Enhancing the Stiffness of Electrospun Nanofiber Scaffolds with Controlled Surface Coating and Mineralization

PubMed Central

Liu, Wenying; Yeh, Yi-Chun; Lipner, Justin; Xie, Jingwei; Sung, Hsing-Wen; Thomopoulos, Stavros; Xia, Younan

2011-01-01

A new method was developed to coat hydroxyapatite (HAp) onto electrospun poly(lactic-co-glycolic acid) (PLGA) nanofibers for tendon-to-bone insertion site repair applications. Prior to mineralization, chitosan and heparin were covalently immobilized onto the surface of the fibers to accelerate the nucleation of bone-like HAp crystals. Uniform coatings of HAp were obtained by immersing the nanofiber scaffolds into a modified 10 times concentrated simulated body fluid (m10SBF) for different periods of time. The new method resulted in thicker and denser coatings of mineral on the fibers compared to previously reported methods. Scanning electron microscopy measurements confirmed the formation of nanoscale HAp particles on the fibers. Mechanical property assessment demonstrated higher stiffness with respect to previous coating methods. A combination of the nanoscale fibrous structure and bone-like mineral coating could mimic the structure, composition, and function of mineralized tissues. PMID:21710996

Effect of silver-doping on the crystal structure, morphology and photocatalytic activity of TiO2 nanofibers

NASA Astrophysics Data System (ADS)

Barakat, N. A. M.; Kim, H. Y.

2012-09-01

In this study, effect of sliver-doping on the crystal structure, the nanofibrous morphology and the photocatalytic activity of titanium oxide nanofibers have been investigated. Silver-doped TiO2 nanofibers having different silver contents were prepared by calcination of electrospun nanofiber mats consisting of silver nitrate, titanium isopropoxide and poly(vinyl acetate) at 600 °C. The results affirmed formation of silver-doped TiO2 nanofibers composed of anatase and rutile when the silver nitrate content in the original electrospun solution was more than 3 wt%. The rutile phase content was directly proportional with the AgNO3 concentration in the electrospun solution. Negative impact of the silver-doping on the nanofibrous morphology was observed as increase the silver content caused to decrease the aspect ratio, i.e. producing nanorods rather nanofibers. However, silver-doping leads to modify the surface roughness. Study of the photocatalytic degradation of methylene blue dye clarified that increase the silver content strongly enhances the dye oxidation process.

Coaxial Electrospinning and Characterization of Core-Shell Structured Cellulose Nanocrystal Reinforced PMMA/PAN Composite Fibers

PubMed Central

Li, Chao; Li, Qingde; Ni, Xiaohui; Liu, Guoxiang; Cheng, Wanli; Han, Guangping

2017-01-01

A modified coaxial electrospinning process was used to prepare composite nanofibrous mats from a poly(methyl methacrylate) (PMMA) solution with the addition of different cellulose nanocrystals (CNCs) as the sheath fluid and polyacrylonitrile (PAN) solution as the core fluid. This study investigated the conductivity of the as-spun solutions that increased significantly with increasing CNCs addition, which favors forming uniform fibers. This study discussed the effect of different CNCs addition on the morphology, thermal behavior, and the multilevel structure of the coaxial electrospun PMMA + CNCs/PAN composite nanofibers. A morphology analysis of the nanofibrous mats clearly demonstrated that the CNCs facilitated the production of the composite nanofibers with a core-shell structure. The diameter of the composite nanofibers decreased and the uniformity increased with increasing CNCs concentrations in the shell fluid. The composite nanofibrous mats had the maximum thermal decomposition temperature that was substantially higher than electrospun pure PMMA, PAN, as well as the core-shell PMMA/PAN nanocomposite. The BET (Brunauer, Emmett and Teller) formula results showed that the specific surface area of the CNCs reinforced core-shell composite significantly increased with increasing CNCs content. The specific surface area of the composite with 20% CNCs loading rose to 9.62 m2/g from 3.76 m2/g for the control. A dense porous structure was formed on the surface of the electrospun core-shell fibers. PMID:28772933

High-Throughput Fabrication of Quality Nanofibers Using a Modified Free Surface Electrospinning.

PubMed

Shao, Zhongbiao; Yu, Liang; Xu, Lan; Wang, Mingdi

2017-12-01

Based on bubble electrospinning (BE), a modified free surface electrospinning (MFSE) using a cone-shaped air nozzle combined with a solution reservoir made of copper tubes was presented to increase the production of quality nanofibers. In the MFSE process, sodium dodecyl benzene sulfonates (SDBS) were added in the electrospun solution to generate bubbles on a liquid surface. The effects of applied voltage and generated bubbles on the morphology and production of nanofibers were investigated experimentally and theoretically. The theoretical analysis results of the electric field were in good agreement with the experimental data and showed that the quality and production of nanofibers were improved with the increase of applied voltage, and the generated bubbles would decrease the quality and production of nanofibers.

High-Throughput Fabrication of Quality Nanofibers Using a Modified Free Surface Electrospinning

NASA Astrophysics Data System (ADS)

Shao, Zhongbiao; Yu, Liang; Xu, Lan; Wang, Mingdi

2017-07-01

Based on bubble electrospinning (BE), a modified free surface electrospinning (MFSE) using a cone-shaped air nozzle combined with a solution reservoir made of copper tubes was presented to increase the production of quality nanofibers. In the MFSE process, sodium dodecyl benzene sulfonates (SDBS) were added in the electrospun solution to generate bubbles on a liquid surface. The effects of applied voltage and generated bubbles on the morphology and production of nanofibers were investigated experimentally and theoretically. The theoretical analysis results of the electric field were in good agreement with the experimental data and showed that the quality and production of nanofibers were improved with the increase of applied voltage, and the generated bubbles would decrease the quality and production of nanofibers.

Biofunctionalization of PAMAM-montmorillonite decorated poly (Ɛ-caprolactone)-chitosan electrospun nanofibers for cell adhesion and electrochemical cytosensing.

PubMed

Kirbay, Fatma Ozturk; Yalcinkaya, Esra Evrim; Atik, Gozde; Evren, Gizem; Unal, Betul; Demirkol, Dilek Odaci; Timur, Suna

2018-06-30

The construction and biofunctionalization of the poly (Ɛ-caprolactone) (PCL)-chitosan (CHIT) nanofibrous mats, which included Polyamidoamine (PAMAM) dendrimer modified montmorillonite (Mt), for the cell adhesion and electrochemical cytosensing were accomplished in this report. After the intercalation of the PAMAM generation zero dendrimer into the Mt, PAMAM-Mt decorated PCL-CHIT electrospun nanofibers were formed. The addition of PAMAM caused the decrease of contact angle of PCL-CHIT nanofibers. The covalent immobilization of a tripeptide namely Arginylglycylaspartate (RGD) on both the PCL-CHIT/Mt and PCL-CHIT/PAMAM-Mt surface was carried out. U87-MG and HaCaT (negative control) cell lines were incubated on the PCL-CHIT/Mt/RGD and PCL-CHIT/PAMAM-Mt/RGD. The proliferation studies and imaging of the cells were carried out on these fibers. Finally, electrochemical measurements were performed after each modification step by differential pulse/cyclic voltammetry and electrochemical impedance spectroscopy. U87-MG cells were grown better than HaCaT cells on the PCL-CHIT/PAMAM-Mt/RGD surfaces. To the best of our knowledge, there is no study that developed electrochemical cytosensor using electrospun nanofibers as a cell adhesion platform. Copyright © 2018 Elsevier B.V. All rights reserved.

An electrospun nanofiber matrix based on organo-clay for biosensors: PVA/PAMAM-Montmorillonite

NASA Astrophysics Data System (ADS)

Unal, Betul; Yalcinkaya, Esra Evrim; Demirkol, Dilek Odaci; Timur, Suna

2018-06-01

Diagnostic techniques based on biomolecules have huge a potential to be applied in the application in various areas such as food/beverage industries, diseases diagnostics, monitoring of bio-processes and environmental pollutants. Immobilization of biomolecules on a transducer is the key parameter to being able to prepare a highly stable diagnostic tests. Electrospun nanofibers are a good alternative to immobilize biomolecules. Here, electrospun nanofibers based on an organoclay were used to design the first generation amperometric enzyme biosensor. PAMAM G2 dendrimers were used to intercalate montmorillonite clay (Mt) and then the modification of Mt by PAMAM was characterized using FTIR, XRD, TGA and zeta potential measurements. After that nanofibers were prepared by electrospinning Mt and PAMAM-Mt using poly(vinyl) alcohol (PVA) as an auxiliary polymer and the formed PVA/PAMAM-Mt electrospun nanofibers were proved by SEM, TEM and AFM techniques. Finally, pyranose oxidases (PyOx) were immobilized on a glassy carbon electrode surface, which was modified using the PVA/PAMAM-Mt electrospun nanofibers. Amperometric measurements were carried out using buffer solution at -0.7 V under stirring conditions. The linear response for glucose was from 0.005 mM to 0.25 mM using PVA/Mt/PyOx and PVA/PAMAM-Mt/PyOx biosensors. The limit of detection was 0.7 μM glucose with PVA/PAMAM-Mt/PyOx biosensor. To detect glucose in real sample, measurements were carried out using soft drink cola as a substrate instead of glucose.

Enhanced performance of immobilized laccase in electrospun fibrous membranes by carbon nanotubes modification and its application for bisphenol A removal from water.

PubMed

Dai, Yunrong; Yao, Jun; Song, Yonghui; Liu, Xiaoling; Wang, Siyu; Yuan, Yu

2016-11-05

Multi-walled carbon nanotubes (MWCNTs) were used as modified materials to improve the performance of laccase-carrying electrospun fibrous membranes (LCEFMs). The MWCNTs modified LCEFMs (MWCNTs-LCEFMs) were successfully fabricated via emulsion electrospinning, with active laccase and MWCNTs encapsulated inside the fibers. After modified by an optimal amount (1.5wt%, vs. polymer) of MWCNTs, the obtained MWCNTs-LCEFMs showed not only higher activity recovery (85.3%, vs. free laccase) than LCEFMs (71.2%), but also better storage and operational stability, which were mainly attributed to the promoted electron transfer in laccase-catalytic reaction. Furthermore, the specific surface area and tensile strength of MWCNTs-LCEFMs have also been enhanced nearly 2 and 3 times than those of LCEFMs, respectively. The MWCNTs-LCEFMs were applied to remove the widespread bisphenol A from water, where their removal efficiency reached above 90%, with the degradation efficiency accounting for over 80%, and their adsorption efficiency increased about 45% than that of LCEFMs. In addition, the endurances of MWCNTs-LCEFMs to environmental factors such as pH and temperature were also improved. Copyright © 2016 Elsevier B.V. All rights reserved.

Bacterial response to different surface chemistries fabricated by plasma polymerization on electrospun nanofibers.

PubMed

Abrigo, Martina; Kingshott, Peter; McArthur, Sally L

2015-12-06

Control over bacterial attachment and proliferation onto nanofibrous materials constitutes a major challenge for a variety of applications, including filtration membranes, protective clothing, wound dressings, and tissue engineering scaffolds. To develop effective devices, the interactions that occur between bacteria and nanofibers with different morphological and physicochemical properties need to be investigated. This paper explores the influence of fiber surface chemistry on bacterial behavior. Different chemical functionalities were generated on the surface of electrospun polystyrene nanofibers through plasma polymerization of four monomers (acrylic acid, allylamine, 1,7-octadiene, and 1,8-cineole). The interactions of Escherichia coli with the surface modified fibers were investigated through a combination of scanning electron microscopy and confocal laser scanning microscopy. Fiber wettability, surface charge, and chemistry were found to affect the ability of bacterial cells to attach and proliferate throughout the nanofiber meshes. The highest proportion of viable cells attachment occurred on the hydrophilic amine rich coating, followed by the hydrophobic octadiene. The acrylic acid coating rich in carboxyl groups showed a significantly lower attraction of bacterial cells. The 1,8-cineole retained the antibacterial activity of the monomer, resulting with a high proportion of dead isolated cells attached onto the fibers. Results showed that the surface chemistry properties of nanofibrous membranes can be strategically tuned to control bacterial behavior.

Characterization and in vitro evaluation of electrospun chitosan/polycaprolactone blend fibrous mat for skin tissue engineering.

PubMed

Prasad, Tilak; Shabeena, E A; Vinod, D; Kumary, T V; Anil Kumar, P R

2015-01-01

The electrospinning technique allows engineering biomimetic scaffolds within micro to nanoscale range mimicking natural extracellular matrix (ECM). Chitosan (CS) and polycaprolactone (PCL) were dissolved in a modified solvent mixture consisting of formic acid and acetone (3:7) and mixed in different weight ratios to get chitosan-polycaprolactone [CS-PCL] blend solutions. The CS-PCL blend polymer was electrospun in the same solvent system and compared with PCL. The physicochemical characterization of the electrospun fibrous mats was done using scanning electron microscopy (SEM), Fourier transform infrared spectroscopy (FTIR), tensile test, swelling properties, water contact angle (WCA) analysis, surface profilometry and thermo gravimetric analysis (TGA). The CS-PCL fibrous mat showed decreased hydrophobicity. The CS-PCL mats also showed improved swelling property, tensile strength, thermal stability and surface roughness. The cytocompatibility of the CS-PCL and PCL fibrous mats were examined using mouse fibroblast (L-929) cell line by direct contact and cellular activity with extract of materials confirmed non-cytotoxic nature. The potential of CS-PCL and PCL fibrous mats as skin tissue engineering scaffolds were assessed by cell adhesion, viability, proliferation and actin distribution using human keratinocytes (HaCaT) and L-929 cell lines. Results indicate that CS-PCL is a better scaffold for attachment and proliferation of keratinocytes and is a potential material for skin tissue engineering.

Mechanical properties and cellular response of novel electrospun nanofibers for ligament tissue engineering: Effects of orientation and geometry.

PubMed

Pauly, Hannah M; Kelly, Daniel J; Popat, Ketul C; Trujillo, Nathan A; Dunne, Nicholas J; McCarthy, Helen O; Haut Donahue, Tammy L

2016-08-01

Electrospun nanofibers are a promising material for ligamentous tissue engineering, however weak mechanical properties of fibers to date have limited their clinical usage. The goal of this work was to modify electrospun nanofibers to create a robust structure that mimics the complex hierarchy of native tendons and ligaments. The scaffolds that were fabricated in this study consisted of either random or aligned nanofibers in flat sheets or rolled nanofiber bundles that mimic the size scale of fascicle units in primarily tensile load bearing soft musculoskeletal tissues. Altering nanofiber orientation and geometry significantly affected mechanical properties; most notably aligned nanofiber sheets had the greatest modulus; 125% higher than that of random nanofiber sheets; and 45% higher than aligned nanofiber bundles. Modifying aligned nanofiber sheets to form aligned nanofiber bundles also resulted in approximately 107% higher yield stresses and 140% higher yield strains. The mechanical properties of aligned nanofiber bundles were in the range of the mechanical properties of the native ACL: modulus=158±32MPa, yield stress=57±23MPa and yield strain=0.38±0.08. Adipose derived stem cells cultured on all surfaces remained viable and proliferated extensively over a 7 day culture period and cells elongated on nanofiber bundles. The results of the study suggest that aligned nanofiber bundles may be useful for ligament and tendon tissue engineering based on their mechanical properties and ability to support cell adhesion, proliferation, and elongation. Copyright © 2016 Elsevier Ltd. All rights reserved.

Galactosylated electrospun membranes for hepatocyte sandwich culture.

PubMed

Chien, Hsiu-Wen; Lai, Juin-Yih; Tsai, Wei-Bor

2014-04-01

In this work, we developed a galactocylated electrospun polyurethane membrane for sandwich culture of hepatocyte sandwich culture. The electrospun fibrous membranes were bio-functionalized with galactose molecules by a UV-crosslinked layer-by-layer polyelectrolyte multilayer deposition technique. The galactosylated electrospun membranes were employed as a top support membrane for the sandwich culture of HepG2/C3A cells on a collagen substrate. Our results demonstrate that HepG2/C3A cells covered by the galactosylated PU membranes form multi-cellular aggregates and lead to improved albumin secretion ability compared to the control membranes (unmodified PU or poly(ethylene imine)-modified PU). Our study reveals the potential of galactosylated electrospun membranes in the application of liver tissue engineering and the regeneration of liver-tissue substitutes. Copyright © 2014 Elsevier B.V. All rights reserved.

Cell proliferation on PVA/sodium alginate and PVA/poly(γ-glutamic acid) electrospun fiber.

PubMed

Yang, Jen Ming; Yang, Jhe Hao; Tsou, Shu Chun; Ding, Chian Hua; Hsu, Chih Chin; Yang, Kai Chiang; Yang, Chun Chen; Chen, Ko Shao; Chen, Szi Wen; Wang, Jong Shyan

2016-09-01

To overcome the obstacles of easy dissolution of PVA nanofibers without crosslinking treatment and the poor electrospinnability of the PVA cross-linked nanofibers via electrospinning process, the PVA based electrospun hydrogel nanofibers are prepared with post-crosslinking method. To expect the electrospun hydrogel fibers might be a promising scaffold for cell culture and tissue engineering applications, the evaluation of cell proliferation on the post-crosslinking electrospun fibers is conducted in this study. At beginning, poly(vinyl alcohol) (PVA), PVA/sodium alginate (PVASA) and PVA/poly(γ-glutamic acid) (PVAPGA) electrospun fibers were prepared by electrospinning method. The electrospun PVA, PVASA and PVAPGA nanofibers were treated with post-cross-linking method with glutaraldehyde (Glu) as crosslinking agent. These electrospun fibers were characterized with thermogravimetry analysis (TGA) and their morphologies were observed with a scanning electron microscope (SEM). To support the evaluation and explanation of cell growth on the fiber, the study of 3T3 mouse fibroblast cell growth on the surface of pure PVA, SA, and PGA thin films is conducted. The proliferation of 3T3 on the electrospun fiber surface of PVA, PVASA, and PVAPGA was evaluated by seeding 3T3 fibroblast cells on these crosslinked electrospun fibers. The cell viability on electrospun fibers was conducted with water-soluble tetrazolium salt-1 assay (Cell Proliferation Reagent WST-1). The morphology of the cells on the fibers was also observed with SEM. The results of WST-1 assay revealed that 3T3 cells cultured on different electrospun fibers had similar viability, and the cell viability increased with time for all electrospun fibers. From the morphology of the cells on electrospun fibers, it is found that 3T3 cells attached on all electrospun fiber after 1day seeded. Cell-cell communication was noticed on day 3 for all electrospun fibers. Extracellular matrix (ECM) productions were found and cell-ECM adhesion was shown on day 7. The cell number was also increased on all of the crosslinked electrospun fibers. It seems that the PVA based electrospun hydrogel nanofibers prepared with post-crosslinking method can be used as scaffold for tissue engineering. Copyright © 2016 Elsevier B.V. All rights reserved.

Vascularization and Cellular Isolation Potential of a Novel Electrospun Cell Delivery Vehicle

PubMed Central

Krishnan, Laxminarayanan; Touroo, Jeremy; Reed, Robert; Boland, Eugene; Hoying, James B.; Williams, Stuart K.

2014-01-01

A clinical need exists for a cell delivery device that supports long term cell viability, cell retention within the device and retrieval of delivered cells if necessary. Previously, cell isolation devices have been based on hollow fiber membranes, porous polymer scaffolds, alginate systems, or micro-machined membranes. We present the development and characterization of a novel dual porosity electrospun membrane based device, which supports cellular infiltration and vascularization of its outer porous layer and maintains cellular isolation within a lumen bounded by an inner low porosity layer. Electrospinning conditions were initially established to support electrospun fiber deposition onto nonconductive silicone surfaces. With these parameters established, devices for in vivo evaluations were produced using nylon as a nonconductive scaffold for deposition of dual porosity electrospun fibers. The outer porous layer supported the development of a penetrating microcirculation and the membrane supported the transfer of insulin from encapsulated sustained release pellets for four weeks. Viable cells implanted within the device could be identified after two weeks of implantation. Through the successful demonstration of survival and cellular isolation of human epithelial cells within the implanted devices and the ability to use the device to deliver insulin, we have established the utility of this device toward localized cell transplantation. The Cell Delivery Device establishes a platform to test the feasibility of approaches to cell dose control and cell localization at the site of implantation in the clinical use of modified autologous or allogeneic cells. PMID:23913805

Robust Fluorine-Free Superhydrophobic Amino-Silicone Oil/SiO2 Modification of Electrospun Polyacrylonitrile Membranes for Waterproof-Breathable Application.

PubMed

Sheng, Junlu; Xu, Yue; Yu, Jianyong; Ding, Bin

2017-05-03

Superhydrophobic waterproof-breathable membranes have attracted considerable interest owing to their multifunctional applications in self-cleaning, anti-icing, anticorrosion, outdoor tents, and protective clothing. Despite the researches pertaning to the construction of superhydrophobic functional membranes by nanoparticle finishing have increased drastically, the disconnected particle component is easy to fall off from the membranes under deformation and wear conditions, which has restricted their wide use in practice. Here, robust superhydrophobic microporous membranes were prepared via a facile and environmentally friendly strategy by dip-coating amino-silicone oil (ASO) onto the electrospun polyacrylonitrile (PAN) membranes, followed by SiO 2 nanoparticles (SiO 2 NPs) blade coating. Compared with hydrophilic PAN membranes, the modified membranes exhibited superhydrophobic surface with an advancing water contact angle up to 156°, after introducing ASO as low surface energy substance and SiO 2 NPs as filler to reduce the pore size and construct the multihierarchical rough structure. Varying the concentrations of ASO and SiO 2 NPs systematically, the PAN electrospun membranes modified with 1 wt % ASO and 0.1 wt % SiO 2 NPs were endowed with good water-resistance (74.3 kPa), relative low thermal conductivity (0.0028 W m -1 K -1 ), modest vapor permeability (11.4 kg m -2 d -1 ), and air permeability (20.5 mm s -1 ). Besides, the inorganic-organic hybrid coating of ASO/SiO 2 NPs could maintain its superhydrophobicity even after 40 abrasion cycles. The resulting membranes were found to resist variations on the pH scale from 0 to 12, and retained their water repellent properties when exposed to harsh acidic and alkali conditions. This facile fabrication of durable fluorine-free superhydrophobic membranes simultaneous with good waterproof-breathable performance provides the advantages for potential applications in self-cleaning materials and versatile protective clothing.

Plasma Modification of Poly Lactic Acid Solutions to Generate High Quality Electrospun PLA Nanofibers.

PubMed

Rezaei, Fatemeh; Nikiforov, Anton; Morent, Rino; De Geyter, Nathalie

2018-02-02

Physical properties of pre-electrospinning polymer solutions play a key role in electrospinning as they strongly determine the morphology of the obtained electrospun nanofibers. In this work, an atmospheric-pressure argon plasma directly submerged in the liquid-phase was used to modify the physical properties of poly lactic acid (PLA) spinning solutions in an effort to improve their electrospinnability. The electrical characteristics of the plasma were investigated by two methods; V-I waveforms and Q-V Lissajous plots while the optical emission characteristics of the plasma were also determined using optical emission spectroscopy (OES). To perform a complete physical characterization of the plasma-modified polymer solutions, measurements of viscosity, surface tension, and electrical conductivity were performed for various PLA concentrations, plasma exposure times, gas flow rates, and applied voltages. Moreover, a fast intensified charge-couple device (ICCD) camera was used to image the bubble dynamics during the plasma treatments. In addition, morphological changes of PLA nanofibers generated from plasma-treated PLA solutions were observed by scanning electron microscopy (SEM). The performed plasma treatments were found to induce significant changes to the main physical properties of the PLA solutions, leading to an enhancement of electrospinnability and an improvement of PLA nanofiber formation.

The use of magnetron sputtering for the deposition of thin titanium coatings on the surface of bioresorbable electrospun fibrous scaffolds for vascular tissue engineering: A pilot study

NASA Astrophysics Data System (ADS)

Bolbasov, E. N.; Antonova, L. V.; Stankevich, K. S.; Ashrafov, A.; Matveeva, V. G.; Velikanova, E. A.; Khodyrevskaya, Yu. I.; Kudryavtseva, Yu. A.; Anissimov, Y. G.; Tverdokhlebov, S. I.; Barbarash, L. S.

2017-03-01

The deposition of thin titanium coatings using magnetron spattering on the surface of bioresorbable fibrous scaffolds produced by electrospinning was investigated. Parameters that allow the surface modification without damaging the "macro" structure of scaffolds were determined. Physicochemical properties of the modified scaffolds were described using SEM, EDS, DSC, optical goniometry, and mechanical testing. It was shown that plasma treatment has a significant influence on the scaffolds' fiber surface relief. The modification process leads to a slight decrease of the scaffold mechanical performance mainly caused by polymer crystallization. Increasing the deposition time increases the amount of titanium on the surface. The biocompatibility of the modified scaffolds was studied using hybridoma of the endothelial cells of human umbilical vein and human lung carcinoma (EA.hy 926 cell line). Cell adhesion, viability, and secretion of interleukin-6 (IL6), interleukin-8 (IL8), and vascular endothelial growth factor (VEGF) were investigated. It was demonstrated that the deposition of thin titanium coatings on the fibrous scaffolds' surface enhances cell adhesion. Additionally, it was determined that modified scaffolds have proangiogenic activity.

Functional electrospun membranes

NASA Astrophysics Data System (ADS)

Ognibene, G.; Fragalà, M. E.; Cristaldi, D. A.; Blanco, I.; Cicala, G.

2016-05-01

In this study we combined electrospun PES nanofibers with ZnO nanostructures in order to obtain a hierarchical nanostructured hybrid material to be use for active water filtration membranes. It benefits of flexibility and high surface area of the polymeric nanofibers as well as of additional functionalities of ZnOnanostructures. First, randomly oriented nanofibers with diameters of 716nm ±365 nm were electrospun on a glass fibers substrate from a solution of PES and DMF-TOL(1:1). ZnO nanorods were grown onto the surface of electrospun PES fibers by a Chemical Bath Deposition (CBD) process. It was preceed by a seeding process necessary to form nucleation sites for the subsequent radially aligned growth of ZnO nanowires. The morfology of the fibers and the effect of the seeding time have been analysed by SEM. The amount of ZnO nanowires grown over electrospun nanofibers was determined as 45% by weight. The high purity and crystallinity of the asobtained products are confirmed by XRD since all reflection peaks can be indexed to hexagonal wurtzite ZnO.

Electrospun polyacrylonitrile nanofibers functionalized with EDTA for adsorption of ionic dyes

NASA Astrophysics Data System (ADS)

Chaúque, Eutilério F. C.; Dlamini, Langelihle N.; Adelodun, Adedeji A.; Greyling, Corinne J.; Ngila, J. Catherine

2017-08-01

The manipulation of nanofibers' surface chemistry could enhance their potential application toward the removal of ionic dyes in wastewater. For this purpose, surface modification of electrospun polyacrylonitrile (PAN) nanofibers with ethylenediaminetetraacetic acid (EDTA) and ethylenediamine (EDA) crosslinker was experimented. The functionalized EDTA-EDA-PAN nanofibers were characterized using Fourier transform infrared (FT-IR) spectroscopy, X-ray photoelectron spectroscopy (XPS), scanning electron microscopy (SEM) and Brunauer-Emmett-Teller (BET) technique. The impregnation of EDA and EDTA chelating agents on the surface of PAN changed the distribution of nanofibers as proximity is increased (accompanied by reduced softness), but the nanofibrous structure of the pristine PAN nanofibers was not substantially altered. Adsorption equilibrium studies were performed with Freundlich, Langmuir and Temkin isotherm models with the former providing better correlation to the experimental data. The modified PAN nanofibers showed efficient sorption of methyl orange (MO) and reactive red (RR) from aqueous synthetic samples, evinced by the maximum adsorption capacities (at 25 °C) of 99.15 and 110.0 mg g-1, respectively. The fabricated nanofibers showed appreciable removal efficiency of the target dye sorptives from wastewater. However, the presence of high metal ions content affected the overall extraction of dyes from wastewater due to the depletion of the adsorbent's active adsorptive sites.

Phospholipid Nonwoven Electrospun Membranes

NASA Astrophysics Data System (ADS)

McKee, Matthew G.; Layman, John M.; Cashion, Matthew P.; Long, Timothy E.

2006-01-01

Nonwoven fibrous membranes were formed from electrospinning lecithin solutions in a single processing step. As the concentration of lecithin increased, the micellar morphology evolved from spherical to cylindrical, and at higher concentrations the cylindrical micelles overlapped and entangled in a fashion similar to polymers in semi-dilute or concentrated solutions. At concentrations above the onset of entanglements of the wormlike micelles, electrospun fibers were fabricated with diameters on the order of 1 to 5 micrometers. The electrospun phospholipid fibers offer the potential for direct fabrication of biologically based, high-surface-area membranes without the use of multiple synthetic steps, complicated electrospinning designs, or postprocessing surface treatments.

Surface energy characteristics of zeolite embedded PVDF nanofiber films with electrospinning process

NASA Astrophysics Data System (ADS)

Kang, Dong Hee; Kang, Hyun Wook

2016-11-01

Electrospinning is a nano-scale fiber production method with various polymer materials. This technique allows simple fiber diameters control by changing the physical conditions such as applied voltage and polymer solution viscosity during the fabrication process. The electrospun polymer fibers form a thin porous film with high surface area to volume ratio. Due to these unique characteristics, it is widely used for many application fields such as photocatalyst, electric sensor, and antibacterial scaffold for tissue engineering. Filtration is one of the main applications of electrospun polymer fibers for specific application of filtering out dust particles and dehumidification. Most polymers which are commonly used in electrospinning are hard to perform the filtering and dehumidification simultaneously because of their low hygroscopic property. To overcome this obstacle, the desiccant polymers are developed such as polyacrylic acid and polysulfobetaine methacrylate. However, the desiccant polymers are generally expensive and need special solvent for electrospinning. An alternating way to solve these problems is mixing desiccant material like zeolite in polymer solution during an electrospinning process. In this study, the free surface energy characteristics of electrospun polyvinylidene fluoride (PVDF) film with various zeolite concentrations are investigated to control the hygroscopic property of general polymers. Fundamental physical property of wettability with PVDF shows hydrophobicity. The electrospun PVDF film with small weight ratio with higher than 0.1% of zeolite powder shows diminished contact angles that certifying the wettability of PVDF can be controlled using desiccant material in electrospinning process. To quantify the surface energy of electrospun PVDF films, sessile water droplets are introduced on the electrospun PVDF film surface and the contact angles are measured. The contact angles of PVDF film are 140° for without zeolite and 80° for with 5 wt% of zeolite respectively. As a result, the surface energy of PVDF film can be controlled by embedding zeolite particles in electrospinning process and applied to filtration application of dust filtering and dehumidification simultaneously with low manufacturing cost.

Urea impedimetric biosensing using electrospun nanofibers modified with zinc oxide nanoparticles

NASA Astrophysics Data System (ADS)

Migliorini, Fernanda L.; Sanfelice, Rafaela C.; Mercante, Luiza A.; Andre, Rafaela S.; Mattoso, Luiz H. C.; Correa, Daniel. S.

2018-06-01

Reliable analytical techniques to evaluate dairy products, including milk, are of outmost importance to ensure food safety against contaminants. Among possible substances employed as adulterants in milk, urea raises deep concern due to its harmful effects to consumer's health. In the present study, a biosensing platform was developed to be applied in the electrochemical detection of urea. The sensing platform was fabricated using polymeric electrospun nanofibers of polyamide 6 (PA6) and polypyrrole (PPy) deposited onto fluorine doped tin oxide (FTO) electrodes, which were then modified with zinc oxide nanoparticles (ZnO). This material showed excellent properties for the immobilization of urease enzyme, conferring the FTO/PA6/PPy/ZnO/urease electrode high sensitivity for urea detection within the concentration range between 0.1 and 250 mg dL-1 with a limit of detection of 0.011 mg dL-1. The results achieved evidence the potential of electrospun nanofibers-based electrodes for applications in biosensors aiming at dairy products analysis.

Characterization and Modification of Electrospun Fiber Mats for Use in Composite Proton Exchange Membranes

NASA Astrophysics Data System (ADS)

Mannarino, Matthew Marchand

Electrostatic fiber formation, or electrospinning, offers a particularly simple and robust method to create polymeric nanofibers of various sizes and morphologies. In electrospinning, a viscoelastic fluid is charged so that a liquid jet is ejected from the surface of the fluid (typically in the form of a drop supplied by a needle or spinneret) and collected on a grounded plate, creating a nonwoven fiber mat. Modification of the diameter of the fibers as well as the porosity, specific surface area, and mechanical properties of the mat allows one to tailor electrospun mats for specific applications. Despite the widespread and rapidly growing use of electrospinning in the fabrication of novel nanomaterials, there are no simple, universal methods of predicting, a priori, the properties of electrospun fibers from knowledge of the polymer solution properties and electrospinning operating conditions alone. Changing a single fluid or processing parameter can affect the jet and fiber formation through several mechanisms. For example, using a different solvent can change several properties of the electrospinning fluid, such as the dielectric constant, conductivity, surface tension, and solute-solvent interaction. The work in this thesis seeks to develop a simple relation for predicting terminal jet diameter during electrospinning, which accounts for solution viscoelasticity as well as solution conductivity and operating parameters that can be easily measured and controlled. The mechanical and tribological properties of electrospun fiber mats are of paramount importance to their utility as components in a variety of applications. Although some mechanical properties of these mats have been investigated previously, reports of their tribological properties are essentially nonexistent. In this thesis, electrospun nanofiber mats of poly(trimethyl hexamethylene terephthalamide) (PA 6(3)T) and poly(hexamethylene adipamide) (PA 6,6) are characterized mechanically and tribologically. Post-spin thermal annealing was used to modify the fiber morphology, inter-fiber welding, and crystallinity within the fibers. Morphological changes, in-plane tensile response, friction coefficient, and wear rate were characterized as functions of the annealing temperature. The Young's moduli, yield stresses and toughnesses of the PA 6(3)T nonwoven mats improved by two- to ten-fold when annealed slightly above the glass transition temperature, but at the expense of mat porosity. The mechanical and tribological properties of the thermally annealed P A 6,6 fiber mats exhibited significant improvements through the Brill transition temperature, comparable to the improvements observed for amorphous P A 6(3)T electrospun mats annealed near the glass transition temperature. The wear rates for both polymer systems correlate with the yield properties of the mat, in accordance with a modified Ratner-Lancaster model. The variation in mechanical and tribological properties of the mats with increasing annealing temperature is consistent with the formation of fiber-to-fiber junctions and a mechanism of abrasive wear that involves the breakage of these junctions between fibers. A mechanically robust proton exchange membrane with high ionic conductivity and selectivity is an important component in many electrochemical energy devices such as fuel cells, batteries, and photovoltaics. The ability to control and improve independently the mechanical response, ionic conductivity, and selectivity properties of a membrane is highly desirable in the development of next generation electrochemical devices. In this thesis, the use of layer-by-layer (LbL) assembly of polyelectrolytes is used to generate three different polymer film morphologies on highly porous electrospun fiber mats: webbed, conformal coating, and pore-bridging films. Specifically, depending on whether a vacuum is applied to the backside of the mat or not, the spray-LbL assembly either fills the voids of the mat with the proton conducting material or forms a continuous fuel-blocking film. The LbL component consists of a proton-conducting, methanolimpermeable poly(diallyl dimethyl ammonium chloride)/sulfonated poly(2,6-dimethyl 1,4-phenylene oxide) (PDAC/sPPO) thin film. The electrospun fiber component consists of PA 6(3)T fibers of average diameter between 400 and 800 nm, in a nonwoven matrix of 60-90% porosity depending on the temperature of thermal annealing utilized to improve the mechanical properties. This thesis demonstrates the versatility and flexibility of this fabrication technique, since any ion conducting LbL system may be sprayed onto any electrospun fiber mat, allowing for independent control of functionality and mechanical properties. The mechanical properties of the spray coated electrospun mats are shown to be superior to the LbL-only system, and possess intrinsically greater dimensional stability and lower mechanical hysteresis than Nafion under hydration cycling. The electrochemical selectivity of the composite LbL-electrospun membrane is found to be superior to Nafion, which makes them a viable alternative proton exchange membrane for fuel cell applications. The composite proton exchange membranes fabricated in this work were tested in an operational direct methanol fuel cell, with results showing the capability for higher open circuit voltages (OCV) and comparable cell resistances when compared to Nafion. (Copies available exclusively from MIT Libraries, libraries.mit.edu/docs - docs@mit.edu)

Enzyme functionalized electrospun chitosan mats for antimicrobial treatment.

PubMed

Bösiger, Peter; Tegl, Gregor; Richard, Isabelle M T; Le Gat, Luce; Huber, Lukas; Stagl, Viktoria; Mensah, Anna; Guebitz, Georg M; Rossi, René M; Fortunato, Giuseppino

2018-02-01

This work presents electrospun chitosan mats, functionalized with glucose oxidase (GOX) to implement an in-situ hydrogen peroxide (H 2 O 2 ) generation system. The as spun CTS-PEO mats exhibited a smooth and homogenous morphology in combination with a high specific surface area (5.4m 2 /g) providing an excellent basis for further functionalization and subsequent glutaraldehyde crosslinking provided them with superior mechanical stability in aqueous environments. GOX was covalently immobilized, as proven by XPS, and resulted in activity recoveries between 20 and 40%. The functional mats generated a steady state concentration of ∼60μM H 2 O 2 per cm 2 which resulted in growth inhibition of E. coli and of S. aureus already after two hours of incubation. Additional cytotoxicity tests of the modified mats against mouse fibroblasts did not show an influence on the viability of the cells which proved it a functional biomaterial of great potential for biomedical applications. Copyright © 2017 Elsevier Ltd. All rights reserved.

Cellulose Acetate Modified Titanium Dioxide (TiO2) Nanoparticles Electrospun Composite Membranes: Fabrication and Characterization

NASA Astrophysics Data System (ADS)

Das, Chandan; Gebru, Kibrom Alebel

2017-12-01

Hybrid membranes from Cellulose Acetate (CA) and titanium oxide (TiO2) nanoparticles were fabricated using electrospinning technique. The electrospun hybrid membranes were characterized using field emission scanning electron microscopy, high energy electrons of the energy dispersive X-ray spectroscopy, X-ray diffraction patterns, atomic force microscopy, zeta potential (ζ), and thermo gravimetric analysis. The impact of TiO2 contents on the electrospun membranes matrix was studied in detail. All these characterization results indicated that TiO2 were uniformly distributed within the CA electrospun membrane's matrix. The addition of TiO2 caused formation of largely interconnected fiber networks which in turn have a positive effect on the enhancement of the membrane pore structures. As the amount of TiO2 addition was raised from 0 to 6.5 wt%, the entanglements of the fibers and the spider-net like network among fibers were increased.

Electrospun composite nanofiber fabrics containing uniformly dispersed antimicrobial agents as an innovative type of polymeric materials with superior antimicrobial efficacy.

PubMed

Sun, Xinbo; Zhang, Lifeng; Cao, Zhengbing; Deng, Ying; Liu, Li; Fong, Hao; Sun, Yuyu

2010-04-01

Herein we report that electrospun composite nanofiber fabrics containing uniformly dispersed antimicrobial agents and having large surface-to-mass ratios are an innovative type of antimicrobial polymeric materials with durable, nonleachable, and biocompatible characteristics, and more importantly, superior antimicrobial efficacy. Specifically, electrospun cellulose acetate (CA) nanofiber fabrics containing an N-halamine antimicrobial agent of bis(N-chloro-2,2,6,6-tetramethyl-4-piperidinyl) sebacate (Cl-BTMP) were prepared and evaluated; the results of antimicrobial efficacy indicated that the electrospun composite nanofiber fabrics substantially outperformed the control samples that were solution-cast films containing identical amounts of CA and Cl-BTMP. Additionally, the results of trypan blue assay test suggested that the electrospun composite nanofiber fabrics also had excellent mammal cell viability. The developed electrospun composite nanofiber fabrics with superior antimicrobial efficacy are expected to find vital applications in biomedical, hygienic, and many other fields.

Facile fabrication of gold nanoparticles-poly(vinyl alcohol) electrospun water-stable nanofibrous mats: efficient substrate materials for biosensors.

PubMed

Wang, Juan; Yao, Hong-Bin; He, Dian; Zhang, Chuan-Ling; Yu, Shu-Hong

2012-04-01

Electrospun nanofibrous mats are intensively studied as efficient scaffold materials applied in the fields of tissue engineering, catalysis, and biosensors due to their flexibility and porosity. In this paper, we report a facile route to fabricate gold nanoparticles-poly(vinyl alcohol) (Au NPs-PVA) hybrid water stable nanofibrous mats with tunable densities of Au NPs and further demonstrate the potential application of as-prepared Au NPs-PVA nanofibrous mats as efficient biosensor substrate materials. First, through the designed in situ cross-linkage in coelectrospun PVA-glutaraldehyde nanofibers, water insoluble PVA nanofibrous mats with suitable tensile strength were successfully prepared. Then, 3-mercaptopropyltrimethoxysilane (MPTES) was modified on the surface of obtained PVA nanofibrous films, which triggered successful homogeneous decoration of Au NPs through gold-sulfur bonding interactions. Finally, the Au NPs-PVA nanofibrous mats embedded with horseradish peroxidase (HRP) by electrostatic interactions were used as biosensor substrate materials for H(2)O(2) detection. The fabricated HRP-Au NPs/PVA biosensor showed a highly sensitive detection of H(2)O(2) with a detection limit of 0.5 μM at a signal-to-noise ratio of 3. By modifying other different functional nanaoparticles or enzyme on the PVA nanofibrous film will further expand their potential applications as substrate materials of different biosensors.

Functional electrospun fibers for the treatment of human skin wounds.

PubMed

Wang, Jing; Windbergs, Maike

2017-10-01

Wounds are trauma induced defects of the human skin involving a multitude of endogenous biochemical events and cellular reactions of the immune system. The healing process is extremely complex and affected by the patient's physiological conditions, potential implications like infectious pathogens and inflammation as well as external factors. Due to increasing incidence of chronic wounds and proceeding resistance of infection pathogens, there is a strong need for effective therapeutic wound care. In this context, electrospun fibers with diameters in the nano- to micrometer range gain increasing interest. While resembling the structure of the native human extracellular matrix, such fiber mats provide physical and mechanical protection (including protection against bacterial invasion). At the same time, the fibers allow for gas exchange and prevent occlusion of the wound bed, thus facilitating wound healing. In addition, drugs can be incorporated within such fiber mats and their release can be adjusted by the material and dimensions of the individual fibers. The review gives a comprehensive overview about the current state of electrospun fibers for therapeutic application on skin wounds. Different materials as well as fabrication techniques are introduced including approaches for incorporation of drugs into or drug attachment onto the fiber surface. Against the background of wound pathophysiology and established therapy approaches, the therapeutic potential of electrospun fiber systems is discussed. A specific focus is set on interactions of fibers with skin cells/tissues as well as wound pathogens and strategies to modify and control them as key aspects for developing effective wound therapeutics. Further, advantages and limitations of controlled drug delivery from fiber mats to skin wounds are discussed and a future perspective is provided. Copyright © 2017 Elsevier B.V. All rights reserved.

Influence of electrospun scaffolds prepared from distinct polymers on proliferation and viability of endothelial cells

DOE Office of Scientific and Technical Information (OSTI.GOV)

Matveeva, V. G., E-mail: matveeva-vg@mail.ru; Antonova, L. V., E-mail: antonova.la@mail.ru; Velikanova, E. A.

We compared electrospun nonwoven scaffolds from polylactic acid (PLA), polycaprolactone (PCL), and polyhydroxybutyrate/valerate (PHBV)/polycaprolactone (PHBV/PCL). The surface of PHBV/PCL and PCL scaffolds was highly porous and consisted of randomly distributed fibers, whilst the surface of PLA scaffolds consisted of thin straight fibers, which located more sparsely, forming large pores. Culture of EA.hy 926 endothelial cells on these scaffolds during 7 days and further fluorescent microscopy demonstrated that the surface of PHBV/PCL scaffolds was most favorable for efficient adhesion, proliferation, and viability of endothelial cells. The lowest proliferation rate and cell viability were detected on PLA scaffolds. Therefore, PHBV/PCL electrospun nonwovenmore » scaffolds demonstrated the best results regarding endothelial cell proliferation and viability as compared to PCL and PLA scaffolds.« less

Evaluation of gallic acid loaded zein sub-micron electrospun fibre mats as novel active packaging materials.

PubMed

Neo, Yun Ping; Swift, Simon; Ray, Sudip; Gizdavic-Nikolaidis, Marija; Jin, Jianyong; Perera, Conrad O

2013-12-01

The applicability of gallic acid loaded zein (Ze-GA) electrospun fibre mats towards potential active food packaging material was evaluated. The surface chemistry of the electrospun fibre mats was determined using X-ray photon spectroscopy (XPS). The electrospun fibre mats showed low water activity and whitish colour. Thermogravimetric analysis (TGA) and Attenuated Total Reflectance-Fourier Transform Infrared (ATR-FTIR) spectroscopy revealed the stability of the fibre mats over time. The Ze-GA fibre mats displayed similar rapid release profiles, with Ze-GA 20% exhibiting the fastest release rate in water as compared to the others. Gallic acid diffuses from the electrospun fibres in a Fickian diffusion manner and the data obtained exhibited a better fit to Higuchi model. L929 fibroblast cells were cultured on the electrospun fibres to demonstrate the absence of cytotoxicity. Overall, the Ze-GA fibre mats demonstrated antibacterial activity and properties consistent with those considered desirable for active packaging material in the food industry. Copyright © 2013 Elsevier Ltd. All rights reserved.

Electrospun composite matrices of poly(ε-caprolactone)-montmorillonite made using tenside free Pickering emulsions.

PubMed

Samanta, Archana; Takkar, Sonam; Kulshreshtha, Ritu; Nandan, Bhanu; Srivastava, Rajiv K

2016-12-01

The production of composite electrospun matrices of poly(ε-caprolactone) (PCL) using an emulsifier-free emulsion, made with minimal organic solvent, as precursor is reported. Pickering emulsions of PCL were prepared using modified montmorillonite (MMT) clay as the stabilizer. Hydrophobic tallow group of the modified MMT clay resulted in analogous interaction of clay with oil and aqueous phase and its adsorption at the interface to provide stability to the resultant emulsion. Composite fibrous matrices of PCL and MMT were produced using electrospinning under controlled conditions. The fiber fineness was found to alter with PCL concentration and volume fraction of the aqueous and oil phases. A higher tensile strength and modulus was obtained with inclusion of MMT in PCL electrospun matrix in comparison to a matrix made using neat PCL. The presence of clay in the fibrous matrix did not change the cell proliferation efficiency in comparison to neat PCL matrix. Composite fibrous matrices of PCL/MMT bearing enhanced tensile properties may find applications in areas other than tissue engineering for example food packaging and filtration. Copyright © 2016 Elsevier B.V. All rights reserved.

Photocatalytic Applications of Electrospun TiO2 Nanofibres Embedded with Bimodal Sized and Prismatic Gold Nanoparticles.

PubMed

Gopika, G; Asha, A M; Sivakumar, N; Balakrishnan, A; Nair, S V; Subramanian, K R V

2015-09-01

In this paper, we have synthesized electrospun TiO2 nanofibers embedded with bimodal sized and prismatic gold nanoparticles. The surface plasmons generated in the gold nanoparticles were used to enhance the performance of photocatalysis. The photocatalytic conversion efficiencies of these bimodal sized/prismatic gold nanoparticles when embedded in electrospun TiO2 fibres showed an enhancement of upto 60% over bare fiber systems and also show higher efficiencies than electrospun fibrous systems embedded with unimodal sized gold nanoparticles. Anisotropic bimodal gold nanoparticles show the highest degree of photocatalytic activity. This may be attributed to greater density/concentration of nanoparticles with higher effective surface area and formation of a junction between the smaller and larger nanoparticles. Such a bimodally distributed range of nanoparticles could also lead to greater trapping of charge carriers at the TiO2 conduction band edge and promoting catalytic reactions on account of these trapped charges. This enhanced photocatalytic activity is explained by invoking different operating mechanisms such as improved surface area, greater trapping, coarse plasmon resonance and band effects. Thus, a useful applicability of the gold nanoparticles is shown in the area of photocatalysis.

Functionalised Silk Fibres

DTIC Science & Technology

2012-07-30

rubber moulds (14 x 5 x 6 mm; RL060, ProSciTech, QLD), frozen at -20ºC overnight, and placed in a freeze - dryer (FD355DMP, FTS Systems) for 24 hours...surface area, low volume materials: electrospun fibres and freeze -dried sponges (Figure 9). Each new material type is described in detail below...surface area materials generated from recombinant honeybee silk proteins. (A) Electrospun fibres, scale bar is 200 nm. (B) Freeze dried sponges

Functionality in Electrospun Nanofibrous Membranes Based on Fiber's Size, Surface Area, and Molecular Orientation

PubMed Central

Matsumoto, Hidetoshi; Tanioka, Akihiko

2011-01-01

Electrospinning is a versatile method for forming continuous thin fibers based on an electrohydrodynamic process. This method has the following advantages: (i) the ability to produce thin fibers with diameters in the micrometer and nanometer ranges; (ii) one-step forming of the two- or three-dimensional nanofiber network assemblies (nanofibrous membranes); and (iii) applicability for a broad spectrum of molecules, such as synthetic and biological polymers and polymerless sol-gel systems. Electrospun nanofibrous membranes have received significant attention in terms of their practical applications. The major advantages of nanofibers or nanofibrous membranes are the functionalities based on their nanoscaled-size, highly specific surface area, and highly molecular orientation. These functionalities of the nanofibrous membranes can be controlled by their fiber diameter, surface chemistry and topology, and internal structure of the nanofibers. This report focuses on our studies and describes fundamental aspects and applications of electrospun nanofibrous membranes. PMID:24957735

Electrospinning and electrospraying of silicon oxycarbide-derived nanoporous carbon for supercapacitor electrodes

NASA Astrophysics Data System (ADS)

Tolosa, Aura; Krüner, Benjamin; Jäckel, Nicolas; Aslan, Mesut; Vakifahmetoglu, Cekdar; Presser, Volker

2016-05-01

In this study, carbide-derived carbon fibers from silicon oxycarbide precursor were synthesized by electrospinning of a commercially available silicone resin without adding a carrier polymer for the electrospinning process. The electrospun fibers were pyrolyzed yielding SiOC. Modifying the synthesis procedure, we were also able to obtain electrosprayed SiOC beads instead of fibers. After chlorine treatment, nanoporous carbon with a specific surface area of up to 2394 m2 g-1 was obtained (3089 m2 g-1 BET). Electrochemical characterization of the SiOC-CDC either as free-standing fiber mat electrodes or polymer-bound bead films was performed in 1 M tetraethylammonium tetrafluoroborate in acetonitrile (TEA-BF4 in ACN). The electrospun fibers presented a high gravimetric capacitance of 135 F g-1 at 10 mV s-1 and a very high power handling, maintaining 63% of the capacitance at 100 A g-1. Comparative data of SiOC-CDC beads and fibers show enhanced power handling for fiber mats only when the fiber network is intact, that is, a lowered performance was observed when using crushed mats that employ polymer binder.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Susanto, H., E-mail: heru.susanto@undip.ac.id; Samsudin, A. M.; Faz, M. W.

