Effect of moisture on the physical and durability properties of methyl methacrylate polymer concrete

DOE Office of Scientific and Technical Information (OSTI.GOV)

Fontana, J.J.; Reams, W.

1983-01-01

The compressive strength of methyl methacrylate PC composites decays very rapidly as the moisture content of the coarse aggregate is increased from 0 to 1 wt %. The durability of the PC also shows evidence of decay. Addition of silane coupling agent, such as A-1120, to the monomer component of a PC composite increases the compressive strength of such composites made with moist coarse aggregates. The compressive strengths of such PC composites are as high as a normal PCC used in highway applications. The durability of PC composites made with a silane additive seems to increase as the composite undergoesmore » freeze-thaw cycling which reinforces the justification that such materials can be used for PCC repairs without a sacrifice in use lifespans. However, for the convenience of using moist aggregates, one must endure the additional cost of the silane coupling agent. If it costs more than $0.02/lb to dry the aggregate, and one is willing to accept the reduced strengths associated with moist aggregates, then the use of a silane coupling agent can be cost effective. 3 figures, 4 tables.« less

Effect of silane coupling agents on the chemical and physical properties of photocrosslinked poly(dimethylsiloxane) dimethacrylate/poly(ethylene glycol) diacrylate hydrogel

NASA Astrophysics Data System (ADS)

Lim, K. W.; Hamid, Z. A. A.

2017-07-01

Inorganic-organic hydrogels based on dimethacrylated polydimethylsiloxane (PDMSMA) and diacrylated poly(ethylene glycol) (PEGDA) macromers were prepared via photocrosslinking method. Silane coupling agent was incorporated into the hydrogel formulations to overcome the phase incompatibility. Pure PEGDA (0:100) hydrogels showed the highest value of ESR %, while pure PDMSMA (100:0) hydrogels showed no swelling as we expected. Inclusion of more hydrophobic domains resulted in a lower value of ESR %, i.e. in 75:25 hybrid hydrogels. Beside, we had noticed 50:50 and 75:25 hybrid hydrogels disintegrate during swelling period. However, their integrity was improved and sustained after the coupling agent was added. Similarly, the value of E* for the hybrid hydrogels showed an increment after the coupling agent was incorporated, and this is in a good agreement with the SEM micrograph which display an improved interfacial adhesion.

Effectiveness and stability of silane coupling agent incorporated in 'universal' adhesives.

PubMed

Yoshihara, Kumiko; Nagaoka, Noriyuki; Sonoda, Akinari; Maruo, Yukinori; Makita, Yoji; Okihara, Takumi; Irie, Masao; Yoshida, Yasuhiro; Van Meerbeek, Bart

2016-10-01

For bonding indirect restorations, some 'universal' adhesives incorporate a silane coupling agent to chemically bond to glass-rich ceramics so that a separate ceramic primer is claimed to be no longer needed. With this work, we investigated the effectiveness/stability of the silane coupling function of the silanecontaining experimentally prepared adhesives and Scotchbond Universal (3MESPE). Experimental adhesives consisted of Scotchbond Universal and the silane-free Clearfil S3 ND Quick (Kuraray Noritake) mixed with Clearfil Porcelain Bond Activator (Kuraray Noritake) and the two adhesives to which γ-methacryloxypropyltrimethoxysilane (γ-MPTS) was added. Shear bond strength was measured onto silica-glass plates; the adhesive formulations were analyzed using fourier transform infrared spectroscopy (FTIR) and 13C nuclear magnetic resonance (NMR). In addition, shear bond strength onto CAD-CAM composite blocks was measured without and after thermo-cycling ageing. A significantly higher bond strength was recorded when Clearfil Porcelain Bond Activator was freshly mixed with the adhesive. Likewise, the experimental adhesives, to which γ-MPTS was added, revealed a significantly higher bond strength, but only when the adhesive was applied immediately after mixing; delayed application resulted in a significantly lower bond strength. FTIR and (13)C NMR revealed hydrolysis and dehydration condensation to progress with the time after γ-MPTS was mixed with the two adhesives. After thermo-cycling, the bond strength onto CAD-CAM composite blocks remained stable only for the two adhesives with which Clearfil Porcelain Bond Activator was mixed. Only the silane coupling effect of freshly prepared silanecontaining adhesives was effective. Clinically, the use of a separate silane primer or silane freshly mixed with the adhesive remains recommended to bond glass-rich ceramics. Copyright © 2016 The Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Influence of surface conditions and silane agent on the bond of resin to IPS Empress 2 ceramic.

PubMed

Spohr, Ana Maria; Sobrinho, Lourenço Correr; Consani, Simonides; Sinhoreti, Mario Alexandre Coelho; Knowles, Jonathan C

2003-01-01

The aim of this study was to evaluate the effect of different ceramic surface treatments on the tensile bond strength between IPS Empress 2 ceramic framework and Rely X adhesive resin cement, with or without the application of a silane coupling agent. One hundred twenty disks were made, embedded in resin, and randomly divided into six groups: group 1 = sandblasting (100 microm), no silanation; group 2 = sandblasting (100 microm), silane treatment; group 3 = sandblasting (50 microm), no silanation; group 4 = sandblasting (50 microm), silane treatment; group 5 = hydrofluoric acid etching, no silanation; and group 6 = hydrofluoric acid etching, silane treatment. The disks were bonded into pairs with adhesive resin cement. All samples were stored in distilled water at 37 degrees C for 24 hours and then thermocycled. The samples were submitted to tensile testing. The use of silane improved the bond strength in relation to the groups in which silane was not applied (P < .05). The most effective surface treatment was etching with 10% hydrofluoric acid, both with (25.6 MPa) and without silane application (16.4 MPa); these values showed a statistically significant difference compared to sandblasting with 50- and 100-microm Al2O3. Sandblasting with 50-microm Al2O3, with (11.8 MPa) and without silane (5.4 MPa), demonstrated significantly higher tensile bond strength than sandblasting with 100-microm Al2O3, with (8.3 MPa) and without silane (3.8 MPa). Combined application of 10% hydrofluoric acid and silane enhanced the bond strength between the IPS Empress 2 ceramic framework and resin agent.

A Study on the Rheological and Mechanical Properties of Photo-Curable Ceramic/Polymer Composites with Different Silane Coupling Agents for SLA 3D Printing Technology.

PubMed

Song, Se Yeon; Park, Min Soo; Lee, Jung Woo; Yun, Ji Sun

2018-02-07

Silane coupling agents (SCAs) with different organofunctional groups were coated on the surfaces of Al₂O₃ ceramic particles through hydrolysis and condensation reactions, and the SCA-coated Al₂O₃ ceramic particles were dispersed in a commercial photopolymer based on interpenetrating networks (IPNs). The organofunctional groups that have high radical reactivity and are more effective in UV curing systems are usually functional groups based on acryl, such as acryloxy groups, methacrloxy groups, and acrylamide groups, and these silane coupling agents seem to improve interfacial adhesion and dispersion stability. The coating morphology and the coating thickness distribution of SCA-coated Al₂O₃ ceramic particles according to the different organofunctional groups were observed by FE-TEM. The initial dispersibility and dispersion stability of the SCA-coated Al₂O₃/High-temp composite solutions were investigated by relaxation NMR and Turbiscan. The rheological properties of the composite solutions were investigated by viscoelastic analysis and the mechanical properties of 3D-printed objects were observed with a nanoindenter.

A Study on the Rheological and Mechanical Properties of Photo-Curable Ceramic/Polymer Composites with Different Silane Coupling Agents for SLA 3D Printing Technology

PubMed Central

Song, Se Yeon; Park, Min Soo; Lee, Jung Woo; Yun, Ji Sun

2018-01-01

Silane coupling agents (SCAs) with different organofunctional groups were coated on the surfaces of Al2O3 ceramic particles through hydrolysis and condensation reactions, and the SCA-coated Al2O3 ceramic particles were dispersed in a commercial photopolymer based on interpenetrating networks (IPNs). The organofunctional groups that have high radical reactivity and are more effective in UV curing systems are usually functional groups based on acryl, such as acryloxy groups, methacrloxy groups, and acrylamide groups, and these silane coupling agents seem to improve interfacial adhesion and dispersion stability. The coating morphology and the coating thickness distribution of SCA-coated Al2O3 ceramic particles according to the different organofunctional groups were observed by FE-TEM. The initial dispersibility and dispersion stability of the SCA-coated Al2O3/High-temp composite solutions were investigated by relaxation NMR and Turbiscan. The rheological properties of the composite solutions were investigated by viscoelastic analysis and the mechanical properties of 3D-printed objects were observed with a nanoindenter. PMID:29414912

Locating a silane coupling agent in silica-filled rubber composites by EFTEM.

PubMed

Dohi, Hidehiko; Horiuchi, Shin

2007-11-20

A silane coupling agent (SA) was added to silica/rubber composites at different mixing temperatures and the formation of a coupling layer at the silica/rubber interface was investigated by energy-filtering transmission electron microscopy. Bis(triethoxysilypropyl)tetrasulfane (TESPT), which was used as the SA, reacted with the silanol groups on the silica surface and with styrene-butadiene rubber to form an interfacial coupling layer. The silicon and sulfur elemental distributions were analyzed by electron energy loss spectroscopy (EELS) and elemental mapping. The amount of TESPT trapped in the rubber matrix could be qualitatively estimated by EELS, and the in situ formed coupling layer could be characterized by elemental mapping. The result indicated that the formation of the coupling layer was affected by the mixing temperature. The technique described here will contribute to the study of interface-property relationships and the evaluation of the role of SAs in polymeric composites.

Hybrid joining of polyamide and hydrogenated acrylonitrile butadiene rubber through heat-resistant functional layer of silane coupling agent

NASA Astrophysics Data System (ADS)

Sang, Jing; Sato, Riku; Aisawa, Sumio; Hirahara, Hidetoshi; Mori, Kunio

2017-08-01

A simple, direct adhesion method was developed to join polyamide (PA6) to hydrogenated acrylonitrile butadiene rubber (HNBR) by grafting a functional layer of a silane coupling agent on plasma functionalized PA6 surfaces. The functional layer of the silane coupling agent was prepared using a self-assembly method, which greatly improved the heat resistance of PA6 from 153 °C up to 325 °C and the resulting PA6/HNBR joints showed excellent adhesion properties with cohesive failure between PA6 and HNBR. X-ray photoelectron spectroscopy (XPS), transmission electron microscopy (TEM), and nanoscale infrared microscopy and chemical imaging (Nano-IR, AFM-IR) were employed to characterize the surfaces and interfaces. The Nano-IR analysis method was employed for the first time to analyze the chemical structures of the adhesion interfaces between different materials and to establish the interface formation mechanism. This study is of significant value for interface research and the study of adhesion between resins and rubbers. There is a promising future for heat-resistant functional layers on resin surfaces, with potential application in fuel hose composite materials for the automotive and aeronautical industries.

Rigidity and retention of ceramic root canal posts.

PubMed

Purton, D G; Love, R M; Chandler, N P

2000-01-01

Ceramic root-canal posts offer potential advantages over other types with respect to aesthetics and biocompatibility. Any post must be sufficiently rigid and retentive to withstand functional forces. Ceraposts (1.2 mm coronal diameter, ceramic, tapering, smooth posts) and Paraposts (1.25 mm, stainless-steel, parallel, serrated posts) were tested for rigidity by means of a three-point bending test. To test retention in roots, ceramic posts were cemented using one of three protocols: (1) glass-ionomer cement, (2) silane coupling agent and resin cement, or (3) sandblasted post surface, silane coupling agent, and resin cement. Stainless-steel posts were cemented with resin. The tensile force required to dislodge the posts, following four weeks of storage in water, was recorded. Data were compared using Student's t-test and Mann-Whitney U analysis. Ceraposts were significantly more rigid than Paraposts (p < 0.001). Paraposts cemented with resin were significantly more strongly retained than Ceraposts following any cementation protocol (p < 0.001). Retention of the ceramic posts was significantly greater with a silane coupling agent and resin cement than with glass-ionomer cement (p < 0.001). Sandblasting the ceramic posts produced variable results and needs further investigation before it could be recommended.

Adhesive bonding to polymer infiltrated ceramic.

PubMed

Schwenter, Judith; Schmidli, Fredy; Weiger, Roland; Fischer, Jens

2016-01-01

Aim of this study was to investigate the mechanism of adhesive bonding to the polymer-infiltrated ceramic VITA Enamic [VE]. Shear bond strength was measured with three resin composite cements: RelyX Unicem 2 Automix, Clearfil SA and Variolink II on polished surfaces of VE and its components silicate ceramic [SC] and polymer [PM] (n=12). Further, the effect of etching VE with 5% HF for 15-240 s and the application of silane coupling agents was analyzed in a screening test (n=6). Shear bond strength measurements were performed after 24 h of water storage at 37°C. Significant bonding to polished substrates could only be achieved on VE and SC when silane coupling agents were used. Etching of VE with 5% HF increased shear bond strength. Following silanization of etched VE, a further increase in shear bond strength could be established. Etching for more than 30 s did not improve shear bond strength.

Method of bonding functional surface materials to substrates and applications in microtechnology and anti-fouling

DOEpatents

Feng, Xiangdong; Liu, Jun; Liang, Liang

2001-01-01

A simple and effective method to bond a thin coating of poly(N-isopropylacylamide) (NIPAAm) on a glass surface by UV photopolymerization, and the use of such a coated surface in nano and micro technology applications. A silane coupling agent with a dithiocarbamate group is provided as a photosensitizer preferably, (N,N'-diethylamine) dithiocarbamoylpropyl-(trimethoxy) silane (DATMS). The thiocarbamate group of the sensitizer is then bonded to the glass surface by coupling the silane agent with the hydroxyl groups on the glass surface. The modified surface is then exposed to a solution of NIPAAm and a crosslinking agent which may be any organic molecule having an acrylamide group and at least two double bonds in its structure, such as N, N'-methylenebisacrylamide, and a polar solvent which may be any polar liquid which will dissolve the monomer and the crosslinking agent such as acetone, water, ethanol, or combinations thereof. By exposing the glass surface to a UV light, free radicals are generated in the thiocarbamate group which then bonds to the crosslinking agent and the NIPAAm. Upon bonding, the crosslinking agent and the NIPAAm polymerize to form a thin coating of PNIPAAm bonded to the glass. Depending upon the particular configuration of the glass, the properties of the PNIPAAm allow applications in micro and nano technology.

Method of bonding functional surface materials to substrates and applications in microtechnology and antifouling

DOEpatents

Feng, Xiangdong; Liu, Jun; Liang, Liang

1999-01-01

A simple and effective method to bond a thin coating of poly(N-isopropylacylamide) (NIPAAm) on a glass surface by UV photopolymerization, and the use of such a coated surface in nano and micro technology applications. A silane coupling agent with a dithiocarbamate group is provided as a photosensitizer, preferably, (N,N'-diethylamine)dithiocarbamoylpropyl-(trimethoxy)silane (DATMS). The thiocarbamate group of the sensitizer is then bonded to the glass surface by coupling the silane agent with the hydroxyl groups on the glass surface. The modified surface is then exposed to a solution of NIPAAm and a crosslinking agent which may be any organic molecule having an acrylamide group and at least two double bonds in its structure, such as N,N'-methylenebisacrylamide, and a polar solvent which may be any polar liquid which will dissolve the monomer and the crosslinking agent such as acetone, water, ethanol, or combinations thereof. By exposing the glass surface to a UV light, free radicals are generated in the thiocarbamate group which then bonds to the crosslinking agent and the NIPAAm. Upon bonding, the crosslinking agent and the NIPAAm polymerize to form a thin coating of PNIPAAm bonded to the glass. Depending upon the particular configuration of the glass, the properties of the PNIPAAm allow applications in micro and nano technology.

Silane coupling agent for attaching fusion-bonded epoxy to steel.

PubMed

Tchoquessi Diodjo, Madeleine R; Belec, Lénaïk; Aragon, Emmanuel; Joliff, Yoann; Lanarde, Lise; Perrin, François-Xavier

2013-07-24

We describe the possibility of using γ-aminopropyltriethoxysilane (γ-APS) to increase the durability of epoxy powder coating/steel joints. The curing temperature of epoxy powder coatings is frequently above 200 °C, which is seen so far as a major limitation for the use of the heat-sensitive aminosilane coupling agent. Despite this limitation, we demonstrate that aminosilane is a competitive alternative to traditional chromate conversion to enhance the durability of epoxy powder coatings/steel joints. Fourier-transform reflection-absorption infrared spectroscopy (FT-RAIRS), X-ray photoelectron spectroscopy (XPS), and atomic force microscopy (AFM) were used to identify the silane deposition conditions that influence the adhesion of epoxy powder coatings on steel. We show that AFM analysis provides highly sensitive measurements of mechanical property development and, as such, the degree of condensation of the silane. The joint durability in water at 60 °C was lower when the pH of the γ-APS solution was controlled at 4.6 using formic acid, rather than that at natural pH (10.6). At the curing temperature of 220 °C, oxidation of the carbon adjacent to the amine headgroup of γ-APS gives amide species by a pseudofirst-order kinetics. However, a few amino functionalities remain to react with oxirane groups of epoxy resin and, thus, strengthen the epoxy/silane interphase. The formation of ammonium formate in the acidic silane inhibits the reaction between silane and epoxy, which consequently decreases the epoxy/silane interphase cohesion. We find that the nanoroughness of silane deposits increases with the cure temperature which is beneficial to the wet stability of the epoxy/steel joints, due to increased mechanical interlocking.

Protein immobilization onto various surfaces using a polymer-bound isocyanate

NASA Astrophysics Data System (ADS)

Kang, Hyun-Jin; Cha, Eun Ji; Park, Hee-Deung

2015-01-01

Silane coupling agents have been widely used for immobilizing proteins onto inorganic surfaces. However, the immobilization method using silane coupling agents requires several treatment steps, and its application is limited to only surfaces containing hydroxyl groups. The aim of this study was to develop a novel method to overcome the limitations of the silane-based immobilization method using a polymer-bound isocyanate. Initially, polymer-bound isocyanate was dissolved in organic solvent and then was used to dip-coat inorganic surfaces. Proteins were then immobilized onto the dip-coated surfaces by the formation of urea bonds between the isocyanate groups of the polymer and the amine groups of the protein. The reaction was verified by FT-IR in which NCO stretching peaks disappeared, and CO and NH stretching peaks appeared after immobilization. The immobilization efficiency of the newly developed method was insensitive to reaction temperatures (4-50 °C), but the efficiency increased with reaction time and reached a maximum after 4 h. Furthermore, the method showed comparable immobilization efficiency to the silane-based immobilization method and was applicable to surfaces that cannot form hydroxyl groups. Taken together, the newly developed method provides a simple and efficient platform for immobilizing proteins onto surfaces.

Silane surface modification for improved bioadhesion of esophageal stents

NASA Astrophysics Data System (ADS)

Karakoy, Mert; Gultepe, Evin; Pandey, Shivendra; Khashab, Mouen A.; Gracias, David H.

2014-08-01

Stent migration occurs in 10-40% of patients who undergo placement of esophageal stents, with higher migration rates seen in those treated for benign esophageal disorders. This remains a major drawback of esophageal stent therapy. In this paper, we propose a new surface modification method to increase the adhesion between self-expandable metallic stents (SEMS) and tissue while preserving their removability. Taking advantage of the well-known affinity between epoxide and amine terminated silane coupling agents with amine and carboxyl groups that are abundant in proteins and related molecules in the human body; we modified the surfaces of silicone coated esophageal SEMS with these adhesive self-assembled monolayers (SAMs). We utilized vapor phase silanization to modify the surfaces of different substrates including PDMS strips and SEMS, and measured the force required to slide these substrates on a tissue piece. Our results suggest that surface modification of esophageal SEMS via covalent attachment of protein-binding coupling agents improves adhesion to tissue and could offer a solution to reduce SEMS migration while preserving their removability.

Interfacial properties of aluminum/glass-fiberreinforced polypropylene sandwich composites

NASA Astrophysics Data System (ADS)

Baştürk, S. B.; Guruşçu, A.; Tanoğlu, M.

2013-07-01

Aluminum/glass-fiber-reinforced polypropylene (Al/GFPP) laminates were manufactured by using various surface pretreatment techniques. Adhesion at the composite/metal interface was achieved by a surface pretreatment of Al sheets with amino-based silane coupling agents, incorporation of a polyolefin-based adhesive film and modification with a PP-based film containing 20 wt.% of maleic-anhydride-modified polypropylene (PP-g-MA). In order to increase the effect of bonding between components of the laminates, the combination of silane treatment and the addition of the PP-based film was also investigated. The mechanical properties (shear, peel, and bending strengths) of adhesively bonded Al/GFPP laminates were examined to evaluate the effects of the surface treatments mentioned. It was revealed that the adhesion in the laminated Al/GFPP systems could be improved by the treatment of aluminum surface with an amino-based silane coupling agent. Judging from the results of peel and bending strength, with incorporation of polyolefin-based films, adhesion in the Al/GFPP laminates increased significantly. The modification of Al/GFPP interfaces with a PP-g-MA/PP layer led to the highest improvement in their adhesion properties. The combination of surface modification with silane and addition of PP-based films did not yield the high bending strength desired. This may be due to the insufficient bonding between silane groups and PP-based films.

Influence of Embedding SMA Fibres and SMA Fibre Surface Modification on the Mechanical Performance of BFRP Composite Laminates

PubMed Central

Liu, Yanfei; Wang, Zhenqing; Li, Hao; Sun, Min; Wang, Fangxin; Chen, Bingjie

2018-01-01

In this paper, a new shape memory alloy (SMA) hybrid basalt fibre reinforced polymer (BFRP) composite laminate was fabricated and a new surface modification method with both silane coupling agent KH550 and Al2O3 nanoparticles was conducted to enhance the interface performance. The mechanical performance of BFRP composite laminates with and without SMA fibres and the influence of SMA surface modification were studied in this paper. Different SMA fibre surface treatment methods, including etching with both H2SO4 and NaOH, modification with the silane coupling agent KH550 and new modification method with both KH550 and Al2O3 nanoparticles, were conducted to enhance the bonding between the SMA fibres and polymer matrix. Scanning electron microscopy (SEM) was used to observe the micromorphology of the SMA fibre surfaces exposed to different treatments and the damage morphology of composite laminates. The mechanical performance of the composites was investigated with tensile, three-point bending and low-velocity impact tests to study the influence of embedded SMA fibres and the different surface modifications of the SMA fibres. The results demonstrated that the embedded Ni-Ti SMA fibres can significantly enhance the mechanical performance of BFRP composite laminates. SMA fibres modified with both the silane coupling agent KH550 and Al2O3 nanoparticles illustrate the best mechanical performance among all samples. PMID:29300321

New insights into the adsorption of 3-(trimethoxysilyl)propylmethacrylate on hydroxylated ZnO nanopowders.

PubMed

Bressy, Christine; Ngo, Van Giang; Ziarelli, Fabio; Margaillan, André

2012-02-14

Functionalization of zinc oxide (ZnO) nano-objects by silane grafting is an attractive method to provide nanostructured materials with a variety of surface properties. Active hydroxyl groups on the oxide surface are one of the causes governing the interfacial bond strength in nanohybrid particles. Here, "as-prepared" and commercially available zinc oxide nanopowders with a wide range of surface hydroxyl density were functionalized by a well-known polymerizable silane coupling agent, i.e., 3-(trimethoxysilyl)propylmethacrylate (MPS). Fourier transform infrared (FTIR) and solid-state (13)C and (29)Si nuclear magnetic resonance (NMR) spectroscopic investigations demonstrated that the silane coupling agent was fully hydrolyzed and linked to the hydroxyl groups already present on the particle surface through covalent and hydrogen bonds. Due to a basic catalyzed condensation of MPS with water, a siloxane layer was shown to be anchored to the nanoparticles through mono- and tridentate structures. Quantitative investigations were performed by thermogravimetric (TGA) and elemental analyses. The amount of silane linked to ZnO particles was shown to be affected by the amount of isolated hydroxyl groups available to react on the particle surface. For as-prepared ZnO nanoparticles, the number of isolated and available hydroxyl groups per square nanometer was up to 3 times higher than the one found on commercially available ZnO nanoparticles, leading to higher amounts of polymerizable silane agent linked to the surface. The MPS molecules were shown to be mainly oriented perpendicular to the oxide surface for all the as-prepared ZnO nanoparticles, whereas a parallel orientation was found for the preheated commercially ZnO nanopowders. In addition, ZnO nanoparticles were shown to be hydrophobized by the MPS treatment with water contact angles higher than 60°.

Characterization of electron-beam-modified surface coated clay fillers and their influence on physical properties of rubbers

NASA Astrophysics Data System (ADS)

Ray, Sudip; Bhowmick, Anil K.; Sarma, K. S. S.; Majali, A. B.; Tikku, V. K.

2002-12-01

A novel process of surface modification of clay filler has been developed by coating this with an acrylate monomer, trimethylol propane triacrylate (TMPTA) or a silane coupling agent, triethoxy vinyl silane (TEVS) followed by electron beam irradiation. Characterization of these surface modified fillers has been carried out by Fourier-transform infrared analysis (FTIR), electron spectroscopy for chemical analysis (ESCA), wettability by dynamic wicking method measuring the rise of a liquid through a filler-packed capillary tube and water flotation test, scanning electron microscopy (SEM), energy dispersive X-ray spectroscopy (EDX), thermogravimetric analysis (TGA), and X-ray diffraction (XRD). Presence of the acrylate and the silane coupling agent on the modified fillers has been confirmed from FTIR, ESCA, and EDX studies, which has also been supported by TGA studies. The contact angle measurement by dynamic wicking method suggests improvement in hydrophobicity of the treated fillers, which is supported by water flotation test especially in the case of silanized clay. However, XRD studies demonstrate that the entire modification process does not affect the bulk properties of the fillers. Finally, both unmodified and modified clay fillers have been incorporated in styrene butadiene rubber (SBR) and nitrile rubber (NBR). Rheometric and mechanical properties reveal that there is a definite improvement using these modified fillers specially in the case of silanized clay compared to the control sample, probably due to successful enhancement in interaction between the treated clay and the base polymer.

Initial and long-term bond strengths of one-step self-etch adhesives with silane coupling agent to enamel-dentin-composite in combined situation.

PubMed

Mamanee, Teerapong; Takahashi, Masahiro; Nakajima, Masatoshi; Foxton, Richard M; Tagami, Junji

2015-01-01

This study evaluated the effect of adding silane coupling agent on initial and long-term bond strengths of one-step self-etch adhesives to enamel-dentin-composite in combined situation. Cervical cavities were prepared on extracted molars and filled with Clearfil AP-X. After water-storage for one-week, the filled teeth were sectioned in halves to expose enamel, dentin and composite surfaces and then enamel-dentin-composite surface was totally applied with one of adhesive treatments (Clearfil SE One, Clearfil SE One with Clearfil Porcelain Bond Activator, Beautibond Multi, Beautibond Multi with Beautibond Multi PR Plus and Scotchbond Universal). After designed period, micro-shear bond strengths (µSBSs) to each substrate were determined. For each period of water-storage, additive silane treatments significantly increased µSBS to composite (p<0.001). On the other hand, they significantly decreased µSBS to dentin (p<0.001), although did not have adverse effect on µSBS to enamel (p>0.05). Moreover, the stability of µSBS was depended on materials and substrates used.

Silane surface modification for improved bioadhesion of esophageal stents

PubMed Central

Karakoy, Mert; Gultepe, Evin; Pandey, Shivendra; Khashab, Mouen A.; Gracias, David H.

2014-01-01

Stent migration occurs in 10-40% of patients who undergo placement of esophageal stents, with higher migration rates seen in those treated for benign esophageal disorders. This remains a major drawback of esophageal stent therapy. In this paper, we propose a new surface modification method to increase the adhesion between self-expandable metallic stents (SEMS) and tissue while preserving their removability. Taking advantage of the well-known affinity between epoxide and amine terminated silane coupling agents with amine and carboxyl groups that are abundant in proteins and related molecules in the human body; we modified the surfaces of silicone coated esophageal SEMS with these adhesive self-assembled monolayers (SAMs). We utilized vapor phase silanization to modify the surfaces of different substrates including PDMS strips and SEMS, and measured the force required to slide these substrates on a tissue piece. Our results suggest that surface modification of esophageal SEMS via covalent attachment of protein-binding coupling agents improves adhesion to tissue and could offer a solution to reduce SEMS migration while preserving their removability. PMID:25663731

The Compatibility Effect Of Coupling Agent On Rheological-Morphological Relationship Of Banana Fibre Reinforced Polypropylene

DOE Office of Scientific and Technical Information (OSTI.GOV)

Chang, S. Y.; Shamsudin, Z.

The rheological properties of banana fibre reinforced polypropylene (PP/BF) composites at different composition were analysed using Shimadzu capillary rheometer. The effect of coupling agent concentration on the rheological properties was studied and followed by drawing a relationship of rheological-morphological properties of PP/BF composites. It was found that all composite system exhibits pseudoplasticity and incorporation of treated fibres consequents enhanced viscosity due to improved interfacial adhesion at fibre-matrix interface. However, it was observed that PP/BF composite with 2 wt% silane concentration does not yield further enhancement in the rheological properties when compared to that of 1 wt%. Composites with 1 wt%more » silane concentration were found to yield most promising compatibility effect with well-oriented and uniformly dispersed fibre morphology.« less

Bonelike apatite formation on ethylene-vinyl alcohol copolymer modified with silane coupling agent and calcium silicate solutions.

PubMed

Oyane, Ayako; Kawashita, Masakazu; Nakanishi, Kazuki; Kokubo, Tadashi; Minoda, Masahiko; Miyamoto, Takeaki; Nakamura, Takashi

2003-05-01

An ethylene-vinyl alcohol copolymer (EVOH) was treated with a silane coupling agent and calcium silicate solutions, and then soaked in a simulated body fluid (SBF) with ion concentrations approximately equal to those of human blood plasma. A smooth and uniform bonelike apatite layer was successfully formed on both the EVOH plate and the EVOH-knitted fibers in SBF within 2 days. Part of the structure of the resulting apatite-EVOH fiber composite was similar to that of natural bone. If this kind of composite can be fabricated into a three-dimensional structure similar to natural bone, the resultant composite is expected to exhibit both mechanical properties analogous to those of natural bone and bone-bonding ability. Hence, it has great potential as a bone substitute. Copyright 2003 Elsevier Science Ltd.

Synthesis route and three different core-shell impacts on magnetic characterization of gadolinium oxide-based nanoparticles as new contrast agents for molecular magnetic resonance imaging

NASA Astrophysics Data System (ADS)

Azizian, Gholamreza; Riyahi-Alam, Nader; Haghgoo, Soheila; Moghimi, Hamid Reza; Zohdiaghdam, Reza; Rafiei, Behrooz; Gorji, Ensieh

2012-10-01

Despite its good resolution, magnetic resonance imaging intrinsically has low sensitivity. Recently, contrast agent nanoparticles have been used as sensitivity and contrast enhancer. The aim of this study was to investigate a new controlled synthesis method for gadolinium oxide-based nanoparticle preparation. For this purpose, diethyleneglycol coating of gadolinium oxide (Gd2O3-DEG) was performed using new supervised polyol route, and small particulate gadolinium oxide (SPGO) PEGylation was obtained with methoxy-polyethylene-glycol-silane (550 and 2,000 Da) coatings as SPGO-mPEG-silane550 and 2,000, respectively. Physicochemical characterization and magnetic properties of these three contrast agents in comparison with conventional Gd-DTPA were verified by dynamic light scattering transmission electron microscopy, Fourier transform infrared spectroscopy, inductively coupled plasma, X-ray diffraction, vibrating sample magnetometer, and the signal intensity and relaxivity measurements were performed using 1.5-T MRI scanner. As a result, the nanoparticle sizes of Gd2O3-DEG, SPGO-mPEG-silane550, and SPGO-mPEG-silane2000 could be reached to 5.9, 51.3, 194.2 nm, respectively. The image signal intensity and longitudinal ( r 1) and transverse relaxivity ( r 2) measurements in different concentrations (0.3 to approximately 2.5 mM), revealed the r 2/ r 1 ratios of 1.13, 0.89, 33.34, and 33.72 for Gd-DTPA, Gd2O3-DEG, SPGO-mPEG-silane550, and SPGO-mPEG-silane2000, respectively. The achievement of new synthesis route of Gd2O3-DEG resulted in lower r 2/ r 1 ratio for Gd2O3-DEG than Gd-DTPA and other previous synthesized methods by this and other groups. The smaller r 2/ r 1 ratios of two PEGylated-SPGO contrast agents in our study in comparison with r 2/ r 1 ratio of previous PEGylation ( r 2/ r 1 = 81.9 for mPEG-silane 6,000 MW) showed that these new three introduced contrast agents could potentially be proper contrast enhancers for cellular and molecular MR imaging.

The Effect of Silane Addition on Chitosan-Fly Ash/CTAB as Electrolyte Membrane

NASA Astrophysics Data System (ADS)

Kusumastuti, E.; Isnaeni, D.; Sulistyaningsih, T.; Mahatmanti, F. W.; Jumaeri; Atmaja, L.; Widiastuti, N.

2017-02-01

Electrolyte membrane is an important component in fuel cell system, because it may influence fuel cell performance. Many efforts have been done to produce electrolyte membrane to replace comercial membrane. In this research, electrolyte membrane is composed of chitosan as an organic matrix and fly ash modified with CTAB and silane as inorganic filler. Fly ash is modified using silane as coupling agent to improve interfacial morphology between organic matrix and inorganic filler. This research aims to determine the best membrane performance based on its characteristics such as water uptake, mechanical properties, proton conductivity, and methanol permeability. The steps that have been done include silica preparation from fly ash, modification of silica surface with CTAB, silica coupling process with silane, synthesis of membranes with inversion phase method, and membrane characterization. The result shows that membrane C-FA/CTAB-Silane 10% (w/w) has the best performance with proton conductivity 8.00 x 10-4 S.cm-1, methanol permeability 3.37 x 10-7 cm.s-1, and selectivity 2.12 x 103 S.s.cm-3. The result of FTIR analysis on membrane C-FA/CTAB-Silane 10% shows that there is only physical interaction occured between chitosan, fly ash and silane, because there is no peak differences significantly at wave number 1000-1250 cm-1, while morphology analysis on membrane with Scanning Electron Microscopy (SEM) shows good dispersion and there is no agglomeration on chitosan matrix.

Medical implants and methods of making medical implants

DOEpatents

Shaw, Wendy J; Yonker, Clement R; Fulton, John L; Tarasevich, Barbara J; McClain, James B; Taylor, Doug

2014-09-16

A medical implant device having a substrate with an oxidized surface and a silane derivative coating covalently bonded to the oxidized surface. A bioactive agent is covalently bonded to the silane derivative coating. An implantable stent device including a stent core having an oxidized surface with a layer of silane derivative covalently bonded thereto. A spacer layer comprising polyethylene glycol (PEG) is covalently bonded to the layer of silane derivative and a protein is covalently bonded to the PEG. A method of making a medical implant device including providing a substrate having a surface, oxidizing the surface and reacting with derivitized silane to form a silane coating covalently bonded to the surface. A bioactive agent is then covalently bonded to the silane coating. In particular instances, an additional coating of bio-absorbable polymer and/or pharmaceutical agent is deposited over the bioactive agent.

Surface modification and characterization of basalt fibers as potential reinforcement of concretes

NASA Astrophysics Data System (ADS)

Iorio, M.; Santarelli, M. L.; González-Gaitano, G.; González-Benito, J.

2018-01-01

Basalt fibers were surface treated with silane coupling agents as a method to enhance the adhesion and durability of fiber-matrix interfaces in concrete based composite materials. In particular, this work has been focused on the study of basalt fibers chemical coatings with aminosilanes and their subsequent characterization. Surface treatments were carried out after removing the original sizing applied by manufacturer and pretreating them with an activation process of surface silanol regeneration. Different samples were considered to make convenient comparisons: as received fibers (commercial), calcinated fibers (without commercial sizing), activated samples (calcinated fibers subjected to an acid process for hydroxyl regeneration), and silanized fibers with γ-aminopropiltriethoxysilane, γ-aminopropilmethyldiethoxysilane and a mixture of 50% by weight of both silanes. A deep characterization was carried out in terms of structure using X-ray diffraction, XRD, and Fourier transform infrared spectroscopy, FTIR, thermal properties by thermogravimetric analysis, TGA, coupled with single differential thermal analysis, SDTA, and morphology by scanning electron microscopy, SEM, and atomic force microscopy, AFM.

Silane coupling agent bearing a photoremovable succinimidyl carbonate for patterning amines on glass and silicon surfaces with controlled surface densities.

PubMed

Nakayama, Hidekazu; Nakanishi, Jun; Shimizu, Takahiro; Yoshino, Yutaro; Iwai, Hideo; Kaneko, Shingo; Horiike, Yasuhiro; Yamaguchi, Kazuo

2010-03-01

Patterned immobilization of synthetic and biological ligands on material surfaces with controlled surface densities is important for various bioanalytical and cell biological purposes. This paper describes the synthesis, characterization, and application of a novel silane coupling agent bearing a photoremovable succinimidyl carbonate, which enables the photopatterning of various primary amines on glass and silicon surfaces. The silane coupling agent is 1-[5-methoxy-2-nitro-4-(3-trimethoxysilylpropyloxy)phenyl]ethyl N-succinimidyl carbonate. The distinct feature of this molecule is that it has a photocleavable 2-nitrobenzyl switch between a trimethoxysilyl group and a succinimidyl carbonate, each reactive to the hydroxy groups of inorganic oxides and primary amines. Based on this molecular design, the compound allows for the one-step introduction of succinimidyl carbonates onto the surface of glass and silicon, immobilization of primary amines, and region-selective and dose-dependent release of the amines by near-UV irradiation. Therefore, we were able to pattern amine ligands on the substrates in given surface densities and arbitrary geometries by controlling the doses and regions of photoirradiation. These features were verified by UV-vis spectroscopy, contact angle measurements, infrared (IR) spectroscopy, X-ray photoelectron spectroscopy (XPS), ellipsometry, and atomic force microscopy (AFM). The compound was applied to form a chemical density gradient of amino-biotin on a silicon substrate in a range of 0.87-0.12 chains/nm(2) by controlling photoirradiation under a standard fluorescence microscope. Furthermore, we also succeeded in forming a chemical density gradient at a lower surface density range (0.15-0.011 chains/nm(2)) on the substrate by diluting the feed amino-biotin with an inert control amine.

EFFECT OF SILANE COUPLING AGENTS ON RHEOLOGICAL PROPERTIES OF SOLVENTLESS MAGNETIC INK. (R826728)

EPA Science Inventory

The perspectives, information and conclusions conveyed in research project abstracts, progress reports, final reports, journal abstracts and journal publications convey the viewpoints of the principal investigator and may not represent the views and policies of ORD and EPA. Concl...

Mercapto-based coupling agent for improved thermophotovoltaic device back surface reflector adhesion and reflectance

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wernsman, Bernard; Fiedor, Joseph N.; Irr, Lawrence G.

2016-10-04

A back surface reflector (BSR) is described. The BSR includes a reflecting layer, a substrate and an adhesion layer between the reflecting layer and the substrate. The adhesion layer includes 3-mercaptopropyl (trimethoxy) silane (a.k.a. Merc).

Vulcanization characteristics and dynamic mechanical behavior of natural rubber reinforced with silane modified silica.

PubMed

Chonkaew, Wunpen; Minghvanish, Withawat; Kungliean, Ulchulee; Rochanawipart, Nutthaya; Brostow, Witold

2011-03-01

Two silane coupling agents were used for hydrolysis-condensation reaction modification of nanosilica surfaces. The surface characteristics were analyzed using Fourier transform infrared spectroscopy (FTIR). The vulcanization kinetics of natural rubber (NR) + silica composites was studied and compared to behavior of the neat NR using differential scanning calorimetry (DSC) in the dynamic scan mode. Dynamic mechanical analysis (DMA) was performed to evaluate the effects of the surface modification. Activation energy E(a) values for the reaction are obtained. The presence of silica, modified or otherwise, inhibits the vulcanization reaction of NR. The neat silica containing system has the lowest cure rate index and the highest activation energy for the vulcanization reaction. The coupling agent with longer chains causes more swelling and moves the glass transition temperature T(g) downwards. Below the glass transition region, silica causes a lowering of the dynamic storage modulus G', a result of hindering the cure reaction. Above the glass transition, silica-again modified or otherwise-provides the expected reinforcement effect.

Nano-hybrid carboxymethyl-hexanoyl chitosan modified with (3-aminopropyl)triethoxysilane for camptothecin delivery.

PubMed

Hsiao, Meng-Hsuan; Tung, Tsan-Hua; Hsiao, Chi-Sheng; Liu, Dean-Mo

2012-06-20

Silane-modified amphiphilic chitosan was synthesized by anchoring a silane coupling agent, (3-aminopropyl)triethoxysilane, to a novel amphiphilic carboxymethyl-hexanoyl chitosan (CHC). The chemical structure of this new organic-inorganic hybrid molecule was characterized by FTIR and 13C-, 29Si-nuclear magnetic resonance, while the structural evolution was examined using scanning electron microscopy (SEM), transmission electron microscopy (TEM), X-ray diffraction (XRD), and dynamic light scattering (DLS). Experimental results indicated a self-assembly behaviour of molecules into nanoparticles with a stable polygonal geometry, consisting of ordered silane layers of 6 nm in thickness. The self-assembly property was found to be influenced by chemical composition and concentration of silane incorporated, while the size can be varied by the amount of anchored silane. It was also demonstrated that such vesicle exhibited excellent cytocompatibility and cellular internalization capability in ARPE-19 cell line, and presented well-controlled encapsulation and release profiles for (S)-(+)-camptothecin. These unique properties render it as a potential drug delivery nanosystem. Copyright © 2012 Elsevier Ltd. All rights reserved.

Coupling of HDPE/hydroxyapatite composites by silane-based methodologies.

PubMed

Sousa, R A; Reis, R L; Cunha, A M; Bevis, M J

2003-06-01

Several coupling treatments based on silane chemicals were investigated for the development of high density (HDPE)/hydroxyapatite (HA) composites. Two HA powders, sintered HA (HAs) and non sintered HA (HAns), were studied in combination with five silanes, namely y-methacryloxy propyltrimethoxy silane (MEMO), 3-(2-aminoethyl)aminopropyltrimethoxy silane (DAMO), vinyltrimethoxy silane (VTMO), 3-aminopropyltriethoxy silane (AMEO) and trimethoxypropyl silane (PTMO). The HA particles were treated by a dipping in method or by spraying with silane solutions. After drying, the treated powders were compounded with HDPE or HDPE with acrylic acid and/or organic peroxide and subsequently compression molded. The tensile test specimens obtained from the molded plates were tensile tested and their fracture surfaces were observed by scanning electron microscopy (SEM). For the sintered HA (HAs) composites, the most effective coupling treatments concerning stiffness are those based on MEMO and AMEO. The low influence of these coupling procedures on strength is believed to be associated to the low volume fraction and the relatively smooth surface of the used HA particles. For the non-sintered HA (HAns) composites, it was possible to improve significantly both the stiffness and the strength. Amino silanes demonstrated to be highly efficient concerning strength enhancement. The higher effectiveness of the coupling treatments for HAns filled composites is attributed to their higher particle surface area, smaller particle size distribution and expected higher chemical reactivity. For both cases, the improvement in mechanical performance after the coupling treatment is consistent with the enhancement in interfacial adhesion observed by SEM.

Effect of γ-aminopropyltriethoxy silane (γ-APS) coupling agent on mechanical and morphological properties of high density polyethylene (HDPE)/acrylonitrile butadiene rubber (NBR)/palm pressed fibre (PPF) composites

NASA Astrophysics Data System (ADS)

Norizan, Nabila Najwa; Santiagoo, Ragunathan; Ismail, Hanafi

2017-07-01

The fabrication of High Density Polyethylene (HDPE)/ Acrylonitrile-butadiene rubber (NBR)/ Palm Pressed Fibre (PPF) composite were investigated. The effect of γ-Aminopropyltriethoxy Silane (APS) as coupling agent on the properties of HDPE/ NBR/ PPF composite were studied. The composites were melt mixed using heated two roll mill at 180°C and speed of 15rpm with six different loading (100/0/10, 80/20/10, 70/30/10, 60/40/10, 50/50/10, and 40/60/10). The effects of γ-APS silane on mechanical, and morphological properties were examined using universal tensile machine (UTM) and scanning electron microscopy (SEM), respectively. Tensile strength and Young's modulus of HDPE/ NBR/ PPF composites decrease with increasing of NBR loading, whilst increasing the elongation at break. However, treated composites have resulted 3% to 29%, and 9% to 19%, higher in tensile strength and young's modulus compared to untreated composites. This was due to the better adhesion between HDPE/ NBR matrices and PPF filler with the presence of silanol moieties. From the morphological study, the micrograph of treated composites has proved the well bonded and good attachment of PPF filler with HDPE/ NBR matrices which resulted to better tensile strength to the HDPE/ NBR/ PPF composites.

The Effect of Different Coupling Agents on Nano-ZnO Materials Obtained via the Sol-Gel Process.

PubMed

Purcar, Violeta; Şomoghi, Raluca; Niţu, Sabina Georgiana; Nicolae, Cristian-Andi; Alexandrescu, Elvira; Gîfu, Ioana Cătălina; Gabor, Augusta Raluca; Stroescu, Hermine; Ianchiş, Raluca; Căprărescu, Simona; Cinteză, Ludmila Otilia

2017-12-12

Hybrid nanomaterials based on zinc oxide were synthesized via the sol-gel method, using different silane coupling agents: (3-glycidyloxypropyl)trimethoxysilane (GPTMS), phenyltriethoxysilane (PhTES), octyltriethoxysilane (OTES), and octadecyltriethoxysilane (ODTES). Morphological properties and the silane precursor type effect on the particle size were investigated using dynamic light scattering (DLS), environmental scanning electron microscopy (ESEM), transmission electron microscopy (TEM), thermogravimetric analysis (TGA), and X-ray diffraction (XRD). The bonding characteristics of modified ZnO materials were investigated using Fourier transform infrared spectroscopy (FTIR). The final solutions were deposited on metallic substrate (aluminum) in order to realize coatings with various wettability and roughness. The morphological studies, obtained by ESEM and TEM analysis, showed that the sizes of the ZnO nanoparticles are changed as function of silane precursor used in synthesis. The thermal stability of modified ZnO materials showed that the degradation of the alkyl groups takes place in the 300-500 °C range. Water wettability study revealed a contact angle of 142 ± 5° for the surface covered with ZnO material modified with ODTES and showed that the water contact angle increases as the alkyl chain from the silica precursor increases. These modified ZnO materials, therefore, can be easily incorporated in coatings for various applications such as anti-corrosion and anti-icing.

Surface modification of cellulose using silane coupling agent.

PubMed

Thakur, Manju Kumari; Gupta, Raju Kumar; Thakur, Vijay Kumar

2014-10-13

Recently there has been a growing interest in substituting traditional synthetic polymers with natural polymers for different applications. However, natural polymers such as cellulose suffer from few drawbacks. To become viable potential alternatives of synthetic polymers, cellulosic polymers must have comparable physico-chemical properties to that of synthetic polymers. So in the present work, cellulose polymer has been modified by a series of mercerization and silane functionalization to optimize the reaction conditions. Structural, thermal and morphological characterization of the cellulose has been done using FTIR, TGA and SEM, techniques. Surface modified cellulose polymers were further subjected to evaluation of their properties like swelling and chemical resistance behavior. Published by Elsevier Ltd.

Effect of Filler Content and Chemical Modification on Mechanical Properties of Polylactic Acid/Polymethyl Methacrylate/Nypa Fruticans Husk Biocomposites

NASA Astrophysics Data System (ADS)

Mohamad Syahmie, MR; Pei Leng, T.; Nurul Najwa, Zabidi

2018-03-01

The main purpose of incorporating Nypa fruticans husks (NFH) into Polylactic acid (PLA)/Polymethylmethacrylate (PMMA) is to decrease the costs and enhanced the properties of the biocomposites. 3-Aminopropyl Triethoxysilane (3-APE) was used as coupling agent. The effect of NFH content and 3-APE on the mechanical properties and morphology of the biocomposites were investigated. Results show that the effect of NFH content increased Young’s modulus but decreased the tensile strength and elongation at break of PLA/PMMA/NFH biocomposites. However, silanized biocomposites using 3-APE) was found to enhanced the tensile strength and Young’s modulus but decreased the elongation at break of the silanized biocomposites. Scanning electron microscopy (SEM) study of the tensile fracture surface of the biocomposites indicated that the used of 3-APE as couling agent improved the interfacial interaction netween NFH and PLA/PMMA blends.

Effect of Er,Cr:YSGG laser, air abrasion, and silane application on repaired shear bond strength of composites.

PubMed

Cho, S D; Rajitrangson, P; Matis, B A; Platt, J A

2013-01-01

Aged resin composites have a limited number of carbon-carbon double bonds to adhere to a new layer of resin. Study objectives were to 1) evaluate various surface treatments on repaired shear bond strength between aged and new resin composites and 2) to assess the influence of a silane coupling agent after surface treatments. Eighty disk-shape resin composite specimens were fabricated and thermocycled 5000 times prior to surface treatment. Specimens were randomly assigned to one of the three surface treatment groups (n=20): 1) air abrasion with 50-μm aluminum oxide, 2) tribochemical silica coating (CoJet), or 3) Er,Cr:YSGG (erbium, chromium: yttrium-scandium-gallium-garnet) laser or to a no-treatment control group (n=20). Specimens were etched with 35% phosphoric acid, rinsed, and dried. Each group was divided into two subgroups (n=10): A) no silanization and B) with silanization. The adhesive agent was applied and new resin composite was bonded to each conditioned surface. Shear bond strength was evaluated and data analyzed using two-way analysis of variance (ANOVA). Air abrasion with 50-μm aluminum oxide showed significantly higher repair bond strength than the Er,Cr:YSGG laser and control groups. Air abrasion with 50-μm aluminum oxide was not significantly different from tribochemical silica coating. Tribochemical silica coating had significantly higher repair bond strength than Er,Cr:YSGG laser and the control. Er,Cr:YSGG laser and the control did not have significantly different repair bond strengths. Silanization had no influence on repair bond strength for any of the surface treatment methods. Air abrasion with 50-μm aluminum oxide and tribochemical silica followed by the application of bonding agent provided the highest repair shear bond strength values, suggesting that they might be adequate methods to improve the quality of repairs of resin composites.

Effect of glass fiber surface treatments on mechanical strength of epoxy based composite materials.

PubMed

Iglesias, J G; González-Benito, J; Aznar, A J; Bravo, J; Baselga, J

2002-06-01

Sizing glass fibers with silane coupling agents enhances the adhesion and the durability of the fiber/polymer matrix interface in composite materials. There are several tests to determine the interfacial strength between a fiber and resin, but all of them present difficulties in interpreting the results and/or sample preparation. In this study, we observed the influence of different aminosilanes fiber coatings on the resistance of epoxy-based composite materials using a very easy fractographic test. In addition, we tried a new fluorescence method to get information on a molecular level precisely at the interface. Strength was taken into account from two standpoints: (i) mechanical strength and (ii) the resistance to hydrolysis of the interface in oriented glass-reinforced epoxy-based composites. Three silanes: gamma-aminopropyltriethoxysilane, gamma-Aminopropylmethyldiethoxysilane, and gamma-Aminopropyldimethylethoxysilane were used to obtain different molecular structures at the interface. It was concluded that: (i) the more accessible amine groups are, the higher the interface rigidity is; (ii) an interpenetrating network mechanism seems to be the most important for adhesion and therefore to the interfacial strength; and (iii) the higher the degree of crosslinking in the silane coupling layer is, the higher the hydrolytic damage rate is.

Performance of waste-paper/PETG wood–plastic composites

NASA Astrophysics Data System (ADS)

Huang, Lijie; An, Shuxiang; Li, Chunying; Huang, Chongxing; Wang, Shuangfei; Zhang, Xiaoxiao; Xu, Mingzi; Chen, Jie; Zhou, Lei

2018-05-01

Wood-plastic composites were prepared from polyethylene terephthalate- 1,4-cyclohexanedimethanol ester (PETG) and waste-paper fiber that was unmodified, modified with alkyl-ketene-dimer (AKD), and modified with a silane-coupling agent. The mechanical properties, water absorption properties, surface structure, and thermal properties of the three prepared materials were compared. The results showed that the optimum amount of waste-paper powder is 10 wt%, while that of the waste-paper particles is 60-80 mesh. The use of AKD and coupling agent KH550 can reduce the water absorption of the composite; however, the reductive effect of the coupling agent is better, in that it is reduced by 0.3%. Modification using a 1-wt% KH550 coupling agent can effectively increase the tensile strength of a composite from 31.36 to 41.67 MPa (increase of 32.8%), while the bending strength increased from 86.47 to 98.31 MPa (increase of 13.7%). This also enhances the thermal stability of the composites. With the addition of the coupling agent, the composite material maintains good mechanical properties even after being immersed in water; this can enable the safe use of these composite materials in outdoor environments.

The effect of surface modification of glass fiber on the performance of poly(lactic acid) composites: Graphene oxide vs. silane coupling agents

NASA Astrophysics Data System (ADS)

Jing, Mengfan; Che, Junjin; Xu, Shuman; Liu, Zhenwei; Fu, Qiang

2018-03-01

In this work, a comparison study was carried out to investigate the efficacy of glass fiber (GF) in reinforcing poly(lactic acid) (PLA) by using traditional silane coupling agents (GF-S) and novel graphene oxide (GF-GO) as surface modifiers. The crystallization behavior of the PLA matrix was investigated by differential scanning calorimetry. The mechanical performances and the thermomechanical properties of the composites were evaluated by uniaxial tensile testing and dynamic mechanical analysis, respectively. For neat GF without any treatment, the poor interfacial adhesion and the sharp shortening of the GF length result in the relatively poor mechanical performances of PLA/GF composites. However, the incorporation of GF-S significantly improves the mechanical strength and keeps relatively good toughness of the composites, while GF-GO exhibits excellent nucleation ability for PLA and could moderately increase the modulus of the composites. The thermomechanical properties of the composites are improved markedly resulting from the crystallinity increase. The different surface modification of glass fiber influences the crystallinity of matrix, the interfacial interaction and the length of fiber, which altogether affect the mechanical performances of the prepared PLA/GF composites.

Organic-Inorganic Hybrids Using Novel Phenylethynyl Imide Silanes

NASA Technical Reports Server (NTRS)

Park, C.; Lowther, S. E.; Smith, J. G., Jr.

2001-01-01

In this presentation, polyimide-silica hybrids using novel phenylethynyl imide silanes are reported. The phenylethynyl group is present in the organic precursor as either a pendent or an end group to bond chemically with the polyimide adhesive containing phenylethynyl groups during processing, while the silane group of the organic precursor would chemically react with the inorganic precursor through oxane bond formation. The chemical compositions of these novel hybrids were examined using X-ray mapping modes of scanning electron microscopy (SEM), which revealed a silicon gradient interphase between the high surface energy substrate and the polyimide adhesive. Novel aromatic phenylethynyl imide silanes (APEISs) and pendent phenylethynyl imide oligomeric disilanes (PPEIDSs) have been synthesized, and sol-gel solutions containing the new silanes, a phenylethynyl terminated imide oligomer (PETI-5), and an inorganic precursor were formulated to develop a gradient hybrid interphase between a titanium alloy and the adhesive. Two different sol-gel systems were investigated to develop organic-inorganic hybrids. Hybrid I was composed of an organic precursor containing both phenylethynyl and silane groups (PPEIDS) and an inorganic precursor. Functional group concentrations were controlled by the variation of the molecular weight of the imide backbone of PPEIDS. Hybrid II was composed of organic and inorganic precursors and a coupling agent containing both phenylethynyl and silane groups. Morphology and chemical composition of the hybrid interphase between the inorganic substrate and the adhesive were investigated, and the bond strength and durability were evaluated using lap shear tests at various conditions. The assessment of how the bonding at an interface is affected by various sol-gel solution compositions and environments is reported.

Formation mechanism of a silane-PVA/PVAc complex film on a glass fiber surface.

PubMed

Repovsky, Daniel; Jane, Eduard; Palszegi, Tibor; Slobodnik, Marek; Velic, Dusan

2013-10-21

Mechanical properties of glass fiber reinforced composite materials are affected by fiber sizing. A complex film formation, based on a silane film and PVA/PVAc (polyvinyl alcohol/polyvinyl acetate) microspheres on a glass fiber surface is determined at 1) the nanoscale by using atomic force microscopy (AFM), and 2) the macroscale by using the zeta potential. Silane groups strongly bind through the Si-O-Si bond to the glass surface, which provides the attachment mechanism as a coupling agent. The silane groups form islands, a homogeneous film, as well as empty sites. The average roughness of the silanized surface is 6.5 nm, whereas it is only 0.6 nm for the non-silanized surface. The silane film vertically penetrates in a honeycomb fashion from the glass surface through the deposited PVA/PVAc microspheres to form a hexagonal close pack structure. The silane film not only penetrates, but also deforms the PVA/PVAc microspheres from the spherical shape in a dispersion to a ellipsoidal shape on the surface with average dimensions of 300/600 nm. The surface area value Sa represents an area of PVA/PVAc microspheres that are not affected by the silane penetration. The areas are found to be 0.2, 0.08, and 0.03 μm(2) if the ellipsoid sizes are 320/570, 300/610, and 270/620 nm for silane concentrations of 0, 3.8, and 7.2 μg mL(-1), respectively. The silane film also moves PVA/PVAc microspheres in the process of complex film formation, from the low silane concentration areas to the complex film area providing enough silane groups to stabilize the structure. The values for the residual silane honeycomb structure heights (Ha ) are 6.5, 7, and 12 nm for silane concentrations of 3.8, 7.2, and 14.3 μg mL(-1), respectively. The pH-dependent zeta-potential results suggest a specific role of the silane groups with effects on the glass fiber surface and also on the PVA/PVAc microspheres. The non-silanized glass fiber surface and the silane film have similar zeta potentials ranging from -64 to -12 mV at pH's of 10.5 and 3, respectively. The zeta potentials for the PVA/PVAc microspheres on the glass fiber surface and within the silane film significantly decrease and range from -25 to -5 mV. The shapes of the pH-dependent zeta potentials are different in the cases of silane groups over a pH range from 7 to 4. A triple-layer model is used to fit the non-silanized glass surface and the silane film. The value of the surface-site density for Γ(Xglass) and Γ(Xsilane), in which X denotes the Al-O-Si group, differs by a factor of 10(-4), which suggests an effective coupling of the silane film. A soft-layer model is used to fit the silane-PVA/PVAc complex film, which is approximated as four layers. Such a simplification and compensation of the microsphere shape gives an approximation of the relevant widths of the layers as the follows: 1) the layer of the silane groups makes up 10% of the total length (27 nm), 2) the layer of the first PVA shell contributes 30% to the total length (81 nm), 3) the layer of the PVAc core contributes 30% to the total length (81 nm), and finally 4) the layer of the second PVA shell provides 30% of the total length (81 nm). The coverage simulation resulted in a value of 0.4, which corresponds with the assumption of low-order coverage, and is supported by the AFM scans. Correlating the results of the AFM scans, and the zeta potentials sheds some light on the formation mechanism of the silane-PVA/PVAc complex film. Copyright © 2013 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Molecular structures of (3-aminopropyl)trialkoxysilane on hydroxylated barium titanate nanoparticle surfaces induced by different solvents and their effect on electrical properties of barium titanate based polymer nanocomposites

NASA Astrophysics Data System (ADS)

Fan, Yanyan; Wang, Guanyao; Huang, Xingyi; Bu, Jing; Sun, Xiaojin; Jiang, Pingkai

2016-02-01

Surface modification of nanoparticles by grafting silane coupling agents has proven to be a significant approach to improve the interfacial compatibility between inorganic filler and polymer matrix. However, the impact of grafted silane molecular structure after the nanoparticle surface modification, induced by the utilized solvents and the silane alkoxy groups, on the electrical properties of the corresponding nanocomposites, has been seldom investigated. Herein, the silanization on the surface of hydroxylated barium titanate (BT-OH) nanoparticles was introduced by using two kinds of trialkoxysilane, 3-aminopropyltriethoxysilane (AMEO) and 3-aminopropyltrimethoxysilane (AMMO), with different solvents (toluene and ethanol), respectively. Solid-state 13C, 29Si nuclear magnetic resonance (NMR) spectroscopy and high-resolution X-ray photoelectron spectroscopy (XPS) were employed to validate the structure differences of alkoxysilane attachment to the nanoparticles. The effect of alkoxysilane structure attached to the nanoparticle surface on the dielectric properties of the BT based poly(vinylidene fluoride) (PVDF) nanocomposites were investigated. The results reveal that the solvents used for BT nanoparticle surface modification exhibit a significant effect on the breakdown strength of the nanocomposites. Nevertheless, the alkoxy groups of silane show a marginal influence on the dielectric properties of the nanocomposites. These research results provide important insights into the fabrication of advanced polymer nanocomposites for dielectric applications.

Durable low surface-energy surfaces

NASA Technical Reports Server (NTRS)

Willis, Paul B. (Inventor); McElroy, Paul M. (Inventor); Hickey, Gregory H. (Inventor)

1993-01-01

A formulation for forming a low surface-energy surface on a substrate having (i) a fluoroalkyl silane having a low surface energy part, (ii) a liquid crystal silane operable for enhancing the orientation of the molecules of the fluoroalkyl silane and for crosslinking with the fluoroalkyl silane, and, (iii) a transport medium for applying the fluoroalkyl silane and the liquid crystal silane to the surface of a substrate. In one embodiment the formulation can includes a crosslinking agent for crosslinking the fluoroalkyl silane. In another embodiment the formulation has a condensation catalyst for enhancing chemical bonding of the fluoroalkyl silane to the substrate. The transport medium can be an alcohol such as methanol or ethanol.

Influences of surface modification of nano-silica by silane coupling agents on the thermal and frictional properties of cyanate ester resin

NASA Astrophysics Data System (ADS)

Chuang, Wang; Geng-sheng, Jiao; Lei, Peng; Bao-lin, Zhu; Ke-zhi, Li; Jun-long, Wang

2018-06-01

The surface of nano-silicon dioxide (nano-SiO2) particles was modified by small molecular coupling agent KH-560 and macromolecular coupling agent SEA-171, respectively, to change the surface activity and structure. The modified nano-SiO2 was then used for reinforcing cyanate ester resin (CE). Influences of the content of nano-SiO2 and the interfacial structure over the thermal and frictional properties of nano-SiO2/CE composites were investigated. The mechanism of the surface modification of silicon dioxide by KH-560 and SEA-171 was discussed. The experimental results show that the addition of coupling agents increased the interfacial bonding between nano-SiO2 particles and the CE resin so that the heat resistance and friction properties of the composites were improved. After surface treatment of nano-SiO2 by SEA-171, the thermal decomposition temperature of the 3.0 wt% nano-SiO2/CE composites increased nearly by 75 °C and the frictional coefficient was reduced by 25% compared with that of the pure CE, and the wear resistance increased by 77%.

Shear Bond Strength of Metal Brackets to Zirconia Conditioned with Various Primer-Adhesive Systems

DTIC Science & Technology

2016-07-01

Reynolds, 1979 ). Bonding orthodontic brackets to ceramic restorative materials poses a unique challenge. Abu et al. measured the strength between...forth by Reynolds and 34 others (Reynolds, 1979 ). The pertinent question is the following: should brackets be chemically bonded to zirconia...conditioned with a new silane coupling agent. Eur J Orthod. 2013 Feb;35(1):103-9. 40 Giannini M, Soares CJ, de Carvalho RM. Ultimate tensile

Update on dental nanocomposites.

PubMed

Chen, M-H

2010-06-01

Dental resin-composites are comprised of a photo-polymerizable organic resin matrix and mixed with silane-treated reinforcing inorganic fillers. In the development of the composites, the three main components can be modified: the inorganic fillers, the organic resin matrix, and the silane coupling agents. The aim of this article is to review recent studies of the development of dental nanocomposites and their clinical applications. In nanocomposites, nanofillers are added and distributed in a dispersed form or as clusters. For increasing the mineral content of the tooth, calcium and phosphate ion-releasing composites and fluoride-releasing nanocomposites were developed by the addition of DCPA-whiskers or TTCP-whiskers or by the use of calcium fluoride or kaolinite. For enhancing mechanical properties, nanocomposites reinforced with nanofibers or nanoparticles were investigated. For reducing polymerization shrinkage, investigators modified the resin matrix by using methacrylate and epoxy functionalized nanocomposites based on silsesquioxane cores or epoxy-resin-based nanocomposites. The effects of silanization were also studied. Clinical consideration of light-curing modes and mechanical properties of nanocomposites, especially strength durability after immersion, was also addressed.

Mesoporous silicas with covalently immobilized β-cyclodextrin moieties: synthesis, structure, and sorption properties

NASA Astrophysics Data System (ADS)

Roik, Nadiia V.; Belyakova, Lyudmila A.; Trofymchuk, Iryna M.; Dziazko, Marina O.; Oranska, Olena I.

2017-09-01

Mesoporous silicas with chemically attached macrocyclic moieties were successfully prepared by sol-gel condensation of tetraethyl orthosilicate and β-cyclodextrin-silane in the presence of a structure-directing agent. Introduction of β-cyclodextrin groups into the silica framework was confirmed by the results of IR spectral, thermogravimetric, and quantitative chemical analysis of surface compounds. The porous structure of the obtained materials was characterized by nitrogen adsorption-desorption measurements, powder X-ray diffraction, transmission electron microscopy, and dynamic light scattering. It was found that the composition of the reaction mixture used in β-cyclodextrin-silane synthesis significantly affects the structural parameters of the resulting silicas. The increase in (3-aminopropyl)triethoxysilane as well as the coupling agent content in relation to β-cyclodextrin leads ultimately to the lowering or complete loss of hexagonal arrangement of pore channels in the synthesized materials. Formation of hexagonally ordered mesoporous structure was observed at molar composition of the mixture 0.049 TEOS:0.001 β-CD-silane:0.007 CTMAB:0.27 NH4OH:7.2 H2O and equimolar ratio of components in β-CD-silane synthesis. The sorption of alizarin yellow on starting silica and synthesized materials with chemically attached β-cyclodextrin moieties was studied in phosphate buffer solutions with pH 7.0. Experimental results of the dye equilibrium sorption were analyzed using Langmuir, Freundlich, and Redlich-Peterson isotherm models. It was proved that the Redlich-Peterson isotherm model is the most appropriate for fitting the equilibrium sorption of alizarin yellow on parent silica with hexagonally arranged mesoporous structure as well as on modified one with chemically immobilized β-cyclodextrin groups. [Figure not available: see fulltext.

Catalytic Dehydrogenative Coupling of Hydrosilanes with Alcohols for the Production of Hydrogen On-demand: Application of a Silane/Alcohol Pair as a Liquid Organic Hydrogen Carrier.

PubMed

Ventura-Espinosa, David; Carretero-Cerdán, Alba; Baya, Miguel; García, Hermenegildo; Mata, Jose A

2017-08-10

The compound [Ru(p-cym)(Cl) 2 (NHC)] is an effective catalyst for the room-temperature coupling of silanes and alcohols with the concomitant formation of molecular hydrogen. High catalyst activity is observed for a variety of substrates affording quantitative yields in minutes at room temperature and with a catalyst loading as low as 0.1 mol %. The coupling reaction is thermodynamically and, in the presence of a Ru complex, kinetically favourable and allows rapid molecular hydrogen generation on-demand at room temperature, under air, and without any additive. The pair silane/alcohol is a potential liquid organic hydrogen carrier (LOHC) for energy storage over long periods in a safe and secure way. Silanes and alcohols are non-toxic compounds and do not require special handling precautions such as high pressure or an inert atmosphere. These properties enhance the practical applications of the pair silane/alcohol as a good LOHC in the automotive industry. The variety and availability of silanes and alcohols permits a pair combination that fulfils the requirements for developing an efficient LOHC. © 2017 Wiley-VCH Verlag GmbH & Co. KGaA, Weinheim.

Cytocompatibility and Mechanical Properties of Short Phosphate Glass Fibre Reinforced Polylactic Acid (PLA) Composites: Effect of Coupling Agent Mediated Interface

PubMed Central

Hasan, Muhammad Sami; Ahmed, Ifty; Parsons, Andrew; Walker, Gavin; Scotchford, Colin

2012-01-01

In this study three chemical agents Amino-propyl-triethoxy-silane (APS), sorbitol ended PLA oligomer (SPLA) and Hexamethylene diisocyanate (HDI) were identified to be used as coupling agents to react with the phosphate glass fibre (PGF) reinforcement and the polylactic acid (PLA) polymer matrix of the composite. Composites were prepared with short chopped strand fibres (l = 20 mm, ϕ = 20 µm) in a random arrangement within PLA matrix. Improved, initial composite flexural strength (~20 MPa) was observed for APS treated fibres, which was suggested to be due to enhanced bonding between the fibres and polymer matrix. Both APS and HDI treated fibres were suggested to be covalently linked with the PLA matrix. The hydrophobicity induced by these coupling agents (HDI, APS) helped to resist hydrolysis of the interface and thus retained their mechanical properties for an extended period of time as compared to non-treated control. Approximately 70% of initial strength and 65% of initial modulus was retained by HDI treated fibre composites in contrast to the control, where only ~50% of strength and modulus was retained after 28 days of immersion in PBS at 37 °C. All coupling agent treated and control composites demonstrated good cytocompatibility which was comparable to the tissue culture polystyrene (TCP) control, supporting the use of these materials as coupling agent’s within medical implant devices. PMID:24955744

Microstructure and electrochemical behavior of cerium conversion coating modified with silane agent on magnesium substrates

NASA Astrophysics Data System (ADS)

Lei, Li; Shi, Jing; Wang, Xin; Liu, Dan; Xu, Haigang

2016-07-01

The cerium conversion coating with and without different concentrations of silane agent bis-(γ-triethoxysilylpropyl)-tetrasulfide (BTESPT) modification is obtained on magnesium alloys. Detailed properties of the coatings and the role of BTESPT as an additive are studied and followed with careful discussion. The coating morphology, wettability, chemical composition and corrosion resistance are characterized by scanning electronic microscope (SEM), water contact-angle, X-ray photoelectron spectroscopy (XPS), potentiodynamic measurements and electrochemical impedance spectroscopy (EIS). The electrochemical behavior of the coatings is investigated using EIS. The results indicate that the coating morphology and composition can be controlled by changing silane concentration. The combination of cerium ions and silane molecules could promote the formation of more homogenous and higher hydrophobic coating. The coating turns to be more compact and the adhesive strength between the coating and the magnesium substrate are strongly improved with the formation of Sisbnd Osbnd Si and Sisbnd Osbnd M chemical bonds. The optimum corrosion resistance of the coating in the corrosive media is obtained by 25 ml L-1 BTESPT modification. This whole study implies that the cerium conversion coating modified with certain silane agent deserves cautiousness before its application for corrosion resistance.

Superhydrophobic diatomaceous earth

DOEpatents

Simpson, John T [Clinton, TN; D& #x27; Urso, Brian R [Clinton, TN

2012-07-10

A superhydrophobic powder is prepared by coating diatomaceous earth (DE) with a hydrophobic coating on the particle surface such that the coating conforms to the topography of the DE particles. The hydrophobic coating can be a self assembly monolayer of a perfluorinated silane coupling agent. The DE is preferably natural-grade DE where organic impurities have been removed. The superhydrophobic powder can be applied as a suspension in a binder solution to a substrate to produce a superhydrophobic surface on the substrate.

Morphology of self assembled monolayers using liquid phase reaction on silica and their effect on the morphology of adsorbed insulin

NASA Astrophysics Data System (ADS)

Sharma, Indu; Pattanayek, Sudip K.; Aggarwal, Varsha; Ghosh, Subhasis

2017-05-01

The effect of roughness of two different categories of self-assembled monolayers (SAMs) with propyl amine and propyl groups respectively on the morphology of adsorbed insulin is observed. SAMs are obtained by liquid phase reaction of silica with organo silane coupling agents (SCA). The influence of the morphology and physical characteristics of the SAMs on the reaction time and concentration of the modifiers are explored. We have tested three SCA containing propyl amine with varying groups linked to Si present on it. In addition, we have used a silane coupling agent to prepare SAM of methyl head group. The approach of these molecules towards the surface depends on the head group and the groups linked to Si of the SCA. The morphology of the surfaces is analysed using power spectral density distribution (PSD), skewness, ellipsometry thickness and surface energy. Both chemical nature and physical morphology of the adsorbent influence the morphology of the adsorbed insulin. In general, a low number of aggregates of big size are formed on the surfaces obtained from low concentration of SAMs, while a higher number but of smaller size of aggregates are formed over surfaces obtained from 1% concentration of SAMs modifiers. The peak to valley ratio of the aggregates of insulin is strongly influenced by the size of grains of SCA over the adsorbent.

Surface modification of silicon carbide with silane coupling agent and hexadecyl iodiele

NASA Astrophysics Data System (ADS)

Shang, Xujing; Zhu, Yumei; Li, Zhihong

2017-02-01

In this paper, two kinds of silane coupling agents, namely 3-aminopropyl triethoxysilane (KH550) and 3-mercaptopropyl trimethoxysilane (KH590), were adopted as preliminary modifiers to improve the hydrophobic surface properties of silicon carbide (SiC) powder for the first step. The factors that influence the modification effects were investigated by measuring the contact angle. The results showed that KH590 has a better effect than KH550 for the hydrophobic modification of SiC, and the contact angle improved most after SiC powder was reacted with 0.3 g KH590 at 75 °C in aqueous/alcohol solution for 4 h. On account of further enhancement of hydrophobicity, the study was focused on utilizing nucleophilic substitution between KH590 and hexadecyl iodiele to extend the length of alkyl chain. Compared with using KH590 alone, SiC powder modified by KH590 and hexadecyl iodiele showed better water resistance with an increase of contact angle from 106.8° to 127.5°. The Fourier transform infrared spectroscopy (FT-IR) and X-ray photoelectron spectra (XPS) as well as X-ray diffraction (XRD) analysis results showed that KH550/KH590 and hexadecyl iodiele can be covalently bonded to the surface of SiC powder without altering its crystal configuration. This methodology may provide a new way of the modification of inorganic materials in further.

Mechanical properties of chemically modified Sansevieria trifasciata/natural rubber/high density polyethylene (STF/NR/HDPE) composites: Effect of silane coupling agent

NASA Astrophysics Data System (ADS)

Zakaria, Nurzam Ezdiani; Baharum, Azizah; Ahmad, Ishak

2018-04-01

The main objective of this research is to study the effects of chemical modification on the mechanical properties of treated Sansevieria trifasciata fiber/natural rubber/high density polyethylene (TSTF/NR/HDPE) composites. Processing of STF/NR/HDPE composites was done by using an internal mixer. The processing parameters used were 135°C for temperature and a mixing rotor speed of 55 rpm for 15 minutes. Filler loading was varied from 10% to 40% of STF and the fiber size used was 125 µm. The composite blends obtained then were pressed with a hot press machine to get test samples of 1 mm and 3 mm of thickness. Samples were evaluated via tensile tests, Izod impact test and scanning electron microscopy (SEM). Results showed that tensile strength and strain value decreased while tensile modulus increased when filler loading increased. Impact strength increased when filler loading increased and began to decrease after 10% of filler amount for treated composites. For untreated composites, impact strength began to decrease after 20% of filler loading. Chemical modification by using silane coupling agent has improved certain mechanical properties of the composites such as tensile strength, strain value and tensile modulus. Adding more amount of filler will also increase the viscosity and the stiffness of the materials.

Morphology and water resistance of mixed silane films of bis[3-(triethoxysilyl) propyl]tetrasulfide and bis-[trimethoxysilylpropyl]amine

DOE Office of Scientific and Technical Information (OSTI.GOV)

Pan, Guirong; Schaefer, Dale W.; van Ooij, Wim J.

