The influence of using volcanic ash and lime ash as filler on compressive strength in self compacting concrete

NASA Astrophysics Data System (ADS)

Karolina, Rahmi; Panatap Simanjuntak, Murydrischy

2018-03-01

Self Compacting Concrete (SCC) is a technology which is developing today in which concrete solidifies by itself without using vibrator. Casting conventional concrete which has a lot of reinforcement bars sometimes finds difficulty in achieving optimal solidity. The method used to solve this problem is by using SCC technology. SCC was made by using filler, volcanic ash, and lime ash as the filling materials so that the concrete became more solid and hollow space could be filled up. The variation of using these two materials was 10%, 15%, 20%, and 25% of the cementitious mass and using 1% of superplasticizer from cementitious material. The supporting testing was done by using the test when the concrete was still fluid and when it was solid. Malleable concrete was tested by using EFNARC 2002 standard in slump flow test, v-funnel test, l-shaped box test, and j-ring test to obtain filling ability and passing ability. In this malleable lime concrete test, there was the decrease, compared with normal SCC concrete without adding volcanic ash and lime ash. Testing was also done in solid concrete in compressive strength, tensile strength, and concrete absorption. The result of the testing showed that the optimum tensile strength in Variation 1, without volcanic ash and lime ash – with 1% of superplasticizer was 39.556 MPa, the optimum tensile strength in Variation 1, without volcanic ash and lime ash- with 1% of super-plasticizer was 3.563 MPa, while the value of optimum absorption which occurred in Variation 5 (25% of volcanic ash + 25% of lime ash + 50% of cement + 1% of superplasticizer) was 1.313%. This was caused by the addition of volcanic ash and lime ash which had high water absorption.

Incorporation mode effect of Nano-silica on the rheological and mechanical properties of cementitious pastes and cement mortars

NASA Astrophysics Data System (ADS)

Safi, B.; Aknouche, H.; Mechakra, H.; Aboutaleb, D.; Bouali, K.

2018-04-01

Previous research indicates that the inclusion of nanosilica (NS) modifies the properties of the fresh and hardened state, compared to the traditional mineral additions. NS decreases the setting times of the cement mortar compared to silica fume (SF) and reduce of required water while improving the cohesion of the mixtures in the fresh state. Some authors estimate that the appropriate percentage of Nano-silica should be small (1 to 5% by weight) because of difficulties caused by agglomeration to particles during mixing, while others indicate that 10% by weight, if adjustments are made to the formulation to avoid an excess of self-drying and micro cracks that could impede strength. For this purpose, the present work aim to see the effect of the introduction mode of the nanosilica on the rheological and physic mechanical properties of cement mortars. In this study, NS was used either powdered with cement or in solution with the superplasticizer (Superplasticizer doped in nanosilica). Results show that the use of nanosilica powder (replacing cement on the one hand) has a negative influence on the rheological parameters and the rheological behavior of cementitious pastes. However, the introduction of nanosilica in solution in the superplasticizer (SP) was significantly improved the rheological parameters and the rheological behavior of cementitious pastes. Indeed, more the dosage of NS-doped SP increases more the shear stress and viscosities of the cementitious pastes become more fluid and manageable. A significant reduction of shear stress and plastic viscosity were observed that due to the increase in superplasticizer. A dosage of 1.5% NS-doped SP gave adequate fluidity and the shear rate was lower.

A novel kind of concrete superplasticizer based on aryl isocyanate polycondensates

NASA Astrophysics Data System (ADS)

Ding, Bei; Qian, Shanshan; Qiu, Ying; Wang, Yi; Zheng, Chunyang; Wang, Gaoming

2017-03-01

A novel superplasticizer was synthesized by polycondensation of Alkyl phenol phosphate and toluene diisocyanate grafting with methoxy polyoxyethylene ether (MPEG). The chemical structure and molecular weight of polycondensates molecules were determined by 1H nuclear magnetic resonance (NMR) and gel permeation chromatography respectively. The experimental results indicated that the polycondensates of Alkyl phenol phosphate and toluene diisocyanate grafting with MPEG not only exhibited good water-reducing properties but also demonstrated effective anti-clay abilities alone. Furthermore, the polycondensates showed good fluidity maintaining abilities within 1-3 h and good workability of concrete. The results of T500 Time experiments show that lower plastic viscosity of the polycondensates leads to fresh concrete much “looser” than conventional PCEs in self-compacting concrete.

Effects of Using Silica Fume and Polycarboxylate-Type Superplasticizer on Physical Properties of Cementitious Grout Mixtures for Semiflexible Pavement Surfacing

PubMed Central

Karim, Mohamed Rehan; Mahmud, Hilmi; Mashaan, Nuha S.; Katman, Herdayati; Husain, Nadiah Md

2014-01-01

Semi-flexible pavement surfacing is a composite pavement that utilizes the porous pavement structure of the flexible bituminous pavement, which is subsequently grouted with appropriate cementitious materials. This study aims to investigate the compressive strength, flexural strength, and workability performance of cementitious grout. The grout mixtures are designed to achieve high strength and maintain flow properties in order to allow the cement slurries to infiltrate easily through unfilled compacted skeletons. A paired-sample t-test was carried out to find out whether water/cement ratio, SP percentages, and use of silica fume influence the cementitious grout performance. The findings showed that the replacement of 5% silica fume with an adequate amount of superplasticizer and water/cement ratio was beneficial in improving the properties of the cementitious grout. PMID:24526911

Effects of using silica fume and polycarboxylate-type superplasticizer on physical properties of cementitious grout mixtures for semiflexible pavement surfacing.

PubMed

Koting, Suhana; Karim, Mohamed Rehan; Mahmud, Hilmi; Mashaan, Nuha S; Ibrahim, Mohd Rasdan; Katman, Herdayati; Husain, Nadiah Md

2014-01-01

Semi-flexible pavement surfacing is a composite pavement that utilizes the porous pavement structure of the flexible bituminous pavement, which is subsequently grouted with appropriate cementitious materials. This study aims to investigate the compressive strength, flexural strength, and workability performance of cementitious grout. The grout mixtures are designed to achieve high strength and maintain flow properties in order to allow the cement slurries to infiltrate easily through unfilled compacted skeletons. A paired-sample t-test was carried out to find out whether water/cement ratio, SP percentages, and use of silica fume influence the cementitious grout performance. The findings showed that the replacement of 5% silica fume with an adequate amount of superplasticizer and water/cement ratio was beneficial in improving the properties of the cementitious grout.

Ultrafine cementitious grout

DOEpatents

Ahrens, E.H.

1998-07-07

An ultrafine cementitious grout is described having a particle size 90% of which are less than 6 {micro}m in diameter and an average size of about 2.5 {micro}m or less, and preferably 90% of which are less than 5 {micro}m in diameter and an average size of about 2 {micro}m or less containing Portland cement, pumice as a pozzolanic material and superplasticizer in the amounts of about 40 wt. % to about 50 wt. % Portland cement; from about 50 wt. % to about 60 wt. % pumice containing at least 60% amorphous silicon dioxide; and from 0.1 wt. % to about 1.5 wt. % superplasticizer. The grout is mixed with water in the W/CM ratio of about 0.4--0.6/1. The grout has very high strength and very low permeability with good workability. The ultrafine particle sizes allow for sealing of microfractures below 10 {micro}m in width. 4 figs.

Ultrafine cementitious grout

DOEpatents

Ahrens, Ernst H.

1998-01-01

An ultrafine cementitious grout having a particle size 90% of which are less than 6 .mu.m in diameter and an average size of about 2.5 .mu.m or less, and preferably 90% of which are less than 5 .mu.m in diameter and an average size of about 2 .mu.m or less containing Portland cement, pumice as a pozzolanic material and superplasticizer in the amounts of about 40 wt. % to about 50 wt. % Portland cement; from about 50 wt. % to about 60 wt. % pumice containing at least 60% amorphous silicon dioxide; and from 0.1 wt. % to about 1.5 wt. % superplasticizer. The grout is mixed with water in the W/CM ratio of about 0.4-0.6/1. The grout has very high strength and very low permeability with good workability. The ultrafine particle sizes allow for sealing of microfractures below 10 .mu.m in width.

Cyclic behavior of self-consolidated concrete.

DOT National Transportation Integrated Search

2014-08-01

This reports highlights on the production of Self-Consolidating concrete using local materials from Las Vegas, Nevada. 4 SCC : mixtures were worked on with 2 different levels of FA replacement and the inclusion of superplasticizers, ADVA 195 and V-MA...

Influence of Polycarboxylate Superplasticizers on Rheological Properties of Cement Slurries Used in Drilling Technologies / Wpływ Superplastyfikatorów Z Grupy Polikarboksylanów Na Właściwości Reologiczne Zaczynów Cementowych Stosowanych W Technologiach Wiertniczych

NASA Astrophysics Data System (ADS)

Stryczek, Stanisław; Wiśniowski, Rafał; Gonet, Andrzej; Złotkowski, Albert; Ziaja, Jan

2013-09-01

Sealing slurries, mainly the cement-based ones, are concentrated dispersive systems, containing solid particles of considerably developed specific surface. Rheologically, such systems are very complex. This also stems from the fact that the rheological properties have a significant effect on: • additives and admixtures modifying technological properties of fresh and set slurries, • chemically complex mechanism of hydration in a slurry in a function of time. Special attention should paid to plasticizing (plasticizers PL) and liquefying (traditional and new- -generation superplasticizers SP) admixtures affecting the modification and optimization of rheological properties of fresh cement slurries as far as providing efficiency of sealing of casing pipes is concerned. Laboratory analyses were focused on proving the following thesis: properly selected type of superplasticizer [by BASF Polska Sp.z o.o. (The Chemical Company) - Admixtures for Concrete Division] advantageously affects the rheological parameters of sealing slurry based on metallurgical cement CEM III /A 32,5. The following variables were used in the analyses: • type of superplasticizer, • type of batch fluid. The laboratory experiments were made on superplasticizers produced by BASF: • SKY 501, • SKY 503, • SKY 591, • ACE 430, • Glenium 115. The superplasticizer concentration in the slurry was 0.5 wt% (as compared with mass of dry cement). Water to cement ratio for the analyzed sealing slurries was equal to 0.5. The sealing slurries were made of metallurgical cement CEM III/A 32,5 N-LH/HSR/N Lafarge Cement S.A. in Małogoszcz. Zaczyny uszczelniające, a zwłaszcza typu cementowego, są skoncentrowanymi układami dyspersyjnymi, zawierającymi cząstki stałe o znacznie rozwiniętej powierzchni właściwej. Układy takie pod względem reologicznym należą do niezwykle złożonych. Wynika to między innymi z faktu, że na właściwości reologiczne w sposób istotny wpływają: • dodatki i domieszki modyfikujące właściwości technologiczne świeżych i stwardniałych zaczynów, • złożony chemicznie mechanizm reakcje hydratacji zachodzące w zaczynie w funkcji czasu. Na szczególną uwagę ze względu na zapewnienie skuteczność uszczelniania kolumn rur okładzinowych w otworach wiertniczych zasługują domieszki uplastyczniające (plastyfikatory PL) i upłynniające (superplastyfikatory SP typu tradycyjnego oraz nowej generacji) wpływające na modyfikację oraz optymalizację cech reologicznych świeżych zaczynów uszczelniających. Przeprowadzone badania laboratoryjne miały na celu udowodnianie następującej tezy: odpowiednio dobrany rodzaj superplastyfikatorów [firmy BASF Polska Sp.z o.o. ( The Chemical Company) - Dział Domieszek do Betonu], wpływa korzystnie na parametry reologiczne zaczynu uszczelniającego sporządzanego na osnowie cementu hutniczego CEM III /A 32,5. W przeprowadzanych badaniach zmiennymi były: • rodzaj superplastyfikatora, • rodzaj cieczy zarobowej. W badaniach laboratoryjnych zastosowano następujące superplastyfikatory firmy BASF: • SKY 501, • SKY 503, • SKY 591, • ACE 430, • Glenium 115. Koncentracja superplastyfikatora w zaczynie wynosiła: 0,5% wagowo (w stosunku do masy suchego cementu). Współczynnik wodno-cementowy dla badanych zaczynów uszczelniających wynosił: 0,5. Do sporządzania zaczynów uszczelniających stosowano cement hutniczy klasy CEM III/A 32,5 N-LH/ HSR/NA - Cementownia Małogoszcz, Grupa Lafarge Cement S.A. w Małogoszczy.