Electrospun nanofibers have many advantages such as high porosity, easy to be fabricated in various size and high ratio of surface area to volume. This paper presents the preparation of electrospun PVA/Chitosan nanofibers and more specifically focuses on the effect of post-treatment on the permeability and morphology of electrospun PVA/chitosan nanofibers. The mixtures of various concentrations of PVA (6,7,8 wt%)and 2 wt%.chitosan solution (with the ratio of 3:1)were used in electrospun with a constant rate of 0.7 ml/hour. The post-treatment was conducted by immersing in a ethanol or glutaraldehyde solution to performed crosslink structure. The electrospun PVA/Chitosan nanofiber was characterized bymore » scanning electron microscopy (SEM) and fourier transform infrared (FTIR) spectroscopy. The results revealed that the viscosity of the mixture solution is directly proportional to its concentration. Increasing the viscosity increased the diameter of fiber but also made the larger beads formation. FTIR measurement exhibited the existence of relevant functional groups of both PVA and chitosan in the composites.The crosslinked structure was found for the electrospun PVA/Chitosan nanofibers treated with glutaraldehyde solution.« less

A Microfluidic Chip Integrated with Hyaluronic Acid-Functionalized Electrospun Chitosan Nanofibers for Specific Capture and Nondestructive Release of CD44-Overexpressing Circulating Tumor Cells.

PubMed

Wang, Mengyuan; Xiao, Yunchao; Lin, Lizhou; Zhu, Xiaoyue; Du, Lianfang; Shi, Xiangyang

2018-04-18

Detection of circulating tumor cells (CTCs) in peripheral blood is of paramount significance for early-stage cancer diagnosis, estimation of cancer development, and individualized cancer therapy. Herein, we report the development of hyaluronic acid (HA)-functionalized electrospun chitosan nanofiber (CNF)-integrated microfludic platform for highly specific capture and nondestructive release of CTCs. First, electrospun CNFs were formed and modified with zwitterion of carboxyl betaine acrylamide (CBAA) via Michael addition reaction and then targeting ligand HA through a disulfide bond. We show that the formed nanofibers still maintain the smooth fibrous morphology after sequential surface modifications, have a good hemocompatibility, and exhibit an excellent antifouling property due to the CBAA modification. After being embedded within a microfluidic chip, the fibrous mat can capture cancer cells (A549, a human lung cancer cell line) with an efficiency of 91% at a flow rate of 1.0 mL/h. Additionally, intact release of cancer cells is able to be achieved after treatment with glutathione for 40 min to have a release efficiency of 90%. Clinical applications show that 9 of 10 nonsmall-cell lung cancer patients and 5 of 5 breast cancer patients are diagnosed to have CTCs (1 to 18 CTCs per mL of blood). Our results suggest that the developed microfluidic system integrated with functionalized CNF mats may be employed for effective CTCs capture for clinical diagnosis of cancer.

Effect of micropatterning induced surface hydrophobicity on drug release from electrospun cellulose acetate nanofibers

NASA Astrophysics Data System (ADS)

Adepu, Shivakalyani; Gaydhane, Mrunalini K.; Kakunuri, Manohar; Sharma, Chandra S.; Khandelwal, Mudrika; Eichhorn, Stephen J.

2017-12-01

Sustained release and prevention of burst release for low half-life drugs like Diclofenac sodium is crucial to prevent drug related toxicity. Electrospun nanofibers have emerged recently as potential carrier materials for controlled and sustained drug release. Here, we present a facile method to prevent burst release by tuning the surface wettability through template assisted micropatterning of drug loaded electrospun cellulose acetate (CA) nanofibers. A known amount of drug (Diclofenac sodium) was first mixed with CA and then electrospun in the form of a nanofabric. This as-spun network was hydrophilic in nature. However, when electrospinning was carried out through non-conducting templates, viz nylon meshes with 50 and 100 μm size openings, two kinds of hydrophobic micro-patterned CA nanofabrics were produced. In vitro transdermal testing of our nanofibrous mats was carried out; these tests were able to show that it would be possible to create a patch for transdermal drug release. Further, our results show that with optimized micro-patterned dimensions, a zero order sustained drug release of up to 12 h may be achieved for the transdermal system when compared to non-patterned samples. This patterning caused a change in the surface wettability, to a hydrophobic surface, resulting in a controlled diffusion of the hydrophilic drug. Patterning assisted in controlling the initial burst release, which is a significant finding especially for low half-life drugs.

The Development of Novel Nanomaterials for Separation Science

NASA Astrophysics Data System (ADS)

Zewe, Joseph William

Separation efficiency is inversely proportional to the diameter of the particles of the stationary phase. Accordingly, a major aim of current separations research is focused on the reduction of both the diameter and particle-to-particle size variation of sorbent materials utilized as stationary phases. Herein, novel methods for the fabrication and application of various nanoscale stationary phases are described. Electrospinning is a simple and cost-effective method of generating nanofibers; here both polymeric and carbon electrospun nanofibers are applied as sorbent materials. Carbon nanofibers are of particular interest; graphite and glassy carbon are widely utilized in separation science due to their chemical and mechanical stability and unique selectivity. Electrospun carbon nanofibers have proven to be ideal for use as an extractive phase for solid phase microextraction (SPME) and have been successfully coupled to both gas and liquid chromatography. The high surface area nanofibrous mat provides extraction efficiencies for both polar and nonpolar compounds that range from 2-8 times greater than those attainable using currently available commercial SPME fibers. The electrospun nanofibrous SPME phases proved to be very stable when immersed in a range of solvents, demonstrating increased stability relative to conventional liquid SPME coatings. The chemical and mechanical stability of the electrospun carbon nanofiber SPME phases expands the range of compounds that are applicable to SPME while extending the lifetime of the SPME fibers. Molecularly imprinted (MI) electrospun polymeric and carbon nanofibers were also generated using the template molecule dibutyl butyl phosphonate (DBBP), a surrogate for chemical warfare agents. Nicotine was also used as a template molecule. The MI-nanofibers imprinted with DBBP were applied as an adsorbent for SPME. The MI-SPME fibers preferentially adsorbed the DBBP template molecule relative to the non-imprinted SPME fibers, demonstrating that imprinted surfaces containing analyte-specific recognition sites can be produced. MI-nicotine electrospun nanofibers were also studied as a solid phase extraction (SPE) adsorbent for the extraction of nicotine from water. The MI-nanofibers showed a greater extraction efficiency for nicotine relative to their non-imprinted counterparts. Electrospun nanofibers have proven to be effective stationary phases in ultra-thin layer chromatography (UTLC), giving more efficient separations in shorter analysis times than traditional particle-based stationary phases. This technology was further enhanced by aligning the nanofibrous mats in a single direction. Aligned electrospun UTLC (AE-UTLC) devices showed improved performance relative to non-aligned electrospun UTLC phases, demonstrating higher separation efficiency and reduced times of analysis. All currently utilized carbon sorbents, including the carbon nanofibers described in this work, possess at least two different surface sites for interaction with solutes, namely basal-plane and edge-plane sites. It is predicted that a more homogenous carbon surface, consisting entirely of either all-basal or all-edge plane sites, would produce a separation with a significant improvement in chromatographic efficiency. Progress toward homogenous carbon phases and their application and sorption behavior are also discussed.

Potential of Electrospun Nanofibers for Biomedical and Dental Applications

PubMed Central

Zafar, Muhammad; Najeeb, Shariq; Khurshid, Zohaib; Vazirzadeh, Masoud; Zohaib, Sana; Najeeb, Bilal; Sefat, Farshid

2016-01-01

Electrospinning is a versatile technique that has gained popularity for various biomedical applications in recent years. Electrospinning is being used for fabricating nanofibers for various biomedical and dental applications such as tooth regeneration, wound healing and prevention of dental caries. Electrospun materials have the benefits of unique properties for instance, high surface area to volume ratio, enhanced cellular interactions, protein absorption to facilitate binding sites for cell receptors. Extensive research has been conducted to explore the potential of electrospun nanofibers for repair and regeneration of various dental and oral tissues including dental pulp, dentin, periodontal tissues, oral mucosa and skeletal tissues. However, there are a few limitations of electrospinning hindering the progress of these materials to practical or clinical applications. In terms of biomaterials aspects, the better understanding of controlled fabrication, properties and functioning of electrospun materials is required to overcome the limitations. More in vivo studies are definitely required to evaluate the biocompatibility of electrospun scaffolds. Furthermore, mechanical properties of such scaffolds should be enhanced so that they resist mechanical stresses during tissue regeneration applications. The objective of this article is to review the current progress of electrospun nanofibers for biomedical and dental applications. In addition, various aspects of electrospun materials in relation to potential dental applications have been discussed. PMID:28787871

Poly (vinyl alcohol)/gum karaya electrospun plasma treated membrane for the removal of nanoparticles (Au, Ag, Pt, CuO and Fe3O4) from aqueous solutions.

PubMed

Padil, Vinod Vellora Thekkae; Černík, Miroslav

2015-04-28

In the present work, nanofibre membranes composed of polyvinyl alcohol (PVA) and a natural gum karaya (GK) hydrocolloid were prepared using electrospinning. The electrospun membranes of PVA/GK were cross-linked with heat treatment and later methane plasma was used to obtain a hydrophobic membrane. The morphology, characterization and adsorption ability of P-NFM was assessed using scanning electron microscopy, UV-vis spectroscopy, ATR-FTIR techniques, water contact angle and ICP-MS analytical methods. The membrane was employed for the extraction of nanoparticles (Ag, Au, Pt, CuO and Fe3O4) from water. The nanoparticle extraction kinetic and adsorption isotherm perform the pseudo-second-order model and Langmuir isotherm model, respectively. The adsorption capacities of the membrane for the removal of NPs from water diverge in the order Pt>Au>Ag>CuO>Fe3O4. The high adsorption efficiency for the removal of NPs from water was compared with an untreated membrane. Physisorption, functional group interactions, complexation reactions between metal/metal oxide nanoparticles with various functional groups present in NFM and modified surface properties such as the balance of hydrophilicity/hydrophobicity, surface free energy, and the high surface area of the plasma treated membrane were possible mechanisms of NPs adsorption onto NFM. The regeneration and reusability were tested in five consecutive adsorption/desorption cycles. Copyright © 2015 Elsevier B.V. All rights reserved.

Thermal, Electrical and Surface Hydrophobic Properties of Electrospun Polyacrylonitrile Nanofibers for Structural Health Monitoring

PubMed Central

Alarifi, Ibrahim M.; Alharbi, Abdulaziz; Khan, Waseem S.; Swindle, Andrew; Asmatulu, Ramazan

2015-01-01

This paper presents an idea of using carbonized electrospun Polyacrylonitrile (PAN) fibers as a sensor material in a structural health monitoring (SHM) system. The electrospun PAN fibers are lightweight, less costly and do not interfere with the functioning of infrastructure. This study deals with the fabrication of PAN-based nanofibers via electrospinning followed by stabilization and carbonization in order to remove all non-carbonaceous material and ensure pure carbon fibers as the resulting material. Electrochemical impedance spectroscopy was used to determine the ionic conductivity of PAN fibers. The X-ray diffraction study showed that the repeated peaks near 42° on the activated nanofiber film were α and β phases, respectively, with crystalline forms. Contact angle, thermogravimetric analysis (TGA), differential scanning calorimetry (DSC) and Fourier transform infrared spectroscopy (FTIR) were also employed to examine the surface, thermal and chemical properties of the carbonized electrospun PAN fibers. The test results indicated that the carbonized PAN nanofibers have superior physical properties, which may be useful for structural health monitoring (SHM) applications in different industries. PMID:28793615

Synergistic effect of topography, surface chemistry and conductivity of the electrospun nanofibrous scaffold on cellular response of PC12 cells.

PubMed

Tian, Lingling; Prabhakaran, Molamma P; Hu, Jue; Chen, Menglin; Besenbacher, Flemming; Ramakrishna, Seeram

2016-09-01

Electrospun nanofibrous nerve implants is a promising therapy for peripheral nerve injury, and its performance can be tailored by chemical cues, topographical features as well as electrical properties. In this paper, a surface modified, electrically conductive, aligned nanofibrous scaffold composed of poly (lactic acid) (PLA) and polypyrrole (Ppy), referred to as o-PLAPpy_A, was fabricated for nerve regeneration. The morphology, surface chemistry and hydrophilicity of nanofibers were characterized by Scanning Electron Microscopy (SEM), Fourier transform infrared spectroscopy (FTIR), X-ray photoelectron spectroscopy (XPS) and water contact angle, respectively. The effects of these nanofibers on neuronal differentiation using PC12 cells were evaluated. A hydrophilic surface was created by Poly-ornithine coating, which was able to provide a better environment for cell attachment, and furthermore aligned fibers were proved to be able to guide PC12 cells grow along the fiber direction and be beneficial for neurite outgrowth. The cellular response of PC12 cells to pulsed electrical stimulation was evaluated by NF 200 and alpha tubulin expression, indicating that electrical stimulation with a voltage of 40mV could enhance the neurite outgrowth. The PC12 cells stimulated with electrical shock showed greater level of neurite outgrowth and smaller cell body size. Moreover, the PC12 cells under electrical stimulation showed better viability. In summary, the o-PLAPpy_A nanofibrous scaffold supported the attachment, proliferation and differentiation of PC12 cells in the absence of electrical stimulation, which could be potential candidate for nerve regeneration applications. Copyright © 2016 Elsevier B.V. All rights reserved.

Method for Coating a Tow with an Electrospun Nanofiber

NASA Technical Reports Server (NTRS)

Kohlman, Lee W. (Inventor); Roberts, Gary D. (Inventor)

2015-01-01

Method and apparatus for enhancing the durability as well as the strength and stiffness of prepreg fiber tows of the sort used in composite materials are disclosed. The method involves adhering electrospun fibers onto the surface of such composite materials as filament-wound composite objects and the surface of prepreg fiber tows of the sort that are subsequently used in the production of composite materials of the filament-wound, woven, and braided sorts. The apparatus performs the methods described herein.

Trifunctional Epoxy Resin Composites Modified by Soluble Electrospun Veils: Effect on the Viscoelastic and Morphological Properties

PubMed Central

Ognibene, Giulia; Mannino, Salvatore

2018-01-01

Electrospun veils from copolyethersulfones (coPES) were prepared as soluble interlaminar veils for carbon fiber/epoxy composites. Neat, resin samples were impregnated into coPES veils with unmodified resin, while dry carbon fabrics were covered with electrospun veils and then infused with the unmodified epoxy resin to prepare reinforced laminates. The thermoplastic content varied from 10 wt% to 20 wt%. TGAP epoxy monomer showed improved and fast dissolution for all the temperatures tested. The unreinforced samples were cured first at 180 °C for 2 h and then were post-cured at 220 °C for 3 h. These sample showed a high dependence on the curing cycle. Carbon reinforced samples showed significant differences compared to the neat resin samples in terms of both viscoelastic and morphological properties. PMID:29522444

Effects of quaternization on the morphological stability and antibacterial activity of electrospun poly(DMAEMA-co-AMA) nanofibers.

PubMed

Xu, Jing-Wei; Wang, Yao; Yang, Yun-Feng; Ye, Xiang-Yu; Yao, Ke; Ji, Jian; Xu, Zhi-Kang

2015-09-01

Electrospun nanofibers with antibacterial activity are greatly promising for medical treatment and water purification. Herein we report antibacterial nanofibers electrospun from a series of poly(dimethylamino ethyl methacrylate-co-alkyl methacrylates) (poly(DMAEMA-co-AMA)) and to distinguish the effects of free and cross-linked cations derived from quanternization on the antibacterial activity. Poly(DMAEMA-co-AMA)s are simply synthesized by free radical polymerization from commercial monomers. DSC analysis indicates that they have Tg lower than room temperature and thus the electrospun nanofibers adhere to each other and evenly tend to form films, instead of keeping cylinderic shape. Benzyl chloride (BC) and p-xylylene dichloride (XDC) can quaternize DMAEMA units and to generate cations on the nanofiber surface. XPS analysis and colorimetric assay determine the quaternization degree and the surface accessible quaternary amines (N(+)), respectively. It is very promising that this quaternization endows the electrospun nanofibers with both stable morphology and antibacterial activity. The BC-quaternized fibers show better antibacterial behavior against Escherichia coli and Staphylococcus aureus than those of the XDC-quaternized/cross-linked ones, because cross-linking suppresses the chain mobility of cations. Our results confirm that antibacterial nanofibers can be facilely prepared and chain mobility of the formed cations is the necessary prerequisite for their antibacterial activity. Copyright © 2015 Elsevier B.V. All rights reserved.

Poly(ɛ-caprolactone)/gelatin composite electrospun scaffolds with porous crater-like structures for tissue engineering.

PubMed

Hwang, Patrick T J; Murdock, Kyle; Alexander, Grant C; Salaam, Amanee D; Ng, Joshua I; Lim, Dong-Jin; Dean, Derrick; Jun, Ho-Wook

2016-04-01

Electrospinning has been widely used to fabricate scaffolds imitating the structure of natural extracellular matrix (ECM). However, conventional electrospinning produces tightly compacted nanofiber layers with only small superficial pores and a lack of bioactivity, which limit the usefulness of electrospinning in biomedical applications. Thus, a porous poly(ε-caprolactone) (PCL)/gelatin composite electrospun scaffold with crater-like structures was developed. Porous crater-like structures were created on the scaffold by a gas foaming/salt leaching process; this unique fiber structure had more large pore areas and higher porosity than the conventional electrospun fiber network. Various ratios of PCL/gelatin (concentration ratios: 100/0, 75/25, and 50/50) composite electrospun scaffolds with and without crater-like structures were characterized by their microstructures, surface chemistry, degradation, mechanical properties, and ability to facilitate cell growth and infiltration. The combination of PCL and gelatin endowed the scaffold with both structural stability of PCL and bioactivity of gelatin. All ratios of scaffolds with crater-like structures showed fairly similar surface chemistry, degradation rates, and mechanical properties to equivalent scaffolds without crater-like structures; however, craterized scaffolds displayed higher human mesenchymal stem cell (hMSC) proliferation and infiltration throughout the scaffolds after 7-day culture. Therefore, these results demonstrated that PCL/gelatin composite electrospun scaffolds with crater-like structures can provide a structurally and biochemically improved three-dimensional ECM-mimicking microenvironment. © 2016 Wiley Periodicals, Inc.

Poly(ε-caprolactone)/gelatin composite electrospun scaffolds with porous crater-like structures for tissue engineering

PubMed Central

Hwang, Patrick T.J.; Murdock, Kyle; Alexander, Grant C.; Salaam, Amanee D.; Ng, Joshua I.; Lim, Dong-Jin; Dean, Derrick; Jun, Ho-Wook

2016-01-01

Electrospinning has been widely used to fabricate scaffolds imitating the structure of natural extracellular matrix (ECM). However, conventional electrospinning produces tightly compacted nanofiber layers with only small superficial pores and a lack of bioactivity, which limit the usefulness of electrospinning in biomedical applications. Thus, a porous poly(ε-caprolactone) (PCL)/gelatin composite electrospun scaffold with crater-like structures was developed. Porous crater-like structures were created on the scaffold by a gas foaming/salt leaching process; this unique fiber structure had more large pore areas and higher porosity than the conventional electrospun fiber network. Various ratios of PCL/gelatin (concentration ratios: 100/0, 75/25, and 50/50) composite electrospun scaffolds with and without crater-like structures were characterized by their microstructures, surface chemistry, degradation, mechanical properties, and ability to facilitate cell growth and infiltration. The combination of PCL and gelatin endowed the scaffold with both structural stability of PCL and bioactivity of gelatin. All ratios of scaffolds with crater-like structures showed fairly similar surface chemistry, degradation rates, and mechanical properties to equivalent scaffolds without crater-like structures; however, craterized scaffolds displayed higher human mesenchymal stem cell (hMSC) proliferation and infiltration throughout the scaffolds after 7-day culture. Therefore, these results demonstrated that PCL/gelatin composite electrospun scaffolds with crater-like structures can provide a structurally and biochemically improved three-dimensional ECM-mimicking microenvironment. PMID:26567028

Electrospun Nanofibers Made of Silver Nanoparticles, Cellulose Nanocrystals, and Polyacrylonitrile as Substrates for Surface-Enhanced Raman Scattering

PubMed Central

Ren, Suxia; Dong, Lili; Zhang, Xiuqiang; Lei, Tingzhou; Ehrenhauser, Franz; Song, Kunlin; Li, Meichun; Sun, Xiuxuan; Wu, Qinglin

2017-01-01

Nanofibers with excellent activities in surface-enhanced Raman scattering (SERS) were developed through electrospinning precursor suspensions consisting of polyacrylonitrile (PAN), silver nanoparticles (AgNPs), silicon nanoparticles (SiNPs), and cellulose nanocrystals (CNCs). Rheology of the precursor suspensions, and morphology, thermal properties, chemical structures, and SERS sensitivity of the nanofibers were investigated. The electrospun nanofibers showed uniform diameters with a smooth surface. Hydrofluoric (HF) acid treatment of the PAN/CNC/Ag composite nanofibers (defined as p-PAN/CNC/Ag) led to rougher fiber surfaces with certain pores and increased mean fiber diameters. X-ray diffraction (XRD) and X-ray photoelectron spectroscopy (XPS) results confirmed the existence of AgNPs that were formed during heat and HF acid treatment processes. In addition, thermal stability of the electrospun nanofibers increased due to the incorporation of CNCs and AgNPs. The p-PAN/CNC/Ag nanofibers were used as a SERS substrate to detect p-aminothiophenol (p-ATP) probe molecule. The results show that this substrate exhibited high sensitivity for the p-ATP probe detection. PMID:28772428

Interfacial Properties of Lignin-Based Electrospun Nanofibers and Films Reinforced with Cellulose Nanocrystals

Treesearch

Mariko Ago; Joseph E. Jakes; Leena-Sisko Johansson; Sunkyu Park; Orlando J. Rojas

2012-01-01

Sub-100 nm resolution local thermal analysis, X-ray photoelectron spectroscopy (XPS), and water contact angle (WCA) measurements were used to relate surface polymer distribution with the composition of electrospun fiber mats and spin coated films obtained from aqueous dispersions of lignin, polyvinyl alcohol (PVA), and cellulose nanocrystal (CNC). Defect-free lignin/...

Electrospun nanofibres in agriculture and the food industry: a review.

PubMed

Noruzi, Masumeh

2016-11-01

The interesting characteristics of electrospun nanofibres, such as high surface-to-volume ratio, nanoporosity, and high safety, make them suitable candidates for use in a variety of applications. In the recent decade, electrospun nanofibres have been applied to different potential fields such as filtration, wound dressing, drug delivery, etc. and a significant number of review papers have been published in these fields. However, the use of electrospun nanofibres in agriculture is comparatively novel and is still in its infancy. In this paper, the specific applications of electrospun nanofibres in agriculture and food science, including plant protection using pheromone-loaded nanofibres, plant protection using encapsulation of biocontrol agents, preparation of protective clothes for farm workers, encapsulation of agrochemical materials, deoxyribonucleic acid extraction in agricultural research studies, pre-concentration and measurement of pesticides in crops and environmental samples, preparation of nanobiosensors for pesticide detection, encapsulation of food materials, fabrication of food packaging materials, and filtration of beverage products are reviewed and discussed. This paper may help researchers develop the use of electrospun nanofibres in agriculture and food science to address some serious problems such as the intensive use of pesticides. © 2016 Society of Chemical Industry. © 2016 Society of Chemical Industry.

Investigation of drug release and matrix degradation of electrospun poly(DL-lactide) fibers with paracetanol inoculation.

PubMed

Cui, Wenguo; Li, Xiaohong; Zhu, Xinli; Yu, Guo; Zhou, Shaobing; Weng, Jie

2006-05-01

This study was aimed at assessing the potential use of electrospun fibers as drug delivery vehicles with focus on the different diameters and drug contents to control drug release and polymer fiber degradation. A drug-loaded solvent-casting polymer film was made with an average thickness of 100 microm for comparative purposes. DSC analysis indicated that electrospun fibers had a lower T(g) but higher transition enthalpy than solvent-casting polymer film due to the inner stress and high degree of alignment and orientation of polymer chains caused by the electrospinning process. Inoculation of paracetanol led to a further slight decrease in the T(g) and transition enthalpy. An in vitro drug release study showed that a pronounced burst release or steady release phase was initially observed followed by a plateau or gradual release during the rest time. Fibers with a larger diameter exhibited a longer period of nearly zero order release, and higher drug encapsulation led to a more significant burst release after incubation. In vitro degradation showed that the smaller diameter and higher drug entrapment led to more significant changes of morphologies. The electrospun fiber mat showed almost no molecular weight reduction, but mass loss was observed for fibers with small and medium size, which was characterized with surface erosion and inconsistent with the ordinarily polymer degrading form. Further wetting behavior analysis showed that the high water repellent property of electrospun fibers led to much slower water penetration into the fiber mat, which may contribute to the degradation profiles of surface erosion. The specific degradation profile and adjustable drug release behaviors by variation of fiber characteristics made the electrospun nonwoven mat a potential drug delivery system rather than polymer films and particles.

Nitric Oxide-Releasing Silica Nanoparticle-Doped Polyurethane Electrospun Fibers

PubMed Central

Koh, Ahyeon; Carpenter, Alexis W.; Slomberg, Danielle L.; Schoenfisch, Mark H.

2013-01-01

Electrospun polyurethane fibers doped with nitric oxide (NO)-releasing silica particles are presented as novel macromolecular scaffolds with prolonged NO-release and high porosity. Fiber diameter (119–614 nm) and mechanical strength (1.7–34.5 MPa of modulus) were varied by altering polyurethane type and concentration, as well as the NO-releasing particle composition, size, and concentration. The resulting NO-releasing electrospun nanofibers exhibited ~83% porosity with flexible plastic or elastomeric behavior. The use of N-diazeniumdiolate- or S-nitrosothiol-modified particles yielded scaffolds exhibiting a wide range of NO release totals and durations (7.5 nmol mg−1–0.12 μmol mg−1 and 7 h to 2 weeks, respectively). The application of NO-releasing porous materials as coating for subcutaneous implants may improve tissue biocompatibility by mitigating the foreign body response and promoting cell integration. PMID:23915047

Chain Confinement in Electrospun Nanocomposites: using Thermal Analysis to Investigate Polymer-Filler Interactions

DOE Office of Scientific and Technical Information (OSTI.GOV)

Q Ma; B Mao; P Cebe

2011-12-31

We investigate the interaction of the polymer matrix and filler in electrospun nanofibers using advanced thermal analysis methods. In particular, we study the ability of silicon dioxide nanoparticles to affect the phase structure of poly(ethylene terephthalate), PET. SiO{sub 2} nanoparticles (either unmodified or modified with silane) ranging from 0 to 2.0 wt% in PET were electrospun from hexafluoro-2-propanol solutions. The morphologies of both the electrospun (ES) nanofibers and the SiO{sub 2} powders were observed by scanning and transmission electron microscopy, while the amorphous or crystalline nature of the fibers was determined by real-time wide-angle X-ray scattering. The fractions of themore » crystal, mobile amorphous, and rigid amorphous phases of the non-woven, nanofibrous composite mats were quantified by using heat capacity measurements. The amount of the immobilized polymer layer, the rigid amorphous fraction, was obtained from the specific reversing heat capacity for both as-spun amorphous fibers and isothermally crystallized fibers. Existence of the rigid amorphous phase in the absence of crystallinity was verified in nanocomposite fibers, and two origins for confinement of the rigid amorphous fraction are proposed. Thermal analysis of electrospun fibers, including quasi-isothermal methods, provides new insights to quantitatively characterize the polymer matrix phase structure and thermal transitions, such as devitrification of the rigid amorphous fraction.« less

Antibacterial poly(lactic acid) (PLA) films grafting electrospun PLA/Ally isothioscyanate (AITC) fibers for food packaging

USDA-ARS?s Scientific Manuscript database

Poly(lactic acid) (PLA) fibers of submicron sizes encapsulating allyl isothiocyanate (AITC) (PfA) were made and electrospun onto the surfaces of PLA films (PfA-g-film). SEM examination confirmed that the fibers were grafted to the PLA film after the (PfA-g-film) underwent air blowing and water washi...

Chondroitin sulfate immobilization at the surface of electrospun nanofiber meshes for cartilage tissue regeneration approaches

NASA Astrophysics Data System (ADS)

Piai, Juliana Francis; da Silva, Marta Alves; Martins, Albino; Torres, Ana Bela; Faria, Susana; Reis, Rui L.; Muniz, Edvani Curti; Neves, Nuno M.

2017-05-01

Aiming at improving the biocompatibility of biomaterial scaffolds, surface modification presents a way to preserve their mechanical properties and to improve the surface bioactivity. In this work, chondroitin sulfate (CS) was immobilized at the surface of electrospun poly(caprolactone) nanofiber meshes (PCL NFMs), previously functionalized by UV/O3 exposure and aminolysis. Contact angle, SEM, optical profilometry, FTIR, X-ray photoelectron spectroscopy techniques confirmed the success of CS-immobilization in PCL NFMs. Furthermore, CS-immobilized PCL NFMs showed lower roughness and higher hydrophilicity than the samples without CS. Human articular chondrocytes (hACs) were cultured on electrospun PCL NFMs with or without CS immobilization. It was observed that hACs proliferated through the entire time course of the experiment in both types of nanofibrous scaffolds, as well as for the production of glycosaminoglycans. Quantitative-PCR results demonstrated over-expression of cartilage-related genes such as Aggrecan, Collagen type II, COMP and Sox9 on both types of nanofibrous scaffolds. Morphological observations from SEM and LSCM revealed that hACs maintained their characteristic round shape and cellular agglomeration exclusively on PCL NFMs with CS immobilization. In conclusion, CS immobilization at the surface of PCL NFMs was achieved successfully and provides a valid platform enabling further surface functionalization methods in scaffolds to be developed for cartilage tissue engineering.

Electrospun materials for affinity-based engineering and drug delivery

NASA Astrophysics Data System (ADS)

Sill, T. J.; von Recum, H. A.

2015-10-01

Electrospinning is a process which can quickly and cheaply create materials of high surface to volume and aspect ratios from many materials, however in application toward drug delivery this can be a strong disadvantage as well. Diffusion of drug is proportional to the thickness of that device. In moving from macro to micro to nano-sized electrospun materials drug release rates change to profiles that are too fast to be therapeutically beneficial. In this work we use molecular interactions to further control the rate of release beyond that capable of diffusion alone. To do this we create materials with molecular pockets, which can "hold" therapeutic drugs through a reversible interaction such as a host/guest complexation. Through these complexes we show we are able to impact delivery of drug from electrospun materials, and also apply them in tissue engineering for the reversible presentation of biomolecules on a fiber surface.

Effects of Electrospun Carbon Nanofibers' Interlayers on High-Performance Lithium-Sulfur Batteries.

PubMed

Gao, Tianji; Le, TrungHieu; Yang, Ying; Yu, Zhihao; Huang, Zhenghong; Kang, Feiyu

2017-03-31

Two different interlayers were introduced in lithium-sulfur batteries to improve the cycling stability with sulfur loading as high as 80% of total mass of cathode. Melamine was recommended as a nitrogen-rich (N-rich) amine component to synthesize a modified polyacrylic acid (MPAA). The electrospun MPAA was carbonized into N-rich carbon nanofibers, which were used as cathode interlayers, while carbon nanofibers from PAA without melamine was used as an anode interlayer. At the rate of 0.1 C, the initial discharge capacity with two interlayers was 983 mAh g -1 , and faded down to 651 mAh g -1 after 100 cycles with the coulombic efficiency of 95.4%. At the rate of 1 C, the discharge capacity was kept to 380 mAh g -1 after 600 cycles with a coulombic efficiency of 98.8%. It apparently demonstrated that the cathode interlayer is extremely effective at shutting down the migration of polysulfide ions. The anode interlayer induced the lithium ions to form uniform lithium metal deposits confined on the fiber surface and in the bulk to strengthen the cycling stability of the lithium metal anode.

Effects of Electrospun Carbon Nanofibers’ Interlayers on High-Performance Lithium–Sulfur Batteries

PubMed Central

Gao, Tianji; Le, TrungHieu; Yang, Ying; Yu, Zhihao; Huang, Zhenghong; Kang, Feiyu

2017-01-01

Two different interlayers were introduced in lithium–sulfur batteries to improve the cycling stability with sulfur loading as high as 80% of total mass of cathode. Melamine was recommended as a nitrogen-rich (N-rich) amine component to synthesize a modified polyacrylic acid (MPAA). The electrospun MPAA was carbonized into N-rich carbon nanofibers, which were used as cathode interlayers, while carbon nanofibers from PAA without melamine was used as an anode interlayer. At the rate of 0.1 C, the initial discharge capacity with two interlayers was 983 mAh g−1, and faded down to 651 mAh g−1 after 100 cycles with the coulombic efficiency of 95.4%. At the rate of 1 C, the discharge capacity was kept to 380 mAh g−1 after 600 cycles with a coulombic efficiency of 98.8%. It apparently demonstrated that the cathode interlayer is extremely effective at shutting down the migration of polysulfide ions. The anode interlayer induced the lithium ions to form uniform lithium metal deposits confined on the fiber surface and in the bulk to strengthen the cycling stability of the lithium metal anode. PMID:28772731

Graphene-doped electrospun nanofiber membrane electrodes and proton exchange membrane fuel cell performance

NASA Astrophysics Data System (ADS)

Wei, Meng; Jiang, Min; Liu, Xiaobo; Wang, Min; Mu, Shichun

2016-09-01

A rational electrode structure can allow proton exchange membrane (PEM) fuel cells own high performance with a low noble metal loading and an optimal transport pathway for reaction species. In this study, we develop a graphene doped polyacrylonitile (PAN)/polyvinylident fluoride (PVDF) (GPP) electrospun nanofiber electrode with improved electrical conductivity and high porosity, which could enhance the triple reaction boundary and promote gas and water transport throughout the porous electrode. Thus the increased electrochemical active surface area (ECSA) of Pt catalysts and fuel cell performance can be expected. As results, the ECSA of hot-pressed electrospun electrodes with 2 wt% graphene oxide (GO) is up to 84.3 m2/g, which is greatly larger than that of the conventional electrode (59.5 m2/g). Significantly, the GPP nanofiber electrospun electrode with Pt loading of 0.2 mg/cm2 exhibits higher fuel cell voltage output and stability than the conventional electrode.

Continuous micron-scaled rope engineering using a rotating multi-nozzle electrospinning emitter

NASA Astrophysics Data System (ADS)

Zhang, Chunchen; Gao, Chengcheng; Chang, Ming-Wei; Ahmad, Zeeshan; Li, Jing-Song

2016-10-01

Electrospinning (ES) enables simple production of fibers for broad applications (e.g., biomedical engineering, energy storage, and electronics). However, resulting structures are predominantly random; displaying significant disordered fiber entanglement, which inevitably gives rise to structural variations and reproducibility on the micron scale. Surface and structural features on this scale are critical for biomaterials, tissue engineering, and pharmaceutical sciences. In this letter, a modified ES technique using a rotating multi-nozzle emitter is developed and utilized to fabricate continuous micron-scaled polycaprolactone (PCL) ropes, providing control on fiber intercalation (twist) and structural order. Micron-scaled ropes comprising 312 twists per millimeter are generated, and rope diameter and pitch length are regulated using polymer concentration and process parameters. Electric field simulations confirm vector and distribution mechanisms, which influence fiber orientation and deposition during the process. The modified fabrication system provides much needed control on reproducibility and fiber entanglement which is crucial for electrospun biomedical materials.

Electrospun polylactic acid and polyvinyl alcohol fibers as efficient and stable nanomaterials for immobilization of lipases.

PubMed

Sóti, Péter Lajos; Weiser, Diana; Vigh, Tamás; Nagy, Zsombor Kristóf; Poppe, László; Marosi, György

2016-03-01

Electrospinning was applied to create easy-to-handle and high-surface-area membranes from continuous nanofibers of polyvinyl alcohol (PVA) or polylactic acid (PLA). Lipase PS from Burkholderia cepacia and Lipase B from Candida antarctica (CaLB) could be immobilized effectively by adsorption onto the fibrous material as well as by entrapment within the electrospun nanofibers. The biocatalytic performance of the resulting membrane biocatalysts was evaluated in the kinetic resolution of racemic 1-phenylethanol (rac-1) and 1-phenylethyl acetate (rac-2). Fine dispersion of the enzymes in the polymer matrix and large surface area of the nanofibers resulted in an enormous increase in the activity of the membrane biocatalyst compared to the non-immobilized crude powder forms of the lipases. PLA as fiber-forming polymer for lipase immobilization performed better than PVA in all aspects. Recycling studies with the various forms of electrospun membrane biocatalysts in ten cycles of the acylation and hydrolysis reactions indicated excellent stability of this forms of immobilized lipases. PLA-entrapped lipases could preserve lipase activity and enantiomer selectivity much better than the PVA-entrapped forms. The electrospun membrane forms of CaLB showed high mechanical stability in the repeated acylations and hydrolyses than commercial forms of CaLB immobilized on polyacrylamide beads (Novozyme 435 and IMMCALB-T2-150).

Towards 4th generation biomaterials: a covalent hybrid polymer-ormoglass architecture

NASA Astrophysics Data System (ADS)

Sachot, N.; Mateos-Timoneda, M. A.; Planell, J. A.; Velders, A. H.; Lewandowska, M.; Engel, E.; Castaño, O.

2015-09-01

Hybrid materials are being extensively investigated with the aim of mimicking the ECM microenvironment to develop effective solutions for bone tissue engineering. However, the common drawbacks of a hybrid material are the lack of interactions between the scaffold's constituents and the masking of its bioactive phase. Conventional hybrids often degrade in a non-homogeneous manner and the biological response is far from optimal. We have developed a novel material with strong interactions between constituents. The bioactive phase is directly exposed on its surface mimicking the structure of the ECM of bone. Here, polylactic acid electrospun fibers have been successfully and reproducibly coated with a bioactive organically modified glass (ormoglass, Si-Ca-P2 system) covalently. In comparison with the pure polymeric mats, the fibers obtained showed improved hydrophilicity and mechanical properties, bioactive ion release, exhibited a nanoroughness and enabled good cell adhesion and spreading after just one day of culture (rMSCs and rEPCs). The fibers were coated with different ormoglass compositions to tailor their surface properties (roughness, stiffness, and morphology) by modifying the experimental parameters. Knowing that cells modulate their behavior according to the exposed physical and chemical signals, the development of this instructive material is a valuable advance in the design of functional regenerative biomaterials.Hybrid materials are being extensively investigated with the aim of mimicking the ECM microenvironment to develop effective solutions for bone tissue engineering. However, the common drawbacks of a hybrid material are the lack of interactions between the scaffold's constituents and the masking of its bioactive phase. Conventional hybrids often degrade in a non-homogeneous manner and the biological response is far from optimal. We have developed a novel material with strong interactions between constituents. The bioactive phase is directly exposed on its surface mimicking the structure of the ECM of bone. Here, polylactic acid electrospun fibers have been successfully and reproducibly coated with a bioactive organically modified glass (ormoglass, Si-Ca-P2 system) covalently. In comparison with the pure polymeric mats, the fibers obtained showed improved hydrophilicity and mechanical properties, bioactive ion release, exhibited a nanoroughness and enabled good cell adhesion and spreading after just one day of culture (rMSCs and rEPCs). The fibers were coated with different ormoglass compositions to tailor their surface properties (roughness, stiffness, and morphology) by modifying the experimental parameters. Knowing that cells modulate their behavior according to the exposed physical and chemical signals, the development of this instructive material is a valuable advance in the design of functional regenerative biomaterials. Electronic supplementary information (ESI) available. See DOI: 10.1039/c5nr04275e

The effect of chemically modified electrospun silica nanofiber on the mRNA and miRNA expression profile of neural stem cell differentiation.

PubMed

Mercado, Augustus T; Yeh, Jui-Ming; Chin, Ting Yu; Chen, Wen Shuo; Chen-Yang, Yui Whei; Chen, Chung-Yung

2016-11-01

A detailed genomic and epigenomic analyses of neural stem cells (NSCs) differentiation in synthetic microenvironments is essential for the advancement of regenerative medicine and therapeutic treatment of diseases. This study identified the changes in mRNA and miRNA expression profile during NSC differentiation on an artificial matrix. NSCs were grown on a surface-modified, electrospun tetraethyl-orthosilicate nanofiber (designated as SNF-AP) by providing a 3D-environment for cell growth and differentiation. Differentially expressed mRNAs and miRNAs of NSC differentiated in this microenvironment were identified through microarray analysis. The genes and miRNA targets responsible for the differentiation fate of NSCs and neuron development process were determined using Ingenuity Pathway Analysis (IPA). SNF-AP enhanced the expression of genes that activates the proliferation, development, and outgrowth of neurons, differentiation and generation of cells, neuritogenesis, outgrowth of neurites, microtubule dynamics, formation of cellular protrusions, and long-term potentiation during NSC differentiation. On the other hand, PDL inhibited neuritogenesis, microtubule dynamics, and proliferation and differentiation of cells and activated the apoptosis function. Moreover, the nanomaterial promoted the expression of more let-7 miRNAs, which have vital roles in NSC differentiation. Overall, SNF-AP is biocompatible and applicable scaffold for NSC differentiation in the development of neural tissue engineering. These findings are useful in enhancing in vitro NSC differentiation potential for preclinical studies and future clinical applications. © 2016 Wiley Periodicals, Inc. J Biomed Mater Res Part A: 104A: 2730-2743, 2016. © 2016 Wiley Periodicals, Inc.

Surface-assisted laser desorption/ionization time-of-flight mass spectrometry of small drug molecules and high molecular weight synthetic/biological polymers using electrospun composite nanofibers.

PubMed

Bian, Juan; Olesik, Susan V

2017-03-27

Polyacrylonitrile/Nafion®/carbon nanotube (PAN/Nafion®/CNT) composite nanofibers were prepared using electrospinning. These electrospun nanofibers were studied as possible substrates for surface-assisted laser desorption/ionization (SALDI) and matrix-enhanced surface-assisted laser desorption/ionization time-of-flight mass spectrometry (ME-SALDI/TOF-MS) for the first time in this paper. Electrospinning provides this novel substrate with a uniform morphology and a narrow size distribution, where CNTs were evenly and firmly immobilized on polymeric nanofibers. The results show that PAN/Nafion®/CNT nanofibrous mats are good substrates for the analysis of both small drug molecules and high molecular weight polymers with high sensitivity. Markedly improved reproducibility was observed relative to MALDI. Due to the composite formation between the polymers and the CNTs, no contamination of the carbon nanotubes to the mass spectrometer was observed. Furthermore, electrospun nanofibers used as SALDI substrates greatly extended the duration of ion signals of target analytes compared to the MALDI matrix. The proposed SALDI approach was successfully used to quantify small drug molecules with no interference in the low mass range. The results show that verapamil could be detected with a surface concentration of 220 femtomoles, indicating the high detection sensitivity of this method. Analysis of peptides and proteins with the electrospun composite substrate using matrix assisted-SALDI was improved and a low limit of detection of approximately 6 femtomoles was obtained for IgG. Both SALDI and ME-SALDI analyses displayed high reproducibility with %RSD ≤ 9% for small drug molecules and %RSD ≤ 14% for synthetic polymers and proteins.

Structure and physico-mechanical properties of low temperature plasma treated electrospun nanofibrous scaffolds examined with atomic force microscopy.

PubMed

Chlanda, Adrian; Kijeńska, Ewa; Rinoldi, Chiara; Tarnowski, Michał; Wierzchoń, Tadeusz; Swieszkowski, Wojciech

2018-04-01

Electrospun nanofibrous scaffolds are willingly used in tissue engineering applications due to their tunable mechanical, chemical and physical properties. Additionally, their complex openworked architecture is similar to the native extracellular matrix of living tissue. After implantation such scaffolds should provide sufficient mechanical support for cells. Moreover, it is of crucial importance to ensure sterility and hydrophilicity of the scaffold. For this purpose, a low temperature surface plasma treatment can be applied. In this paper, we report physico-mechanical evaluation of stiffness and adhesive properties of electrospun mats after their exposition to low temperature plasma. Complex morphological and mechanical studies performed with an atomic force microscope were followed by scanning electron microscope imaging and a wettability assessment. The results suggest that plasma treatment can be a useful method for the modification of the surface of polymeric scaffolds in a desirable manner. Plasma treatment improves wettability of the polymeric mats without changing their morphology. Copyright © 2018 Elsevier Ltd. All rights reserved.

Immobilization of Heparan Sulfate on Electrospun Meshes to Support Embryonic Stem Cell Culture and Differentiation*

PubMed Central

Meade, Kate A.; White, Kathryn J.; Pickford, Claire E.; Holley, Rebecca J.; Marson, Andrew; Tillotson, Donna; van Kuppevelt, Toin H.; Whittle, Jason D.; Day, Anthony J.; Merry, Catherine L. R.

2013-01-01

As our understanding of what guides the behavior of multi- and pluripotent stem cells deepens, so too does our ability to utilize certain cues to manipulate their behavior and maximize their therapeutic potential. Engineered, biologically functionalized materials have the capacity to influence stem cell behavior through a powerful combination of biological, mechanical, and topographical cues. Here, we present the development of a novel electrospun scaffold, functionalized with glycosaminoglycans (GAGs) ionically immobilized onto the fiber surface. Bound GAGs retained the ability to interact with GAG-binding molecules and, crucially, presented GAG sulfation motifs fundamental to mediating stem cell behavior. Bound GAG proved to be biologically active, rescuing the neural differentiation capacity of heparan sulfate-deficient mouse embryonic stem cells and functioning in concert with FGF4 to facilitate the formation of extensive neural processes across the scaffold surface. The combination of GAGs with electrospun scaffolds creates a biomaterial with potent applicability for the propagation and effective differentiation of pluripotent stem cells. PMID:23235146

Immobilization of heparan sulfate on electrospun meshes to support embryonic stem cell culture and differentiation.

PubMed

Meade, Kate A; White, Kathryn J; Pickford, Claire E; Holley, Rebecca J; Marson, Andrew; Tillotson, Donna; van Kuppevelt, Toin H; Whittle, Jason D; Day, Anthony J; Merry, Catherine L R

2013-02-22

As our understanding of what guides the behavior of multi- and pluripotent stem cells deepens, so too does our ability to utilize certain cues to manipulate their behavior and maximize their therapeutic potential. Engineered, biologically functionalized materials have the capacity to influence stem cell behavior through a powerful combination of biological, mechanical, and topographical cues. Here, we present the development of a novel electrospun scaffold, functionalized with glycosaminoglycans (GAGs) ionically immobilized onto the fiber surface. Bound GAGs retained the ability to interact with GAG-binding molecules and, crucially, presented GAG sulfation motifs fundamental to mediating stem cell behavior. Bound GAG proved to be biologically active, rescuing the neural differentiation capacity of heparan sulfate-deficient mouse embryonic stem cells and functioning in concert with FGF4 to facilitate the formation of extensive neural processes across the scaffold surface. The combination of GAGs with electrospun scaffolds creates a biomaterial with potent applicability for the propagation and effective differentiation of pluripotent stem cells.

The deposition of thin titanium-nitrogen coatings on the surface of PCL-based scaffolds for vascular tissue engineering

NASA Astrophysics Data System (ADS)

Kudryavtseva, Valeriya; Stankevich, Ksenia; Kibler, Elina; Golovkin, Alexey; Mishanin, Alexander; Bolbasov, Evgeny; Choynzonov, Evgeny; Tverdokhlebov, Sergei

2018-04-01

Biodegradable polymer scaffolds for tissue engineering is a promising technology for therapies of patients suffering from the loss of tissue or its function including cardiac tissues. However, limitations such as hydrophobicity of polymers prevent cell attachment, cell conductivity, and endothelialization. Plasma modification of polymers allows producing materials for an impressive range of applications due to their unique properties. Here, we demonstrate the possibility of bioresorbable electrospun polycaprolacton (PCL) scaffold surface modification by reactive magnetron sputtering of the titanium target in a nitrogen atmosphere. The influence of the plasma treatment time on the structure and properties of electrospun PCL scaffolds was studied. We show that the plasma treatment does not change the physico-mechanical properties of electrospun PCL scaffolds, leads to an increase in PCL scaffold biocompatibility, and, simultaneously, increases their hydrophilicity. In conclusion, this modification method opens a route to producing scaffolds with enhanced biocompatibility for tissue engineered vascular grafts.

Improvement of Polylactide Properties through Cellulose Nanocrystals Embedded in Poly(Vinyl Alcohol) Electrospun Nanofibers.

PubMed

López de Dicastillo, Carol; Garrido, Luan; Alvarado, Nancy; Romero, Julio; Palma, Juan Luis; Galotto, Maria Jose

2017-05-11

Electrospun nanofibers of poly (vinyl alcohol) (PV) were obtained to improve dispersion of cellulose nanocrystals (CNC) within hydrophobic biopolymeric matrices, such as poly(lactic acid) (PLA). Electrospun nanofibers (PV/CNC) n were successfully obtained with a final concentration of 23% ( w / w ) of CNC. Morphological, structural and thermal properties of developed CNC and electrospun nanofibers were characterized. X-ray diffraction and thermal analysis revealed that the crystallinity of PV was reduced by the electrospinning process, and the incorporation of CNC increased the thermal stability of biodegradable nanofibers. Interactions between CNC and PV polymer also enhanced the thermal stability of CNC and improved the dispersion of CNC within the PLA matrix. PLA materials with CNC lyophilized were also casted in order to compare the properties with materials based on CNC containing nanofibers. Nanofibers and CNC were incorporated into PLA at three concentrations: 0.5%, 1% and 3% (CNC respect to polymer weight) and nanocomposites were fully characterized. Overall, nanofibers containing CNC positively modified the physical properties of PLA materials, such as the crystallinity degree of PLA which was greatly enhanced. Specifically, materials with 1% nanofiber 1PLA(PV/CNC) n presented highest improvements related to mechanical and barrier properties; elongation at break was enhanced almost four times and the permeation of oxygen was reduced by approximately 30%.

Effect of Voltage and Flow Rate Electrospinning Parameters on Polyacrylonitrile Electrospun Fibers

NASA Astrophysics Data System (ADS)

Bakar, S. S. S.; Fong, K. C.; Eleyas, A.; Nazeri, M. F. M.

2018-03-01

Currently, electrospinning is a very famous technique and widely used for forming polymer nanofibers. In this paper, the Polyacrylonitrile (PAN) nanofibers were prepared in concentration of 10wt% with varied processing parameters that can affect the properties of PAN fiber in term of fiber diameter and electrical conductivity was presented. Voltage of 10, 15 and 20 kV with PAN flow rate of 1 electrospun PAN fibers were then undergo pyrolysis at 800°C for 30 minutes. The resultant PAN nanofibers were then analysed by SEM, XRD and four point probe test after pyrolysis process. SEM image show continuos uniform and smooth surface fibrous structure of electrospun PAN fibers with average diameter of 1.81 μm. The fiber morphology is controlled by manipulating the processing parameters of electrospinning process. The results showed that the resistance of electrospun PAN fibers decreases as the processing parameter changes by increasing the applied voltage and flow rate of electrospinning.

Electrospun carbon nanofibers surface-grafted with vapor-grown carbon nanotubes as hierarchical electrodes for supercapacitors

NASA Astrophysics Data System (ADS)

Zhou, Zhengping; Wu, Xiang-Fa; Fong, Hao

2012-01-01

This letter reports the fabrication and electrochemical properties of electrospun carbon nanofibers surface-grafted with vapor-grown carbon nanotubes (CNTs) as hierarchical electrodes for supercapacitors. The specific capacitance of the fabricated electrodes was measured up to 185 F/g at the low discharge current density of 625 mA/g; a decrease of 38% was detected at the high discharge current density of 2.5 A/g. The morphology and microstructure of the electrodes were examined by electron microscopy, and the unique connectivity of the hybrid nanomaterials was responsible for the high specific capacitance and low intrinsic contact electric resistance of the hierarchical electrodes.

Process parameter and surface morphology of pineapple leaf electrospun nanofibers (PALF)

NASA Astrophysics Data System (ADS)

Surip, S. N.; Aziz, F. M. A.; Bonnia, N. N.; Sekak, K. A.; Zakaria, M. N.

