection from ball lens-air interface served as reference signal. The monolithic ball lens probe was assembled within a 560 µmouter diameter drive shaft which was attached to a rotary junction. The drive shaft was placed inside an outer, transparent sheath of 800 µm diameter. Results: With a source input power of 25 mW, we could achieve sensitivity of 100.5 dB. The axial resolution of the system was found to be 15.6 µm in air and the lateral resolution (full width half maximum) was approximately 49 µm. As proof of principal, images of skin acquired using this probe demonstrated clear visualization of the stratum corneum, epidermis, and papillary dermis, along with sweat ducts. Conclusion: In this work we have demonstrated a monolithic, ball lens common, path probe for OCT imaging. The designed ball lens probe is easy to fabricate using a laser splicer. Based on the features and capability of common path probes to provide a simpler solution for OCT, we believe that this development will be an important enhancement for certain types of catheters.

The outer magnetosphere. [composition and comparison with earth

NASA Technical Reports Server (NTRS)

Schardt, A. W.; Behannon, K. W.; Lepping, R. P.; Carbary, J. F.; Eviatar, A.; Siscoe, G. L.

1984-01-01

Similarities between the Saturnian and terrestrial outer magnetosphere are examined. Saturn, like earth, has a fully developed magnetic tail, 80 to 100 RS in diameter. One major difference between the two outer magnetospheres is the hydrogen and nitrogen torus produced by Titan. This plasma is, in general, convected in the corotation direction at nearly the rigid corotation speed. Energies of magnetospheric particles extend to above 500 keV. In contrast, interplanetary protons and ions above 2 MeV have free access to the outer magnetosphere to distances well below the Stormer cutoff. This access presumably occurs through the magnetotail. In addition to the H+, H2+, and H3+ ions primarily of local origin, energetic He, C, N, and O ions are found with solar composition. Their flux can be substantially enhanced over that of interplanetary ions at energies of 0.2 to 0.4 MeV/nuc.

Bypass of the maxillary artery to proximal middle cerebral artery.

PubMed

Ma, Lin; Ren, He-cheng; Huang, Ying

2015-03-01

The objective of this work was to explore the feasibility of bypass between the maxillary artery (MA) and proximity of middle cerebral artery (MCA). Ten fixed and perfused adult cadaver heads were dissected bilaterally, 20 sides in total. The superficial temporal artery and its 2 branches were dissected, and outer diameters were measured. The MA and its branch were exposed as well as deep temporal artery; outer diameter of MA was measured. The lengths between the external carotid artery, internal carotid artery, maxillary artery, and proximal middle cerebral artery were measured. Ten healthy adults as targets (20 sides), inner diameter and blood flow dynamic parameters of the common carotid artery, external carotid artery, internal carotid artery, maxillary artery, superficial temporal artery, and its 2 branches were done with ultrasound examination. The mean outer diameter of MA (2.60 ± 0.20 mm) was larger than that of the temporal artery trunk (1.70 ± 0.30 mm). The mean lengths of graft vessels between the internal carotid artery, external carotid artery, and the bifurcation section of MCA (171.00 ± 2.70 and 162.40 ± 2.60 mm) were longer than the mean lengths of graft vessels between MA and MCA bifurcation section (61.70 ± 1.50 mm). In adults, the mean blood flow of the second part of MA (62.70 ± 13.30 mL/min) was more than that of the 2 branches of the superficial temporal artery (15.90 ± 3.70 mL/min and 17.70 ± 4.10 ml/min). Bypass between the maxillary artery and proximity of middle cerebral artery is feasible. It is a kind of effective high flow bypass with which the graft vessel is shorter and straighter than the bypass between internal carotid artery or external carotid artery and proximity of middle cerebral artery.

Coring device with a improved core sleeve and anti-gripping collar with a collective core catcher

DOE Office of Scientific and Technical Information (OSTI.GOV)

Story, A.L.; Filshtinsky, M.

1986-01-28

This patent describes an improved coring apparatus used in combination with a coring bit and drill string. This device consists of: an outer driving structure adapted to be connected at one end to the coring bit for cutting a core in a borehole, and at the other end to the lower end of the drill string in telescoping and co-rotatable manner therewith; an inner barrel disposed within the outer driving structure and including a lower end portion adjacent to the bit; first means supporting the inner barrel in spaced relationship to the outer driving structure while permitting rotation of themore » driving structure with respect to the inner barrel; a woven metal mesh sleeve mounted in surrounding relation on at least a portion of the exterior surface of the inner barrel; second means, connected to a free end of the sleeve opposite the leading portion of the sleeve, for maintaining the portion of the sleeve which surrounds the inner barrel in compression and to maintain an inside diameter greater than the outside diameter of the inner barrel of the portion of the sleeve surrounding the inner barrel while the portion of the sleeve positioned inside the inner barrel being in tension to grip and compress a core received within the sleeve and having an outside diameter less than the inside diameter of the inner barrel when in tension, wherein the second means is also for engaging the core when the means is drawn into the inner barrel, and third means positioned within the inner barrel and connected to the leading portion of the sleeve to draw the sleeve within the inner barrel and to apply tension to the portion of the sleeve within the barrel to encase and grip the core as it is cut.« less

Unraveling the Helix Nebula: Its Structure and Knots

NASA Astrophysics Data System (ADS)

O'Dell, C. R.; McCullough, Peter R.; Meixner, Margaret

2004-11-01

Through Hubble Space Telescope (HST) imaging of the inner part of the main ring of the Helix Nebula, together with CTIO 4 m images of the fainter outer parts, we have a view of unprecedented quality of the nearest bright planetary nebula. These images have allowed us to determine that the main ring of the nebula is composed of an inner disk of about 499" diameter (0.52 pc) surrounded by an outer ring (in reality a torus) of 742" diameter (0.77 pc) whose plane is highly inclined to the plane of the disk. This outer ring is surrounded by an outermost ring of 1500" (1.76 pc) diameter, which is flattened on the side colliding with the ambient interstellar medium. The inner disk has an extended distribution of low-density gas along its rotational axis of symmetry, and the disk is optically thick to ionizing radiation, as is the outer ring. Published radial velocities of the knots provide support for the two-component structure of the main ring of the nebula and for the idea that the knots found there are expanding along with the nebular material from which they recently originated. These velocities indicate a spatial expansion velocity of the inner disk of 40 and 32 km s-1 for the outer ring, which yields expansion ages of 6560 and 12,100 yr, respectively. The outermost ring may be partially ionized through scattered recombination continuum from the inner parts of the nebula, but shocks certainly are occurring in it. This outermost ring probably represents a third period of mass loss by the central star. There is one compact, outer object that is unexplained, showing shock structures indicating a different orientation of the gas flow from that of the nebula. There is a change in the morphology of the knots as a function of the distance from the local ionization front. This supports a scenario in which the knots are formed in or near the ionization front and are then sculpted by the stellar radiation from the central star as the ionization front advances beyond them. Based in part on observations with the NASA/ESA Hubble Space Telescope, obtained at the Space Telescope Science Institute, which is operated by the Association of Universities for Research in Astronomy, Inc., under NASA contract NAS5-26555. Based in part on observations obtained at the Cerro Tololo Inter-American Observatory, which is operated by the Association of Universities for Research in Astronomy, Inc., under a Cooperative Agreement with the National Science Foundation.

Molecular scaffold reorganization at the transmitter release site with vesicle exocytosis or botulinum toxin C1.

PubMed

Stanley, Elise F; Reese, Tom S; Wang, Gary Z

2003-10-01

Neurotransmitter release sites at the freeze-fractured frog neuromuscular junction are composed of inner and outer paired rows of large membrane particles, the putative calcium channels, anchored by the ribs of an underlying protein scaffold. We analysed the locations of the release site particles as a reflection of the scaffold structure, comparing particle distributions in secreting terminals with those where secretion was blocked with botulinum toxin A, which cleaves a small segment off SNAP-25, or botulinum toxin C1, which cleaves the cytoplasmic domain of syntaxin. In the idle terminal the inner and outer paired rows were located approximately 25 and approximately 44 nm, respectively, from the release site midline. However, adjacent to vesicular fusion sites both particle rows were displaced towards the midline by approximately 25%. The intervals between the particles along each row were examined by a nearest-neighbour approach. In control terminals the peak interval along the inner row was approximately 17 nm, consistent with previous reports and the spacing of the scaffold ribs. While the average distance between particles in the outer row was also approximately 17 nm, a detailed analysis revealed short 'linear clusters' with a approximately 14 nm interval. These clusters were enriched at vesicle fusion sites, suggesting an association with the docking sites, and were eliminated by botulinum C1, but not A. Our findings suggest, first, that the release site scaffold ribs undergo a predictable, and possibly active, shortening during exocytosis and, second, that at the vesicle docking site syntaxin plays a role in the cross-linking of the rib tips to form the vesicle docking sites.

Genotoxicity of nanomaterials: DNA damage and micronuclei induced by carbon nanotubes and graphite nanofibres in human bronchial epithelial cells in vitro.

PubMed

Lindberg, Hanna K; Falck, Ghita C-M; Suhonen, Satu; Vippola, Minnamari; Vanhala, Esa; Catalán, Julia; Savolainen, Kai; Norppa, Hannu

2009-05-08

Despite the increasing industrial use of different nanomaterials, data on their genotoxicity are scant. In the present study, we examined the potential genotoxic effects of carbon nanotubes (CNTs; >50% single-walled, approximately 40% other CNTs; 1.1 nm x 0.5-100 microm; Sigma-Aldrich) and graphite nanofibres (GNFs; 95%; outer diameter 80-200 nm, inner diameter 30-50 nm, length 5-20 microm; Sigma-Aldrich) in vitro. Genotoxicity was assessed by the single cell gel electrophoresis (comet) assay and the micronucleus assay (cytokinesis-block method) in human bronchial epithelial BEAS 2B cells cultured for 24h, 48h, or 72h with various doses (1-100 microg/cm(2), corresponding to 3.8-380 microg/ml) of the carbon nanomaterials. In the comet assay, CNTs induced a dose-dependent increase in DNA damage at all treatment times, with a statistically significant effect starting at the lowest dose tested. GNFs increased DNA damage at all doses in the 24-h treatment, at two doses (40 and 100 microg/cm(2)) in the 48-h treatment (dose-dependent effect) and at four doses (lowest 10 microg/cm(2)) in the 72-h treatment. In the micronucleus assay, no increase in micronucleated cells was observed with either of the nanomaterials after the 24-h treatment or with CNTs after the 72-h treatment. The 48-h treatment caused a significant increase in micronucleated cells at three doses (lowest 10 microg/cm(2)) of CNTs and at two doses (5 and 10 microg/cm(2)) of GNFs. The 72-h treatment with GNFs increased micronucleated cells at four doses (lowest 10 microg/cm(2)). No dose-dependent effects were seen in the micronucleus assay. The presence of carbon nanomaterial on the microscopic slides disturbed the micronucleus analysis and made it impossible at levels higher than 20 microg/cm(2) of GNFs in the 24-h and 48-h treatments. In conclusion, our results suggest that both CNTs and GNFs are genotoxic in human bronchial epithelial BEAS 2B cells in vitro. This activity may be due to the fibrous nature of these carbon nanomaterials with a possible contribution by catalyst metals present in the materials-Co and Mo in CNTs (<5wt.%) and Fe (<3wt.%) in GNFs.

A Dense Poly(ethylene glycol) Coating Improves Penetration of Large Polymeric Nanoparticles within Brain Tissue

PubMed Central

Nance, Elizabeth A.; Woodworth, Graeme F.; Sailor, Kurt A.; Shih, Ting-Yu; Xu, Qingguo; Swaminathan, Ganesh; Xiang, Dennis; Eberhart, Charles; Hanes, Justin

2013-01-01

Prevailing opinion suggests that only substances up to 64 nm in diameter can move at appreciable rates through the brain extracellular space (ECS). This size range is large enough to allow diffusion of signaling molecules, nutrients, and metabolic waste products, but too small to allow efficient penetration of most particulate drug delivery systems and viruses carrying therapeutic genes, thereby limiting effectiveness of many potential therapies. We analyzed the movements of nanoparticles of various diameters and surface coatings within fresh human and rat brain tissue ex vivo and mouse brain in vivo. Nanoparticles as large as 114-nm in diameter diffused within the human and rat brain, but only if they were densely coated with poly(ethylene glycol) (PEG). Using these minimally adhesive PEG-coated particles, we estimated that human brain tissue ECS has some pores larger than 200 nm, and that more than one-quarter of all pores are ≥100 nm. These findings were confirmed in vivo in mice, where 40- and 100-nm, but not 200-nm, nanoparticles, spread rapidly within brain tissue, only if densely coated with PEG. Similar results were observed in rat brain tissue with paclitaxel-loaded biodegradable nanoparticles of similar size (85 nm) and surface properties. The ability to achieve brain penetration with larger nanoparticles is expected to allow more uniform, longer-lasting, and effective delivery of drugs within the brain, and may find use in the treatment of brain tumors, stroke, neuroinflammation, and other brain diseases where the blood-brain barrier is compromised or where local delivery strategies are feasible. PMID:22932224

Bulk synthesis of nanoporous palladium and platinum powders

DOEpatents

Robinson, David B [Fremont, CA; Fares, Stephen J [Pleasanton, CA; Tran, Kim L [Livermore, CA; Langham, Mary E [Pleasanton, CA

2012-04-17

Disclosed is a method for providing nanoporous palladium and platinum powders. These materials were synthesized on milligram to gram scales by chemical reduction of tetrahalo-complexes with ascorbate in a concentrated aqueous surfactant at temperatures between -20.degree. C. and 30.degree. C. The prepared particles have diameters of approximately 50 nm, wherein each particle is perforated by pores having diameters of approximately 3 nm, as determined by electron tomography. These materials are of potential value for hydrogen and electrical charge storage applications.