Evaluation of dense bridge floor concrete using high range water reducer (superplasticizer).

DOT National Transportation Integrated Search

1983-05-01

The objectives of this research project are: (1) To determine the feasibility of proportioning, mixing, placing and finishing a dense portland cement concrete in a bridge floor using conventional mixing, placing and finishing equipment. (2) To determ...

Influence of Silicon-Containing Additives on Concrete Waterproofness Property

NASA Astrophysics Data System (ADS)

Butakova, M. D.; Saribekyan, S. S.; Mikhaylov, A. V.

2017-11-01

The article studies the influence of silicon-containing additives on the property of the water resistance of concrete samples. It provides a review of the literature on common approaches and technologies improving concrete waterproofness and reinforced concrete structures. Normal hardening samples were obtained on the basis of concretes containing microsilica, aerosil or ash, or the combinations thereof. This research is aimed at the study of the complex modifier effect r on the basis of metakaolin, superplasticizer and silicon containing additives on the property of concrete water resistance. The need to use a superplasticizer to reduce the water-cement ratio and metakaolin as a hardening accelerator along with the set of strength is substantiated. This article describes a part of the results of the experiment conducted to find alternative options for colmatizing expensive additives used in the concreting foundations of private house-building. The implementation of the scientific work will not only clarify this area but will also broaden the knowledge of such additive as aerosol.

Preparation and Mechanical Properties of Graphene Oxide: Cement Nanocomposites

PubMed Central

Babak, Fakhim; Abolfazl, Hassani; Alimorad, Rashidi; Parviz, Ghodousi

2014-01-01

We investigate the performance of graphene oxide (GO) in improving mechanical properties of cement composites. A polycarboxylate superplasticizer was used to improve the dispersion of GO flakes in the cement. The mechanical strength of graphene-cement nanocomposites containing 0.1–2 wt% GO and 0.5 wt% superplasticizer was measured and compared with that of cement prepared without GO. We found that the tensile strength of the cement mortar increased with GO content, reaching 1.5%, a 48% increase in tensile strength. Ultra high-resolution field emission scanning electron microscopy (FE-SEM) used to observe the fracture surface of samples containing 1.5 wt% GO indicated that the nano-GO flakes were well dispersed in the matrix, and no aggregates were observed. FE-SEM observation also revealed good bonding between the GO surfaces and the surrounding cement matrix. In addition, XRD diffraction data showed growth of the calcium silicate hydrates (C-S-H) gels in GO cement mortar compared with the normal cement mortar. PMID:24574878

Alleviating Concrete Placement Issues Due to Congestion of Reinforcement in Post-Tensioned Haunch Slab Bridges - Phase 1

DOT National Transportation Integrated Search

2012-07-01

A flowable hybrid concrete mix with a spread of 17 to 20 inches was created with a superplasticizer to be used in post-tension haunch-slab (PTHS) bridges where rebar congestion is heaviest. The mix would allow for proper concrete consolidation. A con...

Assessment of the leaching of metallic elements in the technology of solidification in aqueous solution.

PubMed

Rossetti, V Alunno; Di Palma, L; Medici, F

2002-01-01

Results are presented of experiments performed to optimize the solidification/stabilization system for metallic elements in aqueous solution. This system involves mixing cement and a solution of metallic elements in a conventional mixer: the paste thus obtained is transferred drop by drop into a recipient filled with an aqueous solution of NaOH at 20% by weight, in which it solidifies immediately. The separate use of chloride solutions of Li+, Cr3+, Pb2+ and Zn2+ makes it possible to obtain granules displaying various levels of compressive strength. Three different inertization matrices were used in the experiments, the first consisting solely of Portland cement, the second of Portland cement and a superplasticizer additive, and the third of Portland cement partially replaced with silica-fume and superplasticizer. The results of the tests performed showed a very low level of leaching into the alkaline solidification solution for Cr3+, the quantity leached being under 2% as against higher levels for the other metallic elements. For all the considered elements, the best results were obtained by using silica-fume in the inertization matrix.

High stenghth concrete with high cement substitution by adding fly ash, CaCO3, silica sand, and superplasticizer

NASA Astrophysics Data System (ADS)

Wicaksono, Muchammad Ridho Sigit; Qoly, Amelia; Hidayah, Annisaul; Pangestuti, Endah Kanti

2017-03-01

Concrete is a mixture of cement, fine aggregate, coarse aggregate and water with or without additives. Concrete can be made with substitution of cement with materials like Fly Ash, CaCO3 and silica sand that can increase the binding on pasta and also increase the compressive strength of concrete. The Superplasticizer on a mixture is used to reduce the high water content, improve concrete durability, low permeability concrete by making it more resilient, and improve the quality of concrete. The combination between Fly Ash (30% of cement required), CaCO3 (10% of cement required) and silica sand (5% of cement required) with added MasterGlenium ACE 8595 as much as 1,2% from total cement will produces compressive strength of up to 1080 kN/cm2 or 73,34 Mpa when the concrete is aged at 28 day. By using this technique and innovation, it proves that the cost reduction is calculated at 27%, which is much more efficient. While the strength of the concrete is increased at 5% compared with normal mixture.

Preparation, Characterization and Performances of Powdered Polycarboxylate Superplasticizer with Bulk Polymerization.

PubMed

Liu, Xiao; Wang, Ziming; Zheng, Yunsheng; Cui, Suping; Lan, Mingzhang; Li, Huiqun; Zhu, Jie; Liang, Xu

2014-08-29

A polycarboxylate superplasticizer (PCE) was synthesized in a non-solvent system with bulk polymerization and then was pulverized into powdered form to achieve a rapid transportation and convenient preparation. PCE synthesized by using isopentenyl polyethylene glycol (TPEG) or isobutenyl polyethylene glycol (IPEG) as a macromonomer exhibited the best fluidities and retaining properties at 80 °C and 75 °C, respectively. Besides, azobisisobutyronitrile (AIBN) was suitable as an initiator, and the fumaric acid was suitable as the third monomer. The test results of ¹H nuclear magnetic resonance (¹H NMR) confirmed the occurrences of polymerization, and the measurement results of molecular weight and distribution showed that PCE molecular weight characteristics were in accordance with their fluidity properties in cement paste. The application performances in cement showed that PCEs with the best paste fluidity retentions had the longest final setting time and the shortest setting time interval, and the PCEs with good fluidity properties can obviously delay the hydration process and lower the hydration heat. Accordingly, this is a novel, energy-saving and economical method to prepare powdered PCE in the field of concrete admixtures.

Preparation, Characterization and Performances of Powdered Polycarboxylate Superplasticizer with Bulk Polymerization

PubMed Central

Liu, Xiao; Wang, Ziming; Zheng, Yunsheng; Cui, Suping; Lan, Mingzhang; Li, Huiqun; Zhu, Jie; Liang, Xu

2014-01-01

A polycarboxylate superplasticizer (PCE) was synthesized in a non-solvent system with bulk polymerization and then was pulverized into powdered form to achieve a rapid transportation and convenient preparation. PCE synthesized by using isopentenyl polyethylene glycol (TPEG) or isobutenyl polyethylene glycol (IPEG) as a macromonomer exhibited the best fluidities and retaining properties at 80 °C and 75 °C, respectively. Besides, azobisisobutyronitrile (AIBN) was suitable as an initiator, and the fumaric acid was suitable as the third monomer. The test results of 1H nuclear magnetic resonance (1H NMR) confirmed the occurrences of polymerization, and the measurement results of molecular weight and distribution showed that PCE molecular weight characteristics were in accordance with their fluidity properties in cement paste. The application performances in cement showed that PCEs with the best paste fluidity retentions had the longest final setting time and the shortest setting time interval, and the PCEs with good fluidity properties can obviously delay the hydration process and lower the hydration heat. Accordingly, this is a novel, energy-saving and economical method to prepare powdered PCE in the field of concrete admixtures. PMID:28788184

Flow properties of concentrated suspensions

NASA Technical Reports Server (NTRS)

Hattori, K.; Izumi, K.

1984-01-01

The viscosity and flow behavior of a concentrated suspension, with special emphasis on fresh concrete containing a superplasticizer, is analyzed according to Newton's law of viscosity. The authors interpreted Newton's law in a new way, and explain non-Newton flow from Newton's law. The outline of this new theory is given. Viscosity of suspensions, and the effect of dispersants are analyzed.

Cement paste prior to setting: A rheological approach

DOE Office of Scientific and Technical Information (OSTI.GOV)

Bellotto, Maurizio, E-mail: maurizio.bellotto@bozzetto.it

2013-10-15

The evolution of cement paste during the dormant period is analyzed via small amplitude oscillation rheological measurements. Cement paste, from the very first moments after mixing cement and water, shows the formation of an elastic gel whose strength is rapidly increasing over time. Up to the onset of Portlandite precipitation G′(t) increases by more than 2 orders of magnitude and in the acceleratory period G′(t) continues steadily to increase. A microstructural modification is likely to occur between the dormant and the acceleratory period. At low deformations in the linearity domain the storage modulus G′(ω) exhibits a negligible frequency dependence. Atmore » higher deformations cement paste shows a yield stress which increases on increasing paste concentration. The presence of superplasticizers decreases the yield stress and increases the gelation threshold of the paste. Above the gelation threshold the evolution of cement paste with superplasticizers follows similar trends to the neat paste. -- Highlights: •The gelation of cement paste during the dormant period is analyzed via rheometry. •The observed evolution is proposed to be related to the pore structure refinement. •Similarities are observed with colloidal gels and colloidal glasses.« less

Optimisation of nano-silica modified self-compacting high-Volume fly ash mortar

NASA Astrophysics Data System (ADS)

Achara, Bitrus Emmanuel; Mohammed, Bashar S.; Fadhil Nuruddin, Muhd

2017-05-01

Evaluation of the effects of nano-silica amount and superplasticizer (SP) dosage on the compressive strength, porosity and slump flow on high-volume fly ash self-consolidating mortar was investigated. Multiobjective optimisation technique using Design-Expert software was applied to obtain solution based on desirability function that simultaneously optimises the variables and the responses. A desirability function of 0.811 gives the optimised solution. The experimental and predicted results showed minimal errors in all the measured responses.

Effect of polycarboxylate ether comb-type polymer on viscosity and interfacial properties of kaolinite clay suspensions.

PubMed

Zhang, Ling; Lu, Qingye; Xu, Zhenghe; Liu, Qingxia; Zeng, Hongbo

2012-07-15

The interactions between kaolinite clay particles and a comb-type polymer (polycarboxylate ether or PCE), so-called PCE super-plasticizer, were investigated through viscosity and surface forces measurements by a rheometer and a Surface Forces Apparatus (SFA). The addition of PCE shows a strong impact on the viscosity of concentrated kaolinite suspensions in alkaline solutions (pH=8.3) but a weak effect under acidic conditions (pH=3.4). In acidic solutions, the high viscosity measured is attributed to the strong electrostatic interaction between negatively charged basal planes and positively charged edge surfaces of clay particles. Under the alkaline condition, the suspension viscosity was found to first increase significantly and then decrease with increasing PCE dosages. The results from surface forces measurement show that PCE molecules at low dosages can bridge the kaolinite particles in the concentrated suspensions via hydrogen bonding, leading to the formation of a kaolinite-PCE "network" and hence an increased suspension viscosity. At high PCE dosages, clay particles are fully covered by PCE molecules, leading to a more dispersed kaolinite suspensions and hence lower suspension viscosity due to steric repulsion between the adsorbed PCE molecules. The insights derived from measuring viscosity and interfacial properties of kaolinite suspensions containing varying amount of comb-type super-plasticizer PCE at different pH provide the foundation for many engineering applications and optimizing industrial processes. Copyright © 2012 Elsevier Inc. All rights reserved.

Fly ash/Kaolin based geopolymer green concretes and their mechanical properties

PubMed Central

Okoye, F.N.; Durgaprasad, J.; Singh, N.B.

2015-01-01

Geopolymer concrete mixes were cast using fly ash, kaolin, sodium hydroxide, potassium hydroxide, sodium silicate and aggregates. Portland cement concrete (M30) was used as a reference sample. The effect of silica fume, temperature (40 °C, 60 °C, 80 °C, 100 °C and 120 °C), sodium and potassium hydroxides and different superplasticizers on the compressive strength are reported [1]. Maximum strength was found at 100 °C and 14 M alkali solution [1]. PMID:26693505

Fly ash/Kaolin based geopolymer green concretes and their mechanical properties.

