Effect of Strain Rate on Mechanical Properties of Wrought Sintered Tungsten at Temperatures above 2500 F

NASA Technical Reports Server (NTRS)

Sikora, Paul F.; Hall, Robert W.

1961-01-01

Specimens of wrought sintered commercially pure tungsten were made from 1/8-inch swaged rods. All the specimens were recrystallized at 4050 F for 1 hour prior to testing at temperatures from 2500 to 4000 F at various strain rates from 0.002 to 20 inches per inch per minute. Results showed that, at a constant temperature, increasing the strain rate increased the ultimate tensile strength significantly. The effects of both strain rate and temperature on the ultimate tensile strength of tungsten may be correlated by the linear parameter method of Manson and Haferd and may be used to predict the ultimate tensile strength at higher temperatures, 4500 and 5000 F. As previously reported, ductility, as measured by reduction of area in a tensile test, decreases with increasing temperature above about 3000 F. Increasing the strain rate at temperatures above 3000 F increases the ductility. Fractures are generally transgranular at the higher strain rates and intergranular at the lower strain rates.

Interaction of heat production, strain rate and stress power in a plastically deforming body under tensile test

NASA Technical Reports Server (NTRS)

Paglietti, A.

1982-01-01

At high strain rates the heat produced by plastic deformation can give rise to a rate dependent response even if the material has rate independent constitutive equations. This effect has to be evaluated when interpreting a material test, or else it could erroneously be ascribed to viscosity. A general thermodynamic theory of tensile testing of elastic-plastic materials is given in this paper; it is valid for large strain at finite strain rates. It enables discovery of the parameters governing the thermodynamic strain rate effect, provides a method for proper interpretation of the results of the tests of dynamic plasticity, and suggests a way of planning experiments in order to detect the real contribution of viscosity.

High-rate tensile properties of Si-reduced TRIP sheet steels

NASA Astrophysics Data System (ADS)

Choi, Ildong; Park, Yeongdo; Son, Dongmin; Kim, Sung-Joon; Moon, Manbeen

2010-02-01

There have been efforts to develop Si-reduced TRIP steels to improve the wettability of Zn coatings, since the conventional CMnSi-TRIP steels suffer from poor galvanizability. In addition, for the development of potential applications of Si-reduced TRIP steels in vehicle crash management, a better understanding of high strain rate properties is required. In the present study, the effects of alloying elements, such as Cu, Al, Si, and P, on the high-rate tensile properties of Si-reduced TRIP sheet steels were investigated. Tensile tests were performed with a servo-hydraulic tensile testing machine at strain rates ranging from 10-2 to 6 × 102 s-1, and the ultimate tensile strength, elongation, strain rate sensitivity, and absorbed energy were evaluated. The retained austenite volume fractions and carbon content of the specimens were measured using neutron diffraction. The UTS was increased with Cu, Al, Si, and P alloying throughout the strain rate range, and the alloying effect on UTS was considerable with Cu and P. The effects of alloying on the microstructure were not significant. All the steels tested in this study exhibited positive strain rate sensitivity, and the m value at strain rates higher than 10 s-1 was at least two times higher than that at lower strain rates.

Modeling Strain Rate Effect of Heterogeneous Materials Using SPH Method

NASA Astrophysics Data System (ADS)

Ma, G. W.; Wang, X. J.; Li, Q. M.

2010-11-01

The strain rate effect on the dynamic compressive failure of heterogeneous material based on the smoothed particle hydrodynamics (SPH) method is studied. The SPH method employs a rate-insensitive elasto-plastic damage model incorporated with a Weibull distribution law to reflect the mechanical behavior of heterogeneous rock-like materials. A series of simulations are performed for heterogeneous specimens by applying axial velocity conditions, which induce different strain-rate loadings to the specimen. A detailed failure process of the specimens in terms of microscopic crack-activities and the macro-mechanical response are discussed. Failure mechanisms between the low and high strain rate cases are compared. The result shows that the strain-rate effects on the rock strength are mainly caused by the changing internal pressure due to the inertial effects as well as the material heterogeneity. It also demonstrates that the inertial effect becomes significant only when the induced strain rate exceeds a threshold, below which, the dynamic strength enhancement can be explained due to the heterogeneities in the material. It also shows that the dynamic strength is affected more significantly for a relatively more heterogeneous specimen, which coincides with the experimental results showing that the poor quality specimen had a relatively larger increase in the dynamic strength.

Hot Deformation and Dynamic Recrystallization Behavior of the Cu-Cr-Zr-Y Alloy

NASA Astrophysics Data System (ADS)

Zhang, Yi; Huili, Sun; Volinsky, Alex A.; Tian, Baohong; Chai, Zhe; Liu, Ping; Liu, Yong

2016-03-01

To study the workability and to optimize the hot deformation processing parameters of the Cu-Cr-Zr-Y alloy, the strain hardening effect and dynamic softening behavior of the Cu-Cr-Zr-Y alloy were investigated. The flow stress increases with the strain rate and stress decreases with deformation temperature. The critical conditions, including the critical strain and stress for the occurrence of dynamic recrystallization, were determined based on the alloy strain hardening rate. The critical stress related to the onset of dynamic recrystallization decreases with temperature. The evolution of DRX microstructure strongly depends on the deformation temperature and the strain rate. Dynamic recrystallization appears at high temperatures and low strain rates. The addition of Y can refine the grain and effectively accelerate dynamic recrystallization. Dislocation generation and multiplication are the main hot deformation mechanisms for the alloy. The deformation temperature increase and the strain rate decrease can promote dynamic recrystallization of the alloy.

Implementation of Improved Transverse Shear Calculations and Higher Order Laminate Theory Into Strain Rate Dependent Analyses of Polymer Matrix Composites

NASA Technical Reports Server (NTRS)

Zhu, Lin-Fa; Kim, Soo; Chattopadhyay, Aditi; Goldberg, Robert K.

2004-01-01

A numerical procedure has been developed to investigate the nonlinear and strain rate dependent deformation response of polymer matrix composite laminated plates under high strain rate impact loadings. A recently developed strength of materials based micromechanics model, incorporating a set of nonlinear, strain rate dependent constitutive equations for the polymer matrix, is extended to account for the transverse shear effects during impact. Four different assumptions of transverse shear deformation are investigated in order to improve the developed strain rate dependent micromechanics model. The validities of these assumptions are investigated using numerical and theoretical approaches. A method to determine through the thickness strain and transverse Poisson's ratio of the composite is developed. The revised micromechanics model is then implemented into a higher order laminated plate theory which is modified to include the effects of inelastic strains. Parametric studies are conducted to investigate the mechanical response of composite plates under high strain rate loadings. Results show the transverse shear stresses cannot be neglected in the impact problem. A significant level of strain rate dependency and material nonlinearity is found in the deformation response of representative composite specimens.

Strain rate dependent calcite microfabric evolution - An experiment carried out by nature

NASA Astrophysics Data System (ADS)

Rogowitz, Anna; Grasemann, Bernhard; Huet, Benjamin; Habler, Gerlinde

2014-12-01

A flanking structure developed along a secondary shear zone in calcite marbles, on Syros (Cyclades, Greece), provides a natural laboratory for directly studying the effects of strain rate variations on calcite deformation at identical pressure and temperature conditions. The presence and rotation of a fracture during progressive deformation caused extreme variations in finite strain and strain rate, forming a localized ductile shear zone that shows different microstructures and textures. Textures and the degree of intracrystalline deformation were measured by electron backscattered diffraction. Marbles from the host rocks and the shear zone, which deformed at various strain rates, display crystal-preferred orientation, suggesting that the calcite preferentially deformed by intracrystalline-plastic deformation. Increasing strain rate results in a switch from subgrain rotation to bulging recrystallization in the dislocation-creep regime. With increasing strain rate, we observe in fine-grained (3 μm) ultramylonitic zones a change in deformation regime from grain-size insensitive to grain-size sensitive. Paleowattmeter and the paleopiezometer suggest strain rates for the localized shear zone around 10-10 s-1 and for the marble host rock around 10-12 s-1. We conclude that varying natural strain rates can have a first-order effect on the microstructures and textures that developed under the same metamorphic conditions.

High temperature, low-cycle fatigue of copper-base alloys in argon. Part 2: Zirconium-copper at 482, 538 and 593 C

NASA Technical Reports Server (NTRS)

Conway, J. B.; Stentz, R. H.; Berling, J. T.

1973-01-01

Zirconium-copper (1/2 hard) was tested in argon over the temperature range from 482 to 593 C in an evaluation of short-term tensile and low-cycle fatigue behavior. The effect of strain rate on the tensile properties was evaluated at 538 C and in general it was found that the yield and ultimate strengths increased as the strain rate was increased from 0.0004 to 0.01/sec. Ductility was essentially insensitive to strain rate in the case of the zirconium-copper alloy. Strain-rate and hold-time effects on the low cycle fatigue behavior of zirconium-copper were evaluated in argon at 538 C. These effects were as expected in that decreased fatigue life was noted as the strain rate decreased and when hold times were introduced into the tension portion of the strain-cycle. Hold times in compression were much less detrimental than hold times in tension.

Effect of martensitic transformation on springback behavior of 304L austenitic stainless steel

NASA Astrophysics Data System (ADS)

Fathi, H.; Mohammadian Semnani, H. R.; Emadoddin, E.; Sadeghi, B. Mohammad

2017-09-01

The present paper studies the effect of martensitic transformation on the springback behavior of 304L austenitic stainless steel. Martensite volume fraction was determined at the bent portion under various strain rates after bending test. Martensitic transformation has a significant effect on the springback behavior of this material. The findings of this study indicated that the amount of springback was reduced under a situation of low strain rate, while a higher amount of springback was obtained with a higher strain rate. The reason for this phenomenon is that higher work hardening occurs during the forming process with the low strain rate due to the higher martensite volume fraction, therefore the formability of the sheet is enhanced and it leads to a decreased amount of springback after the bending test. Dependency of the springback on the martensite volume fraction and strain rate was expressed as formulas from the results of the experimental tests and simulation method. Bending tests were simulated using LS-DYNA software and utilizing MAT_TRIP to determine the martensite volume fraction and strain under various strain rates. Experimental result reveals good agreement with the simulation method.

Incorporation of Mean Stress Effects into the Micromechanical Analysis of the High Strain Rate Response of Polymer Matrix Composites

NASA Technical Reports Server (NTRS)

Goldberg, Robert K.; Roberts, Gary D.; Gilat, Amos

2002-01-01

The results presented here are part of an ongoing research program, to develop strain rate dependent deformation and failure models for the analysis of polymer matrix composites subject to high strain rate impact loads. A micromechanics approach is employed in this work, in which state variable constitutive equations originally developed for metals have been modified to model the deformation of the polymer matrix, and a strength of materials based micromechanics method is used to predict the effective response of the composite. In the analysis of the inelastic deformation of the polymer matrix, the definitions of the effective stress and effective inelastic strain have been modified in order to account for the effect of hydrostatic stresses, which are significant in polymers. Two representative polymers, a toughened epoxy and a brittle epoxy, are characterized through the use of data from tensile and shear tests across a variety of strain rates. Results computed by using the developed constitutive equations correlate well with data generated via experiments. The procedure used to incorporate the constitutive equations within a micromechanics method is presented, and sample calculations of the deformation response of a composite for various fiber orientations and strain rates are discussed.

Effect of Loading Rate and Orientation on the Compressive Response of Human Cortical Bone

DTIC Science & Technology

2014-05-01

use thereof. Destroy this report when it is no longer needed. Do not return it to the originator. Army Research Laboratory Aberdeen Proving...quasi-static (0.001/s), intermediate (1/s), and dynamic (1000–2000/s) strain rates using a split-Hopkinson pressure bar to determine the strain rate...6 Figure 5. Strain rate and strain histories of human cortical bone specimen at high rate using bar signals

Effects of strain rate, mixing ratio, and stress-strain definition on the mechanical behavior of the polydimethylsiloxane (PDMS) material as related to its biological applications.

PubMed

Khanafer, Khalil; Duprey, Ambroise; Schlicht, Marty; Berguer, Ramon

2009-04-01

Tensile tests on Polydimethylsiloxane (PDMS) materials were conducted to illustrate the effects of mixing ratio, definition of the stress-strain curve, and the strain rate on the elastic modulus and stress-strain curve. PDMS specimens were prepared according to the ASTM standards for elastic materials. Our results indicate that the physiological elastic modulus depends strongly on the definition of the stress-strain curve, mixing ratio, and the strain rate. For various mixing ratios and strain rates, true stress-strain definition results in higher stress and elastic modulus compared with engineering stress-strain and true stress-engineering strain definitions. The elastic modulus increases as the mixing ratio increases up-to 9:1 ratio after which the elastic modulus begins to decrease even as the mixing ratio continues to increase. The results presented in this study will be helpful to assist the design of in vitro experiments to mimic blood flow in arteries and to understand the complex interaction between blood flow and the walls of arteries using PDMS elastomer.

Effect of strain rate and notch geometry on tensile properties and fracture mechanism of creep strength enhanced ferritic P91 steel

NASA Astrophysics Data System (ADS)

Pandey, Chandan; Mahapatra, M. M.; Kumar, Pradeep; Saini, N.

2018-01-01

Creep strength enhanced ferritic (CSEF) P91 steel were subjected to room temperature tensile test for quasi-static (less than 10-1/s) strain rate by using the Instron Vertical Tensile Testing Machine. Effect of different type of notch geometry, notch depth and angle on mechanical properties were also considered for different strain rate. In quasi-static rates, the P91 steel showed a positive strain rate sensitivity. On the basis of tensile data, fracture toughness of P91 steel was also calculated numerically. For 1 mm notch depth (constant strain rate), notch strength and fracture toughness were found to be increased with increase in notch angle from 45° to 60° while the maximum value attained in U-type notch. Notch angle and notch depth has found a minute effect on P91 steel strength and fracture toughness. The fracture surface morphology was studied by field emission scanning electron microscopy (FESEM).

Computational Simulation of the High Strain Rate Tensile Response of Polymer Matrix Composites

NASA Technical Reports Server (NTRS)

Goldberg, Robert K.

2002-01-01

A research program is underway to develop strain rate dependent deformation and failure models for the analysis of polymer matrix composites subject to high strain rate impact loads. Under these types of loading conditions, the material response can be highly strain rate dependent and nonlinear. State variable constitutive equations based on a viscoplasticity approach have been developed to model the deformation of the polymer matrix. The constitutive equations are then combined with a mechanics of materials based micromechanics model which utilizes fiber substructuring to predict the effective mechanical and thermal response of the composite. To verify the analytical model, tensile stress-strain curves are predicted for a representative composite over strain rates ranging from around 1 x 10(exp -5)/sec to approximately 400/sec. The analytical predictions compare favorably to experimentally obtained values both qualitatively and quantitatively. Effective elastic and thermal constants are predicted for another composite, and compared to finite element results.

High-Strain-Rate Compression Testing of Ice

NASA Technical Reports Server (NTRS)

Shazly, Mostafa; Prakash, Vikas; Lerch, Bradley A.

2006-01-01

In the present study a modified split Hopkinson pressure bar (SHPB) was employed to study the effect of strain rate on the dynamic material response of ice. Disk-shaped ice specimens with flat, parallel end faces were either provided by Dartmouth College (Hanover, NH) or grown at Case Western Reserve University (Cleveland, OH). The SHPB was adapted to perform tests at high strain rates in the range 60 to 1400/s at test temperatures of -10 and -30 C. Experimental results showed that the strength of ice increases with increasing strain rates and this occurs over a change in strain rate of five orders of magnitude. Under these strain rate conditions the ice microstructure has a slight influence on the strength, but it is much less than the influence it has under quasi-static loading conditions. End constraint and frictional effects do not influence the compression tests like they do at slower strain rates, and therefore the diameter/thickness ratio of the samples is not as critical. The strength of ice at high strain rates was found to increase with decreasing test temperatures. Ice has been identified as a potential source of debris to impact the shuttle; data presented in this report can be used to validate and/or develop material models for ice impact analyses for shuttle Return to Flight efforts.

Effects of Recovery Behavior and Strain-Rate Dependence of Stress-Strain Curve on Prediction Accuracy of Thermal Stress Analysis During Casting

NASA Astrophysics Data System (ADS)

Motoyama, Yuichi; Shiga, Hidetoshi; Sato, Takeshi; Kambe, Hiroshi; Yoshida, Makoto

2017-06-01

Recovery behavior (recovery) and strain-rate dependence of the stress-strain curve (strain-rate dependence) are incorporated into constitutive equations of alloys to predict residual stress and thermal stress during casting. Nevertheless, few studies have systematically investigated the effects of these metallurgical phenomena on the prediction accuracy of thermal stress in a casting. This study compares the thermal stress analysis results with in situ thermal stress measurement results of an Al-Si-Cu specimen during casting. The results underscore the importance for the alloy constitutive equation of incorporating strain-rate dependence to predict thermal stress that develops at high temperatures where the alloy shows strong strain-rate dependence of the stress-strain curve. However, the prediction accuracy of the thermal stress developed at low temperatures did not improve by considering the strain-rate dependence. Incorporating recovery into the constitutive equation improved the accuracy of the simulated thermal stress at low temperatures. Results of comparison implied that the constitutive equation should include strain-rate dependence to simulate defects that develop from thermal stress at high temperatures, such as hot tearing and hot cracking. Recovery should be incorporated into the alloy constitutive equation to predict the casting residual stress and deformation caused by the thermal stress developed mainly in the low temperature range.

Stress Corrosion Cracking Behavior of Interstitial Free Steel Via Slow Strain Rate Technique

NASA Astrophysics Data System (ADS)

Murkute, Pratik; Ramkumar, J.; Mondal, K.

2016-07-01

An interstitial free steel is subjected to slow strain rate tests to investigate the stress corrosion cracking (SCC) behavior at strain rates ranging from 10-4 to 10-6s-1 in air and 3.5 wt.% NaCl solution. The ratios of time to failure, failure strain, and ultimate tensile stress at different strain rates in air to that in corrosive were considered as SCC susceptibility. Serrated stress-strain curve observed at lowest strain rate is explained by the Portevin-Le Chatelier effect. Maximum susceptibility to SCC at lowest strain rate is attributed to the soluble γ-FeOOH in the rust analyzed by Fourier Transformed Infrared spectroscopy. Mechanism for SCC relates to the anodic dissolution forming the groove, where hydrogen embrittlement can set in and finally fracture happens due to triaxiality.

Forming limit curves of DP600 determined in high-speed Nakajima tests and predicted by two different strain-rate-sensitive models

NASA Astrophysics Data System (ADS)

Weiß-Borkowski, Nathalie; Lian, Junhe; Camberg, Alan; Tröster, Thomas; Münstermann, Sebastian; Bleck, Wolfgang; Gese, Helmut; Richter, Helmut

2018-05-01

Determination of forming limit curves (FLC) to describe the multi-axial forming behaviour is possible via either experimental measurements or theoretical calculations. In case of theoretical determination, different models are available and some of them consider the influence of strain rate in the quasi-static and dynamic strain rate regime. Consideration of the strain rate effect is necessary as many material characteristics such as yield strength and failure strain are affected by loading speed. In addition, the start of instability and necking depends not only on the strain hardening coefficient but also on the strain rate sensitivity parameter. Therefore, the strain rate dependency of materials for both plasticity and the failure behaviour is taken into account in crash simulations for strain rates up to 1000 s-1 and FLC can be used for the description of the material's instability behaviour at multi-axial loading. In this context, due to the strain rate dependency of the material behaviour, an extrapolation of the quasi-static FLC to dynamic loading condition is not reliable. Therefore, experimental high-speed Nakajima tests or theoretical models shall be used to determine the FLC at high strain rates. In this study, two theoretical models for determination of FLC at high strain rates and results of experimental high-speed Nakajima tests for a DP600 are presented. One of the theoretical models is the numerical algorithm CRACH as part of the modular material and failure model MF GenYld+CrachFEM 4.2, which is based on an initial imperfection. Furthermore, the extended modified maximum force criterion considering the strain rate effect is also used to predict the FLC. These two models are calibrated by the quasi-static and dynamic uniaxial tensile tests and bulge tests. The predictions for the quasi-static and dynamic FLC by both models are presented and compared with the experimental results.

Dynamic compressive properties obtained from a split Hopkinson pressure bar test of Boryeong shale

NASA Astrophysics Data System (ADS)

Kang, Minju; Cho, Jung-Woo; Kim, Yang Gon; Park, Jaeyeong; Jeong, Myeong-Sik; Lee, Sunghak

2016-09-01

Dynamic compressive properties of a Boryeong shale were evaluated by using a split Hopkinson pressure bar, and were compared with those of a Hwangdeung granite which is a typical hard rock. The results indicated that the dynamic compressive loading reduced the resistance to fracture. The dynamic compressive strength was lower in the shale than in the granite, and was raised with increasing strain rate by microcracking effect as well as strain rate strengthening effect. Since the number of microcracked fragments increased with increasing strain rate in the shale having laminated weakness planes, the shale showed the better fragmentation performance than the granite at high strain rates. The effect of transversely isotropic plane on compressive strength decreased with increasing strain rate, which was desirable for increasing the fragmentation performance. Thus, the shale can be more reliably applied to industrial areas requiring good fragmentation performance as the striking speed of drilling or hydraulic fracturing machines increased. The present dynamic compressive test effectively evaluated the fragmentation performance as well as compressive strength and strain energy density by controlling the air pressure, and provided an important idea on which rock was more readily fragmented under dynamically processing conditions such as high-speed drilling and blasting.

Effects of strain rate and surface cracks on the mechanical behaviour of Balmoral Red granite.

PubMed

Mardoukhi, Ahmad; Mardoukhi, Yousof; Hokka, Mikko; Kuokkala, Veli-Tapani

2017-01-28

This work presents a systematic study on the effects of strain rate and surface cracks on the mechanical properties and behaviour of Balmoral Red granite. The tensile behaviour of the rock was studied at low and high strain rates using Brazilian disc samples. Heat shocks were used to produce samples with different amounts of surface cracks. The surface crack patterns were analysed using optical microscopy, and the complexity of the patterns was quantified by calculating the fractal dimensions of the patterns. The strength of the rock clearly drops as a function of increasing fractal dimensions in the studied strain rate range. However, the dynamic strength of the rock drops significantly faster than the quasi-static strength, and, because of this, also the strain rate sensitivity of the rock decreases with increasing fractal dimensions. This can be explained by the fracture behaviour and fragmentation during the dynamic loading, which is more strongly affected by the heat shock than the fragmentation at low strain rates.This article is part of the themed issue 'Experimental testing and modelling of brittle materials at high strain rates'. © 2016 The Author(s).

Experimental and Numerical Study on Tensile Strength of Concrete under Different Strain Rates

PubMed Central

Min, Fanlu; Yao, Zhanhu; Jiang, Teng

2014-01-01

The dynamic characterization of concrete is fundamental to understand the material behavior in case of heavy earthquakes and dynamic events. The implementation of material constitutive law is of capital importance for the numerical simulation of the dynamic processes as those caused by earthquakes. Splitting tensile concrete specimens were tested at strain rates of 10−7 s−1 to 10−4 s−1 in an MTS material test machine. Results of tensile strength versus strain rate are presented and compared with compressive strength and existing models at similar strain rates. Dynamic increase factor versus strain rate curves for tensile strength were also evaluated and discussed. The same tensile data are compared with strength data using a thermodynamic model. Results of the tests show a significant strain rate sensitive behavior, exhibiting dynamic tensile strength increasing with strain rate. In the quasistatic strain rate regime, the existing models often underestimate the experimental results. The thermodynamic theory for the splitting tensile strength of concrete satisfactorily describes the experimental findings of strength as effect of strain rates. PMID:24883355

Strain Rate Dependency of Fracture Toughness, Energy Release Rate and Geomechanical Attributes of Select Indian Shales

NASA Astrophysics Data System (ADS)

Mahanta, B.; Vishal, V.; Singh, T. N.; Ranjith, P.

2016-12-01

In addition to modern improved technology, it requires detailed understanding of rock fractures for the purpose of enhanced energy extraction through hydraulic fracturing of gas shales and geothermal energy systems. The understanding of rock fracture behavior, patterns and properties such as fracture toughness; energy release rate; strength and deformation attributes during fracturing hold significance. Environmental factors like temperature, pressure, humidity, water vapor and experimental condition such as strain rate influence the estimation of these properties. In this study, the effects of strain rates on fracture toughness, energy release rate as well as geomechanical properties like uniaxial compressive strength, Young's modulus, failure strain, tensile strength, and brittleness index of gas shales were investigated. In addition to the rock-mechanical parameters, the fracture toughness and the energy release rates were measured for three different modes viz. mode I, mixed mode (I-II) and mode II. Petrographic and X-ray diffraction (XRD) analyses were performed to identify the mineral composition of the shale samples. Scanning electron microscope (SEM) analyses were conducted to have an insight about the strain rate effects on micro-structure of the rock. The results suggest that the fracture toughness; the energy release rate as well as other geomechanical properties are a function of strain rates. At high strain rates, the strength and stiffness of shale increases which in turn increases the fracture toughness and the energy release rate of shale that may be due to stress redistribution during grain fracturing. The fracture toughness and the strain energy release rates for all the modes (I/I-II/II) are comparable at lower strain rates, but they vary considerably at higher strain rates. In all the cases, mode I and mode II fracturing requires minimum and maximum applied energy, respectively. Mode I energy release rate is maximum, compared to the other modes.

Egg Hatch Rate and Nymphal Survival of the Bed Bug (Hemiptera: Cimicidae) After Exposure to Insecticide Sprays.

PubMed

Hinson, K R; Benson, E P; Zungoli, P A; Bridges, W C; Ellis, B R

2016-12-01

Few studies have addressed the efficacy of insecticides used against eggs and first-instar nymphs of the bed bug, Cimex lectularius L. (Hemiptera: Cimicidae). Insect eggs are often resistant to insecticides; therefore, information on which products are effective is important. We evaluated the efficacy of four commonly used insecticide sprays applied directly to bed bug eggs. We also evaluated the efficacy of these insecticides to first-instar nymphs exposed to residuals resulting from directly spraying eggs. Temprid SC (beta-cyfluthrin, imidacloprid) was the most effective insecticide at preventing egg hatch (13% hatch rate) for pyrethroid-resistant, field-strain (Jersey City) bed bugs compared with a control (water [99% hatch rate]), Bedlam (MGK-264, sumithrin [84% hatch rate]), Demand CS (lambda-cyhalothrin [91% hatch rate]), and Phantom SC (chlorfenapyr [95% hatch rate]). Demand CS and Temprid SC were most effective at preventing egg hatch (0%) for an insecticide-susceptible (Harold Harlan) strain, followed by Bedlam (28%). Phantom SC produced a hatch rate similar to the control (97% and 96%, respectively). Harold Harlan-strain nymphs showed 100% survival for the control but 0% survival for Bedlam and Phantom SC. Jersey City-strain nymphs showed 100% survival for the control, 99% survival for Bedlam, 0% survival for Demand CS, 4% survival for Phantom SC, and 38% survival for Temprid SC. Demand CS was less effective at preventing hatch (91% hatch rate) of Jersey City-strain nymphs but was the only product to kill all nymphs (0% survival). One of the least effective products for preventing Jersey City-strain egg hatch (Phantom SC, 95% hatch rate) was the second most effective at killing nymphs, leaving only six of 141 alive. These findings indicate that survival of directly sprayed eggs and residually exposed, first-instar nymphs varies by strain, life stage, and product used. © The Authors 2016. Published by Oxford University Press on behalf of Entomological Society of America. All rights reserved. For Permissions, please email: journals.permissions@oup.com.

Effect of strain rate on bake hardening response of BH220 steel

NASA Astrophysics Data System (ADS)

Das, Anindya; Tarafder, Soumitro; Sivaprasad, S.; Chakrabarti, Debalay

2015-09-01

This study aims at understanding the bake hardening ability of ultra low carbon BH220 steel at different strain rates. The as-received material has been pre-strained to four different levels and then deformed in tension under (a) as pre-strained state and (b) after baking at 170 ∘C for 20 minutes, at three different strain rates of 0.001, 0.1 and 100/s. In both the conditions, yield stress increased with pre-strain and strain rate, but bake hardening ability was found to decrease when strain rate was increased. The strain rate sensitivity of the material was also found to decrease with bake hardening. Generation of dislocation forests and their subsequent immobility during baking treatment enables them to act as long range obstacles during further deformation. At higher strain rates, less amount of dislocations are produced which can interact with themselves and produce hardening, because of which bake hardening ability and the strain rate drops. A dislocation based strengthening model, as proposed by Larour et al. 2011 [7], was used to predict the yield stress values obtained at different conditions. The equation produced excellent co-relation with the experimental data.

[Community effectiveness of vaccines against infectious parotiditis (mumps). Report of cases].

PubMed

Limón Mora, J; Molina López, T; Domínguez Camacho, J C

1999-01-01

In our country, there are two types of infectious mumps vaccines available. In recent times, doubts have been raised regarding the overall effectiveness of these vaccines and the comparative effectiveness of the two strains (Rubini strain and Jeryl Lynn strain). In the "East Seville" Primary Care district, 245 cases were reported in 1997 (90.1 cases per 100,000 inhabitants). This study is aimed at taking advantage of the outbreak of cases of mumps to evaluate affected populations and comparative incidence according to type of vaccines given during childhood. Descriptive analysis of the cases (age, territorial spread, inoculation history') and trend analysis (annual incident rates) within this health care district and the surrounding area. The overall effectiveness of the mumps vaccines. The case incidence rates among those inoculated with Rubini strain and those inoculated with Jeryl Lynn strain are also estimated. The highest rates of incidence are found among children in the 1-4 age range. Overall effectiveness rates for these vaccines have been estimated. A significantly higher rate of infection has been found among the children inoculated with Rubini strain than those inoculated with the Jeryl Lynn strain (relative risk of 6.5 with a Confidence Interval of 95% 3.6-11.8). The effectiveness which follows from this study does not seem as good as the theoretical effectiveness anticipated for the mumps vaccines. It thus seems advisable for other case studies to be conducted by types of vaccines used. The data to be furnished by means of sero-epidemiological studies are also of major interest.

Spall response of single-crystal copper

NASA Astrophysics Data System (ADS)

Turley, W. D.; Fensin, S. J.; Hixson, R. S.; Jones, D. R.; La Lone, B. M.; Stevens, G. D.; Thomas, S. A.; Veeser, L. R.

2018-02-01

We performed a series of systematic spall experiments on single-crystal copper in an effort to determine and isolate the effects of crystal orientation, peak stress, and unloading strain rate on the tensile spall strength. Strain rates ranging from 0.62 to 2.2 × 106 s-1 and peak shock stresses in the 5-14 GPa range, with one additional experiment near 50 GPa, were explored as part of this work. Gun-driven impactors, called flyer plates, generated flat top shocks followed by spall. This work highlights the effect of crystal anisotropy on the spall strength by showing that the spall strength decreases in the following order: [100], [110], and [111]. Over the range of stresses and strain rates explored, the spall strength of [100] copper depends strongly on both the strain rate and shock stress. Except at the very highest shock stress, the results for the [100] orientation show linear relationships between the spall strength and both the applied compressive stress and the strain rate. In addition, hydrodynamic computer code simulations of the spall experiments were performed to calculate the relationship between the strain rate near the spall plane in the target and the rate of free surface velocity release during the pullback. As expected, strain rates at the spall plane are much higher than the strain rates estimated from the free surface velocity release rate. We have begun soft recovery experiments and molecular dynamics calculations to understand the unusual recompression observed in the spall signature for [100] crystals.

Strain rate effects in stress corrosion cracking

DOE Office of Scientific and Technical Information (OSTI.GOV)

Parkins, R.N.

Slow strain rate testing (SSRT) was initially developed as a rapid, ad hoc laboratory method for assessing the propensity for metals an environments to promote stress corrosion cracking. It is now clear, however, that there are good theoretical reasons why strain rate, as opposed to stress per se, will often be the controlling parameter in determining whether or not cracks are nucleated and, if so, are propagated. The synergistic effects of the time dependence of corrosion-related reactions and microplastic strain provide the basis for mechanistic understanding of stress corrosion cracking in high-pressure pipelines and other structures. However, while this maymore » be readily comprehended in the context of laboratory slow strain tests, its extension to service situations may be less apparent. Laboratory work involving realistic stressing conditions, including low-frequency cyclic loading, shows that strain or creep rates give good correlation with thresholds for cracking and with crack growth kinetics.« less

Implementation of Fiber Substructuring Into Strain Rate Dependent Micromechanics Analysis of Polymer Matrix Composites

NASA Technical Reports Server (NTRS)

Goldberg, Robert K.

2001-01-01

A research program is in progress to develop strain rate dependent deformation and failure models for the analysis of polymer matrix composites subject to impact loads. Previously, strain rate dependent inelastic constitutive equations developed to model the polymer matrix were incorporated into a mechanics of materials based micromechanics method. In the current work, the micromechanics method is revised such that the composite unit cell is divided into a number of slices. Micromechanics equations are then developed for each slice, with laminate theory applied to determine the elastic properties, effective stresses and effective inelastic strains for the unit cell. Verification studies are conducted using two representative polymer matrix composites with a nonlinear, strain rate dependent deformation response. The computed results compare well to experimentally obtained values.

A numerical study on the influence of the Portevin Le Chatelier effect on necking in an aluminium alloy

NASA Astrophysics Data System (ADS)

Hopperstad, O. S.; Børvik, T.; Berstad, T.; Lademo, O.-G.; Benallal, A.

2007-10-01

The constitutive relation proposed by McCormick (1988 Acta Metall. 36 3061-7) for materials exhibiting negative steady-state strain-rate sensitivity and the Portevin-Le Chatelier (PLC) effect is incorporated into an elastic-viscoplastic model for metals with plastic anisotropy. The constitutive model is implemented in LS-DYNA for corotational shell elements. Plastic anisotropy is taken into account by use of the yield criterion Yld2000/Yld2003 proposed by Barlat et al (2003 J. Plast. 19 1297-319) and Aretz (2004 Modelling Simul. Mater. Sci. Eng. 12 491-509). The parameters of the constitutive equations are determined for a rolled aluminium alloy (AA5083-H116) exhibiting negative steady-state strain-rate sensitivity and serrated yielding. The parameter identification is based on existing experimental data. A numerical investigation is conducted to determine the influence of the PLC effect on the onset of necking in uniaxial and biaxial tension for different overall strain rates. The numerical simulations show that the PLC effect leads to significant reductions in the strain to necking for both uniaxial and biaxial stress states. Increased surface roughness with plastic deformation is predicted for strain rates giving serrated yielding in uniaxial tension. It is likely that this is an important reason for the reduced critical strains. The characteristics of the deformation bands (orientation, width, velocity and strain rate) are also studied.

Extension of Viscoplasticity Based on Overstress to Capture the Effects of Prior Aging on the Time Dependent Deformation Behavior of a High-Temperature Polymer: Experiments and Modeling

DTIC Science & Technology

2008-10-01

the standard model characterization procedure is based on creep and recovery tests, where loading and unloading occurs at a fast rate of 1.0 MPa/s...σ − g[ǫ] and on d̊g[ǫ] dǫ = E, where g̊ is defined as the equilibrium stress g[ ] for extremely fast loading. For this case, the stress-strain curves...Strain S tr es s Strain Rate Slow Strain Rate Medium Strain Rate Fast Plastic Flow Fully Established Figure 2.10: Stress Strain Curve Schematic

A multi-scale model of dislocation plasticity in α-Fe: Incorporating temperature, strain rate and non-Schmid effects

DOE PAGES

Lim, H.; Hale, L. M.; Zimmerman, J. A.; ...

2015-01-05

In this study, we develop an atomistically informed crystal plasticity finite element (CP-FE) model for body-centered-cubic (BCC) α-Fe that incorporates non-Schmid stress dependent slip with temperature and strain rate effects. Based on recent insights obtained from atomistic simulations, we propose a new constitutive model that combines a generalized non-Schmid yield law with aspects from a line tension (LT) model for describing activation enthalpy required for the motion of dislocation kinks. Atomistic calculations are conducted to quantify the non-Schmid effects while both experimental data and atomistic simulations are used to assess the temperature and strain rate effects. The parameterized constitutive equationmore » is implemented into a BCC CP-FE model to simulate plastic deformation of single and polycrystalline Fe which is compared with experimental data from the literature. This direct comparison demonstrates that the atomistically informed model accurately captures the effects of crystal orientation, temperature and strain rate on the flow behavior of siangle crystal Fe. Furthermore, our proposed CP-FE model exhibits temperature and strain rate dependent flow and yield surfaces in polycrystalline Fe that deviate from conventional CP-FE models based on Schmid's law.« less

DOE Office of Scientific and Technical Information (OSTI.GOV)

Le, K. C.; Tran, T. M.; Langer, J. S.

The statistical-thermodynamic dislocation theory developed in previous papers is used here in an analysis of high-temperature deformation of aluminum and steel. Using physics-based parameters that we expect theoretically to be independent of strain rate and temperature, we are able to fit experimental stress-strain curves for three different strain rates and three different temperatures for each of these two materials. Here, our theoretical curves include yielding transitions at zero strain in agreement with experiment. We find that thermal softening effects are important even at the lowest temperatures and smallest strain rates.

Effects of strain rate and surface cracks on the mechanical behaviour of Balmoral Red granite

PubMed Central

Kuokkala, Veli-Tapani

2017-01-01

This work presents a systematic study on the effects of strain rate and surface cracks on the mechanical properties and behaviour of Balmoral Red granite. The tensile behaviour of the rock was studied at low and high strain rates using Brazilian disc samples. Heat shocks were used to produce samples with different amounts of surface cracks. The surface crack patterns were analysed using optical microscopy, and the complexity of the patterns was quantified by calculating the fractal dimensions of the patterns. The strength of the rock clearly drops as a function of increasing fractal dimensions in the studied strain rate range. However, the dynamic strength of the rock drops significantly faster than the quasi-static strength, and, because of this, also the strain rate sensitivity of the rock decreases with increasing fractal dimensions. This can be explained by the fracture behaviour and fragmentation during the dynamic loading, which is more strongly affected by the heat shock than the fragmentation at low strain rates. This article is part of the themed issue ‘Experimental testing and modelling of brittle materials at high strain rates’. PMID:27956513

Strain Rate Effect on Tensile Flow Behavior and Anisotropy of a Medium-Manganese TRIP Steel

NASA Astrophysics Data System (ADS)

Alturk, Rakan; Hector, Louis G.; Matthew Enloe, C.; Abu-Farha, Fadi; Brown, Tyson W.

2018-06-01

The dependence of the plastic anisotropy on the nominal strain rate for a medium-manganese (10 wt.% Mn) transformation-induced plasticity (TRIP) steel with initial austenite volume fraction of 66% (balance ferrite) has been investigated. The material exhibited yield point elongation, propagative instabilities during hardening, and austenite transformation to α'-martensite either directly or through ɛ-martensite. Uniaxial strain rates within the range of 0.005-500 s-1 along the 0°, 45°, and 90° orientations were selected based upon their relevance to automotive applications. The plastic anisotropy ( r) and normal anisotropy ( r n) indices corresponding to each direction and strain rate were determined using strain fields obtained from stereo digital image correlation systems that enabled both quasistatic and dynamic measurements. The results provide evidence of significant, orientation-dependent strain rate effects on both the flow stress and the evolution of r and r n with strain. This has implications not only for material performance during forming but also for the development of future strain-rate-dependent anisotropic yield criteria. Since tensile data alone for the subject medium-manganese TRIP steel do not satisfactorily determine the microstructural mechanisms responsible for the macroscopic-scale behavior observed on tensile testing, additional tests that must supplement the mechanical test results presented herein are discussed.

Strain Rate Effect on Tensile Flow Behavior and Anisotropy of a Medium-Manganese TRIP Steel

NASA Astrophysics Data System (ADS)

Alturk, Rakan; Hector, Louis G.; Matthew Enloe, C.; Abu-Farha, Fadi; Brown, Tyson W.

2018-04-01

The dependence of the plastic anisotropy on the nominal strain rate for a medium-manganese (10 wt.% Mn) transformation-induced plasticity (TRIP) steel with initial austenite volume fraction of 66% (balance ferrite) has been investigated. The material exhibited yield point elongation, propagative instabilities during hardening, and austenite transformation to α'-martensite either directly or through ɛ-martensite. Uniaxial strain rates within the range of 0.005-500 s-1 along the 0°, 45°, and 90° orientations were selected based upon their relevance to automotive applications. The plastic anisotropy (r) and normal anisotropy (r n) indices corresponding to each direction and strain rate were determined using strain fields obtained from stereo digital image correlation systems that enabled both quasistatic and dynamic measurements. The results provide evidence of significant, orientation-dependent strain rate effects on both the flow stress and the evolution of r and r n with strain. This has implications not only for material performance during forming but also for the development of future strain-rate-dependent anisotropic yield criteria. Since tensile data alone for the subject medium-manganese TRIP steel do not satisfactorily determine the microstructural mechanisms responsible for the macroscopic-scale behavior observed on tensile testing, additional tests that must supplement the mechanical test results presented herein are discussed.

Effect of Stitching on Debonding in Composite Structural Elements

NASA Technical Reports Server (NTRS)

Raju, I. S.; Glaessgen, E. H.

2001-01-01

Stitched multiaxial warp knit materials have been suggested as viable alternatives to laminated prepreg materials for large aircraft structures such as wing skins. Analyses have been developed to quantify the effectiveness of stitching for reducing strain energy release rates in skin-stiffener debond, lap joint and sandwich debond configurations. Strain energy release rates were computed using the virtual crack closure technique. In all configurations, the stitches were shown to significantly reduce the strain energy release rate.

Effects of cold-treatment and strain-rate on mechanical properties of NbTi/Cu superconducting composite wires.

PubMed

Guan, Mingzhi; Wang, Xingzhe; Zhou, Youhe

2015-01-01

During design and winding of superconducting magnets at room temperature, a pre-tension under different rate is always applied to improve the mechanical stability of the magnets. However, an inconsistency rises for superconductors usually being sensitive to strain and oversized pre-stress which results in degradation of the superconducting composites' critical performance at low temperature. The present study focused on the effects of the cold-treatment and strain-rate of tension deformation on mechanical properties of NbTi/Cu superconducting composite wires. The samples were immersed in a liquid nitrogen (LN2) cryostat for the adiabatic cold-treatment, respectively with 18-hour, 20-hour, 22-hour and 24-hour. A universal testing machine was utilized for tension tests of the NbTi/Cu superconducting composite wires at room temperature; a small-scale extensometer was used to measure strain of samples with variable strain-rate. The strength, elongation at fracture and yield strength of pre-cold-treatment NbTi/Cu composite wires were drawn. It was shown that, the mechanical properties of the superconducting wires are linearly dependent on the holding time of cold-treatment at lower tensile strain-rate, while they exhibit notable nonlinear features at higher strain-rate. The cold-treatment in advance and the strain-rate of pre-tension demonstrate remarkable influences on the mechanical property of the superconducting composite wires.

Demonstration of an adaptive response to preconditioning Frankliniella occidentalis (Pergande) to sublethal doses of spinosad: a hormetic-dose response.

PubMed

Gong, Youhui; Xu, Baoyun; Zhang, Youjun; Gao, Xiwu; Wu, Qingjun

2015-07-01

Sublethal doses of some insecticides have been reported to either stimulate or reduce the survival and fecundity of insects. Many sublethal-effect studies have been conducted after exposure of only one generation to sublethal insecticides, and there is little information about the sublethal effects on insects after long-term exposure to sublethal insecticides. In this study, changes in biological characteristics were investigated in spinosad-susceptible (Spin-S) and sublethal-spinosad-treated (Spin-Sub) strains of Frankliniella occidentalis (Pergande) after exposure to their corresponding sublethal concentrations of spinosad. The results showed that for the Spin-S strain, the LC10 concentration of spinosad slightly affected the biotic fitness both in parents and offspring of F. occidentalis. The LC25 concentration of spinosad prolonged the development time, reduced the fecundity, and significantly reduced the intrinsic rate of increase, the net reproductive rate and the finite rate of increase in the Spin-S strain. However, the negative effects were not as pronounced in the offspring (F1 generation) as in the parent generation. For the Spin-Sub strain, the LC10 and LC25 concentrations of spinosad had little negative effect on the development and fecundity, and no significant difference was found between the effects of the LC10 and LC25 treatments on the Spin-Sub strain. The Spin-Sub strain exhibited a shorter developmental time, and larger intrinsic rates of increase and net reproductive rates, compared with the corresponding treatments of the Spin-S strain. These findings combined with our previous studies suggest that the biotic fitness increased in the Spin-Sub strain and the strain became more adaptable to sublethal doses of spinosad, compared with the Spin-S strain. Physiological and biochemical adaptation may contribute to these changes after long treatment times at sublethal doses.

dK/da effects on the SCC growth rates of nickel base alloys in high-temperature water

NASA Astrophysics Data System (ADS)

Chen, Kai; Wang, Jiamei; Du, Donghai; Andresen, Peter L.; Zhang, Lefu

2018-05-01

The effect of dK/da on crack growth behavior of nickel base alloys has been studied by conducting stress corrosion cracking tests under positive and negative dK/da loading conditions on Alloys 690, 600 and X-750 in high temperature water. Results indicate that positive dK/da accelerates the SCC growth rates, and the accelerating effect increases with dK/da and the initial CGR. The FRI model was found to underestimate the dK/da effect by ∼100X, especially for strain hardening materials, and this underscores the need for improved insight and models for crack tip strain rate. The effect of crack tip strain rate and dK/dt in particular can explain the dK/da accelerating effect.

Development of constitutive models for cyclic plasticity and creep behavior of super alloys at high temperature

NASA Technical Reports Server (NTRS)

Haisler, W. E.

1983-01-01

An uncoupled constitutive model for predicting the transient response of thermal and rate dependent, inelastic material behavior was developed. The uncoupled model assumes that there is a temperature below which the total strain consists essentially of elastic and rate insensitive inelastic strains only. Above this temperature, the rate dependent inelastic strain (creep) dominates. The rate insensitive inelastic strain component is modelled in an incremental form with a yield function, blow rule and hardening law. Revisions to the hardening rule permit the model to predict temperature-dependent kinematic-isotropic hardening behavior, cyclic saturation, asymmetric stress-strain response upon stress reversal, and variable Bauschinger effect. The rate dependent inelastic strain component is modelled using a rate equation in terms of back stress, drag stress and exponent n as functions of temperature and strain. A sequence of hysteresis loops and relaxation tests are utilized to define the rate dependent inelastic strain rate. Evaluation of the model has been performed by comparison with experiments involving various thermal and mechanical load histories on 5086 aluminum alloy, 304 stainless steel and Hastelloy X.

The response of equine cortical bone to loading at strain rates experienced in vivo by the galloping horse.

PubMed

Evans, G P; Behiri, J C; Vaughan, L C; Bonfield, W

1992-03-01

The behaviour of cortical bone under load is strain rate-dependent, i.e. it is dependent on the rate at which the load is applied. This is particularly relevant in the galloping horse since the strain rates experienced by the bone are far in excess of those recorded for any other species. In this study the effect of strain rates between 0.0001 and 1 sec-1 on the mechanical properties of equine cortical bone were assessed. Initially, increasing strain rates resulted in increased mechanical properties. Beyond a critical value, however, further increases in strain rate resulted in lower strain to failure and energy absorbing capacity. This critical rate occurred around 0.1 sec-1 which is within the in vivo range for a galloping racehorse. Analysis of the stress-strain curves revealed a transition in the type of deformation at this point from pseudo-ductile to brittle. Bones undergoing brittle deformation are more likely to fail under load, leading to catastrophic fracture and destruction of the animal.

Work Hardening Behavior of 1020 Steel During Cold-Beating Simulation

NASA Astrophysics Data System (ADS)

CUI, Fengkui; LING, Yuanfei; XUE, Jinxue; LIU, Jia; LIU, Yuhui; LI, Yan

2017-03-01

The present research of cold-beating formation mainly focused on roller design and manufacture, kinematics, constitutive relation, metal flow law, thermo-mechanical coupling, surface micro-topography and microstructure evolution. However, the research on surface quality and performance of workpieces in the process of cold-beating is rare. Cold-beating simulation experiment of 1020 steel is conducted at room temperature and strain rates ranging from 2000 to 4000 s-1 base on the law of plastic forming. According to the experimental data, the model of strain hardening of 1020 steel is established, Scanning Electron Microscopy(SEM) is conducted, the mechanism of the work hardening of 1020 steel is clarified by analyzing microstructure variation of 1020 steel. It is found that the strain rate hardening effect of 1020 steel is stronger than the softening effect induced by increasing temperatures, the process of simulation cold-beating cause the grain shape of 1020 steel significant change and microstructure elongate significantly to form a fibrous tissue parallel to the direction of deformation, the higher strain rate, the more obvious grain refinement and the more hardening effect. Additionally, the change law of the work hardening rate is investigated, the relationship between dislocation density and strain, the relationship between work hardening rate and dislocation density is obtained. Results show that the change trend of the work hardening rate of 1020 steel is divided into two stages, the work hardening rate decreases dramatically in the first stage and slowly decreases in the second stage, finally tending toward zero. Dislocation density increases with increasing strain and strain rate, work hardening rate decreases with increasing dislocation density. The research results provide the basis for solving the problem of improving the surface quality and performance of workpieces under cold-beating formation of 1020 steel.

Suppression and Structure of Low Strain Rate Nonpremixed Flames

NASA Technical Reports Server (NTRS)

Hamins, Anthony; Bundy, Matthew; Park, Woe Chul; Lee, Ki Yong; Logue, Jennifer

2003-01-01

The agent concentration required to achieve suppression of low strain rate nonpremixed flames is an important fire safety consideration. In a microgravity environment such as a space platform, unwanted fires will likely occur in near quiescent conditions where strain rates are very low. Diffusion flames typically become more robust as the strain rate is decreased. When designing a fire suppression system for worst-case conditions, low strain rates should be considered. The objective of this study is to investigate the impact of radiative emission, flame strain, agent addition, and buoyancy on the structure and extinction of low strain rate nonpremixed flames through measurements and comparison with flame simulations. The suppression effectiveness of a suppressant (N2) added to the fuel stream of low strain rate methane-air diffusion flames was measured. Flame temperature measurements were attained in the high temperature region of the flame (T greater than 1200 K) by measurement of thin filament emission intensity. The time varying temperature was measured and simulated as the flame made the transition from normal to microgravity conditions and as the flame extinguished.

Effect of Sodium on the Transport and Utilization of Citric Acid by Aerobacter (Enterobacter) aerogenes

PubMed Central

Wilkerson, L. S.; Eagon, R. G.

1974-01-01

Sodium inhibited citrate uptake by two of the four strains of Aerobacter (Enterobacter) aerogenes used in these studies, had no effect on one strain, and stimulated citrate uptake by one strain. Two of the four strains grew well anaerobically on citrate in the presence of Na+, one grew poorly, and one grew not at all either in the presence or absence of Na+. Na+ stimulated the aerobic growth of one strain on citrate, increased the total growth but not the rate of growth of one strain, and prolonged the lag phase but not the rate of growth or total growth of two strains. The experimental data reported herein, therefore, indicate that there are appreciable physiological differences among strains of A. aerogenes. PMID:4418533

Effect of strain rate and dislocation density on the twinning behavior in Tantalum

DOE PAGES

Florando, Jeffrey N.; El-Dasher, Bassem S.; Chen, Changqiang; ...

2016-04-28

The conditions which affect twinning in tantalum have been investigated across a range of strain rates and initial dislocation densities. Tantalum samples were subjected to a range of strain rates, from 10 –4/s to 10 3/s under uniaxial stress conditions, and under laser-induced shock-loading conditions. In this study, twinning was observed at 77K at strain rates from 1/s to 103/s, and during laser-induced shock experiments. The effect of the initial dislocation density, which was imparted by deforming the material to different amounts of pre-strain, was also studied, and it was shown that twinning is suppressed after a given amount ofmore » pre-strain, even as the global stress continues to increase. These results indicate that the conditions for twinning cannot be represented solely by a critical global stress value, but are also dependent on the evolution of the dislocation density. Additionally, the analysis shows that if twinning is initiated, the nucleated twins may continue to grow as a function of strain, even as the dislocation density continues to increase.« less

Residual thermal and moisture influences on the strain energy release rate analysis of edge delamination

NASA Technical Reports Server (NTRS)

Obrien, T. K.; Raju, I. S.; Garber, D. P.

1985-01-01

A laminated plate theory analysis is developed to calculate the strain energy release rate associated with edge delamination growth in a composite laminate. The analysis includes the contribution of residual thermal and moisture stresses to the strain energy released. The strain energy release rate, G, increased when residual thermal effects were combined with applied mechanical strains, but then decreased when increasing moisture content was included. A quasi-three-dimensional finite element analysis indicated identical trends and demonstrated these same trends for the individual strain energy release rate components, G sub I and G sub II, associated with interlaminar tension and shear. An experimental study indicated that for T300/5208 graphite-epoxy composites, the inclusion of residual thermal and moisture stresses did not significantly alter the calculation of interlaminar fracture toughness from strain energy release rate analysis of edge delamination data taken at room temperature, ambient conditions.

Implementation of Laminate Theory Into Strain Rate Dependent Micromechanics Analysis of Polymer Matrix Composites

NASA Technical Reports Server (NTRS)

Goldberg, Robert K.

2000-01-01

A research program is in progress to develop strain rate dependent deformation and failure models for the analysis of polymer matrix composites subject to impact loads. Previously, strain rate dependent inelastic constitutive equations developed to model the polymer matrix were implemented into a mechanics of materials based micromechanics method. In the current work, the computation of the effective inelastic strain in the micromechanics model was modified to fully incorporate the Poisson effect. The micromechanics equations were also combined with classical laminate theory to enable the analysis of symmetric multilayered laminates subject to in-plane loading. A quasi-incremental trapezoidal integration method was implemented to integrate the constitutive equations within the laminate theory. Verification studies were conducted using an AS4/PEEK composite using a variety of laminate configurations and strain rates. The predicted results compared well with experimentally obtained values.

Characterization of Thermo-Mechanical and Fracture Behaviors of Thermoplastic Polymers

PubMed Central

Ghorbel, Elhem; Hadriche, Ismail; Casalino, Giuseppe; Masmoudi, Neila

2014-01-01

In this paper the effects of the strain rate on the inelastic behavior and the self-heating under load conditions are presented for polymeric materials, such as polymethyl methacrylate (PMMA), polycarbonate (PC), and polyamide (PA66). By a torsion test, it was established that the shear yield stress behavior of PMMA, PC, and PA66 is well-described by the Ree-Eyring theory in the range of the considered strain rates. During the investigation, the surface temperature was monitored using an infrared camera. The heat release appeared at the early stage of the deformation and increased with the strain and strain rate. This suggested that the external work of deformation was dissipated into heat so the torsion tests could not be considered isothermal. Eventually, the effect of the strain rate on the failure modes was analyzed by scanning electron microscopy. PMID:28788462

Strain rate effects for spallation of concrete

NASA Astrophysics Data System (ADS)

Häussler-Combe, Ulrich; Panteki, Evmorfia; Kühn, Tino

2015-09-01

Appropriate triaxial constitutive laws are the key for a realistic simulation of high speed dynamics of concrete. The strain rate effect is still an open issue within this context. In particular the question whether it is a material property - which can be covered by rate dependent stress strain relations - or mainly an effect of inertia is still under discussion. Experimental and theoretical investigations of spallation of concrete specimen in a Hopkinson Bar setup may bring some evidence into this question. For this purpose the paper describes the VERD model, a newly developed constitutive law for concrete based on a damage approach with included strain rate effects [1]. In contrast to other approaches the dynamic strength increase is not directly coupled to strain rate values but related to physical mechanisms like the retarded movement of water in capillary systems and delayed microcracking. The constitutive law is fully triaxial and implemented into explicit finite element codes for the investigation of a wide range of concrete structures exposed to impact and explosions. The current setup models spallation experiments with concrete specimen [2]. The results of such experiments are mainly related to the dynamic tensile strength and the crack energy of concrete which may be derived from, e.g., the velocity of spalled concrete fragments. The experimental results are compared to the VERD model and two further constitutive laws implemented in LS-Dyna. The results indicate that both viscosity and retarded damage are required for a realistic description of the material behaviour of concrete exposed to high strain effects [3].

Effects of Strain Rate and Temperature on the Mechanical Properties of Medium Manganese Steels

DOE Office of Scientific and Technical Information (OSTI.GOV)

Rana, Radhakanta; Matlock, David K; Speer, John G

2016-11-16

The effects of temperature (-60 to 100 °C) and strain rate (0.002 to 0.2 s-1) on the properties of Al-alloyed 7 and 10 wt-% Mn steels containing 34.8 and 57.3 vol-% austenite respectively were evaluated by tensile tests in isothermal liquid baths. The tensile strengths of both medium Mn steels increased with a decrease in temperature owing to the decreased austenite stability with a decrease in temperature. At lower temperatures the strength of the 10MnAl steel was highest, a consequence of the higher strain hardening rate caused by more austenite transformation to martensite with deformation. The resulting properties are assessedmore » with a consideration of the effects of strain rate and deformation on adiabatic heating which was observed to be as high as 95o C.« less

The influence of strain rate and hydrogen on the plane-strain ductility of Zircaloy cladding

DOE Office of Scientific and Technical Information (OSTI.GOV)

Link, T.M.; Motta, A.T.; Koss, D.A.

1998-03-01

The authors studied the ductility of unirradiated Zircaloy-4 cladding under loading conditions prototypical of those found in reactivity-initiated accidents (RIA), i.e.: near plane-strain deformation in the hoop direction (transverse to the cladding axis) at room temperature and 300 C and high strain rates. To conduct these studies, they developed a specimen configuration in which near plane-strain deformation is achieved in the gage section, and a testing methodology that allows one to determine both the limit strain at the onset of localized necking and the fracture strain. The experiments indicate that there is little effect of strain rate (10{sup {minus}3} tomore » 10{sup 2} s{sup {minus}1}) on the ductility of unhydrided Zircaloy tubing deformed under near plane-strain conditions at either room temperature or 300 C. Preliminary experiments on cladding containing 190 ppm hydrogen show only a small loss of fracture strain but no clear effect on limit strain. The experiments also indicate that there is a significant loss of Zircaloy ductility when surface flaws are present in the form of thickness imperfections.« less

Effects of pH and temperature on growth and glycerol production kinetics of two indigenous wine strains of Saccharomyces cerevisiae from Turkey

PubMed Central

Yalcin, Seda Karasu; Yesim Ozbas, Z.

2008-01-01

The study was performed in a batch system in order to determine the effects of pH and temperature on growth and glycerol production kinetics of two indigenous wine yeast strains Saccharomyces cerevisiae Kalecik 1 and Narince 3. The highest values of dry mass and specific growth rate were obtained at pH 4.00 for both of the strains. Maximum specific glycerol production rates were obtained at pH 5.92 and 6.27 for the strains Kalecik 1 and Narince 3, respectively. Kalecik 1 strain produced maximum 8.8 gL−1 of glycerol at pH 6.46. Maximum glycerol concentration obtained by the strain Narince 3 was 9.1 gL−1 at pH 6.48. Both yeasts reached maximum specific growth rate at 30°C. Optimum temperature range for glycerol production was determined as 25-30°C for the strain Kalecik 1. The strain Narince 3 reached maximum specific glycerol production rate at 30°C. Maximum glycerol concentrations at 30°C were obtained as 8.5 and 7.6 gL−1 for Kalecik 1 and Narince 3, respectively. PMID:24031225

Final Report Auto/Steel Partnership Phase II

DOE Office of Scientific and Technical Information (OSTI.GOV)

Cady, C.M.; Chen, S.R.; Gray, G.T. III

1999-06-09

This is the final report in which effects of strain-rate, temperature, and stress-state on the yield stress and the strain hardening behavior of many common steels used in automobile construction were investigated. The yield and flow stresses were found to exhibit very high rate sensitivities for most of the steels while the hardening rates were found to be insensitive to strain rate and temperature at lower temperatures or at higher strain rates. This behavior is consistent with the observation that overcoming the intrinsic Peierls stress is shown to be the rate-controlling mechanism in these materials at low temperatures. The dependencemore » of the yield stress on temperature and strain rate was found to decrease while the strain hardening rate increased. The Mechanical Threshold Stress (MTS) model was adopted to model the stress-strain behavior of the steels. Parameters for the constitutive relations were derived for the MTS model and also for the Johnson-Cook (JC) and the Zerilli-Armstrong (ZA) models. The results of this study substantiate the applicability of these models for describing the high strain-rate deformation of these materials. The JC and ZA models, however, due to their use of a power strain hardening law were found to yield constitutive relations for the materials which are strongly dependent on the range of strains for which the models were optimized.« less

Shrinkage strain-rates of dental resin-monomer and composite systems.

PubMed

Atai, Mohammad; Watts, David C; Atai, Zahra

2005-08-01

The purpose of this study was to investigate the shrinkage strain rate of different monomers, which are commonly used in dental composites and the effect of monomer functionality and molecular mass on the rate. Bis-GMA, TEGDMA, UDMA, MMA, HEMA, HPMA and different ratios of Bis-GMA/TEGDMA were mixed with Camphorquinone and Dimethyl aminoethyle methacrylate as initiator system. The shrinkage strain of the samples photopolymerised at Ca. 550 mW/cm2 and 23 degrees C was measured using the bonded-disk technique of Watts and Cash (Meas. Sci. Technol. 2 (1991) 788-794), and initial shrinkage-strain rates were obtained by numerical differentiation. Shrinkage-strain rates rose rapidly to a maximum, and then fell rapidly upon vitrification. Strain and initial strain rate were dependent upon monomer functionality, molecular mass and viscosity. Strain rates were correlated with Bis-GMA in Bis-GMA/TEGDMA mixtures up to 75-80 w/w%, due to the higher molecular mass of Bis-GMA affecting termination reactions, and then decreased due to its higher viscosity affecting propagation reactions. Monofunctional monomers exhibited lower rates. UDMA, a difunctional monomer of medium viscosity, showed the highest shrinkage strain rate (P < 0.05). Shrinkage strain rate, related to polymerization rate, is an important factor affecting the biomechanics and marginal integrity of composites cured in dental cavities. This study shows how this is related to monomer molecular structure and viscosity. The results are significant for the production, optimization and clinical application of dental composite restoratives.

Interference with the quorum sensing systems in a Vibrio harveyi strain alters the growth rate of gnotobiotically cultured rotifer Brachionus plicatilis.

PubMed

Tinh, N T N; Linh, N D; Wood, T K; Dierckens, K; Sorgeloos, P; Bossier, P

2007-07-01

To evaluate the effect of Vibrio harveyi strains on the growth rate of the gnotobiotically cultured rotifer Brachionus plicatilis, and to establish whether quorum sensing is involved in the observed phenomena. Gnotobiotic B. plicatilis sensu strictu, obtained by hatching glutaraldehyde-treated amictic eggs, were used as test organisms. Challenge tests were performed with 11 V. harveyi strains and different quorum sensing mutants derived from the V. harveyi BB120 strain. Brominated furanone [(5Z)-4-bromo-5-(bromomethylene)-3-butyl-2(5H)-furanone] as a quorum sensing inhibitor was tested in Brachionus challenge tests. Some V. harveyi strains, such as strain BB120, had a significantly negative effect on the Brachionus growth rate. In the challenge test with MM77, an isogenic strain of BB120 in which the two autoinducers (HAI-1 and AI-2) are both inactivated, no negative effect was observed. The effect of single mutants was the same as that observed in the BB120 strain. This indicates that both systems are responsible for the growth-retarding (GR) effect of the BB120 strain towards Brachionus. Moreover, the addition of an exogenous source of HAI-1 or AI-2 could restore the GR effect in the HAI-1 and AI-2 nonproducing mutant MM77. The addition of brominated furanone at a concentration of 2.5 mg l(-1) could neutralize the GR effect of some strains such as BB120 and VH-014. Two quorum sensing systems in V. harveyi strain BB120 (namely HAI-1 and AI-2-mediated) are necessary for its GR effect on B. plicatilis. With some other V. harveyi strains, however, growth inhibition towards Brachionus does not seem to be related to quorum sensing. Interference with the quorum sensing system might help to counteract the GR effect of some V. harveyi strains on Brachionus. However, further studies are needed to demonstrate the positive effect of halogenated furanone in nongnotobiotic Brachionus cultures and eventually, in other segments of the aquaculture industry.

Effect of high strain rates on peak stress in a Zr-based bulk metallic glass

NASA Astrophysics Data System (ADS)

Sunny, George; Yuan, Fuping; Prakash, Vikas; Lewandowski, John

2008-11-01

The mechanical behavior of Zr41.25Ti13.75Cu12.5Ni10Be22.5 (LM-1) has been extensively characterized under quasistatic loading conditions; however, its mechanical behavior under dynamic loading conditions is currently not well understood. A Split-Hopkinson pressure bar (SHPB) and a single-stage gas gun are employed to characterize the mechanical behavior of LM-1 in the strain-rate regime of 102-105/s. The SHPB experiments are conducted with a tapered insert design to mitigate the effects of stress concentrations and preferential failure at the specimen-insert interface. The higher strain-rate plate-impact compression-and-shear experiments are conducted by impacting a thick tungsten carbide (WC) flyer plate with a sandwich sample comprising a thin bulk metallic glass specimen between two thicker WC target plates. Specimens employed in the SHPB experiments failed in the gage-section at a peak stress of approximately 1.8 GPa. Specimens in the high strain-rate plate-impact experiments exhibited a flow stress in shear of approximately 0.9 GPa, regardless of the shear strain-rate. The flow stress under the plate-impact conditions was converted to an equivalent flow stress under uniaxial compression by assuming a von Mises-like material behavior and accounting for the plane strain conditions. The results of these experiments, when compared to the previous work conducted at quasistatic loading rates, indicate that the peak stress of LM-1 is essentially strain rate independent over the strain-rate range up to 105/s.

Mechanical Behavior of Glidcop Al-15 at High Temperature and Strain Rate

NASA Astrophysics Data System (ADS)

Scapin, M.; Peroni, L.; Fichera, C.

2014-05-01

Strain rate and temperature are variables of fundamental importance for the definition of the mechanical behavior of materials. In some elastic-plastic models, the effects, coming from these two quantities, are considered to act independently. This approach should, in some cases, allow to greatly simplify the experimental phase correlated to the parameter identification of the material model. Nevertheless, in several applications, the material is subjected to dynamic load at very high temperature, as, for example, in case of machining operation or high energy deposition on metals. In these cases, to consider the effect of strain rate and temperature decoupled could not be acceptable. In this perspective, in this work, a methodology for testing materials varying both strain rate and temperature was described and applied for the mechanical characterization of Glidcop Al-15, a copper-based composite reinforced with alumina dispersion, often used in nuclear applications. The tests at high strain rate were performed using the Hopkinson Bar setup for the direct tensile tests. The heating of the specimen was performed using an induction coil system and the temperature was controlled on the basis of signals from thermocouples directly welded on the specimen surface. Varying the strain rate, Glidcop Al-15 shows a moderate strain-rate sensitivity at room temperature, while it considerably increases at high temperature: material thermal softening and strain-rate hardening are strongly coupled. The experimental data were fitted using a modified formulation of the Zerilli-Armstrong model able to reproduce this kind of behavior with a good level of accuracy.

Effect of Strain Rate on Hot Ductility Behavior of a High Nitrogen Cr-Mn Austenitic Steel

NASA Astrophysics Data System (ADS)

Wang, Zhenhua; Meng, Qing; Qu, Minggui; Zhou, Zean; Wang, Bo; Fu, Wantang

2016-03-01

18Mn18Cr0.6N steel specimens were tensile tested between 1173 K and 1473 K (900 °C and 1200 °C) at 9 strain rates ranging from 0.001 to 10 s-1. The tensile strained microstructures were analyzed through electron backscatter diffraction analysis. The strain rate was found to affect hot ductility by influencing the strain distribution, the extent of dynamic recrystallization and the resulting grain size, and dynamic recovery. The crack nucleation sites were primarily located at grain boundaries and were not influenced by the strain rate. At 1473 K (1200 °C), a higher strain rate was beneficial for grain refinement and preventing hot cracking; however, dynamic recovery appreciably occurred at 0.001 s-1 and induced transgranular crack propagation. At 1373 K (1100 °C), a high extent of dynamic recrystallization and fine new grains at medium strain rates led to good hot ductility. The strain gradient from the interior of the grain to the grain boundary increased with decreasing strain rate at 1173 K and 1273 K (900 °C and 1000 °C), which promoted hot cracking. Grain boundary sliding accompanied grain rotation and did not contribute to hot cracking.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Song, Bo; Nelson, Kevin; Lipinski, Ronald

In this study, conventional Kolsky tension bar techniques were modified to characterize an iridium alloy in tension at elevated strain rates and temperatures. The specimen was heated to elevated temperatures with an induction coil heater before dynamic loading; whereas, a cooling system was applied to keep the bars at room temperature during heating. A preload system was developed to generate a small pretension load in the bar system during heating in order to compensate for the effect of thermal expansion generated in the high-temperature tensile specimen. A laser system was applied to directly measure the displacements at both ends ofmore » the tensile specimen in order to calculate the strain in the specimen. A pair of high-sensitivity semiconductor strain gages was used to measure the weak transmitted force due to the low flow stress in the thin specimen at elevated temperatures. The dynamic high-temperature tensile stress–strain curves of a DOP-26 iridium alloy were experimentally obtained at two different strain rates (~1000 and 3000 s -1) and temperatures (~750 and 1030°C). The effects of strain rate and temperature on the tensile stress–strain response of the iridium alloy were determined. Finally, the iridium alloy exhibited high ductility in stress–strain response that strongly depended on strain-rate and temperature.« less

High Strain-Rate and Temperature Effects on the Response of Composites

NASA Technical Reports Server (NTRS)

Gilat, Amos

2004-01-01

The objective of the research is to expand the experimental study of the effect of strain rate on mechanical response (deformation and failure) of epoxy resins and carbon fibers/epoxy matrix composites, to include elevated temperature tests. The experimental data provide the information needed for NASA scientists for the development of a nonlinear, strain rate and temperature dependent deformation and strength models for composites that can subsequently be used in design. This year effort was directed into the development and testing of the epoxy resin at elevated temperatures. Two types of epoxy resins were tested in shear at high strain rates of about 700 per second and elevated temperatures of 50 and 80 C. The results show that the temperature significantly affects the response of epoxy.

Effects of the Strain Rate and Temperature on the Microstructural Evolution of Twin-Rolled Cast Wrought AZ31B Alloys Sheets

NASA Astrophysics Data System (ADS)

Rodriguez, A. K.; Kridli, G.; Ayoub, G.; Zbib, H.

2013-10-01

This article investigates the effects of the strain rate and temperature on the microstructural evolution of twin-rolled cast wrought AZ31B sheets. This was achieved through static heating and through tensile test performed at strain rates from 10-4 to 10-1 s-1 and temperatures between room temperature (RT) and 300 °C. While brittle fracture with high stresses and limited elongation was observed at the RT, ductile behavior was obtained at higher temperatures with low strain rates. The strain rate sensitivity and activation energy calculations indicate that grain boundary diffusion and lattice diffusion are the two rate-controlling mechanisms at warm and high temperatures, respectively. An analysis of the evolution of the microstructure provided some indications of the most probable deformation mechanisms in the material: twinning operates at lower temperatures, and dynamic recrystallization dominates at higher temperatures. The static evolution of the microstructure was also studied, proving a gradual static grain growth of the AZ31B with annealing temperature and time.

Early Left and Right Ventricular Response to Aortic Valve Replacement.

PubMed

Duncan, Andra E; Sarwar, Sheryar; Kateby Kashy, Babak; Sonny, Abraham; Sale, Shiva; Alfirevic, Andrej; Yang, Dongsheng; Thomas, James D; Gillinov, Marc; Sessler, Daniel I

2017-02-01

The immediate effect of aortic valve replacement (AVR) for aortic stenosis on perioperative myocardial function is unclear. Left ventricular (LV) function may be impaired by cardioplegia-induced myocardial arrest and ischemia-reperfusion injury, especially in patients with LV hypertrophy. Alternatively, LV function may improve when afterload is reduced after AVR. The right ventricle (RV), however, experiences cardioplegic arrest without benefiting from improved loading conditions. Which of these effects on myocardial function dominate in patients undergoing AVR for aortic stenosis has not been thoroughly explored. Our primary objective is thus to characterize the effect of intraoperative events on LV function during AVR using echocardiographic measures of myocardial deformation. Second, we evaluated RV function. In this supplementary analysis of 100 patients enrolled in a clinical trial (NCT01187329), 97 patients underwent AVR for aortic stenosis. Of these patients, 95 had a standardized intraoperative transesophageal echocardiographic examination of systolic and diastolic function performed before surgical incision and repeated after chest closure. Echocardiographic images were analyzed off-line for global longitudinal myocardial strain and strain rate using 2D speckle-tracking echocardiography. Myocardial deformation assessed at the beginning of surgery was compared with the end of surgery using paired t tests corrected for multiple comparisons. LV volumes and arterial blood pressure decreased, and heart rate increased at the end of surgery. Echocardiographic images were acceptable for analysis in 72 patients for LV strain, 67 for LV strain rate, and 54 for RV strain and strain rate. In 72 patients with LV strain images, 9 patients required epinephrine, 22 required norepinephrine, and 2 required both at the end of surgery. LV strain did not change at the end of surgery compared with the beginning of surgery (difference: 0.7 [97.6% confidence interval, -0.2 to 1.5]%; P = 0.07), whereas LV systolic strain rate improved (became more negative) (-0.3 [-0.4 to -0.2] s; P < 0.001). In contrast, RV systolic strain worsened (became less negative) at the end of surgery (difference: 4.6 [3.1 to 6.0]%; P < 0.001) although RV systolic strain rate was unchanged (0.0 [97.6% confidence interval, -0.1 to 0.1]; P = 0.83). LV function improved after replacement of a stenotic aortic valve demonstrated by improved longitudinal strain rate. In contrast, RV function, assessed by longitudinal strain, was reduced.

Step width alters iliotibial band strain during running.

PubMed

Meardon, Stacey A; Campbell, Samuel; Derrick, Timothy R

2012-11-01

This study assessed the effect of step width during running on factors related to iliotibial band (ITB) syndrome. Three-dimensional (3D) kinematics and kinetics were recorded from 15 healthy recreational runners during overground running under various step width conditions (preferred and at least +/- 5% of their leg length). Strain and strain rate were estimated from a musculoskeletal model of the lower extremity. Greater ITB strain and strain rate were found in the narrower step width condition (p < 0.001, p = 0.040). ITB strain was significantly (p < 0.001) greater in the narrow condition than the preferred and wide conditions and it was greater in the preferred condition than the wide condition. ITB strain rate was significantly greater in the narrow condition than the wide condition (p = 0.020). Polynomial contrasts revealed a linear increase in both ITB strain and strain rate with decreasing step width. We conclude that relatively small decreases in step width can substantially increase ITB strain as well as strain rates. Increasing step width during running, especially in persons whose running style is characterized by a narrow step width, may be beneficial in the treatment and prevention of running-related ITB syndrome.

Dynamic strain aging in the high-temperature low-cycle fatigue of SA508 Cl. 3 forging steel

NASA Astrophysics Data System (ADS)

Lee, Byung Ho; Kim, In Sup

1995-10-01

The effect of dynamic strain aging on cyclic stress response and fatigue resistance of ASME SA508 Cl.3 forging steel for nuclear reactor pressure vessels has been evaluated in the temperature range of room temperature to 500°C. Total strain ranges and strain rates were varied from 0.7 to 2.0% and from 4 × 10 -4 to 1 × 10 -2 s -1, respectively. The cyclic stress response depended on the testing temperature, strain rate, and range. Generally, the initial cyclic hardening was immediately followed by cyclic softening at all strain rates. However, at 300°C, the operating temperature of nuclear reactor pressure vessels, the variation of cyclic stress amplitude showed the primary and secondary hardening stages dependent on the strain rate and strain range. Dynamic strain aging was manifested by enhanced cyclic hardening, distinguished secondary hardening, and negative strain rate sensitivity. A modified cell shutting model was described for the onset of the secondary hardening due to the dynamic strain aging and it was in good agreement with the experimental results. Fatigue life increased in strain rate at all testing temperatures. Specifically the fatigue life was longer at the dynamic strain aging temperature. Further, the dynamic strain aging was easy to initiate the crack, while crack propagation was retarded by crack branching and suppression of plastic zone, hence the dynamic strain aging caused the improvement of fatigue resistance.

Premixed Edge-Flames in Spatially-Varying Straining Flows

NASA Technical Reports Server (NTRS)

Liu, Jian-Bang; Ronney, Paul D.

1999-01-01

Flames subject to temporally and spatially uniform hydrodynamic strain are frequently used to model the local interactions of flame fronts with turbulent flow fields (Williams, 1985; Peters, 1986; Bradley, 1992). The applicability of laminar flamelet models in strongly turbulent flows have been questioned recently (Shay and Ronney, 1998) because in turbulent flows the strain rate (sigma) changes at rates comparable to sigma itself and the scale over which the flame front curvature and sigma changes is comparable to the curvature scale itself. Therefore quasi-static, local models of turbulent strain and curvature effects on laminar flamelets may not be accurate under conditions where the strain and curvature effects are most significant. The purpose of this study is to examine flames in spatially-varying strain and compare their properties to those of uniformly strained flames.

The Effect of Strain Rate on the Evolution of Plane Wakes Subjected to Irrotational Strains

NASA Technical Reports Server (NTRS)

Rogers, Michael M.; Merriam, Marshal (Technical Monitor)

1996-01-01

Direct numerical simulations of time-evolving turbulent plane wakes developing in the presence of irrotational plane strain applied at three different strain rates have been generated. The strain geometry is such that the flow is compressed in the streamwise direction and expanded in the cross-stream direction with the spanwise direction being unstrained. This geometry is the temporally evolving analogue of a spatially evolving wake in an adverse pressure gradient. A pseudospectral numerical method with up to 16 million modes is used to solve the equations in a reference frame moving with the irrotational strain. The initial condition for each simulation is taken from a previous turbulent self-similar plane wake direct numerical simulation at a velocity deficit Reynolds number, Re, of about 2,000. Although the evolutions of many statistics are nearly collapsed when plotted against total strain, there are some differences owing to the different strain rate histories. The impact of strain-rate on the wake spreading rate, the peak velocity deficit, the Reynolds stress profiles, and the flow structure is examined.

Studies of the physical, yield and failure behavior of aliphatic polyketones

NASA Astrophysics Data System (ADS)

Karttunen, Nicole Renee

This thesis describes an investigation into the multiaxial yield and failure behavior of an aliphatic polyketone terpolymer. The behavior is studied as a function of: stress state, strain rate, temperature, and sample processing conditions. Results of this work include: elucidation of the behavior of a recently commercialized polymer, increased understanding of the effects listed above, insight into the effects of processing conditions on the morphology of the polyketone, and a description of yield strength of this material as a function of stress state, temperature, and strain rate. The first portion of work focuses on the behavior of a set of samples that are extruded under "common" processing conditions. Following this reference set of tests, the effect of testing this material at different temperatures is studied. A total of four different temperatures are examined. In addition, the effect of altering strain rate is examined. Testing is performed under pseudo-strain rate control at constant nominal octahedral shear strain rate for each failure envelope. A total of three different rates are studied. An extension of the first portion of work involves modeling the yield envelope. This is done by combining two approaches: continuum level and molecular level. The use of both methods allows the description of the yield envelope as a function of stress state, strain rate and temperature. The second portion of work involves the effects of processing conditions. For this work, additional samples are extruded with different shear and thermal histories than the "standard" material. One set of samples is processed with shear rates higher and lower than the standard. A second set is processed at higher and lower cooling rates than the standard. In order to understand the structural cause for changes in behavior with processing conditions, morphological characterization is performed on these samples. In particular, the effect on spherulitic structure is important. Residual stresses are also determined to be important to the behavior of the samples. Finally, an investigation into the crystalline structure of a family of aliphatic polyketones is performed. The effects of side group concentration and size are described.

