The influence of pozzolanic materials on the mechanical stability of aluminous cement

DOE Office of Scientific and Technical Information (OSTI.GOV)

Collepardi, M.; Monosi, S.; Piccioli, P.

1995-07-01

High alumina cement is particularly suitable for manufacturing sulphate resistant concretes and in particular cement mixes which are able resist the sear water aggression. High alumina cement paste, in the presence of silica fume, shows an increasing strength trend even at 20 C and 40 C, since this pozzolan causes the formation of gehlenite hydrate (C{sub 2}ASH{sub 8}) and therefore strongly reduces the transformation of hexagonal aluminate hydrates (CAH{sub 10}, C{sub 2}AH{sub 8}) into the cubic hydrate (C{sub 3}AH{sub 6}) which is responsible for the strength loss of high-alumina cement mixes at higher temperatures (>20 C). On the contrary, flymore » ash is not suitable for reducing the transformation of hexagonal hydrates into the cubic phase. Consequently, the strength at 20 C and 40 C of the fly ash-high alumina cement mixes decrease as well as the high alumina cement pastes in the absence of pozzolan.« less

Reflective Packaging

NASA Technical Reports Server (NTRS)

1994-01-01

The aluminized polymer film used in spacecraft as a radiation barrier to protect both astronauts and delicate instruments has led to a number of spinoff applications. Among them are aluminized shipping bags, food cart covers and medical bags. Radiant Technologies purchases component materials and assembles a barrier made of layers of aluminized foil. The packaging reflects outside heat away from the product inside the container. The company is developing new aluminized lines, express mailers, large shipping bags, gel packs and insulated panels for the building industry.

Plasma Spray and Pack Cementation Process Optimization and Oxidation Behaviour of Novel Multilayered Coatings

NASA Astrophysics Data System (ADS)

Gao, Feng

The hot section components in gas turbines are subjected to a harsh environment with the temperature being increased continuously. The higher temperature has directly resulted in severe oxidation of these components. Monolithic coatings such as MCrAIY and aluminide have been traditionally used to protect the components from oxidation; however, increased operating temperature quickly deteriorates the coatings due to accelerated diffusion of aluminum in the coatings. To improve the oxidation resistance a group of multilayered coatings are developed in this study. The multilayered coatings consist of a Cr-Si co-deposited layer as the diffusion barrier, a plasma sprayed NiCrA1Y coating as the middle layer and an aluminized top layer. The Cr-Si and aluminized layers are fabricated using pack cementation processes and the NiCrA1Y coatings are produced using the Mettech Axial III(TM) System. All of the coating processes are optimized using the methodology of Design of Experiments (DOE) and the results are analyzed using statistical method. The optimal processes are adopted to fabricate the multilayered coatings for oxidation tests. The coatings are exposed in air at 1050°C and 1150°C for 1000 hr. The results indicate that a Cr layer and a silicon-rich barrier layer have formed on the interface between the Cr-Si coating and the NiCrA1Y coating. This barrier layer not only prevents aluminum and chromium from diffusing into the substrate, but also impedes the diffusion of other elements from the substrate into the coating. The results also reveal that, for optimal oxidation resistance at 1050°C, the top layer in a multilayered coating should have at least Al/Ni ratio of one; whereas the multilayered coating with the All Ni ratio of two in the top layer exhibits the best oxidation resistance at 1150°C. The DOE methodology provides an excellent means for process optimization and the selection of oxidation test matrix, and also offers a more thorough understanding of the effects of process parameters on the coating microstructure, and the effects of layers and their interactions on the oxidation behavior of the multilayered coatings.

Research on Performance and Microstructure of Sewage Pipe Mortar Strengthened with Different Anti-Corrosion Technologies

NASA Astrophysics Data System (ADS)

Mu, Song; Zhou, Huaxin; Shi, Liang; Liu, Jianzhong; Cai, Jingshun; Wang, Feng

2017-10-01

Mostly urban underground sewage is the acidic corrosion environment with a high concentration of aggressive ions and microbe, which resulted in performance deterioration and service-life decrease of sewage concrete pipe. In order to effectively protect durability of the concrete pipe, the present paper briefly analysed the main degradation mechanism of concrete pipe attacked by urban underground sewage, and proposed that using penetrating and strengthening surface sealer based on inorganic chemistry. In addition, using index of compressive strength, weight loss and appearance level to investigate the influence of the sealer on corrosion resistance of mortar samples after different dry-wet cycles. Besides, comparative research on effect of the sealer, aluminate cement and admixture of corrosion resistance was also addressed. At last, the SEM technology was used to reveal the improvement mechanism of different technologies of corrosion resistance. The results indicated that the sealer and aluminate cement can significantly improve corrosion resistance of mortar. Besides, the improvement effect can be described as the descending order: the penetrating and strengthening surface sealer > aluminate cement > admixture of corrosion resistance. The mortar sample treated with the sealer displayed the condensed and sound microstructure which proved that the sealer can improve the corrosion resistance to urban underground sewage.

Cement and concrete

NASA Technical Reports Server (NTRS)

Corley, Gene; Haskin, Larry A.

1992-01-01

To produce lunar cement, high-temperature processing will be required. It may be possible to make calcium-rich silicate and aluminate for cement by solar heating of lunar pyroxene and feldspar, or chemical treatment may be required to enrich the calcium and aluminum in lunar soil. The effects of magnesium and ferrous iron present in the starting materials and products would need to be evaluated. So would the problems of grinding to produce cement, mixing, forming in vacuo and low gravity, and minimizing water loss.

Developing a More Rapid Test to Assess Sulfate Resistance of Hydraulic Cements

PubMed Central

Ferraris, Chiara; Stutzman, Paul; Peltz, Max; Winpigler, John

2005-01-01

External sulfate attack of concrete is a major problem that can appear in regions where concrete is exposed to soil or water containing sulfates, leading to softening and cracking of the concrete. Therefore, it is important that materials selection and proportioning of concrete in susceptible regions be carefully considered to resist sulfate attack. American Society for Testing Materials (ASTM) limits the tricalcium aluminate phase in cements when sulfate exposure is of concern. The hydration products of tricalcium aluminate react with the sulfates resulting in expansion and cracking. While ASTM standard tests are available to determine the susceptibility of cements to sulfate attack, these tests require at least 6 months and often up to a year to perform; a delay that hinders development of new cements. This paper presents a new method for testing cement resistance to sulfate attack that is three to five times faster than the current ASTM tests. Development of the procedure was based upon insights on the degradation process by petrographic examination of sulfate-exposed specimens over time. Also key to the development was the use of smaller samples and tighter environmental control. PMID:27308177

Recycling of red muds with the extraction of metals and special additions to cement

NASA Astrophysics Data System (ADS)

Zinoveev, D. V.; Diubanov, V. G.; Shutova, A. V.; Ziniaeva, M. V.

2015-01-01

The liquid-phase reduction of iron oxides from red mud is experimentally studied. It is shown that, in addition to a metal, a slag suitable for utilization in the construction industry can be produced as a result of pyrometallurgical processing of red mud. Portland cement is shown to be produced from this slag with mineral additions and a high-aluminate expansion addition to cement.

Effect of Tartaric Acid on Hydration of a Sodium-Metasilicate-Activated Blend of Calcium Aluminate Cement and Fly Ash F

PubMed Central

Pyatina, Tatiana; Sugama, Toshifumi; Moon, Juhyuk; James, Simon

2016-01-01

An alkali-activated blend of aluminum cement and class F fly ash is an attractive solution for geothermal wells where cement is exposed to significant thermal shocks and aggressive environments. Set-control additives enable the safe cement placement in a well but may compromise its mechanical properties. This work evaluates the effect of a tartaric-acid set retarder on phase composition, microstructure, and strength development of a sodium-metasilicate-activated calcium aluminate/fly ash class F blend after curing at 85 °C, 200 °C or 300 °C. The hardened materials were characterized with X-ray diffraction, thermogravimetric analysis, X-ray computed tomography, and combined scanning electron microscopy/energy-dispersive X-ray spectroscopy and tested for mechanical strength. With increasing temperature, a higher number of phase transitions in non-retarded specimens was found as a result of fast cement hydration. The differences in the phase compositions were also attributed to tartaric acid interactions with metal ions released by the blend in retarded samples. The retarded samples showed higher total porosity but reduced percentage of large pores (above 500 µm) and greater compressive strength after 300 °C curing. Mechanical properties of the set cements were not compromised by the retarder. PMID:28773543

Effect of Tartaric Acid on Hydration of a Sodium-Metasilicate-Activated Blend of Calcium Aluminate Cement and Fly Ash F

DOE PAGES

Pyatina, Tatiana; Sugama, Toshifumi; Moon, Juhyuk; ...

2016-05-27

An alkali-activated blend of aluminum cement and class F fly ash is an attractive solution for geothermal wells where cement is exposed to significant thermal shocks and aggressive environments. Set-control additives enable the safe cement placement in a well but may compromise its mechanical properties. Here, this work evaluates the effect of a tartaric-acid set retarder on phase composition, microstructure, and strength development of a sodium-metasilicate-activated calcium aluminate/fly ash class F blend after curing at 85 °C, 200 °C or 300 °C. The hardened materials were characterized with X-ray diffraction, thermogravimetric analysis, X-ray computed tomography, and combined scanning electron microscopy/energy-dispersivemore » X-ray spectroscopy and tested for mechanical strength. With increasing temperature, a higher number of phase transitions in non-retarded specimens was found as a result of fast cement hydration. The differences in the phase compositions were also attributed to tartaric acid interactions with metal ions released by the blend in retarded samples. The retarded samples showed higher total porosity but reduced percentage of large pores (above 500 µm) and greater compressive strength after 300 °C curing. Lastly, mechanical properties of the set cements were not compromised by the retarder.« less

Effect of Tartaric Acid on Hydration of a Sodium-Metasilicate-Activated Blend of Calcium Aluminate Cement and Fly Ash F.

PubMed

Pyatina, Tatiana; Sugama, Toshifumi; Moon, Juhyuk; James, Simon

2016-05-27

An alkali-activated blend of aluminum cement and class F fly ash is an attractive solution for geothermal wells where cement is exposed to significant thermal shocks and aggressive environments. Set-control additives enable the safe cement placement in a well but may compromise its mechanical properties. This work evaluates the effect of a tartaric-acid set retarder on phase composition, microstructure, and strength development of a sodium-metasilicate-activated calcium aluminate/fly ash class F blend after curing at 85 °C, 200 °C or 300 °C. The hardened materials were characterized with X-ray diffraction, thermogravimetric analysis, X-ray computed tomography, and combined scanning electron microscopy/energy-dispersive X-ray spectroscopy and tested for mechanical strength. With increasing temperature, a higher number of phase transitions in non-retarded specimens was found as a result of fast cement hydration. The differences in the phase compositions were also attributed to tartaric acid interactions with metal ions released by the blend in retarded samples. The retarded samples showed higher total porosity but reduced percentage of large pores (above 500 µm) and greater compressive strength after 300 °C curing. Mechanical properties of the set cements were not compromised by the retarder.

Investigation into the stabilization/solidification performance of Portland cement through cement clinker phases.

PubMed

Qiao, X C; Poon, C S; Cheeseman, C R

2007-01-10

This research studied the influence of individual heavy metal on the hydration reactions of major cement clinker phases in order to investigate the performance of cement based stabilization/solidification (S/S) system. Tricalcium silicate (C3S) and tricalcium aluminate (C3A) had been mixed with individual heavy metal hydroxide including Zn(OH)2, Pb(OH)2 and Cu(OH)2, respectively. The influences of these heavy metal hydroxides on the hydration of C3S and C3A have been characterized by X-ray diffraction (XRD) and differential scanning calorimetry-thermogravimetry (DSC-TG). A mixture of Zn(OH)2, Pb(OH)2 and Cu(OH)2 was blended with Portland cement (PC) and evaluated through compressive strength and dynamic leach test. XRD and DSC-TG data show that all the heavy metal hydroxides (Zn(OH)2, Pb(OH)2 and Cu(OH)2) have detrimental effects on the hydration of C3A, but only Zn(OH)2 does to the C3S at early curing ages which can completely inhibit the hydration of C3S due to the formation of CaO(Zn(OH)2).2H2O. Cu6Al2O8CO(3).12H2O, Pb2Al4O4(CO3)(4).7H2O and Zn6Al2O8CO(3).12H2O are formed in all the samples containing C3A in the presence of metal hydroxides. After adding CaSO4 into C3A, the detrimental effect of heavy metals increases due to the coating effect of both calcium aluminate sulphates and heavy metal aluminate carbonates. The influence of heavy metal hydroxide on the hydration of C3S and C3A can be used to predict the S/S performance of Portland cement.

The biocompatibility of modified experimental Portland cements with potential for use in dentistry.

PubMed

Camilleri, J

2008-12-01

To evaluate the biocompatibility of a group of new potential dental materials and their eluants by assessing cell viability. Calcium sulpho-aluminate cement (CSA), calcium fluoro-aluminate cement (CFA) and glass-ionomer cement (GIC; Ketac Molar), used as the control, were tested for biocompatibility. Using a direct test method cell viability was measured quantitatively using alamarBluetrade mark dye, and an indirect test method where cells were grown on material elutions and cell viability was assessed using methyltetrazolium (MTT) assay as recommended by ISO 10 993-Part 5 for in vitro testing. Statistical analysis was performed by analysis of variance and Tukey multi-comparison test method. Elution collected from the prototype cements and the GIC cured for 1 and 7 days allowed high cell activity after 24 h cell exposure, which reduced after 48 h when compared to the nontoxic glass-ionomer control, but increased significantly after 72 h cell contact. Elutions collected after 28 days revealed reduced cell activity at all cell exposure times. Cells placed in direct contact with the prototype materials showed reduced cell activity when compared with the control. Cell growth was poor when seeded in direct contact with the prototype cements. GIC encouraged cell growth after 1 day of contact. The eluted species for all the cements tested exhibited adequate cell viability in the early ages with reduced cell activity at 28 days. Changes in the production of calcium hydroxide as a by-product of cement hydration affect the material biocompatibility adversely.

Ternary Blends of High Aluminate Cement, Fly ash and Blast-furnace slag for Sewerage Lining Mortar

NASA Astrophysics Data System (ADS)

Chao, L. C.; Kuo, C. P.

2018-01-01

High aluminate cement (HAC), fly ash (FA) and blast-furnace slag (BFS) have been treated sustainable materials for the use of cement products for wastewater infrastructure due to their capabilities of corrosion resistance. The purpose of this study is to optimize a ternary blend of above mentioned materials for a special type of mortar for sewerage lining. By the using of Taguchi method, four control parameters including water/cementitious material ratio, mix water content, fly ash content and blast-furnace slag content were considered in nine trial mix designs in this study. By evaluating target properties including (1) maximization of compressive strength, (2) maximization of electricity resistance and (3) minimization of water absorption rate, the best possible levels for each control parameter were determined and the optimal mix proportions were verified. Through the implementation of the study, a practical and completed idea for designing corrosion resistive mortar comprising HAC, FA and BSF is provided.

Hydration kinetics of CA{sub 2} and CA-Investigations performed on a synthetic calcium aluminate cement

DOE Office of Scientific and Technical Information (OSTI.GOV)

Klaus, S.R., E-mail: klaus@geol.uni-erlangen.de; Neubauer, J., E-mail: juergen.neubauer@gzn.uni-erlangen.de; Goetz-Neunhoeffer, F., E-mail: friedlinde.goetz@gzn.uni-erlangen.de

2013-01-15

Much is already known about the hydration of monocalcium aluminate (CA) in calcium aluminate cements (CACs). CA{sub 2} is known to be weakly hydraulic. Therefore, the hydration kinetics of CA{sub 2} were not of as great interest as those of the hydration of CAC. We were able to show that the hydration of CA{sub 2} begins as soon as the hydration rate of CA has reached its maximum and the first precipitation of C{sub 2}AH{sub 8} has started. The hydration of different CA/CA{sub 2} ratios was analyzed by the G-factor quantification. The individual contributions of the phases CA and CA{submore » 2} to the heat flow were calculated based on the amounts dissolved by applying thermodynamic data. The heat flow as calculated from XRD data was then compared with the measured heat flow. It obtained a good consistency between the two. The very pronounced influence of CA{sub 2} during hydration of CAC can be clearly demonstrated.« less

DOE Office of Scientific and Technical Information (OSTI.GOV)

Bizzozero, Julien, E-mail: julien.bizzozero@gmail.com; Scrivener, Karen L.

This paper reports a study of ternary blends composed of calcium aluminate cement, calcium sulfate hemihydrate and limestone. Compressive strength tests and hydration kinetics were studied as a function of limestone and calcium sulfate content. The phase evolution and the total porosity were followed and compared to thermodynamic simulation to understand the reactions involved and the effect of limestone on these binders. The reaction of limestone leads to the formation of hemicarboaluminate and monocarboaluminate. Increasing the ratio between sulfate and aluminate decreases the extent of limestone reaction.

Microstructure and elevated-temperature erosion-oxidation behaviour of aluminized 9Cr-1Mo Steel

NASA Astrophysics Data System (ADS)

Huttunen-Saarivirta, E.; Honkanen, M.; Tsipas, S. A.; Omar, H.; Tsipas, D.

2012-10-01

Degradation of materials by a combination of erosive wear and atmospheric oxidation at elevated temperatures constitutes a problem in some power generation processes, such as fluidized-bed combustion. In this work, 9Cr-1Mo steel, a common tube material in combustion chambers, is coated by a pack cementation method from an Al-containing pack in order to improve the resistance to erosion-oxidation at elevated temperatures. The resulting coating is studied in terms of microstructure and microhardness and tested for its resistance against impacts by sand particles in air at temperatures of 550-700 °C under several conditions, with thickness changes and appearance of the exposed surfaces being studied. The coating was found to contain several phases and layers, the outermost of which was essentially Al-rich and contained e.g., small AlN precipitates. The microhardness values for such coating ranged from 950 to 1100 HV20g. The coating provided the substrate with increased protection particularly against normal particle impacts, as manifested by smaller thickness losses for coated specimens as compared to uncoated counterparts. However, much of the coating was lost under all test conditions, despite the fact that particle debris formed a homogeneous layer on the surface. These results are described and discussed in this paper.

Treatment of toxic metal aqueous solutions: encapsulation in a phosphate-calcium aluminate matrix.

PubMed

Fernández, J M; Navarro-Blasco, I; Duran, A; Sirera, R; Alvarez, J I

2014-07-01

Polyphosphate-modified calcium aluminate cement matrices were prepared by using aqueous solutions polluted with toxic metals as mixing water to obtain waste-containing solid blocks with improved management and disposal. Synthetically contaminated waters containing either Pb or Cu or Zn were incorporated into phosphoaluminate cement mortars and the effects of the metal's presence on setting time and mechanical performance were assessed. Sorption and leaching tests were also executed and both retention and release patterns were investigated. For all three metals, high uptake capacities as well as percentages of retention larger than 99.9% were measured. Both Pb and Cu were seen to be largely compatible with this cementitious matrix, rendering the obtained blocks suitable for landfilling or for building purposes. However, Zn spoilt the compressive strength values because of its reaction with hydrogen phosphate anions, hindering the development of the binding matrix. Copyright © 2014 Elsevier Ltd. All rights reserved.

Characterization of films formed by the aluminizing of T91 steel

NASA Astrophysics Data System (ADS)

Sanabria Cala, J. A.; Conde Rodríguez, G. R.; Y Peña Ballesteros, D.; Laverde Cataño, D.; Quintero Rangel, L. S.

2017-12-01

The aluminizing of a T91 martensitic ferritic steel was carried out by a novel modification to the traditional technique of packed cementation, with the objective of producing a diffusion coating of aluminum in a shorter time and operating cost, from a technique that allows the reuse of powder packaging and which the coating of metal parts with complex shapes can be secured. As an aluminum source, commercial foil is used to wrap the piece to be coated, while the powder packaging contains aluminum oxide Al2O3 and an activating salt, ammonium chloride NH4Cl. During the deposition process of the coating, the NH4Cl is decomposed by reacting with foil, and thus, aluminum halides can be transferred to the metallic substrate, which deposit aluminum on the T91 steel surface while Al2O3 can be recycled for subsequent processes. The results of the diffractograms and micrographs indicated the strong influence of temperature, exposure time and ammonium chloride concentration in the formation and growth evolution of a stable coating of iron-aluminum and iron-aluminum-nickel on the T91 steel surface, which was effectively deposited at a temperature of 700°C and an exposure period of 9 hours. The coating formed on the T91 steel surface could play a protective role towards the material by acting as a physical barrier between the alloy and other corrosive species in high temperature operated systems.

New Ultra-Low Permittivity Composites for Use in Ceramic Packaging of Ga:As Integrated Circuits

DTIC Science & Technology

1986-08-11

200 400 600 800 1000 SOAK TEMPERATURE (-C) Figure 8. Effect of leaching and heat treatment on relative permittivity of porous vycor glass. measured by...thermal treatment in strength, shrinkage and dielectric properties. 22 -𔃼 The feasibility of tape casting calcium aluminate cement into thin substrates...materials. (3) Vibro-compaction and calandering of cements containing microspheres. (4) Heat treatment of the polymer-containing materials. 23 V

Evaluation of super-water reducers for highway applications

NASA Astrophysics Data System (ADS)

Whiting, D.

1981-03-01

Super-water reducers were characterized and evaluated as potential candidates for production of low water to cement ratio, high strength concretes for highway construction applications. Admixtures were composed of either naphthalene or melamine sulfonated formaldehyde condensates. A mini-slump procedure was used to assess dosage requirements and behavior of workability with time of cement pastes. Required dosage was found to be a function of tricalcium aluminate content, alkali content, and fineness of the cement. Concretes exhibited high rates of slump loss when super-water reducers were used. The most promising area of application of these products appears to be in production of dense, high cement content concrete using mobile concrete mixer/transporters.

Comparative examination of the microstructure and high temperature oxidation performance of NiCrBSi flame sprayed and pack cementation coatings

NASA Astrophysics Data System (ADS)

Chaliampalias, D.; Vourlias, G.; Pavlidou, E.; Skolianos, S.; Chrissafis, K.; Stergioudis, G.

2009-01-01

Coatings formed from NiCrBSi powder were deposited by thermal spray and pack cementation processes on low carbon steel. The microstructure and morphology of the coatings were studied by scanning electron microscopy (SEM) and X-ray diffraction analysis (XRD). Flame sprayed coatings exhibited high porosity and were mechanically bonded to the substrate while pack cementation coatings were more compact and chemically bonded to the substrate. The microhardness and the high temperature oxidation resistance of the coated samples were evaluated by a Vickers microhardness tester and by thermogravimetric measurements (TG), respectively. Pack cementation coatings showed higher hardness and were more protective to high temperature environments than the flame sprayed coatings.

Thermodynamics and kinetics of reactions in protective coating systems

NASA Technical Reports Server (NTRS)

Gupta, B.; Sarkhel, A.; Shankar, S.; Seigle, L.

1975-01-01

A study of the aluminization of Ni from packs containing various percentages of unalloyed Al confirmed that the surface aluminum content of specimens aluminized tends to decrease with time and consequently a simple parabolic law for the weight-gain vs. time relationship is not obeyed. The diffusivity-composition relationship in NiAl was examined, and a set of curves is presented. A numerical method for the calculation of coating dissolution rates was developed and applied to NiAl-Ni3Al type of coatings.

Impact of welan gum on tricalcium aluminate-gypsum hydration

DOE Office of Scientific and Technical Information (OSTI.GOV)

Ma Lei, E-mail: malei198713@163.com; Zhao Qinglin, E-mail: zhaoqinglin@whut.edu.cn; Yao Chukang

The retarding effect of welan gum on tricalcium aluminate-gypsum hydration, as a partial system of ordinary Portland cement (OPC) hydration, was investigated with several methods. The tricalcium aluminate-gypsum hydration behavior in the presence or absence of welan gum was researched by field emission gun scanning electron microscopy, X-ray diffraction and zeta potential analysis. Meanwhile, we studied the surface electrochemical properties and adsorption characteristics of welan gum by utilizing a zeta potential analyzer and UV-VIS absorption spectrophotometer. By adding welan gum, the morphology change of ettringite and retardation of hydration stages in tricalcium aluminate-gypsum system was observed. Moreover, we detected themore » adsorption behavior and zeta potential inversion of tricalcium aluminate and ettringite, as well as a rapid decrease in the zeta potential of tricalcium aluminate-gypsum system. The reduction on nucleation rate of ettringite and hydration activity of C{sub 3}A was also demonstrated. Thus, through the adsorption effect, welan gum induces a retarding behavior in tricalcium aluminate-gypsum hydration. Highlights: Black-Right-Pointing-Pointer Adsorption characteristics of welan gum on C{sub 3}A and ettringite have been studied. Black-Right-Pointing-Pointer C{sub 3}A-gypsum hydration behavior and the hydration products are examined in L/S = 3. Black-Right-Pointing-Pointer Welan gum retards the process of C{sub 3}A-gypsum hydration. Black-Right-Pointing-Pointer The addition of welan gum changes the nucleation growth of ettringite.« less

Peculiarities of the processes of hydration of binding substances in the arbolite mixture

NASA Astrophysics Data System (ADS)

Innokentieva, L. S.; Egorova, A. D.; Emelianova, Z. V.

2017-09-01

Cement and sand solution is traditionally used for production of wood concrete. But it is known that impact of water-soluble substances of wood on the hardening cement is shown in the stabilizing effect. The "Cement poisons" consisting generally of the HOCH carbohydrate groups, sedimented on a surface of particles of minerals of cement 3CaO.SiO2 (three-calcic silicate) and 3CaO.Al2O3 (three-calcic aluminate) form the thinnest covers which complicate the course of processes of hydration of cement. Plaster in comparison with cement is less sensitive to extractive substances of wood therefore their combination to wood (including waste of logging and a woodworking) both coniferous and deciduous species is allowed. Composite plaster binding with hongurin as active mineral additive agent are applied at selection of composition of arbolite, at the same time dependences of their physicomechanical properties on characteristics of filler are received.

Role of Tartaric Acid in Chemical, Mechanical and Self-Healing Behaviors of a Calcium-Aluminate Cement Blend with Fly Ash F under Steam and Alkali Carbonate Environments at 270 °C

PubMed Central

Pyatina, Tatiana; Sugama, Toshifumi

2017-01-01

Tartaric acid (TA) changes short-term mechanical behavior and phase composition of sodium-metasilicate activated calcium-aluminate cement blend with fly ash, type F, when used as a set control additive to allow sufficient pumping time for underground well placement. The present work focuses on TA effect on self-healing properties of the blend under steam or alkali carbonate environments at 270 °C applicable to geothermal wells. Compressive strength recoveries and cracks sealing were examined to evaluate self-healing of the cement after repeated crush tests followed by two consecutive healing periods of 10 and 5 days at 270 °C. Optical and scanning electron microscopes, X-ray diffraction, Fourier Transform infrared and EDX measurements along with thermal gravimetric analyses were used to identify phases participating in the healing processes. Samples with 1% mass fraction of TA by weight of blend demonstrated improved strength recoveries and crack plugging properties, especially in alkali carbonate environment. This effect was attributed to silicon-rich (C,N)-A-S-H amorphous phase predominant in TA-modified samples, high-temperature stable zeolite phases along with the formation of tobermorite-type crystals in the presence of tartaric acid. PMID:28772701

Role of Tartaric Acid in Chemical, Mechanical and Self-Healing Behaviors of a Calcium-Aluminate Cement Blend with Fly Ash F under Steam and Alkali Carbonate Environments at 270°C

DOE Office of Scientific and Technical Information (OSTI.GOV)

Pyatina, Tatiana; Sugama, Toshifumi

Tartaric acid (TA) changes short-term mechanical behavior and phase composition of sodium-metasilicate activated calcium-aluminate cement blend with fly ash, type F, when used as a set control additive to allow sufficient pumping time for underground well placement. The present work focuses on TA effect on self-healing properties of the blend under steam or alkali carbonate environments at 270°C applicable to geothermal wells. Compressive strength recoveries and cracks sealing were examined to evaluate self-healing of the cement after repeated crush tests followed by two consecutive healing periods of 10 and 5 days at 270°C. Optical and scanning electron microscopes, X-ray diffraction,more » Fourier Transform infrared and EDX measurements along with thermal gravimetric analyses were used to identify phases participating in the healing processes. Samples with 1% mass fraction of TA by weight of blend demonstrated improved strength recoveries and crack plugging properties, especially in alkali carbonate environment. This effect was attributed to silicon-rich (C,N)-A-S-H amorphous phase predominant in TA-modified samples, high-temperature stable zeolite phases along with the formation of tobermorite-type crystals in the presence of tartaric acid.« less

Role of Tartaric Acid in Chemical, Mechanical and Self-Healing Behaviors of a Calcium-Aluminate Cement Blend with Fly Ash F under Steam and Alkali Carbonate Environments at 270°C

DOE PAGES

Pyatina, Tatiana; Sugama, Toshifumi

2017-03-25

Tartaric acid (TA) changes short-term mechanical behavior and phase composition of sodium-metasilicate activated calcium-aluminate cement blend with fly ash, type F, when used as a set control additive to allow sufficient pumping time for underground well placement. The present work focuses on TA effect on self-healing properties of the blend under steam or alkali carbonate environments at 270°C applicable to geothermal wells. Compressive strength recoveries and cracks sealing were examined to evaluate self-healing of the cement after repeated crush tests followed by two consecutive healing periods of 10 and 5 days at 270°C. Optical and scanning electron microscopes, X-ray diffraction,more » Fourier Transform infrared and EDX measurements along with thermal gravimetric analyses were used to identify phases participating in the healing processes. Samples with 1% mass fraction of TA by weight of blend demonstrated improved strength recoveries and crack plugging properties, especially in alkali carbonate environment. This effect was attributed to silicon-rich (C,N)-A-S-H amorphous phase predominant in TA-modified samples, high-temperature stable zeolite phases along with the formation of tobermorite-type crystals in the presence of tartaric acid.« less

Corrosion of aluminium metal in OPC- and CAC-based cement matrices

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kinoshita, Hajime, E-mail: h.kinoshita@sheffield.ac.uk; Swift, Paul; Utton, Claire

Corrosion of aluminium metal in ordinary Portland cement (OPC) based pastes produces hydrogen gas and expansive reaction products causing problems for the encapsulation of aluminium containing nuclear wastes. Although corrosion of aluminium in cements has been long known, the extent of aluminium corrosion in the cement matrices and effects of such reaction on the cement phases are not well established. The present study investigates the corrosion reaction of aluminium in OPC, OPC-blast furnace slag (BFS) and calcium aluminate cement (CAC) based systems. The total amount of aluminium able to corrode in an OPC and 4:1 BFS:OPC system was determined, andmore » the correlation between the amount of calcium hydroxide in the system and the reaction of aluminium obtained. It was also shown that a CAC-based system could offer a potential matrix to incorporate aluminium metal with a further reduction of pH by introduction of phosphate, producing a calcium phosphate cement.« less

Inorganic Corrosion-Inhibitive Pigments for High-Temperature Alkali-activated Well Casing Foam Cement

DOE Office of Scientific and Technical Information (OSTI.GOV)

Sugama, T.; Pyatina, T.

2014-11-01

This study evaluates inorganic pigments for improving carbon steel (CS) brine-corrosion protection by the sodium metasilicate-activated calcium aluminate cement/Fly Ash blend at 300°C. Calcium borosilicate (CBS) and zinc phosphate, significantly improved CS corrosion-protection by decreasing cement’s permeability for corrosive ions and inhibiting anodic corrosion. An amorphous Na 2O-Al 2O 3-SiO 2-H 2O phase tightly attached to CS surface formed at 300oC in CBS-modified cement pore solution. The corrosion rate of the CS covered with this phase was nearly 4-fold lower than in the case of nonmodified cement pore solution where the major phase formed on the surface of CS wasmore » crystalline analcime.« less

Inorganic Corrosion-Inhibitive Pigments for High-Temperature Alkali-activated Well Casing Foam Cement

DOE Office of Scientific and Technical Information (OSTI.GOV)

Sugama, T.; Pyatina, T.

2014-11-14

This study evaluates inorganic pigments for improving carbon steel (CS) brine-corrosion protection by the sodium metasilicate-activated calcium aluminate cement/Fly Ash blend at 300°C. Calcium borosilicate (CBS) and zinc phosphate, significantly improved CS corrosion-protection by decreasing cement’s permeability for corrosive ions and inhibiting anodic corrosion. An amorphous Na 2O-Al 2O 3-SiO 2-H 2O phase tightly attached to CS surface formed at 300oC in CBS-modified cement pore solution. The corrosion rate of the CS covered with this phase was nearly 4-fold lower than in the case of nonmodified cement pore solution where the major phase formed on the surface of CS wasmore » crystalline analcime.« less

Origins of saccharide-dependent hydration at aluminate, silicate, and aluminosilicate surfaces.

PubMed

Smith, Benjamin J; Rawal, Aditya; Funkhouser, Gary P; Roberts, Lawrence R; Gupta, Vijay; Israelachvili, Jacob N; Chmelka, Bradley F

2011-05-31

Sugar molecules adsorbed at hydrated inorganic oxide surfaces occur ubiquitously in nature and in technologically important materials and processes, including marine biomineralization, cement hydration, corrosion inhibition, bioadhesion, and bone resorption. Among these examples, surprisingly diverse hydration behaviors are observed for oxides in the presence of saccharides with closely related compositions and structures. Glucose, sucrose, and maltodextrin, for example, exhibit significant differences in their adsorption selectivities and alkaline reaction properties on hydrating aluminate, silicate, and aluminosilicate surfaces that are shown to be due to the molecular architectures of the saccharides. Solid-state (1)H, (13)C, (29)Si, and (27)Al nuclear magnetic resonance (NMR) spectroscopy measurements, including at very high magnetic fields (19 T), distinguish and quantify the different molecular species, their chemical transformations, and their site-specific adsorption on different aluminate and silicate moieties. Two-dimensional NMR results establish nonselective adsorption of glucose degradation products containing carboxylic acids on both hydrated silicates and aluminates. In contrast, sucrose adsorbs intact at hydrated silicate sites and selectively at anhydrous, but not hydrated, aluminate moieties. Quantitative surface force measurements establish that sucrose adsorbs strongly as multilayers on hydrated aluminosilicate surfaces. The molecular structures and physicochemical properties of the saccharides and their degradation species correlate well with their adsorption behaviors. The results explain the dramatically different effects that small amounts of different types of sugars have on the rates at which aluminate, silicate, and aluminosilicate species hydrate, with important implications for diverse materials and applications.

Sustainable Blended Cements-Influences of Packing Density on Cement Paste Chemical Efficiency.

PubMed

Knop, Yaniv; Peled, Alva

2018-04-18

This paper addresses the development of blended cements with reduced clinker amount by partial replacement of the clinker with more environmentally-friendly material (e.g., limestone powders). This development can lead to more sustainable cements with reduced greenhouse gas emission and energy consumption during their production. The reduced clicker content was based on improved particle packing density and surface area of the cement powder by using three different limestone particle diameters: smaller (7 µm, 3 µm) or larger (70 µm, 53 µm) than the clinker particles, or having a similar size (23 µm). The effects of the different limestone particle sizes on the chemical reactivity of the blended cement were studied by X-ray diffraction (XRD), thermogravimetry and differential thermogravimetry (TG/DTG), loss on ignition (LOI), isothermal calorimetry, and the water demand for reaching normal consistency. It was found that by blending the original cement with limestone, the hydration process and the reactivity of the limestone itself were increased by the increased surface area of the limestone particles. However, the carbonation reaction was decreased with the increased packing density of the blended cement with limestone, having various sizes.

Microstructure of amorphous aluminum hydroxide in belite-calcium sulfoaluminate cement

DOE Office of Scientific and Technical Information (OSTI.GOV)

Song, Fei; Yu, Zhenglei; Yang, Fengling

Belite-calcium sulfoaluminate (BCSA) cement is a promising low-CO{sub 2} alternative to ordinary Portland cement. Herein, aluminum hydroxide (AH{sub 3}), the main amorphous hydration product of BCSA cement, was investigated in detail. The microstructure of AH{sub 3} with various quantities of gypsum was investigated via scanning electron microscopy (SEM) and energy dispersive X-ray spectroscopy (EDS). The AH{sub 3} with various morphologies were observed and confirmed in the resulting pastes. Particular attention was paid to the fact that AH{sub 3} always contained a small amount of Ca according to the results of EDS analysis. The AH{sub 3} was then characterized via highmore » resolution transmission electron microscopy (HRTEM). The results of HRTEM indicated that Ca arose from nanosized tricalcium aluminate hexahydrate which existed in the AH{sub 3}.« less

Identification of the hydrate gel phases present in phosphate-modified calcium aluminate binders

DOE Office of Scientific and Technical Information (OSTI.GOV)

Chavda, Mehul A.; Bernal, Susan A.; Apperley, David C.

The conversion of hexagonal calcium aluminate hydrates to cubic phases in hydrated calcium aluminate cements (CAC) can involve undesirable porosity changes and loss of strength. Modification of CAC by phosphate addition avoids conversion, by altering the nature of the reaction products, yielding a stable amorphous gel instead of the usual crystalline hydrate products. Here, details of the environments of aluminium and phosphorus in this gel were elucidated using solid-state NMR and complementary techniques. Aluminium is identified in both octahedral and tetrahedral coordination states, and phosphorus is present in hydrous environments with varying, but mostly low, degrees of crosslinking. A {supmore » 31}P/{sup 27}Al rotational echo adiabatic passage double resonance (REAPDOR) experiment showed the existence of aluminium–phosphorus interactions, confirming the formation of a hydrated calcium aluminophosphate gel as a key component of the binding phase. This resolves previous disagreements in the literature regarding the nature of the disordered products forming in this system.« less

Physico-chemical mechanisms involved in the acceleration of the hydration of calcium sulfoaluminate cement by lithium ions

DOE Office of Scientific and Technical Information (OSTI.GOV)

Cau Dit Coumes, Céline, E-mail: celine.cau-dit-coumes@cea.fr; Dhoury, Mélanie; Champenois, Jean-Baptiste

This work investigates the influence of lithium ions on the hydration at 25 °C of two calcium sulfoaluminate (CSA) cements comprising 0 or 10% gypsum. Small concentrations of lithium salts (LiOH, LiNO{sub 3}) accelerate the early hydration of both CSA cements either in paste or in diluted and stirred suspension. The effect of the lithium cation is much stronger than its counter-ion. Hydration is accelerated by an increase in the lithium concentration up to 30 μmol Li/g of the used CSA cement (with a high ye'elimite content), and then levels off. The postulated mechanism relies on a fast precipitation ofmore » amorphous Li-containing Al(OH){sub 3}, which acts as seeds for accelerating the precipitation of amorphous Al(OH){sub 3} that speeds up the whole hydration process. This process seems to be closely related to the one involved in the acceleration of the hydration of calcium aluminate cement by lithium ions.« less

Mineralogenic characteristics of osteogenic lineage-committed human dental pulp stem cells following their exposure to a discoloration-free calcium aluminosilicate cement.

PubMed

Niu, Li-Na; Pei, Dan-Dan; Morris, Matthew; Jiao, Kai; Huang, Xue-Qing; Primus, Carolyn M; Susin, Lisiane F; Bergeron, Brian E; Pashley, David H; Tay, Franklin R

2016-10-01

An experimental discoloration-free calcium aluminosilicate cement has been developed with the intention of maximizing the beneficial attributes of tricalcium silicate cements and calcium aluminate cements. The present study examined the effects of this experimental cement (Quick-Set2) on the mineralogenic characteristics of osteogenic lineage-committed human dental pulp stem cells (hDPSCs), by comparing the cellular responses with a commercially available tricalcium silicate cement (white mineral trioxide aggregate (ProRoot(®) MTA); WMTA). The osteogenic potential of hDPSCs exposed to the cements was examined using qRT-PCR for osteogenic gene expressions, Western blot for osteogenic-related protein expressions, alkaline phosphatase enzyme activity, Alizarin red S staining, Fourier transform infrared spectroscopy and transmission electron microscopy of extracellular calcium deposits. Results of the six assays indicated that osteogenic differentiation of hDPSCs was significantly enhanced after exposure to the tricalcium silicate cement or the experimental calcium aluminosilicate cement, with the former demonstrating better mineralogenic stimulation capacity. The better osteogenic stimulating effect of the tricalcium silicate cement on hDPSCs may be due to its relatively higher silicate content, or higher OH(-) and Ca(2+) release. Further investigations with the use of in vivo animal models are required to validate the potential augmenting osteogenic effects of the experimental discoloration-free calcium aluminosilicate cement. Published by Elsevier Ltd.

Ni-Al phase transformation of dual layer coating prepared by pack cementation and electrodeposition

NASA Astrophysics Data System (ADS)

Afandi, A.; Sugiarti, E.; Ekaputra, R.; Sudiro, T.; Thosin, K. A. Z.

2018-03-01

In this work, Fe-Cr alloys were coated via Aluminum (Al) pack cementation, followed by Nickel (Ni) electrodeposition. The process of pack cementation was done with mixing powders of Al, Al203 and NH4Cl with weight percentage of 15%, 85%, and 5% respectively. To control successful Al diffusion to the substrate, pack cementation was conducted for 7 hours with two holding temperatures treatment at 400 °C for 4 hours, and 800 ° C hours for 2 hours. Subsequently, the electrodeposition of Ni was applied with the solution consisting of NiSO4, H3BO3, and NiCl2. The samples were placed in the cathode, and then dipped in the solutions, while Ni plate used as anode. Successfully the samples were coated by dual Al-Ni layers, the samples were slowly heat treated at 900 °C for 10 hours. The inter-diffusion of Al and Ni were characterized with SEM/EDX to investigate the distribution of the elements. Mechanical properties of the coated substrates were analyzed with Hardness Vickers (HV). It was found the hardness of the substrate increased significantly, from originally 255 HV to the 1177 HV after pack cementation. The hardness of the substrates has decreased to 641 HV after Ni plating, but subsequent heat treatment has been able to increase the hardness to 842 HV. This phenomenon can be correlated to the inward Al diffusion, and outward Fe, Cr diffusion. The formation of intermetallic compounds due to Al inward and Fe, Cr outward diffusion were discussed in details.

Pre-packed vacuum bone cement mixing systems. A further step in reducing methylmethacrylate exposure in surgery.

PubMed

Schlegel, Ulf J; Sturm, Michael; Eysel, Peer; Breusch, Steffen J

2010-11-01

Polymethylmethacrylate bone cements are widely used in orthopaedic and trauma surgery as well as in dentistry. The toxic side effects of inhaled methylmethacrylate (MMA) fumes generated during mixing have been well studied. Vacuum cement mixing systems have been shown to reduce the risk of airborne MMA significantly compared to handmixing. In an effort to further reduce MMA exposure, the latest generation of mixing devices are pre-packed with the ingredients and thus allow preparation in nearly closed circuits. Until now, there has been no study proofing the efficacy of those systems in protecting theatre staff from MMA vapours. A pre-packed vacuum mixing system (Optipac®) was compared with two standard systems (Palamix® and Easymix®) regarding MMA emission. The latter systems require loading with the bone cement compounds prior to mixing. Following a standardized procedure, 10 mixes were performed with each system and the emission of MMA vapours in the breathing zone was recorded using photoionization detection over a period of 3 min. The mean MMA exposure was reduced when using the pre-packed system compared to the devices that require filling with the components. The highest emission peaks were recorded during the mixing and preparation steps in all systems. Modern pre-packed vacuum mixing systems further help to reduce the occupational hazards created by bone cement preparation. However, MMA fumes can still be detected using this technique. Although this is an important step in reducing MMA exposure in the operating theatre, further technical effort has to be taken to eliminate the continuous leakage of monomer from the devices while mixing and to minimize necessary manipulation for final delivery.

Systemic effect of mineral aggregate-based cements: histopathological analysis in rats.

PubMed

Garcia, Lucas da Fonseca Roberti; Huck, Claudia; Magalhães, Fernando Augusto Cintra; Souza, Pedro Paulo Chaves de; Souza Costa, Carlos Alberto de

2017-01-01

Several studies reported the local tissue reaction caused by mineral aggregate-based cements. However, few studies have investigated the systemic effects promoted by these cements on liver and kidney when directly applied to connective tissue. The purpose of this in vivo study was to investigate the systemic effect of mineral aggregate-based cements on the livers and kidneys of rats. Samples of Mineral Trioxide Aggregate (MTA) and a calcium aluminate-based cement (EndoBinder) containing different radiopacifiers were implanted into the dorsum of 40 rats. After 7 and 30 d, samples of subcutaneous, liver and kidney tissues were submitted to histopathological analysis. A score (0-3) was used to grade the inflammatory reaction. Blood samples were collected to evaluate changes in hepatic and renal functions of animals. The moderate inflammatory reaction (2) observed for 7 d in the subcutaneous tissue decreased with time for all cements. The thickness of inflammatory capsules also presented a significant decrease with time (P<.05). Systemically, all cements caused adverse inflammatory reactions in the liver and kidney, being more evident for MTA, persisting until the end of the analysis. Liver functions increased significantly for MTA during 30 d (P<.05). The different cements induced to a locally limited inflammatory reaction. However, from the systemic point of view, the cements promoted significant inflammatory reactions in the liver and kidney. For MTA, the reactions were more accentuated.

Synthesis and hydration behavior of calcium zirconium aluminate (Ca{sub 7}ZrAl{sub 6}O{sub 18}) cement

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kang, Eun-Hee; Yoo, Jun-Sang; Kim, Bo-Hye

2014-02-15

Calcium zirconium aluminate (Ca{sub 7}ZrAl{sub 6}O{sub 18}) cements were prepared by solid state reaction and polymeric precursor methods, and their phase evolution, morphology, and hydration behavior were investigated. In polymeric precursor method, a nearly single phase Ca{sub 7}ZrAl{sub 6}O{sub 18} was obtained at relatively lower temperature (1200 °C) whereas in solid state reaction, a small amount of CaZrO{sub 3} coexisted with Ca{sub 7}ZrAl{sub 6}O{sub 18} even at higher temperature (1400 °C). Unexpectedly, Ca{sub 7}ZrAl{sub 6}O{sub 18} synthesized by polymeric precursor process was the large-sized and rough-shaped powder. The planetary ball milling was employed to control the particle size and shape.more » The hydration behavior of Ca{sub 7}ZrAl{sub 6}O{sub 18} was similar to that of Ca{sub 3}Al{sub 2}O{sub 6} (C3A), but the hydration products were Ca{sub 3}Al{sub 2}O{sub 6}·6H{sub 2}O (C3AH6) and several intermediate products. Thus, Zr (or ZrO{sub 2}) stabilized the intermediate hydration products of C3A.« less

Biocompatibility of new calcium aluminate cement (EndoBinder).

PubMed

Aguilar, Fabiano Gamero; Roberti Garcia, Lucas Fonseca; Panzeri Pires-de-Souza, Fernanda Carvalho

2012-03-01

The purpose of this study was to evaluate the biocompatibility of calcium aluminate cement (EndoBinder) in subcutaneous tissue of rats. Fifteen rats, weighing 300 g, were separated into 3 groups (n = 5) in accordance with the time of death (7, 21, 42 days). Two incisions were made in the dorsal subcutaneous tissue of each rat in which were implanted 2 polyethylene tubes filled with the test materials, EndoBinder (EB) and Grey MTA (GMTA). The external tube walls were considered the negative control group (CG). After 7, 21, and 42 days, animals were killed, obtaining 5 samples per group, at each time interval of analysis. From the morphologic and morphometric analyses by using a score of (0-3) (50, 100, and 400×), results showed absence of inflammatory reaction (0) for EB after 42 days. However, for GMTA, a slight inflammatory reaction (1) was observed after 42 days, which means the persistence of a chronic inflammatory process. When compared with CG, tissue reaction ranging from discrete (1-7 days) to absent (0-42 days) was observed. EndoBinder presented satisfactory tissue reaction; it was biocompatible when tested in subcutaneous tissue of rats. Copyright © 2012 American Association of Endodontists. Published by Elsevier Inc. All rights reserved.

Development of an Improved Cement for Geothermal Wells

DOE Office of Scientific and Technical Information (OSTI.GOV)

Trabits, George

2015-04-20

After an oil, gas, or geothermal production well has been drilled, the well must be stabilized with a casing (sections of steel pipe that are joined together) in order to prevent the walls of the well from collapsing. The gap between the casing and the walls of the well is filled with cement, which locks the casing into place. The casing and cementing of geothermal wells is complicated by the harsh conditions of high temperature, high pressure, and a chemical environment (brines with high concentrations of carbon dioxide and sulfuric acid) that degrades conventional Portland cement. During the 1990s andmore » early 2000s, the U.S. Department of Energy’s Geothermal Technologies Office (GTO) provided support for the development of fly-ash-modified calcium aluminate phosphate (CaP) cement, which offers improved resistance to degradation compared with conventional cement. However, the use of CaP cements involves some operational constraints that can increase the cost and complexity of well cementing. In some cases, CaP cements are incompatible with chemical additives that are commonly used to adjust cement setting time. Care must also be taken to ensure that CaP cements do not become contaminated with leftover conventional cement in pumping equipment used in conventional well cementing. With assistance from GTO, Trabits Group, LLC has developed a zeolite-containing cement that performs well in harsh geothermal conditions (thermal stability at temperatures of up to 300°C and resistance to carbonation) and is easy to use (can be easily adjusted with additives and eliminates the need to “sterilize” pumping equipment as with CaP cements). This combination of properties reduces the complexity/cost of well cementing, which will help enable the widespread development of geothermal energy in the United States.« less

A Twofold Comparison between Dual Cure Resin Modified Cement and Glass Ionomer Cement for Orthodontic Band Cementation.

PubMed

Attar, Hanaa El; Elhiny, Omnia; Salem, Ghada; Abdelrahman, Ahmed; Attia, Mazen

2016-12-15

To test the solubility of dual cure resin modified resin cement in a food simulating solution and the shear bond strength compared to conventional Glass ionomer cement. The materials tested were self-adhesive dual cure resin modified cement and Glass Ionomer (GIC). Twenty Teflon moulds were divided into two groups of tens. The first group was injected and packed with the modified resin cement, the second group was packed with GIC. To test the solubility, each mould was weighed before and after being placed in an analytical reagent for 30 days. The solubility was measured as the difference between the initial and final drying mass. To measure the Shear bond strength, 20 freshly extracted wisdom teeth were equally divided into two groups and embedded in self-cure acrylic resin. Four mm sections of stainless steel bands were cemented to the exposed buccal surfaces of teeth under a constant load of 500 g. Shear bond strength was measured using a computer controlled materials testing machine and the load required to deband the samples was recorded in Newtons. GIC showed significantly higher mean weight loss and an insignificant lower Shear bond strength, compared to dual cure resin Cement. It was found that dual cure resin modified cement was less soluble than glass ionomer cement and of comparable bond strength rendering it more useful clinically for orthodontic band cementation.

Development of the Use of Alternative Cements for the Treatment of Intermediate Level Waste

DOE Office of Scientific and Technical Information (OSTI.GOV)

Hayes, M.; Godfrey, I.H.

2007-07-01

This paper describes initial development studies undertaken to investigate the potential use of alternative, non ordinary Portland cement (OPC) based encapsulation matrices to treat historic legacy wastes within the UK's Intermediate Level Waste (ILW) inventory. Currently these wastes are encapsulated in composite OPC cement systems based on high replacement with blast furnace slag of pulverised fuel ash. However, the high alkalinity of these cements can lead to high corrosion rates with reactive metals found in some wastes releasing hydrogen and forming expansive corrosion products. This paper therefore details preliminary results from studies on two commercial products, calcium sulfo-aluminate (CSA) andmore » magnesium phosphate (MP) cement which react with a different hydration chemistry, and which may allow wastes containing these metals to be encapsulated with lower reactivity. The results indicate that grouts can be formulated from both cements over a range of water contents and reactant ratios that have significantly improved fluidity in comparison to typical OPC cements. All designed mixes set in 24 hours with zero bleed and the pH values in the plastic state were in the range 10-11 for CSA and 5-7 for MP cements. In addition, a marked reduction in aluminium corrosion rate has been observed in both types of cements compared to a composite OPC system. These results therefore provide encouragement that both cement types can provide a possible alternative to OPC in the immobilisation of reactive wastes, however further investigation is needed. (authors)« less

New manufacturing method for Fe-Si magnetic powders using modified pack-cementation process

NASA Astrophysics Data System (ADS)

Byun, Ji Young; Kim, Jang Won; Han, Jeong Whan; Jang, Pyungwoo

2013-03-01

This paper describes a new method for making Fe-Si magnetic powders using a pack-cementation process. It was found that Fe-Si alloy powders were formed by a reaction of the pack mixture of Fe, Si, NaF, and Al2O3 powders at 900 °C for 24 h under a hydrogen atmosphere. Separation of the Fe-Si alloy powders was dependent on the particle size of the Fe powders in the pack. For small Fe powders, magnetic separation in a medium of strong alkali solution was recommended. But, for relatively larger Fe powders, the Fe-Si alloy powders were easily separated from Al2O3 powders using a magnet in air atmosphere. The Si content in the Fe-Si magnetic powders were easily controlled by changing the weight ratio of Si to (Si+Fe) in the pack.

Acoustic probing of elastic behavior and damage in weakly cemented granular media

NASA Astrophysics Data System (ADS)

Langlois, V.; Jia, X.

2014-02-01

We investigate the elastic behavior and damage of weakly cemented granular media under external load with ultrasound. The cementation controlled experiments are performed by freezing the capillary liquid at the bead contact in a dense glass or polymeric [poly(methyl methacrylate)] bead pack wet by tetradecane of volume fraction ϕ = 0.1%-4%. When the pendular rings are solidified, an abrupt increase by a factor of 2 in the compressional wave velocity is observed. We interpret the data in terms of effective medium models in which the contact stiffnesses are derived by either a bonded contact model [P. J. Digby, J. Appl. Mech. 48, 803 (1981), 10.1115/1.3157738] or a cemented contact model [J. Dvorkin, A. Nur, and H. Yin, Mech. Mater. 18, 351 (1994), 10.1016/0167-6636(94)90044-2]. The former fails to quantitatively account for the results with a soft cement relative to the grain, whereas the latter considering the mechanical properties of the cement does apply. Moreover, we monitor the irreversible behavior of the cemented granular packs under moderate uniaxial loading (<1.3 MPa) with the correlation method of ultrasound scattering. The damage of the cemented materials is accompanied by a compressional wave velocity decrease up to 60%, likely due to the fractures induced at the grain-cement interfaces.

Systemic effect of mineral aggregate-based cements: histopathological analysis in rats

PubMed Central

Garcia, Lucas da Fonseca Roberti; Huck, Claudia; Magalhães, Fernando Augusto Cintra; de Souza, Pedro Paulo Chaves; de Souza Costa, Carlos Alberto

2017-01-01

Abstract Objective: Several studies reported the local tissue reaction caused by mineral aggregate-based cements. However, few studies have investigated the systemic effects promoted by these cements on liver and kidney when directly applied to connective tissue. The purpose of this in vivo study was to investigate the systemic effect of mineral aggregate-based cements on the livers and kidneys of rats. Material and Methods: Samples of Mineral Trioxide Aggregate (MTA) and a calcium aluminate-based cement (EndoBinder) containing different radiopacifiers were implanted into the dorsum of 40 rats. After 7 and 30 d, samples of subcutaneous, liver and kidney tissues were submitted to histopathological analysis. A score (0-3) was used to grade the inflammatory reaction. Blood samples were collected to evaluate changes in hepatic and renal functions of animals. Results: The moderate inflammatory reaction (2) observed for 7 d in the subcutaneous tissue decreased with time for all cements. The thickness of inflammatory capsules also presented a significant decrease with time (P<.05). Systemically, all cements caused adverse inflammatory reactions in the liver and kidney, being more evident for MTA, persisting until the end of the analysis. Liver functions increased significantly for MTA during 30 d (P<.05). Conclusion: The different cements induced to a locally limited inflammatory reaction. However, from the systemic point of view, the cements promoted significant inflammatory reactions in the liver and kidney. For MTA, the reactions were more accentuated. PMID:29211283

Calcium sulfoaluminate cement blended with OPC: A potential binder to encapsulate low-level radioactive slurries of complex chemistry

DOE Office of Scientific and Technical Information (OSTI.GOV)

Cau Dit Coumes, Celine; Courtois, Simone; Peysson, Sandrine

Investigations were carried out in order to solidify in cement a low-level radioactive waste of complex chemistry obtained by mixing two process streams, a slurry produced by ultra-filtration and an evaporator concentrate with a salinity of 600 gxL{sup -1}. Direct cementation with Portland cement (OPC) was not possible due to a very long setting time of cement resulting from borates and phosphates contained in the waste. According to a classical approach, this difficulty could be solved by pre-treating the waste to reduce adverse cement-waste interactions. A two-stage process was defined, including precipitation of phosphates and sulfates at 60 deg. Cmore » by adding calcium and barium hydroxide to the waste stream, and encapsulation with a blend of OPC and calcium aluminate cement (CAC) to convert borates into calcium quadriboroaluminate. The material obtained with a 30% waste loading complied with specifications. However, the pre-treatment step made the process complex and costly. A new alternative was then developed: the direct encapsulation of the waste with a blend of OPC and calcium sulfoaluminate cement (CSA) at room temperature. Setting inhibition was suppressed, which probably resulted from the fact that, when hydrating, CSA cement formed significant amounts of ettringite and calcium monosulfoaluminate hydrate which incorporated borates into their structure. As a consequence, the waste loading could be increased to 56% while keeping acceptable properties at the laboratory scale.« less

DOE Office of Scientific and Technical Information (OSTI.GOV)

Pyatina, Tatiana; Sugama, Toshifumi; Moon, Juhyuk

An alkali-activated blend of aluminum cement and class F fly ash is an attractive solution for geothermal wells where cement is exposed to significant thermal shocks and aggressive environments. Set-control additives enable the safe cement placement in a well but may compromise its mechanical properties. Here, this work evaluates the effect of a tartaric-acid set retarder on phase composition, microstructure, and strength development of a sodium-metasilicate-activated calcium aluminate/fly ash class F blend after curing at 85 °C, 200 °C or 300 °C. The hardened materials were characterized with X-ray diffraction, thermogravimetric analysis, X-ray computed tomography, and combined scanning electron microscopy/energy-dispersivemore » X-ray spectroscopy and tested for mechanical strength. With increasing temperature, a higher number of phase transitions in non-retarded specimens was found as a result of fast cement hydration. The differences in the phase compositions were also attributed to tartaric acid interactions with metal ions released by the blend in retarded samples. The retarded samples showed higher total porosity but reduced percentage of large pores (above 500 µm) and greater compressive strength after 300 °C curing. Lastly, mechanical properties of the set cements were not compromised by the retarder.« less

A Twofold Comparison between Dual Cure Resin Modified Cement and Glass Ionomer Cement for Orthodontic Band Cementation

PubMed Central

Attar, Hanaa El; Elhiny, Omnia; Salem, Ghada; Abdelrahman, Ahmed; Attia, Mazen

2016-01-01

AIM: To test the solubility of dual cure resin modified resin cement in a food simulating solution and the shear bond strength compared to conventional Glass ionomer cement. MATERIALS AND METHOD: The materials tested were self-adhesive dual cure resin modified cement and Glass Ionomer (GIC). Twenty Teflon moulds were divided into two groups of tens. The first group was injected and packed with the modified resin cement, the second group was packed with GIC. To test the solubility, each mould was weighed before and after being placed in an analytical reagent for 30 days. The solubility was measured as the difference between the initial and final drying mass. To measure the Shear bond strength, 20 freshly extracted wisdom teeth were equally divided into two groups and embedded in self-cure acrylic resin. Four mm sections of stainless steel bands were cemented to the exposed buccal surfaces of teeth under a constant load of 500 g. Shear bond strength was measured using a computer controlled materials testing machine and the load required to deband the samples was recorded in Newtons. RESULTS: GIC showed significantly higher mean weight loss and an insignificant lower Shear bond strength, compared to dual cure resin Cement. CONCLUSION: It was found that dual cure resin modified cement was less soluble than glass ionomer cement and of comparable bond strength rendering it more useful clinically for orthodontic band cementation. PMID:28028417

Interactions between chloride and cement-paste materials.

PubMed

Barberon, Fabien; Baroghel-Bouny, Véronique; Zanni, Hélène; Bresson, Bruno; d'Espinose de la Caillerie, Jean-Baptiste; Malosse, Lucie; Gan, Zehong

2005-02-01

The durability of cement-based materials with respect to exterior aggressions is one of the current priorities in civil engineering. Depending on their use, the cement-based materials can be exposed to different types of aggressive environments. For instance, damages to concrete structures in contact with a saline environment (sea water on bridges, deicing salts on roads, etc.) are of utmost importance. Upon exposure to saline water, Cl- ions penetrate into the structures and subsequently lead to reinforcement corrosion. Chloride attack is often combined with other aggressive influences such as temperature (e.g., freezing) or the ingress of other ions (e.g., sulfates in sea water). We therefore aim to explore the effect of sodium chloride (NaCl) on the structural chemistry of cement paste. Existing studies about reinforcement corrosion by chloride have focused on the penetration of Cl- ions and the comparison between "free" ions (water-soluble ions) and bound ones. However, little is known about the fixation mechanisms, the localization of Cl in the cement matrix and the structural interaction between Cl and the silicate and aluminate hydrate phases present in cement paste. We present here results of a multinuclear nuclear magnetic resonance study on the fixation of chloride in the hydration products and the characterization of new phases potentially appearing due to chloride ingress.

Spectroscopy of Loose and Cemented Sulfate-Bearing Soils: Implications for Duricrust on Mars

NASA Astrophysics Data System (ADS)

Cooper, Christopher D.; Mustard, John F.

2002-07-01

The goal of this work is to determine the spectroscopic properties of sulfate in martian soil analogs over the wavelength range 0.3 to 25 μm (which is relevant to existing and planned remotely sensed data sets for Mars). Sulfate is an abundant component of martian soil (up to 9% SO 3 by weight) and apparently exists as a particulate in the soil but also as a cement. Although previous studies have addressed the spectroscopic identity of sulfates on Mars, none have used laboratory mixtures of materials with sulfates at the abundances measured by landed spacecraft, nor have any works considered the effect of salt-cementation on spectral properties of soil materials. For this work we created mixtures of a palagonitic soil (JSC Mars-1) and sulfates (MgSO 4 and CaSO 4·2H 2O). The effects of cementation were determined and separated from the effects of packing and hydration by measuring the samples as loose powders, packed powders, cemented materials, and disaggregated materials. The results show that the presence of particulate sulfate is best observed in the 4-5 μm region. Soils cemented with sulfate exhibit a pronounced restrahlen band between 8 and 9 μm as well as well-defined absorptions in the 4-5 μm region. Cementation effects are distinct from packing effects and disaggregation of cemented samples rapidly diminishes the strength of the restrahlen bands. The results of this study show that sulfate in loose materials is more detectable in the near infrared (4-5 μm) than in the thermal infrared (8-9 μm). However, cemented materials are easily distinguished from loose mixtures in the thermal infrared because of the high values of their absorption coefficient in this region. Together these results suggest that both wavelength regions are important for determining the spatial extent and physical form of sulfates on the surface of Mars.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Moeschner, Goeril; Lothenbach, Barbara; Figi, Renato

Citric acid can be used to retard the hydration of cement. Experiments were carried out to investigate the influence of citric acid on the composition of solid and liquid phases during cement hydration. Analyses of the solid phases showed that dissolution of alite and aluminate slowed down while analyses of the pore solution showed that citric acid was removed almost completely from the pore solution within the first hours of hydration. The complexation of the ions by citrate was weak, which could also be confirmed by thermodynamic calculations. Only 2% of the dissolved Ca and 0.001% of the dissolved Kmore » formed complexes with citrate during the first hours. Thus, citric acid retards cement hydration not by complex formation, but by slowing down the dissolution of the clinker grains. Thermodynamic calculations did not indicate precipitation of a crystalline citrate species. Thus, it is suggested that citrate sorbed onto the clinker surface and formed a protective layer around the clinker grains retarding their dissolution.« less

High-Temperature Self-Healing and Re-Adhering Geothermal Well Cement Composites

NASA Astrophysics Data System (ADS)

Pyatina, T.; Sugama, T.; Boodhan, Y.; Nazarov, L.

2017-12-01

Self-healing cementitious materials are particularly attractive for the cases where damaged areas are difficult to locate and reach. High-temperature geothermal wells with aggressive environments impose most difficult conditions on cements that must ensure durable zonal isolation under repeated thermal, chemical and mechanical stresses. The present work evaluates matrix and carbon steel (CS) - cement interface self-healing and re-adhering properties of various inorganic cementitious composites under steam, alkali carbonate or brine environments at 270-300oC applicable to geothermal wells. The composite materials included blends based on Ordinary Portland Cement (OPC) and natural zeolites and alkali or phosphate activated composites of Calcium Aluminate Cement (CAC) with fly ash, class F. Class G cement blend with crystalline silica was used as a baseline. Compressive-strength and bond-strength recoveries were examined to evaluate self-healing and re-adhering properties of the composites after repeated crush tests followed by 5-day healing periods in these environments. The optical and scanning electron microscopes, X-ray diffraction, Fourier Transform infrared, Raman spectroscopy and EDX measurements were used to identify phases participating in the strengths recoveries and cracks filling processes. Amorphous silica-rich- and small-size crystalline phases played an important role in the healing of the tested composites in all environments. Possible ways to enhance self-healing properties of cementitious composites under conditions of geothermal wells were identified.

Microstructural characterization of dental zinc phosphate cements using combined small angle neutron scattering and microfocus X-ray computed tomography.

PubMed

Viani, Alberto; Sotiriadis, Konstantinos; Kumpová, Ivana; Mancini, Lucia; Appavou, Marie-Sousai

2017-04-01

To characterize the microstructure of two zinc phosphate cement formulations in order to investigate the role of liquid/solid ratio and composition of powder component, on the developed porosity and, consequently, on compressive strength. X-ray powder diffraction with the Rietveld method was used to study the phase composition of zinc oxide powder and cements. Powder component and cement microstructure were investigated with scanning electron microscopy. Small angle neutron scattering (SANS) and microfocus X-ray computed tomography (XmCT) were together employed to characterize porosity and microstructure of dental cements. Compressive strength tests were performed to evaluate their mechanical performance. The beneficial effects obtained by the addition of Al, Mg and B to modulate powder reactivity were mitigated by the crystallization of a Zn aluminate phase not involved in the cement setting reaction. Both cements showed spherical pores with a bimodal distribution at the micro/nano-scale. Pores, containing a low density gel-like phase, developed through segregation of liquid during setting. Increasing liquid/solid ratio from 0.378 to 0.571, increased both SANS and XmCT-derived specific surface area (by 56% and 22%, respectively), porosity (XmCT-derived porosity increased from 3.8% to 5.2%), the relative fraction of large pores ≥50μm, decreased compressive strength from 50±3MPa to 39±3MPa, and favored microstructural and compositional inhomogeneities. Explain aspects of powder design affecting the setting reaction and, in turn, cement performance, to help in optimizing cement formulation. The mechanism behind development of porosity and specific surface area explains mechanical performance, and processes such as erosion and fluoride release/uptake. Copyright © 2017 The Authors. Published by Elsevier Ltd.. All rights reserved.

The bipolar plate of AISI 1045 steel with chromized coatings prepared by low-temperature pack cementation for proton exchange membrane fuel cell

NASA Astrophysics Data System (ADS)

Bai, Ching-Yuan; Wen, Tse-Min; Hou, Kung-Hsu; Ger, Ming-Der

The low-temperature pack chromization, a reforming pack cementation process, is employed to modify AISI 1045 steel for the application of bipolar plates in PEMFC. The process is conducted to yield a coating, containing major Cr-carbides and minor Cr-nitrides, on the substrate in view of enhancing the steel's corrosion resistance and lowering interfacial contact resistance between the bipolar plate and gas diffusion layer. Electrical discharge machining and rolling approach are used as the pretreatment to produce an activated surface on the steel before pack chromization process to reduce operating temperatures and increase deposition rates. The rolled-chromized steel shows the lowest corrosion current density, 3 × 10 -8 A cm -2, and the smallest interfacial contact resistance, 5.9 mΩ cm 2, at 140 N cm -2 among all tested steels. This study clearly states the performance of 1045 carbon steel modified by activated and low-temperature pack chromization processes, which possess the potential to be bipolar plates in the application of PEMFC.

Biodeterioration of the Cement Composites

NASA Astrophysics Data System (ADS)

Luptáková, Alena; Eštoková, Adriana; Mačingová, Eva; Kovalčíková, Martina; Jenčárová, Jana

2016-10-01

The destruction of natural and synthetic materials is the spontaneous and irreversible process of the elements cycling in nature. It can by accelerated or decelerated by physical, chemical and biological influences. Biological influences are represented by the influence of the vegetation and microorganisms (MO). The destruction of cement composites by different MO through the diverse mechanisms is entitled as the concrete biodeterioration. Several sulphur compounds and species of MO are involved in this complex process. Heterotrophic and chemolithotrophic bacteria together with fungi have all been found in samples of corroding cement composites. The MO involved in the process metabolise the presented sulphur compounds (hydrogen sulphide, elemental sulphur etc.) to sulphuric acid reacting with concrete. When sulphuric acid reacts with a concrete matrix, the first step involves a reaction between the acid and the calcium hydroxide forming calcium sulphate. This is subsequently hydrated to form gypsum, the appearance of which on the surface of concrete pipes takes the form of a white, mushy substance which has no cohesive properties. In the continuing attack, the gypsum would react with the calcium aluminate hydrate to form ettringite, an expansive product. The use supplementary cementing composite materials have been reported to improve the resistance of concrete to biodeterioration. The aim of this work was the study of the cement composites biodeterioration by the bacteria Acidithiobacillus thiooxidans. Experimental works were focused on the comparison of special cement composites and its resistance affected by the activities of used sulphur-oxidising

Characterization of the mechanical behavior of sea ice as a frictional material

NASA Astrophysics Data System (ADS)

Lade, Poul V.

2002-12-01

The mechanical properties of sea ice are determined by the formation process, and the consequent material behavior at the element scale exhibits viscoelastic behavior at the early loading stages, followed by brittle fracture or ductile, irrecoverable deformation that may be captured by hardening/softening plasticity models with nonassociated flow. Failure of sea ice under different loading conditions follows a pattern that demonstrates its highly cross-anisotropic nature as well as its behavior as a frictional material. The interactions between the floes in the pack ice resemble those observed in granular materials. These materials are frictional in nature, they exhibit both contractive and dilative volume changes, the plastic flow is nonassociated, and their stiffnesses and strengths increase with confining pressure, but they do not have any strength when unconfined. The overall behavior of the pack ice may be close to isotropic. Constitutive modeling of this behavior may be achieved by models used in geotechnical engineering. Formation of leads and subsequent freezing of the water results in cementation between the ice floes, and the pack ice becomes stronger. The behavior of the pack ice may now be compared with that observed in cemented soils or concrete. For these materials, increasing amounts of cementation result in increasing rates of dilation when sheared, and this accounts for the largest contribution to the increase in shear strength.

DEVELOPMENT OF A CALCIUM-BASED SORBENT FOR HOT GAS CLEANUP

DOE Office of Scientific and Technical Information (OSTI.GOV)

T.D. Wheelock; L.K. Doraiswamy; K. Constant

1999-10-01

The development and testing of potential calcium-based sorbents for hot gas cleanup continued. One of the most promising materials combines powdered limestone and a calcium aluminate cement by two step pelletization followed by steam curing. Reasonably strong pellets are produced with good adsorption characteristics by incorporating 20 wt.% cement in the core and 40 wt.% cement in the shell. The resulting 4.76 mm diameter pellets are capable of withstanding a crushing force approaching 11.5 N/mm before breaking and are also capable of removing H{sub 2}S from dilute, hot gas streams. The pellets are also regenerable and reusable. Another promising materialmore » combines calcium carbonate powder and finely ground calcined alumina in tablet form. The small tablets are prepared by mixing the materials with water to form a thick paste which is then molded and dried. The tablets are hardened by calcining at either 1000 to 1100 C. The resulting tablets are strong and capable of removing H{sub 2}S from a dilute, hot gas stream.« less

Spheroidization of glass powders for glass ionomer cements.

PubMed

Gu, Y W; Yap, A U J; Cheang, P; Kumar, R

2004-08-01

Commercial angular glass powders were spheroidized using both the flame spraying and inductively coupled radio frequency plasma spraying techniques. Spherical powders with different particle size distributions were obtained after spheroidization. The effects of spherical glass powders on the mechanical properties of glass ionomer cements (GICs) were investigated. Results showed that the particle size distribution of the glass powders had a significant influence on the mechanical properties of GICs. Powders with a bimodal particle size distribution ensured a high packing density of glass ionomer cements, giving relatively high mechanical properties of GICs. GICs prepared by flame-spheroidized powders showed low strength values due to the loss of fine particles during flame spraying, leading to a low packing density and few metal ions reacting with polyacrylic acid to form cross-linking. GICs prepared by the nano-sized powders showed low strength because of the low bulk density of the nano-sized powders and hence low powder/liquid ratio of GICs.

Hydration states of AFm cement phases

DOE Office of Scientific and Technical Information (OSTI.GOV)

Baquerizo, Luis G., E-mail: luis.baquerizoibarra@holcim.com; Matschei, Thomas; Scrivener, Karen L.

2015-07-15

The AFm phase, one of the main products formed during the hydration of Portland and calcium aluminate cement based systems, belongs to the layered double hydrate (LDH) family having positively charged layers and water plus charge-balancing anions in the interlayer. It is known that these phases present different hydration states (i.e. varying water content) depending on the relative humidity (RH), temperature and anion type, which might be linked to volume changes (swelling and shrinkage). Unfortunately the stability conditions of these phases are insufficiently reported. This paper presents novel experimental results on the different hydration states of the most important AFmmore » phases: monocarboaluminate, hemicarboaluminate, strätlingite, hydroxy-AFm and monosulfoaluminate, and the thermodynamic properties associated with changes in their water content during absorption/desorption. This data opens the possibility to model the response of cementitious systems during drying and wetting and to engineer systems more resistant to harsh external conditions.« less

Oxidation of Slurry Aluminide Coatings on Cast Stainless Steel Alloy CF8C-Plus at 800oC in Water Vapor

DOE Office of Scientific and Technical Information (OSTI.GOV)

Haynes, James A; Armstrong, Beth L; Dryepondt, Sebastien N

A new, cast austenitic stainless steel, CF8C-Plus, has been developed for a wide range of high temperature applications, including diesel exhaust components, turbine casings and turbocharger housings. CF8C-Plus offers significant improvements in creep rupture life and creep rupture strength over standard CF8C steel. However, at higher temperatures and in more aggressive environments, such as those containing significant water vapor, an oxidation-resistant protective coating will be necessary. The oxidation behavior of alloys CF8C and CF8C-Plus with various aluminide coatings were compared at 800oC in air plus 10 vol% water vapor. Due to their affordability, slurry aluminides were the primary coating systemmore » of interest, although chemical vapor deposition (CVD) and pack cementation coatings were also compared. Additionally, a preliminary study of the low cycle fatigue behavior of aluminized CF8C-Plus was conducted at 800oC. Each type of coating provided substantial improvements in oxidation behavior, with simple slurry aluminides showing very good oxidation resistance after 4,000 h testing in water vapor. Preliminary low cycle fatigue results indicated that thicker aluminide coatings degraded high temperature fatigue properties of CF8C-Plus, whereas thinner coatings did not. Results suggest that appropriately designed slurry aluminide coatings are a viable option for economical, long-term oxidation protection of austenitic stainless steels in water vapor.« less

Active mineral additives of sapropel ashes

NASA Astrophysics Data System (ADS)

Khomich, V. A.; Danilina, E. V.; Krivonos, O. I.; Plaksin, G. V.