2017-09-01

In recent times, nanofibers have attracted the attention of researchers due to their pronounced micro and nano structural characteristics that enable the development of advanced materials that have sophisticated applications. The production of nanofibers by the electrospinning process is influenced both by the electrostatic forces and the viscoelastic behavior of the polymer. Process parameters, like solution feed rate, applied voltage, nozzle-collector distance, and spinning environment, and material properties, like solution concentration, viscosity, surface tension, conductivity, and solvent vapor pressure, influence the structure and properties of electrospun nanofibers. Significant work has been done to characterize the properties of PALF nanofibers as a function of process and material parameters.

Production of Conductive PEDOT-Coated PVA-GO Composite Nanofibers

NASA Astrophysics Data System (ADS)

Zubair, Nur Afifah; Rahman, Norizah Abdul; Lim, Hong Ngee; Sulaiman, Yusran

2017-02-01

Electrically conductive nanofiber is well known as an excellent nanostructured material for its outstanding performances. In this work, poly(3,4-ethylenedioxythiophene) (PEDOT)-coated polyvinyl alcohol-graphene oxide (PVA-GO)-conducting nanofibers were fabricated via a combined method using electrospinning and electropolymerization techniques. During electrospinning, the concentration of PVA-GO solution and the applied voltage were deliberately altered in order to determine the optimized electrospinning conditions. The optimized parameters obtained were 0.1 mg/mL of GO concentration with electrospinning voltage of 15 kV, which displayed smooth nanofibrous morphology and smaller diameter distribution. The electrospun PVA-GO nanofiber mats were further modified by coating with the conjugated polymer, PEDOT, using electropolymerization technique which is a facile approach for coating the nanofibers. SEM images of the obtained nanofibers indicated that cauliflower-like structures of PEDOT were successfully grown on the surface of the electrospun nanofibers during the potentiostatic mode of the electropolymerization process. The conductive nature of PEDOT coating strongly depends on the different electropolymerization parameters, resulting in good conductivity of PEDOT-coated nanofibers. The optimum electropolymerization of PEDOT was at a potential of 1.2 V in 5 min. The electrochemical measurements demonstrated that the fabricated PVA-GO/PEDOT composite nanofiber could enhance the current response and reduce the charge transfer resistance of the nanofiber.

Poly(amidoamine) dendrimer-enabled simultaneous stabilization and functionalization of electrospun poly(γ-glutamic acid) nanofibers.

PubMed

Wang, Shige; Zhu, Jingyi; Shen, Mingwu; Zhu, Meifang; Shi, Xiangyang

2014-02-12

We report a facile and general approach to using generation 2 (G2) poly(amidoamine) (PAMAM) dendrimers for simultaneous stabilization and functionalization of electrospun poly(γ-glutamic acid) nanofibers (γ-PGA NFs). In this study, uniform γ-PGA NFs with a smooth morphology were generated using electrospinning technology. In order to endow the NFs with good water stability, amine-terminated G2.NH2 PAMAM dendrimers were utilized to crosslink the γ-PGA NFs via 1-ethyl-3-(3-dimethylami-nopropyl) carbodiimide coupling chemistry. Under the optimized crosslinking conditions, G2.NH2 dendrimers partially modified with fluorescein isothiocyanate (FI) or folic acid (FA) were used to crosslink γ-PGA NFs. Our results reveal that G2.NH2-FI is able to simultaneously render the NFs with good water stability and fluorescence property, while G2.NH2-FA is able to simultaneously endow the NFs with water stability and the ability to capture FA receptor-overexpressing cancer cells in vitro via ligand-receptor interaction. With the tunable dendrimer surface chemistry, multifunctional water-stable γ-PGA-based NFs may be generated via a dendrimer crosslinking approach, thereby providing diverse applications in the areas of biosensing, tissue engineering, drug delivery, and environmental sciences.

Long-term drug release from electrospun fibers for in vivo inflammation prevention in the prevention of peritendinous adhesions.

PubMed

Hu, Changmin; Liu, Shen; Zhang, Yang; Li, Bin; Yang, Huilin; Fan, Cunyi; Cui, Wenguo

2013-07-01

Physical barriers such as electrospun fibrous membranes are potentially useful in preventing peritendinous adhesions after surgery. However, inflammatory responses caused by degradation of barrier materials remain a major challenge. This study aimed to fabricate electrospun composite fibrous membranes based on drug-loaded modified mesoporous silica (MMS) and poly (l-lactic acid) (PLLA). Using a co-solvent-based electrospinning method ibuprofen (IBU)-loaded MMS was successfully and uniformly encapsulated in the PLLA fibers. The electrospun PLLA-MMS-IBU composite fibrous membranes showed significantly lower initial burst release (6% release in the first 12h) compared with that of electrospun PLLA-IBU fibrous membranes (46% release in the first 12h) in in vitro release tests. Moreover, the release from PLLA-MMS-IBU was also for significantly longer than that from PLLA-IBU (100 vs. 20days). In animal studies both PLLA-IBU and PLLA-MMS-IBU showed improved anti-adhesion properties and anti-inflammatory effects compared with PLLA fibrous membrane alone 4weeks after implantation. Further, animals implanted with PLLA-MMS-IBU for 8weeks showed the lowest inflammation and best recovery compared with those implanted with PLLA-IBU and PLLA, most likely as a result of its long-term IBU release profile. Therefore, this study provides a platform technique for fabricating fibrous membranes with long-term sustained drug release characteristics which may function as a novel carrier for long-term anti-inflammation and anti-adhesion to prevent peritendinous adhesions. Copyright © 2013 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

Fabricating Superhydrophobic Polymeric Materials for Biomedical Applications

PubMed Central

Kaplan, Jonah; Grinstaff, Mark

2015-01-01

Superhydrophobic materials, with surfaces possessing permanent or metastable non-wetted states, are of interest for a number of biomedical and industrial applications. Here we describe how electrospinning or electrospraying a polymer mixture containing a biodegradable, biocompatible aliphatic polyester (e.g., polycaprolactone and poly(lactide-co-glycolide)), as the major component, doped with a hydrophobic copolymer composed of the polyester and a stearate-modified poly(glycerol carbonate) affords a superhydrophobic biomaterial. The fabrication techniques of electrospinning or electrospraying provide the enhanced surface roughness and porosity on and within the fibers or the particles, respectively. The use of a low surface energy copolymer dopant that blends with the polyester and can be stably electrospun or electrosprayed affords these superhydrophobic materials. Important parameters such as fiber size, copolymer dopant composition and/or concentration, and their effects on wettability are discussed. This combination of polymer chemistry and process engineering affords a versatile approach to develop application-specific materials using scalable techniques, which are likely generalizable to a wider class of polymers for a variety of applications. PMID:26383018

High flux nanofiltration membranes based on layer-by-layer assembly modified electrospun nanofibrous substrate

NASA Astrophysics Data System (ADS)

Xu, Guo-Rong; Liu, Xiao-Yu; Xu, Jian-Mei; Li, Lu; Su, Hui-Chao; Zhao, He-Li; Feng, Hou-Jun

2018-03-01

Herein, high flux nanofiltration (NF) membranes were fabricated by combined procedures of electrospinning, layer-by-layer (LBL) assembly, and phase inversion. The membranes displayed three-dual structure constituted polyether sulfone (PES) coating layer, LBL assembly modified electrospun polyester (PET) nanofibrous mats, and non-woven supports. High flux NF membranes thus prepared are characterized by ultrathin phase inversion layer (∼10 μm) while that of conventional membranes are 100-150 μm, implying that very high flux could be expected. Various factors including electrospinning conditions, chitosan (CHI)/alginate (ALG) concentration, PES concentration, exposed time, coagulating temperature, thermal treatment, and sulfonated poly ether ketone (SPEEK) content were systematically investigated. Structures of the membranes were characterized by field emission scanning electron microscopy (FESEM), mechanical properties test, Fourier transform infrared spectroscopy (FTIR), nuclear magnetic resonance (NMR) and static contact angle measurements. The separation experiments indicated that thus prepared membranes exhibited high flux of as high as ∼75 L m-2 h-1 with Mg SO4 rejection of ∼80%.

Polycaprolactone electrospun mesh conjugated with an MSC affinity peptide for MSC homing in vivo.

PubMed

Shao, Zhenxing; Zhang, Xin; Pi, Yanbin; Wang, Xiaokun; Jia, Zhuqing; Zhu, Jingxian; Dai, Linghui; Chen, Wenqing; Yin, Ling; Chen, Haifeng; Zhou, Chunyan; Ao, Yingfang

2012-04-01

Mesenchymal stem cell (MSC) is a promising cell source candidate in tissue engineering (TE) and regenerative medicine. However, the inability to target MSCs in tissues of interest with high efficiency and engraftment has become a significant barrier for MSC-based therapies. The mobilization and transfer of MSCs to defective/damaged sites in tissues or organs in vivo with high efficacy and efficiency has been a major concern. In the present study, we identified a peptide sequence (E7) with seven amino acids through phage display technology, which has a high specific affinity to bone marrow-derived MSCs. Subsequent analysis suggested that the peptide could efficiently interact specifically with MSCs without any species specificity. Thereafter, E7 was covalently conjugated onto polycaprolactone (PCL) electrospun meshes to construct an "MSC-homing device" for the recruitment of MSCs both in vitro and in vivo. The E7-conjugated PCL electrospun meshes were implanted into a cartilage defect site of rat knee joints, combined with a microfracture procedure to mobilize the endogenous MSCs. After 7 d of implantation, immunofluorescence staining showed that the cells grown into the E7-conjugated PCL electrospun meshes yielded a high positive rate for specific MSC surface markers (CD44, CD90, and CD105) compared with those in arginine-glycine-aspartic acid (RGD)-conjugated PCL electrospun meshes (63.67% vs. 3.03%; 59.37% vs. 2.98%; and 61.45% vs. 3.82%, respectively). Furthermore, the percentage of CD68 positive cells in the E7-conjugated PCL electrospun meshes was much lower than that in the RGD-conjugated PCL electrospun meshes (5.57% vs. 53.43%). This result indicates that E7-conjugated PCL electrospun meshes absorb much less inflammatory cells in vivo than RGD-conjugated PCL electrospun meshes. The results of the present study suggest that the identified E7 peptide sequence has a high specific affinity to MSCs. Covalently conjugating this peptide on the synthetic PCL mesh significantly enhanced the MSC recruitment of PCL in vivo. This method provides a wide range of potential applications in TE. Copyright © 2012 Elsevier Ltd. All rights reserved.

Comparative of fibroblast and osteoblast cells adhesion on surface modified nanofibrous substrates based on polycaprolactone.

PubMed

Sharifi, Fereshteh; Irani, Shiva; Zandi, Mojgan; Soleimani, Masoud; Atyabi, Seyed Mohammad

2016-12-01

One of the determinant factors for successful bioengineering is to achieve appropriate nano-topography and three-dimensional substrate. In this research, polycaprolactone (PCL) nano-fibrous mat with different roughness modified with O 2 plasma was fabricated via electrospinning. The purpose of this study was to evaluate the effect of plasma modification along with surface nano-topography of mats on the quality of human fibroblast (HDFs) and osteoblast cells (OSTs)-substrate interaction. Surface properties were studied using scanning electron microscopy (SEM), atomic force microscopy (AFM), contact angle, Fourier-transformation infrared spectroscopy. We evaluated mechanical properties of fabricated mats by tensile test. The viability and proliferation of HDFs and OSTs on the substrates were followed by 3-[4, 5-dimethylthiazol-2-yl]-2, 5-diphenyltetrazolium bromide (MTT). Mineralization of the substrate was determined by alizarin red staining method and calcium content of OSTs was determined by calcium content kit. Cells morphology was studied by SEM analysis. The results revealed that the plasma-treated electrospun nano-fibrous substrate with higher roughness was an excellent designed substrate. A bioactive topography for stimulating proliferation of HDFs and OSTs is to accelerate the latter's differentiation time. Therefore, the PCL substrate with high density and major nano-topography were considered as a bio-functional and elegant bio-substrate for tissue regeneration applications.

Electrospun Fibro-porous Polyurethane Coatings for Implantable Glucose Biosensors

PubMed Central

Wang, Ning; Burugapalli, Krishna; Song, Wenhui; Halls, Justin; Moussy, Francis; Ray, Asim; Zheng, Yudong

2012-01-01

This study reports methods for coating miniature implantable glucose biosensors with electrospun polyurethane (PU) membranes, their effects on sensor function and efficacy as mass-transport limiting membranes. For electrospinning fibres directly on sensor surface, both static and dynamic collector systems, were designed and tested. Optimum collector configurations were first ascertained by FEA modelling. Both static and dynamic collectors allowed complete covering of sensors, but it was the dynamic collector that produced uniform fibro-porous PU coatings around miniature ellipsoid biosensors. The coatings had random fibre orientation and their uniform thickness increased linearly with increasing electrospinning time. The effects of coatings having an even spread of submicron fibre diameters and sub-100μm thicknesses on glucose biosensor function were investigated. Increasing thickness and fibre diameters caused a statistically insignificant decrease in sensor sensitivity for the tested electrospun coatings. The sensors’ linearity for the glucose detection range of 2 to 30mM remained unaffected. The electrospun coatings also functioned as mass-transport limiting membranes by significantly increasing the linearity, replacing traditional epoxy-PU outer coating. To conclude, electrospun coatings, having controllable fibro-porous structure and thicknesses, on miniature ellipsoid glucose biosensors were demonstrated to have minimal effect on pre-implantation sensitivity and also to have mass-transport limiting ability. PMID:23146433

Electrospun nanofiber membranes for adsorption of dye molecules from textile wastewater

NASA Astrophysics Data System (ADS)

Akduman, C.; Akçakoca Kumbasar, E. P.; Morsunbul, S.

2017-10-01

The nanofiber membranes prepared by the electrospinning method have unique properties such as high specific surface area and high porosity with fine pores. These properties led electrospun nanofiber membranes to use for the removal of dye molecules from textile wastewater. In this study, a hydrophobic Thermoplastic Polyurethane (TPU) and a hydrophilic Poly (vinyl alcohol) (PVA) were selected for producing electrospun nanofibers and their sorption capacities were investigated. The largest sorption capacity reached to maximum 88.31 mg/g, belong to BTCA cross-linked PVA membranes due to hydrophilic character of PVA. Contrary to expectation, hydrophobic character of TPU was dominant and incorporation of CD to the TPU nanofibers did not affect the sorption of the TPU membranes, and showed very low adsorption capacity (14.48 mg/g).

Electrospun fiber surface nanotopography influences astrocyte-mediated neurite outgrowth.

PubMed

Johnson, Christopher D; D'Amato, Anthony R; Puhl, Devan L; Wich, Douglas M; Vespermann, Amanda; Gilbert, Ryan J

2018-05-15

Aligned, electrospun fiber scaffolds provide topographical guidance for regenerating neurons and glia after central nervous system injury. To date, no study has explored how fiber surface nanotopography affects astrocyte response to fibrous scaffolds. Astrocytes play important roles in the glial scar, the blood brain barrier, and in maintaining homeostasis in the central nervous system. In this study, electrospun poly L-lactic acid fibers were engineered with smooth, pitted, or divoted surface nanotopography. Cortical or spinal cord primary rat astrocytes were cultured on the surfaces for either 1 or 3 days to examine the astrocyte response over time. The results showed that cortical astrocytes were significantly shorter and broader on the pitted and divoted fibers compared to those on smooth fibers. However, spinal cord astrocyte morphology was not significantly altered by the surface features. These findings indicate that astrocytes from unique anatomical locations respond differently to the presence of nanotopography. Western Blot results show that the differences in morphology were not associated with significant changes in GFAP or vinculin in either astrocyte population, suggesting that surface pits and divots do not induce a reactive phenotype in either cortical or spinal cord astrocytes. Finally, astrocytes were co-cultured with dorsal root ganglia to determine how the surfaces affected astrocyte-mediated neurite outgrowth. Astrocytes cultured on the fibers for shorter periods of time (1 day) generally supported longer neurite outgrowth. Pitted and divoted fibers restricted spinal cord astrocyte-mediated neurite outgrowth, while smooth fibers increased 3 day spinal cord astrocyte-mediated neurite outgrowth. In total, fiber surface nanotopography can influence astrocyte elongation and influence the capability of astrocytes to direct neurites. Therefore, fiber surface characteristics should be carefully controlled to optimize astrocyte-mediated axonal regeneration. . © 2018 IOP Publishing Ltd.

Electrospinning of Polyvinylidene Fluoride and Polyetherimide From Mixed Solvents

NASA Technical Reports Server (NTRS)

Morgret, Leslie D.; Pawlowski, Kristin J.; Hinkley, Jeffrey A.

2005-01-01

Polyvinylidene fluoride and Ultem(TradeMark) polyetherimide were dissolved in 50/50 acetone/N,N dimethylformamide (DMF) and 80/20 tetrahydrofuran/DMF, respectively, and electrospun. Polymer solution concentrations and molecular weights were changed while other spinning parameters (voltage, distance, solution feed rate) were held constant. Fiber diameters in the resulting electrospun mats varied from 0.25 to 4.4 microns, increasing with polymer concentration and molecular weight; trends in diameter were compared with trends in viscosities and surface tensions of the spinning solutions.

Electrospinning bioactive supramolecular polymers from water.

PubMed

Tayi, Alok S; Pashuck, E Thomas; Newcomb, Christina J; McClendon, Mark T; Stupp, Samuel I

2014-04-14

Electrospinning is a high-throughput, low-cost technique for manufacturing long fibers from solution. Conventionally, this technique is used with covalent polymers with large molecular weights. We report here the electrospinning of functional peptide-based supramolecular polymers from water at very low concentrations (<4 wt %). Molecules with low molecular weights (<1 kDa) could be electrospun because they self-assembled into one-dimensional supramolecular polymers upon solvation and the critical parameters of viscosity, solution conductivity, and surface tension were optimized for this technique. The supramolecular structure of the electrospun fibers could ensure that certain residues, like bioepitopes, are displayed on the surface even after processing. This system provides an opportunity to electrospin bioactive supramolecular materials from water for biomedical applications.

Polymer based nanocomposites with nanofibers and exfoliated clay

NASA Technical Reports Server (NTRS)

Meador, Michael A.; Reneker, Darrell H.

2005-01-01

Polymer solutions, containing clay sheets, were electrospun into nanofibers and microfibers that contained clay sheets inside. Controllable removal of polymer by plasma etching from the surface of fibers revealed the arrangement of clay. The shape, flexibility, size distribution and arrangement of clay sheets were observed by transmission and scanning electron microscopy. The clay sheets were partially aligned in big fibers with normal direction of clay sheets perpendicular to fiber axis. Crumpling of clay sheets inside fibers was observed when the fiber diameter was comparable to the lateral size of clay sheets. Single sheets of clay were observed both by catching clay sheets dispersed in water with electrospun nanofiber mats and by the deliberate removal of most of the polymer in the fibers. Thin, flexible gas barrier films, that are reasonably strong, were assembled from clay sheets and polymer nanofibers. Structure of composite films was characterized with scanning electron microscopy. Continuous film of clay sheets were physically attached to the surface of fiber mats. Spincoating film of polymer and clay sheets was reinforced by electrospun fiber scaffold. Certain alignment of clay sheets was observed in the vicinity of fibers.

Improvement of Polylactide Properties through Cellulose Nanocrystals Embedded in Poly(Vinyl Alcohol) Electrospun Nanofibers

PubMed Central

López de Dicastillo, Carol; Garrido, Luan; Alvarado, Nancy; Romero, Julio; Palma, Juan Luis; Galotto, Maria Jose

2017-01-01

Electrospun nanofibers of poly (vinyl alcohol) (PV) were obtained to improve dispersion of cellulose nanocrystals (CNC) within hydrophobic biopolymeric matrices, such as poly(lactic acid) (PLA). Electrospun nanofibers (PV/CNC)n were successfully obtained with a final concentration of 23% (w/w) of CNC. Morphological, structural and thermal properties of developed CNC and electrospun nanofibers were characterized. X-ray diffraction and thermal analysis revealed that the crystallinity of PV was reduced by the electrospinning process, and the incorporation of CNC increased the thermal stability of biodegradable nanofibers. Interactions between CNC and PV polymer also enhanced the thermal stability of CNC and improved the dispersion of CNC within the PLA matrix. PLA materials with CNC lyophilized were also casted in order to compare the properties with materials based on CNC containing nanofibers. Nanofibers and CNC were incorporated into PLA at three concentrations: 0.5%, 1% and 3% (CNC respect to polymer weight) and nanocomposites were fully characterized. Overall, nanofibers containing CNC positively modified the physical properties of PLA materials, such as the crystallinity degree of PLA which was greatly enhanced. Specifically, materials with 1% nanofiber 1PLA(PV/CNC)n presented highest improvements related to mechanical and barrier properties; elongation at break was enhanced almost four times and the permeation of oxygen was reduced by approximately 30%. PMID:28492470

Utilization of surface differences to improve dyeing properties of poly( m-phenylene isophthalamide) membranes

NASA Astrophysics Data System (ADS)

Ouyang, Shenshen; Wang, Tao; Zhong, Longgang; Wang, Shunli; Wang, Sheng

2018-06-01

Bulk poly( m-phenylene isophthalamide) (PMIA) can achieve flexibility upon dissolution by a LiCl/dimethylacetamide co-solvent, but remains hydrophobic despite the occasional emergence of cis amide groups providing a weak negative charge. In this study, based on the significant surface differences between PMIA membranes processed by nanofiber electrospinning and casting, a series of chemical analyses, in-situ Au nanoparticle depositions, and dye-adsorption experiments revealed that more cis-configuration amide groups appeared on the surface of the electrospun PMIA membrane than on that of the cast membrane. Based on this surface difference, a strategy was proposed to improve the dyeing properties of PMIA by reversibly changing the cis/trans configurations of electrospun and cast membranes. The reversible chain-segment switch mechanism is a novel method for tuning the macroscale properties of polymer materials based on inherent molecular characteristics.

Utilization of surface differences to improve dyeing properties of poly(m-phenylene isophthalamide) membranes

NASA Astrophysics Data System (ADS)

Ouyang, Shenshen; Wang, Tao; Zhong, Longgang; Wang, Shunli; Wang, Sheng

2018-05-01

Bulk poly(m-phenylene isophthalamide) (PMIA) can achieve flexibility upon dissolution by a LiCl/dimethylacetamide co-solvent, but remains hydrophobic despite the occasional emergence of cis amide groups providing a weak negative charge. In this study, based on the significant surface differences between PMIA membranes processed by nanofiber electrospinning and casting, a series of chemical analyses, in-situ Au nanoparticle depositions, and dye-adsorption experiments revealed that more cis-configuration amide groups appeared on the surface of the electrospun PMIA membrane than on that of the cast membrane. Based on this surface difference, a strategy was proposed to improve the dyeing properties of PMIA by reversibly changing the cis/trans configurations of electrospun and cast membranes. The reversible chain-segment switch mechanism is a novel method for tuning the macroscale properties of polymer materials based on inherent molecular characteristics.

Development and characterization of coaxially electrospun gelatin coated poly (3-hydroxybutyric acid) thin films as potential scaffolds for skin regeneration.

PubMed

Nagiah, Naveen; Madhavi, Lakshmi; Anitha, R; Anandan, C; Srinivasan, Natarajan Tirupattur; Sivagnanam, Uma Tirichurapalli

2013-10-01

The morphology of fibers synthesized through electrospinning has been found to mimic extracellular matrix. Coaxially electrospun fibers of gelatin (sheath) coated poly (3-hydroxybutyric acid) (PHB) (core) was developed using 2,2,2 trifluoroethanol(TFE) and 1,1,1,3,3,3 hexafluoro-2-propanol(HFIP) as solvents respectively. The coaxial structure and coating of gelatin with PHB fibers was confirmed through transmission electron microscopy (TEM), scanning electron microscopy (SEM) and X-ray photoelectron spectroscopy (XPS). Thermal stability of the coaxially electrospun fibers was analyzed using thermogravimetric analysis(TGA), differential scanning calorimetry(DSC) and differential thermogravimetric analysis(DTA). Complete evaporation of solvent and gelatin grafting over PHB fibers was confirmed through attenuated total reflection-Fourier transformed infrared spectroscopy (ATR-FTIR). The coaxially electrospun fibers exhibited competent tensile properties for skin regeneration with high surface area and porosity. In vitro degradation studies proved the stability of fibers and its potential applications in tissue engineering. The fibers supported the growth of human dermal fibroblasts and keratinocytes with normal morphology indicating its potential as a scaffold for skin regeneration. © 2013.

Electrospun matrices for localised controlled drug delivery: release of tetracycline hydrochloride from layers of polycaprolactone and poly(ethylene-co-vinyl acetate).

PubMed

Alhusein, Nour; Blagbrough, Ian S; De Bank, Paul A

2012-12-01

We report the controlled release of tetracycline (Tet) HCl from a three-layered electrospun matrix for the first time. Five formulations of electrospun poly-ε-caprolactone (PCL) and poly(ethylene-co-vinyl acetate) (PEVA) have been designed, prepared as micro/nanofibre layers, and assayed for the controlled release of the clinically useful antibiotic Tet HCl with potential applications in wound healing and especially in complicated skin and skin-structure infections. Tet HCl was also chosen as a model drug possessing a good ultraviolet (UV) chromophore and capable of fluorescence together with limited stability. Tet HCl was successfully incorporated (essentially quantitatively at 3 %, w/w) and provided controlled release from multilayered electrospun matrices. The Tet HCl release test was carried out by a total immersion method on 2 × 2 cm(2) electrospun fibrous mats in Tris or phosphate-buffered saline heated to 37 °C. The formulation PCL/PEVA/PCL with Tet HCl in each layer gave a large initial (burst) release followed by a sustained release. Adding a third layer to the two-layered formulations led to release being sustained from 6 days to more than 15 days. There was no detectable loss of Tet chemical stability (as shown by UV and NMR) or bioactivity (as shown by a modified Kirby-Bauer disc assay). Using Tet HCl-sensitive bacteria, Staphylococcus aureus (ATCC 25923), the Tet HCl-loaded three-layered matrix formulations were still showing significantly higher antibacterial effects on days 4 and 5 than commercially available Antimicrobial Susceptibility Test Discs of Tet HCl. Electrospinning provides good encapsulation efficiency of Tet HCl within PCL/PEVA/PCL polymers in micro/nanofibre layers which display sustained antibiotic release.

The effects of electrospun substrate-mediated cell colony morphology on the self-renewal of human induced pluripotent stem cells.

PubMed

Maldonado, Maricela; Wong, Lauren Y; Echeverria, Cristina; Ico, Gerardo; Low, Karen; Fujimoto, Taylor; Johnson, Jed K; Nam, Jin

2015-05-01

The development of xeno-free, chemically defined stem cell culture systems has been a primary focus in the field of regenerative medicine to enhance the clinical application of pluripotent stem cells (PSCs). In this regard, various electrospun substrates with diverse physiochemical properties were synthesized utilizing various polymer precursors and surface treatments. Human induced pluripotent stem cells (IPSCs) cultured on these substrates were characterized by their gene and protein expression to determine the effects of the substrate physiochemical properties on the cells' self-renewal, i.e., proliferation and the maintenance of pluripotency. The results showed that surface chemistry significantly affected cell colony formation via governing the colony edge propagation. More importantly, when surface chemistry of the substrates was uniformly controlled by collagen conjugation, the stiffness of substrate was inversely related to the sphericity, a degree of three dimensionality in colony morphology. The differences in sphericity subsequently affected spontaneous differentiation of IPSCs during a long-term culture, implicating that the colony morphology is a deciding factor in the lineage commitment of PSCs. Overall, we show that the capability of controlling IPSC colony morphology by electrospun substrates provides a means to modulate IPSC self-renewal. Copyright © 2015 Elsevier Ltd. All rights reserved.

Immobilization and Application of Electrospun Nanofiber Scaffold-based Growth Factor in Bone Tissue Engineering.

PubMed

Chen, Guobao; Lv, Yonggang

2015-01-01

Electrospun nanofibers have been extensively used in growth factor delivery and regenerative medicine due to many advantages including large surface area to volume ratio, high porosity, excellent loading capacity, ease of access and cost effectiveness. Their relatively large surface area is helpful for cell adhesion and growth factor loading, while storage and release of growth factor are essential to guide cellular behaviors and tissue formation and organization. In bone tissue engineering, growth factors are expected to transmit signals that stimulate cellular proliferation, migration, differentiation, metabolism, apoptosis and extracellular matrix (ECM) deposition. Bolus administration is not always an effective method for the delivery of growth factors because of their rapid diffusion from the target site and quick deactivation. Therefore, the integration of controlled release strategy within electrospun nanofibers can provide protection for growth factors against in vivo degradation, and can manipulate desired signal at an effective level with extended duration in local microenvironment to support tissue regeneration and repair which normally takes a much longer time. In this review, we provide an overview of growth factor delivery using biomimetic electrospun nanofiber scaffolds in bone tissue engineering. It begins with a brief introduction of different kinds of polymers that were used in electrospinning and their applications in bone tissue engineering. The review further focuses on the nanofiber-based growth factor delivery and summarizes the strategies of growth factors loading on the nanofiber scaffolds for bone tissue engineering applications. The perspectives on future challenges in this area are also pointed out.

Synthesis and Free Radical Polymerization of Fluorinated Polyhedral Oligomeric Silsesquioxane (F-POSS) Macromers: Precursors for Low Surface Energy Materials and Devices

DTIC Science & Technology

2012-10-01

Methylene Iodide Water Superhydrophobic /oleophilic dip-coated fabric Tuteja et al, Science, 2007, 318, 1618 Superamphiphobic electrospun surfaces...door for use a building block material for low surface energy materials • Applications – Mechanical robust superhydrophobic /oleophobic/omniphobic

Novel Lignocellulosic Composites

NASA Astrophysics Data System (ADS)

Peresin, Maria Soledad

2011-12-01

Obtained by acid hydrolysis of ramie fibers, cellulose nanocrystals (CNC) were used to reinforce nanofiber webs of different polymeric matrices via electrospinning. Poly vinyl acetate (PVA) with different degrees of hydrolysis was chosen due to its biodegradability and ease of processability. Homogeneous webs of smooth, defect-free and continuous fibers were prepared presenting diameters on the nanoscale, containing from 5 to 15% wt of CNC. The webs were characterized in terms of chemical, morphological, and thermo-mechanical properties. Strong interaction between PVA matrix with CNC, mainly via hydrogen bond network was evidenced; however, it was reduced in samples with higher content of acetyl groups. Most interestingly, the elastic modulus of the nanocomposite mats increased significantly as a consequence of the reinforcing effect of CNC, via the percolation network held by hydrogen bonds and the efficient stress transfer between the reinforcing CN and the fully hydrolyzed PVA electrospun fibers. Reduction in the degree of crystallinity of CN-loaded webs was observed as a result of transnucleation effect of the nanoparticles. Due to the hydrophilicity of the matrix, the effect of different relative humidities on the morphological and thermo-mechanical properties of the electrospun was also studied. The incorporation of CNC was shown to improve the morphological stability of the webs even at high humidity levels. The thermo-mechanical behavior of the electrospun fiber webs was drastically affected by the balance between the moisture-induced plasticization and the rigidity of the reinforcing CNC. Results indicated that water absorption might have a negative effect on the stabilizing effect of CNC in the PVA matrix due to a disruption of the hydrogen bond network within the structure. Humidity- induced reduction in tensile strength of neat PVA fiber webs was shown to be significantly prevented by the presence of CNC in the webs; and a fully reversible recovery in mechanical strength after cycling of relative humidity was observed in the CN-loaded PVA webs. Target applications for these ultra high surface area webs include the manufacture of sensors and selectively permeable membranes, in which case, their high hydrophilicity can be detrimental in applications were aqueous media is involved. In order to overcome this problem, we proposed a vapor phase, acid catalyzed crosslinking reaction, using maleic anhydride and posterior temperature curing. Interactions of the modified composite webs with solvent of different polarities were analyzed, as well as their mechanical integrity after water immersion, morphological, thermal, and chemical properties before and after modification. Finally, mixtures of cellulose acetate, dissolved in a mixture of acetone and dimethylacetamide, with different degrees of substitution were electrospun, obtaining nanofiber webs of various compositions. The fibers were reinforced with CNC, and also effectively deacetylated via alkaline hydrolysis, to obtain purely cellulosic webs. The effect of deacetylation on morphology and thermal behavior was evaluated using a variety of techniques. Results showed that thermal, surface and chemical properties of the fibers were drastically changed after deacetylation to cellulose; however, the morphological structure was preserved. Finally, the presence of CNC in the CA and regenerated cellulose polymeric matrix induced an increase in hydrophilicity on the electrospun webs, as revealed by water contact angle results.

Release of metronidazole from electrospun poly(L-lactide-co-D/L-lactide) fibers for local periodontitis treatment.

PubMed

Reise, Markus; Wyrwa, Ralf; Müller, Ulrike; Zylinski, Matthias; Völpel, Andrea; Schnabelrauch, Matthias; Berg, Albrecht; Jandt, Klaus D; Watts, David C; Sigusch, Bernd W

2012-02-01

We aimed to achieve detailed biomaterials characterization of a drug delivery system for local periodontitis treatment based on electrospun metronidazole-loaded resorbable polylactide (PLA) fibers. PLA fibers loaded with 0.1-40% (w/w) MNA were electrospun and were characterized by SEM and DSC. HPLC techniques were used to analyze the release profiles of metronidazole (MNA) from these fibers. The antibacterial efficacy was determined by measuring inhibition zones of drug-containing aliquots from the same electrospun fiber mats in an agar diffusion test. Three pathogenic periodontal bacterial strains: Fusobacterium nucleatum, Aggregatibacter actinomycetemcomitans and Porphyromonas gingivalis were studied. Cytotoxicity testing was performed with human gingival fibroblasts by: (i) counting viable cells via live/dead staining methods and (ii) by exposing cells directly onto the surface of MNA-loaded fibers. MNA concentration influenced fiber diameters and thus w/w surface areas: diameter being minimal and area maximal at 20% MNA. HPLC showed that these 20% MNA fibers had the fastest initial MNA release. From the third day, MNA release was slower and nearly linear with time. All fiber mats released 32-48% of their total drug content within the first 7 days. Aliquots of media taken from the fiber mats inhibited the growth of all three bacterial strains. MNA released up to the 28th day from fiber mats containing 40% MNA significantly decreased the viability of F. nucleatum and P. gingivalis and up to the 2nd day also for the resistant A. actinomycetemcomitans. All of the investigated fibers and aliquots showed excellent cytocompatibility. This study shows that MNA-loaded electrospun fiber mats represent an interesting class of resorbable drug delivery systems. Sustained drug release properties and cytocompatibility suggest their potential clinical applicability for the treatment of periodontal diseases. Copyright © 2011 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Silicon-Containing Polymers and Composites

DTIC Science & Technology

2012-03-28

superhydrophobic . FluoroPOSS polymer composite surfaces can be superhydrophobic and superoleophobic. Superhydrophilic and superoleophobic surfaces...Superhydrophilic Hydrophilic Hydrophobic Superhydrophobic θ ~ 0° 0°< θ < 90° θ > 90° θ* > 150° 3DISTRIBUTION A. Approved for public release; distribution...public release; distribution unlimited. . Electrospun Surfaces HV power Electrode P l 160 Superhydrophobic Surfaces supply o ymer flow rate

Hierarchical porous membrane via electrospinning PIM-1 for micropollutants removal

NASA Astrophysics Data System (ADS)

Pan, Ying; Zhang, Lijie; Li, Zhaojing; Ma, Liujia; Zhang, Yufeng; Wang, Jun; Meng, Jianqiang

2018-06-01

Ideal adsorbents are featured by both high adsorption capacity and high adsorption rate. Current adsorptive membranes enjoy good mass transfer performance but have limited sorption capacity. Microporous organic polymer has superiorities of small pore size and high surface area which is conductive to high adsorption capacity, but usually suffers from high mass transfer resistance. In this work, the polymer of intrinsic microporosity PIM-1 was fabricated into microfiber membranes by electrospinning for carbendazim and phenol adsorption. The PIM-1 and its electrospun membranes were characterized by 1H NMR, GPC, ATR-FTIR, FESEM, TG and BET measurements. The electrospun PIM-1 membrane was demonstrated to have hierarchical porous structure with high surface area. The equilibrium adsorption capacity for carbendazim and phenol was 0.084 mmol/g and 0.804 mmol/g, respectively. The adsorption isotherm fits well with Langmuir model and the adsorption kinetic can be described by film diffusion and chemical reaction model. The membrane can retain 95% of its initial capacity after cycling 10 times. Both the sorption capacity and kinetic coefficients are high when comparing with other sorbents for either carbendazim or phenol, demonstrating that the electrospun PIM-1 is a good adsorbent.

Electrospun TiO₂ nanofibers decorated Ti substrate for biomedical application.

PubMed

Dumitriu, Cristina; Stoian, Andrei Bogdan; Titorencu, Irina; Pruna, Vasile; Jinga, Victor V; Latonen, Rose-Marie; Bobacka, Johan; Demetrescu, Ioana

2014-12-01

Various TiO2 nanofibers on Ti surface have been fabricated via electrospinning and calcination. Due to different elaboration conditions the electrospun fibers have different surface feature morphologies, characterized by scanning electronic microscopy, surface roughness, and contact angle measurements. The results have indicated that the average sample diameters are between 32 and 44 nm, roughness between 61 and 416 nm, and all samples are hydrophilic. As biological evaluation, cell culture with MG63 cell line originally derived from a human osteosarcoma was performed and correlation between nanofibers elaboration, properties and cell response was established. The cell adherence and growth are more evident on Ti samples with more aligned fibers, higher roughness and strong hydrophilic character and such fibers have been elaborated with a high speed rotating cylinder collector, confirming the idea that nanostructure elaboration conditions guide the cells' growth. Copyright © 2014 Elsevier B.V. All rights reserved.

A novel hydrogen peroxide biosensor based on hemoglobin-collagen-CNTs composite nanofibers.

PubMed

Li, J; Mei, H; Zheng, W; Pan, P; Sun, X J; Li, F; Guo, F; Zhou, H M; Ma, J Y; Xu, X X; Zheng, Y F

2014-06-01

In this paper, carbon nanotubes (CNTs) were successfully incorporated in the composite composed of hemoglobin (Hb) and collagen using co-electrospinning technology. The formed Hb-collagen-CNTs composite nanofibers possessed distinct advantage of three-dimensional porous structure, biocompatibility and excellent stability. The Hb immobilized in the electrospun nanofibers retained its natural structure and the heterogeneous electron transfer rate constant (ks) of the direct electron transfer between Hb and electrodes was 5.3s(-1). In addition, the electrospun Hb-collagen-CNTs nanofibers modified electrodes showed good electrocatalytic properties toward H2O2 with a detection limit of 0.91μM (signal-to-noise ratio of 3) and the apparent Michaelis-Menten constant (Km(app)) of 32.6μM. Copyright © 2014 Elsevier B.V. All rights reserved.

The fabrication and electrochemical properties of electrospun nanofibers of a multiwalled carbon nanotube grafted by chitosan

NASA Astrophysics Data System (ADS)

Feng, Wei; Wu, Zigang; Li, Yu; Feng, Yiyu; Yuan, Xiaoyan

2008-03-01

Multiwalled carbon nanotubes (MWCNTs) were grafted by chitosan (CS); the product could disperse well in poly(vinyl alcohol) (PVA) aqueous solution with 2% (v/v) acetic acid solution. Because this product has potential in several biological fields, it was electrospun so as to enlarge the surface area. Raman spectra indicated that the electrospinning process did not severely alter the electron hybridization of carbon atoms within the nanotube framework. Moreover and interestingly, these nanofibers showed a novel sheath-core structure; the outer and inner diameters of these sheath-core nanofibers were about 200 nm and 100 nm, respectively. These nanofibers' electrochemical properties were characterized by detection of hydrogen peroxide and voltammetric responses of potassium ferricyanide. The electrospun fibers' web displayed faster electron transfer kinetics and better electrochemical properties than its cast film, which justified further applications in biological areas.

Polymeric biomaterials for nerve regeneration applications: From promoting cellular organization to the delivery of bioactive molecules

NASA Astrophysics Data System (ADS)

Delgado-Rivera, Roberto L.

Thousands of new cases of injury to the central nervous system (CNS) occur each year in the USA and all over the world. However, despite recent advances, at present there is no cure for the resulting paraplegia or quadriplegia. This research is directed towards engineering biomaterial platforms to promote cellular organization at the surface of polymer scaffolds that will be conducive to proper regeneration of injured CNS. In addition, the formulation of a delivery system for neuroactive molecules using polymer-based materials will be evaluated to establish its potential to treat CNS disorders. Initial studies involved the chemical modification of an electrospun nonwoven matrix of nanofibers with fibroblast growth factor 2 (FGF-2). Nanofibers alone up-regulated FGF-2, albeit to a lesser extent than nanofibers covalently modified with FGF-2. These results underscore the importance of both surface topography and growth factor presentation on cellular function. Moreover, that FGF-2 modified nanofibrillar scaffolds may demonstrate utility in tissue engineering applications for replacement and regeneration of damaged tissue following CNS injury or disease. Subsequent research efforts focused on a novel micropatterning technique called microscale plasma-initiated patterning (microPIP). This patterning method uses a polydimethylsiloxane (PDMS) stamp to selectively protect regions of an underlying substrate from oxygen plasma treatment resulting in hydrophobic and hydrophilic regions. FGF-2 and laminin-1 were applied to an electrospun polyamide nanofibrillar matrix following plasma treatment. In this work it, was possible to demonstrate that textured surfaces, such as nanofibrillar scaffolds, can be micropatterned to provide external chemical cues for cellular organization. Finally, a microsphere system capable of encapsulating proteins while minimizing the mechanisms of protein degradation and providing a controlled release was investigated. Microspheres were comprised of a salicylic-acid based poly(anhydride-ester) (PAE), a biodegradable polymer that incorporates salicylic acid into the polymer backbone (PolyAspirin). The use of microspheres formulated from PolyAspirin as a delivery vehicle can be advantageous due its ability of performing a dual delivery; biomolecule (protein) and drug. By combining these two properties, it will be possible to release neurotrophic factors to induce a biological response while mitigating inflammatory pathways due to the localized delivery of salicylic acid.

Novel compaction resistant and ductile nanocomposite nanofibrous microfiltration membranes.

PubMed

Homaeigohar, Seyed Shahin; Elbahri, Mady

2012-04-15

Despite promising filtration abilities, low mechanical properties of extraordinary porous electrospun nanofibrous membranes could be a major challenge in their industrial development. In addition, such kind of membranes are usually hydrophobic and non-wettable. To reinforce an electrospun nanofibrous membrane made of polyethersulfone (PES) mechanically and chemically (to improve wettability), zirconia nanoparticles as a novel nanofiller in membrane technology were added to the nanofibers. The compressive and tensile results obtained through nanoindentation and tensile tests, respectively, implied an optimum mechanical properties after incorporation of zirconia nanoparticles. Especially compaction resistance of the electrospun nanofibrous membranes improved significantly as long as no agglomeration of the nanoparticles occurred and the electrospun nanocomposite membranes showed a higher tensile properties without any brittleness i.e. a high ductility. Noteworthy, for the first time the compaction level was quantified through a nanoindentation test. In addition to obtaining a desired mechanical performance, the hydrophobicity declined. Combination of promising properties of optimum mechanical and surface chemical properties led to a considerably high water permeability also retention efficiency of the nanocomposite PES nanofibrous membranes. Such finding implies a longer life span and lower energy consumption for a water filtration process. Copyright © 2012 Elsevier Inc. All rights reserved.

Polymer surfaces structured with random or aligned electrospun nanofibers to promote the adhesion of blood platelets.

PubMed

Wan, Ling-Shu; Xu, Zhi-Kang

2009-04-01

Fibrous membranes (nonwoven meshes) prepared via electrospinning technique have great potential in tissue engineering. This work is the first study on the behaviors of blood platelets at the nanostructured surface generated by electrospinning. Poly[acrylonitrile-co-(N-vinyl-2-pyrrolidone)] (PANCNVP) that shows excellent antiplatelet adhesion ability was directly electrospun onto its dense membrane surface. Polyacrylonitrile (PAN) samples were used as controls. The depth as well as the density of the nanofibers can be easily controlled. The results showed that the PANCNVP dense membrane certainly suppressed the activation and adhesion of platelets. However, whether the nanofibers and underlying membranes were composed of PAN or PANCNVP, the nanostructured surfaces promoted the activation, adhesion, and orientation of platelets. It was also found that, if the space between fibers was too large or the depth of fibers was too small, the nanostructured surface did not change the property of antiplatelet adhesion of PANCNVP. The promotion of activation and adhesion of platelets was obviously due to the presence of nanofibers, which induced the changes of surface topography and charge. Copyright 2008 Wiley Periodicals, Inc.

Mechanical properties of single electrospun drug-encapsulated nanofibres

PubMed Central

Chew, Sing Yian; Hufnagel, Todd C; Lim, Chwee Teck; Leong, Kam W

2008-01-01

The mechanical and structural properties of a surface play an important role in determining the morphology of attached cells, and ultimately their cellular functions. As such, mechanical and structural integrity are important design parameters for a tissue scaffold. Electrospun fibrous meshes are widely used in tissue engineering. When in contact with electrospun scaffolds, cells see the individual micro- or nanofibres as their immediate microenvironment. In this study, tensile testing of single electrospun nanofibres composed of poly(ε-caprolactone) (PCL), and its copolymer, poly(caprolactone-co-ethyl ethylene phosphate) (PCLEEP), revealed a size effect in the Young's modulus, E, and tensile strength, σT. Both strength and stiffness increase as the fibre diameter decreases from bulk (∼5 μm) into the nanometre region (200–300 nm). In particular, E and σT of individual PCL nanofibres were at least two-fold and an order of magnitude higher than that of PCL film, respectively. PCL films were observed to have more pronounced crystallographic texture than the nanofibres; however no difference in crystalline fraction, perfection, or texture was detected among the various fibres. When drugs were encapsulated into single PCLEEP fibres, mechanical properties were enhanced with 1–20 wt% of loaded retinoic acid, but weakened by 10–20 wt% of encapsulated bovine serum albumin. This understanding of the effect of size and drug and protein encapsulation on the mechanical properties of electrospun fibres may help in the optimization of tissue scaffold design that combines biochemical and biomechanical cues for tissue regeneration. PMID:19079553

Synthesis and Process Optimization of Electrospun PEEK-Sulfonated Nanofibers by Response Surface Methodology

PubMed Central

Boaretti, Carlo; Roso, Martina; Lorenzetti, Alessandra; Modesti, Michele

2015-01-01

In this study electrospun nanofibers of partially sulfonated polyether ether ketone have been produced as a preliminary step for a possible development of composite proton exchange membranes for fuel cells. Response surface methodology has been employed for the modelling and optimization of the electrospinning process, using a Box-Behnken design. The investigation, based on a second order polynomial model, has been focused on the analysis of the effect of both process (voltage, tip-to-collector distance, flow rate) and material (sulfonation degree) variables on the mean fiber diameter. The final model has been verified by a series of statistical tests on the residuals and validated by a comparison procedure of samples at different sulfonation degrees, realized according to optimized conditions, for the production of homogeneous thin nanofibers. PMID:28793427

Synthesis and Process Optimization of Electrospun PEEK-Sulfonated Nanofibers by Response Surface Methodology.

PubMed

Boaretti, Carlo; Roso, Martina; Lorenzetti, Alessandra; Modesti, Michele

2015-07-07

In this study electrospun nanofibers of partially sulfonated polyether ether ketone have been produced as a preliminary step for a possible development of composite proton exchange membranes for fuel cells. Response surface methodology has been employed for the modelling and optimization of the electrospinning process, using a Box-Behnken design. The investigation, based on a second order polynomial model, has been focused on the analysis of the effect of both process (voltage, tip-to-collector distance, flow rate) and material (sulfonation degree) variables on the mean fiber diameter. The final model has been verified by a series of statistical tests on the residuals and validated by a comparison procedure of samples at different sulfonation degrees, realized according to optimized conditions, for the production of homogeneous thin nanofibers.

Atmospheric Pressure Plasma-Electrospin Hybrid Process for Protective Applications

NASA Astrophysics Data System (ADS)

Vitchuli Gangadharan, Narendiran

2011-12-01

Chemical and biological (C-B) warfare agents like sarin, sulfur mustard, anthrax are usually dispersed into atmosphere in the form of micro aerosols. They are considered to be dangerous weapon of mass destruction next to nuclear weapons. The airtight protective clothing materials currently available are able to stop the diffusion of threat agents but not good enough to detoxify them, which endangers the wearers. Extensive research efforts are being made to prepare advanced protective clothing materials that not only prevent the diffusion of C-B agents, but also detoxify them into harmless products thus ensuring the safety and comfort of the wearer. Electrospun nanofiber mats are considered to have effective filtration characteristics to stop the diffusion of submicron level particulates without sacrificing air permeability characteristics and could be used in protective application as barrier material. In addition, functional nanofibers could be potentially developed to detoxify the C-B warfare threats into harmless products. In this research, electrospun nanofibers were deposited on fabric surface to improve barrier efficiency without sacrificing comfort-related properties of the fabrics. Multi-functional nanofibers were fabricated through an electrospinning-electrospraying hybrid process and their ability to detoxify simulants of C-B agents was evaluated. Nanofibers were also deposited onto plasma-pretreated woven fabric substrate through a newly developed plasma-electrospinning hybrid process, to improve the adhesive properties of nanofibers on the fabric surface. The nanofiber adhesion and durability properties were evaluated by peel test, flex and abrasion resistance tests. In this research work, following tasks have been carried out: i) Controlled deposition of nanofiber mat onto woven fabric substrate Electrospun Nylon 6 fiber mats were deposited onto woven 50/50 Nylon/Cotton fabric with the motive of making them into protective material against submicron-level aerosol chemical and biological threats. Polymer solution concentration, electrospinning voltage, and deposition areal density were varied to establish the relationship of processing-structure-filtration efficiency for electrospun fiber mats. A high barrier efficiency of greater than 99.5% was achieved on electrospun fiber mats without sacrificing air permeability and pressure drop. ii) Fabrication and Characterization of Multifunctional ZnO/Nylon 6 nanofibers ZnO/Nylon 6 nanofiber mats were prepared by an electrospinning-electrospraying hybrid process, The electrospinning of polymer solution and electrospraying of ZnO particles were carried out simultaneously such that the ZnO nanoparticles were dispersed on the surface of Nylon 6 nanofibers. The prepared ZnO/Nylon 6 nanofiber mats were tested for detoxifying characteristics against simulants of C-B agents. The results showed that ZnO/Nylon 6 functional nanofiber mats exhibited good detoxification action against paraoxon and have antibacterial efficiency over 99.99% against both the gram-negative E. coli and gram positive B. cereus bacteria. iii) Improving adhesion of electrospun nanofiber mat onto woven fabric by plasma pretreatment of substrate fabric and plasma-electrospinning hybrid process Electrospun nanofibers were deposited onto plasma-pretreated woven fabric to improve the adhesion. In addition, the plasma-electrospinning hybrid process was developed and used in which the nanofibers were subjected to in-situ plasma treatment during electrospinning. The effects of plasma treatement on substrate fabric and electrospun fibers were characterized by water contact angle test, XPS analyses. The improvement of nanofiber adhesive properties on fabric substrate was evaluated by peel test, flex resistance test and abrasion resistance test. The test results showed that the plasma treatment caused introduction of active chemical groups on substrate fabric and electrospun nanofibers. These active chemical assisted in possible cross-linking formation between nanofiber mat and substrate fabric, and this hypothesis was supported by improved adhesion strength, flex resistance and abrasion resistance of nanofiber mat.