Wavelength Independent Optical Microscopy and Lithography

DTIC Science & Technology

1987-10-31

methods have been used in the past to fabricate the submicron apertures needed in near-field microscopy (2-4). However, under this contract we developed an...screens. Durig, et al. (4) in Zurich produced apertures at the tip of a single crystal of quartz etched using HF to make a fine point and covered...stage pulling process was used . Scanning electron li __ NO iI |06 j JlliM ° wm ..... 3 micrographs of a 100nm diameter pipette and a 500nm diameter

Bulk synthesis of nanoporous palladium and platinum powders

DOEpatents

Robinson, David B; Fares, Stephen J; Tran, Kim L; Langham, Mary E

2014-04-15

Disclosed is a method for providing nanoporous palladium and platinum powders. These materials were synthesized on milligram to gram scales by chemical reduction of tetrahalo-complexes with ascorbate in a concentrated aqueous surfactant at temperatures between -20.degree. C. and 30.degree. C. The prepared particles have diameters of approximately 50 nm, wherein each particle is perforated by pores having diameters of approximately 3 nm, as determined by electron tomography. These materials are of potential value for hydrogen and electrical charge storage applications.

Growth of High-Quality Carbon Nanotudes on Free-Standing Diamond Substrates (Postprint)

DTIC Science & Technology

2010-03-01

thickness and consisting of 20 nm diameter tubes were observed to grow in a thermal CVD system using C2H2 as precursor, Transmission electron microscopy...multi walled CNTs forming a mat of 5 lm thickness and consisting of 20 nm diameter tubes were observed to grow in a thermal CVD system using C2H2...desired devices. For example, chip cooling with CNT microfin architectures have been recently proposed by Kordas et al. [5]. CNT films as thermal

High Sensitivity Refractometer Based on Reflective Smf-Small Diameter No Core Fiber Structure.

PubMed

Zhou, Guorui; Wu, Qiang; Kumar, Rahul; Ng, Wai Pang; Liu, Hao; Niu, Longfei; Lalam, Nageswara; Yuan, Xiaodong; Semenova, Yuliya; Farrell, Gerald; Yuan, Jinhui; Yu, Chongxiu; Zeng, Jie; Tian, Gui Yun; Fu, Yong Qing

2017-06-16

A high sensitivity refractive index sensor based on a single mode-small diameter no core fiber structure is proposed. In this structure, a small diameter no core fiber (SDNCF) used as a sensor probe, was fusion spliced to the end face of a traditional single mode fiber (SMF) and the end face of the SDNCF was coated with a thin film of gold to provide reflective light. The influence of SDNCF diameter and length on the refractive index sensitivity of the sensor has been investigated by both simulations and experiments, where results show that the diameter of SDNCF has significant influence. However, SDNCF length has limited influence on the sensitivity. Experimental results show that a sensitivity of 327 nm/RIU (refractive index unit) has been achieved for refractive indices ranging from 1.33 to 1.38, which agrees well with the simulated results with a sensitivity of 349.5 nm/RIU at refractive indices ranging from 1.33 to 1.38.

Electrical transport properties of small diameter single-walled carbon nanotubes aligned on ST-cut quartz substrates

PubMed Central

2014-01-01

A method is introduced to isolate and measure the electrical transport properties of individual single-walled carbon nanotubes (SWNTs) aligned on an ST-cut quartz, from room temperature down to 2 K. The diameter and chirality of the measured SWNTs are accurately defined from Raman spectroscopy and atomic force microscopy (AFM). A significant up-shift in the G-band of the resonance Raman spectra of the SWNTs is observed, which increases with increasing SWNTs diameter, and indicates a strong interaction with the quartz substrate. A semiconducting SWNT, with diameter 0.84 nm, shows Tomonaga-Luttinger liquid and Coulomb blockade behaviors at low temperatures. Another semiconducting SWNT, with a thinner diameter of 0.68 nm, exhibits a transition from the semiconducting state to an insulating state at low temperatures. These results elucidate some of the electrical properties of SWNTs in this unique configuration and help pave the way towards prospective device applications. PMID:25170326

Angular dependence of the magnetic properties of permalloy and nickel nanowires as a function of their diameters

NASA Astrophysics Data System (ADS)

Raviolo, Sofía; Tejo, Felipe; Bajales, Noelia; Escrig, Juan

2018-01-01

In this paper we have compared the angular dependence of the magnetic properties of permalloy (Ni80Fe20) and nickel nanowires by means of micromagnetic simulations. For each material we have chosen two diameters, 40 and 100 nm. Permalloy nanowires with smaller diameters (d = 40 nm) exhibit greater coercivity than nickel nanowires, regardless of the angle at which the external magnetic field is applied. In addition, both Py and Ni nanowires exhibit the same remanence values. However, the nanowires of larger diameters (d = 100 nm) exhibit a more complex behavior, noting that for small angles, nickel nanowires are those that now exhibit a greater coercivity in comparison to those of permalloy. The magnetization reversal modes vary as a function of the angle at which the external field is applied. When the field is applied parallel to the wire axis, it reverts through nucleation and propagation of domain walls, whereas when the field is applied perpendicular to the axis, it reverts by a pseudo-coherent rotation. These results may provide a guide to control the magnetic properties of nanowires for use in potential applications.

Time-dependent preparation of gelatin-stabilized silver nanoparticles by pulsed Nd:YAG laser

NASA Astrophysics Data System (ADS)

Darroudi, Majid; Ahmad, M. B.; Zamiri, Reza; Abdullah, A. H.; Ibrahim, N. A.; Sadrolhosseini, A. R.

2011-03-01

Colloidal silver nanoparticles (Ag-NPs) were successfully prepared using a nanosecond pulsed Nd:YAG laser, λ = 1064 nm, with laser fluence of approximately about 360 mJ/pulse, in an aqueous gelatin solution. In this work, gelatin was used as a stabilizer, and the size and optical absorption properties of samples were studied as a function of the laser ablation times. The results from the UV-vis spectroscopy demonstrated that the mean diameter of Ag-NPs decrease as the laser ablation time increases. The Ag-NPs have mean diameters ranging from approximately 10 nm to 16 nm. Compared with other preparation methods, this work is clean, rapid, and simple to use.

ZnO/(Hf,Zr)O2/ZnO-trilayered nanowire capacitor structure fabricated solely by metalorganic chemical vapor deposition

NASA Astrophysics Data System (ADS)

Fujisawa, Hironori; Kuwamoto, Kei; Nakashima, Seiji; Shimizu, Masaru

2016-02-01

HfO2-based thin films are one of the key dielectric and ferroelectric materials in Si-CMOS LSIs as well as in oxide electronic nanodevices. In this study, we demonstrated the fabrication of a ZnO/(Hf,Zr)O2/ZnO-trilayered nanowire (NW) capacitor structure solely by metalorganic chemical vapor deposition (MOCVD). 15-nm-thick dielectric (Hf,Zr)O2 and 40-nm-thick top ZnO electrode layers were uniformly grown by MOCVD on a ZnO NW template with average diameter, length, and aspect ratio of 110 nm, 10 µm, and ˜90, respectively. The diameter and aspect ratio of the resultant trilayerd NWs are 200-300 nm and above 30, respectively. The crystalline phase of HfO2 and stacked the structure are also discussed.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Ganesh, Panchapakesan; Kent, Paul R; Mochalin, Vadym N

We simulate the experimentally observed graphitization of nanodiamonds into multi-shell onion-like carbon nanostructures, also called carbon onions, at different temperatures, using reactive force fields. The simulations include long-range Coulomb and van der Waals interactions. Our results suggest that long-range interactions play a crucial role in the phase-stability and the graphitization process. Graphitization is both enthalpically and entropically driven and can hence be controlled with temperature. The outer layers of the nanodiamond have a lower kinetic barrier toward graphitization irrespective of the size of the nanodiamond and graphitize within a few-hundred picoseconds, with a large volume increase. The inner core ofmore » the nanodiamonds displays a large size-dependent kinetic barrier, and graphitizes much more slowly with abrupt jumps in the internal energy. It eventually graphitizes by releasing pressure and expands once the outer shells have graphitized. The degree of transformation at a particular temperature is thereby determined by a delicate balance between the thermal energy, long-range interactions, and the entropic/enthalpic free energy gained by graphitization. Upon full graphitization, a multi-shell carbon nanostructure appears, with a shell-shell spacing of about {approx}3.4 {angstrom} for all sizes. The shells are highly defective with predominantly five- and seven-membered rings to curve space. Larger nanodiamonds with a diameter of 4 nm can graphitize into spiral structures with a large ({approx}29-atom carbon ring) pore opening on the outermost shell. Such a large one-way channel is most attractive for a controlled insertion of molecules/ions such as Li ions, water, or ionic liquids, for increased electrochemical capacitor or battery electrode applications.« less

Type IX secretion: the generation of bacterial cell surface coatings involved in virulence, gliding motility and the degradation of complex biopolymers.

PubMed

Veith, Paul D; Glew, Michelle D; Gorasia, Dhana G; Reynolds, Eric C

2017-10-01

The Type IX secretion system (T9SS) is present in over 1000 sequenced species/strains of the Fibrobacteres-Chlorobi-Bacteroidetes superphylum. Proteins secreted by the T9SS have an N-terminal signal peptide for translocation across the inner membrane via the SEC translocon and a C-terminal signal for secretion across the outer membrane via the T9SS. Nineteen protein components of the T9SS have been identified including three, SigP, PorX and PorY that are involved in regulation. The inner membrane proteins PorL and PorM and the outer membrane proteins PorK and PorN interact and a complex comprising PorK and PorN forms a large ring structure of 50 nm in diameter. PorU, PorV, PorQ and PorZ form an attachment complex on the cell surface of the oral pathogen, Porphyromonas gingivalis. P. gingivalis T9SS substrates bind to PorV suggesting that after translocation PorV functions as a shuttle protein to deliver T9SS substrates to the attachment complex. The PorU component of the attachment complex is a novel Gram negative sortase which catalyses the cleavage of the C-terminal signal and conjugation of the protein substrates to lipopolysaccharide, anchoring them to the cell surface. This review presents an overview of the T9SS focusing on the function of T9SS substrates and machinery components. © 2017 John Wiley & Sons Ltd.

49 CFR 195.207 - Transportation of pipe.

Code of Federal Regulations, 2010 CFR

2010-10-01

... stress of 20 percent or more of SMYS, an operator may not use pipe having an outer diameter to wall... barge. In a pipeline operated at a hoop stress of 20 percent or more of SMYS, an operator may not use...

49 CFR 195.207 - Transportation of pipe.

Code of Federal Regulations, 2012 CFR

2012-10-01

... stress of 20 percent or more of SMYS, an operator may not use pipe having an outer diameter to wall... barge. In a pipeline operated at a hoop stress of 20 percent or more of SMYS, an operator may not use...

49 CFR 195.207 - Transportation of pipe.

Code of Federal Regulations, 2011 CFR

2011-10-01

... stress of 20 percent or more of SMYS, an operator may not use pipe having an outer diameter to wall... barge. In a pipeline operated at a hoop stress of 20 percent or more of SMYS, an operator may not use...

Method of making tapered capillary tips with constant inner diameters

DOEpatents

Kelly, Ryan T [West Richland, WA; Page, Jason S [Kennewick, WA; Tang, Keqi [Richland, WA; Smith, Richard D [Richland, WA

2009-02-17

Methods of forming electrospray ionization emitter tips are disclosed herein. In one embodiment, an end portion of a capillary tube can be immersed into an etchant, wherein the etchant forms a concave meniscus on the outer surface of the capillary. Variable etching rates in the meniscus can cause an external taper to form. While etching the outer surface of the capillary wall, a fluid can be flowed through the interior of the capillary tube. Etching continues until the immersed portion of the capillary tube is completely etched away.

Laser pulse stacking method

DOEpatents

Moses, Edward I.

1992-01-01

A laser pulse stacking method is disclosed. A problem with the prior art has been the generation of a series of laser beam pulses where the outer and inner regions of the beams are generated so as to form radially non-synchronous pulses. Such pulses thus have a non-uniform cross-sectional area with respect to the outer and inner edges of the pulses. The present invention provides a solution by combining the temporally non-uniform pulses in a stacking effect to thus provide a more uniform temporal synchronism over the beam diameter.

Laser pulse stacking method

DOEpatents

Moses, E.I.