Ultrafine-grained Aluminm and Boron Carbide Metal Matrix Composites

NASA Astrophysics Data System (ADS)

Vogt, Rustin

Cryomilling is a processing technique used to generate homogenously distributed boron carbide (B4C) particulate reinforcement within an ultrafine-grained aluminum matrix. The motivation behind characterizing a composite consisting of cryomilled aluminum B4C metal matrix composite is to design and develop a high-strength, lightweight aluminum composite for structural and high strain rate applications. Cryomilled Al 5083 and B4C powders were synthesized into bulk composite by various thermomechanical processing methods to form plate and extruded geometries. The effects of processing method on microstructure and mechanical behavior for the final consolidated composite were investigated. Cryomilling for extended periods of time in liquid nitrogen has shown to increase strength and thermal stability. The effects associated with cryomilling with stearic acid additions (as a process-control agent) on the degassing behavior of Al powders is investigated and results show that the liberation of compounds associated with stearic acid were suppressed in cryomilled Al powders. The effect of thermal expansion mismatch strain on strengthening due to geometrically necessary dislocations resulting from quenching is investigated and found not to occur in bulk cryomilled Al 5083 and B 4C composites. Previous cryomilled Al 5083 and B4C composites have exhibited ultrahigh strength associated with considerable strain-to-failure (>14 pct.) at high strain rates (>103/s) during mechanical testing, but only limited strain-to-failure (˜0.75 pct.) at quasi-static strain rates (10-3/s). The increased strain to failure at high strain rates is attributed to micro-flaw developments, including kinking, extensive axial splitting, and grain growth were observed after high strain rate deformation, and the significance of these mechanisms is considered.

Strain Rate and Anisotropic Microstructure Dependent Mechanical Behaviors of Silkworm Cocoon Shells

PubMed Central

Xu, Jun; Zhang, Wen; Gao, Xiang; Meng, Wanlin; Guan, Juan

2016-01-01

Silkworm cocoons are multi-layered composite structures comprised of high strength silk fiber and sericin, and their mechanical properties have been naturally selected to protect pupas during metamorphosis from various types of external attacks. The present study attempts to gain a comprehensive understanding of the mechanical properties of cocoon shell materials from wild silkworm species Antheraea pernyi under dynamic loading rates. Five dynamic strain rates from 0.00625 s-1 to 12.5 s-1 are tested to show the strain rate sensitivity of the cocoon shell material. In the meantime, the anisotropy of the cocoon shell is considered and the cocoon shell specimens are cut along 0°, 45° and 90° orientation to the short axis of cocoons. Typical mechanical properties including Young’s modulus, yield strength, ultimate strength and ultimate strain are extracted and analyzed from the stress-strain curves. Furthermore, the fracture morphologies of the cocoon shell specimens are observed under scanning electron microscopy to help understand the relationship between the mechanical properties and the microstructures of the cocoon material. A discussion on the dynamic strain rate effect on the mechanical properties of cocoon shell material is followed by fitting our experimental results to two previous models, and the effect could be well explained. We also compare natural and dried cocoon materials for the dynamic strain rate effect and interestingly the dried cocoon shells show better overall mechanical properties. This study provides a different perspective on the mechanical properties of cocoon material as a composite material, and provides some insight for bio-inspired engineering materials. PMID:26939063

Effect of loading rate on the monotonic tensile behavior of a continuous-fiber-reinforced glass-ceramic matrix composite

DOE Office of Scientific and Technical Information (OSTI.GOV)

Soerensen, B.F.; Holmes, J.W.

The stress-strain behavior of a continuous-fiber-reinforced ceramic matrix composite has been measured over a wide range of loading rates (0.01 to 500 MPa/s). It was found that the loading rate has a strong effect on almost every feature of the stress-strain curve: the proportionality stress, the composite strength and failure strain increase with increasing loading rate. The microstructural damage varies also with the loading rate; with increasing loading rate, the average matrix crack spacing increases and the average fiber pullout length decreases. Using simple models, it is suggested that these phenomena are caused partly by time-dependent matrix cracking (due tomore » stress corrosion) and partly by an increasing interfacial shear stress with loading rate.« less

The Effect of Ivermectin in Seven Strains of Aedes aegypti (Diptera: Culicidae) Including a Genetically Diverse Laboratory Strain and Three Permethrin Resistant Strains

PubMed Central

Deus, K. M.; Saavedra-rodriguez, K.; Butters, M. P.; Black, W. C.; Foy, B. D.

2014-01-01

Seven different strains of Aedes aegypti (L.), including a genetically diverse laboratory strain, three laboratory-selected permethrin-resistant strains, a standard reference strain, and two recently colonized strains were fed on human blood containing various concentrations of ivermectin. Ivermectin reduced adult survival, fecundity, and hatch rate of eggs laid by ivermectin-treated adults in all seven strains. The LC50 of ivermectin for adults and the concentration that prevented 50% of eggs from hatching was calculated for all strains. Considerable variation in adult survival after an ivermectin-bloodmeal occurred among strains, and all three permethrin-resistant strains were significantly less susceptible to ivermectin than the standard reference strain. The hatch rate after an ivermectin bloodmeal was less variable among strains, and only one of the permethrin-resistant strains differed significantly from the standard reference strain. Our studies suggest that ivermectin induces adult mortality and decreases the hatch rate of eggs through different mechanisms. A correlation analysis of log-transformed LC50 among strains suggests that permethrin and ivermectin cross-resistance may occur. PMID:22493855

Computational micromechanics of dynamic compressive loading of a brittle polycrystalline material using a distribution of grain boundary properties

NASA Astrophysics Data System (ADS)

Kraft, R. H.; Molinari, J. F.; Ramesh, K. T.; Warner, D. H.

A two-dimensional finite element model is used to investigate compressive loading of a brittle ceramic. Intergranular cracking in the microstructure is captured explicitly by using a distribution of cohesive interfaces. The addition of confining stress increases the maximum strength and if high enough, can allow the effective material response to reach large strains before failure. Increasing the friction at the grain boundaries also increases the maximum strength until saturation of the strength is approached. Above a transitional strain rate, increasing the rate-of-deformation also increases the strength and as the strain rate increases, fragment sizes of the damaged specimen decrease. The effects of flaws within the specimen were investigated using a random distribution at various initial flaw densities. The model is able to capture an effective modulus change and degradation of strength as the initial flaw density increases. Effects of confinement, friction, and spatial distribution of flaws seem to depend on the crack coalescence and dilatation of the specimen, while strain-rate effects are result of inertial resistance to motion.

Strain rate effect on fault slip and rupture evolution: Insight from meter-scale rock friction experiments

NASA Astrophysics Data System (ADS)

Xu, Shiqing; Fukuyama, Eiichi; Yamashita, Futoshi; Mizoguchi, Kazuo; Takizawa, Shigeru; Kawakata, Hironori

2018-05-01

We conduct meter-scale rock friction experiments to study strain rate effect on fault slip and rupture evolution. Two rock samples made of Indian metagabbro, with a nominal contact dimension of 1.5 m long and 0.1 m wide, are juxtaposed and loaded in a direct shear configuration to simulate the fault motion. A series of experimental tests, under constant loading rates ranging from 0.01 mm/s to 1 mm/s and under a fixed normal stress of 6.7 MPa, are performed to simulate conditions with changing strain rates. Load cells and displacement transducers are utilized to examine the macroscopic fault behavior, while high-density arrays of strain gauges close to the fault are used to investigate the local fault behavior. The observations show that the macroscopic peak strength, strength drop, and the rate of strength drop can increase with increasing loading rate. At the local scale, the observations reveal that slow loading rates favor generation of characteristic ruptures that always nucleate in the form of slow slip at about the same location. In contrast, fast loading rates can promote very abrupt rupture nucleation and along-strike scatter of hypocenter locations. At a given propagation distance, rupture speed tends to increase with increasing loading rate. We propose that a strain-rate-dependent fault fragmentation process can enhance the efficiency of fault healing during the stick period, which together with healing time controls the recovery of fault strength. In addition, a strain-rate-dependent weakening mechanism can be activated during the slip period, which together with strain energy selects the modes of fault slip and rupture propagation. The results help to understand the spectrum of fault slip and rock deformation modes in nature, and emphasize the role of heterogeneity in tuning fault behavior under different strain rates.

The effect of abdominal pressure on urinary flow rate.

PubMed

Hasegawa, N; Kitagawa, Y; Takasaki, N; Miyazaki, S

1983-07-01

We examined the effect of abdominal pressure on urinary flow rate and urethral closure pressure in 46 subjects, ranging in age from 26 to 82 years. An increase in urinary flow rate caused by abdominal straining was not found when organic obstruction was present in the prostatic urethra in men or the proximal urethra in women, or when dysuria is caused by the lowered detrusor pressure. An increase in urinary flow rate caused by straining was noted when anterior urethral stricture or stress incontinence was present. The increase in urinary flow rate owing to straining was undetermined in the control group. The urethral closure pressure on the anti-stress incontinence zone increased as a result of straining at the same time and to the same degree as did the intravesical pressure. When the anti-stress incontinence zone was subjected to transurethral resection for canal formation urination became possible as a result of straining. The patients who were able to urinate with straining sometimes suffered temporary stress incontinence. The degree of straining did not determine whether the patient could urinate with straining. Therefore, it was concluded that abdominal pressure should be excluded from intravesical pressure in performing several urodynamic studies on the lower urinary tract, such as pressure flow studies, and that it is important to have a sufficient canal formation in the anti-stress incontinence zone when urination with straining is expected when performing an operation on patients with urethral obstruction in the anti-stress incontinence zone.

A Combined Precipitation, Yield Stress, and Work Hardening Model for Al-Mg-Si Alloys Incorporating the Effects of Strain Rate and Temperature

NASA Astrophysics Data System (ADS)

Myhr, Ole Runar; Hopperstad, Odd Sture; Børvik, Tore

2018-05-01

In this study, a combined precipitation, yield strength, and work hardening model for Al-Mg-Si alloys known as NaMo has been further developed to include the effects of strain rate and temperature on the resulting stress-strain behavior. The extension of the model is based on a comprehensive experimental database, where thermomechanical data for three different Al-Mg-Si alloys are available. In the tests, the temperature was varied between 20 °C and 350 °C with strain rates ranging from 10-6 to 750 s-1 using ordinary tension tests for low strain rates and a split-Hopkinson tension bar system for high strain rates, respectively. This large span in temperatures and strain rates covers a broad range of industrial relevant problems from creep to impact loading. Based on the experimental data, a procedure for calibrating the different physical parameters of the model has been developed, starting with the simplest case of a stable precipitate structure and small plastic strains, from which basic kinetic data for obstacle limited dislocation glide were extracted. For larger strains, when work hardening becomes significant, the dynamic recovery was linked to the Zener-Hollomon parameter, again using a stable precipitate structure as a basis for calibration. Finally, the complex situation of concurrent work hardening and dynamic evolution of the precipitate structure was analyzed using a stepwise numerical solution algorithm where parameters representing the instantaneous state of the structure were used to calculate the corresponding instantaneous yield strength and work hardening rate. The model was demonstrated to exhibit a high degree of predictive power as documented by a good agreement between predictions and measurements, and it is deemed well suited for simulations of thermomechanical processing of Al-Mg-Si alloys where plastic deformation is carried out at various strain rates and temperatures.

Constitutive behavior of tantalum and tantalum-tungsten alloys

DOE Office of Scientific and Technical Information (OSTI.GOV)

Chen, S.R.; Gray, G.T. III

1996-10-01

The effects of strain rate, temperature, and tungsten alloying on the yield stress and the strain-hardening behavior of tantalum were investigated. The yield and flow stresses of unalloyed Ta and tantalum-tungsten alloys were found to exhibit very high rate sensitivities, while the hardening rates in Ta and Ta-W alloys were found to be insensitive to strain rate and temperature at lower temperatures or at higher strain rates. This behavior is consistent with the observation that overcoming the intrinsic Peierls stress is shown to be the rate-controlling mechanism in these materials at low temperatures. The dependence of yield stress on temperaturemore » and strain rate was found to decrease, while the strain-hardening rate increased with tungsten alloying content. The mechanical threshold stress (MTS) model was adopted to model the stress-strain behavior of unalloyed Ta and the Ta-W alloys. Parameters for the constitutive relations for Ta and the Ta-W alloys were derived for the MTS model, the Johnson-Cook (JC), and the Zerilli-Armstrong (ZA) models. The results of this study substantiate the applicability of these models for describing the high strain-rate deformation of Ta and Ta-W alloys. The JC and ZA models, however, due to their use of a power strain-hardening law, were found to yield constitutive relations for Ta and Ta-W alloys that are strongly dependent on the range of strains for which the models were optimized.« less

Large Strain Behaviour of ZEK100 Magnesium Alloy at Various Strain Rates

NASA Astrophysics Data System (ADS)

Lévesque, Julie; Kurukuri, Srihari; Mishra, Raja; Worswick, Michael; Inal, Kaan

A constitutive framework based on a rate-dependent crystal plasticity theory is employed to simulate large strain deformation in hexagonal closed-packed metals that deform by slip and twinning. The model allows the twinned zones and the parent matrix to rotate independently. ZEK100 magnesium alloy sheets which significant texture weakening compared to AZ31 sheets are investigated using the model. There is considerable in-plane anisotropy and tension compression asymmetry in the flow behavior of ZEK100. Simulations of uniaxial tension in different directions at various strain rates and the accompanying texture evolution are performed and they are in very good agreement with experimental measurements. The effect of strain rate on the activation of the various slip systems and twinning show that differences in the strain rate dependence of yield stress and Rvalues in ZEK100 have their origin in the activation of different deformation mechanisms.

Microstructure and Strain Rate-Dependent Tensile Deformation Behavior of Fiber Laser-Welded Butt Joints of Dual-Phase Steels

NASA Astrophysics Data System (ADS)

Liu, Yang; Dong, Danyang; Han, Zhiqiang; Yang, Zhibin; Wang, Lu; Dong, Qingwei

2018-05-01

The microstructure and tensile deformation behavior of the fiber laser-welded similar and dissimilar dual-phase (DP) steel joints over a wide range of strain rates from 10-3 to 103 s-1 were investigated for the further applications on the lightweight design of vehicles. The high strain rate dynamic tensile deformation process and full-field strain distribution of the base metals and welded joints were examined using the digital image correlation method and high-speed photography. The strain rate effects on the stress-strain responses, tensile properties, deformation, and fracture behavior of the investigated materials were analyzed. The yield stress (YS) and ultimate tensile strength (UTS) of the dissimilar DP780/DP980 welded joints were lying in-between those of the DP780 and DP980 base metals, and all materials exhibited positive strain rate dependence on the YS and UTS. Owing to the microstructure heterogeneity, the welded joints showed relatively lower ductility in terms of total elongation (TE) than those of the corresponding base metals. The strain localization started before the maximum load was reached, and the strain localization occurred earlier during the whole deformation process with increasing strain rate. As for the dissimilar welded joint, the strain localization tended to occur in the vicinity of the lowest hardness value across the welded joint, which was in the subcritical HAZ at the DP780 side. As the strain rate increased, the typical ductile failure characteristic of the investigated materials did not change.

Microstructure and Strain Rate-Dependent Tensile Deformation Behavior of Fiber Laser-Welded Butt Joints of Dual-Phase Steels

NASA Astrophysics Data System (ADS)

Liu, Yang; Dong, Danyang; Han, Zhiqiang; Yang, Zhibin; Wang, Lu; Dong, Qingwei

2018-04-01

The microstructure and tensile deformation behavior of the fiber laser-welded similar and dissimilar dual-phase (DP) steel joints over a wide range of strain rates from 10-3 to 103 s-1 were investigated for the further applications on the lightweight design of vehicles. The high strain rate dynamic tensile deformation process and full-field strain distribution of the base metals and welded joints were examined using the digital image correlation method and high-speed photography. The strain rate effects on the stress-strain responses, tensile properties, deformation, and fracture behavior of the investigated materials were analyzed. The yield stress (YS) and ultimate tensile strength (UTS) of the dissimilar DP780/DP980 welded joints were lying in-between those of the DP780 and DP980 base metals, and all materials exhibited positive strain rate dependence on the YS and UTS. Owing to the microstructure heterogeneity, the welded joints showed relatively lower ductility in terms of total elongation (TE) than those of the corresponding base metals. The strain localization started before the maximum load was reached, and the strain localization occurred earlier during the whole deformation process with increasing strain rate. As for the dissimilar welded joint, the strain localization tended to occur in the vicinity of the lowest hardness value across the welded joint, which was in the subcritical HAZ at the DP780 side. As the strain rate increased, the typical ductile failure characteristic of the investigated materials did not change.

Mechanical and Infrared Thermography Analysis of Shape Memory Polyurethane

NASA Astrophysics Data System (ADS)

Pieczyska, Elzbieta Alicja; Maj, Michal; Kowalczyk-Gajewska, Katarzyna; Staszczak, Maria; Urbanski, Leszek; Tobushi, Hisaaki; Hayashi, Shunichi; Cristea, Mariana

2014-07-01

Multifunctional new material—polyurethane shape memory polymer (PU-SMP)—was subjected to tension carried out at room temperature at various strain rates. The influence of effects of thermomechanical couplings on the SMP mechanical properties was studied, based on the sample temperature changes, measured by a fast and sensitive infrared camera. It was found that the polymer deformation process strongly depends on the strain rate applied. The initial reversible strain is accompanied by a small drop in temperature, called thermoelastic effect. Its maximal value is related to the SMP yield point and increases upon increase of the strain rate. At higher strains, the stress and temperature significantly increase, caused by reorientation of the polymer molecular chains, followed by the stress drop and its subsequent increase accompanying the sample rupture. The higher strain rate, the higher stress, and temperature changes were obtained, since the deformation process was more dynamic and has occurred in almost adiabatic conditions. The constitutive model of SMP valid in finite strain regime was developed. In the proposed approach, SMP is described as a two-phase material composed of hyperelastic rubbery phase and elastic-viscoplastic glassy phase, while the volume content of phases is specified by the current temperature.

Effect of strain rate and dislocation density on the twinning behavior in tantalum

DOE Office of Scientific and Technical Information (OSTI.GOV)

Florando, Jeffrey N., E-mail: florando1@llnl.gov; Swift, Damian C.; Barton, Nathan R.

2016-04-15

The conditions which affect twinning in tantalum have been investigated across a range of strain rates and initial dislocation densities. Tantalum samples were subjected to a range of strain rates, from 10{sup −4}/s to 10{sup 3}/s under uniaxial stress conditions, and under laser-induced shock-loading conditions. In this study, twinning was observed at 77 K at strain rates from 1/s to 10{sup 3}/s, and during laser-induced shock experiments. The effect of the initial dislocation density, which was imparted by deforming the material to different amounts of pre-strain, was also studied, and it was shown that twinning is suppressed after a givenmore » amount of pre-strain, even as the global stress continues to increase. These results indicate that the conditions for twinning cannot be represented solely by a critical global stress value, but are also dependent on the evolution of the dislocation density. In addition, the analysis shows that if twinning is initiated, the nucleated twins may continue to grow as a function of strain, even as the dislocation density continues to increase.« less

Effect of Strain Rate on Joint Strength and Failure Mode of Lead-Free Solder Joints

NASA Astrophysics Data System (ADS)

Lin, Jian; Lei, Yongping; Fu, Hanguang; Guo, Fu

2018-03-01

In surface mount technology, the Sn-3.0Ag-0.5Cu solder joint has a shorter impact lifetime than a traditional lead-tin solder joint. In order to improve the impact property of SnAgCu lead-free solder joints and identify the effect of silver content on tensile strength and impact property, impact experiments were conducted at various strain rates on three selected SnAgCu based solder joints. It was found that joint failure mainly occurred in the solder material with large plastic deformation under low strain rate, while joint failure occurred at the brittle intermetallic compound layer without any plastic deformation at a high strain rate. Joint strength increased with the silver content in SnAgCu alloys in static tensile tests, while the impact property of the solder joint decreased with increasing silver content. When the strain rate was low, plastic deformation occurred with failure and the tensile strength of the Sn-3.0Ag-0.5Cu solder joint was higher than that of Sn-0.3Ag-0.7Cu; when the strain rate was high, joint failure mainly occurred at the brittle interface layer and the Sn-0.3Ag-0.7Cu solder joint had a better impact resistance with a thinner intermetallic compound layer.

Strain Rate Sensitivity of Epoxy Resin in Tensile and Shear Loading

NASA Technical Reports Server (NTRS)

Gilat, Amos; Goldberg, Robert K.; Roberts, Gary D.

2005-01-01

The mechanical response of E-862 and PR-520 resins is investigated in tensile and shear loadings. At both types of loading the resins are tested at strain rates of about 5x10(exp 5), 2, and 450 to 700 /s. In addition, dynamic shear modulus tests are carried out at various frequencies and temperatures, and tensile stress relaxation tests are conducted at room temperature. The results show that the toughened PR-520 resin can carry higher stresses than the untoughened E-862 resin. Strain rate has a significant effect on the response of both resins. In shear both resins show a ductile response with maximum stress that is increasing with strain rate. In tension a ductile response is observed at low strain rate (approx. 5x10(exp 5) /s), and brittle response is observed at the medium and high strain rates (2, and 700 /s). The hydrostatic component of the stress in the tensile tests causes premature failure in the E-862 resin. Localized deformation develops in the PR-520 resin when loaded in shear. An internal state variable constitutive model is proposed for modeling the response of the resins. The model includes a state variable that accounts for the effect of the hydrostatic component of the stress on the deformation.

The effects of interstitial content and annealing on the flow and fracture behavior on polycrystalline beta-NiAl

NASA Technical Reports Server (NTRS)

Weaver, M. L.; Levit, V.; Kaufman, M. J.; Noebe, R. D.

1994-01-01

The strain behavior of three polycrystalline NiAl alloys has been investigated at temperatures between 300 and 1200 K. Yield stress plateaus, yield stress transients upon a ten-fold increase in strain rate, work hardening peaks, and dips in the strain rate sensitivity (SRS) have been observed between 700 and 800 K. These observations are indicative of dynamic strain aging (DSA) and are discussed in terms of conventional strain aging theories.

The Effect of Grain Size on the Strain Hardening Behavior for Extruded ZK61 Magnesium Alloy

NASA Astrophysics Data System (ADS)

Zhang, Lixin; Zhang, Wencong; Chen, Wenzhen; Duan, Junpeng; Wang, Wenke; Wang, Erde

2017-12-01

The effects of grain size on the tensile and compressive strain hardening behaviors for extruded ZK61 alloys have been investigated by uniaxial tensile and compressive tests along the extrusion directions. Cylindrical tension and compression specimens of extruded ZK61 alloys with various sized grain were fabricated by annealing treatments. Tensile and compressive tests at ambient temperature were conducted at a strain rate of 0.5 × 10-3 s-1. The results indicate that both tensile strain hardening and compressive strain hardening of ZK61 alloys with different grain sizes have an athermal regime of dislocation accumulation in early deformation. The threshold stress value caused dynamic recovery is predominantly related to grain size in tensile strain hardening, but the threshold stress values for different grain sizes are almost identical in compressive strain hardening. There are obvious transition points on the tensile strain hardening curves which indicate the occurrence of dynamic recrystallization (DRX). The tensile strain hardening rate of the coarse-grained alloy obviously decreases faster than that of fine-grained alloys before DRX and the tensile strain hardening curves of different grain sizes basically tend to parallel after DRX. The compressive strain hardening rate of the fine-grained alloy obviously increases faster than that of coarse-grained alloy for twin-induced strain hardening, but compressive strain hardening curves also tend to parallel after twinning is exhausted.

Global stability analysis of two-strain epidemic model with bilinear and non-monotone incidence rates

NASA Astrophysics Data System (ADS)

Baba, Isa Abdullahi; Hincal, Evren

2017-05-01

In this article we studied an epidemic model consisting of two strains with different types of incidence rates; bilinear and non-monotone. The model consists of four equilibrium points: disease-free equilibrium, endemic with respect to strain 1, endemic with respect to strain 2, and endemic with respect to both strains. The global stability analysis of the equilibrium points was carried out through the use of Lyapunov functions. Two basic reproduction ratios R 1 0 and R 2 0 are found, and we have shown that if both are less than one, the disease dies out, and if both are greater than one epidemic occurs. Furthermore, epidemics occur with respect to any strain with a basic reproduction ratio greater than one and disease dies out with respect to any strain with a basic reproduction ratio less than one. It was also shown that any strain with highest basic reproduction ratio will automatically outperform the other strain, thereby eliminating it. Numerical simulations were carried out to support the analytic result and to show the effect of the parameter k in the non-monotone incidence rate, which describes the psychological effect of general public towards infection.

Effect of Strain Rates on the Compressive Response of Neck Rubber From Humanetics HIII 50th Percentile Male Dummy Under Different Loading Sequences

DTIC Science & Technology

2013-02-01

diene monomer ( EPDM ) rubber under high-rate uniaxial compression using an SHPB (5). Additionally, Song and Chen used a strain energy-based function to...describe a one-dimensional constitutive relation to describe the high strain rate behavior of the EPDM rubber , which agreed with the experimental...intermediate rate to about 6 MPa at 500 s -1 . This behavior and rate dependence was similar to the EPDM rubber studied by Chen and Zhang (2), which

The Dynamic Flow and Failure Behavior of Magnesium and Magnesium Alloys

NASA Astrophysics Data System (ADS)

Eswar Prasad, K.; Li, B.; Dixit, N.; Shaffer, M.; Mathaudhu, S. N.; Ramesh, K. T.

2014-01-01

We review the dynamic behavior of magnesium alloys through a survey of the literature and a comparison with our own high-strain-rate experiments. We describe high-strain-rate experiments (at typical strain rates of 103 s-1) on polycrystalline pure magnesium as well as two magnesium alloys, AZ31B and ZK60. Both deformation and failure are considered. The observed behaviors are discussed in terms of the fundamental deformation and failure mechanisms in magnesium, considering the effects of grain size, strain rate, and crystallographic texture. A comparison of current results with the literature studies on these and other Mg alloys reveals that the crystallographic texture, grain size, and alloying elements continue to have a profound influence on the high-strain-rate deformation behavior. The available data set suggests that those materials loaded so as to initiate extension twinning have relatively rate-insensitive strengths up to strain rates of several thousand per second. In contrast, some rate dependence of the flow stress is observed for loading orientations in which the plastic flow is dominated by dislocation mechanisms.

Complex strain fields

NASA Astrophysics Data System (ADS)

Bradshaw, P.

Computational techniques for accounting for extra strain rates, abnormal distributions of delta-U/delta-y, fluctuating strain rates, and the effects of body forces in modeling shear flows are discussed. Consideration is given to simple shears where the extra strain rate does not affect turbulence, thin shear layers, moderately thin shear layers, and strongly distorted flows. Attention is given to formulations based on the exact transport equations for Reynolds stress as derived from the time-averaged Navier-Stokes equations. Extra strain rates arise from curvature, lateral divergence, and bulk compression, with Coriolis forces accounting for the first, intensification of the spanwise vorticity for the second, and compression or dilation of the shear layer producing the third. The curvature forces, e.g., buoyancy and Coriolis forces, are responsible for hurricanes and tornadoes.

Influence of strain rate and temperature on the mechanical behavior of iron aluminide-based alloys

DOE Office of Scientific and Technical Information (OSTI.GOV)

Gray, G.T.

Iron aluminides are receiving increasing attention as potential high temperature structural materials due to their excellent oxidation and sulfidation resistance. Although the influence of strain rate on the microstructure/property relationships of pure iron and a variety of iron alloys and steels has been extensively studied, the effect of strain rate on the stress-strain and deformation response of iron aluminides remains poorly understood. In this paper the influence of strain rate, varied between 0.001 and 10{sup 4} s{sup {minus}1}, and temperature, between 77 & 1073{degree}K, on the mechanical behavior of Fe-40Al-0.1B and Fe-16.12Al-5.44Cr-0.11Zr-0.13C-1.07Mo-006Y, called FAP-Y, (both in at.%) is presented. Themore » rate sensitivity and work hardening of Fe-40Al and the disordered alloy based on Fe-16% Al are discussed as a function of strain rate and temperature.« less

Dynamic High-Temperature Tensile Characterization of an Iridium Alloy with Kolsky Tension Bar Techniques

DOE PAGES

Song, Bo; Nelson, Kevin; Lipinski, Ronald; ...

2015-05-29

In this study, conventional Kolsky tension bar techniques were modified to characterize an iridium alloy in tension at elevated strain rates and temperatures. The specimen was heated to elevated temperatures with an induction coil heater before dynamic loading; whereas, a cooling system was applied to keep the bars at room temperature during heating. A preload system was developed to generate a small pretension load in the bar system during heating in order to compensate for the effect of thermal expansion generated in the high-temperature tensile specimen. A laser system was applied to directly measure the displacements at both ends ofmore » the tensile specimen in order to calculate the strain in the specimen. A pair of high-sensitivity semiconductor strain gages was used to measure the weak transmitted force due to the low flow stress in the thin specimen at elevated temperatures. The dynamic high-temperature tensile stress–strain curves of a DOP-26 iridium alloy were experimentally obtained at two different strain rates (~1000 and 3000 s -1) and temperatures (~750 and 1030°C). The effects of strain rate and temperature on the tensile stress–strain response of the iridium alloy were determined. Finally, the iridium alloy exhibited high ductility in stress–strain response that strongly depended on strain-rate and temperature.« less

Modeling the effects of strain profiles and defects on precessional magnetic switching in multiferroic heterostructures

NASA Astrophysics Data System (ADS)

Chavez, Andres C.; Kundu, Auni A.; Lynch, Christopher S.; Carman, Gregory P.

2018-03-01

Strain-mediated multiferroic heterostructures relying on fast 180° precessional magnetic switching have been proposed as a pathway for energy efficient and high density memory/logic devices. However, proper device performance requires precisely timed high frequency ( GHz) voltage pulses dependent on the magnetization dynamics of the structure. In turn, the dynamic response of the device is greatly influenced by the device geometry, strain amplitude, and strain rate. Hence, we study the effects of increasing the voltage amplitude and application rate on the in-plane magnetization dynamics of a single-domain CoFeB ellipse (100 nm x 80 nm x 6 nm) on a 500 nm thick PZT substrate in addition to studying defects in the geometry. Both a coupled micromagnetics, electrostatics and elastodynamics finite element model and a conventional micromagnetics software was used to study the strain-induced magnetic response of the CoFeB ellipse. Both models predict increased 90° magnetic reorientation speed with increased strain amplitude and rate. However, the fully-coupled model predicts slower reorientation and incoherency in comparison to the uncoupled model. This occurs because the fully-coupled model can capture the expected strain gradients of a fabricated device while the micromagnetics model can only represent uniform strain states. Additional studies which introduce geometric defects result in faster precessional motion under the same strain amplitude and rate. This is attributed to localized changes in the magnetization that influence neighboring regions via exchange and demagnetization effects. The results of these studies can help design better devices that will be less sensitive to defects and voltage applications for future strain-mediated multiferroic devices.

Effects of Temperature and Strain Rate on Tensile Deformation Behavior of 9Cr-0.5Mo-1.8W-VNb Ferritic Heat-Resistant Steel

NASA Astrophysics Data System (ADS)

Guo, Xiaofeng; Weng, Xiaoxiang; Jiang, Yong; Gong, Jianming

2017-09-01

A series of uniaxial tensile tests were carried out at different strain rate and different temperatures to investigate the effects of temperature and strain rate on tensile deformation behavior of P92 steel. In the temperature range of 30-700 °C, the variations of flow stress, average work-hardening rate, tensile strength and ductility with temperature all show three temperature regimes. At intermediate temperature, the material exhibited the serrated flow behavior, the peak in flow stress, the maximum in average work-hardening rate, and the abnormal variations in tensile strength and ductility indicates the occurrence of DSA, whereas the sharp decrease in flow stress, average work-hardening rate as well as strength values, and the remarkable increase in ductility values with increasing temperature from 450 to 700 °C imply that dynamic recovery plays a dominant role in this regime. Additionally, for the temperature ranging from 550 to 650 °C, a significant decrease in flow stress values is observed with decreasing in strain rate. This phenomenon suggests the strain rate has a strong influence on flow stress. Based on the experimental results above, an Arrhenius-type constitutive equation is proposed to predict the flow stress.

Grain-size-independent plastic flow at ultrahigh pressures and strain rates.

PubMed

Park, H-S; Rudd, R E; Cavallo, R M; Barton, N R; Arsenlis, A; Belof, J L; Blobaum, K J M; El-dasher, B S; Florando, J N; Huntington, C M; Maddox, B R; May, M J; Plechaty, C; Prisbrey, S T; Remington, B A; Wallace, R J; Wehrenberg, C E; Wilson, M J; Comley, A J; Giraldez, E; Nikroo, A; Farrell, M; Randall, G; Gray, G T

2015-02-13

A basic tenet of material science is that the flow stress of a metal increases as its grain size decreases, an effect described by the Hall-Petch relation. This relation is used extensively in material design to optimize the hardness, durability, survivability, and ductility of structural metals. This Letter reports experimental results in a new regime of high pressures and strain rates that challenge this basic tenet of mechanical metallurgy. We report measurements of the plastic flow of the model body-centered-cubic metal tantalum made under conditions of high pressure (>100  GPa) and strain rate (∼10(7)  s(-1)) achieved by using the Omega laser. Under these unique plastic deformation ("flow") conditions, the effect of grain size is found to be negligible for grain sizes >0.25  μm sizes. A multiscale model of the plastic flow suggests that pressure and strain rate hardening dominate over the grain-size effects. Theoretical estimates, based on grain compatibility and geometrically necessary dislocations, corroborate this conclusion.

Mapping strain rate dependence of dislocation-defect interactions by atomistic simulations

PubMed Central

Fan, Yue; Osetskiy, Yuri N.; Yip, Sidney; Yildiz, Bilge

2013-01-01

Probing the mechanisms of defect–defect interactions at strain rates lower than 106 s−1 is an unresolved challenge to date to molecular dynamics (MD) techniques. Here we propose an original atomistic approach based on transition state theory and the concept of a strain-dependent effective activation barrier that is capable of simulating the kinetics of dislocation–defect interactions at virtually any strain rate, exemplified within 10−7 to 107 s−1. We apply this approach to the problem of an edge dislocation colliding with a cluster of self-interstitial atoms (SIAs) under shear deformation. Using an activation–relaxation algorithm [Kushima A, et al. (2009) J Chem Phys 130:224504], we uncover a unique strain-rate–dependent trigger mechanism that allows the SIA cluster to be absorbed during the process, leading to dislocation climb. Guided by this finding, we determine the activation barrier of the trigger mechanism as a function of shear strain, and use that in a coarse-graining rate equation formulation for constructing a mechanism map in the phase space of strain rate and temperature. Our predictions of a crossover from a defect recovery at the low strain-rate regime to defect absorption behavior in the high strain-rate regime are validated against our own independent, direct MD simulations at 105 to 107 s−1. Implications of the present approach for probing molecular-level mechanisms in strain-rate regimes previously considered inaccessible to atomistic simulations are discussed. PMID:24114271

The Effects of Elevated Temperatures on the Response of Resins Under Dynamic and Static Loadings

NASA Technical Reports Server (NTRS)

Gilat, Amos

2005-01-01

The overall objective of the research is to experimentally study the combined effects of temperature and strain rate on the response of two resins that are commonly used for the matrix material in composites. The resins are loaded at various temperatures in shear and in tension over a wide range of strain rates. These two types of loadings provide an opportunity to examine also the effect that temperature might have on the effects of the hydrostatic stress component on the material response. The experimental data provide the information needed for NASA scientists for the development of a nonlinear, strain rate, and temperature dependent deformation and strength models for composites that can subsequently be used in design. This year effort was directed into the development and testing of the epoxy resin at elevated temperatures. Two types of epoxy resins were tested in shear at high strain rates of about 10(exp-4)/s and elevated temperatures of 50 and 8OC. The results show that the temperature significantly affects the response of epoxy.

The Time-Dependency of Deformation in Porous Carbonate Rocks

NASA Astrophysics Data System (ADS)

Kibikas, W. M.; Lisabeth, H. P.; Zhu, W.

2016-12-01

Porous carbonate rocks are natural reservoirs for freshwater and hydrocarbons. More recently, due to their potential for geothermal energy generation as well as carbon sequestration, there are renewed interests in better understanding of the deformation behavior of carbonate rocks. We conducted a series of deformation experiments to investigate the effects of strain rate and pore fluid chemistry on rock strength and transport properties of porous limestones. Indiana limestone samples with initial porosity of 16% are deformed at 25 °C under effective pressures of 10, 30, and 50 MPa. Under nominally dry conditions, the limestone samples are deformed under 3 different strain rates, 1.5 x 10-4 s-1, 1.5 x 10-5 s-1 and 1.5 x 10-6 s-1 respectively. The experimental results indicate that the mechanical behavior is both rate- and pressure-dependent. At low confining pressures, post-yielding deformation changes from predominantly strain softening to strain hardening as strain rate decreases. At high confining pressures, while all samples exhibit shear-enhanced compaction, decreasing strain rate leads to an increase in compaction. Slower strain rates enhance compaction at all confining pressure conditions. The rate-dependence of deformation behaviors of porous carbonate rocks at dry conditions indicates there is a strong visco-elastic coupling for the degradation of elastic modulus with increasing plastic deformation. In fluid saturated samples, inelastic strain of limestone is partitioned among low temperature plasticity, cataclasis and solution transport. Comparison of inelastic behaviors of samples deformed with distilled water and CO2-saturated aqueous solution as pore fluids provide experimental constraints on the relative activities of the various mechanisms. Detailed microstructural analysis is conducted to take into account the links between stress, microstructure and the inelastic behavior and failure mechanisms.

Correlation between Reynolds number and eccentricity effect in stenosed artery models.

PubMed

Javadzadegan, Ashkan; Shimizu, Yasutomo; Behnia, Masud; Ohta, Makoto

2013-01-01

Flow recirculation and shear strain are physiological processes within coronary arteries which are associated with pathogenic biological pathways. Distinct Quite apart from coronary stenosis severity, lesion eccentricity can cause flow recirculation and affect shear strain levels within human coronary arteries. The aim of this study is to analyse the effect of lesion eccentricity on the transient flow behaviour in a model of a coronary artery and also to investigate the correlation between Reynolds number (Re) and the eccentricity effect on flow behaviour. A transient particle image velocimetry (PIV) experiment was implemented in two silicone based models with 70% diameter stenosis, one with eccentric stenosis and one with concentric stenosis. At different times throughout the flow cycle, the eccentric model was always associated with a greater recirculation zone length, maximum shear strain rate and maximum axial velocity; however, the highest and lowest impacts of eccentricity were on the recirculation zone length and maximum shear strain rate, respectively. Analysis of the results revealed a negative correlation between the Reynolds number (Re) and the eccentricity effect on maximum axial velocity, maximum shear strain rate and recirculation zone length. As Re number increases the eccentricity effect on the flow behavior becomes negligible.

Effect of cooling rate during hot stamping on low cyclic fatigue of boron steel sheet

NASA Astrophysics Data System (ADS)

Suh, Chang Hee; Jang, Won Seok; Oh, Sang Kyun; Lee, Rac Gyu; Jung, Yun-Chul; Kim, Young Suk

2012-08-01

Boron steel is widely used throughout the automobile industry due to its high tensile strength and hardenability. When boron steel is used for body parts, only high strength is required for crashworthiness. However, when boron steel is used for chassis parts, a high fatigue life is needed. The microstructure of boron steel is mainly affected by the cooling rate during hot stamping. Therefore, this study investigated the low cyclic fatigue life according to the cooling rate. The fatigue life increased at a low strain amplitude when the cooling rate was fast. However, at a high strain amplitude, the fatigue life decreased, due to the low ductility and fracture toughness of the martensite formed by rapid cooling. Martensite formed by a fast cooling rate shows excellent fatigue life at a low total strain amplitude; however, a multiphase microstructure formed by a slow cooling rate is recommended if the parts experience high and low total strain amplitudes alternately. In addition, the cooling rate has little effect on the distribution of solute boron and boron precipitations, so it is expected that boron rarely affects low cyclic fatigue.

Nitrogen requirements of commercial wine yeast strains during fermentation of a synthetic grape must.

PubMed

Gutiérrez, Alicia; Chiva, Rosana; Sancho, Marta; Beltran, Gemma; Arroyo-López, Francisco Noé; Guillamon, José Manuel

2012-08-01

Nitrogen deficiencies in grape musts are one of the main causes of stuck or sluggish wine fermentations. Currently, the most common method for dealing with nitrogen-deficient fermentations is adding supplementary nitrogen (usually ammonium phosphate). However, it is important to know the specific nitrogen requirement of each strain, to avoid excessive addition that can lead to microbial instability and ethyl carbamate accumulation. In this study, we aimed to determine the effect of increasing nitrogen concentrations of three different nitrogen sources on growth and fermentation performance in four industrial wine yeast strains. This task was carried out using statistical modeling techniques. The strains PDM and RVA showed higher growth-rate and maximum population size and consumed nitrogen much more quickly than strains ARM and TTA. Likewise, the strains PDM and RVA were also the greatest nitrogen demanders. Thus, we can conclude that these differences in nitrogen demand positively correlated with higher growth rate and higher nitrogen uptake rate. The most direct effect of employing an adequate nitrogen concentration is the increase in biomass, which involves a higher fermentation rate. However, the impact of nitrogen on fermentation rate is not exclusively due to the increase in biomass because the strain TTA, which showed the worst growth behavior, had the best fermentation activity. Some strains may adapt a strategy whereby fewer cells with higher metabolic activity are produced. Regarding the nitrogen source used, all the strains showed the better and worse fermentation performance with arginine and ammonium, respectively. Copyright © 2012 Elsevier Ltd. All rights reserved.

Effects of Foot Strike and Step Frequency on Achilles Tendon Stress During Running.

PubMed

Lyght, Michael; Nockerts, Matthew; Kernozek, Thomas W; Ragan, Robert

2016-08-01

Achilles tendon (AT) injuries are common in runners. The AT withstands high magnitudes of stress during running which may contribute to injury. Our purpose was to examine the effects of foot strike pattern and step frequency on AT stress and strain during running utilizing muscle forces based on a musculoskeletal model and subject-specific ultrasound-derived AT cross-sectional area. Nineteen female runners performed running trials under 6 conditions, including rearfoot strike and forefoot strike patterns at their preferred cadence, +5%, and -5% preferred cadence. Rearfoot strike patterns had less peak AT stress (P < .001), strain (P < .001), and strain rate (P < .001) compared with the forefoot strike pattern. A reduction in peak AT stress and strain were exhibited with a +5% preferred step frequency relative to the preferred condition using a rearfoot (P < .001) and forefoot (P=.005) strike pattern. Strain rate was not different (P > .05) between step frequencies within each foot strike condition. Our results suggest that a rearfoot pattern may reduce AT stress, strain, and strain rate. Increases in step frequency of 5% above preferred frequency, regardless of foot strike pattern, may also lower peak AT stress and strain.

Major effect of inherited rheology weakening in the crust and mantle on continental intraplate strain and seismicity rates

NASA Astrophysics Data System (ADS)

Gueydan, Frédéric; Mazzotti, Stephane

2017-04-01

Stable Continental Regions (SCR, i.e., intraplate) are commonly viewed as non-deforming and very high resistance lithosphere domains, except in localized regions of higher strain and seismicity rates that often related to fossilized tectonic zones acting as weaker domains (e.g., Rhine Graben, New Madrid). Two main categories of models have been proposed to explain strain concentration in SCR: Local stress concentration (fault intersection, erosion pulse, …) and local lithosphere weakness (high geotherm, mantle anisotropy, …). In order to test the respective role of these various parameters of the stress - rheology - strain relationship, we propose a simple 1D model to quantify first-order continental strain rate variations using laboratory and field-based rheology laws for the crust and mantle. In particular, we include new strain-weakening rheologies in order to simulate tectonic heritage. Within the framework of near-failure equilibrium between tectonic forces and strain rates, we show that inherited rheology weakening plays a fundamental role in allowing for and explaining strain and seismicity concentration in intraplate weak zones. A comparison with empirical strain rate estimations in SCR and intraplate weak zones shows that inherited weakening rheologies can increase local strain rates by as much as three orders of magnitude, about one to two orders higher than that permitted by other processes such as stress concentration, thermal anomaly, etc.

Simulation study of the effect of strain rate on the mechanical properties and tensile deformation of gold nanowire

NASA Astrophysics Data System (ADS)

Shi, Guo-Jie; Wang, Jin-Guo; Hou, Zhao-Yang; Wang, Zhen; Liu, Rang-Su

2017-09-01

The mechanical properties and deformation mechanisms of Au nanowire during the tensile processes at different strain rates are revealed by the molecular dynamics method. It is found that the Au nanowire displays three distinct types of mechanical behaviors when tensioning at low, medium and high strain rates, respectively. At the low strain rate, the stress-strain curve displays a periodic zigzag increase-decrease feature, and the plastic deformation is resulted from the slide of dislocation. The dislocations nucleate, propagate, and finally annihilate in every decreasing stages of stress, and the nanowire always can recover to FCC-ordered structure. At the medium strain rate, the stress-strain curve gently decreases during the plastic process, and the deformation is contributed from sliding and twinning. The dislocations formed in the yield stage do not fully propagate and further escape from the nanowire. At the high strain rate, the stress-strain curve wave-like oscillates during the plastic process, and the deformation is resulted from amorphization. The FCC atoms quickly transform into disordered amorphous structure in the yield stage. The relative magnitude between the loading velocity of strain and the propagation velocity of phonons determines the different deformation mechanisms. The mechanical behavior of Au nanowire is similar to Ni, Cu and Pt nanowires, but their deformation mechanisms are not completely identical with each other.

Processing parameters associated with scale-up of balloon film production

NASA Technical Reports Server (NTRS)

Simpson, D. M.; Harrison, I. R.

1993-01-01

A method is set forth for assessing strain-rate profiles that can be used to develop a scale-up theory for blown-film extrusion. Strain rates are evaluated by placing four ink dots on the stalk of an extruded bubble to follow the displacements of the dots as a function of time. The instantaneous Hencky strain is obtained with the displacement data and plotted for analysis. Specific attention is given to potential sources of error in the distance measurements and corrections for these complex bubble geometries. The method is shown to be effective for deriving strain-rate data related to different processing parameters for the production of balloon film. The strain rates can be compared to frostline height, blow-up ratio, and take-up ratio to optimize these processing variables.

Effects of Applied Strain on Rates of Ageing: Project Overview

NASA Technical Reports Server (NTRS)

Campion, R. P.

1997-01-01

One of the stated intents of this project has been to make some assessment of effects of strain on rates of ageing of project thermoplastics exposed to project fluids. To this end, certain straining jigs which apply in various modes - tensile, four-point bending and crack growth using compact tension samples - were designed and made for holding samples during fluid exposures. During testing, features of the thermoplastics have been observed which have tended to confuse apparent strain effects on the polymers' aged performance, but recent assessments of the topic and its data have led to considerable progress being made in identifying test procedures necessary for strain and related effects on chemical deterioration to manifest themselves. It is the intent of this report to provide a summary of what has been determined on strain and related effects thus far, and provide recommendations for clarifying them in Phase 2 by means of further test procedures which will increase and focus the severity of the conditions applying. The choice of flexible pipe rather than umbilicals service for assessing service strain conditions reflects the major interest of project members. However, Tefzel data are still provided.

Further study on the wheel-rail impact response induced by a single wheel flat: the coupling effect of strain rate and thermal stress

NASA Astrophysics Data System (ADS)

Jing, Lin; Han, Liangliang

2017-12-01

A comprehensive dynamic finite-element simulation method was proposed to study the wheel-rail impact response induced by a single wheel flat based on a 3-D rolling contact model, where the influences of the structural inertia, strain rate effect of wheel-rail materials and thermal stress due to the wheel-rail sliding friction were considered. Four different initial conditions (i.e. pure mechanical loading plus rate-independent, pure mechanical loading plus rate-dependent, thermo-mechanical loading plus rate-independent, and thermo-mechanical loading plus rate-dependent) were involved into explore the corresponding impact responses in term of the vertical impact force, von-Mises equivalent stress, equivalent plastic strain and shear stress. Influences of train speed, flat length and axle load on the flat-induced wheel-rail impact response were discussed, respectively. The results indicate that the maximum thermal stresses are occurred on the tread of the wheel and on the top surface of the middle rail; the strain rate hardening effect contributes to elevate the von-Mises equivalent stress and restrain the plastic deformation; and the initial thermal stress due to the sliding friction will aggravate the plastic deformation of wheel and rail. Besides, the wheel-rail impact responses (i.e. impact force, von-Mises equivalent stress, equivalent plastic strain, and XY shear stress) induced by a flat are sensitive to the train speed, flat length and axle load.

Effects of misalignment on mechanical behavior of metals in creep

NASA Technical Reports Server (NTRS)

Wu, H. C.

1981-01-01

Creep tests were conducted by means of a closed loop servocontrolled materials test system. The strain history prior to creep is carefully monitored. Tests were performed for aluminum alloy 6061-O at 150 C and were monitored by a PDP 11/04 minicomputer at a preset constant plastic strain rate prehistory. The results show that the plastic strain rate prior to creep plays a significant role in creep behavior. The endochronic theory of viscoplasticity was applied to describe the observed creep curves. Intrinsic time and strain rate sensitivity function concepts are employed and modified according to the present observation.

Strain Rate and Stress Relaxation Effects on Pressuremeter Testing in Clays

DTIC Science & Technology

1992-03-01

CHARACTERISTICS OF KAOLINITE AND GROUND SILICA 245 APPENDIX E COMPUTER PROGRAMS ....................... 248 0 0 0 0 0 0 0 iv LIST OF TABLES Table Page 3.1 A...Comparison of Three Types of Boundary Conditions in a Multiaxial Cubical Test Apparatus ................... 37 3.2 Properties of the Kaolinite and Kaolin...to 0.01 %/min Versus Strain Rate for Kaolinite Clay ................... 102 4.3 Shear Strength Normalized with Respect to 0.01 %/min Versus Strain Rate

Physical nature of strain rate sensitivity of metals and alloys at high strain rates

NASA Astrophysics Data System (ADS)

Borodin, E. N.; Gruzdkov, A. A.; Mayer, A. E.; Selyutina, N. S.

2018-04-01

The role of instabilities of plastic flow at plastic deformation of various materials is one of the important cross-disciplinary problems which is equally important in physics, mechanics and material science. The strain rate sensitivities under slow and high strain rate conditions of loading have different physical nature. In the case of low strain rate, the sensitivity arising from the inertness of the defect structures evolution can be expressed by a single parameter characterizing the plasticity mechanism. In our approach, this is the value of the characteristic relaxation time. In the dynamic case, there are additional effects of “high-speed sensitivity” associated with the micro-localization of the plastic flow near the stress concentrators. In the frames of mechanical description, this requires to introduce additional strain rate sensitivity parameters, which is realized in numerous modifications of Johnson–Cook and Zerilli–Armstrong models. The consideration of both these factors is fundamental for an adequate description of the problems of dynamic deformation of highly inhomogeneous metallic materials such as steels and alloys. The measurement of the dispersion of particle velocities on the free surface of a shock-loaded material can be regarded as an experimental expression of the effect of micro-localization. This is also confirmed by our results of numerical simulation of the propagation of shock waves in a two-dimensional formulation and analytical estimations.

Impact of primary antibiotic resistance on the effectiveness of sequential therapy for Helicobacter pylori infection: lessons from a 5-year study on a large number of strains.

PubMed

Gatta, L; Scarpignato, C; Fiorini, G; Belsey, J; Saracino, I M; Ricci, C; Vaira, D

2018-05-01

The increasing prevalence of strains resistant to antimicrobial agents is a critical issue in the management of Helicobacter pylori (H. pylori) infection. (1) To evaluate the prevalence of primary resistance to clarithromycin, metronidazole and levofloxacin (2) to assess the effectiveness of sequential therapy on resistant strains (3) to identify the minimum number of subjects to enrol for evaluating the effectiveness of an eradication regimen in patients harbouring resistant strains. Consecutive 1682 treatment naïve H. pylori-positive patients referred for upper GI endoscopy between 2010 and 2015 were studied and resistances assessed by E-test. Sequential therapy was offered, effectiveness evaluated and analysed. H. pylori-primary resistance to antimicrobials tested was high, and increased between 2010 and 2015. Eradication rates were (estimates and 95% CIs): 97.3% (95.6-98.4) in strains susceptible to clarithromycin and metronidazole; 96.1% (91.7-98.2) in strains resistant to metronidazole but susceptible to clarithromycin; 93.4% (88.2-96.4) in strains resistant to clarithromycin but susceptible to metronidazole; 83.1% (77.7-87.3) in strains resistant to clarithromycin and metronidazole. For any treatment with a 75%-85% eradication rate, some 98-144 patients with resistant strains need to be studied to get reliable information on effectiveness in these patients. H. pylori-primary resistance is increasing and represents the most critical factor affecting effectiveness. Sequential therapy eradicated 83% of strains resistant to clarithromycin and metronidazole. Reliable estimates of the effectiveness of a given regimen in patients harbouring resistant strains can be obtained only by assessing a large number of strains. © 2018 John Wiley & Sons Ltd.

Effects of polyaluminum chloride and lanthanum-modified bentonite on the growth rates of three Cylindrospermopsis raciborskii strains

PubMed Central

van Oosterhout, Frank; Becker, Vanessa; Attayde, José Luiz; Lürling, Miquel

2018-01-01

In tropical and subtropical lakes, eutrophication often leads to nuisance blooms of Cylindrospermopsis raciborskii. In laboratory experiments, we tested the combined effects of flocculant polyaluminum chloride (PAC) and lanthanum-modified bentonite (LMB) on the sinking and growth rates of three C. raciborskii strains. We tested the hypothesis that the combination of PAC and LMB would (1) effectively sink C. raciborskii in a test tube experiment and (2) impair C. raciborskii growth, irrespective of the biomass of the inoculum (bloom) and the strain in the growth experiment. We tested the recommended (LMB1) and a three-times higher dose of LMB (LMB3). The combined addition of PAC and LMB enhanced the sedimentation of all C. raciborskii strains. Moreover, both the PAC and LMB doses decreased the phosphate concentration. PAC and LMB1 decreased the growth rate of all strains, but the efficacy depended on the biomass and strain. The combined addition of PAC and LMB3 inhibited the growth of all strains independently of the biomass and strain. We conclude that a low dose of PAC in combination with the recommended dose of LMB decreases C. raciborskii blooms and that the efficiency of the technique depends on the biomass of the bloom. A higher dose of LMB is needed to obtain a more efficient control of C. raciborskii blooms. PMID:29614118

Effects of polyaluminum chloride and lanthanum-modified bentonite on the growth rates of three Cylindrospermopsis raciborskii strains.

PubMed

Araújo, Fabiana; van Oosterhout, Frank; Becker, Vanessa; Attayde, José Luiz; Lürling, Miquel

2018-01-01

In tropical and subtropical lakes, eutrophication often leads to nuisance blooms of Cylindrospermopsis raciborskii. In laboratory experiments, we tested the combined effects of flocculant polyaluminum chloride (PAC) and lanthanum-modified bentonite (LMB) on the sinking and growth rates of three C. raciborskii strains. We tested the hypothesis that the combination of PAC and LMB would (1) effectively sink C. raciborskii in a test tube experiment and (2) impair C. raciborskii growth, irrespective of the biomass of the inoculum (bloom) and the strain in the growth experiment. We tested the recommended (LMB1) and a three-times higher dose of LMB (LMB3). The combined addition of PAC and LMB enhanced the sedimentation of all C. raciborskii strains. Moreover, both the PAC and LMB doses decreased the phosphate concentration. PAC and LMB1 decreased the growth rate of all strains, but the efficacy depended on the biomass and strain. The combined addition of PAC and LMB3 inhibited the growth of all strains independently of the biomass and strain. We conclude that a low dose of PAC in combination with the recommended dose of LMB decreases C. raciborskii blooms and that the efficiency of the technique depends on the biomass of the bloom. A higher dose of LMB is needed to obtain a more efficient control of C. raciborskii blooms.

Dynamic tensile characterization of Vascomax® maraging C250 and C300 alloys

DOE Office of Scientific and Technical Information (OSTI.GOV)

Song, Bo; Wakeland, Peter Eric; Furnish, Michael D.

Vascomax® maraging C250 and C300 alloys were dynamically characterized in tension with Kolsky tension bar techniques. Compared with conventional Kolsky tension bar experiments, a pair of lock nuts was used to minimize the pseudo stress peak and a laser system was applied to directly measure the specimen displacement. Dynamic engineering stress–strain curves of the C250 and C300 alloys were obtained in tension at 1000 and 3000 s –1. The dynamic yield strengths for both alloys were similar, but significantly higher than those obtained from quasi-static indentation tests. Both alloys exhibited insignificant strain-rate effect on dynamic yield strength. The C300 alloymore » showed approximately 10 % higher in yield strength than the C250 alloy at the same strain rates. Necking was observed in both alloys right after yield. The Bridgman correction was applied to calculate the true stress and strain at failure for both alloys. The true failure stress showed a modest strain rate effect for both alloys but no significant difference between the two alloys at the same strain rate. As a result, the C250 alloy was more ductile than the C300 alloy under dynamic loading.« less

Dynamic tensile characterization of Vascomax® maraging C250 and C300 alloys

DOE PAGES

Song, Bo; Wakeland, Peter Eric; Furnish, Michael D.

2015-04-14

Vascomax® maraging C250 and C300 alloys were dynamically characterized in tension with Kolsky tension bar techniques. Compared with conventional Kolsky tension bar experiments, a pair of lock nuts was used to minimize the pseudo stress peak and a laser system was applied to directly measure the specimen displacement. Dynamic engineering stress–strain curves of the C250 and C300 alloys were obtained in tension at 1000 and 3000 s –1. The dynamic yield strengths for both alloys were similar, but significantly higher than those obtained from quasi-static indentation tests. Both alloys exhibited insignificant strain-rate effect on dynamic yield strength. The C300 alloymore » showed approximately 10 % higher in yield strength than the C250 alloy at the same strain rates. Necking was observed in both alloys right after yield. The Bridgman correction was applied to calculate the true stress and strain at failure for both alloys. The true failure stress showed a modest strain rate effect for both alloys but no significant difference between the two alloys at the same strain rate. As a result, the C250 alloy was more ductile than the C300 alloy under dynamic loading.« less

High Strain Rate Tensile Testing of Silver Nanowires: Rate-Dependent Brittle-to-Ductile Transition.

PubMed

Ramachandramoorthy, Rajaprakash; Gao, Wei; Bernal, Rodrigo; Espinosa, Horacio

2016-01-13

The characterization of nanomaterials under high strain rates is critical to understand their suitability for dynamic applications such as nanoresonators and nanoswitches. It is also of great theoretical importance to explore nanomechanics with dynamic and rate effects. Here, we report in situ scanning electron microscope (SEM) tensile testing of bicrystalline silver nanowires at strain rates up to 2/s, which is 2 orders of magnitude higher than previously reported in the literature. The experiments are enabled by a microelectromechanical system (MEMS) with fast response time. It was identified that the nanowire plastic deformation has a small activation volume (<10b(3)), suggesting dislocation nucleation as the rate controlling mechanism. Also, a remarkable brittle-to-ductile failure mode transition was observed at a threshold strain rate of 0.2/s. Transmission electron microscopy (TEM) revealed that along the nanowire, dislocation density and spatial distribution of plastic regions increase with increasing strain rate. Furthermore, molecular dynamic (MD) simulations show that deformation mechanisms such as grain boundary migration and dislocation interactions are responsible for such ductility. Finally, the MD and experimental results were interpreted using dislocation nucleation theory. The predicted yield stress values are in agreement with the experimental results for strain rates above 0.2/s when ductility is pronounced. At low strain rates, random imperfections on the nanowire surface trigger localized plasticity, leading to a brittle-like failure.

Rate dependent deformation of porous sandstone across the brittle-ductile transition

NASA Astrophysics Data System (ADS)

Jefferd, M.; Brantut, N.; Mitchell, T. M.; Meredith, P. G.

2017-12-01

Porous sandstones transition from dilatant, brittle deformation at low pressure, to compactant, ductile deformation at high pressure. Both deformation modes are driven by microcracking, and are expected to exhibit a time dependency due to chemical interactions between the pore fluid and the rock matrix. In the brittle regime, time-dependent failure and brittle creep are well documented. However, much less is understood in the ductile regime. We present results from a series of triaxial deformation experiments, performed in the brittle-ductile transition zone of fluid saturated Bleurswiller sandstone (initial porosity = 23%). Samples were deformed at 40 MPa effective pressure, to 4% axial strain, under either constant strain rate (10-5 s-1) or constant stress (creep) conditions. In addition to stress, axial strain and pore volume change, P wave velocities and acoustic emission were monitored throughout. During constant stress tests, the strain rate initially decreased with increasing strain, before reaching a minimum and accelerating to a constant level beyond 2% axial strain. When plotted against axial strain, the strain rate evolution under constant stress conditions, mirrors the stress evolution during the constant strain rate tests; where strain hardening occurs prior to peak stress, which is followed by strain softening and an eventual plateau. In all our tests, the minimum strain rate during creep occurs at the same inelastic strain as the peak stress during constant strain tests, and strongly decreases with decreasing applied stress. The microstructural state of the rock, as interpreted from similar volumetric strain curves, as well as the P-wave velocity evolution and AE production rate, appears to be solely a function of the total inelastic strain, and is independent of the length of time required to reach said strain. We tested the sensitivity of fluid chemistry on the time dependency, through a series of experiments performed under similar stress conditions, but with chemically inert decane instead of water as the pore fluid. Under the same applied stress, decane saturated samples reached a minimum strain rate 2 orders of magnitude lower than the water saturated samples. This is consistent with a mechanism of subcritical crack growth driven by chemical interactions between the pore fluid and the rock.

Effect of uniaxial stress on the electrochemical properties of graphene with point defects

NASA Astrophysics Data System (ADS)

Szroeder, Paweł; Sagalianov, Igor Yu.; Radchenko, Taras M.; Tatarenko, Valentyn A.; Prylutskyy, Yuriy I.; Strupiński, Włodzimierz

2018-06-01

We report a calculational study of electron states and the resulting electrochemical properties of uniaxially strained graphene with point defects. For this study the reduction of ferricyanide to ferrocyanide serves as a benchmark electrochemical reaction. We find that the heterogeneous electron transfer activity of the perfect graphene electrode rises under uniaxial strain. However, evolution of the cathodic reaction rate depends on the direction of strain. For moderate lattice deformations, the zigzag strain improves electrochemical performance better than the armchair strain. Standard rate constant increases by 50% at the zigzag strain of 10%. Vacancies, covalently bonded moieties, charged adatoms and substitutional impurities in the zigzag strained graphene induce changes in the shape of the curve of the cathodic reaction rate. However, this changes do not translate into the electrocatalytic activity. Vacancies and covalently bonded moieties at concentration of 0.1% do not affect the electrochemical performance. Charged adatoms and substitutional impurities give a slight increase in the standard rate constant by, respectively, 2.2% and 3.4%.

Matrix resin effects in composite delamination - Mode I fracture aspects

NASA Technical Reports Server (NTRS)

Hunston, Donald L.; Moulton, Richard J.; Johnston, Norman J.; Bascom, Willard D.

1987-01-01

A number of thermoset, toughened thermoset, and thermoplastic resin matrix systems were characterized for Mode I critical strain energy release rates, and their composites were tested for interlaminar critical strain energy release rates using the double cantilever beam method. A clear correlation is found between the two sets of data. With brittle resins, the interlaminar critical strain energy release rates are somewhat larger than the neat resin values due to a full transfer of the neat resin toughness to the composite and toughening mechanisms associated with crack growth. With tougher matrices, the higher critical strain energy release rates are only partially transferred to the composites, presumably because the fibers restrict the crack-tip deformation zones.

Clinical effect of biapenem on nursing and healthcare-associated pneumonia (NHCAP).

PubMed

Okimoto, Niro; Kawai, Yasuhiro; Katoh, Tadashi; Hayashi, Toshikiyo; Kurihara, Takeyuki; Miyashita, Naoyuki

2015-08-01

The clinical effect of Biapenem (BIPM) on Nursing and Healthcare-associated pneumonia (NHCAP) was evaluated. One hundred and three NHCAP patients (Group B: 52 patients, Group C: 51 patients) to whom BIPM was administered were included in this study. Clinical effect, bacteriological effect, and adverse events were examined. Results revealed efficacy in 45 of 52 patients (efficacy rate: 86.5%) of NHCAP Group B, and 43 of 51 patients (efficacy rate: 84.3%) of NHCAP Group C, 88 of 103 patients (efficacy rate: 85.4%) as a whole. As for bacteriological effect, 10 (76.9%) of 13 Pseudomonas aeruginosa strains, 9 (90.0%) of 10 Klebsiella pneumoniae strains, 7 (87.5%) of 8 methicillin-sensitive Staphlococcus aureus strains, and 7 (100%) of 7 Streptococcus pneumonia strains were eradicated. As a whole, 38 (80.9%) of 47 strains were eradicated. Adverse events included drug fever and drug eruption in one patient each, and abnormal laboratory findings, including mild hepatic dysfunction in 18 patients and mild renal dysfunction in 5 patients. Based on the above, it was concluded that BIPM shows excellent clinical effect on NHCAP with fewer adverse events. Copyright © 2015 Japanese Society of Chemotherapy and The Japanese Association for Infectious Diseases. Published by Elsevier Ltd. All rights reserved.

Effect of Control Mode and Test Rate on the Measured Fracture Toughness of Advanced Ceramics

NASA Technical Reports Server (NTRS)

Hausmann, Bronson D.; Salem, Jonathan A.

2018-01-01

The effects of control mode and test rate on the measured fracture toughness of ceramics were evaluated by using chevron-notched flexure specimens in accordance with ASTM C1421. The use of stroke control gave consistent results with about 2% (statistically insignificant) variation in measured fracture toughness for a very wide range of rates (0.005 to 0.5 mm/min). Use of strain or crack mouth opening displacement (CMOD) control gave approx. 5% (statistically significant) variation over a very wide range of rates (1 to 80 µm/m/s), with the measurements being a function of rate. However, the rate effect was eliminated by use of dry nitrogen, implying a stress corrosion effect rather than a stability effect. With the use of a nitrogen environment during strain controlled tests, fracture toughness values were within about 1% over a wide range of rates (1 to 80 micons/m/s). CMOD or strain control did allow stable crack extension well past maximum force, and thus is preferred for energy calculations. The effort is being used to confirm recommendations in ASTM Test Method C1421 on fracture toughness measurement.

[The Influence of Rifampicin Resistant Mutations on the Biosynthesis of Exopolysaccharides by Strain Escherichia coli K-12 lon].

PubMed

Hovhannisyan, H G; Barseghyan, A H

2015-01-01

The influence of RNA polymerase (rif) mutations on the yield of capsular exopolysaccharide--colanic acid (CA) of Escherichia coli K-12 lon strain was studied. Five colanic acid isogenic producing strains were created by transduction transfer of rif alleles possessing pleiotropic effects. The obtained isogenic strains differed by specific growth rate, size and mucoidness of colonies, the dependence of growth on the medium composition and cultivation temperature, as well as by the adsorption rate of virulent bacteriophage M59, specifically lysing E. coli cells producing CA. Direct correlation between the yield of exopolysaccharides, growth rate and adsorption of bacteriophage M59 was revealed. Among rif recombinants strain AH203, which synthesized twice as much CA compared with the parental strain in submerged cultivation was selected.

Influence of strain rate on indentation response of porcine brain.

PubMed

Qian, Long; Zhao, Hongwei; Guo, Yue; Li, Yuanshang; Zhou, Mingxing; Yang, Liguo; Wang, Zhiwei; Sun, Yifan

2018-06-01

Knowledge of brain tissue mechanical properties may be critical for formulating hypotheses about some specific diseases mechanisms and its accurate simulations such as traumatic brain injury (TBI) and tumor growth. Compared to traditional tests (e.g. tensile and compression), indentation shows superiority by virtue of its pinpoint and nondestructive/quasi-nondestructive. As a viscoelastic material, the properties of brain tissue depend on the strain rate by definition. However most efforts focus on the aspect of velocity in the field of brain indentation, rather than strain rate. The influence of strain rate on indentation response of brain tissue is taken little attention. Further, by comparing different results from literatures, it is also obvious that strain rate rather than velocity is more appropriate to characterize mechanical properties of brain. In this paper, to systematically characterize the influence of strain rate, a series of indentation-relaxation tests n = 210) are performed on the cortex of porcine brain using a custom-designed indentation device. The mechanical response that correlates with indenter diameters, depths of indentation and velocities, is revealed for the indentation portion, and elastic behavior of brain tissue is analyzed as the function of strain rate. Similarly, a linear viscoelastic model with a Prony series is employed for the indentation-relaxation portion, wherein the brain tissue shows more viscous and responds more quickly with increasing strain rate. Understanding the effect of strain rate on mechanical properties of brain indentation may be far-reaching for brain injury biomechanics and accurate simulations, but be important for bridging between indentation results of different literatures. Copyright © 2018 Elsevier Ltd. All rights reserved.

Atomistic Simulation of the Rate-Dependent Ductile-to-Brittle Failure Transition in Bicrystalline Metal Nanowires.

PubMed

Tao, Weiwei; Cao, Penghui; Park, Harold S

2018-02-14

The mechanical properties and plastic deformation mechanisms of metal nanowires have been studied intensely for many years. One of the important yet unresolved challenges in this field is to bridge the gap in properties and deformation mechanisms reported for slow strain rate experiments (∼10 -2 s -1 ), and high strain rate molecular dynamics (MD) simulations (∼10 8 s -1 ) such that a complete understanding of strain rate effects on mechanical deformation and plasticity can be obtained. In this work, we use long time scale atomistic modeling based on potential energy surface exploration to elucidate the atomistic mechanisms governing a strain-rate-dependent incipient plasticity and yielding transition for face centered cubic (FCC) copper and silver nanowires. The transition occurs for both metals with both pristine and rough surfaces for all computationally accessible diameters (<10 nm). We find that the yield transition is induced by a transition in the incipient plastic event from Shockley partials nucleated on primary slip systems at MD strain rates to the nucleation of planar defects on non-Schmid slip planes at experimental strain rates, where multiple twin boundaries and planar stacking faults appear in copper and silver, respectively. Finally, we demonstrate that, at experimental strain rates, a ductile-to-brittle transition in failure mode similar to previous experimental studies on bicrystalline silver nanowires is observed, which is driven by differences in dislocation activity and grain boundary mobility as compared to the high strain rate case.

Characterization of mechanical damage mechanisms in ceramic composite materials. Technical report, 23 May 1987-24 May 1988

DOE Office of Scientific and Technical Information (OSTI.GOV)

Lankford, J.

High-strain-rate compressive failure mechanisms in fiber-reinforced ceramic-matrix composite materials were characterized. These are contrasted with composite damage development at low-strain rates, and with the dynamic failure of monolithic ceramics. It is shown that it is possible to derive major strain-rate strengthening benefits if a major fraction of the fiber reinforcement is aligned with the load axis. This effect considerably exceeds the inertial microfracture strengthening observed in monolithic ceramics, and non-aligned composites. Its basis is shown to be the trans-specimen propagation time period for heterogeneously-nucleated, high-strain kink bands. A brief study on zirconia focused on the remarkable inverse strength-strain rate resultmore » previously observed for both fully and partially-stabilized zirconia single crystals, whereby the strength decreased with increasing strain rate. Based on the hypothesis that the suppression of microplastic flow, hence, local stress relaxation, might be responsible for this behavior, fully stabilized (i.e., non-transformable) specimens were strain-gaged and subjected to compressive microstrain. The rather stunning observation was that the crystals are highly microplastic, exhibiting plastic yield on loading and anelasticity and reverse plasticity upon unloading. These results clearly support the hypothesis that with increasing strain rate, microcracking is favored at the expense of microplasticity.« less

High strain rate behaviour of polypropylene microfoams

NASA Astrophysics Data System (ADS)

Gómez-del Río, T.; Garrido, M. A.; Rodríguez, J.; Arencón, D.; Martínez, A. B.

2012-08-01

Microcellular materials such as polypropylene foams are often used in protective applications and passive safety for packaging (electronic components, aeronautical structures, food, etc.) or personal safety (helmets, knee-pads, etc.). In such applications the foams which are used are often designed to absorb the maximum energy and are generally subjected to severe loadings involving high strain rates. The manufacture process to obtain polymeric microcellular foams is based on the polymer saturation with a supercritical gas, at high temperature and pressure. This method presents several advantages over the conventional injection moulding techniques which make it industrially feasible. However, the effect of processing conditions such as blowing agent, concentration and microfoaming time and/or temperature on the microstructure of the resulting microcellular polymer (density, cell size and geometry) is not yet set up. The compressive mechanical behaviour of several microcellular polypropylene foams has been investigated over a wide range of strain rates (0.001 to 3000 s-1) in order to show the effects of the processing parameters and strain rate on the mechanical properties. High strain rate tests were performed using a Split Hopkinson Pressure Bar apparatus (SHPB). Polypropylene and polyethylene-ethylene block copolymer foams of various densities were considered.

The compressive behaviour and constitutive equation of polyimide foam in wide strain rate and temperature

NASA Astrophysics Data System (ADS)

Yoshimoto, Akifumi; Kobayashi, Hidetoshi; Horikawa, Keitaro; Tanigaki, Kenichi

2015-09-01

These days, polymer foams, such as polyurethane foam and polystyrene foam, are used in various situations as a thermal insulator or shock absorber. In general, however, their strength is insufficient in high temperature environments because of their low glass transition temperature. Polyimide is a polymer which has a higher glass transition temperature and high strength. Its mechanical properties do not vary greatly, even in low temperature environments. Therefore, polyimide foam is expected to be used in the aerospace industry. Thus, the constitutive equation of polyimide foam that can be applied across a wide range of strain rates and ambient temperature is very useful. In this study, a series of compression tests at various strain rates, from 10-3 to 103 s-1 were carried out in order to examine the effect of strain rate on the compressive properties of polyimide foam. The flow stress of polyimide foam increased rapidly at dynamic strain rates. The effect of ambient temperature on the properties of polyimide foam was also investigated at temperature from - 190 °C to 270°∘C. The flow stress decreased with increasing temperature.

Strain rate effects on reinforcing steels in tension

NASA Astrophysics Data System (ADS)

Cadoni, Ezio; Forni, Daniele

2015-09-01

It is unquestionable the fact that a structural system should be able to fulfil the function for which it was created, without being damaged to an extent disproportionate to the cause of damage. In addition, it is an undeniable fact that in reinforced concrete structures under severe dynamic loadings, both concrete and reinforcing bars are subjected to high strain-rates. Although the behavior of the reinforcing steel under high strain rates is of capital importance in the structural assessment under the abovementioned conditions, only the behaviour of concrete has been widely studied. Due to this lack of data on the reinforcing steel under high strain rates, an experimental program on rebar reinforcing steels under high strain rates in tension is running at the DynaMat Laboratory. In this paper a comparison of the behaviour in a wide range of strain-rates of several types of reinforcing steel in tension is presented. Three reinforcing steels, commonly proposed by the European Standards, are compared: B500A, B500B and B500C. Lastly, an evaluation of the most common constitutive laws is performed.

Strain, strain rate, and the force frequency relationship in patients with and without heart failure.

PubMed

Mak, Susanna; Van Spall, Harriette G C; Wainstein, Rodrigo V; Sasson, Zion

2012-03-01

The aim of this study was to examine the effect of heart rate (HR) on indices of deformation in adults with and without heart failure (HF) who underwent simultaneous high-fidelity catheterization of the left ventricle to describe the force-frequency relationship. Right atrial pacing to control HR and high-fidelity recordings of left ventricular (LV) pressure were used to inscribe the force-frequency relationship. Simultaneous two-dimensional echocardiographic imaging was acquired for speckle-tracking analysis. Thirteen patients with normal LV function and 12 with systolic HF (LV ejection fraction, 31 ± 13%) were studied. Patients with HF had depressed isovolumic contractility and impaired longitudinal strain and strain rate. HR-dependent increases in LV+dP/dt(max), the force-frequency relationship, was demonstrated in both groups (normal LV function, baseline to 100 beats/min: 1,335 ± 296 to 1,564 ± 320 mm Hg/sec, P < .0001; HF, baseline to 100 beats/min: 970 ± 207 to 1,083 ± 233 mm Hg/sec, P < .01). Longitudinal strain decreased significantly (normal LV function, baseline to 100 beats/min: 18.0 ± 3.5% to 10.8 ± 6.0%, P < .001; HF: 9.4 ± 4.1% to 7.5 ± 3.4%, P < .01). The decrease in longitudinal strain was related to a decrease in LV end-diastolic dimensions. Strain rate did not change with right atrial pacing. Despite the inotropic effect of increasing HR, longitudinal strain decreases in parallel with stroke volume as load-dependent indices of ejection. Strain rate did not reflect the modest HR-related changes in contractility; on the other hand, the use of strain rate for quantitative stress imaging is also less likely to be confounded by chronotropic responses. Copyright © 2012 American Society of Echocardiography. Published by Mosby, Inc. All rights reserved.

Strain localization parameters of AlCu4MgSi processed by high-energy electron beams

DOE Office of Scientific and Technical Information (OSTI.GOV)

Lunev, A. G., E-mail: agl@ispms.ru; Nadezhkin, M. V., E-mail: mvn@ispms.ru; National Research Tomsk Polytechnic University, Tomsk, 634050

2015-10-27

The influence of the electron beam surface treatment of AlCu4MgSi on the strain localization parameters and on the critical strain value of the Portevin–Le Chatelier effect has been considered. The strain localization parameters were measured using speckle imaging of the specimens subjected to the constant strain rate uniaxial tension at a room temperature. Impact of the surface treatment on the Portevin–Le Chatelier effect has been investigated.

Strain and rate-dependent neuronal injury in a 3D in vitro compression model of traumatic brain injury

PubMed Central

Bar-Kochba, Eyal; Scimone, Mark T.; Estrada, Jonathan B.; Franck, Christian

2016-01-01

In the United States over 1.7 million cases of traumatic brain injury are reported yearly, but predictive correlation of cellular injury to impact tissue strain is still lacking, particularly for neuronal injury resulting from compression. Given the prevalence of compressive deformations in most blunt head trauma, this information is critically important for the development of future mitigation and diagnosis strategies. Using a 3D in vitro neuronal compression model, we investigated the role of impact strain and strain rate on neuronal lifetime, viability, and pathomorphology. We find that strain magnitude and rate have profound, yet distinctively different effects on the injury pathology. While strain magnitude affects the time of neuronal death, strain rate influences the pathomorphology and extent of population injury. Cellular injury is not initiated through localized deformation of the cytoskeleton but rather driven by excess strain on the entire cell. Furthermore we find that, mechanoporation, one of the key pathological trigger mechanisms in stretch and shear neuronal injuries, was not observed under compression. PMID:27480807

Moisture Effects on the High Strain-Rate Behavior of Sand (Preprint)

DTIC Science & Technology

2008-04-01

1986) used a conventional SHPB to evaluate a single short pressure pulse traveling through long specimens of 20/40 dry sand, 50/80 dry sand...constant strain-rate within the specimen. In a conventional SHPB experiment, e.g., on dry sand by Veyera (1994), the incident pulse is nearly...strain-rate of 400 s-1. The sand specimen confined in a hardened steel tube, had a dry density of 1.50 g/cm3 with moisture contents varied from 3% to 20

Systematic review and meta-analysis: Multi-strain probiotics as adjunct therapy for Helicobacter pylori eradication and prevention of adverse events

PubMed Central

Huang, Ying; Wang, Lin; Malfertheiner, Peter

2015-01-01

Background Eradication rates with triple therapy for Helicobacter pylori infections have currently declined to unacceptable levels worldwide. Newer quadruple therapies are burdened with a high rate of adverse events. Whether multi-strain probiotics can improve eradication rates or diminish adverse events remains uncertain. Methods Relevant publications in which patients with H. pylori infections were randomized to a multi-strain probiotic or control were identified in PubMed, Cochrane Databases, and other sources from 1 January 1960–3 June 2015. Primary outcomes included eradication rates, incidence of any adverse event and the incidence of antibiotic-associated diarrhea. As probiotic efficacy is strain-specific, pooled relative risks and 95% confidence intervals were calculated using meta-analysis stratified by similar multi-strain probiotic mixtures. Results A total of 19 randomized controlled trials (20 treatment arms, n = 2730) assessing one of six mixtures of strains of probiotics were included. Four multi-strain probiotics significantly improved H. pylori eradication rates, five significantly prevented any adverse reactions and three significantly reduced antibiotic-associated diarrhea. Only two probiotic mixtures (Lactobacillus acidophilus/Bifidobacterium animalis and an eight-strain mixture) had significant efficacy for all three outcomes. Conclusions Our meta-analysis found adjunctive use of some multi-strain probiotics may improve H. pylori eradication rates and prevent the development of adverse events and antibiotic-associated diarrhea, but not all mixtures were effective. PMID:27536365

Strength and Deformation Rate of Plate Boundaries: The Rheological Effects of Grain Size Reduction, Structure, and Serpentinization.

NASA Astrophysics Data System (ADS)

Montesi, L.; Gueydan, F.