2010-12-03

Functional organosilanes are powerful interface-active agents that find applications as adhesion promoters as well as optical, dielectric and protective coatings. Bis-silanes are of particular interest because they are highly crosslinked leading to very robust films. In almost all applications, the water resistance of the films is a critical performance measure. Here we use neutron reflectivity to address the effect of bridging group on the hydrothermal response of bis-silane films prepared using bis[3-(triethoxysilyl) propyl]tetrasulfide and bis-[trimethoxysilylpropyl]amine. Neat and mixed films are examined as-prepared, after exposure to water vapor and then in the re-dried state. The bridging group is the key factormore » that controls the morphology and water resistance of silane films. Although bis-sulfur silane is not as condensed as bis-amino silane, bis-sulfur swells less in water because of the hydrophobic nature of bridging group. The reflectivity of bis-sulfur silane film is reversible after room-temperature water conditioning but not at 80 C, indicating chemical alternation of the film at 80 C. The water resistance of mixed silane is roughly that of both components weighted by their volume fraction. But based on the enhanced shrinkage that occurs following water-vapor conditioning of the mixed film, condensation is accelerated in the mixed silane. Regarding the precursor solution, bis-amino silane may act as a catalyst in the hydrolysis of bis-sulfur silane leading to more silanols in the solution and further condensation in the film. Variation in the structure normal to the substrate is also examined by swelling the film with d-nitrobenzene, a non-reacting swelling agent.« less

Dehydrogenative coupling of silanes with alcohols catalyzed by Cu3(BTC)2.

PubMed

Dhakshinamoorthy, Amarajothi; Concepcion, Patricia; Garcia, Hermenegildo

2016-02-14

Cu3(BTC)2 is an efficient and reusable heterogeneous catalyst for the dehydrogenative coupling of silanes with alcohols. Activity data and CO adsorption suggest that Cu(II) and in situ generated Cu(I) are the active species. Other MOFs such as Fe(BTC), MIL-101(Cr) and UiO-66(Zr) are unable to promote this cross-coupling.

Silanization of boron nitride nanosheets (BNNSs) through microfluidization and their use for producing thermally conductive and electrically insulating polymer nanocomposites

DOE Office of Scientific and Technical Information (OSTI.GOV)

Seyhan, A.Tuğrul, E-mail: atseyhan@anadolu.edu.tr; Composite Materials Manufacturing Science Laboratory; Göncü, Yapıncak

Chemical exfoliation of boron nitride nanosheets (BNNSs) from large flakes of specially synthesized micro-sized hexagonal boron nitride (h-BN) ceramics was carried out through microfluidization. The surface of BNNSs obtained was then functionalized with vinyl-trimethoxy silane (VTS) coupling agent through microfluidization once again in an effort to make them compatible with organic materials, especially those including polymers. The morphology of BNNSs with and without silane treatment was then systematically characterized by conducting various different analytical techniques, including Thermogravimetric analysis (TGA), X-ray diffraction (XRD), Scanning Electron Microscopy (SEM), Bright field Transmission Electron Microscopy (BF-TEM), Contact angle analyzer (CAA), Particle size analyzer (PSA)more » and Fourier Transmission Infrared (FTIR) spectroscopy attached with attenuated total reflectance (ATR) module. As a result, the silane treatment was determined to be properly and successfully carried out and to give rise to the irregularity of large flakes of the BNNSs by folding back their free edges upon themselves, which in turn assists in inducing further exfoliation of the few-layered nanosheets. To gain more insight into the effectiveness of the surface functionalization, thermal conductivity of polypropylene (PP) nanocomposites containing different amounts (1 wt% and 5 wt%) of BNNSs with and without silane treatment was experimentally investigated. Regardless of the weight content, PP nanocomposites containing silanized BNNSs were found to exhibit high thermal conductivity compared to PP nanocomposites containing BNNSs without silane treatment. It was concluded that microfluidization possesses the robustness to provide a reliable product quality, whether in small or large quantities, in a very time effective manner, when it comes to first exfoliating two-dimensional inorganic materials into few layered sheets, and functionalizing the surface of these sheets afterwards to make it possible to utilize them as promising filler constituent in manufacturing thermally conductive and electrically insulating polymer nanocomposites that could be considered as whole or a part of a heat-releasing device.« less

Silanization of boron nitride nanosheets (BNNSs) through microfluidization and their use for producing thermally conductive and electrically insulating polymer nanocomposites

NASA Astrophysics Data System (ADS)

Seyhan, A. Tuğrul; Göncü, Yapıncak; Durukan, Oya; Akay, Atakan; Ay, Nuran

2017-05-01

Chemical exfoliation of boron nitride nanosheets (BNNSs) from large flakes of specially synthesized micro-sized hexagonal boron nitride (h-BN) ceramics was carried out through microfluidization. The surface of BNNSs obtained was then functionalized with vinyl-trimethoxy silane (VTS) coupling agent through microfluidization once again in an effort to make them compatible with organic materials, especially those including polymers. The morphology of BNNSs with and without silane treatment was then systematically characterized by conducting various different analytical techniques, including Thermogravimetric analysis (TGA), X-ray diffraction (XRD), Scanning Electron Microscopy (SEM), Bright field Transmission Electron Microscopy (BF-TEM), Contact angle analyzer (CAA), Particle size analyzer (PSA) and Fourier Transmission Infrared (FTIR) spectroscopy attached with attenuated total reflectance (ATR) module. As a result, the silane treatment was determined to be properly and successfully carried out and to give rise to the irregularity of large flakes of the BNNSs by folding back their free edges upon themselves, which in turn assists in inducing further exfoliation of the few-layered nanosheets. To gain more insight into the effectiveness of the surface functionalization, thermal conductivity of polypropylene (PP) nanocomposites containing different amounts (1 wt% and 5 wt%) of BNNSs with and without silane treatment was experimentally investigated. Regardless of the weight content, PP nanocomposites containing silanized BNNSs were found to exhibit high thermal conductivity compared to PP nanocomposites containing BNNSs without silane treatment. It was concluded that microfluidization possesses the robustness to provide a reliable product quality, whether in small or large quantities, in a very time effective manner, when it comes to first exfoliating two-dimensional inorganic materials into few layered sheets, and functionalizing the surface of these sheets afterwards to make it possible to utilize them as promising filler constituent in manufacturing thermally conductive and electrically insulating polymer nanocomposites that could be considered as whole or a part of a heat-releasing device.

Interpretation of Mechanical and Thermal Properties of Heavy Duty Epoxy Based Floor Coating Doped by Nanosilica

NASA Astrophysics Data System (ADS)

Nikje, M. M. Alavi; Khanmohammadi, M.; Garmarudi, A. Bagheri

Epoxy-nano silica composites were prepared using Bisphenol-A epoxy resin (Araldite® GY 6010) resin obtained from in situ polymerization or blending method. SiO2 nanoparticles were pretreated by a silan based coupling agent. Surface treated nano silica was dispersed excellently by mechanical and ultrasonic homogenizers. A dramatic increase in the interfacial area between fillers and polymer can significantly improve the properties of the epoxy coating product such as tensile, elongation, abrasion resistance, etc.

Fabrication of nanocomposites by collagen templated synthesis of layered double hydroxides assisted by an acrylic silane coupling agent

NASA Astrophysics Data System (ADS)

Sun, Yanqing; Zhou, Yuming; Wang, Zhiqiang; Ye, Xiaoyun

2009-02-01

The purpose of this study was to control the fabrication of nanocomposites at the nanoscale interface by collagen templated synthesis of Zn-Al layered double hydroxides (LDHs) assisted by γ-methacryloxypropyl trimethoxy silane (KH570) with further treatment of graft polymerization. The results show that collagen directs the growth of LDHs into curved nanorods by length of 300 nm in perfect consistency with collagen chain in both the size and flexility under the essential hydrophobic environment on the solid surface provided by KH570. The nanorods are aggregated into thin curved platelets due to strong interaction between collagen molecules themselves and strong interaction between collagen and LDH sheets. By further treatment of graft polymerization, the adjacent curved platelets encircle into numerous hollows via chemical linkage, achieving polyporous nanocomposites. Nanohybrid materials with this structure are especially interesting for applications as biosensors or supported catalysis.

Elusive silane-alane complex [Si-H⋅⋅⋅Al]: isolation, characterization, and multifaceted frustrated Lewis pair type catalysis.

PubMed

Chen, Jiawei; Chen, Eugene Y-X

2015-06-01

The super acidity of the unsolvated Al(C6F5)3 enabled isolation of the elusive silane-alane complex [Si-H⋅⋅⋅Al], which was structurally characterized by spectroscopic and X-ray diffraction methods. The Janus-like nature of this adduct, coupled with strong silane activation, effects multifaceted frustrated-Lewis-pair-type catalysis. When compared with the silane-borane system, the silane-alane system offers unique features or clear advantages in the four types of catalytic transformations examined in this study, including: ligand redistribution of tertiary silanes into secondary and quaternary silanes, polymerization of conjugated polar alkenes, hydrosilylation of unactivated alkenes, and hydrodefluorination of fluoroalkanes. © 2015 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Effects of three silane primers and five adhesive agents on the bond strength of composite material for a computer-aided design and manufacturing system.

PubMed

Shinohara, Ayano; Taira, Yohsuke; Sakihara, Michino; Sawase, Takashi

2018-01-01

Objective The objective of this study was to evaluate the effects of combinations of silane primers and adhesive agents on the bond strength of a composite block for a computer-aided design and manufacturing system. Material and Methods Three silane primers [Clearfil Ceramic Primer (CP), Super-Bond PZ Primer (PZ), and GC Ceramic Primer II (GP)] were used in conjunction with five adhesive agents [G-Premio Bond (P-Bond), Repair Adhe Adhesive (R-Adhesive), Super-Bond D-Liner Dual (SB-Dual), Super-Bond C&B (SB-Self), and SB-Dual without tributylborane derivative (SB-Light)]. The surface of a composite block (Gradia Block) was ground with silicon carbide paper. After treatment with a silane primer, a adhesive agent was applied to each testing specimen. The specimens were then bonded with a light-curing resin composite. After 24 h, the shear bond strength values were determined and compared using a post hoc test (α=0.05, n=8/group). We also prepared control specimens without primer (No primer) and/or without adhesive agent (No adhesive). Results PZ/SB-Dual and GP/SB-Dual presented the highest bond strength, followed by GP/P-Bond, CP/SB-Dual, CP/R-Adhesive, No primer/SB-Dual, GP/R-Adhesive, CP/P-Bond, No primer/R-Adhesive, PZ/R-Adhesive, CP/SB-Self, PZ/P-Bond, PZ/SB-Self, and GP/SB-Self in descending order of bond strength. No primer/P-Bond, No primer/SB-Self, and all specimens in the SB-Light and No adhesive groups presented the lowest bond strengths. Conclusion A dual-curing adhesive agent (SB-Dual) containing a tributylborane derivative in combination with a silane primer (GP or PZ) presents a greater bond strength between the composite block and the repairing resin composite than the comparators used in the study.

Effects of three silane primers and five adhesive agents on the bond strength of composite material for a computer-aided design and manufacturing system

PubMed Central

2018-01-01

Abstract Objective The objective of this study was to evaluate the effects of combinations of silane primers and adhesive agents on the bond strength of a composite block for a computer-aided design and manufacturing system. Material and Methods Three silane primers [Clearfil Ceramic Primer (CP), Super-Bond PZ Primer (PZ), and GC Ceramic Primer II (GP)] were used in conjunction with five adhesive agents [G-Premio Bond (P-Bond), Repair Adhe Adhesive (R-Adhesive), Super-Bond D-Liner Dual (SB-Dual), Super-Bond C&B (SB-Self), and SB-Dual without tributylborane derivative (SB-Light)]. The surface of a composite block (Gradia Block) was ground with silicon carbide paper. After treatment with a silane primer, a adhesive agent was applied to each testing specimen. The specimens were then bonded with a light-curing resin composite. After 24 h, the shear bond strength values were determined and compared using a post hoc test (α=0.05, n=8/group). We also prepared control specimens without primer (No primer) and/or without adhesive agent (No adhesive). Results PZ/SB-Dual and GP/SB-Dual presented the highest bond strength, followed by GP/P-Bond, CP/SB-Dual, CP/R-Adhesive, No primer/SB-Dual, GP/R-Adhesive, CP/P-Bond, No primer/R-Adhesive, PZ/R-Adhesive, CP/SB-Self, PZ/P-Bond, PZ/SB-Self, and GP/SB-Self in descending order of bond strength. No primer/P-Bond, No primer/SB-Self, and all specimens in the SB-Light and No adhesive groups presented the lowest bond strengths. Conclusion A dual-curing adhesive agent (SB-Dual) containing a tributylborane derivative in combination with a silane primer (GP or PZ) presents a greater bond strength between the composite block and the repairing resin composite than the comparators used in the study. PMID:29742254

Lanthanum tricyanide-catalyzed acyl silane-ketone benzoin additions.

PubMed

Tarr, James C; Johnson, Jeffrey S

2009-09-03

Lanthanum tricyanide efficiently catalyzes a benzoin-type coupling between acyl silanes and ketones. Yields range from moderate to excellent over a broad substrate scope encompassing aryl, alkyl, electron-rich, and sterically hindered ketones.

Effects of tributylborane-activated adhesive and two silane agents on bonding computer-aided design and manufacturing (CAD/CAM) resin composite.

PubMed

Shinohara, Ayano; Taira, Yohsuke; Sawase, Takashi

2017-10-01

The present study was conducted to evaluate the effects of an experimental adhesive agent [methyl methacrylate-tributylborane liquid (MT)] and two adhesive agents containing silane on the bonding between a resin composite block of a computer-aided design and manufacturing (CAD/CAM) system and a light-curing resin composite veneering material. The surfaces of CAD/CAM resin composite specimens were ground with silicon-carbide paper, treated with phosphoric acid, and then primed with either one of the two silane agents [Scotchbond Universal Adhesive (SC) and GC Ceramic Primer II (GC)], no adhesive control (Cont), or one of three combinations (MT/SC, MT/GC, and MT/Cont). A light-curing resin composite was veneered on the primed CAD/CAM resin composite surface. The veneered specimens were subjected to thermocycling between 4 and 60 °C for 10,000 cycles, and the shear bond strengths were determined. All data were analyzed using analysis of variance and a post hoc Tukey-Kramer HSD test (α = 0.05, n = 8). MT/SC (38.7 MPa) exhibited the highest mean bond strengths, followed by MT/GC (30.4 MPa), SC (27.9 MPa), and MT/Cont (25.7 MPa), while Cont (12.9 MPa) and GC (12.3 MPa) resulted in the lowest bond strengths. The use of MT in conjunction with a silane agent significantly improved the bond strength. Surface treatment with appropriate adhesive agents was confirmed as a prerequisite for veneering CAD/CAM resin composite restorations.

The Study of the Interaction between Silica Filler and Silicone Rubber

NASA Astrophysics Data System (ADS)

Liu, Jiesheng; Gong, Xiaoqiang; Zhang, Rongtang

2018-01-01

The interaction between silica filler and silicone rubber was studied by swelling ratio, Kraus curve and crosslinking density test. The results showed that lower values of Vro/Vrf and swelling ratio in modified filler system suggests good filler-matrix interactions. The composites with silane coupling agents show higher crosslink-density compared that of untreated ones. In the light of the above statement, it can be concluded that modification of filler is the crucial factor in creating a good interaction between the filler and silicone rubber.

Proceedings of the Critical Review: Techniques for the Characterization of Composite Materials, held Cambridge, Massachusetts, 8-10 June 1981.

DTIC Science & Technology

1982-05-01

systems were used in this study : SP2)J/E-glass and Fiberite 934/ Kevlar 49. The SP250 resin is a diglycidvl ether of bis;,hennl A (DGEBA)/Epoxy...silane coupling agents to the epoxy resin, and the influence of water pH were particularly studied . The theory of generalized fracture mechanics is...the absorbed moisture water molecules are much more restricted in motion than for free water . Although further laboratory studies are needed to better

Laboratory and field performance of silane anti-strip agent

DOT National Transportation Integrated Search

1986-11-01

A previous ADOT research project resulted in strong evidence that the use of organo-silane as an asphalt additive was very effective in preventing stripping in asphalt concrete pavements. A test section approximately 2800 ft long and 12 ft wide incor...

Lanthanum Tricyanide-Catalyzed Acyl Silane-Ketone Benzoin Additions

PubMed Central

Tarr, James C.; Johnson, Jeffrey S.

2009-01-01

Lanthanum tricyanide efficiently catalyzes a benzoin-type coupling between acyl silanes and ketones. Yields range from moderate to excellent over a broad substrate scope encompassing aryl, alkyl, electron-rich, and sterically hindered ketones. PMID:19655731

Safety assessment of nanoparamagnetic contrast agents with different coatings for molecular MRI

NASA Astrophysics Data System (ADS)

Azizian, Gholamreza; Riyahi-Alam, Nader; Haghgoo, Soheila; Saffari, Mojtaba; Zohdiaghdam, Reza; Gorji, Ensieh

2013-04-01

Despite the wide application of gadolinium as a contrast agent for magnetic resonance imaging (MRI), there is a serious lack of information on its toxicity. Gadolinium and gadolinium oxide (Gd-oxide) are used as contrast agents for magnetic resonance imaging (MRI). There are methods for reducing toxicity of these materials, such as core nanoparticles coating or conjugating. Therefore, for toxicity evaluation, we compared the viability of commercial contrast agents in MRI (Gd-DTPA) and three nanoparticles with the same core Gd2O3 and small particulate gadolinium oxide or SPGO (< 40 nm) but different coatings of diethyleneglycol (DEG) as Gd2O3-DEG and methoxy polyethylene glycol-silane (mPEG-silane: 550 and 2000 Dalton) as SPGO-mPEG-silane550 and SPGO-mPEG-silane2000, respectively, in the SK-MEL3 cell line, by light microscopy, MTT assay using 3-[4,5-dimethylthiazol-2-yl]-2,5-diphenyl tetrazolium bromide, and the LDH assay detecting lactate dehydrogenase activity. The viability values were not statistically different between the three nanoparticles and Gd-DTPA. The MTT and LDH assay results showed that Gd2O3-DEG nanoparticles were more toxic than Gd-DTPA and other nanoparticles. Also, SPGO-mPEG-silane2000 was more biocompatible than other nanoparticles. The obtained results did not show any significant increase in cytotoxicity of the nanoparticles and Gd-DTPA, neither dose-dependent nor time-dependent. Therefore, DEG and PEG, due to their considerable properties and irregular sizes (different molecular weights), were selected as the useful surface covering materials of nanomagnetic particles that could reveal noticeable relaxivity and biocompatibility characteristics.

Effect of incorporation of silane in the bonding agent on the repair potential of machinable esthetic blocks

PubMed Central

Zaghloul, Hanaa; Elkassas, Dina Wafik; Haridy, Mohamed Fouad

2014-01-01

Objective: To investigate the repair potential of CAD/CAM (computer-aided design/computer-aided manufacturing) ceramic and composite blocks using a silane-containing bonding agent with different repair protocols. Materials and Methods: Twenty-four discs were constructed from CAD/CAM ceramic and composite blocks. The discs were divided into six groups according to surface pre-treatment employed; GI: Diamond stone roughening (SR), GII: SR+ silanization (SR+S), GIII: Hydrofluoric acid etching (HF), GIV: HF+ silanization (HF+S), GV: Silica coating (SC), GVI: SC+ silanization (SC+S). Silane-containing bonding agent (Single Bond Universal adhesive, 3M ESPE) was applied to the pre-treated discs. Prior to light curing, irises were cut from tygon tubes (internal diameter = 0.8 mm and height = 0.5 mm) and mounted on each treated surface. Nanofilled resin composite (Filtek Z350XT, 3M ESPE) was packed into the cylinder lumen and light-cured (n = 10). The specimens were subjected to microshear bond strength testing (μ-SBS) using universal testing machine. Failure modes of the fractured specimens were analyzed using field emission scanning electron microscope (FESEM). Eight representative discs were prepared to analyze the effect of surface treatments on surface topography using FESEM. μ-SBS results were analyzed using ANOVA and Tukeys post-hoc test. Results: Three-way ANOVA results showed that the materials, surface pre-treatment protocols, and silanization step had a statistically significant effect on the mean μ-SBS values at P ≤ 0.001. For ceramic discs, the groups were ranked; GIV (24.45 ± 7.35)> GVI ((20.18 ± 2.84)> GV (7.14 ± 14)= GII (6.72 ± 1.91)=GI (6.34 ± 2.21)=GIII (5.72 ± 2.18). For composite discs, groups were ranked; GI (24.98 ± 7.69)=GVI (24.84 ± 7.00) >GII (15.85 ± 5.29) =GV (14.65 ± 4.5)= GIV (14.24 ± 2.95)≥ GIII ((9.37 ± 2.78). Conclusion: The additional silanization step cannot be omitted if the repair protocol comprises of either hydrofluoric acid etching or silica coating for both CAD/CAM esthetic restorative materials. However, this step can be suppressed by using silane-containing adhesive with diamond stone roughened repair protocol. PMID:24966745

A new organofunctional ethoxysilane self-assembly monolayer for promoting adhesion of rubber to aluminum.

PubMed

Wang, Fang; Xu, Juan; Luo, Heyi; Wang, Jinggang; Wang, Qian

2009-10-12

Practical adhesion of rubber to aluminum is measured for various aluminum silanization treatments. In this study, 6-(3-triethoxysilylpropylamino)-1,3,5-triazine-2,4-dithiol (TES) was used as the coupling agent for preparing self-assembly monolayers (SAMs) on an aluminum surface. The structure and chemical composition of the SAMs were analyzed using Fourier transform infra-red spectroscopy (FT-IR) and X-ray photoelectron spectroscopy (XPS). The changes in the surface features of the aluminum surface due to TES treatment were investigated by atomic force microscopy (AFM). The adhesive properties of the silanized aluminum surface and EPDM rubber have been evaluated by a T-peel strength test. The results suggested that the Si-O-Al bonding at aluminum TES interface existed and a TES self-assembly monolayer was formed on the aluminum surface. More than 6.0 KN/m adhesion strength is obtained when the aluminum is silanized with 2.5 mmol/dm(3) TES, cured at 160 degrees C and vulcanized with EPDM rubber at 160 degrees C for 30 min. It is suggested that the TES self-assembly monolayer is bound to aluminum through its ethoxysilyl functional group, and the thiol function group is strongly crosslinked to EPDM rubber, respectively.

Organic-Inorganic Hydrophobic Nanocomposite Film with a Core-Shell Structure

PubMed Central

Liu, Peng; Chen, Ying; Yu, Zhiwu

2016-01-01

A method to prepare novel organic-inorganic hydrophobic nanocomposite films was proposed by a site-specific polymerization process. The inorganic part, the core of the nanocomposite, is a ternary SiO2–Al2O3–TiO2 nanoparticles, which is grafted with methacryloxy propyl trimethoxyl silane (KH570), and wrapped by fluoride and siloxane polymers. The synthesized samples are characterized by transmission electron microscopy (TEM), Fourier transform infrared (FTIR) spectrscopy, X-ray diffractometry (XRD), contact angle meter (CA), and scanning electron microscope (SEM). The results indicate that the novel organic-inorganic hydrophobic nanocomposite with a core-shell structure was synthesized successfully. XRD analysis reveals the nanocomposite film has an amorphous structure, and FTIR analysis indicates the nanoparticles react with a silane coupling agent (methacryloxy propyl trimethoxyl silane KH570). Interestingly, the morphology of the nanoparticle film is influenced by the composition of the core. Further, comparing with the film synthesized by silica nanoparticles, the film formed from SiO2–Al2O3–TiO2 nanoparticles has higher hydrophobic performance, i.e., the contact angle is greater than 101.7°. In addition, the TEM analysis reveals that the crystal structure of the particles can be changed at high temperatures. PMID:28774141

Controlling surface property of K2SiF6:Mn4+ for improvement of lighting-emitting diode reliability

NASA Astrophysics Data System (ADS)

Kim, Juseong; Jang, Inseok; Song, Gwang Yeom; Kim, Wan-Ho; Jeon, Sie-Wook; Kim, Jae-Pil

2018-05-01

The surface property of moisture-sensitive K2SiF6:Mn4+ (KSF) as a red-emitting phosphor was controlled through dry-type surface modification in order to improve the photo-performance and reliability of lighting-emitting diode (LED). The phosphor surface was modified with silane coupling agents having different carbon chain length by plasma-assisted method. Comparing between as-prepared and modified KSF, water-resistance and photo-emission efficiency were enhanced due to the formation of hydrophobic shell and the elimination of surface quenching sites. Moreover, the dispersibility of phosphor was increased as increasing the carbon chain length of silane because the interfacial affinity between phosphor and encapsulant was improved. After fabricating LED device, the enhancement of photo-performance and long-term reliability could be successfully achieved in LED device with modified phosphor. It is attributed to that the degradation of phosphor efficiency by moisture was suppressed and heat dissipation in LED PKG was improved through the surface modification.

Chemically modified amino porphyrin/TiO2 for the degradation of Acid Black 1 under day light illumination

NASA Astrophysics Data System (ADS)

Krishnakumar, Balu; Balakrishna, Avula; Arranja, Cláudia T.; Dias, Carlos M. F.; Sobral, Abilio J. F. N.

2017-04-01

In this paper, for the first time, chemically modified 5,10,15,20-meso-tetra-(para-amino)-phenyl-porphyrin/TiO2 (TPAPP/TiO2) was prepared and used for the degradation of an azo dye Acid Black 1 (AB 1) under direct sunlight. Initially, TiO2 was prepared by sol-gel method. Before making a TPAPP/TiO2 composite, the surface modification of TiO2 was carried out with glycidoxypropyltrimethoxy silane (GPTMS) which acts as a coupling agent. This is an epoxy terminated silane and could easily bond to the amino group of TPAPP through epoxy cleavage. The formation of TPAPP/TiO2 was confirmed by different characterization techniques such as FT-IR, XRD, SEM and DRS. The photocatalytic activity of TiO2 was highly influenced by TPAPP. A mechanism was proposed for AB 1 degradation by TPAPP/TiO2 under sun light.

Chemically modified amino porphyrin/TiO2 for the degradation of Acid Black 1 under day light illumination.

PubMed

Krishnakumar, Balu; Balakrishna, Avula; Arranja, Cláudia T; Dias, Carlos M F; Sobral, Abilio J F N

2017-04-05

In this paper, for the first time, chemically modified 5,10,15,20-meso-tetra-(para-amino)-phenyl-porphyrin/TiO 2 (TPAPP/TiO 2 ) was prepared and used for the degradation of an azo dye Acid Black 1 (AB 1) under direct sunlight. Initially, TiO 2 was prepared by sol-gel method. Before making a TPAPP/TiO 2 composite, the surface modification of TiO 2 was carried out with glycidoxypropyltrimethoxy silane (GPTMS) which acts as a coupling agent. This is an epoxy terminated silane and could easily bond to the amino group of TPAPP through epoxy cleavage. The formation of TPAPP/TiO 2 was confirmed by different characterization techniques such as FT-IR, XRD, SEM and DRS. The photocatalytic activity of TiO 2 was highly influenced by TPAPP. A mechanism was proposed for AB 1 degradation by TPAPP/TiO 2 under sun light. Copyright © 2017 Elsevier B.V. All rights reserved.

Effect of an internal coating technique on tensile bond strengths of resin cements to zirconia ceramics.

PubMed

Kitayama, Shuzo; Nikaido, Toru; Maruoka, Rena; Zhu, Lei; Ikeda, Masaomi; Watanabe, Akihiko; Foxton, Richard M; Miura, Hiroyuki; Tagami, Junji

2009-07-01

This study was conducted to enhance the tensile bond strengths of resin cements to zirconia ceramics. Fifty-six zirconia ceramic specimens (Cercon Base) and twenty-eight silica-based ceramic specimens (GN-1, GN-1 Ceramic Block) were air-abraded using alumina. Thereafter, the zirconia ceramic specimens were divided into two subgroups of 28 each according to the surface pretreatment; no pretreatment (Zr); and the internal coating technique (INT). For INT, the surface of zirconia was coated by fusing silica-based ceramics (Cercon Ceram Kiss). Ceramic surfaces were conditioned with/without a silane coupling agent followed by bonding with one of two resin cements; Panavia F 2.0 (PF) and Superbond C&B (SB). After 24 hours storage in water, the tensile bond strengths were tested (n=7). For both PF and SB, silanization significantly improved the bond strength to GN-1 and INT (p<0.05). The INT coating followed by silanizaton demonstrated enhancement of bonding to zirconia ceramics.

Thermal expansion of an epoxy-glass microsphere composite

NASA Technical Reports Server (NTRS)

Price, H. L.; Burks, H. D.

1977-01-01

The thermal expansion of a composite of epoxy (diglycidyl ether of bisphenol A) and solid glass microspheres was investigated. The microspheres had surfaces which were either untreated or treated with a silicone release agent, an epoxy coupling agent, or a general purpose silane coupling agent. Both room temperature (about 300 K) and elevated temperature (about 475 K) cures were used for the epoxy. Two microsphere size ranges were used, about 50 microns, which is applicable in filled moldings, and about 125 microns, which is applicable as bond line spacers. The thermal expansion of the composites was measured from 300 to 350 K or from 300 to 500 K, depending on the epoxy cure temperature. Measurements were made on composites containing up to .6 volume fraction microspheres. Two predictive models, which required only the values of thermal expansion of the polymer and glass and their specific gravities, were tested against the experimental data. A finite element analysis was made of the thermal strain of a composite cell containing a single microsphere surrounded by a finite-thickness interface.

Studies on silicon NMR characterization and kinetic modeling of the structural evolution of siloxane-based materials and their applications in drug delivery and adsorption

NASA Astrophysics Data System (ADS)

Ambati, Jyothirmai

This dissertation presents studies of the synthetic processes and applications of siloxane-based materials. Kinetic investigations of bridged organoalkoxysilanes that are precursors to organic-inorganic hybrid polysilsesquioxanes are a primary focus. Quick gelation despite extensive cyclization is found during the polymerization of bridged silane precursors except for silanes with certain short bridges. This work is an attempt to characterize and understand some of the distinct features of bridged silanes using experimental characterization, kinetic modeling and simulation. In addition to this, the dissertation shows how the properties of siloxane-materials can be engineered for drug delivery and adsorption. The phase behavior of polymerizing mixtures is first investigated to identify the solutions that favor kinetic characterization. Microphase separation is found to cause gradual loss of NMR signal for certain initial compositions. Distortionless Enhancement by Polarization Transfer 29Si NMR is employed to identify the products of polymerization of some short-bridged silanes under no signal loss conditions. This technique requires knowing indirect 29Si-1H scalar coupling constants which sometimes cannot be measured due to second-order effects. However, the B3LYP density functional method with 6-31G basis set is found to predict accurate 29Si- 1H coupling constants of organoalkoxysilanes and siloxanes. The scalar coupling constants thus estimated are employed to resolve non-trivial coupled NMR spectra and quantitative kinetic modeling is performed using the DEPT Si NMR transients. In order to investigate the role of the organic bridging group, the structural evolution of bridged and non-bridged silanes are compared using Monte Carlo simulations. Kinetic and simulation models suggest that cyclization plays a key role right from the onset of polymerization for bridged silanes even more than in non-bridged silanes. The simulations indicate that the carbosiloxane rings formed from short-bridged precursors slow down but do not prevent gelation. The tuning of siloxane-based materials for adsorption technologies are also discussed here. In the first example, antioxidant enzyme loading is investigated as a means to reduce oxidative stress generated by silica nanoparticle drug carriers. Materials are engineered for promising enzyme loading and protection from proteolysis. Second, the potential of copper sulfate impregnation to enhance adsorption of ammonia by silica is explored by molecular simulation. KEYWORDS: Sol-gel Polymerization, Kinetic Investigation, Si NMR, Bridged Silanes, DFT Calculations.

On the mobility of iron particles embedded in elastomeric silicone matrix

NASA Astrophysics Data System (ADS)

Rabindranath, R.; Böse, H.

2013-02-01

In this contribution the rheological and magnetorheological properties of different polydimethylsiloxane (PDMS) based magnetorheological elastomers (MRE) are presented and discussed. In order to investigate the mobility of the iron particles with respect to the rheological characteristics, the iron particles were silanized with vinyltrimethoxysilane to enable a reaction between the modified particle and the cross-linking agent of the silicone elastomer. In addition, the vinyl-functionalized particles were further modified by the coupling of the superficial vinyl groups with a long-chain hydride terminated PDMS, which enables a reaction pathway with the vinyl terminated PDMS. On the other hand, the iron particles were treated with surfactants such as fatty acids, calcium and aluminum soaps, respectively, prior to vulcanization in order to increase the mobility of the iron particles in the elastomeric matrix. It was found, that both, the modification with the long-chain hydride terminated PDMS as well as the treatment with surfactants lead to an increase of the storage modulus G', the loss modulus G" and the loss factor tan δ in the magnetic field. It is concluded that both modifications, the coupling with long-chain hydride terminated PDMS as well as the treatment with surfactants, provide a greater mobility of the iron particles and hence a greater friction represented by the increase of the loss factor tan δ. Consequently it is assumed that untreated iron particles are less mobile in the rubber matrix due to covalent bonding with the silicone components, most likely due to the reaction of the hydroxyl groups on the metal surface with the silane groups of the cross-linking agent.

Effect of silica coating on fracture strength of glass-infiltrated alumina ceramic cemented to dentin.

PubMed

Xie, Haifeng; Zhu, Ye; Chen, Chen; Gu, Ning; Zhang, Feimin

2011-10-01

To examine the availability of sol-gel processed silica coating for alumina-based ceramic bonding, and determine which silica sol concentration was appropriate for silica coating. Sixty disks of In-Ceram alumina ceramic were fabricated and randomly divided into 5 main groups. The disks received 5 different surface conditioning treatments: Group Al, sandblasted; Group AlC, sandblasted + silane coupling agent applied; Groups Al20C, Al30C, and Al40C, sandblasted, silica coating via sol-gel process prepared using 20 wt%, 30 wt%, and 40 wt% silica sols, and then silane coupling agent applied. Before bonding, one-step adhesives were applied on pre-prepared ceramic surfaces of all groups. Then, 60 dentin specimens were prepared and conditioned with phosphoric acid and one-step adhesive. Ceramic disks of all groups were cemented to dentin specimens with dual-curing resin cements. Fracture strength was determined at 24 h and after 20 days of storage in water. Groups Al20C, Al30C, and Al40C revealed significantly higher fracture strength than groups Al and AlC. No statistically significant difference in fracture strength was found between groups Al and AlC, or among groups Al20C, Al30C, and Al40C. Fracture strength values of all the groups did not change after 20 days of water storage. Sol-gel processed silica coating can enhance fracture strength of In-Ceram alumina ceramic after bonding to dentin, and different silica sol concentrations produced the same effects. Twenty days of water storage did not decrease the fracture strength.

Development of high-viscosity, two-paste bioactive bone cements.

PubMed

Deb, S; Aiyathurai, L; Roether, J A; Luklinska, Z B

2005-06-01

Self-curing two-paste bone cements have been developed using methacrylate monomers with a view to formulate cements with low polymerization exotherm, low shrinkage, better mechanical properties, and improved adhesion to bone and implant surfaces. The monomers include bis-phenol A glycidyl dimethacrylate (bis-GMA), urethane dimethacrylate (UDMA) and triethylene glycol dimethacrylate (TEGDMA) as a viscosity modifier. Two-paste systems were formulated containing 60% by weight of a bioactive ceramic, hydroxyapatite. A methacroyloxy silane (A174) was used as a coupling agent due to its higher water stability in comparison to other aminosilanes to silanate the hydroxyapatite particles prior to composite formulation. A comparison of the FT-infrared spectrum of hydroxyapatite and silanated hydroxyapatite showed the presence of the carbonyl groups ( approximately 1720 cm(-1)), -C=C-( approximately 1630 cm(-1)) and Si-O- (1300-1250 cm(-1)) which indicated the availability of silane groups on the filler surface. Two methods of mixing were effected to form the bone cement: firstly by mixing in an open bowl and secondly by extruding the two pastes by an auto-mixing tip using a gun to dispense the pastes. Both types of cements yielded low polymerization exotherms with good mechanical properties; however, the lower viscosity of UDMA allowed better extrusion and handling properties. A biologically active apatite layer formed on the bone cement surface within a short period after its immersion in simulated body fluid, demonstrating in vitro bioactivity of the composite. This preliminary data thus suggests that UDMA is a viable alternative to bis-GMA as a polymerizable matrix in the formation of bone cements.

Lanthanum tricyanide-catalyzed acyl silane-ketone benzoin additions and kinetic resolution of resultant alpha-silyloxyketones.

PubMed

Tarr, James C; Johnson, Jeffrey S

2010-05-21

We report the full account of our efforts on the lanthanum tricyanide-catalyzed acyl silane-ketone benzoin reaction. The reaction exhibits a wide scope in both acyl silane (aryl, alkyl) and ketone (aryl-alkyl, alkyl-alkyl, aryl-aryl, alkenyl-alkyl, alkynyl-alkyl) coupling partners. The diastereoselectivity of the reaction has been examined in both cyclic and acyclic systems. Cyclohexanones give products arising from equatorial attack by the acyl silane. The diastereoselectivity of acyl silane addition to acyclic alpha-hydroxy ketones can be controlled by varying the protecting group to obtain either Felkin-Ahn or chelation control. The resultant alpha-silyloxyketone products can be resolved with selectivity factors from 10 to 15 by subjecting racemic ketone benzoin products to CBS reduction.

Two dimensional fluid simulation in capacitively coupled silane discharges

NASA Astrophysics Data System (ADS)

Song, Yuan-Hong; Liu, Xiang-Mei; Wang, Yan; Wang, You-Nian

2011-10-01

A two-dimensional (2D) self-consistent fluid model is developed to describe the formation, subsequent growth, transport and charging mechanisms of nanoparticles in a capacitively coupled silane plasma. In this discharge process, large anions are produced by a series of chemical reactions of anions with silane molecules, while the lower limit of the initial nanoparticles are taken as large anions to directly link the coagulation module with the nucleation module. The influences of source parameters on the electron density, electron temperature, nanoparticle uniformity, and deposition rate, are carefully studied. Moreover, the behavior of silicon plasma mixed with SiH4, N2 and O2 in a pulse modulated capacitively coupled plasma has been also investigated. Results showed a strong dependence of the electron density and electron temperature on the duty cycle and the modulated frequency. Supported by NSFC (No.10775025 and No. 10805008), INSTSP (Grant No: 2011ZX02403-001), and PNCETU (NCET-08-0073).

Inorganic-organic nanocomposites formed using porous ceramic particles

NASA Astrophysics Data System (ADS)

Luo, Jiazhong

Inorganic-organic nanocomposites are expected to be of great significance in new material technologies impacting many different fields. We develop new nanomaterials of this type that have an interpenetrating network structure via in-situ polymerization of monomer within the nanopores of inorganic gel particles (porosity 20-80 vol.%). Due to strong nanomechanical bonding, these thermosetting polymer composites are expected to exhibit improved mechanical performance. Particle porosity is a primary factor. In contrast to HCl-catalyzed gels, more porous HF-catalyzed gels (porosity 62 vol.%) produced higher composite wear-resistance. At the same loading, the wear rates decrease linearly with increasing filler porosity. Better wear resistance is associated with fine-scale plastic deformation as opposed to brittle fracture and particle pull-out. For the coupling of HF-catalyzed particles with gamma-methacryloxypropyl trimethoxysilane, FTIR and solid-state sp{13}C/sp{29}Si NMR show that the use of a catalyst (n-propylamine) and a nonpolar solvent (cyclohexane), causes the degree of coupling and self-condensation to increase. Ethanol competes with the silane for the surface and results in less silane self-condensation. Surprisingly, the silane diminishes the composite wear resistance due to its pore-filling effect and the subsequent decrease in polymer interpenetration. A transition from plastic deformation to brittle fracture is involved. A new sol-gel technique was found to prepare porous (up to 76.54 vol.%) silica nanoparticles from solution via sodium fluoride (NaF) salt catalysis. Full interpenetration is achieved without the use of silane coupling agents. The resulting composites displayed improved wear resistance, toughness, modulus, hardness and high compressive strength. Toughening and reinforcement can be explained by pore confinement. DMA and DEA were combined with TEM to investigate related structure and property issues. The filler matrix effect on composite wear was evaluated utilizing the phase transformation of porous alumina gels from the stable monohydrate to the gamma-alumina form between 300 and 400sp°C; conveniently the total amount of porosity remains the same. gamma-alumina is more efficient than the monohydrate in improving wear resistance. The susceptibility of the monohydrate to 'transgranular' deformation and the crack-deflection of gamma-alumina in an 'intergranular' mode are responsible for the similar toughening effect of these two reinforcements.

The effects of corn zein protein coupling agent on mechanical properties of flax fiber reinforced composites

NASA Astrophysics Data System (ADS)

Whitacre, Ryan John

In the field of renewable materials, natural fiber composites demonstrate the capacity to be a viable structural material. When normalized by density, flax fiber mechanical properties are competitive with E-glass fibers. However, the hydrophilic nature of flax fibers reduces the interfacial bond strength with polymer thermosets, limiting composite mechanical properties. Corn zein protein was selected as a natural bio-based coupling agent because of its combination of hydrophobic and hydrophilic properties. Zein was deposited on the surface of flax, which was then processed into unidirectional composite. The mechanical properties of zein treated samples where measured and compared against commonly utilized synthetic treatments sodium hydroxide and silane which incorporate harsh chemicals. Fourier transform infrared spectroscopy, chemical analysis, and scanning electron microscopy were also used to determine analyze zein treatments. Results demonstrate the environmentally friendly zein treatment successfully increased tensile strength 8%, flexural strength 17%, and shear strength 30% compared to untreated samples.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Bouza, R.; Barral, L.; Abad, M. J.

The effects of Pinus Sylvestris wood flour as filler in polypropylene matrix was evaluated. The mechanical properties and the morphology of different wood flour/polypropylene composites (WPC) were studied. The composites materials were prepared with several amounts of wood flour from 10 to 30% wt. Mechanical properties show that the wood flour incorporation increases the rigidity of the composites. Morphological analysis indicates that agglomerates are formed, with amounts exceeding 30% of wood flour. For the silane--treated composites, the dispersion of the filler into the polypropylene (PP) matrix improved. Shore D hardness of the composites is decreased with the addition of themore » coupling agent.« less

Lanthanum Tricyanide-Catalyzed Acyl Silane-Ketone Benzoin Additions and Kinetic Resolution of Resultant α-Silyloxyketones

PubMed Central

Tarr, James C.

2010-01-01

We report the full account of our efforts on the lanthanum tricyanide-catalyzed acyl silane-ketone benzoin reaction. The reaction exhibits a wide scope in both acyl silane (aryl, alkyl) and ketone (aryl-alkyl, alkyl-alkyl, aryl-aryl, alkenyl-alkyl, alkynyl-alkyl) coupling partners. The diastereoselectivity of the reaction has been examined in both cyclic and acyclic systems. Cyclohexanones give products arising from equatorial attack by the acyl silane. The diastereoselectivity of acyl silane addition to acyclic α-hydroxy ketones can be controlled by varying the protecting group to obtain either Felkin-Ahn or chelation control. The resultant α-silyloxyketone products can be resolved with selectivity factors from 10 to 15 by subjecting racemic ketone benzoin products to CBS reduction. PMID:20392127

[Effects of different surface conditioning agents on the bond strength of resin-opaque porcelain composite].

PubMed

Liu, Wenjia; Fu, Jing; Liao, Shuang; Su, Naichuan; Wang, Hang; Liao, Yunmao

2014-04-01

The objective of this research is to evaluate the effects of different silane coupling agents on the bond strength between Ceramco3 opaque porcelain and indirect composite resin. Five groups of Co-Cr metal alloy substrates were fabricated according to manufacturer's instruction. The surface of metal alloy with a layer of dental opaque porcelain was heated by fire. After the surface of opaque porcelain was etched, five different surface treatments, i.e. RelyX Ceramic Primer (RCP), Porcelain Bond Activator and SE Bond Primer (mixed with a proportion of 1:1) (PBA), Shofu Porcelain Primer (SPP), SE bond primer (SEP), and no primer treatment (as a control group), were used to combine P60 and opaque porcelain along with resin cement. Shear bond strength of specimens was tested in a universal testing machine. The failure modes of specimens in all groups were observed and classified into four types. Selected specimens were subjected to scanning electron microscope and energy disperse spectroscopy to reveal the relief of the fracture surface and to confirm the failure mode of different types. The experimental results showed that the values of the tested items in all the tested groups were higher than that in the control group. Group PBA exhibited the highest value [(37.52 +/- 2.14) MPa] and this suggested a fact that all of the specimens in group PBA revealed combined failures (failure occurred in metal-porcelain combined surface and within opaque porcelain). Group SPP and RCP showed higher values than SEP (P < 0.05) and most specimens of SPP and RCP performed combined failures (failure occurred in bond surface and within opaque porcelain or composite resin) while all the specimens in group SEP and control group revealed adhesive failures. Conclusions could be drawn that silane coupling agents could reinforce the bond strength of dental composite resin to metal-opaque porcelain substrate. The bond strength between dental composite resin and dental opaque porcelain could meet the clinical requirements.

Virtual Screening as a Strategy for the Identification of Xenobiotics Disrupting Corticosteroid Action

PubMed Central

Praxmarer, Lukas; Chantong, Boonrat; Cereghetti, Diego; Winiger, Rahel; Schuster, Daniela; Odermatt, Alex

2012-01-01

Background Impaired corticosteroid action caused by genetic and environmental influence, including exposure to hazardous xenobiotics, contributes to the development and progression of metabolic diseases, cardiovascular complications and immune disorders. Novel strategies are thus needed for identifying xenobiotics that interfere with corticosteroid homeostasis. 11β-hydroxysteroid dehydrogenase 2 (11β-HSD2) and mineralocorticoid receptors (MR) are major regulators of corticosteroid action. 11β-HSD2 converts the active glucocorticoid cortisol to the inactive cortisone and protects MR from activation by glucocorticoids. 11β-HSD2 has also an essential role in the placenta to protect the fetus from high maternal cortisol concentrations. Methods and Principal Findings We employed a previously constructed 3D-structural library of chemicals with proven and suspected endocrine disrupting effects for virtual screening using a chemical feature-based 11β-HSD pharmacophore. We tested several in silico predicted chemicals in a 11β-HSD2 bioassay. The identified antibiotic lasalocid and the silane-coupling agent AB110873 were found to concentration-dependently inhibit 11β-HSD2. Moreover, the silane AB110873 was shown to activate MR and stimulate mitochondrial ROS generation and the production of the proinflammatory cytokine interleukin-6 (IL-6). Finally, we constructed a MR pharmacophore, which successfully identified the silane AB110873. Conclusions Screening of virtual chemical structure libraries can facilitate the identification of xenobiotics inhibiting 11β-HSD2 and/or activating MR. Lasalocid and AB110873 belong to new classes of 11β-HSD2 inhibitors. The silane AB110873 represents to the best of our knowledge the first industrial chemical shown to activate MR. Furthermore, the MR pharmacophore can now be used for future screening purposes. PMID:23056542

Modifying glass fiber surface with grafting acrylamide by UV-grafting copolymerization for preparation of glass fiber reinforced PVDF composite membrane.

PubMed

Luo, Nan; Zhong, Hui; Yang, Min; Yuan, Xing; Fan, Yaobo

2016-01-01

Experimental design and response surface methodology (RSM) were used to optimize the modification of conditions for glass surface grafting with acrylamide (AM) monomer for preparation of a glass fiber reinforced poly(vinylidene fluoride) (PVDF) composite membrane (GFRP-CM). The factors considered for experimental design were the UV (ultraviolet)-irradiation time, the concentrations of the initiator and solvent, and the kinds and concentrations of the silane coupling agent. The optimum operating conditions determined were UV-irradiation time of 25 min, an initiator concentration of 0-0.25 wt.%, solvent of N-Dimethylacetamide (DMAC), and silane coupling agent KH570 with a concentration of 7 wt.%. The obtained optimal parameters were located in the valid region and the experimental confirmation tests conducted showed good accordance between predicted and experimental values. Under these optimal conditions, the water absorption of the grafted modified glass fiber was improved from 13.6% to 23%; the tensile strength was enhanced and the peeling strength of the glass fiber reinforced PVDF composite membrane was improved by 23.7% and 32.6% with an AM concentration at 1 wt.% and 2 wt.%. The surface composition and microstructure of AM grafted glass fiber were studied via several techniques including Field Emission Scanning Electron Microscopy (FESEM), Fourier transform infrared spectroscopy-attenuated total reflectance (FTIR-ATR) and energy dispersive X-ray spectroscopy (EDX). The analysis of the EDX and FTIR-ATR results confirmed that the AM was grafted to the glass fiber successfully by detecting and proving the existence of nitrogen atoms in the GFRP-CM. Copyright © 2015. Published by Elsevier B.V.

The use of novel biodegradable, optically active and nanostructured poly(amide-ester-imide) as a polymer matrix for preparation of modified ZnO based bionanocomposites

DOE Office of Scientific and Technical Information (OSTI.GOV)

Abdolmaleki, Amir, E-mail: abdolmaleki@cc.iut.ac.ir; Nanotechnology and Advanced Materials Institute, Isfahan University of Technology, Isfahan 84156-83111, Islamic Republic of Iran; Mallakpour, Shadpour, E-mail: mallak@cc.iut.ac.ir

Highlights: Black-Right-Pointing-Pointer A novel biodegradable and nanostructured PAEI based on two amino acids, was synthesized. Black-Right-Pointing-Pointer ZnO nanoparticles were modified via two different silane coupling agents. Black-Right-Pointing-Pointer PAEI/modified ZnO BNCs were synthesized through ultrasound irradiation. Black-Right-Pointing-Pointer ZnO particles were dispersed homogeneously in PAEI matrix on nanoscale. Black-Right-Pointing-Pointer The effect of ZnO nanoparticles on the properties of synthesized polymer was examined. -- Abstract: A novel biodegradable and nanostructured poly(amide-ester-imide) (PAEI) based on two different amino acids, was synthesized via direct polycondensation of biodegradable N,N Prime -bis[2-(methyl-3-(4-hydroxyphenyl)propanoate)]isophthaldiamide and N,N Prime -(pyromellitoyl)-bis-L-phenylalanine diacid. The resulting polymer was characterized by FT-IR, {sup 1}H NMR,more » specific rotation, elemental analysis, thermogravimetric analysis (TGA), differential scanning calorimetry (DSC), X-ray diffraction (XRD) and field emission scanning electron microscopy (FE-SEM) analysis. The synthesized polymer showed good thermal stability with nano and sphere structure. Then PAEI/ZnO bionanocomposites (BNCs) were fabricated via interaction of pure PAEI and ZnO nanoparticles. The surface of ZnO was modified with two different silane coupling agents. PAEI/ZnO BNCs were studied and characterized by FT-IR, XRD, UV/vis, FE-SEM and TEM. The TEM and FE-SEM results indicated that the nanoparticles were dispersed homogeneously in PAEI matrix on nanoscale. Furthermore the effect of ZnO nanoparticle on the thermal stability of the polymer was investigated with TGA and DSC technique.« less

Reduction of non-specific adsorption of drugs to plastic containers used in bioassays or analyses.

PubMed

Fukazawa, Tominaga; Yamazaki, Yuri; Miyamoto, Yohei

2010-01-01

Non-specific adsorption (NSA) of drugs to plastic or glass containers used in clinical use is well known, but methods for reducing NSA have been rarely reported. We assessed the NSA to various containers and then investigated methods to reduce NSA. Probe drugs (methotrexate, warfarin, chloroquine, propranolol, verapamil, digoxin and paclitaxel) dissolved in water were incubated in conventional or low-adsorption containers for 4h at 4 degrees C and the NSA was determined by HPLC. They were also dissolved in aqueous methanol or acetonitrile and the NSA to a conventional polypropylene microplate was determined. Finally, tissue culture microplates were coated with silane coupling agents and the effects of the coatings were evaluated. Hydrophobic drugs (paclitaxel, verapamil and digoxin) were highly adsorbed to conventional plastic microplates, but in addition to hydrophobic drugs, positively charged drugs were well adsorbed to the tissue culture microplate. Low-adsorption microplates could reduce NSA below 15%, but positively charged or neutral hydrophobic drugs showed relatively higher adsorption. Acetonitrile showed stronger NSA inhibition than that of methanol, but the peak shapes of methotrexate and chloroquine were broadened and split. Among the silane coupling agents, GPTMS suppressed the NSA below 10%. Also, AATMS resembled the NSA pattern of GPTMS, but it increased the adsorption of methotrexate to 29%. On conventional plastic microplates, NSA is mainly driven by hydrophobic interactions, but on tissue culture microplates and low-adsorption microplates, in addition to hydrophobic interactions, ionic interactions play a role in the NSA. Therefore, to reduce the NSA to plastic containers, both hydrophobic and ionic interactions should be reduced using amphiphilic organic solvents or neutral and hydrophilic coatings. 2010 Elsevier Inc. All rights reserved.

Importance of surface modification of γ-alumina in creating its nanostructured composites with zeolitic imidazolate framework ZIF-67.

PubMed

Liu, Yuanyuan; Gonçalves, Alexandre A S; Zhou, Yang; Jaroniec, Mietek

2018-05-07

Application of zeolitic imidazolate framework-67 (ZIF-67) as an adsorbent has been greatly hindered by slow mass transfer of adsorbate molecules due to its inherent microporosity. To address this limitation, we have developed binary nanostructures composed of ZIF-67 and γ-alumina (GA) containing respectively micropores and large mesopores. The nanostructured composites were successfully prepared by coupling ZIF-67 and GA with and without surface modification with imidazole silane that mimics the building blocks of ZIF-67 to obtain GA-Im-ZIF-67 (with imidazole silane) and GA-ZIF-67 (without imidazole silane). The sizes of ZIF-67 crystals in these composites were smaller as compared to those of pure ZIF-67, and the textural properties of these composites with and without surface modification were quite similar. However, the surface grafting of alumina with imidazole silane played an important role in improving interfacial coupling between GA and ZIF-67, which resulted in significant changes in the dispersion of ZIF-67 crystals and better adsorption properties. The presence of large mesopores in the alumina-based composites containing smaller ZIF-67 crystals improved their adsorption properties toward dyes such as Rhodamine B (RhB). The RhB adsorption capacity of GA-Im-ZIF-67 was much higher than that of GA-ZIF-67, suggesting that the imidazole silane modification of GA before its coupling with ZIF-67 and the GA mesoporosity were essential for a substantial increase in the adsorption capacity of RhB. Copyright © 2018 Elsevier Inc. All rights reserved.

Effect of silane/hydrogen ratio on microcrystalline silicon thin films by remote inductively coupled plasma

NASA Astrophysics Data System (ADS)

Guo, Y. N.; Wei, D. Y.; Xiao, S. Q.; Huang, S. Y.; Zhou, H. P.; Xu, S.

2013-05-01

Hydrogenated microcrystalline silicon (μc-Si:H) thin films were prepared by remote low frequency inductively coupled plasma (ICP) chemical vapor deposition system, and the effect of silane/hydrogen ratio on the microstructure and electrical properties of μc-Si:H films was systematically investigated. As silane/hydrogen ratio increases, the crystalline volume fraction Fc decreases and the ratio of the intensity of (220) peak to that of (111) peak drops as silane flow rate is increased. The FTIR result indicates that the μc-Si:H films prepared by remote ICP have a high optical response with a low hydrogen content, which is in favor of reducing light-induced degradation effect. Furthermore, the processing window of the phase transition region for remote ICP is much wider than that for typical ICP. The photosensitivity of μc-Si:H films can exceed 100 at the transition region and this ensures the possibility of the fabrication of microcrystalline silicon thin film solar cells with a open-circuit voltage of about 700 mV.

Photovoltaics module interface: General purpose primers

NASA Technical Reports Server (NTRS)

Boerio, J.

1985-01-01

The interfacial chemistry established between ethylene vinyl acetate (EVA) and the aluminized back surface of commercial solar cells was observed experimentally. The technique employed is called Fourier Transform Infrared (FTIR) spectroscopy, with the infrared signal being reflected back from the aluminum surface through the EVA film. Reflection infrared (IR) spectra are given and attention is drawn to the specific IR peak at 1080/cm which forms on hydrolytic aging of the EVA/aluminum system. With this fundamental finding, and the workable experimental techniques, candidate silane coupling agents are employed at the interface, and their effects on eliminating or slowing hydrolytic aging of the EVA/aluminum interface are monitored.

High-Temperature Hot Air/Silane Coupling Modification of Wood Fiber and Its Effect on Properties of Wood Fiber/HDPE Composites.

PubMed

Chen, Feng; Han, Guangping; Li, Qingde; Gao, Xun; Cheng, Wanli

2017-03-13

The surfaces of poplar wood fibers were modified using high-temperature hot air (HTHA) treatment and silane coupling agent. The single factor test was then used to investigate the performances (e.g., the change of functional groups, polarity, cellulose crystallinity, and thermal stability) of modified poplar wood fibers (mPWF) through Fourier transform infrared spectrometry, X-ray diffraction and thermo-gravimetric analysis for the subsequent preparation of wood-plastic composites (WPCs). The effect of HTHA treatment conditions-such as temperature, inlet air velocity, and feed rate-on the performances of WPCs was also investigated by scanning electron microscopy and dynamic mechanical analysis. The main findings indicated that HTHA treatment could promote the hydration of mPWF and improve the mechanical properties of WPCs. Treatment temperature strongly affected the mechanical properties and moisture adsorption characteristics of the prepared composites. With the increase of treated temperature and feed rate, the number of hydroxyl groups, holocellulose content, and the pH of mPWF decreased. The degree of crystallinity and thermal stability and the storage modulus of the prepared composites of mPWF increased. However, dimensional stability and water absorption of WPCs significantly reduced. The best mechanical properties enhancement was observed with treatment temperature at 220 °C. This study demonstrated the feasibility for the application of an HTHA treatment in the WPC production industry.

High-Temperature Hot Air/Silane Coupling Modification of Wood Fiber and Its Effect on Properties of Wood Fiber/HDPE Composites

PubMed Central

Chen, Feng; Han, Guangping; Li, Qingde; Gao, Xun; Cheng, Wanli

2017-01-01

The surfaces of poplar wood fibers were modified using high-temperature hot air (HTHA) treatment and silane coupling agent. The single factor test was then used to investigate the performances (e.g., the change of functional groups, polarity, cellulose crystallinity, and thermal stability) of modified poplar wood fibers (mPWF) through Fourier transform infrared spectrometry, X-ray diffraction and thermo-gravimetric analysis for the subsequent preparation of wood-plastic composites (WPCs). The effect of HTHA treatment conditions—such as temperature, inlet air velocity, and feed rate—on the performances of WPCs was also investigated by scanning electron microscopy and dynamic mechanical analysis. The main findings indicated that HTHA treatment could promote the hydration of mPWF and improve the mechanical properties of WPCs. Treatment temperature strongly affected the mechanical properties and moisture adsorption characteristics of the prepared composites. With the increase of treated temperature and feed rate, the number of hydroxyl groups, holocellulose content, and the pH of mPWF decreased. The degree of crystallinity and thermal stability and the storage modulus of the prepared composites of mPWF increased. However, dimensional stability and water absorption of WPCs significantly reduced. The best mechanical properties enhancement was observed with treatment temperature at 220 °C. This study demonstrated the feasibility for the application of an HTHA treatment in the WPC production industry. PMID:28772646

Polyethylene glycol-covered ultra-small Gd2O3 nanoparticles for positive contrast at 1.5 T magnetic resonance clinical scanning

NASA Astrophysics Data System (ADS)

Fortin, Marc-André; Petoral, Rodrigo M., Jr.; Söderlind, Fredrik; Klasson, A.; Engström, Maria; Veres, Teodor; Käll, Per-Olof; Uvdal, Kajsa

2007-10-01

The size distribution and magnetic properties of ultra-small gadolinium oxide crystals (US-Gd2O3) were studied, and the impact of polyethylene glycol capping on the relaxivity constants (r1, r2) and signal intensity with this contrast agent was investigated. Size distribution and magnetic properties of US-Gd2O3 nanocrystals were measured with a TEM and PPMS magnetometer. For relaxation studies, diethylene glycol (DEG)-capped US-Gd2O3 nanocrystals were reacted with PEG-silane (MW 5000). Suspensions were adequately dialyzed in water to eliminate traces of Gd3+ and surfactants. The particle hydrodynamic radius was measured with dynamic light scattering (DLS) and the proton relaxation times were measured with a 1.5 T MRI scanner. Parallel studies were performed with DEG-Gd2O3 and PEG-silane-SPGO (Gd2O3,< 40 nm diameter). The small and narrow size distribution of US-Gd2O3 was confirmed with TEM (~3 nm) and DLS. PEG-silane-US-Gd2O3 relaxation parameters were twice as high as for Gd-DTPA and the r2/r1 ratio was 1.4. PEG-silane-SPGO gave low r1 relaxivities and high r2/r1 ratios, less compatible with positive contrast agent requirements. Higher r1 were obtained with PEG-silane in comparison to DEG-Gd2O3. Treatment of DEG-US-Gd2O3 with PEG-silane provides enhanced relaxivity while preventing aggregation of the oxide cores. This study confirms that PEG-covered Gd2O3 nanoparticles can be used for positively contrasted MR applications requiring stability, biocompatible coatings and nanocrystal functionalization.

The diametral tensile strength and hydrostability of polymer-ceramic nano-composite (pcnc) material prototypes

NASA Astrophysics Data System (ADS)

Yepez, Johanna

Statement of the problem: There is a weak connection between the filler and the resin matrix of dental composites caused primarily by hydrolysis of silane coupling agent, therefore, jeopardizing the mechanical properties of the dental restorations. Purpose: The purpose of this study was to compare the diametral tensile strength (DTS) of a nano-mechanically bonded polymer ceramic nano composite (pcnc) versus the chemically bonding prototype polymer ceramic nano composite (pcnc) fabricated by using hydrolytically stable interphase. Materials and Methods: Composites were made with 60wt % filler, 38% triethyleneglycol dimethacrylate (TEDGMA), 1% camphorquinone (CQ) and 1% 2-(dimethylamino) ethyl methacrylate (DMAEMA). Tests for DTS were performed using a universal testing machine. The disk-shaped specimens were loaded in compression between two supporting plates at a crosshead speed of 0.5 mm/min until fracture. The samples, measuring 3 mm in height and 6 mm in diameter, were produced in a round stainless steel (SS) mold. A total of 144 samples were created. Groups of 48 samples were made for each of three different fillers. Specimens were soaked in artificial saliva at 37° for four time periods, dry(t=0), 1 day, 7 days, 28 days). At the end of each soaking time DTS tests were performed. Results: There where statistically significant differences in the DTS between the filler groups and the soaking times (p=<0.001) as well as for the pairwise comparison between the different filler group values and between the different soaking times as an individual treatment. Overall, longer soaking times resulted in lower mean DTS values. The DTS of the PCNC for filler #1 decreased to 82.4% of the original value after 1 day of soaking, 67.2% after 7 days and 27.2 % after 28 days. For filler #2 decreased to 54.8% of the original value after 1 day of soaking, 62.3% after 7 days and 61.2% after 28 days. For filler #3 decreased to 71.2% of the original value, 67.3% after 7 days and 51.4% after 28 days (Fig 8). Conclusions: Within the limitation of this study it can be concluded that the use of coupling agent will significantly influence the degradation of the material under wet environment. Clinical Implication: Changes within matrix composition and bonding interphase of resin base composites promise improvements of mechanical properties, decreasing the incidence of clinical failure of posterior composite restorations, hence resulting in a more ideal restorative material for use in posterior segment. The results of this investigation showed that the deficiency of hydrostability in dental composites is a detrimental factor in the mechanical behavior. The silanation of the filler particles have a positive influence on the mechanical properties of dental composites but the hydrolysis of the silane coupling agent can dramatically reduce the average lifetime of dental composites.

Synthesis of amino-silane modified superparamagnetic Fe{sub 3}O{sub 4} nanoparticles and its application in immobilization of lipase from Pseudomonas fluorescens Lp1

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kanimozhi, S., E-mail: skanimo@gmail.com; Perinbam, K.

2013-05-15

Highlights: ► Magnetic nanoparticles were synthesized by chemical co-precipitation method. ► Surface was functionalized with amino-silane and used for lipase immobilization. ► Characterized through TEM, SEM, XRD, FT-IR and VSM analysis. ► The functionalization and immobilization did not affect the magnetite properties. ► The immobilized lipase showed greater functional property than free lipase. - Abstract: Superparamagnetic nanoparticles (Fe{sub 3}O{sub 4}–magnetite) were prepared by chemical co-precipitation method and their surface was functionalized with 3-aminopropyltriethoxysilane via silanization reaction to obtain amino functionalized magnetic nanoparticles. The purified lipase from Pseudomonas fluorescens Lp1 was immobilized onto functionalized magnetite using glutaraldehyde as the coupling agent.more » The characterization of the nanoparticles was done by scanning electron microscopy, transmission electron microscopy, powder X-ray diffraction, vibrating sample magnetometry and Fourier transformed infrared spectroscopy. The size of the magnetite was measured about 10–30 nm. The results of characterization study revealed the successful immobilization of lipase on to functionalized magnetite. The saturation magnetization of magnetic nanoparticles was found to be 28.34 emu/g whereas the immobilized magnetic nanoparticle was 17.074 emu/g. The immobilized lipase had greater activity at 50 °C and thermal stability upto 70 °C. It exhibited excellent reusability for 4 cycles and storage stability upto 15 days by retaining 75% of its initial activity.« less

Method for Waterproofing Ceramic Materials

NASA Technical Reports Server (NTRS)

Cagliostro, Domenick E. (Inventor); Hsu, Ming-Ta S. (Inventor)

1998-01-01

Hygroscopic ceramic materials which are difficult to waterproof with a silane, substituted silane or silazane waterproofing agent, such as an alumina containing fibrous, flexible and porous, fibrous ceramic insulation used on a reentry space vehicle, are rendered easy to waterproof if the interior porous surface of the ceramic is first coated with a thin coating of silica. The silica coating is achieved by coating the interior surface of the ceramic with a silica precursor converting the precursor to silica either in-situ or by oxidative pyrolysis and then applying the waterproofing agent to the silica coated ceramic. The silica precursor comprises almost any suitable silicon containing material such as a silane, silicone, siloxane, silazane and the like applied by solution, vapor deposition and the like. If the waterproofing is removed by e.g., burning, the silica remains and the ceramic is easily rewaterproofed. An alumina containing TABI insulation which absorbs more that five times its weight of water, absorbs less than 10 wt. % water after being waterproofed according to the method of the invention.

Surface modification of TiO2 nanotubes by grafting with APTS coupling agents

NASA Astrophysics Data System (ADS)

Phan Duong, Hong; Le, Minh Duc; Dao, Hung Cuong; Chen, Chia-Yun

2017-10-01

Titanium dioxide nanotubes (TNTs) have been considered the promising nanostructures employed for many practical applications such as biomedical, photonic and optoelectronic devices. Nevertheless, strong aggregation of TNTs within various aqueous media significantly hindered their practical utilizations and the capability of dispersing TNTs in the desired solvents are urgent to be improved. Therefore, in this study, the methodic investigations have been performed on the grafted modification of 3-aminopropyl triethoxysilane (APTS) on the surfaces of synthesized TNTs. A preliminary study was carried out to evaluate the influences of key parameters, including the concentrations of coupling agents, temperatures and the reaction durations, on the grafting efficiency of the aminosilane using Statistical design of experiments (DoE) methodology. TNTs with approximately 10-20 nm in diameter were prepared with the controlled hydrothermal treatment of commercialized P25 particles. The obtained products were revealed by the modern physicochemical systems including x-ray diffraction (XRD), transmission electron microscopy (TEM) and Brunauer-Emmett-Teller (BET) analysis. The additions of silane agent, reaction temperature and time have been adjusted to reveal the influences of the grafting efficiency (from 2.5 to 7.8 wt %) by thermal gravimetric analysis (TGA). Analysis of Fourier transform infrared spectroscopy (FTIR) has confirmed the successful link of Ti-O-Si chemical bonds on the grafted TNTs.

The improvement of the mechanical properties of PMMA denture base by Al2O3 particles with nitrile rubber

NASA Astrophysics Data System (ADS)

Alhareb, Ahmed Omran; Akil, Hazizan Md; Ahmad, Zainal Arifin

2017-07-01

Poly methyl methacrylate (PMMA) is mostly used for fabrication of denture base by heat-curing technique. Therefore, the purpose of this study is to investigate the effect of Al2O3 filler as toughening particles together with nitrile butadiene rubber (NBR) particles as impact modifier were used to reinforce PMMA denture base materials on the impact strength (IS) and fracture toughness (KIC). PMMA powder was mixed with liquid methyl methacrylate (MMA) and ethylene glycol dimethacrylate (EGDMA) as crosslinking agent. The powder components are PMMA, benzoyl peroxide, NBR (5, 7.5 and 10 wt%), and Al2O3 filler (5 wt%) treated by silane. The liquid components are 90% of methyl methacrylate and 10 % ethylene glycol dimethacryate. FTIR analyses confirmed that the Al2O3 filler was successfully treated with silane as coupling agent. The morphology of fracture surfaces was characterized using field emission scanning electron microscopy (FESEM). The results shown that IS and KIC improved significantly when using treated the Al2O3 filler. IS has increased to 56% (8.26 KJ/m2) and 73% (2.77 MPa.m1/2) for KIC when treated Al2O3 filler compared to unreinforced PMMA matrix. Statistical analyses of data results were significantly improved (P<0.05) when using 7.5 wt% NBR with treated Al2O3 filler compared to other the compositions.

Mechanical Property and Thermal Endurance of Room Temperature Vulcanizing Silicone Compound with Reduced Environmental Impact

NASA Astrophysics Data System (ADS)

Cho, Hiroaki; Ashida, Yasunori; Nakamura, Shuhei; Shimizu, Wataru; Murakami, Yasushi

Room temperature vulcanizing (RTV) elastic silicone usually employs organic tin compounds as a hardener. It is well known that they are strong biohazardous. Thus, European Union is going to regulate the use of organic tin compounds and to exclude them from industrial products till 2015. Authors have succeeded in making a substitute of organic tin compounds as a hardener for RTV elastic silicone by using titanium alkoxide and a carboxylate ester as a hardener and a promoter, respectively. In this paper, composites of RTV elastic silicone made with silica particles and a silane coupling agent are studied based on the mechanical, heat-resistive and adhesive properties.

Effect of surface treatments on the bond strength between resin cement and differently sintered zirconium-oxide ceramics.

PubMed

Yenisey, Murat; Dede, Doğu Ömür; Rona, Nergiz

2016-01-01

This study investigated the effects of surface treatments on bond strength between resin cement and differently sintered zirconium-oxide ceramics. 220 zirconium-oxide ceramic (Ceramill ZI) specimens were prepared, sintered in two different period (Short=Ss, Long=Ls) and divided into ten treatment groups as: GC, no treatment; GSil, silanized (ESPE-Sil); GSilPen, silane flame treatment (Silano-Pen); GSb, sandblasted; GSbSil, sandblasted+silanized; GSbCoSil, sandblasted+silica coated (CoJet)+silanized; GSbRoSil, sandblasted+silica coated (Rocatech-Plus)+silanized; GSbDSil, sandblasted+diamond particle abraded (Micron MDA)+silanized; GSbSilPen, sandblasted+silane flame treatment+silanized; GSbLSil, sandblasted+Er:Yag (Asclepion-MCL30) laser treated+silanized. The composite resin (Filtek Z-250) cylinders were cemented to the treated ceramic surfaces with a resin cement (Panavia F2.0). Shear bond strength test was performed after specimens were stored in water for 24h and thermo-cycled for 6000 cycles (5-55 °C). Data were statistically analyzed with two-way analysis of variance (ANOVA) and Tamhane's multiple comparison test (α=0.05). According to the ANOVA, sintering time, surface treatments and their interaction were statistically significant (p<0.05). The highest bond strengths were obtained in GSbCoSil (Ss=13.36/Ls=11.19MPa) and lowest values were obtained in GC (Ss=4.70/Ls=4.62 MPa) for both sinter groups. Sintering time may be effective on the bond strength and 30 μm silica coating (Cojet) with silane coupling application technique increased the bond strength between resin cement and differently sintered zirconium-oxide ceramics. Copyright © 2015 Japan Prosthodontic Society. Published by Elsevier Ltd. All rights reserved.

Bond strength of metal brackets bonded to a silica-based ceramic with light-cured adhesive : Influence of various surface treatment methods.

PubMed

Zhang, Zhe-Chen; Qian, Yu-Fen; Yang, Yi-Ming; Feng, Qi-Ping; Shen, Gang

2016-09-01

The purpose of this work was to evaluate the effects of several surface treatment methods on the shear bond strengths of metal brackets bonded to a silica-based ceramic with a light-cured adhesive. Silica-based ceramic (IPS Classic(®)) with glazed surfaces was cut into discs that were used as substrates. A total of 80 specimens were randomly divided into four groups according to the method used: 9.6 % hydrofluoric acid (group 1), 9.6 % hydrofluoric acid (HF) + silane coupling agent (group 2), sandblasting (aluminum trioxide, 50 μm) + silane (group 3), and tribochemical silica coating (CoJet™ sand, 30 μm) + silane (group 4). Brackets were bonded to the treated specimens with a light-cure adhesive (Transbond XT, 3 M Unitek). Shear bond strength was tested after bracket bonding, and the Adhesive Remnant Index (ARI) scores were quantified after debonding. Group 4 showed the highest bond strength (12.3 ± 1.0 MPa), which was not significantly different from that of group 3 (11.6 ± 1.2 MPa, P > 0.05); however, the bond strength of group 4 was substantially higher than that of group 2 (9.4 ± 1.1 MPa, P < 0.05). The shear bond strength of group 1 (3.1 ± 0.6 MPa, P< 0.05) was significantly lower than that of the other groups. Shear bond strengths exceeded the optimal range of ideal bond strength for clinical practice, except for the isolated HF group. HF acid etching followed by silane was the best suited method for bonding on IPS Classic(®). Failure modes in the sandblasting and silica-coating groups revealed signs of damaged ceramic surfaces.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Lutwack, R.

The goal of the Silicon Material Task, a part of the FSA Project, was to develop and demonstrate the technology for the low-cost production of silicon of suitable purity to be used as the basic material for the manufacture of terrestrial photovoltaic solar cells. To be compatible with the price goals of the FSA Project, the price of the produced silicon was to be less than $10/kg (in 1975 dollars). Summarized in this document are 11 different processes for the production of silicon that were investigated and developed to varying extent by industrial, university, and government researchers. The silane-production sectionmore » of the Union Carbide Corp. (UCC) silane process was developed completely in this program. Coupled with Siemens-type chemical vapor deposition reactors, the process was carried through the pilot plant stage. The overall UCC process involves the conversion of metallurgical-grade silicon to silane followed by decomposition of the silane to purified silicon. Production of very high-purity silane and silicon was demonstrated. Although it has as yet not achieved commercial application, the development of fluidized-bed technology for the low-cost, high-throughput conversion of silane-to-silicon has been demonstrated in the research laboratory and now is in engineering development.« less

A Comparative Evaluation of Effect of Different Chemical Solvents on the Shear Bond Strength of Glass Fiber reinforced Post to Core Material

PubMed Central

Samadi, Firoza; Jaiswal, JN; Saha, Sonali

2014-01-01

ABSTRACT% Aim: To compare the effect of different chemical solvents on glass fiber reinforced posts and to study the effect of these solvents on the shear bond strength of glass fiber reinforced post to core material. Materials and methods: This study was conducted to evaluate the effect of three chemical solvents, i.e. silane coupling agent, 6% H2O2 and 37% phosphoric acid on the shear bond strength of glass fiber post to a composite resin restorative material. The changes in post surface characteristics after different treatments were also observed, using scanning electron microscopy (SEM) and shear bond strength was analyzed using universal testing machine (UTM). Results: Surface treatment with hydrogen peroxide had greatest impact on the post surface followed by 37% phosphoric acid and silane. On evaluation of the shear bond strength, 6% H2O2 exhibited the maximum shear bond strength followed in descending order by 37% phosphoric acid and silane respectively. Conclusion: The surface treatment of glass fiber post enhances the adhesion between the post and composite resin which is used as core material. Failure of a fiber post and composite resin core often occurs at the junction between the two materials. This failure process requires better characterization. How to cite this article: Sharma A, Samadi F, Jaiswal JN, Saha S. A Comparative Evaluation of Effect of Different Chemical Solvents on the Shear Bond Strength of Glass Fiber Reinforced Post to Core Material. Int J Clin Pediatr Dent 2014;7(3):192-196. PMID:25709300

Two-year interfacial bond durability and nanoleakage of repaired silorane-based resin composite.