2015-01-01

The goal of the presented research is to establish a scientific rational for the possibility of sapropel ashes usage as an active mineral additive. The research included the study of producing active mineral additives from sapropels by their thermal treatment at 850900 °C and afterpowdering, the investigation of the properties of paste matrix with an ash additive, and the study of the ash influence on the cement bonding agent. Thermogravimetric analysis and X-ray investigations allowed us to establish that while burning, organic substances are removed, clay minerals are dehydrated and their structure is broken. Sapropel ashes chemical composition was determined. An amorphous ash constituent is mainly formed from silica of the mineral sapropel part and alumosilicagels resulted from clay minerals decomposition. Properties of PC 400 and PC 500A0 sparopel ash additives were studied. Adding ashes containing Glenium plasticizer to the cement increases paste matrix strength and considerably reduces its water absorption. X-ray phase analysis data shows changes in the phase composition of the paste matrix with an ash additive. Ash additives produce a pozzolanic effect on the cement bonding agent. Besides, an ash additive due to the alumosilicagels content causes transformation from unstable calcium aluminate forms to the stable ones.

Method for molding threads in graphite panels

DOEpatents

Short, W.W.; Spencer, C.

1994-11-29

A graphite panel with a hole having a damaged thread is repaired by drilling the hole to remove all of the thread and making a new hole of larger diameter. A bolt with a lubricated thread is placed in the new hole and the hole is packed with graphite cement to fill the hole and the thread on the bolt. The graphite cement is cured, and the bolt is unscrewed therefrom to leave a thread in the cement which is at least as strong as that of the original thread. 8 figures.

Effect of temperature on the durability of class C fly ash belite cement in simulated radioactive liquid waste: synergy of chloride and sulphate ions.

PubMed

Guerrero, A; Goñi, S; Allegro, V R

2009-06-15

The durability of class C fly ash belite cement (FABC-2-W) in simulated radioactive liquid waste (SRLW) rich in a mixed sodium chloride and sulphate solution is presented here. The effect of the temperature and potential synergic effect of chloride and sulfate ions are discussed. This study has been carried out according to the Koch-Steinegger test, at the temperature of 20 degrees C and 40 degrees C during a period of 180 days. The durability has been evaluated by the changes of the flexural strength of mortar, fabricated with this cement, immersed in a simulated radioactive liquid waste rich in sulfate (0.5M), chloride (0.5M) and sodium (1.5M) ions--catalogued like severely aggressive for the traditional Portland cement--and demineralised water, which was used as reference. The reaction mechanism of sulphate, chloride and sodium ions with the mortar was evaluated by scanning electron microscopy (SEM), porosity and pore-size distribution, and X-ray diffraction (XRD). The results showed that the chloride binding and formation of Friedel's salt was inhibited by the presence of sulphate. Sulphate ion reacts preferentially with the calcium aluminate hydrates forming non-expansive ettringite which precipitated inside the pores; the microstructure was refined and the mechanical properties enhanced. This process was faster and more marked at 40 degrees C.

CHEMICALLY BONDED CEMENTS FROM BOILER ASH AND SLUDGE WASTES. PHASE II REPORT, SEPT.1998-JULY 1999.

DOE Office of Scientific and Technical Information (OSTI.GOV)

SUGAMA,T.YAGER,K.A.BLANKENHORN,D.

1999-08-01

Based upon the previous Phase I research program aimed at looking for ways of recycling the KeySpan-generated wastes, such as waste water treatment sludge (WWTS) and bottom ash (BA), into the potentially useful cementitious materials called chemically bonded cement (CBC) materials, the emphasis of this Phase II program done at Brookhaven National Laboratory, in a period of September 1998 through July 1999, was directed towards the two major subjects: One was to assess the technical feasibility of WWTS-based CBC material for use as Pb-exchange adsorbent (PEA) which remediates Pb-contaminated soils in the field; and the other was related to themore » establishment of the optimum-packaging storage system of dry BA-based CBC components that make it a promising matrix material for the steam-cured concrete products containing sand and coarse aggregate. To achieve the goal of the first subject, a small-scale field demonstration test was carried out. Using the PEA material consisting of 30 wt% WWTS, 13 wt% Type I cement and 57 wt% water, the PES slurry was prepared using a rotary shear concrete mixer, and then poured on the Pb-contaminated soil. The PEA-to-soil ratio by weight was a factor of 2.0. The placed PEA slurry was blended with soil using hand mixing tools such as claws and shovels. The wettability of soils with the PEA was very good, thereby facilitating the soil-PEA mix procedures. A very promising result was obtained from this field test; in fact, the mount of Pb leached out from the 25-day-aged PEA-treated soil specimen was only 0.74 mg/l, meeting the requirement for EPA safe regulation of < 5 mg/l. In contrast, a large amount (26.4 mg/l) of Pb was detected from the untreated soil of the same age. Thus, this finding demonstrated that the WWTS-based CBC has a potential for use as PEA material. Regarding the second subject, the dry-packed storage system consisting of 68.7 wt% BA, 13.0 wt% calcium aluminate cement (CAC), 13.0 wt% Type I portland cement and 5.3 wt% sodium polyphosphate (NaP), was designed in response to the identification of the most effective CBC formulation in strengthening the steam-cured concrete specimens. Using this storage system with the material cost of 6.32 cents/lb, the 80 C-20 hour-steam-cured concrete specimens displayed the compressive strength of 3980 psi, tensile splitting of 416 psi, flexural strength of 808 psi, and modulus of elasticity of 3.16 x 10{sup 6} psi. Furthermore, the specimens had a good resistance to acid erosion and a lower permeability of water, compared with those of the conventional Type I cement concrete specimens. Consequently, the cost-effective BA-based CBC gave the promise of being a potentially useful material for fabricating high-performance precast concrete products, such as building blocks, pipes, and slabs.« less

Design and development of advanced castable refractory materials

NASA Astrophysics Data System (ADS)

Davis, Robert Bruce

New formulations of castable refractory composite materials were studied. This technology is used to produce low cost composite concrete structures designed for high temperature stability, superior wear resistance and improved strength. An in situ fired, castable cement installation is a heterogeneous structure divided into three zones according to the temperature history and microstructure. The properties of each zone depend on the predominant bonding mode between constituents. Each zone has a characteristic microstructure that influences the integrity of the monolith. The hot side may have a highly dense and developed network of ceramic bonds between constituent particles while the cold side may never reach temperatures sufficient to drive off free water. The thermal, structural and tribological properties depend on the microstructure and the type of bonding that holds the monolith together. The phase distributions are defined by sets of metastable phase conditions driven by the local hydrated chemistry, nearest neighbor oxide compounds, impurities and sintering temperature. Equilibrium phase diagrams were used to select optimum compositions based on higher melting point phases. The phase diagrams were also used to target high temperature phase fields that are stable over wide temperature and stoichiometric ranges. Materials selection of candidate hydraulic clinkers, high temperature oxides, and reinforcement phases were based on requirements for high temperature stability. The calcium aluminate (CaO-Al2O3) and calcium dialuminate (CaO-(Al2O3)2) are common refractory clinkers used in castable refractory cements. The thermodynamics and kinetics of cement hydrate formation are well studied and suited to become the building block of a design for a superior refractory castable cement. The inert oxides mixed with the calcium aluminate clinkers are magnesia (MgO), alumina (Al 2O3), spinel (MgAl2O4) and chromic (Cr2O3). The bulk of the experiments concentrated in the Al2O3--MgO--CaO ternary system. Materials selection criteria for reinforcement materials was based on improved high temperature stability, increased strength, reduced thermal expansion mismatch, low thermal conductivity and increasing wear resistance. The reinforcement phases selected for this investigation are zircon (ZrSiO4), zirconia (ZrO2), spinel (MgAl2O4) and dead burnt magnesia (MgO). Batches of the formulations were tested for thermal conductivity, wear resistance and mechanical strength. Relative rankings of the formulations against commercial products indicate improved or similar performance with increased maximum temperature limits and improved thermal insulating power. The new cement formulations proved to exhibit superior high temperature stability with an increasing volume fraction of high temperature oxides. The addition of reinforcement aggregates and powder sizing to offset the loss of strength. The room temperature compression strength and wear resistance of the optimized formulations exceeded the properties of conventional refractory, brick and castable cement tested concurrently.

Composition and microstructure of MTA and Aureoseal Plus: XRF, EDS, XRD and FESEM evaluation.

PubMed

Cianconi, L; Palopoli, P; Campanella, V; Mancini, M

2016-12-01

The aim of this study was to determine the chemical composition and the phases' microstructure of Aureoseal Plus (OGNA, Italy) and ProRoot MTA (Dentsply Tulsa Dental, USA) and to compare their characteristics. Study Design: Comparing Aureoseal Plus and ProRoot MTA microstructure by means of several analyses type. The chemical analysis of the two cements was assessed following the UNI EN ISO 196-2 norm. X-Ray fluorescence (XRF) was used to determine the element composition. The crystalline structure was analysed quantitatively using x-ray diffraction (XRD). Powders morphology was evaluated using a scanning electron microscope (SEM) with backscattering detectors, and a field emission scanning electron microscope (FESEM). Elemental analysis was performed by energy dispersive x-ray analysis (EDS). The semi-quantitative XRF analysis showed the presence of heavy metal oxides in both cements. The XRD spectra of the two cements reported the presence of dicalcium silicate, tricalcium silicate, tricalcium aluminate, tetracalcium aluminoferrite, bismuth oxide and gypsum. SEM analysis showed that ProRoot MTA powder is less coarse and more homogeneous than Aureoseal. Both powders are formed by particles of different shapes: round, prismatic and oblong. The EDS analysis showed that some ProRoot MTA particles, differently from Aureoseal, contain Ca, Si, Al and Fe. Oblong particles in ProRoot and Aureoseal are rich of bismuth. The strong interest in developing new Portland cement-based endodontic sealers will create materials with increased handling characteristics and physicochemical properties. A thorough investigation on two cement powders was carried out by using XRF, XRD, SEM and EDS analysis. To date there was a lack of studies on Aureoseal Plus. This cement is similar in composition to ProRoot MTA. Despite that it has distinctive elements that could improve its characteristics, resulting in a good alternative to MTA.

Prospective observation of a new bioactive luting cement: 2-year follow-up.

PubMed

Jefferies, Steven R; Pameijer, Cornelis H; Appleby, David C; Boston, Daniel; Galbraith, Colin; Lööf, Jesper; Glantz, Per-Olof

2012-01-01

A pilot study was conducted to determine the 2-year clinical performance of a new bioactive dental cement (Ceramir C&B, formerly XeraCem) for permanent cementation. The cement used in this study is a new formulation class, a hybrid material comprising calcium aluminate and glass ionomer. Thirty-eight crowns and fixed partial denture (FPD) abutments were cemented in 17 patients. Thirty-one of the abutment teeth were vital, 7 nonvital. Six reconstructions were FPDs comprising 14 abutment teeth (12 vital/2 nonvital). A two-unit fixed splint was also included. Preparation parameters and cement characteristics (dispensing, working time, seating characteristics, ease of cement removal) were recorded. Baseline and postcementation data were recorded for marginal integrity, marginal discoloration, secondary caries, retention, and gingival inflammation. Tooth sensitivity was assessed at pre- and postcementation time points using categorical and visual analogue scale (VAS) assessment measures. Mixing of the cement was reported as "easy." Clinical working time for this cement was deemed acceptable. Assessment of seating characteristics indicated all restorations were seated completely after cementation. Cement removal was determined to be "easy." Fifteen of 17 subjects were available for 1-year recall examination; 13 patients were available for the 2-year recall examination. Restorations at 2-year recall examination included 17 single-unit, full-coverage crown restorations, four 3-unit FPDs comprising 8 abutments, and one 2-unit splint. No retentive failures or sensitivity were recorded at 2-year recall. Marginal integrities of all restorations/abutments at 2 years were rated in the "alpha" category. Average VAS score for tooth sensitivity decreased from 7.63 mm at baseline to 0.44 mm at 6-month recall, 0.20 mm at 1-year recall, and 0.00 mm at 2-year recall. The average gingival index score for gingival inflammation decreased from 0.56 at baseline to 0.11 at 6-month recall, then 0.16 at 1-year recall, and 0.21 at 2-year recall. Two-year recall data yielded no loss of retention, no secondary caries, no marginal discolorations, and no subjective sensitivity. All restorations rated "alpha" for marginal integrity at the 2-year recall. After periodic recalls up to 2 years, the new bioactive cement tested thus far has performed favorably as a luting agent for permanent cementation. © 2011 by the American College of Prosthodontists.

Carburizing treatment of low alloy steels: Effect of technological parameters

NASA Astrophysics Data System (ADS)

Benarioua, Younes

2018-05-01

The surface areas of the parts subjected to mechanical loads influence to a great extent the resistance to wear and fatigue. In majority of cases, producing of a hard superficial layer on a tough substrate is conducive to an increased resistance to mechanical wear and fatigue. Cementation treatment of low alloy steels which bonds superficial martensitic layer of high hardness and lateral compressive to a core of lower hardness and greater toughness is an example of a good solution of the problem. The high hardness of the martensitic layer is due to an increased concentration of interstitial carbon atoms in the austenite before quenching. The lower hardness of the core after quenching is due to the presence of ferrite and pearlite components which appear if the cooling rate after austenitization becomes lower than the critical on. The objective of the present study was to obtain a cemented surface layer on low alloy steel by means of pack carburizing treatment. Different steel grades, austenitization temperatures as well as different soaking times were used as parameters of the pack carburizing treatment. During this treatment, carbon atoms from the pack powder diffuse toward the steels surface and form compounds of iron carbides. The effect of carburizing parameters on the transformation rate of low carbon surface layer of the low alloy steel to the cemented one was investigated by several analytical techniques.

Physico-chemical studies of hardened cement paste structure with micro-reinforcing fibers

DOE Office of Scientific and Technical Information (OSTI.GOV)

Steshenko, Aleksei, E-mail: steshenko.alexey@gmail.com; Kudyakov, Aleksander; Konusheva, Viktoriya

The results of physico-chemical studies of modified hardened cement paste with micro-reinforcing fibers are given in this article. The goal was to study the reasons of the increase of strength properties of modified hardened cement paste by the method of X-ray diffraction and electron microscopy. It is shown that the use of mineral fibers in the production of cement based material has positive effect on its properties. The study found out that the increase in the strength of the hardened cement paste with micro-reinforcing fibers is due to the increase of the rate of hydration of cement without a significantmore » change in the phase composition in comparison with hardened cement paste without additive. The results of microstructure investigation (of control samples and samples of the reinforced hardened cement paste) have shown that introduction of mineral fibers in the amount of 0.1-2 % by weight of cement provides the structure of the homogeneous microporous material with uniform distribution of the crystalline phase provided by densely packed hydrates.« less

DOE Office of Scientific and Technical Information (OSTI.GOV)

Sugama, Toshifumi; Pyatina, Tatiana

The study aims at evaluating the bond durability of a carbon microfiber (CMF)-reinforced alkali-activating calcium aluminate cement (CAC)/fly ash F (FAF) blend cementitious material adhering to carbon steel (CS) under stresses induced by a 350°C heat-25°Cwater cooling cycle. This cementitious material/CS joint sample was originally prepared in an autoclave at 300°C under a pressure of 8.3 MPa. For comparison, two reference geothermal well cements, Class G modified with silica (G) and calciumaluminum phosphate (CaP), were employed as well reinforced with CMF. In the CAC/FAF blending cement systems, the CAC-derived cementitious reaction products preferentially adhered to CS surfaces, rather than thatmore » of FAF-related reaction products. CMF played a pivotal role in creating tough interfacial bond structure of cement layer adhering to CS. The bond toughness also was supported by the crystalline cementitious reaction products including sodalite, brownmillerite, and hedenbergite as major phases, and aragonite, boehmite, and garronite as minor ones. The brownmillerite as an interfacial reaction product between cement and CS promoted the chemical bonding of the cement to CS, while the other phases served in providing the attractive bonding of the cement to CS. The post-stress-test joint samples revealed the formation of additional brown-millerite, aragonite, and garronite, in particular brownmillerite as the major one. The combination of chemical bonding and self-advancing adherence behavior of the cement was essential for creating a better interfacial bond structure. A similar interfacial bond structure was observed with CaP. The crystalline phase composition of the autoclaved cement revealed apatite, zeolite, and ferrowyllieite as major reaction products, and aragonite and al-katoite as the minor ones. Ferrowyllieite was identified as cement/CS interfacial reaction product contributing to the chemical bond of cement, while the other phases aided in providing the attractive bond of cement. After a stress test, two phases, ferrowyllieite and aragonite, promoted the self-advancing adherence of cement to CS. However, the effectiveness of these phases in improving adherence performance of cement was less than that of CAC/FAF blend cement, reflecting the fact that the bond durability of CAC/FAF blend cement was far better than that of the CaP. In contrast, the autoclaved silica-modified G cement consisting of xonotlite, and 0.9 nm-to-bermorite and riversideite, with calcite as the crystalline reaction products, had no significant effect on improving the shear bond strength and the bond’s toughness. No interaction product with CS was found in the cement adhering to CS. After a stress test, the calcite phase acted only to promote the self-advancing adherence of cement, but its extent was minimal compared with that of the other cements, thereby resulting in poor bond durability.« less

Method for molding threads in graphite panels

DOEpatents

Short, William W.; Spencer, Cecil

1994-01-01

A graphite panel (10) with a hole (11) having a damaged thread (12) is repaired by drilling the hole (11) to remove all of the thread and make a new hole (13) of larger diameter. A bolt (14) with a lubricated thread (17) is placed in the new hole (13) and the hole (13) is packed with graphite cement (16) to fill the hole and the thread on the bolt. The graphite cement (16) is cured, and the bolt is unscrewed therefrom to leave a thread (20) in the cement (16) which is at least as strong as that of the original thread (12).

Durability of pulp fiber-cement composites

NASA Astrophysics Data System (ADS)

Mohr, Benjamin J.

Wood pulp fibers are a unique reinforcing material as they are non-hazardous, renewable, and readily available at relatively low cost compared to other commercially available fibers. Today, pulp fiber-cement composites can be found in products such as extruded non-pressure pipes and non-structural building materials, mainly thin-sheet products. Although natural fibers have been used historically to reinforce various building materials, little scientific effort has been devoted to the examination of natural fibers to reinforce engineering materials until recently. The need for this type of fundamental research has been emphasized by widespread awareness of moisture-related failures of some engineered materials; these failures have led to the filing of national- and state-level class action lawsuits against several manufacturers. Thus, if pulp fiber-cement composites are to be used for exterior structural applications, the effects of cyclical wet/dry (rain/heat) exposure on performance must be known. Pulp fiber-cement composites have been tested in flexure to examine the progression of strength and toughness degradation. Based on scanning electron microscopy (SEM), environmental scanning electron microscopy (ESEM), energy dispersive spectroscopy (EDS), a three-part model describing the mechanisms of progressive degradation has been proposed: (1) initial fiber-cement/fiber interlayer debonding, (2) reprecipitation of crystalline and amorphous ettringite within the void space at the former fiber-cement interface, and (3) fiber embrittlement due to reprecipitation of calcium hydroxide filling the spaces within the fiber cell wall structure. Finally, as a means to mitigate kraft pulp fiber-cement composite degradation, the effects of partial portland cement replacement with various supplementary cementitious materials (SCMs) has been investigated for their effect on mitigating kraft pulp fiber-cement composite mechanical property degradation (i.e., strength and toughness losses) during wet/dry cycling. SCMs have been found to be effective in mitigating composite degradation through several processes, including a reduction in the calcium hydroxide content, stabilization of monosulfate by maintaining pore solution pH, and a decrease in ettringite reprecipitation accomplished by increased binding of aluminum in calcium aluminate phases and calcium in the calcium silicate hydrate (C-S-H) phase.

The Effect of TiO2 Doped Photocatalytic Nano-Additives on the Hydration and Microstructure of Portland and High Alumina Cements

PubMed Central

Pérez-Nicolás, María; Alvarez, José Ignacio

2017-01-01

Mortars with two different binders (Portland cement (PC) and high alumina cement (HAC)) were modified upon the bulk incorporation of nano-structured photocatalytic additives (bare TiO2, and TiO2 doped with either iron (Fe-TiO2) or vanadium (V-TiO2)). Plastic and hardened state properties of these mortars were assessed in order to study the influence of these nano-additives. Water demand was increased, slightly by bare TiO2 and Fe-TiO2, and strongly by V-TiO2, in agreement with the reduction of the particle size and the tendency to agglomerate. Isothermal calorimetry showed that hydration of the cementitious matrices was accelerated due to additional nucleation sites offered by the nano-additives. TiO2 and doped TiO2 did not show pozzolanic reactivity in the binding systems. Changes in the pore size distribution, mainly the filler effect of the nano-additives, accounted for the increase in compressive strengths measured for HAC mortars. A complex microstructure was seen in calcium aluminate cement mortars, strongly dependent on the curing conditions. Fe-TiO2 was found to be homogeneously distributed whereas the tendency of V-TiO2 to agglomerate was evidenced by elemental distribution maps. Water absorption capacity was not affected by the nano-additive incorporation in HAC mortars, which is a favourable feature for the application of these mortars. PMID:29036917

A bioactive dental luting cement--its retentive properties and 3-year clinical findings.

PubMed

Jefferies, Steven R; Pameijer, Cornelis H; Appleby, David C; Boston, Daniel; Lööf, Jesper

2013-02-01

A clinical validation study was conducted to determine the performance of a new bioactive dental cement (Ceramir C&B, Doxa Dental AB) for permanent cementation. The cement is a new formulation class, which is a hybrid material comprised of calcium aluminate and glass-ionomer components. A total of 38 crowns and bridges were cemented in 17 patients; 31 of the abutment teeth were vital and seven were non-vital. Six restorations were bridges with a total of 14 abutment teeth (12 vital/ two non-vital). One fixed splint comprising two abutment teeth was also included. Preparation parameters were recorded, as well as cement characteristics such as working time, setting time, seating characteristics, and ease of cement removal. Baseline data were recorded for the handling of the cement, gingival inflammation, and pre-cementation sensitivity. Post-cementation parameters included post-cementation sensitivity, gingival tissue reaction, marginal integrity, and discoloration. All patients were seen for recall examinations at 30 days and 6 months. Fifteen of 17 subjects and 13 of 17 patients were also available for subsequent comprehensive 1- and 2-year recall examination, and 13 patients were available for a 3-year recall examination. Restorations available for the 3-year recall examination included 14 single-unit full-coverage crown restorations, four three-unit bridges comprising eight abutments, and one two-unit splint. Three-year recall data yielded no loss of retention, no secondary caries, no marginal discolorations, and no subjective sensitivity. All restorations rated excellent for marginal integrity. Average visual analogue scale (VAS) score for tooth sensitivity decreased from 7.63 mm at baseline to 0.44 mm at 6-month recall, 0.20 mm at 1-year recall, and 0.00 mm at 2- and 3-year recall. Average gingival index (GI) score for gingival inflammation decreased from 0.56 at baseline to 0.11 at 6-month recall, 0.16 at 1-year recall, 0.21 at 2-year recall, and 0.07 at 3-year recall. After periodic recalls up to 3 years, Ceramir C&B thus far has performed quite favorably as a luting agent for permanent cementation of permanent restorations. In-vitro crown-coping retention studies were also conducted using this cement and various control cementation materials. Mean laboratory retentive forces measured for Ceramir C&B were comparable to other currently available luting agents for both metal and all-ceramic indirect restorative materials.

Bond Durability of Carbon-Microfiber-Reinforced Alkali-Activated High-Temperature Cement Adhering to Carbon Steel

DOE PAGES

Sugama, Toshifumi; Pyatina, Tatiana

2017-02-01

The study aims at evaluating the bond durability of a carbon microfiber (CMF)-reinforced alkali-activating calcium aluminate cement (CAC)/fly ash F (FAF) blend cementitious material adhering to carbon steel (CS) under stresses induced by a 350°C heat-25°Cwater cooling cycle. This cementitious material/CS joint sample was originally prepared in an autoclave at 300°C under a pressure of 8.3 MPa. For comparison, two reference geothermal well cements, Class G modified with silica (G) and calciumaluminum phosphate (CaP), were employed as well reinforced with CMF. In the CAC/FAF blending cement systems, the CAC-derived cementitious reaction products preferentially adhered to CS surfaces, rather than thatmore » of FAF-related reaction products. CMF played a pivotal role in creating tough interfacial bond structure of cement layer adhering to CS. The bond toughness also was supported by the crystalline cementitious reaction products including sodalite, brownmillerite, and hedenbergite as major phases, and aragonite, boehmite, and garronite as minor ones. The brownmillerite as an interfacial reaction product between cement and CS promoted the chemical bonding of the cement to CS, while the other phases served in providing the attractive bonding of the cement to CS. The post-stress-test joint samples revealed the formation of additional brown-millerite, aragonite, and garronite, in particular brownmillerite as the major one. The combination of chemical bonding and self-advancing adherence behavior of the cement was essential for creating a better interfacial bond structure. A similar interfacial bond structure was observed with CaP. The crystalline phase composition of the autoclaved cement revealed apatite, zeolite, and ferrowyllieite as major reaction products, and aragonite and al-katoite as the minor ones. Ferrowyllieite was identified as cement/CS interfacial reaction product contributing to the chemical bond of cement, while the other phases aided in providing the attractive bond of cement. After a stress test, two phases, ferrowyllieite and aragonite, promoted the self-advancing adherence of cement to CS. However, the effectiveness of these phases in improving adherence performance of cement was less than that of CAC/FAF blend cement, reflecting the fact that the bond durability of CAC/FAF blend cement was far better than that of the CaP. In contrast, the autoclaved silica-modified G cement consisting of xonotlite, and 0.9 nm-to-bermorite and riversideite, with calcite as the crystalline reaction products, had no significant effect on improving the shear bond strength and the bond’s toughness. No interaction product with CS was found in the cement adhering to CS. After a stress test, the calcite phase acted only to promote the self-advancing adherence of cement, but its extent was minimal compared with that of the other cements, thereby resulting in poor bond durability.« less

Real-time high-resolution X-ray imaging and nuclear magnetic resonance study of the hydration of pure and Na-doped C3A in the presence of sulfates

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kirchheim,, A. P.; Dal Molin, D.C.; Emwas, Abdul-Hamid

2010-12-01

This study details the differences in real-time hydration between pure tricalcium aluminate (cubic C{sub 3}A or 3CaO {center_dot} Al{sub 2}O{sub 3}) and Na-doped tricalcium aluminate (orthorhombic C{sub 3}A or Na{sub 2}Ca{sub 8}Al{sub 6}O{sub 18}), in aqueous solutions containing sulfate ions. Pure phases were synthesized in the laboratory to develop an independent benchmark for the reactions, meaning that their reactions during hydration in a simulated early age cement pore solution (saturated with respect to gypsum and lime) were able to be isolated. Because the rate of this reaction is extremely rapid, most microscopy methods are not adequate to study the earlymore » phases of the reactions in the early stages. Here, a high-resolution full-field soft X-ray imaging technique operating in the X-ray water window, combined with solution analysis by {sup 27}Al nuclear magnetic resonance (NMR) spectroscopy, was used to capture information regarding the mechanism of C{sub 3}A hydration during the early stages. There are differences in the hydration mechanism between the two types of C{sub 3}A, which are also dependent on the concentration of sulfate ions in the solution. The reactions with cubic C{sub 3}A (pure) seem to be more influenced by higher concentrations of sulfate ions, forming smaller ettringite needles at a slower pace than the orthorhombic C{sub 3}A (Na-doped) sample. The rate of release of aluminate species into the solution phase is also accelerated by Na doping.« less

{sup 13}C chemical shift anisotropies for carbonate ions in cement minerals and the use of {sup 13}C, {sup 27}Al and {sup 29}Si MAS NMR in studies of Portland cement including limestone additions

DOE Office of Scientific and Technical Information (OSTI.GOV)

Sevelsted, Tine F.; Herfort, Duncan; Skibsted, Jørgen, E-mail: jskib@chem.au.dk

2013-10-15

{sup 13}C isotropic chemical shifts and chemical shift anisotropy parameters have been determined for a number of inorganic carbonates relevant in cement chemistry from slow-speed {sup 13}C MAS or {sup 13}C({sup 1}H) CP/MAS NMR spectra (9.4 T or 14.1 T) for {sup 13}C in natural abundance. The variation in the {sup 13}C chemical shift parameters is relatively small, raising some doubts that different carbonate species in Portland cement-based materials may not be sufficiently resolved in {sup 13}C MAS NMR spectra. However, it is shown that by combining {sup 13}C MAS and {sup 13}C({sup 1}H) CP/MAS NMR carbonate anions in anhydrousmore » and hydrated phases can be distinguished, thereby providing valuable information about the reactivity of limestone in cement blends. This is illustrated for three cement pastes prepared from an ordinary Portland cement, including 0, 16, and 25 wt.% limestone, and following the hydration for up to one year. For these blends {sup 29}Si MAS NMR reveals that the limestone filler accelerates the hydration for alite and also results in a smaller fraction of tetrahedrally coordinated Al incorporated in the C-S-H phase. The latter result is more clearly observed in {sup 27}Al MAS NMR spectra of the cement–limestone blends and suggests that dissolved aluminate species in the cement–limestone blends readily react with carbonate ions from the limestone filler, forming calcium monocarboaluminate hydrate. -- Highlights: •{sup 13}C chemical shift anisotropies for inorganic carbonates from {sup 13}C MAS NMR. •Narrow {sup 13}C NMR chemical shift range (163–171 ppm) for inorganic carbonates. •Anhydrous and hydrated carbonate species by {sup 13}C MAS and {sup 13}C({sup 1}H) CP/MAS NMR. •Limestone accelerates the hydration for alite in Portland – limestone cements. •Limestone reduces the amount of aluminium incorporated in the C-S-H phase.« less

Rapid Assessment of Remedial Effectiveness and Rebound in Fractured Bedrock

DTIC Science & Technology

2017-10-01

Permanent 5-inch diameter steel casing was then installed to a depth of 58.3 ft-bgs, and pressure-grouted in place using cement /bentonite grout. Once the...collected from 64 feet to 78 feet bgs. A 2-inch stainless steel well, screened from 64 to 74 feet bgs, was installed within the borehole. A filter pack was...installed from 63.5 ft to 74.5 ft bgs, and the remainder of the borehole was sealed with a bentonite seal and cement /bentonite grout. Therefore

Alkali-activated complex binders from class C fly ash and Ca-containing admixtures.

PubMed

Guo, Xiaolu; Shi, Huisheng; Chen, Liming; Dick, Warren A

2010-01-15

Processes that maximize utilization of industrial solid wastes are greatly needed. Sodium hydroxide and sodium silicate solution were used to create alkali-activated complex binders (AACBs) from class C fly ash (CFA) and other Ca-containing admixtures including Portland cement (PC), flue gas desulfurization gypsum (FGDG), and water treatment residual (WTR). Specimens made only from CFA (CFA100), or the same fly ash mixed with 40 wt% PC (CFA60-PC40), with 10 wt% FGDG (CFA90-FGDG10), or with 10 wt% WTR (CFA90-WTR10) had better mechanical performance compared to binders using other mix ratios. The maximum compressive strength of specimens reached 80.0 MPa. Geopolymeric gel, sodium polysilicate zeolite, and hydrated products coexist when AACB reactions occur. Ca from CFA, PC, and WTR precipitated as Ca(OH)(2), bonded in geopolymers to obtain charge balance, or reacted with dissolved silicate and aluminate species to form calcium silicate hydrate (C-S-H) gel. However, Ca from FGDG probably reacted with dissolved silicate and aluminate species to form ettringite. Utilization of CFA and Ca-containing admixtures in AACB is feasible. These binders may be widely utilized in various applications such as in building materials and for solidification/stabilization of other wastes, thus making the wastes more environmentally benign.

Nanogranular origin of concrete creep.

PubMed

Vandamme, Matthieu; Ulm, Franz-Josef

2009-06-30

Concrete, the solid that forms at room temperature from mixing Portland cement with water, sand, and aggregates, suffers from time-dependent deformation under load. This creep occurs at a rate that deteriorates the durability and truncates the lifespan of concrete structures. However, despite decades of research, the origin of concrete creep remains unknown. Here, we measure the in situ creep behavior of calcium-silicate-hydrates (C-S-H), the nano-meter sized particles that form the fundamental building block of Portland cement concrete. We show that C-S-H exhibits a logarithmic creep that depends only on the packing of 3 structurally distinct but compositionally similar C-S-H forms: low density, high density, ultra-high density. We demonstrate that the creep rate ( approximately 1/t) is likely due to the rearrangement of nanoscale particles around limit packing densities following the free-volume dynamics theory of granular physics. These findings could lead to a new basis for nanoengineering concrete materials and structures with minimal creep rates monitored by packing density distributions of nanoscale particles, and predicted by nanoscale creep measurements in some minute time, which are as exact as macroscopic creep tests carried out over years.

The deposition of aluminide and silicide coatings on γ-TiAl using the halide-activated pack cementation method

NASA Astrophysics Data System (ADS)

Munro, T. C.; Gleeson, B.

1996-12-01

The halide-activated pack cementation method (HAPC) was utilized to deposit aluminide and silicide coatings on nominally stoichiometric γ-TiAl. The deposition temperature was 1000°C and deposition times ranged from 2 to 12 hours. The growth rates of the coatings were diffusion controlled, with the rate of aluminide growth being about a factor of 2 greater than that of silicide growth. The aluminide coating was inward growing and consisted of a thick, uniform outer layer of TiAl3 and a thin inner layer of TiAl2, with the rate-controlling step being the diffusion of aluminum from the pack into the substrate. Annealing experiments at 1100 °C showed that the interdiffusion between the aluminide coating and the γ-TiAl substrate was rapid. In contrast to the aluminide coating, the silicide coating was nonuniform and porous, consisting primarily of TiSi2, TiSi, and Ti5Si4, with the rate-controlling step for the coating growth believed to be the diffusion of aluminum into the γ-TiAl ahead of the silicide/γ-TiAl interface. The microstructural evolution of the aluminide and silicide coating structures is discussed qualitatively.

Nanogranular origin of concrete creep

PubMed Central

Vandamme, Matthieu; Ulm, Franz-Josef

2009-01-01

Concrete, the solid that forms at room temperature from mixing Portland cement with water, sand, and aggregates, suffers from time-dependent deformation under load. This creep occurs at a rate that deteriorates the durability and truncates the lifespan of concrete structures. However, despite decades of research, the origin of concrete creep remains unknown. Here, we measure the in situ creep behavior of calcium–silicate–hydrates (C–S–H), the nano-meter sized particles that form the fundamental building block of Portland cement concrete. We show that C–S–H exhibits a logarithmic creep that depends only on the packing of 3 structurally distinct but compositionally similar C–S–H forms: low density, high density, ultra-high density. We demonstrate that the creep rate (≈1/t) is likely due to the rearrangement of nanoscale particles around limit packing densities following the free-volume dynamics theory of granular physics. These findings could lead to a new basis for nanoengineering concrete materials and structures with minimal creep rates monitored by packing density distributions of nanoscale particles, and predicted by nanoscale creep measurements in some minute time, which are as exact as macroscopic creep tests carried out over years. PMID:19541652

Overview of CO2 Leakage Problems and Sealants for CO2 Leakage Remediation

NASA Astrophysics Data System (ADS)

Peng, Shudai

Excessive Carbon Dioxide (CO2) emission has become a serious issue and caused lots of environmental problems. Carbon Capture and Storage (CCS) program has been developed to reduce the CO2 content in the atmosphere. CO2 storage has been targeted mainly on depleted oil or gas reservoirs and deep saline aquifers. However, leakage could occur through wellbores, cap rocks, formation faults, and fractures during and after CO2 injection. To minimize the risk, different types of sealants have been investigated to prevent CO2 leaks. The aim of this thesis is to provide a comprehensive review of the materials which could be used as CO2 sealants. Based on the difference of materials components, this research has classified the sealants into seven types, including cements, geopolymers, foams, gel systems, resin systems, biofilm barriers, and nanoparticles. For each type of sealants, its chemical components, physical properties, stabilities, impact factors, applied environments, advantages and limitations were summarized. The most commonly used sealant for CO2 leakage control from wellbore is still cement, and the aluminate-calcium based cement has the best properties. It is very challenging to seal the fractures and faults, far from wellbore due to the difficulty to deliver plugging materials into the in-depth of a reservoir. The thermo-stability is also a great challenge for most materials and should be evaluated under supercritical CO2 condition.

Utilization of municipal solid waste incineration (MSWI) fly ash in blended cement Part 1: Processing and characterization of MSWI fly ash.

PubMed

Aubert, J E; Husson, B; Sarramone, N

2006-08-25

This paper is the first of a series of two articles dealing with the processes applied to MSWI fly ash with a view to reusing it safely in cement-based materials. Part 1 presents two stabilization processes and Part 2 deals with the use of the two treated fly ashes (TFA) in mortars. Two types of binder were used: an Ordinary Portland Cement (OPC) containing more than 95% clinker (CEM I 52.5R) and a binary blend cement composed of 70% ground granulated blast furnace slag and 30% clinker (CEM III-B 42.5N). In this first part, two stabilization processes are presented: the conventional process, called "A", based on the washing, phosphation and calcination of the ash, and a modified process, called "B", intended to eliminate metallic aluminum and sulfate contained in the ash. The physical, chemical and mineralogical characteristics of the two TFA were comparable. The main differences observed were those expected, i.e. TFA-B was free of metallic aluminum and sulfate. The mineralogical characterization of the two TFAs highlighted the presence of large amounts of a calcium aluminosilicate phase taking two forms, a crystalline form (gehlenite) and an amorphous form. Hydration studies on pastes containing mixed TFA and calcium hydroxide showed that this phase reacted with calcium hydroxide to form calcium aluminate hydrates. This formation of hydrates was accompanied by a hardening of the pastes. These results are very encouraging for the reuse of such TFA in cement-based materials because they can be considered as pozzolanic additions and could advantageously replace a part of the cement in cement-based materials. Finally, leaching tests were carried out to evaluate the environmental impact of the two TFAs. The elements which were less efficiently stabilized by process A were zinc, cadmium and antimony but, when the results of the leaching tests were compared with the thresholds of the European landfill directive, TFA-A could nevertheless be accepted at landfills for non-hazardous waste. The modifications of the process led to a significant reduction in the stabilization of chromium, selenium and antimony.

Novel method for titanium crown casting using a combination of wax patterns fabricated by a CAD/CAM system and a non-expanded investment.

PubMed

Zhang, Zutai; Tamaki, Yukimichi; Hotta, Yasuhiro; Miyazaki, Takashi

2006-07-01

For titanium casting, most commercial investments for titanium recommend casting at a low mold temperature to reduce oxidation. However, the thermal expansion values of the molds at low casting temperatures may be insufficient. The purpose of the current study was to investigate the possibility of obtaining accurate titanium crown casts using wax pattern fabricated by a CAD/CAM system with a non-expanded mold. Three types of experimental magnesia-based investments (A, B and C) were made and their properties were evaluated for dental use. Two kinds of wax patterns for full-coverage coping crowns (S-0: cement space of 0 microm; S-20: cement space of 20 microm) were fabricated using a commercial CAD/CAM system. A traditional method (TM) using inlay wax was performed for comparison. The investment for titanium casting was decided from the fundamental data of experimental investments. Titanium crowns were replaced on the stone die and the thickness of the cement layer was evaluated. There were no significant differences for the setting time and setting expansion among the experimental investments, but the aluminous cement content played a role in hardening and contracting the mold. The fit of the titanium crowns differed significantly between the TM and the CAD/CAM system. The ranges of thickness obtained from the TM, S-0 and S-20 were 20.78-357.88 microm, 25.12-107.46 microm and 17.84-58.92 microm, respectively. High quality titanium crown casting was obtained using a combination of wax patterns fabricated by a CAD/CAM system and a non-expanded MgO-based investment.

Addition of Silica Fume to Improve Strength of Cement Paste

NASA Astrophysics Data System (ADS)

Chen, Jiajian; Chen, Hongniao; Li, Gu

2018-03-01

This study measured the packing densities of 0 to 30% silica fume (SF) added cementitious materials and strength of the cementitious pastes with various water content. The results revealed that addition of silica fume up to a certain level has great effects on packing density and strength. In-depth analysis illustrated that a lower W/CM ratio would not always result in a higher cube strength, and the range between 0.05 and 0.07 µm would be the amount of water film thickness (WFT) for muximum strength.

Micro- and nano-scale characterization to study the thermal degradation of cement-based materials

DOE Office of Scientific and Technical Information (OSTI.GOV)

Lim, Seungmin, E-mail: lim76@illinois.edu; Mondal, Paramita

2014-06-01

The degradation of hydration products of cement is known to cause changes in the micro- and nano-structure, which ultimately drive thermo-mechanical degradation of cement-based composite materials at elevated temperatures. However, a detailed characterization of these changes is still incomplete. This paper presents results of an extensive experimental study carried out to investigate micro- and nano-structural changes that occur due to exposure of cement paste to high temperatures. Following heat treatment of cement paste up to 1000 °C, damage states were studied by compressive strength test, thermogravimetric analysis (TGA), scanning electron microscopy (SEM) atomic force microscopy (AFM) and AFM image analysis.more » Using experimental results and research from existing literature, new degradation processes that drive the loss of mechanical properties of cement paste are proposed. The development of micro-cracks at the interface between unhydrated cement particles and paste matrix, a change in C–S–H nano-structure and shrinkage of C–S–H, are considered as important factors that cause the thermal degradation of cement paste. - Highlights: • The thermal degradation of hydration products of cement is characterized at micro- and nano-scale using scanning electron microscopy (SEM) and atomic force microscopy (AFM). • The interface between unhydrated cement particles and the paste matrix is considered the origin of micro-cracks. • When cement paste is exposed to temperatures above 300 ºC, the nano-structure of C-S-H becomes a more loosely packed globular structure, which could be indicative of C-S-H shrinkage.« less

Contrasting diagenetic histories of concretions vs. host rocks, Lion Mountain Member, Riley formation (upper Cambrian), Texas

DOE Office of Scientific and Technical Information (OSTI.GOV)

McBride, E.F.

1988-02-01

White, elliptical, calcite-cemented concretion nuclei up to 1 m long contrast markedly in color, composition, and diagenetic history from more glauconite-rich concretion rinds and from dark-green glaucarenite host rocks. Concretion nuclei are loosely packed deposits of trilobite carapaces and minor quartz and glauconite that have intergranular volumes of 58%. The nuclei are shell-lag deposits that were cemented by calcite at the sea floor or after burial of a few meters. Concretion rinds, composed of subequal amounts of quartz and compactionally deformed glauconite, have an intergranular volume of only 32% and minor quartz overgrowths that preceded pore-occluding calcite cement. The rindsmore » underwent burial for several million years to tens of millions of years to depths of several hundred meters before they were cemented. The host rock is predominately glauconite with very minor quartz and calcite cement. Strontium isotopic ratios of host-rock calcite cement are variable (0.7084 to 0.7093), but the lowest value suggests precipitation during the Middle Ordovician. In the absence of significant amounts of carbonate cement, the host rock underwent complete dissolution of trilobite carapaces and maximum compaction with total loss of porosity through squashing of glauconite grains. Maximum burial during this stage was completed by the end of Ordovician time.« less

Physical properties and comparative strength of a bioactive luting cement.

PubMed

Jefferies, Steven; Lööf, Jesper; Pameijer, Cornelis H; Boston, Daniel; Galbraith, Colin; Hermansson, Leif

2013-01-01

New dental cement formulations require testing to determine physical and mechanical laboratory properties. To test an experimental calcium aluminate/glass-ionomer cement, Ceramir C and B (CC and B), regarding compressive strength (CS), film thickness (FT), net setting time (ST) and Vickers hardness. An additional test to evaluate potential dimensional change/expansion properties of this cement was also conducted. CS was measured according to a slightly modified ISO 9917:2003 for the CC and B specimens. The samples were not clamped while being exposed to relative humidity of great than 90 percent at 37 degrees C for 10 minutes before being stored in phosphate-buffered saline at 37 degrees C. For the CS, four groups were tested: Group 1-CC and B; Group 2-RelyX Luting Cement; Group 3-Fuji Plus; and Group 4-RelyX Unicem. Samples from all groups were stored for 24 hours before testing. Only CCandB was tested for ST and FT according to ISO 9917:2003. The FT was tested 2 minutes after mixing. Vickers hardness was evaluated using the CSM Microhardness Indentation Tester using zinc phosphate cement as a comparison material. Expansion testing included evaluating potential cracks in feldspathic porcelain jacket crowns (PJCs). The mean and standard deviation after 24 hours were expressed in MPa: Group 1 equals 160 plus or equal to 27; Group 2 equals 96 plus or equal to 10; Group 3 equals 138 plus or equal to 15; Group 4 equals 157 plus or equal to 10. A single-factor ANOVA demonstrated statistically significant differences between the groups (P less than 0.001). Pair-wise statistical comparison demonstrated a statistically significant difference between Groups 1 and 2. No statistically significant differences were found between other groups. The FT was 16.8 plus or equal to 0.9 and the ST was 4.8 plus or equal to 0.1 min. Vickers hardness for Ceramir C and B was 68.3 plus or equal to 17.2 and was statistically significantly higher (P less than 0.05) than Fleck's Zinc Phosphate cement at Vickers hardness of 51.4 plus or equal to 10. There was no evidence of cracks due to radial expansion in PJCs by the Ceramir C and B cement. All luting cements tested demonstrated compressive strengths well in excess of the ISO requirement for water-based cements of no less than 50 MPa. Ceramir C and B showed significantly higher CS than RelyX Luting Cement after 24 hours, but was not significantly higher than either Fuji Plus or RelyX Unicem. The ST and FT values of CC and B conform to and are within the boundaries of the requirements of the standard. Surface hardness was statistically higher than and comparable to zinc phosphate cement. There was no evidence of potentially clinically significant and deleterious expansion behavior by this cement. All cements tested demonstrated acceptable strength properties. Within the limits of this study, Ceramir C and B is deemed to possess physical properties suitable for a dental luting cement.

Characterization and modeling of the rheology of cement paste: With applications toward self-flowing materials

NASA Astrophysics Data System (ADS)

Saak, Aaron Wilbur

The objective of this research is to better understand the important mechanisms that control the rheology of cement paste. In order to understand these mechanisms, new experimental techniques are developed. The insights gained through these studies are then applied toward designing self-flowing materials, particularly self-compacting concrete (SCC). A new testing program is developed where both the peak and equilibrium stress flow curves of cement paste are obtained by testing only one sample. Additionally, the influence of wall slip on yield stress and viscoelastic measurements is determined using a vane. The results indicate that a slip layer develops when the shear stress approaches the yield point. A three-dimensional model relating slump to yield stress is derived as a function of cone geometry. The results indicate that the model fits experimental data for cylindrical slumps over a wide range of yield stress values for a variety of materials. When compared to other published models, the results suggest that a fundamental relationship exists between yield stress and slump that is material independent and largely independent of cone geometry. The affect of various mixing techniques on the rheology of cement paste is investigated using a rheometer as a highly controlled mixer. The results suggest that there is a characteristic shear rate where the viscosity of cement paste is minimized. The influence of particle packing density, morphology and surface area on the viscosity of cement paste is quantified. The data suggest that even though packing density increases with the addition of fine particles, the benefits are largely overshadowed by a dramatic increase in surface area. Finally, a new methodology is introduced for designing self-compacting concrete. This approach incorporates a "self-flow zone" where the rheology of the paste matrix provides high workability, yet segregation resistance. The flow properties of fresh concrete are measured using a U-tube apparatus to test the general applicability of the proposed methodology. Using the new design approach, concrete with a slump of 29 cm (11 inches) and slump flow diameter of 60.9 cm (24 inches) is produced.

Compression and flexural strength of bone cement mixed with blood.

PubMed

Tan, J H; Koh, B Th; Ramruttun, A K; Wang, W

2016-08-01

To assess the compression and flexural strength of bone cement mixed with 0 ml, 1 ml, or 2 ml of blood. High viscosity polymethyl methacrylate (PMMA) loaded with or without gentamicin was used. Blood was collected from total knee arthroplasty patients. In the same operating room, one pack of cement each was mixed with 0 ml (control), 1 ml, or 2 ml of blood for 1 minute during the dough phase. The dough was extruded into cylindrical and rectangular moulds for 20 minutes of setting, and then cured in phosphate buffered saline at 37±1ºC for 7 days. The samples were visually inspected for fractures and areas of weakness, and then scanned using microcomputed tomography. 48 gentamicin-loaded and 59 non-gentamicin-loaded samples mixed with 0 ml (control), 1 ml, or 2 ml of blood were randomised for flexural and compression strength testing; each group had at least 6 samples. In samples loaded with or without gentamicin, the flexural and compressive strength was highest in controls, followed by samples mixed with 1 ml or 2 ml of blood. In samples mixed with 2 ml of blood, the flexural strength fell below the standard of 50 MPa. In samples mixed with 2 ml of blood and all gentamicin-loaded samples, the compressive strength fell below the standard of 70 MPa. Microcomputed tomography revealed areas of voids and pores indicating the presence of laminations and partitions within. The biomechanical strength of PMMA contaminated with blood may decrease. Precautions such as saline lavage, pack drying the bone, change of gloves, and prompt insertion of the implant should be taken to prevent blood from contaminating bone cement.

Alumina as a filler for bone cement: a feasibility study.

PubMed

Ackley, M A; Monroe, E

1980-10-01

A composite bone cement of Alcoa A-10 Alumina and very finely ground poly(methyl methacrylate) beads (PMMA) was fabricated. It was tested in an attempt to improve on the conventionally used pure PMMA bone cement. By knowing the densities of the powders and their volumes, the mass of each was calculated for the most efficient packing of PMMA and Al2O3 powders and a 65% PMMA: 35% Al2O3 ratio by weight composition was determined. This was tested, as well as the pure cement so comparisons could be made. Cylinders for the strength tests were also made of silane treated Al2O3. The compositions were tested for compressive and tensile strengths. The pure PMMA, composite and silane treated composite had compressive strengths of 79.64 +/- 13.0, 83.17 +/- 4.8, and 71.52 +/- 8.6 MPa and the tensile strengths were 6.69 +/- 0.6, 5.12 +/- 0.3, and 7.12 +/- 0.5 MPa respectively. Also the 65%-35% PMMA-Al2O3 composite required 64% less monomer for mixing than did the pure cement which is thought to be better for tissue healing. The maximum temperature attained from room temperature was 110 degrees-115 degrees C for both cements. The composite took 6.5 min longer to reach its peak temperature than did the pure cement. The bone cements were implanted for one week in a rabbit and both compositions seemed acceptable by the tissue.

Crystal structure control of aluminized clay minerals on the mobility of caesium in contaminated soil environments

NASA Astrophysics Data System (ADS)

Dzene, Liva; Ferrage, Eric; Viennet, Jean-Christophe; Tertre, Emmanuel; Hubert, Fabien

2017-02-01

Radioactive caesium pollution resulting from Fukushima Dai-ichi and Chernobyl nuclear plant accidents involves strong interactions between Cs+ and clays, especially vermiculite-type minerals. In acidic soil environments, such as in Fukushima area, vermiculite is subjected to weathering processes, resulting in aluminization. The crystal structure of aluminized clays and its implications for Cs+ mobility in soils remain poorly understood due to the mixture of these minerals with other clays and organic matter. We performed acidic weathering of a vermiculite to mimic the aluminization process in soils. Combination of structure analysis and Cs+ extractability measurements show that the increase of aluminization is accompanied by an increase in Cs+ mobility. Crystal structure model for aluminized vermiculite is based on the interstratification of unaltered vermiculite layers and aluminized layers within the same particle. Cs+ in vermiculite layers is poorly mobile, while the extractability of Cs+ is greatly enhanced in aluminized layers. The overall reactivity of the weathered clay (cation exchange capacity, Cs+ mobility) is then governed by the relative abundance of the two types of layers. The proposed layer model for aluminized vermiculite with two coexisting populations of caesium is of prime importance for predicting the fate of caesium in contaminated soil environments.

Development of Coatings for Tantalum Alloy Nozzle Vanes

NASA Technical Reports Server (NTRS)

Stetson, A. R.; Wimber, R. T.

1967-01-01

A group of silicide coatings developed for the T222 tantalum-base alloy have afforded over 600 hours of protection at 1600 and 2400 F during cyclic exposure in air. These coatings were applied in two steps. A modifier alloy was applied by slurry techniques and was sintered in vacuum prior to siliciding by pack cementation in argon. Application of the modifier alloy by pack cementation was found to be much less effective. The addition of titanium and vanadium to molybdenum and tungsten yielded beneficial modifier alloys, whereas the addition of chromium showed no improvement. After siliciding, the 15Ti- 35W-15V-35Mo modifier alloy exhibited the best performance; one sample survived 1064 hours of oxidation at 2400 F. This same coating was the only coating to reproducibly provide 600 hours of protection at both 1600 and 2400 F; in the second and third of three experiments, involving oxidation of three to five specimens at each temperature in each experiment, no failures were observed in 600 hours of testing. The slurry coatings were also shown to protect the Cb752 and D43 columbium-base alloys.

Effect of chlorhexidine disinfectant on bond strength of glass ionomer cement to dentin using atraumatic restorative treatment.

PubMed

Wadenya, Rose; Menon, Sandhya; Mante, Francis

2011-01-01

This study investigated the effect of 2% chlorhexidine gluconate (CHX) disinfectant on bond strength (BS) of high-density glass ionomer cement (HDGIC) to dentin following atraumatic restorative treatment (ART) and conventional preparations. Specimens were divided into four groups: Group 1--ART (control); Group 2--ART with CHX disinfection; Group 3--Conventional (control); Group 4--Conventional with CHX disinfection. HDGIC was packed in cylindrical molds placed over flat dentin surfaces; BS was measured after seven days. ART-prepared dentin surfaces disinfected with CHX provided bonding to HDGIC that was comparable to untreated dentin and to conventionally prepared dentin.

High-temperature electrically conductive ceramic composite and method for making same

DOEpatents

Beck, David E.; Gooch, Jack G.; Holcombe, Jr., Cressie E.; Masters, David R.

1983-01-01

The present invention relates to a metal-oxide ceramic composition useful in induction heating applications for treating uranium and uranium alloys. The ceramic composition is electrically conductive at room temperature and is nonreactive with molten uranium. The composition is prepared from a particulate admixture of 20 to 50 vol. % niobium and zirconium oxide which may be stabilized with an addition of a further oxide such as magnesium oxide, calcium oxide, or yttria. The composition is prepared by blending the powders, pressing or casting the blend into the desired product configuration, and then sintering the casting or compact in an inert atmosphere. In the casting operation, calcium aluminate is preferably added to the admixture in place of a like quantity of zirconia for providing a cement to help maintain the integrity of the sintered product.

Performance evaluation of a slow-release packing material-embedded functional microorganisms for biofiltration.

PubMed

Zhu, Rencheng; Li, Shunyi; Wu, Zhenjun; Dumont, Éric

2017-04-01

A composite packing material (CM-5) was prepared in this study, mainly consisting of compost with functional microorganisms, calcium carbonate (CaCO 3 ), perlite, cement and plant fiber. To get stronger compressive strength, mass ratios of these components were optimized based on single factor experiments, and finally adding amounts of perlite, cement, plant fiber, CaCO 3 , compost and binder at 18%, 18%, 7%, 13%, 17% and 27%, respectively. According to the optimum proportion, CM-5 was extruded in cylindrical shape (12 mm in diameter and 20 mm in length) with a bulk density of 470 kg m -3 , a moisture retention capacity of 49% and the microbial counts of × 10 5 CFU g -1 of packing material. The cumulative release rates of total organic carbon (TOC) and total nitrogen (TN) from CM-5 were 3.1% and 6.5%, respectively, after 19 times extraction in distilled water. To evaluate the H 2 S removal capacity, CM-5 was compared with an organic (corncob) and an inorganic (ceramsite) packing material in three biofilters. The results showed that CM-5 had higher H 2 S removal capacity compared with corncob and ceramsite. CM-5 could avoid the large fluctuation of pH value and pressure drop during the operation. The maximum H 2 S removal capacity of CM-5 was 12.9 g m -3  h -1 and the removal efficiency could maintain over 95.4% when the inlet H 2 S loading rate was lower than 11.3 g m -3  h -1 without any addition of nutrients and pH buffer substances. Besides, only 2-3 days were needed for the recovery of biofiltration performance after about two weeks of idle period.

Production of Synthetic Phosphoanhydrite and Its Use as a Binder in Self-Leveling Underlayments (SLU).

PubMed

Schaefer, Cecília Ogliari; Cheriaf, Malik; Rocha, Janaíde Cavalcante

2017-08-17

An experimental study was conducted to investigate the potential use of phosphogypsum (PG) to produce self-leveling underlayments. The study was designed in two stages. Initially a phosphoanhydrite (PA) was produced by heating phosphogypsum at temperatures of 350 °C, 450 °C, 550 °C, and 650 °C. Two periods of heating were applied (2 and 4 h). The formation of anhydrite was determined by thermogravimetric analysis (DTA-TG) and confirmed by X-ray diffraction (XRD). The results show that anhydrite II was obtained at temperatures above 450 °C, and at higher calcination temperatures the PA solubility was lower. In the second stage of this research, the PA was used in self-leveling underlayments as the main binder in the ternary system comprised of calcium sulfate, calcium aluminate cement, and Portland cement. Self-leveling mortar screeds produced using PA (550 °C/4 h) and PA (650 °C/4 h) showed the best performance in terms of mechanical strength and no degradation was observed after immersion and immersion-drying tests. The formation of ettringite, identified by scanning electron microscopy (SEM), may have contributed to these results. Morphological changes were studied using the scanning electron microscopy (SEM) technique.

Production of Synthetic Phosphoanhydrite and Its Use as a Binder in Self-Leveling Underlayments (SLU)

PubMed Central

Schaefer, Cecília Ogliari; Cheriaf, Malik

2017-01-01

An experimental study was conducted to investigate the potential use of phosphogypsum (PG) to produce self-leveling underlayments. The study was designed in two stages. Initially a phosphoanhydrite (PA) was produced by heating phosphogypsum at temperatures of 350 °C, 450 °C, 550 °C, and 650 °C. Two periods of heating were applied (2 and 4 h). The formation of anhydrite was determined by thermogravimetric analysis (DTA-TG) and confirmed by X-ray diffraction (XRD). The results show that anhydrite II was obtained at temperatures above 450 °C, and at higher calcination temperatures the PA solubility was lower. In the second stage of this research, the PA was used in self-leveling underlayments as the main binder in the ternary system comprised of calcium sulfate, calcium aluminate cement, and Portland cement. Self-leveling mortar screeds produced using PA (550 °C/4 h) and PA (650 °C/4 h) showed the best performance in terms of mechanical strength and no degradation was observed after immersion and immersion-drying tests. The formation of ettringite, identified by scanning electron microscopy (SEM), may have contributed to these results. Morphological changes were studied using the scanning electron microscopy (SEM) technique. PMID:28817091

Methane hydrate formation in partially water-saturated Ottawa sand

USGS Publications Warehouse

Waite, W.F.; Winters, W.J.; Mason, D.H.

2004-01-01

Bulk properties of gas hydrate-bearing sediment strongly depend on whether hydrate forms primarily in the pore fluid, becomes a load-bearing member of the sediment matrix, or cements sediment grains. Our compressional wave speed measurements through partially water-saturated, methane hydrate-bearing Ottawa sands suggest hydrate surrounds and cements sediment grains. The three Ottawa sand packs tested in the Gas Hydrate And Sediment Test Laboratory Instrument (GHASTLI) contain 38(1)% porosity, initially with distilled water saturating 58, 31, and 16% of that pore space, respectively. From the volume of methane gas produced during hydrate dissociation, we calculated the hydrate concentration in the pore space to be 70, 37, and 20% respectively. Based on these hydrate concentrations and our measured compressional wave speeds, we used a rock physics model to differentiate between potential pore-space hydrate distributions. Model results suggest methane hydrate cements unconsolidated sediment when forming in systems containing an abundant gas phase.

Evaluation of pH at the Bacteria–Dental Cement Interface

PubMed Central

Mayanagi, G.; Igarashi, K.; Washio, J.; Nakajo, K.; Domon-Tawaraya, H.; Takahashi, N.

2011-01-01

Physiochemical assessment of the parasite-biomaterial interface is essential in the development of new biomaterials. The purpose of this study was to develop a method to evaluate pH at the bacteria-dental cement interface and to demonstrate physiochemical interaction at the interface. The experimental apparatus with a well (4.0 mm in diameter and 2.0 mm deep) was made of polymethyl methacrylate with dental cement or polymethyl methacrylate (control) at the bottom. Three representative dental cements (glass-ionomer, zinc phosphate, and zinc oxide-eugenol cements) were used. Each specimen was immersed in 2 mM potassium phosphate buffer for 10 min, 24 hrs, 1 wk, or 4 wks. The well was packed with Streptococcus mutans NCTC 10449, and a miniature pH electrode was placed at the interface between bacterial cells and dental cement. The pH was monitored after the addition of 1% glucose, and the fluoride contained in the cells was quantified. Glass-ionomer cement inhibited the bacteria-induced pH fall significantly compared with polymethyl methacrylate (control) at the interface (10 min, 5.16 ± 0.19 vs. 4.50 ± 0.07; 24 hrs, 5.20 ± 0.07 vs. 4.59 ± 0.11; 1 wk, 5.34 ± 0.14 vs. 4.57 ± 0.11; and 4 wks, 4.95 ± 0.27 vs. 4.40 ± 0.14), probably due to the fluoride released from the cement. This method could be useful for the assessment of pH at the parasite-biomaterial interface. PMID:21933936

Effect of endodontic cement on bone mineral density using serial dual-energy x-ray absorptiometry.

PubMed

Saghiri, Mohammad Ali; Orangi, Jafar; Tanideh, Nader; Janghorban, Kamal; Sheibani, Nader

2014-05-01

Materials with new compositions were tested in order to develop dental materials with better properties. Calcium silicate-based cements, including white mineral trioxide aggregate (WMTA), may improve osteopromotion because of their composition. Nano-modified cements may help researchers produce ideal root-end filling materials. Serial dual-energy x-ray absorptiometry measurement was used to evaluate the effects of particle size and the addition of tricalcium aluminate (C3A) to a type of mineral trioxide aggregate-based cement on bone mineral density and the surrounding tissues in the mandible of rabbits. Forty mature male rabbits (N = 40) were anesthetized, and a bone defect measuring 7 × 1 × 1 mm was created on the semimandible. The rabbits were divided into 2 groups, which were subdivided into 5 subgroups with 4 animals each based on the defect filled by the following: Nano-WMTA (patent application #13/211.880), WMTA (as standard), WMTA without C3A, Nano-WMTA + 2% Nano-C3A (Fujindonjnan Industrial Co, Ltd, Fujindonjnan Xiamen, China), and a control group. Twenty and forty days postoperatively, the animals were sacrificed, and the semimandibles were removed for DXA measurement. The Kruskal-Wallis test followed by the Mann-Whitney U test showed significant differences between the groups at a significance level of P < .05. P values calculated by the Kruskal-Wallis test were .002 for bone mineral density at both intervals and P20 day = .004 and P40 day = .005 for bone mineral content. This study showed that bone regeneration was enhanced by reducing the particle size (nano-modified) and C3A mixture. This may relate to the existence of an external supply of minerals and a larger surface area of nano-modified material, which may lead to faster release rate of Ca(2+), inducing bone formation. Adding Nano-C3A to Nano-WMTA may improve bone regeneration properties. Copyright © 2014 American Association of Endodontists. All rights reserved.

Solubility and disintegration of new calcium aluminate cement (EndoBinder) containing different radiopacifying agents.

PubMed

Garcia, Lucas da Fonseca Roberti; Chinelatti, Michelle Alexandra; Rossetto, Hebert Luis; Pires-de-Souza, Fernanda de Carvalho Panzeri

2014-02-01

The aim of this study was to evaluate the solubility and disintegration of EndoBinder (EB) containing 3 different radiopacifying agents, bismuth oxide (Bi2O3), zinc oxide (ZnO), or zirconium oxide (ZrO2), in comparison with gray mineral trioxide aggregate (GMTA) and white MTA (WMTA). Ten specimens of each cement were made in a stainless steel matrix (20 × 1.5 mm) according to Specification no. 57 of American National Standards Institute/American Dental Association: EB + Bi2O3, EB + ZrO, EB + ZnO, WMTA, and GMTA. The specimens were weighed on an accurate analytical scale and immersed in 50 mL distilled and deionized water at 37°C for 7 days. Afterwards, specimens were dried and weighed again to determine mass loss (%). Resulting solutions were analyzed in an atomic absorption spectrophotometer for identification and quantification of chemical elements released. All cements presented mean values of solubility and disintegration above the American National Standards Institute/American Dental Association Specification no. 57. EB + Bi2O3 presented the lowest mass loss (5.08%) and WMTA (6.65%) the highest, with no statistically significant difference (P > .05). The release of several chemical elements was observed, mostly metal ions. Only GMTA and EB + Bi2O3 showed the presence of Cr, with significant difference (P < .05). EB + ZnO presented the highest levels of Pb, followed by WMTA (P < .05). For As, the cements presented different release levels, with EB + ZnO showing the highest and GMTA the lowest levels (P < .05). However, the amounts of As and Pb released were lower than the safe limit proposed by ISO 9917-1. Irrespective of the radiopacifying agents used, EndoBinder presented similar behavior to MTA. Copyright © 2014 American Association of Endodontists. Published by Elsevier Inc. All rights reserved.

Physical properties of concrete made with Apollo 16 lunar soil sample

NASA Technical Reports Server (NTRS)

Lin, T. D.; Love, H.; Stark, D.

1992-01-01

This paper describes the first phase of the long-term investigation for the construction of concrete lunar bases. In this phase, petrographic and scanning electron microscope examinations showed that the morphology and elemental composition of the lunar soil made it suitable for use as a fine aggregate for concrete. Based on this finding, calcium aluminate cement and distilled water were mixed with the lunar soil to fabricate test specimens. The test specimens consisted of a 1-in cube, a 1/2-in cube, and three 0.12 x 0.58 x 3.15-in beam specimens. Tests were performed on these specimens to determine compressive strength, modulus of rupture, modulus of elasticity, and thermal coefficient of expansion. Based on examination of the material and test results, it is concluded that lunar soil can be used as a fine aggregate for concrete.

Relief inversion in the geomorphological evolution of sub-Saharan West Africa

NASA Astrophysics Data System (ADS)

Butt, C. R. M.; Bristow, A. P. J.

2013-03-01

The geomorphology of much of sub-Saharan West Africa is dominated by the presence of plateaux and plains with ferruginous and, locally, aluminous (bauxitic) duricrusts. The plateaux occur at different elevations and have been correlated as two or more palaeosurfaces across much of the region. The duricrusts have generally been considered to be residual, formed by conformable erosion and chemical wasting of immediately underlying bedrock. This concept has been central to interpretations as diverse as the formation and evolution of the landscape and the development of geochemical exploration models. Recent regolith landform mapping, field observations and experience from mineral exploration in southern Mali and Burkina Faso, however, demonstrate that the duricrusts are mainly ferricretes, i.e., Fe oxide-cemented sediments. These observations require a re-interpretation of the geomorphological evolution of the region during the Cenozoic. The landscape has evolved by several cycles of weathering and erosion-deposition, triggered by climatic, tectonic or other environmental changes. It is proposed that an initial bauxitic/lateritic regolith was partly eroded following uplift and/or a change to a more arid climate, and that the detritus, rather than being removed, was deposited on slopes and valleys. During a subsequent humid period of lateritic weathering, Fe oxide cementation of this detritus formed ferricrete. Dehydration and hardening of the ferricrete after further uplift or aridity increased its resistance to erosion, resulting in relief inversion, with the detritus, in turn, being deposited downslope. This too has been weathered and cemented, to form a younger ferricrete. The occurrence of ferricrete landforms in adjacent countries, noted by field observation and inferred from satellite imagery, demonstrates that relief inversion is a very widespread and important phenomenon in southern Mali, Burkina Faso and adjacent countries in semi-arid West Africa.

Effect of fabrication pressure on the fatigue performance of Cemex XL acrylic bone cement.

PubMed

Lewis, Gladius; Janna, S I

2004-01-01

During a cemented arthroplasty, the prepared polymerizing dough of acrylic bone cement is subjected to pressurization in a number of ways; first, during delivery into the freshly prepared bone bed, second, during packing in that bed (either digitally or with the aid of a mechanical device), and, third, during the insertion of the prosthesis. Only a few studies have reported on the influence of the level of pressurization experienced during these events (which, depending on the cementing technique used, has been put at between 8 and 273 kPa) on various properties of the cement. That was the focus of the present study, in which the fully reversed tension-compression (+/-15 MPa; 5 Hz) fatigue lives (expressed as number of cycles to fracture, N(f)) of rectangular cross-sectioned "dog-bone" specimens (Type V, per ASTM D 638) fabricated from Cemex XL cement, at pressure applied continuously to the cement dough during curing in the specimen mold, p=75,150, and 300 kPa, were determined. The N(f) results were analyzed using the linearized transformation of the three-parameter Weibull relationship to obtain estimates of the Weibull mean, N(WM), which was taken to be the index of fatigue performance of the specimen set. Over the range of p studied, N(WM) increased as p increased (for example, from 329,118 cycles when p was 75 kPa to 388,496 cycles when p was 300 kPa); however, the increase was not significant over any pair of p increment steps (Mann-Whitney U-test; alpha<0.05).

An ESEM investigation of latex film formation in cement pore solution

DOE Office of Scientific and Technical Information (OSTI.GOV)

Gretz, M.; Plank, J., E-mail: sekretariat@bauchemie.ch.tum.d

2011-02-15

Environmental scanning electron microscopy (ESEM) and complementary methods were employed to study the time dependent film formation of a latex dispersion in water and cement pore solution. First, a model carboxylated styrene/n-butyl acrylate latex dispersion possessing a minimum film forming temperature (MFFT) of 18 {sup o}C was synthesized in aqueous media via emulsion polymerization. Its film forming property was at a temperature of 40 {sup o}C, studied under an ESEM. The analysis revealed that upon removal of water, film formation occurs as a result of particle packing, particle deformation and finally particle coalescence. Film formation is significantly retarded when themore » latex dispersion is present in cement pore solution. This effect can be ascribed to adsorption of Ca{sup 2+} ions onto the surface of the anionic latex particles and to interfacial secondary phases. This layer of adsorbed Ca{sup 2+} ions hinders interdiffusion of the macromolecules and subsequent film formation of the latex polymer.« less

Estimating pore and cement volumes in thin section

USGS Publications Warehouse

Halley, R.B.

1978-01-01

Point count estimates of pore, grain and cement volumes from thin sections are inaccurate, often by more than 100 percent, even though they may be surprisingly precise (reproducibility + or - 3 percent). Errors are produced by: 1) inclusion of submicroscopic pore space within solid volume and 2) edge effects caused by grain curvature within a 30-micron thick thin section. Submicroscopic porosity may be measured by various physical tests or may be visually estimated from scanning electron micrographs. Edge error takes the form of an envelope around grains and increases with decreasing grain size and sorting, increasing grain irregularity and tighter grain packing. Cements are greatly involved in edge error because of their position at grain peripheries and their generally small grain size. Edge error is minimized by methods which reduce the thickness of the sample viewed during point counting. Methods which effectively reduce thickness include use of ultra-thin thin sections or acetate peels, point counting in reflected light, or carefully focusing and counting on the upper surface of the thin section.

40 CFR 721.10423 - Complex strontium aluminate, rare earth doped (generic).

Code of Federal Regulations, 2014 CFR

2014-07-01

... earth doped (generic). 721.10423 Section 721.10423 Protection of Environment ENVIRONMENTAL PROTECTION... New Uses for Specific Chemical Substances § 721.10423 Complex strontium aluminate, rare earth doped... substances identified generically as complex strontium aluminate, rare earth doped (PMNs P-12-22, P-12-23, P...

Occupational stress and strain in relation to personal protective equipment of Japanese firefighters assessed by a questionnaire.

PubMed

Son, Su-Young; Lee, Joo-Young; Tochihara, Yutaka

2013-01-01

The purpose of the present study was to elucidate differences in actual work environments, mobility and satisfaction between firefighters wearing aluminized and non-aluminized personal protective equipment (PPE), and to suggest a proper standard test method for Japanese firefighters' PPE. A survey from two cities in Japan (City A: aluminized PPE; City B: non aluminized PPE) was undertaken. A total of 525 firefighters from City A and 757 from City B participated. Firefighters spent 22.5 min (City A) and 27.3 min (City B) on average firefighting with the full set of PPE in one incident, but the heat strain experienced among firefighters from City A was twice that of firefighters from City B (57.5% and 28.4%). Firefighters spent 65.9 min on one incident and 24.2 min for suppression of fire with the full set of PPE on average. The toughest task that caused physical strain in City A was 'stair climbing' and in City B was 'drawing up a hose filled with water'. The most restricted body region due to PPE was the knee for both groups. Evaluations revealed that the aluminized fire jacket had worse ventilation and mobility than the non-aluminized, while the non-aluminized one received with more unfavorable evaluations for water resistance and maintainability.

Development of oxidation resistance in thoriated nickel-chromium base alloys

NASA Technical Reports Server (NTRS)

Seltzer, M. S.; Wilcox, B. A.; Jaffee, R. I.; Stringer, J.

1971-01-01

A pack process was developed which permits the introduction of nearly six weight percent aluminum into solid solution in the near-surface region of TDNiCr (Ni-20Cr-2ThO2. At this aluminum concentration an adherent alumina scale is produced on the alloy surface upon exposure to an environment of 1330 n/sq m (10 torr) or 101,000 n/sq m (760 torr) air at temperatures of 1093 C (2000 F) and 1204 C (2200 F). Room temperature mechanical properties of the aluminized alloys compare favorably with those of TDNiCr as received. While diffusivities for aluminum are a factor of three higher than those for chromium in TDNiCr or Ni-20Cr, the diffusion rates are similar for either of these elements in the thoriated or unthoriated alloy for a given temperature and grain size.

Diagenetic history of the Surma Group sandstones (Miocene) in the Surma Basin, Bangladesh

NASA Astrophysics Data System (ADS)

Rahman, M. Julleh Jalalur; McCann, Tom

2012-02-01

This study examines the various diagenetic controls of the Miocene Surma Group sandstones encountered in petroleum exploration wells from the Surma Basin, which is situated in the northeastern part of the Bengal Basin, Bangladesh. The principal diagenetic minerals/cements in the Surma Group sandstones are Fe-carbonates (with Fe-calcite dominating), quartz overgrowths and authigenic clays (predominantly chlorite, illite-smectite and minor kaolin). The isotopic composition of the carbonate cement revealed a narrow range of δ 18O values (-10.3‰ to -12.4‰) and a wide range of δ 13C value (+1.4‰ to -23.1‰). The δ 13C VPDB and δ 18O VPDB values of the carbonate cements reveal that carbon was most likely derived from the thermal maturation of organic matter during burial, as well as from the dissolution of isolated carbonate clasts and precipitated from mixed marine-meteoric pore waters. The relationship between the intergranular volume (IGV) versus cement volume indicates that compaction played a more significant role than cementation in destroying the primary porosity. However, cementation also played a major role in drastically reducing porosity and permeability in sandstones with poikilotopic, pore-filling blocky cements formed in early to intermediate and deep burial areas. In addition to Fe-carbonate cements, various clay minerals including illite-smectite and chlorite occur as pore-filling and pore-lining authigenic phases. Significant secondary porosity has been generated at depths from 2500 m to 4728 m. The best reservoir rocks found at depths of 2500-3300 m are well sorted, relatively coarse grained; more loosely packed and better rounded sandstones having good porosities (20-30%) and high permeabilities (12-6000 mD). These good quality reservoir rocks are, however, not uniformly distributed and can be considered to be compartmentalized as a result of interbedding with sandstone layers of low to moderate porosities, low permeabilities owing to poor sorting and extensive compaction and cementation.