1992-12-01

A laser pulse stacking method is disclosed. A problem with the prior art has been the generation of a series of laser beam pulses where the outer and inner regions of the beams are generated so as to form radially non-synchronous pulses. Such pulses thus have a non-uniform cross-sectional area with respect to the outer and inner edges of the pulses. The present invention provides a solution by combining the temporally non-uniform pulses in a stacking effect to thus provide a more uniform temporal synchronism over the beam diameter. 2 figs.

NMR-NOE and MD simulation study on phospholipid membranes: dependence on membrane diameter and multiple time scale dynamics.

PubMed

Shintani, Megumi; Yoshida, Ken; Sakuraba, Shun; Nakahara, Masaru; Matubayasi, Nobuyuki

2011-07-28

Motional correlation times between the hydrophilic and hydrophobic terminal groups in lipid membranes are studied over a wide range of curvatures using the solution-state (1)H NMR-nuclear Overhauser effect (NOE) and molecular dynamics (MD) simulation. To enable (1)H NMR-NOE measurements for large vesicles, the transient NOE method is combined with the spin-echo method, and is successfully applied to a micelle of 1-palmitoyl-lysophosphatidylcholine (PaLPC) with diameter of 5 nm and to vesicles of dipalmitoylphosphatidylcholine (DPPC) with diameters ranging from 30 to 800 nm. It is found that the NOE intensity increases with the diameter up to ∼100 nm, and the model membrane is considered planar on the molecular level beyond ∼100 nm. While the NOE between the hydrophilic terminal and hydrophobic terminal methyl groups is absent for the micelle, its intensity is comparable to that for the neighboring group for vesicles with larger diameters. The origin of NOE signals between distant sites is analyzed by MD simulations of PaLPC micelles and DPPC planar bilayers. The slow relaxation is shown to yield an observable NOE signal even for the hydrophilic and hydrophobic terminal sites. Since the information on distance and dynamics cannot be separated in the experimental NOE alone, the correlation time in large vesicles is determined by combining the experimental NOE intensity and MD-based distance distribution. For large vesicles, the correlation time is found to vary by 2 orders of magnitude over the proton sites. This study shows that NOE provides dynamic information on large vesicles when combined with MD, which provides structural information. © 2011 American Chemical Society

Hierarchically assembled Au microspheres and sea urchin-like architectures: formation mechanism and SERS study.

PubMed

Wang, Xiansong; Yang, Da-Peng; Huang, Peng; Li, Min; Li, Chao; Chen, Di; Cui, Daxiang

2012-12-21

The hierarchically assembled Au microspheres/sea urchin-like structures have been synthesized in aqueous solution at room temperature with and without proteins (bovine serum albumin, BSA) as mediators. The average diameter of an individual Au microsphere is 300-600 nm, which is composed of some compact nanoparticles with an average diameter of about 15 nm. Meanwhile, the sea urchin-like Au architecture exhibits an average diameter of 600-800 nm, which is made up of some nanopricks with an average length of 100-200 nm. These products are characterized by means of scanning electron microscopy (SEM), X-ray diffraction (XRD) and transmission electronic microscopy (TEM). It is found that the BSA and ascorbic acid (AA) have great effects on the morphology of the resulting products. Two different growth mechanisms are proposed. The study on surface enhanced Raman scattering (SERS) activities is also carried out between Au microspheres and Au sea urchin-like architectures. It is found that Au urchin-like architectures possess much higher SERS activity than the Au microspheres. Our work may shed light on the design and synthesis of hierarchically self-assembled 3D micro/nano-architectures for SERS, catalysis and biosensors.

Toward Reconciliation of STEM and SAXS Data from Ionomers by Investigating Gold Nanoparticles

NASA Astrophysics Data System (ADS)

Benetatos, Nicholas; Smith, Brian; Heiney, Paul; Winey, Karen

2005-03-01

We have recently pioneered the use of scanning transmission electron microscopy (STEM) for direct, model independent imaging of the nano-scale morphology of ionomers. To date, the sizes of ionic aggregates determined in STEM experiments are inconsistent with SAXS data interpreted by the Yarusso-Cooper model. To address this discrepancy we have investigated a pair of model nanoparticles (11 and 55 atom Au clusters) with both STEM and SAXS. Using this model system we have improved our method of measuring nanometer scale objects and evaluated the importance of STEM probe size and specimen thickness. While the size of the STEM probe was inconsequential, specimen thicker than 50 nm showed significant depreciation of image quality, which limits our ability to accurately measure particle size. SAXS was performed on dilute suspensions of nanoparticles and fit using a monodisperse, hard-sphere form factor model. For Au11, STEM finds a diameter of 1.3 nm + .14 and SAXS finds a diameter of 1.4 nm. Similarly, both STEM and SAXS determine a diameter of 1.7 nm for Au55. Analysis of these model systems have allowed us to evaluate several factors of potential importance in reconciling STEM and SAXS data from ionomers.

Development of magnetic separation system of magnetoliposomes

NASA Astrophysics Data System (ADS)

Nakao, R.; Matuo, Y.; Mishima, F.; Taguchi, T.; Maenosono, S.; Nishijima, S.

2009-10-01

The magnetic separation technology using sub-microsized ferromagnetic particle is indispensable in many areas of medical biosciences. For example, ferromagnetic particles (200-500 nm) are widely used for cell sorting in stem cell research with the use of cell surface-specific antigens. Nanosized ferromagnetic particles (10-20 nm) have been suggested as more suitable in drug delivery studies given their efficiency of tissue penetration, however, the magnetic separation method for them has not been established. One of the major reasons is that magnetic force acting on the object particles decreases drastically as a particle diameter becomes small. In this study, magnetic force acting on the targets was enhanced by the combination of superconducting magnet and the filter consisting of ferromagnetic particle. By doing so, we confirmed that Fe 3O 4 of 20 nm in diameter was trapped in the magnetic filter under an external magnetic field of 0.5 T. Fe 3O 4 encapsulated with phospholipid liposomes of 200 nm in diameter was also shown to be trapped as external magnetic field of 1.5 T, but not of 0.5 T. We also showed the result of particle trajectory calculation which emulated well the experimental data.

Physicochemical properties of aerosol released in the case of a fire involving materials used in the nuclear industry.

PubMed

Ouf, F-X; Mocho, V-M; Pontreau, S; Wang, Z; Ferry, D; Yon, J

2015-01-01

For industrial concerns, and more especially for nuclear applications, the characterization of soot is essential for predicting the behaviour of containment barriers in fire conditions. This study deals with the characterization (emission factor, composition, size, morphology, microstructure) of particles produced during thermal degradation of materials found in nuclear facilities (electrical cables, polymers, oil and solvents). Small-scale experiments have been conducted for oxygen concentrations [O2] ranging from 15% to 21% in order to imitate the oxygen depletion encountered during a confined fire. Particles denote distinct shapes, from aggregates composed of monomers with diameters ranging from 31.2 nm to 52.8 nm, to compact nanoparticles with diameters ranging from 15 nm to 400 nm, and their composition strongly depends on fuel type. Despite the organic to total carbon ratio (OC/TC), their properties are poorly influenced by the decrease in [O2]. Finally, two empirical correlations are proposed for predicting the OC/TC ratio and the monomer diameter, respectively, as a function of the fuel's carbon to hydrogen ratio and the emission factor. Copyright © 2014 Elsevier B.V. All rights reserved.

Mechanical properties and mechanism of single crystal Cu pillar by in situ TEM compression and molecular dynamics simulation

NASA Astrophysics Data System (ADS)

Lin, Kai-Peng; Fang, Te-Hua; Lin, Ying-Jhin

2018-02-01

In this study, we investigate the mechanical properties of single-crystal copper (Cu) nanopillars. Critical deformation variations of Cu-nanopillared structures are estimated using in situ transmission electron microscopy compression tests and molecular dynamics simulations. The Young’s moduli of Cu nanopillars with diameters of 2-6 nm were 90.20-124.47 GPa. The contact stiffnesses of the Cu nanopillars with diameters of 400 and 500 nm were 1.33 and 3.86 N m-1, respectively; the Poisson’s ratios for these nanopillars were 0.32 and 0.33. The yield strength of the nanopillars varied from 0.25 GPa at 500 nm to 0.42 GPa at 400 nm; the yield strength of single-crystal Cu nanopillars decreased with increasing diameter. The values of the indented hardness of the Cu block were 0.27 and 1.06 GPa, respectively. Through experimental work and molecular dynamics simulations, we demonstrate that Cu nanopillars exhibit internal stress transmission during compression. When compression reaches the maximum strain, it can be observed that Cu slips. Our results are useful for understanding the mechanical properties, contact, and local deformation of Cu nanopillars.

Fabrication of Meso-Porous Sintered Metal Thin Films by Selective Etching of Silica Based Sacrificial Template

PubMed Central

Dumée, Ludovic F.; She, Fenghua; Duke, Mikel; Gray, Stephen; Hodgson, Peter; Kong, Lingxue

2014-01-01

Meso-porous metal materials have enhanced surface energies offering unique surface properties with potential applications in chemical catalysis, molecular sensing and selective separation. In this paper, commercial 20 nm diameter metal nano-particles, including silver and copper were blended with 7 nm silica nano-particles by shear mixing. The resulted powders were cold-sintered to form dense, hybrid thin films. The sacrificial silica template was then removed by selective etching in 12 wt% hydrofluoric acid solutions for 15 min to reveal a purely metallic meso-porous thin film material. The impact of the initial silica nano-particle diameter (7–20 nm) as well as the sintering pressure (5–20 ton·m−2) and etching conditions on the morphology and properties of the final nano-porous thin films were investigated by porometry, pyknometery, gas and liquid permeation and electron microscopy. Furthermore, the morphology of the pores and particle aggregation during shear mixing were assessed through cross-sectioning by focus ion beam milling. It is demonstrated that meso-pores ranging between 50 and 320 nm in average diameter and porosities up to 47% can be successfully formed for the range of materials tested. PMID:28344241

Simulating tissue oxygenation by encapsulating hemoglobin in polymer microcapsules (Conference Presentation)

NASA Astrophysics Data System (ADS)

Liu, Guangli; Wu, Qiang; Shen, Shuwei; Zhao, Gang; Dong, Erbao; Xu, Ronald X.

2017-03-01

We describe a combination of liquid-jet microencapsulation and molding techniques to fabricate tissue-simulating phantoms that mimick functional characteristics of tissue oxygen saturation (StO2). Chicken hemoglobin (Hb) was encapsulated inside a photocurable resin by a coaxial flow focusing process. The microdroplets were cured by ultraviolet (UV) illumination to form Hb loaded polymersome microdroplets. The microdroplets were further freeze-dried to form semipermeable solid microcapules with an outer transparent polymeric shell and an inner core of Hb. The diameter of the microcapsules ranged from 50 to100 μm. The absorption spectrum of the microcapsules was measured by a UV/VIS spectrophotometer over a wavelength range from 400 nm to 1100 nm. To fabricate the tissue-simulating phantom, the Hb loaded microcapsules were dispersed in transparent polydimethylsiloxane (PDMS). The optical properties of the phantom were determined by an vertical double integrating sphere with a reconstruction algorithm. The experimental results showed that the tissue-simulating phantom exhibited the spectral characteristics closely resembling that of oxy-hemoglobin. The phantom had a long-term optical stability when stored in 4 ℃, indicating that microencapsulation effectively protected Hb and improved its shelf time. With the Hb loaded microcapsules, we will produce skin-simulating phantoms for quantitative validation of multispectral imaging techniques. To the best of the authors' knowledge, no solid phantom is able to mimick living tissue oxygenation with good agreement. Therefore, our work provided an engineering platform for validating and calibrating spectral optical devices in biomedical applications.

Self-Assembly Fabrication of Coaxial Te@poly(3,4-ethylenedioxythiophene) Nanocables and Their Conversion to Pd@poly(3,4-ethylenedioxythiophene) Nanocables with a High Peroxidase-like Activity.

PubMed

Chi, Maoqiang; Nie, Guangdi; Jiang, Yanzhou; Yang, Zezhou; Zhang, Zhen; Wang, Ce; Lu, Xiaofeng

2016-01-13

Here, we report a simple one-step procedure to fabricate coaxial Te@poly(3,4-ethylenedioxythiophene) (PEDOT) nanocables via a self-assembly redox polymerization between 3,4-ethylenedioxythiophene monomer and the oxidant of sodium tellurite without the assistance of any templates and surfactants. The as-synthesized Te@PEDOT coaxial nanocables have diameters of center cores in the range of 5-10 nm, and the size of the outer shell from several nanometers to 15 nm. More interestingly, the as-prepared Te@PEDOT nanocables can be converted to Pd@PEDOT nanocables via a galvanic replacement reaction. The center core of the Pd nanowire exhibits a high crystallinity. The application of the synthesized Pd@PEDOT nanocables as peroxidase-like catalysts for the colorimetric detection of H2O2 is reported. The synergistic effect between the Pd nanowire and electrically conducting PEDOT enhances the catalytic activity toward the oxidation of the peroxidase substrate 3,3',5,5'-tetramethylbenzidine in the presence of H2O2. A detection limit toward H2O2 is as low as 4.83 μM, and a linear range from 10 to 100 μM has been achieved. This work offers a potential versatile route for the fabrication of cable-like nanocomposites with conducting polymers and other active components, which display great promise in applications such as catalysis, nanoelectronic devices, and energy storage and conversion.