PubMed

Mobarak, E; El-Deeb, H

2013-01-01

To investigate the effect of silane primer application, intermediate adhesive agent/repair composite, and storage period on the interfacial microtensile bond strength (μTBS) of repaired silorane-based resin composite compared with unrepaired composites and on the nanoleakage. Forty-eight 1-month-old substrate specimens from Filtek P90 were roughened, etched, and distributed over two groups (n=24) based on receiving silane (Clearfil Ceramic Primer) or not. Then, half of the specimens (n=12) were repaired with P90 System Adhesive/Filtek P90 and the other half with Adper Scotchbond Multipurpose adhesive/Filtek Z250 resin composite. Within each repair category, repaired specimens were stored in artificial saliva at 37°C for either 24 hours (n=6) or two years before being serially sectioned into sticks (0.6 ± 0.01 mm(2)). From each specimen, two sticks were prepared for nanoleakage determination and four sticks were used for μTBS testing. Additional unrepaired specimens from each composite (n=12) were made to determine the cohesive strength at 24 hours and two years. Mean μTBS were calculated and statistically analyzed. Modes of failure were also determined. General linear model analysis revealed no significant effect for the silane priming, intermediate adhesive agent/repair composite, and storage period or for their interactions on the μTBS values of the repaired specimens. There was no significant difference between the cohesive strength of Filtek P90 and Filtek Z250; both were significantly higher than all repaired categories. At 24 hours, nanoleakage was not detected when silorane-based composite was repaired with the same material. However, after two years, all repair categories showed nanoleakage. Silane application has no effect on μTBS and nanoleakage. Durability of the interfacial bond of repaired silorane-based resin composite appeared successful regardless of the chemistry of the intermediate adhesive agent/composite used for repair. However, nanoleakage was detected early when a different repair intermediate adhesive agent/composite was used.

Surface Modifications in Adhesion and Wetting

NASA Astrophysics Data System (ADS)

Longley, Jonathan

Advances in surface modification are changing the world. Changing surface properties of bulk materials with nanometer scale coatings enables inventions ranging from the familiar non-stick frying pan to advanced composite aircraft. Nanometer or monolayer coatings used to modify a surface affect the macro-scale properties of a system; for example, composite adhesive joints between the fuselage and internal frame of Boeing's 787 Dreamliner play a vital role in the structural stability of the aircraft. This dissertation focuses on a collection of surface modification techniques that are used in the areas of adhesion and wetting. Adhesive joints are rapidly replacing the familiar bolt and rivet assemblies used by the aerospace and automotive industries. This transition is fueled by the incorporation of composite materials into aircraft and high performance road vehicles. Adhesive joints have several advantages over the traditional rivet, including, significant weight reduction and efficient stress transfer between bonded materials. As fuel costs continue to rise, the weight reduction is accelerating this transition. Traditional surface pretreatments designed to improve the adhesion of polymeric materials to metallic surfaces are extremely toxic. Replacement adhesive technologies must be compatible with the environment without sacrificing adhesive performance. Silane-coupling agents have emerged as ideal surface modifications for improving composite joint strength. As these coatings are generally applied as very thin layers (<50 nm), it is challenging to characterize their material properties for correlation to adhesive performance. We circumvent this problem by estimating the elastic modulus of the silane-based coatings using the buckling instability formed between two materials of a large elastic mismatch. The elastic modulus is found to effectively predict the joint strength of an epoxy/aluminum joint that has been reinforced with silane coupling agents. This buckling technique is extended to investigate the effects of chemical composition on the elastic modulus. Finally, the effect of macro-scale roughness on silane-reinforced joints is investigated within the framework of the unresolved problem of how to best characterize rough surfaces. Initially, the fractal dimension is used to characterize grit-blasted and sanded surfaces. It is found that, contrary to what has been suggested in the literature, the fractal dimension is independent of the roughening mechanism. Instead, the use of an anomalous diffusion coefficient is proposed as a more effective way to characterize a rough surface. Surface modification by preparation of surface energy gradients is then investigated. Materials with gradients in surface energy are useful in the areas of microfluidics, heat transfer and protein adsorption, to name a few. Gradients are prepared by vapor deposition of a reactive silane from a filter paper source. The technique gives control over the size and shape of the gradient. This surface modification is then used to induce droplet motion through repeated stretching and compression of a water drop between two gradient surfaces. This inchworm type motion is studied in detail and offers an alternative method to surface vibration for moving drops in microfluidic devices. The final surface modification considered is the application of a thin layer of rubber to a rigid surface. While this technique has many practical uses, such as easy release coatings in marine environments, it is applied herein to enable spontaneous healing between a rubber surface and a glass cover slip. Study of the diffusion controlled healing of a blister can be made by trapping an air filled blister between a glass cover slip and a rubber film. Through this study we find evidence for an interfacial diffusion process. This mechanism of diffusion is likely to be important in many biological systems.

Influence of spacer length on heparin coupling efficiency and fibrinogen adsorption of modified titanium surfaces

PubMed Central

Tebbe, David; Thull, Roger; Gbureck, Uwe

2007-01-01

Background Chemical bonding of the drug onto surfaces by means of spacer molecules is accompanied with a reduction of the biological activity of the drug due to a constricted mobility since normally only short spacer molecule like aminopropyltrimethoxysilane (APMS) are used for drug coupling. This work aimed to study covalent attachment of heparin to titanium(oxide) surfaces by varying the length of the silane coupling agent, which should affect the biological potency of the drug due to a higher mobility with longer spacer chains. Methods Covalent attachment of heparin to titanium metal and TiO2 powder was carried out using the coupling agents 3-(Trimethoxysilyl)-propylamine (APMS), N- [3-(Trimethoxysilyl)propyl]ethylenediamine (Diamino-APMS) and N1- [3-(Trimethoxy-silyl)-propyl]diethylenetriamine (Triamino-APMS). The amount of bound coupling agent and heparin was quantified photometrically by the ninhydrin reaction and the tolidine-blue test. The biological potency of heparin was determined photometrically by the chromogenic substrate Chromozym TH and fibrinogen adsorption to the modified surfaces was researched using the QCM-D (Quartz Crystal Microbalance with Dissipation Monitoring) technique. Results Zeta-potential measurements confirmed the successful coupling reaction; the potential of the unmodified anatase surface (approx. -26 mV) shifted into the positive range (> + 40 mV) after silanisation. Binding of heparin results in a strongly negatively charged surface with zeta-potentials of approx. -39 mV. The retaining biological activity of heparin was highest for the spacer molecule Triamino-APMS. QCM-D measurements showed a lower viscosity for adsorbed fibrinogen films on heparinised surfaces by means of Triamino-APMS. Conclusion The remaining activity of heparin was found to be highest for the covalent attachment with Triamino-APMS as coupling agent due to the long chain of this spacer molecule and therefore the highest mobility of the drug. Furthermore, the adsorption of fibrinogen on the differently heparinised surfaces in real time demonstrated that with longer spacer chains the ΔD/Δf ratios became higher, which is also associated with better biocompatible properties of the substrates in contact with a biosystem. PMID:17640335

Structuring unbreakable hydrophobic barriers in paper

NASA Astrophysics Data System (ADS)

Nargang, Tobias M.; Kotz, Frederik; Rapp, Bastian E.

2018-02-01

Hydrophobic barriers are one of the key elements of microfluidic paper based analytical devices (μPADs).μPADs are simple and cost efficient and they can be carried out without the need of high standard laboratories. To carry out such a test a method is needed to create stable hydrophobic barriers. Commonly used methods like printing wax or polystyrene have the major drawback that these barriers are stiff and break if bended which means they will no longer be able to retain a liquid sample. Here we present silanes to structure hydrophobic barriers via polycondensation and show a silanization method which combines the advantages of flexible silane/siloxane layers with the short processing times of UV-light based structuring. The barriers are created by using methoxy silanes which are mixed with a photo acid generator (PAG) as photoinitiator. Also a photosensitizer was given to the mixture to increase the effectiveness of the PAG. After the PAG is activated by UV-light the silane is hydrolyzed and coupled to the cellulose via polycondensation. The created hydrophobic barriers are highly stable and do not break if being bended.

Improved antifouling properties and selective biofunctionalization of stainless steel by employing heterobifunctional silane-polyethylene glycol overlayers and avidin-biotin technology

PubMed Central

Hynninen, Ville; Vuori, Leena; Hannula, Markku; Tapio, Kosti; Lahtonen, Kimmo; Isoniemi, Tommi; Lehtonen, Elina; Hirsimäki, Mika; Toppari, J. Jussi; Valden, Mika; Hytönen, Vesa P.

2016-01-01

A straightforward solution-based method to modify the biofunctionality of stainless steel (SS) using heterobifunctional silane-polyethylene glycol (silane-PEG) overlayers is reported. Reduced nonspecific biofouling of both proteins and bacteria onto SS and further selective biofunctionalization of the modified surface were achieved. According to photoelectron spectroscopy analyses, the silane-PEGs formed less than 10 Å thick overlayers with close to 90% surface coverage and reproducible chemical compositions. Consequently, the surfaces also became more hydrophilic, and the observed non-specific biofouling of proteins was reduced by approximately 70%. In addition, the attachment of E. coli was reduced by more than 65%. Moreover, the potential of the overlayer to be further modified was demonstrated by successfully coupling biotinylated alkaline phosphatase (bAP) to a silane-PEG-biotin overlayer via avidin-biotin bridges. The activity of the immobilized enzyme was shown to be well preserved without compromising the achieved antifouling properties. Overall, the simple solution-based approach enables the tailoring of SS to enhance its activity for biomedical and biotechnological applications. PMID:27381834

Improved antifouling properties and selective biofunctionalization of stainless steel by employing heterobifunctional silane-polyethylene glycol overlayers and avidin-biotin technology

NASA Astrophysics Data System (ADS)

Hynninen, Ville; Vuori, Leena; Hannula, Markku; Tapio, Kosti; Lahtonen, Kimmo; Isoniemi, Tommi; Lehtonen, Elina; Hirsimäki, Mika; Toppari, J. Jussi; Valden, Mika; Hytönen, Vesa P.

2016-07-01

A straightforward solution-based method to modify the biofunctionality of stainless steel (SS) using heterobifunctional silane-polyethylene glycol (silane-PEG) overlayers is reported. Reduced nonspecific biofouling of both proteins and bacteria onto SS and further selective biofunctionalization of the modified surface were achieved. According to photoelectron spectroscopy analyses, the silane-PEGs formed less than 10 Å thick overlayers with close to 90% surface coverage and reproducible chemical compositions. Consequently, the surfaces also became more hydrophilic, and the observed non-specific biofouling of proteins was reduced by approximately 70%. In addition, the attachment of E. coli was reduced by more than 65%. Moreover, the potential of the overlayer to be further modified was demonstrated by successfully coupling biotinylated alkaline phosphatase (bAP) to a silane-PEG-biotin overlayer via avidin-biotin bridges. The activity of the immobilized enzyme was shown to be well preserved without compromising the achieved antifouling properties. Overall, the simple solution-based approach enables the tailoring of SS to enhance its activity for biomedical and biotechnological applications.

Influence of surface treatment on shear bond strength of orthodontic brackets.

PubMed

Brunharo, Ione Helena Vieira Portella; Fernandes, Daniel Jogaib; de Miranda, Mauro Sayão; Artese, Flavia

2013-01-01

The shear bond strength of orthodontic brackets bonded to micro-hybrid and micro-particulate resins under different surface treatment methods was assessed. Two hundred and eighty test samples were divided into 28 groups (n = 10), where 140 specimens were filled with Durafill micro-particulate resin and 140 with Charisma composite. In 140 samples, a coupling agent (silane) was applied. The surface treatment methods were: Phosphoric and hydrofluoric acid etching, sodium bicarbonate and aluminum oxide blasting, stone and burs. A Universal Instron Machine was used to apply an occlusal shear force directly to the resin composite bracket surface at a speed of 0.5 mm/min. The means were compared using analysis of variance and multivariate regression to assess the interaction between composites and surface treatment methods. Means and standard deviations for the groups were: Sodium bicarbonate jet 11.27 ± 2.78; burs 9.26 ± 3.01; stone 7.95 ± 3.67; aluminum oxide blasting 7.04 ± 3.21; phosphoric acid 5.82 ± 1.90; hydrofluoric acid 4.54 ± 2.87, and without treatment 2.75 ± 1.49. An increase of 1.94 MPa in shear bond strength was seen in Charisma groups. Silane agent application reduced the Charisma shear bond strength by 0.68 Mpa, but increased Durafill means for bicarbonate blasting (0.83), burs (0.98) and stone drilling (0.46). The sodium bicarbonate blasting, burs and stone drilling methods produced adequate shear bond strength and may be suitable for clinical use. The Charisma micro hybrid resin composite showed higher shear bond means than Durafill micro particle composite.

Tensile strength of glass fiber posts submitted to different surface treatments.

PubMed

Faria, Maria Isabel A; Gomes, Érica Alves; Messias, Danielle Cristine; Silva Filho, João Manoel; Souza Filho, Celso Bernardo; Paulino, Silvana Maria

2013-01-01

The aim of this in vitro study was to evaluate the tensile strength of glass fiber posts submitted to different surface treatments. Forty-eight maxillary canines had their crowns sectioned and root canals endodontically treated. The roots were embedded in acrylic resin and distributed into 3 groups according to the surface treatment: Group I: the posts were treated with silane agent for 30 s and adhesive; Group II: the posts were cleaned with alcohol before treatment with silane agent and adhesive; Group III: the posts were submitted to conditioning with 37% phosphoric acid for 30 s before treatment with silane agent and adhesive. Each group was divided into 2 subgroups for adhesive polymerization or not before insertion into the canal: A - adhesive was not light cured and B - adhesive was light cured. All posts were cemented with Panavia F and the samples were subjected to tensile strength test in a universal testing machine at crosshead speed of 1 mm/min. Data were submitted to one-way ANOVA and Tukey's test at 5% significance level. There was statistically significant difference (p<0.01) only between group GIII-B and groups GI-A and GI-B. No significant difference was found among the other groups (p>0.05). It was concluded that the products used for cleaning the posts influenced the retention regardless of adhesive light curing.

Formation of functionalized nanoclusters by solvent evaporation and their effect on the physicochemical properties of dental composite resins.

PubMed

Rodríguez, Henry A; Giraldo, Luis F; Casanova, Herley

2015-07-01

The aim of this work was to study the effect of silica nanoclusters (SiNC), obtained by a solvent evaporation method and functionalized by 3-methacryloxypropyltrimethoxysilane (MPS) and MPS+octyltrimethoxysilane (OTMS) (50/50wt/wt), on the rheological, mechanical and sorption properties of urethane dimethylacrylate (UDMA)/triethylenglycol dimethacrylate (TEGDMA) (80/20wt/wt) resins blend. Silica nanoparticles (SiNP) were silanized with MPS or MPS+OTMS (50/50wt/wt) and incorporated in an UDMA-isopropanol mix to produce functionalized silica nanoclusters after evaporating the isopropanol. The effect of functionalized SiNC on resins rheological properties was determined by large and small deformation tests. Mechanical, thermal, sorption and solubility properties were evaluated for composite materials. The UDMA/TEGDMA (80/20wt/wt) resins blend with added SiNC (ca. 350nm) and functionalized with MPS showed a Newtonian flow behavior associated to their spheroidal shape, whereas the resins blend with nanoclusters silanized with MPS+OTMS (50/50wt/wt) (ca. 400nm) showed a shear-thinning behavior due to nanoclusters irregular shape. Composite materials prepared with bare silica nanoclusters showed lower compressive strength than functionalized silica nanoclusters. MPS functionalized nanoclusters showed better mechanical properties but higher water sorption than functionalized nanoclusters with both silane coupling agents, MPS and OTMS. The solvent evaporation method applied to functionalized nanoparticles showed to be an alternative way to the sinterization method for producing nanoclusters, which improved some dental composite mechanical properties and reduced water sorption. The shape of functionalized silica nanoclusters showed to have influence on the rheological properties of SiNC resin suspensions and the mechanical and sorption properties of light cured composites. Copyright © 2015 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Effect of Surface-Modified TiO2 Nanoparticles on the Anti-Ultraviolet Aging Performance of Foamed Wheat Straw Fiber/Polypropylene Composites

PubMed Central

Xuan, Lihui; Han, Guangping; Wang, Dong; Cheng, Wanli; Gao, Xun; Chen, Feng; Li, Qingde

2017-01-01

Surface modification and characterization of titanium dioxide (TiO2) nanoparticles and their roles in thermal, mechanical, and accelerated aging behavior of foamed wheat straw fiber/polypropylene (PP) composites are investigated. To improve the dispersion of nanoparticles and increase the possible interactions between wheat straw fiber and the PP matrix, the surface of the TiO2 nanoparticles was modified with ethenyltrimethoxy silane (A171), a silane coupling agent. The grafting of A171 on the TiO2 nanoparticles’ surface was characterized by Fourier transform infrared spectroscopy (FTIR). The wheat straw fibers treated with A171 and modified TiO2 nanoparticles were characterized by FTIR and thermogravimetric analysis (TGA). FTIR spectra confirmed that the organic functional groups of A171 were successfully grafted onto the TiO2 nanoparticles and wheat straw fibers, and the modified TiO2 nanoparticles were adsorbed onto the wheat straw fibers. Thermogravimetric analysis showed that a higher thermal stability of the wheat straw fiber was obtained with the modified TiO2 nanoparticles. The flexural, tensile, and impact properties were improved. A higher ultraviolet (UV) stability of the samples treated with modified TiO2 nanoparticles was exhibited by the study of the color change and loss in mechanical properties. PMID:28772816

Chemical treatment for silica-containing glass surfaces

DOEpatents

Grabbe, Alexis; Michalske, Terry Arthur; Smith, William Larry

1999-01-01

Dehydroxylated, silica-containing, glass surfaces are known to be at least partially terminated by strained siloxane rings. According to the invention, a surface of this kind is exposed to a selected silane compound or mixture of silane compounds under reaction-promoting conditions. The ensuing reaction results in opening of the strained siloxane rings, and termination of surface atoms by chemical species, such as organic or organosilicon species, having desirable properties. These species can be chosen to provide qualities such as hydrophobicity, or improved coupling to a polymeric coating.

Chemical treatment for silica-containing glass surfaces

DOEpatents

Grabbe, Alexis; Michalske, Terry Arthur; Smith, William Larry

1998-01-01

Dehydroxylated, silica-containing, glass surfaces are known to be at least partially terminated by strained siloxane rings. According to the invention, a surface of this kind is exposed to a selected silane compound or mixture of silane compounds under reaction-promoting conditions. The ensuing reaction results in opening of the strained siloxane rings, and termination of surface atoms by chemical species, such as organic or organosilicon species, having desirable properties. These species can be chosen to provide qualities such as hydrophobicity, or improved coupling to a polymeric coating.

Chemical treatment for silica-containing glass surfaces

DOEpatents

Grabbe, Alexis; Michalske, Terry Arthur; Smith, William Larry

1999-01-01

Dehydroxylated, silica-containing, glass surfaces are known to be at least partially terminated by strained siloxane rings. According to the invention, a surface of this kind is exposed to a selected silane compound or mixture of silane compounds under reaction-promoting conditons. The ensuing reaction results in opening of the strained siloxane rings, and termination of surface atoms by chemical species, such as organic or organosilicon species, having desirable properties. These species can be chosen to provide qualities such as hydrophobicity, or improved coupling to a polymeric coating.

Protein attachment to silane-functionalized porous silicon: A comparison of electrostatic and covalent attachment.

PubMed

Baranowska, Malgorzata; Slota, Agata J; Eravuchira, Pinkie J; Alba, Maria; Formentin, Pilar; Pallarès, Josep; Ferré-Borrull, Josep; Marsal, Lluís F

2015-08-15

Porous silicon (pSi) is a prosperous biomaterial, biocompatible, and biodegradable. Obtaining regularly functionalized pSi surfaces is required in many biotechnology applications. Silane-PEG-NHS (triethoxysilane-polyethylene-glycol-N-hydroxysuccinimide) is useful for single-molecule studies due to its ability to attach to only one biomolecule. We investigate the functionalization of pSi with silane-PEG-NHS and compare it with two common grafting agents: APTMS (3-aminopropylotrimethoxysilane) as electrostatic linker, and APTMS modified with glutaraldehyde as covalent spacer. We show the arrangement of two proteins (collagen and bovine serum albumin) as a function of the functionalization and of the pore size. FTIR is used to demonstrate correct functionalization while fluorescence confocal microscopy reveals that silane-PEG-NHS results in a more uniform protein distribution. Reflection interference spectroscopy (RIfS) is used to estimate the attachment of linker and proteins. The results open a way to obtain homogenous chemical modified silicon supports with a great value in biosensing, drug delivery and cell biology. Copyright © 2015 Elsevier Inc. All rights reserved.

Novel Phenylethynyl Imide Silanes as Coupling Agents for Titanium Alloy

NASA Technical Reports Server (NTRS)

Park, C.; Lowther, S. E.; Smith, J. G., Jr.; Conell, J. W.; Hergenrother, P. M.; SaintClair, T. L.

2004-01-01

The durability of titanium (Ti) alloys bonded with high temperature adhesives such as polyimides has failed to attain the level of performance required for many applications. The problem to a large part is attributed to the instability of the surface treatment on the Ti substrate. Although Ti alloy adhesive specimens with surface treatments such as chromic acid anodization, Pasa-Jell, Turco, etc. have provided high initial mechanical properties, these properties have decreased as a function of aging at ambient temperature and faster, when aged at elevated temperatures or in a hot-wet environment. As part of the High Speed Civil Transport program where Ti honeycomb sandwich structure must perform for 60,000 hours at 177 C, work was directed to the development of environmentally safe, durable Ti alloy surface treatments.

Effect of O-methyl-β-cyclodextrin-modified magnetic nanoparticles on the uptake and extracellular level of l-glutamate in brain nerve terminals.

PubMed

Horák, Daniel; Beneš, Milan; Procházková, Zuzana; Trchová, Miroslava; Borysov, Arsenii; Pastukhov, Artem; Paliienko, Konstantin; Borisova, Tatiana

2017-01-01

Changes in cholesterol concentration in the plasma membrane of presynaptic nerve terminals nonspecifically modulate glutamate transport and homeostasis in the central nervous system. Reduction of the cholesterol content in isolated rat brain nerve terminals (synaptosomes) using cholesterol-depleting agents decreases the glutamate uptake and increases the extracellular level of glutamate in nerve terminals. Extraction of cholesterol from the plasma membrane and its further removal from the synaptosomes by external magnetic field can be achieved by means of magnetic nanoparticles with immobilized cholesterol-depleting agent such as O-methyl-β-cyclodextrin (MCD). A simple approach is developed for preparation of maghemite (γ-Fe 2 O 3 ) nanoparticles containing chemically bonded MCD. The method is based on preparation of a silanization agent containing MCD. It is synthesized by the reaction of triethoxy(3-isocyanatopropyl)silane with MCD. Base-catalyzed silanization of superparamagnetic γ-Fe 2 O 3 provides a relatively stable colloid product containing 48μmol of MCDg -1 . MCD-modified γ-Fe 2 O 3 nanoparticles decrease the initial rate of the uptake and accumulation of l-[ 14 C]glutamate and increase the extracellular l-[ 14 C]glutamate level in the preparation of nerve terminals. The effect of MCD-immobilized nanoparticles is the same as that of MCD solution; moreover, magnetic manipulation of the nanoparticles enables removal of bonded cholesterol. Copyright © 2016 Elsevier B.V. All rights reserved.

Influence of the type of solvent on the development of superhydrophobicity from silane-based solution containing nanoparticles

NASA Astrophysics Data System (ADS)

Pantoja, M.; Abenojar, J.; Martinez, M. A.

2017-03-01

Superhydrophobic surfaces are very appealing for numerous industrial applications due to their self-cleaning capacity. Although there are different methods to manufacture superhydrophobic surfaces, some of them do not keep the aesthetic appearance of the neat surface. Sol-gel processes are a valid alternative when transparent coatings are desired. The main goal of this research is to study the viability of this method by making superhydrophobic coatings from silane-based solution containing SiO2 nanoparticles. The effect of using different solvents is investigated, as well as the role played by the different components of the solution (silane, nanoparticles and solvent). Solutions of methyltrimethoxisilane (MTS) and tetraethoxysilane (TEOS) and 1% of SiO2 (%wt) were prepared with different solvents (ethanol, ethanol/water and white spirit). The hydrophobicity of the developed coatings is studied using contact angle measurements, while the aesthetic appearance is evaluated with gloss and color measurements. Also, infrared spectroscopy, dynamic light scattering (DSL), and surface tension measurements are used to study the silane solutions. The results show that the capacity of solvents to promote the dispersion of the nanoparticles is crucial to ensuring superhydrophobicity, since these agglomerates provide the micro- and nano- surface roughness required to get a hierarchical structure. However, the combined use of silanes and nanoparticles is key to make a superhydrophobic surface because physical (the surface roughness provided by nanoparticles) and chemical characteristics (hydrophobicity provided by silanes) are coupled.

Method for chemical surface modification of fumed silica particles

DOEpatents

Grabbe, Alexis; Michalske, Terry Arthur; Smith, William Larry

1999-01-01

Dehydroxylated, silica-containing, glass surfaces are known to be at least partially terminated by strained siloxane rings. According to the invention, a surface of this kind is exposed to a selected silane compound or mixture of silane compounds under reaction-promoting conditions. The ensuing reaction results in opening of the strained siloxane rings, and termination of surface atoms by chemical species, such as organic or organosilicon species, having desirable properties. These species can be chosen to provide qualities such as hydrophobicity, or improved coupling to a polymeric coating.

Flat-plate solar array project. Volume 2: Silicon material

NASA Technical Reports Server (NTRS)

Lutwack, R.

1986-01-01

The goal of the Silicon Material Task, a part of the Flat Plate Solar Array (FSA) Project, was to develop and demonstate the technology for the low cost production of silicon of suitable purity to be used as the basic material for the manufacture of terrestrial photovoltaic solar cells. Summarized are 11 different processes for the production of silicon that were investigated and developed to varying extent by industrial, university, and Government researchers. The silane production section of the Union Carbide Corp. (UCC) silane process was developed completely in this program. Coupled with Siemens-type chemical vapor deposition reactors, the process was carried through the pilot stage. The overall UCC process involves the conversion of metallurgical-grade silicon to silane followed by decomposition of the silane to purified silicon. The other process developments are described to varying extents. Studies are reported on the effects of impurities in silicon on both silicon-material properties and on solar cell performance. These studies on the effects of impurities yielded extensive information and models for relating specific elemental concentrations to levels of deleterious effects.

Flat-plate solar array project. Volume 2: Silicon material

NASA Astrophysics Data System (ADS)

Lutwack, R.

1986-10-01

The goal of the Silicon Material Task, a part of the Flat Plate Solar Array (FSA) Project, was to develop and demonstate the technology for the low cost production of silicon of suitable purity to be used as the basic material for the manufacture of terrestrial photovoltaic solar cells. Summarized are 11 different processes for the production of silicon that were investigated and developed to varying extent by industrial, university, and Government researchers. The silane production section of the Union Carbide Corp. (UCC) silane process was developed completely in this program. Coupled with Siemens-type chemical vapor deposition reactors, the process was carried through the pilot stage. The overall UCC process involves the conversion of metallurgical-grade silicon to silane followed by decomposition of the silane to purified silicon. The other process developments are described to varying extents. Studies are reported on the effects of impurities in silicon on both silicon-material properties and on solar cell performance. These studies on the effects of impurities yielded extensive information and models for relating specific elemental concentrations to levels of deleterious effects.

Production and Structural Investigation of Polyethylene Composites with Modified Kaolin

NASA Astrophysics Data System (ADS)

Domka, L.; Malicka, A.; Stachowiak, N.

2008-08-01

The study was undertaken to evaluate the effect of the filler (kaolin) modification with silane coupling agents on the properties of the polyethylene (HDPE Hostalen ACP 5831) composites. Powder mineral fillers are added to polymers to modify the properties of the latter and to reduce the cost of their production. A very important factor is the filler dispersion in the polymer matrix. Kaolin modified with 3-methacryloxypropyltrimethoxysilane and pure kaolin were characterised by surface area, pore size, water absorbing capacity, paraffin oil absorbing capacity, bulk density, scanning electron microscopy observations and X-ray diffraction measurements. Their performance was characterised by determination of the mechanical resistance upon static stretching and tearing, and their structure was observed in scanning electron microscopy images. The results were compared to those obtained for the composites with unmodified filler and pure HDPE.

Immobilization of Chlorosulfonyl-Calix[4]arene onto the surface of silica gel through the directly estrification

NASA Astrophysics Data System (ADS)

Taghvaei-Ganjali, Saeed; Zadmard, Reza; Saber-Tehrani, Mandana

2012-06-01

For the first time Chlorosulfonyl-Calix[4]arene has been chemically bonded to silica gel through the directly estrification without silane coupling agent to prepare Chlorosulfonyl-Calix[4]arene-bonded silica gel. Sample characterization was performed by various techniques such as elemental analysis, Fourier transform infrared (FTIR) spectroscopy, scanning electron microscopy (SEM), energy dispersive X-ray analysis (EDAX), powder X-ray diffraction (XRD), N2 adsorption-desorption, thermal gravimetric analysis (TGA), 29Si CP/MAS spectroscopy and acid-base titration. All data approve the successful incorporation of organic group via covalent bond. From the comparison between sulfur content determined by elemental analysis and the number of H+ determined by acid-base titration, it was shown that two ester units took place onto the new synthesized sample and two acidic sites exist on the surface.

Reduced adherence of Candida to silane-treated silicone rubber.

PubMed

Price, C L; Williams, D W; Waters, M G J; Coulthwaite, L; Verran, J; Taylor, R L; Stickler, D; Lewis, M A O

2005-07-01

Silicone rubber is widely used in the construction of medical devices that can provide an essential role in the treatment of human illness. However, subsequent microbial colonization of silicone rubber can result in clinical infection or device failure. The objective of this study was to determine the effectiveness of a novel silane-treated silicone rubber in inhibiting microbial adherence and material penetration. Test material was prepared by a combination of argon plasma discharge treatment and fluorinated silane coupling. Chemicophysical changes were then confirmed by X-ray photoelectron spectroscopy, contact-angle measurement, and atomic force microscopy. Two separate adherence assays and a material penetration assay assessed the performance of the new material against four strains of Candida species. Results showed a significant reduction (p < 0.01) of Candida albicans GDH 2346 adherence to silane-treated silicone compared with untreated controls. This reduction was still evident after the incorporation of saliva into the assay. Adherence inhibition also occurred with Candida tropicalis MMU and Candida krusei NCYC, although this was assay dependent. Reduced penetration of silane-treated silicone by Candida was evident when compared to untreated controls, plaster-processed silicone, and acrylic-processed silicone. To summarize, a novel silicone rubber material is described that inhibits both candidal adherence and material penetration. The clinical benefit and performance of this material remains to be determined. Copyright 2005 Wiley Periodicals, Inc.

Ultrasonic activated efficient synthesis of chromenes using amino-silane modified Fe3O4 nanoparticles: A versatile integration of high catalytic activity and facile recovery

NASA Astrophysics Data System (ADS)

Safari, Javad; Zarnegar, Zohre

2014-08-01

An efficient synthesis of 2-amino-4H-chromenes is achieved by one pot three component coupling reaction of aldehyde, malononitrile, and resorcinol using amino-silane modified Fe3O4 nanoparticles (MNPs-NH2) heterogeneous nanocatalyst under sonic condition. The attractive advantages of the present process are mild reaction conditions, short reaction times, easy isolation of products, good yields and simple operational procedures. Combination of the advantages of ultrasonic irradiation and magnetic nanoparticles provides important methodology to carry out catalytic transformations.

Bioinspired Catecholic Primers for Rigid and Ductile Dental Resin Composites.

PubMed

Shin, Eeseul; Ju, Sung Won; An, Larry; Ahn, Eungjin; Ahn, Jin-Soo; Kim, Byeong-Su; Ahn, B Kollbe

2018-01-17

In the construction of dental restorative polymer composite materials, surface priming on mineral fillers is essential to improve the mechanical performance of the composites. Here we present bioinspired catechol-functionalized primers for a tougher dental resin composite containing glass fillers. The catecholic primers with different polymerizable end groups were designed and then coated on glass surfaces using a simple drop-casting or dip-coating process. The surface binding ability and possible cross-linking (coupling or chemical bridging between the glass substrate and the dental resin) of the catecholic bifunctional primers were evaluated using atomic force microscopy, contact angle measurements, and the knife shear bonding test and compared to a state-of-the-art silane-based coupling agent. Various mechanical tests including shrinkage and compression tests of the dental resin composites were also conducted. Compression tests of the composites containing the catecholic primed fillers exhibited enhanced mechanical properties, owing to the bidentate hydrogen bonding of catechol moieties to the oxide mineral surface. Furthermore, the superior biocompatibility of the primed surface was confirmed via cell attachment assay, thus providing applicability of catecholic primers for practical dental and biomedical applications.

Chemical modification of polyvinyl chloride and silicone elastomer in inhibiting adhesion of Aeromonas hydrophila.

PubMed

Kregiel, Dorota; Berlowska, Joanna; Mizerska, Urszula; Fortuniak, Witold; Chojnowski, Julian; Ambroziak, Wojciech

2013-07-01

Disease-causing bacteria of the genus Aeromonas are able to adhere to pipe materials, colonizing the surfaces and forming biofilms in water distribution systems. The aim of our research was to study how the modification of materials used commonly in the water industry can reduce bacterial cell attachment. Polyvinyl chloride and silicone elastomer surfaces were activated and modified with reactive organo-silanes by coupling or co-crosslinking silanes with the native material. Both the native and modified surfaces were tested using the bacterial strain Aeromonas hydrophila, which was isolated from the Polish water distribution system. The surface tension of both the native and modified surfaces was measured. To determine cell viability and bacterial adhesion two methods were used, namely plate count and luminometry. Results were expressed in colony-forming units (c.f.u.) and in relative light units (RLU) per cm(2). Almost all the chemically modified surfaces exhibited higher anti-adhesive and anti-microbial properties in comparison to the native surfaces. Among the modifying agents examined, poly[dimethylsiloxane-co-(N,N-dimethyl-N-n-octylammoniopropyl chloride) methylsiloxane)] terminated with hydroxydimethylsilyl groups (20 %) in silicone elastomer gave the most desirable results. The surface tension of this modifier, was comparable to the non-polar native surface. However, almost half of this value was due to the result of polar forces. In this case, in an adhesion analysis, only 1 RLU cm(-2) and less than 1 c.f.u. cm(-2) were noted. For the native gumosil, the results were 9,375 RLU cm(-2) and 2.5 × 10(8) c.f.u. cm(-2), respectively. The antibacterial activity of active organo-silanes was associated only with the carrier surface because no antibacterial compounds were detected in liquid culture media, in concentrations that were able to inhibit cell growth.

Ceramic Surface Treatment with a Single-component Primer: Resin Adhesion to Glass Ceramics.

PubMed

Prado, Mayara; Prochnow, Catina; Marchionatti, Ana Maria Estivalete; Baldissara, Paolo; Valandro, Luiz Felipe; Wandscher, Vinicius Felipe

2018-04-19

To evaluate the microshear bond strength (μSBS) of composite cement bonded to two machined glass ceramics and its durability, comparing conventional surface conditioning (hydrofluoric acid + silane) to a one-step primer (Monobond Etch & Prime). Machined slices of lithium disilicate ceramic (LDC) (IPS e.max CAD) and feldspathic ceramic (FC) (VITA Mark II) glass ceramics were divided into two groups (n = 10) according to two factors: 1. surface treatment: HF+S (ca 5% hydrofluoric acid [IPS Ceramic Etching GEL] + silane coupling agent [SIL; Monobond Plus]) or MEP (single-component ceramic conditioner; Monobond Etch & Prime); 2. storage condition: baseline (without aging; tested 24 h after cementing) or aged (70 days of water storage + 12,000 thermal cycles). Composite cement (Multilink Automix, Ivoclar Vivadent) was applied to starch matrices on the treated ceramic surfaces and photoactivated. A μSBS test was performed (0.5 mm/min) and the failure pattern was determined. Contact angle and micromorphological analyses were also performed. Data were analyzed with Student's t-test (α = 5%). For both ceramic materials, HF+S resulted in higher mean μSBS (MPa) at baseline (LDC: HF+S 21.2 ± 2.2 > MEP 10.4 ± 2.4; FC: HF+S 19.6 ± 4.3 > MEP 13.5 ± 5.4) and after aging (LDC: HF+S 14.64 ± 2.31 > MEP 9 ± 3.4; FC HF+S: 14.73 ± 3.33 > MEP 11.1 ± 3.3). HF+S resulted in a statistically significant decrease in mean μSBS after aging (p = 0.0001), while MEP yielded no significant reduction. The main failure type was adhesive between composite cement and ceramic. HF+S resuted in the lowest contact angle. Hydrofluoric acid + silane resulted in higher mean μSBS than Monobond Etch & Prime for both ceramics; however, Monobond Etch & Prime had stable bonding after aging.

Evaluation of the effects of aging in synthetic saliva solution of both commercial and silanized Nd-Fe-B magnets for dental application

NASA Astrophysics Data System (ADS)

Fabiano, F.; Puliafito, V.; Calabrese, L.; Borsellino, C.; Bonaccorsi, L. M.; Giordano, A.; Fabiano, V.; Cordasco, G.

2016-04-01

Neodymium-iron-boron magnets are able to ensure a magnetic flux with high maximum energy product also at miniaturized size. In the past, due to their marked corrosion in saliva they were unsuccessfully implemented in orthodontic systems. Thereby, we propose a multi-layered organic-inorganic coating able to supply anticorrosion resistance, wear resistance and durability to the whole assembly. We evaluated the influence on the magnetic force of commercial nickel plated and silanized Nd-Fe-B during aging time in synthetic Fusayama saliva. Two magnets based-micromagnetic simulations were performed in order to analyze the magnetic field generated which is linked to the magnetic force. Our key results underline that the proposed hybrid coating does not affect the magnetic force of Nd-Fe-B magnets, moreover, preventing corrosion degradation in aggressive solution. Thus the limiting aspects avoiding the use of Nd-Fe-B magnets for orthodontic and prosthodontic applications can be overcome by using silane agents as surface coating.

1-butanethiol vapor sensing based on gold nanoparticle immobilized on glass slide by digital color analysis

NASA Astrophysics Data System (ADS)

Shokoufi, Nader; Adeleh, Sara

2017-12-01

We demonstrate that gold nanoparticles (GNPs) immobilized on silanized glass act as an optical sensor that is able to quantify 1-butanethiol vapor. GNPs optical properties in the visible region are dominated by the surface plasmon resonance (SPR). The high affinity between 1-butanethiol and GNPs through Au-s bond leads to change in plasmon feature of GNPs that immobilized on silanized glass and causes absorption decrease at 542 nm in SPR spectrum of GNPs. It can be used as an optical sensor for quantitative detection. In this research, the glass slide surface activated by aminopropyltriethoxysilane (APTES). Spherical GNPs immobilized on silanized glass by silanization agent. The sensor is based on the spectrophotometry and digital color analysis (DCA) through RGB. We monitored R value and linear range 50-700 µM (R 2  =  0.97) with 2.05% relative standard deviation and 26.5 µM value was achieved, for the limit of detection. This method represents advantages of metal gold nanoparticles and solid substrate stability in one package, being inexpensive and low time consuming is another advantage of our method that can be conducted in petrochemical, pharmaceutical industries, and for detection of rotten food in food industries.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Chen, Kuangcai; Lin, Chia -Cheng; Vela, Javier

In this study, three-layer core–shell plasmonic nanorods (Au/Ag/SiO 2–NRs), consisting of a gold nanorod core, a thin silver shell, and a thin silica layer, were synthesized and used as optical imaging probes under a differential interference contrast microscope for single particle orientation and rotational tracking. The localized surface plasmon resonance modes were enhanced upon the addition of the silver shell, and the anisotropic optical properties of gold nanorods were maintained. The silica coating enables surface functionalization with silane coupling agents and provides enhanced stability and biocompatibility. Taking advantage of the longitudinal LSPR enhancement, the orientation and rotational information of themore » hybrid nanorods on synthetic lipid bilayers and on live cell membranes were obtained with millisecond temporal resolution using a scientific complementary metal-oxide-semiconductor camera. The results demonstrate that the as-synthesized hybrid nanorods are promising imaging probes with improved sensitivity and good biocompatibility for single plasmonic particle tracking experiments in biological systems.« less

TOPICAL REVIEW: Surface modification and characterization for dispersion stability of inorganic nanometer-scaled particles in liquid media

NASA Astrophysics Data System (ADS)

Kamiya, Hidehiro; Iijima, Motoyuki

2010-08-01

Inorganic nanoparticles are indispensable for science and technology as materials, pigments and cosmetics products. Improving the dispersion stability of nanoparticles in various liquids is essential for those applications. In this review, we discuss why it is difficult to control the stability of nanoparticles in liquids. We also overview the role of surface interaction between nanoparticles in their dispersion and characterization, e.g. by colloid probe atomic force microscopy (CP-AFM). Two types of surface modification concepts, post-synthesis and in situ modification, were investigated in many previous studies. Here, we focus on post-synthesis modification using adsorption of various kinds of polymer dispersants and surfactants on the particle surface, as well as surface chemical reactions of silane coupling agents. We discuss CP-AFM as a technique to analyze the surface interaction between nanoparticles and the effect of surface modification on the nanoparticle dispersion in liquids.

Functionalized NaA nanozeolites labeled with 224,225Ra for targeted alpha therapy.

PubMed

Piotrowska, Agata; Leszczuk, Edyta; Bruchertseifer, Frank; Morgenstern, Alfred; Bilewicz, Aleksander

2013-01-01

The 223 Ra, 224 Ra, and 225 Ra radioisotopes exhibit very attractive nuclear properties for application in radionuclide therapy. Unfortunately the lack of appropriate bifunctional ligand for radium is the reason why these radionuclides have not found application in receptor-targeted therapy. In the present work, the potential usefulness of the NaA nanozeolite as a carrier for radium radionuclides has been studied. 224 Ra and 225 Ra, α-particle emitting radionuclides, have been absorbed in the nanometer-sized NaA zeolite (30-70 nm) through simple ion exchange. 224,225 Ra-nanozeolites exhibited very high stability in solutions containing physiological salt, EDTA, amino acids, and human serum. To make NaA nanozeolite particles dispersed in water their surface was modified with a silane coupling agent containing poly(ethylene glycol) molecules. This functionalization approach let us covalently attach a biomolecule to the NaA nanozeolite surface.

Treatment of high-latency microcapsules containing an aluminium complex with an epoxy-functionalised trialkoxysilane.

PubMed

Kamiya, Kazunobu; Suzuki, Noboru

2016-12-01

Some aluminium complexes are excellent catalysts of cationic polymerisation and are used for low-temperature and fast-curing adhesive, used in electronic part mounting. Microencapsulation is a suitable technique for getting high latency of the catalysts and long shelf life of the adhesives. For the higher latency in a cycloaliphatic epoxy compound, the microcapsule surface which retained small amount of aluminium complex was coated with epoxy polymer and the effect was examined. From the X-ray photoelectron spectroscopic results, the surface was recognised to be sufficiently coated and the differential scanning calorimetric analyses showed that the coating did not significantly affect the low-temperature and fast-curing properties of adhesive. After storing the mixture of cycloaliphatic epoxy compound, coated microcapsules, triphenylsilanol and silane coupling agent for 48 h at room temperature, the increase in viscosity was only 0.01 Pa s, resulting in the excellent shelf life.

A pH sensor based on electric properties of nanotubes on a glass substrate

PubMed Central

Nakamura, Motonori; Ishii, Atsushi; Subagyo, Agus; Hosoi, Hirotaka; Sueoka, Kazuhisa; Mukasa, Koichi

2007-01-01

We fabricated a pH-sensitive device on a glass substrate based on properties of carbon nanotubes. Nanotubes were immobilized specifically on chemically modified areas on a substrate followed by deposition of metallic source and drain electrodes on the area. Some nanotubes connected the source and drain electrodes. A top gate electrode was fabricated on an insulating layer of silane coupling agent on the nanotube. The device showed properties of ann-type field effect transistor when a potential was applied to the nanotube from the top gate electrode. Before fabrication of the insulating layer, the device showed that thep-type field effect transistor and the current through the source and drain electrodes depend on the buffer pH. The current increases with decreasing pH of the CNT solution. This device, which can detect pH, is applicable for use as a biosensor through modification of the CNT surface. PMID:21806848

Soft liquid phase adsorption for fabrication of organic semiconductor films on wettability patterned surfaces.

PubMed

Watanabe, Satoshi; Akiyoshi, Yuri; Matsumoto, Mutsuyoshi

2014-01-01

We report a soft liquid-phase adsorption (SLPA) technique for the fabrication of organic semiconductor films on wettability-patterned substrates using toluene/water emulsions. Wettability-patterned substrates were obtained by the UV-ozone treatment of self-assembled monolayers of silane coupling agents on glass plates using a metal mask. Organic semiconductor polymer films were formed selectively on the hydrophobic part of the wettability-patterned substrates. The thickness of the films fabricated by the SLPA technique is significantly larger than that of the films fabricated by dip-coating and spin-coating techniques. The film thickness can be controlled by adjusting the volume ratio of toluene to water, immersion angle, immersion temperature, and immersion time. The SLPA technique allows for the direct production of organic semiconductor films on wettability-patterned substrates with minimized material consumption and reduced number of fabrication steps.

High elastic modulus nanopowder reinforced resin composites for dental applications

NASA Astrophysics Data System (ADS)

Wang, Yijun

2007-12-01

Dental restorations account for more than $3 billion dollars a year on the market. Among them, all-ceramic dental crowns draw more and more attention and their popularity has risen because of their superior aesthetics and biocompatibility. However, their relatively high failure rate and labor-intensive fabrication procedure still limit their application. In this thesis, a new family of high elastic modulus nanopowder reinforced resin composites and their mechanical properties are studied. Materials with higher elastic modulus, such as alumina and diamond, are used to replace the routine filler material, silica, in dental resin composites to achieve the desired properties. This class of composites is developed to serve (1) as a high stiffness support to all-ceramic crowns and (2) as a means of joining independently fabricated crown core and veneer layers. Most of the work focuses on nano-sized Al2O3 (average particle size 47 nm) reinforcement in a polymeric matrix with 50:50 Bisphenol A glycidyl methacrylate (Bis-GMA): triethylene glycol dimethacrylate (TEGDMA) monomers. Surfactants, silanizing agents and primers are examined to obtain higher filler levels and enhance the bonding between filler and matrix. Silane agents work best. The elastic modulus of a 57.5 vol% alumina/resin composite is 31.5 GPa compared to current commercial resin composites with elastic modulus <15 GPa. Chemical additives can also effectively raise the hardness to as much as 1.34 GPa. Besides>alumina, diamond/resin composites are studied. An elastic modulus of about 45 GPa is obtained for a 57 vol% diamond/resin composite. Our results indicate that with a generally monodispersed nano-sized high modulus filler, relatively high elastic modulus resin-based composite cements are possible. Time-dependent behavior of our resin composites is also investigated. This is valuable for understanding the behavior of our material and possible fatigue testing in the future. Our results indicate that with effective coupling agents and higher filler loading, viscous flow can be greatly decreased due to the attenuation of mobility of polymer chains. Complementary studies indicate that our resin composites are promising for the proposed applications as a stiff support to all-ceramic crowns.

Development of a mucin4-targeting SPIO contrast agent for effective detection of pancreatic tumor cells in vitro and in vivo.

PubMed

Wu, Shou-Cheng; Chen, Yu-Jen; Lin, Yi-Jan; Wu, Tung-Ho; Wang, Yun-Ming

2013-11-27

In search of a unique and reliable contrast agent targeting pancreatic adenocarcinoma, new multifunctional nanoparticles (MnMEIO-silane-NH2-(MUC4)-mPEG NPs) were successfully developed in this study. Mucin4-expression levels were determined through different imaging studies in a panel of pancreatic tumor cells (HPAC, BxPC-3, and Panc-1) both in vitro and in vivo studies. The in vitro T2-weighted MR imaging study in HPAC and Panc-1 tumor cells treated with NPs showed -89.1 ± 5.7% and -0.9 ± 0.2% contrast enhancement, whereas in in vivo study, it is found to be -81.5 ± 4.5% versus -19.6 ± 5.2% (24 h postinjection, 7.0 T), respectively. The T2-weighted MR and optical imaging studies revealed that the novel contrast agent can specifically and effectively target to mucin4-expressing tumors in nude mice. Hence, it is suggested that MnMEIO-silane-NH2-(MUC4)-mPEG NPs are able to provide an efficient and targeted delivery of MUC4 antibodies to mucin4-expressing pancreatic tumors.

Surface modification of poly(dimethylsiloxane) for microfluidic assay applications

NASA Astrophysics Data System (ADS)

Séguin, Christine; McLachlan, Jessica M.; Norton, Peter R.; Lagugné-Labarthet, François

2010-02-01

The surface of a poly(dimethylsiloxane) (PDMS) film was imparted with patterned functionalities at the micron-scale level. Arrays of circles with diameters of 180 and 230 μm were functionalized using plasma oxidation coupled with aluminum deposition, followed by silanization with solutions of 3-aminopropyltrimethoxy silane (3-APTMS) and 3-mercaptopropyltrimethoxy silane (3-MPTMS), to obtain patterned amine and thiol functionalities, respectively. The modification of the samples was confirmed using X-ray photoelectron spectroscopy (XPS), gold nanoparticle adhesion coupled with optical microscopy, as well as by derivatization with fluorescent dyes. To further exploit the novel surface chemistry of the modified PDMS, samples with surface amine functionalities were used to develop a protein assay as well as an array capable of cellular capture and patterning. The modified substrate was shown to successfully selectively immobilize fluorescently labeled immunoglobulin G (IgG) by tethering Protein A to the surface, and, for the cellular arrays, C2C12 rat endothelial cells were captured. Finally, this novel method of patterning chemical functionalities onto PDMS has been incorporated into microfluidic channels. Finally, we demonstrate the in situ chemical modification of the protected PDMS oxidized surface within a microfluidic device. This emphasizes the potential of our method for applications involving micron-scale assays since the aluminum protective layer permits to functionalize the oxidized PDMS surface several weeks after plasma treatment simply after etching away the metallic thin film.

Silyl Radical Activation of Alkyl Halides in Metallaphotoredox Catalysis: A Unique Pathway for Cross-Electrophile Coupling.

PubMed

Zhang, Patricia; Le, Chi Chip; MacMillan, David W C

2016-07-06

A strategy for cross-electrophile coupling has been developed via the merger of photoredox and transition metal catalysis. In this report, we demonstrate the use of commercially available tris(trimethylsilyl)silane with metallaphotoredox catalysis to efficiently couple alkyl bromides with aryl or heteroaryl bromides in excellent yields. We hypothesize that a photocatalytically generated silyl radical species can perform halogen-atom abstraction to activate alkyl halides as nucleophilic cross-coupling partners. This protocol allows the use of mild yet robust conditions to construct Csp(3)-Csp(2) bonds generically via a unique cross-coupling pathway.

Friction and wear study of NR/SBR blends with Si3N4Filler

NASA Astrophysics Data System (ADS)

GaneshKumar, A.; Balaganesan, G.; Sivakumar, M. S.

2018-04-01

The aim of this paper is to investigate mechanical and frictional properties of natural rubber/styrene butadiene rubber (NR/SBR) blends with and without silicon nitride (Si3N4) filler. The rubber is surface modified by silane coupling agent (Si-69) for enhancing hydrophobic property. The Si3N4of percentage 0 1, 3, 5 and 7, is incorporated into NR/SBR rubber compounds with 20% precipitated silica. The specimens with and without fillers are prepared as per standard for tensile and friction testing. Fourier transform infrared (FTIR) spectroscopy test is conducted and it is inferred that the coupling agent is covalently bonded on the surface of Si3N4 particles and an organic coating layer is formed. The co-efficient of friction and specific wear rate of NR/SBR blends are examined using an in-house built friction tester in a disc-on-plate (DOP) configuration. The specimens are tested to find coefficient of friction (COF) against steel grip antiskid plate under dry, mud, wet and oil environmental conditions. It is found that the increase in tensile strength and modulus at low percentage of Si3N4 dispersion. It is also observed that increase in sliding friction co-efficient and decrease in wear rate for 1% of Si3N4 dispersion in NR/SBR blends. The friction tested surfaces are inspected using Scanning Electron Microscope (SEM) and 3D non contact surface profiler.

Isolation of N-linked glycopeptides by hydrazine-functionalized magnetic particles.

PubMed

Sun, Shisheng; Yang, Ganglong; Wang, Ting; Wang, Qinzhe; Chen, Chao; Li, Zheng

2010-04-01

We introduce a novel combination of magnetic particles with hydrazine chemistry, dubbed as hydrazine-functionalized magnetic particles (HFMP) for isolation of glycopeptides. Four methods have been developed and compared for the production of HFMP by hydrazine modification of the surface of the carboxyl and epoxy-silanized magnetic particles, respectively. The evaluation of the capability and specificity of HFMP as well as the optimization of the coupling condition for capturing of glycoproteins were systematically investigated. The results showed that HFMP prepared by adipic dihydrazide functionalization from carboxyl-silanized magnetic particles (HFCA) displayed the maximum capture capacity and isolated efficiency for glycoprotein. When measured with glycoproteins, the capacity of the HFCA (1 g) for coupling bovine fetuin was 130 +/- 5.3 mg. The capability of this method was also confirmed by successful isolation of all formerly glycosylated peptides from standard glycoproteins and identification of their glycosylation sites, which demonstrated the feasibility of the HFCA as an alternative solid support for isolation of glycoproteins/glycopeptides.

Tailored interphase structure for improved strength and energy absorption of composites

NASA Astrophysics Data System (ADS)

Gao, Xiao

Fiber reinforced polymeric composites are lightweight, high-strength and high impact-resistant materials used widely for various applications. It has been shown that the mechanical performance of composites are dependent on the interphase, a three-dimensional region of nanometer size in the vicinity of the fiber-matrix boundary that possesses properties different from those of either the fiber reinforcement or the matrix resin and governs the load transfer from matrix to fiber. This research conducts a systematic study on glass fiber-epoxy interphase structure by tailoring adhesion between constituents and the creation of textures to control strength and energy absorption through mechanical interlocking between glass fiber and epoxy matrix. Our objective is to establish the foundation for microstructural design and optimization of the composite's structural and impact performance. Two ways of roughening the glass fiber surface have been studied to create the mechanical interlocking between fiber and resin; the first technique involves forming in-situ islands on the glass fiber surface by using silane blends of Glycidoxypropyltrimethoxy silane (GPS) and Tetraethoxy silane (TEOS); the second technique applies a silane coupling agents based sizing with the incorporation of silica nanoparticles (Ludox TMA, 22 nm) onto the fiber surface. The microdroplet test was selected to characterize the influence of adhesion and mechanical interlocking effects on interphase properties of different sizing sized glass fiber reinforced epoxy systems. A suitable data reduction scheme enables the strength and specified energy absorbed due to debonding, dynamic sliding, and quasi-static sliding to be quantified. In order to validate the effect of tailored interphase structure, which is induced by creating mechanical interlocking between fiber and resin, on macroscopic composite properties, composite panels were made from these four different sizing sized glass fibers and tested using the punch shear test. The composite panel made from the hybrid sizing sized glass fiber exhibited improved strength and energy absorption consistent with the trends in micromechanical measurements. Through all failure stages under macromechanical testing, hybrid sizing sized glass fiber/epoxyamine composite panel shows an increase in the strength and total energy absorption by 13% and 26%, respectively, compared to the compatible sizing sized baseline. Both micromechanical and macromechanical tests demonstrate the significant influence of tailoring the interphase structure on improving the impact performance of the composites. The hybrid sizing with the incorporation of nanoparticles, in particular, can greatly improve the impact resistance (i.e. energy absorption) of composites without sacrificing its structural performance (i.e. strength).

Effect of various surface treatment methods on the bond strength of the heat-pressed ceramic samples.

PubMed

Saraçoğlu, A; Cura, C; Cötert, H S

2004-08-01

This in vitro study was conducted to evaluate the interaction between the shear bond strength and the surface treatment method for a commercial dental ceramic. Ninety bonded ceramic units were manufactured for this study. Each unit was made by luting two cylinder-shaped ceramic samples to each other with a resin-composite luting agent. The units were then divided into nine groups, containing 10 units in each group. Samples from each group were treated with one of the following: etching with 4.9% hydrofluoric acid for 10, 20 and 40 s, 9.5% hydrofluoric acid for 10, 20 and 40 s, 40% orthophosphoric acid for 40 s, air abrasion with alumina in 50-microm particles, and grinding with a high-speed diamond bur. The treated samples were then silanated and luted with a resin-composite luting agent. The luted units were then loaded to failure. Two samples from each group were neither silanated nor luted after the surface treatment procedure, and morphological changes obtained by various surface treatment regimens were investigated by scanning electron microscopy. A statistically significant difference was observed among the mean shear bond strengths of the groups prepared with different surface treatment techniques (P = 0.00). Hydrofluoric acid appeared to be the most suitable chemical medium to produce a reliable ceramic bond. Etching time and concentration of the acidic medium were also observed as important prognostic variates. Orthophosphoric acid treatment was observed to be the least effective surface treatment method on the heat-pressed ceramic samples. Physical applications such as bur grinding and air blasting maintained stronger bonds than the orthophosphoric acid, while producing weaker bonds than surfaces treated with hydrofluoric acid in all concentrations and etching periods. The effect of the silane priming agent was not considered in this study. Copyright 2004 Blackwell Publishing Ltd.

Processing and properties of ceramic matrix-polymer composites for dental applications

NASA Astrophysics Data System (ADS)

Huang, Hsuan Yao

The basic composite structure of natural hard tissue was used to guide the design and processing of dental restorative materials. The design incorporates the methodology of using inorganic minerals as the main structural phase reinforced with a more ductile but tougher organic phase. Ceramic-polymer composites were prepared by slip casting a porous ceramic structure, heating and chemical treating the porous preform, infiltrating with monomer and then curing. The three factors that determined the mechanical properties of alumina-polymer composites were the type of polymer used, the method of silane treatments, and the type of bond between particles in the porous preforms. Without the use of silane coupling agents, the composites were measured to have a lower strength. The composite with a more "flexible" porous alumina network had a greater ability to plastically dissipate the energy of propagating cracks. However, the aggressive nature of the alumina particles on opposing enamel requires that these alumina-polymer composites have a wear compatible coating for practical application. A route to dense bioactive apatite wollastonite glass ceramics (AWGC)-polymer composites was developed. The problems associated with glass dissolution into the aqueous medium for slip casting were overcome with the use of silane. The role of heating rate and development of ceramic compact microstructure on composite properties was explored. In general, if isothermal heating was not applied, decreasing heating rate increased glass crystallinity and particle-particle fusion, but decreased pore volume. Also composite strength and fracture toughness decreased while modulus and hardness increased with decreasing heating rate. If isothermal heating was applied, glass crystallinity, pore content, and composite mechanical properties showed relatively little change regardless of the initial heating rate. The potential of AWGC-polymer composites for dental and implant applications was explored. Strengths and toughnesses were not severely degraded by immersion in simulated body fluids up to 30 days. The composite elastic modulus approached that of hard tissues and its wear behavior with opposing tooth was excellent. Growth of apatite over the entire composite surface was achieved in SBF. Growth of apatite in human whole saliva was achieved on the bioactive glass surface, but not on the composite surface.

Solution-Based Synthesis of Crystalline Silicon from Liquid Silane through Laser and Chemical Annealing

DOE PAGES

Iyer, Ganjigunte R. S.; Hobbie, Erik K.; Guruvenket, Srinivasan; ...

2012-05-23

We report a solution process for the synthesis of crystalline silicon from the liquid silane precursor cyclohexasilane (Si 6H 12). Polysilane films were crystallized through thermal and laser annealing, with plasma hydrogenation at atmospheric pressure generating further structural changes in the films. The evolution from amorphous to microcrystalline is characterized using scanning electron microscopy (SEM), atomic force microscopy (AFM), Raman spectroscopy and impedance spectroscopy. A four-decade enhancement in the electrical conductivity is attributed to a disorder-order transition in a bonded Si network. Lastly, our results demonstrate a potentially attractive approach that employs a solution process coupled with ambient post-processing tomore » produce crystalline silicon thin films.« less

Surface functionalization of microwave plasma-synthesized silica nanoparticles for enhancing the stability of dispersions

NASA Astrophysics Data System (ADS)

Sehlleier, Yee Hwa; Abdali, Ali; Schnurre, Sophie Marie; Wiggers, Hartmut; Schulz, Christof

2014-08-01

Gas phase-synthesized silica nanoparticles were functionalized with three different silane coupling agents (SCAs) including amine, amine/phosphonate and octyltriethoxy functional groups and the stability of dispersions in polar and non-polar dispersing media such as water, ethanol, methanol, chloroform, benzene, and toluene was studied. Fourier transform infrared spectroscopy showed that all three SCAs are chemically attached to the surface of silica nanoparticles. Amine-functionalized particles using steric dispersion stabilization alone showed limited stability. Thus, an additional SCA with sufficiently long hydrocarbon chains and strong positively charged phosphonate groups was introduced in order to achieve electrosteric stabilization. Steric stabilization was successful with hydrophobic octyltriethoxy-functionalized silica nanoparticles in non-polar solvents. The results from dynamic light scattering measurements showed that in dispersions of amine/phosphonate- and octyltriethoxy-functionalized silica particles are dispersed on a primary particle level. Stable dispersions were successfully prepared from initially agglomerated nanoparticles synthesized in a microwave plasma reactor by designing the surface functionalization.

Recycling of asbestos tailings used as reinforcing fillers in polypropylene based composites.

PubMed

Zhai, Wensi; Wang, Yao; Deng, Yuan; Gao, Hongli; Lin, Zhen; Li, Mao

2014-04-15

In this work, asbestos tailings were recycled and used as reinforcing fillers to enhance the mechanical properties of polypropylene (PP). A silane coupling agent was used to chemically modify the asbestos tailings to increase the compatibility between asbestos tailings and polypropylene matrix. Both raw and chemically treated asbestos tailings with different loading levels (from 3 to 30 wt%) were utilized to fabricate composites. Mechanical properties of these composites have been investigated by dynamic mechanical analysis, tensile test and notched impact test. Results showed that hybridization of asbestos tailings in the composites enhanced the mechanical properties of neat PP evidently, and treated asbestos tailings/PP composites yielded even better mechanical properties compared with those of raw asbestos tailings/PP composites. This recycling method of asbestos tailings not only reduces disposal costs and avoids secondary pollution but also produces a new PP-based composite material with enhanced mechanical properties. Copyright © 2014 Elsevier B.V. All rights reserved.

Particle morphology dependent superhydrophobicity in treated diatomaceous earth/polystyrene coatings

NASA Astrophysics Data System (ADS)

Sedai, Bhishma R.; Alavi, S. Habib; Harimkar, Sandip P.; McCollum, Mark; Donoghue, Joseph F.; Blum, Frank D.

2017-09-01

Superhydrophobic surfaces have been prepared from three different types of diatomaceous earth (DE) particles treated with 3-(heptafluoroisopropoxy)propyltrimethoxysilane (HFIP-TMS) and low molecular mass polystyrene. The untreated particles, consisting of CelTix DE (disk shape), DiaFil DE (rod shape) and EcoFlat DE (irregular), were studied using particle size analysis, bulk density, pore volume and surface area analysis (via Brunauer-Emmett-Teller, BET, methods). The treated particles were characterized with thermogravimetric analysis (TGA), contact angles, scanning electron microscopy, profilometry, and FTIR spectroscopy. The minimum amount of silane coupling agent on the DE surfaces required to obtain superhydrophobicity of the particles was determined and found to be dependent on the particle morphology. In the coatings made from different particles with 2.4 wt% HFIP-TMS, the minimum amounts of treated particles (loadings) for superhydrophobicity was determined with the less dense CelTix DE requiring about 30 wt%, DiaFil DE requiring about 40 wt%, and EcoFlat DE each requiring about 60 wt% loading of treated particles.

Silane surface modification effects on the electromagnetic properties of phosphatized iron-based SMCs

NASA Astrophysics Data System (ADS)

Fan, Liang-Fang; Hsiang, Hsing-I.; Hung, Jia-Jing

2018-03-01

It is difficult to achieve homogeneous phosphatized iron powder dispersion in organic resins during the preparation of soft magnetic composites (SMCs). Inhomogeneous iron powder mixing in organic resins generally leads to the formation of micro-structural defects in SMCs and hence causes the magnetic properties to become worse. Phosphatized iron powder dispersion in organic resins can be improved by coating the phosphatized iron powder surfaces with a coupling agent. This study investigated the (3-aminopropyl) triethoxysilane (APTES) surface modification effects on the electromagnetic properties of phosphatized iron-based soft magnetic composites (SMCs). The results showed that the phosphatized iron powder surface can be modified using APTES to improve the phosphatized iron powder and epoxy resin compatibility and hence enhance phosphate iron powder epoxy mixing. The tensile strength, initial permeability, rated current under DC-bias superposition and magnetic loss in SMCs prepared using phosphatized iron powders can be effectively improved using APTES surface modification, which provides a promising candidate for power chip inductor applications.

Silicon Oxycarbide/Carbon Nanohybrids with Tiny Silicon Oxycarbide Particles Embedded in Free Carbon Matrix Based on Photoactive Dental Methacrylates.

PubMed

Wang, Meimei; Xia, Yonggao; Wang, Xiaoyan; Xiao, Ying; Liu, Rui; Wu, Qiang; Qiu, Bao; Metwalli, Ezzeldin; Xia, Senlin; Yao, Yuan; Chen, Guoxin; Liu, Yan; Liu, Zhaoping; Meng, Jian-Qiang; Yang, Zhaohui; Sun, Ling-Dong; Yan, Chun-Hua; Müller-Buschbaum, Peter; Pan, Jing; Cheng, Ya-Jun

2016-06-08

A new facile scalable method has been developed to synthesize silicon oxycarbide (SiOC)/carbon nanohybrids using difunctional dental methacrylate monomers as solvent and carbon source and the silane coupling agent as the precursor for SiOC. The content (from 100% to 40% by mass) and structure (ratio of disordered carbon over ordered carbon) of the free carbon matrix have been systematically tuned by varying the mass ratio of methacryloxypropyltrimethoxysilane (MPTMS) over the total mass of the resin monomers from 0.0 to 6.0. Compared to the bare carbon anode, the introduction of MPTMS significantly improves the electrochemical performance as a lithium-ion battery anode. The initial and cycled discharge/charge capacities of the SiOC/C nanohybrid anodes reach maximum with the MPTMS ratio of 0.50, which displays very good rate performance as well. Detailed structures and electrochemical performance as lithium-ion battery anodes have been systematically investigated. The structure-property correlation and corresponding mechanism have been discussed.

Mechanical properties of HDPE/UHMWPE blends: effect of filler loading and filler treatment.

PubMed

Lai, K L K; Roziyanna, A; Ogunniyi, D S; Zainal, Arifin M I; Azlan, Ariffin A

2004-05-01

Various blend ratios of high-density polyethylene (HDPE) and ultra high molecular weight polyethylene (UHMWPE) were prepared with the objective of determining their suitability as biomaterials. In the unfilled state, a blend of 50/50 (HDPE/UHMWPE) ratio by weight was found to yield optimum properties in terms of processability and mechanical properties. Hydroxyapatite (HA) was compounded with the optimum blend ratio. The effects of HA loading, varied from 0 to 50wt% for both filled and unfilled blends were tested for mechanical properties. It was found that the inclusion of HA in the blend led to a remarkable improvement of mechanical properties compared to the unfilled blend. In order to improve the bonding between the polymer blend and the filler, the HA used was chemically treated with a coupling agent known as 3-(trimethoxysiyl) propyl methacrylate and the treated HA was mixed into the blend. The effect of mixing the blend with silane-treated HA also led to an overall improvement of mechanical properties.

Shear bond, wettability and AFM evaluations on CO2 laser-irradiated CAD/CAM ceramic surfaces.

PubMed

El Gamal, Ahmed; Medioni, Etienne; Rocca, Jean Paul; Fornaini, Carlo; Muhammad, Omid H; Brulat-Bouchard, Nathalie

2017-05-01

The purpose of this study is to determine the CO 2 laser irradiation in comparison with sandblasting (Sb), hydrofluoric acid (Hf) and silane coupling agent (Si) on shear bond strength (SBS), roughness (Rg) and wettability (Wt) of resin cement to CAD/CAM ceramics. Sixty (CAD/CAM) ceramic discs were prepared and distributed into six different groups: group A, control lithium disilicate (Li); group B, control zirconia (Zr); group C, Li: CO 2 /HF/Si; group D, Li: HF/Si; group E, Zr: CO 2 /Sb/Si; group F, Zr: Sb/Si. Result showed significant difference between irradiated and non-irradiated in terms of shear bond strength for zirconia ceramics (p value = 0.014). Moreover, partial surface wettability for irradiated and non-irradiated ceramics. Irradiated surface demonstrated more rough surface in lithium disilicate than zirconia ceramics. CO 2 irradiation could increase shear bond strength, surface roughness and wettability for both CAD/CAM ceramics.

An overview of biofunctionalization of metals in Japan

PubMed Central

Hanawa, Takao

2009-01-01

Surface modification is an important and predominant technique for obtaining biofunction and biocompatibility in metals for biomedical use. The surface modification technique is a process that changes the surface composition, structure and morphology of a material, leaving the bulk mechanical properties intact. A tremendous number of surface modification techniques using dry and wet processes to improve the hard tissue compatibility of titanium have been developed. Some are now commercially available. Most of these processes have been developed by Japanese institutions since the 1990s. A second approach is the immobilization of biofunctional molecules to the metal surface to control the adsorption of proteins and adhesion of cells, platelets and bacteria. The immobilization of poly(ethylene glycol) to a metal surface with electrodeposition and its effect on biofunction are reviewed. The creation of a metal–polymer composite is another way to obtain metal-based biofunctional materials. The relationship between the shear bonding strength and the chemical structure at the bonding interface of a Ti-segmentated polyurethane composite through a silane coupling agent is explained. PMID:19158014

Magnetic mesoporous silica nanoparticles: fabrication and their laccase immobilization performance.

PubMed

Wang, Feng; Guo, Chen; Yang, Liang-rong; Liu, Chun-Zhao

2010-12-01

Newly large-pore magnetic mesoporous silica nanoparticles (MMSNPs) with wormhole framework structures were synthesized for the first time by using tetraethyl orthosilicate as the silica source and amine-terminated Jeffamine surfactants as template. Iminodiacerate was attached on these MMSNPs through a silane-coupling agent and chelated with Cu(2+). The Cu(2+)-chelated MMSNPs (MMSNPs-CPTS-IDA-Cu(2+)) showed higher adsorption capacity of 98.1 mg g(-1)-particles and activity recovery of 92.5% for laccase via metal affinity adsorption in comparison with MMSNPs via physical adsorption. The Michaelis constant (K(m)) and catalytic constant (k(cat)) of laccase immobilized on the MMSNPs-CPTS-IDA-Cu(2+) were 3.28 mM and 155.4 min(-1), respectively. Storage stability and temperature endurance of the immobilized laccase on MMSNPs-CPTS-IDA-Cu(2+) increased significantly, and the immobilized laccase retained 86.6% of its initial activity after 10 successive batch reactions operated with magnetic separation. 2010 Elsevier Ltd. All rights reserved.

Effect of different adhesion strategies on bond strength of resin composite to composite-dentin complex.

PubMed

Özcan, M; Pekkan, G

2013-01-01

Service life of discolored and abraded resin composite restorations could be prolonged by repair or relayering actions. Composite-composite adhesion can be achieved successfully using some surface conditioning methods, but the most effective adhesion protocol for relayering is not known when the composite restorations are surrounded with dentin. This study evaluated the effect of three adhesion strategies on the bond strength of resin composite to the composite-dentin complex. Intact maxillary central incisors (N=72, n=8 per subgroup) were collected and the coronal parts of the teeth were embedded in autopolymerized poly(methyl tfr54methacrylate) surrounded by a polyvinyl chloride cylinder. Cylindrical cavities (diameter: 2.6 mm; depth: 2 mm) were opened in the middle of the labial surfaces of the teeth using a standard diamond bur, and the specimens were randomly divided into three groups. Two types of resin composite, namely microhybrid (Quadrant Anterior Shine; AS) and nanohybrid (Grandio; G), were photo-polymerized incrementally in the cavities according to each manufacturer's recommendations. The composite-enamel surfaces were ground finished to 1200-grit silicone carbide paper until the dentin was exposed. The surfaces of the substrate composites and the surrounding dentin were conditioned according to one of the following adhesion protocols: protocol 1: acid-etching (dentin) + silica coating (composite) + silanization (composite) + primer (dentin) + bonding agent (dentin + composite); protocol 2: silica coating (composite) + acid-etching (dentin) + silanization (composite) + primer (dentin) + bonding agent (dentin + composite); and protocol 3: acid-etching (dentin) + primer (dentin) + silanization (composite) + bonding agent (dentin + composite). Applied primer and bonding agents were the corresponding materials of the composite manufacturer. Silica coating (CoJet sand, 30 μm) was achieved using a chairside air-abrasion device (distance: 10 mm; duration: four seconds in circular motion). After conditioning protocols, the repair resin was adhered to the substrate surfaces using transparent polyethylene molds (diameter: 3.6 mm) incrementally and photo-polymerized. The substrate-adherend combinations were as follows: AS-AS, G-G, AS-G. Shear force was applied to the adhesive interface in a Universal Testing Machine (crosshead speed: 1 mm/min). The types of failures were further evaluated and categorized as follows: 1) cohesive in the composite substrate and 2) adhesive at the interface. Bond strength values (MPa) were statistically analyzed using two-way analysis of variance and least significant difference post hoc tests (α=0.05). Significant effects of the adhesion strategy (p=0.006) and the composite type (p=0.000) were found. Interaction terms were not significant (p=0.292). Regardless of the substrate-adherend combination, protocol 1 (17-22 MPa) showed significantly higher results than did protocols 2 (15-17 MPa) and 3 (11-17 MPa) (p=0.028, p=0.002, respectively). The highest results were obtained from the G-G combination after all three protocols (17-22 MPa). The incidence of cohesive failures was more common when the substrate and the adherend were the same composite type (AS-AS: 87.5%, 87.5%, 75%; G-G: 100%, 75%, 50% for protocols 1, 2, and 3, respectively). When substrate and adherend were used interchangeably, adhesive failures were more frequent (25%, 50%, and 100% for protocol 1, 2, and 3, respectively). When the substrate and the adherend are of the same type, greater repair strength could be expected. In the repair of composites next to the dentin, depending on the composite type, conditioning the composite with silica coating and silanization after etching the dentin adds to the repair strength compared to the results obtained with silane application only.

The effects of hyaluronic acid incorporated as a wetting agent on lysozyme denaturation in model contact lens materials.

PubMed

Weeks, Andrea; Boone, Adrienne; Luensmann, Doerte; Jones, Lyndon; Sheardown, Heather

2013-09-01

Conventional and silicone hydrogels as models for contact lenses were prepared to determine the effect of the presence of hyaluronic acid on lysozyme sorption and denaturation. Hyaluronic acid was loaded into poly(2-hydroxyethyl methacrylate) and poly(2-hydroxyethyl methacrylate)/TRIS--methacryloxypropyltris (trimethylsiloxy silane) hydrogels, which served as models for conventional and silicone hydrogel contact lens materials. The hyaluronic acid was cross-linked using 1-ethyl-3-(3-dimethylaminopropyl)-carbodiimide in the presence of dendrimers. Active lysozyme was quantified using a Micrococcus lysodeikticus assay while total lysozyme was determined using 125-I radiolabeled protein. To examine the location of hyaluronic acid in the gels, 6-aminofluorescein labeled hyaluronic acid was incorporated into the gels using 1-ethyl-3-(3-dimethylaminopropyl)-carbodiimide chemistry and the gels were examined using confocal laser scanning microscopy. Hyaluronic acid incorporation significantly reduced lysozyme sorption in poly(2-hydroxyethyl methacrylate) (p < 0.00001) and poly(2-hydroxyethyl methacrylate)/TRIS--methacryloxypropyltris (trimethylsiloxy silane) (p < 0.001) hydrogels, with the modified materials sorbing only 20% and 16% that of the control, respectively. More importantly, hyaluronic acid also decreased lysozyme denaturation in poly(2-hydroxyethyl methacrylate) (p < 0.005) and poly(2-hydroxyethyl methacrylate)/TRIS--methacryloxypropyltris (trimethylsiloxy silane) (p < 0.02) hydrogels. The confocal laser scanning microscopy results showed that the hyaluronic acid distribution was dependent on both the material type and the molecular weight of hyaluronic acid. This study demonstrates that hyaluronic acid incorporated as a wetting agent has the potential to reduce lysozyme sorption and denaturation in contact lens applications. The distribution of hyaluronic acid within hydrogels appears to affect denaturation, with more surface mobile, lower molecular weight hyaluronic acid being more effective in preventing denaturation.