Determination of Chlorinated Solvent Sorption by Porous Material-Application to Trichloroethene Vapor on Cement Mortar.

PubMed

Musielak, Marion; Brusseau, Mark L; Marcoux, Manuel; Morrison, Candice; Quintard, Michel

2014-08-01

Experiments have been performed to investigate the sorption of trichloroethene (TCE) vapor by concrete material or, more specifically, the cement mortar component. Gas-flow experiments were conducted using columns packed with small pieces of cement mortar obtained from the grinding of typical concrete material. Transport and retardation of TCE at high vapor concentrations (500 mg L -1 ) was compared to that of a non-reactive gas tracer (Sulfur Hexafluoride, SF6). The results show a large magnitude of retardation (retardation factor = 23) and sorption (sorption coefficient = 10.6 cm 3 g -1 ) for TCE, compared to negligible sorption for SF6. This magnitude of sorption obtained with pollutant vapor is much bigger than the one obtained for aqueous-flow experiments conducted for water-saturated systems. The considerable sorption exhibited for TCE under vapor-flow conditions is attributed to some combination of accumulation at the air-water interface and vapor-phase adsorption, both of which are anticipated to be significant for this system given the large surface area associated with the cement mortar. Transport of both SF6 and TCE was simulated successfully with a two-region physical non-equilibrium model, consistent with the dual-medium structure of the crushed cement mortar. This work emphasizes the importance of taking into account sorption phenomena when modeling transport of volatile organic compounds through concrete material, especially in regard to assessing vapor intrusion.

Prediction of the explosion effect of aluminized explosives

NASA Astrophysics Data System (ADS)

Zhang, Qi; Xiang, Cong; Liang, HuiMin

2013-05-01

We present an approach to predict the explosion load for aluminized explosives using a numerical calculation. A code to calculate the species of detonation products of high energy ingredients and those of the secondary reaction of aluminum and the detonation products, velocity of detonation, pressure, temperature and JWL parameters of aluminized explosives has been developed in this study. Through numerical calculations carried out with this code, the predicted JWL parameters for aluminized explosives have been compared with those measured by the cylinder test. The predicted JWL parameters with this code agree with those measured by the cylinder test. Furthermore, the load of explosion for the aluminized explosive was calculated using the numerical simulation by using the JWL equation of state. The loads of explosion for the aluminized explosive obtained using the predicted JWL parameters have been compared with those using the measured JWL parameters. Both of them are almost the same. The numerical results using the predicted JWL parameters show that the explosion air shock wave is the strongest when the mass fraction of aluminum powder in the explosive mixtures is 30%. This result agrees with the empirical data.

Method of preparing electrolyte for use in fuel cells

DOEpatents

Kinoshita, Kimio; Ackerman, John P.

1978-01-01

An electrolyte compact for fuel cells includes a particulate support material of lithium aluminate that contains a mixture of alkali metal compounds, such as carbonates or hydroxides, as the active electrolyte material. The porous lithium aluminate support structure is formed by mixing alumina particles with a solution of lithium hydroxide and another alkali metal hydroxide, evaporating the solvent from the solution and heating to a temperature sufficient to react the lithium hydroxide with alumina to form lithium aluminate. Carbonates are formed by reacting the alkali metal hydroxides with carbon dioxide gas in an exothermic reaction which may proceed simultaneously with the formation with the lithium aluminate. The mixture of lithium aluminate and alkali metal in an electrolyte active material is pressed or otherwise processed to form the electrolyte structure for assembly into a fuel cell.

Interdiffusion behaviors of iron aluminide coatings on China low activation martensitic steel

NASA Astrophysics Data System (ADS)

Zhu, X. X.; Yang, H. G.; Yuan, X. M.; Zhao, W. W.; Zhan, Q.

2014-12-01

The iron aluminide coating on China Low Activation Martensitic (CLAM) steel was prepared by pack cementation and subsequent heat treatment. A surface Fe2Al5 layer was formed on CLAM substrate by pack cementation process with Fe2Al5 donor powder and NH4Cl activator. Diffusion heat treatment was performed in order to allow the phase transformation from Fe2Al5 to a phase with lower aluminum content. Morphology and composition of the coatings were characterized by optical microscopy (OM), scanning electron microscopy (SEM) equipped with energy dispersive spectroscopy (EDS), glow discharge optical emission spectroscopy (GDOES) and X-ray diffraction (XRD). There is a need to study the interdiffusion behaviors in these Al containing systems, as a basis for controlling the formation and subsequent degradation of the coating. In this paper, a predictive model was developed to describe the phase transformation of Fe2Al5 as a function of processing parameters. The Wagner's equation was used to calculate the interdiffusion coefficients based on the analysis of the Al concentration profiles. The results showed that the interdiffusion coefficients in the FeAl and α-Fe(Al) phase strongly depends on Al content and showed a maximum at about 28 at.% Al.

Stylolitization as source of cement in Mississippian Salem Limestone, west-central Indiana

DOE Office of Scientific and Technical Information (OSTI.GOV)

Finkel, E.A.; Wilkinson, B.H.

The Mississippian Salem Limestone of west-central Indiana is a homogeneous cross-bedded grainstone containing numerous stylolites with amplitudes ranging up to 25 cm. Petrographic and geochemical analyses of closely spaced samples from four 1-m thick stylolite-bounded units document spatial trends in grainstone texture and composition, which correlate with proximity to bounding solution seams. Textural data indicate that stylolitization was locally preceded by grain compaction and that seam solution preferentially occurred within layers where grain packing was tightest. Amount of cement largely corresponds to volume of available pore space, and remaining porosity varies inversely to stylolite proximity. Trace-element compositions demonstrate that intergranularmore » spar is enriched in Mn and depleted in Mg relative to grains, and suggest a significant contribution of carbonate cement to grainstone pores from bounding solution seams. Data on grainstone and stylolite insoluble contents indicate that stylolite amplitude records 43% of actual section shortening. On average, seam solution within the Salem Limestone could have provided no less than 47% and no more than 90% of the CaCO{sub 3}, Fe, and Mn mass now in grainstone pores as intergranular spar cement. As such, stylolitization has played an important role during burial diagenesis, porosity occlusion, and permeability reduction within this Mississippian grainstone sequence. 17 figs., 1 tab.« less

A safer disposal of hazardous phosphate coating sludge by formation of an amorphous calcium phosphate matrix.

PubMed

Navarro-Blasco, I; Duran, A; Pérez-Nicolás, M; Fernández, J M; Sirera, R; Alvarez, J I

2015-08-15

Phosphate coating hazardous wastes originated from the automotive industry were efficiently encapsulated by an acid-base reaction between phosphates present in the sludge and calcium aluminate cement, yielding very inert and stable monolithic blocks of amorphous calcium phosphate (ACP). Two different compositions of industrial sludge were characterized and loaded in ratios ranging from 10 to 50 wt.%. Setting times and compressive strengths were recorded to establish the feasibility of this method to achieve a good handling and a safe landfilling of these samples. Short solidification periods were found and leaching tests showed an excellent retention for toxic metals (Zn, Ni, Cu, Cr and Mn) and for organic matter. Retentions over 99.9% for Zn and Mn were observed even for loadings as high as 50 wt.% of the wastes. The formation of ACP phase of low porosity and high stability accounted for the effective immobilization of the hazardous components of the wastes. Copyright © 2015 Elsevier Ltd. All rights reserved.

Reuse of ultrafine mineral wool production waste in the manufacture of refractory concrete.

PubMed

Stonys, R; Kuznetsov, D; Krasnikovs, A; Škamat, J; Baltakys, K; Antonovič, V; Černašėjus, O

2016-07-01

The paper deals with the mineral wool production waste (cupola dust - CD), presents CD characterization and aims to reuse CD in production of refractory concrete with calcium aluminate cement. The study of CD covers its chemical, phase and thermal analyses along with the morphological study and determination of particles size distribution. Zeta-potential, electrical conductivity and pH values of CD suspension are presented in the paper as well. Commercial microsilica additive in refractory concrete has been replaced with cupola dust. Compositions of refractory concrete have been prepared by incorporating 1%, 2% and 3% of CD. The bulk density, ultrasonic wave velocity, cold crushing strength and thermal shock resistance of the created refractory concrete have been determined. Based on experimental results, it has been found that cupola dust may be used for the production of refractory concrete. The environmental impact related to the CD reuse in refractory concrete production has been evaluated as well. Copyright © 2016 Elsevier Ltd. All rights reserved.

Shock Initiation Characteristics of an Aluminized DNAN/RDX Melt-Cast Explosive

NASA Astrophysics Data System (ADS)

Cao, Tong-Tang; Zhou, Lin; Zhang, Xiang-Rong; Zhang, Wei; Miao, Fei-Chao

2017-10-01

Shock sensitivity is one of the key parameters for newly developed, 2,4-dinitroanisole (DNAN)-based, melt-cast explosives. For this paper, a series of shock initiation experiments were conducted using a one-dimensional Lagrangian system with a manganin piezoresistive pressure gauge technique to evaluate the shock sensitivity of an aluminized DNAN/cyclotrimethylenetrinitramine (RDX) melt-cast explosive. This study fully investigated the effects of particle size distributions in both RDX and aluminum, as well as the RDX's crystal quality on the shock sensitivity of the aluminized DNAN/RDX melt-cast explosive. Ultimately, the shock sensitivity of the aluminized DNAN/RDX melt-cast explosives increases when the particle size decreases in both RDX and aluminum. Additionally, shock sensitivity increases when the RDX's crystal quality decreases. In order to simulate these effects, an Ignition and Growth (I&G) reactive flow model was calibrated. This calibrated I&G model was able to predict the shock initiation characteristics of the aluminized DNAN/RDX melt-cast explosive.

Synthesis of magnesium aluminate spinel by periclase and alumina chlorination

DOE Office of Scientific and Technical Information (OSTI.GOV)

Orosco, Pablo, E-mail: porosco@unsl.edu.ar; Facultad de Química, Bioquímica y Farmacia, Universidad Nacional de San Luis Chacabuco y Pedernera, San Luis; Barbosa, Lucía

2014-11-15

Highlights: • Use of chlorination for the synthesis of magnesium aluminate spinel. • The reagents used were alumina, periclase and chlorine. • Isothermal and non-isothermal assays were performed in air and Cl{sub 2}–N{sub 2} flows. • The chlorination produced magnesium aluminate spinel at 700 °C. • Selectivity of the chlorination reaction to obtain spinel is very high. - Abstract: A pyrometallurgical route for the synthesis of magnesium aluminate spinel by thermal treatment of a mechanical mixture containing 29 wt% MgO (periclase) and 71 wt% Al{sub 2}O{sub 3} (alumina) in chlorine atmosphere was developed and the results were compared with thosemore » obtained by calcining the same mixture of oxides in air atmosphere. Isothermal and non-isothermal assays were performed in an experimental piece of equipment adapted to work in corrosive atmospheres. Both reagents and products were analyzed by differential thermal analysis (DTA), X-ray diffraction (XRD) and X-ray fluorescence (XRF). Thermal treatment in Cl{sub 2} atmosphere of the MgO–Al{sub 2}O{sub 3} mixture produces magnesium aluminate spinel at 700 °C, while in air, magnesium spinel is generated at 930 °C. The synthesis reaction of magnesium aluminate spinel was complete at 800 °C.« less

Multicale modeling of the detonation of aluminized explosives using SPH-MD-QM method

NASA Astrophysics Data System (ADS)

Peng, Qing; Wang, Guangyu; Liu, Gui-Rong; de, Suvranu

Aluminized explosives have been applied in military industry since decades ago. Compared with ideal explosives, aluminized explosives feature both fast detonation and slow metal combustion chemistry, generating a complex multi-phase reactive flow. Here, we introduce a sequential multiscale model of SPH-MD-QM to simulate the detonation behavior of aluminized explosives. At the bottom level, first-principles quantum mechanics (QM) calculations are employed to obtain the training sets for fitting the ReaxFF potentials, which are used in turn in the reactive molecular dynamics (MD) simulations in the middle level to obtain the chemical reaction rates and equations of states. At the up lever, a smooth particle hydrodynamics (SPH) method incorporated ignition and growth model and afterburning model has been used for the simulation of the detonation and combustion of the aluminized explosive. Simulation is compared with experiment and good agreement is observed. The proposed multiscale method of SPH-MD-QM could be used to optimize the performance of aluminized explosives. The authors would like to acknowledge the generous financial support from the Defense Threat Reduction Agency (DTRA) Grant No. HDTRA1-13-1-0025 and the Office of Naval Research Grants ONR Award No. N00014-08-1-0462 and No. N00014-12-1-0527.

Quantitative analysis for the determination of aluminum percentage and detonation performance of aluminized plastic bonded explosives by laser-induced breakdown spectroscopy

NASA Astrophysics Data System (ADS)

Rezaei, A. H.; Keshavarz, M. H.; Kavosh Tehrani, M.; Darbani, S. M. R.

2018-06-01

The aluminized plastic-bonded explosive (PBX) is a composite material in which solid explosive particles are dispersed in a polymer matrix, which includes three major components, i.e. polymeric binder, metal fuel (aluminum) and nitramine explosive. This work introduces a new method on the basis of the laser-induced breakdown spectroscopy (LIBS) technique in air and argon atmospheres to investigate the determination of aluminum content and detonation performance of aluminized PBXs. Plasma emissions of aluminized PBXs are recorded where atomic lines of Al, C and H as well as molecular bands of AlO and CN are identified. The experimental results demonstrate that a good discrimination and separation between the aluminized PBXs is possible using LIBS and principle component analysis, although they have similar atomic composition. Relative intensity of the AlO/Al is used to determine aluminum percentage of the aluminized PBXs. The obtained quantitative calibration curve using the relative intensity of the AlO/Al is better than the resulting calibration curve using only the intensity of Al. By using the LIBS method and the measured intensity ratio of CN/C, an Al content of 15% is found to be the optimum value in terms of velocity of detonation of the RDX/Al/HTPB standard samples.

Effect of Tricalcium Aluminate on the Physicochemical Properties, Bioactivity, and Biocompatibility of Partially Stabilized Cements

PubMed Central

Chang, Kai-Chun; Chang, Chia-Chieh; Huang, Ying-Chieh; Chen, Min-Hua; Lin, Feng-Huei; Lin, Chun-Pin

2014-01-01

Background/Purpose Mineral Trioxide Aggregate (MTA) was widely used as a root-end filling material and for vital pulp therapy. A significant disadvantage to MTA is the prolonged setting time has limited the application in endodontic treatments. This study examined the physicochemical properties and biological performance of novel partially stabilized cements (PSCs) prepared to address some of the drawbacks of MTA, without causing any change in biological properties. PSC has a great potential as the vital pulp therapy material in dentistry. Methods This study examined three experimental groups consisting of samples that were fabricated using sol-gel processes in C3S/C3A molar ratios of 9/1, 7/3, and 5/5 (denoted as PSC-91, PSC-73, and PSC-55, respectively). The comparison group consisted of MTA samples. The setting times, pH variation, compressive strength, morphology, and phase composition of hydration products and ex vivo bioactivity were evaluated. Moreover, biocompatibility was assessed by using lactate dehydrogenase to determine the cytotoxicity and a cell proliferation (WST-1) assay kit to determine cell viability. Mineralization was evaluated using Alizarin Red S staining. Results Crystalline phases, which were determined using X-ray diffraction analysis, confirmed that the C3A contents of the material powder differed. The initial setting times of PSC-73 and PSC-55 ranged between 15 and 25 min; these values are significantly (p<0.05, ANOVA and post-hoc test) lower than those obtained for MTA (165 min) and PSC-91 (80.5 min). All of the PSCs exhibited ex vivo bioactivity when immersed in simulated body fluid. The biocompatibility results for all of the tested cements were as favorable as those of the negative control, except for PSC-55, which exhibited mild cytotoxicity. Conclusion PSC-91 is a favorable material for vital pulp therapy because it exhibits optimal compressive strength, a short setting time, and high biocompatibility and bioactivity. PMID:25247808

Role of Grain Crushing in the Alteration of Mechanical and Flow Properties of Sandstones during Mechanical Failure

NASA Astrophysics Data System (ADS)

Mirabolghasemi, M.; Prodanovic, M.; Choens, R. C., II; Dewers, T. A.

2016-12-01

We present a workflow to study the alteration of flow and mechanical characteristics of sandstones after shear failure, specifically modeling weakening of the formation due to CO2 injection. We use discrete elements method (DEM) to represent each sand grain as a cluster of bonded sub-particles, and model their potential crushing. We also introduce bonds between sand grain clusters to enable the modeling of the mechanical behavior of consolidated sandstones. The model is tuned by comparing our numerical compression tests on single sand grains with the experimental results reported in the literature. Once the mechanical behavior of individual grains is adequately captured by the model, a packing of such grains is subjected to shear stress. Once the packing fails under the imposed shear stress, its mechanical properties, permeability, and porosity are calculated. This test is repeated for various conditions by varying parameters such as the brittleness of single grains (the relative quartz-feldspar content of the grains), normal stress, and cement strength (assuming (chemical) weakening of the inter- and intra-grain-cluster bonds due to CO2 injection). We specifically compare the effect of cement/bond strength weakening on mechanical properties to triaxial compression experimental measurements before and after hydrous scCO2 and CO2-saturated brine injection in Boise sandstone performed in Sandia National Laboratory.

Anticorrosion performance of chromized coating prepared by pack cementation in simulated solution with H2S and CO2

NASA Astrophysics Data System (ADS)

Wang, Qin-Ying; Behnamian, Yashar; Luo, Hong; Wang, Xian-Zong; Leitch, Michael; Zeng, Hongbo; Luo, Jing-Li

2017-10-01

A hash service environment containing H2S and CO2 in oil industry usually causes corrosion of carbon steel. In this study, the chromized coatings with different deposited time were prepared on the surface of carbon steel by the method of pack cementation to enhance its corrosion resistance. Then the microstructure, hardness, corrosion resistance as well as the semiconductor behavior of coatings in the simulated solution with saturated H2S and CO2 were investigated. The results show that the content of Cr in coating was increased by prolonging deposited time, and both chromium carbides and chromium nitrides were formed. Furthermore, coatings display higher polarization resistance, Rp, than that of the substrate, indicating a higher resistance to charge transfer on coating surface. The corrosion rates of coatings with different deposited time were significantly lower than that of substrate. Chemical analysis showed the formation of heavy sulfides on the surface of substrates after corrosion, while the least corrosion products were detected on the surface of coating with deposited time of 12 h. Mott-Schottky results indicated that coating of 12 h displayed less defects than the other two coatings with deposited time of 4 h and 8 h, which will be beneficial to improve corrosion resistance. The investigation showed that chromized coatings exhibited high corrosion resistance and owned a potential application in oil industry for corrosion prevention.

A case report: reconstruction of a damaged knee following treatment of giant cell tumor of the proximal tibia with cryosurgery and cementation.

PubMed

Wakitani, S; Imoto, K; Saito, M; Yamamoto, T; Kawabata, H

2002-05-01

Reconstruction of a knee damaged by cement packed to cure a giant-cell tumor is sometimes difficult. We reconstructed such a knee by removal of the cement, autologous bone transplantation and distraction osteogenesis using the Ilizarov apparatus. In this paper the results 29 months after the salvage surgery are given. We saw a 31-year-old woman's knee joint that showed osteoarthritic change after curettage, cryosurgery and cementation performed 4 years previously for a giant-cell tumor of the proximal tibia. We reconstructed the knee joint. This procedure included cement removal, alignment correction by tibial osteotomy, subchondral bone reconstruction by autologous bone transplantation, and filling the defect after removing the bone cement by elongating the diaphysis using the Ilizarov apparatus. Distraction was terminated 4 months later when 54 mm of elongation was performed. All devices were removed 12 months after the surgery. Seventeen months after the removal of the apparatus, the range of motion of the right knee was 0 degrees extension and 110 degrees flexion, and the patient was able to walk without pain. Although the treatment period is long and there may be some complications of Ilizarov lengthening and distraction osteogenesis, this procedure has numerous benefits. Bony defects can be soundly reconstructed and, at the same time, the alignment of the knee can be corrected. Also it is not necessary to reconstruct the ligaments because the insertions are intact. If osteoarthritis progresses, a surface type total knee replacement can be performed, not constrained type prosthesis, which would be used if the bony structure had not been reconstructed. This procedure may be one of the candidates for reconstructing such knee joints destroyed by bone cement. Copyright 2002 OsteoArthritis Research Society International. Published by Elsevier Science Ltd. All rights reserved.

The optimization of concrete mixtures for use in highway applications

NASA Astrophysics Data System (ADS)

Moini, Mohamadreza

Portland cement concrete is most used commodity in the world after water. Major part of civil and transportation infrastructure including bridges, roadway pavements, dams, and buildings is made of concrete. In addition to this, concrete durability is often of major concerns. In 2013 American Society of Civil Engineers (ASCE) estimated that an annual investment of 170 billion on roads and 20.5 billion for bridges is needed on an annual basis to substantially improve the condition of infrastructure. Same article reports that one-third of America's major roads are in poor or mediocre condition [1]. However, portland cement production is recognized with approximately one cubic meter of carbon dioxide emission. Indeed, the proper and systematic design of concrete mixtures for highway applications is essential as concrete pavements represent up to 60% of interstate highway systems with heavier traffic loads. Combined principles of material science and engineering can provide adequate methods and tools to facilitate the concrete design and improve the existing specifications. In the same manner, the durability must be addressed in the design and enhancement of long-term performance. Concrete used for highway pavement applications has low cement content and can be placed at low slump. However, further reduction of cement content (e.g., versus current specifications of Wisconsin Department of Transportation to 315-338 kg/m 3 (530-570 lb/yd3) for mainstream concrete pavements and 335 kg/m3 (565 lb/yd3) for bridge substructure and superstructures) requires delicate design of the mixture to maintain the expected workability, overall performance, and long-term durability in the field. The design includes, but not limited to optimization of aggregates, supplementary cementitious materials (SCMs), chemical and air-entraining admixtures. This research investigated various theoretical and experimental methods of aggregate optimization applicable for the reduction of cement content. Conducted research enabled further reduction of cement contents to 250 kg/m3 (420 lb/yd3) as required for the design of sustainable concrete pavements. This research demonstrated that aggregate packing can be used in multiple ways as a tool to optimize the aggregates assemblies and achieve the optimal particle size distribution of aggregate blends. The SCMs, and air-entraining admixtures were selected to comply with existing WisDOT performance requirements and chemical admixtures were selected using the separate optimization study excluded from this thesis. The performance of different concrete mixtures was evaluated for fresh properties, strength development, and compressive and flexural strength ranging from 1 to 360 days. The methods and tools discussed in this research are applicable, but not limited to concrete pavement applications. The current concrete proportioning standards such as ACI 211 or current WisDOT roadway standard specifications (Part 5: Structures, Section 501: Concrete) for concrete have limited or no recommendations, methods or guidelines on aggregate optimization, the use of ternary aggregate blends (e.g., such as those used in asphalt industry), the optimization of SCMs (e.g., class F and C fly ash, slag, metakaolin, silica fume), modern superplasticizers (such as polycarboxylate ether, PCE) and air-entraining admixtures. This research has demonstrated that the optimization of concrete mixture proportions can be achieved by the use and proper selection of optimal aggregate blends and result in 12% to 35% reduction of cement content and also more than 50% enhancement of performance. To prove the proposed concrete proportioning method the following steps were performed: • The experimental aggregate packing was investigated using northern and southern source of aggregates from Wisconsin; • The theoretical aggregate packing models were utilized and results were compared with experiments; • Multiple aggregate optimization methods (e.g., optimal grading, coarseness chart) were studied and compared to aggregate packing results and performance of experimented concrete mixtures; • Optimal aggregate blends were selected and used for concrete mixtures; • The optimal dosage of admixtures were selected for three types of plasticizing and superplasticizing admixtures based on a separately conducted study; • The SCM dosages were selected based on current WisDOT specifications; • The optimal air-entraining admixture dosage was investigated based on performance of preliminary concrete mixtures; • Finally, optimal concrete mixtures were tested for fresh properties, compressive strength development, modulus of rupture, at early ages (1day) and ultimate ages (360 days). • Durability performance indicators for optimal concrete mixtures were also tested for resistance of concrete to rapid chloride permeability (RCP) at 30 days and 90 days and resistance to rapid freezing and thawing at 56 days.

Quantitative description of yttrium aluminate ceramic composition by means of Er+3 microluminescence spectrum

NASA Astrophysics Data System (ADS)

Videla, F. A.; Tejerina, M. R.; Moreira-Osorio, L.; Conconi, M. S.; Orzi, D. J. O.; Flores, T.; Ponce, L. V.; Bilmes, G. M.; Torchia, G. A.

2018-05-01

The composition of erbium-doped yttrium aluminate ceramics was analyzed by means of confocal luminescence spectroscopy, EDX, and X-ray diffraction. A well-defined linear correlation was found between a proposed estimator computed from the luminescence spectrum and the proportion of ceramic phases coexisting in different samples. This result shows the feasibility of using erbium luminescence spectroscopy to perform a quantitative determination of different phases of yttrium aluminates within a micrometric region in nanograined ceramics.

Pack Cementation Aluminide Coatings on Superalloys: Codeposition of Cr and Reactive Elements (RE). Technical Report 1. Chromium and Reactive Element(RE)- Modified Aluminide Diffusion Coatings on Superalloys: Environmental Testing. Technical Report 2

DTIC Science & Technology

1992-11-01

Godlewska and K. Godlewski, Oxid. Met., 22 (1984) 117. 4. J.E. Restall, U.S. Patent #4,687,684 (1987). 5. P.N. Walsh, in Proceeding of the Fourth...McCarron, N.R. Lindblad, and D. Chatterji, Corrosion, 32 (1976) 476. 34 33. E. Godlewska and K. Godlewski, Oxid. Met., 22 (1984) 117. 34. B. Pieraggi

Le Châtelier's conjecture: Measurement of colloidal eigenstresses in chemically reactive materials

NASA Astrophysics Data System (ADS)

Abuhaikal, Muhannad; Ioannidou, Katerina; Petersen, Thomas; Pellenq, Roland J.-M.; Ulm, Franz-Josef

2018-03-01

Volume changes in chemically reactive materials, such as hydrating cement, play a critical role in many engineering applications that require precise estimates of stress and pressure developments. But a means to determine bulk volume changes in the absence of other deformation mechanisms related to thermal, pressure and load variations, is still missing. Herein, we present such a measuring devise, and a hybrid experimental-theoretical technique that permits the determination of colloidal eigenstresses. Applied to cementitious materials, it is found that bulk volume changes in saturated cement pastes at constant pressure and temperature conditions result from a competition of repulsive and attractive phenomena that originate from the relative distance of the solid particles - much as Henry Louis Le Châtelier, the father of modern cement science, had conjectured in the late 19th century. Precipitation of hydration products in confined spaces entails a repulsion, whereas the concurrent reduction in interparticle distance entails activation of attractive forces in charged colloidal particles. This cross-over from repulsion to attraction can be viewed as a phase transition between a liquid state (below the solid percolation) and the limit packing of hard spheres, separated by an energy barrier that defines the temperature-dependent eigenstress magnitude.

Method of preparing a sintered lithium aluminate structure for containing electrolyte

DOEpatents

Sim, James W.; Kinoshita, Kimio

1981-01-01

A porous sintered tile is formed of lithium aluminate for retaining molten lectrolyte within a fuel cell. The tile is prepared by reacting lithium hydroxide in aqueous solution with alumina particles to form beta lithium aluminate particles. The slurry is evaporated to dryness and the solids dehydrated to form a beta lithium aluminate powder. The powder is compacted into the desired shape and sintered at a temperature in excess of 1200 K. but less than 1900 K. to form a porous integral structure that is subsequently filled with molten electrolyte. A tile of this type is intended for use in containing molten alkali metal carbonates as electolyte for use in a fuel cell having porous metal or metal oxide electrodes for burning a fuel gas such as hydrogen and/or carbon monoxide with an oxidant gas containing oxygen.

Effects of grain size distribution on the packing fraction and shear strength of frictionless disk packings.

PubMed

Estrada, Nicolas

2016-12-01

Using discrete element methods, the effects of the grain size distribution on the density and the shear strength of frictionless disk packings are analyzed. Specifically, two recent findings on the relationship between the system's grain size distribution and its rheology are revisited, and their validity is tested across a broader range of distributions than what has been used in previous studies. First, the effects of the distribution on the solid fraction are explored. It is found that the distribution that produces the densest packing is not the uniform distribution by volume fractions as suggested in a recent publication. In fact, the maximal packing fraction is obtained when the grading curve follows a power law with an exponent close to 0.5 as suggested by Fuller and Thompson in 1907 and 1919 [Trans Am. Soc. Civ. Eng. 59, 1 (1907) and A Treatise on Concrete, Plain and Reinforced (1919), respectively] while studying mixtures of cement and stone aggregates. Second, the effects of the distribution on the shear strength are analyzed. It is confirmed that these systems exhibit a small shear strength, even if composed of frictionless particles as has been shown recently in several works. It is also found that this shear strength is independent of the grain size distribution. This counterintuitive result has previously been shown for the uniform distribution by volume fractions. In this paper, it is shown that this observation keeps true for different shapes of the grain size distribution.

Results of Characterization and Retrieval Testing on Tank 241-C-109 Heel Solids

DOE Office of Scientific and Technical Information (OSTI.GOV)

Callaway, William S.

Eight samples of heel solids from tank 241-C-109 were delivered to the 222-S Laboratory for characterization and dissolution testing. After being drained thoroughly, one-half to two-thirds of the solids were off-white to tan solids that, visually, were fairly evenly graded in size from coarse silt (30-60 μm) to medium pebbles (8-16 mm). The remaining solids were mostly strongly cemented aggregates ranging from coarse pebbles (16-32 mm) to fine cobbles (6-15 cm) in size. Solid phase characterization and chemical analysis indicated that the air-dry heel solids contained ≈58 wt% gibbsite [Al(OH){sub 3}] and ≈37 wt% natrophosphate [Na{sub 7}F(PO{sub 4}){sub 2}·19H{sub 2}O].more » The strongly cemented aggregates were mostly fine-grained gibbsite cemented with additional gibbsite. Dissolution testing was performed on two test samples. One set of tests was performed on large pieces of aggregate solids removed from the heel solids samples. The other set of dissolution tests was performed on a composite sample prepared from well-drained, air-dry heel solids that were crushed to pass a 1/4-in. sieve. The bulk density of the composite sample was 2.04 g/mL. The dissolution tests included water dissolution followed by caustic dissolution testing. In each step of the three-step water dissolution tests, a volume of water approximately equal to 3 times the initial volume of the test solids was added. In each step, the test samples were gently but thoroughly mixed for approximately 2 days at an average ambient temperature of 25 °C. The caustic dissolution tests began with the addition of sufficient 49.6 wt% NaOH to the water dissolution residues to provide ≈3.1 moles of OH for each mole of Al estimated to have been present in the starting composite sample and ≈2.6 moles of OH for each mole of Al potentially present in the starting aggregate sample. Metathesis of gibbsite to sodium aluminate was then allowed to proceed over 10 days of gentle mixing of the test samples at temperatures ranging from 26-30 °C. The metathesized sodium aluminate was then dissolved by addition of volumes of water approximately equal to 1.3 times the volumes of caustic added to the test slurries. Aluminate dissolution was allowed to proceed for 2 days at ambient temperatures of ≈29 °C. Overall, the sequential water and caustic dissolution tests dissolved and removed 80.0 wt% of the tank 241-C-109 crushed heel solids composite test sample. The 20 wt% of solids remaining after the dissolution tests were 85-88 wt% gibbsite. If the density of the residual solids was approximately equal to that of gibbsite, they represented ≈17 vol% of the initial crushed solids composite test sample. In the water dissolution tests, addition of a volume of water ≈6.9 times the initial volume of the crushed solids composite was sufficient to dissolve and recover essentially all of the natrophosphate present. The ratio of the weight of water required to dissolve the natrophosphate solids to the estimated weight of natrophosphate present was 8.51. The Environmental Simulation Program (OLI Systems, Inc., Morris Plains, New Jersey) predicts that an 8.36 w/w ratio would be required to dissolve the estimated weight of natrophosphate present in the absence of other components of the heel solids. Only minor amounts of Al-bearing solids were removed from the composite solids in the water dissolution tests. The caustic metathesis/aluminate dissolution test sequence, executed at temperatures ranging from 27-30 °C, dissolved and recovered ≈69 wt% of the gibbsite estimated to have been present in the initial crushed heel solids composite. This level of gibbsite recovery is consistent with that measured in previous scoping tests on the dissolution of gibbsite in strong caustic solutions. Overall, the sequential water and caustic dissolution tests dissolved and removed 80.3 wt% of the tank 241-C-109 aggregate solids test sample. The residual solids were 92-95 wt% gibbsite. Only a minor portion (≈4.5 wt%) of the aggregate solids was dissolved and recovered in the water dissolution test. Other than some smoothing caused by continuous mixing, the aggregates were essentially unaffected by the water dissolution tests. During the caustic metathesis/aluminate dissolution test sequence, ≈81 wt% of the gibbsite estimated to have been present in the aggregate solids was dissolved and recovered. The pieces of aggregate were significantly reduced in size but persisted as distinct pieces of solids. The increased level of gibbsite recovery, as compared to that for the crushed heel solids composite, suggests that the way the gibbsite solids and caustic solution are mixed is a key determinant of the overall efficiency of gibbsite dissolution and recovery. The liquids recovered after the caustic dissolution tests on the crushed solids composite and the aggregate solids were observed for 170 days. No precipitation of gibbsite was observed. The distribution of particle sizes in the residual solids recovered following the dissolution tests on the crushed heel solids composite was characterized. Wet sieving indicated that 21.4 wt% of the residual solids were >710 μm in size, and laser light scattering indicated that the median equivalent spherical diameter in the <710-μm solids was 35 μm. The settling behavior of the residual solids following the large-scale dissolution tests was also studied. When dispersed at a concentration of ≈1 vol% in water, ≈24 wt% of the residual solids settled at a rate >0.43 in./s; ≈68 wt% settled at rates between 0.02 and 0.43 in./s; and ≈7 wt% settled slower than 0.02 in./s.« less

A drift chamber constructed of aluminized mylar tubes

NASA Astrophysics Data System (ADS)

Baringer, P.; Jung, C.; Ogren, H. O.; Rust, D. R.

1987-03-01

A thin reliable drift chamber has been constructed to be used near the interaction point of the PEP storage ring in the HRS detector. It is composed of individual drift tubes with aluminized mylar walls.

Classification and statistical analysis of mine spoils chemical composition from Oliete basin (Teruel, NE Spain)

NASA Astrophysics Data System (ADS)

Meseguer, S.; Sanfeliu, T.; Jordán, M. M.

2009-02-01

The Oliete basin (Early Cretaceous, NE Teruel, Spain) is one of the most important areas for the supply of mine spoils used as ball clays for the production of white and red stoneware in the Spanish ceramic industry of wall and floor tiles. This study corresponds to the second part of the paper published recently by Meseguer et al. (Environ Geol 2008) about the use of mine spoils from Teruel coal mining district. The present study shows a statistical data analysis from chemical data (major, minor and trace elements). The performed statistical analysis of chemical data included descriptive statistics and cluster analysis (with ANOVA and Scheffé methods). The cluster analysis of chemical data provided three main groups: C3 with the highest mean SiO2 content (66%) and lowest mean Al2O3 content (20%); C2 with lower SiO2 content (48%) and higher mean Al2O3 content (28%); and C1 with medium values for the SiO2 and Al2O3 mean content. The main applications of these materials are refractory, white and red ceramics, stoneware, heavy ceramics (including red earthenware, bricks and roof tiles), and components of white Portland cement and aluminous cement. Clays from group 2 are used in refractories (with higher kaolinite content, and constrictions to CaO + MgO and K2O + Na2O contents). All materials can be used in fine ceramics (white or red, according to the Fe2O3 + TiO2 content).

Eigenvalue Detonation of Combined Effects Aluminized Explosives

NASA Astrophysics Data System (ADS)

Capellos, C.; Baker, E. L.; Nicolich, S.; Balas, W.; Pincay, J.; Stiel, L. I.

2007-12-01

Theory and performance for recently developed combined—effects aluminized explosives are presented. Our recently developed combined-effects aluminized explosives (PAX-29C, PAX-30, PAX-42) are capable of achieving excellent metal pushing, as well as high blast energies. Metal pushing capability refers to the early volume expansion work produced during the first few volume expansions associated with cylinder and wall velocities and Gurney energies. Eigenvalue detonation explains the observed detonation states achieved by these combined effects explosives. Cylinder expansion data and thermochemical calculations (JAGUAR and CHEETAH) verify the eigenvalue detonation behavior.

Effect of aluminum substitution on the reflectance spectra of hematite

NASA Technical Reports Server (NTRS)

Morris, R. V.; Lauer, H. V., Jr.; Mendell, W. W.

1982-01-01

Hematite and aluminous hematite were synthesized and the diffuse reflectance spectra were recorded for the region between 0.35 and 1.20 microns. Results show that the near-IR based minimum for the aluminous hematite is shifted longward by about 0.02 microns and is much more shallow. Also, the aluminous specimen is considerably more reflective shortward of approximately 0.55 microns where the ferritic specimen is strongly absorbing. This is noteworthy since the visible slope and the red shoulder are often used in the construction of false color and band ratio images.

Corrosion of Spiral Rib Aluminized Pipe

DOT National Transportation Integrated Search

2012-08-01

Large diameter, corrugated steel pipes are a common sight in the culverts that run alongside many Florida roads. Spiral-ribbed aluminized pipe (SRAP) has been widely specified by the Florida Department of Transportation (FDOT) for runoff drainage. Th...

Corrosion of Spiral Rib Aluminized Pipe : [Summary

DOT National Transportation Integrated Search

2012-01-01

Large diameter, corrugated steel pipes are a common sight in the culverts that run alongside many Florida roads. Spiral-ribbed aluminized pipe (SRAP) has been widely specified by the Florida Department of Transportation (FDOT) for runoff drainage. Th...

Calcium aluminate coated and uncoated free form fabricated CoCr implants: a comparative study in rabbit.

PubMed

Palmquist, A; Jarmar, T; Hermansson, L; Emanuelsson, L; Taylor, A; Taylor, M; Engqvist, H; Thomsen, P

2009-10-01

The purpose of this study was to compare the integration in bone of uncoated free form fabricated cobalt chromium (CoCr) implants to the same implant with a calcium aluminate coating. The implants of cylindrical design with a pyramidal surface structure were press-fit into the limbs of New Zealand white rabbits. After 6 weeks, the rabbits were sacrificed, and samples were retrieved and embedded. Ground sections were subjected to histological analysis and histomorphometry. The section counter part was used for preparing an electron transparent transmission electron microscopy sample by focused ion beam milling. Calcium aluminate dip coating provided a significantly greater degree of bone contact than that of the native CoCr. The gibbsite hydrate formed in the hardening reaction of the calcium aluminate was found to be the exclusive crystalline phase material in direct contact with bone. (c) 2009 Wiley Periodicals, Inc.

Research on Equation of State For Detonation Products of Aluminized Explosive

NASA Astrophysics Data System (ADS)

Yue, Jun-Zheng; Duan, Zhuo-Ping; Zhang, Zhen-Yu; Ou, Zhuo-Cheng

2017-10-01

The secondary reaction of the aluminum powder contained in an aluminized explosive is investigated, from which the energy loss resulted from the quantity reduce of the gaseous products is demonstrated. Moreover, taking the energy loss into account, the existing improved Jones-Wilkins-Lee (JWL) equation of state for detonation products of aluminized explosive is modified. Furthermore, the new modified JWL equation of state is implemented into the dynamic analysis software (DYNA)-2D hydro-code to simulate numerically the metal plate acceleration tests of the Hexogen (RDX)-based aluminized explosives. It is found that the numerical results are in good agreement with previous experimental data. In addition, it is also demonstrated that the reaction rate of explosive before the Chapman-Jouget (CJ) state has little influence on the motion of the metal plate, based on which a simple approach is proposed to simulate numerically the products expansion process after the CJ state.

Software framework for the upcoming MMT Observatory primary mirror re-aluminization

NASA Astrophysics Data System (ADS)

Gibson, J. Duane; Clark, Dusty; Porter, Dallan

2014-07-01

Details of the software framework for the upcoming in-situ re-aluminization of the 6.5m MMT Observatory (MMTO) primary mirror are presented. This framework includes: 1) a centralized key-value store and data structure server for data exchange between software modules, 2) a newly developed hardware-software interface for faster data sampling and better hardware control, 3) automated control algorithms that are based upon empirical testing, modeling, and simulation of the aluminization process, 4) re-engineered graphical user interfaces (GUI's) that use state-of-the-art web technologies, and 5) redundant relational databases for data logging. Redesign of the software framework has several objectives: 1) automated process control to provide more consistent and uniform mirror coatings, 2) optional manual control of the aluminization process, 3) modular design to allow flexibility in process control and software implementation, 4) faster data sampling and logging rates to better characterize the approximately 100-second aluminization event, and 5) synchronized "real-time" web application GUI's to provide all users with exactly the same data. The framework has been implemented as four modules interconnected by a data store/server. The four modules are integrated into two Linux system services that start automatically at boot-time and remain running at all times. Performance of the software framework is assessed through extensive testing within 2.0 meter and smaller coating chambers at the Sunnyside Test Facility. The redesigned software framework helps ensure that a better performing and longer lasting coating will be achieved during the re-aluminization of the MMTO primary mirror.

Rupture in cemented granular media: application to wheat endosperm

NASA Astrophysics Data System (ADS)

Topin, V.; Delenne, J.-Y.; Radjai, F.

2009-06-01

The mechanical origin of the wheat hardness used to classify wheat flours is an open issue. Wheat endosperm can be considered as a cemented granular material, consisting of densely packed solid particles (the starch granules) and a pore-filling solid matrix (the protein) sticking to the particles. We use the lattice element method to investigate cemented granular materials with a texture close to that of wheat endosperm and with variable matrix volume fraction and particle-matrix adherence. From the shape of the probability density of vertical stresses we distinguish weak, intermediate and strong stresses. The large stresses occur mostly at the contact zones as in noncohesive granular media with a decreasing exponential distribution. The weak forces reflect the arching effect. The intermediate stresses belong mostly to the bulk of the particles and their distribution is well fit to a Gaussian distribution. We also observe that the stress chains are essentially guided by the cementing matrix in tension and by the particulate backbone in compression. Crack formation is analyzed in terms of particle damage as a function of matrix volume fraction and particle-matrix adherence. Our data provide evidence for three regimes of crack propagation depending on the crack path through the material. We find that particle damage scales well with the relative toughness of the particle-matrix interface. The interface toughness appears therefore to be strongly correlated with particle damage and determines transition from soft to hard behavior in wheat endosperm.

Long term mechanical properties of alkali activated slag

NASA Astrophysics Data System (ADS)

Zhu, J.; Zheng, W. Z.; Xu, Z. Z.; Leng, Y. F.; Qin, C. Z.

2018-01-01

This article reports a study on the microstructural and long-term mechanical properties of the alkali activated slag up to 180 days, and cement paste is studied as the comparison. The mechanical properties including compressive strength, flexural strength, axis tensile strength and splitting tensile strength are analyzed. The results showed that the alkali activated slag had higher compressive and tensile strength, Slag is activated by potassium silicate (K2SiO3) and sodium hydroxide (NaOH) solutions for attaining silicate modulus of 1 using 12 potassium silicate and 5.35% sodium hydroxide. The volume dosage of water is 35% and 42%. The results indicate that alkali activated slag is a kind of rapid hardening and early strength cementitious material with excellent long-term mechanical properties. Single row of holes block compressive strength, single-hole block compressive strength and standard solid brick compressive strength basically meet engineering requirements. The microstructures of alkali activated slag are studied by X-ray diffraction (XRD). The hydration products of alkali-activated slag are assured as hydrated calcium silicate and hydrated calcium aluminate.

Job Tasks as Determinants of Thoracic Aerosol Exposure in the Cement Production Industry.

PubMed

Notø, Hilde; Nordby, Karl-Christian; Skare, Øivind; Eduard, Wijnand

2017-12-15

The aims of this study were to identify important determinants and investigate the variance components of thoracic aerosol exposure for the workers in the production departments of European cement plants. Personal thoracic aerosol measurements and questionnaire information (Notø et al., 2015) were the basis for this study. Determinants categorized in three levels were selected to describe the exposure relationships separately for the job types production, cleaning, maintenance, foreman, administration, laboratory, and other jobs by linear mixed models. The influence of plant and job determinants on variance components were explored separately and also combined in full models (plant&job) against models with no determinants (null). The best mixed models (best) describing the exposure for each job type were selected by the lowest Akaike information criterion (AIC; Akaike, 1974) after running all possible combination of the determinants. Tasks that significantly increased the thoracic aerosol exposure above the mean level for production workers were: packing and shipping, raw meal, cement and filter cleaning, and de-clogging of the cyclones. For maintenance workers, time spent with welding and dismantling before repair work increased the exposure while time with electrical maintenance and oiling decreased the exposure. Administration work decreased the exposure among foremen. A subjective tidiness factor scored by the research team explained up to a 3-fold (cleaners) variation in thoracic aerosol levels. Within-worker (WW) variance contained a major part of the total variance (35-58%) for all job types. Job determinants had little influence on the WW variance (0-4% reduction), some influence on the between-plant (BP) variance (from 5% to 39% reduction for production, maintenance, and other jobs respectively but an 79% increase for foremen) and a substantial influence on the between-worker within-plant variance (30-96% for production, foremen, and other workers). Plant determinants had little influence on the WW variance (0-2% reduction), some influence on the between-worker variance (0-1% reduction and 8% increase), and considerable influence on the BP variance (36-58% reduction) compared to the null models. Some job tasks contribute to low levels of thoracic aerosol exposure and others to higher exposure among cement plant workers. Thus, job task may predict exposure in this industry. Dust control measures in the packing and shipping departments and in the areas of raw meal and cement handling could contribute substantially to reduce the exposure levels. Rotation between low and higher exposed tasks may contribute to equalize the exposure levels between high and low exposed workers as a temporary solution before more permanent dust reduction measures is implemented. A tidy plant may reduce the overall exposure for almost all workers no matter of job type. © The Author 2017. Published by Oxford University Press on behalf of the British Occupational Hygiene Society.

Does a simple syringe applicator enhance bone cement set up time in knee arthroplasty?

PubMed Central

Sodhi, Nipun; Dalton, Sarah E.; Khlopas, Anton; Sultan, Assem A.; Curtis, Gannon L.; Harb, Matthew A.; Naziri, Qais; Barrington, John W.; Mont, Michael A.

2017-01-01

Background The time required for polymethylmethacrylate (PMMA) cement curing or hardening can be modified by a number of variables including the mixing technique, and the temperature and pressure at which the process is taking place. Therefore, the purpose of this study was to evaluate two different methods of PMMA application in terms of set up time. Specifically, we (I) compared the PMMA set up time of cement that remained in the mixing bowl to cement that was placed in a syringe and (II) extrapolated the associated annual cost difference on the national and individual surgeon levels. Methods The cement set up time was measured for a total of 146 consecutive patients who underwent either unicompartmental knee arthroplasty (n=136) or patellofemoral arthroplasty (n=10) between January 2016 and April 2017. One pack of PMMA powder and monomer were mixed, placed in a 300 mL small plastic bowl, and mixed with a tongue depressor. Then, 50 mL of the mixed PMMA was placed in a sterile 60 mL syringe with the tip cut to a 6-mm opening, and the syringe was used to apply the cement to the bone and the prosthesis surface. The remaining unused cement in the syringe (syringe group) and the remaining unused cement in the plastic bowl (bowl group) were removed and formed into a two separate 2 cm diameter cubes that were allowed to cure at room temperature on a sterile set of osteotomes. The two cubes of cement were timed for complete PMMA curing. A two-tailed student’s t-test was used to compare the curing time for the two groups. Annual cost differences were calculated on the national and individual surgeon level. The total number of daily cases performed and the operative time savings using the syringe applicator was used to find daily and annual cost savings. Results The mean time for the cement to set up in the bowl group was 16.8±2.1 minutes, and the mean time for cement set up in the syringe group was 15.1±1.7 minutes. Compared to the bowl group cement set up time, the syringe group set up time was significantly lower (P<0.0001). An estimated 350,000 cemented knee arthroplasties are performed each year in the United States. With 1.7 minutes saved per case, 595,000 operating room minutes per year could be saved, resulting in a nearly $71,000,000 national and $110,000 individual surgeon annual cost savings. Conclusions The results of the present study demonstrated that the utilization of a simple, inexpensive syringe applicator enhanced the cement set up time by over one and a half minutes. This may be a result of the pressure differences in the syringe applicator. In addition to the control of and precision of where the cement is placed, the syringe applicator could provide an important potential time advantage to the arthroplasty surgeon. PMID:29299472

High temperature surface protection. [10 gas turbines

NASA Technical Reports Server (NTRS)

Levine, S. R.

1978-01-01

Alloys of the MCrAlX type are the basis for high temperature surface protection systems in gas turbines. M can be one or more of Ni, Co, or Fe and X denotes a reactive metal added to enhance oxide scale adherence. The selection and formation as well as the oxidation, hot corrosion and thermal fatigue performance of MCrAlX coatings are discussed. Coatings covered range from simple aluminides formed by pack cementation to the more advanced physical vapor deposition overlay coatings and developmental plasma spray deposited thermal barrier coatings.

Mechanical Behavior of Three-Dimensional Braided Nickel-Based Superalloys Synthesized via Pack Cementation

NASA Astrophysics Data System (ADS)

Lippitz, Nicolas; Erdeniz, Dinc; Sharp, Keith W.; Dunand, David C.

2018-03-01

Braided tubes of Ni-based superalloys are fabricated via three-dimensional (3-D) braiding of ductile Ni-20Cr (wt pct) wires followed by post-textile gas-phase alloying with Al and Ti to create, after homogenization and aging, γ/ γ' strengthened lightweight, porous structures. Tensile tests reveal an increase in strength by 100 MPa compared to as-braided Ni-20Cr (wt pct). An interrupted tensile test, combined with X-ray tomographic scans between each step, sheds light on the failure behavior of the braided superalloy tubes.

SINTERING AND SULFATION OF CALCIUM SILICATE-ALUMINATE

EPA Science Inventory

The effect of sintering on the reactivity of solids at high temperature was studied. The nature of the interaction was studied with calcium silicate-aluminate reacting with SO2 between 665 and 800 C. The kinetics of the sintering and sulfation processes were measured independentl...

Ion microprobe analyses of aluminous lunar glasses - A test of the 'rock type' hypothesis

NASA Technical Reports Server (NTRS)

Meyer, C., Jr.

1978-01-01

Previous soil survey investigations found that there are natural groupings of glass compositions in lunar soils and that the average major element composition of some of these groupings is the same at widely separated lunar landing sites. This led soil survey enthusiasts to promote the hypothesis that the average composition of glass groupings represents the composition of primary lunar 'rock types'. In this investigation the trace element composition of numerous aluminous glass particles was determined by the ion microprobe method as a test of the above mentioned 'rock type' hypothesis. It was found that within any grouping of aluminous lunar glasses by major element content, there is considerable scatter in the refractory trace element content. In addition, aluminous glasses grouped by major elements were found to have different average trace element contents at different sites (Apollo 15, 16 and Luna 20). This evidence argues that natural groupings in glass compositions are determined by regolith processes and may not represent the composition of primary lunar 'rock types'.

Methods of use of calcium hexa aluminate refractory linings and/or chemical barriers in high alkali or alkaline environments

DOE Office of Scientific and Technical Information (OSTI.GOV)

McGowan, Kenneth A; Cullen, Robert M; Keiser, James R

A method for improving the insulating character/and or penetration resistance of a liner in contact with at least one of an alkali and/or alkaline environments is provided. The method comprises lining a surface that is subject to wear by an alkali environment and/or an alkaline environment with a refractory composition comprising a refractory aggregate consisting essentially of a calcium hexa aluminate clinker having the formula CA.sub.6, wherein C is equal to calcium oxide, wherein A is equal to aluminum oxide, and wherein the hexa aluminate clinker has from zero to less than about fifty weight percent C.sub.12A.sub.7, and wherein greatermore » than 98 weight percent of the calcium hexa aluminate clinker having a particle size ranging from -20 microns to +3 millimeters, for forming a liner of the surface. This method improves the insulating character/and or penetration resistance of the liner.« less

Pre-packing of cost effective antibiotic cement beads for the treatment of traumatic osteomyelitis in the developing world - an in-vitro study based in Cambodia.

PubMed

Noor, S; Gilson, A; Kennedy, K; Swanson, A; Vanny, V; Mony, K; Chaudhry, T; Gollogly, J

2016-04-01

The developing world often lacks the resources to effectively treat the most serious injuries including osteomyelitis following open fractures or surgical fracture treatment. Antibiotic cement beads are a widely accepted method of delivering antibiotics locally to the infected area following trauma. This study is based in Cambodia, a low income country struggling to recover from a recent genocide. The study aims to test the effectiveness of locally made antibiotic beads and analyse their effectiveness after being gas sterilised, packaged and kept in storage Different antibiotic beads were manufactured locally using bone cement and tested against MRSA bacteria grown from a case of osteomyelitis. Each antibiotic was tested before and after a process of gas sterilisation as well as later being tested after storage in packaging up to 42 days. The gentamicin, vancomycin, amikacin and ceftriaxone beads all inhibited growth of the MRSA on the TSB and agar plates, both before and after gas sterilisation. All four antibiotics continued to show similar zones of inhibition after 42 days of storage. The results show significant promise to produce beads with locally obtainable ingredients in an austere environment and improve cost effectiveness by storing them in a sterilised condition. Copyright © 2016 Elsevier Ltd. All rights reserved.

Fabrication of polystyrene/gold nanotubes and nanostructure-controlled growth of aluminate.

PubMed

Zhu, Haifeng; Ai, Sufen; He, Qiang; Cui, Yue; Li, Junbai

2007-07-01

Direct adsorption of gold nanoparticles in the inner of alumina template and following immersion of polystyrene (PS) dichloromethane solution in the template resulted in the fabrication of composite nanotubes of PS and gold nanoparticles. Several methods have been used to characterize the tubular structure. Nanostructured sodium aluminates were formed when the anodic alumina oxide membrane was dissolved by the sodium hydroxide. A "flower" shape was found after etching the template while the synthesis process was recorded as function of a time. The results demonstrate that the shape and size of the aluminates nanostructure can be controlled by etching time and the pore diameter of the alumina membrane.

Lithium aluminate/zirconium material useful in the production of tritium

DOEpatents

Cawley, W.E.; Trapp, T.J.

A composition is described useful in the production of tritium in a nuclear reactor. Lithium aluminate particles are dispersed in a matrix of zirconium. Tritium produced by the reactor of neutrons with the lithium are absorbed by the zirconium, thereby decreasing gas pressure within capsules carrying the material.

Lithium aluminate/zirconium material useful in the production of tritium

DOEpatents

Cawley, W.E.; Trapp, T.J.

1984-10-09

A composition is described useful in the production of tritium in a nuclear reactor. Lithium aluminate particles are dispersed in a matrix of zirconium. Tritium produced by the reactor of neutrons with the lithium are absorbed by the zirconium, thereby decreasing gas pressure within capsules carrying the material.

Lithium aluminate/zirconium material useful in the production of tritium

DOEpatents

Cawley, William E.; Trapp, Turner J.

1984-10-09

A composition is described useful in the production of tritium in a nuclear eactor. Lithium aluminate particles are dispersed in a matrix of zirconium. Tritium produced by the reactor of neutrons with the lithium are absorbed by the zirconium, thereby decreasing gas pressure within capsules carrying the material.

Duplex aluminized coatings

NASA Technical Reports Server (NTRS)

Gedwill, M. A.; Grisaffe, S. J. (Inventor)

1975-01-01

The surface of a metallic base system is initially coated with a metallic alloy layer that is ductile and oxidation resistant. An aluminide coating is then applied to the metallic alloy layer. The chemistry of the metallic alloy layer is such that the oxidation resistance of the subsequently aluminized outermost layer is not seriously degraded.

Repair of bone defect by nano-modified white mineral trioxide aggregates in rabbit: A histopathological study.

PubMed

Saghiri, Mohammad-Ali; Orangi, Jafar; Tanideh, Nader; Asatourian, Armen; Janghorban, Kamal; Garcia-Godoy, Franklin; Sheibani, Nader

2015-09-01

Many researchers have tried to enhance materials functions in different aspects of science using nano-modification method, and in many cases the results have been encouraging. To evaluate the histopathological responses of the micro-/nano-size cement-type biomaterials derived from calcium silicate-based composition with addition of nano tricalcium aluminate (3CaO.Al2O3) on bone healing response. Ninety mature male rabbits were anesthetized and a bone defect was created in the right mandible. The rabbits were divided into three groups, which were in turn subdivided into five subgroups with six animals each based on the defect filled by: white mineral trioxide aggregate (WMTA), Nano-WMTA, WMTA without 3CaO.Al2O3, Nano-WMTA with 2% Nano-3CaO.Al2O3, and empty as control. Twenty, forty and sixty days postoperatively the animals were sacrificed and the right mandibles were removed for histopathological evaluations. Kruskal-Wallis test with post-hoc comparisons based on the LSMeans procedure was used for data analysis. All the experimental materials provoked a moderate to severe inflammatory reaction, which significantly differed from the control group (p< 0.05). Statistical analysis of bone formation and bone regeneration data showed significant differences between groups at 40- and 60- day intervals in all groups. Absence of 3CaO.Al2O3 leads to more inflammation and foreign body reaction than other groups in all time intervals. Both powder nano-modification and addition of 2% Nano-3CaO.Al2O3 to calcium silicate-based cement enhanced the favorable tissue response and osteogenesis properties of WMTA based materials.

Study of optical properties of cerium ion doped barium aluminate phosphor

DOE Office of Scientific and Technical Information (OSTI.GOV)

Lohe, P. P., E-mail: prachiti.lohe2012@gmail.com; Omanwar, S. K.; Bajaj, N. S.

2016-05-06

In the recent years due to their various optical and technological applications aluminate materials have attracted attention of several researchers. When these materials are doped with rare earth ions they show properties favorable for many optical applications such as high quantum efficiencies. These materials are used in various applications such as lamp phosphors, optically and thermoluminescence dosimeter etc Barium aluminate BaAl{sub 2}O{sub 4} doped with Ce is well known long lasting phosphor. This paper reports synthesis of BaAl{sub 2}O{sub 4}: Ce phosphor prepared by a simple combustion synthesis. The samples were characterized for the phase purity, chemical bonds and luminescentmore » properties.« less

Optimization of a Strontium Aluminate

DOE Office of Scientific and Technical Information (OSTI.GOV)

Bone, Alexandria N.

2017-08-01

Strontium aluminate with Eu 2+ and Dy 3+ has been at the forefront of emerging applications for storage phosphors since its discovery in 1996. In this study, the emission intensity and luminescence lifetime of SrAl 2O 4: Eu 2+, Dy 3+ were enhanced by partial substitution of Ca 2+ into Sr 2+ sites in the matrix.

Novel mechanism for the modification of Al2O3-based inclusions in ultra-low carbon Al-killed steel considering the effects of magnesium and calcium

NASA Astrophysics Data System (ADS)

Guo, Jing; Cheng, Shu-sen; Guo, Han-jie; Mei, Ya-guang

2018-03-01

Many researchers have explored the inclusion modification mechanism to improve non-metallic inclusion modifications in steelmaking. In this study, two types of industrial trials on inclusion modifications in liquid steel were conducted using ultra-low-carbon Al-killed steel with different Mg and Ca contents to verify the effects of Ca and Mg contents on the modification mechanism of Al2O3-based inclusions during secondary refining. The results showed that Al2O3-based inclusions can be modified into liquid calcium aluminate or a multi-component inclusion with the addition of a suitable amount of Ca. In addition, [Mg] in liquid steel can further reduce CaO in liquid calcium aluminate to drive its evolution into CaO-MgO-Al2O3 multi-component inclusions. Thermodynamic analysis confirmed that the reaction between [Mg] and CaO in liquid calcium aluminate occurs when the MgO content of liquid calcium aluminate is less than 3wt% and the temperature is higher than 1843 K.

Numerical prediction on static and dynamic properties for rotating mirror of ultra-high-speed photography

NASA Astrophysics Data System (ADS)

Huang, Hongbin; Li, Jingzhen; Gong, Xiangdong; Sun, Fengshan; He, Tiefeng

2007-01-01

The methods of numerical analysis for the strength and vibration modals of rotating mirrors were presented based respectively on the three-dimensional elastic mechanics and dynamics. On strength computation, the finite element models of rotating mirror were established according to the real structure of mirror, and the rotating three-faced aluminous and beryllium mirrors were analysed contrastively. Results display that the surface deformation quantity of the aluminous mirror is approximately 20 times as large as beryllium one, and the maximum stress is 1.6 times against the latter. Then, the three-faced aluminous mirrors were analyzed at variedly fit between shaft and axle hole. One conclusion is gotten out that the mirror strength is foreign to fits, but it is weaken by the axle hole obviously. On the modal analysis of vibration, this method can simulates accurately the natural frequencies and corresponding modalities of mirror. And the results from three-face aluminous mirror indicate that the resonance points of a new mirror may be guaranteed existing in selected speed range.

Detonation Chemistry: An Investigation of Fluorine as an Oxidizing Moiety in Explosives

DTIC Science & Technology

1982-07-07

Aluminized Explosives .. .. .... ....... ....... .... 32 Conclusion .. .. ....... ....... ....... .........34 References...heats with a knifeblade heater. A small centrifugal pump circulates water from the jacket through the jacket lid. The thermometric system is a Hewlett...and that the relative flatness of the expansion adiabats for products of aluminized explosives is due to very high vibrational energy (temperature) and

Environmental Benefit Assessment for the Carbonation Process of Petroleum Coke Fly Ash in a Rotating Packed Bed.

PubMed

Pei, Si-Lu; Pan, Shu-Yuan; Li, Ye-Mei; Chiang, Pen-Chi

2017-09-19

A high-gravity carbonation process was deployed at a petrochemical plant using petroleum coke fly ash and blowdown wastewater to simultaneously mineralized CO 2 and remove nitrogen oxides and particulate matters from the flue gas. With a high-gravity carbonation process, the CO 2 removal efficiency was found to be 95.6%, corresponding to a capture capacity of 600 kg CO 2 per day, at a gas flow rate of 1.47 m 3 /min under ambient temperature and pressure. Moreover, the removal efficiency of nitrogen oxides and particulate matters was 99.1% and 83.2%, respectively. After carbonation, the reacted fly ash was further utilized as supplementary cementitious materials in the blended cement mortar. The results indicated that cement with carbonated fly ash exhibited superior compressive strength (38.1 ± 2.5 MPa at 28 days in 5% substitution ratio) compared to the cement with fresh fly ash. Furthermore, the environmental benefits for the high-gravity carbonation process using fly ash were critically assessed. The energy consumption of the entire high-gravity carbonation ranged from 80 to 169 kWh/t-CO 2 (0.29-0.61 GJ/t-CO 2 ). Compared with the scenarios of business-as-usual and conventional carbon capture and storage plant, the economic benefit from the high-gravity carbonation process was approximately 90 and 74 USD per ton of CO 2 fixation, respectively.

Carbonate petrography of the Burlington/Keokuk contact in southeastern Iowa

DOE Office of Scientific and Technical Information (OSTI.GOV)

Maguire, T.D.

1993-02-01

The top of the Burlington Formation (Mississippian, Osagean Series), a dominantly skeletal packstone/grainstone unit in southeastern Iowa, is defined by a regionally persistent bone bed horizon and is overlain by the lower Keokuk Formation, a dominant skeletal wackestone and chert. A thin gray-green shale at some localities at the contact is interpreted as a condensed section that corresponds to a deepening event during the beginning of the Keokuk deposition. Both units represent similar carbonate bank settings deposited during rapid, uninterrupted progradation of carbonate sediments during changing sea levels. The upper Burlington facies consists dominantly of crinoids and has the highestmore » biotic diversity (i.e., bryozoan, corals, and brachiopods) during the most open marine conditions. In thin section most crinoid grains show moderate abrasion and some evidence of early fragmentation. Frequent winnowing during storm events resulted in relatively clean packed calcarenite fabrics. Both formations acted as a single paragenetic unit during the induration process, characterized by multiple episodes of cementation, dolomitization, and compaction. Crinoidal syntaxial overgrowths and crushed bryozoan matrix make up most of the packstone/grainstone fabrics in both formations. The presence of mashed bryozoans suggests that some compaction may have preceded complete stabilization of the sedimentary mass by crinoidal syntaxial overgrowth cements. Staining revealed at least three generations of syntaxial overgrowth cements which probably formed in a meteoric phreatic environment during a relatively short period of geologic time.« less

Steel slag: a waste industrial by-product as an alternative sustainable green building material in construction applications--an attempt for solid waste management.

PubMed

Pofale, Arun D; Nadeem, Mohammed

2012-01-01

This investigation explores the possibility of utilizing granular slag as an alternative to fine aggregate (natural sand) in construction applications like masonry and plastering. Construction industry utilizes large volume of fine aggregate in all the applications which has resulted into shortage of good quality naturally available fine aggregate. Use of granular slag serves two fold purposes, i.e. waste utilisation as well as alternative eco-friendly green building material for construction. The investigation highlights comparative study of properties with partial and full replacement of fine aggregate (natural sand) by granular slag in cement mortar applications (masonry and plastering). For this purpose, cement mortar mix proportions from 1:3, 1:4, 1:5 & 1:6 by volume were selected for 0, 25, 50, 75 & 100% replacement levels with w/c ratios of 0.60, 0.65, 0.70 & 0.72 respectively. Based on the study results, it could be inferred that replacement of natural sand with granular slag from 25 to 75% increased the packing density of mortar which resulted into reduced w/c ratio, increased strength properties of all mortar mixes. Hence, it could be recommended that the granular slag could be effectively utilized as fine aggregate in masonry and plastering applications in place of conventional cement mortar mixes using natural sand.

Charge division in a small proportional chamber constructed with aluminized mylar tubes

NASA Astrophysics Data System (ADS)

Biino, C.; Mussa, R.; Palestini, S.; Pastrone, N.; Pesando, L.

1988-09-01

A tracking detector composed of aluminized mylar drift tubes is under development for the Fermilab experiment 760. A prototype chamber has been constructed. Results on the longitudinal coordinate determined by charge division are given. Spatial resolution values below 2 mm (rms) were found, corresponding to <1% of the chamber length. Results on chamber ageing are also discussed.

High Temperature Oxidation of Hot-Dip Aluminized T92 Steels

NASA Astrophysics Data System (ADS)

Abro, Muhammad Ali; Hahn, Junhee; Lee, Dong Bok

2018-03-01

The T92 steel plate was hot-dip aluminized, and oxidized in order to characterize the high-temperature oxidation behavior of hot-dip aluminized T92 steel. The coating consisted of Al-rich topcoat with scattered Al3Fe grains, Al3Fe-rich upper alloy layer with scattered (Al, Al5Fe2, AlFe)-grains, and Al5Fe2-rich lower alloy layer with scattered (Al5Fe2, AlFe)-grains. Oxidation at 800 °C for 20 h formed (α-Al2O3 scale)/(AlFe layer)/(AlFe3 layer)/(α-Fe(Al) layer), while oxidation at 900 °C for 20 h formed (α-Al2O3 scale plus some Fe2O3)/(AlFe layer)/(AlFe3 layer)/(α-Fe(Al) layer) from the surface. During oxidation, outward migration of all substrate elements, inward diffusion of oxygen, and back and forth diffusion of Al occurred according to concentration gradients. Also, diffusion transformed and broadened AlFe and AlFe3 layers dissolved with some oxygen and substrate alloying elements. Hot-dip aluminizing improved the high-temperature oxidation resistance of T92 steel through preferential oxidation of Al at the surface.

High Temperature Oxidation of Hot-Dip Aluminized T92 Steels

NASA Astrophysics Data System (ADS)

Abro, Muhammad Ali; Hahn, Junhee; Lee, Dong Bok

2018-05-01

The T92 steel plate was hot-dip aluminized, and oxidized in order to characterize the high-temperature oxidation behavior of hot-dip aluminized T92 steel. The coating consisted of Al-rich topcoat with scattered Al3Fe grains, Al3Fe-rich upper alloy layer with scattered (Al, Al5Fe2, AlFe)-grains, and Al5Fe2-rich lower alloy layer with scattered (Al5Fe2, AlFe)-grains. Oxidation at 800 °C for 20 h formed (α-Al2O3 scale)/(AlFe layer)/(AlFe3 layer)/(α-Fe(Al) layer), while oxidation at 900 °C for 20 h formed (α-Al2O3 scale plus some Fe2O3)/(AlFe layer)/(AlFe3 layer)/(α-Fe(Al) layer) from the surface. During oxidation, outward migration of all substrate elements, inward diffusion of oxygen, and back and forth diffusion of Al occurred according to concentration gradients. Also, diffusion transformed and broadened AlFe and AlFe3 layers dissolved with some oxygen and substrate alloying elements. Hot-dip aluminizing improved the high-temperature oxidation resistance of T92 steel through preferential oxidation of Al at the surface.

Preparation and Oxidation Performance of Y and Ce-Modified Cr Coating on open-cell Ni-Cr-Fe Alloy Foam by the Pack Cementation

NASA Astrophysics Data System (ADS)

Pang, Q.; Hu, Z. L.; Wu, G. H.

2016-12-01

Metallic foams with a high fraction of porosity, low density and high-energy absorption capacity are a rapidly emerging class of novel ultralight weight materials for various engineering applications. In this study, Y-Cr and Ce-Cr-coated Ni-Cr-Fe alloy foams were prepared via the pack cementation method, and the effects of Y and Ce addition on the coating microstructure and oxidation performance were analyzed in order to improve the oxidation resistance of open-cell nickel-based alloy foams. The results show that the Ce-Cr coating is relatively more uniform and has a denser distribution on the surface of the nickel-based alloy foam. The surface grains of the Ce-Cr-coated alloy foam are finer compared to those of the Y-Cr-coated alloy foam. An obvious Ce peak appears on the interface between the coating and the alloy foam strut, which gives rise to a "site-blocking" effect for the short-circuit transport of the cation in the substrate. X-ray diffraction analysis shows that the Y-Cr-coated alloy foam mainly consists of Cr, (Fe, Ni) and (Ni, Cr) phases in the surface layer. The Ce-Cr-coated alloy foam is mainly composed of Cr and (Ni, Cr) phases. Furthermore, the addition of Y and Ce clearly lead to an improvement in the oxidation resistance of the coated alloy foams in the temperature range of 900-1000 °C. The addition of Ce is especially effective in enhancing the diffusion of chromium to the oxidation front, thus, accelerating the formation of a Cr2O3 layer.

Determination of performance of non-ideal aluminized explosives.

PubMed

Keshavarz, Mohammad Hossein; Mofrad, Reza Teimuri; Poor, Karim Esmail; Shokrollahi, Arash; Zali, Abbas; Yousefi, Mohammad Hassan

2006-09-01

Non-ideal explosives can have Chapman-Jouguet (C-J) detonation pressure significantly different from those expected from existing thermodynamic computer codes, which usually allows finding the parameters of ideal detonation of individual high explosives with good accuracy. A simple method is introduced by which detonation pressure of non-ideal aluminized explosives with general formula C(a)H(b)N(c)O(d)Al(e) can be predicted only from a, b, c, d and e at any loading density without using any assumed detonation products and experimental data. Calculated detonation pressures show good agreement with experimental values with respect to computed results obtained by complicated computer code. It is shown here how loading density and atomic composition can be integrated into an empirical formula for predicting detonation pressure of proposed aluminized explosives.

Synthesis of nano grade hollow silica sphere via a soft template method.

PubMed

Tsai, Ming-Shyong; Li, Miao Ju; Yen, Fu-Hsu

2008-06-01

The nano grade hollow silica sphere (HSS) was synthesized by a novel soft template method. We found that the precipitate of aluminate had a porous structure that could be the soft template for HSS. After mixing the colloidal silica with the aluminate precipitate, the bubble trapped in this porous structure could form the nano grade HSS. The aluminate precipitate was removed by adjusting the pH of the slurry to approximately 1. The outside diameter, the specific surface, and the mean pore size diameter of the forming HSS were 60-90 nm, 571 m2/g, and 3 nm, respectively. The formed HSS was collected by modifying the surface with Si(OCH3)3CHCH2 (VTMO) and then filtrating the precipitated gel in the n-butanol and ethanol solvent system.

Réactivité du laitier de hauts fourneaux d'Annaba (Algérie) en substitution partielle du ciment

NASA Astrophysics Data System (ADS)

Behim, M.; Redjel, B.; Jauberthie, R.

2002-07-01

Iron industry provides blast-furnace slag production as waste. Blast-furnace slag are made of non ironic elements, flux and coke ash. These elements might have binding properties such as cement. Usually, only blastfurnace slag chemical composition is considered to evaluate its quality as a binder. Other properties such as crystal phases amount, grading, specific area or temperature are not considered Some studies have shown that binding properties exist when the blast-furnace slag is quenched and crushed in very fine grains, and that an increase of the temperature has a benefit aspect on the kinetic of the reaction. We have used X ray diffraction, SEM observations with micro analysis on different samples of blast-furnace slag that undergone different cure modes. At low temperature, only non complete crystal phases appear. At room temperature, calcium sulphate and hydrated aluminium sulphate (ettringite) exist such as for Portland cement while setting. Under a steam curing mode, there is very few lime in the blast-furnace slag because lime has reacted with silicate, therefore there is much more CSH in the binder. No ettringite can be detected, on the other hand, the steam curing mode produce formation of hydrated calcium aluminate. Les laitiers de haut fourneau sont des sous produit de l'élaboration de la fonte. lis sont formés de constituants non ferreux, des fondants et des cendres de coke. Leur composition chimique laisse présager des propriétés liantes comme celles que l'on obtient avec les ciments. Les qualités hydrauliques de ces matériaux sont actuellement estimées par des calculs basés sur leur composition chimique. Elles ne tiennent pas compte d'autres paramètres tels que le caractère vitreux ou cristallin, la granulométrie ou la surface spécifique, la température entre autres. Les propriétés liantes apparaissent lorsque le laitier est trempé et broyé très finement, la température augmentant la cinétique. Les produits formés analysés par diffraction X et observés au MEB couplé à une micro analyse sont, pour des températures faibles, des phases semi cristallines. Dans les produits étuvés, la chaux est en plus faible quantité, elle a réagi avec la silice: les CSH sont en plus grande quantité. Le sulfate de calcium et d'aluminium hydraté (ettringite) apparaît à température ambiante comme dans le cas de la prise des ciments Portland mais est absente dans le ciment au laitier étuvé. A l'inverse, la formation de l'aluminate de calcium hydraté est favorisée par l'étuvage.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Altay, A.; Carter, C.B., E-mail: cbcarter@engr.uconn.ed; Rulis, P.