Membrane current of retinal rods of Caudiverbera caudiverbera (Amphibia: Leptodactylidae): dark noise, spectral and absolute light sensitivity.

PubMed

Palma, F; Roncagliolo, P; Bacigalupo, J; Palacios, A G

2001-01-01

We investigated the photocurrents from isolated rods of the South American anuran, Caudiverbera caudiverbera. Rod outer segments were on average 66.4 +/- 11.2 microm (mean +/- S.D., n = 104) in length and 6.6 +/- 0.9 microm (mean +/- S.D.) in diameter: 40 +/- 22 photoisomerizations (mean +/- S.D., range 10-99, n = 16) were required for eliciting a half-saturating photocurrent response. The time-to-peak was 911 +/- 217 ms (mean +/- S.D., n = 14, 20 degrees C) in the linear range of the response and the integration time of the current response was 1744 +/- 451 ms (mean +/- S.D., n = 14). The time-to-peak appears to be slower and the integration time shorter in Caudiverbera than in Ambystoma tigrinum, Rana pipiens or Xenopus laevis rods under similar experimental conditions. The a-band of rod spectral sensitivity has a lambda(max) at 520 +/- 2.1 nm (mean +/- S.D., range 516-525 nm, n = 24) and the bandwidth fits a porphyropsin visual pigment. The single-event response amplitude ranges from 0.31-0.51 pA, depending on the calculation method. The intrinsic dark current (variance at dark minus variance under bright light) was 0.045 +/- 0.040 pA2 (mean +/- S.D., n = 24). Our results support the presence of a dark-noise component below 1 Hz, with kinetics similar to the single-photon evoked response and a rate of 0.006 events s(-1) (n = 9).

Electronic transport behavior of diameter-graded Ag nanowires

NASA Astrophysics Data System (ADS)

Wang, Xue Wei; Yuan, Zhi Hao

2010-05-01

Ag nanowires with a graded diameter in anodic aluminum oxide (AAO) membranes were fabricated by the direct-current electrodeposition. The Ag nanowires have a graded-change in diameter from 8 to 32 nm, which is matched with the graded-change of the AAO pore diameter. Electronic transport measurements show that there is a transport behavior similar to that of a metal-semiconductor junction along the axial direction in the diameter-graded Ag nanowires. Such a novel homogeneous nanojunction will be of great fundamental and practical significance.

Vortex formation in magnetic narrow rings

NASA Astrophysics Data System (ADS)

Bland, J. A. C.

2002-03-01

Underlying the current interest in magnetic elements is the possibility such systems provide both for the study of fundamental phenomena in magnetism (such as domain wall trapping and spin switching) and for technological applications, such as high density magnetic storage or magnetic random access memories (MRAM). One key issue is to control the magnetic switching precisely. To achieve this one needs first to have a well defined and reproducible remanent state, and second the switching process itself must be simple and reproducible. Among the many studied geometries, rings are shown to exhibit several advantages over other geometries, in that they show relatively simple stable magnetic states at remanence, with fast and simple magnetisation switching mechanisms. This is borne out of our systematic investigation of the magnetic properties of epitaxial and polycrystalline Co rings, where both the static, dynamic and transport properties have been studied. Magnetic measurements and micromagnetic simulations show that for appropriate ring structures a two step switching process occurs at high fields, indicating the existence of two different stable states. In addition to the vortex state, which occurs at intermediate fields, we have identified a new bi-domain state, which we term the `onion state', corresponding to opposite circulation of the magnetisation in each half of the ring. The magnetic elements were fabricated using a new technique based on the pre-patterning of Si ring structures and subsequent epitaxial growth of Cu/Co/Cu sandwich films on top of the Si elements. This technique has allowed the growth of epitaxial fcc Co(001) structures and in contrast to conventional lithographic methods, no damage to the magnetic layer structure is introduced by the patterning process [1,2]. We have studied the magnetic switching properties of arrays of narrow Co(100) epitaxial ring magnets, with outer diameters between 1 μm and 2 μm, varying inner diameters and varying film thickness, using magneto-optic Kerr effect (MOKE) magnetometry. The data indicates that the outer diameter of the ring only plays a minor role in determining the value of the switching field. As a general trend, the switching field decreases with increasing ring width and with decreasing film thickness. In particular, the dependence of the switching field on ring width becomes more pronounced for smaller ring widths. This stems from the fact that the vortex state becomes more stable for the narrower rings due to the exchange energy contribution to the barrier for reversal to the onion state. Thicker films also favour the vortex state over the onion state, since the magnetostatic energy associated with the latter state increases with film thickness [3]. Using micromagnetic simulations we show also that the magnetisation reversal in narrow rings can take place via a nucleation-free domain wall motion process when a field pulse is applied in the plane of the film and perpendicular to the net magnetisation. Switching times of the order of 400 ps can be achieved with this approach. A lower bound for the depinning time of the domain walls and a weak dependence of the domain wall velocity with the applied field are described [4]. The magnetic nanostructure of epitaxial fcc Co/Cu(001) circular elements has been imaged with scanning electron microscopy with polarisation analysis (SEMPA) [5]. The elements vary from disks to rings according to the dimensions of the inner diameter of the ring structure and have a nominal composition 4 nm Au/2 nm Cu/34 nm Co/100 nm Cu. In this study the outer diameter was fixed at 1.7 μm while the smallest ring width varies in the range 0.3-0.5 μm. A closed flux quadrant configuration is observed for some of the disks, characteristic of systems with cubic anisotropy (i.e., near vortex structure), besides other more complex configurations at remanence. The width of the 90^o domain wall in the disks is around 0.20 ± 0.05 μm. This value is larger than what expected for continuous films and is a result of the constraints imposed by the geometry of the element. The value is in good agreement with micromagnetic calculations. For the rings we observe directly the `onion-state', the closest configuration to saturation that these structures allow [1]. The results prove that this state is stable in zero applied field. The internal structure of the two head-to-head domain walls in the onion state is analysed. Wider rings (ring width w=0.5 μm) present vortex walls, whereas thinner ones (ring width w=0.3 μm) exhibit transverse walls [6]. This is in good agreement with micromagnetic simulations. We have also investigated the magnetic states and the switching properties of magnetic rings using magneto-resistance (MR) measurements. We chose narrow rings, where particularly simple magnetic states are expected. Some of the rings have notches of different sizes that help to pin, and thereby define, the positions of domain walls. The rings were fabricated using a multi-stage lift-off process, where six non-magnetic contacts in different positions of the ring were made. The rings consist of polycrystalline Co or Ni_80Fe_20 3-30 nm thick capped with 6 nm Au, with outer ring diameter 1.4 μm, ring width 80 nm, and notches of different sizes. Conventional MR-H loop measurements with a fixed magnetic field direction, and measurements with rotating constant field magnitude were performed. In one example of the first type of MR measurements, the direction of the field and the contacts were chosen so that at saturation the magnetization is perpendicular to the current. As expected, at saturation the resistance is low whereas at remanence it is high. There is a clear two-step switching process between the `onion' state and the vortex state as expected from previous studies on rings [1]. During the first switching the resistance increases, corresponding to the transition into the vortex state. Since no domain wall is present between the contacts, the magnetization is everywhere parallel to the current, and the resistance is high. After the second switching into the reverse `onion' state a domain wall is now present between the contacts. This means some of the magnetization in the transverse domain wall is perpendicular to the current and hence the resistance decreases. This shows that one can clearly distinguish between the onion and vortex state using MR measurements. In addition, using the field dependent voltage drop between different contacts, the switching field at which each part of the ring reverses can be determined. >From the second type of measurements clear hysteretic behaviour is seen, indicating that there is some domain wall pinning. This demonstrates that the position of the domain walls can be identified by looking at the voltage drop between different contacts. By measuring at different magnitudes of the applied field the pinning strength of the domain walls is determined, and in particular the dependence of the domain wall pinning on the notch size. Furthermore the structure of the domain wall changes for different notch sizes, and hence the contribution of the wall to the resistance changes as well. Real-time measurements between different contacts might allow for domain wall speed measurements and other domain wall propagation studies. References: [1] J. Rothman, M. Kläui, L. Lopez-Diaz, C.A.F. Vaz, A. Bleloch, J.A.C. Bland, Z. Cui, R. Speaks, Phys. Rev. Lett. 86 (2001) 1098. [2] Z. Cui, J. Rothman, M. Kläui, L. Lopez-Diaz, C.A.F. Vaz, J.A.C. Bland, to be published. [3] M. Kläui, L. Lopez-Diaz, J. Rothman, C.A.F. Vaz, J.A.C. Bland, Z. Cui, J. Magn. Magn. Mat., to be published. [4] L. Lopez-Diaz, J. Rothman, M. Kläui, J.A.C. Bland, IEEE Trans. Mag. 36 (2000) 3155. [5] C.A.F. Vaz, L. Lopez-Diaz, M. Kläui, J.A.C. Bland, T.L. Monchesky, J. Unguris, Z. Cui, 46th MMM Conference, Seattle, 2001. [6] R. D. McMichael and M. J. Donahue, IEEE Trans. Mag. 33, 4167-4169 (1997).

Annular recuperator design

DOEpatents

Kang, Yungmo

2005-10-04

An annular heat recuperator is formed with alternating hot and cold cells to separate counter-flowing hot and cold fluid streams. Each cold cell has a fluid inlet formed in the inner diameter of the recuperator near one axial end, and a fluid outlet formed in the outer diameter of the recuperator near the other axial end to evenly distribute fluid mass flow throughout the cell. Cold cells may be joined with the outlet of one cell fluidly connected to the inlet of an adjacent downstream cell to form multi-stage cells.

Spatially Controlled Fabrication of Brightly Fluorescent Nanodiamond-Array with Enhanced Far-Red Si-V Luminescence

PubMed Central

Singh, Sonal; Thomas, Vinoy; Martyshkin, Dmitry; Kozlovskaya, Veronika; Kharlampieva, Eugenia

2014-01-01

We demonstrate a novel approach to precise pattern fluorescent nanodiamond-arrays with enhanced far-red intense photostable luminescence from silicon-vacancy (Si-V) defect centers. The precision-patterned pre-growth seeding of nanodiamonds is achieved by scanning probe “Dip-Pen” nanolithography technique using electrostatically-driven transfer of nanodiamonds from “inked” cantilevers to a UV-treated hydrophilic SiO2 substrate. The enhanced emission from nanodiamond-dots in the far-red is achieved by incorporating Si-V defect centers in subsequent chemical vapor deposition treatment. The development of a suitable nanodiamond ink, mechanism of ink transport, and effect of humidity, dwell time on nanodiamond patterning are investigated. The precision-patterning of as-printed (pre-CVD) arrays with dot diameter and dot height as small as 735 nm ± 27 nm, 61 nm ± 3 nm, respectively and CVD-treated fluorescent ND-arrays with consistently patterned dots having diameter and height as small as 820 nm ± 20 nm, 245 nm ± 23 nm, respectively using 1 s dwell time and 30% RH is successfully achieved. We anticipate that the far-red intense photostable luminescence (~738 nm) observed from Si-V defect centers integrated in spatially arranged nanodiamonds could be beneficial for the development of the next generation fluorescent based devices and applications. PMID:24394286

Cryo-transmission electron tomography of native casein micelles from bovine milk

PubMed Central

Trejo, R.; Dokland, T.; Jurat-Fuentes, J.; Harte, F.

2013-01-01

Caseins are the principal protein components in milk and an important ingredient in the food industry. In liquid milk, caseins are found as micelles of casein proteins and colloidal calcium nanoclusters. Casein micelles were isolated from raw skim milk by size exclusion chromatography and suspended in milk protein-free serum produced by ultrafiltration (molecular weight cut-off of 3 kDa) of raw skim milk. The micelles were imaged by cryo-electron microscopy and subjected to tomographic reconstruction methods to visualize the 3-dimensional and internal organization of native casein micelles. This provided new insights into the internal architecture of the casein micelle that had not been apparent from prior cryo-transmission electron microscopy studies. This analysis demonstrated the presence of water-filled cavities (~20 to 30 nm in diameter), channels (diameter greater than ~5 nm), and several hundred high-density nanoclusters (6 to 12 nm in diameter) within the interior of the micelles. No spherical protein submicellar structures were observed. PMID:22118067

Laser-treated electrospun fibers loaded with nano-hydroxyapatite for bone tissue engineering.

PubMed

Aragon, Javier; Navascues, Nuria; Mendoza, Gracia; Irusta, Silvia

2017-06-15

Core-shell polycaprolactone/polycaprolactone (PCL/PCL) and polycaprolactone/polyvinyl acetate (PCL/PVAc) electrospun fibers loaded with synthesized nanohydroxyapatite (HAn) were lased treated to create microporosity. The prepared materials were characterized by XRD, FTIR, TEM and SEM. Uniform and randomly oriented beadless fibrous structures were obtained in all cases. Fibers diameters were in the 150-300nm range. Needle-like HAn nanoparticles with mean diameters of 20nm and length of approximately 150nm were mostly encase inside the fibers. Laser treated materials present micropores with diameters in the range 70-120μm for PCL-HAn/PCL fibers and in the 50-90μm range for PCL-HAn/PVAC material. Only samples containing HAn presented bioactivity after incubation during 30days in simulated body fluid. All scaffolds presented high viability, very low mortality, and human osteoblast proliferation. Biocompatibility was increased by laser treatment due to the surface and porosity modification. Copyright © 2017 Elsevier B.V. All rights reserved.