Timolol maleate release from hyaluronic acid-containing model silicone hydrogel contact lens materials.

PubMed

Korogiannaki, Myrto; Guidi, Giuliano; Jones, Lyndon; Sheardown, Heather

2015-09-01

This study was designed to assess the impact of a releasable wetting agent, such as hyaluronic acid (HA), on the release profile of timolol maleate (TM) from model silicone hydrogel contact lens materials. Polyvinylpyrrolidone (PVP) was used as an alternative wetting agent for comparison. The model lenses consisted of a hydrophilic monomer, either 2-hydroxyethyl methacrylate or N,N-dimethylacrylamide and a hydrophobic silicone monomer of methacryloxypropyltris (trimethylsiloxy) silane. The loading of the wetting and the therapeutic agent occurred during the synthesis of the silicone hydrogels through the method of direct entrapment. The developed materials were characterized by minimal changes in the water uptake, while lower molecular weight of HA improved their surface wettability. The transparency of the examined silicone hydrogels was found to be affected by the miscibility of the wetting agent in the prepolymer mixture as well as the composition of the developed silicone hydrogels. Sustained release of TM from 4 to 14 days was observed, with the drug transport occurring presumably through the hydrophilic domains of the silicone hydrogels. The release profile was strongly dependent on the hydrophilic monomer composition, the distribution of hydrophobic (silane) domains, and the affinity of the therapeutic agent for the silicone hydrogel matrix. Noncovalent entrapment of the wetting agent did not change the in vitro release duration and kinetics of TM, however the drug release profile was found to be controlled by the simultaneous release of TM and HA or PVP. In the case of HA, depending on the HA:drug ratio, the release rate was decreased and controlled by the release of HA, likely due to electrostatic interactions between protonated TM and anionic HA. Overall, partitioning of the drug within the hydrophilic domains of the silicone hydrogels as well as interactions with the wetting agent determined the drug release profile. © The Author(s) 2015.

Effects of Mechanical and Chemical Pretreatments of Zirconia or Fiber Posts on Resin Cement Bonding

PubMed Central

Li, Rui; Zhou, Hui; Wei, Wei; Wang, Chen; Sun, Ying Chun; Gao, Ping

2015-01-01

The bonding strength between resin cement and posts is important for post and core restorations. An important method of improving the bonding strength is the use of various surface pretreatments of the post. In this study, the surfaces of zirconia (fiber) posts were treated by mechanical and/or chemical methods such as sandblasting and silanization. The bonding strength between the zirconia (fiber) post and the resin cement was measured by a push-out method after thermocycling based on the adhesion to Panavia F 2.0 resin cement. The zirconia and fiber posts exhibited different bonding strengths after sandblasting and/or silanization because of the different strengths and chemical structures. The zirconia post showed a high bonding strength of up to 17.1 MPa after a combined treatment of sandblasting and silanization because of the rough surface and covalent bonds at the interface. This effect was also enhanced by using 1,2-bis(trimethoxysilyl)ethane for the formation of a flexible layer at the interface. In contrast, a high bonding strength of 13.9 MPa was obtained for the fiber post treated by silane agents because the sandblasting treatment resulted in damage to the fiber post, as observed by scanning electron microscopy. The results indicated that the improvement in the bonding strength between the post and the resin cement could be controlled by different chemical and/or mechanical treatments. Enhanced bonding strength depended on covalent bonding and the surface roughness. A zirconia post with high bonding strength could potentially be used for the restoration of teeth in the future. PMID:26066349

Bond strength of selected composite resin-cements to zirconium-oxide ceramic

PubMed Central

Fons-Font, Antonio; Amigó-Borrás, Vicente; Granell-Ruiz, María; Busquets-Mataix, David; Panadero, Rubén A.; Solá-Ruiz, Maria F.

2013-01-01

Objectives: The aim of this study was to evaluate bond strengths of zirconium-oxide (zirconia) ceramic and a selection of different composite resin cements. Study Design: 130 Lava TM cylinders were fabricated. The cylinders were sandblasted with 80 µm aluminium oxide or silica coated with CoJet Sand. Silane, and bonding agent and/or Clearfil Ceramic Primer were applied. One hundred thirty composite cement cylinders, comprising two dual-polymerizing (Variolink II and Panavia F) and two autopolymerizing (Rely X and Multilink) resins were bonded to the ceramic samples. A shear test was conducted, followed by an optical microscopy study to identify the location and type of failure, an electron microscopy study (SEM and TEM) and statistical analysis using the Kruskal-Wallis test for more than two independent samples and Mann-Whitney for two independent samples. Given the large number of combinations, Bonferroni correction was applied (α=0.001). Results: Dual-polymerizing cements provided better adhesion values (11.7 MPa) than the autopolymerizing (7.47 MPa) (p-value M-W<0.001). The worst techniques were Lava TM + sandblasting + Silane + Rely X; Lava TM + sandblasting + Silane + Multilink and Lava TM + CoJet + silane + Multilink. Adhesive failure (separation of cement and ceramic) was produced at a lesser force than cohesive failure (fracture of cement) (p-value M-W<0.001). Electron microscopy confirmed that the surface treatments modified the zirconium-oxide ceramic, creating a more rough and retentive surface, thus providing an improved micromechanical interlocking between the cement and the ceramic. Key words:Shear bond strength, silica coating, surface treatment, zirconia ceramics, phosphate monomer. PMID:22926485

Enhancing the protein resistance of silicone via surface-restructuring PEO-silane amphiphiles with variable PEO length

PubMed Central

Rufin, M. A.; Gruetzner, J. A.; Hurley, M. J.; Hawkins, M. L.; Raymond, E. S.; Raymond, J. E.

2015-01-01

Silicones with superior protein resistance were produced by bulk-modification with poly(ethylene oxide) (PEO)-silane amphiphiles that demonstrated a higher capacity to restructure to the surface-water interface versus conventional non-amphiphilic PEO-silanes. The PEO-silane amphiphiles were prepared with a single siloxane tether length but variable PEO segment lengths: α-(EtO)3Si(CH2)2-oligodimethylsiloxane13-block-poly(ethylene oxide)n-OCH3 (n = 3, 8, and 16). Conventional PEO-silane analogues (n = 3, 8 and 16) as well as a siloxane tether-silane (i.e. no PEO segment) were prepared as controls. When surface-grafted onto silicon wafer, PEO-silane amphiphiles produced surfaces that were more hydrophobic and thus more adherent towards fibrinogen versus the corresponding PEO-silane. However, when blended into a silicone, PEO-silane amphiphiles exhibited rapid restructuring to the surface-water interface and excellent protein resistance whereas the PEO-silanes did not. Silicones modified with PEO-silane amphiphiles of PEO segment lengths n = 8 and 16 achieved the highest protein resistance. PMID:26339488

DOE Office of Scientific and Technical Information (OSTI.GOV)

Addleman, Raymond S; Atkinson, David A; Bays, John T

An enhanced swipe sampler and method of making are described. The swipe sampler is made of a fabric containing selected glass, metal oxide, and/or oxide-coated glass or metal fibers. Fibers are modified with silane ligands that are directly attached to the surface of the fibers to functionalize the sampling surface of the fabric. The swipe sampler collects various target analytes including explosives and other threat agents on the surface of the sampler.

Deterministic Aperiodic Structures for on-chip Nanophotonics and Nanoplasmonics Device Applications

DTIC Science & Technology

2013-04-01

the origin of the superior field enhancement and localization observed in several aperiodic plasmonic structures. Due to the ...removed by hot acetone bath, resulting in the Si nano-hole master . The Si master is first treated with a silanizing agent to reduce the adhesion of ...arrays needs to be utilized, as illustrated in Figs. 7(a-d). The nanodot master fabrication proceeds

Chemical Initiation of FAE Clouds

DTIC Science & Technology

1979-11-01

F 2 -Explosions.:•; (Ref. 1) lkýi :i •i; I .................................................. i . *- LIQUID FUELS WITH FLUORINE, CHLORINE TRIFLUORIDE ...CTF) AND BROMINE TRIFLUORIDE (BTF)AY F does not ignite droplet dispersions of liquid fuels in air even in large concentration, evidently because the...Gerstein suggested numerous candi- date agents that may be grouped into metal alkylates such as triethyl " aluminum (TEA); volatile hydrides such as silanes

Bonding to new CAD/CAM resin composites: influence of air abrasion and conditioning agents as pretreatment strategy.

PubMed

Reymus, Marcel; Roos, Malgorzata; Eichberger, Marlis; Edelhoff, Daniel; Hickel, Reinhard; Stawarczyk, Bogna

2018-04-27

Because of their industrially standardized process of manufacturing, CAD/CAM resin composites show a high degree of conversion, making a reliable bond difficult to achieve. The purpose of this experiment was to investigate the tensile bond strength (TBS) of luting composite to CAD/CAM resin composite materials as influenced by air abrasion and pretreatment strategies. The treatment factors of the present study were (1) brand of the CAD/CAM resin composite (Brilliant Crios [Coltene/Whaledent], Cerasmart [GC Europe], Shofu Block HC [Shofu], and Lava Ultimate [3M]); (2) air abrasion vs. no air abrasion; and (3) pretreatment using a silane primer (Clearfil Ceramic Primer, Kuraray) vs. a resin primer (One Coat 7 Universal, Coltene/Whaledent). Subsequently, luting composite (DuoCem, Coltene/Whaledent) was polymerized onto the substrate surface using a mold. For each combination of the levels of the three treatment factors (4 (materials) × 2 (air abrasion vs. no air abrasion; resin) × 2 (primer vs. silane primer)), n = 15, specimens were prepared. After 24 h of water storage at 37 °C and 5000 thermo-cycles (5/55 °C), TBS was measured and failure types were examined. The resulting data was analyzed using Kaplan-Meier estimates of the cumulative failure distribution function with Breslow-Gehan tests and non-parametric ANOVA (Kruskal-Wallis test) followed by the multiple pairwise Mann-Whitney U test with α-error adjustment using the Benjamini-Hochberg procedure and chi-square test (p < 0.05). The additional air abrasion step increased TBS values and lowered failure rates. Specimens pretreated using a resin primer showed significantly higher TBS and lower failure rates than those pretreated using a silane primer. The highest failure rates were observed for groups pretreated with a silane primer. Within the Shofu Block HC group, all specimens without air abrasion and pretreatment with a silane primer debonded during the aging procedure. Before fixation of CAD/CAM resin composites, the restorations should be air abraded and pretreated using a resin primer containing methyl-methacrylate to successfully bond to the luting composite. The pretreatment of the CAD/CAM resin composite using merely a silane primer results in deficient adhesion. For a reliable bond of CAD/CAM resin composites to the luting composite, air abrasion and a special pretreatment strategy are necessary in order to achieve promising long-term results.

Facile Preparation of Nanostructured, Superhydrophobic Filter Paper for Efficient Water/Oil Separation

PubMed Central

Wang, Jianhua; Wong, Jessica X. H.; Kwok, Honoria; Li, Xiaochun; Yu, Hua-Zhong

2016-01-01

In this paper, we present a facile and cost-effective method to obtain superhydrophobic filter paper and demonstrate its application for efficient water/oil separation. By coupling structurally distinct organosilane precursors (e.g., octadecyltrichlorosilane and methyltrichlorosilane) to paper fibers under controlled reaction conditions, we have formulated a simple, inexpensive, and efficient protocol to achieve a desirable superhydrophobic and superoleophilic surface on conventional filter paper. The silanized superhydrophobic filter paper showed nanostructured morphology and demonstrated great separation efficiency (up to 99.4%) for water/oil mixtures. The modified filter paper is stable in both aqueous solutions and organic solvents, and can be reused multiple times. The present study shows that our newly developed binary silanization is a promising method of modifying cellulose-based materials for practical applications, in particular the treatment of industrial waste water and ecosystem recovery. PMID:26982055

Effect of modified graphene on thermal, mechanical and tribological performance of polyimide based composites

NASA Astrophysics Data System (ADS)

Li, Duxin; Yang, Wenyan; Chen, Yue; Xiao, Chunguang; Wei, Mengling

2018-06-01

The graphene oxide sheets (GO) were modified by silane coupling before incorporation into the aromatic polyimide (PI) matrix via in situ polymerization. The successful grafting of silane coupling onto the surface of the graphene was confirmed by FTIR, x-ray diffraction, and Raman spectroscopy. The incorporation of modified graphene oxide(K-GO) sheets significantly enhanced the thermal stability and tensile properties of PI. It was found that the tensile stress and the Young’s modulus of 0.5 wt%K-GO/PI were increased by 27.2% and 28.0% from pure PI, respectively. The T5% values of 0.5%K-GO/PI (507 °C) were obviously higher than that of pure PI (491 °C). Compared to pure PI, the PI composites with the K-GO addition of 0.5 wt% exhibits much lower friction coefficient (0.361) and wear rate (1.247 × 10‑5 mm3 N‑1m‑1). This can be attributed to the enhanced effect of K-GO addition on the properties of the composites. This study aims to expand the range of applications of graphene and to solve wear-related mechanical failures for polymer parts.

Improved bonding of adhesive resin to sintered porcelain with the combination of acid etching and a two-liquid silane conditioner.

PubMed

Kato, H; Matsumura, H; Ide, T; Atsuta, M

2001-01-01

This study determined the bond strengths of adhesive resins joined to a feldspathic porcelain (VMK 68) for the purpose of developing the most durable surface preparation for the porcelain. Three porcelain surfaces-ground, air-abraded with alumina, and etched with hydrofluoric acid-were prepared. A two-liquid porcelain conditioner that contained both 4-methacryloyloxyethyl trimellitate anhydride (4-META) and a silane coupler (Porcelain Liner M) was used as the priming agent. Each of the two liquid components of the conditioner was also used individually in order to examine the effects of the respective chemical ingredients on adhesive bonding. Two methyl methacrylate (MMA)-based resins initiated with tri-n-butylborane (TBB) either with or without 4-META (MMA-TBB and 4-META/MMA-TBB resins) were used as the luting agents. Shear bond strengths were determined both before and after thermocycling. Shear testing results indicated that thermocycling was effective for disclosing poor bonding systems, and that both mechanical and chemical retention were indispensable for bonding the porcelain. Of the combinations assessed, etching with hydrofluoric acid followed by two-liquid priming with the Porcelain Liner M material generated the most durable bond strength (33.3 MPa) for the porcelain bonded with the 4-META/MMA-TBB resin (Super-Bond C&B).

A coating of silane modified silica nanoparticles on PET substrate film for inkjet printing

NASA Astrophysics Data System (ADS)

Wu, J.; Liu, L.; Jiang, B.; Hu, Z.; Wang, X. Q.; Huang, Y. D.; Lin, D. R.; Zhang, Q. H.

2012-04-01

The paper aims to design nanoporous coatings for inkjet printing and study its microstructure influence on the ink absorption. In the present work, two inkjet materials were prepared: one with unmodified nano-SiO2 (S_1), the other with silica coupling agent modified nano-SiO2 (S_2). The surface characteristic changing after modification was investigated by scanning electron microscopy (SEM), atomic force microscopy (AFM). Wetting with contact angles was determined by the dynamic contact angle analysis test (DCAT). Through measurements, the dispersion of modified nano-SiO2 particles in the coating was superior to the dispersion of unmodified nano-SiO2 particles, surface roughness value (Ra) of S_1 was significantly higher than that of S_2, dynamic contact angle of S_2 is smaller than that of S_1 and ink droplet absorption in S_2 was much faster than in S_1. These results also reveal that the modification method is effective and offers a potential way to fabricate inkjet material with the advantages of microstructure and ink absorption over traditional methods.

Multishell Au/Ag/SiO 2 nanorods with tunable optical properties as single particle orientation and rotational tracking probes

DOE PAGES

Chen, Kuangcai; Lin, Chia -Cheng; Vela, Javier; ...

2015-04-07

In this study, three-layer core–shell plasmonic nanorods (Au/Ag/SiO 2–NRs), consisting of a gold nanorod core, a thin silver shell, and a thin silica layer, were synthesized and used as optical imaging probes under a differential interference contrast microscope for single particle orientation and rotational tracking. The localized surface plasmon resonance modes were enhanced upon the addition of the silver shell, and the anisotropic optical properties of gold nanorods were maintained. The silica coating enables surface functionalization with silane coupling agents and provides enhanced stability and biocompatibility. Taking advantage of the longitudinal LSPR enhancement, the orientation and rotational information of themore » hybrid nanorods on synthetic lipid bilayers and on live cell membranes were obtained with millisecond temporal resolution using a scientific complementary metal-oxide-semiconductor camera. The results demonstrate that the as-synthesized hybrid nanorods are promising imaging probes with improved sensitivity and good biocompatibility for single plasmonic particle tracking experiments in biological systems.« less

On-demand tuned hazard free elastomeric composites: A green approach.

PubMed

Manoharan, Partheban; Chandra Das, Narayan; Naskar, Kinsuk

2017-07-01

Rising ecological concerns and depletion of the potentially harmful environmental impacts caused by rubber products, are of prime importance in the industry. Therefore, implementation of sustainable greener materials is required to minimize the detrimental influences. In this research, we investigated the beneficial influence of naturally derived bio-resin toward the effects of association with Zinc Oxide Nanoparticles in highly dispersible silica (HDS) reinforced Natural rubber (NR)/Epoxidized Natural Rubber (ENR)-based composites. This novel green composite offers impressive properties which were analyzed based on bound rubber content, transmission electron microscopy, physico-mechanical, dynamic mechanical, and cure characteristics. Nanoindentation studies demonstrated the enhanced hysteresis phenomenon of the green composites. The small angle X-ray scattering (SAXS) characterization has been studied by using a Beaucage model and results corroborates that the insertion of bio-resin exhibits ameliorated state of silica dispersion in the green composites. Overall, the study with the bio-resin has provided the impetus in employing it as an alternative to the expensive synthetic route of silane coupling agent and toxic process oil. © 2017 Wiley Periodicals, Inc.

A Novel Method for Fabricating Wearable, Piezoresistive, and Pressure Sensors Based on Modified-Graphite/Polyurethane Composite Films

PubMed Central

He, Yin; Li, Wei; Yang, Guilin; Liu, Hao; Lu, Junyu; Zheng, Tongtong; Li, Xiaojiu

2017-01-01

A wearable, low-cost, highly repeatable piezoresistive sensor was fabricated by the synthesis of modified-graphite and polyurethane (PU) composites and polydimethylsiloxane (PDMS). Graphite sheets functionalized by using a silane coupling agent (KH550) were distributed in PU/N,N-dimethylformamide (DMF) solution, which were then molded to modified-graphite/PU (MG/PU) composite films. Experimental results show that with increasing modified-graphite content, the tensile strength of the MG/PU films first increased and then decreased, and the elongation at break of the composite films showed a decreasing trend. The electrical conductivity of the composite films can be influenced by filler modification and concentration, and the percolation threshold of MG/PU was 28.03 wt %. Under liner uniaxial compression, the 30 wt % MG/PU composite films exhibited 0.274 kPa−1 piezoresistive sensitivity within the range of low pressure, and possessed better stability and hysteresis. The flexible MG/PU composite piezoresistive sensors have great potential for body motion, wearable devices for human healthcare, and garment pressure testing. PMID:28773047

Comparative investigation of two methods for Acetylcholinesterase enzyme immobilization on modified porous silicon

NASA Astrophysics Data System (ADS)

Khaldi, Khadidja; Sam, Sabrina; Lounas, Amel; Yaddaden, Chafiaa; Gabouze, Noure-Eddine

2017-11-01

In this work, Acetylcholinesterase enzyme (AChE) was immobilized on porous silicon (PSi) surface using two strategies. In the first method, acid chains were covalently grafted on the hydrogenated PSi by hydrosilylation reaction. The obtained acid-terminated surface was activated by a reaction with N-hydroxysuccinimide (NHS) in the presence of a peptide-coupling agent N-ethyl-N‧-(3-dimethylaminopropyl)-carbodiimide (EDC), and then reacted with the amino linker of the lysine residues AChE to anchor the enzyme by a covalent amide bond. In the second procedure, the PSi surface was first hydroxylated in piranha solution, followed by a silanization reaction with 3-aminopropyltriethoxysilane (APTES) to form amine-terminated surface. Finally, AChE was attached to the terminal amine groups by an aminolysis reaction with carboxylic acid groups of AChE in the presence of NHS/EDC mixture. Fourier transform infrared spectroscopy (FTIR) confirmed the efficiency of the surface modifications. The enzymatic activity of immobilized AChE was determined by means of a colorimetric test and was discussed according to the enzyme orientation on the surface which was revealed by contact angle measurements.

PLA and single component silicone rubber blends for sub-zero temperature blown film packaging applications

NASA Astrophysics Data System (ADS)

Meekum, Utai; Khiansanoi, Apichart

2018-06-01

The poly(lactic acid) (PLA) blend with single component silicone rubber in the presence of reactive amino silane coupling agent and polyester polyols plasticizer were studied. The manufacturing of film packaging for sub-zero temperature applications from the PLA blend was the main objective. The mechanical properties, especially the impact strengths, of PLA/silicone blends were significantly depended on the silicone loading. The outstanding impact strengths, tested at sub-zero temperature, of the blend having silicone content of 8.0 phr was achieved. It was chosen as the best candidate for the processability improvement. Adding the talc filler into the PLA/silicone blend to enhance the rheological properties was investigated. The ductility of the talc filled blends were decreased with increasing the filler contents. However, the shear viscosity of the blend was raised with talc loading. The blend loaded with 40 phr of talc filler was justified as the optimal formula for the blown film process testing and it was successfully performed with a few difficulties. The obtained blown film showed relative good flexibility in comparison with LDPE but it has low transparency.

Recycling polyethylene terephthalate wastes as short fibers in Strain-Hardening Cementitious Composites (SHCC).

PubMed

Lin, Xiuyi; Yu, Jing; Li, Hedong; Lam, Jeffery Y K; Shih, Kaimin; Sham, Ivan M L; Leung, Christopher K Y

2018-05-26

As an important portion of the total plastic waste bulk but lack of reuse and recycling, the enormous amounts of polyethylene terephthalate (PET) solid wastes have led to serious environmental issues. This study explores the feasibility of recycling PET solid wastes as short fibers in Strain-Hardening Cementitious Composites (SHCCs), which exhibit strain-hardening and multiple cracking under tension, and therefore have clear advantages over conventional concrete for many construction applications. Based on micromechanical modeling, fiber dispersion and alkali resistance, the size of recycled PET fibers was first determined. Then the hydrophobic PET surface was treated with NaOH solution followed by a silane coupling agent to achieve the dual purpose of improving the fiber/matrix interfacial frictional bond (from 0.64 MPa to 0.80 MPa) and enhancing the alkali resistance for applications in alkaline cementitious environment. With surface treatment, recycling PET wastes as fibers in SHCCs is a promising approach to significantly reduce the material cost of SHCCs while disposing hazardous PET wastes in construction industry. Copyright © 2018 Elsevier B.V. All rights reserved.

Comparison of detailed and reduced kinetics mechanisms of silane oxidation in the basis of detonation wave structure problem

NASA Astrophysics Data System (ADS)

Fedorov, A. V.; Tropin, D. A.; Fomin, P. A.

2018-03-01

The paper deals with the problem of the structure of detonation waves in the silane-air mixture within the framework of mathematical model of a nonequilibrium gas dynamics. Detailed kinetic scheme of silane oxidation as well as the newly developed reduced kinetic model of detonation combustion of silane are used. On its basis the detonation wave (DW) structure in stoichiometric silane - air mixture and dependences of Chapman-Jouguet parameters of mixture on stoichiometric ratio between the fuel (silane) and an oxidizer (air) were obtained.

Organic-dye-coupled magnetic nanoparticles encaged inside thermoresponsive PNIPAM Microcapsules.

PubMed

Guo, Jia; Yang, Wuli; Deng, Yonghui; Wang, Changchun; Fu, Shoukuan

2005-07-01

We present a new approach for the fabrication of thermoresponsive polymer microcapsules with mobile magnetic cores that undergo a volume phase-transition upon changing the temperature and are collected under an external magnetic field. We have prepared organic/inorganic composite microspheres with a well-defined core-shell structure that are composed of a crosslinked poly(N-isopropylacrylamide) (PNIPAM) shell and silica cores dotted centrally by magnetite nanoparticles. Since the infiltration of template-decomposed products is dependent on the permeability of PNIPAM shells triggered by changes of exterior temperature, the silica layer sandwiched between the magnetic core and the PNIPAM shell was quantitatively removed to generate PNIPAM microcapsules with mobile magnetic cores by treatment with aqueous NaOH solution. For development of the desired multifunctional microcapsules, modification of the unetched silica surface interiors can be realized by treatment with a silane coupling agent containing functional groups that can easily bind to catalysts, enzymes, or labeling molecules. Herein, fluorescein isothiocyanate (FITC), which is a common organic dye, is attached to the insides of the mobile magnetic cores to give PNIPAM microcapsules with FITC-labeled magnetic cores. In this system, it can be expected that an extension of the functionalization of the cavity properties of smart polymer microcapsules is to immobilize other target molecules onto the mobile cores in order to introduce other desired functions in the hollow cage.

Mild partial deoxygenation of esters catalyzed by an oxazolinylborate-coordinated rhodium silylene

DOE PAGES

Xu, Songchen; Boschen, Jeffery S.; Biswas, Abhranil; ...

2015-08-17

An electrophilic, coordinatively unsaturated rhodium complex supported by borate-linked oxazoline, oxazoline-coordinated silylene, and N-heterocyclic carbene donors [{κ³-N,Si,C-PhB(Ox Me²)(Ox Me²SiHPh)Im Mes}Rh(H)CO][HB(C₆F₅)₃] (2, Ox Me² = 4,4-dimethyl-2-oxazoline; Im Mes = 1-mesitylimidazole) is synthesized from the neutral rhodium silyl {PhB(Ox Me²)₂Im Mes}RhH(SiH 2Ph)CO (1) and B(C 6F 5) 3. The unusual oxazoline-coordinated silylene structure in 2 is proposed to form by rearrangement of an unobserved isomeric cationic rhodium silylene species [{PhB(Ox Me²)₂Im Mes}RhH(SiHPh)CO][HB(C₆F₅)₃] generated by H abstraction. Complex 2 catalyzes reductions of organic carbonyl compounds with silanes to give hydrosilylation products or deoxygenation products. The pathway to these reactions is primarily influenced bymore » the degree of substitution of the organosilane. Reactions with primary silanes give deoxygenation of esters to ethers, amides to amines, and ketones and aldehydes to hydrocarbons, whereas tertiary silanes react to give 1,2-hydrosilylation of the carbonyl functionality. In contrast, the strong Lewis acid B(C₆F₅)₃ catalyzes the complete deoxygenation of carbonyl compounds to hydrocarbons with PhSiH₃ as the reducing agent.« less

Mild partial deoxygenation of esters catalyzed by an oxazolinylborate-coordinated rhodium silylene

DOE Office of Scientific and Technical Information (OSTI.GOV)

Xu, Songchen; Boschen, Jeffery S.; Biswas, Abhranil

An electrophilic, coordinatively unsaturated rhodium complex supported by borate-linked oxazoline, oxazoline-coordinated silylene, and N-heterocyclic carbene donors [{κ³-N,Si,C-PhB(Ox Me²)(Ox Me²SiHPh)Im Mes}Rh(H)CO][HB(C₆F₅)₃] (2, Ox Me² = 4,4-dimethyl-2-oxazoline; Im Mes = 1-mesitylimidazole) is synthesized from the neutral rhodium silyl {PhB(Ox Me²)₂Im Mes}RhH(SiH 2Ph)CO (1) and B(C 6F 5) 3. The unusual oxazoline-coordinated silylene structure in 2 is proposed to form by rearrangement of an unobserved isomeric cationic rhodium silylene species [{PhB(Ox Me²)₂Im Mes}RhH(SiHPh)CO][HB(C₆F₅)₃] generated by H abstraction. Complex 2 catalyzes reductions of organic carbonyl compounds with silanes to give hydrosilylation products or deoxygenation products. The pathway to these reactions is primarily influenced bymore » the degree of substitution of the organosilane. Reactions with primary silanes give deoxygenation of esters to ethers, amides to amines, and ketones and aldehydes to hydrocarbons, whereas tertiary silanes react to give 1,2-hydrosilylation of the carbonyl functionality. In contrast, the strong Lewis acid B(C₆F₅)₃ catalyzes the complete deoxygenation of carbonyl compounds to hydrocarbons with PhSiH₃ as the reducing agent.« less

Measuring Trace Hydrocarbons in Silanes

NASA Technical Reports Server (NTRS)

Lesser, L. A.

1984-01-01

Technique rapid and uses standard analytical equipment. Silane gas containing traces of hydrocarbons injected into carrier gas of moist nitrogen having about 0.2 percent water vapor. Carrier, water and silane pass through short column packed with powdered sodium hydroxide which combines moisture and silane to form nonvolatile sodium silicate. Carrier gas free of silane but containing nonreactive hydrocarbons, pass to silica-gel column where chromatographic separation takes place. Hydrocarbons measured by FID.

Mechanistic Study of Nickel-Catalyzed Ynal Reductive Cyclizations Through Kinetic Analysis

PubMed Central

Baxter, Ryan D.; Montgomery, John

2011-01-01

The mechanism of nickel-catalyzed, silane-mediated reductive cyclization of ynals has been evaluated. The cyclizations are first-order in [Ni] and [ynal] and zeroth-order in [silane]. These results, in combination with the lack of rapid silane consumption upon reaction initiation are inconsistent with mechanisms involving reaction initiation by oxidative addition of Ni(0) to the silane. Silane consumption occurs only when both the alkyne and aldehyde and are present. Mechanisms involving rate-determining oxidative cyclization to a metallacycle followed by rapid reaction with the silane are consistent with the data obtained. PMID:21438642

Effect of silane pretreatment on the immediate bonding of universal adhesives to computer-aided design/computer-aided manufacturing lithium disilicate glass ceramics.

PubMed

Yao, Chenmin; Zhou, Liqun; Yang, Hongye; Wang, Yake; Sun, Hualing; Guo, Jingmei; Huang, Cui

2017-04-01

The aim of this study was to investigate the effect of silane pretreatment on the universal adhesive bonding between lithium disilicate glass ceramic and composite resin. IPS e.max ceramic blocks etched with hydrofluoric acid were randomly assigned to one of eight groups treated with one of four universal adhesives (two silane-free adhesives and two silane-containing adhesives), each with or without silane pretreatment. Bonded specimens were stored in water for 24 h. The shear bond strength (SBS) of the ceramic-resin interface was measured to evaluate bond strength, and the debonded interface after the SBS test was analysed using field-emission scanning electron microscopy to determine failure mode. Light microscopy was performed to analyse microleakage and marginal sealing ability. Silane pretreatment significantly and positively influenced SBS and marginal sealing ability. For all the universal adhesive groups, SBS increased and the percentage of microleakage decreased after the pretreatment. Without the pretreatment, SBS and the percentage of microleakage were not significantly different between the silane-containing universal adhesive groups and the silane-free groups. Cohesive failure was the main fracture pattern. The results suggest that additional silane pretreatment can effectively improve the bonding strength and marginal sealing of adhesives to lithium disilicate glass ceramics. The bonding performance of silane-containing universal adhesives without pretreatment is similar to that of silane-free adhesives. © 2017 Eur J Oral Sci.

Reactor for fluidized bed silane decomposition

NASA Technical Reports Server (NTRS)

Iya, Sridhar K. (Inventor)

1989-01-01

An improved heated fluidized bed reactor and method for the production of high purity polycrystalline silicon by silane pyrolysis wherein silicon seed particles are heated in an upper heating zone of the reactor and admixed with particles in a lower zone, in which zone a silane-containing gas stream, having passed through a lower cooled gas distribution zone not conducive to silane pyrolysis, contacts the heated seed particles whereon the silane is heterogeneously reduced to silicon.

Corrosion Protection of Nd-Fe Magnets via Phophatization, Silanization and Electrostatic Spraying with Organic Resin Composite Coatings

NASA Astrophysics Data System (ADS)

Ding, Xia; Li, Jingjie; Li, Musen; Ge, Shengsong; Wang, Xiuchun; Ding, Kaihong; Cui, Shengli; Sun, Yongcong

2014-09-01

Nd-Fe-B permanent magnets possess excellent properties. However, they are highly sensitive to the attack of corrosive environment. The aim of this work is to improve the corrosion resistance of the magnets by phosphatization, silanization, and electrostatic spraying with organic resin composite coatings. Field emission scanning electron microscope (FE-SEM) and energy dispersive spectrometer (EDS) tests showed that uniform phosphate conversion coatings and spray layers were formed on the surface of the Nd-Fe-B magnets. Neutral salt spray tests exhibited that, after treated by either phosphating, silanization or electrostatic spraying, the protectiveness of Nd-Fe-B alloys was apparently increased. And corrosion performance of magnets treated with silane only was slightly inferior to those of phosphatized ones. However, significant improvement in corrosion protection was achieved after two-step treatments, i.e. by top-coating spray layer with phosphate or silane films underneath. Grid test indicated that the phosphate and silane coating were strongly attached to the substrate while silane film was slightly weaker than the phosphate-treated ones. Magnetic property analysis revealed phosphatization, silanization, and electrostatic spraying caused decrease in magnetism, but silanization had the relatively smaller effect.

Zone heating for fluidized bed silane pyrolysis

NASA Technical Reports Server (NTRS)

Iya, Sridhar K. (Inventor)

1987-01-01

An improved heated fluidized bed reactor and method for the production of high purity polycrystalline silicon by silane pyrolysis wherein silicon seed particles are heated in an upper heating zone of the reactor and admixed with particles in a lower reaction zone, in which zone a silane-containing gas stream, having passed through a lower cooled gas distribution zone not conducive to silane pyrolysis, contacts the heated seed particles whereon the silane is heterogeneously reduced to silicon.

Surface characterization and cytocompatibility evaluation of silanized magnesium alloy AZ91 for biomedical applications

PubMed Central

Witecka, Agnieszka; Yamamoto, Akiko; Dybiec, Henryk; Swieszkowski, Wojciech

2012-01-01

Mg alloys with high Al contents have superior corrosion resistance in aqueous environments, but poor cytocompatibility compared to that of pure Mg. We have silanized the cast AZ91 alloy to improve its cytocompatibility using five different silanes: ethyltriethoxysilane (S1), 3-aminopropyltriethoxysilane (S2), 3-isocyanatopyltriethoxysilane (S3), phenyltriethoxysilane (S4) and octadecyltriethoxysilane (S5). The surface hydrophilicity/hydrophobicity was evaluated by water contact angle measurements. X-ray photoelectron analysis was performed to investigate the changes in surface states and chemical composition. All silane reagents increased adsorption of the albumin to the modified surface. In vitro cytocompatibility evaluation revealed that silanization improved cell growth on AZ91 modified by silane S1. Measurement of the concentration of Mg2+ ions released during the cell culture indicated that silanization does not affect substrate degradation. PMID:27877541

Surface characterization and cytocompatibility evaluation of silanized magnesium alloy AZ91 for biomedical applications

NASA Astrophysics Data System (ADS)

Witecka, Agnieszka; Yamamoto, Akiko; Dybiec, Henryk; Swieszkowski, Wojciech

2012-12-01

Mg alloys with high Al contents have superior corrosion resistance in aqueous environments, but poor cytocompatibility compared to that of pure Mg. We have silanized the cast AZ91 alloy to improve its cytocompatibility using five different silanes: ethyltriethoxysilane (S1), 3-aminopropyltriethoxysilane (S2), 3-isocyanatopyltriethoxysilane (S3), phenyltriethoxysilane (S4) and octadecyltriethoxysilane (S5). The surface hydrophilicity/hydrophobicity was evaluated by water contact angle measurements. X-ray photoelectron analysis was performed to investigate the changes in surface states and chemical composition. All silane reagents increased adsorption of the albumin to the modified surface. In vitro cytocompatibility evaluation revealed that silanization improved cell growth on AZ91 modified by silane S1. Measurement of the concentration of Mg2+ ions released during the cell culture indicated that silanization does not affect substrate degradation.

Effect of silane concentration on the supersonic combustion of a silane/methane mixture

NASA Technical Reports Server (NTRS)

Northam, G. B.; Mclain, A. G.; Pellett, G. L.; Diskin, G. S.

1986-01-01

A series of direct connect combustor tests was conducted to determine the effect of silane concentration on the supersonic combustion characteristics of silane/methane mixtures. Shock tube ignition delay data indicated more than an order of magnitude reduction in ignition delay times for both 10 and 20 percent silane/methane mixtures as compared to methane. The ignition delay time of the 10 percent mixture was only a factor of 2.3 greater than that of the 20 percent mixture. Supersonic combustion tests were conducted with the fuel injected into a model scramjet combustor. The combustor was mounted at the exit of a Mach 2 nozzle and a hydrogen fired heater was used to provide a variation in test gas total temperature. Tests using the 20 percent silane/methane mixture indicated considerable combustion enhancement when compared to methane alone. This mixture had an autoignition total temperature of 1650 R. This autoignition temperature can be contrasted with 2330 R for hydrogen and 1350 R for a 20 percent silane/hydrogen mixture in similar hardware. Methane without the silane additive did not autoignite in this configuration at total temperatures as high as 3900 R, the maximum temperature at which tests were conducted. Supersonic combustion tests with the silane concentration reduced to 10 percent indicated little improvement in combustion performance over pure methane. The addition of 20 percent silane to methane resulted in a pyrophoric fuel with good supersonic combustion performance. Reducing the silane concentration below this level, however, yielded a less pyrophoric fuel that exhibited poor supersonic combustion performance.

40 CFR 721.9507 - Polyester silane.

Code of Federal Regulations, 2011 CFR

2011-07-01

... 40 Protection of Environment 31 2011-07-01 2011-07-01 false Polyester silane. 721.9507 Section 721... Polyester silane. (a) Chemical substance and significant new uses subject to reporting. (1) The chemical substance identified as a polyester silane (P-95-1022) is subject to reporting under this section for the...

40 CFR 721.9507 - Polyester silane.

Code of Federal Regulations, 2010 CFR

2010-07-01

... 40 Protection of Environment 30 2010-07-01 2010-07-01 false Polyester silane. 721.9507 Section 721... Polyester silane. (a) Chemical substance and significant new uses subject to reporting. (1) The chemical substance identified as a polyester silane (P-95-1022) is subject to reporting under this section for the...

40 CFR 721.10262 - Oxime, Me vinyl silane (generic).

Code of Federal Regulations, 2012 CFR

2012-07-01

... 40 Protection of Environment 32 2012-07-01 2012-07-01 false Oxime, Me vinyl silane (generic). 721... Substances § 721.10262 Oxime, Me vinyl silane (generic). (a) Chemical substance and significant new uses subject to reporting. (1) The chemical substance identified generically as oxime, Me vinyl silane (PMN P...

40 CFR 721.10262 - Oxime, Me vinyl silane (generic).

Code of Federal Regulations, 2013 CFR

2013-07-01

... 40 Protection of Environment 32 2013-07-01 2013-07-01 false Oxime, Me vinyl silane (generic). 721... Substances § 721.10262 Oxime, Me vinyl silane (generic). (a) Chemical substance and significant new uses subject to reporting. (1) The chemical substance identified generically as oxime, Me vinyl silane (PMN P...

Ion Kinetics in Silane Plasmas

DTIC Science & Technology

1988-04-20

field and orthogonal to the excite plates. The image current is amplified, digitized, and Fourier analyzed to yield a spectrum of 0 cyclotron...Laboratory (AFWAL/P0OC). 17. COSATI CODES 18. SUBJECT TERMS (Continue on reverse if necessary and identify by block number) FIELD GROUP SUB-GROUP 20 U9 09 03...d.c., microwave, or capacatively coupled, radiofrequency electric fields . Alternatively, hollow cath- ode or electron beam approaches may be employed

Fracture Strength of Monolithic All-Ceramic Crowns on Titanium Implant Abutments.

PubMed

Weyhrauch, Michael; Igiel, Christopher; Scheller, Herbert; Weibrich, Gernot; Lehmann, Karl Martin

2016-01-01

The fracture strengths of all-ceramic crowns cemented on titanium implant abutments may vary depending on crown materials and luting agents. The purpose of this study was to examine differences in fracture strength among crowns cemented on implant abutments using crowns made of seven different monolithic ceramic materials and five different luting agents. In total, 525 crowns (75 each of Vita Mark II, feldspathic ceramic [FSC]; Ivoclar Empress CAD, leucite-reinforced glass ceramic [LrGC]; Ivoclar e.max CAD, lithium disilicate [LiDS]; Vita Suprinity, presintered zirconia-reinforced lithium silicate ceramic [PSZirLS]; Vita Enamic, polymer-reinforced fine-structure feldspathic ceramic [PolyFSP], Lava Ultimate; resin nanoceramic [ResNC], Celtra Duo; fully crystallized zirconia-reinforced lithium silicate [FcZirLS]) were milled using a CAD/CAM system. The inner surfaces of the crowns were etched and silanized. Titanium implant abutments were fixed on implant analogs, and airborne-particle abrasion was used on their exterior specific adhesion surfaces (Al2O3, 50 μm). Then, the abutments were degreased and silanized. The crowns were cemented on the implant abutments using five luting agents (Multilink Implant, Variolink II, RelyX Unicem, GC FujiCEM, Panavia 2.0). After thermocycling for 5,000 cycles (5 to 55°C, 30 seconds dwell time), the crowns were subjected to fracture strength testing under static load using a universal testing machine. Statistical analyses were performed using analysis of variance (α = .0002) and the Bonferroni correction. No significant difference among the luting agents was found using the different all-ceramic materials. Ceramic materials LiDS, PSZirLS, PolyFSP, and ResNC showed significantly higher fracture strength values compared with FSC, FcZirLS, and LrGC. The PSZirLS especially showed significantly better results. Within the limitations of this study, fracture strength was not differentially affected by the various luting agents. However, the fracture strength was significantly higher for PSZirLS, PolyFSP, ResNC, and LiDS ceramics than for the FSP, LrGC, and the FcZirLS ceramic with all luting agents tested.

40 CFR 721.10261 - Oxime, di-Me silane (generic).

Code of Federal Regulations, 2013 CFR

2013-07-01

... 40 Protection of Environment 32 2013-07-01 2013-07-01 false Oxime, di-Me silane (generic). 721... Substances § 721.10261 Oxime, di-Me silane (generic). (a) Chemical substance and significant new uses subject to reporting. (1) The chemical substance identified generically as oxime, di-Me silane (PMN P-09-589...

40 CFR 721.10261 - Oxime, di-Me silane (generic).

Code of Federal Regulations, 2012 CFR

2012-07-01

... 40 Protection of Environment 32 2012-07-01 2012-07-01 false Oxime, di-Me silane (generic). 721... Substances § 721.10261 Oxime, di-Me silane (generic). (a) Chemical substance and significant new uses subject to reporting. (1) The chemical substance identified generically as oxime, di-Me silane (PMN P-09-589...

Demonstrating the feasibility of monitoring the molecular-level structures of moving polymer/silane interfaces during silane diffusion using SFG.

PubMed

Chen, Chunyan; Wang, Jie; Loch, Cheryl L; Ahn, Dongchan; Chen, Zhan

2004-02-04

In this paper, the feasibility of monitoring molecular structures at a moving polymer/liquid interface by sum frequency generation (SFG) vibrational spectroscopy has been demonstrated. N-(2-Aminoethyl)-3-aminopropyltrimethoxysilane (AATM, NH2(CH2)2NH(CH2)3Si(OCH3)3) has been brought into contact with a deuterated poly(methyl methacrylate) (d-PMMA) film, and the interfacial silane structure has been monitored using SFG. Upon initial contact, the SFG spectra can be detected, but as time progresses, the spectral intensity changes and finally disappears. Additional experiments indicate that these silane molecules can diffuse into the polymer film and the detected SFG signals are actually from the moving polymer/silane interface. Our results show that the molecular order of the polymer/silane interface exists during the entire diffusion process and is lost when the silane molecules traverse through the thickness of the d-PMMA film. The loss of the SFG signal is due to the formation of a new disordered substrate/silane interface, which contributes no detectable SFG signal. The kinetics of the diffusion of the silane into the polymer have been deduced from the time-dependent SFG signals detected from the AATM molecules as they diffuse through polymer films of different thickness.

Redox and Lewis acid relay catalysis: a titanocene/zinc catalytic platform in the development of multicomponent coupling reactions.

PubMed

Gianino, Joseph B; Campos, Catherine A; Lepore, Antonio J; Pinkerton, David M; Ashfeld, Brandon L

2014-12-19

A titanocene-catalyzed multicomponent coupling is described herein. Using catalytic titanocene, phosphine, and zinc dust, zinc acetylides can be generated from the corresponding iodoalkynes to affect sequential nucleophilic additions to aromatic aldehydes. The intermediate propargylic alkoxides are trapped in situ with acetic anhydride, which are susceptible to a second nucleophilic displacement upon treatment with a variety of electron-rich species, including acetylides, allyl silanes, electron-rich aromatics, silyl enol ethers, and silyl ketene acetals. Additionally, employing cyclopropane carboxaldehydes led to ring-opened products resulting from iodine incorporation. Taken together, these results form the basis for a new mode of three-component coupling reactions, which allows for rapid access to value added products in a single synthetic operation.

Silane Modification of Glass and Silica Surfaces to Obtain Equally Oil-Wet Surfaces in Glass-Covered Silicon Micromodel Applications

DOE Office of Scientific and Technical Information (OSTI.GOV)

Grate, Jay W.; Warner, Marvin G.; Pittman, Jonathan W.

2013-08-05

The wettability of silicon and glass surfaces can be modified by silanization. However, similar treatments of glass and silica surfaces using the same silane do not necessarily yield the same wettability as determined by the oil-water contact angle. In this technical note, surface cleaning pretreatments were investigated to determine conditions that would yield oil-wet surfaces on glass with similar wettability to silica surfaces treated with the same silane, and both air-water and oil-water contact angles were determined. Air-water contact angles were less sensitive to differences between silanized silica and glass surfaces, often yielding similar values while the oil-water contact anglesmore » were quite different. Borosilicate glass surfaces cleaned with standard cleaning solution 1 (SC1) yield intermediate-wet surfaces when silanized with hexamethyldisilazane, while the same cleaning and silanization yields oil-wet surfaces on silica. However, cleaning glass in boiling concentrated nitric acid creates a surface that can be silanized to obtain oil-wet surfaces using HDMS. Moreover, this method is effective on glass with prior thermal treatment at an elevated temperature of 400oC. In this way, silica and glass can be silanized to obtain equally oil-wet surfaces using HMDS. It is demonstrated that pretreatment and silanization is feasible in silicon-silica/glass micromodels previously assembled by anodic bonding, and that the change in wettability has a significant observable effect on immiscisble fluid displacements in the pore network.« less

Hydrogen-dominated plasma, due to silane depletion, for microcrystalline silicon deposition

DOE Office of Scientific and Technical Information (OSTI.GOV)

Howling, A. A.; Sobbia, R.; Hollenstein, Ch.

2010-07-15

Plasma conditions for microcrystalline silicon deposition generally require a high flux of atomic hydrogen, relative to SiH{sub {alpha}=0{yields}3} radicals, on the growing film. The necessary dominant partial pressure of hydrogen in the plasma is conventionally obtained by hydrogen dilution of silane in the inlet flow. However, a hydrogen-dominated plasma environment can also be obtained due to plasma depletion of the silane in the gas mixture, even up to the limit of pure silane inlet flow, provided that the silane depletion is strong enough. At first sight, it may seem surprising that the composition of a strongly depleted pure silane plasmamore » consists principally of molecular hydrogen, without significant contribution from the partial pressure of silane radicals. The aim here is to bring some physical insight by means of a zero-dimensional, analytical plasma chemistry model. The model is appropriate for uniform large-area showerhead reactors, as shown by comparison with a three-dimensional numerical simulations. The SiH{sub {alpha}} densities remain very low because of their rapid diffusion and surface reactivity, contributing to film growth which is the desired scenario for efficient silane utilization. Significant SiH{sub {alpha}} densities due to poor design of reactor and gas flow, on the other hand, would result in powder formation wasting silane. Conversely, hydrogen atoms are not deposited, but recombine on the film surface and reappear as molecular hydrogen in the plasma. Therefore, in the limit of extremely high silane depletion fraction (>99.9%), the silane density falls below the low SiH{sub {alpha}} densities, but only the H radical can eventually reach significant concentrations in the hydrogen-dominated plasma.« less

Effect of laser heat treatment on Pull-out bond strength of fiber posts treated with different silanes.

PubMed

Shafiei, Fereshteh; Saadat, Maryam; Jowkar, Zahra

2018-05-01

This study evaluated the effect of three different silanes and post-silanization treatments on the retentive strength of fiber posts luted with an etch-and-rinse resin cement. One hundred intact maxillary central incisors were randomly divided into 10 groups after endodontic treatment and post space preparation (n=10). The fiber posts were etched using 24% hydrogen peroxide. Posts of the control group did not receive silane. In nine experimental groups, each of the three silanes used, Scotchbond Universal adhesive, Bis-Silane and Porcelain Primer, was subjected to three treatments: air-drying at 25°C, warm air-drying and CO2 laser heat treatment. After cementation of the treated posts using One-Step Plus/Duo-Link cement, the specimens were stored for one weak and then subjected to pull-out bond strength (PBS) testing. The data in Newton (N) were analyzed using two-way ANOVA and Tukey tests (α=0.05). PBS was significantly affected by silane type and post-silanization treatment ( p <0.001). The interaction of the two factors was not statistically significant ( p =0.15). The effect of Porcelain Primer on PBS was significantly higher than those of universal adhesive ( p <0.001) and Bis-Silane ( p =0.01), with similar results for the two latter. Warm air-drying and laser treatment significantly increased PBS ( p <0.001). The lowest and highest PBS was obtained in the control (no silane) group (190.9±31) and laser-treated/ Porcelain Primer group (377.1±50), respectively. Warm air-drying and CO2 laser heat treatment had a significantly beneficial effect on retentive strength of fiber posts. Porcelain Primer was significantly more effective than universal adhesive and Bis-Silane. Key words: Laser heat treatment, Pull-out bond strength, fiber post.

Influence of Etching Protocol and Silane Treatment with a Universal Adhesive on Lithium Disilicate Bond Strength.

PubMed

Kalavacharla, V K; Lawson, N C; Ramp, L C; Burgess, J O

2015-01-01

To measure the effects of hydrofluoric acid (HF) etching and silane prior to the application of a universal adhesive on the bond strength between lithium disilicate and a resin. Sixty blocks of lithium disilicate (e.max CAD, Ivoclar Vivadent) were sectioned into coupons and polished. Specimens were divided into six groups (n=10) based on surface pretreatments, as follows: 1) no treatment (control); 2) 5% HF etch for 20 seconds (5HF); 3) 9.5% HF etch for 60 seconds (9.5HF); 4) silane with no HF (S); 5) 5% HF for 20 seconds + silane (5HFS); and 6) 9.5% HF for 60 seconds + silane (9.5HFS). All etching was followed by rinsing, and all silane was applied in one coat for 20 seconds and then dried. The universal adhesive (Scotchbond Universal, 3M ESPE) was applied onto the pretreated ceramic surface, air thinned, and light cured for 10 seconds. A 1.5-mm-diameter plastic tube filled with Z100 composite (3M ESPE) was applied over the bonded ceramic surface and light cured for 20 seconds on all four sides. The specimens were thermocycled for 10,000 cycles (5°C-50°C/15 s dwell time). Specimens were loaded until failure using a universal testing machine at a crosshead speed of 1 mm/min. The peak failure load was used to calculate the shear bond strength. Scanning electron microscopy images were taken of representative e.max specimens from each group. A two-way analysis of variance (ANOVA) determined that there were significant differences between HF etching, silane treatment, and the interaction between HF and silane treatment (p<0.01). Silane treatment provided higher shear bond strength regardless of the use or concentration of the HF etchant. Individual one-way ANOVA and Tukey post hoc analyses were performed for each silane group. Shear bond strength values for each etch time were significantly different (p<0.01) and could be divided into significantly different groups based on silane treatment: no silane treatment: 0 HF < 5% HF < 9.5% HF; and RelyX silane treatment: 0 HF < 5% HF and 9.5% HF. Both HF and silane treatment significantly improved the bond strength between resin and lithium disilicate when used with a universal adhesive.

Development of the silane process for the production of low-cost polysilicon

NASA Technical Reports Server (NTRS)

Iya, S. K.

1986-01-01

It was recognized that the traditional hot rod type deposition process for decomposing silane is energy intensive, and a different approach for converting silane to silicon was chosen. A 1200 metric tons/year capacity commercial plant was constructed in Moses Lake, Washington. A fluidized bed processor was chosen as the most promising technology and several encouraging test runs were conducted. This technology continues to be very promising in producing low cost polysilicon. The Union Carbide silane process and the research development on the fluidized bed silane decomposition are discussed.

Salt exclusion in silane-laced epoxy coatings.

PubMed

Wang, Peng; Schaefer, Dale W

2010-01-05

The corrosion protection mechanism of a one-step silane-laced epoxy coating system was investigated using neutron reflectivity. Pure epoxy and silane-laced epoxy films were examined at equilibrium with saturated NaCl water solution. The results demonstrate that the addition of silane introduces a salt-exclusion effect to epoxy coating. Specifically, the addition of silane densifies the epoxy network, which leads to exclusion of hydrated salt ions by a size effect. The effect is particularly significant at the metal-coating interface. Exclusion of ions improves the corrosion resistance, particularly for metals susceptible to pitting.

Self-assembly and graft polymerization route to Monodispersed Fe3O4@SiO2--polyaniline core-shell composite nanoparticles: physical properties.

PubMed

Reddy, Kakarla Raghava; Lee, Kwang-Pill; Kim, Ju Young; Lee, Youngil

2008-11-01

This study describes the synthesis of monodispersed core-shell composites of silica-modified magnetic nanoparticles and conducting polyaniline by self-assembly and graft polymerization. Magnetic ferrite nanoparticles (Fe3O4) were prepared by coprecipitation of Fe+2 and Fe+3 ions in alkaline solution, and then silananized. The silanation of magnetic particles (Fe3O4@SiO2) was carried out using 3-bromopropyltrichlorosilane (BPTS) as the coupling agent. FT-IR spectra indicated the presence of Fe--O--Si chemical bonds in Fe3O4@SiO2. Core-shell type nanocomposites (Fe3O4@SiO2/PANI) were prepared by grafting polyaniline (PANI) on the surface of silanized magnetic particles through surface initiated in-situ chemical oxidative graft polymerization. The nanocomposites were characterized by high resolution transmission electron microscopy (HRTEM), X-ray diffraction (XRD), X-ray photoelectron spectra (XPS), Fourier transform infrared (FTIR) spectra, UV-visible spectroscopy, photoluminescence (PL) spectra, electrical conductivity and magnetic characteristics. HRTEM images of the nanocomposites revealed that the silica-modified magnetic particles made up the core while PANI made up the shell. The XPS spectrum revealed the presence of silica in the composites, and the XRD results showed that the composites were more crystalline than pure PANI. PL spectra show that composites exhibit photoluminescent property. Conductivity of the composites (6.2 to 9.4 x 10(-2) S/cm) was higher than that of pristine PANI (3.7 x 10(-3) S/cm). The nanocomposites exhibited superparamagnetism. Formation mechanism of the core-shell structured nanocomposites and the effect of modified magnetic nanoparticles on the electro-magnetic properties of the Fe3O4@SiO2/PANI nanocomposites are also investigated. This method provides a new strategy for the generation of multi-functional nanocomposites that composed of other conducting polymers and metal nanoparticles.

Shrinkage vectors of a flowable composite in artificial cavity models with different boundary conditions: Ceramic and Teflon.

PubMed

Kaisarly, Dalia; El Gezawi, Moataz; Xu, Xiaohui; Rösch, Peter; Kunzelmann, Karl-Heinz

2018-01-01

Polymerization shrinkage of dental resin composites leads to stress build-up at the tooth-restoration interface that predisposes the restoration to debonding. In contrast to the heterogeneity of enamel and dentin, this study investigated the effect of boundary conditions in artificial cavity models such as ceramic and Teflon. Ceramic serves as a homogenous substrate that provides optimal bonding conditions, which we presented in the form of etched and silanized ceramic in addition to an etched, silanized and bonded ceramic cavity. In contrast, the Teflon cavity presented a non-adhesive boundary condition that provided an exaggerated condition of poor bonding as in the case of contamination during the application procedure or a poor bonding substrate such as sclerotic or deep dentin. The greatest 3D shrinkage vectors and movement in the axial direction were observed in the ceramic cavity with the bonding agent followed by the silanized ceramic cavity, and smallest shrinkage vectors and axial movements were observed in the Teflon cavity. The shrinkage vectors in the ceramic cavities exhibited downward movement toward the cavity bottom with great downward shrinkage of the free surface. The shrinkage vectors in the Teflon cavity pointed towards the center of the restoration with lateral movement greater at one side denoting the site of first detachment from the cavity walls. These results proved that the boundary conditions, in terms of bonding substrates, significantly influenced the shrinkage direction. Copyright © 2017 Elsevier Ltd. All rights reserved.

Cytotoxicity of silica-glass fiber reinforced composites.

PubMed

Meriç, Gökçe; Dahl, Jon E; Ruyter, I Eystein

2008-09-01

Silica-glass fiber reinforced polymers can be used for many kinds of dental applications. The fiber reinforcement enhances the mechanical properties of the polymers, and they have good esthetic attributes. There is good initial bonding of glass fibers to polymers via an interface made from silane coupling agents. The aim of this in vitro study was to determine the cytotoxicity of two polymers reinforced with two differently sized silica-glass fibers before and after thermal cycling. Cytotoxicity of the polymers without fibers was also evaluated. Two different resin mixtures (A and B) were prepared from poly(vinyl chloridecovinylacetate) powder and poly(methyl methacrylate) (PMMA) dissolved in methyl methacrylate and mixed with different cross-linking agents. The resin A contained the cross-linking agents ethylene glycol dimethacrylate and 1,4-butanediol dimethacrylate, and for resin B diethylene glycol dimethacrylate was used. Woven silica-glass fibers were used for reinforcement. The fibers were sized with either linear poly(butyl methacrylate)-sizing or cross-linking PMMA-sizing. Cytotoxicity was evaluated by filter diffusion test (ISO 7405:1997) of newly made and thermocycled test specimens. Extracts were prepared according to ISO 10993-12 from newly made and from thermocycled specimens and tested by the MTT assay. The results from the experiments were statistically analyzed by one-way ANOVA and Tukey's test (rho<0.05). The filter diffusion test disclosed no change in staining intensity at the cell-test sample contact area indicating non-cytotoxicity in all experimental groups. Cell viability assessed by MTT assay was more than 90% in all experimental groups. All are non-cytotoxic. It can be concluded that correctly processed heat polymerized silica-glass fiber reinforced polymers induced no cytotoxicity and that thermocycling did not alter this property.

Silanes as Fuel for Aerospace Propulsion

NASA Astrophysics Data System (ADS)

Simone, Domenico; Bruno, Claudio; Hidding, Bernhard

In the light of recently revived interest in high energy density fuels for aerospace applications1,2), a new look is being given at unconventional fuels. Among the latter are hydrides, because their hydrogen content and density. Among hydrides silanes are of interest because of their combustion and energetic properties.Silanes are silicon hydrides organized in molecular chains similar to those of hydrocarbons; at STP, lower silanes (SiH4, Si2H6) are gaseous and extremely pyrophoric; with increasing chain length, silanes become liquid from trisilane (Si3H8) on, and therefore easily pumped. Another important feature of silanes is the large amount of hydrogen theoretically available by thermal decomposition: in fact at moderate temperatures (about 500 K) the chains begin to break and at 700 K their decomposition is complete, yielding silicon and gaseous hydrogen, useful for propulsion in combination with air nitrogen and oxygen. This last feature, if confirmed, could identify silanes not only as energy carriers but also components in bi-fuel systems. To assess their theoretical performance, simulations were conducted assuming silanes and/or their thermal decomposition products in combination with various oxidizers and air. Preliminary results are suggestive of their potential for some specialized applications, especially where compactness is at premium.

Degradation of bare and silanized silicon wafer surfaces by constituents of biological fluids.

PubMed

Dekeyser, C M; Buron, C C; Derclaye, S R; Jonas, A M; Marchand-Brynaert, J; Rouxhet, P G

2012-07-15

The 24 h stability of bare silicon wafers as such or silanized with CH(3)O-(CH(2)-CH(2)-O)(n)-C(3)H(6)-trichlorosilane (n=6-9) was investigated in water, NaCl, phosphate and carbonate solutions, and in phosphate buffered saline (PBS) at 37 °C (close to biological conditions regarding temperature, high ionic strength, and pH). The resulting surfaces were analyzed using ellipsometry, X-ray Reflectometry (XRR), X-ray Photoelectron Spectroscopy (XPS), and Atomic Force Microscopy (AFM). Incubation of the silanized wafers in phosphate solution and PBS provokes a detachment of the silane layer. This is due to a hydrolysis of Si-O bonds which is favored by the action of phosphate, also responsible for a corrosion of non-silanized wafers. The surface alteration (detachment of silane layer and corrosion of the non-silanized wafer) is also important with carbonate solution, due to a higher pH (8.3). The protection of the silicon oxide layer brought by silane against the action of the salts is noticeable for phosphate but not for carbonate. Copyright © 2012 Elsevier Inc. All rights reserved.

Synthesis of Secondary Aromatic Amides via Pd-Catalyzed Aminocarbonylation of Aryl Halides Using Carbamoylsilane as an Amide Source.

PubMed

Tong, Wenting; Cao, Pei; Liu, Yanhong; Chen, Jianxin

2017-11-03

Using N-methoxymethyl-N-organylcarbamoyl(trimethyl)silanes as secondary amides source, the direct transformation of aryl halides into the corresponding secondary aromatic amides via palladium-catalyzed aminocarbonylation is described. The reactions tolerated a broad range of functional groups on the aryl ring except big steric hindrance of substituent. The types and the relative position of substituents on the aryl ring impact the coupling efficiency.

Natural Attenuation of Persistent Chemical Warfare Agent VX ...

EPA Pesticide Factsheets

Report Natural attenuation of persistent CWAs such as VX was investigated and occurs, given sufficient time (days to weeks). Natural attenuation was found to be faster at warmer temperatures (i.e., 35 °C and 25 °C) than cooler temperatures (i.e., 10 °C). Attenuation of VX was material dependent with a general trend of faster to slower attenuation in the order ceramic tile - galvanized metal - silanized glass - painted drywall. Trace amounts of VX may still be present weeks to months after a contamination event.

Conservation studies on ornamental and building stones of north-eastern Sicily. Geomineralogical and porosimetric investigations.

PubMed

Cardiano, P; Sergi, S; Triscari, M; Piraino, P

2001-01-01

The effectiveness, as preserving agents, of a series of chemical compounds (silanes, siloxanes, epoxides, perfluoropolyethers, acrylates, acrylsilicones) has been tested on lithic materials mainly used in artistic stoneworks of north-eastern Sicily. The selection and classification of the stone types, based on geomineralogical criteria follows a brief excursus about their use as artistic materials. The results of the porosimetric investigations, before and after conservation treatments, are reported. In addition, polarizing mineralogical microscope photos of the studied lithoid materials are presented.

Effect of surface treatment of fiberglass posts on bond strength to root dentin.

PubMed

Valdivia, Andréa Dolores Correia Miranda; Novais, Veridiana Resende; Menezes, Murilo de Sousa; Roscoe, Marina Guimarães; Estrela, Carlos; Soares, Carlos José

2014-01-01

This study evaluated the influence of the surface treatments of fiberglass posts on bond strength to root dentin using push-out test. Forty bovine incisor roots were endodontically treated. The surface of the fiberglass posts (Exacto #2, Angelus) were treated using 4 different protocols (n=10): Control - 70% ethanol for 1 min; 37% phosphoric acid for 1 min; 10% hydrofluoric acid for 1 min; and 24% hydrogen peroxide for 1 min. After a silane coupling agent was applied for 1 min and all posts were cemented using self-adhesive resin cement (RelyX Unicem, 3M-ESPE). The roots were sectioned and two 1-mm-thick slices were obtained from each third: cervical, middle and apical. The specimens were subjected to the push-out test with a crosshead speed of 0.5 mm/min. Data were analyzed by repeated measures ANOVA followed by Tukey's HSD tests (=0.05). The surface treatment (p<0.001) and root third region (p=0.007) factors were significant. The retention to root canal was affected by surface treatment type. The post surface treatment with 24% hydrogen peroxide for 1 min yielded significantly higher bond strength when the fiberglass posts were cemented with RelyX Unicem.

Enhanced interfacial interaction and antioxidative behavior of novel halloysite nanotubes/silica hybrid supported antioxidant in styrene-butadiene rubber

NASA Astrophysics Data System (ADS)

Lin, Jing; Luo, Yuanfang; Zhong, Bangchao; Hu, Dechao; Jia, Zhixin; Jia, Demin

2018-05-01

A novel antioxidant (HS-s-RT) to improve the mechanical properties and anti-aging performance of styrene-butadiene (SBR) composites was prepared by antioxidant intermediate p-aminodiphenylamine (RT) grafting on the surface of halloysite nanotubes/silica hybrid (HS) via the linkage of silane coupling agent. The analysis of SEM and rubber processing analyzer (RPA) demonstrated HS-s-RT was uniformly dispersed in SBR, and stronger interfacial interaction between HS-s-RT and SBR was formed. Consequently, SBR/HS-s-RT composites have improving mechanical properties. Furthermore, the test of the retention of mechanical properties, Fourier transform infrared spectroscopy with attenuated total reflectance (FTIR-ATR), and oxidation induction time (OIT) showed HS-s-RT can effectively improve the anti-aging effect of SBR composites than corresponding low molecular-weight antioxidant N-isopropyl-N‧-phenyl-4-phenylenediamin (4010NA). Then, the mechanism of thermo-oxidative aging of SBR/HS composites was also investigated, and the superior antioxidative efficiency is attributed to the uniform dispersion and excellent migration resistance of HS-s-RT. Hence, this novel antioxidant might open up new opportunities for the fabrication of high-performance rubber composites due to its superior anti-aging effect and reinforcement.

Highly Stable and Flexible Pressure Sensors with Modified Multi-Walled Carbon Nanotube/Polymer Composites for Human Monitoring

PubMed Central

He, Yin; Ming, Yue; Li, Wei; Li, Yafang; Wu, Maoqi; Song, Jinzhong; Li, Xiaojiu; Liu, Hao

2018-01-01

A facile method for preparing an easy processing, repeatable and flexible pressure sensor was presented via the synthesis of modified multi-walled carbon nanotubes (m-MWNTs) and polyurethane (PU) films. The surface modification of multi-walled carbon nanotubes (MWNTs) simultaneously used a silane coupling agent (KH550) and sodium dodecyl benzene sulfonate (SDBS) to improve the dispersibility and compatibility of the MWNTs in a polymer matrix. The electrical property and piezoresistive behavior of the m-MWNT/PU composites were compared with raw multi-walled carbon nanotube (raw MWNT)/PU composites. Under linear uniaxial pressure, the m-MWNT/PU composite exhibited 4.282%kPa−1 sensitivity within the pressure of 1 kPa. The nonlinear error, hysteresis error and repeatability error of the piezoresistivity of m-MWNT/PU decreased 9%, 16.72% and 54.95% relative to raw MWNT/PU respectively. Therefore, the piezoresistive response of m-MWNT/PU had better stability than that of raw MWNT/PU composites. The m-MWNT/PU sensors could be utilized in wearable devices for body movement detection, monitoring of respiration and pressure detection in garments. PMID:29701643

Highly Stable and Flexible Pressure Sensors with Modified Multi-Walled Carbon Nanotube/Polymer Composites for Human Monitoring.

PubMed

He, Yin; Ming, Yue; Li, Wei; Li, Yafang; Wu, Maoqi; Song, Jinzhong; Li, Xiaojiu; Liu, Hao

2018-04-26

A facile method for preparing an easy processing, repeatable and flexible pressure sensor was presented via the synthesis of modified multi-walled carbon nanotubes (m-MWNTs) and polyurethane (PU) films. The surface modification of multi-walled carbon nanotubes (MWNTs) simultaneously used a silane coupling agent (KH550) and sodium dodecyl benzene sulfonate (SDBS) to improve the dispersibility and compatibility of the MWNTs in a polymer matrix. The electrical property and piezoresistive behavior of the m-MWNT/PU composites were compared with raw multi-walled carbon nanotube (raw MWNT)/PU composites. Under linear uniaxial pressure, the m-MWNT/PU composite exhibited 4.282%kPa −1 sensitivity within the pressure of 1 kPa. The nonlinear error, hysteresis error and repeatability error of the piezoresistivity of m-MWNT/PU decreased 9%, 16.72% and 54.95% relative to raw MWNT/PU respectively. Therefore, the piezoresistive response of m-MWNT/PU had better stability than that of raw MWNT/PU composites. The m-MWNT/PU sensors could be utilized in wearable devices for body movement detection, monitoring of respiration and pressure detection in garments.

An insight into current concepts and techniques in resin bonding to high strength ceramics.

PubMed

Luthra, R; Kaur, P

2016-06-01

Reliable bonding between high strength ceramics and resin composite cement is difficult to achieve because of their chemical inertness and lack of silica content. The aim of this review was to assess the current literature describing methods for resin bonding to ceramics with high flexural strength such as glass-infiltrated alumina and zirconia, densely sintered alumina and yttria-partially stabilized tetragonal zirconia polycrystalline ceramic (Y-TZP) with respect to bond strength and bond durability. Suitable peer reviewed publications in the English language were identified through searches performed in PubMed, Google Search and handsearches. The keywords or phrases used were 'resin-ceramic bond', 'silane coupling agents', 'air particle abrasion', 'zirconia ceramic' and 'resin composite cements'. Studies from January 1989 to June 2015 were included. The literature demonstrated that there are multiple techniques available for surface treatments but bond strength testing under different investigations have produced conflicting results. Within the scope of this review, there is no evidence to support a universal technique of ceramic surface treatment for adhesive cementation. A combination of chemical and mechanical treatments might be the recommended solution. The hydrolytic stability of the resin ceramic bond should be enhanced. © 2016 Australian Dental Association.

A New Antiwear Additive/Surface Pretreatment for PFPE Liquid Lubricants

NASA Technical Reports Server (NTRS)

Morales, Wilfredo; Fusaro, Robert L.; Siebert, Mark; Keith, Theo; Jansen, Ralph; Herrera-Fierro, Pilar

1995-01-01

Pin-on-disk tribology experiments were conducted on a perfluoroalkylelher (PFPE) liquid lubricant with and without a new PFPE lubricant antiwear additive material, a silane. It was found that the silane provided moderate improvement in the antiwear performance of the PFPE lubricant when applied to the metallic surface as a surface coating or when added to the PFPE as a dispersion (emulsion). Slightly better results were obtained by using the combination of a surface coating and an emulsion of the silane. The silane emulsions or coatings did not affect the friction properties of the lubricant. Micro-Fourier transformation infrared (muFTIR) spectroscopy analysis was performed to study silane transfer films and the degradation of the PFPE. The silane was found to mitigate degradation of the PFPE which may have been the major reason for the improved antiwear performance observed.

Chitosan-silane sol-gel hybrid thin films with controllable layer thickness and morphology.

PubMed

Spirk, Stefan; Findenig, Gerald; Doliska, Ales; Reichel, Victoria E; Swanson, Nicole L; Kargl, Rupert; Ribitsch, Volker; Stana-Kleinschek, Karin

2013-03-01

The preparation of thin films of chitosan-silane hybrid materials by combining sol-gel processing and spin coating is reported. A variety of silanes can be used as starting materials for the preparation of such thin films, namely tetraethoxysilane, tri-tert-butoxysilanol, trimethylethoxysilane, p-trifluoromethyltetra-fluorophenyltriethoxysilane, trivinylmethoxysilane, (methoxymethyl)trimethyl-silane, and hexamethoxydisilane. These silanes are subjected to a sol-gel process before they are added to acidic chitosan solutions. The chitosan:silane ratio is kept constant at 6:1 (w/w) and dilutions with ethanol are prepared and spin coated. Depending on the degree of dilution, film thickness can be controlled in a range between 5 and 70 nm. For the determination of additional surface properties, static water contact angle measurements and atomic force microscopy have been employed. Copyright © 2012 Elsevier Ltd. All rights reserved.

Reinforcement of Dental Methacrylate with Glass Fiber after Heated Silane Application

PubMed Central

Fonseca, Rodrigo Borges; de Paula, Marcella Silva; Favarão, Isabella Negro; Kasuya, Amanda Vessoni Barbosa; de Almeida, Letícia Nunes; Mendes, Gustavo Adolfo Martins; Carlo, Hugo Lemes

2014-01-01

This study evaluated the influence of silane heat treatment and glass fiber fabrication type, industrially treated (I) or pure (P), on flexural and compressive strength of methacrylate resin bars (BISGMA/TEGDMA, 50/50%). Six groups (n = 10) were created: I-sil: I/silanated; P-sil: P-silanated; I-sil/heat: I/silanated heated to 100°; P-sil/heat: P/silanated heated to 100°; (I: I/not silanated; and P: P/not silanated. Specimens were prepared for flexural strength (10 × 2 × 1 mm) and for compressive strength 9.5 × 5.5 × 3 mm) and tested at 0.5 mm/min. Statistical analysis demonstrated the following for flexural strength (P < 0.05): I-sil: 155.89 ± 45.27BC; P-sil: 155.89 ± 45.27BC; I-sil/heat: 130.20 ± 22.11C; P-sil/heat: 169.86 ± 50.29AB; I: 131.87 ± 15.86C. For compressive strength, the following are demonstrated: I-sil: 1367.25 ± 188.77ab; P-sil: 867.61 ± 102.76d; I-sil/heat: 1162.98 ± 222.07c; P-sil/heat: 1499.35 ± 339.06a; and I: 1245.78 ± 211.16bc. Due to the impossibility of incorporating the stipulated amount of fiber, P group was excluded. Glass fiber treatment with heated silane enhanced flexural and compressive strength of a reinforced dental methacrylate. PMID:24967361

Stoichiometry and possible mechanism of SiH/sub 4/-O/sub 2/ explosions

DOE Office of Scientific and Technical Information (OSTI.GOV)

Hartman, J.R.; Famil-Ghiriha, J.; Ring, M.A.

1987-04-01

The products of silane-O/sub 2/ mixture explosions vary with mixture composition. For O/sub 2/-rich mixtures (>70% O/sub 2/), the products are H/sub 2/O and SiO/sub 2/. As the mixtures become richer in silane, H/sub 2/ replaces H/sub 2/O as a final product. For very SiH/sub 4/-rich mixtures (>70% SiH/sub 4/), the products are H/sub 2/, SiO/sub x/, and Si. The fact that silane is totally consumed in silane-rich mixtures (70-90% silane) demonstrates that solid particle formation (SiO/sub 2/, SiO, and Si) occurs very rapidly and that the accompanying heat release is essential to drive the reactions to completion. It ismore » also clear that the explosion of a silane-rich mixture is primarily a thermal explosion of silane. Effects due to problems associated with upper pressure limit measurements and mechanistic aspects of the SiH/sub 4/-O/sub 2/ explosion reaction are discussed.« less

Characterization of the reactivity of a silica derived from acid activation of sepiolite with silane by 29Si and 13C solid-state NMR.

PubMed

Valentín, J L; López-Manchado, M A; Posadas, P; Rodríguez, A; Marcos-Fernández, A; Ibarra, L

2006-06-15

The mechanism of the reaction between a silica sample coming from acid treatment of sepiolite (denominated Silsep) and an organosilane, namely bis(triethoxysilylpropyl)tetrasulfane (TESPT), has been evaluated by solid state NMR spectroscopy, being compared with the silanization reaction of a commercial silica. The effect of the silane concentration and temperature on the course of the reaction was considered. Experimental results indicate that the silanization reaction is more effective in the case of Silsep, favoring both the reaction of silane molecules with the filler surface and the reaction between neighboring silane molecules. This different behavior is attributed to structural factors, moisture, and number of acid centers on silica surface. Environmental scanning electron microscopy (ESEM) was used to deposit micrometric water drops on the surface of these samples and to evaluate the proportion and distribution of the organophylization process.

Molecularly imprinted nanopatterns for the recognition of biological warfare agent ricin.