Calcium aluminates, compounds in the CaO-Al{sub 2}O{sub 3} phase system, are used in high-temperature cements and refractory oxides and have wide range of potential technological applications due to their interesting optical, electrical, thermal, and mechanical properties. They are used in both crystalline and glassy form; the glass is an isotropic material while the crystalline materials may be highly anisotropic. This paper will consider two particular crystalline materials, CA{sub 2} and CA{sub 6}, but the results should be applicable to all calcium aluminates. Although CA{sub 2} and CA{sub 6} crystals contain the same chemical species, Ca, Al, and O, the coordinationmore » and local environments of these species are different in the two structures and hence they show very different energy-loss near-edge structures (ELNES) when examined by electron energy-loss spectroscopy (EELS) in the TEM. The data obtained using ELNES can effectively provide a fingerprint for each compound and a map for their electronic structure. Once such fingerprints are obtained, they can be used to identify nano-sized particles/grains or material at interfaces and grain boundaries. In the present study, the local symmetry fingerprints for CA{sub 2} and CA{sub 6} structures are reported combining experimental spectra with electronic-structure calculations that allow the different features in the spectra to be interpreted. Al-L{sub 2,3} and O-K edge core-loss spectra from CA{sub 2} and CA{sub 6} were measured experimentally using electron energy-loss spectroscopy in a monochromated scanning transmission electron microscope. The near-edge structures were calculated for the different phases using the orthogonalized linear combination of atomic-orbitals method, and took account of core-hole interactions. It is shown that CA{sub 2} and CA{sub 6} structures exhibit distinctive experimental ELNES fingerprints so that these two phases can be separately identified even when present in small volumes. - Graphical abstract: Projection of the CA{sub 2} structure viewed in the [010] direction. Green atoms represent the Ca{sup 2+} ions and blue atoms represent the Al{sup 3+} ions. Two unit cells are outlined..« less

Reuse of ornamental rock-cutting waste in aluminous porcelain.

PubMed

Silva, M A; Paes, H R; Holanda, J N F

2011-03-01

Large amounts of solid wastes are discarded in the ornamental rocks industry. This work investigates the incorporation of ornamental rock-cutting waste as a raw material into an aluminous porcelain body, replacing natural feldspar material by up to 35 wt.%. Formulations containing rock-cutting waste were pressed and sintered at 1350 °C. The porcelain pieces were tested to determine their properties (linear shrinkage, water absorption, apparent density, mechanical strength, and electrical resistivity). Development of the microstructure was followed by scanning electron microscopy (SEM) and X-ray diffraction (XRD) analyses. The results showed that ornamental rock-cutting waste could be used in aluminous porcelains, in the range up to 10 wt.%, as a partial replacement for traditional flux material, resulting in a valid route for management of this abundant waste. Copyright © 2010 Elsevier Ltd. All rights reserved.

Driving Ability of HMX based Aluminized Explosive Affected by the Reaction Degree of Aluminum Powder

NASA Astrophysics Data System (ADS)

Duan, Yingliang

2017-06-01

Due to the time scale of aluminum reaction, the detonation process of the aluminized explosive becomes very complex, and there is less agreement on the reaction mechanism of aluminum powder. If the reaction of aluminum occurs in the reaction zone, the energy released will further strengthen the work ability of detonation wave. So it is very important for characterizing the detonation parameters and detonation driving ability to accurately understand the role of aluminum powder in the reaction zone. In this paper, detonation driving process of HMX based aluminized explosive was studied by cylinder test, obtaining the expansion track of cylinder wall. In order to further research the reaction degree (λ) of aluminum in the reaction zone, the thermodynamic program VHL was used to calculate the detonation process at different reaction degrees, obtaining the parameters of detonation products thermodynamic state. Using the dynamic software LS-DYNA and the JWL equation of state by fitting the pressure and relative volume relationship, the cylinder test was simulated. Compared with the experimental results, when the reaction degree is 20%, the driving ability is found to be in agreement with measured ones. It is concluded that the driving ability of HMX based aluminized explosive can be more accurately characterized by considering the reaction degree of aluminum powder in the reaction zone.

The effect of explosive percentage on underwater explosion energy release of hexanitrohexaazaisowurtzitane and octogen based aluminized explosives

NASA Astrophysics Data System (ADS)

Jiao, Qingjie; Wang, Qiushi; Nie, Jianxin; Guo, Xueyong; Zhang, Wei; Fan, Wenqi

2018-03-01

To control the explosion energy output by optimizing explosive components is a key requirement in a number of different application areas. The effect of different Al/O Ratio on underwater explosion of aluminized explosives has been studied detailedly. However, the effect of explosive percentage in the same Al/O Ratio is rarely researched, especially for Hexanitrohexaazaisowurtzitane (CL-20) based aluminized explosives. In this study, we performed the underwater explosion experiments with 1.2-kilogram explosives in order to investigate the explosion energy released from CL-20 and Octogen (HMX) based aluminized explosives. The percentage of the explosive varied from 5% to 30% and it is shown that: the shockwave peak pressure (pm) grows gradually; shock wave energy (Es) continues increasing, bubble energy (Eb) increases then decreases peaking at 15% for both formulas, and the total energy (E) and energy release rate (η) peak at 20% for CL-20 and 15% for HMX. This paper outlines the physical mechanism of Eb change under the influence of an aluminium initial reaction temperature and reaction active detonation product percentage coupling. The result shows that CL-20 is superior as a new high explosive and has promising application prospects in the regulation of explosive energy output for underwater explosives.

Percolation behavior of tritiated water into a soil packed bed

DOE Office of Scientific and Technical Information (OSTI.GOV)

Honda, T.; Katayama, K.; Uehara, K.

2015-03-15

A large amount of cooling water is used in a D-T fusion reactor. The cooling water will contain tritium with high concentration because tritium can permeate metal walls at high temperature easily. A development of tritium handling technology for confining tritiated water in the fusion facility is an important issue. In addition, it is also important to understand tritium behavior in environment assuming severe accidents. In this study, percolation experiments of tritiated water in soil packed bed were carried out and tritium behavior in soil was discussed. Six soil samples were collected in Hakozaki campus of Kyushu University. These particlemore » densities were of the same degree as that of general soils and moisture contents were related to BET surface area. For two soil samples used in the percolation experiment of tritiated water, saturated hydraulic conductivity agreed well with the estimating value by Creager. Tritium retention ratio in the soil packed bed was larger than water retention. This is considered to be due to an effect of tritium sorption on the surface of soil particles. The isotope exchange capacity estimated by assuming that H/T ratio of supplied tritiated water and H/T ratio of surface water of soil particle was equal was comparable to that on cement paste and mortar which were obtained by exposure of tritiated water vapor. (authors)« less

Effect of conditioning methods on the microtensile bond strength of phosphate monomer-based cement on zirconia ceramic in dry and aged conditions.

PubMed

Amaral, Regina; Ozcan, Mutlu; Valandro, Luiz Felipe; Balducci, Ivan; Bottino, Marco Antonio

2008-04-01

The objective of this study was to evaluate the durability of bond strength between a resin cement and aluminous ceramic submitted to various surface conditioning methods. Twenty-four blocks (5 x 5 x 4 mm(3)) of a glass-infiltrated zirconia-alumina ceramic (In-Ceram Zirconia Classic) were randomly divided into three surface treatment groups: ST1-Air-abrasion with 110-mum Al2O3 particles + silanization; ST2-Laboratory tribochemical silica coating method (110-microm Al2O3, 110-microm silica) (Rocatec) + silanization; ST3-Chairside tribochemical silica coating method (30-microm SiO(x)) (CoJet) + silanization. Each treated ceramic block was placed in its silicone mold with the treated surface exposed. The resin cement (Panavia F) was prepared and injected into the mold over the treated surface. Specimens were sectioned to achieve nontrimmed bar specimens (14 sp/block) that were randomly divided into two conditions: (a) Dry-microtensile test after sectioning; (b) Thermocycling (TC)-(6,000x, 5-55 degrees C) and water storage (150 days). Thus, six experimental groups were obtained (n = 50): Gr1-ST1 + dry; Gr2-ST1 + TC(;) Gr3-ST2 + dry; Gr4-ST2 + TC; Gr5-ST3 + dry; Gr6-ST3 + TC. After microtensile testing, the failure types were noted. ST2 (25.1 +/- 11) and ST3 (24.1 +/- 7.4) presented statistically higher bond strength (MPa) than that of ST1 (17.5 +/- 8) regardless of aging conditions (p < 0.0001). While Gr2 revealed the lowest results (13.3 +/- 6.4), the other groups (21.7 +/- 7.4-25. 9 +/- 9.1) showed statistically no significant differences (two-way ANOVA and Tukey's test, alpha = 0.05). The majority of the failures were mixed (82%) followed by adhesive failures (18%). Gr2 presented significantly higher incidence of ADHESIVE failures (54%) than those of other groups (p = 0.0001). Both laboratory and chairside silica coating plus silanization showed durable bond strength. After aging, air-abrasion with 110-microm Al(2)O(3) + silanization showed the largest decrease indicating that aging is fundamental for bond strength testing for acid-resistant zirconia ceramics in order to estimate their long-term performance in the mouth.

Educational Brief: Using Space for a Better Foundation on Earth Mechanics of Granular Materials

NASA Technical Reports Server (NTRS)

Dooling, Dave (Editor)

2002-01-01

Soils are three-phase composite materials that consist of soil, solid particles, and voids filled with water and/or air. Based on the particle-size distribution, they are generally classified as fine-grained (clays and plastic silts) and coarse-grained soils (nonplastic silts, sand, and gravel). Soil's resistance to external loadings is mainly derived from friction between particles and cohesion. Friction resistance is due to particles' surface-to-surface friction, interlocking, crushing, rearrangement, and dilation (or expansion) during shearing. Cohesion can be due to chemical cementation between particles, electrostatic and electromagnetic forces, and soil-water reaction and equilibrium. The basic factor responsible for the strength of coarse-grained soils is friction. Cohesion can be ignored. This educational brief focuses on measuring shear strength of sands (typical example of coarse-grained soils) where, for the same material, packing density is a main factor to be considered when one asks about the shear strength value. As the external load is applied, the soil's resistance is attained through shearing resistance, which causes the soil volume to increase (expand) or decrease (compress) depending on the initial packing density.

Crystal structures and optical properties of new quaternary strontium europium aluminate luminescent nanoribbons

DOE PAGES

Li, Xufan; Budai, John D.; Liu, Feng; ...

2014-11-12

We report the synthesis and characterizations of three series of quaternary strontium europium aluminate (Sr-Eu-Al-O; SEAO) luminescent nanoribbons that show blue, green, and yellow luminescence from localized Eu2+ luminescent centers. These three series of SEAO nanoribbons are: blue luminescent, tetragonal Sr1-xEuxAl6O10 (01-xEu xAl 2O 4 (01-xEu xAl 2O 4 (0

Development of High Temperature Superconducting Josephson Junction Device Technology

DTIC Science & Technology

1998-07-09

neodymium gallate , cerium oxide-buffered sapphire, and lanthanum aluminate, are not ideal for an in situ thallium cuprate junction technology. Moreover...determined that the standard HTS substrates, neodymium gallate , cerium oxide-buffered sapphire, and lanthanum aluminate, are not ideal for an in situ...2.2.1. Deposition Uniformity 10 2.2.2. Radiative Element 12 2.3. SUBSTRATES 13 2.3.1. Neodymium gallate 14 2.3.2. Cerium Oxide-Buffered Sapphire 16

Eigenvalue Detonation of Combined Effects Aluminized Explosives

NASA Astrophysics Data System (ADS)

Capellos, Christos; Baker, Ernest; Balas, Wendy; Nicolich, Steven; Stiel, Leonard

2007-06-01

This paper reports on the development of theory and performance for recently developed combined effects aluminized explosives. Traditional high energy explosives used for metal pushing incorporate high loading percentages of HMX or RDX, whereas blast explosives incorporate some percentage of aluminum. However, the high blast explosives produce increased blast energies, with reduced metal pushing capability due to late time aluminum reaction. Metal pushing capability refers to the early volume expansion work produced during the first few volume expansions associated with cylinder wall velocities and Gurney energies. Our Recently developed combined effects aluminized explosives (PAX-29C, PAX-30, PAX-42) are capable of achieving excellent metal pushing and high blast energies. Traditional Chapman-Jouguet detonation theory does not explain the observed detonation states achieved by these combined effects explosives. This work demonstrates, with the use of cylinder expansion data and thermochemical code calculations (JAGUAR and CHEETAH), that eigenvalue detonation theory explains the observed behavior.

Study of photoluminescence properties of CaAl{sub 2}O{sub 4}: Eu{sup 2+} prepared by combustion synthesis method

DOE Office of Scientific and Technical Information (OSTI.GOV)

Hingwe, V. S., E-mail: vishwas.hingwe@yahoo.in; Omanwar, S. K.; Bajaj, N. S.

2016-05-06

Eu{sup 2+} doped alkaline earth metals such as strontium aluminate, calcium aluminate and barium aluminate prepared by using modified combustion synthesis method at 600°C with Urea as fuel. Crystal structure is determined by using XRD and the sample confirmation by using the FTIR. The effect of the host material on the photoluminescence (PL) and phosphorescence properties were studied by using the Hitachi F-7000 spectrofluorimeter equipped with a 450W Xenon lamp, in the range 200-650 nm. The emission spectra of Eu{sup 2+} range from 450 to 500 nm in the Blue to aqua region and the transition 4f{sup 7}-4f{sup 6} 5d{sup 1}.more » The observed emission in CaAl{sub 2}O{sub 4} is 440 nm.« less

Spacecraft outer thermal blankets as hypervelocity impact bumpers

NASA Astrophysics Data System (ADS)

Cour-Palais, B. G.

1996-05-01

A thermal barrier consisting of a woven fabric outer layer followed by several layers of aluminized mylar insulation has been the primary impact protection against micrometeoroid and orbital impacts for many spacecraft currently in orbit. This paper examines its effectiveness as a hypervelocity "bumper" based on the performance of a NASA space suit. In this case, the thermal barrier consisted of a fabric layer followed by five layers of the aluminized mylar, which shielded either an aluminum rear wall or a rubberized pressure garment. The total areal density of the fabric and mylar layers was 0.052 g/cm2 and the fabric stand-off was 4 mm from the protected surfaces, with the aluminized mylar filling the space. Test results obtained with hypervelocity aluminum projectile impacts up to 8.5 km/s on the thermal barrier and aluminum wall are described, and a semi-empirical equation for this type of shielding is suggested.

Method of processing aluminous ores

DOEpatents

Loutfy, Raouf O.; Keller, Rudolf; Yao, Neng-Ping

1981-01-01

A method of producing aluminum chloride from aluminous materials containing compounds of iron, titanium and silicon comprising reacting the aluminous materials with carbon and a chlorine-containing gas at a temperature of about 900.degree. K. to form a gaseous mixture containing chlorides of aluminum, iron, titanium and silicon and oxides of carbon; cooling the gaseous mixture to a temperature of about 400.degree. K. or lower to condense the aluminum chlorides and iron chlorides while titanium chloride and silicon chloride remain in the gas phase to effect a separation thereof; heating the mixture of iron chlorides and aluminum chlorides to a temperature of about 800.degree. K. to form gaseous aluminum chlorides and iron chlorides; passing the heated gases into intimate contact with aluminum sulfide to precipitate solid iron sulfide and to form additional gaseous aluminum chlorides; and separating the gaseous aluminum chloride from the solid iron sulfide.

Hydrolysis of aluminum dross material to achieve zero hazardous waste.

PubMed

David, E; Kopac, J

2012-03-30

A simple method with high efficiency for generating high pure hydrogen by hydrolysis in tap water of highly activated aluminum dross is established. Aluminum dross is activated by mechanically milling to particles of about 45 μm. This leads to removal of surface layer of the aluminum particles and creation of a fresh chemically active metal surface. In contact with water the hydrolysis reaction takes place and hydrogen is released. In this process a Zero Waste concept is achieved because the other product of reaction is aluminum oxide hydroxide (AlOOH), which is nature-friendly and can be used to make high quality refractory or calcium aluminate cement. For comparison we also used pure aluminum powder and alkaline tap water solution (NaOH, KOH) at a ratio similar to that of aluminum dross content. The rates of hydrogen generated in hydrolysis reaction of pure aluminum and aluminum dross have been found to be similar. As a result of the experimental setup, a hydrogen generator was designed and assembled. Hydrogen volume generated by hydrolysis reaction was measured. The experimental results obtained reveal that aluminum dross could be economically recycled by hydrolysis process with achieving zero hazardous aluminum dross waste and hydrogen generation. Copyright © 2012 Elsevier B.V. All rights reserved.

A Combined Brazing and Aluminizing Process for Repairing Turbine Blades by Thermal Spraying Using the Coating System NiCrSi/NiCoCrAlY/Al

NASA Astrophysics Data System (ADS)

Nicolaus, M.; Möhwald, K.; Maier, H. J.

2017-10-01

The repair and maintenance of components in the aerospace industry play an increasingly important role due to rising manufacturing costs. Besides welding, vacuum brazing is a well-established repair process for turbine blades made of nickel-based alloys. After the coating of the worn turbine blade has been removed, the manual application of the nickel-based filler metal follows. Subsequently, the hot gas corrosion-protective coating is applied by thermal spraying. The brazed turbine blade is aluminized to increase the hot gas corrosion resistance. The thermal spray technology is used to develop a two-stage hybrid technology that allows shortening the process chain for repair brazing turbine blades and is described in the present paper. In the first step, the coating is applied on the base material. Specifically, the coating system employed here is a layer system consisting of nickel filler metal, NiCoCrAlY and aluminum. The second step represents the combination of brazing and aluminizing of the coating system which is subjected to a heat treatment. The microstructure, which results from the combined brazing and aluminizing process, is characterized and the relevant diffusion processes in the coating system are illustrated. The properties of the coating and the ramifications with respect to actual applications will be discussed.

Efficient solid rocket propulsion for access to space

NASA Astrophysics Data System (ADS)

Maggi, Filippo; Bandera, Alessio; Galfetti, Luciano; De Luca, Luigi T.; Jackson, Thomas L.

2010-06-01

Space launch activity is expected to grow in the next few years in order to follow the current trend of space exploitation for business purpose. Granting high specific thrust and volumetric specific impulse, and counting on decades of intense development, solid rocket propulsion is a good candidate for commercial access to space, even with common propellant formulations. Yet, some drawbacks such as low theoretical specific impulse, losses as well as safety issues, suggest more efficient propulsion systems, digging into the enhancement of consolidated techniques. Focusing the attention on delivered specific impulse, a consistent fraction of losses can be ascribed to the multiphase medium inside the nozzle which, in turn, is related to agglomeration; a reduction of agglomerate size is likely. The present paper proposes a model based on heterogeneity characterization capable of describing the agglomeration trend for a standard aluminized solid propellant formulation. Material microstructure is characterized through the use of two statistical descriptors (pair correlation function and near-contact particles) looking at the mean metal pocket size inside the bulk. Given the real formulation and density of a propellant, a packing code generates the material representative which is then statistically analyzed. Agglomerate predictions are successfully contrasted to experimental data at 5 bar for four different formulations.

Installation Restoration Program (IRP), Phase II, Stage 1 - Problem Confirmation Study, Norton Air Force Base, San Bernardino, California. Volume 1. Technical Report.

DTIC Science & Technology

1985-07-01

protein, and AFFF (Air Force Firefighting Foam). The frequency of training exercises has varied considerably over the years. During the early 1970’s...Surface ’ Cement/ Bentonite Grout Bentonite Seal Sand Pack 1. Ground Water Elevation r Mamaur July 4.5, 194 * . FIGURE 3-9 WELL CONSTRUCTION SUMMARY, ZONE...e zzzzzzzzz z I z z Z 0 -. N N E-3 3 0 3 3 w 3 w 0 o z ~ zzzzzzzz z z z z E- 0 0 E- 0z zzzzzzzz zz aua E- 0 4 10 zw 3 E- z 0 0 U)z V fC InZ OE- 3

The Stability of Hydrous Silicates in Earth's Lower Mantle: Experimental constraints from the System MgO-Al2O3-SiO2-H2O

NASA Astrophysics Data System (ADS)

Walter, M. J.; Thomson, A. R.; Wang, W.; Lord, O. T.; Kleppe, A. K.; Ross, J.; Kohn, S. C.

2014-12-01

Laser-heated diamond anvil cell experiments were performed at pressures from ~ 30 to 125 GPa on bulk compositions in the system MgO-Al2O3-SiO2-H2O (MASH) to constrain the stability of hydrous phases in Earth's lower mantle. Phase identification in run products by synchrotron powder diffraction reveals a consistent set of stability relations for the high-pressure, dense hydrous silicate phases D and H. Experiments show that aluminous phase D is stable to ~ 55 GPa. Aluminous phase H becomes stable at ~ 40 GPa and remains stable to higher pressures throughout the lower mantle depth range in both model peridotitic and basaltic lithologies. Preliminary FEG-probe analyses indicate that Phase H is alumina-rich at ~ 50 GPa, with only 5 to 10 wt% each of MgO and SiO2. Variations in ambient unit cell volumes show that Mg-perovskite becomes more aluminous with pressure throughout the pressure range studied, and that Phase H may become more Mg- and Si-rich with pressure. We also find that at pressures above ~ 90 GPa stishovite is replaced in Si-rich compositions by seifertite, at which point there is a corresponding increase in the Al-content of phase H. The melting curves of MASH compositions have been determined using thermal perturbations in power versus temperature curves, and are observed to be shallow with dT/dP slopes of ~ 4K/GPa. Our results show that hydrated peridotitic or basaltic compositions in the lower mantle should be partially molten at all depths along an adiabatic mantle geotherm. Aluminous Phase H will be stable in colder, hydrated subducting slabs, potentially to the core-mantle boundary. Thus, aluminous phase H is the primary vessel for transport of hydrogen to the deepest mantle, but hydrous silicate melt will be the host of hydrogen at ambient mantle temperatures.

Effect of Co2+ Ions Doping on the Structural and Optical Properties of Magnesium Aluminate

NASA Astrophysics Data System (ADS)

Kanwal, Kiran; Ismail, Bushra; Rajani, K. S.; Kissinger, N. J. Suthan; Zeb, Aurang

2017-07-01

Cobalt-doped nanosized magnesium aluminate (Mg1-xCoxAl2O4) samples having different compositions ( x = 0.2, 0.4, 0.6, 0.8, 1.0) were synthesized by a chemical co-precipitation method. All samples were characterized by means of x-ray diffraction (XRD), scanning electron microscopy, Fourier transform infrared spectroscopy, ultra violet-visible spectroscopy, photoluminescence and diffused reflectance spectroscopy. The results of XRD revealed that the samples were spinel single phase cubic close packed crystalline materials. The lattice constant and x-ray density were found to be affected by the ionic radii of the doped metal cations. Using the Debye-Scherrer formula, the calculated crystalline size was found to be Co2+ ion concentration-dependent and varied between 32 nm and 40 nm. Nano-dimensions and phase of the Mg1-xCoxAl2O4 samples were analyzed and the replacement of Mg2+ ions with Co2+ ions was confirmed by elemental analysis. Three strong absorption bands at 540 nm, 580 nm and 630 nm were observed for the doped samples which are attributed to the three spin-allowed 4T1g (4F) → 4T2g, 4A2g, 4T1g (4P) electronic transitions of Co2+ at tetrahedral lattice sites. Nanophosphors have optical properties different from bulk because of spatial confinement and non-radiative relaxation. Decreases in particle size can increase the surface area and the defects, which can in turn increase the luminescent efficiency to make it very useful for tunable laser operations, persistent phosphorescence, color centers, photoconductivity and luminescence for display technology. MgAl2O4 was doped with Co2+ ions using a co-precipitation method and the optical absorption studies revealed that there is a decrease of band gap due to the increase of Co2+ content. The emission intensity of this phosphor is observed at 449 nm with a sharp peak attributed to the smaller size of the particles and the homogeneity of the powder.

Water-sensitive positron trapping modes in nanoporous magnesium aluminate ceramics

NASA Astrophysics Data System (ADS)

Filipecki, J.; Ingram, A.; Klym, H.; Shpotyuk, O.; Vakiv, M.

2007-08-01

The water-sensitive positron trapping modes in nanoporous MgAl2O4 ceramics with a spinel structure are studied. It is shown that water-sorption processes in magnesium aluminate ceramics leads to corresponding increase in positron trapping rates of extended defects located near intergranual boundaries. This catalytic affect has reversible nature, being strongly dependent on sorption water fluxes in ceramics. The fixation of all water-dependent positron trapping inputs allow to refine the most significant changes in positron trapping rate of extended defects.

Growth and Structure of Strontium Doped LaGaO3

DTIC Science & Technology

2001-01-01

Sandstrom, E.A. Giess, W.J. Gallagher, A. Segmifler, E.I. Cooper, M.F. Chisholm, A. Gupta, S. Shinole, R.B. Laibowitz," Lanthanum gallate substrates...that a structural phase transition occurs at -150 °C 5. The phase transition is the most serious drawback of many lanthanide gallates and aluminates5 for...and C.D. Brandle, "Thermal analysis of rare earth gallates and aluminates", J Mater. Res. 5, p. 183, 1990. 6. S. Miyazawa," Surface roughening

Nondestructive evaluation of orthopaedic implant stability in THA using highly nonlinear solitary waves

NASA Astrophysics Data System (ADS)

Yang, Jinkyu; Silvestro, Claudio; Sangiorgio, Sophia N.; Borkowski, Sean L.; Ebramzadeh, Edward; De Nardo, Luigi; Daraio, Chiara

2012-01-01

We propose a new biomedical sensing technique based on highly nonlinear solitary waves to assess orthopaedic implant stability in a nondestructive and efficient manner. We assemble a granular crystal actuator consisting of a one-dimensional tightly packed array of spherical particles, to generate acoustic solitary waves. Via direct contact with the specimen, we inject acoustic solitary waves into a biomedical prosthesis, and we nondestructively evaluate the mechanical integrity of the bone-prosthesis interface, studying the properties of the waves reflected from the contact zone between the granular crystal and the implant. The granular crystal contains a piezoelectric sensor to measure the travelling solitary waves, which allows it to function also as a sensor. We perform a feasibility study using total hip arthroplasty (THA) samples made of metallic stems implanted in artificial composite femurs using polymethylmethacrylate for fixation. We first evaluate the sensitivity of the proposed granular crystal sensor to various levels of prosthesis insertion into the composite femur. Then, we impose a sequence of harsh mechanical loading on the THA samples to degrade the mechanical integrity at the stem-cement interfaces, using a femoral load simulator that simulates aggressive, accelerated physiological loading. We investigate the implant stability via the granular crystal sensor-actuator during testing. Preliminary results suggest that the reflected waves respond sensitively to the degree of implant fixation. In particular, the granular crystal sensor-actuator successfully detects implant loosening at the stem-cement interface following violent cyclic loading. This study suggests that the granular crystal sensor and actuator has the potential to detect metal-cement defects in a nondestructive manner for orthopaedic applications.

New support for high-performance liquid chromatography based on silica coated with alumina particles.

PubMed

Silveira, José Leandro R; Dib, Samia R; Faria, Anizio M

2014-01-01

A new material based on silica coated with alumina nanoparticles was proposed for use as a chromatographic support for reversed-phase high-performance liquid chromatography. Alumina nanoparticles were synthesized by a sol-gel process in reversed micelles composed of sodium bis(2-ethylhexyl)sulfosuccinate, and the support material was formed by the self-assembly of alumina layers on silica spheres. Spectroscopic and (29)Si nuclear magnetic resonance results showed evidence of chemical bonds between the alumina nanoparticles and the silica spheres, while morphological characterizations showed that the aluminized silica maintained the morphological properties of silica desired for chromatographic purposes after alumina incorporation. Stability studies indicated that bare silica showed high dissolution (~83%), while the aluminized silica remained practically unchanged (99%) after passing one liter of the alkaline mobile phase, indicating high stability under alkaline conditions. The C18 bonded aluminized silica phase showed great potential for use in high-performance liquid chromatography to separate basic molecules in the reversed-phase mode.

Rear surface light emission measurements from laser-produced shock waves in clear and Al-coated polystyrene targets

NASA Astrophysics Data System (ADS)

McLean, E. A.; Deniz, A. V.; Schmitt, A. J.; Stamper, J. A.; Obenschain, S. P.; Lehecka, T.; Mostovych, A. N.; Seely, J.

1999-08-01

The Nike KrF laser, with its very uniform focal distributions, has been used at intensities near 10 14 W/cm 2 to launch shock waves in polystyrene targets. The rear surface visible light emission differed between clear polystyrene (CH) targets and targets with a thin (125 nm) Al coating on the rear side. The uncoated CH targets showed a relatively slowly rising emission followed by a sudden fall when the shock emerges, while the Al-coated targets showed a rapid rise in emission when the shock emerges followed by a slower fall, allowing an unambiguous determination of the time the shock arrived at the rear surface. A half-aluminized target allowed us to observe this difference in a single shot. The brightness temperature of both the aluminized targets and the non-aluminized targets was slightly below but close to rear surface temperature predictions of a hydrodynamic code. A discussion of preheat effects is given.

Aluminate effect on desilication product phase transformation

NASA Astrophysics Data System (ADS)

Peng, Hong; Vaughan, James

2018-06-01

It remains a grand challenge in the treatment of bauxite residue to physically separate zeolite (also known as the DeSilication Product, DSP) from other unleached mineral phases owing to their fine sizes, typically less than 2 μm in diameter. In this study, the effect of aluminate concentration on DSP phase transformation was investigated from synthetic NaOH-NaAl(OH)4-Na2SiO3-H2O solution at 90 °C. The results show how at relatively low aluminate concentrations of 0.125 and 0.25 M NaAl(OH)4(aq), larger zeolite crystals of up to 60 μm in diameter are formed during homogenous precipitation from aqueous solution. The precipitation process involves the conversion of zeolite LTA to sodalite via the formation of an intermediate phase, octahedral LTN. Initial amorphous solids precipitate as aggregates in which cubic zeolite LTA nucleation occurs. As the reaction proceeds, truncated octahedral LTN appears with the cubic zeolite LTA and finally sodalite crystallizes on the LTA-LTN aggregates resulting in coarsened particles.

Formation of Aluminide Coatings on Fe-Based Alloys by Chemical Vapor Deposition

DOE Office of Scientific and Technical Information (OSTI.GOV)

Zhang, Ying; Pint, Bruce A; Cooley, Kevin M

2008-01-01

Aluminide and Al-containing coatings were synthesized on commercial ferritic (P91) and austenitic (304L) alloys via a laboratory chemical vapor deposition (CVD) procedure for rigorous control over coating composition, purity and microstructure. The effect of the CVD aluminizing parameters such as temperature, Al activity, and post-aluminizing anneal on coating growth was investigated. Two procedures involving different Al activities were employed with and without including Cr-Al pellets in the CVD reactor to produce coatings with suitable thickness and composition for coating performance evaluation. The phase constitution of the as-synthesized coatings was assessed with the aid of a combination of X-ray diffraction, electronmore » probe microanalysis, and existing phase diagrams. The mechanisms of formation of these CVD coatings on the Fe-based alloys are discussed, and compared with nickel aluminide coatings on Ni-base superalloys. In addition, Cr-Al pellets were replaced with Fe-Al metals in some aluminizing process runs and similar coatings were achieved.« less

A New Method for Determining the Equation of State of Aluminized Explosive

NASA Astrophysics Data System (ADS)

Zhou, Zheng-Qing; Nie, Jian-Xin; Guo, Xue-Yong; Wang, Qiu-Shi; Ou, Zhuo-Cheng; Jiao, Qing-Jie

2015-01-01

The time-dependent Jones—Wilkins—Lee equation of state (JWL-EOS) is applied to describe detonation state products for aluminized explosives. To obtain the time-dependent JWL-EOS parameters, cylinder tests and underwater explosion experiments are performed. According to the result of the wall radial velocity in cylinder tests and the shock wave pressures in underwater explosion experiments, the time-dependent JWL-EOS parameters are determined by iterating these variables in AUTODYN hydrocode simulations until the experimental values are reproduced. In addition, to verify the reliability of the derived JWL-EOS parameters, the aluminized explosive experiment is conducted in concrete. The shock wave pressures in the affected concrete bodies are measured by using manganin pressure sensors, and the rod velocity is obtained by using a high-speed camera. Simultaneously, the shock wave pressure and the rod velocity are calculated by using the derived time-dependent JWL equation of state. The calculated results are in good agreement with the experimental data.

The Effect of Petrographic Characteristics on Engineering Properties of Conglomerates from Famenin Region, Northeast of Hamedan, Iran

NASA Astrophysics Data System (ADS)

Khanlari, G. R.; Heidari, M.; Noori, M.; Momeni, A.

2016-07-01

To assess relationship between engineering characteristics and petrographic features, conglomerates samples related to Qom formation from Famenin region in northeast of Hamedan province were studied. Samples were tested in laboratory to determine the uniaxial compressive strength, point load strength index, modulus of elasticity, porosity, dry and saturation densities. For determining petrographic features, textural and mineralogical parameters, thin sections of the samples were prepared and studied. The results show that the effect of textural characteristics on the engineering properties of conglomerates supposed to be more important than mineralogical composition. It also was concluded that the packing proximity, packing density, grain shape and mean grain size, cement and matrix frequency are as textural features that have a significant effect on the physical and mechanical properties of the studied conglomerates. In this study, predictive statistical relationships were developed to estimate the physical and mechanical properties of the rocks based on the results of petrographic features. Furthermore, multivariate linear regression was used in four different steps comprising various combinations of petrographical characteristics for each engineering parameters. Finally, the best equations with specific arrangement were suggested to estimate engineering properties of the Qom formation conglomerates.

Temperature and Pressure Sensors Based on Spin-Allowed Broadband Luminescence of Doped Orthorhombic Perovskite Structures

NASA Technical Reports Server (NTRS)

Eldridge, Jeffrey I. (Inventor); Chambers, Matthew D. (Inventor)

2014-01-01

Systems and methods that are capable of measuring pressure or temperature based on luminescence are discussed herein. These systems and methods are based on spin-allowed broadband luminescence of sensors with orthorhombic perovskite structures of rare earth aluminates doped with chromium or similar transition metals, such as chromium-doped gadolinium aluminate. Luminescence from these sensors can be measured to determine at least one of temperature or pressure, based on either the intense luminescence of these sensors, even at high temperatures, or low temperature techniques discussed herein.

System and process for aluminization of metal-containing substrates

DOEpatents

Chou, Yeong-Shyung; Stevenson, Jeffry W.

2017-12-12

A system and method are detailed for aluminizing surfaces of metallic substrates, parts, and components with a protective alumina layer in-situ. Aluminum (Al) foil sandwiched between the metallic components and a refractory material when heated in an oxidizing gas under a compression load at a selected temperature forms the protective alumina coating on the surface of the metallic components. The alumina coating minimizes evaporation of volatile metals from the metallic substrates, parts, and components in assembled devices that can degrade performance during operation at high temperature.

System and process for aluminization of metal-containing substrates

DOEpatents

Chou, Yeong-Shyung; Stevenson, Jeffry W

2015-11-03

A system and method are detailed for aluminizing surfaces of metallic substrates, parts, and components with a protective alumina layer in-situ. Aluminum (Al) foil sandwiched between the metallic components and a refractory material when heated in an oxidizing gas under a compression load at a selected temperature forms the protective alumina coating on the surface of the metallic components. The alumina coating minimizes evaporation of volatile metals from the metallic substrates, parts, and components in assembled devices during operation at high temperature that can degrade performance.

Possibilities and Limitations of Multioxides Crystals Growth

DTIC Science & Technology

2001-01-01

between 1 26 neodymium and lanthanum along growth direction of c,=33 mol % NdGaO3 Laj-,Nd.GaO3 single crystals 7. Concentration of 2 24- k= 0.77 (A-0.008...50, 60 and 66.6 mol.% of lanthanum aluminate concentration. The crystals adopt cubic structure at x up to 0.50 with the half of lattice constant...from the melt containing 22 mol.% and 30 Proc. SPIE Vol. 4412 more lanthanum aluminate were light yellow if the 3.90 processes were carried out in pure

Porous electrolyte retainer for molten carbonate fuel cell. [lithium aluminate

DOEpatents

Singh, R.N.; Dusek, J.T.

1979-12-27

A porous tile for retaining molten electrolyte within a fuel cell is prepared by sintering particles of lithium aluminate into a stable structure. The tile is assembled between two porous metal plates which serve as electrodes with fuels gases such as H/sub 2/ and CO opposite to oxidant gases such as O/sub 2/ and CO/sub 2/. The tile is prepared with a porosity of 55 to 65% and a pore size distribution selected to permit release of sufficient molten electrolyte to wet but not to flood the adjacent electrodes.

Phase Equilibria of Stored Chemical Energy Reactants.

DTIC Science & Technology

1984-07-25

aluminate-lithium ferrate system. Detection of a Li1 Al4/7Fe 3/704 compound: C. R. Acad. Sci., Ser. C, V. 273, No. 15, p. 888-90. McNicol, B. D. and Pott...thermodynamic properties of lithium ferrate (LiO.5Fe2 .504) and lithium aluminate (LiO 5Al 2 504) from 5 to 545 K: J. Chem. Thermodyn., V. 7, No. 7, p. 693- 2...1977, Study of low-temperature hydrothermal crystallization in lithium oxide-silicon dioxide-water, potassium oxide-silicon dioxide-water, and

Oxidation of high-temperature intermetallics; Proceedings of the Workshop, Cleveland, OH, Sept. 22, 23, 1988

NASA Technical Reports Server (NTRS)

Grobstein, Toni (Editor); Doychak, Joseph (Editor)

1989-01-01

The present conference on the high-temperature oxidation behavior of aerospace structures-applicable intermetallic compounds discusses the influence of reactive-element additions on the oxidation of Ni3Al base alloys, the effect of Ni3Al oxidation below 850 C on fracture behavior, the oxidation of FeAl + Hf, Zr, and B, the synergistic effect of Al and Si on the oxidation resistance of Fe alloys, and pack cementation coatings of Cr-Al on Fe, Ni, and Co alloys. Also discussed are the formation of alumina on Nb- and Ti-base alloys, the oxidation behavior of titanium aluminide alloys, silicide coatings for refractory metals, the oxidation of chromium disilicide, and the oxidation behavior of nickel beryllides.

Textural evidence for jamming and dewatering of a sub-surface, fluid-saturated granular flow

NASA Astrophysics Data System (ADS)

Sherry, T. J.; Rowe, C. D.; Kirkpatrick, J. D.; Brodsky, E. E.

2011-12-01

Sand injectites are spectacular examples of large-scale granular flows involving migration of hundreds of cubic meters of sand slurry over hundreds of meters to kilometers in the sub-surface. By studying the macro- and microstructural textures of a kilometer-scale sand injectite, we interpret the fluid flow regimes during emplacement and define the timing of formation of specific textures in the injected material. Fluidized sand sourced from the Santa Margarita Fm., was injected upward into the Santa Cruz Mudstone, Santa Cruz County, California. The sand injectite exposed at Yellow Bank Beach records emplacement of both hydrocarbon and aqueous sand slurries. Elongate, angular mudstone clasts were ripped from the wall rock during sand migration, providing evidence for high velocity, turbid flow. However, clast long axis orientations are consistently sub-horizontal suggesting the slurry transitioned to a laminar flow as the flow velocity decreased in the sill-like intrusion. Millimeter to centimeter scale laminations are ubiquitous throughout the sand body and are locally parallel to the mudstone clast long axes. The laminations are distinct in exposure because alternating layers are preferentially cemented with limonite sourced from later groundwater infiltration. Quantitative microstructural analyses show that the laminations are defined by subtle oscillations in grain alignment between limonite and non-limonite stained layers. Grain packing, size and shape distributions do not vary. The presence of limonite in alternating layers results from differential infiltration of groundwater, indicating permeability changes between the layers despite minimal grain scale differences. Convolute dewatering structures deform the laminations. Dolomite-cemented sand, a signature of hydrocarbon saturation, forms irregular bodies that cross-cut the laminations and dewatering structures. Laminations are not formed in the dolomite-cemented sand. The relative viscosity difference between the hydrocarbon and aqueous sand slurries controls the the critical radius of the contacts between dolomite cemented and limonite cemented sand bodies. The cross-cutting relationships established in the field show that the laminations formed at the jamming transition in the aqueous sand slurry. We interpret the laminations as preserving evidence for dynamic permeability instabilities in the dewatering slurry. Relatively high permeability channels formed as pore fluid flow rearranged grains during initial dewatering. Once initiated, the flow localized further into the higher permeability channels resulting in a feedback that caused the permeability in the channels to increase.

DNA adsorption onto glass surfaces

NASA Astrophysics Data System (ADS)

Carlson, Krista Lynn

Streaming potential measurements were performed on microspheres of silica, lime silicate (SLS) and calcium aluminate (CA) glasses containing silica and iron oxide (CASi and CAFe). The silicate based glasses exhibited acidic surfaces with isoelectric points (IEP) around a pH of 3 while the calcium aluminates displayed more basic surfaces with IEP ranging from 8--9.5. The surface of the calcium aluminate microspheres containing silica reacted with the background electrolyte, altering the measured zeta potential values and inhibiting electrolyte flow past the sample at ˜ pH 4 due to formation of a solid plug. DNA adsorption experiments were performed using the microspheres and a commercially available silicate based DNA isolation filter using a known quantity of DNA suspended in a chaotropic agent free 0.35 wt% Tris(hydroxymethyl)aminomethane (Tris) buffer solution. The microspheres and commercial filter were also used to isolate DNA from macrophage cells in the presence of chaotropic agents. UV absorbance at ˜260 nm and gel electrophoresis were used to quantify the amount and size of the DNA strands that adsorbed to the microsphere surfaces. In both experiments, the 43--106 microm CAFe microspheres adsorbed the largest quantity of DNA. However, the 43--106 microm SLS microspheres isolated more DNA from the cells than the <43 microm CAFe microspheres, indicating that microsphere size contributes to isolation ability. The UV absorbance of DNA at ˜260 nm was slightly altered due to the dissolution of the calcium aluminate glasses during the adsorption process. Inductively coupled plasma-optical emission spectroscopy (ICP-OES) determined that calcium and aluminum ions leached from the CA and CAFe microsphere surfaces during these experiments. Circular dichroism (CD) spectroscopy showed that the leached ions had no effect on the conformation of the DNA, and therefore would not be expected to interfere in downstream applications such as DNA replication. The 0.35 wt% Tris solution completely inhibited the formation of the hydrated crystalline layer that develops when the calcium aluminate glassess are incubated in deionized water. A Tris concentration of 0.24 wt% allowed for the formation of both hexagonal and cubic hydrates, however they were severely distorted and present in low amounts such that they were undectable by XRD.

Preparation of ceramic coating on Ti substrate by Plasma electrolytic oxidation in different electrolytes and evaluation of its corrosion resistance

NASA Astrophysics Data System (ADS)

Shokouhfar, M.; Dehghanian, C.; Baradaran, A.

2011-01-01

Ceramic oxide coatings (titania) were produced on Ti by micro-arc oxidation in different aluminate and carbonate based electrolytes. This process was conducted under constant pulsed DC voltage condition. The effect of KOH and NaF in aluminate based solution was also studied. The surface morphology, growth and phase composition of coatings were investigated using scanning electron microscope and X-ray diffraction. Corrosion behavior of the coatings was also examined by potentiodynamic polarization and electrochemical impedance spectroscopy. It was found that the sparking initiation voltage (spark voltage) had a significant effect on the form and properties of coatings. Coatings obtained from potassium aluminate based solution had a lower spark voltage, higher surface homogeneity and a better corrosion resistance than the carbonate based solution. Addition of NaF instead of KOH had improper effects on the homogeneity and adhesion of coatings which in turn caused a poor corrosion protection behavior of the oxide layer. AC impedance curves showed two time constants which is an indication of the coatings with an outer porous layer and an inner compact layer.

Effect of Air and Vacuum Storage on the Tensile Properties of X-Ray Exposed Aluminized-FEP

NASA Technical Reports Server (NTRS)

deGroh, Kim K.; Gummow, Jonathan D.

2000-01-01

Metallized Teflon(Registered Trademark) FEP (fluorinated ethylene propylene), a common spacecraft thermal control material, from the exterior layer of the Hubble Space Telescope (HST) has become embrittled and suffers from extensive cracking. Teflon samples retrieved during Hubble servicing missions and from the Long Duration Exposure Facility (LDEF) indicate that there may be continued degradation in tensile properties over time. An investigation has been conducted to evaluate the effect of air and vacuum storage on the mechanical properties of x-ray exposed FEP. Aluminized-FEP (Al-FEP) tensile samples were irradiated with 15.3 kV Cu x-rays and stored in air or under vacuum for various time periods. Tensile data indicate that samples stored in air display larger decreases in tensile properties than for samples stored under vacuum. Air-stored samples developed a hazy appearance, which corresponded to a roughening of the aluminized surface. Optical property changes were also characterized. These findings indicate that air exposure plays a role in the degradation of irradiated FEP, therefore proper sample handling and storage is necessary with materials retrieved from space.

Using Underwater Explosion and Cylinder Expansion Tests to Calibrate Afterburn Models for Aluminized Explosives

NASA Astrophysics Data System (ADS)

Wedberg, Rasmus

2017-06-01

The study explores the combined use of underwater performance tests and cylinder expansion tests in order to parameterize detonation models for aluminized explosives which exhibit afterburning. The approach is suggested to be used in conjunction with thermochemical computation. A formulation containing RDX and aluminum powder is considered and several charges with varying masses are submerged and detonated. Pressure gauges are employed at horizontal distances scaling with the charge diameter, and the specific shock wave energy is shown to increase with charge mass. This is attributed to the combustion of aluminum particles after the Chapman-Jouguet plane. Cylinder expansion tests are carried out using Photon Doppler Velocimetry to register the wall expansion velocity. The tests are modeled using a multi-material arbitrary Lagrangian-Eulerian approach with the Guirguis-Miller model describing detonation with afterburning. The equation of state and afterburn rate law parameters are adjusted such that the model reproduces the results from the cylinder expansion and underwater tests. The approach seems promising, and might be valuable for aluminized explosive formulations intended to be used in a variety of confinement conditions. Swedish Armed Forces.

Sodium Aluminate Concentration Effects on Microstructure and Corrosion Behavior of the Plasma Electrolytic Oxidation Coatings on Pure Titanium

NASA Astrophysics Data System (ADS)

Molaei, Maryam; Fattah-Alhosseini, Arash; Gashti, Seyed Omid

2018-01-01

Sodium aluminate (NaAlO2) concentration was varied in order to understand the influence of the chemical composition of electrolyte on the spark characteristics, microstructure, and corrosion behavior of plasma electrolytic oxidation (PEO) coatings. For this purpose, PEO coatings were formed on the pure titanium substrate surface using solutions of four diverse sodium aluminate concentrations (6, 8, 10, and 12 g/L). The PEO process was carried out at constant time and voltage (180 seconds and 420 V). Studying the microstructures of samples by scanning electron microscope (SEM) and their corrosion behavior in 3.5 wt pct NaCl solutions indicated that the increase in NaAlO2 concentration (up to 10 g/L) led to an increase in uniformity and compactness, thus decreasing the size of micro-pores and increment of corrosion resistance. However, at a certain level of NaAlO2 concentration (12 g/L), large and severe sparks were created on the surface of the sample during the process, worsening the corrosion resistance and microstructure of coating.

Ground Laboratory Soft X-Ray Durability Evaluation of Aluminized Teflon FEP Thermal Control Insulation

NASA Technical Reports Server (NTRS)

Banks, Bruce A.; deGroh, Kim K.; Stueber, Thomas J.; Sechkar, Edward A.

1998-01-01

Metallized Teflon fluorinated ethylene propylene (FEP) thermal control insulation is mechanically degraded if exposed to a sufficient fluence of soft x-ray radiation. Soft x-ray photons (4-8 A in wavelength or 1.55 - 3.2 keV) emitted during solar flares have been proposed as a cause of mechanical properties degradation of aluminized Teflon FEP thermal control insulation on the Hubble Space Telescope (HST). Such degradation can be characterized by a reduction in elongation-to-failure of the Teflon FER Ground laboratory soft x-ray exposure tests of aluminized Teflon FEP were conducted to assess the degree of elongation degradation which would occur as a result of exposure to soft x-rays in the range of 3-10 keV. Tests results indicate that soft x-ray exposure in the 3-10 keV range, at mission fluence levels, does not alone cause the observed reduction in elongation of flight retrieved samples. The soft x-ray exposure facility design, mechanical properties degradation results and implications will be presented.

Ground Laboratory Soft X-Ray Durability Evaluation of Aluminized Teflon FEP Thermal Control Insulation. Revised

NASA Technical Reports Server (NTRS)

Banks, Bruce A.; deGroh, Kim K.; Stueber, Thomas J.; Sechkar, Edward A.; Hall, Rachelle L.

1998-01-01

Metallized Teflon fluorinated ethylene propylene (FEP) thermal control insulation is mechanically degraded if exposed to a sufficient fluence of soft x-ray radiation. Soft x-ray photons (4-8 A in wavelength or 1.55 - 3.2 keV) emitted during solar flares have been proposed as a cause of mechanical properties degradation of aluminized Teflon FEP thermal control insulation on the Hubble Space Telescope (HST). Such degradation can be characterized by a reduction in elongation-to-failure of the Teflon FEP. Ground laboratory soft x-ray exposure tests of aluminized Teflon FEP were conducted to assess the degree of elongation degradation which would occur as a result of exposure to soft x-rays in the range of 3-10 keV. Tests results indicate that soft x-ray exposure in the 3-10 keV range, at mission fluence levels, does not alone cause the observed reduction in elongation of flight retrieved samples. The soft x-ray exposure facility design, mechanical properties degradation results and implications will be presented.

Effect of rapid set binder on early strength and permeability of HES latex modified road repair pre-packed concrete

NASA Astrophysics Data System (ADS)

Han, J. W.; Lee, S. K.; Yu, C.; Park, C. G.

2015-12-01

The early strength development characteristics and permeability resistance of high early strength (HES) pre-packed road repair concrete incorporating a rapid-set binder material were evaluated for emergency repairs to road pavement. The rapid-set binder is a mixture of rapid-set cement and silica sands whose fluidity improves with the addition of styrene butadiene latex (latex). The resulting mixture has a compressive strength of 21 MPa or higher and a flexural strength of greater than 3.5 MPa after 4 hours, the maximum curing age allowed for emergency repair materials. This study examines the strength development properties and permeability resistance of HES latex-modified pre-packed road repair concrete using a rapid- set binder as a function of the latex-to-binder mixing ratio at values of 0.40, 0.33, 0.29 and 0.25. Both early strength development properties and permeability resistance increased as the ratio of latex to rapid-set binder decreased. The mixture showed a compressive strength of 21 MPa or higher after 4 hours, which is the design standard of emergency repair concrete, only when this ratio was 0.29 or lower. A flexural strength of 3.5 MPa or greater was observed after hours only when this ratio was 0.33 or lower. The standard for permeability resistance, less than 2,000 C of chloride after 7 days of curing, was satisfied by all ratios. The ratio of latex to rapid-set binder satisfying all of the conditions for an emergency road repair material was 0.29 or less.

Three diverse target preparations: 14C (12 mg/cm 2), 71Ga 24Mg (12 mg/cm 271Ga, 3 mg/cm 224Mg), and 66,67Zn (1.8-14.9 mg/cm 2)

NASA Astrophysics Data System (ADS)

Lozowski, W. R.

1989-10-01

A natural-carbon analog of fluffy, intractable 14C powder was produced. With it, a method was developed to produce a pressed disk of 14C of 12.7-mg/cm 2 thickness and 1.27-cm diameter, bound with 2.1 wt.% of adhesive. Aluminized Mylar cover foils and a fritted-disc filter were used to contain the target for ( overlinep, p') experiments. Reduction of 71Ga 2O 3 to the metal was accomplished with an efficiency of 94.3% in a small electroplating cell. Magnesium was chosen as the companion element because 50 at.% could be tolerated in the (p, n) experiment, and GaMg has a melting point of 646 K. A 1.27-cm diameter target, supported at the edge by a Mg foil, was produced in several simple steps. Directly rollable 66,67Zn foils were obtained from an electroplating cell with a Pt screen anode and a highly polished tungsten-carbide cathode. Plating times of 3 h provided metal-recovery efficiencies ranging from 94.2 to 96.5%. The as-deposited foils had many holes but were hole-free and shiny after reduction of 25% by pack rolling.

Local structural relaxation around Co2+ along the hardystonite-Co-åkermanite melilite solid solution

NASA Astrophysics Data System (ADS)

Ardit, Matteo; Cruciani, Giuseppe; Dondi, Michele

2012-10-01

Six pure compounds belonging to the hardystonite (Ca2ZnSi2O7)-Co-åkermanite (Ca2CoSi2O7) solid solution were investigated by the combined application of X-ray powder diffraction and electronic absorption spectroscopy. Structural refinements of the XRPD data revealed a negative excess volume of mixing due to the single isovalent substitution of Co for Zn in the tetrahedral site. In agreement with the diffraction data, deconvolution of the optical spectra showed a progressive decreasing of the crystal field strength parameter 10 Dq moving toward the Co-åkermanite end-member, meaning that the local cobalt-oxygen bond distance, < {{Co}}{-}{{O}}rangle^{{local}} , increased along the join with the amount of cobalt. The calculated structural relaxation coefficient around the fourfold coordinated Co2+ in the Ca2(Zn1- x Co x )Si2O7 join was ɛ = 0.69, very far from the one predicted by the Vegard's law ( ɛ = 0) and at variance with ɛ = 0.47 previously found for tetrahedrally coordinated Co2+ in gahnite-Co-aluminate spinel solid solution. This difference is consistent with the largest constraints existing on the spinel structure, based on cubic closest packing, compared to the more flexible layered melilite structure.

Large Binocular Telescope project

NASA Astrophysics Data System (ADS)

Hill, John M.; Salinari, Piero

2003-02-01

The Large Binocular Telescope (LBT) Project is a collaboration between institutions in Arizona, Germany, Italy, and Ohio. The first of two 8.4-meter borosilicate honeycomb primary mirrors for LBT is being polished at the Steward Observatory Mirror Lab this year. The second of the two 8.4-meter mirror blanks waits its turn in the polishing queue. The baseline optical configuration of LBT includes adaptive infrared secondaries of a Gregorian design. The F/15 secondaries are undersized to provide a low thermal background focal plane which is unvignetted over a 4-arcminute diameter field-of-view. These adaptive secondary mirrors with 672 voice-coil actuators are now in the early stages of fabrication. The interferometric focus combining the light from the two 8.4-meter primaries will reimage the two folded Gregorian focal planes to three central locations for phased array imaging. The telescope elevation structure accommodates swing arm spiders which allow rapid interchange of the various secondary and tertiary mirrors as well as prime focus cameras. The telescope structure accommodates installation of a vacuum bell jar for aluminizing the primary mirrors in-situ on the telescope. The telescope structure was fabricated and pre-assembled in Italy by Ansaldo-Camozzi in Milan. The structure was disassembled, packed and shipped to Arizona. The enclosure was built on Mt. Graham and is ready for telescope installation.

Space Environmental Effects Testing and Characterization of the Candidate Solar Sail Material Aluminized Mylar

NASA Technical Reports Server (NTRS)

Edwards, D. L.; Hubbs, W. S.; Wertz, G. E.; Alstatt, R.; Munafo, Paul (Technical Monitor)

2001-01-01

The usage of solar sails as a propellantless propulsion system has been proposed for many years. The technical challenges associated with solar sails are fabrication of ultralightweight films, deploying the sails and controlling the spacecraft. Integral to all these challenges is the mechanical property integrity of the sail while exposed to the harsh environment of space. This paper describes testing and characterization of a candidate solar sail material, Aluminized Mylar. This material was exposed to a simulated Geosynchronous Transfer Orbit (GTO) and evaluated by measuring thermooptical and mechanical property changes. Testing procedures and results are presented.

Flexure Strength and Optical Transparency of Magnesium-Aluminate Spinel (MgAlO4): Influence of Polishing and Glass Coating

DTIC Science & Technology

2016-12-01

resulting from the addition of a sodium aluminosilicate ( SiO2 -BaO- Na2O-B2O3-Al2O3) glass coating on coarse-grained transparent spinel having 3...MgAlO4): Influence of Polishing and Glass Coating by Steve M Kilczewski, Robert J Pavlacka, Jeffrey J Swab, Jane W Adams, and Jared C Wright...Magnesium–Aluminate Spinel (MgAlO4): Influence of Polishing and Glass Coating by Steve M Kilczewski and Jared C Wright TKC Global, Herndon, VA

Formation of copper aluminate spinel and cuprous aluminate delafossite to thermally stabilize simulated copper-laden sludge.

PubMed

Hu, Ching-Yao; Shih, Kaimin; Leckie, James O

2010-09-15

The study reported herein indicated the stabilization mechanisms at work when copper-laden sludge is thermally treated with gamma-alumina and kaolinite precursors, and evaluated the prolonged leachability of their product phases. Four copper-containing phases - copper oxide (CuO), cuprous oxide (Cu(2)O), copper aluminate spinel (CuAl(2)O(4)), and cuprous aluminate delafossite (CuAlO(2)) - were found in the thermal reactions of the investigated systems. These phases were independently synthesized for leaching by 0.1M HCl aqueous solution, and the relative leachabilities were found to be CuAl(2)O(4)

Prolonged toxicity characteristic leaching procedure for nickel and copper aluminates.

PubMed

Shih, Kaimin; Tang, Yuanyuan

2011-04-01

The toxicity characteristic leaching procedure (TCLP) is a regulatory testing method widely employed to evaluate the environmental friendliness of waste materials. TCLP analysis provides a fast, easy and economical way to determine the mobility of waste pollutants under simulated landfill conditions. Recent studies on metal stabilization have reported the potential for nickel and copper aluminates to form in thermal treatment conditions, and suggested a more reliable method of stabilizing hazardous metals, particularly when products are to be reused. There is thus an urgent need for a convenient and effective method of quantifying metal leachability and identifying the metal leaching behavior of sparingly soluble materials. In this study, standard TCLP analysis was modified into a prolonged leaching experiment to investigate the leaching behavior of nickel and copper oxides (NiO and CuO) and their aluminates (NiAl(2)O(4), CuAl(2)O(4) and CuAlO(2)). The results demonstrate the difficulty of differentiating the leachability of highly insoluble phases, such as NiO and NiAl(2)O(4), using the standard TCLP. The prolonged TCLP method, however, confirmed NiAl(2)O(4) to have a lower degree of intrinsic leachability than NiO and that it could be expected to undergo congruent dissolution under landfill conditions. For the more soluble copper system, the aluminates were still found to possess a much lower degree of leachability, and their leaching behavior to follow an incongruent dissolution pattern. The results of this study prove prolonged TCLP analysis to be a convenient and effective way to evaluate the environmental friendliness of metal waste and to identify the leaching behavior of waste materials.

Reinforced Carbon Carbon (RCC) oxidation resistant material samples - Baseline coated, and baseline coated with tetraethyl orthosilicate (TEOS) impregnation

NASA Technical Reports Server (NTRS)

Gantz, E. E.

1977-01-01

Reinforced carbon-carbon material specimens were machined from 19 and 33 ply flat panels which were fabricated and processed in accordance with the specifications and procedures accepted for the fabrication and processing of the leading edge structural subsystem (LESS) elements for the space shuttle orbiter. The specimens were then baseline coated and tetraethyl orthosilicate impregnated, as applicable, in accordance with the procedures and requirements of the appropriate LESS production specifications. Three heater bars were ATJ graphite silicon carbide coated with the Vought 'pack cementation' coating process, and three were stackpole grade 2020 graphite silicon carbide coated with the chemical vapor deposition process utilized by Vought in coating the LESS shell development program entry heater elements. Nondestructive test results are reported.

Chronic Osteomyelitis of the Distal Femur Treated with Resection and Delayed Endoprosthetic Reconstruction: A Report of Three Cases.

PubMed

Ryan, Sean; Eward, William; Brigman, Brian; Zura, Robert

2017-01-01

Chronic osteomyelitis involving the distal femur often results in amputation or arthrodesis. This article presents three cases of chronic osteomyelitis treated with a staged approach culminating in endoprosthetic reconstruction. Stage one involved resection of infected bone and placement of an intramedullary nail spanning the bony defect between proximal femur and tibia, with antibiotic cement packed around the nail. Patients were then placed on long-term IV +/- oral antibiotics to clear the infection. A "cooldown" period was then used between stages where patients were off antibiotics and inflammatory markers were monitored for signs of remaining infection. Stage two then involved reconstruction of the distal femur and knee with an endoprosthesis. In the appropriate patient, this treatment strategy offers another option in this challenging population.

Interaction between solar energetic particles and interplanetary grains

NASA Astrophysics Data System (ADS)

Strazzulla, G.; Calcagno, L.; Foti, G.; Sheng, K. L.

Some laboratory-studied effects induced by the fluence of fast ions on frosts of astrophysical interest are summarized. The results are applied to the interaction between energetic solar ions and interplanetary dust grains assumed to be cometary debris which spends about one-million yr before being collected in the earth's atmosphere or colliding on the moon's surface. The importance of erosion by particles to the stability of ice grains is confirmed. The build up of carbonaceous material by ion fluence on hydrocarbon containing grains is discussed. It is suggested that these new materials could be the glue which cements submicron silicate particles to form a complex agglomeration whose density increases with increasing proton fluence (packing effect). The IR spectra of laboratory synthesized carbonaceous material are compared with those observed in some carbonaceous meteoritic extracts.

Investigation of carbonate rocks appropriate for the production of natural hydraulic lime binders

NASA Astrophysics Data System (ADS)

Triantafyllou, George; Panagopoulos, George; Manoutsoglou, Emmanouil; Christidis, George; Přikryl, Richard

2014-05-01

Cement industry is facing growing challenges in conserving materials and conforming to the demanding environmental standards. Therefore, there is great interest in the development, investigation and use of binders alternatives to Portland cement. Natural hydraulic lime (NHL) binders have become nowadays materials with high added value, due to their advantages in various construction applications. Some of them include compatibility, suitability, workability and the versatility in applications. NHL binders are made from limestones which contain sufficient argillaceous or siliceous components fired at relatively low temperatures, with reduction to powder by slaking with or without grinding. This study is focused in developing technology for small-scale production of cementitious binders, combining the knowledge and experience of geologists and mineral resources engineers. The first step of investigation includes field techniques to the study the lithology, texture and sedimentary structure of Neogene carbonate sediments, from various basins of Crete Island, Greece and the construction of 3D geological models, in order to determine the deposits of each different geological formation. Sampling of appropriate quantity of raw materials is crucial for the investigation. Petrographic studies on the basis of the study of grain type, grain size, types of porosity and depositional texture, are necessary to classify effectively industrial mineral raw materials for this kind of application. Laboratory tests should also include the study of mineralogical and chemical composition of the bulk raw materials, as well as the content of insoluble limestone impurities, thus determining the amount of active clay and silica components required to produce binders of different degree of hydraulicity. Firing of the samples in various temperatures and time conditions, followed by X-ray diffraction analysis and slaking rate tests of the produced binders, is essential to insure the beneficiation of their behavior. Beneficiation is defined as the implementation of the best available techniques to insure the production of an economically usable final product which combines both the hydraulicity of the silicates, aluminates and ferrites, as well as the reactivity of the calcium oxide amounts that are present.

Nano- and Macro-wear of Bio-carbo-nitrided AISI 8620 Steel Surfaces

NASA Astrophysics Data System (ADS)

Arthur, Emmanuel Kwesi; Ampaw, Edward; Zebaze Kana, M. G.; Adetunji, A. R.; Olusunle, S. O. O.; Adewoye, O. O.; Soboyejo, W. O.

2015-12-01

This paper presents the results of an experimental study of nano- and macro-scale wear in a carbo-nitrided AISI 8620 steel. Carbo-nitriding is carried out using a novel method that involves the use of dried, cyanide-containing cassava leaves, as sources of carbon and nitrogen. These are used in a pack cementation that is used to diffuse carbon and nitrogen into case layers at intermediate temperatures [673.15 K, 723.15 K, 773.15 K, and 823.15 K (400 °C, 450 °C, 500 °C, and 550 °C)]. Nano- and macro-scale wear properties are studied in the case-hardened surfaces, using a combination of nano-scratch and pin-on-disk experiments. The measured wear volumes (at both nano- and macro-length scales) are shown to increase with decreasing pack cyaniding temperature. The nano- and macro-wear resistances are also shown to be enhanced by the in situ diffusion of carbon and nitrogen from cyanide-containing bio-processed waste. The underlying wear mechanisms are also elucidated via atomic force microscopy and scanning electron microscopy observations of the wear tracks. The implications of the results are discussed for the design of hardened carbo-nitrided steel surfaces with improved wear resistance.

High temperature oxidation in boiler environment of chromized steel

NASA Astrophysics Data System (ADS)

Alia, F. F.; Kurniawan, T.; Asmara, Y. P.; Ani, M. H. B.; Nandiyanto, A. B. D.

2017-10-01

The demand for increasing efficiency has led to the development and construction of higher operating temperature power plant. This condition may lead to more severe thickness losses in boiler tubes due to excessive corrosion process. Hence, the research to improve the corrosion resistance of the current operated material is needed so that it can be applied for higher temperature application. In this research, the effect of chromizing process on the oxidation behaviour of T91 steel was investigated under steam condition. In order to deposit chromium, mixture of chromium (Cr) powder as master alloy, halide salt (NH4Cl) powder as activator and alumina (Al2O3) powder as inert filler were inserted into alumina retort together with the steel sample and heated inside furnace at 1050°C for ten hours under argon gas environment. Furthermore, for the oxidation process, steels were exposed at 700°C at different oxidation time (6h-24h) under steam condition. From FESEM/EDX analysis, it was found that oxidation rate of pack cemented steel was lower than the un-packed steel. These results show that Cr from chromizing process was able to become reservoir for the formation of Cr2O3 in high temperature steam oxidation, and its existence can be used for a longer oxidation time.

Palladium-Catalyzed Carbon-Fluorine and Carbon-Hydrogen Bond Alumination of Fluoroarenes and Heteroarenes.

PubMed

Chen, Wenyi; Hooper, Thomas N; Ng, Jamues; White, Andrew J P; Crimmin, Mark R

2017-10-02

Through serendipitous discovery, a palladium bis(phosphine) complex was identified as a catalyst for the selective transformation of sp 2 C-F and sp 2 C-H bonds of fluoroarenes and heteroarenes to sp 2 C-Al bonds (19 examples, 1 mol % Pd loading). The carbon-fluorine bond functionalization reaction is highly selective for the formation of organoaluminium products in preference to hydrodefluorination products (selectivity=4.4:1 to 27:1). Evidence is presented for a tandem catalytic process in which hydrodefluorination is followed by sp 2 C-H alumination. © 2017 Wiley-VCH Verlag GmbH & Co. KGaA, Weinheim.

Properties of lithium aluminate for application as an OSL dosimeter

NASA Astrophysics Data System (ADS)

Twardak, A.; Bilski, P.; Marczewska, B.; Lee, J. I.; Kim, J. L.; Gieszczyk, W.; Mrozik, A.; Sądel, M.; Wróbel, D.

2014-11-01

Several samples of undoped and carbon or copper doped lithium aluminate (LiAlO2) were prepared in an attempt to achieve a material, which can be applicable in optically stimulated luminescence (OSL) dosimetry. All investigated samples are highly sensitive to ionizing radiation and show good reproducibility. The undoped and copper doped samples exhibit sensitivity several times higher than that of Al2O3:C, while sensitivity of the carbon doped samples is lower. The studied samples exhibit significant fading, but dynamics of signal loss is different for differently doped samples, what indicates a possibility of improving this characteristic by optimizing dopant composition.

Thermal Properties of Double-Aluminized Kapton at Low Temperatures

NASA Technical Reports Server (NTRS)

Tuttle, J.; DiPirro, M.; Canavan, E.; Hait, T.

2007-01-01

Double-aluminized kapton (DAK) is commonly used in multi-layer insulation blankets in cryogenic systems. NASA plans to use individual DAK sheets in lightweight deployable shields for satellites carrying instruments. A set of these shields will reflect away thermal radiation from the sun, the earth, and the instrument's warm side and allow the instrument's cold side to radiate its own heat to deep space. In order to optimally design such a shield system, it is important to understand the thermal characteristics of DAK down to low temperatures. We describe experiments which measured the thermal conductivity and electrical resistivity down to 4 Kelvin and the emissivity down to 10 Kelvin.

High-T sub c thin films on low microwave loss alkaline-rare-earth-aluminate crystals

DOE Office of Scientific and Technical Information (OSTI.GOV)

Sobolewski, R.; Gierlowski, P.; Kula, W.

1991-03-01

This paper reports on the alkaline-rare-earth aluminates (K{sub 2}NiF{sub 4}-type perovskites) which are an excellent choice as the substrate material for the growth of high-T{sub c} thin films suitable for microwave and far-infrared applications. The CaNdAlO{sub 4}, and SrLaAlO{sub 4} single crystals have been grown by Czochralski pulling and fabricated into the form of (001) oriented wafers. The Y-Ba-Cu-O and Bi-Sr-Ca-Cu-O films deposited on these substrates by a single-target magnetron sputtering exhibited very good superconducting and structural properties.

Aluminization and mirror removal of the Magellan 6.5-meter telescope

NASA Astrophysics Data System (ADS)

Perez, Frank S.

1994-06-01

The Magellan Project 6.5-meter telescope is a collaboration of the Carnegie Institution of Washington and the University of Arizona. The telescope will be located on Cerro Manqui, at the Las Campanas Observatory, Chile. At the beginning of the Magellan Project several schemes were investigated for realuminizing the primary mirror. We have chosen to leave the primary mirror in its cell with the mirror support system intact. Two major advantages of leaving the mirror in its cell are that it does not have to be lifted or handled and the support system does not have to be removed or reinstalled for aluminization.

Acyl silicates and acyl aluminates as activated intermediates in peptide formation on clays

NASA Technical Reports Server (NTRS)

White, D. H.; Kennedy, R. M.; Macklin, J.

1984-01-01

Glycine reacts with heating on dried clays and other minerals to give peptides in much better yield than in the absence of mineral. This reaction was proposed to occur by way of an activated intermediate such as an acyl silicate or acyl aluminate analogous to acyl phosphates involved in several biochemical reactions including peptide bond synthesis. The proposed mechanism has been confirmed by trapping the intermediate, as well as by direct spectroscopic observation of a related intermediate. The reaction of amino acids on periodically dried mineral surfaces represents a widespead, geologically realistic setting for prebiotic peptide formation via in situ activation.

Maximum allowable exposure to different heat radiation levels in three types of heat protective clothing

PubMed Central

HEUS, Ronald; DENHARTOG, Emiel A.

2017-01-01

To determine safe working conditions in emergency situations at petro-chemical plants in the Netherlands a study was performed on three protective clothing combinations (operator’s, firefighter’s and aluminized). The clothing was evaluated at four different heat radiation levels (3.0, 4.6, 6.3 and 10.0 k∙W∙m−2) in standing and walking posture with a thermal manikin RadMan™. Time till pain threshold (43°C) is set as a cut-off criterion for regular activities. Operator’s clothing did not fulfil requirements to serve as protective clothing for necessary activities at heat radiation levels above 1.5 k∙W∙m−2 as was stated earlier by Den Hartog and Heus1). With firefighter’s clothing it was possible to work almost three min up to 4.6 k∙W∙m−2. At higher heat radiation levels firefighter’s clothing gave insufficient protection and aluminized clothing should be used. Maximum working times in aluminized clothing at 6.3 k∙W∙m−2 was about five min. At levels of 10.0 k∙W∙m−2 (emergency conditions) emergency responders should move immediately to lower heat radiation levels. PMID:28978903

A slow positron beam generator for lifetime studies

NASA Technical Reports Server (NTRS)

Singh, Jag J.; Eftekhari, Abe; St.clair, Terry L.

1989-01-01

A slow positron beam generator using well-annealed polycrystalline tungsten moderators and a Na-22 positron source was developed. A 250 micro c source, deposited on a 2.54 micron thick aluminized mylar, is sandwiched between two (2.54 cm x 2.54 cm x 0.0127 cm) tungsten pieces. Two (2.54 cm x 2.54 cm x t cm) test polymer films insulate the two tungsten moderator pieces from the aluminized mylar source holder (t=0.00127 to 0.0127). A potential difference of 10 to 100 volts--depending on the test polymer film thickness (t)--is applied between the tungsten pieces and the source foil. Thermalized positrons diffusing out of the moderator pieces are attracted to the source foil held at an appropriate potential below the moderator pieces. These positrons have to pass through the test polymer films before they can reach the source foil. The potential difference between the moderator pieces and the aluminized mylar is so adjusted as to force the positrons to stop in the test polymer films. Thus the new generator becomes an effective source of positrons for assaying thin polymer films for their molecular morphology.

The Quantified Characterization Method of the Micro-Macro Contacts of Three-Dimensional Granular Materials on the Basis of Graph Theory.

PubMed

Guan, Yanpeng; Wang, Enzhi; Liu, Xiaoli; Wang, Sijing; Luan, Hebing

2017-08-03

We have attempted a multiscale and quantified characterization method of the contact in three-dimensional granular material made of spherical particles, particularly in cemented granular material. Particle contact is defined as a type of surface contact with voids in its surroundings, rather than a point contact. Macro contact is a particle contact set satisfying the restrictive condition of a two-dimensional manifold with a boundary. On the basis of graph theory, two dual geometrical systems are abstracted from the granular pack. The face and the face set, which satisfies the two-dimensional manifold with a boundary in the solid cell system, are extracted to characterize the particle contact and the macro contact, respectively. This characterization method is utilized to improve the post-processing in DEM (Discrete Element Method) from a micro perspective to describe the macro effect of the cemented granular material made of spherical particles. Since the crack has the same shape as its corresponding contact, this method is adopted to characterize the crack and realize its visualization. The integral failure route of the sample can be determined by a graph theory algorithm. The contact force is assigned to the weight value of the face characterizing the particle contact. Since the force vectors can be added, the macro contact force can be solved by adding the weight of its corresponding faces.

Evaluation of the influence of mechanical activation on physical and chemical properties of municipal solid waste incineration sludge.

PubMed

Caprai, V; Florea, M V A; Brouwers, H J H

2018-06-15

Despite numerous studies concerning the application of by-products in the construction field, municipal solid waste incineration (MSWI) residues are not widely used as secondary building materials. In some European countries, washing treatment to the full bottom ash (BA) fraction (0-32 mm) is applied, isolating more contaminated particles, smaller than 0.063 mm. Therefore, a MWSI sludge is produced, having a high moisture content, and thus a limited presence of soluble species. In order to enhance its performance as building material, here, dry mechanical activation is applied on MSWI sludge. Thereafter, a reactivity comparison between reference BA and untreated and treated MSWI sludge is provided, evaluating their behaviour in the presence of cement and their pozzolanic activity. Moreover, the mechanical performances, as 25% substitution of Portland cement (PC) are assessed, based on the EN 450. Mechanical activation enhances MSWI sludge physically due to the improved particle morphology and packing. Chemically, the hydration degree of PC is enhanced by the MSWI sludge by ≈25%. The milling treatment proved to be beneficial to the residues performances in the presence of PC, providing 32% higher strength than untreated sample. Environmentally, the compliance with the unshaped material legislation is successfully verified, according to the Soil Quality Decree. Copyright © 2017 Elsevier Ltd. All rights reserved.

Thermal targets for satellite calibration

NASA Astrophysics Data System (ADS)

Villa-Aleman, Eliel; Garrett, Alfred J.; Kurzeja, Robert J.; O'Steen, Byron L.; Pendergast, Malcolm M.

2001-03-01

The Savannah River Technology Center (SRTC) is currently calibrating the Multispectral Thermal Imager (MTI) satellite sponsored by the Department of Energy. The MTI imager is a research and development project with 15 wavebands in the visible, near-infrared, short-wave infrared, mid-wave infrared and long-wave infrared spectral regions. A plethora of targets with known temperatures such as power plant heated lakes, volcano lava vents, desert playas and aluminized Mylar tarps are being used in the validation of the five thermal bands of the MTI satellite. SRTC efforts in the production of cold targets with aluminized Mylar tarps will be described. Visible and thermal imagery and wavelength dependent radiance measurements of the calibration targets will be presented.