PubMed

Okoye, F N; Durgaprasad, J; Singh, N B

2015-12-01

Geopolymer concrete mixes were cast using fly ash, kaolin, sodium hydroxide, potassium hydroxide, sodium silicate and aggregates. Portland cement concrete (M30) was used as a reference sample. The effect of silica fume, temperature (40 °C, 60 °C, 80 °C, 100 °C and 120 °C), sodium and potassium hydroxides and different superplasticizers on the compressive strength are reported [1]. Maximum strength was found at 100 °C and 14 M alkali solution [1].

Performance of rice husk ash produced using a new technology as a mineral admixture in concrete

DOE Office of Scientific and Technical Information (OSTI.GOV)

Nehdi, M.; Duquette, J.; El Damatty, A

2003-08-01

This article investigates the use of a new technique for the controlled combustion of Egyptian rice husk to mitigate the environmental concerns associated with its uncontrolled burning and provide a supplementary cementing material for the local construction industry. The reactor used provides efficient combustion of rice husk in a short residency time via the suspension of processed particles by jets of a process air stream that is forced though stationary angled blades at high velocity. Investigations on the rice husk ash (RHA) thus produced included oxide analysis, X-ray diffraction, carbon content, grindability, water demand, pozzolanic activity index, surface area, andmore » particle size distribution measurements. In addition, concrete mixtures incorporating various proportions of silica fume (SF) and Egyptian RHA (EG-RHA) produced at different combustion temperatures were made and compared. The workability, superplasticizer and air-entraining admixture requirements, and compressive strength at various ages of these concrete mixtures were evaluated, and their resistance to rapid chloride penetrability and deicing salt surface scaling were examined. Test results indicate that contrary to RHA produced using existing technology, the superplasticizer and air-entraining agent requirements did not increase drastically when the RHA developed in this study was used. Compressive strengths achieved by concrete mixtures incorporating the new RHA exceeded those of concretes containing similar proportions of SF. The resistance to surface scaling of RHA concrete was better than that of concrete containing similar proportions of SF. While the chloride penetrability was substantially decreased by RHA, it remained slightly higher than that achieved by SF concrete.« less

Influence of Eco-Friendly Mineral Additives on Early Age Compressive Strength and Temperature Development of High-Performance Concrete

NASA Astrophysics Data System (ADS)

Kaszynska, Maria; Skibicki, Szymon

2017-12-01

High-performance concrete (HPC) which contains increased amount of both higher grade cement and pozzolanic additives generates more hydration heat than the ordinary concrete. Prolonged periods of elevated temperature influence the rate of hydration process in result affecting the development of early-age strength and subsequent mechanical properties. The purpose of the presented research is to determine the relationship between the kinetics of the heat generation process and the compressive strength of early-age high performance concrete. All mixes were based on the Portland Cement CEM I 52.5 with between 7.5% to 15% of the cement mass replaced by the silica fume or metakaolin. Two characteristic for HPC water/binder ratios of w/b = 0.2 and w/b = 0.3 were chosen. A superplasticizer was used to maintain a 20-50 mm slump. Compressive strength was determined at 8h, 24h, 3, 7 and 28 days on 10x10x10 cm specimens that were cured in a calorimeter in a constant temperature of T = 20°C. The temperature inside the concrete was monitored continuously for 7 days. The study determined that the early-age strength (t<24h) of concrete with reactive mineral additives is lower than concrete without them. This is clearly visible for concretes with metakaolin which had the lowest compressive strength in early stages of hardening. The amount of the superplasticizer significantly influenced the early-age compressive strength of concrete. Concretes with additives reached the maximum temperature later than the concretes without them.

Effect of Ca2+ ion concentration on adsorption of poly(carboxylate ether)-based (PCE) superplasticizer on mica.

PubMed

Wu, Bo; Chun, Byong-Wa; Gu, Le; Kuhl, Tonya L

2018-05-09

Poly(carboxylate ether)-based (PCE) superplasticizers consist of a carboxylic acid backbone and grafted poly(ethylene glycol) (PEG) side chains. Ca 2+ ion bridging mechanism is commonly purported to control PCE's adsorption on negatively charged cement particle surfaces in cement suspension, thus PCE was expected to adsorb on negatively charged surfaces in synthetic pore solutions via Ca 2+ /COO - interactions. Adsorption behaviors of a commercial PCE on negatively charged mica were studied in aqueous electrolyte solutions by a surface forces apparatus. Direct force measurements indicated that the PCE adsorbed onto mica from 0.1 M K 2 SO 4 due to K + ion chelation by the ether oxygen units CH 2 CH 2 O on the PEG chains, but surprisingly did not adsorb from either 0.1 M K 2 SO 4 with saturated Ca(OH) 2 or 0.1 M Ca(NO 3 ) 2 . The adsorption in K 2 SO 4 was weak, enabling the adsorbed PCE layers to be squeezed out under modest compression. Upon separating the surfaces, the PCE immediately achieved an identical re-adsorption. In high-calcium conditions, the PCE was highly positively charged due to Ca 2+ ion chelation by PEG chains and backbone carboxylic groups COO - , and mica also underwent charge reversal due to electrostatic adsorption/binding of Ca 2+ ions. Consequently, the interaction between mica and PCE was electrostatically repulsive and no PCE adsorption occurred. These findings can be explained by the complex interplay of ion chelation by PEG chains, electrostatic binding and screening interactions with charged surfaces in the presence of monovalent and divalent counterions, and ultimately charge reversal of both the charged surfaces and polyelectrolyte in high divalent ion conditions. Copyright © 2018 Elsevier Inc. All rights reserved.

Theoretical and practical aspects of improving the durability of steel reinforcement in transport designs, using passivation and plasticizing chemical additives

NASA Astrophysics Data System (ADS)

Velichko, Evgenij; Talipov, Linar

2017-10-01

The article deals with the problem of steel reinforcement corrosion in reinforced concrete structures exposed to aggressive media, in particular in reinforced concrete construction of transport infrastructure, in snowy areas, and subject to the influence of chlorides contained in applied deicing agents. Basic schemes for preventing the reinforcement corrosion in reinforced-concrete structures have been considered and analyzed. Prospects of primary protection against corrosion of reinforcement by introducing chemical additives with plasticizing/passivating action in a concrete mixture with mixing water have been considered in detail. The physical/chemical mechanism of the protective action of a superplasticizer together with a passivator has been highlighted.

Effect of Silica Fume on two-stage Concrete Strength

NASA Astrophysics Data System (ADS)

Abdelgader, H. S.; El-Baden, A. S.

2015-11-01

Two-stage concrete (TSC) is an innovative concrete that does not require vibration for placing and compaction. TSC is a simple concept; it is made using the same basic constituents as traditional concrete: cement, coarse aggregate, sand and water as well as mineral and chemical admixtures. As its name suggests, it is produced through a two-stage process. Firstly washed coarse aggregate is placed into the formwork in-situ. Later a specifically designed self compacting grout is introduced into the form from the lowest point under gravity pressure to fill the voids, cementing the aggregate into a monolith. The hardened concrete is dense, homogeneous and has in general improved engineering properties and durability. This paper presents the results from a research work attempt to study the effect of silica fume (SF) and superplasticizers admixtures (SP) on compressive and tensile strength of TSC using various combinations of water to cement ratio (w/c) and cement to sand ratio (c/s). Thirty six concrete mixes with different grout constituents were tested. From each mix twenty four standard cylinder samples of size (150mm×300mm) of concrete containing crushed aggregate were produced. The tested samples were made from combinations of w/c equal to: 0.45, 0.55 and 0.85, and three c/s of values: 0.5, 1 and 1.5. Silica fume was added at a dosage of 6% of weight of cement, while superplasticizer was added at a dosage of 2% of cement weight. Results indicated that both tensile and compressive strength of TSC can be statistically derived as a function of w/c and c/s with good correlation coefficients. The basic principle of traditional concrete, which says that an increase in water/cement ratio will lead to a reduction in compressive strength, was shown to hold true for TSC specimens tested. Using a combination of both silica fume and superplasticisers caused a significant increase in strength relative to control mixes.

The effect of steel slag as a coarse aggregate and Sinabung volcanic ash a filler on high strength concrete

NASA Astrophysics Data System (ADS)

Karolina, R.; Putra, A. L. A.

2018-02-01

The Development of concrete technology is continues to grow. The requisite for efficient constructions that are often viewed in terms of concrete mechanical behavior, application on the field, and cost estimation of implementation increasingly require engineers to optimize construction materials, especially for concrete materials. Various types of concrete have now been developed according to their needs, such as high strength concrete. On high strength concrete design, it is necessary to consider several factors that will affect the reach of the quality strength, Those are cement, water cement ratio (w/c), aggregates, and proper admixture. In the use of natural mineral, it is important for an engineer to keep an eye on the natural conditions that have been explored. So the selection of aggregates as possible is a material that is not causing nature destruction. On this experiment the use of steel slag from PT.Growth Sumatra Industry as a substitute of coarse and fine aggregate, and volcanic ash of mount Sinabung as microsilka in concrete mixture substituted to create high strength concrete that is harmless for the environment. The use of mount sinabung volcanic ash as microsilika coupled with the use of Master Glenium Sky 8614 superplasticizer. This experiment intend to compare high strength concrete based slag steel as the main constituent aggregates and high strength concrete with a conventional mixture. The research result for 28 days old concrete shows that conventional concrete compressive strength is 67.567 MPa, slag concrete 75.958 Mpa, conventional tensile strength 5.435 Mpa while slag concrete 5.053 Mpa, conventional concrete bending strength 44064.96 kgcm while concrete slag 51473.94 kgcm and modulus of conventional concrete fracture 124.978 kg / cm2 while slag concrete 145.956 kg / cm2. Both concrete slump values shows similar results due to the use of superplasticizer.

On Gravitational Radiation: A Nonlinear Wave Theory in a Viscoelastic Kerr-Lambda Spacetime

NASA Astrophysics Data System (ADS)

Gamble, Ronald

This project presents the experimental results concerning the mix design, fresh and hardened properties of an ultra-high strength concrete that has already been developed for high performance construction applications but now needs to be evaluated for a 3D printing process. The concrete is designed to be extruded through a nozzle and pump system, and have layers printed to analyze deformation within printed layers. The key factors for printable concrete are, the ability to be extruded through a pump and nozzle (flowability) and buildability. The flow of mortar will be studied by looking at the rheological properties of the mix and assessing the acceptable range of shear strength. Three different water to cement ratios and varying dosages of superplasticizers were incorporated to optimize a workable mortar/concrete mix to be applied for 3D printing. A Brookfield DV-III Ultra programmable rheometer was used to determine the viscosity and yield strength of the mortar mixes; these values were used to calculate the shear strength of the printable concrete. Compressive strengths of optimal mixtures were taken to assess the feasibility of 3D printed concrete as compared to traditional means. Compression test was conducted on a High Capacity Series Compression Testing Machine with 2" x 2" mortars cubes. The results indicated that the mortars that have shear ranges between of 0.3 - 0.9 kPa could be used in a 3D printer. The compressive strength of the concrete made with a 25% water/cement ratio and 10% superplasticizer dosage reached 62.8 MPa, which qualifies it as ultrahigh strength mortar. An optimum mix will be validated by printing the most filaments until deformation occurs. The end goal of this project is to develop an optimal concrete to produce the strength needed for 3D printed concrete. Using our predesigned ultra-high strength concrete mix ingredients, we will optimize that mix to have the same performance characteristics and be used in 3D printing applications.

Dataset on predictive compressive strength model for self-compacting concrete.

PubMed

Ofuyatan, O M; Edeki, S O

2018-04-01

The determination of compressive strength is affected by many variables such as the water cement (WC) ratio, the superplasticizer (SP), the aggregate combination, and the binder combination. In this dataset article, 7, 28, and 90-day compressive strength models are derived using statistical analysis. The response surface methodology is used toinvestigate the effect of the parameters: Varying percentages of ash, cement, WC, and SP on hardened properties-compressive strengthat 7,28 and 90 days. Thelevels of independent parameters are determinedbased on preliminary experiments. The experimental values for compressive strengthat 7, 28 and 90 days and modulus of elasticity underdifferent treatment conditions are also discussed and presented.These dataset can effectively be used for modelling and prediction in concrete production settings.