2016-12-01

Global strain rate maps reveal 1000-fold contrasts between plate interiors, oceanic or continental diffuse plate boundaries and narrow plate boundaries. Here, we show that rheological models based on the concepts of shear zone localization and the evolution of rock structure upon strain can explain these strain rate contrasts. Ductile shear zones constitute a mechanical paradox in the lithosphere. As every plastic deformation mechanism is strain-rate-hardening, ductile rocks are expected to deform at low strain rate and low stress (broad zone of deformation). Localized ductile shear zones require either a localized forcing (locally high stress) or a thermal or structural anomaly in the shear zone; either can be inherited or develop progressively as rocks deform. We previously identified the most effective process at each depth level of the lithosphere. In the upper crust and middle crust, rocks fabric controls localization. Grain size reduction is the most efficient mechanism in the uppermost mantle. This analysis can be generalized to consider a complete lithospheric section. We assume strain rate does not vary with depth and that the depth-integrated strength of the lithospheric does not change over time, as the total force is controlled by external process such as mantle convection and plate and slab buoyancy. Reducing grain size from a coarse value typical of undeformed peridotite to a value in agreement with the stress level (piezometer) while letting that stress vary from depth to depth (the integrated stress remains the same) increases the lithospheric strain rate by about a factor of 1000. This can explain the development of diffuse plate boundaries. The slightly higher strain rate of continental plate boundary may reflect development of a layered rock fabric in the middle crust. Narrow plate boundaries require additional weakening process. The high heat flux near mid-ocean ridge implies a thin lithosphere, which enhances stress (for constant integrated stress). While this can increase strain rate by another factor of 1000, another process must generate the lithospheric thickness variation in the first place. One possibility is serpentinization, which reduces the strength of the brittle crust, especially when coupled with the development of a fabric in brittle faults.

Deformation behavior of open-cell dry natural rubber foam: Effect of different concentration of blowing agent and compression strain rate

NASA Astrophysics Data System (ADS)

Samsudin, M. S. F.; Ariff, Z. M.; Ariffin, A.

2017-04-01

Compression and deformation behavior of partially open cell natural rubber (NR) foam produced from dry natural rubber (DNR), were investigated by performing compressive deformation at different strains and strain rates. Different concentrations of sodium bicarbonate as a blowing agent (BA) were utilized, from 4 to 16 phr in order to produce foams with range of cell size and morphology. Overall, increasing of blowing agent concentration had significantly changed relative foam density. Compression stress-strain curves of the foams exhibited that the compression behavior was directly correlated to the foam cells morphology and physical density. Pronounced changes were noticed for foams with bigger cells particularly at 4 phr concentration of BA where the compression stress at plateau region was greater compared to those with higher concentration of BA. Cell deformation progressive images confirmed that the foams demonstrated small degree of struts bending at 15% of strain and followed by continuous severe struts bending and elastic buckling up to 50% of strain. Compression test at different strain rates revealed that the strain rate factor only affected the foams with 4 phr of BA by causing immediate increment in the compression stress value when higher strain rate was applied.

High strain rate properties of angle-ply composite laminates, part 3

NASA Technical Reports Server (NTRS)

Daniel, I. M.

1991-01-01

Angle-ply graphite/epoxy and graphite/S-glass/epoxy laminates were characterized in uniaxial tension at strain rates ranging from quasi-static to over 500 s(sup -1). Laminate ring specimens of +/-15(sub 2s), +/-22.5(sub 2s), +/-30(sub 2s), +/-45(sub 2s), +/-60(sub 2s), +/-67.5(sub 2s), and +/-75(sub 2s) degree layups were loaded under internal pressure. Results were presented in the form of stress-strain curves to failure. Properties determined included moduli, Poisson's ratios, strength, and ultimate strain. In all seven laminates for the two materials tested the modulus and strength increase with strain rate. The effect of strain rate varies with layup, being lowest for the fiber dominated +/-15(sub 2s) degree laminates and highest for the matrix dominated +/-75(sub 2s) degree laminates. The highest increments over the static values are 10 to 25 percent for the +/-15(sub 2s) degree layup and 200 to 275 percent for the +/-75(sub 2s) degree layup. Ultimate strains do not show any significant trends with strain rate. In almost all cases the ultimate strain values are within +/-20 percent of the mean value and in half of the cases the deviation from the mean are less than 10 percent.

Propagation mode of Portevin-Le Chatelier plastic instabilities in an aluminium-magnesium alloy

DOE Office of Scientific and Technical Information (OSTI.GOV)

Zeghloul, A.; Mliha-Touati, M.; Bakir, S.

1996-11-01

The Portevin-Le Chatelier (PLC) effect is characterized by the appearance of serrations in load (hard tensile machine for constant strain rate tests) or by steps (soft tensile machine for constant stress rate tests) or by steps (soft tensile machine for constant stress rate tests) on the stress-strain curves. It is now widely accepted that the PLC propagative instability stems from the dynamic interaction between diffusing solute atoms and mobile dislocations in the temperature and strain rate ranges where dynamic strain ageing (DSA) takes place. This competition results in a negative strain-rate sensitivity. However, in some alloys, like concentrated solid solutions,more » shearing of precipitates accompanied by their dissolution and subsequent reprecipitation during tensile test may also lead to a negative strain rate sensitivity. In view of the renewed theoretical interest in propagative instabilities, it is important that the experimental features of band propagation be well characterized. In this work the authors present experimental results that are obtained from the investigation of the PLC bands associated with discontinuous yielding. These results show that the band strain, the band velocity and the propagation mode of the bands depend on the stress rate when the test is carried out on a soft tensile machine.« less

Modeling creep behavior of fiber composites

NASA Technical Reports Server (NTRS)

Chen, J. L.; Sun, C. T.

1988-01-01

A micromechanical model for the creep behavior of fiber composites is developed based on a typical cell consisting of a fiber and the surrounding matrix. The fiber is assumed to be linearly elastic and the matrix nonlinearly viscous. The creep strain rate in the matrix is assumed to be a function of stress. The nominal stress-strain relations are derived in the form of differential equations which are solved numerically for off-axis specimens under uniaxial loading. A potential function and the associated effective stress and effective creep strain rates are introduced to simplify the orthotropic relations.

Molecular simulation of flow-enhanced nucleation in n-eicosane melts under steady shear and uniaxial extension.

PubMed

Nicholson, David A; Rutledge, Gregory C

2016-12-28

Non-equilibrium molecular dynamics is used to study crystal nucleation of n-eicosane under planar shear and, for the first time, uniaxial extension. A method of analysis based on the mean first-passage time is applied to the simulation results in order to determine the effect of the applied flow field type and strain rate on the steady-state nucleation rate and a characteristic growth rate, as well as the effects on kinetic parameters associated with nucleation: the free energy barrier, critical nucleus size, and monomer attachment pre-factor. The onset of flow-enhanced nucleation (FEN) occurs at a smaller critical strain rate in extension as compared to shear. For strain rates larger than the critical rate, a rapid increase in the nucleation rate is accompanied by decreases in the free energy barrier and critical nucleus size, as well as an increase in chain extension. These observations accord with a mechanism in which FEN is caused by an increase in the driving force for crystallization due to flow-induced entropy reduction. At high applied strain rates, the free energy barrier, critical nucleus size, and degree of stretching saturate, while the monomer attachment pre-factor and degree of orientational order increase steadily. This trend is indicative of a significant diffusive contribution to the nucleation rate under intense flows that is correlated with the degree of global orientational order in a nucleating system. Both flow fields give similar results for all kinetic quantities with respect to the reduced strain rate, which we define as the ratio of the applied strain rate to the critical rate. The characteristic growth rate increases with increasing strain rate, and shows a correspondence with the nucleation rate that does not depend on the type of flow field applied. Additionally, a structural analysis of the crystalline clusters indicates that the flow field suppresses the compaction and crystalline ordering of clusters, leading to the formation of large articulated clusters under strong flow fields, and compact well-ordered clusters under weak flow fields.

Dynamic Behavior of AA2519-T8 Aluminum Alloy Under High Strain Rate Loading in Compression

NASA Astrophysics Data System (ADS)

Olasumboye, A. T.; Owolabi, G. M.; Odeshi, A. G.; Yilmaz, N.; Zeytinci, A.

2018-06-01

In this study, the effects of strain rate on the dynamic behavior, microstructure evolution and hence, failure of the AA2519-T8 aluminum alloy were investigated under compression at strain rates ranging from 1000 to 3500 s-1. Cylindrical specimens of dimensions 3.3 mm × 3.3 mm (L/D = 1) were tested using the split-Hopkinson pressure bar integrated with a digital image correlation system. The microstructure of the alloy was assessed using optical and scanning electron microscopes. Results showed that the dynamic yield strength of the alloy is strain rate dependent, with the maximum yield strength attained by the material being 500 MPa. The peak flow stress of 562 MPa was attained by the material at 3500 s-1. The alloy also showed a significant rate of strain hardening that is typical of other Al-Cu alloys; the rate of strain hardening, however, decreased with increase in strain rate. It was determined that the strain rate sensitivity coefficient of the alloy within the range of high strain rates used in this study is approximately 0.05 at 0.12 plastic strain; a more significant value than what was reported in literature under quasi-static loading. Micrographs obtained showed potential sites for the evolution of adiabatic shear band at 3500 s-1, with a characteristic circular-shaped surface profile comprising partially dissolved second phase particles in the continuous phase across the incident plane of the deformed specimen. The regions surrounding the site showed little or no change in the size of particles. However, the constituent coarse particles were observed as agglomerations of fractured pieces, thus having a shape factor different from those contained in the as-received alloy. Since the investigated alloy is a choice material for military application where it can be exposed to massive deformation at high strain rates, this study provides information on its microstructural and mechanical responses to such extreme loading condition.

Dynamic Behavior of AA2519-T8 Aluminum Alloy Under High Strain Rate Loading in Compression

NASA Astrophysics Data System (ADS)

Olasumboye, A. T.; Owolabi, G. M.; Odeshi, A. G.; Yilmaz, N.; Zeytinci, A.

2018-02-01

In this study, the effects of strain rate on the dynamic behavior, microstructure evolution and hence, failure of the AA2519-T8 aluminum alloy were investigated under compression at strain rates ranging from 1000 to 3500 s-1. Cylindrical specimens of dimensions 3.3 mm × 3.3 mm (L/D = 1) were tested using the split-Hopkinson pressure bar integrated with a digital image correlation system. The microstructure of the alloy was assessed using optical and scanning electron microscopes. Results showed that the dynamic yield strength of the alloy is strain rate dependent, with the maximum yield strength attained by the material being 500 MPa. The peak flow stress of 562 MPa was attained by the material at 3500 s-1. The alloy also showed a significant rate of strain hardening that is typical of other Al-Cu alloys; the rate of strain hardening, however, decreased with increase in strain rate. It was determined that the strain rate sensitivity coefficient of the alloy within the range of high strain rates used in this study is approximately 0.05 at 0.12 plastic strain; a more significant value than what was reported in literature under quasi-static loading. Micrographs obtained showed potential sites for the evolution of adiabatic shear band at 3500 s-1, with a characteristic circular-shaped surface profile comprising partially dissolved second phase particles in the continuous phase across the incident plane of the deformed specimen. The regions surrounding the site showed little or no change in the size of particles. However, the constituent coarse particles were observed as agglomerations of fractured pieces, thus having a shape factor different from those contained in the as-received alloy. Since the investigated alloy is a choice material for military application where it can be exposed to massive deformation at high strain rates, this study provides information on its microstructural and mechanical responses to such extreme loading condition.

A quantitative analysis of the effects of qualitatively different reinforcers on fixed ratio responding in inbred strains of mice

PubMed Central

Hutsell, Blake A.; Newland, M. Christopher

2013-01-01

Previous studies of inbred mouse strains have shown reinforcer-strain interactions that may potentially mask differences among strains in memory performance. The present research examined the effects of two qualitatively different reinforcers (heterogeneous mix of flavored pellets and sweetened-condensed milk) on responding maintained by fixed-ratio schedules of reinforcement in three inbred strains of mice (BALB/c, C57BL/6, & DBA/2). Responses rates for all strains were a bitonic (inverted U) function of the size of the fixed-ratio schedule and were generally higher when responding was maintained by milk. For the DBA/2 and C57BL/6 and to a lesser extent the BALB/c, milk primarily increased response rates at moderate fixed ratios, but not at the largest fixed ratios tested. A formal model of ratio-schedule performance, Mathematical Principles of Reinforcement (MPR), was applied to the response rate functions of individual mice. According to MPR, the differences in response rates maintained by pellets and milk were mostly due to changes in motoric processes as indicated by changes in the minimum response time (δ) produced by each reinforcer type and not specific activation (a), a model term that represents value and is correlated with reinforcer magnitude and the break point obtained under progressive ratio schedules. In addition, MPR also revealed that, although affected by reinforcer type, a parameter interpreted as the rate of saturation of working memory (λ), differed among the strains. PMID:23357283

Effect of strain wave shape on low-cycle fatigue crack propagation of SUS 304 stainless steel at elevated temperatures

NASA Astrophysics Data System (ADS)

Okazaki, Masakazu; Hattori, Ichiro; Shiraiwa, Fujio; Koizumi, Takashi

1983-08-01

Effect of strain wave shape on strain-controlled low-cycle fatigue crack propagation of SUS 304 stainless steel was investigated at 600 and 700 °C. It was found that the rate of crack propagation in a cycle-dependent region was successfully correlated with the range of cyclic J-integral, Δ Jf, regardless of the strain wave shape, frequency, and test temperature. It was also shown that the rate of crack propagation gradually increased from cycle-dependent curve to time-dependent one with decreasing frequency and slow-fast strain wave shape, and that one of the factors governing the rate of crack propagation in such a region was the ratio of the range of creep J-integral to that of total J-integral, Δ J c/Δ JT. Based on the results thus obtained, an interaction damage rule proposed semi-empirically was interpreted, with regard to crack propagation. Furthermore, fatigue crack initiation mechanism in slow-fast strain wave shape was studied, and it was shown that grain boundary sliding took an important role in it.

Study on Mechanical Properties of Barite Concrete under Impact Load

NASA Astrophysics Data System (ADS)

Chen, Z. F.; Cheng, K.; Wu, D.; Gan, Y. C.; Tao, Q. W.

2018-03-01

In order to research the mechanical properties of Barite concrete under impact load, a group of concrete compression tests was carried out under the impact load by using the drop test machine. A high-speed camera was used to record the failure process of the specimen during the impact process. The test results show that:with the increase of drop height, the loading rate, the peak load, the strain under peak load, the strain rate and the dynamic increase factor (DIF) all increase gradually. The ultimate tensile strain is close to each other, and the time of impact force decreases significantly, showing significant strain rate effect.

The effect of strain rate on the evolution of microstructure in aluminium alloys.

PubMed

Leszczyńska-Madej, B; Richert, M

2010-03-01

Intensive deformations influence strongly microstructure. The very well-known phenomenon is the diminishing dimension of grain size by the severe plastic deformation (SPD) methods. The nanometric features of microstructure were discovered after the SPD deformation of various materials, such as aluminium alloys, iron and others. The observed changes depended on the kind of the deformed material, amount of deformation, strain rate, existence of different phases and stacking fault energy. The influence of the strain and strain rate on the microstructure is commonly investigated nowadays. It was found that the high strain rates activate deformation in shear bands, microbands and adiabatic shear bands. It was observed that bands were places of the nucleation of nanograins in the material deformed by SPD methods. In the work, the refinement of microstructure of the aluminium alloys influenced by the high strain rate was investigated. The samples were compressed by a specially designed hammer to the deformation of phi= 0/0.62 with the strain rate in the range of [Formula in text]. The highest reduction of microbands width with the increase of the strain was found in the AlCu4Zr alloy. The influence of the strain rate on the microstructure refinement indicated that the increase of the strain rate caused the reduction of the microbands width in the all investigated materials (Al99.5, AlCu4Zr, AlMg5, AlZn6Mg2.5CuZr). A characteristic feature of the microstructure of the compressed material was large density of the shear bands and microbands. It was found that the microbands show a large misorientation to the surrounds and, except Al99.5, the large density of dislocation.

The role of local strains from prior cold work on stress corrosion cracking of α-brass in Mattsson's solution

DOE Office of Scientific and Technical Information (OSTI.GOV)

Ulaganathan, Jaganathan, E-mail: jagan.ulaganathan@mail.utoronto.ca; Newman, Roger C., E-mail: roger.newman@utoronto.ca

2014-06-01

The dynamic strain rate ahead of a crack tip formed during stress corrosion cracking (SCC) under a static load is assumed to arise from the crack propagation. The strain surrounding the crack tip would be redistributed as the crack grows, thereby having the effect of dynamic strain. Recently, several studies have shown cold work to cause accelerated crack growth rates during SCC, and the slip-dissolution mechanism has been widely applied to account for this via a supposedly increased crack-tip strain rate in cold worked material. While these interpretations consider cold work as a homogeneous effect, dislocations are generated inhomogeneously withinmore » the microstructure during cold work. The presence of grain boundaries results in dislocation pile-ups that cause local strain concentrations. The local strains generated from cold working α-brass by tensile elongation were characterized using electron backscatter diffraction (EBSD). The role of these local strains in SCC was studied by measuring the strain distributions from the same regions of the sample before cold work, after cold work, and after SCC. Though, the cracks did not always initiate or propagate along boundaries with pre-existing local strains from the applied cold work, the local strains surrounding the cracked boundaries had contributions from both the crack propagation and the prior cold work. - Highlights: • Plastic strain localization has a complex relationship with SCC susceptibility. • Surface relief created by cold work creates its own granular strain localization. • Cold work promotes crack growth but several other factors are involved.« less

Finite element simulations of the Portevin Le Chatelier effect in aluminium alloy

NASA Astrophysics Data System (ADS)

Hopperstad, O. S.; Børvik, T.; Berstad, T.; Benallal, A.

2006-08-01

Finite element simulations of the Portevin-Le Chatelier effect in aluminium alloy 5083-H116 are presented and evaluated against existing experimental results. The constitutive model of McCormick (1988) for materials exhibiting negative steady-state strain-rate sensitivity is incorporated into an elastic-viscoplastic model for large plastic deformations and implemented in LS-DYNA for use with the explicit or implicit solver. Axisymmetric tensile specimens loaded at different strain rates are studied numerically, and it is shown that the model predicts the experimental behaviour with reasonable accuracy; including serrated yielding and propagating bands of localized plastic deformation along the gauge length of the specimen at intermediate strain rates.

Characterization and Prediction of Flow Behavior in High-Manganese Twinning Induced Plasticity Steels: Part II. Jerky Flow and Instantaneous Strain Rate

NASA Astrophysics Data System (ADS)

Saeed-Akbari, A.; Mishra, A. K.; Mayer, J.; Bleck, W.

2012-05-01

The jerky and smooth flow curves in high-manganese twinning induced plasticity (TWIP) steels were investigated by comparing Fe-Mn-C and Fe-Mn-Al-C systems. The pronounced serrations on the flow curves of Fe-Mn-C TWIP steel, produced during tensile testing at 300 K (27 °C) and 373 K (100 °C), were shown to be the result of localized high-temperature Portevin Le-Chatelier (PLC) bands moving across the gage length throughout the deformation. The speed of the PLC bands and their temperature effects were found to be strongly dependent on the applied strain rate, which was controlled by adjusting the cross-head speed of the tensile testing machine. The localized temperature-dependent stacking fault energy (SFE) variations resulting from the PLC effect and adiabatic heating were analyzed and compared for both slow and fast deformation rates. The instabilities in the measured logarithmic strain values caused by jerky flow could cause the local strain rate to deviate systematically from the targeted (applied) strain rate. These instabilities are better observed by calculating the instantaneous strain rate (ISR) values for each instant of deformation along the entire gage length. Finally, a new type of diagram was developed by plotting the true stress against the ISR values. From the diagram, the onset of different mechanisms, such as deformation twinning, nonpronounced, and pronounced serrations, could be marked precisely.

Modeling the effect of laser heating on the strength and failure of 7075-T6 aluminum

DOE PAGES

Florando, J. N.; Margraf, J. D.; Reus, J. F.; ...

2015-06-06

The effect of rapid laser heating on the response of 7075-T6 aluminum has been characterized using 3-D digital image correlation and a series of thermocouples. The experimental results indicate that as the samples are held under a constant load, the heating from the laser profile causes non-uniform temperature and strain fields, and the strain-rate increases dramatically as the sample nears failure. Simulations have been conducted using the LLNL multi-physics code ALE3D, and compared to the experiments. The strength and failure of the material was modeled using the Johnson–Cook strength and damage models. Here, in order to capture the response, amore » dual-condition criterion was utilized which calibrated one set of parameters to low temperature quasi-static strain rate data, while the other parameter set is calibrated to high temperature high strain rate data. The thermal effects were captured using temperature dependent thermal constants and invoking thermal transport with conduction, convection, and thermal radiation.« less

Dynamic tensile stress-strain characteristics of carbon/epoxy laminated composites in through-thickness direction

NASA Astrophysics Data System (ADS)

Nakai, Kenji; Yokoyama, Takashi

2015-09-01

The effect of strain rate up to approximately ɛ˙ = 102/s on the tensile stress-strain properties of unidirectional and cross-ply carbon/epoxy laminated composites in the through-thickness direction is investigated. Waisted cylindrical specimens machined out of the laminated composites in the through-thickness direction are used in both static and dynamic tests. The dynamic tensile stress-strain curves up to fracture are determined using the split Hopkinson bar (SHB). The low and intermediate strain-rate tensile stress-strain relations up to fracture are measured on an Instron 5500R testing machine. It is demonstrated that the ultimate tensile strength and absorbed energy up to fracture increase significantly, while the fracture strain decreases slightly with increasing strain rate. Macro- and micro-scopic examinations reveal a marked difference in the fracture surfaces between the static and dynamic tension specimens.

Effects of Adiabatic Heating on the High Strain Rate Deformation of Polymer Matrix Composites

NASA Technical Reports Server (NTRS)

Sorini, Chris; Chattopadhyay, Aditi; Goldberg, Robert K.

2017-01-01

Polymer matrix composites (PMCs) are increasingly being used in aerospace structures that are expected to experience complex dynamic loading conditions throughout their lifetime. As such, a detailed understanding of the high strain rate behavior of the constituents, particularly the strain rate, temperature, and pressure dependent polymer matrix, is paramount. In this paper, preliminary efforts in modeling experimentally observed temperature rises due to plastic deformation in PMCs subjected to dynamic loading are presented. To this end, an existing isothermal viscoplastic polymer constitutive formulation is extended to model adiabatic conditions by incorporating temperature dependent elastic properties and modifying the components of the inelastic strain rate tensor to explicitly depend on temperature. It is demonstrated that the modified polymer constitutive model is capable of capturing strain rate and temperature dependent yield as well as thermal softening associated with the conversion of plastic work to heat at high rates of strain. The modified constitutive model is then embedded within a strength of materials based micromechanics framework to investigate the manifestation of matrix thermal softening, due to the conversion of plastic work to heat, on the high strain rate response of a T700Epon 862 (T700E862) unidirectional composite. Adiabatic model predictions for high strain rate composite longitudinal tensile, transverse tensile, and in-plane shear loading are presented. Results show a substantial deviation from isothermal conditions; significant thermal softening is observed for matrix dominated deformation modes (transverse tension and in-plane shear), highlighting the importance of accounting for the conversion of plastic work to heat in the polymer matrix in the high strain rate analysis of PMC structures.

Modeling of grain size strengthening in tantalum at high pressures and strain rates

DOE PAGES

Rudd, Robert E.; Park, H. -S.; Cavallo, R. M.; ...

2017-01-01

Laser-driven ramp wave compression experiments have been used to investigate the strength (flow stress) of tantalum and other metals at high pressures and high strain rates. Recently this kind of experiment has been used to assess the dependence of the strength on the average grain size of the material, finding no detectable variation with grain size. The insensitivity to grain size has been understood theoretically to result from the dominant effect of the high dislocation density generated at the extremely high strain rates of the experiment. Here we review the experiments and describe in detail the multiscale strength model usedmore » to simulate them. The multiscale strength model has been extended to include the effect of geometrically necessary dislocations generated at the grain boundaries during compatible plastic flow in the polycrystalline metal. Lastly, we use the extended model to make predictions of the threshold strain rates and grain sizes below which grain size strengthening would be observed in the laser-driven Rayleigh-Taylor experiments.« less

Probing collagen-enzyme mechanochemistry in native tissue with dynamic, enzyme-induced creep

PubMed Central

Zareian, Ramin; Church, Kelli P.; Saeidi, Nima; Flynn, Brendan P.; Beale, John W.; Ruberti, Jeffrey W.

2012-01-01

Mechanical strain or stretch of collagen has been shown to be protective of fibrils against both thermal and enzymatic degradation. The details of this mechanochemical relationship could change our understanding of load-bearing tissue formation, growth, maintenance and disease in vertebrate animals. However, extracting a quantitative relationship between strain and the rate of enzymatic degradation is extremely difficult in bulk tissue due to confounding diffusion effects. In this investigation, we develop a dynamic, enzyme-induced creep assay and diffusion/reaction rate scaling arguments to extract a lower bound on the relationship between strain and the cutting rate of bacterial collagenase (BC) at low strains. The assay method permits continuous, forced probing of enzyme-induced strain which is very sensitive to degradation rate differences between specimens at low initial strain. The results, obtained on uniaxially-loaded strips of bovine corneal tissue (0.1, 0.25 or 0.5 N), demonstrate that small differences in strain alter the enzymatic cutting rate of the BC substantially. It was estimated that a change in tissue elongation of only 1.5% (at ~5% strain) reduces the maximum cutting-rate of the enzyme by more than half. Estimation of the average load per monomer in the tissue strips indicates that this protective “cutoff” occurs when the collagen monomers are transitioning from an entropic to an energetic mechanical regime. The continuous tracking of the enzymatic cleavage rate as a function of strain during the initial creep response indicates that the decrease in the cleavage rate of the BC is non-linear (initially-steep between 4.5 and 6.5% then flattens out from 6.5–9.5%). The high sensitivity to strain at low strain implies that even lightly-loaded collagenous tissue may exhibit significant strain-protection. The dynamic, enzyme-induced creep assay described herein has the potential to permit the rapid characterization of collagen/enzyme mechanochemistry in many different tissue types. PMID:20429513

Suppression of Low Strain Rate Nonpremixed Flames by an Agent

NASA Technical Reports Server (NTRS)

Hamins, A.; Bundy, M.; Puri, I. K.; McGrattan, K.; Park, W. C.

2001-01-01

The agent concentration required to achieve the suppression of low strain rate nonpremixed flames is an important consideration for fire protection in a microgravity environment such as a space platform. Currently, there is a lack of understanding of the structure and extinction of low strain rate (<20 s(exp -1)) nonpremixed flames. The exception to this statement is the study by Maruta et al., who reported measurements of low strain rate suppression of methane-air diffusion flames with N2 added to the fuel stream under microgravity conditions. They found that the nitrogen concentration required to achieve extinction increased as the strain rate decreased until a critical value was obtained. As the strain rate was further decreased, the required N2 concentration decreased. This phenomenon was termed "turning point" behavior and was attributed to radiation-induced nonpremixed flame extinction. In terms of fire safety, a critical agent concentration assuring suppression under all flow conditions represents a fundamental limit for nonpremixed flames. Counterflow flames are a convenient configuration for control of the flame strain rate. In high and moderately strained near-extinction nonpremixed flames, analysis of flame structure typically neglects radiant energy loss because the flames are nonluminous and the hot gas species are confined to a thin reaction zone. In counterflowing CH4-air flames, for example, radiative heat loss fractions ranging from 1 to 6 percent have been predicted and measured. The objective of this study is to investigate the impact of radiative emission, flame strain, agent addition, and buoyancy on the structure and extinction of low strain rate nonpremixed flames through measurements and comparison with flame simulations. The suppression effectiveness of a number of suppressants (N2, CO2, or CF3Br) was considered as they were added to either the fuel or oxidizer streams of low strain rate methane-air diffusion flames.

Strain rate sensitivity of a TRIP-assisted dual-phase high-entropy alloy

NASA Astrophysics Data System (ADS)

Basu, Silva; Li, Zhiming; Pradeep, K. G.; Raabe, Dierk

2018-05-01

Dual-phase high-entropy alloys (DP-HEAs) with transformation induced plasticity (TRIP) have an excellent strength-ductility combination. To reveal their strain-rate sensitivity and hence further understand the corresponding deformation mechanisms, we investigated the tensile behavior and microstructural evolution of a typical TRIP-DP-HEA (Fe50Mn30Co10Cr10, at. %) under different strain rates (i.e., 5 × 10-3 s-1, 1 × 10-3 s-1, 5 × 10-4 s-1 and 1 × 10-4 s-1) at room temperature. The strain rate range was confined to this regime in order to apply the digital image correlation technique for probing the local strain evolution during tensile deformation at high resolution and to correlate it to the microstructure evolution. Grain size effects of the face-centered cubic (FCC) matrix and the volume fractions of the hexagonal-close packed (HCP) phase prior to deformation were also considered. The results show that within the explored strain rate regime the TRIP-DP-HEA has a fairly low strain rate sensitivity parameter within the range from 0.004 to 0.04, which is significantly lower than that of DP and TRIP steels. Samples with varying grain sizes (e.g., 2.8 μm and 38 μm) and starting HCP phase fractions (e.g., 25% and 72%) at different strain rates show similar deformation mechanisms, i.e., dislocation plasticity and strain-induced transformation from the FCC matrix to the HCP phase. The low strain rate sensitivity is attributed to the observed dominant displacive transformation mechanism. Also, the coarse-grained alloy samples with a very high starting HCP phase fraction ( 72%) prior to deformation show very good ductility with a total elongation of 60%, suggesting that both, the initial and the transformed HCP phase in the TRIP-DP-HEA are ductile and deform further via dislocation slip at the different strain rates which were probed.

Constitutive modeling of the mechanical behavior of high strength ferritic steels for static and dynamic applications

NASA Astrophysics Data System (ADS)

Abed, Farid H.

2010-11-01

A constitutive relation is presented in this paper to describe the plastic behavior of ferritic steel over a broad range of temperatures and strain rates. The thermo-mechanical behavior of high strength low alloy (HSLA-65) and DH-63 naval structural steels is considered in this study at strains over 40%. The temperatures and strain rates are considered in the range where dynamic strain aging is not effective. The concept of thermal activation analysis as well as the dislocation interaction mechanism is used in developing the flow model for both the isothermal and adiabatic viscoplastic deformation. The flow stresses of the two steels are very sensitive to temperature and strain rate, the yield stresses increase with decreasing temperatures and increasing strain rates. That is, the thermal flow stress is mainly captured by the yield stresses while the hardening stresses are totally pertained to the athermal component of the flow stress. The proposed constitutive model predicts results that compare very well with the measured ones at initial temperature range of 77 K to 1000 K and strain rates between 0.001 s-1 and 8500 s-1 for both steels.

Generalization of exponential based hyperelastic to hyper-viscoelastic model for investigation of mechanical behavior of rate dependent materials.

PubMed

Narooei, K; Arman, M

2018-03-01

In this research, the exponential stretched based hyperelastic strain energy was generalized to the hyper-viscoelastic model using the heredity integral of deformation history to take into account the strain rate effects on the mechanical behavior of materials. The heredity integral was approximated by the approach of Goh et al. to determine the model parameters and the same estimation was used for constitutive modeling. To present the ability of the proposed hyper-viscoelastic model, the stress-strain response of the thermoplastic elastomer gel tissue at different strain rates from 0.001 to 100/s was studied. In addition to better agreement between the current model and experimental data in comparison to the extended Mooney-Rivlin hyper-viscoelastic model, a stable material behavior was predicted for pure shear and balance biaxial deformation modes. To present the engineering application of current model, the Kolsky bars impact test of gel tissue was simulated and the effects of specimen size and inertia on the uniform deformation were investigated. As the mechanical response of polyurea was provided over wide strain rates of 0.0016-6500/s, the current model was applied to fit the experimental data. The results were shown more accuracy could be expected from the current research than the extended Ogden hyper-viscoelastic model. In the final verification example, the pig skin experimental data was used to determine parameters of the hyper-viscoelastic model. Subsequently, a specimen of pig skin at different strain rates was loaded to a fixed strain and the change of stress with time (stress relaxation) was obtained. The stress relaxation results were revealed the peak stress increases by applied strain rate until the saturated loading rate and the equilibrium stress with magnitude of 0.281MPa could be reached. Copyright © 2017 Elsevier Ltd. All rights reserved.

High temperature monotonic and cyclic deformation in a directionally solidified nickel-base superalloy

NASA Technical Reports Server (NTRS)

Huron, Eric S.

1986-01-01

Directionally solidified (DS) MAR-M246+Hf was tested in tension and fatigue, at temperatures from 20 C to 1093 C. Tests were performed on (001) oriented specimens at strain rates of 50 % and 0.5 % per minute. In tension, the yield strength was constant up to 704 C, above which the strength dropped off rapidly. A strong dependence of strength on strain rate was seen at the higher temperatures. The deformation mode was observed to change from heterogeneous to homogeneous with increasing temperature. Low Cycle Fatigue tests were done using a fully reversed waveform and total strain control. For a given plastic strain range, lives increased with increasing temperature. For a given temperature strain rate had a strong effect on life. At 704 C, decreasing strain rates decreased life, while at the higher temperatures, decreasing strain rates increased life, for a given plastic strain range. These results could be explained through considerations of the deformation modes and stress levels. At the higher temperatures, marked coarsening caused beneficial stress reductions, but oxidation limited the life. The longitudinal grain boundaries were found to influence slip behavior. The degree of secondary slip adjacent to the boundaries was found to be related to the degree of misorientation between the grains.

Fermentation of Acid-pretreated Corn Stover to Ethanol Without Detoxification Using Pichia stipitis

NASA Astrophysics Data System (ADS)

Agbogbo, Frank K.; Haagensen, Frank D.; Milam, David; Wenger, Kevin S.

In this work, the effect of adaptation on P. stipitis fermentation using acidpretreated corn stover hydrolyzates without detoxification was examined. Two different types of adaptation were employed, liquid hydrolyzate and solid state agar adaptation. Fermentation of 12.5% total solids undetoxified acid-pretreated corn stover was performed in shake flasks at different rotation speeds. At low rotation speed (100 rpm), both liquid hydrolyzate and solid agar adaptation highly improved the sugar consumption rate as well as ethanol production rate compared to the wild-type strains. The fermentation rate was higher for solid agar-adapted strains compared to liquid hydrolyzate-adapted strains. At a higher rotation speed (150 rpm), there was a faster sugar consumption and ethanol production for both the liquid-adapted and the wild-type strains. However, improvements in the fermentation rate between the liquid-adapted and wild strains were less pronounced at the high rotation speed.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Song, Bo; Nelson, Kevin; Jin, Helena

Iridium alloys have been utilized as structural materials for certain high-temperature applications, due to their superior strength and ductility at elevated temperatures. The mechanical properties, including failure response at high strain rates and elevated temperatures of the iridium alloys need to be characterized to better understand high-speed impacts at elevated temperatures. A DOP-26 iridium alloy has been dynamically characterized in compression at elevated temperatures with high-temperature Kolsky compression bar techniques. However, the dynamic high-temperature compression tests were not able to provide sufficient dynamic high-temperature failure information of the iridium alloy. In this study, we modified current room-temperature Kolsky tension barmore » techniques for obtaining dynamic tensile stress-strain curves of the DOP-26 iridium alloy at two different strain rates (~1000 and ~3000 s-1) and temperatures (~750°C and ~1030°C). The effects of strain rate and temperature on the tensile stress-strain response of the iridium alloy were determined. The DOP-26 iridium alloy exhibited high ductility in stress-strain response that strongly depended on both strain rate and temperature.« less

Constant strain rate and peri-implant bone modeling: an in vivo longitudinal micro-CT analysis.

PubMed

De Smet, Els; Jaecques, Siegfried V N; Wevers, Martine; Sloten, Jos Vander; Naert, Ignace E

2013-06-01

Strain, frequency, loading time, and strain rate, among others, determine mechanical parameters in osteogenic loading. We showed a significant osteogenic effect on bone mass (BM) by daily peri-implant loading at 1.600µε.s(-1) after 4 weeks. To study the peri-implant osteogenic effect of frequency and strain in the guinea pig tibia by in vivo longitudinal micro-computed tomography (CT) analysis. One week after implant installation in both hind limb tibiae, one implant was loaded daily for 10' during 4 weeks, while the other served as control. Frequencies (3, 10, and 30Hz) and strains varied alike in the three series to keep the strain rate constant at 1.600µε.s(-1) . In vivo micro-CT scans were taken of both tibiae: 1 week after implantation but before loading (v1) and after 2 (v2) and 4 weeks (v3) of loading as well as postmortem (pm). BM (BM (%) bone-occupied area fraction) was calculated as well as the difference between test and control sides (delta BM) RESULTS: All implants (n=78) were clinically stable at 4 weeks. Significant increase in BM was measured between v1 and v2 (p<.0001) and between v1 and v3 (p<.0001). A significant positive effect of loading on delta BM was observed in the distal peri-implant marrow 500 Region of Interest already 2 weeks after loading (p=.01) and was significantly larger (11%) in series 1 compared with series 2 (p=.006) and 3 (p=.016). Within the constraints of constant loading time and strain rate, the effect of early implant loading on the peri-implant bone is strongly dependent on strain and frequency. This cortical bone model has shown to be most sensitive for high force loading at low frequency. © 2011 Wiley Periodicals, Inc.

Strain Rate and Stress Triaxiality Effects on Ductile Damage of Additive Manufactured TI-6AL-4V

NASA Astrophysics Data System (ADS)

Iannitti, Gianluca; Bonora, Nicola; Gentile, Domenico; Ruggiero, Andrew; Testa, Gabriel; Gubbioni, Simone

2017-06-01

In this work, the effects of strain rate and stress triaxiality on ductile damage of additive manufactured Ti-6Al-4V, also considering the build direction, were investigated. Raw material was manufactured by means of EOSSINT M2 80 machine, based on Direct Metal Laser Sintering technology, and machined to obtain round notched bar and Rod-on-Rod (RoR) specimens. Tensile tests on round notched bar specimens were performed in a wide range of strain rates. The failure strains at different stress triaxiality were used to calibrate the Bonora Damage Model. In order to design the RoR tests, numerical simulations were performed for assessing velocities at which incipient and fully developed damage occur. Tests at selected velocities were carried out and soft-recovered specimens were sectioning and polishing to observe the developed damage. Nucleated voids maps were compared with numerical simulations results.

Characterizing the adhesion of motile and nonmotile Escherichia coli to a glass surface using a parallel-plate flow chamber.

PubMed

McClaine, Jennifer W; Ford, Roseanne M

2002-04-20

A parallel-plate flow chamber was used to measure the attachment and detachment rates of Escherichia coli to a glass surface at various fluid velocities. The effect of flagella on adhesion was investigated by performing experiments with several E. coli strains: AW405 (motile); HCB136 (nonmotile mutant with paralyzed flagella); and HCB137 (nonmotile mutant without flagella). We compared the total attachment rates and the fraction of bacteria retained on the surface to determine how the presence and movement of the flagella influence transport to the surface and adhesion strength in this dynamic system. At the lower fluid velocities, there was no significant difference in the total attachment rates for the three bacterial strains; nonmotile strains settled at a rate that was of the same order of magnitude as the diffusion rate of the motile strain. At the highest fluid velocity, the effect of settling was minimized to better illustrate the importance of motility, and the attachment rates of both nonmotile strains were approximately five times slower than that of the motile bacteria. Thus, different processes controlled the attachment rate depending on the parameter regime in which the experiment was performed. The fractions of motile bacteria retained on the glass surface increased with increasing velocity, whereas the opposite trend was found for the nonmotile strains. This suggests that the rotation of the flagella enables cells to detach from the surface (at the lower fluid velocities) and strengthens adhesion (at higher fluid velocities), whereas nonmotile cells detach as a result of shear. There was no significant difference in the initial attachment rates of the two nonmotile species, which suggests that merely the presence of flagella was not important in this stage of biofilm development. Copyright 2002 Wiley Periodicals, Inc.

Gas Release as a Deformation Signal

DOE Office of Scientific and Technical Information (OSTI.GOV)

Bauer, Stephen J.

Radiogenic noble gases are contained in crustal rock at inter and intra granular sites. The gas composition depends on lithology, geologic history, fluid phases, and the aging effect by decay of U, Th, and K. The isotopic signature of noble gases found in rocks is vastly different than that of the atmosphere which is contributed by a variety of sources. When rock is subjected to stress conditions exceeding about half its yield strength, micro-cracks begin to form. As rock deformation progresses a fracture network evolves, releasing trapped noble gases and changing the transport properties to gas migration. Thus, changes inmore » gas emanation and noble gas composition from rocks could be used to infer changes in stress-state and deformation. The purpose of this study has been to evaluate the effect of deformation/strain rate upon noble gas release. Four triaxial experiments were attempted for a strain rate range of %7E10-8 /s (180,000s) to %7E 10-4/s (500s); the three fully successful experiments (at the faster strain rates) imply the following: (1) helium is measurably released for all strain rates during deformation, this release is in amounts 1-2 orders of magnitude greater than that present in the air, and (2) helium gas release increases with decreasing strain rate.« less

[Effect of elastic strain rate ratio method and virtual touch tissue quantification on the diagnosis of breast masses].

PubMed

Gong, LiJie; He, Yan; Tian, Peng; Yan, Yan

2016-07-01

To determine the effect of elastic strain rate ratio method and virtual touch tissue quantification (VTQ) on the diagnosis of breast masses.
 Sixty female patients with breast cancer, who received surgical treatment in Daqing Oilfield General Hospital, were enrolled. All patients signed the informed consent paperwork and they were treated by routine ultrasound examination, compression elastography (CE) examination, and VTQ examination in turn. Strain ratio (SR) was checked by CE and shear wave velocity (SWV) value was measured by VTQ. The diagnostic values of different methods were evaluated by receiver operating characteristic (ROC) curves in the diagnosis of benign and malignant breast tumors.
 The maximum diameter and SWV value of the benign tumors were lower than those of the malignant tumors, and the SR ratio of benign masses was higher than that of malignant tumors (P<0.01). The AUC, sensitivity and specificity for elastic strain rate and VTQ for single or combined use were higher than those of conventional ultrasound (0.904, 97.5%, 69.2%; 0.946, 87.5%, 87.2%; 0.976, 90%, 97.4% vs 0.783, 85%, 61.5%). The AUC and specificity of VTQ were higher than those of the elastic strain rate (0.946, 87.2% vs 0.904, 69.2%), but the sensitivity of VTQ was higher than that of the latter (87.5% vs 97.5%). The AUC and specificity for combination of both methods were higher than those of single method, but the sensitivity was lower than that of the elastic strain rate. 
 Combination of elastic strain rate ratio method with VTQ possesses the best diagnostic value and the highest diagnostic accuracy in the diagnosis of breast mass than that used alone.

An equivalent dissipation rate model for capturing history effects in non-premixed flames

DOE PAGES

Kundu, Prithwish; Echekki, Tarek; Pei, Yuanjiang; ...

2016-11-11

The effects of strain rate history on turbulent flames have been studied in the. past decades with 1D counter flow diffusion flame (CFDF) configurations subjected to oscillating strain rates. In this work, these unsteady effects are studied for complex hydrocarbon fuel surrogates at engine relevant conditions with unsteady strain rates experienced by flamelets in a typical spray flame. Tabulated combustion models are based on a steady scalar dissipation rate (SDR) assumption and hence cannot capture these unsteady strain effects; even though they can capture the unsteady chemistry. In this work, 1D CFDF with varying strain rates are simulated using twomore » different modeling approaches: steady SDR assumption and unsteady flamelet model. Comparative studies show that the history effects due to unsteady SDR are directly proportional to the temporal gradient of the SDR. A new equivalent SDR model based on the history of a flamelet is proposed. An averaging procedure is constructed such that the most recent histories are given higher weights. This equivalent SDR is then used with the steady SDR assumption in 1D flamelets. Results show a good agreement between tabulated flamelet solution and the unsteady flamelet results. This equivalent SDR concept is further implemented and compared against 3D spray flames (Engine Combustion Network Spray A). Tabulated models based on steady SDR assumption under-predict autoignition and flame lift-off when compared with an unsteady Representative Interactive Flamelet (RIF) model. However, equivalent SDR model coupled with the tabulated model predicted autoignition and flame lift-off very close to those reported by the RIF model. This model is further validated for a range of injection pressures for Spray A flames. As a result, the new modeling framework now enables tabulated models with significantly lower computational cost to account for unsteady history effects.« less

An equivalent dissipation rate model for capturing history effects in non-premixed flames

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kundu, Prithwish; Echekki, Tarek; Pei, Yuanjiang

The effects of strain rate history on turbulent flames have been studied in the. past decades with 1D counter flow diffusion flame (CFDF) configurations subjected to oscillating strain rates. In this work, these unsteady effects are studied for complex hydrocarbon fuel surrogates at engine relevant conditions with unsteady strain rates experienced by flamelets in a typical spray flame. Tabulated combustion models are based on a steady scalar dissipation rate (SDR) assumption and hence cannot capture these unsteady strain effects; even though they can capture the unsteady chemistry. In this work, 1D CFDF with varying strain rates are simulated using twomore » different modeling approaches: steady SDR assumption and unsteady flamelet model. Comparative studies show that the history effects due to unsteady SDR are directly proportional to the temporal gradient of the SDR. A new equivalent SDR model based on the history of a flamelet is proposed. An averaging procedure is constructed such that the most recent histories are given higher weights. This equivalent SDR is then used with the steady SDR assumption in 1D flamelets. Results show a good agreement between tabulated flamelet solution and the unsteady flamelet results. This equivalent SDR concept is further implemented and compared against 3D spray flames (Engine Combustion Network Spray A). Tabulated models based on steady SDR assumption under-predict autoignition and flame lift-off when compared with an unsteady Representative Interactive Flamelet (RIF) model. However, equivalent SDR model coupled with the tabulated model predicted autoignition and flame lift-off very close to those reported by the RIF model. This model is further validated for a range of injection pressures for Spray A flames. As a result, the new modeling framework now enables tabulated models with significantly lower computational cost to account for unsteady history effects.« less

Reactive Molecular Dynamics Simulations to Understand Mechanical Response of Thaumasite under Temperature and Strain Rate Effects.

PubMed

Hajilar, Shahin; Shafei, Behrouz; Cheng, Tao; Jaramillo-Botero, Andres

2017-06-22

Understanding the structural, thermal, and mechanical properties of thaumasite is of great interest to the cement industry, mainly because it is the phase responsible for the aging and deterioration of civil infrastructures made of cementitious materials attacked by external sources of sulfate. Despite the importance, effects of temperature and strain rate on the mechanical response of thaumasite had remained unexplored prior to the current study, in which the mechanical properties of thaumasite are fully characterized using the reactive molecular dynamics (RMD) method. With employing a first-principles based reactive force field, the RMD simulations enable the description of bond dissociation and formation under realistic conditions. From the stress-strain curves of thaumasite generated in the x, y, and z directions, the tensile strength, Young's modulus, and fracture strain are determined for the three orthogonal directions. During the course of each simulation, the chemical bonds undergoing tensile deformations are monitored to reveal the bonds responsible for the mechanical strength of thaumasite. The temperature increase is found to accelerate the bond breaking rate and consequently the degradation of mechanical properties of thaumasite, while the strain rate only leads to a slight enhancement of them for the ranges considered in this study.

Mechanics of wafer bonding: Effect of clamping

NASA Astrophysics Data System (ADS)

Turner, K. T.; Thouless, M. D.; Spearing, S. M.

2004-01-01

A mechanics-based model is developed to examine the effects of clamping during wafer bonding processes. The model provides closed-form expressions that relate the initial geometry and elastic properties of the wafers to the final shape of the bonded pair and the strain energy release rate at the interface for two different clamping configurations. The results demonstrate that the curvature of bonded pairs may be controlled through the use of specific clamping arrangements during the bonding process. Furthermore, it is demonstrated that the strain energy release rate depends on the clamping configuration and that using applied loads usually leads to an undesirable increase in the strain energy release rate. The results are discussed in detail and implications for process development and bonding tool design are highlighted.

Strain Rate Sensitivity of Polymer-Matrix Composites under Mode I delamination

DTIC Science & Technology

1990-12-01

unstable growth system requires two values. In reality , the fracture toughness may vary along the length of the specimen due to strain rate effects...18 M. F. Kanninen. An Augmented Double Cantilever Beam Model for Studying Crack Propagation and Arrest. International Journal of Fracture. Vol. 9

Effect of long-term caloric restriction on oxygen consumption and body temperature in two different strains of mice

PubMed Central

Ferguson, Melissa; Sohal, Barbara H.; Forster, Michael J.; Sohal, Rajindar S.

2007-01-01

The hypothesis, that a decrease in metabolic rate mediates the life span prolonging effect of caloric restriction (CR), was tested using two strains of mice, one of which, C57BL/6, exhibits life span extension as a result of CR, while the other, DBA/2, shows little or no effect. Comparisons of the rate of resting oxygen consumption and body temperature were made between the strains after they were fed ad libitum (AL) or maintained under 40% CR, from 4 to 16 months of age. Ad libitum-fed mice of the two strains weighed the same when young and consumed similar amounts of food throughout the experiment; however, the C57BL/6 mice weighed 25% more than DBA/2 mice at 15 months of age. The rate of oxygen consumption was normalized as per gram body weight, lean body mass or organ weight as well as per animal. The body temperature and the rate of oxygen consumption, expressed according to all of the four criteria, were decreased in the DBA/2 mice following CR. The C57BL/6 mice also showed a CR-related decrease in body temperature and in the rate of oxygen consumption per animal and when normalized according to lean body mass or organ weight. The results of this study indicate that CR indeed lowers the rate of metabolism; however, this effect by CR does not necessarily entail the prolongation of the life span of mice. PMID:17822741

Effect of long-term caloric restriction on oxygen consumption and body temperature in two different strains of mice.

PubMed

Ferguson, Melissa; Sohal, Barbara H; Forster, Michael J; Sohal, Rajindar S

2007-10-01

The hypothesis, that a decrease in metabolic rate mediates the life span prolonging effect of caloric restriction (CR), was tested using two strains of mice, one of which, C57BL/6, exhibits life span extension as a result of CR, while the other, DBA/2, shows little or no effect. Comparisons of the rate of resting oxygen consumption and body temperature were made between the strains after they were fed ad libitum (AL) or maintained under 40% CR, from 4 to 16 months of age. Ad libitum-fed mice of the two strains weighed the same when young and consumed similar amounts of food throughout the experiment; however, the C57BL/6 mice weighed 25% more than DBA/2 mice at 15 months of age. The rate of oxygen consumption was normalized as per gram body weight, lean body mass or organ weight as well as per animal. The body temperature and the rate of oxygen consumption, expressed according to all of the four criteria, were decreased in the DBA/2 mice following CR. The C57BL/6 mice also showed a CR-related decrease in body temperature and in the rate of oxygen consumption per animal and when normalized according to lean body mass or organ weight. The results of this study indicate that CR indeed lowers the rate of metabolism; however, this effect by CR does not necessarily entail the prolongation of the life span of mice.

Thermomechanical coupling and dynamic strain ageing in ductile fracture

NASA Astrophysics Data System (ADS)

Delafosse, David

1995-01-01

This work is concerned with plastic deformation at the tip of a ductile tearing crack during propagation. Two kinds of effects are investigated: the thermomechanical coupling at the tip of a mobile ductile crack, and the influence of Dynamic Strain Aging (DSA) on ductile fracture. Three alloys are studied: a nickel based superalloy (N18), a soft carbon steel, and an Al-Li light alloy (2091). The experimental study of the thermo mechanical coupling effects by means of infrared thermography stresses the importance of plastic dissipation in the energy balance of ductile fracture. Numerical simulations involving plastic deformation as the only dissipation mechanism account for the main part of the measured heating. The effects of DSA on ductile tearing are investigated in the 2091 Al-Li alloy. Based on the strain rate/temperature dependence predicted by the standard model of DSA, an experimental procedure is set up for this purpose. Three main effects are evidenced. A maximum in tearing resistance is shown to be associated with the minimum of strain rate sensitivity. Through a simple model, this peak in tearing resistance is attributed to an increase in plastic dissipation as the strain rate sensitivity is decreased. Heterogenous plastic deformation is observed in the crack tip plastic zone. Comparison with uniaxial testing allows us to identify the observed strain heterogeneities as Portevin-Le Chatelier instabilities in the crack tip plastic zone. We perform a simplified numerical analysis of the effect of strain localization on crack tip screening. Finally, small crack propagation instabilities appear at temperatures slightly above that of the tearing resistance peak. These are interpreted as resulting from a positive feed-back between the local heating at the tip of a moving crack and the decrease in tearing resistance with increasing temperature.

Impact of measurement uncertainty from experimental load distribution factors on bridge load rating

NASA Astrophysics Data System (ADS)

Gangone, Michael V.; Whelan, Matthew J.

2018-03-01

Load rating and testing of highway bridges is important in determining the capacity of the structure. Experimental load rating utilizes strain transducers placed at critical locations of the superstructure to measure normal strains. These strains are then used in computing diagnostic performance measures (neutral axis of bending, load distribution factor) and ultimately a load rating. However, it has been shown that experimentally obtained strain measurements contain uncertainties associated with the accuracy and precision of the sensor and sensing system. These uncertainties propagate through to the diagnostic indicators that in turn transmit into the load rating calculation. This paper will analyze the effect that measurement uncertainties have on the experimental load rating results of a 3 span multi-girder/stringer steel and concrete bridge. The focus of this paper will be limited to the uncertainty associated with the experimental distribution factor estimate. For the testing discussed, strain readings were gathered at the midspan of each span of both exterior girders and the center girder. Test vehicles of known weight were positioned at specified locations on each span to generate maximum strain response for each of the five girders. The strain uncertainties were used in conjunction with a propagation formula developed by the authors to determine the standard uncertainty in the distribution factor estimates. This distribution factor uncertainty is then introduced into the load rating computation to determine the possible range of the load rating. The results show the importance of understanding measurement uncertainty in experimental load testing.

Shock Response and Dynamic Failure of Spatially Tailored Aero-Thermal Structures

DTIC Science & Technology

2012-09-15

Deformation Behavior of Nanolaminated Titanium Aluminum Carbide. 36th International Conference and Exposition on Advanced Ceramics and Composites ...Deformation Behavior of Nanolaminated Titanium Aluminum Carbide. Effect of Strain-rate and Temperature on Dynamic Deformation of Nanolaminated...conditions, we are unaware of any studies published in the open literature on the effect of high strain rate deformation behavior of Ti2AlC at room or

Force-Strain Characteristics and Rupture-Load Capability of Viking-Type Suspension-Line Material Under Dynamic Loading Conditions

NASA Technical Reports Server (NTRS)

Poole, Lamont R.; Councill, Earl L., Jr.

1972-01-01

A series of tests has been conducted to investigate the elastic behavior of Viking-type suspension-line material under dynamic loading conditions. Results indicate that there is a decrease in both rupture-load capability and elongation at rupture as the test strain rate is increased. Preliminary examination of force-strain characteristics indicates that, on the average, the material exhibits some type of viscous effect which results in a greater force being produced, for a particular value of strain, under dynamic loading conditions than that produced under quasi-static loading conditions. A great deal of uncertainty exists in defining a priori the tensile properties of viscoelastic materials, such as nylon or dacron, under dynamic loading conditions. Additional uncertainty enters the picture when woven configurations such as suspension,line material are considered. To eliminate these uncertainties, with respect to the Viking parachute configuration, a test program has been conducted to obtain data on the tensile properties of Viking-type suspension-line material over a wide range of strain rates. Based on preliminary examination of these data, the following conclusions can be drawn: 1. Material rupture-load capability decreases as strain-rate is increased. At strain rates above 75 percent/sec, no rupture loads were observed which would meet the minimum tensile strength specification of 880 pounds. 2. The material, on the average, exhibits some type of viscous effect which, for a particular value of strain, produces a greater load under dynamic loading conditions than that produced under quasi-static loading conditions.

Effect of extremely low frequency electromagnetic fields on growth rate and morphology of bacteria.

PubMed

Inhan-Garip, Ayse; Aksu, Burak; Akan, Zafer; Akakin, Dilek; Ozaydin, A Nilufer; San, Tangul

2011-12-01

To determine the effect of extremely low frequency (<300 Hz) electromagnetic fields (ELF-EMF) on the growth rate of Gram-positive and Gram-negative bacteria and to determine any morphological changes that might have been caused by ELF-EMF. Six bacterial strains, three Gram-negative and three Gram-positive were subjected to 50 Hz, 0.5 mT ELF-EMF for 6 h. To determine growth rate after ELF-EMF application, bacteria exposed to ELF-EMF for 3 h were collected, transferred to fresh medium and cultured without field application for another 4 h. Growth-rate was determined by optical density (OD) measurements made every hour. Morphological changes were determined with Transmission electron microscopy (TEM) for two gram-negative and two gram-positive strains collected after 3 h of field application. A decrease in growth rate with respect to control samples was observed for all strains during ELF-EMF application. The decrease in growth-rate continued when exposed bacteria were cultured without field application. Significant ultrastructural changes were observed in all bacterial strains, which were seen to resemble the alterations caused by cationic peptides. This study shows that ELF-EMF induces a decrease in growth rate and morphological changes for both Gram-negative and Gram-positive bacteria.

The Effects of Specimen Geometry and Size on the Dynamic Failure of Aluminum Alloy 2219-T8 Under Impact Loading

NASA Astrophysics Data System (ADS)

Bolling, Denzell Tamarcus

A significant amount of research has been devoted to the characterization of new engineering materials. Searching for new alloys which may improve weight, ultimate strength, or fatigue life are just a few of the reasons why researchers study different materials. In support of that mission this study focuses on the effects of specimen geometry and size on the dynamic failure of AA2219 aluminum alloy subjected to impact loading. Using the Split Hopkinson Pressure Bar (SHPB) system different geometric samples including cubic, rectangular, cylindrical, and frustum samples are loaded at different strain rates ranging from 1000s-1 to 6000s-1. The deformation properties, including the potential for the formation of adiabatic shear bands, of the different geometries are compared. Overall the cubic geometry achieves the highest critical strain and the maximum stress values at low strain rates and the rectangular geometry has the highest critical strain and the maximum stress at high strain rates. The frustum geometry type consistently achieves the lowest the maximum stress value compared to the other geometries under equal strain rates. All sample types clearly indicated susceptibility to strain localization at different locations within the sample geometry. Micrograph analysis indicated that adiabatic shear band geometry was influenced by sample geometry, and that specimens with a circular cross section are more susceptible to shear band formation than specimens with a rectangular cross section.

Assessment of structural, thermal, and mechanical properties of portlandite through molecular dynamics simulations

DOE Office of Scientific and Technical Information (OSTI.GOV)

Hajilar, Shahin, E-mail: shajilar@iastate.edu; Shafei, Behrouz, E-mail: shafei@iastate.edu

The structural, thermal, and mechanical properties of portlandite, the primary solid phase of ordinary hydrated cement paste, are investigated using the molecular dynamics method. To understand the effects of temperature on the structural properties of portlandite, the coefficients of thermal expansion of portlandite are determined in the current study and validated with what reported from the experimental tests. The atomic structure of portlandite equilibrated at various temperatures is then subjected to uniaxial tensile strains in the three orthogonal directions and the stress-strain curves are developed. Based on the obtained results, the effect of the direction of straining on the mechanicalmore » properties of portlandite is investigated in detail. Structural damage analysis is performed to reveal the failure mechanisms in different directions. The energies of the fractured surfaces are calculated in different directions and compared to those of the ideal surfaces available in the literature. The key mechanical properties, including tensile strength, Young's modulus, and fracture strain, are extracted from the stress-strain curves. The sensitivity of the obtained mechanical properties to temperature and strain rate is then explored in a systematic way. This leads to valuable information on how the structural and mechanical properties of portlandite are affected under various exposure conditions and loading rates. - Graphical abstract: Fracture mechanism of portlandite under uniaxial strain in the z-direction. - Highlights: • The structural, thermal, and mechanical properties of portlandite are investigated. • The coefficients of thermal expansion are determined. • The stress-strain relationships are studied in three orthogonal directions. • The effects of temperature and strain rate on mechanical properties are examined. • The plastic energy required for fracture in the crystalline structure is reported.« less

[Pharmacokinetics and clinical effects of aspoxicillin in pediatric patients].

PubMed

Fujii, R; Meguro, H; Kim, B; Yonezawa, H; Kawaoi, T; Tajima, T; Mashiko, J; Nakazawa, S; Niino, K; Sato, H

1987-09-01

Since the efficacy and the safety of aspoxicillin (ASPC, TA-058) have been established on adult patients and the need of ASPC use on pediatric patients was anticipated, we performed a 16 center study on the clinical utility of ASPC in pediatric patients. 1. Pharmacokinetics ASPC was intravenously administered to 45 patients at a dose of 10, 20 or 40 mg/kg by one shot. Serum concentrations of ASPC were dependent of dose levels, and maximum levels of 58.4-230.8 micrograms/ml and half-lives (beta) of 1.08-1.16 hours were observed. Urinary recovery rates were 62.7-67.2% in 6 hours. Results obtained upon drip infusions (0.5-1 hour) were similar to one shot injections. 2. Clinical results (1) Clinical effectiveness Of 318 evaluable patients including 175 boys and 143 girls, 18.2% were nurslings and 61% were young children under 4 years of age. One hundred eighty six patients from whom causative organisms were isolated were classified as A group. Among them were 5 patients suffered with sepsis, but the ASPC treatment eradicated all the bacteria but Salmonella java in 1 case. All of 4 patients with meningitis were cured and all causative organisms (3 cases with Haemophilus influenzae and 1 case with Gram-positive coccus) were eradicated. Cure rates were 90% for 130 patients with respiratory tract infection, 88.6% for 35 with urinary tract infection, 85.7% for 7 with skin soft tissue infection and 89.8% for all the A group patients. Meanwhile, no causative organisms were isolated from 132 patients (B group patients) but cure rate of 91.7% was obtained for this group. No statistical difference was observed between A and B groups. For all the patients (318), the cure rate was 90.6%. (2) Bacteriological effects Of 63 Gram-positive bacteria isolated as pathogens, 58 strains were eradicated. Of 117 Gram-negative bacterial, 101 were eradicated. The eradication rate on all 180 strains was 88.3%. Overall, ASPC showed excellent effects against Streptococcus. Among strains of Staphylococcus aureus, 18 of 20 strains were eradicated. Of 59 strains of H. influenzae, 52 were eradicated and 3 decreased. Among strains of Escherichia coli, 25 of 28 strains were eradicated. Of Pseudomonas aeruginosa, 2 strains were decreased and one was unchanged. (3) ASPC was effective in 93.3% of 30 patients with serious infections and 79.2% of 72 patients with underlying diseases. Cure rates for patients with and without underlying disease were significantly different statistically (chi 2: P less than 0.005).(ABSTRACT TRUNCATED AT 400 WORDS)

Dynamic strain-aging effect on fracture toughness of vessel steels

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kang, S.S.; Kim, I.S.

1992-03-01

In this paper the effect of dynamic strain aging (DSA) on fracture is investigated on the quenched and tempered specimens of American Society of Mechanical Engineers (ASME) standard SA508 class 3 nuclear pressure vessel steel. Serrated flow by DSA is observed between 180 and 340{degrees}C at a tensile strain rate of 2.08 {times} 10{sup {minus}4}/s and 1.25 {times} 10{sup {minus}3}/s. The DSA causes a sharp rise in the ultimate tensile strength and a marked decrease in ductility. The DSA range shifts to higher temperatures with increased strain rates. The temperature and strain rate dependence of the onset of serrations yieldsmore » an activation energy of 16.2 kcal/mol, which suggests that the process is controlled by interstitial diffusion of carbon and nitrogen in ferrite. The J{sub i} value obtained from the direct current potential drop (DCPD) method, for true crack initiation, is lowered by DSA. The drop in J{sub i} at elevated temperatures may be because of the interaction of the interstitial impurities with dislocations at the crack front.« less

Effects of strain rate and temperature on the mechanical behavior of carbon black reinforced elastomers based on butyl rubber and high molecular weight polyethylene

NASA Astrophysics Data System (ADS)

Hussein, M.

2018-06-01

The influence of the mechanical property and morphology of different blend ratio of Butyl rubber (IIR)/high molecular weight polyethylene (PE) by temperature and strain rate are performed. Special attention has been considered to a ductile-brittle transition that is known to occur at around 60 °C. The idea is to explain the unexpected phenomenon of brittleness which directly related to all tensile mechanical properties such as the strength of blends, modulus of elasticity of filled and unfilled IIR-polyethylene blends. In particular, the initial Young's modulus, tensile strength and strain at failure exhibit similar dependency on strain rate and temperature. These quantities lowered and increased with an increment of temperature, whereas the increased with increasing of strain rate. Furthermore, the tensile strength and strain at failure decreases for all temperatures range with the increase of PE content in the blend, except Young's modulus in reverse. The strain rate sensitivity index parameter of the examined polymeric materials is consistent with the micro-mechanisms of deformation and the behavior was well described by an Eyring relationship leading to an activation volume of ∼1 nm3, except for the highest value of unfilled IIR ∼8.45 nm3.

Effects of uniaxial strain on electron effective mass and tunneling capability of direct gap Ge{sub 1−x}Sn{sub x} alloys

DOE Office of Scientific and Technical Information (OSTI.GOV)

Liu, Lei; Liang, Renrong, E-mail: liangrr@tsinghua.edu.cn; Wang, Jing

2016-01-15

Direct gap Ge{sub 1−x}Sn{sub x} alloys under [100] and [110] uniaxial strain are comprehensively investigated by theoretical calculations using the nonlocal empirical pseudopotential method (EPM). It is shown that [100] uniaxial tensile strain aids indirect-to-direct gap transition in Ge{sub 1−x}Sn{sub x} alloys. The Γ electron effective mass along the optimal direction under [110] uniaxial strain is smaller than those under [100] uniaxial strain and (001) biaxial strain. Additionally, the direct tunneling gap is smallest along the strain-perpendicular direction under [110] uniaxial tensile strain, resulting in a maximum direct band-to-band tunneling generation rate. An optimal [110] uniaxial tensile strain is favorablemore » for high-performance direct gap Ge{sub 1−x}Sn{sub x} electronic devices.« less

Orientation and length of mammalian skeletal myocytes in response to a unidirectional stretch

NASA Technical Reports Server (NTRS)

Collinsworth, A. M.; Torgan, C. E.; Nagda, S. N.; Rajalingam, R. J.; Kraus, W. E.; Truskey, G. A.

2000-01-01

Effects of mechanical forces exerted on mammalian skeletal muscle cells during development were studied using an in vitro model to unidirectionally stretch cultured C2C12 cells grown on silastic membrane. Previous models to date have not studied these responses of the mammalian system specifically. The silastic membrane upon which these cells were grown exhibited linear strain behavior over the range of 3.6-14.6% strain, with a Poisson's ratio of approximately 0.5. To mimic murine in utero long bone growth, cell substrates were stretched at an average strain rate of 2.36%/day for 4 days or 1.77%/day for 6 days with an overall membrane strain of 9.5% and 10.6%, respectively. Both control and stretched fibers stained positively for the contractile protein, alpha-actinin, demonstrating muscle fiber development. An effect of stretch on orientation and length of myofibers was observed. At both strain rates, stretched fibers aligned at a smaller angle relative to the direction of stretch and were significantly longer compared to randomly oriented control fibers. There was no effect of duration of stretch on orientation or length, suggesting the cellular responses are independent of strain rate for the range tested. These results demonstrate that, under conditions simulating mammalian long bone growth, cultured myocytes respond to mechanical forces by lengthening and orienting along the direction of stretch.

Microstructural and strain rate effects on plastic deformation in aluminum 2219-T87

NASA Astrophysics Data System (ADS)

Rincon, Carlos D.

A fundamental investigation has been conducted on the effects of microstructure and strain rate on the plastic deformation of theta-prime-strengthened 2219 aluminum. The motivation for this work is based upon a previous study which showed inhomogeneous and locally extreme work hardening in the HAZ regions in VPPA 2219-T87 butt welds. This strongly suggests that the HAZ microstructure plays a major role in the deformation and fracture process in precipitation hardened aluminum alloy 2219. Tensile specimens of the weld joint exhibited more rapid work hardening in the heat-affected-zone (HAZ) at higher strain levels. Microhardness contour maps for these welds illustrated that late stage deformation was concentrated in two crossing bands at about 45sp° to the tensile axis. The width of the deformation bands and the ultimate tensile strength seemed to be dictated by the amount of work hardening in the HAZ. In this study, three different heat treatments were used to produce samples with different particle sizes and particle spacings, but all hardened by copper aluminide precipitates of the thetasp' structure. The heat treatments were categorized as being (A) as-received T87 condition, (B) T87 condition aged at approximately 204sp°C for 3 hours and (C) T87 over-aged at 204sp°C for 7 days. Uniaxial tensile tests consisted of two sets of experiments: (1) three heat treatments (A, B, and C) at two strain rates (0.02 minsp{-1} and 0.2 minsp{-1}) and (2) three heat treatments that were interrupted at select stress-strain levels (0.8% and 2% total strain) during the tensile tests at strain rate equal to 0.02 minsp{-1} at room temperature. Furthermore, a detailed transmission electron microscopy (TEM) study demonstrates the microstructural development during tensile deformation. The Voce equation of strain-hardening provides a slightly better fit to the tensile curves than the Ludwik-Hollomon equation. At higher strains, localized areas showed strain fields around thetasp' platelets had diminished. Lastly, in every treatment, both the yield and tensile strength were slightly higher for the higher strain rate, but only by 0.5 to 2.0 ksi.

Experimental and numerical investigation of strain rate effect on low cycle fatigue behaviour of AA 5754 alloy

NASA Astrophysics Data System (ADS)

Kumar, P.; Singh, A.

2018-04-01

The present study deals with evaluation of low cycle fatigue (LCF) behavior of aluminum alloy 5754 (AA 5754) at different strain rates. This alloy has magnesium (Mg) as main alloying element (Al-Mg alloy) which makes this alloy suitable for Marines and Cryogenics applications. The testing procedure and specimen preparation are guided by ASTM E606 standard. The tests are performed at 0.5% strain amplitude with three different strain rates i.e. 0.5×10-3 sec-1, 1×10-3 sec-1 and 2×10-3 sec-1 thus the frequency of tests vary accordingly. The experimental results show that there is significant decrease in the fatigue life with the increase in strain rate. LCF behavior of AA 5754 is also simulated at different strain rates by finite element method. Chaboche kinematic hardening cyclic plasticity model is used for simulating the hardening behavior of the material. Axisymmetric finite element model is created to reduce the computational cost of the simulation. The material coefficients used for “Chaboche Model” are determined by experimentally obtained stabilized hysteresis loop. The results obtained from finite element simulation are compared with those obtained through LCF experiments.

Increased longitudinal contractility and diastolic function at rest in well-trained amateur Marathon runners: a speckle tracking echocardiography study

PubMed Central

2014-01-01

Background Regular physical activity reduces cardiovascular risk. There is concern that Marathon running might acutely damage the heart. It is unknown to what extent intensive physical endurance activity influences the cardiac mechanics at resting condition. Methods Eighty-four amateur marathon runners (43 women and 41 men) from Berlin-Brandenburg area who had completed at least one marathon previously underwent clinical examination and echocardiography at least 10 days before the Berlin Marathon at rest. Standard transthoracic echocardiography and 2D strain and strain rate analysis were performed. The 2D Strain and strain rate values were compared to previous published data of healthy untrained individuals. Results The average global longitudinal peak systolic strain of the left ventricle was -23 +/- 2% with peak systolic strain rate -1.39 +/- 0.21/s, early diastolic strain rate 2.0 +/- 0.40/s and late diastolic strain rate 1.21 +/- 0.31/s. These values are significantly higher compared to the previous published values of normal age-adjusted individuals. In addition, no age-related decline of longitudinal contractility in well-trained athletes was observed. Conclusions There is increased overall longitudinal myocardial contractility at rest in experienced endurance athletes compared to the published normal values in the literature indicating a preserved and even supra-normal contractility in the athletes. There is no age dependent decline of the longitudinal 2D Strain values. This underlines the beneficial effects of regular physical exercise even in advanced age. PMID:24571726

A constitutive model accounting for strain ageing effects on work-hardening. Application to a C-Mn steel

NASA Astrophysics Data System (ADS)

Ren, Sicong; Mazière, Matthieu; Forest, Samuel; Morgeneyer, Thilo F.; Rousselier, Gilles

2017-12-01

One of the most successful models for describing the Portevin-Le Chatelier effect in engineering applications is the Kubin-Estrin-McCormick model (KEMC). In the present work, the influence of dynamic strain ageing on dynamic recovery due to dislocation annihilation is introduced in order to improve the KEMC model. This modification accounts for additional strain hardening rate due to limited dislocation annihilation by the diffusion of solute atoms and dislocation pinning at low strain rate and/or high temperature. The parameters associated with this novel formulation are identified based on tensile tests for a C-Mn steel at seven temperatures ranging from 20 °C to 350 °C. The validity of the model and the improvement compared to existing models are tested using 2D and 3D finite element simulations of the Portevin-Le Chatelier effect in tension.

Determining a Prony Series for a Viscoelastic Material From Time Varying Strain Data

NASA Technical Reports Server (NTRS)

Tzikang, Chen

2000-01-01

In this study a method of determining the coefficients in a Prony series representation of a viscoelastic modulus from rate dependent data is presented. Load versus time test data for a sequence of different rate loading segments is least-squares fitted to a Prony series hereditary integral model of the material tested. A nonlinear least squares regression algorithm is employed. The measured data includes ramp loading, relaxation, and unloading stress-strain data. The resulting Prony series which captures strain rate loading and unloading effects, produces an excellent fit to the complex loading sequence.

Rheology of water and ammonia-water ices

NASA Technical Reports Server (NTRS)

Goldsby, D. L.; Kohlstedt, D. L.; Durham, W. B.

1993-01-01

Creep experiments on fine-grained water and ammonia-water ices have been performed at one atmosphere and high confining pressure in order to develop constitutive relationships necessary to model tectonic processes and interpret surface features of icy moons of the outer solar system. The present series of experiments explores the effects of temperature, strain rate, grain size, and melt fraction on creep strength. In general, creep strength decreases with increasing temperature, decreasing strain rate, and increasing melt fraction. A transition from dislocation creep to diffusion creep occurs at finer grain sizes, higher temperatures, and lower strain rates.

A Comparison of Deformation Textures and Mechanical Properties Predicted by Different Crystal Plasticity Codes

DTIC Science & Technology

2008-04-01

ensemble (TEX), from which pole figures can be calculated, and the effective Taylor factor (M) for the ensemble. All employ a form of the Voce hardening...strain rate, using a strain-rate sensitivity exponent, m = 1/n. Both hardening and non-hardening conditions were investigated using an empirical Voce

Serrated Flow Behavior of Aisi 316l Austenitic Stainless Steel for Nuclear Reactors

NASA Astrophysics Data System (ADS)

Li, Qingshan; Shen, Yinzhong; Han, Pengcheng

2017-10-01

AISI 316L austenitic stainless steel is a candidate material for Generation IV reactors. In order to investigate the influence of temperature on serrated flow behavior, tensile tests were performed at temperatures ranging from 300 to 700 °C at an initial strain rate of 2×10-4 s-1. Another group of tensile tests were carried out at strain rates ranging from 1×10-4 to 1×10-2 s-1 at 600 °C to examine the influence of strain rates on serrated flow behavior. The steel exhibited serrated flow, suggesting the occurrence of dynamic strain ageing at 450-650°C. No plateau of yield stresses of the steel was observed at an initial strain rate of 2×10-4 s-1. The effective activation energy for serrated flow occurrence was calculated to be about 254.72 kJ/mol-1. Cr, Mn, Ni and Mo solute atoms are expected to be responsible for dynamic strain ageing at high temperatures of 450-650 °C in the steel.

Ductile fracture mechanism of low-temperature In-48Sn alloy joint under high strain rate loading.

PubMed

Kim, Jong-Woong; Jung, Seung-Boo

2012-04-01

The failure behaviors of In-48Sn solder ball joints under various strain rate loadings were investigated with both experimental and finite element modeling study. The bonding force of In-48Sn solder on an Ni plated Cu pad increased with increasing shear speed, mainly due to the high strain-rate sensitivity of the solder alloy. In contrast to the cases of Sn-based Pb-free solder joints, the transition of the fracture mode from a ductile mode to a brittle mode was not observed in this solder joint system due to the soft nature of the In-48Sn alloy. This result is discussed in terms of the relationship between the strain-rate of the solder alloy, the work-hardening effect and the resulting stress concentration at the interfacial regions.

Environmental and strain rate effects on graphite/epoxy composites. Final Report; M.S. Thesis, 1987

NASA Technical Reports Server (NTRS)

Peimandis, Konstantinos

1991-01-01

The hygrothermal characterization of unidirectional graphite/epoxy composites over a range of strain rates was investigated. Special techniques developed for such hygrothermal characterization are also described. The mechanical properties of the composite material were obtained and analyzed by means of a time-temperature-moisture superposition principle. The results show the following: (1) the embedded gage technique was thoroughly examined and found to be appropriate for both hygrothermal expansion and mechanical strain measurements; (2) all transverse properties were found to decrease with increasing temperature and moisture content; and (3) ultimate transverse properties were found to increase with strain rate at low temperatures but follow an opposite trend at high temperatures compared to dry specimens.

Modeling the Hot Ductility of AA6061 Aluminum Alloy After Severe Plastic Deformation

NASA Astrophysics Data System (ADS)

Khamei, A. A.; Dehghani, K.; Mahmudi, R.

2015-05-01

Solutionized AA6061 aluminum alloy was processed by equal-channel angular pressing followed by cold rolling. The hot ductility of the material was studied after severe plastic deformation. The hot tensile tests were carried out in the temperature range of 300-500°C and at the strain rates of 0.0005-0.01 s-1. Depending on the temperature and strain rate, the applied strain level exhibited significant effects on the hot ductility, strain-rate sensitivity, and activation energy. It can be suggested that the possible mechanism dominated the hot deformation during tensile testing is dynamic recovery and dislocation creep. Constitutive equations were developed to model the hot ductility of the severe plastic deformed AA6061 alloy.

Ignition, Burning, and Extinction of a Strained Fuel Strip

NASA Technical Reports Server (NTRS)

Selerland, T.; Karagozian, A. R.

1996-01-01

Flame structure and ignition and extinction processes associated with a strained fuel strip are explored numerically using detailed transport and complex kinetics for a propane-air reaction. Ignition modes are identified that are similar to those predicted by one-step activation energy asymptotics, i.e., modes in which diffusion flames can ignite as independent or dependent interfaces, and modes in which single premixed or partially premixed flames ignite. These ignition modes are found to be dependent on critical combinations of strain rate, fuel strip thickness, and initial reactant temperatures. Extinction in this configuration is seen to occur due to fuel consumption by adjacent flames, although viscosity is seen to have the effect of delaying extinction by reducing the effective strain rate and velocity field experienced by the flames.

Comparative growth rates of cultured marine dinoflagellates in the genus Symbiodinium and the effects of temperature and light.

PubMed

Klueter, Anke; Trapani, Jennifer; Archer, Frederick I; McIlroy, Shelby E; Coffroth, Mary Alice

2017-01-01

Many dinoflagellate microalgae of the genus Symbiodinium form successful symbioses with a large group of metazoans and selected protists. Yet knowledge of growth kinetics of these endosymbionts and their ecological and evolutionary implications is limited. We used a Bayesian biphasic generalized logistic model to estimate key parameters of the growth of five strains of cultured Symbiodinium, S. microadriaticum (cp-type A194; strain 04-503), S. microadriaticum (cp-type A194; strain CassKB8), S. minutum (cp-type B184; strain Mf 1.05b.01.SCI.01), S. psygmophilum (cp-type B224; strain Mf 11.05b.01) and S. trenchii (cp-type D206; strain Mf 2.2b), grown in four different combinations of temperature and light. Growth kinetics varied among Symbiodinium strains and across treatments. Biphasic growth was especially evident for S. minutum and S. psygmophilum across all treatments. Monophasic growth was more common when final asymptotic densities were relatively low (~ 200 million cells ml-1). All species tended to grow faster and / or reached a higher asymptote at 26°C than at 18°C. The fastest growth was exhibited by S. minutum, with an approximate four-fold increase in estimated cell density after 60 days. The strongest effect of light was seen in S. trenchii, in which increasing light levels resulted in a decrease in initial growth rate, and an increase in asymptotic density, time when growth rate was at its maximum, final growth rate, and maximum growth rate. Results suggest that Symbiodinium species have different photokinetic and thermal optima, which may affect their growth-related nutritional physiology and allow them to modify their response to environmental changes.

Experimental and numerical investigation of dual phase steels formability during laser-assisted hole-flanging

NASA Astrophysics Data System (ADS)

Motaman, S. A. H.; Komerla, K.; Storms, T.; Prahl, U.; Brecher, C.; Bleck, W.