A reference standard for bidirectional reflection distribution function and bidirectional transmission distribution function measurement

NASA Technical Reports Server (NTRS)

Witherow, William K. (Inventor)

1988-01-01

A Lambertian reference standard for uniformly scattering a beam of light is constructed of a plate having a planar surface with a layer of glue disposed on the surface. An evenly packed layer of monodisperse spheres is set in the layer, and when the standard is used for bi-directional (BRDF) measurements, the spheres are coated with a layer of highly relective substance, such as gold or silver. When the standard is used for bi-directional transmittance distribution function (BTDF) measurements, the spheres are of a transparent material and are provided with a roughened surface, as by acid etching. In this case, the layer of glue is an optical cement, and the plate is of glass, with the spheres, the layer, and the plate all possessing a similar refractive index.

Novel application of DEM to modelling comminution processes

NASA Astrophysics Data System (ADS)

Delaney, Gary W.; Cleary, Paul W.; Sinnott, Matt D.; Morrison, Rob D.

2010-06-01

Comminution processes in which grains are broken down into smaller and smaller sizes represent a critical component in many industries including mineral processing, cement production, food processing and pharmaceuticals. We present a novel DEM implementation capable of realistically modelling such comminution processes. This extends on a previous implementation of DEM particle breakage that utilized spherical particles. Our new extension uses super-quadric particles, where daughter fragments with realistic size and shape distributions are packed inside a bounding parent super-quadric. We demonstrate the flexibility of our approach in different particle breakage scenarios and examine the effect of the chosen minimum resolved particle size. This incorporation of the effect of particle shape in the breakage process allows for more realistic DEM simulations to be performed, that can provide additional fundamental insights into comminution processes and into the behaviour of individual pieces of industrial machinery.

Development of leachate test for delayed ettringite formation potential in cementitious materials

NASA Astrophysics Data System (ADS)

France-Mensah, Jojo

Delayed Ettringite Formation (DEF) has been known to be the cause of expansion and cracking at latter ages in concrete that has been heat cured at temperatures around 70 degree Celsius or above. Currently, the only method available for measuring DEF-related physical expansion in concrete can sometimes take over a year to yield relevant results. A leachate method was proposed as a means of taking advantage of the release and solubility of the adsorbed ions (e.g., calcium, sulfates and aluminates) and alkali ions (e.g., sodium and potassium) in the pore solution after heat curing of the cement paste matrix. These ions, known to contribute to DEF, were leached out of concrete into the leaching solution. The results of the leachate test were correlated to physical expansion data of similar samples from an earlier study. The aim of this research is to apply this knowledge to develop an accelerated leachate test method for identifying the potential for DEF in cementitious materials in a shorter time than the existing method. The objectives of this research are: (1) to identify the ion(s) through leaching that is/are the controlling factors in predicting the rate of expansion and overall expansion of mortar; (2) to identify the ion(s) that is/are responsible for the lag time or age of deleterious expansion through DEF; and (3) to investigate the effect of heat curing on the overall, rate of, and age (time) of expansion.

Synthesis of zinc aluminate with high surface area by microwave hydrothermal method applied in the transesterification of soybean oil (biodiesel)

DOE Office of Scientific and Technical Information (OSTI.GOV)

Quirino, M.R.; Oliveira, M.J.C.; Keyson, D.

Highlights: • ZnAl{sub 2}O{sub 4} spinel was synthesized by the microwave hydrothermal method in only 15 or 30 min. • The powders show high specific surface area. • ZAT{sub b}15 showed activity of 52.22% for the conversion of soybean oil into biodiesel. - Abstract: Zinc aluminate is a material with high thermal stability and high mechanical strength that, owing to these properties, is used as a catalyst or support. In this work, zinc aluminate spinel was synthesized by the microwave hydrothermal method in only 15 or 30 min at a low temperature (150 °C) without templates, using only Al(NO{sub 3}){submore » 3}·9H{sub 2}O, Zn(NO{sub 3}){sub 2}·6H{sub 2}O, and urea as precursors and applied in the transesterification of soybean oil. X-ray diffraction analysis showed that ZnAl{sub 2}O{sub 4} had a cubic structure without secondary phases. The nitrogen adsorption measurements (BET) revealed a high surface area (266.57 m{sup 2} g{sup −1}) for the nanopowder synthesized in 15 min. This powder showed activity of 52.22% for the catalytic conversion of soybean oil into biodiesel by transesterification.« less

Studies on densification, mechanical, micro-structural and structure–properties relationship of magnesium aluminate spinel refractory aggregates prepared from Indian magnesite

DOE Office of Scientific and Technical Information (OSTI.GOV)

Ghosh, Chandrima; Ghosh, Arup; Haldar, Manas Kamal, E-mail: manashaldar@cgcri.res.in

The present work intends to study the development of magnesium aluminate spinel aggregates from Indian magnesite in a single firing stage. The raw magnesite has been evaluated in terms of chemical analysis, differential thermal analysis, thermogravimetric analysis, infrared spectroscopy, and X-ray diffraction. The experimental batch containing Indian magnesite and calcined alumina has been sintered in the temperature range of 1550 °C–1700 °C. The sintered material has been characterized in terms of physico-chemical properties like bulk density, apparent porosity, true density, relative density and thermo-mechanical/mechanical properties like hot modulus of rupture, thermal shock resistance, cold modulus of rupture and structural propertiesmore » by X-ray diffraction in terms of phase identification and evaluation of crystal structure parameters of corresponding phases by Rietveld analysis. The microstructures developed at different temperatures have been analyzed by field emission scanning electron microscope study and compositional analysis of the developed phase has been carried out by energy dispersive X-ray study. - Highlights: • The studies have been done to characterize the developed magnesium aluminate spinel. • The studies reveal correlation between refractory behavior of spinel and developed microstructures. • The studies show the values of lattice parameters of developed phases.« less

Formation Mechanism of CaS-Bearing Inclusions and the Rolling Deformation in Al-Killed, Low-Alloy Steel with Ca Treatment

NASA Astrophysics Data System (ADS)

Xu, Guang; Jiang, Zhouhua; Li, Yang

2016-08-01

The existing form of CaS inclusion in Ca-treated, Al-killed steel during secondary refining process was investigated with scanning electron microscopy and an energy-dispersive spectrometer (EDS). The results of 12 heats industrial tests showed that CaS has two kinds of precipitation forms. One form takes place by the direct reaction of Ca and S, and the other takes place by the reaction of CaO in calcium aluminates with dissolved Al and S in liquid steel. Thermodynamic research for different precipitation modes of CaS under different temperature was carried out. In particular, CaO-Al2O3-CaS isothermal section diagrams and component activities of calcium aluminates were calculated by the thermodynamic software FactSage. By thermodynamic calculation, a precipitation-area diagram of oxide-sulfide duplex inclusion was established by fixing the sulfur content. The quantity of CaS, which was precipitated in a reaction between [Al], [S] and (CaO), can be calculated and predicted based on the precipitation-area diagram of oxide-sulfide duplex inclusion. Electron probe microanalysis and EDS were used for observing rolling deformation of different types of CaS-bearing inclusions during the rolling process. Low modification of calcium aluminates wrapped by CaS has different degrees of harm to steel in the rolling process. A thick CaS layer can prevent some fragile calcium aluminates from being crushed during the rolling process. Some oxide-sulfide duplex inclusion contains little CaS performed better deformation during the rolling process, but when CaS in oxide-sulfide duplex inclusion becomes more, it will cause the whole inclusion to lose plastic yielding ability. The plastic deformation region of CaS-bearing inclusion in a CaO-Al2O3-CaS isothermal section diagram is confirmed.

Thin-window high-efficiency position sensitive proportional counter for the vacuum flat crystal spectrometers on the Lawrence Livermore National Laboratory electron beam ion trap (abstract)

DOE Office of Scientific and Technical Information (OSTI.GOV)

Brown, G. V.; Beiersdorfer, P.; Goddard, R.

2001-01-01

We have mounted 1 {mu}m thick aluminized polyimide windows onto the position sensitive proportional counters employed by the wide-band flat crystal spectrometers at the Lawrence Livermore National Laboratory electron beam ion trap experiment. The aluminized polyimide, supported by thin wires across the short axis of the window, is used to isolate the detection chamber of the proportional counters, which operate at a pressure of 760 Torr, from the vacuum chamber of the spectrometer. The windows are modified versions of those developed for the proportional counters which were used during ground calibration of the Chandra X-ray Observatory. The transmission properties ofmore » these windows are, therefore, well known. The increased transmission efficiency of the polyimide windows relative to the 4 {mu}m thick polypropylene window material previously employed by our proportional counters has extended the useful range of the spectrometer from roughly 20 to 30 Aa at energies below the carbon edge, as well as increasing detection efficiency at wavelengths beyond the carbon edge. Using an octadecyl hydrogen maleate crystal with 2d=63.5Aa, we demonstrate the increased wavelength coverage by measuring the resonance, intercombination, and forbidden lines in helium-like NVII in two different density regimes. The thin polyimide windows have also increased the efficiency of the spectrometers entire wavelength range. To demonstrate the increased efficiency we compare the FeXVII spectrum in the 15--17 Aa band measured with the 1 {mu}m aluminized polyimide windows to the 4 {mu}m aluminized polypropylene windows. The comparison shows an average increase in efficiency of {approx}40%. The polyimide windows have a significantly lower leak rate than the polypropylene windows making it possible to achieve approximately an order of magnitude lower pressure in the spectrometer vacuum chamber which reduces the gas load on the trap region.« less

Diagenetic pathways in deposits of cool- and cold-water carbonate factories

NASA Astrophysics Data System (ADS)

Frank, T. D.; James, N. P.

2017-12-01

This investigation integrates sedimentological, petrographic, and geochemical observations from modern and ancient heterozoan carbonate deposits that formed at temperate to polar latitudes with the aim of evaluating diagenetic pathways characteristic of these systems. These factories operate under conditions distinct from those of photozoan counterparts. Lower temperatures, higher trophic resources, lower carbonate saturation states, and strong seasonality govern not only the nature of carbonate communities, but also how deposits translate into the rock record. In these settings, carbonate production is entirely biogenic, assemblages are of low diversity, and there are no significant calcareous phototrophs. Aragonitic taxa may be present in living communities, but allochems rapidly disappear via dissolution. Carbonate producers are not capable of building rigid frameworks, so their deposits accumulate as sands and gravels and are prone to winnowing and reworking. Low production rates lead to long seafloor residence times (1000s of years) for grains, which undergo physical reworking, dissolution, and repeated infestation by endolithic borers. Microborings remain empty, increasing grain susceptibility to disintegration. Intergranular cementation on the seafloor is rare and restricted to hardgrounds. Periods of subaerial exposure do not leave traces of meteoric alteration. Results show that the deposits of heterozoan carbonate factories tend enter the geologic record as taphonomic remnants, namely reworked, unconsolidated sands and gravels with low diagenetic potential. During burial, physical and chemical compaction produce limestones with tightly packed, grain-supported fabrics, often with grains in sutured contact. Significant cementation is associated with the deep burial realm. Results reveal a dramatically different diagenetic pathway than is typical for deposits of tropical photozoan factories, in which significant recrystallization and lithification occur on the seafloor and upon subaerial exposure. Interpretations of ancient deposits should take into account the potential for taphonomic loss of aragonitic allochems, modification of depositional textures via reworking and compaction, and grain alteration and cementation focused in the burial environment.

Effects of loading concentration, blood and synovial fluid on antibiotic release and anti-biofilm activity of bone cement beads.

PubMed

Dusane, Devendra H; Diamond, Scott M; Knecht, Cory S; Farrar, Nicholas R; Peters, Casey W; Howlin, Robert P; Swearingen, Matthew C; Calhoun, Jason H; Plaut, Roger D; Nocera, Tanya M; Granger, Jeffrey F; Stoodley, Paul

2017-02-28

Antibiotic loaded cement beads are commonly used for the treatment of biofilm related orthopaedic periprosthetic infections; however the effects of antibiotic loading and exposure of beads to body fluids on release kinetics are unclear. The purpose of this study was to determine the effects of (i) antibiotic loading density (ii) loading amount (iii) material type and (iv) exposure to body fluids (blood or synovial fluid) on release kinetics and efficacy of antibiotics against planktonic and lawn biofilm bacteria. Short-term release into an agar gel was evaluated using a fluorescent tracer (fluorescein) incorporated in the carrier materials calcium sulfate (CaSO 4 ) and poly methyl methacrylate (PMMA). Different fluorescein concentrations in CaSO 4 beads were evaluated. Mechanical properties of fluorescein-incorporated beads were analyzed. Efficacy of the antibiotics vancomycin (VAN) or tobramycin (TOB) alone and in combination was evaluated against lawn biofilms of bioluminescent strains of Staphylococcus aureus and Pseudomonas aeruginosa. Zones of inhibition of cultures (ZOI) were measured visually and using an in-vivo imaging system (IVIS). The influence of body fluids on release was assessed using CaSO 4 beads that contained fluorescein or antibiotics and were pre-coated with human blood or synovial fluid. The spread from the beads followed a square root of time relationship in all cases. The loading concentration had no influence on short-term fluorescein release and pre-coating of beads with body fluids did not affect short-term release or antibacterial activity. Compared to PMMA, CaSO 4 had a more rapid short term rate of elution and activity against planktonic and lawn biofilms. This study highlights the importance of considering antibiotic loading and packing density when investigating the clinical application of bone cements for infection management. Copyright © 2017 The Authors. Published by Elsevier B.V. All rights reserved.

Mechanical and Permeability Characteristics of Latex-Modified Pre-Packed Pavement Repair Concrete as a Function of the Rapid-Set Binder Content

PubMed Central

Han, Jae-Woong; Jeon, Ji-Hong; Park, Chan-Gi

2015-01-01

We evaluated the strength and durability characteristics of latex-polymer-modified, pre-packed pavement repair concrete (LMPPRC) with a rapid-set binder. The rapid-set binder was a mixture of rapid-set cement and silica sand, where the fluidity was controlled using a latex polymer. The resulting mix exhibited a compressive strength of ≥21 MPa and a flexural strength of ≥3.5 MPa after 4 h of curing (i.e., the traffic opening term for emergency repairs of pavement). The ratio of latex polymer to rapid-set binder material was varied through 0.40, 0.33, 0.29, and 0.25. Mechanical characterization revealed that the mechanical performance, permeability, and impact resistance increased as the ratio of latex polymer to rapid-set binder decreased. The mixture exhibited a compressive strength of ≥21 MPa after 4 h when the ratio of latex polymer to rapid-set binder material was ≤0.29. The mixture exhibited a flexural strength of ≥3.5 MPa after 4 h when the ratio of latex polymer to rapid-set binder material was ≤0.33. The permeability resistance to chloride ions satisfied 2000 C after 7 days of curing for all ratios. The ratio of latex polymer to rapid-set binder material that satisfied all conditions for emergency pavement repair was ≤0.29. PMID:28793596

Mechanical and Permeability Characteristics of Latex-Modified Pre-Packed Pavement Repair Concrete as a Function of the Rapid-Set Binder Content.

PubMed

Han, Jae-Woong; Jeon, Ji-Hong; Park, Chan-Gi

2015-10-01

We evaluated the strength and durability characteristics of latex-polymer-modified, pre-packed pavement repair concrete (LMPPRC) with a rapid-set binder. The rapid-set binder was a mixture of rapid-set cement and silica sand, where the fluidity was controlled using a latex polymer. The resulting mix exhibited a compressive strength of ¥21 MPa and a flexural strength of ¥3.5 MPa after 4 h of curing (i.e., the traffic opening term for emergency repairs of pavement). The ratio of latex polymer to rapid-set binder material was varied through 0.40, 0.33, 0.29, and 0.25. Mechanical characterization revealed that the mechanical performance, permeability, and impact resistance increased as the ratio of latex polymer to rapid-set binder decreased. The mixture exhibited a compressive strength of ¥21 MPa after 4 h when the ratio of latex polymer to rapid-set binder material was ¤0.29. The mixture exhibited a flexural strength of ¥3.5 MPa after 4 h when the ratio of latex polymer to rapid-set binder material was ¤0.33. The permeability resistance to chloride ions satisfied 2000 C after 7 days of curing for all ratios. The ratio of latex polymer to rapid-set binder material that satisfied all conditions for emergency pavement repair was ¤0.29.

Ethylene glycol contamination effects on first surface aluminized mirrors

NASA Astrophysics Data System (ADS)

Dunlop, Patrick; Probst, Ronald G.; Evatt, Matthew; Reddell, Larry; Sprayberry, David

2016-07-01

The Dark Energy Spectroscopic Instrument (DESI) is under construction for installation on the Mayall 4 Meter telescope. The use of a liquid cooling system is proposed to maintain the DESI prime focus assembly temperature within ±1°C of ambient. Due to concerns of fluid deposition onto optical surfaces from possible leaks, systematic tests were performed of the effects on first surface aluminized mirrors of ethylene glycol and two other candidate coolants. Objective measurement of scattering and reflectivity was an important supplement to visual inspection. Rapid cleanup of a coolant spill followed by a hand wash of the mirror limited surface degradation to the equivalent of a few months of general environmental exposure. Prolonged exposure to corrosive coolants dissolved the aluminum, necesitating mirror recoating.

Method of winning aluminum metal from aluminous ore

DOEpatents

Loutfy, Raouf O.; Keller, Rudolf; Yao, Neng-Ping

1981-01-01

Aluminous ore such as bauxite containing alumina is blended with coke or other suitable form of carbon and reacted with sulfur gas at an elevated temperature. For handling, the ore and coke can be extruded into conveniently sized pellets. The reaction with sulfur gas produces molten aluminum sulfide which is separated from residual solid reactants and impurities. The aluminum sulfide is further increased in temperature to cause its decomposition or sublimation, yielding aluminum subsulfide liquid (AlS) and sulfur gas that is recycled. The aluminum monosulfide is then cooled to below its disproportionation temperature to again form molten aluminum sulfide and aluminum metal. A liquid-liquid or liquid-solid separation, depending on the separation temperature, provides product aluminum and aluminum sulfide for recycle to the disproportionation step.

Basic performance of a multilayer insulation system containing 20 to 160 layers. [thermal effectiveness of aluminized Mylar-silk net system

NASA Technical Reports Server (NTRS)

Stochl, R. J.

1974-01-01

An experimental investigation was conducted to determine the thermal effectiveness of an aluminized Mylar-silk net insulation system containing up to 160 layers. The experimentally measured heat flux was compared with results predicted by using (1) a previously developed semi-empirical equation and (2) an effective-thermal-conductivity value. All tests were conducted at a nominal hot-boundary temperature of 294 K (530 R) with liquid hydrogen as the heat sink. The experimental results show that the insulation performed as expected and that both the semi-empirical equation and effective thermal conductivity of a small number of layers were adequate in predicting the thermal performance of a large number of layers of insulation.

Laser-Induced Fluorescence Photogrammetry for Dynamic Characterization of Transparent and Aluminized Membrane Structures

NASA Technical Reports Server (NTRS)

Dorrington, Adrian A.; Jones, Thomas W.; Danehy, Paul M.; Pappa, Richard S.

2003-01-01

Photogrammetry has proven to be a valuable tool for static and dynamic profiling of membrane based inflatable and ultra-lightweight space structures. However, the traditional photogrammetric targeting techniques used for solid structures, such as attached retro-reflective targets and white-light dot projection, have some disadvantages and are not ideally suited for measuring highly transparent or reflective membrane structures. In this paper, we describe a new laser-induced fluorescence based target generation technique that is more suitable for these types of structures. We also present several examples of non-contact non-invasive photogrammetric measurements of laser-dye doped polymers, including the dynamic measurement and modal analysis of a 1m-by-1m aluminized solar sail style membrane.

Performance of Diffusion Aluminide Coatings Applied on Alloy CF8C-Plus at 800oC

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kumar, Deepak; Dryepondt, Sebastien N; Zhang, Ying

2012-01-01

High performance cast stainless steel, CF8C-Plus, is a low cost alloy with prospective applications ranging from covers and casings of small and medium size gas turbines to turbocharger housing and manifolds in internal combustion engines. Diffusion aluminide coatings were applied on this alloy as a potential strategy for improved oxidation resistance, particularly in wet air and steam. In this paper the performance of the aluminide coatings evaluated by cyclic oxidation experiments in air containing 10 vol.% H2O at 800 C and conventional tension-compression low-cycle-fatigue tests in air at 800 C with a strain range of 0.5% is presented. The resultsmore » show that specimens coated by a chemical vapor deposition process provide better oxidation resistance than those coated by an Al-slurry coating process. The application of a coating by pack cementation reduced the fatigue life by 15%.« less

Strength Development of High-Strength Ductile Concrete Incorporating Metakaolin and PVA Fibers

PubMed Central

Nuruddin, Muhammad Fadhil; Shafiq, Nasir

2014-01-01

The mechanical properties of high-strength ductile concrete (HSDC) have been investigated using Metakaolin (MK) as the cement replacing material and PVA fibers. Total twenty-seven (27) mixes of concrete have been examined with varying content of MK and PVA fibers. It has been found that the coarser type PVA fibers provide strengths competitive to control or higher than control. Concrete with coarser type PVA fibers has also refined microstructure, but the microstructure has been undergone with the increase in aspect ratio of fibers. The microstructure of concrete with MK has also more refined and packing of material is much better with MK. PVA fibers not only give higher stiffness but also showed the deflection hardening response. Toughness Index of HSDC reflects the improvement in flexural toughness over the plain concrete and the maximum toughness indices have been observed with 10% MK and 2% volume fraction of PVA fibers. PMID:24707202

Strength development of high-strength ductile concrete incorporating Metakaolin and PVA fibers.

PubMed

Nuruddin, Muhammad Fadhil; Khan, Sadaqat Ullah; Shafiq, Nasir; Ayub, Tehmina

2014-01-01

The mechanical properties of high-strength ductile concrete (HSDC) have been investigated using Metakaolin (MK) as the cement replacing material and PVA fibers. Total twenty-seven (27) mixes of concrete have been examined with varying content of MK and PVA fibers. It has been found that the coarser type PVA fibers provide strengths competitive to control or higher than control. Concrete with coarser type PVA fibers has also refined microstructure, but the microstructure has been undergone with the increase in aspect ratio of fibers. The microstructure of concrete with MK has also more refined and packing of material is much better with MK. PVA fibers not only give higher stiffness but also showed the deflection hardening response. Toughness Index of HSDC reflects the improvement in flexural toughness over the plain concrete and the maximum toughness indices have been observed with 10% MK and 2% volume fraction of PVA fibers.

Treatment of giant cell tumor of bone: Current concepts.

PubMed

Puri, Ajay; Agarwal, Manish

2007-04-01

Giant cell tumor (GCT) of bone though one of the commonest bone tumors encountered by an orthopedic surgeon continues to intrigue treating surgeons. Usually benign, they are locally aggressive and may occasionally undergo malignant transformation. The surgeon needs to strike a balance during treatment between reducing the incidence of local recurrence while preserving maximal function.Differing opinions pertaining to the use of adjuvants for extension of curettage, the relative role of bone graft or cement to pack the defect and the management of recurrent lesions are some of the issues that offer topics for eternal debate.Current literature suggests that intralesional curettage strikes the best balance between controlling disease and preserving optimum function in the majority of the cases though there may be occasions where the extent of the disease mandates resection to ensure adequate disease clearance.An accompanying treatment algorithm helps outline the management strategy in GCT.

Differences in the Nature of Active Sites for Methane Dry Reforming and Methane Steam Reforming over Nickel Aluminate Catalysts

DOE Office of Scientific and Technical Information (OSTI.GOV)

Rogers, Jessica L.; Mangarella, Michael C.; D’Amico, Andrew D.

In this paper, the Pechini synthesis was used to prepare nickel aluminate catalysts with the compositions NiAl 4O 7, NiAl 2O 4, and Ni 2Al 2O 5. The samples have been characterized by N 2 physisorption, temperature-programmed reduction (TPR), temperature-programmed oxidation (TPO), X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), transmission electron microscopy (TEM), and X-ray absorption spectroscopy (XAS). Characterization results indicate unique structural properties and excellent regeneration potential of nickel aluminates. Prepared samples were tested when unreduced and reduced prior to reaction for methane dry reforming and methane steam reforming reactivity. NiAl 2O 4 in the reduced and unreduced statemore » as well as NiAl 4O 7 in the reduced state are active and stable for methane dry reforming due to the presence of 4-fold coordinated oxidized nickel. The limited amount of metallic nickel in these samples minimizes carbon deposition. Finally, on the other hand, the presence of metallic nickel is required for methane steam reforming. Ni 2Al 2O 5 in the reduced and unreduced states and NiAl 2O 4 in the reduced state are found to be active for methane steam reforming due to the presence of sufficiently small nickel nanoparticles that catalyze the reaction without accumulating carbonaceous deposits.« less

Spin transition of ferric iron in the calcium-ferrite type aluminous phase: Fe 3+ Spin Transition in the CF Phase

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wu, Ye; Qin, Fei; Wu, Xiang

2017-08-01

We investigated Fe-free and Fe-bearing CF phases using nuclear forward scattering and X-ray diffraction coupled with diamond anvil cells up to 80 GPa at room temperature. Octahedral Fe3+ ions in the Fe-bearing CF phase undergo a high-spin to low-spin transition at 25–35 GPa, accompanied by a volume reduction of ~2.0% and a softening of bulk sound velocity up to 17.6%. Based on the results of this study and our previous studies, both the NAL and CF phases, which account for 10–30 vol % of subducted MORB in the lower mantle, are predicted to undergo a spin transition of octahedral Fe3+more » at lower mantle pressures. Spin transitions in these two aluminous phases result in an increase of density of 0.24% and a pronounced softening of bulk sound velocity up to 2.3% for subducted MORB at 25–60 GPa and 300 K. The anomalous elasticity region expands and moves to 30–75 GPa at 1200 K and the maximum of the VΦ reduction decreases to ~1.8%. This anomalous elastic behavior of Fe-bearing aluminous phases across spin transition zones may be relevant in understanding the observed seismic signatures in the lower mantle.« less

The Use of Rietveld Technique to Study Phase Composition and Developments of Calcium Aluminate

NASA Astrophysics Data System (ADS)

Ridwan, I.; Asmi, D.

2008-03-01

The phase composition and development of calcium aluminates (CA, CA2, and CA6) processed by in-situ reaction sintering of Al2O3 and CaCO3 have been studied by Rietveld refinement technique. The formation of calcium aluminates is temperature-dependent. X-ray diffraction result revealed that the CA, CA2, and CA6 phases starts to develop at approximately 1000 °C, 1100 °C and 1375 °C, respectively. The relative phase compositions obtained from x-ray diffraction patterns for the α-Al2O3 phase decreased markedly with increasing temperature, i.e. from 86.0(1.1) wt% at 1000 °C to 34.7(0.4) wt% at 1400 °C. The wt% of CA decreased from 10.9(0.3)-1.9(0.2) wt% at 1100-1200 °C but disappeared at 1300 °C. The wt% of CA2 reached 36.0(0.7) wt% at 1300 °C and decreased to 18.5 (0.5) wt% at 1400 °C. The wt% CA6 increased markedly from 1375 to 1400 °C, i.e. 12.80(0.6)-47.3(0.9) wt%. The goodness of fit values is relatively low and the fluctuation in the difference plots shows a reasonable fit between the observed and the calculated plot.

Differences in the Nature of Active Sites for Methane Dry Reforming and Methane Steam Reforming over Nickel Aluminate Catalysts

DOE PAGES

Rogers, Jessica L.; Mangarella, Michael C.; D’Amico, Andrew D.; ...

2016-07-20

In this paper, the Pechini synthesis was used to prepare nickel aluminate catalysts with the compositions NiAl 4O 7, NiAl 2O 4, and Ni 2Al 2O 5. The samples have been characterized by N 2 physisorption, temperature-programmed reduction (TPR), temperature-programmed oxidation (TPO), X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), transmission electron microscopy (TEM), and X-ray absorption spectroscopy (XAS). Characterization results indicate unique structural properties and excellent regeneration potential of nickel aluminates. Prepared samples were tested when unreduced and reduced prior to reaction for methane dry reforming and methane steam reforming reactivity. NiAl 2O 4 in the reduced and unreduced statemore » as well as NiAl 4O 7 in the reduced state are active and stable for methane dry reforming due to the presence of 4-fold coordinated oxidized nickel. The limited amount of metallic nickel in these samples minimizes carbon deposition. Finally, on the other hand, the presence of metallic nickel is required for methane steam reforming. Ni 2Al 2O 5 in the reduced and unreduced states and NiAl 2O 4 in the reduced state are found to be active for methane steam reforming due to the presence of sufficiently small nickel nanoparticles that catalyze the reaction without accumulating carbonaceous deposits.« less

Fabrication of Nanocomposites of SnO2 and MgAl2O4 for Gas Sensing Applications

NASA Astrophysics Data System (ADS)

Nithyavathy, N.; Arunmetha, S.; Vinoth, M.; Sriram, G.; Rajendran, V.

2016-04-01

Simple solid-state and sol-gel routes have been used to synthesize nanocomposites of tin oxide and magnesium aluminate at calcination temperature of 900 K for gas sensing applications. The effects of the surface structure of magnesium aluminate on the gas response for different concentrations of tin oxide addition were investigated for potential use in gas sensors. (SnO2) x doped in small amounts x into magnesium aluminate resulted in three nanocomposite samples MAS0.25, MAS0.50, and MAS0.75 for x = 0.25, 0.50, and 0.75, respectively, plus MgAl2O4 (MA) for x = 0. The response to different pressures of gases such as oxygen (O2), carbon monoxide (CO), and ethanol (C2H5OH) was quantitatively analyzed for all samples at different operating temperatures. The temperature was varied linearly by increasing the supply to a heating pad mounted below the sensor sample, regardless of the gas pressure inside the chamber. All the sample materials showed good response at different gas pressures (1 bar to 2 bar) and operating temperatures (300 K to 600 K). It was noted that the composite samples showed enhanced and fast response to gases, at both lower and higher operating temperatures, with detection of even the smallest change in gas pressure.

A two-phase model for aluminized explosives on the ballistic and brisance performance

NASA Astrophysics Data System (ADS)

Kim, Wuhyun; Gwak, Min-cheol; Lee, Young-hun; Yoh, Jack J.

2018-02-01

The performance of aluminized high explosives is considered by varying the aluminum (Al) mass fraction in a heterogeneous mixture model. Since the time scales of the characteristic induction and combustion of high explosives and Al particles differ, the process of energy release behind the leading detonation wave front occurs over an extended period of time. For simulating the performance of aluminized explosives with varying Al mass fraction, HMX (1,3,5,7-tetrahexmine-1,3,5,7-tetrazocane) is considered as a base explosive when formulating the multiphase conservation laws of mass, momentum, and energy exchanges between the HMX product gases and Al particles. In the current study, a two-phase model is utilized in order to determine the effects of the Al mass fraction in a condensed phase explosive. First, two types of confined rate stick tests are considered to investigate the detonation velocity and the acceleration ability, which refers to the radial expansion velocity of the confinement shell. The simulation results of the confined rate stick test are compared with the experimental data for the Al mass fraction range of 0%-25%, and the optimal Al mass fraction is provided, which is consistent with the experimental observations. Additionally, a series of plate dent test simulations are conducted, the results of which show the same tendency as those of the experimental tests with varying Al mass fractions.

Petrology of Mississippian carbonate eolianites and associated facies: Ste. Genevieve Limestone of Indiana

DOE Office of Scientific and Technical Information (OSTI.GOV)

Dodd, J.R.; Brown, T.W.; Harris, C.D.

1990-05-01

Descriptions of carbonate eolianites of pre-Pleistocene age are rare. Based largely on sedimentary structures and facies associations, Hunter has recently identified eolian deposits in the middle Mississippian Ste. Genevieve Limestone near Corydon, Indiana. Eolianite grainstones contain a diverse assemblage of allochems, including a variety of skeletal grains, ooids (some broken and abraded), peloids, intraclasts, and abundant quartz silt. Carbonate grains, which rarely exceed 0.5 mm are usually more spherical than grains from associated marine unit. Eolian units contain cross-laminations that sometimes coarsen upward. No evidence for vadose cement was found in the eolianite units; the extensive solution packing suggest thatmore » cementation did not occur until burial to considerable depth. Marine grainstones, which probably formed on shallow shoals or an open platform, are common in the section. They contain a diverse assemblage of skeletal grain types as well as ooids, peloids, and intraclasts; however, one grain type (such as ooids) frequently dominates an individual unit. Detrital quartz grains are rare. Rounding of grains is usually good, but sphericity of skeletal grains which were not originally spherical is low. Fine laminations are uncommon, and no systematic grading is found on a thin-section scale. Grains and fossils in excess of 10 mm are common in the marine unit. Carbonate mud-rich rocks that probably formed in a shallow lagoonal setting also occur in the Ste. Genevieve section as do poorly developed exposure surfaces with pedogenic features.« less

On Characterizing Particle Shape

NASA Technical Reports Server (NTRS)

Ennis, Bryan J.; Rickman, Douglas; Rollins, A. Brent; Ennis, Brandon

2014-01-01

It is well known that particle shape affects flow characteristics of granular materials, as well as a variety of other solids processing issues such as compaction, rheology, filtration and other two-phase flow problems. The impact of shape crosses many diverse and commercially important applications, including pharmaceuticals, civil engineering, metallurgy, health, and food processing. Two applications studied here include the dry solids flow of lunar simulants (e.g. JSC-1, NU-LHT-2M, OB-1), and the flow properties of wet concrete, including final compressive strength. A multi-dimensional generalized, engineering method to quantitatively characterize particle shapes has been developed, applicable to both single particle orientation and multi-particle assemblies. The two-dimension, three dimension inversion problem is also treated, and the application of these methods to DEM model particles will be discussed. In the case of lunar simulants, flow properties of six lunar simulants have been measured, and the impact of particle shape on flowability - as characterized by the shape method developed here -- is discussed, especially in the context of three simulants of similar size range. In the context of concrete processing, concrete construction is a major contributor to greenhouse gas production, of which the major contributor is cement binding loading. Any optimization in concrete rheology and packing that can reduce cement loading and improve strength loading can also reduce currently required construction safety factors. The characterization approach here is also demonstrated for the impact of rock aggregate shape on concrete slump rheology and dry compressive strength.

Photo-Luminescent Targets in Space

NASA Technical Reports Server (NTRS)

Maida, James; Kolomenski, Andrei

2017-01-01

Photo-luminescent ("glow in the dark") products have seen a dramatic increase in performance is the last 15 years with the use of a strontium aluminate formulation. Because of this, ISS uses photo-luminescent markers for interior emergency egress guidance. The marker is COTS material composed of strontium aluminate doped with europium, imbedded in PVC and achieves a light emission performance rated at 600/90 (600 mcd at 10 minutes and 90 mcd at 1 hour, 2 mcd is minimum required for human visibility). The ICA goal is to determine this material's effectiveness for use externally on ISS and/or on visiting vehicles, when packaged in Lexan for UV protection. A thermal test was conducted by EC to characterize the luminance emission profile of the material at extreme cold and hot temperatures, such as experienced on ISS.

Method of winning aluminum metal from aluminous ore

DOEpatents

Loutfy, R.O.; Keller, R.; Yao, N.P.

Aluminous ore such as bauxite containing alumina is blended with coke or other suitable form of carbon and reacted with sulfur gas at an elevated temperature. For handling, the ore and coke can be extruded into conveniently sized pellets. The reaction with sulfur gas produces molten aluminum sulfide which is separated from residual solid reactants and impurities. The aluminum sulfide is further increased in temperature to cause its decomposition or sublimation, yielding aluminum subsulfide liquid (A1S) and sulfur gas that is recycled. The aluminum monosulfide is then cooled to below its disproportionation temperature to again form molten aluminum sulfide and aluminum metal. A liquid-liquid or liquid-solid separation, depending on the separation temperature, provides product aluminum and aluminum sulfide for recycle to the disproportionation step.

Correlation between thermoluminescence glow curve and emission spectra of gamma ray irradiated LaAlO3

NASA Astrophysics Data System (ADS)

Shivaramu, N. J.; Lakshminarasappa, B. N.; Nagabhushana, K. R.; Coetsee, E.; Swart, H. C.

2018-04-01

Lanthanum aluminate (LaAlO3) is synthesized by solution combustion method and the resultant powder is annealed at 900°C for 2 hours. X-ray diffraction (XRD) pattern confirms the rhombohedral structure LaAlO3 with space group R3 ¯c. γ-irradiated nanocrystalline lanthanum aluminate gives two prominent TL glow with peaks at 399 and 639 K and weak one at 547 K. TL intensity at 399 K increases up to 9.0 kGy and then decreases with increasing γ-dose. TL emission shows at 650 nm and 736 nm is attributed to the charge transfer from oxygen to metal ions. The glow curves are analyzed and the trap parameters are calculated by glow curve deconvoluted technique.

Water solubility in aluminous orthopyroxene and the origin of Earth's asthenosphere.

PubMed

Mierdel, Katrin; Keppler, Hans; Smyth, Joseph R; Langenhorst, Falko

2007-01-19

Plate tectonics is based on the concept of rigid lithosphere plates sliding on a mechanically weak asthenosphere. Many models assume that the weakness of the asthenosphere is related to the presence of small amounts of hydrous melts. However, the mechanism that may cause melting in the asthenosphere is not well understood. We show that the asthenosphere coincides with a zone where the water solubility in mantle minerals has a pronounced minimum. The minimum is due to a sharp decrease of water solubility in aluminous orthopyroxene with depth, whereas the water solubility in olivine continuously increases with pressure. Melting in the asthenosphere may therefore be related not to volatile enrichment but to a minimum in water solubility, which causes excess water to form a hydrous silicate melt.

Preparation and Characterization of Fine-Particle NTO and Its Formulation with Al Nanopowders

NASA Astrophysics Data System (ADS)

Lee, K.-Y.; Kennedy, J. E.; Asay, B. W.; Son, S. F.; Martin, E. S.

2004-07-01

We have initiated study of the effect of nano-aluminum on the detonation performance of NTO. A novel method for the preparation of both fine-particle NTO (UF-NTO) and its formulation with Al nanopowder has been developed. Results from small-scale sensitivity tests on both the UF-NTO and aluminized NTO composite indicated that they are insensitive to impact, friction and HESD. The performance of both UF-NTO and NTO/Al mix was evaluated by detonation-spreading floret tests. At the same pressed density, it was found that, when initiated by a 3-mm-diameter flyer plate, the aluminized NTO composite produced a shallower dent on a copper witness plate than neat UF-NTO and thus was inferior to UF-NTO in detonation spreading.

Influence of mineralogical, petrographical, and geochemical characteristics of impure limestones on the composition of fired hydraulic lime: a case study on Lower Palaeozoic limestones from the Prague Basin (Barrandian area, Czech Republic)

NASA Astrophysics Data System (ADS)

Kozlovcev, Petr; Přikryl, Richard

2014-05-01

Prague Basin, making part of the Barrandian area (Bohemian Massif, Czech Republic), is a rift-like depression filled with non-metamorphosed sedimentary series of Upper Proterozoic - Lower Palaeozoic age. Among other sedimentary rocks, different types of limestones are present. These limestone were historically exploited and used for various purposes including natural and decorative stone, common construction material, and also a raw material for firing of inorganic binders: aerial lime, hydraulic lime and/or, more recently, Ordinary Portland Cement (OPC). Lithotypes with higher amount of silica and/or clay component were of special interest due to the hydraulicity of fired product known as "pasta di Praga" in Baroque. However, our recent knowledge of these limestones is incomplete in terms of the contribution of mineralogical, geochemical, and petrographical characteristics on the properties of fired hydraulic lime. In the recent study, representative samples of 4 facies of the Lower Devonian limestone (Kosoř ls., Řeporyje ls., Dvorce-Prokop ls., and Zlíchov ls.) were subjected to a detailed mineralogical and petrographic study of raw material by means of polarizing microscopy, cathodoluminiscence of thin sections and scanning electron microscopy with an energy dispersive spectrometer (SEM-EDS). X-ray diffraction (XRD) of insoluble residues obtained by treatment with both the hydrochloric acid and the acetic acid solution was used. Wet silicate analysis provided data on the content of major elements from which standard cement and lime indexes and modules were calculated. Laboratory firing experiments of these limestone were performed by a calcination at temperature ranging from 850 to 1200°C (after 50°C). XRD of fired products shows that limestones with high content of silica (some of the Dvorce-Prokop ls.) produced binder with high amount of newly formed calcium silicates (larnite). Gehlenite and others calcium aluminates and aluminosilicates are typical for firing of limestones with higher content of clay minerals (illite and kaolinite) which are common in Kosoř ls., Řeporyje ls., and Dvorce-Prokop ls. Brownmillerite was formed in limestones exhibiting higher proportion of Fe-oxihydroxides (specifically Řeporyje ls). Presence of free lime and portlandite correlates with decreasing content of non-carbonate material (some varieties of the Dvorce-Prokop ls. from Bráník Rocks).

Electroplate Short Mix

DOE Office of Scientific and Technical Information (OSTI.GOV)

None

2017-06-19

Modifying the surface chemistry of materials by aluminization can protect vulnerable materials from corroding in harsh environments. The industry deals with corrosion issues is to regularly inspect components and replace them with corrosion resistant components.

Space Station WP-2 application of LDEF MLI results

NASA Technical Reports Server (NTRS)

Smith, Charles A.; Hasegawa, Mark M.; Jones, Cherie A.

1993-01-01

The Cascaded Variable Conductance Heat Pipe Experiment, which was developed by Michael Grote of McDonnell Douglas Electronic Systems Company, was located in Tray F-9 of the Long Duration Exposure Facility (LDEF), where it received atomic oxygen almost normal to its surface. The majority of the tray was covered by aluminized Kapton polyimide multilayer insulation (MLI), which showed substantial changes from atomic oxygen erosion. Most of the outermost Kapton layer of the MLI and the polyester scrim cloth under it were lost, and there was evidence of contaminant deposition which discolored the edges of the MLI blanket. Micrometeoroid and orbital debris (MM/OD) hits caused small rips in the MLI layers, and in some cases left cloudy areas where the vapor plume caused by a hit condensed on the next layer. The MLI was bent gradually through 90 deg at the edges to enclose the experiment, and the Kapton that survived along the curved portion showed the effects of atomic oxygen erosion at oblique angles. In spite of space environment effects over the period of the LDEF mission, the MLI blanket remained functional. The results of the analysis of LDEF MLI were used in developing the standard MLI blanket for Space Station Work Package-2 (WP-2). This blanket is expected to last 30 years when exposed to the low Earth orbit (LEO) environment constituents of atomic oxygen and MM/OD, which are the most damaging to MLI materials. The WP-2 standard blanket consists of an outer cover made from Beta-cloth glass fiber fabric which is aluminized on the interior surface, and an inner cover of 0.076-mm (0.003-in) double-side-aluminized perforated Kapton. The inner reflector layers are 0.0076-mm (0.0003-in) double-side aluminized, perforated Kapton separated by layers of Dacron polyester fabric. The outer cover was selected to be resistant to the LEO environment and durable enough to survive in orbit for 30 years. This paper describes the analyses of the LDEF MLI results, and how these results contributed to the selection of the WP-2 MLI blanket materials and configuration.

Origin of coronas in metagabbros of the Adirondack mts., N. Y

USGS Publications Warehouse

Whitney, P.R.; McLelland, J.M.

1973-01-01

Metagabbros from two widely separated areas in the Adirondacks show development of coronas. In the Southern Adirondacks, these are cored by olivine which is enclosed in a shell of orthopyroxene that is partially, or completely, rimmed by symplectites consisting of clinopyroxene and spinel. Compositions of the corona phases have been determined by electron probe and are consistent with a mechanism involving three partial reactions, thus: (a) Olivine=Orthopyroxene+(Mg, Fe)++. (b) Plagioclase+(Mg, Fe)+++Ca++=Clinopyroxene+Spinel+Na+. (c) Plagioclase+(Mg, Fe)+++Na+=Spinel+more sodic plagioclase+Ca++. Reaction (a) occurs in the inner shell of the corona adjacent to olivine; reaction (b) in the outer shell; and (c) in the surrounding plagioclase, giving rise to the spinel clouding which is characteristic of the plagioclase in these rocks. Alumina and silica remain relatively immobile. These reactions, when balanced, can be generalized to account for the aluminous nature of the pyroxenes and for changing plagioclase composition. Summed together, the partial reactions are equivalent to: (d) Olivine + Anorthite = Aluminous orthopyroxene + Aluminous Clinopyroxene + Spinel (Kushiro and Yoder, 1966). In the Adirondack Highlands, coronas between olivine and plagioclase commonly have an outer shell of garnet replacing the clinopyroxene/spinel shell. The origin of the garnet can also be explained in terms of three partial reactions: (e) Orthopyroxene+Ca++=Clinopyroxene+(Mg, Fe)++. (f) Clinopyroxene+Spinel+Plagioclase+(Mg, Fe)++=Garnet+Ca+++Na+. (g) Plagioclase+(Mg, Fe)+++Na+=Spinel + more sodic plagioclase+Ca++. These occur in the inner and outer corona shell and the surrounding plagioclase, respectively, and involve the products of reactions (a)-(d). Alumina and silica are again relatively immobile. Balanced, and generalized to account for aluminous pyroxenes and variable An content of plagioclase, they are equivalent to: (h) Orthopyroxene+Anorthite+Spinel=Garnet (Green and Ringwood, 1967). Amphibole coronas about opaque oxides in rocks of both areas are the result of oxide/plagioclase reactions with addition of magnesium from coexisting olivine. Based on published experimental data, pressure and temperature at the time of corona formation were on the order of 8 kb and 800?? C for the garnet bearing coronas, with somewhat lower pressures indicated for the clinopyroxene/spinel coronas. ?? 1973 Springer-Verlag.

A practical method for estimating maximum shear modulus of cemented sands using unconfined compressive strength

NASA Astrophysics Data System (ADS)

Choo, Hyunwook; Nam, Hongyeop; Lee, Woojin

2017-12-01

The composition of naturally cemented deposits is very complicated; thus, estimating the maximum shear modulus (Gmax, or shear modulus at very small strains) of cemented sands using the previous empirical formulas is very difficult. The purpose of this experimental investigation is to evaluate the effects of particle size and cement type on the Gmax and unconfined compressive strength (qucs) of cemented sands, with the ultimate goal of estimating Gmax of cemented sands using qucs. Two sands were artificially cemented using Portland cement or gypsum under varying cement contents (2%-9%) and relative densities (30%-80%). Unconfined compression tests and bender element tests were performed, and the results from previous studies of two cemented sands were incorporated in this study. The results of this study demonstrate that the effect of particle size on the qucs and Gmax of four cemented sands is insignificant, and the variation of qucs and Gmax can be captured by the ratio between volume of void and volume of cement. qucs and Gmax of sand cemented with Portland cement are greater than those of sand cemented with gypsum. However, the relationship between qucs and Gmax of the cemented sand is not affected by the void ratio, cement type and cement content, revealing that Gmax of the complex naturally cemented soils with unknown in-situ void ratio, cement type and cement content can be estimated using qucs.

Physico-chemical characterization of mortars as a tool in studying specific hydraulic components: application to the study of ancient Naxos aqueduct

NASA Astrophysics Data System (ADS)

Maravelaki-Kalaitzaki, P.; Galanos, A.; Doganis, I.; Kallithrakas-Kontos, N.

2011-07-01

Mortars and plasters from the ancient aqueduct on the island of Naxos, Greece, were studied with regard to mineralogical and chemical composition, grain size distribution, raw materials and hydraulic properties, in order to assess their characteristics and design compatible repair mortars. The authentic materials contained lime, crushed-brick, siliceous and calcitic aggregates, in different proportions according to mortar type. Crushed-bricks fired at low temperatures and lightweight volcanic aggregates contained amorphous phases, which upon reaction with lime yielded hydraulic components capable of protecting the construction from the continuous presence of water. Hydraulic calcium silicate/aluminate hydrates, the proportions and the perfect packing of the raw materials, along with the diligent application justify the longevity and durability of the studied samples. The hydraulic properties of samples were pointed out through (a) the well-established CO2/H2O ratio derived from the thermogravimetric analysis and (b) by introducing two powerful indices issued from the chemical analysis, namely CaOhydr and soluble SiO2 hydr. These indices improved the clustering of hydraulic mortars and provided better correlation between mortars, plasters and their binders. By comparing grain size distribution and hydraulicity indices it was possible to distinguish among the construction phases. Based on this study, repair mortars were formulated by hydraulic lime, siliceous sand, calcareous and crushed-brick aggregates, with the optimal water content, ensuring optimum workability and compatible appearance with the authentic ones.

Content and distribution of noncollagenous matrix proteins in bone and cementum: relationship to speed of formation and collagen packing density.

PubMed

Nanci, A

1999-06-30

The organic matrix of collagen-based calcified tissues consists of a supporting collagen meshwork and various noncollagenous matrix proteins (NCPs). Together, they contribute to determining the structure and biomechanical properties of the tissue. Their respective organization and interrelation can advantageously be examined by immunocytochemistry, an approach which allows correlation of composition with structure. The aim of this article is to review postembedding immuno- and lectin-gold-labeling data on the characterization of the noncollagenous compartment in rat and human bone and cementum, and on its relationship to collagen. The two major NCPs, bone sialoprotein and osteopontin, generally codistribute and accumulate in cement lines and in the spaces among the mineralized collagen fibrils. However, there are variations in their distribution and density of labeling throughout the tissue. Indeed, bone and cementum can form in environments that are either poor or enriched in NCPs. The amount of NCPs generally correlates with bone and cementum types and with speed of formation of the tissue and packing density of collagen fibrils. Taken together, the data suggest that production of both collagenous and noncollagenous constituents can be "modulated" during formation of collagen-based calcified tissues. It is concluded that, in addition to structural and compositional parameters, tissue dynamics must be taken into consideration in order to understand the significance of the apparent accumulation of NCPs at some sites and to determine the mechanisms of normal and pathological calcified tissue formation. Copyright 1999 Academic Press.

Textural and mineralogical study of sandstones from the onshore Gulf of Alaska Tertiary Province, southern Alaska

USGS Publications Warehouse

Winkler, Gary R.; McLean, Hugh; Plafker, George

1976-01-01

Petrographic examination of 74 outcrop samples of Paleocene through Pliocene age from the onshore Gulf of Alaska Tertiary Province indicates that sandstones of the province characteristically are texturally immature and mineralogically unstable. Diagenetic alteration of framework grains throughout the stratigraphic sequence has produced widespread zeolite cement or phyllosilicate grain coatings and pseudomatrix. Multiple deformation and deep burial of the older Tertiary sequence--the Orca Group, the shale of Haydon Peak, and the Kulthieth and Tokun Formations--caused extensive alteration and grain interpenetration, resulting in low porosity values. Less intense deformation and intermediate depth of burial of the younger Tertiary sequence--the Katalla, Poul Creek, Redwood, and Yakataga Formations--has resulted in a greater range in textural properties. Most sandstone samples in the younger Tertiary sequence are poorly sorted, tightly packed, and have strongly appressed framework grains, but some are less tightly packed and contain less matrix. Soft and mineralogically unstable framework grains have undergone considerable alteration, reducing pore space even in the youngest rocks. Measurements of porosity, permeability, grain density, and sonic velocity of outcrop samples of the younger Tertiary sequence indicate a modest up-section improvement in sandstone reservoir characteristics. Nonetheless porosity and permeability values typically are below 16 percent and 15 millidarcies respectively and grain densities are consistently high, about 2.7 gm/cc. Low permeability and porosity values, and high grain densities and sonic velocities appear to be typical of most outcrop areas throughout the onshore Gulf of Alaska Tertiary Province.

Composite flexible blanket insulation

NASA Technical Reports Server (NTRS)

Kourtides, Demetrius A. (Inventor); Lowe, David M. (Inventor)

1994-01-01

An improved composite flexible blanket insulation is presented comprising top silicon carbide having an interlock design, wherein the reflective shield is composed of single or double aluminized polyimide and wherein the polyimide film has a honeycomb pattern.

Inexpensive cryogenic insulation replaces vacuum jacketed line

NASA Technical Reports Server (NTRS)

Fuchs, C. E.

1967-01-01

Commercially available aluminized Mylar, cork and fiber glass form a multilayered sealed system and provide rugged and economical field installed insulation for cryogenic /liquid nitrogen or oxygen/ pipe lines in an exposed environment.

Synthesis and use of (perfluoroaryl) fluoro-aluminate anion

DOEpatents

Marks, T.J.; Chen, Y.X.

1998-12-29

A trityl perfluorophenyl alumninate such as tris(2,2{prime},2{double_prime}nonafluorobiphenyl) fluoroaluminate (PBA{sup {minus}}) and its role as a cocatalyst in metallocene-mediated olefin polymerization is disclosed. 4 figs.

Methods for both coating a substrate with aluminum oxide and infusing the substrate with elemental aluminum

DOEpatents

Choi, Jung-Pyung; Weil, Kenneth Scott

2016-11-01

Methods of aluminizing the surface of a metal substrate. The methods of the present invention do not require establishment of a vacuum or a reducing atmosphere, as is typically necessary. Accordingly, aluminization can occur in the presence of oxygen, which greatly simplifies and reduces processing costs by allowing deposition of the aluminum coating to be performed, for example, in air. Embodiments of the present invention can be characterized by applying a slurry that includes a binder and powder granules containing aluminum to the metal substrate surface. Then, in a combined step, a portion of the aluminum is diffused into the substrate and a portion of the aluminum is oxidized by heating the slurry to a temperature greater than the melting point of the aluminum in an oxygen-containing atmosphere.

Alternative Sodium Recovery Technology—High Hydroxide Leaching: FY10 Status Report

DOE Office of Scientific and Technical Information (OSTI.GOV)

Mahoney, Lenna A.; Neiner, Doinita; Peterson, Reid A.

2011-02-04

Boehmite leaching tests were carried out at NaOH concentrations of 10 M and 12 M, temperatures of 85°C and 60°C, and a range of initial aluminate concentrations. These data, and data obtained during earlier 100°C tests using 1 M and 5 M NaOH, were used to establish the dependence of the boehmite dissolution rate on hydroxide concentration, temperature, and initial aluminate concentration. A semi-empirical kinetic model for boehmite leaching was fitted to the data and used to calculate the NaOH additions required for leaching at different hydroxide concentrations. The optimal NaOH concentration for boehmite leaching at 85°C was estimated, basedmore » on minimizing the amount of Na that had to be added in NaOH to produce a given boehmite conversion.« less

Thermal and mechanical properties of aluminized fabrics for use in ferrous metal handling operations.

PubMed

Wren, J E; Scott, W D; Bates, C E

1977-11-01

Protective garments are normally worn in molten handling operations to provide some protection against molten metal splashes. These garments are also intended to provide protection against radiant heat, and they should be as heat resistant and comfortable as possible. Asbestos-based fabrics have been employed for many years, but recently some concern has been expressed over possible asbestos exposure. This program was undertaken to explore the ability of several types of fabrics to resist heat transfer during molten metal impact. A molten metal splash test, along with standard methods for determining tensile strength, flame resistance, and abrasion-flexing resistance were used to evaluate several classes of protective fabrics. The results indicate that there are materials available that offer equal or better mechanical properties and thermal protection compared to aluminized asbestos.

A general strategy for the ultrafast surface modification of metals.

PubMed

Shen, Mingli; Zhu, Shenglong; Wang, Fuhui

2016-12-07

Surface modification is an essential step in engineering materials that can withstand the increasingly aggressive environments encountered in various modern energy-conversion systems and chemical processing industries. However, most traditional technologies exhibit disadvantages such as slow diffusion kinetics, processing difficulties or compatibility issues. Here, we present a general strategy for the ultrafast surface modification of metals inspired by electromigration, using aluminizing austenitic stainless steel as an example. Our strategy facilitates the rapid formation of a favourable ductile surface layer composed of FeCrAl or β-FeAl within only 10 min compared with several hours in conventional processes. This result indicates that electromigration can be used to achieve the ultrafast surface modification of metals and can overcome the limitations of traditional technologies. This strategy could be used to aluminize ultra-supercritical steam tubing to withstand aggressive oxidizing environments.

Oxidation of Uncoated and Aluminized 9-12% Cr Boiler Steels at 550-650 °C

NASA Astrophysics Data System (ADS)

Metsäjoki, J.; Huttunen-Saarivirta, E.; Lepistö, T.

2011-03-01

In this paper, oxidation behavior of 9-12% Cr steels P91 and HCM12A is studied in air and in a mixture of air and water vapor. Comparison is made between these steels in uncoated condition and coated with aluminum diffusion coating by a slurry method. Oxidation tests were carried out at 550, 600, and 650 °C for a discontinued duration of 1000 h; every 250 h the specimens were slowly cooled to room temperature and weighed. SEM + EDS and XRD characterization were performed after 500 and 1000 h. The results showed that oxidation rate of uncoated P91 and HCM12A was significantly higher in the mixture of air and water vapor than in air. Oxidation resistance of the studied materials improved substantially when they were aluminized.

Production of Magnesium by Vacuum Aluminothermic Reduction with Magnesium Aluminate Spinel as a By-Product

NASA Astrophysics Data System (ADS)

Wang, Yaowu; You, Jing; Peng, Jianping; Di, Yuezhong

2016-06-01

The Pidgeon process currently accounts for 85% of the world's magnesium production. Although the Pidgeon process has been greatly improved over the past 10 years, such production still consumes much energy and material and creates much pollution. The present study investigates the process of producing magnesium by employing vacuum aluminothermic reduction and by using magnesite as material and obtaining magnesium aluminate spinel as a by-product. The results show that compared with the Pidgeon process, producing magnesium by vacuum aluminothermic reduction can save materials by as much as 50%, increase productivity up to 100%, and save energy by more than 50%. It can also reduce CO2 emission by up to 60% and realize zero discharge of waste residue. Vacuum aluminothermic reduction is a highly efficient, low-energy-consumption, and environmentally friendly method of producing magnesium.

Prediction of the mass gain during high temperature oxidation of aluminized nanostructured nickel using adaptive neuro-fuzzy inference system

NASA Astrophysics Data System (ADS)

Hayati, M.; Rashidi, A. M.; Rezaei, A.

2012-10-01

In this paper, the applicability of ANFIS as an accurate model for the prediction of the mass gain during high temperature oxidation using experimental data obtained for aluminized nanostructured (NS) nickel is presented. For developing the model, exposure time and temperature are taken as input and the mass gain as output. A hybrid learning algorithm consists of back-propagation and least-squares estimation is used for training the network. We have compared the proposed ANFIS model with experimental data. The predicted data are found to be in good agreement with the experimental data with mean relative error less than 1.1%. Therefore, we can use ANFIS model to predict the performances of thermal systems in engineering applications, such as modeling the mass gain for NS materials.

The Effect of (Ag, Ni, Zn)-Addition on the Thermoelectric Properties of Copper Aluminate

PubMed Central

Yanagiya, Shun-ichi; Van Nong, Ngo; Xu, Jianxiao; Pryds, Nini

2010-01-01

Polycrystalline bulk copper aluminate Cu1-x-yAgxByAlO2 with B = Ni or Zn were prepared by spark plasma sintering and subsequent thermal treatment. The influence of partial substitution of Ag, Ni and Zn for Cu-sites in CuAlO2 on the high temperature thermoelectric properties has been studied. The addition of Ag and Zn was found to enhance the formation of CuAlO2 phase and to increase the electrical conductivity. The addition of Ag or Ag and Ni on the other hand decreases the electrical conductivity. The highest power factor of 1.26 × 10-4 W/mK2 was obtained for the addition of Ag and Zn at 1,060 K, indicating a significant improvement compared with the non-doped CuAlO2 sample.

Nickel stabilization efficiency of aluminate and ferrite spinels and their leaching behavior.

PubMed

Shih, Kaimin; White, Tim; Leckie, James O

2006-09-01

Stabilization efficiencies of spinel-based construction ceramics incorporating simulated nickel-laden waste sludge were evaluated and the leaching behavior of products investigated. To simulate the process of immobilization, nickel oxide was mixed alternatively with gamma-alumina, kaolinite, and hematite. These tailoring precursors are commonly used to prepare construction ceramics in the building industry. After sintering from 600 to 1480 degrees C at 3 h, the nickel aluminate spinel (NiAl204) and the nickel ferrite spinel (NiFe204) crystallized with the ferrite spinel formation commencing about 200-300 degrees C lower than for the aluminate spinel. All the precursors showed high nickel incorporation efficiencies when sintered at temperatures greater than 1250 degrees C. Prolonged leach tests (up to 26 days) of product phases were carried out using a pH 2.9 acetic acid solution, and the spinel products were invariably superior to nickel oxide for immobilization over longer leaching periods. The leaching behavior of NiAl2O4 was consistent with congruent dissolution without significant reprecipitation, but for NiFe2O4, ferric hydroxide precipitation was evident. The major leaching reaction of sintered kaolinite-based products was the dissolution of cristobalite rather than NiAl2O4. This study demonstrated the feasibility of transforming nickel-laden sludge into spinel phases with the use of readily available and inexpensive ceramic raw materials, and the successful reduction of metal mobility under acidic environments.

An advanced NMR protocol for the structural characterization of aluminophosphate glasses.

PubMed

van Wüllen, Leo; Tricot, Grégory; Wegner, Sebastian

2007-10-01

In this work a combination of complementary advanced solid-state nuclear magnetic resonance (NMR) strategies is employed to analyse the network organization in aluminophosphate glasses to an unprecedented level of detailed insight. The combined results from MAS, MQMAS and (31)P-{(27)Al}-CP-heteronuclear correlation spectroscopy (HETCOR) NMR experiments allow for a detailed speciation of the different phosphate and aluminate species present in the glass. The interconnection of these local building units to an extended three-dimensional network is explored employing heteronuclear dipolar and scalar NMR approaches to quantify P-O-Al connectivity by (31)P{(27)Al}-heteronuclear multiple quantum coherence (HMQC), -rotational echo adiabatic passage double resonance (REAPDOR) and -HETCOR NMR as well as (27)Al{(31)P}-rotational echo double resonance (REDOR) NMR experiments, complemented by (31)P-2D-J-RESolved MAS NMR experiments to probe P-O-P connectivity utilizing the through bond scalar J-coupling. The combination of the results from the various NMR approaches enables us to not only quantify the phosphate units present in the glass but also to identify their respective structural environments within the three-dimensional network on a medium length scale employing a modified Q notation, Q(n)(m),(AlO)(x), where n denotes the number of connected tetrahedral phosphate, m gives the number of aluminate species connected to a central phosphate unit and x specifies the nature of the bonded aluminate species (i.e. 4, 5 or 6 coordinate aluminium).

Germanium abundances in lunar basalts: Evidence of mantle metasomatism

DOE Office of Scientific and Technical Information (OSTI.GOV)

Dickinson, T.; Taylor, G.J.; Keil, T.K.

1988-01-01

To fill in gaps in the present Ge data base, mare basalts were analyzed for Ge and other elements by RNAA and INAA. Mare basalts from Apollo 11, 12, 15, 17 landing sites are rather uniform in Ge abundance, but Apollo 14 aluminous mare basalts and KREEP are enriched in Ge by factors of up to 300 compared to typical mare basalts. These Ge enrichments are not associated with other siderophile element enrichments and, thus, are not due to differences in the amount of metal segregated during core formation. Based on crystal-chemical and inter-element variations, it does not appear thatmore » the observed Ge enrichments are due to silicate liquid immiscibility. Elemental ratios in Apollo 14 aluminous mare basalts, green and orange glass, average basalts and KREEP suggest that incorporation of late accreting material into the source regions or interaction of the magmas with primitive undifferentiated material is not a likely cause for the observed Ge enrichments. We speculate that the most plausible explanation for these Ge enrichments is complexing and concentration of Ge by F, Cl or S in volatile phases. In this manner, the KREEP basalt source regions may have been metasomatized and Apollo 14 aluminous mare basalt magmas may have become enriched in Ge by interacting with these metasomatized areas. The presence of volatile- and Ge-rich regions in the Moon suggests that the Moon was never totally molten. 71 refs., 1 fig., 6 tabs.« less

Lewis acid properties of alumina based catalysts: study by paramagnetic complexes of probe molecules

NASA Astrophysics Data System (ADS)

Fionov, Alexander V.

2002-06-01

Lewis acid properties of LiAl 5O 8/Al 2O 3 (2 wt.% Li) and MgAl 2O 4/Al 2O 3 (3 wt.% Mg) catalysts were studied by EPR of adsorbed probe molecules--anthraquinone and 2,2,6,6-tetramethylpiperidine- N-oxyl (TEMPO). The lesser (in comparison with γ-Al 2O 3) concentration and the strength of Lewis acid sites (LAS) formed on the surface of aluminate layer has been shown. The stability of this layer plays important role in the change of Lewis acid properties during the calcination of modified alumina. The lithium aluminate layer was stable at used calcination temperature, 773 K, meanwhile magnesium aluminate layer observed only at calcination temperature below 723 K. The increase of the calcination temperature to 773 K caused the segregation of MgAl 2O 4 on the surface resulted in the release of alumina surface and recovery of the Lewis acid properties. The differences in the LAS manifestations towards TEMPO and anthraquinone was discussed. The mechanism of the formation of anthraquinone paramagnetic complexes with LAS--three-coordinated aluminum ions--was proposed. This mechanism includes the formation of anthrasemiquinone, and then--anthrasemiquinone ion pair or triple ion. Fragments like -O-Al +-O- play the role of cations in these ion pairs and triple ions. Proposed mechanism can also be applied for the consideration of similar anthraquinone paramagnetic complexes on the surface of gallium oxide containing systems.

Influence of Chloride-Ion Adsorption Agent on Chloride Ions in Concrete and Mortar.

PubMed

Peng, Gai-Fei; Feng, Nai-Qian; Song, Qi-Ming

2014-04-30

The influence of a chloride-ion adsorption agent (Cl agent in short), composed of zeolite, calcium aluminate hydrate and calcium nitrite, on the ingress of chloride ions into concrete and mortar has been experimentally studied. The permeability of concrete was measured, and the chloride ion content in mortar was tested. The experimental results reveal that the Cl agent could adsorb chloride ions effectively, which had penetrated into concrete and mortar. When the Cl agent was used at a dosage of 6% by mass of cementitious materials in mortar, the resistance to the penetration of chloride ions could be improved greatly, which was more pronounced when a combination of the Cl agent and fly ash or slag was employed. Such an effect is not the result of the low permeability of the mortar, but might be a result of the interaction between the Cl agent and the chloride ions penetrated into the mortar. There are two possible mechanisms for the interaction between the Cl agent and chloride ion ingress. One is the reaction between calcium aluminate hydrate in the Cl agent and chloride ions to form Friedel's salt, and the other one is that calcium aluminate hydrate reacts with calcium nitrite to form AFm during the early-age hydration of mortar and later the NO₂ - in AFm is replaced by chloride ions, which then penetrate into the mortar, also forming Friedel's salt. More research is needed to confirm the mechanisms.

Influence of Chloride-Ion Adsorption Agent on Chloride Ions in Concrete and Mortar

PubMed Central

Peng, Gai-Fei; Feng, Nai-Qian; Song, Qi-Ming

2014-01-01

The influence of a chloride-ion adsorption agent (Cl agent in short), composed of zeolite, calcium aluminate hydrate and calcium nitrite, on the ingress of chloride ions into concrete and mortar has been experimentally studied. The permeability of concrete was measured, and the chloride ion content in mortar was tested. The experimental results reveal that the Cl agent could adsorb chloride ions effectively, which had penetrated into concrete and mortar. When the Cl agent was used at a dosage of 6% by mass of cementitious materials in mortar, the resistance to the penetration of chloride ions could be improved greatly, which was more pronounced when a combination of the Cl agent and fly ash or slag was employed. Such an effect is not the result of the low permeability of the mortar, but might be a result of the interaction between the Cl agent and the chloride ions penetrated into the mortar. There are two possible mechanisms for the interaction between the Cl agent and chloride ion ingress. One is the reaction between calcium aluminate hydrate in the Cl agent and chloride ions to form Friedel’s salt, and the other one is that calcium aluminate hydrate reacts with calcium nitrite to form AFm during the early-age hydration of mortar and later the NO2− in AFm is replaced by chloride ions, which then penetrate into the mortar, also forming Friedel’s salt. More research is needed to confirm the mechanisms. PMID:28788625

A modified PMMA cement (Sub-cement) for accelerated fatigue testing of cemented implant constructs using cadaveric bone.

PubMed

Race, Amos; Miller, Mark A; Mann, Kenneth A

2008-10-20

Pre-clinical screening of cemented implant systems could be improved by modeling the longer-term response of the implant/cement/bone construct to cyclic loading. We formulated bone cement with degraded fatigue fracture properties (Sub-cement) such that long-term fatigue could be simulated in short-term cadaver tests. Sub-cement was made by adding a chain-transfer agent to standard polymethylmethacrylate (PMMA) cement. This reduced the molecular weight of the inter-bead matrix without changing reaction-rate or handling characteristics. Static mechanical properties were approximately equivalent to normal cement. Over a physiologically reasonable range of stress-intensity factor, fatigue crack propagation rates for Sub-cement were higher by a factor of 25+/-19. When tested in a simplified 2 1/2-D physical model of a stem-cement-bone system, crack growth from the stem was accelerated by a factor of 100. Sub-cement accelerated both crack initiation and growth rate. Sub-cement is now being evaluated in full stem/cement/femur models.

Mineral resource of the month: hydraulic cement

USGS Publications Warehouse

van Oss, Hendrik G.

2012-01-01

Hydraulic cements are the binders in concrete and most mortars and stuccos. Concrete, particularly the reinforced variety, is the most versatile of all construction materials, and most of the hydraulic cement produced worldwide is portland cement or similar cements that have portland cement as a basis, such as blended cements and masonry cements. Cement typically makes up less than 15 percent of the concrete mix; most of the rest is aggregates. Not counting the weight of reinforcing media, 1 ton of cement will typically yield about 8 tons of concrete.

Evaluation of the amount of excess cement around the margins of cement-retained dental implant restorations: the effect of the cement application method.

PubMed

Chee, Winston W L; Duncan, Jesse; Afshar, Manijeh; Moshaverinia, Alireza

2013-04-01

Complete removal of excess cement from subgingival margins after cementation of implant-supported restorations has been shown to be unpredictable. Remaining cement has been shown to be associated with periimplant inflammation and bleeding. The purpose of this study was to investigate and compare the amount of excess cement after cementation with 4 different methods of cement application for cement-retained implant-supported restorations. Ten implant replicas/abutments (3i) were embedded in acrylic resin blocks. Forty complete veneer crowns (CVCs) were fabricated by waxing onto the corresponding plastic waxing sleeves. The wax patterns were cast and the crowns were cemented to the implant replicas with either an interim (Temp Bond) or a definitive luting agent (FujiCEM). Four methods of cement application were used for cementation: Group IM-Cement applied on the internal marginal area of the crown only; Group AH-Cement applied on the apical half of the axial walls of the crown; Group AA-Cement applied to all axial walls of the interior surface of the crown, excluding the occlusal surface; and Group PI-Crown filled with cement then seated on a putty index formed to the internal configuration of the restoration (cementation device) (n=10). Cement on the external surfaces was removed before seating the restoration. Cement layers were applied on each crown, after which the crown was seated under constant load (80 N) for 10 minutes. The excess cement from each specimen was collected and measured. One operator performed all the procedures. Results for the groups were compared, with 1 and 2-way ANOVA and the Tukey multiple range test (α=.05). No significant difference in the amount of excess/used cement was observed between the 2 different types of cements (P=.1). Group PI showed the least amount of excess cement in comparison to other test groups (P=.031). No significant difference was found in the amount of excess cement among groups MI, AH, and AA. Group AA showed the highest amount of excess cement. The volume of cement used for group PI specimens was significantly higher than for those in the other groups (P=.001). With respect to the volume of cement loaded into the test crowns no statistically significant difference was observed among other test groups (groups IM, AH, and AA). Group MI used the least amount of cement, followed by group AH and AA. No correlation between the amount of used cement and the amount of excess cement was found in any of the tested groups. Within the limitations of this in vitro study, the least amount of excess cement was present when a cementation device was used to displace the excess cement before seating the crown on the abutment (Group PI). With this technique a uniform layer of the luting agent is distributed over the internal surface of the crown leaving minimal excess cement when the restoration is seated. Copyright © 2013 The Editorial Council of the Journal of Prosthetic Dentistry. Published by Mosby, Inc. All rights reserved.

Effects of a cementing technique in addition to luting agent on the uniaxial retention force of a single-tooth implant-supported restoration: an in vitro study.

PubMed

Santosa, Robert E; Martin, William; Morton, Dean

2010-01-01

Excess residual cement around the implant margin has been shown to be detrimental to the peri-implant tissue. This in vitro study examines the retentive strengths of two different cementing techniques and two different luting agents on a machined titanium abutment and solid screw implants. The amount of reduction of excess cement weight between the two cementation techniques was assessed. Forty gold castings were fabricated for 4.1 mm in diameter and 10 mm in length solid-screw dental implants paired with 5.5-mm machined titanium abutments. Twenty implants received a provisional cement, and 20 implants received a definitive cement. Each group was further divided into two groups. In the control group, cement was applied and the castings seated over the implant-abutment assembly. The excess cement was then removed. In the study group, a "practice abutment" was used to express excess cement prior to cementation. The weight of the implant-casting assembly was measured and the residual weight of cement was calculated. The samples were then stored for 24 hours at 100% humidity prior to tensile strength testing. Statistical analysis revealed significant differences in tensile strength across the groups. Further Tukey tests showed no significant difference in tensile strength between the practice abutment technique and the conventional technique for both definitive and provisional cements. There was a significant reduction in residual cement weight, irrespective of the type of cement, when the practice abutment was used prior to cementation. Cementation of implant restorations on a machined abutment using the practice abutment technique and definitive cement may provide similar uniaxial retention force and significantly reduced residual cement weight compared to the conventional technique of cement removal.

Influence of cement film thickness on the retention of implant-retained crowns.

PubMed

Mehl, Christian; Harder, Sönke; Steiner, Martin; Vollrath, Oliver; Kern, Matthias

2013-12-01

The main goal of this study was to establish a new, high precision procedure to evaluate the influence of cement film thickness on the retention of cemented implant-retained crowns. Ninety-six tapered titanium abutments (6° taper, 4.3 mm diameter, Camlog) were shortened to 4 mm. Computer-aided design was used to design the crowns, and selective laser sintering, using a cobalt-chromium alloy, was used to produce the crowns. This method used a focused high-energy laser beam to fuse a localized region of metal powder to build up the crowns gradually. Before cementing, preset cement film thicknesses of 15, 50, 80, or 110 μm were established. Glass ionomer, polycarboxylate, or resin cements were used for cementation. After 3 days storage in demineralized water, the retention of the crowns was measured in tension using a universal testing machine. The cement film thicknesses could be achieved with a high level of precision. Interactions between the factors cement and cement film thickness could be found (p ≤ 0.001). For all cements, crown retention decreased significantly between a cement film thickness of 15 and 50 μm (p ≤ 0.001). At 15 μm cement film thickness, the resin cement was the most retentive cement, followed by the polycarboxylate and then the glass ionomer cement (p ≤ 0.05). The results suggest that cement film thickness has an influence on the retentive strength of cemented implant-retained crowns. © 2013 by the American College of Prosthodontists.

The mechanical effect of the existing cement mantle on the in-cement femoral revision.

PubMed

Keeling, Parnell; Lennon, Alexander B; Kenny, Patrick J; O'Reilly, Peter; Prendergast, Patrick J

2012-08-01

Cement-in-cement revision hip arthroplasty is an increasingly popular technique to replace a loose femoral stem which retains much of the original cement mantle. However, some concern exists regarding the retention of the existing fatigued and aged cement in such cement-in-cement revisions. This study investigates whether leaving an existing fatigued and aged cement mantle degrades the mechanical performance of a cement-in-cement revision construct. Primary cement mantles were formed by cementing a polished stem into sections of tubular steel. If in the test group, the mantle underwent conditioning in saline to simulate ageing and was subject to a fatigue of 1 million cycles. If in the control group no such conditioning or fatigue was carried out. The cement-in-cement procedure was then undertaken. Both groups underwent a fatigue of 1 million cycles subsequent to the revision procedure. Application of a Mann-Whitney test on the recorded subsidence (means: 0.51, 0.46, n=10+10, P=0.496) and inducible displacement (means: 0.38, 0.36, P=0.96) revealed that there was no statistical difference between the groups. This study represents further biomechanical investigation of the mechanical behaviour of cement-in-cement revision constructs. Results suggest that pre-revision fatigue and ageing of the cement may not be deleterious to the mechanical performance of the revision construct. Thus, this study provides biomechanical evidence to back-up recent successes with this useful revision technique. Copyright © 2012 Elsevier Ltd. All rights reserved.