Experimental study on the performance of pervious concrete

NASA Astrophysics Data System (ADS)

Liu, Haojie; Liu, Rentai; Yang, Honglu; Ma, Chenyang; Zhou, Heng

2018-02-01

With the construction of sponge city, the pervious concrete material has been developed rapidly. A high-performance pervious concrete is developed by using cement, silica fume (SF) and superplasticizer (SP). The effects of SF, SP, aggregate size, water-cement ration and aggregate-cement ratio on the permeability coefficient, compressive strength and flexural strength are studied by controlling variables, and exploring the corrosion resistance and abrasion resistance of pervious concrete. The results show that using 0.5% SP, 5% SF and small aggregate can greatly improve the strength. There is an optimum value for water-cement ratio to make the strength and permeability coefficient maximum. Compared to ordinary pervious concrete, the corrosion resistance and abrasion resistance of this pervious concrete are very good.

The assessment of bond strength between heat damaged concrete and high strength fibre reinforced concrete

NASA Astrophysics Data System (ADS)

Zahid, M. Z. A. Mohd; Muhamad, K.

2017-09-01

The aim of this study is to assess the bond strength between heat damaged concrete and high strength fibre reinforced concrete (HPFRC). Firstly, this paper presents the various steps taken to prepare the HPFRC with self-compacting property. The minimum targeted slump flow is 600 mm and minimum targeted compressive strength is 80 MPa. The key mix variables considered are such as type of superplasticizer, water cement ratio and silica fume content. Then, the bond strength between the heat damaged concrete with HPFRC was examined. The experimental parameters are heating temperature, surface treatment technique and curing method and the results show that, all experimental parameters are significantly affected the bond strength between heat damaged concrete and HPFRC.

Thermally conductive cementitious grout for geothermal heat pump systems

DOEpatents

Allan, Marita

2001-01-01

A thermally conductive cement-sand grout for use with a geothermal heat pump system. The cement sand grout contains cement, silica sand, a superplasticizer, water and optionally bentonite. The present invention also includes a method of filling boreholes used for geothermal heat pump systems with the thermally conductive cement-sand grout. The cement-sand grout has improved thermal conductivity over neat cement and bentonite grouts, which allows shallower bore holes to be used to provide an equivalent heat transfer capacity. In addition, the cement-sand grouts of the present invention also provide improved bond strengths and decreased permeabilities. The cement-sand grouts can also contain blast furnace slag, fly ash, a thermoplastic air entraining agent, latex, a shrinkage reducing admixture, calcium oxide and combinations thereof.

Effect of Admixtures on the Yield Stresses of Cement Pastes under High Hydrostatic Pressures

PubMed Central

Yim, Hong Jae; Kim, Jae Hong; Kwon, Seung Hee

2016-01-01

When cement-based materials are transported at a construction site, they undergo high pressures during the pumping process. The rheological properties of the materials under such high pressures are unknown, and estimating the workability of the materials after pumping is a complex problem. Among various influential factors on the rheology of concrete, this study investigated the effect of mineral and chemical admixtures on the high-pressure rheology. A rheometer was fabricated that could measure the rheological properties while maintaining a high pressure to simulate the pumping process. The effects of superplasticizer, silica fume, nanoclay, fly ash, or ground granulated blast furnace slag were investigated when mixed with two control cement pastes. The water-to-cement ratios were 0.35 and 0.50. PMID:28773273

Effects of surfactants on the properties of mortar containing styrene/methacrylate superplasticizer.

PubMed

Negim, El-Sayed; Kozhamzharova, Latipa; Khatib, Jamal; Bekbayeva, Lyazzat; Williams, Craig

2014-01-01

The physical and mechanical properties of mortar containing synthetic cosurfactants as air entraining agent are investigated. The cosurfactants consist of a combination of 2% dodecyl benzene sodium sulfonate (DBSS) and either 1.5% polyvinyl alcohol (PVA) or 1.5% polyoxyethylene glycol monomethyl ether (POE). Also these cosurfactants were used to prepare copolymers latex: styrene/butyl methacrylate (St/BuMA), styrene/methyl methacrylate (St/MMA), and styrene/glycidyl methacrylate (St/GMA), in order to study their effects on the properties of mortar. The properties of mortar examined included flow table, W/C ratio, setting time, water absorption, compressive strength, and combined water. The results indicate that the latex causes improvement in mortar properties compared with cosurfactants. Also polymer latex containing DBSS/POE is more effective than that containing DBSS/PVA.

Effects of Surfactants on the Properties of Mortar Containing Styrene/Methacrylate Superplasticizer

PubMed Central

Negim, El-Sayed; Kozhamzharova, Latipa; Khatib, Jamal; Bekbayeva, Lyazzat; Williams, Craig

2014-01-01

The physical and mechanical properties of mortar containing synthetic cosurfactants as air entraining agent are investigated. The cosurfactants consist of a combination of 2% dodecyl benzene sodium sulfonate (DBSS) and either 1.5% polyvinyl alcohol (PVA) or 1.5% polyoxyethylene glycol monomethyl ether (POE). Also these cosurfactants were used to prepare copolymers latex: styrene/butyl methacrylate (St/BuMA), styrene/methyl methacrylate (St/MMA), and styrene/glycidyl methacrylate (St/GMA), in order to study their effects on the properties of mortar. The properties of mortar examined included flow table, W/C ratio, setting time, water absorption, compressive strength, and combined water. The results indicate that the latex causes improvement in mortar properties compared with cosurfactants. Also polymer latex containing DBSS/POE is more effective than that containing DBSS/PVA. PMID:24955426

Characteristics of SCC with Fly Ash and Manufactured Sand

NASA Astrophysics Data System (ADS)

Praveen Kumar, K.; Radhakrishna

2016-09-01

Self compacting concrete (SCC) of M40 grade was designed. The binder in SCC consists of OPC and fly ash in the ratio of 65:35. River sand was replaced by manufactured sand (M-sand) at replacement levels of 20,40,60,80 and 100%. An attempt was made to evaluate the workability and strength characteristics of self compacting concrete with river sand and manufactured sand as fine aggregates. For each replacement level, constant workability was maintained by varying the dosage of superplasticizer. T50 flow time, V Funnel time, V-funnel T5 time as well as compressive, split tensile and flexural strength of SCC were found at each replacement level of M-sand. They were compared to SCC with river sand. Results indicate favourable use of M-sand in preparation of Self Compacting Concrete.

Aggregate assesment and durability evaluation of optimized graded concrete in the state of Oklahoma

NASA Astrophysics Data System (ADS)

Ghaeezadeh, Ashkan

This research is a part of a larger project that emphasizes on creating a more scientific approach to designing concrete mixtures for concrete pavements that use less cement and more aggregate which is called optimized graded concrete. The most challenging obstacle in optimized mixtures is reaching enough workability so that one doesn't have to add more cement or super-plasticizer to reach the desired level of flowability. Aggregate gradation and characteristics have found to be very important when it comes to the workabaility of optimized graded concrete. In this research a new automated method of aggregate assessment was used to compare the shape and the surface of different aggregates as well as their influence on the concrete flowability. At the end, the performance of optimized graded concrete against drying shrinkage and freezing and thawing condition were investigated.

Possibilities of using aluminate cements in high-rise construction

NASA Astrophysics Data System (ADS)

Kaddo, Maria

2018-03-01

The article describes preferable ways of usage of alternative binders for high-rise construction based on aluminate cements. Possible areas of rational use of aluminate cements with the purpose of increasing the service life of materials and the adequacy of the durability of materials with the required durability of the building are analyzed. The results of the structure, shrinkage and physical and mechanical properties of concrete obtained from dry mixes on the base of aluminate cements for self-leveling floors are presented. To study the shrinkage mechanism of curing binders and to evaluate the role of evaporation of water in the development of shrinkage was undertaken experiment with simple unfilled systems: gypsum binder, portland cement and «corrosion resistant high alumina cement + gypsum». Principle possibility of binder with compensated shrinkage based on aluminate cement, gypsum and modern superplasticizers was defined, as well as cracking resistance and corrosion resistance provide durability of the composition.

Design of rapid hardening engineered cementitious composites for sustainable construction

NASA Astrophysics Data System (ADS)

Marushchak, Uliana; Sanytsky, Myroslav; Sydor, Nazar

2017-12-01

This paper deals with design of environmentally friendly Rapid Hardening Engineered Cementitious Composite (RHECC) nanomodified with ultrafine mineral additives, polycarboxylate ether based superplasticizer, calcium hydrosilicate nanoparticles and dispersal reinforced by fibers. The incremental coefficient of surface activity was proposed in order to estimation of ultrafine supplementary materials (fly ash, methakaolin, microsilica) efficiency. A characterization of RHECC's compressive and flexural properties at different ages is reported in this paper. Early compressive strength of ECC is 45-50 MPa, standard strength - 84-95 MPa and parameter Rc2/Rc28 - 65-70%. The microstructure of the cement matrix and RHECC was investigated. The use of ultrafine mineral supplementary materials provides reinforcement of structure on micro- and nanoscale level (cementing matrix) due to formation of sub-microreinforcing hydrate phase as AFt- and C-S-H phases in unclinker part of cement matrix, resulting in the phenomena of "self-reinforcement" on the microstructure level. Designed RHECC may be regarded as lower brittle since the crack resistance coefficient is higher comparison to conventional fine grain concrete.

Fresh and mechanical properties of self-compacting concrete with coarse aggregate replacement using Waste of Oil Palm Shell

NASA Astrophysics Data System (ADS)

Prayuda, Hakas; Saleh, Fadillawaty; Ilham Maulana, Taufiq; Monika, Fanny

2018-05-01

Self-compacting Concrete (SCC) is a real innovation that can solidify itself without the help of tools to ease field practice. In its implementation, SCC can use alternative materials to reduce waste, such as Oil Palm Shell (OPS). In this research, OPS used as a replacement of crushed stone as the main coarse aggregate. The concrete mixture used consists of cement, sand, crushed stone, OPS as a variation of aggregate substitutes, palm oil fuel ash, and superplasticizer. OPS used were variated with 0%, 5%, 10%, 25% and 50% of crushed stone aggregate weight with age up to 28 days. Tests were conducted on fresh and mechanical properties. From the results, it is known that replacement of aggregate using OPS meets fresh properties criteria and although the compressive strength of OPS concrete mixture is lower than normal SCC, OPS still can be an alternative in making SCC and reducing palm oil industrial waste.

Rheological and Mechanical Response Modifications for a Self-Leveling Mortar

NASA Astrophysics Data System (ADS)

Katsiadramis, N. J.; Sotiropoulou, A. B.; Pandermarakis, Z. G.

2010-06-01

In many cases cement based materials demand a higher flowability and workability and this conventionally can’t be done without loss of its strength, due to the fact that the common practice to increase the workability is the addition of water. But, nowadays using a third generation superplasticizer (SP) we can achieve the desire flowability without loss of its strength. The action of superplastisizers is to spread efficiently the cement grains and so to wetting better the cement grains giving a more homogeneous mixture with higher strength. Nine different mixtures were prepared adding a small percentage of SP (1%). The conditions to get a self levelling mortar, have to do not only with rheological but also with mechanical demands. The bending and compression test gave the achieving mechanical strength whereas their rheological response came through slump flow and v-funnel flow tests. With the help of a small amount of stabilizer we obtain a robust mixture that deserves the desire response at the field too.

Triple-activated blast furnace slag

DOE Office of Scientific and Technical Information (OSTI.GOV)

Clarke, W.J.

