Metal-boride phase formation on tungsten carbide (WC-Co) during microwave plasma chemical vapor deposition

NASA Astrophysics Data System (ADS)

Johnston, Jamin M.; Catledge, Shane A.

2016-02-01

Strengthening of cemented tungsten carbide by boriding is used to improve the wear resistance and lifetime of carbide tools; however, many conventional boriding techniques render the bulk carbide too brittle for extreme conditions, such as hard rock drilling. This research explored the variation in metal-boride phase formation during the microwave plasma enhanced chemical vapor deposition process at surface temperatures from 700 to 1100 °C. We showed several well-adhered metal-boride surface layers consisting of WCoB, CoB and/or W2CoB2 with average hardness from 23 to 27 GPa and average elastic modulus of 600-730 GPa. The metal-boride interlayer was shown to be an effective diffusion barrier against elemental cobalt; migration of elemental cobalt to the surface of the interlayer was significantly reduced. A combination of glancing angle X-ray diffraction, electron dispersive spectroscopy, nanoindentation and scratch testing was used to evaluate the surface composition and material properties. An evaluation of the material properties shows that plasma enhanced chemical vapor deposited borides formed at substrate temperatures of 800 °C, 850 °C, 900 °C and 1000 °C strengthen the material by increasing the hardness and elastic modulus of cemented tungsten carbide. Additionally, these boride surface layers may offer potential for adhesion of ultra-hard carbon coatings.

Characterization of AISI 4140 borided steels

NASA Astrophysics Data System (ADS)

Campos-Silva, I.; Ortiz-Domínguez, M.; López-Perrusquia, N.; Meneses-Amador, A.; Escobar-Galindo, R.; Martínez-Trinidad, J.

2010-02-01

The present study characterizes the surface of AISI 4140 steels exposed to the paste-boriding process. The formation of Fe 2B hard coatings was obtained in the temperature range 1123-1273 K with different exposure times, using a 4 mm thick layer of boron carbide paste over the material surface. First, the growth kinetics of boride layers at the surface of AISI 4140 steels was evaluated. Second, the presence and distribution of alloying elements on the Fe 2B phase was measured using the Glow Discharge Optical Emission Spectrometry (GDOES) technique. Further, thermal residual stresses produced on the borided phase were evaluated by X-ray diffraction (XRD) analysis. The fracture toughness of the iron boride layer of the AISI 4140 borided steels was estimated using a Vickers microindentation induced-fracture testing at a constant distance of 25 μm from the surface. The force criterion of fracture toughness was determined from the extent of brittle cracks, both parallel and perpendicular to the surface, originating at the tips of an indenter impression. The fracture toughness values obtained by the Palmqvist crack model are expressed in the form KC( π/2) > KC > KC(0) for the different applied loads and experimental parameters of the boriding process.

Computational-Experimental Processing of Boride/Carbide Composites by Reactive Infusion of Hf Alloy Melts into B4C

DTIC Science & Technology

2015-09-16

AFRL-AFOSR-VA-TR-2015-0314 Computational -Experimental Processing of Boride /Carbide Composites by Reactive Infusion of Hf Alloy Melts into B4C...Computational -Experimental Processing of Boride /Carbide Composites by Reactive Infusion of Hf Alloy Melts into B4C 5a.  CONTRACT NUMBER 5b.  GRANT...with a packed bed of B4C to form boride - carbide precipitates. Although the ultimate goal of the research endeavor is to enhance significantly the

Method of making crack-free zirconium hydride

DOEpatents

Sullivan, Richard W.

1980-01-01

Crack-free hydrides of zirconium and zirconium-uranium alloys are produced by alloying the zirconium or zirconium-uranium alloy with beryllium, or nickel, or beryllium and scandium, or nickel and scandium, or beryllium and nickel, or beryllium, nickel and scandium and thereafter hydriding.

Field free, directly heated lanthanum boride cathode

DOEpatents

Leung, Ka-Ngo; Moussa, D.; Wilde, S.B.

1987-02-02

A directly heated cylindrical lanthanum boride cathode assembly is disclosed which minimizes generation of magnetic field which would interfere with electron emission from the cathode. The cathode assembly comprises a lanthanum boride cylinder in electrical contact at one end with a central support shaft which functions as one electrode to carry current to the lanthanum boride cylinder and in electrical contact, at its opposite end with a second electrode which is coaxially position around the central support shaft so that magnetic fields generated by heater current flowing in one direction through the central support shaft are cancelled by an opposite magnetic field generated by current flowing through the lanthanum boride cylinder and the coaxial electrode in a direction opposite to the current flow in the central shaft.

Methods of repairing a substrate

NASA Technical Reports Server (NTRS)

Riedell, James A. (Inventor); Easler, Timothy E. (Inventor)

2011-01-01

A precursor of a ceramic adhesive suitable for use in a vacuum, thermal, and microgravity environment. The precursor of the ceramic adhesive includes a silicon-based, preceramic polymer and at least one ceramic powder selected from the group consisting of aluminum oxide, aluminum nitride, boron carbide, boron oxide, boron nitride, hafnium boride, hafnium carbide, hafnium oxide, lithium aluminate, molybdenum silicide, niobium carbide, niobium nitride, silicon boride, silicon carbide, silicon oxide, silicon nitride, tin oxide, tantalum boride, tantalum carbide, tantalum oxide, tantalum nitride, titanium boride, titanium carbide, titanium oxide, titanium nitride, yttrium oxide, zirconium boride, zirconium carbide, zirconium oxide, and zirconium silicate. Methods of forming the ceramic adhesive and of repairing a substrate in a vacuum and microgravity environment are also disclosed, as is a substrate repaired with the ceramic adhesive.

Characterization and diffusion model for the titanium boride layers formed on the Ti6Al4V alloy by plasma paste boriding

NASA Astrophysics Data System (ADS)

Keddam, Mourad; Taktak, Sukru

2017-03-01

The present study is focused on the estimation of activation energy of boron in the plasma paste borided Ti6Al4V alloy, which is extensively used in technological applications, using an analytical diffusion model. Titanium boride layers were successfully produced by plasma paste boriding method on the Ti6Al4V alloy in the temperature range of 973-1073 K for a treatment time ranging from 3 to 7 h. The presence of both TiB2 top-layer and TiB whiskers sub-layer was confirmed by the XRD analysis and SEM observations. The surface hardness of the borided alloy was evaluated using Micro-Knoop indenter. The formation rates of the TiB2 and TiB layers were found to have a parabolic character at all applied process temperatures. A diffusion model was suggested to estimate the boron diffusivities in TiB2 and TiB layers under certain assumptions, by considering the effect of boride incubation times. Basing on own experimental data on boriding kinetics, the activation energies of boron in TiB2 and TiB phases were estimated as 136.24 ± 0.5 and 63.76 ± 0.5 kJ mol-1, respectively. Finally, the obtained values of boron activation energies for Ti6Al4V alloy were compared with the data available in the literature.

Properties of boride-added powder metallurgy magnesium alloys

NASA Astrophysics Data System (ADS)

Tanaka, Atsushi; Yoshimura, Syota; Fujima, Takuya; Takagi, Ken-ichi

2009-06-01

Magnesium alloys with metallic borides, magnesium diboride (MgB2) or aluminum diboride (AlB2), were investigated regarding their mechanical properties, transverse rupture strength (TRS) and micro Vickers hardness (HV). The alloys were made from pure Mg, Al and B powders by mechanical alloying and hot pressing to have boride content of between 2.0 and 20 vol%. The alloy with AlB2 exhibited an obvious improvement of HV around a boride content of 6 vol% though the other alloy, with MgB2, did not. TRS showed moderate maxima around the same boride content region for the both alloys. X-ray diffraction measurements indicated an intermetallic compound, Mg17Al12, formed in the alloy with AlB2, which was consistent with its higher hardness.

Influence of laser alloying with boron and niobium on microstructure and properties of Nimonic 80A-alloy

NASA Astrophysics Data System (ADS)

Makuch, N.; Piasecki, A.; Dziarski, P.; Kulka, M.

2015-12-01

Ni-base superalloys were widely used in aeronautics, chemical and petrochemical industries due to their high corrosion resistance, high creep and rupture strength at high temperature. However, these alloys were not considered for applications in which conditions of appreciable mechanical wear were predominant. The diffusion boriding provided suitable protection against wear. Unfortunately, this process required long duration and high temperature. In this study, instead of the diffusion process, the laser alloying with boron and niobium was used in order to produce the hard and wear resistant layer on Nimonic 80A-alloy. The laser-alloying was carried out as a two-step process. First, the external cylindrical surface of specimens was pre-placed with a paste containing boron and niobium. Then, the pre-placed coating and the thin surface layer of the substrate were re-melted by a laser beam. The high laser beam power (P=1.56 kW) and high averaging irradiance (E=49.66 kW/cm2) provided the thick laser re-melted zone. The laser-borided layers were significantly thicker (470 μm) in comparison with the layers obtained as a consequence of the diffusion boriding. Simultaneously, the high overlapping of multiple laser tracks (86%) caused that the laser-alloyed layer was uniform in respect of the thickness. The produced layer consisted of nickel borides (Ni3B, Ni2B, Ni4B3, NiB), chromium borides (CrB, Cr2B), niobium borides (NbB2, NbB) and Ni-phase. The presence of hard borides caused the increase in microhardness up to 1000 HV in the re-melted zone. However, the measured values were lower than those-characteristic of niobium borides, chromium borides and nickel borides. The presence of the soft Ni-phase in re-melted zone was the reason for such a situation. After laser alloying, the significant increase in abrasive wear resistance was also observed. The mass wear intensity factor, as well as the relative mass loss of the laser-alloyed specimens, was over 10 times smaller in comparison with untreated Nimonic 80A-alloy.

In Situ Solid-Gas Reactivity of Nanoscaled Metal Borides from Molten Salt Synthesis.

PubMed

Gouget, Guillaume; Debecker, Damien P; Kim, Ara; Olivieri, Giorgia; Gallet, Jean-Jacques; Bournel, Fabrice; Thomas, Cyril; Ersen, Ovidiu; Moldovan, Simona; Sanchez, Clément; Carenco, Sophie; Portehault, David

2017-08-07

Metal borides have mostly been studied as bulk materials. The nanoscale provides new opportunities to investigate the properties of these materials, e.g., nanoscale hardening and surface reactivity. Metal borides are often considered stable solids because of their covalent character, but little is known on their behavior under a reactive atmosphere, especially reductive gases. We use molten salt synthesis at 750 °C to provide cobalt monoboride (CoB) nanocrystals embedded in an amorphous layer of cobalt(II) and partially oxidized boron as a model platform to study morphological, chemical, and structural evolutions of the boride and the superficial layer exposed to argon, dihydrogen (H 2 ), and a mixture of H 2 and carbon dioxide (CO 2 ) through a multiscale in situ approach: environmental transmission electron microscopy, synchrotron-based near-ambient-pressure X-ray photoelectron spectroscopy, and near-edge X-ray absorption spectroscopy. Although the material is stable under argon, H 2 triggers at 400 °C decomposition of CoB, leading to cobalt(0) nanoparticles. We then show that H 2 activates CoB for the catalysis of CO 2 methanation. A similar decomposition process is also observed on NiB nanocrystals under oxidizing conditions at 300 °C. Our work highlights the instability under reactive atmospheres of nanocrystalline cobalt and nickel borides obtained from molten salt synthesis. Therefore, we question the general stability of metal borides with distinct compositions under such conditions. These results shed light on the actual species in metal boride catalysis and provide the framework for future applications of metal borides in their stability domains.

Interlayer utilization (including metal borides) for subsequent deposition of NSD films via microwave plasma CVD on 316 and 440C stainless steels

NASA Astrophysics Data System (ADS)

Ballinger, Jared

Diamond thin films have promising applications in numerous fields due to the extreme properties of diamonds in conjunction with the surface enhancement of thin films. Biomedical applications are numerous including temporary implants and various dental and surgical instruments. The unique combination of properties offered by nanostructured diamond films that make it such an attractive surface coating include extreme hardness, low obtainable surface roughness, excellent thermal conductivity, and chemical inertness. Regrettably, numerous problems exist when attempting to coat stainless steel with diamond generating a readily delaminated film: outward diffusion of iron to the surface, inward diffusion of carbon limiting necessary surface carbon precursor, and the mismatch between the coefficients of thermal expansion yielding substantial residual stress. While some exotic methods have been attempted to overcome these hindrances, the most common approach is the use of an intermediate layer between the stainless steel substrate and the diamond thin film. In this research, both 316 stainless steel disks and 440C stainless steel ball bearings were tested with interlayers including discrete coatings and graded, diffusion-based surface enhancements. Titanium nitride and thermochemical diffusion boride interlayers were both examined for their effectiveness at allowing for the growth of continuous and adherent diamond films. Titanium nitride interlayers were deposited by cathodic arc vacuum deposition on 440C bearings. Lower temperature diamond processing resulted in improved surface coverage after cooling, but ultimately, both continuity and adhesion of the nanostructured diamond films were unacceptable. The ability to grow quality diamond films on TiN interlayers is in agreement with previous work on iron and low alloy steel substrates, and the similarly seen inadequate adhesion strength is partially a consequence of the lacking establishment of an interfacial carbide phase. Surface boriding was implemented using the novel method of microwave plasma CVD with a mixture of hydrogen and diborane gases. On 440C bearings, dual phase boride layers of Fe2B and FeB were formed which supported adhered nanostructured diamond films. Continuity of the films was not seamless with limited regions remaining uncoated potentially corresponding to delamination of the film as evidenced by the presence of tubular structures presumably composed of sp2 bonded carbon. Surface boriding of 316 stainless steel discs was conducted at various powers and pressures to achieve temperatures ranging from 550-800 °C. The substrate boriding temperature was found to substantially influence the resultant interlayer by altering the metal boride(s) present. The lowest temperatures produced an interlayer where CrB was the single detected phase, higher temperatures yielded the presence of only Fe2B, and a combination of the two phases resulted from an intermediate boriding temperature. Compared with the more common, commercialized boriding methods, this a profound result given the problems posed by the FeB phase in addition to other advantages offered by CVD processes and microwave generated plasmas in general. Indentation testing of the boride layers revealed excellent adhesion strength for all borided interlayers, and above all, no evidence of cracking was observed for a sole Fe2B phase. As with boriding of 440C bearings, subsequent diamond deposition was achieved on these interlayers with substantially improved adhesion strength relative to diamond coated TiN interlayers. Both XRD and Raman spectroscopy confirmed a nanostructured diamond film with interfacial chromium carbides responsible for enhanced adhesion strength. Interlayers consisting solely of Fe2B have displayed an ability to support fully continuous nanostructured diamond films, yet additional study is required for consistent reproduction. This is in good agreement with initial work on pack borided high alloy steels to promote diamond film surface modification. The future direction for continued research of nanostructured diamond coatings on microwave plasma CVD borided stainless steel should further investigate the adhesion of both borided interlayers and subsequent NSD films in addition to short, interrupted diamond depositions to study the interlayer/diamond film interface.

Plasma boriding of a cobalt-chromium alloy as an interlayer for nanostructured diamond growth

NASA Astrophysics Data System (ADS)

Johnston, Jamin M.; Jubinsky, Matthew; Catledge, Shane A.

2015-02-01

Chemical vapor deposited (CVD) diamond coatings can potentially improve the wear resistance of cobalt-chromium medical implant surfaces, but the high cobalt content in these alloys acts as a catalyst to form graphitic carbon. Boriding by high temperature liquid baths and powder packing has been shown to improve CVD diamond compatibility with cobalt alloys. We use the microwave plasma-enhanced (PE) CVD process to deposit interlayers composed primarily of the borides of cobalt and chromium. The use of diborane (B2H6) in the plasma feedgas allows for the formation of a robust boride interlayer for suppressing graphitic carbon during subsequent CVD of nano-structured diamond (NSD). This metal-boride interlayer is shown to be an effective diffusion barrier against elemental cobalt for improving nucleation and adhesion of NSD coatings on a CoCrMo alloy. Migration of elemental cobalt to the surface of the interlayer is significantly reduced and undetectable on the surface of the subsequently-grown NSD coating. The effects of PECVD boriding are compared for a range of substrate temperatures and deposition times and are evaluated using glancing-angle X-ray diffraction (XRD), cross-sectional scanning electron microscopy (SEM), energy dispersive X-ray spectroscopy (EDS), and micro-Raman spectroscopy. Boriding of CoCrMo results in adhered nanostructured diamond coatings with low surface roughness.

Analysis of Deformation Substructures in a Notched LCF Sample Under Dwell Condition in a Ni-Based Superalloy (PREPRINT)

DTIC Science & Technology

2012-08-01

interior, and carbides and borides at the grain boundaries. Blocky carbide particles can also be seen in the grain interior (Figure 1b). The borides ...can be seen distributed (b) higher magnification image of a typical grain boundary decorated with carbide and boride particles. Bi-modal distribution

Future Directions for Selected Topics in Physics and Materials Science

DTIC Science & Technology

2012-07-12

referred to as lightides (e.g. borides , nitrides, phosphides) • Materials for energy conversion, energy storage, energy transport and energy production...Distributed nanosystems and sensors • Strategy for multilayered combinatorics • lightides ( borides , nitrides, phosphides, • New applications for...Strategy for multilayered combinatorics Lightides ( borides , nitrides, phosphides) • Energy conversion, .storage and production • Precision control

Dianionic Carbon-Bridged Scandium-Copper/Silver Heterobimetallic Complexes: Synthesis, Bonding, and Reactivity.

PubMed

Wang, Chen; Xiang, Li; Yang, Yan; Fang, Jian; Maron, Laurent; Leng, Xuebing; Chen, Yaofeng

2018-04-11

Alkylidene-bridged scandium-copper/silver heterobimetallic complexes were synthesized and structurally characterized. The complexes contain different Sc-C and M-C (M=Cu I , Ag I ) bonds. The reactivity of the scandium-copper heterobimetallic complex was also studied, which reveals that the heterobimetallic complex is a reaction intermediate for the transmetalation of akylidene group from Sc III to Cu I . The scandium-copper heterobimetallic complex also undergoes an addition reaction with CO, resulting in the formation of a new C=C double bond. DFT calculations were used to study the bonding and the subsequent reactivity with CO of the scandium-copper heterobimetallic complex. It clearly demonstrates a cooperative effect between the two metal centers through the formation of a direct Sc⋅⋅⋅Cu interaction that drives the reactivity with CO. © 2018 Wiley-VCH Verlag GmbH & Co. KGaA, Weinheim.

Plasma metallurgical production of nanocrystalline borides and carbides

NASA Astrophysics Data System (ADS)

Galevsky, G. V.; Rudneva, V. V.; Cherepanov, A. N.; Galevsky, S. G.; Efimova, K. A.

2016-09-01

he experience in production and study of properties of nanocrystalline borides and chromium carbides, titanium, silicon was summarized. The design and features of the vertical three-jet once-through reactor with power 150 kW, used in the plasma metallurgical production, was described. The technological, thermotechnical and resource characteristics of the reactor were identified. The parameters of borides and carbides synthesis, their main characteristics in the nanodispersed state and equipment-technological scheme of production were provided. Evaluation of engineering-and-economical performance of the laboratory and industrial levels of borides and carbides production and the state corresponding to the segment of the world market was carried out.

The Growth Behavior of Titanium Boride Layers in α and β Phase Fields of Titanium

NASA Astrophysics Data System (ADS)

Lv, Xiaojun; Hu, Lingyun; Shuang, Yajing; Liu, Jianhua; Lai, Yanqing; Jiang, Liangxing; Li, Jie

2016-07-01

In this study, the commercially pure titanium was successfully electrochemical borided in a borax-based electrolyte. The process was carried out at a constant cathodic current density of 300 mA cm-2 and at temperatures of 1123 K and 1223 K (850 °C and 950 °C) for 0.5, 1, 2, 3, and 5 hours. The growth behavior of titanium boride layers in the α phase field of titanium was compared with that in the β phase field. After boriding, the presence of both the TiB2 top layer and TiB whisker sub-layer was confirmed by the X-ray diffraction (XRD) and scanning electron microscope. The relationship between the thickness of boride layers and boriding time was found to have a parabolic character in both α and β phase fields of titanium. The TiB whiskers showed ultra-fast growth rate in the β phase field. Its growth rate constant was found to be as high as 3.2002 × 10-13 m2 s-1. Besides, the chemical resistance of the TiB2 layer on the surface of titanium substrate was characterized by immersion tests in molten aluminum.

Kinetic Investigation and Wear Properties of Fe2B Layers on AISI 12L14 Steel

NASA Astrophysics Data System (ADS)

Keddam, M.; Ortiz-Dominguez, M.; Elias-Espinosa, M.; Arenas-Flores, A.; Zuno-Silva, J.; Zamarripa-Zepeda, D.; Gomez-Vargas, O. A.

2018-03-01

In the current study, the powder-pack boriding was applied to the AISI 12L14 steel in the temperature range 1123 K to 1273 K for an exposure time between 2 and 8 hours. The produced boride layer was composed of Fe2B with a sawtooth morphology. A diffusion model based on the integral method was applied to investigate the growth kinetics of Fe2B layers. As a main result, the boron diffusion coefficients in Fe2B were estimated by considering the principle of mass balance at the (Fe2B/substrate) interface with an inclusion of boride incubation times. The value of activation energy for boron diffusion in AISI 12L14 steel was estimated as 165 kJ mol-1 and compared with other values of activation energy found in the literature. An experimental validation of the present model was made by using four different boriding conditions. Furthermore, the Rockwell-C adhesion test was employed to assess the cohesion of boride layers to the base metal. The scratch and pin-on-disc tests were also carried out to analyze the effect of boriding on wear behavior of AISI 12L14 steel.

Suppression of Boride Formation in Transient Liquid Phase Bonding of Pairings of Parent Superalloy Materials with Different Compositions and Grain Structures and Resulting Mechanical Properties

NASA Astrophysics Data System (ADS)

Steuer, Susanne; Singer, Robert F.

2014-07-01

Two Ni-based superalloys, columnar grained Alloy 247 and single-crystal PWA1483, are joined by transient liquid phase bonding using an amorphous brazing foil containing boron as a melting point depressant. At lower brazing temperatures, two different morphologies of borides develop in both base materials: plate-like and globular ones. Their ratio to each other is temperature dependent. With very high brazing temperatures, the deleterious boride formation in Alloy 247 can be totally avoided, probably because the three-phase-field moves to higher alloying element contents. For the superalloy PWA1483, the formation of borides cannot be completely avoided at high brazing temperatures as incipient melting occurs. During subsequent solidification of these areas, Chinese-script-like borides precipitate. The mechanical properties (tensile tests at room and elevated temperatures and short-term creep rupture tests at elevated temperatures) for brazed samples without boride precipitation are very promising. Tensile strengths and creep times to 1 pct strain are comparable, respectively, higher than the ones of the weaker parent material for all tested temperatures and creep conditions (from 90 to 100 pct rsp. 175 to 250 pct).

Applied research of shaking table for scandium concentration from a silicate ore

NASA Astrophysics Data System (ADS)

Yan, P.; Zhang, G. F.; Gao, L.; Shi, B. H.; Shi, Z.; Yang, Y. D.

2018-03-01

A poor magnetite iron ore is a super large independent scandium deposit with over the multi-billion potential utilizable value. Shaking table separation is very useful for impurities removing and scandium content increasing as a follow-up step of high-intensity magnetic separation. In the present study, a satisfactory index, namely scandium content of 83.10 g/t and recovery rate of 79.45 wt%, was obtained by shaking table separation. The good result was achieved under the conditions which the parameters were feed concentrate of 18 wt%, feeding quantity of 11 L/min, stroke frequency of 275 times/min and stroke of 17mm.

Recovery of Scandium from Leachate of Sulfation-Roasted Bayer Red Mud by Liquid-Liquid Extraction

NASA Astrophysics Data System (ADS)

Liu, Zhaobo; Li, Hongxu; Jing, Qiankun; Zhang, Mingming

2017-11-01

The leachate obtained from sulfation-roasted Bayer red mud is suitable for extraction of scandium by liquid-liquid solvent extraction because it contains trace amounts of Fe3+ and Si4+. In this study, a completely new metallurgical process for selective recovery of scandium from Bayer red mud was proposed. The extraction performances of Sc3+, Fe3+, Al3+, Si4+, Ca2+, and Na+ from synthetic leachate of sulfation-roasted red mud were first investigated using organophosphorus extractants (di-2-ethylhexyl phosphoric acid P204 and 2-ethylhexyl phosphoric acid mono-2-ethylhexyl ester P507) and carboxylic acid extractant (Versatic acid 10). It shows that P204 has an excellent extraction ability and that it can be applied to the scandium recovery. P507 and Versatic acid 10 are much poorer in performance for selective extraction of scandium. In the leachate of sulfation-roasted red mud, approximately 97% scandium can be recovered using a P204/sulfonated kerosene (1% v/v) extraction system under the condition of an organic-to-aqueous phase ratio of 10:1 and with an extraction temperature of 15°C.

Microstructure Evolution and Composition Control during the Processing of Thin-gage Metallic Foil (Preprint)

DTIC Science & Technology

2012-02-01

the presence of somewhat randomly-distributed carbides and borides (white particles in BSE images), this grain size was comparable to that observed...pinned by carbide/ boride particles (imaging white in Figure 8c). The very fine gamma-prime precipitates likely produced during magnetron sputtering...sputtered material. First, the carbide/ boride particles were nucleated and hence located preferentially at the grain boundaries in the sputtered

Novel Routes to Tune Thermal Conductivities and Thermoelectric Properties of Materials

DTIC Science & Technology

2012-11-15

expand the possibilities of borides as functional compou nds. A series of indium-free novel TCO compounds with novel crystal structures, has...powerful methods for modification were demonstrated in the borides , silicides and oxides. Introduction: The goal of this project is to...the possibility to modify the crystal structures can expand the possibilities of borides as functional compounds. A series of indium-free novel TCO

Alloying-Element Loss during High-Temperature Processing of a Nickel-Base Superalloy (Preprint)

DTIC Science & Technology

2013-01-01

precipitates, and the fine white/gray particles are carbides and borides . ............................................. 23 Figure 2. Aluminum...comparable size, and submicron carbides and borides . A fifteen-minute heat treatment at the subsolvus temperature used in the present work (i.e...precipitates, and ~0.3 volume pct. of carbides and borides with an average diameter of ~0.3 m (Figure 1) [5, 6]. B. Procedures To establish the

Amorphous Iron Borides: Preparation, Structure and Magnetic Properties.

DTIC Science & Technology

1982-09-28

temperature. External magnetic field experiments were performed in a superconducting solenoid with both source and absor- ber at 4.2 K. The observed...D-Ai20 919 AMORPHOUS IRON BORIDES: PREPARATION STRUCTURE AND i/i MAGNETIC PROPERTIES(U) JOHNS HOPKINS UNIV LAUREL NO APPLIED PHYSICS LRB K MOORJRNI...NATIONAL BUREAU OF STANOANOS-93-A 10 AMORPHOUS IRON BORIDES: PREPARATION, STRUCTURE ~AND MAGNETIC PROPERTIES FINAL REPORT Kishin Moorjani September 1982 U

Effect of Heat Treatment on Borides Precipitation and Mechanical Properties of CoCrFeNiAl1.8Cu0.7B0.3Si0.1 High-Entropy Alloy Prepared by Arc-Melting and Laser-Cladding

NASA Astrophysics Data System (ADS)

Zhang, H.; Tang, H.; He, Y. Z.; Zhang, J. L.; Li, W. H.; Guo, S.

2017-11-01

Effects of heat treatment on borides precipitation and mechanical properties of arc-melted and laser-cladded CoCrNiFeAl1.8Cu0.7B0.3Si0.1 high-entropy alloys were comparatively studied. The arc-melted alloy contains lots of long strip borides distributed in the body-centered cubic phase, with a hardness about 643 HV0.5. Laser-cladding can effectively inhibit the boride precipitation and the laser-cladded alloy is mainly composed of a simple bcc solid solution, with a high hardness about 769 HV0.5, indicating the strengthening effect by interstitial boron atoms is greater than the strengthening by borides precipitation. Heat treatments between 800°C and 1200°C can simultaneously improve the hardness and fracture toughness of arc-melted alloys, owing to the boride spheroidization, dissolution, re-precipitation, and hence the increased boron solubility and nano-precipitation in the bcc solid solution. By contrast, the hardness of laser-cladded alloys reduce after heat treatments in the same temperature range, due to the decreased boron solubility in the matrix.

SEPARATION OF SCANDIUM VALUES FORM IRON VALUES BY SOLVENT EXTRACTION

DOEpatents

Kuhlman, C.W. Jr.; Lang, G.P.

1961-12-19

A process is given for separating scandium from trivalent iron values. In this process, an aqueous nitric acid solution is contacted with a water- immiscible alkyl phosphate solution, the aqueous solution containing the values to be separated, whereby the scandium is taken up by the alkyl phosphate. The aqueous so1ution is preferably saturated with magnesium nitrate to retain the iron in the aqueous solution. (AEC)

Certain physical properties of cobalt and nickel borides

NASA Technical Reports Server (NTRS)

Kostetskiy, I. I.; Lvov, S. N.

1981-01-01

The temperature dependence of the electrical resistivity, the thermal conductivity, and the thermal emf of cobalt and nickel borides were studied. In the case of the nickel borides the magnetic susceptibility and the Hall coefficient were determined at room temperature. The results are discussed with allowance for the current carrier concentration, the effect of various mechanisms of current-carrier scattering and the location of the Fermi level in relation to the 3d band.

A study on the formation of solid state nanoscale materials using polyhedral borane compounds

NASA Astrophysics Data System (ADS)

Romero, Jennifer V.

The formation of boron containing materials using a variety of methods was explored. The pyrolysis of a metal boride precursor solution can be accomplished using a one-source method by combining TiCl4, B10H 14 and CH3CN in one reaction vessel and pyrolyzing it at temperatures above 900 °C. Amorphous dark blue colored films were obtained after the pyrolysis reactions. Well-defined spherical shaped grains or particles were observed by SEM. The amorphous films generated contained titanium, however, the determination of the boron content of the films was inconclusive. This one pot method making metal boride thin films has the advantage of being able to dictate the stoichiometry of the reactants. Another part of this work represents the first report of both the use of metal boride materials and the use of a titanium-based compound for the formation of nanotubes. This method provides a facile method for generating well-formed boron-containing carbon nanotubes in a "one-pot" process through an efficient aerosol process. The formation of metal boride corrosion resistant layers was also explored. It was shown that metallic substrates can be effectively boronized using paste mixtures containing boron carbide and borax. The formation of a Fe4B 2 iron boride phase was achieved, however, this iron boride phase does not give enough corrosion protection. The formation of a corrosion resistant metal boride coating with strong adhesion was accomplished by boronization of a thermal sprayed nickel layer on the surface of steel. Surfactants were explored as possible nanoreactors in which metal boride nanoparticles could be formed to use as nanotube growth catalyst via room temperature reaction. Different surfactants were used, but none of them successfully generated very well dispersed metal boride nanoparticles. Nanoparticles with varying shapes and sizes were generated which were highly amorphous. The carboxylic acid derivative of closo-C2B 10 cages was explored as a ligand in the hydrothermal preparation of coordination polymers with zinc salts. It was found that the stability of the cage is apparently insufficient under these conditions and cage degradation was observed. Consequently, a preliminary investigation of the preparation of dipyridyl derivatives of both the closo-C2B 10 and the closo-B12 cages was performed.

Synthesis and Characterization of YB4 Ceramics

DTIC Science & Technology

2011-06-24

capa bility at temperatures above 2000°C1 with adequate mechani cal properties and oxidation resistance. Refractory metal borides based on HfB2 and ZrB2...increase in the oxidation resistance was accomplished by the addition of the Group IV VI transition metal borides , which was the result of phase...metal borides for use as materials for ultra high temper ature (UHT) applications. However, for instance, yttrium tet raboride, YB4, appears promising as

Finding the Stable Structures of WxN1-x with an ab-initio High-Throughput Approach

DTIC Science & Technology

2014-03-13

cubic boron nitride[4], carbonitrides,[5] and transition metal borides .[6, 7] Over the past several years there has been considerable theoretical...include ionic and covalent structures which seem chemically similar to W-N. These include borides , carbides, oxides, and other nitrides. In this paper we...metallic alloys, [23–27] we extended it to include over fifty new structures. These include nitrides, oxides, borides , and carbides. The important

Magnesium Aluminum Borides as Explosive Materials

DTIC Science & Technology

2011-12-20

Metal Silicides , and Metal Borides by Chemical Vapour Deposition Using Single Organometallic Precursors,” Trans. Inst. Met. Finishing, 72, 127-129...391 (2003). 62. X. Xiaojing, D. Bohua, Q. Zuanhui, and L. Yuanhui, “ Preparation and Synthesis Mechanism of Li-B Alloy,” Rare Metal Materials and...SUPPLEMENTARY NOTES 14. ABSTRACT Metal boride.; and boroo carbide Witted l’"irh Al ’I\\· ere compared co B. Mg. Al Mg:-AJ and Si a.s poteotia! fuel ad.diti

Size Effects on Deformation and Fracture of Scandium Deuteride Films.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Teresi, C. S.; Hintsala, E.; Adams, David P.

Metal hydride films have been observed to crack during production and use, prompting mechanical property studies of scandium deuteride films. The following focuses on elastic modulus, fracture, and size effects observed in the system for future film mechanical behavior modeling efforts. Scandium deuteride films were produced through the deuterium charging of electron beam evaporated scandium films using X-ray diffraction, scanning Auger microscopy, and electron backscatter diffraction to monitor changes in the films before and after charging. Scanning electron microscopy, nanoindentation, and focused ion beam machined micropillar compression tests were used for mechanical characterization of the scandium deuteride films. The micropillarsmore » showed a size effect for flow stress, indicating that film thickness is a relevant tuning parameter for film performance, and that fracture was controlled by the presence of grain boundaries. Elastic modulus was determined by both micropillar compression and nanoindentation to be approximately 150 GPa, Fracture studies of bulk film channel cracking as well as compression induced cracks in some of the pillars yielded a fracture toughness around 1.0 MPa-m1/2. Preliminary Weibull distributions of fracture in the micropillars are provided. Despite this relatively low value of fracture toughness, scandium deuteride micropillars can undergo a large degree of plasticity in small volumes and can harden to some degree, demonstrating the ductile and brittle nature of this material« less

Development of high temperature stable Ohmic and Schottky contacts on n-gallium nitride

NASA Astrophysics Data System (ADS)

Khanna, Rohit

In this work the effort was made to towards develop and investigate high temperature stable Ohmic and Schottky contacts for n type GaN. Various borides and refractory materials were incorporated in metallization scheme to best attain the desired effect of minimal degradation of contacts when placed at high temperatures. This work focuses on achieving a contact scheme using different borides which include two Tungsten Borides (namely W2B, W2B 5), Titanium Boride (TiB2), Chromium Boride (CrB2) and Zirconium Boride (ZrB2). Further a high temperature metal namely Iridium (Ir) was evaluated as a potential contact to n-GaN, as part of continuing improved device technology development. The main goal of this project was to investigate the most promising boride-based contact metallurgies on GaN, and finally to fabricate a High Electron Mobility Transistor (HEMT) and compare its reliability to a HEMT using present technology contact. Ohmic contacts were fabricated on n GaN using borides in the metallization scheme of Ti/Al/boride/Ti/Au. The characterization of the contacts was done using current-voltage measurements, scanning electron microscopy (SEM) and Auger Electron Spectroscopy (AES) measurements. The contacts formed gave specific contact resistance of the order of 10-5 to 10-6 Ohm-cm2. A minimum contact resistance of 1.5x10-6 O.cm 2 was achieved for the TiB2 based scheme at an annealing temperature of 850-900°C, which was comparable to a regular ohmic contact of Ti/Al/Ni/Au on n GaN. When some of borides contacts were placed on a hot plate or in hot oven for temperature ranging from 200°C to 350°C, the regular metallization contacts degraded before than borides ones. Even with a certain amount of intermixing of the metallization scheme the boride contacts showed minimal roughening and smoother morphology, which, in terms of edge acuity, is crucial for very small gate devices. Schottky contacts were also fabricated and characterized using all the five boride compounds. The barrier height obtained on n GaN was ˜0-5-0.6 eV which was low compared to those obtained by Pt or Ni. This barrier height is too low for use as a gate contact and they can only have limited use, perhaps, in gas sensors where large leakage current can be tolerated in exchange for better thermal reliability. AlGaN/GaN High Electron Mobility Transistors (HEMTs) were fabricated with Ti/Al/TiB2/Ti/Au source/drain ohmic contacts and a variety of gate metal schemes (Pt/Au, Ni/Au, Pt/TiB2/Au or Ni/TiB 2/Au) and were subjected to long-term annealing at 350°C. By comparison with companion devices with conventional Ti/Al/Pt/Au ohmic contacts and Pt/Au gate contacts, the HEMTs with boride-based ohmic metal and either Pt/Au, Ni/Au or Ni/TiB2/Au gate metal showed superior stability of both source-drain current and transconductance after 25 days aging at 350°C. The need for sputter deposition of the borides causes' problem in achieving significantly lower specific contact resistance than with conventional schemes deposited using e-beam evaporation. The borides also seem to be, in general, good getters for oxygen leading to sheet resistivity issues. Ir/Au Schottky contacts and Ti/Al/Ir/Au ohmic contacts on n-type GaN were investigated as a function of annealing temperature and compared to their more common Ni-based counterparts. The Ir/Au ohmic contacts on n-type GaN with n˜1017 cm-3 exhibited barrier heights of 0.55 eV after annealing at 700°C and displayed less intermixing of the contact metals compared to Ni/Au. A minimum specific contact resistance of 1.6 x 10-6 O.cm2 was obtained for the ohmic contacts on n-type GaN with n˜1018 cm-3 after annealing at 900°C. The measurement temperature dependence of contact resistance was similar for both Ti/Al/Ir/Au and Ti/Al/Ni/Au, suggesting the same transport mechanism was present in both types of contacts. The Ir-based ohmic contacts displayed superior thermal aging characteristics at 350°C. Auger Electron Spectroscopy showed that Ir is a superior diffusion barrier at these moderate temperatures than Ni.

Fabrication and Characterization of Plasma Electrolytic Borocarburized Layers on Q235 Low-Carbon Steel at Different Discharge Voltages

NASA Astrophysics Data System (ADS)

Wang, Bin; Wu, Jie; Jin, Xiaoyue; Wu, Xiaoling; Wu, Zhenglong; Xue, Wenbin

The influence of applied voltage on the plasma electrolytic borocarburizing (PEB/C) layer of Q235 low-carbon steel in high-concentration borax solution was investigated. XRD and XPS spectra of PEB/C layer confirmed that the modified boride layer mainly consisted of Fe2B phase, and the FeB phase only exists in the loose top layer. The applied voltage on Q235 steel played a key role in determining the properties of hardened layers. The thickness and microhardness of boride layers increased with the increase of the applied voltage, which led to superior corrosion and wear resistances of Q235 low-carbon steel. The diffusion coefficient (D) of boride layer at 280, 300 and 330V increased with borocarburizing temperature and ranged from 0.062×10-12m2/s to 0.462×10-12m2/s. The activation energy (Q) of boride layer growth during PEB/C treatment was only 52.83kJṡmol-1, which was much lower than that of the conventional boriding process.

Niobium boride layers deposition on the surface AISI D2 steel by a duplex treatment

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kon, O., E-mail: okon42@htotmail.com; Pazarlioglu, S.; Sen, S.

2015-03-30

In this paper, we investigated the possibility of deposition of niobium boride layers on the surface of AISI D2 steel by a duplex treatment. At the first step of duplex treatment, boronizing was performed on AISI D2 steel samples at 1000{sup o}C for 2h and then pre-boronized samples niobized at 850°C, 900°C and 950°C using thermo-reactive deposition method for 1–4 h. The presence of the niobium boride layers such as NbB, NbB{sub 2} and Nb{sub 3}B{sub 4} and also iron boride phases such as FeB, Fe{sub 2}B were examined by X-ray diffraction analysis. Scanning electron microscope (SEM) and micro-hardness measurementsmore » were realized. Experimental studies showed that the depth of the coating layers increased with increasing temperature and times and also ranged from 0.42 µm to 2.43 µm, depending on treatment time and temperature. The hardness of the niobium boride layer was 2620±180 HV{sub 0.005}.« less

Stabilization of scandium rich spinel ferrite CoFe{sub 2−x}Sc{sub x}O{sub 4} (x≤1) in thin films

DOE Office of Scientific and Technical Information (OSTI.GOV)

Lefevre, Christophe, E-mail: christophe.lefevre@ipcms.unistra.fr; Roulland, François; Thomasson, Alexandre

2015-12-15

Scandium rich cobalt ferrites Co{sub y}Fe{sub 3−x−y}Sc{sub x}O{sub 4} with y~1 never obtained in bulk could be stabilized in pulsed laser deposited thin films. Scandium contents of up to x=1 are reached. The cell parameter increases versus x as awaited when considering the size of scandium. It is equal to 0.8620 nm for x=1, significantly higher than that of CoFe{sub 2}O{sub 4} (0.8396 nm). The lattice mismatch between the MgO (100) substrate and the scandium-containing spinel leads to an increased roughness. Cobalt is displaced from the octahedral site by Sc and mainly occupies the tetrahedral sites for high x values.more » - Graphical abstract: Magnification of the XRD patterns recorded on thin films of CoFe{sub 2-x}Sc{sub x}O{sub 4} for x=0, 0.45, 1 and 1.2, the arrows denote the (004) and (008) diffraction lines of the spinel phase.« less

Crystal structure and phase stability of tungsten borides

NASA Astrophysics Data System (ADS)

Li, Quan; Zhou, Dan; Ma, Yanming; Chen, Changfeng

2013-03-01

We address the longstanding and controversial issue of ground-state structures of technically important tungsten borides using a first-principles structural search method via a particle-swarm optimization (PSO) algorithm. We have explored a large set of stable chemical compositions (convex hull) and clarified the ground-state structures for a wide range of boron concentrations, including W2B, W3B2,WB,W2B3, WB2,W2B5, WB3, and WB4. We further assessed relative stability of various tungsten borides and compared the calculated results with previously reported experimental data. The phase diagram predicted by the presented calculations may serve as a useful guide for synthesis of a variety of tungsten borides. This work was supported by DOE Grant No. DE-FC52-06NA26274.

Thermomechanical treatment of welded joints of aluminum-lithium alloys modified by scandium

NASA Astrophysics Data System (ADS)

Malikov, A. G.

2017-12-01

At present, the aeronautical equipment manufacture involves up-to-date high-strength aluminum alloys of decreased density resulting from the lithium admixture. Various technologies of fusible welding of these alloys are being developed. The paper presents experimental investigations of the optimization of the laser welding of aluminum alloys with the scandium-modified welded joint after thermomechanical treatment. The effect of scandium on the micro- and macrostructure is studied along with strength characteristics of the welded joint. It is found that thermomechanical treatment allows us to obtain the strength of the welded joint 0.89 for the Al-Mg-Li system and 0.99 for the Al-Cu-Li system with the welded joint modified by scandium in comparison with the base alloy after treatment.

High Energy Advanced Thermal Storage for Spacecraft Solar Thermal Power and Propulsion Systems

DTIC Science & Technology

2011-10-12

Vol. 108, No. 6, June 1961, pp. 568-572. 38. Storms, E. and Mueller, B., "Phase Relations and Thermodynamic Properties of Transition Metal Borides ...T., and Naka, S., "Formation Process of Tungsten Borides by Solid State Reaction Between Tungsten and Amorphous Boron," Journal of Materials...Molybdenum- Borides ," Journal of Metals, September 1952, pp. 983-988. 41. Ellis, R.C., “Various Preparations of Elemental Boron,” Proceedings of the 1st

Finding the Stable Structures of N1-xWx with an Ab Initio High-Throughput Approach

DTIC Science & Technology

2015-05-26

W. These include borides , carbides, oxides, and other nitrides. We also invented many structures to mimic the random pattern of vacancies on both the...structures. These include nitrides, oxides, borides , and carbides, as well as supercells of standard structures with atoms removed to mimic the random patter...1930). [15] R. Kiessling and Y. H. Liu, Thermal stability of the chromium, iron, and tungsten borides in streaming ammonia and the existence of a new

Molten Boron Phase-Change Thermal Energy Storage to Augment Solar Thermal Propulsion Systems

DTIC Science & Technology

2011-07-13

Thermodynamic Properties of Transition Metal Borides . I. The Molybdenum-boron system and Elemental Boron," Journal of Physical Chemistry, Vol. 81...February 1977, pp. 318-324. 38Itoh, H., Matsudaira, T., and Naka, S., "Formation Process of Tungsten Borides by Solid State Reaction Between Tungsten...Molybdenum-Boron and Some Properties of The Molybdenum- Borides ," Journal of Metals, September 1952, pp. 983-988. 40Stout, N. D., Mar, R. W., and Boo, W. O

Solid state lasers based on chromium- and neodymium-activated scandium garnets operating in the Q-switched mode

NASA Astrophysics Data System (ADS)

Denisov, A. L.; Zharikov, E. V.; Zavartsev, Iu. D.; Zagumennyi, A. I.; Lutts, G. B.

1991-02-01

The development of passively Q-switched and self-Q-switched lasers based on chromium-containing scandium garnets with phototropic centers is reported. The lasers operate over a wide frequency repetition rate with a mean output up to 100 W. The characteristics of phototropic absorption in the 1-micron region are examined, and the possibility of lasing at the weak transition of the Nd(3+) ion in chromium-containing scandium garnets with phototropic centers is discussed.

Gadolinium Scandium Gallium Garnet (GSGG) as a Solid-State Laser Host

DTIC Science & Technology

1987-07-01

o*SATI CODSi1.SBEC EM (otne nrvrs fnceayad dniy nb)k ubr ~~~~~~~~ Gadolinium Scandium Gallium Garnet (GSGG)asaSldtteLerHt 17. ABSTRACT 6.SUJCTTEM...certain other garnet materials for replacement. It also addresses the solid-state laser host material Gadolinium Scandium Gal- lium Garnet (GSGG) and its...by neodymium-doped yttrium aluminum garnet (Nd:YAG) or other mate- rials for most applications. In the years after the invention of the ruby laser, in

Effects of Tungsten Addition on the Microstructure and Corrosion Resistance of Fe-3.5B Alloy in Liquid Zinc

PubMed Central

Liu, Xin; Wang, Mengmeng; Yin, Fucheng; Ouyang, Xuemei; Li, Zhi

2017-01-01

The effects of tungsten addition on the microstructure and corrosion resistance of Fe-3.5B alloys in a liquid zinc bath at 520 °C were investigated by means of scanning electron microscopy, X-ray diffraction and electron probe micro-analysis. The microstructure evolution in different alloys is analyzed and discussed using an extrapolated Fe-B-W ternary phase diagram. Experimental results show that there are three kinds of borides, the reticular (Fe, W)2B, the rod-like (Fe, W)3B and flower-like FeWB. The addition of tungsten can refine the microstructure and improve the stability of the reticular borides. Besides, it is beneficial to the formation of the metastable (Fe, W)3B phase. The resultant Fe-3.5B-11W (wt %) alloy possesses excellent corrosion resistance to liquid zinc. When tungsten content exceeds 11 wt %, the formed flower-like FeWB phase destroys the integrity of the reticular borides and results in the deterioration of the corrosion resistance. Also, the corrosion failure resulting from the spalling of borides due to the initiation of micro-cracks in the grain boundary of borides is discussed in this paper. PMID:28772759

Non-Contact Tabletop Mechanical Testing of Ultra-High Temperature Ceramics

DTIC Science & Technology

2012-05-01

class of refractory materials including transition metal borides , carbides and nitrides e.g. ZrB2l HfB2) ZrC, HfC, TaC, HfN and ZrN. They recently...ike oxidizing atmospheres, at very high temperatures Refractory borides like ZrB2 and HfB2 have extremely high melting temperatures (over 3000°C...But borides are very poor in oxidation resistance, due to the nature of thär oxides Non-protective ZrCfe or Hf02 and volatile liquid B203. Addition

Dislocation Decorrelation and Relationship to Deformation Microtwins during Creep of a Gamma’ Precipitate Strengthened Ni-based Superalloy

DTIC Science & Technology

2011-11-01

Deformation is highly localized around stress concentrators such as carbides, borides and serrated grain boundaries, which act as sources of a/2h110i...highly localized around stress concentrators such as carbides, borides and serrated grain boundaries, which act as sources of a/2h110i matrix-type...phase at different thicknesses. 7328 R.R. Unocic et al. / Acta Materialia 59 (2011) 7325–7339 the image. A number of carbide and/or boride phases are

Beta cell device using icosahedral boride compounds

DOEpatents

Aselage, Terrence L.; Emin, David

2002-01-01

A beta cell for converting beta-particle energies into electrical energy having a semiconductor junction that incorporates an icosahedral boride compound selected from B.sub.12 As.sub.2, B.sub.12 P.sub.2, elemental boron having an .alpha.-rhombohedral structure, elemental boron having a .beta.-rhombohedral structure, and boron carbides of the chemical formula B.sub.12-x C.sub.3-x, where 0.15

The calculated rovibronic spectrum of scandium hydride, ScH

NASA Astrophysics Data System (ADS)

Lodi, Lorenzo; Yurchenko, Sergei N.; Tennyson, Jonathan

2015-07-01

The electronic structure of six low-lying electronic states of scandium hydride, X 1Σ+, a 3Δ, b 3Π, A 1Δ, c 3Σ+ and B 1Π, is studied using multi-reference configuration interaction as a function of bond length. Diagonal and off-diagonal dipole moment, spin-orbit coupling and electronic angular momentum curves are also computed. The results are benchmarked against experimental measurements and calculations on atomic scandium. The resulting curves are used to compute a line list of molecular rovibronic transitions for 45ScH.

Nano-Disperse Borides and Carbides: Plasma Technology Production, Specific Properties, Economic Evaluation

NASA Astrophysics Data System (ADS)

Galevskii, G. V.; Rudneva, V. V.; Galevskii, S. G.; Tomas, K. I.; Zubkov, M. S.

2016-04-01

The experience of production and study on properties of nano-disperse chromium and titanium borides and carbides, and silicon carbide has been generalized. The structure and special service aspects of utilized plasma-metallurgical complex equipped with a three-jet direct-flow reactor with a capacity of 150 kW have been outlined. Processing, heat engineering and service life characteristics of the reactor are specified. The synthesis parameters of borides and carbides, as well as their basic characteristics in nano-disperse condition and their production flow diagram are outlined. Engineering and economic performance of synthesizing borides in laboratory and industrial conditions is assessed, and the respective segment of the international market as well. The work is performed at State Siberian Industrial University as a project part of the State Order of Ministry of Science and Education of the Russian Federation No. 11.1531/2014/K.

The effect of boriding on wear resistance of cold work tool steel

NASA Astrophysics Data System (ADS)

Anzawa, Y.; Koyama, S.; Shohji, I.

2017-05-01

Recently, boriding has attracted extensive attention as surface stiffening processing of plain steel. In this research, the influence of processing time on the formation layer of cold work tool steel (KD11MAX) by Al added fused salt bath was examined. In addition, in order to improve the abrasion resistance of KD11MAX, the effect of the treatment of boronization on the formation layer has been investigated. Boriding were performed in molten borax which contained about 10 mass% Al at processing time of 1.8 ~ 7.2 ks (processing temperature of 1303 K). As a result of the examination, the hardness of the boriding layer becomes about 1900 HV when the processing time of 3.6 ks. Also the abrasion resistance has improved remarkably. Furthermore, it was revealed that the formation layer was boronized iron from the Vickers hardness and analysis of the X-ray diffraction measurement.

Metal Immiscibility Route to Synthesis of Ultrathin Carbides, Borides, and Nitrides.

PubMed

Wang, Zixing; Kochat, Vidya; Pandey, Prafull; Kashyap, Sanjay; Chattopadhyay, Soham; Samanta, Atanu; Sarkar, Suman; Manimunda, Praveena; Zhang, Xiang; Asif, Syed; Singh, Abhisek K; Chattopadhyay, Kamanio; Tiwary, Chandra Sekhar; Ajayan, Pulickel M

2017-08-01

Ultrathin ceramic coatings are of high interest as protective coatings from aviation to biomedical applications. Here, a generic approach of making scalable ultrathin transition metal-carbide/boride/nitride using immiscibility of two metals is demonstrated. Ultrathin tantalum carbide, nitride, and boride are grown using chemical vapor deposition by heating a tantalum-copper bilayer with corresponding precursor (C 2 H 2 , B powder, and NH 3 ). The ultrathin crystals are found on the copper surface (opposite of the metal-metal junction). A detailed microscopy analysis followed by density functional theory based calculation demonstrates the migration mechanism, where Ta atoms prefer to stay in clusters in the Cu matrix. These ultrathin materials have good interface attachment with Cu, improving the scratch resistance and oxidation resistance of Cu. This metal-metal immiscibility system can be extended to other metals to synthesize metal carbide, boride, and nitride coatings. © 2017 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Kinetics and Tribological Characterization of Pack-Borided AISI 1025 Steel

NASA Astrophysics Data System (ADS)

Gómez-Vargas, O. A.; Keddam, M.; Ortiz-Domínguez, M.

2017-03-01

In this present study, the AISI 1025 steel was pack-borided in the temperature range of 1,123-1,273 K for different treatment times ranging from 2 to 8 h. A diffusion model was suggested to estimate the boron diffusion coefficients in the Fe2B layers. As a result, the boron activation energy for the AISI 1025 steel was estimated as 174.36 kJ/mol. This value of energy was compared with the literature data. To extend the validity of the present model, other additional boriding conditions were considered. The boride layers formed on the AISI 1025 steel were characterized by the following experimental techniques: scanning electron microscopy, X-ray diffraction analysis and the Daimler-Benz Rockwell-C indentation technique. Finally, the scratch and pin-on-disc tests for wear resistance were achieved using an LG Motion Ltd and a CSM tribometer, respectively, under dry sliding conditions.

Ceramic material suitable for repair of a space vehicle component in a microgravity and vacuum environment, method of making same, and method of repairing a space vehicle component

NASA Technical Reports Server (NTRS)

Riedell, James A. (Inventor); Easler, Timothy E. (Inventor)

2009-01-01

A precursor of a ceramic adhesive suitable for use in a vacuum, thermal, and microgravity environment. The precursor of the ceramic adhesive includes a silicon-based, preceramic polymer and at least one ceramic powder selected from the group consisting of aluminum oxide, aluminum nitride, boron carbide, boron oxide, boron nitride, hafnium boride, hafnium carbide, hafnium oxide, lithium aluminate, molybdenum silicide, niobium carbide, niobium nitride, silicon boride, silicon carbide, silicon oxide, silicon nitride, tin oxide, tantalum boride, tantalum carbide, tantalum oxide, tantalum nitride, titanium boride, titanium carbide, titanium oxide, titanium nitride, yttrium oxide, zirconium diboride, zirconium carbide, zirconium oxide, and zirconium silicate. Methods of forming the ceramic adhesive and of repairing a substrate in a vacuum and microgravity environment are also disclosed, as is a substrate repaired with the ceramic adhesive.

Influence of scandium on the microstructure and strength properties of the welded joint at the laser welding of aluminum-lithium alloys

NASA Astrophysics Data System (ADS)

Malikov, A. G.; Golyshev, A. A.; Ivanova, M. Yu.

2017-10-01

Today, aeronautical equipment manufacture involves up-to-date high-strength aluminum alloys of decreased density resulting from lithium admixture. Various technologies of fusible welding of these alloys are being developed. Serious demands are imposed to the welded joints of aluminum alloys in respect to their strength characteristics. The paper presents experimental investigations of the optimization of the laser welding of aluminum alloys with the scandium-modified welded joint. The effect of scandium on the micro-and macro-structure has been studied as well as the strength characteristics of the welded joint. It has been found that scandium under in the laser welding process increases the welded joint elasticity for the system Al-Mg-Li, aluminum alloy 1420 by 20 %, and almost doubles the same for the system Al-Cu-Li, aluminum alloy 1441.

Effect of borides on hot deformation behavior and microstructure evolution of powder metallurgy high borated stainless steel

DOE Office of Scientific and Technical Information (OSTI.GOV)

Zhou, Xuan

To investigate borides effect on the hot deformation behavior and microstructure evolution of powder metallurgy high borated stainless steel, hot compression tests at the temperatures of 950– 1150 °C and the strain rates of 0.01– 10 s{sup −1} were performed. Flow stress curves indicated that borides increased the material's stress level at low temperature but the strength was sacrificed at temperatures above 1100 °C. A hyperbolic-sine equation was used to characterize the dependence of the flow stress on the deformation temperature and strain rate. The hot deformation activation energy and stress exponent were determined to be 355 kJ/mol and 3.2,more » respectively. The main factors leading to activation energy and stress exponent of studied steel lower than those of commercial 304 stainless steel were discussed. Processing maps at the strains of 0.1, 0.3, 0.5, and 0.7 showed that flow instability mainly concentrated at 950– 1150 °C and strain rate higher than 0.6 s{sup −1}. Results of microstructure illustrated that dynamic recrystallization was fully completed at both high temperature-low strain rate and low temperature-high strain rate. In the instability region cracks were generated in addition to cavities. Interestingly, borides maintained a preferential orientation resulting from particle rotation during compression. - Highlights: •The decrement of activation energy was affected by boride and boron solution. •The decrease of stress exponent was influenced by composition and Cottrell atmosphere. •Boride represented a preferential orientation caused by particle rotation.« less

On the Correlation between Morphology of alpha and Its Crystallographic Orientation Relationship with TiB and Beta in Boron Containing Ti-5Al-5Mo-5V-3Cr-0.5Fe Alloy (Preprint)

DTIC Science & Technology

2012-01-01

submitted to Metallurgical Transactions. This document contains color. 14. ABSTRACT While the role of borides on the microstructure of titanium...Ohio, U.S.A. Abstract While the role of borides on the microstructure of titanium alloys has been discussed in many previous reports, this paper...morphology of  precipitates nucleating from boride precipitates present in the  matrix of a titanium alloy; and (b) to investigate the role of presence or

Thermodynamic modelling of phase equilibrium in system Ti-B-Si-C, synthesis and phases composition of borides and carbides layers on titanic alloyVT-1 at electron beam treatment in vacuum

NASA Astrophysics Data System (ADS)

Smirnyagina, N. N.; Khaltanova, V. M.; Lapina, A. E.; Dasheev, D. E.

2017-01-01

Composite layers on the basis of carbides and borides the titan and silicon on titanic alloy VT-1 are generated at diffused saturation in vacuum. Formation in a composite of MAX phase Ti3SiC2 is shown. Thermodynamic research of phase equilibrium in systems Ti-Si-C and Ti-B-C in the conditions of high vacuum is executed. The thermodynamics, formation mechanisms of superfirm layers borides and carbides of the titan and silicon are investigated.

Effect of mechanical activation on jell boronizing treatment of the AISI 4140

NASA Astrophysics Data System (ADS)

Yılmaz, S. O.; Karataş, S.

2013-06-01

The article presents the effect of mechanical activation on the growth kinetics of boride layer of boronized AISI 4140 steel. The samples were boronized by ferroboron + (SiO2-Na2O) powders for 873-1173 K temperature and 2, 4, 6 and 8 h times, respectively. The morphology and types of borides formed on the surface of AISI 4140 steel substrate were analyzed. Layer growth kinetics were analyzed by measuring the extent of penetration of FeB and Fe2B sublayers as function of treatment time and temperature in the range of 873-1173 K. High diffusivity was obtained by creating a large number of defects through mechanical activation in the form of nanometer sized crystalline particles through the repeated fracturing and cold-welding of the powder particles, and a depth of 100 μm was found in the specimen borided by the 2 h MA powders, for 4 h and 1073 K, where 2000-2350 HV were measured. Consequently, the application conditions of boronizing were improved by usage of mechanical activation. The preferred Fe2B boride without FeB could be formed in the boride layer under 973 K boronizing temperature by mechanically activated by ferroboron + sodium silicate powder mixture due to the decrease of the activation energy.

Selective recovery of vanadium and scandium by ion exchange with D201 and solvent extraction using P507 from hydrochloric acid leaching solution of red mud.

PubMed

Zhu, Xiaobo; Li, Wang; Tang, Sen; Zeng, Majian; Bai, Pengyuan; Chen, Lunjian

2017-05-01

D201 resin and P507 extractant diluted with sulfonated kerosene were used to respectively separate vanadium and scandium, and impurity ions from hydrochloric acid leaching solution of red mud. More than 99% of vanadium was selectively adsorbed from the hydrochloric acid leaching solution under the conditions of pH value of 1.8, volume ratio of leaching solution to resin of 10, and flow rate of 3.33 mL/min. Maximum extraction and separation of scandium was observed from the acid leaching solution at an aqueous pH value of 0.2. More than 99% of scandium can be selectively extracted using 15% P507, 5% TBP at the aqueous solution/organic phase (A/O) ratio of 10:1 for 6 min. The loaded organic phase was washed with 0.3 mol/L sulfuric acid, wherein most impurities were removed. After the process of desorption or stripping, precipitation, and roasting, high-purity V 2 O 5 and Sc 2 O 3 were obtained. Finally, a conceptual flow sheet was established to separate and recover vanadium and scandium from red mud hydrochloric acid leaching solution. Copyright © 2017 Elsevier Ltd. All rights reserved.

Yttria Nanoparticle Reinforced Commercially Pure (CP) Titanium

DTIC Science & Technology

2011-09-01

nanoparticles as well as titanium boride (TiB) reinforcements were produced through gas atomization. After consolidation and extrusion, room temperature...pure FE iron O oxygen Ti titanium TiB titanium boride TYS tensile yield strength UTS ultimate tensile strength wt% weight percent Y2O3

Growth kinetics of borided layers: Artificial neural network and least square approaches

NASA Astrophysics Data System (ADS)

Campos, I.; Islas, M.; Ramírez, G.; VillaVelázquez, C.; Mota, C.

2007-05-01

The present study evaluates the growth kinetics of the boride layer Fe 2B in AISI 1045 steel, by means of neural networks and the least square techniques. The Fe 2B phase was formed at the material surface using the paste boriding process. The surface boron potential was modified considering different boron paste thicknesses, with exposure times of 2, 4 and 6 h, and treatment temperatures of 1193, 1223 and 1273 K. The neural network and the least square models were set by the layer thickness of Fe 2B phase, and assuming that the growth of the boride layer follows a parabolic law. The reliability of the techniques used is compared with a set of experiments at a temperature of 1223 K with 5 h of treatment time and boron potentials of 2, 3, 4 and 5 mm. The results of the Fe 2B layer thicknesses show a mean error of 5.31% for the neural network and 3.42% for the least square method.

Effect of scandium on the phase composition and mechanical properties of ABM alloys

NASA Astrophysics Data System (ADS)

Molchanova, L. V.

2010-09-01

The effect of scandium on the composition and mechanical properties of ABM-1 alloys (Al-30% Be-5% Mg) is studied. The scandium content is varied from 0.1 to 0.5 wt %. It is established that, in the studied part of the Al-Be-Mg-Sc system, an aluminum solid solution (Al) and the ScBe13 compound are in equilibrium with a beryllium solid solution (Be). Magnesium dissolves in both the aluminum component and the ScBe13 compound. The strengthening effect related to the decomposition of the solid solution and the precipitation of Al3Sc cannot be extended to the strengthening of ABM-type alloys. Additions of 0.1-0.15 wt % Sc only weakly improve the mechanical properties of the alloys due to the refinement of beryllium-component grains. At high scandium contents, the strength increases insignificantly due to primary precipitation of ScBe13 and the plasticity decreases simultaneously.

Scandium places aluminium welding on a new plateau

DOE Office of Scientific and Technical Information (OSTI.GOV)

Irving, B.

1997-07-01

An interesting new development in nonferrous metallurgy seems to be taking the world by storm. The topic is scandium, a rare metal that is now being mined in the Ukraine. Known for its toughness, it was formerly a top secret material used in fighter planes, including the MIG 29, during the existence of the Soviet Union. This metal is now being introduced into a variety of aluminum alloys in this country, both in base metal and filler metal forms. The results are increases in strength, fatigue life and weldability. US interest in scandium-containing products is burgeoning, examples include aircraft, componentsmore » for automobiles and trucks, high-speed trains, and boats. The technology is being developed and implemented at two laboratories, one in Baltimore, MD, and the other in Kiev, Ukraine. Both laboratories belong to Ashurst Technology Ltd., Hamilton, Bermuda. The author recently visited the Baltimore laboratory where he learned more about scandium and its current and potential effects on industry. This report documents what he learned.« less

Selection of peptides binding to metallic borides by screening M13 phage display libraries.

PubMed

Ploss, Martin; Facey, Sandra J; Bruhn, Carina; Zemel, Limor; Hofmann, Kathrin; Stark, Robert W; Albert, Barbara; Hauer, Bernhard

2014-02-10

Metal borides are a class of inorganic solids that is much less known and investigated than for example metal oxides or intermetallics. At the same time it is a highly versatile and interesting class of compounds in terms of physical and chemical properties, like semiconductivity, ferromagnetism, or catalytic activity. This makes these substances attractive for the generation of new materials. Very little is known about the interaction between organic materials and borides. To generate nanostructured and composite materials which consist of metal borides and organic modifiers it is necessary to develop new synthetic strategies. Phage peptide display libraries are commonly used to select peptides that bind specifically to metals, metal oxides, and semiconductors. Further, these binding peptides can serve as templates to control the nucleation and growth of inorganic nanoparticles. Additionally, the combination of two different binding motifs into a single bifunctional phage could be useful for the generation of new composite materials. In this study, we have identified a unique set of sequences that bind to amorphous and crystalline nickel boride (Ni3B) nanoparticles, from a random peptide library using the phage display technique. Using this technique, strong binders were identified that are selective for nickel boride. Sequence analysis of the peptides revealed that the sequences exhibit similar, yet subtle different patterns of amino acid usage. Although a predominant binding motif was not observed, certain charged amino acids emerged as essential in specific binding to both substrates. The 7-mer peptide sequence LGFREKE, isolated on amorphous Ni3B emerged as the best binder for both substrates. Fluorescence microscopy and atomic force microscopy confirmed the specific binding affinity of LGFREKE expressing phage to amorphous and crystalline Ni3B nanoparticles. This study is, to our knowledge, the first to identify peptides that bind specifically to amorphous and to crystalline Ni3B nanoparticles. We think that the identified strong binding sequences described here could potentially serve for the utilisation of M13 phage as a viable alternative to other methods to create tailor-made boride composite materials or new catalytic surfaces by a biologically driven nano-assembly synthesis and structuring.