2018-05-01

Today, in the automotive industry dual phase (DP) steels are extensively used in the production of various structural parts due to their superior mechanical properties. Hole-flanging of such steels due to simultaneous bending and stretching of sheet metal, is complex and associated with some issues such as strain and strain rate localization, development of micro-cracks, inhomogeneous sheet thinning, etc. In this study an attempt is made to improve the formability of DP sheets, by localized Laser heating. The Laser beam was oscillated in circular pattern rapidly around the pre-hole, blanked prior to the flanging process. In order to investigate formability of DP steel (DP1000), several uniaxial tensile tests were conducted from quasi to intermediate strain rates at different temperatures in warm regime. Additionally, experimentally acquired temperature and strain rate-dependent flow curves were fed into thermomechanical finite element (FE) simulation of the hole-flanging process using the commercial FE software ABAQUS/Explicit. Several FE simulations were performed in order to evaluate the effect of blank's initial temperature and punch speed on deformation localization, stress evolution and temperature distribution in DP1000 sheets during warm hole-flanging process. The experimental and numerical analyses revealed that prescribing a distribution of initial temperature between 300 to 400 °C to the blank and setting a punch speed that accommodates strain rate range of 1 to 5 s-1 in the blank, provides the highest strain hardening capacity in the considered rate and temperature regimes for DP1000. This is in fact largely due to the dynamic strain aging (DSA) effect which occurs due to pinning of mobile dislocations by interstitial solute atoms, particularly at elevated temperatures.

Experimental study of vorticity-strain rate interaction in turbulent partially-premixed jet flames using tomographic particle image velocimetry

DOE PAGES

Coriton, Bruno; Frank, Jonathan H.

2016-02-16

In turbulent flows, the interaction between vorticity, ω, and strain rate, s, is considered a primary mechanism for the transfer of energy from large to small scales through vortex stretching. The ω-s coupling in turbulent jet flames is investigated using tomographic particle image velocimetry (TPIV). TPIV provides a direct measurement of the three-dimensional velocity field from which ω and s are determined. The effects of combustion and mean shear on the ω-s interaction are investigated in turbulent partially premixed methane/air jet flames with high and low probabilities of localized extinction as well as in a non-reacting isothermal air jet withmore » Reynolds number of approximately 13,000. Results show that combustion causes structures of high vorticity and strain rate to agglomerate in highly correlated, elongated layers that span the height of the probe volume. In the non-reacting jet, these structures have a more varied morphology, greater fragmentation, and are not as well correlated. The enhanced spatiotemporal correlation of vorticity and strain rate in the stable flame results in stronger ω-s interaction characterized by increased enstrophy and strain-rate production rates via vortex stretching and straining, respectively. The probability of preferential local alignment between ω and the eigenvector of the intermediate principal strain rate, s 2, which is intrinsic to the ω-s coupling in turbulent flows, is larger in the flames and increases with the flame stability. The larger mean shear in the flame imposes a preferential orientation of ω and s 2 tangential to the shear layer. The extensive and compressive principal strain rates, s 1 and s 3, respectively, are preferentially oriented at approximately 45° with respect to the jet axis. As a result, the production rates of strain and vorticity tend to be dominated by instances in which ω is parallel to the s 1¯-s 2¯ plane and orthogonal to s 3¯.« less

Fatigue History and in-situ Loading Studies of the overload Effect Using High Resolution X-ray Strain Profiling

DOE Office of Scientific and Technical Information (OSTI.GOV)

Croft,M.; Jisrawi, N.; Zhong, Z.

High-energy synchrotron X-ray diffraction experiments are used to perform local crack plane strain profiling of 4140 steel compact tension specimens fatigued at constant amplitude, subjected to a single overload cycle, then fatigued some more at constant amplitude. X-ray strain profiling results on a series of samples employing in-situ load cycling are correlated with the crack growth rate (da/dN) providing insight into the da/dN retardation known as the 'overload effect'. Immediately after the overload, the strain under maximum load is greatly reduced but the range of strain, between zero and maximum load, remains unchanged compared to the pre-overload values. At themore » point of maximum retardation, it is the strain range that is greatly reduced while the maximum-load strain has begun to recover to the pre-overload value. For a sample that has recovered to approximately half of the original da/dN value following the overload, the strain at maximum load is fully recovered while the strain range, though partially recovered, is still substantially reduced. The dominance of the strain range in the overload effect is clearly indicated. Subject to some assumptions, strong quantitative support for a crack growth rate driving force of the suggested form [(K{sub max}){sup -p}({Delta}K){sup p}]{sup {gamma}} is found. A dramatic nonlinear load dependence in the spatial distribution of the strain at maximum retardation is also demonstrated: at low load the response is dominantly at the overload position; whereas at high loads it is dominantly at the crack tip position. This transfer of load response away from the crack tip to the overload position appears fundamental to the overload effect for high R-ratio fatigue as studied here.« less

Physically-based strength model of tantalum incorporating effects of temperature, strain rate and pressure

DOE PAGES

Lim, Hojun; Battaile, Corbett C.; Brown, Justin L.; ...

2016-06-14

In this work, we develop a tantalum strength model that incorporates e ects of temperature, strain rate and pressure. Dislocation kink-pair theory is used to incorporate temperature and strain rate e ects while the pressure dependent yield is obtained through the pressure dependent shear modulus. Material constants used in the model are parameterized from tantalum single crystal tests and polycrystalline ramp compression experiments. It is shown that the proposed strength model agrees well with the temperature and strain rate dependent yield obtained from polycrystalline tantalum experiments. Furthermore, the model accurately reproduces the pressure dependent yield stresses up to 250 GPa.more » The proposed strength model is then used to conduct simulations of a Taylor cylinder impact test and validated with experiments. This approach provides a physically-based multi-scale strength model that is able to predict the plastic deformation of polycrystalline tantalum through a wide range of temperature, strain and pressure regimes.« less

Experiments and Model for Serration Statistics in Low-Entropy, Medium-Entropy, and High-Entropy Alloys

DOE PAGES

Carroll, Robert; Lee, Chi; Tsai, Che-Wei; ...

2015-11-23

In this study, high-entropy alloys (HEAs) are new alloys that contain five or more elements in roughly-equal proportion. We present new experiments and theory on the deformation behavior of HEAs under slow stretching (straining), and observe differences, compared to conventional alloys with fewer elements. For a specific range of temperatures and strain-rates, HEAs deform in a jerky way, with sudden slips that make it difficult to precisely control the deformation. An analytic model explains these slips as avalanches of slipping weak spots and predicts the observed slip statistics, stress-strain curves, and their dependence on temperature, strain-rate, and material composition. Themore » ratio of the weak spots’ healing rate to the strain-rate is the main tuning parameter, reminiscent of the Portevin- LeChatellier effect and time-temperature superposition in polymers. Our model predictions agree with the experimental results. The proposed widely-applicable deformation mechanism is useful for deformation control and alloy design.« less

Effect of a personal ambient ventilation system on physiological strain during heat stress wearing a ballistic vest.

PubMed

Hadid, A; Yanovich, R; Erlich, T; Khomenok, G; Moran, D S

2008-09-01

The present study was conducted in order to evaluate whether physiological strain is alleviated by a new personal cooling system (CS) consisting of a layered vest and integrated blower that generate a flow of air. Twelve male volunteers were exposed to climatic conditions of 40 degrees C, 40%RH (40/40), and 35 degrees C, 60%RH (35/60) during a 115 min exercise routine, followed by 70 min resting recovery, while wearing a battle dress uniform (BDU) and a ballistic vest, with (COOL) or without (NOCOOL) CS. The CS was able to attenuate the physiological strain levels during exercise, when compared to identical exposures without the CS. Temperature elevation, (DeltaT (re)) after 100 min of exercise, was lower by 0.26 +/- 0.20 and 0.34 +/- 0.21 degrees C in 40/40 and 35/60, respectively, (p < 0.05). Mean skin temperature (T(sk)) was lower by 0.9 +/- 0.4 and 0.6 +/- 0.5 degrees C for 40/40 and 35/60, respectively. Heart rate (HR) was not significantly different for COOL versus NOCOOL for 40/40. At 35/60, HR was lower by 10 beats per min (bpm) (p < 0.05). Physiological strain index (PSI) was 9 and 21% lower for the 40/40 and 35/60, respectively, for COOL versus NOCOOL (p < 0.05). Heat storage (S) rates were 19 and 24% lower and sweat rates were 21 and 25% lower for the 40/40 and 35/60, respectively, for COOL versus NOCOOL (p < 0.05). However, the CS was not effective in alleviating physiological strain during resting recovery with no difference in T (re) cooling rate, S, or HR drop rate between groups over resting recovery periods. The CS tested in this study was found to be an effective tool for lowering physiological strain while exercising but not during resting recovery. Therefore, the CS should be further developed in order to achieve greater attenuation of the thermal strain during exercise and improve effectiveness during rest. Overall, it has the potential to be useful for both military and sports personnel.

Statistics of strain rates and surface density function in a flame-resolved high-fidelity simulation of a turbulent premixed bluff body burner

NASA Astrophysics Data System (ADS)

Sandeep, Anurag; Proch, Fabian; Kempf, Andreas M.; Chakraborty, Nilanjan

2018-06-01

The statistical behavior of the surface density function (SDF, the magnitude of the reaction progress variable gradient) and the strain rates, which govern the evolution of the SDF, have been analyzed using a three-dimensional flame-resolved simulation database of a turbulent lean premixed methane-air flame in a bluff-body configuration. It has been found that the turbulence intensity increases with the distance from the burner, changing the flame curvature distribution and increasing the probability of the negative curvature in the downstream direction. The curvature dependences of dilatation rate ∇ṡu → and displacement speed Sd give rise to variations of these quantities in the axial direction. These variations affect the nature of the alignment between the progress variable gradient and the local principal strain rates, which in turn affects the mean flame normal strain rate, which assumes positive values close to the burner but increasingly becomes negative as the effect of turbulence increases with the axial distance from the burner exit. The axial distance dependences of the curvature and displacement speed also induce a considerable variation in the mean value of the curvature stretch. The axial distance dependences of the dilatation rate and flame normal strain rate govern the behavior of the flame tangential strain rate, and its mean value increases in the downstream direction. The current analysis indicates that the statistical behaviors of different strain rates and displacement speed and their curvature dependences need to be included in the modeling of flame surface density and scalar dissipation rate in order to accurately capture their local behaviors.

A Continuum Model for the Effect of Dynamic Recrystallization on the Stress⁻Strain Response.

PubMed

Kooiker, H; Perdahcıoğlu, E S; van den Boogaard, A H

2018-05-22

Austenitic Stainless Steels and High-Strength Low-Alloy (HSLA) steels show significant dynamic recovery and dynamic recrystallization (DRX) during hot forming. In order to design optimal and safe hot-formed products, a good understanding and constitutive description of the material behavior is vital. A new continuum model is presented and validated on a wide range of deformation conditions including high strain rate deformation. The model is presented in rate form to allow for the prediction of material behavior in transient process conditions. The proposed model is capable of accurately describing the stress⁻strain behavior of AISI 316LN in hot forming conditions, also the high strain rate DRX-induced softening observed during hot torsion of HSLA is accurately predicted. It is shown that the increase in recrystallization rate at high strain rates observed in experiments can be captured by including the elastic energy due to the dynamic stress in the driving pressure for recrystallization. Furthermore, the predicted resulting grain sizes follow the power-law dependence with steady state stress that is often reported in literature and the evolution during hot deformation shows the expected trend.

Comparison of Quantitative Wall Motion Analysis and Strain For Detection Of Coronary Stenosis With Three-Dimensional Dobutamine Stress Echocardiography

PubMed Central

Parker, Katherine M.; Clark, Alexander P.; Goodman, Norman C.; Glover, David K.; Holmes, Jeffrey W.

2015-01-01

Background Quantitative analysis of wall motion from three-dimensional (3D) dobutamine stress echocardiography (DSE) could provide additional diagnostic information not available from qualitative analysis. In this study we compare the effectiveness of 3D fractional shortening (3DFS), a measure of wall motion computed from 3D echocardiography (3DE), to strain and strain rate measured with sonomicrometry for detecting critical stenoses during DSE. Methods Eleven open-chest dogs underwent DSE both with and without a critical stenosis. 3DFS was measured from 3DE images acquired at peak stress. 3DFS was normalized by subtracting average 3DFS during control peak stress (Δ3DFS). Strains in the perfusion defect (PD) were measured from sonomicrometry, and PD size and location were measured with microspheres. Results A Δ3DFS abnormality indicated the presence of a critical stenosis with high sensitivity and specificity (88% and 100%, respectively), and Δ3DFS abnormality size correlated with PD size (R2=0.54). The sensitivity and specificity for Δ3DFS was similar to that for area strain (88%, 100%) and circumferential strain and strain rate (88%, 92% and 88%, 86%, respectively), while longitudinal strain and strain rate were less specific. Δ3DFS correlated significantly with both coronary flow reserve (R2=0.71) and PD size (R2=0.97), while area strain correlated with PD size only (R2=0.67), and other measures were not significantly correlated with flow reserve or PD size. Conclusion Quantitative wall motion analysis using Δ3DFS is effective for detecting critical stenoses during DSE, performing similarly to 3D strain, and provides potentially useful information on the size and location of a perfusion defect. PMID:24815588

Chromosomal Effects on Mutability in the P-M System of Hybrid Dysgenesis in DROSOPHILA MELANOGASTER

PubMed Central

Simmons, Michael J.; Raymond, John D.; Laverty, Todd R.; Doll, Rhonda F.; Raymond, Nancy C.; Kocur, Gordon J.; Drier, Eric A.

1985-01-01

Two manifestations of hybrid dysgenesis were studied in flies with chromosomes derived from two different P strains. In one set of experiments, the occurrence of recessive X-linked lethal mutations in the germ cells of dysgenic males was monitored. In the other, the behavior of an X-linked P-element insertion mutation, sn w, was studied in dysgenic males and also in dysgenic females. The chromosomes of one P strain were more proficient at causing dysgenesis in both sets of experiments. However, there was variation among the chromosomes of each strain in regard to the ability to induce lethals or to destabilize snw. The X chromosome, especially when it came from the stronger P strain, had a pronounced effect on both measures of dysgenesis, but in combination with the major autosomes, these effects were reduced. For the stronger P strain, the autosomes by themselves contributed significantly to the production of X-linked lethals and also had large effects on the behavior of snw, but they did not act additively on these two characters. For this strain, the effects of the autosomes on the X-linked lethal mutation rate suggest that only 1/100 P element transpositions causes a recessive lethal mutation. For the weaker P strain, the autosomes had only slight effects on the behavior of snw and appeared to have negligible effects on the X-linked lethal mutation rate. Combinations of chromosomes from either the strong or the weak P strain affected both aspects of dysgenesis in a nonadditive fashion, suggesting that the P elements on these chromosomes competed with each other for transposase, the P-encoded function that triggers P element activity. Age and sex also influenced the ability of chromosomes and combinations of chromosomes to cause dysgenesis. PMID:3934034

Toughening mechanism in elastometer-modified epoxy resins: Part 1

NASA Technical Reports Server (NTRS)

Yee, A. F.; Pearson, R. A.

1983-01-01

Several plaques of Epon 828, cured with piperidine, modified with hycar(r) CTBN 1300X8, Hycar(R) CTBN 1300X13, and Hycar(R) CTBN 1300x15, and in some cases modified with biphenol A (BPA), yielded properly toughened epoxies with rubber particle diameters ranging from 0.1 to 10 microns. Fracture toughness experiments indicate that toughness was more a function of rubber content than the rubber particle size. Tensile volumetric behavior of the near resin exhibits two regions: an initial region where the increase in volume strain was due to the Poisson's effect, and a second region where a slower rate of increase in volume strain was due to shear deformation. Tensile volumetric deformation of an elastomer-modified epoxy exhibits the same type of behavior to that of the neat resin at low rates ( 3.2x0.01 sec(-1)). But at very high strain rates, which correspond more closely to the strain rates at the crack tip, there exists an increase in volume strain beyond the Poisson's effect. TEM, SEM and OM studies indicate that the rubber particles had voided. When a thin section from the deformed region is viewed under crossed-polarized light, shear bands are seen connecting voided rubber particles. From this information cavitation and enhanced shear band formation is proposed as the toughening mechanism.

Effects of a temperature-dependent rheology on large scale continental extension

NASA Technical Reports Server (NTRS)

Sonder, Leslie J.; England, Philip C.

1988-01-01

The effects of a temperature-dependent rheology on large-scale continental extension are investigated using a thin viscous sheet model. A vertically-averaged rheology is used that is consistent with laboratory experiments on power-law creep of olivine and that depends exponentially on temperature. Results of the calculations depend principally on two parameters: the Peclet number, which describes the relative rates of advection and diffusion of heat, and a dimensionless activation energy, which controls the temperature dependence of the rheology. At short times following the beginning of extension, deformation occurs with negligible change in temperature, so that only small changes in lithospheric strength occur due to attenuation of the lithosphere. However, after a certain critical time interval, thermal diffusion lowers temperatures in the lithosphere, strongly increasing lithospheric strength and slowing the rate of extension. This critical time depends principally on the Peclet number and is short compared with the thermal time constant of the lithosphere. The strength changes cause the locus of high extensional strain rates to shift with time from regions of high strain to regions of low strain. Results of the calculations are compared with observations from the Aegean, where maximum extensional strains are found in the south, near Crete, but maximum present-day strain rates are largest about 300 km further north.

Modeling the Effects of Cu Content and Deformation Variables on the High-Temperature Flow Behavior of Dilute Al-Fe-Si Alloys Using an Artificial Neural Network.

PubMed

Shakiba, Mohammad; Parson, Nick; Chen, X-Grant

2016-06-30

The hot deformation behavior of Al-0.12Fe-0.1Si alloys with varied amounts of Cu (0.002-0.31 wt %) was investigated by uniaxial compression tests conducted at different temperatures (400 °C-550 °C) and strain rates (0.01-10 s -1 ). The results demonstrated that flow stress decreased with increasing deformation temperature and decreasing strain rate, while flow stress increased with increasing Cu content for all deformation conditions studied due to the solute drag effect. Based on the experimental data, an artificial neural network (ANN) model was developed to study the relationship between chemical composition, deformation variables and high-temperature flow behavior. A three-layer feed-forward back-propagation artificial neural network with 20 neurons in a hidden layer was established in this study. The input parameters were Cu content, temperature, strain rate and strain, while the flow stress was the output. The performance of the proposed model was evaluated using the K-fold cross-validation method. The results showed excellent generalization capability of the developed model. Sensitivity analysis indicated that the strain rate is the most important parameter, while the Cu content exhibited a modest but significant influence on the flow stress.

Modeling the Effects of Cu Content and Deformation Variables on the High-Temperature Flow Behavior of Dilute Al-Fe-Si Alloys Using an Artificial Neural Network

PubMed Central

Shakiba, Mohammad; Parson, Nick; Chen, X.-Grant

2016-01-01

The hot deformation behavior of Al-0.12Fe-0.1Si alloys with varied amounts of Cu (0.002–0.31 wt %) was investigated by uniaxial compression tests conducted at different temperatures (400 °C–550 °C) and strain rates (0.01–10 s−1). The results demonstrated that flow stress decreased with increasing deformation temperature and decreasing strain rate, while flow stress increased with increasing Cu content for all deformation conditions studied due to the solute drag effect. Based on the experimental data, an artificial neural network (ANN) model was developed to study the relationship between chemical composition, deformation variables and high-temperature flow behavior. A three-layer feed-forward back-propagation artificial neural network with 20 neurons in a hidden layer was established in this study. The input parameters were Cu content, temperature, strain rate and strain, while the flow stress was the output. The performance of the proposed model was evaluated using the K-fold cross-validation method. The results showed excellent generalization capability of the developed model. Sensitivity analysis indicated that the strain rate is the most important parameter, while the Cu content exhibited a modest but significant influence on the flow stress. PMID:28773658

Effects of NaCl, pH, and Potential on the Static Creep Behavior of AA1100

NASA Astrophysics Data System (ADS)

Wan, Quanhe; Quesnel, David J.

2013-03-01

The creep rates of AA1100 are measured during exposure to a variety of aggressive environments. NaCl solutions of various concentrations have no influence on the steady-state creep behavior, producing creep rates comparable to those measured in lab air at room temperature. However, after an initial incubation period of steady strain rate, a dramatic increase of strain rate is observed on exposure to HCl solutions and NaOH solutions, as well as during cathodic polarization of specimens in NaCl solutions. Creep strain produces a continuous deformation and elongation of the sample surface that is comparable to slow strain rates at crack tips thought to control the kinetics of crack growth during stress corrosion cracking (SCC). In this experiment, we separate the strain and surface deformation from the complex geometry of the crack tip to better understand the processes at work. Based on this concept, two possible explanations for the environmental influences on creep strain rates are discussed relating to the anodic dissolution of the free surface and hydrogen influences on deformation mechanisms. Consistencies of pH dependence between corrosion creep and SCC at low pH prove a creep-involved SCC mechanism, while the discrepancies between corrosion creep behavior and previous SCC results at high pH indicate a rate-limit step change in the crack propagation of the SCC process.

On massive carbide precipitation during high temperature low cycle fatigue in alloy 800H

NASA Technical Reports Server (NTRS)

Sankararao, K. Bhanu; Schuster, H.; Halford, G. R.

1994-01-01

The effect of strain rate on massive precipitation and the mechanism for the occurrence of massive precipitation of M23C6 in alloy 800H is investigated during elevated temperature low cycle fatigue testing. It was observed that large M23C6 platelets were in the vicinity of grain and incoherent twin boundaries. The strain controlled fatigue testing at higher strain rates that promoted cyclic hardening enabled massive precipitation to occur more easily.

Prediction of Ductile Fracture Behaviors for 42CrMo Steel at Elevated Temperatures

NASA Astrophysics Data System (ADS)

Lin, Y. C.; Liu, Yan-Xing; Liu, Ge; Chen, Ming-Song; Huang, Yuan-Chun

2015-01-01

The ductile fracture behaviors of 42CrMo steel are studied by hot tensile tests with the deformation temperature range of 1123-1373 K and strain rate range of 0.0001-0.1 s-1. Effects of deformation temperature and strain rate on the flow stress and fracture strain of the studied steel are discussed in detail. Based on the experimental results, a ductile damage model is established to describe the combined effects of deformation temperature and strain rate on the ductile fracture behaviors of 42CrMo steel. It is found that the flow stress first increases to a peak value and then decreases, showing an obvious dynamic softening. This is mainly attributed to the dynamic recrystallization and material intrinsic damage during the hot tensile deformation. The established damage model is verified by hot forging experiments and finite element simulations. Comparisons between the predicted and experimental results indicate that the established ductile damage model is capable of predicting the fracture behaviors of 42CrMo steel during hot forging.

A physical model for strain accumulation in the San Francisco Bay Region

USGS Publications Warehouse

Pollitz, F.F.; Nyst, M.

2005-01-01

Strain accumulation in tectonically active regions is generally a superposition of the effects of background tectonic loading, steady-state dislocation processes, such as creep, and transient deformation. In the San Francisco Bay region (SFBR), the most uncertain of these processes is transient deformation, which arises primarily in association with large earthquakes. As such, it depends upon the history of faulting and the rheology of the crust and mantle, which together determine the pattern of longer term (decade-scale) post-seismic response to earthquakes. We utilize a set of 102 GPS velocity vectors in the SFBR in order to characterize the strain rate field and construct a physical model of its present deformation. We first perform an inversion for the continuous velocity gradient field from the discrete GPS velocity field, from which both tensor strain rate and rotation rate may be extracted. The present strain rate pattern is well described as a nearly uniform shear strain rate oriented approximately N34??W (140 nanostrain yr-1) plus a N56??E uniaxial compression rate averaging 20 nanostrain yr-1 across the shear zone. We fit the velocity and strain rate fields to a model of time-dependent deformation within a 135-kin-wide, arcuate shear zone bounded by strong Pacific Plate and Sierra Nevada block lithosphere to the SW and NE, respectively. Driving forces are purely lateral, consisting of shear zone deformation imposed by the relative motions between the thick Pacific Plate and Sierra Nevada block lithospheres. Assuming a depth-dependent viscoelastic structure within the shear zone, we account for the effects of steady creep on faults and viscoelastic relaxation following the 1906 San Francisco and 1989 Loma Prieta earthquakes, subject to constant velocity boundary conditions on the edges of the shear zone. Fault creep is realized by evaluating dislocations on the creeping portions of faults in the fluid limit of the viscoelastic model. A priori plate-boundary(PB)-parallel motion is set to 38 mm yr -1. A grid search based on fitting the observed strain rate pattern yields a mantle viscosity of 1.2 ?? 1019 Pa s and a PB-perpendicular convergence rate of ???3 mm yr-1. Most of this convergence appears to be uniformly distributed in the Pacific-Sierra Nevada plate boundary zone. ?? 2005 RAS.

Ratcheting fatigue behavior of Zircaloy-2 at room temperature

NASA Astrophysics Data System (ADS)

Rajpurohit, R. S.; Sudhakar Rao, G.; Chattopadhyay, K.; Santhi Srinivas, N. C.; Singh, Vakil

2016-08-01

Nuclear core components of zirconium alloys experience asymmetric stress or strain cycling during service which leads to plastic strain accumulation and drastic reduction in fatigue life as well as dimensional instability of the component. Variables like loading rate, mean stress, and stress amplitude affect the influence of asymmetric loading. In the present investigation asymmetric stress controlled fatigue tests were conducted with mean stress from 80 to 150 MPa, stress amplitude from 270 to 340 MPa and stress rate from 30 to 750 MPa/s to study the process of plastic strain accumulation and its effect on fatigue life of Zircaloy-2 at room temperature. It was observed that with increase in mean stress and stress amplitude accumulation of ratcheting strain was increased and fatigue life was reduced. However, increase in stress rate led to improvement in fatigue life due to less accumulation of ratcheting strain.

Investigation of the Microstructure Evolution in a Fe-17Mn-1.5Al-0.3C Steel via In Situ Synchrotron X-ray Diffraction during a Tensile Test

PubMed Central

Song, Wenwen; Bleck, Wolfgang

2017-01-01

The quantitative characterization of the microstructure evolution in high-Mn steel during deformation is of great importance to understanding its strain-hardening behavior. In the current study, in situ high-energy synchrotron X-ray diffraction was employed to characterize the microstructure evolution in a Fe-17Mn-1.5Al-0.3C steel during a tensile test. The microstructure at different engineering strain levels—in terms of ε-martensite and α’-martensite volume fractions, the stacking fault probability, and the twin fault probability—was analyzed by the Rietveld refinement method. The Fe-17Mn-1.5Al-0.3C steel exhibits a high ultimate tensile strength with a superior uniform elongation and a high strain-hardening rate. The remaining high strain-hardening rate at the strain level about 0.025 to 0.35 results from ε-martensite dominant transformation-induced-plasticity (TRIP) effect. The increase in the strain-hardening rate at the strain level around 0.35 to 0.43 is attributed to the synergetic α’-martensite dominant TRIP and twinning-induced-plasticity (TWIP) effects. An evaluation of the stacking fault energy (SFE) of the Fe-17Mn-1.5Al-0.3C steel by the synchrotron measurements shows good agreement with the thermodynamic calculation of the SFE. PMID:28946692

Investigation of the Microstructure Evolution in a Fe-17Mn-1.5Al-0.3C Steel via In Situ Synchrotron X-ray Diffraction during a Tensile Test.

PubMed

Ma, Yan; Song, Wenwen; Bleck, Wolfgang

2017-09-25

The quantitative characterization of the microstructure evolution in high-Mn steel during deformation is of great importance to understanding its strain-hardening behavior. In the current study, in situ high-energy synchrotron X-ray diffraction was employed to characterize the microstructure evolution in a Fe-17Mn-1.5Al-0.3C steel during a tensile test. The microstructure at different engineering strain levels-in terms of ε-martensite and α'-martensite volume fractions, the stacking fault probability, and the twin fault probability-was analyzed by the Rietveld refinement method. The Fe-17Mn-1.5Al-0.3C steel exhibits a high ultimate tensile strength with a superior uniform elongation and a high strain-hardening rate. The remaining high strain-hardening rate at the strain level about 0.025 to 0.35 results from ε-martensite dominant transformation-induced-plasticity (TRIP) effect. The increase in the strain-hardening rate at the strain level around 0.35 to 0.43 is attributed to the synergetic α'-martensite dominant TRIP and twinning-induced-plasticity (TWIP) effects. An evaluation of the stacking fault energy (SFE) of the Fe-17Mn-1.5Al-0.3C steel by the synchrotron measurements shows good agreement with the thermodynamic calculation of the SFE.

Phenomenological Constitutive Modeling of High-Temperature Flow Behavior Incorporating Individual and Coupled Effects of Processing Parameters in Super-austenitic Stainless Steel

NASA Astrophysics Data System (ADS)

Roy, Swagata; Biswas, Srija; Babu, K. Arun; Mandal, Sumantra

2018-05-01

A novel constitutive model has been developed for predicting flow responses of super-austenitic stainless steel over a wide range of strains (0.05-0.6), temperatures (1173-1423 K) and strain rates (0.001-1 s-1). Further, the predictability of this new model has been compared with the existing Johnson-Cook (JC) and modified Zerilli-Armstrong (M-ZA) model. The JC model is not befitted for flow prediction as it is found to be exhibiting very high ( 36%) average absolute error (δ) and low ( 0.92) correlation coefficient (R). On the contrary, the M-ZA model has demonstrated relatively lower δ ( 13%) and higher R ( 0.96) for flow prediction. The incorporation of couplings of processing parameters in M-ZA model has led to exhibit better prediction than JC model. However, the flow analyses of the studied alloy have revealed the additional synergistic influences of strain and strain rate as well as strain, temperature, and strain rate apart from those considered in M-ZA model. Hence, the new phenomenological model has been formulated incorporating all the individual and synergistic effects of processing parameters and a `strain-shifting' parameter. The proposed model predicted the flow behavior of the alloy with much better correlation and generalization than M-ZA model as substantiated by its lower δ ( 7.9%) and higher R ( 0.99) of prediction.

The newly described heterotrophic dinoflagellate Gyrodinium moestrupii, an effective protistan grazer of toxic dinoflagellates.

PubMed

Yoo, Yeong Du; Yoon, Eun Young; Jeong, Hae Jin; Lee, Kyung Ha; Hwang, Yeong Jong; Seong, Kyeong Ah; Kim, Jae Seong; Park, Jae Yeon

2013-01-01

Few protistan grazers feed on toxic dinoflagellates, and low grazing pressure on toxic dinoflagellates allows these dinoflagellates to form red-tide patches. We explored the feeding ecology of the newly described heterotrophic dinoflagellate Gyrodinium moestrupii when it fed on toxic strains of Alexandrium minutum, Alexandrium tamarense, and Karenia brevis and on nontoxic strains of A. tamarense, Prorocentrum minimum, and Scrippsiella trochoidea. Specific growth rates of G. moestrupii feeding on each of these dinoflagellates either increased continuously or became saturated with increasing mean prey concentration. The maximum specific growth rate of G. moestrupii feeding on toxic A. minutum (1.60/d) was higher than that when feeding on nontoxic S. trochoidea (1.50/d) or P. minimum (1.07/d). In addition, the maximum growth rate of G. moestrupii feeding on the toxic strain of A. tamarense (0.68/d) was similar to that when feeding on the nontoxic strain of A. tamarense (0.71/d). Furthermore, the maximum ingestion rate of G. moestrupii on A. minutum (2.6 ng C/grazer/d) was comparable to that of S. trochoidea (3.0 ng C/grazer/d). Additionally, the maximum ingestion rate of G. moestrupii on the toxic strain of A. tamarense (2.1 ng C/grazer/d) was higher than that when feeding on the nontoxic strain of A. tamarense (1.3 ng C/grazer/d). Thus, feeding by G. moestrupii is not suppressed by toxic dinoflagellate prey, suggesting that it is an effective protistan grazer of toxic dinoflagellates. © 2012 The Author(s) Journal of Eukaryotic Microbiology © 2012 International Society of Protistologists.

Effect of borides on hot deformation behavior and microstructure evolution of powder metallurgy high borated stainless steel

DOE Office of Scientific and Technical Information (OSTI.GOV)

Zhou, Xuan

To investigate borides effect on the hot deformation behavior and microstructure evolution of powder metallurgy high borated stainless steel, hot compression tests at the temperatures of 950– 1150 °C and the strain rates of 0.01– 10 s{sup −1} were performed. Flow stress curves indicated that borides increased the material's stress level at low temperature but the strength was sacrificed at temperatures above 1100 °C. A hyperbolic-sine equation was used to characterize the dependence of the flow stress on the deformation temperature and strain rate. The hot deformation activation energy and stress exponent were determined to be 355 kJ/mol and 3.2,more » respectively. The main factors leading to activation energy and stress exponent of studied steel lower than those of commercial 304 stainless steel were discussed. Processing maps at the strains of 0.1, 0.3, 0.5, and 0.7 showed that flow instability mainly concentrated at 950– 1150 °C and strain rate higher than 0.6 s{sup −1}. Results of microstructure illustrated that dynamic recrystallization was fully completed at both high temperature-low strain rate and low temperature-high strain rate. In the instability region cracks were generated in addition to cavities. Interestingly, borides maintained a preferential orientation resulting from particle rotation during compression. - Highlights: •The decrement of activation energy was affected by boride and boron solution. •The decrease of stress exponent was influenced by composition and Cottrell atmosphere. •Boride represented a preferential orientation caused by particle rotation.« less

Strain-Rate Dependence of Deformation-Twinning in Tantalum

NASA Astrophysics Data System (ADS)

Abeywardhana, Jayalath; Germann, Tim; Ravelo, Ramon

2017-06-01

Large-Scale molecular dynamics (MD) simulations are used to model quasi-isentropic compression and expansion (QIC) in tantalum crystals varying the rate of deformation between the range 108 -1012s-1 and compressive pressures up to 100 GPa. The atomic interactions were modeled employing an embedded-atom method (EAM) potential of Ta. Isentropic expansion was done employing samples initially compressed to pressures of 60 and 100 GPa followed by uniaxial and quasi-isentropically expansion to zero pressure. The effect of initial dislocation density on twinning was also examined by varying the initial defect density of the Ta samples (1010 -1012cm-2). At these high-strain rates, a threshold in strain-rate on deformation twining is observed. Under expansion or compression, deformation twinning increases with strain rate for strain-rates >109s-1 . Below this value, small fraction of twins nucleates but anneal out with time. Samples with lower fraction of twins equilibrate to defect states containing higher screw dislocation densities from those with initially higher twinning fractions. This work was supported by the Department of Energy under contract DE-AC52-06NA25396 and by the Air Force Office of Scientific Research under AFOSR Award No. FA9550-12-1-0476.

Kinetics of the Removal of Iron Pyrite from Coal by Microbial Catalysis

PubMed Central

Hoffmann, Michael R.; Faust, Bruce C.; Panda, Fern A.; Koo, Hong H.; Tsuchiya, Henry M.

1981-01-01

Different strains of Thiobacillus ferrooxidans and Thiobacillus thiooxidans were used to catalyze the oxidative dissolution of iron pyrite, FeS2, in nine different coal samples. Kinetic variables and parametric factors that were determined to have a pronounced effect on the rate and extent of oxidative dissolution at a fixed Po2 were: the bacterial strain, the nitrogen/phosphorus molar ratio, the partial pressure of CO2, the coal source, and the total reactive surface area of FeS2. The overall rate of leaching, which exhibited a first-order dependence on the total surface area of FeS2, was analyzed mathematically in terms of the sum of a biochemical rate, ν1, and a chemical rate, ν2. Results of this study show that bacterial desulfurization (90 to 98%) of coal samples which are relatively high in pyritic sulfur can be achieved within a time-frame of 8 to 12 days when pulp densities are ≤20% and particle sizes are ≤74 μm. The most effective strains of T. ferrooxidans were those that were isolated from natural systems, and T. ferrooxidans ATCC 19859 was the most effective pure strain. The most effective nutrient media contained relatively low phosphate concentrations, with an optimal N/P molar ratio of 90:1. These results suggest that minimal nutrient additions may be required for a commercial desulfurization process. PMID:16345826

A new radial strain and strain rate estimation method using autocorrelation for carotid artery

NASA Astrophysics Data System (ADS)

Ye, Jihui; Kim, Hoonmin; Park, Jongho; Yeo, Sunmi; Shim, Hwan; Lim, Hyungjoon; Yoo, Yangmo

2014-03-01

Atherosclerosis is a leading cause of cardiovascular disease. The early diagnosis of atherosclerosis is of clinical interest since it can prevent any adverse effects of atherosclerotic vascular diseases. In this paper, a new carotid artery radial strain estimation method based on autocorrelation is presented. In the proposed method, the strain is first estimated by the autocorrelation of two complex signals from the consecutive frames. Then, the angular phase from autocorrelation is converted to strain and strain rate and they are analyzed over time. In addition, a 2D strain image over region of interest in a carotid artery can be displayed. To evaluate the feasibility of the proposed radial strain estimation method, radiofrequency (RF) data of 408 frames in the carotid artery of a volunteer were acquired by a commercial ultrasound system equipped with a research package (V10, Samsung Medison, Korea) by using a L5-13IS linear array transducer. From in vivo carotid artery data, the mean strain estimate was -0.1372 while its minimum and maximum values were -2.961 and 0.909, respectively. Moreover, the overall strain estimates are highly correlated with the reconstructed M-mode trace. Similar results were obtained from the estimation of the strain rate change over time. These results indicate that the proposed carotid artery radial strain estimation method is useful for assessing the arterial wall's stiffness noninvasively without increasing the computational complexity.

Strain Modulations as a Mechanism to Reduce Stress Relaxation in Laryngeal Tissues

PubMed Central

Hunter, Eric J.; Siegmund, Thomas; Chan, Roger W.

2014-01-01

Vocal fold tissues in animal and human species undergo deformation processes at several types of loading rates: a slow strain involved in vocal fold posturing (on the order of 1 Hz or so), cyclic and faster posturing often found in speech tasks or vocal embellishment (1–10 Hz), and shear strain associated with vocal fold vibration during phonation (100 Hz and higher). Relevant to these deformation patterns are the viscous properties of laryngeal tissues, which exhibit non-linear stress relaxation and recovery. In the current study, a large strain time-dependent constitutive model of human vocal fold tissue is used to investigate effects of phonatory posturing cyclic strain in the range of 1 Hz to 10 Hz. Tissue data for two subjects are considered and used to contrast the potential effects of age. Results suggest that modulation frequency and extent (amplitude), as well as the amount of vocal fold overall strain, all affect the change in stress relaxation with modulation added. Generally, the vocal fold cover reduces the rate of relaxation while the opposite is true for the vocal ligament. Further, higher modulation frequencies appear to reduce the rate of relaxation, primarily affecting the ligament. The potential benefits of cyclic strain, often found in vibrato (around 5 Hz modulation) and intonational inflection, are discussed in terms of vocal effort and vocal pitch maintenance. Additionally, elderly tissue appears to not exhibit these benefits to modulation. The exacerbating effect such modulations may have on certain voice disorders, such as muscle tension dysphonia, are explored. PMID:24614616

Strain modulations as a mechanism to reduce stress relaxation in laryngeal tissues.

PubMed

Hunter, Eric J; Siegmund, Thomas; Chan, Roger W

2014-01-01

Vocal fold tissues in animal and human species undergo deformation processes at several types of loading rates: a slow strain involved in vocal fold posturing (on the order of 1 Hz or so), cyclic and faster posturing often found in speech tasks or vocal embellishment (1-10 Hz), and shear strain associated with vocal fold vibration during phonation (100 Hz and higher). Relevant to these deformation patterns are the viscous properties of laryngeal tissues, which exhibit non-linear stress relaxation and recovery. In the current study, a large strain time-dependent constitutive model of human vocal fold tissue is used to investigate effects of phonatory posturing cyclic strain in the range of 1 Hz to 10 Hz. Tissue data for two subjects are considered and used to contrast the potential effects of age. Results suggest that modulation frequency and extent (amplitude), as well as the amount of vocal fold overall strain, all affect the change in stress relaxation with modulation added. Generally, the vocal fold cover reduces the rate of relaxation while the opposite is true for the vocal ligament. Further, higher modulation frequencies appear to reduce the rate of relaxation, primarily affecting the ligament. The potential benefits of cyclic strain, often found in vibrato (around 5 Hz modulation) and intonational inflection, are discussed in terms of vocal effort and vocal pitch maintenance. Additionally, elderly tissue appears to not exhibit these benefits to modulation. The exacerbating effect such modulations may have on certain voice disorders, such as muscle tension dysphonia, are explored.

Influence of 12C6+ ion irradiation on mutant avermitilis

NASA Astrophysics Data System (ADS)

Wang, Shu-Yang; Chen, Ji-Hong; Li, Wen-Jian; Liang, Jian-Ping; Bo, Yong-Heng; Ma, Xiao-Qi; Liu, Jing

2012-11-01

The effects of 12C+6 ion irradiation on colony morphology and mycelia morphology, as well as on mutation rate have been studied in the B1a high-product strains (ZJAV-Y1-203) mutated by heavy ion irradiation and compared with that in the original strain (ZJAV-A-1). After irradiating the rate of a straw hat colony type having a high ability of producing B1a in ZJAV-Y1-203 strains was higher than that found in ZJAV-A-1 strains. When strains were cultured in a liquid medium for 24 hours, the mycelium becoming thinner could be observed in all of the irradiated ZJAV- Y1-203 groups, but only in the ZJAV-A-1 groups irradiated at the dose of 50 Gy or more. The early growth of mycelium was inhibited in the ZJAV- Y1-203 group irradiated with a high dose. The highest positive mutation rate (23.5%) of ZJAV - Y1 - 203 was reached at the lower dose of 30 Gy while the highest positive mutation rate of 34.2% in ZJAV-A-1 appeared at 50 Gy. These results indicate that the effects of heavy ion irradiation still exist even in the mutated Streptomyces avermitilis, and only the dose is lower and the effects not so strong compared with the one that is first irradiated with optimized heavy ion doses. This is evidence of the one directional mutation being controlled by many more factors in a organism.

Limits on rock strength under high confinement

NASA Astrophysics Data System (ADS)

Renshaw, Carl E.; Schulson, Erland M.

2007-06-01

Understanding of deep earthquake source mechanisms requires knowledge of failure processes active under high confinement. Under low confinement the compressive strength of rock is well known to be limited by frictional sliding along stress-concentrating flaws. Under higher confinement strength is usually assumed limited by power-law creep associated with the movement of dislocations. In a review of existing experimental data, we find that when the confinement is high enough to suppress frictional sliding, rock strength increases as a power-law function only up to a critical normalized strain rate. Within the regime where frictional sliding is suppressed and the normalized strain rate is below the critical rate, both globally distributed ductile flow and localized brittle-like failure are observed. When frictional sliding is suppressed and the normalized strain rate is above the critical rate, failure is always localized in a brittle-like manner at a stress that is independent of the degree of confinement. Within the high-confinement, high-strain rate regime, the similarity in normalized failure strengths across a variety of rock types and minerals precludes both transformational faulting and dehydration embrittlement as strength-limiting mechanisms. The magnitude of the normalized failure strength corresponding to the transition to the high-confinement, high-strain rate regime and the observed weak dependence of failure strength on strain rate within this regime are consistent with a localized Peierls-type strength-limiting mechanism. At the highest strain rates the normalized strengths approach the theoretical limit for crystalline materials. Near-theoretical strengths have previously been observed only in nano- and micro-scale regions of materials that are effectively defect-free. Results are summarized in a new deformation mechanism map revealing that when confinement and strain rate are sufficient, strengths approaching the theoretical limit can be achieved in cm-scale sized samples of rocks rich in defects. Thus, non-frictional failure processes must be considered when interpreting rock deformation data collected under high confinement and low temperature. Further, even at higher temperatures the load-bearing ability of crustal rocks under high confinement may not be limited by a frictional process under typical geologic strain rates.

Different effects of BCG strains - A natural experiment evaluating the impact of the Danish and the Russian BCG strains on morbidity and scar formation in Guinea-Bissau.

PubMed

Frankel, H; Byberg, S; Bjerregaard-Andersen, M; Martins, C L; Aaby, P; Benn, C S; Fisker, A B

2016-08-31

Different Bacillus Calmette-Guerin (BCG) vaccine strains may have different non-specific effects. We assessed the effect of two BCG strains (Danish and Russian) on childhood morbidity and BCG scarification in Guinea-Bissau. During 2011-2013, infants in the Bandim Health Project's urban study area received the Danish or Russian BCG in a natural experiment. Health center consultations were registered at point of care and scar status and size at age 4½ months. We assessed the effect of strain on consultation rates between vaccination and age 45days in Cox proportional hazards models. Scar prevalence and size were compared using binomial regression and ranksum tests. Among 1206 children, 18% received Danish BCG (n=215) and 82% Russian BCG (n=991). The adjusted hazard ratio (aHR) for consultations was 0.94 (95% CI 0.60-1.46) for Danish BCG compared with Russian BCG. Girls vaccinated with Danish BCG tended to have lower consultation rates compared with girls vaccinated with Russian BCG (aHR 0.56 (0.25-1.24)), whereas the effect was opposite for boys (aHR 1.24 (0.74-2.11)), p=0.09. Children vaccinated with Danish BCG were more likely to develop a scar (97%) than children vaccinated with Russian BCG (87%), the relative risk (RR) being 1.11 (1.06-1.16). The effect was stronger in girls, and BCG scar size was larger among infants vaccinated with the Danish strain. BCG strain influences scar prevalence and scar size, and may have sex differential effects on morbidity. BCG strains are currently used interchangeably, but BCG scarring has been linked to subsequent survival. Hence, more research into the health effects of different BCG strains is warranted. Small adjustments of BCG production could potentially lower childhood morbidity and mortality at low cost. Copyright © 2016 Elsevier Ltd. All rights reserved.

Survivial Strategies in Bacterial Range Expansions

NASA Astrophysics Data System (ADS)

Frey, Erwin

2014-03-01

Bacterial communities represent complex and dynamic ecological systems. Different environmental conditions as well as bacterial interactions determine the establishment and sustainability of bacterial diversity. In this talk we discuss the competition of three Escherichia coli strains during range expansions on agar plates. In this bacterial model system, a colicin E2 producing strain C competes with a colicin resistant strain R and with a colicin sensitive strain S for new territory. Genetic engineering allows us to tune the growth rates of the strains and to study distinct ecological scenarios. These scenarios may lead to either single-strain dominance, pairwise coexistence, or to the coexistence of all three strains. In order to elucidate the survival mechanisms of the individual strains, we also developed a stochastic agent-based model to capture the ecological scenarios in silico. In a combined theoretical and experimental approach we are able to show that the level of biodiversity depends crucially on the composition of the inoculum, on the relative growth rates of the three strains, and on the effective reach of colicin toxicity.

Strain-rate and temperature-driven transition in the shear transformation zone for two-dimensional amorphous solids

NASA Astrophysics Data System (ADS)

Cao, Penghui; Park, Harold S.; Lin, Xi

2013-10-01

We couple the recently developed self-learning metabasin escape algorithm, which enables efficient exploration of the potential energy surface (PES), with shear deformation to elucidate strain-rate and temperature effects on the shear transformation zone (STZ) characteristics in two-dimensional amorphous solids. In doing so, we report a transition in the STZ characteristics that can be obtained through either increasing the temperature or decreasing the strain rate. The transition separates regions having two distinct STZ characteristics. Specifically, at high temperatures and high strain rates, we show that the STZs have characteristics identical to those that emerge from purely strain-driven, athermal quasistatic atomistic calculations. At lower temperatures and experimentally relevant strain rates, we use the newly coupled PES + shear deformation method to show that the STZs have characteristics identical to those that emerge from a purely thermally activated state. The specific changes in STZ characteristics that occur in moving from the strain-driven to thermally activated STZ regime include a 33% increase in STZ size, faster spatial decay of the displacement field, a change in the deformation mechanism inside the STZ from shear to tension, a reduction in the stress needed to nucleate the first STZ, and finally a notable loss in characteristic quadrupolar symmetry of the surrounding elastic matrix that has previously been seen in athermal, quasistatic shear studies of STZs.

High-temperature, low-cycle fatigue of advanced copper-base alloys for rocket nozzles. Part 2: NASA 1.1, Glidcop, and sputtered copper alloys

NASA Technical Reports Server (NTRS)

Conway, J. B.; Stentz, R. H.; Berling, J. T.

1974-01-01

Short-term tensile and low-cycle fatigue data are reported for five advance copper-base alloys: Sputtered Zr-Cu as received, sputtered Zr-Cu heat-treated, Glidcop AL-10, and NASA alloys 1-1A and 1-1B. Tensile tests were performed in argon at 538 C using an axial strain rate of 0.002/sec. Yield strength and ultimate tensile strength data are reported along with reduction in area values. Axial strain controlled low-cycle fatigue tests were performed in argon at 538C using an axial strain rate of 0.002/sec to define the fatigue life over the range from 100 to 3000 cycles for the five materials studied. It was found that the fatigue characteristics of the NASA 1-1A and NASA 1-1B compositions are identical and represent fatique life values which are much greater than those for the other materials tested. The effect of temperature on NASA 1-1B alloy at a strain rate of 0.002/sec was evaluated along with the effect of strain rates of 0.0004 and 0.01/sec at 538 C. Hold-time data are reported for the NASA 1-1B alloy at 538 C using 5 minute hold periods in tension only and compression only at two different strain range values. Hold periods in tension were much more detrimental than hold periods in compression.

Single-Cell Microfluidics to Study the Effects of Genome Deletion on Bacterial Growth Behavior.

PubMed

Yuan, Xiaofei; Couto, Jillian M; Glidle, Andrew; Song, Yanqing; Sloan, William; Yin, Huabing

2017-12-15

By directly monitoring single cell growth in a microfluidic platform, we interrogated genome-deletion effects in Escherichia coli strains. We compared the growth dynamics of a wild type strain with a clean genome strain, and their derived mutants at the single-cell level. A decreased average growth rate and extended average lag time were found for the clean genome strain, compared to those of the wild type strain. Direct correlation between the growth rate and lag time of individual cells showed that the clean genome population was more heterogeneous. Cell culturability (the ratio of growing cells to the sum of growing and nongrowing cells) of the clean genome population was also lower. Interestingly, after the random mutations induced by a glucose starvation treatment, for the clean genome population mutants that had survived the competition of chemostat culture, each parameter markedly improved (i.e., the average growth rate and cell culturability increased, and the lag time and heterogeneity decreased). However, this effect was not seen in the wild type strain; the wild type mutants cultured in a chemostat retained a high diversity of growth phenotypes. These results suggest that quasi-essential genes that were deleted in the clean genome might be required to retain a diversity of growth characteristics at the individual cell level under environmental stress. These observations highlight that single-cell microfluidics can reveal subtle individual cellular responses, enabling in-depth understanding of the population.

Strains of infectious hematopoietic necrosis (IHN) virus may be identified by structural protein differences

USGS Publications Warehouse

Leong, J.C.; Hsu, Ya Li; Engelking, H. Mark; Mulcahy, Daniel M.; Anderson, D.P.

1981-01-01

The development of an effective vaccine to infectious hematopoietic necrosis virus (IHNV) in fish requires a knowledge of the virus serotypes in nature. At least two serotypes were found among three IHNV strains (12). Attempts in our laboratory to extend this study with additional virus strains by classical immunological techniques were unsatisfactory. Thus, we sought another method for comparing IHNV strains. We report here that different strains of IHNV can be distinguished by the sodium dodecyl sulfate-polyacrylamide gel electrophoresis (SDS-PAGE) of the viron polypeptides. Major strain differences were noted in the molecular weights of the envelope glycoprotein, G, and the nucleocapsid protein, N.The strains of IHNV were established from samples taken at several locations in California, Oregon, Washington, and Alaska. These strains were also characterized by growth rate at 15° and 18°C and average plaque size. Distinct differences in growth rate at the two temperatures were found for the California strains. The California strains were distinguished from the other strains by the production of minute plaques.

Temperature and strain rate dependent behavior of polymer separator for Li-ion batteries

DOE PAGES

Kalnaus, Sergiy; Wang, Yanli; Li, Jianlin; ...

2018-03-07

Safe performance of advanced Li-ion batteries relies on integrity of the separator membrane which prevents contact between electrodes of opposite polarity. Current work provides detailed study of mechanical behavior of such membrane. Temperature and strain rate sensitivity of the triple-layer polypropylene (PP)/polyethylene (PE)/polypropylene (PP) porous separator for Li-ion batteries was studied experimentally under controlled temperatures of up to 120° (393 K), and strain rates (from 1∙10-4s-1 to 0.1s-1). Digital image correlation was used to study strain localization in separator under load. The results show significant dependence of mechanical properties on temperature, with the yield stress decreasing by 30% and elasticmore » modulus decreasing by a factor of two when the temperature is increased from 20 °C to 50 °C. The strain rate strengthening also decreased with higher temperatures while the temperature softening remained independent of the applied strain rate. Application of temperature creates long lasting changes in mechanical behavior of separator as was revealed by performing experiments after the annealing. Such delayed effect of temperature application appears to have directional dependence. The results demonstrate complex behavior of polymer separator which needs to be considered in proper safety assessments of Li-ion batteries.« less

Experimental investigation of anisotropy evolution of AZ31 magnesium alloy sheets under tensile loading

NASA Astrophysics Data System (ADS)

Tari, D. Ghaffari; Worswick, M. J.

2011-05-01

Increasing demand for lighter final products has created new opportunities for the application of new light weight materials. Due to high strength to density ratio and good magnetic resistance properties, magnesium alloys are good candidates to replace steel and aluminum for same application. However, limited numbers of active slip deformation mechanisms, result in a decreased formability at room temperature. Furthermore, wrought magnesium alloys have an initial crystallographic texture, remained from the prior rolling operations, which makes them highly anisotropic. In this paper, tensile tests are performed at room temperature and 200° C at different strain rates and orientations relative to the rolling direction, including rolling, 30°, 45°, 60° and transverse orientation. The strain rates adopted for these experiments varied from 0.001 to 1.0. The testing results show the effect of temperature on the strain rate sensitivity of AZ31 sheets. The extent of deformation is continuously recorded using two separate high temperature extensometers. The results of testing show an increase in the r-values with the plastic deformation. The strain rate sensitivity of AZ31 increased as the temperature was elevated. At higher strain rates the measured r-values are larger and the slope of its evolution with the plastic strain is steeper.

Temperature and strain rate dependent behavior of polymer separator for Li-ion batteries

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kalnaus, Sergiy; Wang, Yanli; Li, Jianlin

Safe performance of advanced Li-ion batteries relies on integrity of the separator membrane which prevents contact between electrodes of opposite polarity. Current work provides detailed study of mechanical behavior of such membrane. Temperature and strain rate sensitivity of the triple-layer polypropylene (PP)/polyethylene (PE)/polypropylene (PP) porous separator for Li-ion batteries was studied experimentally under controlled temperatures of up to 120° (393 K), and strain rates (from 1∙10-4s-1 to 0.1s-1). Digital image correlation was used to study strain localization in separator under load. The results show significant dependence of mechanical properties on temperature, with the yield stress decreasing by 30% and elasticmore » modulus decreasing by a factor of two when the temperature is increased from 20 °C to 50 °C. The strain rate strengthening also decreased with higher temperatures while the temperature softening remained independent of the applied strain rate. Application of temperature creates long lasting changes in mechanical behavior of separator as was revealed by performing experiments after the annealing. Such delayed effect of temperature application appears to have directional dependence. The results demonstrate complex behavior of polymer separator which needs to be considered in proper safety assessments of Li-ion batteries.« less

The fluid-dynamics of bubble-bearing magmas

NASA Astrophysics Data System (ADS)

colucci, simone; papale, paolo; montagna, chiara

2014-05-01

The rheological properties of a fluid establish how the shear stress, τ, is related to the shear strain-rate, γ . The simplest constitutive equation is represented by the linear relationship τ = μγ, where the viscosity parameter, μ, is independent of strain-rate and the velocity profile is parabolic. Fluids with such a flow curve are called Newtonian. Many fluids, though, exhibit non-Newtonian rheology, typically arising in magmas from the presence of a dispersed phase of either crystals or bubbles. In this case it is not possible to define a strain-rate-independent viscosity and the velocity profile is complex. In this work we extend the 1D, steady, isothermal, multiphase non-homogeneous magma ascent model of Papale (2001) to 1.5D including the Non-Newtonian rheology of the bubble-bearing magma. We describe such rheology in terms of an apparent viscosity, η, which is the ratio of stress to strain-rate (η = τ/γ) and varies with strain-rate across the conduit radius. In this way we calculate a depth-dependent Non-newtonian velocity profile across the radius along with shear strain-rate and viscosity distributions. The evolution of the velocity profile can now be studied in order to investigate processes which occur close to the conduit wall, such as fragmentation. Moreover, the model can quantify the effects of the Non-Newtonian rheology on conduit flow dynamics, in terms of flow variables (e.g. velocity, pressure).

Assessment of a miniature four-roll mill and a cross-slot microchannel for high-strain-rate stagnation point flows

NASA Astrophysics Data System (ADS)

Akbaridoust, Farzan; Philip, Jimmy; Marusic, Ivan

2018-04-01

Stagnation point flows have been widely used to study the deformation and break-up of objects in two-dimensional pure straining flows. Here, we report a systematic study of the characterisation of stagnation point flows in two devices, a miniature Taylor’s four-roll mill and a cross-slot microchannel. The aim of the study is to find the best platform suitable for investigating the effect of strain rate on the mechanical properties of waterborne microorganisms. Using micro-PIV, the velocity field and the strain rates in both devices were measured at different flow rates and compared with an ideal hyperbolic stagnation point flow. The cross-slot microchannel was found to be a better experimental device than the miniature four-roll mill for the purpose of confining micron-sized objects in a controlled stagnation point flow. This is mainly due to the difficulty of maintaining a fixed location for the stagnation point within one micron in the miniature four-roll mill and achieving high strain rates beyond 10 s-1 . However, with no moving parts, the cross-slot microchannel was found to maintain a steady flow, with the stagnation point varying less than one micron at a cross-junction of 400× 400~μm2 , and was able to reach uniform strain rates up to 140 s-1 .

Structure of Laminar Permanently Blue, Opposed-Jet Ethylene-Fueled Diffusion Flames

NASA Technical Reports Server (NTRS)

Lin, K.-C.; Faeth, G. M.; Urban, D. L. (Technical Monitor)

2000-01-01

The structure and state relationships of laminar soot-free (permanently blue) ethylene-fueled diffusion flames at various strain rates were studied both experimentally and computationally using an opposed-jet configuration. Measurements of gas velocities, temperatures, and compositions were carried out along the stagnation stream line. Corresponding predictions of flame structure were obtained, based on numerical simulations using several contemporary reaction mechanisms for methane oxidation. Flame conditions studied included ethylene-fueled opposed-jet diffusion flames having stoichiometric mixture fractions of 0.7 with measurements involving strain rates of 60-240/s and predictions involving strain rates of 0-1140/s at normal temperature and pressure. It was found that measured major gas species concentrations and temperature distributions were in reasonably good agreement with predictions using mechanisms due to GRI-Mech and Peters and that effects of preferential diffusion significantly influence flame structure even when reactant mass diffusivities are similar. Oxygen leakage to fuel-rich conditions and carbon monoxide leakage to fuel-lean conditions both increased as strain rates increased. Furthermore, increased strain rates caused increased fuel concentrations near the flame sheet, decreased peak gas temperatures, and decreased concentrations of carbon dioxide and water vapor throughout the flames. State relationships for major gas species and gas temperatures were found to exist over a broad range of strain rates, providing potential for significant computational simplifications for modeling purposes in some instances.

Structure of Laminar Permanently Blue, Opposed-Jet Ethylene-Fueled Diffusion Flames. Appendix E

NASA Technical Reports Server (NTRS)

Lin, K.-C.; Faeth, G. M.; Urban, D. L. (Technical Monitor)

2000-01-01

The structure and state relationships of laminar soot-free (permanently blue) ethylene-fueled diffusion flames at various strain rates were studied both experimentally and computationally using an opposed-jet configuration. Measurements of gas velocities, temperatures, and compositions were carried out along the stagnation stream line. Corresponding predictions of flame structure were obtained, based on numerical simulations using several contemporary reaction mechanisms for methane oxidation. Flame conditions studied included ethylene-fueled opposed-jet diffusion flames having stoichiometric mixture fractions of 0.7 with measurements involving strain rates of 60-240/s and predictions involving strain rates of 0-1140/s at normal temperature and pressure. It was found that measured major gas species concentrations and temperature distributions were in reasonably good agreement with predictions using mechanisms due to GRI-Mech and Peters and that effects of preferential diffusion significantly influence flame structure even when reactant mass diffusivities are similar. Oxygen leakage to fuel-rich conditions and carbon monoxide leakage to fuel-lean conditions both increased as strain rates increased. Furthermore, increased strain rates caused increased fuel concentrations near the flame sheet, decreased peak gas temperatures, and decreased concentrations of carbon dioxide and water vapor throughout the flames. State relationships for major gas species and gas temperatures were found to exist over a broad range of strain rates, providing potential for significant computational simplifications for modeling purposes in some instances.

Influence of particle size on the low and high strain rate behavior of dense colloidal dispersions of nanosilica

NASA Astrophysics Data System (ADS)

Asija, Neelanchali; Chouhan, Hemant; Gebremeskel, Shishay Amare; Bhatnagar, Naresh

2017-01-01

Shear thickening is a non-Newtonian flow behavior characterized by the increase in apparent viscosity with the increase in applied shear rate, particularly when the shear rate exceeds a critical value termed as the critical shear rate (CSR). Due to this remarkable property of shear-thickening fluids (STFs), they are extensively used in hip protection pads, protective gear for athletes, and more recently in body armor. The use of STFs in body armor has led to the development of the concept of liquid body armor. In this study, the effect of particle size is explored on the low and high strain rate behavior of nanosilica dispersions, so as to predict the efficacy of STF-aided personal protection systems (PPS), specifically for ballistic applications. The low strain rate study was conducted on cone and plate rheometer, whereas the high strain rate characterization of STF was conducted on in-house fabricated split Hopkinson pressure bar (SHPB) system. Spherical nanosilica particles of three different sizes (100, 300, and 500 nm) as well as fumed silica particles of four different specific surface areas (Aerosil A-90, A-130, A-150, and A-200), respectively, were used in this study. The test samples were prepared by dispersing nanosilica particles in polypropylene glycol (PPG) using ultrasonic homogenization method. The low strain rate studies aided in determining the CSR of the synthesized STF dispersions, whereas the high strain rate studies explored the impact-resisting ability of STFs in terms of the impact toughness and the peak stress attained during the impact loading of STF in SHPB testing.

Significant contribution of stacking faults to the strain hardening behavior of Cu-15%Al alloy with different grain sizes.

PubMed

Tian, Y Z; Zhao, L J; Chen, S; Shibata, A; Zhang, Z F; Tsuji, N

2015-11-19

It is commonly accepted that twinning can induce an increase of strain-hardening rate during the tensile process of face-centered cubic (FCC) metals and alloys with low stacking fault energy (SFE). In this study, we explored the grain size effect on the strain-hardening behavior of a Cu-15 at.%Al alloy with low SFE. Instead of twinning, we detected a significant contribution of stacking faults (SFs) irrespective of the grain size even in the initial stage of tensile process. In contrast, twinning was more sensitive to the grain size, and the onset of deformation twins might be postponed to a higher strain with increasing the grain size. In the Cu-15 at.%Al alloy with a mean grain size of 47 μm, there was a stage where the strain-hardening rate increases with strain, and this was mainly induced by the SFs instead of twinning. Thus in parallel with the TWIP effect, we proposed that SFs also contribute significantly to the plasticity of FCC alloys with low SFE.

Significant contribution of stacking faults to the strain hardening behavior of Cu-15%Al alloy with different grain sizes

PubMed Central

Tian, Y. Z.; Zhao, L. J.; Chen, S.; Shibata, A.; Zhang, Z. F.; Tsuji, N.

2015-01-01

It is commonly accepted that twinning can induce an increase of strain-hardening rate during the tensile process of face-centered cubic (FCC) metals and alloys with low stacking fault energy (SFE). In this study, we explored the grain size effect on the strain-hardening behavior of a Cu-15 at.%Al alloy with low SFE. Instead of twinning, we detected a significant contribution of stacking faults (SFs) irrespective of the grain size even in the initial stage of tensile process. In contrast, twinning was more sensitive to the grain size, and the onset of deformation twins might be postponed to a higher strain with increasing the grain size. In the Cu-15 at.%Al alloy with a mean grain size of 47 μm, there was a stage where the strain-hardening rate increases with strain, and this was mainly induced by the SFs instead of twinning. Thus in parallel with the TWIP effect, we proposed that SFs also contribute significantly to the plasticity of FCC alloys with low SFE. PMID:26582568

On the Importance of Adiabatic Heating on Deformation Behavior of Medium-Manganese Sheet Steels

NASA Astrophysics Data System (ADS)

Rana, Radhakanta; De Moor, Emmanuel; Speer, John G.; Matlock, David K.

2018-02-01

The effects of adiabatic heating during deformation of a medium-manganese transformation-induced plasticity steel containing 10.1Mn-1.68Al-0.14C-0.2Si (wt.%) processed with initially 57 vol.% retained austenite were investigated over the temperature range from - 60°C to 100°C at strain rates from 0.002 s-1 to 0.2 s-1. Tensile tests were performed on specimens immersed in isothermal baths, which reduced but did not completely eliminate adiabatic heating. The specimen temperature depended on the extent of adiabatic heating, which increased with strain and strain rate. The measured properties primarily reflected the effects of temperature on austenite stability and the corresponding resistance of austenite transformation to martensite with strain. Changes in austenite stability were monitored by measurements of austenite fractions at a specific strain and observation of microstructures after deformation. The results of this study provide a basis to identify input material parameters required for numerical models applicable to sheet metal forming of medium-Mn steels.

Normal Ranges of Right Ventricular Systolic and Diastolic Strain Measures in Children: A Systematic Review and Meta-Analysis

PubMed Central

Levy, Philip T.; Sanchez, Aura; Machefsky, Aliza; Fowler, Susan; Holland, Mark R.; Singh, Gautam K.

2014-01-01

Background Establishment of the range of normal values and associated variations of two-dimensional speckle-tracking echocardiography (2DSTE) derived right ventricular (RV) strain is a prerequisite for its routine clinical application in children. The objectives of this study were to perform a meta-analysis of normal ranges of RV longitudinal strain measurements derived by 2DSTE in children and identify confounders that may contribute to differences in reported measures. Methods A systematic review was launched in PubMed, Embase, Scopus, Cochrane, and ClinicTrials.gov. Search hedges were created to cover the concepts of pediatrics, speckle-tracking echocardiography, and right heart ventricle. Two investigators independently identified and included studies if they reported the 2DSTE derived RV strain measures: RV peak global longitudinal strain (pGLS), systolic strain rate (pGLSRs), early diastolic strain rate (pGLSRe), late diastolic strain rate (pGLSRa), or segmental longitudinal strain at the apical, mid, and basal ventricular levels in healthy children. Quality and reporting of the studies were assessed. The weighted mean was estimated by using random-effects with 95% confidence intervals (CI), heterogeneity was assessed by the Cochran's Q statistic and the inconsistency index (I2), and publication bias was evaluated using funnel plots and the Egger test. Effects of demographic, clinical, equipment, and software variables were assessed in a meta-regression. Results The search identified 226 children from 10 studies. The reported normal mean values of pGLS among the studies varied from −20.80% to −34.10% (mean, −29.03%, 95%CI, −31.52% to −26.54%), pGLSRs varied from −1.30 to −2.40 1/sec (mean, −1.88, 95%CI, −2.10 to −1.59), pGLSRe ranged from 1.7 to 2.69 1/sec (mean, 2.34, 95%CI, 2.00 to 2.67) and pGLSRa ranged from 1.00 to 1.30 1/sec (mean, 1.18, 95% CI, 1.04 to 1.33). A significant base-to-apex segmental strain gradient (p <0.05) was observed in the right ventricular free wall. There was significant between-study heterogeneity and inconsistency (I2>88% and p<0.01 for each strain measure), which was not explained by age, gender, body surface area, heart rate, frame rate, tissue tracking methodology, equipment, or software. The meta-regression showed that these effects were not significant determinants of variations among normal ranges of strain values. There was no evidence of publication bias (Egger test, p=0.59). Conclusions This study is the first to define normal values of two-dimensional speckle tracking echocardiographic (2DSTE) derived right ventricle strain in children on the basis of a meta-analysis. The normal mean value in children for RV global strain is −29.03% (95% CI, −31.52% to −26.54%). The normal mean value for RV global systolic strain rate is −1.88 1/sec (95% CI, −2.10 to −1.59). RV segmental strain has a stable base-to-apex gradient that highlights the dominance of deep longitudinal layers of the RV that are aligned base to apex. Variations among different normal ranges do not appear to be dependent on differences in demographic, clinical, or equipment parameters in this meta-analysis. All of the eligible studies used equipment and software from one manufacturer, General Electric (GE). PMID:24582163

Mechanical characterization and modeling for anodes and cathodes in lithium-ion batteries

NASA Astrophysics Data System (ADS)

Wang, Lubing; Yin, Sha; Zhang, Chao; Huan, Yong; Xu, Jun

2018-07-01

Mechanical properties of electrode materials have significant influence over electrochemical properties as well as mechanical integrity of lithium-ion battery cells. Here, anode and cathode in a commercially available 18650 NCA (Nickel Cobalt Aluminum Oxide)/graphite cell were comprehensively studied by tensile tests considering material anisotropy, SOC (state of charge), strain rate and electrolyte content. Results showed that the mechanical properties of both electrodes were highly dependent on strain rate and electrolyte content; however, anode was SOC dependent while cathode was not. Besides, coupled effects of strain rate and SOC of anodes were also discussed. SEM (scanning electron microscope) images of surfaces and cross-sections of electrodes showed the fracture morphology. In addition, mechanical behavior of Cu foil separated from anode with different SOC values were studied and compared. Finally, constitutive models of electrodes considering both strain rate and anisotropy effects were established. This study reveals the relationship between electrochemical dependent mechanical behavior of the electrodes. The established mechanical models of electrodes can be applied to the numerical computation of battery cells. Results are essential to predict the mechanical responses as well as the deformation of battery cell under various loading conditions, facilitating safer battery design and manufacturing.

Effect of mechanical properties on erosion resistance of ductile materials

NASA Astrophysics Data System (ADS)

Levin, Boris Feliksovih

Solid particle erosion (SPE) resistance of ductile Fe, Ni, and Co-based alloys as well as commercially pure Ni and Cu was studied. A model for SPE behavior of ductile materials is presented. The model incorporates the mechanical properties of the materials at the deformation conditions associated with SPE process, as well as the evolution of these properties during the erosion induced deformation. An erosion parameter was formulated based on consideration of the energy loss during erosion, and incorporates the material's hardness and toughness at high strain rates. The erosion model predicts that materials combining high hardness and toughness can exhibit good erosion resistance. To measure mechanical properties of materials, high strain rate compression tests using Hopkinson bar technique were conducted at strain rates similar to those during erosion. From these tests, failure strength and strain during erosion were estimated and used to calculate toughness of the materials. The proposed erosion parameter shows good correlation with experimentally measured erosion rates for all tested materials. To analyze subsurface deformation during erosion, microhardness and nanoindentation tests were performed on the cross-sections of the eroded materials and the size of the plastically deformed zone and the increase in materials hardness due to erosion were determined. A nanoindentation method was developed to estimate the restitution coefficient within plastically deformed regions of the eroded samples which provides a measure of the rebounding ability of a material during particle impact. An increase in hardness near the eroded surface led to an increase in restitution coefficient. Also, the stress rates imposed below the eroded surface were comparable to those measured during high strain-rate compression tests (10sp3-10sp4 ssp{-1}). A new parameter, "area under the microhardness curve" was developed that represents the ability of a material to absorb impact energy. By incorporating this parameter into a new erosion model, good correlation was observed with experimentally measured erosion rates. An increase in area under the microhardness curve led to an increase in erosion resistance. It was shown that an increase in hardness below the eroded surface occurs mainly due to the strain-rate hardening effect. Strain-rate sensitivities of tested materials were estimated from the nanoindentation tests and showed a decrease with an increase in materials hardness. Also, materials combining high hardness and strain-rate sensitivity may offer good erosion resistance. A methodology is presented to determine the proper mechanical properties to incorporate into the erosion parameter based on the physical model of the erosion mechanism in ductile materials.

Use of Slow Strain Rate Tensile Testing to Assess the Ability of Several Superalloys to Resist Environmentally-Assisted Intergranular Cracking

NASA Technical Reports Server (NTRS)

Gabb, Timothy P.; Telesman, Jack; Banik, Anthony; McDevitt, Erin

2014-01-01

Intergranular fatigue crack initiation and growth due to environmental degradation, especially at notched features, can often limit the fatigue life of disk superalloys at high temperatures. For clear comparisons, the effects of alloy composition on cracking in air needs to be understood and compared separately from variables associated with notches and cracks such as effective stress concentration, plastic flow, stress relaxation, and stress redistribution. The objective of this study was to attempt using simple tensile tests of specimens with uniform gage sections to compare the effects of varied alloy composition on environment-assisted cracking of several powder metal and cast and wrought superalloys including ME3, LSHR, Udimet 720(TradeMark) ATI 718Plus(Registered TradeMark) alloy, Haynes 282(Trademark), and Inconel 740(TradeMark) Slow and fast strain-rate tensile tests were found to be a useful tool to compare propensities for intergranular surface crack initiation and growth. The effects of composition and heat treatment on tensile fracture strain and associated failure modes were compared. Environment interactions were determined to often limit ductility, by promoting intergranular surface cracking. The response of various superalloys and heat treatments to slow strain rate tensile testing varied substantially, showing that composition and microstructure can significantly influence environmental resistance to cracking.

Resilience to temperature and pH changes in a future climate change scenario in six strains of the polar diatom Fragilariopsis cylindrus

NASA Astrophysics Data System (ADS)

Pančić, M.; Hansen, P. J.; Tammilehto, A.; Lundholm, N.

2015-07-01

The effects of ocean acidification and increased temperature on physiology of six strains of the polar diatom Fragilariopsis cylindrus from Greenland were investigated. Experiments were performed under manipulated pH levels (8.0, 7.7, 7.4, and 7.1) and different temperatures (1, 5, and 8 °C) to simulate changes from present to plausible future levels. Each of the 12 scenarios was run for 7 days, and a significant interaction between temperature and pH on growth was detected. By combining increased temperature and acidification, the two factors counterbalanced each other, and therefore no effect on the growth rates was found. However, the growth rates increased with elevated temperatures by ~ 20-50 % depending on the strain. In addition, a general negative effect of increasing acidification on growth was observed. At pH 7.7 and 7.4, the growth response varied considerably among strains. However, a more uniform response was detected at pH 7.1 with most of the strains exhibiting reduced growth rates by 20-37 % compared to pH 8.0. It should be emphasized that a significant interaction between temperature and pH was found, meaning that the combination of the two parameters affected growth differently than when considering one at a time. Based on these results, we anticipate that the polar diatom F. cylindrus will be unaffected by changes in temperature and pH within the range expected by the end of the century. In each simulated scenario, the variation in growth rates among the strains was larger than the variation observed due to the whole range of changes in either pH or temperature. Climate change may therefore not affect the species as such, but may lead to changes in the population structure of the species, with the strains exhibiting high phenotypic plasticity, in terms of temperature and pH tolerance towards future conditions, dominating the population.

Resilience to temperature and pH changes in a future climate change scenario in six strains of the polar diatom Fragilariopsis cylindrus

NASA Astrophysics Data System (ADS)

Pančić, M.; Hansen, P. J.; Tammilehto, A.; Lundholm, N.

2015-03-01

The effects of ocean acidification and increased temperature on physiology of six strains of the polar diatom Fragilariopsis cylindrus from Greenland were investigated. Experiments were performed under manipulated pH levels (8.0, 7.7, 7.4, and 7.1) and different temperatures (1, 5 and 8 °C) to simulate changes from present to plausible future levels. Each of the 12 scenarios was run for 7 days, and a significant interaction between temperature and pH on growth was detected. By combining increased temperature and acidification, the two factors counterbalanced each other, and therefore no effect on the growth rates was found. However, the growth rates increased with elevated temperatures by ∼20-50% depending on the strain. In addition, a general negative effect of increasing acidification on growth was observed. At pH 7.7 and 7.4, the growth response varied considerably among strains. However, a more uniform response was detected at pH 7.1 with most of the strains exhibiting reduced growth rates by 20-37% compared to pH 8.0. It should be emphasized that a significant interaction between temperature and pH was found, meaning that the combination of the two parameters affected growth differently than when considering one at a time. Based on these results, we anticipate that the polar diatom F. cylindrus will be unaffected by changes in temperature and pH within the range expected by the end of the century. In each simulated scenario, the variation in growth rates among the strains was larger than the variation observed due to the whole range of changes in either pH or temperature. Climate change may therefore not affect the species as such, but may lead to changes in the population structure of the species, with the strains exhibiting high phenotypic plasticity, in terms of temperature and pH tolerance towards future conditions, dominating the population.

High-Temperature Tensile Behaviors of Base Metal and Electron Beam-Welded Joints of Ni-20Cr-9Mo-4Nb Superalloy

NASA Astrophysics Data System (ADS)

Gupta, R. K.; Anil Kumar, V.; Sukumaran, Arjun; Kumar, Vinod

2018-05-01

Electron beam welding of Ni-20Cr-9Mo-4Nb alloy sheets was carried out, and high-temperature tensile behaviors of base metal and weldments were studied. Tensile properties were evaluated at ambient temperature, at elevated temperatures of 625 °C to 1025 °C, and at strain rates of 0.1 to 0.001 s-1. Microstructure of the weld consisted of columnar dendritic structure and revealed epitaxial mode of solidification. Weld efficiency of 90 pct in terms of strength (UTS) was observed at ambient temperature and up to an elevated temperature of 850 °C. Reduction in strength continued with further increase of test temperature (up to 1025 °C); however, a significant improvement in pct elongation is found up to 775 °C, which was sustained even at higher test temperatures. The tensile behaviors of base metal and weldments were similar at the elevated temperatures at the respective strain rates. Strain hardening exponent `n' of the base metal and weldment was 0.519. Activation energy `Q' of base metal and EB weldments were 420 to 535 kJ mol-1 determined through isothermal tensile tests and 625 to 662 kJ mol-1 through jump-temperature tensile tests. Strain rate sensitivity `m' was low (< 0.119) for the base metal and (< 0.164) for the weldment. The δ phase was revealed in specimens annealed at 700 °C, whereas, twins and fully recrystallized grains were observed in specimens annealed at 1025 °C. Low-angle misorientation and strain localization in the welds and the HAZ during tensile testing at higher temperature and strain rates indicates subgrain formation and recrystallization. Higher elongation in the weldment (at Test temperature > 775 °C) is attributed to the presence of recrystallized grains. Up to 700 °C, the deformation is through slip, where strain hardening is predominant and effect of strain rate is minimal. Between 775 °C to 850 °C, strain hardening is counterbalanced by flow softening, where cavitation limits the deformation (predominantly at lower strain rate). Above 925 °C, flow softening is predominant resulting in a significant reduction in strength. Presence of precipitates/accumulated strain at high strain rate results in high strength, but when the precipitates were coarsened at lower strain rates or precipitates were dissolved at a higher temperature, the result was a reduction in strength. Further, the accumulated strain assisted in recrystallization, which also resulted in a reduction in strength.

Effect of Mo on dynamic recrystallization and microstructure development of microalloyed steels

NASA Astrophysics Data System (ADS)

Schambron, Thomas; Dehghan-Manshadi, Ali; Chen, Liang; Gooch, Taliah; Killmore, Chris; Pereloma, Elena

2017-07-01

The dynamic recrystallization (DRX) behaviour, mechanical properties and microstructure development of four low carbon, Nb-Ti-containing micro-alloyed steels with Mo contents from 0 to 0.27 wt% were studied. Plane strain compression tests were performed in a Gleeble 3500 thermomechanical simulator. The effects of composition, deformation temperature and strain rate on the DRX parameters and resultant microstructures were examined. The volume fraction of recrystallised grains was estimated from micrographs and a DRX model. The stress-strain curves showed the typical signs of DRX over a wide range of deformation conditions. Dynamic recovery was only observed for higher strain rates (5 s-1) and/or lower deformation temperatures (below 1000 °C). It was shown that Mo increases the hot strength by around 100 MPa per weight percent. In addition, it has an effect on retarding recrystallization in microalloyed steels by increasing the activation energy for DRX by 320 kJ/molK per weight percent. This was attributed to solute drag and the interaction with other microalloying elements.

A Continuum Model for the Effect of Dynamic Recrystallization on the Stress–Strain Response

PubMed Central

Perdahcıoğlu, E. S.; van den Boogaard, A. H.