1995-12-31

The current shortage of portland cement in the world will require the use of Ground Granulated Blast Furnace Slag (GGBFS) to fill demands in many industrialized countries. Therefore, an extensive series of triple-activated slag experiments have been undertaken to optimize an economical combination of mechanical properties for alkali-activated slags. Na{sub 2}OSiO{sub 2} (N Grade), Ca(OH){sub 2}, H{sub 2}O and Na{sub 2}CO{sub 3} have been added as activators in 5 to 10, 0 to 5 and 0 to 5 weight percentages of water and slag in a mix with a water:cement ratio of 1:1. Silica Fume and Sika 10 superplasticizer havemore » been added as 1 and 10 weight percent of slag. Set times, initial hardening times and compressive strengths at percentages of the mix to identify more refined formulations. Finally, the resulting aggregate to develop a triple-activated slag formulation with the ultimate objective of contributing toward satisfying the world shortage of high performance concrete.« less

Preferential adsorption of polycarboxylate superplasticizers on cement and silica fume in ultra-high performance concrete (UHPC)

DOE Office of Scientific and Technical Information (OSTI.GOV)

Schroefl, Ch.; Gruber, M.; Plank, J., E-mail: sekretariat@bauchemie.ch.tum.de

2012-11-15

UHPC is fluidized particularly well when a blend of MPEG- and APEG-type PCEs is applied. Here, the mechanism for this behavior was investigated. Testing individual cement and micro silica pastes revealed that the MPEG-PCE disperses cement better than silica whereas the APEG-PCE fluidizes silica particularly well. This behavior is explained by preferential adsorption of APEG-PCE on silica while MPEG-PCEs exhibit a more balanced affinity to both cement and silica. Adsorption data obtained from individual cement and micro silica pastes were compared with those found for the fully formulated UHPC containing a cement/silica blend. In the UHPC formulation, both PCEs stillmore » exhibit preferential and selective adsorption similar as was observed for individual cement and silica pastes. Preferential adsorption of PCEs is explained by their different stereochemistry whereby the carboxylate groups have to match with the steric position of calcium ions/atoms situated at the surfaces of cement hydrates or silica.« less

Performance of mechanical behavior of kenaf fibre reinforced foamed composite

NASA Astrophysics Data System (ADS)

Mahzabin, Mst. Sadia; Hock, Lim Jee; Kang, Lim Siong; Jarghouyeh, Ehsan Nikbakht

2017-10-01

This paper investigates the mechanical properties of lightweight foamed composite (LFC) with the inclusion of kenaf fibres and superplasticizer. NaOH treated kenaf fibre contents of 0.4%, 0.45% and 0.5% (by weight of cement) with 5cm length were used in composite. The density of 1000kg/m3 to 2000kg/m3 foamed concrete was used for all the tested specimens. The ratio of cement, sand and water used was 1:1.5:0.45. All the experiments were set up in accordance with International standard methods of testing. In reference to the results and discussion, the different percentages of fibre used were proven to have a lesser contribution towards compressive strength or might even have reduced the result. The results also showed that water absorption and density of the composite mortar increased as the volume of fiber increased from 0.4% to 0.5% However, a higher percentage of fiber inclusions had been recorded to have a positive contribution towards flexural and tensile splitting properties of composites.

Advances in understanding hydration of Portland cement

DOE Office of Scientific and Technical Information (OSTI.GOV)

Scrivener, Karen L., E-mail: Karen.scrivener@epfl.ch; Juilland, Patrick; Monteiro, Paulo J.M.

2015-12-15

Progress in understanding hydration is summarized. Evidence supports the geochemistry dissolution theory as an explanation for the induction period, in preference to the inhibiting layer theory. The growth of C–S–H is the principal factor controlling the main heat evolution peak. Electron microscopy indicates that C–S–H “needles” grow from the surface of grains. At the peak, the surface is covered, but deceleration cannot be attributed to diffusion control. The shoulder peak comes from renewed reaction of C{sub 3}A after depletion of sulfate in solution, but release of sulfate absorbed on C–S–H means that ettringite continues to form. After several days spacemore » becomes the major factor controlling hydration. The use of new analytical technique is improving our knowledge of the action of superplasticizers and leading to the design of molecules for different applications. Atomistic modeling is becoming a topic of increasing interest. Recent publications in this area are reviewed.« less

Effects of Different Mineral Admixtures on the Properties of Fresh Concrete

PubMed Central

Nuruddin, Muhammad Fadhil; Shafiq, Nasir

2014-01-01

This paper presents a review of the properties of fresh concrete including workability, heat of hydration, setting time, bleeding, and reactivity by using mineral admixtures fly ash (FA), silica fume (SF), ground granulated blast furnace slag (GGBS), metakaolin (MK), and rice husk ash (RHA). Comparison of normal and high-strength concrete in which cement has been partially supplemented by mineral admixture has been considered. It has been concluded that mineral admixtures may be categorized into two groups: chemically active mineral admixtures and microfiller mineral admixtures. Chemically active mineral admixtures decrease workability and setting time of concrete but increase the heat of hydration and reactivity. On the other hand, microfiller mineral admixtures increase workability and setting time of concrete but decrease the heat of hydration and reactivity. In general, small particle size and higher specific surface area of mineral admixture are favourable to produce highly dense and impermeable concrete; however, they cause low workability and demand more water which may be offset by adding effective superplasticizer. PMID:24701196

Effects of different mineral admixtures on the properties of fresh concrete.

PubMed

Khan, Sadaqat Ullah; Nuruddin, Muhammad Fadhil; Ayub, Tehmina; Shafiq, Nasir

2014-01-01

This paper presents a review of the properties of fresh concrete including workability, heat of hydration, setting time, bleeding, and reactivity by using mineral admixtures fly ash (FA), silica fume (SF), ground granulated blast furnace slag (GGBS), metakaolin (MK), and rice husk ash (RHA). Comparison of normal and high-strength concrete in which cement has been partially supplemented by mineral admixture has been considered. It has been concluded that mineral admixtures may be categorized into two groups: chemically active mineral admixtures and microfiller mineral admixtures. Chemically active mineral admixtures decrease workability and setting time of concrete but increase the heat of hydration and reactivity. On the other hand, microfiller mineral admixtures increase workability and setting time of concrete but decrease the heat of hydration and reactivity. In general, small particle size and higher specific surface area of mineral admixture are favourable to produce highly dense and impermeable concrete; however, they cause low workability and demand more water which may be offset by adding effective superplasticizer.

Preparation and thermal insulation performance of cast-in-situ phosphogypsum wall.

PubMed

Li, Yubo; Dai, Shaobin; Zhang, Yichao; Huang, Jun; Su, Ying; Ma, Baoguo

2018-01-01

The mass accumulation of phosphogypsum has caused serious environmental pollution, which has become a worldwide problem. Gypsum is a kind of green building material, which is lighter, has better heat and sound insulation performance, and is easier to recycle compared to cement. The application of cast-in-situ phosphogypsum wall could consume a large amount of pollutant, and improve the efficiency of building construction. The preparation and thermal insulation performance of cast-in-situ phosphogypsum wall were investigated. The property of phosphogypsum-fly ash-lime (PFL) triad cementing materials, the adaptability of retarders and superplasticizers, and the influences of vitrified microsphere as aggregates were explored. Thus, the optimum mix was proposed. Thermal insulation performance tests and ANSYS simulation of this material was carried out. Optimal structures based on heat channels and the method of calculation determining related parameters were proposed, which achieved a 12.3% reduction in the heat transfer coefficient of the wall. With good performance, phosphogypsum could be used in cast-in-situ walls. This paper provides the theoretical basis for the preparation and energy-saving application of phosphogypsum in the walls of buildings.

Sustainability, Eco-Point and Engineering Performance of Different Workability OPC Fly-Ash Mortar Mixes.

PubMed

Razi, Putri Zulaiha; Abdul Razak, Hashim; Khalid, Nur Hafizah A

2016-05-06

This study investigates the engineering performance and CO₂ footprint of mortar mixers by replacing Portland cement with 10%, 20%, 40% and 60% fly ash, a common industrial waste material. Samples of self-compacting mortar (SCM) were prepared with four different water/binder ratios and varying dosages of superplasticizer to give three ranges of workability, i.e. , normal, high and self-compacting mortar mix. The engineering performance was assessed in term of compressive strength after designated curing periods for all mixes. CO₂ footprint was the environmental impact indicator of each production stage. The optimum mix obtained was at 10% replacement rate for all mixes. Total production emission reduced by 56% when the fly ash replacement rate increased from 0% to 60% (maximum). This is translated to a reduction of 80% in eco-points (assuming that the energy consumption rate of production with 0% fly ash is at 100%). Such re-utilization is encouraged since it is able to reduce possible soil toxicity due to sulfur leaching by 5% to 27% and landfill area by 15% to 91% on average.

Sustainability, Eco-Point and Engineering Performance of Different Workability OPC Fly-Ash Mortar Mixes

PubMed Central

Razi, Putri Zulaiha; Abdul Razak, Hashim; Khalid, Nur Hafizah A.

2016-01-01

This study investigates the engineering performance and CO2 footprint of mortar mixers by replacing Portland cement with 10%, 20%, 40% and 60% fly ash, a common industrial waste material. Samples of self-compacting mortar (SCM) were prepared with four different water/binder ratios and varying dosages of superplasticizer to give three ranges of workability, i.e., normal, high and self-compacting mortar mix. The engineering performance was assessed in term of compressive strength after designated curing periods for all mixes. CO2 footprint was the environmental impact indicator of each production stage. The optimum mix obtained was at 10% replacement rate for all mixes. Total production emission reduced by 56% when the fly ash replacement rate increased from 0% to 60% (maximum). This is translated to a reduction of 80% in eco-points (assuming that the energy consumption rate of production with 0% fly ash is at 100%). Such re-utilization is encouraged since it is able to reduce possible soil toxicity due to sulfur leaching by 5% to 27% and landfill area by 15% to 91% on average. PMID:28773465

Comparison of Glass Powder and Fly Ash Effect on the Fresh Properties of Self-Compacting Mortars

NASA Astrophysics Data System (ADS)

Öznur Öz, Hatice; Erhan Yücel, Hasan; Güneş, Muhammet

2017-10-01

This study is aimed to determine effects of glass powder on fresh properties of self-compacting mortars. Self-compacting mortars incorporating glass powder (SCMGPs) were designed with a water/binder ratio of 0.40 and a total binder content of 550 kg/m3. At first, the control mixture was produced with 20% fly ash and % 80 cement of the total binder content without using the glass powder. Then, glass powder was used in the proportions 5%, 10%, 15% and 20% instead of fly ash in the mortars. Mini-slump flow and mini-v funnel tests experimentally investigated on SCMGPs to compare the effect of fly ash and glass powder. With increasing the amount of glass powder used in SCMGPs increased the amount of superplasticizer used to obtain the desired mini-slump flow diameter. So, the use of glass powder reduced the flow ability of SCMGPs in comparison to fly ash. Additionally, the compressive strength and flexural strength of the mortar mixtures were determined at the 28th day. The test results indicated that the mechanical characteristics of SCMGPs improved when the fly ash was replaced with glass powder in SCMGPs.

The Effect of Graphene Oxide on Cement Mortar

NASA Astrophysics Data System (ADS)

Kjaernsmo, Henrik; Kakay, Samdar; Fossa, Kjell T.; Gronli, John

2018-05-01

This paper investigates the effect of water dispersed- and powder Graphene oxide (GO) nanoparticle on fresh cement mortar, microstructure and mechanical strength after 3,7, and 28 days of curing. These properties were studied by treating the cement mortar with 0.03 wt%, 0.05 wt%, and 0.2 wt% GO of the cement weight combined with 0.8wt % polycarboxylate superplasticizer. The results show that the workability decreases as increasing the content of water dispersed GO. The heat of hydration is increased for both types of GO systems. The percent air content in 0.03 wt% and 0.05 wt% GO is almost constant, but increased from 3.2 % to 4.9 % in 0.2 wt% water dispersed GO. The increased air content has effect on poor compaction and workability. GO has the potential of accelerating the hydration process and enhance the early mechanical strength (3 and 7 days), but the workability seems to diminish the mechanical strength after 28 days of curing, particularly for the highest content of water dispersed GO. No distinct influence of GO on the microstructure. The overall results showed that the impact of water dispersed GO was found out to be higher than the powder GO.

Recycling ground granulated blast furnace slag as cold bonded artificial aggregate partially used in self-compacting concrete.

PubMed

Gesoğlu, Mehmet; Güneyisi, Erhan; Mahmood, Swara Fuad; Öz, Hatice Öznur; Mermerdaş, Kasım

2012-10-15

Ground granulated blast furnace slag (GGBFS), a by-product from iron industry, was recycled as artificial coarse aggregate through cold bonding pelletization process. The artificial slag aggregates (ASA) replaced partially the natural coarse aggregates in production of self-compacting concrete (SCC). Moreover, as being one of the most widely used mineral admixtures in concrete industry, fly ash (FA) was incorporated as a part of total binder content to impart desired fluidity to SCCs. A total of six concrete mixtures having various ASA replacement levels (0%, 20%, 40%, 60%, and 100%) were designed with a water-to-binder (w/b) ratio of 0.32. Fresh properties of self-compacting concretes (SCC) were observed through slump flow time, flow diameter, V-funnel flow time, and L-box filling height ratio. Compressive strength of hardened SCCs was also determined at 28 days of curing. It was observed that increasing the replacement level of ASA resulted in decrease in the amount of superplasticizer to achieve a constant slump flow diameter. Moreover, passing ability and viscosity of SCC's enhanced with increasing the amount of ASA in the concrete. The maximum compressive strength was achieved for the SCC having 60% ASA replacement. Copyright © 2012 Elsevier B.V. All rights reserved.