Aligned and Electrospun Piezoelectric Polymer Fiber Assembly and Scaffold

NASA Technical Reports Server (NTRS)

Holloway, Nancy M. (Inventor); Scott-Carnell, Lisa A. (Inventor); Siochi, Emilie J. (Inventor); Leong, Kam W. (Inventor); Kulangara, Karina (Inventor)

2015-01-01

A scaffold assembly and related methods of manufacturing and/or using the scaffold for stem cell culture and tissue engineering applications are disclosed which at least partially mimic a native biological environment by providing biochemical, topographical, mechanical and electrical cues by using an electroactive material. The assembly includes at least one layer of substantially aligned, electrospun polymer fiber having an operative connection for individual voltage application. A method of cell tissue engineering and/or stem cell differentiation uses the assembly seeded with a sample of cells suspended in cell culture media, incubates and applies voltage to one or more layers, and thus produces cells and/or a tissue construct. In another aspect, the invention provides a method of manufacturing the assembly including the steps of providing a first pre-electroded substrate surface; electrospinning a first substantially aligned polymer fiber layer onto the first surface; providing a second pre-electroded substrate surface; electrospinning a second substantially aligned polymer fiber layer onto the second surface; and, retaining together the layered surfaces with a clamp and/or an adhesive compound.

Aligned and Electrospun Piezoelectric Polymer Fiber Assembly and Scaffold

NASA Technical Reports Server (NTRS)

Kulangara, Karina (Inventor); Scott Carnell, Lisa A. (Inventor); Holloway, Nancy M. (Inventor); Leong, Kam W. (Inventor); Siochi, Emilie J. (Inventor)

2017-01-01

A method of manufacturing and/or using a scaffold assembly for stem cell culture and tissue engineering applications is disclosed. The scaffold at least partially mimics a native biological environment by providing biochemical, topographical, mechanical and electrical cues by using an electroactive material. The assembly includes at least one layer of substantially aligned, electrospun polymer fiber having an operative connection for individual voltage application. A method of cell tissue engineering and/or stem cell differentiation that uses the assembly seeded with a sample of cells suspended in cell culture media, incubates and applies voltage to one or more layers, and thus produces cells and/or a tissue construct. In another aspect, the invention provides a method of manufacturing the assembly including the steps of providing a first pre-electroded substrate surface; electrospinning a first substantially aligned polymer fiber layer onto the first surface; providing a second pre-electroded substrate surface; electrospinning a second substantially aligned polymer fiber layer onto the second surface; and, retaining together the layered surfaces with a clamp and/or an adhesive compound.

Guidance of neurite outgrowth on aligned electrospun polypyrrole/poly(styrene-beta-isobutylene-beta-styrene) fiber platforms.

PubMed

Liu, Xiao; Chen, Jun; Gilmore, Kerry J; Higgins, Michael J; Liu, Yong; Wallace, Gordon G

2010-09-15

The purpose of this work was to investigate the potential biomedical application of novel aligned electrospun polypyrrole (PPy)/poly(styrene-beta-isobutylene-beta-styrene) (SIBS) fibers. After successfully aligning the electroactive PPy/SIBS fibers based on our modified electrospinning method, we demonstrated that neurite outgrowth from PC12 cells could be highly orientated parallel to the aligned PPy/SIBS fibers. Physical interactions between the nerve cells and PPy/SIBS fibers through filopodia "sensing" were observed using atomic force microscopy. These observations indicate a role of contact guidance as a mechanism for the observed alignment. This work highlights the capacity for electroactive PPy/SIBS fibers to support and guide nerve cell differentiation through topographic cues, which is a highly desirable characteristic in medical implants for neurological applications. (c) 2010 Wiley Periodicals, Inc.

Photocatalytic antibacterial effect of ZnO nanoparticles into coaxial electrospun PCL fibers to prevent infections from skin injuries

NASA Astrophysics Data System (ADS)

Prado-Prone, G.; Silva-Bermúdez, P.; García-Macedo, J. A.; Almaguer-Flores, A.; Ibarra, C.; Velasquillo-Martínez, C.

2017-02-01

Antibacterial studies of inorganic nanoparticles (nps) have become important due to the increased bacterial resistance against antibiotics. We used Zinc oxide nanoparticles (ZnO nps), which possess excellent photocatalytic properties with a wide band gap (Eg), are listed as "generally recognized as safe" by the Food and Drug Administration (FDA) and have shown antibacterial activity (AA) against many bacterial strains. The AA of ZnO nps is partly attributed to the production of Reactive Oxygen Species (ROS) by photocatalysis. When ZnO nps in aqueous media are illuminated with an energy

Protein adsorption on electrospun zinc doped hydroxyapatite containing nylon 6 membrane: kinetics and isotherm.

PubMed

Esfahani, Hamid; Prabhakaran, Molamma P; Salahi, Esmaeil; Tayebifard, Ali; Keyanpour-Rad, Mansour; Rahimipour, Mohamad Reza; Ramakrishna, Seeram

2015-04-01

Surface modification of electrospun polymeric membrane surfaces is a critical step towards the separation process including protein adsorption. In this study, the electrospun Nylon fibers was incorporated with positively charged zinc doped hydroxyapatite (HAp) nanoparticles to study the adsorption of negatively charged proteins, namely bovine serum albumin (BSA). Effects of zinc amount within the atomic structure of HAp (nZH; n=0, 4, 8 At.%) was evaluated on produced scaffolds and consequently protein adsorption. The results showed that the ability of Nylon membrane to adsorb BSA increased with incorporation of nZH nanoparticles within the nylon structure. This phenomenon is appeared to be relate to different electrostatic charge and not to physical characteristic of scaffolds. The incorporated membrane (N-4ZH) by nanoparticles with highest zeta (ξ) potential adsorbed the maximum amount of protein. The adsorption of BSA was best fitted with pseudo-second order kinetic model. The experimental isotherm data were further analyzed by using Langmuir and Freundlich equations. By comparing the correlation coefficients obtained for each linear transformation of isotherm analysis, it was found that the Langmuir equation was the best fit equilibrium model that described the adsorption of BSA on these membranes. Copyright © 2014 Elsevier Inc. All rights reserved.

The synergistic effect of nano-hydroxyapatite and dexamethasone in the fibrous delivery system of gelatin and poly(l-lactide) on the osteogenesis of mesenchymal stem cells.

PubMed

Amjadian, Sara; Seyedjafari, Ehsan; Zeynali, Bahman; Shabani, Iman

2016-06-30

Recently, electrospun nanofibrous scaffolds are vastly taken into consideration in the bone tissue engineering due to mimicking the natural structure of native tissue. In our study, surface features of nanofibers were modified through simultaneous electrospining of the synthetic and natural polymers using poly l-lactide (PLLA) and gelatin to fabricate the hybrid scaffold (PLLA/gelatin). Then, hydroxyapatite nanoparticles (nHA) were loaded in electrospun PLLA nanofibers (PLLA,nHA/gelatin) and also dexamethasone (DEX) was incorporated in these fibers (PLLA,nHA,DEX/gelatin) in the second experiment. Fabricated nanofibrous composite scaffolds were characterized via SEM, FTIR spectroscopy, contact angle, tensile strength measurements, DEX release profile and MTT assay. After seeding adipose derived mesenchymal stem cells, osteoinductivity and osteoconductivity of fabricated scaffolds were analyzed using common osteogenic markers such as alkaline phosphatase activity, calcium depositions and gene expression. These results confirmed that all properties of nanofibers were improved by modifications. Moreover, osteogenic differentiation of stem cells increased in PLLA,nHA/gelatin group in comparison with PLLA/gelatin. The sustained release of DEX was obtained from PLLA,nHA,DEX/gelatin which subsequently led to more osteogenic differentiation. Taken together, PLLA,nHA,DEX/gelatin showed significant potential to support the stem cell proliferation and ostogenic differentiation, and can be a good candidates for tissue engineering and regenerative medicine applications. Copyright © 2016 Elsevier B.V. All rights reserved.

Plasma modified nanofibres based on gum kondagogu and their use for collection of nanoparticulate silver, gold and platinum.

PubMed

Padil, Vinod Vellora Thekkae; Stuchlík, Martin; Černík, Miroslav

2015-05-05

Electrospun nanofibre membranes from blend solutions of deacetylated gum kondagogu and polyvinyl alcohol of various weight proportions were prepared. The electrospun membrane was cross linked by heating at 150°C for 6h and later modified by methane plasma treatment. Membranes were successively used for the removal of nanoparticles (Ag, Au and Pt) from water. Pt nanoparticles with the smallest size (2.4 ± 0.7 nm) has a higher adsorption capacity (270.4 mg/g and 327.2mg/g) compared to Au and Ag nanoparticles with particle sizes 7.8 ± 2.3 nm and 10.5 ± 3.5 nm onto nanofibre membrane (NFM) and methane plasma treated membrane (P-NFM). The extraction efficiency of P-NFM for the removal of nanoparticles in water is higher compared to untreated membranes. The adsorption kinetics were evaluated by pseudo-first order and pseudo-second order models for the extraction of nanoparticles from water, with the pseudo-second order model providing a better fit. The reusability and regeneration of the P-NFM for consecutive adsorption was also established. Copyright © 2015 Elsevier Ltd. All rights reserved.

High Areal Capacity Si/LiCoO 2 Batteries from Electrospun Composite Fiber Mats

DOE Office of Scientific and Technical Information (OSTI.GOV)

Self, Ethan C.; Naguib, Michael; Ruther, Rose E.

Here, freestanding nanofiber mat Li-ion battery anodes containing Si nanoparticles, carbon black, and poly(acrylic acid) (Si/C/PAA) are prepared using electrospinning. The mats are compacted to a high fiber volume fraction (~0.85), and interfiber contacts are welded by exposing the mat to methanol vapor. A compacted+welded fiber mat anode containing 40 wt % Si exhibits high capacities of 1,484 mA h g -1 (3,500 mA h gmore » $$-1\\atop{Si}$$) at 0.1 C and 489 mAh g -1 at 1 C and good cycling stability (e.g., 73% capacity retention over 50 cycles). Post-mortem analysis of the fiber mats shows that the overall electrode structure is preserved during cycling. Whereas many nanostructured Si anodes are hindered by their low active material loadings and densities, thick, densely packed Si/C/PAA fiber mat anodes reported here have high areal and volumetric capacities (e.g., 4.5 mA h cm -2 and 750 mA h cm -3, respectively). A full cell containing an electrospun Si/C/PAA anode and electrospun LiCoO 2-based cathode has a high specific energy density of 270 Wh kg -1. The excellent performance of the electrospun Si/C/PAA fiber mat anodes is attributed to the: (i) PAA binder which interacts with the SiO x surface of Si nanoparticles and (ii) high material loading, high fiber volume fraction, and welded interfiber contacts of the electrospun mats« less

Electrospun fibers for the prevention of human immunodeficiency virus

NASA Astrophysics Data System (ADS)

Ball, Cameron

HIV/AIDS education, testing, and treatment have thus far failed to cease the pandemic spread of the HIV virus. HIV prevention is hindered by a lack of protective options beyond the ABC approach of abstinence, being faithful, and using condoms. One approach to address this inadequacy is to develop antiviral products for vaginal or rectal application that provide receptive partner-initiated protection against viral infection during sex. Such products, termed anti-HIV microbicides, can especially empower young women to take control over their sexual health. This work explored a new approach to anti-HIV microbicides: electrospun fibers for the delivery of small-molecule antiretroviral drugs. Electrospun microbicides are nonwoven fabrics made from polymer-based nanofibers. The wide array of polymers available for electrospinning allowed for the incorporation and release of chemically diverse agents. Since electrospun fibers have an extremely high surface area to volume ratio, they serve as excellent delivery systems for rapid drug delivery of both hydrophilic and hydrophobic agents. The flexibility in the design of electrospun fibers afforded by coaxial electrospinning further enabled the formulation of sustained-release microbicides. To demonstrate the power of electrospinning to deliver drugs over multiple timescales, composite microbicide fabrics were created to provide both rapid and sustained drug release from a single device. This work has produced alternative microbicide formulations, while establishing methods for the thorough characterization of these systems and solutions for the needs of people at risk of HIV infection. By addressing problems in both HIV prevention and drug delivery, this work has expanded our capacity to engineer elegant solutions to complex and pressing global health challenges.

High Areal Capacity Si/LiCoO 2 Batteries from Electrospun Composite Fiber Mats

DOE PAGES

Self, Ethan C.; Naguib, Michael; Ruther, Rose E.; ...

2017-03-24

Here, freestanding nanofiber mat Li-ion battery anodes containing Si nanoparticles, carbon black, and poly(acrylic acid) (Si/C/PAA) are prepared using electrospinning. The mats are compacted to a high fiber volume fraction (~0.85), and interfiber contacts are welded by exposing the mat to methanol vapor. A compacted+welded fiber mat anode containing 40 wt % Si exhibits high capacities of 1,484 mA h g -1 (3,500 mA h gmore » $$-1\\atop{Si}$$) at 0.1 C and 489 mAh g -1 at 1 C and good cycling stability (e.g., 73% capacity retention over 50 cycles). Post-mortem analysis of the fiber mats shows that the overall electrode structure is preserved during cycling. Whereas many nanostructured Si anodes are hindered by their low active material loadings and densities, thick, densely packed Si/C/PAA fiber mat anodes reported here have high areal and volumetric capacities (e.g., 4.5 mA h cm -2 and 750 mA h cm -3, respectively). A full cell containing an electrospun Si/C/PAA anode and electrospun LiCoO 2-based cathode has a high specific energy density of 270 Wh kg -1. The excellent performance of the electrospun Si/C/PAA fiber mat anodes is attributed to the: (i) PAA binder which interacts with the SiO x surface of Si nanoparticles and (ii) high material loading, high fiber volume fraction, and welded interfiber contacts of the electrospun mats« less

Assessing the Increase in Specific Surface Area for Electrospun Fibrous Network due to Pore Induction.

PubMed

Katsogiannis, Konstantinos Alexandros G; Vladisavljević, Goran T; Georgiadou, Stella; Rahmani, Ramin

2016-10-26

The effect of pore induction on increasing electrospun fibrous network specific surface area was investigated in this study. Theoretical models based on the available surface area of the fibrous network and exclusion of the surface area lost due to fiber-to-fiber contacts were developed. The models for calculation of the excluded area are based on Hertzian, Derjaguin-Muller-Toporov (DMT), and Johnson-Kendall-Roberts (JKR) contact models. Overall, the theoretical models correlated the network specific surface area to the material properties including density, surface tension, Young's modulus, Poisson's ratio, as well as network physical properties, such as density and geometrical characteristics including fiber radius, fiber aspect ratio and network thickness. Pore induction proved to increase the network specific surface area up to 52%, compared to the maximum surface area that could be achieved by nonporous fiber network with the same physical properties and geometrical characteristics. The model based on Johnson-Kendall-Roberts contact model describes accurately the fiber-to-fiber contact area under the experimental conditions used for pore generation. The experimental results and the theoretical model based on Johnson-Kendall-Roberts contact model show that the increase in network surface area due to pore induction can reach to up to 58%.

Development of Omniphobic Desalination Membranes Using a Charged Electrospun Nanofiber Scaffold.

PubMed

Lee, Jongho; Boo, Chanhee; Ryu, Won-Hee; Taylor, André D; Elimelech, Menachem

2016-05-04

In this study, we present a facile and scalable approach to fabricate omniphobic nanofiber membranes by constructing multilevel re-entrant structures with low surface energy. We first prepared positively charged nanofiber mats by electrospinning a blend polymer-surfactant solution of poly(vinylidene fluoride-co-hexafluoropropylene) (PVDF-HFP) and cationic surfactant (benzyltriethylammonium). Negatively charged silica nanoparticles (SiNPs) were grafted on the positively charged electrospun nanofibers via dip-coating to achieve multilevel re-entrant structures. Grafted SiNPs were then coated with fluoroalkylsilane to lower the surface energy of the membrane. The fabricated membrane showed excellent omniphobicity, as demonstrated by its wetting resistance to various low surface tension liquids, including ethanol with a surface tension of 22.1 mN/m. As a promising application, the prepared omniphobic membrane was tested in direct contact membrane distillation to extract water from highly saline feed solutions containing low surface tension substances, mimicking emerging industrial wastewaters (e.g., from shale gas production). While a control hydrophobic PVDF-HFP nanofiber membrane failed in the desalination/separation process due to low wetting resistance, our fabricated omniphobic membrane exhibited a stable desalination performance for 8 h of operation, successfully demonstrating clean water production from the low surface tension feedwater.

Surface Modified Biodegradable Electrospun Membranes as a Carrier for Human Embryonic Stem Cell-Derived Retinal Pigment Epithelial Cells.

PubMed

Sorkio, Anni; Porter, Patrick J; Juuti-Uusitalo, Kati; Meenan, Brian J; Skottman, Heli; Burke, George A

2015-09-01

Human embryonic stem cell-derived retinal pigment epithelial (hESC-RPE) cells are currently undergoing clinical trials to treat retinal degenerative diseases. Transplantation of hESC-RPE cells in conjuction with a supportive biomaterial carrier holds great potential as a future treatment for retinal degeneration. However, there has been no such biodegradable material that could support the growth and maturation of hESC-RPE cells so far. The primary aim of this work was to create a thin porous poly (L-lactide-co-caprolactone) (PLCL) membrane that could promote attachment, proliferation, and maturation of the hESC-RPE cells in serum-free culture conditions. The PLCL membranes were modified by atmospheric pressure plasma processing and coated with collagen IV to enhance cell growth and maturation. Permeability of the membranes was analyzed with an Ussing chamber system. Analysis with scanning electron microscopy, contact angle measurement, atomic force microscopy, and X-ray photoelectron spectroscopy demonstrated that plasma surface treatment augments the surface properties of the membrane, which enhances the binding and conformation of the protein. Cell proliferation assays, reverse transcription-polymerase chain reaction, indirect immunofluoresence staining, trans-epithelial electrical resistance measurements, and in vitro phagocytosis assay clearly demonstrated that the plasma treated PLCL membranes supported the adherence, proliferation, maturation and functionality of hESC-RPE cells in serum-free culture conditions. Here, we report for the first time, how PLCL membranes can be modified with atmospheric pressure plasma processing to enable the formation of a functional hESC-RPE monolayer on a porous biodegradable substrate, which have a potential as a tissue-engineered construct for regenerative retinal repair applications.

Design of electrospun nanofibrous mats for osteogenic differentiation of mesenchymal stem cells.

PubMed

Wang, Shige; Hu, Fei; Li, Jingchao; Zhang, Shuping; Shen, Mingwu; Huang, Mingxian; Shi, Xiangyang

2017-05-26

The clinical translation potential of mesenchymal stem cells (MSCs) in regenerative medicine has been greatly exploited. With the merits of high surface area to volume ratio, facile control of components, well retained topography, and the capacity to mimic the native extracellular matrix (ECM), nanofibers have received a great deal of attention as bone tissue engineering scaffolds. Electrospinning has been considered as an efficient approach for scale-up fabrication of nanofibrous materials. Electrospun nanofibers are capable of stimulating cell-matrix interaction to form a cell niche, directing cellular behavior, and promoting the MSCs adhesion and proliferation. In this review, we give a comprehensive literature survey on the mechanisms of electrospun nanofibers in supporting the MSCs differentiation. Specifically, the influences of biological and physical osteogenic inductive cues on the MSCs osteogenic differentiation are reviewed. Along with the significant advances in the field, current research challenges and future perspectives are also discussed. Copyright © 2017 Elsevier Inc. All rights reserved.

Acoustoelectric Effect on the Responses of SAW Sensors Coated with Electrospun ZnO Nanostructured Thin Film

PubMed Central

Tasaltin, Cihat; Ebeoglu, Mehmet Ali; Ozturk, Zafer Ziya

2012-01-01

In this study, zinc oxide (ZnO) was a very good candidate for improving the sensitivity of gas sensor technology. The preparation of an electrospun ZnO nanostructured thin film on a 433 MHz Rayleigh wave based Surface Acoustic Wave (SAW) sensor and the investigation of the acoustoelectric effect on the responses of the SAW sensor are reported. We prepared an electrospun ZnO nanostructured thin film on the SAW devices by using an electrospray technique. To investigate the dependency of the sensor response on the structure and the number of the ZnO nanoparticles, SAW sensors were prepared with different coating loads. The coating frequency shifts were adjusted to fall between 100 kHz and 2.4 MHz. The sensor measurements were performed against VOCs such as acetone, trichloroethylene, chloroform, ethanol, n-propanol and methanol vapor. The sensor responses of n-propanol have opposite characteristics to the other VOCs, and we attributed these characteristics to the elastic effect/acoustoelectric effect.

Neurogenic differentiation of human umbilical cord mesenchymal stem cells on aligned electrospun polypyrrole/polylactide composite nanofibers with electrical stimulation

NASA Astrophysics Data System (ADS)

Zhou, Junfeng; Cheng, Liang; Sun, Xiaodan; Wang, Xiumei; Jin, Shouhong; Li, Junxiang; Wu, Qiong

2016-09-01

Adult central nervous system (CNS) tissue has a limited capacity to recover after trauma or disease. Recent medical cell therapy using polymeric biomaterialloaded stem cells with the capability of differentiation to specific neural population has directed focuses toward the recovery of CNS. Fibers that can provide topographical, biochemical and electrical cues would be attractive for directing the differentiation of stem cells into electro-responsive cells such as neuronal cells. Here we report on the fabrication of an electrospun polypyrrole/polylactide composite nanofiber film that direct or determine the fate of mesenchymal stem cells (MSCs), via combination of aligned surface topography, and electrical stimulation (ES). The surface morphology, mechanical properties and electric properties of the film were characterized. Comparing with that on random surface film, expression of neurofilament-lowest and nestin of human umbilical cord mesenchymal stemcells (huMSCs) cultured on film with aligned surface topography and ES were obviously enhanced. These results suggest that aligned topography combining with ES facilitates the neurogenic differentiation of huMSCs and the aligned conductive film can act as a potential nerve scaffold.

Effect of surface modification of nanofibres with glutamic acid peptide on calcium phosphate nucleation and osteogenic differentiation of marrow stromal cells.

PubMed

Karaman, Ozan; Kumar, Ankur; Moeinzadeh, Seyedsina; He, Xuezhong; Cui, Tong; Jabbari, Esmaiel

2016-02-01

Biomineralization is mediated by extracellular matrix (ECM) proteins with amino acid sequences rich in glutamic acid. The objective of this study was to investigate the effect of calcium phosphate deposition on aligned nanofibres surface-modified with a glutamic acid peptide on osteogenic differentiation of rat marrow stromal cells. Blend of EEGGC peptide (GLU) conjugated low molecular weight polylactide (PLA) and high molecular weight poly(lactide-co-glycolide) (PLGA) was electrospun to form aligned nanofibres (GLU-NF). The GLU-NF microsheets were incubated in a modified simulated body fluid for nucleation of calcium phosphate crystals on the fibre surface. To achieve a high calcium phosphate to fibre ratio, a layer-by-layer approach was used to improve diffusion of calcium and phosphate ions inside the microsheets. Based on dissipative particle dynamics simulation of PLGA/PLA-GLU fibres, > 80% of GLU peptide was localized to the fibre surface. Calcium phosphate to fibre ratios as high as 200%, between those of cancellous (160%) and cortical (310%) bone, was obtained with the layer-by-layer approach. The extent of osteogenic differentiation and mineralization of marrow stromal cells seeded on GLU-NF microsheets was directly related to the amount of calcium phosphate deposition on the fibres prior to cell seeding. Expression of osteogenic markers osteopontin, alkaline phosphatase (ALP), osteocalcin and type 1 collagen increased gradually with calcium phosphate deposition on GLU-NF microsheets. Results demonstrate that surface modification of aligned synthetic nanofibres with EEGGC peptide dramatically affects nucleation and growth of calcium phosphate crystals on the fibres leading to increased osteogenic differentiation of marrow stromal cells and mineralization. Copyright © 2013 John Wiley & Sons, Ltd.

Feedback System Control Optimized Electrospinning for Fabrication of an Excellent Superhydrophobic Surface.

PubMed

Yang, Jian; Liu, Chuangui; Wang, Boqian; Ding, Xianting

2017-10-13

Superhydrophobic surface, as a promising micro/nano material, has tremendous applications in biological and artificial investigations. The electrohydrodynamics (EHD) technique is a versatile and effective method for fabricating micro- to nanoscale fibers and particles from a variety of materials. A combination of critical parameters, such as mass fraction, ratio of N, N-Dimethylformamide (DMF) to Tetrahydrofuran (THF), inner diameter of needle, feed rate, receiving distance, applied voltage as well as temperature, during electrospinning process, to determine the morphology of the electrospun membranes, which in turn determines the superhydrophobic property of the membrane. In this study, we applied a recently developed feedback system control (FSC) scheme for rapid identification of the optimal combination of these controllable parameters to fabricate superhydrophobic surface by one-step electrospinning method without any further modification. Within five rounds of experiments by testing totally forty-six data points, FSC scheme successfully identified an optimal parameter combination that generated electrospun membranes with a static water contact angle of 160 degrees or larger. Scanning electron microscope (SEM) imaging indicates that the FSC optimized surface attains unique morphology. The optimized setup introduced here therefore serves as a one-step, straightforward, and economic approach to fabricate superhydrophobic surface with electrospinning approach.

Zein/Poly(3-hydroxybutyrate-co-4-hydroxybutyrate) electrospun blend fiber scaffolds: Preparation, characterization and cytocompatibility.

PubMed

Zhijiang, Cai; Qin, Zhang; Xianyou, Song; Yuanpei, Liu

2017-02-01

In the present work, a series of Zein/Poly(3-hydroxybutyrate-co-4-hydroxybutyrate) blend fiber scaffolds have been prepared by electrospinning method. The electrospun fibers showed a circular and uniform morphology with random distribution. The blend fiber scaffolds possessed well interconnected porous fibrous network structure with high porosity and large aspect surface areas. The FTIR and XPS spectra of Zein/P(3HB-co-4HB) blend fibers demonstrated the same characteristics to that of pure Zein and P(3HB-co-4HB) electrospun fibers. However, Zein might hinder the crystallization of P(3HB-co-4HB) owing to the formation of weak intermolecular interactions, which can affect the preferential orientation of P(3HB-co-4HB) molecules. Only one glass transition temperature (Tg) can be detected for electrospun Zein/P(3HB-co-4HB) blend fiber scaffolds implying the miscibility of Zein and P(3HB-co-4HB) in the blend fibers. The Zein/P(3HB-co-4HB) blend fiber scaffolds showed about 50% of improvement in tensile strength and 400% of increase in elongation at break by increasing P(3HB-co-4HB) content from 20% to 80%. The cytocompatibility of the Zein/P(3HB-co-4HB) blend fiber scaffolds was preliminarily evaluated by cell culture in vitro. The as-prepared electrospun Zein/P(3HB-co-4HB) blend fiber scaffolds with the characteristics of good biocompatibility, excellent pore characteristic as well as sufficient mechanical properties should be more promising for applications as tissue engineering scaffold. Copyright © 2016 Elsevier B.V. All rights reserved.

Attachment of nanoparticulate drug-release systems on poly(ε-caprolactone) nanofibers via a graftpolymer as interlayer.

PubMed

de Cassan, Dominik; Sydow, Steffen; Schmidt, Nadeschda; Behrens, Peter; Roger, Yvonne; Hoffmann, Andrea; Hoheisel, Anna Lena; Glasmacher, Birgit; Hänsch, Robert; Menzel, Henning

2018-03-01

Electrospun poly(ε-caprolactone) (PCL) fiber mats are modified using a chitosan grafted with PCL (CS-g-PCL), to improve the biological performance and to enable further modifications. The graft copolymer is immobilized by the crystallization of the PCL grafts on the PCL fiber surface as binding mechanism. In this way, the surface of the fibers is covered with chitosan bearing cationic amino groups, which allow adsorption of oppositely charged nanoparticulate drug-delivery systems. The modification of the fiber mats and the attachment of the drug delivery systems are easy and scalable dip processes. The process is also versatile; it is possible to attach different polymeric and inorganic nanoparticulate drug-release systems of cationic or anionic nature. The modifications are verified using scanning electron microscopy (SEM) and confocal laser scanning microscopy (CLSM). As proof of principle, the release of ciprofloxacin from silica nanoparticles attached to the modified fiber mats is shown; however, the method is also suited for other biologically active substances including growth factors. The initial cellular attachment and proliferation as well as vitality of the cells is improved by the modification with CS-g-PCL and is further influenced by the type of the drug delivery system attached. Hence, this method can be used to transfer PCL fiber mats into bioactive implants for in-situ tissue engineering applications. Copyright © 2018 Elsevier B.V. All rights reserved.

Evaluation of polyacrylonitrile electrospun nano-fibrous mats as leukocyte removal filter media.

PubMed

Pourbaghi, Raha; Zarrebini, Mohammad; Semnani, Dariush; Pourazar, Abbasali; Akbari, Nahid; Shamsfar, Reihaneh

2018-07-01

Removal of leukocytes from blood products is the most effective means for elimination of undesirable side effects and prevention of possible reactions in recipients. Micro-fibrous mats are currently used for removal of leukocytes from blood. In this study, samples of electrospun nano-fibrous mats were produced. The performance of the produced electrospun nano-fibrous mats as means of leukocytes removal from fresh whole blood was both evaluated and compared with that of commercially available micro-fibrous mats. In order to produce the samples, polyacrylonitrile (PAN) nano-fibrous mats were made under different electrospinning conditions. Mean fiber diameter, pore characterization and surface roughness of the PAN nano-fibrous mats were determined using image processing technique. In order to evaluate the surface tension of the fabricated mats, water contact angle was measured. The leukocyte removal performance, erythrocytes recovery percent and hemolysis rate of the nano-fibrous mats were compared. The effectiveness of nano-fibrous mats in removing leukocyte was established using both scanning electron microscope and optical microscope. Results showed that for given weight, the fabricated nano-fibrous mats were not only more efficient but also more cost-effective than their commercial counterparts. Results confirmed that changes in mean fiber diameter, the number of layer and weight of each layer in the absence of any chemical reaction or physical surface modification, the fabricated nano-fibrous mats were able to remove 5-log of leukocytes. © 2017 Wiley Periodicals, Inc. J Biomed Mater Res Part B: Appl Biomater, 106B: 1759-1769, 2018. © 2017 Wiley Periodicals, Inc.

Use of lecithin to control fiber morphology in electrospun poly (ɛ-caprolactone) scaffolds for improved tissue engineering applications.

PubMed

Coverdale, Benjamin D M; Gough, Julie E; Sampson, William W; Hoyland, Judith A

2017-10-01

We elucidate the effects of incorporating surfactants into electrospun poly (ɛ-caprolactone) (PCL) scaffolds on network homogeneity, cellular adherence and osteogenic differentiation. Lecithin was added with a range of concentrations to PCL solutions, which were electrospun to yield functionalized scaffolds. Addition of lecithin yielded a dose-dependent reduction in scaffold hydrophobicity, whilst reducing fiber width and hence increasing specific surface area. These changes in scaffold morphology were associated with increased cellular attachment of Saos-2 osteoblasts 3-h postseeding. Furthermore, cells on scaffolds showed comparable proliferation over 14 days of incubation to TCP controls. Through model-based interpretation of image analysis combined with gravimetric estimates of porosity, lecithin is shown to reduce scaffold porosity and mean pore size. Additionally, lecithin incorporation is found to reduce fiber curvature, resulting in increased scaffold specific elastic modulus. Low concentrations of lecithin were found to induce upregulation of several genes associated with osteogenesis in primary mesenchymal stem cells. The results demonstrate that functionalization of electrospun PCL scaffolds with lecithin can increase the biocompatibility and regenerative potential of these networks for bone tissue engineering applications. © 2017 The Authors Journal of Biomedical Materials Research Part A Published by Wiley Periodicals, Inc. J Biomed Mater Res Part A: 105A: 2865-2874, 2017. © 2017 The Authors Journal of Biomedical Materials Research Part A Published by Wiley Periodicals, Inc.

Synthetic vs natural scaffolds for human limbal stem cells

PubMed Central

Tominac Trcin, Mirna; Dekaris, Iva; Mijović, Budimir; Bujić, Marina; Zdraveva, Emilija; Dolenec, Tamara; Pauk-Gulić, Maja; Primorac, Dragan; Crnjac, Josip; Špoljarić, Branimira; Mršić, Gordan; Kuna, Krunoslav; Špoljarić, Daniel; Popović, Maja

2015-01-01

Aim To investigate the impact of synthetic electrospun polyurethane (PU) and polycaprolactone (PCL) nanoscaffolds, before and after hydrolytic surface modification, on viability and differentiation of cultured human eye epithelial cells, in comparison with natural scaffolds: fibrin and human amniotic membrane. Methods Human placenta was taken at elective cesarean delivery. Fibrin scaffolds were prepared from commercial fibrin glue kits. Nanoscaffolds were fabricated by electrospinning. Limbal cells were isolated from surpluses of human cadaveric cornea and seeded on feeder 3T3 cells. The scaffolds used for viability testing and immunofluorescence analysis were amniotic membrane, fibrin, PU, and PCL nanoscaffolds, with or without prior NaOH treatment. Results Scanning electron microscope photographs of all tested scaffolds showed good colony spreading of seeded limbal cells. There was a significant difference in viability performance between cells with highest viability cultured on tissue culture plastic and cells cultured on all other scaffolds. On the other hand, electrospun PU, PCL, and electrospun PCL treated with NaOH had more than 80% of limbal cells positive for stem cell marker p63 compared to only 27%of p63 positive cells on fibrin. Conclusion Natural scaffolds, fibrin and amniotic membrane, showed better cell viability than electrospun scaffolds. On the contrary, high percentages of p63 positive cells obtained on these scaffolds still makes them good candidates for efficient delivery systems for therapeutic purposes. PMID:26088849

Adsorption of ciprofloxacin, bisphenol and 2-chlorophenol on electrospun carbon nanofibers: in comparison with powder activated carbon.

PubMed

Li, Xiaona; Chen, Shuo; Fan, Xinfei; Quan, Xie; Tan, Feng; Zhang, Yaobin; Gao, Jinsuo

2015-06-01

Carbon nanofibers (CNFs) were prepared by electrospun polyacrylonitrile (PAN) polymer solutions followed by thermal treatment. For the first time, the influence of stabilization procedure on the structure properties of CNFs was explored to improve the adsorption capacity of CNFs towards the environmental pollutants from aqueous solution. The adsorption of three organic chemicals including ciprofloxacin (CIP), bisphenol (BPA) and 2-chlorophenol (2-CP) on electrospun CNFs with high surface area of 2326m(2)/g and micro/mesoporous structure characteristics were investigated. The adsorption affinities were compared with that of the commercial powder activated carbon (PAC). The adsorption kinetics and isotherms showed that the maximum adsorption capacities (qm) of CNFs towards the three pollutants are sequenced in the order of CIP>BPA>2-CP, which are 2.6-fold (CIP), 1.6-fold (BPA) and 1.1-fold (2-CP) increase respectively in comparison with that of PAC adsorption. It was assumed that the micro/mesoporous structure of CNFs, molecular size of the pollutants and the π electron interaction play important roles on the high adsorption capacity exhibited by CNFs. In addition, electrostatic interaction and hydrophobic interaction also contribute to the adsorption of CNFs. This study demonstrates that the electrospun CNFs are promising adsorbents for the removal of pollutants from aqueous solutions. Copyright © 2015 Elsevier Inc. All rights reserved.

Surface Entrapment of Fibronectin on Electrospun PLGA Scaffolds for Periodontal Tissue Engineering

PubMed Central

Gritsch, Kerstin; Salles, Vincent; Attik, Ghania N.; Grosgogeat, Brigitte

2014-01-01

Abstract Nowadays, the challenge in the tissue engineering field consists in the development of biomaterials designed to regenerate ad integrum damaged tissues. Despite the current use of bioresorbable polyesters such as poly(l-lactide) (PLA), poly(d,l-lactide-co-glycolide) (PLGA), and poly-ɛ-caprolactone in soft tissue regeneration researches, their hydrophobic properties negatively influence the cell adhesion. Here, to overcome it, we have developed a fibronectin (FN)-functionalized electrospun PLGA scaffold for periodontal ligament regeneration. Functionalization of electrospun PLGA scaffolds was performed by alkaline hydrolysis (0.1 or 0.01 M NaOH). Then, hydrolyzed scaffolds were coated by simple deposition of an FN layer (10 μg/mL). FN coating was evidenced by X-ray photoelectron analysis. A decrease of contact angle and greater cell adhesion to hydrolyzed, FN-coated PLGA scaffolds were noticed. Suitable degradation behavior without pH variations was observed for all samples up to 28 days. All treated materials presented strong shrinkage, fiber orientation loss, and collapsed fibers. However, functionalization process using 0.01 M NaOH concentration resulted in unchanged scaffold porosity, preserved chemical composition, and similar mechanical properties compared with untreated scaffolds. The proposed simplified method to functionalize electrospun PLGA fibers is an efficient route to make polyester scaffolds more biocompatible and shows potential for tissue engineering. PMID:24940563

Superhydrophilic graphene oxide@electrospun cellulose nanofiber hybrid membrane for high-efficiency oil/water separation.

PubMed

Ao, Chenghong; Yuan, Wei; Zhao, Jiangqi; He, Xu; Zhang, Xiaofang; Li, Qingye; Xia, Tian; Zhang, Wei; Lu, Canhui

2017-11-01

Inspired from fishscales, membranes with special surface wettability have been applied widely for the treatment of oily waste water. Herein, a novel superhydrophilic graphene oxide (GO)@electrospun cellulose nanofiber (CNF) membrane was successfully fabricated. This membrane exhibited a high separation efficiency, excellent antifouling properties, as well as a high flux for the gravity-driven oil/water separation. Moreover, the GO@CNF membrane was capable to effectively separate oil/water mixtures in a broad pH range or with a high concentration of salt, suggesting that this membrane was quite promising for future real-world practice in oil spill cleanup and oily wastewater treatment. Copyright © 2017 Elsevier Ltd. All rights reserved.

Process of making titanium carbide (TiC) nano-fibrous felts

DOEpatents

Fong, Hao; Zhang, Lifeng; Zhao, Yong; Zhu, Zhengtao

2015-01-13

A method of synthesizing mechanically resilient titanium carbide (TiC) nanofibrous felts comprising continuous nanofibers or nano-ribbons with TiC crystallites embedded in carbon matrix, comprising: (a) electrospinning a spin dope for making precursor nanofibers with diameters less than 0.5 J.Lm; (b) overlaying the nanofibers to produce a nanofibrous mat (felt); and then (c) heating the nano-felts first at a low temperature, and then at a high temperature for making electrospun continuous nanofibers or nano-ribbons with TiC crystallites embedded in carbon matrix; and (d) chlorinating the above electrospun nano-felts at an elevated temperature to remove titanium for producing carbide derived carbon (CDC) nano-fibrous felt with high specific surface areas.

In situ mineralization of hydroxyapatite on electrospun chitosan-based nanofibrous scaffolds.

PubMed

Yang, Dongzhi; Jin, Yu; Zhou, Yingshan; Ma, Guiping; Chen, Xiangmei; Lu, Fengmin; Nie, Jun

2008-03-10

A biocomposite of hydroxyapatite (HAp) with electrospun nanofibrous scaffolds was prepared by using chitosan/polyvinyl alcohol (CS/PVA) and N-carboxyethyl chitosan/PVA (CECS/PVA) electrospun membranes as organic matrix, and HAp was formed in supersaturated CaCl2 and KH2PO4 solution. The influences of carboxylic acid groups in CECS/PVA fibrous scaffold and polyanionic additive poly(acrylic acid) (PAA) in the incubation solution on the crystal distribution of the HAp were investigated. Field-emission scanning electron microscopy (FE-SEM), energy-dispersive spectroscopy (EDS), wide-angle X-ray diffraction (WAXD), and Fourier transform infrared (FTIR) were used to characterize the morphology and structure of the deposited mineral phase on the scaffolds. It was found that addition of PAA to the mineral solution and use of matrix with carboxylic acid groups promoted mineral growth and distribution of HAp. MTT testing and SEM imaging from mouse fibroblast (L929) cell culture revealed the attachment and growth of mouse fibroblast on the surface of biocomposite scaffold, and that the cell morphology and viability were satisfactory for the composite to be used in bioapplications.

Copper ion sensing with fluorescent electrospun nanofibers.

PubMed

Ongun, Merve Zeyrek; Ertekin, Kadriye; Gocmenturk, Mustafa; Ergun, Yavuz; Suslu, Aslıhan

2012-05-01

In this work, the use of electrospun nanofibrous materials as highly responsive fluorescence quenching-based copper sensitive chemosensor is reported. Poly(methyl methacrylate) and ethyl cellulose were used as polymeric support materials. Sensing slides were fabricated by electrospinning technique. Copper sensors based on the change in the fluorescence signal intensity of fluoroionophore; N'-3-(4-(dimethylamino phenly)allylidene)isonicotinohydrazide. The sensor slides exhibited high sensitivities due to the high surface area of the nanofibrous membrane structures. The preliminary results of Stern-Volmer analysis show that the sensitivities of electrospun nanofibrous membranes to detect Cu(II) ions are 6-20-fold higher than those of the continuous thin films. By this way we obtained linear calibration plots for Cu(II) ions in the concentration range of 10(-12)-10(-5)M. The response times of the sensing slides were less than 1 min. Stability of the employed ionophore in the matrix materials was excellent and when stored in the ambient air of the laboratory there was no significant drift in signal intensity after 6 months. Our stability tests are still in progress. Copyright © 2012 Elsevier B.V. All rights reserved.

Optimization of protein cross-linking in bicomponent electrospun scaffolds for therapeutic use

NASA Astrophysics Data System (ADS)

Papa, Antonio; Guarino, Vincenzo; Cirillo, Valentina; Oliviero, Olimpia; Ambrosio, Luigi

2015-12-01

Bio-instructive electrospun scaffolds based on the combination of synthetic polymers, such as PCL or PLLA, and natural polymers (e.g., collagen) have been extensively investigated as temporary extracellular matrix (ECM) analogues able to support cell proliferation and stem cell differentiation for the regeneration of several tissues. The growing use of natural polymers as carrier of bioactive molecules is introducing new ideas for the design of polymeric drug delivery systems based on electrospun fibers with improved bioavailability, therapeutic efficacy and programmed drug release. In particular, the release mechanism is driven by the use of water soluble proteins (i.e., collagen, gelatin) which fully degrade in in vitro microenvironment, thus delivering the active principles. However, these protein are generally rapidly digested by enzymes (i.e., collagenase) produced by many different cell types, both in vivo and in vitro with significant drawbacks in tissue engineering and controlled drug delivery. Here, we aim at investigating different chemical strategies to improve the in vitro stability and mechanical strength of scaffolds against enzymatic degradation, by modifying the biodegradation rates of proteins embedded in bicomponent fibers. By comparing scaffolds treated by different cross-linking agents (i.e., GC, EDC, BDDGE), we have provided an extensive morphological/chemical/physical characterization via SEM and TGA to identify the best conditions to control drug release via protein degradation from bicomponent fibers without compromising in vitro cell response.

Enhanced mechanical properties of thermosensitive chitosan hydrogel by silk fibers for cartilage tissue engineering.

PubMed

Mirahmadi, Fereshteh; Tafazzoli-Shadpour, Mohammad; Shokrgozar, Mohammad Ali; Bonakdar, Shahin

2013-12-01

Articular cartilage has limited repair capability following traumatic injuries and current methods of treatment remain inefficient. Reconstructing cartilage provides a new way for cartilage repair and natural polymers are often used as scaffold because of their biocompatibility and biofunctionality. In this study, we added degummed chopped silk fibers and electrospun silk fibers to the thermosensitive chitosan/glycerophosphate hydrogels to reinforce two hydrogel constructs which were used as scaffold for hyaline cartilage regeneration. The gelation temperature and gelation time of hydrogel were analyzed by the rheometer and vial tilting method. Mechanical characterization was measured by uniaxial compression, indentation and dynamic mechanical analysis assay. Chondrocytes were then harvested from the knee joint of the New Zealand white rabbits and cultured in constructs. The cell proliferation, viability, production of glycosaminoglycans and collagen type II were assessed. The results showed that mechanical properties of the hydrogel were significantly enhanced when a hybrid with two layers of electrospun silk fibers was made. The results of GAG and collagen type II in cell-seeded scaffolds indicate support of the chondrogenic phenotype for chondrocytes with a significant increase in degummed silk fiber-hydrogel composite for GAG content and in two-layer electrospun fiber-hydrogel composite for Col II. It was concluded that these two modified scaffolds could be employed for cartilage tissue engineering. © 2013.

Optimization of protein cross-linking in bicomponent electrospun scaffolds for therapeutic use

DOE Office of Scientific and Technical Information (OSTI.GOV)

Papa, Antonio; IMAST SCaRL, Piazza Bovio 22, 80133 Naples; Guarino, Vincenzo, E-mail: vincenzo.guarino@cnr.it

Bio-instructive electrospun scaffolds based on the combination of synthetic polymers, such as PCL or PLLA, and natural polymers (e.g., collagen) have been extensively investigated as temporary extracellular matrix (ECM) analogues able to support cell proliferation and stem cell differentiation for the regeneration of several tissues. The growing use of natural polymers as carrier of bioactive molecules is introducing new ideas for the design of polymeric drug delivery systems based on electrospun fibers with improved bioavailability, therapeutic efficacy and programmed drug release. In particular, the release mechanism is driven by the use of water soluble proteins (i.e., collagen, gelatin) which fullymore » degrade in in vitro microenvironment, thus delivering the active principles. However, these protein are generally rapidly digested by enzymes (i.e., collagenase) produced by many different cell types, both in vivo and in vitro with significant drawbacks in tissue engineering and controlled drug delivery. Here, we aim at investigating different chemical strategies to improve the in vitro stability and mechanical strength of scaffolds against enzymatic degradation, by modifying the biodegradation rates of proteins embedded in bicomponent fibers. By comparing scaffolds treated by different cross-linking agents (i.e., GC, EDC, BDDGE), we have provided an extensive morphological/chemical/physical characterization via SEM and TGA to identify the best conditions to control drug release via protein degradation from bicomponent fibers without compromising in vitro cell response.« less

Skeletal myotube formation enhanced by electrospun polyurethane carbon nanotube scaffolds

PubMed Central

Sirivisoot, Sirinrath; Harrison, Benjamin S

2011-01-01

Background This study examined the effects of electrically conductive materials made from electrospun single- or multiwalled carbon nanotubes with polyurethane to promote myoblast differentiation into myotubes in the presence and absence of electrical stimulation. Methods and results After electrical stimulation, the number of multinucleated myotubes on the electrospun polyurethane carbon nanotube scaffolds was significantly larger than that on nonconductive electrospun polyurethane scaffolds (5% and 10% w/v polyurethane). In the absence of electrical stimulation, myoblasts also differentiated on the electrospun polyurethane carbon nanotube scaffolds, as evidenced by expression of Myf-5 and myosin heavy chains. The myotube number and length were significantly greater on the electrospun carbon nanotubes with 10% w/v polyurethane than on those with 5% w/v polyurethane. The results suggest that, in the absence of electrical stimulation, skeletal myotube formation is dependent on the morphology of the electrospun scaffolds, while with electrical stimulation it is dependent on the electrical conductivity of the scaffolds. Conclusion This study indicates that electrospun polyurethane carbon nanotubes can be used to modulate skeletal myotube formation with or without application of electrical stimulation. PMID:22072883

Electrospun polymer nanofibers reinforced by tannic acid/Fe+++ complexes

USDA-ARS?s Scientific Manuscript database

Nanofibers and fibrous mats of polyvinyl alcohol (PVA) loaded with tannic acid (TA) and ferric ion (Fe+++) complexes (TA-Fe+++) were synthesized by the electrospinning technique. The spinning solutions were characterized for surface tension, electrical conductivity, and viscosity. It was found that ...

Fabrication of mineralized electrospun PLGA and PLGA/gelatin nanofibers and their potential in bone tissue engineering.

PubMed

Meng, Z X; Li, H F; Sun, Z Z; Zheng, W; Zheng, Y F

2013-03-01

Surface mineralization is an effective method to produce calcium phosphate apatite coating on the surface of bone tissue scaffold which could create an osteophilic environment similar to the natural extracellular matrix for bone cells. In this study, we prepared mineralized poly(D,L-lactide-co-glycolide) (PLGA) and PLGA/gelatin electrospun nanofibers via depositing calcium phosphate apatite coating on the surface of these nanofibers to fabricate bone tissue engineering scaffolds by concentrated simulated body fluid method, supersaturated calcification solution method and alternate soaking method. The apatite products were characterized by the scanning electron microscopy (SEM), Fourier transform-infrared spectroscopy (FT-IR), and X-ray diffractometry (XRD) methods. A large amount of calcium phosphate apatite composed of dicalcium phosphate dihydrate (DCPD), hydroxyapatite (HA) and octacalcium phosphate (OCP) was deposited on the surface of resulting nanofibers in short times via three mineralizing methods. A larger amount of calcium phosphate was deposited on the surface of PLGA/gelatin nanofibers rather than PLGA nanofibers because gelatin acted as nucleation center for the formation of calcium phosphate. The cell culture experiments revealed that the difference of morphology and components of calcium phosphate apatite did not show much influence on the cell adhesion, proliferation and activity. Copyright © 2012 Elsevier B.V. All rights reserved.

Electrospinning onto Insulating Substrates by Controlling Surface Wettability and Humidity

NASA Astrophysics Data System (ADS)

Choi, WooSeok; Kim, Geon Hwee; Shin, Jung Hwal; Lim, Geunbae; An, Taechang

2017-11-01

We report a simple method for electrospinning polymers onto flexible, insulating substrates by controlling the wettability of the substrate surface. Water molecules were adsorbed onto the surface of a hydrophilic polymer substrate by increasing the local humidity around the substrate. The adsorbed water was used as the ground electrode for electrospinning. The electrospun fibers were deposited only onto hydrophilic areas of the substrate, allowing for patterning through wettability control. Direct writing of polymer fiber was also possible through near-field electrospinning onto a hydrophilic surface.

Fabrication of polyurethane and polyurethane based composite fibres by the electrospinning technique for soft tissue engineering of cardiovascular system.

PubMed

Kucinska-Lipka, J; Gubanska, I; Janik, H; Sienkiewicz, M

2015-01-01

Electrospinning is a unique technique, which provides forming of polymeric scaffolds for soft tissue engineering, which include tissue scaffolds for soft tissues of the cardiovascular system. Such artificial soft tissues of the cardiovascular system may possess mechanical properties comparable to native vascular tissues. Electrospinning technique gives the opportunity to form fibres with nm- to μm-scale in diameter. The arrangement of obtained fibres and their surface determine the biocompatibility of the scaffolds. Polyurethanes (PUs) are being commonly used as a prosthesis of cardiovascular soft tissues due to their excellent biocompatibility, non-toxicity, elasticity and mechanical properties. PUs also possess fine spinning properties. The combination of a variety of PU properties with an electrospinning technique, conducted at the well tailored conditions, gives unlimited possibilities of forming novel polyurethane materials suitable for soft tissue scaffolds applied in cardiovascular tissue engineering. This paper can help researches to gain more widespread and deeper understanding of designing electrospinable PU materials, which may be used as cardiovascular soft tissue scaffolds. In this paper we focus on reagents used in PU synthesis designed to increase PU biocompatibility (polyols) and biodegradability (isocyanates). We also describe suggested surface modifications of electrospun PUs, and the direct influence of surface wettability on providing enhanced biocompatibility of scaffolds. We indicate a great influence of electrospinning parameters (voltage, flow rate, working distance) and used solvents (mostly DMF, THF and HFIP) on fibre alignment and diameter - what impacts the biocompatibility and hemocompatibility of such electrospun PU scaffolds. Moreover, we present PU modifications with natural polymers with novel approach applied in electrospinning of PU scaffolds. This work may contribute with further developing of novel electrospun PUs, which may be applied as soft tissue scaffolds of the cardiovascular system. Copyright © 2014. Published by Elsevier B.V.