The effect of using a cement gun with a narrow nozzle on cement penetration for total elbow arthroplasty: a cadaveric study.

PubMed

Smith, Geoffrey C S; McCann, Phillip S; Simpson, Danielle; Blewitt, Neil; Amirfeyz, Rouin

2015-02-01

To compare the cement mantle characteristics associated with use of a narrow nozzle cement gun versus the use of a 60-mL catheter tip syringe. Twelve cadaveric distal humeri were cemented with either a cement gun or a syringe without canal occlusion. The humeri were sectioned and photographed. The corticocancellous junction and the outer margin of the cement mantle were analyzed digitally. The corticocancellous junction defined the available area for cement penetration. The outline of the cement mantle defined the actual area of penetration. The ratio of penetration to the available area was recorded for each slice. The mean ratio for each humerus was multiplied by the number of slices in that sample containing cement to calculate a cement index. The cement penetration ratios observed in cross-sections at the same level and the cement index were significantly greater with the use of the cement gun than with the use of the syringe. There was no difference in the number of slices that contained cement. The use of a cement gun with a narrow nozzle improved cement mantle characteristics compared with the use of a syringe when measured in a cadaveric model in the absence of canal occlusion. Improving cement mantle characteristics may decrease the incidence of aseptic loosening after total elbow arythroplasty. Copyright © 2015 American Society for Surgery of the Hand. Published by Elsevier Inc. All rights reserved.

Effect of temporary cements on the shear bond strength of luting cements

PubMed Central

FIORI-JÚNIOR, Marco; MATSUMOTO, Wilson; SILVA, Raquel Assed Bezerra; PORTO-NETO, Sizenando Toledo; SILVA, Jaciara Miranda Gomes

2010-01-01

Objective The purpose of this study was to evaluate, by shear bond strength (SBS) testing, the influence of different types of temporary cements on the final cementation using conventional and self-etching resin-based luting cements. Material and Methods Forty human teeth divided in two halves were assigned to 8 groups (n=10): I and V (no temporary cementation); II and VI: Ca(OH)2-based cement; III and VII: zinc oxide (ZO)based cement; IV and VIII: ZO-eugenol (ZOE)-based cement. Final cementation was done with RelyX ARC cement (groups I to IV) and RelyX Unicem cement (groups V to VIII). Data were analyzed statistically by ANOVA and Tukey's test at 5% significance level. Results Means were (MPa): I - 3.80 (±1.481); II - 5.24 (±2.297); III - 6.98 (±1.885); IV - 6.54 (±1.459); V - 5.22 (±2.465); VI - 4.48 (±1.705); VII - 6.29 (±2.280); VIII - 2.47 (±2.076). Comparison of the groups that had the same temporary cementation (Groups II and VI; III and VII; IV and VIII) showed statistically significant difference (p<0.001) only between Groups IV and VIII, in which ZOE-based cements were used. The use of either Ca(OH)2 based (Groups II and VI) or ZO-based (Groups III and VII) cements showed no statistically significant difference (p>0.05) for the different luting cements (RelyXTM ARC and RelyXTM Unicem). The groups that had no temporary cementation (Groups I and V) did not differ significantly from each other either (p>0.05). Conclusion When temporary cementation was done with ZO- or ZOE-based cements and final cementation was done with RelyX ARC, there was an increase in the SBS compared to the control. In the groups cemented with RelyX Unicem, however, the use of a ZOE-based temporary cement affected negatively the SBS of the luting agent used for final cementation. PMID:20379679

Luminescence in Ba2 Sr2 Al2 O7 :RE (RE = Tb(3) (+) ,Eu(3) (+) and Dy(3) (+) ) novel aluminate phosphors.

PubMed

Pardhi, S A; Panse, V R; Dhoble, S J

2016-09-01

The luminescence of novel rare earth (Tb(3) (+) , Eu(3) (+) and Dy(3) (+) )-activated Ba2 Sr2 Al2 O7 phosphors for solid-state lighting is presented. The aluminate phosphors were synthesized using a one-step combustion method. X-Ray diffraction, scanning electron microscopy and photoluminescence characterizations were performed to understand the mechanism of excitation and the corresponding emission in the as-prepared phosphor, as characterized the phase purity and microstructure. Improvements in the luminescence properties of the phosphors with rare earth concentration were observed. The phosphor hue could be tuned from blue, green and red by proper selection of rare earth ions in typical concentrations. Effective absorption in the near-ultraviolet region was observed, which makes the phosphor a potential candidate for ultraviolet light-emitting diodes. Copyright © 2016 John Wiley & Sons, Ltd. Copyright © 2016 John Wiley & Sons, Ltd.

Life Model of Hollow Cathodes Using a Barium Calcium Aluminate Impregnated Tungsten Emitter

NASA Technical Reports Server (NTRS)

Kovaleski, S. D.; Burke, Tom (Technical Monitor)

2001-01-01

Hollow cathodes with barium calcium aluminate impregnated tungsten emitters for thermionic emission are widely used in electric propulsion. These high current, low power cathodes are employed in ion thrusters, Hall thrusters, and on the International Space Station in plasma contactors. The requirements on hollow cathode life are growing more stringent with the increasing use of electric propulsion technology. The life limiting mechanism that determines the entitlement lifetime of a barium impregnated thermionic emission cathode is the evolution and transport of barium away from the emitter surface. A model is being developed to study the process of barium transport and loss from the emitter insert in hollow cathodes. The model accounts for the production of barium through analysis of the relevant impregnate chemistry. Transport of barium through the approximately static gas is also being treated. Finally, the effect of temperature gradients within the cathode are considered.

Chlordetect: Commercial Calcium Aluminate Based Conductimetric Sensor for Chloride Presence Detection

PubMed Central

Torres-Luque, Magda; Sánchez-Silva, Mauricio

2017-01-01

Chloride presence affects different environments (soil, water, concrete) decreasing their qualities. In order to assess chloride concentration this paper proposes a novel sensor for detecting and measuring it. This sensor is based on electric changes of commercial monocalcium aluminate (CA) when it interacts with chloride aqueous solutions. CA is used as a dielectric material between two coplanar capacitors. The geometry proposed for this sensor allows to assess the chloride content profile, or to make four times the same measurement. Besides, the experimental design gives us the possibility of study not just the chloride effect, but also the time and some geometric effects due to the sensor design. As a result, this sensor shows a limit of detection, sensitivity, and response time: 0.01 wt % Cl− and 0.06 wt % Cl−, and 2 min, respectively, comparable with other non invasive techniques as optical fibre sensors. PMID:28902147

A general strategy for the ultrafast surface modification of metals

PubMed Central

Shen, Mingli; Zhu, Shenglong; Wang, Fuhui

2016-01-01

Surface modification is an essential step in engineering materials that can withstand the increasingly aggressive environments encountered in various modern energy-conversion systems and chemical processing industries. However, most traditional technologies exhibit disadvantages such as slow diffusion kinetics, processing difficulties or compatibility issues. Here, we present a general strategy for the ultrafast surface modification of metals inspired by electromigration, using aluminizing austenitic stainless steel as an example. Our strategy facilitates the rapid formation of a favourable ductile surface layer composed of FeCrAl or β-FeAl within only 10 min compared with several hours in conventional processes. This result indicates that electromigration can be used to achieve the ultrafast surface modification of metals and can overcome the limitations of traditional technologies. This strategy could be used to aluminize ultra-supercritical steam tubing to withstand aggressive oxidizing environments. PMID:27924909

Base catalysed isomerisation of aldoses of the arabino and lyxo series in the presence of aluminate.

PubMed

Ekeberg, Dag; Morgenlie, Svein; Stenstrøm, Yngve

2002-04-30

Base-catalysed isomerisation of aldoses of the arabino and lyxo series in aluminate solution has been investigated. L-Arabinose and D-galactose give L-erythro-2-pentulose (L-ribulose) and D-lyxo-2-hexulose (D-tagatose), respectively, in good yields, whereas lower reactivity is observed for 6-deoxy-D-galactose (D-fucose). From D-lyxose, D-mannose and 6-deoxy-L-mannose (L-rhamnose) are obtained mixtures of ketoses and C-2 epimeric aldoses. Small amounts of the 3-epimers of the ketoses were also formed. 6-Deoxy-L-arabino-2-hexulose (6-deoxy-L-fructose) and 6-deoxy-L-glucose (L-quinovose) were formed in low yields from 6-deoxy-L-mannose and isolated as their O-isopropylidene derivatives. Explanations of the differences in reactivity and course of the reaction have been suggested on the basis of steric effects.

Immobilization of LiCl-Li2O pyroprocessing salt wastes in chlorosodalite using glass-bonded hydrothermal and salt-occlusion methods

NASA Astrophysics Data System (ADS)

Riley, Brian J.; Peterson, Jacob A.; Kroll, Jared O.; Frank, Steven M.

2018-04-01

In this study, hydrothermal and salt-occlusion processes were used to make chlorosodalite through reactions with a high-LiCl salt simulating a waste stream generated from pyrochemical treatment of oxide-based used nuclear fuel. Some products were reacted with glass binders to increase chlorosodalite yield through alkali ion exchange and to aid in densification. Hydrothermal processes included reaction of the salt simulant in an autoclave with either zeolite 4A or sodium aluminate and colloidal silica. Chlorosodalite yields in the crystalline products were nearly complete in the glass-bonded materials at values of 100 mass% for the salt-occlusion method, up to 99.0 mass% for the hydrothermal synthesis with zeolite 4A, and up to 96 mass% for the hydrothermal synthesis with sodium aluminate and colloidal silica. These results show promise for using chemically stable chlorosodalite to immobilize oxide reduction salt wastes.

Evaluating the use of electronegativity in band alignment models through the experimental slope parameter of lanthanum aluminate heterostructures

DOE Office of Scientific and Technical Information (OSTI.GOV)

Liu, Z. Q.; Chim, W. K.; Chiam, S. Y

2011-11-01

In this work, photoelectron spectroscopy is used to characterize the band alignment of lanthanum aluminate heterostructures which possess a wide range of potential applications. It is found that our experimental slope parameter agrees with theory using the metal-induced gap states model while the interface induced gap states (IFIGS) model yields unsatisfactory results. We show that this discrepancy can be attributed to the correlation between the dielectric work function and the electronegativity in the IFIGS model. It is found that the original trend, as established largely by metals, may not be accurate for larger band gap materials. By using a newmore » correlation, our experimental data shows good agreement of the slope parameter using the IFIGS model. This correlation, therefore, plays a crucial role in heterostructures involving wider bandgap materials for accurate band alignment prediction using the IFIGS model.« less

Researches concerning influence of magnesium, aluminum and titanium lime on steel desulfurization

NASA Astrophysics Data System (ADS)

Putan, V.; Putan, A.; Josan, A.; Vilceanu, L.

2016-02-01

The paper presents the results of laboratory experiments on steel desulphurisation with slag from the system MgO-Al2O3-TiO2. To determine the influence, on the desulphurisation process, of the titanium oxide added in calcium aluminate slag, we experimented, in the laboratory phase, the steel treatment with a mechanical mixture consisting of lime, aluminous slag and slag obtained from the titanium making process through the aluminothermic technology. The steel melting was carried out in an induction furnace of 10 kg capacity, existent in the "Metallic Melts" laboratory of the Engineering Faculty of Hunedoara. During the research, we aimed to establish correlation equations between the sulphur distribution coefficient and the slag components (MgO, Al2O3, TiO2). The data obtained in the experiments were processed in MATLAB programs, resulting multiple correlation equations, which allowed the elucidation of some physical-chemical phenomena specific to the desulphurisation processes.

Synthesis, Microstructure and Properties of Nickel Aluminide Foams

NASA Technical Reports Server (NTRS)

Dunand, David C.

2003-01-01

Two Ph.D. students were involved in the project: Mr. Christopher Schuh (part-time, graduated in Spring 2001) and Ms. Andrea Hodge (full-time, graduated Summer 2002). One post-doctoral fellow, Dr. Heeman Choe, worked full-time on the project from July to December 2002. A new process to aluminize and chromize nickel foams was created. A kinetic aluminization model was developed. Creep testing was conducted on the foams. A finite-element model and a simplified analytical model for foam creep were produced. Four articles were written: one is published, two are accepted for publication, and one is in preparation. Ms. Hodge spent four months at NASA Glenn Research Center (9-12/2001 and 2-3/2002) under the supervision of Dr. Nathal. She conducted research on NiAl foam fabrication, mechanical testing and numerical modeling. She gave a talk at the ASM annual conference in November 2001 and presented her results at NASA in December 2001.

Meteoric calcite cementation: diagenetic response to relative fall in sea-level and effect on porosity and permeability, Las Negras area, southeastern Spain

NASA Astrophysics Data System (ADS)

Li, Zhaoqi; Goldstein, Robert H.; Franseen, Evan K.

2017-03-01

A dolomitized Upper Miocene carbonate system in southeast Spain contains extensive upper and lower zones of calcite cementation that cut across the stratigraphy. Cement textures including isopachous and circumgranular, which are consistent with phreatic-zone cementation. Cements in the upper cemented zone are non-luminescent, whereas those in the lower cemented zone exhibit multiple bands of luminescent and non-luminescent cements. In the upper cemented zone, isotopic data show two meteoric calcite lines (MCL) with mean δ18O at - 5.1‰ and - 5.8‰ VPDB, whereas no clear MCL is defined in the lower cemented zone where mean δ18O for calcite cement is at - 6.7‰ VPDB. δ13C values in both cement zones are predominantly negative, ranging from - 10 to + 2‰ VPDB, suggestive of carbon from soil gas or decayed organics. Measurements of Tm ice in primary fluid inclusions yield a mode of 0.0 °C in both zones, indicating calcite cementation from fresh water. These two zones define the positions of two different paleo-water tables that formed during a relative sea-level fall and erosional downcutting during the Plio-Pleistocene. The upper cemented zone pre-dated the lower cemented zone on the basis of known relative sea-level history. Meteoric calcite cementation reduced porosity and permeability, but measured values are inconsistent with simple filling of open pore space. Each texture, boundstone, grainstone, packstone, wackestone, produces a different relationship between percent calcite cement and porosity/permeability. Distribution of cements may be predictable on the basis of known sea-level history, and the effect of the cementation can be incorporated into subsurface geomodels by defining surfaces of rock boundaries that separate cemented zones from uncemented zones, and applying texture-specific relationships among cementation, porosity and permeability.

Traction test of temporary dental cements.

PubMed

Román-Rodríguez, Juan-Luis; Millan-Martínez, Diego; Fons-Font, Antonio; Agustín-Panadero, Rubén; Fernández-Estevan, Lucía

2017-04-01

Classic self-curing temporary cements obstruct the translucence of provisional restorations. New dual-cure esthetic temporary cements need investigation and comparison with classic cements to ensure that they are equally retentive and provide adequate translucence. The objective is to analyze by means of traction testing in a in vitro study the retention of five temporary cements. Ten molars were prepared and ten provisional resin restorations were fabricated using CAD-CAM technology (n=10). Five temporary cements were selected: self-curing temporary cements, Dycal (D), Temp Bond (TB), Temp Bond Non Eugenol (TBNE); dual-curing esthetic cements Temp Bond Clear (TBC) and Telio CS link (TE). Each sample underwent traction testing, both with thermocycling (190 cycles at 5-55º) and without thermocycling. TE and TBC obtained the highest traction resistance values. Thermocycling reduced the resistance of all cements except TBC. The dual-cure esthetic cements tested provided optimum outcomes for bonding provisional restorations. Key words: Temporary dental cements, cements resistance.

High Early-Age Strength Concrete for Rapid Repair

NASA Astrophysics Data System (ADS)

Maler, Matthew O.

The aim of this research was to identify High Early-Age Strength (HES) concrete batch designs, and evaluate their suitability for use in the rapid repair of highways and bridge decks. To this end, two criteria needed to be met; a minimum compressive strength of 20.68 MPa (3000 psi) in no later than 12 hours, and a drying shrinkage of less than 0.06 % at 28 days after curing. The evaluations included both air-entrained, and non-air-entrained concretes. The cement types chosen for this study included Type III and Type V Portland cement and "Rapid Set"--a Calcium Sulfoaluminate (CSA) cement. In addition, two blended concretes containing different ratios of Type V Portland cement and CSA cement were investigated. The evaluation of the studied concretes included mechanical properties and transport properties. Additionally, dimensional stability and durability were investigated. Evaluations were conducted based on cement type and common cement factor. Fresh property tests showed that in order to provide a comparable workability, and still remain within manufactures guideline for plasticizer, the water-to-cement ratio was adjusted for each type of cement utilized. This resulted in the need to increase the water-to-cement ratio as the Blaine Fineness of the cement type increased (0.275 for Type V Portland cement, 0.35 for Type III Portland cement, and 0.4 for Rapid Set cement). It was also observed that negligible changes in setting time occurred with increasing cement content, whereas changes in cement type produced notable differences. The addition of air-entrainment had beneficial effect on workability for the lower cement factors. Increasing trends for peak hydration heat were seen with increases in cement factor, cement Blaine Fineness, and accelerator dosage. Evaluation of hardened properties revealed opening times as low as 5 hours for Type V Portland cement with 2.0 % accelerator per cement weight and further reduction in opening time by an hour when accelerator dosage was increased to 2.8 % by cement weight. When Type III Portland cement and Rapid Set cement were used, the opening time reduced to as low as 4.5 hours and 1 hour, respectively. The results for Type V Portland cement concretes showed that as cement factor increased so did mechanical properties until the cement factor exceeded 504 kg/m3 (850 lb/yd3), at which point the peak heat of hydration exceeded 46.1 °C (115 °F) and the mechanical properties decreased. Other evaluations on the studied High Early-Age Strength Type V Portland cement concretes revealed increases in absorption, rapid chloride penetration, water permeability, drying shrinkage, corrosion resistance, and resistance to wear with increases in cement content. The addition of air-entrainment had adverse effects on compressive strength, absorption, and rapid chloride migration; while showing lower values for rapid chloride penetration. Curing had positive effects on all hardened properties of the studied HES concretes containing Type V cement. When examining the studied Type III Portland cement concretes, it was seen that an increase in cement content led to decreases in mechanical properties. It is noted that the peak heat of hydration for these concrete exceeded the threshold of 46.1 °C (115 °F). In addition, increases in cement factor also resulted in decreases in rapid chloride migration, frost resistance and resistance to wear. Increases in cement content resulted in increases in absorption, rapid chloride penetration, water permeability, drying shrinkage, and corrosion resistance. The use of air-entrainment imparted decreases in compressive strength and rapid chloride penetration, increases in absorption, and negligible effects on rapid chloride migration. Extending curing period resulted in beneficial effects on all properties of the studied Type III cement concretes. The studied CSA cement concretes had slightly decreasing strength trends as cement content was increased. Concretes containing CSA cement produced the lowest opening time (one hour) and the highest peak hydration heats of all concretes studied. While its corrosion and frost resistance reduced as cement content increased, the absorption and rapid chloride penetration increased with increasing cement content. For drying shrinkage, opening time curing showed more volume change with increasing cement content, whereas extending curing to 24 hours and 28 days resulted in reduction of drying shrinkage. Increasing cement factor had minimal effects on water permeability and abrasion resistance. Air-entrainments reduced compressive strength, but increased absorption and rapid chloride penetration. Rapid chloride migration was found to be incompatible with CSA cements concretes. All hardened properties of the studied CSA cement concretes improved once curing age was extended to 24 hours and 28 days. (Abstract shortened by ProQuest.).

Synthesis of Portland cement and calcium sulfoaluminate-belite cement for sustainable development and performance

NASA Astrophysics Data System (ADS)

Chen, Irvin Allen

Portland cement concrete, the most widely used manufactured material in the world, is made primarily from water, mineral aggregates, and portland cement. The production of portland cement is energy intensive, accounting for 2% of primary energy consumption and 5% of industrial energy consumption globally. Moreover, portland cement manufacturing contributes significantly to greenhouse gases and accounts for 5% of the global CO2 emissions resulting from human activity. The primary objective of this research was to explore methods of reducing the environmental impact of cement production while maintaining or improving current performance standards. Two approaches were taken, (1) incorporation of waste materials in portland cement synthesis, and (2) optimization of an alternative environmental friendly binder, calcium sulfoaluminate-belite cement. These approaches can lead to less energy consumption, less emission of CO2, and more reuse of industrial waste materials for cement manufacturing. In the portland cement part of the research, portland cement clinkers conforming to the compositional specifications in ASTM C 150 for Type I cement were successfully synthesized from reagent-grade chemicals with 0% to 40% fly ash and 0% to 60% slag incorporation (with 10% intervals), 72.5% limestone with 27.5% fly ash, and 65% limestone with 35% slag. The synthesized portland cements had similar early-age hydration behavior to commercial portland cement. However, waste materials significantly affected cement phase formation. The C3S--C2S ratio decreased with increasing amounts of waste materials incorporated. These differences could have implications on proportioning of raw materials for cement production when using waste materials. In the calcium sulfoaluminate-belite cement part of the research, three calcium sulfoaluminate-belite cement clinkers with a range of phase compositions were successfully synthesized from reagent-grade chemicals. The synthesized calcium sulfoaluminate-belite cement that contained medium C4A3 S¯ and C2S contents showed good dimensional stability, sulfate resistance, and compressive strength development and was considered the optimum phase composition for calcium sulfoaluminate-belite cement in terms of comparable performance characteristics to portland cement. Furthermore, two calcium sulfoaluminate-belite cement clinkers were successfully synthesized from natural and waste materials such as limestone, bauxite, flue gas desulfurization sludge, Class C fly ash, and fluidized bed ash proportioned to the optimum calcium sulfoaluminate-belite cement synthesized from reagent-grade chemicals. Waste materials composed 30% and 41% of the raw ingredients. The two calcium sulfoaluminate-belite cements synthesized from natural and waste materials showed good dimensional stability, sulfate resistance, and compressive strength development, comparable to commercial portland cement.

Comparative study on strength properties of cement mortar by partial replacement of cement with ceramic powder and silica fume

NASA Astrophysics Data System (ADS)

Himabindu, Ch.; Geethasri, Ch.; Hari, N.

2018-05-01

Cement mortar is a mixture of cement and sand. Usage of high amount of cement increases the consumption of natural resources and electric power. To overcome this problem we need to replace cement with some other material. Cement is replaced with many other materials like ceramic powder, silica fume, fly ash, granulated blast furnace slag, metakaolin etc.. In this research cement is replaced with ceramic powder and silica fume. Different combinations of ceramic powder and silica fume in cement were replaced. Cement mortar cubes of 1:3 grade were prepared. These cubes were cured under normal water for 7 days, 14days and 28 days. Compressive strength test was conducted for all mixes of cement mortar cubes.

Effect of dental cements on peri-implant microbial community: comparison of the microbial communities inhabiting the peri-implant tissue when using different luting cements.

PubMed

Korsch, Michael; Marten, Silke-Mareike; Dötsch, Andreas; Jáuregui, Ruy; Pieper, Dietmar H; Obst, Ursula

2016-12-01

Cementing dental restorations on implants poses the risk of undetected excess cement. Such cement remnants may favor the development of inflammation in the peri-implant tissue. The effect of excess cement on the bacterial community is not yet known. The aim of this study was to analyze the effect of two different dental cements on the composition of the microbial peri-implant community. In a cohort of 38 patients, samples of the peri-implant tissue were taken with paper points from one implant per patient. In 15 patients, the suprastructure had been cemented with a zinc oxide-eugenol cement (Temp Bond, TB) and in 23 patients with a methacrylate cement (Premier Implant Cement, PIC). The excess cement found as well as suppuration was documented. Subgingival samples of all patients were analyzed for taxonomic composition by means of 16S amplicon sequencing. None of the TB-cemented implants had excess cement or suppuration. In 14 (61%) of the PIC, excess cement was found. Suppuration was detected in 33% of the PIC implants without excess cement and in 100% of the PIC implants with excess cement. The taxonomic analysis of the microbial samples revealed an accumulation of oral pathogens in the PIC patients independent of the presence of excess cement. Significantly fewer oral pathogens occurred in patients with TB compared to patients with PIC. Compared with TB, PIC favors the development of suppuration and the growth of periodontal pathogens. © 2015 John Wiley & Sons A/S. Published by John Wiley & Sons Ltd.

Comparison of the Solubility of Conventional Luting Cements with that of the Polyacid Modified Composite Luting Cement and Resin-modified Glass lonomer Cement.

PubMed

Karkera, Reshma; Raj, A P Nirmal; Isaac, Lijo; Mustafa, Mohammed; Reddy, R Naveen; Thomas, Mathew

2016-12-01

This study was planned to find the solubility of the conventional luting cements in comparison with that of the polyacid-modified composite luting cement and recently introduced resin-modified glass ionomer cement (RMGIC) with exposure to water at early stages of mixing. An in vitro study of the solubility of the following five commercially available luting cements, viz., glass ionomer cement (GIC) (Fuji I, GC), zinc phosphate (Elite 100, GC), polyacid-modified resin cement (PMCR) (Principle, Dentsply), polycarboxylate cement (PC) (Poly - F, Dentsply), RMGIC (Vitremer, 3M), was conducted. For each of these groups of cements, three resin holders were prepared containing two circular cavities of 5 mm diameter and 2 mm depth. All the cements to be studied were mixed in 30 seconds and then placed in the prepared cavities in the resin cement holder for 30 seconds. From all of the observed luting cements, PMCR cement had shown the lowest mean loss of substance at all immersion times and RMGIC showed the highest mean loss of substanceat all immersion times in water from 2 to 8 minutes. The solubility of cements decreased by 38% for GIC, 33% for ZnPO 4 , 50% for PMCR, 29% for PC, and 17% for RMGIC. The PMCR cement (Principle-Dentsply) had shown lowest solubility to water at the given time intervals of immersion. This was followed by PC, zinc phosphate, and GIC to various time intervals of immersion.

Development of high-performance blended cements

NASA Astrophysics Data System (ADS)

Wu, Zichao

2000-10-01

This thesis presents the development of high-performance blended cements from industrial by-products. To overcome the low-early strength of blended cements, several chemicals were studied as the activators for cement hydration. Sodium sulfate was discovered as the best activator. The blending proportions were optimized by Taguchi experimental design. The optimized blended cements containing up to 80% fly ash performed better than Type I cement in strength development and durability. Maintaining a constant cement content, concrete produced from the optimized blended cements had equal or higher strength and higher durability than that produced from Type I cement alone. The key for the activation mechanism was the reaction between added SO4 2- and Ca2+ dissolved from cement hydration products.

Calcium phosphate compatible bone cement: Characterization, bonding properties and tissue response

NASA Astrophysics Data System (ADS)

Roemhildt, Maria Lynn

A novel, inorganic, bone cement, containing calcium phosphate, developed for implant fixation was evaluated. Setting properties were determined over a range of temperatures. The flow of the cement was greatly increased by application of vibration. Changes in the cement during hydration and aging were evaluated. Compressive strength of the cement over time was studied under simulated physiological conditions from 1 hour to 1 year after setting. After 1 day, this cement had equivalent compressive strength to commercially used PMMA cement. The strength was found to increase over 1 month and high strength was maintained up to 1 year. The shear strength of the cement-metal interface was studied in vitro using a pull-out test. Prepared specimens were stored under physiological conditions and tested at 4 hours, 24 hours, and 60 days. Comparable interfacial shear strength values were found at 4 hours, 24 hours and 60 days for the experimental cement and were not significantly different from values obtained for PMMA cement. In vivo tissue response was evaluated after cement implantation in the femoral medullary canal in canines. Tissue response and bonding at the cement-bone interface were evaluated at 2, 6, and 12 weeks. Cortical bone was found in direct contact with the OC-cement and was healthy. The strength of the cement-bone interface, measured using a push-out test, was significantly higher for the experimental cement than for commercial PMMA bone cement.

Peri-Implantitis Associated with Type of Cement: A Retrospective Analysis of Different Types of Cement and Their Clinical Correlation to the Peri-Implant Tissue.

PubMed

Korsch, Michael; Walther, Winfried

2015-10-01

The cementation of fixed implant-supported dental restorations involves the risk of leaving excess cement in the mouth which can promote biofilm formation in the peri-implant sulcus. As a result, an inflammation may develop. The aim of the present study was to investigate the clinical effect of two different luting cements on the peri-implant tissue. Within the scope of a retrospective clinical follow-up study, the prosthetic structures of 22 patients with 45 implants were revised. In all cases, a methacrylate cement (Premier Implant Cement [PIC], Premier® Dental Products Company, Plymouth Meeting, PA, USA) had been used for cementation. In 16 additional patients with 28 implants, the suprastructures were retained with a zinc oxide-eugenol cement (Temp Bond [TB], Kerr Sybron Dental Specialities, Glendora, CA, USA). These patients were evaluated in the course of routine treatment. In both populations, the retention time of the suprastructures was similar (TB 3.77 years, PIC 4.07 years). In the PIC cases, 62% of all implants had excess cement. In the TB cases, excess cement was not detectable on any of the implants. Bleeding on probing was significantly more frequent on implants cemented with PIC (100% with and 94% without excess cement) than on implants cemented with TB (46%). Pocket suppuration was observed on 89% of the PIC-cemented implants with excess cement (PIC without excess cement 24%), whereas implants with TB were not affected by it at all. The peri-implant bone loss was significantly greater in the PIC patients (with excess cement 1.37 mm, without excess cement 0.41 mm) than it was in the TB patients (0.07 mm). The frequency of undetected excess cement depends essentially on the type of cement used. Cements that tend to leave more undetected excess have a higher prevalence for peri-implant inflammation and cause a more severe peri-implant bone loss. © 2014 Wiley Periodicals, Inc.

In vitro bond strength and fatigue stress test evaluation of different adhesive cements used for fixed space maintainer cementation

PubMed Central

Cantekin, Kenan; Delikan, Ebru; Cetin, Secil

2014-01-01

Objective: The purposes of this research were to (1) compare the shear-peel bond strength (SPBS) of a band of a fixed space maintainer (SM) cemented with five different adhesive cements; and (2) compare the survival time of bands of SM with each cement type after simulating mechanical fatigue stress. Materials and Methods: Seventy-five teeth were used to assess retentive strength and another 50 teeth were used to assess the fatigue survival time. SPBS was determined with a universal testing machine. Fatigue testing was conducted in a ball mill device. Results: The mean survival time of bands cemented with R & D series Nova Glass-LC (6.2 h), Transbond Plus (6.7 h), and R & D series Nova Resin (6.8 h) was significantly longer than for bands cemented with Ketac-Cem (5.4 h) and GC Equia (5.2 h) (P < 0.05). Conclusion: Although traditional glass ionomer cement (GIC) cement presented higher retentive strength than resin-based cements (resin, resin modified GIC, and compomer cement), resin based cements, especially dual cure resin cement (nova resin cement) and compomer (Transbond Plus), can be expected to have lower failure rates for band cementation than GIC (Ketac-Cem) in the light of the results of the ball mill test. PMID:25202209

Influence of temporary cement contamination on the surface free energy and dentine bond strength of self-adhesive cements.

PubMed

Takimoto, Masayuki; Ishii, Ryo; Iino, Masayoshi; Shimizu, Yusuke; Tsujimoto, Akimasa; Takamizawa, Toshiki; Ando, Susumu; Miyazaki, Masashi

2012-02-01

The surface free energy and dentine bond strength of self-adhesive cements were examined after the removal of temporary cements. The labial dentine surfaces of bovine mandibular incisors were wet ground with #600-grit SiC paper. Acrylic resin blocks were luted to the prepared dentine surfaces using HY Bond Temporary Cement Hard (HY), IP Temp Cement (IP), Fuji TEMP (FT) or Freegenol Temporary Cement (TC), and stored for 1 week. After removal of the temporary cements with an ultrasonic tip, the contact angle values of five specimens per test group were determined for the three test liquids, and the surface-energy parameters of the dentine surfaces were calculated. The dentine bond strengths of the self-adhesive cements were measured after removal of the temporary cements in a shear mode at a crosshead speed of 1.0mm/min. The data were subjected to one-way analysis of variance (ANOVA) followed by Tukey's HSD test. For all surfaces, the value of the estimated surface tension component γ(S)(d) (dispersion) was relatively constant at 41.7-43.3 mJm(-2). After removal of the temporary cements, the value of the γ(S)(h) (hydrogen-bonding) component decreased, particularly with FT and TC. The dentine bond strength of the self-adhesive cements was significantly higher for those without temporary cement contamination (8.2-10.6 MPa) than for those with temporary cement contamination (4.3-7.1 MPa). The γ(S) values decreased due to the decrease of γ(S)(h) values for the temporary cement-contaminated dentine. Contamination with temporary cements led to lower dentine bond strength. The presence of temporary cement interferes with the bonding performance of self-adhesive cements to dentine. Care should be taken in the methods of removal of temporary cement when using self-adhesive cements. Copyright © 2011 Elsevier Ltd. All rights reserved.

Wear Resistance Enhancement of Ti-6Al-4 V Alloy by Applying Zr-Modified Silicide Coatings

NASA Astrophysics Data System (ADS)

Li, Xuan; Hu, Guangzhong; Tian, Jin; Tian, Wei; Xie, Wenling; Li, Xiulan

2018-03-01

Zr-modified silicide coatings were prepared on Ti-6Al-4 V alloy by pack cementation process to enhance its wear resistance. The microstructure and wear properties of the substrate and the coatings were comparatively investigated using GCr15 and Al2O3 as the counterparts under different sliding loads. The obtained Zr-modified silicide coating had a multilayer structure, consisting of a thick (Ti, X)Si2 (X represents Al, Zr and V elements) outer layer, a TiSi middle layer and a Ti5Si4 + Ti5Si3 inner layer. The micro-hardness of the coating was much higher than the substrate and displayed a decrease tendency from the coating surface to the interior. Sliding against either GCr15 or Al2O3 balls, the coatings showed superior anti-friction property to the Ti-6Al-4 V alloy, as confirmed by its much lower wear rate under each employed sliding condition.

Formation mechanism of a silicon carbide coating for a reinforced carbon-carbon composite

NASA Technical Reports Server (NTRS)

Rogers, D. C.; Shuford, D. M.; Mueller, J. I.

1975-01-01

Results are presented for a study to determine the mechanisms involved in a high-temperature pack cementation process which provides a silicon carbide coating on a carbon-carbon composite. The process and materials used are physically and chemically analyzed. Possible reactions are evaluated using the results of these analytical data. The coating is believed to develop in two stages. The first is a liquid controlled phase process in which silicon carbide is formed due to reactions between molten silicon metal and the carbon. The second stage is a vapor transport controlled reaction in which silicon vapors react with the carbon. There is very little volume change associated with the coating process. The original thickness changes by less than 0.7%. This indicates that the coating process is one of reactive penetration. The coating thickness can be increased or decreased by varying the furnace cycle process time and/or temperature to provide a wide range of coating thicknesses.

Coatings for directional eutectics

NASA Technical Reports Server (NTRS)

Rairden, J. R.; Jackson, M. R.

1976-01-01

Coatings developed to provide oxidation protection for the directionally-solidified eutectic alloy NiTaC-B (4.4 weight percent Cr) were evaluated. Of seven Co-, Fe- and Ni-base coatings that were initially investigated, best resistance to cyclic oxidation was demonstrated by duplex coatings fabricated by depositing a layer of NiCrAl(Y) by vacuum evaporation from an electron beam source followed by deposition of an Al overlayer using the pack cementation process. It was found that addition of carbon to the coating alloy substantially eliminated the problem of fiber denudation in TaC-type eutectic alloys. Burner rig cycled NiTaC-B samples coated with Ni-20Cr-5Al-0.1C-0.1Y+Al and rupture-tested at 1100 deg C performed as well as or better than uncoated, vacuum cycled and air-tested NiTaC-13; however, a slight degradation with respect to uncoated material was noted in air-stress rupture tests at 870 deg C for both cycled and uncycled samples.

Ranking protective coatings: Laboratory vs. field experience

NASA Astrophysics Data System (ADS)

Conner, Jeffrey A.; Connor, William B.

1994-12-01

Environmentally protective coatings are used on a wide range of gas turbine components for survival in the harsh operating conditions of engines. A host of coatings are commercially available to protect hot-section components, ranging from simple aluminides to designer metallic overlays and ceramic thermal barrier coatings. A variety of coating-application processes are available, and they range from simple pack cementation processing to complex physical vapor deposition, which requires multimillion dollar facilities. Detailed databases are available for most coatings and coating/process combinations for a range of laboratory tests. Still, the analysis of components actually used in engines often yields surprises when compared against predicted coating behavior from laboratory testing. This paper highlights recent work to develop new laboratory tests that better simulate engine environments. Comparison of in-flight coating performance as well as industrial and factory engine testing on a range of hardware is presented along with laboratory predictions from standard testing and from recently developed cyclic burner-rig testing.

Monitoring the integrity of the cement-metal interface of total joint components in vitro using acoustic emission and ultrasound.

PubMed

Davies, J P; Tse, M K; Harris, W H

1996-08-01

Debonding of the cement-metal interface of cemented femoral components of total hip arthroplasty has been shown from clinical and autopsy material to be a common occurrence. Experimentally, debonding has been shown to increase markedly the strains in the adjacent cement mantle. Studies of autopsy-retrieved specimens demonstrate that debonding of the cement-metal interface is a key initiating event in loosening of cemented femoral components of total hip arthroplasty. However, both the radiographic and autopsy evidence of cement-metal interfacial debonding exist after the fact, that is, after debonding has occurred. The lack of prospective data showing that debonding does indeed occur under physiologic loading and occurs prior to other forms of failure of fixation leaves uncertain the issue of debonding and its role in initiating loosening of cemented femoral components. Knowing when, where, and to what extent the cement-metal interface debonds is critical information in understanding the process of loosening of cemented femoral components. Such information would contribute to improving the durability of stems and improving cementing techniques. In this study, the two nondestructive techniques of acoustic emission and ultrasonic evaluation of the cement-metal interface of cemented femoral stems of total hip arthroplasty were combined to investigate when, where, and to what extent cement-metal debonding occurred in vitro in simulated femurs loaded physiologically in fatigue in simulated single-leg stance. Debonding of the cement-metal interface of a cemented femoral component in this model was both an initiating event and a major mechanism of compromise of the cement-metal interface. Additional acoustic emission signals arose from cracks that developed in the cement.

Durability Analysis of Aluminized Type 2 Corrugated Metal Pipe

DOT National Transportation Integrated Search

2000-01-01

The Literature Review and Field Studies portion of this investigation were completed by August 1995. Both revealed myriad factors affecting culvert durability. The literature review considered more than 140 research papers on or relating to the topic...

Durability Analysis of Aluminized Type 2 Corrugated Metal Pipe

DOT National Transportation Integrated Search

2000-01-01

The literature review and field studies portion of this investigation were completed by August 1995. Both revealed myriad factors affecting culvert durability. The literature review considered more than 140 research papers on or relating to the topic...

Electronic and chemical state of aluminum from the single- (K) and double-electron excitation (KL II&III, KL I) x-ray absorption near-edge spectra of α-alumina, sodium aluminate, aqueous Al³⁺•(H₂O)₆, and aqueous Al(OH)₄⁻

DOE Office of Scientific and Technical Information (OSTI.GOV)

Fulton, John L.; Govind, Niranjan; Huthwelker, Thomas

2015-07-02

We probe, at high energy resolution, the double electron excitation (KL II&II) x-ray absorption region that lies approximately 115 eV above the main Al K-edge (1566 eV) of α-alumina and sodium aluminate. The two solid standards, α-alumina (octahedral) and sodium aluminate (tetrahedral) are compared to aqueous species that have the same Al coordination symmetries, Al³⁺•6H₂O (octahedral) and Al(OH)₄⁻ (tetrahedral). For the octahedral species, the edge height of the KL II&III-edge is approximately 10% of the main K-edge however the edge height is much weaker (3% of K-edge height) for Al species with tetrahedral symmetry. For the α-alumina and aqueous Al³⁺•6H₂Omore » the KL II&III spectra contain white line features and extended absorption fine structure (EXAFS) that mimics the K-edge spectra. The KL II&III-edge feature interferes with an important region of the extended-XAFS region of the spectra for the K-edge of the crystalline and aqueous standards. The K-edge spectra and K-edge positions are predicted using time-dependent density functional theory (TDDFT). The TDDFT calculations for the K-edge XANES spectra reproduce the observed transitions in the experimental spectra of the four Al species. The KL II&III and KL I onsets and their corresponding chemical shifts for the four standards are estimated using the delta self-consistent field (ΔSCF) method. Research by JLF, NG, EJB, AV, TDS was supported by U.S. Department of Energy’s (DOE), Office of Science, Office of Basic Energy Sciences, Division of Chemical Sciences, Geosciences, and Biosciences. NG thanks Amity Andersen for help with the α-Al₂O₃ and tetrahedral sodium aluminate (NaAlO₂) clusters. All the calculations were performed using the Molecular Science Computing Capability at EMSL, a national scientific user facility sponsored by the U.S. Department of Energy’s Office of Biological and Environmental Research and located at Pacific Northwest National Laboratory (PNNL). PNNL is a multi-program national laboratory operated for DOE by Battelle under Contract # AC05-76RL01830.« less

Micro-mechanical damage of trabecular bone-cement interface under selected loading conditions: a finite element study.

PubMed

Zhang, Qing-Hang; Tozzi, Gianluca; Tong, Jie

2014-01-01

In this study, two micro finite element models of trabecular bone-cement interface developed from high resolution computed tomography (CT) images were loaded under compression and validated using the in situ experimental data. The models were then used under tension and shear to examine the load transfer between the bone and cement and the micro damage development at the bone-cement interface. In addition, one models was further modified to investigate the effect of cement penetration on the bone-cement interfacial behaviour. The simulated results show that the load transfer at the bone-cement interface occurred mainly in the bone cement partially interdigitated region, while the fully interdigitated region seemed to contribute little to the mechanical response. Consequently, cement penetration beyond a certain value would seem to be ineffective in improving the mechanical strength of trabecular bone-cement interface. Under tension and shear loading conditions, more cement failures were found in denser bones, while the cement damage is generally low under compression.

Traction test of temporary dental cements

PubMed Central

Millan-Martínez, Diego; Fons-Font, Antonio; Agustín-Panadero, Rubén; Fernández-Estevan, Lucía

2017-01-01

Background Classic self-curing temporary cements obstruct the translucence of provisional restorations. New dual-cure esthetic temporary cements need investigation and comparison with classic cements to ensure that they are equally retentive and provide adequate translucence. The objective is to analyze by means of traction testing in a in vitro study the retention of five temporary cements. Material and Methods Ten molars were prepared and ten provisional resin restorations were fabricated using CAD-CAM technology (n=10). Five temporary cements were selected: self-curing temporary cements, Dycal (D), Temp Bond (TB), Temp Bond Non Eugenol (TBNE); dual-curing esthetic cements Temp Bond Clear (TBC) and Telio CS link (TE). Each sample underwent traction testing, both with thermocycling (190 cycles at 5-55º) and without thermocycling. Results TE and TBC obtained the highest traction resistance values. Thermocycling reduced the resistance of all cements except TBC. Conclusions The dual-cure esthetic cements tested provided optimum outcomes for bonding provisional restorations. Key words:Temporary dental cements, cements resistance. PMID:28469824

Creep and fatigue behavior of a novel 2-component paste-like formulation of acrylic bone cements.

PubMed

Köster, Ulrike; Jaeger, Raimund; Bardts, Mareike; Wahnes, Christian; Büchner, Hubert; Kühn, Klaus-Dieter; Vogt, Sebastian

2013-06-01

The fatigue and creep performance of two novel acrylic bone cement formulations (one bone cement without antibiotics, one with antibiotics) was compared to the performance of clinically used bone cements (Osteopal V, Palacos R, Simplex P, SmartSet GHV, Palacos R+G and CMW1 with Gentamicin). The preparation of the novel bone cement formulations involves the mixing of two paste-like substances in a static mixer integrated into the cartridge which is used to apply the bone cement. The fatigue performance of the two novel bone cement formulations is comparable to the performance of the reference bone cements. The creep compliance of the bone cements is significantly influenced by the effects of physical ageing. The model parameters of Struik's creep law are used to compare the creep behavior of different bone cements. The novel 2-component paste-like bone cement formulations are in the group of bone cements which exhibit a higher creep resistance.

In-situ Mechanical Manipulation of Wellbore Cements as a Solution to Leaky Wells

NASA Astrophysics Data System (ADS)

Kupresan, D.; Radonjic, M.; Heathman, J.

2013-12-01

Wellbore cement provides casing support, zonal isolation, and casing protection from corrosive fluids, which are essential for wellbore integrity. Cements can undergo one or more forms of failure such as debonding at cement/formation and cement/casing interface, fracturing and defects within cement matrix. Failures and defects within cement will ultimately lead to fluids migration, resulting in inter-zonal fluid migration and premature well abandonment. There are over 27,000 abandoned oil and gas wells only in The Gulf of Mexico (some of them dating from the late 1940s) with no gas leakage monitoring. Cement degradation linked with carbon sequestration can potentially lead to contamination of fresh water aquifers with CO2. Gas leaks can particularly be observed in deviated wells used for hydraulic fracking (60% leakage rate as they age) as high pressure fracturing increases the potential for migration pathways. Experimental method utilized in this study enables formation of impermeable seals at interfaces present in a wellbore by mechanically manipulating wellbore cement. Preliminary measurements obtained in bench scale experiments demonstrate that an impermeable cement/formation and cement/casing interface can be obtained. In post-modified cement, nitrogen gas flow-through experiments showed complete zonal isolation and no permeability in samples with pre-engineered microannulus. Material characterization experiments of modified cement revealed altered microstructural properties of cement as well as changes in mineralogical composition. Calcium-silicate-hydrate (CSH), the dominant mineral in hydrated cement which provides low permeability of cement, was modified as a result of cement pore water displacement, resulting in more dense structures. Calcium hydroxide (CH), which is associated with low resistance of cement to acidic fluids and therefore detrimental in most wellbore cements, was almost completely displaced and/or integrated in CSH as a result of mechanical manipulation (shear stress). The main advantage of this methodology is that mechanical manipulation of cement can induce healing of existing fractures, channels and microannulus seal in a wellbore without introducing new materials (e.g. cement squeeze jobs). Furthermore, this methodology is less sensitive to the influence of downhole conditions such as pressure, temperature and formation fluids, since it uses cement pore water as a medium to alter cement sheath. Based on lab experiments observation, it is possible to perceive that once tested at the industrial scale and if successful, the implementation of this method in the field can potentially mitigate leaky wells in CO2 sequestration projects, wellbores completed for hydraulic-fracturing and other conventional oil and gas producing wells. Key words: Wellbore cement integrity; Leaky wells; Cement microstructures; Casing expansion effect on cement mineralogy alterations.

Increased Antibiotic Release from a Bone Cement Containing Bacterial Cellulose

PubMed Central

Nakai, Takahisa; Enomoto, Koichi; Uchio, Yuji; Yoshino, Katsumi

2010-01-01

Background Major disadvantages of antibiotic bone cements include limited drug release and reduced strength resulting from the addition of high doses of antibiotics. Bacterial cellulose, a three-dimensional hydrophilic mesh, may retain antibiotics and release them gradually. We hypothesized that the addition of cellulose to antibiotic bone cement would improve mechanical strength and antibiotic release. Questions/purposes We therefore examined the mechanical strength and antibiotic release of cellulose antibiotic cement. Methods A high dose of antibiotics (5 g per 40 g cement powder) was incorporated into bacterial cellulose and then mixed with bone cement. We compared the compression strength, fracture toughness, fatigue life, and elution kinetics of this formulation with those of plain cement and a traditional antibiotic cement. Results The average values for compression strength, fracture toughness, and fatigue life of the cellulose antibiotic cement were 97%, 97%, and 78% of the values obtained for plain cement, respectively. The corresponding values for the traditional antibiotic cement were 79%, 82%, and 17%, respectively. The cumulative elution over 35 days was 129% greater from the cellulose antibiotic cement than from the traditional antibiotic cement. Conclusions With a high dose of antibiotics, incorporating cellulose into the bone cement prevented compression and fracture fragility, improved fatigue life, and increased antibiotic elution. Clinical Relevance Antibiotic cements containing cellulose may have applications in clinical situations that require high levels of antibiotic release and preservation of the mechanical properties of the cement. PMID:20945120

Investigation of Possible Wellbore Cement Failures During Hydraulic Fracturing Operations

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kim, Jihoon; Moridis, George

2014-11-01

We model and assess the possibility of shear failure, using the Mohr-Coulomb model ? along the vertical well by employing a rigorous coupled flow-geomechanic analysis. To this end, we vary the values of cohesion between the well casing and the surrounding cement to representing different quality levels of the cementing operation (low cohesion corresponds to low-quality cement and/or incomplete cementing). The simulation results show that there is very little fracturing when the cement is of high quality.. Conversely, incomplete cementing and/or weak cement can causes significant shear failure and the evolution of long fractures/cracks along the vertical well. Specifically, lowmore » cohesion between the well and cemented areas can cause significant shear failure along the well, but the same cohesion as the cemented zone does not cause shear failure. When the hydraulic fracturing pressure is high, low cohesion of the cement can causes fast propagation of shear failure and of the resulting fracture/crack, but a high-quality cement with no weak zones exhibits limited shear failure that is concentrated near the bottom of the vertical part of the well. Thus, high-quality cement and complete cementing along the vertical well appears to be the strongest protection against shear failure of the wellbore cement and, consequently, against contamination hazards to drinking water aquifers during hydraulic fracturing operations.« less

[Pathological fractures of the femoral neck in hemodialyzed patients. Apropos of 26 cases].

PubMed

Hardy, P; Benoit, J; Donneaud, B; Jehanno, P; Lortat-Jacob, A

1994-01-01

This study is based on a retrospective analysis of 26 pathological fractures of the femoral neck in 19 chronic haemodialysis patients. The purpose of this study is to analyze the epidemiological and etiological factors of these fractures in relation to osteo-arthropathy of the dialyzed patient, as well as the results of various treatments, both curative and preventive. 26 pathological fractures of the femoral neck appeared in 19 chronic haemodialysis patients, 11 men and 8 women, 6 patients presented bilateral fractures. The patient's average age at the time of the fracture was 61 years (27 to 82). The average duration of dialysis was 11 years with a minimum of 2 years and a maximum of 21 years. Hyper parathyroidism was found in 14 patients, aluminic intoxication in 6 and amyloidosis at the level of the coxo-femoral joint 18 times. Surgical treatment consisted of 6 osteosynthesis, 2 cephalic arthroplasties, 13 modular arthroplasties and 5 total hip arthroplasties. For each case, we studied the presence of necrosis of the femoral neck due to aluminic intoxication, osteoporosis due to hyperparathyroidism and also the presence of amyloidosis without aluminic intoxication. Cortisonic necrosis and porosis was found 4 times out of 26 cases, hyperparathyroidism once, aluminic osteomalacy 3 times and beta-2-microglobulin amyloid 18 times. Amyloidosis remains the most frequent etiological factor. All patients had been operated for median nerve compression in the carpal tunnel, usually 2.5 years before appearance of the pathological fracture. Non surgical treatment was used 5 times in undisplaced fractures without any sign of amyloidosis and was successful 3 times and unsuccessful twice necessitating a new operation by osteosynthesis. Out of 6 osteosynthesis performed for fractures either with little or no displacement we observed 4 failures, all of them in the cases with intra-osseous amyloidosis. Best results were obtained by arthroplasties. Modular arthroplasty has given us 11 long term excellent results in 11 of 13 cases. The analysis of etiological factors shows two very different groups. The first one consisted of 8 fractures without coxofemoral amyloidosis. The average duration of dialysis was 5 years, average age, 44 years. Etiology was 3 times aluminic osteomalacy, once the only factor found was osteoporosis and 4 times necrosis and porosis as a complication, not of haemodialysis but of renal transplantation with concomittant corticosteroid treatment. The second group consisted of 18 fractures with hip amyloidosis in 14 patients. The average age was 63.5 years, the dialysis duration was 11.5 years, the two extremes 5 and 21 years. Etiology was beta-2-microglobulin amylosis. The pathological fracture was due to the presence of voluminous subchondral amyloidosis geodes. Amyloidosis always associated with hyperparathyroidism and aluminic intoxication in one of 3 cases. Osteosynthesis gave good results only in cases presenting no intra-osseous amyloidosis. Modular arthroplasty has allowed us to obtain excellent long term functional results with simpler outcome. Total arthroplasty should be used only for evident acetabular involvement. Amyloidosis remains the etiological factor most frequently found in pathological fractures of the femoral neck in chronic haemodialysis patients. The study of the etiological factors is essential since they will guide us in the choice of the mode or treatment. It is totally licit to propose conservative treatment for non displaced fractures without osseous amylosis. In all other cases, prosthetic replacement is necessary and osteosynthesis contra-indicated. When the acetabulum is not altered a modular arthroplasty must be used. We do not recommend preventive surgical treatment for patients having a threatening geode of the femoral neck as all osteosynthesis realized on amyloidotic bone, even without any displacement, resulted

Imaging Wellbore Cement Degradation by Carbon Dioxide under Geologic Sequestration Conditions Using X-ray Computed Microtomography

DOE Office of Scientific and Technical Information (OSTI.GOV)

Jung, Hun Bok; Jansik, Danielle; Um, Wooyong

2013-01-02

ABSTRACT: X-ray microtomography (XMT), a nondestructive three-dimensional imaging technique, was applied to demonstrate its capability to visualize the mineralogical alteration and microstructure changes in hydrated Portland cement exposed to carbon dioxide under geologic sequestration conditions. Steel coupons and basalt fragments were added to the cement paste in order to simulate cement-steel and cement-rock interfaces. XMT image analysis showed the changes of material density and porosity in the degradation front (density: 1.98 g/cm3, porosity: 40%) and the carbonated zone (density: 2.27 g/cm3, porosity: 23%) after reaction with CO2- saturated water for 5 months compared to unaltered cement (density: 2.15 g/cm3, porosity:more » 30%). Three-dimensional XMT imaging was capable of displaying spatially heterogeneous alteration in cement pores, calcium carbonate precipitation in cement cracks, and preferential cement alteration along the cement-steel and cement-rock interfaces. This result also indicates that the interface between cement and host rock or steel casing is likely more vulnerable to a CO2 attack than the cement matrix in a wellbore environment. It is shown here that XMT imaging can potentially provide a new insight into the physical and chemical degradation of wellbore cement by CO2 leakage.« less

The Influence of Cement Morphology Parameters on the Strength of the Cement-Bone Interface in Tibial Tray Fixation.

PubMed

Nagel, Katrin; Bishop, Nicholas E; Schlegel, Ulf J; Püschel, Klaus; Morlock, Michael M

2017-02-01

The strength of the cement-bone interface in tibial component fixation depends on the morphology of the cement mantle. The purpose of this study was to identify thresholds of cement morphology parameters to maximize fixation strength using a minimum amount of cement. Twenty-three cadaveric tibiae were analyzed that had been implanted with tibial trays in previous studies and for which the pull-out strength of the tray had been measured. Specimens were separated into a group failing at the cement-bone interface (INTERFACE) and one failing in the bulk bone (BULK). Maximum pull-out strength corresponds to the ultimate strength of the bulk bone if the cement-bone interface is sufficiently strong. 3D models of the cement mantle in situ were reconstructed from computed tomography scans. The influences of bone mineral density and 6 cement morphology parameters (reflecting cement penetration, bone-cement interface, cement volume) on pull-out strength of the BULK group were determined using multiple regression analysis. The threshold of each parameter for classification of the specimens into either group was determined using receiver operating characteristic analysis. Cement penetration exceeding a mean of 1.1 mm or with a maximum of 5.6 mm exclusively categorized all BULK bone failure specimens. Failure strength of BULK failure specimens increased with bone mineral density (R 2  = 0.67, P < .001) but was independent of the cement morphology parameters. To maximize fixation strength, a mean cement penetration depth of at least 1.1 mm should be achieved during tibial tray cementing. Copyright © 2016 Elsevier Inc. All rights reserved.

Comparison of microleakage of three acid-base luting cements versus one resin-bonded cement for Class V direct composite inlays.

PubMed

Piemjai, Morakot; Miyasaka, Kumiko; Iwasaki, Yasuhiko; Nakabayashi, Nobuo

2002-12-01

Demineralized dentin beneath set cement may adversely affect microleakage under fixed restorations. Microleakage of direct composite inlays cemented with acid-base cements and a methyl methacrylate resin cement were evaluated to determine their effect on the integrity of the underlying hybridized dentin. Sixty Class V box preparations (3 mm x 3 mm x 1.5 mm) were precisely prepared in previously frozen bovine teeth with one margin in enamel and another margin in dentin. Direct composite inlays (EPIC-TMPT) for each preparation were divided into 4 groups of 15 specimens each and cemented with 3 acid-base cements (control group): Elite, Ketac-Cem, Hy-Bond Carbo-Cem, and 1 adhesive resin cement: C&B Metabond. All specimens were stored in distilled water for 24 hours at 37 degrees C before immersion in 0.5% basic fuchsin for 24 hours. The dye penetration was measured on the sectioned specimens at the tooth-cement interface of enamel and cementum margins and recorded with graded criteria under light microscopy (Olympus Vanox-T) at original magnification x 50, 100, and 200. A Kruskal-Wallis and the Mann-Whitney test at P<.05 were used to analyze leakage score. All cementum margins of the 3 acid-base cements tested demonstrated significantly higher leakage scores than cementum margins for inlays cemented with the resin cement tested(P<.01). No leakage along the tooth-cement interface was found for inlays retained with the adhesive resin cement. Within the limitations of this study, the 3 acid-base cements tested exhibited greater microleakage at the cementum margins than did the adhesive resin cement that was tested.

Retention of cast crown copings cemented to implant abutments.

PubMed

Dudley, J E; Richards, L C; Abbott, J R

2008-12-01

The cementation of crowns to dental implant abutments is an accepted form of crown retention that requires consideration of the properties of available cements within the applied clinical context. Dental luting agents are exposed to a number of stressors that may reduce crown retention in vivo, not the least of which is occlusal loading. This study investigated the influence of compressive cyclic loading on the physical retention of cast crown copings cemented to implant abutments. Cast crown copings were cemented to Straumann synOcta titanium implant abutments with three different readily used and available cements. Specimens were placed in a humidifier, thermocycled and subjected to one of four quantities of compressive cyclic loading. The uniaxial tensile force required to remove the cast crown copings was then recorded. The mean retention values for crown copings cemented with Panavia-F cement were statistically significantly greater than both KetacCem and TempBond non-eugenol cements at each compressive cyclic loading quantity. KetacCem and TempBond non-eugenol cements produced relatively low mean retention values that were not statistically significantly different at each quantity of compressive cyclic loading. Compressive cyclic loading had a statistically significant effect on Panavia-F specimens alone, but increased loading quantities produced no further statistically significant difference in mean retention. Within the limitations of the current in vitro conditions employed in this study, the retention of cast crown copings cemented to Straumann synOcta implant abutments with a resin, glass ionomer and temporary cement was significantly affected by cement type but not compressive cyclic loading. Resin cement is the cement of choice for the definitive non-retrievable cementation of cast crown copings to Straumann synOcta implant abutments out of the three cements tested.

Carbon nanotube balls and their application in supercapacitors.

PubMed

Kang, Da-Young; Moon, Jun Hyuk

2014-01-08

We have provided a design of the macroscopic morphology of carbon nanotubes (CNTs) using emulsion droplet confinement. The evaporation of CNT-dispersed aqueous emulsion droplets in oil produces spherical CNT assemblies, i.e., CNT balls. In this emulsion-assisted method, compact packing of CNT was obtained by the presence of capillary pressure during droplet evaporation. The size of the CNT balls could be controlled by changing the concentration of the CNT dispersion solution; typically, CNT balls with an average size in the range of 8-12 μm were obtained with a Brunauer-Emmett-Teller (BET) specific area of 200 m(2)/g. Heat treatment of the CNT balls, which was required to remove residual solvent, and cement CNTs was followed, and their effect has been characterized; the heat treatment at high temperature desorbed surface oxygenated groups of CNTs and created defective carbon structures, but did not change pore structure. The dispersion of CNT balls was applied to form CNT ball-assembled film for a supercapacitor electrode. The specific capacitance of 80 F/g was obtained at 500 °C heat treatment, but the CNT balls prepared at a higher temperature actually decreased the capacitance, because of the removal of surface oxygenated groups, thereby decreasing the pseudo-capacitance. The capacitive properties of CNT ball-assembled electrodes were compared to CNT films; the CNT ball electrodes showed 40% higher specific electrochemical capacitance and higher rate performance, which is attributed to the compact packing of CNTs in the CNT ball and the hierarchical porous structures in the ball assemblies.

Environmentally Resistant Mo-Si-B-Based Coatings

NASA Astrophysics Data System (ADS)

Perepezko, J. H.; Sossaman, T. A.; Taylor, M.

2017-06-01

High-temperature applications have demonstrated aluminide-coated nickel-base superalloys to be remarkably effective, but are reaching their service limit. Alternate materials such as refractory (e.g., W, Mo) silicide alloys and SiC composites are being considered to extend high temperature capability, but the silica surfaces on these materials require coatings for enhanced environmental resistance. This can be accomplished with a Mo-Si-B-based coating that is deposited by a spray deposition of Mo followed by a chemical vapor deposition of Si and B by pack cementation to develop an aluminoborosilica surface. Oxidation of the as-deposited (Si + B)-pack coatings proceeds with partial consumption of the initial MoSi2 forming amorphous silica. This Si depletion leads to formation of a B-saturated Mo5Si3 (T1) phase. Reactions between the Mo and the B rich phases develop an underlying Mo5SiB2 (T2) layer. The T1 phase saturated with B has robust oxidation resistance, and the Si depletion is prevented by the underlying diffusion barrier (T2). Further, due to the natural phase transformation characteristics of the Mo-Si-B system, cracks or scratches to the outer silica and T1 layers can be repaired from the Si and B reservoirs of T2 + MoB layer to yield a self-healing characteristic. Mo-Si-B-based coatings demonstrate robust performance up to at least 1700 °C not only to the rigors of elevated temperature oxidation, but also to CMAS attack, hot corrosion attack, water vapor and thermal cycling.

Hydration products and thermokinetic properties of cement-bentonite and cement-chalk mortars

DOE Office of Scientific and Technical Information (OSTI.GOV)

Klyusov, A.A.

1988-08-20

Bentonite and chalk are the most popular auxiliary additives to portland cement for borehole cementation. The authors studied by physicochemical analysis methods (x-ray phase, derivatographic, and scanning and electron microscopy in combination with microdiffraction) the newly formed solid-phase composition of cement-bentonite and cement-chalk mortars (binder-additive ratio 9:1) prepared from portland cement for cold boreholes and 8% calcium chloride solution at a water-mixing ratio of 0.9. The mechanism of the influence of Ca-bentonite and chalk additives on the portland cement hydration rate was ascertained from the heat evolution rate curves. It was found that the phase compositions of the hydration productsmore » are represented in the studied systems by newly formed substances typical for portland cement. It has been noted that Ca-bentonite interacts with the calcium hydroxide of hydrated cement with the formation of hexagonal and cubic calcium hydroaluminates. Unlike Ca-bentonite, chalk does not react with portland cement at normal and reduced temperatures, does not block hydrated cement particles, which, in turn, ensures all other conditions remaining equal, a higher initial rate of hydration of cement-chalk mortar.« less

Influence of Cements Containing Calcareous Fly Ash as a Main Component Properties of Fresh Cement Mixtures

NASA Astrophysics Data System (ADS)

Gołaszewski, Jacek; Kostrzanowska-Siedlarz, Aleksandra; Ponikiewski, Tomasz; Miera, Patrycja

2017-10-01

The main goal of presented research was to examine usability of cements containing calcareous fly ash (W) from technological point of view. In the paper the results of tests concerning the influence of CEM II and CEM IV cements containing fly ash (W) on rheological properties, air content, setting times and plastic shrinkage of mortars are presented and discussed. Moreover, compatibility of plasticizers with cements containing fly ash (W) was also studied. Additionally, setting time and hydration heat of cements containing calcareous fly ash (W) were determined. In a broader aspect, the research contributes to promulgation of the possibility of using calcareous fly ash (W) in cement and concrete technology, what greatly benefits the environment protection (utilization of waste fly ash). Calcareous fly ash can be used successfully as the main component of cement. Cements produced by blending with processed fly ash or cements produced by interginding are characterized by acceptable technological properties. In respect to CEM I cements, cements containing calcareous fly ash worsen workability, decrease air content, delay setting time of mixtures. Cements with calcareous fly ash show good compatibility with plasticizers.

Optimization of soil stabilization with class C fly ash.

DOT National Transportation Integrated Search

1987-01-01

Previous Iowa DOT sponsored research has shown that some Class : C fly ashes are cementitious (because calcium is combined as calcium : aluminates) while other Class C ashes containing similar amounts of : elemental calcium are not (1). Fly ashes fro...

76 FR 76760 - Gray Portland Cement and Cement Clinker From Japan

Federal Register 2010, 2011, 2012, 2013, 2014

2011-12-08

... and Cement Clinker From Japan Determination On the basis of the record \\1\\ developed in the subject... duty order on gray Portland cement and cement clinker from Japan would be likely to lead to... and Cement Clinker from Japan: Investigation No. 731- TA-461 (Third Review). By order of the...

The extent of slits at the interfaces between luting cements and enamel, dentin and alloy.

PubMed

Oilo, G

1978-01-01

Four different cements were used to assess the presence of slits at the cement/tooth or the cement/alloy interfaces using a tooth-crown model. The model consisted of ground sections of teeth and plane plates of silver/palladium alloy. The plates were fixed with bolts between two brass plates and with three different dimensions of the cement film between tooth and alloy, i.e. 50 micrometer, 100 micrometer and 200 micrometer. The tooth-alloy specimens were sectioned and the adaption of cements was studied with an indirect technique (replica) in a scanning electron microscope. The extent of slits was expressed as the length of all slits relative to the total length of the interface in each specimen. The results showed that the zinc phosphate cement and polycarboxylate cement exhibited a slight to moderate tendency to formation of slits at the interfaces. The EBA cement had a small extent of slits adjacent to thin cement films, but more slits were observed with increasing film thickness. The composite resin cement had a marked tendency to slit formation independent of the cement film thickness.

In vitro tensile strength of luting cements on metallic substrate.

PubMed

Orsi, Iara A; Varoli, Fernando K; Pieroni, Carlos H P; Ferreira, Marly C C G; Borie, Eduardo

2014-01-01

The aim of this study was to determine the tensile strength of crowns cemented on metallic substrate with four different types of luting agents. Twenty human maxillary molars with similar diameters were selected and prepared to receive metallic core castings (Cu-Al). After cementation and preparation the cores were measured and the area of crown's portion was calculated. The teeth were divided into four groups based on the luting agent used to cement the crowns: zinc phosphate cement; glass ionomer cement; resin cement Rely X; and resin cement Panavia F. The teeth with the crowns cemented were subjected to thermocycling and later to the tensile strength test using universal testing machine with a load cell of 200 kgf and a crosshead speed of 0.5 mm/min. The load required to dislodge the crowns was recorded and converted to MPa/mm(2). Data were subjected to Kruskal-Wallis analysis with a significance level of 1%. Panavia F showed significantly higher retention in core casts (3.067 MPa/mm(2)), when compared with the other cements. Rely X showed a mean retention value of 1.877 MPa/mm(2) and the zinc phosphate cement with 1.155 MPa/mm(2). Glass ionomer cement (0.884 MPa/mm(2)) exhibited the lowest tensile strength value. Crowns cemented with Panavia F on cast metallic posts and cores presented higher tensile strength. The glass ionomer cement showed the lowest tensile strength among all the cements studied.

Impact of Casing Expansion on the Mechanical and Petro-Physical Properties of Wellbore Cements

NASA Astrophysics Data System (ADS)

Oyibo, A. E.

2014-12-01

The main objective of this research is to investigate the applicability of expandable casing technology as a remediation technique for leaky wells resulting in gas migration problems. Micro annulus is usually created at the cement-formation/cement-casing interface or within the cement matrix either due to poor primary cementing or as a result of activities such as temperature and pressure variation or fracturing operations. Recent reports on gas migration in hydraulically fractured wellbores, has raised concerns on the contamination of fresh water aquifers resulting from fluid migration though this flow path. A unique bench-scale physical model which utilizes expandable tubulars in the remediation of micro annular gas flow has been used to simulate expansion of a previously-cemented casing under field-like conditions. Three different designs of cement slurry: regular 16.4 lb. /gal, 16.4 lb. /gal base slurry foamed to 13 lb. /gal and 16.4 lb. /gal cement slurry with 10% salt concentration. Gas flow path (microannulus) was artificially created at the pipe-cement interface by rotating the inner pipe in a pipe inside pipe assembly with cement in the annulus within the first few hours of hydration to create debonding at the cement-casing interface. Nitrogen gas flow-through experiments were performed before and after the expansion to confirm the sealing of the microannulus. The results obtained confirmed the effectiveness of this technique in the complete closure of gas leakage path, providing seal-tight cement-formation interface free of microannulus. The manipulation of the cement sheath during the casing expansion resulted in improved porosity, permeability and the strength of the cement sheath. SEM micrographs revealed decrease in pore size and fracturing of unhydrated cement grains within the cement matrix. This technology has great potential to become one of the leading cement remediation techniques for leaks behind the casing if implemented. Keywords: Wellbore Integrity, Casing Expansion, Well Gas Leaks, CSH, Pore Collapse, Cement Pore Water.

Apatite formation on bioactive calcium-silicate cements for dentistry affects surface topography and human marrow stromal cells proliferation.

PubMed

Gandolfi, Maria Giovanna; Ciapetti, Gabriela; Taddei, Paola; Perut, Francesca; Tinti, Anna; Cardoso, Marcio Vivan; Van Meerbeek, Bart; Prati, Carlo

2010-10-01

The effect of ageing in phosphate-containing solution of bioactive calcium-silicate cements on the chemistry, morphology and topography of the surface, as well as on in vitro human marrow stromal cells viability and proliferation was investigated. A calcium-silicate cement (wTC) mainly based on dicalcium-silicate and tricalcium-silicate was prepared. Alpha-TCP was added to wTC to obtain wTC-TCP. Bismuth oxide was inserted in wTC to prepare a radiopaque cement (wTC-Bi). A commercial calcium-silicate cement (ProRoot MTA) was tested as control. Cement disks were aged in DPBS for 5 h ('fresh samples'), 14 and 28 days, and analyzed by ESEM/EDX, SEM/EDX, ATR-FTIR, micro-Raman techniques and scanning white-light interferometry. Proliferation, LDH release, ALP activity and collagen production of human marrow stromal cells (MSC) seeded for 1-28 days on the cements were evaluated. Fresh samples exposed a surface mainly composed of calcium-silicate hydrates CSH (from the hydration of belite and alite), calcium hydroxide, calcium carbonate, and ettringite. Apatite nano-spherulites rapidly precipitated on cement surfaces within 5 h. On wTC-TCP the Ca-P deposits appeared thicker than on the other cements. Aged cements showed an irregular porous calcium-phosphate (Ca-P) coating, formed by aggregated apatite spherulites with interspersed calcite crystals. All the experimental cements exerted no acute toxicity in the cell assay system and allowed cell growth. Using biochemical results, the scores were: fresh cements>aged cements for cell proliferation and ALP activity (except for wTC-Bi), whereas fresh cements

Cemented fixation with PMMA or Bis-GMA resin hydroxyapatite cement: effect of implant surface roughness.

PubMed

Walsh, W R; Svehla, M J; Russell, J; Saito, M; Nakashima, T; Gillies, R M; Bruce, W; Hori, R

2004-09-01

Implant surface roughness is an important parameter governing the overall mechanical properties at the implant-cement interface. This study investigated the influence of surface roughness using polymethylmethcrylate (PMMA) and a Bisphenol-a-glycidylmethacyrlate resin-hydroxyapatite cement (CAP). Mechanical fixation at the implant-cement interface was evaluated in vitro using static shear and fatigue loading with cobalt chrome alloy (CoCr) dowels with different surface roughness preparations. Increasing surface roughness improved the mechanical properties at the implant-cement interface for both types of cement. CAP cement fixation was superior to PMMA under static and dynamic loading.

Longevity of metal-ceramic crowns cemented with self-adhesive resin cement: a prospective clinical study

PubMed

Brondani, Lucas Pradebon; Pereira-Cenci, Tatiana; Wandsher, Vinicius Felipe; Pereira, Gabriel Kalil; Valandro, Luis Felipe; Bergoli, César Dalmolin

2017-04-10

Resin cements are often used for single crown cementation due to their physical properties. Self-adhesive resin cements gained widespread due to their simplified technique compared to regular resin cement. However, there is lacking clinical evidence about the long-term behavior of this material. The aim of this prospective clinical trial was to assess the survival rates of metal-ceramic crowns cemented with self-adhesive resin cement up to six years. One hundred and twenty-nine subjects received 152 metal-ceramic crowns. The cementation procedures were standardized and performed by previously trained operators. The crowns were assessed as to primary outcome (debonding) and FDI criteria. Statistical analysis was performed using Kaplan-Meier statistics and descriptive analysis. Three failures occurred (debonding), resulting in a 97.6% survival rate. FDI criteria assessment resulted in scores 1 and 2 (acceptable clinical evaluation) for all surviving crowns. The use of self-adhesive resin cement is a feasible alternative for metal-ceramic crowns cementation, achieving high and adequate survival rates.

Influence of the temperature on the cement disintegration in cement-retained implant restorations.

PubMed

Linkevicius, Tomas; Vindasiute, Egle; Puisys, Algirdas; Linkeviciene, Laura; Svediene, Olga

2012-01-01

The aim of this study was to estimate the average disintegration temperature of three dental cements used for the cementation of the implant-supported prostheses. One hundred and twenty metal frameworks were fabricated and cemented on the prosthetic abutments with different dental cements. After heat treatment in the dental furnace, the samples were set for the separation to test the integration of the cement. Results have shown that resin-modified glass-ionomer cement (RGIC) exhibited the lowest disintegration temperature (p<0.05), but there was no difference between zinc phosphate cement (ZPC) and dual cure resin cement (RC) (p>0.05). Average separation temperatures: RGIC - 306 ± 23 °C, RC - 363 ± 71 °C, it could not be calculated for the ZPC due to the eight unseparated specimens. Within the limitations of the study, it could be concluded that RGIC cement disintegrates at the lowest temperature and ZPC is not prone to break down after exposure to temperature.

Retrieval of Cement Embolus from Inferior Vena Cava After Percutaneous Vertebroplasty

DOE Office of Scientific and Technical Information (OSTI.GOV)

Athreya, S., E-mail: sathreya@stjoes.c; Mathias, N.; Rogers, P.

Percutaneous vertebroplasty is an accepted treatment for painful vertebral compression fractures caused by osteoporosis and malignant disease. Venous leakage of cement and pulmonary cement embolism have been reported complications. We describe a paravertebral venous cement leak resulting in the deposition of a cement cast in the inferior vena cava and successful retrieval of the cement embolus.

76 FR 54206 - Gray Portland Cement and Clinker From Japan: Final Results of the Expedited Third Sunset Review...

Federal Register 2010, 2011, 2012, 2013, 2014

2011-08-31

... manufacturing cement, has no use other than grinding into finished cement. Microfine cement was specifically... DEPARTMENT OF COMMERCE International Trade Administration [A-588-815] Gray Portland Cement and... portland cement and clinker from Japan. As a result of this third sunset review, the Department finds that...