Synthesis of Binary Transition Metal Nitrides, Carbides and Borides from the Elements in the Laser-Heated Diamond Anvil Cell and Their Structure-Property Relations

PubMed Central

Friedrich, Alexandra; Winkler, Björn; Juarez-Arellano, Erick A.; Bayarjargal, Lkhamsuren

2011-01-01

Transition metal nitrides, carbides and borides have a high potential for industrial applications as they not only have a high melting point but are generally harder and less compressible than the pure metals. Here we summarize recent advances in the synthesis of binary transition metal nitrides, carbides and borides focusing on the reaction of the elements at extreme conditions generated within the laser-heated diamond anvil cell. The current knowledge of their structures and high-pressure properties like high-(p,T) stability, compressibility and hardness is described as obtained from experiments. PMID:28824101

Directionally Solidified Eutectic Ceramics for Multifunctional Aerospace Applications

DTIC Science & Technology

2013-01-01

eutectic materials development through a new initiative entitled Boride Eutectic Project. These results first time organize and populate materials...property databases, and utilize an iterative feedback routine to constantly improve the design process of the boride eutectics LaB6-MeB2 (Me = Zr, Hf, Ti

Hydrogen-rich scandium compounds at high pressures

NASA Astrophysics Data System (ADS)

Abe, Kazutaka

2017-10-01

Scandium hydrides at high pressures have been investigated by using ab initio density functional calculations. Although the stable scandium hydride so far known to have the highest content rate of hydrogen is ScH3, other more hydrogen-rich compounds are found to be possible at high pressures. These are ScH4 in the I 4 /m m m structure above 160 GPa, ScH6 in the P 63/m m c structure from 135 to 265 GPa, and ScH6 in the I m 3 ¯m structure above 265 GPa. The three phases are all metallic, and the superconducting transition temperatures estimated from the extended McMillan equation are 67 K in the I 4 /m m m ScH4 at 195 GPa, 63 K in the P 63/m m c ScH6 at 145 GPa, and 130 K in the I m 3 ¯m ScH6 at 285 GPa. While the I 4 /m m m tetrahydride and the I m 3 ¯m hexahydride were similarly predicted for yttrium (another group-3 element), the P 63/m m c hexahydride is possible only for scandium. The smaller atomic size of scandium stabilizes the P 63/m m c structure, and other nearby d -block elements, whose atomic sizes are smaller or comparable, might be likewise capable of forming such polyhydrides.

Superabrasive boride and a method of preparing the same by mechanical alloying and hot pressing

DOEpatents

Cook, Bruce A.; Harringa, Joel L.; Russell, Alan M.

2002-08-13

A ceramic material which is an orthorhombic boride of the general formula: AlMgB.sub.14 :X, with X being a doping agent. The ceramic is a superabrasive, and in most instances provides a hardness of 40 GPa or greater.

Scandium oxide antireflection coatings for superluminescent LEDs

NASA Technical Reports Server (NTRS)

Ladany, I.; Zanzucchi, P. J.; Andrews, J. T.; Kane, J.; Depiano, E.

1986-01-01

For an employment of laser diodes as superluminescent LEDs (SLDs) or amplifiers, the facets of the diodes must be coated with antireflection films. In the work reported, scandium oxide was evaporated from an e-beam source onto Supersil II fused silica substrates. The obtained samples were used for measurements of absorption and reflectivity. Results of index measurements on e-beam evaporated films are presented. It is shown that excellent coatings with reflectivities of 0.00025 can be obtained using these films. Attention is given to the refractive indices for scandium oxide films as a function of wavelength, the power output vs current for laser before coating and after coating with Sc2O3.

Theoretical and Experimental Investigations on the Mechanism of Carbothermal Reduction of Zirconia (Preprint)

DTIC Science & Technology

2012-08-01

Properties. Abyss Books, Washington, D.C., 2002. 2. G. Montel, A. Lebugle and H. Pastor. "Manufacture of Materials Containing Refractory Borides ...and ZrO2," International Journal of Refractory Metals and Hard Materials, 17, 235-43 (1999). 10. A.W. Weimer, Carbide, nitride and boride

Adhesive and Cohesive Strength in FeB/Fe2B Systems

NASA Astrophysics Data System (ADS)

Meneses-Amador, A.; Blancas-Pérez, D.; Corpus-Mejía, R.; Rodríguez-Castro, G. A.; Martínez-Trinidad, J.; Jiménez-Tinoco, L. F.

2018-05-01

In this work, FeB/Fe2B systems were evaluated by the scratch test. The powder-pack boriding process was performed on the surface of AISI M2 steel. The mechanical parameters, such as yield stress and Young's modulus of the boride layer, were obtained by the instrumented indentation technique. Residual stresses produced on the boride layer were estimated by using the x-ray diffraction (XRD) technique. The scratch test was performed in order to evaluate the cohesive/adhesive strength of the FeB/Fe2B coating. In addition, a numerical evaluation of the scratch test on boride layers was performed by the finite element method. Maximum principal stresses were related to the failure mechanisms observed by the experimental scratch test. Shear stresses at the interfaces of the FeB/Fe2B/substrate system were also evaluated. Finally, the results obtained provide essential information about the effect of the layer thickness, the residual stresses, and the resilience modulus on the cohesive/adhesive strength in FeB/Fe2B systems.

The Effects of Borides on the Mechanical Properties of TLPB Repaired Inconel 738 Superalloy

NASA Astrophysics Data System (ADS)

Wei, J.; Ye, Y.; Sun, Z.; Zou, G.; Bai, H.; Wu, A.; Liu, L.

2017-10-01

The transient liquid phase diffusion bonding (TLPB) method was used to repair an artificial crack in Inconel 738, which was notched by a femtosecond laser. Mixed ratios of BNi-1a:DF-4B were investigated at the bonding temperature of 1373 K (1100 °C) for 2 to 36 hours. The effect of borides on the mechanical properties of TLPB repaired joints was studied through analysis of the microstructure, fracture path, and morphology observations. The borides formation, morphology, distribution, and joints strength were studied in detail. The results showed that the diffusion of B can either increase or decrease the joint strength, depending on its distribution and morphology. The amount of large blocky Ni-B compounds in the precipitate zone were reduced with increasing holding time, which resulted in an increase in joint strength. Nevertheless, further increasing the holding time led to a decrease in joint strength because of the formation of continuous acicular borides in the diffusion-affected zone. The fracture modes of TLPB joints were also discussed on the basis of the microstructure and fractography.

Study of strength properties of semi-finished products from economically alloyed high-strength aluminium-scandium alloys for application in automobile transport and shipbuilding

NASA Astrophysics Data System (ADS)

Baranov, Vladimir; Sidelnikov, Sergey; Zenkin, Evgeny; Frolov, Viktor; Voroshilov, Denis; Yakivyuk, Olga; Konstantinov, Igor; Sokolov, Ruslan; Belokonova, Irina

2018-04-01

The results of a study on the strength of rolled products from aluminium alloys doped with scandium under various processing conditions of hot and cold rolling are presented. The regularities of metal flow and the level of strength of deformed semi-finished products from aluminum-scandium alloys are established, depending on the total degree of deformation and the various modes of single reduction during rolling. It is shown that when using one heating of a cast billet to obtain high-quality semi-finished products, the temperature during the rolling process should not be lower than 350-370°, and the total degree of deformation does not exceed 50-60%. It was found that the semi-finished products from alloys with a content of scandium in the range 0.11-0.12% in the deformed state had elevated values of ultimate tensile strength and yield strength of the metal, which allows them to be recommended for industrial production of sheet metal products.

Micro-Abrasion Wear Resistance of Borided 316L Stainless Steel and AISI 1018 Steel

NASA Astrophysics Data System (ADS)

Reséndiz-Calderon, C. D.; Rodríguez-Castro, G. A.; Meneses-Amador, A.; Campos-Silva, I. E.; Andraca-Adame, J.; Palomar-Pardavé, M. E.; Gallardo-Hernández, E. A.

2017-11-01

The 316L stainless steel has high corrosion resistance but low tribological performance. In different industrial sectors (biomedical, chemical, petrochemical, and nuclear engineering), improvement upon wear resistance of 316L stainless steel components using accessible and inexpensive methods is critical. The AISI 1018 steel is widely used in industry, but its tribological performance is not the best among steels. Therefore, in this study the behavior of the borided 316L stainless steel and 1018 steel is evaluated under micro-abrasion wear. The boriding was carried out at 1223 K over 6 h of exposure time, resulting in a biphase layer composed of FeB/Fe2B phases. In order to evaluate Fe2B phase with no influence from FeB phase, AISI 1018 steel samples were borided at 1273 K for over 20 min and then diffusion annealed at 1273 K over 2 h to obtain a Fe2B mono-phase layer. Micro-abrasion wear resistance was evaluated by a commercial micro-abrasion testing rig using a mix of F-1200 SiC particles with deionized water as abrasive slurry. The obtained wear rates for FeB and Fe2B phases and for the 316L stainless steel were compared. Wear resistance of 316L stainless steel increases after boriding. The wear mechanisms for both phases and for the stainless steel were identified. Also, transient conditions for rolling and grooving abrasion were determined for the FeB and Fe2B phases.

Surface decoration through electrostatic interaction leading to enhanced reactivity: Low temperature synthesis of nanostructured chromium borides (CrB and CrB{sub 2})

DOE Office of Scientific and Technical Information (OSTI.GOV)

Menaka,; Kumar, Bharat; Kumar, Sandeep

The present study describes a novel low temperature route at ambient pressure for the synthesis of nanocrystalline chromium borides (CrB and CrB{sub 2}) without using any flux or additives. The favorable and intimate mixing of nanoparticles of chromium acetate (Cr source) and boron forms an active chromium–boron precursor which decomposes at much lower temperature (400 °C) to form CrB (which is ∼1000 °C less than the known ambient pressure synthesis). The chromium acetate nanoparticles (∼5 nm) decorate the larger boron particles (150–200 nm) due to electrostatic interactions resulting from opposing surface charges of boron (zeta potential:+48.101 mV) and chromium acetatemore » (zeta potential:−4.021 mV) in ethanolic medium and is evident in the TEM micrographs. The above method leads to the formation of pure CrB film like structure at 400 °C and nanospheres (40–60 nm) at 600 °C. Also, chromium diboride (CrB{sub 2}) nanoparticles (25 nm) could be obtained at 1000 °C. - Graphical abstract: Variation of surface charge of reactants, precursor and the products, chromium borides (CrB and CrB{sub 2}). Highlights: ► Novel borothermal reduction process for synthesis of chromium boride. ► Significant lowering of reaction temperature to obtain nanocrystalline chromium boride. ► Enhanced reactivity due to appropriate surface interactions.« less

Investigation of diffusional interaction between P91 grade ferritic steel and Fe-15 wt.%B alloy and study of kinetics of boride formation at high temperature

NASA Astrophysics Data System (ADS)

Rai, Arun Kumar; Vijayashanthi, N.; Tripathy, H.; Hajra, R. N.; Raju, S.; Murugesan, S.; Saroja, S.

2017-11-01

In the present study, the feasibility of employing the indigenously developed ferroboron alloy (Fe-15 wt.%B) as an alternate neutron shield material in combination with 9Cr-based ferritic steel (P91) clad in future Indian fast breeder reactors (FBR), has been investigated from a metallurgical perspective. Towards this goal, a series of diffusion couple experiments have been conducted at three different temperatures namely, 600, 700 and 800 °C for time durations up to 5000 h. The thickness of interaction layer has been monitored using standard metallographic procedures. The experiments revealed that ferroboron/P91 combination exhibited a tendency to form complex intermetallic borides at the interface. The structural and microstructural characterization of the interface confirmed that the reaction layer consists predominantly of borides of Fe and Cr of type FeB, Fe2B, (Fe,Cr)2B and (Fe,Cr)B. The measured variation of interaction layer thickness as a function of time and temperature have been modelled in terms of diffusion mediated interaction. The growth kinetics of borided layer has followed the parabolic law at each temperature, and the apparent activation energy for boride layer formation is found to be of the order of 115 kJ mol-1. This indicates that the kinetics of boriding could be governed by diffusion of B into the P91 matrix. Based on the findings of present study, an extrapolative estimate of the clad attack thickness at 550 °C for 60 years of operating time has been made and it turns out to be 210 ± 15 μm, which is less than the clad thickness of FBR shielding subassembly (4 mm) [1]. Thus, this study confirms that at testing temperatures from 550 to 600 °C, the ferroboron/P91 steel combination can be safely employed for shielding subassembly applications in fast reactors.

Kinetics of electrolysis current reversal boriding of tool steels in a boron-containing oxychloride melt based on CaCl2

NASA Astrophysics Data System (ADS)

Chernov, Ya. B.; Filatov, E. S.

2017-08-01

The kinetics of thermal diffusion boriding in a melt based on calcium chloride with a boron oxide additive is studied using reversed current. The main temperature, concentration, and current parameters of the process are determined. The phase composition of the coating is determined by a metallographic method.

Search for New Superconductors for Energy and Power Applications

DTIC Science & Technology

2014-10-21

superconductors, borides , carbides, silicides, and chalcogenides. In addition, a number of thin film systems have been explored: A15s, superlattices, arrays of...YBa2Cu3O7 Bi2Se3 Eu-Si-C ErRh4B4 Bi2Sr2CaCu2O8 (UD, OD) Sb2Se3 V-Si-C (Ga,Mn)As CuO ZrSe2 Sm-Si-C Hf(FeCo)P Y1-xCaxCrO3 Fe-Te-Se BORIDES Hf-Fe-C-P...Physics, Warsaw, Poland Table III New superconductors, discovered by UCSD MURI team. BORIDES Tc (K) Nb0.9Zr0.1B 11.2 ZrNbxB 9.0 ZrVxB 9.0

Silicon carbide sintered body manufactured from silicon carbide powder containing boron, silicon and carbonaceous additive

NASA Technical Reports Server (NTRS)

Tanaka, Hidehiko

1987-01-01

A silicon carbide powder of a 5-micron grain size is mixed with 0.15 to 0.60 wt% mixture of a boron compound, i.e., boric acid, boron carbide (B4C), silicon boride (SiB4 or SiB6), aluminum boride, etc., and an aluminum compound, i.e., aluminum, aluminum oxide, aluminum hydroxide, aluminum carbide, etc., or aluminum boride (AlB2) alone, in such a proportion that the boron/aluminum atomic ratio in the sintered body becomes 0.05 to 0.25 wt% and 0.05 to 0.40 wt%, respectively, together with a carbonaceous additive to supply enough carbon to convert oxygen accompanying raw materials and additives into carbon monoxide.

Method of boronizing transition metal surfaces

DOEpatents

Koyama, Koichiro; Shimotake, Hiroshi

1983-01-01

A method is presented for preparing a boride layer on a transition metal substrate for use in corrosive environments or as a harden surface in machine applications. This method is particularly useful in treating current collectors for use within a high temperature and corrosive electrochemical cell environment. A melt of a alkali metal boride tetrafluoride salt including such as KF to lower its melting point is prepared including a dissolved boron containing material, for instance NiB, MnB.sub.2, or CrB.sub.2. A transition metal to be coated is immersed in the melt at a temperature of no more than 700.degree. C. and a surface boride layer of that transition metal is formed within a period of about 24 hours on the substrate surface.

Structural properties of scandium inorganic salts

DOE PAGES

Sears, Jeremiah M.; Boyle, Timothy J.

2016-12-16

Here, the structural properties of reported inorganic scandium (Sc) salts were reviewed, including the halide (Cl, Br, and I), nitrate, sulfate, and phosphate salts. Additional analytical techniques used for characterization of these complexes (metrical data, FTIR and 45Sc NMR spectroscopy) were tabulated. A structural comparison of Sc to select lanthanide (La, Gd, Lu) salt complexes was briefly evaluated.

Highly Reactive Scandium Phosphinoalkylidene Complex: C-H and H-H Bonds Activation.

PubMed

Mao, Weiqing; Xiang, Li; Alvarez Lamsfus, Carlos; Maron, Laurent; Leng, Xuebing; Chen, Yaofeng

2017-01-25

The first scandium phosphinoalkylidene complex was synthesized and structurally characterized. The complex has the shortest Sc-C bond lengths reported to date (2.089(3) Å). DFT calculations reveal the presence of a three center π interaction in the complex. This scandium phosphinoalkylidene complex undergoes intermolecular C-H bond activation of pyridine, 4-dimethylamino pyridine and 1,3-dimethylpyrazole at room temperature. Furthermore, the complex rapidly activates H 2 under mild conditions. DFT calculations also demonstrate that the C-H activation of 1,3-dimethylpyrazole is selective for thermodynamic reasons and the relatively slow reaction is due to the need of fully breaking the chelating effect of the phosphino group to undergo the reaction whereas this is not the case for H 2 .

Lifetime measurements and oscillator strengths in singly ionized scandium and the solar abundance of scandium

NASA Astrophysics Data System (ADS)

Pehlivan Rhodin, A.; Belmonte, M. T.; Engström, L.; Lundberg, H.; Nilsson, H.; Hartman, H.; Pickering, J. C.; Clear, C.; Quinet, P.; Fivet, V.; Palmeri, P.

2017-12-01

The lifetimes of 17 even-parity levels (3d5s, 3d4d, 3d6s and 4p2) in the region 57 743-77 837 cm-1 of singly ionized scandium (Sc II) were measured by two-step time-resolved laser induced fluorescence spectroscopy. Oscillator strengths of 57 lines from these highly excited upper levels were derived using a hollow cathode discharge lamp and a Fourier transform spectrometer. In addition, Hartree-Fock calculations where both the main relativistic and core-polarization effects were taken into account were carried out for both low- and high-excitation levels. There is a good agreement for most of the lines between our calculated branching fractions and the measurements of Lawler & Dakin in the region 9000-45 000 cm-1 for low excitation levels and with our measurements for high excitation levels in the region 23 500-63 100 cm-1. This, in turn, allowed us to combine the calculated branching fractions with the available experimental lifetimes to determine semi-empirical oscillator strengths for a set of 380 E1 transitions in Sc II. These oscillator strengths include the weak lines that were used previously to derive the solar abundance of scandium. The solar abundance of scandium is now estimated to logε⊙ = 3.04 ± 0.13 using these semi-empirical oscillator strengths to shift the values determined by Scott et al. The new estimated abundance value is in agreement with the meteoritic value (logεmet = 3.05 ± 0.02) of Lodders, Palme & Gail.

Subminiature eddy current transducers for studying boride coatings

NASA Astrophysics Data System (ADS)

Dmitriev, S. F.; Ishkov, A. V.; Malikov, V. N.; Sagalakov, A. M.

2016-07-01

Strengthening of parts and units of machines, increased reliability and longer service life is an important task of modern mechanical engineering. The main objects of study in the work were selected steel 65G and 50HGA, wear-resistant boride coatings ternary system Fe-B-Fe n B which were investigated by scanning electron microscopy and eddy-current nondestructive methods.

Demonstration of Shear Localization in Ultrafine Grained Tungsten Alloys via Powder Metallurgy Processing Route

DTIC Science & Technology

2012-09-01

of a di-tungsten boride (W2B) phase was not detected in the nW-B sample, but the low concentration of boron may have made this phase undetectable by...Split Hopkinson Bar UFG ultrafine grained W2B di-tungsten boride XRD x-ray diffraction NO. OF NO. OF COPIES ORGANIZATION COPIES

Slater-Pauling behavior within quaternary intermetallic borides of the Ti{sub 3}Co{sub 5}B{sub 2} structure-type

DOE Office of Scientific and Technical Information (OSTI.GOV)

Burghaus, Jens; Dronskowski, Richard, E-mail: drons@HAL9000.ac.rwth-aachen.d; Miller, Gordon J.

2009-10-15

First-principles, density-functional studies of several intermetallic borides of the general type M{sub 2}M'Ru{sub 5-n}Rh{sub n}B{sub 2} (n=0-5; M=Sc, Ti, Nb; M'=Fe, Co) show that the variation in saturation magnetic moment with valence-electron count follows a Slater-Pauling curve, with a maximum moment occurring typically at 66 valence electrons. The magnetic moments in these compounds occur primarily from the 3d electrons of the magnetically active M' sites, with some contribution from the Ru/Rh sites via magnetic polarization. Electronic DOS curves reveal that a rigid-band approach is a reasonable approximation for the estimation of saturation moments and the analysis of orbital interactions inmore » this family of complex borides. COHP analyses of the M'-M' orbital interactions indicate optimized interactions in the minority spin states for Co-containing phases, but strong bonding interactions remaining in Fe-containing phases. - Graphical abstract: Theoretically determined (spin-polarized LMTO-GGA) local magnetic moments as a function of the chemical valence Z for various intermetallic borides.« less

Superplastic behavior of two ultrahigh boron steels

NASA Astrophysics Data System (ADS)

Jiménez, J. A.; González-Doncel, G.; Acosta, P.; Ruano, O. A.

1994-06-01

The high-temperature deformation behavior of two ultrahigh boron steels containing 2.2 pct and 4.9 pct B was investigated. Both alloys were processed via powder metallurgy involving gas atomization and hot isostatic pressing (hipping) at various temperatures. After hipping at 700 °C, the Fe-2.2 pct B alloy showed a fine microstructure consisting of l- µm grains and small elongated borides (less than 1 µm) . At 1100 °C, a coarser microstructure with rounded borides was formed. This alloy was superplastic at 850 °C with stress exponents of about two and tensile elongations as high as 435 pct. The microstructure of the Fe-4.9 pct B alloy was similar to that of the Fe-2.2 pct B alloy showing, in addition, coarse borides. This alloy also showed low stress exponent values but lacked high tensile elongation (less than 65 pct), which was attributed to the presence of stress accumulation at the interface between the matrix and the large borides. A change in the activation energy value at the α-γ transformation temperature was seen in the Fe-2.2 pct B alloy. The plastic flow data were in agreement with grain boundary sliding and slip creep models.

Friction and wear of radiofrequency-sputtered borides, silicides, and carbides

NASA Technical Reports Server (NTRS)

Brainard, W. A.; Wheeler, D. R.

1978-01-01

The friction and wear properties of several refractory compound coatings were examined. These compounds were applied to 440 C bearing steel surfaces by radiofrequency (RF) sputtering. The refractory compounds were the titanium and molybdenum borides, the titanium and molybdenum silicides, and the titanium, molybdenum, and boron carbides. Friction testing was done with a pin-on-disk wear apparatus at loads from 0.1 to 5.0 newtons. Generally, the best wear properties were obtained when the coatings were bias sputtered onto 440 C disks that had been preoxidized. Adherence was improved because of the better bonding of the coatings to the iron oxide formed during preoxidation. As a class the carbides provided wear protection to the highest loads. Titanium boride coatings provided low friction and good wear properties to moderate loads.

Low temperature InP /Si wafer bonding using boride treated surface

NASA Astrophysics Data System (ADS)

Huang, Hui; Ren, Xiaomin; Wang, Wenjuan; Song, Hailan; Wang, Qi; Cai, Shiwei; Huang, Yongqing

2007-04-01

An approach for InP /Si wafer bonding based on boride-solution treatment was presented. The bonding energy is higher than the InP fracture energy by annealing at 280°C. An In0.53Ga0.47As/InP multiple-quantum-well (MQW) structure grown on InP was transferred onto Si substrate via the bonding process. X-ray diffraction and photoluminescence reveal that crystal quality of the bonded MQW was preserved. A thin B2O3-POx-SiO2 oxide layer of about 28nm thick at the bonding interface was detected. X-ray photoelectron spectroscopy and Raman analyses indicate that the formation of oxygen bridging bonds by boride treatment is responsible for the strong fusion obtained at such low temperature.

Method of boronizing transition metal surfaces

DOEpatents

Koyama, Koichiro; Shimotake, Hiroshi.

1983-08-16

A method is presented for preparing a boride layer on a transition metal substrate for use in corrosive environments or as a harden surface in machine applications. This method is particularly useful in treating current collectors for use within a high temperature and corrosive electrochemical cell environment. A melt of a alkali metal boride tetrafluoride salt including such as KF to lower its melting point is prepared including a dissolved boron containing material, for instance NiB, MnB[sub 2], or CrB[sub 2]. A transition metal to be coated is immersed in the melt at a temperature of no more than 700 C and a surface boride layer of that transition metal is formed within a period of about 24 hours on the substrate surface. 4 figs.

Tunable and mode-locked laser action of Cr4+ in codoped forsterite Cr, Sc:Mg2SiO4

NASA Astrophysics Data System (ADS)

Sanina, V. V.; Mitrokhin, V. P.; Subbotin, K. A.; Lis, D. A.; Lis, O. N.; Ivanov, A. A.; Zharikov, E. V.

2018-01-01

The laser oscillation of tetravalent chromium and scandium codoped forsterite Cr4+,Sc:Mg2SiO4 single crystal has been demonstrated for the first time for continuous wave, tunable and mode-locked regimes. For comparison, the laser experiments have also been performed in the same configuration with the reference forsterite single crystal solely doped by chromium. The aim of scandium codoping is to inhibit the formation of parasitic trivalent chromium in the crystal. The crystal with scandium demonstrates a wider tuning range, lower lasing threshold and wider mode-locked lasing spectrum than those of the reference crystal, although the total lasing efficiency achieved by both crystals is nearly the same. The obtained results are discussed.

Taguchi Analysis on the Effect of Process Parameters on Densification During Spark Plasma Sintering of HfB2-20SiC (Preprint)

DTIC Science & Technology

2011-11-01

30 kN pressure and heating rate of 100 K/min. Introduction Boride , carbides and nitrides of the group IVB and VB transition metals are considered...10. Sciti D., Silvestroni L., Nygren M. Spark plasma sintering of Zr- and Hf- borides with decreasing amounts of MoSi2 as sintering aid Journal of

Phase identification in boron-containing powder metallurgy steel using EBSD in combination with EPMA

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wu, Ming-Wei, E-mail: mwwu@ntut.edu.tw; Cai, Wen-Zhang

2016-03-15

Boron (B) is extensively used to induce liquid phase sintering (LPS) in powder metallurgy (PM) steels and thereby increase the densification. The alloying elements in B-containing PM steels affect the boride phase, stability of the boride, the temperature of liquid formation, and the progress of LPS. However, the boride phase has not been systematically identified yet. The main objective of this study was to clarify the influences of alloying elements, including C, Cr, and Ni, on the boride phases using electron backscatter diffraction (EBSD) in combination with electron probe microanalysis (EPMA). Network structures consisting of ferrite, Fe{sub 2}B boride, andmore » Fe{sub 3}C carbide were extensively observed in the Fe–0.4B–0.5C steel. The portions of Fe{sub 2}B were sufficiently larger than those of Fe{sub 3}C, and Fe{sub 3}C was mostly distributed at the interfaces between ferrite and Fe{sub 2}B. Adding 1.5 wt.% Cr or 1.8 wt.% Ni to Fe–0.4B–0.5C steel completely changes the Fe{sub 2}B and Fe{sub 3}C phases to a M{sub 3}(B,C) phase, where M represents the metallic elements, including Fe, Cr, Mo, and Ni. Furthermore, Cr, Mo, B, and C atoms tend to concentrate on the M{sub 3}(B,C) phase, but Ni atoms do not. - Highlights: • Network structures consisting of ferrite, Fe{sub 2}B boride, and Fe{sub 3}C carbide were extensively observed in the Fe–0.4B–0.5C steel. • Adding 1.5 wt.% Cr or 1.8 wt.% Ni to Fe–0.4B–0.5C steel completely transforms the Fe{sub 2}B and Fe{sub 3}C phases to a M{sub 3}(B,C) phase. • Cr, Mo, B, and C atoms tend to concentrate on the M{sub 3}(B,C) phase, but Ni atoms do not.« less

Ultrafast X-Ray Diffraction Studies of the Phase Transitions and Equation of State of Scandium Shock Compressed to 82 GPa

DOE PAGES

Briggs, R.; Gorman, M. G.; Coleman, A. L.; ...

2017-01-09

Using x-ray diffraction at the Linac Coherent Light Source x-ray free-electron laser, we have determined simultaneously and self-consistently the phase transitions and equation of state (EOS) of the lightest transition metal, scandium, under shock compression. On compression scandium undergoes a structural phase transition between 32 and 35 GPa to the same bcc structure seen at high temperatures at ambient pressures, and then a further transition at 46 GPa to the incommensurate host-guest polymorph found above 21 GPa in static compression at room temperature. Furthermore, shock melting of the host-guest phase is observed between 53 and 72 GPa with the disappearancemore » of Bragg scattering and the growth of a broad asymmetric diffraction peak from the high-density liquid.« less

Ultrafast X-Ray Diffraction Studies of the Phase Transitions and Equation of State of Scandium Shock Compressed to 82 GPa.

PubMed

Briggs, R; Gorman, M G; Coleman, A L; McWilliams, R S; McBride, E E; McGonegle, D; Wark, J S; Peacock, L; Rothman, S; Macleod, S G; Bolme, C A; Gleason, A E; Collins, G W; Eggert, J H; Fratanduono, D E; Smith, R F; Galtier, E; Granados, E; Lee, H J; Nagler, B; Nam, I; Xing, Z; McMahon, M I

2017-01-13

Using x-ray diffraction at the Linac Coherent Light Source x-ray free-electron laser, we have determined simultaneously and self-consistently the phase transitions and equation of state (EOS) of the lightest transition metal, scandium, under shock compression. On compression scandium undergoes a structural phase transition between 32 and 35 GPa to the same bcc structure seen at high temperatures at ambient pressures, and then a further transition at 46 GPa to the incommensurate host-guest polymorph found above 21 GPa in static compression at room temperature. Shock melting of the host-guest phase is observed between 53 and 72 GPa with the disappearance of Bragg scattering and the growth of a broad asymmetric diffraction peak from the high-density liquid.

The interactions between the sterically demanding trimesitylphosphine oxide and trimesityphosphine with scandium and selected lanthanide ions

NASA Astrophysics Data System (ADS)

Platt, Andrew W. G.; Singh, Kuldip

2016-05-01

The reactions between lanthanide nitrates, Ln(NO3)3 and scandium and lanthanide trifluoromethane sulfonates, Ln(Tf)3 with trimesitylphosphine oxide, Mes3PO show that coordination to the metal ions does not lead to crystalline complexes. Investigation of the reactions by 31-P NMR spectroscopy shows that weak complexes are formed in solution. The crystal structures of Mes3PO·0.5CH3CN (1) and [Mes3PO]3H3O·2CH3CN·Tf (2), formed in the reaction between ScTf3 and Mes3PO, are reported. Trimesitylphosphine, Mes3P, is protonated by scandium and lanthanide trifluoromethane sulfonates and lanthanide nitrates in CD3CN and the structure of [Mes3PH]Cl·HCl·2H2O (3) is reported.

Multifunctional Ceramic Nanostructured Coatings

DTIC Science & Technology

2010-12-01

silicon carbide composites // J. Europ. Cer. Soc. − 2004. − Vol. 24. − P. 2169−2179. 22. Yu. P. Udalov, E. E. Valova, S. S. Ordanian. Fabrication and...by the titanium and tungsten borides and carbides . The analysis was done using the X-ray and electron-optical methods. This information expands our...coating compositions should be based on limited solubility materials. Such systems include carbides , nitrides, borides and silicides based on

Structure of superhard tungsten tetraboride: A missing link between MB2 and MB12 higher borides

PubMed Central

Lech, Andrew T.; Turner, Christopher L.; Mohammadi, Reza; Tolbert, Sarah H.; Kaner, Richard B.

2015-01-01

Superhard metals are of interest as possible replacements with enhanced properties over the metal carbides commonly used in cutting, drilling, and wear-resistant tooling. Of the superhard metals, the highest boride of tungsten—often referred to as WB4 and sometimes as W1–xB3—is one of the most promising candidates. The structure of this boride, however, has never been fully resolved, despite the fact that it was discovered in 1961—a fact that severely limits our understanding of its structure–property relationships and has generated increasing controversy in the literature. Here, we present a new crystallographic model of this compound based on refinement against time-of-flight neutron diffraction data. Contrary to previous X-ray–only structural refinements, there is strong evidence for the presence of interstitial arrangements of boron atoms and polyhedral bonding. The formation of these polyhedra—slightly distorted boron cuboctahedra—appears to be dependent upon the defective nature of the tungsten-deficient metal sublattice. This previously unidentified structure type has an intermediary relationship between MB2 and MB12 type boride polymorphs. Manipulation of the fractionally occupied metal and boron sites may provide insight for the rational design of new superhard metals. PMID:25733870

Analysis of boron carbides' electronic structure

NASA Technical Reports Server (NTRS)

Howard, Iris A.; Beckel, Charles L.

1986-01-01

The electronic properties of boron-rich icosahedral clusters were studied as a means of understanding the electronic structure of the icosahedral borides such as boron carbide. A lower bound was estimated on bipolaron formation energies in B12 and B11C icosahedra, and the associated distortions. While the magnitude of the distortion associated with bipolaron formation is similar in both cases, the calculated formation energies differ greatly, formation being much more favorable on B11C icosahedra. The stable positions of a divalent atom relative to an icosahedral borane was also investigated, with the result that a stable energy minimum was found when the atom is at the center of the borane, internal to the B12 cage. If incorporation of dopant atoms into B12 cages in icosahedral boride solids is feasible, novel materials might result. In addition, the normal modes of a B12H12 cluster, of the C2B10 cage in para-carborane, and of a B12 icosahedron of reduced (D sub 3d) symmetry, such as is found in the icosahedral borides, were calculated. The nature of these vibrational modes will be important in determining, for instance, the character of the electron-lattice coupling in the borides, and in analyzing the lattice contribution to the thermal conductivity.

Electrochemical Corrosion Behavior of Spray-Formed Boron-Modified Supermartensitic Stainless Steel

NASA Astrophysics Data System (ADS)

Zepon, Guilherme; Nogueira, Ricardo P.; Kiminami, Claudio S.; Botta, Walter J.; Bolfarini, Claudemiro

2017-04-01

Spray-formed boron-modified supermartensitic stainless steel (SMSS) grades are alloys developed to withstand severe wear conditions. The addition of boron to the conventional chemical composition of SMSS, combined with the solidification features promoted by the spray forming process, leads to a microstructure composed of low carbon martensitic matrix reinforced by an eutectic network of M2B-type borides, which considerably increases the wear resistance of the stainless steel. Although the presence of borides in the microstructure has a very beneficial effect on the wear properties of the alloy, their effect on the corrosion resistance of the stainless steel was not comprehensively evaluated. The present work presents a study of the effect of boron addition on the corrosion resistance of the spray-formed boron-modified SMSS grades by means of electrochemical techniques. The borides fraction seems to have some influence on the repassivation kinetics of the spray-formed boron-modified SMSS. It was shown that the Cr content of the martensitic matrix is the microstructural feature deciding the corrosion resistance of this sort of alloys. Therefore, if the Cr content in the alloy is increased to around 14 wt pct to compensate for the boron consumed by the borides formation, the corrosion resistance of the alloy is kept at the same level of the alloy without boron addition.

Miniature High Density Scandate Cathodes for Linear Beam Devices

DTIC Science & Technology

2008-07-14

oxalic acid is added and nanoparticles of scandia precipitate out. We were successful with this process. 2.3 Experimental Method Measurement...process. The scandium oxide doped porous matrix is subsequently impregnated in the molten phase with 4:1:1 barium calcium aluminates to form the...scandium nitrate dissolved in pure alcohol using oxalic acid dehydrate as the precipitant. E-beam has successfully used this process to produce a

A Crossover from High Stiffness to High Hardness: The Case of Osmium and Its Borides

NASA Astrophysics Data System (ADS)

Bian, Yongming; Liu, Xiaomei; Li, Anhu; Liang, Yongcheng

2016-09-01

Transition-metal light-element compounds are currently raising great expectations for hard and superhard materials. Using the widely attracting osmium (Os) and its borides (OsB, Os2B3 and OsB2) as prototypes, we demonstrate by first-principles calculations that heavy transition metals, which possess high stiffness but low hardness, can be converted into highly hard materials by incorporating of light elements to form compounds. Such a crossover is a manifestation that the underlying sources of high stiffness and high hardness are fundamentally different. The stiffness is related to elastic deformation that is closely associated with valence electron density, whereas the hardness depends strongly on plastic deformation that is determined by bonding nature. Therefore, the incorporation of light atoms into transition metal should be a valid pathway of designing hard and superhard materials. This strategy is in principle also applicable to other transition-metal borides, carbides, and nitrides.

Investigation of the structure and properties of boron-containing coatings obtained by electron-beam treatment

DOE Office of Scientific and Technical Information (OSTI.GOV)

Krivezhenko, Dina S., E-mail: dinylkaa@yandex.ru; Drobyaz, Ekaterina A., E-mail: ekaterina.drobyaz@yandex.ru; Bataev, Ivan A., E-mail: ivanbataev@ngs.ru

2015-10-27

An investigation of surface-hardened materials obtained by cladding with an electron beam injected into the air atmosphere was carried out. Structural investigations of coatings revealed that an increase in boron carbide concentration in a saturating mixture contributed to a rise of a volume fraction of iron borides in coatings. The maximum hardened depth reached 2 mm. Hardened layers were characterized by the formation of heterogeneous structure which consisted of iron borides and titanium carbides distributed uniformly in the eutectic matrix. Areas of titanium boride conglomerations were detected. It was found that an increase in the boron carbide content led to anmore » enhancement in hardness of the investigated materials. Friction testing against loosely fixed abrasive particles showed that electron-beam cladding of powder mixtures containing boron carbides, titanium, and iron in air atmosphere allowed enhancing a resistance of materials hardened in two times.« less

Thermodynamical and thermoelectric properties of boron doped YPd{sub 3} and YRh{sub 3}

DOE Office of Scientific and Technical Information (OSTI.GOV)

Dwivedi, Shalini; Sharma, Yamini, E-mail: sharma.yamini62@gmail.com; Sharma, Ramesh

2016-05-23

The structural, electronic, thermal, and optical properties of borides of cubic non-magnetic YX{sub 3} (X=Rh, Pd) compounds and their borides which crystallize in the AuCu{sub 3} structure have been studied using the density functional theory (DFT). The flat bands in the vicinity of E{sub F} which are associated with superconductivity appear in YPd{sub 3} and YRh{sub 3} band structures. However, the B s-states enhance the flat band only in YRh{sub 3}B. The optical properties clearly show that boron insertion modifies the absorption and transmittance. The YX{sub 3} alloys and their borides exhibit valuable changes in the thermopower and ZT. Itmore » is observed that the properties of the Y-X intermetallics change significantly for the Y-Rh and Y-Pd alloys and the presence of single boron atom modifies the properties to a great extent.« less

Magnetization Analysis of Magnesium Boride Wires

NASA Astrophysics Data System (ADS)

Cave, J. R.; Zhu, W.

2006-03-01

Cycled applied field magnetization curves contain a wealth of information on critical current density and flux pinning that is not commonly exploited. Detailed magnetization data for magnesium boride wire cores have been analyzed for critical state model consistency. The iron-sheathed silicon nitride doped magnesium boride wires were prepared from pure magnesium and boron powders with nano-scale silicon nitride additions (MgB2-x(Si3N4)x/7 with x = 0 - 0.4). A subsequent short annealing heat treatment, 800 degrees C and of 1 hour duration in Argon, was applied to create the desired phase. Magnetization critical current densities were up to ˜340 kA/cm2 at 5K and 1T. Major and minor loop analysis will be described, for field sweeps up to 3 tesla at fixed temperatures and for temperature sweeps from 5K to 45K in fixed fields, with respect to parameters describing the critical state model.

Investigation of the structure and properties of boron-containing coatings obtained by electron-beam treatment

NASA Astrophysics Data System (ADS)

Krivezhenko, Dina S.; Drobyaz, Ekaterina A.; Bataev, Ivan A.; Chuchkova, Lyubov V.

2015-10-01

An investigation of surface-hardened materials obtained by cladding with an electron beam injected into the air atmosphere was carried out. Structural investigations of coatings revealed that an increase in boron carbide concentration in a saturating mixture contributed to a rise of a volume fraction of iron borides in coatings. The maximum hardened depth reached 2 mm. Hardened layers were characterized by the formation of heterogeneous structure which consisted of iron borides and titanium carbides distributed uniformly in the eutectic matrix. Areas of titanium boride conglomerations were detected. It was found that an increase in the boron carbide content led to an enhancement in hardness of the investigated materials. Friction testing against loosely fixed abrasive particles showed that electron-beam cladding of powder mixtures containing boron carbides, titanium, and iron in air atmosphere allowed enhancing a resistance of materials hardened in two times.

Rare earths, the lanthanides, yttrium and scandium

USGS Publications Warehouse

Bedinger, G.; Bleiwas, D.

2012-01-01

In 2011, rare earths were recovered from bastnasite concentrates at the Mountain Pass Mine in California. Consumption of refined rare-earth products decreased in 2011 from 2010. U.S. rare-earth imports originated primarily from China, with lesser amounts from Austria, Estonia, France and Japan. The United States imported all of its demand for yttrium metal and yttrium compounds, with most of it originating from China. Scandium was imported in various forms and processed domestically.

Synthesis, structures, and electroluminescent properties of scandium N,O-chelated complexes toward near-white organic light-emitting diodes.

PubMed

Katkova, Marina A; Balashova, Tatyana V; Ilichev, Vasilii A; Konev, Alexey N; Isachenkov, Nikolai A; Fukin, Georgy K; Ketkov, Sergey Yu; Bochkarev, Mikhail N

2010-06-07

Three members of a new class of electroluminescent, neutral, and monomeric scandium N,O-chelate complexes, namely, Sc(III)-tris-2-(2-benzoimidazol-2-yl)phenolate (1), Sc(III)-tris-2-(2-benzoxyazol-2-yl)phenolate (2), and Sc(III)-tris-2-(2-benzothiazol-2-yl)phenolate (3), have been prepared and X-ray characterized. DFT calculations have been performed. In contrast to the most frequently applied dual or multiple dopants in multilayer white OLED devices, all our simpler devices with the configuration of indium tin oxide/N,N'-bis(3-methylphenyl)-N,N'-diphenylbenzidine/neat scandium complex/Yb exhibit close to near-white emission with a blue hue (CIE(x,y) = 0.2147, 0.2379) in the case of 1, a cyan hue (0.2702, 0.3524) in the case of 2, and a yellowish hue (0.3468; 0.4284) in the case of 3.

Removal of acidic or basic α-amino acids in water by poorly water soluble scandium complexes.

PubMed

Hayashi, Nobuyuki; Jin, Shigeki; Ujihara, Tomomi

2012-11-02

To recognize α-amino acids with highly polar side chains in water, poorly water soluble scandium complexes with both Lewis acidic and basic portions were synthesized as artificial receptors. A suspension of some of these receptor molecules in an α-amino acid solution could remove acidic and basic α-amino acids from the solution. The compound most efficient at preferentially removing basic α-amino acids (arginine, histidine, and lysine) was the receptor with 7,7'-[1,3-phenylenebis(carbonylimino)]bis(2-naphthalenesulfonate) as the ligand. The neutral α-amino acids were barely removed by these receptors. Removal experiments using a mixed amino acid solution generally gave results similar to those obtained using solutions containing a single amino acid. The results demonstrated that the scandium complex receptors were useful for binding acidic and basic α-amino acids.

Surface studies on scandate cathodes and synthesized scandates

NASA Technical Reports Server (NTRS)

Lesny, Gary; Forman, Ralph

1990-01-01

Auger, ESCA, electron emission, evaporation, and desorption measurements were made on three different types of scandate surfaces. They are: (1) an impregnated top layer scandate cathode, (2) an unimpregnated top layer scandate cathode with a deposited barium or barium oxide adsorbate surface layer, and (3) a synthesized scandate surface, which replicates a scandate cathode surface. The purpose of these experiments was to determine the role that Sc2O3 plays in making the scandate cathode a more copious electron emitter than the conventional impregnated-type cathode. The synthesized scandate surface experiments consisted of depositing multilayer scandium on a tungsten surface, oxidizing the scandium, and then depositing either Ba or BaO on the scandium oxide surface. The results of these measurements showed that the low work function portions of the thin-film scandate cathode are where the Sc2O3 is the substrate and BaO is the adsorbate.

Current German Laser and Quantum Optics Research Reviewed at the 50th Annual Meeting of the Physikalische Gesellschaft.

DTIC Science & Technology

1986-04-23

Physics, Munster In the area of generating useable University) studied an interesting de- coherent high-frequency radiation, I vice, a silicon Fabry ...has a substantial crys- tingen) described studies with Cr- plus tal growing capability. One paper from Nd-doped gadolinium -scandium-gallium the Hamburg...institute, read by J. Drube, garnets (GSGG), and also with Cr-doped reported on Xe-flashlamp-pumped Cr:CSA(; % gadolinium -scandium-aluminum garnets

Crystallography, Spectroscopic Analysis, and Lasing Properties of Nd(3+) :Y3Sc2Al3O12

DTIC Science & Technology

1989-12-01

aluminum garnet (GSAG), are formed from more stable constitu- ent oxides than gallium-containing materials, 2. Experimental Results and such as gadolinium ...the which an assessment can be made regarding aluminum -based systems, such as YAG, YSAG, Nd:YSAG as a laser material. or gadolinium scandium...Structure oxidation state variation or oxygen vacancies, and this problem is greatly reduced in alumi- Yttrium scandium aluminum garnet be- nate systems

Enhancing Magnetic Functionality with Scandium: Breaking Stereotypes in the Design of Rare Earth Materials

DOE PAGES

Mudryk, Yaroslav; Paudyal, Durga; Liu, Jing; ...

2017-04-11

Replacement of strongly magnetic gadolinium with weakly magnetic scandium unexpectedly enhances ferromagnetic interactions in (Gd 1–xSc x) 5Ge 4. Based upon this counterintuitive experimental finding we demonstrate the unique role 3d 1 electrons of scandium atoms play in mediating magnetic interactions between the gadolinium atoms from the neighboring layers in the Sm 5Ge 4-type crystal lattice. Scandium substitutions at and below 20% rapidly increase the Curie temperature, TC, of the Gd 5Ge 4 parent, eliminate both the kinetic arrest and hysteresis, and drastically improve reversibility of the first-order magnetostructural transformation at T C. In agreement with first-principles predictions, higher thanmore » 20% Sc leads to the formation of a closely related Pu 5Rh 4-type structure where the first-order magnetostructural transformation is replaced by a conventional second-order ferromagnetic ordering that remains accompanied by a continuous rearrangement of the crystal lattice. In conclusion, comparison of two materials with similar structures and compositions shows that significantly stronger magnetocaloric effect occurs in the first-order material, which also shows very small hysteresis. Furthermore, we demonstrate that a behavior of a specific interatomic distance can predict anomalous physical properties in a series of alloys where compositional dependence of lattice parameters suggests a rather trivial solid solubility and uninteresting magnetism.« less

Crystal structures and compressibility of novel iron borides Fe{sub 2}B{sub 7} and Fe{sub x}B{sub 50} synthesized at high pressure and high temperature

DOE Office of Scientific and Technical Information (OSTI.GOV)

Bykova, E., E-mail: elena.bykova@uni-bayreuth.de; Laboratory of Crystallography, University of Bayreuth, D-95440 Bayreuth; Gou, H.

2015-10-15

We present here a detailed description of the crystal structures of novel iron borides, Fe{sub 2}B{sub 7} and Fe{sub x}B{sub 50} with various iron content (x=1.01(1), 1.04(1), 1.32(1)), synthesized at high pressures and high temperatures. As revealed by high-pressure single-crystal X-ray diffraction, the structure of Fe{sub 2}B{sub 7} possesses short incompressible B–B bonds, which make it as stiff as diamond in one crystallographic direction. The volume compressibility of Fe{sub 2}B{sub 7} (the bulk modulus K{sub 0}= 259(1.8) GPa, K{sub 0}′= 4 (fixed)) is even lower than that of FeB{sub 4} and comparable with that of MnB{sub 4}, known for highmore » bulk moduli among 3d metal borides. Fe{sub x}B{sub 50} adopts the structure of the tetragonal δ-B, in which Fe atoms occupy an interstitial position. Fe{sub x}B{sub 50} does not show considerable anisotropy in the elastic behavior. - Graphical abstract: Crystal structures of novel iron borides, Fe{sub 2}B{sub 7} and Fe{sub x}B{sub 50} (x=1.01(1), 1.04(1), 1.32(1)). - Highlights: • Novel iron borides, Fe{sub 2}B{sub 7} and Fe{sub x}B{sub 50}, were synthesized under HPHT conditions. • Fe{sub 2}B{sub 7} has a unique orthorhombic structure (space group Pbam). • Fe{sub 2}B{sub 7} possesses short incompressible B–B bonds that results in high bulk modulus. • Fe{sub x}B{sub 50} adopts the structure of the tetragonal δ-B composed of B{sub 12} icosahedra. • In Fe{sub x}B{sub 50} intraicosahedral bonds are stiffer than intericosahedral ones.« less

The effect of melt refining upon inclusions in aluminum

NASA Astrophysics Data System (ADS)

Simensen, C. J.

1982-03-01

A series of aluminum melts has been refined with respect to inclusions by use of ALCOA 469, FILD, or SNIF. The content and size distribution of inclusions in the original-and the refined melts-have been measured by use of neutron activation (oxygen content), gas chromatography (carbide content), sedimentation analysis, and dissolution of metal in hydrochloric acid and subsequent analysis of oxides by means of a Coulter Counter. All the units tested have a beneficial effect and decrease the inclusion content, but the number of analyses are too few to make general conclusions. However, for melts cleaned by use of SNIF, it was found that oxides larger than 50 μm in cross section and borides larger than 20 μm in diameter were removed, while the smaller borides were agglomerated only. The effect of FILD and ALCOA 469 upon the melt tested was removal of borides larger than 5-10 μ m and oxides larger than 15μm in diameter, respectively.

Interfacial reactions in borsic/Ti-3Al-2-1/2V composite

NASA Technical Reports Server (NTRS)

Rao, V. B.; Houska, C. R.; Unnam, J.; Brewer, W. D.; Tenney, D. R.

1979-01-01

The paper provides a detailed X-ray characterization of a borsic/Ti-3Al-2-1/2V composite, and to correlate the relative intensities of the reaction products with the mechanical properties. Based on X-ray integrated intensity data two stages of interface reactions were identified: during the first stage there is a simultaneous interdiffusion of Si, C, and Ti atoms at the filament/matrix interface resulting in the formation of Ti5Si3, TiSi and small amounts of TiSi2 and TiC. The second stage is associated with considerable TiSi2 and boride formation. It appears that the alpha-phase of Ti is more reactive in forming silicides and borides than the beta-phase. The silicide intensities and the reaction zone thicknesses are shown to be directly related to the reduction of the ultimate tensile strength by thermal degradation, and the results indicate that silicide reaction products are as detrimental to strength as the borides.

A Simple Kinetic Model for the Growth of Fe2B Layers on AISI 1026 Steel During the Powder-pack Boriding

NASA Astrophysics Data System (ADS)

Flores-Rentería, M. A.; Ortiz-Domínguez, M.; Keddam, M.; Damián-Mejía, O.; Elias-Espinosa, M.; Flores-González, M. A.; Medina-Moreno, S. A.; Cruz-Avilés, A.; Villanueva-Ibañez, M.

2015-02-01

This work focused on the determination of boron diffusion coefficient through the Fe2B layers on AISI 1026 steel using a mathematical model. The suggested model solves the mass balance equation at the (Fe2B/substrate) interface. This thermochemical treatment was carried out in the temperature range of 1123-1273 K for a treatment time ranging from 2 to 8 h. The generated boride layers were characterized by different experimental techniques such as light optical microscopy, scanning electron microscopy, XRD analysis and the Daimler-Benz Rockwell-C indentation technique. As a result, the boron activation energy for AISI 1026 steel was estimated as 178.4 kJ/mol. Furthermore, this kinetic model was validated by comparing the experimental Fe2B layer thickness with the predicted one at a temperature of 1253 K for 5 h of treatment. A contour diagram relating the layer thickness to the boriding parameters was proposed to be used in practical applications.

Amorphous nickel boride membrane on a platinum-nickel alloy surface for enhanced oxygen reduction reaction.

PubMed

He, Daping; Zhang, Libo; He, Dongsheng; Zhou, Gang; Lin, Yue; Deng, Zhaoxiang; Hong, Xun; Wu, Yuen; Chen, Chen; Li, Yadong

2016-08-09

The low activity of the oxygen reduction reaction in polymer electrolyte membrane fuel cells is a major barrier for electrocatalysis, and hence needs to be optimized. Tuning the surface electronic structure of platinum-based bimetallic alloys, a promising oxygen reduction reaction catalyst, plays a key role in controlling its interaction with reactants, and thus affects the efficiency. Here we report that a dealloying process can be utilized to experimentally fabricate the interface between dealloyed platinum-nickel alloy and amorphous nickel boride membrane. The coating membrane works as an electron acceptor to tune the surface electronic structure of the platinum-nickel catalyst, and this composite catalyst composed of crystalline platinum-nickel covered by amorphous nickel boride achieves a 27-times enhancement in mass activity relative to commercial platinum/carbon at 0.9 V for the oxygen reduction reaction performance. Moreover, this interactional effect between a crystalline surface and amorphous membrane can be readily generalized to facilitate the 3-times higher catalytic activity of commercial platinum/carbon.

Influence of heat treatment on microstructure and hot crack susceptibility of laser-drilled turbine blades made from Rene 80

DOE Office of Scientific and Technical Information (OSTI.GOV)

Osterle, W.; Krause, S.; Moelders, T.

2008-11-15

Turbine components from conventionally cast nickel-base alloy Rene 80 show different hot cracking susceptibilities depending on their heat treatment conditions leading to slightly different microstructures. Electron probe micro-analysis, focused ion beam technique and analytical transmission electron microscopy were applied to reveal and identify grain boundary precipitates and the {gamma}-{gamma}'-microstructure. The distribution of borides along grain boundaries was evaluated statistically by quantitative metallography. The following features could be correlated with an increase of cracking susceptibility: i) Increasing grain size, ii) increasing fraction of grain boundaries with densely spaced borides, iii) lack of secondary {gamma}'-particles in matrix channels between the coarse cuboidalmore » {gamma}'-precipitates. The latter feature seems to be responsible for linking-up of cracked grain boundary precipitates which occurred as an additional cracking mechanism after one heat treatment, whereas decohesion at the boride-matrix-interface in the heat affected zone of laser-drilled holes was observed for both heat treatments.« less

Method of making an icosahedral boride structure

DOEpatents

Hersee, Stephen D.; Wang, Ronghua; Zubia, David; Aselage, Terrance L.; Emin, David

2005-01-11

A method for fabricating thin films of an icosahedral boride on a silicon carbide (SiC) substrate is provided. Preferably the icosahedral boride layer is comprised of either boron phosphide (B.sub.12 P.sub.2) or boron arsenide (B.sub.12 As.sub.2). The provided method achieves improved film crystallinity and lowered impurity concentrations. In one aspect, an epitaxially grown layer of B.sub.12 P.sub.2 with a base layer or substrate of SiC is provided. In another aspect, an epitaxially grown layer of B.sub.12 As.sub.2 with a base layer or substrate of SiC is provided. In yet another aspect, thin films of B.sub.12 P.sub.2 or B.sub.12 As.sub.2 are formed on SiC using CVD or other vapor deposition means. If CVD techniques are employed, preferably the deposition temperature is above 1050.degree. C., more preferably in the range of 1100.degree. C. to 1400.degree. C., and still more preferably approximately 1150.degree. C.

Microstructure and mechanical properties of Ni and Fe-base boride-dispersion-strengthened microcrystalline alloys

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wade, C.S.; Park, H.G.; Hoagland, R.G.

This paper considers the relation between microstructure and mechanical properties of two Ni-base and two Fe-base Boride-Dispersion-Strengthened Microcrystalline (BDSM) alloys. In these very fine grained materials the borides were primarily Cr, Mo, and MoFe in a fcc matrix in three of the alloys, and a bcc in one of the Fe-base alloys. Strength data and resistance to stress corrosion cracking are reported and, in the latter case, extraordinary resistance to SCC in NaCl, Na{sub 2}S{sub 2}O{sub 3} and boiling MgCl{sub 2} environments was observed in every case. The fcc BDSM alloys also demonstrated excellent thermal stability in terms of strengthmore » and fracture roughness up to 1000 C. The bcc alloy suffered severe loss of toughness. The fracture mode involved ductile rupture in all alloys and they display a reasonably linear correlation between K{sub Ic} and the square root of particle spacing.« less

Magnetic properties and magnetic hardening mechansim of Pt-Co-B alloys

NASA Technical Reports Server (NTRS)

Qiu, Ning; Flanagan, F.; Wittig, James E.

1994-01-01

The intrinsic coercivity is found to be maximized in the Pt42Co45B13 ternary alloy which is undercooled and rapidly solidified (quenched using a 70 m/s wheel speed after undercooling), and then annealed (800 C for 2400 min). The same alloy, processed at slower cooling rates and annealed in the same way, has a much larger scale microstructure and a much lower resulting magnetic coercivity. The microstructure which would optimize the coercitvity of this coercivity of this ternary alloy is a completely ordered L1(sub zero) Pt-Co matrix with a submicron magnetic single-domion Co-boride precipitate. The L1(sub zero) phase is highly anistropic magnetically while the Co-boride precipate is somewhat less so. Annealing treatments designed to produced single-domain Co-boride precipitates enhance the coercivity. This suggests that the refined microstructures is responsible for the high coercivities found in the rapidly solidified and annealed alloy. The magnetic domain wall thickness for a Co-boride precipitate is determined from both experimental observation and theoretical calculation in order to evaluate its influence on the coercivity of the alloy. The effects of the pinning of domain walls and the barrier to the nucleation of reverse domains on the coercivity are discussed. Both microstrucutral analysis and theoretical calculation indicate that the high coercivities in the Pt42Co45B13 alloy are due to the difficult nucleation of reverse magnetic domains.

Electroplating of the superconductive boride MgB2 from molten salts

NASA Astrophysics Data System (ADS)

Abe, Hideki; Yoshii, Kenji; Nishida, Kenji; Imai, Motoharu; Kitazawa, Hideaki

2005-02-01

An electroplating technique of the superconductive boride MgB2 onto graphite substrates is reported. Films of MgB2 with a thickness of tens micrometer were fabricated on the planar and curved surfaces of graphite substrates by means of electrolysis on a mixture of magnesium chloride, potassium chloride, sodium chloride, and magnesium borate fused at 600 °C under an Ar atmosphere. The electrical resistivity and magnetization measurements revealed that the electroplated MgB2 films undergo a superconducting transition with the critical temperature (Tc) of 36 K.

Fine structure of the K X-ray absorption spectra of titanium in some hydrides, borides, and silicides (in Russian)

DOE Office of Scientific and Technical Information (OSTI.GOV)

Vainshtein, �. E.; Zhurakovskii, E. A.

1959-08-01

X-ray spectral analyses confirmed the hypothesis on the metal-like state of hydrogen in tithnium hydrides. Experiments with titunium borides and silicides indicate the special character and degree of the 3d--level participation in the metallic'' bond between the atoms of various complexes. The structure of metalloid elements becomes more complicated with an increase in the specific number of boron and silicon atoms and the bond between the atoms tends to become covalent. (R.V.J.)

History of ``NANO''-Scale VERY EARLY Solid-State (and Liquid-State) Physics/Chemistry/Metallurgy/ Ceramics; Interstitial-Alloys Carbides/Nitrides/Borides/...Powders and Cermets, Rock Shocks, ...

NASA Astrophysics Data System (ADS)

Maiden, Colin; Siegel, Edward

History of ``NANO'': Siegel-Matsubara-Vest-Gregson[Mtls. Sci. and Eng. 8, 6, 323(`71); Physica Status Solidi (a)11,45(`72)] VERY EARLY carbides/nitrides/borides powders/cermets solid-state physics/chemistry/metallurgy/ ceramics FIRST-EVER EXPERIMENTAL NANO-physics/chemistry[1968 ->Physica Status Solidi (a)11,45(`72); and EARLY NANO-``physics''/NANO-``chemistry'' THEORY(after: Kubo(`62)-Matsubara(`60s-`70s)-Fulde (`65) [ref.: Sugano[Microcluster-Physics, Springer('82 `98)

A crystalline anionic complex of scandium nitride endometallofullerene: experimental observation of single-bonded (Sc3N@Ih-C80−)2 dimers†

PubMed Central

Konarev, Dmitri V.; Zorina, Leokadiya V.; Khasanov, Salavat S.; Popov, Alexey A.; Otsuka, Akihiro; Yamochi, Hideki; Saito, Gunzi; Lyubovskaya, Rimma N.

2017-01-01

Reduction of scandium nitride clusterfullerene, Sc3N@Ih-C80, by sodium fluorenone ketyl in the presence of cryptand[2,2,2] allows the crystallization of the {cryptand[2,2,2](Na+)}2(Sc3N@Ih-C80−)2·2.5C6H4Cl2 (1) salt. The Sc3N@Ih-C80•− radical anions are dimerized to form single-bonded (Sc3N@Ih-C80−)2 dimers. PMID:27511304

Rare-Earth Ion-Host Lattice Interactions: 15. Analysis of the Spectra of Nd3+ in Gd3Sc2Ga3O12.

DTIC Science & Technology

1984-05-01

Luminescence of Cr3+ Ions in Gadolinium Gallium and Gadolinium Scandium Gallium Garnet CT’stals, Soy. J. Quant. Electron. 12 (1982), 1124. 6M. Dutoit, J. C...Shcherbakov, Absolute Quantum Efficiency of the Luminescence of Cr3+ Ions in Gadolinium Gallium and Gadolinium Scandium Gallium Garnet Crystals, Soy. J...HDL Project: 324332 19. KEY WORDS (Continue on reverse side it necessary end Identify by block number) Rare earth Mixed garnet Spectra Laser Judd-Ofelt

On the Possibility of using Alluminium-Magnesium Alloys with Improved Mechanical Characteristics for Body Elements of Zenit-2S Launch Vehicle Propellant Tanks

NASA Astrophysics Data System (ADS)

Sitalo, V.; Lytvyshko, T.

2002-01-01

Yuzhnoye SDO developed several generations of launch vehicles and spacecraft that are characterized by weight perfection, optimal cost, accuracy of output geometrical characteristics, stable strength characteristics, high tightness. The main structural material of launch vehicles are thermally welded non-strengthened aluminium- magnesium alloys. The aluminium-magnesium alloys in the annealed state have insufficiently high strength characteristics. Considerable increase of yield strength of sheets and plates can be reached by cold working but in this case, plasticity reduces. An effective way to improve strength of aluminium-magnesium alloys is their alloying with scandium. The alloying with scandium leads to modification of the structure of ingots (size reduction of cast grain) and formation of supersaturated solid solutions of scandium and aluminium during crystallization. During subsequent heatings (annealing of the ingots, heating for deformation) the solid solution disintegrates with the formation of disperse particles of Al3Sc type, that cause great strengthening of the alloy. High degree of dispersion and density of distribution in the matrix of secondary Al3Sc particles contribute to the considerable increase of the temperature of recrystallization of deformed intermediate products and to the formation of stable non-recrystallized structure. The alloying of alluminium-magnesium alloys with scandium increases their strength and operational characteristics, preserves their technological and corrosion properties, improves weldability. The alloys can be used within the temperature limits ­196-/+150 0C. The experimental structures of propellant tanks made of alluminium-magnesium alloys with scandium have been manufactured and tested. It was ascertained that the propellant tanks have higher margin of safety during loading with internal pressure and higher stability factor of the shrouds during loading with axial compression force which is caused by higher value of yield strength. The analysis of the performed work showed good prospects of using the alluminium-magnesium alloys with increased mechanical characteristics for making body elements of propellant tanks of the Zenit -2S launch vehicles. The use of these alloys can give the increase of structural strength by 20-30% and considerable increase of payload weight.

Synthesis and Characterization of Low-Cost Superhard Transition-Metal Borides

NASA Astrophysics Data System (ADS)

Kaner, Richard

2013-06-01

The increasing demand for high-performance cutting and forming tools, along with the shortcomings of traditional tool materials such as diamond (unable to cut ferrous materials), cubic boron nitride (expensive) and tungsten carbide (relatively-low hardness), has motivated the search for new superhard materials for these applications. This has led us to a new class of superhard materials, dense refractory transition-metal borides, which promise to address some of the existing problems of conventional superhard materials. For example, we have synthesized rhenium diboride (ReB2) using arc melting at ambient pressure. This superhard material has demonstrated an excellent electrical conductivity and superior mechanical properties, including a Vickers hardness of 48.0 GPa (under an applied load of 0.49 N). To further increase the hardness and lower the materials costs, we have begun exploring high boron content metal borides including tungsten tetraboride (WB4) . We have synthesized WB4 by arc melting and studied its hardness and high-pressure behavior. With a similar Vickers hardness (43.3 GPa under a load of 0.49 N) and bulk modulus (326-339 GPa) to ReB2, WB4 offers a lower cost alternative and has the potential to be used in cutting tools. To further enhance the hardness of this superhard metal, we have created the binary and ternary solid solutions of WB4 with Cr, Mn and Ta, the results of which show a hardness increase of up to 20 percent. As with other metals, these metallic borides can be readily cut and shaped using electric discharge machining (EDM).

Arctic Deep Water Ferromanganese-Oxide Deposits Reflect the Unique Characteristics of the Arctic Ocean

NASA Astrophysics Data System (ADS)

Hein, James R.; Konstantinova, Natalia; Mikesell, Mariah; Mizell, Kira; Fitzsimmons, Jessica N.; Lam, Phoebe J.; Jensen, Laramie T.; Xiang, Yang; Gartman, Amy; Cherkashov, Georgy; Hutchinson, Deborah R.; Till, Claire P.