Gold nanoparticles-decorated electrospun poly(N-vinyl-2-pyrrolidone) nanofibers with tunable size and coverage density for nanomolar detection of single and binary component dyes by surface-enhanced raman spectroscopy

NASA Astrophysics Data System (ADS)

Kurniawan, Alfin; Wang, Meng-Jiy

2017-09-01

The application of the electrospun nanomaterials to surface-enhanced Raman spectroscopy (SERS) is a rapidly evolving field which holds potential for future developments in the generation of portable plasmonic-based detection platforms. In this study, a simple approach to fabricate electrospun poly(N-vinylpyrrolidone) (PVP) mats decorated with gold nanoparticles (AuNPs) by combining electrospinning and calcination was presented. AuNPs were decorated on the fiber mat surface through electrostatic interactions between positively charged aminosilane groups and negatively charged AuNPs. The size and coverage density of AuNPs on the fiber mats could be tuned by varying the calcination temperature. Calcination of AuNPs-decorated PVP fibers at 500 °C-700 °C resulted in the uniform decoration of high density AuNPs with very narrow gaps on every single fiber, which in turn contribute to strong electromagnetic SERS enhancement. The robust free-standing AuNPs-decorated mat which calcined at 500 °C (500/AuNPs-F) exhibited high SERS activity toward cationic (methylene blue, MB) and anionic (methyl orange, MO) dyes in single and binary systems with a detection range from tens of nM to a few hundred μM. The fabricated SERS substrate demonstrated high reproducibility with the spot-to-spot variation in SERS signal intensities was ±10% and ±12% for single and binary dye systems, respectively. The determination of MB and MO in spiked river water and tap water with 500/AuNPs-F substrate gave satisfactory results in terms of the percent spike recoveries (ranging from 92.6%-96.6%) and reproducibility (%RSD values less than 15 for all samples).

Development of Electrospun Nanomaterials and their Applications in Separation Science

NASA Astrophysics Data System (ADS)

Newsome, Toni Elwell

In separations, efficiency is inversely related to the diameter of the sorbent particles of the stationary phase. Thus, materials research in separation science has primarily been directed towards reducing the diameter of the sorbent particle used in the stationary phase. In this dissertation, innovative methods designed for the fabrication and application of electrospun sorbent nanomaterials for separation science are described. Electrospinning is a facile, cost-effective technique that relies on repulsive electrostatic forces to produce nanofibers from a viscoelastic solution. Here, electrospinning is used to generate polymer, carbon, and silica-based nanofibers which are employed as sorbent nanomaterials in extractions and separations. Electrospun carbon nanofibers have proven to be ideal extractive phases for solid-phase microextraction (SPME) when coupled to gas chromatography (GC) for headspace sampling of volatile analytes. Herein, these carbon nanofibers were employed in the direct extraction of nonvolatile analytes and coupled to liquid chromatography (LC) for the first time. The high surface area of the coatings led to enhanced extraction efficiencies; they offered a 3-33 fold increase in efficiency relative to a commercial SPME phase. Carbon nanofibers proved to be stable when immersed in liquids common to LC demonstrating the enhanced stability of these coatings in SPME coupled to LC relative to conventional SPME fibers. The enhanced chemical and mechanical stability of the carbon SPME coatings considerably expanded the range of compounds applicable to SPME and extended the lifetimes of the fibers. Electrospun nanofibers have also proven to be ideal stationary phases in ultra-thin layer chromatography (UTLC). Nanofibers provide faster separations and enhanced separation efficiencies compared to commercial particle-based stationary phases in a relatively short distance. Here, the electrospun-UTLC technology was extended for the first time to nanofibers composed of silica, the most commonly used surface for TLC. An electrospinning method was optimized to produce silica-based nanofibers with the smallest diameter possible (300-380 nm) while maintaining homogenous nanofiber morphology. Highly efficient separations were performed in 15 mm with observed plate heights as low as 8.6 mum. Silica-based nanofibers proved to be chemically stable with a wide variety of TLC reagents demonstrating the enhanced compatibility of these phases with common TLC methods relative to polymer and carbon nanofiber UTLC plates. The extension of electrospun UTLC to silica-based nanofibers vastly expanded the range of analytes and TLC methods which can be used with this technology. The main disadvantage of conventional TLC development methods is that the mobile phase velocity decreases with increasing separation distance. Here, the chromatographic performance of electrospun polymer stationary phases was further improved by using a forced-flow mobile phase in planar electrochromatography (PEC) in which mobile phase velocity does not diminish with increasing distance. Separations were performed on polymer nanofiber UTLC plates in 1-2 min. Compared to UTLC, PEC offered unique selectivity, decreased analysis times (> 4 times faster), and enhanced efficiency (2-3 times lower plate height). In addition, two-dimensional (2D) separations of a complex analyte mixture using UTLC followed by PEC required only 11 min and exhibited a significant increase in separation number (70-77).

Fabrication of functional PLGA-based electrospun scaffolds and their applications in biomedical engineering.

PubMed

Zhao, Wen; Li, Jiaojiao; Jin, Kaixiang; Liu, Wenlong; Qiu, Xuefeng; Li, Chenrui

2016-02-01

Electrospun PLGA-based scaffolds have been applied extensively in biomedical engineering, such as tissue engineering and drug delivery system. Due to lack of the recognition sites on cells, hydropholicity and single-function, the applications of PLGA fibrous scaffolds are limited. In order to tackle these issues, many works have been done to obtain functional PLGA-based scaffolds, including surface modifications, the fabrication of PLGA-based composite scaffolds and drug-loaded scaffolds. The functional PLGA-based scaffolds have significantly improved cell adhesion, attachment and proliferation. Moreover, the current study has summarized the applications of functional PLGA-based scaffolds in wound dressing, vascular and bone tissue engineering area as well as drug delivery system. Copyright © 2015 Elsevier B.V. All rights reserved.

Morphology and crystalline phase study of electrospun TiO2 SiO2 nanofibres

NASA Astrophysics Data System (ADS)

Ding, Bin; Kim, Hakyong; Kim, Chulki; Khil, Myungseob; Park, Soojin

2003-05-01

Nanofibres of TiO2-SiO2 (Ti:Si = 50: 50 mol%) with diameters of 50-400 nm were prepared by calcining electrospun nanofibres of polyvinyl acetate (PVac)/titania-silica composite as precursor. These PVac/titania-silica hybrid nanofibres were obtained from a homogenous solution of PVac with a sol-gel of titanium isopropoxide (TiP) and tetraethoxysilane by using the electrospinning technique. The nanofibres were characterized by scanning electron microscopy (SEM), wide-angle x-ray diffraction (WAXD), Fourier transform infrared (FTIR) spectroscopy and Brunauer-Emmett-Teller (BET) surface area. SEM, WAXD and FTIR results indicated that the morphology and crystalline phase of TiO2-SiO2 nanofibres were strongly influenced by the calcination temperature and the content of titania and silica in the nanofibres. Additionally, the BET results showed that the surface area of TiO2-SiO2 nanofibres was decreased with increasing calcination temperature and the content of titania and silica in nanofibres.

Biomedical Exploitation of Chitin and Chitosan via Mechano-Chemical Disassembly, Electrospinning, Dissolution in Imidazolium Ionic Liquids, and Supercritical Drying

PubMed Central

Muzzarelli, Riccardo A. A.

2011-01-01

Recently developed technology permits to optimize simultaneously surface area, porosity, density, rigidity and surface morphology of chitin-derived materials of biomedical interest. Safe and ecofriendly disassembly of chitin has superseded the dangerous acid hydrolysis and provides higher yields and scaling-up possibilities: the chitosan nanofibrils are finding applications in reinforced bone scaffolds and composite dressings for dermal wounds. Electrospun chitosan nanofibers, in the form of biocompatible thin mats and non-wovens, are being actively studied: composites of gelatin + chitosan + polyurethane have been proposed for cardiac valves and for nerve conduits; fibers are also manufactured from electrospun particles that self-assemble during subsequent freeze-drying. Ionic liquids (salts of alkylated imidazolium) are suitable as non-aqueous solvents that permit desirable reactions to occur for drug delivery purposes. Gel drying with supercritical CO2 leads to structures most similar to the extracellular matrix, even when the chitosan is crosslinked, or in combination with metal oxides of interest in orthopedics. PMID:22131955

Denaturing of single electrospun fibrinogen fibers studied by deep ultraviolet fluorescence microscopy.

PubMed

Kim, Jeongyong; Song, Hugeun; Park, Inho; Carlisle, Christine R; Bonin, Keith; Guthold, Martin

2011-03-01

Deep ultraviolet (DUV) microscopy is a fluorescence microscopy technique to image unlabeled proteins via the native fluorescence of some of their amino acids. We constructed a DUV fluorescence microscope, capable of 280 nm wavelength excitation by modifying an inverted optical microscope. Moreover, we integrated a nanomanipulator-controlled micropipette into this instrument for precise delivery of picoliter amounts of fluid to selected regions of the sample. In proof-of-principle experiments, we used this instrument to study, in situ, the effect of a denaturing agent on the autofluorescence intensity of single, unlabeled, electrospun fibrinogen nanofibers. Autofluorescence emission from the nanofibers was excited at 280 nm and detected at ∼350 nm. A denaturant solution was discretely applied to small, select sections of the nanofibers and a clear local reduction in autofluorescence intensity was observed. This reduction is attributed to the dissolution of the fibers and the unfolding of proteins in the fibers. Copyright © 2010 Wiley-Liss, Inc.

Recent advances in electrospun nanofibers for wound healing.

PubMed

Chen, Shixuan; Liu, Bing; Carlson, Mark A; Gombart, Adrian F; Reilly, Debra A; Xie, Jingwei

2017-06-01

Electrospun nanofibers represent a novel class of materials that show great potential in many biomedical applications including biosensing, regenerative medicine, tissue engineering, drug delivery and wound healing. In this work, we review recent advances in electrospun nanofibers for wound healing. This article begins with a brief introduction on the wound, and then discusses the unique features of electrospun nanofibers critical for wound healing. It further highlights recent studies that have used electrospun nanofibers for wound healing applications and devices, including sutures, multifunctional dressings, dermal substitutes, engineered epidermis and full-thickness skin regeneration. Finally, we finish with conclusions and future perspective in this field.

Impact of Electro-Magneto Concave Collector on the Characterizations of Electrospun Nanofibers

NASA Astrophysics Data System (ADS)

Shehata, Nader; Abdelkader, Mohamed

2018-05-01

We introduce a modified approach to produce aligned nanofibers through electro-magneto concave collectors. Both electric and magnetic fields distributions are simulated with COMSOL Multiphysics for different collectors including conventional, concave and modified concave collectors by adding magnetic discs in the back. Orientation matrices are evaluated for each collector in the study, and the highest degree of alignment is found to be with the modified concave collector with a percentage of 68%, followed by the concave collector with a percentage of 57%, which shows an improvement of the proposed method by adding a magnetic field. The generated nanofiber mats from the electro-magneto concave collector show improvements in both mechanical (Young's modulus = 117.66 MPa) and thermal properties compared to both concave and conventional collectors.

Trends in polymeric electrospun fibers and their use as oral biomaterials.

PubMed

Meireles, Agnes B; Corrêa, Daniella K; da Silveira, João Vw; Millás, Ana Lg; Bittencourt, Edison; de Brito-Melo, Gustavo Ea; González-Torres, Libardo A

2018-05-01

Electrospinning is one of the techniques to produce structured polymeric fibers in the micro or nano scale and to generate novel materials for biomedical proposes. Electrospinning versatility provides fibers that could support different surgical and rehabilitation treatments. However, its diversity in equipment assembly, polymeric materials, and functional molecules to be incorporated in fibers result in profusion of recent biomaterials that are not fully explored, even though the recognized relevance of the technique. The present article describes the main electrospun polymeric materials used in oral applications, and the main aspects and parameters of the technique. Natural and synthetic polymers, blends, and composites were identified from the available literature and recent developments. Main applications of electrospun fibers were focused on drug delivery systems, tissue regeneration, and material reinforcement or modification, although studies require further investigation in order to enable direct use in human. Current and potential usages as biomaterials for oral applications must motivate the development in the use of electrospinning as an efficient method to produce highly innovative biomaterials, over the next few years. Impact statement Nanotechnology is a challenge for many researchers that look for obtaining different materials behaviors by modifying characteristics at a very low scale. Thus, the production of nanostructured materials represents a very important field in bioengineering, in which the electrospinning technique appears as a suitable alternative. This review discusses and provides further explanation on this versatile technique to produce novel polymeric biomaterials for oral applications. The use of electrospun fibers is incipient in oral areas, mainly because of the unfamiliarity with the technique. Provided disclosure, possibilities and state of the art are aimed at supporting interested researchers to better choose proper materials, understand, and design new experiments. This work seeks to encourage many other researchers-Dentists, Biologists, Engineers, Pharmacists-to develop innovative materials from different polymers. We highlight synthetic and natural polymers as trends in treatments to motivate an advance in the worldwide discussion and exploration of this interdisciplinary field.

Encapsulation and immobilization of papain in electrospun nanofibrous membranes of PVA cross-linked with glutaraldehyde vapor.

PubMed

Moreno-Cortez, Iván E; Romero-García, Jorge; González-González, Virgilio; García-Gutierrez, Domingo I; Garza-Navarro, Marco A; Cruz-Silva, Rodolfo

2015-01-01

In this paper, papain enzyme (E.C. 3.4.22.2, 1.6 U/mg) was successfully immobilized in poly(vinyl alcohol) (PVA) nanofibers prepared by electrospinning. The morphology of the electrospun nanofibers was characterized by scanning electron microscopy (SEM) and the diameter distribution was in the range of 80 to 170 nm. The presence of the enzyme within the PVA nanofibers was confirmed by infrared spectroscopy (FTIR), X-ray photoelectron spectroscopy (XPS) and energy dispersive X-ray spectroscopy (EDXS) analyses. The maximum catalytic activity was reached when the enzyme loading was 13%. The immobilization of papain in the nanofiber membrane was achieved by chemical crosslinking with a glutaraldehyde vapor treatment (GAvt). The catalytic activity of the immobilized papain was 88% with respect to the free enzyme. The crosslinking time by GAvt to immobilize the enzyme onto the nanofiber mat was 24h, and the enzyme retained its catalytic activity after six cycles. The crosslinked samples maintained 40% of their initial activity after being stored for 14 days. PVA electrospun nanofibers are excellent matrices for the immobilization of enzymes due to their high surface area and their nanoporous structure. Copyright © 2015. Published by Elsevier B.V.

Optical CO2 sensing with ionic liquid doped electrospun nanofibers.

PubMed

Aydogdu, Sibel; Ertekin, Kadriye; Suslu, Aslihan; Ozdemir, Mehtap; Celik, Erdal; Cocen, Umit

2011-03-01

The first use of electrospun nanofibrous materials as highly responsive fluorescence quenching-based optical CO(2) sensors is reported. Poly(methyl methacrylate) and ethyl cellulose were used as polymeric materials. Sensing slides were fabricated by electrospinning technique. A fiber-optic bundle was used for the gas detection. CO(2) sensors based on the change in the fluorescence signal intensity of ion pair form of 8-hydroxypyrene-1,3,6-trisulfonic acid (HPTS). The sensor slides showed high sensitivities due to the high surface area-to-volume ratio of the nanofibrous membrane structures. The preliminary results of Stern-Volmer analysis show that the sensitivities of electrospun nanofibrous membranes to detect CO(2) are 24 to 120 fold higher than those of the thin film based sensors. The response times of the sensing reagents were short and the signal changes were fully reversible. The stability of ion pair form of HPTS in the employed matrix materials was excellent and when stored in the ambient air of the laboratory there was no significant drift in signal intensity after 7 months. Our stability tests are still in progress. © Springer Science+Business Media, LLC 2010

In vitro evaluation of crosslinked electrospun fish gelatin scaffolds.

PubMed

Gomes, S R; Rodrigues, G; Martins, G G; Henriques, C M R; Silva, J C

2013-04-01

Gelatin from cold water fish skin was electrospun, crosslinked and investigated as a substrate for the adhesion and proliferation of cells. Gelatin was first dissolved in either water or concentrated acetic acid and both solutions were successfully electrospun. Cross-linking was achieved via three different routes: glutaraldehyde vapor, genipin and dehydrothermal treatment. Solution's properties (surface tension, electrical conductivity and viscosity) and scaffold's properties (chemical bonds, weight loss and fiber diameters) were measured. Cellular viability was analyzed culturing 3T3 fibroblasts plated on the scaffolds and grown up to 7 days. The cells were fixed and observed with SEM or stained for DNA and F-actin and observed with confocal microscopy. In all scaffolds, the cells attached and spread with varying degrees. The evaluation of cell viability showed proliferation of cells until confluence in scaffolds crosslinked by glutaraldehyde and genipin; however the rate of growth in genipin crosslinked scaffolds was slow, recovering only by day five. The results using the dehydrothermal treatment were the less satisfactory. Our results show that glutaraldehyde treated fish gelatin is the most suitable substrate, of the three studied, for fibroblast adhesion and proliferation. Copyright © 2012 Elsevier B.V. All rights reserved.

Axial and radial nanostructures in electrospun polymer fibers

NASA Astrophysics Data System (ADS)

Greenfeld, Israel; Camposeo, Andrea; Tantussi, Francesco; Pagliara, Stefano; Fuso, Francesco; Allegrini, Maria; Pisignano, Dario; Zussman, Eyal

2013-03-01

The high tensional stresses during electrospinning of semidilute polymer solutions affect the dynamic conformation of the polymer network within the liquid jet, leaving a distinctive trace in the molecular structure after solidification. We investigated such effects in electrospun nanofibers made of conjugated polymers. Modeling the polymer network evolution during electrospinning showed that as the network stretches axially, it contracts towards the jet core. The model represents the semi-flexible conjugated polymer chains as flexible freely-jointed chains, whose joints are bonding defects. Using the conjugated polymer MEH-PPV dissolved in a mixture of THF and DMF solvents, and taking advantage of its unique photophysical characteristics, we investigated optically the variations in the density and orientation of the polymer macromolecules in electrospun nanofibers. In agreement with our model, we found higher density and axial orientation at the fiber core, while lower density and radial orientation closer to the fiber surface. The non-uniformity of the resulting molecular structure can be tuned and exploited in diverse optical and structural applications. We acknowledge: V. Fasano, G. Potente, S. Girardo and E. Caldi for assistance in measurements; United States-Israel BSF, RBNI Institute, and the Israel Science Foundation for financial support.

Polyethylenimine/silk fibroin multilayers deposited nanofibrics for cell culture.

PubMed

Ye, Xinguo; Li, Sheng; Chen, Xuanxuan; Zhan, Yingfei; Li, Xiaonan

2017-01-01

Scaffold with good three-dimensional (3D) structure and appropriate surface modification is essential to tissue regeneration in the treatment of tissue or organ failure. Silk fibroin (SF) is a promising scaffolding material with high biocompatibility, cytocompatibility, biodegradability and flexibility. In this study, positively charged polyethylenimine (PEI) and negatively charged SF assembled alternately onto cellulose nanofibrous substrates hydrolyzed from electrospun cellulose acetate nanofibrous mats. The obtained nanofibrous membranes modified with multiple layers of PEI/SF were characterized by field emission scanning electron microscopy, X-ray photoelectron spectroscopy, Fourier transform infrared spectroscopy and thermogravimetric analysis. L929 cells were applied to examine the cytocompatibility of PEI/SF coated membranes. The results demonstrated that the nanofibrous membranes after modification with multiple layers of PEI/SF maintained 3D nanofibrous structure, and cells cultured on them showed good adherence and spreading on them as well, which indicated that PEI/SF coated membranes had potential application in tissue engineering. Copyright © 2016 Elsevier B.V. All rights reserved.

Poly-m-aramid nanofiber mats: Production for application as structural modifiers in CFRP laminates

NASA Astrophysics Data System (ADS)

Mazzocchetti, Laura; D'Angelo, Emanuele; Benelli, Tiziana; Belcari, Juri; Brugo, Tommaso Maria; Zucchelli, Andrea; Giorgini, Loris

2016-05-01

Poly(m-phenylene isophtalamide) electrospun nanofibrous membranes were produced to be used as structural reinforcements for carbon fiber reinforced composites production. In order for the polymer to be electrospun, it needs however to be fully solubilized, so the addition of some salts is required to help disrupt the tight macromolecular packing based on intra- and inter-molecular hydrogen bonding. Such salts may also contribute to the electrospinnability of the overall solution, since the provide it with a higher conductivity, whatever the solvent might be. The salt haobwever stays in the final nanofibrous mat. The membranes containing the salt are also observed to be highly hygroscopic, with a water content up to 26%, in the presence of 20%wt LiCl in the nanofibrous mat. When those membranes were interleaved among prepregs to produce a laminates, the obtained composite displayed thermal properties comparable to those of a reference nanofiber-free composite, though the former showed also easier delamination. Hence the removal of the hygroscopic salt was performed, that lead to thinner membranes, whose water content matched that of the pristine polymer. The washing step induced a thinning of the layers and of the fibers diameters, though no fiber shrinking nor membrane macroscopic damages were observed. These preliminary encouraging results thus pave the way to a deeper study of the optimized condition for producing convenient poly(m-phenylene isophtalamide) electrospun nanofibrous membranes to be used for carbon fiber reinforced composites structural modification.

Electrospun Superhydrophobic Organic/Inorganic Composite Nanofibrous Membranes for Membrane Distillation.

PubMed

Li, Xiong; Yu, Xufeng; Cheng, Cheng; Deng, Li; Wang, Min; Wang, Xuefen

2015-10-07

Electrospun superhydrophobic organic/inorganic composite nanofibrous membranes exhibiting excellent direct contact membrane distillation (DCMD) performance were fabricated by a facile route combining the hydrophobization of silica nanoparticles (SiO2 NPs) and colloid electrospinning of the hydrophobic silica/poly(vinylidene fluoride) (PVDF) matrix. Benefiting from the utilization of SiO2 NPs with three different particle sizes, the electrospun nanofibrous membranes (ENMs) were endowed with three different delicate nanofiber morphologies and fiber diameter distribution, high porosity, and superhydrophobic property, which resulted in excellent waterproofing and breathability. Significantly, structural attributes analyses have indicated the major contributing role of fiber diameter distribution on determining the augment of permeate vapor flux through regulating mean flow pore size (MFP). Meanwhile, the extremely high liquid entry pressure of water (LEPw, 2.40 ± 0.10 bar), robust nanofiber morphology of PVDF immobilized SiO2 NPs, remarkable mechanical properties, thermal stability, and corrosion resistance endowed the as-prepared membranes with prominent desalination capability and stability for long-term MD process. The resultant choreographed PVDF/silica ENMs with optimized MFP presented an outstanding permeate vapor flux of 41.1 kg/(m(2)·h) and stable low permeate conductivity (∼2.45 μs/cm) (3.5 wt % NaCl salt feed; ΔT = 40 °C) over a DCMD test period of 24 h without membrane pores wetting detected. This result was better than those of typical commercial PVDF membranes and PVDF and modified PVDF ENMs reported so far, suggesting them as promising alternatives for MD applications.

Influence of Controlled Cooling in Bimodal Scaffold Fabrication Using Polymers with Different Melting Temperatures.

PubMed

Lara-Padilla, Hernan; Mendoza-Buenrostro, Christian; Cardenas, Diego; Rodriguez-Garcia, Aida; Rodriguez, Ciro A

2017-06-11

The combination of different materials and capabilities to manufacture at several scales open new possibilities in scaffold design for bone regeneration. This work is focused on bimodal scaffolds that combine polylactic acid (PLA) melt extruded strands with polycaprolactone (PCL) electrospun fibers. This type of bimodal scaffold offers better mechanical properties, compared to the use of PCL for the extruded strands, and provides potential a means for controlled drug and/or growth factor delivery through the electrospun fibers. The technologies of fused deposition modeling (FDM) and electrospinning were combined to create 3D bimodal constructs. The system uses a controlled cooling system allowing the combination of polymers with different melting temperatures to generate integrated scaffold architecture. The thermoplastic polymers used in the FDM process enhance the mechanical properties of the bimodal scaffold and control the pore structure. Integrated layers of electrospun microfibers induce an increase of the surface area for cell culture purposes, as well as potential in situ controlled drug and/or growth factor delivery. The proposed bimodal scaffolds (PLA extruded strands and PCL electrospun fibers) show appropriate morphology and better mechanical properties when compared to the use of PCL extruded strands. On average, bimodal scaffolds with overall dimensions of 30 × 30 × 2.4 mm³ (strand diameter of 0.5 mm, strand stepover of 2.5 mm, pore size of 2 mm, and layer height of 0.3 mm) showed scaffold stiffness of 23.73 MPa and compression strength of 3.85 MPa. A cytotoxicity assay based human fibroblasts showed viability of the scaffold materials.

Influence of Controlled Cooling in Bimodal Scaffold Fabrication Using Polymers with Different Melting Temperatures

PubMed Central

Lara-Padilla, Hernan; Mendoza-Buenrostro, Christian; Cardenas, Diego; Rodriguez-Garcia, Aida; Rodriguez, Ciro A.

2017-01-01

The combination of different materials and capabilities to manufacture at several scales open new possibilities in scaffold design for bone regeneration. This work is focused on bimodal scaffolds that combine polylactic acid (PLA) melt extruded strands with polycaprolactone (PCL) electrospun fibers. This type of bimodal scaffold offers better mechanical properties, compared to the use of PCL for the extruded strands, and provides potential a means for controlled drug and/or growth factor delivery through the electrospun fibers. The technologies of fused deposition modeling (FDM) and electrospinning were combined to create 3D bimodal constructs. The system uses a controlled cooling system allowing the combination of polymers with different melting temperatures to generate integrated scaffold architecture. The thermoplastic polymers used in the FDM process enhance the mechanical properties of the bimodal scaffold and control the pore structure. Integrated layers of electrospun microfibers induce an increase of the surface area for cell culture purposes, as well as potential in situ controlled drug and/or growth factor delivery. The proposed bimodal scaffolds (PLA extruded strands and PCL electrospun fibers) show appropriate morphology and better mechanical properties when compared to the use of PCL extruded strands. On average, bimodal scaffolds with overall dimensions of 30 × 30 × 2.4 mm3 (strand diameter of 0.5 mm, strand stepover of 2.5 mm, pore size of 2 mm, and layer height of 0.3 mm) showed scaffold stiffness of 23.73 MPa and compression strength of 3.85 MPa. A cytotoxicity assay based human fibroblasts showed viability of the scaffold materials. PMID:28773000

Enhancing surface properties of breast implants by using electrospun silk fibroin.

PubMed

Valencia-Lazcano, A A; Román-Doval, R; De La Cruz-Burelo, E; Millán-Casarrubias, E J; Rodríguez-Ortega, A

2017-08-24

In the present study, a new electrospun silk fibroin coating of silicone breast implants with improved biocompatibility and mechanical properties was obtained. Fibrous scaffolds were produced by electrospinning a solution containing silk fibroin, derived from Bombyx mori cocoons, and polyethylene oxide (PEO) to be used as a coating of breast implants. A randomly oriented structure of fibroin/PEO was electrospun on implants as assessed by SEM analysis, roughness measurements and ATR-FTIR spectroscopy. The scaffold showed 0.25 µm diameter fibres, 0.76 µm size superficial pores, arithmetic roughness of 0.632 ± 0.12 µm and texture aspect ratio of 0.893 ± 0.04. ATR-FTIR spectroscopy demonstrates the presence of PEO and fibroin in the coating. The mechanical characterisation of the implants before and after being coated with fibroin/PEO demonstrated that the fibroin/PEO scaffold contributes to the increase in the elastic modulus from 0.392 ± 0.02 to 0.560 ± 0.03 MPa and to a more elastic behaviour of the breast implants. Using the fibroin/PEO coating, human fibroblasts seeded on this matrix increased viability up to 30% compared to conventional breast implants. Electrospun silk fibroin could represent a clinically compatible, viable form to coat breast implants. Low cytotoxicity by the fibroin coating and its physico-chemical and mechanical properties may find application in improving breast implants biocompatibility. © 2017 Wiley Periodicals, Inc. J Biomed Mater Res Part B: Appl Biomater, 2017. © 2017 Wiley Periodicals, Inc.

Optical fiber ultrasound transmitter with electrospun carbon nanotube-polymer composite

NASA Astrophysics Data System (ADS)

Poduval, Radhika K.; Noimark, Sacha; Colchester, Richard J.; Macdonald, Thomas J.; Parkin, Ivan P.; Desjardins, Adrien E.; Papakonstantinou, Ioannis

2017-05-01

All-optical ultrasound transducers are promising for imaging applications in minimally invasive surgery. In these devices, ultrasound is transmitted and received through laser modulation, and they can be readily miniaturized using optical fibers for light delivery. Here, we report optical ultrasound transmitters fabricated by electrospinning an absorbing polymer composite directly onto the end-face of optical fibers. The composite coating consisting of an aqueous dispersion of multi-walled carbon nanotubes (MWCNTs) in polyvinyl alcohol was directly electrospun onto the cleaved surface of a multimode optical fiber and subsequently dip-coated with polydimethylsiloxane (PDMS). This formed a uniform nanofibrous absorbing mesh over the optical fiber end-face wherein the constituent MWCNTs were aligned preferentially along individual nanofibers. Infiltration of the PDMS through this nanofibrous mesh onto the underlying substrate was observed and the resulting composites exhibited high optical absorption (>97%). Thickness control from 2.3 μm to 41.4 μm was obtained by varying the electrospinning time. Under laser excitation with 11 μJ pulse energy, ultrasound pressures of 1.59 MPa were achieved at 1.5 mm from the coatings. On comparing the electrospun ultrasound transmitters with a dip-coated reference fabricated using the same constituent materials and possessing identical optical absorption, a five-fold increase in the generated pressure and wider bandwidth was observed. The electrospun transmitters exhibited high optical absorption, good elastomer infiltration, and ultrasound generation capability in the range of pressures used for clinical pulse-echo imaging. All-optical ultrasound probes with such transmitters fabricated by electrospinning could be well-suited for incorporation into catheters and needles for diagnostics and therapeutic applications.

VOCs Air Pollutant Cleaning with Polyacrylonitrile/Fly Ash Nanocomposite Electrospun Nanofibrous Membranes

NASA Astrophysics Data System (ADS)

Cong Ge, Jun; Wang, Zi Jian; Kim, Min Soo; Choi, Nag Jung

2018-01-01

Volatile organic compounds (VOCs) as an environmental pollution, which have many kinds of chemical structures, and many of them are very toxic. Therefore, controlling and reducing the presence of VOCs has become a hot topic among researchers for many years. In this study, the VOCs adsorption capacity of polyacrylonitrile/fly ash (PAN/FA) nanocomposite electrospun nanofibrous membranes were investigated. The results indicated that the PAN with different contents of FA powder (20%, 40%, 60%, 80%, and 100% compared with PAN by weight) could be spun well by electrospinning. The diameter of the fiber was very fine and its arrangement was irregular. The PAN nanofibrous membrane containing 60 wt% FA powder had the highest VOCs absorption capacity compared with other nanofibrous membranes due to its large specific surface area.

Elastin-PLGA hybrid electrospun nanofiber scaffolds for salivary epithelial cell self-organization and polarization.

PubMed

Foraida, Zahraa I; Kamaldinov, Tim; Nelson, Deirdre A; Larsen, Melinda; Castracane, James

2017-10-15

Development of electrospun nanofibers that mimic the structural, mechanical and biochemical properties of natural extracellular matrices (ECMs) is a promising approach for tissue regeneration. Electrospun fibers of synthetic polymers partially mimic the topography of the ECM, however, their high stiffness, poor hydrophilicity and lack of in vivo-like biochemical cues is not optimal for epithelial cell self-organization and function. In search of a biomimetic scaffold for salivary gland tissue regeneration, we investigated the potential of elastin, an ECM protein, to generate elastin hybrid nanofibers that have favorable physical and biochemical properties for regeneration of the salivary glands. Elastin was introduced to our previously developed poly-lactic-co-glycolic acid (PLGA) nanofiber scaffolds by two methods, blend electrospinning (EP-blend) and covalent conjugation (EP-covalent). Both methods for elastin incorporation into the nanofibers improved the wettability of the scaffolds while only blend electrospinning of elastin-PLGA nanofibers and not surface conjugation of elastin to PLGA fibers, conferred increased elasticity to the nanofibers measured by Young's modulus. After two days, only the blend electrospun nanofiber scaffolds facilitated epithelial cell self-organization into cell clusters, assessed with nuclear area and nearest neighbor distance measurements, leading to the apicobasal polarization of salivary gland epithelial cells after six days, which is vital for cell function. This study suggests that elastin electrospun nanofiber scaffolds have potential application in regenerative therapies for salivary glands and other epithelial organs. Regenerating the salivary glands by mimicking the extracellular matrix (ECM) is a promising approach for long term treatment of salivary gland damage. Despite their topographic similarity to the ECM, electrospun fibers of synthetic polymers lack the biochemical complexity, elasticity and hydrophilicity of the ECM. Elastin is an ECM protein abundant in the salivary glands and responsible for tissue elasticity. Although it's widely used for tissue regeneration of other organs, little is known about its utility in regenerating the salivary tissue. This study describes the use of elastin to improve the elasticity, hydrophilicity and biochemical complexity of synthetic nanofibers and its potential in directing in vivo-like organization of epithelial salivary cells which helps the design of efficient salivary gland regeneration scaffolds. Copyright © 2017 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

Electrostatic Assemblies of Well-Dispersed AgNPs on the Surface of Electrospun Nanofibers as Highly Active SERS Substrates for Wide-Range pH Sensing.

PubMed

Yang, Tong; Ma, Jun; Zhen, Shu Jun; Huang, Cheng Zhi

2016-06-15

Surface-enhanced Raman scattering (SERS) has shown high promise in analysis and bioanalysis, wherein noble metal nanoparticles (NMNPs) such as silver nanoparticles were employed as substrates because of their strong localized surface plasmon resonance (LSPR) properties. However, SERS-based pH sensing was restricted because of the aggregation of NMNPs in acidic medium or biosamples with high ionic strength. Herein, by using the electrostatic interaction as a driving force, AgNPs are assembled on the surface of ethylene imine polymer (PEI)/poly(vinyl alcohol) (PVA) electrospun nanofibers, which are then applied as highly sensitive and reproducible SERS substrate with an enhancement factor (EF) of 10(7)-10(8). When p-aminothiophenol (p-ATP) is used as an indicator with its b2 mode, a good and wide linear response to pH ranging from 2.56 to 11.20 could be available, and the as-prepared nanocomposite fibers then could be fabricated as excellent pH sensors in complicated biological samples such as urine, considering that the pH of urine could reflect the acid-base status of a person. This work not only emerges a cost-effective, direct, and convenient approach to homogeneously decorate AgNPs on the surface of polymer nanofibers but also supplies a route for preparing other noble metal nanofibrous sensing membranes.

Fabrication and Evaluation of Electrospun, 3D-Bioplotted, and Combination of Electrospun/3D-Bioplotted Scaffolds for Tissue Engineering Applications

PubMed Central

Mellor, Liliana F.; Huebner, Pedro; Cai, Shaobo; Taylor, Michael A.; Spang, Jeffrey

2017-01-01

Electrospun scaffolds provide a dense framework of nanofibers with pore sizes and fiber diameters that closely resemble the architecture of native extracellular matrix. However, it generates limited three-dimensional structures of relevant physiological thicknesses. 3D printing allows digitally controlled fabrication of three-dimensional single/multimaterial constructs with precisely ordered fiber and pore architecture in a single build. However, this approach generally lacks the ability to achieve submicron resolution features to mimic native tissue. The goal of this study was to fabricate and evaluate 3D printed, electrospun, and combination of 3D printed/electrospun scaffolds to mimic the native architecture of heterogeneous tissue. We assessed their ability to support viability and proliferation of human adipose derived stem cells (hASC). Cells had increased proliferation and high viability over 21 days on all scaffolds. We further tested implantation of stacked-electrospun scaffold versus combined electrospun/3D scaffold on a cadaveric pig knee model and found that stacked-electrospun scaffold easily delaminated during implantation while the combined scaffold was easier to implant. Our approach combining these two commonly used scaffold fabrication technologies allows for the creation of a scaffold with more close resemblance to heterogeneous tissue architecture, holding great potential for tissue engineering and regenerative medicine applications of osteochondral tissue and other heterogeneous tissues. PMID:28536700

Microbes encapsulated within crosslinkable polymers

DOEpatents

Chidambaram, Devicharan; Liu, Ying; Rafailovich, Miriam H

2013-02-05

The invention relates to porous films comprising crosslinked electrospun hydrogel fibers. Viable microbes are encapsulated within the crosslinked electrospun hydrogel fibers. The crosslinked electrospun hydrogel fibers are water insoluble and permeable. The invention also relates to methods of making and using such porous films.

Polydopamine Inter-Fiber Networks: New Strategy for Producing Rigid, Sticky, 3D Fluffy Electrospun Fibrous Polycaprolactone Sponges.

PubMed

Choi, Wuyong; Lee, Slgirim; Kim, Seung-Hyun; Jang, Jae-Hyung

2016-06-01

Designing versatile 3D interfaces that can precisely represent a biological environment is a prerequisite for the creation of artificial tissue structures. To this end, electrospun fibrous sponges, precisely mimicking an extracellular matrix and providing highly porous interfaces, have capabilities that can function as versatile physical cues to regenerate various tissues. However, their intrinsic features, such as sheet-like, thin, and weak structures, limit the design of a number of uses in tissue engineering applications. Herein, a highly facile methodology capable of fabricating rigid, sticky, spatially expanded fluffy electrospun fibrous sponges is proposed. A bio-inspired adhesive material, poly(dopamine) (pDA), is employed as a key mediator to provide rigidity and stickiness to the 3D poly(ε-caprolactone) (PCL) fibrous sponges, which are fabricated using a coaxial electrospinning with polystyrene followed by a selective leaching process. The iron ion induced oxidation of dopamine into pDA networks interwoven with PCL fibers results in significant increases in the rigidity of 3D fibrous sponges. Furthermore, the exposure of catecholamine groups on the fiber surfaces promotes the stable attachment of the sponges on wet organ surfaces and triggers the robust immobilization of biomolecules (e.g., proteins and gene vectors), demonstrating their potential for 3D scaffolds as well as drug delivery vehicles. Because fibrous structures are ubiquitous in the human body, these rigid, sticky, 3D fibrous sponges are good candidates for powerful biomaterial systems that functionally mimic a variety of tissue structures. © 2016 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Interactions between Surfactants in Solution and Electrospun Protein Fibers: Effects on Release Behavior and Fiber Properties.

PubMed

Stephansen, Karen; García-Díaz, María; Jessen, Flemming; Chronakis, Ioannis S; Nielsen, Hanne M

2016-03-07

Intermolecular interaction phenomena occurring between endogenous compounds, such as proteins and bile salts, and electrospun compounds are so far unreported, despite the exposure of fibers to such biorelevant compounds when applied for biomedical purposes, e.g., tissue engineering, wound healing, and drug delivery. In the present study, we present a systematic investigation of how surfactants and proteins, as physiologically relevant components, interact with insulin-loaded fish sarcoplasmic protein (FSP) electrospun fibers (FSP-Ins fibers) in solution and thereby affect fiber properties such as accessible surface hydrophilicity, physical stability, and release characteristics of an encapsulated drug. Interactions between insulin-loaded protein fibers and five anionic surfactants (sodium taurocholate, sodium taurodeoxycholate, sodium glycocholate, sodium glycodeoxycholate, and sodium dodecyl sulfate), a cationic surfactant (benzalkonium chloride), and a neutral surfactant (Triton X-100) were studied. The anionic surfactants increased the insulin release in a concentration-dependent manner, whereas the neutral surfactant had no significant effect on the release. Interestingly, only minute amounts of insulin were released from the fibers when benzalkonium chloride was present. The FSP-Ins fibers appeared dense after incubation with this cationic surfactant, whereas high fiber porosity was observed after incubation with anionic or neutral surfactants. Contact angle measurements and staining with the hydrophobic dye 8-anilino-1-naphthalenesulfonic acid indicated that the FSP-Ins fibers were hydrophobic, and showed that the fiber surface properties were affected differently by the surfactants. Bovine serum albumin also affected insulin release in vitro, indicating that also proteins may affect the fiber performance in an in vivo setting.

Removal of aniline from air and water by polymers of intrinsic microporosity (PIM-1) electrospun ultrafine fibers.

PubMed

Satilmis, Bekir; Uyar, Tamer

2018-04-15

This research aims to investigate the possibility of electrospun fibers from Polymers of Intrinsic Microporosity (PIM-1) as an alternative adsorbent for aniline removal from both air and aqueous solution. Adsorption properties of electrospun PIM-1 fibers were compared with powder and film form of PIM-1. While electrospun PIM-1 nanofibrous mat can adsorb 871 mg g -1 aniline from air, it can also adsorb 78 ± 5.4 mg g -1 aniline from aqueous environment when 50 mg L -1 aniline solution is used. The experimental maximum adsorption capacity of electrospun PIM-1 fibers was found as (q e ) 138 mg g -1 . Langmuir and Freundlich isotherm models have been studied and Langmuir model found more appropriate for aniline adsorption on electrospun PIM-1 fibers. The study reveals that self-standing electrospun fibrous mat of PIM-1 has shown potential to be used as an efficient adsorbent material for the adsorption of VOCs from air and aqueous system thanks to its fast kinetic and high adsorption capacity. Copyright © 2018 Elsevier Inc. All rights reserved.

Effect of electrospun nanofibers on flexural properties of fiberglass composites

NASA Astrophysics Data System (ADS)

White, Fatima T.

In the present study, sintered electrospun TEOS nanofibers were interleaved in S2 fiberglass woven fabric layers, and composite panels were fabricated using the heated vacuum assisted resin transfer molding (H-VARTM) process. Cured panels were water jet cut to obtain the flexural test coupons. Flexural coupons were then tested using ASTM D7264 standard. The mechanical properties such as flexural strength, ultimate flexural failure strains, flexural modulus, and fiber volume fraction were measured. The S-2 fiberglass composite with the sintered TEOS electrospun nanofibers displayed lower flexural stiffness and strength as compared to the composites that were fabricated using S-2 fiberglass composite without the TEOS electrospun nanofibers. The present study also indicated that the composites fabricated with sintered TEOS electrospun nanofibers have larger failure strains as compared to the ones that were fabricated without the presence of electrospun nanofibers. The study indicates that the nanoengineered composites have better energy absorbing mechanism under flexural loading as compared to conventional fiberglass composites without presence of nanofibers.

Lignin-Based Electrospun Nanofibers Reinforced with Cellulose Nanocrystals

Treesearch

Mariko Ago; Kunihiko Okajima; Joseph E. Jakes; Park Sunkyu; Orlando J. Rojas

2012-01-01

Lignin-based fibers were produced by electrospinning aqueous dispersions of lignin, poly(vinyl alcohol) (PVA), and cellulose nanocrystals (CNCs). Defect-free nanofibers with up to 90 wt % lignin and 15% CNCs were achieved. The properties of the aqueous dispersions, including viscosity, electrical conductivity, and surface tension, were examined and correlated to the...

Layer-by-layer assembly of MXene and carbon nanotubes on electrospun polymer films for flexible energy storage.

PubMed

Zhou, Zehang; Panatdasirisuk, Weerapha; Mathis, Tyler S; Anasori, Babak; Lu, Canhui; Zhang, Xinxing; Liao, Zhiwei; Gogotsi, Yury; Yang, Shu

2018-03-29

Free-standing, highly flexible and foldable supercapacitor electrodes were fabricated through the spray-coating assisted layer-by-layer assembly of Ti3C2Tx (MXene) nanoflakes together with multi-walled carbon nanotubes (MWCNTs) on electrospun polycaprolactone (PCL) fiber networks. The open structure of the PCL network and the use of MWCNTs as spacers not only limit the restacking of Ti3C2Tx flakes but also increase the accessible surface of the active materials, facilitating fast diffusion of electrolyte ions within the electrode. Composite electrodes have areal capacitance (30-50 mF cm-2) comparable to other templated electrodes reported in the literature, but showed significantly improved rate performance (14-16% capacitance retention at a scan rate of 100 V s-1). Furthermore, the composite electrodes are flexible and foldable, demonstrating good tolerance against repeated mechanical deformation, including twisting and folding. Therefore, these tens of micron thick fiber electrodes will be attractive for applications in energy storage, electroanalytical chemistry, brain electrodes, electrocatalysis and other fields, where flexible freestanding electrodes with an open and accessible surface are highly desired.

Comparative evaluation of Chitosan, Cellulose Acetate, and Polyethersulfone Nanofiber Scaffolds for Neural Differentiation

PubMed Central

Du, Jian; Tan, Elaine; Kim, Hyo Jun; Zhang, Allen; Bhattacharya, Rahul; Yarema, Kevin J

2013-01-01

Based on accumulating evidence that the 3D topography and the chemical features of a growth surface influence neuronal differentiation, we combined these two features by evaluating the cytotoxicity, proliferation, and differentiation of the rat PC12 line and human neural stem cells (hNSCs) on chitosan (CS), cellulose acetate (CA), and polyethersulfone (PES)-derived electrospun nanofibers that had similar diameters, centered in the 200 to 500 nm range. None of the nanofibrous materials were cytotoxic compared to 2D (e.g., flat surface) controls; however, proliferation generally was inhibited on the nanofibrous scaffolds although to a lesser extent on the polysaccharide-derived materials compared to PES. In an exception to the trend towards slower growth on the 3D substrates, hNSCs differentiated on the CS nanofibers proliferated faster than the 2D controls and both cell types showed enhanced indication of neuronal differentiation on the CS scaffolds. Together, these results demonstrate beneficial attributes of CS for neural tissue engineering when this polysaccharide is used in the context of the defined 3D topography found in electrospun nanofibers. PMID:24274534

Integrated antibacterial and antifouling surfaces via cross-linking chitosan-g-eugenol/zwitterionic copolymer on electrospun membranes.

PubMed

Li, Zhenguang; Hu, Wenhong; Zhao, Yunhui; Ren, Lixia; Yuan, Xiaoyan

2018-04-27

Integrated antibacterial and antifouling surfaces in favor of avoiding implant-related infections are necessarily required for biomaterials when they contact with the body fluid. In this work, an antibacterial and antifouling membrane was developed via cross-linking chitosan-g-eugenol and the zwitterionic copolymer poly(sulfobetaine methylacrylate-co-2-aminoethyl methacrylate) on the electrospun polycarbonate urethane substrate using genipin as a cross-linker. Antibacterial assays demonstrated that the prepared membranes had efficient antibacterial activity with 92.8 ± 2.5% and 95.2 ± 1.3% growth inhibition rates against Escherichia coli and Staphylococcus aureus, respectively. The investigations on antifouling activity and hemocompatibility of the membranes showed significant resistances to bacterial attachment, non-specific protein adsorption and platelet adhesion, and presented lower hemolytic activity and good anticoagulant activity as well. Moreover, cell culture assays indicated that the prepared membranes exerted no obvious cytotoxicity with more than 80% of relative L929 fibroblast viability. Therefore, the membranes with integrated antibacterial and antifouling properties could be potentially applied in promising indwelling devices. Copyright © 2018 Elsevier B.V. All rights reserved.

Functional Electrospun Nanofibrous Scaffolds for Biomedical Applications

PubMed Central

Liang, Dehai; Hsiao, Benjamin S.; Chu, Benjamin

2009-01-01

Functional nanofibrous scaffolds produced by electrospinning have great potential in many biomedical applications, such as tissue engineering, wound dressing, enzyme immobilization and drug (gene) delivery. For a specific successful application, the chemical, physical and biological properties of electrospun scaffolds should be adjusted to match the environment by using a combination of multi-component compositions and fabrication techniques where electrospinning has often become a pivotal tool. The property of the nanofibrous scaffold can be further improved with innovative development in electrospinning processes, such as two-component electrospinning and in-situ mixing electrospinning. Post modifications of electrospun membranes also provide effective means to render the electrospun scaffolds with controlled anisotropy and porosity. In this review, we review the materials, techniques and post modification methods to functionalize electrospun nanofibrous scaffolds suitable for biomedical applications. PMID:17884240

Putting Electrospun Nanofibers to Work for Biomedical Research

PubMed Central

Xie, Jingwei; Li, Xiaoran; Xia, Younan

2009-01-01

Electrospinning has been exploited for almost one century to process polymers and related materials into nanofibers with controllable compositions, diameters, porosities, and porous structures for a variety of applications. Owing to its high porosity and large surface area, a non-woven mat of electrospun nanofibers can serve as an ideal scaffold to mimic the extracellular matrix for cell attachment and nutrient transportation. The nanofiber itself can also be functionalized through encapsulation or attachment of bioactive species such as extracellular matrix proteins, enzymes, and growth factors. In addition, the nanofibers can be further assembled into a variety of arrays or architectures by manipulating their alignment, stacking, or folding. All these attributes make electrospinning a powerful tool for generating nanostructured materials for a range of biomedical applications that include controlled release, drug delivery, and tissue engineering. PMID:20011452

Electrospun Fibers for Recruitment and Differentiation of Stem Cells in Regenerative Medicine.

PubMed

Sankar, Sharanya; Sharma, Chandra S; Rath, Subha N; Ramakrishna, Seeram

2017-12-01

Electrospinning is a popular technique used to mimic the natural sub-micron features of the native tissue. The ultra-fine fibers provide a favorable extracellular matrix-like environment for regulation of cellular functions. This article summarizes and reviews the current advances in electrospun fiber application and focuses on the novel strategies applied for tissue regeneration and repair. It explores the different factors affecting the attachment and proliferation of mesenchymal stem cells (MSCs) on the electrospun substrates. The influence of different features of electrospun fibers in the differentiation of MSCs into specific lineages (bone, cartilage, tendon/ligament, and nerves) has been elaborated. In addition, the different techniques to mimic the hierarchical features of tissues and its effect on cellular functions are reviewed. Additionally, the new developments like three-dimensional (3D) electrospinning, 3D spheroid double strategy and the comparative analysis of dynamic and static culture on electrospun scaffolds are discussed. With the intricate understanding of the interaction between the cells and the electrospun fiber matrix we can aim to combine the newer strategies to overcome the existing challenges and improve the potential application of electrospun fibers in the field of tissue regeneration and repair. © 2017 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Killing bacteria within biofilms by sustained release of tetracycline from triple-layered electrospun micro/nanofibre matrices of polycaprolactone and poly(ethylene-co-vinyl acetate).

PubMed

Alhusein, Nour; De Bank, Paul A; Blagbrough, Ian S; Bolhuis, Albert

2013-12-01

We report the controlled release of the antibiotic tetracycline (tet) HCl from a triple-layered electrospun matrix consisting of a central layer of poly(ethylene-co-vinyl acetate (PEVA) sandwiched between outer layers of poly-ε-caprolactone (PCL). These micro/nanofibre layers with tet successfully encapsulated (essentially quantitatively at 3 and 5 % w/w) in each layer, efficiently inhibited the growth of a panel of bacteria, including clinical isolates, as shown by a modified Kirby-Bauer disc assay. Furthermore, they demonstrated high biological activity in increasingly complex models of biofilm formation (models that are moving closer to the situation in a wound) by stopping biofilm formation, by killing preformed biofilms and killing mature, dense biofilm colonies of Staphylococcus aureus MRSA252. Tet is clinically useful with potential applications in wound healing and especially in complicated skin and skin-structure infections; electrospinning provides good encapsulation efficiency of tet within PCL/PEVA/PCL polymers in micro/nanofibre layers which display sustained antibiotic release in formulations that are anti-biofilm.