PubMed

Pradhan, Santwana; Boopathi, M; Kumar, Om; Baghel, Anuradha; Pandey, Pratibha; Mahato, T H; Singh, Beer; Vijayaraghavan, R

2009-11-15

Molecularly imprinted polymer (MIP) for biological warfare agent (BWA) ricin was synthesized using silanes in order to avoid harsh environments during the synthesis of MIP. The synthesized MIP was utilized for the recognition of ricin. The complete removal of ricin from polymer was confirmed by fluorescence spectrometer and SEM-EDAX. SEM and EDAX studies confirmed the attachment of silane polymer on the surface of silica gel matrix. SEM image of Ricin-MIP exhibited nanopatterns and it was found to be entirely different from the SEM image of non-imprinted polymer (NIP). BET surface area analysis revealed more surface area (227 m(2)/g) for Ricin-MIP than that of NIP (143 m(2)/g). In addition, surface area study also showed more pore volume (0.5010 cm(3)/g) for Ricin-MIP than that of NIP (0.2828 cm(3)/g) at 12 nm pore diameter confirming the presence of imprinted sites for ricin as the reported diameter of ricin is 12 nm. The recognition and rebinding ability of the Ricin-MIP was tested in aqueous solution. Ricin-MIP rebound more ricin when compared to the NIP. Chromatogram obtained with Ricin-MIP exhibited two peaks due to imprinting, however, chromatogram of NIP exhibited only one peak for free ricin. SDS-PAGE result confirmed the second peak observed in chromatogram of Ricin-MIP as ricin peak. Ricin-MIP exhibited an imprinting efficiency of 1.76 and it also showed 10% interference from the structurally similar protein abrin.

Synthesis of tris- and tetrakis(pentafluoroethyl)silanes.

PubMed

Steinhauer, Simon; Bader, Julia; Stammler, Hans-Georg; Ignat'ev, Nikolai; Hoge, Berthold

2014-05-12

The synthesis and complete characterization of functional, highly Lewis acidic tris(pentafluoroethyl)silanes as well as tetrakis(perfluoroalkyl)silanes Si(C2F5)4 and Si(C2F5)3 CF3 by direct fluorination is described. The reaction of SiCl4 with LiC2F5 invariably affords (pentafluoroethyl)fluorosilicates. To avoid silicate formation by fluoride transfer from LiC2F5 the Lewis acidity of the silane has to be decreased by electron-donating substituents, such as dialkylamino groups. The easily accessible Si(C2F5)3 NEt2 is a valuable precursor for a series of tris(pentafluoroethyl)silanes. © 2014 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Silane-propane ignitor/burner

DOEpatents

Hill, R.W.; Skinner, D.F. Jr.; Thorsness, C.B.

1983-05-26

A silane propane burner for an underground coal gasification process which is used to ignite the coal and to controllably retract the injection point by cutting the injection pipe. A narrow tube with a burner tip is positioned in the injection pipe through which an oxidant (oxygen or air) is flowed. A charge of silane followed by a supply of fuel, such as propane, is flowed through the tube. The silane spontaneously ignites on contact with oxygen and burns the propane fuel.

Silane-propane ignitor/burner

DOEpatents

Hill, Richard W.; Skinner, Dewey F.; Thorsness, Charles B.

1985-01-01

A silane propane burner for an underground coal gasification process which is used to ignite the coal and to controllably retract the injection point by cutting the injection pipe. A narrow tube with a burner tip is positioned in the injection pipe through which an oxidant (oxygen or air) is flowed. A charge of silane followed by a supply of fuel, such as propane, is flowed through the tube. The silane spontaneously ignites on contact with oxygen and burns the propane fuel.

Effects of sandblasting and silica coating on the bond strength of rebonded mechanically retentive ceramic brackets.

PubMed

Toroglu, M Serdar; Yaylali, Sirin

2008-08-01

The aim of this study was to determine the bond strength of rebonded mechanically retentive ceramic brackets after treatment with 2 abrasive techniques. In addition to a group of new brackets, 3 groups were treated according to the following conditions of debonded ceramic bracket bases: sandblasting, sandblasting + silane, and silica coating + silane (15 in each group). Treated ceramic brackets were rebonded on premolars. The samples were stored in distilled deionized water for 24 hours at 37 degrees C in an incubator and then thermocycled for 1000 times between 5 degrees C and 55 degrees C. Shear force was applied to the enamel-adhesive interface until debonding. The highest bond strength values were in the silica coating + silane and the new bracket groups (12.7 and 12.0 MPa, respectively), followed by the sandblasting + silane group (10.5 MPa). The sandblasting group had a significantly lower bond strength value (4.5 MPa). No enamel fracture was noted in any sample tested. In the new bracket and the sandblasting + silane groups, 20% of the samples had adhesive remnant index scores of 2, and 80% had scores of 3. In the sandblasting group, all specimens debonded at the bracket-adhesive interface. The silica coating + silane group showed mixed failures. Sandblasting + silane and silica coating + silane applications on debonded ceramic bracket base can produce bond strengths comparable with new brackets.

Heat treatment of pre-hydrolyzed silane increases adhesion of phosphate monomer-based resin cement to glass ceramic.

PubMed

de Carvalho, Rodrigo Furtado; Cotes, Caroline; Kimpara, Estevão Tomomitsu; Leite, Fabíola Pessoa Pereira; Özcan, Mutlu

2015-01-01

This study evaluated the influence of different forms of heat treatment on a pre-hydrolyzed silane to improve the adhesion of phosphate monomer-based (MDP) resin cement to glass ceramic. Resin and feldspathic ceramic blocks (n=48, n=6 for bond test, n=2 for microscopy) were randomly divided into 6 groups and subject to surface treatments: G1: Hydrofluoric acid (HF) 9.6% for 20 s + Silane + MDP resin cement (Panavia F); G2: HF 9.6% for 20 s + Silane + Heat Treatment (oven) + Panavia F; G3: Silane + Heat Treatment (oven) + Panavia F; G4: HF 9.6% for 20 s + Silane + Heat Treatment (hot air) + Panavia F; G5: Silane + Heat Treatment (hot air) + Panavia F; G6: Silane + Panavia F. Microtensile bond strength (MTBS) test was performed using a universal testing machine (1 mm/min). After debonding, the substrate and adherent surfaces were analyzed using stereomicroscope and scanning electron microscope (SEM) to categorize the failure types. Data were analyzed statistically using two-way test ANOVA and Tukey's test (=0.05). Heat treatment of the silane containing MDP, with prior etching with HF (G2: 13.15 ± 0.89a; G4: 12.58 ± 1.03a) presented significantly higher bond strength values than the control group (G1: 9.16 ± 0.64b). The groups without prior etching (G3: 10.47 ± 0.70b; G5: 9.47 ± 0.32b) showed statistically similar bond strength values between them and the control group (G1). The silane application without prior etching and heat treatment resulted in the lowest mean bond strength (G6: 8.05 ± 0.37c). SEM analysis showed predominantly adhesive failures and EDS analysis showed common elements of spectra (Si, Na, Al, K, O, C) characterizing the microstructure of the glass-ceramic studied. Heat treatment of the pre-hydrolyzed silane containing MDP in an oven at 100 °C for 2 min or with hot air application at 50 ± 5 ºC for 1 min, was effective in increasing the bond strength values between the ceramic and resin cement containing MDP.

[Spectroscopic study on film formation mechanism and structure of composite silanes-V-Zr passive film].

PubMed

Wang, Lei; Liu, Chang-sheng; Shi, Lei; An, Cheng-qiang

2015-02-01

A composite silanes-V-Zr passive film was overlayed on hot-dip galvanized steel. Attenuated total reflection Fourier transformed infrared spectroscopy (ATR-FTIR), X-ray photoelectron spectrometer (XPS) and radio frequency glow discharge optical emission spectrometry (rf-GD-OES) were used to characterize the molecular structure of the silanes-V-Zr passive film. The mechanism of film formation was discussed: The results show that the silane molecules are crosslinked as the main film former and inorganic inhibitor is even distributed in the film. The fitting peak of 100.7 eV in XPS single Si2p energy range spectra of the composite silanes-V-Zr passive film and the widening and strengthening of the Si--O infrared absorption peak at 1100 cm(-1) indicate that the silanes were adsorbed on the surface of zinc with chemical bond of Si--O--Zn, and the silane molecules were connected with each other by bond of Si--O--Si. Two characteristic absorption peaks of amide at 1650 and 1560 cm(-1) appear in the infrared spectroscopy of the composite silanes-V-Zr passive film, and a characteristic absorption peak of epoxy groups at 910 cm(-1) disappears in the infrared spectroscopy of the passive film. The results indicate that gamma-APT can be prepared through nucleophilic ring-opening of ethylene oxide in gamma-GPT molecule to form C--N covalent bonds. The rf-GD-OES results indicate that there is a oxygen enriched layer in 0.3 microm depth of the composite silanes-V-Zr passive film. Moreover, ZrF4, ZrO2 and some inorganic matter obtained by the reaction during the forming processof the composite silanes-V-Zr passive film are distributed evenly throughout the film. According to the film composition, the physical processes and chemical reactions during the film forming process were studied by using ATR-FTIR. Based on this, the film forming mechanism was proposed.

Corrosion protection and adhesion properties of the epoxy coating applied on the steel substrate pre-treated by a sol-gel based silane coating filled with amino and isocyanate silane functionalized graphene oxide nanosheets

NASA Astrophysics Data System (ADS)

Parhizkar, Nafise; Ramezanzadeh, Bahram; Shahrabi, Taghi

2018-05-01

This research has focused on the effect of graphene oxide (GO) nano-fillers embedded in the sol-gel based silane coating on the corrosion protection and adhesion properties of the epoxy coating applied on the steel substrate pre-treated by silane coatings. For this purpose, a mixture of Methyltriethoxysilane (MTES) and Tetraethylorthosilicate (TEOS) silane precursors was used for preparation of composite matrix and the GO nanosheets, which are covalently functionalized with 3-(Triethoxysilyl)propyl isocyanate (TEPI, IGO nano-fillers) and 3-aminopropyltriethoxysilane (APTES, AGO nano-fillers), were used as filler. The GO, AGO and IGO nanosheets were characterized by Fourier Transform Infrared Spectroscopy (FT-IR), UV-Visible analysis and field emission-scanning electron microscopy techniques. The performance of the silane/epoxy coatings was investigated by pull-off adhesion, cathodic delamination, salt spray and electrochemical impedance spectroscopy (EIS) tests. Results revealed that AGO and IGO nano-fillers significantly improved the corrosion resistance and adhesion properties of the top epoxy coating due to better compatibility with silane matrix, excellent barrier properties and the formation of covalent bonds with the top epoxy coating.

VAPOR PHASE MERCURY SORPTION BY ORGANIC SULFIDE MODIFIED BIMETALLIC IRON-COPPER NANOPARTICLE AGGREGATES

EPA Science Inventory

Novel organic sulfide modified bimetallic iron-copper nanoparticle aggregate sorbent materials have been synthesized for removing elemental mercury from vapor streams at elevated temperatures (120-140 °C). Silane based (disulfide silane and tetrasulfide silane) and alkyl sulfide ...

40 CFR 721.9501 - Silane, triethoxy[3-oxiranylmethoxy)propyl]-.

Code of Federal Regulations, 2010 CFR

2010-07-01

...) TOXIC SUBSTANCES CONTROL ACT SIGNIFICANT NEW USES OF CHEMICAL SUBSTANCES Significant New Uses for Specific Chemical Substances § 721.9501 Silane, triethoxy[3-oxiranylmethoxy)propyl]-. (a) Chemical substance and significant new uses subject to reporting. (1) The chemical substance identified as silane...

Method and apparatus for forming a carbon-silicon bond in a silane

DOEpatents

Schattenmann, Florian Johannes

2002-01-01

A method for forming at least one product silane, comprising reacting a transition metal hydride with a starting silane in a presence of a catalyst and at a temperature that exceeds a threshold temperature associated with said reacting.

Development of acceptance criteria for batches of silane primer for external tank thermal protection system bonding applications

NASA Technical Reports Server (NTRS)

Mikes, F.

1984-01-01

Silane primers for use as thermal protection on external tanks were subjected to various analytic techniques to determine the most effective testing method for silane lot evaluation. The analytic methods included high performance liquid chromatography, gas chromatography, thermogravimetry (TGA), and fourier transform infrared spectroscopy (FTIR). It is suggested that FTIR be used as the method for silane lot evaluation. Chromatograms, TGA profiles, bar graphs showing IR absorbances, and FTIR spectra are presented.

Potential of Silanes for Chromate Replacement in Metal Finishing Industries

DTIC Science & Technology

2002-09-16

POTENTIAL OF SILANES FOR CHROMATE REPLACEMENT IN METAL FINISHING INDUSTRIES Wim J. van Ooij*, Danqing Zhu, Vignesh Palanivel, J. Anna Lamar...18 2 POTENTIAL OF SILANES FOR CHROMATE REPLACEMENT IN METAL FINISHING INDUSTRIES Wim J. van Ooij, Danqing Zhu, Vignesh Palanivel, J. Anna Lamar

Preparation of a surface-grafted imprinted ceramic membrane for selective separation of molybdate anion from water solutions.

PubMed

Zeng, Jianxian; Dong, Zhihui; Zhang, Zhe; Liu, Yuan

2017-07-05

A surface-grafted imprinted ceramic membrane (IIP-PVI/CM) for recognizing molybdate (Mo(VI)) anion was prepared by surface-initiated graft-polymerization. Firstly, raw alumina ceramic membrane (CM) was deposited with SiO 2 active layer by situ hydrolysis deposition method. Subsequently, γ-methacryloxy propyl trimethoxyl silane (MPS) was used as a coupling agent to introduce double bonds onto the SiO 2 layer (MPS-CM). Then, 1-vinylimidazole (VI) was employed as a functional monomer to graft-polymerization onto the MPS-CM (PVI-CM). During the graft-polymerization, the influence factors of grafting degree of PVI were investigated in detail. Under optimum conditions (monomer concentration 20wt%, temperature 70°C, initiator amount 1.1wt% and reaction time 8h), the grafting degree of 20.39g/100g was obtained. Further, Mo(VI) anion was used as a template to imprint in the PVI-CM by employing 1,6-dibromohexane as a cross-linking agent, and then Mo(VI) was removed, obtaining the IIP-PVI/CM with many imprinted cavities for Mo(VI). Thereafter, static adsorption and dynamic separation properties of IIP-PVI/CM for Mo(VI) were studied. Results indicate that IIP-PVI/CM shows a specific selectivity for Mo(VI) with the adsorption capacity of 0.69mmol/100g, and the selectivity coefficient of IIP-PVI/CM is 7.48 for molybdate to tungstate anions. During the dynamic separation, IIP-PVI/CM has also good selectivity for separation of Mo(VI) and W(VI) anions. Copyright © 2017 Elsevier B.V. All rights reserved.

Union Carbide Corp. polysilicon status and plans

NASA Technical Reports Server (NTRS)

Leipold, M. H.

1982-01-01

The status of polysilicon activities is summarized highlighted by moving the silane portion of the experimental process system development unit (EPSDU) to Washougal, Washington. The completion and operation of the silane EPSDU, is discussed along with research on the silane-to-silicon deposition process. Progress on the dichlorosilane process is also reported.

Review of the potential of silanes as rocket/scramjet fuels

NASA Astrophysics Data System (ADS)

Hidding, Bernhard; Pfitzner, Michael; Simone, Domenico; Bruno, Claudio

2008-07-01

Experimental use as well as theoretical considerations regarding silanes as fuels for spacecrafts and supersonic flight are reviewed. The historical circumstances leading to the utilization of monosilane as a fuel additive for scramjets are highlighted and milestones in the chemical research on silanes are summarized. Recent developments such as the use of monosilane as an ignition aid in the NASA X-43A scramjet flights as well as general progress in silicon hydride research, including liquid higher silanes and the resulting potential for the propulsion field are discussed.

Enhanced diode characteristics of organic solar cell with silanized fluorine doped tin oxide electrode

NASA Astrophysics Data System (ADS)

Sachdeva, Sheenam; Sharma, Sameeksha; Singh, Devinder; Tripathi, S. K.

2018-05-01

To investigate the diode characteristics of organic solar cell based on the planar heterojunction of 4,4'- cyclohexylidenebis[N,N-bis(4-methylphenyl)benzenamine] (TAPC) and fullerene (C70), we report the use of silanized fluorine-doped tin oxide (FTO) anode with N1-(3-trimethoxysilylpropyl)diethyltriamine (DETA) forming monolayer. The use of silanized FTO results in the decrease of saturation current density and diode ideality factor of the device. Such silanized FTO anode is found to enhance the material quality and improve the device properties.

Impact Strength and Flexural Properties Enhancement of Methacrylate Silane Treated Oil Palm Mesocarp Fiber Reinforced Biodegradable Hybrid Composites

PubMed Central

Ibrahim, Nor Azowa; Ariffin, Hidayah; Yunus, Wan Md. Zin Wan

2014-01-01

Natural fiber as reinforcement filler in polymer composites is an attractive approach due to being fully biodegradable and cheap. However, incompatibility between hydrophilic natural fiber and hydrophobic polymer matrix restricts the application. The current studies focus on the effects of incorporation of silane treated OPMF into polylactic acid (PLA)/polycaprolactone (PCL)/nanoclay/OPMF hybrid composites. The composites were prepared by melt blending technique and characterize the composites with Fourier transform infrared spectroscopy (FTIR), thermogravimetric analysis (TGA), and scanning electron microscopy (SEM). FTIR spectra indicated that peak shifting occurs when silane treated OPMF was incorporated into hybrid composites. Based on mechanical properties results, incorporation of silane treated OPMF enhances the mechanical properties of unmodified OPMF hybrid composites with the enhancement of flexural and impact strength being 17.60% and 48.43%, respectively, at 10% fiber loading. TGA thermogram shows that incorporation of silane treated OPMF did not show increment in thermal properties of hybrid composites. SEM micrographs revealed that silane treated OPMF hybrid composites show good fiber/matrix adhesion as fiber is still embedded in the matrix and no cavity is present on the surface. Water absorption test shows that addition of less hydrophilic silane treated OPMF successfully reduces the water uptake of hybrid composites. PMID:25254230

Impact strength and flexural properties enhancement of methacrylate silane treated oil palm mesocarp fiber reinforced biodegradable hybrid composites.

PubMed

Eng, Chern Chiet; Ibrahim, Nor Azowa; Zainuddin, Norhazlin; Ariffin, Hidayah; Yunus, Wan Md Zin Wan

2014-01-01

Natural fiber as reinforcement filler in polymer composites is an attractive approach due to being fully biodegradable and cheap. However, incompatibility between hydrophilic natural fiber and hydrophobic polymer matrix restricts the application. The current studies focus on the effects of incorporation of silane treated OPMF into polylactic acid (PLA)/polycaprolactone (PCL)/nanoclay/OPMF hybrid composites. The composites were prepared by melt blending technique and characterize the composites with Fourier transform infrared spectroscopy (FTIR), thermogravimetric analysis (TGA), and scanning electron microscopy (SEM). FTIR spectra indicated that peak shifting occurs when silane treated OPMF was incorporated into hybrid composites. Based on mechanical properties results, incorporation of silane treated OPMF enhances the mechanical properties of unmodified OPMF hybrid composites with the enhancement of flexural and impact strength being 17.60% and 48.43%, respectively, at 10% fiber loading. TGA thermogram shows that incorporation of silane treated OPMF did not show increment in thermal properties of hybrid composites. SEM micrographs revealed that silane treated OPMF hybrid composites show good fiber/matrix adhesion as fiber is still embedded in the matrix and no cavity is present on the surface. Water absorption test shows that addition of less hydrophilic silane treated OPMF successfully reduces the water uptake of hybrid composites.

ICRF wall conditioning at TEXTOR-94 in the presence of a 2.25 T magnetic field

NASA Astrophysics Data System (ADS)

Esser, H. G.; Lyssoivan, A.; Freisinger, M.; Koch, R.; van Oost, G.; Weschenfelder, F.; Winter, J.; Textor-Icrh-Team

1997-02-01

To investigate alternative conditioning concepts for future fusion devices with permanent magnetic fields, plasmas produced by the coupling of ICRF power to He and gas mixtures of Helium + silane, have been analyzed in the presence of a 2.25 T toroidal magnetic field at TEXTOR-94. Their qualification for wall conditioning has been investigated for different He-pressures, PHe (1 × 10 -3 < PHe ( Pa) < 1 × 10 -1) and ICRF power, PICRF (100 < PICRF ( kW) < 800). Electron densities n e averaged along different radial lines of sight across the vacuum vessel from the top to the bottom have been obtained in the range 5 × 10 10 < ne ( cm-3) < 3 × 10 12. To study quantitatively the efficiency of hydrogen desorption from the first wall at different ICRF plasma conditions in a reproducible way, the first wall was presaturated by RG-glow discharges in H 2. The amount and the evolution of the H 2 desorption from rf discharge to rf discharge was determined by ion gauge measurements combined with mass spectrometry. To demonstrate the capability of the new method for plasma assisted thin film deposition, different amounts of silane (<50%) were added to the He gas. During the ICRF pulses, the silane molecules were dissociated in the plasma and the Si atoms stick to the wall. A good balance of the amount of Si disappearing from the gas phase and that measured by post mortem surface analyses of collector probes at the wall position was found.

Bioactive glass/polymer composite materials with mechanical properties matching those of cortical bone.

PubMed

Koleganova, Veronika A; Bernier, Suzanne M; Dixon, S Jeffrey; Rizkalla, Amin S

2006-06-01

Stress shielding resulting from mismatch in dynamic mechanical properties contributes to the reduced stability of osseous implants. Our objective was to develop biocompatible composites having mechanical properties similar to those of cortical bone. Polymers of urethane dimethacrylate (UDMA) and 2-hydroxyethyl methacrylate (HEMA, 0-20%) and composites containing bioactive glass particles (70% SiO(2), 25% CaO, and 5% P(2)O(5)), with or without silane treatment were prepared. Young's moduli of composites containing silane-treated glass (16 GPa) were significantly greater than those of composites containing untreated glass (12-13 GPa) or of unfilled polymers (5-6 GPa). Bioactive glass reduced water sorption by the composites and incorporation of silane-treated glass prevented HEMA-induced increases in water sorption. Osteoblast-like cells attached equally well to UDMA polymer and composite containing silane-treated bioactive glass. Thus, silane treatment improved the mechanical properties of bioactive glass composites without compromising biocompatibility. This material has a Young's modulus comparable to that of cortical bone. Therefore, silane-treated bioactive glass composites, when used as implant or cement materials, would reduce stress shielding and improve implant stability.

UV-SPR biosensor for biomolecular interaction studies

NASA Astrophysics Data System (ADS)

Geiss, F. A.; Fossati, S.; Khan, I.; Gisbert Quilis, N.; Knoll, W.; Dostalek, J.

2017-05-01

UV surface plasmon resonance (SPR) for direct in situ detection of protein binding events is reported. A crossed relief aluminum grating was employed for diffraction coupling to surface plasmons as an alternative to more commonly used attenuated total reflection method. Wavelength interrogation of SPR was carried out by using transmission measurements in order to probe odorant-binding protein 14 (OBP14) of the honey bee (Apis mellifera). The native oxide layer on the top of an aluminum grating sensor chip allows for covalent coupling of protein molecules by using regular silane-based linkers. The probing of bound OBP14 protein at UV with confined field of surface plasmons holds potential for further studies of interaction with recently developed artificial fluorescent odorants.

High-pressure synthesis, amorphization, and decomposition of silane.

PubMed

Hanfland, Michael; Proctor, John E; Guillaume, Christophe L; Degtyareva, Olga; Gregoryanz, Eugene

2011-03-04

By compressing elemental silicon and hydrogen in a diamond anvil cell, we have synthesized polymeric silicon tetrahydride (SiH(4)) at 124 GPa and 300 K. In situ synchrotron x-ray diffraction reveals that the compound forms the insulating I4(1)/a structure previously proposed from ab initio calculations for the high-pressure phase of silane. From a series of high-pressure experiments at room and low temperature on silane itself, we find that its tetrahedral molecules break up, while silane undergoes pressure-induced amorphization at pressures above 60 GPa, recrystallizing at 90 GPa into the polymeric crystal structures.

Chelating capture and magnetic removal of non-magnetic heavy metal substances from soil

PubMed Central

Fan, Liren; Song, Jiqing; Bai, Wenbo; Wang, Shengping; Zeng, Ming; Li, Xiaoming; Zhou, Yang; Li, Haifeng; Lu, Haiwei

2016-01-01

A soil remediation method based on magnetic beneficiation is reported. A new magnetic solid chelator powder, FS@IDA (core-shell Fe3O4@SiO2 nanoparticles coated with iminodiacetic acid chelators), was used as a reactive magnetic carrier to selectively capture non-magnetic heavy metals in soil by chelation and removal by magnetic separation. FS@IDA was prepared via inorganic-organic and organic synthesis reactions that generated chelating groups on the surface of magnetic, multi-core, core-shell Fe3O4@SiO2 (FS) nanoparticles. These reactions used a silane coupling agent and sodium chloroacetate. The results show that FS@IDA could chelate the heavy metal component of Cd, Zn, Pb, Cu and Ni carbonates, lead sulfate and lead chloride in water-insoluble salt systems. The resulting FS@IDA-Cd and FS@IDA-Pb chelates could be magnetically separated, resulting in removal rates of approximately 84.9% and 72.2% for Cd and Pb, respectively. FS@IDA could not remove the residual heavy metals and those bound to organic matter in the soil. FS@IDA did not significantly alter the chemical composition of the soil, and it allowed for fast chelating capture, simple magnetic separation and facilitated heavy metal elution. FS@IDA could also be easily prepared and reprocessed. PMID:26878770

Facile synthesis of functionalized ionic surfactant templated mesoporous silica for incorporation of poorly water-soluble drug.

PubMed

Li, Jing; Xu, Lu; Yang, Baixue; Wang, Hongyu; Bao, Zhihong; Pan, Weisan; Li, Sanming

2015-08-15

The present paper reported amino group functionalized anionic surfactant templated mesoporous silica (Amino-AMS) for loading and release of poorly water-soluble drug indomethacin (IMC) and carboxyl group functionalized cationic surfactant templated mesoporous silica (Carboxyl-CMS) for loading and release of poorly water-soluble drug famotidine (FMT). Herein, Amino-AMS and Carboxyl-CMS were facilely synthesized using co-condensation method through two types of silane coupling agent. Amino-AMS was spherical nanoparticles, and Carboxyl-CMS was well-formed spherical nanosphere with a thin layer presented at the edge. Drug loading capacity was obviously enhanced when using Amino-AMS and Carboxyl-CMS as drug carriers due to the stronger hydrogen bonding force formed between surface modified carrier and drug. Amino-AMS and Carboxyl-CMS had the ability to transform crystalline state of loaded drug from crystalline phase to amorphous phase. Therefore, IMC loaded Amino-AMS presented obviously faster release than IMC because amorphous phase of IMC favored its dissolution. The application of asymmetric membrane capsule delayed FMT release significantly, and Carboxyl-CMS favored sustained release of FMT due to its long mesoporous channels and strong interaction formed between its carboxyl group and amino group of FMT. Copyright © 2015 Elsevier B.V. All rights reserved.

Modification and investigation of silica particles as a foam stabilizer

NASA Astrophysics Data System (ADS)

Zhu, Qian; Zhou, Hua-lei; Song, Ying-xiao; Chang, Zhi-dong; Li, Wen-jun

2017-02-01

As a solid foam stabilizer, spherical silica particles with diameters ranging from 150 to 190 nm were prepared via an improved Stöber method and were subsequently modified using three different silane coupling agents to attain the optimum surface hydrophobicity of the particles. Fourier transform infrared (FTIR) spectra and the measured contact angles were used to characterize the surface properties of the prepared particles. The foam stability was investigated by the foam drainage half-life and the expansion viscoelastic modulus of the liquid film. The results demonstrate that all of the modified silica nanoparticles effectively improve the foam stability. The surface hydrophobicity of the modified particles is found to be a key factor influencing the foam stability. The optimum contact angle of the particles lies in the approximate range from 50° to 55°. The modifier molecular structure used can also influence the stabilizing foam property of the solid particles. The foam system stabilized by (CH3)2SiCl2-modified silica particles exhibits the highest stability; its drainage half-life at maximum increases by 27% compared to that of the blank foam system and is substantially greater than those of the foam systems stabilized by KH570- and KH550-modified particles.

Nacre-mimetic bulk lamellar composites reinforced with high aspect ratio glass flakes.

PubMed

Guner, Selen N Gurbuz; Dericioglu, Arcan F

2016-12-05

Nacre-mimetic epoxy matrix composites reinforced with readily available micron-sized high aspect ratio C-glass flakes were fabricated by a relatively simple, single-step, scalable, time, cost and man-power effective processing strategy: hot-press assisted slip casting (HASC). HASC enables the fabrication of preferentially oriented two-dimensional inorganic reinforcement-polymer matrix bulk lamellar composites with a micro-scale structure resembling the brick-and-mortar architecture of nacre. By applying the micro-scale design guideline found in nacre and optimizing the relative volume fractions of the reinforcement and the matrix as well as by anchoring the brick-and-mortar architecture, and tailoring the interface between reinforcements and the matrix via silane coupling agents, strong, stiff and tough bio-inspired nacre-mimetic bulk composites were fabricated. As a result of high shear stress transfer lengths and effective stress transfer at the interface achieved through surface functionalization of the reinforcements, fabricated bulk composites exhibited enhanced mechanical performance as compared to neat epoxy. Furthermore, governed flake pull-out mode along with a highly torturous crack path, which resulted from extensive deflection and meandering of the advancing crack around well-aligned high aspect ratio C-glass flakes, have led to high work-of-fracture values similar to nacre.

Flame retardant and hydrophobic properties of novel sol-gel derived phytic acid/silica hybrid organic-inorganic coatings for silk fabric

NASA Astrophysics Data System (ADS)

Cheng, Xian-Wei; Liang, Cheng-Xi; Guan, Jin-Ping; Yang, Xu-Hong; Tang, Ren-Cheng

2018-01-01

In this work, a novel phosphorus-rich hybrid organic-inorganic silica coating for improving the flame retardancy of silk fabric was prepared using naturally occurring phytic acid as phosphorus precursor and catalyst for the hydrolysis of tetraethoxysilane. In addition, three silane coupling agents, namely 3-aminopropyldimethoxymethylsilane, 3-chloropropyltrimethoxysilane and 3-methacryloxypropyltrimethoxysilane, were added in the hybrid sol as cross-linkers with the aim of developing hydrophobic coatings and improving the washing durability of the treated silk fabric. The condensation degree of the hybrid sol was characterized by solid-state 29Si nuclear magnetic resonance spectroscopy. The flammability and thermal degradation properties of the treated silk fabrics were determined in terms of limiting oxygen index, vertical burning, pyrolysis combustion flow calorimetry and thermogravimetric analyses. The surface morphology and hydrophobicity of the treated silk fabrics were evaluated by scanning electron microscopy, atomic force microscopy and water contact angle tests. The flammability tests revealed that the silicon sol could endow silk fabric with excellent flame retardancy when doped with phytic acid, and the treated silk fabrics self-extinguished immediately when the ignition source was removed. The silk fabrics treated with the modified hybrid sols exhibited hydrophobic surface and also better durability to washing.

Highly stable precursor solution containing ZnO nanoparticles for the preparation of ZnO thin film transistors.

PubMed

Huang, Heh-Chang; Hsieh, Tsung-Eong

2010-07-23

ZnO particles with an average size of about 5 nm were prepared via a sol-gel chemical route and the silane coupling agent, (3-glycidyloxypropyl)-trimethoxysilane (GPTS), was adopted to enhance the dispersion of the ZnO nanoparticles in ethyl glycol (EG) solution. A ZnO surface potential as high as 66 mV was observed and a sedimentation test showed that the ZnO precursor solution remains transparent for six months of storage, elucidating the success of surface modification on ZnO nanoparticles. The ZnO thin films were then prepared by spin coating the precursor solution on a Si wafer and annealing treatments at temperatures up to 500 degrees C were performed for subsequent preparation of ZnO thin film transistors (TFTs). Microstructure characterization revealed that the coalescence of ZnO nanoparticles occurs at temperatures as low as 200 degrees C to result in a highly uniform, nearly pore-free layer. However, annealing at higher temperatures was required to remove organic residues in the ZnO layer for satisfactory device performance. The 500 degrees C-annealed ZnO TFT sample exhibited the best electrical properties with on/off ratio = 10(5), threshold voltage = 17.1 V and mobility (micro) = 0.104 cm(2) V(-1) s(-1).

Facile method for preparing organic/inorganic hybrid capsules using amino-functional silane coupling agent in aqueous media.

PubMed

Kurayama, Fumio; Suzuki, Satoru; Oyamada, Tetsuro; Furusawa, Takeshi; Sato, Masahide; Suzuki, Noboru

2010-09-01

A new and facile method for preparing microcapsules with 3-aminopropyltriethoxysilane (APTES)/alginate hybrid shell (AP-capsule) is proposed based on gelling and sol-gel processes. In this method, conventional capsules with alginate shells (Alg-capsule) are produced by dripping carboxymethyl cellulose solution containing calcium chloride into a sodium alginate solution. Subsequently, addition of the Alg-capsules to an aqueous APTES solution induces the formation of APTES/alginate hybrid shells. The optical observation shows that the texture of AP-capsules is more glossy and transparent than that of Alg-capsules. The surface morphology and elemental composition of microcapsules were characterized by Scanning Electron Microscopy (SEM), Fourier Transform Infrared Spectroscopy (FT-IR) and X-ray Photoelectron Spectroscopy (XPS). The results suggest that APTES molecules are incorporated to the framework of the alginate shells via electrostatic interaction between amino groups of APTES and carboxyl groups of alginate and the hybrid shells have a dense and homogeneous structure. In the formation reaction, the shrinking of the capsule shells occurs and the accumulation of APTES in the capsule shells proceeds with pseudo first-order kinetics. Moreover, these behaviors are greatly influenced by pH of the reaction solution, especially promoted under acidic and alkaline conditions. Copyright 2010 Elsevier Inc. All rights reserved.

Chelating capture and magnetic removal of non-magnetic heavy metal substances from soil.

PubMed

Fan, Liren; Song, Jiqing; Bai, Wenbo; Wang, Shengping; Zeng, Ming; Li, Xiaoming; Zhou, Yang; Li, Haifeng; Lu, Haiwei

2016-02-16

A soil remediation method based on magnetic beneficiation is reported. A new magnetic solid chelator powder, FS@IDA (core-shell Fe3O4@SiO2 nanoparticles coated with iminodiacetic acid chelators), was used as a reactive magnetic carrier to selectively capture non-magnetic heavy metals in soil by chelation and removal by magnetic separation. FS@IDA was prepared via inorganic-organic and organic synthesis reactions that generated chelating groups on the surface of magnetic, multi-core, core-shell Fe3O4@SiO2 (FS) nanoparticles. These reactions used a silane coupling agent and sodium chloroacetate. The results show that FS@IDA could chelate the heavy metal component of Cd, Zn, Pb, Cu and Ni carbonates, lead sulfate and lead chloride in water-insoluble salt systems. The resulting FS@IDA-Cd and FS@IDA-Pb chelates could be magnetically separated, resulting in removal rates of approximately 84.9% and 72.2% for Cd and Pb, respectively. FS@IDA could not remove the residual heavy metals and those bound to organic matter in the soil. FS@IDA did not significantly alter the chemical composition of the soil, and it allowed for fast chelating capture, simple magnetic separation and facilitated heavy metal elution. FS@IDA could also be easily prepared and reprocessed.

Simple and efficient synthesis of copper(II)-modified uniform magnetic Fe3O4@SiO2 core/shell microspheres for immobilization of cellulase

NASA Astrophysics Data System (ADS)

Li, Shi-Kuo; Hou, Xiao-Cheng; Huang, Fang-Zhi; Li, Chuan-Hao; Kang, Wen-Juan; Xie, An-Jian; Shen, Yu-Hua

2013-11-01

In this paper, we reported a simple and efficient protocol for preparation of Cu2+-modified magnetic Fe3O4@SiO2 core/shell microspheres for immobilization of cellulase. The uniform magnetic Fe3O4@SiO2 core/shell microspheres with a thin shell of 20 nm were synthesized through a solvothermal method followed by a sol-gel process. An amino-terminated silane coupling agent of (3-aminopropyl)triethoxysilane (APTS) was then grafted on them for capturing Cu2+ ions. The reaction process is very simple, efficient, and economical. Noticeably, the content of Cu2+ ions on the magnetic core/shell microspheres can reach 4.6 Wt%, endowing them possess as high immobilization capacity as 225.5 mg/g for cellulase. And the immobilized cellulase can be retained over 90 % on the magnetic microspheres after six cycles. Meanwhile, the magnetic microspheres decorated with Cu2+ ions show a superparamagnetic character with a high magnetic saturation of 58.5 emu/g at room temperature, suggesting conveniently and rapidly recycle the enzyme from solution. This facile, recyclable, high immobilization capacity and activity strategy may find potential applications in enzyme catalytic reactions with low cost.

Chelating capture and magnetic removal of non-magnetic heavy metal substances from soil

NASA Astrophysics Data System (ADS)

Fan, Liren; Song, Jiqing; Bai, Wenbo; Wang, Shengping; Zeng, Ming; Li, Xiaoming; Zhou, Yang; Li, Haifeng; Lu, Haiwei

2016-02-01

A soil remediation method based on magnetic beneficiation is reported. A new magnetic solid chelator powder, FS@IDA (core-shell Fe3O4@SiO2 nanoparticles coated with iminodiacetic acid chelators), was used as a reactive magnetic carrier to selectively capture non-magnetic heavy metals in soil by chelation and removal by magnetic separation. FS@IDA was prepared via inorganic-organic and organic synthesis reactions that generated chelating groups on the surface of magnetic, multi-core, core-shell Fe3O4@SiO2 (FS) nanoparticles. These reactions used a silane coupling agent and sodium chloroacetate. The results show that FS@IDA could chelate the heavy metal component of Cd, Zn, Pb, Cu and Ni carbonates, lead sulfate and lead chloride in water-insoluble salt systems. The resulting FS@IDA-Cd and FS@IDA-Pb chelates could be magnetically separated, resulting in removal rates of approximately 84.9% and 72.2% for Cd and Pb, respectively. FS@IDA could not remove the residual heavy metals and those bound to organic matter in the soil. FS@IDA did not significantly alter the chemical composition of the soil, and it allowed for fast chelating capture, simple magnetic separation and facilitated heavy metal elution. FS@IDA could also be easily prepared and reprocessed.

Enhanced electromagnetic interference shielding properties of carbon fiber veil/Fe3O4 nanoparticles/epoxy multiscale composites

NASA Astrophysics Data System (ADS)

Chen, Wei; Wang, Jun; Zhang, Bin; Wu, Qilei; Su, Xiaogang

2017-12-01

The multiscale approach has been adapted to enhance the electromagnetic interference shielding properties of carbon fiber (CF) veil epoxy-based composites. The Fe3O4 nanoparticles (NPs) were homogeneously dispersed in the epoxy matrix after surface modification by using silane coupling agent. The CF veil/Fe3O4 NPs/epoxy multiscale composites were manufactured by impregnating the CF veils with Fe3O4 NPs/epoxy mixture to prepare prepreg followed by vacuum bagging process. The electromagnetic interference shielding properties combined with the complex permittivity and complex permeability of the composites were investigated in the X-band (8.2-12.4 GHz) range. The total shielding effectiveness (SET) increases with increasing Fe3O4 NPs loadings and the maximum SET is 51.5 dB at low thickness of 1 mm. The incorporation of Fe3O4 NPs into the composites enhances the complex permittivity and complex permeability thus enhancing the electromagnetic wave absorption capability. The increased SET dominated by absorption loss SEA is attributed to the enhanced magnetic loss and dielectric loss generated by Fe3O4 NPs and multilayer construction of the composites. The microwave conductivity increases and the skin depth decreases with increasing Fe3O4 NPs loadings.

Optically active polyurethane@indium tin oxide nanocomposite: Preparation, characterization and study of infrared emissivity

DOE Office of Scientific and Technical Information (OSTI.GOV)

Yang, Yong; Zhou, Yuming, E-mail: ymzhou@seu.edu.cn; Ge, Jianhua

Highlights: ► Silane coupling agent of KH550 was used to connect the ITO and polyurethanes. ► Infrared emissivity values of the hybrids were compared and analyzed. ► Interfacial synergistic action and orderly secondary structure were the key factors. -- Abstract: Optically active polyurethane@indium tin oxide and racemic polyurethane@indium tin oxide nanocomposites (LPU@ITO and RPU@ITO) were prepared by grafting the organics onto the surfaces of modified ITO nanoparticles. LPU@ITO and RPU@ITO composites based on the chiral and racemic tyrosine were characterized by FT-IR, UV–vis spectroscopy, X-ray diffraction (XRD), SEM, TEM, and thermogravimetric analysis (TGA), and the infrared emissivity values (8–14 μm)more » were investigated in addition. The results indicated that the polyurethanes had been successfully grafted onto the surfaces of ITO without destroying the crystalline structure. Both composites possessed the lower infrared emissivity values than the bare ITO nanoparticles, which indicated that the interfacial interaction had great effect on the infrared emissivity. Furthermore, LPU@ITO based on the optically active polyurethane had the virtue of regular secondary structure and more interfacial synergistic actions between organics and inorganics, thus it exhibited lower infrared emissivity value than RPU@ITO based on the racemic polyurethane.« less

Tapered Optical Fiber Probe Assembled with Plasmonic Nanostructures for Surface-Enhanced Raman Scattering Application.

PubMed

Huang, Zhulin; Lei, Xing; Liu, Ye; Wang, Zhiwei; Wang, Xiujuan; Wang, Zhaoming; Mao, Qinghe; Meng, Guowen

2015-08-12

Optical fiber-Raman devices integrated with plasmonic nanostructures have promising potentials for in situ probing remote liquid samples and biological samples. In this system, the fiber probe is required to simultaneously demonstrate stable surface enhanced Raman scattering (SERS) signals and high sensitivity toward the target species. Here we demonstrate a generic approach to integrate presynthesized plasmonic nanostructures with tapered fiber probes that are prepared by a dipping-etching method, through reversed electrostatic attraction between the silane couple agent modified silica fiber probe and the nanostructures. Using this approach, both negatively and positively charged plasmonic nanostructures with various morphologies (such as Au nanosphere, Ag nanocube, Au nanorod, Au@Ag core-shell nanorod) can be stably assembled on the tapered silica fiber probes. Attributed to the electrostatic force between the plasmonic units and the fiber surface, the nanostructures do not disperse in liquid samples easily, making the relative standard deviation of SERS signals as low as 2% in analyte solution. Importantly, the detection sensitivity of the system can be optimized by adjusting the cone angle (from 3.6° to 22°) and the morphology of nanostructures assembled on the fiber. Thus, the nanostructures-sensitized optical fiber-Raman probes show great potentials in the applications of SERS-based environmental detection of liquid samples.

Synthesis of highly monodisperse particles composed of a magnetic core and fluorescent shell.

PubMed

Nagao, Daisuke; Yokoyama, Mikio; Yamauchi, Noriko; Matsumoto, Hideki; Kobayashi, Yoshio; Konno, Mikio

2008-09-02

Highly monodisperse particles composed of a magnetic silica core and fluorescent polymer shell were synthesized with a combined technique of heterocoagulation and soap-free emulsion polymerization. Prior to heterocoagulation, monodisperse, submicrometer-sized silica particles were prepared with the Stober method, and magnetic nanoparticles were prepared with a modified Massart method in which a cationic silane coupling agent of N-trimethoxysilylpropyl- N, N, N-trimethylammonium chloride was added just after coprecipitation of Fe (2+) and Fe (3+). The silica particles with negative surface potential were heterocoagulated with the magnetic nanoparticles with positive surface potential. The magnetic silica particles obtained with the heterocoagulation were treated with sodium silicate to modify their surfaces with silica. In the formation of a fluorescent polymer shell onto the silica-coated magnetic silica cores, an amphoteric initiator of 2,2'-azobis[ N-(2-carboxyethyl)-2-2-methylpropionamidine] (VA-057) was used to control the colloidal stability of the magnetic cores during the polymer coating. The polymerization of St in the presence of a hydrophobic fluorophore of pyrene could coat the cores with fluorescent polymer shells, resulting in monodisperse particles with a magnetic silica core and fluorescent polymer shell. Measurements of zeta potential for the composite particles in different pH values indicated that the composite particles had an amphoteric property originating from VA-057 initiator.

Thermal properties of Bentonite Modified with 3-aminopropyltrimethoxysilane

NASA Astrophysics Data System (ADS)

Pramono, E.; Pratiwi, W.; Wahyuningrum, D.; Radiman, C. L.

2018-03-01

Chemical modifications of Bentonite (BNT) clay have been carried out by using 3-aminoprophyltrimethoxysilane (APS) in various solvent media. The degradation properties of products (BNTAPS) were characterized by thermogravimetric analysis (TGA). Samples were heated at 30 to 700°C with a heating rate 10 deg/min, and the total silane-grafted amount was determined by calculating the weight loss at 200 – 600°C. The thermogram of TGA showed that there were three main decomposition regions which are attributed to the elimination of physically adsorbed water, decomposition of silane and dehydroxylation of Bentonite. High weight loss attributed to the thermal decomposition of silane was observed between 200 to 550°C. Quantitative analysis of grafted silane results high silane loaded using a solvent with high surface energy, which indicates the type of solvent affected interaction and adsorption of APS in BNT platelets.

Palladium nanoparticles deposited on silanized halloysite nanotubes: synthesis, characterization and enhanced catalytic property

NASA Astrophysics Data System (ADS)

Zhang, Yi; He, Xi; Ouyang, Jing; Yang, Huaming

2013-10-01

Palladium (Pd) nanoparticles were deposited on the surface of halloysite nanotubes (HNTs) modified with γ-aminopropyltriethoxysilane (APTES) to produce Pd/NH2-HNTs nanocomposites. The results indicated that Pd nanoparticles were densely immobilized onto NH2-HNTs with an average diameter of ~ 3 nm. The Pd distribution on the surface of silanized HNTs showed much more uniform, and the Pd nanoparticle size became smaller compared with those directly deposited onto HNTs without silanization. Systematic characterization demonstrated that APTES were chemically bonded onto HNTs, and further confirmed the bond formation between Pd and -NH2 groups, which could ensure the firm deposit of Pd nanoparticles on the surface of silanized HNTs. The as-synthesized Pd/NH2-HNTs exhibited an excellent catalytic activity in the liquid-phase hydrogenation of styrene to ethylbenzene with full conversion within 30 min. The mechanism of the deposit of Pd nanoparticles on silanized HNTs was also investigated.

Enhanced corrosion resistance of magnesium alloy by a silane-based solution treatment after an in-situ formation of the Mg(OH)2 layer

NASA Astrophysics Data System (ADS)

Gong, Fubao; Shen, Jun; Gao, Runhua; Xie, Xiong; Luo, Xiong

2016-03-01

A novel organic-inorganic Mg(OH)2/silane surface layer has been developed for corrosion protection of AZ31 magnesium alloy. The results of electrochemical impedance spectroscopy (EIS), the immersion tests, Fourier-transform infrared spectroscopy (FTIR) and sellotape tests showed that the Mg(OH)2/silane-based composite surface layer possessed excellent corrosion resistance and very good adhesion due to the formation of Si-O-Mg bond between Mg(OH)2 layer and silane layer. Electrochemical impedance spectroscopy tests results indicated that for the long-term corrosion protection of AZ31 the increase of the curing temperature improved the impedance of the composited layer when the curing temperature was lower than 130 °С. However, the impedance of the composited layer deceased when the curing temperature was more than 130 °С due to the carbonization of the silane layer.

Durability and mechanical properties of silane cross-linked wood thermoplastic composites

Treesearch

Magnus Bengtsson; Nicole M. Stark; Kristiina Oksman

2007-01-01

In this study, silane cross-linked wood–polyethylene composite profiles were manufactured by reactive extrusion. These composites were evaluated regarding their durability and mechanical properties in comparison with two non-cross-linked wood– polyethylene composites. An addition of only 2% w/w of silane solution during manufacturing was enough to achieve almost 60%...

The effects of different silane crosslinking approaches on composites of polyethylene blends and wood flour

Treesearch

Craig M. Clemons; Ronald C. Sabo; Kolby C. Hirth

2011-01-01

Though silane chemistry has been used to crosslink unfilled polyethylene for many years, such crosslinking has only been recently applied to wood plastic composites to improve properties such as creep resistance. However, the presence of wood significantly changes the silane chemistry and a greater understanding is necessary for optimal processing and performance. We...

Durable hydrophobic coating composition for metallic surfaces and method for the preparation of the composition

DOE Office of Scientific and Technical Information (OSTI.GOV)

Liu, Jiong

A durable hydrophobic coating composition containing fluorinated silanes for metallic surfaces, such as stainless steel surfaces. The composition includes at least one fluorine-containing silane compound, at least one phosphorus-containing silane compound, and at least one hydrolysable compound. This coating is suitable for condenser tubes, among other applications, to promote dropwise condensation.

Assessment of corrosion resistance of Nd-Fe-B magnets by silanization for orthodontic applications

NASA Astrophysics Data System (ADS)

Fabiano, F.; Celegato, F.; Giordano, A.; Borsellino, C.; Bonaccorsi, L.; Calabrese, L.; Tiberto, P.; Cordasco, G.; Matarese, G.; Fabiano, V.; Azzerboni, B.

2014-02-01

Nd-Fe-B permanent magnets are characterised by excellent magnetic properties. However, being extremely vulnerable to the attack of both climate and corrosive environments, their applications are limited. This paper describes how, at different thicknesses of N-propyl-trimetoxy-silane, the coating affects the magnetic force of nickel plated magnets. We also investigate if the corrosion resistance of silanized Nd-Fe-B magnets increases in mildly corrosive environments by immersing them in a synthetic saliva solution. It was found that the silanization treatment does not affect the strength of the magnetic force and provide an enhancement of the corrosion resistance of the substrate.

Functionalisation of Detonation Nanodiamond for Monodispersed, Soluble DNA-Nanodiamond Conjugates Using Mixed Silane Bead-Assisted Sonication Disintegration

DOE PAGES

Edgington, Robert; Spillane, Katelyn M.; Papageorgiou, George; ...

2018-01-15

Here, nanodiamonds have many attractive properties that make them suitable for a range of biological applications, but their practical use has been limited because nanodiamond conjugates tend to aggregate in solution during or after functionalisation. Here we demonstrate the production of DNA-detonation nanodiamond (DNA-DND) conjugates with high dispersion and solubility using an ultrasonic, mixed-silanization chemistry protocol based on the in situ Bead-Assisted Sonication Disintegration (BASD) silanization method. We use two silanes to achieve these properties: (1) 3-(trihydroxysilyl)propyl methylphosphonate (THPMP); a negatively charged silane that imparts high zeta potential and solubility in solution; and (2) (3-aminopropyl)triethoxysilane (APTES); a commonly used functionalmore » silane that contributes an amino group for subsequent bioconjugation. We target these amino groups for covalent conjugation to thiolated, single-stranded DNA oligomers using the heterobifunctional crosslinker sulfosuccinimidyl 4-(N-maleimidomethyl)cyclohexane-1-carboxylate (Sulfo-SMCC). The resulting DNA-DND conjugates are the smallest reported to date, as determined by Dynamic Light Scattering (DLS) and Atomic Force Microscopy (AFM). The functionalisation method we describe is versatile and can be used to produce a wide variety of soluble DND-biomolecule conjugates.« less

Mid-Infrared Interferometry on Spectral Lines. III. Ammonia and Silane around IRC +10216 and VY Canis Majoris

NASA Astrophysics Data System (ADS)

Monnier, J. D.; Danchi, W. C.; Hale, D. S.; Tuthill, P. G.; Townes, C. H.

2000-11-01

Using the University of California Berkeley Infrared Spatial Interferometer with a radio frequency (RF) filter bank, the first interferometric observations of mid-infrared molecular absorption features of ammonia (NH3) and silane (SiH4) with very high spectral resolution (λ/Δλ~105) were made. Under the assumptions of spherical symmetry and uniform outflow, these new data permitted the molecular stratification around carbon star IRC +10216 and red supergiant VY CMa to be investigated. For IRC +10216, both ammonia and silane were found to form in the dusty outflow significantly beyond both the dust formation and gas acceleration zones. Specifically, ammonia was found to form before silane in a region of decaying gas turbulence (>~20R*), while the silane is produced in a region of relatively smooth gas flow much farther from the star (>~80R*). The depletion of gas-phase SiS onto grains soon after dust formation may fuel silane-producing reactions on the grain surfaces. For VY CMa, a combination of interferometric and spectral observations suggest that NH3 is forming near the termination of the gas acceleration phase in a region of high gas turbulence (~40R*).

Functionalisation of Detonation Nanodiamond for Monodispersed, Soluble DNA-Nanodiamond Conjugates Using Mixed Silane Bead-Assisted Sonication Disintegration.

PubMed

Edgington, Robert; Spillane, Katelyn M; Papageorgiou, George; Wray, William; Ishiwata, Hitoshi; Labarca, Mariana; Leal-Ortiz, Sergio; Reid, Gordon; Webb, Martin; Foord, John; Melosh, Nicholas; Schaefer, Andreas T

2018-01-15

Nanodiamonds have many attractive properties that make them suitable for a range of biological applications, but their practical use has been limited because nanodiamond conjugates tend to aggregate in solution during or after functionalisation. Here we demonstrate the production of DNA-detonation nanodiamond (DNA-DND) conjugates with high dispersion and solubility using an ultrasonic, mixed-silanization chemistry protocol based on the in situ Bead-Assisted Sonication Disintegration (BASD) silanization method. We use two silanes to achieve these properties: (1) 3-(trihydroxysilyl)propyl methylphosphonate (THPMP); a negatively charged silane that imparts high zeta potential and solubility in solution; and (2) (3-aminopropyl)triethoxysilane (APTES); a commonly used functional silane that contributes an amino group for subsequent bioconjugation. We target these amino groups for covalent conjugation to thiolated, single-stranded DNA oligomers using the heterobifunctional crosslinker sulfosuccinimidyl 4-(N-maleimidomethyl)cyclohexane-1-carboxylate (Sulfo-SMCC). The resulting DNA-DND conjugates are the smallest reported to date, as determined by Dynamic Light Scattering (DLS) and Atomic Force Microscopy (AFM). The functionalisation method we describe is versatile and can be used to produce a wide variety of soluble DND-biomolecule conjugates.

Simple Heat Treatment of Zirconia Ceramic Pre-Treated with Silane Primer to Improve Resin Bonding.

PubMed

Ha, Jung-Yun; Son, Jun Sik; Kim, Kyo-Han; Kwon, Tae-Yub

2015-01-01

Establishing a strong resin bond to dental zirconia ceramic remains difficult. Previous studies have shown that the conventional application of silane does not work well with zirconia. This paper reports that a silane pre-treatment of dental zirconia ceramic combined with subsequent heat treatment has potential as an adhesive cementation protocol for improving zirconia-resin bonding. Among the various concentrations (0.1 to 16 vol%) of experimental γ-methacryloxypropyltrimethoxysilane (γ-MPTS) primers assessed, the 1% solution was found to be the most effective in terms of the shear bond strength of the resin cement to dental zirconia ceramic. A high shear bond strength (approx. 30 MPa) was obtained when zirconia specimens were pre-treated with this primer and then heat-treated in a furnace for 60 min at 150 degrees C. Heat treatment appeared to remove the hydrophilic constituents from the silane film formed on the zirconia ceramic surface and accelerate the condensation reactions between the silanol groups of the hydrolyzed silane molecules at the zirconia/resin interface, finally making a more desirable surface for bonding with resin. This estimation was supported by Fourier transform infrared spectroscopy of the silanes prepared in this study.

Functionalisation of Detonation Nanodiamond for Monodispersed, Soluble DNA-Nanodiamond Conjugates Using Mixed Silane Bead-Assisted Sonication Disintegration

DOE Office of Scientific and Technical Information (OSTI.GOV)

Edgington, Robert; Spillane, Katelyn M.; Papageorgiou, George

Here, nanodiamonds have many attractive properties that make them suitable for a range of biological applications, but their practical use has been limited because nanodiamond conjugates tend to aggregate in solution during or after functionalisation. Here we demonstrate the production of DNA-detonation nanodiamond (DNA-DND) conjugates with high dispersion and solubility using an ultrasonic, mixed-silanization chemistry protocol based on the in situ Bead-Assisted Sonication Disintegration (BASD) silanization method. We use two silanes to achieve these properties: (1) 3-(trihydroxysilyl)propyl methylphosphonate (THPMP); a negatively charged silane that imparts high zeta potential and solubility in solution; and (2) (3-aminopropyl)triethoxysilane (APTES); a commonly used functionalmore » silane that contributes an amino group for subsequent bioconjugation. We target these amino groups for covalent conjugation to thiolated, single-stranded DNA oligomers using the heterobifunctional crosslinker sulfosuccinimidyl 4-(N-maleimidomethyl)cyclohexane-1-carboxylate (Sulfo-SMCC). The resulting DNA-DND conjugates are the smallest reported to date, as determined by Dynamic Light Scattering (DLS) and Atomic Force Microscopy (AFM). The functionalisation method we describe is versatile and can be used to produce a wide variety of soluble DND-biomolecule conjugates.« less

DOE Office of Scientific and Technical Information (OSTI.GOV)

Bowman, Adam J.; Scherrer, Joseph R.; Reiserer, Ronald S., E-mail: ron.reiserer@vanderbilt.edu

We present a simple apparatus for improved surface modification of polydimethylsiloxane (PDMS) microfluidic devices. A single treatment chamber for plasma activation and chemical/physical vapor deposition steps minimizes the time-dependent degradation of surface activation that is inherent in multi-chamber techniques. Contamination and deposition irregularities are also minimized by conducting plasma activation and treatment phases in the same vacuum environment. An inductively coupled plasma driver allows for interchangeable treatment chambers. Atomic force microscopy confirms that silane deposition on PDMS gives much better surface quality than standard deposition methods, which yield a higher local roughness and pronounced irregularities in the surface.

Silicon-directed rhenium-catalyzed allylic carbaminations and oxidative fragmentations of γ-silyl allylic alcohols.

PubMed

Chavhan, Sanjay W; Cook, Matthew J

2014-04-22

A highly regioselective allylic substitution of β-silyl allylic alcohols has been achieved that provides the branched isomer as a single product. This high level of regiocontrol is achieved through the use of a vinyl silane group that can perform a Hiyama coupling providing 1,3-disubstituted allylic amines. An unusual oxidative fragmentation product was also observed at elevated temperature that appears to proceed by a Fleming-Tamao-type oxidation-elimination pathway. © 2014 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Fluorinated silica microchannel surfaces

DOEpatents

Kirby, Brian J.; Shepodd, Timothy Jon

2005-03-15

A method for surface modification of microchannels and capillaries. The method produces a chemically inert surface having a lowered surface free energy and improved frictional properties by attaching a fluorinated alkane group to the surface. The coating is produced by hydrolysis of a silane agent that is functionalized with either alkoxy or chloro ligands and an uncharged C.sub.3 -C.sub.10 fluorinated alkane chain. It has been found that the extent of surface coverage can be controlled by controlling the contact time from a minimum of about 2 minutes to a maximum of 120 minutes for complete surface coverage.

Monolayer coated aerogels and method of making

DOEpatents

Zemanian, Thomas Samuel [Richland, WA; Fryxell, Glen [Kennwick, WA; Ustyugov, Oleksiy A [Spokane, WA

2006-03-28

Aerogels having a monolayer coating are described. The aerogel and a monolayer forming precursor are provided in a supercritical fluid, whereupon the aerogel and the monolayer forming precursor are reacted in said supercritical fluid to form a covalent bond between the aerogel and the monolayer forming precursor. Suitable aerogels are ceramic oxides such as silica, alumina, aluminosilicate, and combinations thereof. Suitable monolayer forming precursors include alkyl silanes, chlorosilanes, boranes, chloroboranes, germanes, and combinations thereof. The method may also include providing a surface preparation agent such as water, or hydroetching an aerogel to enhance the coating of the monolayer.

Shear bond strength between an indirect composite layering material and feldspathic porcelain-coated zirconia ceramics.

PubMed

Fushiki, Ryosuke; Komine, Futoshi; Blatz, Markus B; Koizuka, Mai; Taguchi, Kohei; Matsumura, Hideo

2012-10-01

This study aims to evaluate the effect of both feldspathic porcelain coating of zirconia frameworks and priming agents on shear bond strength between an indirect composite material and zirconia frameworks. A total of 462 airborne-particle-abraded zirconia disks were divided into three groups: untreated disks (ZR-AB), airborne-particle-abraded zirconia disks coated with feldspathic porcelain, (ZR-PO-AB), and hydrofluoric acid-etched zirconia disks coated with feldspathic porcelain (ZR-PO-HF). Indirect composite (Estenia C&B) was bonded to zirconia specimens with no (CON) or one of four priming agents--Clearfil Photo Bond (CPB), Clearfil Photo Bond with Clearfil Porcelain Bond Activator (CPB + activator), Estenia Opaque primer, or Porcelain Liner M Liquid B (PLB)--with or without an opaque material (Estenia C&B Opaque). All specimens were tested for shear bond strength before and after 20,000 thermocycles. The Steel-Dwass test and Mann-Whitney U test were used to compare shear bond strength. In ZR-AB specimens, the initial bond strength of the CPB and CPB + Activator groups was significantly higher as compared with the other three groups (P < 0.05), whereas the PLB and CPB + Activator groups had the highest pre- and post-thermocycling bond strengths in ZR-PO-AB and ZR-PO-HF specimens. Among CON disks without opaque material, bond strength was significantly lower in ZR-AB specimens than in ZR-PO-AB and ZR-PO-HF specimens (P < 0.05). Feldspathic porcelain coating of a Katana zirconia framework enhanced the bond strength of Estenia C&B indirect composite to zirconia independent of surface treatment. The use of a silane coupling agent and opaque material yields durable bond strength between the indirect composite and feldspathic-porcelain-coated zirconia. The results of the present study suggest that feldspathic porcelain coating of zirconia frameworks is an effective method to obtain clinically acceptable bond strengths of a layering indirect composite material to a zirconia framework.

The ignition delay times of hydrogen/silan/air mixtures at low temperatures

NASA Astrophysics Data System (ADS)

Tropin, D. A.; Bochenkov, E. S.; Fedorov, A. V.

2018-03-01

In the paper the ignition delay times of hydrogen-silane-air mixtures at low pressures from 0.4 atm to 1 atm and mixture temperatures from 300 K to 900 K using the detailed kinetic mechanisms were calculated. It was shown that dependencies of ignition delay time on temperature are non-monotonic. In these dependences a region of "negative temperature coefficient" is presented. The effect of the mixture pressure and the silane concentration in the mixture on the length of this region was revealed. It was shown that the increasing of the silane concentration in the mixture, as well as the increasing the mixture pressure, leads to increasing of the "negative temperature coefficient" region length.

Low cost silicon solar array project: Feasibility of low-cost, high-volume production of silane and pyrolysis of silane to semiconductor-grade silicon

NASA Technical Reports Server (NTRS)

Breneman, W. C.

1978-01-01

Silicon epitaxy analysis of silane produced in the Process Development Unit operating in a completely integrated mode consuming only hydrogen and metallurgical silicon resulted in film resistivities of up to 120 ohms cm N type. Preliminary kinetic studies of dichlorosilane disproportionation in the liquid phase have shown that 11.59% SiH4 is formed at equilibrium after 12 minutes contact time at 56 C. The fluid-bed reactor was operated continuously for 48 hours with a mixture of one percent silane in helium as the fluidizing gas. A high silane pyrolysis efficiency was obtained without the generation of excessive fines. Gas flow conditions near the base of the reactor were unfavorable for maintaining a bubbling bed with good heat transfer characteristics. Consequently, a porous agglomerate formed in the lower portion of the reactor. Dense coherent plating was obtained on the silicon seed particles which had remained fluidizied throughout the experiment.

Thermal reactor. [liquid silicon production from silane gas

NASA Technical Reports Server (NTRS)

Levin, H.; Ford, L. B. (Inventor)

1982-01-01

A thermal reactor apparatus and method of pyrolyticaly decomposing silane gas into liquid silicon product and hydrogen by-product gas is disclosed. The thermal reactor has a reaction chamber which is heated well above the decomposition temperature of silane. An injector probe introduces the silane gas tangentially into the reaction chamber to form a first, outer, forwardly moving vortex containing the liquid silicon product and a second, inner, rewardly moving vortex containing the by-product hydrogen gas. The liquid silicon in the first outer vortex deposits onto the interior walls of the reaction chamber to form an equilibrium skull layer which flows to the forward or bottom end of the reaction chamber where it is removed. The by-product hydrogen gas in the second inner vortex is removed from the top or rear of the reaction chamber by a vortex finder. The injector probe which introduces the silane gas into the reaction chamber is continually cooled by a cooling jacket.

Palladium nanoparticles deposited on silanized halloysite nanotubes: synthesis, characterization and enhanced catalytic property

PubMed Central

Zhang, Yi; He, Xi; Ouyang, Jing; Yang, Huaming

2013-01-01

Palladium (Pd) nanoparticles were deposited on the surface of halloysite nanotubes (HNTs) modified with γ-aminopropyltriethoxysilane (APTES) to produce Pd/NH2-HNTs nanocomposites. The results indicated that Pd nanoparticles were densely immobilized onto NH2-HNTs with an average diameter of ~ 3 nm. The Pd distribution on the surface of silanized HNTs showed much more uniform, and the Pd nanoparticle size became smaller compared with those directly deposited onto HNTs without silanization. Systematic characterization demonstrated that APTES were chemically bonded onto HNTs, and further confirmed the bond formation between Pd and -NH2 groups, which could ensure the firm deposit of Pd nanoparticles on the surface of silanized HNTs. The as-synthesized Pd/NH2-HNTs exhibited an excellent catalytic activity in the liquid-phase hydrogenation of styrene to ethylbenzene with full conversion within 30 min. The mechanism of the deposit of Pd nanoparticles on silanized HNTs was also investigated. PMID:24126604

Bond strength of self-adhesive resin cements to composite submitted to different surface pretreatments.

PubMed

Dos Santos, Victor Hugo; Griza, Sandro; de Moraes, Rafael Ratto; Faria-E-Silva, André Luis

2014-02-01

Extensively destroyed teeth are commonly restored with composite resin before cavity preparation for indirect restorations. The longevity of the restoration can be related to the proper bonding of the resin cement to the composite. This study aimed to evaluate the microshear bond strength of two self-adhesive resin cements to composite resin. COMPOSITE DISCS WERE SUBJECT TO ONE OF SIX DIFFERENT SURFACE PRETREATMENTS: none (control), 35% phosphoric acid etching for 30 seconds (PA), application of silane (silane), PA + silane, PA + adhesive, or PA + silane + adhesive (n = 6). A silicone mold containing a cylindrical orifice (1 mm(2) diameter) was placed over the composite resin. RelyX Unicem (3M ESPE) or BisCem (Bisco Inc.) self-adhesive resin cement was inserted into the orifices and light-cured. Self-adhesive cement cylinders were submitted to shear loading. Data were analyzed by two-way ANOVA and Tukey's test (p < 0.05). Independent of the cement used, the PA + Silane + Adhesive group showed higher microshear bond strength than those of the PA and PA + Silane groups. There was no difference among the other treatments. Unicem presented higher bond strength than BisCem for all experimental conditions. Pretreatments of the composite resin surface might have an effect on the bond strength of self-adhesive resin cements to this substrate.

Synthesis of waterborne polyurethane containing alkoxysilane side groups and the properties of the hybrid coating films

NASA Astrophysics Data System (ADS)

Li, Qi; Guo, Longhai; Qiu, Teng; Xiao, Weidong; Du, Dianxing; Li, Xiaoyu

2016-07-01

A series of waterborne polyurethane (WPU) containing alkoxysilane side groups were synthesized by using the dihydroxy functionalized alkoxysilane. The diol with trimethoxysilane groups at the side chains was synthesized via Michael addition between 3-(methacryloxypropyl)trimethoxysilane (MAPTS) and diethanolamine (DEA). The silane diol was applied as the chain extender for the NCO-endcapped prepolymer of isophorone diisocyanate, polycarbonate diol, 2,2-bis(hydroxymethyl) butyric acid and 1,4-butanediol. The products with the silane content varied from 1.2 to 16.5 wt% were dispersed in water after neutralization. The effect of the silane diol on the particle size and morphology of the WPU dispersion was studied by dynamic light scattering (DLS) and transmission electron microscopy (TEM), respectively. X-ray photoelectron spectroscopy (XPS) characterization was carried out on the coating film of the WPU, revealing that the long flexible side chain is favorable for the silane components to emigrate toward the film surface and crosslink during the film formation process. As a result, both the surface contact angle to water and water adsorption of the WPU coating films increased with the silane content. Furthermore, the mechanical properties including the modulus and tensile strength of the films were also improved by the incorporation of silane diol.

Resistivity behavior of hydrogen and liquid silane at high shock compression

NASA Astrophysics Data System (ADS)

Wang, Yi-Gao; Liu, Fu-Sheng; Liu, Qi-Jun

2018-07-01

To study the electrical properties of hydrogen rich compounds under extreme conditions, the electrical resistivity of density hydrogen and silane fluid was measured, respectively. The hydrogen sample was prepared by compressing pure hydrogen gas to 10 MPa in a coolant target system at the temperature of 77 K. The silane sample can be obtained with the same method. High-pressure and high-temperature experiments were performed using a two-stage light-gas gun. The electrical resistivity of the sample decreased with increasing pressure and temperature as expected. A minimum electrical resistivity value of 0.3 × 10-3 Ω cm at 138 GPa and 4100 K was obtained for silane. The minimum resistivity of hydrogen in the state of 102 GPa and 4300 K was 0.35 Ω cm. It showed that the measured electrical resistivity of the shock-compressed hydrogen was an order of magnitude higher than fluid silane at 50-90 GPa. However, beyond 100 GPa, the resistivity difference between silane and hydrogen was very minor. The carriers in the sample were hydrogen, and the concentration of hydrogen atoms in these two substances was close to each other. These results supported the theoretical prediction that silane was interpreted simply in terms of chemical decomposition into silicon nanoparticles and fluid hydrogen, and electrical conduction flows predominately dominated by the fluid hydrogen. In addition, the results also supported the theory of "chemical precompression", the existence of Sisbnd H bond helped to reduce the pressure of hydrogen metallization. These findings could lead the way for further metallic phases of hydrogen-rich materials and experimental studies.

Analysis of gas membrane ultra-high purification of small quantities of mono-isotopic silane

DOE PAGES

de Almeida, Valmor F.; Hart, Kevin J.

2017-01-03

A small quantity of high-value, crude, mono-isotopic silane is a prospective gas for a small-scale, high-recovery, ultra-high membrane purification process. This is an unusual application of gas membrane separation for which we provide a comprehensive analysis of a simple purification model. The goal is to develop direct analytic expressions for estimating the feasibility and efficiency of the method, and guide process design; this is only possible for binary mixtures of silane in the dilute limit which is a somewhat realistic case. In addition, analytic solutions are invaluable to verify numerical solutions obtained from computer-aided methods. Hence, in this paper wemore » provide new analytic solutions for the purification loops proposed. Among the common impurities in crude silane, methane poses a special membrane separation challenge since it is chemically similar to silane. Other potential problematic compounds are: ethylene, diborane and ethane (in this order). Nevertheless, we demonstrate, theoretically, that a carefully designed membrane system may be able to purify mono-isotopic, crude silane to electronics-grade level in a reasonable amount of time and expenses. We advocate a combination of membrane materials that preferentially reject heavy impurities based on mobility selectivity, and light impurities based on solubility selectivity. We provide estimates for the purification of significant contaminants of interest. In this study, we suggest cellulose acetate and polydimethylsiloxane as examples of membrane materials on the basis of limited permeability data found in the open literature. We provide estimates on the membrane area needed and priming volume of the cell enclosure for fabrication purposes when using the suggested membrane materials. These estimates are largely theoretical in view of the absence of reliable experimental data for the permeability of silane. And finally, future extension of this work to the non-dilute limit may apply to the recovery of silane from rejected streams of natural silicon semi-conductor processes.« less

Analysis of gas membrane ultra-high purification of small quantities of mono-isotopic silane

DOE Office of Scientific and Technical Information (OSTI.GOV)

de Almeida, Valmor F.; Hart, Kevin J.

A small quantity of high-value, crude, mono-isotopic silane is a prospective gas for a small-scale, high-recovery, ultra-high membrane purification process. This is an unusual application of gas membrane separation for which we provide a comprehensive analysis of a simple purification model. The goal is to develop direct analytic expressions for estimating the feasibility and efficiency of the method, and guide process design; this is only possible for binary mixtures of silane in the dilute limit which is a somewhat realistic case. In addition, analytic solutions are invaluable to verify numerical solutions obtained from computer-aided methods. Hence, in this paper wemore » provide new analytic solutions for the purification loops proposed. Among the common impurities in crude silane, methane poses a special membrane separation challenge since it is chemically similar to silane. Other potential problematic compounds are: ethylene, diborane and ethane (in this order). Nevertheless, we demonstrate, theoretically, that a carefully designed membrane system may be able to purify mono-isotopic, crude silane to electronics-grade level in a reasonable amount of time and expenses. We advocate a combination of membrane materials that preferentially reject heavy impurities based on mobility selectivity, and light impurities based on solubility selectivity. We provide estimates for the purification of significant contaminants of interest. In this study, we suggest cellulose acetate and polydimethylsiloxane as examples of membrane materials on the basis of limited permeability data found in the open literature. We provide estimates on the membrane area needed and priming volume of the cell enclosure for fabrication purposes when using the suggested membrane materials. These estimates are largely theoretical in view of the absence of reliable experimental data for the permeability of silane. And finally, future extension of this work to the non-dilute limit may apply to the recovery of silane from rejected streams of natural silicon semi-conductor processes.« less

Analysis of Gas Membrane Ultra-High Purification of Small Quantities of Mono-Isotopic Silane

DOE Office of Scientific and Technical Information (OSTI.GOV)

de Almeida, Valmor F.; Hart, Kevin J.

A small quantity of high-value, crude, mono-isotopic silane is a prospective gas for a small-scale, high-recovery, ultra-high membrane purification process. This is an unusual application of gas membrane separation for which we provide a comprehensive analysis of a simple purification model. The goal is to develop direct analytic expressions for estimating the feasibility and efficiency of the method, and guide process design; this is only possible for binary mixtures of silane in the dilute limit which is a somewhat realistic case. Among the common impurities in crude silane, methane poses a special membrane separation challenge since it is chemically similarmore » to silane. Other potential problematic surprises are: ethylene, diborane and ethane (in this order). Nevertheless, we demonstrate, theoretically, that a carefully designed membrane system may be able to purify mono-isotopic, crude silane to electronics-grade level in a reasonable amount of time and expenses. We advocate a combination of membrane materials that preferentially reject heavy impurities based on mobility selectivity, and light impurities based on solubility selectivity. We provide estimates for the purification of significant contaminants of interest. To improve the separation selectivity, it is advantageous to use a permeate chamber under vacuum, however this also requires greater control of in-leakage of impurities in the system. In this study, we suggest cellulose acetate and polydimethylsiloxane as examples of membrane materials on the basis of limited permeability data found in the open literature. We provide estimates on the membrane area needed and priming volume of the cell enclosure for fabrication purposes when using the suggested membrane materials. These estimates are largely theoretical in view of the absence of reliable experimental data for the permeability of silane. Last but not least, future extension of this work to the non-dilute limit may apply to the recovery of silane from rejected streams of natural silicon semi-conductor processes.« less

A simple and effective approach to prepare injectable macroporous calcium phosphate cement for bone repair: Syringe-foaming using a viscous hydrophilic polymeric solution.