2017-11-01

Little is known about marine mineral deposits in the Arctic Ocean, an ocean dominated by continental shelf and basins semi-closed to deep-water circulation. Here, we present data for ferromanganese crusts and nodules collected from the Amerasia Arctic Ocean in 2008, 2009, and 2012 (HLY0805, HLY0905, and HLY1202). We determined mineral and chemical compositions of the crusts and nodules and the onset of their formation. Water column samples from the GEOTRACES program were analyzed for dissolved and particulate scandium concentrations, an element uniquely enriched in these deposits. The Arctic crusts and nodules are characterized by unique mineral and chemical compositions with atypically high growth rates, detrital contents, Fe/Mn ratios, and low Si/Al ratios, compared to deposits found elsewhere. High detritus reflects erosion of submarine outcrops and North America and Siberia cratons, transport by rivers and glaciers to the sea, and distribution by sea ice, brines, and currents. Uniquely high Fe/Mn ratios are attributed to expansive continental shelves, where diagenetic cycling releases Fe to bottom waters, and density flows transport shelf bottom water to the open Arctic Ocean. Low Mn contents reflect the lack of a mid-water oxygen minimum zone that would act as a reservoir for dissolved Mn. The potential host phases and sources for elements with uniquely high contents are discussed with an emphasis on scandium. Scandium sorption onto Fe oxyhydroxides and Sc-rich detritus account for atypically high scandium contents. The opening of Fram Strait in the Miocene and ventilation of the deep basins initiated Fe-Mn crust growth ˜15 Myr ago.

Arctic deep-water ferromanganese-oxide deposits reflect the unique characteristics of the Arctic Ocean

USGS Publications Warehouse

Hein, James; Konstantinova, Natalia; Mikesell, Mariah; Mizell, Kira; Fitzsimmons, Jessica N.; Lam, Phoebe; Jensen, Laramie T.; Xiang, Yang; Gartman, Amy; Cherkashov, Georgy; Hutchinson, Deborah; Till, Claire P.

2017-01-01

Little is known about marine mineral deposits in the Arctic Ocean, an ocean dominated by continental shelf and basins semi-closed to deep-water circulation. Here, we present data for ferromanganese crusts and nodules collected from the Amerasia Arctic Ocean in 2008, 2009, and 2012 (HLY0805, HLY0905, HLY1202). We determined mineral and chemical compositions of the crusts and nodules and the onset of their formation. Water column samples from the GEOTRACES program were analyzed for dissolved and particulate scandium concentrations, an element uniquely enriched in these deposits.The Arctic crusts and nodules are characterized by unique mineral and chemical compositions with atypically high growth rates, detrital contents, Fe/Mn ratios, and low Si/Al ratios, compared to deposits found elsewhere. High detritus reflects erosion of submarine outcrops and North America and Siberia cratons, transport by rivers and glaciers to the sea, and distribution by sea ice, brines, and currents. Uniquely high Fe/Mn ratios are attributed to expansive continental shelves, where diagenetic cycling releases Fe to bottom waters, and density flows transport shelf bottom water to the open Arctic Ocean. Low Mn contents reflect the lack of a mid-water oxygen minimum zone that would act as a reservoir for dissolved Mn. The potential host phases and sources for elements with uniquely high contents are discussed with an emphasis on scandium. Scandium sorption onto Fe oxyhydroxides and Sc-rich detritus account for atypically high scandium contents. The opening of Fram Strait in the Miocene and ventilation of the deep basins initiated Fe-Mn crust growth ∼15 Myr ago.

Microstructure of Vacuum-Brazed Joints of Super-Ni/NiCr Laminated Composite Using Nickel-Based Amorphous Filler Metal

NASA Astrophysics Data System (ADS)

Ma, Qunshuang; Li, Yajiang; Wu, Na; Wang, Juan

2013-06-01

Vacuum brazing of super-Ni/NiCr laminated composite and Cr18-Ni8 stainless steel was carried out using Ni-Cr-Si-B amorphous filler metal at 1060, 1080, and 1100 °C, respectively. Microstructure and phase constitution were investigated by means of optical and scanning electron microscopy, energy-dispersive spectroscopy, x-ray diffraction, and micro-hardness tester. When brazed at 1060-1080 °C, the brazed region can be divided into two distinct zones: isothermally solidified zone (ISZ) consisting of γ-Ni solid solution and athermally solidified zone (ASZ) consisting of Cr-rich borides. Micro-hardness of the Cr-rich borides formed in the ASZ was as high as 809 HV50 g. ASZ decreased with increase of the brazing temperature. Isothermal solidification occurred sufficiently at 1100 °C and an excellent joint composed of γ-Ni solid solution formed. The segregation of boron from ISZ to residual liquid phase is the reason of Cr-rich borides formed in ASZ. The formation of secondary precipitates in diffusion-affected zone is mainly controlled by diffusion of B.

Microstructure and High Temperature Mechanical Property of Fe-Cr-B Based Metal/Ceramic Composite Manufactured by Metal Injection Molding Process

NASA Astrophysics Data System (ADS)

Lee, Kee-Ahn; Gwon, Jin-Han; Yoon, Tae-Sik

2018-03-01

This study investigated the microstructure and the room and high temperature mechanical properties of Fe-Cr-B alloy manufactured by metal injection molding. In addition, hot isostatic pressing was performed to increase the density of the material, and a comparison of properties was made. Microstructural observation confirmed a bi-continuous structure composed of a three-dimensional network of α-Fe phase and (Cr,Fe)2B phase. The HIPed specimen featured a well-formed adhesion between the α-Fe phase and boride, and the number of fine pores was significantly reduced. The tensile results confirmed that the HIPed specimen (RT to 900 °C) had higher strengths compared to the as-sintered specimen, and the change of elongation starting from 700 °C was significantly greater in the HIPed specimen. Fractography suggested that cracks propagated mostly along the interface between the α-Fe matrix and boride in the as-sintered specimen, while direct fracture of boride was observed in addition to interface separation in the HIPed specimen.

Separation of 44Ti from proton irradiated scandium by using solid-phase extraction chromatography and design of 44Ti/44Sc generator system.

PubMed

Radchenko, V; Meyer, C A L; Engle, J W; Naranjo, C M; Unc, G A; Mastren, T; Brugh, M; Birnbaum, E R; John, K D; Nortier, F M; Fassbender, M E

2016-12-16

Scandium-44g (half-life 3.97h [1]) shows promise for positron emission tomography (PET) imaging of longer biological processes than that of the current gold standard, 18 F, due to its favorable decay parameters. One source of 44g Sc is the long-lived parent nuclide 44 Ti (half-life 60.0 a). A 44 Ti/ 44g Sc generator would have the ability to provide radionuclidically pure 44g Sc on a daily basis. The production of 44 Ti via the 45 Sc(p,2n) reaction requires high proton beam currents and long irradiation times. Recovery and purification of no-carrier added (nca) 44 Ti from scandium metal targets involves complex separation chemistry. In this study, separation systems based on solid phase extraction chromatography were investigated, including branched diglycolamide (BDGA) resin and hydroxamate based ZR resin. Results indicate that ZR resin in HCl media represents an effective 44 Ti/ 44g Sc separation system. Copyright © 2016 Elsevier B.V. All rights reserved.

Separation of 44Ti from proton irradiated scandium by using solid-phase extraction chromatography and design of 44Ti/ 44Sc generator system

DOE PAGES

Radchenko, Valery; Meyer, Catherine Anne Louise; Engle, Jonathan Ward; ...

2016-11-24

Scandium-44 g (half-life 3.97 h) shows promise for positron emission tomography (PET) imaging of longer biological processes than that of the current gold standard, 18F, due to its favorable decay parameters. One source of 44gSc is the long-lived parent nuclide 44Ti (half-life 60.0 a). A 44Ti/ 44gSc generator would have the ability to provide radionuclidically pure 44gSc on a daily basis. The production of 44Ti via the 45Sc(p,2n) reaction requires high proton beam currents and long irradiation times. Recovery and purification of no-carrier added (nca) 44Ti from scandium metal targets involves complex separation chemistry. In this study, separation systems basedmore » on solid phase extraction chromatography were investigated, including branched diglycolamide (BDGA) resin and hydroxamate based ZR resin. Lastly, results indicate that ZR resin in HCl media represents an effective 44Ti/ 44gSc separation system.« less

Change of the arc attachment mode and its effect on the lifetime in automotive high intensity discharge lamps

NASA Astrophysics Data System (ADS)

Alexejev, Alexander; Flesch, Peter; Mentel, Jürgen; Awakowicz, Peter

2016-10-01

In modern cars, the new generation Hg-free high intensity discharge (HID) lamps, the so called xenon lamps, take an important role. The long lifetime of these lamps is achieved by doping the tungsten electrodes with thorium. Thorium forms a dipole layer on the electrode surface, thus reducing the work function of tungsten. However, thoriating the electrodes is also an issue of trade and transport regulation, so a substitute is looked into. This work shows the influence of the arc attachment mode on the lifetime of the lamps. The mode of the arc attachment changes during the run-up phase of automotive HID lamps after a characteristic time period depending, i.e., on the filling of the lamps, which is dominated by scandium. It will be shown that this characteristic time period for the change of the attachment mode determines the long term performance of Hg-free xenon lamps. Measurements attributing the mode change to the scandium density in the filling are presented. The emitter effect of scandium will be suggested to be the reason of the mode change.

Electrically conductive containment vessel for molten aluminum

DOEpatents

Holcombe, C.E.; Scott, D.G.

1984-06-25

The present invention is directed to a containment vessel which is particularly useful in melting aluminum. The vessel of the present invention is a multilayered vessel characterized by being electrically conductive, essentially nonwettable by and nonreactive with molten aluminum. The vessel is formed by coating a tantalum substrate of a suitable configuration with a mixture of yttria and particulate metal 10 borides. The yttria in the coating inhibits the wetting of the coating while the boride particulate material provides the electrical conductivity through the vessel. The vessel of the present invention is particularly suitable for use in melting aluminum by ion bombardment.

Electrically conductive containment vessel for molten aluminum

DOEpatents

Holcombe, Cressie E.; Scott, Donald G.

1985-01-01

The present invention is directed to a containment vessel which is particularly useful in melting aluminum. The vessel of the present invention is a multilayered vessel characterized by being electrically conductive, essentially nonwettable by and nonreactive with molten aluminum. The vessel is formed by coating a tantalum substrate of a suitable configuration with a mixture of yttria and particulate metal borides. The yttria in the coating inhibits the wetting of the coating while the boride particulate material provides the electrical conductivity through the vessel. The vessel of the present invention is particularly suitable for use in melting aluminum by ion bombardment.

Phase equilibrium in system Ti-Si-C-B and synthesis of MAX phase layers in vacuum under the influence of electron beam

NASA Astrophysics Data System (ADS)

Smirnyagina, N. N.; Khaltanova, V. M.; Dasheev, D. E.; Lapina, A. E.

2017-05-01

Composite layers on the basis of carbides and borides the titan and silicon on titanic alloy VТ-1 are generated at diffused saturation by electron beam treatment in vacuum. Formation in a composite of MAX phase Ti3SiC2 is shown. Thermodynamic research of phase equilibrium in systems Ti-Si-C and Ti-B-C in the conditions of high vacuum is executed. The thermodynamics, formation mechanisms of superfirm layers borides and carbides of the titan and silicon are investigated.

Brazing Inconel 625 Using Two Ni/(Fe)-Based Amorphous Filler Foils

NASA Astrophysics Data System (ADS)

Chen, Wen-Shiang; Shiue, Ren-Kae

2012-07-01

For MBF-51 filler, the brazed joint consists of interfacial grain boundary borides, coarse Nb6Ni16Si7, and Ni/Cr-rich matrix. In contrast, the VZ-2106 brazed joint is composed of interfacial Nb6Ni16Si7 precipitates as well as grain boundary borides, coarse Nb6Ni16Si7, and Ni/Cr/Fe-rich matrix. The maximum tensile strength of 443 MPa is obtained from the MBF-51 brazed specimen. The tensile strengths of VZ-2106 brazed joints are approximately 300 MPa. Both amorphous filler foils demonstrate potential in brazing IN-625 substrate.

Betavoltaics using scandium tritide and contact potential difference

NASA Astrophysics Data System (ADS)

Liu, Baojun; Chen, Kevin P.; Kherani, Nazir P.; Zukotynski, Stefan; Antoniazzi, Armando B.

2008-02-01

Tritium-powered betavoltaic micropower sources using contact potential difference (CPD) are demonstrated. Thermally stable scandium tritide thin films with a surface activity of 15mCi/cm2 were used as the beta particle source. The electrical field created by the work function difference between the ScT film and a platinum or copper electrode was used to separate the beta-generated electrical charge carriers. Open circuit voltages of 0.5 and 0.16V and short circuit current densities of 2.7 and 5.3nA/cm2 were achieved for gaseous and solid dielectric media-based CPD cells, respectively.

Scandium(III) complexes of monophosphorus acid DOTA analogues: a thermodynamic and radiolabelling study with (44)Sc from cyclotron and from a (44)Ti/(44)Sc generator.

PubMed

Kerdjoudj, R; Pniok, M; Alliot, C; Kubíček, V; Havlíčková, J; Rösch, F; Hermann, P; Huclier-Markai, S

2016-01-28

The complexation ability of DOTA analogs bearing one methylenephosphonic (DO3AP) or methylenephosphinic (DO3AP(PrA) and DO3AP(ABn)) acid pendant arm toward scandium was evaluated. Stability constants of their scandium(iii) complexes were determined by potentiometry combined with (45)Sc NMR spectroscopy. The stability constants of the monophosphinate analogues are somewhat lower than that of the Sc-DOTA complex. The phosphorus acid moiety interacts with trivalent scandium even in very acidic solutions forming out-of-cage complexes; the strong affinity of the phosphonate group to Sc(iii) precludes stability constant determination of the Sc-DO3AP complex. These results were compared with those obtained by the free-ion selective radiotracer extraction (FISRE) method which is suitable for trace concentrations. FISRE underestimated the stability constants but their relative order was preserved. Nonetheless, as this method is experimentally simple, it is suitable for a quick relative comparison of stability constant values under trace concentrations. Radiolabelling of the ligands with (44)Sc was performed using the radioisotope from two sources, a (44)Ti/(44)Sc generator and (44m)Sc/(44)Sc from a cyclotron. The best radiolabelling conditions for the ligands were pH = 4, 70 °C and 20 min which were, however, not superior to those of the parent DOTA. Nonetheless, in vitro behaviour of the Sc(iii) complexes in the presence of hydroxyapatite and rat serum showed sufficient stability of (44)Sc complexes of these ligands for in vivo applications. PET images and ex vivo biodistribution of the (44)Sc-DO3AP complex performed on healthy Wistar male rats showed no specific bone uptake and rapid clearance through urine.

Synthesis, Structure, and Properties of Refractory Hard-Metal Borides

NASA Astrophysics Data System (ADS)

Lech, Andrew Thomas

As the limits of what can be achieved with conventional hard compounds, such as tungsten carbide, are nearing reach, super-hard materials are an area of increasing industrial interest. The refractory hard metal borides, such as ReB2 and WB4, offer an increasingly attractive alternative to diamond and cubic boron nitride as a next-generation tool material. In this Thesis, a thorough discussion is made of the progress achieved by our laboratory towards understanding the synthesis, structure, and properties of these extremely hard compounds. Particular emphasis is placed on structural manipulation, solid solution formation, and the unique crystallographic manifestations of what might also be called "super-hard metals".

Interaction of scandium and titanium atoms with a carbon surface containing five- and seven-membered rings

DOE Office of Scientific and Technical Information (OSTI.GOV)

Krasnov, P. O., E-mail: kpo1980@gmail.com; Eliseeva, N. S.; Kuzubov, A. A., E-mail: alex_xx@rambler.ru

2012-01-15

The use of carbon nanotubes coated by atoms of transition metals to store molecular hydrogen is associated with the problem of the aggregation of these atoms, which leads to the formation of metal clusters. The quantum-chemical simulation of cluster models of the carbon surface of a graphene type with scandium and titanium atoms has been performed. It has been shown that the presence of five- and seven-membered rings, in addition to six-membered rings, in these structures makes it possible to strongly suppress the processes of the migration of metal atoms over the surface, preventing their clustering.

Rare earths, the lanthanides, yttrium and scandium

USGS Publications Warehouse

Hedrick, J.B.

2006-01-01

In 2005, rare earths were not mined in the United States. The major supplier, Molycorp, continued to maintain a large stockpile of rare-earth concentrates and compounds. Consumption decreased of refined rare-earth products. The United States remained a major importer and exporter of rare earths in 2005. During the same period, yttrium was not mined or refined in the US. Hence, supply of yttrium compounds for refined yttrium products came from China, France and Japan. Scandium was not also mined. World production was primarily in China, Russia and Ukraine. Demand for rare earths in 2006 is expected to be closely tied to economic conditions in the US.

Static high pressure studies on Nd and Sc

DOE Office of Scientific and Technical Information (OSTI.GOV)

Akella, J.; Xu, J.; Smith, G.S.

1985-06-24

We have investigated the crystal structural transformations in neodymium and scandium up to 4.0 GPa pressure and at room temperature, in a diamond-anvil high pressure apparatus. Nd has a double hexagonal-close packed (dhcp) structure at ambient pressure and temperature. Then it transforms to a face-centered cubic (fcc) structure at 3.8 GPa, which further transforms to a triple hexagonal-close packed structure (thcp) at about 18.0 GPa. In scandium we observed only one transformation from the hexagonal-close packed (hcp) structure at room temperature to a tetragonal structure. This transformation occurs between 19.0 and 23.2 GPa pressure.

Energy levels, oscillator strengths, and transition probabilities for sulfur-like scandium, Sc VI

NASA Astrophysics Data System (ADS)

El-Maaref, A. A.; Abou Halaka, M. M.; Saddeek, Yasser B.

2017-09-01

Energy levels, Oscillator strengths, and transition probabilities for sulfur-like scandium are calculated using CIV3 code. The calculations have been executed in an intermediate coupling scheme using Breit-Pauli Hamiltonian. The present calculations have been compared with the experimental data and other theoretical calculations. LANL code has been used to confirm the accuracy of the present calculations, where the calculations using CIV3 code agree well with the corresponding values by LANL code. The calculated energy levels and oscillator strengths are in reasonable agreement with the published experimental data and theoretical values. We have calculated lifetimes of some excited levels, as well.

Structural, electronic and thermal properties of super hard ternary boride, WAlB

NASA Astrophysics Data System (ADS)

Rajpoot, Priyanka; Rastogi, Anugya; Verma, U. P.

2018-04-01

A first principle study of the structural, electronic and thermal properties of Tungsten Aluminum Boride (WAlB) using full-potential linearized augmented plane wave (FP-LAPW) in the frame work of density function theory (DFT) have been calculated. The calculated equilibrium structural parameters are in excellent agreement with available experimental results. The calculated electronic band structure reveals that WAlB is metallic in nature. The quasi-harmonic Debye model is applied to study of the temperature and pressure effect on volume, Debye temperature, thermal expansion coefficient and specific heat at constant volume and constant pressure. To the best of our knowledge theoretical investigation of these properties of WAlB is reported for the first time.

Infiltration processing of boron carbide-, boron-, and boride-reactive metal cermets

DOEpatents

Halverson, Danny C.; Landingham, Richard L.

1988-01-01

A chemical pretreatment method is used to produce boron carbide-, boron-, and boride-reactive metal composites by an infiltration process. The boron carbide or other starting constituents, in powder form, are immersed in various alcohols, or other chemical agents, to change the surface chemistry of the starting constituents. The chemically treated starting constituents are consolidated into a porous ceramic precursor which is then infiltrated by molten aluminum or other metal by heating to wetting conditions. Chemical treatment of the starting constituents allows infiltration to full density. The infiltrated precursor is further heat treated to produce a tailorable microstructure. The process at low cost produces composites with improved characteristics, including increased toughness, strength.

The Quantitative Significance of Nondestructive Evaluation of Graphite and Ceramic Materials.

DTIC Science & Technology

NONDESTRUCTIVE TESTING), (* GRAPHITE , (*BORIDES, NONDESTRUCTIVE TESTING), (*REFRACTORY MATERIALS, NONDESTRUCTIVE TESTING), DEFECTS(MATERIALS), TENSILE PROPERTIES, RADIOGRAPHY, ULTRASONIC PROPERTIES, DENSITY.

High-Temperature Syntheses of New, Thermally-Stable Chemical Compounds.

DTIC Science & Technology

SYNTHESIS(CHEMISTRY), HEAT RESISTANT PLASTICS, NITRILES, FLUORINE COMPOUNDS, COMPLEX COMPOUNDS, NITROGEN, SULFIDES, ORGANOMETALLIC COMPOUNDS, ORGANOBORANES, BORIDES, SPINEL, CARBIDES, NITRIDES, SILICIDES .

B Layers and Adhesion on Armco Iron Substrate

NASA Astrophysics Data System (ADS)

Elias-Espinosa, M.; Ortiz-Domínguez, M.; Keddam, M.; Flores-Rentería, M. A.; Damián-Mejía, O.; Zuno-Silva, J.; Hernández-Ávila, J.; Cardoso-Legorreta, E.; Arenas-Flores, A.

2014-08-01

In this work, a kinetic model was suggested to evaluate the boron diffusion coefficient in the Fe2B layers grown on the Armco iron substrate by the powder-pack boriding. This thermochemical treatment was carried out in the temperature range of 1123-1273 K for treatment times ranging from 2 to 8 h. The boron diffusion coefficient in the Fe2B layers was estimated by solving the mass balance equation at the (Fe2B/substrate) interface with an inclusion of boride incubation time. To validate the present model, the simulated value of Fe2B layer thickness was compared with the experimental value obtained at 1253 K for a treatment time of 5 h. The morphology of Fe2B layers was observed by SEM and optical microscopy. Metallographic studies showed that the boride layer has a saw-tooth morphology in all the samples. The layer thickness measurements were done with the help of MSQ PLUS software. The Fe2B phase was identified by x-ray diffraction method. Finally, the adherence of Fe2B layers on the Armco iron substrate was qualitatively evaluated by using the Daimler-Benz Rockwell-C indentation technique. In addition, the estimated value of boron activation energy was compared to the literature data.

A Simple, General Synthetic Route toward Nanoscale Transition Metal Borides.

PubMed

Jothi, Palani R; Yubuta, Kunio; Fokwa, Boniface P T

2018-04-01

Most nanomaterials, such as transition metal carbides, phosphides, nitrides, chalcogenides, etc., have been extensively studied for their various properties in recent years. The similarly attractive transition metal borides, on the contrary, have seen little interest from the materials science community, mainly because nanomaterials are notoriously difficult to synthesize. Herein, a simple, general synthetic method toward crystalline transition metal boride nanomaterials is proposed. This new method takes advantage of the redox chemistry of Sn/SnCl 2 , the volatility and recrystallization of SnCl 2 at the synthesis conditions, as well as the immiscibility of tin with boron, to produce crystalline phases of 3d, 4d, and 5d transition metal nanoborides with different morphologies (nanorods, nanosheets, nanoprisms, nanoplates, nanoparticles, etc.). Importantly, this method allows flexibility in the choice of the transition metal, as well as the ability to target several compositions within the same binary phase diagram (e.g., Mo 2 B, α-MoB, MoB 2 , Mo 2 B 4 ). The simplicity and wide applicability of the method should enable the fulfillment of the great potential of this understudied class of materials, which show a variety of excellent chemical, electrochemical, and physical properties at the microscale. © 2018 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Corrosion and wear behaviors of boronized AISI 316L stainless steel

NASA Astrophysics Data System (ADS)

Kayali, Yusuf; Büyüksaǧiş, Aysel; Yalçin, Yılmaz

2013-09-01

In this study, the effects of a boronizing treatment on the corrosion and wear behaviors of AISI 316L austenitic stainless steel (AISI 316L) were examined. The corrosion behavior of the boronized samples was studied via electrochemical methods in a simulation body fluid (SBF) and the wear behavior was examined using the ball-on-disk wear method. It was observed that the boride layer that formed on the AISI 316L surface had a flat and smooth morphology. Furthermore, X-ray diffraction analyses show that the boride layer contained FeB, Fe2B, CrB, Cr2B, NiB, and Ni2B phases. Boride layer thickness increased with an increasing boronizing temperature and time. The boronizing treatment also increased the surface hardness of the AISI 316L. Although there was no positive effect of the coating on the corrosion resistance in the SBF medium. Furthermore, a decrease in the friction coefficient was recorded for the boronized AISI 316L. As the boronizing temperature increased, the wear rate decreased in both dry and wet mediums. As a result, the boronizing treatment contributed positively to the wear resistance by increasing the surface hardness and by decreasing the friction coefficient of the AISI 316L.

Determination of scandium in acid mine drainage by ICP-OES with flow injection on-line preconcentration using oxidized multiwalled carbon nanotubes.

PubMed

Jerez, Javier; Isaguirre, Andrea C; Bazán, Cristian; Martinez, Luis D; Cerutti, Soledad

2014-06-01

An on-line scandium preconcentration and determination system implemented with inductively coupled plasma optical emission spectrometry associated with flow injection was studied. Trace amounts of scandium were preconcentrated by sorption on a minicolumn packed with oxidized multiwalled carbon nanotubes, at pH 1.5. The retained analyte was removed from the minicolumn with 30% (v/v) nitric acid. A total enrichment factor of 225-fold was obtained within a preconcentration time of 300 s (for a 25 mL sample volume). The overall time required for preconcentration and elution of 25 mL of sample was about 6 min; the throughput was about 10 samples per hour. The value of the detection limit was 4 ng L(-1) and the precision for 10 replicate determinations at 100 ng L(-1) Sc level was 5% relative standard deviation, calculated from the peak heights obtained. The calibration graph using the preconcentration system was linear with a correlation coefficient of 0.9996 at levels near the detection limits up to at least 10 mg L(-1). After optimization, the method was successfully applied to the determination of Sc in an acid drainage from an abandoned mine located in the province of San Luis, Argentina. Copyright © 2014 Elsevier B.V. All rights reserved.

Design of cemented tungsten carbide and boride-containing shields for a fusion power plant

NASA Astrophysics Data System (ADS)

Windsor, C. G.; Marshall, J. M.; Morgan, J. G.; Fair, J.; Smith, G. D. W.; Rajczyk-Wryk, A.; Tarragó, J. M.

2018-07-01

Results are reported on cemented tungsten carbide (cWC) and boride-containing composite materials for the task of shielding the centre column of a superconducting tokamak power plant. The shield is based on five concentric annular shells consisting of cWC and water layers of which the innermost cWC shield can be replaced with boride composites. Sample materials have been fabricated changing the parameters of porosity P, binder alloy fraction f binder and boron weight fraction f boron. For the fabricated materials, and other hypothetical samples with chosen parameters, Monte Carlo studies are made of: (i) the power deposition into the superconducting core, (ii) the fast neutron and gamma fluxes and (iii) the attenuation coefficients through the shield for the deposited power and neutron and gamma fluxes. It is shown that conventional Co-based cWC binder alloy can be replaced with a Fe–Cr alloy (92 wt.% Fe, 8 wt.% Cr), which has lower activation than cobalt with minor changes in shield performance. Boride-based composite materials have been prepared and shown to give a significant reduction in power deposition and flux, when placed close to the superconducting core. A typical shield of cemented tungsten carbide with 10 wt.% of Fe–8Cr binder and 0.1% porosity has a power reduction half-length of 0.06 m. It is shown that the power deposition increases by 4.3% for every 1% additional porosity, and 1.7% for every 1 wt.% additional binder. Power deposition decreased by 26% for an initial 1 wt.% boron addition, but further increases in f boron showed only a marginal decrease. The dependences of power deposited in the core, the maximum neutron and gamma fluxes on the core surface, and the half attenuation distances through the shield have been fitted to within a fractional percentage error by analytic functions of the porosity, metallic binder alloy and boron weight fractions.

Autocatalytic formation of an iron(IV)-oxo complex via scandium ion-promoted radical chain autoxidation of an iron(II) complex with dioxygen and tetraphenylborate.

PubMed

Nishida, Yusuke; Lee, Yong-Min; Nam, Wonwoo; Fukuzumi, Shunichi

2014-06-04

A non-heme iron(IV)-oxo complex, [(TMC)Fe(IV)(O)](2+) (TMC = 1,4,8,11-tetramethyl-1,4,8,11-tetraazacyclotetradecane), was formed by oxidation of an iron(II) complex ([(TMC)Fe(II)](2+)) with dioxygen (O2) and tetraphenylborate (BPh4(-)) in the presence of scandium triflate (Sc(OTf)3) in acetonitrile at 298 K via autocatalytic radical chain reactions rather than by a direct O2 activation pathway. The autocatalytic radical chain reaction is initiated by scandium ion-promoted electron transfer from BPh4(-) to [(TMC)Fe(IV)(O)](2+) to produce phenyl radical (Ph(•)). The chain propagation step is composed of the addition of O2 to Ph(•) and the reduction of the resulting phenylperoxyl radical (PhOO(•)) by scandium ion-promoted electron transfer from BPh4(-) to PhOO(•) to produce phenyl hydroperoxide (PhOOH), accompanied by regeneration of phenyl radical. PhOOH reacts with [(TMC)Fe(II)](2+) to yield phenol (PhOH) and [(TMC)Fe(IV)(O)](2+). Biphenyl (Ph-Ph) was formed via the radical chain autoxidation of BPh3 by O2. The induction period of the autocatalytic radical chain reactions was shortened by addition of a catalytic amount of [(TMC)Fe(IV)(O)](2+), whereas addition of a catalytic amount of ferrocene that can reduce [(TMC)Fe(IV)(O)](2+) resulted in elongation of the induction period. Radical chain autoxidation of BPh4(-) by O2 also occurred in the presence of Sc(OTf)3 without [(TMC)Fe(IV)(O)](2+), initiating the autocatalytic oxidation of [(TMC)Fe(II)](2+) with O2 and BPh4(-) to yield [(TMC)Fe(IV)(O)](2+). Thus, the general view for formation of non-heme iron(IV)-oxo complexes via O2-binding iron species (e.g., Fe(III)(O2(•-))) without contribution of autocatalytic radical chain reactions should be viewed with caution.

Effects of scandium substitution on the crystal structure and luminescence properties of LuBO{sub 3}: Ce{sup 3+}

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wu, Yuntao, E-mail: caswyt@hotmail.com; Ren, Guohao, E-mail: rgh@mail.sic.ac.cn; Ding, Dongzhou

2012-10-15

The calcite phase of LuBO{sub 3} and ScBO{sub 3} polycrystalline powders were synthesized by solid state reaction method, and the Lu{sub 1-x}Sc{sub x}BO{sub 3}:Ce (x=0.2, 0.5, 0.7) single crystals were grown by the Czochralski method. A large composition deviation between the initial polycrystalline powders and final single crystal was confirmed by electron probe micro-analysis. Raman spectroscopy revealed that moderate lattice disorder was induced by scandium substitution. However, based on the single crystal X-ray study, we finally concluded that the crystal structure of lutetium scandium orthoborate still crystallized in the rhombohedral system belonging to R3{sup -}c. Furthermore, the relationship between themore » energies of the five 5d levels of Ce{sup 3+} and the crystalline environment was revealed. The total redshift, total crystal field splitting, and centroid shift of Lu{sub 1-x}Sc{sub x}BO{sub 3}:Ce{sup 3+} were calculated based on their VUV excitation spectra. The variations trend of these observed spectroscopic parameters was in accordance with the predicted ones. - Graphical abstract: The crystal structure of Lu{sub 1-x}Sc{sub x}BO{sub 3}:Ce is rhombohedral system with R3{sup -}c space group. The relationship between the energies of the five Ce{sup 3+} 5d levels and the crystalline environment is established. Highlights: Black-Right-Pointing-Pointer Moderate lattice disorder is induced by scandium doping. Black-Right-Pointing-Pointer The crystal structure of Lu{sub 1-x}Sc{sub x}BO{sub 3}:Ce is rhombohedral system with R3{sup -}c space group. Black-Right-Pointing-Pointer Relationship between energies of Ce{sup 3+} 5d levels and crystalline environment is established. Black-Right-Pointing-Pointer The spectroscopic parameters are experimentally and theoretically calculated.« less

Etude des mecanismes de formation des microstructures lors du brasage isotherme de superalliages a base de nickel

NASA Astrophysics Data System (ADS)

Ruiz-Vargas, Jose

This thesis reports theoretical and experimental investigations carried out to understand the mechanisms of microstructure formation during isothermal brazing, produced by brazing Inconel 625 and MC2 nickel-based superalloys with filler metal BNi-2. Firstly, studies were made on pure Ni to interpret microstructure's formation with simplified alloy chemistry. Microstructure formation have been studied when varying time at constant temperature (isothermal kinetics), but also when varying temperature for constant hold time (isochronal kinetics). The chemical composition and crystallography of the present phases have been identified, with the following results : (i) the fraction of dissolved base metal has been found proportional to the initial thickness of the brazing alloy, so that the composition of the liquid remains homogeneous with a precise initial equilibrium composition during the whole brazing process, (ii) the melting of the joint occurs in two steps : at lower temperature, it involves only partially melting, and boron diffusion in pure Ni leads to the precipitation of fine Ni3B borides at the interface ; in a second stage, at higher temperature, melting is complete and thermodynamic equilibrium requires significant dissolution of nickel, which also involves the dissolution of part of borides already formed. Secondly, nickel plating technique was used on Inconel 625 nickel-based superalloy. A thin layer of Ni with varying thickness, has been electrodeposited to observe the gradual dissolution of Inconel and microstructural features formation due to the presence of superalloy alloying elements. It has been observed that the nickel coating does not prevent precipitation in the base metal as boron diffuse rapidly through the coating width. In the intermediate nickel plating width, fragile precipitates of nickel borides have been observed, because the contribution of Inconel alloying elements to the melt was very limited. In absence of nickel plating on the superalloy, the formation of Nb and Cr-Mo borides phase has been observed. Efforts have been made to evaluate the accuracy of Boron measurement by energy dispersion X-ray spectroscopy (EDS) in the MC2 superalloy and BNi-2 filler metal. The most accurate method to quantify Boron using EDS is by composition difference. A precision of 5 at.% has been reached when using optimized data acquisition and post processing schemes. Ultimately, Electron Backscatter Diffraction (EBSD) combined with localized EDS analysis has been proven invaluable in conclusively identifying micrometer sized boride precipitates ; thus further improving the characterization of brazed Ni-based superalloys.

Plasma enhanced chemical vapor deposition of metalboride interfacial layers as diffusion barriers for nanostructured diamond growth on cobalt containing alloys CoCrMo and WC-Co

NASA Astrophysics Data System (ADS)

Johnston, Jamin M.

This work is a compilation of theory, finite element modeling and experimental research related to the use of microwave plasma enhanced chemical vapor deposition (MPECVD) of diborane to create metal-boride surface coatings on CoCrMo and WC-Co, including the subsequent growth of nanostructured diamond (NSD). Motivation for this research stems from the need for wear resistant coatings on industrial materials, which require improved wear resistance and product lifetime to remain competitive and satisfy growing demand. Nanostructured diamond coatings are a promising solution to material wear but cannot be directly applied to cobalt containing substrates due to graphite nucleation. Unfortunately, conventional pre-treatment methods, such as acid etching, render the substrate too brittle. Thus, the use of boron in a MPECVD process is explored to create robust interlayers which inhibit carbon-cobalt interaction. Furthermore, modeling of the MPECVD process, through the COMSOL MultiphysicsRTM platform, is performed to provide insight into plasma-surface interactions using the simulation of a real-world apparatus. Experimental investigation of MPECVD boriding and NSD deposition was conducted at surface temperatures from 700 to 1100 °C. Several well-adhered metal-boride surface layers were formed: consisting of CoB, CrB, WCoB, CoB and/or W2CoB2. Many of the interlayers were shown to be effective diffusion barriers against elemental cobalt for improving nucleation and adhesion of NSD coatings; diamond on W2CoB2 was well adhered. However, predominantly WCoB and CoB phase interlayers suffered from diamond film delamination. Metal-boride and NSD surfaces were evaluated using glancing-angle x-ray diffraction (XRD), x-ray photoelectron spectroscopy (XPS), cross-sectional scanning electron microscopy (SEM), energy dispersive x-ray spectroscopy (EDS), micro-Raman spectroscopy, nanoindentation, scratch testing and epoxy pull testing. COMSOL MultiphysicsRTM was used to construct a representation of the MPECVD chamber. Relevant material properties, boundary conditions and adjustable parameters were applied to match the actual experimental set-up. Despite approximations, simulations for the surface temperature and surface accumulation matched well with experimental data. The combination of data from CoCrMo, WC-Co and modeling of the MPECVD process confirms that the use of boron to create metal-boride interlayers is applicable for subsequent nanostructured diamond coatings and that the surface temperature and deposition thickness can be predicted using finite element modeling.

Deposition and characterization of aluminum magnesium boride thin film coatings

NASA Astrophysics Data System (ADS)

Tian, Yun

Boron-rich borides are a special group of materials possessing complex structures typically comprised of B12 icosahedra. All of the boron-rich borides sharing this common structural unit exhibit a variety of exceptional physical and electrical properties. In this work, a new ternary boride compound AlMgB14, which has been extensively studied in bulk form due to its novel mechanical properties, was fabricated into thin film coatings by pulsed laser deposition (PLD) technology. The effect of processing conditions (laser operating modes, vacuum level, substrate temperature, and postannealing, etc.) on the composition, microstructure evolution, chemical bonding, and surface morphology of AlMgB14 thin film coatings has been investigated by X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), transmission electron microscopy (TEM), atomic force microscopy (AFM) and Fourier transform infrared (FTIR) spectrometry; the mechanical, electrical, and optical properties of AlMgB14 thin films have been characterized by nanoindentation, four-point probe, van der Pauw Hall measurement, activation energy measurement, and UV-VIS-NIR spectrophotometer. Experimental results show that AlMgB14 films deposited in the temperature range of 300 K - 873 K are amorphous. Depositions under a low vacuum level (5 x 10-5 Torr) can introduce a significant amount of C and O impurities into AlMgB14 films and lead to a complex oxide glass structure. Orthorhombic AlMgB14 phase cannot be obtained by subsequent high temperature annealing. By contrast, the orthorhombic AlMgB 14 crystal structure can be attained via high temperature-annealing of AlMgB14 films deposited under a high vacuum level (< 3 x 10-6 Torr), accompanied by strong texture formation. Low vacuum level-as deposited AlMgB14 films have low hardness (10 GPa), but high vacuum level-as deposited AlMgB14 films exhibit an extremely high hardness (45 GPa - 51 GPa), and the higher deposition temperature results in still higher hardness. Furthermore, a very low friction coefficient (0.04 - 0.05) has been observed for high vacuum level-as deposited AlMgB14 films, which could be ascribed to the in situ formation of a surface self-lubricating layer. Unlike most boron-rich boride films, high vacuum level-as deposited AlMgB14 films also possess a low n-type electrical resistivity, which is a consequence of high carrier concentration and moderate carrier mobility. The operative electrical transport mechanism and doping behavior for high vacuum level-as deposited AlMgB14 films are discussed in detail in this thesis.

Thermodynamic and kinetic study of scandium(III) complexes of DTPA and DOTA: a step toward scandium radiopharmaceuticals.

PubMed

Pniok, Miroslav; Kubíček, Vojtěch; Havlíčková, Jana; Kotek, Jan; Sabatie-Gogová, Andrea; Plutnar, Jan; Huclier-Markai, Sandrine; Hermann, Petr

2014-06-23

Diethylenetriamine-N,N,N',N'',N''-pentaacetic acid (DTPA) and 1,4,7,10-tetraazacyclododecane-1,4,7,10-tetraacetic acid (DOTA) scandium(III) complexes were investigated in the solution and solid state. Three (45)Sc NMR spectroscopic references suitable for aqueous solutions were suggested: 0.1 M Sc(ClO4)3 in 1 M aq. HClO4 (δSc =0.0 ppm), 0.1 M ScCl3 in 1 M aq. HCl (δSc =1.75 ppm) and 0.01 M [Sc(ox)4](5-) (ox(2-) = oxalato) in 1 M aq. K2C2O4 (δSc =8.31 ppm). In solution, [Sc(dtpa)](2-) complex (δSc = 83 ppm, Δν = 770 Hz) has a rather symmetric ligand field unlike highly unsymmetrical donor atom arrangement in [Sc(dota)](-) anion (δSc = 100 ppm, Δν = 4300 Hz). The solid-state structure of K8[Sc2(ox)7]⋅13 H2O contains two [Sc(ox)3](3-) units bridged by twice "side-on" coordinated oxalate anion with Sc(3+) ion in a dodecahedral O8 arrangement. Structures of [Sc(dtpa)](2-) and [Sc(dota)](-) in [(Hguanidine)]2[Sc(dtpa)]⋅3 H2O and K[Sc(dota)][H6 dota]Cl2⋅4 H2O, respectively, are analogous to those of trivalent lanthanide complexes with the same ligands. The [Sc(dota)](-) unit exhibits twisted square-antiprismatic arrangement without an axial ligand (TSA' isomer) and [Sc(dota)](-) and (H6 dota)(2+) units are bridged by a K(+) cation. A surprisingly high value of the last DOTA dissociation constant (pKa =12.9) was determined by potentiometry and confirmed by using NMR spectroscopy. Stability constants of scandium(III) complexes (log KScL 27.43 and 30.79 for DTPA and DOTA, respectively) were determined from potentiometric and (45)Sc NMR spectroscopic data. Both complexes are fully formed even below pH 2. Complexation of DOTA with the Sc(3+) ion is much faster than with trivalent lanthanides. Proton-assisted decomplexation of the [Sc(dota)](-) complex (τ1/2 =45 h; 1 M aq. HCl, 25 °C) is much slower than that for [Ln(dota)](-) complexes. Therefore, DOTA and its derivatives seem to be very suitable ligands for scandium radioisotopes. © 2014 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Improving sensitivity and resolution of MQMAS spectra: A 45Sc-NMR case study of scandium sulphate pentahydrate

NASA Astrophysics Data System (ADS)

Chandran, C. Vinod; Cuny, Jérôme; Gautier, Régis; Pollès, Laurent Le; Pickard, Chris J.; Bräuniger, Thomas

2010-04-01

To efficiently obtain multiple-quantum magic-angle spinning (MQMAS) spectra of the nuclide 45Sc (I = 7/2), we have combined several previously suggested techniques to enhance the signal-to-noise ratio and to improve spectral resolution for the test sample, scandium sulphate pentahydrate (ScSPH). Whereas the 45Sc-3QMAS spectrum of ScSPH does not offer sufficient resolution to clearly distinguish between the 3 scandium sites present in the crystal structure, these sites are well-resolved in the 5QMAS spectrum. The loss of sensitivity incurred by using MQMAS with 5Q coherence order is partly compensated for by using fast-amplitude modulated (FAM) sequences to improve the efficiency of both 5Q coherence excitation and conversion. Also, heteronuclear decoupling is employed to minimise dephasing of the 45Sc signal during the 5Q evolution period due to dipolar couplings with the water protons in the ScSPH sample. Application of multi-pulse decoupling schemes such as TPPM and SPINAL results in improved sensitivity and resolution in the F1 (isotropic) dimension of the 5QMAS spectrum, the best results being achieved with the recently suggested SWf-TPPM sequence. By numerical fitting of the 45Sc-NMR spectra of ScSPH from 3QMAS, 5QMAS and single-quantum MAS at magnetic fields B0 = 9.4 T and 17.6 T, the isotropic chemical shift δiso, the quadrupolar coupling constant χ, and the asymmetry parameter η were obtained. Averaging over all experiments, the NMR parameters determined for the 3 scandium sites, designated (a), (b) and (c) are: δiso(a) = -15.5 ± 0.5 ppm, χ(a) = 5.60 ± 0.10 MHz, η(a) = 0.06 ± 0.05; δiso(b) = -12.9 ± 0.5 ppm, χ(b) = 4.50 ± 0.10 MHz, η(b) = 1.00 ± 0.00; and δiso(c) = -4.7 ± 0.2 ppm, χ(c) = 4.55 ± 0.05 MHz, η(c) = 0.50 ± 0.02. The NMR scandium species were assigned to the independent crystallographic sites by evaluating their experimental response to proton decoupling, and by density functional theory (DFT) calculations using the PAW and GIPAW approaches, in the following way: Sc(1) to (c), Sc(2) to (a), and Sc(3) to (b). The need to compute NMR parameters using an energy-optimised crystal structure is once again demonstrated.

Improving sensitivity and resolution of MQMAS spectra: a 45Sc-NMR case study of scandium sulphate pentahydrate.

PubMed

Chandran, C Vinod; Cuny, Jérôme; Gautier, Régis; Le Pollès, Laurent; Pickard, Chris J; Bräuniger, Thomas

2010-04-01

To efficiently obtain multiple-quantum magic-angle spinning (MQMAS) spectra of the nuclide 45Sc (I=7/2), we have combined several previously suggested techniques to enhance the signal-to-noise ratio and to improve spectral resolution for the test sample, scandium sulphate pentahydrate (ScSPH). Whereas the 45Sc-3QMAS spectrum of ScSPH does not offer sufficient resolution to clearly distinguish between the 3 scandium sites present in the crystal structure, these sites are well-resolved in the 5QMAS spectrum. The loss of sensitivity incurred by using MQMAS with 5Q coherence order is partly compensated for by using fast-amplitude modulated (FAM) sequences to improve the efficiency of both 5Q coherence excitation and conversion. Also, heteronuclear decoupling is employed to minimise dephasing of the 45Sc signal during the 5Q evolution period due to dipolar couplings with the water protons in the ScSPH sample. Application of multi-pulse decoupling schemes such as TPPM and SPINAL results in improved sensitivity and resolution in the F(1) (isotropic) dimension of the 5QMAS spectrum, the best results being achieved with the recently suggested SW(f)-TPPM sequence. By numerical fitting of the 45Sc-NMR spectra of ScSPH from 3QMAS, 5QMAS and single-quantum MAS at magnetic fields B(0)=9.4 T and 17.6 T, the isotropic chemical shift delta(iso), the quadrupolar coupling constant chi, and the asymmetry parameter eta were obtained. Averaging over all experiments, the NMR parameters determined for the 3 scandium sites, designated (a), (b) and (c) are: delta(iso)(a)=-15.5+/-0.5 ppm, chi(a)=5.60+/-0.10 MHz, eta(a)=0.06+/-0.05; delta(iso)(b)=-12.9+/-0.5 ppm, chi(b)=4.50+/-0.10 MHz, eta(b)=1.00+/-0.00; and delta(iso)(c)=-4.7+/-0.2 ppm, chi(c)=4.55+/-0.05 MHz, eta(c)=0.50+/-0.02. The NMR scandium species were assigned to the independent crystallographic sites by evaluating their experimental response to proton decoupling, and by density functional theory (DFT) calculations using the PAW and GIPAW approaches, in the following way: Sc(1) to (c), Sc(2) to (a), and Sc(3) to (b). The need to compute NMR parameters using an energy-optimised crystal structure is once again demonstrated. 2009 Elsevier Inc. All rights reserved.

Direct synthesis of magnesium borohydride

DOEpatents

Ronnebro, Ewa Carin Ellinor [Kennewick, WA; Severa, Godwin [Honolulu, HI; Jensen, Craig M [Kailua, HI

2012-04-03

A method is disclosed for directly preparing an alkaline earth metal borohydride, i.e. Mg(BH.sub.4).sub.2, from the alkaline earth metal boride MgB.sub.2 by hydrogenating the MgB.sub.2 at an elevated temperature and pressure. The boride may also be doped with small amounts of a metal chloride catalyst such as TiCl.sub.3 and/or NiCl.sub.2. The process provides for charging MgB.sub.2 with high pressure hydrogen above at least 70 MPa while simultaneously heating the material to about 350.degree. C. to about 400.degree. C. The method is relatively simple and inexpensive and provides a reversible hydride compound having a hydrogen capacity of at least 11 wt %.

The low-lying quartet electronic states of group 14 diatomic borides XB (X = C, Si, Ge, Sn, Pb)

NASA Astrophysics Data System (ADS)

Pontes, Marcelo A. P.; de Oliveira, Marcos H.; Fernandes, Gabriel F. S.; Da Motta Neto, Joaquim D.; Ferrão, Luiz F. A.; Machado, Francisco B. C.

2018-04-01

The present work focuses in the characterization of the low-lying quartet electronic and spin-orbit states of diatomic borides XB, in which X is an element of group 14 (C, Si, Ge, Sn, PB). The wavefunction was obtained at the CASSCF/MRCI level with a quintuple-ζ quality basis set. Scalar relativistic effects were also taken into account. A systematic and comparative analysis of the spectroscopic properties for the title molecular series was carried out, showing that the (1)4Π→X4Σ- transition band is expected to be measurable by emission spectroscopy to the GeB, SnB and PbB molecules, as already observed for the lighter CB and SiB species.

Energy-consistent small-core pseudopotentials for 3d-transition metals adapted to quantum Monte Carlo calculations.

PubMed

Burkatzki, M; Filippi, Claudia; Dolg, M

2008-10-28

We extend our recently published set of energy-consistent scalar-relativistic Hartree-Fock pseudopotentials by the 3d-transition metal elements, scandium through zinc. The pseudopotentials do not exhibit a singularity at the nucleus and are therefore suitable for quantum Monte Carlo (QMC) calculations. The pseudopotentials and the accompanying basis sets (VnZ with n=T,Q) are given in standard Gaussian representation and their parameter sets are presented. Coupled cluster, configuration interaction, and QMC studies are carried out for the scandium and titanium atoms and their oxides, demonstrating the good performance of the pseudopotentials. Even though the choice of pseudopotential form is motivated by QMC, these pseudopotentials can also be employed in other quantum chemical approaches.

Laser ceramic materials for subpicosecond solid-state lasers using Nd3+-doped mixed scandium garnets.

PubMed

Okada, Hajime; Tanaka, Momoko; Kiriyama, Hiromitsu; Nakai, Yoshiki; Ochi, Yoshihiro; Sugiyama, Akira; Daido, Hiroyuki; Kimura, Toyoaki; Yanagitani, Takagimi; Yagi, Hideki; Meichin, Noriyuki

2010-09-15

We have successfully developed and demonstrated broadband emission Nd-doped mixed scandium garnets based on laser ceramic technology. The inhomogeneous broadening of Nd(3+) fluorescence lines results in a bandwidth above 5 nm that is significantly broader than that for Nd:YAG and enables subpicosecond mode-locked pulse durations. We have also found the emission cross section of 7.8 × 10(-20) cm(2) to be adequate for efficient energy extraction and thermal conductivity of 4.7 W/mK from these new Nd-doped laser ceramics. The new laser ceramics are good candidates for laser host material in a diode-pumped subpicosecond laser system with high efficiency and high repetition rate.

Synthesis of aluminum-based scandium-yttrium master alloys

NASA Astrophysics Data System (ADS)

Bazhin, V. Yu.; Kosov, Ya. I.; Lobacheva, O. L.; Dzhevaga, N. V.

2015-07-01

The preparation technology for an Al-2% Sc-0.5% Y master alloy using aluminum-manganese alloys has been developed and tested. The microstructure of the prepared master alloy is studied and the compositions of intermetallics is determined. The efficient technological parameters of the synthesis are determined. It is shown that varying the compositions of starting reagents and alloying additions and optimizing the process conditions (temperature, mixing, etc.) allow us to forecast the manufacturing and operating characteristics of aluminum-based master alloys. Joint additions of scandium and yttrium oxides to a charge favor a substantial decrease in the grain size of the formed intermetallics; this effect appears to the utmost in the case of microallying with yttrium up to 0.5 wt %.

Microstructural characterization of Ni-based self-fluxing alloy after selective surface-engineering using diode laser

NASA Astrophysics Data System (ADS)

Chun, Eun-Joon; Park, Changkyoo; Nishikawa, Hiroshi; Kim, Min-Su

2018-06-01

The microstructural characterization of thermal-sprayed Ni-based self-fluxing alloy (Metco-16C®) after laser-assisted homogenization treatment was performed. To this end, a high-power diode laser system was used. This supported the real-time control of the target homogenization temperature at the substrate surface. Non-homogeneities of the macrosegregation of certain elements (C and Cu) and the local concentration of Cr-based carbides and borides in certain regions in the as-sprayed state could be enhanced with the application of homogenization. After homogenization at 1423 K, the hardness of the thermal-sprayed layer was found to have increased by 1280 HV from the as-sprayed state (750 HV). At this homogenization temperature, the microstructure of the thermal-sprayed layer consisted of a lamellar structuring of the matrix phase (austenite and Ni3Si) with fine (<5 μm) carbides and borides (the rod-like phase of Cr5B3, the lumpy phase of M23C6, and the extra-fine phase of M7C3). Despite the formation of several kinds of carbides and borides during homogenization at 1473 K, the lowest hardness level was found to be less than that of the as-sprayed state, because of the liquid-state homogenization treatment without formation of lamellar structuring between austenite and Ni3Si.

Proton-induced production and radiochemical isolation of 44Ti from scandium metal targets for 44Ti/44Sc generator development.

PubMed

Radchenko, Valery; Engle, Jonathan W; Medvedev, Dmitri G; Maassen, Joel M; Naranjo, Cleo M; Unc, George A; Meyer, Catherine A L; Mastren, Tara; Brugh, Mark; Mausner, Leonard; Cutler, Cathy S; Birnbaum, Eva R; John, Kevin D; Nortier, F Meiring; Fassbender, Michael E

2017-07-01

Scandium-44g (half-life 3.97h) shows promise for application in positron emission tomography (PET), due to favorable decay parameters. One of the sources of 44g Sc is the 44 Ti/ 44g Sc generator, which can conveniently provide this radioisotope on a daily basis at a diagnostic facility. Titanium-44 (half-life 60.0 a), in turn, can be obtained via proton irradiation of scandium metal targets. A substantial 44 Ti product batch, however, requires high beam currents, long irradiation times and an elaborate chemical procedure for 44 Ti isolation and purification. This study describes the production of a combined 175MBq (4.7mCi) batch yield of 44 Ti in week long proton irradiations at the Los Alamos Isotope Production Facility (LANL-IPF) and the Brookhaven Linac Isotope Producer (BNL-BLIP). A two-step ion exchange chromatography based chemical separation method is introduced: first, a coarse separation of 44 Ti via anion exchange sorption in concentrated HCl results in a 44 Tc/Sc separation factor of 10 2 -10 3 . A second, cation exchange based step in HCl media is then applied for 44 Ti fine purification from residual Sc mass. In summary, this method yields a 90-97% 44 Ti recovery with an overall Ti/Sc separation factor of ≥10 6 . Copyright © 2017 Elsevier Inc. All rights reserved.

Proton induced production and radiochemical isolation of 44Ti from scandium metal targets for 44Ti/ 44Sc generator development

DOE PAGES

Radchenko, Valery; Engle, Jonathan Ward; Medvedev, Dmitri G.; ...

2017-04-07

Scandium-44 g (half-life 3.97 h) shows promise for application in positron emission tomography (PET), due to favorable decay parameters. One of the sources of 44gSc is the 44Ti/ 44gSc generator, which can conveniently provide this radioisotope on a daily basis at a diagnostic facility. Titanium-44 (half-life 60.0 a), in turn, can be obtained via proton irradiation of scandium metal targets. A substantial 44Ti product batch, however, requires high beam currents, long irradiation times and an elaborate chemical procedure for 44Ti isolation and purification. This study describes the production of a combined 175 MBq (4.7 mCi) batch yield of 44Ti inmore » week long proton irradiations at the Los Alamos Isotope Production Facility (LANL-IPF) and the Brookhaven Linac Isotope Producer (BNL-BLIP). A two-step ion exchange chromatography based chemical separation method is introduced: first, a coarse separation of 44Ti via anion exchange sorption in concentrated HCl results in a 44Tc/Sc separation factor of 10 2–10 3. A second, cation exchange based step in HCl media is then applied for 44Ti fine purification from residual Sc mass. In conclusion, this method yields a 90–97% 44Ti recovery with an overall Ti/Sc separation factor of ≥10 6.« less

NASA research on refractory compounds.

NASA Technical Reports Server (NTRS)

Gangler, J. J.

1971-01-01

The behavior and properties of the refractory carbides, nitrides, and borides are being investigated by NASA as part of its research aimed at developing superior heat resistant materials for aerospace applications. Studies of the zirconium-carbon-oxygen system show that zirconium oxycarbides of different compositions and lattice parameters can be formed between 1500 C and 1900 C and are stable below 1500 C. More applied studies show that hot working generally improves the microstructure and therefore the strength of TiC and NbC. Sintering studies on UN indicate that very high densities can be achieved. Hot pressing of cermets of HfN and HfC produces good mechanical properties for high temperature bearing applications. Attempts to improve the impact resistance of boride composites by the addition of a nickel or carbon yarn were not overly successful.

Ceramic fibers from Si-B-C polymer precursors

NASA Technical Reports Server (NTRS)

Riccitiello, S. R.; Hsu, M. S.; Chen, T. S.

1993-01-01

Non-oxide ceramics such as silicon carbide (SiC), silicon nitride (Si3N4), and silicon borides (SiB4, SiB6) have thermal stability, oxidation resistance, hardness, and varied electrical properties. All these materials can be prepared in a fiber form from a suitable polymer precursor. The above mentioned fibers, when tested over a temperature range from 25 to 1400 C, experience degradation at elevated temperatures. Past work in ceramic materials has shown that the strength of ceramics containing both carbides and borides is sustained at elevated temperatures, with minimum oxidation. The work presented here describes the formation of ceramic fibers containing both elements, boron and silicon, prepared via the polymer precursor route previously reported by the authors, and discusses the fiber mechanical properties that are retained over the temperature range studied.

Low-cost industrially available molybdenum boride and carbide as "platinum-like" catalysts for the hydrogen evolution reaction in biphasic liquid systems.

PubMed

Scanlon, Micheál D; Bian, Xiaojun; Vrubel, Heron; Amstutz, Véronique; Schenk, Kurt; Hu, Xile; Liu, BaoHong; Girault, Hubert H

2013-02-28

Rarely reported low-cost molybdenum boride and carbide microparticles, both of which are available in abundant quantities due to their widespread use in industry, adsorb at aqueous acid-1,2-dichloroethane interfaces and efficiently catalyse the hydrogen evolution reaction in the presence of the organic electron donor - decamethylferrocene. Kinetic studies monitoring biphasic reactions by UV/vis spectroscopy, and further evidence provided by gas chromatography, highlight (a) their superior rates of catalysis relative to other industrially significant transition metal carbides and silicides, as well as a main group refractory compound, and (b) their highly comparable rates of catalysis to Pt microparticles of similar dimensions. Insight into the catalytic processes occurring for each adsorbed microparticle was obtained by voltammetry at the liquid-liquid interface.

Ternary ceramic thermal spraying powder and method of manufacturing thermal sprayed coating using said powder

DOE Office of Scientific and Technical Information (OSTI.GOV)

Vogli, Evelina; Sherman, Andrew J.; Glasgow, Curtis P.

The invention describes a method for producing ternary and binary ceramic powders and their thermal spraying capable of manufacturing thermal sprayed coatings with superior properties. Powder contain at least 30% by weight ternary ceramic, at least 20% by weight binary molybdenum borides, at least one of the binary borides of Cr, Fe, Ni, W and Co and a maximum of 10% by weight of nano and submicro-sized boron nitride. The primary crystal phase of the manufactured thermal sprayed coatings from these powders is a ternary ceramic, while the secondary phases are binary ceramics. The coatings have extremely high resistance againstmore » corrosion of molten metal, extremely thermal shock resistance and superior tribological properties at low and at high temperatures.« less

Design of Wear-Resistant Austenitic Steels for Selective Laser Melting

NASA Astrophysics Data System (ADS)

Lemke, J. N.; Casati, R.; Lecis, N.; Andrianopoli, C.; Varone, A.; Montanari, R.; Vedani, M.

2018-03-01

Type 316L stainless steel feedstock powder was modified by alloying with powders containing carbide/boride-forming elements to create improved wear-resistant austenitic alloys that can be readily processed by Selective Laser Melting. Fe-based alloys with high C, B, V, and Nb contents were thus produced, resulting in a microstructure that consisted of austenitic grains and a significant amount of hard carbides and borides. Heat treatments were performed to modify the carbide distribution and morphology. Optimal hard-phase spheroidization was achieved by annealing the proposed alloys at 1150 °C for 1 hour followed by water quenching. The total increase in hardness of samples containing 20 pct of C/B-rich alloy powder was of 82.7 pct while the wear resistance could be increased by a factor of 6.

Phase stable rare earth garnets

DOEpatents

Kuntz, Joshua D.; Cherepy, Nerine J.; Roberts, Jeffery J.; Payne, Stephen A.

2013-06-11

A transparent ceramic according to one embodiment includes a rare earth garnet comprising A.sub.hB.sub.iC.sub.jO.sub.12, where h is 3.+-.10%, i is 2.+-.10%, and j is 3.+-.10%. A includes a rare earth element or a mixture of rare earth elements, B includes at least one of aluminum, gallium and scandium, and C includes at least one of aluminum, gallium and scandium, where A is at a dodecahedral site of the garnet, B is at an octahedral site of the garnet, and C is at a tetrahedral site of the garnet. In one embodiment, the rare earth garment has scintillation properties. A radiation detector in one embodiment includes a transparent ceramic as described above and a photo detector optically coupled to the rare earth garnet.

Intracavity frequency doubling of a continuous-wave, diode-laser-pumped neodymium lanthanum scandium borate laser.

PubMed

Meyn, J P; Huber, G

1994-09-15

Neodymium-doped lanthanum scandium borate [Nd:LaSc(3)(BO(3))(4)] is a new material for efficient and compact diode-pumped solid-state lasers. A simple plane-plane 3-mm-long resonator is formed by a coated Nd(10%):LaSc(3)(BO(3))(4) crystal and a coated potassium titanyl phosphate (KTP) crystal. The second-harmonic output power at 531 nm is 522 mW at 2.05-W incident pump power of the diode laser. The corresponding optical efficiency is 25%, and the conversion efficiency from the fundamental to the second harmonic is 55%. The wellknown chaotic power fluctuations of intracavity frequency-doubled lasers (green problem) are avoided by use of a short KTP crystal, between 0.5 and 2 mm in length.

Electronic Structure Properties and a Bonding Model of Thermoelectric Half-Heusler and Boride Phases

NASA Astrophysics Data System (ADS)

Simonson, Jack William

Half-Heusler alloys MNiSn and MCoSb (M = Ti, Zr, Hf) and layered boride intermetallics with structure types YCrB4 and Er 3CrB7 were designed, synthesized, and characterized. The thermoelectric properties of these two classes of alloys were measured from room temperature to 1100 K with the intent of indirectly studying their electronic structure properties and gauging not only their suitability but that of related alloys for high temperature thermoelectric power generation. In the case of the half-Heusler alloys, transition metals were substituted to both the M and Ni/Co sites to study the resultant modifications of the d-orbital-rich portion of the electronic structure near the Fermi energy. This modification and subsequent pinning of the Fermi energy within the gap is discussed herein in terms of first principles electronic structure calculations from the literature. In the half-Heusler alloys, it was found that substitution of transition metals invariably led to a decrease in the thermopower, while the resistivity typically maintained its semiconducting trend. On the other hand, Sn doping in MCoSb type alloys -- a dopant that has been known for some time to be efficient -- was shown to result in high ZT at temperatures in excess of 1000 K. Moreover, the band gaps of the transition metal-doped alloys measured in this work offer insight into the discrepancy between the predicted and measured band gaps in the undoped parent compositions. In the case of the layered boride alloys, on the other hand, few electronic calculations have been published, thus prompting the generalization of a well-known electron counting rule -- which is typically used to study molecular organometallics, boranes, and metallocenes -- to predict the trends in the densities of states of crystalline solids that possess the requisite deltahedral bonding geometry. In accordance with these generalized electronic counting rules, alloys of the form RMB4 (R = Y, Gd, Ho; M = Cr, Mo, W) were measured to be n-type semiconductors with band gaps ranging from 0.15 eV to 0.25 eV. These alloys exhibited thermoelectric power factors comparable with those of other potential boride thermoelectric materials reported in the literature. Furthermore, as a result of the procedure developed for precision synthesis of boron-rich intermetallics and the improved understanding of bonding trends, layered borides of several previously overlooked structure-types were synthesized and screened for superconductivity. Consequently, alloys of the MoB4 phase were discovered to be superconducting when doped with Nb or Ti. Electrical resistivity measurements of superconducting transitions between 6 and 8 K in these materials were confirmed via magnetic susceptibility measurements and x-ray diffraction. Structural measurements indicated opposite trends in lattice modification than those reported for the superconducting transition metal diborides.

NEUTRONIC REACTOR FUEL COMPOSITION

DOEpatents

Thurber, W.C.

1961-01-10

Uranium-aluminum alloys in which boron is homogeneously dispersed by adding it as a nickel boride are described. These compositions have particular utility as fuels for neutronic reactors, boron being present as a burnable poison.

Anomalous stress response of ultrahard WB n compounds

DOE PAGES

Li, Quan; Zhou, Dan; Zheng, Weitao; ...

2015-10-29

Boron-rich tungsten borides are premier prototypes of a new class of ultrahard compounds. Here, we show by first-principles calculations that their stress-strain relations display surprisingly diverse and anomalous behavior under a variety of loading conditions. Most remarkable is the dramatically changing bonding configurations and deformation modes with rising boron concentration in WB n (n=2, 3, 4), resulting in significantly different stress responses and unexpected indentation strength variations. This novel phenomenon stems from the peculiar structural arrangements in tungsten borides driven by boron’s ability to form unusually versatile bonding states. Our results elucidate the intriguing deformation mechanisms that define a distinctmore » type of ultrahard material. Here, these new insights underscore the need to explore unconventional structure-property relations in a broad range of transition-metal light-element compounds.« less

X-Ray photoelectron spectroscopy study of radiofrequency-sputtered titanium, carbide, molybdenum carbide, and titanium boride coatings and their friction properties

NASA Technical Reports Server (NTRS)

Brainard, W. A.; Wheeler, D. R.