Electrospun montmorillonite modified poly(vinylidene fluoride) nanocomposite separators for lithium-ion batteries

DOE Office of Scientific and Technical Information (OSTI.GOV)

Fang, Changjiang; Yang, Shuli; Zhao, Xinfei

2016-07-15

Highlights: • Composite separators of PVDF and MMT for lithium-ion batteries were electrospun. • Thermal dimensional stability and tensile property of composite separators get improved. • Presence of montmorillonite promotes electrical properties of PVDF fibrous separators. • Batteries consisting of PVDF/MMT-5% separator achieve the best performance. - Abstract: Composite separators of poly(vinylidene fluoride) (PVDF) with different contents of montmorillonite (MMT) for Li-ion batteries have been fabricated by electrospinning. The morphology, function group, crystallinity, and mechanical properties of membranes were investigated by scanning electron microscope (SEM), Fourier Transform infrared spectra (FT-IR), differential scanning calorimetry (DSC), and tensile test, respectively. Interlayer spacingmore » of MMT in polymer was characterized by X-ray diffraction (XRD). In addition, the results of electrochemical measurements suggest that PVDF/MMT-5% composite membrane has maximum ionic conductivity of 4.2 mS cm{sup −1}, minimum interfacial resistance of 97 Ω, and excellent electrochemical stability. The cell comprising PVDF/MMT-5% composite membrane shows higher capacity and more stable cycle performance than the one using commercial Celgard PP membrane.« less

Effects of humidity and solution viscosity on electrospun fiber morphology.

PubMed

Nezarati, Roya M; Eifert, Michelle B; Cosgriff-Hernandez, Elizabeth

2013-10-01

Electrospinning is a popular technique to fabricate tissue engineering scaffolds due to the exceptional tunability of fiber morphology that can be used to control scaffold mechanical properties, degradation rate, and cell behavior. Although the effects of modulating processing or solution parameters on fiber morphology have been extensively studied, there remains limited understanding of the impact of environmental parameters such as humidity. To address this gap, three polymers (poly(ethylene glycol) [PEG], polycaprolactone [PCL], and poly(carbonate urethane) [PCU]) were electrospun at a range of relative humidities (RH = 5%-75%) and the resulting fiber architecture characterized with scanning electron microscopy. Low relative humidity (< 50%) resulted in fiber breakage for all three polymers due to decreased electrostatic discharge from the jet. At high relative humidity (> 50%), three distinct effects were observed based on individual polymer properties. An increase in fiber breakage and loss of fiber morphology occurred in the PEG system as a result of increased water absorption at high relative humidity. In contrast, surface pores on PCL fibers were observed and hypothesized to have formed via vapor-induced phase separation. Finally, decreased PCU fiber collection occurred at high humidity likely due to increased electrostatic discharge. These findings highlight that the effects of relative humidity on electrospun fiber morphology are dependent on polymer hydrophobicity, solvent miscibility with water, and solvent volatility. An additional study was conducted to highlight that small changes in molecular weight can strongly influence solution viscosity and resulting fiber morphology. We propose that solution viscosity rather than concentration is a more useful parameter to report in electrospinning methodology to enable reproduction of findings. In summary, this study further elucidates key mechanisms in electrospun fiber formation that can be utilized to fabricate tissue engineering scaffolds with tunable and reproducible properties.

Effects of Humidity and Solution Viscosity on Electrospun Fiber Morphology

PubMed Central

Nezarati, Roya M.; Eifert, Michelle B.

2013-01-01

Electrospinning is a popular technique to fabricate tissue engineering scaffolds due to the exceptional tunability of fiber morphology that can be used to control scaffold mechanical properties, degradation rate, and cell behavior. Although the effects of modulating processing or solution parameters on fiber morphology have been extensively studied, there remains limited understanding of the impact of environmental parameters such as humidity. To address this gap, three polymers (poly(ethylene glycol) [PEG], polycaprolactone [PCL], and poly(carbonate urethane) [PCU]) were electrospun at a range of relative humidities (RH=5%–75%) and the resulting fiber architecture characterized with scanning electron microscopy. Low relative humidity (<50%) resulted in fiber breakage for all three polymers due to decreased electrostatic discharge from the jet. At high relative humidity (>50%), three distinct effects were observed based on individual polymer properties. An increase in fiber breakage and loss of fiber morphology occurred in the PEG system as a result of increased water absorption at high relative humidity. In contrast, surface pores on PCL fibers were observed and hypothesized to have formed via vapor-induced phase separation. Finally, decreased PCU fiber collection occurred at high humidity likely due to increased electrostatic discharge. These findings highlight that the effects of relative humidity on electrospun fiber morphology are dependent on polymer hydrophobicity, solvent miscibility with water, and solvent volatility. An additional study was conducted to highlight that small changes in molecular weight can strongly influence solution viscosity and resulting fiber morphology. We propose that solution viscosity rather than concentration is a more useful parameter to report in electrospinning methodology to enable reproduction of findings. In summary, this study further elucidates key mechanisms in electrospun fiber formation that can be utilized to fabricate tissue engineering scaffolds with tunable and reproducible properties. PMID:23469941

Production and cross-sectional characterization of aligned co-electrospun hollow microfibrous bulk assemblies

DOE Office of Scientific and Technical Information (OSTI.GOV)

Zhou, Feng-Lei; The School of Materials, The University of Manchester, Manchester M13 9PL; CRUK-EPSRC Cancer Imaging Centre in Cambridge and Manchester

2015-11-15

The development of co-electrospun (co-ES) hollow microfibrous assemblies of an appreciable thickness is critical for many practical applications, including filtration membranes and tissue-mimicking scaffolds. In this study, thick uniaxially aligned hollow microfibrous assemblies forming fiber bundles and strips were prepared by co-ES of polycaprolactone (PCL) and polyethylene oxide (PEO) as shell and core materials, respectively. Hollow microfiber bundles were deposited on a fixed rotating disc, which resulted in non-controllable cross-sectional shapes on a macroscopic scale. In comparison, fiber strips were produced with tuneable thickness and width by additionally employing an x–y translation stage in co-ES. Scanning electron microscopy (SEM) imagesmore » of cross-sections of fiber assemblies were analyzed to investigate the effects of production time (from 0.5 h to 12 h), core flow rate (from 0.8 mL/h to 2.0 mL/h) and/or translation speed (from 0.2 mm/s to 5 mm/s) on the pores and porosity. We observed significant changes in pore size and shape with core flow rate but the influence of production time varied; five strips produced under the same conditions had reasonably good size and porosity reproducibility; pore sizes didn't vary significantly from strip bottom to surface, although the porosity gradually decreased and then returned to the initial level. - Highlights: • Hollow microfibrous assemblies based on co-electrospinning are demonstrated. • The thickness and width of co-electrospun strips were controllable. • Cross-sections of fibres had non-normally distributed pore sizes and shapes. • Cross-sections were significantly influenced by production time and flow rate. • Co-electrospun strips had reasonably good reproducible cross-sections.« less

Conducting electrospun fibres with polyanionic grafts as highly selective, label-free, electrochemical biosensor with a low detection limit for non-Hodgkin lymphoma gene.

PubMed

Kerr-Phillips, Thomas E; Aydemir, Nihan; Chan, Eddie Wai Chi; Barker, David; Malmström, Jenny; Plesse, Cedric; Travas-Sejdic, Jadranka

2018-02-15

A highly selective, label-free sensor for the non-Hodgkin lymphoma gene, with an aM detection limit, utilizing electrochemical impedance spectroscopy (EIS) is presented. The sensor consists of a conducting electrospun fibre mat, surface-grafted with poly(acrylic acid) (PAA) brushes and a conducting polymer sensing element with covalently attached oligonucleotide probes. The sensor was fabricated from electrospun NBR rubber, embedded with poly(3,4-ethylenedioxythiophene) (PEDOT), followed by grafting poly(acrylic acid) brushes and then electrochemically polymerizing a conducting polymer monomer with ssDNA probe sequence pre-attached. The resulting non-Hodgkin lymphoma gene sensor showed a detection limit of 1aM (1 × 10 -18 mol/L), more than 400 folds lower compared to a thin-film analogue. The sensor presented extraordinary selectivity, with only 1%, 2.7% and 4.6% of the signal recorded for the fully non-complimentary, T-A and G-C base mismatch oligonucleotide sequences, respectively. We suggest that such greatly enhanced selectivity is due to the presence of negatively charged carboxylic acid moieties from PAA grafts that electrostatically repel the non-complementary and mismatch DNA sequences, overcoming the non-specific binding. Copyright © 2017 Elsevier B.V. All rights reserved.

Electrospun Fiber Pads of Cellulose Acetate and Essential Oils with Antimicrobial Activity.

PubMed

Liakos, Ioannis L; Holban, Alina Maria; Carzino, Riccardo; Lauciello, Simone; Grumezescu, Alexandru Mihai

2017-04-12

The method of electrospinning was used to create nanofibers made of cellulose acetate (CA) and essential oils (EOs). CA polymer at 15% w / v was dissolved in acetone and then 1% or 5% v / v of EOs was added to the polymer solution. The utilized essential oils were rosemary and oregano oils. Then, the CA/EOs in acetone solution were electrospun, creating micro/nanofibers, approximately 700-1500 nm in diameter. Raman spectroscopy was used to detect the attachment of the EOs in the CA electrospun fibers (ESFs). Scanning electron microscopy was used to study the morphology, topography and dimensions of the ESFs. The formed CA/EOs ESFs are found to have good antimicrobial properties against three common microbial species, frequently found in difficult to treat infections: Bacteria species Staphylococcus aureus , Escherichia coli and the yeast Candida albicans . ESFs with 5% v / v oregano oil with respect to the initial solution, showed the best antimicrobial and anti-biofilm effects due to the potency of this EO against bacteria and fungi, especially for Escherichia coli and Candida albicans . This work describes an effective and simple method to prepare CA/EOs ESFs and opens up many new applications of micro/nanofibers such as improved antimicrobial wound dressings, anti-biofilm surfaces, sensors and packaging alternatives.

A novel electrospun nerve conduit enhanced by carbon nanotubes for peripheral nerve regeneration

NASA Astrophysics Data System (ADS)

Yu, Wenwen; Jiang, Xinquan; Cai, Ming; Zhao, Wen; Ye, Dongxia; Zhou, Yong; Zhu, Chao; Zhang, Xiuli; Lu, Xiaofeng; Zhang, Zhiyuan

2014-04-01

For artificial nerve conduits, great improvements have been achieved in mimicking the structures and components of autologous nerves. However, there are still some problems in conduit construction, especially in terms of mechanical properties, biomimetic surface tomography, electrical conductivity and sustained release of neurotrophic factors or cells. In this study, we designed and fabricated a novel electrospun nerve conduit enhanced by multi-walled carbon nanotubes (MWNTs) on the basis of a collagen/poly(ɛ-caprolactone) (collagen/PCL) fibrous scaffold. Our aim was to provide further knowledge about the mechanical effects and efficacy of MWNTs on nerve conduits as well as the biocompatibility and toxicology of MWNTs when applied in vivo. The results showed that as one component, carboxyl MWNTs could greatly alter the composite scaffold’s hydrophilicity, mechanical properties and degradability. The electrospun fibers enhanced by MWNTs could support Schwann cell adhesion and elongation as a substrate in vitro. In vivo animal studies demonstrated that the MWNT-enhanced collagen/PCL conduit could effectively promote nerve regeneration of sciatic nerve defect in rats and prevent muscle atrophy without invoking body rejection or serious chronic inflammation. All of these results showed that this MWNT-enhanced scaffold possesses good biocompatibility and MWNTs might be excellent candidates as engineered nanocarriers for further neurotrophic factor delivery research.

Flexible all-fiber electrospun supercapacitor

NASA Astrophysics Data System (ADS)

Liu, Xinhua; Naylor Marlow, Max; Cooper, Samuel J.; Song, Bowen; Chen, Xiaolong; Brandon, Nigel P.; Wu, Billy

2018-04-01

We present an all-fiber flexible supercapacitor with composite nanofiber electrodes made via electrospinning and an electrospun separator. With the addition of manganese acetylacetonate (MnACAC) to polyacrylonitrile (PAN) as a precursor for the electrospinning process and subsequent heat treatment, the performance of pure PAN supercapacitors was improved from 90 F g-1 to 200 F g-1 (2.5 mV s-1) with possible mass loadings of MnACAC demonstrated as high as 40 wt%. X-ray diffraction measurements showed that after thermal treatment, the MnACAC was converted to MnO, meanwile, the thermal decomposition of MnACAC increased the graphitic degree of the carbonised PAN. Scanning electron microscopy and image processing showed that static electrospinning of pure PAN and PAN-Mn resulted in fiber diameters of 460 nm and 480 nm respectively after carbonisation. Further analysis showed that the fiber orientation exhibited a slight bias which was amplified with the addition of MnACAC. Use of focused ion beam scanning electron microscopy tomography also showed that MnO particles were evenly distributed through the fiber at low MnACAC concentrations, while at a 40 wt% loading the MnO particles were also visible on the surface. Comparison of the electrospun separators showed improved performance relative to a commercial Celgard separator (200 F g-1 vs 141 F g-1).

A miniature microbial fuel cell with conducting nanofibers-based 3D porous biofilm

NASA Astrophysics Data System (ADS)

Jiang, Huawei; Halverson, Larry J.; Dong, Liang

2015-12-01

Miniature microbial fuel cell (MFC) technology has received growing interest due to its potential applications in high-throughput screening of bacteria and mutants to elucidate mechanisms of electricity generation. This paper reports a novel miniature MFC with an improved output power density and short startup time, utilizing electrospun conducting poly(3,4-ethylenedioxythiophene) (PEDOT) nanofibers as a 3D porous anode within a 12 μl anolyte chamber. This device results in 423 μW cm-3 power density based on the volume of the anolyte chamber, using Shewanella oneidensis MR-1 as a model biocatalyst without any optimization of bacterial culture. The device also excels in a startup time of only 1hr. The high conductivity of the electrospun nanofibers makes them suitable for efficient electron transfer. The mean pore size of the conducting nanofibers is several micrometers, which is favorable for bacterial penetration and colonization of surfaces of the nanofibers. We demonstrate that S. oneidensis can fully colonize the interior region of this nanofibers-based porous anode. This work represents a new attempt to explore the use of electrospun PEDOT nanofibers as a 3D anode material for MFCs. The presented miniature MFC potentially will provide a high-sensitivity, high-throughput tool to screen suitable bacterial species and mutant strains for use in large-size MFCs.

Porous Electrospun Fibers with Self-Sealing Functionality: An Enabling Strategy for Trapping Biomacromolecules.

PubMed

Zhang, Jin; Zheng, Ting; Alarçin, Emine; Byambaa, Batzaya; Guan, Xiaofei; Ding, Jianxun; Zhang, Yu Shrike; Li, Zhongming

2017-12-01

Stimuli-responsive porous polymer materials have promising biomedical application due to their ability to trap and release biomacromolecules. In this work, a class of highly porous electrospun fibers is designed using polylactide as the polymer matrix and poly(ethylene oxide) as a porogen. Carbon nanotubes (CNTs) with different concentrations are further impregnated onto the fibers to achieve self-sealing functionality induced by photothermal conversion upon light irradiation. The fibers with 0.4 mg mL -1 of CNTs exhibit the optimum encapsulation efficiency of model biomacromolecules such as dextran, bovine serum albumin, and nucleic acids, although their photothermal conversion ability is slightly lower than the fibers with 0.8 mg mL -1 of CNTs. Interestingly, reversible reopening of the surface pores is accomplished with the degradation of PLA, affording a further possibility for sustained release of biomacromolecules after encapsulation. Effects of CNT loading on fiber morphology, structure, thermal/mechanical properties, degradation, and cell viability are also investigated. This novel class of porous electrospun fibers with self-sealing capability has great potential to serve as an enabling strategy for trapping/release of biomacromolecules with promising applications in, for example, preventing inflammatory diseases by scavenging cytokines from interstitial body fluids. © 2017 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

A novel electrospun nerve conduit enhanced by carbon nanotubes for peripheral nerve regeneration.

PubMed

Yu, Wenwen; Jiang, Xinquan; Cai, Ming; Zhao, Wen; Ye, Dongxia; Zhou, Yong; Zhu, Chao; Zhang, Xiuli; Lu, Xiaofeng; Zhang, Zhiyuan

2014-04-25

For artificial nerve conduits, great improvements have been achieved in mimicking the structures and components of autologous nerves. However, there are still some problems in conduit construction, especially in terms of mechanical properties, biomimetic surface tomography, electrical conductivity and sustained release of neurotrophic factors or cells. In this study, we designed and fabricated a novel electrospun nerve conduit enhanced by multi-walled carbon nanotubes (MWNTs) on the basis of a collagen/poly(ε-caprolactone) (collagen/PCL) fibrous scaffold. Our aim was to provide further knowledge about the mechanical effects and efficacy of MWNTs on nerve conduits as well as the biocompatibility and toxicology of MWNTs when applied in vivo.The results showed that as one component, carboxyl MWNTs could greatly alter the composite scaffold's hydrophilicity, mechanical properties and degradability. The electrospun fibers enhanced by MWNTs could support Schwann cell adhesion and elongation as a substrate in vitro. In vivo animal studies demonstrated that the MWNT-enhanced collagen/PCL conduit could effectively promote nerve regeneration of sciatic nerve defect in rats and prevent muscle atrophy without invoking body rejection or serious chronic inflammation. All of these results showed that this MWNT-enhanced scaffold possesses good biocompatibility and MWNTs might be excellent candidates as engineered nanocarriers for further neurotrophic factor delivery research.

TiO2 films with rich bulk oxygen vacancies prepared by electrospinning for dye-sensitized solar cells

NASA Astrophysics Data System (ADS)

Li, Xiaodong; Gao, Caitian; Wang, Jiangtao; Lu, Bingan; Chen, Wanjun; Song, Jie; Zhang, Shanshan; Zhang, Zhenxing; Pan, Xiaojun; Xie, Erqing

2012-09-01

Highly transparent nanocrystalline TiO2 films have been fabricated by electrospinning (ES) technique based on a transmutation process from as-spun nanofibers with an appropriate amount of tri-ethanolamine (TEOA) added to the precursor. A possible evolution mechanism of the transparent nanocrystalline TiO2 films is proposed. It is found that the films prepared via transmutation from electrospun nanofibers possess rich bulk oxygen vacancies (BOVs, PL band at 621-640 nm) by using photoluminescence (PL) spectroscopy. Contrastively, the dominant peak in PL spectrum of the spin-coated film is the emission from surface oxygen vacancies (SOVs, PL band at 537-555 nm). The electrospun TiO2 films with rich BOVs induce large open-circuit voltage (Voc) and fill factor (FF) improvements in dye-sensitized solar cells (DSCs), and thus a large improvement of energy conversion efficiency (η). In addition, these performance advantages are maintained for a double-layer cell with a doctor-bladed ˜7 μm top layer (P25 nanometer TiO2, Degussa) and an electrospun ˜3 μm bottom layer. The double-layer cell yields a high η of 6.01%, which has increased by 14% as compared with that obtained from a 10 μm thick P25 film.

Tailoring Wettability Through the Surface Modification of Electro-spun Polymers by Plasma and Sol-gel Treatments

DTIC Science & Technology

2014-11-01

Sa Majesté la Reine (en droit du Canada), telle que représentée par le ministre de la Défense nationale, 2014 DRDC-RDDC-2014-R102 i...avec la surface des matériaux est d’une importance fondamentale pour de nombreux processus, dont l’adhésion, les réactions chimiques, le transport...hydrodynamique et la nettoyabilité des surfaces. Les propriétés des surfaces peuvent se situer dans une gamme allant d’un caractère hydrophile ou

Albumin fiber scaffolds for engineering functional cardiac tissues.

PubMed

Fleischer, Sharon; Shapira, Assaf; Regev, Omri; Nseir, Nora; Zussman, Eyal; Dvir, Tal

2014-06-01

In recent years attempts to engineer contracting cardiac patches were focused on recapitulation of the myocardium extracellular microenvironment. We report here on our work, where for the first time, a three-dimensional cardiac patch was fabricated from albumin fibers. We hypothesized that since albumin fibers' mechanical properties resemble those of cardiac tissue extracellular matrix (ECM) and their biochemical character enables their use as protein carriers, they can support the assembly of cardiac tissues capable of generating strong contraction forces. Here, we have fabricated aligned and randomly oriented electrospun albumin fibers and investigated their structure, mechanical properties, and chemical nature. Our measurements showed that the scaffolds have improved elasticity as compared to synthetic electrospun PCL fibers, and that they are capable of adsorbing serum proteins, such as laminin leading to strong cell-matrix interactions. Moreover, due to the functional groups on their backbone, the fibers can be chemically modified with essential biomolecules. When seeded with rat neonatal cardiac cells the engineered scaffolds induced the assembly of aligned cardiac tissues with high aspect ratio cardiomyocytes and massive actinin striation. Compared to synthetic fibrous scaffolds, cardiac cells cultured within aligned or randomly oriented scaffolds formed functional tissues, exhibiting significantly improved function already on Day 3, including higher beating rate (P = 0.0002 and P < 0.0001, respectively), and higher contraction amplitude (P = 0.009 and P = 0.003, respectively). Collectively, our results suggest that albumin electrospun scaffolds can play a key role in contributing to the ex vivo formation of a contracting cardiac muscle tissue. © 2014 Wiley Periodicals, Inc.

Long-term liver-specific functions of hepatocytes in electrospun chitosan nanofiber scaffolds coated with fibronectin.

PubMed

Rajendran, Divya; Hussain, Ali; Yip, Derek; Parekh, Amit; Shrirao, Anil; Cho, Cheul H

2017-08-01

In this study, a new 3D liver model was developed using biomimetic nanofiber scaffolds and co-culture system consisting of hepatocytes and fibroblasts for the maintenance of long-term liver functions. The chitosan nanofiber scaffolds were fabricated by the electrospinning technique. To enhance cellular adhesion and spreading, the surfaces of the chitosan scaffolds were coated with fibronectin (FN) by adsorption and evaluated for various cell types. Cellular phenotype, protein expression, and liver-specific functions were extensively characterized by immunofluorescent and histochemical stainings, albumin enzyme-linked immunosorbent assay and Cytochrome p450 detoxification assays, and scanning electron microscopy. The electrospun chitosan scaffolds exhibited a highly porous and randomly oriented nanofibrous structure. The FN coating on the surface of the chitosan nanofibers significantly enhanced cell attachment and spreading, as expected, as surface modification with this cell adhesion molecule on the chitosan surface is important for focal adhesion formation and integrin binding. Comparison of hepatocyte mono-cultures and co-cultures in 3D culture systems indicated that the hepatocytes in co-cultures formed colonies and maintained their morphologies and functions for prolonged periods of time. The 3D liver tissue model developed in this study will provide useful tools toward the development of engineered liver tissues for drug screening and tissue engineering applications. © 2017 Wiley Periodicals, Inc. J Biomed Mater Res Part A: 105A: 2119-2128, 2017. © 2017 Wiley Periodicals, Inc.

Properties of electrospun pollock gelatin/poly(vinyl alcohol) and pollock gelatin/poly(lactic acid) fibers

USDA-ARS?s Scientific Manuscript database

Pollock gelatin/poly(vinyl alcohol) (PVA) fibers were electrospun using deionized water as the solvent and pollock gelatin/poly(lactic acid) (PLA) fibers were electrospun using 1,1,1,3,3,3-hexafluoro-2-propanol (HFIP) as the solvent. The chemical, thermal, and thermal stability properties were exami...

An aligned porous electrospun fibrous membrane with controlled drug delivery - An efficient strategy to accelerate diabetic wound healing with improved angiogenesis.

PubMed

Ren, Xiaozhi; Han, Yiming; Wang, Jie; Jiang, Yuqi; Yi, Zhengfang; Xu, He; Ke, Qinfei

2018-04-01

A chronic wound in diabetic patients is usually characterized by poor angiogenesis and delayed wound closure. The exploration of efficient strategy to significantly improve angiogenesis in the diabetic wound bed and thereby accelerate wound healing is still a significant challenge. Herein, we reported a kind of aligned porous poly (l-lactic acid) (PlLA) electrospun fibrous membranes containing dimethyloxalylglycine (DMOG)-loaded mesoporous silica nanoparticles (DS) for diabetic wound healing. The PlLA electrospun fibers aligned in a single direction and there were ellipse-shaped nano-pores in situ generated onto the surface of fibers, while the DS were well distributed in the fibers and the DMOG as well as Si ion could be controlled released from the nanopores on the fibers. The in vitro results revealed that the aligned porous composite membranes (DS-PL) could stimulate the proliferation, migration and angiogenesis-related gene expression of human umbilical vein endothelial cells (HUVECs) compared with the pure PlLA membranes. The in vivo study further demonstrated that the prepared DS-PL membranes significantly improved neo-vascularization, re-epithelialization and collagen formation as well as inhibited inflammatory reaction in the diabetic wound bed, which eventually stimulated the healing of the diabetic wound. Collectively, these results suggest that the combination of hierarchical structures (nanopores on the aligned fibers) with the controllable released DMOG drugs as well as Si ions from the membranes, which could create a synergetic effect on the rapid stimulation of angiogenesis in the diabetic wound bed, is a potential novel therapeutic strategy for highly efficient diabetic wound healing. A chronic wound in diabetic patients is usually characterized by the poor angiogenesis and the delayed wound closure. The main innovation of this study is to design a new kind of skin tissue engineered scaffold, aligned porous poly (l-lactic acid) (PlLA) electrospun membranes containing dimethyloxalylglycine (DMOG)-loaded mesoporous silica nanoparticles (DS), which could significantly improve angiogenesis in the diabetic wound bed and thereby accelerate diabetic wound healing. The results revealed that the electrospun fibers with ellipse-shaped nano-pores on the surface were aligned in a single direction, while there were DS particles distributed in the fibers and the DMOG as well as Si ions could be controllably released from the nanopores on the fibers. The in vitro studies demonstrated that the hierarchical nanostructures (nanopores on the aligned fibers) and the controllable released chemical active agents (DMOG drugs and Si ions) from the DS-PL membranes could exert a synergistic effect on inducing the endothelial cell proliferation, migration and differentiation. Above all, the scaffolds distinctly induced the angiogenesis, collagen deposition and re-epithelialization as well as inhibited inflammation reaction in the wound sites, which eventually stimulated the healing of diabetic wounds in vivo. The significance of the current study is that the combination of the hierarchical aligned porous nanofibrous structure with DMOG-loaded MSNs incorporated in electrospun fibers may suggest a high-efficiency strategy for chronic wound healing. Copyright © 2018 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

Development and application of biomimetic electrospun nanofibers in total joint replacement

NASA Astrophysics Data System (ADS)

Song, Wei

Failure of osseointegration (direct anchorage of an implant by bone formation at the bone-implant surface) and implant infection (such as that caused by Staphylococcus aureus, S. aureus) are the two main causes of implant failure and loosening. There is a critical need for orthopedic implants that promote rapid osseointegration and prevent bacterial colonization, particularly when placed in bone compromised by disease or physiology of the patients. A better understanding of the key factors that influence cell fate decisions at the bone-implant interface is required. Our study is to develop a class of "bone-like" nanofibers (NFs) that promote osseointegration while preventing bacterial colonization and subsequent infections. This research goal is supported by our preliminary data on the preparation of coaxial electrospun NFs composed of polycaprolactone (PCL) and polyvinyl alcohol (PVA) polymers arranged in a core-sheath shape. The PCL/PVA NFs are biocompatible and biodegradable with appropriate fiber diameter, pore size and mechanical strength, leading to enhanced cell adhesion, proliferation and differentiation of osteoblast precursor cells. The objective is to develop functionalized "bone-like" PCL/PVA NFs matrix embedded with antibiotics (doxycycline (Doxy), bactericidal and anti-osteoclastic) on prosthesis surface. Through a rat tibia implantation model, the Doxy incorporated coaxial NFs has demonstrated excellent in promoting osseointegration and bacteria inhibitory efficacy. NFs coatings significantly enhanced the bonding between implant and bone remodeling within 8 weeks. The SA-induced osteomyelitis was prevented by the sustained release of Doxy from NFs. The capability of embedding numerous bio-components including proteins, growth factors, drugs, etc. enables NFs an effective solution to overcome the current challenged issue in Total joint replacement. In summary, we proposed PCL/PVA electrospun nanofibers as promising biomaterials that can be applied on joint replacement prosthesis to improve osseointegration and prevent osteomyelitis.

Biomimetic coating of cross-linked gelatin to improve mechanical and biological properties of electrospun PET: A promising approach for small caliber vascular graft applications.

PubMed

Pezzoli, Daniele; Cauli, Elisa; Chevallier, Pascale; Farè, Silvia; Mantovani, Diego

2017-09-01

Electrospun PET (ePET) is a promising material for small caliber vascular graft applications owing to its tunable mechanical properties, biocompatibility, and nanofibrous structure that mimic the morphology of natural extracellular matrix. However, the inherent inertness of PET impairs the adhesion and proliferation of endothelial cells on the inner surface of ePET tubular grafts, hindering the formation of a functional endothelium. Gelatin coatings, owing to their ability to promote endothelialization, are a valuable approach to overcome the limitations of ePET. Herein, a novel process for the deposition of stable biomimetic coatings of gelatin on ePET tubular grafts is proposed. Electrospun PET was first aminated by plasma treatment and then coated with a gelatin hydrogel cross-linked in situ by a Michael-type addition reaction. Amination provided a superhydrophilic behavior to the ePET surface, allowing easy gelatin interpenetration along the wall thickness of the tubular structure, and the obtainment of thin coatings that maintained the morphology of ePET fibers. Gelatin coating was stable at long term in a physiological-like environment, noncytotoxic and promoted in vitro cell adhesion and proliferation. Noteworthy, the mechanical properties of gelatin-coated ePET tubular grafts were improved in terms of elastic modulus, compliance, and elastic recoil, finally better matching the characteristics of native blood vessels. Altogether, the proposed coating technique successfully combines the advantages of ePET nanofibrous structure with cross-linked gelatin biological cues and mechanical reinforcement, and emerges as a promising strategy for the development of biocompatible small caliber vascular grafts with superior biomimetic and mechanical properties. © 2017 Wiley Periodicals, Inc. J Biomed Mater Res Part A: 105A: 2405-2415, 2017. © 2017 Wiley Periodicals, Inc.

Functional electrospun nanofibers for multimodal sensitive detection of biogenic amines in food via a simple dipstick assay.

PubMed

Yurova, Nadezhda S; Danchuk, Alexandra; Mobarez, Sarah N; Wongkaew, Nongnoot; Rusanova, Tatiana; Baeumner, Antje J; Duerkop, Axel

2018-01-01

Electrospun nanofibers (ENFs) are promising materials for rapid diagnostic tests like lateral flow assays and dipsticks because they offer an immense surface area while excluding minimal volume, a variety of functional surface groups, and can entrap functional additives within their interior. Here, we show that ENFs on sample pads are superior in comparison to standard polymer membranes for the optical detection of biogenic amines (BAs) in food using a dipstick format. Specifically, cellulose acetate (CA) fibers doped with 2 mg/mL of the chromogenic and fluorogenic amine-reactive chameleon dye Py-1 were electrospun into uniform anionic mats. Those extract cationic BAs from real samples and Py-1 transduces BA concentrations into a change of color, reflectance, and fluorescence. Dropping a BA sample onto the nanofiber mat converts the weakly fluorescent pyrylium dye Py-1 into a strongly red emitting pyridinium dye. For the first time, a simple UV lamp excites fluorescence and a digital camera acts as detector. The intensity ratio of the red to the blue channel of the digital image is dependent on the concentration of most relevant BAs indicating food spoilage from 10 to 250 μM. This matches the permitted limits for BAs in foods and no false positive signals arise from secondary and tertiary amines. BA detection in seafood samples was also demonstrated successfully. The nanofiber mat dipsticks were up to sixfold more sensitive than those using a polymer membrane with the same dye embedded. Hence, nanofiber-based tests are not only superior to polymer-based dipstick assays, but will also improve the performance of established tests related to food safety, medical diagnostics, and environmental testing. Graphical Absract ᅟ.

Plasma treatment induces internal surface modifications of electrospun poly(L-lactic) acid scaffold to enhance protein coating

DOE Office of Scientific and Technical Information (OSTI.GOV)

Jin Seo, Hyok; Hee Lee, Mi; Kwon, Byeong-Ju

2013-08-21

Advanced biomaterials should also be bioactive with regard to desirable cellular responses, such as selective protein adsorption and cell attachment, proliferation, and differentiation. To enhance cell-material interactions, surface modifications have commonly been performed. Among the various surface modification approaches, atmospheric pressure glow discharge plasma has been used to change a hydrophobic polymer surface to a hydrophilic surface. Poly(L-lactic acid) (PLLA)-derived scaffolds lack cell recognition signals and the hydrophobic nature of PLLA hinders cell seeding. To make PLLA surfaces more conducive to cell attachment and spreading, surface modifications may be used to create cell-biomaterial interfaces that elicit controlled cell adhesion andmore » maintain differentiated phenotypes. In this study, (He) gaseous atmospheric plasma glow discharge was used to change the characteristics of a 3D-type polymeric scaffold from hydrophobic to hydrophilic on both the outer and inner surfaces of the scaffold and the penetration efficiency with fibronectin was investigated. Field-emission scanning electron microscope images showed that some grooves were formed on the PLLA fibers after plasma treatment. X-ray photoelectron spectroscopy data also showed chemical changes in the PLLA structure. After plasma treatment, -CN (285.76 eV) was increased in C1s and -NH{sub 2} (399.70 eV) was increased significantly and –N=CH (400.80 eV) and –NH{sub 3}{sup +} (402.05 eV) were newly appeared in N1s. These changes allowed fibronectin to penetrate into the PLLA scaffold; this could be observed by confocal microscopy. In conclusion, helium atmospheric pressure plasma treatment was effective in modifying the polymeric scaffold, making it hydrophilic, and this treatment can also be used in tissue engineering research as needed to make polymers hydrophilic.« less

Flexible SERS Substrates: Challenges and Opportunities

DTIC Science & Technology

2016-01-28

interactions between the analyte, silver nanoparticles , and a salt. This system has also been applied to detection of trace antibiotics for food safety...Cleanable SERS Substrates Based on Silver Nanoparticle Decorated Electrospun Nano-fibrous Membranes Chaoyang Jiang Porous electrospun nanofibrous...present our recent work on the preparation, characterization, and SERS activity of silver nanoparticle decorated polymeric electrospun nanofibers

Nitroxyl radical incorporated electrospun biodegradable poly(ester Amide) nanofiber membranes.

PubMed

Li, Lei; Chu, Chih-Chang

2009-01-01

Biodegradable amino-acid-based poly(ester amide) (PEA) ultra-fine fibers pre-loaded with a nitroxyl radical model compound, 4-amino-2.2.6.6-tetramethylpiperidine-1-oxy (4-amino-TEMPO), were prepared by electrospinning. The fiber size and morphology were shown to be greatly affected by the composition ratio of the solvent mixture (chloroform to DMF) prepared for electrospinning. Nano-size PEA fibers (approx. 640 nm) were obtained when PEA dope was electrospun from the chloroform/DMF solvent mixture at a volume ratio of 2 to 1 vs. 3.5 mum size PEA fibers obtained from chloroform-based electrospun dope. Due to the low glass transition temperature and completely amorphous structures, the PEA electrospun fibrous membranes gradually lost their fiber characteristic during 1 month incubation in PBS buffer at 37 degrees C. The glass transition temperature and heat of fusion of PEA electrospun fibers increased with an increasing incubation time and the most significant change occurred in the first day of incubation in PBS. A sustained release of 4-amino-TEMPO from the electrospun PEA nanofiber membranes was observed over the 1-month incubation period in PBS buffer at 37 degrees C and 38% of the incorporated 4-amino-TEMPO (initial loading level 10 mg/g PEA fibers) was released in one month. During this 1 month incubation in PBS buffer, there were only 1.2% weight loss and 11.7% molecular weight reduction for the electrospun PEA fibrous membranes. In an alpha-chymotrypsin medium (0.1 mg/ml PBS), however, the same electrospun PEA fibrous membranes showed more than 80% weight loss within 6 days and a complete release of encapsulated 4-amino-TEMPO within 5 days.

A super hydrophilic modification of poly(vinylidene fluoride) (PVDF) nanofibers: By in situ hydrothermal approach

NASA Astrophysics Data System (ADS)

Sheikh, Faheem A.; Zargar, Mohammad Afzal; Tamboli, Ashif H.; Kim, Hern

2016-11-01

Nanofibers fabricated from Poly(vinylidene fluoride) (PVDF) possesses potential applications in the field of filtrations, because of their excellent resistance towards harsh chemicals. However, the hydrophobicity restricts its further application. In this work, we focus on optimal parameters for post-electrospun tethering of Poly(vinyl alcohol) (PVA) as superhydrophilic domain onto each individual PVDF nanofibers by exploiting the in situ hydrothermal approach. The results indicated an increase in nanofiber diameters due to coating of PVA and improved surface wettability of PVDF nanofibers. The tensile tests of nanofibers indicated that mechanical properties of PVDF nanofibers could be sharply tuned from rigid to ductile. Furthermore, the studies strongly suggest that in situ hydrothermal treatment of post-electrospun nanofibers can improve the water contact angle and these nanofibers can be used in varied applications (e.g., in water purification systems).

MOFabric: Electrospun Nanofiber Mats from PVDF/UiO-66-NH2 for Chemical Protection and Decontamination.

PubMed

Lu, Annie Xi; McEntee, Monica; Browe, Matthew A; Hall, Morgan G; DeCoste, Jared B; Peterson, Gregory W

2017-04-19

Textiles capable of capture and detoxification of toxic chemicals, such as chemical-warfare agents (CWAs), are of high interest. Some metal-organic frameworks (MOFs) exhibit superior reactivity toward CWAs. However, it remains a challenge to integrate powder MOFs into engineered materials like textiles, while retaining functionalities like crystallinity, adsorptivity, and reactivity. Here, we present a simple method of electrospinning UiO-66-NH 2 , a zirconium MOF, with polyvinylidene fluoride (PVDF). The electrospun composite, which we refer to as "MOFabric", exhibits comparable crystal patterns, surface area, chlorine uptake, and simulant hydrolysis to powder UiO-66-NH 2 . The MOFabric is also capable of breaking down GD (O-pinacolyl methylphosphonofluoridae) faster than powder UiO-66-NH 2. Half-life of GD monitored by solid-state NMR for MOFabric is 131 min versus 315 min on powder UiO-66-NH 2 .

Enhanced vapor transport in membrane distillation via functionalized carbon nanotubes anchored into electrospun nanofibres

PubMed Central

Kyoungjin An, Alicia; Lee, Eui-Jong; Guo, Jiaxin; Jeong, Sanghyun; Lee, Jung-Gil; Ghaffour, Noreddine

2017-01-01

To ascertain membrane distillation (MD) as an emerging desalination technology to meet the global water challenge, development of membranes with ideal material properties is crucial. Functionalized carbon nanotubes (CNTs) were anchored to nanofibres of electrospun membranes. Covalent modification and fluorination of CNTs improved their dispersibility and interfacial interaction with the polymer membrane, resulting in well-aligned CNTs inside crystalline fibres with superhydrophobicity. Consideration for the chemical/physical properties of the CNT composite membranes and calculation of their theoretical fluxes revealed the mechanism of MD: CNTs facilitated the repulsive force for Knudsen and molecular diffusions, reduced the boundary-layer effect in viscous flow, and assisted surface diffusion, allowing for fast vapor transport with anti-wetting. This study shows that the role of CNTs and an optimal composite ratio can be used to reduce the gap between theoretical and experimental approaches to desalination. PMID:28134288

The research and preparation of a novel nano biodegradable polymer external reinforcement

NASA Astrophysics Data System (ADS)

Zhang, Xiangman; Chen, Bin; Fu, Weiguo; Fang, Zhengdong; Liu, Zhenjie; Lu, Weifeng; Shi, Zhengyu; Chen, Lili; Chen, Tao

2011-10-01

The use of current drug-loaded vascular scaffolds is limited in sustained drug release and stability studies in clinical and preclinical trials. We found that poly( L-glutamic acid)-b-poly(propylene oxide)-b-poly( L-glutamic acid) (PLGA-b-PPO-b-PLGA) triblock copolymers can deliver multiple poorly water-soluble drugs (e.g., Paclitaxel) at clinically relevant doses. In this study, we synthesized a new drug-loaded vascular external graft with electrospun nanofibrous scaffolds [poly( L-lactide-co-ɛ-caprolactone) (PLCL):fibrinogen; 2:1 (w/w)] and drug-loaded PLGA-b-PPO-b-PLGA micelles. Cell proliferation and viability assay results showed that beagle smooth muscle cells grew well on the surface of vascular graft-coated micelles at a percentages of 10% (w/w) GPG:PLCL-fibrinogen. This study demonstrates that micelle-coated electrospun PLCL-fibrinogen vascular scaffolds have potential applications in vascular tissue engineering.

The role of nanostructured mesoporous silicon in discriminating in vitro calcification for electrospun composite tissue engineering scaffolds

NASA Astrophysics Data System (ADS)

Fan, Dongmei; Akkaraju, Giridhar R.; Couch, Ernest F.; CanhamCurrent Address, Intrinsiq Materials Ltd, Geraldine Road, Malvern Wr14 3SZ Uk, Leigh T.; Coffer, Jeffery L.

2011-02-01

The impact of mesoporous silicon (PSi) particles-embedded either on the surface, or totally encapsulated within electrospun poly (ε-caprolactone) (PCL) fibers-on its properties as a tissue engineering scaffold is assessed. Our findings suggest that the resorbable porous silicon component can sensitively accelerate the necessary calcification process in such composites. Calcium phosphate deposition on the scaffolds was measured via in vitro calcification assays both at acellular and cellular levels. Extensive attachment of fibroblasts, human adult mesenchymal stem cells, and mouse stromal cells to the scaffold were observed. Complementary cell differentiation assays and ultrastructural measurements were also carried out; the levels of alkaline phosphatase expression, a specific biomarker for mesenchymal stem cell differentiation, show that the scaffolds have the ability to mediate such processes, and that the location of the Si plays a key role in levels of expression.

Synergism of Electrospinning and Nano-alumina Trihydrate on the Polymorphism, Crystallinity and Piezoelectric Performance of PVDF Nanofibers

NASA Astrophysics Data System (ADS)

Khalifa, Mohammed; Deeksha, B.; Mahendran, Arunjunairaj; Anandhan, S.

2018-03-01

Poly(vinlylidene fluoride) (PVDF) is known for its electroactive phases, which can be nucleated by incorporating nanoparticles into PVDF to enhance its piezoelectric performance. In this study, the synergistic effect of electrospinning and nano alumina trihydrate (ATH) filler was used to enhance the electroactive β phase of PVDF. Electrospun nanofibers of PVDF/ATH nanocomposite (PANCF) were synthesized with different loadings of ATH. The presence of ATH enhances the surface charges of the electrospun droplets, leading to thinner fibers. The highest β-phase content was found to be 70.1% for PANCF with 10% ATH. The piezoelectric performance of the nanofiber mats was studied using an indigenous setup. The highest voltage output of 840 mV was produced by PANCF with 10% ATH. These nanofibers could be a promising material in the field of sensors, actuators and energy-harvesting applications.

Improved electrical conductivity of poly(ethylene oxide) nanofibers using multi-walled carbon nanotubes

NASA Astrophysics Data System (ADS)

Lee, J. Y.; Kang, T.-H.; Choi, J. H.; Choi, I.-S.; Yu, W.-R.

2018-03-01

Highly conductive nanofibers with 1570 S/m were obtained from an electrospun solution of polymer containing multiwalled carbon nanotubes (MWCNTs). Homogeneous dispersion of high concentrations of MWCNTs was achieved by attaching poly(styrenesulfonic acid graft aniline) (PSS-g-ANI), an amphiphilic surfactant, to the MWCNT surface. The hydrophilic sulfonic acid group facilitated the dissolution of PSS-g-ANI-grafted MWCNTs in a polyethylene oxide (PEO) solution up to 6.7 wt% MWCNT. To our knowledge, this is the highest level of MWCNT doping attained in a solution designed for electrospinning. With the incorporation of PSS-g-ANI, the concentration of MWCNTs embedded in the electrospun nanofibers increased. More importantly, the alignment of MWCNTs along the nanofiber axis increased significantly, as confirmed by observed birefringence under crossed polarizers. The combination of higher doping levels and better alignment afforded highly conductive nanofibers suitable for electronic nanodevices.

[Application of electrostatic spinning technology in nano-structured polymer scaffold].

PubMed

Chen, Denglong; Li, Min; Fang, Qian

2007-04-01

To review the latest development in the research on the application of the electrostatic spinning technology in preparation of the nanometer high polymer scaffold. The related articles published at home and abroad during the recent years were extensively reviewed and comprehensively analyzed. Micro/nano-structure and space topology on the surfaces of the scaffold materials, especially the weaving structure, were considered to have an important effect on the cell adhesion, proliferation, directional growth, and biological activation. The electrospun scaffold was reported to have a resemblance to the structure of the extracellular matrix and could be used as a promising scaffold for the tissue engineering application. The electrospun scaffolds were applied to the cartilage, bone, blood vessel, heart, and nerve tissue engineering fields. The nano-structured polymer scaffold can support the cell adhesion, proliferation, location, and differentiation, and this kind of scaffold has a considerable value in the tissue engineering field.

Enhanced vapor transport in membrane distillation via functionalized carbon nanotubes anchored into electrospun nanofibres

NASA Astrophysics Data System (ADS)

Kyoungjin An, Alicia; Lee, Eui-Jong; Guo, Jiaxin; Jeong, Sanghyun; Lee, Jung-Gil; Ghaffour, Noreddine

2017-01-01

To ascertain membrane distillation (MD) as an emerging desalination technology to meet the global water challenge, development of membranes with ideal material properties is crucial. Functionalized carbon nanotubes (CNTs) were anchored to nanofibres of electrospun membranes. Covalent modification and fluorination of CNTs improved their dispersibility and interfacial interaction with the polymer membrane, resulting in well-aligned CNTs inside crystalline fibres with superhydrophobicity. Consideration for the chemical/physical properties of the CNT composite membranes and calculation of their theoretical fluxes revealed the mechanism of MD: CNTs facilitated the repulsive force for Knudsen and molecular diffusions, reduced the boundary-layer effect in viscous flow, and assisted surface diffusion, allowing for fast vapor transport with anti-wetting. This study shows that the role of CNTs and an optimal composite ratio can be used to reduce the gap between theoretical and experimental approaches to desalination.

Exploring the effects of electrospinning processing protocols on fiber surface morphology and polymer chain conformation

NASA Astrophysics Data System (ADS)

Stephens, Jean S.

Electrospinning is a fiber formation technique that uses electrostatic forces to create continuous, nanometer diameter fibers. The work presented here focuses on the continuing efforts to build a stronger fundamental understanding of electrospinning by exploring structure/property/process relationships by investigating the effects of process protocols on fiber surface morphology and polymer chain conformation. By varying the processing parameters it has been possible to produce fibers with unique surface features, microtextured/nanoporous fibers and nanowebs. In the microtextured/nanoporous fiber studies, changing the solution concentration, solvent volatility, and relative humidity was found to alter the size, shape, and distribution of pores on the fiber surface. The mechanisms that can explain the pore formation and texturing on the surface of the fibers are phase separation (aggregation into polymer rich and polymer lean regions) and breath figures (evaporative cooling and vapor condensation). Through a judicious choice of the electrospinning processing parameters we have also been able to create "web" like structures of nanofibers (5--25 nm) from collagen, dragline silk analog, nylon, and denatured collagen. Electrostatic repulsion and thin film dewetting are thought to be responsible for the formation of the nanowebs. These unique structures were characterized using FESEM, TEM, OM, and AFM. Raman spectroscopy, initially developed as a "real time" characterization technique to study electrospun fiber formation, has also been used to investigate the effect of electrospinning on the chain conformation of bioinspired polymers. Comparing the spectrum of the bulk material to that of the electrospun material identified conformational changes in nylon 6 and dragline silk analog. The conformational change in nylon 6 (alpha-form to gamma-form) results from the stresses induced on the electrospinning jet during fiber formation, whereas the conformational change in the silk analog (beta-sheet to alpha-helical) result from electric field assembling of the charged a-helical segments of the protein polymer in solution. The investigations described here have allowed us to build a virtual database of the processing conditions needed to create materials for tissue engineering constructs. Electrospun collagen membranes have been used in preliminary cell attachment studies. From the trials it was observed that the cells migrated into the membranes indicating that the membranes are suitable for tissue engineering scaffolds.

Highly sensitive biofunctionalized mesoporous electrospun TiO(2) nanofiber based interface for biosensing.

PubMed

Mondal, Kunal; Ali, Md Azahar; Agrawal, Ved V; Malhotra, Bansi D; Sharma, Ashutosh

2014-02-26

The surface modified and aligned mesoporous anatase titania nanofiber mats (TiO2-NF) have been fabricated by electrospinning for esterified cholesterol detection by electrochemical technique. The electrospinning and porosity of mesoporous TiO2-NF were controlled by use of polyvinylpyrrolidone (PVP) as a sacrificial carrier polymer in the titanium isopropoxide precursor. The mesoporous TiO2-NF of diameters ranging from 30 to 60 nm were obtained by calcination at 470 °C and partially aligned on a rotating drum collector. The functional groups such as -COOH, -CHO etc. were introduced on TiO2-NF surface via oxygen plasma treatment making the surface hydrophilic. Cholesterol esterase (ChEt) and cholesterol oxidase (ChOx) were covalently immobilized on the plasma treated surface of NF (cTiO2-NF) via N-ethyl-N0-(3-dimethylaminopropyl carbodiimide) and N-hydroxysuccinimide (EDC-NHS) chemistry. The high mesoporosity (∼61%) of the fibrous film allowed enhanced loading of the enzyme molecules in the TiO2-NF mat. The ChEt-ChOx/cTiO2-NF-based bioelectrode was used to detect esterified cholesterol using electrochemical technique. The high aspect ratio, surface area of aligned TiO2-NF showed excellent voltammetric and catalytic response resulting in improved detection limit (0.49 mM). The results of response studies of this biosensor show excellent sensitivity (181.6 μA/mg dL(-1)/cm(2)) and rapid detection (20 s). This proposed strategy of biomolecule detection is thus a promising platform for the development of miniaturized device for biosensing applications.

Thermomechanical Properties of Lignin-Based Electrospun Nanofibers and Films Reinforced with Cellulose Nanocrystals: A Dynamic Mechanical and Nanoindentation Study

Treesearch

Mariko Ago; Joseph E. Jakes; Orlando J. Rojas

2013-01-01

We produced defect-free electrospun fibers from aqueous dispersions of lignin, poly(vinyl alcohol) (PVA), and cellulose nanocrystals (CNCs), which were used as reinforcing nanoparticles. The thermomechanical performance of the lignin-based electrospun fibers and the spin-coated thin films was improved when they were embedded with CNCs. Isochronal dynamic mechanical...

In vitro feasibility study of the use of a magnetic electrospun chitosan nanofiber composite for hyperthermia treatment of tumor cells.

PubMed

Lin, Ta-Chun; Lin, Feng-Huei; Lin, Jui-Che

2012-07-01

Hyperthermia has been reported to be an effective cancer treatment modality, as tumor cells are more temperature-sensitive than their normal counterparts. Since the ambient temperature can be increased by placing magnetic nanoparticles in an alternating magnetic field it has become of interest to incorporate these magnetic nanoparticles into biodegradable nanofibers for possible endoscopic hyperthermia treatment of malignant tumors. In this preliminary investigation we have explored various characteristics of biodegradable electrospun chitosan nanofibers containing magnetic nanoparticles prepared by different methods. These methods included: (1) E-CHS-Fe(3)O(4), with electrospun chitosan nanofibers directly immersed in a magnetic nanoparticle solution; (2) E-CHS-Fe(2+), with the electrospun chitosan nanofibers initially immersed in Fe(+2)/Fe(+3) solution, followed by chemical co-precipitation of the magnetic nanoparticles. The morphology and crystalline phase of the magnetic electrospun nanofiber matrices were determined by scanning electron microscopy, transmission electron microscopy, selected area electron diffraction, and X-ray diffraction spectroscopy. The magnetic characteristics were measured using a superconducting quantum interference device. The heating properties of these magnetic electrospun nanofiber matrices in an alternating magnetic field were investigated at a frequency of 750 kHz and magnetic intensity of 6.4 kW. In vitro cell incubation experiments indicated that these magnetic electrospun nanofiber matrices are non-cytotoxic and can effectively reduce tumor cell proliferation upon application of a magnetic field. Copyright © 2012 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

Preparation and adsorption behavior of aminated electrospun polyacrylonitrile nanofiber mats for heavy metal ion removal.