2018-01-01

Austenitic Stainless Steels and High-Strength Low-Alloy (HSLA) steels show significant dynamic recovery and dynamic recrystallization (DRX) during hot forming. In order to design optimal and safe hot-formed products, a good understanding and constitutive description of the material behavior is vital. A new continuum model is presented and validated on a wide range of deformation conditions including high strain rate deformation. The model is presented in rate form to allow for the prediction of material behavior in transient process conditions. The proposed model is capable of accurately describing the stress–strain behavior of AISI 316LN in hot forming conditions, also the high strain rate DRX-induced softening observed during hot torsion of HSLA is accurately predicted. It is shown that the increase in recrystallization rate at high strain rates observed in experiments can be captured by including the elastic energy due to the dynamic stress in the driving pressure for recrystallization. Furthermore, the predicted resulting grain sizes follow the power-law dependence with steady state stress that is often reported in literature and the evolution during hot deformation shows the expected trend. PMID:29789492

Effect of Temperature and Dynamic Loading on the Mechanical Properties of Copper-Alloyed High-Strength Interstitial-Free Steel

NASA Astrophysics Data System (ADS)

Rana, R.; Singh, S. B.; Bleck, W.; Mohanty, O. N.

2009-04-01

Crash resistance and formability relevant mechanical properties of a copper-alloyed interstitial-free (IF) steel processed under various conditions of batch annealing (BA), continuous annealing (CA), and postcontinuous annealing aging have been studied in a wide range of strain rate (3.33 × 10-4 to 200 s-1) and temperature (-100 °C to +20 °C). These properties have been compared with similarly processed traditional mild and high-strength IF steels. Assessment of various parameters such as strength, elongation, strain rate sensitivity of stress, strain-hardening capacity, temperature sensitivity of stress, activation volume, and specific energy absorption of all these steels implies that copper-alloyed IF steel is soft and formable in CA condition. It can be made stronger and more crash resistant than the conventional mild- or high-strength IF steels when aged to peak strength after CA. Room-temperature strain rate sensitivity of stress of the investigated steels exhibits a two-stage behavior. Copper in solution in ferrite causes solid solution softening at low temperatures (≤20 °C) and at high strain rates (200 s-1).

Characterization of Hot Deformation Behavior of a Fe-Cr-Ni-Mo-N Superaustenitic Stainless Steel Using Dynamic Materials Modeling

NASA Astrophysics Data System (ADS)

Pu, Enxiang; Zheng, Wenjie; Song, Zhigang; Feng, Han; Zhu, Yuliang

2017-03-01

Hot deformation behavior of a Fe-24Cr-22Ni-7Mo-0.5N superaustenitic stainless steel was investigated by hot compression tests in a wide temperature range of 950-1250 °C and strain rate range of 0.001-10 s-1. The flow curves show that the flow stress decreases as the deformation temperature increases or the strain rate decreases. The processing maps developed on the basis of the dynamic materials model and flow stress data were adopted to optimize the parameters of hot working. It was found that the strain higher than 0.2 has no significant effect on the processing maps. The optimum processing conditions were in the temperature range of 1125-1220 °C and strain rate range of 0.1-3 s-1. Comparing to other stable domains, microstructural observations in this domain revealed the complete dynamic recrystallization (DRX) with finer and more uniform grain size. Flow instability occurred in the domain of temperature lower than 1100 °C and strain rate higher than 0.1 s-1.

Effect of Light Intensity on the Relative Dominance of Toxigenic and Nontoxigenic Strains of Microcystis aeruginosa ▿

PubMed Central

LeBlanc Renaud, Susan; Pick, Frances R.; Fortin, Nathalie

2011-01-01

In aquatic ecosystems, the factors that regulate the dominance of toxin-producing cyanobacteria over non-toxin-producing strains of the same species are largely unknown. One possible hypothesis is that limiting resources lead to the dominance of the latter because of the metabolic costs associated with toxin production. In this study, we tested the effect of light intensity on the performance of a microcystin-producing strain of Microcystis aeruginosa (UTCC 300) when grown in mixed cultures with non-microcystin-producing strains with similar intrinsic growth rates (UTCC 632 and UTCC 633). The endpoints measured included culture growth rates, microcystin concentrations and composition, and mcyD gene copy numbers determined using quantitative PCR (Q-PCR). In contrast to the predicted results, under conditions of low light intensity (20 μmol·m−2·s−1), the toxigenic strain became dominant in both of the mixed cultures based on gene copy numbers and microcystin concentrations. When grown under conditions of high light intensity (80 μmol·m−2·s−1), the toxigenic strain still appeared to dominate over nontoxigenic strain UTCC 632 but less so over strain UTCC 633. Microcystins may not be so costly to produce that toxigenic cyanobacteria are at a disadvantage in competition for limiting resources. PMID:21841026

HIGH-RATE FORMABILITY OF HIGH-STRENGTH ALUMINUM ALLOYS: A STUDY ON OBJECTIVITY OF MEASURED STRAIN AND STRAIN RATE

DOE Office of Scientific and Technical Information (OSTI.GOV)

Upadhyay, Piyush; Rohatgi, Aashish; Stephens, Elizabeth V.

2015-02-18

Al alloy AA7075 sheets were deformed at room temperature at strain-rates exceeding 1000 /s using the electrohydraulic forming (EHF) technique. A method that combines high speed imaging and digital image correlation technique, developed at Pacific Northwest National Laboratory, is used to investigate high strain rate deformation behavior of AA7075. For strain-rate sensitive materials, the ability to accurately model their high-rate deformation behavior is dependent upon the ability to accurately quantify the strain-rate that the material is subjected to. This work investigates the objectivity of software-calculated strain and strain rate by varying different parameters within commonly used commercially available digital imagemore » correlation software. Except for very close to the time of crack opening the calculated strain and strain rates are very consistent and independent of the adjustable parameters of the software.« less

Contrasting effects of a nonionic surfactant on the biotransformation of polycyclic aromatic hydrocarbons to cis-dihydrodiols by soil bacteria

DOE Office of Scientific and Technical Information (OSTI.GOV)

Allen, C.C.R.; Boyd, D.R.; Hempenstall, F.

The biotransformation of the polycyclic aromatic hydrocarbons (PAHs) naphthalene and phenanthrene was investigated by using two dioxygenase-expressing bacteria, Pseudomonas sp. strain 9816/11 and Sphingomonas yanoikuyae B8/36, under conditions which facilitate mass-transfer limited substrate oxidation. Both of these strains are mutants that accumulate cis-dihydrodiol metabolites under the reaction conditions used. The effects of the nonpolar solvent 2,2,4,4,6,8,8-heptamethylnonane (HMN) and the nonionic surfactant Triton X-100 on the rate of accumulation of these metabolites were determined. HMN increased the rate of accumulation of metabolites for both microorganisms, with both substrates. The enhancement effect was most noticeable with phenanthrene, which has a lower aqueousmore » solubility than naphthalene. Triton X-100 increased the rate of oxidation of the PAHs with strain 9816/11 with the effect being most noticeable when phenanthrene was used as a substrate. However, the surfactant inhibited the biotransformation of both naphthalene and phenanthrene with strain B8/36 under the same conditions. The observation that a nonionic surfactant could have such contrasting effects on PAH oxidation by different bacteria, which are known to be important for the degradation of these compounds in the environment, may explain why previous research on the application of the surfactants to PAH bioremediation has yielded inconclusive results. The surfactant inhibited growth of the wild-type strain S. yanoikuyae B1 on aromatic compounds but did not inhibit B8/36 dioxygenase enzyme activity in vitro.« less

Strain-rate dependence of ramp-wave evolution and strength in tantalum

DOE PAGES

Lane, J. Matthew D.; Foiles, Stephen M.; Lim, Hojun; ...

2016-08-25

We have conducted molecular dynamics (MD) simulations of quasi-isentropic ramp-wave compression to very high pressures over a range of strain rates from 10 11 down to 10 8 1/s. Using scaling methods, we collapse wave profiles from various strain rates to a master profile curve, which shows deviations when material response is strain-rate dependent. Thus, we can show with precision where, and how, strain-rate dependence affects the ramp wave. We find that strain rate affects the stress-strain material response most dramatically at strains below 20%, and that above 30% strain the material response is largely independent of strain rate. Wemore » show good overall agreement with experimental stress-strain curves up to approximately 30% strain, above which simulated response is somewhat too stiff. We postulate that this could be due to our interatomic potential or to differences in grain structure and/or size between simulation and experiment. Strength is directly measured from per-atom stress tensor and shows significantly enhanced elastic response at the highest strain rates. As a result, this enhanced elastic response is less pronounced at higher pressures and at lower strain rates.« less

Strain rate dependency of bovine trabecular bone under impact loading at sideways fall velocity.

PubMed

Enns-Bray, William S; Ferguson, Stephen J; Helgason, Benedikt

2018-05-03

There is currently a knowledge gap in scientific literature concerning the strain rate dependent properties of trabecular bone at intermediate strain rates. Meanwhile, strain rates between 10 and 200/s have been observed in previous dynamic finite element models of the proximal femur loaded at realistic sideways fall speeds. This study aimed to quantify the effect of strain rate (ε̇) on modulus of elasticity (E), ultimate stress (σ u ), failure energy (U f ), and minimum stress (σ m ) of trabecular bone in order to improve the biofidelity of material properties used in dynamic simulations of sideways fall loading on the hip. Cylindrical cores of trabecular bone (D = 8 mm, L gauge  = 16 mm, n = 34) from bovine proximal tibiae and distal femurs were scanned in µCT (10 µm), quantifying apparent density (ρ app ) and degree of anisotropy (DA), and subsequently impacted within a miniature drop tower. Force of impact was measured using a piezoelectric load cell (400 kHz), while displacement during compression was measured from high speed video (50,000 frames/s). Four groups, with similar density distributions, were loaded at different impact velocities (0.84, 1.33, 1.75, and 2.16 m/s) with constant kinetic energy (0.4 J) by adjusting the impact mass. The mean strain rates of each group were significantly different (p < 0.05) except for the two fastest impact speeds (p = 0.09). Non-linear regression models correlated strain rate, DA, and ρ app with ultimate stress (R 2  = 0.76), elastic modulus (R 2  = 0.63), failure energy (R 2  = 0.38), and minimum stress (R 2  = 0.57). These results indicate that previous estimates of σ u could be under predicting the mechanical properties at strain rates above 10/s. Copyright © 2018 Elsevier Ltd. All rights reserved.

Internal state variable plasticity-damage modeling of AISI 4140 steel including microstructure-property relations: temperature and strain rate effects

NASA Astrophysics Data System (ADS)

Nacif el Alaoui, Reda

Mechanical structure-property relations have been quantified for AISI 4140 steel. under different strain rates and temperatures. The structure-property relations were used. to calibrate a microstructure-based internal state variable plasticity-damage model for. monotonic tension, compression and torsion plasticity, as well as damage evolution. Strong stress state and temperature dependences were observed for the AISI 4140 steel. Tension tests on three different notched Bridgman specimens were undertaken to study. the damage-triaxiality dependence for model validation purposes. Fracture surface. analysis was performed using Scanning Electron Microscopy (SEM) to quantify the void. nucleation and void sizes in the different specimens. The stress-strain behavior exhibited. a fairly large applied stress state (tension, compression dependence, and torsion), a. moderate temperature dependence, and a relatively small strain rate dependence.

A mechanism for crustal recycling on Venus

NASA Technical Reports Server (NTRS)

Lenardic, A.; Kaula, W. M.; Bindschadler, D. L.

1993-01-01

Entrainment of lower crust by convective mantle downflows is proposed as a crustal recycling mechanism on Venus. The mechanism is characterized by thin sheets of crust being pulled into the mantle by viscous flow stresses. Finite element models of crust/mantle interaction are used to explore tectonic conditions under which crustal entrainment may occur. The recycling scenarios suggested by the numerical models are analogous to previously studied problems for which analytic and experimental relationships assessing entrainment rates have been derived. We use these relationships to estimate crustal recycling rates on Venus. Estimated rates are largely determined by (1) strain rate at the crust/mantle interface (higher strain rate leads to greater entrainment); and (2) effective viscosity of the lower crust (viscosity closer to that of mantle lithosphere leads to greater entrainment). Reasonable geologic strain rates and available crustal flow laws suggest entrainment can recycle approximately equal 1 cu km of crust per year under favorable conditions.

Impacts of cooling intervention on the heat strain attenuation of construction workers

NASA Astrophysics Data System (ADS)

Zhao, Yijie; Yi, Wen; Chan, Albert P. C.; Wong, Del P.

2018-05-01

This study aimed to evaluate the effectiveness and practicality of a cooling intervention with a newly designed cooling vest on heat strain attenuation in the construction industry. Fourteen construction workers volunteered to participate in the field study. Each participant took part in two trials, i.e., cooling and control. Construction work included morning and afternoon sessions. Cooling intervention was implemented for 15 and 30 min during the morning and afternoon rest periods, respectively, between repeated bouts of work. Micrometeorological (wet-bulb globe temperature [WBGT]), physiological (tympanic temperature and heart rate), and perceptual (ratings of perceived exertion [RPE] and thermal sensation) measurements were taken during the test. Heat strain indices, including physiological strain index (PSIHR) and perceptual strain index (PeSI), were estimated accordingly. During the study, construction workers were exposed to a hot environment with a mean WBGT of 31.56 ± 1.87 °C. Compared with the control, physiological and perceptual strain were significantly reduced in the cooling condition during rest and subsequent work periods (p < 0.05; d = 0.24-1.07, small to large cooling effect). Cooling intervention significantly alleviates heat strain in the construction industry. The effectiveness and practicality of a proposed cooling intervention were tested in a field study. Results provide a reference for setting guidelines and promoting application on a range of construction sites.

Impacts of cooling intervention on the heat strain attenuation of construction workers.

PubMed

Zhao, Yijie; Yi, Wen; Chan, Albert P C; Wong, Del P

2018-05-25

This study aimed to evaluate the effectiveness and practicality of a cooling intervention with a newly designed cooling vest on heat strain attenuation in the construction industry. Fourteen construction workers volunteered to participate in the field study. Each participant took part in two trials, i.e., cooling and control. Construction work included morning and afternoon sessions. Cooling intervention was implemented for 15 and 30 min during the morning and afternoon rest periods, respectively, between repeated bouts of work. Micrometeorological (wet-bulb globe temperature [WBGT]), physiological (tympanic temperature and heart rate), and perceptual (ratings of perceived exertion [RPE] and thermal sensation) measurements were taken during the test. Heat strain indices, including physiological strain index (PSI HR ) and perceptual strain index (PeSI), were estimated accordingly. During the study, construction workers were exposed to a hot environment with a mean WBGT of 31.56 ± 1.87 °C. Compared with the control, physiological and perceptual strain were significantly reduced in the cooling condition during rest and subsequent work periods (p < 0.05; d = 0.24-1.07, small to large cooling effect). Cooling intervention significantly alleviates heat strain in the construction industry. The effectiveness and practicality of a proposed cooling intervention were tested in a field study. Results provide a reference for setting guidelines and promoting application on a range of construction sites.

Effects of Thermal Damage on Strain Burst Mechanism for Brittle Rocks Under True-Triaxial Loading Conditions

NASA Astrophysics Data System (ADS)

Akdag, Selahattin; Karakus, Murat; Taheri, Abbas; Nguyen, Giang; Manchao, He

2018-06-01

Strain burst is a common problem encountered in brittle rocks in deep, high-stress mining applications. Limited research focuses on the effects of temperature on the strain burst mechanism and the kinetic energies of rocks. This study aims to investigate the effects of thermal damage on the strain burst characteristics of brittle rocks under true-triaxial loading-unloading conditions using the acoustic emission (AE) and kinetic energy analyses. The time-domain and frequency-domain responses related to strain burst were studied, and the damage evolution was quantified by b-values, cumulative AE energy and events rates. The ejection velocities of the rock fragments from the free face of the granite specimens were used to calculate kinetic energies. The experimental results showed that thermal damage resulted in a delay in bursting but increased the bursting rate at 95% of normalised stress level. This is believed to be due to the micro-cracks induced by temperature exposure, and thus the accumulated AE energy (also supported by cumulative AE counts) at the initial loading stage was reduced, causing a delay in bursting. The strain burst stress, initial rock fragment ejection velocity, and kinetic energy decreased from room temperature (25 °C) to 100 °C, whereas they resulted in a gradual rise from 100 to 150 °C demonstrating more intense strain burst behaviour.

The tensile effect on crack formation in single crystal silicon irradiated by intense pulsed ion beam

NASA Astrophysics Data System (ADS)

Liang, Guoying; Shen, Jie; Zhang, Jie; Zhong, Haowen; Cui, Xiaojun; Yan, Sha; Zhang, Xiaofu; Yu, Xiao; Le, Xiaoyun

2017-10-01

Improving antifatigue performance of silicon substrate is very important for the development of semiconductor industry. The cracking behavior of silicon under intense pulsed ion beam irradiation was studied by numerical simulation in order to understand the mechanism of induced surface peeling observed by experimental means. Using molecular dynamics simulation based on Stillinger Weber potential, tensile effect on crack growth and propagation in single crystal silicon was investigated. Simulation results reveal that stress-strain curves of single crystal silicon at a constant strain rate can be divided into three stages, which are not similar to metal stress-strain curves; different tensile load velocities induce difference of single silicon crack formation speed; the layered stress results in crack formation in single crystal silicon. It is concluded that the crack growth and propagation is more sensitive to strain rate, tensile load velocity, stress distribution in single crystal silicon.

Turbulence Modeling Effects on the Prediction of Equilibrium States of Buoyant Shear Flows

NASA Technical Reports Server (NTRS)

Zhao, C. Y.; So, R. M. C.; Gatski, T. B.

2001-01-01

The effects of turbulence modeling on the prediction of equilibrium states of turbulent buoyant shear flows were investigated. The velocity field models used include a two-equation closure, a Reynolds-stress closure assuming two different pressure-strain models and three different dissipation rate tensor models. As for the thermal field closure models, two different pressure-scrambling models and nine different temperature variance dissipation rate, Epsilon(0) equations were considered. The emphasis of this paper is focused on the effects of the Epsilon(0)-equation, of the dissipation rate models, of the pressure-strain models and of the pressure-scrambling models on the prediction of the approach to equilibrium turbulence. Equilibrium turbulence is defined by the time rate (if change of the scaled Reynolds stress anisotropic tensor and heat flux vector becoming zero. These conditions lead to the equilibrium state parameters. Calculations show that the Epsilon(0)-equation has a significant effect on the prediction of the approach to equilibrium turbulence. For a particular Epsilon(0)-equation, all velocity closure models considered give an equilibrium state if anisotropic dissipation is accounted for in one form or another in the dissipation rate tensor or in the Epsilon(0)-equation. It is further found that the models considered for the pressure-strain tensor and the pressure-scrambling vector have little or no effect on the prediction of the approach to equilibrium turbulence.

Evaluation of immunomodulatory activity of two potential probiotic Lactobacillus strains by in vivo tests.

PubMed

Ren, Dayong; Li, Chang; Qin, Yanqing; Yin, Ronglan; Du, Shouwen; Liu, Hongfeng; Zhang, Yanfang; Wang, Cuiyan; Rong, Fengjun; Jin, Ningyi

2015-10-01

Here we evaluate the immunomodulatory function of two potential probiotic strains, Lactobacillus salivarius CICC 23174 and Lactobacillus plantarum CGMCC 1.557. Mice were fed with each Lactobacillus strain at different doses for several consecutive days. The effects of the two probiotic strains on immune organs, immune cells and immune molecules were investigated on days 10 and 20. Both Lactobacillus strains increased the spleen index, improved the spleen lymphocyte transformation rate, enhanced sIgA production and improved the number of CD11c(+) CD80(+) double-positive cells. L. plantarum CGMCC 1.557 was the more active strain in enhancing the phagocytic activity of macrophages, while, L. salivarius CICC 23174 was the more effective strain at maintaining the Th1/Th2 balance. This study suggests that these two Lactobacillus strains have beneficial effects on regulation of immune responses, which has promising implications for the development of ecological agents and functional foods. Copyright © 2015 Elsevier Ltd. All rights reserved.

Effect of irradiation temperature and strain rate on the mechanical properties of V-4Cr-4Ti irradiated to low doses in fission reactors

DOE Office of Scientific and Technical Information (OSTI.GOV)

Zinkle, S.J.; Snead, L.L.; Rowcliffe, A.F.

Tensile tests performed on irradiated V-(3-6%)Cr-(3-6%)Ti alloys indicate that pronounced hardening and loss of strain hardening capacity occurs for doses of 0.1--20 dpa at irradiation temperatures below {approximately}330 C. The amount of radiation hardening decreases rapidly for irradiation temperatures above 400 C, with a concomitant increase in strain hardening capacity. Low-dose (0.1--0.5 dpa) irradiation shifts the dynamic strain aging regime to higher temperatures and lower strain rates compared to unirradiated specimens. Very low fracture toughness values were observed in miniature disk compact specimens irradiated at 200--320 C to {approximately}1.5--15 dpa and tested at 200 C.

Impact behaviour of an innovative plasticized poly(vinyl chloride) for the automotive industry

NASA Astrophysics Data System (ADS)

Bernard, C. A.; Bahlouli, N.; Wagner-Kocher, C.; Ahzi, S.; Rémond, Y.

2015-09-01

Plasticized poly(vinyl chloride) (PPVC) is widely used in the automotive industry in the design of structural parts for crashworthiness applications. Thus, it is necessary to study and understand the influence of the mechanical response and mechanical properties of PPVC over a wide range of strain rate, from quasi-static to dynamic loadings. The process is also investigated using different sample thicknesses. In this work, the strain rate effect of a new PPVC is investigated over a wide range of strain rates at three temperatures and for three thicknesses. A modelling of the yield stress is also proposed. The numerical prediction is in good agreement with the experimental results.

Effects of Internal and External Hydrogen on Inconel 718

NASA Technical Reports Server (NTRS)

Walter, R. J.; Frandsen, J. D.

1999-01-01

Internal hydrogen embrittlement (IHE) and hydrogen environment embrittlement (HEE) tensile and bend crack growth tests were performed on Inconel 718. For the IHE tests, the specimens were precharged to approximately 90 ppm hydrogen by exposure to 34.5 MPa H2 at 650 C. The HEE tests were performed in 34.5 MPa H2. Parameters evaluated were test temperature, strain rate for smooth and notch specimen geometries. The strain rate effect was very significant at ambient temperature for both IHE and HEE and decreased with increasing temperatures. For IHE, the strain rate effect was neglible at 260'C, and for HEE the strain rate effect was neglible at 400 C. At low temperatures, IHE was more severe than HEE, and at high temperatures HEE was more severe than IHE with a cross over temperature about 350 C. At 350 C, the equilibrium hydrogen concentration in Inconel 718 is about 50% lower than the hydrogen content of the precharged IHE specimens. Dislocation hydrogen sweeping of surface absorbed hydrogen was the likely transport mechanism for increasing the hydrogen concentration in the HEE tests sufficiently to produce the same degree of embrittlement as that of the more highly hydrogen charged IHE specimens. The main IHE fracture characteristic was formation of large, brittle flat facets, which decreased with increasing test temperature. The IHE fracture matrix surrounding the large facets ranged between brittle fine faceted to microvoid ductility depending upon strain rate, specimen geometry as well as temperature. The HEE fractures were characteristically fine featured, transgranular and brittle with a significant portion forming a "saw tooth" crystallographic pattern. Both IHE and HEE fractures were predominantly along the {1 1 1) slip and twin boundaries. With respect to embrittlement mechanism, it was postulated that dislocation hydrogen sweeping and hydrogen enhanced localized plasticity were active in HEE and IHE for concentrating hydrogen along (1 1 1) slip and twin planes. Final brittle failure occurred by hydrogen induced planer decohesion.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Hansen, Benjamin L; Bronkhorst, Curt; Beyerlein, Irene

The goal of this work is to formulate a constitutive model for the deformation of metals over a wide range of strain rates. Damage and failure of materials frequently occurs at a variety of deformation rates within the same sample. The present state of the art in single crystal constitutive models relies on thermally-activated models which are believed to become less reliable for problems exceeding strain rates of 10{sup 4} s{sup -1}. This talk presents work in which we extend the applicability of the single crystal model to the strain rate region where dislocation drag is believed to dominate. Themore » elastic model includes effects from volumetric change and pressure sensitive moduli. The plastic model transitions from the low-rate thermally-activated regime to the high-rate drag dominated regime. The direct use of dislocation density as a state parameter gives a measurable physical mechanism to strain hardening. Dislocation densities are separated according to type and given a systematic set of interactions rates adaptable by type. The form of the constitutive model is motivated by previously published dislocation dynamics work which articulated important behaviors unique to high-rate response in fcc systems. The proposed material model incorporates thermal coupling. The hardening model tracks the varying dislocation population with respect to each slip plane and computes the slip resistance based on those values. Comparisons can be made between the responses of single crystals and polycrystals at a variety of strain rates. The material model is fit to copper.« less

Natural Strain

NASA Technical Reports Server (NTRS)

Freed, Alan D.

1995-01-01

The purpose of this paper is to present a consistent and thorough development of the strain and strain-rate measures affiliated with Hencky. Natural measures for strain and strain-rate, as I refer to them, are first expressed in terms of of the fundamental body-metric tensors of Lodge. These strain and strain-rate measures are mixed tensor fields. They are mapped from the body to space in both the Eulerian and Lagrangian configurations, and then transformed from general to Cartesian fields. There they are compared with the various strain and strain-rate measures found in the literature. A simple Cartesian description for Hencky strain-rate in the Lagrangian state is obtained.

The effect of muscle fatigue on in vivo tibial strains.

PubMed

Milgrom, Charles; Radeva-Petrova, Denitsa R; Finestone, Aharon; Nyska, Meir; Mendelson, Stephen; Benjuya, Nisim; Simkin, Ariel; Burr, David

2007-01-01

Stress fracture is a common musculoskeletal problem affecting athletes and soldiers. Repetitive high bone strains and strain rates are considered to be its etiology. The strain level necessary to cause fatigue failure of bone ex vivo is higher than the strains recorded in humans during vigorous physical activity. We hypothesized that during fatiguing exercises, bone strains may increase and reach levels exceeding those measured in the non-fatigued state. To test this hypothesis, we measured in vivo tibial strains, the maximum gastrocnemius isokinetic torque and ground reaction forces in four subjects before and after two fatiguing levels of exercise: a 2km run and a 30km desert march. Strains were measured using strain-gauged staples inserted percutaneously in the medial aspect of their mid-tibial diaphysis. There was a decrease in the peak gastrocnemius isokinetic torque of all four subjects' post-march as compared to pre-run (p=0.0001), indicating the presence of gastrocnemius muscle fatigue. Tension strains increased 26% post-run (p=0.002, 95 % confidence interval (CI) and 29% post-march (p=0.0002, 95% CI) as compared to the pre-run phase. Tension strain rates increased 13% post-run (p=0.001, 95% CI) and 11% post-march (p=0.009, 95% CI) and the compression strain rates increased 9% post-run (p=0.0004, 95% CI) and 17% post-march (p=0.0001, 95% CI). The fatigue state increases bone strains well above those recorded in rested individuals and may be a major factor in the stress fracture etiology.

Static versus dynamic fracturing in shallow carbonate fault zones

NASA Astrophysics Data System (ADS)

Fondriest, M.; Doan, M. L.; Aben, F. M.; Fusseis, F.; Mitchell, T. M.; Di Toro, G.

2015-12-01

Moderate to large earthquakes often nucleate within and propagate through carbonates in the shallow crust, therefore several field and experimental studies were recently aimed to constrain earthquake-related deformation processes within carbonate fault rocks. In particular, the occurrence of thick belts (10-100s m) of low-strain fault-related breccias (average size of rock fragments >1 cm), which is relatively common within carbonate damage zones, was generally interpreted as resulting from the quasi-static growth of fault zones rather than from the cumulative effect of multiple earthquake ruptures. Here we report the occurrence of up to hundreds of meters thick belts of intensely fragmented dolostones along the major transpressive Foiana Fault Zone (Italian Southern Alps) which was exhumed from < 2 km depth. Such dolostones are reduced into fragments ranging from few centimeters down to few millimeters in size with ultrafine-grained layers in proximity to the principal slip zones. Preservation of the original bedding indicates a lack of significant shear strain in the fragmented dolostones which seem to have been shattered in situ. To investigate the origin of the in-situ shattered rocks, the host dolostones were deformed in uniaxial compression both under quasi-static loading (strain rate ~10-3 s-1) and dynamic loading (strain rate >50 s-1). Dolostones deformed up to failure under low-strain rate were affected by single to multiple discrete (i.e. not interconnected) extensional fractures sub-parallel to the loading direction. Dolostones deformed under high-strain rate were shattered above a strain rate threshold of ~200 s-1(strain >1.2%) while they were split in few fragments or were macroscopically intact for lower strain rates. Experimentally shattered dolostones were reduced into a non-cohesive material with most rock fragments a few millimeters in size and elongated parallel to the loading direction. Fracture networks were investigated by X-ray microtomography showing that low- and high-strain rate damage patterns are different with the latter being similar to that of natural in-situ shattered dolostones. In-situ shattered dolostones are thus interpreted as the product of off-fault dynamic stress wave loading and can potentially be used to constrain coseismic energy release in fault zones.

The Compressive Behavior of Isocyanate-crosslinked Silica Aerogel at High Strain Rates

NASA Technical Reports Server (NTRS)

Luo, H.; Lu, H.; Leventis, N.

2006-01-01

Aerogels are low-density, highly nano-porous materials. Their engineering applications are limited due to their brittleness and hydrophilicity. Recently, a strong lightweight crosslinked silica aerogel has been developed by encapsulating the skeletal framework of amine-modified silica aerogels with polyureas derived by isocyanate. The mesoporous structure of the underlying silica framework is preserved through conformal polymer coating, and the thermal conductivity remains low. Characterization has been conducted on the thermal, physical properties and the mechanical properties under quasi-static loading conditions. In this paper, we present results on the dynamic compressive behavior of the crosslinked silica aerogel (CSA) using a split Hopkinson pressure bar (SHPB). A new tubing pulse shaper was employed to help reach the dynamic stress equilibrium and constant strain rate. The stress-strain relationship was determined at high strain rates within 114-4386/s. The effects of strain rate, density, specimen thickness and water absorption on the dynamic behavior of the CSA were investigated through a series of dynamic experiments. The Young's moduli (or 0.2% offset compressive yield strengths) at a strain rate approx.350/s were determined as 10.96/2.08, 159.5/6.75, 192.2/7.68, 304.6/11.46, 407.0/20.91 and 640.5/30.47 MPa for CSA with densities 0.205, 0.454, 0.492, 0.551,0.628 and 0.731 g/cu cm, respectively. The deformation and failure behaviors of a native silica aerogel with density (0.472 g/cu cm ), approximately the same as a typical CSA sample were observed with a high speed digital camera. Digital image correlation technique was used to determine the surface strains through a series of images acquired using high speed photography. The relative uniform axial deformation indicated that localized compaction did not occur at a compressive strain level of approx.17%, suggesting most likely failure mechanism at high strain rate to be different from that under quasi-static loading condition. The Poisson s ratio was determined to be 0.162 in nonlinear regime under high strain rates. CSA samples failed generally by splitting, but were much more ductile than native silica aerogels.

Flow Behavior and Constitutive Equation of Ti-6.5Al-2Sn-4Zr-4Mo-1W-0.2Si Titanium Alloy

NASA Astrophysics Data System (ADS)

Yang, Xuemei; Guo, Hongzhen; Liang, Houquan; Yao, Zekun; Yuan, Shichong

2016-04-01

In order to get a reliable constitutive equation for the finite element simulation, flow behavior of Ti-6.5Al-2Sn-4Zr-4Mo-1W-0.2Si alloy under high temperature was investigated by carrying a series of isothermal compression tests at temperatures of 1153-1293 K and strain rates of 0.01-10.0 s-1 on the Gleeble-1500 simulator. Results showed that the true stress-strain curves exhibited peaks at small strains, after which the flow stress decreased monotonically. Ultimately, the flow curves reached steady state at the strain of 0.6, showing a dynamic flow softening phenomenon. The effects of strain rate, temperature, and strain on the flow behavior were researched by establishing a constitutive equation. The relations among stress exponent, deformation activation energy, and strain were preliminarily discussed by using strain rate sensitivity exponent and dynamic recrystallization kinetics curve. Stress values predicted by the modified constitutive equation showed a good agreement with the experimental ones. The correlation coefficient ( R) and average absolute relative error (AARE) were 98.2% and 4.88%, respectively, which confirmed that the modified constitutive equation could give an accurate estimation of the flow stress for BT25y titanium alloy.

A cost-effective edge-filter-based FBG strain interrogator using catastrophic fuse effect microcavity interferometers

NASA Astrophysics Data System (ADS)

Díaz, Camilo A. R.; Marques, Carlos A. F.; Domingues, M. Fátima F.; Ribeiro, Moisés. R. N.; Neto, Anselmo F.; Pontes, Maria J.; André, Paulo S.; Antunes, Paulo F. C.

2018-02-01

This paper presents a simple, compact, stable and inexpensive in-line solution based on catastrophic fuse effect micro-cavity interferometers for edge-filter strain interrogation of a fiber Bragg grating sensor. By using a commercial spliced machine and recycling damage fiber for the catastrophic fuse effect it is possible to construct a micro-cavity with high contrast of more than 20dB, and acceptable half free spectra range (FSR) around 13nm of interrogation range. The strain from 0 to 1440μStrain of the FBG sensor is measured with evidences of high repeatability and stability. Future work will investigate the use of the proposed method for applications requiring higher interrogation rates.

Finite Element Modeling of the Behavior of Armor Materials Under High Strain Rates and Large Strains

NASA Astrophysics Data System (ADS)

Polyzois, Ioannis

For years high strength steels and alloys have been widely used by the military for making armor plates. Advances in technology have led to the development of materials with improved resistance to penetration and deformation. Until recently, the behavior of these materials under high strain rates and large strains has been primarily based on laboratory testing using the Split Hopkinson Pressure Bar apparatus. With the advent of sophisticated computer programs, computer modeling and finite element simulations are being developed to predict the deformation behavior of these metals for a variety of conditions similar to those experienced during combat. In the present investigation, a modified direct impact Split Hopkinson Pressure Bar apparatus was modeled using the finite element software ABAQUS 6.8 for the purpose of simulating high strain rate compression of specimens of three armor materials: maraging steel 300, high hardness armor (HHA), and aluminum alloy 5083. These armor materials, provided by the Canadian Department of National Defence, were tested at the University of Manitoba by others. In this study, the empirical Johnson-Cook visco-plastic and damage models were used to simulate the deformation behavior obtained experimentally. A series of stress-time plots at various projectile impact momenta were produced and verified by comparison with experimental data. The impact momentum parameter was chosen rather than projectile velocity to normalize the initial conditions for each simulation. Phenomena such as the formation of adiabatic shear bands caused by deformation at high strains and strain rates were investigated through simulations. It was found that the Johnson-Cook model can accurately simulate the behavior of body-centered cubic (BCC) metals such as steels. The maximum shear stress was calculated for each simulation at various impact momenta. The finite element model showed that shear failure first occurred in the center of the cylindrical specimen and propagated outwards diagonally towards the front and back edges forming an hourglass pattern. This pattern matched the failure behavior of specimens tested experimentally, which also exhibited failure through the formation of adiabatic shear bands. Adiabatic shear bands are known to lead to a complete shear failure. Both mechanical and thermal mechanisms contribute to the formation of shear bands. However, the finite element simulations did not show the effects of temperature rise within the material, a phenomenon which is known to contribute to thermal instabilities, whereby strain hardening effects are outweighed by thermal softening effects and adiabatic shear bands begin to form. In the simulations, the purely mechanical maximum shear stress failure, nucleating from the center of the specimens, was used as an indicator of the time at which these shear bands begin to form. The time and compressive stress at the moment of thermal instability in experimental results which have shown to form adiabatic shear bands, matched closely to those at which shear failure was first observed in the simulations. Although versatile in modeling BCC behavior, the Johnson-Cook model did not show the correct stress response in face-centered cubic (FCC) metals, such as aluminum 5083, where effects of strain rate and temperature depend on strain. Similar observations have been reported in literature. In the Johnson-Cook model, temperature, strain rate and strain" parameters are independent of each other. To this end, a more physical-based model based on dislocation mechanics, namely the Feng and Bassim constitutive model, would be more appropriate.

The Portevin–Le Chatelier effect: a review of experimental findings

PubMed Central

Yilmaz, Ahmet

2011-01-01

The Portevin–Le Chatelier (PLC) effect manifests itself as an unstable plastic flow during tensile tests of some dilute alloys under certain regimes of strain rate and temperature. The plastic strain becomes localized in the form of bands which move along a specimen gauge in various ways as the PLC effect occurs. Because the localization of strain causes degradation of the inherent structural properties and surface quality of materials, understanding the effect is crucial for the effective use of alloys. The characteristic behaviors of localized strain bands and techniques commonly used to study the PLC effect are summarized in this review. A brief overview of experimental findings, the effect of material properties and test parameters on the PLC effect, and some discussion on the mechanisms of the effect are included. Tests for predicting the early failure of structural materials due to embrittlement induced by the PLC effect are also discussed. PMID:27877450

Molecular Based Temperature and Strain Rate Dependent Yield Criterion for Anisotropic Elastomeric Thin Films

NASA Technical Reports Server (NTRS)

Bosi, F.; Pellegrino, S.

2017-01-01

A molecular formulation of the onset of plasticity is proposed to assess temperature and strain rate effects in anisotropic semi-crystalline rubbery films. The presented plane stress criterion is based on the strain rate-temperature superposition principle and the cooperative theory of yielding, where some parameters are assumed to be material constants, while others are considered to depend on specific modes of deformation. An orthotropic yield function is developed for a linear low density polyethylene thin film. Uniaxial and biaxial inflation experiments were carried out to determine the yield stress of the membrane via a strain recovery method. It is shown that the 3% offset method predicts the uniaxial elastoplastic transition with good accuracy. Both the tensile yield points along the two principal directions of the film and the biaxial yield stresses are found to obey the superposition principle. The proposed yield criterion is compared against experimental measurements, showing excellent agreement over a wide range of deformation rates and temperatures.

Accumulated financial strain and women's health over three decades.

PubMed

Shippee, Tetyana Pylypiv; Wilkinson, Lindsay R; Ferraro, Kenneth F

2012-09-01

Drawing from cumulative inequality theory, this research examines how accumulated financial strain affects women's self-rated health in middle and later life. Using data from the National Longitudinal Survey of Mature Women (1967-2003), we employ random-coefficient growth curve models to examine whether recurring financial strain influences women's health, above and beyond several measures of objective social status. Predicted probabilities of poor health were estimated by the frequency of financial strain. Financial strain is associated with rapid declines in women's health during middle and later life, especially for those women who reported recurrent strain. Changes in household income and household wealth were also associated with women's health but did not eliminate the effects due to accumulated financial strain. Accumulated financial strain has long-term effects on women's health during middle and later life. The findings demonstrate the importance of measuring life course exposure to stressors in studies of health trajectories.

Fatigue crack tip deformation and fatigue crack propagation

NASA Technical Reports Server (NTRS)

Kang, T. S.; Liu, H. W.

1972-01-01

The effects of stress ratio, prestress cycling and plate thickness on the fatigue crack propagation rate are studied on 2024-T351 aluminum alloy. Fatigue crack propagation rate increases with the plate thickness and the stress ratio. Prestress cycling below the static yield strength has no noticeable effect on the fatigue crack propagation rate. However, prestress cycling above the static yield strength causes the material to strain harden and increases the fatigue crack propagation rate. Crack tip deformation is used to study the fatigue crack propagation. The crack tip strains and the crack opening displacements were measured from moire fringe patterns. The moire fringe patterns were obtained by a double exposure technique, using a very high density master grille (13,400 lines per inch).

Early Impairment of Cardiac Function and Asynchronization of Systemic Amyloidosis with Preserved Ejection Fraction Using Two-Dimensional Speckle Tracking Echocardiography.

PubMed

Huang, He; Jing, Xian-chao; Hu, Zhang-xue; Chen, Xi; Liu, Xiao-qin

2015-12-01

To observe the ventricular global and regional function of the patients with systemic amyloidosis using two-dimensional speckle tracking echocardiography. The study enrolled 31 consecutive biopsy-proved patients with systemic amyloidosis who underwent echocardiographic examination and EF ≥ 55% and 37 age- and gender-matched healthy controls. We compared systolic strain and strain rate, diastolic strain rate, time to peak strain, peak delay time in longitudinal, radial, circumferential directions in 16 left ventricular segments. The global peak systolic longitudinal and radial strain of left ventricle, peak systolic longitudinal strain and strain rate, diastolic strain rate of right ventricular free wall were also compared. (1) Global peak systolic longitudinal strain (GPSLS), peak systolic longitudinal strain (PSLS) and strain rate (PSLSR), peak early diastolic longitudinal strain rate (PELSR) in 16 segments were decreased in case (P < 0.05). (2) Peak systolic radial strain and strain rate of inferoseptum and inferolateral at the level of papillary muscle were lower (P < 0.05), and peak early diastolic radial strain rate (PERSR) was reduced (P < 0.05). (3) Peak early diastolic circumferential strain rate was lower (P < 0.05). (4) Time to peak systolic longitudinal, radial, circumferential strain was longer, and peak delay time at the same level retarded (P < 0.05). (5) Into right ventricular wall, PSLS and PSLSR at mid-segment, and PSLSR, PELSR, peak atrial systolic longitudinal strain rate (PALSR) at basal were reduced (P < 0.05). (6) Inverse correlation between interventricular septum (IVS) thickness and GPSLS and GPSRS was found (P < 0.05). Systolic and diastolic dysfunction existed in systemic amyloidosis with preserved EF. Mechanical contraction disorder may be one reason for systolic dysfunction. GPLSR and GPRSR were negatively related to IVS thickness. © 2015, Wiley Periodicals, Inc.

Radiant extinction of gaseous diffusion flames

NASA Technical Reports Server (NTRS)

Atreya, Arvind; Agrawal, Sanjay; Shamim, Tariq; Pickett, Kent; Sacksteder, Kurt R.; Baum, Howard R.

1995-01-01

The absence of buoyancy-induced flows in microgravity significantly alters the fundamentals of many combustion processes. Substantial differences between normal-gravity and microgravity flames have been reported during droplet combustion, flame spread over solids, candle flames, and others. These differences are more basic than just in the visible flame shape. Longer residence time and higher concentration of combustion products create a thermochemical environment which changes the flame chemistry. Processes such as flame radiation, that are often ignored under normal gravity, become very important and sometimes even controlling. This is particularly true for conditions at extinction of a microgravity diffusion flame. Under normal-gravity, the buoyant flow, which may be characterized by the strain rate, assists the diffusion process to transport the fuel and oxidizer to the combustion zone and remove the hot combustion products from it. These are essential functions for the survival of the flame which needs fuel and oxidizer. Thus, as the strain rate is increased, the diffusion flame which is 'weak' (reduced burning rate per unit flame area) at low strain rates is initially 'strengthened' and eventually it may be 'blown-out'. Most of the previous research on diffusion flame extinction has been conducted at the high strain rate 'blow-off' limit. The literature substantially lacks information on low strain rate, radiation-induced, extinction of diffusion flames. At the low strain rates encountered in microgravity, flame radiation is enhanced due to: (1) build-up of combustion products in the flame zone which increases the gas radiation, and (2) low strain rates provide sufficient residence time for substantial amounts of soot to form which further increases the flame radiation. It is expected that this radiative heat loss will extinguish the already 'weak' diffusion flame under certain conditions. Identifying these conditions (ambient atmosphere, fuel flow rate, fuel type, etc.) is important for spacecraft fire safety. Thus, the objective is to experimentally and theoretically investigate the radiation-induced extinction of diffusion flames in microgravity and determine the effect of flame radiation on the 'weak' microgravity diffusion flame.

Mechanical Properties of EPON 826/DEA Epoxy

DTIC Science & Technology

2008-07-26

Eβ ( ε̇− ε̇pβ ) . (5b) Equations (2) and (5) are solved simultaneously as a system of time-dependant differential equations to determine the stress in...this implies that estimates of these underlying physical parameters are highly uncertain but also has a weak effect on the stress -strain relationships...20), 4923–4928 (1998) Chou, S.C., Robertson, K.D., et al.: The effect of strain rate and heat developed during deformation on the stress -strain curve

DOE Office of Scientific and Technical Information (OSTI.GOV)

Cook, J.M.; Sheppard, M.C.; Houwen, O.H.

Previous work on shale mechanical properties has focused on the slow deformation rates appropriate to wellbore deformation. Deformation of shale under a drill bit occurs at a very high rate, and the failure properties of the rock under these conditions are crucial in determining bit performance and in extracting lithology and pore-pressure information from drilling parameters. Triaxial tests were performed on two nonswelling shales under a wide range of strain rates and confining and pore pressures. At low strain rates, when fluid is relatively free to move within the shale, shale deformation and failure are governed by effective stress ormore » pressure (i.e., total confining pressure minus pore pressure), as is the case for ordinary rock. If the pore pressure in the shale is high, increasing the strain rate beyond about 0.1%/sec causes large increases in the strength and ductility of the shale. Total pressure begins to influence the strength. At high stain rates, the influence of effective pressure decreases, except when it is very low (i.e., when pore pressure is very high); ductility then rises rapidly. This behavior is opposite that expected in ordinary rocks. This paper briefly discusses the reasons for these phenomena and their impact on wellbore and drilling problems.« less

Band Gap Engineering with Ultralarge Biaxial Strains in Suspended Monolayer MoS2.

PubMed

Lloyd, David; Liu, Xinghui; Christopher, Jason W; Cantley, Lauren; Wadehra, Anubhav; Kim, Brian L; Goldberg, Bennett B; Swan, Anna K; Bunch, J Scott

2016-09-14

We demonstrate the continuous and reversible tuning of the optical band gap of suspended monolayer MoS2 membranes by as much as 500 meV by applying very large biaxial strains. By using chemical vapor deposition (CVD) to grow crystals that are highly impermeable to gas, we are able to apply a pressure difference across suspended membranes to induce biaxial strains. We observe the effect of strain on the energy and intensity of the peaks in the photoluminescence (PL) spectrum and find a linear tuning rate of the optical band gap of 99 meV/%. This method is then used to study the PL spectra of bilayer and trilayer devices under strain and to find the shift rates and Grüneisen parameters of two Raman modes in monolayer MoS2. Finally, we use this result to show that we can apply biaxial strains as large as 5.6% across micron-sized areas and report evidence for the strain tuning of higher level optical transitions.

Relationship of compressive stress-strain response of engineering materials obtained at constant engineering and true strain rates

DOE PAGES

Song, Bo; Sanborn, Brett

2018-05-07

In this paper, a Johnson–Cook model was used as an example to analyze the relationship of compressive stress-strain response of engineering materials experimentally obtained at constant engineering and true strain rates. There was a minimal deviation between the stress-strain curves obtained at the same constant engineering and true strain rates. The stress-strain curves obtained at either constant engineering or true strain rates could be converted from one to the other, which both represented the intrinsic material response. There is no need to specify the testing requirement of constant engineering or true strain rates for material property characterization, provided that eithermore » constant engineering or constant true strain rate is attained during the experiment.« less

Relationship of compressive stress-strain response of engineering materials obtained at constant engineering and true strain rates

DOE Office of Scientific and Technical Information (OSTI.GOV)

Song, Bo; Sanborn, Brett

In this paper, a Johnson–Cook model was used as an example to analyze the relationship of compressive stress-strain response of engineering materials experimentally obtained at constant engineering and true strain rates. There was a minimal deviation between the stress-strain curves obtained at the same constant engineering and true strain rates. The stress-strain curves obtained at either constant engineering or true strain rates could be converted from one to the other, which both represented the intrinsic material response. There is no need to specify the testing requirement of constant engineering or true strain rates for material property characterization, provided that eithermore » constant engineering or constant true strain rate is attained during the experiment.« less

Mechanistic Considerations Used in the Development of the PROFIT PCI Failure Model

DOE Office of Scientific and Technical Information (OSTI.GOV)

Pankaskie, P. J.

A fuel Pellet-Zircaloy Cladding (thermo-mechanical-chemical) Interactions (PC!) failure model for estimating the probability of failure in !ransient increases in power (PROFIT) was developed. PROFIT is based on 1) standard statistical methods applied to available PC! fuel failure data and 2) a mechanistic analysis of the environmental and strain-rate-dependent stress versus strain characteristics of Zircaloy cladding. The statistical analysis of fuel failures attributable to PCI suggested that parameters in addition to power, transient increase in power, and burnup are needed to define PCI fuel failures in terms of probability estimates with known confidence limits. The PROFIT model, therefore, introduces an environmentalmore » and strain-rate dependent strain energy absorption to failure (SEAF) concept to account for the stress versus strain anomalies attributable to interstitial-disloction interaction effects in the Zircaloy cladding. Assuming that the power ramping rate is the operating corollary of strain-rate in the Zircaloy cladding, then the variables of first order importance in the PCI fuel failure phenomenon are postulated to be: 1. pre-transient fuel rod power, P{sub I}, 2. transient increase in fuel rod power, {Delta}P, 3. fuel burnup, Bu, and 4. the constitutive material property of the Zircaloy cladding, SEAF.« less

Experimental Techniques for Evaluating the Effects of Aging on Impact and High Strain Rate Properties of Triaxial Braided Composite Materials

NASA Technical Reports Server (NTRS)

Pereira, J. Michael; Roberts, Gary D.; Ruggeri, Charles R.; Gilat, Amos; Matrka, Thomas

2010-01-01

An experimental program is underway to measure the impact and high strain rate properties of triaxial braided composite materials and to quantify any degradation in properties as a result of thermal and hygroscopic aging typically encountered during service. Impact tests are being conducted on flat panels using a projectile designed to induce high rate deformation similar to that experienced in a jet engine fan case during a fan blade-out event. The tests are being conducted on as-fabricated panels and panels subjected to various numbers of aging cycles. High strain rate properties are being measured using a unique Hopkinson bar apparatus that has a larger diameter than conventional Hopkinson bars. This larger diameter is needed to measure representative material properties because of the large unit cell size of the materials examined in this work. In this paper the experimental techniques used for impact and high strain rate testing are described and some preliminary results are presented for both as-fabricated and aged composites.

Left ventricular diastolic dysfunction in type 2 diabetes patients: a novel 2D strain analysis based on cardiac magnetic resonance imaging.

PubMed

Chen, Qiang; Gan, Yan; Li, Zhi-Yong

2016-09-01

This study was to develop a strain analysis method to evaluate the left ventricular (LV) functions in type 2 diabetic patients with an asymptomatic LV diastolic dysfunction. Two groups (10 asymptomatic type 2 diabetic subjects and 10 control ones) were considered. All of the subjects had normal ejection fraction values but impaired diastolic functions assessed by the transmitral blood flow velocity. For each subject, based on cardiac MRI, global indexes including LV volume, LV myocardial mass, cardiac index (CI), and transmitral peak velocity, were measured, and regional indexes (i.e., LV deformation, strain and strain rate) were calculated through an image-registration technology. Most of the global indexes did not differentiate between the two groups, except for the CI, LV myocardial mass and transmitral peak velocity. While for the regional indexes, the global LV diastolic dysfunction of the diabetic indicated an increased strain (0.08 ± 0.044 vs. -0.031 ± 0.077, p = 0.001) and a reduced strain rate (1.834 ± 0.909 vs. 3.791 ± 2.394, p = 0.033) compared to the controls, moreover, the local LV diastolic dysfunction reflected by the strain and strain rate varied, and the degree of dysfunction gradually decreased from the basal level to the apical level. The results showed that the strain and strain rates are effective to capture the subtle alterations of the LV functions, and the proposed method can be used to estimate the LV myocardial function based on cardiac MRI.

EFFECT OF AXIAL TIBIAL TORQUE DIRECTION ON ACL RELATIVE STRAIN AND STRAIN RATE IN AN IN VITRO SIMULATED PIVOT LANDING

PubMed Central

Oh, Youkeun K.; Kreinbrink, Jennifer L.; Wojtys, Edward M.; Ashton-Miller, James A.

2011-01-01

Anterior cruciate ligament (ACL) injuries most frequently occur under the large loads associated with a unipedal jump landing involving a cutting or pivoting maneuver. We tested the hypotheses that internal tibial torque would increase the anteromedial (AM) bundle ACL relative strain and strain rate more than would the corresponding external tibial torque under the large impulsive loads associated with such landing maneuvers. Twelve cadaveric female knees [mean (SD) age: 65.0 (10.5) years] were tested. Pretensioned quadriceps, hamstring and gastrocnemius muscle-tendon unit forces maintained an initial knee flexion angle of 15°. A compound impulsive test load (compression, flexion moment and internal or external tibial torque) was applied to the distal tibia while recording the 3-D knee loads and tibofemoral kinematics. AM-ACL relative strain was measured using a 3mm DVRT. In this repeated measures experiment, the Wilcoxon Signed-Rank test was used to test the null hypotheses with p<0.05 considered significant. The mean (± SD) peak AM-ACL relative strains were 5.4±3.7 % and 3.1±2.8 % under internal and external tibial torque, respectively. The corresponding mean (± SD) peak AM-ACL strain rates reached 254.4±160.1 %/sec and 179.4±109.9 %/sec, respectively. The hypotheses were supported in that the normalized mean peak AM-ACL relative strain and strain rate were 70% and 42% greater under internal than external tibial torque, respectively (p=0.023, p=0.041). We conclude that internal tibial torque is a potent stressor of the ACL because it induces a considerably (70%) larger peak strain in the AM-ACL than does a corresponding external tibial torque. PMID:22025178

Effects of laser power density on static and dynamic mechanical properties of dissimilar stainless steel welded joints

NASA Astrophysics Data System (ADS)

Wei, Yan-Peng; Li, Mao-Hui; Yu, Gang; Wu, Xian-Qian; Huang, Chen-Guang; Duan, Zhu-Ping

2012-10-01

The mechanical properties of laser welded joints under impact loadings such as explosion and car crash etc. are critical for the engineering designs. The hardness, static and dynamic mechanical properties of AISI304 and AISI316 L dissimilar stainless steel welded joints by CO2 laser were experimentally studied. The dynamic strain-stress curves at the strain rate around 103 s-1 were obtained by the split Hopkinson tensile bar (SHTB). The static mechanical properties of the welded joints have little changes with the laser power density and all fracture occurs at 316 L side. However, the strain rate sensitivity has a strong dependence on laser power density. The value of strain rate factor decreases with the increase of laser power density. The welded joint which may be applied for the impact loading can be obtained by reducing the laser power density in the case of welding quality assurance.

Analysis of Crushing Response of Composite Crashworthy Structures

NASA Astrophysics Data System (ADS)

David, Matthew; Johnson, Alastair F.; Voggenreiter, H.

2013-10-01

The paper describes quasi-static and dynamic tests to characterise the energy absorption properties of polymer composite crash energy absorbing segment elements under axial loads. Detailed computer tomography scans of failed specimens are used to identify local compression crush failure mechanisms at the crush front. The varied crushing morphology between the compression strain rates identified in this paper is observed to be due to the differences in the response modes and mechanical properties of the strain dependent epoxy matrix. The importance of understanding the role of strain rate effects in composite crash energy absorbing structures is highlighted in this paper.

Reduction of physiological strain under a hot and humid environment by a hybrid cooling vest.

PubMed

Chan, Albert P C; Yang, Y; Wong, Francis K W; Yam, Michael C H; Wong, Del P; Song, W F

2017-02-08

Cooling treatment is regarded as one of good practices to provide safe training conditions to athletic trainers in the hot environment. The present study aimed to investigate whether wearing a commercial lightweight and portable hybrid cooling vest that combines air ventilation fans with frozen gel packs was an effective means to reduce participants' body heat strain. In this within-subject repeated measures study, 10 male volunteers participated in two heat-stress trials (one with the cooling vest - COOL condition, and another without - CON condition, in a randomized order) inside a climatic chamber with a controlled ambient temperature 33 °C and relative humidity (RH) 75% on an experimental day. Each trial included a progressively incremental running test, followed by a 40 min post-exercise recovery. Core temperature (Tc), heart rate (HR), sweat rate, rating of perceived exertion (RPE), exercise duration, running distance, power output, and sweat rate were measured. When comparing the two conditions, a non-statistically significant moderate cooling effect in rate of increase in Tc (0.03±0.02 °C/min for COOL vs. 0.04±0.02 °C/min for CON, p=0.054, d=0.57), HR (3±1 bpm/min for COOL vs. 4±1 bpm/min for CON, p=0.229, d=0.40), and physiological strain index (PSI) (0.20±0.06 unit/min for COOL vs. 0.23±0.06 unit/min for CON, p=0.072, d=0.50) was found in the COOL condition during exercise. A non-statistically significant (p>0.05) trivial cooling effect (d<0.2) was observed between the COOL and CON conditions for measures of exercise duration, running distance, power output, sweat rate and RPE. It is concluded that the use of the hybrid cooling vest achieved a moderate cooling effect in lowering the rate of increase in physiological strain without impeding the performance of progressively incremental exercise in the heat.

Endochronic theory of transient creep and creep recovery

NASA Technical Reports Server (NTRS)

Wu, H. C.; Chen, L.

1979-01-01

Short time creep and creep recovery were investigated by means of the endochronic theory of viscoplasticity. It is shown that the constitutive equations for constant-strain-rate stress-strain behavior, creep, creep recovery, and stress relaxation can all ber derived from the general constitutive equation by imposing appropriate constraints. In this unified approach, the effect of strain-hardening is naturally accounted for when describing creep and creep recovery. The theory predicts with reasonable accuracy the creep and creep recovery behaviors for Aluminum 1100-0 at 150 C. It was found that the strain-rate history at prestraining stage affects the subsequent creep. A critical stress was also established for creep recovery. The theory predicts a forward creep for creep recovery stress greater than the critical stress. For creep recovery stress less than the critical stress, the theory then predicts a normal strain recovery.

The agreement between 3D, standard 2D and triplane 2D speckle tracking: effects of image quality and 3D volume rate.

PubMed

Trache, Tudor; Stöbe, Stephan; Tarr, Adrienn; Pfeiffer, Dietrich; Hagendorff, Andreas

2014-12-01

Comparison of 3D and 2D speckle tracking performed on standard 2D and triplane 2D datasets of normal and pathological left ventricular (LV) wall-motion patterns with a focus on the effect that 3D volume rate (3DVR), image quality and tracking artifacts have on the agreement between 2D and 3D speckle tracking. 37 patients with normal LV function and 18 patients with ischaemic wall-motion abnormalities underwent 2D and 3D echocardiography, followed by offline speckle tracking measurements. The values of 3D global, regional and segmental strain were compared with the standard 2D and triplane 2D strain values. Correlation analysis with the LV ejection fraction (LVEF) was also performed. The 3D and 2D global strain values correlated good in both normally and abnormally contracting hearts, though systematic differences between the two methods were observed. Of the 3D strain parameters, the area strain showed the best correlation with the LVEF. The numerical agreement of 3D and 2D analyses varied significantly with the volume rate and image quality of the 3D datasets. The highest correlation between 2D and 3D peak systolic strain values was found between 3D area and standard 2D longitudinal strain. Regional wall-motion abnormalities were similarly detected by 2D and 3D speckle tracking. 2DST of triplane datasets showed similar results to those of conventional 2D datasets. 2D and 3D speckle tracking similarly detect normal and pathological wall-motion patterns. Limited image quality has a significant impact on the agreement between 3D and 2D numerical strain values.

Job strain and resting heart rate: a cross-sectional study in a Swedish random working sample.

PubMed

Eriksson, Peter; Schiöler, Linus; Söderberg, Mia; Rosengren, Annika; Torén, Kjell

2016-03-05

Numerous studies have reported an association between stressing work conditions and cardiovascular disease. However, more evidence is needed, and the etiological mechanisms are unknown. Elevated resting heart rate has emerged as a possible risk factor for cardiovascular disease, but little is known about the relation to work-related stress. This study therefore investigated the association between job strain, job control, and job demands and resting heart rate. We conducted a cross-sectional survey of randomly selected men and women in Västra Götalandsregionen, Sweden (West county of Sweden) (n = 1552). Information about job strain, job demands, job control, heart rate and covariates was collected during the period 2001-2004 as part of the INTERGENE/ADONIX research project. Six different linear regression models were used with adjustments for gender, age, BMI, smoking, education, and physical activity in the fully adjusted model. Job strain was operationalized as the log-transformed ratio of job demands over job control in the statistical analyses. No associations were seen between resting heart rate and job demands. Job strain was associated with elevated resting heart rate in the unadjusted model (linear regression coefficient 1.26, 95 % CI 0.14 to 2.38), but not in any of the extended models. Low job control was associated with elevated resting heart rate after adjustments for gender, age, BMI, and smoking (linear regression coefficient -0.18, 95 % CI -0.30 to -0.02). However, there were no significant associations in the fully adjusted model. Low job control and job strain, but not job demands, were associated with elevated resting heart rate. However, the observed associations were modest and may be explained by confounding effects.

High Strain Rate Material Behavior

DTIC Science & Technology

1985-12-01

data. iii Mr. Dennis Paisely conducted the single plate impact test. Mr. Danny Yaziv is responsible for developing the double flyer plate technique and...neck developed . The sharp rise in the flow stress is due to the increased strain-rates during necking. The maximum observed value of effective stress...for the material modeling. Computer programs and special purpose subroutines were developed to use the Bodner-Partom model in the STEALTH finite

Environmental and High-Strain Rate effects on composites for engine applications

NASA Technical Reports Server (NTRS)

Chamis, C. C.; Smith, G. T.

1982-01-01

The Lewis Research Center is conducting a series of programs intended to investigate and develop the application of composite materials to structural components for turbojet engines. A significant part of that effort is directed to establishing resistance, defect growth, and strain rate characteristics of composite materials over the wide range of environmental and load conditions found in commercial turbojet engine operations. Both analytical and experimental efforts are involved.

High-Temperature Creep Behaviour and Positive Effect on Straightening Deformation of Q345c Continuous Casting Slab

NASA Astrophysics Data System (ADS)

Guo, Long; Zhang, Xingzhong

2018-03-01

Mechanical and creep properties of Q345c continuous casting slab subjected to uniaxial tensile tests at high temperature were considered in this paper. The minimum creep strain rate and creep rupture life equations whose parameters are calculated by inverse-estimation using the regression analysis were derived based on experimental data. The minimum creep strain rate under constant stress increases with the increase of the temperature from 1000 °C to 1200 °C. A new casting machine curve with the aim of fully using high-temperature creep behaviour is proposed in this paper. The basic arc segment is cancelled in the new curve so that length of the straightening area can be extended and time of creep behaviour can be increased significantly. For the new casting machine curve, the maximum straightening strain rate at the slab surface is less than the minimum creep strain rate. So slab straightening deformation based on the steel creep behaviour at high temperature can be carried out in the process of Q345c steel continuous casting. The effect of creep property at high temperature on slab straightening deformation is positive. It is helpful for the design of new casting machine and improvement of old casting machine.

Effect of temperature on the anisotropy of AZ31 magnesium alloy rolling sheet under high strain rate deformation

NASA Astrophysics Data System (ADS)

Liu, Yanyu; Mao, Pingli; Zhang, Feng; Liu, Zheng; Wang, Zhi

2018-04-01

In order to investigate the effect of temperature on the anisotropic behaviour of AZ31 magnesium alloy rolling sheet under high strain rate deformation, the Split Hopkinson Pressure Bar was used to analyse the dynamic mechanical properties of AZ31 magnesium alloy rolling sheet in three directions, rolling direction(RD), transverse direction (TD) and normal direction (ND). The texture of the rolling sheet was characterised by X-ray analysis and the microstructure prior and after high strain rate deformation was observed by optical microscope (OM). The results demonstrated that AZ31magnesium alloy rolling sheet has strong initial {0 0 0 2} texture, which resulted at the obvious anisotropy in high strain rate deformation at 20 °C. The anisotropy reflected in stress-strain curve, yield stress, peak stress and microstructure. The anisotropy became much weaker when the deformation temperature increased up to 250 °C. Continuing to increase the deformation temperature to 350 °C the anisotropy of AZ31 rolling sheet essentially disappeared. The decreasing tendency of anisotropy with increasing temperature was due to the fact that when the deformation temperature increased, the critical resolved shear stress (CRSS) for pyramidal 〈c + a〉 slip, which was the predominant slip mechanism for ND, decreased close to that of twinning, which was the predominant deformation mechanism for RD and TD. The deformation mechanism at different directions and temperatures and the Schmid factor (SF) at different directions were discussed in the present paper.

Modeling High Temperature Deformation Behavior of Large-Scaled Mg-Al-Zn Magnesium Alloy Fabricated by Semi-continuous Casting

NASA Astrophysics Data System (ADS)

Li, Jianping; Xia, Xiangsheng

2015-09-01

In order to improve the understanding of the hot deformation and dynamic recrystallization (DRX) behaviors of large-scaled AZ80 magnesium alloy fabricated by semi-continuous casting, compression tests were carried out in the temperature range from 250 to 400 °C and strain rate range from 0.001 to 0.1 s-1 on a Gleeble 1500 thermo-mechanical machine. The effects of the temperature and strain rate on the hot deformation behavior have been expressed by means of the conventional hyperbolic sine equation, and the influence of the strain has been incorporated in the equation by considering its effect on different material constants for large-scaled AZ80 magnesium alloy. In addition, the DRX behavior has been discussed. The result shows that the deformation temperature and strain rate exerted remarkable influences on the flow stress. The constitutive equation of large-scaled AZ80 magnesium alloy for hot deformation at steady-state stage (ɛ = 0.5) was The true stress-true strain curves predicted by the extracted model were in good agreement with the experimental results, thereby confirming the validity of the developed constitutive relation. The DRX kinetic model of large-scaled AZ80 magnesium alloy was established as X d = 1 - exp[-0.95((ɛ - ɛc)/ɛ*)2.4904]. The rate of DRX increases with increasing deformation temperature, and high temperature is beneficial for achieving complete DRX in the large-scaled AZ80 magnesium alloy.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Huang, Cindy Xiaohui; Lim, Chao Voon; Castagne, Sylvie

Titanium and its alloys have a wide range of applications in various industries such as aerospace, medical, automotive and even commercial products. However, formability of titanium alloys has always been an issue. This study presents the results of an investigation on the workability and response of Ti-6Al-4V deformed at different strain rates and lower elevated temperatures with different initial microstructures. Compression tests of cylindrical specimens were performed at various temperatures (300 deg. C, 400 deg. C, 450 deg. C, 500 deg. C) and at different strain rates (0.001 s{sup -1}, 0.02 s{sup -1} and 0.1 s{sup -1}). The effects ofmore » strain rate, temperature and initial microstructure on the workability of the Ti alloy were investigated. Based on these experimental results, workability maps for the respective initial microstructures were developed. Results showed that temperature played an important role in the formability of Ti-6Al-4V titanium alloys unlike strain rate. In addition, feasibility study on Multi-Directional Forging (MDF) was performed and positive results were obtained. It was demonstrated that Ti-6Al-4V titanium alloys can undergo severe plastic deformation at lower elevated temperature (400-500 deg. C) and at a higher strain rate of 0.1 s{sup -1}.« less

A numerical and experimental study of temperature effects on deformation behavior of carbon steels at high strain rates

NASA Astrophysics Data System (ADS)

Pouya, M.; Winter, S.; Fritsch, S.; F-X Wagner, M.

2017-03-01

Both in research and in the light of industrial applications, there is a growing interest in methods to characterize the mechanical behavior of materials at high strain rates. This is particularly true for steels (the most important structural materials), where often the strain rate-dependent material behavior also needs to be characterized in a wide temperature range. In this study, we use the Finite Element Method (FEM), first, to model the compressive deformation behavior of carbon steels under quasi-static loading conditions. The results are then compared to experimental data (for a simple C75 steel) at room temperature, and up to testing temperatures of 1000 °C. Second, an explicit FEM model that captures wave propagation phenomena during dynamic loading is developed to closely reflect the complex loading conditions in a Split-Hopkinson Pressure Bar (SHPB) - an experimental setup that allows loading of compression samples with strain rates up to 104 s-1 The dynamic simulations provide a useful basis for an accurate analysis of dynamically measured experimental data, which considers reflected elastic waves. By combining numerical and experimental investigations, we derive material parameters that capture the strain rate- and temperature-dependent behavior of the C75 steel from room temperature to 1000 °C, and from quasi-static to dynamic loading.

Associative Flow Rule Used to Include Hydrostatic Stress Effects in Analysis of Strain-Rate-Dependent Deformation of Polymer Matrix Composites

NASA Technical Reports Server (NTRS)

Goldberg, Robert K.; Roberts, Gary D.

2004-01-01

designing reliable composite engine cases that are lighter than the metal cases in current use. The types of polymer matrix composites that are likely to be used in such an application have a deformation response that is nonlinear and that varies with strain rate. The nonlinearity and the strain-rate dependence of the composite response are due primarily to the matrix constituent. Therefore, in developing material models to be used in the design of impact-resistant composite engine cases, the deformation of the polymer matrix must be correctly analyzed. However, unlike in metals, the nonlinear response of polymers depends on the hydrostatic stresses, which must be accounted for within an analytical model. By applying micromechanics techniques along with given fiber properties, one can also determine the effects of the hydrostatic stresses in the polymer on the overall composite deformation response. First efforts to account for the hydrostatic stress effects in the composite deformation applied purely empirical methods that relied on composite-level data. In later efforts, to allow polymer properties to be characterized solely on the basis of polymer data, researchers at the NASA Glenn Research Center developed equations to model the polymers that were based on a non-associative flow rule, and efforts to use these equations to simulate the deformation of representative polymer materials were reasonably successful. However, these equations were found to have difficulty in correctly analyzing the multiaxial stress states found in the polymer matrix constituent of a composite material. To correct these difficulties, and to allow for the accurate simulation of the nonlinear strain-rate-dependent deformation analysis of polymer matrix composites, in the efforts reported here Glenn researchers reformulated the polymer constitutive equations from basic principles using the concept of an associative flow rule. These revised equations were characterized and validated in an experimental program carried out through a university grant with the Ohio State University, wherein tensile and shear deformation data were obtained for a representative polymer for strain rates ranging from quasi-static to high rates of several hundred per second. Tensile deformation data also were obtained over a variety of strain rates and fiber orientation angles for a representative polymer matrix composite composed using the polymer.

Isolation and Characterization of Nisin-Resistant Leuconostoc mesenteroides for Use in Cabbage Fermentations

PubMed Central

Breidt, F.; Crowley, K. A.; Fleming, H. P.

1993-01-01

Leuconostoc mesenteroides strains that are resistant to high levels of nisin (up to 25,000 IU/ml in broth) were isolated. These nisin-resistant mutants were evaluated to determine their potential use as starter culture strains for cabbage fermentations. We found that some L. mesenteroides strains could be adapted to high levels of nisin resistance, while others could not. The nisin resistance trait was found to be stable for at least 35 generations, in the absence of nisin selection, for all mutants tested. The effects of nisin and salt, separately and in combination, on growth kinetics of the nisin-resistant strains were determined. Salt was the most influential factor on the specific growth rates of the mutants, and no synergistic effect between nisin and salt on specific growth rates was observed. The nisin-resistant strains were unimpaired in their ability to rapidly produce normal heterolactic fermentation end products. The use of these L. mesenteroides mutants as starter cultures in combination with nisin may extend the heterolactic phase of cabbage fermentations. PMID:16349090

Flame thickness and conditional scalar dissipation rate in a premixed temporal turbulent reacting jet

DOE Office of Scientific and Technical Information (OSTI.GOV)

Chaudhuri, Swetaprovo; Kolla, Hemanth; Dave, Himanshu L.

The flame structure corresponding to lean hydrogen–air premixed flames in intense sheared turbulence in the thin reaction zone regime is quantified from flame thickness and conditional scalar dissipation rate statistics, obtained from recent direct numerical simulation data of premixed temporally-evolving turbulent slot jet flames. It is found that, on average, these sheared turbulent flames are thinner than their corresponding planar laminar flames. Extensive analysis is performed to identify the reason for this counter-intuitive thinning effect. The factors controlling the flame thickness are analyzed through two different routes i.e., the kinematic route, and the transport and chemical kinetics route. The kinematicmore » route is examined by comparing the statistics of the normal strain rate due to fluid motion with the statistics of the normal strain rate due to varying flame displacement speed or self-propagation. It is found that while the fluid normal straining is positive and tends to separate iso-scalar surfaces, the dominating normal strain rate due to self-propagation is negative and tends to bring the iso-scalar surfaces closer resulting in overall thinning of the flame. The transport and chemical kinetics route is examined by studying the non-unity Lewis number effect on the premixed flames. The effects from the kinematic route are found to couple with the transport and chemical kinetics route. In addition, the intermittency of the conditional scalar dissipation rate is also examined. It is found to exhibit a unique non-monotonicity of the exponent of the stretched exponential function, conventionally used to describe probability density function tails of such variables. As a result, the non-monotonicity is attributed to the detailed chemical structure of hydrogen-air flames in which heat release occurs close to the unburnt reactants at near free-stream temperatures.« less

Flame thickness and conditional scalar dissipation rate in a premixed temporal turbulent reacting jet

DOE PAGES

Chaudhuri, Swetaprovo; Kolla, Hemanth; Dave, Himanshu L.; ...

2017-07-07

The flame structure corresponding to lean hydrogen–air premixed flames in intense sheared turbulence in the thin reaction zone regime is quantified from flame thickness and conditional scalar dissipation rate statistics, obtained from recent direct numerical simulation data of premixed temporally-evolving turbulent slot jet flames. It is found that, on average, these sheared turbulent flames are thinner than their corresponding planar laminar flames. Extensive analysis is performed to identify the reason for this counter-intuitive thinning effect. The factors controlling the flame thickness are analyzed through two different routes i.e., the kinematic route, and the transport and chemical kinetics route. The kinematicmore » route is examined by comparing the statistics of the normal strain rate due to fluid motion with the statistics of the normal strain rate due to varying flame displacement speed or self-propagation. It is found that while the fluid normal straining is positive and tends to separate iso-scalar surfaces, the dominating normal strain rate due to self-propagation is negative and tends to bring the iso-scalar surfaces closer resulting in overall thinning of the flame. The transport and chemical kinetics route is examined by studying the non-unity Lewis number effect on the premixed flames. The effects from the kinematic route are found to couple with the transport and chemical kinetics route. In addition, the intermittency of the conditional scalar dissipation rate is also examined. It is found to exhibit a unique non-monotonicity of the exponent of the stretched exponential function, conventionally used to describe probability density function tails of such variables. As a result, the non-monotonicity is attributed to the detailed chemical structure of hydrogen-air flames in which heat release occurs close to the unburnt reactants at near free-stream temperatures.« less

Matrix dominated stress/strain behavior in polymeric composites: Effects of hold time, nonlinearity and rate dependency

NASA Technical Reports Server (NTRS)

Gates, Thomas S.

1992-01-01

In order to understand matrix dominated behavior in laminated polymer matrix composites, an elastic/viscoplastic constitutive model was developed and used to predict stress strain behavior of off-axis and angle-ply symmetric laminates under in-plane, tensile axial loading. The model was validated for short duration tests at elevated temperatures. Short term stress relaxation and short term creep, strain rate sensitivity, and material nonlinearity were accounted for. The testing times were extended for longer durations, and periods of creep and stress relaxation were used to investigate the ability of the model to account for long term behavior. The model generally underestimated the total change in strain and stress for both long term creep and long term relaxation respectively.

Machining and grinding: High rate deformation in practice

DOE Office of Scientific and Technical Information (OSTI.GOV)

Follansbee, P.S.

1993-04-01

Machining and grinding are well-established material-working operations involving highly non-uniform deformation and failure processes. A typical machining operation is characterized by uncertain boundary conditions (e.g.,surface interactions), three-dimensional stress states, large strains, high strain rates, non-uniform temperatures, highly localized deformations, and failure by both nominally ductile and brittle mechanisms. While machining and grinding are thought to be dominated by empiricism, even a cursory inspection leads one to the conclusion that this results more from necessity arising out of the complicated and highly interdisciplinary nature of the processes than from the lack thereof. With these conditions in mind, the purpose of thismore » paper is to outline the current understanding of strain rate effects in metals.« less

Machining and grinding: High rate deformation in practice

DOE Office of Scientific and Technical Information (OSTI.GOV)

Follansbee, P.S.

1993-01-01

Machining and grinding are well-established material-working operations involving highly non-uniform deformation and failure processes. A typical machining operation is characterized by uncertain boundary conditions (e.g.,surface interactions), three-dimensional stress states, large strains, high strain rates, non-uniform temperatures, highly localized deformations, and failure by both nominally ductile and brittle mechanisms. While machining and grinding are thought to be dominated by empiricism, even a cursory inspection leads one to the conclusion that this results more from necessity arising out of the complicated and highly interdisciplinary nature of the processes than from the lack thereof. With these conditions in mind, the purpose of thismore » paper is to outline the current understanding of strain rate effects in metals.« less

Debond Analyses for Stitched Composite Structures

NASA Technical Reports Server (NTRS)

Glaessgen, E. H.; Raju, I. S.; Poe, C. C., Jr.

1998-01-01

The effect of stitching on mode I and mode II strain energy release rates for debond configurations is studied using an analysis based on plate finite elements and the virtual crack closure technique. The stitches were modeled as discrete nonlinear fastener elements with a compliance determined by experiment. The axial and shear behavior of the stitches was considered with both the compliances and failure loads assumed to be independent. The mode I strain energy release rate, G(sub I), was shown to decrease once the debond had grown beyond the first row of stitches and was reduced to zero for long debonds, however, the mode II strain energy release rate, G(sub II), continued to be of significant magnitude over the range of debond lengths considered.

relA-dependent RNA polymerase activity in Escherichia coli.

PubMed Central

Ryals, J; Bremer, H

1982-01-01

Parameters relating to RNA synthesis were measured after a temperature shift from 30 to 42 degrees C, in a relA+ and relA- isogenic pair of Escherichia coli strains containing a temperature-sensitive valyl tRNA synthetase. The following results were obtained: (i) the rRNA chain growth rate increased 2-fold in both strains; (ii) newly synthesized rRNA became unstable in both strains; (iii) the stable RNA gene activity (rRNA and tRNA, measured as stable RNA synthesis rate relative to the total instantaneous rate of RNA synthesis) decreased 1.7-fold in the relA+ strain and increased 1.9-fold in the relA mutant; and (iv) the RNA polymerase activity (measured by the percentage of total RNA polymerase enzyme active in transcription an any instant) decreased from 20 to 3.6% in the relA+ strain and remained unchanged (or increased at most to 22%) in the relA mutant. It is suggested that both rRNA gene activity and the RNA polymerase activity depend on the intracellular concentration of guanosine tetraphosphate, whereas the altered chain elongation rate and stability of rRNA are temperature or amino acid starvation effects, respectively, without involvement of relA function. PMID:6174501

Study of microstructure and fracture properties of blunt notched and sharp cracked high density polyethylene specimens.

PubMed

Pan, Huanyu; Devasahayam, Sheila; Bandyopadhyay, Sri

2017-07-21

This paper examines the effect of a broad range of crosshead speed (0.05 to 100 mm/min) and a small range of temperature (25 °C and 45 °C) on the failure behaviour of high density polyethylene (HDPE) specimens containing a) standard size blunt notch and b) standard size blunt notch plus small sharp crack - all tested in air. It was observed that the yield stress properties showed linear increase with the natural logarithm of strain rate. The stress intensity factors under blunt notch and sharp crack conditions also increased linearly with natural logarithm of the crosshead speed. The results indicate that in the practical temperature range of 25 °C and 45 °C under normal atmosphere and increasing strain rates, HDPE specimens with both blunt notches and sharp cracks possess superior fracture properties. SEM microstructure studies of fracture surfaces showed craze initiation mechanisms at lower strain rate, whilst at higher strain rates there is evidence of dimple patterns absorbing the strain energy and creating plastic deformation. The stress intensity factor and the yield strength were higher at 25 °C compared to those at 45 °C.

A slice of an aluminum particle: Examining grains, strain and reactivity

DOE PAGES

McCollum, Jena; Smith, Dylan K.; Hill, Kevin J.; ...