Absorption spectra of localized surface plasmon resonance observed in an inline/picoliter spectrometer cell fabricated by a near ultraviolet femtosecond laser

NASA Astrophysics Data System (ADS)

Shiraishi, Masahiko; Nishiyama, Michiko; Watanabe, Kazuhiro; Kubodera, Shoichi

2018-03-01

Absorption spectra based on localized surface plasmon resonance (LSPR) were obtained with an inline/picoliter spectrometer cell. The spectrometer cell was fabricated into an optical glass fiber by focusing a near UV (NUV) femtosecond laser pulses at a wavelength of 400 nm with an energy of 30 μJ. The laser beam was focused from two directions opposite to each other to fabricate a through-hole spectrometer cell. A diameter of the cell was approximately 3 μm, and the length was approximately 62.5 μm, which was nearly equal to the core diameter of the optical fiber. Liquid solution of gold nanoparticles (GNPs) with a diameter of 5-10 nm was injected into the spectrometer cell with its volume of 0.4 pL. The absorption peak centered at 518 nm was observed. An increase of absorption associated with the increase of the number of nanoparticles was in agreement with the numerical calculation based on the Lambert-Beer law.

Dimensional analysis of human saphenous vein grafts: Implications for external mesh support.

PubMed

Human, Paul; Franz, Thomas; Scherman, Jacques; Moodley, Lovendran; Zilla, Peter

2009-05-01

Constrictive external mesh support of vein grafts was shown to mitigate intimal hyperplasia in animal experiments. To determine the degree of constriction required for the elimination of dimensional irregularities in clinically used vein grafts, a detailed anatomic study of human saphenous veins was conducted. In 200 consecutive patients having coronary artery bypass grafting, harvested saphenous veins (length 34.4 +/- 10.8 cm) were analyzed regarding diameter irregularities, side branch distribution, and microstructure. The mean outer diameter of surgically distended saphenous veins was 4.2 +/- 0.6 mm (men, 4.3 +/- 0.6 mm vs women, 3.9 +/- 0.5 mm; P < .0001). Although the outer diameter significantly decreased over the initial 18 cm (-7.6%; P < .0001), the overall increase between malleolus and thigh was not significant (+11.2%). Smaller-diameter veins (<3.5 mm) had more pronounced diameter fluctuations than larger veins (31.8% +/- 11.0% vs 21.2% +/- 8.8%; P < .0001), with more than 71% of all veins showing caliber changes of more than 20%. There was 1 side branch every 5.4 +/- 4.3 cm, with a significantly higher incidence between 20 and 32 cm from the malleolus (P < .0001 to distal, P < .0004 to proximal). Generally, women had more side branches than men (0.30 +/- 0.15 cm(-1) vs 0.25 +/- 0.12 cm(-1); P = .0190). Thick-walled veins (565.7 +/- 138.4 mum) had a significantly higher number of large side branches (P < .0001), and thin-walled veins (398.7 +/- 123.2 mum) had significantly more small side branches (P < .0001). Pronounced intimal thickening ("cushions") was found in 28% of vessels (119.8 +/- 28.0 mum vs 40.1 +/- 18.2 mum; P < .0001). Although the preferential location of side branches may be addressed by the deliberate discarding of infragenicular vein segments, a diameter constriction of 27% on average would eliminate diameter irregularities in 98% of vein grafts.

Simulation of Young’s moduli for hexagonal ZnO [0 0 0 1]-oriented nanowires: first principles and molecular mechanical calculations

NASA Astrophysics Data System (ADS)

Bandura, Andrei V.; Evarestov, Robert A.; Lukyanov, Sergey I.; Piskunov, Sergei; Zhukovskii, Yuri F.

2017-08-01

Morphologically reproducible wurtzite-structured zinc oxide nanowires (ZnO NWs) can be synthesized by different methods. Since ZnO NWs have been found to possess piezoelectricity, a comprehensive study of their mechanical properties, e.g. deformations caused by external compression or stretching, is one of the actual tasks of this paper. We have calculated wurtzite-structured [0 0 0 1]-oriented ZnO NWs whose diameters have been varied within 1-5 nm and 1-20 nm ranges when using either ab initio (hybrid DFT-LCAO) or force-field (molecular mechanical) methods, respectively (the minimum diameter d NW of experimentally synthesized NWs has been estimated on average to be ~20 nm). When using both chosen calculation approaches, the values of Young’s moduli determined for the mentioned ranges of NW diameters have been found to be qualitatively compatible (168-169 GPa for 5 nm NW thickness), whereas results of molecular mechanical simulations on Y NW for 20 nm-thick NWs (160-162 GPa) have been qualitatively comparable with those experimentally measured along the [0 0 0 1] direction of NW loading. In all the cases, a gradual increase of the NW diameter has resulted in an asymptotic decrease of Young’s modulus consequently approaching that (Y b) of wurtzite-structured ZnO bulk along its [0 0 0 1] axis. The novelty of this study is that we combine the computation methods of quantum chemistry and molecular mechanics, while the majority of previous studies with the same aim have focused on the application of different classical molecular dynamical methods.

Mechanochemical synthesis of fluorescent carbon dots from cellulose powders

NASA Astrophysics Data System (ADS)

Chae, Ari; Ram Choi, Bo; Choi, Yujin; Jo, Seongho; Kang, Eun Bi; Lee, Hyukjin; Park, Sung Young; In, Insik

2018-04-01

A novel mechanochemical method was firstly developed to synthesize carbon nanodots (CNDs) or carbon nano-onions (CNOs) through high-pressure homogenization of cellulose powders as naturally abundant resource depending on the treatment times. While CNDs (less than 5 nm in size) showed spherical and amorphous morphology, CNOs (10-50 nm in size) presented polyhedral shape, and onion-like outer lattice structure, graphene-like interlattice spacing of 0.36 nm. CNOs showed blue emissions, moderate dispersibility in aqueous media, and high cell viability, which enables efficient fluorescence imaging of cellular media.

Diameter-Sensitive Breakdown of Single-Walled Carbon Nanotubes upon KOH Activation.

PubMed

Ye, Jianglin; Wu, Shuilin; Ni, Kun; Tan, Ziqi; Xu, Jin; Tao, Zhuchen; Zhu, Yanwu

2017-07-19

While potassium hydroxide (KOH) activation has been used to create pores in carbon nanotubes (CNTs) for improved energy-storage performance, the KOH activation mechanism of CNTs has been rarely investigated. In this work, the reaction between single-walled CNTs (SWCNTs) and KOH is studied in situ by thermogravimetric analysis coupled to infrared (IR) spectroscopy and gas chromatography/mass spectrometry (MS). The IR and MS results clearly demonstrate the sequential evolution of CO, hydrocarbons, CO 2 , and H 2 O in the activation process. By using the radial breathing mode of Raman spectroscopy, a diameter-sensitive selectivity is observed in the reaction between SWCNTs and KOH, leading to a preferential distribution of SWCNTs with diameters larger than 1 nm after activation at 900 °C and a preferential removal of SWCNTs with diameters below 1 nm upon activation. © 2017 Wiley-VCH Verlag GmbH & Co. KGaA, Weinheim.

Effect of restricted geometry on the superconducting properties of low-melting metals (Review Article)

NASA Astrophysics Data System (ADS)

Kumzerov, Yu. A.; Naberezhnov, A. A.

2016-11-01

This is a review of results from studies of the effect of artificially restricted geometry (the size effect) on the superconducting properties of nanoparticles of low-melting metals (Hg, Pb, Sn, In). Restricted geometrical conditions are created by embedding molten metals under high pressure into nanoporous matrices of two types: channel structures based on chrysotile asbestos and porous alkali-borosilicate glasses. Chrysotile asbestos is a system of parallel nanotubes with channel diameters ranging from 2 to 20 nm and an aspect ratio (channel length to diameter) of up to 107. The glasses are a random dendritic three-dimensional system of interconnected channels with a technologically controllable mean diameter of 2-30 nm. Temperature dependences of the resistance and heat capacity in the region of the superconducting transition and the dependences of the critical temperature on the mean pore diameter are obtained. The critical magnetic fields are also determined.

Determination of critical diameters for intrinsic carrier diffusion-length of GaN nanorods with cryo-scanning near-field optical microscopy

PubMed Central

Chen, Y. T.; Karlsson, K. F.; Birch, J.; Holtz, P. O.

2016-01-01

Direct measurements of carrier diffusion in GaN nanorods with a designed InGaN/GaN layer-in-a-wire structure by scanning near-field optical microscopy (SNOM) were performed at liquid-helium temperatures of 10 K. Without an applied voltage, intrinsic diffusion lengths of photo-excited carriers were measured as the diameters of the nanorods differ from 50 to 800 nm. The critical diameter of nanorods for carrier diffusion is concluded as 170 nm with a statistical approach. Photoluminescence spectra were acquired for different positions of the SNOM tip on the nanorod, corresponding to the origins of the well-defined luminescence peaks, each being related to recombination-centers. The phenomenon originated from surface oxide by direct comparison of two nanorods with similar diameters in a single map has been observed and investigated. PMID:26876009

Effects of nanopillar array diameter and spacing on cancer cell capture and cell behaviors

NASA Astrophysics Data System (ADS)

Wang, Shunqiang; Wan, Yuan; Liu, Yaling

2014-10-01

While substrates with nanopillars (NPs) have emerged as promising platforms for isolation of circulating tumor cells (CTCs), the influence of diameter and spacing of NPs on CTC capture is still unclear. In this paper, CTC-capture yield and cell behaviors have been investigated by using antibody functionalized NPs of various diameters (120-1100 nm) and spacings (35-800 nm). The results show a linear relationship between the cell capture yield and effective contact area of NP substrates where a NP array of small diameter and reasonable spacing is preferred; however, spacing that is too small or too large adversely impairs the capture efficiency and specificity, respectively. In addition, the formation of pseudopodia between captured cells and the substrate is found to be dependent not only on cell adhesion status but also on elution strength and shear direction. These findings provide essential guidance in designing NP substrates for more efficient capture of CTCs and manipulation of cytomorphology in future.While substrates with nanopillars (NPs) have emerged as promising platforms for isolation of circulating tumor cells (CTCs), the influence of diameter and spacing of NPs on CTC capture is still unclear. In this paper, CTC-capture yield and cell behaviors have been investigated by using antibody functionalized NPs of various diameters (120-1100 nm) and spacings (35-800 nm). The results show a linear relationship between the cell capture yield and effective contact area of NP substrates where a NP array of small diameter and reasonable spacing is preferred; however, spacing that is too small or too large adversely impairs the capture efficiency and specificity, respectively. In addition, the formation of pseudopodia between captured cells and the substrate is found to be dependent not only on cell adhesion status but also on elution strength and shear direction. These findings provide essential guidance in designing NP substrates for more efficient capture of CTCs and manipulation of cytomorphology in future. Electronic supplementary information (ESI) available: Additional details about calculation of maximal displacement of an individual NP; additional study of substrate wettability through Cassie's Law; additional details about selection of incubation time and shaking speeds. See DOI: 10.1039/c4nr02854f

The Density of Mid-sized Kuiper Belt Objects from ALMA Thermal Observations

DOE Office of Scientific and Technical Information (OSTI.GOV)

Brown, Michael E.; Butler, Bryan J.

The densities of mid-sized Kuiper Belt objects (KBOs) are a key constraint in understanding the assembly of objects in the outer solar system. These objects are critical for understanding the currently unexplained transition from the smallest KBOs with densities lower than that of water, to the largest objects with significant rock content. Mapping this transition is made difficult by the uncertainties in the diameters of these objects, which maps into an even larger uncertainty in volume and thus density. The substantial collecting area of the Atacama Large Millimeter Array allows significantly more precise measurements of thermal emission from outer solarmore » system objects and could potentially greatly improve the density measurements. Here we use new thermal observations of four objects with satellites to explore the improvements possible with millimeter data. We find that effects due to effective emissivity at millimeter wavelengths make it difficult to use the millimeter data directly to find diameters and thus volumes for these bodies. In addition, we find that when including the effects of model uncertainty, the true uncertainties on the sizes of outer solar system objects measured with radiometry are likely larger than those previously published. Substantial improvement in object sizes will likely require precise occultation measurements.« less

Improved Quick-Release Pin Mechanism

NASA Technical Reports Server (NTRS)

Wright, Jay M.

2007-01-01

An improved quick-release pin mechanism supplants a prior such mechanism in which the pin bears a shear load to hold two objects together. The prior mechanism, of a ball-locking design, can fail when vibrations cause balls to fall out. The load-bearing pin is an outer tube with a handle at one end (hereafter denoted the near end). Within the outer tube is a spring-loaded inner tube that includes a handle at its near end and a pivoting tab at its far end. The pin is inserted through holes in the objects to be retained and the inner tube is pushed against an offset pivot inside the outer tube to make the tab rotate outward so that it protrudes past the outer diameter of the outer tube, and the spring load maintains this configuration so that the pin cannot be withdrawn through the holes. Pushing the handles together against the spring load moves the locking tab out far enough that the tab becomes free to rotate inward. Then releasing the inner-tube handle causes the tab to be pulled into a resting position inside the outer tube. The pin can then be pulled out through the holes.