1977-01-01

Radiofrequency sputtered coatings of titanium carbide, molybdenum carbide and titanium boride were tested as wear resistant coatings on stainless steel in a pin on disk apparatus. X-ray photoelectron spectroscopy (XPS) was used to analyze the sputtered films with regard to both bulk and interface composition in order to obtain maximum film performance. Significant improvements in friction behavior were obtained when properly biased films were deposited on deliberately preoxidized substrates. XPS depth profile data showed thick graded interfaces for bias deposited films even when adherence was poor. The addition of 10 percent hydrogen to the sputtering gas produced coatings with thin poorly adherent interfaces. Results suggest that some of the common practices in the field of sputtering may be detrimental to achieving maximum adherence and optimum composition for these refractory compounds.

Electronic, structural and magnetic studies of niobium borides of group 8 transition metals, Nb2MB2 (M=Fe, Ru, Os) from first principles calculations

NASA Astrophysics Data System (ADS)

Touzani, Rachid St.; Fokwa, Boniface P. T.

2014-03-01

The Nb2FeB2 phase (U3Si2-type, space group P4/mbm, no. 127) is known for almost 50 years, but until now its magnetic properties have not been investigated. While the synthesis of Nb2OsB2 (space group P4/mnc, no. 128, a twofold superstructure of U3Si2-type) with distorted Nb-layers and Os2-dumbbells was recently achieved, "Nb2RuB2" is still not synthesized and its crystal structure is yet to be revealed. Our first principles density functional theory (DFT) calculations have confirmed not only the experimental structures of Nb2FeB2 and Nb2OsB2, but also predict "Nb2RuB2" to crystalize with the Nb2OsB2 structure type. According to chemical bonding analysis, the homoatomic B-B interactions are optimized and very strong, but relatively strong heteroatomic M-B, B-Nb and M-Nb bonds (M=Fe, Ru, Os) are also found. These interactions, which together build a three-dimensional network, are mainly responsible for the structural stability of these ternary borides. The density-of-states at the Fermi level predicts metallic behavior, as expected, from metal-rich borides. Analysis of possible magnetic structures concluded preferred antiferromagnetic ordering for Nb2FeB2, originating from ferromagnetic interactions within iron chains and antiferromagnetic exchange interactions between them.

Specific features of thermal and magnetic properties of Yb B50 at low temperatures

NASA Astrophysics Data System (ADS)

Novikov, V. V.; Zhemoedov, N. A.; Matovnikov, A. V.; Mitroshenkov, N. V.; Popova, E. A.; Tolstosheev, A. K.; Malkin, B. Z.; Bud'ko, S. L.

2018-05-01

Heat capacity, thermal expansion, and magnetization of ytterbium boride Yb B50 were studied at temperatures 0.6-300 K, 5-300 K, and 2-300 K, respectively. We revealed two smooth peaks at about 4.0 and 60 K in the temperature dependence of the heat capacity. A comparison with the heat capacity of the diamagnetic isostructural boride Lu B50 shows that these anomalies can be attributed to excitations in the ytterbium sublattice (Schottky anomalies). A scheme for splitting of the ground F 7 /2 2 multiplet of Y b3 + ions in the crystal field is proposed. Reliability of the proposed crystal-field energies of the Y b3 + ions is confirmed by the analysis of temperature dependencies of magnetic susceptibility and magnetization in applied magnetic fields up to 55 kOe. A clear anisotropy of the thermal expansion and a negative expansion within a wide temperature range (40-185 K) were observed. Assuming that this anomaly of the thermal expansion in higher borides is caused by the specific thermal evolution of a crystal lattice observed earlier, in particular, in Lu B50 , and the interaction of rare-earth ions with lattice strains, we have determined phenomenological Grüneisen parameters which characterize effects due to thermal transitions of Y b3 + ions between the ground and excited states. A phase transition of Yb B50 to any magnetically ordered state was not observed down to the lowest temperatures of experiments.

Fusion welding of a modern borated stainless steel

DOE Office of Scientific and Technical Information (OSTI.GOV)

Robino, C.V.; Cieslak, M.J.

1997-01-01

Experiments designed to assess the fabrication and service weldability of 304B4A borated stainless steel were conducted. Welding procedures and parameters for manual gas tungsten arc (GTA) welding, autogenous electron beam (EB) welding and filler-added EB welding were developed and found to be similar to those for austenitic stainless steels. Following the procedure development, four test welds were produced and evaluated by microstructural analysis and Charpy impact testing. Further samples were used for determination of the postweld heat treatment (PWHT) response of the welds. The fusion zone structure of welds in this alloy consists of primary austenite dendrites with an interdendriticmore » eutectic-like austenite/boride constituent. Welds also show an appreciable partially molten zone that consists of the austenite/boride eutectic surrounding unmelted austenite islands. The microstructure of the EB welds was substantially finer than that of the GTA welds, and boride coarsening was not observed in the solid state heat-affected zone (HAZ) of either weld type. The impact toughness of as-welded samples was found to be relatively poor, averaging less than 10 J for both GTA and EB welds. For fusion zone notched GTA and EB samples and centerline notched EB samples, fracture generally occurred along the boundary between the partially molten and solid-state regions of the HAZ. The results of the PWHT study were very encouraging, with typical values of the impact energy for HAZ notched samples approaching 40 J, or twice the minimum code-acceptable value.« less

Electron linear accelerator production and purification of scandium-47 from titanium dioxide targets.

PubMed

Rotsch, David A; Brown, M Alex; Nolen, Jerry A; Brossard, Thomas; Henning, Walter F; Chemerisov, Sergey D; Gromov, Roman G; Greene, John

2018-01-01

The photonuclear production of no-carrier-added (NCA) 47 Sc from solid Nat TiO 2 and the subsequent chemical processing and purification have been developed. Scandium-47 was produced by the 48 Ti(γ,p) 47 Sc reaction with Bremsstrahlung photons produced from the braking of electrons in a high-Z (W or Ta) convertor. Production yields were simulated with the PHITS code (Particle and Heavy Ion Transport-code System) and compared to experimental results. Irradiated TiO 2 targets were dissolved in fuming H 2 SO 4 in the presence of Na 2 SO 4 and 47 Sc was purified using the commercially available Eichrom DGA resin. Typical 47 Sc recovery yields were >90% with excellent specific activity for small batches (<185 MBq batches). Copyright © 2017 Elsevier Ltd. All rights reserved.

Electron linear accelerator production and purification of scandium-47 from titanium dioxide targets

DOE PAGES

Rotsch, David A.; Brown, M. Alex; Nolen, Jerry A.; ...

2017-11-06

Here, the photonuclear production of no-carrier-added (NCA) 47Sc from solid NatTiO 2 and the subsequent chemical processing and purification have been developed. Scandium-47 was produced by the 48Ti(γ,p) 47Sc reaction with Bremsstrahlung photons produced from the braking of electrons in a high-Z (W or Ta) convertor. Production yields were simulated with the PHITS code (Particle and Heavy Ion Transport-code System) and compared to experimental results. Irradiated TiO 2 targets were dissolved in fuming H 2SO 4 in the presence of Na 2SO 4 and 47Sc was purified using the commercially available Eichrom DGA resin. Typical 47Sc recovery yields were >90%more » with excellent specific activity for small batches (<185 MBq batches).« less

Electron linear accelerator production and purification of scandium-47 from titanium dioxide targets

DOE Office of Scientific and Technical Information (OSTI.GOV)

Rotsch, David A.; Brown, M. Alex; Nolen, Jerry A.

Here, the photonuclear production of no-carrier-added (NCA) 47Sc from solid NatTiO 2 and the subsequent chemical processing and purification have been developed. Scandium-47 was produced by the 48Ti(γ,p) 47Sc reaction with Bremsstrahlung photons produced from the braking of electrons in a high-Z (W or Ta) convertor. Production yields were simulated with the PHITS code (Particle and Heavy Ion Transport-code System) and compared to experimental results. Irradiated TiO 2 targets were dissolved in fuming H 2SO 4 in the presence of Na 2SO 4 and 47Sc was purified using the commercially available Eichrom DGA resin. Typical 47Sc recovery yields were >90%more » with excellent specific activity for small batches (<185 MBq batches).« less

The physical and mechanical metallurgy of advanced O+BCC titanium alloys

NASA Astrophysics Data System (ADS)

Cowen, Christopher John

This thesis comprises a systematic study of the microstructural evolution, phase transformation behavior, elevated-temperature creep behavior, room-temperature and elevated-temperature tensile behavior, and room-temperature fatigue behavior of advanced titanium-aluminum-niobium (Ti-Al-Nb) alloys with and without boron additions. The specific alloys studied were: Ti-5A1-45Nb (at%), Ti-15Al-33Nb (at%), Ti-15Al-33Nb-0.5B (at%), Ti-15Al-33Nb-5B (at%), Ti-21Al-29Nb (at%), Ti-22Al-26Nb (at%), and Ti-22Al-26Nb-5B (at%). The only alloy composition that had been previously studied before this thesis work began was Ti-22Al-26Nb (at%). Publication in peer-reviewed material science journals of the work performed in this thesis has made data available in the scientific literature that was previously non-existent. The knowledge gap for Ti-Al-Nb phase equilibria over the compositional range of Ti-23Al-27Nb (at%) to Ti-12Al-38Nb (at%) that existed before this work began was successfully filled. The addition of 5 at% boron to the Ti-15Al-33Nb alloy produced 5-9 volume percent boride phase needles within the microstructure. The chemical composition of the boride phase measured by electron microprobe was determined to be approximately B 2TiNb. The lattice parameters of the boride phase were simulated through density functional theory calculations by collaborators at the Air Force Research Laboratory based on the measured composition. Using the simulated lattice parameters, electron backscatter diffraction kikuchi patterns and selected area electron diffraction patterns obtained from the boride phase were successfully indexed according to the space group and site occupancies of the B27 orthorhombic crystal structure. This suggests that half the Ti (c) Wyckoff positions are occupied by Ti atoms and the other half are occupied by Nb atoms in the boride phase lattice. Creep deformation behavior is the main focus of this thesis and in particular understanding the dominant creep deformation mechanisms as a function of stress, temperature, and strain rate. Microstructure-creep relationships for Ti-Al-Nb-xB alloys were developed with the understanding gained. A rule-of-mixtures empirical model based on constituent phase volume fractions and strain rates was developed to predict the minimum creep rates of two-phase O+BCC microstructures. The most innovative results of this thesis were produced through the development of an in-situ creep testing methodology. The creep deformation evolution was chronicled in-situ during high temperature creep experiments, while creep displacement versus time data was simultaneously obtained. The in-situ experiments revealed that prior-BCC grain boundaries were the locus of damage accumulation during creep deformation. A methodology that allows in-situ observation of surface creep deformation as a function of creep displacement has yet to be presented in the literature.

Scandium Terminal Imido Chemistry.

PubMed

Lu, Erli; Chu, Jiaxiang; Chen, Yaofeng

2018-02-20

Research into transition metal complexes bearing multiply bonded main-group ligands has developed into a thriving and fruitful field over the past half century. These complexes, featuring terminal M═E/M≡E (M = transition metal; E = main-group element) multiple bonds, exhibit unique structural properties as well as rich reactivity, which render them attractive targets for inorganic/organometallic chemists as well as indispensable tools for organic/catalytic chemists. This fact has been highlighted by their widespread applications in organic synthesis, for example, as olefin metathesis catalysts. In the ongoing renaissance of transition metal-ligand multiple-bonding chemistry, there have been reports of M═E/M≡E interactions for the majority of the metallic elements of the periodic table, even some actinide metals. In stark contrast, the largest subgroup of the periodic table, rare-earth metals (Ln = Sc, Y, and lanthanides), have been excluded from this upsurge. Indeed, the synthesis of terminal Ln═E/Ln≡E multiple-bonding species lagged behind that of the transition metal and actinide congeners for decades. Although these species had been pursued since the discovery of a rare-earth metal bridging imide in 1991, such a terminal (nonpincer/bridging hapticities) Ln═E/Ln≡E bond species was not obtained until 2010. The scarcity is mainly attributed to the energy mismatch between the frontier orbitals of the metal and the ligand atoms. This renders the putative terminal Ln═E/Ln≡E bonds extremely reactive, thus resulting in the formation of aggregates and/or reaction with the ligand/environment, quenching the multiple-bond character. In 2010, the stalemate was broken by the isolation and structural characterization of the first rare-earth metal terminal imide-a scandium terminal imide-by our group. The double-bond character of the Sc═N bond was unequivocally confirmed by single-crystal X-ray diffraction. Theoretical investigations revealed the presence of two p-d π bonds between the scandium ion and the nitrogen atom of the imido ligand and showed that the dianionic [NR] 2- imido ligand acts as a 2σ,4π electron donor. Subsequent studies of the scandium terminal imides revealed highly versatile and intriguing reactivity of the Sc═N bond. This included cycloaddition toward various unsaturated bonds, C-H/Si-H/B-H bond activations and catalytic hydrosilylation, dehydrofluorination of fluoro-substituted benzenes/alkanes, CO 2 and H 2 activations, activation of elemental selenium, coordination with other transition metal halides, etc. Since our initial success in 2010, and with contributions from us and across the community, this young, vibrant research field has rapidly flourished into one of the most active frontiers of rare-earth metal chemistry. The prospect of extending Ln═N chemistry to other rare-earth metals and/or different metal oxidation states, as well as exploiting their stoichiometric and catalytic reactivities, continues to attract research effort. Herein we present an account of our investigations into scandium terminal imido chemistry as a timely summary, in the hope that our studies will be of interest to this readership.

Formal Synthesis of (±)-Roseophilin

PubMed Central

Bitar, Abdallah Y.; Frontier, Alison J.

2009-01-01

A formal synthesis of (±)-roseophilin is described. Scandium(III)-catalyzed Nazarov cyclization of 2,5-disubstituted N-tosylpyrrole 19 gives a 5,5’-fused ketopyrrole, and ansa-bridge formation via π-allyl palladium macrocyclization gives 21. PMID:19053717

Magnetism and structural chemistry of ternary borides RE2MB 6 ( RE = rare earth, M = Ru, Os)

NASA Astrophysics Data System (ADS)

Hiebl, K.; Rogl, P.; Nowotny, H.

1984-10-01

The magnetic behavior of the ternary borides RE2RuB 6 and RE2OsB 6 ( RE = Y, Gd, Tb, Dy, Ho, Er, Tm, Yb, Lu) was studied in the temperature range 1.5 K < T < 1100 K. All compounds crystallize with the Y 2ReB 6-type structure and are characterized by direct RE- RE contacts and the formation of planar infinite two-dimensional rigid boron nets. The magnetic properties reveal a typical Van Vleck paramagnetism of free RE3+-ions at temperatures higher than 200 K with ferromagnetic interaction in the low-temperature range T < 55 K. The ferromagnetic ordering temperatures vary with the De Gennes factor. There is no indication for a magnetic contribution from the Ru(Os)-sublattice. Above 1.8 K none of the samples were found to be superconducting.

Electronic structure and mechanical properties of osmium borides, carbides and nitrides from first principles

NASA Astrophysics Data System (ADS)

Liang, Yongcheng; Zhao, Jianzhi; Zhang, Bin

2008-06-01

The stabilities, mechanical properties and electronic structures of osmium boride (OsB), carbide (OsC) and nitride (OsN), in the tungsten carbide (WC), rocksalt (NaCl), cesium chloride (CsCl) and zinc blende (ZnS) structures respectively, are systematically predicted by calculations from first-principles. Only four phases, namely, OsB(WC), OsB(CsCl), OsC(WC), and OsC(ZnS), are mechanically stable, and none is a superhard compound, contrary to previous speculation. Most importantly, we find that the changing trends of bulk modulus and shear modulus are completely different for OsB, OsC and OsN in same hexagonal WC structure, which indicates that the underlying sources of hardness and incompressibility are fundamentally different: the former is determined by bonding nature while the latter is closely associated with valence electron density.

The Influence of Nano-Scale Silicon Nitride Additions on the Physical and Magnetic Properties of Iron Sheathed Magnesium Boride Wires

NASA Astrophysics Data System (ADS)

Zhu, W.; Cave, J.

2006-03-01

The enhancement of flux line pinning in magnesium boride wires is a critical issue for their future applications in devices and machines. It is well known that small size dopants can significantly influence the current densities of these materials. Here, the influence of nanometric (<30nm) silicon nitride on physical properties and current density is presented. The iron-sheathed powder in tube wires were prepared using pure magnesium and boron powders with silicon nitride additions. The wires were rolled flat and treated at up to 900 degrees C in flowing argon. SEM and XRD were used to identify phases and microstructures. Magnetization critical currents, up to several 100 of thousands A/cm2, at various temperatures and fields (5K - 20K and up to 3 tesla) show that there are competing mechanisms from chemical and flux pinning effects.

Magnetic and magnetothermal studies of iron boride (FeB) nanoparticles

NASA Astrophysics Data System (ADS)

Hamayun, M. Asif; Abramchuk, Mykola; Alnasir, Hisham; Khan, Mohsin; Pak, Chongin; Lenhert, Steven; Ghazanfari, Lida; Shatruk, Michael; Manzoor, Sadia

2018-04-01

We report magnetic and magnetothermal properties of iron boride (FeB) nanoparticles prepared by surfactant-assisted ball milling of arc-melted bulk ingots of this binary alloy. Size-dependent magnetic properties were used to identify the transition to the single domain limit and calculate the anisotropy and exchange stiffness constants for this system. Extended milling is seen to produce coercivity enhancement and exchange bias of up to 270 Ôe at room temperature. The magnetothermal properties were investigated by measuring the response of single domain FeB nanoparticles to externally applied ac magnetic fields. All investigated particle sizes show a significant heating response, demonstrating their potential as candidates for magnetically induced hyperthermia. FeB nanoparticles were encapsulated into lipophilic domains of liposomes as evidenced by TEM. Exposure of HeLa cells to these liposomes did not affect cell viability, suggesting the biocompatibility of these new magnetic nanomaterials.

Identification of delamination failure of boride layer on common Cr-based steels

NASA Astrophysics Data System (ADS)

Taktak, Sukru; Tasgetiren, Suleyman

2006-10-01

Adhesion is an important aspect in the reliability of coated components. With low-adhesion of interfaces, different crack paths may develop depending on the local stress field at the interface and the fracture toughness of the coating, substrate, and interface. In the current study, an attempt has been made to identify the delamination failure of coated Cr-based steels by boronizing. For this reason, two commonly used steels (AISI H13, AISI 304) are considered. The steels contain 5.3 and 18.3 wt.% Cr, respectively. Boriding treatment is carried out in a slurry salt bath consisting of borax, boric acid, and ferrosilicon at a temperature range of 800 950 °C for 3, 5, and 7 h. The general properties of the boron coating are obtained by mechanical and metallographic characterization tests. For identification of coating layer failure, some fracture toughness tests and the Daimler-Benz Rockwell-C adhesion test are used.

Investigation of concentration-dependence of thermodynamic properties of lanthanum, yttrium, scandium and terbium in eutectic LiCl-KCl molten salt

NASA Astrophysics Data System (ADS)

Wang, Yafei; Zhou, Wentao; Zhang, Jinsuo

2016-09-01

Thermodynamic properties of rare earth metals in LiCl-KCl molten salt electrolyte are crucial to the development of electrochemical separation for the treatment of used nuclear fuels. In the present study, activity coefficient, apparent potential, and diffusion coefficient of lanthanum, yttrium, scandium, and terbium in the molten salt (58 at% LiCl and 42 at% KCl) were calculated by the method of molecular dynamics simulation up to a concentration around 3 at% at temperatures of 723 K and 773 K. It was found that the activity coefficient and the apparent potential increase with the species concentration while diffusion coefficient shows a trend of increase followed by decrease. The calculated results were validated by available measurement data of dilution cases. This research extends the range of data to a wide component and would provide further insight to the pyroprocessing design and safeguards.

Improvement in the Shape Memory Response of Ti50.5Ni24.5Pd25 High-Temperature Shape Memory Alloy with Scandium Microalloying

NASA Technical Reports Server (NTRS)

Atli, K. C.; Karaman, I; Noebe, R. D.; Garg, A.; Chumlyakov, Y. I.; Kireeva, I. V.

2010-01-01

A Ti(50.5)Ni(24.5)Pd25 high-temperature shape memory alloy (HTSMA) is microalloyed with 0.5 at. pct scandium (Sc) to enhance its shape-memory characteristics, in particular, dimensional stability under repeated thermomechanical cycles. For both Ti(50.5)Ni(24.5)Pd25 and the Sc-alloyed material, differential scanning calorimetry is conducted for multiple cycles to characterize cyclic stability of the transformation temperatures. The microstructure is evaluated using electron microscopy, X-ray diffractometry, and wavelength dispersive spectroscopy. Isobaric thermal cycling experiments are used to determine transformation temperatures, dimensional stability, and work output as a function of stress. The Sc-doped alloy displays more stable shape memory response with smaller irrecoverable strain and narrower thermal hysteresis than the baseline ternary alloy. This improvement in performance is attributed to the solid solution hardening effect of Sc.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Radchenko, Valery; Meyer, Catherine Anne Louise; Engle, Jonathan Ward

Scandium-44 g (half-life 3.97 h) shows promise for positron emission tomography (PET) imaging of longer biological processes than that of the current gold standard, 18F, due to its favorable decay parameters. One source of 44gSc is the long-lived parent nuclide 44Ti (half-life 60.0 a). A 44Ti/ 44gSc generator would have the ability to provide radionuclidically pure 44gSc on a daily basis. The production of 44Ti via the 45Sc(p,2n) reaction requires high proton beam currents and long irradiation times. Recovery and purification of no-carrier added (nca) 44Ti from scandium metal targets involves complex separation chemistry. In this study, separation systems basedmore » on solid phase extraction chromatography were investigated, including branched diglycolamide (BDGA) resin and hydroxamate based ZR resin. Lastly, results indicate that ZR resin in HCl media represents an effective 44Ti/ 44gSc separation system.« less

Investigation of ionic transport in sodium scandium phosphate (NSP) and related compounds

NASA Astrophysics Data System (ADS)

Bhat, Kaustubh; Blügel, Stefan; Lustfeld, Hans

Sodium ionic conductors offer significant advantages for application in large scale energy storage systems. In this study, we investigate the different pathways available for sodium ion conduction in NSP and calculate energy barriers for ionic transport using Density Functional Theory (DFT) and the Nudged Elastic Band Method. We identify the structural parameters that reduce the energy barrier, by calculating the influence of positive and negative external pressure on the energy barrier. Lattice strain can be introduced by cation or anion substitution within the NASICON structure. We substitute the scandium atom with other trivalent atoms such as aluminium and yttrium, and calculate the resulting energy barriers. Sodium thiophosphate (Na3PS4) has previously shown about two orders of magnitude higher ionic conductivity than sodium phosphate (Na3PO4). We investigate the effect of substituting oxygen with sulphur in NSP. We acknowledge discussions with our experimental colleagues F. Tietz and M. Guin toward this work

Reducing the stochasticity of crystal nucleation to enable subnanosecond memory writing

NASA Astrophysics Data System (ADS)

Rao, Feng; Ding, Keyuan; Zhou, Yuxing; Zheng, Yonghui; Xia, Mengjiao; Lv, Shilong; Song, Zhitang; Feng, Songlin; Ronneberger, Ider; Mazzarello, Riccardo; Zhang, Wei; Ma, Evan

2017-12-01

Operation speed is a key challenge in phase-change random-access memory (PCRAM) technology, especially for achieving subnanosecond high-speed cache memory. Commercialized PCRAM products are limited by the tens of nanoseconds writing speed, originating from the stochastic crystal nucleation during the crystallization of amorphous germanium antimony telluride (Ge2Sb2Te5). Here, we demonstrate an alloying strategy to speed up the crystallization kinetics. The scandium antimony telluride (Sc0.2Sb2Te3) compound that we designed allows a writing speed of only 700 picoseconds without preprogramming in a large conventional PCRAM device. This ultrafast crystallization stems from the reduced stochasticity of nucleation through geometrically matched and robust scandium telluride (ScTe) chemical bonds that stabilize crystal precursors in the amorphous state. Controlling nucleation through alloy design paves the way for the development of cache-type PCRAM technology to boost the working efficiency of computing systems.

Effect of Discharge Time on Plasma Electrolytic Borocarbonitriding of Pure Iron

NASA Astrophysics Data System (ADS)

Jin, Xiaoyue; Wu, Jie; Wang, Bin; Yang, Xuan; Chen, Lin; Qu, Yao; Xue, Wenbin

The plasma electrolytic borocarbonitriding (PEB/C/N) process on pure iron was carried out in 25% borax solution with glycerine and carbamide additives under different discharge time at 360V. The morphology and structure of PEB/C/N hardened layers were analyzed by SEM and XRD. The hardness profiles of hardened layers were measured by microhardness test. Corrosion behavior of PEB/C/N layers was evaluated by potentiodynamic polarization and electrochemical impedance spectroscopy (EIS). Their wear performance was carried out using a pin-disc friction and wear tester under dry sliding test. The PEB/C/N samples mainly consisted of α-Fe, Fe2B, Fe3C, FeN, FeB, Fe2O3 and Fe4N phases, and the Fe2B phase was the dominant phase in the boride layer. It was found that the thickness of boride layer increased with the discharge time and reached 14μm after 60min treatment. The microhardness of the boride layer was up to 2100HV, which was much higher than that of the bare pure iron (about 150HV). After PEB/C/N treatment, the corrosion resistance of pure iron was slightly improved. The friction coefficient of PEB/C/N treated pure iron decreased to 0.129 from 0.556 of pure iron substrate. The wear rate of the PEB/C/N layer after 60min under dry sliding against ZrO2 ball was only 1/10 of that of the bare pure iron. The PEB/C/N treatment is an effective way to improve the wear behavior of pure iron.

Correlation between structural stability of LiBH4 and cation electronegativity in metal borides: an experimental insight for catalyst design.

PubMed

Cai, Weitong; Yang, Yuanzheng; Tao, Pingjun; Ouyang, Liuzhang; Wang, Hui

2018-04-03

Nanosized metal borides MBx (M = Mg, Ti, Fe, Si) are found to play an important role in enhancing the hydrogen storage performance of LiBH4 in this work. The hydrogen storage behavior and mechanism of these modified systems are investigated through TPD-MS, XRD, FTIR and SEM characterization methods. By introducing these metal borides into LiBH4 through ball milling, the systems display three dehydrogenation stages disclosing their similarity and distinction. The 1st stage starts at 190 °C, the 2nd stage ranges from 280 °C to 400 °C and the 3rd stage ends at 550 °C with a peak at round 440 °C similar to that of pristine LiBH4. Distinguishing features exist at the 2nd stage revealing the effectiveness of MBx in an order of MgB2 < TiB2 < FeB < SiB4. Significantly, reversibility up to 9.7 wt% is achieved from LiBH4 with assistance of SiB4. The catalytic effect of MBx is influenced by the Pauling electronegativity of M in MBx and the interfacial contact characteristic between LiBH4 and MBx. The larger electronegativity leads to an enhanced catalytic effect and consequently lower temperature at the major stage. In contrast to the components in the solid state, the molten LiBH4 promotes a catalytic effect due to a superior interfacial contact. These results provide an insight into designing high-performance catalysts applied to LiBH4 as a hydrogen storage material.

Boron-Based Hydrogen Storage: Ternary Borides and Beyond

DOE Office of Scientific and Technical Information (OSTI.GOV)

Vajo, John J.

DOE continues to seek reversible solid-state hydrogen materials with hydrogen densities of ≥11 wt% and ≥80 g/L that can deliver hydrogen and be recharged at moderate temperatures (≤100 °C) and pressures (≤100 bar) enabling incorporation into hydrogen storage systems suitable for transportation applications. Boron-based hydrogen storage materials have the potential to meet the density requirements given boron’s low atomic weight, high chemical valance, and versatile chemistry. However, the rates of hydrogen exchange in boron-based compounds are thus far much too slow for practical applications. Although contributing to the high hydrogen densities, the high valance of boron also leads to slowmore » rates of hydrogen exchange due to extensive boron-boron atom rearrangements during hydrogen cycling. This rearrangement often leads to multiple solid phases occurring over hydrogen release and recharge cycles. These phases must nucleate and react with each other across solid-solid phase boundaries leading to energy barriers that slow the rates of hydrogen exchange. This project sought to overcome the slow rates of hydrogen exchange in boron-based hydrogen storage materials by minimizing the number of solid phases and the boron atom rearrangement over a hydrogen release and recharge cycle. Two novel approaches were explored: 1) developing matched pairs of ternary borides and mixed-metal borohydrides that could exchange hydrogen with only one hydrogenated phase (the mixed-metal borohydride) and only one dehydrogenated phase (the ternary boride); and 2) developing boranes that could release hydrogen by being lithiated using lithium hydride with no boron-boron atom rearrangement.« less

DOE Office of Scientific and Technical Information (OSTI.GOV)

Sitler, Steven J.; Raja, Krishnan S.; Charit, Indrajit

Solid solutions of HfB 2-ZrB 2 mixtures were prepared by high-energy ball milling of diboride and additive powders followed by spark plasma sintering (SPS). A mixture of stoichiometric 1:1 HfB 2-ZrB 2 borides was the base composition to which Hf, Zr, Ta, LaB 6 or Gd 2O 3 was added. Hf, Zr and Ta were added in order to bring the boron-to-metal ratio down to 1.86, rendering the boride as MeB 1.86. In the case of LaB 6 and Gd 2O 3, 1.8 mol% was added. Electroanalytical behavior of hydrogen evolution reactions was evaluated in 1 M H 2SO 4more » and 1 M NaOH solutions. The LaB 6 additive material showed Tafel slopes of 125 and 90 mV/decade in acidic and alkaline solutions respectively. The Hf and Zr rich samples showed Tafel slopes of about 120 mV/decade in both electrolytes. The over potentials of hydrogen evolution reactions (at 10 mA/cm 2) in the alkaline solution were about 100 mV lower than those in acidic solution. The metal-rich diborides and addition of LaB 6 showed better hydrogen evolution reaction (HER) activities than the base 1:1 HfB 2-ZrB 2 stoichiometric diboride solid solution. Furthermore, the higher activity of metal-rich borides could be attributed to the increased electron population at the d-orbitals of the metal shown by band structure modeling calculations using the Density Functional Theory approach.« less

Photovoltaic cell

DOEpatents

Gordon, Roy G.; Kurtz, Sarah

1984-11-27

In a photovoltaic cell structure containing a visibly transparent, electrically conductive first layer of metal oxide, and a light-absorbing semiconductive photovoltaic second layer, the improvement comprising a thin layer of transition metal nitride, carbide or boride interposed between said first and second layers.

Unusual Metals in Galactic Center Stars

NASA Astrophysics Data System (ADS)

Hensley, Kerry

2018-03-01

Far from the galactic suburbs where the Sun resides, a cluster of stars in the nucleus of the Milky Way orbits a supermassive black hole. Can chemical abundance measurements help us understand the formation history of the galactic center nuclear star cluster?Studying Stellar PopulationsMetallicity distributions for stars in the inner two degrees of the Milky Way (blue) and the central parsec (orange). [Do et al. 2018]While many galaxies host nuclear star clusters, most are too distant for us to study in detail; only in the Milky Way can we resolve individual stars within one parsec of a supermassive black hole. The nucleus of our galaxy is an exotic and dangerous place, and its not yet clear how these stars came to be where they are were they siphoned off from other parts of the galaxy, or did they form in place, in an environment rocked by tidal forces?Studying the chemical abundances of stars provides a way to separate distinct stellar populations and discern when and where these stars formed. Previous studies using medium-resolution spectroscopy have revealed that many stars within the central parsec of our galaxy have very high metallicities possibly higher than any other region of the Milky Way. Can high-resolution spectroscopy tell us more about this unusual population of stars?Spectral Lines on DisplayTuan Do (University of California, Los Angeles, Galactic Center Group) and collaborators performed high-resolution spectroscopic observations of two late-type giant starslocated half a parsec from the Milky Ways supermassive black hole.Comparison of the observed spectra of the two galactic center stars (black) with synthetic spectra with low (blue) and high (orange) [Sc/Fe] values. Click to enlarge. [Do et al. 2018]In order to constrain the metallicities of these stars, Do and collaborators compared the observed spectra to a grid of synthetic spectra and used a spectral synthesis technique to determine the abundances of individual elements. They found that while one star is only slightly above solar metallicity, the other is likely more than four times as metal-rich as the Sun.The features in the observed and synthetic spectra generally matched well, but the absorption lines of scandium, vanadium, and yttrium were consistently stronger in the observed spectra than in the synthetic spectra. This led the authors to conclude that these galactic center stars are unusually rich in these metals trace elements that could reveal the formation history of the galactic nucleus.Old Stars, New Trends?Scandium to iron ratio versusiron abundance for stars in the disk of the Milky Way (blue) and the stars in this sample (orange). The value reported for this sample is a 95% lower limit. [Do et al. 2018]For stars in the disk of the Milky Way, the abundance of scandium relative to iron tends to decrease as the overall metallicity increases, but the stars investigated in this study are both iron-rich and anomalously high in scandium. This hints that the nuclear star cluster might represent a distinct stellar population with different metallicity trends.However, its not yet clear what could cause the elevated abundances of scandium, vanadium, and yttrium relative to other metals. Each of these elements is linked to a different source; scandium and vanadium are mainly produced in Type II and Type Ia supernovae, respectively, while yttrium is likely synthesized in asymptotic giant branch stars. Future observations of stars near the center of the Milky Way may help answer this question and further constrain the origin of our galaxys nuclear star cluster.CitationTuan Do et al 2018 ApJL 855 L5. doi:10.3847/2041-8213/aaaec3

LEWIS ACID CATALYZED FORMATION OF TETRAHYDROPYRANS IN IONIC LIQUID

EPA Science Inventory

Tetrahydropyrans are integral moieties in innumerable natural products and have inspired the development of a variety of different methodologies. A Prins-type cyclization involving the coupling of a homoallylic alcohol and an aldehyde in the presence of catalytic scandium triflat...

DFT investigations of hydrogen storage materials

NASA Astrophysics Data System (ADS)

Wang, Gang

Hydrogen serves as a promising new energy source having no pollution and abundant on earth. However the most difficult problem of applying hydrogen is to store it effectively and safely, which is smartly resolved by attempting to keep hydrogen in some metal hydrides to reach a high hydrogen density in a safe way. There are several promising metal hydrides, the thermodynamic and chemical properties of which are to be investigated in this dissertation. Sodium alanate (NaAlH4) is one of the promising metal hydrides with high hydrogen storage capacity around 7.4 wt. % and relatively low decomposition temperature of around 100 °C with proper catalyst. Sodium hydride is a product of the decomposition of NaAlH4 that may affect the dynamics of NaAlH4. The two materials with oxygen contamination such as OH- may influence the kinetics of the dehydriding/rehydriding processes. Thus the solid solubility of OH - groups (NaOH) in NaAlH4 and NaH is studied theoretically by DFT calculations. Magnesium boride [Mg(BH4)2] is has higher hydrogen capacity about 14.9 wt. % and the decomposition temparture of around 250 °C. However one flaw restraining its application is that some polyboron compounds like MgB12H12 preventing from further release of hydrogen. Adding some transition metals that form magnesium transition metal ternary borohydride [MgaTMb(BH4)c] may simply the decomposition process to release hydrogen with ternary borides (MgaTMbBc). The search for the probable ternary borides and the corresponding pseudo phase diagrams as well as the decomposition thermodynamics are performed using DFT calculations and GCLP method to present some possible candidates.

Metallic Borides, La 2 Re 3 B 7 and La 3 Re 2 B 5 , Featuring Extensive Boron–Boron Bonding

DOE Office of Scientific and Technical Information (OSTI.GOV)

Bugaris, Daniel E.; Malliakas, Christos D.; Chung, Duck Young

We synthesized La 2Re 3B 7 and La 3Re 2B 5 in single-crystalline form from a molten La/Ni eutectic at 1000°C, in the first example of the flux crystal growth of ternary rare-earth rhenium borides. Both compounds crystallize in their own orthorhombic structure types, with La 2Re 3B 7 (space group Pcca) having lattice parameters a = 7.657(2) Å, b = 6.755(1) Å, and c = 11.617(2) Å, and La 3Re 2B 5 (space group Pmma) having lattice parameters a = 10.809(2) Å, b = 5.287(1) Å, and c = 5.747(1) Å. Furthermore, the compounds possess three-dimensional framework structures thatmore » are built up from rhenium boride polyhedra and boron-boron bonding. La 3Re 2B 5 features fairly common B 2 dumbbells, whereas La 2Re 3B 7 has unique one-dimensional subunits composed of alternating triangular B3 and trans-B4 zigzag chain fragments. Also observed in La 3Re 2B 5 is an unusual coordination of B by an octahedron of La atoms. Electronic band structure calculations predict that La 2Re 3B 7 is a semimetal, which is observed in the electrical resistivity data as measured on single crystals, with behavior obeying the Bloch-Grüneisen model and a room-temperature resistivity ρ300K of ~ 375 μΩ cm. The electronic band structure calculations also suggest that La 3Re 2B 5 is a regular metal.« less

Metallic Borides, La 2 Re 3 B 7 and La 3 Re 2 B 5 , Featuring Extensive Boron–Boron Bonding

DOE PAGES

Bugaris, Daniel E.; Malliakas, Christos D.; Chung, Duck Young; ...

2016-01-26

We synthesized La 2Re 3B 7 and La 3Re 2B 5 in single-crystalline form from a molten La/Ni eutectic at 1000°C, in the first example of the flux crystal growth of ternary rare-earth rhenium borides. Both compounds crystallize in their own orthorhombic structure types, with La 2Re 3B 7 (space group Pcca) having lattice parameters a = 7.657(2) Å, b = 6.755(1) Å, and c = 11.617(2) Å, and La 3Re 2B 5 (space group Pmma) having lattice parameters a = 10.809(2) Å, b = 5.287(1) Å, and c = 5.747(1) Å. Furthermore, the compounds possess three-dimensional framework structures thatmore » are built up from rhenium boride polyhedra and boron-boron bonding. La 3Re 2B 5 features fairly common B 2 dumbbells, whereas La 2Re 3B 7 has unique one-dimensional subunits composed of alternating triangular B3 and trans-B4 zigzag chain fragments. Also observed in La 3Re 2B 5 is an unusual coordination of B by an octahedron of La atoms. Electronic band structure calculations predict that La 2Re 3B 7 is a semimetal, which is observed in the electrical resistivity data as measured on single crystals, with behavior obeying the Bloch-Grüneisen model and a room-temperature resistivity ρ300K of ~ 375 μΩ cm. The electronic band structure calculations also suggest that La 3Re 2B 5 is a regular metal.« less

Metal-Rich Transition Metal Diborides as Electrocatalysts for Hydrogen Evolution Reactions in a Wide Range of pH

DOE PAGES

Sitler, Steven J.; Raja, Krishnan S.; Charit, Indrajit

2016-09-23

Solid solutions of HfB 2-ZrB 2 mixtures were prepared by high-energy ball milling of diboride and additive powders followed by spark plasma sintering (SPS). A mixture of stoichiometric 1:1 HfB 2-ZrB 2 borides was the base composition to which Hf, Zr, Ta, LaB 6 or Gd 2O 3 was added. Hf, Zr and Ta were added in order to bring the boron-to-metal ratio down to 1.86, rendering the boride as MeB 1.86. In the case of LaB 6 and Gd 2O 3, 1.8 mol% was added. Electroanalytical behavior of hydrogen evolution reactions was evaluated in 1 M H 2SO 4more » and 1 M NaOH solutions. The LaB 6 additive material showed Tafel slopes of 125 and 90 mV/decade in acidic and alkaline solutions respectively. The Hf and Zr rich samples showed Tafel slopes of about 120 mV/decade in both electrolytes. The over potentials of hydrogen evolution reactions (at 10 mA/cm 2) in the alkaline solution were about 100 mV lower than those in acidic solution. The metal-rich diborides and addition of LaB 6 showed better hydrogen evolution reaction (HER) activities than the base 1:1 HfB 2-ZrB 2 stoichiometric diboride solid solution. Furthermore, the higher activity of metal-rich borides could be attributed to the increased electron population at the d-orbitals of the metal shown by band structure modeling calculations using the Density Functional Theory approach.« less

Thermal properties of zirconium diboride -- transition metal boride solid solutions

NASA Astrophysics Data System (ADS)

McClane, Devon Lee

This research focuses on the thermal properties of zirconium diboride (ZrB2) based ceramics. The overall goal was to improve the understanding of how different transition metal (TM) additives influence thermal transport in ZrB2. To achieve this, ZrB2 with 0.5 wt% carbon, and 3 mol% of individual transition metal borides, was densified by hot-press sintering. The transition metals that were investigated were: Y, Ti, Hf, V, Nb, Ta, Cr, Mo, W, and Re. The room temperature thermal diffusivities of the compositions ranged from 0.331 cm2/s for nominally pure ZrB2 to 0.105 cm2/s for (Zr,Cr)B2 and converged around 0.155cm2/s at higher temperatures for all compositions. Thermal conductivities were calculated from the diffusivities, using temperature-dependent values for density and heat capacity. The electron contribution to thermal conductivity was calculated from measured electrical resistivity according to the Wiedemann-Franz law. The phonon contribution to thermal conductivity was calculated by subtracting the electron contribution from the total thermal conductivity. Rietveld refinement of x-ray diffraction data was used to determine the lattice parameters of the compositions. The decrease in thermal conductivity for individual additives correlated directly to the metallic radius of the additive. Additional strain appeared to exist for additives when the stable TM boride for that metal had different crystal symmetries than ZrB2. This research provided insight into how additives and impurities affect thermal transport in ZrB2. The research potentially offers a basis for future modeling of thermal conductivity in ultra-high temperature ceramics based on the correlation between metallic radius and the decrease in thermal conductivity.

Molecular Line Lists for Scandium and Titanium Hydride Using the DUO Program

NASA Astrophysics Data System (ADS)

Lodi, Lorenzo; Yurchenko, Sergei N.; Tennyson, Jonathan

2015-06-01

Transition-metal-containing (TMC) molecules often have very complex electronic spectra because of their large number of low-lying, interacting electronic states, of the large multi-reference character of the electronic states and of the large magnitude of spin-orbit and relativistic effects. As a result, fully ab initio calculations of line positions and intensities of TMC molecules have an accuracy which is considerably worse than the one usually achievable for molecules made up by main-group atoms only. In this presentation we report on new theoretical line lists for scandium hydride ScH and titanium hydride TiH. Scandium and titanium are the lightest transition metal atoms and by virtue of their small number of valence electrons are amenable to high-level electronic-structure treatments and serve as ideal benchmark systems. We report for both systems energy curves, dipole curves and various coupling curves (including spin-orbit) characterising their electronic spectra up to about 20 000 cm-1. Curves were obtained using Internally-Contracted Multi Reference Configuration Interaction (IC-MRCI) as implemented in the quantum chemistry package MOLPRO. The curves where used for the solution of the coupled-surface ro-vibronic problem using the in-house program DUO. DUO is a newly-developed, general program for the spectroscopy of diatomic molecules and its main functionality will be described. The resulting line lists for ScH and TiH are made available as part of the Exomol project. L. Lodi, S. N. Yurchenko and J. Tennyson, Mol. Phys. (Handy special issue) in press. S. N. Yurchenko, L. Lodi, J. Tennyson and A. V. Stolyarov, Computer Phys. Comms., to be submitted.

Insights into the mantle geochemistry of scandium from a meta-analysis of garnet data

NASA Astrophysics Data System (ADS)

Chassé, Mathieu; Griffin, William L.; Alard, Olivier; O'Reilly, Suzanne Y.; Calas, Georges

2018-06-01

The meta-analysis of about 13,000 analyses of scandium content in garnet grains shows that, below the spinel-garnet transition, this phase carries about three-quarters of the Sc budget of the mantle, indicating its control on Sc mobility. The Sc content of garnets in mafic rocks is low, due to a dilution effect resulting from their high modal content in garnet. Garnets from ultramafic rocks exhibit a wider range of Sc concentrations. We assess the relative influence of thermobarometry, crystal chemistry and fluid-related events on the distribution of Sc in garnet from such rocks to improve the tracking of geochemical processes in the mantle. Pressure and temperature of equilibration in the mantle are second-order factors influencing the Sc content of garnet, while crystal chemistry, in particular Cr/Cr+Al and Ca/Ca+Mg, is the main parameter controlling the compatibility of Sc. Scandium is incorporated in both X and Y sites of Cr-Ca-rich garnets, resulting in a behaviour intermediate between rare-earth elements, incorporated in the X site, and trivalent transition elements, occupying the Y site. This affinity for both sites results in a mild compatibility of Sc in the garnet stability field of the mantle; hence Sc concentration in garnet increases with melt extraction and can be reduced by silicate-melt metasomatism. In contrast, metasomatism by volatile-rich fluids increases the Sc concentration in garnet. The control of garnet on the compatibility of Sc in deep lithospheric rocks demonstrates the potential of using Sc to track the conditions of formation of magmas and their residual rocks, as well as the origin and nature of metasomatic fluids.

Luminescence behaviour and deposition of Sc2O3 thin films from scandium(III) acetylacetonate at ambient pressure

NASA Astrophysics Data System (ADS)

Dixon, Sebastian C.; Jiamprasertboon, Arreerat; Carmalt, Claire J.; Parkin, Ivan P.

2018-05-01

Scandium(III) oxide thin film deposition has been historically difficult to achieve without the use of vacuum-based or wet chemical systems due to precursor limitations of low vapour pressure or ambient instability. In this letter, the adoption of aerosol-assisted delivery of scandium(III) acetylacetonate has enabled the chemical vapour deposition of polycrystalline and amorphous Sc2O3 thin films at ambient pressure with high growth rates (ca. 500 nm h-1). The scandia films were intrinsically highly photoluminescent, exhibiting broad emission bands centred at 3.6 and 3.0 eV, which increased significantly in intensity upon aerobic annealing, accompanying a transition from amorphous to crystalline, while bands appearing at 2.1 and 2.3 eV seemed to occur only in the crystalline films. In addition, both amorphous and crystalline scandia films exhibited blue-green vibronic fine structure between 2.3 and 3.2 eV attributed to the electronic transition B→κ Σ+ 2 Σ+ in surface ⋯ O - ⋯ O - S c = O groups and split by a vibrational mode observed at 920 ± 60 cm - 1 by infrared spectroscopy. Band gaps of amorphous and crystalline Sc2O3 were determined to be 5.3 and 5.7 eV, respectively via diffuse reflectance. All films had high refractive indices, varying between 1.8 and 2.0 at 400 nm depending on film thickness and carrier gas used in the deposition; film thicknesses less than ca. 300 nm were observed to have a strong influence on the refractive index measured, while there was little variation for films thicker than this. The synthesis process itself is exceedingly low-cost and facile thus promising streamlined industrial scalability.

40 CFR 421.271 - Specialized definitions.

Code of Federal Regulations, 2013 CFR

2013-07-01

... AND STANDARDS NONFERROUS METALS MANUFACTURING POINT SOURCE CATEGORY Primary Rare Earth Metals.... (b) The term rare earth metals refers to the elements scandium, yttrium, and lanthanum to lutetium, inclusive. (c) The term mischmetal refers to a rare earth metal alloy comprised of the natural mixture of...

40 CFR 421.271 - Specialized definitions.

Code of Federal Regulations, 2014 CFR

2014-07-01

... AND STANDARDS NONFERROUS METALS MANUFACTURING POINT SOURCE CATEGORY Primary Rare Earth Metals.... (b) The term rare earth metals refers to the elements scandium, yttrium, and lanthanum to lutetium, inclusive. (c) The term mischmetal refers to a rare earth metal alloy comprised of the natural mixture of...

40 CFR 421.271 - Specialized definitions.

Code of Federal Regulations, 2012 CFR

2012-07-01

... AND STANDARDS NONFERROUS METALS MANUFACTURING POINT SOURCE CATEGORY Primary Rare Earth Metals.... (b) The term rare earth metals refers to the elements scandium, yttrium, and lanthanum to lutetium, inclusive. (c) The term mischmetal refers to a rare earth metal alloy comprised of the natural mixture of...

40 CFR 421.271 - Specialized definitions.

Code of Federal Regulations, 2011 CFR

2011-07-01

... AND STANDARDS NONFERROUS METALS MANUFACTURING POINT SOURCE CATEGORY Primary Rare Earth Metals.... (b) The term rare earth metals refers to the elements scandium, yttrium, and lanthanum to lutetium, inclusive. (c) The term mischmetal refers to a rare earth metal alloy comprised of the natural mixture of...

Boride Formation Induced by pcBN Tool Wear in Friction-Stir-Welded Stainless Steels

NASA Astrophysics Data System (ADS)

Park, Seung Hwan C.; Sato, Yutaka S.; Kokawa, Hiroyuki; Okamoto, Kazutaka; Hirano, Satoshi; Inagaki, Masahisa

2009-03-01

The wear of polycrystalline cubic boron nitride (pcBN) tool and its effect on second phase formation were investigated in stainless steel friction-stir (FS) welds. The nitrogen content and the flow stress were analyzed in these welds to examine pcBN tool wear. The nitrogen content in stir zone (SZ) was found to be higher in the austenitic stainless steel FS welds than in the ferritic and duplex stainless steel welds. The flow stress of austenitic stainless steels was almost 1.5 times larger than that of ferritic and duplex stainless steels. These results suggest that the higher flow stress causes the severe tool wear in austenitic stainless steels, which results in greater nitrogen pickup in austenitic stainless steel FS welds. From the microstructural observation, a possibility was suggested that Cr-rich borides with a crystallographic structure of Cr2B and Cr5B3 formed through the reaction between the increased boron and nitrogen and the matrix during FS welding (FSW).

Transition metal carbides, nitrides and borides, and their oxygen containing analogs useful as water gas shift catalysts

DOEpatents

Thompson, Levi T.; Patt, Jeremy; Moon, Dong Ju; Phillips, Cory

2003-09-23

Mono- and bimetallic transition metal carbides, nitrides and borides, and their oxygen containing analogs (e.g. oxycarbides) for use as water gas shift catalysts are described. In a preferred embodiment, the catalysts have the general formula of M1.sub.A M2.sub.B Z.sub.C O.sub.D, wherein M1 is selected from the group consisting of Mo, W, and combinations thereof; M2 is selected from the group consisting of Fe, Ni, Cu, Co, and combinations thereof; Z is selected from the group consisting of carbon, nitrogen, boron, and combinations thereof; A is an integer; B is 0 or an integer greater than 0; C is an integer; O is oxygen; and D is 0 or an integer greater than 0. The catalysts exhibit good reactivity, stability, and sulfur tolerance, as compared to conventional water shift gas catalysts. These catalysts hold promise for use in conjunction with proton exchange membrane fuel cell powered systems.

Ultra High Temperature Ceramics' Processing Routes and Microstructures Compared

NASA Technical Reports Server (NTRS)

Gusman, Michael; Stackpoole, Mairead; Johnson, Sylvia; Gasch, Matt; Lau, Kai-Hung; Sanjurjo, Angel

2009-01-01

Ultra High Temperature Ceramics (UHTCs), such as HfB2 and ZrB2 composites containing SiC, are known to have good thermal shock resistance and high thermal conductivity at elevated temperatures. These UHTCs have been proposed for a number of structural applications in hypersonic vehicles, nozzles, and sharp leading edges. NASA Ames is working on controlling UHTC properties (especially, mechanical properties, thermal conductivity, and oxidation resistance) through processing, composition, and microstructure. In addition to using traditional methods of combining additives to boride powders, we are preparing UHTCs using coat ing powders to produce both borides and additives. These coatings and additions to the powders are used to manipulate and control grain-boundary composition and second- and third-phase variations within the UHTCs. Controlling the composition of high temperature oxidation by-products is also an important consideration. The powders are consolidated by hot-pressing or field-assisted sintering (FAS). Comparisons of microstructures and hardness data will be presented.

A superconducting battery material: Lithium gold boride (LiAu3B)

NASA Astrophysics Data System (ADS)

Aydin, Sezgin; Şimşek, Mehmet

2018-04-01

The superconducting and potential cathode material properties of ternary boride of LiAu3B have been investigated by density functional first principles. The Li-concentration effects on the actual electronic and structural properties, namely the properties of LixAu9B3 (x = 0, 1, 2) sub-systems are studied. It is remarkably shown that the existence of Li-atoms has no considerable effect on the structural properties of Au-B skeleton in LiAu3B. Then, it can be offered as a potential cathode material for Li-ion batteries with the very small volume deviation of 0.42%, and the suitable average open circuit voltage of ∼1.30 V. Furthermore, the vibrational and superconducting properties such as electron-phonon coupling constant (λ) and critical temperature (Tc) of LiAu3B are studied. The calculated results suggest that LiAu3B should be a superconductor with Tc ∼5.8 K, also.

High performance AlScN thin film based surface acoustic wave devices with large electromechanical coupling coefficient

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wang, Wenbo; He, Xingli; Ye, Zhi, E-mail: yezhi@zju.edu.cn, E-mail: jl2@bolton.ac.uk

AlN and AlScN thin films with 27% scandium (Sc) were synthesized by DC magnetron sputtering deposition and used to fabricate surface acoustic wave (SAW) devices. Compared with AlN-based devices, the AlScN SAW devices exhibit much better transmission properties. Scandium doping results in electromechanical coupling coefficient, K{sup 2}, in the range of 2.0% ∼ 2.2% for a wide normalized thickness range, more than a 300% increase compared to that of AlN-based SAW devices, thus demonstrating the potential applications of AlScN in high frequency resonators, sensors, and high efficiency energy harvesting devices. The coupling coefficients of the present AlScN based SAW devices are muchmore » higher than that of the theoretical calculation based on some assumptions for AlScN piezoelectric material properties, implying there is a need for in-depth investigations on the material properties of AlScN.« less

Mid-Infrared Spectroscopy Analysis of the Effects of Erbium, Chromium:Yattrium-Scandium-Gallium-Garnet (Er,Cr:YSGG) Laser Irradiation on Bone Mineral and Organic Components.

PubMed

Benetti, Carolina; Ana, Patricia Aparecida; Bachmann, Luciano; Zezell, Denise Maria

2015-12-01

The effects of varying the energy density of a high-intensity erbium, chromium: yttrium-scandium-gallium-garnet (Er,Cr:YSGG) laser on the mineral and organic components of bone tissue were evaluated using Fourier transform infrared spectroscopy. Bone samples obtained from the tibias of rabbits were irradiated with five energy densities (3, 6, 8, 12, and 15 J/cm(2)), and the effects on the carbonate to phosphate ratio and in the organic components were compared with those of nonirradiated samples. The increased temperature during the laser irradiation was also measured using infrared thermography to relate the observed spectral changes to the laser thermal effects. The analyses of the infrared spectra suggests that the irradiation with Er,Cr:YSGG promoted changes in bone tissue in both the mineral and organic components that depend on the laser energy density, pointing to the importance of using the proper energy density in clinical procedures.

Yb-doped mixed-sesquioxide films grown by pulsed laser deposition

NASA Astrophysics Data System (ADS)

Prentice, Jake J.; Grant-Jacob, James A.; Shepherd, David P.; Eason, Robert W.; Mackenzie, Jacob I.

2018-06-01

Growth and characterization of compositionally tuned, ytterbium-doped mixed lutetium-scandium oxide, and pure lutetia and scandia crystalline films are presented. Pulsed laser deposition was employed to grow these sesquioxide films, of thicknesses up to 20 μm, on (0 0 0 1)-sapphire substrates. By varying the atomic ratio of lutetium to scandium in the target, the lattice parameter of the resulting films could be tuned to match that of the single-crystal c-cut sapphire substrate and thereby achieve a lattice mismatch of <0.1%. Optimization of growth parameters led to a reduction of undesirable particulates and scattering points within the film. X-ray diffraction measurements show (2 2 2)-orientated epitaxial growth with crystallinity comparable to bulk crystals. Through pole figure and electron-backscatter imaging measurements, it was found that two inverted cubic lattice orientations grow with micron-scaled domains. Growth of these lattice-matched mixed sesquioxides paves the way for fabrication of high-quality waveguides suitable for generation of ultrashort laser pulses.

Labeling of DOTA-conjugated HPMA-based polymers with trivalent metallic radionuclides for molecular imaging.

PubMed

Eppard, Elisabeth; de la Fuente, Ana; Mohr, Nicole; Allmeroth, Mareli; Zentel, Rudolf; Miederer, Matthias; Pektor, Stefanie; Rösch, Frank

2018-02-27

In this work, the in vitro and in vivo stabilities and the pharmacology of HPMA-made homopolymers were studied by means of radiometal-labeled derivatives. Aiming to identify the fewer amount and the optimal DOTA-linker structure that provides quantitative labeling yields, diverse DOTA-linker systems were conjugated in different amounts to HPMA homopolymers to coordinate trivalent radiometals Me(III)* = gallium-68, scandium-44, and lutetium-177. Short linkers and as low as 1.6% DOTA were enough to obtain labeling yields > 90%. Alkoxy linkers generally exhibited lower labeling yields than alkane analogues despite of similar chain length and DOTA incorporation rate. High stability of the radiolabel in all examined solutions was observed for all conjugates. Labeling with scandium-44 allowed for in vivo PET imaging and ex vivo measurements of organ distribution for up to 24 h. This study confirms the principle applicability of DOTA-HPMA conjugates for labeling with different trivalent metallic radionuclides allowing for diagnosis and therapy.

Evaluation of the Benjamin type proportional counter for absolute neutron spectrometry

DOE Office of Scientific and Technical Information (OSTI.GOV)

Taeb, M.

1985-01-01

This evaluation has shown that the major sources of uncertainty in experimental measurements with a Benjamin detector are: (1) detector pressure, (2) hydrogen gas purity, (3) detector calibration, and (4) operating voltage. To test these operational parameters, neutron spectra were measured at the University of Missouri Research Reactor (MURR) for silicon, scandium, iron, and bismuth filtered beams and angular penetration data through an 20.3 cm water slab. Results were then critically compared with theoretical calculations and with data from other spectrometer systems in regions of energy overlap. Neutron spectra having relatively small contributions from neutrons with energies higher than themore » energy range of the Benjamin spectrometer (at a specific pressure) generally exhibit excellent results. This is particularly true for the silicon filter (which produces two quasi-monoenergetic peaks at 55 keV and 144 keV) and the scandium filter (which creates a spectrum which decreases with increasing energy). For those spectra exhibiting relatively larger high energy neutron components, the results are less satisfying.« less

Effects of an erbium, chromium: yttrium, scandium, gallium, garnet laser on mucocutanous soft tissues.

PubMed

Rizoiu, I M; Eversole, L R; Kimmel, A I

1996-10-01

Lasers are effective tools for soft tissue surgery. The erbium, chromium: yttrium, scandium, gallium, garnet laser is a new system that incorporates an air-water spray. This study evaluates the cutting margins of this laser and compares healing with laser and conventional scalpel and punch biopsy-induced wounds. New Zealand white rabbits were divided into serial sacrifice groups; the tissues were grossly and microscopically analyzed after laser and convential steel surgical wounding. Wound margins were found to show minimal edge coagulation artifact and were 20 to 40 mm in width. Laser wounds showed minimal to no hemorrhage and re-epithelialization and collagenization were found to occur by day 7 in both laser and conventional groups. The new laser system is an effective soft tissue surgical device; wound healing is comparable to that associated with surgical steel wounds. The minimal edge artifact observed with this laser system should allow for the procurement of diagnostic biopsy specimens.

The Nature of the Microstructure and Interface Boundary Formation in Directionally Solidified Ceramic Boride Composites

DTIC Science & Technology

2011-05-01

failure resistance, which results from their different microplasticity (microbrittleness) and relaxation ability. In order to evaluate the... microplasticity (microbrittleness) in the series of isomorphic hexaborides produced by zone melting we have plotted a number of statistical curves that show

Ultracapacitor current collector

DOEpatents

Jerabek, Elihu Calfin; Mikkor, Mati

2001-10-16

An ultracapacitor having two solid, nonporous current collectors, two porous electrodes separating the collectors, a porous separator between the electrodes and an electrolyte occupying the pores in the electrodes and separator. At least one of the current collectors comprises a conductive metal substrate coated with a metal nitride, carbide or boride coating.

SCANDIUM TRIFLATE CATALYZED IN SITU PRINS-TYPE CYCLIZATION: FORMATIONS OF 4-TETRAHYDROPYRANOLS AND ETHERS. (R822668)

EPA Science Inventory

The perspectives, information and conclusions conveyed in research project abstracts, progress reports, final reports, journal abstracts and journal publications convey the viewpoints of the principal investigator and may not represent the views and policies of ORD and EPA. Concl...

Temperature dependence of the 1.06-microm stimulated emission cross section of neodymium in YAG and in GSGG.

PubMed

Rapaport, Alexandra; Zhao, Shengzhi; Xiao, Guohua; Howard, Andrew; Bass, Michael

2002-11-20

A linear temperature dependence between -70 degrees C and +70 degrees C is reported for the peak stimulated emission cross section of Nd3+ ions in both yttrium aluminum garnet (YAG) and gadolinium scandium gallium garnet (GSGG).

Pressed boride cathodes

NASA Technical Reports Server (NTRS)

Wolski, W.

1985-01-01

Results of experimental studies of emission cathodes made from lanthanum, yttrium, and gadolinium hexaborides are presented. Maximum thermal emission was obtained from lanthanum hexaboride electrodes. The hexaboride cathodes operated stably under conditions of large current density power draw, at high voltages and poor vacuum. A microtron electron gun with a lanthanum hexaboride cathode is described.

Thermophysical and Electronic Properties Information Analysis Center (TEPIAC): A Continuing Systematic Program on Tables of Thermophysical and Electronic Properties of Materials.

DTIC Science & Technology

1977-02-01

oxides and their mixtures, arsenides, borides, bromides , carbides , chlorides , fluoride s, nitride s, phosphides, silicides , sulfides , tellurides...ivity of alkali elements (lithium , sodium , potassium , rubi- dium , ces ium , and francium) and contains recomme nded reference values generated

Molecular Modeling of High-Temperature Oxidation of Refractory Borides

DTIC Science & Technology

2008-02-01

generate the classical potential, we adopt the van Beest , Kramer and van Santen (BKS) parameterization for Si-O interactions, but fit B-O and Si-B...seminar at Department of Aerospace and Mechanical Engineering, University of Notre Dame, March 20, 2007. 6 Los Alamos National Lab Physics & Theoretical

RARE EARTH ELEMENTS: A REVIEW OF PRODUCTION, PROCESSING, RECYCLING, AND ASSOCIATED ENVIRONMENTAL ISSUES

EPA Science Inventory

Rare earth elements (REEs) are a group of 15 chemical elements in the periodic table, specifically the lanthanides. Two other elements, scandium and yttrium, have a similar physiochemistry to the lanthanides, are commonly found in the same mineral assemblages, and are often refe...

Lithium Borides - High Energy Materials

DTIC Science & Technology

2000-02-28

1993. 99, 7983. (32) Pulay P.; Hamilton. T. P. J. Chem. Phys. 1988, 88. 4926 . (33) Frisch. M. J.: Trucks. G. W.; Schlegel. H. B.: Gill, P. M. W...25] P.V. Sudhakar, K. Lammertsma, J. Chem. Phys. 99 (1993) 7929. [26] M.J. van der Woerd, K. Lammertsma, B.J. Duke, H.F. Schaefer , III, J

Grain Refinement and Texture Mitigation in Low Boron Containing TiAl-Alloys

NASA Astrophysics Data System (ADS)

Hecht, Ulrike; Witusiewicz, Victor T.

2017-12-01

Controlling the grain size and texture of lamellar TiAl-alloys is essential for well-balanced creep and fatigue properties. Excellent refinement and texture mitigation are achieved in aluminum lean alloys by low boron additions of 0.2 at.%. This amount is sufficient to promote in situ formation of ultrafine borides during the last stages of body centered cubic (BCC) solidification. The borides subsequently serve as nucleation sites for hexagonal close packed (HCP) during the BCC-HCP phase transformation. Bridgman solidification experiments with alloy Ti-43Al-8Nb-0.2C-0.2B were performed under a different growth velocity, i.e., cooling rate, to evaluate the HCP grain size distribution and texture. For slow-to-moderate cooling rates, about 65% of HCP grains are randomly oriented, despite the pronounced texture of the parent BCC phase resulting from directional solidification. For high cooling rates, obtained by quenching, texture mitigation is less pronounced. Only 28% of the HCP grains are randomly oriented, the majority being crystallographic variants of the Burgers orientation relationship.

An XPS study of the adherence of refractory carbide, silicide, and boride RF-sputtered wear-resistant coatings. [X-ray Photoelectron Spectroscopy of steel surfaces

NASA Technical Reports Server (NTRS)

Brainard, W. A.; Wheeler, D. R.

1978-01-01

Radio frequency sputtering was used to deposit refractory carbide, silicide, and boride coatings on 440-C steel substrates. Both sputter etched and pre-oxidized substrates were used and the films were deposited with and without a substrate bias. The composition of the coatings was determined as a function of depth by X-ray photoelectron spectroscopy combined with argon ion etching. Friction and wear tests were conducted to evaluate coating adherence. In the interfacial region there was evidence that bias may produce a graded interface for some compounds. Biasing, while generally improving bulk film stoichiometry, can adversely affect adherence by removing interfacial oxide layers. Oxides of all film constituents except carbon and iron were present in all cases but the iron oxide coverage was only complete on the preoxidized substrates. The film and iron oxides were mixed in the MoSi2 and Mo2C films but layered in the Mo2B5 films. In the case of mixed oxides, preoxidation enhanced film adherence. In the layered case it did not.

Boronization and Carburization of Superplastic Stainless Steel and Titanium-Based Alloys

PubMed Central

Matsushita, Masafumi

2011-01-01

Bronization and carburization of fine-grain superplastic stainless steel is reviewed, and new experimental results for fine grain Ti88.5Al4.5V3Fe2Mo2 are reported. In superplastic duplex stainless steel, the diffusion of carbon and boron is faster than in non-superplastic duplex stainless steel. Further, diffusion is activated by uniaxial compressive stress. Moreover, non-superplastic duplex stainless steel shows typical grain boundary diffusion; however, inner grain diffusion is confirmed in superplastic stainless steel. The presence of Fe and Cr carbides or borides is confirmed by X-ray diffraction, which indicates that the diffused carbon and boron react with the Fe and Cr in superplastic stainless steel. The Vickers hardness of the carburized and boronized layers is similar to that achieved with other surface treatments such as electro-deposition. Diffusion of boron into the superplastic Ti88.5Al4.5V3Fe2Mo2 alloy was investigated. The hardness of the surface exposed to boron powder can be increased by annealing above the superplastic temperature. However, the Vickers hardness is lower than that of Ti boride. PMID:28824144

10 CFR Appendix L to Part 110 - Illustrative List of Byproduct Materials Under NRC Export/Import Licensing Authority a

Code of Federal Regulations, 2012 CFR

2012-01-01

...) Scandium 48 (Sc 48) Selenium 75 (Se 75) Silicon 31 (Si 31) Silver 105 (Ag 105) Silver 110m (Ag 110m) Silver 111 (Ag 111) Sodium 22 (Na 22) Sodium 24 (Na 24) Strontium 85 (Sr 85) Strontium 89 (Sr 89) Strontium...