Effects of abutment diameter, luting agent type, and re-cementation on the retention of implant-supported CAD/CAM metal copings over short abutments.

PubMed

Safari, Sina; Hosseini Ghavam, Fereshteh; Amini, Parviz; Yaghmaei, Kaveh

2018-02-01

The aim of this study was to evaluate the effects of abutment diameter, cement type, and re-cementation on the retention of implant-supported CAD/CAM metal copings over short abutments. Sixty abutments with two different diameters, the height of which was reduced to 3 mm, were vertically mounted in acrylic resin blocks with matching implant analogues. The specimens were divided into 2 diameter groups: 4.5 mm and 5.5 mm (n=30). For each abutment a CAD/CAM metal coping was manufactured, with an occlusal loop. Each group was sub-divided into 3 sub-groups (n=10). In each subgroup, a different cement type was used: resin-modified glass-ionomer, resin cement and zinc-oxide-eugenol. After incubation and thermocycling, the removal force was measured using a universal testing machine at a cross-head speed of 0.5 mm/min. In zinc-oxide-eugenol group, after removal of the coping, the cement remnants were completely cleaned and the copings were re-cemented with resin cement and re-tested. Two-way ANOVA, post hoc Tukey tests, and paired t-test were used to analyze data (α=.05). The highest pulling force was registered in the resin cement group (414.8 N), followed by the re-cementation group (380.5 N). Increasing the diameter improved the retention significantly ( P =.006). The difference in retention between the cemented and recemented copings was not statistically significant ( P =.40). Resin cement provided retention almost twice as strong as that of the RMGI. Increasing the abutment diameter improved retention significantly. Re-cementation with resin cement did not exhibit any difference from the initial cementation with resin cement.

Fracture Resistance of Lithium Disilicate Ceramics Bonded to Enamel or Dentin Using Different Resin Cement Types and Film Thicknesses.

PubMed

Rojpaibool, Thitithorn; Leevailoj, Chalermpol

2017-02-01

To investigate the influence of cement film thickness, cement type, and substrate (enamel or dentin) on ceramic fracture resistance. One hundred extracted human third molars were polished to obtain 50 enamel and 50 dentin specimens. The specimens were cemented to 1-mm-thick lithium disilicate ceramic plates with different cement film thicknesses (100 and 300 μm) using metal strips as spacers. The cements used were etch-and-rinse (RelyX Ultimate) and self-adhesive (RelyX U200) resin cements. Compressive load was applied on the ceramic plates using a universal testing machine, and fracture loads were recorded in Newtons (N). Statistical analysis was performed by multiple regression (p < 0.05). Representative specimens were evaluated by scanning electron microscopy to control the cement film thickness. The RelyX Ultimate group with a cement thickness of 100 μm cemented to enamel showed the highest mean fracture load (MFL; 1591 ± 172.59 N). The RelyX Ultimate groups MFLs were significantly higher than the corresponding RelyX U200 groups (p < 0.05), and thinner film cement demonstrated a higher MFL than thicker films (p < 0.05). Bonding to dentin resulted in lower MFL than with enamel (p < 0.001). Higher fracture loads were related to thinner cement film thickness and RelyX Ultimate resin cement. Bonding to dentin resulted in lower fracture loads than bonding to enamel. Reduced resin film thickness could reduce lithium disilicate restoration fracture. Etch-and-rinse resin cements are recommended for cementing on either enamel or dentin, compared with self-adhesive resin cement, for improved fracture resistance. © 2015 by the American College of Prosthodontists.

Effects of abutment diameter, luting agent type, and re-cementation on the retention of implant-supported CAD/CAM metal copings over short abutments

PubMed Central

Safari, Sina; Amini, Parviz; Yaghmaei, Kaveh

2018-01-01

PURPOSE The aim of this study was to evaluate the effects of abutment diameter, cement type, and re-cementation on the retention of implant-supported CAD/CAM metal copings over short abutments. MATERIALS AND METHODS Sixty abutments with two different diameters, the height of which was reduced to 3 mm, were vertically mounted in acrylic resin blocks with matching implant analogues. The specimens were divided into 2 diameter groups: 4.5 mm and 5.5 mm (n=30). For each abutment a CAD/CAM metal coping was manufactured, with an occlusal loop. Each group was sub-divided into 3 sub-groups (n=10). In each subgroup, a different cement type was used: resin-modified glass-ionomer, resin cement and zinc-oxide-eugenol. After incubation and thermocycling, the removal force was measured using a universal testing machine at a cross-head speed of 0.5 mm/min. In zinc-oxide-eugenol group, after removal of the coping, the cement remnants were completely cleaned and the copings were re-cemented with resin cement and re-tested. Two-way ANOVA, post hoc Tukey tests, and paired t-test were used to analyze data (α=.05). RESULTS The highest pulling force was registered in the resin cement group (414.8 N), followed by the re-cementation group (380.5 N). Increasing the diameter improved the retention significantly (P=.006). The difference in retention between the cemented and recemented copings was not statistically significant (P=.40). CONCLUSION Resin cement provided retention almost twice as strong as that of the RMGI. Increasing the abutment diameter improved retention significantly. Re-cementation with resin cement did not exhibit any difference from the initial cementation with resin cement. PMID:29503708

Evaluation of stainless steel crowns cemented with glass-ionomer and resin-modified glass-ionomer luting cements.

PubMed

Yilmaz, Yucel; Simsek, Sera; Dalmis, Anya; Gurbuz, Taskin; Kocogullari, M Elcin

2006-04-01

To evaluate in vitro and in vivo conditions of stainless steel crowns (SSC) cemented using one luting glass-ionomer cement (Aqua Meron) and one luting resin-modified glass-ionomer cement (Vitremer). In the in vitro part of this study, retentive properties of SSCs cemented using Aqua Meron and Vitremer on extracted primary first molars were tested. In addition, two specimens of each group were used to evaluate the tooth hard tissue-cement, within the cement itself, cement-SSC, and tooth hard tissue-cement-SSC under scanning electron microscope (SEM). In the in vivo part of this study, 152 SSCs were placed on the first or second primary molars of 86 children, and cemented using either Aqua Meron or Vitremer. The crowns were examined for retention. In addition, the clinical views of the crowns were recorded with an intraoral camera. No significant difference was found between the mean retentive forces of Aqua Meron and Vitremer (P> 0.05). SSCs cemented with Aqua Meron and Vitremer had an average lifespan of 26.44 and 24.07 months respectively. Only one (0.66%) of 152 SSCs was lost from the Aqua Meron group during post-cementation periods. Nineteen of the 152 SSCs (12.5%) had dents or perforations.

Microleakage of adhesive and nonadhesive luting cements for stainless steel crowns.

PubMed

Memarpour, Mahtab; Mesbahi, Maryam; Rezvani, Gita; Rahimi, Mehran

2011-01-01

This study's purpose was to compare the ability of 5 luting cements to reduce microleakage at stainless steel crown (SSC) margins on primary molar teeth. Standard preparations were performed on 100 extracted primary molar teeth for SSC restoration. After fitting SSCs, samples were randomly divided into 5 groups of 20 teeth each, which were cemented with nonadhesive cement consisting of polycarboxylate (PC) or zinc phosphate (ZP), or with adhesive cement consisting of glass ionomer (GIC), resin-modified glass ionomer cement (RMGIC), or RMGIC with a bonding agent (RMGIC+DBA). After aging and thermocycling, the specimens were placed in 1% methylene blue, sectioned, and evaluated under a digital microscope. The data were compared between groups with the t test, analysis of variance, and the least significant difference test. Microleakage with adhesive cements was significantly lower than with nonadhesive cements (P<.05). Differences between cements were statistically significant at P<.001. RMGIC+DBA showed the lowest microleakage, followed in increasing order by RMGIC, GIC, and ZP. The PC cement showed the greatest microleakage. Adhesive cements were more effective in reducing microleakage in stainless steel crowns than nonadhesive cements. Use of a bonding agent with a resin-modified glass ionomer cement yielded better results than using the latter alone.

Elasticity and expansion test performance of geopolymer as oil well cement

NASA Astrophysics Data System (ADS)

Ridha, S.; Hamid, A. I. Abd; Halim, A. H. Abdul; Zamzuri, N. A.

2018-04-01

History has shown that geopolymer cement provides high compressive strength as compared to Class G cement. However, the research had been done at ambient temperature, not at elevated condition which is the common oil well situation. In this research, the physical and mechanical properties performance of the oil well cement were investigated by laboratory work for two types of cement that are geopolymer and Class G cement. The cement samples were produced by mixing the cement according to the API standards. Class C fly ash was used in this study. The alkaline solution was prepared by mixing sodium silicate with NaOH solution. The NaOH solution was prepared by diluting NaOH pellets with distilled water to 8M. The cement samples were cured at a pressure of 3000 psi and a temperature of 130 °C to simulate the downhole condition. After curing, the physical properties of the cement samples were investigated using OYO Sonic Viewer to determine their elastic properties. Autoclave expansion test and compressive strength tests were conducted to determine the expansion value and the strength of the cement samples, respectively. The results showed that the geopolymer cement has a better physical and mechanical properties as compared with Class G cement at elevated condition.

Effect of temporary cements on the microtensile bond strength of self-etching and self-adhesive resin cement.

PubMed

Carvalho, Edilausson Moreno; Carvalho, Ceci Nunes; Loguercio, Alessandro Dourado; Lima, Darlon Martins; Bauer, José

2014-11-01

The aim of this study was to evaluate the microtensile bond strength (µTBS) of self-etching and self-adhesive resin cement systems to dentin affected by the presence of remnants of either eugenol-containing or eugenol-free temporary cements. Thirty extracted teeth were obtained and a flat dentin surface was exposed on each tooth. Acrylic blocks were fabricated and cemented either with one of two temporary cements, one zinc oxide eugenol (ZOE) and one eugenol free (ZOE-free), or without cement (control). After cementation, specimens were stored in water at 37°C for 1 week. The restorations and remnants of temporary cements were removed and dentin surfaces were cleaned with pumice. Resin composite blocks were cemented to the bonded dentin surfaces with one of two resin cements, either self-etching (Panavia F 2.0) or self-adhesive (RelyX U-100). After 24 h, the specimens were sectioned to obtain beams for submission to µTBS. The fracture mode was evaluated under a stereoscopic loupe and a scanning electron microscope (SEM). Data from µTBS were submitted to two-way repeated-measure ANOVA and the Tukey test (alpha = 0.05). The cross-product interaction was statistically significant (p < 0.0003). The presence of temporary cements reduced the bond strength to Panavia self-etching resin cements only (p < 0.05). Fracture occurred predominantly at the dentin-adhesive interface. The presence of eugenol-containing temporary cements did not interfere in the bond strength to dentin of self-adhesive resin cements.

Evaluation of selected properties of a new root repair cement containing surface pre-reacted glass ionomer fillers.

PubMed

Yassen, Ghaeth H; Huang, Ruijie; Al-Zain, Afnan; Yoshida, Takamitsu; Gregory, Richard L; Platt, Jeffrey A

2016-11-01

This study evaluated selected properties of a prototype root repair cement containing surface pre-reacted glass ionomer fillers (S-PRG) in comparison to mineral trioxide aggregate (MTA) and intermediate restorative material (IRM). The antibacterial effect of S-PRG, MTA, and IRM cements was tested against Porphyromonas gingivalis and Enterococcus faecalis after 1 and 3 days of aging of the cements. The set cements were immersed in distilled water for 4 h to 28 days, and ion-releasing ability was evaluated. Initial and final setting times of all cements were evaluated using Gilmore needles. The push-out bond strength between radicular dentin and all cements was tested at different levels of the roots. S-PRG and IRM cements, but not MTA cement, demonstrated significant antibacterial effect against P. gingivalis. All types of cements exhibited significant antibacterial effect against E. faecalis without being able to eliminate the bacterium. S-PRG cement provided continuous release of fluoride, strontium, boron, sodium, aluminum, and zinc throughout all tested time points. Both initial and final setting times were significantly shorter for S-PRG and IRM cements in comparison to MTA. The push-out bond strength was significantly lower for S-PRG cement in comparison to MTA and IRM at coronal and middle levels of the roots. S-PRG cement demonstrated significant antibacterial effects against endodontic pathogens, multiple ion-releasing ability, relatively short setting time, and low bonding strength. S-PRG cement can be used as a one-visit root repair material with promising antibacterial properties and ion-releasing capacity.

Effect of wet curing duration on durability parameters of hydraulic cement concretes.

DOT National Transportation Integrated Search

2010-01-01

Hydraulic cement concrete slabs were cast and stored outdoors in Charlottesville, Virginia, to study the impact of wet curing duration on durability parameters. Concrete mixtures were produced using portland cement, portland cement with slag cement, ...

[Experimental rationale for carcinogenic risk of asbestos cement industry and its products].

PubMed

Pylev, D N; Smirnova, O V; Vasil'eva, L A; Khrustalev, S A; Vezentsev, A I; Gudkova, E A; Naumova, L N

2010-01-01

During intraperitoneal administration of dispersiveness-comparable chrysotile or asbestos cement fibers to rats (20 mg thrice), mesotheliomas were found in 45.1 and 7.7% of cases respectively. Asbestos cement dust induced tumors in 2.5% of cases, which is of biological importance. Cement or freeze asbestos destruction cement dust failed to cause tumors. The latter were not detected in a control group receiving physiological saline. Asbestos cement fibers and fascicles are covered by a cement matrix. Fiber amorphization gradually occurs. In lung tissue, there may be destruction of the cement coat of fascicles and release of native chrysotile fibers that are carcinogenic.

In Vitro Evaluation of Planktonic Growth on Experimental Cement-Retained Titanium Surfaces.

PubMed

Balci, Nur; Cakan, Umut; Aksu, Burak; Akgul, Oncu; Ulger, Nurver

2016-04-08

BACKGROUND The purpose of this study was to compare the effects of selected cements, or their combination with titanium, on the growth of two periodontopathic bacteria: Prevotella intermedia (Pi) and Fusobacterium nucleatum (Fn). MATERIAL AND METHODS This study was comprised of several experimental groups: 1) Dental luting cements (glass ionomer cement, methacrylate-based resin cement, zinc-oxide eugenol cement, eugenol-free zinc oxide cement; 2) titanium discs; and 3) titanium combination cement discs. The disks were submerged in bacterial suspensions of either Fn or Pi. Planktonic bacterial growth within the test media was measured by determining the optical density of the cultures (OD600). Mean and standard deviations were calculated for planktonic growth from three separate experiments. RESULTS Intergroup comparison of all experimental groups revealed increased growth of Pi associated with cement-titanium specimens in comparison with cement specimens. Regarding the comparison of all groups for Fn, there was an increased amount of bacterial growth in cement-titanium specimens although the increase was not statistically significant. CONCLUSIONS The combination of cement with titanium may exacerbate the bacterial growth capacity of Pi and Fn in contrast to their sole effect.

In Vitro Evaluation of Planktonic Growth on Experimental Cement-Retained Titanium Surfaces

PubMed Central

Balci, Nur; Cakan, Umut; Aksu, Burak; Akgul, Oncu; Ulger, Nurver

2016-01-01

Background The purpose of this study was to compare the effects of selected cements, or their combination with titanium, on the growth of two periodontopathic bacteria: Prevotella intermedia (Pi) and Fusobacterium nucleatum (Fn). Material/Methods This study was comprised of several experimental groups: 1) Dental luting cements (glass ionomer cement, methacrylate-based resin cement, zinc-oxide eugenol cement, eugenol-free zinc oxide cement; 2) titanium discs; and 3) titanium combination cement discs. The disks were submerged in bacterial suspensions of either Fn or Pi. Planktonic bacterial growth within the test media was measured by determining the optical density of the cultures (OD600). Mean and standard deviations were calculated for planktonic growth from three separate experiments. Results Intergroup comparison of all experimental groups revealed increased growth of Pi associated with cement-titanium specimens in comparison with cement specimens. Regarding the comparison of all groups for Fn, there was an increased amount of bacterial growth in cement-titanium specimens although the increase was not statistically significant. Conclusions The combination of cement with titanium may exacerbate the bacterial growth capacity of Pi and Fn in contrast to their sole effect. PMID:27058704

Comparison of retention and demineralization inhibition potential of adhesive banding cements in primary teeth.

PubMed

Prabhakar, A R; Mahantesh, T; Ahuja, Vipin

2010-01-01

The purpose of this study was to evaluate the efficacy of banding cements in terms of retentive capability and demineralization inhibition potential. We included 48 non-carious primary mandibular second molar teeth. Preformed stainless steel bands were adapted onto the teeth. All teeth were randomly assigned to four groups: Group I (Adaptation of bands without cementation), Group II (Cementation of bands using conventional Glass Ionomer Cement), Group III (Cementation of bands using Resin-modified Glass Ionomer Cement), Group IV (Cementation of bands using Resin cement), and placed in artificial saliva. Each day, specimens were taken from artificial saliva and suspended in an artificial caries solution for 35 minutes, every 8 hours. At the end of 3 months, retention of bands was estimated using an Instron Universal Testing Machine. The mode of failure was recorded and specimens were sectioned and examined under polarized microscope for demineralized lesions. The mean retention value was highest with resin cement, followed by RMGIC, GIC, and Control group respectively. The RMGIC group showed more favorable modes of failures. All the experimental groups showed significant demineralization inhibition potential. RMGIC is the preferable banding cement and can be used effectively to cement bands in primary dentition.

Cement selection for implant-supported crowns fabricated with different luting space settings.

PubMed

Gultekin, Pinar; Gultekin, B Alper; Aydin, Murat; Yalcin, Serdar

2013-02-01

To measure and compare the retentive strength of cements specifically formulated for luting restorations onto implant abutments and to investigate the effect of varying cement gap on retention strength of implant-supported crowns. Standard titanium abutments were scanned by means of a 3D digital laser scanner. One hundred and sixty standard metal copings were designed by a Computer Aided Design/Computer Aided Manufacturing (CAD/CAM) system with two cement gap values (20 and 40 μm). The copings were cemented to the abutments using the following eight cements with one being the control, zinc oxide temporary cement, while the other seven were specifically formulated implant cements (n = 10): Premier Implant Cement, ImProv, Multilink Implant, EsTemp Implant, Cem-Implant, ImplaTemp, MIS Crown Set, and TempBond NE. The specimens were placed in 100% humidity for 24 hours, and subjected to a pull-out test using a universal testing machine at a 0.5 mm/min crosshead speed. The test results were analyzed with two-way ANOVA, one-way ANOVA, post hoc Tamhane' s T2, and student's t-tests at a significance level of 0.05. Statistical analysis revealed significant differences in retention strength across the cement groups (p < 0.01). Resin-based cements showed significantly higher decementation loads than a noneugenol zinc oxide provisional cement (TempBond NE) (p < 0.01), with the highest tensile resistance seen with Multilink Implant, followed by Cem-Implant, MIS Crown Set, ImProv, Premier Implant Cement, EsTemp Implant, and ImplaTemp. Increasing the cement gap from 20 to 40 μm improved retention significantly for the higher strength cements: Multilink Implant, Premier Implant Cement, ImProv, Cem-Implant, and MIS Crown Set (p < 0.01), while it had no significant effect on retention for the lower strength cements: EsTemp Implant, ImplaTemp, and TempBond NE (p > 0.05). Resin cements specifically formulated for implant-supported restorations demonstrated significant differences in retention strength. The ranking of cements presented in the study is meant to be an arbitrary guide for the clinician in deciding the appropriate cement selection for CAD/CAM-fabricated metal copings onto implant abutments with different luting space settings. © 2012 by the American College of Prosthodontists.

PRECIPITATION AND INACTIVATION OF PHOSPHORUS AS A LAKE RESTORATION TECHNIQUE

EPA Science Inventory

Many eutrophic lakes respond slowly following nutrient diversion because of long water retention times, and the recycling of phosphorus from sediments and other internal sources. Treatment of lakes with aluminum sulfate and/or sodium aluminate is a successful method for removing ...

Microleakage of Glass Ionomer-based Provisional Cement in CAD/CAM-Fabricated Interim Crowns: An in vitro Study.

PubMed

Farah, Ra'fat I; Al-Harethi, Naji

2016-10-01

The aim of this study was to compare in vitro the marginal microleakage of glass ionomer-based provisional cement with resin-based provisional cement and zinc oxide non-eugenol (ZONE) provisional cement in computer-aided design and computer-aided manufacturing (CAD/CAM)-fabricated interim restorations. Fifteen intact human premolars were prepared in a standardized manner for complete coverage of crown restorations. Interim crowns for the prepared teeth were then fabricated using CAD/CAM, and the specimens were randomized into three groups of provisional cementing agents (n = 5 each): Glass ionomer-based provisional cement (GC Fuji TEMP LT™), bisphenol-A-glycidyldimethacrylate (Bis-GMA)/ triethylene glycol dimethacrylate (TEGDMA) resin-based cement (UltraTemp® REZ), and ZONE cement (TempBond NE). After 24 hours of storage in distilled water at 37°C, the specimens were thermocycled and then stored again for 24 hours in distilled water at room temperature. Next, the specimens were placed in freshly prepared 2% aqueous methylene blue dye for 24 hours and then embedded in autopolymerizing acrylic resin blocks and sectioned in buccolingual and mesiodistal directions to assess dye penetration using a stereomicroscope. The results were statistically analyzed using a nonparametric Kruskal-Wallis test. Dunn's post hoc test with a Bonferroni correction test was used to compute multiple pairwise comparisons that identified differences among groups; the level of significance was set at p < 0.05. All groups exhibited marginal microleakage; the Bis-GMA/TEGDMA resin-based provisional cement demonstrated the lowest microleakage scores, which were statistically different from those of the glass ionomer-based provisional cement and the ZONE cement. The provisional cementing agents exhibited different sealing abilities. The Bis-GMA/TEGDMA resin-based provisional cement exhibited the most effective favorable sealing properties against dye penetration compared with the glass ionomer-based provisional cement and conventional ZONE cement. Newly introduced glass ionomer-based provisional cement proved to be inferior to resin-based provisional cement as far as marginal microleakage is concerned.

[Significance of bone mineral density and modern cementing technique for in vitro cement penetration in total shoulder arthroplasty].

PubMed

Pape, G; Raiss, P; Kleinschmidt, K; Schuld, C; Mohr, G; Loew, M; Rickert, M

2010-12-01

Loosening of the glenoid component is one of the major causes of failure in total shoulder arthroplasty. Possible risk factors for loosening of cemented components include an eccentric loading, poor bone quality, inadequate cementing technique and insufficient cement penetration. The application of a modern cementing technique has become an established procedure in total hip arthroplasty. The goal of modern cementing techniques in general is to improve the cement-penetration into the cancellous bone. Modern cementing techniques include the cement vacuum-mixing technique, retrograde filling of the cement under pressurisation and the use of a pulsatile lavage system. The main purpose of this study was to analyse cement penetration into the glenoid bone by using modern cement techniques and to investigate the relationship between the bone mineral density (BMD) and the cement penetration. Furthermore we measured the temperature at the glenoid surface before and after jet-lavage of different patients during total shoulder arthroplasty. It is known that the surrounding temperature of the bone has an effect on the polymerisation of the cement. Data from this experiment provide the temperature setting for the in-vitro study. The glenoid surface temperature was measured in 10 patients with a hand-held non-contact temperature measurement device. The bone mineral density was measured by DEXA. Eight paired cadaver scapulae were allocated (n = 16). Each pair comprised two scapulae from one donor (matched-pair design). Two different glenoid components were used, one with pegs and the other with a keel. The glenoids for the in-vitro study were prepared with the bone compaction technique by the same surgeon in all cases. Pulsatile lavage was used to clean the glenoid of blood and bone fragments. Low viscosity bone cement was applied retrogradely into the glenoid by using a syringe. A constant pressure was applied with a modified force sensor impactor. Micro-computed tomography scans were applied to analyse the cement penetration into the cancellous bone. The mean temperature during the in-vivo arthroplasty of the glenoid was 29.4 °C (27.2-31 °C) before and 26.2 °C (25-27.5 °C) after jet-lavage. The overall peak BMD was 0.59 (range 0.33-0.99) g/cm (2). Mean cement penetration was 107.9 (range 67.6-142.3) mm (2) in the peg group and 128.3 (range 102.6-170.8) mm (2) in the keel group. The thickness of the cement layer varied from 0 to 2.1 mm in the pegged group and from 0 to 2.4 mm in the keeled group. A strong negative correlation between BMD and mean cement penetration was found for the peg group (r (2) = -0.834; p < 0.01) and for the keel group (r (2) = -0.727; p < 0.041). Micro-CT shows an inhomogenous dispersion of the cement into the cancellous bone. Data from the in-vivo temperature measurement indicate that the temperature at the glenohumeral surface under operation differs from the body core temperature and should be considered in further in-vitro studies with human specimens. Bone mineral density is negatively correlated to cement penetration in the glenoid. The application of a modern cementing technique in the glenoid provides sufficient cementing penetration although there is an inhomogenous dispersion of the cement. The findings of this study should be considered in further discussions about cementing technique and cement penetration into the cancellous bone of the glenoid. © Georg Thieme Verlag KG Stuttgart · New York.

Effect of surface treatment and type of cement on push-out bond strength of zirconium oxide posts.

PubMed

Almufleh, Balqees S; Aleisa, Khalil I; Morgano, Steven M

2014-10-01

The effect of the surface treatment of zirconium oxide posts on their push-out bond strength is controversial. The purpose of this study was to compare the effects of 2 surface treatments on the bond strength of zirconium oxide posts cemented with different cements and to assess the failure mode. Seventy extracted human teeth were divided into 7 groups (n=10). Custom zirconium oxide posts (Cercon; Degudent) were fabricated for 6 groups. Posts in 3 groups were airborne-particle abraded (A). Posts in the other 3 groups were tribochemical silica coated (T). Three cements were used. Zinc phosphate cement was used to cement the zirconium oxide posts in groups AZ and TZ, RelyX ARC cement was used in groups ARA and TRA, and RelyX Unicem cement was used in groups ARU and TRU. Group C contained custom metal posts cemented with zinc phosphate cement. Specimens were horizontally sectioned into 3 sections and subjected to a push-out test. A mixed model analysis of variance, 1-way ANOVA, and the Tukey multiple comparison tests were used for statistical analysis. The highest push-out bond strength was recorded for Group ARU (21.03 MPa), and the lowest was recorded for Group ARA (7.57 MPa). No significant difference in push-out bond strength was found among the different surface treatments and root regions (P>.05). The type of cement had a significant effect on the push-out bond strength of zirconium oxide posts (P=.049). RelyX Unicem cement recorded (19.57 ±8.83 MPa) significantly higher push-out bond strength compared with zinc phosphate (9.95 ±6.31 MPa) and RelyX ARC cements (9.39 ±5.45 MPa). Adhesive failure at the post-cement interface was recorded for 75% of the posts cemented with zinc phosphate and RelyX ARC cements, while mixed failure was recorded for 75% of the posts cemented with RelyX Unicem cement. The type of cement used resulted in a statistically significant difference in the push-out bond strength of zirconium oxide posts, while both the surface treatment and root region resulted in no statistically significant effect after artificial aging. RelyX Unicem cement had significantly higher push-out bond strength than did zinc phosphate and RelyX ARC cements. Copyright © 2014 Editorial Council for the Journal of Prosthetic Dentistry. Published by Elsevier Inc. All rights reserved.

Development of monetite-nanosilica bone cement: a preliminary study.

PubMed

Zhou, Huan; Luchini, Timothy J F; Agarwal, Anand K; Goel, Vijay K; Bhaduri, Sarit B

2014-11-01

In this paper, we reported the results of our efforts in developing DCPA/nanosilica composite orthopedic cement. It is motivated by the significances of DCPA and silicon in bone physiological activities. More specifically, this paper examined the effects of various experimental parameters on the properties of such composite cements. In this work, DCPA cement powders were synthesized using a microwave synthesis technique. Mixing colloidal nanosilica directly with synthesized DCPA cement powders can significantly reduce the washout resistance of DCPA cement. In contrast, a DCPA-nanosilica cement powder prepared by reacting Ca(OH)2 , H3 PO4 and nanosilica together showed good washout resistance. The incorporation of nanosilica in DCPA can improve compressive strength, accelerate cement solidification, and intensify surface bioactivity. In addition, it was observed that by controlling the content of NaHCO3 during cement preparation, the resulting composite cement properties could be modified. Allowing for the development of different setting times, mechanical performance and crystal features. It is suggested that DCPA-nanosilica composite cement can be a potential candidate for bone healing applications. © 2014 Wiley Periodicals, Inc.

[Augmentation with PMMA cement].

PubMed

Kühn, K-D; Höntzsch, D

2015-09-01

Cements based on polymethyl methacrylate (PMMA) can be used without any problem in a variety of clinical augmentations. Cement-related complications in surgical procedures involving PMMA cements, such as embolism, thermal necrosis, toxicity and hypersensitivity, are often due to other causes. Knowledge about the properties of the cement helps the user to safely employ PMMA cements in augmentations. High radio-opacity is required in vertebral body augmentations and this is provided in particular by zirconium dioxide. In vertebral body augmentations, a low benzoyl peroxide (BPO) content can considerably prolong the liquid dough phase. In augmentations with cement fillings in the region of a tumor, a high BPO content can specifically increase the peak temperature of the PMMA cement. In osteosynthetic augmentations with PMMA, necrosis is rare because heat development in the presence of metallic implants is low due to heat conduction via the implant. Larger cement fillings where there is no heat conduction via metal implants can exhibit substantially higher peak temperatures. The flow properties of PMMA cements are of particular importance for the user to allow optimum handling of PMMA cements. In patients with hypersensitivity to antibiotics, there is no need to avoid the use of PMMA as there are sufficient PMMA-based alternatives. The PMMA cements are local drug delivery systems and antibiotics, antiseptics, antimycotics and also cytostatics can be mixed with the cement. Attention must be paid to antagonistic and synergistic effects.

Effect of cement washout on loosening of abutment screws and vice versa in screw- and cement- retained implant-supported dental prosthesis

PubMed Central

Kim, Seok-Gyu; Son, Mee-Kyoung

2015-01-01

PURPOSE The purpose of this study was to examine the abutment screw stability of screw- and cement-retained implant-supported dental prosthesis (SCP) after simulated cement washout as well as the stability of SCP cements after complete loosening of abutment screws. MATERIALS AND METHODS Thirty-six titanium CAD/CAM-made implant prostheses were fabricated on two implants placed in the resin models. Each prosthesis is a two-unit SCP: one screw-retained and the other cemented. After evaluating the passive fit of each prosthesis, all implant prostheses were randomly divided into 3 groups: screwed and cemented SCP (Control), screwed and noncemented SCP (Group 1), unscrewed and cemented SCP (Group 2). Each prosthesis in Control and Group 1 was screwed and/or cemented, and the preloading reverse torque value (RTV) was evaluated. SCP in Group 2 was screwed and cemented, and then unscrewed (RTV=0) after the cement was set. After cyclic loading was applied, the postloading RTV was measured. RTV loss and decementation ratios were calculated for statistical analysis. RESULTS There was no significant difference in RTV loss ratio between Control and Group 1 (P=.16). No decemented prosthesis was found among Control and Group 2. CONCLUSION Within the limits of this in vitro study, the stabilities of SCP abutment screws and cement were not significantly changed after simulated cement washout or screw loosening. PMID:26140172

Biomechanical three-dimensional finite element analysis of monolithic zirconia crown with different cement type

PubMed Central

2015-01-01

PURPOSE The objective of this study was to evaluate the influence of various cement types on the stress distribution in monolithic zirconia crowns under maximum bite force using the finite element analysis. MATERIALS AND METHODS The models of the prepared #46 crown (deep chamfer margin) were scanned and solid models composed of the monolithic zirconia crown, cement layer, and prepared tooth were produced using the computer-aided design technology and were subsequently translated into 3-dimensional finite element models. Four models were prepared according to different cement types (zinc phosphate, polycarboxylate, glass ionomer, and resin). A load of 700 N was applied vertically on the crowns (8 loading points). Maximum principal stress was determined. RESULTS Zinc phosphate cement had a greater stress concentration in the cement layer, while polycarboxylate cement had a greater stress concentration on the distal surface of the monolithic zirconia crown and abutment tooth. Resin cement and glass ionomer cement showed similar patterns, but resin cement showed a lower stress distribution on the lingual and mesial surface of the cement layer. CONCLUSION The test results indicate that the use of different luting agents that have various elastic moduli has an impact on the stress distribution of the monolithic zirconia crowns, cement layers, and abutment tooth. Resin cement is recommended for the luting agent of the monolithic zirconia crowns. PMID:26816578

Properties of Cement Mortar Produced from Mixed Waste Materials with Pozzolanic Characteristics.

PubMed

Yen, Chi-Liang; Tseng, Dyi-Hwa; Wu, Yue-Ze

2012-07-01

Waste materials with pozzolanic characteristics, such as sewage sludge ash (SSA), coal combustion fly ash (FA), and granulated blast furnace slag (GBS), were reused as partial cement replacements for making cement mortar in this study. Experimental results revealed that with dual replacement of cement by SSA and GBS and triple replacement by SSA, FA, and GBS at 50% of total cement replacement, the compressive strength (Sc) of the blended cement mortars at 56 days was 93.7% and 92.9% of the control cement mortar, respectively. GBS had the highest strength activity index value and could produce large amounts of CaO to enhance the pozzolanic activity of SSA/FA and form calcium silicate hydrate gels to fill the capillary pores of the cement mortar. Consequently, the Sc development of cement mortar with GBS replacement was better than that without GBS, and the total pore volume of blended cement mortars with GBS/SSA replacement was less than that with FA/SSA replacement. In the cement mortar with modified SSA and GBS at 70% of total cement replacement, the Sc at 56 days was 92.4% of the control mortar. Modifying the content of calcium in SSA also increased its pozzolanic reaction. CaCl(2) accelerated the pozzolanic activity of SSA better than lime did. Moreover, blending cement mortars with GBS/SSA replacement could generate more monosulfoaluminate to fill capillary pores.

Properties of Cement Mortar Produced from Mixed Waste Materials with Pozzolanic Characteristics

PubMed Central

Yen, Chi-Liang; Tseng, Dyi-Hwa; Wu, Yue-Ze

2012-01-01

Abstract Waste materials with pozzolanic characteristics, such as sewage sludge ash (SSA), coal combustion fly ash (FA), and granulated blast furnace slag (GBS), were reused as partial cement replacements for making cement mortar in this study. Experimental results revealed that with dual replacement of cement by SSA and GBS and triple replacement by SSA, FA, and GBS at 50% of total cement replacement, the compressive strength (Sc) of the blended cement mortars at 56 days was 93.7% and 92.9% of the control cement mortar, respectively. GBS had the highest strength activity index value and could produce large amounts of CaO to enhance the pozzolanic activity of SSA/FA and form calcium silicate hydrate gels to fill the capillary pores of the cement mortar. Consequently, the Sc development of cement mortar with GBS replacement was better than that without GBS, and the total pore volume of blended cement mortars with GBS/SSA replacement was less than that with FA/SSA replacement. In the cement mortar with modified SSA and GBS at 70% of total cement replacement, the Sc at 56 days was 92.4% of the control mortar. Modifying the content of calcium in SSA also increased its pozzolanic reaction. CaCl2 accelerated the pozzolanic activity of SSA better than lime did. Moreover, blending cement mortars with GBS/SSA replacement could generate more monosulfoaluminate to fill capillary pores. PMID:22783062

N-acetyl cysteine (NAC)-mediated detoxification and functionalization of poly(methyl methacrylate) bone cement.

PubMed

Tsukimura, Naoki; Yamada, Masahiro; Aita, Hideki; Hori, Norio; Yoshino, Fumihiko; Chang-Il Lee, Masaichi; Kimoto, Katsuhiko; Jewett, Anahid; Ogawa, Takahiro

2009-07-01

Currently used poly(methyl methacrylate) (PMMA)-based bone cement lacks osteoconductivity and induces osteolysis and implant loosening due to its cellular and tissue-toxicity. A high percentage of revision surgery following the use of bone cement has become a significant universal problem. This study determined whether incorporation of the amino acid derivative N-acetyl cysteine (NAC) in bone cement reduces its cytotoxicity and adds osteoconductivity to the material. Biocompatibility and bioactivity of PMMA-based bone cement with or without 25mm NAC incorporation was examined using rat bone marrow-derived osteoblastic cells. Osteoconductive potential of NAC-incorporated bone cement was determined by microCT bone morphometry and implant biomechanical test in the rat model. Generation of free radicals within the polymerizing bone cement was examined using electron spin resonance spectroscopy. Severely compromised viability and completely suppressed phenotypes of osteoblasts on untreated bone cement were restored to the normal level by NAC incorporation. Bone volume formed around 25mm NAC-incorporated bone cement was threefold greater than that around control bone cement. The strength of bone-bone cement integration was 2.2 times greater for NAC-incorporated bone cement. For NAC-incorporated bone cement, the spike of free radical generation ended within 12h, whereas for control bone cement, a peak level lasted for 6 days and a level greater than half the level of the peak was sustained for 20 days. NAC also increased the level of antioxidant glutathione in osteoblasts. These results suggest that incorporation of NAC in PMMA bone cement detoxifies the material by immediate and effective in situ scavenging of free radicals and increasing intracellular antioxidant reserves, and consequently adds osteoconductivity to the material.

Effects of Cement, Abutment Surface Pretreatment, and Artificial Aging on the Force Required to Detach Cantilever Fixed Dental Prostheses from Dental Implants.

PubMed

Kappel, Stefanie; Chepura, Taras; Schmitter, Marc; Rammelsberg, Peter; Rues, Stefan

To examine the in vitro effects of different cements, abutment surface preconditioning, and artificial aging on the maximum tensile force needed to detach cantilever fixed dental prostheses (FDPs) from dental implants with titanium abutments. A total of 32 tissue-level implants were combined with standardized titanium abutments. For each test group, eight cantilever FDPs were fabricated using selective laser melting (cobalt-chromium [CoCr] alloy). The inner surfaces of the cantilever FDPs and half of the abutments were sandblasted and then joined by use of four different cements (two permanent and two semi-permanent) in two different amounts per cement. Subgroups were tested after either artificial aging (thermocycling and chewing simulation) or 3 days of water storage. Finally, axial pull off-tests were performed for each abutment separately. Cement type and surface pretreatment significantly affected decementation behavior. The highest retention forces (approximately 1,200 N) were associated with sandblasted abutments and permanent cements. With unconditioned abutments, temporary cements (Fu < 100 N), as well as glass-ionomer cement (Fu ≈ 100 N), resulted in rather low retention forces. Zinc phosphate cement guaranteed high retention forces. After aging, retention was sufficient only for cementation with zinc phosphate cement and for the combination of sandblasted abutments and glass-ionomer cement. When glass-ionomer cement is used to fix cantilever FDPs on implants, sandblasting of standard titanium abutments may help prevent loss of retention. Retention forces were still high for FDPs fixed with zinc phosphate cement, even when the abutments were not pretreated. Use of permanent cements only, however, is recommended to prevent unwanted loosening of cantilever FDPs.

Micro-mechanical modeling of the cement-bone interface: the effect of friction, morphology and material properties on the micromechanical response.

PubMed

Janssen, Dennis; Mann, Kenneth A; Verdonschot, Nico

2008-11-14

In order to gain insight into the micro-mechanical behavior of the cement-bone interface, the effect of parametric variations of frictional, morphological and material properties on the mechanical response of the cement-bone interface were analyzed using a finite element approach. Finite element models of a cement-bone interface specimen were created from micro-computed tomography data of a physical specimen that was sectioned from an in vitro cemented total hip arthroplasty. In five models the friction coefficient was varied (mu=0.0; 0.3; 0.7; 1.0 and 3.0), while in one model an ideally bonded interface was assumed. In two models cement interface gaps and an optimal cement penetration were simulated. Finally, the effect of bone cement stiffness variations was simulated (2.0 and 2.5 GPa, relative to the default 3.0 GPa). All models were loaded for a cycle of fully reversible tension-compression. From the simulated stress-displacement curves the interface deformation, stiffness and hysteresis were calculated. The results indicate that in the current model the mechanical properties of the cement-bone interface were caused by frictional phenomena at the shape-closed interlock rather than by adhesive properties of the cement. Our findings furthermore show that in our model maximizing cement penetration improved the micromechanical response of the cement-bone interface stiffness, while interface gaps had a detrimental effect. Relative to the frictional and morphological variations, variations in the cement stiffness had only a modest effect on the micro-mechanical behavior of the cement-bone interface. The current study provides information that may help to better understand the load-transfer mechanisms taking place at the cement-bone interface.

Comparative study on the tensile bond strength and marginal fit of complete veneer cast metal crowns using various luting agents: An in vitro study

PubMed Central

Parameswari, B. Devi; Rajakumar, M.; Lambodaran, G.; Sundar, Shyam

2016-01-01

Introduction: Several commercially available luting agents are used to cement the dental restorations such as intra-coronal, extra-coronal, and fixed partial dentures. Tensile bond strength (TBS) and accurate marginal fit are the essential factors to determine the good clinical results in fixed prosthesis. The retentivity of the luting cements is assessed by their adhesive capacity over the tooth surface and metal surface. Generally, the adhesive ability has been evaluated with in vitro testing, with tensile bond tests. The failure of fixed prosthesis may be happened as a result of incomplete seating during cementation. Most research on cementation of crowns relates seating failure to the thickness of the cement film. Materials and Methods: The study is divided into four groups with 10 samples for each of the luting cement taken up for testing TBS and four groups with 5 samples for each luting agent chosen for assessing marginal fit. The results were tabulated and statistically analyzed. Results: In this in vitro study, the TBS of luting cements, and marginal fit in relation to luting cements were tested by using appropriate testing devices. The TBS of cement is measured using universal testing machine, and the results are tabulated. The marginal gap that exists between the margin of the cast metal crown, and the finish line is measured using travelling microscope before and after cementation. The difference between these two values gives the discrepancy that is due to the film thickness of cement used for luting the restoration. Summary and Conclusion: The TBS value of zinc phosphate cement and glass ionomer cement were found to be almost same. The chemical adhesiveness of the glass ionomer with calcium ions of enamel and dentin may be the attributed reason (ionic bonding). In this study, the polycarboxylate is the one that showed low TBS, and it may be attributed to the weakness of the cement due to reduced film thickness, though this cement has a chemical bonding nature. The observation of results of marginal fit in this study is the increased gap found in zinc phosphate cement followed by resin cement, zinc polycarboxylate, and glass ionomer cement. It is agreeable to estimate the marginal fit of the restoration, which could be affected by the film thickness of the luting cement along with other factors. PMID:27829765

Comparative study on the tensile bond strength and marginal fit of complete veneer cast metal crowns using various luting agents: An in vitro study.

PubMed

Parameswari, B Devi; Rajakumar, M; Lambodaran, G; Sundar, Shyam

2016-10-01

Several commercially available luting agents are used to cement the dental restorations such as intra-coronal, extra-coronal, and fixed partial dentures. Tensile bond strength (TBS) and accurate marginal fit are the essential factors to determine the good clinical results in fixed prosthesis. The retentivity of the luting cements is assessed by their adhesive capacity over the tooth surface and metal surface. Generally, the adhesive ability has been evaluated with in vitro testing, with tensile bond tests. The failure of fixed prosthesis may be happened as a result of incomplete seating during cementation. Most research on cementation of crowns relates seating failure to the thickness of the cement film. The study is divided into four groups with 10 samples for each of the luting cement taken up for testing TBS and four groups with 5 samples for each luting agent chosen for assessing marginal fit. The results were tabulated and statistically analyzed. In this in vitro study, the TBS of luting cements, and marginal fit in relation to luting cements were tested by using appropriate testing devices. The TBS of cement is measured using universal testing machine, and the results are tabulated. The marginal gap that exists between the margin of the cast metal crown, and the finish line is measured using travelling microscope before and after cementation. The difference between these two values gives the discrepancy that is due to the film thickness of cement used for luting the restoration. The TBS value of zinc phosphate cement and glass ionomer cement were found to be almost same. The chemical adhesiveness of the glass ionomer with calcium ions of enamel and dentin may be the attributed reason (ionic bonding). In this study, the polycarboxylate is the one that showed low TBS, and it may be attributed to the weakness of the cement due to reduced film thickness, though this cement has a chemical bonding nature. The observation of results of marginal fit in this study is the increased gap found in zinc phosphate cement followed by resin cement, zinc polycarboxylate, and glass ionomer cement. It is agreeable to estimate the marginal fit of the restoration, which could be affected by the film thickness of the luting cement along with other factors.

Use of Incineration Solid Waste Bottom Ash as Cement Mixture in Cement Production

NASA Astrophysics Data System (ADS)

Jun, N. H.; Abdullah, M. M. A. B.; Jin, T. S.; Kadir, A. A.; Tugui, C. A.; Sandu, A. V.

2017-06-01

Incineration solid waste bottom ash was use to examine the suitability as a substitution in cement production. This study enveloped an innovative technology option for designing new equivalent cement that contains incineration solid waste bottom ash. The compressive strength of the samples was determined at 7, 14, 28 and 90 days. The result was compared to control cement with cement mixture containing incineration waste bottom ash where the result proved that bottom ash cement mixture able achieve its equivalent performance compared to control cement which meeting the requirement of the standards according to EN 196-1. The pozzolanic activity index of bottom ash cement mixture reached 0.92 at 28 days and 0.95 at 90 and this values can be concluded as a pozzolanic material with positive pozzolanic activity. Calcium hydroxide in Portland cement decreasing with the increasing replacement of bottom ash where the reaction occur between Ca(OH)2 and active SiO2.

The dynamic volume changes of polymerising polymethyl methacrylate bone cement.

PubMed

Muller, Scott D; Green, Sarah M; McCaskie, Andrew W

2002-12-01

The Swedish hip register found an increased risk of early revision of vacuum-mixed cemented total hip replacements. The influence of cement mixing technique on the dynamic volume change in polymerising PMMA is not well understood and may be relevant to this observation. Applying Archimedes' principle, we have investigated the dynamic volume changes in polymerising cement and determined the influence of mixing technique. All specimens showed an overall volume reduction: hand-mixed 3.4% and vacuum-mixed 6.0%. Regression analysis of sectional porosity and volume reduction showed a highly significant relationship. Hand-mixed porous cement showed a transient volume increase before solidification. However, vacuum-mixed cement showed a progressive volume reduction throughout polymerisation. Transient expansion of porous cement occurs at the critical time of micro-interlock formation, possibly improving fixation. Conversely, progressive volume reduction of vacuum-mixed cement throughout the formation of interlock may damage fixation. Stable fixation of vacuum-mixed cement may depend on additional techniques to offset the altered volumetric behaviour of vacuum-mixed cement.

Study on Cr(VI) Leaching from Cement and Cement Composites

PubMed Central

Palascakova, Lenka; Kanuchova, Maria

2018-01-01

This paper reports an experimental study on hexavalent chromium leaching from cement samples and cement composites containing silica fume and zeolite additions that were subjected to various leaching agents. The water-soluble Cr(VI) concentrations in cements ranged from 0.2 to 3.2 mg/kg and represented only 1.8% of the total chromium content. The presence of chromium compounds with both chromium oxidation states of III and VI was detected in the cement samples by X-ray photoelectron spectroscopy (XPS). Leaching tests were performed in a Britton-Robinson buffer to simulate natural conditions and showed increased dissolution of Cr(VI) up to 6 mg/kg. The highest amount of leached hexavalent chromium was detected after leaching in HCl. The findings revealed that the leaching of chromium from cements was higher by 55–80% than that from the cement composites. A minimum concentration was observed for all cement samples when studying the relationship between the soluble Cr(VI) and the cement storage time. PMID:29690550

Study on Cr(VI) Leaching from Cement and Cement Composites.

PubMed

Estokova, Adriana; Palascakova, Lenka; Kanuchova, Maria

2018-04-22

This paper reports an experimental study on hexavalent chromium leaching from cement samples and cement composites containing silica fume and zeolite additions that were subjected to various leaching agents. The water-soluble Cr(VI) concentrations in cements ranged from 0.2 to 3.2 mg/kg and represented only 1.8% of the total chromium content. The presence of chromium compounds with both chromium oxidation states of III and VI was detected in the cement samples by X-ray photoelectron spectroscopy (XPS). Leaching tests were performed in a Britton-Robinson buffer to simulate natural conditions and showed increased dissolution of Cr(VI) up to 6 mg/kg. The highest amount of leached hexavalent chromium was detected after leaching in HCl. The findings revealed that the leaching of chromium from cements was higher by 55⁻80% than that from the cement composites. A minimum concentration was observed for all cement samples when studying the relationship between the soluble Cr(VI) and the cement storage time.

Effects of Coal Gangue on Cement Grouting Material Properties

NASA Astrophysics Data System (ADS)

Liu, J. Y.; Chen, H. X.

2018-05-01

The coal gangue is one of the most abundant industrial solid wastes and pollute source of air and water. The use of coal gangue in the production of cement grouting material comforms to the basic state policy of environment protection and the circular using of natural resources. Through coal gangue processing experiment, coal gangue cement grouting materials making test, properties detection of properties and theoretical analysis, the paper studied the effects of coal gangue on the properties of cement grouting materials. It is found that at the range of 600 to 700 °C, the fluidity and the compressive and flexural strengths of the cement grouting materials increase with the rising up of the calcination temperatures of coal gangue. The optimum calcination temperature is around 700 °C. The part substitution of cement by the calcined coal gangue in the cement grouting material will improve the mechanical properties of the cement grouting material, even thought it will decrease its fluidity. The best substitution amount of cement by coal gangue is about 30%. The fluidity and the long term strength of the ordinary silicate cement grouting material is obviously higher than that of the sulphoaluminate cement one as well as that of the silicate-sulphoaluminate complex cement one.

Enhanced osteointegration of poly(methylmethacrylate) bone cements by incorporating strontium-containing borate bioactive glass

PubMed Central

Huang, Chengcheng; Zhang, Meng; Ruan, Changshun; Peng, Songlin; Li, Li; Liu, Wenlong; Wang, Ting; Li, Bing; Huang, Wenhai; Rahaman, Mohamed N.; Lu, William W.; Pan, Haobo

2017-01-01

Although poly(methylmethacrylate) (PMMA) cements are widely used in orthopaedics, they have numerous drawbacks. This study aimed to improve their bioactivity and osseointegration by incorporating strontium-containing borate bioactive glass (SrBG) as the reinforcement phase and bioactive filler of PMMA cement. The prepared SrBG/PMMA composite cements showed significantly decreased polymerization temperature when compared with PMMA and retained properties of appropriate setting time and high mechanical strength. The bioactivity of SrBG/PMMA composite cements was confirmed in vitro, evidenced by ion release (Ca, P, B and Sr) from SrBG particles. The cellular responses of MC3T3-E1 cells in vitro demonstrated that SrBG incorporation could promote adhesion, migration, proliferation and collagen secretion of cells. Furthermore, our in vivo investigation revealed that SrBG/PMMA composite cements presented better osseointegration than PMMA bone cement. SrBG in the composite cement could stimulate new-bone formation around the interface between the composite cement and host bone at eight and 12 weeks post-implantation, whereas PMMA bone cement only stimulated development of an intervening connective tissue layer. Consequently, the SrBG/PMMA composite cement may be a better alternative to PMMA cement in clinical applications and has promising orthopaedic applications by minimal invasive surgery. PMID:28615491

Characterization of PCC Cement by Addition of Napa Soil from Subdistrict Sarilamak 50 Kota District as Alternative Additional Material for Semen Padang

NASA Astrophysics Data System (ADS)

Mawardi, M.; Deyundha, D.; Zainul, R.; Zalmi P, R.

2018-04-01

The study has been conducted to determine characteristics of the portland composite cement by the addition of napa soil from Sarilamak subdistrict, 50 Kota District as an alternative additional material at PT. Semen Padang. Napa soil is a natural material highly containing silica and alumina minerals so that it can be one of material in producing cement. This study aims to determine the effect of napa soil on the quality of portland composite cement. Napa soil used in the variation compositions 0%, 4%, 8%, 12% and 16%, for control of cement used 8 % of pozzolan and 0 % of napa soil. Determination of cement quality by testing cement characteristics include blaine test, sieving, lost of ignition or LOI, insoluble residue, normal consistency, setting time and compressive strength. Cement was characterized using XRF. Fineness of cement decreases with the addition of napa soil. Lost of Ignition of cement decreased, while the insoluble residue increased with the addition of napa soil. Normal consistency of cement increasing, so does initial setting time and final setting time of cement. While the resultant compressive strength decreases with the addition of napa soil on 28 days, 342, 325, 307, 306, and 300 kg / cm2.

Enhanced osteointegration of poly(methylmethacrylate) bone cements by incorporating strontium-containing borate bioactive glass.

PubMed

Cui, Xu; Huang, Chengcheng; Zhang, Meng; Ruan, Changshun; Peng, Songlin; Li, Li; Liu, Wenlong; Wang, Ting; Li, Bing; Huang, Wenhai; Rahaman, Mohamed N; Lu, William W; Pan, Haobo

2017-06-01

Although poly(methylmethacrylate) (PMMA) cements are widely used in orthopaedics, they have numerous drawbacks. This study aimed to improve their bioactivity and osseointegration by incorporating strontium-containing borate bioactive glass (SrBG) as the reinforcement phase and bioactive filler of PMMA cement. The prepared SrBG/PMMA composite cements showed significantly decreased polymerization temperature when compared with PMMA and retained properties of appropriate setting time and high mechanical strength. The bioactivity of SrBG/PMMA composite cements was confirmed in vitro , evidenced by ion release (Ca, P, B and Sr) from SrBG particles. The cellular responses of MC3T3-E1 cells in vitro demonstrated that SrBG incorporation could promote adhesion, migration, proliferation and collagen secretion of cells. Furthermore, our in vivo investigation revealed that SrBG/PMMA composite cements presented better osseointegration than PMMA bone cement. SrBG in the composite cement could stimulate new-bone formation around the interface between the composite cement and host bone at eight and 12 weeks post-implantation, whereas PMMA bone cement only stimulated development of an intervening connective tissue layer. Consequently, the SrBG/PMMA composite cement may be a better alternative to PMMA cement in clinical applications and has promising orthopaedic applications by minimal invasive surgery. © 2017 The Author(s).

[Atmospheric emission of PCDD/Fs from modern dry processing cement kilns with preheating in the southwest area, China].

PubMed

Zhang, Xiao-Ling; Lu, Yi; Jian, Chuan; Guo, Zhi-Shun; Zhu, Ming-Ji; Deng, Li; Sun, Jing; Zhang, Qin

2014-01-01

Six cement kilns were measured for emissions of PCDD/Fs in the Southwest Area, China. The results indicated that the emission levels of PCDD/Fs were 0.0029-0.0062 ng-m(-3) (Average, 0.0043 ng X m(-3)) from cement kilns which did not burn solid waste, and 0.028 ng X m(-3) from co-processing sewage sludge in cement kiln. The levels of PCDD/Fs emissions from cement manufacturing in the Southwest Area were significantly below the national emissions standard (0.1 ng x m(-3)). Emission factors of PCDD/Fs from the six cement kilns varied between 0.0089 and 0.084 microg x t(-1) cement, which were near or below the lowest emission factor reported by UNEP in 2005. Moreover, the emission factor of PCDD/Fs from co-processing sewage sludge in cement kiln was 7.6 times of the average factors from the other five cement kilns. Moreover,congener distribution of PCDD/F in stack gas from the two types of cement kilns was very different. The results showed that modern dry process cement kilns with preheating have lower emissions of PCDD/Fs. This suggested that the product of co-processing solid waste in cement kilns should be largely enhanced in China in future.

Optimisation of a two-liquid component pre-filled acrylic bone cement system: a design of experiments approach to optimise cement final properties.

PubMed

Clements, James; Walker, Gavin; Pentlavalli, Sreekanth; Dunne, Nicholas

2014-10-01

The initial composition of acrylic bone cement along with the mixing and delivery technique used can influence its final properties and therefore its clinical success in vivo. The polymerisation of acrylic bone cement is complex with a number of processes happening simultaneously. Acrylic bone cement mixing and delivery systems have undergone several design changes in their advancement, although the cement constituents themselves have remained unchanged since they were first used. This study was conducted to determine the factors that had the greatest effect on the final properties of acrylic bone cement using a pre-filled bone cement mixing and delivery system. A design of experiments (DoE) approach was used to determine the impact of the factors associated with this mixing and delivery method on the final properties of the cement produced. The DoE illustrated that all factors present within this study had a significant impact on the final properties of the cement. An optimum cement composition was hypothesised and tested. This optimum recipe produced cement with final mechanical and thermal properties within the clinical guidelines and stated by ISO 5833 (International Standard Organisation (ISO), International standard 5833: implants for surgery-acrylic resin cements, 2002), however the low setting times observed would not be clinically viable and could result in complications during the surgical technique. As a result further development would be required to improve the setting time of the cement in order for it to be deemed suitable for use in total joint replacement surgery.

A comparison of retentive strength of implant cement depending on various methods of removing provisional cement from implant abutment

PubMed Central

Keum, Eun-Cheol

2013-01-01

PURPOSE This study evaluated the effectiveness of various methods for removing provisional cement from implant abutments, and what effect these methods have on the retention of prosthesis during the definitive cementation. MATERIALS AND METHODS Forty implant fixture analogues and abutments were embedded in resin blocks. Forty cast crowns were fabricated and divided into 4 groups each containing 10 implants. Group A was cemented directly with the definitive cement (Cem-Implant). The remainder were cemented with provisional cement (Temp-Bond NE), and classified according to the method for cleaning the abutments. Group B used a plastic curette and wet gauze, Group C used a rubber cup and pumice, and Group D used an airborne particle abrasion technique. The abutments were observed using a stereomicroscope after removing the provisional cement. The tensile bond strength was measured after the definitive cementation. Statistical analysis was performed using one-way analysis of variance test (α=.05). RESULTS Group B clearly showed provisional cement remaining, whereas the other groups showed almost no cement. Groups A and B showed a relatively smooth surface. More roughness was observed in Group C, and apparent roughness was noted in Group D. The tensile bond strength tests revealed Group D to have significantly the highest tensile bond strength followed in order by Groups C, A and B. CONCLUSION A plastic curette and wet gauze alone cannot effectively remove the residual provisional cement on the abutment. The definitive retention increased when the abutments were treated with rubber cup/pumice or airborne particle abraded to remove the provisional cement. PMID:24049563

In vitro evaluation of microleakage of various types of dental cements.

PubMed

Medić, Vesna; Obradović-Djuricić, Kosovka; Dodić, Slobodan; Petrović, Renata

2010-01-01

Microleakage is defined as the clinically undetectable seepage of oral fluids containing bacteria and debris between cement layer and tooth restoration. This in vitro study investigated the effect of different dental cements (zinc-phosphate, polycarboxylate, glass-ionomer and resin cement) on microleakage in different ceramic crown systems (metal ceramic crown, metal ceramic crown with a porcelain margin, Empress 2 and in Ceram all-ceramic crowns) fixed on extracted human teeth. One hundred and sixty intact human premolars were randomized to four groups of forty teeth each, according to the different ceramic crown systems. They were prepared in a standardized manner for metal-ceramic and all-ceramic crowns. Crowns were made following a standard laboratory technique, and each group of crowns were divided into four groups according to the different cement agents and cemented on their respective abutments. The specimens were subjected to thermocycling, placed in methylene blue solutions, embedded in resin blocks and vertically cut in the bucco-oral and meso-distal direction. The microleakage in the area of tooth-cement interface was defined as linear penetration of methylene blue and was determined with a microscope to assign microleakage scores using a five-point scale. A significant association was found between a cement type and degree of microleakage (p = 0.001). No statistically significant differences were found among the different ceramic crown systems luted with the same dental cement. The smallest degree of microleakage was observed in specimens luted with resin cement (X = 1.73), followed by glass-ionomer cement (X=2.45) and polycarboxylate cement (X = 3.20). The greatest degree of microleakage was detected in the crowns fixed with zincphosphate cement (X = 3.33). The investigated dental cements revealed different sealing abilities. The use of resin cement resulted in the percentage of 0 microleakage scores. Due to this feature, the resin cement is to be recommended in everyday clinical practice.

In-vitro study of resin-modified glass ionomer cements for cementation of orthodontic bands. Isolation, surplus removal and humidity as factors influencing the bond strength between enamel, cement and metal.

PubMed

Liebmann, S M; Jost-Brinkmann, P G

1999-01-01

The aim of this in vitro study was to investigate different light-cured and chemically cured resin-modified glass ionomer cements used for the cementation of orthodontic bands and to analyze various factors influencing the adhesive strength between enamel, cement and stainless steel. Four resin-modified glass ionomers (Fuji Ortho LC/GC, Fuji Duet/GC, Unitek Multi-Cure Glass Ionomer Orthodontic Band Cement/3M Unitek, Vitremer/3M) and 1 compomer (Band-Lok/Reliance) were examined. Flattened and polished bovine teeth embedded in polyurethane resin were used as enamel specimens. Before cementation, 50% of the specimens were moistened with the aerosol of an inhalation device, while the rest were dried with compressed air. Stainless steel cylinders (CrNi 18 10) were perpendicularly bonded onto the polished enamel using a custom-made cementation device and immediately topped with a pressure of 0.25 MPa. The cement was isolated with either Ketac Glaze/ESPE, Fuji Coat/GC, Cacao Butter/GC, Dryfoil/Jalenko or Final Varnish/VOCO, or was left uncoated. Eight minutes after the beginning of mixing, either the surplus cement was removed with a scalpel or surplus removal was simulated with ultrasound. After 24 hours storage in a water bath at 37 degrees C and 1,000 thermocycles the shear bond strength was determined. Significant differences with respect to the shear bond strength were found among the following cements, ranking from highest to lowest: Fuji Duet, Unitek cement > Fuji Ortho LC > Vitremer > Band-Lok. The application of a barrier coating significantly increased the shear bond strength of all cements except Fuji Ortho LC. The light-cured resin Ketac Glaze proved to be the most effective barrier coating. A dry enamel surface increased the bond strength of all investigated cements except Unitek cement. The use of ultrasound led to no significant reduction in shear bond strength in comparison with surplus removal with a scalpel.

Electron Trap Energy Distribution in ALD Al2O3, LaAl4Ox, and GdyAl2-yO3 Layers on Silicon

NASA Astrophysics Data System (ADS)

Wang, W. C.; Badylevich, M.; Adelmann, C.; Swerts, J.; Kittl, J. A.; Afanas'ev, V. V.

2012-12-01

The energy distribution of electron trap density in atomic layer deposited Al2O3, LaAl4Ox and GdyAl2-yO3 insulating layers was studied by using the exhaustive photodepopulation spectroscopy. Upon filling the traps by electron tunneling from Si substrate, a broad energy distribution of trap levels in the energy range 2-4 eV is found in all studied insulators with trap densities in the range of 1012 cm-2eV-1. The incorporation of La and Gd cations reduces the trap density in aluminate layers as compared to Al2O3. Crystallization of the insulator by the post-deposition annealing is found to increase the trap density while the energy distribution remains unchanged. The similar trap spectra in the Al2O3 and La or Gd aluminate layers suggest the common nature of the traps, probably originating from imperfections in the AlOx sub-network.

Static and Dynamic Compaction of CL-20 Powders

NASA Astrophysics Data System (ADS)

Cooper, Marcia; Brundage, Aaron; Dudley, Evan

2009-06-01

Hexanitrohexaazaisowurtzitane (CL-20) powders were compacted under quasi-static and dynamic loading conditions. A uniaxial compression apparatus quasi-statically compressed the powders to 90% theoretical maximum density with applied stresses up to 0.5 GPa. Dynamic compaction measurements using low-density pressings (62-70% theoretical maximum density) were obtained in a single-stage gas gun at impact velocities between 0.17-0.70 km/s. Experiments were conducted in a reverse ballistic arrangement in which the CL-20 ladened projectile impacted a target consisting of an aluminized window. VISAR-measured particle velocities at the explosive-window interface determined the shock Hugoniot states for pressures up to 0.9 GPa. The powder compaction behavior is found to be stiffer under dynamic loading than under quasi-static loading. Additional gas gun tests were conducted in which the low-density CL-20 pressings were confined within a target cup by the aluminized window. This arrangement enabled temporal measurement of the transmitted wave profiles in which elastic wave precursors were observed.

Coatings for directional eutectics

NASA Technical Reports Server (NTRS)

Rairden, J. R.; Jackson, M. R.

1976-01-01

Significant advances have been made in the development of an environmentally stable coating for a very high strength, directionally solidified eutectic alloy designated NiTaC-13. Three duplex (two-layer) coatings survived 3,000 hours on a cyclic oxidation test (1,100 C to 90 C). These coatings were fabricated by first depositing a layer of NiCrAl(Y) by vacuum evaporation from an electron beam heated source, followed by depositing an aluminizing overlayer. The alloy after exposure with these coatings was denuded of carbide fibers at the substrate/coating interface. It was demonstrated that TaC fiber denudation can be greatly retarded by applying a carbon-bearing coating. The coating was applied by thermal spraying followed by aluminization. Specimens coated with NiCrAlCY+Al survived over 2,000 hours in the cyclic oxidation test with essentially no TaC denudation. Coating ductility was studied for coated and heat-treated bars, and stress rupture life at 871 C and 1,100 C was determined for coated and cycled bars.

Recent progress in advanced optical materials based on gadolinium aluminate garnet (Gd3Al5O12)

PubMed Central

Li, Ji-Guang; Sakka, Yoshio

2015-01-01

This review article summarizes the recent achievements in stabilization of the metastable lattice of gadolinium aluminate garnet (Gd3Al5O12, GAG) and the related developments of advanced optical materials, including down-conversion phosphors, up-conversion phosphors, transparent ceramics, and single crystals. Whenever possible, the materials are compared with their better known YAG and LuAG counterparts to demonstrate the merits of the GAG host. It is shown that novel emission features and significantly improved luminescence can be attained for a number of phosphor systems with the more covalent GAG lattice and the efficient energy transfer from Gd3+ to the activator. Ce3+ doped GAG-based single crystals and transparent ceramics are also shown to simultaneously possess the advantages of high theoretical density, fast scintillation decay, and high light yields, and hold great potential as scintillators for a wide range of applications. The unresolved issues are also pointed out. PMID:27877750

Impact initiation of reactive aluminized fluorinated acrylic nanocomposites

DOE PAGES

White, Bradley W.; Crouse, Christopher A.; Spowart, Jonathan E.; ...

2016-04-18

The initiation of aluminized fluorinated acrylic (AlFA) nanocomposites during modified Taylor impact tests was investigated. Samples were impacted against a steel or sapphire anvil at a nominal velocity of 150 m/s. A framing camera was used to capture head-on and side-profile impact images for the sapphire window and steel plate rigid anvils, respectively. Correlations were drawn between both experimental setups to determine the initiation locations and reaction times. Reactions were found to initiate at an intermediate radius on the impact face of the pellet at a time near full compaction. From simulations, the highest strains and temperatures were found atmore » radii similar to those observed in experiments at the time of ignition. Off-normal impacts produced higher localized straining and temperatures on one-half of the pellet. As a result, the copper projectile, used for delivery, was revealed to aid in a shear assisted reaction by helping to drive the pellet material outward as the projectile deformed radially.« less

Hot corrosion evaluation of aluminide coated superalloys in support of an ASTM Round Robin program

NASA Technical Reports Server (NTRS)

Santoro, G.

1975-01-01

Commercial aluminized coatings on substrates were hot corroded at 900 C in a 0.3 Mach burner rig with 5 ppm synthetic sea salt and at two cycling frequencies. Extensive post-exposure examinations were conducted on the corroded specimens such as metallography, X-ray diffraction, scanning electron microscopy, microprobe raster scans, and spectrographic analyses. Thermodynamic calculations were made of the equilibrium burner flame composition and the calculations were compared to the experimental findings. It was found that localized spalling of the coatings preceded coating failure. It is suggested that the spalling of the coatings is due to the formation of localized stresses caused by the depletion of chromium and aluminum in the coating or the enrichment of the coating with sulfur. For the materials and test conditions investigated, it was found that coating life is dependent only upon the initial coating thickness and not on the type of aluminized coating, the substrate, or the cycle frequency.

Immobilization of LiCl-Li 2 O pyroprocessing salt wastes in chlorosodalite using glass-bonded hydrothermal and salt-occlusion methods

DOE Office of Scientific and Technical Information (OSTI.GOV)

Riley, Brian J.; Peterson, Jacob A.; Kroll, Jared O.

In this study, salt occlusion and hydrothermal processes were used to make chlorosodalite through reaction with a high-LiCl salt simulating a waste stream following pyrochemical treatment of oxide-based used nuclear fuel. Some products were reacted with glass binders to increase chlorosodalite yield through alkali ion exchange and aide in densification. Hydrothermal processes included reaction of the salt simulant in an acid digestion vessel with either zeolite 4A or sodium aluminate and colloidal silica. Chlorosodalite yields in the crystalline products were nearly complete in the glass-bonded materials at values of 100 mass% for the salt-occlusion method, up to 99.0 mass% formore » the hydrothermal synthesis with zeolite 4A, and up to 96 mass% for the hydrothermal synthesis with sodium aluminate and colloidal silica. These results show promise for using chemically stable chlorosodalite to immobilize oxide reduction salt wastes.« less

Tracing high-pressure metamorphism in marbles: Phase relations in high-grade aluminous calcite-dolomite marbles from the Greek Rhodope massif in the system CaO-MgO-Al 2O 3-SiO 2-CO 2 and indications of prior aragonite

NASA Astrophysics Data System (ADS)

Proyer, A.; Mposkos, E.; Baziotis, I.; Hoinkes, G.

2008-08-01

Four different types of parageneses of the minerals calcite, dolomite, diopside, forsterite, spinel, amphibole (pargasite), (Ti-)clinohumite and phlogopite were observed in calcite-dolomite marbles collected in the Kimi-Complex of the Rhodope Metamorphic Province (RMP). The presence of former aragonite can be inferred from carbonate inclusions, which, in combination with an analysis of phase relations in the simplified system CaO-MgO-Al 2O 3-SiO 2-CO 2 (CMAS-CO 2) show that the mineral assemblages preserved in these marbles most likely equilibrated at the aragonite-calcite transition, slightly below the coesite stability field, at ca. 720 °C, 25 kbar and aCO 2 ~ 0.01. The thermodynamic model predicts that no matter what activity of CO 2, garnet has to be present in aluminous calcite-dolomite-marble at UHP conditions.

Micro-stress dominant displacive reconstructive transition in lithium aluminate

DOE Office of Scientific and Technical Information (OSTI.GOV)

Hu, Qiwei; Yan, Xiaozhi; Zhang, Leilei

It is supposed that diffusive reconstructive transitions usually take place under hydrostatic pressure or low stresses, and displacive reconstructive phase transitions easily occur at nonhydrostatic pressure. Here, by in-situ high pressure synchrotron X-ray diffraction and single-crystal Raman scattering studies on lithium aluminate at room temperature, we show that the reconstructive transition mechanism is dependent on the internal microscopic stresses rather than the macroscopic stresses. In this case, even hydrostatic pressure can favor the displacive transition if the compressibility of crystal is anisotropic. During hydrostatic compression, γ-LiAlO{sub 2} transforms to δ-LiAlO{sub 2} at about 4 GPa, which is much lower than thatmore » in previous nonhydrostatic experiments (above 9 GPa). In the region where both phases coexist, there are enormous microscopic stresses stemming from the lattice mismatch, suggesting that this transition is displacive. Furthermore, the atomic picture is drawn with the help of the shear Raman modes.« less

Three-dimensionally Ordered Macroporous Structure Enabled Nanothermite Membrane of Mn2O3/Al

PubMed Central

Zheng, Guoqiang; Zhang, Wenchao; Shen, Ruiqi; Ye, Jiahai; Qin, Zhichun; Chao, Yimin

2016-01-01

Mn2O3 has been selected to realize nanothermite membrane for the first time in the literature. Mn2O3/Al nanothermite has been synthesized by magnetron sputtering a layer of Al film onto three-dimensionally ordered macroporous (3DOM) Mn2O3 skeleton. The energy release is significantly enhanced owing to the unusual 3DOM structure, which ensures Al and Mn2O3 to integrate compactly in nanoscale and greatly increase effective contact area. The morphology and DSC curve of the nanothermite membrane have been investigated at various aluminizing times. At the optimized aluminizing time of 30 min, energy release reaches a maximum of 2.09 kJ∙g−1, where the Al layer thickness plays a decisive role in the total energy release. This method possesses advantages of high compatibility with MEMS and can be applied to other nanothermite systems easily, which will make great contribution to little-known nanothermite research. PMID:26935405

Lightweight Thermal Insulation for a Liquid-Oxygen Tank

NASA Technical Reports Server (NTRS)

Willen, G. Scott; Lock, Jennifer; Nieczkoski, Steve

2005-01-01

A proposed lightweight, reusable thermal-insulation blanket has been designed for application to a tank containing liquid oxygen, in place of a non-reusable spray-on insulating foam. The blanket would be of the multilayer-insulation (MLI) type and equipped with a pressure-regulated nitrogen purge system. The blanket would contain 16 layers in two 8-layer sub-blankets. Double-aluminized polyimide 0.3 mil (.0.008 mm) thick was selected as a reflective shield material because of its compatibility with oxygen and its ability to withstand ionizing radiation and high temperature. The inner and outer sub-blanket layers, 1 mil (approximately equals 0.025 mm) and 3 mils (approximately equals 0.076 mm) thick, respectively, would be made of the double-aluminized polyimide reinforced with aramid. The inner and outer layers would provide structural support for the more fragile layers between them and would bear the insulation-to-tank attachment loads. The layers would be spaced apart by lightweight, low-thermal-conductance netting made from polyethylene terephthalate.

Apollo 16 site geology and impact melts - Implications for the geologic history of the lunar highlands

DOE Office of Scientific and Technical Information (OSTI.GOV)

Spudis, P.D.

1984-11-15

The geology of the Apollo 16 site is reconsidered on the basis of data from photogeology, geochemical remote sensing, and lunar samples. The site possesses an upper surface of anorthositic gabbro and related rocks. Mafic components were deposited as basin ejecta. The events involved in its geological evolution were the Nectaris impact and the Imbrium impact. The role of large, local craters in the history of the region was to serve as topographic depressions to accumulate basin ejecta. The most abundant melt composition at Apollo 16 is an aluminous variety of LKFM basalt supplied by the Nectaris impact as ejectedmore » basin impact melt. The mafic LKFM melt may have been supplied by the Imbrium impact. More aluminous melt groups are probably derived from local, small craters. The remainder of the deposits in the region are composed of anorthositic clastic debris derived from the Nectaris basin, the local crustal substrate, and Imbrium and other basins.« less

Cr6+-containing phases in the system CaO-Al2O3-CrO42--H2O at 23 °C

NASA Astrophysics Data System (ADS)

Pöllmann, Herbert; Auer, Stephan

2012-01-01

Synthesis and investigation of lamellar calcium aluminium hydroxy salts was performed to study the incorporation of chromate ions in the interlayer of lamellar calcium aluminium hydroxy salts. Different AFm-phases (calcium aluminate hydrate with alumina, ferric oxide, mono-anion phase) containing chromate were synthesized. These AFm-phases belong to the group of layered double hydroxides (LDHs). 3CaO·Al2O3·CaCrO4·nH2O and C3A·1/2Ca(OH)2·1/2CaCrO4·12H2O were obtained as pure phases and their different distinct interlayer water contents and properties determined. Solid solution of chromate-containing phases and tetracalcium-aluminate-hydrate (TCAH) were studied. The uptake of chromate into TCAH from solutions was proven. Chromate contents in solution decrease to <0.2 mg/l.