PubMed

Zhang, Jingtao; Liu, Weizhen; Gauthier, Olivier; Sourice, Sophie; Pilet, Paul; Rethore, Gildas; Khairoun, Khalid; Bouler, Jean-Michel; Tancret, Franck; Weiss, Pierre

2016-02-01

In this study, we propose a simple and effective strategy to prepare injectable macroporous calcium phosphate cements (CPCs) by syringe-foaming via hydrophilic viscous polymeric solution, such as using silanized-hydroxypropyl methylcellulose (Si-HPMC) as a foaming agent. The Si-HPMC foamed CPCs demonstrate excellent handling properties such as injectability and cohesion. After hardening the foamed CPCs possess hierarchical macropores and their mechanical properties (Young's modulus and compressive strength) are comparable to those of cancellous bone. Moreover, a preliminary in vivo study in the distal femoral sites of rabbits was conducted to evaluate the biofunctionality of this injectable macroporous CPC. The evidence of newly formed bone in the central zone of implantation site indicates the feasibility and effectiveness of this foaming strategy that will have to be optimized by further extensive animal experiments. A major challenge in the design of biomaterial-based injectable bone substitutes is the development of cohesive, macroporous and self-setting calcium phosphate cement (CPC) that enables rapid cell invasion with adequate initial mechanical properties without the use of complex processing and additives. Thus, we propose a simple and effective strategy to prepare injectable macroporous CPCs through syringe-foaming using a hydrophilic viscous polymeric solution (silanized-hydroxypropyl methylcellulose, Si-HPMC) as a foaming agent, that simultaneously meets all the aforementioned aims. Evidence from our in vivo studies shows the existence of newly formed bone within the implantation site, indicating the feasibility and effectiveness of this foaming strategy, which could be used in various CPC systems using other hydrophilic viscous polymeric solutions. Copyright © 2015 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

Surface modification of ZnO quantum dots by organosilanes and oleic acid with enhanced luminescence for potential biological application

NASA Astrophysics Data System (ADS)

Rissi, Nathalia Cristina; Hammer, Peter; Aparecida Chiavacci, Leila

2017-01-01

Luminescent ZnO-QDs is a promising candidate for biological application, especially due to their low toxicity. Nevertheless, colloidal ZnO-QDs prepared by sol-gel route are unstable in water and incompatible with lipophilic systems, hindering their application in biology and medicine. To tackle the problem, this study reports three different strategies for surface modification of ZnO-QDs by: (i) hydrophilic (3-glycidyloxypropyl) trimethoxysilane (GPTMS), (ii) hydrophobic hexadecyltrimethoxysilane (HTMS) and then by (iii) oleic acid (OA) and HTMS bilayer. Capped ZnO-QDs by GPTMS and HTMS were performed by hydrolysis and condensation reactions under basic catalysis, leading to the formation of siloxane layer, involving strong interaction between the silanes with hydroxylated surface of ZnO, thereby creating a covalent bond—ZnO-O-Si. Alternatively, OA and HTMS were employed as hydrophobic agent to form a bilayer barrier surrounding the nanoparticles (NPs). Capped ZnO-QDS were analyzed by techniques including: Fourier transform infrared spectroscopy, x-ray photoelectron spectroscopy, x-ray diffraction and transmission electron microscopy, as well as the monitoring of excitonic peak of ZnO by UV-vis absorption spectroscopy. Photoluminescence measurements confirmed the importance of capping agents. Bare ZnO-QDs powder showed lowest photoluminescence intensity and displacement to yellow region when compared with ZnO-QDs capped, which present a higher photoluminescence in the green region. The above results can be related to changes of the concentration of oxygen vacancies (V o) and also by increased presence of surface defect density. Silane capping represents the best choice for high stability and photoluminescence enhancement of ZnO-QDs.

Synthesis and Characterization of a Novel Reactive Perfluorinated Alkynyl Silane Monomer

DTIC Science & Technology

2010-10-21

8217 For practical purposes, alkoxy- and th loro-silanes arc the most convenient precurwrs to alkynylsilanes because an alkynyl Grignard or lith ium reagent ...of alkoxy silanes has been accomplished by the treatment of Grignard or organa-lithium reagents with eithet" SiC!.. (followed by alcoholysis)," CI_Si...procedure. Grignard reagents nave been rc:poncd to have significantly lowcr re~ctivity than the litbium rcagents, wbicb rapidly decompose at ambient

Polyfibroblast: A Self-Healing and Galvanic Protection Additive

DTIC Science & Technology

2011-06-27

Isocyanatopropyltrimethoxy silane (ITS): This silane forms a covalent bond with both the oxide layer of the underlying steel and the polyurea resin released from the...group that can react with amines in the polyurea to form a covalent bond. The fact that it reacts more slowly than ITS makes it easier to process, but...it may take longer to develop stronger adhesion with the polyurea scar. • Methacryloxypropyltrimethoxy silane (MPTMS): With an exposed vinyl group

Structure and electrochemical behaviour of 4,7-diazaheptyl-trimethoxy-silane and vinyl-trialkoxy-silane adsorbed at silver surface

NASA Astrophysics Data System (ADS)

Łuczak, Teresa; Pankiewicz, Radosław; Łęska, Bogusława; Schroeder, Grzegorz; Bełtowska-Brzezinska, Maria; Brzezinski, Bogumil

2006-12-01

Novel self-assembled monolayers were obtained on silver using 4,7-diazaheptyl-trimethoxy-silane (SiN) and vinyl-trialkoxy-silane (SiVA, where the alkyl group is 3,6,9,12,15,18,21,24,27,30,33,36,39,42,45,48,51,54,57,60-eicozaoxa- hexaheptaconan). It was shown that thus modified metal surface was protected against electrooxidation. A densely packed monolayer remained stable and did not desorb from the Ag electrode on the potential cycling. The structure of SiN and SiVA as well as their complexes with Li + cations were calculated and visualised by the AM1d and PM5 semi-empirical methods.

Chemical modification of TiO2 surfaces with methylsilanes and characterization by infrared absorption spectroscopy

NASA Technical Reports Server (NTRS)

Finklea, H. O.; Vithanage, R.

1982-01-01

Infrared absorption spectra of methylsilanes bonded to a TiO2 powder were obtained. The reacting silanes include Me sub (4-n)SiX sub n (n=1-4; X=Cl, OMe) and hexamethyldisilazane (HMDS). Reactions were performed on hydroxylated-but-anhydrous TiO2 surfaces in the gas phase. IR spectra confirm the presence of a bonded silane layer. Terminal surface OH groups are found to react more readily than bridging OH groups. By-products of the modification adsorp tenaciously to the surface. The various silanes show only small differences in their ability to sequester surface OH groups. Following hydrolysis in moist air, Si-OH groups are observed only for the tetrafunctional silanes.

Mesoporous silicas synthesis and application for lignin peroxidase immobilization by covalent binding method.

PubMed

Hu, Zunfang; Xu, Longqian; Wen, Xianghua

2013-01-01

Immobilization of enzymes on mesoporous silicas (MS) allows for good reusability. MS with two-dimensional hexagonal pores in diameter up to 14.13 nm were synthesized using Pluronic P123 as template and 1,3,5-triisopropylbenzene as a swelling agent in acetate buffer. The surface of MS was modified by the silanization reagents 3-aminopropyltriethoxysilane. Lignin peroxidase (LiP) was successfully immobilized on the modified MS through covalent binding method by four agents: glutaraldehyde, 1,4-phenylene diisothiocyanate, cyanotic chloride and water-soluble carbodiimide. Results showed that cyanotic chloride provided the best performance for LIP immobilization. The loaded protein concentration was 12.15 mg/g and the immobilized LiP activity was 812.9 U/L. Immobilized LiP had better pH stability. Acid Orange II was used to examine the reusability of immobilized LiP, showing more than 50% of the dye was decolorized at the fifth cycle.

The influence of different cementation modes on the fracture resistance of feldspathic ceramic crowns.

PubMed

Groten, M; Pröbster, L

1997-01-01

One hundred twenty pressed feldspathic ceramic crowns were luted to 20 steel dies using six different cementation modes. Fracture resistance was tested under an angle of 45 degrees and was determined as the maximal fracture load. Crowns were tested with luting agent only (groups A and C) and after etching with hydrofluoric acid, silanating, and the application of a bonding agent (groups B, D, E, and F). The resulting means were: phosphate cement 294.3 (A) and 282.2 (B); glass-ionomer cement 217.2 (C) and 255.4 (D); resin composite 382.2 (E) and 687.6 (F). Statistical analysis revealed significantly greater fracture resistance (P < .01) of resin luted crowns. Bonding to the die almost doubled the fracture resistance. Conditioning of the inner surfaces of the crowns did not improve the fracture resistance of crowns luted using zinc phosphate or glass-ionomer cements.

Poly(silyl silane) homo and copolymers

DOEpatents

Zeigler, J.K.

1991-08-13

Poly(silyl silanes) have been prepared. They have high photosensitivity and excellent resistance to oxygen-reactive ion etching processes. They are useful as photodepolymerizable photoresists, barrier layers, etc.

Poly(silyl silane)homo and copolymers

DOEpatents

Zeigler, J.M.

1989-04-11

Poly(silyl silanes) have been prepared. They have high photosensitivity and show excellent resistance to oxygen-reactive ion etching processes. They are useful as photodepolymerizable photoresists, barrier layers, etc.

An improved method for constructing and selectively silanizing double-barreled, neutral liquid-carrier, ion-selective microelectrodes

PubMed Central

Deveau, Jason S.T.; Grodzinski, Bernard

2005-01-01

We describe an improved, efficient and reliable method for the vapour-phase silanization of multi-barreled, ion-selective microelectrodes of which the silanized barrel(s) are to be filled with neutral liquid ion-exchanger (LIX). The technique employs a metal manifold to exclusively and simultaneously deliver dimethyldichlorosilane to only the ion-selective barrels of several multi-barreled microelectrodes. Compared to previously published methods the technique requires fewer procedural steps, less handling of individual microelectrodes, improved reproducibility of silanization of the selected microelectrode barrels and employs standard borosilicate tubing rather than the less-conventional theta-type glass. The electrodes remain stable for up to 3 weeks after the silanization procedure. The efficacy of a double-barreled electrode containing a proton ionophore in the ion-selective barrel is demonstrated in situ in the leaf apoplasm of pea (Pisum) and sunflower (Helianthus). Individual leaves were penetrated to depth of ~150 μm through the abaxial surface. Microelectrode readings remained stable after multiple impalements without the need for a stabilizing PVC matrix. PMID:16136222

Coating extracellular matrix proteins on a (3-aminopropyl)triethoxysilane-treated glass substrate for improved cell culture.

PubMed

Masuda, Hiro-taka; Ishihara, Seiichiro; Harada, Ichiro; Mizutani, Takeomi; Ishikawa, Masayori; Kawabata, Kazushige; Haga, Hisashi

2014-01-01

We demonstrate that a (3-aminopropyl)triethoxysilane-treated glass surface is superior to an untreated glass surface for coating with extracellular matrix (ECM) proteins when used as a cell culture substrate to observe cell physiology and behavior. We found that MDCK cells cultured on untreated glass coated with ECM removed the coated ECM protein and secreted different ECM proteins. In contrast, the cells did not remove the coated ECM protein when seeded on (3-aminopropyl)triethoxysilane-treated (i.e., silanized) glass coated with ECM. Furthermore, the morphology and motility of cells grown on silanized glass differed from those grown on non-treated glass, even when both types of glass were initially coated with laminin. We also found that cells on silanized glass coated with laminin had higher motility than those on silanized glass coated with fibronectin. Based on our results, we suggest that silanized glass is a more suitable cell culture substrate than conventional non-treated glass when coated by ECM for observations of ECM effects on cell physiology.

Simulated molecular-scale interaction of supercritical fluid mobile and stationary phases.

PubMed

Siders, Paul D

2017-12-08

In supercritical fluid chromatography, molecules from the mobile phase adsorb on the stationary phase. Stationary-phase alkylsilane-terminated silica surfaces might adsorb molecules at the silica, among the silanes, on a silane layer, or in pore space between surfaces. Mobile phases of carbon dioxide, pure and modified with methanol, and stationary phases were simulated at the molecular scale. Classical atomistic force fields were used in Gibbs-ensemble hybrid Monte Carlo calculations. Excess adsorption of pure carbon dioxide mobile phase peaked at fluid densities of 0.002-0.003Å -3 . Mobile phase adsorption from 7% methanol in carbon dioxide peaked at lower fluid density. Methanol was preferentially adsorbed from the mixed fluid. Surface silanes prevented direct interaction of fluid-phase molecules with silica. Some adsorbed molecules mixed with tails of bonded silanes; some formed layers above the silanes. Much adsorption occurred by filling the space between surfaces in the stationary-phase model. The distribution in the stationary phase of methanol molecules from a modified fluid phase varied with pressure. Copyright © 2017 Elsevier B.V. All rights reserved.

Method of high purity silane preparation

DOEpatents

Tsuo, Y. Simon; Belov, Eugene P.; Gerlivanov, Vadim G.; Zadde, Vitali V.; Kleschevnikova, Solomonida I.; Korneev, Nikolai N.; Lebedev, Eugene N.; Pinov, Akhsarbek B.; Ryabenko, Eugene A.; Strebkov, Dmitry S.; Chernyshev, Eugene A.

2000-01-01

A process for the preparation of high purity silane, suitable for forming thin layer silicon structures in various semiconductor devices and high purity poly- and single crystal silicon for a variety of applications, is provided. Synthesis of high-purity silane starts with a temperature assisted reaction of metallurgical silicon with alcohol in the presence of a catalyst. Alcoxysilanes formed in the silicon-alcohol reaction are separated from other products and purified. Simultaneous reduction and oxidation of alcoxysilanes produces gaseous silane and liquid secondary products, including, active part of a catalyst, tetra-alcoxysilanes, and impurity compounds having silicon-hydrogen bonds. Silane is purified by an impurity adsorption technique. Unreacted alcohol is extracted and returned to the reaction with silicon. Concentrated mixture of alcoxysilanes undergoes simultaneous oxidation and reduction in the presence of a catalyst at the temperature -20.degree. C. to +40.degree. C. during 1 to 50 hours. Tetra-alcoxysilane extracted from liquid products of simultaneous oxidation and reduction reaction is directed to a complete hydrolysis. Complete hydrolysis of tetra-alcoxysilane results in formation of industrial silica sol and alcohol. Alcohol is dehydrated by tetra-alcoxysilane and returned to the reaction with silicon.

Effect of surface modification on protein retention and cell proliferation under strain.

PubMed

Dunkers, J P; Lee, H-J; Matos, M A; Pakstis, L M; Taboas, J M; Hudson, S D; Cicerone, M T

2011-07-01

When culturing cells on flexible surfaces, it is important to consider extracellular matrix treatments that will remain on the surface under mechanical strain. Here we investigate differences in laminin deposited on oxidized polydimethylsiloxane (PDMS) with plasma treatment (plasma-only) vs. plasma and aminopropyltrimethoxysilane treatment (silane-linked). We use specular X-ray reflectivity (SXR), transmission electron microscopy (TEM), and immunofluorescence to probe the quantity and uniformity of laminin. The surface coverage of laminin is approximately 45% for the plasma-only and 50% for the silane-linked treatment as determined by SXR. TEM and immunofluorescence reveal additional islands of laminin aggregates on the plasma-only PDMS compared with the relatively smooth and uniform silane-linked laminin surface. We also examine laminin retention under strain and vascular smooth muscle cell viability and proliferation under static and strain conditions. Equibiaxial stretching of the PDMS surfaces shows greatly improved retention of the silane-linked laminin over plasma-only. There are significantly more cells on the silane-linked surface after 4 days of equibiaxial strain. Published by Elsevier Ltd.

Chip PCR. I. Surface passivation of microfabricated silicon-glass chips for PCR.

PubMed Central

Shoffner, M A; Cheng, J; Hvichia, G E; Kricka, L J; Wilding, P

1996-01-01

The microreaction volumes of PCR chips (a microfabricated silicon chip bonded to a piece of flat glass to form a PCR reaction chamber) create a relatively high surface to volume ratio that increases the significance of the surface chemistry in the polymerase chain reaction (PCR). We investigated several surface passivations in an attempt to identify 'PCR friendly' surfaces and used those surfaces to obtain amplifications comparable with those obtained in conventional PCR amplification systems using polyethylene tubes. Surface passivations by a silanization procedure followed by a coating of a selected protein or polynucleotide and the deposition of a nitride or oxide layer onto the silicon surface were investigated. Native silicon was found to be an inhibitor of PCR and amplification in an untreated PCR chip (i.e. native slicon) had a high failure rate. A silicon nitride (Si(3)N(4) reaction surface also resulted in consistent inhibition of PCR. Passivating the PCR chip using a silanizing agent followed by a polymer treatment resulted in good amplification. However, amplification yields were inconsistent and were not always comparable with PCR in a conventional tube. An oxidized silicon (SiO(2) surface gave consistent amplifications comparable with reactions performed in a conventional PCR tube. PMID:8628665

Investigation of Test Methods, Material Properties, and Processes for Solar Cell Encapsulants

NASA Technical Reports Server (NTRS)

1979-01-01

During this quarter the technical activities were directed toward the reformulation of ethylene/vinyl acetate copolymer for use as a compound in solar cell module fabrication. Successful formulations were devised that lowered the temperature required for cure and raised the gel content. A major volatile component was also eliminated (acrylate crosslinking agent) which should aid in the production of bubble free laminates. Adhesive strengths and primers for the bonding of ethylene/vinyl acetate to supersyrate and substrate materials was assessed with encouraging results. The incorporation of silane compounds gave high bond strengths. A survey of scrim materials was also conducted.

Kinetics of (3-aminopropyl)triethoxylsilane (APTES) silanization of superparamagnetic iron oxide nanoparticles.

PubMed

Liu, Yue; Li, Yueming; Li, Xue-Mei; He, Tao

2013-12-10

Silanization of magnetic ironoxide nanoparticles with (3-aminopropyl)triethoxylsilane (APTES) is reported. The kinetics of silanization toward saturation was investigated using different solvents including water, water/ethanol (1/1), and toluene/methanol (1/1) at different reaction temperature with different APTES loading. The nanoparticles were characterized by Fourier transform infrared spectroscopy, vibrating sample magnetometry, transmission electron microscopy, and thermal gravimetric analysis (TGA). Grafting density data based on TGA were used for the kinetic modeling. It is shown that initial silanization takes place very fast but the progress toward saturation is very slow, and the mechanism may involve adsorption, chemical sorption, and chemical diffusion processes. The highest equilibrium grafting density of 301 mg/g was yielded when using toluene/methanol mixture as the solvent at a reaction temperature of 70 °C.

KISS: Kinetics and Structure of Superagglomerates Produced by Silane and Acetylene

NASA Technical Reports Server (NTRS)

Mulholland, G. W.; Yang, J. C.; Scott, J. H.; Sivithanu, Y.

2001-01-01

The objective of this study is to understand the process of gas phase agglomeration leading to superagglomerates and a gel-like structure for microgravity (0-g) silane and acetylene flames. Ultimately one would apply this understanding to predicting flame conditions that could lead to the gas phase production of an aero-gel. The approach is to burn acetylene and silane and to analyze the evolution of the soot and silica agglomerates. Acetylene is chosen because it has one of the highest soot volume fractions and there is evidence of super agglomerates being formed in laminar acetylene flames. Silane has the advantage that silica particles are the major combustion product resulting in a particle volume fraction a factor of ten greater than that for a carbonaceous smoke.

Photochemical dimerization and functionalization of alkanes, ethers, primary alcohols and silanes

DOEpatents

Crabtree, Robert H.; Brown, Stephen H.

1988-01-01

The space-time yield and/or the selectivity of the photochemical dimerization of alkanes, ethers, primary alcohols and tertiary silanes with Hg and U.V. light is enhanced by refluxing the substrate in the irradiated reaction zone at a temperature at which the dimer product condenses and remains condensed promptly upon its formation. Cross-dimerization of the alkanes, ethers and silanes with primary alcohols is disclosed, as is the functionalization to aldehydes of the alkanes with carbon monoxide.

Photochemical dimerization and functionalization of alkanes, ethers, primary alcohols and silanes

DOEpatents

Crabtree, R.H.; Brown, S.H.

1988-02-16

The space-time yield and/or the selectivity of the photochemical dimerization of alkanes, ethers, primary alcohols and tertiary silanes with Hg and U.V. light is enhanced by refluxing the substrate in the irradiated reaction zone at a temperature at which the dimer product condenses and remains condensed promptly upon its formation. Cross-dimerization of the alkanes, ethers and silanes with primary alcohols is disclosed, as is the functionalization to aldehydes of the alkanes with carbon monoxide.

High damping properties of magnetic particles doped rubber composites at wide frequency

DOE Office of Scientific and Technical Information (OSTI.GOV)

Tian, Ye, E-mail: schtiany@163.com; College of Material Science and Engineering, North University of China, Taiyuan 030051; Liu, Yaqing, E-mail: lyq@nuc.edu.cn

Highlights: ► A new kind of permanent magnetic rubber was prepared. ► The microstructure and magnetic properties were investigated. ► The mechanical and damping properties were discussed. ► The new material is expected to be an isolator material to a changed frequency. - Abstract: A new kind of rubber composite was prepared by doping SrFe{sub 12}O{sub 19} nanoparticles coated with silane coupling agents (Si-69) into nitrile butadiene rubber (NBR) matrix, which was characterized by the scanning electron microscopy and X-ray spectroscopy. The results showed that the SrFe{sub 12}O{sub 19} nanoparticles were well dispersed in rubber matrix. Furthermore, the mechanical andmore » magnetic properties of the rubber composites were investigated, in which the high tensile strength (15.8 MPa) and high saturation magnetization (22.9 emu/g) were observed. What is more, the high loss factor of the rubber composites was also obtained in a wide frequency range (0–100 Hz) at high loading (80 phr). The result is attributed to that the permanent magnetic field in rubber nanocomposites can absorb shock energy. These results indicate that the new kind of permanent magnetic rubber is expected to be a smart isolator material, in which the isolator will be able to adapt to a changed frequency.« less

A novel approach for UV-patterning with binary polymer brushes.

PubMed

Li, Lifu; Nakaji-Hirabayashi, Tadashi; Kitano, Hiromi; Ohno, Kohji; Saruwatari, Yoshiyuki; Matsuoka, Kazuyoshi

2018-01-01

A mixed self-assembled monolayer (SAM) of an initiator (3-(2-bromo-2-isobutyryloxy)propyl triethoxysilane) for atom transfer radical polymerization (ATRP) and an agent (6-(triethoxysilyl)hexyl 2-(((methylthio)carbonothioyl)thio)-2-phenylacetate) for reversible addition-fragmentation chain transfer (RAFT) polymerization was constructed on the surface of a silicon wafer or glass plate by a silane coupling reaction. When a UV light at 254nm was irradiated at the mixed SAM through a photomask, the surface density of the bromine atom at the end of BPE in the irradiated region was drastically reduced by UV-driven scission of the BrC bond, as observed by X-ray photoelectron spectroscopy. Consequently, the surface-initiated (SI)-ATRP of 2-ethylhexyl methacrylate (EHMA) was used to easily construct the poly(EHMA) (PEHMA) brush domain. Subsequently, SI-RAFT polymerization of a zwitterionic vinyl monomer, carboxymethyl betaine (CMB), was performed. Using the sequential polymerization, the PCMB and PEHMA brush domains on the solid substrate could be very easily patterned. Patterning proteins and cells with the binary polymer brush is expected because the PCMB brush indicated strong suppression of protein adsorption and cell adhesion, and the PEHMA brush had non-polar properties. This technique is very simple and useful for regulating the shape and size of bio-fouling and anti-biofouling domains on solid surfaces. Copyright © 2017 Elsevier B.V. All rights reserved.

Synthesis and adsorption of silica gel modified 3-aminopropyltriethoxysilane (APTS) from corn cobs against Cu(II) in water

NASA Astrophysics Data System (ADS)

Purwanto, Agung; Yusmaniar, Ferdiani, Fatmawati; Damayanti, Rachma

2017-03-01

Silica gel modified APTS was synthesized from silica gel which was obtained from corn cobs via sol-gel process. Silica gel was synthesized from corn cobs and then chemically modified with silane coupling agent which has an amine group (NH2). This process resulting modified silica gel 3-aminopropyltriethoxysilane (APTS). Characterization of silica gel modified APTS by SEM-EDX showed that the size of the particles of silica gel modified APTS was 20µm with mass percentage of individual elements were nitrogen (N) 15.56%, silicon (Si) 50.69% and oxygen (O) 33.75%. In addition, silica gel modified APTS also showed absorption bands of functional groups silanol (Si-OH), siloxane (Si-O-Si), and an aliphatic chain (-CH2-), as well as amine (NH2) from FTIR spectra. Based on the characterization of XRD, silica gel 2θ of 21.094° and 21.32° respectively. It indicated that both material were amorphous. Determination of optimum pH and contact time on adsorption of silica gel 3-aminopropyltriethoxysilane (APTS) against Cu(II). The optimum pH and contact time was measured by using AAS. Optimum pH of adsorption silica gel modified APTS against metal Cu(II) could be obtained at pH 6 while optimum contact time was at 30 minutes, with the process of adsorption metal Cu(II) occured based on the model Freundlich isotherm.

Improving the bioactivity of bioglass/ (PMMA-co-MPMA) organic/inorganic hybrid.

PubMed

Ravarian, R; Wei, H; Dehghani, F

2011-01-01

Binary system of CaO-SiO(2) glasses enables the apatite formation in simulated body fluid (SBF). However, the presence of phosphate content in SiO(2)-CaO-P(2)O(5) glasses leads to the formation of orthophosphate nanocrystalline nuclei, which facilitates the generation of carbonate hydroxyapatite; this compound is more compatible with natural bone. The brittle and less flexible properties of bioactive glasses are the major obstacle for their application as bone implant. The hybridization of essential constituents of bioactive glasses and glass-ceramics with polymers such as PMMA can improve their poor mechanical properties. The aim of this study was to improve the bioactivity of nanocomposites fabricated from poly(methyl metacrylate) (PMMA) and bioglass for bone implant applications. Bioglass compounds with various phosphate contents were used for the preparation of PMMA/bioglass hybrid matrices. Since the lack of adhesion between the two phases impedes the homogenous composite formation, a silane coupling agent such as 3-(trimethoxysilyl)propyl methacrylates (MPMA) was incorporated into the polymer structure. The effect of addition of MPMA on the molecular structure of composite was investigated. Furthermore, the presence of MPMA in the system improved the homogeneity of sample. Increasing phosphate content in the inorganic segment of hybrid up to 10 mol% resulted in the formation of apatite layer on the surface; hence the hybrid was bioactive and suitable candidate for bone tissue engineering.

Advanced buffer materials for indoor air CO2 control in commercial buildings.

PubMed

Rajan, P E; Krishnamurthy, A; Morrison, G; Rezaei, F

2017-11-01

In this study, we evaluated solid sorbents for their ability to passively control indoor CO 2 concentration in buildings or rooms with cyclic occupancy (eg, offices, bedrooms). Silica supported amines were identified as suitable candidates and systematically evaluated in the removal of CO 2 from indoor air by equilibrium and dynamic techniques. In particular, sorbents with various amine loadings were synthesized using tetraethylenepentamine (TEPA), poly(ethyleneimine) (PEI) and a silane coupling agent 3-aminopropyltriethoxysilane (APS). TGA analysis indicates that TEPA impregnated silica not only displays a relatively high adsorption capacity when exposed to ppm level CO 2 concentrations, but also is capable of desorbing the majority of CO 2 by air flow (eg, by concentration gradient). In 10 L flow-through chamber experiments, TEPA-based sorbents reduced outlet CO 2 by up to 5% at 50% RH and up to 93% of CO 2 adsorbed over 8 hours was desorbed within 16 hours. In 8 m 3 flow-through chamber experiments, 18 g of the sorbent powder spread over a 2 m 2 area removed approximately 8% of CO 2 injected. By extrapolating these results to real buildings, we estimate that meaningful reductions in the CO 2 can be achieved, which may help reduce energy requirements for ventilation and/or improve air quality. © 2017 John Wiley & Sons A/S. Published by John Wiley & Sons Ltd.

Effect of addition of plants-derived polyamide 11 elastomer on the mechanical and tribological properties of hemp fiber reinforced polyamide 1010 composites

NASA Astrophysics Data System (ADS)

Mukaida, Jun; Nishitani, Yosuke; Kitano, Takeshi

2015-05-01

For the purpose of developing the new engineering materials such as structural materials and tribomaterials based on all plants-derived materials, the effect of the addition of plant-derived polyamide 11 Elastomer (PA11E) on the mechanical and tribological properties of hemp fiber(HF) reinforced polyamide 1010 (HF/PA1010) composites was investigated. PA1010 and PA11E (except the polyether groups used as soft segment) were made from plant-derived castor oil. Hemp fiber was surface-treated by two types of treatment: alkali treatment by NaOH solution and surface treatment by ureido silane coupling agent. HF/PA1010/PA11E ternary composites were extruded by a twin screw extruder and injection-molded. Their mechanical properties such as tensile, bending, Izod impact and tribological properties by ring-on-plate type sliding wear testing were evaluated. The effect of the addition of PA11E on the mechanical and tribological properties of HF/PA1010 composite differed for each property. Izod impact strength and specific wear rate improved with the addition of PA11E although tensile strength, modulus, and friction coefficient decreased with PA11E. It follows from these results that it may be possible to develop the new engineering materials with sufficient balance between mechanical and tribological properties.

RGD-conjugated silica-coated gold nanorods on the surface of carbon nanotubes for targeted photoacoustic imaging of gastric cancer

NASA Astrophysics Data System (ADS)

Wang, Can; Bao, Chenchen; Liang, Shujing; Fu, Hualin; Wang, Kan; Deng, Min; Liao, Qiande; Cui, Daxiang

2014-05-01

Herein, we reported for the first time that RGD-conjugated silica-coated gold nanorods on the surface of multiwalled carbon nanotubes were successfully used for targeted photoacoustic imaging of in vivo gastric cancer cells. A simple strategy was used to attach covalently silica-coated gold nanorods (sGNRs) onto the surface of multiwalled carbon nanotubes (MWNTs) to fabricate a hybrid nanostructure. The cross-linked reaction occurred through the combination of carboxyl groups on the MWNTs and the amino group on the surface of sGNRs modified with a silane coupling agent. RGD peptides were conjugated with the sGNR/MWNT nanostructure; resultant RGD-conjugated sGNR/MWNT probes were investigated for their influences on viability of MGC803 and GES-1 cells. The nude mice models loaded with gastric cancer cells were prepared, the RGD-conjugated sGNR/MWNT probes were injected into gastric cancer-bearing nude mice models via the tail vein, and the nude mice were observed by an optoacoustic imaging system. Results showed that RGD-conjugated sGNR/MWNT probes showed good water solubility and low cellular toxicity, could target in vivo gastric cancer cells, and obtained strong photoacoustic imaging in the nude model. RGD-conjugated sGNR/MWNT probes will own great potential in applications such as targeted photoacoustic imaging and photothermal therapy in the near future.

Stability and activity of lactate dehydrogenase on biofunctional layers deposited by activated vapor silanization (AVS) and immersion silanization (IS)

NASA Astrophysics Data System (ADS)

Calvo, Jorge Nieto-Márquez; Elices, Manuel; Guinea, Gustavo V.; Pérez-Rigueiro, José; Arroyo-Hernández, María

2017-09-01

The interaction between surfaces and biological elements, in particular, proteins is critical for the performance of biomaterials and biosensors. This interaction can be controlled by modifying the surface in a process known as biofunctionalization. In this work, the enzyme lactate dehydrogenase (LDH) is used to study the stability of the interaction between a functional protein and amine-functionalized surfaces. Two different functionalization procedures were compared: Activated Vapor Silanization (AVS) and Immersion Silanization (IS). Adsorption kinetics is shown to follow the Langmuir model for AVS-functionalized samples, while IS-functionalized samples show a certain instability if immersed in an aqueous medium for several hours. In turn, the enzymatic activity of LDH is preserved for longer times by using glutaraldehyde as crosslinker between the AVS biofunctional surface and the enzyme.

Impacts of Different Functional Groups on the Kinetic Rates of α-Amine Ketoximesilanes Hydrolysis in the Preparation of Room Temperature Vulcanized Silicone Rubber

PubMed Central

Xu, Huihui; Liu, Zihou; Liu, Qingyang; Bei, Yiling; Zhu, Qingzeng

2018-01-01

α-Amine ketoximesilanes are proven to be effective crosslinkers in the preparation of ketone-oxime one-component room temperature vulcanized (RTV) silicone rubber without the use of toxic metal catalyst. This work aimed to investigate the hydrolysis kinetic of α-amine ketoximesilanes, which is vitally important for the preparation of RTV silicone rubber. Five kinds of α-amine ketoximesilanes, namely α-(N,N-diethyl)aminomethyltri(methylethylketoxime)silane (DEMOS), α-(N,N-di-n-butyl)aminomethyltri(methylethylketoxime)silane (DBMOS), α-(N-n-butyl)aminomethyltri(methylethylketoxime)silane (n-BMOS), α-(N-cyclohexyl)aminomethyltri(methylethylketoxime)silane (CMOS) and α-(β-aminomethyl)aminomethyltri(methylethylketoxime)silane (AEMOS), were successfully obtained and confirmed using Fourier transform infrared spectrometer (FT-IR) and hydrogen-1 nuclear magnetic resonance ( 1H NMR). Kinetics of hydrolysis reactions were measured by FT-IR and conductivity. Our results illustrated that the kinetic constant rates ranged from 12.2 × 10−4 s−1 to 7.6 × 10−4 s−1, with the decreasing order of DEMOS > n-BMOS > DBMOS > CMOS > AEMOS at the given temperature and humidity. Better performances of thermal stability could be achieved when using the α-amine ketoximesilanes as crosslinkers in the preparation of RTV silicon rubber than that of RTV silicone rubber with the use of methyltri(methylethylketoxime)silane (MOS) as a crosslinker and organic tin as a catalyst. PMID:29757263

Impacts of Different Functional Groups on the Kinetic Rates of α-Amine Ketoximesilanes Hydrolysis in the Preparation of Room Temperature Vulcanized Silicone Rubber.

PubMed

Xu, Huihui; Liu, Zihou; Liu, Qingyang; Bei, Yiling; Zhu, Qingzeng

2018-05-13

α-Amine ketoximesilanes are proven to be effective crosslinkers in the preparation of ketone-oxime one-component room temperature vulcanized (RTV) silicone rubber without the use of toxic metal catalyst. This work aimed to investigate the hydrolysis kinetic of α-amine ketoximesilanes, which is vitally important for the preparation of RTV silicone rubber. Five kinds of α-amine ketoximesilanes, namely α-(N,N-diethyl)aminomethyltri(methylethylketoxime)silane (DEMOS), α-(N,N-di-n-butyl)aminomethyltri(methylethylketoxime)silane (DBMOS), α-(N-n-butyl)aminomethyltri(methylethylketoxime)silane (n-BMOS), α-(N-cyclohexyl)aminomethyltri(methylethylketoxime)silane (CMOS) and α-(β-aminomethyl)aminomethyltri(methylethylketoxime)silane (AEMOS), were successfully obtained and confirmed using Fourier transform infrared spectrometer (FT-IR) and hydrogen-1 nuclear magnetic resonance ( ¹H NMR). Kinetics of hydrolysis reactions were measured by FT-IR and conductivity. Our results illustrated that the kinetic constant rates ranged from 12.2 × 10 −4 s −1 to 7.6 × 10 −4 s −1 , with the decreasing order of DEMOS > n-BMOS > DBMOS > CMOS > AEMOS at the given temperature and humidity. Better performances of thermal stability could be achieved when using the α-amine ketoximesilanes as crosslinkers in the preparation of RTV silicon rubber than that of RTV silicone rubber with the use of methyltri(methylethylketoxime)silane (MOS) as a crosslinker and organic tin as a catalyst.

Exercising Spatiotemporal Control of Cell Attachment with Optically Transparent Microelectrodes

PubMed Central

Shah, Sunny S.; Lee, Ji Youn; Verkhoturov, Stanislav; Tuleuova, Nazgul; Schweikert, Emile A.; Ramanculov, Erlan; Revzin, Alexander

2013-01-01

This paper describes a novel approach of controlling cell-surface interactions through an electrochemical “switching” of biointerfacial properties of optically transparent microelectrodes. The indium tin oxide (ITO) microelectrodes, fabricated on glass substrates, were modified with poly(ethylene glycol) (PEG) silane to make glass and ITO regions resistant to protein and cell adhesion. Cyclic voltammetry, with potassium ferricyanide serving as a redox reporter molecule, was used to monitor electron transfer across the electrolyte–ITO interface. PEG silane modification of ITO correlated with diminished electron transfer, judged by the disappearance of ferricyanide redox activity. Importantly, application of reductive potential (−1.4 V vs Ag/AgCl reference) corresponded with reappearance of typical ferricyanide redox peaks, thus pointing to desorption of an insulating PEG silane layer. Time-of-flight secondary ion mass spectrometry (ToF-SIMS) characterization of the silanized ITO surfaces after electrical stimulation indicated complete removal of the silane layer. Significantly, electrical stimulation allowed to “switch” chosen electrodes from nonfouling to protein-adhesive while leaving other ITO and glass regions protected by a nonfouling PEG silane layer. The spatial and temporal control of biointerfacial properties afforded by our approach was utilized to micropattern proteins and cells and to construct micropatterned co-cultures. In the future, control of the biointerfacial properties afforded by this novel approach may allow the organization of multiple cell types into precise geometric configurations in order to create better in vitro mimics of cellular complexity of the native tissues. PMID:18512875

An in vitro comparison of shear bond strength of zirconia to enamel using different surface treatments.

PubMed

Zandparsa, Roya; Talua, Nayrouz A; Finkelman, Matthew D; Schaus, Scott E

2014-02-01

The purpose of this in vitro study was to compare the shear bond strength of an airborne-particle abraded zirconia, an acid-etched zirconia (Piranha solution), an Alloy Primer treated zirconia, and a silaned zirconia to enamel, all bonded with a phosphate-methacrylate resin luting agent. Seventy extracted intact human molars were collected, cleaned, and mounted in autopolymerizing acrylic resin, with the experimental surface of the teeth exposed. The specimens were randomly divided into seven groups of zirconia specimens (4 mm diameter, 2 mm thick). Group 1: Airborne-particle abrasion; group 2: Airborne-particle abrasion and Z-PRIME Plus; group 3: Airborne-particle abrasion and alloy primer; group 4: Piranha solution 7:1; group 5: Piranha solution 7:1 and Z-PRIME Plus; group 6: Piranha solution 7:1 and Alloy primer; group 7: CoJet and silane. All specimens were luted with a phosphate-methacrylate resin luting agent (Panavia F2.0) and stored in distilled water for 1 day, then thermocycled (5°C and 55°C) for 500 cycles and tested for shear bond strength (SBS), measured in MPa, with a universal testing machine at a 0.55 mm/min crosshead speed. All specimens were inspected under a scanning electron microscope to determine mode of failure. The mean values and standard deviations of all specimens were calculated for each group. A one-way ANOVA was performed, and multiple pairwise comparisons were then completed with post hoc Tukey test (alpha = 0.05). The airborne-particle abrasion and Z-PRIME Plus group resulted in a significantly higher SBS than the other groups (21.11 ± 6.32 MPa) (p < 0.001). The CoJet and silane group (15.99 ± 8.92 MPa) and airborne-particle abrasion and alloy primer group (11.07 ± 4.34 MPa) showed high shear bond strength but not statistically significant from the airborne-particle abrasion group (14.23 ± 5.68 MPa). Failure mode was predominately mixed in groups 1, 2, 3, and 7 with islands of retained resin on the zirconia and enamel surfaces; however, groups 4, 5, and 6 showed mostly adhesive failures, which left the zirconia surface free of the adhesive materials. No cohesive failures of the substrates (ceramic, resin, or enamel) were observed. Airborne-particle abrasion followed by the application of a zirconia primer produced the highest bond strength to enamel. Therefore, it can be recommended as a promising surface treatment method to achieve a durable bond to densely sintered zirconia ceramics. © 2013 by the American College of Prosthodontists.

Low Cost Solar Array Project. Feasibility of the silane process for producing semiconductor-grade silicon. Final report, October 1975-March 1979

DOE Office of Scientific and Technical Information (OSTI.GOV)

Not Available

1979-06-01

The commercial production of low-cost semiconductor-grade silicon is an essential requirement of the JPL/DOE (Department of Energy) Low-Cost Solar Array (LSA) Project. A 1000-metric-ton-per-year commercial facility using the Union Carbide Silane Process will produce molten silicon for an estimated price of $7.56/kg (1975 dollars, private financing), meeting the DOE goal of less than $10/kg. Conclusions and technology status are reported for both contract phases, which had the following objectives: (1) establish the feasibility of Union Carbide's Silane Process for commercial application, and (2) develop an integrated process design for an Experimental Process System Development Unit (EPSDU) and a commercial facility,more » and estimate the corresponding commercial plant economic performance. To assemble the facility design, the following work was performed: (a) collection of Union Carbide's applicable background technology; (b) design, assembly, and operation of a small integrated silane-producing Process Development Unit (PDU); (c) analysis, testing, and comparison of two high-temperature methods for converting pure silane to silicon metal; and (d) determination of chemical reaction equilibria and kinetics, and vapor-liquid equilibria for chlorosilanes.« less

Spatial Resolution of Small Particles in Silane Discharge.

DTIC Science & Technology

1985-02-18

report our results and attempt to qualitatively describe how these zones relate to plasma chemistry and film deposition processes. Originator supplied...keywords include: Rf discharge, Silane, Plasma chemistry , Particles, Clusters, and Laser light scattering.

Programmatic Summary: Self-Regulating, Self-Pressurizing Tubules for Integrated Circulatory Systems

DTIC Science & Technology

2009-02-01

Conditions: (i) 3- aminopropyl silane; (ii) 2-furoyl chloride, Et3N, CH2Cl2, 0 C to RT, 24 h; (iii) Compound 2, THF, RT, 24 h.; and (iv) Toluene, reflux... aminopropyl )trimethoxy silane. Next, we treated the amino-terminated slides with a solution of 2-furoyl chloride to yield furan functionalized slides...Conditions: (i) 3- aminopropyl silane; (ii) 2-furoyl chloride, Et3N, CH2Cl2, 0 C to RT, 24 h; (iii) Compound 2, THF, RT, 24 h.; and (iv) Toluene, reflux

Development of acceptance criteria for batches of silane primer for external tank thermal protection system bonding applications

NASA Technical Reports Server (NTRS)

Mikes, F.

1985-01-01

Fourier transform infrared spectroscopy is currently the best technique for observing hydrolytic changes in DC 1200 silane the primers caused by moisture in the atmosphere. To further prove that FTIR can be used as a criterion test for acceptance of silane primer lots, intensities of the FTIR OH- band are being compared with primer adhesive bond strength using a mechanical test suggested by NASA. Results of tests for shear strength and Oh-absorption are tabulated and compared with FTIR absorption intensities in the OH-region.

Photochemical dimerization and functionalization of alkanes, ethers, primary and secondary alcohols, phosphine oxides and silanes

DOEpatents

Crabtree, Robert H.; Brown, Stephen H.

1989-01-01

The space-time yield and/or the selectivity of the photochemical dimerization of alkanes, ethers, primary and secondary alcohols, phosphine oxides and primary, secondary and tertiary silanes with Hg and U.V. light is enhanced by refluxing the substrate in the irradiated reaction zone at a temperature at which the dimer product condenses and remains condensed promptly upon its formation. Cross-dimerization of the alkanes, ethers and silanes with primary alcohols is disclosed, as is the functionalization to aldehydes of the alkanes with carbon monoxide.

Photochemical dimerization and functionalization of alkanes, ethers, primary and secondary alcohols, phosphine oxides and silanes

DOEpatents

Crabtree, R.H.; Brown, S.H.

1989-10-17

The space-time yield and/or the selectivity of the photochemical dimerization of alkanes, ethers, primary and secondary alcohols, phosphine oxides and primary, secondary and tertiary silanes with Hg and U.V. light is enhanced by refluxing the substrate in the irradiated reaction zone at a temperature at which the dimer product condenses and remains condensed promptly upon its formation. Cross-dimerization of the alkanes, ethers and silanes with primary alcohols is disclosed, as is the functionalization to aldehydes of the alkanes with carbon monoxide.

Phospholipid Polymer Biointerfaces for Lab-on-a-Chip Devices.

PubMed

Xu, Yan; Takai, Madoka; Ishihara, Kazuhiko

2010-06-01

This review summarizes recent achievements and progress in the development of various functional 2-methacryloyloxyethyl phosphorylcholine (MPC) polymer biointerfaces for lab-on-a-chip devices and applications. As phospholipid polymers, MPC polymers can form cell-membrane-like surfaces by surface chemistry and physics and thereby provide biointerfaces capable of suppressing protein adsorption and many subsequent biological responses. In order to enable application to microfluidic devices, a number of MPC polymers with diverse functions have been specially designed and synthesized by incorporating functional units such as charge and active ester for generating the microfluidic flow and conjugating biomolecules, respectively. Furthermore, these polymers were incorporated with silane or hydrophobic moiety to construct stable interfaces on various substrate materials such as glass, quartz, poly(methyl methacrylate), and poly(dimethylsiloxane), via a silane-coupling reaction or hydrophobic interactions. The basic interfacial properties of these interfaces have been characterized from multiple aspects of chemistry, physics, and biology, and the suppression of nonspecific bioadsorption and control of microfluidic flow have been successfully achieved using these biointerfaces on a chip. Further, many chip-based biomedical applications such as immunoassays and DNA separation have been accomplished by integrating these biointerfaces on a chip. Therefore, functional phospholipid polymer interfaces are promising and useful for application to lab-on-a-chip devices in biomedicine.

Biomarker Sensors and Method for Multi-Color Imaging and Processing of Single-Molecule Life Signatures

NASA Technical Reports Server (NTRS)

Wade, Lawrence A. (Inventor); Collier, Charles Patrick (Inventor)

2013-01-01

The invention is a device including array of active regions for use in reacting one or more species in at least two of the active regions in a sequential process, e.g., sequential reactions. The device has a transparent substrate member, which has a surface region and a silane material overlying the surface region. A first active region overlies a first portion of the silane material. The first region has a first dimension of less than 1 micron in size and has first molecules capable of binding to the first portion of the silane material. A second active region overlies a second portion of the silane material. The second region has a second dimension of less than 1 micron in size, second molecules capable of binding to the second portion of the active region, and a spatial distance separates the first active region and the second active region.

High purity silane and silicon production

NASA Technical Reports Server (NTRS)

Breneman, William C. (Inventor)

1987-01-01

Silicon tetrachloride, hydrogen and metallurgical silicon are reacted at about 400.degree.-600.degree. C. and at pressures in excess of 100 psi, and specifically from about 300 up to about 600 psi to form di- and trichlorosilane that is subjected to disproportionation in the presence of an anion exchange resin to form high purity silane. By-product and unreacted materials are recycled, with metallurgical silicon and hydrogen being essentially the only consumed feed materials. The silane product may be further purified, as by means of activated carbon or cryogenic distillation, and decomposed in a fluid bed or free space reactor to form high purity polycrystalline silicon and by-product hydrogen which can be recycled for further use. The process results in simplified waste disposal operations and enhances the overall conversion of metallurgical grade silicon to silane and high purity silicon for solar cell and semiconductor silicon applications.

Preparation and Characterization of Silanes Films to Protect Electrogalvanized Steel

NASA Astrophysics Data System (ADS)

Seré, Pablo R.; Egli, Walter; Di Sarli, Alejandro R.; Deyá, Cecilia

2018-03-01

Silanes are an interesting alternative to chromate-based surface treatments for temporary protection of electrogalvanized steel. In this work, the protective behavior of 3-mercaptopropyltrimethoxysilane (MTMO), 3-aminopropyltriethoxysilane (AMEO), or 3-glycidoxypropyltrimethoxysilane (GLYMO) films applied on electrogalvanized automotive quality steel sheets has been studied. The silane coating morphology, composition, and porosity were characterized by scanning electron microscopy (SEM), energy-dispersive x-ray spectroscopy (EDS), x-ray fluorescence, immersion in copper sulfate, and cyclic voltammetry. The corrosion protection was evaluated by polarization curves, electrochemical noise measurements, electrochemical impedance spectrometry, and accelerated humidity chamber tests. The results showed that the silanes protect temporarily electrogalvanized steel from corrosion. MTMO forms a relatively thick and cracked film. AMEO and GLYMO films were so thin that they could not be observed by SEM but silicon was detected by EDS. MTMO provided good temporary protection, being an alternative to replace Cr(VI) as protector of electrogalvanized steel.

Chemical treatment of the intra-canal dentin surface: a new approach to modify dentin hydrophobicity

PubMed Central

GAITAN-FONSECA, Cesar; COLLART-DUTILLEUL, Pierre-Yves; SEMETEY, Vincent; ROMIEU, Olivier; CRUZ, Roel; FLORES, Hector; CUISINIER, Frédéric; PÉREZ, Elías; POZOS-GUILLEN, Amaury

2013-01-01

Objective: This study evaluated the hydrophobicity of dentin surfaces that were modified through chemical silanization with octadecyltrichlorosilane (OTS). Material and Methods: An in vitro experimental study was performed using 40 human permanent incisors that were divided into the following two groups: non-silanized and silanized. The specimens were pretreated and chemically modified with OTS. After the chemical modification, the dentin hydrophobicity was examined using a water contact angle measurement (WCA). The effectiveness of the modification of hydrophobicity was verified by the fluid permeability test (FPT). Results and Conclusions: Statistically significant differences were found in the values of WCA and FPT between the two groups. After silanization, the hydrophobic intraradicular dentin surface exhibited in vitro properties that limit fluid penetration into the sealed root canal. This chemical treatment is a new approach for improving the sealing of the root canal system. PMID:23559114

Light-weight ceramic insulation

NASA Technical Reports Server (NTRS)

Hsu, Ming-Ta S. (Inventor); Chen, Timothy S. (Inventor)

2002-01-01

Ultra-high temperature, light-weight, ceramic insulation such as ceramic tile is obtained by pyrolyzing a siloxane gel derived from the reaction of at least one organo dialkoxy silane and at least one tetralkoxy silane in an acid or base liquid medium. The reaction mixture of the tetra- and dialkoxy silanes may contain also an effective amount of a mono- or trialkoxy silane to obtain the siloxane gel. The siloxane gel is dried at ambient pressures to form a siloxane ceramic precursor without significant shrinkage. The siloxane ceramic precursor is subsequently pyrolyzed, in an inert atmosphere, to form the black ceramic insulation comprising atoms of silicon, carbon and oxygen. The ceramic insulation, can be characterized as a porous, uniform ceramic tile resistant to oxidation at temperatures ranging as high as 1700.degree. C. and is particularly useful as lightweight tiles for spacecraft and other high-temperature insulation applications.

Further development of high temperature-resistant graphite fiber coupling agents

NASA Technical Reports Server (NTRS)

Griffin, R. N.

1976-01-01

Potential coupling agents for graphite fibers were screened by their effect on the weight losses of Thornel 300, HMS, and HTS fibers at 588K for 200 and 400 hours. Unidirectional laminates were made from HMS and HTS fibers, untreated, and treated with each of the seven coupling agents. The matrix of all laminates was PMR polyimide (PMR-PR). On the basis of the best overall retention of elevated temperature interlaminar shear strength after 200 hours at 588K, composite weight after 200 hours at 588K, and fiber weight after 400 hours at 588K, ventromer T-1 applied from aqueous solution and pyrolyzed PPQ were selected for further evaluation as coupling agents for HTS fiber while ventromer T-2 and pyrolyzed PPQ were selected as coupling agents for HMS fiber. It was shown that pyrolyzed PPQ as a coupling agent improves the oxidative stability of HTS/PMR-PI composites.

μ3-η(2):η(2):η(2)-Coordination of Primary Silane on a Triruthenium Plane.

PubMed

Nagaoka, Masahiro; Tsuruda, Hiroyuki; Amako, Masa-aki; Suzuki, Hiroharu; Takao, Toshiro

2015-12-01

A μ3-η(2):η(2):η(2)-silane complex, [(Cp*Ru)3(μ3-η(2):η(2):η(2)-H3SitBu)(μ-H)3] (2 a; Cp* = η(5)-C5Me5), was synthesized from the reaction of [{Cp*Ru(μ-H)}3(μ3-H)2] (1) with tBuSiH3. Complex 2 a is the first example of a silane ligand adopting a μ3-η(2):η(2):η(2) coordination mode. This unprecedented coordination mode was established by NMR and IR spectroscopy as well as X-ray diffraction analysis and supported by a density functional study. Variable-temperature NMR analysis implied that 2 a equilibrates with a tautomeric μ3-silyl complex (3 a). Although 3 a was not isolated, the corresponding μ3-silyl complex, [(Cp*Ru)3(μ3-η(2):η(2)-H2SiPh)(H)(μ-H)3] (3 b), was obtained from the reaction of 1 with PhSiH3. Treatment of 2 a with PhSiH3 resulted in a silane exchange reaction, leading to the formation of 3 b accompanied by the elimination of tBuSiH3. This result indicates that the μ3-silane complex can be regarded as an "arrested" intermediate for the oxidative addition/reductive elimination of a primary silane to a trinuclear site. © 2015 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Effect of prior silane application on the bond strength of a universal adhesive to a lithium disilicate ceramic.

PubMed

Moro, André Fábio Vasconcelos; Ramos, Amanda Barreto; Rocha, Gustavo Miranda; Perez, Cesar Dos Reis

2017-11-01

Universal adhesives combine silane and various monomers in a single bottle to make them more versatile. Their adhesive performance is unclear. The purpose of this in vitro study was to assess the effects of an additional silane application before using a universal adhesive on the adhesion between a disilicate glass ceramic and a composite resin by using a microshear bond strength test (μSBS) and fracture analysis immediately and after thermocycling. One hundred lithium disilicate glass ceramic disks were divided into 10 groups for bond strength testing according to the following 3 surface treatments: silane application (built-in universal adhesive or with additional application), adhesive (Adper Single Bond Plus [SB, 3M ESPE], Scotchbond Universal Adhesive [U, 3M ESPE], and mixed U with Dual Cure Activator [DCA, 3M ESPE]); or thermocycling (half of the specimens were thermocycled 10000 times). After surface treatment, 5 resin cylinders were bonded to each disk and submitted to a μSBS test. The failure mode was analyzed under a stereomicroscope and evaluated by scanning electron microscope and energy-dispersive x-ray spectroscopy. Data from the μSBS test were analyzed by 3-way ANOVA followed by the Tukey HSD post hoc test (α=.05). An additional silane application resulted in a higher μSBS result for all adhesive groups (P<.05). Ceramic surface treatment influenced the performance of adhesives, which may be improved with an additional silane application. Copyright © 2017 Editorial Council for the Journal of Prosthetic Dentistry. Published by Elsevier Inc. All rights reserved.

Effect of Surface Treatments on the Bond Strength to Turkom-Cera All-ceramic Material.

PubMed

Razak, Abdul Aa; Abu-Hassan, Mohamed I; Al-Makramani, Bandar Ma; Al-Sanabani, Fuad A; Al-Shami, Ibrahim Z; Almansour, Hosain M

2016-11-01

The aim of this study was to evaluate the effect of surface treatments on shear bond strength (SBS) of Turkom-Cera (Turkom-Ceramic (M) Sdn. Bhd., Puchong, Malaysia) all-ceramic material cemented with resin cement Panavia-F (Kuraray Medical Inc., Okayama, Japan). Forty Turkom-Cera ceramic disks (10 mm × 3 mm) were prepared and randomly divided into four groups. The disks were wet ground to 1000-grit and subjected to four surface treatments: (1) No treatment (Control), (2) sandblasting, (3) silane application, and (4) sandblasting + silane. The four groups of 10 specimens each were bonded with Panavia-F resin cement according to manufacturer's recommendations. The SBS was determined using the universal testing machine (Instron) at 0.5 mm/min crosshead speed. Failure modes were recorded and a qualitative micromorphologic examination of different surface treatments was performed. The data were analyzed using the one-way analysis of variance (ANOVA) and Tukey honestly significant difference (HSD) tests. The SBS of the control, sandblasting, silane, and sandblasting + silane groups were: 10.8 ± 1.5, 16.4 ± 3.4, 16.2 ± 2.5, and 19.1 ± 2.4 MPa respectively. According to the Tukey HSD test, only the mean SBS of the control group was significantly different from the other three groups. There was no significant difference between sandblasting, silane, and sandblasting + silane groups. In this study, the three surface treatments used improved the bond strength of resin cement to Turkom-Cera disks. The surface treatments used in this study appeared to be suitable methods for the cementation of glass infiltrated all-ceramic restorations.

Effects of silica coating and silane surface conditioning on the bond strength of rebonded metal and ceramic brackets.

PubMed

Atsü, Saadet; Çatalbaş, Bülent; Gelgör, İbrahim Erhan

2011-01-01

The aim of this study was to evaluate the effects of tribochemical silica coating and silane surface conditioning on the bond strength of rebonded metal and ceramic brackets. Twenty debonded metal and 20 debonded ceramic brackets were randomly assigned to receive one of the following surface treatments (n=10 for each group): (1) sandblasting (control); (2) tribochemical silica coating combined with silane. Brackets were rebonded to the enamel surface on the labial and lingual sides of premolars with a light-polymerized resin composite. All specimens were stored in distilled water for 1 week and then thermocycled (5,000 cycles) between 5-55ºC. Shear bond strength values were measured using a universal testing machine. Student's t-test was used to compare the data (α=0.05). Failure mode was assessed using a stereomicroscope, and the treated and non-treated bracket surfaces were observed by scanning electron microscopy. Rebonded ceramic brackets treated with silica coating followed by silanization had significantly greater bond strength values (17.7±4.4 MPa) than the sandblasting group (2.4±0.8 MPa, P<0.001). No significant difference was observed between the rebonded metal brackets treated with silica coating with silanization (15±3.9 MPa) and the sandblasted brackets (13.6±3.9 MPa). Treated rebonded ceramic specimens primarily exhibited cohesive failure in resin and adhesive failure at the enamel-adhesive interface. In comparison to sandblasting, silica coating with aluminum trioxide particles followed by silanization resulted in higher bond strengths of rebonded ceramic brackets.

Effect of Surface Treatment, Silane, and Universal Adhesive on Microshear Bond Strength of Nanofilled Composite Repairs.

PubMed

Fornazari, I A; Wille, I; Meda, E M; Brum, R T; Souza, E M

 The aim of this study was to evaluate the effect of surface treatment and universal adhesive on the microshear bond strength of nanoparticle composite repairs.  One hundred and forty-four specimens were built with a nanofilled composite (Filtek Supreme Ultra, 3M ESPE). The surfaces of all the specimens were polished with SiC paper and stored in distilled water at 37°C for 14 days. Half of the specimens were then air abraded with Al 2 O 3 particles and cleaned with phosphoric acid. Polished specimens (P) and polished and air-abraded specimens (A), respectively, were randomly divided into two sets of six groups (n=12) according to the following treatments: hydrophobic adhesive only (PH and AH, respectively), silane and hydrophobic adhesive (PCH, ACH), methacryloyloxydecyl dihydrogen phosphate (MDP)-containing silane and hydrophobic adhesive (PMH, AMH), universal adhesive only (PU, AU), silane and universal adhesive (PCU, ACU), and MDP-containing silane and universal adhesive (PMU, AMU). A cylinder with the same composite resin (1.1-mm diameter) was bonded to the treated surfaces to simulate the repair. After 48 hours, the specimens were subjected to microshear testing in a universal testing machine. The failure area was analyzed under an optical microscope at 50× magnification to identify the failure type, and the data were analyzed by three-way analysis of variance and the Games-Howell test (α=0.05).  The variables "surface treatment" and "adhesive" showed statistically significant differences for p<0.05. The highest mean shear bond strength was found in the ACU group but was not statistically different from the means for the other air-abraded groups except AH. All the polished groups except PU showed statistically significant differences compared with the air-abraded groups. The PU group had the highest mean among the polished groups. Cohesive failure was the most frequent failure mode in the air-abraded specimens, while mixed failure was the most common mode in the polished specimens.  While air abrasion with Al 2 O 3 particles increased the repair bond strength of the nanoparticle composite, the use of MDP-containing silane did not lead to a statistically significant increase in bond strength. Silane-containing universal adhesive on its own was as effective as any combination of silane and adhesive, particularly when applied on air-abraded surfaces.

Evaluation of experimental installation of silane treatment on bridges : final report.

DOT National Transportation Integrated Search

1988-04-01

In this project the effectiveness of silane-based chemicals as concrete sealants was evaluated for selected bridges throughout the state of Louisiana for a five-year period. The field evaluation was initiated after satisfactory results in the laborat...

Silane cross-linkable ethylene-propylene elastomer compositions prepared by reactive processing

NASA Astrophysics Data System (ADS)

Kozawa, Eiji; Nakajima, Yasuo; Kim, Jae Kyung

2015-05-01

Thermoplastic Elastomers (TPEs) have received attention as the alternative materials of EPDM due to an advantage for mass production. In recent years, by the progress of polymerization technology, Ethylene-propylene Elastomer (EP), one of the TPEs, is beginning to be applied to many products because of its good properties as rubber. However, as much as a complete replacement for EPDM, it is not provided with sufficient properties. In such circumstance, we found that EP's performance properties can be further enhanced via chemical modification such as cross-linking. The advent of a newer technique, involving the grafting of organo-functional silane onto the polymer chain in the reaction extrusion process is more attractive due to various industrial advantages. Although the functionalization of the EP by silane grafting through reactive processing is very useful, the silane grafting process of EP has a difficulty. It is most likely a consequence of the nature of the PP chain scission (β-scission), which is the dominant reaction in PP when subjected to free radicals at elevated temperature during processing. Therefore, the objective of our current work is to investigate a reactive extrusion process for the silane cross-linkable EP while minimizing the degradation, as well as evaluate the properties of the modified polymer.

Optimization and characterization of biomolecule immobilization on silicon substrates using (3-aminopropyl)triethoxysilane (APTES) and glutaraldehyde linker

NASA Astrophysics Data System (ADS)

Gunda, Naga Siva Kumar; Singh, Minashree; Norman, Lana; Kaur, Kamaljit; Mitra, Sushanta K.

2014-06-01

In the present work, we developed and optimized a technique to produce a thin, stable silane layer on silicon substrate in a controlled environment using (3-aminopropyl)triethoxysilane (APTES). The effect of APTES concentration and silanization time on the formation of silane layer is studied using spectroscopic ellipsometry and Fourier transform infrared spectroscopy (FTIR). Biomolecules of interest are immobilized on optimized silane layer formed silicon substrates using glutaraldehyde linker. Surface analytical techniques such as ellipsometry, FTIR, contact angle measurement system, and atomic force microscopy are employed to characterize the bio-chemically modified silicon surfaces at each step of the biomolecule immobilization process. It is observed that a uniform, homogenous and highly dense layer of biomolecules are immobilized with optimized silane layer on the silicon substrate. The developed immobilization method is successfully implemented on different silicon substrates (flat and pillar). Also, different types of biomolecules such as anti-human IgG (rabbit monoclonal to human IgG), Listeria monocytogenes, myoglobin and dengue capture antibodies were successfully immobilized. Further, standard sandwich immunoassay (antibody-antigen-antibody) is employed on respective capture antibody coated silicon substrates. Fluorescence microscopy is used to detect the respective FITC tagged detection antibodies bound to the surface after immunoassay.

Effect of tetraethoxysilane coating on the improvement of plasma treated polypropylene adhesion

NASA Astrophysics Data System (ADS)

Pantoja, M.; Encinas, N.; Abenojar, J.; Martínez, M. A.

2013-09-01

Polypropylene is one of the most used polymers due to its lightweight and recyclability properties, among others. However, its poor characteristics regarding surface energy and lack of polar functional groups have to be overcome to perform adhesion processes. The main objective of this work is to improve the adhesion behavior of polypropylene by combining atmospheric pressure plasma surface activation and silane adhesion promoter. Tetraethoxysilane hydrolysis and condensation are followed through infrared spectroscopy by attenuated total reflectance in order to set the coating conditions. Contact angle measurements and surface energy calculations as well as infrared and X-ray photoelectron spectroscopy are used to evaluate polymer chemical modifications. Morphological changes are studied through scanning electron and atomic force microscopy. Results show the ability of plasma treatment to create active oxydised functional groups on the polypropylene surface. These groups lead to a proper wetting of the polymer by the silane. Shear strength of single-lap bonding of polypropylene with a polyurethane adhesive suffers a significant improvement when the silane coating is applied on previously plasma activated samples. It has been also demonstrated that the silane curing conditions play a decisive role on the adhesion response. Finally, the stability of the silane solution is tested up to 30 days, yielding diminished but still acceptable adhesion strength values.

Resistance of poly(ethylene oxide)-silane monolayers to the growth of polyelectrolyte multilayers.

PubMed

Buron, Cédric C; Callegari, Vincent; Nysten, Bernard; Jonas, Alain M

2007-09-11

The ability of poly(ethylene oxide)-silane (PEO-silane) monolayers grafted onto silicon surfaces to resist the growth of polyelectrolyte multilayers under various pH conditions is assessed for different pairs of polyelectrolytes of varying molar mass. For acidic conditions (pH 3), the PEO-silane monolayers exhibit good polyelectrolyte repellency provided the polyelectrolytes bear no moieties that are able to form hydrogen bonds with the ether groups of the PEO chains. At basic pH, PEO-silane monolayers undergo substantial hydrolysis leading to the formation of negatively charged defects in the monolayers, which then play the role of adsorption sites for the polycation. Once the polycation is adsorbed, multilayer growth ensues. Because this is defect-driven growth, the multilayer is not continuous and is made of blobs or an open network of adsorbed strands. For such conditions, the molar mass of the polyelectrolyte plays a key role, with polyelectrolyte chains of larger molar mass adsorbing on a larger number of defects, resulting in stronger anchoring of the polyelectrolyte complex on the surfaces and faster subsequent growth of the multilayer. For polyelectrolytes of sufficiently low molar mass at pH 9, the growth of the multilayer can nevertheless be prevented for as much as five cycles of deposition.

Development of an environmentally benign anticorrosion coating for aluminum alloy using green pigments and organofunctional silanes

NASA Astrophysics Data System (ADS)

Yin, Zhangzhang

Aerospace aluminum alloys such as Al alloy 2024-T3 and 7075-T6 are subject to localized corrosion due the existence of intermetallics containing Cu, Mg or Zn. Current protection measurement employs substantial use of chromate and high VOC organics, both of which are identified as environment and health hazards. The approach of this study is to utilize a combination of organofunctional silanes and a compatible inhibitor integrated into high-performance waterborne resins. First, an extensive pigment screening has been done to find replacements for chromates using the testing methodology for fast corrosion inhibition evaluation and pigment. Zinc phosphate and calcium zinc phosphomolybdate were found to have the best overall performance on Al alloys. Some new corrosion inhibitors were synthesized by chemical methods or modified by plasma polymerization for use in the coatings. Low-VOC, chromate-free primers (superprimer) were developed using these pigments with silane and acrylic-epoxy resins. The developed superprimer demonstrated good corrosion inhibition on aluminum substrates. The functions of inhibitor and silane in the coating were investigated. Both silane and inhibitor are critical for the performance of the superprimer. Silane was found to improve the adhesion of the coating to the substrate and also facilitate corrosion prevention. Addition of zinc phosphate to the coating improved the resistance of a scratched area against corrosion. The microstructure of the acrylic-epoxy superprimer coating was studied. SEM/EDAX revealed that the superprimer has a self-assembled stratified double-layer structure which accounts for the strong anti-corrosion performance of the zinc phosphate pigment. Zinc phosphate leaches out from the coating to actively protect the scratched area. The leaching of pigment was confirmed in the ICP-MS analysis and the leaching rate was measured. Coating-metal interface and the scribe of coated panels subjected to corrosion test was studied. ToF-SIMS studies confirmed the presence of silane at the interface and the hydrolysis of the silane. The abundant presence of silane was believed to improve the adhesion and also facilitate the corrosion prevention. The protection mechanism of the acrylic-epoxy superprimer was proposed. The self-assembled double-layer structure of the acrylic-epoxy superprimer consist of a less-penetrable hydrophobic layer (epoxy-dominated) on the top and a hydrophilic layer (acrylic-dominated) accommodating the inhibitors underneath. This unique structure of the acrylic-epoxy accounts for the good protection of the coating. Furthermore, the inhibition mechanism of zinc phosphate was explored and compared to those which have been reported. Based on the protection mechanism of the superprimer, electrodeposition was explored in order to achieve a more organized coating with a better engineered metal/coating interface. The electrodeposited coatings were found to have higher barrier property and anticorrosion performance.

Production of hybrid lipid-based particles loaded with inorganic nanoparticles and active compounds for prolonged topical release.

PubMed

García-González, C A; Sampaio da Sousa, A R; Argemí, A; López Periago, A; Saurina, J; Duarte, C M M; Domingo, C

2009-12-01

The production of particulate hybrid carriers containing a glyceryl monostearate (Lumulse GMS-K), a waxy triglyceride (Cutina HR), silanized TiO(2) and caffeine were investigated with the aim of producing sunscreens with UV-radiation protection properties. Particles were obtained using the supercritical PGSS (Particles from Gas Saturated Solutions) technique. This method takes advantages of the lower melting temperatures of the lipids obtained from the dissolution of CO(2) in the bulk mixture. Experiments were performed at 13 MPa and 345 K, according to previous melting point measurements. Blends containing Lumulse GMS-K and Cutina HR lipids (50 wt%) were loaded with silanized TiO(2) and caffeine in percentile proportions of 6 and 4 wt%, respectively. The particles produced were characterized using several analytical techniques as follows: system crystallinity was checked by X-ray diffraction and differential scanning calorimetry, thermal stability by thermogravimetric analysis, and morphology by scanning and transmission electron microscopy. Further, the UV-shielding ability of TiO(2) after its dispersion in the lipidic matrix was assessed by solid UV-vis spectroscopy. Preliminary results indicated that caffeine-loaded solid lipid particles presented a two-step dissolution profile, with an initial burst of 60 wt% of the loaded active agent. Lipid blends loaded with TiO(2) and caffeine encompassed the UV-filter behavior of TiO(2) and the photoaging prevention properties of caffeine.

Magnesium silicide nanoparticles as a deoxygenation agent for cancer starvation therapy

NASA Astrophysics Data System (ADS)

Zhang, Chen; Ni, Dalong; Liu, Yanyan; Yao, Heliang; Bu, Wenbo; Shi, Jianlin

2017-05-01

A material that rapidly absorbs molecular oxygen (known as an oxygen scavenger or deoxygenation agent (DOA)) has various industrial applications, such as in food preservation, anticorrosion of metal and coal deoxidation. Given that oxygen is vital to cancer growth, to starve tumours through the consumption of intratumoral oxygen is a potentially useful strategy in fighting cancer. Here we show that an injectable polymer-modified magnesium silicide (Mg2Si) nanoparticle can act as a DOA by scavenging oxygen in tumours and form by-products that block tumour capillaries from being reoxygenated. The nanoparticles are prepared by a self-propagating high-temperature synthesis strategy. In the acidic tumour microenvironment, the Mg2Si releases silane, which efficiently reacts with both tissue-dissolved and haemoglobin-bound oxygen to form silicon oxide (SiO2) aggregates. This in situ formation of SiO2 blocks the tumour blood capillaries and prevents tumours from receiving new supplies of oxygen and nutrients.

Magnesium silicide nanoparticles as a deoxygenation agent for cancer starvation therapy.

PubMed

Zhang, Chen; Ni, Dalong; Liu, Yanyan; Yao, Heliang; Bu, Wenbo; Shi, Jianlin

2017-05-01

A material that rapidly absorbs molecular oxygen (known as an oxygen scavenger or deoxygenation agent (DOA)) has various industrial applications, such as in food preservation, anticorrosion of metal and coal deoxidation. Given that oxygen is vital to cancer growth, to starve tumours through the consumption of intratumoral oxygen is a potentially useful strategy in fighting cancer. Here we show that an injectable polymer-modified magnesium silicide (Mg 2 Si) nanoparticle can act as a DOA by scavenging oxygen in tumours and form by-products that block tumour capillaries from being reoxygenated. The nanoparticles are prepared by a self-propagating high-temperature synthesis strategy. In the acidic tumour microenvironment, the Mg 2 Si releases silane, which efficiently reacts with both tissue-dissolved and haemoglobin-bound oxygen to form silicon oxide (SiO 2 ) aggregates. This in situ formation of SiO 2 blocks the tumour blood capillaries and prevents tumours from receiving new supplies of oxygen and nutrients.

Development of acceptance criteria for batches of silane primer for external tank thermal protection system bonding applications

NASA Technical Reports Server (NTRS)

Mikes, F.; Mowrey, C.; Reis, E.

1985-01-01

Results of lap shear tests of various silane primers are presented in graphs and tables. The OH-absorption of these primers (FTIR area values) are correlated with the lap shear tests of coated panels.

Viscoelastic Properties of Alkoxy Silane-Epoxy Interpenetrating Networks

DTIC Science & Technology

2003-11-01

Owens Corning Fiberglass for supply of the epoxy film former emulsion used in the model silane formulation. The authors also wish to acknowledge the...inclusion filled composite µm- powderproperties 4 triblock copolymer surfactant. The Owens Corning Company generously provided the film former emulsion

Mechanical properties of dental resin/composite containing urchin-like hydroxyapatite.

PubMed

Liu, Fengwei; Sun, Bin; Jiang, Xiaoze; Aldeyab, Sultan S; Zhang, Qinghong; Zhu, Meifang

2014-12-01

To investigate the reinforcing effect of urchin-like hydroxyapatite (UHA) in bisphenol A glycidyl methacrylate (Bis-GMA)/triethylene glycol dimethacrylate (TEGDMA) dental resin (without silica nanoparticles) and dental composites (with silica nanoparticles), and explore the effect of HA filler morphologies and loadings on the mechanical properties. UHA was synthesized by a facile method of microwave irradiation and studied by X-ray diffraction (XRD), scanning electron microscope (SEM), and thermogravimetric analysis (TGA). Mechanical properties of the dental resin composites containing silanized UHA were tested by a universal mechanical testing machine. Analysis of variance was used for the statistical analysis of the acquired data. The fracture morphologies of tested composites were observed by SEM. Composites with silanized irregular particulate hydroxyapatite (IPHA) and hydroxyapatite whisker (HW) were prepared for comparative studies. Impregnation of lower loadings (5 wt% and 10 wt%) of silanized UHA into dental resin (without silica nanoparticles) substantially improved the mechanical properties; higher UHA loadings (20 wt% and 30 wt%) of impregnation continuously improved the flexural modulus and microhardness, while the strength would no longer be increased. Compared with silanized IPHA and HW, silanized UHA consisting of rods extending radially from center were embedded into the matrix closely and well dispersed in the composite, increasing filler-matrix interfacial contact area and combination. At higher filler loadings, UHA interlaced together tightly without affecting the mobility of monomer inside, which might bear higher loads during fracture of the composite, leading to higher strengths than those of dental resins with IPHA and HW. Besides, impregnation of silanized UHA into dental composites (with silica nanoparticles) significantly improved the strength and modulus. UHA could serve as novel reinforcing HA filler to improve the mechanical properties of dental resin and dental composite.

Effect of water storage on the silanization in porcelain repair strength.

PubMed

Berry, T; Barghi, N; Chung, K

1999-06-01

This study examined the long-term water storage affect of silanization on shear bond strength of composite resin to porcelain. One hundred and sixty square-shaped specimens were fabricated and sanded flat sequentially with silicone carbide papers. The specimens were then placed into four groups and 16 subgroups of 10 specimens each randomly. Four commercially available silane systems, two one-mix and two two-mix, were tested in this study. Teflon tubes with an internal diameter of 2.97 mm and 2 mm in height were filled with a dual cure composite resin (Mirage FLC), placed on the silanated surfaces and light-cured for 120 s. Specimens were stored in room temperature water and subjected to shear bond strength testing after 24 h, 1 week, 1 month and 3 month periods of immersion. An Instron Universal testing machine with a crosshead speed of 0.5 mm/min was used for the testing. The mean values of the shear bond strengths ranged from 4.38 MPa (24-h period) to 23.90 MPa (3-month period). ANOVA and Scheffe' tests were used to analyse data with confidence level at 95%. All groups recorded an increase in bond strength after one week as compared with the 24-h period (P<0.05). With the exception of a one-mix system, all systems showed significantly higher bond strength at 3 weeks as compared with the 24-h and 1-week water storage periods. In conclusion, bond strength of composite resin to porcelain resulting from silanization of porcelain increased during the experimental period. The bond strength also varied for different silanes used in this study.

Silanated Surface Treatment: Effects on the Bond Strength to Lithium Disilicate Glass-Ceramic.