2016-09-12

The Combustion Institute Micron-scale aluminum (Al) particles are plagued by incomplete combustion that inhibits their reactivity. One approach to improving reactivity is to anneal Al particles to increase dilatational (volumetric) strain which has also been linked to increased combustion performance. While optimal annealing temperatures have been identified (roughly 300 °C), little is known about cooling rate effects on particle combustion performance. This study examines the effect of quenching after annealing Al microparticles to 100, 200 and 300 °C on intra-particle dilatational strain and reactivity. Synchrotron X-ray diffraction analysis of the particles reveals the cooling rates in the range from 0.007 to 0.38 K/smore » have little effect on the dilatational strain of the aluminum-core, alumina-shell particles. The annealed and quenched Al particles were then combined with a metal oxidizer (copper oxide) to examine reactivity. Flame propagation experiments follow the same trend: flame speeds are unchanged until a critical annealing temperature of 300 °C is reached and performance is maintained for each annealing temperature regardless of cooling rate. These results show that altering the mechanical properties and combustion performance of Al particles is strongly dependent on the annealing temperature and unchanged with variation in cooling rate. The contributions from elastic and plastic deformation mechanisms on strain are also considered and additional experimental results are shown on the microstructure of an Al particle. Focused ion beam milling of an Al particle to electron transparency was combined with transmission electron microscope imaging in order to examine the microstructure of the Al particles. This confirmed that the Al microparticles have a polycrystalline structure shown by grains all exceeding 100 nm in size.« less

Strain Rate Dependency of Bronze Metal Matrix Composite Mechanical Properties as a Function of Casting Technique

NASA Astrophysics Data System (ADS)

Brown, Lloyd; Joyce, Peter; Radice, Joshua; Gregorian, Dro; Gobble, Michael

2012-07-01

Strain rate dependency of mechanical properties of tungsten carbide (WC)-filled bronze castings fabricated by centrifugal and sedimentation-casting techniques are examined, in this study. Both casting techniques are an attempt to produce a functionally graded material with high wear resistance at a chosen surface. Potential applications of such materials include shaft bushings, electrical contact surfaces, and brake rotors. Knowledge of strain rate-dependent mechanical properties is recommended for predicting component response due to dynamic loading or impact events. A brief overview of the casting techniques for the materials considered in this study is followed by an explanation of the test matrix and testing techniques. Hardness testing, density measurement, and determination of the volume fraction of WC particles are performed throughout the castings using both image analysis and optical microscopy. The effects of particle filling on mechanical properties are first evaluated through a microhardness survey of the castings. The volume fraction of WC particles is validated using a thorough density survey and a rule-of-mixtures model. Split Hopkinson Pressure Bar (SHPB) testing of various volume fraction specimens is conducted to determine strain dependence of mechanical properties and to compare the process-property relationships between the two casting techniques. The baseline performances of C95400 bronze are provided for comparison. The results show that the addition of WC particles improves microhardness significantly for the centrifugally cast specimens, and, to a lesser extent, in the sedimentation-cast specimens, largely because the WC particles are more concentrated as a result of the centrifugal-casting process. Both metal matrix composites (MMCs) demonstrate strain rate dependency, with sedimentation casting having a greater, but variable, effects on material response. This difference is attributed to legacy effects from the casting process, namely, porosity and localized WC particle grouping.

Strain rate effects on the mechanical behavior of two Dual Phase steels in tension

NASA Astrophysics Data System (ADS)

Cadoni, E.; Singh, N. K.; Forni, D.; Singha, M. K.; Gupta, N. K.

2016-05-01

This paper presents an experimental investigation on the strain rate sensitivity of Dual Phase steel 1200 (DP1200) and Dual Phase steel 1400 (DP1400) under uni-axial tensile loads in the strain rate range from 0.001 s-1 to 600 s-1. These materials are advanced high strength steels (AHSS) having high strength, high capacity to dissipate crash energy and high formability. Flat sheet specimens of the materials having gauge length 10 mm, width 4 mm and thickness 2 mm (DP1200) and 1.25 mm (DP1400), are tested at room temperature (20∘C) on electromechanical universal testing machine to obtain their stress-strain relation under quasi-static condition (0.001 s-1), and on Hydro-Pneumatic machine and modified Hopkinson bar to study their mechanical behavior at medium (3 s-1, and 18 s-1) and high strain rates (200 s-1, 400 s-1, and 600 s-1) respectively. Tests under quasi-static condition are performed at high temperature (200∘C) also, and found that tensile flow stress is a increasing function of temperature. The stress-strain data has been analysed to determine the material parameters of the Cowper-Symonds and the Johnson-Cook models. A simple modification of the Johnson-Cook model has been proposed in order to obtain a better fit of tests at high temperatures. Finally, the fractographs of the broken specimens are taken by scanning electron microscope (SEM) to understand the fracture mechanism of these advanced high strength steels at different strain rates.

Geometrically nonlinear analysis of adhesively bonded joints

NASA Technical Reports Server (NTRS)

Dattaguru, B.; Everett, R. A., Jr.; Whitcomb, J. D.; Johnson, W. S.

1982-01-01

A geometrically nonlinear finite element analysis of cohesive failure in typical joints is presented. Cracked-lap-shear joints were chosen for analysis. Results obtained from linear and nonlinear analysis show that nonlinear effects, due to large rotations, significantly affect the calculated mode 1, crack opening, and mode 2, inplane shear, strain-energy-release rates. The ratio of the mode 1 to mode 2 strain-energy-relase rates (G1/G2) was found to be strongly affected by he adhesive modulus and the adherend thickness. The ratios between 0.2 and 0.8 can be obtained by varying adherend thickness and using either a single or double cracked-lap-shear specimen configuration. Debond growth rate data, together with the analysis, indicate that mode 1 strain-energy-release rate governs debond growth. Results from the present analysis agree well with experimentally measured joint opening displacements.

State Relationships of Laminar Permanently-Blue Opposed-Jet Hydrocarbon-Fueled Diffusion Flames. Appendix D

NASA Technical Reports Server (NTRS)

Lin, K.-C.; Faeth, G. M.; Urban, D. L. (Technical Monitor)

2000-01-01

The structure and state relationships of laminar soot-free (permanently-blue) diffusion flames at various strain rates were studied experimentally using an opposed-jet configuration, motivated by the importance of soot-free hydrocarbon-fueled diffusion flames for many practical applications. Measurements of gas velocities, temperatures and compositions were carried out along the stagnation stream line. Flame conditions studied included propylene- and 1,3-butadiene-fueled opposed-jet diffusion flames having a stoichiometric mixture fractions of 0.7 and strain rates of 60-240 s (exp -1) at normal temperature and pressure. It was found that oxygen leakage to fuel-rich conditions and carbon monoxide leakage to fuel-lean conditions both increased as strain rates increased. Furthermore, increased strain rates caused increased fuel concentrations near the flame sheet, decreased peak gas temperatures, and decreased concentrations of carbon dioxide and water vapor throughout the flames. State relationships for major gas species and gas temperatures for these flames were found to exist over broad ranges of strain rates. In addition, current measurements, as well as previous measurements and predictions of ethylene-fueled permanently-blue diffusion flames, all having a stoichiometric mixture fraction of 0.7, were combined to establish generalized state relationships for permanently-blue diffusion flames for this stoichiometric mixture fraction. The combined measurements and predictions support relatively universal generalized state relationships for N2, CO2, H2O and fuel over a broad range of strain rates and fuel types. State relationships for O2 in the fuel-rich region, and for CO in the fuel-lean region, however, are functions of strain rate and fuel type. State relationships for H2 and temperature exhibit less universality, mainly due to the increased experimental uncertainties for these variables. The existence of state relationships for soot-free hydrocarbon-fueled diffusion flames provides potential for significant computational simplifications for modeling purposes in many instances, allowing for effects of finite-rate chemistry while avoiding time-consuming computations of Arrhenius expressions.

Effects of Bacterial Host and Dichloromethane Dehalogenase on the Competitiveness of Methylotrophic Bacteria Growing with Dichloromethane

PubMed Central

Gisi, Daniel; Willi, Laurent; Traber, Hubert; Leisinger, Thomas; Vuilleumier, Stéphane

1998-01-01

Methylobacterium sp. strain DM4 and Methylophilus sp. strain DM11 can grow with dichloromethane (DCM) as the sole source of carbon and energy by virtue of homologous glutathione-dependent DCM dehalogenases with markedly different kinetic properties (the kcat values of the enzymes of these strains are 0.6 and 3.3 s−1, respectively, and the Km values are 9 and 59 μM, respectively). These strains, as well as transconjugant bacteria expressing the DCM dehalogenase gene (dcmA) from DM11 or DM4 on a broad-host-range plasmid in the background of dcmA mutant DM4-2cr, were investigated by growing them under growth-limiting conditions and in the presence of an excess of DCM. The maximal growth rates and maximal levels of dehalogenase for chemostat-adapted bacteria were higher than the maximal growth rates and maximal levels of dehalogenase for batch-grown bacteria. The substrate saturation constant of strain DM4 was much lower than the Km of its associated dehalogenase, suggesting that this strain is adapted to scavenge low concentrations of DCM. Strains and transconjugants expressing the DCM dehalogenase from strain DM11, on the other hand, had higher growth rates than bacteria expressing the homologous dehalogenase from strain DM4. Competition experiments performed with pairs of DCM-degrading strains revealed that a strain expressing the dehalogenase from DM4 had a selective advantage in continuous culture under substrate-limiting conditions, while strains expressing the DM11 dehalogenase were superior in batch culture when there was an excess of substrate. Only DCM-degrading bacteria with a dcmA gene similar to that from strain DM4, however, were obtained in batch enrichment cultures prepared with activated sludge from sewage treatment plants. PMID:9546153

Time-dependent brittle deformation (creep) at Mt. Etna volcano

NASA Astrophysics Data System (ADS)

Heap, M. J.; Baud, P.; Meredith, P. G.; Vinciguerra, S.; Bell, A. F.; Main, I. G.

2009-04-01

Mt. Etna is the largest and most active volcano in Europe. Time-dependent weakening mechanisms, leading to slow fracturing, have been shown to act during pre-eruptive patterns of flank eruptions at Mt. Etna volcano. Due to the high permeability of its volcanic rocks, the volcanic edifice hosts one of the biggest hydrogeologic reservoirs of Sicily (Ogniben, 1966). The presence of a fluid phase in cracks within rock has been shown to dramatically affect both mechanical and chemical interactions. Chemically, it promotes time-dependent brittle deformation through such mechanisms as stress corrosion cracking that allows rocks to deform at stresses far below their short-term failure strength. Such crack growth is highly non-linear and accelerates towards dynamic failure over extended periods of time, even under constant applied stress; a phenomenon known as ‘brittle creep'. Here we report results from a study of time-dependent brittle creep in water-saturated samples of Etna basalt (EB) under triaxial stress conditions (confining pressure of 50 MPa and pore fluid pressure of 20 MPa). Samples of EB were loaded at a constant strain rate of 10-5 s-1 to a pre-determined percentage of the short-term strength and left to deform under constant stress until failure. Crack damage evolution was monitored throughout each experiment by measuring the independent damage proxies of axial strain, pore volume change and output of acoustic emission (AE) energy, during brittle creep of creep strain rates ranging over four orders of magnitude. Our data not only demonstrates that basalt creeps in the brittle regime but also that the applied differential stress exerts a crucial influence on both time-to-failure and creep strain rate in EB. Furthermore, stress corrosion is considered to be responsible for the acceleratory cracking and seismicity prior to volcanic eruptions and is invoked as an important mechanism in forecasting models. Stress-stepping creep experiments were then performed to allow the influence of the effective confining stress to be studied in detail. Experiments were performed under effective stress conditions of 10, 30 and 50 MPa (whilst maintaining a constant pore fluid pressure of 20 MPa). In addition to the purely mechanical influence of water, governed by the effective stress, which results in a shift of the creep strain rate curves to lower strain rates at higher effective stresses. Our results also demonstrate that the chemically-driven process of stress corrosion cracking appears to be inhibited at higher effective stress. This results in an increase in the gradient of the creep strain rate curves with increasing effective stress. We suggest that the most likely cause of this change is a decrease in water mobility due to a reduction in crack aperture and an increase in water viscosity at higher pressure. Finally, we show that a theoretical model based on mean-field damage mechanics creep laws is able to reproduce the experimental strain-time relations. Our results indicate that the local changes in the stress field and fluid circulation can have a profound impact in the time-to-failure properties of the basaltic volcanic pile.

Time-dependent Brittle Deformation in Etna Basalt

NASA Astrophysics Data System (ADS)

Heap, M. J.; Baud, P.; Meredith, P. G.; Vinciguerra, S.; Bell, A. F.; Main, I. G.

2008-12-01

Mt Etna is the largest and most active volcano in Europe. Due to the high permeability of its volcanic rocks, the volcanic edifice hosts one of the biggest hydrogeologic reservoirs of Sicily (Ogniben, 1966). Pre-eruptive patterns of flank eruptions, closely monitored by means of ground deformation and seismicity, revealed the slow development of fracture systems at different altitudes, marked by repeated bursts of seismicity and accelerating/decelerating deformation patterns acting over the scale of months to days. The presence of a fluid phase in cracks within rock has been shown to dramatically affect both mechanical and chemical interactions. Chemically, it promotes time-dependent brittle deformation through such mechanisms as stress corrosion cracking that allows rocks to deform at stresses far below their short-term failure strength. Such crack growth is highly non-linear and accelerates towards dynamic failure over extended periods of time, even under constant applied stress; a phenomenon known as 'brittle creep'. Stress corrosion is considered to be responsible for the acceleratory cracking and seismicity prior to volcanic eruptions and is invoked as an important mechanism in forecasting models. Here we report results from a study of time-dependent brittle creep in water-saturated samples of Etna basalt (EB) under triaxial stress conditions (confining pressure of 50 MPa and pore fluid pressure of 20 MPa). Samples of EB were loaded at a constant strain rate of 10-5 s-1 to a pre-determined percentage of the short- term strength and left to deform under constant stress until failure. Crack damage evolution was monitored throughout each experiment by measuring the independent damage proxies of axial strain, pore volume change and output of acoustic emission (AE) energy, during brittle creep of creep strain rates ranging over four orders of magnitude. Our data demonstrate that the applied differential stress exerts a crucial influence on both time-to-failure and creep strain rate in EB. Stress-stepping creep experiments were then performed to allow the influence of the effective confining stress to be studied in detail. Experiments were performed under effective stress conditions of 10, 30 and 50 MPa (whilst maintaining a constant pore fluid pressure of 20 MPa). In addition to the purely mechanical influence of water, governed by the effective stress, which results in a shift of the creep strain rate curves to lower strain rates at higher effective stresses. Our results also demonstrate that the chemically-driven process of stress corrosion cracking appears to be inhibited at higher effective stress. This results in an increase in the gradient of the creep strain rate curves with increasing effective stress. We suggest that the most likely cause of this change is a decrease in water mobility due to a reduction in crack aperture and an increase in water viscosity at higher pressure. Finally, we show that a theoretical model based on mean-field damage mechanics creep laws is able to reproduce the experimental strain-time relations. Our results indicate that the local changes in the stress field and fluid circulation can have a profound impact in the time- to-failure properties of the basaltic volcanic pile.

Time-dependent brittle deformation at Mt. Etna volcano

NASA Astrophysics Data System (ADS)

Baud, Patrick; Heap, Michael; Meredith, Philip; Vinciguerra, Sergio; Bell, Andrew; Main, Ian

2010-05-01

Time-dependent weakening mechanisms, leading to slow fracturing, are likely to act during the build up to flank eruptions at Mt. Etna volcano and are potentially a primary control on pre-eruptive patterns of seismicity and deformation. Due to the high permeability of its volcanic rocks, the volcanic edifice hosts a large water reservoir (Ogniben, 1966). The presence of a fluid phase in cracks within rock has been shown to dramatically affect both mechanical and chemical interactions. Chemically, it promotes time-dependent brittle deformation through such mechanisms as stress corrosion cracking that allows rocks to deform at stresses far below their short-term failure strength. Such crack growth is highly non-linear and accelerates towards dynamic failure over extended periods of time, even under constant applied stress; a phenomenon known as ‘brittle creep'. Here we report results from a study of time-dependent brittle creep in water-saturated samples of Etna basalt (EB) under triaxial stress conditions (confining pressure of 50 MPa and pore fluid pressure of 20 MPa). Samples of EB were loaded at a constant strain rate of 10-5 s-1 to a pre-determined percentage of the short-term strength and left to deform under constant stress until failure. Crack damage evolution was monitored throughout each experiment by measuring the independent damage proxies of axial strain, pore volume change and output of acoustic emission (AE) energy, during brittle creep of creep strain rates ranging over four orders of magnitude. Our data not only demonstrates that basalt creeps in the brittle regime but also that the applied differential stress exerts a crucial influence on both time-to-failure and creep strain rate in EB. Furthermore, stress corrosion is considered to be responsible for the acceleratory cracking and seismicity prior to volcanic eruptions and is invoked as an important mechanism in forecasting models. Stress-stepping creep experiments were then performed to allow the influence of the effective confining stress to be studied in detail. Experiments were performed under effective stress conditions of 10, 30 and 50 MPa (whilst maintaining a constant pore fluid pressure of 20 MPa). In addition to the purely mechanical influence of water, governed by the effective stress, which results in a shift of the creep strain rate curves to lower strain rates at higher effective stresses. Our results also demonstrate that the chemically-driven process of stress corrosion cracking appears to be inhibited at higher effective stress. This results in an increase in the gradient of the creep strain rate curves with increasing effective stress. We suggest that the most likely cause of this change is a decrease in water mobility due to a reduction in crack aperture and an increase in water viscosity at higher pressure. Finally, we show that a theoretical model based on mean-field damage mechanics creep laws is able to reproduce the experimental strain-time relations and inverse seismicity plots using our experimental AE data. Our results indicate that the local changes in the stress field and fluid circulation can have a profound impact in the time-to-failure properties of the basaltic volcanic pile.

Manufacture of gradient micro-structures of magnesium alloys using two stage extrusion dies

DOE Office of Scientific and Technical Information (OSTI.GOV)

Hwang, Yeong-Maw; Huang, Tze-Hui; Alexandrov, Sergei

2013-12-16

This paper aims to manufacture magnesium alloy metals with gradient micro-structures using hot extrusion process. The extrusion die was designed to have a straight channel part combined with a conical part. Materials pushed through this specially-designed die generate a non-uniform velocity distribution at cross sections inside the die and result in different strain and strain rate distributions. Accordingly, a gradient microstructure product can be obtained. Using the finite element analysis, the forming temperature, effective strain, and effective strain rate distributions at the die exit were firstly discussed for various inclination angles in the conical die. Then, hot extrusion experiments withmore » a two stage die were conducted to obtain magnesium alloy products with gradient micro-structures. The effects of the inclination angle on the grain size distribution at cross sections of the products were also discussed. Using a die of an inclination angle of 15°, gradient micro-structures of the grain size decreasing gradually from 17 μm at the center to 4 μm at the edge of product were achieved.« less

Atomistic simulations to characterize the influence of applied strain and PKA energy on radiation damage evolution in pure aluminum

NASA Astrophysics Data System (ADS)

Sahi, Qurat-ul-ain; Kim, Yong-Soo

2018-05-01

Knowledge of defects generation, their mobility, growth rate, and spatial distribution is the cornerstone for understanding the surface and structural evolution of a material used under irradiation conditions. In this study, molecular dynamics simulations were used to investigate the coupled effect of primary knock-on atom (PKA) energy and applied strain (uniaxial and hydrostatic) fields on primary radiation damage evolution in pure aluminum. Cascade damage simulations were carried out for PKA energy ranging between 1 and 20 keV and for applied strain values ranging between -2% and 2% at the fixed temperature of 300 K. Simulation results showed that as the atomic displacement cascade proceeds under uniaxial and hydrostatic strains, the peak and surviving number of Frenkel point defects increases with increasing tension; however, these increments were more prominent under larger volume changing deformations (hydrostatic strain). The percentage fraction of point defects that aggregate into clusters increases under tension conditions; compared to the reference conditions with no strain, these increases are around 13% and 7% for interstitials and vacancies, respectively (under 2% uniaxial strain), and 19% and 11% for interstitials and vacancies, respectively (under 2% hydrostatic strain). Clusters formed of vacancies and interstitials were both larger under tensile strain conditions, with increases in both the average and maximum cluster sizes. The rate of increase/decrease in the number of Frenkel pairs, their clustering, and their size distributions under expansion/compression strain conditions were higher for higher PKA energies. Overall, the present results suggest that strain effects should be considered carefully in radiation damage environments, specifically for conditions of low temperature and high radiation energy. Compressive strain conditions could be beneficial for materials used in nuclear reactor power systems.

Effective temperature dynamics of shear bands in metallic glasses

NASA Astrophysics Data System (ADS)

Daub, Eric G.; Klaumünzer, David; Löffler, Jörg F.

2014-12-01

We study the plastic deformation of bulk metallic glasses with shear transformation zone (STZ) theory, a physical model for plasticity in amorphous systems, and compare it with experimental data. In STZ theory, plastic deformation occurs when localized regions rearrange due to applied stress and the density of these regions is determined by a dynamically evolving effective disorder temperature. We compare the predictions of STZ theory to experiments that explore the low-temperature deformation of Zr-based bulk metallic glasses via shear bands at various thermal temperatures and strain rates. By following the evolution of effective temperature with time, strain rate, and temperature through a series of approximate and numerical solutions to the STZ equations, we successfully model a suite of experimentally observed phenomena, including shear-band aging as apparent from slide-hold-slide tests, a temperature-dependent steady-state flow stress, and a strain-rate- and temperature-dependent transition from stick-slip (serrated flow) to steady-sliding (nonserrated flow). We find that STZ theory quantitatively matches the observed experimental data and provides a framework for relating the experimentally measured energy scales to different types of atomic rearrangements.

Demonstration test of burner liner strain measurements using resistance strain gages

NASA Technical Reports Server (NTRS)

Grant, H. P.; Anderson, W. L.

1984-01-01

A demonstration test of burner liner strain measurements using resistance strain gages as well as a feasibility test of an optical speckle technique for strain measurement are presented. The strain gage results are reported. Ten Kanthal A-1 wire strain gages were used for low cycle fatigue strain measurements to 950 K and .002 apparent strain on a JT12D burner can in a high pressure (10 atmospheres) burner test. The procedure for use of the strain gages involved extensive precalibration and postcalibration to correct for cooling rate dependence, drift, and temperature effects. Results were repeatable within + or - .0002 to .0006 strain, with best results during fast decels from 950 K. The results agreed with analytical prediction based on an axisymmetric burner model, and results indicated a non-uniform circumferential distribution of axial strain, suggesting temperature streaking.

Control of bone remodelling by applied dynamic loads

NASA Technical Reports Server (NTRS)

Lanyon, L. E.; Rubin, C. T.

1984-01-01

The data showing the relationship between bone mass and peak strain magnitude prepared and submitted for publication. The data from experiments relating remodelling activity with static or dynamic loads were prepared and submitted for publication. Development of programs to relate the location of remodelling activity with he natural and artificial dynamic strain distributions continued. Experiments on the effect of different strain rates on the remodelling response continued.

Effects of juvenile hormone analog formulations on development and reproduction in the bed bug Cimex lectularius (Hemiptera: Cimicidae).

PubMed

Goodman, Mark H; Potter, Michael F; Haynes, Kenneth F

2013-02-01

Bed bugs (Cimex lectularius L.) have become a common insect pest in urban areas and are often difficult to manage. Eradication is made more problematic by widespread insecticide resistance, raising interest in alternative control products. Juvenile hormone analogs (JHAs) such as methoprene and hydroprene are relatively harmless to non-arthropods and have proved to be effective against other urban insect pests. Two JHA products (Gentrol(®) and Precor(®), Central Life Sciences, Schaumburg, IL) were tested for efficacy against various bed bug stages as direct spray and as dry residue using three bed bug strains. At 1× and 2× the label rate, Precor(®) [active ingredient (S)-methoprene] had no significant effect on the development or fecundity of bed bugs. At 2× the label rate, confinement to residues of Gentrol(®) [active ingredient (S)-hydroprene] had no significant effect, but residues at 3× and 10× the label rate caused a reduction in fecundity and impaired development. Field strains were more susceptible to the reproductive effects of (S)-hydroprene than a long-maintained laboratory strain. While JHAs are attractive alternatives for pest management because of their inherent safety and distinct mode of action, these JHA formulations would have little impact on bed bug populations without relabeling to allow for higher application rates. Copyright © 2012 Society of Chemical Industry.

Job strain in the public sector and hospital in-patient care use in old age: a 28-year prospective follow-up.

PubMed

von Bonsdorff, Mikaela Birgitta; von Bonsdorff, Monika; Kulmala, Jenni; Törmäkangas, Timo; Seitsamo, Jorma; Leino-Arjas, Päivi; Nygård, Clas-Håkan; Ilmarinen, Juhani; Rantanen, Taina

2014-05-01

high job strain increases the risk of health decline, but little is known about the specific consequences and long-term effects of job strain on old age health. purpose was to investigate whether physical and mental job strain in midlife was associated with hospital care use in old age. study population included 5,625 Finnish public sector employees aged 44-58 years who worked in blue- and white-collar professions in 1981. The number of in-patient hospital care days was collected from the Finnish Hospital Discharge Register for the 28-year follow-up period. rates of hospital care days per 1,000 person-years for men were 7.78 (95% confidence interval [CI] 7.71-7.84) for low, 9.68 (95% CI 9.50-9.74) for intermediate and 12.56 (95% CI 12.47-12.66) for high physical job strain in midlife. The corresponding rates for women were 6.63 (95% CI 6.57-6.68), 7.91 (95% CI 7.87-7.95) and 10.35 (95% CI 10.25-10.42), respectively. Rates were parallel but lower for mental job strain. Reporting high physical job strain in midlife increased the risk of hospital care in old age compared with those who reported low job strain, fully adjusted incidence rate ratio 1.17 (95% CI 1.00-1.38) for men and 1.42 (95% CI 1.25-1.61) for women. These associations were robust in analyses confined to hospital care that took place after the employees had turned 65 years. exposure to high mental and, particularly, high physical job strain in midlife may set employees on a higher healthcare use trajectory which persists into old age.

Biocontrol Agents Increase the Specific Rate of Patulin Production by Penicillium expansum but Decrease the Disease and Total Patulin Contamination of Apples

PubMed Central

Zheng, Xiangfeng; Yang, Qiya; Zhang, Xiaoyun; Apaliya, Maurice T.; Ianiri, Giuseppe; Zhang, Hongyin; Castoria, Raffaello

2017-01-01

Synthetic fungicides are commonly employed for the control of postharvest diseases of fruits. However, due to health concerns about the use of these chemicals, alternative control methods including biocontrol based on antagonistic yeasts are gaining in popularity. In this study, we investigated the effects of two biocontrol yeasts, Rhodotorula mucilaginosa strain 3617 and Rhodotorula kratochvilovae strain LS11, on blue mold and patulin (PAT) contamination caused by Penicillium expansum strains PY and FS7 in artificially inoculated Fuji apples stored at 20°C for 9 days. To correlate the development of the P. expansum strains in yeast-treated and untreated apples with PAT production, we quantified their biomass in the infected fruits using a recently published quantitative real-time polymerase chain reaction method based on specific primers for patF, a gene from P. expansum that is involved in PAT biosynthesis. Both yeasts significantly reduced the disease incidence caused by the two strains of P. expansum up to 5–7 days of incubation, and lowered their biomass and the progression of symptoms up to 9 days. Interestingly, both yeasts strains increased the rate of PAT production (expressed as ng patulin/μg fungal DNA) by the two pathogenic strains. Nevertheless, both biocontrol agents reduced the total PAT contamination, especially in the case of P. expansum strain FS7, the higher PAT producer of the two tested P. expansum strains. Comparing between the yeast strains, R. kratochvilovae LS11 was more effective than R. mucilaginosa 3617 for the control of P. expansum. PMID:28713362

Wheat Bran Enhances the Cytotoxicity of Immobilized Alcaligenes aquatilis F8 against Microcystis aeruginosa

PubMed Central

Sun, Pengfei; Lin, Hui; Wang, Guan; Zhang, Ximing; Zhang, Qichun; Zhao, Yuhua

2015-01-01

Algicidal bacteria offer a promising option for killing cyanobacteria. Therefore, a new Alcaligenes aquatilis strain F8 was isolated to control Microcystis aeruginosa in this study. The algicidal activity of strain F8 was dependent on the cell density of M. aeruginosa, and the maximal algicidal rate of the free bacterium reached 88.45% within 72 h. With a view to its application to the control of M. aeruginosa in the natural environment, strain F8 was immobilized in sodium alginate beads, but immobilization of the strain decreased its algicidal rate compared to that of the free bacterium. However, addition of wheat bran to the sodium alginate matrix used to immobilize strain F8 not only eliminated the adverse effects of immobilization on the bacteria but also resulted in an 8.83% higher algicidal rate of the immobilized than free bacteria. Exclusion and recovery methods were used to identify key ingredients of wheat bran and gain insight into the mechanism underlying the observed enhancement of algicidal activity. This analysis indicated that certain factors in wheat bran, including vitamins B1, B2, B9, and E were responsible for promoting bacterial growth and thereby improving the algicidal rate of immobilized strain F8. Our findings indicate that wheat bran is able to improve the algicidal efficiency of A. aquatilis strain F8 for killing M. aeruginosa and is a good source of not only carbon and nitrogen but also vitamins for bacteria. PMID:26295573

The strain-rate sensitivity of high-strength high-toughness steels.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Dilmore, M.F.; Crenshaw, Thomas B.; Boyce, Brad Lee

2006-01-01

The present study examines the strain-rate sensitivity of four high strength, high-toughness alloys at strain rates ranging from 0.0002 s-1 to 200 s-1: Aermet 100, a modified 4340, modified HP9-4-20, and a recently developed Eglin AFB steel alloy, ES-1c. A refined dynamic servohydraulic method was used to perform tensile tests over this entire range. Each of these alloys exhibit only modest strain-rate sensitivity. Specifically, the strain-rate sensitivity exponent m, is found to be in the range of 0.004-0.007 depending on the alloy. This corresponds to a {approx}10% increase in the yield strength over the 7-orders of magnitude change in strain-rate.more » Interestingly, while three of the alloys showed a concominant {approx}3-10% drop in their ductility with increasing strain-rate, the ES1-c alloy actually exhibited a 25% increase in ductility with increasing strain-rate. Fractography suggests the possibility that at higher strain-rates ES-1c evolves towards a more ductile dimple fracture mode associated with microvoid coalescence.« less

Effects of {10-12} Twins on Dynamic Torsional Properties of Extruded AZ31 Magnesium Alloy

NASA Astrophysics Data System (ADS)

Lee, Jong Un; Song, Seok Weon; Kim, Yongjin; Kim, Sang-Hoon; Kim, Ye Jin; Park, Sung Hyuk

2018-03-01

Effects of initial twins on dynamic torsional properties of extruded AZ31 alloy were investigated by introducing {10-12} twins into it through precompression to 3 and 6% strains along the extrusion direction and performing torsional testing at a strain rate of 1.4 × 103 s-1 using a torsional Kolsky bar system. The as-extruded sample without twins showed higher dynamic torsional properties than the precompressed samples with many initial twins; the maximum shear strength and fracture shear strain decreased with increasing amount of initial twins. In the as-extruded sample, twinning occurred vigorously throughout the gage section of the tubular specimen during high-strain-rate torsional tests, resulting in heavily deformed morphology, many macrocracks, and rough fractured surfaces. The increased amount of initial twins suppressed the twinning behavior and localized the applied torsional deformation; this resulted in an almost unchanged sample shape, no secondary cracks, and a flat fracture plane, thereby deteriorating the dynamic torsional properties of the extruded alloy.

Static Recrystallization Behavior of Z12CN13 Martensite Stainless Steel

NASA Astrophysics Data System (ADS)

Luo, Min; Zhou, Bing; Li, Rong-bin; Xu, Chun; Guo, Yan-hui

2017-09-01

In order to increase the hot workability and provide proper hot forming parameters of forging Z12CN13 martensite stainless steel for the simulation and production, the static recrystallization behavior has been studied by double-pass hot compression tests. The effects of deformation temperature, strain rate and inter-pass time on the static recrystallization fraction by the 2% offset method are extensively studied. The results indicate that increasing the inter-pass time and the deformation temperature as well as strain rate appropriately can increase the fraction of static recrystallization. At the temperature of 1050-1150 °C, inter-pass time of 30-100 s and strain rate of 0.1-5 s-1, the static recrystallization behavior is obvious. In addition, the kinetics of static recrystallization behavior of Z12CN13 steel has been established and the activation energy of static recrystallization is 173.030 kJ/mol. The substructure and precipitates have been studied by TEM. The results reveal that the nucleation mode is bulging at grain boundary. Undissolved precipitates such as MoNi3 and Fe3C have a retarding effect on the recrystallization kinetics. The effect is weaker than the accelerating effect of deformation temperature.

Improved cider fermentation performance and quality with newly generated Saccharomyces cerevisiae × Saccharomyces eubayanus hybrids.

PubMed

Magalhães, Frederico; Krogerus, Kristoffer; Vidgren, Virve; Sandell, Mari; Gibson, Brian

2017-08-01

Yeast cryotolerance may be advantageous for cider making, where low temperatures are usually employed. Here, we crossed the cryotolerant S. eubayanus with a S. cerevisiae wine strain and assessed the suitability of the hybrids for low-temperature cider fermentation. All strains fermented the juice to 5% ABV, but at different rates; hybrid strains outperformed S. cerevisiae, which was sensitive to low temperatures. The best hybrid fermented similarly to S. eubayanus. S. eubayanus produced sulphurous off flavours which masked a high concentration of fruity ester notes. This phenotype was absent in the hybrid strains, resulting in distinctly fruitier ciders. Aroma was assessed by an independent consumer panel, which rated the hybrid ciders as identical to the wine strain cider. Both were significantly more pleasant than the S. eubayanus cider. Interspecific hybridization can apparently be used effectively to improve low-temperature fermentation performance without compromising product quality.

Mapping the ductile-brittle transition of magma

NASA Astrophysics Data System (ADS)

Kendrick, J. E.; Lavallee, Y.; Dingwell, D. B.

2010-12-01

During volcanic unrest, eruptive activity can switch rapidly from effusive to explosive. Explosive eruptions require the fragmentation of magma, in which, if deformation rate is too fast to be relaxed, magma undergoes a transition in deformation mechanism from viscous and/or ductile to brittle. Our knowledge of the deformation mechanisms of magma ascent and eruption remains, to date, poor. Many studies have constrained the glass transition (Tg) of the interstitial melt phase; yet the effect of crystals and bubbles are unresolved. During ascent, magma undergoes P-T changes which induce crystallization, thereby inducing a transition from viscous to ductile and, in some cases, to brittle deformation. Here, we explore the deformation mechanisms of magma involved in the dome-building eruptions and explosions that occurred at Volcán de Colima (Mexico) since 1998. For this purpose, we investigated the rheology of dome lavas, containing 10-45 vol.% rhyolitic interstitial melt, 55-90 vol.% crystals and 5-20 vol.% bubbles. The interstitial glass is characterized by electron microprobe and Tg is characterized using a differential scanning calorimeter and a dilatometer. The population of crystals (fraction, shape and size distribution) is described optically and quantified using ImageJ and AMOCADO. The rheological effects of crystals on the deformation of magmas are constrained via acoustic emission (AE) and uniaxial deformation experiments at temperature above Tg (900-980 °C) and at varied applied stresses (and strain rates: 10-6 to 10-2 s-1). The ratio of ductile to brittle deformation across the ductile-brittle transition is quantified using the output AE energy and optical and SEM analysis. We find that individual dome lava sample types have different mechanical responses, yielding a significant range of measured strain rates under a given temperature and applied stress. Optical analysis suggests that at low strain rates, ductile deformation is mainly controlled by the groundmass, whereas fractures initiate sporadically in phenocrysts. At high strain rates continuous fracture initiate in the phenocrysts and propagate through the groundmass. AE analysis suggests the ductile-brittle transition to approximate two orders of magnitude of strain rate and that it is temperature dependent. Within the transition, the different ratio of ductile to brittle deformation processes controls the strain to failure. This study shows that the presence of crystals widens the range of strain rates of the ductile-brittle transition and the failure of magma becomes dependent on total strain. Our findings will be discussed in the context of different eruptive scenarios.

Acoustic Emission Characteristics of Red Sandstone Specimens Under Uniaxial Cyclic Loading and Unloading Compression

NASA Astrophysics Data System (ADS)

Meng, Qingbin; Zhang, Mingwei; Han, Lijun; Pu, Hai; Chen, Yanlong

2018-04-01

To explore the acoustic emission (AE) characteristics of rock materials during the deformation and failure process under periodic loads, a uniaxial cyclic loading and unloading compression experiment was conducted based on an MTS 815 rock mechanics test system and an AE21C acoustic emissions test system. The relationships among stress, strain, AE activity, accumulated AE activity and duration for 180 rock specimens under 36 loading and unloading rates were established. The cyclic AE evolutionary laws with rock stress-strain variation at loading and unloading stages were analyzed. The Kaiser and Felicity effects of rock AE activity were disclosed, and the impact of the significant increase in the scale of AE events on the Felicity effect was discussed. It was observed that the AE characteristics are closely related to the stress-strain properties of rock materials and that they are affected by the developmental state and degree of internal microcracks. AE events occur in either the loading or unloading stages if the strain is greater than zero. Evolutionary laws of AE activity agree with changes in rock strain. Strain deformation is accompanied by AE activity, and the density and intensity of AE events directly reflect the damage degree of the rock mass. The Kaiser effect exists in the linear elastic stage of rock material, and the Felicity effect is effective in the plastic yield and post-peak failure stages, which are divided by the elastic yield strength. This study suggests that the stress level needed to determine a significant increase in AE activity was 70% of the i + 1 peak stress. The Felicity ratio of rock specimens decreases with the growth of loading-unloading cycles. The cycle magnitude and variation of the Felicity effect, in which loading and unloading rates play a weak role, are almost consistent.

Strain Hardening Behaviour and Its Effect on Properties of ZrB2 Reinforced Al Composite Prepared by Powder Metallurgy Technique

NASA Astrophysics Data System (ADS)

Kaku, Sai Mahesh Yadav; Khanra, Asit Kumar; Davidson, M. J.

2018-04-01

Strain hardening behaviour has significant effect on altering the properties of materials. In the present study, Al-ZrB2 metal matrix composites are made through powder metallurgy route. Incremental weight percentage (wt%) of ZrB2 (0, 2, 4 and 6 wt%) are added to Aluminium matrix to produce different composites. The homogenous powder mixture is compacted and pressurelessly sintered. Sintering of composites is performed over a range of 450-575 °C. The optimized sintered condition is observed at 550 °C for 1 h in controlled atmosphere (argon gas flow). The sintered compacts are strained in incremental steps in different levels up to failure. A visible crack on the bulge of the powder preform is considered as the failure. Composites are strain hardened up to failure. To evaluate the effect of temperature on strain hardening, strain hardening is carried out at different temperatures. Composites are densified with the extent of straining and hardness increases with the increase of strain. Hardness increase with the increase in temperature is maintained during strain hardening. To evaluate the corrosion behaviour of Al-ZrB2 composite, potentiodynamic polarization study are performed on the strained composites. Corrosion rate decrease with the extent of straining.

Observations of Dynamic Strain Aging in Polycrystalline NiAl

NASA Technical Reports Server (NTRS)

Weaver, M. L.; Noebe, R. D.; Kaufman, M. J.

1996-01-01

Dynamic strain aging has been investigated at temperatures between 77 and 1100 K in eight polycrystalline NiAl alloys. The 0.2% offset yield stress and work hardening rates for these alloys generally decreased with increasing temperature. However, local plateaus or maxima were observed in conventional purity and carbon doped alloys at intermediate temperatures (600-900 K). This anomalous behavior was not observed in low interstitial high-purity, nitrogen doped, or in titanium doped materials. Low or negative strain rate sensitivities (SRS) were also observed in all eight alloys in this intermediate temperature range. Coincident with the occurrence of negative SRS was the occurrence of serrated flow in conventional purity alloys containing high concentrations of Si in addition to C. These phenomena have been attributed to dynamic strain aging (DSA). Chemical analysis of the alloys used in this study suggests that the main species causing strain aging in polycrystalline NiAl is C but indicate that residual Si impurities can enhance the strain aging effect.

Comparison of strain rates of dart impacted plaques and pendulum impacted bumpers

DOE Office of Scientific and Technical Information (OSTI.GOV)

Scammell, K.L.

1987-01-01

The difference in strain rates prevailing during pendulum impact of bumpers versus high speed dart impact of plaques was investigated. Uni-axial strain gages were applied to the tension side of the plaques and bumpers directly opposite the point of impact. The plaques were impacted with an instrumented high rate dart impact tester and the bumpers impacted with a full scale bumper pendulum impact tester. Theoretical calculations and actual strain rate data support the conclusion that the strain rate of a plaque during dart impact significantly exceeds that of bumper strain rate during pendulum impact.

Preliminary report on the biological effects of space flight on the producing strain of a new immunosuppressant, Kanglemycin C.

PubMed

Zhou, Jianqin; Sun, Chenghang; Wang, Nanjin; Gao, Rongmei; Bai, Shuoke; Zheng, Huanrong; You, Xuefu; Li, Rongfeng

2006-08-01

Kanglemycin C (K-C) is a new immunosuppressant isolated from the culture broth of Nocardia mediterranei var. kanglensis 1747-64. To improve the productivity of K-C and to study the biological effects of space flight on its producing strain, spores from five K-C producing strains (U-10, U-15, U-7, M-13, gamma-33) mutated from the wild strain N. mediterranei var. kanglensis 1747-64 were carried into space by an unmanned spaceship, "Shenzhou III" (Divine Vessel III) on March 25, 2002. Comparatively, the strain U-7 was the highest K-C producing strain among the above five starting strains when cultivated in 500-ml Erlenmeyer flasks. After a 6 day and 18 h flight, the treated spores went through serial screening processes to screen for high-yield K-C mutant strains, using thin layer chromatography and high performance liquid chromatography (HPLC). The K-C yield produced by one mutant strain, designated as F-16, derived from the starting strain U-7 was increased by up to 200% when compared to that produced by the starting strain U-7 in 500-ml Erlenmeyer flasks after careful postflight HPLC analysis. Another mutant strain, designated as F-210, derived from the starting strain M-13 showed reduced productivity of K-C as well as exhibited changes in some morphological and physiological characteristics. For example, the broth color of the strain F-210 changed from yellow to purple after 96 h of culture, but that of the ground control strain M-13 remained yellow. Similarly, the mycelium morphological change from filamentous to coccoid of F-210 occurred later than that of ground control M-13. Examination of the survivability of postflight spores indicated that exposure to radiation, during the 162 h of space flight, plays a critical role in the survival rates of spores such that spores exposed to strong radiation exhibited lower survival rates than spores exposed to weak radiation.

Power-law viscous materials for analogue experiments: New data on the rheology of highly-filled silicone polymers

NASA Astrophysics Data System (ADS)

Boutelier, D.; Schrank, C.; Cruden, A.

2008-03-01

The selection of appropriate analogue materials is a central consideration in the design of realistic physical models. We investigate the rheology of highly-filled silicone polymers in order to find materials with a power-law strain-rate softening rheology suitable for modelling rock deformation by dislocation creep and report the rheological properties of the materials as functions of the filler content. The mixtures exhibit strain-rate softening behaviour but with increasing amounts of filler become strain-dependent. For the strain-independent viscous materials, flow laws are presented while for strain-dependent materials the relative importance of strain and strain rate softening/hardening is reported. If the stress or strain rate is above a threshold value some highly-filled silicone polymers may be considered linear visco-elastic (strain independent) and power-law strain-rate softening. The power-law exponent can be raised from 1 to ˜3 by using mixtures of high-viscosity silicone and plasticine. However, the need for high shear strain rates to obtain the power-law rheology imposes some restrictions on the usage of such materials for geodynamic modelling. Two simple shear experiments are presented that use Newtonian and power-law strain-rate softening materials. The results demonstrate how materials with power-law rheology result in better strain localization in analogue experiments.

A Biocontrol Strain of Bacillus subtilis WXCDD105 Used to Control Tomato Botrytis cinerea and Cladosporium fulvum Cooke and Promote the Growth of Seedlings

PubMed Central

Wang, Hui; Shi, Yuying; Wang, Doudou; Yao, Zhongtong; Wang, Yimei; Liu, Jiayin; Zhang, Shumei; Wang, Aoxue

2018-01-01

In this study, a strain named WXCDD105, which has strong antagonistic effects on Botrytis cinerea and Cladosporium fulvum Cooke, was screened out from the rhizosphere of healthy tomato plants. The tomato plants had inhibition diameter zones of 5.00 mm during the dual culture for four days. Based on the morphological and physiological characteristics, the 16S rDNA sequence, and the gyrB gene sequence analysis, the strain WXCDD105 was identified as Bacillus subtilis suBap. subtilis. The results of the mycelial growth test showed that the sterile filtrate of the strain WXCDD105 could significantly inhibit mycelial growth of Botrytis cinerea and Cladosporium fulvum Cooke. The inhibition rates were 95.28 and 94.44%, respectively. The potting experiment showed that the strain WXCDD105 made effective the control of tomato gray mold and tomato leaf mold. The control efficiencies were 74.70 and 72.07%. The antagonistic test results showed that the strain WXCDD105 had different degrees of inhibition on 10 kinds of plant pathogenic fungi and the average inhibition rates were more than 80%. We also found that the strain WXCDD105 stimulated both the seed germination and seedling growth of tomatoes. Using the fermentation liquid of WXCDD105 (108 cfu·mL−1) to treat the seeds, the germination rate and radicle length were increased. Under the treatment of the fermentation liquid of the strain WXCDD105 (106 cfu·mL−1), nearly all physiological indexes of tomato seedlings were significantly higher than that of the control groups. This could not only keep the nutritional quality of tomato fruits but also prevent them from rotting. This study provided us with an excellent strain for biological control of tomato gray mold, tomato leaf mold, and tomato growth promotion. This also laid the technical foundation for its application. PMID:29734678

A Biocontrol Strain of Bacillus subtilis WXCDD105 Used to Control Tomato Botrytis cinerea and Cladosporium fulvum Cooke and Promote the Growth of Seedlings.

PubMed

Wang, Hui; Shi, Yuying; Wang, Doudou; Yao, Zhongtong; Wang, Yimei; Liu, Jiayin; Zhang, Shumei; Wang, Aoxue

2018-05-04

In this study, a strain named WXCDD105, which has strong antagonistic effects on Botrytis cinerea and Cladosporium fulvum Cooke, was screened out from the rhizosphere of healthy tomato plants. The tomato plants had inhibition diameter zones of 5.00 mm during the dual culture for four days. Based on the morphological and physiological characteristics, the 16S rDNA sequence, and the gyrB gene sequence analysis, the strain WXCDD105 was identified as Bacillus subtilis suBap. subtilis . The results of the mycelial growth test showed that the sterile filtrate of the strain WXCDD105 could significantly inhibit mycelial growth of Botrytis cinerea and Cladosporium fulvum Cooke. The inhibition rates were 95.28 and 94.44%, respectively. The potting experiment showed that the strain WXCDD105 made effective the control of tomato gray mold and tomato leaf mold. The control efficiencies were 74.70 and 72.07%. The antagonistic test results showed that the strain WXCDD105 had different degrees of inhibition on 10 kinds of plant pathogenic fungi and the average inhibition rates were more than 80%. We also found that the strain WXCDD105 stimulated both the seed germination and seedling growth of tomatoes. Using the fermentation liquid of WXCDD105 (10⁸ cfu·mL −1 ) to treat the seeds, the germination rate and radicle length were increased. Under the treatment of the fermentation liquid of the strain WXCDD105 (10⁶ cfu·mL −1 ), nearly all physiological indexes of tomato seedlings were significantly higher than that of the control groups. This could not only keep the nutritional quality of tomato fruits but also prevent them from rotting. This study provided us with an excellent strain for biological control of tomato gray mold, tomato leaf mold, and tomato growth promotion. This also laid the technical foundation for its application.

Effect of the determination method of the material parameters on the accuracy of the hole expansion simulation for cold rolled steel sheet

NASA Astrophysics Data System (ADS)

Nakano, Hayato; Hakoyama, Tomoyuki; Kuwabara, Toshihiko

2017-10-01

Hole expansion forming of a cold rolled steel sheet is investigated both experimentally and analytically to clarify the effects of material models on the predictive accuracy of finite element analyses (FEA). The multiaxial plastic deformation behavior of a cold rolled steel sheet with a thickness of 1.2 mm was measured using a servo-controlled multiaxial tube expansion testing machine for the range of strain from initial yield to fracture. Tubular specimens were fabricated from the sheet sample by roller bending and laser welding. Many linear stress paths in the first quadrant of stress space were applied to the tubular specimens to measure the contours of plastic work in stress space up to a reference plastic strain of 0.24 along with the directions of plastic strain rates. The anisotropic parameters and exponent of the Yld2000-2d yield function (Barlat et al., 2003) were optimized to approximate the contours of plastic work and the directions of plastic strain rates. The hole expansion forming simulations were performed using the different model identifications based on the Yld2000-2d yield function. It is concluded that the yield function best capturing both the plastic work contours and the directions of plastic strain rates leads to the most accurate predicted FEA.

Dynamic Mechanical Response of Biomedical 316L Stainless Steel as Function of Strain Rate and Temperature

PubMed Central

Lee, Woei-Shyan; Chen, Tao-Hsing; Lin, Chi-Feng; Luo, Wen-Zhen

2011-01-01

A split Hopkinson pressure bar is used to investigate the dynamic mechanical properties of biomedical 316L stainless steel under strain rates ranging from 1 × 103 s−1 to 5 × 103 s−1 and temperatures between 25°C and 800°C. The results indicate that the flow stress, work-hardening rate, strain rate sensitivity, and thermal activation energy are all significantly dependent on the strain, strain rate, and temperature. For a constant temperature, the flow stress, work-hardening rate, and strain rate sensitivity increase with increasing strain rate, while the thermal activation energy decreases. Catastrophic failure occurs only for the specimens deformed at a strain rate of 5 × 103 s−1 and temperatures of 25°C or 200°C. Scanning electron microscopy observations show that the specimens fracture in a ductile shear mode. Optical microscopy analyses reveal that the number of slip bands within the grains increases with an increasing strain rate. Moreover, a dynamic recrystallisation of the deformed microstructure is observed in the specimens tested at the highest temperature of 800°C. PMID:22216015

Strain rate dependent hyperelastic stress-stretch behavior of a silica nanoparticle reinforced poly (ethylene glycol) diacrylate nanocomposite hydrogel.

PubMed

Zhan, Yuexing; Pan, Yihui; Chen, Bing; Lu, Jian; Zhong, Zheng; Niu, Xinrui

2017-11-01

Poly (ethylene glycol) diacrylate (PEGDA) derivatives are important biomedical materials. PEGDA based hydrogels have emerged as one of the popular regenerative orthopedic materials. This work aims to study the mechanical behavior of a PEGDA based silica nanoparticle (NP) reinforced nanocomposite (NC) hydrogel at physiological strain rates. The work combines materials fabrication, mechanical experiments, mathematical modeling and structural analysis. The strain rate dependent stress-stretch behaviors were observed, analyzed and quantified. Visco-hyperelasticity was identified as the deformation mechanism of the nano-silica/PEGDA NC hydrogel. NPs showed significant effect on both initial shear modulus and viscoelastic materials properties. A structure-based quasi-linear viscoelastic (QLV) model was constructed and capable to describe the visco-hyperelastic stress-stretch behavior of the NC hydrogel. A group of unified material parameters was extracted by the model from the stress-stretch curves obtained at different strain rates. Visco-hyperelastic behavior of NP/polymer interphase was not only identified but also quantified. The work could provide guidance to the structural design of next-generation NC hydrogel. Copyright © 2017. Published by Elsevier Ltd.

In-Situ Strain Analysis of Potential Habitat Composites Exposed to a Simulated Long-Term Lunar Radiation Exposure

NASA Technical Reports Server (NTRS)

Rojdev, Kristina; O'Rourke, Mary Jane; Hill, Charles; Nutt, Steven; Atwell, William

2010-01-01

NASA is studying the effects of long-term space radiation on potential multifunctional composite materials for habitats to better determine their characteristics in the harsh space environment. Two composite materials were selected for the study and were placed in a test stand that simulated the stresses of a pressure vessel wall on the material. The samples in the test stand were exposed to radiation at either a fast dose rate or a slow dose rate, and their strain and temperature was recorded during the exposure. It was found that during a fast dose rate exposure the materials saw a decreased strain with time, or a shrinking of the materials. Given previous radiation studies of polymers, this is believed to be a result of crosslinking occurring in the matrix material. However, with a slow dose rate, the materials saw an increase in strain with time, or a stretching of the materials. This result is consistent with scission or degradation of the matrix occurring, possibly due to oxidative degradation.

Stress and Strain Distributions during Machining of Ti-6Al-4V at Ambient and Cryogenic Temperatures

NASA Astrophysics Data System (ADS)

Rahman, Md. Fahim

Dry and liquid nitrogen pre-cooled Ti-6Al-4V samples were machined at a cutting speed of 43.2 m/min and at low (0.1 mm/rev) to high (0.4 mm/rev) feed rates for understanding the effects of temperature and strain rate on chip microstructures. During cryogenic machining, it was observed that between feed rates of 0.10 and 0.30 mm/rev, a 25% pressure reduction on tool occurred. Smaller number of chips and low tool/chip contact time and temperature were observed (compared to dry machining under ambient conditions). An in-situ set-up that consisted of a microscope and a lathe was constructed and helped to propose a novel serrated chip formation mechanism when microstructures (strain localization) and surface roughness were considered. Dimpled fracture surfaces observed in high-speed-machined chips were formed due to stable crack propagation that was also recorded during in-situ machining. An instability criterion was developed that showed easier strain localization within the 0.10-0.30mm/rev feed rate range.

Twinning and martensite in a 304 austenitic stainless steel

DOE Office of Scientific and Technical Information (OSTI.GOV)

Shen, Yongfeng; Li, Xi; Sun, Xin

2012-08-30

The microstructure characteristics and deformation behavior of 304L stainless steel during tensile deformation at two different strain rates have been investigated by means of interrupted tensile tests, electron-backscatter-diffraction (EBSD) and transmission electron microscopy (TEM) techniques. The volume fractions of transformed martensite and deformation twins at different stages of the deformation process were measured using X-ray diffraction method and TEM observations. It is found that the volume fraction of martensite monotonically increases with increasing strain but decreases with increasing strain rate. On the other hand, the volume fraction of twins increases with increasing strain for strain level less than 57%. Beyondmore » that, the volume fraction of twins decreases with increasing strain. Careful TEM observations show that stacking faults (SFs) and twins preferentially occur before the nucleation of martensite. Meanwhile, both {var_epsilon}-martensite and {alpha}{prime}-martensite are observed in the deformation microstructures, indicating the co-existence of stress induced- transformation and strain-induced-transformation. We also discussed the effects of twinning and martensite transformation on work-hardening as well as the relationship between stacking faults, twinning and martensite transformation.« less

Selection of Lecanicillium Strain with High Virulence against Developmental Stages of Bemisia tabaci

PubMed Central

Park, Heeyong

2010-01-01

Selection of fungal strains with high virulence against the developmental stages of Bemisia tabaci was performed using internal transcribed spacer regions. The growth rate of hyphae was measured and bioassay of each developmental stage of B. tabaci was conducted for seven days. All of the fungal strains tested were identified as Lecanicillium spp., with strain 4078 showing the fastest mycelium growth rate (colony diameter, 16.3 ± 0.9 mm) among the strains. Compared to strain 4075, which showed the slowest growth rate, the growth rate of strain 4078 was increased almost 2-fold after seven days. Strains 4078 and Btab01 were most virulent against the egg and larva stages, respectively. The virulence of fungal strains against the adult stage was high, except for strains 41185 and 3387. Based on the growth rate of mycelium and level of virulence, strains 4078 and Btab01 were selected as the best fungal strains for application to B. tabaci, regardless of developmental stage. PMID:23956657

Characterization of DP600 Steel Subject to Electrohydraulic Forming

NASA Astrophysics Data System (ADS)

McCallum, Brent

Electrohydraulic forming (EHF) is a manufacturing technique that transforms electrical energy into work. In EHF, a shockwave is produced as a result of a high-voltage electrical discharge between two electrodes in a water chamber, which travels through water toward the sheet and forms it into the final shape at high velocity. Strain rates can reach 10 4 s-1 in EHF. DP600 dual phase steel was formed in the Nakazima test in quasi-static (QS) condition, and EHF, performed without a mating die (free forming) and using a 34° conical die (die forming). The sheets were etched with a grid prior to testing to determine strains across each specimen. Analysis of voids was carried out to investigate the micro-mechanisms of failure in DP600 steel formed in these three processes. Nakazima specimens exhibited uniform strain behaviour up to 0.65 effective strain; EHFF up to 0.45 effective strain; and EHDF up to 0.7 effective strain.

Strain Rate Sensitivity of Graphite/Polymer Laminate Composites

NASA Astrophysics Data System (ADS)

Syed, Izhar H.; Brar, N. S.

2002-07-01

Strain rate sensitivities of Graphite/Epoxy and Graphite/Peek laminate composites are investigated by measuring their stress-strain response at strain rates of 0.001/s, 0.1/s, and 400/s. Tension specimens of the composite laminates are fabricated in a dog-bone shape. Stress-strain data at quasi-static rates of 0.001/s and 0.1/s are obtained using a servohydraulic test system. High strain rate data are produced with a Direct Tension Split Hopkinson Bar (DTSHB). A tensile stress pulse is generated in the DTSHB by impacting a stopper flange at the end of the incident bar with an aluminum/polymeric tube launched around the incident bar. The failure (flow) tensile stress of Graphite/Epoxy increases from 240 MPa to 280±10 MPa (ɛ = 0.06) when the strain rate is raised from 0.001/s to 400/s. For Graphite/Peek, failure (flow) tension stress increases from 175 MPa at a strain rate of 0.001/s to 270±20 MPa at a strain rate of 400/s.

2016 Accomplishments. Tritium aging studies on stainless steel. Forging process effects on the fracture toughness properties of tritium-precharged stainless steel

DOE Office of Scientific and Technical Information (OSTI.GOV)

Morgan, Michael J.

Forged austenitic stainless steels are used as the materials of construction for pressure vessels designed to contain tritium at high pressure. These steels are highly resistant to tritium-assisted fracture but their resistance can depend on the details of the forging microstructure. During FY16, the effects of forging strain rate and deformation temperature on the fracture toughness properties of tritium-exposed-and-aged Type 304L stainless steel were studied. Forgings were produced from a single heat of steel using four types of production forging equipment – hydraulic press, mechanical press, screw press, and high-energy-rate forging (HERF). Each machine imparted a different nominal strain ratemore » during the deformation. The objective of the study was to characterize the J-Integral fracture toughness properties as a function of the industrial strain rate and temperature. The second objective was to measure the effects of tritium and decay helium on toughness. Tritium and decay helium effects were measured by thermally precharging the as-forged specimens with tritium gas at 34.5 MPa and 350°C and aging for up to five years at -80°C to build-in decay helium prior to testing. The results of this study show that the fracture toughness properties of the as-forged steels vary with forging strain rate and forging temperature. The effect is largely due to yield strength as the higher-strength forgings had the lower toughness values. For non-charged specimens, fracture toughness properties were improved by forging at 871°C versus 816°C and Screw-Press forgings tended to have lower fracture toughness values than the other forgings. Tritium exposures reduced the fracture toughness values remarkably to fracture toughness values averaging 10-20% of as-forged values. However, forging strain rate and temperature had little or no effect on the fracture toughness after tritium precharging and aging. The result was confirmed by fractography which indicated that fracture modes in the tritium-exposed specimens were similar for all forgings. Another FY16 objective was to prepare fracture toughness specimens from Types 304L and 21-6-9 stainless steel weldments and heat-affected zones (HAZ) for tritium charging.« less

Isolation and lipid degradation profile of Raoultella planticola strain 232-2 capable of efficiently catabolizing edible oils under acidic conditions.

PubMed

Sugimori, Daisuke; Watanabe, Mika; Utsue, Tomohiro

2013-01-01

The lipids (fats and oils) degradation capabilities of soil microorganisms were investigated for possible application in treatment of lipids-contaminated wastewater. We isolated a strain of the bacterium Raoultella planticola strain 232-2 that is capable of efficiently catabolizing lipids under acidic conditions such as in grease traps in restaurants and food processing plants. The strain 232-2 efficiently catabolized a mixture (mixed lipids) of commercial vegetable oil, lard, and beef tallow (1:1:1, w/w/w) at 20-35 °C, pH 3-9, and 1,000-5,000 ppm lipid content. Highly effective degradation rate was observed at 35 °C and pH 4.0, and the 24-h degradation rate was 62.5 ± 10.5 % for 3,000 ppm mixed lipids. The 24-h degradation rate for 3,000 ppm commercial vegetable oil, lard, beef tallow, mixed lipids, and oleic acid was 71.8 %, 58.7 %, 56.1 %, 55.3 ± 8.5 %, and 91.9 % at pH 4 and 30 °C, respectively. R. planticola NBRC14939 (type strain) was also able to efficiently catabolize the lipids after repeated subculturing. The composition of the culture medium strongly influenced the degradation efficiency, with yeast extract supporting more complete dissimilation than BactoPeptone or beef extract. The acid tolerance of strain 232-2 is proposed to result from neutralization of the culture medium by urease-mediated decomposition of urea to NH(3). The rate of lipids degradation increased with the rates of neutralization and cell growth. Efficient lipids degradation using strain 232-2 has been achieved in the batch treatment of a restaurant wastewater.

The Brittle-Ductile Transition in Crystal and Bubble-bearing Magmas

NASA Astrophysics Data System (ADS)

Caricchi, L.; Pistone, M.; Cordonnier, B.; Tripoli, B.; Ulmer, P.; Reusser, E.; Marone, F.; Burlini, L.

2011-12-01

The strain response of magma is critically dependent upon its viscosity, the magnitude of the applied stress and the experimental time-scale. The brittle-ductile transition in pure silicate melts is expected for an applied stress approaching 108±0.5 Pa (Dingwell, 1997). However, magmas are mostly mixture of crystal and bubble-bearing silicate melts. To date, there are no data to constrain the ductile-brittle transition for three-phase magmas. Thus, we conducted consistent torsion experiments at high temperature (673-973 K) and high pressure (200 MPa), in the strain rate range 1*10-5-4*10-3 s-1, using a HT-HP internally-heated Paterson-type rock deformation apparatus. The samples are composed of hydrous haplogranitic glass, quartz crystals (24-65 vol%) and CO2-rich gas-pressurized bubbles (9-12 vol%). The applied strain rate was increased until brittle failure occurred; micro-fracturing and healing processes commonly occurred before sample macroscopic fracturing. The experimental results highlight a clear relationship between the effective viscosity of the three-phase magmas, strain rate, temperature and the onset of brittle-ductile behavior. Crystal- and bubble-free melts at high viscosity (1011-1011.6 Pa*s at 673 K) show brittle behavior in the strain rate range between 1*10-4 and 5*10-4 s-1. For comparable viscosities crystal and bubble-bearing magmas show a transition to brittle behavior at lower strain rates. Synchrotron-based 3D imaging of fractured samples, show the presence of fractures with an antithetic trend with respect to shear strain directions. The law found in this study expresses the transition from ductile to brittle behavior for real magmas and could significantly improve our understanding of the control of brittle processes on extrusion of high-viscosity magmas and degassing at silicic volcanoes.

Modelling deformation of partially melted rock using a poroviscoelastic rheology with dynamic power law viscosity

NASA Astrophysics Data System (ADS)

Simakin, A.; Ghassemi, A.

2005-03-01

A poroviscoelastic constitutive model is developed and used to study coupled rock deformation and fluid flow. The model allows the relaxation of both shear and symmetric components of the effective stress. Experimental results are usually interpreted in terms of the power law viscous material. However, in this work the effect of strain damage on viscosity is considered by treating the viscosity as a dynamic time-dependent parameter that varies proportionally to the second invariant of the strain rate. Healing is also taken into account so that the dynamic power law viscosity has a constant asymptotic at a given strain rate. The theoretical model is implemented in a finite element (FE) formulation that couples fluid flow and mechanical equilibrium equations. The FE method is applied to numerically study the triaxial compression of partially melted rocks at elevated PT conditions. It is found that the numerically calculated stress-strain curves demonstrate maxima similar to those observed in laboratory experiments. Also, the computed pattern of melt redistribution and strain localization at the contact between the rock sample and a stiff spacer is qualitatively similar to the experimental observations. The results also indicate that the matrix sensitivity to damage affects the scale of strain localization and melt redistribution.

Synergistic Effects of Sodium Chloride, Glucose, and Temperature on Biofilm Formation by Listeria monocytogenes Serotype 1/2a and 4b Strains ▿ † ‡

PubMed Central

Pan, Youwen; Breidt, Frederick; Gorski, Lisa

2010-01-01

Biofilm formation by Listeria monocytogenes is generally associated with its persistence in the food-processing environment. Serotype 1/2a strains make up more than 50% of the total isolates recovered from food and the environment, while serotype 4b strains are most often associated with major outbreaks of human listeriosis. Using a microplate assay with crystal violet staining, we examined biofilm formation by 18 strains of each serotype in tryptic soy broth with varying concentrations of glucose (from 0.25% to 10.0%, wt/vol), sodium chloride (from 0.5% to 7.0%, wt/vol) and ethanol (from 1% to 5.0%, vol/vol), and at different temperatures (22.5°C, 30°C, and 37°C). A synergistic effect on biofilm formation was observed for glucose, sodium chloride, and temperature. The serotype 1/2a strains generally formed higher-density biofilms than the 4b strains under most conditions tested. Interestingly, most serotype 4b strains had a higher growth rate than the 1/2a strains, suggesting that the growth rate may not be directly related to the capacity for biofilm formation. Crystal violet was found to stain both bacterial cells and biofilm matrix material. The enhancement in biofilm formation by environmental factors was apparently due to the production of extracellular polymeric substances instead of the accumulation of viable biofilm cells. PMID:20048067

Modeling of the static recrystallization for 7055 aluminum alloy by cellular automaton

NASA Astrophysics Data System (ADS)

Zhang, Tao; Lu, Shi-hong; Zhang, Jia-bin; Li, Zheng-fang; Chen, Peng; Gong, Hai; Wu, Yun-xin

2017-09-01

In order to simulate the flow behavior and microstructure evolution during the pass interval period of the multi-pass deformation process, models of static recovery (SR) and static recrystallization (SRX) by the cellular automaton (CA) method for the 7055 aluminum alloy were established. Double-pass hot compression tests were conducted to acquire flow stress and microstructure variation during the pass interval period. With the basis of the material constants obtained from the compression tests, models of the SR, incubation period, nucleation rate and grain growth were fitted by least square method. A model of the grain topology and a statistical computation of the CA results were also introduced. The effects of the pass interval time, temperature, strain, strain rate and initial grain size on the microstructure variation for the SRX of the 7055 aluminum alloy were studied. The results show that a long pass interval time, large strain, high temperature and large strain rate are beneficial for finer grains during the pass interval period. The stable size of the static recrystallized grain is not concerned with the initial grain size, but mainly depends on the strain rate and temperature. The SRX plays a vital role in grain refinement, while the SR has no effect on the variation of microstructure morphology. Using flow stress and microstructure comparisons of the simulated and experimental CA results, the established CA models can accurately predict the flow stress and microstructure evolution during the pass interval period, and provide guidance for the selection of optimized parameters for the multi-pass deformation process.

Intrinsic mechanical behavior of femoral cortical bone in young, osteoporotic and bisphosphonate-treated individuals in low- and high energy fracture conditions

DOE PAGES

Zimmermann, Elizabeth A.; Schaible, Eric; Gludovatz, Bernd; ...

2016-02-16

Bisphosphonates are a common treatment to reduce osteoporotic fractures. This treatment induces osseous structural and compositional changes accompanied by positive effects on osteoblasts and osteocytes. Here, we test the hypothesis that restored osseous cell behavior, which resembles characteristics of younger, healthy cortical bone, leads to improved bone quality. Microarchitecture and mechanical properties of young, treatment-naïve osteoporosis, and bisphosphonate-treated cases were investigated in femoral cortices. Tissue strength was measured using three-point bending. Collagen fibril-level deformation was assessed in non-traumatic and traumatic fracture states using synchrotron small-angle x-ray scattering (SAXS) at low and high strain rates. The lower modulus, strength and fibrilmore » deformation measured at low strain rates reflects susceptibility for osteoporotic low-energy fragility fractures. Independent of age, disease and treatment status, SAXS revealed reduced fibril plasticity at high strain rates, characteristic of traumatic fracture. We find the significantly reduced mechanical integrity in osteoporosis may originate from porosity and alterations to the intra/extrafibrillar structure, while the fibril deformation under treatment indicates improved nano-scale characteristics. In conclusion, losses in strength and fibril deformation at low strain rates correlate with the occurrence of fragility fractures in osteoporosis, while improvements in structural and mechanical properties following bisphosphonate treatment may foster resistance to fracture during physiological strain rates.« less

Grain size dependence of dynamic mechanical behavior of AZ31B magnesium alloy sheet under compressive shock loading

DOE Office of Scientific and Technical Information (OSTI.GOV)

Asgari, H., E-mail: hamed.asgari@usask.ca; Odeshi, A.G.; Szpunar, J.A.

2015-08-15

The effects of grain size on the dynamic deformation behavior of rolled AZ31B alloy at high strain rates were investigated. Rolled AZ31B alloy samples with grain sizes of 6, 18 and 37 μm, were subjected to shock loading tests using Split Hopkinson Pressure Bar at room temperature and at a strain rate of 1100 s{sup −} {sup 1}. It was found that a double-peak basal texture formed in the shock loaded samples. The strength and ductility of the alloy under the high strain-rate compressive loading increased with decreasing grain size. However, twinning fraction and strain hardening rate were found tomore » decrease with decreasing grain size. In addition, orientation imaging microscopy showed a higher contribution of double and contraction twins in the deformation process of the coarse-grained samples. Using transmission electron microscopy, pyramidal dislocations were detected in the shock loaded sample, proving the activation of pyramidal slip system under dynamic impact loading. - Highlights: • A double-peak basal texture developed in all shock loaded samples. • Both strength and ductility increased with decreasing grain size. • Twinning fraction and strain hardening rate decreased with decreasing grain size. • ‘g.b’ analysis confirmed the presence of dislocations in shock loaded alloy.« less

Intrinsic mechanical behavior of femoral cortical bone in young, osteoporotic and bisphosphonate-treated individuals in low- and high energy fracture conditions

NASA Astrophysics Data System (ADS)

Zimmermann, Elizabeth A.; Schaible, Eric; Gludovatz, Bernd; Schmidt, Felix N.; Riedel, Christoph; Krause, Matthias; Vettorazzi, Eik; Acevedo, Claire; Hahn, Michael; Püschel, Klaus; Tang, Simon; Amling, Michael; Ritchie, Robert O.; Busse, Björn

2016-02-01

Bisphosphonates are a common treatment to reduce osteoporotic fractures. This treatment induces osseous structural and compositional changes accompanied by positive effects on osteoblasts and osteocytes. Here, we test the hypothesis that restored osseous cell behavior, which resembles characteristics of younger, healthy cortical bone, leads to improved bone quality. Microarchitecture and mechanical properties of young, treatment-naïve osteoporosis, and bisphosphonate-treated cases were investigated in femoral cortices. Tissue strength was measured using three-point bending. Collagen fibril-level deformation was assessed in non-traumatic and traumatic fracture states using synchrotron small-angle x-ray scattering (SAXS) at low and high strain rates. The lower modulus, strength and fibril deformation measured at low strain rates reflects susceptibility for osteoporotic low-energy fragility fractures. Independent of age, disease and treatment status, SAXS revealed reduced fibril plasticity at high strain rates, characteristic of traumatic fracture. The significantly reduced mechanical integrity in osteoporosis may originate from porosity and alterations to the intra/extrafibrillar structure, while the fibril deformation under treatment indicates improved nano-scale characteristics. In conclusion, losses in strength and fibril deformation at low strain rates correlate with the occurrence of fragility fractures in osteoporosis, while improvements in structural and mechanical properties following bisphosphonate treatment may foster resistance to fracture during physiological strain rates.

Intrinsic mechanical behavior of femoral cortical bone in young, osteoporotic and bisphosphonate-treated individuals in low- and high energy fracture conditions

DOE Office of Scientific and Technical Information (OSTI.GOV)

Zimmermann, Elizabeth A.; Schaible, Eric; Gludovatz, Bernd

Bisphosphonates are a common treatment to reduce osteoporotic fractures. This treatment induces osseous structural and compositional changes accompanied by positive effects on osteoblasts and osteocytes. Here, we test the hypothesis that restored osseous cell behavior, which resembles characteristics of younger, healthy cortical bone, leads to improved bone quality. Microarchitecture and mechanical properties of young, treatment-naïve osteoporosis, and bisphosphonate-treated cases were investigated in femoral cortices. Tissue strength was measured using three-point bending. Collagen fibril-level deformation was assessed in non-traumatic and traumatic fracture states using synchrotron small-angle x-ray scattering (SAXS) at low and high strain rates. The lower modulus, strength and fibrilmore » deformation measured at low strain rates reflects susceptibility for osteoporotic low-energy fragility fractures. Independent of age, disease and treatment status, SAXS revealed reduced fibril plasticity at high strain rates, characteristic of traumatic fracture. We find the significantly reduced mechanical integrity in osteoporosis may originate from porosity and alterations to the intra/extrafibrillar structure, while the fibril deformation under treatment indicates improved nano-scale characteristics. In conclusion, losses in strength and fibril deformation at low strain rates correlate with the occurrence of fragility fractures in osteoporosis, while improvements in structural and mechanical properties following bisphosphonate treatment may foster resistance to fracture during physiological strain rates.« less

Characterization of a novel Pseudomonas sp. that mineralizes high concentrations of pentachlorophenol.

PubMed Central

Radehaus, P M; Schmidt, S K

1992-01-01

A pentachlorophenol (PCP)-mineralizing bacterium was isolated from polluted soil and identified as Pseudomonas sp. strain RA2. In batch cultures, Pseudomonas sp. strain RA2 used PCP as its sole source of carbon and energy and was capable of completely degrading this compound as indicated by radiotracer studies, stoichiometric release of chloride, and biomass formation. Pseudomonas sp. strain RA2 was able to mineralize a higher concentration of PCP (160 mg liter-1) than any previously reported PCP-degrading pseudomonad. At a PCP concentration of 200 mg liter-1, cell growth was completely inhibited and PCP was not degraded, although an active population of Pseudomonas sp. RA2 was still present in these cultures after 2 weeks. The inhibitory effect of PCP was partially attributable to its effect on the growth rate of Pseudomonas sp. strain RA2. The highest specific growth rate (mu = 0.09 h-1) was reached at a PCP concentration of 40 mg liter-1 but decreased at higher or lower PCP concentrations, with the lowest mu (0.05 h-1) occurring at 150 mg liter-1. Despite this reduction in growth rate, total biomass production was proportional to PCP concentration at all PCP concentrations degraded by Pseudomonas sp. RA2. In contrast, final cell density was reduced to below expected values at PCP concentrations greater than 100 mg liter-1. These results indicate that, in addition to its effect as an uncoupler of oxidative phosphorylation, PCP may also inhibit cell division in Pseudomonas sp. strain RA2.(ABSTRACT TRUNCATED AT 250 WORDS) PMID:1444401

Effect of methyl mercury on the growth of the green alga, Coelastrum microporum Naeg, strain 280

DOE Office of Scientific and Technical Information (OSTI.GOV)

Holderness, J.; Fenwick, M.G.; Lynch, D.L.

The effect of methylmercury on the growth of the green alga, coelastrum microporum Naeg. strain 280 was examined. Growth was drastically reduced at a level of .006 ppM methylmercury chloride. It was noted that the organism stored more starch at higher concentrations of methylmercury. Levels of .0008 ppm were found to affect gross photosynthetic rates. (JWP)

Dynamic compressive strength of epoxy composites

NASA Astrophysics Data System (ADS)

Plastinin, A. V.; Sil'vestrov, V. V.

1996-11-01

The strength of laminated and unidirectionally reinforced composite materials was investigated in conditions of dynamic uniaxial compression with a strain rate of 50-1000 sec-1 using the split Hopkinson pressure bar method. It was shown that in conditions of dynamic compression, glass/epoxy, aramid/epoxy, and carbon/epoxy composites exhibit elastic-brittle behavior with anisotropy of the strength and elastic properties. The effect of the strain rate on the strength characteristics of fiberglass-reinforced plastics was demonstrated.

Effect of Initial Microstructure on the Microstructural Evolution and Joint Efficiency of a WE43 Alloy During Friction Stir Welding

DTIC Science & Technology

2013-04-01

to maximize joint efficiency. 15. SUBJECT TERMS friction stir welding, strain rate, dynamic recrystallization , joint efficiency, stir zone (SZ...stir welding, Strain rate, Dynamic recrystallization , Joint efficiency, Stir Zone (SZ) Abstract The initial microstructure plays an important role in... eutectic Mg17Al12 phase. Park et al. [7] demonstrated the importance of texture and related it to the mechanical properties of an AZ61 alloy

Moisture, anisotropy, stress state, and strain rate effects on bighorn sheep horn keratin mechanical properties

DOE PAGES

Johnson, K. L.; Trim, M. W.; Francis, D. K.; ...

2016-10-01

Our paper investigates the effects of moisture, anisotropy, stress state, and strain rate on the mechanical properties of the bighorn sheep (Ovis Canadensis) horn keratin. The horns consist of fibrous keratin tubules extending along the length of the horn and are contained within an amorphous keratin matrix. We tested samples in the rehydrated (35 wt.% water) and ambient dry (10 wt.% water) conditions along the longitudinal and radial directions under tension and compression. Increased moisture content was found to increase ductility and decrease strength, as well as alter the stress state dependent nature of the material. Furthermore, the horn keratinmore » demonstrates a significant strain rate dependence in both tension and compression, and also showed increased energy absorption in the hydrated condition at high strain rates when compared to quasi-static data, with increases of 114% in tension and 192% in compression. Compressive failure occurred by lamellar buckling in the longitudinal orientation followed by shear delamination. Tensile failure in the longitudinal orientation occurred by lamellar delamination combined with tubule pullout and fracture. Finally, the structure-property relationships quantified here for bighorn sheep horn keratin can be used to help validate finite element simulations of ram’s impacting each other as well as being useful for other analysis regarding horn keratin on other animals.« less

Moisture, anisotropy, stress state, and strain rate effects on bighorn sheep horn keratin mechanical properties

DOE Office of Scientific and Technical Information (OSTI.GOV)

Johnson, K. L.; Trim, M. W.; Francis, D. K.

Our paper investigates the effects of moisture, anisotropy, stress state, and strain rate on the mechanical properties of the bighorn sheep (Ovis Canadensis) horn keratin. The horns consist of fibrous keratin tubules extending along the length of the horn and are contained within an amorphous keratin matrix. We tested samples in the rehydrated (35 wt.% water) and ambient dry (10 wt.% water) conditions along the longitudinal and radial directions under tension and compression. Increased moisture content was found to increase ductility and decrease strength, as well as alter the stress state dependent nature of the material. Furthermore, the horn keratinmore » demonstrates a significant strain rate dependence in both tension and compression, and also showed increased energy absorption in the hydrated condition at high strain rates when compared to quasi-static data, with increases of 114% in tension and 192% in compression. Compressive failure occurred by lamellar buckling in the longitudinal orientation followed by shear delamination. Tensile failure in the longitudinal orientation occurred by lamellar delamination combined with tubule pullout and fracture. Finally, the structure-property relationships quantified here for bighorn sheep horn keratin can be used to help validate finite element simulations of ram’s impacting each other as well as being useful for other analysis regarding horn keratin on other animals.« less

Fitness cost of reassortment in human influenza.

PubMed

Villa, Mara; Lässig, Michael

2017-11-01

Reassortment, which is the exchange of genome sequence between viruses co-infecting a host cell, plays an important role in the evolution of segmented viruses. In the human influenza virus, reassortment happens most frequently between co-existing variants within the same lineage. This process breaks genetic linkage and fitness correlations between viral genome segments, but the resulting net effect on viral fitness has remained unclear. In this paper, we determine rate and average selective effect of reassortment processes in the human influenza lineage A/H3N2. For the surface proteins hemagglutinin and neuraminidase, reassortant variants with a mean distance of at least 3 nucleotides to their parent strains get established at a rate of about 10-2 in units of the neutral point mutation rate. Our inference is based on a new method to map reassortment events from joint genealogies of multiple genome segments, which is tested by extensive simulations. We show that intra-lineage reassortment processes are, on average, under substantial negative selection that increases in strength with increasing sequence distance between the parent strains. The deleterious effects of reassortment manifest themselves in two ways: there are fewer reassortment events than expected from a null model of neutral reassortment, and reassortant strains have fewer descendants than their non-reassortant counterparts. Our results suggest that influenza evolves under ubiquitous epistasis across proteins, which produces fitness barriers against reassortment even between co-circulating strains within one lineage.