10 CFR Appendix L to Part 110 - Illustrative List of Byproduct Materials Under NRC Export/Import Licensing Authority a

Code of Federal Regulations, 2014 CFR

2014-01-01

...) Scandium 48 (Sc 48) Selenium 75 (Se 75) Silicon 31 (Si 31) Silver 105 (Ag 105) Silver 110m (Ag 110m) Silver 111 (Ag 111) Sodium 22 (Na 22) Sodium 24 (Na 24) Strontium 85 (Sr 85) Strontium 89 (Sr 89) Strontium...

Electron spin resonance studies of Bi1-xScxFeO3 nanoparticulates: Observation of an enhanced spin canting over a large temperature range

NASA Astrophysics Data System (ADS)

Titus, S.; Balakumar, S.; Sakar, M.; Das, J.; Srinivasu, V. V.

2017-12-01

Bi1-xScxFeO3 (x = 0.0, 0.1, 0.15, 0.25) nano particles were synthesized by sol gel method. We then probed the spin system in these nano particles using electron spin resonance technique. Our ESR results strongly suggest the scenario of modified spin canted structures. Spin canting parameter Δg/g as a function of temperature for Scandium doped BFO is qualitatively different from undoped BFO. A broad peak is observed for all the Scandium doped BFO samples and an enhanced spin canting over a large temperature range (75-210 K) in the case of x = 0.15 doping. We also showed that the asymmetry parameter and thereby the magneto-crystalline anisotropy in these BSFO nanoparticles show peaks around 230 K for (x = 0.10 and 0.15) and beyond 300 K for x = 0.25 system. Thus, we established that the Sc doping significantly modifies the spin canting and magneto crystalline anisotropy in the BFO system.

Aluminum-Scandium Alloys: Material Characterization, Friction Stir Welding, and Compatibility With Hydrogen Peroxide (MSFC Center Director's Discretionary Fund Final Report, Proj. No. 04-14)

NASA Technical Reports Server (NTRS)

Lee, J. A.; Chen, P. S.

2004-01-01

This Technical Memorandum describes the development of several high-strength aluminum (Al) alloys that are compatible with hydrogen peroxide (H2O2) propellant for NASA Hypersonic-X (Hyper-X) vehicles fuel tanks and structures. The yield strengths for some of these Al-magnesium-based alloys are more than 3 times stronger than the conventional 5254-H112 Al alloy, while maintaining excellent H2O2 compatibility similar to class 1 5254 alloy. The alloy development strategy is to add scandium, zirconium, and other transitional metals with unique electrochemical properties, which will not act as catalysts, to decompose the highly concentrated 90 percent H2O2. Test coupons are machined from sheet metals for H2O2 long-term exposure testing and mechanical properties testing. In addition, the ability to weld the new alloys using friction stir welding has also been explored. The new high-strength alloys could represent an enabling material technology for Hyper-X vehicles, where flight weight reduction is a critical requirement.

Accumulation of radionuclides in bed sediments of the Columbia River between Hanford reactors and McNary Dam

USGS Publications Warehouse

Nelson, Jack L.; Haushild, W.L.

1970-01-01

Amounts of radionuclides from the Hanford reactors contained in bed sediments of the Columbia River were estimated by two methods: (1) from data on radionuclide concentration for the bed sediments between the reactors and McNary Dam, and (2) from data on radionuclide discharge for river stations at Pasco, Washington, and Umatilla, Oregon. Umatilla is 3.2 kilometers below McNary Dam. Accumulations of radionuclides in the Pasco to Umatilla reach estimated by the two methods agree within about 8%. In October 1965 approximately 16,000 curies of gamma emitting radionuclides were resident in bed sediments of the river between the Hanford reactors and McNary Dam. Concentrations and accumulations of chromium-51, zinc-65, cobalt-60, manganese-54, and scandium-46 generally are much higher near McNary Dam than they are in the vicinity of the reactors. These changes are caused by an increase downstream from the reactors in the proportion of the bed sediment that is fine grained and the proportions of the transported zinc, cobalt, manganese, and scandium radionuclides associated with sediment particles.

Stress controlled pulsed direct current co-sputtered Al{sub 1−x}Sc{sub x}N as piezoelectric phase for micromechanical sensor applications

DOE Office of Scientific and Technical Information (OSTI.GOV)

Fichtner, Simon, E-mail: sif@tf.uni-kiel.de; Reimer, Tim; Chemnitz, Steffen

2015-11-01

Scandium alloyed aluminum nitride (Al{sub 1−x}Sc{sub x}N) thin films were fabricated by reactive pulsed direct current co-sputtering of separate scandium and aluminum targets with x ≤ 0.37. A significant improvement of the clamped transversal piezoelectric response to strain e{sub 31,f} from −1.28 C/m{sup 2} to −3.01 C/m{sup 2} was recorded, while dielectric constant and loss angle remain low. Further, the built-in stress level of Al{sub 1−x}Sc{sub x}N was found to be tuneable by varying pressure, Ar/N{sub 2} ratio, and Sc content. The thus resulting enhancement of the expectable signal to noise ratio by a factor of 2.1 and the abilitymore » to control built-in stress make the integration of Al{sub 1−x}Sc{sub x}N as the piezoelectric phase of micro-electro-mechanical system sensor applications highly attractive.« less

Optical fluoride sensor based on monomer-dimer equilibrium of scandium(III)-octaethylporphyrin in a plasticized polymeric film.

PubMed

Kang, Youngjea; Kampf, Jeff W; Meyerhoff, Mark E

2007-08-29

A fluoride-selective optical sensor based on scandium(III)-octaethylporphyrin (Sc(III)OEP) as an ionophore within a plasticized PVC film is described. The presence of fluoride ion in the aqueous sample phase increases the formation of a difluoro-bridged Sc(III)OEP dimer species in the polymer film. The ability of the Sc(III) porphyrin to form the dimeric structure in the presence of fluoride is confirmed by UV-vis spectroscopy and X-ray crystallography. For more practical sensing applications, a pH chromoionophore (ETH 7075) is added to the plasticized PVC film along with Sc(III)OEP and the observed optical response is based on coextraction of protons with sample phase fluoride to create the dimeric porphyrin and a protonated chromoionophore species. The selectivity pattern observed is F- > ClO4(-), SCN-, NO3(-) > Br-, Cl-. Only organic salicylate is a significant interferent. Fast and reversible fluoride response is observed over the range of 10(-4) to 10(-2) M fluoride, allowing use of the sensing film in a waveguide configuration for flow-injection measurements.

Optical Fluoride Sensor Based on Monomer-Dimer Equilibrium of Scandium(III)-Octaethylporphyrin in a Plasticized Polymeric Film

PubMed Central

Kang, Youngjea; Kampf, Jeff W.; Meyerhoff, Mark E.

2007-01-01

A fluoride-selective optical sensor based on scandium(III) octaethylporphyrin (Sc(III)OEP) as an ionophore within a plasticized PVC film is described. The presence of fluoride ion in the aqueous sample phase increases the formation of a difluoro-bridged Sc(III)OEP dimer species in the polymer film. The ability of the Sc(III) porphyrin to form the dimeric structure in the presence of fluoride is confirmed by UV-Vis spectroscopy and X-ray crystallography. For more practical sensing applications, a pH chromoionophore (ETH 7075) is added to the plasticized PVC film along with Sc(III)OEP and the observed optical response is based on co-extraction of protons with sample phase fluoride to create the dimeric porphyrin and a protonated chromoionophore species. The selectivity pattern observed is F-≫ClO4-, SCN-, NO3->Br-, Cl-. Only organic salicylate is a significant interferent. Fast and reversible fluoride response is observed over the range of 10-4 ~10-2 M fluoride, allowing use of the sensing film in a waveguide configuration for flow-injection measurements. PMID:17719905

Impact of layer and substrate properties on the surface acoustic wave velocity in scandium doped aluminum nitride based SAW devices on sapphire

DOE Office of Scientific and Technical Information (OSTI.GOV)

Gillinger, M., E-mail: manuel.gillinger@tuwien.ac.at; Knobloch, T.; Schneider, M.

2016-06-06

This paper investigates the performance of surface acoustic wave (SAW) devices consisting of reactively sputter deposited scandium doped aluminum nitride (Sc{sub x}Al{sub 1-x}N) thin films as piezoelectric layers on sapphire substrates for wireless sensor or for RF-MEMS applications. To investigate the influence of piezoelectric film thickness on the device properties, samples with thickness ranging from 500 nm up to 3000 nm are fabricated. S{sub 21} measurements and simulations demonstrate that the phase velocity is predominantly influenced by the mass density of the electrode material rather than by the thickness of the piezoelectric film. Additionally, the wave propagation direction is varied by rotatingmore » the interdigital transducer structures with respect to the crystal orientation of the substrate. The phase velocity is about 2.5% higher for a-direction compared to m-direction of the sapphire substrate, which is in excellent agreement with the difference in the anisotropic Young's modulus of the substrate corresponding to these directions.« less

Ratcheting rotation or speedy spinning: EPR and dynamics of Sc3C2@C80.

PubMed

Roukala, Juho; Straka, Michal; Taubert, Stefan; Vaara, Juha; Lantto, Perttu

2017-08-08

Besides their technological applications, endohedral fullerenes provide ideal conditions for investigating molecular dynamics in restricted geometries. A representative of this class of systems, Sc 3 C 2 @C 80 displays complex intramolecular dynamics. The motion of the 45 Sc trimer has a remarkable effect on its electron paramagnetic resonance (EPR) spectrum, which changes from a symmetric 22-peak pattern at high temperature to a single broad lineshape at low temperature. The scandium trimer consists of two equivalent and one inequivalent metal atom, due to the carbon dimer rocking through the Sc 3 triangle. We demonstrate through first-principles molecular dynamics (MD), EPR parameter tensor averaging, and spectral modelling that, at high temperatures, three-dimensional movement of the enclosed Sc 3 C 2 moiety takes place, which renders the metal centers equivalent and their magnetic parameters effectively isotropic. In contrast, at low temperatures the dynamics becomes restricted to two dimensions within the equatorial belt of the I h symmetric C 80 host fullerene. This restores the inequivalence of the scandium centers and causes their anisotropic hyperfine couplings to broaden the experimental spectrum.

Reducing the stochasticity of crystal nucleation to enable subnanosecond memory writing.

PubMed

Rao, Feng; Ding, Keyuan; Zhou, Yuxing; Zheng, Yonghui; Xia, Mengjiao; Lv, Shilong; Song, Zhitang; Feng, Songlin; Ronneberger, Ider; Mazzarello, Riccardo; Zhang, Wei; Ma, Evan

2017-12-15

Operation speed is a key challenge in phase-change random-access memory (PCRAM) technology, especially for achieving subnanosecond high-speed cache memory. Commercialized PCRAM products are limited by the tens of nanoseconds writing speed, originating from the stochastic crystal nucleation during the crystallization of amorphous germanium antimony telluride (Ge 2 Sb 2 Te 5 ). Here, we demonstrate an alloying strategy to speed up the crystallization kinetics. The scandium antimony telluride (Sc 0.2 Sb 2 Te 3 ) compound that we designed allows a writing speed of only 700 picoseconds without preprogramming in a large conventional PCRAM device. This ultrafast crystallization stems from the reduced stochasticity of nucleation through geometrically matched and robust scandium telluride (ScTe) chemical bonds that stabilize crystal precursors in the amorphous state. Controlling nucleation through alloy design paves the way for the development of cache-type PCRAM technology to boost the working efficiency of computing systems. Copyright © 2017 The Authors, some rights reserved; exclusive licensee American Association for the Advancement of Science. No claim to original U.S. Government Works.

Frenolicins C-G, pyranonaphthoquinones from Streptomyces sp. RM-4-15.

PubMed

Wang, Xiachang; Shaaban, Khaled A; Elshahawi, Sherif I; Ponomareva, Larissa V; Sunkara, Manjula; Zhang, Yinan; Copley, Gregory C; Hower, James C; Morris, Andrew J; Kharel, Madan K; Thorson, Jon S

2013-08-23

Appalachian active coal fire sites were selected for the isolation of bacterial strains belonging to the class actinobacteria. A comparison of high-resolution electrospray ionization mass spectrometry (HRESIMS) and ultraviolet (UV) absorption profiles from isolate extracts to natural product databases suggested Streptomyces sp. RM-4-15 to produce unique metabolites. Four new pyranonaphthoquinones, frenolicins C-F (1-4), along with three known analogues, frenolicin (6), frenolicin B (7), and UCF76-A (8), were isolated from the fermentation of this strain. An additional new analogue, frenolicin G (5), along with two known compounds, deoxyfrenolicin (9) and UCF 13 (10), were isolated from the fermentation supplied with 18 mg/L of scandium chloride, the first example, to the best of our knowledge, wherein scandium chloride supplementation led to the confirmed production of new bacterial secondary metabolites. Structures 1-5 were elucidated on the basis of spectral analysis and chemical modification. While frenolicins are best known for their anticoccidial activity, the current study revealed compounds 6-9 to exhibit moderate cytotoxicity against the human lung carcinoma cell line (A549) and thereby extends the anticancer SAR for this privileged scaffold.

Proceedings 43rd Stanford Geothermal Workshop

DOE Office of Scientific and Technical Information (OSTI.GOV)

Simmons, Stuart; Kirby, Stefan; Verplanck, Philip

Herein we summarize the results of an investigation dealing with the concentrations and inventories of strategic, critical and valuable materials (SCVM) in produced fluids from geothermal and hydrocarbon reservoirs (50-250° C) in Nevada and Utah. Water samples were collected from thirty-four production wells across eight geothermal fields, the Uinta Basin oil/gas province in northeast Utah, and the Covenant oil field in southwestern Utah; additional water samples were collected from six hot springs in the Sevier Thermal Belt in southwestern Utah. Most SCVM concentrations in produced waters range from <0.1 to 100 µg/kg; the main exception is lithium, which has concentrationsmore » that range from <1000 to 25,000 ug/kg. Relatively high concentrations of gallium, germanium, scandium, selenium, and tellurium are measured too. Geothermal waters contain very low concentrations of REEs, below analytical detections limits (0.01 µg/kg), but the concentrations of lanthanum, cerium, and europium range from 0.05 to 5 µg/kg in Uinta basin waters. Among the geothermal fields, the Roosevelt Hot Spring reservoir appears to have the largest inventories of germanium and lithium, and Patua appears to have the largest inventories of gallium, scandium, selenium, and tellurium. By comparison, the Uinta basin has larger inventories of gallium. The concentrations of gallium, germanium, lithium, scandium, selenium, and tellurium in produced waters appear to be partly related to reservoir temperature and concentrations of total dissolved salts. The relatively high concentration and large inventory of lithium occurring at Roosevelt Hot Springs may be related to granitic-gneissic crystalline rocks, which host the reservoir. Analyses of calcite scales from Dixie Valley indicate enrichments in cobalt, gallium, gold, palladium, selenium and tellurium, and these metals appear to be depositing at deep levels in production wells due to boiling. Comparisons with SCVM mineral deposits suggest that brines in sedimentary basins, or derived from lacustrine evaporites, enable aqueous transport of gallium, germanium, and lithium.« less

Lewis Acid-Induced Change from Four- to Two-Electron Reduction of Dioxygen Catalyzed by Copper Complexes Using Scandium Triflate

PubMed Central

Kakuda, Saya; Rolle, Clarence; Ohkubo, Kei; Siegler, Maxime A.; Karlin, Kenneth D.; Fukuzumi, Shunichi

2015-01-01

Mononuclear copper complexes, [(tmpa)CuII(CH3CN)](ClO4)2 (1, tmpa = tris(2-pyridylmethyl)amine) and [(BzQ)CuII(H2O)2](ClO4)2 (2, BzQ = bis(2-quinolinylmethyl)benzylamine)], act as efficient catalysts for the selective two-electron reduction of O2 by ferrocene derivatives in the presence of scandium triflate (Sc(OTf)3), in acetone, whereas 1 catalyzes the four-electron reduction of O2 by the same reductant in the presence of Brønsted acids such as triflic acid. Following formation of the peroxo-bridged dicopper(II) complex [(tmpa)CuII(O2)CuII(tmpa)]2+, the two-electron reduced product of O2 with Sc3+ is observed to be scandium peroxide ([Sc3+(O22−)]+). In the presence of three equiv of hexamethylphosphoric triamide (HMPA), [Sc3+(O22−)]+ was oxidized by [Fe(bpy)3]3+ (bpy = 2,2′-bipyridine) to the known superoxide species [(HMPA)3Sc3+(O2•−)]2+ as detected by EPR spectroscopy. A kinetic study revealed that the rate-determining step of the catalytic cycle for the two-electron reduction of O2 with 1 is electron transfer from Fc* to 1 to give a cuprous complex which is highly reactive toward O2, whereas the rate-determining step with 2 is changed to the reaction of the cuprous complex with O2 following electron transfer from ferrocene derivatives to 2. The explanation for the change in catalytic O2-reaction stoichiometry from four-electron with Brønsted acids to two-electron reduction in the presence of Sc3+ and also for the change in the rate-determining step is clarified based on a kinetics interrogation of the overall catalytic cycle as well as each step of the catalytic cycle with study of the observed effects of Sc3+ on copper-oxygen intermediates. PMID:25659416

Pt-B System Revisited: Pt2B, a New Structure Type of Binary Borides. Ternary WAl12-Type Derivative Borides.

PubMed

Sologub, Oksana; Salamakha, Leonid; Rogl, Peter; Stöger, Berthold; Bauer, Ernst; Bernardi, Johannes; Giester, Gerald; Waas, Monika; Svagera, Robert

2015-11-16

On the basis of a detailed study applying X-ray single-crystal and powder diffraction, differential scanning calorimetry, and scanning electron microscopy analysis, it was possible to resolve existing uncertainties in the Pt-rich section (≥65 atom % Pt) of the binary Pt-B phase diagram above 600 °C. The formation of a unique structure has been observed for Pt2B [X-ray single-crystal data: space group C2/m, a = 1.62717(11) nm, b = 0.32788(2) nm, c = 0.44200(3) nm, β = 104.401(4)°, RF2 = 0.030]. Within the homogeneity range of "Pt3B", X-ray powder diffraction phase analysis prompted two structural modifications as a function of temperature. The crystal structure of "hT-Pt3B" complies with the hitherto reported structure of anti-MoS2 [space group P63/mmc, a = 0.279377(2) nm, c = 1.04895(1) nm, RF = 0.075, RI = 0.090]. The structure of the new "[Formula: see text]T-Pt3B" is still unknown. The formation of previously reported Pt∼4B has not been confirmed from binary samples. Exploration of the Pt-rich section of the Pt-Cu-B system at 600 °C revealed a new ternary compound, Pt12CuB6-y [X-ray single-crystal data: space group Im3̅, a = 0.75790(2) nm, y = 3, RF2 = 0.0129], which exhibits the filled WAl12-type structure accommodating boron in the interstitial trigonal-prismatic site 12e. The isotypic platinum-aluminum-boride was synthesized and studied. The solubility of copper in binary platinum borides has been found to attain ∼7 atom % Cu for Pt2B but to be insignificant for "[Formula: see text]T-Pt3B". The architecture of the new Pt2B structure combines puckered layers of boron-filled and empty [Pt6] octahedra (anti-CaCl2-type fragment) alternating along the x axis with a double layer of boron-semifilled [Pt6] trigonal prisms interbedded with a layer of empty tetrahedra and tetragonal pyramids (B-deficient α-T[Formula: see text]I fragment). Assuming boron vacancies ordering (space group R3), the Pt12CuB6-y structure exhibits serpentine-like columns of edge-connected boron-filled [Pt6] trigonal prisms running infinitely along the z axis and embedding the icosahedrally coordinated Cu atom. Pt2B, (Pt1-yCuy)2B (y = 0.045), and Pt12CuB6-y (y = 3) behave metallically, as revealed by temperature-dependent electrical resistivity measurements.

PREFACE: The 16th International Symposium on Boron, Borides and Related Materials (ISBB 2008)

NASA Astrophysics Data System (ADS)

Tanaka, Takaho

2009-07-01

This volume of Journal of Physics: Conference Series contains invited and contributed peer-reviewed papers that were presented at the 16th International Symposium on Boron, Borides and Related Materials (ISBB 2008), which was held on 7-12 September 2008, at Kunibiki Messe, Matsue, Japan. This triennial symposium has a half-century long history starting from the 1st meeting in 1959 at Asbury Park, New Jersey. We were very pleased to organize ISBB 2008, which gathered chemists, physicists, materials scientists as well as diamond and high-pressure researchers. This meeting had a strong background in the boron-related Japanese research history, which includes the discovery of superconductivity in MgB2 and development of Nd-Fe-B hard magnets and of YB66 soft X-ray monochromator. The scope of ISBB 2008 spans both basic and applied interdisciplinary research that is centered on boron, borides and related materials, and the collection of articles defines the state of the art in research on these materials. The topics are centered on: 1. Preparation of new materials (single crystals, thin films, nanostructures, ceramics, etc) under normal or extreme conditions. 2. Crystal structure and chemical bonding (new crystal structures, nonstoichiometry, defects, clusters, quantum-chemical calculations). 3. Physical and chemical properties (band structure, phonon spectra, superconductivity; optical, electrical, magnetic, emissive, mechanical properties; phase diagrams, thermodynamics, catalytic activity, etc) in a wide range of temperatures and pressures. 4. Applications and prospects (thermoelectric converters, composites, ceramics, coatings, etc) There were a few discoveries of new materials, such as nanomaterials, and developments in applications. Many contributions were related to 4f heavy Fermion systems of rare-earth borides. Exotic mechanisms of magnetism and Kondo effects have been discussed, which may indicate another direction of development of boride. Two special sessions, 'Boron chemistry' and 'Superconductivity', were also held at the symposium. The session on Boron chemistry was planned to honor the scientific work in boron chemistry of Professor J Bauer on the occasion of his retirement. Many recent results were discussed in the session, and Professor Bauer himself introduced novel rare-earth-boron-carbon compounds RE10B7C10 (RE = Gd - Er) in his lecture. In the latter session, on the basis of recent discoveries of superconductivity in MgB2 and in β-boron under high pressure, the superconductivity of boron and related materials was discussed and the superconductivity of boron-doped diamond was also addressed. More than 120 participants from 16 countries attended the ISBB 2008, and active presentations (22 invited, 33 oral and 68 posters) and discussions suggest that research on boron and borides is entering a new phase of development. This volume contains 46 articles from 52 submitted manuscripts. The reviewers were invited not only from symposium participants but also from specialists worldwide, and they did a great job of evaluating and commenting on the submitted manuscripts to maintain the highest quality standard of this volume. Recent discoveries of superconductivity in boron under high pressure, synthesis of a new allotrope of boron and of various boron and boride nanostructures will lead this highly interdisciplinary field of science, which will further grow and gain attention in terms of both basic and applied research. In this context, we are very much looking forward to the next symposium, which will be held in Istanbul, Turkey, in 2011, organized by Professor Onuralp Yucel, Istanbul Technical University. Turkey currently has the world highest share of borate production and is expected to be involved more in boron-related research. Acknowledgements We gratefully acknowledge the style improvement by Dr K Iakoubovskii, and sincerely thank Shimane Prefecture and Matsue City for their financial support. The symposium was also supported by Tokyo University of Science, Suwa and foundations including, the Kajima Foundation, Foundation for Promotion of Material Science and Technology of Japan and Nippon Sheet Glass Foundation for Materials Science and Engineering, as well as companies including JFE Steel Corporation, Shincron Co, Ltd, Toyo Kohan Co, Ltd, Fukuda Metal Foil and Powder Co, Ltd, Japan New Metals Co, Ltd, H C Starck Ltd and Fritsch Japan Co, Ltd. Editors Chair Takaho Tanaka (National Institute for Materials Science, Japan) Vice chairs Koun Shirai (Osaka University, Japan) Kaoru Kimura (The University of Tokyo, Japan) Ken-ichi Takagi (Tokyo City University, Japan) Touetsu Shishido (Tohoku University, Japan) Shigeru Okada (Kokushikan University) Hideaki Itoh (Nagoya University,Japan) Katsumitsu Nakamura (Nihon University, Japan) Organizing committee of ISBB 2008 K Takagi Chairman (Tokyo City University) T Tanaka Program Committee Chairman (National Institute for Materials Science) K Kimura Secretary (The University of Tokyo) J Akimitsu (Aoyama University)K Shirai (Osaka University) H Itoh (Nagoya University)T Shishido (Tohoku University) K Nakamura (Nihon University)K Soga (Tokyo University of Science) K Nishiyama (Tokyo University of Science, Suwa)M Takeda (Nagaoka University of Technology) S Okada (Kokushikan University)Y Yamazaki (Toyo Kohan Co, Ltd) International Scientific Committee 0f ISBB (2008-2011) K Takagi Chairman (Japan) B Albert (Germany) J-F Halet (France) M Takeda (Japan) M Antadze (Georgia) H Hillebrecht (Germany) T Tanaka (Japan) J Bauer (France) W Jung (Germany) R Telle (Germany) I Boustani (Germany) K Kimura (Japan) M Trenary (USA) D Emin (USA) T Mori (Japan) O Tsagareishvili (Georgia) M Engler (Germany) P D Ownby (USA) H Werheit (Germany) N Frage (Israel) P Rogl (Austria) G Will (Germany) Yu Grin (Germany) S Shalamberidze (Georgia) O Yucel (Turkey) V N Gurin (Russia) N Shitsevalova (Ukraine) G Zhang (China)

Thermal emission property of solid solution Gd{sub 1-x}Nd{sub x}B{sub 6} (x=0, 0.6, 0.8)

DOE Office of Scientific and Technical Information (OSTI.GOV)

Xing Zhang, Jiu; Hong Bao, Li; Lin Zhou, Shen, E-mail: zjiuxing@bjut.edu.cn, E-mail: Baolihong_10@yahoo.com.cn, E-mail: zhoushenlin@emails.bjut.edu.cn

2011-07-01

In this paper, to further explore the excellent emission properties of rare earth boride cathode, herein we present the synthesis, characterization and properties of polycrystalline Nd{sub 1-x}Gd{sub x}B{sub 6} (x = 0, 0.6, 0.8) bulk via arc plasma and reactive SPS. (author)

Process research into metallic pipe wear of hot chamber die casting machines and methods ofincreasing wear resistance

NASA Astrophysics Data System (ADS)

Mukhametzyanova, G. F.; Kolesnikov, MS; Mukhametzyanov, I. R.; Astatshenko, V. I.

2017-09-01

The kinetics and reasons for metallic pipe wear of hot chamberzinc alloy die casting machines are established.Increasing metallic pipe wear components wear resistance is being achieved by means of die steelДИ - 22 with electroslag remelting modification and electron-beamremelting modification and after the processes of nitriding and boriding besides.

Nb2OsB2, with a new twofold superstructure of the U3Si2 type: Synthesis, crystal chemistry and chemical bonding

NASA Astrophysics Data System (ADS)

Mbarki, Mohammed; Touzani, Rachid St.; Fokwa, Boniface P. T.

2013-07-01

The new ternary metal-rich boride, Nb2OsB2, was synthesized by arc-melting the elements in a water-cooled copper crucible under an argon atmosphere. The compound was characterized from single-crystal X-ray data and EDX measurements. It crystallizes as a new superstructure (space group P4/mnc, no. 128) of the tetragonal U3Si2-structure type with lattice parameters a=5.922(1) Å and c=6.879(2) Å. All of the B atoms are involved in B2 dumbbells with B-B distances of 1.89(4) Å. Structure relaxation using VASP (Vienna ab intio Simulation Package) has confirmed the space group and the lattice parameters. According to electronic structure calculations (TB-LMTO-ASA), the homoatomic B-B interactions are optimized and very strong, but relatively strong heteroatomic Os-B, Nb-B and Nb-Os bonds are also found: These interactions, which together build a three-dimensional network, are mainly responsible for the structural stability of this new phase. The density of state at the Fermi level predicts metallic behavior, as expected, from this metal-rich boride.

The use of surface layer with boron in friction pairs lubricated by engine oils

NASA Astrophysics Data System (ADS)

Szczypiński-Sala, W.; Lubas, J.

2016-09-01

The aim of the present work is to determine the influence of surface layers with boron and engine oil on the processes of friction and wear in friction pairs. The ring samples with borided surface layer cooperated under test conditions with counterparts made with CuPb30 and AlSn20 bearing alloys. During the tests, the friction pairs were lubricated with 15W/40 Lotos mineral oil and 5W/40 Lotos synthetic oil. The lubrication of friction area with Lotos mineral oil causes the reduction of the friction force, the temperature in the friction area and the wear of the bearing alloys under study, whereas the lubrication with Lotos synthetic oil reduces the changes in the geometrical structure of the cooperating friction pair elements. Lubrication of the friction area in the start-up phase of the friction pair by mineral oil causes faster stabilization of the friction conditions in the contact area than in the cause of lubrication of the friction pair by synthetic oil. The intensity of wear of the AlSn20 bearing alloy cooperating with the borided surface layer is three times smaller than the intensity of use of the CuPb30 alloy bearing.

Synthesis, crystal structure investigation and magnetism of the complex metal-rich boride series Crx(Rh1-yRuy)7-xB3 (x=0.88-1; y=0-1) with Th7Fe3-type structure

NASA Astrophysics Data System (ADS)

Misse, Patrick R. N.; Mbarki, Mohammed; Fokwa, Boniface P. T.

2012-08-01

Powder samples and single crystals of the new complex boride series Crx(Rh1-yRuy)7-xB3 (x=0.88-1; y=0-1) have been synthesized by arc-melting the elements under purified argon atmosphere on a water-cooled copper crucible. The products, which have metallic luster, were structurally characterized by single-crystal and powder X-ray diffraction as well as EDX measurements. Within the whole solid solution range the hexagonal Th7Fe3 structure type (space group P63mc, no. 186, Z=2) was identified. Single-crystal structure refinement results indicate the presence of chromium at two sites (6c and 2b) of the available three metal Wyckoff sites, with a pronounced preference for the 6c site. An unexpected Rh/Ru site preference was found in the Ru-rich region only, leading to two different magnetic behaviors in the solid solution: The Rh-rich region shows a temperature-independent (Pauli) paramagnetism whereas an additional temperature-dependent paramagnetic component is found in the Ru-rich region.

On the transferability of electron density in binary vanadium borides VB, V3B4 and VB2.

PubMed

Terlan, Bürgehan; Akselrud, Lev; Baranov, Alexey I; Borrmann, Horst; Grin, Yuri

2015-12-01

Binary vanadium borides are suitable model systems for a systematic analysis of the transferability concept in intermetallic compounds due to chemical intergrowth in their crystal structures. In order to underline this structural relationship, topological properties of the electron density in VB, V3B4 and VB2 reconstructed from high-resolution single-crystal X-ray diffraction data as well as derived from quantum chemical calculations, are analysed in terms of Bader's Quantum Theory of Atoms in Molecules [Bader (1990). Atoms in Molecules: A Quantum Theory, 1st ed. Oxford: Clarendon Press]. The compounds VB, V3B4 and VB2 are characterized by a charge transfer from the metal to boron together with two predominant atomic interactions, the shared covalent B-B interactions and the polar covalent B-M interactions. The resembling features of the crystal structures are well reflected by the respective B-B interatomic distances as well as by ρ(r) values at the B-B bond critical points. The latter decrease with an increase in the corresponding interatomic distances. The B-B bonds show transferable electron density properties at bond critical points depending on the respective bond distances.

Production of scandium-44 m and scandium-44 g with deuterons on calcium-44: cross section measurements and production yield calculations.

PubMed

Duchemin, C; Guertin, A; Haddad, F; Michel, N; Métivier, V

2015-09-07

HIGHLIGHTS • Production of Sc-44 m, Sc-44 g and contaminants. • Experimental values determined using the stacked-foil technique. • Thick-Target production Yield (TTY) calculations. • Comparison with the TALYS code version 1.6.Among the large number of radionuclides of medical interest, Sc-44 is promising for PET imaging. Either the ground-state Sc-44 g or the metastable-state Sc-44 m can be used for such applications, depending on the molecule used as vector. This study compares the production rates of both Sc-44 states, when protons or deuterons are used as projectiles on an enriched Calcium-44 target. This work presents the first set of data for the deuteron route. The results are compared with the TALYS code. The Thick-Target production Yields of Sc-44 m and Sc-44 g are calculated and compared with those for the proton route for three different scenarios: the production of Sc-44 g for conventional PET imaging, its production for the new 3 γ imaging technique developed at the SUBATECH laboratory and the production of a Sc-44 m/Sc-44 g in vivo generator for antibody labelling.

Evaluation of stability region for scandium-containing rare-earth garnet single crystals and their congruent-melting compositions

NASA Astrophysics Data System (ADS)

Kaurova, I. A.; Domoroshchina, E. N.; Kuz'micheva, G. M.; Rybakov, V. B.

2017-06-01

Single crystals of scandium-containing rare-earth garnets in system R-Sc-C-O (R3+=Y, Gd; C3+=Al, Ga) have been grown by the Czochralski technique. X-ray diffraction analysis has been used to refine crystal compositions. The fundamental difference between the melt compositions and compositions of grown crystals has been found (except for compositions of congruent-melting compounds, CMC). The specific features of garnet solid solution formation have been established and the ternary diagrams with real or hypothetical phases have been built. The dinamics of coordination polyhedra changes with the formation of substitutional solid solutions have been proposed based on the mathematical modeling and experimental data. Possible existence of CMC with garnet structure in different systems as well as limit content of Sc ions in dodecahedral and octahedral sites prior to their partial substitution of ions, located in other sites, have been evaluated. It was established that the redistribution of cations over crystallographic sites (antistructural point defects) due to system self-organization to maintain its stability may be accompanied by cation ordering and the symmetry change of individual polyhedrons and/or the whole crystal.

Near Infrared Laser Spectroscopy of Scandium Monobromide

NASA Astrophysics Data System (ADS)

Xia, Ye; Cheung, A. S.-C.; Liao, Zhenwu; Yang, Mei; Chan, Man-Chor

2012-06-01

High resolution laser spectrum of scandium monobromide (ScBr) between 787 and 845 nm has been investigated using the technique of laser vaporization/reaction with free jet expansion and laser induced fluorescence spectroscopy. ScBr was produced by reacting laser vaporized Sc atoms with ethyl bromide (C2H5Br). Spectra of six vibrational bands of both Sc79Br and Sc81Br isotopomers of the C1 Σ+ - X1 Σ+ transition and seven vibrational bands of the e3 Δ - a3 Δ transition were obtained and analyzed. Least-squares fit of the measured line positions for the singlet transitions yielded accurate molecular constants for the v = 0 - 3 levels of the C1 Σ+ state and the v = 0 - 2 levels of the X1 Σ+ state. Similar least-squares fit for the triplet transitions yielded molecular constants for the v = 0 - 2 levels of both e3 Δ and a3 Δ states. The equilibrium bond length, r_0, of the a3 Δ state has been determined to be 2.4789 Å. Financial support from the Research Grants Council of the Hong Kong Special Administrative Region, China (Project No. HKU 701008P) is gratefully acknowledged

Mutual solubility of scandium oxide-hematite magnetic nanocomposites: Mössbauer spectroscopy investigation

NASA Astrophysics Data System (ADS)

Allwes, Mark; Mekaoui, Mehdi; Sorescu, Monica

2017-08-01

xSc2O3-(1-x)α-Fe2O3 (x = 0.1, 0.3 and 0.5) nanocomposite systems were successfully synthesized by mechanochemical activation of Sc2O3 and α-Fe2O3 mixtures for 0-12 h of ball milling time. Mössbauer investigations were performed to study the structural and magnetic properties of xSc2O3-(1-x)α-Fe2O3 nanoparticle systems during the mechanochemical activation treatment. The Mössbauer studies showed that the spectrum of the mechanochemically activated composites evolved from a sextet for hematite to sextets and a doublet upon duration of the milling process with scandium oxide. Mutual solubility was achieved at the nanoscopic level only. A comprehensive Mössbauer study was performed by recording the recoilless fraction f as function of the ball milling time using our dual absorber method. The results obtained indicate that prolonged ball milling times favor formation of the Fe:Sc2O3 non-magnetic phase and decrease of the grain sizes for both magnetic and non-magnetic components, leading to a maximum in the recoilless fraction followed by its decay.

Green and selective polycondensation methods toward linear sorbitol-based polyesters: enzymatic versus organic and metal-based catalysis.

PubMed

Gustini, Liliana; Lavilla, Cristina; Janssen, William W T J; Martínez de Ilarduya, Antxon; Muñoz-Guerra, Sebastián; Koning, Cor E

2016-08-23

Renewable polyesters derived from a sugar alcohol (i.e., sorbitol) were synthesized by solvent-free polycondensation. The aim was to prepare linear polyesters with pendant hydroxyl groups along the polymer backbone. The performance of the sustainable biocatalyst SPRIN liposorb CALB [an immobilized form of Candida antarctica lipase B (CALB); SPRIN technologies] and the organo-base catalyst 1,5,7-triazabicyclo[4,4,0]dec-5-ene (TBD) were compared with two metal-based catalysts: dibutyl tin oxide (DBTO) and scandium trifluoromethanesulfonate [also known as scandium triflate, Sc(OTf)3 ]. For the four catalytic systems, the efficiency and selectivity for the incorporation of sorbitol were studied, mainly using (13) C and (31) P NMR spectroscopies, whereas side reactions, such as ether formation and dehydration of sorbitol, were evaluated using MALDI-TOF-MS. Especially the biocatalyst SPRIN liposorb CALB succeeded in incorporating sorbitol in a selective way without side reactions, leading to close-to-linear polyesters. By using a renewable hydroxyl-reactive curing agent based on l-lysine, transparent and glossy poly(ester urethane) networks were successfully synthesized offering a tangible example of bio-based coatings. © 2016 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Vapor pressure and evaporation rate of certain heat-resistant compounds in a vacuum at high temperatures

NASA Technical Reports Server (NTRS)

Bolgar, A. S.; Verkhoglyadova, T. S.; Samsonov, G. V.

1985-01-01

The vapor pressure and evaporation rate of borides of titanium, zirconium, and chrome; and of strontium and carbides of titanium, zirconium, and chrome, molybdenum silicide; and nitrides of titanium, niobium, and tantalum in a vacuum were studied. It is concluded that all subject compounds evaporate by molecular structures except AlB sub 12' which dissociates, losing the aluminum.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Erdemir, Ali; Eryilmaz, Osman Levent; Urgen, Mustafa

A nanocomposite coating and method of making and using the coating. The nanocomposite coating is disposed on a base material, such as a metal or ceramic; and the nanocomposite consists essentially of a matrix of an alloy selected from the group of Cu, Ni, Pd, Pt and Re which are catalytically active for cracking of carbon bonds in oils and greases and a grain structure selected from the group of borides, carbides and nitrides.

LINER FOR EXTRUSION BILLET CONTAINERS

DTIC Science & Technology

Shrink-fit assembly device for buildup of ceramic-coated liner and sleeve assemblies was tested and modified to develop desired temperatures and...preliminary evaluation of suitability for extrusion liner use. Procedures were developed for welding short, hollow ceramic cylinders of high-strength metal...carbides and borides to form a ceramic extrusion liner of suitable length. Disassembly tooling for rapid separation of shrink-fitted sleeves from a worn

Precipitation hardening austenitic superalloys

DOEpatents

Korenko, Michael K.

1985-01-01

Precipitation hardening, austenitic type superalloys are described. These alloys contain 0.5 to 1.5 weight percent silicon in combination with about 0.05 to 0.5 weight percent of a post irradiation ductility enhancing agent selected from the group of hafnium, yttrium, lanthanum and scandium, alone or in combination with each other. In addition, when hafnium or yttrium are selected, reductions in irradiation induced swelling have been noted.

Correlation between thermodynamical stabilities of metal borohydrides and cation electronegativites: First-principles calculations and experiments

NASA Astrophysics Data System (ADS)

Nakamori, Yuko; Miwa, Kazutoshi; Ninomiya, Akihito; Li, Haiwen; Ohba, Nobuko; Towata, Shin-Ichi; Züttel, Andreas; Orimo, Shin-Ichi

2006-07-01

The thermodynamical stabilities for the series of metal borohydrides M(BH4)n ( M=Li , Na, K, Cu, Mg, Zn, Sc, Zr, and Hf; n=1-4 ) have been systematically investigated by first-principles calculations. The results indicated that an ionic bonding between Mn+ cations and [BH4]- anions exists in M(BH4)n , and the charge transfer from Mn+ cations to [BH4]- anions is a key feature for the stability of M(BH4)n . A good correlation between the heat of formation ΔHboro of M(BH4)n and the Pauling electronegativity of the cation χP can be found, which is represented by the linear relation, ΔHboro=248.7χP-390.8 in the unit of kJ/mol BH4 . In order to confirm the predicted correlation experimentally, the hydrogen desorption reactions were studied for M(BH4)n ( M=Li , Na, K, Mg, Zn, Sc, Zr, and Hf), where the samples of the later five borohydrides were mechanochemically synthesized. The thermal desorption analyses indicate that LiBH4 , NaBH4 , and KBH4 desorb hydrogen to hydride phases. Mg(BH4)2 , Sc(BH4)3 , and Zr(BH4)4 show multistep desorption reactions through the intermediate phases of hydrides and/or borides. On the other hand, Zn(BH4)2 desorbs hydrogen and borane to elemental Zn due to instabilities of Zn hydride and boride. A correlation between the desorption temperature Td and the Pauling electronegativity χP is observed experimentally and so χP is an indicator to approximately estimate the stability of M(BH4)n . The enthalpy change for the desorption reaction, ΔHdes , is estimated using the predicted ΔHboro and the reported data for decomposed product, ΔHhyd/boride . The estimated ΔHdes show a good correlation with the observed Td , indicating that the predicted stability of borohydride is experimentally supported. These results are useful for exploring M(BH4)n with appropriate stability as hydrogen storage materials.

Complete titanium substitution by boron in a tetragonal prism: exploring the complex boride series Ti(3-x)Ru(5-y)Ir(y)B(2+x) (0 ≤ x ≤ 1 and 1 < y < 3) by experiment and theory.

PubMed

Fokwa, Boniface P T; Hermus, Martin

2011-04-18

Polycrystalline samples and single crystals of four members of the new complex boride series Ti(3-x)Ru(5-y)Ir(y)B(2+x) (0 ≤ x ≤ 1 and 1 < y < 3) were synthesized by arc-melting the elements in a water-cooled copper crucible under an argon atmosphere. The new silvery phases were structurally characterized by powder and single-crystal X-ray diffraction as well as energy- and wavelength-dispersive X-ray spectroscopy analyses. They crystallize with the tetragonal Ti(3)Co(5)B(2) structure type in space group P4/mbm (No. 127). Tetragonal prisms of Ru/Ir atoms are filled with titanium in the boron-poorest phase (Ti(3)Ru(2.9)Ir(2.1)B(2)). Gradual substitution of titanium by boron then results in the successive filling of this site by a Ti/B mixture en route to the complete boron occupation, leading to the boron-richest phase (Ti(2)Ru(2.8)Ir(2.2)B(3)). Furthermore, both ruthenium and iridium share two sites in these structures, but a clear Ru/Ir site preference is found. First-principles density functional theory calculations (Vienna ab initio simulation package) on appropriate structural models (using a supercell approach) have provided more evidence on the stability of the boron-richest and -poorest phases, and the calculated lattice parameters corroborate very well with the experimentally found ones. Linear muffin-tin orbital atomic sphere approximation calculations further supported these findings through crystal orbital Hamilton population bonding analyses, which also show that the Ru/Ir-B and Ru/Ir-Ti heteroatomic interactions are mainly responsible for the structural stability of these compounds. Furthermore, some stable and unstable phases of this complex series could be predicted using the rigid-band model. According to the density of states analyses, all phases should be metallic conductors, as was expected from these metal-rich borides.

Scandium induced structural transformation and B′:B″ cationic ordering in Pb(Fe{sub 0.5}Nb{sub 0.5})O{sub 3} multiferroic ceramics

DOE Office of Scientific and Technical Information (OSTI.GOV)

Mallesham, B.; Ranjith, R., E-mail: ranjith@iith.ac.in; Manivelraja, M.

2014-07-21

The current study explores non-magnetic Sc{sup 3+} induced structural transformation, evolution of local B-site cation ordering and associated effect on ferroelectric phase transition temperature T{sub max} (temperature corresponding to dielectric maxima) on increasing the atom percent of Sc substitution in [Pb(Fe{sub 0.5}Nb{sub 0.5})O{sub 3} (PFN)] ceramics. In this regard, the phase pure Pb[(Fe{sub 0.5−x}Sc{sub x})Nb{sub 0.5}]O{sub 3} ceramics with x varying from 0 to 0.5 were synthesized through solid state reaction route. The detailed structural analysis through Rietveld refinement confirms the room temperature transformation from a monoclinic Cm to rhombohedral R3m structure at x = 0.3 mol. % of Sc. Absorption spectra studies showmore » that there is a considerable increment in the bandgap at higher scandium content. Most interestingly, the T{sub max} exhibited an increment for lower scandium contents (x = 0.1 to 0.25) followed by a drop in T{sub max} (x = 0.3 to 0.5). Such anomalous behavior in T{sub max} is expected to arise due to the onset of B′, B″ local cation ordering beyond Sc content x = 0.25. The B-site cation ordering at and beyond x = 0.3 was also confirmed by the evolution of cation order induced Pb-O coupled vibrational mode in Raman scattering studies. In addition, the Mössbauer spectra of PFN (x = 0) and Pb(Fe{sub 0.4}Sc{sub 0.1}Nb{sub 0.5})O{sub 3} (x = 0.1) are reported to verify the spin state and oxidation state of iron. The lattice distortion due to the radius ratio difference between a Sc{sup 3+} cation and Fe{sup 3+} cation in low spin state is responsible for the structural transformation, which in turn facilitates a B′:B″ cation ordering.« less

Ternary boride product and process

NASA Technical Reports Server (NTRS)

Clougherty, Edward V. (Inventor)

1976-01-01

A hard, tough, strong ceramic body is formed by hot pressing a mixture of a powdered metal and a powdered metal diboride. The metal employed is zirconium, titanium or hafnium and the diboride is the diboride of a different member of the same group of zirconium, titanium or hafnium to form a ternary composition. During hot pressing at temperatures above about 2,000.degree.F., a substantial proportion of acicular ternary monoboride is formed.

Mechanical, Electronic and Optical Properties of Two Phases of NbB4: First-Principles Calculations

NASA Astrophysics Data System (ADS)

Yang, Ruike; Ma, Shaowei; Wei, Qun; Zhang, Dongyun

2018-05-01

As transition metal borides have been successfully synthesised, the study of the combination of transition metal and boron is another effective way to investigate the properties of boride. We have predicted the novel phase Amm2-NbB4. Using the Cambridge Serial Total Energy Package (CASTEP) code, we further researched on the mechanical, electronic and optical properties of C2/c- and Amm2-NbB4. It is found that both the phases of NbB4 are dynamically and mechanically stable at 0 and 100 GPa. Their Vickers hardness values are both 34 GPa, which indicate that they are hard materials. The band gap of C2/c-NbB4 is 0.145 eV, which indicates that it is a semiconductor (or metalloid) at 0 GPa. For the Amm2-NbB4, the band structure without band gap indicates it is a metal at 0 GPa. The optical properties of these two structures are similar. At 0 eV, the real part of dielectric function is 28.8 for C2/c-NbB4, and the real part value for Amm2-NbB4 is 43. We hope our work will provide some help to the experimental work about the technology of the material.

A study of the microstructure of a rapidly solidified nickel-base superalloy modified with boron. M.S. Thesis. Final Contractor Report

NASA Technical Reports Server (NTRS)

Speck, J. S.

1986-01-01

The microstructures of melt-spun superalloy ribbons with variable boron levels have been studied by transmission electron microscopy. The base alloy was of approximate composition Ni-11% Cr-5%Mo-5%Al-4%Ti with boron levels of 0.06, 0.12, and 0.60 percent (all by weight). Thirty micron thick ribbons display an equiaxed chill zone near the wheel contact side which develops into primary dendrite arms in the ribbon center. Secondary dendrite arms are observed near the ribbon free surface. In the higher boron bearing alloys, boride precipitates are observed along grain boundaries. A concerted effort has been made to elucidate true grain shapes by the use of bright field/dark field microscopy. In the low boron alloy, grain shapes are often convex, and grain faces are flat. Boundary faces frequently have large curvature, and grain shapes form concave polygons in the higher boron level alloys. It is proposed that just after solidification, in all of the alloys studied, grain shapes were initially concave and boundaries were wavy. Boundary straightening is presumed to occur on cooling in the low boron alloy. Boundary migration is precluded in the higher boron alloys by fast precipitation of borides at internal interfaces.

Phosphors containing boron and metals of Group IIIA and IIIB

DOEpatents

Setlur, Anant Achyut; Srivastava, Alok Mani; Comanzo, Holly Ann; Manivannan, Venkatesan

2006-10-31

A phosphor comprises: (a) at least a first metal selected from the group consisting of yttrium and elements of lanthanide series other than europium; (b) at least a second metal selected from the group consisting of aluminum, gallium, indium, and scandium; (c) boron; and (d) europium. The phosphor is used in light source that comprises a UV radiation source to convert UV radiation to visible light.

Quantum Electronics in the UK. A National-Survey Conference.

DTIC Science & Technology

1985-10-30

flashlamp pumped chromium action, including transitions in dopants doped gadolinium /scandium/gallium garnet which have not previously shown laser lasers...frac- factors that limit performance. They ture. The Southampton scientists fabri - concluded that excited state absorption, cated the fibers by a...topics such as transverse power on the long wavelength side of a switching waves and cross-talk of bista- Fabry -Perot resonance peak at 844 nm, ble

Sc20C60: a volleyballene

NASA Astrophysics Data System (ADS)

Wang, Jing; Ma, Hong-Man; Liu, Ying

2016-06-01

An exceptionally stable hollow cage containing 20 scandium atoms and 60 carbon atoms has been identified. This Sc20C60 molecular cluster has a Th point group symmetry and a volleyball-like shape that we refer to below as ``Volleyballene''. Electronic structure analysis shows that the formation of delocalized π bonds between Sc atoms and the neighboring pentagonal rings made of carbon atoms is crucial for stabilizing the cage structure. A relatively large HOMO-LUMO gap (~1.4 eV) was found. The results of vibrational frequency analysis and molecular dynamics simulations both demonstrate that this Volleyballene molecule is exceptionally stable.An exceptionally stable hollow cage containing 20 scandium atoms and 60 carbon atoms has been identified. This Sc20C60 molecular cluster has a Th point group symmetry and a volleyball-like shape that we refer to below as ``Volleyballene''. Electronic structure analysis shows that the formation of delocalized π bonds between Sc atoms and the neighboring pentagonal rings made of carbon atoms is crucial for stabilizing the cage structure. A relatively large HOMO-LUMO gap (~1.4 eV) was found. The results of vibrational frequency analysis and molecular dynamics simulations both demonstrate that this Volleyballene molecule is exceptionally stable. Electronic supplementary information (ESI) available: Sc20C60: a Volleyballene_SI. See DOI: 10.1039/c5nr07784b

Aluminum-Scandium: A Material for Semiconductor Packaging

NASA Astrophysics Data System (ADS)

Geissler, Ute; Thomas, Sven; Schneider-Ramelow, Martin; Mukhopadhyay, Biswajit; Lang, Klaus-Dieter

2016-10-01

A well-known aluminum-scandium (Al-Sc) alloy, already used in lightweight sports equipment, is about to be established for use in electronic packaging. One application for Al-Sc alloy is manufacture of bonding wires. The special feature of the alloy is its ability to harden by precipitation. The new bonding wires with electrical conductivity similar to pure Al wires can be processed on common wire bonders for aluminum wedge/wedge (w/w) bonding. The wires exhibit very fine-grained microstructure. Small Al3Sc particles are the main reason for its high strength and prevent recrystallization and grain growth at higher temperatures (>150°C). After the wire-bonding process, the interface is well closed. Reliability investigations by active power cycling demonstrated considerably improved lifetime compared with pure Al heavy wires. Furthermore, the Al-Sc alloy was sputter-deposited onto silicon wafer to test it as chip metallization in copper (Cu) ball/wedge bonding technology. After deposition, the layers exhibited fine-grained columnar structure and small coherent Al3Sc particles with dimensions of a few nanometers. These particles inhibit softening processes such as Al splashing in fine wire bonding processes and increase the thickness of remnant Al under the copper balls to 85% of the initial thickness.

High-Performance, Solution-Processed Quantum Dot Light-Emitting Field-Effect Transistors with a Scandium-Incorporated Indium Oxide Semiconductor.

PubMed

He, Penghui; Jiang, Congbiao; Lan, Linfeng; Sun, Sheng; Li, Yizhi; Gao, Peixiong; Zhang, Peng; Dai, Xingqiang; Wang, Jian; Peng, Junbiao; Cao, Yong

2018-05-22

Light-emitting field-effect transistors (LEFETs) have attained great attention due to their special characteristics of both the switching capacity and the electroluminescence capacity. However, high-performance LEFETs with high mobility, high brightness, and high efficiency have not been realized due to the difficulty in developing high electron and hole mobility materials with suitable band structures. In this paper, quantum dot hybrid LEFETs (QD-HLEFETs) combining high-luminous-efficiency quantum dots (QDs) and a solution-processed scandium-incorporated indium oxide (Sc:In 2 O 3 ) semiconductor were demonstrated. The red QD-HLEFET showed high electrical and optical performance with an electron mobility of 0.8 cm 2 V -1 s -1 , a maximum brightness of 13 400 cd/m 2 , and a maximum external quantum efficiency of 8.7%. The high performance of the QD-HLEFET is attributed to the good energy band matching between Sc:In 2 O 3 and QDs and the balanced hole and electron injection (less exciton nonradiative recombination). In addition, incorporation of Sc into In 2 O 3 can suppress the oxygen vacancy and free carrier generation and brings about excellent current and optical modulation (the on/off current ratio is 10 5 and the on/off brightness ratio is 10 6 ).

DOE Office of Scientific and Technical Information (OSTI.GOV)

Radchenko, Valery; Engle, Jonathan Ward; Medvedev, Dmitri G.

Scandium-44 g (half-life 3.97 h) shows promise for application in positron emission tomography (PET), due to favorable decay parameters. One of the sources of 44gSc is the 44Ti/ 44gSc generator, which can conveniently provide this radioisotope on a daily basis at a diagnostic facility. Titanium-44 (half-life 60.0 a), in turn, can be obtained via proton irradiation of scandium metal targets. A substantial 44Ti product batch, however, requires high beam currents, long irradiation times and an elaborate chemical procedure for 44Ti isolation and purification. This study describes the production of a combined 175 MBq (4.7 mCi) batch yield of 44Ti inmore » week long proton irradiations at the Los Alamos Isotope Production Facility (LANL-IPF) and the Brookhaven Linac Isotope Producer (BNL-BLIP). A two-step ion exchange chromatography based chemical separation method is introduced: first, a coarse separation of 44Ti via anion exchange sorption in concentrated HCl results in a 44Tc/Sc separation factor of 10 2–10 3. A second, cation exchange based step in HCl media is then applied for 44Ti fine purification from residual Sc mass. In conclusion, this method yields a 90–97% 44Ti recovery with an overall Ti/Sc separation factor of ≥10 6.« less

Thermal, spectroscopic and laser properties of Nd3+ in gadolinium scandium gallium garnet crystal produced by optical floating zone method

NASA Astrophysics Data System (ADS)

Tian, Li; Wang, Shuxian; Wu, Kui; Wang, Baolin; Yu, Haohai; Zhang, Huaijin; Cai, Huaqiang; Huang, Hui

2013-12-01

A neodymium-doped gadolinium scandium gallium garnet (Nd:GSGG) single crystal with dimensions of Φ 5 × 20 mm2 has been grown by means of optical floating zone (OFZ). X-ray powder diffraction (XRPD) result shows that the as-grown Nd:GSGG crystal possesses a cubic structure with space group Ia3d and a cell parameter of a = 1.2561 nm. Effective elemental segregation coefficients of the Nd:GSGG as-grown crystal were calculated by using X-ray fluorescence (XRF). The thermal properties of the Nd:GSGG crystal were systematically studied by measuring the specific heat, thermal expansion and thermal diffusion coefficient, and the thermal conductivity of this crystal was calculated. The absorption and luminescence spectra of Nd:GSGG were measured at room temperature (RT). By using the Judd-Ofelt (J-O) theory, the theoretical radiative lifetime was calculated and compared with the experimental result. Continuous wave (CW) laser performance was achieved with the Nd:GSGG at the wavelength of 1062 nm when it was pumped by a laser diode (LD). A maximum output power of 0.792 W at 1062 nm was obtained with a slope efficiency of 11.89% under a pump power of 7.36 W, and an optical-optical conversion efficiency of 11.72%.

Method to produce catalytically active nanocomposite coatings

DOEpatents

Erdemir, Ali; Eryilmaz, Osman Levent; Urgen, Mustafa; Kazmanli, Kursat

2016-02-09

A nanocomposite coating and method of making and using the coating. The nanocomposite coating is disposed on a base material, such as a metal or ceramic; and the nanocomposite consists essentially of a matrix of an alloy selected from the group of Cu, Ni, Pd, Pt and Re which are catalytically active for cracking of carbon bonds in oils and greases and a grain structure selected from the group of borides, carbides and nitrides.

High-Temperature Ceramic Matrix Composite with High Corrosion Resistance

DTIC Science & Technology

2010-06-02

ceramics with silicide additives may be explained in the following ways: 1) metal oxide, for example Ta2O5, formed at oxidation of TaSi2, in the...practically monophase ones, possibly, the additives of corresponding metals in silicide powders were present in insignificant amounts. For...boride with zirconium silicide we prepared the mixtures with 20 vol. % of silicide , the latter being hot pressed in the temperature range of 1600

Computer Modeling of Ceramic Boride Composites

DTIC Science & Technology

2014-11-01

the reinforcer deform elastically, for the theoretical strength of the composite it can be written [46] BBBAAABBAAK EE δεδεσδσδσ +=+= (51) where...coefficients of thermal expansion. Approximately linear expansion coefficient of the composite is determined by the relation [52] EEE BBBAAAk...1 δαδαα ⋅+⋅= , (58) where AE and BE are Young moduli of components, and E – average modulus for composition BBAA EEE δδ

Ground State Structures of Boron-Rich Rhodium Boride: An Ab Initio Study

NASA Astrophysics Data System (ADS)

Chu, Bin-Hua; Zhao, Yuan; Yan, Jin-Liang; Li, Da

2018-01-01

Not Available Supported by the Natural Science Foundation of Shandong Province under Grant Nos ZR2016AP02, ZR2016FM38 and ZR2016EMP01, the Innovation Project of Ludong University under Grant No LB2016013, the Open Project of State Key Laboratory of Superhard Materials of Jilin University under Grant No 201605, and the National Natural Science Foundation of China under Grant Nos 11704170 and 61705097.

Investigation of the thermophysical properties of high-melting materials with the aid of a complex of instruments

NASA Technical Reports Server (NTRS)

Bolgar, A. S.; Gordiyenko, S. P.; Guseva, Y. A.; Turchanin, A. G.; Fenochka, B. V.; Fesenko, V. V.

1984-01-01

The evaporation rate, vapor pressure, heats of evaporation reaction (sublimation, dissociation), enthalpy, electrical resistance, heat capacity, emissivity, and heat conductivity of various carbides, borides, sulfides, nitrides, selenides, and phosphides were investigated. A set of high temperature high vacuum devices, calorimeters (designed for operation at 400 to 1300 K and from 1200 K), and mass spectrometers, most of which were specially developed for these studies, is described.

Nanocomposites for Electronic Applications. Volume 1

DTIC Science & Technology

1993-06-14

for a PZT thin film micro- motor using a rotating flexure wave generated in a PZT film on a silicon oxynitride diaphragm. The rotating wave has been...Solid State Science, The Pennsylvania State University (May 1992). 6. Jayne R. Giniewicz. "An Investigation of the Lead Scandium Tantalate-Lead...Materials and Structures, SPIE, Albuquerque, NM (February 1-4, 1993). 24. G. Harshe, J. P. Dougherty, and R. E. Newnham. "Theoretical Modelling of 3-0/0-3

Obsidian sources characterized by neutron-activation analysis.

PubMed

Gordus, A A; Wright, G A; Griffin, J B

1968-07-26

Concentrations of elements such as manganese, scandium, lanthanum, rubidium, samarium, barium, and zirconium in obsidian samples from different flows show ranges of 1000 percent or more, whereas the variation in element content in obsidian samples from a single flow appears to be less than 40 percent. Neutron-activation analysis of these elements, as well as of sodium and iron, provides a means of identifying the geologic source of an archeological artifact of obsidian.

Mineral resource of the month: rare earth elements

USGS Publications Warehouse

,

2011-01-01

The article provides information on rare earth elements, which are group of 17 natural metallic elements. The rare earth elements are scandium, yttrium and lanthanides and classified into light rare earth elements (LREE) and heavy rate earth elements (HREE). The principal ores of the rare earth elements are identified. An overview of China's production of 97 percent of the rare earths in the world is provided. Commercial applications of rare earths are described.

Origin of howardites, diogenites and eucrites - A mass balance constraint

NASA Technical Reports Server (NTRS)

Warren, P. H.

1985-01-01

Two petrogenetic models for the noncumulate-basaltic parts of howardite meteorites are discussed. A mass balance constraint is developed which indicates that more than half of the basaltic components in howardites formed as residual liquids from fractional crystallization of melts that had earlier produced diogentelike pyroxene cumulate components. Other model constriants involving scandium trends, clustering near olivine-pyroxene-plagioclase peritectic, and MgO/(MgO + FeO) ratios are discussed.

Cobalt and scandium partitioning versus iron content for crystalline phases in ultramafic nodules

USGS Publications Warehouse

Glassley, W.E.; Piper, D.Z.

1978-01-01

Fractionation of Co and Sc between garnets, olivines, and clino- and orthopyroxenes, separated from a suite of Salt Lake Crater ultramafic nodules that equilibrated at the same T and P, is strongly dependent on Fe contents. This observation suggests that petrogenetic equilibrium models of partial melting and crystal fractionation must take into account effects of magma composition, if they are to describe quantitatively geochemical evolutionary trends. ?? 1978.

Cr-doped scandium borate laser

DOEpatents

Chai, Bruce H.; Lai, Shui T.; Long, Margaret N.

1989-01-01

A broadly wavelength-tunable laser is provided which comprises as the laser medium a single crystal of MBO.sub.3 :Cr.sup.3+, where M is selected from the group of Sc, In and Lu. The laser may be operated over a broad temperature range from cryogenic temperatures to elevated temperatures. Emission is in a spectral range from red to infrared, and the laser is useful in the fields of defense, communications, isotope separation, photochemistry, etc.

Feasibility study of the welding of SiC

NASA Technical Reports Server (NTRS)

Moore, T. J.

1985-01-01

In a brief study of the feasibility of welding sintered alpha-SiC, solid-state welding and brazing were investigated. Joint quality was determined solely by microstructural examination. Hot-pressure welding was shown to be feasible at 1950 C. Diffusion welding and brazing were also successful under hot isostatic pressure at 1950 C when boride, carbide, and silicide interlayers were used. Furnace brazing was accomplished at 1750 C when a TiSi2 interlayer was introduced.

Titanium Diboride Electrodeposited Coatings

DTIC Science & Technology

1977-06-01

4 Ti02. This material was deposited in the form of a porous mass or loose particles which must be leached in water and acid to remove adherent...poudres metallique par electrolyse ignee. Revue de Metallurgie, v. 45, 1948, p. 49-59. 7. POWELL, C. F. Borides in High Temperature Materials and... water solution of thallium formate-thallium malonate 50-50 mole percent mixture with a density ranging from about 5 g/cm^ at the bottom to about 2 g/cm

METHOD OF PROTECTING TANTALUM CRUCIBLES AGAINST REACTION WITH MOLTEN URANIUM

DOEpatents

Feder, H.M.; Chellew, N.R.

1960-08-16

Tantalum crucibles against reaction with molten uranium by contacting the surfaces to be protected with metallic boron (as powder, vapor, or suspension in a liquid-volatilenonreacting medium, such as acetone and petroleum oil) at about 1800 deg C in vacuum, discontinuing contact with the boron, and heating the crucibles to a temperature of between 1800 aad 2000 deg C, whereby the tantalum boride formed in the first heating step is converted to tantalum monoboride.

Alumina-based ceramic composite

DOEpatents

Alexander, Kathleen B.; Tiegs, Terry N.; Becher, Paul F.; Waters, Shirley B.

1996-01-01

An improved ceramic composite comprising oxide ceramic particulates, nonoxide ceramic particulates selected from the group consisting of carbides, borides, nitrides of silicon and transition metals and mixtures thereof, and a ductile binder selected from the group consisting of metallic, intermetallic alloys and mixtures thereof is described. The ceramic composite is made by blending powders of the ceramic particulates and the ductile to form a mixture and consolidating the mixture of under conditions of temperature and pressure sufficient to produce a densified ceramic composite.