Numerical simulation of double front detonations in a non-ideal explosive with varying aluminum concentration

NASA Astrophysics Data System (ADS)

Kim, Wuhyun; Gwak, Min-Cheol; Yoh, Jack; Seoul National University Team

2017-06-01

The performance characteristics of aluminized HMX are considered by varying the aluminum (Al) concentration in a hybrid non-ideal detonation model. Two cardinal observations are reported: a decrease in detonation velocity with an increase in Al concentration and a double front detonation (DFD) feature when aerobic Al reaction occurs behind the front. While experimental studies have been reported on the effect of Al concentration on both gas-phase and solid-phase detonations, the numerical investigations were limited to only gas-phase detonation for the varying Al concentration. In the current study, a two-phase model is utilized for understanding the volumetric effects of Al concentration in the condensed phase detonations. A series of unconfined and confined rate sticks are considered for characterizing the performance of aluminized HMX with a maximum Al concentration of 50%. The simulated results are compared with the experimental data for 5%-25% concentrations, and the formation of DFD structure under varying Al concentration (0%-50%) in HMX is investigated.

Recent progress in advanced optical materials based on gadolinium aluminate garnet (Gd3Al5O12)

NASA Astrophysics Data System (ADS)

Li, Ji-Guang; Sakka, Yoshio

2015-02-01

This review article summarizes the recent achievements in stabilization of the metastable lattice of gadolinium aluminate garnet (Gd3Al5O12, GAG) and the related developments of advanced optical materials, including down-conversion phosphors, up-conversion phosphors, transparent ceramics, and single crystals. Whenever possible, the materials are compared with their better known YAG and LuAG counterparts to demonstrate the merits of the GAG host. It is shown that novel emission features and significantly improved luminescence can be attained for a number of phosphor systems with the more covalent GAG lattice and the efficient energy transfer from Gd3+ to the activator. Ce3+ doped GAG-based single crystals and transparent ceramics are also shown to simultaneously possess the advantages of high theoretical density, fast scintillation decay, and high light yields, and hold great potential as scintillators for a wide range of applications. The unresolved issues are also pointed out.

Impact initiation of reactive aluminized fluorinated acrylic nanocomposites

DOE Office of Scientific and Technical Information (OSTI.GOV)

White, Bradley W.; Crouse, Christopher A.; Spowart, Jonathan E.

The initiation of aluminized fluorinated acrylic (AlFA) nanocomposites during modified Taylor impact tests was investigated. Samples were impacted against a steel or sapphire anvil at a nominal velocity of 150 m/s. A framing camera was used to capture head-on and side-profile impact images for the sapphire window and steel plate rigid anvils, respectively. Correlations were drawn between both experimental setups to determine the initiation locations and reaction times. Reactions were found to initiate at an intermediate radius on the impact face of the pellet at a time near full compaction. From simulations, the highest strains and temperatures were found atmore » radii similar to those observed in experiments at the time of ignition. Off-normal impacts produced higher localized straining and temperatures on one-half of the pellet. As a result, the copper projectile, used for delivery, was revealed to aid in a shear assisted reaction by helping to drive the pellet material outward as the projectile deformed radially.« less

Criteria for Remote Sensing Detection of Sulfate Cemented Soils on Mars

NASA Technical Reports Server (NTRS)

Cooper, Christopher D.; Mustard, John F.

2000-01-01

Spectral measurements of loose and cemented mixtures of palagonitic soil and sulfates were made to determine whether cemented soils could be identified on Mars. Cemented MgSO4 mixtures exhibit an enhanced 9 micron sulfate fundamental compared to gypsum mixtures due to more diffuse and pervasive cementing.

21 CFR 888.4200 - Cement dispenser.

Code of Federal Regulations, 2014 CFR

2014-04-01

... 21 Food and Drugs 8 2014-04-01 2014-04-01 false Cement dispenser. 888.4200 Section 888.4200 Food... DEVICES ORTHOPEDIC DEVICES Surgical Devices § 888.4200 Cement dispenser. (a) Identification. A cement dispenser is a nonpowered syringe-like device intended for use in placing bone cement (§ 888.3027) into...

21 CFR 888.4200 - Cement dispenser.

Code of Federal Regulations, 2013 CFR

2013-04-01

... 21 Food and Drugs 8 2013-04-01 2013-04-01 false Cement dispenser. 888.4200 Section 888.4200 Food... DEVICES ORTHOPEDIC DEVICES Surgical Devices § 888.4200 Cement dispenser. (a) Identification. A cement dispenser is a nonpowered syringe-like device intended for use in placing bone cement (§ 888.3027) into...

21 CFR 888.4200 - Cement dispenser.

Code of Federal Regulations, 2011 CFR

2011-04-01

... 21 Food and Drugs 8 2011-04-01 2011-04-01 false Cement dispenser. 888.4200 Section 888.4200 Food... DEVICES ORTHOPEDIC DEVICES Surgical Devices § 888.4200 Cement dispenser. (a) Identification. A cement dispenser is a nonpowered syringe-like device intended for use in placing bone cement (§ 888.3027) into...

21 CFR 888.4200 - Cement dispenser.

Code of Federal Regulations, 2012 CFR

2012-04-01

... 21 Food and Drugs 8 2012-04-01 2012-04-01 false Cement dispenser. 888.4200 Section 888.4200 Food... DEVICES ORTHOPEDIC DEVICES Surgical Devices § 888.4200 Cement dispenser. (a) Identification. A cement dispenser is a nonpowered syringe-like device intended for use in placing bone cement (§ 888.3027) into...

40 CFR 146.86 - Injection well construction requirements.

Code of Federal Regulations, 2011 CFR

2011-07-01

... stages. (4) Circulation of cement may be accomplished by staging. The Director may approve an alternative... injection tubing and long string casing. (b) Casing and cementing of Class VI wells. (1) Casing and cement... confining zone(s); (viii) Type or grade of cement and cement additives; and (ix) Quantity, chemical...

Test using expansive cement in cement stabilized base to eliminate or prevent cracking : experimental projects.

DOT National Transportation Integrated Search

1975-08-01

The purpose of this study was to determine the feasibility of using an : expansive cement, TXI 4C Chem Comp, in lieu of the regular Type I Portland : Cement in a cement stabilized gravel screenings base so as to eliminate : or reduce cracks associate...

21 CFR 888.4200 - Cement dispenser.

Code of Federal Regulations, 2010 CFR

2010-04-01

... 21 Food and Drugs 8 2010-04-01 2010-04-01 false Cement dispenser. 888.4200 Section 888.4200 Food... DEVICES ORTHOPEDIC DEVICES Surgical Devices § 888.4200 Cement dispenser. (a) Identification. A cement dispenser is a nonpowered syringe-like device intended for use in placing bone cement (§ 888.3027) into...

75 FR 7305 - Drake Switching Company, LLC-Operation Exemption- Drake Cement, LLC

Federal Register 2010, 2011, 2012, 2013, 2014

2010-02-18

... Switching Company, LLC--Operation Exemption-- Drake Cement, LLC Drake Switching Company, LLC (DSC), a... and operated by Drake Cement, LLC.\\1\\ \\1\\ Drake Cement, LLC filed a verified notice of exemption to acquire these track in STB Finance Docket No. 35350, Drake Cement, LLC--Acquisition Exemption--Clarkdale...

Retardation effect of different alcohols on the cement coagulation in polycarboxylate- and naphthalene-based cement admixtures

NASA Astrophysics Data System (ADS)

Huang, S. M.; Zhou, F. L.

2017-12-01

Alcohol has great potential to delay the coagulation of cement. The effects of alcohol on paste fluidity and normal consistency coagulation time have been studied for polycarboxylate superplasticizer and naphthene cement admixture. Seven alcohols were combined with polycarboxylate superplasticizer and naphthene at a concentration of 0.01-0.09%, respectively, including n-propanol, methanol, sorbitol, ethylene glycol, glycerol, ethanol, and mannitol. The fluidity and normal consistency coagulation time of each cement admixture were measured. The performance of both polycarboxylate superplasticizer and naphthene cement admixtures were compared to develop cement admixture with delayed coagulation.

Thermally conductive cementitious grout for geothermal heat pump systems

DOEpatents

Allan, Marita

2001-01-01

A thermally conductive cement-sand grout for use with a geothermal heat pump system. The cement sand grout contains cement, silica sand, a superplasticizer, water and optionally bentonite. The present invention also includes a method of filling boreholes used for geothermal heat pump systems with the thermally conductive cement-sand grout. The cement-sand grout has improved thermal conductivity over neat cement and bentonite grouts, which allows shallower bore holes to be used to provide an equivalent heat transfer capacity. In addition, the cement-sand grouts of the present invention also provide improved bond strengths and decreased permeabilities. The cement-sand grouts can also contain blast furnace slag, fly ash, a thermoplastic air entraining agent, latex, a shrinkage reducing admixture, calcium oxide and combinations thereof.

Vibrational investigation of calcium-silicate cements for endodontics in simulated body fluids

NASA Astrophysics Data System (ADS)

Taddei, Paola; Modena, Enrico; Tinti, Anna; Siboni, Francesco; Prati, Carlo; Gandolfi, Maria Giovanna

2011-05-01

Calcium-silicate MTA (Mineral Trioxide Aggregate) cements have been recently developed for oral and endodontic surgery. This study was aimed at investigating commercial (White ProRoot MTA, White and Grey MTA-Angelus) and experimental (wTC-Bi) accelerated calcium-silicate cements with regards to composition, hydration products and bioactivity upon incubation for 1-28 days at 37 °C, in Dulbecco's Phosphate Buffered Saline (DPBS). Deposits on the surface of the cements and the composition changes during incubation were investigated by micro-Raman and ATR/FT-IR spectroscopy, and pH measurements. Vibrational techniques disclosed significant differences in composition among the unhydrated cements, which significantly affected the bioactivity as well as pH, and hydration products of the cements. After one day in DPBS, all the cements were covered by a more or less homogeneous layer of B-type carbonated apatite. The experimental cement maintained a high bioactivity, only slightly lower than the other cements and appears a valid alternative to commercial cements, in view of its adequate setting time properties. The bioactivity represents an essential property to favour bone healing and makes the calcium-silicate cements the gold standard materials for root-apical endodontic surgery.

Influence of Blended Cements with Calcareous Fly Ash on Chloride Ion Migration and Carbonation Resistance of Concrete for Durable Structures.

PubMed

Glinicki, Michał A; Jóźwiak-Niedźwiedzka, Daria; Gibas, Karolina; Dąbrowski, Mariusz

2016-01-02

The objective of this paper is to examine the possible use of new blended cements containing calcareous fly ash in structural concrete, potentially adequate for structural elements of nuclear power plants. The investigation included five new cements made with different contents of non-clinker constituents: calcareous fly ash, siliceous fly ash, ground granulated blastfurnace slag, and a reference cement-ordinary Portland cement. The influence of innovative cements on the resistance of concrete to chloride and carbonation exposure was studied. Additionally, an evaluation of the microstructure was performed using optical microscopy on concrete thin sections. Test results revealed a substantial improvement of the resistance to chloride ion penetration into concrete containing blended cements. The resistance was higher for increased clinker replacement levels and increased with curing time. However, concrete made with blended cements exhibited higher depth of carbonation than the Portland cement concrete, except the Portland-fly ash cement with 14.3% of calcareous fly ash. The thin sections analysis confirmed the values of the carbonation depth obtained from the phenolphthalein test. Test results indicate the possible range of application for new cements containing calcareous fly ash.

The contemporary cement cycle of the United States

USGS Publications Warehouse

Kapur, A.; Van Oss, H. G.; Keoleian, G.; Kesler, S.E.; Kendall, A.

2009-01-01

A country-level stock and flow model for cement, an important construction material, was developed based on a material flow analysis framework. Using this model, the contemporary cement cycle of the United States was constructed by analyzing production, import, and export data for different stages of the cement cycle. The United States currently supplies approximately 80% of its cement consumption through domestic production and the rest is imported. The average annual net addition of in-use new cement stock over the period 2000-2004 was approximately 83 million metric tons and amounts to 2.3 tons per capita of concrete. Nonfuel carbon dioxide emissions (42 million metric tons per year) from the calcination phase of cement manufacture account for 62% of the total 68 million tons per year of cement production residues. The end-of-life cement discards are estimated to be 33 million metric tons per year, of which between 30% and 80% is recycled. A significant portion of the infrastructure in the United States is reaching the end of its useful life and will need to be replaced or rehabilitated; this could require far more cement than might be expected from economic forecasts of demand for cement. ?? 2009 Springer Japan.

Effect of cements on fracture resistance of monolithic zirconia crowns

PubMed Central

Nakamura, Keisuke; Mouhat, Mathieu; Nergård, John Magnus; Lægreid, Solveig Jenssen; Kanno, Taro; Milleding, Percy; Örtengren, Ulf

2016-01-01

Abstract Objectives The present study investigated the effect of cements on fracture resistance of monolithic zirconia crowns in relation to their compressive strength. Materials and methods Four different cements were tested: zinc phosphate cement (ZPC), glass-ionomer cement (GIC), self-adhesive resin-based cement (SRC) and resin-based cement (RC). RC was used in both dual cure mode (RC-D) and chemical cure mode (RC-C). First, the compressive strength of each cement was tested according to a standard (ISO 9917-1:2004). Second, load-to-failure test was performed to analyze the crown fracture resistance. CAD/CAM-produced monolithic zirconia crowns with a minimal thickness of 0.5 mm were prepared and cemented to dies with each cement. The crown–die samples were loaded until fracture. Results The compressive strength of SRC, RC-D and RC-C was significantly higher than those of ZPC and GIC (p < 0.05). However, there was no significant difference in the fracture load of the crown between the groups. Conclusion The values achieved in the load-to-failure test suggest that monolithic zirconia crowns with a minimal thickness of 0.5 mm may have good resistance against fracture regardless of types of cements. PMID:27335900

Influence of Photoinitiator on Accelerated Artificial Aging and Bond Strength of Experimental Resin Cements.

PubMed

Righi, Helouise; Costa, Ana Rosa; Oliveira, Dayane Carvalho Ramos Salles de; Abuna, Gabriel Flores; Sinhoreti, Mario Alexandre Coelho; Naufel, Fabiana Scarparo

2018-01-01

The goal of this study was to evaluate in vitro the effect of the photoinitiator phenylpropanedione (PPD), alone or combined with camphorquinone (CQ), on color stability of photoactivated resin cements and their bond strength to ceramics using a micro-shear test. Four resin cements were used: a commercial brand cement (RelyX Veneer®) and 3 experimental cements with different types and concentration of photoinitiators. For color analysis, ceramic discs were cemented on bovine dentin specimens to simulate indirect restorations (n=8) and were exposed to UV for 120 h and tested for color alteration using a reflectance spectrophotometer and the CIEL*a*b* system. Data were analyzed by Anova and Tukey's test at 5% significance level. The color test results did not present statistically significant difference for the ∆E for all the studied cements, neither for ∆L, ∆a and ∆b. For the bond strength, all the studied cements showed statistically significant differences to each other, with the highest result for the RelyX Veneer® (29.07 MPa) cement, followed by the cement with CQ (21.74 MPa) and CQ+PPD (19.09 MPa) cement; the lowest result was obtained by the cement using only PPD as a photoinitiator (13.99 MPa). So, based on the studied parameters, PPD was not advantageous as photoinitiator of resin cements, because it showed a low value of bond strength to the ceramics and no superior color stability.

Incidence of undetected cement on CAD/CAM monolithic zirconia crowns and customized CAD/CAM implant abutments. A prospective case series.

PubMed

Wasiluk, Grzegorz; Chomik, Ewa; Gehrke, Peter; Pietruska, Małgorzata; Skurska, Anna; Pietruski, Jan

2017-07-01

The aim of this study was to assess the frequency of cement residues after cementation of CAD/CAM monolithic zirconia crowns on customized CAD/CAM titanium abutments. Sixty premolars and molars were restored on Astra Tech Osseospeed TX ™ implants using single monolithic zirconia crowns fixed on two types of custom-made abutments: Atlantis ™ titanium or Atlantis ™ Gold Hue. Occlusal openings providing access to the abutment screws were designed for retrievability of the crown/abutment connection. After fixation with glass ionomer cement, the crown/abutment units were unscrewed to evaluate the presence of residual cement. Dichotomous assessment of the presence or absence of cement at the crown/abutment unit and peri-implant tissues was performed. Clinically undetected cement excess was visible on 44 of 60 restorations (73.3%). There was no interdependency between residual cement presence and implant location or diameter. However, a dependency between the presence of residual cement and the aspect of the abutment/crown connection could be noted. The majority of the residues were observed on the distal (17.9%) and mesial (15%) aspects. While on the palatal/lingual aspect, the cement was visible in 8.8%; only 3.4% of all surfaces displayed cement residues. Within the limitations of the study, it can be concluded that the use of customized CAD/CAM abutments do not guarantee avoidance of subgingival cement residues after crown cementation. © 2016 John Wiley & Sons A/S. Published by John Wiley & Sons Ltd.

Influence of technique and manipulation on self-adhesive resin cements used to cement intraradicular posts.

PubMed

Shiratori, Fábio Kenji; Valle, Accácio Lins do; Pegoraro, Thiago Amadei; Carvalho, Ricardo Marins; Pereira, Jefferson Ricardo

2013-07-01

Resin cements are widely used to cement intraradicular posts, but bond strength is significantly influenced by the technique and material used for cementation. The purpose of this study was to evaluate the bond strength of 3 self-adhesive cements used to cement intraradicular glass fiber posts. The cements all required different application and handling techniques. Forty-five human maxillary canines were selected and randomly divided into 3 groups n= 15 by drawing lots: Group BIS - Biscem, Group BRE - Breeze, and Group MAX - Maxcem. Each group was divided into 3 subgroups according to application and handling techniques: Sub-group A - Automix/Point tip applicator, Sub-group L - Handmix/Lentulo, and Sub-group C - Handmix/Centrix. Cementation of the posts was performed according to the manufacturers' instructions. The push-out test was performed with a crosshead speed of 0.5 mm/min, and bond strength was expressed in megapascals. The results were evaluated by 2-way ANOVA and the all pairwise multiple comparison procedures (Tukey test) (α=.05). Breeze cement showed the highest average for the subgroups A, L, and C when compared to the Biscem cement and Maxcem Elite (P<.05). Statistically significant differences among the subgroups were only observed for Biscem. This study shows that application and handling techniques may influence the bond strength of different self-adhesive cements when used for intraradicular post cementation. Copyright © 2013 The Editorial Council of the Journal of Prosthetic Dentistry. Published by Mosby, Inc. All rights reserved.

Comparative evaluation of marginal leakage of provisional crowns cemented with different temporary luting cements: In vitro study.

PubMed

Arora, Sheen Juneja; Arora, Aman; Upadhyaya, Viram; Jain, Shilpi

2016-01-01

As, the longevity of provisional restorations is related to, a perfect adaptation and a strong, long-term union between restoration and teeth structures, therefore, evaluation of marginal leakage of provisional restorative materials luted with cements using the standardized procedures is essential. To compare the marginal leakage of the provisional crowns fabricated from Autopolymerizing acrylic resin crowns and bisphenol A-glycidyl dimethacrylate (BIS-GMA) resin crowns. To compare the marginal leakage of the provisional crowns fabricated from autopolymerizing acrylic resin crowns and BIS-GMA resin crowns cemented with different temporary luting cements. To compare the marginal leakage of the provisional crowns fabricated from autopolymerizing acrylic resin (SC-10) crowns cemented with different temporary luting cements. To compare the marginal leakage of the provisional crowns fabricated from BIS-GMA resin crowns (Protemp 4) cemented with different temporary luting cements. Freshly extracted 60 maxillary premolars of approximately similar dimensions were mounted in dental plaster. Tooth reduction with shoulder margin was planned to use a customized handpiece-holding jig. Provisional crowns were prepared using the wax pattern fabricated from computer aided designing/computer aided manufacturing milling machine following the tooth preparation. Sixty provisional crowns were made, thirty each of SC-10 and Protemp 4 and were then cemented with three different luting cements. Specimens were thermocycled, submerged in a 2% methylene blue solution, then sectioned and observed under a stereomicroscope for the evaluation of marginal microleakage. A five-level scale was used to score dye penetration in the tooth/cement interface and the results of this study was analyzed using the Chi-square test, Mann-Whitney U-test, Kruskal-Wallis H-test and the results were statistically significant P < 0.05 the power of study - 80%. Marginal leakage was significant in both provisional crowns cemented with three different luting cements along the axial walls of teeth (P < 0.05) confidence interval - 95%. The temporary cements with eugenol showed more microleakage than those without eugenol. SC-10 crowns showed more microleakage compared to Protemp 4 crowns. SC-10 crowns cemented with Kalzinol showed maximum microleakage and Protemp 4 crowns cemented with HY bond showed least microleakage.

Effective Permeability Change in Wellbore Cement with Carbon Dioxide Reaction

DOE Office of Scientific and Technical Information (OSTI.GOV)

Um, Wooyong; Jung, Hun Bok; Martin, Paul F.

2011-11-01

Portland cement, a common sealing material for wellbores for geological carbon sequestration was reacted with CO{sub 2} in supercritical, gaseous, and aqueous phases at various pressure and temperature conditions to simulate cement-CO{sub 2} reaction along the wellbore from carbon injection depth to the near-surface. Hydrated Portland cement columns (14 mm diameter x 90 mm length; water-to-cement ratio = 0.33) including additives such as steel coupons and Wallula basalt fragments were reacted with CO{sub 2} in the wet supercritical (the top half) and dissolved (the bottom half) phases under carbon sequestration condition with high pressure (10 MPa) and temperature (50 C)more » for 5 months, while small-sized hydrated Portland cement columns (7 mm diameter x 20 mm length; water-to-cement ratio = 0.38) were reacted with CO{sub 2} in dissolved phase at high pressure (10 MPa) and temperature (50 C) for 1 month or with wet CO{sub 2} in gaseous phase at low pressure (0.2 MPa) and temperature (20 C) for 3 months. XMT images reveal that the cement reacted with CO{sub 2} saturated groundwater had degradation depth of {approx}1 mm for 1 month and {approx}3.5 mm for 5 month, whereas the degradation was minor with cement exposure to supercritical CO{sub 2}. SEM-EDS analysis showed that the carbonated cement was comprised of three distinct zones; the innermost less degraded zone with Ca atom % > C atom %, the inner degraded zone with Ca atom % {approx} C atom % due to precipitation of calcite, the outer degraded zone with C atom % > Ca atom % due to dissolution of calcite and C-S-H, as well as adsorption of carbon to cement matrix. The outer degraded zone of carbonated cement was porous and fractured because of dissolution-dominated reaction by carbonic acid exposure, which resulted in the increase in BJH pore volume and BET surface area. In contrast, cement-wet CO{sub 2}(g) reaction at low P (0.2 MPa)-T (20 C) conditions for 1 to 3 months was dominated by precipitation of micron-sized calcite on the outside surface of cement, which resulted in the decrease in BJH pore volume and BET surface area. Cement carbonation and pore structure change are significantly dependent on pressure and temperature conditions as well as the phase of CO{sub 2}, which controls the balance between precipitation and dissolution in cement matrix. Geochemical modeling result suggests that ratio of solid (cement)-to-solution (carbonated water) has a significant effect on cement carbonation, thus the cement-CO{sub 2} reaction experiment needs to be conducted under realistic conditions representing the in-situ wellbore environment of carbon sequestration field site. Total porosity and air permeability for a duplicate cement column with water-to-cement ratio of 0.38 measured after oven-drying by Core Laboratories using Boyle's Law technique and steady-state method were 31% and 0.576 mD. A novel method to measure the effective liquid permeability of a cement column using X-ray micro-tomography images after injection of pressurized KI (potassium iodide) is under development by PNNL. Preliminary results indicate the permeability of a cement column with water-to-cement ratio of 0.38 is 4-8 mD. PNNL will apply the method to understand the effective permeability change of Portland cement by CO{sub 2}(g) reaction under a variety of pressure and temperature conditions to develop a more reliable well-bore leakage risk model.« less

Correlation of pull-out strength of cement-augmented pedicle screws with CT-volumetric measurement of cement.

PubMed

Fölsch, Christian; Goost, Hans; Figiel, Jens; Paletta, Jürgen R J; Schultz, Wolfgang; Lakemeier, Stefan

2012-12-01

Cement augmentation of pedicle screws increases fixation strength in an osteoporotic spine. This study was designed to determine the cement distribution and the correlation between the pull-out strength of the augmented screw and the cement volume within polyurethane (PU) foam. Twenty-eight cannulated pedicle screws (6×45 mm) (Peter Brehm, Erlangen, Germany) with four holes at the distal end of the screw were augmented with the acrylic Stabilit ER Bone Cement Vertebral Augmentation System (DFine Inc., San Jose, CA, USA) and implanted into open-cell rigid PU foam (Pacific Research Laboratories, Vashon Island, WA, USA) with a density of 0.12 g/cm3, resembling severe osteoporosis. Volumetric measurement of the cement with consideration of the distribution around the screws was done with multislice computed tomography scan (Somatom Definition, Siemens, Erlangen, Germany). Pull-out strength was tested with a servohydraulic system (MTS System Corporation, Eden Prairie, MN, USA), and nonaugmented screws served as control. Pearson's correlation coefficient with significance level α=0.05 and one-way analysis of variance test were used. We found a high (r=0.88) and significant (p<0.01) correlation between the cement volume and the pull-out strength, which increased by more than 5-fold with a volume of 3 ml. The correlation appeared linear at least up to 4 ml cement volume and failure always occurred at the cement-bone interface. The cement distribution was symmetric and circular around the most proximal hole, with a distance of 14 mm from the tip, and nearly 90% of the cement was found 6 mm distal and cranial to it. The 95% confidence interval for the relative amount of cement was 37%-41% within 2 mm of the most proximal hole. Compared with the control, a cement volume between 2.0 and 3.0 ml increased the pull-out strength significantly and is relevant for clinical purposes, whereas a volume of 0.5 ml did not. A cement volume beyond 3.0 ml should further increase the pull-out strength because the correlation was linear at least up to 4.0 ml, but the possibility of in vivo cement leakage with increasing volume has to be considered. Pressure-controlled cement application might be a tool to avoid this complication. The cement almost completely penetrated the most proximal perforation.

In vitro shear bond strength of cementing agents to fixed prosthodontic restorative materials.

PubMed

Piwowarczyk, Andree; Lauer, Hans-Christoph; Sorensen, John A

2004-09-01

Durable bonding to fixed prosthodontic restorations is desirable; however, little information is available on the strength of the bond between different cements and fixed prosthodontic restorative materials. This study determined the shear-bond strength of cementing agents to high-gold-content alloy castings and different dental ceramics: high-strength aluminum oxide (Procera AllCeram), leucite-reinforced (IPS Empress), and lithium disilicate glass-ceramic (IPS Empress 2). Prepolymerized resin composite cylinders (5.5 mm internal diameter, n=20) were bonded to the pretreated surfaces of prosthodontic materials. High-gold-content alloy and high-strength aluminum oxide surfaces were airborne-particle-abraded, and pressable ceramics were hydrofluoric acid-etched and silanized prior to cementing. The cementing agents tested were a zinc-phosphate cement (Fleck's zinc cement), glass ionomer cements (Fuji I, Ketac-Cem), resin-modified glass ionomer cements (Fuji Plus, Fuji Cem, RelyX Luting), resin cements (RelyX ARC, Panavia F, Variolink II, Compolute), and a self-adhesive universal resin cement (RelyX Unicem). Half the specimens (n=10) were tested after 30 minutes; the other half (n=10) were stored in distilled water at 37 degrees C for 14 days and then thermal cycled 1000 times between 5 degrees C and 55 degrees C prior to testing. Shear-bond strength tests were performed using a universal testing machine at a constant crosshead speed of 0.5 mm/min. Statistical analysis was performed by multifactorial analysis of variance taking interactions between effects into account. For multiple paired comparisons, the Tukey method was used (alpha=.05). In a 3-way ANOVA model, the main factors substrate, cement, time, and all corresponding interactions were statistically significant (all P <.0001). In subsequent separate 1-way or 2-way ANOVA models for each substrate type, significant differences between cement types and polymerizing modes were found (all P <.001). None of the cement types provided the highest bonding values with all substrate types. After 14 days of water storage followed by thermal cycling, only the self-adhesive universal resin cement (RelyX Unicem) and 2 of the resin cements (Panavia F and Compolute) exhibited strong bond strengths to specific prosthodontic materials. In contrast, zinc-phosphate, glass ionomer, and resin-modified glass ionomer cements showed the lowest values of all tested cementing agents after 14 days of water storage followed by thermal cycling.

Marginal Adaptation and Quality of Interfaces in Lithium Disilicate Crowns - Influence of Manufacturing and Cementation Techniques.

PubMed

Melo Freire, C A; Borges, G A; Caldas, Dbm; Santos, R S; Ignácio, S A; Mazur, R F

To evaluate the cement line thickness and the interface quality in milled or injected lithium disilicate ceramic restorations and their influence on marginal adaptation using different cement types and different adhesive cementation techniques. Sixty-four bovine teeth were prepared for full crown restoration (7.0±0.5 mm in height, 8.0 mm in cervical diameter, and 4.2 mm in incisal diameter) and were divided into two groups: CAD/CAM automation technology, IPS e.max CAD (CAD), and isostatic injection by heat technology, IPS e.max Press (PRESS). RelyX ARC (ARC) and RelyX U200 resin cements were used as luting agents in two activation methods: initial self-activation and light pre-activation for one second (tack-cure). Next, the specimens were stored in distilled water at 23°C ± 2°C for 72 hours. The cement line thickness was measured in micrometers, and the interface quality received scores according to the characteristics and sealing aspects. The evaluations were performed with an optical microscope, and scanning electron microscope images were presented to demonstrate the various features found in the cement line. For the cement line thickness, data were analyzed with three-way analysis of variance (ANOVA) and the Games-Howell test (α=0.05). For the variable interface quality, the data were analyzed with the Mann-Whitney U-test, the Kruskal-Wallis test, and multiple comparisons nonparametric Dunn test (α=0.05). The ANOVA presented statistical differences among the ceramic restoration manufacturing methods as well as a significant interaction between the manufacturing methods and types of cement (p<0.05). The U200 presented lower cement line thickness values when compared to the ARC with both cementation techniques (p<0.05). With regard to the interface quality, the Mann-Whitney U-test and the Kruskal-Wallis test demonstrated statistical differences between the ceramic restoration manufacturing methods and cementation techniques. The PRESS ceramics obtained lower scores than did the CAD ceramics when using ARC cement (p<0.05). Milled restorations cemented with self-adhesive resin cement resulted in a thinner cement line that is statistically different from that of CAD or pressed ceramics cemented with resin cement with adhesive application. No difference between one-second tack-cure and self-activation was noted.

Phase distribution and microstructural changes of self-compacting cement paste at elevated temperature

DOE Office of Scientific and Technical Information (OSTI.GOV)

Ye, G.; Liu, X.; De Schutter, G.

2007-06-15

Self-compacting concrete, as a new smart building material with various advanced properties, has been used for a wide range of structures and infrastructures. However little investigation have been reported on the properties of Self-compacting when it is exposed to elevated temperatures. Previous experiments on fire test have shown the differences between high performance concrete and traditional concrete at elevated temperature. This difference is largely depending on the microstructural properties of concrete matrix, i.e. the cement paste, especially on the porosity, pore size distribution and the connectivity of pores in cement pastes. In this contribution, the investigations are focused on themore » cement paste. The phase distribution and microstructural changes of self-compacting cement paste at elevated temperatures are examined by mercury intrusion porosimetry and scanning electron microscopy. The chemical decomposition of self-compacting cement paste at different temperatures is determined by thermogravimetric analysis. The experimental results of self-compacting cement paste are compared with those of high performance cement paste and traditional cement paste. It was found that self-compacting cement paste shows a higher change of the total porosity in comparison with high performance cement paste. When the temperature is higher than 700 deg. C, a dramatic loss of mass was observed in the self-compacting cement paste samples with addition of limestone filler. This implies that the SCC made by this type of self-compacting cement paste will probably show larger damage once exposed to fire. Investigation has shown that 0.5 kg/m{sup 3} of Polypropylene fibers in the self-compacting cement paste can avoid the damage efficiently.« less

DOE Office of Scientific and Technical Information (OSTI.GOV)

Um, Wooyong; Rod, Kenton A.; Jung, Hun Bok

Cement samples were reacted with CO 2-saturated groundwater, with or without added H2S (1 wt.%), at 50°C and 10 MPa for up to 13 months (CO 2 only) or for up to 3.5 months (CO 2 + H 2S) under static conditions. After the reaction, X-ray computed tomography images revealed that calcium carbonate precipitation (CaCO 3) occurred extensively within the fractures in the cement matrix, but only partially along fractures at the cement-basalt interface. Exposure of a fractured cement sample to CO2-saturated groundwater (50°C and 10 MPa) over a period of 13 months demonstrated progressive healing of cement fractures bymore » CaCO 3(s) precipitation. After reaction with CO 2 + H 2S-saturated groundwater, CaCO 3 (s) precipitation also occurred more extensively within the cement fracture than along the cement-basalt caprock interfaces. X-ray diffraction analysis showed that major cement carbonation products of the CO 2 + H 2S-saturated groundwater were calcite, aragonite, and vaterite, all consistent with cement carbonation by CO 2-saturated groundwater. While pyrite is thermodynamically favored to form, due to the low H 2S concentration it was not identified by XRD in this study. The cement alteration rate into neat Portland cement columns by CO 2-saturated groundwater was similar at ~0.02 mm/d, regardless of the cement-curing pressure and temperature (P-T) conditions, or the presence of H 2S in the brine. The experimental results imply that the wellbore cement with fractures is likely to be healed during exposure to CO 2- or CO 2 + H 2S-saturated groundwater, whereas fractures along the cement-caprock interface are likely to remain open and vulnerable to the leakage of CO 2.« less

A Novel Injectable Borate Bioactive Glass Cement as an Antibiotic Delivery Vehicle for Treating Osteomyelitis

PubMed Central

Cui, Xu; Gu, Yi-Fei; Jia, Wei-Tao; Rahaman, Mohamed N.; Wang, Yang; Huang, Wen-Hai; Zhang, Chang-Qing

2014-01-01

Background A novel injectable cement composed of chitosan-bonded borate bioactive glass (BG) particles was evaluated as a carrier for local delivery of vancomycin in the treatment of osteomyelitis in a rabbit tibial model. Materials and Methods The setting time, injectability, and compressive strength of the borate BG cement, and the release profile of vancomycin from the cement were measured in vitro. The capacity of the vancomycin-loaded BG cement to eradicate methicillin-resistant Staphylococcus aureus (MRSA)-induced osteomyelitis in rabbit tibiae in vivo was evaluated and compared with that for a vancomycin-loaded calcium sulfate (CS) cement and for intravenous injection of vancomycin. Results The BG cement had an injectability of >90% during the first 3 minutes after mixing, hardened within 30 minutes and, after hardening, had a compressive strength of 18±2 MPa. Vancomycin was released from the BG cement into phosphate-buffered saline for up to 36 days, and the cumulative amount of vancomycin released was 86% of the amount initially loaded into the cement. In comparison, vancomycin was released from the CS cement for up 28 days and the cumulative amount released was 89%. Two months post-surgery, radiography and microbiological tests showed that the BG and CS cements had a better ability to eradicate osteomyelitis when compared to intravenous injection of vancomycin, but there was no significant difference between the BG and CS cements in eradicating the infection. Histological examination showed that the BG cement was biocompatible and had a good capacity for regenerating bone in the tibial defects. Conclusions These results indicate that borate BG cement is a promising material both as an injectable carrier for vancomycin in the eradication of osteomyelitis and as an osteoconductive matrix to regenerate bone after the infection is cured. PMID:24427311

The fatigue behavior of an amorphous brittle composite material

NASA Astrophysics Data System (ADS)

Kumar, Brijesh

The use of poly methyl methacrylate (PMMA) based bone cement as a grouting agent for the in-vivo fixation of orthopaedic implants has been in practice for nearly fifty years. Fatigue failure of the bone cement has been identified as the primary cause of cement failure. Implant loosening due to the failure of the cement is one of the major reasons necessitating revision surgery. The need for a more fatigue resistant bone cement is well documented in the literature. One method of producing a more fatigue resistant bone cement is to reinforce it with short fibers. The fundamental purpose of this work was to investigate the possible improvement of the fatigue characteristics of bone cement provided by the following two types of fiber reinforcements: short flexible Polyethylene Terephalate (PET) fibers and stiff milled carbon fibers. It has been shown that the reinforcement of the bone cement with fibers provides substantial improvement of the fracture toughness of the bone cement. In this investigation the impact of fiber reinforcement on the fatigue properties of the bone cement was studied. The effects of the fiber reinforcement on the fatigue life of bone cement has been determined experimentally. Since fatigue characteristics are known to have considerable scatter, a methodology was developed to analyze the experimental data in a statistically rigorous manner. The effect of the fiber reinforcement on bone cement was also analyzed using a theoretical approach and by conducting extensive Scanning Electron Microscopy (SEM) of the fractured surfaces. The results of this study indicate that fiber reinforcement improves the fatigue life of bone cement at a very high level of reliability. This could potentially lead to a more fatigue tolerant bone cement, which would delay the need for revision surgery due to implant loosening.

Influence of the spatial distribution of cementation on the permeability and mechanical attributes of sedimentary and fault rocks

NASA Astrophysics Data System (ADS)

Mozley, P.; Yoon, H.; Williams, R. T.; Goodwin, L. B.

2015-12-01

The spatial distribution of pore-filling authigenic minerals (cements) is highly variable and controlled in large part by the mineralogy of the cements and host sediment grains. Two end-member distributions of cements that commonly occur in sedimentary material are: (1) concretionary, in which precipitation occurred in specific zones throughout the sediment, with intervening areas largely uncemented; and (2) grain-rimming, in which precipitation occurred on grain-surfaces relatively uniformly throughout the rock. Concretions form in rocks in which sediment grains have a different composition from the cement, whereas rim cements form in those that have the same composition. Both the mechanical attributes and permeability of a given volume of rock are affected to a much greater extent by grain rimming cements, which have a significant impact on properties at even low abundances. Concretionary cements have little impact on bulk properties until relatively large volumes have precipitated (~80% cemented) and concretions begin to link up. Precipitation of cement in fault zones also impacts both mechanical and hydrologic properties. Cementation will stiffen and strengthen unlithified sediment, thereby controlling the locus of fracturing in protolith or damage zones. Where fracture networks form in fault damage zones, they are initially high permeability elements. However, progressive cementation greatly diminishes fracture permeability, resulting in cyclical permeability variation linked to fault slip. To quantitatively describe the interactions of groundwater flow, permeability, and patterns and abundance of cements, we use pore-scale modeling of coupled fluid flow, reactive transport, and heterogeneous mineral-surface reactions. By exploring the effects of varying distributions of porosity and mineralogy, which impact patterns of cementation, we provide mechanistic explanations of the interactions of coupled processes under various flow and chemistry conditions.

A novel injectable borate bioactive glass cement as an antibiotic delivery vehicle for treating osteomyelitis.

PubMed

Ding, Hao; Zhao, Cun-Ju; Cui, Xu; Gu, Yi-Fei; Jia, Wei-Tao; Rahaman, Mohamed N; Wang, Yang; Huang, Wen-Hai; Zhang, Chang-Qing

2014-01-01

A novel injectable cement composed of chitosan-bonded borate bioactive glass (BG) particles was evaluated as a carrier for local delivery of vancomycin in the treatment of osteomyelitis in a rabbit tibial model. The setting time, injectability, and compressive strength of the borate BG cement, and the release profile of vancomycin from the cement were measured in vitro. The capacity of the vancomycin-loaded BG cement to eradicate methicillin-resistant Staphylococcus aureus (MRSA)-induced osteomyelitis in rabbit tibiae in vivo was evaluated and compared with that for a vancomycin-loaded calcium sulfate (CS) cement and for intravenous injection of vancomycin. The BG cement had an injectability of >90% during the first 3 minutes after mixing, hardened within 30 minutes and, after hardening, had a compressive strength of 18 ± 2 MPa. Vancomycin was released from the BG cement into phosphate-buffered saline for up to 36 days, and the cumulative amount of vancomycin released was 86% of the amount initially loaded into the cement. In comparison, vancomycin was released from the CS cement for up 28 days and the cumulative amount released was 89%. Two months post-surgery, radiography and microbiological tests showed that the BG and CS cements had a better ability to eradicate osteomyelitis when compared to intravenous injection of vancomycin, but there was no significant difference between the BG and CS cements in eradicating the infection. Histological examination showed that the BG cement was biocompatible and had a good capacity for regenerating bone in the tibial defects. These results indicate that borate BG cement is a promising material both as an injectable carrier for vancomycin in the eradication of osteomyelitis and as an osteoconductive matrix to regenerate bone after the infection is cured.

Influence of carbonation on the acid neutralization capacity of cements and cement-solidified/stabilized electroplating sludge.

PubMed

Chen, Quanyuan; Zhang, Lina; Ke, Yujuan; Hills, Colin; Kang, Yanming

2009-02-01

Portland cement (PC) and blended cements containing pulverized fuel ash (PFA) or granulated blast-furnace slag (GGBS) were used to solidify/stabilize an electroplating sludge in this work. The acid neutralization capacity (ANC) of the hydrated pastes increased in the order of PC > PC/GGBS > PC/PFA. The GGBS or PFA replacement (80 wt%) reduced the ANC of the hydrated pastes by 30-50%. The ANC of the blended cement-solidified electroplating sludge (cement/sludge 1:2) was 20-30% higher than that of the hydrated blended cement pastes. Upon carbonation, there was little difference in the ANC of the three cement pastes, but the presence of electroplating sludge (cement/sludge 1:2) increased the ANC by 20%. Blended cements were more effective binders for immobilization of Ni, Cr and Cu, compared with PC, whereas Zn was encapsulated more effectively in the latter. Accelerated carbonation improved the immobilization of Cr, Cu and Zn, but not Ni. The geochemical code PHREEQC, with the edited database from EQ3/6 and HATCHES, was used to calculate the saturation index and solubility of likely heavy metal precipitates in cement-based solidification/stabilization systems. The release of heavy metals could be related to the disruption of cement matrices and the remarkable variation of solubility of heavy metal precipitates at different pH values.

Peri-implant stress correlates with bone and cement morphology: Micro-FE modeling of implanted cadaveric glenoids.

PubMed

Wee, Hwabok; Armstrong, April D; Flint, Wesley W; Kunselman, Allen R; Lewis, Gregory S

2015-11-01

Aseptic loosening of cemented joint replacements is a complex biological and mechanical process, and remains a clinical concern especially in patients with poor bone quality. Utilizing high resolution finite element analysis of a series of implanted cadaver glenoids, the objective of this study was to quantify relationships between construct morphology and resulting mechanical stresses in cement and trabeculae. Eight glenoid cadavers were implanted with a cemented central peg implant. Specimens were imaged by micro-CT, and subject-specific finite element models were developed. Bone volume fraction, glenoid width, implant-cortex distance, cement volume, cement-cortex contact, and cement-bone interface area were measured. Axial loading was applied to the implant of each model and stress distributions were characterized. Correlation analysis was completed across all specimens for pairs of morphological and mechanical variables. The amount of trabecular bone with high stress was strongly negatively correlated with both cement volume and contact between the cement and cortex (r = -0.85 and -0.84, p < 0.05). Bone with high stress was also correlated with both glenoid width and implant-cortex distance. Contact between the cement and underlying cortex may dramatically reduce trabecular bone stresses surrounding the cement, and this contact depends on bone shape, cement amount, and implant positioning. © 2015 Orthopaedic Research Society. Published by Wiley Periodicals, Inc.

Cement-in-cement acetabular revision with a constrained tripolar component.

PubMed

Leonidou, Andreas; Pagkalos, Joseph; Luscombe, Jonathan

2012-02-17

Dislocation of a total hip replacement (THR) is common following total hip arthroplasty (THA). When nonoperative management fails to maintain reduction, revision surgery is considered. The use of constrained acetabular liners has been extensively described. Complete removal of the old cement mantle during revision THA can be challenging and is associated with significant complications. Cement-in-cement revision is an established technique. However, the available clinical and experimental studies focus on femoral stem revision. The purpose of this study was to present a case of cement-in-cement acetabular revision with a constrained component for recurrent dislocations and to investigate the current best evidence for this technique. This article describes the case of a 74-year-old woman who underwent revision of a Charnley THR for recurrent low-energy dislocations. A tripolar constrained acetabular component was cemented over the primary cement mantle following removal of the original liner by reaming, roughening the surface, and thoroughly irrigating and drying the primary cement. Clinical and radiological results were good, with the Oxford Hip Score improving from 11 preoperatively to 24 at 6 months postoperatively. The good short-term results of this case and the current clinical and biomechanical data encourage the use of the cement-in-cement technique for acetabular revision. Careful irrigation, drying, and roughening of the primary surface are necessary. Copyright 2012, SLACK Incorporated.

Morphological and chemical characterization of the dentin/resin cement interface produced with a self-etching primer.

PubMed

Walker, Mary P; Wang, Yong; Spencer, Paulette

2002-01-01

The purpose of this study was to analyze a resin cement/dentin interface by comparing the diffusion of a resin cement into dentin surfaces pretreated with a self-etching primer with or without pretreatment by conventional acid etching. Dentin surfaces of 8 unerupted human third molars were treated with a self-etch primer (Panavia 21) with or without conventional phosphoric acid pretreatment. Panavia 21 resin cement was applied according to manufacturer's instructions. Dentin/resin cement interface sections from each tooth were examined with scanning electron microscopy and micro-Raman spectroscopy. When the self-etch primer was used following conventional acid pretreatment, the resin cement did not penetrate to the depth of the zone of demineralized dentin, leaving a substantial area of exposed dentin matrix at the dentin/cement interface. In contrast, there was substantial resin cement diffusion throughout the demineralized dentin when the self-etch primer was used without acid etching pretreatment. The in vitro evaluation of resin cement penetration throughout the zone of demineralized dentin is an important step in identifying sites of exposed dentin matrix that may promote postoperative sensitivity and may leave the dentin/resin cement interface vulnerable to premature degradation under clinical conditions. In this study, the self-etch primer used alone produced substantial resin cement penetration and left no exposed dentin matrix at the dentin/resin cement interface.

The long-term in vivo behavior of polymethyl methacrylate bone cement in total hip arthroplasty.

PubMed

Oonishi, Hiroyuki; Akiyama, Haruhiko; Takemoto, Mitsuru; Kawai, Toshiyuki; Yamamoto, Koji; Yamamuro, Takao; Oonishi, Hironobu; Nakamura, Takashi

2011-10-01

The long-term success of cemented total hip arthroplasty (THA) has been well established. Improved outcomes, both radiographically and clinically, have resulted mainly from advances in stem design and improvements in operating techniques. However, there is concern about the durability of bone cement in vivo. We evaluated the physical and chemical properties of CMW1 bone cements retrieved from patients undergoing revision THA. CMW1 cements were retrieved from 14 patients who underwent acetabular revision because of aseptic loosening. The time in vivo before revision was 7-30 years. The bending properties of the retrieved bone cement were assessed using the three-point bending method. The molecular weight and chemical structure were analyzed by gel permeation chromatography and Fourier-transform infrared spectroscopy. The porosity of the bone cements was evaluated by 3-D microcomputer tomography. The bending strength decreased with increasing time in vivo and depended on the density of the bone cement, which we assume to be determined by the porosity. There was no correlation between molecular weight and time in vivo. The infrared spectra were similar in the retrieved cements and in the control CMW1 cements. Our results indicate that polymer chain scission and significant hydrolysis do not occur in CMW1 cement after implantation in vivo, even in the long term. CMW1 cement was stable through long-term implantation and functional loading.

Post retention: the effect of sequence of post-space preparation, cementation time, and different sealers.

PubMed

Boone, K J; Murchison, D F; Schindler, W G; Walker, W A

2001-12-01

Many endodontic sealers contain constituents that have been shown to inhibit the polymerization of resin cements. This may be important when prefabricated posts are cemented at the same appointment as root canal obturation. This study evaluated the effects of cementing posts with a resin cement immediately or at a delayed time period after obturation using Roth's 801 Elite Grade or AH26 sealer cements. The contribution of mechanical post-space preparation was also assessed as a critical variable. One hundred twenty extracted canines were randomly divided into eight experimental groups. The variables evaluated were the order of post preparation (either before or after obturation), the type of sealer used, and the time of post cementation. All teeth received a stainless steel #6 Parapost XP cemented with a resin cement, Panavia 21. Each experimental group underwent tensile testing for retention using an Instron universal testing machine. For both sealers posts cemented in teeth in which the canal was obturated before post-space preparation and thus had sealer-contaminated dentin removed by the space preparation procedure had significantly higher retentive values than those obturated after post-space preparation in which contaminated dentin might remain. Sealer used and time of cementation had no specific effect on retention. Achieving a clean, "freshened" dentinal surface during mechanical post-space preparation seems to be a critical variable for post retention when a resin cement is used.

Cermet cements.

PubMed

McLean, J W

1990-01-01

Cermet ionomer cements are sintered metal/glass powders, which can be made to react with poly(acids). These new cements are significantly more resistant to abrasion than regular glass ionomer cements and are widely accepted as core build-up materials and lining cements. They can strengthen teeth and provide the clinician with an opportunity to treat early dental caries.

Evaluation of a Glass Ionomer Restoration to Treat Hypersensitive Cervical Anatomic Deficiencies.

DTIC Science & Technology

1983-03-01

glass ionomer cement to existing dental cements such as...that the milder pulp reaction to a glass ionomer cement as opposed to a phosphoric acid cement may be explained by the weaker acid makeup of the ASPA...7 Sensitivity Evaluation ........................... 9 Treatment of Dentinal Sensitivity................. 12 Glass Ionomer Cements

40 CFR 146.12 - Construction requirements.

Code of Federal Regulations, 2010 CFR

2010-07-01

...; and (B) A cement bond, temperature, or density log after the casing is set and cemented. (ii) For... cement bond, temperature, or density log after the casing is set and cemented. (e) At a minimum, the... water. The casing and cement used in the construction of each newly drilled well shall be designed for...

40 CFR 60.541 - Definitions.

Code of Federal Regulations, 2010 CFR

2010-07-01

... facility (parts per million by volume) Dc=density of cement or spray material (grams per liter (lb per... which the tire is mounted. Bead cementing operation means the system that is used to apply cement to the... consists of a cement application station, such as a dip tank, spray booth and nozzles, cement trough and...

77 FR 46371 - National Emission Standards for Hazardous Air Pollutants for the Portland Cement Manufacturing...

Federal Register 2010, 2011, 2012, 2013, 2014

2012-08-03

...-AQ93 National Emission Standards for Hazardous Air Pollutants for the Portland Cement Manufacturing... Portland Cement Manufacturing Industry and Standards of Performance for Portland Cement Plants,'' which was... Manufacturing Industry and Standards of Performance for Portland Cement Plants'' under Docket ID No. EPA-HQ-OAR...

Waiting time for coronal preparation and the influence of different cements on tensile strength of metal posts.

PubMed

Oliveira, Ilione Kruschewsky Costa Sousa; Arsati, Ynara Bosco de Oliveira Lima; Basting, Roberta Tarkany; França, Fabiana Mantovani Gomes

2012-01-01

This study aimed to assess the effect of post-cementation waiting time for core preparation of cemented cast posts and cores had on retention in the root canal, using two different luting materials. Sixty extracted human canines were sectioned 16 mm from the root apex. After cast nickel-chromium metal posts and cores were fabricated and luted with zinc phosphate (ZP) cement or resin cement (RC), the specimens were divided into 3 groups (n = 10) according to the waiting time for core preparation: no preparation (control), 15 minutes, or 1 week after the core cementation. At the appropriate time, the specimens were subjected to a tensile load test (0.5 mm/min) until failure. Two-way ANOVA (time versus cement) and the Tukey tests (P < 0.05) showed significantly higher (P < 0.05) tensile strength values for the ZP cement groups than for the RC groups. Core preparation and post-cementation waiting time for core recontouring did not influence the retention strength. ZP was the best material for intraradicular metal post cementation.

Experimental Investigation of Multi-mode Fiber Laser Cutting of Cement Mortar.

PubMed

Lee, Dongkyoung; Pyo, Sukhoon

2018-02-10

This study successfully applied multi-mode laser cutting with the variation of the laser cutting speed to cement mortar for the first time. The effects of the amount of silica sand in the cement mortar on laser cutting are tested and analyzed. The kerf width and penetration depth of the specimens after laser cutting are investigated. As the laser cutting speed increases, the penetration depth decreases for both cement paste and cement mortar, whereas the kerf width becomes saturated and increases, respectively, for cement paste and cement mortar. Cross sections of the specimens are compared with illustrations. Top-view images of the cement mortar with indicators of the physical characteristics, such as re-solidification, burning, and cracks are examined, and the possible causes of these characteristics are explained. The optical absorption rates of cement-based materials are quantified at wide ranges of wavelength to compare the absorption rates in accordance with the materials compositions. The chemical composition variation before and after laser cutting is also compared by EDX (Energy Dispersive X-Ray) analysis. In addition to these observations, material removal mechanisms for cement mortar are proposed.

Experimental Investigation of Multi-mode Fiber Laser Cutting of Cement Mortar

PubMed Central

2018-01-01

This study successfully applied multi-mode laser cutting with the variation of the laser cutting speed to cement mortar for the first time. The effects of the amount of silica sand in the cement mortar on laser cutting are tested and analyzed. The kerf width and penetration depth of the specimens after laser cutting are investigated. As the laser cutting speed increases, the penetration depth decreases for both cement paste and cement mortar, whereas the kerf width becomes saturated and increases, respectively, for cement paste and cement mortar. Cross sections of the specimens are compared with illustrations. Top-view images of the cement mortar with indicators of the physical characteristics, such as re-solidification, burning, and cracks are examined, and the possible causes of these characteristics are explained. The optical absorption rates of cement-based materials are quantified at wide ranges of wavelength to compare the absorption rates in accordance with the materials compositions. The chemical composition variation before and after laser cutting is also compared by EDX (Energy Dispersive X-Ray) analysis. In addition to these observations, material removal mechanisms for cement mortar are proposed. PMID:29439431

Evaluation of four biodegradable, injectable bone cements in an experimental drill hole model in sheep.

PubMed

von Rechenberg, Brigitte; Génot, Oliver R; Nuss, Katja; Galuppo, Larry; Fulmer, Mark; Jacobson, Evan; Kronen, Peter; Zlinszky, Kati; Auer, Jörg A

2013-09-01

Four cement applications were tested in this investigation. Two dicalcium phosphate dihydrate (DCPD-brushite) hydraulic cements, an apatite hydraulic fiber loaded cement, and a calcium sulfate cement (Plaster of Paris) were implanted in epiphyseal and metaphyseal cylindrical bone defects in sheep. The in vivo study was performed to assess the biocompatibility and bone remodeling of four cement formulations. After time periods of 2, 4, and 6 months, the cement samples were clinically and histologically evaluated. Histomorphometrically, the amount of new bone formation, fibrous tissue, and bone marrow and the area of remaining cement were measured. In all specimens, no signs of inflammation were detectable either macroscopically or microscopically. Cements differed mainly in their resorption time. Calcium sulfate was already completely resorbed at 2 months and showed a variable amount of new bone formation and/or fibrous tissue in the original drill hole over all time periods. The two DCPD cements in contrast were degraded to a large amount at 6 months, whereas the apatite was almost unchanged over all time periods. Copyright © 2013. Published by Elsevier B.V.

Modified femoral pressuriser generates a longer lasting high pressure during cement pressurisation

PubMed Central

2011-01-01

Background The strength of the cement-bone interface in hip arthroplasty is strongly related to cement penetration into the bone. A modified femoral pressuriser has been investigated, designed for closer fitting into the femoral opening to generate higher and more constant cement pressure compared to a commercial (conventional) design. Methods Femoral cementation was performed in 10 Sawbones® models, five using the modified pressuriser and five using a current commercial pressuriser as a control. Pressure during the cementation was recorded at the proximal and distal regions of the femoral implant. The peak pressure and the pressure-time curves were analysed by student's t-test and Two way ANOVA. Results The modified pressuriser showed significantly and substantially longer durations at higher cementation pressures and slightly, although not statistically, higher peak pressures compared to the conventional pressuriser. The modified pressuriser also produced more controlled cement leakage. Conclusion The modified pressuriser generates longer higher pressure durations in the femoral model. This design modification may enhance cement penetration into cancellous bone and could improve femoral cementation. PMID:22004662

Wide-scale utilization of MSWI fly ashes in cement production and its impact on average heavy metal contents in cements: The case of Austria.

PubMed

Lederer, Jakob; Trinkel, Verena; Fellner, Johann

2017-02-01

A number of studies present the utilization of fly ashes from municipal solid waste incineration (MSWI) in cement production as a recycling alternative to landfilling. While there is a lot of research on the impact of MSWI fly ashes utilization in cement production on the quality of concrete or the leaching of heavy metals, only a few studies have determined the resulting heavy metal content in cements caused by this MSWI fly ashes utilization. Making use of the case of Austria, this study (1) determines the total content of selected heavy metals in cements currently produced in the country, (2) designs a scenario and calculates the resulting heavy metal contents in cements assuming that all MSWI fly ashes from Austrian grate incinerators were used as secondary raw materials for Portland cement clinker production and (3) evaluates the legal recyclability of demolished concretes produced from MSWI fly ash amended cements based on their total heavy metal contents. To do so, data from literature and statistics are combined in a material flow analysis model to calculate the average total contents of heavy metals in cements and in the resulting concretes according to the above scenario. The resulting heavy metal contents are then compared (i) to their respective limit values for cements as defined in a new technical guideline in Austria (BMLFUW, 2016), and (ii) to their respective limit values for recycling materials from demolished concrete. Results show that MSWI fly ashes utilization increases the raw material input in cement production by only +0.9%, but the total contents of Cd by +310%, and Hg, Pb, and Zn by +70% to +170%. However these and other heavy metal contents are still below their respective limit values for Austrian cements. The same legal conformity counts for recycling material derived from concretes produced from the MSWI fly ash cements. However, if the MSWI fly ash ratio in all raw materials used for cement production were increased from 0.9% to 22%, which is suggested by some studies, the limit values for cements as defined by the BMLFUW (2016) will be exceeded. Furthermore, the concrete produced from this cement will not be recyclable anymore due to its high total heavy metal contents. This and the comparatively high contribution of MSWI fly ashes to total heavy metal contents in cements indicate their relatively low resource potential if compared to other secondary raw materials in the cement industry. Copyright © 2016 Elsevier Ltd. All rights reserved.

Experimental study of potential wellbore cement carbonation by various phases of carbon dioxide during geologic carbon sequestration

DOE Office of Scientific and Technical Information (OSTI.GOV)

Jung, Hun Bok; Um, Wooyong

2013-08-16

Hydrated Portland cement was reacted with carbon dioxide (CO2) in supercritical, gaseous, and aqueous phases to understand the potential cement alteration processes along the length of a wellbore, extending from deep CO2 storage reservoir to the shallow subsurface during geologic carbon sequestration. The 3-D X-ray microtomography (XMT) images displayed that the cement alteration was significantly more extensive by CO2-saturated synthetic groundwater than dry or wet supercritical CO2 at high P (10 MPa)-T (50°C) conditions. Scanning electron microscopy with energy dispersive spectroscopy (SEM-EDS) analysis also exhibited a systematic Ca depletion and C enrichment in cement matrix exposed to CO2-saturated groundwater. Integratedmore » XMT, XRD, and SEM-EDS analyses identified the formation of extensive carbonated zone filled with CaCO3(s), as well as the porous degradation front and the outermost silica-rich zone in cement after exposure to CO2-saturated groundwater. The cement alteration by CO2-saturated groundwater for 2-8 months overall decreased the porosity from 31% to 22% and the permeability by an order of magnitude. Cement alteration by dry or wet supercritical CO2 was slow and minor compared to CO2-saturated groundwater. A thin single carbonation zone was formed in cement after exposure to wet supercritical CO2 for 8 months or dry supercritical CO2 for 15 months. Extensive calcite coating was formed on the outside surface of a cement sample after exposure to wet gaseous CO2 for 1-3 months. The chemical-physical characterization of hydrated Portland cement after exposure to various phases of carbon dioxide indicates that the extent of cement carbonation can be significantly heterogeneous depending on CO2 phase present in the wellbore environment. Both experimental and geochemical modeling results suggest that wellbore cement exposure to supercritical, gaseous, and aqueous phases of CO2 during geologic carbon sequestration is unlikely to damage the wellbore integrity because cement alteration by all phases of CO2 is dominated by carbonation reaction. This is consistent with previous field studies of wellbore cement with extensive carbonation after exposure to CO2 for 3 decades. However, XMT imaging indicates that preferential cement alteration by supercritical CO2 or CO2-saturated groundwater can occur along the cement-steel or cement-rock interfaces. This highlights the importance of further investigation of cement degradation along the interfaces of wellbore materials to ensure permanent geologic carbon storage.« less

Study of deformation of resin cements used in fixing of root posts through fiber Bragg grating sensors

NASA Astrophysics Data System (ADS)

Pulido, C. A.; Franco, A. P. G. O.; Karam, L. Z.; Kalinowski, H. J.; Gomes, O. M. M.

2014-05-01

The aim of the study was to evaluate the polymerization shrinkage "in situ" in resin cements inside the root canal during the fixation of glass fiber posts. For cementation teeth were randomly divided into 2 groups according to the resin cement used: Group1 - resin cement dual Relyx ARC (3M/ESPE), and Group 2 - resin cement dual Relyx U200 (3M/ESPE). Before inserting the resin cement into the root canal, two Bragg grating sensors were recorded and pasted in the region without contact with the canal, one at the apical and other at the coronal thirds of the post. The sensors measured the deformation of the resin cements in coronal and apical root thirds to obtain the values in micro-strain (μɛ).

In vivo response of bioactive PMMA-based bone cement modified with alkoxysilane and calcium acetate.

PubMed

Sugino, Atsushi; Ohtsuki, Chikara; Miyazaki, Toshiki

2008-11-01

The use of polymethylmethacrylate (PMMA)-based bone cement is popular in orthopedics for the fixation of artificial joints with bone. However, it has a major problem with prostheses loosening because of coverage by fibrous tissue after long-term implantation. Recently, a bioactive bone cement has been developed that shows direct bonding to living bone through modification of PMMA resin with gamma-methacryloxypropyltrimethoxysilane (MPS) and calcium acetate. The cement is designed to exhibit bioactivity, through incorporation of silanol groups and calcium ions. Thus, it has the potential to form a layer of bone-like hydroxyapatite, which is essential for achieving direct bonding to living bone. This type of modification allows the cement to show spontaneous hydroxyapatite formation on its surface in a simulated body fluid after one day, and there is evidence of osteoconduction of the cement in rabbit tibia for periods of more than three weeks. However, the influence of the dissolved ions from the modified cement has not yet been clarified. Thus, the authors focused on the dissolution of the modified PMMA-based bone cement and its tissue response in muscle and bone by comparison with the behavior of non-modified PMMA-based bone cement. One week after implantation in the latissimus dorsi of a rabbit, the modified PMMA-based bone cement showed more inflammatory width than the commercial cement. However, four weeks after implantation, the inflammatory width of both cements was essentially the same. The osteoconductivity around the modified cement was higher than that for the conventional cement after four weeks implantation. These results indicate that the initial dissolution of calcium acetate from the modified cement to form the hydroxyapatite induced the acute inflammation around tissue, but also developed the osteoconductivity. It is suggested that the initial inflammation can be effective for inducing osteoconduction through a bone healing reaction when the material provides an environment that promotes bone formation.

Influence of Temporary Cements on the Bond Strength of Self-Adhesive Cement to the Metal Coronal Substrate.

PubMed

Peixoto, Raniel Fernandes; De Aguiar, Caio Rocha; Jacob, Eduardo Santana; Macedo, Ana Paula; De Mattos, Maria da Gloria Chiarello; Antunes, Rossana Pereira de Almeida

2015-01-01

This research evaluated the influence of temporary cements (eugenol-containing [EC] or eugenol-free [EF]) on the tensile strength of Ni-Cr copings fixed with self-adhesive resin cement to the metal coronal substrate. Thirty-six temporary crowns were divided into 4 groups (n=9) according to the temporary cements: Provy, Dentsply (eugenol-containing), Temp Cem, Vigodent (eugenol-containing), RelyX Temp NE, 3M ESPE (eugenol-free) and Temp Bond NE, Kerr Corp (eugenol-free). After 24 h of temporary cementation, tensile strength tests were performed in a universal testing machine at a crosshead speed of 0.5 mm/min and 1 kN (100 kgf) load cell. Afterwards, the cast metal cores were cleaned by scraping with curettes and air jet. Thirty-six Ni-Cr copings were cemented to the cast metal cores with self-adhesive resin cement (RelyX U200, 3M ESPE). Tensile strength tests were performed again. In the temporary cementation, Temp Bond NE (12.91 ± 2.54) and Temp Cem (12.22 ± 2.96) presented the highest values of tensile strength and were statistically similar to each other (p>0.05). Statistically significant difference (p<0.05) was observed only between Provy (164.44 ± 31.23) and Temp Bond NE (88.48 ± 21.83) after cementation of Ni-Cr copings with self-adhesive resin cement. In addition, Temp Cem (120.68 ± 48.27) and RelyX Temp NE (103.04 ± 26.09) showed intermediate tensile strength values. In conclusion, the Provy eugenol-containing temporary cement was associated with the highest bond strength among the resin cements when Ni-Cr copings were cemented to cast metal cores. However, the eugenol cannot be considered a determining factor in increased bond strength, since the other tested cements (1 eugenol-containing and 2 eugenol-free) were similar.

Cementing a wellbore using cementing material encapsulated in a shell

DOEpatents

Aines, Roger D.; Bourcier, William L.; Duoss, Eric B.; Spadaccini, Christopher M.; Cowan, Kenneth Michael

2016-08-16

A system for cementing a wellbore penetrating an earth formation into which a pipe extends. A cement material is positioned in the space between the wellbore and the pipe by circulated capsules containing the cement material through the pipe into the space between the wellbore and the pipe. The capsules contain the cementing material encapsulated in a shell. The capsules are added to a fluid and the fluid with capsules is circulated through the pipe into the space between the wellbore and the pipe. The shell is breached once the capsules contain the cementing material are in position in the space between the wellbore and the pipe.

Biomechanical evaluation of bone screw fixation with a novel bone cement.

PubMed

Juvonen, Tiina; Nuutinen, Juha-Pekka; Koistinen, Arto P; Kröger, Heikki; Lappalainen, Reijo

2015-07-30

Bone cement augmentation is commonly used to improve the fixation stability of orthopaedic implants in osteoporotic bone. The aim of this study was to evaluate the effect of novel bone cements on the stability of bone screw fixation by biomechanical testing and to compare them with a conventional Simplex(®)P bone cement and requirements of the standards. Basic biomechanical properties were compared with standard tests. Adhesion of bone cements were tested with polished, glass blasted and corundum blasted stainless steel surfaces. Screw pullout testing with/without cement was carried out using a synthetic bone model and cancellous and cortical bone screws. All the tested bone cements fulfilled the requirements of the standard for biomechanical properties and improved the screw fixation stability. Even a threefold increase in shear and tensile strength was achieved with increasing surface roughness. The augmentation improved the screw pullout force compared to fixation without augmentation, 1.2-5.7 times depending on the cement and the screw type. The good biomechanical properties of novel bone cement for osteoporotic bone were confirmed by experimental testing. Medium viscosity of the bone cements allowed easy handling and well-controlled penetration of bone cement into osteoporotic bone. By proper parameters and procedures it is possible to achieve biomechanically stable fixation in osteoporotic bone. Based on this study, novel biostable bone cements are very potential biomaterials to enhance bone screw fixation in osteoporotic bone. Novel bone cement is easy to use without hand mixing using a dual syringe and thus makes it possibility to use it as required during the operation.

Incorporation of chlorhexidine diacetate in provisional cements: antimicrobial activity against Streptococcus mutans and the effect on tensile strength in vitro.

PubMed

Lewinstein, I; Zenziper, E; Block, J; Kfir, A

2012-11-01

To test the antibacterial capacities and tensile strengths of three commercially available provisional cements to which chlorhexidine diacetate was added and compare them to the same unmodified cements. Sixty cylindrical samples were prepared from either three noneugenol provisional cements or the same cements modified by the addition of chlorhexidine diacetate at 7.5% w/w, with a total of 360 samples. The cements tested included Tempbond NE, Rely X Temp NE and Freegenol. Forty-eight samples from each cement were aged in saline that was replaced twice a week for up to 96 days. Twelve of these samples were removed at either 1, 15, 30 or 96 days and assessed for antibacterial properties against Streptococcus mutans with an agar diffusion test. Twelve samples of each cement, with and without chlorhexidine diacetate, were also tested 7 days after the initial setting for their tensile strength using a diametrical tensile strength test applied with an Instron machine. The results were analysed using either one-way or three-way anova. The addition of chlorhexidine diacetate resulted in provisional cements with antibacterial properties that persisted through ageing in saline for up to 96 days. The addition of chlorhexidine did not reduce the diametrical strength of the cements. The addition of chlorhexidine diacetate to provisional cements rendered all three cements antibacterial against S. mutans and this activity was maintained even after prolonged ageing of the cements, without compromising their tensile strength at 7 days. © 2012 International Endodontic Journal.

Study of the Peak Shear Strength of a Cement-Filled Hard Rock Joint

NASA Astrophysics Data System (ADS)

She, Cheng-Xue; Sun, Fu-Ting

2018-03-01

The peak shear strength of a cement-filled hard rock joint is studied by theoretical analysis and laboratory testing. Based on the concept of the shear resistance angle, by combining the statistical method and fractal theory, three new parameters are proposed to characterize the three-dimensional joint morphology, reflecting the effects of the average roughness, multi-scale asperities and the dispersion degree of the roughness distribution. These factors are independent of the measurement scale, and they reflect the anisotropy of the joint roughness. Compressive shear tests are conducted on cement-filled joints. Because joints without cement can be considered special cement-filled joints in which the filling degree of cement is zero, they are also tested. The cement-filled granite joint fails primarily along the granite-cement interfaces. The filling degree of cement controls the joint failure and affects its mechanical behaviour. With a decrease in the filling degree of cement, the joint cohesion decreases; however, the dilatancy angle and the basic friction angle of the interface increase. As the filling degree approaches zero, the cohesion approaches zero, while the dilatancy angle and the basic friction angle increase to those of the joint without cement. A set of formulas is proposed to evaluate the peak shear strength of the joints with and without cement. The formulas are shown to be reasonable by comparison with the tested peak shear strength, and they reflect the anisotropy of the strength. This research deepens the understanding of cement-filled joints and provides a method to evaluate their peak shear strength.

Effect of eugenol-based endodontic sealer on the adhesion of intraradicular posts cemented after different periods.

PubMed

Dias, Larissa Lustosa Lima; Giovani, Alessandro Rogério; Silva Sousa, Yara Teresinha Corrêa; Vansan, Luiz Pascoal; Alfredo, Edson; Sousa-Neto, Manoel Damião; Paulino, Silvana Maria

2009-01-01

This study evaluated in vitro the influence of an eugenol-based sealer (EndoFill) on the retention of stainless steel prefabricated posts cemented with zinc phosphate and resin-based (Panavia F) cements after different periods of root canal obturation, using the pull-out test. Sixty upper canines were decoronated and the roots were embedded in resin blocks. The specimens were distributed into 3 groups, according to the period elapsed between canal obturation and post cementation: Group I - immediately; Group II - 72 h and Group III - 4 months. The groups were subdivided according to the type of cement used for post cementation: A - zinc phosphate and B - Panavia F. Following the experimental periods, specimens were subjected to pullout test in an Instron machine with application of tensile force at a crosshead speed of 0.5 mm/min until post dislodgement. The maximum forces required for post removal were recorded (kN) and means were subjected to statistical analysis by 2-way ANOVA and Tukey-Kramer test (alpha=0.001) There were statistically significant differences (p<0.01) between the posts cemented with zinc phosphate cement (0.2112 kN) and Panavia F (0.0501 kN). However, no statistically significant differences (p>0.05) were found between the three post cementation periods, regardless of the cement. It was concluded that the eugenol-based sealer influenced the tensile strength of the posts cemented with the resin cement, but had no influence on the time waited between root canal obturation and post space preparation/post cementation.

EFFECT OF EUGENOL-BASED ENDODONTIC SEALER ON THE ADHESION OF INTRARADICULAR POSTS CEMENTED AFTER DIFFERENT PERIODS

PubMed Central

Dias, Larissa Lustosa Lima; Giovani, Alessandro Rogério; Sousa, Yara Teresinha Corrêa Silva; Vansan, Luiz Pascoal; Alfredo, Edson; Sousa-Neto, Manoel Damião; Paulino, Silvana Maria

2009-01-01

Objective: This study evaluated in vitro the influence of an eugenol-based sealer (EndoFill) on the retention of stainless steel prefabricated posts cemented with zinc phosphate and resin-based (Panavia F) cements after different periods of root canal obturation, using the pull-out test. Material and methods: Sixty upper canines were decoronated and the roots were embedded in resin blocks. The specimens were distributed into 3 groups, according to the period elapsed between canal obturation and post cementation: Group I - immediately; Group II - 72 h and Group III - 4 months. The groups were subdivided according to the type of cement used for post cementation: A - zinc phosphate and B - Panavia F. Following the experimental periods, specimens were subjected to pull- out test in an Instron machine with application of tensile force at a crosshead speed of 0.5 mm/min until post dislodgement. The maximum forces required for post removal were recorded (kN) and means were subjected to statistical analysis by 2-way ANOVA and Tukey-Kramer test (α=0.001) Results: There were statistically significant differences (p<0.01) between the posts cemented with zinc phosphate cement (0.2112 kN) and Panavia F (0.0501 kN). However, no statistically significant differences (p>0.05) were found between the three post cementation periods, regardless of the cement. Conclusions: It was concluded that the eugenol-based sealer influenced the tensile strength of the posts cemented with the resin cement, but had no influence on the time waited between root canal obturation and post space preparation/post cementation. PMID:20027430

Considerations for proper selection of dental cements.

PubMed

Simon, James F; Darnell, Laura A

2012-01-01

Selecting the proper cement for sufficient bond strength has become progressively complicated as the number of different materials for indirect restorations has increased. The success of any restoration is highly dependent on the proper cement being chosen and used. The function of the cement is not only to seal the restoration on the tooth but also, in some cases, to support the retention of the restoration. This ability to strengthen retention varies by the cement chosen by the clinician; therefore, careful consideration must precede cement selection.

Development of fluorapatite cement for dental enamel defects repair.

PubMed

Wei, Jie; Wang, Jiecheng; Shan, Wenpeng; Liu, Xiaochen; Ma, Jian; Liu, Changsheng; Fang, Jing; Wei, Shicheng

2011-06-01

In order to restore the badly carious lesion of human dental enamel, a crystalline paste of fluoride substituted apatite cement was synthesized by using the mixture of tetracalcium phosphate (TTCP), dicalcium phosphate anhydrous (DCPA) and ammonium fluoride. The apatite cement paste could be directly filled into the enamel defects (cavities) to repair damaged dental enamel. The results indicated that the hardened cement was fluorapatite [Ca(10)(PO(4))(6)F(2), FA] with calcium to phosphorus atom molar ratio (Ca/P) of 1.67 and Ca/F ratio of 5. The solubility of FA cement in Tris-HCl solution (pH = 5) was slightly lower than the natural enamel, indicating the FA cement was much insensitive to the weakly acidic solutions. The FA cement was tightly combined with the enamel surface, and there was no obvious difference of the hardness between the FA cement and natural enamel. The extracts of FA cement caused no cytotoxicity on L929 cells, which satisfied the relevant criterion on dental biomaterials, revealing good cytocompatibility. In addition, the results showed that the FA cement had good mechanical strength, hydrophilicity, and anti-bacterial adhesion properties. The study suggested that using FA cement was simple and promising approach to effectively and conveniently restore enamel defects.