Dataset of producing and curing concrete using domestic treated wastewater

PubMed Central

Asadollahfardi, Gholamreza; Delnavaz, Mohammad; Rashnoiee, Vahid; Fazeli, Alireza; Gonabadi, Navid

2015-01-01

We tested the setting time of cement, slump and compressive and tensile strength of 54 triplicate cubic samples and 9 cylindrical samples of concrete with and without a Super plasticizer admixture. We produced concrete samples made with drinking water and treated domestic wastewater containing 300, 400 kg/m3 of cement before chlorination and then cured concrete samples made with drinking water and treated wastewater. Second, concrete samples made with 350 kg/m3 of cement with a Superplasticizer admixture made with drinking water and treated wastewater and then cured with treated wastewater. The compressive strength of all the concrete samples made with treated wastewater had a high coefficient of determination with the control concrete samples. A 28-day tensile strength of all the samples was 96–100% of the tensile strength of the control samples and the setting time was reduced by 30 min which was consistent with a ASTMC191 standard. All samples produced and cured with treated waste water did not have a significant effect on water absorption, slump and surface electrical resistivity tests. However, compressive strength at 21 days of concrete samples using 300 kg/m3 of cement in rapid freezing and thawing conditions was about 11% lower than concrete samples made with drinking water. PMID:26862577

Dataset of producing and curing concrete using domestic treated wastewater.

PubMed

Asadollahfardi, Gholamreza; Delnavaz, Mohammad; Rashnoiee, Vahid; Fazeli, Alireza; Gonabadi, Navid

2016-03-01

We tested the setting time of cement, slump and compressive and tensile strength of 54 triplicate cubic samples and 9 cylindrical samples of concrete with and without a Super plasticizer admixture. We produced concrete samples made with drinking water and treated domestic wastewater containing 300, 400 kg/m(3) of cement before chlorination and then cured concrete samples made with drinking water and treated wastewater. Second, concrete samples made with 350 kg/m(3) of cement with a Superplasticizer admixture made with drinking water and treated wastewater and then cured with treated wastewater. The compressive strength of all the concrete samples made with treated wastewater had a high coefficient of determination with the control concrete samples. A 28-day tensile strength of all the samples was 96-100% of the tensile strength of the control samples and the setting time was reduced by 30 min which was consistent with a ASTMC191 standard. All samples produced and cured with treated waste water did not have a significant effect on water absorption, slump and surface electrical resistivity tests. However, compressive strength at 21 days of concrete samples using 300 kg/m(3) of cement in rapid freezing and thawing conditions was about 11% lower than concrete samples made with drinking water.

Development of Mix Design Method in Efforts to Increase Concrete Performance Using Portland Pozzolana Cement (PPC)

NASA Astrophysics Data System (ADS)

Krisnamurti; Soehardjono, A.; Zacoeb, A.; Wibowo, A.

2018-01-01

Earthquake disaster can cause infrastructure damage. Prevention of human casualties from disasters should do. Prevention efforts can do through improving the mechanical performance of building materials. To achieve high-performance concrete (HPC), usually used Ordinary Portland Cement (OPC). However, the most widely circulating cement types today are Portland Pozzolana Cement (PPC) or Portland Composite Cement (PCC). Therefore, the proportion of materials used in the HPC mix design needs to adjust to achieve the expected performance. This study aims to develop a concrete mix design method using PPC to fulfil the criteria of HPC. The study refers to the code/regulation of concrete mixtures that use OPC based on the results of laboratory testing. This research uses PPC material, gravel from Malang area, Lumajang sand, water, silica fume and superplasticizer of a polycarboxylate copolymer. The analyzed information includes the investigation results of aggregate properties, concrete mixed composition, water-binder ratio variation, specimen dimension, compressive strength and elasticity modulus of the specimen. The test results show that the concrete compressive strength achieves value between 25 MPa to 55 MPa. The mix design method that has developed can simplify the process of concrete mix design using PPC to achieve the certain desired performance of concrete.

Physical and mechanical properties of self-compacting concrete containing superplasticizer and metakaolin

NASA Astrophysics Data System (ADS)

Shahidan, Shahiron; Tayeh, Bassam A.; Jamaludin, A. A.; Bahari, N. A. A. S.; Mohd, S. S.; Zuki Ali, N.; Khalid, F. S.

2017-11-01

The development of concrete technology shows a variety of admixtures in concrete to produce special concrete. This includes the production of self-compacting concrete which is able to fill up all spaces, take formwork shapes and pass through congested reinforcement bars without vibrating or needing any external energy. In this study, the main objective is to compare the physical and mechanical properties of self-compacting concrete containing metakaolin with normal concrete. Four types of samples were produced to study the effect of metakaolin towards the physical and mechanical properties of self-compacting concrete where 0%, 5%, 10% and 15% of metakaolin were used as cement replacement. The physical properties were investigated using slump test for normal concrete and slump flow test for self-compacting concrete. The mechanical properties were tested for compressive strength and tensile strength. The findings of this study show that the inclusion of metakaolin as cement replacement can increase both compressive and tensile strength compared to normal concrete. The highest compressive strength was found in self-compacting concrete with 15% metakaolin replacement at 53.3 MPa while self-compacting concrete with 10% metakaolin replacement showed the highest tensile strength at 3.6 MPa. On top of that, the finishing or concrete surface of both cube and cylinder samples made of self-compacting concrete produced a smooth surface with the appearance of less honeycombs compared to normal concrete.

Toxicity and environmental and economic performance of fly ash and recycled concrete aggregates use in concrete: A review.

PubMed

Kurda, Rawaz; Silvestre, José D; de Brito, Jorge

2018-04-01

This paper presents an overview of previous studies on the environmental impact (EI) and toxicity of producing recycled concrete aggregates (RCA), fly ash (FA), cement, superplasticizer, and water as raw materials, and also on the effect of replacing cement and natural aggregates (NA) with FA and RCA, respectively, on the mentioned aspects. EI and toxicity were analysed simultaneously because considering concrete with alternative materials as sustainable depends on whether their risk assessment is high. Therefore, this study mainly focuses on the cradle-to-gate EI of one cubic meter of concrete, namely abiotic depletion potential (ADP), global warming potential (GWP), ozone depletion potential (ODP), photochemical ozone creation (POCP), acidification potential (AP), eutrophication potential (EP), non-renewable energy (PE-NRe) and renewable energy (PE-Re). In terms of toxicity, leachability (chemical and ecotoxicological characterization) was considered. The results also include the economic performance of these materials, and show that the incorporation of FA in concrete significantly decreases the EI and cost of concrete. Thus, the simultaneous incorporation of FA and RCA decrease the EI, cost, use of landfill space and natural resources extraction. Nonetheless, the leaching metals of FA decrease when they are incorporated in concrete. Relative to FA, the incorporation of RCA does not significantly affect the EI and cost of concrete, but it significantly reduces the use of landfill space and the need of virgin materials.

Performance Using Bamboo Fiber Ash Concrete as Admixture Adding Superplasticizer

NASA Astrophysics Data System (ADS)

Vasudevan, Gunalaan

2017-06-01

The increasing demand on natural resources for housing provisions in developing countries have called for sourcing and use of sustainable local materials for building and housing delivery. Natural materials to be considered sustainable for building construction should be ‘green’ and obtained from local sources, including rapidly renewable plant materials like palm fronds and bamboo, recycled materials and other products that are reusable and renewable. Each year, tens of millions of tons of bamboo are utilized commercially, generating a vast amount of waste. Besides that, bamboo fiber is easy availability, low density, low production cost and satisfactory mechanical properties. One solution is to activate this waste by using it as an additive admixture in concrete to keep it out of landfills and save money on waste disposal. The research investigates the mechanical and physical properties of bamboo fiber powder in a blended Portland cement. The structural value of the bamboo fiber powder in a blended Portland cement was evaluated with consideration for its suitability in concrete. Varied percentage of bamboo fiber powder (BFP) at 0%, 5%, 10%, 15%, and 20% as an admixture in 1:2:4 concrete mixes. The workability of the mix was determined through slump; standard consistency test was carried on the cement. Compressive strength of hardened cured (150 x 150 x 150) mm concrete cubes at 7days, 14days and 28days were tested.

Modelling the minislump spread of superplasticized PPC paste using RLS with the application of Random Kitchen sink

NASA Astrophysics Data System (ADS)

Sathyan, Dhanya; Anand, K. B.; Jose, Chinnu; Aravind, N. R.

2018-02-01

Super plasticizers(SPs) are added to the concrete to improve its workability with out changing the water cement ratio. Property of fresh concrete is mainly governed by the cement paste which depends on the dispersion of cement particle. Cement dispersive properties of the SP depends up on its dosage and the family. Mini slump spread diameter with different dosages and families of SP is taken as the measure of workability characteristic of cement paste chosen for measuring the rheological properties of cement paste. The main purpose of this study includes measure the dispersive ability of different families of SP by conducting minislump test and model the minislump spread diameter of the super plasticized Portland Pozzolona Cement (PPC)paste using regularized least square (RLS) approach along with the application of Random kitchen sink (RKS) algorithm. For preparing test and training data for the model 287 different mixes were prepared in the laboratory at a water cement ratio of 0.37 using four locally available brand of Portland Pozzolona cement (PPC) and SP belonging to four different families. Water content, cement weight and amount of SP (by considering it as seven separate input based on their family and brand) were the input parameters and mini slump spread diameter was the output parameter for the model. The variation of predicted and measured values of spread diameters were compared and validated. From this study it was observed that, the model could effectively predict the minislump spread of cement paste

Influences of Steelmaking Slags on Hydration and Hardening of Concretes

NASA Astrophysics Data System (ADS)

Kirsanova, A. A.; Dildin, A. N.; Maksimov, S. P.

2017-11-01

It is shown that the slag of metallurgical production can be used in the construction industry as an active mineral additive for concrete. This approach allows us to solve environmental problems and reduce costs for the production of binder and concrete simultaneously. Most often slag is used in the form of a filler, an active mineral additive or as a part of a binder for artificial conglomerates. The introduction of slag allows one to notice a part of the cement, to obtain concretes that are more resistant to the impact of aggressive sulfate media. The paper shows the possibility of using recycled steel-smelting slags in the construction industry for the production of cement. An assessment was made of their effect on the hydration of the cement stone and hardening of the concrete together with the plasticizer under normal conditions. In the process of work, we used the slag of the Zlatoust Electrometallurgical Factory. Possible limitations of the content of steel-slag slag in concrete because of the possible presence of harmful impurities are shown. It is necessary to enter slag in conjunction with superplasticizers to reduce the flow of water mixing. Slags can be used as a hardening accelerator for cement concrete as they allow one to increase the degree of cement hydration and concrete strength. It is shown that slags can be used to produce fast-hardening concretes and their comparative characteristics with other active mineral additives are given.

Experimental Study On Flexural Behaviour Of Beams Reinforced With GFRP Rebars

NASA Astrophysics Data System (ADS)

Naveen Kumar, G.; Sundaravadivelu, Karthik

2017-07-01

In saline, moisture and cold conditions corrosion of steel is inevitable and the lot of economy is used for rehabilitation works. Corrosion of steel is nothing but oxidation of iron in moisture conditions and this corrosion leads to the spalling of concrete which intern reduces the strength of the structure. To reduce this corrosion effects, new materials with resistance against corrosion have to be introduced. Many experiments are going on using Glass Fiber Reinforced Polymer (GFRP) as alternate material for steel due to its non-corrosive nature, weight of GFRP is nearly one third of steel and ultimate tensile strength is higher than steel. In this paper, six beams are casted in which three beams are casted with steel as main and shear reinforcement and another three beams are casted with GFRP as main reinforcement with steel as shear reinforcing material. All beams casted are of same dimensions with variation in reinforcement percentage. The size of the beams casted is of length 1200 mm, breadth 100 mm and depth 200 mm. The clear cover of 25 mm is provided on top and bottom of the beam. Beams are tested under two-point loading with constant aspect ratio (a/d) and comparing the flexural strength, load deflection curves and types of failures of beams reinforced with GFRP as main reinforcement and beams reinforced with conventional steel. The final experimental results are compared with numerical results. M30 grade concrete with Conplast as a superplasticizer is used for casting beams.