PubMed

Kampalanonwat, Pimolpun; Supaphol, Pitt

2010-12-01

Polyacrylonitrile (PAN) nanofiber mats were prepared by electrospinning and they were further modified to contain amidino diethylenediamine chelating groups on their surface via heterogeneous reaction with diethylenetriamine (DETA). The obtained aminated PAN (APAN) nanofiber mats were evaluated for their chelating property with four types of metal ions, namely Cu(II), Ag(I), Fe(II), and Pb(II) ions. The amounts of the metal ions adsorbed onto the APAN nanofiber mats were influenced by the initial pH and the initial concentration of the metal ion solutions. Increasing the contact time also resulted in a monotonous increase in the adsorbed amounts of the metal ions, which finally reached equilibria at about 10 h for Cu(II) ions and about 5 h for Ag(I), Fe(II), and Pb(II) ions. The maximal adsorption capacities of the metal ions on the APAN nanofiber mats, as calculated from the Langmuir model, were 150.6, 155.5, 116.5, and 60.6 mg g(-1), respectively. Lastly, the spent APAN nanofiber mats could be facilely regenerated with a hydrochloric acid (HCl) aqueous solution.

Comparison of cell behavior on pva/pva-gelatin electrospun nanofibers with random and aligned configuration

NASA Astrophysics Data System (ADS)

Huang, Chen-Yu; Hu, Keng-Hsiang; Wei, Zung-Hang

2016-12-01

Electrospinning technique is able to create nanofibers with specific orientation. Poly(vinyl alcohol) (PVA) have good mechanical stability but poor cell adhesion property due to the low affinity of protein. In this paper, extracellular matrix, gelatin is incorporated into PVA solution to form electrospun PVA-gelatin nanofibers membrane. Both randomly oriented and aligned nanofibers are used to investigate the topography-induced behavior of fibroblasts. Surface morphology of the fibers is studied by optical microscopy and scanning electron microscopy (SEM) coupled with image analysis. Functional group composition in PVA or PVA-gelatin is investigated by Fourier Transform Infrared (FTIR). The morphological changes, surface coverage, viability and proliferation of fibroblasts influenced by PVA and PVA-gelatin nanofibers with randomly orientated or aligned configuration are systematically compared. Fibroblasts growing on PVA-gelatin fibers show significantly larger projected areas as compared with those cultivated on PVA fibers which p-value is smaller than 0.005. Cells on PVA-gelatin aligned fibers stretch out extensively and their intracellular stress fiber pull nucleus to deform. Results suggest that instead of the anisotropic topology within the scaffold trigger the preferential orientation of cells, the adhesion of cell membrane to gelatin have substantial influence on cellular behavior.

Calcium phosphate coated Keratin-PCL scaffolds for potential bone tissue regeneration.

PubMed

Zhao, Xinxin; Lui, Yuan Siang; Choo, Caleb Kai Chuen; Sow, Wan Ting; Huang, Charlotte Liwen; Ng, Kee Woei; Tan, Lay Poh; Loo, Joachim Say Chye

2015-04-01

The incorporation of hydroxyapatite (HA) nanoparticles within or on the surface of electrospun polymeric scaffolds is a popular approach for bone tissue engineering. However, the fabrication of osteoconductive composite scaffolds via benign processing conditions still remains a major challenge to date. In this work, a new method was developed to achieve a uniform coating of calcium phosphate (CaP) onto electrospun keratin-polycaprolactone composites (Keratin-PCL). Keratin within PCL was crosslinked to decrease its solubility, before coating of CaP. A homogeneous coating was achieved within a short time frame (~10min) by immersing the scaffolds into Ca(2+) and (PO4)(3-) solutions separately. Results showed that the incorporation of keratin into PCL scaffolds not only provided nucleation sites for Ca(2+) adsorption and subsequent homogeneous CaP surface deposition, but also facilitated cell-matrix interactions. An improvement in the mechanical strength of the resultant composite scaffold, as compared to other conventional coating methods, was also observed. This approach of developing a biocompatible bone tissue engineering scaffold would be adopted for further in vitro osteogenic differentiation studies in the future. Copyright © 2015 Elsevier B.V. All rights reserved.

Distributed feedback imprinted electrospun fiber lasers.

PubMed

Persano, Luana; Camposeo, Andrea; Del Carro, Pompilio; Fasano, Vito; Moffa, Maria; Manco, Rita; D'Agostino, Stefania; Pisignano, Dario

2014-10-01

Imprinted, distributed feedback lasers are demonstrated on individual, active electrospun polymer nanofibers. In addition to advantages related to miniaturization, optical confinement and grating nanopatterning lead to a significant threshold reduction compared to conventional thin-film lasers. The possibility of imprinting arbitrary photonic crystal geometries on electrospun lasing nanofibers opens new opportunities for realizing optical circuits and chips. © 2014 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Sulfophenyl-Functionalized Reduced Graphene Oxide Networks on Electrospun 3D Scaffold for Ultrasensitive NO₂ Gas Sensor.

PubMed

Zou, Bin; Guo, Yunlong; Shen, Nannan; Xiao, Anshan; Li, Mingjun; Zhu, Liang; Wan, Pengbo; Sun, Xiaoming

2017-12-19

Ultrasensitive room temperature real-time NO₂ sensors are highly desirable due to potential threats on environmental security and personal respiratory. Traditional NO₂ gas sensors with highly operated temperatures (200-600 °C) and limited reversibility are mainly constructed from semiconducting oxide-deposited ceramic tubes or inter-finger probes. Herein, we report the functionalized graphene network film sensors assembled on an electrospun three-dimensional (3D) nanonetwork skeleton for ultrasensitive NO₂ sensing. The functional 3D scaffold was prepared by electrospinning interconnected polyacrylonitrile (PAN) nanofibers onto a nylon window screen to provide a 3D nanonetwork skeleton. Then, the sulfophenyl-functionalized reduced graphene oxide (SFRGO) was assembled on the electrospun 3D nanonetwork skeleton to form SFRGO network films. The assembled functionalized graphene network film sensors exhibit excellent NO₂ sensing performance (10 ppb to 20 ppm) at room temperature, reliable reversibility, good selectivity, and better sensing cycle stability. These improvements can be ascribed to the functionalization of graphene with electron-withdrawing sulfophenyl groups, the high surface-to-volume ratio, and the effective sensing channels from SFRGO wrapping onto the interconnected 3D scaffold. The SFRGO network-sensing film has the advantages of simple preparation, low cost, good processability, and ultrasensitive NO₂ sensing, all advantages that can be utilized for potential integration into smart windows and wearable electronic devices for real-time household gas sensors.

Biosilica-loaded poly(ϵ-caprolactone) nanofibers mats provide a morphogenetically active surface scaffold for the growth and mineralization of the osteoclast-related SaOS-2 cells.

PubMed

Müller, Werner E G; Tolba, Emad; Schröder, Heinz C; Diehl-Seifert, Bärbel; Link, Thorben; Wang, Xiaohong

2014-10-01

Bioprinting/3D cell printing procedures for the preparation of scaffolds/implants have the potential to revolutionize regenerative medicine. Besides biocompatibility and biodegradability, the hardness of the scaffold material is of critical importance to allow sufficient mechanical protection and, to the same extent, allow migration, cell-cell, and cell-substrate contact formation of the matrix-embedded cells. In the present study, we present a strategy to encase a bioprinted, cell-containing, and soft scaffold with an electrospun mat. The electrospun poly(ϵ-caprolactone) (PCL) nanofibers mats, containing tetraethyl orthosilicate (TEOS), were subsequently incubated with silicatein. Silicatein synthesizes polymeric biosilica by polycondensation of ortho-silicate that is formed from prehydrolyzed TEOS. Biosilica provides a morphogenetically active matrix for the growth and mineralization of osteoblast-related SaOS-2 cells in vitro. Analysis of the microstructure of the 300-700 nm thick PCL/TEOS nanofibers, incubated with silicatein and prehydrolyzed TEOS, displayed biosilica deposits on the mats formed by the nanofibers. We conclude and propose that electrospun PCL nanofibers mats, coated with biosilica, may represent a morphogenetically active and protective cover for bioprinted cell/tissue-like units with a suitable mechanical stability, even if the cells are embedded in a softer matrix. Copyright © 2014 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

The effect of controlled release of PDGF-BB from heparin-conjugated electrospun PCL/gelatin scaffolds on cellular bioactivity and infiltration

PubMed Central

Lee, Jongman; Yoo, James J.; Atala, Anthony; Lee, Sang Jin

2013-01-01

Heparin-conjugated electrospun poly(ε-caprolactone) (PCL)/gelatin scaffolds were developed to provide controlled release of platelet-derived growth factor-BB (PDGF-BB) and allow prolonged bioactivity of this molecule. A mixture of PCL and gelatin was electrospun into three different morphologies. Next, heparin molecules were conjugated to the reactive surface of the scaffolds. This heparin-conjugated scaffold allowed the immobilization of PDGF-BB via electrostatic interaction. In vitro PDGF-BB release profiles indicated that passive physical adsorption of PDGF-BB to non-heparinized scaffolds resulted in an initial burst release of PDGF-BB within 5 days, which then leveled off. However, electrostatic interaction between PDGF-BB and the heparin-conjugated scaffolds gave rise to a sustained release of PDGF-BB over the course of 20 days without an initial burst. Moreover, PDGF-BB that was strongly bound to the heparin-conjugated scaffolds enhanced smooth muscle cell (SMC) proliferation. In addition, scaffolds composed of 3.0 µm diameter fibers that were immobilized with PDGF-BB accelerated SMC infiltration into the scaffold when compared to scaffolds composed of smaller diameter fibers or scaffolds that did not release PDGF-BB. We concluded that the combination of the large pore structure in the scaffolds and the heparin-mediated delivery of PDGF-BB provided the most effective cellular interactions through synergistic physical and chemical cues. PMID:22770570

Effect of fiber orientation of collagen-based electrospun meshes on human fibroblasts for ligament tissue engineering applications.

PubMed

Full, Sean Michael; Delman, Connor; Gluck, Jessica M; Abdmaulen, Raushan; Shemin, Richard J; Heydarkhan-Hagvall, Sepideh

2015-01-01

Within the past two decades polylactic-co-glycolic acid (PLGA) has gained considerable attention as a biocompatible and biodegradable polymer that is suitable for tissue engineering and regenerative medicine. In this present study, we have investigated the potential of PLGA, collagen I (ColI), and polyurethane (PU) scaffolds for ligament tissue regeneration. Two different ratios of PLGA (50:50 and 85:15) were used to determine the effects on mechanical tensile properties and cell adhesion. The Young's modulus, tensile stress at yield, and ultimate tensile strain of PLGA(50:50)-ColI-PU scaffolds demonstrated similar tensile properties to that of ligaments found in the knee. Whereas, scaffolds composed of PLGA(85:15)-ColI-PU had lower tensile properties than that of ligaments. Furthermore, we investigated the effect of fiber orientation on mechanical properties and our results indicate that aligned fiber scaffolds demonstrate higher tensile properties than scaffolds with random fiber orientation. Also, human fibroblasts attached and proliferated with no need for additional surface modifications to the presented electrospun scaffolds in both categories. Collectively, our investigation demonstrates the effectiveness of electrospun PLGA scaffolds as a suitable candidate for regenerative medicine, capable of being manipulated and combined with other polymers to create three-dimensional microenvironments with adjustable tensile properties to mimic native tissues. © 2014 Wiley Periodicals, Inc.

Electrospun Polymer Blend Nanofibers for Tunable Drug Delivery: The Role of Transformative Phase Separation on Controlling the Release Rate.

PubMed

Tipduangta, Pratchaya; Belton, Peter; Fábián, László; Wang, Li Ying; Tang, Huiru; Eddleston, Mark; Qi, Sheng

2016-01-04

Electrospun fibrous materials have a wide range of biomedical applications, many of them involving the use of polymers as matrices for incorporation of therapeutic agents. The use of polymer blends improves the tuneability of the physicochemical and mechanical properties of the drug loaded fibers. This also benefits the development of controlled drug release formulations, for which the release rate can be modified by altering the ratio of the polymers in the blend. However, to realize these benefits, a clear understanding of the phase behavior of the processed polymer blend is essential. This study reports an in depth investigation of the impact of the electrospinning process on the phase separation of a model partially miscible polymer blend, PVP K90 and HPMCAS, in comparison to other conventional solvent evaporation based processes including film casting and spin coating. The nanoscale stretching and ultrafast solvent removal of electrospinning lead to an enhanced apparent miscibility between the polymers, with the same blends showing micronscale phase separation when processed using film casting and spin coating. Nanoscale phase separation in electrospun blend fibers was confirmed in the dry state. Rapid, layered, macroscale phase separation of the two polymers occurred during the wetting of the fibers. This led to a biphasic drug release profile from the fibers, with a burst release from PVP-rich phases and a slower, more continuous release from HPMCAS-rich phases. It was noted that the model drug, paracetamol, had more favorable partitioning into the PVP-rich phase, which is likely to be a result of greater hydrogen bonding between PVP and paracetamol. This led to higher drug contents in the PVP-rich phases than the HPMCAS-rich phases. By alternating the proportions of the PVP and HPMCAS, the drug release rate can be modulated.

Atmospheric plasma surface modifications of electrospun PCL/chitosan/PCL hybrid scaffolds by nozzle type plasma jets for usage of cell cultivation

NASA Astrophysics Data System (ADS)

Surucu, Seda; Masur, Kai; Turkoglu Sasmazel, Hilal; Von Woedtke, Thomas; Weltmann, Klaus Dieter

2016-11-01

This paper reports Ar gas, Ar + O2, Ar + O2 + N2 gas mixtures and dry air plasma modifications by atmospheric pressure argon driven kINPen and air driven Diener (PlasmaBeam) plasma jets to alter surface properties of three dimensional (3D), electrospun PCL/Chitosan/PCL layer by layer hybrid scaffolds to improve human fibroblast (MRC5) cell attachment and growth. The characterizations of the samples were done by contact angle (CA) measurements, scanning electron microscopy (SEM), X-Ray Photoelectron spectroscopy (XPS) analysis. The results showed that the plasma modification carried out under dry air and Ar + O2 + N2 gas mixtures were altered effectively the nanotopography and the functionality of the material surfaces. It was found that the samples treated with Ar + O2 + N2 gas mixtures for 1 min and dry air for 9 min have better hydrophilicity 78.9° ± 1.0 and 75.6° ± 0.1, respectively compared to the untreated samples (126.5°). Biocompatibility performance of the scaffolds was determined with alamarBlue (aB) assay and MTT assay methods, Giemsa staining, fluorescence microscope, confocal laser scanning microscope (CLSM) and scanning electron microscope (SEM) analyses. The results showed that plasma treated samples increased the hydrophilicity and oxygen functionality and topography of the surfaces significantly, thus affecting the cell viability and proliferation on/within scaffolds.

Release of tetracycline hydrochloride from electrospun poly(ethylene-co-vinylacetate), poly(lactic acid), and a blend.

PubMed

Kenawy, El-Refaie; Bowlin, Gary L; Mansfield, Kevin; Layman, John; Simpson, David G; Sanders, Elliot H; Wnek, Gary E

2002-05-17

Electrospun fiber mats are explored as drug delivery vehicles using tetracycline hydrochloride as a model drug. The mats were made either from poly(lactic acid) (PLA), poly(ethylene-co-vinyl acetate) (PEVA), or from a 50:50 blend of the two. The fibers were electrospun from chloroform solutions containing a small amount of methanol to solubilize the drug. The release of the tetracycline hydrochloride from these new drug delivery systems was followed by UV-VIS spectroscopy. Release profiles from the electrospun mats were compared to a commercially available drug delivery system, Actisite (Alza Corporation, Palo Alto, CA), as well as to cast films of the various formulations.

Photovoltaic and thermal properties of electrolytes based on electrospun poly(vinylidene fluoride-hexafluoro propylene)/poly(methyl methacrylate) nanofibers for dye-sensitized solar cells.

PubMed

Jang, Young-Wook; Won, Du-Hyun; Kim, Young-Keun; Hwang, Won-Pill; Jang, Sung-Il; Jeong, Sung-Hoon; Kim, Mi-Ra; Lee, Jin-Kook

2014-08-01

We prepared electrospun polymer nanofibers by electrospnning method and investigated about their applications to dye-sensitized solar cells (DSSCs). Electrospun polymer nanofibers applied to the polymer matrix in electrolyte for DSSCs. To improve the stiffness of polymer nanofiber, poly(vinylidene fluoride-hexafluoro propylene)/Poly(methyl methacrylate) (PVDF-HFP/PMMA) blend nanofibers were prepared and examined. In the electrospun PVDF-HFP/PMMA (1:1) blend nanofibers, the best results of VOC, JSC, FF, and efficiency of the DSSC devices showed 0.71 V, 12.8 mA/cm2, 0.61, and 5.56% under AM 1.5 illumination.

Environmental fate and effect of biodegradable electro-spun scaffolds (biomaterial)-a case study.

PubMed

Irizar, A; Amorim, M J B; Fuller, K P; Zeugolis, D I; Scott-Fordsmand, J J

2018-04-30

Poly-ε-caprolactone (PCL) based medical devices are increasingly produced and thus, their presence in the environment is likely to increase. The present study analysed the biodegradation of PCL electro-spun scaffolds (alone) and PCL electro-spun scaffolds coated with human recombinant (hR) collagen and Bovine Achilles tendon (BAT) collagen in sewage sludge and in soil. Additionally, an eco-toxicological test with the model organism Enchytraeus crypticus was performed to assess environmental hazard of the produced materials in soils. The electro-spun scaffolds were exposed to activated sludge and three different soils for various time periods (0-7-14-21-28-56-180 days); subsequently the degradation was determined by weight loss and microscopical analysis. Although no toxicity occurred in terms of Enchytraeus crypticus reproduction, our data indicate that biodegradation was dependent on the coating of the material and exposure condition. Further, only partial PCL decomposition was possible in sewage treatment plants. Collectively, these data indicate that electro-spun PCL scaffolds are transferred to amended soils.

Preparation and Properties of Electrospun Poly (Vinyl Pyrrolidone)/Cellulose Nanocrystal/Silver Nanoparticle Composite Fibers

PubMed Central

Huang, Siwei; Zhou, Ling; Li, Mei-Chun; Wu, Qinglin; Kojima, Yoichi; Zhou, Dingguo

2016-01-01

Poly (vinyl pyrrolidone) (PVP)/cellulose nanocrystal (CNC)/silver nanoparticle composite fibers were prepared via electrospinning using N,N′-dimethylformamide (DMF) as a solvent. Rheology, morphology, thermal properties, mechanical properties, and antimicrobial activity of nanocomposites were characterized as a function of material composition. The PVP/CNC/Ag electrospun suspensions exhibited higher conductivity and better rheological properties compared with those of the pure PVP solution. The average diameter of the PVP electrospun fibers decreased with the increase in the amount of CNCs and Ag nanoparticles. Thermal stability of electrospun composite fibers was decreased with the addition of CNCs. The CNCs help increase the composite tensile strength, while the elongation at break decreased. The composite fibers included Ag nanoparticles showed improved antimicrobial activity against both the Gram-negative bacterium Escherichia coli (E. coli) and the Gram-positive bacterium Staphylococcus aureus (S. aureus). The enhanced strength and antimicrobial performances of PVP/CNC/Ag electrospun composite fibers make the mat material an attractive candidate for application in the biomedical field. PMID:28773644

Effect of surface topography and bioactive properties on early adhesion and growth behavior of mouse preosteoblast MC3T3-E1 cells.

PubMed

Li, Na; Chen, Gang; Liu, Jue; Xia, Yang; Chen, Hanbang; Tang, Hui; Zhang, Feimin; Gu, Ning

2014-10-08

The effects of bioactive properties and surface topography of biomaterials on the adhesion and spreading properties of mouse preosteoblast MC3T3-E1 cells was investigated by preparation of different surfaces. Poly lactic-co-glycolic acid (PLGA) electrospun fibers (ES) were produced as a porous rough surface. In our study, coverslips were used as a substrate for the immobilization of 3,4-dihydroxyphenylalanine (DOPA) and collagen type I (COL I) in the preparation of bioactive surfaces. In addition, COL I was immobilized onto porous electrospun fibers surfaces (E-COL) to investigate the combined effects of bioactive molecules and topography. Untreated coverslips were used as controls. Early adhesion and growth behavior of MC3T3-E1 cells cultured on the different surfaces were studied at 6, 12, and 24 h. Evaluation of cell adhesion and morphological changes showed that the all the surfaces were favorable for promoting the adhesion and spreading of cells. CCK-8 assays and flow cytometry revealed that both topography and bioactive properties were favorable for cell growth. Analysis of β1, α1, α2, α5, α10 and α11 integrin expression levels by immunofluorescence, real-time RT-PCR, and Western blot and indicated that surface topography plays an important role in the early stage of cell adhesion. However, the influence of topography and bioactive properties of surfaces on integrins is variable. Compared with any of the topographic or bioactive properties in isolation, the combined effect of both types of properties provided an advantage for the growth and spreading of MC3T3-E1 cells. This study provides a new insight into the functions and effects of topographic and bioactive modifications of surfaces at the interface between cells and biomaterials for tissue engineering.

Electro-Responsive Behaviour Multi-Wall Nanotubes/Gelatin Composites and Cross-Linked Gelatin Electrospun Mats

DTIC Science & Technology

2008-02-11

sample , could explain large swelling in blend samples which might enhance ions diffusion and lead to an increase of bending. 21 References [1...1 Final Report on Electro-responsive behaviour multi-wall nanotubes/gelatin composites and cross-linked gelatin electrospun mats...12-10-2007 4. TITLE AND SUBTITLE Electro-responsive behaviour multi-wall nanotubes/gelatin composites and cross-linked gelatin electrospun mats

Recent Advances in Electrospun Nanofiber Interfaces for Biosensing Devices

PubMed Central

Sapountzi, Eleni; Braiek, Mohamed; Chateaux, Jean-François; Lagarde, Florence

2017-01-01

Electrospinning has emerged as a very powerful method combining efficiency, versatility and low cost to elaborate scalable ordered and complex nanofibrous assemblies from a rich variety of polymers. Electrospun nanofibers have demonstrated high potential for a wide spectrum of applications, including drug delivery, tissue engineering, energy conversion and storage, or physical and chemical sensors. The number of works related to biosensing devices integrating electrospun nanofibers has also increased substantially over the last decade. This review provides an overview of the current research activities and new trends in the field. Retaining the bioreceptor functionality is one of the main challenges associated with the production of nanofiber-based biosensing interfaces. The bioreceptors can be immobilized using various strategies, depending on the physical and chemical characteristics of both bioreceptors and nanofiber scaffolds, and on their interfacial interactions. The production of nanobiocomposites constituted by carbon, metal oxide or polymer electrospun nanofibers integrating bioreceptors and conductive nanomaterials (e.g., carbon nanotubes, metal nanoparticles) has been one of the major trends in the last few years. The use of electrospun nanofibers in ELISA-type bioassays, lab-on-a-chip and paper-based point-of-care devices is also highly promising. After a short and general description of electrospinning process, the different strategies to produce electrospun nanofiber biosensing interfaces are discussed. PMID:28813013

Poly(L-lactide)/halloysite nanotube electrospun mats as dual-drug delivery systems and their therapeutic efficacy in infected full-thickness burns.

PubMed

Zhang, Xiazhi; Guo, Rui; Xu, Jiqing; Lan, Yong; Jiao, Yanpeng; Zhou, Changren; Zhao, Yaowu

2015-11-01

In this study, poly(L-lactide) (PLLA)/halloysite nanotube (HNT) electrospun mats were prepared as a dual-drug delivery system. HNTs were used to encapsulate polymyxin B sulphate (a hydrophilic drug). Dexamethasone (a hydrophobic drug) was directly dissolved in the PLLA solution. The drug-loaded HNTs with optimised encapsulation efficiency were then mixed with the PLLA solution for subsequent electrospinning to form composite dual-drug-loaded fibre mats. The structure, morphology, degradability and mechanical properties of the electrospun composite mats were characterised in detail. The results showed that the HNTs were uniformly distributed in the composite PLLA mats. The HNTs content in the mats could change the morphology and average diameter of the electrospun fibres. The HNTs improved both the tensile strength of the PLLA electrospun mats and their degradation ratio. The drug-release kinetics of the electrospun mats were investigated using ultraviolet-visible spectrophotometry. The HNTs/PLLA ratio could be varied to adjust the release of polymyxin B sulphate and dexamethasone. The antibacterial activity in vitro of the mats was evaluated using agar diffusion and turbidimetry tests, which indicated the antibacterial efficacy of the dual-drug delivery system against Gram-positive and -negative bacteria. Healing in vivo of infected full-thickness burns and infected wounds was investigated by macroscopic observation, histological observation and immunohistochemical staining. The results indicated that the electrospun mats were capable of co-loading and co-delivering hydrophilic and hydrophobic drugs, and could potentially be used as novel antibacterial wound dressings. © The Author(s) 2015.

Synthesis of polycaprolactone-titanium oxide multilayer films by nanosecond laser pulses and electrospinning technique for better implant fabrication

NASA Astrophysics Data System (ADS)

Naghshine, Babak B.; Cosman, James A.; Kiani, Amirkianoosh

2016-08-01

In this study, a combination of electrospinning and laser texturing is introduced as a novel method for increasing the biocompatibility of metal implants. Besides having a rough laser treated surface, the implant benefits from the high porosity and better wettability of an electrospun fibrous structure, which is a more favorable environment for cell proliferation. Titanium samples were patterned using a nanosecond laser beam and were placed as collectors in an electrospinning machine. They were then soaked in simulated body fluid for four weeks. Energy Dispersive X-ray and X-Ray Diffraction results indicate significantly more hydroxyapatite formation on laser treated samples with nanoscale fibers deposited on their surface. This shows that having a laser treated surface underneath the fibrous layer can improve short-term biocompatibility even before degradation of fibers. The thermal conductivity of the electrospun layer, measured using a Hot Disk Transient Plane Source instrument and computer code, was shown to be considerably lower than that of titanium and very close to bone. The presence of this layer can therefore be beneficial in making the implant more compatible to a biological medium. In case of dental implants, it was shown that this layer can act as a thermal barrier while a hot beverage is consumed and it can decrease the temperature rise by about 60%, which avoids any possible damage to newly formed cells during the healing period.

Electrospun N-Doped Porous Carbon Nanofibers Incorporated with NiO Nanoparticles as Free-Standing Film Electrodes for High-Performance Supercapacitors and CO2 Capture.

PubMed

Li, Qi; Guo, Jiangna; Xu, Dan; Guo, Jianqiang; Ou, Xu; Hu, Yin; Qi, Haojun; Yan, Feng

2018-04-01

Carbon nanofibers (CNF) with a 1D porous structure offer promising support to encapsulate transition-metal oxides in energy storage/conversion relying on their high specific surface area and pore volume. Here, the preparation of NiO nanoparticle-dispersed electrospun N-doped porous CNF (NiO/PCNF) and as free-standing film electrode for high-performance electrochemical supercapacitors is reported. Polyacrylonitrile and nickel acetylacetone are selected as precursors of CNF and Ni sources, respectively. Dicyandiamide not only improves the specific surface area and pore volume, but also increases the N-doping level of PCNF. Benefiting from the synergistic effect between NiO nanoparticles (NPs) and PCNF, the prepared free-standing NiO/PCNF electrodes show a high specific capacitance of 850 F g -1 at a current density of 1 A g -1 in 6 m KOH aqueous solution, good rate capability, as well as excellent long-term cycling stability. Moreover, NiO NPs dispersed in PCNF and large specific surface area provide many electroactive sites, leading to high CO 2 uptake, and high-efficiency CO 2 electroreduction. The synthesis strategy in this study provides a new insight into the design and fabrication of promising multifunctional materials for high-performance supercapacitors and CO 2 electroreduction. © 2018 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Cell-matrix mechanical interaction in electrospun polymeric scaffolds for tissue engineering: Implications for scaffold design and performance.

PubMed

Kennedy, Kelsey M; Bhaw-Luximon, Archana; Jhurry, Dhanjay

2017-03-01

Engineered scaffolds produced by electrospinning of biodegradable polymers offer a 3D, nanofibrous environment with controllable structural, chemical, and mechanical properties that mimic the extracellular matrix of native tissues and have shown promise for a number of tissue engineering applications. The microscale mechanical interactions between cells and electrospun matrices drive cell behaviors including migration and differentiation that are critical to promote tissue regeneration. Recent developments in understanding these mechanical interactions in electrospun environments are reviewed, with emphasis on how fiber geometry and polymer structure impact on the local mechanical properties of scaffolds, how altering the micromechanics cues cell behaviors, and how, in turn, cellular and extrinsic forces exerted on the matrix mechanically remodel an electrospun scaffold throughout tissue development. Techniques used to measure and visualize these mechanical interactions are described. We provide a critical outlook on technological gaps that must be overcome to advance the ability to design, assess, and manipulate the mechanical environment in electrospun scaffolds toward constructs that may be successfully applied in tissue engineering and regenerative medicine. Tissue engineering requires design of scaffolds that interact with cells to promote tissue development. Electrospinning is a promising technique for fabricating fibrous, biomimetic scaffolds. Effects of electrospun matrix microstructure and biochemical properties on cell behavior have been extensively reviewed previously; here, we consider cell-matrix interaction from a mechanical perspective. Micromechanical properties as a driver of cell behavior has been well established in planar substrates, but more recently, many studies have provided new insights into mechanical interaction in fibrillar, electrospun environments. This review provides readers with an overview of how electrospun scaffold mechanics and cell behavior work in a dynamic feedback loop to drive tissue development, and discusses opportunities for improved design of mechanical environments that are conducive to tissue development. Copyright © 2016 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

Cell infiltration and growth in a low density, uncompressed three-dimensional electrospun nanofibrous scaffold.

PubMed

Blakeney, Bryan A; Tambralli, Ajay; Anderson, Joel M; Andukuri, Adinarayana; Lim, Dong-Jin; Dean, Derrick R; Jun, Ho-Wook

2011-02-01

A limiting factor of traditional electrospinning is that the electrospun scaffolds consist entirely of tightly packed nanofiber layers that only provide a superficial porous structure due to the sheet-like assembly process. This unavoidable characteristic hinders cell infiltration and growth throughout the nanofibrous scaffolds. Numerous strategies have been tried to overcome this challenge, including the incorporation of nanoparticles, using larger microfibers, or removing embedded salt or water-soluble fibers to increase porosity. However, these methods still produce sheet-like nanofibrous scaffolds, failing to create a porous three-dimensional scaffold with good structural integrity. Thus, we have developed a three-dimensional cotton ball-like electrospun scaffold that consists of an accumulation of nanofibers in a low density and uncompressed manner. Instead of a traditional flat-plate collector, a grounded spherical dish and an array of needle-like probes were used to create a Focused, Low density, Uncompressed nanoFiber (FLUF) mesh scaffold. Scanning electron microscopy showed that the cotton ball-like scaffold consisted of electrospun nanofibers with a similar diameter but larger pores and less-dense structure compared to the traditional electrospun scaffolds. In addition, laser confocal microscopy demonstrated an open porosity and loosely packed structure throughout the depth of the cotton ball-like scaffold, contrasting the superficially porous and tightly packed structure of the traditional electrospun scaffold. Cells seeded on the cotton ball-like scaffold infiltrated into the scaffold after 7 days of growth, compared to no penetrating growth for the traditional electrospun scaffold. Quantitative analysis showed approximately a 40% higher growth rate for cells on the cotton ball-like scaffold over a 7 day period, possibly due to the increased space for in-growth within the three-dimensional scaffolds. Overall, this method assembles a nanofibrous scaffold that is more advantageous for highly porous interconnectivity and demonstrates great potential for tackling current challenges of electrospun scaffolds. 2010 Elsevier Ltd. All rights reserved.

Polymer-free nanofibers from vanillin/cyclodextrin inclusion complexes: high thermal stability, enhanced solubility and antioxidant property.

PubMed

Celebioglu, Asli; Kayaci-Senirmak, Fatma; İpek, Semran; Durgun, Engin; Uyar, Tamer

2016-07-13

Vanillin/cyclodextrin inclusion complex nanofibers (vanillin/CD-IC NFs) were successfully obtained from three modified CD types (HPβCD, HPγCD and MβCD) in three different solvent systems (water, DMF and DMAc) via an electrospinning technique without using a carrier polymeric matrix. Vanillin/CD-IC NFs with uniform and bead-free fiber morphology were successfully produced and their free-standing nanofibrous webs were obtained. The polymer-free CD/vanillin-IC-NFs allow us to accomplish a much higher vanillin loading (∼12%, w/w) when compared to electrospun polymeric nanofibers containing CD/vanillin-IC (∼5%, w/w). Vanillin has a volatile nature yet, after electrospinning, a significant amount of vanillin was preserved due to complex formation depending on the CD types. Maximum preservation of vanillin was observed for vanillin/MβCD-IC NFs which is up to ∼85% w/w, besides, a considerable amount of vanillin (∼75% w/w) was also preserved for vanillin/HPβCD-IC NFs and vanillin/HPγCD-IC NFs. Phase solubility studies suggested a 1 : 1 molar complexation tendency between guest vanillin and host CD molecules. Molecular modelling studies and experimental findings revealed that vanillin : CD complexation was strongest for MβCD when compared to HPβCD and HPγCD in vanillin/CD-IC NFs. For vanillin/CD-IC NFs, water solubility and the antioxidant property of vanillin was improved significantly owing to inclusion complexation. In brief, polymer-free vanillin/CD-IC NFs are capable of incorporating a much higher loading of vanillin and effectively preserve volatile vanillin. Hence, encapsulation of volatile active agents such as flavor, fragrance and essential oils in electrospun polymer-free CD-IC NFs may have potential for food related applications by integrating the particularly large surface area of NFs with the non-toxic nature of CD and inclusion complexation benefits, such as high temperature stability, improved water solubility and an enhanced antioxidant property, etc.

Blend-electrospun graphene oxide/Poly(vinylidene fluoride) nanofibrous membranes with high flux, tetracycline removal and anti-fouling properties.

PubMed

Park, Jeong-Ann; Nam, Aram; Kim, Jae-Hyun; Yun, Seong-Taek; Choi, Jae-Woo; Lee, Sang-Hyup

2018-09-01

Graphene oxide (GO)/poly(vinylidene fluoride) (PVDF) electrospun nanofibrous membranes (ENMs) have been fabricated to remove tetracycline (TC) from water via adsorptive-filtration. The pure water permeation flux of GO/PVDF ENMs (27,407-29,337 LMH/bar) was increased compared with that of PVDF ENMs. The flow pore diameter was steadily reduced by increasing the GO content from 0 to 1.5 wt% in the GO/PVDF ENMs. The maximum TC adsorption capacity of GO is 720.26 mg/g (Langmuir model) and GO retained its TC adsorption property after incorporation into GO/PVDF ENMs during water filtration (transmembrane pressure = 0.91 bar). The maximum experimental TC removal capacity (q a , exp ) was 17.92 mg/g with 1.5 wt% of GO (GO 1.5 /PVDF) ENMs, which was similar to the modified dose-response model value of 18.03 mg/g. In the presence of natural organic matter, TC adsorption was enhanced, because hydrophobic organic carbon improved hydrophobic and π-π interactions. The presence of Cu(II) further improved the TC adsorption capacity of GO 1.5 /PVDF ENMs through cation bridging. However, the presence of Ca(II) hindered TC adsorption by an electron shielding effect. For examining anti-fouling activity of GO 1.5 /PVDF ENMs, the log removal values of both bacteria, Escherichia coli and Staphylococcus aureus, were maintained at over 5 during water filtration. In addition, incorporation of GO in PVDF ENMs prevents bovine serum albumin (BSA) adsorption by both increasing the hydrophilicity of the ENMs forming hydration layer on the surface and electrostatic repulsion between both negatively charged BSA and GO in GO 1.5 /PVDF ENMs (zeta potential = - 14.14 mV, deionized water at pH 6). Copyright © 2018 Elsevier Ltd. All rights reserved.

Synthesis of hybrid inorganic/organic nitric oxide-releasing silica nanoparticles for biomedical applications

NASA Astrophysics Data System (ADS)

Carpenter, Alexis Wells

Nitric oxide (NO) is an endogenously produced free radical involved in a number of physiological processes. Thus, much research has focused on developing scaffolds that store and deliver exogenous NO. Herein, the synthesis of N-diazeniumdiolate-modified silica nanoparticles of various physical and chemical properties for biomedical applications is presented. To further develop NO-releasing silica particles for antimicrobial applications, a reverse microemulsion synthesis was designed to achieve nanoparticles of distinct sizes and similar NO release characteristics. Decreasing scaffold size resulted in improved bactericidal activity against Pseudomonas aeruginosa. Confocal microscopy revealed that the improved efficacy resulted from faster particle-bacterium association kinetics. To broaden the therapeutic potential of NO-releasing silica particles, strategies to tune NO release characteristics were evaluated. Initially, surface hydrophobicity and NO release kinetics were tuned by grafting hydrocarbon- and fluorocarbon-based silanes onto the surface of N-diazeniumdiolate-modified particles. The addition of fluorocarbons resulted in a 10x increase in the NO release half-life. The addition of short-chained hydrocarbons to the particle surface increased their stability in hydrophobic electrospun polyurethanes. Although NO release kinetics were longer than that of unmodified particles, durations were still limited to <7 days. An alternative strategy for increasing NO release duration involved directly stabilizing the N-diazeniumdiolate using O2-protecting groups. O2-Methoxymethyl 1-(4-(3-(trimethoxysilyl)propyl))piperazin-1-yl)diazen-1-ium-1,2-diolate (MOM-Pip/NO) was grafted onto mesoporous silica nanoparticles to yield scaffolds with an NO payload of 2.5 μmol NO/mg and an NO release half-life of 23 d. Doping the MOM-Pip/NO-modified particles into resin composites yielded antibacterial NO-releasing dental restorative materials. A 3-log reduction in viable adhered Streptococcus mutans was observed with the MOM-Pip/NO-doped composites compared to undoped controls. The greater chemical flexibility of macromolecular scaffolds is a major advantage over LMW NO donors as it allows for the incorporation of multiple functionalities onto a single scaffold. To demonstrate this advantage, dual functional particles were synthesized by covalently binding quaternary ammonium (QA) functionalities to the surface of NO-releasing silica particles. The QA functionality proved more effective against Staphylococcus aureus than P. aeruginosa, and increasing alkyl chain length correlated with increased efficacy. Nitric oxide-releasing QA-functionalized particles were found to be more effective against S. aureus compared to monofunctional particles.

Electrospun regenerated cellulose nanofibrous membranes surface-grafted with polymer chains/brushes via the atom transfer radical polymerization method for catalase immobilization.

PubMed

Feng, Quan; Hou, Dayin; Zhao, Yong; Xu, Tao; Menkhaus, Todd J; Fong, Hao

2014-12-10

In this study, an electrospun regenerated cellulose (RC) nanofibrous membrane with fiber diameters of ∼200-400 nm was prepared first; subsequently, 2-hydroxyethyl methacrylate (HEMA), 2-dimethylaminoethyl methacrylate (DMAEMA), and acrylic acid (AA) were selected as the monomers for surface grafting of polymer chains/brushes via the atom transfer radical polymerization (ATRP) method. Thereafter, four nanofibrous membranes (i.e., RC, RC-poly(HEMA), RC-poly(DMAEMA), and RC-poly(AA)) were explored as innovative supports for immobilization of an enzyme of bovine liver catalase (CAT). The amount/capacity, activity, stability, and reusability of immobilized catalase were evaluated, and the kinetic parameters (Vmax and Km) for immobilized and free catalase were determined. The results indicated that the respective amounts/capacities of immobilized catalase on RC-poly(HEMA) and RC-poly(DMAEMA) nanofibrous membranes reached 78 ± 3.5 and 67 ± 2.7 mg g(-1), which were considerably higher than the previously reported values. Meanwhile, compared to that of free CAT (i.e., 18 days), the half-life periods of RC-CAT, RC-poly(HEMA)-CAT, RC-poly(DMAEMA)-CAT, and RC-poly(AA)-CAT were 49, 58, 56, and 60 days, respectively, indicating that the storage stability of immobilized catalase was also significantly improved. Furthermore, the immobilized catalase exhibited substantially higher resistance to temperature variation (tested from 5 to 70 °C) and lower degree of sensitivity to pH value (tested from 4.0 and 10.0) than the free catalase. In particular, according to the kinetic parameters of Vmax and Km, the nanofibrous membranes of RC-poly(HEMA) (i.e., 5102 μmol mg(-1) min(-1) and 44.89 mM) and RC-poly(DMAEMA) (i.e., 4651 μmol mg(-1) min(-1) and 46.98 mM) had the most satisfactory biocompatibility with immobilized catalase. It was therefore concluded that the electrospun RC nanofibrous membranes surface-grafted with 3-dimensional nanolayers of polymer chains/brushes would be suitable/ideal as efficient supports for high-density and reusable enzyme immobilization.

Nanoparticles meet electrospinning: recent advances and future prospects.

PubMed

Zhang, Chuan-Ling; Yu, Shu-Hong

2014-07-07

Nanofibres can be fabricated by various methods and perhaps electrospinning is the most facile route. In past years, electrospinning has been used as a synthesis technique and the fibres have been prepared from a variety of starting materials and show various properties. Recently, incorporating functional nanoparticles (NPs) with electrospun fibres has emerged as one of most exciting research topics in the field of electrospinning. When NPs are incorporated, on the one hand the NPs endow the electrospun fibres/mats novel or better performance, on the other hand the electrospun fibres/mats could preserve the NPs from corrosion and/or oxidation, especially for NPs with anisotropic structures. More importantly, electrospinning shows potential applications in self-assembly of nanoscale building blocks for generating new functions, and has some obvious advantages that are not available by other self-assembly methods, i.e., the obtained free-standing hybrid mats are usually flexible and with large area, which is favourable for their commercial applications. In this critical review, we will focus on the fabrication and applications of NPs-electrospun fibre composites and give an overview on this emerging field combining nanoparticles and electrospinning. Firstly, two main strategies for producing NPs-electrospun fibres will be discussed, i.e., one is preparing the NPs-electrospun fibres after electrospinning process that is usually combined with other post-processing methods, and the other is fabricating the composite nanofibres during the electrospinning process. In particular, the NPs in the latter method will be classified and introduced to show the assembling effect of electrospinning on NPs with different anisotropic structures. The subsequent section describes the applications of these NPs-electrospun fibre mats and nanocomposites, and finally a conclusion and perspectives of the future research in this emerging field is given.

Increasing Mechanical Properties of 2-D-Structured Electrospun Nylon 6 Non-Woven Fiber Mats.

PubMed

Xiang, Chunhui; Frey, Margaret W

2016-04-07

Tensile strength, Young's modulus, and toughness of electrospun nylon 6 non-woven fiber mats were improved by increasing individual nanofiber strength and fiber-fiber load sharing. Single-walled carbon nanotubes (CNTs) were used as reinforcement to increase the strength of the electrospun nylon 6 nanofibers. Young's modulus, tensile strength, and toughness of the nylon 6 non-woven fiber mats electrospun from 20 wt % solutions increased 51%, 87%, and 136%, respectively, after incorporating 1 wt % CNTs into the nylon 6 nanofibers. Three methods were investigated to enhance fiber-fiber load sharing: increasing friction between fibers, thermal bonding, and solvent bonding. The addition of beaded nylon 6 nanofibers into the non-woven fiber mats to increase fiber-fiber friction resulted in a statistically significantly increase in Young's modulus over comparable smooth non-woven fiber mats. After annealing, tensile strength, elongation, and toughness of the nylon 6 non-woven fiber mats electrospun from 20 wt % + 10 wt % solutions increased 26%, 28%, and 68% compared to those from 20 wt % solutions. Solvent bonding with formic acid vapor at room temperature for 30 min caused increases of 56%, 67%, and 39% in the Young's modulus, tensile strength, and toughness of non-woven fiber mats, respectively. The increases attributed to increased individual nanofiber strength and solvent bonding synergistically resulted in the improvement of Young's modulus of the electrospun nylon 6 non-woven fiber mats.

Synergetic effect of topological cue and periodic mechanical tension-stress on osteogenic differentiation of rat bone mesenchymal stem cells.

PubMed

Liu, Yao; Yang, Guang; Ji, Huanzhong; Xiang, Tao; Luo, En; Zhou, Shaobing

2017-06-01

Mesenchymal stem cells (MSCs) are able to self-renew and differentiate into tissues of mesenchymal origin, making them to be significant for cell-based therapies, such as metabolic bone diseases and bone repair. Regulating the differentiation of MSCs is significant for bone regeneration. Electrospun fibers mimicking natural extracellular matrix (ECM), is an effective artificial ECM to regulate the behaviors and fates of MSCs. The aligned electrospun fibers can modulate polar cell pattern of bone mesenchymal stem cells, which leads to more obvious osteogenic differentiation. Apart from the topographic effect of electrospun fibers, mechanical cues can also intervene the cell behaviors. In this study, the osteogenic differentiation of rat bone mesenchymal stem cells was evaluated, which were cultured on aligned/random electrospun fiber mats materials under mechanical tension intervention. Scanning electron microscope and immune-fluorescent staining were used to directly observe the polarity changing of cellular morphology and cytoskeleton. The results proved that aligned electrospun fibers could be more conducive to promote osteogenic differentiation of rat bone mesenchymal stem cells and this promotion of osteogenic differentiation was enhanced by tension intervention. These results were correlated to the quantitative real-time PCR assay. In general, culturing rat bone mesenchymal stem cells on electrospun fibers under the intervention of mechanical tension is an effective way to mimic a more real cellular microenvironment. Copyright © 2017 Elsevier B.V. All rights reserved.

Modulation of anisotropy in electrospun tissue-engineering scaffolds: Analysis of fiber alignment by the fast Fourier transform

PubMed Central

Ayres, Chantal; Bowlin, Gary L.; Henderson, Scott C.; Taylor, Leander; Shultz, Jackie; Alexander, John; Telemeco, Todd A.; Simpson, David G.

2010-01-01

We describe the use of the fast Fourier transform (FFT) in the measurement of anisotropy in electrospun scaffolds of gelatin as a function of the starting conditions. In electrospinning, fiber alignment and overall scaffold anisotropy can be manipulated by controlling the motion of the collecting mandrel with respect to the source electrospinning solution. By using FFT to assign relative alignment values to an electrospun matrix it is possible to systematically evaluate how different processing variables impact the structure and material properties of a scaffold. Gelatin was suspended at varying concentrations (80, 100, 130, 150 mg/ml) and electrospun from 2,2,2 trifluoroethanol onto rotating mandrels (200–7000 RPM). At each starting concentration, fiber diameter remained constant over a wide range of mandrel RPM. Scaffold anisotropy developed as a function of fiber diameter and mandrel RPM. The induction of varying degrees of anisotropy imparted distinctive material properties to the electrospun scaffolds. The FFT is a rapid method for evaluating fiber alignment in tissue-engineering materials. PMID:16859744

Controlled surface morphology and hydrophilicity of polycaprolactone toward human retinal pigment epithelium cells.

PubMed

Shahmoradi, Saleheh; Yazdian, Fatemeh; Tabandeh, Fatemeh; Soheili, Zahra-Soheila; Hatamian Zarami, Ashraf Sadat; Navaei-Nigjeh, Mona

2017-04-01

Applying scaffolds as a bed to enhance cell proliferation and even differentiation is one of the treatment of retina diseases such as age-related macular degeneration (AMD) which deteriorating photoreceptors and finally happening blindness. In this study, aligned polycaprolactone (PCL) nanofibers were electrospun and at different conditions and their characteristics were measured by scanning electron microscope (SEM) and contact angle. Response surface methodology (RSM) was used to optimize the diameter of fabricated nanofibers. Two factors as solution concentration and voltage value were considered as independent variables and their effects on nanofibers' diameters were evaluated by central composite design and the optimum conditions were obtained as 0.12g/mL and 20kV, respectively. In order to decrease the hydrophobicity of PCL, the surface of the fabricated scaffolds was modified by alkaline hydrolysis method. Contact time of the scaffolds and alkaline solution and concentration of alkaline solution were optimized using Box Behnken design and (120min and 5M were the optimal, respectively). Contact angle measurement showed the high hydrophilicity of treated scaffolds (with contact angle 7.48°). Plasma surface treatment was applied to compare the effect of using two kinds of surface modification methods simultaneously on hydrolyzed scaffolds. The RPE cells grown on scaffolds were examined by immunocytochemistry (ICC), MTT and continuous inspection of cellular morphology. Interestingly, Human RPE cells revealed their characteristic morphology on hydrolyzed scaffold well. As a result, we introduced a culture substrate with low diameter (185.8nm), high porosity (82%) and suitable hydrophilicity (with contact angle 7.48 degree) which can be promising for hRPE cell transplantation. Copyright © 2016. Published by Elsevier B.V.

Electrospinning Nanofiber Based Organic Solar Cell

NASA Astrophysics Data System (ADS)

Yang, Zhenhua; Liu, Ying; Moffa, Maria; Nam, Chang-Yong; Pisignano, Dario; Rafailovich, Miriam

Bulk heterojunction (BHJ) polymer solar cells are an area of intense interest due to their potential to result in printable, inexpensive solar cells which can be processed onto flexible substrates. The active layer is typically spin coated from the solution of polythiophene derivatives (donor) and fullerenes (acceptor) and interconnected domains are formed because of phase separation. However, the power conversion efficiency (PCE) of BHJ solar cell is restricted by the presence of unfavorable morphological features, including dead ends or isolated domains. Here we MEH-PPV:PVP:PCBM electrospun nanofiber into BHJ solar cell for the active layer morphology optimization. Larger interfacial area between donor and acceptor is abtained with electrospinning method and the high aspect ratio of the MEH-PPV:PVP:PCBM nanofibers allow them to easily form a continuous pathway. The surface morphology is investigated with atomic force microscopy (AFM) and scanning electron microscopy (SEM). Electrospun nanofibers are discussed as a favorable structure for application in bulk-heterojunction organic solar cells. Electrospinning Nanofiber Based Bulk Heterojunction Organic Solar Cell.

Osteogenesis of human adipose-derived stem cells on hydroxyapatite-mineralized poly(lactic acid) nanofiber sheets.

PubMed

Kung, Fu-Chen; Lin, Chi-Chang; Lai, Wen-Fu T

2014-12-01

Electrospun fiber sheets with various orientations (random, partially aligned, and aligned) and smooth and roughened casted membranes were prepared. Hydroxyapatite (HA) crystals were in situ formed on these material surfaces via immersion in 10× simulated body fluid solution. The size and morphology of the resulting fibers were examined using scanning electron microscopy. The average diameter of the fibers ranged from 225±25 to 1050±150 nm depending on the electrospinning parameters. Biological experiment results show that human adipose-derived stem cells exhibit different adhesion and osteogenic differentiation on the three types of fiber. The cell proliferation and osteogenic differentiation were best on the aligned fibers. Similar results were found for phosphorylated focal adhesion kinase expression. Electrospun poly(lactic acid) aligned fibers mineralized with HA crystals provide a good environment for cell growth and osteogenic differentiation and thus have great potential in the tissue engineering field. Copyright © 2014 Elsevier B.V. All rights reserved.