Elasticity of excised dog lung parenchyma

NASA Technical Reports Server (NTRS)

Vawter, D. L.; Fung, Y. C.; West, J. B.

1978-01-01

An optical-electromechanical system is used to measure the force-deformation behavior of biaxially loaded rectangular slabs of excised dog lung parenchyma. In the course of the study, the effects of time, the consistency of reference lengths and areas, the presence of hysteresis, the necessity of preconditioning, the repeatability of results, the effects of lateral load, the effect of strain rate, the effect of pH, the influence of temperature, and the variations among specimens are considered. A new finding is that there is a change in elastic behavior when the tissue undergoes a compressive strain. When the tissue is in tension, increasing the lateral load decreases the compliance, whereas the opposite is true when compressive strain is present.

Numerical prediction of mechanical properties of Pb-Sn solder alloys containing antimony, bismuth and or silver ternary trace elements

NASA Astrophysics Data System (ADS)

Gadag, Shiva P.; Patra, Susant

2000-12-01

Solder joint interconnects are mechanical means of structural support for bridging the various electronic components and providing electrical contacts and a thermal path for heat dissipation. The functionality of the electronic device often relies on the structural integrity of the solder. The dimensional stability of solder joints is numerically predicted based on their mechanical properties. Algorithms to model the kinetics of dissolution and subsequent growth of intermetallic from the complete knowledge of a single history of time-temperature-reflow profile, by considering equivalent isothermal time intervals, have been developed. The information for dissolution is derived during the heating cycle of reflow and for the growth process from cooling curve of reflow profile. A simple and quick analysis tool to derive tensile stress-strain maps as a function of the reflow temperature of solder and strain rate has been developed by numerical program. The tensile properties are used in modeling thermal strain, thermal fatigue and to predict the overall fatigue life of solder joints. The numerical analysis of the tensile properties as affected by their composition and rate of testing, has been compiled in this paper. A numerical model using constitutive equation has been developed to evaluate the interfacial fatigue crack growth rate. The model can assess the effect of cooling rate, which depends on the level of strain energy release rate. Increasing cooling rate from normalizing to water-quenching, enhanced the fatigue resistance to interfacial crack growth by up to 50% at low strain energy release rate. The increased cooling rates enhanced the fatigue crack growth resistance by surface roughening at the interface of solder joint. This paper highlights salient features of process modeling. Interfacial intermetallic microstructure is affected by cooling rate and thereby affects the mechanical properties.

Strain rate dependence in the nanoindentation-induced deformation of Mg-Al intermetallic compounds produced by packed powder diffusion coating

NASA Astrophysics Data System (ADS)

Chang, Haiwei; Lu, Mingyuan; Zhang, Mingxing; Atrens, Andrej; Huang, Han

2015-09-01

Nanoindentation was performed on τ-Mg32(Al, Zn)49 and β-Mg17Al12 intermetallic coatings and on a AZ91E Mg alloy substrate using loading rates of 0.03 to 30 mNs-1. Pop-in phenomenon was observed during loading in the two intermetallic coatings and in the substrate. Both the magnitude of the pop-ins and the time interval between two consecutive pop-ins increased with increasing loads. The phenomenon was attributed to plastic instability, which is known as the Portevin-Le Châtelier effect. The morphologies of the indent impressions at different strain rates on the t phase, the β phase and the substrate were also investigated using atomic force microscopy. Pile-up occurred in the τ and β phases and was found independent of the strain rate; no obvious pile-up occurred on the AZ91E substrate. The AZ91E substrate exhibited creep rates greater than those of the intermetallic phases, and all of the creep rates increased with the loading rate.

A Novel Method for Enhancing Strains' Biodegradation of 4-Chloronitrobenzene.

PubMed

Li, Tian; Zhang, Tian C; He, Lin

2017-12-20

This paper introduces a novel approach to enhance the strains' biodegradation of 4-chloronitrobenzene by utilizing the synergistic effect of the organic reductant mannitol and the substrate beef extraction. Our results demonstrate that 4-chloronitrobenzene could not be an available nitrogen source to support target strains' growth, which induced the limited 4-chloronitrobenzene biodegradation. In addition, the organic reducing agent and substrate had a better synergistic effect than inorganic reducing agent and substrate to enhance the strains' 4-chloronitrobenzene cometabolic biodegradation. Employing the synergistic effect of the optimal mixture (mannitol and beef extraction), the biodegradation rates of 50mgL -1 4-chloronitrobenzene by seven of the ten target strains were enhanced up to 100% from previous removals of no more than 19.1% after 7days. Three of the strains could even completely degrade 100mgL -1 4-chloronitrobenzene while five strains degraded over 91.4%. The method has good potential to enhance bioremediation of various 4-Chloronitrobenzene-contaminated environments as mannitol and beef extraction are non-toxic to the environment. Copyright © 2017 Elsevier B.V. All rights reserved.

Stretch-rate relationships for turbulent premixed combustion LES subgrid models measured using temporally resolved diagnostics

DOE Office of Scientific and Technical Information (OSTI.GOV)

Steinberg, Adam M.; Driscoll, James F.

2010-07-15

Temporally resolved measurements of turbulence-flame interaction were used to experimentally determine relationships for the strain-rate and curvature stretch-rate exerted on a premixed flame surface. These relationships include a series of transfer functions that are analogous to, but not equal to, stretch-efficiency functions. The measurements were obtained by applying high-repetition-rate particle image velocimetry in a turbulent slot Bunsen flame and were able to resolve the range of turbulent scales that cause flame surface straining and wrinkling. Fluid control masses were tracked in a Lagrangian manner as they interacted with the flame surface. From each interaction, the spatially and temporally filtered subgridmore » strain-rate and curvature stretch-rate were measured. By analyzing the statistics of thousands of turbulence-flame interactions, relationships for the strain-rate and curvature stretch-rate were determined that are appropriate for Large Eddy Simulation. It was found that the strain-rate exerted on the flame during these interactions was better correlated with the strength of the subgrid fluid-dynamic strain-rate field than with previously used characteristic strain-rates. Furthermore, stretch-efficiency functions developed from simplified vortex-flame interactions significantly over-predict the measurements. Hence, the proposed relationship relates the strain-rate on the flame to the filtered subgrid fluid-dynamic strain-rate field during real turbulence-flame interactions using an empirically determined Strain-Rate Transfer function. It was found that the curvature stretch-rate did not locally balance the strain-rate as has been proposed in previous models. A geometric relationship was found to exist between the subgrid flame surface wrinkling factor and subgrid curvature stretch-rate, which could be expressed using an empirically determined wrinkling factor transfer function. Curve fits to the measured relationships are provided that could be implemented in numerical simulations of turbulent premixed combustion. (author)« less

Comparison of epoxy-based encapsulating materials over temperature and strain rate

NASA Astrophysics Data System (ADS)

Khan, Amnah S.; Wilgeroth, James; Balzer, Jens; Proud, William G.

2017-01-01

The highly insulating, adhesive and bonding properties of thermosetting epoxies, their ability to be injection moulded in an uncured state, as well as their presence in a wide number of composites, has resulted in their widespread use in both electrical and aerospace applications. There is thus a need to understand the compressive response of epoxies over the range of temperatures likely to be experienced within their working environment. The effects of varying strain rates and temperatures on an epoxy resin (Scotchcast 8) and an epoxy-based syntactic foam (Stycast 1090) were investigated. The samples were studied from -20 °C to +80 °C over a range of strain rates (10-4 - 10+3 s-1). Stress-strain data was obtained, with further analysis from high-speed images. Dynamic Mechanical Analysis (DMA) was also performed on the two materials. Data obtained from these experiments demonstrated key differences in the behaviour of the two materials, forming a basis for comparison with numerical simulations.

Microstructure and hot compression deformation of the as-cast Mg-5.0Sn-1.5Y-0.1Zr alloy

NASA Astrophysics Data System (ADS)

Luo, Xiaoping; Kang, Li; Li, Qiushu; Chai, Yuesheng

2015-08-01

The hot compression deformation behavior and microstructure of as-cast Mg-5.0Sn-1.5Y-0.1Zr alloy were investigated by performing isothermal hot compression tests. The tests were conducted using a thermal mechanical simulator at 250-450 °C and strain rates ranging from 0.002 to 2 s-1, with a maximum deformation strain of 50 %. The effects of the deformation parameters on the microstructure evolution of the Mg-5.0Sn-1.5Y-0.1Zr alloy were discussed. The study revealed the flow behavior and the deformation mechanism of the Mg-5.0Sn-1.5Y-0.1Zr alloy. The dependence of flow stress on temperature and strain rate was described by a hyperbolic sine constitutive equation. Through regression analysis, the activation energy of 223.26 kJ mol-1 for plastic deformation was determined by considering flow stress at a strain rate of 0.2. Microstructure observation showed that dynamic recrystallization occurred extensively along grain boundaries at temperatures higher than 300 °C and strain rates lower than 0.02 s-1. This observation provides a theoretical basis for the manufacture and application of the Mg-5.0Sn-1.5Y-0.1Zr alloy.

A study of the interaction between H. pylori mice passage strains and gastric epithelial cells.

PubMed

Rahman, Inayatur; Idrees, Muhammad; Waqas, Mohammad; Karim, Abdul

2018-05-01

Helicobacter pylori (H. pylori) infections are very serious health problem that are further worsened by increasing/developing resistance to the current antibiotics. Therefore, new therapeutic agents are needed for H. pylori eradication. Use of a CD46 derived peptide (P3) as bactericidal agent against H. pylori has shown high activity rate in vivo and this study examines the changes in H. pylori features in response to effect of P3 treatment.AGS cells were infected with H. pylori wild type strain 67:21 and its mice passage strains (P3 treated and untreated strains) and further examined using immunoblotting assay, FACS and Urease activity analysis. Comparatively we found increased level of Urease alpha subunit A (UreA) and alkyl hydroperoxide reductase C (AhpC) proteins for P3 treated strain of H. pylori than its wild type or untreated strain after infection of AGS cells. Conclusion These results suggest that there might be a high rate of adherence to host cells for the P3 treated passage strain than untreated or wild type strain. Our findings also indicate that either adhesins are being changed or H. pylori interaction to the host cells is affected after P3 treatment.

Antibiotic resistance monitoring in Vibrio spp. isolated from rearing environment and intestines of abalone Haliotis diversicolor.

PubMed

Wang, R X; Wang, J Y; Sun, Y C; B L Yang; A L Wang

2015-12-30

546 Vibrio isolates from rearing seawater (292 strains) and intestines of abalone (254 strains) were tested to ten antibiotics using Kirby-Bauer diffusion method. Resistant rates of abalone-derived Vibrio isolates to chloramphenicol (C), enrofloxacin (ENX) and norfloxacin (NOR) were <28%, whereas those from seawater showed large fluctuations in resistance to each of the tested antibiotics. Many strains showed higher resistant rates (>40%) to kanamycin (KNA), furazolidone (F), tetracycline (TE), gentamicin (GM) and rifampin (RA). 332 isolates from seawater (n=258) and abalone (n=74) were resistant to more than three antibiotics. Peaked resistant rates of seawater-derived isolates to multiple antibiotics were overlapped in May and August. Statistical analysis showed that pH had an important effect on resistant rates of abalone-derived Vibrio isolates to RA, NOR, and ENX. Salinity and dissolved oxygen were negatively correlated with resistant rates of seawater-derived Vibrio isolates to KNA, RA, and PG. Copyright © 2015 Elsevier Ltd. All rights reserved.

Effect of Different Loading Conditions on the Nucleation and Development of Shear Zones Around Material Heterogeneities

NASA Astrophysics Data System (ADS)

Rybacki, E.; Nardini, L.; Morales, L. F.; Dresen, G.

2017-12-01

Rock deformation at depths in the Earth's crust is often localized in high temperature shear zones, which occur in the field at different scales and in a variety of lithologies. The presence of material heterogeneities has long been recognized to be an important cause for shear zones evolution, but the mechanisms controlling initiation and development of localization are not fully understood, and the question of which loading conditions (constant stress or constant deformation rate) are most favourable is still open. To better understand the effect of boundary conditions on shear zone nucleation around heterogeneities, we performed a series of torsion experiments under constant twist rate (CTR) and constant torque (CT) conditions in a Paterson-type deformation apparatus. The sample assemblage consisted of copper-jacketed Carrara marble hollow cylinders with one weak inclusion of Solnhofen limestone. The CTR experiments were performed at maximum bulk strain rates of 1.8-1.9*10-4 s-1, yielding shear stresses of 19-20 MPa. CT tests were conducted at shear stresses between 18.4 and 19.8 MPa resulting in shear strain rates of 1-2*10-4 s-1. All experiments were run at 900 °C temperature and 400 MPa confining pressure. Maximum bulk shear strains (γ) were ca. 0.3 and 1. Strain localized within the host marble in front of the inclusion in an area termed process zone. Here grain size reduction is intense and local shear strain (estimated from markers on the jackets) is up to 8 times higher than the applied bulk strain, rapidly dropping to 2 times higher at larger distance from the inclusion. The evolution of key microstructural parameters such as average grain size and average grain orientation spread (GOS, a measure of lattice distortion) within the process zone, determined by electron backscatter diffraction analysis, differs significantly as a function of loading conditions. Both parameters indicate that, independent of bulk strain and distance from the inclusion, the contribution of small strain-free recrystallized grains is larger in CTR than in CT samples. Our results suggest that loading conditions substantially affect material heterogeneity-induced localization in its nucleation and transient stages.

The Effects of Specimen Geometry on the Plastic Deformation of AA 2219-T8 Aluminum Alloy Under Dynamic Impact Loading

NASA Astrophysics Data System (ADS)

Owolabi, G. M.; Bolling, D. T.; Odeshi, A. G.; Whitworth, H. A.; Yilmaz, N.; Zeytinci, A.

2017-12-01

The effects of specimen geometry on shear strain localization in AA 2219-T8 aluminum alloy under dynamic impact loading were investigated. The alloy was machined into cylindrical, cuboidal and conical (frustum) test specimens. Both deformed and transformed adiabatic shear bands developed in the alloy during the impact loading. The critical strain rate for formation of the deformed band was determined to be 2500 s-1 irrespective of the specimen geometry. The critical strain rate required for formation of transformed band is higher than 3000 s-1 depending on the specimen geometry. The critical strain rate for formation of transformed bands is lowest (3000 s-1) in the Ø5 mm × 5 mm cylindrical specimens and highest (> 6000 s-1) in the conical specimens. The cylindrical specimens showed the greatest tendency to form transformed bands, whereas the conical specimen showed the least tendency. The shape of the shear bands on the impacted plane was also observed to be dependent on the specimen geometry. Whereas the shear bands on the compression plane of the conical specimens formed elongated cycles, two elliptical shaped shear bands facing each other were observed on the cylindrical specimens. Two parallel shear bands were observed on the compression planes of the cuboidal specimens. The dynamic stress-strain curves vary slightly with the specimen geometry. The cuboidal specimens exhibit higher tendency for strain hardening and higher maximum flow stress than the other specimens. The microstructure evolution leading to the formation of transformed bands is also discussed in this paper.

Numerical Study of Head/Helmet Interaction Due to Blast Loading

DTIC Science & Technology

2014-10-01

unidirectional laminate sheets. The MAT_162 material model in LS-DYNA is used to account for the effects of strain rate and strain softening after damage...C., Tan V., Lee H., 2008, “Ballistic Impact of a KEVLAR Helmet: Experimental and Simulations”, International Journal of Impact Engineering, 35, pp

Job demands and job performance: the mediating effect of psychological and physical strain and the moderating effect of role clarity.

PubMed

Lang, Jessica; Thomas, Jeffrey L; Bliese, Paul D; Adler, Amy B

2007-04-01

The aims of the present study were twofold: First, in differentiating between specific job characteristics, the authors examined the moderating influence of role clarity on the relationship between job demands and psychological and physical strain. Second, in providing a more comprehensive link between job demands and job performance, the authors examined strain as a mediator of that relationship. Participants were 1,418 Army cadets attending a 35-day assessment center. Survey data were collected on Day 26 of the assessment center and performance ratings were assessed throughout the assessment center period by expert evaluators. Role clarity was found to moderate the job demands-strain relationship. Specifically, cadets experiencing high demands reported less physical and psychological strain when they reported high role clarity. Moreover, psychological strain significantly mediated the demands-performance relationship. Implications are discussed from theoretical and applied perspectives. Copyright (c) 2007 APA, all rights reserved.

Heart Rate Reduction With Ivabradine Protects Against Left Ventricular Remodeling by Attenuating Infarct Expansion and Preserving Remote-Zone Contractile Function and Synchrony in a Mouse Model of Reperfused Myocardial Infarction.

PubMed

O'Connor, Daniel M; Smith, Robert S; Piras, Bryan A; Beyers, Ronald J; Lin, Dan; Hossack, John A; French, Brent A

2016-04-22

Ivabradine selectively inhibits the pacemaker current of the sinoatrial node, slowing heart rate. Few studies have examined the effects of ivabradine on the mechanical properties of the heart after reperfused myocardial infarction (MI). Advances in ultrasound speckle-tracking allow strain analyses to be performed in small-animal models, enabling the assessment of regional mechanical function. After 1 hour of coronary occlusion followed by reperfusion, mice received 10 mg/kg per day of ivabradine dissolved in drinking water (n=10), or were treated as infarcted controls (n=9). Three-dimensional high-frequency echocardiography was performed at baseline and at days 2, 7, 14, and 28 post-MI. Speckle-tracking software was used to calculate intramural longitudinal myocardial strain (Ell) and strain rate. Standard deviation time to peak radial strain (SD Tpeak Err) and temporal uniformity of strain were calculated from short-axis cines acquired in the left ventricular remote zone. Ivabradine reduced heart rate by 8% to 16% over the course of 28 days compared to controls (P<0.001). On day 28 post-MI, the ivabradine group was found to have significantly smaller end-systolic volumes, greater ejection fraction, reduced wall thinning, and greater peak Ell and Ell rate in the remote zone, as well as globally. Temporal uniformity of strain and SD Tpeak Err were significantly smaller in the ivabradine-treated group by day 28 (P<0.05). High-frequency ultrasound speckle-tracking demonstrated decreased left ventricular remodeling and dyssynchrony, as well as improved mechanical performance in remote myocardium after heart rate reduction with ivabradine. © 2016 The Authors. Published on behalf of the American Heart Association, Inc., by Wiley Blackwell.

Accuracy of speckle tracking in the context of stress echocardiography in short axis view: An in vitro validation study.

PubMed

Hodzic, Amir; Chayer, Boris; Wang, Diya; Porée, Jonathan; Cloutier, Guy; Milliez, Paul; Normand, Hervé; Garcia, Damien; Saloux, Eric; Tournoux, Francois

2018-01-01

This study aimed to test the accuracy of a speckle tracking algorithm to assess myocardial deformation in a large range of heart rates and strain magnitudes compared to sonomicrometry. Using a tissue-mimicking phantom with cyclic radial deformation, radial strain derived from speckle tracking (RS-SpT) of the upper segment was assessed in short axis view by conventional echocardiography (Vivid q, GE) and post-processed with clinical software (EchoPAC, GE). RS-SpT was compared with radial strain measured simultaneously by sonomicrometers (RS-SN). Radial strain was assessed with increasing deformation rates (60 to 160 beats/min) and increasing pulsed volumes (50 to 100 ml/beat) to simulate physiological changes occurring during stress echocardiography. There was a significant correlation (R2 = 0.978, P <0.001) and a close agreement (bias ± 2SD, 0.39 ± 1.5%) between RS-SpT and RS-SN. For low strain values (<15%), speckle tracking showed a small but significant overestimation of radial strain compared to sonomicrometers. Two-way analysis of variance did not show any significant effect of the deformation rate. For RS-SpT, the feasibility was excellent and the intra- and inter-observer variability were low (the intraclass correlation coefficients were 0.96 and 0.97, respectively). Speckle tracking demonstrated a good correlation with sonomicrometry for the assessment of radial strain independently of the heart rate and strain magnitude in a physiological range of values. Though speckle tracking seems to be a reliable and reproducible technique to assess myocardial deformation variations during stress echocardiography, further studies are mandated to analyze the impact of angulated and artefactual out-of-plane motions and inter-vendor variability.

Accuracy of speckle tracking in the context of stress echocardiography in short axis view: An in vitro validation study

PubMed Central

Chayer, Boris; Wang, Diya; Porée, Jonathan; Cloutier, Guy; Milliez, Paul; Normand, Hervé; Garcia, Damien; Saloux, Eric; Tournoux, Francois

2018-01-01

Aim This study aimed to test the accuracy of a speckle tracking algorithm to assess myocardial deformation in a large range of heart rates and strain magnitudes compared to sonomicrometry. Methods and results Using a tissue-mimicking phantom with cyclic radial deformation, radial strain derived from speckle tracking (RS-SpT) of the upper segment was assessed in short axis view by conventional echocardiography (Vivid q, GE) and post-processed with clinical software (EchoPAC, GE). RS-SpT was compared with radial strain measured simultaneously by sonomicrometers (RS-SN). Radial strain was assessed with increasing deformation rates (60 to 160 beats/min) and increasing pulsed volumes (50 to 100 ml/beat) to simulate physiological changes occurring during stress echocardiography. There was a significant correlation (R2 = 0.978, P <0.001) and a close agreement (bias ± 2SD, 0.39 ± 1.5%) between RS-SpT and RS-SN. For low strain values (<15%), speckle tracking showed a small but significant overestimation of radial strain compared to sonomicrometers. Two-way analysis of variance did not show any significant effect of the deformation rate. For RS-SpT, the feasibility was excellent and the intra- and inter-observer variability were low (the intraclass correlation coefficients were 0.96 and 0.97, respectively). Conclusions Speckle tracking demonstrated a good correlation with sonomicrometry for the assessment of radial strain independently of the heart rate and strain magnitude in a physiological range of values. Though speckle tracking seems to be a reliable and reproducible technique to assess myocardial deformation variations during stress echocardiography, further studies are mandated to analyze the impact of angulated and artefactual out-of-plane motions and inter-vendor variability. PMID:29584751

Hyperinsulinemic Normoglycemia does not meaningfully improve Myocardial Performance during Cardiac Surgery: A Randomized Trial

PubMed Central

Duncan, Andra E.; Kashy, Babak Kateby; Sarwar, Sheryar; Singh, Akhil; Stenina-Adognravi, Olga; Christoffersen, Steffen; Alfirevic, Andrej; Sale, Shiva; Yang, Dongsheng; Thomas, James D.; Gillinov, Marc; Sessler, Daniel I.

2015-01-01

Background Glucose-insulin-potassium (GIK) administration during cardiac surgery inconsistently improves myocardial function, perhaps because hyperglycemia negates the beneficial effects of GIK. The hyperinsulinemic normoglycemic clamp (HNC) technique may better enhance the myocardial benefits of GIK. We extended previous GIK investigations by: 1) targeting normoglycemia while administering a glucose-insulin-potassium infusion (HNC); 2) using improved echocardiographic measures of myocardial deformation, specifically myocardial longitudinal strain and strain rate; and, 3) assessing activation of glucose metabolic pathways. Methods 100 patients having aortic valve replacement for aortic stenosis were randomly assigned to HNC (high-dose insulin with concomitant glucose infusion titrated to normoglycemia) versus standard therapy (insulin treatment if glucose >150 mg/dL). Our primary outcomes were left ventricular longitudinal strain and strain rate, assessed using speckle-tracking echocardiography. Right atrial tissue was analyzed for activation of glycolysis/pyruvate oxidation and alternative metabolic pathways. Results Time-weighted mean glucose concentrations were lower with HNC (127±19 mg/dL) than standard care (177±41 mg/dL; P<0.001). Echocardiographic data were adequate in 72 patients for strain analysis and 67 patients for strain rate analysis. HNC did not improve myocardial strain, with an HNC minus standard therapy difference of −1.2 (97.5%CI: −2.9, 0.5)%; P=0.11. Strain rate was significantly better, but by a clinically unimportant amount: −0.16 (−0.30, −0.03) sec−1, P = 0.007. There was no evidence of increased glycolytic, pyruvate oxidation, or hexosamine biosynthetic pathway activation in right atrial samples (n = 20, HNC; 22, standard therapy). Conclusions Administration of glucose and insulin while targeting normoglycemia during aortic valve replacement did not meaningfully improve myocardial function. PMID:26200180

Effect of substrate preheating temperature and coating thickness on residual stress in plasma sprayed hydroxyapatite coating

NASA Astrophysics Data System (ADS)

Tang, Dapei

2015-07-01

A thermal-mechanical coupling model was developed based on thermal-elastic- plastic theory according the special process of plasma spraying Hydroxyapatite (HA) coating upon Ti-6Al-4V substrate. On the one hand, the classical Fourier transient heat conduction equation was modified by introducing the effect item of deformation on temperature, on the other hand, the Johnson-Cook model, suitable for high temperature and high strain rate conditions, was used as constitutive equation after considering temperature softening effect, strain hardening effect and strain rate reinforcement effect. Based on the above coupling model, the residual stress field within the HA coating was simulated by using finite element method (FEM). Meanwhile, the substrate preheating temperature and coating thickness on the influence of residual stress components were calculated, respectively. The failure modes of coating were also preliminary analyzed. In addition, in order to verify the reliability of calculation, the material removal measurement technique was applied to determine the residual stress of HA coating near the interface. Some important conclusions are obtained.

Tensile Strength of Carbon Nanotubes Under Realistic Temperature and Strain Rate

NASA Technical Reports Server (NTRS)

Wei, Chen-Yu; Cho, Kyeong-Jae; Srivastava, Deepak; Biegel, Bryan (Technical Monitor)

2002-01-01

Strain rate and temperature dependence of the tensile strength of single-wall carbon nanotubes has been investigated with molecular dynamics simulations. The tensile failure or yield strain is found to be strongly dependent on the temperature and strain rate. A transition state theory based predictive model is developed for the tensile failure of nanotubes. Based on the parameters fitted from high-strain rate and temperature dependent molecular dynamics simulations, the model predicts that a defect free micrometer long single-wall nanotube at 300 K, stretched with a strain rate of 1%/hour, fails at about 9 plus or minus 1% tensile strain. This is in good agreement with recent experimental findings.

Effect of axial tibial torque direction on ACL relative strain and strain rate in an in vitro simulated pivot landing.

PubMed

Oh, Youkeun K; Kreinbrink, Jennifer L; Wojtys, Edward M; Ashton-Miller, James A

2012-04-01

Anterior cruciate ligament (ACL) injuries most frequently occur under the large loads associated with a unipedal jump landing involving a cutting or pivoting maneuver. We tested the hypotheses that internal tibial torque would increase the anteromedial (AM) bundle ACL relative strain and strain rate more than would the corresponding external tibial torque under the large impulsive loads associated with such landing maneuvers. Twelve cadaveric female knees [mean (SD) age: 65.0 (10.5) years] were tested. Pretensioned quadriceps, hamstring, and gastrocnemius muscle-tendon unit forces maintained an initial knee flexion angle of 15°. A compound impulsive test load (compression, flexion moment, and internal or external tibial torque) was applied to the distal tibia while recording the 3D knee loads and tibofemoral kinematics. AM-ACL relative strain was measured using a 3 mm DVRT. In this repeated measures experiment, the Wilcoxon signed-rank test was used to test the null hypotheses with p < 0.05 considered significant. The mean (±SD) peak AM-ACL relative strains were 5.4 ± 3.7% and 3.1 ± 2.8% under internal and external tibial torque, respectively. The corresponding mean (± SD) peak AM-ACL strain rates reached 254.4 ± 160.1%/s and 179.4 ± 109.9%/s, respectively. The hypotheses were supported in that the normalized mean peak AM-ACL relative strain and strain rate were 70 and 42% greater under internal than under external tibial torque, respectively (p = 0.023, p = 0.041). We conclude that internal tibial torque is a potent stressor of the ACL because it induces a considerably (70%) larger peak strain in the AM-ACL than does a corresponding external tibial torque. Copyright © 2011 Orthopaedic Research Society.

Evidence for initiation of frictional partial slip as the mechanism behind nonlinear stress-strain hysteresis in rock fractures under seismic-frequency torsion

NASA Astrophysics Data System (ADS)

Saltiel, S.; Bonner, B. P.; Delbridge, B. G.; Ajo Franklin, J. B.

2016-12-01

We have adapted a low-frequency (0.1 - 64 Hz) torsional apparatus to explore the pure shear behavior of rock fractures under low normal stresses, simulating low effective stress environments - shallow depths and/or under high pore pressures. The instrument is unique in this ability to measure under very low confinement as well as to probe partial slip on the outside of asperities, before full slip nucleation occurs. Using a sinusoidal oscillation around this condition, we can probe the stress-strain constitutive relation at a range of strain amplitudes and the rate-dependence of the initiation of asperity slip. We find different, nonlinear, stress-strain constitutive relations for dolomite, rhyolite, and granite fractured samples, but all show softening at high strain amplitudes (above microstrain or micron-scale displacement). All measured samples exhibit qualitatively similar time-series hysteresis loops and frequency-dependence. The low frequency stress-strain loops stiffen at the high strain static end of the sinusoidal oscillation. This shape is determined by harmonic generation in the strain, while the stress signal has low power in harmonics, confirming that the driver and electronics are not the source of this nonlinearity. We also observe that this stiffening cusp does not occur as frequency increases above 8 Hz (opposite to normal dispersion seen at higher normal stresses). We monitor the fracture surface wear with repeated cycles to show the extent of slip on mapped asperities. These observations suggest that a rate dependent, healing, process causes the nonlinear responce of fracture faces under low normal stress to periodic shear. We propose that static friction at the low strain-rate part of the cycle, when given enough time at low oscillation frequencies, causes this stiffening cusp shape in the hysteretic stress-strain curve. An analytic model with idealized contact area is used to constrain the rate-state friction constitutive model parameters needed to provide this dynamic behavior.

Ability to Discriminate Between Sustainable and Unsustainable Heat Stress Exposures-Part 2: Physiological Indicators.

PubMed

Garzón-Villalba, Ximena P; Wu, Yougui; Ashley, Candi D; Bernard, Thomas E

2017-07-01

There are times when it is not practical to assess heat stress using environmental metrics and metabolic rate, and heat strain may provide an alternative approach. Heat strain indicators have been used for decades as tools for monitoring physiological responses to work in hot environments. Common indicators of heat strain are body core temperature (assessed here as rectal temperature Tre), heart rate (HR), and average skin temperature (Tsk). Data collected from progressive heat stress trials were used to (1) demonstrate if physiological heat strain indicators (PHSIs) at the upper limit of Sustainable heat stress were below generally accepted limits; (2) suggest values for PHSIs that demonstrate a Sustainable level of heat stress; (3) suggest alternative PHSIs; and (4) determine if metabolic rate was an effect modifier. Two previous progressive heat stress studies included 176 trials with 352 pairs of Sustainable and Unsustainable exposures over a range of relative humidities and metabolic rates using 29 participants. To assess the discrimination ability of PHSIs, conditional logistic regression and stepwise logistic regression were used to find the best combinations of predictors of Unsustainable exposures. The accuracy of the models was assessed using receiver operating characteristic curves. Current recommendations for physiological heat strain limits were associated with probabilities of Unsustainable greater than 0.5. Screening limits for Sustainable heat stress were Tre of 37.5°C, HR of 105 bpm, and Tsk of 35.8°C. Tsk alone resulted in an area under the curve of 0.85 and the combination of Tsk and HR (area under the curve = 0.88) performed the best. The adjustment for metabolic rate was statistically significant for physiological strain index or ∆Tre-sk as main predictors, but its effect modification was negligible and could be ignored. Based on the receiver operating characteristic curve, PHSIs (Tre, HR, and Tsk) can accurately predict Unsustainable heat stress exposures. Tsk alone or in combination with HR has a high sensitivity, and makes better discriminations than the other PHSIs under relatively constant exposure (metabolic rate and environment) for an hour or so. Screening limits with high sensitivity, however, have low thresholds that limit utility. To the extent that the observed strain is low, there is good evidence that the exposure is Sustainable. © The Author 2017. Published by Oxford University Press on behalf of the British Occupational Hygiene Society.

Development and evaluation of the TD97 measles virus vaccine

DOE Office of Scientific and Technical Information (OSTI.GOV)

Suzuki, K.; Morita, M.; Katoh, M.

1990-11-01

The TD97 strain vaccine virus was prepared from the Tanabe strain measles virus by low-temperature passages in primary cell cultures and ultraviolet (UV) mutagenesis. The TD97 strain exhibited the following characteristics: highly temperature sensitive, neither multiplying nor forming any plaques at 40 degrees C in Vero cells; genetically stable, maintaining high temperature sensitivity after ten successive passages in CE cells at 30 degrees C or 35 degrees C; and M proteins of this virus about 1 KD slower in mobility in SDS-PAGE than that of the Tanabe strain. The TD97 strain was further confirmed to be attenuated by an inoculationmore » test into primate brain. In field trials, 752 healthy children were inoculated with a live virus vaccine prepared with this strain, and the following results were obtained: the seroconversion rate was 97% (517/533), and the average HI antibody titer was 2(5.2). An antibody-increasing effect was also observed in children who were initially seropositive. In children who seroconverted, the rates of fever were 15.7% (55/351) for 37.5 degrees C or higher and 4.0% (14/351) for 39 degrees C or higher. The rash rate was 7.7% (27/351), and the incidence of local reaction was 5.4% (19/351). The TD97 strain is thus considered to be suitable in use for an attenuated measles vaccine.« less

Analysis of the Lankford coefficient evolution at different strain rates for AA6016-T4, DP800 and DC06

NASA Astrophysics Data System (ADS)

Lenzen, Matthias; Merklein, Marion

2017-10-01

In the automotive sector, a major challenge is the deep-drawing of modern lightweight sheet metals with limited formability. Thus, conventional material models lack in accuracy due to the complex material behavior. A current field of research takes into account the evolution of the Lankford coefficient. Today, changes in anisotropy under increasing degree of deformation are not considered. Only a consolidated average value of the Lankford coefficient is included in conventional material models. This leads to an increasing error in prediction of the flow behavior and therefore to an inaccurate prognosis of the forming behavior. To increase the accuracy of the prediction quality, the strain dependent Lankford coefficient should be respected, because the R-value has a direct effect on the contour of the associated flow rule. Further, the investigated materials show a more or less extinct rate dependency of the yield stress. For this reason, the rate dependency of the Lankford coefficient during uniaxial tension is focused within this contribution. To quantify the influence of strain rate on the Lankford coefficient, tensile tests are performed for three commonly used materials, the aluminum alloy AA6016-T4, the advanced high strength steel DP800 and the deep drawing steel DC06 at three different strain rates. The strain measurement is carried out by an optical strain measurement system. An evolution of the Lankford coefficient was observed for all investigated materials. Also, an influence of the deformation velocity on the anisotropy could be detected.

Motor unit recruitment patterns 2: the influence of myoelectric intensity and muscle fascicle strain rate.

PubMed

Hodson-Tole, Emma F; Wakeling, James M

2008-06-01

To effectively meet the force requirements of a given movement an appropriate number and combination of motor units must be recruited between and within muscles. Orderly recruitment of motor units has been shown to occur in a wide range of skeletal muscles, however, alternative strategies do occur. Faster motor units are better suited to developing force rapidly, and produce higher mechanical power with greater efficiency at faster shortening strain rates than slower motor units. As the frequency content of the myoelectric signal is related to the fibre type of the active motor units, we hypothesised that, in addition to an association between myoelectric frequency and intensity, there would be a significant association between muscle fascicle shortening strain rate and myoelectric frequency content. Myoelectric and sonomicrometric data were collected from the three ankle extensor muscles of the rat hind limb during walking and running. Myoelectric signals were analysed using wavelet transformation and principal component analysis to give a measure of the signal frequency content. Sonomicrometric signals were analysed to give measures of muscle fascicle strain and strain rate. The relationship between myoelectric frequency and both intensity and muscle fascicle strain rate was found to change across the time course of a stride, with differences also occurring in the strength of the associations between and within muscles. In addition to the orderly recruitment of motor units, a mechanical strategy of motor unit recruitment was therefore identified. Motor unit recruitment is therefore a multifactorial phenomenon, which is more complex than typically thought.

Effect of lineage-specific metabolic traits of Lactobacillus reuteri on sourdough microbial ecology.

PubMed

Lin, Xiaoxi B; Gänzle, Michael G

2014-09-01

This study determined the effects of specific metabolic traits of Lactobacillus reuteri on its competitiveness in sourdoughs. The competitiveness of lactobacilli in sourdough generally depends on their growth rate; acid resistance additionally contributes to competitiveness in sourdoughs with long fermentation times. Glycerol metabolism via glycerol dehydratase (gupCDE) accelerates growth by the regeneration of reduced cofactors; glutamate metabolism via glutamate decarboxylase (gadB) increases acid resistance by generating a proton motive force. Glycerol and glutamate metabolisms are lineage-specific traits in L. reuteri; therefore, this study employed glycerol dehydratase-positive sourdough isolates of human-adapted L. reuteri lineage I, glutamate decarboxylase-positive strains of rodent-adapted L. reuteri lineage II, as well as mutants with deletions in gadB or gupCDE. The competitivenesses of the strains were quantified by inoculation of wheat and sorghum sourdoughs with defined strains, followed by propagation of doughs with a 10% inoculum and 12-h or 72-h fermentation cycles. Lineage I L. reuteri strains dominated sourdoughs propagated with 12-h fermentation cycles; lineage II L. reuteri strains dominated sourdoughs propagated with 72-h fermentation cycles. L. reuteri 100-23ΔgadB was outcompeted by its wild-type strain in sourdoughs fermented with 72-h fermentation cycles; L. reuteri FUA3400ΔgupCDE was outcompeted by its wild-type strain in sourdoughs fermented with both 12-h and 72-h fermentation cycles. Competition experiments with isogenic pairs of strains resulted in a constant rate of strain displacement of the less competitive mutant strain. In conclusion, lineage-specific traits of L. reuteri determine the competitiveness of this species in sourdough fermentations. Copyright © 2014, American Society for Microbiology. All Rights Reserved.

Mechanical Properties of Transgenic Silkworm Silk Under High Strain Rate Tensile Loading

NASA Astrophysics Data System (ADS)

Chu, J.-M.; Claus, B.; Chen, W.

2017-12-01

Studies have shown that transgenic silkworm silk may be capable of having similar properties of spider silk while being mass-producible. In this research, the tensile stress-strain response of transgenic silkworm silk fiber is systematically characterized using a quasi-static load frame and a tension Kolsky bar over a range of strain-rates between 10^{-3} and 700/s. The results show that transgenic silkworm silk tends to have higher overall ultimate stress and failure strain at high strain rate (700/s) compared to quasi-static strain rates, indicating rate sensitivity of the material. The failure strain at the high strain rate is higher than that of spider silk. However, the stress levels are significantly below that of spider silk, and far below that of high-performance fiber. Failure surfaces are examined via scanning electron microscopy and reveal that the failure modes are similar to those of spider silk.

Characterization of a Strain Rate Transient Along the San Andreas and San Jacinto Faults Following the October 1999 Hector Mine Earthquake.

NASA Astrophysics Data System (ADS)

Hernandez, D.; Holt, W. E.; Bennett, R. A.; Dimitrova, L.; Haines, A. J.

2006-12-01

We are continuing work on developing and refining a tool for recognizing strain rate transients as well as for quantifying the magnitude and style of their temporal and spatial variations. We determined time-averaged velocity values in 0.05 year epochs using time-varying velocity estimates for continuous GPS station data from the Southern California Integrated GPS Network (SCIGN) for the time period between October 1999 and February 2004 [Li et al., 2005]. A self-consistent model velocity gradient tensor field solution is determined for each epoch by fitting bi-cubic Bessel interpolation to the GPS velocity vectors and we determine model dilatation strain rates, shear strain rates, and the rotation rates. Departures of the time dependent model strain rate and velocity fields from a master solution, obtained from a time-averaged solution for the period 1999-2004, with imposed plate motion constraints and Quaternary fault data, are evaluated in order to best characterize the time dependent strain rate field. A particular problem in determining the transient strain rate fields is the level of smoothing or damping that is applied. Our current approach is to choose a damping that both maximizes the departure of the transient strain rate field from the long-term master solution and achieves a reduced chi-squared value between model and observed GPS velocities of around 1.0 for all time epochs. We observe several noteworthy time-dependent changes. First, in the Eastern California Shear Zone (ECSZ) region, immediately following the October 1999 Hector Mine earthquake, there occurs a significant spatial increase of relatively high shear strain rate, which encompasses a significant portion of the ECSZ. Second, also following the Hector Mine event, there is a strain rate corridor that extends through the Pinto Mt. fault connecting the ECSZ to the San Andreas fault segment in the Salton Trough region. As this signal slowly decays, shear strain rates on segments of the San Andreas fault, just east of Palm Springs, and the San Jacinto fault increase during 2001-2004. During this period shear strain rates increase by roughly 20 nanostrain per year on the San Andreas fault and 20-30 nanostrain per year on the San Jacinto fault (over a zone approximately 20 km wide). Lastly, a further investigation into this strain rate recovery reveals a power law flow mechanism during the first six months after the earthquake for the Anza segment, after which strain rates appear to reach a steady state for the remainder of the data. Moreover, seismicity rates increase along these segments following the period of shear strain rate increase. These results quantify the spatial coverage of the strain rate changes and provide some bounds on their magnitude and confidence, as well as constraints on the associated regional rheology and interseismic cycle strain rate pattern. The compiled epoch solution "movies" may be viewed at the additional resources site.

Unraveling complex nonlinear elastic behaviors in rocks using dynamic acousto-elasticity

NASA Astrophysics Data System (ADS)

Riviere, J.; Guyer, R.; Renaud, G.; TenCate, J. A.; Johnson, P. A.

2012-12-01

In comparison with standard nonlinear ultrasonic methods like frequency mixing or resonance based measurements that allow one to extract average, bulk variations of modulus and attenuation versus strain level, dynamic acousto-elasticity (DAE) allows to obtain the elastic behavior over the entire dynamic cycle, detailing the full nonlinear behavior under tension and compression, including hysteresis and memory effects. This method consists of exciting a sample in Bulk-mode resonance at strains of 10-7 to 10-5 and simultaneously probing with a sequence of high frequency, low amplitude pulses. Time of flight and amplitudes of these pulses, respectively related to nonlinear elastic and dissipative parameters, can be plotted versus vibration strain level. Despite complex nonlinear signatures obtained for most rocks, it can be shown that for low strain amplitude (< 10-6), the nonlinear classical theory issued from a Taylor decomposition can explain the harmonic content. For higher strain, harmonic content becomes richer and the material exhibits more hysteretic behaviors, i.e. strain rate dependencies. Such observations have been made in the past (e.g., Pasqualini et al., JGR 2007), but not with the extreme detail of elasticity provided by DAE. Previous quasi-static measurements made in Berea sandstone (Claytor et al, GRL 2009), show that the hysteretic behavior disappears when the protocol is performed at a very low strain-rate (static limit). Therefore, future work will aim at linking quasi-static and dynamic observations, i.e. the frequency or strain-rate dependence, in order to understand underlying physical phenomena.

Effect of strain on evolution of dynamic recrystallization in Nb-1 wt%Zr-0.1 wt%C alloy at 1500 and 1600 °C

DOE Office of Scientific and Technical Information (OSTI.GOV)

Behera, A.N.

Uniaxial compression tests were carried out on Nb-1 wt%Zr-0.1 wt%C alloy at temperature of 1500 and 1600 °C and strain rate of 0.1 s{sup −1} to study the evolution of dynamic recrystallization with strain. Electron back scatter diffraction was used to quantify the microstructural evolution. Nb-1Zr-0.1C alloy showed a necklace structure at a strain of 0.9 when deformed at 1500 °C and at strain of 0.6 when deformed at 1600 °C, both at strain rate of 0.1 s{sup −1}. This suggested the occurrence of dynamic recrystallization. At 1500 °C and strain of 0.9 the local average misorientation and the grainmore » orientation spread was low confirming the presence of dynamic recrystallization at this deformation condition. At both 1500 and 1600 °C and all measured strains the recrystallized grains had a strong fiber component of <001>. - Highlights: • Necklace formation of dynamically recrystallized grains occurred at strain of 0.6 and 0.9 for 1500 and 1600 °C, respectively. • Equiaxed microstructures were seen with increase in strain for both 1500 and 1600 °C. • At large strains the predominant recrystallized texture evolved to <001> pole.« less

Influence of strain rate and temperature on tensile properties and flow behaviour of a reduced activation ferritic-martensitic steel

NASA Astrophysics Data System (ADS)

Vanaja, J.; Laha, K.; Sam, Shiju; Nandagopal, M.; Panneer Selvi, S.; Mathew, M. D.; Jayakumar, T.; Rajendra Kumar, E.

2012-05-01

Tensile strength and flow behaviour of a Reduced Activation Ferritic-Martensitic (RAFM) steel (9Cr-1W-0.06Ta-0.22V-0.08C) have been investigated over a temperature range of 300-873 K at different strain rates. Tensile strength of the steel decreased with temperature and increased with strain rate except at intermediate temperatures. Negative strain rate sensitivity of flow stress of the steel at intermediate temperatures revealed the occurrence of dynamic strain ageing in the steel, even though no serrated flow was observed. The tensile flow behaviour of the material was well represented by the Voce strain hardening equation for all the test conditions. Temperature and strain rate dependence of the various parameters of Voce equation were interpreted with the possible deformation mechanisms. The equivalence between the saturation stress at a given strain rate in tensile test and steady state deformation rate at a given stress in creep test was found to be satisfied by the RAFM steel.

Strain-specific functional and numerical responses are required to evaluate impacts on predator-prey dynamics.

PubMed

Yang, Zhou; Lowe, Chris D; Crowther, Will; Fenton, Andy; Watts, Phillip C; Montagnes, David J S

2013-02-01

We use strains recently collected from the field to establish cultures; then, through laboratory studies we investigate how among strain variation in protozoan ingestion and growth rates influences population dynamics and intraspecific competition. We focused on the impact of changing temperature because of its well-established effects on protozoan rates and its ecological relevance, from daily fluctuations to climate change. We show, first, that there is considerable inter-strain variability in thermal sensitivity of maximum growth rate, revealing distinct differences among multiple strains of our model species Oxyrrhis marina. We then intensively examined two representative strains that exhibit distinctly different thermal responses and parameterised the influence of temperature on their functional and numerical responses. Finally, we assessed how these responses alter predator-prey population dynamics. We do this first considering a standard approach, which assumes that functional and numerical responses are directly coupled, and then compare these results with a novel framework that incorporates both functional and numerical responses in a fully parameterised model. We conclude that: (i) including functional diversity of protozoa at the sub-species level will alter model predictions and (ii) including directly measured, independent functional and numerical responses in a model can provide a more realistic account of predator-prey dynamics.

Elevated temperature mechanical properties of line pipe steels

NASA Astrophysics Data System (ADS)

Jacobs, Taylor Roth

The effects of test temperature on the tensile properties of four line pipe steels were evaluated. The four materials include a ferrite-pearlite line pipe steel with a yield strength specification of 359 MPa (52 ksi) and three 485 MPa (70 ksi) yield strength acicular ferrite line pipe steels. Deformation behavior, ductility, strength, strain hardening rate, strain rate sensitivity, and fracture behavior were characterized at room temperature and in the temperature range of 200--350 °C, the potential operating range for steels used in oil production by the steam assisted gravity drainage process. Elevated temperature tensile testing was conducted on commercially produced as-received plates at engineering strain rates of 1.67 x 10 -4, 8.33 x 10-4, and 1.67 x 10-3 s-1. The acicular ferrite (X70) line pipe steels were also tested at elevated temperatures after aging at 200, 275, and 350 °C for 100 h under a tensile load of 419 MPa. The presence of serrated yielding depended on temperature and strain rate, and the upper bound of the temperature range where serrated yielding was observed was independent of microstructure between the ferrite-pearlite (X52) steel and the X70 steels. Serrated yielding was observed at intermediate temperatures and continuous plastic deformation was observed at room temperature and high temperatures. All steels exhibited a minimum in ductility as a function of temperature at testing conditions where serrated yielding was observed. At the higher temperatures (>275 °C) the X52 steel exhibited an increase in ductility with an increase in temperature and the X70 steels exhibited a maximum in ductility as a function of temperature. All steels exhibited a maximum in flow strength and average strain hardening rate as a function of temperature. The X52 steel exhibited maxima in flow strength and average strain hardening rate at lower temperatures than observed for the X70 steels. For all steels, the temperature where the maximum in both flow strength and strain hardening occurred increased with increasing strain rate. Strain rate sensitivities were measured using flow stress data from multiple tensile tests and strain rate jump tests on single tensile samples. In flow stress strain rate sensitivity measurements, a transition from negative to positive strain rate sensitivity was observed in the X52 steel at approximately 275--300 °C, and negative strain rate sensitivity was observed at all elevated temperature testing conditions in the X70 steels. In jump test strain rate sensitivity measurements, all four steels exhibited a transition from negative to positive strain rate sensitivity at approximately 250--275 °C. Anisotropic deformation in the X70 steels was observed by measuring the geometry of the fracture surfaces of the tensile samples. The degree of anisotropy changed as a function of temperature and minima in the degree of anisotropy was observed at approximately 300 °C for all three X70 steels. DSA was verified as an active strengthening mechanism at elevated temperatures for all line pipe steels tested resulting in serrated yielding, a minimum in ductility as a function of temperature, a maximum in flow strength as a function of temperature, a maximum in average strain hardening rate as a function of temperature, and negative strain rate sensitivities. Mechanical properties of the X70 steels exhibited different functionality with respect to temperature compared to the X52 steels at temperatures greater than 250 ºC. Changes in the acicular ferrite microstructure during deformation such as precipitate coarsening, dynamic precipitation, tempering of martensite in martensite-austenite islands, or transformation of retained austenite could account for differences in tensile property functionality between the X52 and X70 steels. Long term aging under load (LTA) testing of the X70 steels resulted in increased yield strength compared to standard elevated temperature tensile tests at all temperatures as a result of static strain aging. LTA specimen ultimate tensile strengths (UTS) increased slightly at 200 °C, were comparable at 275 °C, and decreased significantly at 350 °C when compared to as-received (standard) tests at 350 °C. Observed reductions in UTS were a result of decreased strain hardening in the LTA specimens compared to standard tensile specimens. Ideal elevated temperature operating conditions (based on tensile properties) for the X70 line pipe steels in the temperature range relevant to the steam assisted gravity drainage process are around 275--325 °C at the strain rates tested. In the temperature range of 275--325 °C the X70 steels exhibited continuous plastic deformation, a maximum in ductility, a maximum in flow stress, improved strain hardening compared to intermediate temperatures, reduced anisotropic deformation, and after extended use at elevated temperatures, yield strength increases with little change in UTS.

Bone strain magnitude is correlated with bone strain rate in tetrapods: implications for models of mechanotransduction

PubMed Central

Aiello, B. R.; Iriarte-Diaz, J.; Blob, R. W.; Butcher, M. T.; Carrano, M. T.; Espinoza, N. R.; Main, R. P.; Ross, C. F.

2015-01-01

Hypotheses suggest that structural integrity of vertebrate bones is maintained by controlling bone strain magnitude via adaptive modelling in response to mechanical stimuli. Increased tissue-level strain magnitude and rate have both been identified as potent stimuli leading to increased bone formation. Mechanotransduction models hypothesize that osteocytes sense bone deformation by detecting fluid flow-induced drag in the bone's lacunar–canalicular porosity. This model suggests that the osteocyte's intracellular response depends on fluid-flow rate, a product of bone strain rate and gradient, but does not provide a mechanism for detection of strain magnitude. Such a mechanism is necessary for bone modelling to adapt to loads, because strain magnitude is an important determinant of skeletal fracture. Using strain gauge data from the limb bones of amphibians, reptiles, birds and mammals, we identified strong correlations between strain rate and magnitude across clades employing diverse locomotor styles and degrees of rhythmicity. The breadth of our sample suggests that this pattern is likely to be a common feature of tetrapod bone loading. Moreover, finding that bone strain magnitude is encoded in strain rate at the tissue level is consistent with the hypothesis that it might be encoded in fluid-flow rate at the cellular level, facilitating bone adaptation via mechanotransduction. PMID:26063842

Tissue Doppler, strain, and strain rate echocardiography for the assessment of left and right systolic ventricular function

PubMed Central

Pellerin, D; Sharma, R; Elliott, P; Veyrat, C

2003-01-01

Tissue Doppler (TDE), strain, and strain rate echocardiography are emerging real time ultrasound techniques that provide a measure of wall motion. They offer an objective means to quantify global and regional left and right ventricular function and to improve the accuracy and reproducibility of conventional echocardiography studies. Radial and longitudinal ventricular function can be assessed by the analysis of myocardial wall velocity and displacement indices, or by the analysis of wall deformation using the rate of deformation of a myocardial segment (strain rate) and its deformation over time (strain). A quick and easy assessment of left ventricular ejection fraction is obtained by mitral annular velocity measurement during a routine study, especially in patients with poor endocardial definition or abnormal septal motion. Strain rate and strain are less affected by passive myocardial motion and tend to be uniform throughout the left ventricle in normal subjects. This paper reviews the underlying principles of TDE, strain, and strain rate echocardiography and discusses currently available quantification tools and clinical applications. PMID:14594870

Highly Invasive Listeria monocytogenes Strains Have Growth and Invasion Advantages in Strain Competition

PubMed Central

Manthou, Evanthia; Ciolacu, Luminita; Wagner, Martin; Skandamis, Panagiotis N.

2015-01-01

Multiple Listeria monocytogenes strains can be present in the same food sample; moreover, infection with more than one L. monocytogenes strain can also occur. In this study we investigated the impact of strain competition on the growth and in vitro virulence potential of L. monocytogenes. We identified two strong competitor strains, whose growth was not (or only slightly) influenced by the presence of other strains and two weak competitor strains, which were outcompeted by other strains. Cell contact was essential for growth inhibition. In vitro virulence assays using human intestinal epithelial Caco2 cells showed a correlation between the invasion efficiency and growth inhibition: the strong growth competitor strains showed high invasiveness. Moreover, invasion efficiency of the highly invasive strain was further increased in certain combinations by the presence of a low invasive strain. In all tested combinations, the less invasive strain was outcompeted by the higher invasive strain. Studying the effect of cell contact on in vitro virulence competition revealed a complex pattern in which the observed effects depended only partially on cell-contact suggesting that competition occurs at two different levels: i) during co-cultivation prior to infection, which might influence the expression of virulence factors, and ii) during infection, when bacterial cells compete for the host cell. In conclusion, we show that growth of L. monocytogenes can be inhibited by strains of the same species leading potentially to biased recovery during enrichment procedures. Furthermore, the presence of more than one L. monocytogenes strain in food can lead to increased infection rates due to synergistic effects on the virulence potential. PMID:26529510

Dynamic Tensile Properties of Iron and Steels for a Wide Range of Strain Rates and Strain

NASA Astrophysics Data System (ADS)

Kojima, Nobusato; Hayashi, Hiroyuki; Yamamoto, Terumi; Mimura, Koji; Tanimura, Shinji

The tensile stress-strain curves of iron and a variety of steels, covering a wide range of strength level, over a wide strain rate range on the order of 10-3 ~ 103 s-1, were obtained systematically by using the Sensing Block Type High Speed Material Testing System (SBTS, Saginomiya). Through intensive analysis of these results, the strain rate sensitivity of the flow stress for the large strain region, including the viscous term at high strain rates, the true fracture strength and the true fracture strain were cleared for the material group of the ferrous metals. These systematical data may be useful to develop a practical constitutive model for computer codes, including a fracture criterion for simulations of the dynamic behavior in crash worthiness studies and of work-pieces subjected to dynamic plastic working for a wide strain rate range.

Strain accumulation across the central Nevada seismic zone, 1973-1994

NASA Astrophysics Data System (ADS)

Savage, J. C.; Lisowski, M.; Svarc, J. L.; Gross, W. K.

1995-10-01

Five trilateration networks extending for 280 km along the central Nevada seismic zone (1915 Pleasant Valley, M = 7.3; 1954 Dixie Valley, M = 6.8; 1954 Stillwater, M = 6.8; 1954 Rainbow Mountain, M = 6.6; 1954 Fairview Peak, M = 7.1; and 1932 Cedar Mountain, M = 7.2) have been surveyed 6 times since 1973 to determine deformation along the zone. Within the precision of measurement the deformation appears uniform along the zone and is described by the principal strain rates 0.036±0.008 μstrain/yr N60°W±3° and -0.031±0.008 μstrain/yr N30°E±3°, extension reckoned positive. The observed strain rates are consistent with simple, right-lateral, tensor shear at the rate of 0.033 μstrain/yr across a shear zone striking N15°W. This central Nevada shear zone appears to be the northward continuation of the eastern California shear zone. The orientation of the strike-slip and normal-slip ruptures within the central Nevada seismic zone are consistent with principal stress axes parallel to the measured principal strain rate axes. Space-based geodetic measurements (very long baseline interferometry) indicate that the relative motion accommodated across the Basin and Range province west of Ely, Nevada, is about 9.1±1.5 mm/yr N16°W±8° (Dixon et al., 1995.) Notice that the right-lateral shear zone postulated to explain deformation in the central Nevada seismic zone is properly oriented to accommodate that relative motion. However, a 135-km effective width of the shear zone would be required to accommodate all of the 9.1 mm/yr relative motion at the strain rates observed in the Nevada seismic zone; only about 3 mm/yr of that relative motion is accommodated within the span of the trilateration networks.

The dynamic compressive behavior and constitutive modeling of D1 railway wheel steel over a wide range of strain rates and temperatures

NASA Astrophysics Data System (ADS)

Jing, Lin; Su, Xingya; Zhao, Longmao

The dynamic compressive behavior of D1 railway wheel steel at high strain rates was investigated using a split Hopkinson pressure bar (SHPB) apparatus. Three types of specimens, which were derived from the different positions (i.e., the rim, web and hub) of a railway wheel, were tested over a wide range of strain rates from 10-3 s-1 to 2.4 × 103 s-1 and temperatures from 213 K to 973 K. Influences of the strain rate and temperature on flow stress were discussed, and rate- and temperature-dependent constitutive relationships were assessed by the Cowper-Symonds model, Johnson-Cook model and a physically-based model, respectively. The experimental results show that the compressive true stress versus true strain response of D1 wheel steel is strain rate-dependent, and the strain hardening rate during the plastic flow stage decreases with the elevation of strain rate. Besides, the D1 wheel steel displays obvious temperature-dependence, and the third-type strain aging (3rd SA) is occurred at the temperature region of 673-973 K at a strain rate of ∼1500 s-1. Comparisons of experimental results with theoretical predictions indicate that the physically-based model has a better prediction capability for the 3rd SA characteristic of the tested D1 wheel steel.

Strain rate dependent calcite microfabric evolution - an experiment carried out by nature

NASA Astrophysics Data System (ADS)

Rogowitz, A.; Huet, B.; Grasemann, B.; Habler, G.

2013-12-01

The deformation behaviour of calcite has been studied extensively in a number of experiments. Different strain rates and pressure and temperature conditions have been used to investigate a wide range of deformation regimes. However, a direct comparison with natural fault rocks remains difficult because of extreme differences between experimental and natural strain rates. A secondary shear zone (flanking structure) developed in almost pure calcite marble on Syros (Greece). Due to rotation of an elliptical inclusion (crack) a heterogeneous strain field in the surrounding area occurred resulting in different strain domains and the formation of the flanking structure. Assuming that deformation was active continuously during the development of the flanking structure, the different strain domains correspond to different strain-rate domains. The outcrop thus represents the final state of a natural experiment and gives us a great opportunity to get natural constraints on strain rate dependent deformation behaviour of calcite. Comparing the microfabrics in the 1 to 2.5 cm thick shear zone and the surrounding host rocks, which formed under the same metamorphic conditions but with different strain rates, is the central focus of this study. Due to the extreme variation in strain and strain rate, different microstructures and textures can be observed corresponding to different deformation mechanisms. With increasing strain rate we observe a change in dominant deformation mechanism from dislocation glide to dislocation creep and finally diffusion creep. Additionally, a change from subgrain rotation (SGR) to bulging (BLG) recrystallization can be observed in the dislocation creep regime. Textures and the degree of intracrystalline deformation have been measured by electron back scatter diffraction (EBSD). At all strain rates clear CPOs developed leading to the assumption that calcite preferentially deforms within the dislocation creep field. However, we can also find clear evidence for grain size sensitive deformation mechanisms at smaller grain sizes (3.6 μm) consistent with experimental observations and determined flaw laws. Although mylonitic layers evolve at high (10^-10 s^-1) and intermediate strain rates (10^-11 s^-1) by SGR recrystallization we observe variations in texture leading to the assumption that at varying strain rates different gliding systems were active. The results of this study are compared with experimental data, closing the gap between experimental and natural geological strain rates.

Organised Genome Dynamics in the Escherichia coli Species Results in Highly Diverse Adaptive Paths

PubMed Central

Barbe, Valérie; Baeriswyl, Simon; Bidet, Philippe; Bingen, Edouard; Bonacorsi, Stéphane; Bouchier, Christiane; Bouvet, Odile; Calteau, Alexandra; Chiapello, Hélène; Clermont, Olivier; Cruveiller, Stéphane; Danchin, Antoine; Diard, Médéric; Dossat, Carole; Karoui, Meriem El; Frapy, Eric; Garry, Louis; Ghigo, Jean Marc; Gilles, Anne Marie; Johnson, James; Le Bouguénec, Chantal; Lescat, Mathilde; Mangenot, Sophie; Martinez-Jéhanne, Vanessa; Matic, Ivan; Nassif, Xavier; Oztas, Sophie; Petit, Marie Agnès; Pichon, Christophe; Rouy, Zoé; Ruf, Claude Saint; Schneider, Dominique; Tourret, Jérôme; Vacherie, Benoit; Vallenet, David; Médigue, Claudine; Rocha, Eduardo P. C.; Denamur, Erick

2009-01-01

The Escherichia coli species represents one of the best-studied model organisms, but also encompasses a variety of commensal and pathogenic strains that diversify by high rates of genetic change. We uniformly (re-) annotated the genomes of 20 commensal and pathogenic E. coli strains and one strain of E. fergusonii (the closest E. coli related species), including seven that we sequenced to completion. Within the ∼18,000 families of orthologous genes, we found ∼2,000 common to all strains. Although recombination rates are much higher than mutation rates, we show, both theoretically and using phylogenetic inference, that this does not obscure the phylogenetic signal, which places the B2 phylogenetic group and one group D strain at the basal position. Based on this phylogeny, we inferred past evolutionary events of gain and loss of genes, identifying functional classes under opposite selection pressures. We found an important adaptive role for metabolism diversification within group B2 and Shigella strains, but identified few or no extraintestinal virulence-specific genes, which could render difficult the development of a vaccine against extraintestinal infections. Genome flux in E. coli is confined to a small number of conserved positions in the chromosome, which most often are not associated with integrases or tRNA genes. Core genes flanking some of these regions show higher rates of recombination, suggesting that a gene, once acquired by a strain, spreads within the species by homologous recombination at the flanking genes. Finally, the genome's long-scale structure of recombination indicates lower recombination rates, but not higher mutation rates, at the terminus of replication. The ensuing effect of background selection and biased gene conversion may thus explain why this region is A+T-rich and shows high sequence divergence but low sequence polymorphism. Overall, despite a very high gene flow, genes co-exist in an organised genome. PMID:19165319

Modeling of Impression Testing to Obtain Mechanical Properties of Lead-Free Solders Microelectronic Interconnects

DTIC Science & Technology

2005-12-01

hardening exponent and Cimp is the impression strain-rate hardening coefficient. The strain-rate hardening exponent m is a parameter that is...exponent and Cimp is the impression strain-rate hardening coefficient. The strain-rate hardening exponent m is a parameter that is related to the creep

The present state and future direction of second order closure models for compressible flows

NASA Technical Reports Server (NTRS)

Gatski, Thomas B.; Sarkar, Sutanu; Speziale, Charles G.

1992-01-01

The topics are presented in viewgraph form and include: (1) Reynolds stress closure models; (2) Favre averages and governing equations; (3) the model for the deviatoric part of the pressure-strain rate correlation; (4) the SSG pressure-strain correlation model; (5) a compressible turbulent dissipation rate model; (6) variable viscosity effects; (7) near-wall stiffness problems; (8) models of the Reynolds mass and heat flux; and (9) a numerical solution of the compressible turbulent transport equation.

Effect of chemistry and turbulence on NO formation in oxygen-natural gas flames

NASA Technical Reports Server (NTRS)

Samaniego, J. -M.; Egolfopoulos, F. N.; Bowman, C. T.

1996-01-01

The effects of chemistry and turbulence on NO formation in oxygen-natural turbulent diffusion flames gas flames have been investigated. The chemistry of nitric oxides has been studied numerically in the counterflow configuration. Systematic calculations with the GRI 2.11 mechanism for combustion of methane and NO chemistry were conducted to provide a base case. It was shown that the 'simple' Zeldovich mechanism accounts for more than 75% of N2 consumption in the flame in a range of strain-rates varying between 10 and 1000 s-l. The main shortcomings of this mechanism are: 1) overestimation (15%) of the NO production rate at low strain-rates because it does not capture the reburn due to the hydrocarbon chemistry, and 2) underestimation (25%) of the NO production rate at high strainrates because it ignores NO production through the prompt mechanism. Reburn through the Zeldovich mechanism alone proves to be significant at low strain-rates. A one-step model based on the Zeldovich mechanism and including reburn has been developed. It shows good agreement with the GRI mechanism at low strain-rates but underestimates significantly N2 consumption (about 50%) at high strain-rates. The role of turbulence has been assessed by using an existing 3-D DNS data base of a diffusion flame in decaying turbulence. Two PDF closure models used in practical industrial codes for turbulent NO formation have been tested. A simpler version of the global one-step chemical scheme for NO compared to that developed in this study was used to test the closure assumptions of the PDF models, because the data base could not provide all the necessary ingredients. Despite this simplification, it was possible to demonstrate that the current PDF models for NO overestimate significantly the NO production rate due to the fact that they neglect the correlations between the fluctuations in oxygen concentration and temperature. A single scalar PDF model for temperature that accounts for such correlations based on laminar flame considerations has been developed and showed excellent agreement with the values given by the DNS.

Job strain associated with increases in ambulatory blood and pulse pressure during and after work hours among female hotel room cleaners.

PubMed

Feaster, Matt; Krause, Niklas

2018-06-01

Previously documented elevated hypertension rates among Las Vegas hotel room cleaners are hypothesized to be associated with job strain. Job strain was assessed by questionnaire. Ambulatory blood pressure (ABP) was recorded among 419 female cleaners from five hotels during 18 waking hours. Multiple linear regression models assessed associations of job strain with ABP and pulse pressure for 18-h, work hours, and after work hours. Higher job strain was associated with increased 18-h systolic ABP, after work hours systolic ABP, and ambulatory pulse pressure. Dependents at home but not social support at work attenuated effects. Among hypertensive workers, job strain effects were partially buffered by anti-hypertensive medication. High job strain is positively associated with blood pressure among female hotel workers suggesting potential for primary prevention at work. Work organizational changes, stress management, and active ABP surveillance and hypertension management should be considered for integrated intervention programs. © 2018 Wiley Periodicals, Inc.

An optimized strain demodulation method for PZT driven fiber Fabry-Perot tunable filter

NASA Astrophysics Data System (ADS)

Sheng, Wenjuan; Peng, G. D.; Liu, Yang; Yang, Ning

2015-08-01

An optimized strain-demodulation-method based on piezo-electrical transducer (PZT) driven fiber Fabry-Perot (FFP) filter is proposed and experimentally demonstrated. Using a parallel processing mode to drive the PZT continuously, the hysteresis effect is eliminated, and the system demodulation rate is increased. Furthermore, an AC-DC compensation method is developed to address the intrinsic nonlinear relationship between the displacement and voltage of PZT. The experimental results show that the actual demodulation rate is improved from 15 Hz to 30 Hz, the random error of the strain measurement is decreased by 95%, and the deviation between the test values after compensation and the theoretical values is less than 1 pm/με.

Measurement of the mechanical properties of car body sheet steels at high strain rates and non ambient temperature

NASA Astrophysics Data System (ADS)

Bleck, W.; Larour, P.

2003-09-01

Crash behaviour and light weight have become the major design criteria for car bodies. Modem high strength steels offer appropriate solutions for these requirements. The prediction of the crash behaviour in simulation programs requires the information on materials behaviour during dynamic testing. The reduction of the signal waviness and the inertia effects at strain rates above 50s^{-1} are major issues in dynamic tensile testing. Damping techniques or load measurement on the sample itself are the common way to reduce oscillations. Strain measurement from the piston displacement or from optical devices on the specimen itself are also compared. Advantages and drawbacks of those various measurement techniques are presented.

Chronic Sublethal Effects of Cantharidin on the Diamondback Moth Plutella xylostella (Lepidoptera: Plutellidae).

PubMed

Huang, Zhengyu; Zhang, Yalin

2015-05-29

The diamondback moth, Plutella xylostella (Linnaeus) (Lepidoptera: Plutellidae), is a major pest of cruciferous vegetables worldwide. Cantharidin, a natural toxin isolated from blister beetles, has been reported to be toxic to P. xylostella. However, little is known on the chronic sublethal effects of cantharidin on this species. In this study, we assessed the changes of susceptibility, development, reproduction and other demographic parameters in both the selected P. xylostella strain (Sub, selected by LC25 cantharidin for consecutive 12 generations) and the revertant strain (SubR, derived from the Sub strain without being exposed to cantharidin for 12 generations). Results revealed that the two strains maintained a relatively high-level susceptibility to cantharidin. Severe adverse effects on the population dynamics and fitness in Sub strain were observed. In addition, repeated exposure of P. xylostella to sublethal concentration of cantharidin resulted in negative effects on adult performance and deformities in adults. Although morphologically normal for individuals, the SubR strain exhibited a disadvantage in population growth rate. Our results showed that sublethal concentration of cantharidin exhibited severe negative effects on population growth for longtime. These findings would be useful for assessing the potential effects and risk of cantharidin on P. xylostella and for developing effective integrated pest management.

Chronic Sublethal Effects of Cantharidin on the Diamondback Moth Plutella xylostella (Lepidoptera: Plutellidae)

PubMed Central

Huang, Zhengyu; Zhang, Yalin

2015-01-01

The diamondback moth, Plutella xylostella (Linnaeus) (Lepidoptera: Plutellidae), is a major pest of cruciferous vegetables worldwide. Cantharidin, a natural toxin isolated from blister beetles, has been reported to be toxic to P. xylostella. However, little is known on the chronic sublethal effects of cantharidin on this species. In this study, we assessed the changes of susceptibility, development, reproduction and other demographic parameters in both the selected P. xylostella strain (Sub, selected by LC25 cantharidin for consecutive 12 generations) and the revertant strain (SubR, derived from the Sub strain without being exposed to cantharidin for 12 generations). Results revealed that the two strains maintained a relatively high-level susceptibility to cantharidin. Severe adverse effects on the population dynamics and fitness in Sub strain were observed. In addition, repeated exposure of P. xylostella to sublethal concentration of cantharidin resulted in negative effects on adult performance and deformities in adults. Although morphologically normal for individuals, the SubR strain exhibited a disadvantage in population growth rate. Our results showed that sublethal concentration of cantharidin exhibited severe negative effects on population growth for longtime. These findings would be useful for assessing the potential effects and risk of cantharidin on P. xylostella and for developing effective integrated pest management. PMID:26035491

Earthquake potential in California-Nevada implied by correlation of strain rate and seismicity

USGS Publications Warehouse

Zeng, Yuehua; Petersen, Mark D.; Shen, Zheng-Kang

2018-01-01

Rock mechanics studies and dynamic earthquake simulations show that patterns of seismicity evolve with time through (1) accumulation phase, (2) localization phase, and (3) rupture phase. We observe a similar pattern of changes in seismicity during the past century across California and Nevada. To quantify these changes, we correlate GPS strain rates with seismicity. Earthquakes of M > 6.5 are collocated with regions of highest strain rates. By contrast, smaller magnitude earthquakes of M ≥ 4 show clear spatiotemporal changes. From 1933 to the late 1980s, earthquakes of M ≥ 4 were more diffused and broadly distributed in both high and low strain rate regions (accumulation phase). From the late 1980s to 2016, earthquakes were more concentrated within the high strain rate areas focused on the major fault strands (localization phase). In the same time period, the rate of M > 6.5 events also increased significantly in the high strain rate areas. The strong correlation between current strain rate and the later period of seismicity indicates that seismicity is closely related to the strain rate. The spatial patterns suggest that before the late 1980s, the strain rate field was also broadly distributed because of the stress shadows from previous large earthquakes. As the deformation field evolved out of the shadow in the late 1980s, strain has refocused on the major fault systems and we are entering a period of increased risk for large earthquakes in California.

Earthquake Potential in California-Nevada Implied by Correlation of Strain Rate and Seismicity

NASA Astrophysics Data System (ADS)

Zeng, Yuehua; Petersen, Mark D.; Shen, Zheng-Kang

2018-02-01

Rock mechanics studies and dynamic earthquake simulations show that patterns of seismicity evolve with time through (1) accumulation phase, (2) localization phase, and (3) rupture phase. We observe a similar pattern of changes in seismicity during the past century across California and Nevada. To quantify these changes, we correlate GPS strain rates with seismicity. Earthquakes of M > 6.5 are collocated with regions of highest strain rates. By contrast, smaller magnitude earthquakes of M ≥ 4 show clear spatiotemporal changes. From 1933 to the late 1980s, earthquakes of M ≥ 4 were more diffused and broadly distributed in both high and low strain rate regions (accumulation phase). From the late 1980s to 2016, earthquakes were more concentrated within the high strain rate areas focused on the major fault strands (localization phase). In the same time period, the rate of M > 6.5 events also increased significantly in the high strain rate areas. The strong correlation between current strain rate and the later period of seismicity indicates that seismicity is closely related to the strain rate. The spatial patterns suggest that before the late 1980s, the strain rate field was also broadly distributed because of the stress shadows from previous large earthquakes. As the deformation field evolved out of the shadow in the late 1980s, strain has refocused on the major fault systems and we are entering a period of increased risk for large earthquakes in California.

Peculiarities of dislocation motion in aluminum with allowance for the Peierls relief in the presence of ultrasound

NASA Astrophysics Data System (ADS)

Arakelyan, M. M.

2017-11-01

The effect of ultrasound on motion of the Frenkel-Kontorova dislocations in aluminum has been studied with inclusion of the Peierls relief. A dislocation moves at a variable rate when overcoming the Peierls barrier. The dislocation mean free path is changed under action of ultrasound at various frequencies comparable to the dislocation transition time to a neighboring valley. The stress-strain dependences have been obtained for high and low strain rates. In both the cases, a disordering takes place; however, the disordering rates and characters are different. At the resonance frequency, the strain resistance decreases, the hardening stage is shortened and the disordering stage is elongated. The dependence of the coefficient of hardening on coordinate has three segments different in characters. The coefficient of hardening decreases at the resonance frequency.

Effect of High Strain-Rate Deformation and Aging Temperature on the Evolution of Structure, Microhardness, and Wear Resistance of Low-Alloyed Cu-Cr-Zr Alloy

NASA Astrophysics Data System (ADS)

Kheifets, A. E.; Khomskaya, I. V.; Korshunov, L. G.; Zel'dovich, V. I.; Frolova, N. Yu.

2018-04-01

The effect of the preliminary high strain-rate deformation, performed via the method of dynamic channel-angular pressing (DCAP), and subsequent annealings on the tribological properties of a dispersionhardened Cu-0.092 wt % Cr-0.086 wt % Zr alloy has been investigated. It has been shown that the surfacelayer material of the alloy with a submicrocrystalline (SMC) structure obtained by the DCAP method can be strengthened using severe plastic deformation by sliding friction at the expense of creating a nanocrystalline structure with crystallites of 15-60 nm in size. It has been shown that the SMC structure obtained by the high strain-rate DCAP deformation decreases the wear rate of the samples upon sliding friction by a factor of 1.4 compared to the initial coarse-grained state. The maximum values of the microhardness and minimum values of the coefficient of friction and shear strength have been obtained in the samples preliminarily subjected to DCAP and aging at 400°C. The attained level of microhardness is 3350 MPa, which exceeds the microhardness of the alloy in the initial coarse-grained state by five times.

Identification and evaluation of a new entomopathogenic fungal strain against Riptortus pedestris (Hemiptera: Alydidae) and its two egg parasitoids

PubMed Central

Lim, Un Taek

2018-01-01

A strain (ARP14) of the entomopathogenic fungus Beauveria bassiana (Balsamo) Vuillemin was isolated from field-collected Riptortus pedestris (Fabricius) (Hemiptera: Alydidae). The lethal median concentration of the ARP14 strain was compared with that of a commercialized strain (GHA) of the same fungus against R. pedestris and its two egg parasitoids, Ooencyrtus nezarae Ishii (Hymenoptera: Encyrtidae) and Gryon japonicum (Ashmead) (Hymenoptera: Platygastridae). Mortality and mycosis rates were evaluated after exposure to five concentrations of the fungus, i.e., 1×109, 1×108, 1×107, 1×106, and 1×105 conidia/mL, using a glass scintillation vial as an exposure arena in 25.0 ± 0.5°C and 93.7 ± 2.9% RH. The lethal median concentrations (LC50) for 2nd and 4th instar nymphs, and adults of R. pedestris were not significantly different between the two strains of B. bassiana. However, the mycosis rate of ARP14 was 1.3 and 1.8 times higher than that of the GHA strain in 4th instar nymphs and adult females of R. pedestris, respectively, at the 1×108 conidia/mL concentration. More interestingly, the mycosis rates at 1×108 conidia/mL concentration in the parasitoids G. japonicum and O. nezarae were much lower in the ARP14 strain (15.0 and 0%) than in the GHA strain (73.3 and 66.0%), respectively, suggesting that the B. bassiana strain ARP14 is less virulent to these parasitoids than the commercially available strain. Our results suggest that B. bassiana ARP14 may be a potential new biopesticide against R. pedestris with fewer negative effects on beneficial parasitoids than currently available options. PMID:29664929

Identification and evaluation of a new entomopathogenic fungal strain against Riptortus pedestris (Hemiptera: Alydidae) and its two egg parasitoids.

PubMed

Dangi, Naresh; Lim, Un Taek

2018-01-01

A strain (ARP14) of the entomopathogenic fungus Beauveria bassiana (Balsamo) Vuillemin was isolated from field-collected Riptortus pedestris (Fabricius) (Hemiptera: Alydidae). The lethal median concentration of the ARP14 strain was compared with that of a commercialized strain (GHA) of the same fungus against R. pedestris and its two egg parasitoids, Ooencyrtus nezarae Ishii (Hymenoptera: Encyrtidae) and Gryon japonicum (Ashmead) (Hymenoptera: Platygastridae). Mortality and mycosis rates were evaluated after exposure to five concentrations of the fungus, i.e., 1×109, 1×108, 1×107, 1×106, and 1×105 conidia/mL, using a glass scintillation vial as an exposure arena in 25.0 ± 0.5°C and 93.7 ± 2.9% RH. The lethal median concentrations (LC50) for 2nd and 4th instar nymphs, and adults of R. pedestris were not significantly different between the two strains of B. bassiana. However, the mycosis rate of ARP14 was 1.3 and 1.8 times higher than that of the GHA strain in 4th instar nymphs and adult females of R. pedestris, respectively, at the 1×108 conidia/mL concentration. More interestingly, the mycosis rates at 1×108 conidia/mL concentration in the parasitoids G. japonicum and O. nezarae were much lower in the ARP14 strain (15.0 and 0%) than in the GHA strain (73.3 and 66.0%), respectively, suggesting that the B. bassiana strain ARP14 is less virulent to these parasitoids than the commercially available strain. Our results suggest that B. bassiana ARP14 may be a potential new biopesticide against R. pedestris with fewer negative effects on beneficial parasitoids than currently available options.

Evaluation of Strains of Metarhizium anisopliae and Beauveria bassiana against Spodoptera litura on the Basis of Their Virulence, Germination Rate, Conidia Production, Radial Growth and Enzyme Activity.