The effectiveness of stone ash and volcanic ash of mount Sinabung as a filler on the initial strength of self-compacting concrete

NASA Astrophysics Data System (ADS)

Karolina, R.; Muhammad, W.; Saragih, M. D. S. M.; Mustaqa, T.

2018-02-01

Self Compacting Concrete is a concrete variant that has a high degree of workability and also has great initial strength, but low water cement factor. It is also self-flowable that can be molded on formwork with a very little or no compacted use of compactors. This concrete, using a variety of aggregate sizes, aggregate portions and superplasticizer admixture to achieve a special viscosity that allows it to flow on its own without the aid of a compactor. Lightweight concrete brick is a type of brick made from cement, sand, water, and developers. Lightweight concrete bricks are divided into 2 based on the developed materials used are AAC (Autoclave Aerated Concrete) using aluminum paste and CLC (Cellular Lightweight Concrete) that use Foaming Agent from BASF as a developer material. In this experiment, the lightweight bricks that will be made are CLC type which uses Foaming Agent as the developer material by mixing the Ash Stone produced by Stone Crusher machine which has the density of 2666 kg / m3 as Partial Pair Substitution. In this study the variation of Ash Stone used is 10%, 15%, and 20% of the planned amount of sand. After doing the tasting the result is obtained for 10% variation. Compressive Strength and Absorption Increase will decrease by 25.07% and 39.005% and Variation of 15% compressive strength will decrease by 65,8% and decrease of absorbtion equal to 17,441% and variation of 20% compressive strength will decreased by 67,4 and absorption increase equal to 17,956%.

The optimization of concrete mixtures for use in highway applications

NASA Astrophysics Data System (ADS)

Moini, Mohamadreza

Portland cement concrete is most used commodity in the world after water. Major part of civil and transportation infrastructure including bridges, roadway pavements, dams, and buildings is made of concrete. In addition to this, concrete durability is often of major concerns. In 2013 American Society of Civil Engineers (ASCE) estimated that an annual investment of 170 billion on roads and 20.5 billion for bridges is needed on an annual basis to substantially improve the condition of infrastructure. Same article reports that one-third of America's major roads are in poor or mediocre condition [1]. However, portland cement production is recognized with approximately one cubic meter of carbon dioxide emission. Indeed, the proper and systematic design of concrete mixtures for highway applications is essential as concrete pavements represent up to 60% of interstate highway systems with heavier traffic loads. Combined principles of material science and engineering can provide adequate methods and tools to facilitate the concrete design and improve the existing specifications. In the same manner, the durability must be addressed in the design and enhancement of long-term performance. Concrete used for highway pavement applications has low cement content and can be placed at low slump. However, further reduction of cement content (e.g., versus current specifications of Wisconsin Department of Transportation to 315-338 kg/m 3 (530-570 lb/yd3) for mainstream concrete pavements and 335 kg/m3 (565 lb/yd3) for bridge substructure and superstructures) requires delicate design of the mixture to maintain the expected workability, overall performance, and long-term durability in the field. The design includes, but not limited to optimization of aggregates, supplementary cementitious materials (SCMs), chemical and air-entraining admixtures. This research investigated various theoretical and experimental methods of aggregate optimization applicable for the reduction of cement content. Conducted research enabled further reduction of cement contents to 250 kg/m3 (420 lb/yd3) as required for the design of sustainable concrete pavements. This research demonstrated that aggregate packing can be used in multiple ways as a tool to optimize the aggregates assemblies and achieve the optimal particle size distribution of aggregate blends. The SCMs, and air-entraining admixtures were selected to comply with existing WisDOT performance requirements and chemical admixtures were selected using the separate optimization study excluded from this thesis. The performance of different concrete mixtures was evaluated for fresh properties, strength development, and compressive and flexural strength ranging from 1 to 360 days. The methods and tools discussed in this research are applicable, but not limited to concrete pavement applications. The current concrete proportioning standards such as ACI 211 or current WisDOT roadway standard specifications (Part 5: Structures, Section 501: Concrete) for concrete have limited or no recommendations, methods or guidelines on aggregate optimization, the use of ternary aggregate blends (e.g., such as those used in asphalt industry), the optimization of SCMs (e.g., class F and C fly ash, slag, metakaolin, silica fume), modern superplasticizers (such as polycarboxylate ether, PCE) and air-entraining admixtures. This research has demonstrated that the optimization of concrete mixture proportions can be achieved by the use and proper selection of optimal aggregate blends and result in 12% to 35% reduction of cement content and also more than 50% enhancement of performance. To prove the proposed concrete proportioning method the following steps were performed: • The experimental aggregate packing was investigated using northern and southern source of aggregates from Wisconsin; • The theoretical aggregate packing models were utilized and results were compared with experiments; • Multiple aggregate optimization methods (e.g., optimal grading, coarseness chart) were studied and compared to aggregate packing results and performance of experimented concrete mixtures; • Optimal aggregate blends were selected and used for concrete mixtures; • The optimal dosage of admixtures were selected for three types of plasticizing and superplasticizing admixtures based on a separately conducted study; • The SCM dosages were selected based on current WisDOT specifications; • The optimal air-entraining admixture dosage was investigated based on performance of preliminary concrete mixtures; • Finally, optimal concrete mixtures were tested for fresh properties, compressive strength development, modulus of rupture, at early ages (1day) and ultimate ages (360 days). • Durability performance indicators for optimal concrete mixtures were also tested for resistance of concrete to rapid chloride permeability (RCP) at 30 days and 90 days and resistance to rapid freezing and thawing at 56 days.

Usage of Crushed Concrete Fines in Decorative Concrete

NASA Astrophysics Data System (ADS)

Pilipenko, Anton; Bazhenova, Sofia

2017-10-01

The article is devoted to the questions of usage of crushed concrete fines from concrete scrap for the production of high-quality decorative composite materials based on mixed binder. The main problem in the application of crushed concrete in the manufacture of decorative concrete products is extremely low decorative properties of crushed concrete fines itself, as well as concrete products based on them. However, crushed concrete fines could have a positive impact on the structure of the concrete matrix and could improve the environmental and economic characteristics of the concrete products. Dust fraction of crushed concrete fines contains non-hydrated cement grains, which can be opened in screening process due to the low strength of the contact zone between the hydrated and non-hydrated cement. In addition, the screening process could increase activity of the crushed concrete fines, so it can be used as a fine aggregate and filler for concrete mixes. Previous studies have shown that the effect of the usage of the crushed concrete fines is small and does not allow to obtain concrete products with high strength. However, it is possible to improve the efficiency of the crushed concrete fines as a filler due to the complex of measures prior to mixing. Such measures may include a preliminary mechanochemical activation of the binder (cement binder, iron oxide pigment, silica fume and crushed concrete fines), as well as the usage of polycarboxylate superplasticizers. The development of specific surface area of activated crushed concrete fines ensures strong adhesion between grains of binder and filler during the formation of cement stone matrix. The particle size distribution of the crushed concrete fines could achieve the densest structure of cement stone matrix and improve its resistance to environmental effects. The authors examined the mechanisms of structure of concrete products with crushed concrete fines as a filler. The results of studies of the properties of the crushed concrete fines were provided. It is shown that the admixture of the crushed concrete fines has little effect on the colour characteristics of the decorative concrete products. The preferred options to improve the surfaces of decorative concrete are also proposed.

Experimental study of self-compacted concrete in hardened state

NASA Astrophysics Data System (ADS)

Parra Costa, Carlos Jose

The main aim of this work is to investigate the hardened behaviour of Self-Compacting Concrete (SCC). Self compacting Concrete is a special concrete that can flow in its gravity and fill in the formwork alone to its self-weight, passing through the bars and congested sections without the need of any internal or external vibration, while maintaining adequate homogeneity. SCC avoids most of the materials defects due to bleeding or segregation. With regard to its composition, SCC consists of the same components as traditional vibrated concrete (TC), but in different proportions. Thus, the high amount of superplasticizer and high powder content have to taken into account. The high workability of SCC does not allow to use traditional methods for measuring the fresh state properties, so new tests has developed (slump-flow, V-funnel, L-box, and others). The properties of the hardened SCC, which depend on the mix design, should be different from traditional concrete. In order to study the possible modifications of SCC hardened state properties, a review of the bibliography was done. The state of art was focused on the mechanical behaviour (compressive strength, tension strength and elastic modulus), on bond strength of reinforcement steel, and on material durability. The experimental program consisted in the production of two types of concretes: Self-Compacting Concrete and Traditional Concrete. Four different dosages was made with three different water/cement ratio and two strength types of Portland cement, in order to cover the ordinary strength used in construction. Based on this study it can be concluded that compressive strength of SCC and TC are similar (the differences are lesser than 10%), whereas the tensile strength of TC are up to 18% higher. The values of elastic modulus of both concrete are similar. On the other hand, in the ultimate state the bond strength of SCC and TC is similar, although SCC shows higher bond stiffness in the serviceability state (initial displacement). Thus SCC reaches higher average bond strength. Although the variation in bond strength at different elevations, due to top-bar effect, is also observed in SCC the extent is less significant than that of TC. Finally, tests show that water depth penetration under pressure is much lower for SCC than for TC.

Compatibilite deformationnelle des betons autoplacants pour des utilisations dans les reparations des infrastructures routieres

NASA Astrophysics Data System (ADS)

Ghezal, Aicha Fadela

Concrete structures repairs in Civil Engineering by using a thin bonded overlay is common practice. However the repaired structures are often victim of premature deterioration of the new repair material due to the appearance of restrained shrinkage cracks. In this context, the main objective of this thesis is to identify, through the experimental program called Phase I the principal parameters that significantly influence the creep potential of the evaluated mixtures. Once these parameters identified, the experimental entitled Phase II is conducted under conditions simulating repairs, and emphasis was placed on restrained shrinkage using instrumented ring test. Article 1 summarized the laboratory investigation undertaken to evaluate the potential of flexural creep behavior of several SCC. The results show clearly that the flexural creep potential of SCC varies widely depending on the nature of HRWR in use. In general, the use of naphthalene sulfonate leads to higher creep by comparison to polycarboxylate. It has been shown also that even when belonging to the same A.S.T.M. classification (polycarboxylic family) the magnitude of flexural creep varies also widely depending on the properties of polycarboxylic chemicals admixture. Based on the identified parameters in phase I, namely PNS superplasticizers type and PC2, with two ternary blended cements with fly ash (BTCFA) and slag (BTCS), the second experimental program was undertaken and summarized in articles 2 and 3. As presented in article 2, the results indicate that optimized SCCs produced with blended ternary cement with fly ash (BTCFA) developed at earlier age lower compressive and splitting-tensile strengths than the corresponding SCCs with blended cement with slag (BTCS). Test results also indicated that the drying shrinkage of SCCs based on BTCFA is higher than the corresponding SCCs proportioned with BTCS and attributed in part to higher total pores volume measured at 120 days on SCC BTCFA. The restrained shrinkage of SCC summarized in article 3 show that the resistance of SCC to shrinkage cracks was quite different depending on the nature of HRWR and the binder type in use. The cracking age increases in mixtures proportioned with PC-HRWR comparatively to PNS-HRWR. The SCC mixtures based on blended ternary cement containing Class F fly ash show shorter cracking age than the corresponding SCCs proportioned with ternary blended cement containing slag. Moreover, a data analysis of current research shows that the ratio of tensile strength to free shrinkage and modulus of elasticity, referred as index of dimensional compatibility, is a promising assessment of cracking resistant performance. In this way, only the free shrinkage test (ASTM C157) and basic mechanical properties are required to assess cracking of candidate concrete mixture designs.