PubMed

Baratto, Samantha Schaffer Pugsley; Spina, Denis Roberto Falcão; Gonzaga, Carla Castiglia; Cunha, Leonardo Fernandes da; Furuse, Adilson Yoshio; Baratto Filho, Flares; Correr, Gisele Maria

2015-10-01

The aim of this study was to evaluate the effect of silanization protocols on the bond strength of two resin cements to a lithium disilicate glass-ceramic. Thirty-two ceramic discs were assigned to 2 groups (n=16): G1 - dual-cured resin cement and G2 - light-cured resin cement. Four subgroups were evaluated according to the used silanization protocol. The glass-ceramic was etched with 10% hydrofluoric acid for 20 s and silane was applied for 1 min, as follows: CTL - according to the manufacturer's instructions; HA - dried with hot air; NWA - washed and dried with water and air at room temperature; HWA - washed and dried with hot water and hot air. Thereafter, adhesive was applied and light-cured for 20 s. Silicon molds were used to prepare resin cement cylinders (1x1 mm) on the ceramic surface. The specimens were stored in deionized water at 37 °C for 48 h and subjected to a micro-shear test. The data were submitted to statistical analysis (?#61537;=0.05). Group G1 showed higher bond strengths than G2, except for the CTL and NWA subgroups. Differences as function of the silanization protocol were only observed in G1: HWA (25.13±6.83)≥HA (22.95±7.78)≥CTL(17.44±7.24) ≥NWA(14.63±8.76). For G2 there was no difference among the subgroups. In conclusion, the silanization protocol affected the resin cement/ceramic bond strengths, depending on the material. Washing/drying with hot water and/or hot air increased only the bond strength of the dual-cured resin cement.

Four chemical methods of porcelain conditioning and their influence over bond strength and surface integrity

PubMed Central

Stella, João Paulo Fragomeni; Oliveira, Andrea Becker; Nojima, Lincoln Issamu; Marquezan, Mariana

2015-01-01

OBJECTIVE: To assess four different chemical surface conditioning methods for ceramic material before bracket bonding, and their impact on shear bond strength and surface integrity at debonding. METHODS: Four experimental groups (n = 13) were set up according to the ceramic conditioning method: G1 = 37% phosphoric acid etching followed by silane application; G2 = 37% liquid phosphoric acid etching, no rinsing, followed by silane application; G3 = 10% hydrofluoric acid etching alone; and G4 = 10% hydrofluoric acid etching followed by silane application. After surface conditioning, metal brackets were bonded to porcelain by means of the Transbond XP system (3M Unitek). Samples were submitted to shear bond strength tests in a universal testing machine and the surfaces were later assessed with a microscope under 8 X magnification. ANOVA/Tukey tests were performed to establish the difference between groups (α= 5%). RESULTS: The highest shear bond strength values were found in groups G3 and G4 (22.01 ± 2.15 MPa and 22.83 ± 3.32 Mpa, respectively), followed by G1 (16.42 ± 3.61 MPa) and G2 (9.29 ± 1.95 MPa). As regards surface evaluation after bracket debonding, the use of liquid phosphoric acid followed by silane application (G2) produced the least damage to porcelain. When hydrofluoric acid and silane were applied, the risk of ceramic fracture increased. CONCLUSIONS: Acceptable levels of bond strength for clinical use were reached by all methods tested; however, liquid phosphoric acid etching followed by silane application (G2) resulted in the least damage to the ceramic surface. PMID:26352845

Surface modification for enhanced silanation of zirconia ceramics.

PubMed

Piascik, J R; Swift, E J; Thompson, J Y; Grego, S; Stoner, B R

2009-09-01

The overall goal of this research was to develop a practical method to chemically modify the surface of high strength dental ceramics (i.e. zirconia) to facilitate viable, robust adhesive bonding using commercially available silanes and resin cements. Investigation focused on a novel approach to surface functionalize zirconia with a Si(x)O(y) "seed" layer that would promote chemical bonding with traditional silanes. ProCAD and ZirCAD blocks were bonded to a dimensionally similar composite block using standard techniques designed for silica-containing materials (silane and resin cement). ZirCAD blocks were treated with SiCl4 by vapor deposition under two different conditions prior to bonding. Microtensile bars were prepared and subjected to tensile forces at a crosshead speed of 1 mm/min scanning electron microscopy was used to analyze fracture surfaces and determine failure mode; either composite cohesive failure (partial or complete cohesive failure within composite) or adhesive failure (partial or complete adhesive failure). Peak stress values were analyzed using single-factor ANOVA (p<0.05). Microtensile testing results revealed that zirconia with a surface treatment of 2.6 nm Si(x)O(y) thick "seed" layer was similar in strength to the porcelain group (control). Analysis of failure modes indicated the above groups displayed higher percentages of in-composite failures. Other groups tested had lower strength values and displayed adhesive failure characteristics. Mechanical data support that utilizing a gas-phase chloro-silane pretreatment to deposit ultra-thin silica-like seed layers can improve adhesion to zirconia using traditional silanation and bonding techniques. This technology could have clinical impact on how high strength dental materials are used today.

Plasma processes for producing silanes and derivatives thereof

DOEpatents

Laine, Richard M; Massey, Dean Richard; Peterson, Peter Young

2014-03-25

The invention is generally related to process for generating one or more molecules having the formula Si.sub.xH.sub.y, Si.sub.xD.sub.y, Si.sub.xH.sub.yD.sub.z, and mixtures thereof, where x,y and z are integers .gtoreq.1, H is hydrogen and D is deuterium, such as silane, comprising the steps of: providing a silicon containing material, wherein the silicon containing material includes at least 20 weight percent silicon atoms based on the total weight of the silicon containing material; generating a plasma capable of vaporizing a silicon atom, sputtering a silicon atom, or both using a plasma generating device; and contacting the plasma to the silicon containing material in a chamber having an atmosphere that includes at least about 0.5 mole percent hydrogen atoms and/or deuterium atoms based on the total moles of atoms in the atmosphere; so that a molecule having the formula Si.sub.xH.sub.y; (e.g., silane) is generated. The process preferably includes a step of removing one or more impurities from the Si.sub.xH.sub.y (e.g., the silane) to form a clean Si.sub.xH.sub.y, Si.sub.xD.sub.y, Si.sub.xH.sub.yD.sub.z (e.g., silane). The process may also include a step of reacting the Si.sub.xH.sub.y, Si.sub.xD.sub.y, Si.sub.xH.sub.yD.sub.z (e.g., the silane) to produce a high purity silicon containing material such as electronic grade metallic silicon, photovoltaic grade metallic silicon, or both.

Effect of curing and silanizing on composite repair bond strength using an improved micro-tensile test method

PubMed Central

Eliasson, Sigfus Thor; Dahl, Jon E.

2017-01-01

Abstract Objectives: To evaluate the micro-tensile repair bond strength between aged and new composite, using silane and adhesives that were cured or left uncured when new composite was placed. Methods: Eighty Filtek Supreme XLT composite blocks and four control blocks were stored in water for two weeks and thermo-cycled. Sandpaper ground, etched and rinsed specimens were divided into two experimental groups: A, no further treatment and B, the surface was coated with bis-silane. Each group was divided into subgroups: (1) Adper Scotchbond Multi-Purpose, (2) Adper Scotchbond Multi-Purpose adhesive, (3) Adper Scotchbond Universal, (4) Clearfil SE Bond and (5) One Step Plus. For each adhesive group, the adhesive was (a) cured according to manufacturer’s instructions or (b) not cured before repair. The substrate blocks were repaired with Filtek Supreme XLT. After aging, they were serially sectioned, producing 1.1 × 1.1 mm square test rods. The rods were prepared for tensile testing and tensile strength calculated at fracture. Type of fracture was examined under microscope. Results: Leaving the adhesive uncured prior to composite repair placement increased the mean tensile values statistically significant for all adhesives tested, with or without silane pretreatment. Silane surface treatment improved significantly (p < 0.001) tensile strength values for all adhesives, both for the cured and uncured groups. The mean strength of the control composite was higher than the strongest repair strength (p < 0.001). Conclusions: Application of freshly made silane and a thin bonding layer, rendered higher tensile bond strength. Not curing the adhesive before composite placement increased the tensile bond strength. PMID:28642928

An Ex-vivo Shear and tensile bond strengths of orthodontic molar tubes bonded using different techniques.

PubMed

Abu-Alhaija, Elham; Jaradat, Mohammad; Alwahadni, Ahed

2017-03-01

Molar bonding procedures need continuous improvement to be widely accepted clinically and eventually replace molar bands. The purpose of this study was to determine the effects of enamel micro-abrasion and silane coating of the base of molar tubes on shear and tensile bond strengths of orthodontic molar tubes. A total of 200 third molars were randomly allocated into five groups of 40 teeth as follows: group 1: molar tubes bonded to etched teeth (37% phosphoric acid gel; control group); group 2: molar tubes bonded to etched teeth (37% phosphoric acid) with the addition of silane to the base of molar tubes; group 3: molar tubes bonded to teeth pre-treated with 18% hydrochloric acid and pumice (micro-abrasion); group 4: molar tubes bonded to teeth pre-treated with microabrasion with the addition of silane to the base of molar tubes; group 5: molar tubes bonded to teeth pre-treated with microabrasion before conventional acid etching combined with the addition of silane to the base of molar tubes. The bond strength testing was performed using a computer control electromechanical universal testing machine. The highest mean shear and tensile bond strengths were recorded in group 5 (13.81±2.54MPa and 13.97±2.29 MPa, respectively). Micro-abrasion alone (group 3) and the combination of enamel micro-abrasion and the addition of silane (group 4) produced bond strength values comparable to the control. Enamel surface pre-treatment (micro abrasion) before conventional acid etching combined with the addition of silane to the base of the molar tube produced the highest bond strengths among all tested groups. Key words: Molar, shear strength, tensile strength, orthodontic appliances.

An Ex-vivo Shear and tensile bond strengths of orthodontic molar tubes bonded using different techniques

PubMed Central

Alwahadni, Ahed

2017-01-01

Background Molar bonding procedures need continuous improvement to be widely accepted clinically and eventually replace molar bands. Material and Methods The purpose of this study was to determine the effects of enamel micro-abrasion and silane coating of the base of molar tubes on shear and tensile bond strengths of orthodontic molar tubes. A total of 200 third molars were randomly allocated into five groups of 40 teeth as follows: group 1: molar tubes bonded to etched teeth (37% phosphoric acid gel; control group); group 2: molar tubes bonded to etched teeth (37% phosphoric acid) with the addition of silane to the base of molar tubes; group 3: molar tubes bonded to teeth pre-treated with 18% hydrochloric acid and pumice (micro-abrasion); group 4: molar tubes bonded to teeth pre-treated with microabrasion with the addition of silane to the base of molar tubes; group 5: molar tubes bonded to teeth pre-treated with microabrasion before conventional acid etching combined with the addition of silane to the base of molar tubes. The bond strength testing was performed using a computer control electromechanical universal testing machine. Results The highest mean shear and tensile bond strengths were recorded in group 5 (13.81±2.54MPa and 13.97±2.29 MPa, respectively). Micro-abrasion alone (group 3) and the combination of enamel micro-abrasion and the addition of silane (group 4) produced bond strength values comparable to the control. Conclusions Enamel surface pre-treatment (micro abrasion) before conventional acid etching combined with the addition of silane to the base of the molar tube produced the highest bond strengths among all tested groups. Key words:Molar, shear strength, tensile strength, orthodontic appliances. PMID:28298990

Dual nickel and Lewis acid catalysis for cross-electrophile coupling: the allylation of aryl halides with allylic alcohols† †Electronic supplementary information (ESI) available. CCDC 1515176. For ESI and crystallographic data in CIF or other electronic format see DOI: 10.1039/c7sc03140h

PubMed Central

Jia, Xue-Gong; Guo, Peng; Duan, Jicheng

2017-01-01

Controlling the selectivity in cross-electrophile coupling reactions is a significant challenge, particularly when one electrophile is much more reactive. We report a general and practical strategy to address this problem in the reaction between reactive and unreactive electrophiles by a combination of nickel and Lewis acid catalysis. This strategy is used for the coupling of aryl halides with allylic alcohols to form linear allylarenes selectively. The reaction tolerates a wide range of functional groups (e.g. silanes, boronates, anilines, esters, alcohols, and various heterocycles) and works with various allylic alcohols. Complementary to most current routes for the C3 allylation of an unprotected indole, this method provides access to C2 and C4–C7 allylated indoles. Preliminary mechanistic experiments reveal that the reaction might start with an aryl nickel intermediate, which then reacts with Lewis acid activated allylic alcohols in the presence of Mn. PMID:29629130

DOE Office of Scientific and Technical Information (OSTI.GOV)

Thomas, Reshmi; Thomas, Anoop; Pullanchery, Saranya

Strong coupling interactions between plasmon and exciton-based excitations have been proposed to be useful in the design of optoelectronic systems. However, the role of various optical parameters dictating the plasmon-exciton (plexciton) interactions is less understood. Herein, we propose an inequality for achieving strong coupling between plasmons and excitons through appropriate variation of their oscillator strengths and spectral widths. These aspects are found to be consistent with experiments on two sets of free-standing plexcitonic systems obtained by (i) linking fluorescein isothiocyanate on Ag nanoparticles of varying sizes through silane coupling and (ii) electrostatic binding of cyanine dyes on polystyrenesulfonate-coated Au nanorodsmore » of varying aspect ratios. Being covalently linked on Ag nanoparticles, fluorescein isothiocyanate remains in monomeric state, and its high oscillator strength and narrow spectral width enable us to approach the strong coupling limit. In contrast, in the presence of polystyrenesulfonate, monomeric forms of cyanine dyes exist in equilibrium with their aggregates: Coupling is not observed for monomers and H-aggregates whose optical parameters are unfavorable. The large aggregation number, narrow spectral width, and extremely high oscillator strength of J-aggregates of cyanines permit effective delocalization of excitons along the linear assembly of chromophores, which in turn leads to efficient coupling with the plasmons. Further, the results obtained from experiments and theoretical models are jointly employed to describe the plexcitonic states, estimate the coupling strengths, and rationalize the dispersion curves. The experimental results and the theoretical analysis presented here portray a way forward to the rational design of plexcitonic systems attaining the strong coupling limits.« less

Bioactive composites with designed interfaces

NASA Astrophysics Data System (ADS)

Orefice, Rodrigo Lambert

Bioactive glasses can bond to bone and even soft tissue. However, they are usually weak, brittle and hard to process in specific shapes. The goal of this work is to produce polymer composites having bioactive materials as a reinforcing phase that would display both bioactive behavior and mechanical properties compatible to bone. Polysulfone and bioactive glass particulate were combined in composites with different volume fractions. Composites with 40 vol.% of particulate were submitted to in vitro tests in simulated body fluids. The recorded rates of hydroxy-carbonate-apatite layer deposition were close to the ones observed for pure bioactive glasses. Mechanical properties showed values of elastic modulus, strain at failure and strength within the range of cortical bone for composites with high volume fraction of particles. Fibers can usually favor higher levels of reinforcement in composites than particles. Novel multicomponent fibers were prepared by using the sol-gel method. They were determined to be bioactive in vitro and were successfully used as a reinforcing phase in polysulfone composites. Properties of the bioactive composites were modified by altering the chemistry and structure of the interfaces. Polymers with sulfonic acid and silane groups were specially designed to interact with both the silica surface and the polymer matrix. Nano-composites with a structure and chemistry in between the macrocomponents of the composite were prepared by combining a silanated polymer and silica sol-gel. When applied as interfacial agents, these nano-composites as well as the modified polymers improved the overall properties of the bioactive system. A decay in mechanical properties was observed for composites submitted to an in vitro test. The developed interfacial agents successfully reduced the degree of degradation in properties. Interactions occurring at the interfaces of bioactive composites were studied using Atomic Force Microscopy (AFM). The effect of the structure and chemistry of interfaces was correlated to physical and chemical processes occurring at the interfaces and to the overall properties of composites.

Low-cost Solar Array Project. Feasibility of the Silane Process for Producing Semiconductor-grade Silicon

NASA Technical Reports Server (NTRS)

1979-01-01

The feasibility of Union Carbide's silane process for commercial application was established. An integrated process design for an experimental process system development unit and a commercial facility were developed. The corresponding commercial plant economic performance was then estimated.

Characterization of immobilization methods of antiviral antibodies in serum for electrochemical biosensors

NASA Astrophysics Data System (ADS)

Huy, Tran Quang; Hanh, Nguyen Thi Hong; Van Chung, Pham; Anh, Dang Duc; Nga, Phan Thi; Tuan, Mai Anh

2011-06-01

In this paper, we describes different methods to immobilize Japanese encephalitis virus (JEV) antibodies in human serum onto the interdigitated surface of a microelectrode sensor for optimizing electrochemical detection: (1) direct covalent binding to the silanized surface, (2) binding to the silanized surface via a cross-linker of glutaraldehyde (GA), (3) binding to glutaraldehyde/silanized surface via goat anti-human IgG polyclonal antibody and (4) binding to glutaraldehyde/silanized surface via protein A (PrA). Field emission scanning electron microscopy, Fourier transform infrared spectrometry, and fluorescence microscopy are used to verify the characteristics of antibodies on the interdigitated surface after the serum antibodies immobilization. The analyzed results indicate that the use of protein A is an effective choice for immobilization and orientation of antibodies in serum for electrochemical biosensors. This study provides an advantageous immobilization method of serum containing antiviral antibodies to develop electrochemical biosensors for preliminary screening of viruses in clinical samples from outbreaks.

Homoleptic ligands vs heteroleptic ligands on coordination polymerizations: Construction and properties of silver(I) coordination polymers containing dialkylbis(4-pyridy)silanes

NASA Astrophysics Data System (ADS)

Park, Minwoo; Jang, Jaeseong; Moon, So Yun; Jung, Ok-Sang

2014-03-01

Investigations into pure bidentate ligand vs mixed bidentate ligands on self-assembly of AgPF6 with the respective L1, L2, L3, L1/L2, L1/L3, and L2/L3 (L1 = diethylbis(4-pyridyl)silane; L2 = ethylmethylbis(4-pyridyl)silane; L3 = cyclotetramethylenebis(4-pyridyl)silane) were carried out. The self-assembly reactions of AgPF6 with the respective ligand system produce desirable homoleptic or heteroleptic silver(I) coordination polymers. [Ag(L1)2](PF6) gives rise to a tubular loop chain whereas the other five products lead to a twofold interpenetration diamonoid structure. [Ag(L1)2](PF6) shows a strong blue luminescence at 453 nm (λex = 270 nm), which is useful to recognize alcohols. All products were characterized by thermal analyses, and in particular, calcination of [Ag(L3)2](PF6)ṡCH3OH at 600 °C finally produces silver(0) microcrystalline morphology.

Development of processes for the production of solar grade silicon from halides and alkali metals, phase 1 and phase 2

NASA Technical Reports Server (NTRS)

Dickson, C. R.; Gould, R. K.; Felder, W.

1981-01-01

High temperature reactions of silicon halides with alkali metals for the production of solar grade silicon are described. Product separation and collection processes were evaluated, measure heat release parameters for scaling purposes and effects of reactants and/or products on materials of reactor construction were determined, and preliminary engineering and economic analysis of a scaled up process were made. The feasibility of the basic process to make and collect silicon was demonstrated. The jet impaction/separation process was demonstrated to be a purification process. The rate at which gas phase species from silicon particle precursors, the time required for silane decomposition to produce particles, and the competing rate of growth of silicon seed particles injected into a decomposing silane environment were determined. The extent of silane decomposition as a function of residence time, temperature, and pressure was measured by infrared absorption spectroscopy. A simplistic model is presented to explain the growth of silicon in a decomposing silane enviroment.

Adsorption behavior of glycidoxypropyl-trimethoxy-silane on titanium alloy Ti-6.5Al-1Mo-1V-2Zr

NASA Astrophysics Data System (ADS)

Liu, Jian-hua; Zhan, Zhong-wei; Yu, Mei; Li, Song-mei

2013-01-01

The adsorption behavior of glycidoxypropyl-trimethoxy-silane (GTMS) on titanium alloy Ti-6.5Al-1Mo-1V-2Zr was investigated by using X-ray photoelectron spectroscopy (XPS), Tafel polarization test, and electrochemical impedance spectroscopy (EIS). From the XPS results, it was found that the silane coverage on the titanium surface generally increased with GTMS concentration, with a slight decrease at concentration of 0.1%. Based on the relationship between isoelectronic point (IEP) of titanium surface and the pH values of silane solutions, adsorption mechanisms at different concentrations were proposed. The surface coverage data of GTMS on titanium surface was also derived from electrochemical measurements. By linear fitting the coverage data, it revealed that the adsorption of GTMS on the titanium alloy surface at 30 °C was of a physisorption-based mechanism, and obeyed Langmuir adsorption isotherm. The adsorption equilibrium constant (Kads) and free energy of adsorption process (ΔGads) were calculated to elaborate the mechanism of GTMS adsorption.

Silver Makes Better Electrical Contacts to Thiol-Terminated Silanes than Gold.

PubMed

Li, Haixing; Su, Timothy A; Camarasa-Gómez, María; Hernangómez-Pérez, Daniel; Henn, Simon E; Pokorný, Vladislav; Caniglia, Caravaggio D; Inkpen, Michael S; Korytár, Richard; Steigerwald, Michael L; Nuckolls, Colin; Evers, Ferdinand; Venkataraman, Latha

2017-11-06

We report that the single-molecule junction conductance of thiol-terminated silanes with Ag electrodes are higher than the conductance of those formed with Au electrodes. These results are in contrast to the trends in the metal work function Φ(Ag)<Φ(Au). As such, a better alignment of the Au Fermi level to the molecular orbital of silane that mediates charge transport would be expected. This conductance trend is reversed when we replace the thiols with amines, highlighting the impact of metal-S covalent and metal-NH 2 dative bonds in controlling the molecular conductance. Density functional theory calculations elucidate the crucial role of the chemical linkers in determining the level alignment when molecules are attached to different metal contacts. We also demonstrate that conductance of thiol-terminated silanes with Pt electrodes is lower than the ones formed with Au and Ag electrodes, again in contrast to the trends in the metal work-functions. © 2017 Wiley-VCH Verlag GmbH & Co. KGaA, Weinheim.

Fluidized-bed reactor modeling for production of silicon by silane pyrolysis

NASA Technical Reports Server (NTRS)

Dudukovic, M. P.; Ramachandran, P. A.; Lai, S.

1986-01-01

An ideal backmixed reactor model (CSTR) and a fluidized bed bubbling reactor model (FBBR) were developed for silane pyrolysis. Silane decomposition is assumed to occur via two pathways: homogeneous decomposition and heterogeneous chemical vapor deposition (CVD). Both models account for homogeneous and heterogeneous silane decomposition, homogeneous nucleation, coagulation and growth by diffusion of fines, scavenging of fines by large particles, elutriation of fines and CVD growth of large seed particles. At present the models do not account for attrition. The preliminary comparison of the model predictions with experimental results shows reasonable agreement. The CSTR model with no adjustable parameter yields a lower bound on fines formed and upper estimate on production rates. The FBBR model overpredicts the formation of fines but could be matched to experimental data by adjusting the unkown jet emulsion exchange efficients. The models clearly indicate that in order to suppress the formation of fines (smoke) good gas-solid contacting in the grid region must be achieved and the formation of the bubbles suppressed.

Enhancing stability and efficiency of perovskite solar cells with crosslinkable silane-functionalized and doped fullerene

DOE PAGES

Bai, Yang; Dong, Qingfeng; Shao, Yuchuan; ...

2016-10-05

The instability of hybrid perovskite materials due to water and moisture arises as one major challenge to be addressed before any practical application of the demonstrated high efficiency perovskite solar cells. Here we report a facile strategy that can simultaneously enhance the stability and efficiency of p-i-n planar heterojunction-structure perovskite devices. Crosslinkable silane molecules with hydrophobic functional groups are bonded onto fullerene to make the fullerene layer highly water-resistant. Methylammonium iodide is introduced in the fullerene layer for n-doping via anion-induced electron transfer, resulting in dramatically increased conductivity over 100-fold. With crosslinkable silane-functionalized and doped fullerene electron transport layer, themore » perovskite devices deliver an efficiency of 19.5% with a high fill factor of 80.6%. Furthermore, a crosslinked silane-modified fullerene layer also enhances the water and moisture stability of the non-sealed perovskite devices by retaining nearly 90% of their original efficiencies after 30 days’ exposure in an ambient environment.« less

Light-weight black ceramic insulation

NASA Technical Reports Server (NTRS)

Hsu, Ming-Ta S. (Inventor); Chen, Timothy S. (Inventor)

2003-01-01

Ultra-high temperature, light-weight, black ceramic insulation having a density ranging from about 0.12 g/cc. to 0.6 g/cc. such as ceramic tile is obtained by pyrolyzing siloxane gels derived from the reaction of at least one organo dialkoxy silane and at least one tetralkoxy silane in an acid or base liquid medium. The reaction mixture of the tetra- and dialkoxy silanes also may contain an effective amount of a mono- or trialkoxy silane to obtain the siloxane gels. The siloxane gels are dried at ambient temperatures and pressures to form siloxane ceramic precursors without significant shrinkage. The siloxane ceramic precursors are subsequently pyrolyzed, in an inert atmosphere, to form the black ceramic insulation comprising atoms of silicon, carbon and oxygen. The ceramic insulation can be characterized as a porous, uniform ceramic tile resistant to oxidation at temperatures ranging as high as 1700.degree. C., and particularly useful as lightweight tiles for spacecraft and other high-temperature insulation applications.

Enhancing stability and efficiency of perovskite solar cells with crosslinkable silane-functionalized and doped fullerene

PubMed Central

Bai, Yang; Dong, Qingfeng; Shao, Yuchuan; Deng, Yehao; Wang, Qi; Shen, Liang; Wang, Dong; Wei, Wei; Huang, Jinsong

2016-01-01

The instability of hybrid perovskite materials due to water and moisture arises as one major challenge to be addressed before any practical application of the demonstrated high efficiency perovskite solar cells. Here we report a facile strategy that can simultaneously enhance the stability and efficiency of p–i–n planar heterojunction-structure perovskite devices. Crosslinkable silane molecules with hydrophobic functional groups are bonded onto fullerene to make the fullerene layer highly water-resistant. Methylammonium iodide is introduced in the fullerene layer for n-doping via anion-induced electron transfer, resulting in dramatically increased conductivity over 100-fold. With crosslinkable silane-functionalized and doped fullerene electron transport layer, the perovskite devices deliver an efficiency of 19.5% with a high fill factor of 80.6%. A crosslinked silane-modified fullerene layer also enhances the water and moisture stability of the non-sealed perovskite devices by retaining nearly 90% of their original efficiencies after 30 days' exposure in an ambient environment. PMID:27703136

Facile and high-efficient immobilization of histidine-tagged multimeric protein G on magnetic nanoparticles

NASA Astrophysics Data System (ADS)

Lee, Jiho; Chang, Jeong Ho

2014-12-01

This work reports the high-efficient and one-step immobilization of multimeric protein G on magnetic nanoparticles. The histidine-tagged (His-tag) recombinant multimeric protein G was overexpressed in Escherichia coli BL21 by the repeated linking of protein G monomers with a flexible linker. High-efficient immobilization on magnetic nanoparticles was demonstrated by two different preparation methods through the amino-silane and chloro-silane functionalization on silica-coated magnetic nanoparticles. Three kinds of multimeric protein G such as His-tag monomer, dimer, and trimer were tested for immobilization efficiency. For these tests, bicinchoninic acid (BCA) assay was employed to determine the amount of immobilized His-tag multimeric protein G. The result showed that the immobilization efficiency of the His-tag multimeric protein G of the monomer, dimer, and trimer was increased with the use of chloro-silane-functionalized magnetic nanoparticles in the range of 98% to 99%, rather than the use of amino-silane-functionalized magnetic nanoparticles in the range of 55% to 77%, respectively.

Delay-dependent coupling for a multi-agent LTI consensus system with inter-agent delays

NASA Astrophysics Data System (ADS)

Qiao, Wei; Sipahi, Rifat

2014-01-01

Delay-dependent coupling (DDC) is considered in this paper in a broadly studied linear time-invariant multi-agent consensus system in which agents communicate with each other under homogeneous delays, while attempting to reach consensus. The coupling among the agents is designed here as an explicit parameter of this delay, allowing couplings to autonomously adapt based on the delay value, and in order to guarantee stability and a certain degree of robustness in the network despite the destabilizing effect of delay. Design procedures, analysis of convergence speed of consensus, comprehensive numerical studies for the case of time-varying delay, and limitations are presented.

Methods for attaching polymerizable ceragenins to water treatment membranes using silane linkages

DOEpatents

Hibbs, Michael; Altman, Susan J.; Jones, Howland D. T.; Savage, Paul B.

2013-09-10

This invention relates to methods for chemically grafting and attaching ceragenin molecules to polymer substrates; methods for synthesizing ceragenin-containing copolymers; methods for making ceragenin-modified water treatment membranes and spacers; and methods of treating contaminated water using ceragenin-modified treatment membranes and spacers. Ceragenins are synthetically produced antimicrobial peptide mimics that display broad-spectrum bactericidal activity. Alkene-functionalized ceragenins (e.g., acrylamide-functionalized ceragenins) can be attached to polyamide reverse osmosis membranes using amine-linking, amide-linking, UV-grafting, or silane-coating methods. In addition, silane-functionalized ceragenins can be directly attached to polymer surfaces that have free hydroxyls.

40 CFR 721.6920 - Butyl acrylate, polymer with substituted methyl styrene, methyl methacrylate, and substituted...

Code of Federal Regulations, 2010 CFR

2010-07-01

... 40 Protection of Environment 30 2010-07-01 2010-07-01 false Butyl acrylate, polymer with... acrylate, polymer with substituted methyl styrene, methyl methacrylate, and substituted silane. (a... butyl acrylate, polymer with substituted methyl styrene, methyl methacrylate, and substituted silane...

40 CFR 721.6920 - Butyl acrylate, polymer with substituted methyl styrene, methyl methacrylate, and substituted...

Code of Federal Regulations, 2014 CFR

2014-07-01

... 40 Protection of Environment 31 2014-07-01 2014-07-01 false Butyl acrylate, polymer with... acrylate, polymer with substituted methyl styrene, methyl methacrylate, and substituted silane. (a... butyl acrylate, polymer with substituted methyl styrene, methyl methacrylate, and substituted silane...

40 CFR 721.6920 - Butyl acrylate, polymer with substituted methyl styrene, methyl methacrylate, and substituted...

Code of Federal Regulations, 2013 CFR

2013-07-01

... 40 Protection of Environment 32 2013-07-01 2013-07-01 false Butyl acrylate, polymer with... acrylate, polymer with substituted methyl styrene, methyl methacrylate, and substituted silane. (a... butyl acrylate, polymer with substituted methyl styrene, methyl methacrylate, and substituted silane...

40 CFR 721.6920 - Butyl acrylate, polymer with substituted methyl styrene, methyl methacrylate, and substituted...

Code of Federal Regulations, 2012 CFR

2012-07-01

... 40 Protection of Environment 32 2012-07-01 2012-07-01 false Butyl acrylate, polymer with... acrylate, polymer with substituted methyl styrene, methyl methacrylate, and substituted silane. (a... butyl acrylate, polymer with substituted methyl styrene, methyl methacrylate, and substituted silane...

Luminescent properties of YVO4:Eu/SiO2 core-shell composite particles

NASA Astrophysics Data System (ADS)

Bao, Amurisana; Lai, Hua; Yang, Yuming; Liu, Zhilong; Tao, Chunyan; Yang, Hua

2010-02-01

We report an efficient process for preparing monodisperse SiO2@Y0.95Eu0.05VO4 core-shell phosphors using a simple citrate sol-gel method and without the use of surface-coupling silane agents or large stabilizers. X-ray diffraction (XRD), field emission scanning electron microscopy (FESEM), transmission electron microscopy (TEM), and photoluminescence (PL) spectra were used to characterize the resulting SiO2@Y0.95Eu0.05VO4 core-shell phosphors. The XRD results demonstrate that the Y0.95Eu0.05VO4 particles crystallization on the surface of SiO2 annealing at 800 °C is perfectly and the crystallinity increases with raising the annealing temperature. The obtained core-shell phosphors have a near perfect spherical shape with narrow size distribution (average size ca. 500 nm and an average thickness of 50 nm), are not agglomerated, and have a smooth surface. The thickness of the YVO4:Eu3+ shells on the SiO2 cores could be easily tailored by changing the mass ratio of shell to core ( W = [YVO4]/[SiO2]) ( 50 nm for W = 30%). The Eu3+ shows a strong PL luminescence (dominated by 5D0 - 7F2 red emission at 618 nm) under the excitation of 320 nm UV light. The PL intensity of Eu3+ increases with increasing the annealing temperature and the values of W.

Foaming in chemical surfactant free aqueous dispersions of anatase (titanium dioxide) particles.

PubMed

Pugh, R J

2007-07-17

Steady-state dynamic aqueous foams were generated from surfactant-free dispersion of aggregated anatase nanoparticles (in the micrometer size range). In order to tune the particle surfaces, to ensure a critical degree of hydrophobicity (so that they disperse in water and generate foam), the particles were subjected to low-temperature plasma treatment in the presence of a vapor-phase silane coupling agents. From ESCA it was shown that hydrophobization only occurred at a small number of surface sites. Foamability (foam generation) experiments were carried out under well-defined conditions at a range of gas flow rates using the Bikermann Foaming Column.1 The volume of the steady-state foams was determined under constant gas flow conditions, but on removing the gas flow, transient foams with short decay times (<5 s) were observed. The foamability of the steady-state foams was found to be dependent on (a) the time of plasma treatment of the particles (surface hydrophobicity), (b) the particle concentration in the suspension, and (c) the state of dispersion of the particles. High foamability was promoted in the neutral pH regions where the charged particles were highly dispersed. In the low and high pH regions where the particles were coagulated, the foamability was considerably reduced. This behavior was explained by the fact that the large coagula were less easily captured by the bubbles and more easily detached from the interface (during the turbulent foaming conditions) than individual dispersed particles.

[Disintegration of visible light-cured composite resins caused by long-term water immersion].

PubMed

Hino, T; Arai, K

1989-05-01

The purpose of this study is to clarify a cause of disintegration of composite resins by long-term immersion in distilled water. Three kinds of visible light-cured composite resins (Heliosit, Plurafil Super and Visio Dispers) and one conventional composite resin (Clearfil F II) were prepared as the specimens with a 20 mm diameter and 1 mm thickness. These specimens were immersed in distilled water at 37 +/- 1 degree C for 3 years. These specimens were analysed and observed by a comprehensive multi analyzer and scanning electron microscope. The other hand residues in distilled water were analysed by infrared (IR) and nuclear magnetic resonance (NMR) spectrometers. The surface layer of all four composite resins showed signs of disintegration. The composite resins with abundant dissolved substances had disintegrated markedly, and such disintegration occurred deep inside the specimens. In IR and 1H-NMR spectra of dissolved substances, two visible light-cured composite resins (Heliosit and Plurafil Super) could be detected unreacted monomers, but one visible light-cured composite resin (Visio Dispers) and one conventional composite resin (Clearfil F II) could not be detected them. In 1H-NMR spectra of dissolved substances of all four composite resins, new signals not composed originally were observed. The progress of disintegration were demonstrated clearly. The dissolved substances were shown as the disintegrated substance between resin matrixs and silane coupling agents. It is suggested that the disintegration of composite resins by long-term water immersion is derived from hydrolysis.

Selective Adsorption of Pb(II) from Aqueous Solution by Triethylenetetramine-Grafted Polyacrylamide/Vermiculite

PubMed Central

Gu, Shiqing; Wang, Lan; Mao, Xinyou; Yang, Liping; Wang, Chuanyi

2018-01-01

Amine groups play significant roles in polymeric composites for heavy metals removal. However, generating a composite with a large number of functional and stable amine groups based on clay is still a challenge. In this work, a new amine-functionalized adsorbent based on acid-activated vermiculite (a-Verm) was prepared by organic modification of silane coupling agent as bridge, followed by in situ polymerization of acrylamide (AM) and further grafting of triethylene tetramine (TETA). The obtained polymeric composite g-PAM/OVerm was characterized by scanning electron microscope (SEM), energy dispersive spectrometer (EDS), Fourier transform infrared (FTIR), thermal analysis (TG/DTG), X-ray photoelectron spectroscopy (XPS) and Brunauer–Emmett–Teller (BET) analyses, confirming that amine groups were successfully grafted onto the surface of Verm. The efficacy g-PAM/OVerm for removing Pb(II) was tested. The adsorption equilibrium data on g-PAM/OVerm was in good accordance with the Langmuir adsorption isotherms, and the adsorption maximal value of Pb(II) was 219.4 mg·g−1. The adsorption kinetic data fit the pseudo-second-order kinetic model well. Additionally, g-PAM/OVerm has better selectivity for Pb(II) ion in comparison with Zn(II), Cd(II) and Cu(II) ions. The present work shows that g-PAM/OVerm holds great potential for removing Pb(II) from wastewater, and provides a new and efficient method for the removal of heavy metal ions from industrial wastewater. PMID:29597288

Long-term Bond Strength between Layering Indirect Composite Material and Zirconia Coated with Silicabased Ceramics.

PubMed

Fushiki, Ryosuke; Komine, Futoshi; Honda, Junichi; Kamio, Shingo; Blatz, Markus B; Matsumura, Hideo

2015-06-01

This study evaluated the long-term shear bond strength between an indirect composite material and a zirconia framework coated with silica-based ceramics, taking the effect of different primers into account. A total of 165 airborne-particle abraded zirconia disks were subjected to one of three pretreatments: no pretreatment (ZR-AB), airborne-particle abrasion of zirconia coated with feldspathic porcelain (ZR-PO-AB), and 9.5% hydrofluoric acid etching of zirconia coated with feldspathic porcelain (ZR-PO-HF). An indirect composite material (Estenia C&B) was then bonded to the zirconia disks after they were treated with one of the following primers: Clearfil Photo Bond (CPB), Clearfil Photo Bond with Clearfil Porcelain Bond Activator (CPB + Activator), Estenia Opaque Primer (EOP), Porcelain Liner M Liquid B (PLB), or no priming (CON, control group). Shear bond strength was tested after 100,000 thermocycles, and the data were analyzed using the Steel-Dwass U-test (α = 0.05). For ZR-PO-AB and ZR-PO-HF specimens, bond strength was highest in the CPB+Activator group (25.8 MPa and 22.4 MPa, respectively). Bond strengths were significantly lower for ZR-AB specimens in the CON and PLB groups and for ZR-PO-AB specimens in the CON, CPB, and EOP groups. Combined application of a hydrophobic phosphate monomer (MDP) and silane coupling agent enhanced the long-term bond strength of indirect composite material to a zirconia coated with silica-based ceramics.

Effects of different surface modification and contents on municipal solid waste incineration fly ash/epoxy composites.

PubMed

Goh, C K; Valavan, S E; Low, T K; Tang, L H

2016-12-01

Incineration fly ash, a waste from municipal solid waste incineration plant can be used to replace conventional filler as reinforcing filler to enhance the mechanical strength of a composite. Surface modification was performed on the incineration fly ash before mixing into the soft polymer matrix so as to improve interfacial bond of the filler and epoxy resin. In this study, detailed characterisation of mechanical, morphological and leaching behaviours of municipal solid waste incineration (MSWI) fly ash infused composite has been carried out. Flexural and tensile test was conducted to determine the effect on mechanical properties of the composite by varying the concentration of incineration fly ash filler added into polymer matrix and surface modification of incineration fly ash filler using silane coupling agent and colloidal mesoporous silica (CMS). The results indicated that composite infused with incineration fly ash filler surface treated with CMS shown improvement on the tensile and flexural strengths. In addition, SEM images showed that surface modification of incineration fly ash with colloidal mesoporous silica enhanced the interfacial bonding with polymer resin which explained the improvement of mechanical strength. Leaching test showed result of toxic metals such as Pb, Zn, Fe, Cu, Cr, Cd and Rb immobilised in the polymer matrix of the composite. Hence, the use of MSWI fly ash as reinforcing filler in the composite appears green and sustainable because this approach is a promising opportunity to substitute valuable raw material with MSWI fly ash. Copyright © 2016 Elsevier Ltd. All rights reserved.

Reaction of silanes in supercritical CO2 with TiO2 and Al2O3.

PubMed

Gu, Wei; Tripp, Carl P

2006-06-20

Infrared spectroscopy was used to investigate the reaction of silanes with TiO2 and Al2O3 using supercritical CO2 (Sc-CO2) as a solvent. It was found that contact of Sc-CO2 with TiO2 leads to partial removal of the water layer and to the formation of carbonate, bicarbonate, and carboxylate species on the surface. Although these carbonate species are weakly bound to the TiO2 surface and can be removed by a N2 purge, they poison the surface, resulting in a lower level of reaction of silanes with TiO2. Specifically, the amount of hexamethyldisilazane adsorbed on TiO2 is about 10% of the value obtained when the reaction is performed from the gas phase. This is not unique to TiO2, as the formation of carbonate species also occurs upon contact of Al2O3 with Sc-CO2 and this leads to a lower level of reaction with hexamethyldisilazane. This is in contrast to reactions of silanes on SiO2 where Sc-CO2 has several advantages over conventional gaseous or nonaqueous methods. As a result, caution needs to be applied when using Sc-CO2 as a solvent for silanization reactions on oxides other than SiO2.

Adhesive strength of total knee endoprostheses to bone cement - analysis of metallic and ceramic femoral components under worst-case conditions.

PubMed

Bergschmidt, Philipp; Dammer, Rebecca; Zietz, Carmen; Finze, Susanne; Mittelmeier, Wolfram; Bader, Rainer

2016-06-01

Evaluation of the adhesive strength of femoral components to the bone cement is a relevant parameter for predicting implant safety. In the present experimental study, three types of cemented femoral components (metallic, ceramic and silica/silane-layered ceramic) of the bicondylar Multigen Plus knee system, implanted on composite femora were analysed. A pull-off test with the femoral components was performed after different load and several cementing conditions (four groups and n=3 components of each metallic, ceramic and silica/silane-layered ceramic in each group). Pull-off forces were comparable for the metallic and the silica/silane-layered ceramic femoral components (mean 4769 N and 4298 N) under standard test condition, whereas uncoated ceramic femoral components showed reduced pull-off forces (mean 2322 N). Loading under worst-case conditions led to decreased adhesive strength by loosening of the interface implant and bone cement using uncoated metallic and ceramic femoral components, respectively. Silica/silane-coated ceramic components were stably fixed even under worst-case conditions. Loading under high flexion angles can induce interfacial tensile stress, which could promote early implant loosening. In conclusion, a silica/silane-coating layer on the femoral component increased their adhesive strength to bone cement. Thicker cement mantles (>2 mm) reduce adhesive strength of the femoral component and can increase the risk of cement break-off.

Hardness of model dental composites - the effect of filler volume fraction and silanation.

PubMed

McCabe, J F; Wassell, R W

1999-05-01

The relationship between structure and mechanical properties for dental composites has often proved difficult to determine due to the use of commercially available materials having a number of differences in composition i.e. different type of resin, different type of filler, etc. This makes a scientific study of any one variable such as filler content difficult if not impossible. In the current study it was the aim to test the hypothesis that hardness measurements of dental composites could be used to monitor the status of the resin-filler interface and to determine the efficacy of any particle silanation process. Ten model composites formulated from a single batch of resin and containing a common type of glass filler were formulated to contain varying amounts of filler. Some materials contained silanated filler, others contained unsilanated filler. Specimens were prepared and stored in water and hardness (Vickers') was determined at 24 h using loads of 50, 100, 200 and 300 g. Composites containing silanated fillers were significantly harder than materials containing unsilanated fillers. For unsilanated products hardness was independent of applied load and in this respect they behaved like homogeneous materials. For composites containing silanated fillers there was a marked increase in measured hardness as applied load was increased. This suggests that the hardness-load profile could be used to monitor the status of the resin-filler interface. Copyright 1999 Kluwer Academic Publishers

Functionalized sorbent for chemical separations and sequential forming process

DOEpatents

Fryxell, Glen E [Kennewick, WA; Zemanian, Thomas S [Richland, WA

2012-03-20

A highly functionalized sorbent and sequential process for making are disclosed. The sorbent includes organic short-length amino silanes and organic oligomeric polyfunctional amino silanes that are dispersed within pores of a porous support that form a 3-dimensional structure containing highly functionalized active binding sites for sorption of analytes.

Spatial Concentrations of Silicon Atoms in RF Discharges of Silane.

DTIC Science & Technology

1985-02-18

regions. These profiles were much more sensitive to plasma chemistry changes than profiles obtained from plasma emission. Experiments with nitrogen...addition demonstrated significant changes in the silicon atom profiles near the sheath boundary. Originator supplied keywords include: rf discharge, silane, plasma chemistry , silicon atom, laser-induced fluorescence.

Effect of hydrofluoric acid surface treatments on micro-shear bond strength of CAD/CAM ceramics

PubMed Central

Mokhtarpour, Faraneh; Alaghehmand, Homayoon; Khafri, Soraya

2017-01-01

Introduction Dental ceramics are appreciated as highly esthetic restorative materials that can simulate the appearance of natural dentition better than other materials. The aim of this study was to evaluate the effect of hydrofluoric acid concentration and etching time on micro-shear bond strength (μSBS) to IPS e.max CAD and Vita Mark II of a dual cured resin cement (Panavia F2.0). Methods This study was an experimental in vitro study, performed in the dental material research center of Babol University of Medical Sciences in 2016. Two hydrofluoric acid concentrations (5% and 10%) and three different etching times (20, 60 and 120 seconds) were used to etch the specimens respectively. A silane coupling agent (Clearfil porcelain activator) and priming and bonding agent (Clearfil SE bond) were used on the etched surfaces in accordance to the manufacturer’s instructions of use. Then resin cement was applied on the prepared ceramic surfaces and light cured. μSBS between resin cement and the porcelains were measured with a universal testing machine. Mode of failure was observed with 40× magnification by means of a Stereo microscope. Data were analyzed with ANOVA and independent-samples t-test and Chi-square tests. Results In both e.max and Vita Mark II groups, μSBS were not significantly different when different etching times (one-way ANOVA) and HF acid concentrations (Independent-samples t-test) were used (p>0.05), but the highest μSBS was shown in e.max specimens etched 60 s with 5% HF and Vita Mark II specimens etched 20 s with 10% HF. μSBS of e.max was significantly higher than Vita Mark II (p=0.00). Conclusion Best surface treatment for e.max and Vita Mark II ceramics is 20 s etch using 5 % hydrofluoric acid. PMID:29238488

Plexcitons: The Role of Oscillator Strengths and Spectral Widths in Determining Strong Coupling.

PubMed

Thomas, Reshmi; Thomas, Anoop; Pullanchery, Saranya; Joseph, Linta; Somasundaran, Sanoop Mambully; Swathi, Rotti Srinivasamurthy; Gray, Stephen K; Thomas, K George

2018-01-23

Strong coupling interactions between plasmon and exciton-based excitations have been proposed to be useful in the design of optoelectronic systems. However, the role of various optical parameters dictating the plasmon-exciton (plexciton) interactions is less understood. Herein, we propose an inequality for achieving strong coupling between plasmons and excitons through appropriate variation of their oscillator strengths and spectral widths. These aspects are found to be consistent with experiments on two sets of free-standing plexcitonic systems obtained by (i) linking fluorescein isothiocyanate on Ag nanoparticles of varying sizes through silane coupling and (ii) electrostatic binding of cyanine dyes on polystyrenesulfonate-coated Au nanorods of varying aspect ratios. Being covalently linked on Ag nanoparticles, fluorescein isothiocyanate remains in monomeric state, and its high oscillator strength and narrow spectral width enable us to approach the strong coupling limit. In contrast, in the presence of polystyrenesulfonate, monomeric forms of cyanine dyes exist in equilibrium with their aggregates: Coupling is not observed for monomers and H-aggregates whose optical parameters are unfavorable. The large aggregation number, narrow spectral width, and extremely high oscillator strength of J-aggregates of cyanines permit effective delocalization of excitons along the linear assembly of chromophores, which in turn leads to efficient coupling with the plasmons. Further, the results obtained from experiments and theoretical models are jointly employed to describe the plexcitonic states, estimate the coupling strengths, and rationalize the dispersion curves. The experimental results and the theoretical analysis presented here portray a way forward to the rational design of plexcitonic systems attaining the strong coupling limits.

Heterogeneous decomposition of silane in a fixed bed reactor

NASA Technical Reports Server (NTRS)

Iya, S. K.; Flagella, R. N.; Dipaolo, F. S.

1982-01-01

Heterogeneous decomposition of silane in a fluidized bed offers an attractive route for the low-cost production of silicon for photovoltaic application. To obtain design data for a fluid bed silane pyrolysis reactor, deposition experiments were conducted in a small-scale fixed bed apparatus. Data on the decomposition mode, plating rate, and deposition morphology were obtained in the temperature range 600-900 C. Conditions favorable for heterogeneous decomposition with good deposition morphology were identified. The kinetic rate data showed the reaction to be first order with an activation energy of 38.8 kcal/mol, which agrees well with work done by others. The results are promising for the development of an economically attractive fluid bed process.

Studies on silane to 70 GPa

NASA Astrophysics Data System (ADS)

Narayana, C.; Greene, R. G.; Ruoff, A. L.

2008-07-01

Raman and x-ray diffraction studies were made on silane in the diamond anvil cell using three different gaskets, stainless steel, tungsten and rhenium. The structure existing between 10 and 27 GPa is well characterized by the monoclinic space group P21c (#14). While the Gibbs free energy of formation of silane is positive at one atmosphere, it is calculated from the equation of state of silane and its reactants that this becomes negative near 4 GPa and remains negative until 13 GPa and then becomes positive again. At about 27 GPa, where quasi-quantum mechanical calculations suggest there should be a transformation from 4-fold to 6-fold (or even higher), the sample turns black. The Raman modes seize to exist beyond 30 GPa after showing softening above 25 GPa. At higher pressures it turns silvery. The gaskets play a different role as will be discussed. The sample brought back from 70 GPa contains amorphous Si (with attached hydrogen) as well as crystalline silicon. The lowest free energy system at high pressure is the decomposed reactants as observed.

Comparative Study of Solution Phase and Vapor Phase Deposition of Aminosilanes on Silicon Dioxide Surfaces

PubMed Central

Yadav, Amrita R.; Sriram, Rashmi; Carter, Jared A.; Miller, Benjamin L.

2014-01-01

The uniformity of aminosilane layers typically used for the modification of hydroxyl bearing surfaces such as silicon dioxide is critical for a wide variety of applications, including biosensors. However, in spite of many studies that have been undertaken on surface silanization, there remains a paucity of easy-to-implement deposition methods reproducibly yielding smooth aminosilane monolayers. In this study, solution- and vapor-phase deposition methods for three aminoalkoxysilanes differing in the number of reactive groups (3-aminopropyl triethoxysilane (APTES), 3-aminopropyl methyl diethoxysilane (APMDES) and 3-aminopropyl dimethyl ethoxysilane (APDMES)) were assessed with the aim of identifying methods that yield highly uniform and reproducible silane layers that are resistant to minor procedural variations. Silane film quality was characterized based on measured thickness, hydrophilicity and surface roughness. Additionally, hydrolytic stability of the films was assessed via these thickness and contact angle values following desorption in water. We found that two simple solution-phase methods, an aqueous deposition of APTES and a toluene based deposition of APDMES, yielded high quality silane layers that exhibit comparable characteristics to those deposited via vapor-phase methods. PMID:24411379

A novel combination of silane-coated silica colloid with hybrid RNA extraction protocol and RNA enrichment for downstream applications of spermatozoal RNA.

PubMed

Vijayalakshmy, K; Kumar, P; Virmani, M; Pawaria, S; Lalaji, N S; Sharma, P; Rajendran, R; Yadav, P S; Kumar, D

2018-05-14

Spermatozoa are specialised cells with low RNA content as compared to somatic cells. The suitable sperm RNA extraction and enrichment protocols for downstream applications are available for human, cattle, stallion and mouse but not for buffalo spermatozoa. Therefore, the present work was conducted to find out suitable colloidal solution for sperm purification and appropriate protocol for sperm RNA extraction and enrichment/amplification of RNA. For purification, we used PVP-coated silica colloidal solution (PVP-Si), silane-coated silica colloidal solution (Silane-Si) and iodixanol. Sperm recovery rate, total sperm motility and progressive sperm motility were significantly improved after separation by Silane-Si and iodixanol compared to PVA-Si method. The combined guanidinium thiocyanate-phenol-chloroform (GTPC) with silica matrix (SM)-based RNA extraction yielded more quantity of RNA in compared to individual method. The hybrid of SM and GTPC into a single protocol yielded 360-450 ng RNA from 30 million buffalo spermatozoa. For the first time, we adopted new way to enrich sperm RNA that increased the RNA concentration 4-5 times that was sufficient for downstream applications. The linear amplification of sperm RNA increased RNA concentration around 27-45 times. In summary, Silane-Si colloid for sperm separation, hybrid SM and GTPC protocol for sperm RNA extraction followed by enrichment or amplification of RNA was found suitable for high-throughput analyses of buffalo sperm RNA. © 2018 Blackwell Verlag GmbH.

Effects of age condition on the distribution and integrity of inorganic fillers in dental resin composites.

PubMed

D'Alpino, Paulo Henrique Perlatti; Svizero, Nádia da Rocha; Bim Júnior, Odair; Valduga, Claudete Justina; Graeff, Carlos Frederico de Oliveira; Sauro, Salvatore

2016-06-01

The aim of this study is to evaluate the distribution of the filler size along with the zeta potential, and the integrity of silane-bonded filler surface in different types of restorative dental composites as a function of the material age condition. Filtek P60 (hybrid composite), Filtek Z250 (small-particle filled composite), Filtek Z350XT (nanofilled composite), and Filtek Silorane (silorane composite) (3M ESPE) were tested at different stage condition (i.e., fresh/new, aged, and expired). Composites were submitted to an accelerated aging protocol (Arrhenius model). Specimens were obtained by first diluting each composite specimen in ethanol and then dispersed in potassium chloride solution (0.001 mol%). Composite fillers were characterized for their zeta potential, mean particle size, size distribution, via poly-dispersion dynamic light scattering. The integrity of the silane-bonded surface of the fillers was characterized by FTIR. The material age influenced significantly the outcomes; Zeta potential, filler characteristics, and silane integrity varied both after aging and expiration. Silorane presented the broadest filler distribution and lowest zeta potential. Nanofilled and silorane composites exhibited decreased peak intensities in the FTIR analysis, indicating a deficiency of the silane integrity after aging or expiry time. Regardless to the material condition, the hybrid and the small-particle-filled composites were more stable overtime as no significant alteration in filler size distribution, diameter, and zeta potential occurred. A deficiency in the silane integrity in the nanofilled and silorane composites seems to be affected by the material stage condition. The materials conditions tested in this study influenced the filler size distribution, the zeta potential, and integrity of the silane adsorbed on fillers in the nanofilled and silorane composites. Thus, this may result in a decrease of the clinical performance of aforementioned composites, in particular, if these are used after inappropriate storage conditions.

Silane-based coatings on the pyrite for remediation of acid mine drainage.

PubMed

Diao, Zenghui; Shi, Taihong; Wang, Shizhong; Huang, Xiongfei; Zhang, Tao; Tang, Yetao; Zhang, Xiaying; Qiu, Rongliang

2013-09-01

Acid mine drainage (AMD) resulting from the oxidation of pyrite and other metal sulfides has caused significant environmental problems, including acidification of rivers and streams as well as leaching of toxic metals. With the goal of controlling AMD at the source, we evaluated the potential of tetraethylorthosilicate (TEOS) and n-propyltrimethoxysilane (NPS) coatings to suppress pyrite oxidation. The release of total Fe and SO4(-2) from uncoated and coated pyrite in the presence of a chemical oxidizing agent (H2O2) or iron-oxidizing bacteria (Acidithiobacillus ferrooxidans) was measured. Results showed that TEOS- and NPS-based coatings reduced chemical oxidation of pyrite by as much as 59 and 96% (based on Fe release), respectively, while biological oxidation of pyrite was reduced by 69 and 95%, respectively. These results were attributed to the formation of a dense network of Fe-O-Si and Si-O-Si bonds on the pyrite surface that limited permeation of oxygen, water, and bacteria. Compared with results for TEOS-coated pyrite, higher pH and lower concentrations of total Fe and SO4(-2) were observed for oxidation of NPS-coated pyrite, which was attributed to its crack-free morphology and the presence of hydrophobic groups on the NPS-based coating surface. The silane-based NPS coating was shown to be highly effective in suppressing pyrite oxidation, making it a promising alternative for remediation of AMD at its source. Copyright © 2013 Elsevier Ltd. All rights reserved.

Comparative assessment of different recycling methods of orthodontic brackets for clinical use.

PubMed

de Oliveira Correia, Ayla M; de Souza Matos, Felipe; Pilli Jóias, Renata; de Mello Rode, Sigmar; Cesar, Paulo F; Paranhos, Luiz R

2017-06-01

This study aimed to assess bond strength of the resin/bracket interface, under in-vitro shear stress, of metal brackets recycled by different clinical protocols. Sixty stainless steel orthodontic brackets were bonded on acrylic resin. The Transbond XT™ resin was applied at the base of the bracket aided by a matrix, obtaining 1 mm of thickness, and photoactivated with a LED device (40 s; 500 mW/cm2). Samples were randomly divided into four groups (N.=15) according to the reconditioning/recycling protocol: aluminum oxide (AO) 90 µm; hydrofluoric acid 60 s (HA60); hydrofluoric acid 120 s (HA120); hydrofluoric acid 60 s + silane (HA60S). After recycling, the resin was applied at the base of the bracket for shear testing in a universal testing machine (0.5 mm/min). After reconditioning/recycling, the surfaces were analyzed by Scanning Electron Microscopy. Data obtained after the shear test were subjected to ANOVA and Tukey's test (P<0.05). The AO group presented higher values of shear bond strength compared to the other reconditioning/recycling protocols (P<0.05). The HA120 and HA60S groups presented statistically similar results, but HA120 presented strength below the recommended limit. The recycling technique by aluminum oxide sandblasting was more effective for reconditioning orthodontic brackets when compared to the other protocols. The reconditioning technique with 10% hydrofluoric acid followed by the application of silane bonding agent may be used as an alternative protocol.

Modeling of the silane FBR system

NASA Technical Reports Server (NTRS)

Dudokovic, M. P.; Ramachandran, P. A.; Lai, S.

1984-01-01

Development of a mathematical model for fluidized bed pyrolysis of silane that relates production rate and product properties (size, size distribution, presence or absence of fines) with bed size and operating conditions (temperature, feed concentration, flow rate, seed size, etc.) and development of user oriented algorithm for the model are considered. A parameter sensitivity study of the model was also developed.

Profile extrusion and mechanical properties of crosslinked wood–thermoplastic composites

Treesearch

Magnus Bengtsson; Kristiina Oksman; Stark Nicole M.

2006-01-01

Challenges for wood-thermoplastic composites to be utilized in structural applications are to lower product weight and to improve the long-term load performance. Silane crosslinking of the composites is one way to reduce the creep during long-term loading and to improve the mechanical properties. In this study, silane crosslinked wood-polyethylene composites were...

Fluoroalkyl silane modified silicone rubber/nanoparticle composite: a super durable, robust superhydrophobic fabric coating.

PubMed

Zhou, Hua; Wang, Hongxia; Niu, Haitao; Gestos, Adrian; Wang, Xungai; Lin, Tong

2012-05-08

A superhydrophobic fabric coating made of a crosslinked polydimethylsiloxane elastomer, containing well-dispersed hydrophobic silica nanoparticles and fluorinated alkyl silane, shows remarkable durability against repeated machine washes, severe abrasion, strong acid or base, boiling water or beverages and excellent stain resistance. Copyright © 2012 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Improvement of thermal conductivities for silicone nanocomposite via incorporating poly(γ-methacryloxypropyltrimethoxy silane) grafted graphene fillers

NASA Astrophysics Data System (ADS)

Chen, Tian; Liu, Bo

2018-02-01

The proposed grafting polymerization of γ-methacryloxypropyltrimethoxy silane was performed to functionalize graphene, aiming to fabricate functionalized graphene/silicone with excellent thermal conductivities. The surface morphology and element content of poly(γ-methacryloxypropyltrimethoxy silane) grafted reduced graphene oxide (g-RGO) was characterized by Atomic force microscope (AFM) and X-ray photoelectron spectroscopy (XPS). The usage of g-RGO was benefit for improving the thermal conductivity of silicone (SI). The g-RGO/SI (2 wt% filler) had thermal conductivity of 1.31 W·m-1·K-1 and thermal diffusivity of 1.08 mm2·s-1 (increased by 620% compared to that of SI), which held potential for electronic packaging materials and micro-electro-mechanical systems apparatus.

Fluorination of Boron-Doped Diamond Film Electrodes for Minimization of Perchlorate Formation.

PubMed

Gayen, Pralay; Chaplin, Brian P

2017-08-23

This research investigated the effects of surface fluorination on both rates of organic compound oxidation (phenol and terephthalic acid (TA)) and ClO 4 - formation at boron-doped diamond (BDD) film anodes at 22 °C. Different fluorination methods (i.e., electrochemical oxidation with perfluorooctanoic acid (PFOA), radio frequency plasma, and silanization) were used to incorporate fluorinated moieties on the BDD surface, which was confirmed by X-ray photoelectron spectroscopy (XPS). The silanization method was found to be the most effective fluorination method using a 1H,1H,2H,2H-perfluorodecyltrichlorosilane precursor to form a self-assembled monolayer (SAM) on the oxygenated BDD surface. The ClO 4 - formation decreased from rates of 0.45 ± 0.03 mmol m -2 min -1 during 1 mM NaClO 3 oxidation and 0.28 ± 0.01 mmol m -2 min -1 during 10 mM NaCl oxidation on the BDD electrode to below detectable levels (<0.12 μmoles m -2 min -1 ) for the BDD electrode functionalized by a 1H,1H,2H,2H-perfluorodecyltrichlorosilane SAM. These decreases in rates corresponded to 99.94 and 99.85% decreases in selectivity for ClO 4 - formation during the electrolysis of 10 mM NaCl and 1 mM NaClO 3 electrolytes, respectively. By contrast, the oxidation rates of phenol were reduced by only 16.3% in the NaCl electrolyte and 61% in a nonreactive 0.1 M KH 2 PO 4 electrolyte. Cyclic voltammetry with Fe(CN) 6 3-/4- and Fe 3+/2+ redox couples indicated that the long fluorinated chains created a blocking layer on the BDD surface that inhibited charge transfer via steric hindrance and hydrophobic effects. The surface coverages and thicknesses of the fluorinated films controlled the charge transfer rates, which was confirmed by estimates of film thicknesses using XPS and density functional theory simulations. The aliphatic silanized electrode also showed very high stability during OH • production. Perchlorate formation rates were below the detection limit (<0.12 μmoles m -2 min -1 ) for up to 10 consecutive NaClO 3 oxidation experiments.

[Influence of different porcelain surface treatment method on the bonding of metal brackets to porcelain].

PubMed

Fan, Cun-Hui; Chen, Jie; Liu, Xin-Qiang; Ma, Xin

2005-08-01

To investigate the influence of different porcelain surface treatment methods on the shear bond strength of metal brackets bonded to porcelain. 80 porcelain facets were divided randomly into two groups according to different adhesive material that was used to bond metal brackets. Adhesive material were Jing-Jin enamel adhesive and light-cured composite resin. Each group was further divided into 4 subgroups according to different surface treatment methods, which were acid etching with 37% phosphoric acid (H3PO4), acid etching with 9.6% hydrofluoric acid (HF), deglazing by grinding and silanating the porcelain surface. All specimens were stored in 37 degrees C water for 24 hours and then the shear bond strength and the porcelain fracture after debonding was determined. The porcelain surfaces after HF etching, H3PO4 etching and deglazing by grinding were examined by scanning electron microscopy respectively. The shear bond strengths in the HF etching groups, the deglazing groups and the silanating groups were much greater than that in the phosphoric etching groups (P < 0.01). Adequate orthodontic bonding strength was achieved both when bonded with light-cured composite resin after deglazing by grinding and when bonded with either of these adhesives after HF etching or surface silanating. There were no differences in the rates of porcelain fractures among groups (P > 0.05). HF etching, deglazing by grinding and silanating can all increase the shear bond strength between metal bracket and porcelain. Surface silanating of porcelain is a better surface treatment when metal brackets bonded to porcelain.

Comparison of the Microtensile Bond Strength of a Polyetherketoneketone (PEKK) Tooth Post Cemented with Various Surface Treatments and Various Resin Cements.

PubMed

Song, Chan-Hong; Choi, Jae-Won; Jeon, Young-Chan; Jeong, Chang-Mo; Lee, So-Hyoun; Kang, Eun-Sook; Yun, Mi-Jung; Huh, Jung-Bo

2018-05-29

The aim of this in-vitro research was to evaluate the microtensile bond strength in the newly introduced PEKK tooth post with various surface treatments and resin cements. A fiberglass tooth post was included in order to compare it with PEKK as a possible post material. The microtensile bond strengths of the fiberglass post (FRC Postec Plus) and the PEKK post (Pekkton ® ) were tested using three kinds of self-adhesive resin cements (G-CEM LinkAce, Multilink Speed, and RelyX U200) and one self-etching resin cement (PANAVIA F2.0). The surface treatments of the fiberglass posts were processed according to the manufacturer's recommendations (F1, application of 37% phosphoric acid etching gel and silanization). For the PEKK post groups, various surface treatments were performed like no surface treatment (P1), sandblasting (P2), silica-coating and silanization (P3), and sandblasting with a composite primer (P4). In the surface treatment, PEKK posts with silica coating and silane treatment (P3) showed a significantly higher microtensile bond strength (mean MPa: 18.09, p < 0.05). The highest microtensile bond strength was shown when the PEKK posts were treated with a silica coating and silane treatment and cemented with RelyX U200 (mean MPa: 22.22). The PEKK posts with surface treatments of silica-coating and silanization or sandblasting displayed superior microtensile bond strengths (mean MPa: 18.09 and 16.25, respectively) compared to the conventional fiberglass posts (mean MPa: 14.93, p < 0.05).

Nano-thermometers with thermo-sensitive polymer grafted USPIOs behaving as positive contrast agents in low-field MRI

NASA Astrophysics Data System (ADS)

Hannecart, Adeline; Stanicki, Dimitri; Vander Elst, Luce; Muller, Robert N.; Lecommandoux, Sébastien; Thévenot, Julie; Bonduelle, Colin; Trotier, Aurélien; Massot, Philippe; Miraux, Sylvain; Sandre, Olivier; Laurent, Sophie

2015-02-01

Two commercial statistical copolymers of ethylene oxide and propylene oxide, Jeffamine® M-2005 (PEO5-st-PPO37) and M-2070 (PEO46-st-PPO13), exhibiting lower critical solution temperature (LCST) in water, were grafted onto the surface of ultra-small superparamagnetic iron oxide nanoparticles (USPIOs) using silanization and amide-bond coupling reactions. The LCSTs of the polymers in solution were measured by dynamic light scattering (DLS) and nuclear magnetic resonance (NMR). In accordance with the compositions of EO vs. PO, the transition temperature was measured to be 22 +/- 2 °C for M-2005 by both DLS and NMR, while the LCST was much higher, 52 +/- 2 °C, for M-2070 (a second transition was also detected above 80 °C by NMR in that case, ascribed to the full dehydration of chains at the molecular level). The resulting polymer-grafted USPIOs exhibit a temperature-responsive colloidal behaviour, their surface reversibly changing from hydrophilic below LCST to hydrophobic above it. This phenomenon was utilised to design thermo-sensitive contrast agents for MRI. Transverse relaxivities (r2) of the USPIO@PEO5-st-PPO37 core-shell nanoparticles were measured at 8.25, 20, 60, and 300 MHz. Nuclear magnetic resonance dispersion (NMRD) profiles, giving longitudinal relaxivities (r1) between 0.01 and 60 MHz, were acquired at temperatures ranging from 15 to 50 °C. For all tested frequencies except 300 MHz, both r1 and r2 decrease with temperature and show an inflection point at 25 °C, near the LCST. To illustrate the interest of such polymer-coated USPIOs for MRI thermometry, sample tubes were imaged on both low-field (8.25 MHz/0.194 Tesla) and high-field (300 MHz/7.05 Tesla) MRI scanners with either T1- or T2*-weighted spin echo sequences. The positive contrast on low-field MR images and the perfect linearity of the signal with a T2*-weighted sequence over the entire temperature range 15-50 °C render these LCST polymer coated USPIOs interesting positive contrast agents, also working as ``nano-thermometers''.Two commercial statistical copolymers of ethylene oxide and propylene oxide, Jeffamine® M-2005 (PEO5-st-PPO37) and M-2070 (PEO46-st-PPO13), exhibiting lower critical solution temperature (LCST) in water, were grafted onto the surface of ultra-small superparamagnetic iron oxide nanoparticles (USPIOs) using silanization and amide-bond coupling reactions. The LCSTs of the polymers in solution were measured by dynamic light scattering (DLS) and nuclear magnetic resonance (NMR). In accordance with the compositions of EO vs. PO, the transition temperature was measured to be 22 +/- 2 °C for M-2005 by both DLS and NMR, while the LCST was much higher, 52 +/- 2 °C, for M-2070 (a second transition was also detected above 80 °C by NMR in that case, ascribed to the full dehydration of chains at the molecular level). The resulting polymer-grafted USPIOs exhibit a temperature-responsive colloidal behaviour, their surface reversibly changing from hydrophilic below LCST to hydrophobic above it. This phenomenon was utilised to design thermo-sensitive contrast agents for MRI. Transverse relaxivities (r2) of the USPIO@PEO5-st-PPO37 core-shell nanoparticles were measured at 8.25, 20, 60, and 300 MHz. Nuclear magnetic resonance dispersion (NMRD) profiles, giving longitudinal relaxivities (r1) between 0.01 and 60 MHz, were acquired at temperatures ranging from 15 to 50 °C. For all tested frequencies except 300 MHz, both r1 and r2 decrease with temperature and show an inflection point at 25 °C, near the LCST. To illustrate the interest of such polymer-coated USPIOs for MRI thermometry, sample tubes were imaged on both low-field (8.25 MHz/0.194 Tesla) and high-field (300 MHz/7.05 Tesla) MRI scanners with either T1- or T2*-weighted spin echo sequences. The positive contrast on low-field MR images and the perfect linearity of the signal with a T2*-weighted sequence over the entire temperature range 15-50 °C render these LCST polymer coated USPIOs interesting positive contrast agents, also working as ``nano-thermometers''. Electronic supplementary information (ESI) available: Fig. S1: (a) 1H NMR spectra vs. temperature for Jeffamine® M-2005, (b) and M-2070 at 30 mg mL-1 in D2O; Fig. S2: FT-IR spectra of iron oxide nanoparticles (a) just after coprecipitation and (b) after coating with TEPSA; Fig. S3: Thermogravimetric analyses (TGA) of USPIOs silanized by TEPSA (red curve) and after coupling with Jeffamine® M-2005 (green curve) and M-2070 (blue curve); Fig. S4: FT-IR spectra (a) of the difference between the normalised spectra of USPIOs coated with TEPSA before and after grafting of Jeffamine® M-2005 and (b) of Jeffamine® M-2005 alone; Fig. S5: FT-IR spectra (a) of the difference between the normalised spectra of USPIOs coated with TEPSA before and after grafting of Jeffamine® M-2070, and (b) of Jeffamine® M-2070 alone; Fig. S6: NMRD profiles of the longitudinal relaxivity vs. proton Larmor frequency for (a) TEPSA-coated USPIOs and (b) USPIOs grafted with Jeffamine® M-2070 as a function of temperature; Fig. S7: (a) Outer sphere radius RNMR and saturation magnetisation MSvs. temperature for USPIOs coated with Jeffamine® M-2070 (green markers) and TEPSA only (purple markers); Fig. S8: longitudinal r1 and transverse r2 relaxivities of USPIOs grafted with Jeffamine® M-2005, normalised by the corresponding r1 or r2 of TEPSA-coated USPIOs, as a function of temperature ranging from 10 to 50 °C, for clinically relevant frequencies: 8.25, 20, 60, and 300 MHz. Movie 1: 8.25 MHz MR image of Jeffamine® M-2005 NP-coated and NP-TEPSA control tubes during a temperature cycle with the T1-weighted sequence. Movie 2: 8.25 MHz MR image of Jeffamine® M-2005 NP-coated and NP-TEPSA control tubes during a temperature cycle with the T2*-weighted sequence. See DOI: 10.1039/c4nr07064j

Collective motion patterns of swarms with delay coupling: Theory and experiment.

PubMed

Szwaykowska, Klementyna; Schwartz, Ira B; Mier-Y-Teran Romero, Luis; Heckman, Christoffer R; Mox, Dan; Hsieh, M Ani

2016-03-01

The formation of coherent patterns in swarms of interacting self-propelled autonomous agents is a subject of great interest in a wide range of application areas, ranging from engineering and physics to biology. In this paper, we model and experimentally realize a mixed-reality large-scale swarm of delay-coupled agents. The coupling term is modeled as a delayed communication relay of position. Our analyses, assuming agents communicating over an Erdös-Renyi network, demonstrate the existence of stable coherent patterns that can be achieved only with delay coupling and that are robust to decreasing network connectivity and heterogeneity in agent dynamics. We also show how the bifurcation structure for emergence of different patterns changes with heterogeneity in agent acceleration capabilities and limited connectivity in the network as a function of coupling strength and delay. Our results are verified through simulation as well as preliminary experimental results of delay-induced pattern formation in a mixed-reality swarm.

Collective motion patterns of swarms with delay coupling: Theory and experiment

NASA Astrophysics Data System (ADS)

Szwaykowska, Klementyna; Schwartz, Ira B.; Mier-y-Teran Romero, Luis; Heckman, Christoffer R.; Mox, Dan; Hsieh, M. Ani

2016-03-01

The formation of coherent patterns in swarms of interacting self-propelled autonomous agents is a subject of great interest in a wide range of application areas, ranging from engineering and physics to biology. In this paper, we model and experimentally realize a mixed-reality large-scale swarm of delay-coupled agents. The coupling term is modeled as a delayed communication relay of position. Our analyses, assuming agents communicating over an Erdös-Renyi network, demonstrate the existence of stable coherent patterns that can be achieved only with delay coupling and that are robust to decreasing network connectivity and heterogeneity in agent dynamics. We also show how the bifurcation structure for emergence of different patterns changes with heterogeneity in agent acceleration capabilities and limited connectivity in the network as a function of coupling strength and delay. Our results are verified through simulation as well as preliminary experimental results of delay-induced pattern formation in a mixed-reality swarm.

Development of high temperature resistant graphite fiber coupling agents

NASA Technical Reports Server (NTRS)

Griffin, R. N.

1975-01-01

Surface treatments were investigated as potential coupling agents to improve the elevated temperature shear strength retention of polyimide/graphite and polyphenylquinoxaline/graphite composites. The potential coupling agents were evaluated by fiber strand tensile tests, fiber and composite weight losses at 533 and 588K, and by interlaminar shear strength retention at 533 and 588K. The two surface treatments selected for more extensive evaluation were a coating of Ventromer T-1, a complex organometallic reaction product of titanium tetrachloride and trimethyl borate, and a polyphenylquinoxaline (PPQ) sizing which was pyrolyzed in nitrogen to form a carbonaceous layer on the fiber. Pyrolyzed polyphenylquinoxaline is a satisfactory coupling agent for polyimide/Thornel 300 graphite fiber composites. During 1000 hours aging at 588K such composites lose a little over half their transverse tensile strength, and suffer a slight loss in flexural modulus. No degradation of flexural strength or interlaminar shear strength occured during 1000 hours aging at 588K. None of the coupling agents examined had a markedly beneficial effect with polyphenylquinoxaline composites.

Boron-carbon-silicon polymers and ceramic and a process for the production thereof

NASA Technical Reports Server (NTRS)

Riccitiello, Salvatore (Inventor); Hsu, Ming-Ta (Inventor); Chen, Timothy S. (Inventor)

1992-01-01

The present invention relates to a process for the production of an organoborosilicon preceramic polymer. The polymer is prepared by the reaction of vinylsilane or vinlymethylsilanes (acetylene)silane or acetylene alkyl silanes and borane or borane derivatives. The prepolymer form is pyrolyzed to produce a ceramic article useful in high temperature (e.g., aerospace) or extreme environmental applications.