Exposure of phototrophs to 548 days in low Earth orbit: microbial selection pressures in outer space and on early earth

PubMed Central

Cockell, Charles S; Rettberg, Petra; Rabbow, Elke; Olsson-Francis, Karen

2011-01-01

An epilithic microbial community was launched into low Earth orbit, and exposed to conditions in outer space for 548 days on the European Space Agency EXPOSE-E facility outside the International Space Station. The natural phototroph biofilm was augmented with akinetes of Anabaena cylindrica and vegetative cells of Nostoc commune and Chroococcidiopsis. In space-exposed dark controls, two algae (Chlorella and Rosenvingiella spp.), a cyanobacterium (Gloeocapsa sp.) and two bacteria associated with the natural community survived. Of the augmented organisms, cells of A. cylindrica and Chroococcidiopsis survived, but no cells of N. commune. Only cells of Chroococcidiopsis were cultured from samples exposed to the unattenuated extraterrestrial ultraviolet (UV) spectrum (>110 nm or 200 nm). Raman spectroscopy and bright-field microscopy showed that under these conditions the surface cells were bleached and their carotenoids were destroyed, although cell morphology was preserved. These experiments demonstrate that outer space can act as a selection pressure on the composition of microbial communities. The results obtained from samples exposed to >200 nm UV (simulating the putative worst-case UV exposure on the early Earth) demonstrate the potential for epilithic colonization of land masses during that time, but that UV radiation on anoxic planets can act as a strong selection pressure on surface-dwelling organisms. Finally, these experiments have yielded new phototrophic organisms of potential use in biomass and oxygen production in space exploration. PMID:21593797

Exposure of phototrophs to 548 days in low Earth orbit: microbial selection pressures in outer space and on early earth.

PubMed

Cockell, Charles S; Rettberg, Petra; Rabbow, Elke; Olsson-Francis, Karen

2011-10-01

An epilithic microbial community was launched into low Earth orbit, and exposed to conditions in outer space for 548 days on the European Space Agency EXPOSE-E facility outside the International Space Station. The natural phototroph biofilm was augmented with akinetes of Anabaena cylindrica and vegetative cells of Nostoc commune and Chroococcidiopsis. In space-exposed dark controls, two algae (Chlorella and Rosenvingiella spp.), a cyanobacterium (Gloeocapsa sp.) and two bacteria associated with the natural community survived. Of the augmented organisms, cells of A. cylindrica and Chroococcidiopsis survived, but no cells of N. commune. Only cells of Chroococcidiopsis were cultured from samples exposed to the unattenuated extraterrestrial ultraviolet (UV) spectrum (>110 nm or 200 nm). Raman spectroscopy and bright-field microscopy showed that under these conditions the surface cells were bleached and their carotenoids were destroyed, although cell morphology was preserved. These experiments demonstrate that outer space can act as a selection pressure on the composition of microbial communities. The results obtained from samples exposed to >200 nm UV (simulating the putative worst-case UV exposure on the early Earth) demonstrate the potential for epilithic colonization of land masses during that time, but that UV radiation on anoxic planets can act as a strong selection pressure on surface-dwelling organisms. Finally, these experiments have yielded new phototrophic organisms of potential use in biomass and oxygen production in space exploration.

Pore diameter effects on phase behavior of a gas condensate in graphitic one-and two-dimensional nanopores.

PubMed

Welch, William R W; Piri, Mohammad

2016-01-01

Molecular dynamics (MD) simulations were performed on a hydrocarbon mixture representing a typical gas condensate composed mostly of methane and other small molecules with small fractions of heavier hydrocarbons, representative of mixtures found in tight shale reservoirs. The fluid was examined both in bulk and confined to graphitic nano-scale slits and pores. Numerous widths and diameters of slits and pores respectively were examined under variable pressures at 300 K in order to find conditions in which the fluid at the center of the apertures would not be affected by capillary condensation due to the oil-wet walls. For the bulk fluid, retrograde phase behavior was verified by liquid volumes obtained from Voronoi tessellations. In cases of both one and two-dimensional confinement, for the smallest apertures, heavy molecules aggregated inside the pore space and compression of the gas outside the solid structure lead to decreases in density of the confined fluid. Normal density/pressure relationships were observed for slits having gaps of above 3 nm and pores having diameters above 6 nm. At 70 bar, the minimum gap width at which the fluid could pass through the center of slits without condensation effects was predicted to be 6 nm and the corresponding diameter in pores was predicted to be 8 nm. The models suggest that in nanoscale networks involving pores smaller than these limiting dimensions, capillary condensation should significantly impede transmission of natural gases with similar composition.

Optical and Nanoparticle Analysis of Normal and Cancer Cells by Light Transmission Spectroscopy

NASA Astrophysics Data System (ADS)

Deatsch, Alison; Sun, Nan; Johnson, Jeffery; Stack, Sharon; Szajko, John; Sander, Christopher; Rebuyon, Roland; Easton, Judah; Tanner, Carol; Ruggiero, Steven

2015-03-01

We have investigated the optical properties of human oral and ovarian cancer and normal cells. Specifically, we have measured the absolute optical extinction for intra-cellular material (lysates) in aqueous suspension. Measurements were conducted over a wavelength range of 250 to 1000 nm with 1 nm resolution using Light Transmission Spectroscopy (LTS). This provides both the absolute extinction of materials under study and, with Mie inversion, the absolute number of particles of a given diameter as a function of diameter in the range of 1 to 3000 nm. Our preliminary studies show significant differences in both the extinction and particle size distributions associated with cancer versus normal cells, which appear to be correlated with differences in the particle size distribution in the range of approximately 50 to 250 nm. Especially significant is a clearly higher density of particles at about 100 nm and smaller for normal cells. Department of Physics, Harper Cancer Research Institute, and the Office of Research at the University of Notre Dame.

Visualizing viral transport and host infection

NASA Astrophysics Data System (ADS)

Son, Kwangmin; Guasto, Jeffrey; Cubillos-Ruiz, Andres; Sullivan, Matthew; Stocker, Roman; MIT Team

2013-11-01

A virus is a non-motile infectious agent that can only replicate inside a living host. They consist of a <100 nm diameter capsid which houses their DNA, and a <20 nm diameter tail used to inject DNA to the host, which are classified into three different morphologies by the tail type: short tail (~ 10 nm, podovirus), rigid contractile tail (~ 100 nm, myovirus), or flexible noncontractile tail (~ 300 nm, siphovirus). Combining microfluidics with epifluorescent microscopy, we studied the simultaneous diffusive transport governing the initial encounter and ultimately the infection of a non-motile cyanobacteria host (~ 1 μm prochlorococcus) and their viral (phage) counterparts in real time. This methodology allows us to quantify the virus-host encounter/adsorption dynamics and subsequently the effectiveness of various tail morphologies for viral infection. Viral transport and the role of viral morphology in host-virus interactions are critical to our understanding of both ecosystem dynamics and human health, as well as to the evolution of virus morphology.

Simulation of a Dispersive Tsunami due to the 2016 El Salvador-Nicaragua Outer-Rise Earthquake (M w 6.9)

NASA Astrophysics Data System (ADS)

Tanioka, Yuichiro; Ramirez, Amilcar Geovanny Cabrera; Yamanaka, Yusuke

2018-01-01

The 2016 El Salvador-Nicaragua outer-rise earthquake (M w 6.9) generated a small tsunami observed at the ocean bottom pressure sensor, DART 32411, in the Pacific Ocean off Central America. The dispersive observed tsunami is well simulated using the linear Boussinesq equations. From the dispersive character of tsunami waveform, the fault length and width of the outer-rise event is estimated to be 30 and 15 km, respectively. The estimated seismic moment of 3.16 × 1019 Nm is the same as the estimation in the Global CMT catalog. The dispersive character of the tsunami in the deep ocean caused by the 2016 outer-rise El Salvador-Nicaragua earthquake could constrain the fault size and the slip amount or the seismic moment of the event.

Simulation of a Dispersive Tsunami due to the 2016 El Salvador-Nicaragua Outer-Rise Earthquake ( M w 6.9)

NASA Astrophysics Data System (ADS)

Tanioka, Yuichiro; Ramirez, Amilcar Geovanny Cabrera; Yamanaka, Yusuke

2018-04-01

The 2016 El Salvador-Nicaragua outer-rise earthquake ( M w 6.9) generated a small tsunami observed at the ocean bottom pressure sensor, DART 32411, in the Pacific Ocean off Central America. The dispersive observed tsunami is well simulated using the linear Boussinesq equations. From the dispersive character of tsunami waveform, the fault length and width of the outer-rise event is estimated to be 30 and 15 km, respectively. The estimated seismic moment of 3.16 × 1019 Nm is the same as the estimation in the Global CMT catalog. The dispersive character of the tsunami in the deep ocean caused by the 2016 outer-rise El Salvador-Nicaragua earthquake could constrain the fault size and the slip amount or the seismic moment of the event.

Physical vapor deposition of one-dimensional nanoparticle arrays on graphite: seeding the electrodeposition of gold nanowires.

PubMed

Cross, C E; Hemminger, J C; Penner, R M

2007-09-25

One-dimensional (1D) ensembles of 2-15 nm diameter gold nanoparticles were prepared using physical vapor deposition (PVD) on highly oriented pyrolytic graphite (HOPG) basal plane surfaces. These 1D Au nanoparticle ensembles (NPEs) were prepared by depositing gold (0.2-0.6 nm/s) at an equivalent thickness of 3-4 nm onto HOPG surfaces at 670-690 K. Under these conditions, vapor-deposited gold nucleated selectively at the linear step edge defects present on these HOPG surfaces with virtually no nucleation of gold particles on terraces. The number density of 2-15 nm diameter gold particles at step edges was 30-40 microm-1. These 1D NPEs were up to a millimeter in length and organized into parallel arrays on the HOPG surface, following the organization of step edges. Surprisingly, the deposition of more gold by PVD did not lead to the formation of continuous gold nanowires at step edges under the range of sample temperature or deposition flux we have investigated. Instead, these 1D Au NPEs were used as nucleation templates for the preparation by electrodeposition of gold nanowires. The electrodeposition of gold occurred selectively on PVD gold nanoparticles over the potential range from 700-640 mV vs SCE, and after optimization of the electrodeposition parameters continuous gold nanowires as small as 80-90 nm in diameter and several micrometers in length were obtained.

Pineal organs of deep-sea fish: photopigments and structure.

PubMed

Bowmaker, James K; Wagner, Hans-Joachim

2004-06-01

We have examined the morphology and photopigments of the pineal organs from a number of mesopelagic fish, including representatives of the hatchet fish (Sternoptychidae), scaly dragon-fish (Chauliodontidae) and bristlemouths (Gonostomidae). Although these fish were caught at depths of between 500 and 1000 m, the morphological organisation of their pineal organs is remarkably similar to that of surface-dwelling fish. Photoreceptor inner and outer segments protrude into the lumen of the pineal vesicle, and the outer segment is composed of a stack of up to 20 curved disks that form a cap-like cover over the inner segment. In all species, the pineal photopigment was spectrally distinct from the retinal rod pigment, with lambdamax displaced to longer wavelengths, between approximately 485 and 503 nm. We also investigated the pineal organ of the deep demersal eel, Synaphobranchus kaupi, caught at depths below 2000 m, which possesses a rod visual pigment with lambdamax at 478 nm, but the pineal pigment has lambdamax at approximately 515 nm. In one species of hatchet fish, Argyropelecus affinis, two spectral classes of pinealocyte were identified, both spectrally distinct from the retinal rod photopigment.

Variation of nanopore diameter along porous anodic alumina channels by multi-step anodization.

PubMed

Lee, Kwang Hong; Lim, Xin Yuan; Wai, Kah Wing; Romanato, Filippo; Wong, Chee Cheong

2011-02-01

In order to form tapered nanocapillaries, we investigated a method to vary the nanopore diameter along the porous anodic alumina (PAA) channels using multi-step anodization. By anodizing the aluminum in either single acid (H3PO4) or multi-acid (H2SO4, oxalic acid and H3PO4) with increasing or decreasing voltage, the diameter of the nanopore along the PAA channel can be varied systematically corresponding to the applied voltages. The pore size along the channel can be enlarged or shrunken in the range of 20 nm to 200 nm. Structural engineering of the template along the film growth direction can be achieved by deliberately designing a suitable voltage and electrolyte together with anodization time.

Second harmonic generation quantitative measurements on collagen fibrils through correlation to electron microscopy

NASA Astrophysics Data System (ADS)

Bancelin, S.; Aimé, C.; Gusachenko, I.; Kowalczuk, L.; Latour, G.; Coradin, T.; Schanne-Klein, M.-C.