Ceramic Near-Net Shaped Processing Using Highly-Loaded Aqueous Suspensions

NASA Astrophysics Data System (ADS)

Rueschhoff, Lisa

Ceramic materials offer great advantages over their metal counterparts, due to their lower density, higher hardness and wear resistance, and higher melting temperatures. However, the use of ceramics in applications where their properties would offer tremendous advantages are often limited due to the difficulty of forming them into complex and near-net shaped parts. Methods that have been developed to injection-mold or cast ceramics into more complicated shapes often use significant volume fractions of a carrier (often greater than 35 vol.% polymer), elevated temperature processing, or less-than-environmentally friendly chemicals where a complex chemical synthesis reaction must be timed perfectly for the approach to work. Furthermore, the continuing maturation of additive manufacturing methods requires a new approach for flowing/placing ceramic powders into useful designs. This thesis addresses the limitations of the current ceramic forming approaches by developing highly-stabilized and therefore high solids loading ceramic suspensions, with the requisite rheology for a variety of complex and near-net shaped forming techniques. Silicon nitride was chosen as a material of focus due to its high fracture toughness compared to other ceramic materials. Designing ceramic suspensions that are flowable at room temperature greatly simplifies processing as neither heating nor cooling are required during forming. Highly-loaded suspensions (>40 vol.%) are desired because all formed ceramic bodies have to be sintered to remove pores. Finally, using aqueous-based suspensions reduces any detrimental effect on the environment and tooling. The preparation of highly-loaded suspensions requires the development of a suitable dispersant through which particle-particle interactions are controlled. However, silicon nitride is difficult to stabilize in water due to complex surface and solution chemistry. In this study, aqueous silicon nitride suspensions up to 45 vol.% solids loading were dispersed using commercially available comb-type copolymer. These copolymers are used as superplasticizers in the concrete industry and are referred to as water-reducing admixtures (WRAs). Four different WRA dispersants were examined and chemical analysis determined that each was made up of a sodium salt of polyacrylic acid (PAA-Na) backbone with neutral polyethylene oxide (PEO) side chains that afford steric stabilization. The general structures of the WRAs were compared to each other by measuring the relative areas of their prominent FTIR peaks and calculating a PAA-Na/PEO peak ratio. Suspensions were made with as-received silicon nitride powders with 5 wt.% aluminum oxide and 5 wt.% yttrium oxide added as sintering aids. Three of the four WRA dispersants studied were able to produce suspensions with 43 vol.% solids loading and 5 vol.% polymer dispersant, while exhibiting a yield-pseudoplastic behavior for shear rates up to 30 s-1. At higher solids loading (45 to 47 vol.%), a shift to shear thickening behavior was observed at a critical shear rate for these WRAs. Those WRAs with a lower PAA-Na/PEO peak ratio displayed better stabilization and diminished shear thickening behavior. The vol.% of the dispersant was optimized, producing yield-pseudoplastic suspensions containing 45 vol.% solids loading with yield stresses less than 75 Pa, no shear thickening behavior, and viscosities less than 75 Pa-s for shear rates in the range of 1 to 30 s-1. Using suspensions prepared with two of the WRAs investigated in this work, silicon nitride near-net shaped parts were formed via a novel injection molding process by loading each suspension in a syringe and injecting them at a controlled rate into a mold. Each suspensions had carefully tailored yield-pseudoplastic rheology such that they can be injection molded at room temperature and low pressures (< 150 kPa). Four suspensions were studied; two different commercially available concrete water-reducing admixtures (WRAs) were used as dispersants with and without a polymer binder (Polyvinylprolidone, PVP) added for rheological modification and improved green body strength. Test bars formed via this process were sintered to high densities (up to 97% TD) without the use of external pressure, and had complete conversion to the desirable beta-Si3N4 phase with high flexural strengths up to 700 MPa. The specimen sets with the smallest average pore size on the fracture surface (77 mum) had the highest average flexural strengths of 573 MPa. The hardness of all specimens was approximately 16 GPa. The water-based suspensions, ease and low cost of processing, and robust mechanical properties obtained demonstrate this as a viable process for the economical and environmentally friendly production of Si3N4 parts. Finally, additive manufacturing was also used as a method to overcome ceramic forming difficulties and to create near-net shaped dense components via room-temperature direct ink writing. In this processes, highly loaded aqueous alumina suspensions were extruded in a layer-by-layer fashion using a low-cost syringe style 3D printer. With alumina as a model material, the effect of solids loading on rheology, specimen uniformity, density, microstructure, and mechanical properties was studied. All suspensions contained a polymer binder ( 5 vol.%), dispersant, and 51 to 58 vol.% alumina powder. Rheological measurements indicated all suspensions to be yield-pseudoplastic, and both yield stress and viscosity were found to increase with increasing alumina solids loading. Shear rates ranging from 19.5 to 24.2 s-1, corresponding to viscosities of 9.8 to 17.2 Pa·s, for the 53 - 56 vol.% alumina suspensions were found to produce the best results for the 1.25 mm tip employed during writing. All parts were sintered to greater than 98% of true density, with grain sizes ranging from 3.2 to 3.7 mum. The average flexure strength, which ranged from 134 to 157 MPa, was not influenced by the alumina solids loading. In limited study, additive manufacturing of silicon nitride suspensions stabilized with a WRA has been established. These processing routes have been proven as low-cost and viable means for producing robust ceramic parts, both of which can be tailored to many systems to expand the use of ceramics materials. Further studies on utilizing the flow stress behavior during both injection molding and direct ink writing could be beneficial in creating ceramic materials with carefully tailored microstructure to increase mechanical performance.

PREFACE: Dynamic crossover phenomena in water and other glass-forming liquids Dynamic crossover phenomena in water and other glass-forming liquids

NASA Astrophysics Data System (ADS)

Chen, Sow-Hsin; Baglioni, Piero

2012-02-01

This special section has been inspired by the workshop on Dynamic Crossover Phenomena in Water and Other Glass-Forming Liquids, held during November 11-13, 2010 at Pensione Bencistà, Fiesole, Italy, a well-preserved 14th century Italian villa tucked high in the hills overlooking Florence. The meeting, an assembly of world renowned scientists, was organized as a special occasion to celebrate the 75th birthday of Professor Sow-Hsin Chen of MIT, a pioneer in several aspects of complex fluids and soft matter physics. The workshop covered a large variety of experimental and theoretical research topics of current interest related to dynamic crossover phenomena in water and, more generally, in other glass-forming liquids. The 30 invited speakers/lecturers and approximately 60 participants were a select group of prominent physicists and chemists from the USA, Europe, Asia and Mexico, who are actively working in the field. Some highlights of this special issue include the following works. Professor Yamaguchi's group and their collaborators present a neutron spin echo study of the coherent intermediate scattering function of heavy water confined in cylindrical pores of MCM-41-C10 silica material in the temperature range 190-298 K. They clearly show that a fragile-to-strong (FTS) dynamic crossover occurs at about 225 K. They attribute the FTS dynamic crossover to the formation of a tetrahedral-like structure, which is preserved in the bulk-like water confined to the central part of the cylindrical pores. Mamontov and Kolesnikov et al study the collective excitations in an aqueous solution of lithium chloride over a temperature range of 205-270 K using neutron and x-ray Rayleigh-Brillouin (coherent) scattering. They detect both the low-frequency and the high-frequency sounds known to exist in pure bulk water above the melting temperature. They also perform neutron (incoherent) and x-ray (coherent) elastic intensity scan measurements. Clear evidence of the crossover in the dynamics of the water molecules in the solution is observed in the single-particle relaxational dynamics in the μeV (nanosecond) time scale, but not in the collective dynamics on the meV (picosecond) time scale. Mallamace et al discuss the dynamic crossover phenomenon in both bulk water and protein hydration water. They collect previous and new experimental data from different experimental techniques and molecular dynamic simulations, and are able to develop a unified picture for the different dynamical findings. Gallo et al present a MD study of confined water in MCM-41S-15 in order to test the applicability of Mode Coupling Theory (MCT) to the dynamics of the hydration water confined in the cylindrical pores of nominal diameter 15 Å. They find that the self dynamics of the hydration water is well described by MCT down to the crossover temperature TC. However, below TC the predictions of idealized MCT no longer apply, since hopping processes intervene and water turns into a strong liquid. Soper raises some questions as to the validity of the analysis method employed to determine the density of water confined in porous silica material MCM-41-S15 from recent neutron scattering experiments. Professors Stanley, Franzese and his collaborators describe an efficient Monte Carlo simulation of a coarse-grained model of water to study the phase diagram of a water monolayer confined in a fixed disordered matrix of hydrophobic nanoparticles between two hydrophobic plates. They find a drastic change of phase behavior of the confined water, such as shortening of the liquid-liquid phase transition line, upon increasing the concentration of the hydrophobic nano-particles. Sciortino and collaborators compute the equilibrium phase diagram of two simple models for patchy particles with three and five patches in a very broad range of pressure and temperature. The three-patch model produces a stable gas-liquid critical point. Yun Liu et al investigate, via small angle neutron scattering and neutron spin echo measurements, the effect of temperature on dynamic cluster formation of concentrated lysozyme solutions. Xin Li et al explore the use of the newly developed technique of spin echo small angle neutron scattering (SESANS) to investigate the structure of a colloid. They find the SESANS is able to resolve structural heterogeneity, at both intra- and inter-colloidal length scales. The choice of the topics and their elaboration reflects both the diversified current and past research interests of Professor Chen to whom this special section of Journal of Physics: Condensed Matter is dedicated. The issue contains papers from a substantial number of the invited speakers. The papers are arranged in the three categories of water, other glass-forming liquids, and colloids. It is our pleasure to thank all speakers, section chairs and participants who contributed to the great success of the workshop, and to all authors for their additional efforts in preparing their manuscripts. The scientific program of the workshop was organized by Professor Sow-Hsin Chen and Professor Piero Baglioni. The meeting was only possible with the generous financial support of the Consorzio per lo Sviluppo dei Sistemi a Grande Interfase (CSGI) and the University of Florence, Italy. Finally, we express our warmest gratitude to all the members of the local organizing committee and to the staff of the CSGI for all their assistance and great efforts in organizing this meeting. Dynamic crossover phenomena in water and other glass-forming liquids contents Water Neutron spin echo measurements of monolayer and capillary condensed water in MCM-41 at low temperaturesK Yoshida, T Yamaguchi, S Kittaka, M-C Bellissent-Funel and P Fouquet Water dynamics in a lithium chloride aqueous solution probed by Brillouin neutron and x-ray scatteringE Mamontov, A De Francesco, F Formisano, A Laloni, L Sani, B M Leu, A H Said and A I Kolesnikov The dynamical crossover phenomenon in bulk water, confined water and protein hydration water Francesco Mallamace, Carmelo Corsaro, Piero Baglioni, Emiliano Fratini and Sow-Hsin Chen Common features in the microscopic dynamics of hydration water on organic and inorganic surfacesE Mamontov, H O'Neill, Q Zhang, W Wang and D J Wesolowski Water dynamics as affected by interaction with biomolecules and change of thermodynamic state: a neutron scattering studyA Orecchini, A Paciaroni, C Petrillo, F Sebastiani, A De Francesco and F Sacchetti Temperature dependence of structure and density for D2O confined in MCM-41-SWilliam A Kamitakahara, Antonio Faraone, Kao-Hsiang Liu and Chung-Yuan Mou Density profile of water confined in cylindrical pores in MCM-41 silicaAlan K Soper Dynamic crossover in hydration water of curing cement paste: the effect of superplasticizerHua Li, Wei-Shan Chiang, Emiliano Fratini, Francesca Ridi, Francesco Bausi, Piero Baglioni, Madhu Tyagi and Sow-Hsin Chen Water confined in MCM-41: a mode coupling theory analysisP Gallo, M Rovere and S-H Chen Computer simulations of dynamic crossover phenomena in nanoconfined waterG B Suffritti, P Demontis, J Gulín-Gonźlez and M Masia Hydrophobic nanoconfinement suppresses fluctuations in supercooled waterE G Strekalova, M G Mazza, H E Stanley and G Franzese Other glass-forming liquids Quasi-elastic neutron scattering studies of the slow dynamics of supercooled and glassy aspirinYang Zhang, Madhusudan Tyagi, Eugene Mamontov and Sow-Hsin Chen Colloids Phase diagram of trivalent and pentavalent patchy particlesFlavio Romano, Eduardo Sanz, Piero Tartaglia and Francesco Sciortino Distinguishing the monomer to cluster phase transition in concentrated lysozyme solutions by studying the temperature dependence of the short-time dynamicsPéter Falus, Lionel Porcar, Emiliano Fratini, Wei-Ren Chen, Antonio Faraone, Kunlun Hong, Piero Baglioni and Yun Liu Contrast variation in spin-echo small angle neutron scatteringXin Li, Bin Wu, Yun Liu, Roger Pynn, Chwen-Yang Shew, Gregory S Smith, Kenneth W Herwig, J Lee Robertson, Wei-Ren Chen and Li Liu Structural response of polyelectrolyte dendrimer towards molecular protonation: the inconsistency revealed by SANS and NMRKunlun Hong, Yun Liu, Lionel Porcar, Dazhi Liu, Carrie Y Gao, Gregory S Smith, Kenneth W Herwig, Sheng Cai, Xin Li, Bin Wu, Wei-Ren Chen and Li Liu