Preliminary investigation of zirconium boride ceramals for gas-turbine blade applications

NASA Technical Reports Server (NTRS)

Hoffman, Charles A

1953-01-01

Zirconium boride ZrB2 ceramals were investigated for possible gas-turbine-blade application. Included in the study were thermal shock evaluations of disks, preliminary turbine-blade operation, and observations of oxidation resistance. Thermal shock disks of the following three compositions were studied: (a) 97.5 percent ZrB2 plus 2.5 percent B by weight; (b) 92.5 percent ZrB2 plus 7.5 percent B by weight; and (c) 100 percent ZrB2. Thermal shock disks were quenched from temperatures of 1800 degrees, 2000 degrees, 2200 degrees, and 2400 degrees F. The life of turbine blades containing 93 percent ZrB2 plus 7 percent B by weight was determined in gas-turbine tests. The blades were run at approximately 1600 degrees F and 15,000 to 26,000 rpm. The thermal shock resistance of the 97.5 percent ZrB2 plus 2.5 percent boron ceramals compares favorably with that of TiC plus Co and TiC plus Ni ceramals. Oxidation of the disks during the thermal shock evaluation was slight for the comparatively short time (8.3 hr) up through 2000 degrees F. Oxidation of a specimen was severe, however, after 100 hours at 2000 degrees F. The turbine blade performance evaluation of the 93 percent ZrB2 plus 7 percent B composition was preliminary in scope ; no conclusions can be drawn.

Probing the superconducting ground state of the rare-earth ternary boride superconductors R RuB2 (R = Lu,Y) using muon-spin rotation and relaxation

NASA Astrophysics Data System (ADS)

Barker, J. A. T.; Singh, R. P.; Hillier, A. D.; Paul, D. McK.

2018-03-01

The superconductivity in the rare-earth transition-metal ternary borides R RuB2 (where R =Lu and Y) has been investigated using muon-spin rotation and relaxation. Measurements made in zero field suggest that time-reversal symmetry is preserved upon entering the superconducting state in both materials; a small difference in depolarization is observed above and below the superconducting transition in both compounds, however, this has been attributed to quasistatic magnetic fluctuations. Transverse-field measurements of the flux-line lattice indicate that the superconductivity in both materials is fully gapped, with a conventional s -wave pairing symmetry and BCS-like magnitudes for the zero-temperature gap energies. The electronic properties of the charge carriers in the superconducting state have been calculated, with effective masses m*/me=9.8 ±0.1 and 15.0 ±0.1 in the Lu and Y compounds, respectively, with superconducting carrier densities ns=(2.73 ±0.04 ) ×1028m-3 and (2.17 ±0.02 ) ×1028m-3 . The materials have been classified according to the Uemura scheme for superconductivity, with values for Tc/TF of 1 /(414 ±6 ) and 1 /(304 ±3 ) , implying that the superconductivity may not be entirely conventional in nature.

The Reactivity of Transition Metal-Silicon Compounds

DTIC Science & Technology

1988-08-08

light, and appear to follow both thermal and photochemical pathways. Compounds 9 and 10 are efficient acetylene polymerization catalysts . The scandium...containing both silicon and an early-transition- metal, Previously this field was quite undeveloped, therefore we surveyed a number ( approaches to...15- C5Me5)Ta(SiMe 3)C13 ," J Arnold and T D Tilley, J Am Chem Soc, 107, 6409 (1985) "Tetrahedral Lewis Base Adducts of an Acyl. Preparation and X-ray

High-Efficiency Silicon Carbide (SiC) Converters. Delivery Order 0001: Development of High-Temperature, High-Power, High-Efficiency, High-Voltage Converters Using Silicon Carbide

DTIC Science & Technology

2004-03-01

32 Silicon Dioxide as a Mask ......................................................... 34 Silicon Nitride as a Mask...phosphorous (P), and arsenic (As) for n-type material and aluminum (Al), boron (B), beryllium (Be), gallium (Ga), oxygen (O), and scandium (Sc) for...O2 in carbon tetrafluoride (CF4), nitrogen trifluoride (NF3), and sulfur hexafluoride (SF6) were observed because these gases produce high fluorine

A general method for the catalytic nazarov cyclization of heteroaromatic compounds.

PubMed

Malona, John A; Colbourne, Jessica M; Frontier, Alison J

2006-11-23

A general, catalytic method for efficient Nazarov cyclization of systems containing heteroaromatic components has been developed. Scandium triflate was identified as the most reactive promoter, and it was found that addition of lithium perchlorate was necessary for synthetically useful catalytic cyclizations. The method was used to synthesize a range of cyclopentanone-fused heteroaromatic systems in 36-97% yield, and the reactivity trends observed demonstrate the impact of polarization on cyclization efficiency. [reaction: see text].

In the presence of fluoride, free Sc³⁺ is not a good predictor of Sc bioaccumulation by two unicellular algae: possible role of fluoro-complexes.

PubMed

Crémazy, Anne; Campbell, Peter G C; Fortin, Claude

2014-08-19

We investigated the effect of fluoride complexation on scandium accumulation by two unicellular algae, Chlamydomonas reinhardtii and Pseudokirchneriella subcapitata. This trivalent metal was selected for its chemical similarities with aluminum and for its convenient radioisotope (Sc-46), which can be used as a tracer in short-term bioaccumulation studies. Scandium surface-bound concentrations (Sc(ads)) and uptake fluxes (J(int)) were estimated in the two algae over short-term (<1 h) exposures at pH 5 and in the presence of 0 to 40 μM F(-). Although the computed proportion of dissolved Sc(3+) dropped from 20% to 0.01% over this [F(-)] range, Sc(ads) and J(int) values for both algae decreased only slightly, suggesting a participation of Sc fluoro-complexes in both processes. Surface adsorption and uptake of fluoride complexes with aluminum have been reported in the literature. These observations are not taken into account by current models for trace metal bioaccumulation (e.g., the biotic ligand model). Results from a previous study, where the effects of pH on Sc uptake were investigated, suggested that Sc hydroxo-complexes were internalized by C. reinhardtii. There is thus growing evidence that the free ion concentration may not be adequate to predict the accumulation of Sc (and potentially of other trivalent metals) in aquatic organisms.

The effect of an erbium, chromium: yttrium-scandium-gallium-garnet laser on the microleakage and bond strength of silorane and micro-hybrid composite restorations

PubMed Central

Korkmaz, Fatih Mehmet; Baygin, Ozgul; Tuzuner, Tamer; Bagis, Bora; Arslan, Ipek

2013-01-01

Objective: The aim of this in vitro study was to compare the microleakage and bond strength of Class V silorane-based and universal micro-hybrid composite restorations prepared either with diamond bur or with an erbium, chromium: yttrium-scandium-gallium-garnet (Er, Cr:YSGG) laser. Materials and Methods: A total of 160 molar teeth were used for microleakage assessment and shear bond strength (SBS) test. The specimens were prepared using either diamond bur or 3 W-, 4 W- and 5 W-20 Hz Er, Cr:YSGG laser irradiation. All specimens were subjected to thermocycling (500 times at 5 ± 2°C to 55 ± 2°C, dwell time 15 s and transfer time 10 s). Microleakage was assessed using a 0.5% basic-fuchsin solution. The bond strengths were determined using a microtensile tester at a crosshead speed of 0.5 mm/min. The Kruskal Wallis test was used for the analysis of microleakage and a one-way analysis of variance test was used to analyze the SBS (P < 0.05). Results: No statistically significant differences were found (P > 0.05) between Er, Cr:YSGG laser and bur preparation methods regarding microleakage and bond strength values. Conclusion: Irradiation with Er, Cr:YSGG laser was confirmed to be as effective as conventional methods for preparing cavities before adhesive restorations. PMID:24966726

Optimization of reaction conditions for the radiolabeling of DOTA and DOTA-peptide with (44m/44)Sc and experimental evidence of the feasibility of an in vivo PET generator.

PubMed

Huclier-Markai, S; Kerdjoudj, R; Alliot, C; Bonraisin, A C; Michel, N; Haddad, F; Barbet, J

2014-05-01

Among the number of generator systems providing radionuclides with decay parameters promising for imaging and treatment applications, there is the (44)Ti (T1/2=60 years)/(44)Sc (T1/2=3.97 h) generator. This generator provides a longer-lived daughter for extended PET/CT measurements compared to the chemically similar system (68)Ge/(68)Ga. Scandium also exists as (47)Sc, a potential therapeutic radionuclide. It is possible to produce (44)Sc in a cyclotron using, for example, the (44)Ca (d, n) (44)Sc nuclear reaction. In that case, the isomeric state (44 m)Sc (T1/2=58.6h) is co-produced and may be used as an in vivo(44 m)Sc/(44)Sc generator. The aim of this study is to evaluate the feasibility of this in vivo(44 m)Sc/(44)Sc generator and to demonstrate that the daughter radionuclide stays inside the chelator after decay of the parent radionuclide. Indeed, the physico-chemical process occurring after the primary radioactive decay (EC, IT, Auger electron …) has prevented in many cases the use of in-vivo generator, because of the post-effect as described in the literature. The DOTA macrocyclic ligand forms stable complexes with many cations and has been shown to be the most suitable chelating moiety for scandium. Initially, the radiolabeling of DOTA and a DOTA-peptide (DOTATATE) with Sc was performed and optimized as a function of time, pH, metal-to-ligand ratio and temperature. Next, the physico-chemical processes that could occur after the decay (post-effect) were studied. (44 m)Sc(III)-labeled DOTA-peptide was quantitatively adsorbed on a solid phase matrix through a hydrophobic interaction. Elutions were then performed at regular time intervals using a DTPA solution at various concentrations. Finally, the radiolabelled complex stability was studied in serum. Radiolabeling yields ranged from 90% to 99% for metal-to-ligand ratio ranging from 1:10 to 1:500 for DOTA or DOTATATE respectively. The optimum physico-chemical parameters were pH=4-6, t=20 min, T=70°C. Then, the (44 m)Sc-DOTATATE complex, radiolabeled at 98%, was adsorbed through a hydrophobic interaction to a solid phase. Unlabeled scandium was completely eluted from the column whereas the Sc-DOTATATE complex was 100% retained. The release of (44)Sc from the complex due to decay was less than 1% over 2 periods of (44 m)Sc, independent of the DTPA concentration used for elution. (44 m)Sc/(44)Sc-DOTATATE was stable in serum over 72 h. The results indicate that the decay of (44 m)Sc to (44)Sc does not affect the integrity of the radiolabeled compound. Thus the (44 m)Sc/(44)Sc generator is chemically valid and stable in serum. It could be used for PET imaging as an in-vivo generator increasing the life time of the scandium and allowing the use of antibody as labelled compound. Further in-vivo biological evaluations should complete this work. Copyright © 2014 Elsevier Inc. All rights reserved.

Method of making a light weight battery plaque

NASA Technical Reports Server (NTRS)

Reid, M. A.; Post, R. E.; Soltis, D. G. (Inventor)

1984-01-01

A nickel plaque which may be coated with a suitable metal or compound to make an electrode for a fuel cell or battery is fabricated by directing nickel sensitizer, catalyst and plating solutions through a porous plastic substrate in the order named and at prescribed temperatures and flow rates. A boride compound dissolved in the plating solution decreases the electrical resistance of the plaque. Certain substrates may require treatment in an alkali solution to dissolve filler materials thereby increasing porosity to a required 65%.

Development of a method for fabricating metallic matrix composite shapes by a continuous mechanical process

NASA Technical Reports Server (NTRS)

Divecha, A. P.

1974-01-01

Attempts made to develop processes capable of producing metal composites in structural shapes and sizes suitable for space applications are described. The processes must be continuous and promise to lower fabrication costs. Special attention was given to the aluminum boride (Al/b) composite system. Results show that despite adequate temperature control, the consolidation characteristics did not improve as expected. Inadequate binder removal was identified as the cause responsible. An Al/c (aluminum-graphite) composite was also examined.

Identification of thermodynamically stable ceramic reinforcement materials for iron aluminide matrices

NASA Technical Reports Server (NTRS)

Misra, Ajay K.

1990-01-01

Aluminide-base intermetallic matrix composites are currently being considered as potential high-temperature materials. One of the key factors in the selection of a reinforcement material is its chemical stability in the matrix. In this study, chemical interactions between iron aluminides and several potential reinforcement materials, which include carbides, oxides, borides, and nitrides, are analyzed from thermodynamic considerations. Several chemically compatible reinforcement materials are identified for the iron aluminides with Al concentrations ranging from 40 to 50 at. pct.

The Physics and Chemistry of carbides, Nitrides and Borides. Volume 185

DTIC Science & Technology

1990-01-01

and C-B-C chains [15,17]. Clearly, the use of boron-rich solids as electronic materials will place new demands on the quality of materials. In this...first heated in a pyrolytic boron nitride (PBN) crucible ( Union Carbide Corp.) under high vacuum (< 50 mTorr) to 1900°C. This removed surface...contamination of the sample. The powders were loaded into a graphite die with a high-purity BN die liner ( Union Carbide Grade HBC) with inner diameter of 3/8

Alumina-based ceramic composite

DOEpatents

Alexander, K.B.; Tiegs, T.N.; Becher, P.F.; Waters, S.B.

1996-07-23

An improved ceramic composite comprising oxide ceramic particulates, nonoxide ceramic particulates selected from the group consisting of carbides, borides, nitrides of silicon and transition metals and mixtures thereof, and a ductile binder selected from the group consisting of metallic, intermetallic alloys and mixtures thereof is described. The ceramic composite is made by blending powders of the ceramic particulates and the ductile to form a mixture and consolidating the mixture of under conditions of temperature and pressure sufficient to produce a densified ceramic composite. 5 figs.

Anti-scratch AlMgB14 Gorilla® Glass coating

NASA Astrophysics Data System (ADS)

Putrolaynen, V. V.; Grishin, A. M.; Rigoev, I. V.

2017-10-01

Hard aluminum-magnesium boride (BAM) films were fabricated onto Corning® Gorilla® Glass by radio-frequency magnetron sputtering of a single stoichiometric AlMgB14 target. BAM films exhibit a Vickers hardness from 10 to 30 GPa and a Young's modulus from 80 to 160 GPa depending on applied loading forces. Deposited hard coating increases the critical load at which glass substrate cracks. The adhesion energy of BAM films on Gorilla® Glass is 6.4 J/m2.

Synthesis and properties of nickel cobalt boron nanoparticles

NASA Astrophysics Data System (ADS)

Patel, J.; Pankhurst, Q. A.; Parkin, I. P.

2005-01-01

Amorphous cobalt nickel boride nanoparticles were synthesised by chemical reduction synthesis in aqueous solution. Careful control of synthesis conditions and post reaction oxidation enabled the nanoparticles to be converted into a core-shell structure comprising of an amorphous Co-Ni-B core and an outer metal oxide sheet. These particles had interesting magnetic properties including saturation magnetisations and coercivities of the order of 80 emu/g and 170 Oe respectively, making them suitable for a potential use as an exchange-pinned magnetic material.

Identification of New Potential Scientific and Technology Areas for DoD Application. Summary of Activities

DTIC Science & Technology

1983-08-02

laser, a Cr3+-Nd 3 + gadolinium-scandium- gallium- garnet (GSGG) crystal, reputedly having three 15 times the slope efficiency of an equivalent... garnet , lithium gallium garnet , and lanthium-lutetium gallium garnet . Dr. Cooper asked for an indication of what it might take to put a program together in...Langmuir-Blodgett films , a subject mostly pursued in the U. K. Two groups, one at the University of California, San Diego (UCSD) (contact: Professor W

[Leaching of Rare Earth Elements from Coal Ashes Using Acidophilic Chemolithotrophic Microbial Communities].

PubMed

Muravyov, M I; Bulaev, A G; Melamud, V S; Kondrat'eva, T F

2015-01-01

A method for leaching rare earth elements from coal ash in the presence of elemental sulfur using communities of acidophilic chemolithotrophic microorganisms was proposed. The optimal parameters determined for rare element leaching in reactors were as follows: temperature, 45 degrees C; initial pH, 2.0; pulp density, 10%; and the coal ash to elemental sulfur ratio, 10 : 1. After ten days of leaching, 52.0, 52.6, and 59.5% of scandium, yttrium, and lanthanum, respectively, were recovered.

Thermophysical Properties of Matter - The TPRC Data Series. Volume 4. Specific Heat - Metallic Elements and Alloys

DTIC Science & Technology

1971-01-01

alloys— sodium — sodium alloya— solder—carbon ateels—chromium steels—silicon steels—tantalum—tantalum alloys—terbium—thallium—thallium alloys—thorium...Praseodymium 45 Rhenium 46 Rhodium 47 Rubidium 48 Ruthenium 4» Samarium 50 Scandium 51 Selenium 52 Silicon 5:i Silver 54 Sodium 55 Strontium 56...Potassium ♦ Sodium 111 Sodium * Potassium 112 Tantalum ♦ Tungsten 113 Thallium + Lead, PbTl| 114 Tin ♦ Bismuth 115 Tin ♦ Indium 116 Tin+ Lead 117

Titanium(IV)-Catalyzed Stereoselective Synthesis of Spirooxindole-1-pyrrolines

PubMed Central

2015-01-01

A stereoselective cyclization between alkylidene oxindoles and 5-methoxyoxazoles has been developed using catalytic titanium(IV) chloride (as low as 5 mol %) to afford spiro[3,3′-oxindole-1-pyrrolines] in excellent yield (up to 99%) and diastereoselectivity (up to 99:1). Using a chiral scandium(III)–indapybox/BArF complex affords enantioenriched spirooxindole-1-pyrrolines where a ligand-induced reversal of diastereoselectivity is observed. This methodology is further demonstrated for the synthesis of pyrrolines from malonate alkylidene and coumarin derivatives. PMID:25474118

High rate buffer layer for IBAD MgO coated conductors

DOEpatents

Foltyn, Stephen R [Los Alamos, NM; Jia, Quanxi [Los Alamos, NM; Arendt, Paul N [Los Alamos, NM

2007-08-21

Articles are provided including a base substrate having a layer of an oriented material thereon, and, a layer of hafnium oxide upon the layer of an oriented material. The layer of hafnium oxide can further include a secondary oxide such as cerium oxide, yttrium oxide, lanthanum oxide, scandium oxide, calcium oxide and magnesium oxide. Such articles can further include thin films of high temperature superconductive oxides such as YBCO upon the layer of hafnium oxide or layer of hafnium oxide and secondary oxide.

Radiationless Transitions and Excited-State Absorption of Low-Field Chromium Complexes in Solids

DTIC Science & Technology

1989-07-20

host-lattice modes and, in the case of the scandium compound with 5 % chromium concentration, of the a and tIg 2g localized modes. The local-mode...Radiationless transitions and excited-state Final report I/I/86-5/31/89 absorption of low-field chromium complexes 6. PERFORMING ORG. REPORT NUMBER ( 1 in...complexes, chromium ; tunable lasers, high pressure,-photoluminescence 4. 26, AMTVrAC? (Cbm e @CAP N Igemem’ a IdoMit’ by block nambew) The continuation of a

Features of surface phase formation during case-hardening of iron- and titanium-based alloys

NASA Astrophysics Data System (ADS)

Vintaikin, B. E.; Kamynin, A. V.; Kraposhin, V. S.; Smirnov, A. E.; Terezanova, K. V.; Cherenkova, S. A.; Sheykina, V. I.

2017-11-01

The article provides a detailed analysis of formation features for surface phases in technical iron and Cr20-Ni80 alloy samples that undergo case-hardening at a temperature of 850°C for 2, 4 and 6 hours of saturation in two different environments: acetylene, and molten salt consisting of sodium tetraborate and amorphous boron. We carried out an X-ray phase analysis to determine the phase structure of surface material layers that formed as a result of the case-hardening process. We discovered that after carburising it was possible to detect Fe3C and Fe-α phases on the surface of technical iron samples, and after boriding we found FeB, Fe2B and Fe3B phases; we noted a lack of characteristic Fe-α and Fe-γ peaks on the X-ray diffraction pattern. We detected many different phases in the Cr20-Ni80 alloy after the same type of case-hardening. Titanium oxides appeared after case-hardening of titanium in air at 800°C. We provide data on surface structure of samples subjected to vacuum carburising: over a 2 to 6 hour interval, the layer thickness is a parabolic function of time. When carrying out electrolysis-free liquid boriding, increasing exposure time from 2 to 6 hours alters the thickness of the strengthened layer only slightly, so, when carrying out case-hardening, it is less efficient to increase saturation time in molten salt containing sodium tetraborate and amorphous boron.

Role of atomic bonding for compound and glass formation in Ni-Si, Pd-Si, and Ni-B systems

NASA Astrophysics Data System (ADS)

Tanaka, K.; Saito, T.; Suzuki, K.; Hasegawa, R.

1985-11-01

Valence electronic structures of crystalline compounds and glassy alloys of Ni silicides, Pd silicides, and Ni borides are studied by soft-x-ray spectroscopy over wide ranges of Si and B concentrations. The samples prepared include bulk compounds, glassy ribbons, and amorphous sputtered films. Silicon Kβ emissions of Ni and Pd silicides generally consist of a prominent peak fixed at ~=4.5 and ~=5.8 eV below the Fermi level EF, respectively, with a shoulder near EF which grows and shifts toward lower energy with increasing Si concentration. The former is identified as due to Si p-like states forming Si 3p-Ni 3d or Si 3p-Pd 4d bonding states while the latter as due to the corresponding antibonding states. Ni L3 and Pd L3 emissions of these silicides indicate that Ni 3d and Pd 4d states lie between the above two states. These local electronic configurations are consistent with partial-density-of-states (PDOS) calculations performed by Bisi and Calandra. Similar electronic configurations are suggested for Ni borides from B Kα and Ni L3 emissions. Differences of emission spectra between compounds and glasses of similar compositions are rather small, but some enhancement of the contribution of antibonding states to the PDOS near EF is suggested for certain glasses over that of the corresponding compounds. These features are discussed in connection with the compound stability and glass formability.

The effect of scandium addition on microstructure and mechanical properties of Al–Si–Mg alloy: A multi-refinement modifier

DOE Office of Scientific and Technical Information (OSTI.GOV)

Xu, Cong, E-mail: xucong55555@gmail.com; Xiao, Wenlong, E-mail: wlxiao@buaa.edu.cn; Hanada, Shuji

2015-12-15

Effect of scandium (Sc) additions on the microstructure, mechanical properties and fracture behavior of Al–Si–Mg casting alloy (F357) were systematically investigated. It was found that Sc addition caused a multi-refining efficiency on the microstructure of as-cast F357 alloy, including refinement of grains and secondary dendrite arm spacing (SDAS), modification of eutectic Si and harmless disposal of β-Al{sub 5}FeSi phase. Subsequent T6 heat treatment had further induced the complete spheroidization of eutectic Si and precipitation of fine secondary Al{sub 3}Sc dispersoids in the Sc modified alloys. Thus the mechanical properties, especially the ductility, were significantly enhanced by the addition of Scmore » combined with the heat treatment. The highest ultimate tensile strength, yield strength and elongation were achieved in 0.8 wt.% Sc modified F357 alloy combined with T6 heat treatment. Furthermore, fractographic examinations indicated that the ductile fracture mechanism served as a dominate role in the modified alloys due to the formation of fine, deep and uniformly distributed dimples. - Highlights: • Detailed characterization of the multi-refining microstructure of Sc modified F357 alloy was performed. • The multi-refinement was proposed to refine grain and SDAS, modify eutectic Si and β-phase. • Sc modifier combined with T6 treatment is effective in improving tensile properties. • Modification of eutectic Si in F357 alloy with Sc is consistent with the IIT mechanism.« less

Responses of trace elements to aerobic maximal exercise in elite sportsmen.

PubMed

Otag, Aynur; Hazar, Muhsin; Otag, Ilhan; Gürkan, Alper Cenk; Okan, Ilyas

2014-02-21

Trace elements are chemical elements needed in minute quantities for the proper growth, development, and physiology of the organism. In biochemistry, a trace element is also referred to as a micronutrient. Trace elements, such as nickel, cadmium, aluminum, silver, chromium, molybdenum, germanium, tin, titanium, tungsten, scandium, are found naturally in the environment and human exposure derives from a variety of sources, including air, drinking water and food. The Purpose of this study was investigated the effect of aerobic maximal intensity endurance exercise on serum trace elements as well-trained individuals of 28 wrestlers (age (year) 19.64±1.13, weight (Kg) 70.07 ± 15.69, height (cm) 176.97 ± 6.69) during and after a 2000 meter Ergometer test protocol was used to perform aerobic (75 %) maximal endurance exercise. Trace element serum levels were analyzed from blood samples taken before, immediately after and one hour after the exercise. While an increase was detected in Chromium (Cr), Nickel (Ni), Molybdenum (Mo) and Titanium (Ti) serum levels immediately after the exercise, a decrease was detected in Aluminum (Al), Scandium (Sc) and Tungsten (W) serum levels. Except for aluminum, the trace elements we worked on showed statistically meaningful responses (P < 0.05 and P < 0.001). According to the responses of trace elements to the exercise showed us the selection and application of the convenient sport is important not only in terms of sportsman performance but also in terms of future healthy life plans and clinically.

Evaluation of microtensile and tensile bond strength tests determining effects of erbium, chromium: yttrium-scandium-gallium-garnet laser pulse frequency on resin-enamel bonding.

PubMed

Yildirim, T; Ayar, M K; Yesilyurt, C; Kilic, S

2016-01-01

The aim of the present study was to compare two different bond strength test methods (tensile and microtensile) in investing the influence of erbium, chromium: yttrium-scandium-gallium-garnet (Er, Cr: YSGG) laser pulse frequency on resin-enamel bonding. One-hundred and twenty-five bovine incisors were used in the present study. Two test methods were used: Tensile bond strength (TBS; n = 20) and micro-TBS (μTBS; n = 5). Those two groups were further split into three subgroups according to Er, Cr: YSGG laser frequency (20, 35, and 50 Hz). Following adhesive procedures, microhybrid composite was placed in a custom-made bonding jig for TBS testing and incrementally for μTBS testing. TBS and μTBS tests were carried out using a universal testing machine and a microtensile tester, respectively. Analysis of TBS results showed that means were not significantly different. For μTBS, the Laser-50 Hz group showed the highest bond strength (P < 0.05), and increasing frequency significantly increased bond strength (P < 0.05). Comparing the two tests, the μTBS results showed higher means and lower standard deviations. It was demonstrated that increasing μTBS pulse frequency significantly improved immediate bond strength while TBS showed no significant effect. It can, therefore, be concluded that test method may play a significant role in determining optimum laser parameters for resin bonding.

Application of reflectance confocal microscopy to evaluate skin damage after irradiation with an yttrium-scandium-gallium-garnet (YSGG) laser.

PubMed

Yue, Xueping; Wang, Hongwei; Li, Qing; Li, Linfeng

2017-02-01

The objective of this study was to observe the characteristics of the skin after irradiation with a 2790-nm yttrium-scandium-gallium-garnet (YSGG) laser using reflectance confocal microscopy (RCM). A 2790-nm YSGG laser was used to irradiate fresh foreskin (four doses, at spot density 3) in vitro. The characteristics of microscopic ablative columns (MAC), thermal coagulation zone (TCZ), and microscopic treatment zones (MTZ) were observed immediately after irradiation using digital microscope and RCM. The characteristics of MAC, TCZ, and MTZ with variations in pulse energy were comparatively analyzed. After irradiation, MAC, TCZ, and MTZ characteristics and undamaged skin between MTZs can be observed by RCM. The depth and width of MTZ obviously increased with the increase in pulse energy. At 80, 120, and 160 mJ/microbeam (MB), the MTZ actual area and proportion were about two times that of the theoretical value and three times at 200 mJ/MB. With increases in depth, the single MAC gradually decreased in a fingertip-shaped model, with TCZ slowly increasing, and MTZ slightly decreasing in a columnar shape. RCM was able to determine the characteristics of thermal injury on the skin after the 2790-nm YSGG laser irradiation with different pulse energies. Pulse energy higher than 200 mJ/MB may have much larger thermal injury and side effect. RCM could be used in the clinic in future.

Pulpal thermal responses to an erbium,chromium: YSGG pulsed laser hydrokinetic system.

PubMed

Rizoiu, I; Kohanghadosh, F; Kimmel, A I; Eversole, L R

1998-08-01

Laser systems are known to raise pulpal temperatures when applied to tooth surfaces. Dental biocalcified tissues can be cut with an erbium,chromium:yttrium-scandium-gallium-garnet laser-powered hydrokinetic system. This device is effective for caries removal and cavity preparation in vitro. Pulpal monitoring of temperature changes during hard tissue cutting by a hydrokinetic system have not been reported. This study compared the effects of hydrokinetic system, dry bur, and wet bur tooth cutting on pulpal temperature. In vivo thermocouple intrapulpal measurements were made on cuspid teeth in anesthetized beagle dogs. In vitro measurements were made on extracted human molar teeth preserved in high-salt solution and later rinsed in phosphate-buffered saline (pH 7.4) to simulate in vivo conditions. The hydrokinetic system was compared with conventional air-turbine-powered bur cutting. The hydrokinetic system cuts and bur preparations were randomly made on the buccal surfaces at the cervical one third of the crown and extended until exposure of the pulp was confirmed clinically. Pulpal temperatures associated with the hydrokinetic system either showed no change or decreased by up to 2 degrees C. Wet bur preparations resulted in a 3 degrees to 4 degrees C rise. With dry bur preparations, a 14 degrees C rise in temperature was recorded. Under the conditions of this study, the erbium,chromium:yttrium-scandium-gallium-garnet laser-powered hydrokinetic system, when used for cavity preparation, had no apparent adverse thermal effect as measured in the pulp space.

Synthesis and characterization of nanocrystalline Nd{sup 3+}-doped gadolinium scandium aluminum garnet powders by a gel-combustion method

DOE Office of Scientific and Technical Information (OSTI.GOV)

Su, Jing, E-mail: zlj007@126.com; Miao, Ju-hong; Xu, Lin-hua

2012-07-15

Graphical abstract: The graph shows the emission spectra (λ{sub ex} = 808 nm) of 1 at.% Nd:GSAG powders sintered at different temperatures for 3 h. Compared with the powder sintered at 900 °C, the PL intensity of the powder sintered at 1000 °C decreased significantly. The changes in the PL intensity should mainly due to the crystallinity and dispersion of the powders. Highlights: ► We synthesized Nd:GSAG nano-powders by gel-combustion method successfully. ► We analyzed the structure and the morphology of the heat-treated products. ► We studied the optical characteristics of Nd:GSAG nano-powders. -- Abstract: Nd{sup 3+}-doped gadolinium scandium aluminummore » garnet (Nd:GSAG) precursor was synthesized by a gel combustion method using metal nitrates and citric acid as raw materials. The structure and morphology of the precursor and the sintered powders were studied by means of X-ray diffraction (XRD), infrared spectroscopy (IR) and transmission electron microscopy (TEM). The results showed that the precursor transformed into pure GSAG polycrystalline phase at about 800 °C, and the powders sintered at 800–1000 °C were well-dispersed with average particle sizes in the range of 30–80 nm. Optical properties of Nd:GSAG nano-powders were characterized by using photoluminescence spectroscopy. The highest photoluminescence intensity was achieved for the powder sintered at 900 °C.« less

Chemical precursors to non-oxide ceramics: Macro to nanoscale materials

NASA Astrophysics Data System (ADS)

Forsthoefel, Kersten M.

Non-oxide ceramics exhibit a number of important properties that make them ideal for technologically important applications (thermal and chemical stability, high strength and hardness, wear-resistance, light weight, and a range of electronic and optical properties). Unfortunately, traditional methodologies to these types of materials are limited to fairly simple shapes and complex processed forms cannot be attained through these methods. The establishment of the polymeric precursor approach has allowed for the generation of advanced materials, such as refractory non-oxide ceramics, with controlled compositions, under moderate conditions, and in processed forms. The goal of the work described in this dissertation was both to develop new processible precursors to technologically important ceramics and to achieve the formation of advanced materials in processed forms. One aspect of this research exploited previously developed preceramic precursors to boron carbide, boron nitride and silicon carbide for the generation of a wide variety of advanced materials: (1) ultra-high temperature ceramic (UHTC) structural materials composed of hafnium boride and related composite materials, (2) the quaternary borocarbide superconductors, and (3) on the nanoscale, non-oxide ceramic nanotubules. The generation of the UHTC and the quaternary borocarbide materials was achieved through a method that employs a processible polymer/metal(s) dispersion followed by subsequent pyrolyses. In the case of the UHTC, hafnium oxide, hafnium, or hafnium boride powders were dispersed in a suitable precursor to afford hafnium borides or related composite materials (HfB2/HfC, HfB2/HfN, HfB2/SiC) in high yields and purities. The quaternary borocarbide superconducting materials were produced from pyrolyses of dispersions containing appropriate stoichiometric amounts of transition metal, lanthanide metal, and the polyhexenyldecaborane polymer. Both chemical vapor deposition (CVD) based routes employing a molecular precursor and porous alumina templating routes paired with solution-based methodologies are shown to generate non-oxide ceramic nanotubules of boron carbide, boron nitride and silicon carbide compositions. In the final phase of this work, a new metal-catalyzed route to poly(1-alkenyl- o-carborane) homopolymers and related copolymers was developed. Both homopolymers of 1-alkenyl-o-carboranes (1-vinyl-, 1-butenyl-, 1-hexenyl-) and copolymers of 1-hexenyl-o-carborane and allyltrimethylsilane or 1-hexenyl-o-carborane and 6-hexenyldecaborane were synthesized via the Cp2ZrMe2/B(C6F5) 3 catalyst system. A copolymer containing 1-hexenyl-o-carborane and the cross-linking agent, 6-hexenyldecaborane, was synthetically designed which exhibits initial cross-linking at ˜250°C and then converts in 75% yields to boron carbide at 1250°C.

Method For Synthesizing Extremely High-Temperature Melting Materials

DOEpatents

Saboungi, Marie-Louise; Glorieux, Benoit

2005-11-22

The invention relates to a method of synthesizing high-temperature melting materials. More specifically the invention relates to a containerless method of synthesizing very high temperature melting materials such as borides, carbides and transition-metal, lanthanide and actinide oxides, using an Aerodynamic Levitator and a laser. The object of the invention is to provide a method for synthesizing extremely high-temperature melting materials that are otherwise difficult to produce, without the use of containers, allowing the manipulation of the phase (amorphous/crystalline/metastable) and permitting changes of the environment such as different gaseous compositions.

Preparation of actinide boride materials via solid-state metathesis reactions and actinide dicarbollide precursors

NASA Astrophysics Data System (ADS)

Lupinetti, Anthony J.; Fife, Julie; Garcia, Eduardo; Abney, Kent D.

2000-07-01

Information gaps exist in the knowledge base needed for choosing among the alternate processes to be used in the safe conversion of fissile materials to optimal forms for safe interim storage, long-term storage, and ultimate disposition. The current baseline storage technology for various wastes uses borosilicate glasses.1 The focus of this paper is the synthesis of actinide-containing ceramic materials at low and moderate temperatures (200 °C-1000 °C) using molecular and polymeric actinide borane and carborane complexes.

Corrosion of Ceramic Materials

NASA Technical Reports Server (NTRS)

Opila, Elizabeth J.; Jacobson, Nathan S.

1999-01-01

Non-oxide ceramics are promising materials for a range of high temperature applications. Selected current and future applications are listed. In all such applications, the ceramics are exposed to high temperature gases. Therefore it is critical to understand the response of these materials to their environment. The variables to be considered here include both the type of ceramic and the environment to which it is exposed. Non-oxide ceramics include borides, nitrides, and carbides. Most high temperature corrosion environments contain oxygen and hence the emphasis of this chapter will be on oxidation processes.

Reactive multilayer synthesis of hard ceramic foils and films

DOEpatents

Makowiecki, Daniel M.; Holt, Joseph B.

1996-01-01

A method for synthesizing hard ceramic materials such as carbides, borides nd aluminides, particularly in the form of coatings provided on another material so as to improve the wear and abrasion performance of machine tools, for example. The method involves the sputter deposition of alternating layers of reactive metals with layers of carbon, boron, or aluminum and the subsequent reaction of the multilayered structure to produce a dense crystalline ceramic. The material can be coated on a substrate or formed as a foil which can be coild as a tape for later use.

High temperature solar energy absorbing surfaces

DOEpatents

Schreyer, J.M.; Schmitt, C.R.; Abbatiello, L.A.

A solar collector having an improved coating is provided. The coating is a plasma-sprayed coating comprising a material having a melting point above 500/sup 0/C at which it is stable and selected from the group of boron carbide, boron nitride, metals and metal oxides, nitrides, carbides, borides, and silicates. The coatings preferably have a porosity of about 15 to 25% and a thickness of less than 200 micrometers. The coatings can be provided by plasma-spraying particles having a mean diameter of about 10 to 200 micrometers.

Fundamental Thermal and Mechanical Properties of Boride Ceramics

DTIC Science & Technology

2014-02-28

Zr ,Y)B2 ( Zr ,Hf)B2 ( Zr ,Ti)B2 ZrB2 El ec tri ca l R es is tiv ity (µ Ω -c m ) Temperature (°C) Figure 17. Electrical resistivity as a function...family as Zr , namely Ti and Hf, had minimal effect on thermal conductivity, while others such as Nb , Ta, and W had an increasing impact based on their...diffusivity (α), heat capacity (Cp) from the NIST-JANAF tables, and bulk density (ρ) using Equation 6. (5) (6) Electrical resistivity

Method for Synthesizing Extremeley High Temperature Melting Materials

DOEpatents

Saboungi, Marie-Louise and Glorieux, Benoit

2005-11-22

The invention relates to a method of synthesizing high-temperature melting materials. More specifically the invention relates to a containerless method of synthesizing very high temperature melting materials such as borides, carbides and transition-metal, lanthanide and actinide oxides, using an Aerodynamic Levitator and a laser. The object of the invention is to provide a method for synthesizing extremely high-temperature melting materials that are otherwise difficult to produce, without the use of containers, allowing the manipulation of the phase (amorphous/crystalline/metastable) and permitting changes of the environment such as different gaseous compositions.

Thermodynamic analysis of chemical compatibility of several reinforcement materials with niobium aluminides

NASA Technical Reports Server (NTRS)

Misra, Ajay K.

1989-01-01

Chemical compatibility of several reinforcement materials with three niobium aluminides, Nb3Al, Nb2Al, and NbAl3, were examined from thermodynamic considerations. The reinforcement materials considered in this study include carbides, borides, nitrides, oxides, silicides, and Engel-Brewer compounds. Thermodynamics of the Nb-Al system were reviewed and activities of Nb and Al were derived at desired calculation temperatures. Criteria for chemical compatibility between the reinforcement material and Nb-Al compounds have been defined and several chemically compatible reinforcement materials have been identified.

Ultra-hard AlMgB14 coatings fabricated by RF magnetron sputtering from a stoichiometric target

NASA Astrophysics Data System (ADS)

Grishin, A. M.; Khartsev, S. I.; Böhlmark, J.; Ahlgren, M.

2015-01-01

For the first time hard aluminum magnesium boride films were fabricated by RF magnetron sputtering from a single stoichiometric ceramic AlMgB14 target. Optimized processing conditions (substrate temperature, target sputtering power and target-to-substrate distance) enable fabrication of stoichiometric in-depth compositionally homogeneous films with the peak values of nanohardness 88 GPa and Young's modulus 517 GPa at the penetration depth of 26 nm and, respectively, 35 and 275 GPa at 200 nm depth in 2 μm thick film.

Foreword

NASA Astrophysics Data System (ADS)

Manghnani, Murli H.

2015-09-01

The 18th International Symposium on Boron, Borides and Related Materials was held in Hawaii Prince Hotel Waikiki, Honolulu, Hawaii, USA on August 31 to September 5, 2014 (ISBB 2014). A booklet of the Program and Abstracts prepared for the Symposium served as an important record of the scientific papers presented as oral paper (68) and as posters (53). The wide range of contributions in various areas of inter-disciplinary research in boron-related materials, and the discussions during the sessions, demonstrated impressive advancements and offer many future opportunities for individual as well as collaborative endeavors globally.

Accumulation of rare earth elements by siderophore-forming Arthrobacter luteolus isolated from rare earth environment of Chavara, India.

PubMed

Emmanuel, E S Challaraj; Ananthi, T; Anandkumar, B; Maruthamuthu, S

2012-03-01

In this study, Arthrobacter luteolus, isolated from rare earth environment of Chavara (Quilon district, Kerala, India), were found to produce catechol-type siderophores. The bacterial strain accumulated rare earth elements such as samarium and scandium. The siderophores may play a role in the accumulation of rare earth elements. Catecholate siderophore and low-molecular-weight organic acids were found to be present in experiments with Arthrobacter luteolus. The influence of siderophore on the accumulation of rare earth elements by bacteria has been extensively discussed.

Very high efficacy electrodeless high intensity discharge lamps

DOEpatents

Johnson, Peter D.

1987-01-01

An electrodeless arc lamp comprises an outer jacket hermetically sealing and thermally protecting an arc tube inside which has an upwardly convex bottom center section. The absence of chemically reactive electrode material makes it possible to use metal halides other than iodides. The tube contains chlorides, bromides or a mixture thereof of scandium and sodium in a nearly equimolar relationship in addition to mercury and an inert gas. Good color balance can be obtained at reduced reservoir temperature and with less power loss. Reduction in wall temperature makes it possible to attain longer lamp life.

Very high efficacy electrodeless high intensity discharge lamps

DOEpatents

Johnson, P.D.

1985-10-03

An electrodeless arc lamp comprises an outer jacket hermetically sealing and thermally protecting an arc tube inside which has an upwardly convex bottom center section. The absence of chemically reactive electrode material makes it possible to use metal halides other than iodides. The tube contains chlorides, bromides or a mixture thereof of scandium and sodium in a nearly equimolar relationship in addition to mercury and an inert gas. Good color balance can be obtained at reduced reservoir temperature and with less power loss. Reduction in wall temperature makes it possible to attain longer lamp life.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Hossain, M. Anwar; Center for Crystal Science and Technology, University of Yamanashi, Miyamae 7-32, Kofu, Yamanashi 400-8511; Tanaka, Isao

We studied thermoelectric properties of YB{sub 41}Si{sub 1.3} single crystals grown by the floating zone method. The composition of the grown crystal was confirmed by electron probe micro-analysis. We have determined the growth direction for the first time for these borosilicides, and discovered relatively large anisotropy in electrical properties. We measured the electrical resistivity and Seebeck coefficient along [510] (the growth direction) and [052] directions and we found that this crystal exhibits strong electrical anisotropy with a maximum of more than 8 times. An interesting layered structural feature is revealed along [510] with dense boron cluster layers and yttrium layers,more » with conductivity enhanced along this direction. We obtained 3.6 times higher power factor along [510] compared to that along [052]. Although the ZT of the present system is low, anisotropy in the thermoelectric properties of a boride was reported for the first time, and can be a clue in developing other boride systems also. - Graphical abstract: The growth direction ([510]) was determined for the first time in YB{sub 41}Si{sub 1.3} single crystals and revealed an interesting layered feature of boron clusters and metal atoms, along which the electrical conductivity and thermoelectric power factor was strongly enhanced. - Highlights: • We have grown YB{sub 41}Si{sub 1.3} single crystals by the floating zone method. • Growth direction of [510] determined for first time in REB{sub 41}Si{sub 1.2}. • Electrical resistivity was strongly anisotropic with possible enhancement along metal layers. • The obtained power factor along [510] is 3.6 times higher than that along [052].« less

Boron oxynitride nanoclusters on tungsten trioxide as a metal-free cocatalyst for photocatalytic oxygen evolution from water splitting

NASA Astrophysics Data System (ADS)

Xie, Ying Peng; Liu, Gang; Lu, Gao Qing (Max); Cheng, Hui-Ming

2012-02-01

Here we show that B2O3-xNx nanoclusters can be formed on the surface of WO3 particles by a combination of thermal oxidation of tungsten boride (WB) in air and the subsequent nitriding process in gaseous ammonia. The resultant nanoclusters are found to play an apparent role in improving the photocatalytic oxygen evolution of WO3 by promoting the surface separation of photoexcited charge-carriers.Here we show that B2O3-xNx nanoclusters can be formed on the surface of WO3 particles by a combination of thermal oxidation of tungsten boride (WB) in air and the subsequent nitriding process in gaseous ammonia. The resultant nanoclusters are found to play an apparent role in improving the photocatalytic oxygen evolution of WO3 by promoting the surface separation of photoexcited charge-carriers. Electronic supplementary information (ESI) available: (1) Experimental section. (2) XRD patterns, FT-IR and Raman spectra of B2O3@WO3 and B2O3-xNx@WO3. (3) Time course of O2 evolution from water splitting using B2O3@WO3 and B2O3-xNx@WO3. (4) XRD pattern and SEM image of pure WO3, UV-visible absorption spectra of pure WO3 and N-WO3. (5) UV-visible absorption spectra of bulk B2O3 and schematic of band edges of WO3, bulk B2O3, and B2O3-xNx nanocluster. See DOI: 10.1039/c2nr11846g

Removal of Dental Implants Using the Erbium,Chromium:Yttrium-Scandium-Gallium-Garnet Laser and the Conventional Trephine Bur: An in Vitro Comparative Study.

PubMed

Hajji, Mohammad; Franzen, Rene; Grümer, Stefan; Modabber, Ali; Nasher, Riman; Prescher, Andreas; Gutknecht, Norbert

2016-02-01

The purpose of this study was to compare the conventional trephine bur and the Erbium,chromium: yttrium-scandium-gallium-garnet (Er,Cr:YSGG) laser in removing implants in terms of the volume of removed bone, duration of the procedure, and morphological changes on the bone surface. Three human mandibles were utilized, and four implants were inserted in each mandible using a drilling handpiece and burs. The implants were divided into two groups (n = 6) in which two implants from each mandible were removed using a trephine bur running at 1200 rounds per minute (rpm) with water irrigation. The remaining implants (n = 6) were removed with Er,Cr:YSGG laser (power 6 W, frequency 20 Hz, pulse duration 50 μs, water 60, air 30). The volume of bone loss was calculated by filling the holes with mercury and measuring its volume. The preparation time was measured with a digital stopwatch and the postoperative bone surfaces were examined under a scanning electron microscope (SEM). The laser group exhibited a smaller amount of bone loss than the trephine bur group, whereas the latter required a shorter time of preparation. SEM revealed empty trabecular spaces with no signs of carbonization and well-defined edges in the laser group, whereas the trephine group displayed a surface covered with a smear layer and microcracks. The Er,Cr:YSGG laser provides superior results over the trephine bur in terms of bone preservation, thermal damage, and cutting efficiency.

Comparative evaluation of surface topography of tooth prepared using erbium, chromium: Yttrium, scandium, gallium, garnet laser and bur and its clinical implications.

PubMed

Verma, Mahesh; Kumari, Pooja; Gupta, Rekha; Gill, Shubhra; Gupta, Ankur

2015-01-01

Erbium, chromium: Yttrium, scandium, gallium, garnet (Er, Cr: YSGG) laser has been successfully used in the ablation of dental hard and soft tissues. It has been reported that this system is also useful for preparing tooth surfaces and etching, but no consensus exist in the literature regarding the advantage of lasers over conventional tooth preparation technique. Labial surfaces of 25 extracted human maxillary central incisors were divided into two halves. Right half was prepared with diamond bur and left half with Er, Cr; YSGG laser and a reduction of 0.3-0.5 mm was carried out. Topography of prepared surfaces of five teeth were examined under scanning electron microscope (SEM). The remaining samples were divided into 4 groups of 10 specimens each based on the surface treatment received: One group was acid etched and other was nonetched. Composite resin cylinders were bonded on prepared surfaces and shear bond strength was assessed using a universal testing machine. The SEM observation revealed that the laser prepared surfaces were clean, highly irregular and devoid of a smear layer. Bur prepared surfaces were relatively smooth but covered with smear layer. Highest bond strength was shown by laser prepared acid etched group, followed by bur prepared the acid etched group. The bur prepared nonacid etched group showed least bond strength. Er, Cr: YSGG laser can be used for preparing tooth and bond strength value achieved by laser preparation alone without surface treatment procedure lies in the range of clinical acceptability.

Use of the erbium, chromium:yttrium-scandium-gallium-garnet laser on human enamel tissues. Influence of the air-water spray on the laser-tissue interaction: scanning electron microscope evaluations.

PubMed

Olivi, Giovanni; Angiero, Francesca; Benedicenti, Stefano; Iaria, Giuseppe; Signore, Antonio; Kaitsas, Vassilios

2010-11-01

The study investigated the influence of varying amounts of air/water spray and the energy used by an erbium, chromium:yttrium-scandium-gallium-garnet (Er,Cr:YSGG) 2,780 nm laser when treating dental tissues. The morphological effects produced by the laser interaction on healthy human enamel were evaluated by scanning electron microscopy (SEM). The vestibular and lingual surfaces of ten molars were treated with laser at different power settings; each surface was subdivided into cervical, median, and occlusal parts and treated with different proportions of water spray; the series contained 60 tooth portions. Treatment differed in terms of power setting and air/water percentage. All specimens were then subjected to dehydration and metallisation. At SEM evaluation, the classic aspect of laser-treated enamel was visible: grooves, flakes, shelves and sharp edges, indicative of micro-explosion rather than melting. Vaporisation of the tissue created a clear delimitation from surrounding healthy tissue, with partial respect to the prismatic structure of the treated enamel. The aspect of the enamel was rarely type 1 Silverstone but more frequently type 2 or 3, with prismatic structure not respected and/or completely disordered. These morphological differences appeared to be correlated with the inclination of the laser beam aimed at the enamel prisms and with the percentage of air/water used. The laser system analysed showed itself to be effective at removing human dental enamel. The results appeared to be closely correlated with the variation of the percentage of the laser's water-air spray.

Thermal effects from modified endodontic laser tips used in the apical third of root canals with erbium-doped yttrium aluminium garnet and erbium, chromium-doped yttrium scandium gallium garnet lasers.

PubMed

George, Roy; Walsh, Laurence J

2010-04-01

To evaluate the temperature changes occurring on the apical third of root surfaces when erbium-doped yttrium aluminium garnet (Er:YAG) and erbium, chromium-doped yttrium scandium gallium garnet (Er,Cr:YSGG) laser energy was delivered with a tube etched, laterally emitting conical tip and a conventional bare design optical fiber tip. Thermal effects of root canal laser treatments on periodontal ligament cells and alveolar bone are of concern in terms of safety. A total of 64 single-rooted extracted teeth were prepared 1 mm short of the working length using rotary nickel-titanium Pro-Taper files to an apical size corresponding to a F5 Pro-Taper instrument. A thermocouple located 2 mm from the apex was used to record temperature changes arising from delivery of laser energy through laterally emitting conical tips or plain tips, using an Er:YAG or Er,Cr:YSGG laser. For the Er:YAG and Er,Cr:YSGG systems, conical fibers showed greater lateral emissions (452 + 69% and 443 + 64%) and corresponding lower forward emissions (48 + 5% and 49 + 5%) than conventional plain-fiber tips. All four combinations of laser system and fiber design elicited temperature increases less than 2.5 degrees C during lasing. The use of water irrigation attenuated completely the thermal effects of individual lasing cycles. Laterally emitting conical fiber tips can be used safely under defined conditions for intracanal irradiation without harmful thermal effects on the periodontal apparatus.

Investigation and modeling of Al3(Sc, Zr) precipitation strengthening in the presence of enhanced supersaturation and within Al-Cu binary alloys

NASA Astrophysics Data System (ADS)

Deane, Kyle

Diffuse Al-Sc and Al-Zr alloys have been demonstrated in literature to be relatively coarsening resistant at higher temperatures when compared with commonly used precipitation strengthening alloys (e.g. 2000 series, 6000 series). However, because of a limited strengthening due to the low solubility of scandium and zirconium in aluminum, and owing to the scarcity and therefore sizeable price tag attached to scandium, little research has been done in the way of optimizing these alloys for commercial applications. With this in mind, this dissertation describes research which aims to tackle several important areas of Al-Sc-Zr research that have been yet unresolved. In Chapter 4, rapid solidification was utilized to enhance the achievable supersaturation of the alloy in an effort to increase the achievable precipitate strengthening. In Chapter 5, Additive Friction Stir processing (AFS), a novel method of mechanically combining materials without melting, was employed in an attempt to pass the benefits of supersaturation from melt spun ribbon into a more structurally useful bulk material. In Chapter 6, a Matlab program written to predict precipitate nucleation, growth, and coarsening with a modified Kampmann and Wagner Numerical (KWN) model, was used to predict heat treatment regimens for more efficient strengthening. Those predictions were then tested experimentally to test the validity of the results. And lastly, in Chapter 7, the effect of zirconium on Al-Cu secondary precipitates was studied in an attempt to increase their thermal stability, as much higher phase fractions of Al-Cu precipitates are achievable than Al-Zr precipitates.

Processing development of 4 tantalum carbide-hafnium carbide and related carbides and borides for extreme environments

NASA Astrophysics Data System (ADS)

Gaballa, Osama Gaballa Bahig

Carbides, nitrides, and borides ceramics are of interest for many applications because of their high melting temperatures and good mechanical properties. Wear-resistant coatings are among the most important applications for these materials. Materials with high wear resistance and high melting temperatures have the potential to produce coatings that resist degradation when subjected to high temperatures and high contact stresses. Among the carbides, Al4SiC4 is a low density (3.03 g/cm3), high melting temperature (>2000°C) compound, characterized by superior oxidation resistance, and high compressive strength. These desirable properties motivated this investigation to (1) obtain high-density Al4SiC4 at lower sintering temperatures by hot pressing, and (2) to enhance its mechanical properties by adding WC and TiC to the Al4SiC4. Also among the carbides, tantalum carbide and hafnium carbide have outstanding hardness; high melting points (3880°C and 3890°C respectively); good resistance to chemical attack, thermal shock, and oxidation; and excellent electronic conductivity. Tantalum hafnium carbide (Ta4HfC 5) is a 4-to-1 ratio of TaC to HfC with an extremely high melting point of 4215 K (3942°C), which is the highest melting point of all currently known compounds. Due to the properties of these carbides, they are considered candidates for extremely high-temperature applications such as rocket nozzles and scramjet components, where the operating temperatures can exceed 3000°C. Sintering bulk components comprised of these carbides is difficult, since sintering typically occurs above 50% of the melting point. Thus, Ta4 HfC5 is difficult to sinter in conventional furnaces or hot presses; furnaces designed for very high temperatures are expensive to purchase and operate. Our research attempted to sinter Ta4HfC5 in a hot press at relatively low temperature by reducing powder particle size and optimizing the powder-handling atmosphere, milling conditions, sintering temperature, and hot-pressing pressure. Also, WC additions to Ta4HfC5 were found to improve densification and increase microhardness. The ability to process these materials at relatively low temperature would save energy and reduce cost. Boron-based hard materials are used in numerous applications such as industrial machining, armor plating, and wear-resistant coatings. It was often thought that in addition to strong bonding, super-hard materials must also possess simple crystallographic unit cells with high symmetry and a minimum number of crystal defects (e.g., diamond and cubic boron nitride (cBN)). However, one ternary boride, AlMgB14, deviates from this paradigm; AlMgB 14 has a large, orthorhombic unit cell (oI64) with multiple icosahedral boron units. TiB2 has been shown to be an effective reinforcing phase in AlMgB 14, raising hardness, wear resistance, and corrosion resistance. Thus, it was thought that adding other, similar phases (i.e., ZrB2 and HfB2) to AlMgB14 could lead to useful improvements in properties vis-à-vis pure AlMgB14. Group IV metal diborides (XB2, where X = Ti, Zr, or Hf) are hard, ultra-high temperature ceramics. These compounds have a primitive hexagonal crystal structure (hP3) with planes of graphite-like boride rings above and below planes of metal atoms. Unlike graphite, there is strong bonding between the planes, resulting in high hardness. For this study two-phase composites of 60 vol. % metal diborides with 40 vol. % AlMgB14 were produced and characterized.

How to estimate hardness of crystals on a pocket calculator

NASA Astrophysics Data System (ADS)

Šimůnek, Antonín

2007-05-01

A generalization of the semiempirical microscopic model of hardness is presented and applied to currently studied borides, carbides, and nitrides of heavy transition metals. The hardness of OsB, OsC, OsN, PtN, RuC, RuB2 , ReB2 , OsB2 , IrN2 , PtN2 , and OsN2 crystals in various structural phases is predicted. It is found that none of the transition metal crystals is superhard, i.e., with hardness greater than 40GPa . The presented method provides materials researchers with a practical tool in the search for new hard materials.

First-principles modeling of hardness in transition-metal diborides

NASA Astrophysics Data System (ADS)

Lazar, Petr; Chen, Xing-Qiu; Podloucky, Raimund

2009-07-01

Based on recent experiments, the diborides OsB2 and ReB2 were proposed to be ultraincompressible and superhard materials. By application of an ab initio density-functional theory approach we investigate the elastic and cleavage fracture properties of the borides MB2 ( M=Hf , Ta, W, Re, Os, and Ir). We derive a direct correlation between the lowest calculated critical cleavage stress and the experimental (micro)hardness. By calculating the critical shear stress and estimating the possibility of dislocation emission we can justify the prediction that ReB2 is indeed a superhard material.

Reactive multilayer synthesis of hard ceramic foils and films

DOEpatents

Makowiecki, D.M.; Holt, J.B.

1996-02-13

A method is disclosed for synthesizing hard ceramic materials such as carbides, borides and aluminides, particularly in the form of coatings provided on another material so as to improve the wear and abrasion performance of machine tools, for example. The method involves the sputter deposition of alternating layers of reactive metals with layers of carbon, boron, or aluminum and the subsequent reaction of the multilayered structure to produce a dense crystalline ceramic. The material can be coated on a substrate or formed as a foil which can be coiled as a tape for later use.

Thermodynamic analysis of chemical compatibility of several compounds with Fe-Cr-Al alloys

NASA Technical Reports Server (NTRS)

Misra, Ajay K.

1993-01-01

Chemical compatibility between Fe-19.8Cr-4.8Al (weight percent), which is the base composition for the commercial superalloy MA956, and several carbides, borides, nitrides, oxides, and silicides was analyzed from thermodynamic considerations. The effect of addition of minor alloying elements, such as Ti, Y, and Y2O3, to the Fe-Cr-Al alloy on chemical compatibility between the alloy and various compounds was also analyzed. Several chemically compatible compounds that can be potential reinforcement materials and/or interface coating materials for Fe-Cr-Al based composites were identified.

Lightweight porous plastic plaque. [nickel cadmium batteries

NASA Technical Reports Server (NTRS)

Reid, M.

1978-01-01

The porosity and platability of various materials were investigated to determine a suitable substrate for nickel-plated electrodes. Immersion, ultrasonics, and flow-through plating techniques were tried using nonproprietary formulations, and proprietary phosphide and boride baths. Modifications to the selected material include variations in formulation and treatment, carbon loading to increase conductivity, and the incorporation of a grid. Problems to be solved relate to determining conductivities and porosities as a function of amount of nickel plated on the plastics; loading; charge and discharge curves of electrodes at different current densities; cell performance; and long-term degradation of electrodes.

In-situ Formation of Reinforcement Phases in Ultra High Temperature Ceramic Composites

NASA Technical Reports Server (NTRS)

Stackpoole, Margaret M (Inventor); Gasch, Matthew J (Inventor); Olson, Michael W (Inventor); Hamby, Ian W. (Inventor); Johnson, Sylvia M (Inventor)

2013-01-01

A tough ultra-high temperature ceramic (UHTC) composite comprises grains of UHTC matrix material, such as HfB.sub.2, ZrB.sub.2 or other metal boride, carbide, nitride, etc., surrounded by a uniform distribution of acicular high aspect ratio reinforcement ceramic rods or whiskers, such as of SiC, is formed from uniformly mixing a powder of the UHTC material and a pre-ceramic polymer selected to form the desired reinforcement species, then thermally consolidating the mixture by hot pressing. The acicular reinforcement rods may make up from 5 to 30 vol % of the resulting microstructure.

Photoelectrochemical cells including chalcogenophosphate photoelectrodes

NASA Technical Reports Server (NTRS)

Reichman, B.; Byvik, C. E. (Inventor)

1984-01-01

Photoelectrochemical cells employing chalcogenophosphate (MPX3) photoelectrodes are described where M is selected from the group of transition metal series of elements beginning with scandium (atomic number 21) through germanium (atomic number 32) yttrium (atomic number 39) through antimony (atomic number 51) and lanthanum (atomic number 57) through polonium (atomic number 84); P is phosphorus; and X is selected from the chalogenide series consisting of sulfur, selenium, and tellurium. These compounds have bandgaps in the desirable range from 2.0 eV to 2.2 eV for the photoelectrolysis of water and are stable when used as photoelectrodes for the same.

Semimicrodetermination of tantalum with selenous acid

USGS Publications Warehouse

Grimaldi, F.S.; Schnepfe, M.M.

1958-01-01

Tantalum is separated and determined gravimetrically by precipitation with selenous acid from a highly acidic solution containing oxalic and tartaric acids. The method is selective for the determination of up to 30 mg. of tantalum pentoxide, and tolerates relatively large amounts of scandium, yttrium, cerium, titanium, zirconium, thorium, vanadium, niobium, molybdenum, tungsten, uranium, iron, aluminum, gallium, tin, lead, antimony, and bismuth. The separation of tantalum from niobium and titanium is not strictly quantitative, and correction is made colorimetrically for the small amounts of niobium and titanium co-precipitating with the tantalum. The method was applied to the determination of tantalum in tantaloniobate ores.

Production Potential of 47Sc Using Spallation Neutron Flux at the Los Alamos Isotope Production Facility

DTIC Science & Technology

2014-03-27

Kowash, PhD (Chairman) Date //signed// 14 March 2014 LTC Stephen McHale, PhD (Member) Date //signed// 10 March 2014 Dr. Jonathan Engle, PhD (Member) Date ...signed// 14 March 2014 Dr. Justin Clinton, PhD (Member) Date AFIT-ENP-14-M-02 Abstract Scandium-47 (T1/2 = 3.41d) forms stable complexes with...0.2 µCi g−1 µAh−1 in the 47Ti and 50Ti-oxide samples, respectively. Radioisotopic purities of 47Sc in excess of 90% are achieved by activation of 47Ti

Handbook of Isotopes in the Cosmos

NASA Astrophysics Data System (ADS)

Clayton, Donald

2007-08-01

List of illustrations; Preface; Introduction; 1. Hydrogen (H); 2. Helium (He); 3. Lithium (Li); 4. Beryllium (Be); 5. Boron (B); 6. Carbon (C); 7. Nitrogen (N); 8. Oxygen (O); 9. Fluorine (F); 10. Neon (Ne); 11. Sodium (Na); 12. Magnesium (Mg); 13. Aluminium (Al); 14. Silicon (Si); 15. Phosphorous (P); 16. Sulphur (S); 17. Chlorine (Cl); 18. Argon (Ar); 19. Potassium (K); 20. Calcium (Ca); 21. Scandium (Sc); 22. Titanium (Ti); 23. Vanadium (V); 24. Chromium (Cr); 25. Manganese (Mn); 26. Iron (Fe); 27. Cobalt (Co); 28. Nickel (Ni); 29. Copper (Cu); 30. Zinc (Zn); 31. Gallium (Ga); Glossary.

Handbook of Isotopes in the Cosmos

NASA Astrophysics Data System (ADS)

Clayton, Donald

2003-09-01

List of illustrations; Preface; Introduction; 1. Hydrogen (H); 2. Helium (He); 3. Lithium (Li); 4. Beryllium (Be); 5. Boron (B); 6. Carbon (C); 7. Nitrogen (N); 8. Oxygen (O); 9. Fluorine (F); 10. Neon (Ne); 11. Sodium (Na); 12. Magnesium (Mg); 13. Aluminium (Al); 14. Silicon (Si); 15. Phosphorous (P); 16. Sulphur (S); 17. Chlorine (Cl); 18. Argon (Ar); 19. Potassium (K); 20. Calcium (Ca); 21. Scandium (Sc); 22. Titanium (Ti); 23. Vanadium (V); 24. Chromium (Cr); 25. Manganese (Mn); 26. Iron (Fe); 27. Cobalt (Co); 28. Nickel (Ni); 29. Copper (Cu); 30. Zinc (Zn); 31. Gallium (Ga); Glossary.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Mbarki, Mohammed; Touzani, Rachid St.; Rehorn, Christian W.G.

The new ternary transition metal-rich borides Ta{sub 2}OsB{sub 2} and TaRuB have been successfully synthesized by arc-melting the elements in a water-cooled crucible under an argon atmosphere. The crystal structures of both compounds were solved by single-crystal X-ray diffraction and their metal compositions were confirmed by EDX analysis. It was found that Ta{sub 2}OsB{sub 2} and TaRuB crystallize in the tetragonal Nb{sub 2}OsB{sub 2} (space group P4/mnc, no. 128) and the orthorhombic NbRuB (space group Pmma, no. 51) structure types with lattice parameters a=5.878(2) Å, c=6.857(2) Å and a=10.806(2) Å, b=3.196(1) Å, c=6.312(2) Å, respectively. Furthermore, crystallographic, electronic and bondingmore » characteristics have been studied by density functional theory (DFT). Electronic structure relaxation has confirmed the crystallographic parameters while COHP bonding analysis indicates that B{sub 2}-dummbells are the strongest bonds in both compounds. Moreover, the formation of osmium dumbbells in Ta{sub 2}OsB{sub 2} through a Peierls distortion along the c-axis, is found to be the origin of superstructure formation. Magnetic susceptibility measurements reveal that the two phases are Pauli paramagnets, thus confirming the theoretical DOS prediction of metallic character. Also hints of superconductivity are found in the two phases, however lack of single phase samples has prevented confirmation. Furthermore, the thermodynamic stability of the two modifications of AMB (A=Nb, Ta; M =Ru, Os) are studied using DFT, as new possible phases containing either B{sub 4}- or B{sub 2}-units are predicted, the former being the most thermodynamically stable modification. - Graphical abstract: The two new ternary tantalum borides, Ta{sub 2}OsB{sub 2} and TaRuB, have been discovered. Their crystal structures contain boron dumbbells, which are the strongest bonds. Peirls distortion is found responsible for Os{sub 2}-dumbbells formation in Ta{sub 2}OsB{sub 2}. Ta{sub 2}OsB{sub 2} and TaRuB are Pauli paramagnet and potential superconductors. - Highlights: • Two new ternary tantalum borides, Ta{sub 2}OsB{sub 2} and TaRuB, discovered. • Boron dumbbells are the strongest bonds in Ta{sub 2}OsB{sub 2} and TaRuB. • Peierls distortion responsible for Os{sub 2}-dumbbells formation in Ta{sub 2}OsB{sub 2.} • Ta{sub 2}OsB{sub 2} and TaRuB are Pauli paramagnet. • Ta{sub 2}OsB{sub 2} and TaRuB contain pseudogaps and are potential superconductors.« less

New ternary tantalum borides containing boron dumbbells: Experimental and theoretical studies of Ta2OsB2 and TaRuB

NASA Astrophysics Data System (ADS)

Mbarki, Mohammed; Touzani, Rachid St.; Rehorn, Christian W. G.; Gladisch, Fabian C.; Fokwa, Boniface P. T.