2015-03-01

Type I collagen is a major structural protein in mammals that shows highly structured macromolecular organizations specific to each tissue. This biopolymer is synthesized as triple helices, which self-assemble into fibrils (Ø =10-300 nm) and further form various 3D organization. In recent years, Second Harmonic Generation (SHG) microscopy has emerged as a powerful technique to probe in situ the fibrillar collagenous network within tissues. However, this optical technique cannot resolve most of the fibrils and is a coherent process, which has impeded quantitative measurements of the fibril diameter so far. In this study, we correlated SHG microscopy with Transmission Electron Microscopy to determine the sensitivity of SHG microscopy and to calibrate SHG signals as a function of the fibril diameter in reconstructed collagen gels. To that end, we synthetized isolated fibrils with various diameters and successfully imaged the very same fibrils with both techniques, down to 30 nm diameter. We observed that SHG signals scaled as the fourth power of the fibril diameter, as expected from analytical and numerical calculations. This calibration was then applied to diabetic rat cornea in which we successfully recovered the diameter of hyperglycemia-induced fibrils in the Descemet's membrane without having to resolve them. Finally we derived the first hyperpolarizability from a single collagen triple helix which validates the bottom-up approach used to calculate the non-linear response at the fibrillar scale and denotes a parallel alignment of triple helices within the fibrils. These results represent a major step towards quantitative SHG imaging of nm-sized collagen fibrils.

The fluorescence properties of aerosol larger than 0.8 μm in an urban and a PBA-dominated location

NASA Astrophysics Data System (ADS)

Gabey, A. M.; Stanley, W. R.; Gallagher, M. W.; Kaye, P. H.

2011-01-01

Dual-wavelength Ultraviolet light-induced fluorescence (UV-LIF) measurements were performed on ambient environmental aerosol in Manchester, UK (urban city centre, winter) and Borneo, Malaysia (remote, tropical), which are taken to represent environments with negligible and significant primary biological aerosol (PBA) influences, respectively. Single-particle fluorescence intensity and optical equivalent diameter were measured with a Wide Issue Bioaerosol Sensor, version 3 (WIBS3) in the diameter range 0.8 μm≤DP≤20 μm for 2-3 weeks and filters were analysed using energy dispersive X-ray (EDX) spectroscopy, which revealed mostly non-PBA dominated particle sizes larger than 1 μm in Manchester. The WIBS3 features three fluorescence channels: Fluorescence excited at 280 nm is recorded at 310-400 nm and 400-600 nm and fluorescence excited at 370 nm is detected at 400-600 nm. In Manchester the primary size mode of fluorescent and non-fluorescent material was at 1.2 μm. In Borneo non-fluorescent material peaked at 1.2 μm and fluorescent at 3-4 μm. The fluorescence intensity at 400-600 nm generally increased with DP at both sites, as did the 310-400 nm intensity in Borneo. In Manchester the 310-400 m fluorescence decreased at DP>4 μm, suggesting this channel offers additional discrimination between fluorescent particle types. Finally, the ratio of fluorescence intensity in two pairs of channels was investigated as a function of particle diameter and this varied significantly between the two environments, demonstrating that the fluorescent aerosol in each can in principle be distinguished using a combination of fluorescence and elastic scattering measurements.

Flexural models of trench/outer rise topography of coronae on Venus with axisymmetric spherical shell elastic plates

NASA Technical Reports Server (NTRS)

Moore, W.; Schubert, Gerald; Sandwell, David T.

1992-01-01

Magellan altimetry has revealed that many coronae on Venus have trenches or moats around their peripheries and rises outboard of the trenches. This trench/outer rise topographic signature is generally associated with the tectonic annulus of the corona. Sandwell and Schubert have interpreted the trench/outer rise topography and the associated tectonic annulus around coronae to be the result of elastic bending of the Venus lithosphere (though the tectonic structures are consequences of inelastic deformation of the lithosphere). They used two-dimensional elastic plate flexure theory to fit topographic profiles across a number of large coronae and inferred elastic lithosphere thicknesses between about 15 and 40 km, similar to inferred values of elastic thickness for the Earth's lithosphere at subduction zones around the Pacific Ocean. Here, we report the results of using axisymmetric elastic flexure theory for the deformation of thin spherical shell plates to interpret the trench/outer rise topography of the large coronae modeled by Sandwell and Schubert and of coronae as small as 250 km in diameter. In the case of a corona only a few hundred kilometers in diameter, the model accounts for the small planform radius of the moat and the nonradial orientation of altimetric traces across the corona. By fitting the flexural topography of coronae we determine the elastic thickness and loading necessary to account for the observed flexure. We calculate the associated bending moment and determine whether the corona interior topographic load can provide the required moment. We also calculate surface stresses and compare the stress distribution with the location of annular tectonic features.

Mechanical behavior enhancement of ZnO nanowire by embedding different nanowires

NASA Astrophysics Data System (ADS)

Vazinishayan, Ali; Yang, Shuming; Lambada, Dasaradha Rao; Wang, Yiming

2018-06-01

In this work, we employed commercial finite element modeling (FEM) software package ABAQUS to analyze mechanical properties of ZnO nanowire before and after embedding with different kinds of nanowires, having different materials and cross-section models such as Au (circular), Ag (pentagonal) and Si (rectangular) using three point bending technique. The length and diameter of the ZnO nanowire were measured to be 12,280 nm and 103.2 nm, respectively. In addition, Au, Ag and Si nanowires were considered to have the length of 12,280 nm and the diameter of 27 nm. It was found that after embedding Si nanowire with rectangular cross-section into the ZnO nanowire, the distribution of Von Misses stresses criterion, displacement and strain were decreased than the other nanowires embedded. The highest stiffness, the elastic deformation and the high strength against brittle failure have been made by Si nanowire comparison to the Au and Ag nanowires, respectively.

Structural and magnetic properties of self-assembled cobalt on porous silicon; experimental and micromagnetic investigations

NASA Astrophysics Data System (ADS)

Saidani, M.; Belkacem, W.; Bessais, L.; Mliki, N.

2017-08-01

In this paper, we report on self-assembled Co nanoparticles deposited in and on porous silicon (PS) matrix by using UHV evaporation. Four samples were prepared by varying the Co deposited thickness (t = 3, 5, 7 and 10 nm). All samples have been investigated by means of Scanning Electron Microscopy (SEM), Transmission Electron Microscopy (TEM) and Physical Properties Measurement System (PPMS). The increase of t has induced an increase of the nanoparticle diameter from 3 nm to about 150 nm. Referring to the magnetic characterizations, this increase has been followed by a single to multi-domain transition. Therefore, this has been evidenced by a switching from superparamagnetism to purely ferromagnetism accompanied by a change in the magnetic reversal dynamics. Thus, by performing micromagnetic calculation, we have shown that a transition from the uniform rotation to vortex state occurs at a critical diameter of about 55 nm.

Dielectrophoretic trapping of nanoparticles with an electrokinetic nanoprobe.

PubMed

Wood, Nicholas R; Wolsiefer, Amanda I; Cohn, Robert W; Williams, Stuart J

2013-07-01

A high aspect ratio 3D electrokinetic nanoprobe is used to trap polystyrene particles (200 nm), gold nanoshells (120 nm), and gold nanoparticles (mean diameter 35 nm) at low voltages (<1 V(rms)). The nanoprobe is fabricated using room temperature self-assembly methods, without the need for nanoresolution lithography. The nanoprobe (150-500 nm in diameter, 2-150 μm in length) is mounted on the end of a glass micropipette, enabling user-specified positioning. The nanoprobe is one electrode within a point-and-plate configuration, with an indium-tin oxide cover slip serving as the planar electrode. The 3D structure of the nanoprobe enhances dielectrophoretic capture; further, electro-hydrodynamic flow enhances trapping, increasing the effective trapping region. Numerical simulations show low heating (1 K), even in biological media of moderate conductivity (1 S/m). © 2013 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Effect of porosity variation on the electrochemical behavior of vertically aligned multi-walled carbon nanotubes.

PubMed

Raut, Akshay S; Parker, Charles B; Stoner, Brian R; Glass, Jeffrey T

2012-06-01

Electrochemical charge storage characteristics of vertically aligned multi-walled carbon nanotubes (MWCNTs) as a function of varying diameter and spacing are reported. It was observed that the specific capacitance of the MWCNTs increased as both diameter and inter-tube spacing decreased. The MWCNT films with 229 nm inter-MWCNT spacing exhibited specific capacitance of 228 F/g versus 70 F/g for 506 nm spacing, when tested in a non-aqueous electrolyte. Further, a trend in specific capacitance versus pore size is proposed. Coupled with previously reported trends observed in the sub-10 nm pore size regime, this is expected to offer better understanding of electrochemical behavior of porous carbon materials over a wide range of pore sizes.

High Pressure Structure and Electrical Resistance Measurements on Cadmium Sulfide Nanoparticles

NASA Astrophysics Data System (ADS)

Montgomery, J. M.; Stemshorn, A. K.; Stanishevsky, A.; Vohra, Y. K.; Weir, S. T.

2010-03-01

Room-temperature four-probe electrical resistance and synchrotron x-ray diffraction measurements have been performed on dried and aqueous suspensions of CdS nanoparticles (25 nm in diameter) to 35 GPa. Nanoparticles used in these experiments were synthesized using the reaction between a cadmium salt and thiourea under hydrothermal conditions without using any surfactants. While the x-ray structure data confirms the irreversible wurtzite -> rocksalt transition seen at 2.5 GPa in bulk CdS, the corresponding resistance drop was not observed in the measured range, indicating that the nanoparticle boundaries may prevent electronic communication between particles. Further studies on dry and aqueous 10 nm nano-spheres and 9 nm diameter nano-rods are planned, and the results of these experiments will be presented.

Nanodiamonds do not provide unique evidence for a Younger Dryas impact

PubMed Central

Tian, H.; Schryvers, D.; Claeys, Ph.

2011-01-01

Microstructural, δ13C isotope and C/N ratio investigations were conducted on excavated material from the black Younger Dryas boundary in Lommel, Belgium, aiming for a characterisation of the carbon content and structures. Cubic diamond nanoparticles are found in large numbers. The larger ones with diameters around or above 10 nm often exhibit single or multiple twins. The smaller ones around 5 nm in diameter are mostly defect-free. Also larger flake-like particles, around 100 nm in lateral dimension, with a cubic diamond structure are observed as well as large carbon onion structures. The combination of these characteristics does not yield unique evidence for an exogenic impact related to the investigated layer. PMID:21173270

Magnetic properties of superparamagnetic nanoparticles loaded into silicon nanotubes.

PubMed

Granitzer, Petra; Rumpf, Klemens; Gonzalez, Roberto; Coffer, Jeffery; Reissner, Michael

2014-01-01

In this work, the magnetic properties of silicon nanotubes (SiNTs) filled with Fe3O4 nanoparticles (NPs) are investigated. SiNTs with different wall thicknesses of 10 and 70 nm and an inner diameter of approximately 50 nm are prepared and filled with superparamagnetic iron oxide nanoparticles of 4 and 10 nm in diameter. The infiltration process of the NPs into the tubes and dependence on the wall-thickness is described. Furthermore, data from magnetization measurements of the nanocomposite systems are analyzed in terms of iron oxide nanoparticle size dependence. Such biocompatible nanocomposites have potential merit in the field of magnetically guided drug delivery vehicles. 61.46.Fg; 62.23.Pq; 75.75.-c; 75.20.-g.

Synthesis of nanosized (<20 nm) polymer particles by radical polymerization in miniemulsion employing in situ surfactant formation.

PubMed

Guo, Yi; Zetterlund, Per B

2011-10-18

A novel method for synthesis of ultrafine polymeric nanoparticles of diameters less than 20 nm has been developed. The method is based on miniemulsion polymerization exploiting combination of the in situ surfactant generation approach (whereby the surfactant is formed at the oil-water interface by reaction between an organic acid and a base) and ultrasonication. Conventional radical polymerization and nitroxide-mediated radical polymerization of styrene have been conducted in miniemulsion using oleic acid/potassium hydroxide, demonstrating that particles with diameters less than 20 nm can be obtained by this approach at surfactant contents much lower than traditionally required in microemulsion polymerizations. Copyright © 2011 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Design of a new static micromixer having simple structure and excellent mixing performance.

PubMed

Kamio, Eiji; Ono, Tsutomu; Yoshizawa, Hidekazu

2009-06-21

A novel micromixer with simple construction and excellent mixing performance is developed. The micromixer is composed of two stainless steel tubes with different diameters: one is an outer tube and another is an inner tube which fits in the outer tube. In this micromixer, one reactant fluid flows in the mixing zone from the inner tube and the other flows from the outer tube. The excellent mixing performance is confirmed by comparing the results of a Villermaux/Dushman reaction with those for the other micromixers. The developed micromixer has a mixing cascade with multiple means and an asymmetric structure to achieve effective mixing. The excellent mixing performance of the developed micromixer suggests that serial addition of multiple phenomena for mixing will give us an efficient micromixing.