PubMed

Petlamul, Wanida; Prasertsan, Poonsuk

2012-06-01

Ten strains of the entomopathogenic fungi Metarhizium anisopliae and Beauveria bassiana were evaluated to find the most effective strain for optimization studies. The first criterion tested for strain selection was the mortality (> 50%) of Spodoptera litura larvae after inoculation of the fungus for 4 days. Results on several bioassays revealed that B. bassiana BNBCRC showed the most virulence on mortality S. litura larvae (80% mortality). B. bassiana BNBCRC also showed the highest germination rate (72.22%). However, its conidia yield (7.2 × 10(8) conidia/mL) was lower than those of B. bassiana B 14841 (8.3 × 10(8) conidia/mL) and M. anisopliae M6 (8.2 × 10(8) conidia/mL). The highest accumulative radial growth was obtained from the strain B14841 (37.10 mm/day) while the strain BNBCRC showed moderate radial growth (24.40 mm/day). M. anisopliae M6 possessed the highest protease activity (145.00 mU/mL) while M. anisopliae M8 possessed the highest chitinase activity (20.00 mU/mL) during 96~144 hr cultivation. Amongst these criteria, selection based on virulence and germination rate lead to the selection of B. bassiana BNBCRC. B. bassiana B14841 would be selected if based on growth rate while M. anisopliae M6 and M8 possessed the highest enzyme activities.

Nonlinearity and Strain-Rate Dependence in the Deformation Response of Polymer Matrix Composites Modeled

NASA Technical Reports Server (NTRS)

Goldberg, Robert K.

2000-01-01

There has been no accurate procedure for modeling the high-speed impact of composite materials, but such an analytical capability will be required in designing reliable lightweight engine-containment systems. The majority of the models in use assume a linear elastic material response that does not vary with strain rate. However, for containment systems, polymer matrix composites incorporating ductile polymers are likely to be used. For such a material, the deformation response is likely to be nonlinear and to vary with strain rate. An analytical model has been developed at the NASA Glenn Research Center at Lewis Field that incorporates both of these features. A set of constitutive equations that was originally developed to analyze the viscoplastic deformation of metals (Ramaswamy-Stouffer equations) was modified to simulate the nonlinear, rate-dependent deformation of polymers. Specifically, the effects of hydrostatic stresses on the inelastic response, which can be significant in polymers, were accounted for by a modification of the definition of the effective stress. The constitutive equations were then incorporated into a composite micromechanics model based on the mechanics of materials theory. This theory predicts the deformation response of a composite material from the properties and behavior of the individual constituents. In this manner, the nonlinear, rate-dependent deformation response of a polymer matrix composite can be predicted.

Stress in nonregular work arrangements: A longitudinal study of task- and employment-related aspects of stress.

PubMed

Vahle-Hinz, Tim

2016-10-01

In nonregular forms of employment, such as fixed-term or temporary agency work, 2 sources of stress must be distinguished: task-related stress components (e.g., time pressure) and employment-related stress components (e.g., effort to maintain employment). The present study investigated the relationship between task- and employment-related demands and resources and indicators of strain, well-being, work engagement, and self-rated performance in a sample of nonregular employed workers. Using a 2-wave longitudinal design, the results of autoregressive cross-lagged structural equation models demonstrated that time pressure, as a task-related demand, is positively related to strain and negatively related to well-being and self-rated performance. Autonomy, as a task-related resource, exhibited no significant relationships in the current study. Employment-related demands exhibited negative relationships with well-being and work engagement as well as negative and positive relationships with self-rated performance over time. Employment-related resources were primarily positive predictors of well-being and self-rated performance. Fit indices of comparative models indicated that reciprocal effect models (which enable causal and reverse effects) best fit the data. Accordingly, demands and resources predicted strain, well-being, work engagement, and self-rated performance over time and vice versa. (PsycINFO Database Record (c) 2016 APA, all rights reserved).

Bacillus subtilis from Soybean Food Shows Antimicrobial Activity for Multidrug-Resistant Acinetobacter baumannii by Affecting the adeS Gene.

PubMed

Wang, Tieshan; Su, Jianrong

2016-12-28

Exploring novel antibiotics is necessary for multidrug-resistant pathogenic bacteria. Because the probiotics in soybean food have antimicrobial activities, we investigated their effects on multidrug-resistant Acinetobacter baumannii . Nineteen multidrug-resistant A. baumannii strains were clinifcally isolated as an experimental group and 11 multidrug-sensitive strains as controls. The growth rates of all bacteria were determined by using the analysis for xCELLigence Real-Time Cell. The combination of antibiotics showed synergistic effects on the strains in the control group but no effect on the strains in the experimental group. Efflux pump gene adeS was absent in all the strains from the control group, whereas it exists in all the strains from the experimental group. Furthermore, all the strains lost multidrug resistance when an adeS inhibitor was used. One strain of probiotics isolated from soybean food showed high antimicrobial activity for multidrug-resistant A. baumannii . The isolated strain belongs to Bacillus subtilis according to 16S RNA analysis. Furthermore, E. coli showed multidrug resistance when it was transformed with the adeS gene from A. baumannii whereas the resistant bacteria could be inhibited completely by isolated Bacillus subtilis . Thus, probiotics from soybean food provide potential antibiotics against multidrug-resistant pathogenic bacteria.

Ultra High Strain Rate Nanoindentation Testing.

PubMed

Sudharshan Phani, Pardhasaradhi; Oliver, Warren Carl

2017-06-17

Strain rate dependence of indentation hardness has been widely used to study time-dependent plasticity. However, the currently available techniques limit the range of strain rates that can be achieved during indentation testing. Recent advances in electronics have enabled nanomechanical measurements with very low noise levels (sub nanometer) at fast time constants (20 µs) and high data acquisition rates (100 KHz). These capabilities open the doors for a wide range of ultra-fast nanomechanical testing, for instance, indentation testing at very high strain rates. With an accurate dynamic model and an instrument with fast time constants, step load tests can be performed which enable access to indentation strain rates approaching ballistic levels (i.e., 4000 1/s). A novel indentation based testing technique involving a combination of step load and constant load and hold tests that enables measurement of strain rate dependence of hardness spanning over seven orders of magnitude in strain rate is presented. A simple analysis is used to calculate the equivalent uniaxial response from indentation data and compared to the conventional uniaxial data for commercial purity aluminum. Excellent agreement is found between the indentation and uniaxial data over several orders of magnitude of strain rate.

Creep Strain and Strain Rate Response of 2219 Al Alloy at High Stress Levels

NASA Technical Reports Server (NTRS)

Taminger, Karen M. B.; Wagner, John A.; Lisagor, W. Barry

1998-01-01

As a result of high localized plastic deformation experienced during proof testing in an International Space Station connecting module, a study was undertaken to determine the deformation response of a 2219-T851 roll forging. After prestraining 2219-T851 Al specimens to simulate strains observed during the proof testing, creep tests were conducted in the temperature range from ambient temperature to 107 C (225 F) at stress levels approaching the ultimate tensile strength of 2219-T851 Al. Strain-time histories and strain rate responses were examined. The strain rate response was extremely high initially, but decayed rapidly, spanning as much as five orders of magnitude during primary creep. Select specimens were subjected to incremental step loading and exhibited initial creep rates of similar magnitude for each load step. Although the creep rates decreased quickly at all loads, the creep rates dropped faster and reached lower strain rate levels for lower applied loads. The initial creep rate and creep rate decay associated with primary creep were similar for specimens with and without prestrain; however, prestraining (strain hardening) the specimens, as in the aforementioned proof test, resulted in significantly longer creep life.

Relationships of left ventricular strain and strain rate to wall stress and their afterload dependency.

PubMed

Murai, Daisuke; Yamada, Satoshi; Hayashi, Taichi; Okada, Kazunori; Nishino, Hisao; Nakabachi, Masahiro; Yokoyama, Shinobu; Abe, Ayumu; Ichikawa, Ayako; Ono, Kota; Kaga, Sanae; Iwano, Hiroyuki; Mikami, Taisei; Tsutsui, Hiroyuki

2017-05-01

Whether and how left ventricular (LV) strain and strain rate correlate with wall stress is not known. Furthermore, it is not determined whether strain or strain rate is less dependent on the afterload. In 41 healthy young adults, LV global peak strain and systolic peak strain rate in the longitudinal direction (LS and LSR, respectively) and circumferential direction (CS and CSR, respectively) were measured layer-specifically using speckle tracking echocardiography (STE) before and during a handgrip exercise. Among all the points before and during the exercise, all the STE parameters significantly correlated linearly with wall stress (LS: r = -0.53, p < 0.01, LSR: r = -0.28, p < 0.05, CS in the inner layer: r = -0.72, p < 0.01, CSR in the inner layer: r = -0.47, p < 0.01). Strain more strongly correlated with wall stress than strain rate (r = -0.53 for LS vs. r = -0.28 for LSR, p < 0.05; r = -0.72 for CS vs. r = -0.47 for CSR in the inner layer, p < 0.05), whereas the interobserver variability was similar between strain and strain rate (longitudinal 6.2 vs. 5.2 %, inner circumferential 4.8 vs. 4.7 %, mid-circumferential 7.9 vs. 6.9 %, outer circumferential 10.4 vs. 9.7 %), indicating that the differences in correlation coefficients reflect those in afterload dependency. It was thus concluded that LV strain and strain rate linearly and inversely correlated with wall stress in the longitudinal and circumferential directions, and strain more strongly depended on afterload than did strain rate. Myocardial shortening should be evaluated based on the relationships between these parameters and wall stress.

Assessment of myocardial mechanics in patients with end-stage renal disease and renal transplant recipients using speckle tracking echocardiography.

PubMed

Pirat, Bahar; Bozbas, Huseyin; Simsek, Vahide; Sade, L Elif; Sayin, Burak; Muderrisoglu, Haldun; Haberal, Mehmet

2015-04-01

Velocity vector imaging allows quantitation of myocardial strain and strain rate from 2-dimensional images based on speckle tracking echocardiography. The aim of this study was to analyze the changes in myocardial strain and strain rate patterns in patients with end-stage renal disease and renal transplant recipients. We studied 33 patients with end-stage renal disease on hemodialysis (19 men; mean age, 36 ± 8 y), 24 renal transplant recipients with functional grafts (21 men; mean age, 36 ± 7 y) and 26 age- and sex-matched control subjects. Longitudinal peak systolic strain and strain rate for basal, mid, and apical segments of the left ventricular wall were determined by velocity vector imaging from apical 4- and 2-chamber views. The average longitudinal strain and strain rate for the left ventricle were noted. From short-axis views at the level of papillary muscles, average circumferential, and radial strain, and strain rate were assessed. Mean heart rate and systolic and diastolic blood pressure during imaging were similar between the groups. Longitudinal peak systolic strain and strain rate at basal and mid-segments of the lateral wall were significantly higher in renal transplant recipients and control groups than endstage renal disease patients. Average longitudinal systolic strain from the 4-chamber view was highest in control subjects (-14.5% ± 2.9%) and was higher in renal transplant recipients (-12.5% ± 3.0%) than end-stage renal disease patients (-10.2% ± 1.6%; P ≤ .001). Radial and circumferential strain and strain rate at the level of the papillary muscle were lower in patients with end-stage renal disease than other groups. Differences in myocardial function in patients with end-stage renal disease, renal transplant recipients, and normal controls can be quantified by strain imaging. Myocardial function is improved in renal transplant recipients compared with end-stage renal disease patients.

Anisotropic effects on constitutive model parameters of aluminum alloys

NASA Astrophysics Data System (ADS)

Brar, Nachhatter S.; Joshi, Vasant S.

2012-03-01

Simulation of low velocity impact on structures or high velocity penetration in armor materials heavily rely on constitutive material models. Model constants are determined from tension, compression or torsion stress-strain at low and high strain rates at different temperatures. These model constants are required input to computer codes (LS-DYNA, DYNA3D or SPH) to accurately simulate fragment impact on structural components made of high strength 7075-T651 aluminum alloy. Johnson- Cook model constants determined for Al7075-T651 alloy bar material failed to simulate correctly the penetration into 1' thick Al-7075-T651plates. When simulation go well beyond minor parameter tweaking and experimental results show drastically different behavior it becomes important to determine constitutive parameters from the actual material used in impact/penetration experiments. To investigate anisotropic effects on the yield/flow stress of this alloy quasi-static and high strain rate tensile tests were performed on specimens fabricated in the longitudinal "L", transverse "T", and thickness "TH" directions of 1' thick Al7075 Plate. While flow stress at a strain rate of ~1/s as well as ~1100/s in the thickness and transverse directions are lower than the longitudinal direction. The flow stress in the bar was comparable to flow stress in the longitudinal direction of the plate. Fracture strain data from notched tensile specimens fabricated in the L, T, and Thickness directions of 1' thick plate are used to derive fracture constants.

Modification of glucose import capacity in Escherichia coli: physiologic consequences and utility for improving DNA vaccine production

PubMed Central

2013-01-01

Background The bacterium Escherichia coli can be grown employing various carbohydrates as sole carbon and energy source. Among them, glucose affords the highest growth rate. This sugar is nowadays widely employed as raw material in industrial fermentations. When E. coli grows in a medium containing non-limiting concentrations of glucose, a metabolic imbalance occurs whose main consequence is acetate secretion. The production of this toxic organic acid reduces strain productivity and viability. Solutions to this problem include reducing glucose concentration by substrate feeding strategies or the generation of mutant strains with impaired glucose import capacity. In this work, a collection of E. coli strains with inactive genes encoding proteins involved in glucose transport where generated to determine the effects of reduced glucose import capacity on growth rate, biomass yield, acetate and production of an experimental plasmid DNA vaccine (pHN). Results A group of 15 isogenic derivatives of E. coli W3110 were generated with single and multiple deletions of genes encoding glucose, mannose, beta-glucoside, maltose and N-acetylglucosamine components of the phosphoenolpyruvate:sugar phosphotransferase system (PTS), as well as the galactose symporter and the Mgl galactose/glucose ABC transporter. These strains were characterized by growing them in mineral salts medium supplemented with 2.5 g/L glucose. Maximum specific rates of glucose consumption (qs) spanning from 1.33 to 0.32 g/g h were displayed by the group of mutants and W3110, which resulted in specific growth rates ranging from 0.65-0.18 h-1. Acetate accumulation was reduced or abolished in cultures with all mutant strains. W3110 and five selected mutant derivatives were transformed with pHN. A 3.2-fold increase in pHN yield on biomass was observed in cultures of a mutant strain with deletion of genes encoding the glucose and mannose PTS components, as well as Mgl. Conclusions The group of E. coli mutants generated in this study displayed a reduction or elimination of overflow metabolism and a linear correlation between qs and the maximum specific growth rate as well as the acetate production rate. By comparing DNA vaccine production parameters among some of these mutants, it was possible to identify a near-optimal glucose import rate value for this particular application. The strains employed in this study should be a useful resource for studying the effects of different predefined qs values on production capacity for various biotechnological products. PMID:23638701

Paradox of vaccination: is vaccination really effective against avian flu epidemics?

PubMed

Iwami, Shingo; Suzuki, Takafumi; Takeuchi, Yasuhiro

2009-01-01

Although vaccination can be a useful tool for control of avian influenza epidemics, it might engender emergence of a vaccine-resistant strain. Field and experimental studies show that some avian influenza strains acquire resistance ability against vaccination. We investigated, in the context of the emergence of a vaccine-resistant strain, whether a vaccination program can prevent the spread of infectious disease. We also investigated how losses from immunization by vaccination imposed by the resistant strain affect the spread of the disease. We designed and analyzed a deterministic compartment model illustrating transmission of vaccine-sensitive and vaccine-resistant strains during a vaccination program. We investigated how the loss of protection effectiveness impacts the program. Results show that a vaccination to prevent the spread of disease can instead spread the disease when the resistant strain is less virulent than the sensitive strain. If the loss is high, the program does not prevent the spread of the resistant strain despite a large prevalence rate of the program. The epidemic's final size can be larger than that before the vaccination program. We propose how to use poor vaccines, which have a large loss, to maximize program effects and describe various program risks, which can be estimated using available epidemiological data. We presented clear and simple concepts to elucidate vaccination program guidelines to avoid negative program effects. Using our theory, monitoring the virulence of the resistant strain and investigating the loss caused by the resistant strain better development of vaccination strategies is possible.

Assertiveness of Lactobacillus sakei and Lactobacillus curvatus in a fermented sausage model.

PubMed

Janßen, Dorothee; Eisenbach, Lara; Ehrmann, Matthias A; Vogel, Rudi F

2018-04-20

Fresh meat harbors autochthonous microbiota with unknown risk potential, which is introduced in raw fermented sausages. Their growth can be limited by the use of safe, competitive starter strains. In the lack of time and cost-effective methods to track those starters at strain level, their assertiveness upon meat fermentation is widely unknown. Lactobacillus (L.) sakei and L. curvatus, which can be isolated from a variety of habitats, are frequently used as starter cultures. We monitored the assertiveness of 9 L. sakei and 9 L. curvatus strains in a model fermentation using MALDI-TOF-MS. An "in-house" MALDI-TOF-MS database with sub-proteome spectra of L. sakei and L. curvatus strains, as well as members of the autochthonous, spontaneously growing meat microbiota was established, validated and recognition rates were determined for each L. curvatus and L. sakei strain used. Competition studies were performed with standardized sausage batter, which was inoculated with a total of 10 6 cells of sets of 4-5 strains each of L. sakei and L. curvatus and 10 6 Staphylococcus carnosus ssp. carnosus cells. The pH and redox potential were monitored continuously. On days 0, 2 and 5 samples were taken to determine the CfU/g and a total of 96 isolates per sample were identified via MALDI-TOF-MS. MALDI-TOF-MS generally proved suitable for identification of isolates on strain level within the starter sets employed, but the recognition rate varied depending on the strain. Competition studies revealed dominance or co-dominance of strains within each set. However, their assertiveness significantly depended on the composition of the strain sets. Still, co-dominance or cooperation appeared effective to outgrow other members of the autochthonous meat microbiota, rather than dominance of single strains. For the latter, the ability to produce bacteriocins suggested itself for a crucial role in the assertiveness of starter strains. Copyright © 2018 Elsevier B.V. All rights reserved.

Characteristic systolic waveform of left ventricular longitudinal strain rate in patients with hypertrophic cardiomyopathy.

PubMed

Okada, Kazunori; Kaga, Sanae; Mikami, Taisei; Masauzi, Nobuo; Abe, Ayumu; Nakabachi, Masahiro; Yokoyama, Shinobu; Nishino, Hisao; Ichikawa, Ayako; Nishida, Mutsumi; Murai, Daisuke; Hayashi, Taichi; Shimizu, Chikara; Iwano, Hiroyuki; Yamada, Satoshi; Tsutsui, Hiroyuki

2017-05-01

We analyzed the waveform of systolic strain and strain-rate curves to find a characteristic left ventricular (LV) myocardial contraction pattern in patients with hypertrophic cardiomyopathy (HCM), and evaluated the utility of these parameters for the differentiation of HCM and LV hypertrophy secondary to hypertension (HT). From global strain and strain-rate curves in the longitudinal and circumferential directions, the time from mitral valve closure to the peak strains (T-LS and T-CS, respectively) and the peak systolic strain rates (T-LSSR and T-CSSR, respectively) were measured in 34 patients with HCM, 30 patients with HT, and 25 control subjects. The systolic strain-rate waveform was classified into 3 patterns ("V", "W", and "√" pattern). In the HCM group, T-LS was prolonged, but T-LSSR was shortened; consequently, T-LSSR/T-LS ratio was distinctly lower than in the HT and control groups. The "√" pattern of longitudinal strain-rate waveform was more frequently seen in the HCM group (74 %) than in the control (4 %) and HT (20 %) groups. Similar but less distinct results were obtained in the circumferential direction. To differentiate HCM from HT, the sensitivity and specificity of the T-LSSR/T-LS ratio <0.34 and the "√"-shaped longitudinal strain-rate waveform were 85 and 63 %, and 74 and 80 %, respectively. In conclusion, in patients with HCM, a reduced T-LSSR/T-LS ratio and a characteristic "√"-shaped waveform of LV systolic strain rate was seen, especially in the longitudinal direction. The timing and waveform analyses of systolic strain rate may be useful to distinguish between HCM and HT.

Mechanotransduction in bone: osteoblasts are more responsive to fluid forces than mechanical strain

NASA Technical Reports Server (NTRS)

Owan, I.; Burr, D. B.; Turner, C. H.; Qiu, J.; Tu, Y.; Onyia, J. E.; Duncan, R. L.

1997-01-01

Mechanical force applied to bone produces two localized mechanical signals on the cell: deformation of the extracellular matrix (substrate strain) and extracellular fluid flow. To study the effects of these stimuli on osteoblasts, MC3T3-E1 cells were grown on type I collagen-coated plastic plates and subjected to four-point bending. This technique produces uniform levels of physiological strain and fluid forces on the cells. Each of these parameters can be varied independently. Osteopontin (OPN) mRNA expression was used to assess the anabolic response of MC3T3-E1 cells. When fluid forces were low, neither strain magnitude nor strain rate was correlated with OPN expression. However, higher-magnitude fluid forces significantly increased OPN message levels independently of the strain magnitude or rate. These data indicate that fluid forces, and not mechanical stretch, influence OPN expression in osteoblasts and suggest that fluid forces induced by extracellular fluid flow within the bone matrix may play an important role in bone formation in response to mechanical loading.

Enhanced hydrogen production from glucose using ldh- and frd-inactivated Escherichia coli strains.

PubMed

Yoshida, Akihito; Nishimura, Taku; Kawaguchi, Hideo; Inui, Masayuki; Yukawa, Hideaki

2006-11-01

We improved the hydrogen yield from glucose using a genetically modified Escherichia coli. E. coli strain SR15 (DeltaldhA, DeltafrdBC), in which glucose metabolism was directed to pyruvate formate lyase (PFL), was constructed. The hydrogen yield of wild-type strain of 1.08 mol/mol glucose, was enhanced to 1.82 mol/mol glucose in strain SR15. This figure is greater than 90 % of the theoretical hydrogen yield of facultative anaerobes (2.0 mol/mol glucose). Moreover, the specific hydrogen production rate of strain SR15 (13.4 mmol h(-1) g(-1) dry cell) was 1.4-fold higher than that of wild-type strain. In addition, the volumetric hydrogen production rate increased using the process where cells behaved as an effective catalyst. At 94.3 g dry cell/l, a productivity of 793 mmol h(-1) l(-1) (20.2 l h(-1) l(-1) at 37 degrees C) was achieved using SR15. The reported productivity substantially surpasses that of conventional biological hydrogen production processes and can be a trigger for practical applications.

Financial Strain, Trajectories of Marital Processes, and African American Newlyweds' Marital Instability

PubMed Central

Barton, Allen W.; Bryant, Chalandra M.

2016-01-01

The present study examined the longitudinal associations among financial strain, trajectories of marital processes, and increases in marital instability concerns among a sample of 280 African American newlywed couples followed over the first three years of marriage. Results from dyadic structural equation modeling revealed that financial strain experienced during the early years of marriage was associated with increased marital instability concerns for both husbands and wives. Latent growth curves of marital processes revealed mean declines in appraisals of spousal warmth and increases in appraisals of spousal hostility, with variability between individuals in rates of decline in warmth; further, wives' appraisals of spousal warmth covaried with levels of financial strain, such that high levels of financial strain were associated with steeper declines in spousal warmth appraisals. For both husbands and wives, rates of change in spousal warmth appraisals had a greater influence on increases in marital instability concerns than either starting levels of spousal warmth appraisals or financial strain. Findings highlight the long-term associations between external stress and trajectories of marital appraisals as well as their relative effects on marital distress. PMID:26998640

Effect of Board Thickness on Sn-Ag-Cu Joint Interconnect Mechanical Shock Performance

NASA Astrophysics Data System (ADS)

Lee, Tae-Kyu; Xie, Weidong

2014-12-01

The mechanical stability of solder joints with Sn-Ag-Cu alloy joints on various board thicknesses was investigated with a high G level shock environment. A test vehicle with three different board thicknesses was used for board drop shock performance tests. These vehicles have three different strain and shock level condition couples per board, and are used to identify the joint stability and failure modes based on the board responses. The results revealed that joint stability is sensitive to board thickness. The board drop shock test showed that the first failure location shifts from the corner location near the standoff to the center with increased board thickness due to the shock wave response. From analysis of the thickness variation and failure cycle number, the strain rate during the pulse strain cycle is the dominant factor, which defines the life cycle number per board thickness, and not the maximum strain value. The failure location shift and the shock performance differentiation are discussed from the perspective of maximum principal strain, cycle frequency and strain rate per cycle.

Low escape-rate genome safeguards with minimal molecular perturbation of Saccharomyces cerevisiae.

PubMed

Agmon, Neta; Tang, Zuojian; Yang, Kun; Sutter, Ben; Ikushima, Shigehito; Cai, Yizhi; Caravelli, Katrina; Martin, James A; Sun, Xiaoji; Choi, Woo Jin; Zhang, Allen; Stracquadanio, Giovanni; Hao, Haiping; Tu, Benjamin P; Fenyo, David; Bader, Joel S; Boeke, Jef D

2017-02-21

As the use of synthetic biology both in industry and in academia grows, there is an increasing need to ensure biocontainment. There is growing interest in engineering bacterial- and yeast-based safeguard (SG) strains. First-generation SGs were based on metabolic auxotrophy; however, the risk of cross-feeding and the cost of growth-controlling nutrients led researchers to look for other avenues. Recent strategies include bacteria engineered to be dependent on nonnatural amino acids and yeast SG strains that have both transcriptional- and recombinational-based biocontainment. We describe improving yeast Saccharomyces cerevisiae -based transcriptional SG strains, which have near-WT fitness, the lowest possible escape rate, and nanomolar ligands controlling growth. We screened a library of essential genes, as well as the best-performing promoter and terminators, yielding the best SG strains in yeast. The best constructs were fine-tuned, resulting in two tightly controlled inducible systems. In addition, for potential use in the prevention of industrial espionage, we screened an array of possible "decoy molecules" that can be used to mask any proprietary supplement to the SG strain, with minimal effect on strain fitness.

Largely Tunable Band Structures of Few-Layer InSe by Uniaxial Strain.

PubMed

Song, Chaoyu; Fan, Fengren; Xuan, Ningning; Huang, Shenyang; Zhang, Guowei; Wang, Chong; Sun, Zhengzong; Wu, Hua; Yan, Hugen

2018-01-31

Because of the strong quantum confinement effect, few-layer γ-InSe exhibits a layer-dependent band gap, spanning the visible and near infrared regions, and thus recently has been drawing tremendous attention. As a two-dimensional material, the mechanical flexibility provides an additional tuning knob for the electronic structures. Here, for the first time, we engineer the band structures of few-layer and bulk-like InSe by uniaxial tensile strain and observe a salient shift of photoluminescence peaks. The shift rate of the optical gap is approximately 90-100 meV per 1% strain for four- to eight-layer samples, which is much larger than that for the widely studied MoS 2 monolayer. Density functional theory calculations well reproduce the observed layer-dependent band gaps and the strain effect and reveal that the shift rate decreases with the increasing layer number for few-layer InSe. Our study demonstrates that InSe is a very versatile two-dimensional electronic and optoelectronic material, which is suitable for tunable light emitters, photodetectors, and other optoelectronic devices.

Mechanical responses, texture evolution, and yield loci of extruded AZ31 magnesium alloy under various loading conditions: Experiment and modeling

NASA Astrophysics Data System (ADS)

Kabirian, Farhoud

Mechanical responses and texture evolution of extruded AZ31 Mg are measured under uniaxial (tension-compression) and multiaxial (free-end torsion) loadings. Compression loading is carried out in three different directions at temperature and strain rate ranges of 77-423 K and 10-4 -3000 s -1, respectively. Texture evolution at different intermediate strains reveals that crystal reorientation is exhausted at smaller strains with increase in strain rate while increase in temperature retards twinning. In addition to the well-known tension-compression yield asymmetry, a strong anisotropy in strain hardening response is observed. Strain hardening during the compression experiment is intensified with decreasing and increasing temperature and strain rate, respectively. This complex behavior is explained through understanding the roles of deformation mechanisms using the Visco-Plastic Self Consistent (VPSC) model. In order to calibrate the VPSC model's constants as accurate as possible, a vast number of mechanical responses including stress-strain curves in tension, compression in three directions, and free-end torsion, texture evolution at different strains, lateral strains of compression samples, twin volume fraction, and axial strain during the torsion experiment. Modeling results show that depending on the number of measurements used for calibration, roles of different mechanisms in plastic deformation change significantly. In addition, a precise definition of yield is established for the extruded AZ31magnesium alloy after it is subjected to different loading conditions (uniaxial to multiaxial) at four different plastic strains. The yield response is measured in ?-? space. Several yield criteria are studied to predict yield response of extruded AZ31. This study proposes an asymmetrical fourth-order polynomial yield function. Material constants in this model can be directly calculated using mechanical measurements. Convexity of the proposed model is discussed, and domains of constants where convexity holds are determined. Effects of grain refinement induced by Equal Channel Angular Pressing, ECAP, on mechanical responses and texture evolution are investigated. Yield strength in compression increases after ECAP, however, strain-hardening rate drops with number of ECAP passes while failure strain increases. Texture measurements reveal the higher propensity to twinning in the extruded material compared with ECAPed magnesium. Calculated Schmid factor maps are utilized to connect the observed mechanical responses to the texture.

Development of a strain rate dependent material model of human cortical bone for computer-aided reconstruction of injury mechanisms.

PubMed

Asgharpour, Zahra; Zioupos, Peter; Graw, Matthias; Peldschus, Steffen

2014-03-01

Computer-aided methods such as finite-element simulation offer a great potential in the forensic reconstruction of injury mechanisms. Numerous studies have been performed on understanding and analysing the mechanical properties of bone and the mechanism of its fracture. Determination of the mechanical properties of bones is made on the same basis used for other structural materials. The mechanical behaviour of bones is affected by the mechanical properties of the bone material, the geometry, the loading direction and mode and of course the loading rate. Strain rate dependency of mechanical properties of cortical bone has been well demonstrated in literature studies, but as many of these were performed on animal bones and at non-physiological strain rates it is questionable how these will apply in the human situations. High strain-rates dominate in a lot of forensic applications in automotive crashes and assault scenarios. There is an overwhelming need to a model which can describe the complex behaviour of bone at lower strain rates as well as higher ones. Some attempts have been made to model the viscoelastic and viscoplastic properties of the bone at high strain rates using constitutive mathematical models with little demonstrated success. The main objective of the present study is to model the rate dependent behaviour of the bones based on experimental data. An isotropic material model of human cortical bone with strain rate dependency effects is implemented using the LS-DYNA material library. We employed a human finite element model called THUMS (Total Human Model for Safety), developed by Toyota R&D Labs and the Wayne State University, USA. The finite element model of the human femur is extracted from the THUMS model. Different methods have been employed to develop a strain rate dependent material model for the femur bone. Results of one the recent experimental studies on human femur have been employed to obtain the numerical model for cortical femur. A forensic application of the model is explained in which impacts to the arm have been reconstructed using the finite element model of THUMS. The advantage of the numerical method is that a wide range of impact conditions can be easily reconstructed. Impact velocity has been changed as a parameter to find the tolerance levels of injuries to the lower arm. The method can be further developed to study the assaults and the injury mechanism which can lead to severe traumatic injuries in forensic cases. Copyright © 2013 Elsevier Ireland Ltd. All rights reserved.

Health effects of unemployment in Europe (2008-2011): a longitudinal analysis of income and financial strain as mediating factors.

PubMed

Tøge, Anne Grete

2016-05-06

Unemployment has a number of negative consequences, such as decreased income and poor self-rated health. However, the relationships between unemployment, income, and health are not fully understood. Longitudinal studies have investigated the health effect of unemployment and income separately, but the mediating role of income remains to be scrutinized. Using longitudinal data and methods, this paper investigates whether the effect of unemployment on self-rated health (SRH) is mediated by income, financial strain and unemployment benefits. The analyses use data from the longitudinal panel of European Union Statistics on Income and Living Conditions (EU-SILC) over the 4 years of 2008 to 2011. Individual fixed effects models are applied, estimating the longitudinal change in SRH as people move from employment to unemployment, and investigating whether this change is reduced after controlling for possible mediating mechanisms, absolute income change, relative income change, relative income rank, income deprivation, financial strain, and unemployment benefits. Becoming unemployed is associated with decreased SRH (-0.048, SE 0.012). This decrease is 19 % weaker (-0.039, SE 0.010) after controlling for change in financial strain. Absolute and relative changes in household equalized income, as well as changes in relative rank and transitions into income deprivation, are not found to be associated with change in SRH. Financial strain is found to be a potential mediator of the individual health effect of unemployment, while neither absolute income, relative income, relative rank, income deprivation nor unemployment benefits are found to be mediators of this relationship.

Velocity Fields of Axisymmetric Hydrogen-Air Counterflow Diffusion Flames from LDV, PIV, and Numerical Computation

NASA Technical Reports Server (NTRS)

Pellett, Gerald L.; Wilson, Lloyd G.; Humphreys, William M., Jr.; Bartram, Scott M.; Gartrell, Luther R.; Isaac, K. M.

1995-01-01

Laminar fuel-air counterflow diffusion flames (CFDFs) were studied using axisymmetric convergent-nozzle and straight-tube opposed jet burners (OJBs). The subject diagnostics were used to probe a systematic set of H2/N2-air CFDFs over wide ranges of fuel input (22 to 100% Ha), and input axial strain rate (130 to 1700 Us) just upstream of the airside edge, for both plug-flow and parabolic input velocity profiles. Laser Doppler Velocimetry (LDV) was applied along the centerline of seeded air flows from a convergent nozzle OJB (7.2 mm i.d.), and Particle Imaging Velocimetry (PIV) was applied on the entire airside of both nozzle and tube OJBs (7 and 5 mm i.d.) to characterize global velocity structure. Data are compared to numerical results from a one-dimensional (1-D) CFDF code based on a stream function solution for a potential flow input boundary condition. Axial strain rate inputs at the airside edge of nozzle-OJB flows, using LDV and PIV, were consistent with 1-D impingement theory, and supported earlier diagnostic studies. The LDV results also characterized a heat-release hump. Radial strain rates in the flame substantially exceeded 1-D numerical predictions. Whereas the 1-D model closely predicted the max I min axial velocity ratio in the hot layer, it overpredicted its thickness. The results also support previously measured effects of plug-flow and parabolic input strain rates on CFDF extinction limits. Finally, the submillimeter-scale LDV and PIV diagnostics were tested under severe conditions, which reinforced their use with subcentimeter OJB tools to assess effects of aerodynamic strain, and fueVair composition, on laminar CFDF properties, including extinction.

Quantitative Characterization of the Growth of Deinococcus geothermalis DSM-11302: Effect of Inoculum Size, Growth Medium and Culture Conditions.

PubMed

Bornot, Julie; Molina-Jouve, Carole; Uribelarrea, Jean-Louis; Gorret, Nathalie

2015-08-20

Due to their remarkable resistance to extreme conditions, Deinococcaceae strains are of great interest to biotechnological prospects. However, the physiology of the extremophile strain Deinococcus geothermalis has scarcely been studied and is not well understood. The physiological behaviour was then studied in well-controlled conditions in flask and bioreactor cultures. The growth of D. geothermalis type strains was compared. Among the strains tested, the strain from the German Collection of Microorganisms (Deutsche Sammlung von Mikroorganismen DSM) DSM-11302 was found to give the highest biomass concentration and growth rate: in a complex medium with glucose, the growth rate reached 0.75 h(-1) at 45 °C. Yeast extract concentration in the medium had significant constitutive and catalytic effects. Furthermore, the results showed that the physiological descriptors were not affected by the inoculum preparation steps. A batch culture of D. geothermalis DSM-11302 on defined medium was carried out: cells grew exponentially with a maximal growth rate of 0.28 h(-1) and D. geothermalis DSM-11302 biomass reached 1.4 g·L(-1) in 20 h. Then, 1.4 gDryCellWeight of biomass (X) was obtained from 5.6 g glucose (Glc) consumed as carbon source, corresponding to a yield of 0.3 CmolX·CmolGlc(-1); cell specific oxygen uptake and carbon dioxide production rates reached 216 and 226 mmol.CmolX(-1)·h(-1), respectively, and the respiratory quotient (QR) value varied from 1.1 to 1.7. This is the first time that kinetic parameters and yields are reported for D. geothermalis DSM-11302 grown on a mineral medium in well-controlled batch culture.

Quantitative Characterization of the Growth of Deinococcus geothermalis DSM-11302: Effect of Inoculum Size, Growth Medium and Culture Conditions

PubMed Central

Bornot, Julie; Molina-Jouve, Carole; Uribelarrea, Jean-Louis; Gorret, Nathalie

2015-01-01

Due to their remarkable resistance to extreme conditions, Deinococcaceae strains are of great interest to biotechnological prospects. However, the physiology of the extremophile strain Deinococcus geothermalis has scarcely been studied and is not well understood. The physiological behaviour was then studied in well-controlled conditions in flask and bioreactor cultures. The growth of D. geothermalis type strains was compared. Among the strains tested, the strain from the German Collection of Microorganisms (Deutsche Sammlung von Mikroorganismen DSM) DSM-11302 was found to give the highest biomass concentration and growth rate: in a complex medium with glucose, the growth rate reached 0.75 h−1 at 45 °C. Yeast extract concentration in the medium had significant constitutive and catalytic effects. Furthermore, the results showed that the physiological descriptors were not affected by the inoculum preparation steps. A batch culture of D. geothermalis DSM-11302 on defined medium was carried out: cells grew exponentially with a maximal growth rate of 0.28 h−1 and D. geothermalis DSM-11302 biomass reached 1.4 g·L−1 in 20 h. Then, 1.4 gDryCellWeight of biomass (X) was obtained from 5.6 g glucose (Glc) consumed as carbon source, corresponding to a yield of 0.3 CmolX·CmolGlc−1; cell specific oxygen uptake and carbon dioxide production rates reached 216 and 226 mmol.CmolX−1·h−1, respectively, and the respiratory quotient (QR) value varied from 1.1 to 1.7. This is the first time that kinetic parameters and yields are reported for D. geothermalis DSM-11302 grown on a mineral medium in well-controlled batch culture. PMID:27682099

Cryopreservation of Embryos of the Mediterranean Fruit Fly Ceratitis capitata Vienna 8 Genetic Sexing Strain

PubMed Central

Augustinos, Antonios A.; Rajamohan, Arun; Kyritsis, Georgios A.; Zacharopoulou, Antigone; Haq, Ihsan ul; Targovska, Asya; Caceres, Carlos; Bourtzis, Kostas; Abd-Alla, Adly M. M.

2016-01-01

The Mediterranean fruit fly, Ceratitis capitata, is one of the most serious pests of fruit crops world-wide. During the last decades, area-wide pest management (AW-IPM) approaches with a sterile insect technique (SIT) component have been used to control populations of this pest in an effective and environment-friendly manner. The development of genetic sexing strains (GSS), such as the Vienna 8 strain, has been played a major role in increasing the efficacy and reducing the cost of SIT programs. However, mass rearing, extensive inbreeding, possible bottleneck phenomena and hitch-hiking effects might pose major risks for deterioration and loss of important genetic characteristics of domesticated insect. In the present study, we present a modified procedure to cryopreserve the embryos of the medfly Vienna 8 GSS based on vitrification and used this strain as insect model to assess the impact of the cryopreservation process on the genetic structure of the cryopreserved insects. Forty-eight hours old embryos, incubated at 24°C, were found to be the most suitable developmental stage for cryopreservation treatment for high production of acceptable hatch rate (38%). Our data suggest the absence of any negative impact of the cryopreservation process on egg hatch rate, pupation rates, adult emergence rates and stability of the temperature sensitive lethal (tsl) character on two established cryopreserved lines (flies emerged from cryopreserved embryos), named V8-118 and V8-228. Taken together, our study provides an optimized procedure to cryopreserve the medfly Vienna 8 GSS and documents the absence of any negative impact on the genetic structure and quality of the strain. Benefits and sceneries for utilization of this technology to support operational SIT projects are discussed in this paper. PMID:27537351

Cryopreservation of Embryos of the Mediterranean Fruit Fly Ceratitis capitata Vienna 8 Genetic Sexing Strain.

PubMed

Augustinos, Antonios A; Rajamohan, Arun; Kyritsis, Georgios A; Zacharopoulou, Antigone; Haq, Ihsan Ul; Targovska, Asya; Caceres, Carlos; Bourtzis, Kostas; Abd-Alla, Adly M M

2016-01-01

The Mediterranean fruit fly, Ceratitis capitata, is one of the most serious pests of fruit crops world-wide. During the last decades, area-wide pest management (AW-IPM) approaches with a sterile insect technique (SIT) component have been used to control populations of this pest in an effective and environment-friendly manner. The development of genetic sexing strains (GSS), such as the Vienna 8 strain, has been played a major role in increasing the efficacy and reducing the cost of SIT programs. However, mass rearing, extensive inbreeding, possible bottleneck phenomena and hitch-hiking effects might pose major risks for deterioration and loss of important genetic characteristics of domesticated insect. In the present study, we present a modified procedure to cryopreserve the embryos of the medfly Vienna 8 GSS based on vitrification and used this strain as insect model to assess the impact of the cryopreservation process on the genetic structure of the cryopreserved insects. Forty-eight hours old embryos, incubated at 24°C, were found to be the most suitable developmental stage for cryopreservation treatment for high production of acceptable hatch rate (38%). Our data suggest the absence of any negative impact of the cryopreservation process on egg hatch rate, pupation rates, adult emergence rates and stability of the temperature sensitive lethal (tsl) character on two established cryopreserved lines (flies emerged from cryopreserved embryos), named V8-118 and V8-228. Taken together, our study provides an optimized procedure to cryopreserve the medfly Vienna 8 GSS and documents the absence of any negative impact on the genetic structure and quality of the strain. Benefits and sceneries for utilization of this technology to support operational SIT projects are discussed in this paper.

A Modified Double Multiple Nonlinear Regression Constitutive Equation for Modeling and Prediction of High Temperature Flow Behavior of BFe10-1-2 Alloy

NASA Astrophysics Data System (ADS)

Cai, Jun; Wang, Kuaishe; Shi, Jiamin; Wang, Wen; Liu, Yingying

2018-01-01

Constitutive analysis for hot working of BFe10-1-2 alloy was carried out by using experimental stress-strain data from isothermal hot compression tests, in a wide range of temperature of 1,023 1,273 K, and strain rate range of 0.001 10 s-1. A constitutive equation based on modified double multiple nonlinear regression was proposed considering the independent effects of strain, strain rate, temperature and their interrelation. The predicted flow stress data calculated from the developed equation was compared with the experimental data. Correlation coefficient (R), average absolute relative error (AARE) and relative errors were introduced to verify the validity of the developed constitutive equation. Subsequently, a comparative study was made on the capability of strain-compensated Arrhenius-type constitutive model. The results showed that the developed constitutive equation based on modified double multiple nonlinear regression could predict flow stress of BFe10-1-2 alloy with good correlation and generalization.

Dynamic Recrystallization Behavior of AISI 422 Stainless Steel During Hot Deformation Processes

NASA Astrophysics Data System (ADS)

Ahmadabadi, R. Mohammadi; Naderi, M.; Mohandesi, J. Aghazadeh; Cabrera, Jose Maria

2018-02-01

In this work, hot compression tests were performed to investigate the dynamic recrystallization (DRX) process of a martensitic stainless steel (AISI 422) at temperatures of 950, 1000, 1050, 1100 and 1150 °C and strain rates of 0.01, 0.1 and 1 s-1. The dependency of strain-hardening rate on flow stress was used to estimate the critical stress for the onset of DRX. Accordingly, the critical stress to peak stress ratio was calculated as 0.84. Moreover, the effect of true strain was examined by fitting stress values to an Arrhenius type constitutive equation, and then considering material constants as a function of strain by using a third-order polynomial equation. Finally, two constitutive models were used to investigate the competency of the strain-dependent constitutive equations to predict the flow stress curves of the studied steel. It was concluded that one model offers better precision on the flow stress values after the peak stress, while the other model gives more accurate results before the peak stress.

High variability in strain estimation errors when using a commercial ultrasound speckle tracking algorithm on tendon tissue.

PubMed

Fröberg, Åsa; Mårtensson, Mattias; Larsson, Matilda; Janerot-Sjöberg, Birgitta; D'Hooge, Jan; Arndt, Anton

2016-10-01

Ultrasound speckle tracking offers a non-invasive way of studying strain in the free Achilles tendon where no anatomical landmarks are available for tracking. This provides new possibilities for studying injury mechanisms during sport activity and the effects of shoes, orthotic devices, and rehabilitation protocols on tendon biomechanics. To investigate the feasibility of using a commercial ultrasound speckle tracking algorithm for assessing strain in tendon tissue. A polyvinyl alcohol (PVA) phantom, three porcine tendons, and a human Achilles tendon were mounted in a materials testing machine and loaded to 4% peak strain. Ultrasound long-axis cine-loops of the samples were recorded. Speckle tracking analysis of axial strain was performed using a commercial speckle tracking software. Estimated strain was then compared to reference strain known from the materials testing machine. Two frame rates and two region of interest (ROI) sizes were evaluated. Best agreement between estimated strain and reference strain was found in the PVA phantom (absolute error in peak strain: 0.21 ± 0.08%). The absolute error in peak strain varied between 0.72 ± 0.65% and 10.64 ± 3.40% in the different tendon samples. Strain determined with a frame rate of 39.4 Hz had lower errors than 78.6 Hz as was the case with a 22 mm compared to an 11 mm ROI. Errors in peak strain estimation showed high variability between tendon samples and were large in relation to strain levels previously described in the Achilles tendon. © The Foundation Acta Radiologica 2016.

Effect of test temperature and strain rate on the tensile properties of high-strength, high-conductivity copper alloys

DOE Office of Scientific and Technical Information (OSTI.GOV)

Zinkle, S.J.; Eatherly, W.S.

1997-04-01

The unirradiated tensile properties of wrought GlidCop AL25 (ITER grade zero, IGO) solutionized and aged CuCrZr, and cold-worked and aged and solutionized and aged Hycon 3HP{trademark} CuNiBe have been measured over the temperature range of 20-500{degrees}C at strain rates between 4 x 10{sup {minus}4} s{sup {minus}1} and 0.06 s{sup {minus}1}. The measured room temperature electrical conductivity ranged from 64 to 90% IACS for the different alloys. All of the alloys were relatively insensitive to strain rate at room temperature, but the strain rate sensitivity of GlidCop Al25 increased significantly with increasing temperature. The CuNiBe alloys exhibited the best combination ofmore » high strength and high conductivity at room temperature. The strength of CuNiBe decreased slowly with increasing temperature. However, the ductility of CuNiBe decreased rapidly with increasing temperature due to localized deformation near grain boundaries, making these alloy heats unsuitable for typical structural applications above 300{degrees}C. The strength and uniform elongation of GlidCop Al25 decreased significantly with increasing temperature at a strain rate of 1 x 10{sup {minus}3} s{sup {minus}1}, whereas the total elongation was independent of test temperature. The strength and ductility of CuCrZr decreased slowly with increasing temperature.« less

Strain rate dependent orthotropic properties of pristine and impulsively loaded porcine temporomandibular joint disk.

PubMed

Beatty, M W; Bruno, M J; Iwasaki, L R; Nickel, J C

2001-10-01

The purpose of this study was to characterize the tensile stress-strain behavior of the porcine temporomandibular joint (TMJ) disk with respect to collagen orientation and strain rate dependency. The apparent elastic modulus, ultimate tensile strength, and strain at maximum stress were measured at three elongation rates (0.5, 50, and 500 mm/min) for dumbbell-shaped samples oriented along either anteroposterior or mediolateral axes of the disks. In order to study the effects of impact-induced fissuring on the mechanical behavior, the same properties were measured along each orientation at an elongation rate of 500 mm/min for disks subjected to impulsive loads of 0.5 N. s. The results suggested a strongly orthotropic nature to the healthy pristine disk. The values for the apparent modulus and ultimate strength were 10-fold higher along the anteroposterior axis (p < or = 0.01), which represented the primary orientation of the collagen fibers. Strain rate dependency was evident for loading along the anteroposterior axis but not along the mediolateral axis. No significant differences in any property were noted between pristine and impulsively loaded disks for either orientation (p > 0.05). The results demonstrated the importance of choosing an orthotropic model for the TMJ disk to conduct finite element modeling, to develop failure criteria, and to construct tissue-engineered replacements. Impact-induced fissuring requires further study to determine if the TMJ disk is orthotropic with respect to fatigue.

Lack of supportive leadership behavior predicts suboptimal self-rated health independent of job strain after 10 years of follow-up: findings from the population-based MONICA/KORA study.

PubMed

Schmidt, Burkhard; Herr, Raphael M; Jarczok, Marc N; Baumert, Jens; Lukaschek, Karoline; Emeny, Rebecca T; Ladwig, Karl-Heinz

2018-04-23

Emerging cross-sectional research has identified lack of supportive leadership behavior (SLB) as a risk factor for workforce health. However, prospective evidence is hitherto lacking. SLB denotes support in difficult situations, recognition and feedback on work tasks. This study aims to determine the effect of SLB on suboptimal self-rated health (SRH) after 10 years considering potential moderators such as ages, sex, occupation and job strain. The sample included 884 employed participants drawn from the population-based prospective MONICA/KORA Study. SLB, SRH, as well as job strain were assessed by questionnaire. Logistic regressions estimated odds ratios (ORs) and corresponding 95% confidence intervals (CIs) for the effect of SLB at baseline on suboptimal SRH at follow-up. Analyses were adjusted for age, gender, lifestyle (alcohol, smoking, physical activity), socioeconomic status as well as for SRH and job strain at baseline. Lack of SLB was associated with suboptimal SRH at baseline [OR 2.00, (95% CI 1.19-3.46)] and at follow-up [OR 2.33, (95% CI 1.40-3.89)]. Additional adjustment for job strain did not substantially alter this association [OR 2.06, (95% CI 1.20-3.52)]. However, interactions between SLB and job strain as well as gender became evident, indicating moderating influences on the association between SLB and SRH. Lack of supportive leadership was associated with suboptimal SRH at 10 years' follow-up in men, even if SRH at baseline and other risk factors were taken into account. This effect is likely to be moderated by job strain.

A new analytical method for estimating lumped parameter constants of linear viscoelastic models from strain rate tests

NASA Astrophysics Data System (ADS)

Mattei, G.; Ahluwalia, A.

2018-04-01

We introduce a new function, the apparent elastic modulus strain-rate spectrum, E_{app} ( \\dot{ɛ} ), for the derivation of lumped parameter constants for Generalized Maxwell (GM) linear viscoelastic models from stress-strain data obtained at various compressive strain rates ( \\dot{ɛ}). The E_{app} ( \\dot{ɛ} ) function was derived using the tangent modulus function obtained from the GM model stress-strain response to a constant \\dot{ɛ} input. Material viscoelastic parameters can be rapidly derived by fitting experimental E_{app} data obtained at different strain rates to the E_{app} ( \\dot{ɛ} ) function. This single-curve fitting returns similar viscoelastic constants as the original epsilon dot method based on a multi-curve global fitting procedure with shared parameters. Its low computational cost permits quick and robust identification of viscoelastic constants even when a large number of strain rates or replicates per strain rate are considered. This method is particularly suited for the analysis of bulk compression and nano-indentation data of soft (bio)materials.

Comparative amperometric study of uptake hydrogenase and hydrogen photoproduction activities between heterocystous cyanobacterium Anabaena cylindrica B629 and nonheterocystous cyanobacterium Oscillatoria sp. strain Miami BG7

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kumazawa, S.; Mitsui, A.

Heterocystous filamentous cyanobacterium Anabaena cylindrica B629 and nonheterocystous filamentous cyanobacterium Oscillatoria sp. strain Miami BG7 were cultured in media with N/sub 2/ as the sole nitrogen source; and activities of oxygen-dependent hydrogen uptake, photohydrogen production photooxygen evolution, and respiration were compared amperometrically under the same or similar experimental conditions for both strains. Distinct differences in these activities were observed in both strains. The rates of hydrogen photoproduction and hydrogen accumulation were significantly higher in Oscillatoria sp. strain BG7 than in A. cylindrica B629 at every light intensity tested. The major reason for the difference was attributable to the fact thatmore » the heterocystous cyanobacterium had a high rate of oxygen-dependent hydrogen consumption activity and the nonheterocystous cyanobacterium did not. The activity of oxygen photoevolution and respiration also contributed to the difference. Oscillatoria sp. strain BG7 had lower O/sub 2/ evolution and higher respiration than did A. cylindrica B629. Thus, the effect of O/sub 2/ on hydrogen photoproduction was minimized in Oscillatoria sp. strain BG7. 32 references, 5 figures.« less

Reference Ranges of Left Ventricular Strain Measures by Two-Dimensional Speckle-Tracking Echocardiography in Children: A Systematic Review and Meta-Analysis.

PubMed

Levy, Philip T; Machefsky, Aliza; Sanchez, Aura A; Patel, Meghna D; Rogal, Sarah; Fowler, Susan; Yaeger, Lauren; Hardi, Angela; Holland, Mark R; Hamvas, Aaron; Singh, Gautam K

2016-03-01

Establishment of the range of reference values and associated variations of two-dimensional speckle-tracking echocardiography (2DSTE)-derived left ventricular (LV) strain is a prerequisite for its routine clinical adoption in pediatrics. The aims of this study were to perform a meta-analysis of normal ranges of LV global longitudinal strain (GLS), global circumferential strain (GCS), and global radial strain (GRS) measurements derived by 2DSTE in children and to identify confounding factors that may contribute to variance in reported measures. A systematic review was launched in MEDLINE, Embase, Scopus, the Cumulative Index to Nursing and Allied Health Literature, and the Cochrane Library. Search hedges were created to cover the concepts of pediatrics, STE, and left-heart ventricle. Two investigators independently identified and included studies if they reported 2DSTE-derived LV GLS, GCS, or GRS. The weighted mean was estimated by using random effects models with 95% CIs, heterogeneity was assessed using the Cochran Q statistic and the inconsistency index (I(2)), and publication bias was evaluated using the Egger test. Effects of demographic (age), clinical, and vendor variables were assessed in a metaregression. The search identified 2,325 children from 43 data sets. The reported normal mean values of GLS among the studies varied from -16.7% to -23.6% (mean, -20.2%; 95% CI, -19.5% to -20.8%), GCS varied from -12.9% to -31.4% (mean, -22.3%; 95% CI, -19.9% to -24.6%), and GRS varied from 33.9% to 54.5% (mean, 45.2%; 95% CI, 38.3% to 51.7%). Twenty-six studies reported longitudinal strain only from the apical four-chamber view, with a mean of -20.4% (95% CI, -19.8% to -21.7%). Twenty-three studies reported circumferential strain (mean, -20.3%; 95% CI, -19.4% to -21.2%) and radial strain (mean, 46.7%; 95% CI, 42.3% to 51.1%) from the short-axis view at the midventricular level. A significant apex-to-base segmental longitudinal strain gradient (P < .01) was observed in the LV free wall. There was significant between-study heterogeneity and inconsistency (I(2) > 94% and P < .001 for each strain measure), which was not explained by age, gender, body surface area, blood pressure, heart rate, frame rate, frame rate/heart rate ratio, tissue-tracking methodology, location of reported strain value along the strain curve, ultrasound equipment, or software. The metaregression showed that these effects were not significant determinants of variations among normal ranges of strain values. There was no evidence of publication bias (P = .40). This study defines reference values of 2DSTE-derived LV strain in children on the basis of a meta-analysis. In healthy children, mean LV GLS was -20.2% (95% CI, -19.5% to -20.8%), mean GCS was -22.3% (95% CI, -19.9% to -24.6%), and mean GRS was 45.2% (95% CI, 38.3% to 51.7%). LV segmental longitudinal strain has a stable apex-to-base gradient that is preserved throughout maturation. Although variations among different reference ranges in this meta-analysis were not dependent on differences in demographic, clinical, or vendor parameters, age- and vendor-specific referenced ranges were established as well. Copyright © 2016 American Society of Echocardiography. Published by Elsevier Inc. All rights reserved.

Pancreatic Effects of a Bruton's Tyrosine Kinase Small-molecule Inhibitor in Rats Are Strain-dependent.

PubMed

Bhaskaran, Manoj; Cornwell, Paul D; Sorden, Steven D; Elwell, Michael R; Russell, Natalie R; Pritt, Michael L; Vahle, John L

2018-01-01

Inhibitors of Bruton's tyrosine kinase (BTK) are under development as potential therapies for various autoimmune diseases. In repeat-dose toxicity studies, small-molecule BTK inhibitors (BTKi) have been reported to cause a constellation of histologic effects at the pancreatic endocrine-exocrine interface in male rats; however, similar findings were not reported in other species. Since the BTKi-induced pancreatic effect is morphologically similar to well-documented spontaneous changes (predominantly characterized by insular/peri-insular hemorrhage, pigment deposition, chronic inflammation, and fibrosis) that are known to vary by rat strain, we investigated potential strain-dependent differences in the pancreatic effects of a small-molecule BTKi, LY3337641. Following 13 weeks of LY3337641 treatment, Crl:CD(SD) rats were most sensitive, Crl:WI(Han) rats were of intermediate sensitivity, and Hsd:SD rats were least sensitive. These strain differences appear to be related to differences in rate of weight gain across strains and sexes; however, a definitive mechanism was not determined. This study demonstrated that BTKi-induced pancreatic effects were highly dependent on rat strain and correlated with differences in the incidence and severity of the spontaneous background change. When considered with the lack of pancreas effects in nonrat species, these changes in rats are unlikely predictive of similar changes in humans administered a BTK inhibitor.

Variation of strain rate sensitivity index of a superplastic aluminum alloy in different testing methods

NASA Astrophysics Data System (ADS)

Majidi, Omid; Jahazi, Mohammad; Bombardier, Nicolas; Samuel, Ehab

2017-10-01

The strain rate sensitivity index, m-value, is being applied as a common tool to evaluate the impact of the strain rate on the viscoplastic behaviour of materials. The m-value, as a constant number, has been frequently taken into consideration for modeling material behaviour in the numerical simulation of superplastic forming processes. However, the impact of the testing variables on the measured m-values has not been investigated comprehensively. In this study, the m-value for a superplastic grade of an aluminum alloy (i.e., AA5083) has been investigated. The conditions and the parameters that influence the strain rate sensitivity for the material are compared with three different testing methods, i.e., monotonic uniaxial tension test, strain rate jump test and stress relaxation test. All tests were conducted at elevated temperature (470°C) and at strain rates up to 0.1 s-1. The results show that the m-value is not constant and is highly dependent on the applied strain rate, strain level and testing method.

Interactions between creep, fatigue and strain aging in two refractory alloys

NASA Technical Reports Server (NTRS)

Sheffler, K. D.

1972-01-01

The application of low-amplitude, high-frequency fatigue vibrations during creep testing of two strain-aging refractory alloys (molybdenum-base TZC and tantalum-base T-111) significantly reduced the creep strength of these materials. This strength reduction caused dramatic increases in both the first stage creep strain and the second stage creep rate. The magnitude of the creep rate acceleration varied directly with both frequency and A ratio (ratio of alternating to mean stress), and also varied with temperature, being greatest in the range where the strain-aging phenomenon was most prominent. It was concluded that the creep rate acceleration resulted from a negative strain rate sensitivity which is associated with the strain aging phenomenon in these materials. (A negative rate sensitivity causes flow stress to decrease with increasing strain rate, instead of increasing as in normal materials). By combining two analytical expressions which are normally used to describe creep and strain aging behavior, an expression was developed which correctly described the influence of temperature, frequency, and A ratio on the TZC creep rate acceleration.

The young's modulus of 1018 steel and 67061-T6 aluminum measured from quasi-static to elastic precursor strain-rates

DOE Office of Scientific and Technical Information (OSTI.GOV)

Rae, Philip J; Trujillo, Carl; Lovato, Manuel

2009-01-01

The assumption that Young's modulus is strain-rate invariant is tested for 6061-T6 aluminium alloy and 1018 steel over 10 decades of strain-rate. For the same billets of material, 3 quasi-static strain-rates are investigated with foil strain gauges at room temperature. The ultrasonic sound speeds are measured and used to calculate the moduli at approximately 10{sup 4} s{sup -1}. Finally, ID plate impact is used to generate an elastic pre-cursor in the alloys at a strain-rate of approximately 10{sup 6} s{sup -1} from which the longitudinal sound speed may be obtained. It is found that indeed the Young's modulus is strain-ratemore » independent within the experimental accuracy.« less

Prediction of Mechanical Behaviour of Low Carbon Steel at High Strain Rate Using Thermal Activation Theory and Static Data

NASA Astrophysics Data System (ADS)

Ogawa, Kinya; Kobayashi, Hidetoshi; Sugiyama, Fumiko; Horikawa, Keitaro

Thermal activation theory is well-known to be a useful theory to explain the mechanical behaviour of various metals in the wide range of temperature and strain-rate. In this study, a number of trials to obtain the lower yield stress or flow stress at high strain rates from quasi-static data were carried out using the data shown in the report titled “The final report of research group on high-speed deformation of steels for automotive use”. A relation between the thermal component of stress and the strain rate obtained from experiments for αFe and the temperature-strain rate parameter were used with thermal activation theory. The predictions were successfully performed and they showed that the stress-strain behaviour at high strain rates can be evaluated from quasi-static data with good accuracy.

Recombinant protein expression in Pichia pastoris strains with an engineered methanol utilization pathway

PubMed Central

2012-01-01

Βackground The methylotrophic yeast Pichia pastoris has become an important host organism for recombinant protein production and is able to use methanol as a sole carbon source. The methanol utilization pathway describes all the catalytic reactions, which happen during methanol metabolism. Despite the importance of certain key enzymes in this pathway, so far very little is known about possible effects of overexpressing either of these key enzymes on the overall energetic behavior, the productivity and the substrate uptake rate in P. pastoris strains. Results A fast and easy-to-do approach based on batch cultivations with methanol pulses was used to characterize different P. pastoris strains. A strain with MutS phenotype was found to be superior over a strain with Mut+ phenotype in both the volumetric productivity and the efficiency in expressing recombinant horseradish peroxidase C1A. Consequently, either of the enzymes dihydroxyacetone synthase, transketolase or formaldehyde dehydrogenase, which play key roles in the methanol utilization pathway, was co-overexpressed in MutS strains harboring either of the reporter enzymes horseradish peroxidase or Candida antarctica lipase B. Although the co-overexpression of these enzymes did not change the stoichiometric yields of the recombinant MutS strains, significant changes in the specific growth rate, the specific substrate uptake rate and the specific productivity were observed. Co-overexpression of dihydroxyacetone synthase yielded a 2- to 3-fold more efficient conversion of the substrate methanol into product, but also resulted in a reduced volumetric productivity. Co-overexpression of formaldehyde dehydrogenase resulted in a 2-fold more efficient conversion of the substrate into product and at least similar volumetric productivities compared to strains without an engineered methanol utilization pathway, and thus turned out to be a valuable strategy to improve recombinant protein production. Conclusions Co-overexpressing enzymes of the methanol utilization pathway significantly affected the specific growth rate, the methanol uptake and the specific productivity of recombinant P. pastoris MutS strains. A recently developed methodology to determine strain specific parameters based on dynamic batch cultivations proved to be a valuable tool for fast strain characterization and thus early process development. PMID:22330134

Elongational flow of polymer melts at constant strain rate, constant stress and constant force

NASA Astrophysics Data System (ADS)

Wagner, Manfred H.; Rolón-Garrido, Víctor H.

2013-04-01

Characterization of polymer melts in elongational flow is typically performed at constant elongational rate or rarely at constant tensile stress conditions. One of the disadvantages of these deformation modes is that they are hampered by the onset of "necking" instabilities according to the Considère criterion. Experiments at constant tensile force have been performed even more rarely, in spite of the fact that this deformation mode is free from necking instabilities and is of considerable industrial relevance as it is the correct analogue of steady fiber spinning. It is the objective of the present contribution to present for the first time a full experimental characterization of a long-chain branched polyethylene melt in elongational flow. Experiments were performed at constant elongation rate, constant tensile stress and constant tensile force by use of a Sentmanat Extensional Rheometer (SER) in combination with an Anton Paar MCR301 rotational rheometer. The accessible experimental window and experimental limitations are discussed. The experimental data are modelled by using the Wagner I model. Predictions of the steady-start elongational viscosity in constant strain rate and creep experiments are found to be identical, albeit only by extrapolation of the experimental data to Hencky strains of the order of 6. For constant stress experiments, a minimum in the strain rate and a corresponding maximum in the elongational viscosity is found at a Hencky strain of the order of 3, which, although larger than the steady-state value, follows roughly the general trend of the steady-state elongational viscosity. The constitutive analysis also reveals that constant tensile force experiments indicate a larger strain hardening potential than seen in constant elongation rate or constant tensile stress experiments. This may be indicative of the effect of necking under constant elongation rate or constant tensile stress conditions according to the Considère criterion.

Microstructural and mechanical evolution during deformation and annealing of poly-phase marbles - constraints from laboratory experiments and field observations

NASA Astrophysics Data System (ADS)

Austin, N. J.; Evans, B.; Dresen, G. H.; Rybacki, E.

2009-12-01

Deformed rocks commonly consist of several mineral phases, each with dramatically different mechanical properties. In both naturally and experimentally deformed rocks, deformation mechanisms and, in turn, strength, are commonly investigated by analyzing microstructural elements such as crystallographic preferred orientation (CPO) and recrystallized grain size. Here, we investigated the effect of variations in the volume fraction and the geometry of rigid second phases on the strength and evolution of CPO and grain size of synthetic calcite rocks. Experiments using triaxial compression and torsional loading were conducted at 1023 K and equivalent strain rates between ~2e-6 and 1e-3 s-1. The second phases in these synthetic assemblages are rigid carbon spheres or splinters with known particle size distributions and geometries, which are chemically inert at our experimental conditions. Under hydrostatic conditions, the addition of as little as 1 vol.% carbon spheres poisons normal grain growth. Shape is also important: for an equivalent volume fraction and grain dimension, carbon splinters result in a finer calcite grain size than carbon spheres. In samples deformed at “high” strain rates, or which have “large” mean free spacing of the pinning phase, the final recrystallized grain size is well explained by competing grain growth and grain size reduction processes, where the grain-size reduction rate is determined by the rate that mechanical work is done during deformation. In these samples, the final grain size is finer than in samples heat-treated hydrostatically for equivalent durations. The addition of 1 vol.% spheres to calcite has little effect on either the strength or CPO development. Adding 10 vol.% splinters increases the strength at low strains and low strain rates, but has little effect on the strength at high strains and/or high strain rates, compared to pure samples. A CPO similar to that in pure samples is observed, although the intensity is reduced in samples containing 10 vol.% splinters. When 10 vol.% spheres are added to calcite, the strength of the aggregate is reduced, and a distinct and strong CPO develops. Viscoplastic self consistent calculations were used to model the evolution of CPO in these materials, and these suggest a variation in the activity of the various slip systems within pure samples and those containing 10 vol.% spheres. The applicability of these laboratory observations has been tested with field-based observations made in the Morcles Nappe (Swiss Helvetic Alps). In the Morcles Nappe, calcite grain size becomes progressively finer as the thrust contact is approached, and there is a concomitant increase in CPO intensity, with the strongest CPO’s in the finest-grained, quartz-rich limestones, nearest the thrust contact, which are interpreted to have been deformed to the highest strains. Thus, our laboratory results may be used to provide insight into the distribution of strain observed in natural shear zones.

Strain localisation in mechanically layered rocks beneath detachment zones: insights from numerical modelling

NASA Astrophysics Data System (ADS)

Le Pourhiet, L.; Huet, B.; Labrousse, L.; Yao, K.; Agard, P.; Jolivet, L.

2013-04-01

We have designed a series of fully dynamic numerical simulations aimed at assessing how the orientation of mechanical layering in rocks controls the orientation of shear bands and the depth of penetration of strain in the footwall of detachment zones. Two parametric studies are presented. In the first one, the influence of stratification orientation on the occurrence and mode of strain localisation is tested by varying initial dip of inherited layering in the footwall with regard to the orientation of simple shear applied at the rigid boundary simulating a rigid hanging wall, all scaling and rheological parameter kept constant. It appears that when Mohr-Coulomb plasticity is being used, shear bands are found to localise only when the layering is being stretched. This corresponds to early deformational stages for inital layering dipping in the same direction as the shear is applied, and to later stages for intial layering dipping towards the opposite direction of shear. In all the cases, localisation of the strain after only γ=1 requires plastic yielding to be activated in the strong layer. The second parametric study shows that results are length-scale independent and that orientation of shear bands is not sensitive to the viscosity contrast or the strain rate. However, decreasing or increasing strain rate is shown to reduce the capacity of the shear zone to localise strain. In the later case, the strain pattern resembles a mylonitic band but the rheology is shown to be effectively linear. Based on the results, a conceptual model for strain localisation under detachment faults is presented. In the early stages, strain localisation occurs at slow rates by viscous shear instabilities but as the layered media is exhumed, the temperature drops and the strong layers start yielding plastically, forming shear bands and localising strain at the top of the shear zone. Once strain localisation has occured, the deformation in the shear band becomes extremely penetrative but the strength cannot drop since the shear zone has a finite thickness.

Fitness cost of reassortment in human influenza

PubMed Central

Lässig, Michael

2017-01-01

Reassortment, which is the exchange of genome sequence between viruses co-infecting a host cell, plays an important role in the evolution of segmented viruses. In the human influenza virus, reassortment happens most frequently between co-existing variants within the same lineage. This process breaks genetic linkage and fitness correlations between viral genome segments, but the resulting net effect on viral fitness has remained unclear. In this paper, we determine rate and average selective effect of reassortment processes in the human influenza lineage A/H3N2. For the surface proteins hemagglutinin and neuraminidase, reassortant variants with a mean distance of at least 3 nucleotides to their parent strains get established at a rate of about 10−2 in units of the neutral point mutation rate. Our inference is based on a new method to map reassortment events from joint genealogies of multiple genome segments, which is tested by extensive simulations. We show that intra-lineage reassortment processes are, on average, under substantial negative selection that increases in strength with increasing sequence distance between the parent strains. The deleterious effects of reassortment manifest themselves in two ways: there are fewer reassortment events than expected from a null model of neutral reassortment, and reassortant strains have fewer descendants than their non-reassortant counterparts. Our results suggest that influenza evolves under ubiquitous epistasis across proteins, which produces fitness barriers against reassortment even between co-circulating strains within one lineage. PMID:29112968

Investigation of precipitate refinement in Mg alloys by an analytical composite failure model

DOE Office of Scientific and Technical Information (OSTI.GOV)

Tabei, Ali; Li, Dongsheng; Lavender, Curt A.

2015-10-01

An analytical model is developed to simulate precipitate refinement in second phase strengthened magnesium alloys. The model is developed based on determination of the stress fields inside elliptical precipitates embedded in a rate dependent inelastic matrix. The stress fields are utilized to determine the failure mode that governs the refinement behavior. Using an AZ31 Mg alloy as an example, the effects the applied load, aspect ratio and orientation of the particle is studied on the macroscopic failure of a single α-Mg17Al12 precipitate. Additionally, a temperature dependent version of the corresponding constitutive law is used to incorporate the effects of temperature.more » In plane strain compression, an extensional failure mode always fragments the precipitates. The critical strain rate at which the precipitates start to fail strongly depends on the orientation of the precipitate with respect to loading direction. The results show that the higher the aspect ratio is, the easier the precipitate fractures. Precipitate shape is another factor influencing the failure response. In contrast to elliptical precipitates with high aspect ratio, spherical precipitates are strongly resistant to sectioning. In pure shear loading, in addition to the extensional mode of precipitate failure, a shearing mode may get activated depending on orientation and aspect ratio of the precipitate. The effect of temperature in relation to strain rate was also verified for plane strain compression and pure shear loading cases.« less

Strain Anomalies during an Earthquake Sequence in the South Iceland Seismic Zone

NASA Astrophysics Data System (ADS)

Arnadottir, T.; Haines, A. J.; Geirsson, H.; Hreinsdottir, S.

2017-12-01

The South Iceland Seismic Zone (SISZ) accommodates E-W translation due to oblique spreading between the North American/Hreppar microplate and Eurasian plate, in South Iceland. Strain is released in the SISZ during earthquake sequences that last days to years, at average intervals of 80-100 years. The SISZ is currently in the midst of an earthquake sequence that started with two M6.5 earthquakes in June 2000, and continued with two M6 earthquakes in May 2008. Estimates of geometric strain accumulation, and seismic strain release in these events indicate that they released at most only half of the strain accumulated since the last earthquake cycle in 1896-1912. Annual GPS campaigns and continuous measurements during 2001-2015 were used to calculate station velocities and strain rates from a new method using the vertical derivatives of horizontal stress (VDoHS). This new method allows higher resolution of strain rates than other (older) approaches, as the strain rates are estimated by integrating VDoHS rates obtained by inversion rather than differentiating interpolated GPS velocities. Estimating the strain rates for eight 1-2 year intervals indicates temporal and spatial variation of strain rates in the SISZ. In addition to earthquake faulting, the strain rates in the SISZ are influenced by anthropogenic signals due to geothermal exploitation, and magma movements in neighboring volcanoes - Hekla and Eyjafjallajökull. Subtle signals of post-seismic strain rate changes are seen following the June 2000 M6.5 main shocks, but interestingly, much larger strain rate variations are observed after the two May 2008 M6 main shocks. A prominent strain anomaly is evident in the epicentral area prior to the May 2008 earthquake sequence. The strain signal persists over at least 4 years in the epicentral area, leading up to the M6 main shocks. The strain is primarily extension in ESE-WNW direction (sub-parallel to the direction of plate spreading), but overall shear across the N-S faults that subsequently ruptured, increases with time. The pre-2008 strain anomaly and large post-2008 strain variations are enigmatic, but may signify crustal fluids and/or differences in rheology and crustal thickness between the 2000 and 2008 epicentral areas.

Multi-Ethnic Study of Atherosclerosis: Association between Left Atrial Function Using Tissue Tracking from Cine MR Imaging and Myocardial Fibrosis

PubMed Central

Imai, Masamichi; Ambale Venkatesh, Bharath; Samiei, Sanaz; Donekal, Sirisha; Habibi, Mohammadali; Armstrong, Anderson C.; Heckbert, Susan R.; Wu, Colin O.; Bluemke, David A.

2014-01-01

Purpose To investigate the association between left atrial (LAleft atrium) function and left ventricular myocardial fibrosis using cardiac magnetic resonance (MR) imaging in a multi-ethnic population. Materials and Methods For this HIPAA-compliant study, the institutional review board at each participating center approved the study protocol, and all participants provided informed consent. Of 2839 participants who had undergone cardiac MR in 2010–2012, 143 participants with myocardial scar determined with late gadolinium enhancement and 286 age-, sex-, and ethnicity-matched control participants were identified. LAleft atrium volume, strain, and strain rate were analyzed by using multimodality tissue tracking from cine MR imaging. T1 mapping was applied to assess diffuse myocardial fibrosis. The association between LAleft atrium parameters and myocardial fibrosis was evaluated with the Student t test and multivariable regression analysis. Results The scar group had significantly higher minimum LAleft atrium volume than the control group (mean, 22.0 ± 10.5 [standard deviation] vs 19.0 ± 7.8, P = .002) and lower LAleft atrium ejection fraction (45.9 ± 10.7 vs 51.3 ± 8.7, P < .001), maximal LAleft atrium strain (Smaxmaximum LA strain) (25.4 ± 10.7 vs 30.6 ± 10.6, P < .001) and maximum LAleft atrium strain rate (SRmaxmaximum LA strain rate) (1.08 ± 0.45 vs 1.29 ± 0.51, P < .001), and lower absolute LAleft atrium strain rate at early diastolic peak (SRELA strain rate at early diastolic peak) (−0.77 ± 0.42 vs −1.01 ± 0.48, P < .001) and LAleft atrium strain rate at atrial contraction peak (SRALA strain rate at atrial contraction peak) (−1.50 ± 0.62 vs −1.78 ± 0.69, P < .001) than the control group. T1 time 12 minutes after contrast material injection was significantly associated with Smaxmaximum LA strain (β coefficient = 0.043, P = .013), SRmaxmaximum LA strain rate (β coefficient = 0.0025, P = .001), SRELA strain rate at early diastolic peak (β coefficient = −0.0016, P = .027), and SRALA strain rate at atrial contraction peakLA strain rate at atrial contraction peak (β coefficient −0.0028, P = .01) in the regression model. T1 time 25 minutes after contrast material injection was significantly associated with SRmaxmaximum LA strain rate (β coefficient = 0.0019, P = .016) and SRALA strain rate at atrial contraction peak (β coefficient = −0.0022, P = .034). Conclusion Reduced LAleft atrium regional and global function are related to both replacement and diffuse myocardial fibrosis processes. Clinical trial registration no. NCT00005487 © RSNA, 2014 Online supplemental material is available for this article. PMID:25019562

On the use of a split Hopkinson pressure bar in structural geology: High strain rate deformation of Seeberger sandstone and Carrara marble under uniaxial compression

NASA Astrophysics Data System (ADS)

Zwiessler, Ruprecht; Kenkmann, Thomas; Poelchau, Michael H.; Nau, Siegfried; Hess, Sebastian

2017-04-01

There is increasing evidence that seismogenic fractures can propagate faster than the shear wave velocity of the surrounding rocks. Strain rates within the tip region of such super-shear earthquake ruptures can reach deformation conditions similar to impact processes, resulting in rock pulverization. The physical response of brittle rocks at high strain rates changes dramatically with respect to quasi-static conditions. Rocks become stiffer and their strength increases. A measure for the dynamic behavior of a rock and its strain dependency is the dynamic increase factor (DIF) which is the ratio of the dynamic compressive strength to the quasi-static uniaxial compressive strength. To investigate deformation in the high strain rate regime experimentally, we introduce the split Hopkinson pressure bar technology to the structural geology community, a method that is frequently used by rock and impact engineers. We measure the stress-strain response of homogeneous, fine-grained Seeberger sandstone and Carrara marble in uniaxial compression at strain rates ranging from 10+1 to 10+2 s-1 with respect to tangent modulus and dynamic uniaxial compressive strength. We present full stress-strain response curves of Seeberger sandstone and Carrara marble at high strain rates and an evaluation method to determine representative rates of deformation. Results indicate a rate-dependent elastic behavior of Carrara marble where an average increase of ∼18% could be observed at high strain rates of about 100 s-1. DIF reaches a factor of 2.2-2.4. Seeberger sandstone does not have a rate-dependent linear stress-strain response at high strain rates. Its DIF was found to be about 1.6-1.7 at rates of 100 s-1. The onset of dynamic behavior is accompanied with changes in the fracture pattern from single to multiple fractures to pervasive pulverization for increasing rates of deformation. Seismogenic shear zones and their associated fragment-size spectra should be carefully revisited in the light of dynamic deformation.

Molecular evolution of respiratory syncytial virus subgroup A genotype NA1 and ON1 attachment glycoprotein (G) gene in central Vietnam.

PubMed

Yoshihara, Keisuke; Le, Minh Nhat; Nagasawa, Koo; Tsukagoshi, Hiroyuki; Nguyen, Hien Anh; Toizumi, Michiko; Moriuchi, Hiroyuki; Hashizume, Masahiro; Ariyoshi, Koya; Dang, Duc Anh; Kimura, Hirokazu; Yoshida, Lay-Myint

2016-11-01

We performed molecular evolutionary analyses of the G gene C-terminal 3rd hypervariable region of RSV-A genotypes NA1 and ON1 strains from the paediatric acute respiratory infection patients in central Vietnam during the 2010-2012 study period. Time-scaled phylogenetic analyses were performed using Bayesian Markov Chain Monte Carlo (MCMC) method, and pairwise distances (p-distances) were calculated. Bayesian Skyline Plot (BSP) was constructed to analyze the time-trend relative genetic diversity of central Vietnam RSV-A strains. We also estimated the N-glycosylation sites within G gene hypervariable region. Amino acid substitutions under positive and negative selection pressure were examined using Conservative Single Likelihood Ancestor Counting (SLAC), Fixed Effects Likelihood (FEL), Internal Fixed Effects Likelihood (IFEL) and Mixed Effects Model for Episodic Diversifying Selection (MEME) models. The majority of central Vietnam ON1 strains detected in 2012 were classified into lineage 1 with few positively selected substitutions. As for the Vietnamese NA1 strains, four lineages were circulating during the study period with a few positive selection sites. Shifting patterns of the predominantly circulating NA1 lineage were observed in each year during the investigation period. Median p-distance of central Vietnam NA1 strains was wider (p-distance=0.028) than that of ON1 (p-distance=0.012). The molecular evolutionary rate of central Vietnam ON1 strains was estimated to be 2.55×10 -2 (substitutions/site/year) and was faster than NA1 (7.12×10 -3 (substitutions/site/year)). Interestingly, the evolutionary rates of both genotypes ON1 and NA1 strains from central Vietnam were faster than the global strains respectively. Furthermore, the shifts of N-glycosylation pattern within the G gene 3rd hypervariable region of Vietnamese NA1 strains were observed in each year. BSP analysis indicated the rapid growth of RSV-A effective population size in early 2012. These results suggested that the molecular evolution of RSV-A G gene detected in central Vietnam was fast with unique evolutionary dynamics. Copyright © 2016 Elsevier B.V. All rights reserved.