2016-10-01

The new ternary transition metal-rich borides Ta2OsB2 and TaRuB have been successfully synthesized by arc-melting the elements in a water-cooled crucible under an argon atmosphere. The crystal structures of both compounds were solved by single-crystal X-ray diffraction and their metal compositions were confirmed by EDX analysis. It was found that Ta2OsB2 and TaRuB crystallize in the tetragonal Nb2OsB2 (space group P4/mnc, no. 128) and the orthorhombic NbRuB (space group Pmma, no. 51) structure types with lattice parameters a=5.878(2) Å, c=6.857(2) Å and a=10.806(2) Å, b=3.196(1) Å, c=6.312(2) Å, respectively. Furthermore, crystallographic, electronic and bonding characteristics have been studied by density functional theory (DFT). Electronic structure relaxation has confirmed the crystallographic parameters while COHP bonding analysis indicates that B2-dummbells are the strongest bonds in both compounds. Moreover, the formation of osmium dumbbells in Ta2OsB2 through a Peierls distortion along the c-axis, is found to be the origin of superstructure formation. Magnetic susceptibility measurements reveal that the two phases are Pauli paramagnets, thus confirming the theoretical DOS prediction of metallic character. Also hints of superconductivity are found in the two phases, however lack of single phase samples has prevented confirmation. Furthermore, the thermodynamic stability of the two modifications of AMB (A=Nb, Ta; M =Ru, Os) are studied using DFT, as new possible phases containing either B4- or B2-units are predicted, the former being the most thermodynamically stable modification.

Design for low-cost gas metal arc weld-based aluminum 3-D printing

NASA Astrophysics Data System (ADS)

Haselhuhn, Amberlee S.

Additive manufacturing, commonly known as 3-D printing, has the potential to change the state of manufacturing across the globe. Parts are made, or printed, layer by layer using only the materials required to form the part, resulting in much less waste than traditional manufacturing methods. Additive manufacturing has been implemented in a wide variety of industries including aerospace, medical, consumer products, and fashion, using metals, ceramics, polymers, composites, and even organic tissues. However, traditional 3-D printing technologies, particularly those used to print metals, can be prohibitively expensive for small enterprises and the average consumer. A low-cost open-source metal 3-D printer has been developed based upon gas metal arc weld (GMAW) technology. Using this technology, substrate release mechanisms have been developed, allowing the user to remove a printed metal part from a metal substrate by hand. The mechanical and microstructural properties of commercially available weld alloys were characterized and used to guide alloy development in 4000 series aluminum-silicon alloys. Wedge casting experiments were performed to screen magnesium, strontium, and titanium boride alloying additions in hypoeutectic aluminum-silicon alloys for their properties and the ease with which they could be printed. Finally, the top performing alloys, which were approximately 11.6% Si modified with strontium and titanium boride were cast, extruded, and drawn into wire. These wires were printed and the mechanical and microstructural properties were compared with those of commercially available alloys. This work resulted in an easier-to-print aluminum-silicon-strontium alloy that exhibited lower porosity, equivalent yield and tensile strengths, yet nearly twice the ductility compared to commercial alloys.

The complex metal-rich boride Ti1+xRh2-x+yIr3-yB3 (x=0.68, y=1.06) with a new structure type containing B4 zigzag fragments: Synthesis, crystal chemistry and theoretical calculations

NASA Astrophysics Data System (ADS)

Goerens, Christian; Fokwa, Boniface P. T.

2012-08-01

Polycrystalline samples and single crystals of the new complex boride Ti1+xRh2-x+yIr3-yB3 (x=0.68; y=1.06) were synthesized by arc-melting the elements in a water-cooled copper crucible under an argon atmosphere and characterized by X-Ray diffraction as well as EDX measurements. The crystal structure was refined on the basis of single crystal data. The new phase, which represents a new structure type containing trans zigzag B4 fragments as well as isolated boron atoms crystallizes in the orthorhombic space group Pbam (Nr. 55) with the lattice parameters a=8.620(1) Å, b=14.995(2) Å and c=3.234(1) Å. First-principles density functional theory calculations using the Vienna ab-initio simulation package (VASP) were performed on an appropriate structural model (using a supercell approach) and the experimental crystallographic data could be reproduced accurately. Based on this model, the density of states and crystal orbital Hamilton population (for bonding analysis) were calculated, using the linear muffin-tin orbital atomic sphere approximation (LMTO-ASA) method. According to these calculations, this metal-rich compound should be metallic, as expected. Furthermore, very strong boron-boron interactions are observed in the trans zigzag B4 fragment, which induce a clear differentiation of two types of metal-boron contacts with different strength. The observed three-dimensional metal-metal interaction is in good agreement with the predicted metallic behavior.

Three-dimensional nanometer scale analyses of precipitate structures and local compositions in titanium aluminide engineering alloys

NASA Astrophysics Data System (ADS)

Gerstl, Stephan S. A.

Titanium aluminide (TiAl) alloys are among the fastest developing class of materials for use in high temperature structural applications. Their low density and high strength make them excellent candidates for both engine and airframe applications. Creep properties of TiAl alloys, however, have been a limiting factor in applying the material to a larger commercial market. In this research, nanometer scale compositional and structural analyses of several TiAl alloys, ranging from model Ti-Al-C ternary alloys to putative commercial alloys with 10 components are investigated utilizing three dimensional atom probe (3DAP) and transmission electron microscopies. Nanometer sized borides, silicides, and carbide precipitates are involved in strengthening TiAl alloys, however, chemical partitioning measurements reveal oxygen concentrations up to 14 at. % within the precipitate phases, resulting in the realization of oxycarbide formation contributing to the precipitation strengthening of TiAl alloys. The local compositions of lamellar microstructures and a variety of precipitates in the TiAl system, including boride, silicide, binary carbides, and intermetallic carbides are investigated. Chemical partitioning of the microalloying elements between the alpha2/gamma lamellar phases, and the precipitate/gamma-matrix phases are determined. Both W and Hf have been shown to exhibit a near interfacial excess of 0.26 and 0.35 atoms nm-2 respectively within ca. 7 nm of lamellar interfaces in a complex TiAl alloy. In the case of needle-shaped perovskite Ti3AlC carbide precipitates, periodic domain boundaries are observed 5.3+/-0.8 nm apart along their growth axis parallel to the TiAl[001] crystallographic direction with concomitant composition variations after 24 hrs. at 800°C.

Stabilization of scandium terephthalate MOFs against reversible amorphization and structural phase transition by guest uptake at extreme pressure.

PubMed

Graham, Alexander J; Banu, Ana-Maria; Düren, Tina; Greenaway, Alex; McKellar, Scott C; Mowat, John P S; Ward, Kenneth; Wright, Paul A; Moggach, Stephen A

2014-06-18

Previous high-pressure experiments have shown that pressure-transmitting fluids composed of small molecules can be forced inside the pores of metal organic framework materials, where they can cause phase transitions and amorphization and can even induce porosity in conventionally nonporous materials. Here we report a combined high-pressure diffraction and computational study of the structural response to methanol uptake at high pressure on a scandium terephthalate MOF (Sc2BDC3, BDC = 1,4-benzenedicarboxylate) and its nitro-functionalized derivative (Sc2(NO2-BDC)3) and compare it to direct compression behavior in a nonpenetrative hydrostatic fluid, Fluorinert-77. In Fluorinert-77, Sc2BDC3 displays amorphization above 0.1 GPa, reversible upon pressure release, whereas Sc2(NO2-BDC)3 undergoes a phase transition (C2/c to Fdd2) to a denser but topologically identical polymorph. In the presence of methanol, the reversible amorphization of Sc2BDC3 and the displacive phase transition of the nitro-form are completely inhibited (at least up to 3 GPa). Upon uptake of methanol on Sc2BDC3, the methanol molecules are found by diffraction to occupy two sites, with preferential relative filling of one site compared to the other: grand canonical Monte Carlo simulations support these experimental observations, and molecular dynamics simulations reveal the likely orientations of the methanol molecules, which are controlled at least in part by H-bonding interactions between guests. As well as revealing the atomistic origin of the stabilization of these MOFs against nonpenetrative hydrostatic fluids at high pressure, this study demonstrates a novel high-pressure approach to study adsorption within a porous framework as a function of increasing guest content, and so to determine the most energetically favorable adsorption sites.

Structure and temperature effects on Nd3+ spectra in polycrystalline mixed scandium aluminum garnets Y3ScxAl5-xO12

NASA Astrophysics Data System (ADS)

Lupei, A.; Lupei, V.; Hau, S.; Gheorghe, C.; Voicu, F.

2015-09-01

New spectroscopic data obtained from high resolution low temperature absorption and emission spectra of Nd3+ in mixed scandium aluminum garnets Y3ScxAl5-xO12 - (x = 0-2) translucent ceramics revealed transition dependent composition effects: modification of the shapes (Lorentz at x = 0 and 2, quasi-Gauss at x = 1, x-dependent asymmetric for other x values, with obvious multicenter structure for low x), widths and shifts of the lines. Nd3+ electronic structure dependence on structural changes with composition is analyzed in terms of nephelauxetic effect and maximum splitting of manifolds: Sc3+ co-doping reduces the nephelauxetic effect, and the increase of 4F3/2 splitting from 85 cm-1 (x = 0) to 98 cm-1 (x = 2) denotes the lowering of local symmetry. The multicenter structure and inhomogeneous broadening of Nd3+ lines is attributed to crystal field distributions determined by the random occupancy of the octahedral sites by Sc3+ and Al3+. For low x (0.2) the resolved two satellites S1, S2 that accompany Nd:YAG lines are correlated to anisotropic crystal field perturbations produced by the n.n. Sc3+ by analogy to those determined by Y3+-antisites (excess of Y3+ ions that enter in octahedral sites of the melt-grown YAG crystals). The temperature evolution of the Nd3+ spectral characteristics (line intensity, shift, broadening) in the 10-300 K range is analyzed in terms of thermal population of the Stark levels, of the effect on electron-phonon interaction and on lattice expansion. The relevance of the spectroscopic properties on the laser emission characteristics in these systems is discussed.

China's rare-earth industry

USGS Publications Warehouse

Tse, Pui-Kwan

2011-01-01

Introduction China's dominant position as the producer of over 95 percent of the world output of rare-earth minerals and rapid increases in the consumption of rare earths owing to the emergence of new clean-energy and defense-related technologies, combined with China's decisions to restrict exports of rare earths, have resulted in heightened concerns about the future availability of rare earths. As a result, industrial countries such as Japan, the United States, and countries of the European Union face tighter supplies and higher prices for rare earths. This paper briefly reviews China's rare-earth production, consumption, and reserves and the important policies and regulations regarding the production and trade of rare earths, including recently announced export quotas. The 15 lanthanide elements-lanthanum, cerium, praseodymium, neodymium, promethium, samarium, europium, gadolinium, terbium, dysprosium, holmium, erbium, thulium, ytterbium, and lutetium (atomic numbers 57-71)-were originally known as the rare earths from their occurrence in oxides mixtures. Recently, some researchers have included two other elements-scandium and yttrium-in their discussion of rare earths. Yttrium (atomic number 39), which lies above lanthanum in transition group III of the periodic table and has a similar 3+ ion with a noble gas core, has both atomic and ionic radii similar in size to those of terbium and dysprosium and is generally found in nature with lanthanides. Scandium (atomic number 21) has a smaller ionic radius than yttrium and the lanthanides, and its chemical behavior is intermediate between that of aluminum and the lanthanides. It is found in nature with the lanthanides and yttrium. Rare earths are used widely in high-technology and clean-energy products because they impart special properties of magnetism, luminescence, and strength. Rare earths are also used in weapon systems to obtain the same properties.

Thermodynamic Analysis of Compatibility of Several Reinforcement Materials with Beta Phase NiAl Alloys

NASA Technical Reports Server (NTRS)

Misra, Ajay K.

1988-01-01

Chemical compatibility of several reinforcement materials with beta phase NiAl alloys within the concentration range 40 to 50 at. percent Al have been analyzed from thermodynamic considerations at 1373 and 1573 K. The reinforcement materials considered in this study include carbides, borides, oxides, nitrides, beryllides, and silicides. Thermodynamic data for NiAl alloys have been reviewed and activity of Ni and Al in the beta phase have been derived at 1373 and 1573 K. Criteria for chemical compatibility between the reinforcement material and the matrix have been defined and several chemically compatible reinforcement materials have been defined.

Material comprising two different non-metallic parrticles having different particle sizes for use in solar reactor

DOE Office of Scientific and Technical Information (OSTI.GOV)

Klausner, James F.; Momen, Ayyoub Mehdizadeh; Al-Raqom, Fotouh A.

Disclosed herein is a composite particle comprising a first non-metallic particle in which is dispersed a second non-metallic particle, where the first non-metallic particle and the second non-metallic particle are inorganic; and where a chemical composition of the first non-metallic particle is different from a chemical composition of the second non-metallic particle; and where the first non-metallic particle and the second non-metallic particle are metal oxides, metal carbides, metal nitrides, metal borides, metal silicides, metal oxycarbides, metal oxynitrides, metal boronitrides, metal carbonitrides, metal borocarbides, or a combination thereof.

Plasma-induced damage of tungsten coatings on graphite limiters

NASA Astrophysics Data System (ADS)

Fortuna, E.; Rubel, M. J.; Psoda, M.; Andrzejczuk, M.; Kurzydowski, K. J.; Miskiewicz, M.; Philipps, V.; Pospieszczyk, A.; Sergienko, G.; Spychalski, M.; Zielinski, W.

2007-03-01

Vaccum plasma sprayed tungsten coatings with an evaporated sandwich Re-W interlayer on graphite limiter blocks were studied after the experimental campaign in the TEXTOR tokamak. The coating morphology was modified by high-heat loads and co-deposition of species from the plasma. Co-deposits contained fuel species, carbon, boron and silicon. X-ray diffractometer phase analysis indicated the coexistence of metallic tungsten and its carbides (WC and W2C) and boride (W2B). In the Re-W layer the presence of carbon was detected in a several micrometres thick zone. In the overheated part of the limiter, the Re-W layer was transformed into a sigma phase.

First principle study of UHTC ternary diboride, Cr2AlB2

NASA Astrophysics Data System (ADS)

Rastogi, Anugya; Rajpoot, Priyanka; Verma, U. P.

2018-04-01

In this paper ab-initio study of the structural, electronic and optical properties of ternary metal boride Cr2AlB2 using full potential linear augmented plane wave (FP-LAPW) method based on the density functional theory (DFT). The study of structural properties shows that Cr2AlB2 is metallic in nature and have orthorhombic crystal structure. The optical properties show that it possess anisotropic behavior, which have wide applications in electricity production through concentration of solar power (CSP) technology. To the best of our knowledge, theoretical study of the optical properties of Cr2AlB2 is reported for the first time.

Modeling the mechanical behavior of ceramic and heterophase structures manufactured using selective laser sintering and spark plasma sintering

NASA Astrophysics Data System (ADS)

Skripnyak, Vladimir A.; Skripnyak, Evgeniya G.; Skripnyak, Vladimir V.; Vaganova, Irina K.

A model for predicting mechanical properties of ultra-high temperature ceramics and composites manufactured by selective laser sintering (SLS) and spark plasma sintering (SPS) under shock loading is presented. The model takes into account the porous structure, the specific volume and average sizes of phases, and the temperature of sintering. Residual stresses in ceramic composites reinforced with particles of refractory borides, carbides and nitrides after SLS or SPS were calculated. It is shown that the spall strength of diboride-zirconium matrix composites can be increased by the decreasing of porosity and the introduction of inclusions of specially selected refractory strengthening phases.

Materials for high-temperature thermoelectric conversion

NASA Technical Reports Server (NTRS)

Feigelson, R. S.; Elwell, D.

1983-01-01

High boron materials of high efficiency for thermoelectric power generation and capable of prolonged operation at temperatures over 1200 C are discussed. Background theoretical studies indicated that the low carrier mobility of materials with beta boron and related structures is probably associated with the high density of traps. Experimental work was mainly concerned with silicon borides in view of promising data from European laboratories. A systematic study using structure determination and lattice constant measurements failed to confirm the existence of an SiBn phase. Only SiB6 and a solid solution of silicon in beta boron with a maximum solid solubility of 5.5-6 at % at 1650 C were found.

Solid-state structures and properties of scandium hydride; hydrogen storage and switchable mirrors application

NASA Astrophysics Data System (ADS)

Khodja, Khadidja; Bouhadda, Youcef; Seddik, Larbi; Benyelloul, Kamel

2016-05-01

First-principles calculation has been performed on the rare earth hydride ScH2 for hydrogen storage and switchable mirror applications, using the pseudo-potentials and plane waves based on the density-functional theory (DFT). The electronic and structural properties are studied within both local-density and generalized gradient approximations for exchange energy. The formation energy and the optical properties have been investigated and discussed. Our calculated results are generally in good agreement with theoretical and experimental data. Contribution to the topical issue "Materials for Energy Harvesting, Conversion and Storage (ICOME 2015) - Elected submissions", edited by Jean-Michel Nunzi, Rachid Bennacer and Mohammed El Ganaoui

Jet-cooled laser-induced fluorescence spectroscopy of ScH: Observation of an Ω‧=2-Ω″=1 transition

NASA Astrophysics Data System (ADS)

Mukund, Sheo; Bhattacharyya, Soumen; Nakhate, S. G.

2014-11-01

New bands of scandium monohydride at origins 17,914.5 and 17,942.3 cm-1 have been observed in a jet-cooled beam with laser-induced fluorescence spectroscopy. Mass-selected resonant photoionization spectroscopy also confirmed the carrier of the band as ScH. The rotational analysis indicated that both transitions at 17,914.5 and 17,942.3 cm-1 are of Ω‧=2-Ω″=1 type with vibrational assignments (0,0) and (1,1) respectively. The assigned g3Φ2-a3Δ1 excitation is the first observed triplet-triplet transition in ScH.

Power-scaling performance of a three-dimensional tritium betavoltaic diode

NASA Astrophysics Data System (ADS)

Liu, Baojun; Chen, Kevin P.; Kherani, Nazir P.; Zukotynski, Stefan

2009-12-01

Three-dimensional diodes fabricated by electrochemical etching are exposed to tritium gas at pressures from 0.05 to 33 atm at room temperature to examine its power scaling performance. It is shown that the three-dimensional microporous structure overcomes the self-absorption limited saturation of beta flux at high tritium pressures. These results are contrasted against the three-dimensional device powered in one instance by tritium absorbed in the near surface region of the three-dimensional microporous network, and in another by a planar scandium tritide foil. These findings suggest that direct tritium occlusion in the near surface of three-dimensional diode can improve the specific power production.

Resource potential for commodities in addition to Uranium in sandstone-hosted deposits: Chapter 13

USGS Publications Warehouse

Breit, George N.

2016-01-01

Sandstone-hosted deposits mined primarily for their uranium content also have been a source of vanadium and modest amounts of copper. Processing of these ores has also recovered small amounts of molybdenum, rhenium, rare earth elements, scandium, and selenium. These deposits share a generally common origin, but variations in the source of metals, composition of ore-forming solutions, and geologic history result in complex variability in deposit composition. This heterogeneity is evident regionally within the same host rock, as well as within districts. Future recovery of elements associated with uranium in these deposits will be strongly dependent on mining and ore-processing methods.

High-strength laser welding of aluminum-lithium scandium-doped alloys

NASA Astrophysics Data System (ADS)

Malikov, A. G.; Ivanova, M. Yu.

2016-11-01

The work presents the experimental investigation of laser welding of an aluminum alloy (system Al-Mg-Li) and aluminum alloy (system Al-Cu-Li) doped with Sc. The influence of nano-structuring of the surface layer welded joint by cold plastic deformation on the strength properties of the welded joint is determined. It is founded that, regarding the deformation degree over the thickness, the varying value of the welded joint strength is different for these aluminum alloys. The strength of the plastically deformed welded joint, aluminum alloys of the Al-Mg-Li and Al-Cu-Li systems reached 0.95 and 0.6 of the base alloy strength, respectively.

Clinical Translation and First In-Human Use of [44Sc]Sc-PSMA-617 for PET Imaging of Metastasized Castrate-Resistant Prostate Cancer.

PubMed

Eppard, Elisabeth; de la Fuente, Ana; Benešová, Martina; Khawar, Ambreen; Bundschuh, Ralph A; Gärtner, Florian C; Kreppel, Barbara; Kopka, Klaus; Essler, Markus; Rösch, Frank

2017-01-01

Various trivalent radiometals are well suited for labeling of DOTA-conjugated variants of Glu-ureido-based prostate-specific membrane antigen (PSMA) inhibitors. The DOTA-conjugate PSMA-617 has proven high potential in PSMA radioligand therapy (PSMA-RLT) of prostate cancer as well as PET imaging when labeled with lutetium-177 and gallium-68 respectively. Considering the relatively short physical half-life of gallium-68 this positron emitter precludes prolonged acquisition periods, as required for pre-therapeutic dosimetry or intraoperative applications. In this context, the positron emitter scandium-44 is an attractive alternative for PET imaging. We report the synthesis of [ 44 Sc]Sc-PSMA-617 as radiopharmaceutical with generator produced scandium-44, its in vitro characterization and clinical translation as part of a first in-human study. Scandium-44 was obtained from a 44 Ti/ 44 Sc radionuclide generator. PSMA-617 was labeled with 142.4±12.7 MBq of scandium-44 in analogy to [ 68 Ga]Ga-PSMA-617 and evaluated in vitro and in cell studies using PSMA+ LNCaP cells. A first-in-human investigation was subsequently carried out in a cohort of 4 patients (mean age 70±1.8 a) registered for [ 177 Lu]Lu-PSMA-617 therapy. 50.5±9.3 MBq (40 µg, 38.4 nmol) [ 44 Sc]Sc-PSMA-617 were applied via intravenous injection (i.v.), respectively. A Siemens Biograph 2 PET/CT system was used to acquire initial dynamic PET data (30 min) of abdomen in list mode followed by static PET/CT data (skull to mid-thigh) at 45 min, 2 and 18 h post-injection (p.i.). For quantitative analysis, dynamic images were reconstructed as 6 data sets of 300 s each. The noise ratio was measured in liver, lung and an additional region outside the body. SUV values in different organs and lesions were measured and compared to [ 68 Ga]Ga-PSMA-11 data of the same patients. Residence times and organ absorbed doses were calculated using OLINDA/EXM software. Quantitative radiochemical yields of ≥98 % were achieved using 18 nmol of PSMA-617 after 20 min at 95 °C with apparent molar activity of 6.69±0.78 MBq/nmol. Following purification, >99 % radiochemical purity was obtained. [ 44 Sc]Sc-PSMA-617 showed high stability (>95 %) in serum for 24 h. The binding affinity and internalization fraction were determined in PSMA+ LNCaP cells (IC 50 = 4.72±0.7 nM and internalization fraction: 15.78±2.14 % IA/10 6 LNCaP cells) and compared to [ 68 Ga]Ga-PSMA-11 (12.0±2.8 nM and 9.47±2.56 % IA/10 6 LNCaP cells). Physiological tracer uptake was observed in kidneys, liver, spleen, small intestine, urinary bladder, and salivary glands and pathological uptake in both soft and skeletal metastases. SUV values were significantly lower in the kidneys (14.0) compared to [ 68 Ga]Ga-PSMA-11 OET (30.5). All other measured SUV values did not show a statistically significant difference. Tumor to liver ratios were found to lie between 1.9 and 8.3 for [ 68 Ga]Ga-PSMA-11 and between 2.5 and 8.8 for [ 44 Sc]Sc-PSMA-617 after 120 min. For [ 44 Sc]Sc-PSMA-617 the ratios were higher and no statistically significant differences were observed. Total and % activity were highest in liver followed by kidneys, spleen, small intestine and salivary glands. Rapid wash out was seen in liver and spleen and gradually over time in kidneys. Kidneys received the highest radiation absorbed dose of 0.354 (0.180-0.488) mSv/MBq. No adverse pharmacological effects were observed. In conclusion [ 44 Sc]Sc-PSMA-617 PET is suitable for PET imaging of prostate cancer tissue. [ 44 Sc]Sc-PSMA-617 shows promise to enable pre-therapeutic dosimetry in clinical settings. However, the clinical advantages for individual dosimetry or other applications like intraoperative applications have to be investigated in further studies.

Clinical Translation and First In-Human Use of [44Sc]Sc-PSMA-617 for PET Imaging of Metastasized Castrate-Resistant Prostate Cancer

PubMed Central

Eppard, Elisabeth; de la Fuente, Ana; Benešová, Martina; Khawar, Ambreen; Bundschuh, Ralph A.; Gärtner, Florian C.; Kreppel, Barbara; Kopka, Klaus; Essler, Markus; Rösch, Frank

2017-01-01

Background: Various trivalent radiometals are well suited for labeling of DOTA-conjugated variants of Glu-ureido-based prostate-specific membrane antigen (PSMA) inhibitors. The DOTA-conjugate PSMA-617 has proven high potential in PSMA radioligand therapy (PSMA-RLT) of prostate cancer as well as PET imaging when labeled with lutetium-177 and gallium-68 respectively. Considering the relatively short physical half-life of gallium-68 this positron emitter precludes prolonged acquisition periods, as required for pre-therapeutic dosimetry or intraoperative applications. In this context, the positron emitter scandium-44 is an attractive alternative for PET imaging. We report the synthesis of [44Sc]Sc-PSMA-617 as radiopharmaceutical with generator produced scandium-44, its in vitro characterization and clinical translation as part of a first in-human study. Methods: Scandium-44 was obtained from a 44Ti/44Sc radionuclide generator. PSMA-617 was labeled with 142.4±12.7 MBq of scandium-44 in analogy to [68Ga]Ga-PSMA-617 and evaluated in vitro and in cell studies using PSMA+ LNCaP cells. A first-in-human investigation was subsequently carried out in a cohort of 4 patients (mean age 70±1.8 a) registered for [177Lu]Lu-PSMA-617 therapy. 50.5±9.3 MBq (40 µg, 38.4 nmol) [44Sc]Sc-PSMA-617 were applied via intravenous injection (i.v.), respectively. A Siemens Biograph 2 PET/CT system was used to acquire initial dynamic PET data (30 min) of abdomen in list mode followed by static PET/CT data (skull to mid-thigh) at 45 min, 2 and 18 h post-injection (p.i.). For quantitative analysis, dynamic images were reconstructed as 6 data sets of 300 s each. The noise ratio was measured in liver, lung and an additional region outside the body. SUV values in different organs and lesions were measured and compared to [68Ga]Ga-PSMA-11 data of the same patients. Residence times and organ absorbed doses were calculated using OLINDA/EXM software. Results: Quantitative radiochemical yields of ≥98 % were achieved using 18 nmol of PSMA-617 after 20 min at 95 °C with apparent molar activity of 6.69±0.78 MBq/nmol. Following purification, >99 % radiochemical purity was obtained. [44Sc]Sc-PSMA-617 showed high stability (>95 %) in serum for 24 h. The binding affinity and internalization fraction were determined in PSMA+ LNCaP cells (IC50 = 4.72±0.7 nM and internalization fraction: 15.78±2.14 % IA/106 LNCaP cells) and compared to [68Ga]Ga-PSMA-11 (12.0±2.8 nM and 9.47±2.56 % IA/106 LNCaP cells). Physiological tracer uptake was observed in kidneys, liver, spleen, small intestine, urinary bladder, and salivary glands and pathological uptake in both soft and skeletal metastases. SUV values were significantly lower in the kidneys (14.0) compared to [68Ga]Ga-PSMA-11 OET (30.5). All other measured SUV values did not show a statistically significant difference. Tumor to liver ratios were found to lie between 1.9 and 8.3 for [68Ga]Ga-PSMA-11 and between 2.5 and 8.8 for [44Sc]Sc-PSMA-617 after 120 min. For [44Sc]Sc-PSMA-617 the ratios were higher and no statistically significant differences were observed. Total and % activity were highest in liver followed by kidneys, spleen, small intestine and salivary glands. Rapid wash out was seen in liver and spleen and gradually over time in kidneys. Kidneys received the highest radiation absorbed dose of 0.354 (0.180-0.488) mSv/MBq. No adverse pharmacological effects were observed. Conclusion: In conclusion [44Sc]Sc-PSMA-617 PET is suitable for PET imaging of prostate cancer tissue. [44Sc]Sc-PSMA-617 shows promise to enable pre-therapeutic dosimetry in clinical settings. However, the clinical advantages for individual dosimetry or other applications like intraoperative applications have to be investigated in further studies. PMID:29158832

Numerical and experimental study of electron-beam coatings with modifying particles FeB and FeTi

NASA Astrophysics Data System (ADS)

Kryukova, Olga; Kolesnikova, Kseniya; Gal'chenko, Nina

2016-07-01

An experimental study of wear-resistant composite coatings based on titanium borides synthesized in the process of electron-beam welding of components thermo-reacting powders are composed of boron-containing mixture. A model of the process of electron beam coating with modifying particles of boron and titanium based on physical-chemical transformations is supposed. The dissolution process is described on the basis of formal kinetic approach. The result of numerical solution is the phase and chemical composition of the coating under nonequilibrium conditions, which is one of the important characteristics of the coating forming during electron beam processing. Qualitative agreement numerical calculations with experimental data was shown.

A new superhard material: Osmium diboride OsB 2

NASA Astrophysics Data System (ADS)

Hebbache, M.; Stuparević, L.; Živković, D.

2006-08-01

Superhard materials have many industrial applications, wherever resistance to abrasion and wear are important. The synthesis of new superhard materials is one of the great challenges to scientists. We re-examined the phase diagram of the binary osmium-boron system and confirmed the existence of two hexagonal phases, OsB 1.1, Os 2B 3, and an orthorhombic phase, OsB 2. Almost nothing is known about the physical properties of osmium borides. Microhardness measurements show that OsB 2 is extremely hard. Ab initio calculations show that this is due to formation of covalent bonds between boron atoms. OsB 2 is also a low compressibility material. It can be used as hard coating.

First-principles study of low compressibility osmium borides

NASA Astrophysics Data System (ADS)

Gou, Huiyang; Hou, Li; Zhang, Jingwu; Li, Hui; Sun, Guifang; Gao, Faming

2006-05-01

Using first-principles total energy calculations we investigate the structural, elastic, and electronic properties of OsB2 and OsB, respectively. The calculated equilibrium structural parameters of OsB2 are in agreement with the available experimental results. The calculations indicate that OsB in tungsten carbide is more energetically stable under the ambient condition than the metastable cesium chloride phase of OsB. Results of bulk modulus show that they are potential low compressible materials. The hardness of OsB2 is estimated by employing a semiempirical theory. The results indicate that OsB2 is an ultraincompressible material, but not a superhard material. The method designing superhard materials is different from one creating ultraincompressible materials.

The friction and wear properties of sputtered hard refractory compounds

NASA Technical Reports Server (NTRS)

Brainard, W. A.

1978-01-01

Several refractory silicide, boride, and carbide coatings were examined. The coatings were applied to type 440C steel surfaces by radio-frequency sputtering. The friction and wear properties of the coatings were found to be related to stoichiometry and impurity content of the bulk coating as well as the degree of interfacial adherence between coating and substrate. Bulk coating stoichiometry could to a large extent be controlled by the application of a negative bias voltage during deposition. Adherence was promoted by the formation of an oxidized layer at the interface. Deliberate preoxidizing of the 440C produced enhanced adherence for many compounds which are related to the formation of a mixed oxide transition region.

Passivating overcoat bilayer for multilayer reflective coatings for extreme ultraviolet lithography

DOEpatents

Montcalm, Claude; Stearns, Daniel G.; Vernon, Stephen P.

1999-01-01

A passivating overcoat bilayer is used for multilayer reflective coatings for extreme ultraviolet (EUV) or soft x-ray applications to prevent oxidation and corrosion of the multilayer coating, thereby improving the EUV optical performance. The overcoat bilayer comprises a layer of silicon or beryllium underneath at least one top layer of an elemental or a compound material that resists oxidation and corrosion. Materials for the top layer include carbon, palladium, carbides, borides, nitrides, and oxides. The thicknesses of the two layers that make up the overcoat bilayer are optimized to produce the highest reflectance at the wavelength range of operation. Protective overcoat systems comprising three or more layers are also possible.

Assessment of the State of the Art of Ultra High Temperature Ceramics

NASA Technical Reports Server (NTRS)

Johnson, Sylvia; Gasch, Matt; Stackpoole, Mairead

2009-01-01

Ultra High Temperature Ceramics (UHTCs) are a family of materials that includes the borides, carbides and nitrides of hafnium-, zirconium- and titanium-based systems. UHTCs are famous for possessing some of the highest melting points of known materials. In addition, they are very hard, have good wear resistance, mechanical strength, and relatively high thermal conductivities (compared to other ceramic materials). Because of these attributes, UHTCs are ideal for thermal protection systems, especially those that require chemical and structural stability at extremely high operating temperatures. UHTCs have the potential to revolutionize the aerospace industry by enabling the development of sharp hypersonic vehicles or atmospheric entry probes capable of the most extreme entry conditions.

Identification of novel sulfur-containing steroids in sediments and petroleum: probable incorporation of sulfur into δ 5,7-sterols during early diagenesis

NASA Astrophysics Data System (ADS)

Sinninghe Damsté, Jaap S.; Schouten, Stefan; de Leeuw, Jan W.; van Duin, Adri C. T.; Geenevasen, Jan A. J.

1999-01-01

A novel sulfur-containing sterane, 4α,7α-epithio-5β-cholestane, has been identified in a sediment extract from the Miocene Northern Apennines marl (Italy) after its isolation by column chromatography and high pressure liquid chromatography. The compound has been characterised by GC-MS and mild Nickel boride desulfurisation and one and two-dimensional 1H NMR techniques. C 27-C 29 homologs have been detected in sediment extracts of three different formations and in one petroleum sample. These sulfur-containing steroids are probably formed by an intramolecular reaction of inorganic sulfides with early diagenetic products of Δ 5,7-sterols.

Synthetic laser medium

DOEpatents

Stokowski, S.E.

1987-10-20

A laser medium is particularly useful in high average power solid state lasers. The laser medium includes a chromium dopant and preferably neodymium ions as codopant, and is primarily a gadolinium scandium gallium garnet, or an analog thereof. Divalent cations inhibit spiral morphology as large boules from which the laser medium is derived are grown, and a source of ions convertible between a trivalent state and a tetravalent state at a low ionization energy are in the laser medium to reduce an absorption coefficient at about one micron wavelength otherwise caused by the divalent cations. These divalent cations and convertible ions are dispersed in the laser medium. Preferred convertible ions are provided from titanium or cerium sources.

Synthetic laser medium

DOEpatents

Stokowski, Stanley E.

1989-01-01

A laser medium is particularly useful in high average power solid state lasers. The laser medium includes a chormium dopant and preferably neodymium ions as codopant, and is primarily a gadolinium scandium gallium garnet, or an analog thereof. Divalent cations inhibit spiral morphology as large boules from which the laser medium is derived are grown, and a source of ions convertible between a trivalent state and a tetravalent state at a low ionization energy are in the laser medium to reduce an absorption coefficient at about one micron wavelength otherwise caused by the divalent cations. These divalent cations and convertible ions are dispersed in the laser medium. Preferred convertible ions are provided from titanium or cerium sources.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Saha, Bivas; Birck Nanotechnology Center, Purdue University, West Lafayette, Indiana 47907; Lawrence, Samantha K.

High hardness TiAlN alloys for wear-resistant coatings exhibit limited lifetimes at elevated temperatures due to a cubic-AlN to hexagonal-AlN phase transformation that leads to decreasing hardness. We enhance the hardness (up to 46 GPa) and maximum operating temperature (up to 1050 °C) of TiAlN-based coatings by alloying with scandium nitride to form both an epitaxial TiAlScN alloy film and epitaxial rocksalt TiN/(Al,Sc)N superlattices on MgO substrates. The superlattice hardness increases with decreasing period thickness, which is understood by the Orowan bowing mechanism of the confined layer slip model. These results make them worthy of additional research for industrial coating applications.

RESEARCH ON PHYSICAL AND CHEMICAL PRINCIPLES AFFECTING HIGH TEMPERATURE MATERIALS FOR ROCKET NOZZLES. Quarterly Progress Report, April 1, 1963-June 30, 1963

DOE Office of Scientific and Technical Information (OSTI.GOV)

Lowrie, R.

1963-10-31

The development and properties of refractory materials are described. Corrosion of zirconium carbide, niobium carbide, and niobium carbide-zirconium carbide systems by carbon dioxide and hydrochloric acid at 2250 deg C is reported. Corrosion of silver-tungsten alloys by carbon dioxide and oxygen at 2150 to 2440 deg K is summarized. Measurements of pyrolytic and ZTA graphite corrosion by carbon dioxide and oxygen at 2100 to 2800 deg K are shown. At 2300 deg C the rate of formation of methane from graphite and hydrogen is greatly reduced by the addition of helium, at constant hydrogen pressure. Up to 2000 deg Cmore » the effect of helium is small. The pyrolysis of methane on graphite at 2000 deg C is tabulated. Oxidation of tungsten to form WO/sub 2/ and WO/sub 3/ is reported. Vaporization of hafnium borides at 2297 to 2538 deg K is analyzed. The lattice parameters of ZrB/sub 2/ at of TiN/sub 0.6/ and TiN/sub 0.75/ are discussed. Powder metallurgical techniques are used to prepare TiB/sub 2/, ZrB/sub 2/, HfB/ sub 2/, NbB/sub 2/, a nd TaB/sub 2/ for detailed x-ray characterization. The electric conductivity of NbC-ZrC systems is reported. General descriptions are given of analytical techniques for free carbon in carbides and spectrographic methods for metallic impurities in carbides and borides. Preliminary roomtemperature measurements are reported of the elastic properties of polycrystalline ZrB/sub 2/. Titanium carbide is brazed to tungsten with a platinum-boron system. A largegrained polycrystalline specimen of ZrC is plastically deformed in creep at 2134 deg C. Metallographic and x-ray examinations of polycrystalline TiC specimens deformed in creep reveal an increasing development with deformation of subgrains having preferred orientation. (N.W.R.)« less

Implant Bed Preparation with an Erbium, Chromium Doped Yttrium Scandium Gallium Garnet (Er,Cr: YSGG) Laser Using Stereolithographic Surgical Guide

PubMed Central

Seymen, Gülin; Turgut, Zeynep; Berk, Gizem; Bodur, Ayşen

2013-01-01

Background: Implant bed preparation with laser is taken into consideration owing to the increased interest in use of lasers in hard tissue surgery. The purpose of this study is to determine the deviations in the position and inclination between the planned and prepared implant beds with Erbium, Chromium doped Yttrium Scandium Gallium Garnet (Er,Cr:YSGG) laser using stereolithographic (SLA) surgical guides. Methods: After 3-dimensional (3D) imaging of six sheep lower jaws, computed tomography (CT) images were transformed into 3D models. Locations of implant beds were determined on these models. Two implant beds in each half jaw were prepared with an Er,Cr:YSGG laser system and a conventional drilling method using a total of 12 SLA surgical guides. A new CT was taken to analyze the deviation values between planned and prepared implant beds. Finally, a software program was used to superimpose the images on 3D models, then the laser and conventional drilling groups were compared. Results: Differences of mean angular deviations between the planned and prepared implant beds were 5.17±4.91° in the laser group and 2.02±1.94° in the conventional drilling group.The mean coronal deviation values were found to be 0.48±0.25 mm and 0.23±0.14 mm in the laser group and conventional drilling group, respectively. While the mean deviation at the apex between the planned and prepared implant beds were 0.70±0.26 mm and 0.26±0.08 ,the mean vertical deviations were 0.06±0.15 mm and 0.02±0.05 mm for the laser group and the conventional drilling group, respectively. Conclusion: It is possible to prepare an implant bed properly with the aid of Er,Cr:YSGGlaser by using SLA surgical guide. PMID:25606303

Efficacy of Erbium, Chromium-doped:Yttrium, Scandium, Gallium, and Garnet Laser Irradiation Combined with Resin-based Tricalcium Silicate and Calcium Hydroxide on Direct Pulp Capping: A Randomized Clinical Trial.

PubMed

Cengiz, Esra; Yilmaz, Hasan Guney

2016-03-01

The purpose of this randomized clinical study was to evaluate the efficiency of erbium, chromium-doped:yttrium, scandium, gallium, and garnet (Er,Cr:YSGG) laser irradiation combined with a resin-based tricalcium silicate material and calcium hydroxide in direct pulp capping for a 6-month follow-up period. A total of 60 teeth of 60 patients between the ages of 18 and 41 years were recruited for this study. Sixty permanent vital teeth without symptoms and radiographic changes were randomly assigned to the following 4 groups (n = 15): Gr CH, the exposed area was sealed with calcium hydroxide (CH) paste; Gr laser CH, the treated area was sealed with CH paste after Er,Cr:YSGG laser irradiation at an energy level of 0.5 W without water and with 45% air; Gr TheraCal, TheraCal LC (Bisco, Schaumburg, IL) was applied directly to the exposed pulp; and Gr Laser TheraCal, TheraCal LC was applied after irradiation with an Er,Cr:YSGG laser. At the 1-week and 1-, 3-, and 6-month recall examinations, the loss of vitality, spontaneous pain, reactions to thermal stimuli and percussion, and radiographic changes were considered as failure. The success rates in the CH and TheraCal groups were 73.3% and 66.6%, respectively. These rates did not reveal any significant difference. In both laser groups, success rates were 100%. The Er,Cr:YSGG laser-irradiated TheraCal and Er,Cr:YSGG laser-irradiated CH groups showed statistically higher success rates than the TheraCal and CH groups, respectively. Er,Cr:YSGG laser irradiation at 0.5 W without water combined with pulp capping agents can be recommended for direct pulp therapy. Copyright © 2016 American Association of Endodontists. Published by Elsevier Inc. All rights reserved.

Studies of soil and ecohydrological processes in oil-gas production regions.

NASA Astrophysics Data System (ADS)

Khodyreva, E. Ya.; Khodyrev, Yu. P.

2009-04-01

For a better understanding and describing of the functional interactions between processes in soil and drinking, underground and stratum waters in oil-gas production regions we used laboratory and field monitoring methods of studies. The control of ecological situation dynamics in oil-gas production regions proposes a presence of primary data about parameter-indicators, which characterize a state of the object under investigation. One of these parameters is the concentration of heavy metal salts in drinking and stratum waters. Isolation of some compounds, which are extracted as impurities of oil and water during recovery of hydrocarbons from productive horizons, would enhance profitableness of recovery. Because accompanying impurities are a mixture of different salts and complexes, the methods of multielement analysis give the most objective evaluation of total content of some elements by search and prospecting. The developed method of laser mass-spectrometric analysis of oil and drinking, underground and industrial waters allows to investigate the samples on all elements of the periodical system simultaneously with limit sensitivity 0.1 mkg/l. The preparation of the oil and water probes was carried out by sublimation of highly volatile fractions in vacuum at 100 0C. The samples of drinking and underground waters, oils and industrial waters from wells of oil field Romashkin (Tatarstan) were chosen as the object for the research. In respect to possible metal extraction scandium is of most interest in inspected area because it's very high cost and availability of water-soluble pattern, most probably chloride. Its concentration in one well was 1 mg/l in water and 0.01 mg/l in oil. According to the received data of laser mass-spectrometric analysis, industrial waters on the activity investigated territory joint-stock company "Tatneft" contain 220-330 kg / ton of salts of metals that does by their potential source of alternative raw material for the chemical industry. Soil is an important component of the earth's biosphere because of its crucial role in the hydrological cycle. For revealing possible correlation between spatial distributions of the valuable elements contained both in industrial waters and in tests of soils, 79 samples are prepared and investigated. These tests are selected at superficial geochemical shooting (field monitoring methods of studies) Aznakaevskoi, Karamalinskoi and Sabanchinskoi areas of joint-stock company " Tatneft ". Circuits of distribution of valuable elements on the investigated territory are constructed also a quantitative estimation of the maintenance makro- and microcomponents is given. From the found out elements the greatest interest Na, Mg, K, Ca, Cl, Br and their connections represent because of very high concentration and scandium owing to the cost. Now cost of scandium in the world market approximately in 25 times exceeds cost of gold and is not observed yet tendencies to its decrease. Presence of impurity of salts of heavy metals and their connections in soils, drinking, underground and stratum waters, definition of their concentration and comparison from maximum concentration limit allows to establish the control over dynamics of ecohydrological conditions and in due time to take measures on reduction of negative influence of processes of development of hydrocarbon raw material by an environment.

Scandium complexes with the tetraphenylethylene and anthracene dianions.

PubMed

Ellis, John E; Minyaev, Mikhail E; Nifant'ev, Ilya E; Churakov, Andrei V

2018-06-01

The structural study of Sc complexes containing dianions of anthracene and tetraphenylethylene should shed some light on the nature of rare-earth metal-carbon bonding. The crystal structures of (18-crown-6)bis(tetrahydrofuran-κO)sodium bis(η 6 -1,1,2,2-tetraphenylethenediyl)scandium(III) tetrahydrofuran disolvate, [Na(C 4 H 8 O) 2 (C 12 H 24 O 6 )][Sc(C 26 H 20 ) 2 ]·2C 4 H 8 O or [Na(18-crown-6)(THF) 2 ][Sc(η 6 -C 2 Ph 4 ) 2 ]·2(THF), (1b), (η 5 -1,3-diphenylcyclopentadienyl)(tetrahydrofuran-κO)(η 6 -1,1,2,2-tetraphenylethenediyl)scandium(III) toluene hemisolvate, [Sc(C 17 H 13 )(C 26 H 20 )(C 4 H 8 O)]·0.5C 7 H 8 or [(η 5 -1,3-Ph 2 C 5 H 3 )Sc(η 6 -C 2 Ph 4 )(THF)]·0.5(toluene), (5b), poly[[(μ 2 -η 3 :η 3 -anthracenediyl)bis(η 6 -anthracenediyl)bis(η 5 -1,3-diphenylcyclopentadienyl)tetrakis(tetrahydrofuran)dipotassiumdiscandium(III)] tetrahydrofuran monosolvate], {[K 2 Sc 2 (C 14 H 10 ) 3 (C 17 H 13 ) 2 (C 4 H 8 O) 4 ]·C 4 H 8 O} n or [K(THF) 2 ] 2 [(1,3-Ph 2 C 5 H 3 ) 2 Sc 2 (C 14 H 10 ) 3 ]·THF, (6), and 1,4-diphenylcyclopenta-1,3-diene, C 17 H 14 , (3a), have been established. The [Sc(η 6 -C 2 Ph 4 ) 2 ] - complex anion in (1b) contains the tetraphenylethylene dianion in a symmetrical bis-η 3 -allyl coordination mode. The complex homoleptic [Sc(η 6 -C 2 Ph 4 ) 2 ] - anion retains its structure in THF solution, displaying hindered rotation of the coordinated phenyl rings. The 1D 1 H and 13 C{ 1 H}, and 2D COSY 1 H- 1 H and 13 C- 1 H NMR data are presented for M[Sc(Ph 4 C 2 ) 2 ]·xTHF [M = Na and x = 4 for (1a); M = K and x = 3.5 for (2a)] in THF-d 8 media. Complex (5b) exhibits an unsymmetrical bis-η 3 -allyl coordination mode of the dianion, but this changes to a η 4 coordination mode for (1,3-Ph 2 C 5 H 3 )Sc(Ph 4 C 2 )(THF) 2 , (5a), in THF-d 8 solution. A 45 Sc NMR study of (2a) and UV-Vis studies of (1a), (2a) and (5a) indicate a significant covalent contribution to the Sc-Ph 4 C 2 bond character. The unique Sc ate complex, (6), contains three anthracenide dianions demonstrating both a η 6 -coordination mode for two bent ligands and a μ 2 -η 3 :η 3 -bridging mode of a flat ligand. Each [(1,3-Ph 2 C 5 H 3 ) 2 Sc 2 (C 14 H 10 ) 3 ] 2- dianionic unit is connected to four neighbouring units via short contacts with [K(THF) 2 ] + cations, forming a two-dimensional coordination polymer framework parallel to (001).

The effect of anti-phase domain size on the ductility of a rapidly solidified Ni3Al-Cr alloy

NASA Technical Reports Server (NTRS)

Carro, G.; Bertero, G. A.; Wittig, J. E.; Flanagan, W. F.

1989-01-01

Tensile tests on splat-quenched Ni3Al-Cr alloys showed a sharp decrease in ductility with long-time annealing. The growth of the initially very-fine-size anti-phase domains showed a tenuous correlation with ductility up to a critical size, where ductility was lost. The grain size was relatively unaffected by these annealing treatments, but the grain-boundary curvature decreased, implying less toughness. An important observation was that, for the longest annealing time, a chromium-rich precipitate formed, which the data indicate could be a boride. Miniaturized tensile tests were performed on samples which were all obtained from the same splat-quenched foil, and the various domain sizes were controlled by subsequent annealing treatments.

Two phase titanium aluminide alloy

DOEpatents

Deevi, Seetharama C.; Liu, C. T.

2001-01-01

A two-phase titanic aluminide alloy having a lamellar microstructure with little intercolony structures. The alloy can include fine particles such as boride particles at colony boundaries and/or grain boundary equiaxed structures. The alloy can include alloying additions such as .ltoreq.10 at % W, Nb and/or Mo. The alloy can be free of Cr, V, Mn, Cu and/or Ni and can include, in atomic %, 45 to 55% Ti, 40 to 50% Al, 1 to 5% Nb, 0.3 to 2% W, up to 1% Mo and 0.1 to 0.3% B. In weight %, the alloy can include 57 to 60% Ti, 30 to 32% Al, 4 to 9% Nb, up to 2% Mo, 2 to 8% W and 0.02 to 0.08% B.

Combustion synthesis of boride and other composites

DOEpatents

Halverson, Danny C.; Lum, Beverly Y.; Munir, Zuhair A.

1989-01-01

A self-sustaining combustion synthesis process for producing hard, tough, lightweight B.sub.4 C/TiB.sub.2 composites is based on the thermodynamic dependence of adiabatic temperature and product composition on the stoichiometry of the B.sub.4 C and TiB.sub.2 reactants. For lightweight products the composition must be relatively rich in the B.sub.4 C component. B.sub.4 C-rich composites are obtained by varying the initial temperature of the reactants. The product is hard, porous material whose toughness can be enhanced by filling the pores with aluminum or other metal phases using a liquid metal infiltration process. The process can be extended to the formation of other composites having a low exothermic component.

Oxidation-induced contraction and strengthening of boron fibers

NASA Technical Reports Server (NTRS)

Dicarlo, J. A.; Wagner, T. C.

1981-01-01

An investigation was conducted to measure and understand the physical and mechanical effects that occur in boron fibers during and after thermal treatment in a controlled oxygen argon gaseous mixture. Of principal concern was the optimization of this treatment as a secondary processing method for significantly improving fiber tensile strength. Strengthening was accomplished by an oxidation induced axial contraction of the fiber and a resulting axial compression of strength limiting flaws within the fiber's tungsten boride core. Various physical observations were used to develop mechanistic models for oxidation, contraction, and flow formation. Processing guidelines are discussed for possibly exceeding the 5.5 GN/sq m strength limit and also for achieving fiber strengthening during application of boron containing diffusion barrier coatings.

Characterization and Computational Modeling of Minor Phases in Alloy LSHR

NASA Technical Reports Server (NTRS)

Jou, Herng-Jeng; Olson, Gregory; Gabb, Timothy; Garg, Anita; Miller, Derek

2012-01-01

The minor phases of powder metallurgy disk superalloy LSHR were studied. Samples were consistently heat treated at three different temperatures for long times to approach equilibrium. Additional heat treatments were also performed for shorter times, to assess minor phase kinetics in non-equilibrium conditions. Minor phases including MC carbides, M23C6 carbides, M3B2 borides, and sigma were identified. Their average sizes and total area fractions were determined. CALPHAD thermodynamics databases and PrecipiCalc(TradeMark), a computational precipitation modeling tool, were employed with Ni-base thermodynamics and diffusion databases to model and simulate the phase microstructural evolution observed in the experiments with an objective to identify the model limitations and the directions of model enhancement.

Self-propagating high-temperature synthesis and luminescent properties of ytterbium doped rare earth (Y, Sc, Lu) oxides nanopowders

NASA Astrophysics Data System (ADS)

Permin, D. A.; Novikova, A. V.; Balabanov, S. S.; Gavrishchuk, E. M.; Kurashkin, S. V.; Savikin, A. P.

2018-04-01

This paper describes a comparative study of structural and luminescent properties of 5%Yb-doped yttrium, scandium, and lutetium oxides (Yb:RE2O3) powders and ceramics fabricated by self-propagating high-temperature synthesis. According to X-ray diffractometry and electron microscopy the chosen method ensures preparation of low-agglomerated cubic Ctype crystal structured powders at one step. No crucial differences in luminescence spectra were found the Yb:RE2O3 powders and ceramics. It was shown that the emission lifetimes of the Yb:RE2O3 powders are lowered by crystal structure defects, while its values for ceramics samples are compared to that of monocrystals and more influenced by rare earth impurities.

Selective Precipitation of Thorium lodate from a Tartaric Acid-Hydrogen Peroxide Medium Application to Rapid Spectrophotometric Determination of Thorium in Silicate Rocks and in Ores

USGS Publications Warehouse

Grimaldi, F.S.

1957-01-01

This paper presents a selective iodate separation of thorium from nitric acid medium containing d-tartaric acid and hydrogen peroxide. The catalytic decomposition of hydrogen peroxide is prevented by the use of 8quinolinol. A few micrograms of thorium are separated sufficiently clean from 30 mg. of such oxides as cerium, zirconium, titanium, niobium, tantalum, scandium, or iron with one iodate precipitation to allow an accurate determination of thorium with the thoronmesotartaric acid spectrophotometric method. The method is successful for the determination of 0.001% or more of thorium dioxide in silicate rocks and for 0.01% or more in black sand, monazite, thorite, thorianite, eschynite, euxenite, and zircon.

Releasing effects in flame photometry: Determination of calcium

USGS Publications Warehouse

Dinnin, J.I.

1960-01-01

Strontium, lanthanum, neodymium, samarium, and yttrium completely release the flame emission of calcium from the depressive effects of sulfate, phosphate, and aluminate. Magnesium, beryllium, barium, and scandium release most of the calcium emission. These cations, when present in high concentration, preferentially form compounds with the depressing anions when the solution is evaporated rapidly in the flame. The mechanism of the interference and releasing effects is explained on the basis of the chemical equilibria in the evaporating droplets of solution and is shown to depend upon the nature of the compounds present in the aqueous phase of the solution. The need for background correction techniques is stressed. The releasing effect is used in the determination of calcium in silicate rocks without the need for separations.

Preparation and quantification of radioactive particles for tracking hydrodynamic behavior in multiphase reactors.

PubMed

Yunos, Mohd Amirul Syafiq Mohd; Hussain, Siti Aslina; Yusoff, Hamdan Mohamed; Abdullah, Jaafar

2014-09-01

Radioactive particle tracking (RPT) has emerged as a promising and versatile technique that can provide rich information about a variety of multiphase flow systems. However, RPT is not an off-the-shelf technique, and thus, users must customize RPT for their applications. This paper presents a simple procedure for preparing radioactive tracer particles created via irradiation with neutrons from the TRIGA Mark II research reactor. The present study focuses on the performance evaluation of encapsulated gold and scandium particles for applications as individual radioactive tracer particles using qualitative and quantitative neutron activation analysis (NAA) and an X-ray microcomputed tomography (X-ray Micro-CT) scanner installed at the Malaysian Nuclear Agency. Copyright © 2014 Elsevier Ltd. All rights reserved.

Longitudinal residual stresses in boron fibers

NASA Technical Reports Server (NTRS)

Behrendt, D. R.

1976-01-01

A method of measuring the longitudinal residual stress distribution in boron fibers is presented. The residual stresses in commercial CVD boron on tungsten fibers of 102, 142, and 203 microns (4, 5.6, and 8 mil) diameters were determined. Results for the three sizes show a compressive stress at the surface 800 to -1400 MN/sq m 120 to -200 ksi), changing monotonically to a region of tensile stress within the boron. At approximately 25 percent of the original radius, the stress reaches a maximum tensile 600 to 1000 MN/sq m(90 to 150 ksi) and then decreases to compressive near the tungsten boride core. The core itself is under a compressive stress of approximately -1300 MN/sq m (-190 ksi). The effects of surface removal on core residual stress and core-initiated fracture are discussed.

High-pressure, high-temperature synthesis of superhard boron suboxide

DOE Office of Scientific and Technical Information (OSTI.GOV)

Hubert, H.; Garvie, L.A.J.; Leinenweber, K.

A multianvil device was used to investigate the formation of B{sub x}O phases produced in the 2 to 10 GPa pressure range with temperatures between 1,000 and 1,800 C. Amorphous and crystalline B and BP were oxidized using B{sub 2}O{sub 3} and CrO{sub 3}. Using powder X-ray diffraction and parallel electron energy-loss spectroscopy (PEELS), the authors were unable to detect graphitic or diamond-structured B{sub 2}O, reported in previous studies. The refractory boride B{sub 6}O, which has the {alpha}-rhombohedral boron structure, is the dominant suboxide in the P and T range of the investigation. PEELS with a transmission electron microscope wasmore » used to characterize the boron oxides.« less

Combustion synthesis of boride and other composites

DOEpatents

Halverson, D.C.; Lum, B.Y.; Munir, Z.A.

1988-07-28

A self-sustaining combustion synthesis process for producing hard, tough, lightweight B/sub 4/C/TiB/sub 2/ composites is described. It is based on the thermodynamic dependence of adiabatic temperature and product composition on the stoichiometry of the B/sub 4/C and TiB/sub 2/ reactants. For lightweight products the composition must be relatively rich in the B/sub 4/C component. B/sub 4/C-rich composites are obtained by varying the initial temperature of the reactants. The product is hard, porous material whose toughness can be enhanced by filling the pores with aluminum or other metal phases using a liquid metal infiltration process. The process can be extended to the formation of other composites having a low exothermic component. 9 figs., 4 tabs.

Oxidation-induced contraction and strengthening of boron fibers

NASA Technical Reports Server (NTRS)

Dicarlo, J. A.; Wagner, T. C.

1981-01-01

An investigation of the physical and mechanical effects of thermal treatment in a controlled oxygen-argon atmosphere on boron fibers is reported, with attention to the optimization of such treatment as a secondary processing method for improvement of fiber strength. The strengthening mechanism is comprised of an oxidation-induced axial contraction of the fiber, accompanied by axial compression of strength-limiting flaws within the fiber's tungsten boride core. It was found that after an oxidation contraction of 0.3% near 900 C, and a slight surface etch near 100 C, the average tensile strength of 203-micron fibers increased from 500 to 800 ksi. Various physical observations are used to develop mechanistic models of oxidation, contraction, and the formation of new flaws in the boron sheath at contractions greater than 0.3%.

Direct synthesis of calcium borohydride

DOEpatents

Ronnebro, Ewa Carin Ellinor [Dublin, CA; Majzoub, Eric H [Pleasanton, CA

2009-10-27

A method is disclosed for directly preparing an alkaline earth metal borohydride, i.e. Ca(BH.sub.4).sub.2, from the alkaline earth metal hydride and the alkaline earth metal boride. The borohydride thus prepared is doped with a small portion of a metal chloride catalyst compound, such as RuCl.sub.3, TiCl.sub.3, or a mixture of TiCl.sub.3 and palladium metal. The process provides for mechanically mixing the dry reagents under an inert atmosphere followed by charging the mixed materials with high pressure hydrogen at about 70 MPa while heating the mixture to about 400.degree. C. The method is relatively simple and inexpensive and provides reversible hydride compounds which are free of the usual contamination introduced by prior art wet chemical methods.

The measurement of radiation exposure of astronauts by radiochemical techniques

NASA Technical Reports Server (NTRS)

Brodzinski, R. L.

1971-01-01

The concentrations of 23 major, minor, and trace elements in the fecal samples from the Apollo 12 and 13 astronauts are reported. Most elemental excretion rates are comparable to rates reported for earlier missions. Exceptions are noted for calcium, iron, and tin. Body calcium and iron losses appear to be reduced during the Apollo 12 and 13 missions such that losses now seem to be insignificant. Refined measurements of tin excretion rates agree with normal dietary intakes. Earlier reported tin values are in error. A new passive dosimetry canister was designed which contains foils of tantalum, copper, titanium, iron, cobalt, aluminum, and scandium. By measuring the concentrations of the various products of nuclear reactions in these metals after space exposure, the characteristics of the incident cosmic particles can be determined.

High magnesium mobility in ternary spinel chalcogenides

DOE Office of Scientific and Technical Information (OSTI.GOV)

Canepa, Pieremanuele; Bo, Shou-Hang; Sai Gautam, Gopalakrishnan

Magnesium batteries appear a viable alternative to overcome the safety and energy density limitations faced by current lithium-ion technology. Furthermore, the development of a competitive magnesium battery is plagued by the existing notion of poor magnesium mobility in solids. We demonstrate by using ab initio calculations, nuclear magnetic resonance, and impedance spectroscopy measurements that substantial magnesium ion mobility can indeed be achieved in close-packed frameworks (~ 0.01-0.1 mS cm -1 at 298 K), specifically in the magnesium scandium selenide spinel. Our theoretical predictions also indicate that high magnesium ion mobility is possible in other chalcogenide spinels, opening the door formore » the realization of other magnesium solid ionic conductors and the eventual development of an all-solid-state magnesium battery.« less

Developing targets for radiation transport experiments at the Omega laser facility

DOE PAGES

Capelli, Deanna; Charsley-Groffman, C. A.; Randolph, Randall Blaine; ...

2017-07-13

Targets have been developed to measure supersonic radiation transport in aerogel foams using absorption spectroscopy. The target consists of an aerogel foam uniformly doped with either titanium or scandium inserted into an undoped aerogel foam package. This creates a localized doped foam region to provide spatial resolution for the measurement. Development and characterization of the foams is a key challenge in addition to machining and assembling the two foams so they mate without gaps. The foam package is inserted into a beryllium sleeve and mounted on a gold hohlraum. The target is mounted to a holder created using additive manufacturingmore » and mounted on a stalk. As a result, the manufacturing of the components, along with assembly and metrology of the target are described here.« less

Developing targets for radiation transport experiments at the Omega laser facility

DOE Office of Scientific and Technical Information (OSTI.GOV)

Capelli, Deanna; Charsley-Groffman, C. A.; Randolph, Randall Blaine

Targets have been developed to measure supersonic radiation transport in aerogel foams using absorption spectroscopy. The target consists of an aerogel foam uniformly doped with either titanium or scandium inserted into an undoped aerogel foam package. This creates a localized doped foam region to provide spatial resolution for the measurement. Development and characterization of the foams is a key challenge in addition to machining and assembling the two foams so they mate without gaps. The foam package is inserted into a beryllium sleeve and mounted on a gold hohlraum. The target is mounted to a holder created using additive manufacturingmore » and mounted on a stalk. As a result, the manufacturing of the components, along with assembly and metrology of the target are described here.« less

High magnesium mobility in ternary spinel chalcogenides

DOE PAGES

Canepa, Pieremanuele; Bo, Shou-Hang; Sai Gautam, Gopalakrishnan; ...