The DarkSide-50 outer detectors

NASA Astrophysics Data System (ADS)

Westerdale, S.; Agnes, P.; Agostino, L.; Albuquerque, I. F. M.; Alexander, T.; Alton, A. K.; Arisaka, K.; Back, H. O.; Baldin, B.; Biery, K.; Bonfini, G.; Bossa, M.; Bottino, B.; Brigatti, A.; Brodsky, J.; Budano, F.; Bussino, S.; Cadeddu, M.; Cadonati, L.; Cadoni, M.; Calaprice, F.; Canci, N.; Candela, A.; Cao, H.; Cariello, M.; Carlini, M.; Catalanotti, S.; Cavalcante, P.; Chepurnov, A.; Cocco, A. G.; Covone, G.; D'Angelo, D.; D'Incecco, M.; Davini, S.; De Cecco, S.; De Deo, M.; De Vincenzi, M.; Derbin, A.; Devoto, A.; Di Eusanio, F.; Di Pietro, G.; Edkins, E.; Empl, A.; Fan, A.; Fiorillo, G.; Fomenko, K.; Foster, G.; Franco, D.; Gabriele, F.; Galbiati, C.; Giganti, C.; Goretti, A. M.; Granato, F.; Grandi, L.; Gromov, M.; Guan, M.; Guardincerri, Y.; Hackett, B. R.; Herner, K. R.; Hungerford, E. V.; Aldo, Ianni; Andrea, Ianni; James, I.; Jollet, C.; Keeter, K.; Kendziora, C. L.; Kobychev, V.; Koh, G.; Korablev, D.; Korga, G.; Kubankin, A.; Li, X.; Lissia, M.; Lombardi, P.; Luitz, S.; Ma, Y.; Machulin, I. N.; Mandarano, A.; Mari, S. M.; Maricic, J.; Marini, L.; Martoff, C. J.; Meregaglia, A.; Meyers, P. D.; Miletic, T.; Milincic, R.; Montanari, D.; Monte, A.; Montuschi, M.; Monzani, M. E.; Mosteiro, P.; Mount, B. J.; Muratova, V. N.; Musico, P.; Napolitano, J.; Orsini, M.; Ortica, F.; Pagani, L.; Pallavicini, M.; Pantic, E.; Parmeggiano, S.; Pelczar, K.; Pelliccia, N.; Perasso, S.; Pocar, A.; Pordes, S.; Pugachev, D. A.; Qian, H.; Randle, K.; Ranucci, G.; Razeto, A.; Reinhold, B.; Renshaw, A. L.; Romani, A.; Rossi, B.; Rossi, N.; Rountree, S. D.; Sablone, D.; Saggese, P.; Saldanha, R.; Sands, W.; Sangiorgio, S.; Savarese, C.; Segreto, E.; Semenov, D. A.; Shields, E.; Singh, P. N.; DSkorokhvatov, M.; Smirnov, O.; Sotnikov, A.; Stanford, C.; Suvorov, Y.; Tartaglia, R.; Tatarowicz, J.; Testera, G.; Tonazzo, A.; Trinchese, P.; Unzhakov, E. V.; Vishneva, A.; Vogelaar, B.; Wada, M.; Walker, S.; Wang, H.; Wang, Y.; Watson, A. W.; Wilhelmi, J.; Wojcik, M. M.; Xiang, X.; Xu, J.; Yang, C.; Yoo, J.; Zavatarelli, S.; Zec, A.; Zhong, W.; Zhu, C.; Zuzel, G.; DarkSide Collaboration

2016-05-01

DarkSide-50 is a dark matter detection experiment searching for Weakly Interacting Massive Particles (WIMPs), in Gran Sasso National Laboratory. For experiments like DarkSide-50, neutrons are one of the primary backgrounds that can mimic WIMP signals. The experiment consists of three nested detectors: a liquid argon time projection chamber surrounded by two outer detectors. The outermost detector is a 10 m by 11 m cylindrical water Cherenkov detector with 80 PMTs, designed to provide shielding and muon vetoing. Inside the water Cherenkov detector is the 4 m diameter spherical boron-loaded liquid scintillator veto, with a cocktail of pseudocumene, trimethyl borate, and PPO wavelength shifter, designed to provide shielding, neutron vetoing, and in situ measurements of the TPC backgrounds. We present design and performance details of the DarkSide-50 outer detectors.

Wall-to-lumen ratio of intracranial arteries measured by indocyanine green angiography

PubMed Central

Nakagawa, Daichi; Shojima, Masaaki; Yoshino, Masanori; Kin, Taichi; Imai, Hideaki; Nomura, Seiji; Saito, Toki; Nakatomi, Hirofumi; Oyama, Hiroshi; Saito, Nobuhito

2016-01-01

Background: The wall-to-lumen ratio (WLR) is an important parameter in vascular medicine because it indicates the character of vascular wall as well as the degree of stenosis. Despite the advances in medical imaging technologies, it is still difficult to measure the thin-walled normal intracranial arteries, and the reports on the WLR of normal intracranial artery are limited. It might be possible to calculate the WLR using the indocyanine green (ICG) angiography, which is used to observe intracranial vessels during microsurgery. Purpose: To evaluate the WLR of normal intracranial arteries using ICG angiography. Materials and Methods: From the three cases in which ICG angiography was recorded with a ruler during microsurgery, 20 measurement points were chosen for the analysis. The ICG was injected intravenously with a dose of 0.2 mg/kg, and the vessels were inspected at high magnification using an operating microscope equipped with near-infrared illumination system. The vessel outer diameter and the luminal diameter were measured using the images before and after the ICG arrival based on the pixel ratio method using a ruler as reference, respectively. The WLR was calculated as 0.5 × (vessel outer diameter − vessel luminal diameter). Results: The WLR (mean ± standard deviation) of normal intracranial arteries was 0.086 ± 0.022. The WLR tended to be high in small arteries. Conclusion: The WLR of normal intracranial arteries calculated using ICG angiography was consistent with the WLR reported in the previous reports based on human autopsy. PMID:27695538

Self-Assembly of Ordered Hybrid Materials with over 100 nm Domain Spacings and up to 15 nm Nanoparticles using Bottle Brush Block Copolymers

NASA Astrophysics Data System (ADS)

Song, Dongpo; Lin, Ying; Qian, Gang; Wang, Xinyu; Liu, Xiaohui; Li, Cheng; Watkins, James

2014-03-01

The preparation of well-ordered nanocomposites using block copolymers and nanoparticles (NPs) with precise control over their spatial organization at different length scales remains challenging, especially for NP cores up to 10 nm in diameter and for domain spacings greater than 100 nm. In this work, these challenges have been overcome using amphiphilic bottle brush block copolymers as templates for the self-assembly of ordered, periodic hybrid materials with domain spacings more than 130 nm using functionalized NPs with core diameters up to 15 nm. CdSe NPs of 10 nm or gold NPs of 15 nm bearing 11-mercaptoundecyl-hydroquinone or poly(4-vinylphenol) ligands were selectively incorporated within (polynorbornene-g-polystyrene)-b- (polynorbornene-g-polyethylene oxide) copolymers by taking advantage of hydrogen bonding between the ligand and PEO domain. Well-ordered composites with cylindrical and lamellar morphologies and NP loadings of up to 30 wt% in the target domains were achieved. This strategy provides a simple and robust means to create ordered hybrid materials of large domain spacings allowing for relatively large functional nanoparticles. This work was supported by the NSF Center for Hierarchical Manufacturing at the University of Massachusetts (CMMI-1025020).

78 FR 62597 - 36(b)(1) Arms Sales Notification

Federal Register 2010, 2011, 2012, 2013, 2014

2013-10-22

... Block II missiles, 1000 GBU-39/B Small Diameter Bomb (SDB) with BRU-61 carriage systems, 40 CATM-84H... missiles, 1000 GBU-39/B Small Diameter Bombs (SDB), 40 CATM-84H Captive Air Training Missiles (CATM), 20... Small Diameter Bomb (SDB) I weapon is a 250-lb class, all-up round (AUR) that provides greater than 50nm...

[Resolving characteristic of CDOM by excitation-emission matrix spectroscopy combined with parallel factor analysis in the seawater of outer Yangtze Estuary in Autumn in 2010].

PubMed

Yan, Li-Hong; Chen, Xue-Jun; Su, Rong-Guo; Han, Xiu-Rong; Zhang, Chuan-Song; Shi, Xiao-Yong

2013-01-01

The distribution and estuarine behavior of fluorescent components of chromophoric dissolved organic matter in the seawater of outer Yangtze Estuary were determined by fluorescence excitation emission matrix spectra combined with parallel factor analysis. Six individual fluorescent components were identified by PARAFAC models, including three terrestrial humic-like components C1 [330 nm/390(430) nm], C2 (390 nm/480 nm), C3 (360 nm/440 nm), marine biological production component C5 (300 nm/400 nm) and protein-like components C4 (290 nm/350 nm) and C6 (275 nm/300 nm). The results indicated that C1, C2, and C3 showed a conservative mixing behavior in the whole estuarine region, especially in high-salinity region. And the fluorescence intensity proportion of C1 and C3 decreased with increase of salinity and fluorescence intensity proportion of C2 kept constant with increase of salinity in the whole estuarine region. While C4 showed conservative mixing behavior in low-salinity region and non-conservative mixing behavior in high-salinity region, and fluorescence intensity proportion of C4 increased with increase of salinity. However, C5 and C6 showed a non-conservative mixing behavior and fluorescence intensity proportion increased with increase of salinity in high-salinity region. Significantly spatial difference was recorded for CDOM absorption coefficient in the coastal region and in the open water areas with the highest value in coastal region and the lowest value in the open water areas. The scope of absorption coefficient and absorption slope was higher in coastal region than that in the open water areas. Significantly positive correlations were found between CDOM absorption coefficient and the fluorescence intensities of C1, C2, C3, and C4, but no significant correlation was found between C5 and C6, suggesting that the river inputs contributed to the coastal areas, while CDOM in the open water areas was affected by terrestrial inputs and phytoplankton degradation.

Laser-induced retinal injury thresholds: variation with retinal irradiated area

NASA Astrophysics Data System (ADS)

Lund, David J.; Schulmeister, Karl; Seiser, Bernhard; Edthofer, Florian

2005-04-01

The retinal injury threshold for exposure to a laser source varies as a function of the irradiated area on the retina. Currently accepted guidelines for the safe use of lasers provide that the MPE will increase as the diameter of the irradiated area for retinal diameters between 25 mm and 1700 mm, based on the ED50 data available in the late 1970s. Recent studies by Zuclich and Lund produced data showing that the ED50 for ns-duration exposures at 532 nm and ms duration exposures at 590 nm varied as the square of the diameter of the irradiated area on the retina. This paper will discuss efforts to resolve the disagreement between the new data and the earlier data though an analysis of all accessible data relating the retinal injury threshold to the diameter of the incident beam on the retina and through simulations using computer models of laser-induced injury. The results show that the retinal radiant exposure required to produce retinal injury is a function of both exposure duration and retinal irradiance diameter and that the current guidelines for irradiance diameter dependence do not accurately reflect the variation of the threshold data.

Uncertainty propagation using the Monte Carlo method in the measurement of airborne particle size distribution with a scanning mobility particle sizer

NASA Astrophysics Data System (ADS)

Coquelin, L.; Le Brusquet, L.; Fischer, N.; Gensdarmes, F.; Motzkus, C.; Mace, T.; Fleury, G.

2018-05-01

A scanning mobility particle sizer (SMPS) is a high resolution nanoparticle sizing system that is widely used as the standard method to measure airborne particle size distributions (PSD) in the size range 1 nm–1 μm. This paper addresses the problem to assess the uncertainty associated with PSD when a differential mobility analyzer (DMA) operates under scanning mode. The sources of uncertainty are described and then modeled either through experiments or knowledge extracted from the literature. Special care is brought to model the physics and to account for competing theories. Indeed, it appears that the modeling errors resulting from approximations of the physics can largely affect the final estimate of this indirect measurement, especially for quantities that are not measured during day-to-day experiments. The Monte Carlo method is used to compute the uncertainty associated with PSD. The method is tested against real data sets that are monosize polystyrene latex spheres (PSL) with nominal diameters of 100 nm, 200 nm and 450 nm. The median diameters and associated standard uncertainty of the aerosol particles are estimated as 101.22 nm  ±  0.18 nm, 204.39 nm  ±  1.71 nm and 443.87 nm  ±  1.52 nm with the new approach. Other statistical parameters, such as the mean diameter, the mode and the geometric mean and associated standard uncertainty, are also computed. These results are then compared with the results obtained by SMPS embedded software.

Synthesis of a fine neurological electrode by plasma polymerization processing.

PubMed

Cannon, J G; Dillon, R O; Bunshah, R F; Crandall, P H; Dymond, A M

1980-05-01

This research is part of a continuing program for the development of a coaxial depth electrode for research and diagnostic studies of neurological diseases. The requirements for this electrode include (1) strength and resistance to buckling sufficient to ensure self-forced penetration of brain tissue to a depth of 6 cm; (2) biocompatibility of the materials employed; (3) resistance to brittle fracture; and (4) a total diameter of less than 200 micrometer to minimize tissue damage. Earlier synthesis efforts using chemical vapor deposition techniques have been successful, although the process yield was 40% and an outer insulating layer had yet to be deposited. Plasma polymerization processes have been employed to realize an increase in the yield and provide an outer insulating layer. The starting material is W-26 at.% Re wire, nominally 125 micrometer in diameter. Hexamethyldisilazane(CH3)3SiNHSi(CH3)3 is used to deposit the insulating layers. The paper describes factors influencing the choice of materials, deposition techniques, and properties of electrodes.