Effect of Silver or Copper Nanoparticles-Dispersed Silane Coatings on Biofilm Formation in Cooling Water Systems

PubMed Central

Ogawa, Akiko; Kanematsu, Hideyuki; Sano, Katsuhiko; Sakai, Yoshiyuki; Ishida, Kunimitsu; Beech, Iwona B.; Suzuki, Osamu; Tanaka, Toshihiro

2016-01-01

Biofouling often occurs in cooling water systems, resulting in the reduction of heat exchange efficiency and corrosion of the cooling pipes, which raises the running costs. Therefore, controlling biofouling is very important. To regulate biofouling, we focus on the formation of biofilm, which is the early step of biofouling. In this study, we investigated whether silver or copper nanoparticles-dispersed silane coatings inhibited biofilm formation in cooling systems. We developed a closed laboratory biofilm reactor as a model of a cooling pipe and used seawater as a model for cooling water. Silver or copper nanoparticles-dispersed silane coating (Ag coating and Cu coating) coupons were soaked in seawater, and the seawater was circulated in the laboratory biofilm reactor for several days to create biofilms. Three-dimensional images of the surface showed that sea-island-like structures were formed on silane coatings and low concentration Cu coating, whereas nothing was formed on high concentration Cu coatings and low concentration Ag coating. The sea-island-like structures were analyzed by Raman spectroscopy to estimate the components of the biofilm. We found that both the Cu coating and Ag coating were effective methods to inhibit biofilm formation in cooling pipes. PMID:28773758

Hybrid electrolytes incorporated with dandelion-like silane-Al2O3 nanoparticles for high-safety high-voltage lithium ion batteries

NASA Astrophysics Data System (ADS)

Xu, Hewei; Shi, Junli; Hu, Guosheng; He, Ying; Xia, Yonggao; Yin, Shanshan; Liu, Zhaoping

2018-07-01

One of the crucial challenge for developing high safety and high voltage lithium ion batteries is to find a reliable electrolyte system. In this work, we report a kind of hybrid electrolytes, which are used for high-voltage lithium ion batteries and are expected to be able to effectively enhance the battery safety. The hybrid electrolytes are obtained by incorporating silane-Al2O3 (Al2O3-ST) into liquid electrolyte, which combines the merits of both solid electrolyte and liquid electrolyte. The Al2O3-ST nanoparticles help to increase lithium-ion transference number and to enhance battery safety, while liquid electrolyte contributes to high ionic conductivity. The cycling stability and rate capacity of LiNi0.5Mn1.5O4/Li batteries are improved by using the hybrid electrolytes. Nail-penetration tests indicate that LiNi0.6Mn0.2Co0.2O2/graphite battery with hybrid electrolyte owns obviously enhanced safety than that using traditional liquid electrolyte. This work provides new insight on electrolyte design for high-safety high-voltage lithium ion batteries.

The influence of silanisation on the mechanical and degradation behaviour of PLGA/HA composites.

PubMed

Naik, Ashutosh; Best, Serena M; Cameron, Ruth E

2015-03-01

This study investigates the influence of silanisation on the mechanical and degradation behaviour of PLGA/HA composites. Three different silanes (mercaptopropyl trimethoxy silane (MPTMS), aminopropyl trimethoxy silane (APTMS) and aminopropyltriethoxy silane (APTES)) were applied to HA substrates in order to study the effect of head group (which binds to the polymer) and tail group (which binds to the surface hydroxyl groups in HA). A composite of hydroxyapatite (HA) and poly(d,l lactide-co-glycolide (50:50)) (PLGA) was investigated. The influence of concentration, the reaction time, drying temperature and substrate surface on silanisation was examined. TGA was used to detect the degree of silanisation. HA with MPTMS (1wt.% MPTMS with reaction time of 1h) was used as filler in PLGA-30wt.% HA composites for an in-vitro degradation study carried out in PBS. In addition, the mechanical properties of the composites were studied. Silanisation affects the properties of the composite by improving the bonding at the interface and hence it was found to influence the plastic mechanical properties rather than the elastic mechanical properties or the degradation profile of the composite. Copyright © 2014. Published by Elsevier B.V.

Comparative study of solution-phase and vapor-phase deposition of aminosilanes on silicon dioxide surfaces.

PubMed

Yadav, Amrita R; Sriram, Rashmi; Carter, Jared A; Miller, Benjamin L

2014-02-01

The uniformity of aminosilane layers typically used for the modification of hydroxyl bearing surfaces such as silicon dioxide is critical for a wide variety of applications, including biosensors. However, in spite of many studies that have been undertaken on surface silanization, there remains a paucity of easy-to-implement deposition methods reproducibly yielding smooth aminosilane monolayers. In this study, solution- and vapor-phase deposition methods for three aminoalkoxysilanes differing in the number of reactive groups (3-aminopropyl triethoxysilane (APTES), 3-aminopropyl methyl diethoxysilane (APMDES) and 3-aminopropyl dimethyl ethoxysilane (APDMES)) were assessed with the aim of identifying methods that yield highly uniform and reproducible silane layers that are resistant to minor procedural variations. Silane film quality was characterized based on measured thickness, hydrophilicity and surface roughness. Additionally, hydrolytic stability of the films was assessed via these thickness and contact angle values following desorption in water. We found that two simple solution-phase methods, an aqueous deposition of APTES and a toluene based deposition of APDMES, yielded high quality silane layers that exhibit comparable characteristics to those deposited via vapor-phase methods. Copyright © 2013 Elsevier B.V. All rights reserved.

Chemically-modified cellulose paper as a microstructured catalytic reactor.

PubMed

Koga, Hirotaka; Kitaoka, Takuya; Isogai, Akira

2015-01-15

We discuss the successful use of chemically-modified cellulose paper as a microstructured catalytic reactor for the production of useful chemicals. The chemical modification of cellulose paper was achieved using a silane-coupling technique. Amine-modified paper was directly used as a base catalyst for the Knoevenagel condensation reaction. Methacrylate-modified paper was used for the immobilization of lipase and then in nonaqueous transesterification processes. These catalytic paper materials offer high reaction efficiencies and have excellent practical properties. We suggest that the paper-specific interconnected microstructure with pulp fiber networks provides fast mixing of the reactants and efficient transport of the reactants to the catalytically-active sites. This concept is expected to be a promising route to green and sustainable chemistry.

A facile method to modify bentonite nanoclay with silane

NASA Astrophysics Data System (ADS)

Abeywardena, Sujani B. Y.; Perera, Srimala; Nalin de Silva, K. M.; Tissera, Nadeeka P.

2017-07-01

Immobilization of smectite clay onto a desirable surface has received much attention, since its nanospace can be utilized for many applications in material science. Here, we present an efficient method to functionalize surface of bentonite nanoclay (BNC) through the grafting of 3-aminotriethoxysilane (APTES). Infrared spectroscopy and elemental analysis confirmed the presence of organic chains and amine groups in modified nanoclay. XRD analysis confirmed grafting of APTES on the surface of bentonite nanoclay without intercalation. The accomplishment of the surface modification was quantitatively proved by TGA analysis. Modified BNC can covalently couple with different material surfaces, allowing its nanospace to be utilized for intercalation of cations, bio-molecules, and polymeric materials, to be used in advanced military aerospace, pharmaceuticals, and many other commercial applications.

Polypropylene/Short Glass Fibers Composites: Effects of Coupling Agents on Mechanical Properties, Thermal Behaviors, and Morphology

PubMed Central

Lin, Jia-Horng; Huang, Chien-Lin; Liu, Chi-Fan; Chen, Chih-Kuang; Lin, Zheng-Ian; Lou, Ching-Wen

2015-01-01

This study uses the melt compounding method to produce polypropylene (PP)/short glass fibers (SGF) composites. PP serves as matrix while SGF serves as reinforcement. Two coupling agents, maleic anhydride grafted polypropylene, (PP-g-MA) and maleic anhydride grafted styrene-ethylene-butylene-styrene block copolymer (SEBS-g-MA) are incorporated in the PP/SGF composites during the compounding process, in order to improve the interfacial adhesion and create diverse desired properties of the composites. According to the mechanical property evaluations, increasing PP-g-MA as a coupling agent provides the composites with higher tensile, flexural, and impact properties. In contrast, increasing SEBS-g-MA as a coupling agent provides the composites with decreasing tensile and flexural strengths, but also increasing impact strength. The DSC results indicate that using either PP-g-MA or SEBS-g-MA as the coupling agent increases the crystallization temperature. However, the melting temperature of PP barely changes. The spherulitic morphology results show that PP has a smaller spherulite size when it is processed with PP-g-MA or SEBS-g-MA as the coupling agent. The SEM results indicate that SGF is evenly distributed in PP matrices, but there are distinct voids between these two materials, indicating a poor interfacial adhesion. After PP-g-MA or SEBS-g-MA is incorporated, SGF can be encapsulated by PP, and the voids between them are fewer and indistinctive. This indicates that the coupling agents can effectively improve the interfacial compatibility between PP and SGF, and as a result improves the diverse properties of PP/SGF composites. PMID:28793710

Effect of silane dilution on intrinsic stress in glow discharge hydrogenated amorphous silicon films

NASA Astrophysics Data System (ADS)

Harbison, J. P.; Williams, A. J.; Lang, D. V.

1984-02-01

Measurements of the intrinsic stress in hydrogenated amorphous silicon (a-Si : H) films grown by rf glow discharge decomposition of silane diluted to varying degrees in argon are presented. Films are found to grow under exceedingly high compressive stress. Low values of macroscopic film density and low stress values are found to correlate with high growth rate. An abrupt drop in stress occurs between 2 and 3% silane at precisely the point where columnar growth morphology appears. No corresponding abrupt change is noted in density, growth rate, or plasma species concentrations as determined by optical emissioin spectroscopy. Finally a model of diffusive incorporation of hydrogen or some gaseous impurity during growth into the bulk of the film behind the growing interface is proposed to explain the results.

A comprehensive model to determine the effects of temperature and species fluctuations on reaction rates in turbulent reacting flows

NASA Technical Reports Server (NTRS)

Goldstein, D.; Magnotti, F.; Chinitz, W.

1983-01-01

Reaction rates in turbulent, reacting flows are reviewed. Assumed probability density functions (pdf) modeling of reaction rates is being investigated in relation to a three variable pdf employing a 'most likely pdf' model. Chemical kinetic mechanisms treating hydrogen air combustion is studied. Perfectly stirred reactor modeling of flame stabilizing recirculation regions was used to investigate the stable flame regions for silane, hydrogen, methane, and propane, and for certain mixtures thereof. It is concluded that in general, silane can be counted upon to stabilize flames only when the overall fuel air ratio is close to or greater than unity. For lean flames, silane may tend to destabilize the flame. Other factors favoring stable flames are high initial reactant temperatures and system pressure.

Lewis Acidity of Bis(perfluorocatecholato)silane: Aldehyde Hydrosilylation Catalyzed by a Neutral Silicon Compound

DOE PAGES

Liberman-Martin, Allegra L.; Bergman, Robert G.; Tilley, T. Don

2015-04-16

Bis(perfluorocatecholato)silane Si(cat( F) 2 was prepared, and stoichiometric binding to Lewis bases was demonstrated with fluoride, triethylphosphine oxide, and N,N'-diisopropylbenzamide. The potent Lewis acidity of Si(cat( F) 2 was suggested from catalytic hydrosilylation and silylcyanation reactions with aldehydes. Mechanistic studies of hydrosilylation using an optically active silane substrate, R-(+)-methyl-(1-naphthyl)phenylsilane, proceeded with predominant stereochemical retention at silicon, consistent with a carbonyl activation pathway. The enantiospecificity was dependent on solvent and salt effects, with increasing solvent polarity or addition of NBu 4BAr( F) 4 leading to a diminished enantiomeric ratio. The medium effects are consistent with an ionic mechanism, wherein hydride transfermore » occurs prior to silicon-oxygen bond formation.« less

Cellular effect of high doses of silica-coated quantum dot profiled with high throughput gene expression analysis and high content cellomics measurements.

PubMed

Zhang, Tingting; Stilwell, Jackie L; Gerion, Daniele; Ding, Lianghao; Elboudwarej, Omeed; Cooke, Patrick A; Gray, Joe W; Alivisatos, A Paul; Chen, Fanqing Frank

2006-04-01

Quantum dots (Qdots) are now used extensively for labeling in biomedical research, and this use is predicted to grow because of their many advantages over alternative labeling methods. Uncoated Qdots made of core/shell CdSe/ZnS are toxic to cells because of the release of Cd2+ ions into the cellular environment. This problem has been partially overcome by coating Qdots with polymers, poly(ethylene glycol) (PEG), or other inert molecules. The most promising coating to date, for reducing toxicity, appears to be PEG. When PEG-coated silanized Qdots (PEG-silane-Qdots) are used to treat cells, toxicity is not observed, even at dosages above 10-20 nM, a concentration inducing death when cells are treated with polymer or mercaptoacid coated Qdots. Because of the importance of Qdots in current and future biomedical and clinical applications, we believe it is essential to more completely understand and verify this negative global response from cells treated with PEG-silane-Qdots. Consequently, we examined the molecular and cellular response of cells treated with two different dosages of PEG-silane-Qdots. Human fibroblasts were exposed to 8 and 80 nM of these Qdots, and both phenotypic as well as whole genome expression measurements were made. PEG-silane-Qdots did not induce any statistically significant cell cycle changes and minimal apoptosis/necrosis in lung fibroblasts (IMR-90) as measured by high content image analysis, regardless of the treatment dosage. A slight increase in apoptosis/necrosis was observed in treated human skin fibroblasts (HSF-42) at both the low and the high dosages. We performed genome-wide expression array analysis of HSF-42 exposed to doses 8 and 80 nM to link the global cell response to a molecular and genetic phenotype. We used a gene array containing approximately 22,000 total probe sets, containing 18,400 probe sets from known genes. Only approximately 50 genes (approximately 0.2% of all the genes tested) exhibited a statistically significant change in expression level of greater than 2-fold. Genes activated in treated cells included those involved in carbohydrate binding, intracellular vesicle formation, and cellular response to stress. Conversely, PEG-silane-Qdots induce a down-regulation of genes involved in controlling the M-phase progression of mitosis, spindle formation, and cytokinesis. Promoter analysis of these results reveals that expression changes may be attributed to the down-regulation of FOXM and BHLB2 transcription factors. Remarkably, PEG-silane-Qdots, unlike carbon nanotubes, do not activate genes indicative of a strong immune and inflammatory response or heavy-metal-related toxicity. The experimental evidence shows that CdSe/ZnS Qdots, if appropriately protected, induce negligible toxicity to the model cell system studied here, even when exposed to high dosages. This study indicates that PEG-coated silanized Qdots pose minimal impact to cells and are a very promising alternative to uncoated Qdots.

Evaluation of Adhesive Bonding of Lithium Disilicate Ceramic Material with Duel Cured Resin Luting Agents

PubMed Central

Gundawar, Sham M.; Radke, Usha M.

2015-01-01

Purpose: The purpose of this vitro study was to comparatively evaluate the adhesive bonding of dual cured resin luting agents with lithium disilicate ceramic material. Materials and Methods: Porcelain laminate veneers were prepared with lithium disilicate ceramic material i.e. IPS Empress II( E-Max Press). These laminates were bonded with RelyX ARC, Panavia F 2.0, Variolink II, Duolink and Nexus NX3.The porcelain laminates were etched with 9.6% hydrofluoric acid (Pulpdent Corporation) for one minute, washed for 15 sec with three way syringe and dried for 15 sec with air syringe. The silane (Ultradent) was applied with the help of applicator tip in a single coat and kept undisturbed for one minute. The prepared surfaces of the premolars were treated with 37% phosphoric acid (Prime dent) for 15 sec, thoroughly rinsed and dried as per manufactures instructions. The shear bond test was carried out on all samples with the Universal testing machine (Instron U.S.A.) The scanning electron microscopic study was performed at the fractured interface of representative samples from each group of luting agents. Result: In this study, the highest value of shear bond strength was obtained for NEXUS NX3 and the lowest for VARIOLINK II. Conclusion: The difference in bond strength can be interpreted as the difference in fracture resistance of luting agents, to which shearing load was applied during the shear bond strength test. It is inferred from this study that the composition of the luting agent determines the adhesive characteristics in addition to surface treatment and bonding surface area. PMID:25859514

Organosilane-functionalized graphene quantum dots and their encapsulation into bi-layer hollow silica spheres for bioimaging applications.

PubMed

Wen, Ting; Yang, Baocheng; Guo, Yanzhen; Sun, Jing; Zhao, Chunmei; Zhang, Shouren; Zhang, Miao; Wang, Yonggang

2014-11-14

Graphene quantum dots (GQDs) represent an important class of luminescent quantum dots owing to their low toxicity and superior biocompatibility. Chemical functionalization of GQDs and subsequent combination with other materials further provide attractive techniques for advanced bioapplications. Herein, we report the facile fabrication of fluorescent organosilane-functionalized graphene quantum dots (Si-GQDs) and their embedding into mesoporous hollow silica spheres as a biolabel for the first time. Well-proportioned Si-GQDs with bright and excitation dependent tunable emissions in the visible region were obtained via a simple and economical solvothermal route adopting graphite oxide as a carbon source and 3-(2-aminoethylamino)-propyltrimethoxysilane as a surface modifier. The as-synthesized Si-GQDs can be well dispersed and stored in organic solvents, easily manufactured into transparent film and bulk form, and particularly provide great potential to be combined with other materials. As a proof-of-principle experiment, we demonstrate the successful incorporation of Si-GQDs into hollow mesoporous silica spheres and conduct preliminary cellular imaging experiments. Interestingly, the Si-GQDs not only serve as fluorescent chromophores in the composite material, but also play a crucial role in the formation of mesoporous hollow silica spheres with a distinctive bi-layer architecture. The layer thickness and optical properties can be precisely controlled by simply adjusting the silane coupling agent addition procedure in the preparation process. Our demonstration of low-cost Si-GQDs and their encapsulation into multifunctional composites may expand the applications of carbon-based nanomaterials for future biomedical imaging and other optoelectronic applications.

Fabrication of the superhydrophobic surface on aluminum alloy by anodizing and polymeric coating

NASA Astrophysics Data System (ADS)

Liu, Wenyong; Luo, Yuting; Sun, Linyu; Wu, Ruomei; Jiang, Haiyun; Liu, Yuejun

2013-01-01

We reported the preparation of the superhydrophobic surface on aluminum alloy via anodizing and polymeric coating. Both the different anodizing processes and different polymeric coatings of aluminum alloy were investigated. The effects of different anodizing conditions, such as electrolyte concentration, anodization time and current on the superhydrophobic surface were discussed. The results showed that a good superhydrophobic surface was facilely fabricated by polypropylene (PP) coating after anodizing. The optimum conditions for anodizing were determined by orthogonal experiments. When the concentration of oxalic acid was 10 g/L, the concentration of NaCl was 1.25 g/L, anodization time was 40 min, and anodization current was 0.4 A, the best superhydrophobic surface on aluminum alloy with the contact angle (CA) of 162° and the sliding angle of 2° was obtained. On the other hand, the different polymeric coatings, such as polystyrene (PS), polypropylene (PP) and polypropylene grafting maleic anhydride (PP-g-MAH) were used to coat the aluminum alloy surface after anodizing. The results showed that the superhydrophobicity was most excellent by coating PP, while the duration of the hydrophobic surface was poor. By modifying the surface with the silane coupling agent before PP coating, the duration of the superhydrophobic surface was improved. The morphologies of the superhydrophobic surface were further confirmed by optical microscope (OM) and scanning electron microscope (SEM). Combined with the material of PP with the low surface free energy, the micro/nano-structures of the surface resulted in the superhydrophobicity of the aluminum alloy surface.

Covalent Binding of Antibodies to Cellulose Paper Discs and Their Applications in Naked-eye Colorimetric Immunoassays.

PubMed

Peng, Yanfen; Gelder, Victor Van; Amaladoss, Anburaj; Patel, Kadamb Haribhai

2016-10-21

This report presents two methods for the covalent immobilization of capture antibodies on cellulose filter paper grade No. 1 (medium-flow filter paper) discs and grade No. 113 (fast-flow filter paper) discs. These cellulose paper discs were grafted with amine functional groups through a silane coupling technique before the antibodies were immobilized on them. Periodate oxidation and glutaraldehyde cross-linking methods were used to graft capture antibodies on the cellulose paper discs. In order to ensure the maximum binding capacity of the capture antibodies to their targets after immobilization, the effects of various concentrations of sodium periodate, glutaraldehyde, and capture antibodies on the surface of the paper discs were investigated. The antibodies that were coated on the amine-functionalized cellulose paper discs through a glutaraldehyde cross-linking agent showed enhanced binding activity to the target when compared to the periodate oxidation method. IgG (in mouse reference serum) was used as a reference target in this study to test the application of covalently immobilized antibodies through glutaraldehyde. A new paper-based, enzyme-linked immunosorbent assay (ELISA) was successfully developed and validated for the detection of IgG. This method does not require equipment, and it can detect 100 ng/ml of IgG. The fast-flow filter paper was more sensitive than the medium-flow filter paper. The incubation period of this assay was short and required small sample volumes. This naked-eye, colorimetric immunoassay can be extended to detect other targets that are identified with conventional ELISA.

Effect of Modified Red Pottery Clay on the Moisture Absorption Behavior and Weatherability of Polyethylene-Based Wood-Plastic Composites

PubMed Central

Li, Qingde; Gao, Xun; Cheng, Wanli; Han, Guangping

2017-01-01

Red pottery clay (RPC) was modified using a silane coupling agent, and the modified RPC (mRPC) was then used to enhance the performance of high-density polyethylene-based wood-plastic composites. The effect of the mRPC content on the performances of the composites was investigated through Fourier transform infrared spectrometry, differential mechanical analysis (DMA) and ultraviolet (UV)-accelerated aging tests. After adding the mRPC, a moisture adsorption hysteresis was observed. The DMA results indicated that the mRPC effectively enhanced the rigidity and elasticity of the composites. The mRPC affected the thermal gravimetric, leading to a reduction of the thermal degradation rate and a right-shift of the thermal degradation peak; the initial thermal degradation temperature was increased. After 3000 h of UV-accelerated aging, the flexural strength and impact strength both declined. For aging time between 0 and 1000 h, the increase in amplitude of ΔL* (luminescence) and ΔE* (color) reached a maximum; the surface fading did not became obvious. ΔL* and ΔE* increased more significantly between 1000 and 2000 h. These characterization results indicate that the chromophores of the mRPC became briefly active. However, when the aging times were higher than 2000 h, the photo-degradation reaction was effectively prevented by adding the mRPC. The best overall enhancement was observed for an mRPC mass percentage of 5%, with a storage modulus of 3264 MPa and an increase in loss modulus by 16.8%, the best anti-aging performance and the lowest degree of color fading. PMID:28772470

Investigation of zinc oxide particles in cosmetic products by means of centrifugal and asymmetrical flow field-flow fractionation.

PubMed

Sogne, Vanessa; Meier, Florian; Klein, Thorsten; Contado, Catia

2017-09-15

The dimensional characterization of insoluble, inorganic particles, such as zinc oxide ZnO, dispersed in cosmetic or pharmaceutical formulations, is of great interest considering the current need of declaring the possible presence of nanomaterials on the label of commercial products. This work compares the separation abilities of Centrifugal- and Asymmetrical Flow Field-Flow Fractionation techniques (CF3 and AF4, respectively), equipped with UV-vis, MALS and DLS detectors, in size sorting ZnO particles, both as pristine powders and after their extraction from cosmetic matrices. ZnO particles, bare and superficially modified with triethoxycaprylyl silane, were used as test materials. To identify the most suitable procedure necessary to isolate the ZnO particles from the cosmetic matrix, two O/W and two W/O emulsions were formulated on purpose. The suspensions, containing the extracted particles ZnO, were separated by both Field-Flow Fractionation (FFF) techniques to establish a common analysis protocol, applicable for the analysis of ZnO particles extracted from three commercial products, sold in Europe for the baby skin care. Key aspects of this study were the selection of an appropriate dispersing agent enabling the particles to stay in stable suspensions (>24h)and the use of multiple detectors (UV-vis, MALS and DLS) coupled on-line with the FFF channels, to determine the particle dimensions without using the retention parameters. Between the two FFF techniques, CF3 revealed to be the most robust one, able to sort all suspensions created in this work. Copyright © 2017 Elsevier B.V. All rights reserved.

Spectroscopic studies of trimetoxypropylsilane and bis(trimethoxysilyl)ethane sol-gel coatings on aluminum and copper.

PubMed

Li, Ying-Sing; Tran, Tuan; Xu, Yue; Vecchio, Nicolas E

2006-11-01

Trimethoxypropylsilane (TMPS) and bis(trimethoxysilyl)ethane (BTMSE) were used as surface modifiers of metal vie the sol-gel process and dip coating. In addition to the single coating of Al, Cu and Sn, double treatments of Al were also conducted by combining coatings with these sol-gels in different sequences. Reflection and absorption infrared spectroscopy (RAIR) was employed to characterize and to trace the proceeding of the sol-gel process of the films. It was found that the silanol condensation occurs in the coating films on Al and the covalent linkage exists between the TMPS film and copper surface. From the assigned vibration modes, two conformers were identified in pure TMPS, TMPS sol-gel and coated film. A series of dip coating experiments with different concentrations of TMPS sol-gel was conducted, and the results from the collected RAIR spectra of the coated samples suggested that the coated Cu consistently has a better RAIR spectrum than that of the coated Al. The TMPS sol-gel appeared to have a better affinity to Cu than to Al. The temperature effect and the aging effect in the coating films were studied. X-ray photoelectronic spectroscopy (XPS) was employed to characterize the coated film, and the XPS data confirm the formation of the siloxane film from the silane coupling agents (SCA). Electrochemical impedance spectra (EIS) have been collected for bare Al and Cu, BTMSE sol-gel coated Al, and TMPS sol-gel coated Cu in 0.15M NaCl solution. The corresponding electronic circuit parameters have been determined to match the experimental EIS data.

A comparison between the shear bond strength of brackets bonded to glazed and deglazed porcelain surfaces with resin-reinforced glass-ionomer cement and a bis-GMA resin adhesive.

PubMed

Lifshitz, Abraham B; Cárdenas, Marianela

2006-01-01

This study compared the shear bond strength of a light-cure resin-reinforced glass-ionomer cement with a bis-GMA light-cure resin system in the bonding of stainless steel brackets to glazed and deglazed porcelain surfaces. Porcelain surfaces were divided into 4 groups: group 1, deglazed porcelain surfaces with Transbond XT, group 2, glazed porcelain surfaces with Transbond XT; group 3, deglazed porcelain surfaces with Fuji Ortho LC; and group 4, porcelain surfaces with Fuji Ortho LC. Microetching with 50-microm aluminum oxide for 2 seconds at a distance of 5 mm deglazed the porcelain surfaces in groups 1 and 3. All brackets were bonded to the porcelain surfaces using the same procedure and light-cured for 40 seconds with a visible light. All samples were thermocycled between 5 degrees C and 55 degrees C for 300 cycles before testing for shear bond strength with a universal testing machine. The analysis of variance showed no significant difference (P < .05) among the 4 groups; ie, group 1, 10.12 MPa; group 2, 7.00 MPa; group 3, 6.78 MPa; and group 4, 11.15 MPa. The F test also failed to demonstrate any statistical difference among the groups. Conditioning the porcelain surfaces with 37% phosphoric acid immediately followed by a nonhydrolyzed silane coupling agent resulted in clinically adequate bond strength when using either a composite resin or a resin-reinforced glass-ionomer cement. Microetching of these porcelain surfaces apparently offers no bonding advantage.

Regiospecific Nucleation and Growth of Silane Coupling Agent Droplets onto Colloidal Particles

PubMed Central

2017-01-01

Nucleation-and-growth processes are used extensively in the synthesis of spherical colloids, and more recently regiospecific nucleation-and-growth processes have been exploited to prepare more complex colloids such as patchy particles. We demonstrate that surface geometry alone can be made to play the dominant role in determining the final particle geometry in such syntheses, meaning that intricate chemical surface patternings are not required. We present a synthesis method for “lollipop”-shaped colloidal heterodimers (patchy particles), combining a recently published nucleation-and-growth technique with our recent findings that particle geometry influences the locus of droplet adsorption onto anisotropic template particles. Specifically, 3-methacryloxypropyl trimethoxysilane (MPTMS) is nucleated and grown onto bullet-shaped and nail-shaped colloids. The shape of the template particle can be chosen such that the MPTMS adsorbs regiospecifically onto the flat ends. In particular, we find that particles with a wider base increase the range of droplet volumes for which the minimum in the free energy of adsorption is located at the flat end of the particle compared with bullet-shaped particles of the same aspect ratio. We put forward an extensive analysis of the synthesis mechanism and experimentally determine the physical properties of the heterodimers, supported by theoretical simulations. Here we numerically optimize, for the first time, the shape of finite-sized droplets as a function of their position on the rod-like silica particle surface. We expect that our findings will give an impulse to complex particle creation by regiospecific nucleation and growth. PMID:29057028

Development of acceptance criteria for batches of silane primer for external tank thermal protection system bonding applications

NASA Technical Reports Server (NTRS)

Mikes, F.

1985-01-01

Concluding tests for the thermogravimetric and FTIR analyses of DC 1200 silane primers are discussed as well as methods for HPLC and GC analyses and for determining titanium and silicon by atomic absorption spectroscopy. Tables summarizes results obtained for residue, ash, titanium, silicone, Si/Ti ratio, OH-absorption, the lap-shear test, and the GC headspace for alcohols.

Silylated Zeolites With Enhanced Hydrothermal Stability for the Aqueous-Phase Hydrogenation of Levulinic Acid to γ-Valerolactone

PubMed Central

Vu, Hue-Tong; Harth, Florian M.; Wilde, Nicole

2018-01-01

A systematic silylation approach using mono-, di-, and trichlorosilanes with different alkyl chain lengths was employed to enhance the hydrothermal stability of zeolite Y. DRIFT spectra of the silylated zeolites indicate that the attachment of the silanes takes place at surface silanol groups. Regarding hydrothermal stability under aqueous-phase processing (APP) conditions, i.e., pH ≈ 2, 473 K and autogenous pressure, the selective silylation of the zeolite surface using monochlorosilanes has no considerable influence. By using trichlorosilanes, the hydrothermal stability of zeolite Y can be improved significantly as proven by a stability test in an aqueous solution of 0.2 M levulinic acid (LA) and 0.6 M formic acid (FA) at 473 K. However, the silylation with trichlorosilanes results in a significant loss of total specific pore volume and total specific surface area, e.g., 0.35 cm3 g−1 and 507 m2 g−1 for the silylated zeolite Y functionalized with n-octadecyltrichlorosilane compared to 0.51 cm3 g−1 and 788 m2 g−1 for the parent zeolite Y. The hydrogenation of LA to γ-valerolactone (GVL) was conducted over 3 wt.-% Pt on zeolite Y (3PtY) silylated with either n-octadecyltrichlorosilane or methyltrichlorosilane using different reducing agents, e.g., FA or H2. While in the stability test an enhanced hydrothermal stability was found for zeolite Y silylated with n-octadecyltrichlorosilane, its stability in the hydrogenation of LA was far less pronounced. Only by applying an excess amount of methyltrichlorosilane, i.e., 10 mmol per 1 g of zeolite Y, presumably resulting in a high degree of polymerization among the silanes, a recognizable improvement of the stability of the 3 PtY catalyst could be achieved. Nonetheless, the pore blockage found for zeolite Y silylated with an excess amount of methyltrichlorosilane was reflected in a drastically lower GVL yield at 493 K using FA as reducing agent, i.e., 12 vs. 34% for 3PtY after 24 h. PMID:29868552

Silylated Zeolites with Enhanced Hydrothermal Stability for the Aqueous-Phase Hydrogenation of Levulinic Acid to γ-Valerolactone

NASA Astrophysics Data System (ADS)

Vu, Hue-Tong; Harth, Florian M.; Wilde, Nicole

2018-05-01

A systematic silylation approach using mono-, di- and trichlorosilanes with different alkyl chain lengths was employed to enhance the hydrothermal stability of zeolite Y. DRIFT spectra of the silylated zeolites indicate that the attachment of the silanes takes place at surface silanol groups. Regarding hydrothermal stability under aqueous-phase processing conditions, i.e., pH ≈ 2, 473 K and autogenous pressure, the selective silylation of the zeolite surface using monochlorosilanes has no considerable influence. By using trichlorosilanes, the hydrothermal stability of zeolite Y can be improved significantly as proven by a stability test in an aqueous solution of 0.6 M levulinic acid (LA) and 0.2 M formic acid (FA) at 473 K. However, the silylation with trichlorosilanes results in a significant loss of total specific pore volume and total specific surface area, e.g., 0.35 cm3 g-1 and 507 m2 g 1 for the silylated zeolite Y functionalized with n octadecyltrichlorosilane compared to 0.51 cm3 g 1 and 788 m2 g-1 for the parent zeolite Y. The hydrogenation of LA to γ valerolactone (GVL) was conducted over 3 wt.-% Pt on zeolite Y (3PtY) silylated with either n octadecyltrichlorosilane or methyltrichlorosilane using different reducing agents, e.g., FA or H2. While in the stability test an enhanced hydrothermal stability was found for zeolite Y silylated with n octadecyltrichlorosilane, its stability in the hydrogenation of LA was far less pronounced. Only by applying an excess amount of methyltrichlorosilane, i.e., 10 mmol per 1 g of zeolite Y, presumably resulting in a high degree of polymerization among the silanes, a recognizable improvement of the stability of the 3 PtY catalyst could be achieved. Nonetheless, the pore blockage found for zeolite Y silylated with an excess amount of methyltrichlorosilane was reflected in a drastically lower GVL yield at 493 K using FA as reducing agent, i.e., 12% vs. 34% for 3PtY after 24 h.

Effect of composite surface treatment and aging on the bond strength between a core build-up composite and a luting agent

PubMed Central

COTES, Caroline; CARDOSO, Mayra; de MELO, Renata Marques; VALANDRO, Luiz Felipe; BOTTINO, Marco Antonio

2015-01-01

Objective The purpose of this study was to assess the influence of conditioning methods and thermocycling on the bond strength between composite core and resin cement. Material and Methods Eighty blocks (8×8×4 mm) were prepared with core build-up composite. The cementation surface was roughened with 120-grit carbide paper and the blocks were thermocycled (5,000 cycles, between 5°C and 55°C, with a 30 s dwell time in each bath). A layer of temporary luting agent was applied. After 24 h, the layer was removed, and the blocks were divided into five groups, according to surface treatment: (NT) No treatment (control); (SP) Grinding with 120-grit carbide paper; (AC) Etching with 37% phosphoric acid; (SC) Sandblasting with 30 mm SiO2 particles, silane application; (AO) Sandblasting with 50 mm Al2O3 particles, silane application. Two composite blocks were cemented to each other (n=8) and sectioned into sticks. Half of the specimens from each block were immediately tested for microtensile bond strength (µTBS), while the other half was subjected to storage for 6 months, thermocycling (12,000 cycles, between 5°C and 55°C, with a dwell time of 30 s in each bath) and µTBS test in a mechanical testing machine. Bond strength data were analyzed by repeated measures two-way ANOVA and Tukey test (α=0.05). Results The µTBS was significantly affected by surface treatment (p=0.007) and thermocycling (p=0.000). Before aging, the SP group presented higher bond strength when compared to NT and AC groups, whereas all the other groups were statistically similar. After aging, all the groups were statistically similar. SP submitted to thermocycling showed lower bond strength than SP without thermocycling. Conclusion Core composites should be roughened with a diamond bur before the luting process. Thermocycling tends to reduce the bond strength between composite and resin cement. PMID:25760269

Characterization of a hybrid-smectite nanomaterial formed by immobilizing of N-pyridin-2-ylmethylsuccinamic acid onto (3-aminopropyl)triethoxysilane modified smectite and its potentiometric sensor application

NASA Astrophysics Data System (ADS)

Topcu, Cihan; Caglar, Sema; Caglar, Bulent; Coldur, Fatih; Cubuk, Osman; Sarp, Gokhan; Gedik, Kubra; Bozkurt Cirak, Burcu; Tabak, Ahmet

2016-09-01

A novel N-pyridin-2-ylmethylsuccinamic acid-functionalized smectite nanomaterial was synthesized by immobilizing of N-pyridin-2-ylmethylsuccinamic acid through chemical bonding onto (3-aminopropyl)triethoxysilane modified smectite. The structural, thermal, morphological and surface properties of raw, silane-grafted and the N-pyridin-2-ylmethylsuccinamic acid-functionalized smectites were investigated by various characterization techniques. The thermal analysis data showed the presence of peaks in the temperature range from 200 °C to 600 °C due to the presence of physically adsorbed silanes, intercalated silanes, surface grafted silanes and chemically grafted silane molecules between the smectite layers. The powder x-ray diffraction patterns clearly indicated that the aminopropyl molecules also intercalated into the smectite interlayers as bilayer arrangement whereas N-pyridin-2-ylmethylsuccinamic acid molecules were only attached to 3-aminopropyltriethoxysilane molecules on the external surface and edges of clay and they did not intercalate. Fourier transform infrared spectroscopy confirms N-pyridin-2-ylmethylsuccinamic acid molecules bonding through the amide bond between the amine group of aminopropyltriethoxysilane molecules and a carboxylic acid functional group of N-pyridin-2-ylmethylsuccinamic acid molecules. The guest molecules functionalized onto the smectite caused significant alterations in the textural and morphological parameters of the raw smectite. The anchoring of N-pyridin-2-ylmethylsuccinamic acid molecules led to positive electrophoretic mobility values when compared to starting materials. N-pyridin-2-ylmethylsuccinamic acid-functionalized smectite was employed as an electroactive ingredient in the structure of potentiometric PVC-membrane sensor. The sensor exhibited more selective potentiometric response towards chlorate ions compared to the other common anionic species.

The effect of silane applied to glass ceramics on surface structure and bonding strength at different temperatures

PubMed Central

Eraslan, Oguz

2016-01-01

PURPOSE To evaluate the effect of various surface treatments on the surface structure and shear bond strength (SBS) of different ceramics. MATERIALS AND METHODS 288 specimens (lithium-disilicate, leucite-reinforced, and glass infiltrated zirconia) were first divided into two groups according to the resin cement used, and were later divided into four groups according to the given surface treatments: G1 (hydrofluoric acid (HF)+silane), G2 (silane alone-no heat-treatment), G3 (silane alone-then dried with 60℃ heat-treatment), and G4 (silane alone-then dried with 100℃ heat-treatment). Two different adhesive luting systems were applied onto the ceramic discs in all groups. SBS (in MPa) was calculated from the failure load per bonded area (in N/mm2). Subsequently, one specimen from each group was prepared for SEM evaluation of the separated-resin–ceramic interface. RESULTS SBS values of G1 were significantly higher than those of the other groups in the lithium disilicate ceramic and leucite reinforced ceramic, and the SBS values of G4 and G1 were significantly higher than those of G2 and G3 in glass infiltrated zirconia. The three-way ANOVA revealed that the SBS values were significantly affected by the type of resin cement (P<.001). FIN ceramics had the highest rate of cohesive failure on the ceramic surfaces than other ceramic groups. AFM images showed that the surface treatment groups exhibited similar topographies, except the group treated with HF. CONCLUSION The heat treatment was not sufficient to achieve high SBS values as compared with HF acid etching. The surface topography of ceramics was affected by surface treatments. PMID:27141250

Sandblasting may damage the surface of composite CAD-CAM blocks.

PubMed

Yoshihara, Kumiko; Nagaoka, Noriyuki; Maruo, Yukinori; Nishigawa, Goro; Irie, Masao; Yoshida, Yasuhiro; Van Meerbeek, Bart

2017-03-01

CAD-CAM blocks to fabricate semi-direct and indirect restorations are available in different sorts of ceramics as well as composite. In order to bond restorations prepared out of composite blocks into tooth cavities, it is recommended to gently sandblast the surface prior to the application of a primer/adhesive. Today, the effect of sandblasting composite block surfaces has not thoroughly been investigated. In this study, the ultra-structure of composite CAD-CAM blocks was investigated with special attention to the effect of sandblasting on the surface topography and of silanization on the bonding performance. Five different composite CAD-CAM blocks were involved. We correlatively investigated their structural and chemical composition using X-ray diffraction (XRD), energy dispersion spectroscopy (EDS), scanning electron microscopy (SEM) and (scanning) transmission electron microscopy ((S)TEM). The effect of sandblasting was also imaged in cross-section and at the interface with composite cement. Finally, we measured the shear bond strength to the sandblasted block surface with and without silanization. All composite blocks revealed a different ultra-structure. Sandblasting increased surface roughness and resulted in an irregular surface with some filler exposure. Sandblasting also damaged the surface. When the sandblasted composite blocks were silanized, superior bonding receptiveness in terms of higher bond strength was achieved except for Shofu Block HC. Sandblasting followed by silanization improved the bond strength to composite CAD-CAM blocks. However, sandblasting may also damage the composite CAD-CAM block surface. For the composite CAD-CAM block Shofu Block HC, the damage was so severe that silanization did not improve bond strength. Copyright © 2016 The Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Effects of silica coating and silane surface conditioning on the bond strength of metal and ceramic brackets to enamel.

PubMed

Atsü, Saadet Sağlam; Gelgör, Ibrahim Erhan; Sahin, Volkan

2006-09-01

To evaluate the effect of tribochemical silica coating and silane surface conditioning on the bond strength of metal and ceramic brackets bonded to enamel surfaces with light-cured composite resin. Twenty metal and 20 ceramic brackets were divided into four groups (n = 10 for each group). The specimens were randomly assigned to one of the following treatment conditions of the metal and ceramic brackets' surface: (1) tribochemical silica coating combined with silane and (2) no treatment. Brackets were bonded to the enamel surface on the labial and lingual sides of human maxillary premolars (20 total) with a light-polymerized resin composite. All specimens were stored in water for 1 week at 37 degrees C and then thermocycled (5000 cycles, 5 degrees C to 55 degrees C, 30 seconds). The shear bond strength values were measured on a universal testing machine. Student's t-test was used to compare the data (alpha = 0.05). The types of failures were observed using a stereomicroscope. Metal and ceramic brackets treated with silica coating with silanization had significantly greater bond strength values (metal brackets: 14.2 +/- 1.7 MPa, P < .01; ceramic brackets: 25.9 +/- 4.4 MPa, P < .0001) than the control groups (metal brackets: 11.9 +/- 1.3 MPa; ceramic brackets: 15.6 +/- 4.2 MPa). Treated specimens of metal and ceramic exhibited cohesive failures in resin and adhesive failures at the enamel-adhesive interface, whereas control specimens showed mixed types of failures. Silica coating with aluminum trioxide particles coated with silica followed by silanization gave higher bond strengths in both metal and ceramic brackets than in the control group.

Protein resistance efficacy of PEO-silane amphiphiles: Dependence on PEO-segment length and concentration

PubMed Central

Rufin, Marc A.; Barry, Mikayla E.; Adair, Paige A.; Hawkins, Melissa L.; Raymond, Jeffery E.; Grunlan, Melissa A.

2016-01-01

In contrast to modification with conventional PEO-silanes (i.e. no siloxane tether), silicones with dramatically enhanced protein resistance have been previously achieved via bulk-modification with poly (ethylene oxide) (PEO)-silane amphiphiles α-(EtO)3Si(CH2)2-oligodimethylsiloxane13-block-PEOn-OCH3 when n = 8 and 16 but not when n = 3. In this work, their efficacy was evaluated in terms of optimal PEO-segment length and minimum concentration required in silicone. For each PEO-silane amphiphile (n = 3, 8, and 16), five concentrations (5, 10, 25, 50, and 100 μmol per 1 g silicone) were evaluated. Efficacy was quantified in terms of the modified silicones’ abilities to undergo rapid, water-driven surface restructuring to form hydrophilic surfaces as well as resistance to fibrinogen adsorption. Only n = 8 and 16 were effective, with a lower minimum concentration in silicone required for n = 8 (10 μmol per 1 g silicone) versus n = 16 (25 μmol per 1 g silicone). Statement of Significance Silicone is commonly used for implantable medical devices, but its hydrophobic surface promotes protein adsorption which leads to thrombosis and infection. Typical methods to incorporate poly(ethylene oxide) (PEO) into silicones have not been effective due to the poor migration of PEO to the surface-biological interface. In this work, PEO-silane amphiphiles – comprised of a siloxane tether (m = 13) and variable PEO segment lengths (n = 3, 8, 16) – were blended into silicone to improve its protein resistance. The efficacy of the amphiphiles was determined to be dependent on PEO length. With the intermediate PEO length (n = 8), water-driven surface restructuring and resulting protein resistance was achieved with a concentration of only 1.7 wt%. PMID:27090588

Novel SiO2-deposited CaF2 substrate for vibrational sum-frequency generation (SFG) measurements of chemisorbed monolayers in an aqueous environment.

PubMed

Padermshoke, Adchara; Konishi, Shouta; Ara, Masato; Tada, Hirokazu; Ishibashi, Taka-Aki

2012-06-01

A novel SiO(2)-deposited CaF(2) (SiO(2)/CaF(2)) substrate for measuring vibrational sum-frequency generation (SFG) spectra of silane-based chemisorbed monolayers in aqueous media has been developed. The substrate is suitable for silanization and transparent over a broad range of the infrared (IR) probe. The present work demonstrates the practical application of the SiO(2)/CaF(2) substrate and, to our knowledge, the first SFG spectrum at the solid/water interface of a silanized monolayer observed over the IR fingerprint region (1780-1400 cm(-1)) using a back-side probing geometry. This new substrate can be very useful for SFG studies of various chemisorbed organic molecules, particularly biological compounds, in aqueous environments.

Energy efficient synthesis of boranes

DOEpatents

Thorn, David L [Los Alamos, NM; Tumas, William [Los Alamos, NM; Schwarz, Daniel E [Los Alamos, NM; Burrell, Anthony K [Los Alamos, NM

2012-01-24

The reaction of halo-boron compounds (B--X compounds, compounds having one or more boron-halogen bonds) with silanes provides boranes (B--H compounds, compounds having one or more B--H bonds) and halosilanes. Inorganic hydrides, such as surface-bound silane hydrides (Si--H) react with B--X compounds to form B--H compounds and surface-bound halosilanes. The surface bound halosilanes are converted back to surface-bound silanes electrochemically. Halo-boron compounds react with stannanes (tin compounds having a Sn--H bond) to form boranes and halostannanes (tin compounds having a Sn--X bond). The halostannanes are converted back to stannanes electrochemically or by the thermolysis of Sn-formate compounds. When the halo-boron compound is BCl.sub.3, the B--H compound is B.sub.2H.sub.6, and where the reducing potential is provided electrochemically or by the thermolysis of formate.

Energy efficient synthesis of boranes

DOEpatents

Thorn, David L.; Tumas, William; Schwarz, Daniel E.; Burrell, Anthony K.

2010-11-23

The reaction of halo-boron compounds (B--X compounds, compounds having one or more boron-halogen bonds) with silanes provides boranes (B--H compounds, compounds having one or more B--H bonds) and halosilanes. Inorganic hydrides, such as surface-bound silane hydrides (Si--H) react with B--X compounds to form B--H compounds and surface-bound halosilanes. The surface bound halosilanes are converted back to surface-bound silanes electrochemically. Halo-boron compounds react with stannanes (tin compounds having a Sn--H bond) to form boranes and halostannanes (tin compounds having a Sn--X bond). The halostannanes are converted back to stannanes electrochemically or by the thermolysis of Sn-formate compounds. When the halo-boron compound is BCl.sub.3, the B--H compound is B.sub.2H.sub.6, and where the reducing potential is provided electrochemically or by the thermolysis of formate.

Removing Chlorides From Metallurgical-Grade Silicon

NASA Technical Reports Server (NTRS)

Breneman, W. C.; Coleman, L. M.

1982-01-01

Process for making low-cost silicon for solar cells is further improved. Silane product recycled to feed stripper column converts some of heavy impurities to volatile ones that pass off at top of column with light wastes. Impurities--chlorides of arsenic, phosphorus, and boron-would otherwise be carried to subsequent distillations where they would be difficult to remove. Since only a small amount of silane is recycled, silicon production efficiency remains high.

Silane-O/sub 2/ explosions, their characteristics and their control

DOE Office of Scientific and Technical Information (OSTI.GOV)

Ring, M.A.; O'Neil, H.E.; Famil-Ghiriha, J.

1988-07-15

Prior results on the stoichiometry, upper pressure explosion limits and reaction mechanism of SiH/sub 2/-O/sub 2/ explosion reactions are discussed, and new data on the effects of added disilane on the pyrophoric and explosive characters of metastable SiH/sub 4/-O/sub 2/ mixtures are presented. The results have possible application to the prevention of serious explosions due to silane leaks into air.

Synthesis of borasiloxanes by oxidative hydrolysis of silanes and pinacolborane using Cu3(BTC)2 as a solid catalyst.

PubMed

Dhakshinamoorthy, Amarajothi; Asiri, Abdullah M; Concepcion, Patricia; Garcia, Hermenegildo

2017-09-05

A convenient method for the synthesis of borasiloxanes from silanes and pinacolboranes using Cu 3 (BTC) 2 as a heterogeneous catalyst in acetonitrile at 70 °C is reported. This procedure is more convenient than Ru and Pd based homogeneous catalysts because it avoids the use of noble metals, easy handling of starting materials and the catalyst can be reused.

Method for encapsulating and isolating hazardous cations, medium for encapsulating and isolating hazardous cations

DOEpatents

Wasserman, S.R.; Anderson, K.B.; Song, K.; Yuchs, S.E.; Marshall, C.L.

1998-04-28

A method for encapsulating hazardous cations is provided comprising supplying a pretreated substrate containing the cations; contacting the substrate with an organo-silane compound to form a coating on the substrate; and allowing the coating to cure. A medium for containing hazardous cations is also provided, comprising a substrate having ion-exchange capacity and a silane-containing coating on the substrate. 3 figs.

Thermal decomposition of silane to form hydrogenated amorphous Si

DOEpatents

Strongin, M.; Ghosh, A.K.; Wiesmann, H.J.; Rock, E.B.; Lutz, H.A. III

Hydrogenated amorphous silicon is produced by thermally decomposing silane (SiH/sub 4/) or other gases comprising H and Si, at elevated temperatures of about 1700 to 2300/sup 0/C, in a vacuum of about 10/sup -8/ to 10/sup -4/ torr. A gaseous mixture is formed of atomic hydrogen and atomic silicon. The gaseous mixture is deposited onto a substrate to form hydrogenated amorphous silicon.

The influence of silanized nano-SiO{sub 2} on the hydration of cement paste: NMR investigations

DOE Office of Scientific and Technical Information (OSTI.GOV)

Bede, A., E-mail: Andrea.Bede@phys.utcluj.ro; Pop, A.; Ardelean, I.

2015-12-23

It is known that by adding a small amount of nanoparticles to the cement-based materials a strong influence on the workability, strength and durability is obtained. These characteristics of the material are fundamentally determined by the hydration process taking place after mixing the cement grains with water. In the present study the influence introduced by the addition of nano-silica with silanized surfaces on the hydration process was investigated using low-field nuclear magnetic resonance (NMR) relaxometry. The cement samples were prepared using gray cement at a water-to-cement ratio of 0.4 and a 5% addition of nanosilica. The surface of the nanoparticlesmore » was modified using a coating of Silane A174. The cement pastes were monitored during their standard curing time of 28 days. It was established that, by using unmodified nanosilica particles, an acceleration of the hydration process takes place as compared with the pure cement paste. On the other side, by adding silanized nanoparticles, the dormancy stage significantly extends and the hydration process is slower. This slowing down process could enhance the mechanical strength of cement based materials as a result of a better compaction of the hydrated samples.« less

Detection and distribution analysis of organosilicon compounds in wood by means of SEM-EDX and micro-CT

DOE Office of Scientific and Technical Information (OSTI.GOV)

Vetter, L. de; Cnudde, V.; Masschaele, B.

This article explores the potential of a scanning electron microscope with an energy dispersive X-ray spectrometer in combination with a new non-destructive 3D visualization technique, X-ray micro-computed tomography, as detection methods for siloxanes/silanes mixtures applied as wood preservatives. In order to have a higher contrast, bromine functional silane was added to the mixture. Scots pine and beech samples were dipped or impregnated with the mixture and subsequently scanned. Both silicon and bromine were easily detectable with both techniques. Dipped siloxanes/silanes covered the cell walls partly in beech and the lumen partly or completely in Scots pine. Impregnated siloxanes/silanes could bemore » found in the cell walls of both wood species. From the results, it can be concluded that, under the circumstances as described in the article, impregnation with a siloxane is necessary to have cell wall penetration. The combination of scanning electron microscopy, energy dispersive X-ray spectroscopy and micro-computed tomography can offer important information concerning the localization of certain products inside wood. While the last of these can monitor changes in 3D, the other two techniques can provide detailed 2D information. Both techniques are complementary and provide important extra information.« less

Rational interface design of epoxy-organoclay nanocomposites: role of structure-property relationship for silane modifiers.

PubMed

Bruce, Alex N; Lieber, Danielle; Hua, Inez; Howarter, John A

2014-04-01

Montmorillonite was modified by three silane surfactants with different functionalities to investigate the role of surfactant structure on the properties of a final epoxy-organoclay nanocomposite. N-aminopropyldimethylethoxysilane (APDMES), an aminated monofunctional silane, was chosen as a promising surfactant for several reasons: (1) it will bond to silica in montmorillonite, (2) it will bond to epoxide groups, and (3) to overcome difficulties found with trifunctional aminosilane bonding clay layers together and preventing exfoliation. A trifunctional and non-aminated version of APDMES, 3-aminopropyltriethoxysilane (APTES) and n-propyldimethylmethoxysilane (PDMMS), respectively, was also studied to provide comparison to this rationally chosen surfactant. APDMES and APTES were grafted onto montmorillonite in the same amount, while PDMMS was barely grafted (<1 wt%). The gallery spacing of APDMES organoclay was greater than APTES or PDMMS, but the final nanocomposite gallery spacing was not dependent on the surfactant used. Different concentrations of APDMES modified montmorillonite yielded different properties, as concentration decreased glass transition temperature increased, thermal stability increased, and the storage modulus decreased. Storage modulus, glass transition temperature, and thermal stability were more similar for epoxy-organoclay composites modified with the same concentration of silane surfactant, neat epoxy, and epoxy-montmorillonite nanocomposite. Copyright © 2013 Elsevier Inc. All rights reserved.

Reduced Zeta potential through use of cationic adhesion promoter for improved resist process performance and minimizing material consumption

NASA Astrophysics Data System (ADS)

Hodgson, Lorna; Thompson, Andrew

2012-03-01

This paper presents the results of a non-HMDS (non-silane) adhesion promoter that was used to reduce the zeta potential for very thin (proprietary) polymer on silicon. By reducing the zeta potential, as measured by the minimum sample required to fully coat a wafer, the amount of polymer required to coat silicon substrates was significantly reduced in the manufacture of X-ray windows used for high transmission of low-energy X-rays. Moreover, this approach used aqueous based adhesion promoter described as a cationic surface active agent that has been shown to improve adhesion of photoresists (positive, negative, epoxy [SU8], e-beam and dry film). As well as reducing the amount of polymer required to coat substrates, this aqueous adhesion promoter is nonhazardous, and contains non-volatile solvents.

Aqueous synthesis of polyhedral “brick-like” iron oxide nanoparticles for hyperthermia and T2 MRI contrast enhancement†

PubMed Central

Worden, Matthew; Bruckman, Michael A.; Kim, Min-Ho; Steinmetz, Nicole F.; Kikkawa, James M.; LaSpina, Catherine

2015-01-01

A low temperature, aqueous synthesis of polyhedral iron oxide nanoparticles (IONPs) is presented. The modification of the co-precipitation hydrolysis method with Triton X surfactants results in the formation of crystalline polyhedral particles. The particles are herein termed iron oxide “nanobricks” (IONBs) as the variety of particles made are all variations on a simple “brick-like” rhombohedral shape as evaluated by TEM. These IONBs can be easily coated with hydrophilic silane ligands, allowing them to be dispersed in aqueous media. The dispersed particles are investigated for potential applications as hyperthermia and T2 MRI contrast agents. The results demonstrate that the IONBs perform better than comparable spherical IONPs in both applications, and show r2 values amongst the highest for iron oxide based materials reported in the literature. PMID:26693011

Aircraft Fuel Tank Inerting System

DTIC Science & Technology

1983-07-01

The 4950th T~st Wing was to determine If any compass/navigation problems were encoun- tered. Boeing reported that the " Winglet Program" Is encountering... blending TPX, silane, and a peroxide catalyst and reacting the grafted material with water. 2. Extrusioa of the grafted TPX was not successful under a...experiments, particularly in order to evaluate how much of a problem a loss of silane by evaporation would be at the high blending temperatures that had

Silane-Pyrolysis Reactor With Nonuniform Heating

NASA Technical Reports Server (NTRS)

Iya, Sridhar K.

1991-01-01

Improved reactor serves as last stage in system processing metallurgical-grade silicon feedstock into silicon powder of ultrahigh purity. Silane pyrolized to silicon powder and hydrogen gas via homogeneous decomposition reaction in free space. Features set of individually adjustable electrical heaters and purge flow of hydrogen to improve control of pyrolysis conditions. Power supplied to each heater set in conjunction with flow in reactor to obtain desired distribution of temperature as function of position along reactor.

Reactivity of sulfide-containing silane toward boehmite and in situ modified rubber/boehmite composites by the silane

NASA Astrophysics Data System (ADS)

Lin, Tengfei; Zhu, Lixin; Chen, Weiwei; Wu, Siwu; Guo, Baochun; Jia, Demin

2013-09-01

The silanization reaction between boehmite (BM) nanoplatelets and bis-[3-(triethoxysilyl)-propyl]-tetrasulfide (TESPT) was characterized in detail. Via such modification process, the grafted sulfide moieties on the BM endow reactivity toward rubber and substantially improved hydrophobicity for BM. Accordingly, TESPT was employed as in situ modifier for the nitrile rubber (NBR)/BM compounds to improve the mechanical properties of the reinforced vulcanizates. The effects of BM content and in situ modification on the mechanical properties, curing characteristics and morphology were investigated. BM was found to be effective in improving the mechanical performance of NBR vulcanizates. The NBR/BM composites could be further strengthened by the incorporation of TESPT. The interfacial adhesion of NBR/BM composites was obviously improved by the addition of TESPT. The substantially improved mechanical performance was correlated to the interfacial reaction and the improved dispersion of BM in rubber matrix.

The Effect of Silane on the Microstructure, Corrosion, and Abrasion Resistances of the Anodic Films on Ti Alloy

NASA Astrophysics Data System (ADS)

Wang, Jinwei; Chen, Jiali

2016-04-01

Anodic oxide films on Ti-6Al-4V alloy are prepared using sodium hydroxide as the base electrolyte containing aminopropyl trimethoxysilane (APS) as an additive. Some APS undergo hydrolysis, adsorption, and chemical reaction with the TiO x to form Ti-O-Si bond as confirmed by ATR-FTIR and XPS spectra, and in turn their surface appearance and roughness are greatly changed with the addition of APS as observed by their SEM images. These amino anodic films possess much higher corrosive resistances since the formation of Ti-O-Si complex enhances the compactness of the anodic films and the existence of aminopropyl groups inside the pores provides additional blocking effects. Besides, their improvement in anti-abrasive capability is attributed to the toughening effect of the chemically bonded silanes and the lubrication functions from both the chemically bonded and physically absorbed silanes between the touched interfaces.

Low cost silicon solar array project silicon materials task: Establishment of the feasibility of a process capable of low-cost, high volume production of silane (step 1) and the pyrolysis of silane to semiconductor-grade silicon (step 2)

NASA Technical Reports Server (NTRS)

Breneman, W. C.; Cheung, H.; Farrier, E. G.; Morihara, H.

1977-01-01

A quartz fluid bed reactor capable of operating at temperatures of up to 1000 C was designed, constructed, and successfully operated. During a 30 minute experiment, silane was decomposed within the reactor with no pyrolysis occurring on the reactor wall or on the gas injection system. A hammer mill/roller-crusher system appeared to be the most practical method for producing seed material from bulk silicon. No measurable impurities were detected in the silicon powder produced by the free space reactor, using the cathode layer emission spectroscopic technique. Impurity concentration followed by emission spectroscopic examination of the residue indicated a total impurity level of 2 micrograms/gram. A pellet cast from this powder had an electrical resistivity of 35 to 45 ohm-cm and P-type conductivity.

Low cost silicon solar array project silicon materials task: Establishment of the feasibility of a process capable of low-cost, high volume production of silane (step 1) and the pyrolysis of silane to semiconductor-grade silicon (step 2)

NASA Technical Reports Server (NTRS)

Breneman, W. C.; Farrier, E. G.; Rexer, J.

1977-01-01

Extended operation of a small process-development unit routinely produced high quality silane in 97+% yield from dichlorosilane. The production rate was consistent with design loadings for the fractionating column and for the redistribution reactor. A glass fluid-bed reactor was constructed for room temperature operation. The behavior of a bed of silcon particles was observed as a function of various feedstocks, component configurations, and operating conditions. For operating modes other than spouting, the bed behaved in an erratic and unstable manner. A method was developed for casting molten silicon powder into crack-free solid pellets for process evaluation. The silicon powder was melted and cast into thin walled quartz tubes that sacrificially broke on cooling.

Ultrahigh molecular weight aromatic siloxane polymers

NASA Technical Reports Server (NTRS)

Ludwick, L. M.

1982-01-01

The condensation of a diol with a silane in toluene yields a silphenylene-siloxane polymer. The reaction of stiochiometric amounts of the diol and silane produced products with molecular weights in the range 2.0 - 6.0 x 10 to the 5th power. The molecular weight of the product was greatly increased by a multistep technique. The methodology for synthesis of high molecular weight polymers using a two step procedure was refined. Polymers with weight average molecular weights in excess of 1.0 x 10 to the 6th power produced by this method. Two more reactive silanes, bis(pyrrolidinyl)dimethylsilane and bis(gamma butyrolactam)dimethylsilane, are compared with the dimethyleminodimethylsilane in ability to advance the molecular weight of the prepolymer. The polymers produced are characterized by intrinsic viscosity in tetrahydrofuran. Weight and number average molecular weights and polydispersity are determined by gel permeation chromatography.

Process feasibility study in support of silicon material task 1

NASA Technical Reports Server (NTRS)

Fang, C. S.; Hansen, K. C.; Miller, J. W., Jr.; Yaws, C. L.

1978-01-01

Initial results for gas thermal conductivity of silicon tetrafluoride and trichlorosilane are reported in respective temperature ranges of 25 to 400 C and 50 to 400 C. For chemical engineering analyses, the preliminary process design for the original silane process of Union Carbide was completed for Cases A and B, Regular and Minimum Process Storage. Included are raw material usage, utility requirements, major process equipment lists, and production labor requirements. Because of the large differences in surge tankage between major unit operations the fixed capital investment varied from $19,094,000 to $11,138,000 for Cases A and B, respectively. For the silane process the original flowsheet was revised for a more optimum arrangement of major equipment, raw materials and operating conditions. The initial issue of the revised flowsheet (Case C) for the silane process indicated favorable cost benefits over the original scheme.

Chemical vapor deposition of silicon, silicon dioxide, titanium and ferroelectric thin films

NASA Astrophysics Data System (ADS)

Chen, Feng

Various silicon-based thin films (such as epitaxial, polycrystalline and amorphous silicon thin films, silicon dioxide thin films and silicon nitride thin films), titanium thin film and various ferroelectric thin films (such as BaTiO3 and PbTiO3 thin films) play critical roles in the manufacture of microelectronics circuits. For the past few years, there have been tremendous interests to search for cheap, safe and easy-to-use methods to develop those thin films with high quality and good step coverage. Silane is a critical chemical reagent widely used to deposit silicon-based thin films. Despite its wide use, silane is a dangerous material. It is pyrophoric, extremely flammable and may explode from heat, shock and/or friction. Because of the nature of silane, serious safety issues have been raised concerning the use, transportation, and storage of compressed gas cylinders of silane. Therefore it is desired to develop safer ways to deposit silicon-based films. In chapter III, I present the results of our research in the following fields: (1) Silane generator, (2) Substitutes of silane for deposition of silicon and silicon dioxide thin films, (3) Substitutes of silane for silicon dioxide thin film deposition. In chapter IV, hydropyridine is introduced as a new ligand for use in constructing precursors for chemical vapor deposition. Detachement of hydropyridine occurs by a low-temperature reaction leaving hydrogen in place of the hydropyridine ligands. Hydropyridine ligands can be attached to a variety of elements, including main group metals, such as aluminum and antimony, transition metals, such as titanium and tantalum, semiconductors such as silicon, and non-metals such as phosphorus and arsenic. In this study, hydropyridine-containing titanium compounds were synthesized and used as chemical vapor deposition precursors for deposition of titanium containing thin films. Some other titanium compounds were also studied for comparison. In chapter V, Chemical Vapor Depositions (CVD) of many oxide thin films including ferroelectric and high dielectric constant BaTiO3, SrTiO 3 and PbTiO3 films had been carried out under reduced pressure (30 torr--80 torr) using liquid precursors containing beta-diketone ligands. The relative reactivities of Ba(beta-diketonate)2, Sr(beta-diketonate) 2, Pb(beta-diketonate)2, Ti(beta-diketonate)3, TiO(beta-diketonate)2 and Ti(OiPr)2(beta-diketonate) 2 had been studied individually prior to the deposition of BaTiO 3, SrTiO3 and PbTiO3 thin films from the mixtures of corresponding precursors. By using multi-step deposition method, carbon free stoichiometric BaTiO3 thin films uniform in large area have been achieved.

Effect of surface treatments on the flexural properties and adhesion of glass fiber-reinforced composite post to self-adhesive luting agent and radicular dentin.

PubMed

Elnaghy, Amr M; Elsaka, Shaymaa E

2016-01-01

This study evaluated the effect of different surface treatments on the flexural properties and adhesion of glass fiber post to self-adhesive luting agent and radicular dentin. Seventy-five single-rooted human teeth were prepared to receive a glass fiber post (Reblida). The posts were divided into five groups according to the surface treatment: Gr C (control; no treatment), Gr S (silanization for 60 s), Gr AP (airborne-particle abrasion), Gr HF (etching with 9 % hydrofluoric acid for 1 min), and Gr M10 (etching with CH2Cl2 for 10 min). Dual-cure self-adhesive luting agent (Rely X Unicem) was applied to each group for testing the adhesion using micropush-out test. Failure types were examined with stereomicroscope and surface morphology of the posts was characterized using a scanning electron microscopy (SEM). Flexural properties of posts were assessed using a three-point bending test. Data were analyzed using ANOVA and Tukey's HSD test. Statistical significance was set at the 0.05 probability level. Groups treated with M10 showed significantly higher bond strength than those obtained with other surface treatments (P < 0.05). In general, improvements in bond strength (MPa) were found in the following order: M10 > C > S > AP > HF. Most failure modes were adhesive type of failures between dentin and luting agent (48.2%). SEM analysis revealed that the fiber post surfaces were modified after surface treatments. The surface treatments did not compromise the flexural properties of fiber posts. Application of M10 to the fiber post surfaces enhanced the adhesion to self-adhesive luting agent and radicular dentin.

A Financial Market Model Incorporating Herd Behaviour.

PubMed

Wray, Christopher M; Bishop, Steven R

2016-01-01

Herd behaviour in financial markets is a recurring phenomenon that exacerbates asset price volatility, and is considered a possible contributor to market fragility. While numerous studies investigate herd behaviour in financial markets, it is often considered without reference to the pricing of financial instruments or other market dynamics. Here, a trader interaction model based upon informational cascades in the presence of information thresholds is used to construct a new model of asset price returns that allows for both quiescent and herd-like regimes. Agent interaction is modelled using a stochastic pulse-coupled network, parametrised by information thresholds and a network coupling probability. Agents may possess either one or two information thresholds that, in each case, determine the number of distinct states an agent may occupy before trading takes place. In the case where agents possess two thresholds (labelled as the finite state-space model, corresponding to agents' accumulating information over a bounded state-space), and where coupling strength is maximal, an asymptotic expression for the cascade-size probability is derived and shown to follow a power law when a critical value of network coupling probability is attained. For a range of model parameters, a mixture of negative binomial distributions is used to approximate the cascade-size distribution. This approximation is subsequently used to express the volatility of model price returns in terms of the model parameter which controls the network coupling probability. In the case where agents possess a single pulse-coupling threshold (labelled as the semi-infinite state-space model corresponding to agents' accumulating information over an unbounded state-space), numerical evidence is presented that demonstrates volatility clustering and long-memory patterns in the volatility of asset returns. Finally, output from the model is compared to both the distribution of historical stock returns and the market price of an equity index option.

Decoupling Coupled Constraints Through Utility Design

DOE Office of Scientific and Technical Information (OSTI.GOV)

Li, N; Marden, JR

2014-08-01

Several multiagent systems exemplify the need for establishing distributed control laws that ensure the resulting agents' collective behavior satisfies a given coupled constraint. This technical note focuses on the design of such control laws through a game-theoretic framework. In particular, this technical note provides two systematic methodologies for the design of local agent objective functions that guarantee all resulting Nash equilibria optimize the system level objective while also satisfying a given coupled constraint. Furthermore, the designed local agent objective functions fit into the framework of state based potential games. Consequently, one can appeal to existing results in game-theoretic learning tomore » derive a distributed process that guarantees the agents will reach such an equilibrium.« less

The effects of dentin and intaglio indirect ceramic optimized polymer restoration surface treatment on the shear bond strength of resin cement

NASA Astrophysics Data System (ADS)

Puspitarini, A.; Suprastiwi, E.; Usman, M.

2017-08-01

Ceramic optimized polymer (ceromer) bonds to the tooth substrate through resin cements. The bond strength between dentin, resin cement, and ceromer depends on the applied surface treatment. To analyze the effects of dentin and intaglio ceromer surface treatment on the shear bond strength self-adhesive resin cement. Forty-five dentin premolar and ceromer specimens were bonded with resin cement and divided into three groups as follows: in group 1, no treatment was applied; in group 2, dentin surface treatment was carried out with acid etching and a bonding agent; and in group 3, dentin surface treatment was carried out with acid etching, a bonding agent, and intaglio ceromer surface treatment with etching and silane. All specimens were incubated at 37 °C for 24 hours, and the shear bond strength was measured using a universal testing machine. Group 3 showed the highest shear bond strength, followed by group 2. The surface treatment of dentin and intaglio ceromer showed significantly improved shear bond strength in the group comparison. Dentin and intaglio ceromer surface treatment can improved the shear bond strength self-adhesive resin cement.

Synthesis of Silane and Silicon in a Non-equilibrium Plasma Jet

NASA Technical Reports Server (NTRS)

Calcote, H. F.

1978-01-01

The original objective of this program was to determine the feasibility of high volume, low-cost production of high purity silane or solar cell grade silicon using a non equilibrium plasma jet. The emphasis was changed near the end of the program to determine the feasibility of preparing photovoltaic amorphous silicon films directly using this method. The non equilibrium plasma jet should be further evaluated as a technique for producing high efficiency photovoltaic amorphous silicon films.

Ion Kinetics in Silane Plasmas

DTIC Science & Technology

1988-02-01

stimulated emission. Rg2 + is then a classical excimer laser scheme which ought to apply generally to the homonuclear and heteronuclear rare- gas dimer...kinetics of ion formation by electron impact and subsequent reaction in silane:noble- gas mixtures have been examined using pulsed ion cyclotron reso...charge transfer reactions such as X + + SiH4 -- SiH + + X + (4 - n)(H, H2) where X+ is a rare- gas or s:licon-hydride ion. Room-temperature rate constants

Aryl diazonium salts: a new class of coupling agents for bonding polymers, biomacromolecules and nanoparticles to surfaces.

PubMed

Mahouche-Chergui, Samia; Gam-Derouich, Sarra; Mangeney, Claire; Chehimi, Mohamed M

2011-07-01

This critical review summarizes existing knowledge on the use of diazonium salts as a new generation of surface modifiers and coupling agents for binding synthetic polymers, biomacromolecules, and nanoparticles to surfaces. Polymer grafts can be directly grown at surfaces through the so-called grafting from approaches based on several polymerization methods but can also be pre-formed in solution and then grafted to surfaces through grafting onto strategies including "click" reactions. Several routes are also described for binding biomacromolecules through aryl layers in view of developing biosensors and protein arrays, while the use of aryl diazonium coupling agents is extended to the attachment of nanoparticles. Patents and industrial applications of the surface chemistry of diazonium compounds are covered. This review stresses the paramount role of aryl diazonium coupling agents in adhesion, surface and materials sciences (114 references).

Fast and Selective Preconcentration of Europium from Wastewater and Coal Soil by Graphene Oxide/Silane@Fe3O4 Dendritic Nanostructure.

PubMed

Patra, Santanu; Roy, Ekta; Madhuri, Rashmi; Sharma, Prashant K

2015-05-19

In this study, nanocomposite of graphene oxide and silane modified magnetic nanoparticles (silane@Fe3O4) were synthesized in a form of dendritic structure. For this, silane@Fe3O4 nanoparticle gets sandwiched between two layers of graphene oxide by chemical synthesis route. The synthesized dendritic structure was used as a monomer for synthesis of europium ion imprinted polymer. The synthesis of imprinted polymer was contemplated onto the surface of the vinyl group modified silica fiber by activated generated free radical atom-transfer radical polymerization, that is, AGET-ATRP technique. The synthesized dendritic monomer was characterized by XRD, FT-IR, VSM, FE-SEM, and TEM analyses. The imprinted polymer modified silica fiber was first validated in the aqueous and blood samples for successful extraction and detection of europium ion with limit of detection = 0.050 pg mL(-1) (signal/noise = 3). The imprinted polymer modified silica fiber was also used for preconcentration and separation of europium metal ion from various soil samples of coal mine areas. However, the same silica fiber was also used for wastewater treatment and shows 100% performance for europium removal. The findings herein suggested that dendritic nanocomposite could be potentially used as a highly effective material for the enrichment and preconcentration of europium or other trivalent lanthanides/actinides in nuclear waste management.

Influence of surface treatments on the shear bond strength of orthodontic brackets to porcelain

NASA Astrophysics Data System (ADS)

Wang, Cong; Zeng, Jishan; Wang, Shaoan; Yang, Zheng; Huang, Qian; Chen, Pixiu; Zhou, Shujuan; Liu, Xiaoqing

2008-11-01

The purpose of this study was to investigate the effect of various surface treatments after different storage time and thermocycling on the shear bond strength of orthodontic brackets to the feldspathic porcelain surfaces. 128 disc-shaped porcelain specimens were randomly assigned to the following surface treatments: 9.6% HFA, 9.6% HFA combined with silane, 50 μ aluminum trioxide sandblasting followed by silane and application of silane after 37% phosphoric acid. Metal or ceramic brackets were bonded onto each treated porcelain facet with light cured resin. The samples were stored in 37 °C water 1 day or 7 days, thermocycled 500 times from 5 to 55 °C. The shear bond strengths were measured (1 mm/min), and statistically analyzed. The bond failure sites were classified according to ARI system. The surface of the glazed, sandblasted, hydrofluoric and phosphoric acid etched porcelain were examined with SEM. All groups achieved reasonable bond strengths to withstand the application of orthodontic forces. Water storage for 7 days caused lower shear bond strength than that of 1 day. But there is no statistically significant difference between the two groups. The mean shear bond strength provided by ceramic bracket with mechanical retention had no statistical difference with that of metal bracket. Therefore, the optimal treatment for orthodontic brackets bonding to feldspathic porcelain was to apply phosphoric acid combined with silane.

Modification of silicone elastomer with zwitterionic silane for durable antifouling properties.

PubMed

Yeh, Shiou-Bang; Chen, Chien-Sheng; Chen, Wen-Yih; Huang, Chun-Jen

2014-09-30

Biofouling on medical devices generally causes adverse complications, such as thrombosis, infection, and pathogenic calcification. Silicone is a widely used material for medical applications. Its surface modification typically encounters undesirable "hydrophobic recovery", leading to deterioration of surface engineering. In this study, we developed a stable superhydrophilic zwitterionic interface on polydimethylsiloxane (PDMS) elastomer by covalent silanization of sulfobetaine silane (SBSi) to resist nonspecific adsorption of bacteria, proteins, and lipids. SBSi is a zwitterionic organosilane assembly, enabling resisting surface reconstruction by forming a cross-linked network and polar segregation. Surface elemental composition was confirmed by X-ray photoelectron spectroscopy (XPS), and the long-term stability of modification was accessed using a contact angle goniometer. The biofouling tests were carried out by exposing substrates to bacterial, protein, and lipid solutions, revealing the excellent bioinertness of SBSi-tailored PDMS, even after 30 day storage in ambient. For the real-world application, we modified commercially available silicone hydrogel contact lenses with developed zwitterionic silane, presenting its antibacterial adhesion property. Moreover, the cytotoxicity of SBSi was accessed with NIH-3T3 fibroblast by the MTT assay, showing negligible cytotoxicity up to a concentration of 5 mM. Consequently, the strategy of surface engineering in this work can effectively retard the "hydrophobic recovery" occurrence and can be applied to other silicone-based medical devices in a facile way.