2017-11-24

Magnesium batteries appear a viable alternative to overcome the safety and energy density limitations faced by current lithium-ion technology. Furthermore, the development of a competitive magnesium battery is plagued by the existing notion of poor magnesium mobility in solids. We demonstrate by using ab initio calculations, nuclear magnetic resonance, and impedance spectroscopy measurements that substantial magnesium ion mobility can indeed be achieved in close-packed frameworks (~ 0.01-0.1 mS cm -1 at 298 K), specifically in the magnesium scandium selenide spinel. Our theoretical predictions also indicate that high magnesium ion mobility is possible in other chalcogenide spinels, opening the door formore » the realization of other magnesium solid ionic conductors and the eventual development of an all-solid-state magnesium battery.« less

(Pt{sub 1–x}Cu{sub x}){sub 3}Cu{sub 2}B and Pt{sub 9}Cu{sub 3}B{sub 5}, the first examples of copper platinum borides. Observation of superconductivity in a novel boron filled β-Mn-type compound

DOE Office of Scientific and Technical Information (OSTI.GOV)

Salamakha, Leonid P.; Sologub, Oksana, E-mail: oksana.sologub@univie.ac.at; Stöger, Berthold

New ternary copper platinum borides have been synthesized by arc melting of pure elements followed by annealing at 600 °C. The structures have been studied by X-ray single crystal and powder diffraction. (Pt{sub 1−x}Cu{sub x}){sub 3}Cu{sub 2}B (x=0.33) forms a B-filled β-Mn-type structure (space group P4{sub 1}32; a=0.6671(1) nm). Cu atoms are distributed preferentially on the 8c atom sites, whereas the 12d site is randomly occupied by Pt and Cu atoms (0.670(4) Pt±0.330(4) Cu). Boron is located in octahedral voids of the parent β-Mn-type structure. Pt{sub 9}Cu{sub 3}B{sub 5} (space group P-62m; a=0.9048(3) nm, c=0.2908(1) nm) adopts the Pt{sub 9}Zn{submore » 3}B{sub 5–δ}-type structure. It has a columnar architecture along the short translation vector exhibiting three kinds of [Pt{sub 6}] trigonal prism columns (boron filled, boron semi-filled and empty) and Pt channels with a pentagonal cross section filled with Cu atoms. The striking structural feature is a [Pt{sub 6}] cluster in form of an empty trigonal prism at the origin of the unit cell, which is surrounded by coupled [BPt{sub 6}] and [Pt{sub 6}] trigonal prisms, rotated perpendicularly to the central one. There is no B–B contact as well as Cu–B contact in the structure. The relationships of Pt{sub 9}Cu{sub 3}B{sub 5} structure with the structure of Ti{sub 1+x}Os{sub 2−x}RuB{sub 2} as well as with the structure families of metal sulfides and aluminides have been elucidated. (Pt{sub 1–x}Cu{sub x}){sub 3}Cu{sub 2}B (x=0.3) (B-filled β-Mn-type structure) is a bulk superconductor with a transition temperature of about 2.06 K and an upper critical field μ{sub 0}H{sub C2}(0){sup WHH} of 1.2 T, whereas no superconducting transition has been observed up to 0.3 K in Pt{sub 9}Cu{sub 3}B{sub 5} (Pt{sub 9}Zn{sub 3}B{sub 5–δ}-type structure) from electrical resistivity measurements. - Highlights: • First two copper platinum borides, (Pt{sub 0.67}Cu{sub 0.33}){sub 3}Cu{sub 2}B and Pt{sub 9}Cu{sub 3}B{sub 5} were obtained. • (Pt{sub 0.67}Cu{sub 0.33}){sub 3}Cu{sub 2}B forms a B-filled β-Mn-type structure. • Pt{sub 9}Cu{sub 3}B{sub 5} adopts a Pt{sub 9}Zn{sub 3}B{sub 5–δ}-type structure. • Boron atoms exhibit octahedral and trigonal prismatic coordination. • (Pt{sub 1–x}Cu{sub x})3Cu{sub 2}B (x=0.3) is a bulk superconductor with T{sub c} 2.06 K.« less

New high boron content polyborane precursors to advanced ceramic materials: New syntheses, new applications

NASA Astrophysics Data System (ADS)

Guron, Marta

There is a need for new synthetic routes to high boron content materials for applications as polymeric precursors to ceramics, as well as in neutron shielding and potential medical applications. To this end, new ruthenium-catalyzed olefin metathesis routes have been devised to form new complex polyboranes and polymeric species. Metathesis of di-alkenyl substituted o-carboranes allowed the synthesis of ring-closed products fused to the carborane cage, many of which are new compounds and one that offers a superior synthetic method to one previously published. Acyclic diene metathesis of di-alkenyl substituted m-carboranes resulted in the formation of new main-chain carborane-containing polymers of modest molecular weights. Due to their extremely low char yields, and in order to explore other metathesis routes, ring opening metathesis polymerization (ROMP) was used to generate the first examples of poly(norbornenyl- o-carboranes). Monomer synthesis was achieved via a two-step process, incorporating Ti-catalyzed hydroboration to make 6-(5-norbornenyl)-decaborane, followed by alkyne insertion in ionic liquid media to achieve 1,2-R2 -3-norbornenyl o-carborane species. The monomers were then polymerized using ROMP to afford several examples of poly(norbornenyl- o-carboranes) with relatively high molecular weights. One such polymer, [1-Ph, 3-(=CH2-C5H7-CH2=)-1,2-C 2B10H10]n, had a char yield very close to the theoretical char yield of 44%. Upon random copolymerization with poly(6-(5-norbornenyl) decaborane), char yields significantly increased to 80%, but this number was well above the theoretical value implicating the formation of a boron-carbide/carbon ceramic. Finally, applications of polyboranes were explored via polymer blends toward the synthesis of ceramic composites and the use of polymer precursors as reagents for potential ultra high temperature ceramic applications. Upon pyrolysis, polymer blends of poly(6-(5-norbornenyl)-decaborane) and poly(methylcarbosilane) converted into boron-carbide/silicon-carbide ceramics with high char yields. These polymer blends were also shown to be useful as reagents for synthesis of hafnium-boride/hafnium-carbide/silicon carbide and zirconium-boride/zirconium-carbide/silicon carbide composites.

New examples of ternary rare-earth metal boride carbides containing finite boron carbon chains: The crystal and electronic structure of RE15B6C20 (RE=Pr, Nd)

NASA Astrophysics Data System (ADS)

Babizhetskyy, Volodymyr; Mattausch, Hansjürgen; Simon, Arndt; Hiebl, Kurt; Ben Yahia, Mouna; Gautier, Régis; Halet, Jean-François

2008-08-01

The ternary rare-earth metal boride carbides RE15B6C20 (RE=Pr, Nd) were synthesized by co-melting the elements. They exist above 1270 K. Their crystal structures were determined from single-crystal X-ray diffraction data. Both crystallize in the space group P1¯, Z=1, a=8.3431(8) Å, b=9.2492(9) Å, c=8.3581(8) Å, α=84.72(1)°, β=89.68(1)°, γ =84.23(1)° (R1=0.041 (wR2=0.10) for 3291 reflections with Io>2σ(Io)) for Pr15B6C20, and a=8.284(1) Å, b=9.228(1) Å, c=8.309(1) Å, α=84.74(1)°, β=89.68(1)°, γ=84.17(2)° (R1=0.033 (wR2=0.049) for 2970 reflections with Io>2σ(Io)) for Nd15B6C20. Their structure consists of a three-dimensional framework of rare-earth metal atoms resulting from the stacking of slightly corrugated and distorted square nets, leading to cavities filled with unprecedented B2C4 finite chains, disordered C3 entities and isolated carbon atoms, respectively. Structural and theoretical analyses suggest the ionic formulation (RE3+)15([B2C4]6-)3([C3]4-)2(C4-)2·11ē. Accordingly, density functional theory calculations indicate that the compounds are metallic. Both structural arguments as well as energy calculations on different boron vs. carbon distributions in the B2C4 chains support the presence of a CBCCBC unit. Pr15B6C18 exhibits antiferromagnetic order at TN=7.9 K, followed by a meta-magnetic transition above a critical external field B>0.03 T. On the other hand, Nd15B6C18 is a ferromagnet below TC≈40 K.

High-Entropy Metal Diborides: A New Class of High-Entropy Materials and a New Type of Ultrahigh Temperature Ceramics

NASA Astrophysics Data System (ADS)

Gild, Joshua; Zhang, Yuanyao; Harrington, Tyler; Jiang, Sicong; Hu, Tao; Quinn, Matthew C.; Mellor, William M.; Zhou, Naixie; Vecchio, Kenneth; Luo, Jian

2016-11-01

Seven equimolar, five-component, metal diborides were fabricated via high-energy ball milling and spark plasma sintering. Six of them, including (Hf0.2Zr0.2Ta0.2Nb0.2Ti0.2)B2, (Hf0.2Zr0.2Ta0.2Mo0.2Ti0.2)B2, (Hf0.2Zr0.2Mo0.2Nb0.2Ti0.2)B2, (Hf0.2Mo0.2Ta0.2Nb0.2Ti0.2)B2, (Mo0.2Zr0.2Ta0.2Nb0.2Ti0.2)B2, and (Hf0.2Zr0.2Ta0.2Cr0.2Ti0.2)B2, possess virtually one solid-solution boride phase of the hexagonal AlB2 structure. Revised Hume-Rothery size-difference factors are used to rationalize the formation of high-entropy solid solutions in these metal diborides. Greater than 92% of the theoretical densities have been generally achieved with largely uniform compositions from nanoscale to microscale. Aberration-corrected scanning transmission electron microscopy (AC STEM), with high-angle annular dark-field and annular bright-field (HAADF and ABF) imaging and nanoscale compositional mapping, has been conducted to confirm the formation of 2-D high-entropy metal layers, separated by rigid 2-D boron nets, without any detectable layered segregation along the c-axis. These materials represent a new type of ultra-high temperature ceramics (UHTCs) as well as a new class of high-entropy materials, which not only exemplify the first high-entropy non-oxide ceramics (borides) fabricated but also possess a unique non-cubic (hexagonal) and layered (quasi-2D) high-entropy crystal structure that markedly differs from all those reported in prior studies. Initial property assessments show that both the hardness and the oxidation resistance of these high-entropy metal diborides are generally higher/better than the average performances of five individual metal diborides made by identical fabrication processing.

Nano-scale investigations of electric-dipole-layer enhanced field and thermionic emission from high current density cathodes

NASA Astrophysics Data System (ADS)

Vlahos, Vasilios

Cesium iodide coated graphitic fibers and scandate cathodes are two important electron emission technologies. The coated fibers are utilized as field emitters for high power microwave sources. The scandate cathodes are promising thermionic cathode materials for pulsed power vacuum electron devices. This work attempts to understand the fundamental physical and chemical relationships between the atomic structure of the emitting cathode surfaces and the superior emission characteristics of these cathodes. Ab initio computational modeling in conjunction with experimental investigations was performed on coated fiber cathodes to understand the origin of their very low turn on electric field, which can be reduced by as much as ten-fold compared to uncoated fibers. Copious amounts of cesium and oxygen were found co-localized on the fiber, but no iodine was detected on the surface. Additional ab initio studies confirmed that cesium oxide dimers could lower the work function significantly. Surface cesium oxide dipoles are therefore proposed as the source of the observed reduction in the turn on electric field. It is also proposed that emission may be further enhanced by secondary electrons from cesium oxide during operation. Thermal conditioning of the coated cathode may be a mechanism by which surface cesium iodide is converted into cesium oxide, promoting the depletion of iodine by formation of volatile gas. Ab initio modeling was also utilized to investigate the stability and work functions of scandate structures. The work demonstrated that monolayer barium-scandium-oxygen surface structures on tungsten can dramatically lower the work function of the underlying tungsten substrate from 4.6 eV down to 1.16 eV, by the formation of multiple surface dipoles. On the basis of this work, we conclude that high temperature kinetics force conventional dispenser cathodes (barium-oxygen monolayers on tungsten) to operate in a non-equilibrium compositional steady state with higher than optimal work functions of ˜2 eV. We hypothesize that scandium enables the barium-oxygen surface monolayer kinetics to access a more thermodynamically stable phase with reported work functions as low as ˜1.3 eV.

Effects of erbium-and chromium-doped yttrium scandium gallium garnet and diode lasers on the surfaces of restorative dental materials: a scanning electron microscope study.

PubMed

Hatipoglu, M; Barutcigil, C

2015-01-01

The aim of this study is to evaluate the potential effects of laser irradiation, which is commonly performed in periodontal surgery, on the surfaces of restorative materials. Five different restorative dental materials were used in this study, as follows: (1) Resin composite, (2) poly acid-modified resin composite (compomer), (3) conventional glass ionomer cement (GIC), (4) resin-modified glass ionomer cement (RMGIC), and (5) amalgam. Four cylindrical samples (8 mm diameter, 2 mm height) were prepared for each restorative material. In addition, four freshly extracted, sound human incisors teeth were selected. Two different laser systems commonly used in periodontal surgery were examined in this study: A 810 nm diode laser at a setting of 1 W with continuous-phase laser irradiation for 10 s, and an erbium-and chromium-doped yttrium scandium gallium garnet (Er, Cr: YSGG) laser at settings of 2.5 W, 3.25 W, and 4 W with 25 Hz laser irradiation for 10 s. Scanning electron microscopy (SEM) analysis was performed to evaluate the morphology and surface deformation of the restorative materials and tooth surfaces. According to the SEM images, the Er, Cr: YSGG laser causes irradiation markings that appear as demineralized surfaces on tooth samples. The Er, Cr: YSGG laser also caused deep defects on composite, compomer, and RMGIC surfaces because of its high power, and the ablation was deeper for these samples. High-magnification SEM images of GIC samples showed the melting and combustion effects of the Er, Cr: YSGG laser, which increased as the laser power was increased. In amalgam samples, neither laser left significant harmful effects at the lowest power setting. The diode laser did cause irradiation markings, but they were insignificant compared with those left by the Er, Cr: YSGG laser on the surfaces of the different materials and teeth. Within the limitations of this study, it can be concluded that Er, Cr: YSGG laser irradiation could cause distortions of the surfaces of restorative materials. Diode lasers can be preferred for periodontal surgery.

Carbon-Hydrogen Activation in Zerovalent Bis(1,5-cyclooctadiene) Complexes of the First Row Transition Metals: A Theoretical Study.

PubMed

Hu, Jia; Feng, Hao; Xie, Yaoming; King, R Bruce; Schaefer, Henry F

2018-03-29

Stepwise interaction of first row transition metal atoms with 1,5-cyclooctadiene to give (C 8 H 12 ) 2 M complexes is studied using the M06-L/DZP density functional method. The experimentally known (C 8 H 12 ) 2 Ni is the thermodynamically most favorable complex, with a predicted geometry consistent with its experimental structure as determined by X-ray crystallography. The other transition metal atoms from scandium to zinc also interact exothermically with 1,5-cyclooctadiene to give (C 8 H 12 ) 2 M derivatives, but these exhibit lower symmetry than the S 4 symmetry exhibited by (C 8 H 12 ) 2 Ni. Carbon-hydrogen activation of CH 2 groups in a C 8 H 12 ligand is predicted for most systems. Thus, conversion of (η 2,2 -C 8 H 12 ) 2 M to (η 3,2 -C 8 H 11 )(η 2,1 -C 8 H 13 )M, through a hydride intermediate (η 3,2 -C 8 H 11 )(η 2,2 -C 8 H 12 )MH, is predicted for scandium, vanadium, chromium, manganese, and cobalt. For titanium with a low-lying empty orbital, further C-H activation through a hydride intermediate (η 6 -C 8 H 10 )(η 2,1 -C 8 H 13 )TiH is predicted, leading ultimately to (η 6 -C 8 H 10 )(η 1,1 -C 8 H 14 )Ti, in which the hexahapto η 6 -C 8 H 10 ligand is shown by NICS to be aromatic. These two C-H activation processes on a titanium center represent the dehydrogenation of 1,5-cyclooctadiene to 1,3,5-cyclooctatriene with the second 1,5-cyclooctadiene ligand as the hydrogen acceptor. For zinc C-H activation terminates at (η 1 -C 8 H 11 )(C 8 H 12 )ZnH, which has a C-Zn-H three-center bond. No energetically favorable C-H activation processes are predicted for the iron, nickel, and copper (η 2,2 -C 8 H 12 ) 2 M derivatives.

The use of moments of momentum to account for crystal habits

NASA Technical Reports Server (NTRS)

Barber, P. G.

1985-01-01

A three-step theory of crystal growth is proposed which involves first an association of molecules or ions in solution to form an impinging growth unit, then second the orientation of this unit prior to its impact on the surface of a crystal, and finally the attachment of this unit to the crystal face. From this theory the habit of a crystal is dependent upon the moments of momentum of the impinging growth unit. The results of sample calculations are presented or sodium chloride, succinic acid, sucrose, and chromium boride. The faces predicted by this proposed theory are compared with those predicted by other, energy-based calculations and with those experimentally observed. The proposed theory suggests alternative strategies for crystallization and habit modification which may be of technological importance. Listings of the two computer programs that were used are provided.

Superconductivity between standard types: Multiband versus single-band materials

DOE Office of Scientific and Technical Information (OSTI.GOV)

Vagov, A.; Shanenko, A. A.; Milošević, M. V.

In the nearest vicinity of the critical temperature, types I and II of conventional single-band superconductors interchange at the Ginzburg-Landau parameter κ = 1/√2. At lower temperatures this point unfolds into a narrow but finite interval of κ’s, shaping an intertype (transitional) domain in the (κ,T ) plane. In the present work, based on the extended Ginzburg-Landau formalism, we show that the same picture of the two standard types with the transitional domain in between applies also to multiband superconductors. However, the intertype domain notably widens in the presence of multiple bands and can become extremely large when the systemmore » has a significant disparity between the band parameters. It is concluded that many multiband superconductors, such as recently discovered borides and iron-based materials, can belong to the intertype regime.« less

Liner for extrusion billet containers. Interim Technical Documentary Progress Report, February 1--April 30, 1963

DOE Office of Scientific and Technical Information (OSTI.GOV)

Spachner, S. A.

1963-05-01

A shrink-fit assembly device for buildup of ceramiccoated liner and sleeve assemblies was tested and modified to develop desired temperatures and suitable heat distribution in sleeves, which were heated. Nine different compositions of fiber metal reinforced ceramic compacts were produced for preliminary evaluation of suitability for extrusion liner use. Procedures were developed for welding short, hollow ceramic cylinders of high-strength metal carbides and borides to form a ceramic extrusion liner of suitable length. Dissassembly tooling for rapid separation of shrink-fitted sleeves from a worn liner was designed, fabricated, and tested. Preliminary extrusion testing of an alumina-coated liner was carried out,more » using SAE 4340 steel billets extruded to rod at 12 : 1 and 16 : 1 ratios. No coating wear was noted after extrusion of 3 billets. (auth)« less

Systematic investigation of structural, electronic, optical and thermal properties of ternary MoAlB; an ab initio approach

NASA Astrophysics Data System (ADS)

Rajpoot, Priyanka; Rastogi, Anugya; Verma, U. P.

2018-02-01

Structural, electronic, optical and thermal properties of molybdenum aluminum boride (MoAlB) have been analyzed systematically using the full potential linearized augmented plane wave method based on density functional theory at ambient condition as well as high pressure and high temperature. Density of states and band structure calculation reflect the metallic character of MoAlB. In addition to this, the electron charge density calculation reveals the strong covalent bonding, in between ‘B’ atoms as well as ‘Mo’ and ‘B’ atoms. Optical parameters exhibit anisotropic nature and MoAlB become transparent in ultraviolet region for the radiation of energy above 25 eV. The thermal properties were investigated by using the quasi-harmonic Debye model at high temperature and high pressure.

NASA research on refractory compounds.

NASA Technical Reports Server (NTRS)

Gangler, J. J.

1971-01-01

The behavior and properties of the refractory carbides, nitrides, and borides are being investigated by NASA as part of its research aimed at developing superior heat resistant materials for aerospace applications. Fundamental studies on the electronic and defect structures of the carbides indicate that there is promise for improving the strength and ductility of these materials. Studies of the zirconium-carbon-oxygen system show that zirconium oxycarbides of different compositions and lattice parameters can be formed between 1500 and 1900 C and are stable below 1500 C. More applied studies show that hot working generally improves the microstructure and therefore the strength of TiC and NbC. Sintering studies on UN indicate that very high densities can be achieved. Hot pressing of cermets of HfN and HfC produces good mechanical properties for high temperature bearing applications.

Formation of Minor Phases in a Nickel-Based Disk Superalloy

NASA Technical Reports Server (NTRS)

Gabb, T. P.; Garg, A.; Miller, D. R.; Sudbrack, C. K.; Hull, D. R.; Johnson, D.; Rogers, R. B.; Gayda, J.; Semiatin, S. L.

2012-01-01

The minor phases of powder metallurgy disk superalloy LSHR were studied. Samples were consistently heat treated at three different temperatures for long times to approximate equilibrium. Additional heat treatments were also performed for shorter times, to then assess non-equilibrium conditions. Minor phases including MC carbides, M23C6 carbides, M3B2 borides, and sigma were identified. Their transformation temperatures, lattice parameters, compositions, average sizes and total area fractions were determined, and compared to estimates of an existing phase prediction software package. Parameters measured at equilibrium sometimes agreed reasonably well with software model estimates, with potential for further improvements. Results for shorter times representing non-equilibrium indicated significant potential for further extension of the software to such conditions, which are more commonly observed during heat treatments and service at high temperatures for disk applications.

Development and Characterization of Titanium Compound N anostructures

NASA Astrophysics Data System (ADS)

Zhou, Zhou

The development and characterization of titanium compound nanostructures have been achieved, for potential applications in energy industry. Oil and gas, one of the traditional industry fields, observes accumulating demands on active implementations of nanotechnology, for the numerous advantages that nanomaterials can introduce to both product performances and field operations. By using chemical vapor deposition and liquid exfoliation, various titanium compound nanostructures have been synthesized through this project. Attractively, these two material fabrication methods have been recognized to be industrial friendly in terms of cost efficiency and productivity. The development of nanostructures, aiming at oil and gas field applications, presents novel solutions for existing issues, such as low durability of drilling tools, high friction in mechanical operations and ineffective heat dissipation. Titanium compound nanostructures, including titanium borides, nitrides and sulfides are therefore investigated for such applications as protective coating, lubrication and thermal management.

Sc2O@Cs(126339)-C92: Di-scandium oxide cluster encapsulated into a large fullerene cage

NASA Astrophysics Data System (ADS)

Gu, Yong-Xin; Li, Qiao-Zhi; Li, De-Huai; Zhao, Rui-Sheng; Zhao, Xiang

2018-04-01

The geometric, electronic structure and thermodynamic stability of Sc2O@C92 has been characterized by using hybrid density functional theory calculations combined with statistical thermodynamic analyses. Results indicate that the isolated pentagon rule (IPR) isomers Sc2O@Cs(126339)-C92, Sc2O@C1(126367)-C92 and Sc2O@C1(126390)-C92 are favorable. Noteworthy, it is the first time to declare that fullerene isomer Cs(126339)-C92 could be considered as the suitable cage to encapsulate metallic cluster. The electronic properties of these three isomers were performed with frontier molecular orbital (HOMO and LUMO) analyses and bond order calculations. Finally, 13C NMR and UV-vis-NIR spectra were simulated to provide valuable information for future experiments.

Experimental parameters optimization of instrumental neutron activation analysis in order to determine selected elements in some industrial soils in Turkey

NASA Astrophysics Data System (ADS)

Haciyakupoglu, Sevilay; Nur Esen, Ayse; Erenturk, Sema

2014-08-01

The purpose of this study is optimization of the experimental parameters for analysis of soil matrix by instrumental neutron activation analysis and quantitative determination of barium, cerium, lanthanum, rubidium, scandium and thorium in soil samples collected from industrialized urban areas near Istanbul. Samples were irradiated in TRIGA MARK II Research Reactor of Istanbul Technical University. Two types of reference materials were used to check the accuracy of the applied method. The achieved results were found to be in compliance with certified values of the reference materials. The calculated En numbers for mentioned elements were found to be less than 1. The presented data of element concentrations in soil samples will help to trace the pollution as an impact of urbanization and industrialization, as well as providing database for future studies.

Analysis of inorganic and organic constituents of myrrh resin by GC-MS and ICP-MS: An emphasis on medicinal assets.

PubMed

Ahamad, Syed Rizwan; Al-Ghadeer, Abdul Rahman; Ali, Raisuddin; Qamar, Wajhul; Aljarboa, Suliman

2017-07-01

The aim of the present investigation was to explore the constituents of the Arabian myrrh resin obtained from Commiphora myrrha. The organic and inorganic composition of the myrrh gum resin has been investigated using gas chromatography-mass spectrometry (GC-MS) and inductively coupled plasma-mass spectrometry (ICP-MS). Analysis executed by ICP-MS reveals the presence of various inorganic elements in significant amount in the myrrh resin. The elements that were found to be present in large amounts include calcium, magnesium, aluminum, phosphorus, chlorine, chromium, bromine and scandium. The important organic constituents identified in the myrrh ethanolic extract include limonene, curzerene, germacrene B, isocericenine, myrcenol, beta selinene, and spathulenol,. The present work complements other myrrh associated investigations done in the past and provides additional data for the future researches.

Pressure-Stabilized Cubic Perovskite Oxyhydride BaScO2H.

PubMed

Goto, Yoshihiro; Tassel, Cédric; Noda, Yasuto; Hernandez, Olivier; Pickard, Chris J; Green, Mark A; Sakaebe, Hikari; Taguchi, Noboru; Uchimoto, Yoshiharu; Kobayashi, Yoji; Kageyama, Hiroshi

2017-05-01

We report a scandium oxyhydride BaScO 2 H prepared by solid state reaction under high pressure. Rietveld refinements against powder synchrotron X-ray and neutron diffraction data revealed that BaScO 2 H adopts the ideal cubic perovskite structure (Pm3̅m), where oxide (O 2- ) and hydride (H - ) anions are disordered. 1 H nuclear magnetic resonance (NMR) spectroscopy provides a positive chemical shift of about +4.4 ppm, which can be understood by the distance to the nearest (and possibly the next nearest) cation from the H nucleus. A further analysis of the NMR data and calculations based on ab initio random structure searches suggest a partial cis preference in ScO 4 H 2 octahedra. The present oxyhydride, if compositionally or structurally tuned, may become a candidate for H - conductors.

Catalyst-Dependent Chemoselective Formal Insertion of Diazo Compounds into C-C or C-H Bonds of 1,3-Dicarbonyl Compounds.

PubMed

Liu, Zhaohong; Sivaguru, Paramasivam; Zanoni, Giuseppe; Anderson, Edward A; Bi, Xihe

2018-05-08

A catalyst-dependent chemoselective one-carbon insertion of diazo compounds into the C-C or C-H bonds of 1,3-dicarbonyl species is reported. In the presence of silver(I) triflate, diazo insertion into the C(=O)-C bond of the 1,3-dicarbonyl substrate leads to a 1,4-dicarbonyl product containing an all-carbon α-quaternary center. This reaction constitutes the first example of an insertion of diazo-derived carbenoids into acyclic C-C bonds. When instead scandium(III) triflate was applied as the catalyst, the reaction pathway switched to formal C-H insertion, affording 2-alkylated 1,3-dicarbonyl products. Different reaction pathways are proposed to account for this powerful catalyst-dependent chemoselectivity. © 2018 Wiley-VCH Verlag GmbH & Co. KGaA, Weinheim.

IUPAC-NIST Solubility Data Series. 100. Rare Earth Metal Fluorides in Water and Aqueous Systems. Part 1. Scandium Group (Sc, Y, La)

DOE Office of Scientific and Technical Information (OSTI.GOV)

Mioduski, Tomasz; Gumiński, Cezary, E-mail: cegie@chem.uw.edu.pl; Zeng, Dewen, E-mail: dewen-zeng@hotmail.com

2014-03-15

This work presents an assessment of solubility data for rare earth metal fluorides (generally of trivalent metals and of CeF{sub 4}) in water and in aqueous ternary systems. Compilations of all available experimental data are introduced for each rare earth metal fluoride with a corresponding critical evaluation. Every such evaluation contains a collection of all solubility results in water, a selection of suggested solubility data, and a brief discussion of the multicomponent systems. Because the ternary systems were seldom studied more than once, no critical evaluations of such data were possible. Only simple fluorides (no complexes or binary salts) aremore » treated as the input substances in this report. The literature has been covered through the end of 2013.« less

DOE Office of Scientific and Technical Information (OSTI.GOV)

Hazi, A

According to the results from a Livermore computer model, some of the small change jingling in your pocket contains zinc and copper created in massive gamma-ray bursts (GRBs) that rank as the most impressive light shows in the universe. Livermore astrophysicist Jason Pruet and his colleagues Rebecca Surman and Gail McLaughlin from North Carolina State University (NCSU) reported on their calculations in the February 20, 2004, issue of ''Astrophysical Journal Letters''. They found that GRBs from black holes surrounded by a disk of dense, hot plasma may have contributed heavily to the galactic inventory of elements such as calcium, scandium,more » titanium, zinc, and copper. ''A typical GRB of this kind briefly outshines all the stars in millions of galaxies combined'', says Pruet. ''Plus it makes about 100 times as much of some common elements as an ordinary supernova''.« less

Mixed-metal effects on ultra-incompressible metal diborides: Density functional computations

NASA Astrophysics Data System (ADS)

Lin, Fei; Wu, Kechen; He, Jiangang; Sa, Rongjian; Li, Qiaohong; Wei, Yongqin

2010-07-01

Mixed-metal borides are promising superhard materials (Kaner et al. (2005) [1]). In this Letter, density functional computations have been applied to the structural, electronic and elastic properties of mixed-metal diborides Re 0.5Ir 0.5B 2, Re 0.5Tc 0.5B 2, Os 0.5W 0.5B 2 and Os 0.5Ru 0.5B 2. The elastic moduli decrease from pure metal diboride ReB 2 to Re 0.5Ir 0.5B 2 and on the contrary increase from OsB 2 to Os 0.5W 0.5B 2 because boron-metal interactions are contaminated by the occupied anti-bonding orbitals. Alloying ReB 2 (OsB 2) with Tc (Ru) decreases the elastic moduli owing to the relativistic effects. Mixed-metal effects on elastic deformations focus on bonding strengths, which effectively tune the elastic properties of metal diborides.

Mechanical characteristics of heterogeneous structures obtained by high-temperature brazing of corrosion-resistant steels with rapidly quenched non-boron nickel-based alloys

NASA Astrophysics Data System (ADS)

Kalin, B.; Penyaz, M.; Ivannikov, A.; Sevryukov, O.; Bachurina, D.; Fedotov, I.; Voennov, A.; Abramov, E.

2018-01-01

Recently, the use rapidly quenched boron-containing nickel filler metals for high temperature brazing corrosion resistance steels different classes is perspective. The use of these alloys leads to the formation of a complex heterogeneous structure in the diffusion zone that contains separations of intermediate phases such as silicides and borides. This structure negatively affects the strength characteristics of the joint, especially under dynamic loads and in corrosive environment. The use of non-boron filler metals based on the Ni-Si-Be system is proposed to eliminate this structure in the brazed seam. Widely used austenitic 12Cr18Ni10Ti and ferrite-martensitic 16Cr12MoSiWNiVNb reactor steels were selected for research and brazing was carried out. The mechanical characteristics of brazed joints were determined using uniaxial tensile and impact toughness tests, and fractography was investigated by electron microscopy.

Structure and properties of Hardox 450 steel with arc welded coatings

NASA Astrophysics Data System (ADS)

Ivanov, Yu. F.; Konovalov, S. V.; Kormyshev, V. E.; Gromov, V. E.; Teresov, A. D.; Semina, O. A.

2017-12-01

The paper reports on a study of the surface structure, phase composition, and microhardness of Hardox 450 steel with coatings deposited by arc welding of powder wires differing in chemical composition. The study shows that to a depth of 6-8 mm, the microhardness of the thus formed coatings is more than two times the microhardness of the base metal and that their higher mechanical properties are provided by martensite structure containing Nb2C and NbC carbides and Fe2B borides as eutectic lamellae with a transverse size of 30-70 nm; their volume reveals a net-like dislocation substructure with a scalar dislocation density of 1011 cm-2. The highest surface hardness is found for the steel coated with boron-containing wire material. Some ideas are suggested on possible mechanisms and temperature for the formation of Nb and B carbides during the process.

Impact of B 4C co-sputtering on structure and optical performance of Cr/Sc multilayer X-ray mirrors

DOE PAGES

Ghafoor, Naureen; Eriksson, Fredrik; Aquila, Andrew; ...

2017-01-01

We investigate the influence of B 4C incorporation during magnetron sputter deposition of Cr/Sc multilayers intended for soft X-ray reflective optics. Chemical analysis suggests formation of metal: boride and carbide bonds which stabilize an amorphous layer structure, resulting in smoother interfaces and an increased reflectivity. A near-normal incidence reflectivity of 11.7%, corresponding to a 67% increase, is achieved at λ = 3.11 nm upon adding 23 at.% (B + C). The advantage is significant for the multilayer periods larger than 1.8 nm, where amorphization results in smaller interface widths, for example, giving 36% reflectance and 99.89% degree of polarization nearmore » Brewster angle for a multilayer polarizer. The modulated ion-energy-assistance during the growth is considered vital to avoid intermixing during the interface formation even when B + C are added.« less

Review of Thermal Spray Coating Applications in the Steel Industry: Part 2—Zinc Pot Hardware in the Continuous Galvanizing Line

NASA Astrophysics Data System (ADS)

Matthews, S.; James, B.

2010-12-01

This two-part article series reviews the application of thermal spray coating technology in the production of steel and steel sheet products. Part 2 of this article series is dedicated to coating solutions in the continuous galvanizing line. The corrosion mechanisms of Fe- and Co-based bulk materials are briefly reviewed as a basis for the development of thermal spray coating solutions. WC-Co thermal spray coatings are commonly applied to low Al-content galvanizing hardware due to their superior corrosion resistance compared to Fe and Co alloys. The effect of phase degradation, carbon content, and WC grain size are discussed. At high Al concentrations, the properties of WC-Co coatings degrade significantly, leading to the application of oxide-based coatings and corrosion-resistant boride containing coatings. The latest results of testing are summarized, highlighting the critical coating parameters.

Microstructural observations in rapidly-solidified and heat-treated Ni3Al-Cr alloys

DOE Office of Scientific and Technical Information (OSTI.GOV)

Carro, G.; Flanagan, W.F.

1992-08-01

The microstructural development following heat treatments of several rapidly-solidified Ni3Al-Cr and Ni3Al-Cr-B alloys is presented. Depending on composition, the as-solidified samples were either 100 percent gamma-prime phase - in the form of fine antiphase domains (APD) - or a mixture of gamma-prime (APDs) and beta phases. Upon annealing, the as-solidified microstructures transform to either APD-free gamma-prime or mixtures of gamma and gamma-prime phases. For those compositions where the quenched microstructures were 100 percent gamma-prime it was observed that APD coarsening followed conventional grain-growth kinetics, but when gamma phase precipitated on the APD boundaries the rate constant changed abruptly while themore » time exponent remained unaffected. It was also found that alloys containing critical amounts of chromium and boron are susceptible to precipitation of the boride Cr5B3. 14 refs.« less

Microstructural observations in rapidly-solidified and heat-treated Ni sub 3 Al-Cr alloys

DOE Office of Scientific and Technical Information (OSTI.GOV)

Carro, G.; Flanagan, W.F.

1992-01-01

In this paper , the microstructural development following heat treatments of several rapidly-solidified Ni{sub 3}Al-Cr and Ni{sub 3}Al-Cr-B alloys is presented. Depending on composition, the as-solidified samples were either 100% {gamma} phase-in the form of fine anti-phase domains (APD)-or a mixture of {gamma} (APDs) and {beta} phases. Upon annealing, the as-solidified microstructures transform to either APD-free {gamma}or mixtures of {gamma}and {gamma}{prime} phases. For those compositions where the quenched microstructures were 100{gamma}{prime} it was observed that APD coarsening followed conventional grain-growth kinetics, but when {gamma} phase precipitated on the APD boundaries the rate constant changed abruptly while the time exponent remainedmore » unaffected. It was also found that alloys containing critical amounts of chromium and boron are susceptible to precipitation of the boride Cr{sub 5}B{sub 3}.« less

Microstructural observations in rapidly-solidified and heat-treated Ni3Al-Cr alloys

NASA Technical Reports Server (NTRS)

Carro, G.; Flanagan, W. F.

1992-01-01

The microstructural development following heat treatments of several rapidly-solidified Ni3Al-Cr and Ni3Al-Cr-B alloys is presented. Depending on composition, the as-solidified samples were either 100 percent gamma-prime phase - in the form of fine antiphase domains (APD) - or a mixture of gamma-prime (APDs) and beta phases. Upon annealing, the as-solidified microstructures transform to either APD-free gamma-prime or mixtures of gamma and gamma-prime phases. For those compositions where the quenched microstructures were 100 percent gamma-prime it was observed that APD coarsening followed conventional grain-growth kinetics, but when gamma phase precipitated on the APD boundaries the rate constant changed abruptly while the time exponent remained unaffected. It was also found that alloys containing critical amounts of chromium and boron are susceptible to precipitation of the boride Cr5B3.

Effects of cobalt on the microstructure of Udimet 700. M.S. Thesis Final Report

NASA Technical Reports Server (NTRS)

Engel, M. A.

1982-01-01

Cobalt, a critical and "strategic" alloying element in many superalloys, was systematically substituted by nickel in experimental alloys Udimet 700 containing 0.1, 4.3, 8.6, 12.8 and the standard 17.0 wt.% cobalt. Electrolytic and chemical extraction techniques, X-ray diffraction, scanning electron and optical microscopy were used for the microstructural studies. The total weight fraction of gamma' was not significantly affected by the cobalt content, although a difference in the size and quantities of the primary and secondary gamma' phases was apparent. The lattice parameters of the gamma' were found to increase with increasing cobalt content while the lattice mismatch between the gamma matrix and gamma' phases decreased. Other significant effects of cobalt on the weight fraction, distribution and formation of the carbide and boride phases as well as the relative stability of the experimental alloys during long-time aging are also discussed.

Impact of B 4C co-sputtering on structure and optical performance of Cr/Sc multilayer X-ray mirrors

DOE Office of Scientific and Technical Information (OSTI.GOV)

Ghafoor, Naureen; Eriksson, Fredrik; Aquila, Andrew

We investigate the influence of B 4C incorporation during magnetron sputter deposition of Cr/Sc multilayers intended for soft X-ray reflective optics. Chemical analysis suggests formation of metal: boride and carbide bonds which stabilize an amorphous layer structure, resulting in smoother interfaces and an increased reflectivity. A near-normal incidence reflectivity of 11.7%, corresponding to a 67% increase, is achieved at λ = 3.11 nm upon adding 23 at.% (B + C). The advantage is significant for the multilayer periods larger than 1.8 nm, where amorphization results in smaller interface widths, for example, giving 36% reflectance and 99.89% degree of polarization nearmore » Brewster angle for a multilayer polarizer. The modulated ion-energy-assistance during the growth is considered vital to avoid intermixing during the interface formation even when B + C are added.« less

Energy conversion device and method of reducing friction therein

DOEpatents

Solovyeva, Lyudmila Mikhaylovna; Jansson, Kyle S; Elmoursi, Alaa AbdelAzim; Zhu, Dong; Milner, Robert; Daughterty, Early Eugene; Higdon, Clifton Baxter; Elagamy, Kamel Abdel-Khalik; Hicks, Aaron Michael

2013-10-08

A device configured for converting energy includes a first surface, a second surface configured for moving with respect to the first surface during operation of the device, and a coating disposed on at least one of the first surface and the second surface. The coating includes a first layer of a ceramic alloy represented by the general formula AlMgB.sub.14--X, wherein X is present in an amount of from 0 to 70 parts by weight based on 100 parts by weight of the ceramic alloy and is a doping agent selected from the group of Group IV elements and borides and nitrides thereof, and a second layer disposed on the first layer and including carbon in a gradient concentration. The coating has a hardness of from 10 to 20 GPa and a coefficient of friction of less than or equal to 0.12.

Wet-chemical synthesis of nanoscale iron boride, XAFS analysis and crystallisation to α-FeB.

PubMed

Rades, Steffi; Kornowski, Andreas; Weller, Horst; Albert, Barbara

2011-06-20

The reaction of lithium tetrahydridoborate and iron bromide in high boiling ether as reaction medium produces an ultrafine, pyrophoric and magnetic precipitate. X-ray and electron diffraction proved the product to be amorphous. According to X-ray absorption fine structure spectroscopy (XAFS) the precipitate has FeB structure up to nearly two coordination spheres around an iron absorber atom. Transmission electron microscopy (TEM) confirms the ultrafine powder to be nanoscale. Subsequent annealing at 450 °C causes the atoms to arrange in a more distinct FeB structure, and further thermal treatment to 1050 °C extends the local structure to the α-modification of FeB. Between 1050 °C and 1500 °C α-FeB is transformed into β-FeB. Copyright © 2011 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Effect of Laser Power on Metallurgical, Mechanical and Tribological Characteristics of Hardfaced Surfaces of Nickel-Based Alloy

NASA Astrophysics Data System (ADS)

Gnanasekaran, S.; Padmanaban, G.; Balasubramanian, V.

2017-12-01

In this present work, nickel based alloy was deposited on 316 LN austenitic stainless steel (ASS) by a laser hardfacing technique to investigate the influence of laser power on macrostructure, microstructure, microhardness, dilution and wear characteristics. The laser power varied from 1.1 to 1.9 kW. The phase constitution, microstructure and microhardness were examined by optical microscope, scanning electron microscopy, energy dispersion spectroscopy and Vickers microhardness tester. The wear characteristics of the hardfaced surfaces and substrate were evaluated at room temperature (RT) under dry sliding wear condition (pin-on-disc). The outcome demonstrates that as the laser power increases, dilution increases and hardness of the deposit decreases. This is because excess heat melts more volume of substrate material and increases the dilution; subsequently it decreases the hardness of the deposit. The microstructure of the deposit is characterized by Ni-rich carbide, boride and silicide.

Techniques for increasing boron fiber fracture strain

NASA Technical Reports Server (NTRS)

Dicarlo, J. A.

1977-01-01

Improvement in the strain-to-failure of CVD boron fibers is shown possible by contracting the tungsten boride core region and its inherent flaws. The results of three methods are presented in which etching and thermal processing techniques were employed to achieve core flaw contraction by internal stresses available in the boron sheath. After commercially and treatment induced surface flaws were removed from 203 micrometers (8 mil) fibers, the core flaw was observed to be essentially the only source of fiber fracture. Thus, fiber strain-to-failure was found to improve by an amount equal to the treatment induced contraction on the core flaw. Commercial feasibility considerations suggest as the most cost effective technique that method in which as-produced fibers are given a rapid heat treatment above 700 C. Preliminary results concerning the contraction kinetics and fracture behavior observed are presented and discussed both for high vacuum and argon gas heat treatment environments.

Refractory materials for high-temperature thermoelectric energy conversion

NASA Technical Reports Server (NTRS)

Wood, C.; Emin, D.

1983-01-01

Theoretical work of two decades ago adequately explained the transport behavior and effectively guided the development of thermoelectric materials of high conversion efficiencies of conventional semiconductors (e.g., SiGe alloys). The more significant contributions involved the estimation of optimum doping concentrations, the reduction of thermal conductivity by solid solution doping and the development of a variety of materials with ZT approx. 1 in the temperature range 300 K to 1200 K. ZT approx. 1 is not a theoretical limitation although, experimentally, values in excess of one were not achieved. Work has continued with emphasis on higher temperature energy conversion. A number of promising materials have been discovered in which it appears that ZT 1 is realizable. These materials are divided into two classes: (1) the rare-earth chalcogenides which behave as itinerant highly-degenerate n-type semiconductors at room-temperature, and (2) the boron-rich borides, which exhibit p-type small-polaronic hopping conductivity.

The microstructure and properties of rapidly solidified, dispersion-strengthened NiAl

NASA Technical Reports Server (NTRS)

Jha, S. C.; Ray, R.

1990-01-01

An advanced rapid solidification technology for processing reactive and refractory alloys, utilized to produce large quantities of melt-spun filaments of NiAl, is presented. The melt-spun filaments are pulverized to fine particle sizes, and subsequently consolidated by hot extrusion or hot isostatic pressing. Rapid solidification process gives rise to very fine-grained microstructures. However, exposure to elevated temperature during hot consolidation leads to grain growth. Alloying agents such as borides, carbides, and tungsten can pin the grain boundaries and retard the grain growth. Various alloy compositions are investigated. The eventual goal is to utilize the hot-extruded and forged stock to grow single-crystal NiAl blades for advanced gas-turbine engine applications. Single-crystal NiAl, containing a uniform dispersion of carbide strengthening precipitates, is expected to lead to highly creep-resistant turbine blades, and is of considerable interest to the aerospace propulsion industry.

Fracture Strength of AlLiB14

NASA Astrophysics Data System (ADS)

Wan, L. F.; Beckman, S. P.

2012-10-01

The orthorhombic boride crystal family XYB14, where X and Y are metal atoms, plays a critical role in a unique class of superhard compounds, yet there have been no studies aimed at understanding the origin of the mechanical strength of this compound. We present here the results from a comprehensive investigation into the fracture strength of the archetypal AlLiB14 crystal. First principles, ab initio, methods are used to determine the ideal brittle cleavage strength for several high-symmetry orientations. The elastic tensor and the orientation-dependent Young’s modulus are calculated. From these results the lower bound fracture strength of AlLiB14 is predicted to be between 29 and 31 GPa, which is near the measured hardness reported in the literature. These results indicate that the intrinsic strength of AlLiB14 is limited by the interatomic B-B bonds that span between the B layers.

Direct solar-pumped iodine laser amplifier

NASA Technical Reports Server (NTRS)

Han, Kwang S.; Kim, K. H.; Stock, L. V.

1987-01-01

The improvement on the collection system of the Tarmarack Solar Simulator beam was attemped. The basic study of evaluating the solid state laser materials for the solar pumping and also the work to construct a kinetic model algorithm for the flashlamp pumped iodine lasers were carried out. It was observed that the collector cone worked better than the lens assembly in order to collect the solar simulator beam and to focus it down to a strong power density. The study on the various laser materials and their lasing characteristics shows that the neodymium and chromium co-doped gadolinium scandium gallium garnet (Nr:Cr:GSGG) may be a strong candidate for the high power solar pumped solid state laser crystal. On the other hand the improved kinetic modeling for the flashlamp pumped iodine laser provides a good agreement between the theoretical model and the experimental data on the laser power output, and predicts the output parameters of a solar pumped iodine laser.

Development of a fluorescent chelating ligand for scandium ion having a Schiff base moiety

NASA Astrophysics Data System (ADS)

Yamada, Hiroshi; Kojo, Masahito; Nakahara, Tomomi; Murakami, Kumi; Kakima, Takashi; Ichiba, Hideaki; Yajima, Takehiko; Fukushima, Takeshi

2012-05-01

A fluorescent ligand, 1-(2-hydroxy-3-methoxybenzaldehyde)-4-aminosalicylhydrazone (HMB-ASH), was newly designed and synthesized, and its fluorescence characteristics for metal ions were investigated in the pH range 3.0-10.5 (at a difference of 0.5 for each metal). After testing 31 different metal ions, it was found that HMB-ASH was able to emit fluorescence intensely at 512 nm with an excitation wavelength of 353 nm in the presence of Sc3+, one of the rare earth metals, at pH values around 3.5 and 8.0. The other metal ions hardly showed fluorescence with HMB-ASH. The fluorescence was more intense at pH 8.0, and the detection limit of Sc3+ in a buffer solution (pH 8.0) was approximately 18.8 nmol L-1 (0.85 ppb).

Experimental Study of Codeposition Electrochemistry Using Mixtures of ScCl 3 and YCl 3 in LiCl-KCl Eutectic Salt at 500°C

DOE Office of Scientific and Technical Information (OSTI.GOV)

Shaltry, Michael R.; Yoo, Tae-Sic; Fredrickson, Guy L.

2017-09-12

Cyclic voltammetry and chronopotentiometry tests were applied to molten LiCl-KCl eutectic at 500 °C including amounts of ScCl 3 and YCl 3. The purpose of the testing was to observe the effect of applied electrical current on the codeposition of scandium and yttrium, which were chosen as surrogate elements for uranium and plutonium, respectively. Features of the work were to vary the concentration of ScCl 3 (at relatively low concentrations) as well as varying the applied current, all with a fixed concentration of YCl 3. Results of the experiments could provide insight of uranium electrorefining and may provide evidence, whichmore » suggests the electrorefiner could be operated at lower UCl 3 concentration whereby codeposition (U and Pu) could be more effectively controlled.« less

Terbium Radionuclides for Theranostics Applications: A Focus On MEDICIS-PROMED

NASA Astrophysics Data System (ADS)

Cavaier, R. Formento; Haddad, F.; Sounalet, T.; Stora, T.; Zahi, I.

A new facility, named CERN-MEDICIS, is under construction at CERN to produce radionuclides for medical applications. In parallel, the MEDICIS-PROMED, a Marie Sklodowska-Curie innovative training network of the Horizon 2020 European Commission's program, is being coordinated by CERN to train young scientists on the production and use of innovative radionuclides and develop a network of experts within Europe. One program within MEDICIS-PROMED is to determine the feasibility of producing innovative radioisotopes for theranostics using a commercial middle-sized high-current cyclotron and the mass separation technology developed at CERN-MEDICIS. This will allow the production of high specific activity radioisotopes not achievable with the common post-processing by chemical separation. Radioisotopes of scandium, copper, arsenic and terbium have been identified. Preliminary studies of activation yield and irradiation parameters optimization for the production of Tb-149 will be described.

Experimental partitioning of rare earth elements and scandium among armalcolite, ilmenite, olivine and mare basalt liquid

NASA Technical Reports Server (NTRS)

Irving, A. J.; Merrill, R. B.; Singleton, D. E.

1978-01-01

An experimental study was carried out to measure partition coefficients for two rare-earth elements (Sm and Tm) and Sc among armalcolite, ilmenite, olivine and liquid coexisting in a system modeled on high-Ti mare basalt 74275. This 'primitive' sample was chosen for study because its major and trace element chemistry as well as its equilibrium phase relations at atmospheric pressure are known from previous studies. Beta-track analytical techniques were used so that partition coefficients could be measured in an environment whose bulk trace element composition is similar to that of the natural basalt. Partition coefficients for Cr and Mn were determined in the same experiments by microprobe analysis. The only equilibrium partial melting model appears to be one in which ilmenite is initially present in the source region but is consumed by melting before segregation of the high-Ti mare basalt liquid from the residue.

Sustainability of rare earth elements chain: from production to food - a review.

PubMed

Turra, Christian

2018-02-01

Rare earth elements (REE) are a group of chemical elements that include lanthanoids (lanthanum to lutetium), scandium and yttrium. In the last decades, the REE demand in the industry and other areas has increased significantly. In general, REE have shown low concentrations in soils, plants, water and atmosphere, but they may accumulate in such environments due to anthropogenic inputs. In areas where there is REE contamination, the slow accumulation of these elements in the environment could become problematic. Many studies have shown environmental areas contaminated with REE and their toxic effects. Thus, it is important to review, in order to improve the current understanding of these elements in the environment, showing the effects of REE exposure in mining, soil, water, plants and food. Besides, there are few suppliers and a limited quantity of these elements in the world. This paper suggests options to improve the sustainability management of REE chain.

Soft X-ray imaging of thick carbon-based materials using the normal incidence multilayer optics.

PubMed

Artyukov, I A; Feschenko, R M; Vinogradov, A V; Bugayev, Ye A; Devizenko, O Y; Kondratenko, V V; Kasyanov, Yu S; Hatano, T; Yamamoto, M; Saveliev, S V

2010-10-01

The high transparency of carbon-containing materials in the spectral region of "carbon window" (lambda approximately 4.5-5nm) introduces new opportunities for various soft X-ray microscopy applications. The development of efficient multilayer coated X-ray optics operating at the wavelengths of about 4.5nm has stimulated a series of our imaging experiments to study thick biological and synthetic objects. Our experimental set-up consisted of a laser plasma X-ray source generated with the 2nd harmonics of Nd-glass laser, scandium-based thin-film filters, Co/C multilayer mirror and X-ray film UF-4. All soft X-ray images were produced with a single nanosecond exposure and demonstrated appropriate absorption contrast and detector-limited spatial resolution. A special attention was paid to the 3D imaging of thick low-density foam materials to be used in design of laser fusion targets.

Low work function materials for microminiature energy conversion and recovery applications

DOEpatents

Zavadil, Kevin R.; Ruffner, Judith A.; King, Donald B.

2003-05-13

Low work function materials are disclosed together with methods for their manufacture and integration with electrodes used in thermionic conversion applications (specifically microminiature thermionic conversion applications). The materials include a mixed oxide system and metal in a compositionally modulated structure comprised of localized discontinuous structures of material that are deposited using techniques suited to IC manufacture, such as rf sputtering or CVD. The structures, which can include layers are then heated to coalescence yielding a thin film that is both durable and capable of electron emission under thermionic conversion conditions used for microminiature thermionic converters. Using the principles of the invention, thin film electrodes (emitters and collectors) required for microconverter technology are manufactured using a single process deposition so as to allow for full fabrication integration consistent with batch processing, and tailoring of emission/collection properties. In the preferred embodiment, the individual layers include mixed BaSrCaO, scandium oxide and tungsten.

Tritium target manufacturing for use in accelerators

NASA Astrophysics Data System (ADS)

Bach, P.; Monnin, C.; Van Rompay, M.; Ballanger, A.

2001-07-01

As a neutron tube manufacturer, SODERN is now in charge of manufacturing tritium targets for accelerators, in cooperation with CEA/DAM/DTMN in Valduc. Specific deuterium and tritium targets are manufactured on request, according to the requirements of the users, starting from titanium target on copper substrate, and going to more sophisticated devices. A wide range of possible uses is covered, including thin targets for neutron calibration, thick targets with controlled loading of deuterium and tritium, rotating targets for higher lifetimes, or large size rotating targets for accelerators used in boron neutron therapy. Activity of targets lies in the 1 to 1000 Curie, diameter of targets being up to 30 cm. Special targets are also considered, including surface layer targets for lowering tritium desorption under irradiation, or those made from different kinds of occluders such as titanium, zirconium, erbium, scandium, with different substrates. It is then possible to optimize either neutron output, or lifetime and stability, or thermal behavior.

High-temperature deformation and microstructural analysis for silicon nitride-scandium(III) oxide

NASA Technical Reports Server (NTRS)

Cheong, Deock-Soo; Sanders, William A.

1992-01-01

It was indicated that Si3N4 doped with Sc2O3 may exhibit high temperature mechanical properties superior to Si3N4 systems with various other oxide sintered additives. High temperature deformation of samples was studied by characterizing the microstructures before and after deformation. It was found that elements of the additive, such as Sc and O, exist in small amounts at very thin grain boundary layers and most of them stay in secondary phases at tripple and multiple grain boundary junctions. These secondary phases are devitrified as crystalline Sc2Si2O7. Deformation of the samples was dominated by cavitational processes rather than movements of dislocations. Thus the excellent deformation resistance of the samples at high temperature can be attributed to the very small thickness of the grain boundary layers and the crystalline secondary phase.

A nanospherical ordered mesoporous Lewis acid polymer for the direct glycosylation of unprotected and unactivated sugars in water.

PubMed

Zhang, Fang; Liang, Chao; Wu, Xiaotao; Li, Hexing

2014-08-04

The design of robust solid catalysts which can selectively synthesize highly functionalized carbohydrate derivatives from unprotected and unactivated simple sugars in water is an outstanding challenge. Herein we describe the preparation of a novel nanospherical ordered mesoporous Lewis acid polymer (Sc(OTf)2-NSMP) by functionalizing the mesoporous phenol-formaldehyde polymer framework with scandium triflate groups. In the C-glycosylation reaction between D-glucose and dimedone with the Sc(OTf)2-NSMP catalyst, the conversion was 99% and the yield of xanthone-C-glucoside reached 92% after 2 days, which exceeded the previous best results. It was shown that other xanthone glycosides can be obtained from various sugars with moderate to good yields. Furthermore, the catalyst can be easily recovered and reused at least seven times without loss of catalytic activity. © 2014 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Point Defects and p -Type Doping in ScN from First Principles

NASA Astrophysics Data System (ADS)

Kumagai, Yu; Tsunoda, Naoki; Oba, Fumiyasu

2018-03-01

Scandium nitride (ScN) has been intensively researched as a prototype of rocksalt nitrides and a potential counterpart of the wurtzite group IIIa nitrides. It also holds great promise for applications in various fields, including optoelectronics, thermoelectrics, spintronics, and piezoelectrics. We theoretically investigate the bulk properties, band-edge positions, chemical stability, and point defects, i.e., native defects, unintentionally doped impurities, and p -type dopants of ScN using the Heyd-Scuseria-Ernzerhof hybrid functional. We find several fascinating behaviors: (i) a high level for the valence-band maximum, (ii) the lowest formation energy among binary nitrides, (iii) high formation energies of native point defects, (iv) low formation energies of donor-type impurities, and (v) a p -type conversion by Mg doping. Furthermore, we uncover the origins of the Burstein-Moss shift commonly observed in ScN. Our work sheds light on a fundamental understanding of ScN in regard to its technological applications.

Sc(2)MgGa(2) and Y(2)MgGa(2).

PubMed

Sahlberg, Martin; Andersson, Yvonne

2009-03-01

Scandium magnesium gallide, Sc(2)MgGa(2), and yttrium magnesium gallide, Y(2)MgGa(2), were synthesized from the corresponding elements by heating under an argon atmosphere in an induction furnace. These intermetallic compounds crystallize in the tetragonal Mo(2)FeB(2)-type structure. All three crystallographically unique atoms occupy special positions and the site symmetries of (Sc/Y, Ga) and Mg are m2m and 4/m, respectively. The coordinations around Sc/Y, Mg and Ga are pentagonal (Sc/Y), tetragonal (Mg) and triangular (Ga) prisms, with four (Mg) or three (Ga) additional capping atoms leading to the coordination numbers [10], [8+4] and [6+3], respectively. The crystal structure of Sc(2)MgGa(2 )was determined from single-crystal diffraction intensities and the isostructural Y(2)MgGa(2) was identified from powder diffraction data.

Metal halide arc discharge lamp having short arc length

NASA Technical Reports Server (NTRS)

Muzeroll, Martin E. (Inventor)

1994-01-01

A metal halide arc discharge lamp includes a sealed light-transmissive outer jacket, a light-transmissive shroud located within the outer jacket and an arc tube assembly located within the shroud. The arc tube assembly includes an arc tube, electrodes mounted within the arc tube and a fill material for supporting an arc discharge. The electrodes have a spacing such that an electric field in a range of about 60 to 95 volts per centimeter is established between the electrodes. The diameter of the arc tube and the spacing of the electrodes are selected to provide an arc having an arc diameter to arc length ratio in a range of about 1.6 to 1.8. The fill material includes mercury, sodium iodide, scandium tri-iodide and a rare gas, and may include lithium iodide. The lamp exhibits a high color rendering index, high lumen output and high color temperature.

Scandium(III) catalysis of transimination reactions. Independent and constitutionally coupled reversible processes.

PubMed

Giuseppone, Nicolas; Schmitt, Jean-Louis; Schwartz, Evan; Lehn, Jean-Marie

2005-04-20

Sc(OTf)(3) efficiently catalyzes the self-sufficient transimination reaction between various types of C=N bonds in organic solvents, with turnover frequencies up to 3600 h(-)(1) and rate accelerations up to 6 x 10(5). The mechanism of the crossover reaction in mixtures of amines and imines is studied, comparing parallel individual reactions with coupled equilibria. The intrinsic kinetic parameters for isolated reactions cannot simply be added up when several components are mixed, and the behavior of the system agrees with the presence of a unique mediator that constitutes the core of a network of competing reactions. In mixed systems, every single amine or imine competes for the same central hub, in accordance with their binding affinity for the catalyst metal ion center. More generally, the study extends the basic principles of constitutional dynamic chemistry to interconnected chemical transformations and provides a step toward dynamic systems of increasing complexity.

(Pt1-xCux)3Cu2B and Pt9Cu3B5, the first examples of copper platinum borides. Observation of superconductivity in a novel boron filled β-Mn-type compound

NASA Astrophysics Data System (ADS)

Salamakha, Leonid P.; Sologub, Oksana; Stöger, Berthold; Michor, Herwig; Bauer, Ernst; Rogl, Peter F.

2015-09-01

New ternary copper platinum borides have been synthesized by arc melting of pure elements followed by annealing at 600 °C. The structures have been studied by X-ray single crystal and powder diffraction. (Pt1-xCux)3Cu2B (x=0.33) forms a B-filled β-Mn-type structure (space group P4132; a=0.6671(1) nm). Cu atoms are distributed preferentially on the 8c atom sites, whereas the 12d site is randomly occupied by Pt and Cu atoms (0.670(4) Pt±0.330(4) Cu). Boron is located in octahedral voids of the parent β-Mn-type structure. Pt9Cu3B5 (space group P-62m; a=0.9048(3) nm, c=0.2908(1) nm) adopts the Pt9Zn3B5-δ-type structure. It has a columnar architecture along the short translation vector exhibiting three kinds of [Pt6] trigonal prism columns (boron filled, boron semi-filled and empty) and Pt channels with a pentagonal cross section filled with Cu atoms. The striking structural feature is a [Pt6] cluster in form of an empty trigonal prism at the origin of the unit cell, which is surrounded by coupled [BPt6] and [Pt6] trigonal prisms, rotated perpendicularly to the central one. There is no B-B contact as well as Cu-B contact in the structure. The relationships of Pt9Cu3B5 structure with the structure of Ti1+xOs2-xRuB2 as well as with the structure families of metal sulfides and aluminides have been elucidated. (Pt1-xCux)3Cu2B (x=0.3) (B-filled β-Mn-type structure) is a bulk superconductor with a transition temperature of about 2.06 K and an upper critical field μ0HC2(0)WHH of 1.2 T, whereas no superconducting transition has been observed up to 0.3 K in Pt9Cu3B5 (Pt9Zn3B5-δ-type structure) from electrical resistivity measurements.

Methods and computer executable instructions for marking a downhole elongate line and detecting same

DOEpatents

Watkins, Arthur D.

2003-05-13

Methods and computer executable instructions are provided for making an elongate line (22) with a plurality of marks (30) and detecting those marks (30) to determine a distance of the elongate line (22) in a downhole or a physical integrity thereof. In a preferred embodiment, each mark comprises a plurality of particles (44) having a substantially permanent magnetizing capability adhered to an exterior surface of the elongate line (22) at preselected intervals with an epoxy paint. The particles (44) are arranged at each interval as a plurality of bands (40). Thereafter, the particles are oriented into a magnetic signature for that interval by magnetizing the particles to create a magnetic field substantially normal to the exterior surface. This facilitates detection by a Hall effect probe. The magnetic signatures are stored in a computing configuration and, once a mark is detected, a correlation is made to a unique position on the elongate line by comparison with the stored magnetic signatures. Preferred particles include samarium-cobalt and neodymium-iron-boride.

Stability of Ceramics in Hydrogen between 4000 and 4500 F

NASA Technical Reports Server (NTRS)

May, Charles E.; Koneval, Donald; Fryburg, George C.

1959-01-01

The various reactions that are possible between hydrogen and certain ceramic materials are discussed as well as the means of measuring the extent of such reactions. Powdered carbides, nitrides, borides, and oxides were tested. These materials were heated inductively in a tungsten cup between 4000 and 4500 F for two 1-hour periods under a static hydrogen atmosphere. Weight, pressure, and diffraction pattern changes were observed, and these served to indicate the extent of reaction. Most of the ceramics, HfC, ZrC, TiC, TaC, NbC, WC, MO2C, HfN, ZrN, NbN, ZrB2, NbB2, and WB, showed less reaction than the minimum detectable value. However, the ceramics, TiN, TaN, HfB2, TiB2, ZrO2, and Cr2O3, apparently reacted to a measurable extent with hydrogen. Reactions of SiC, VC, and TaB2 with hydrogen were not determinable because of their incompatibility with the tungsten container.

Axial residual stresses in boron fibers

NASA Technical Reports Server (NTRS)

Behrendt, D. R.

1978-01-01

The axial residual stress distribution as a function of radius was determined from the fiber surface to the core including the average residual stress in the core. Such measurements on boron on tungsten (B/W) fibers show that the residual stresses for 102, 142, 203, and 366 micron diameter fibers were similar, being compressive at the surface and changing monotonically to a region of tensile within the boron. At approximately 25 percent of the original radius, the stress reaches a maximum tensile stress of about 860 mn/sq.m and then decreases to a compressive stress near the tungsten boride core. Data were presented for 203 micron diameter B/W fibers that show annealing above 900 C reduces the residual stresses. A comparison between 102 micron diameter B/W and boron on carbon (b/C) shows that the residual stresses were similar in the outer regions of the fibers, but that large differences near and in the core were observed. The effects of these residual stresses on the fracture of boron fibers were discussed.

Manganese mono-boride, an inexpensive room temperature ferromagnetic hard material

PubMed Central

Ma, Shuailing; Bao, Kuo; Tao, Qiang; Zhu, Pinwen; Ma, Teng; Liu, Bo; Liu, Yazhou; Cui, Tian

2017-01-01

We synthesized orthorhombic FeB-type MnB (space group: Pnma) with high pressure and high temperature method. MnB is a promising soft magnetic material, which is ferromagnetic with Curie temperature as high as 546.3 K, and high magnetization value up to 155.5 emu/g, and comparatively low coercive field. The strong room temperature ferromagnetic properties stem from the positive exchange-correlation between manganese atoms and the large number of unpaired Mn 3d electrons. The asymptotic Vickers hardness (AVH) is 15.7 GPa which is far higher than that of traditional ferromagnetic materials. The high hardness is ascribed to the zigzag boron chains running through manganese lattice, as unraveled by X-ray photoelectron spectroscopy result and first principle calculations. This exploration opens a new class of materials with the integration of superior mechanical properties, lower cost, electrical conductivity, and fantastic soft magnetic properties which will be significant for scientific research and industrial application as advanced structural and functional materials. PMID:28262805

Laser-assisted selective fusing of thermal sprayed Ni-based self-fluxing alloys by using high-power diode lasers

NASA Astrophysics Data System (ADS)

Chun, Eun-Joon; Kim, Min-Su; Nishikawa, Hiroshi; Park, Changkyoo; Suh, Jeong

2018-03-01

Fusing treatment of Ni-based self-fluxing alloys (Metco-16C and 1276F) was performed using high-power diode lasers to control the temperature of the substrate's surface in real time. The effects of the fusing treatment temperature on the microstructural change and hardness distribution were also investigated. For Metco-16C and 1276F, the macrostructural inhomogeneity (voids) within the thermal sprayed layer decreased considerably as the fusing temperature increased. For both self-fluxing alloys, the optimal temperature for fusing was approximately 1423 K (for Metco-16C) and 1373 K (for 1276F), both of which are within the solid state temperature range; these temperatures maximize the alloy hardness together with the macrostructural homogeneity. In this temperature range, the microstructure consists of a lamellar-structured matrix phase with fine (<5 μm) carbides and borides. Selective fusing for a thermal sprayed layer 0.2-0.5 mm in thickness could be successfully achieved in a high-power diode laser system.

Effect of In-Situ Titanium Boride Particle Addition and Friction Stir Processing on Wear Behavior of Aluminum Alloy 2219

NASA Astrophysics Data System (ADS)

Sampath, V.; Rajasekaran, N. R.

There is paucity of data on the effect of in-situ TiB2 particles on the different behavior of 2219 Al alloy. In the present work, therefore, composites with 2219 Al alloy matrix reinforced with in-situ TiB2 particles were produced by flux-assisted synthesis. Different amounts (5 and 10 wt.%) of TiB2 were incorporated. The base alloy and the composites were subjected to friction stir processing to reduce particle clustering. The wear behavior of the materials was studied. The base alloy showed considerable improvement in the wear behavior due to the in-situ particle addition which is attributed to the presence of finer particles with good interfacial bonding and high hardness. Uniform distribution of TiB2 particles and good interface between the matrix and the particles led to reduction in the wear of friction stir processed composites by 30%. The results are analyzed and discussed in detail in the paper.