Poly(2-ethyloxazoline) as matrix for highly active electrospun enzymes in organic solvents.

PubMed

Plothe, Ramona; Sittko, Ina; Lanfer, Franziska; Fortmann, Maximilian; Roth, Meike; Kolbach, Vivien; Tiller, Joerg C

2017-01-01

Nanofibers are advantageous carriers for biocatalysts, because they show lower diffusion limitations due to their high surface/volume ratio. Only a few samples are known where enzymes are directly spun into nanofibers, mostly because there are not many suited polymer carriers. In this study, poly(2-ethyloxazoline) (PEtOx) was explored regarding its usefulness to activate various enzymes in organic solvents by directly electrospinning them from aqueous solutions containing the polymer. It was found that the concentration of PEtOx in the spinning solution and also the swellability of the fibers play a great role in the activity of the enzymes in organic solvents. Using electrospun lipase B from Candida antarctica (CaLB) under optimized conditions revealed a higher carrier activity than the commercial Novozyme 435 with 10 times less immobilized protein. The electrospinning of PEtOx/CaLB fibers onto a stirrer is used to realize a biocatalytic stirrer for organic solvents. Biotechnol. Bioeng. 2017;114: 39-45. © 2016 Wiley Periodicals, Inc. © 2016 Wiley Periodicals, Inc.

Laser-treated electrospun fibers loaded with nano-hydroxyapatite for bone tissue engineering.

PubMed

Aragon, Javier; Navascues, Nuria; Mendoza, Gracia; Irusta, Silvia

2017-06-15

Core-shell polycaprolactone/polycaprolactone (PCL/PCL) and polycaprolactone/polyvinyl acetate (PCL/PVAc) electrospun fibers loaded with synthesized nanohydroxyapatite (HAn) were lased treated to create microporosity. The prepared materials were characterized by XRD, FTIR, TEM and SEM. Uniform and randomly oriented beadless fibrous structures were obtained in all cases. Fibers diameters were in the 150-300nm range. Needle-like HAn nanoparticles with mean diameters of 20nm and length of approximately 150nm were mostly encase inside the fibers. Laser treated materials present micropores with diameters in the range 70-120μm for PCL-HAn/PCL fibers and in the 50-90μm range for PCL-HAn/PVAC material. Only samples containing HAn presented bioactivity after incubation during 30days in simulated body fluid. All scaffolds presented high viability, very low mortality, and human osteoblast proliferation. Biocompatibility was increased by laser treatment due to the surface and porosity modification. Copyright © 2017 Elsevier B.V. All rights reserved.

Fabrication and characterization of electrospun gelatin nanofibers crosslinked with oxidized phenolic compounds.

PubMed

Tavassoli-Kafrani, Elham; Goli, Sayed Amir Hossein; Fathi, Milad

2017-10-01

In this study, the ability of oxidized phenolic compounds of tannic, gallic, ferulic and caffeic acids to crosslink gelatin (G) was investigated. The electrospun crosslinked gelatin nanofibers were assessed in terms of gelatin solution properties, fiber morphology, thermal properties, FTIR spectra, XRD pattern and antioxidant activity. Tannic acid showed the most crosslinking activity towards gelatin (13.3 vs 7.44, 4.65, and 3.45% for caffeic, gallic and ferulic, respectively). Crosslinking enhanced roughly electrical conductivity of gelatin solution while the surface tension and viscosity reduced. According to scanning electron microscopy (SEM) results, the fibrous structure of crosslinked gelatin nanofibers didn't change while their diameter increased to the highest value of 280nm for gelatin-tannic. Gelatin-gallic sample showed the highest total phenolic content (86.3mg gallic acid equivalent/g) and antioxidant activity (86.5%). Surprisingly, from differential scanning calorimetry (DSC) curves, it was found that crosslinking led to the reduction of thermal stability of gelatin nanofibers. Copyright © 2017 Elsevier B.V. All rights reserved.

Enhanced Differentiation of Human Preosteoblasts on Electrospun Blend Fiber Mats of Polydioxanone and Anionic Sulfated Polysaccharides

PubMed Central

2017-01-01

The viability and differentiation of SaOS-2 preosteoblasts on fiber mats of blends comprising of the biodegradable poly(ester-ether) polydioxanone (PDX) and the sulfate-containing anionic polysaccharides kappa-carrageenan (KCG) and fucoidan (FUC) were investigated for a range of different blend compositions. The detailed analysis of the blend nanofiber properties revealed a different degree of miscibility of PDX and the polysaccharide leading to a different enrichment at the surface of the blend nanofibers, which were observed to be stable in phosphate buffer solution (PBS) for up to 5 weeks. The fibrous mats of PDX/FUC led to the highest osteogenic differentiation with very good cell viability. The electrospun blend fibers also supported human-induced pluripotent stem (iPS) cells and iPS cell-derived embryoid bodies with high cell viability, which underlines the potential of these novel blend fiber systems for optimized performance in bone tissue engineering applications. PMID:29285521

Preparation and Characterization of Electro-Spun Fabricated Ag-TiO2 Composite Nanofibers and Its Enhanced Photo-Catalytic Activity for the Degradation of Congo Red.

PubMed

Jadhav, Arvind H; Zhang, Hongliang; Agyemang, Frank O; Hiremath, Vishwanath; Lee, Kyuyoung; Chandradass, Jeyaseelan; Seo, Jeong Gil; Kim, Hern

2015-10-01

Electro-spun fabricated TiO2 nanofibers were prepared by simple electro-spinning method, in subsequent step silver (Ag) was deposited using precipitation method and obtained Ag-TiO2 composite nanofibers. The properties and morphology of these prepared composite nanofibers were characterized by XRD, SEM, EDX, and TGA. The prepared electro-spun composite nanofibers were applied as catalyst for the photodegradation of Congo-red under immited solar light in aqueous solution. Result reveals that, Ag loaded TiO2 composite nanofibers were effectively increased photodegradation of Congo red compared with pure TiO2 nanofibers in analogous condition. As a result, 92.0% decomposition of Congo red was obtained by using 5 wt% of Ag loaded TiO2 composite nanofibers at room temperature in short reaction time using 300 W of solar light. In addition, photodegradation of Congo red was also studied under different experimental conditions such as amount of Ag loaded in TiO2 nanofibers and contact time. Moreover, we also studied sintering effect on TiO2 nanofibers and their consequent effect on photodegradation reaction. After completion of reaction, the nanofibers can be easily separated by filtration process and reused several times without significant loss of activity. Overall study reveals that, Ag-TiO2 composite nanofibers were strongly enhanced the surface activity for the photo catalytic degradation of Congo red under ambient condition.

Tuning the Morphology and Activity of Electrospun Polystyrene/UiO-66-NH2 Metal-Organic Framework Composites to Enhance Chemical Warfare Agent Removal.

PubMed

Peterson, Gregory W; Lu, Annie X; Epps, Thomas H

2017-09-20

This work investigates the processing-structure-activity relationships that ultimately facilitate the enhanced performance of UiO-66-NH 2 metal-organic frameworks (MOFs) in electrospun polystyrene (PS) fibers for chemical warfare agent detoxification. Key electrospinning processing parameters including solvent type (dimethylformamide [DMF]) vs DMF/tetrahydrofuran [THF]), PS weight fraction in solution, and MOF weight fraction relative to PS were varied to optimize MOF incorporation into the fibers and ultimately improve composite performance. It was found that composites spun from pure DMF generally resulted in MOF crystal deposition on the surface of the fibers, while composites spun from DMF/THF typically led to MOF crystal deposition within the fibers. For cases in which the MOF was incorporated on the periphery of the fibers, the composites generally demonstrated better gas uptake (e.g., nitrogen, chlorine) because of enhanced access to the MOF pores. Additionally, increasing both the polymer and MOF weight percentages in the electrospun solutions resulted in larger diameter fibers, with polymer concentration having a more pronounced effect on fiber size; however, these larger fibers were generally less efficient at gas separations. Overall, exploring the electrospinning parameter space resulted in composites that outperformed previously reported materials for the detoxification of the chemical warfare agent, soman. The data and strategies herein thus provide guiding principles applicable to the design of future systems for protection and separations as well as a wide range of environmental remediation applications.

Time-Resolved Study of Nanomorphology and Nanomechanic Change of Early-Stage Mineralized Electrospun Poly(lactic acid) Fiber by Scanning Electron Microscopy, Raman Spectroscopy and Atomic Force Microscopy

PubMed Central

Wang, Mengmeng; Cai, Yin; Zhao, Bo; Zhu, Peizhi

2017-01-01

In this study, scanning electron microscopy (SEM), Raman spectroscopy and high-resolution atomic force microscopy (AFM) were used to reveal the early-stage change of nanomorphology and nanomechanical properties of poly(lactic acid) (PLA) fibers in a time-resolved manner during the mineralization process. Electrospun PLA nanofibers were soaked in simulated body fluid (SBF) for different periods of time (0, 1, 3, 5, 7 and 21 days) at 10 °C, much lower than the conventional 37 °C, to simulate the slow biomineralization process. Time-resolved Raman spectroscopy analysis can confirm that apatites were deposited on PLA nanofibers after 21 days of mineralization. However, there is no significant signal change among several Raman spectra before 21 days. SEM images can reveal the mineral deposit on PLA nanofibers during the process of mineralization. In this work, for the first time, time-resolved AFM was used to monitor early-stage nanomorphology and nanomechanical changes of PLA nanofibers. The Surface Roughness and Young’s Modulus of the PLA nanofiber quantitatively increased with the time of mineralization. The electrospun PLA nanofibers with delicate porous structure could mimic the extracellular matrix (ECM) and serve as a model to study the early-stage mineralization. Tested by the mode of PLA nanofibers, we demonstrated that AFM technique could be developed as a potential diagnostic tool to monitor the early onset of pathologic mineralization of soft tissues. PMID:28817096

New poly(ester urea) derived from L-leucine: electrospun scaffolds loaded with antibacterial drugs and enzymes.

PubMed

Díaz, Angélica; del Valle, Luis J; Tugushi, David; Katsarava, Ramaz; Puiggalí, Jordi

2015-01-01

Electrospun scaffolds from an amino acid containing poly(ester urea) (PEU) were developed as promising materials in the biomedical field and specifically in tissue engineering applications. The selected poly(ester urea) was obtained with a high yield and molecular weight by reaction of phosgene with a bis(α-aminoacyl)-α,ω-diol-diester monomer. The polymer having L-leucine, 1,6-hexanediol and carbonic acid units had a semicrystalline character and relatively high glass transition and melting temperatures. Furthermore it was highly soluble in most organic solvents, an interesting feature that facilitated the electrospinning process and the effective incorporation of drugs with bactericidal activity (e.g. biguanide derivatives such as clorhexidine and polyhexamethylenebiguanide) and enzymes (e.g. α-chymotrypsin) that accelerated the degradation process. Continuous micro/nanofibers were obtained under a wide range of processing conditions, being diameters of electrospun fibers dependent on the drug and solvent used. Poly(ester urea) samples were degradable in media containing lipases and proteinases but the degradation rate was highly dependent on the surface area, being specifically greater for scaffolds with respect to films. The high hydrophobicity of new scaffolds had repercussions on enzymatic degradability since different weight loss rates were found depending on how samples were exposed to the medium (e.g. forced or non-forced immersion). New scaffolds were biocompatible, as demonstrated by adhesion and proliferation assays performed with fibroblast and epithelial cells. Copyright © 2014 Elsevier B.V. All rights reserved.

Electrospun collagen-based nanofibres: A sustainable material for improved antibiotic utilisation in tissue engineering applications.

PubMed

Hall Barrientos, Ivan J; Paladino, Eleonora; Szabó, Peter; Brozio, Sarah; Hall, Peter J; Oseghale, Charles I; Passarelli, Melissa K; Moug, Susan J; Black, Richard A; Wilson, Clive G; Zelkó, Romana; Lamprou, Dimitrios A

2017-10-05

For the creation of scaffolds in tissue engineering applications, it is essential to control the physical morphology of fibres and to choose compositions which do not disturb normal physiological function. Collagen, the most abundant protein in the human body, is a well-established biopolymer used in electrospinning compositions. It shows high in-vivo stability and is able to maintain a high biomechanical strength over time. In this study, the effects of collagen type I in polylactic acid-drug electrospun scaffolds for tissue engineering applications are examined. The samples produced were subsequently characterised using a range of techniques. Scanning electron microscopy analysis shows that the fibre morphologies varied across PLA-drug and PLA-collagen-drug samples - the addition of collagen caused a decrease in average fibre diameter by nearly half, and produced nanofibres. Atomic force microscopy imaging revealed collagen-banding patterns which show the successful integration of collagen with PLA. Solid-state characterisation suggested a chemical interaction between PLA and drug compounds, irgasan and levofloxacin, and the collagen increased the amorphous regions within the samples. Surface energy analysis of drug powders showed a higher dispersive surface energy of levofloxacin compared with irgasan, and contact angle goniometry showed an increase in hydrophobicity in PLA-collagen-drug samples. The antibacterial studies showed a high efficacy of resistance against the growth of both E. coli and S. Aureus, except with PLA-collagen-LEVO which showed a regrowth of bacteria after 48h. This can be attributed to the low drug release percentage incorporated into the nanofibre during the in vitro release study. However, the studies did show that collagen helped shift both drugs into sustained release behaviour. These ideal modifications to electrospun scaffolds may prove useful in further research regarding the acceptance of human tissue by inhibiting the potential for bacterial infection. Copyright © 2017 The Authors. Published by Elsevier B.V. All rights reserved.

Tissue factor activity and ECM-related gene expression in human aortic endothelial cells grown on electrospun biohybrid scaffolds.

PubMed

Han, Jingjia; Gerstenhaber, Jonathan A; Lazarovici, Philip; Lelkes, Peter I

2013-05-13

All blood vessels are lined with a quiescent endothelium, which aids in regulating regular blood flow and avoiding thrombus formation. Current attempts at replacing diseased blood vessels frequently fail due to the intrinsic thrombogenicity of the materials used as vascular grafts. In extending our previous work where we introduced a new candidate scaffolds for vascular grafts electrospun from a blend solution of PLGA, gelatin, and elastin (PGE), this study aimed to evaluate the potential of PGE scaffolds to support nonthrombogenic monolayers of primary isolates of human aortic endothelial cells (HAECs), as assessed by a combination of biochemical, molecular, and bioinformatics-based analyses. After 24 h of culture on 3-D fibrous PGE scaffolds, HAECs formed a confluent, nonthrombogenic, and physiologically competent monolayer, as assessed by tissue factor (TF) gene expression and protein activity assays. The levels of TF mRNA/protein activity in HAECs grown on PGE scaffolds were similar to those on gelatin or collagen IV-coated 2-D surfaces. In addition, bioinformatics-based analysis of a focused microarray containing 84 ECM-related cDNA probes demonstrated that HAECs essentially expressed a histotypic ECM-related "transcriptome" on PGE scaffolds, where cells were more quiescent than cells cultured on 2-D coverslips coated with gelatin (a well-known "inert" substrate for conventional EC culture), but less so than on 2-D PGE films. These data suggest an important role for nanorough substrates (PGE films) in passivating endothelial cells and confirm the crucial effect of substrate composition in this process. Principal component analysis of microarray data on the above substrates (including collagen IV) implied that substrate composition plays a greater role than surface topography in affecting the endothelial ECM-related "transcriptome". Taken together, our findings suggest that electrospun PGE scaffolds are potentially suitable for application in small diameter vascular tissue engineering.

Electrospun polycaprolactone/gelatin composites with enhanced cell-matrix interactions as blood vessel endothelial layer scaffolds.

PubMed

Jiang, Yong-Chao; Jiang, Lin; Huang, An; Wang, Xiao-Feng; Li, Qian; Turng, Lih-Sheng

2017-02-01

During the fabrication of tissue engineering scaffolds and subsequent tissue regeneration, surface bioactivity is vital for cell adhesion, spreading, and proliferation, especially for endothelium dysfunction repair. In this paper, synthetic polymer polycaprolactone (PCL) was blended with natural polymer gelatin at four different weight ratios followed by crosslinking (i.e., 100:0, 70:30, 50:50, 30:70, labeled as PCL-C, P7G3-C, P5G5-C, and P3G7-C) to impart enhanced bioactivity and tunable mechanical properties. The PCL/gelatin blends were first dissolved in 2,2,2-trifluroethanol (TFE) and supplementary acetic acid (1% relative to TFE) solvent, electrospun, and then cross-linked to produce PBS-proof fibrous scaffolds. Scanning electron micrographs (SEM) indicated that fibers of each sample were smooth and homogeneous, with the fiber diameters increasing from 1.01±0.51μm to 1.61±0.46μm as the content of gelatin increased. While thermal resistance and crystallization of the blends were affected by the presence of gelatin, as reflected by differential scanning calorimetry (DSC) results, water contact angle (WCA) tests confirmed that the scaffold surfaces became more hydrophilic. Tensile tests showed that PCL-C and P7G3-C scaffolds had mechanical properties comparable to those of human coronary arteries. As for cytocompatibility, skeleton staining images showed that human mesenchymal stem cells (hMSCs) had more favorable binding sites on PCL/gelatin scaffolds than those on PCL scaffolds. Cell proliferation assays revealed that P7G3-C scaffolds could support the most number of hMSCs. The results of this study demonstrated the enhanced cell-matrix interactions and potential use of electrospun PCL/gelatin scaffolds in the tissue engineering field, especially in wound dressings and endothelium regeneration. Copyright © 2016 Elsevier B.V. All rights reserved.

Electrospun Membranes for Environmental Protection

NASA Astrophysics Data System (ADS)

Manea, L. R.; Bertea, A.; Popa, A.; Bertea, A. P.

2018-06-01

Electrospinning is a much-used process for making nano-sized fibres as a result of its simplicity and versatility and of unique mechanical and thermodynamic properties of the obtained nanofibres. Electrospun membranes, which have a porous structure characterized by high uniformity and porosity, find applications in many membrane processes, ranging from membrane distillation to reverse osmosis. The paper reviews electrospun membranes applications in environmental protection, focusing on water and wastewater treatment and air purification. Recent progress and prospects for future development are highlighted.

[Experimental study on long-term prevention effect of chitosan electrospun membrane on cerebrospinal fluid leakage].

PubMed

Guo, Xingfeng; Hou, Chunlin; Dou, Yuandong; Lin, Ye; Lei, Deqiao

2014-08-01

To study the long-term prevention effect of self-developed chitosan electrospun membrane on cerebrospinal fluid leakage. Twenty-five healthy adult New Zealand rabbits were selected to prepare the bilateral dural defect (0.8 cem x 0.8 cm in size) via midline incision of head. Defect of the right was repaired with chitosan electrospun membrane as the experimental group; defect of the left was not repaired as the control group. At 2-16 weeks after operation, one rabbit was sacrificed for the general observation of inflammatory response surrounding bone window and absorption of chitosan electrospun membrane; at 3 and 6 weeks after operation, 5 rabbits were sacrificed for sampling to observe histological change and collagen expression by_HE and Masson staining, and to measure the expressions of epidermal growth factor receptor (EGFR) and basic fibroblast growth factor (bFGF) by immunohistochemical staining. No inflammatory reaction of swelling, exudation, and sppuration appeared in the skin and subcutaneous tissue after operation in 2 groups. There was no adhesion around the chitosan electrospun membrane, and new fiber membrane formed under the chitosan electrospun membrane in the experimental group; no cerebrospinal fluid leakage happened; the chitosan electrospun membrane was gradually degraded with time, and was completely absorbed at 16 weeks. There was uneven scar around the dural detect in control group. Histological observation showed less inflammatory cell infiltration in the experimental group, showing significant difference in the number of inflammatory cells compared with control group at 3, 6 weeks (P < 0.05); capillary, granulation tissue and collagen fiber massively proliferated; collagen fiber arranged in line, and there was a clear borderline between chitosan electrospurn membrane and adjacent collagen fiber. The immunohistochemical staining showed that there were high expressions of bFGF and EGFR in the experimental group, and low expressions of bFGF and EGFR in the control group. Chitosan electrospun membrane for dural defect of rabbit can effectively reconstruct the dura, and it has exact long-term prevention effect on cerebrospinal fluid leakage.

PLLA scaffolds surface-engineered via poly (propylene imine) dendrimers for improvement on its biocompatibility/controlled pH biodegradability

NASA Astrophysics Data System (ADS)

Ganjalinia, Atiyeah.; Akbari, Somaye.; Solouk, Atefeh.

2017-02-01

Novel aminolyzed Poly (L) Lactic Acid (PLLA) films and electrospun nanofibrous scaffolds were fabricated and characterized as potential substrates for tissue engineering. The second generation polypropylene imine dendrimer (PPI-G2) was used as the aminolysis agent to functionalize the inert surface of PLLA substrates directly without any pre-modification process. The effect of the solvent type, G2 concentration, reaction temperature and time were studied by following weight reduction percentage, FTIR and contact angle measurements due to determined optimum conditions. In addition, the modified scaffolds abbreviated by PLLA/G2 were analyzed using mechanical properties, SEM images and dye assays as host-guest modeling. The results indicate that under the 0.5 (wt.%) G2 concentration, ethanol as the solvent, room temperature and 4 h of treatment, the optimum conditions were obtained. It was shown that the hydrophilic properties of PLLA/G2 were greatly enhanced. Also, pH value analysis revealed that after 4 weeks, the biodegradation of PLLA caused massive immune cells infusion and inflammation in the medium through increasing the acidic rate by secretion the lactic acid, whereas the PLLA/G2 scaffolds greatly reduced and stabilize the acidic rate through aminolysis reaction. Finally, promoted cell adhesion and viability underlined the favorable properties of PLLA/G2 scaffolds as a biodegradable biomaterial for biomedical implants.

Desalination by Membrane Distillation using Electrospun Polyamide Fiber Membranes with Surface Fluorination by Chemical Vapor Deposition.

PubMed

Guo, Fei; Servi, Amelia; Liu, Andong; Gleason, Karen K; Rutledge, Gregory C

2015-04-22

Fibrous membranes of poly(trimethyl hexamethylene terephthalamide) (PA6(3)T) were fabricated by electrospinning and rendered hydrophobic by applying a conformal coating of poly(1H,1H,2H,2H-perfluorodecyl acrylate) (PPFDA) using initiated chemical vapor deposition (iCVD). A set of iCVD-treated electrospun PA6(3)T fiber membranes with fiber diameters ranging from 0.25 to 1.8 μm were tested for desalination using the air gap membrane distillation configuration. Permeate fluxes of 2-11 kg/m2/h were observed for temperature differentials of 20-45 °C between the feed stream and condenser plate, with rejections in excess of 99.98%. The liquid entry pressure was observed to increase dramatically, from 15 to 373 kPa with reduction in fiber diameter. Contrary to expectation, for a given feed temperature the permeate flux was observed to increase for membranes of decreasing fiber diameter. The results for permeate flux and salt rejection show that it is possible to construct membranes for membrane distillation even from intrinsically hydrophilic materials after surface modification by iCVD and that the fiber diameter is shown to play an important role on the membrane distillation performance in terms of permeate flux, salt rejection, and liquid entry pressure.

Environment-Modulated Crystallization of Cu2O and CuO Nanowires by Electrospinning and Their Charge Storage Properties.

PubMed

Harilal, Midhun; G Krishnan, Syam; Pal, Bhupender; Reddy, M Venkatashamy; Ab Rahim, Mohd Hasbi; Yusoff, Mashitah Mohd; Jose, Rajan

2018-02-06

This article reports the synthesis of cuprous oxide (Cu 2 O) and cupric oxide (CuO) nanowires by controlling the calcination environment of electrospun polymeric nanowires and their charge storage properties. The Cu 2 O nanowires showed higher surface area (86 m 2 g -1 ) and pore size than the CuO nanowires (36 m 2 g -1 ). Electrochemical analysis was carried out in 6 M KOH, and both the electrodes showed battery-type charge storage mechanism. The electrospun Cu 2 O electrodes delivered high discharge capacity (126 mA h g -1 ) than CuO (72 mA h g -1 ) at a current density of 2.4 mA cm -2 . Electrochemical impedance spectroscopy measurements show almost similar charge-transfer resistance in Cu 2 O (1.2 Ω) and CuO (1.6 Ω); however, Cu 2 O showed an order of magnitude higher ion diffusion. The difference in charge storage between these electrodes is attributed to the difference in surface properties and charge kinetics at the electrode. The electrode also shows superior cyclic stability (98%) and Coulombic efficiency (98%) after 5000 cycles. Therefore, these materials could be acceptable choices as a battery-type or pseudocapacitive electrode in asymmetric supercapacitors.

Tailoring barrier properties of thermoplastic corn starch-based films (TPCS) by means of a multilayer design.

PubMed

Fabra, María José; López-Rubio, Amparo; Cabedo, Luis; Lagaron, Jose M

2016-12-01

This work compares the effect of adding different biopolyester electrospun coatings made of polycaprolactone (PCL), polylactic acid (PLA) and polyhydroxybutyrate (PHB) on oxygen and water vapour barrier properties of a thermoplastic corn starch (TPCS) film. The morphology of the developed multilayer structures was also examined by Scanning Electron Microscopy (SEM). Results showed a positive linear relationship between the amount of the electrospun coatings deposited onto both sides of the TPCS film and the thickness of the coating. Interestingly, the addition of electrospun biopolyester coatings led to an exponential oxygen and water vapour permeability drop as the amount of the electrospun coating increased. This study demonstrated the versatility of the technology here proposed to tailor the barrier properties of food packaging materials according to the final intended use. Copyright © 2016 Elsevier Inc. All rights reserved.

Increasing Mechanical Properties of 2-D-Structured Electrospun Nylon 6 Non-Woven Fiber Mats

PubMed Central

Xiang, Chunhui; Frey, Margaret W.

2016-01-01

Tensile strength, Young’s modulus, and toughness of electrospun nylon 6 non-woven fiber mats were improved by increasing individual nanofiber strength and fiber–fiber load sharing. Single-walled carbon nanotubes (CNTs) were used as reinforcement to increase the strength of the electrospun nylon 6 nanofibers. Young’s modulus, tensile strength, and toughness of the nylon 6 non-woven fiber mats electrospun from 20 wt % solutions increased 51%, 87%, and 136%, respectively, after incorporating 1 wt % CNTs into the nylon 6 nanofibers. Three methods were investigated to enhance fiber–fiber load sharing: increasing friction between fibers, thermal bonding, and solvent bonding. The addition of beaded nylon 6 nanofibers into the non-woven fiber mats to increase fiber-fiber friction resulted in a statistically significantly increase in Young’s modulus over comparable smooth non-woven fiber mats. After annealing, tensile strength, elongation, and toughness of the nylon 6 non-woven fiber mats electrospun from 20 wt % + 10 wt % solutions increased 26%, 28%, and 68% compared to those from 20 wt % solutions. Solvent bonding with formic acid vapor at room temperature for 30 min caused increases of 56%, 67%, and 39% in the Young’s modulus, tensile strength, and toughness of non-woven fiber mats, respectively. The increases attributed to increased individual nanofiber strength and solvent bonding synergistically resulted in the improvement of Young’s modulus of the electrospun nylon 6 non-woven fiber mats. PMID:28773397

Synthesis of polycaprolactone-titanium oxide multilayer films by nanosecond laser pulses and electrospinning technique for better implant fabrication

DOE Office of Scientific and Technical Information (OSTI.GOV)

Naghshine, Babak B.; Cosman, James A.; Kiani, Amirkianoosh, E-mail: a.kiani@unb.ca

In this study, a combination of electrospinning and laser texturing is introduced as a novel method for increasing the biocompatibility of metal implants. Besides having a rough laser treated surface, the implant benefits from the high porosity and better wettability of an electrospun fibrous structure, which is a more favorable environment for cell proliferation. Titanium samples were patterned using a nanosecond laser beam and were placed as collectors in an electrospinning machine. They were then soaked in simulated body fluid for four weeks. Energy Dispersive X-ray and X-Ray Diffraction results indicate significantly more hydroxyapatite formation on laser treated samples withmore » nanoscale fibers deposited on their surface. This shows that having a laser treated surface underneath the fibrous layer can improve short-term biocompatibility even before degradation of fibers. The thermal conductivity of the electrospun layer, measured using a Hot Disk Transient Plane Source instrument and computer code, was shown to be considerably lower than that of titanium and very close to bone. The presence of this layer can therefore be beneficial in making the implant more compatible to a biological medium. In case of dental implants, it was shown that this layer can act as a thermal barrier while a hot beverage is consumed and it can decrease the temperature rise by about 60%, which avoids any possible damage to newly formed cells during the healing period.« less

In-situ synthesis of magnetic iron-oxide nanoparticle-nanofibre composites using electrospinning.

PubMed

Burke, Luke; Mortimer, Chris J; Curtis, Daniel J; Lewis, Aled R; Williams, Rhodri; Hawkins, Karl; Maffeis, Thierry G G; Wright, Chris J

2017-01-01

We demonstrate a facile, one-step process to form polymer scaffolds composed of magnetic iron oxide nanoparticles (MNPs) contained within electrospun nano- and micro-fibres of two biocompatible polymers, Poly(ethylene oxide) (PEO) and Poly(vinyl pyrrolidone) (PVP). This was achieved with both needle and free-surface electrospinning systems demonstrating the scalability of the composite fibre manufacture; a 228 fold increase in fibre fabrication was observed for the free-surface system. In all cases the nanoparticle-nanofibre composite scaffolds displayed morphological properties as good as or better than those previously described and fabricated using complex multi-stage techniques. Fibres produced had an average diameter (Needle-spun: 125±18nm (PEO) and 1.58±0.28μm (PVP); Free-surface electrospun: 155±31nm (PEO)) similar to that reported previously, were smooth with no bead defects. Nanoparticle-nanofibre composites were characterised using scanning electron microscopy (SEM), energy dispersive X-ray spectroscopy (EDX), dynamic light scattering (DLS) (Nanoparticle average diameter ranging from 8±3nm to 27±5nm), XRD (Phase of iron oxide nanoparticles identified as magnetite) and nuclear magnetic resonance relaxation measurements (NMR) (T1/T2: 32.44 for PEO fibres containing MNPs) were used to verify the magnetic behaviour of MNPs. This study represents a significant step forward for production rates of magnetic nanoparticle-nanofibre composite scaffolds by the electrospinning technique. Copyright © 2016 Elsevier B.V. All rights reserved.

Protein valves prepared by click reaction grafting of poly(N-isopropylacrylamide) to electrospun poly(vinyl chloride) fibrous membranes

NASA Astrophysics Data System (ADS)

Guo, Jian-Wei; Lin, Zhen-Yu; Chang, Chi-Jung; Lu, Chien-Hsing; Chen, Jem-Kun

2018-05-01

In this study, poly(vinyl chloride) (PVC) was electrospun into fibrous membranes and then reacted with NaN3 to generate azido-terminated PVC fibrous membranes. A propargyl-terminated poly(N-isopropylacrylamide) (PNIPAAm) was also synthesized and then grafted, through click reactions, onto the azido-terminated PVC fiber surface. Protrusion-, scale-, and joint-like structures of the PNIPAAm grafts on the PVC fibers were formed upon increasing the molecular weight of the PNIPAAm grafts. The PNIPAAm-grafted PVC fibrous mats exhibited completely wetted surfaces at 25 °C because of their high roughness. The static water contact angle of the PNIPAAm-grafted PVC fibrous mats reached 140° when the temperature was increased to 45 °C. This thermoresponsive behavior was significantly greater than that of the PNIPAAm grafted on a flat surface. Temperature-responsive membranes were constructed having a pore size of 1.38 μm and applied as protein valves to block and release an antibody (fluorescein-conjugated AffiniPure goat anti-rabbit IgG). At 25 °C, the collection efficiency remained at 94% for antibody concentrations up to 60 ng/L. As the temperature increased to 45 °C, the collection efficiency decreased abruptly, to 4%, when the antibody concentration was greater than 20 ng/L. Accordingly, this system of PNIPAAm-grafted PVC fibers functioned as a protein valve allowing the capture and concentration of proteins.

Drug-loaded electrospun mats of poly(vinyl alcohol) fibres and their release characteristics of four model drugs

NASA Astrophysics Data System (ADS)

Taepaiboon, Pattama; Rungsardthong, Uracha; Supaphol, Pitt

2006-05-01

Mats of PVA nanofibres were successfully prepared by the electrospinning process and were developed as carriers of drugs for a transdermal drug delivery system. Four types of non-steroidal anti-inflammatory drug with varying water solubility property, i.e. sodium salicylate (freely soluble in water), diclofenac sodium (sparingly soluble in water), naproxen (NAP), and indomethacin (IND) (both insoluble in water), were selected as model drugs. The morphological appearance of the drug-loaded electrospun PVA mats depended on the nature of the model drugs. The 1H-nuclear magnetic resonance results confirmed that the electrospinning process did not affect the chemical integrity of the drugs. Thermal properties of the drug-loaded electrospun PVA mats were analysed by differential scanning calorimetry and thermogravimetric analysis. The molecular weight of the model drugs played a major role on both the rate and the total amount of drugs released from the as-prepared drug-loaded electrospun PVA mats, with the rate and the total amount of the drugs released decreasing with increasing molecular weight of the drugs. Lastly, the drug-loaded electrospun PVA mats exhibited much better release characteristics of the model drugs than drug-loaded as-cast films.

Emulsion Electrospinning as an Approach to Fabricate PLGA/Chitosan Nanofibers for Biomedical Applications

PubMed Central

Tavanai, Hossein; Hilborn, Jöns; Donzel-Gargand, Olivier; Leifer, Klaus; Arpanaei, Ayyoob

2014-01-01

Novel nanofibers from blends of polylactic-co-glycolic acid (PLGA) and chitosan have been produced through an emulsion electrospinning process. The spinning solution employed polyvinyl alcohol (PVA) as the emulsifier. PVA was extracted from the electrospun nanofibers, resulting in a final scaffold consisting of a blend of PLGA and chitosan. The fraction of chitosan in the final electrospun mat was adjusted from 0 to 33%. Analyses by scanning and transmission electron microscopy show uniform nanofibers with homogenous distribution of PLGA and chitosan in their cross section. Infrared spectroscopy verifies that electrospun mats contain both PLGA and chitosan. Moreover, contact angle measurements show that the electrospun PLGA/chitosan mats are more hydrophilic than electrospun mats of pure PLGA. Tensile strengths of 4.94 MPa and 4.21 MPa for PLGA/chitosan in dry and wet conditions, respectively, illustrate that the polyblend mats of PLGA/chitosan are strong enough for many biomedical applications. Cell culture studies suggest that PLGA/chitosan nanofibers promote fibroblast attachment and proliferation compared to PLGA membranes. It can be assumed that the nanofibrous composite scaffold of PLGA/chitosan could be potentially used for skin tissue reconstruction. PMID:24689041

Preparation and characterization of hydrophobic P(TFE) blend electrospun gel polymer electrolyte fibrous membranes for Li-O2 battery

NASA Astrophysics Data System (ADS)

Padmaraj, O.; Suthanthiraraj, S. Austin

2018-04-01

A novel stable electrospun gel polymer electrolyte [(100-x)% P(VdF-co-HFP)+(x)% P(TFE), (x = 5, 10, 15, 20, 25 & 30)/1 M Li(CF3SO2)2N-] fibrous membranes with an addition of various concentrations of hydrophobic P(TFE) polymer were prepared by an electrospinning technique. All the prepared electrospun polymer blend fibrous membranes were characterized by X-ray diffraction, Fourier transform infrared spectroscopy, differential scanning calorimetry, high resolution scanning electron microscopy techniques and water contact angle measurements. The newly developed electrospun pure and hydrophobic P(TFE) blend fibrous membranes were activated into separator-cum gel polymer electrolyte fibrous membranes by soaking in an electrolyte solution contains 1 M Li(CF3SO2)2N- in EC: PC (1:1, v/v) in an argon filled glove box. Among the various concentrations of hydrophobic P(TFE) blend polymer fibrous membranes, the electrospun gel polymer blend electrolyte with 5% P(TFE) showed low crystallinity, high thermal stability, high electrolyte uptake, good hydrophobicity and high ionic conductivity (2.680×10-2 S cm-1) at room temperature.

Electrospun Fibers as a Dressing Material for Drug and Biological Agent Delivery in Wound Healing Applications

PubMed Central

Gizaw, Mulugeta; Thompson, Jeffrey; Faglie, Addison; Lee, Shih-Yu; Neuenschwander, Pierre; Chou, Shih-Feng

2018-01-01

Wound healing is a complex tissue regeneration process that promotes the growth of new tissue to provide the body with the necessary barrier from the outside environment. In the class of non-healing wounds, diabetic wounds, and ulcers, dressing materials that are available clinically (e.g., gels and creams) have demonstrated only a slow improvement with current available technologies. Among all available current technologies, electrospun fibers exhibit several characteristics that may provide novel replacement dressing materials for the above-mentioned wounds. Therefore, in this review, we focus on recent achievements in electrospun drug-eluting fibers for wound healing applications. In particular, we review drug release, including small molecule drugs, proteins and peptides, and gene vectors from electrospun fibers with respect to wound healing. Furthermore, we provide an overview on multifunctional dressing materials based on electrospun fibers, including those that are capable of achieving wound debridement and wound healing simultaneously as well as multi-drugs loading/types suitable for various stages of the healing process. Our review provides important and sufficient information to inform the field in development of fiber-based dressing materials for clinical treatment of non-healing wounds. PMID:29382065

Electrospun Polymer Nanofibers Decorated with Noble Metal Nanoparticles for Chemical Sensing.

PubMed

Chen, Chen; Tang, Yongan; Vlahovic, Branislav; Yan, Fei

2017-12-01

The integration of different noble metal nanostructures, which exhibit desirable plasmonic and/or electrocatalytic properties, with electrospun polymer nanofibers, which display unique mechanical and thermodynamic properties, yields novel hybrid nanoscale systems of synergistic properties and functions. This review summarizes recent advances on how to incorporate noble metal nanoparticles into electrospun polymer nanofibers and illustrates how such integration paves the way towards chemical sensing applications with improved sensitivity, stability, flexibility, compatibility, and selectivity. It is expected that further development of this field will eventually make a wide impact on many areas of research.

Electrospun Polyurethane-Core and Gelatin-Shell Coaxial Fibre Coatings for Miniature Implantable Biosensors

PubMed Central

Wang, Ning; Burugapalli, Krishna; Wijesuriya, Shavini; Far, Mahshid Yazdi; Song, Wenhui; Moussy, Francis; Zheng, Yudong; Ma, Yanxuan; Wu, Zhentao; Li, Kang

2014-01-01

The aim of this study was to introduce bioactivity to the electrospun coating for implantable glucose biosensors. Coaxial fibre membranes having polyurethane as the core and gelatin as the shell were produced using a range of polyurethane concentrations (2, 4, 6 & 8% wt/v) while keeping gelatin concentration (10% wt/v) constant in 2,2,2-trifluoroethanol. The gelatin shell was stabilized using glutaraldehyde vapour. The formation of core-shell structure was confirmed using TEM, SEM and FTIR. The coaxial fibre membranes showed uniaxial tensile properties intermediate to that of the pure polyurethane and the gelatin fibre membranes. The gelatin shell increased hydrophilicity and glucose transport flux across the coaxial fibre membranes. The coaxial fibre membranes having small fibre diameter (541 nm) and a thick gelatin shell (52%) did not affect the sensor sensitivity, but decreased sensor’s linearity in the long run. In contrast, thicker coaxial fibre membranes (1133 nm) having a thin gelatin shell (34%) maintained both sensitivity and linearity till 84 days of the study period. To conclude, polyurethane-gelatin co-axial fibre membranes, due to their faster permeability to glucose, tailorable mechanical properties and bioactivity are potential candidates for coatings to favourably modify the host responses to extend the reliable in vivo lifetime of implantable glucose biosensors. PMID:24346001

ELECTROSPUN MESOFIBERS, A NOVEL BIODEGRADABLE PHEROMONE DISPENSER TECHNOLOGY, ARE COMBINED WITH MECHANICAL DEPLOYMENT FOR EFFICIENT IPM OF LOBESIA BOTRANA IN VINEYARDS.

PubMed

Hummel, Hans E; Langner, S S; Breuer, M

2015-01-01

Behaviour modifying pheromones are well known agents for disrupting mating communication of pest insects. For optimal activity, they must be dispensed in time and space at a quantitatively measurable, predetermined release rate covering the flight period of the target species. Pheromones appeal to environmentally conscientious entomologists for their biodegradability, non-toxicity and ecological compatibility. In attempts of combining the virtues of pheromones, suitable slow release dispensers, and their mechanical deployment, an ecologically sensible, reasonably priced and patented procedure was developed and tested with the vineyard pest Lobesia botrana (Lep.: Tortricidae). It is characterized by (1) Electrospun mesofibers with diameters ranging from 0.6 to 3.5 micrometres, containing disruptants and dispensing it by slow release diffusion into the crop, (2) simultaneous application of the fully biodegradable combination of pheromone with Ecoflex polyester mesofiber, (3) combination of mechanical deployment by multi-purpose cultivators of the prefabricated pheromone dispensers with other simultaneous cultivation measures, and thus further reducing labour time and treatment costs. The dispensers are biodegradable within half a year without leaving any objectionable residues. In the standard eco-toxicology tests pheromone dispensers are harmless to non-target organisms. The disruptive effect of one treatment lasts for seven weeks which covers well one of several flight periods of L. botrana.

Compliant electrospun silk fibroin tubes for small vessel bypass grafting.

PubMed

Marelli, Benedetto; Alessandrino, Antonio; Farè, Silvia; Freddi, Giuliano; Mantovani, Diego; Tanzi, Maria Cristina

2010-10-01

Processing silk fibroin (SF) by electrospinning offers a very attractive opportunity for producing three-dimensional nanofibrillar matrices in tubular form, which may be useful for a biomimetic approach to small calibre vessel regeneration. Bypass grafting of small calibre vessels, with a diameter less than 6mm, is performed mainly using autografts, like the saphenous vein or internal mammary artery. At present no polymeric grafts made of SF are commercially available, mainly due to inadequate properties (low compliance and lack of endothelium cells). The aim of this work was to electrospin SF into tubular structures (Ø=6mm) for small calibre vessel grafting, characterize the morphological, chemico-physical and mechanical properties of the electrospun SF structures and to validate their potential to interact with cells. The morphological properties of electrospun SF nanofibres were investigated by scanning electron microscopy. Chemico-physical analyses revealed an increase in the crystallinity of the structure of SF nanofibres on methanol treatment. Mechanical tests, i.e. compliance and burst pressure measurements, of the electrospun SF tubes showed that the inner pressure to radial deformation ratio was linear for elongation up to 15% and pressure up to 400 mm Hg. The mean compliance value between 80 and 120 mm Hg was higher than the values reported for both Goretex(R) and Dacron(R) grafts and for bovine heterografts, but still slightly lower than those of saphenous and umbilical vein, which nowadays represent the gold standard for the replacement of small calibre arteries. The electrospun tubes resisted up to 575+/-17 mmHg, which is more than four times the upper physiological pressure of 120 mmHg and more than twice the pathological upper pressures (range 180-220 mmHg). The in vitro tests showed a good cytocompatibility of the electrospun SF tubes. Therefore, the electrospun SF tubes developed within this work represent a suitable candidate for small calibre blood vessel replacement. 2010 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

Strong size-dependent stress relaxation in electrospun polymer nanofibers

NASA Astrophysics Data System (ADS)

Wingert, Matthew C.; Jiang, Zhang; Chen, Renkun; Cai, Shengqiang

2017-01-01

Electrospun polymer nanofibers have garnered significant interest due to their strong size-dependent material properties, such as tensile moduli, strength, toughness, and glass transition temperatures. These properties are closely correlated with polymer chain dynamics. In most applications, polymers usually exhibit viscoelastic behaviors such as stress relaxation and creep, which are also determined by the motion of polymer chains. However, the size-dependent viscoelasticity has not been studied previously in polymer nanofibers. Here, we report the first experimental evidence of significant size-dependent stress relaxation in electrospun Nylon-11 nanofibers as well as size-dependent viscosity of the confined amorphous regions. In conjunction with the dramatically increasing stiffness of nano-scaled fibers, this strong relaxation enables size-tunable properties which break the traditional damping-stiffness tradeoff, qualifying electrospun nanofibers as a promising set of size-tunable materials with an unusual and highly desirable combination of simultaneously high stiffness and large mechanical energy dissipation.

Smart Electrospun Nanofibers for Controlled Drug Release: Recent Advances and New Perspectives

PubMed Central

Weng, Lin; Xie, Jingwei

2017-01-01

In biological systems, chemical molecules or ions often release upon certain conditions, at a specific location, and over a desired period of time. Electrospun nanofibers that undergo alterations in the physicochemical characteristics corresponding to environmental changes have gained considerable interest for various applications. Inspired by biological systems, therapeutic molecules have been integrated with these smart electrospun nanofibers, presenting activation-modulated or feedback-regulated control of drug release. Compared to other materials like smart hydrogels, environment-responsive nanofiber-based drug delivery systems are relatively new but possess incomparable advantages due to their greater permeability, which allows shorter response time and more precise control over the release rate. In this article, we review the mechanisms of various environmental parameters functioning as stimuli to tailor the release rates of smart electrospun nanofibers. We also illustrate several typical examples in specific applications. We conclude this article with a discussion on perspectives and future possibilities in this field. PMID:25732665

Electrospinning: An enabling nanotechnology platform for drug delivery and regenerative medicine.

PubMed

Chen, Shixuan; Li, Ruiquan; Li, Xiaoran; Xie, Jingwei

2018-05-02

Electrospinning provides an enabling nanotechnology platform for generating a rich variety of novel structured materials in many biomedical applications including drug delivery, biosensing, tissue engineering, and regenerative medicine. In this review article, we begin with a thorough discussion on the method of producing 1D, 2D, and 3D electrospun nanofiber materials. In particular, we emphasize on how the 3D printing technology can contribute to the improvement of traditional electrospinning technology for the fabrication of 3D electrospun nanofiber materials as drug delivery devices/implants, scaffolds or living tissue constructs. We then highlight several notable examples of electrospun nanofiber materials in specific biomedical applications including cancer therapy, guiding cellular responses, engineering in vitro 3D tissue models, and tissue regeneration. Finally, we finish with conclusions and future perspectives of electrospun nanofiber materials for drug delivery and regenerative medicine. Copyright © 2018 Elsevier B.V. All rights reserved.

Smart electrospun nanofibers for controlled drug release: recent advances and new perspectives.

PubMed

Weng, Lin; Xie, Jingwei

2015-01-01

In biological systems, chemical molecules or ions often release upon certain conditions, at a specific location, and over a desired period of time. Electrospun nanofibers that undergo alterations in the physicochemical characteristics corresponding to environmental changes have gained considerable interest for various applications. Inspired by biological systems, therapeutic molecules have been integrated with these smart electrospun nanofibers, presenting activation-modulated or feedback-regulated control of drug release. Compared to other materials like smart hydrogels, environment-responsive nanofiber-based drug delivery systems are relatively new but possess incomparable advantages due to their greater permeability, which allows shorter response time and more precise control over the release rate. In this article, we review the mechanisms of various environmental parameters functioning as stimuli to tailor the release rates of smart electrospun nanofibers. We also illustrate several typical examples in specific applications. We conclude this article with a discussion on perspectives and future possibilities in this field.

Strong size-dependent stress relaxation in electrospun polymer nanofibers

DOE PAGES

Wingert, Matthew C.; Jiang, Zhang; Chen, Renkun; ...

2017-01-04

Here, electrospun polymer nanofibers have garnered significant interest due to their strong size-dependent material properties, such as tensile moduli, strength, toughness, and glass transition temperatures. These properties are closely correlated with polymer chain dynamics. In most applications, polymers usually exhibit viscoelastic behaviors such as stress relaxation and creep, which are also determined by the motion of polymer chains. However, the size-dependent viscoelasticity has not been studied previously in polymer nanofibers. Here, we report the first experimental evidence of significant size-dependent stress relaxation in electrospun Nylon-11 nanofibers as well as size-dependent viscosity of the confined amorphous regions. In conjunction with themore » dramatically increasing stiffness of nano-scaled fibers, this strong relaxation enables size-tunable properties which break the traditional damping-stiffness tradeoff, qualifying electrospun nanofibers as a promising set of size-tunable materials with an unusual and highly desirable combination of simultaneously high stiffness and large mechanical energy dissipation.« less

Bactericidal Activity of Usnic Acid-Loaded Electrospun Fibers.

PubMed

Araújo, Evando S; Pereira, Eugênia C; da Costa, Mateus M; da Silva, Nicácio H; de Oliveira, Helinando P

2016-01-01

Usnic acid has been progressively reported in the literature as one of the most important lichen metabolites characterized by a rich diversity of applications such as antifungal, antimicrobial, antiprotozoal and antiviral agent. Particularly, antimicrobial activity of usnic acid can be improved by encapsulation of active molecules in enteric electrospun fibers, allowing the controlled release of active molecule at specific pH. Few relevant patents to the topic have been reviewed and cited. Bactericidal activity of usnic acid-loaded electrospun fibers of Eudragit L-100 and polyvinylpyrrolidone was examined against Staphylococcus aureus using inhibition hales methodology. The controlled release of active material at high pH is established after 10 minutes of interaction with media and results in reasonable activity against S. aureus, as detected by inhibition hales. The strong biological activity of usnic acid-loaded electrospun fibers provides a promising application for corresponding material as a bactericidal agent for wound healing treatment.

Developing and physicochemical evaluation of cross-linked electrospun gelatin-glycerol nanofibrous membranes for medical applications

NASA Astrophysics Data System (ADS)

Morsy, Reda; Hosny, Marwa; Reicha, Fikry; Elnimr, Tarek

2017-05-01

This study aims to develop optimal cross-linked electrospun gelatin-glycerol (GEL-GLY) nano-fibrous mats suitable for tissue engineering and wound dressing applications. The optimized procedure involves heating the gelatin and gelatin-glycerol solutions up to 90 °C. The electrospinning process was performed, followed by further cross-linking of electrospun films in a container containing glutaraldehyde (GTA) vapor. The results of X-ray diffraction (XRD), Fourier transformed infrared (FTIR), and Differential thermal analysis (DTA) confirmed that heating gelatin solution up to 90 °C in the presence of glycerol affected the cross-linking efficiency and interactions between GTA molecules and gelatin chains. Scanning Electron Microscope (SEM) analysis showed that GEL-GLY nano-fibrous mats with weight ratios less than or equal (12:3 w/w) exhibited a regular morphology with defect free in addition to increasing the degradation time, cross-linking efficiency, and swelling degree of electrospun gelatin/glycerol.

Electrospun polymeric dressings functionalized with antimicrobial peptides and collagen type I for enhanced wound healing

NASA Astrophysics Data System (ADS)

Felgueiras, H. P.; Amorim, M. T. P.

2017-10-01

Modern wound dressings combine medical textiles with active compounds that stimulate wound healing while protecting against infection. Electrospun wound dressings have been extensively studied and the electrospinning technique recognized as an efficient approach for the production of nanoscale fibrous mats. The unique diverse function and architecture of antimicrobial peptides (AMPs) has attracted considerable attention as a tool for the design of new anti-infective drugs. Functionalizing electrospun wound dressings with these AMPs is nowadays being researched. In the present work, we explore these new systems by highlighting the most important characteristics of electropsun wound dressings, revealing the importance of AMPs to wound healing, and the methods available to functionalize the electrospun mats with these molecules. The combined therapeutic potential of collagen type I and these AMP functionalized dressings will be highlighted as well; the significance of these new strategies for the future of wound healing will be clarified.

NiO Nanofibers as a Candidate for a Nanophotocathode

PubMed Central

Macdonald, Thomas J.; Xu, Jie; Elmas, Sait; Mange, Yatin J.; Skinner, William M.; Xu, Haolan; Nann, Thomas

2014-01-01

p-type NiO nanofibers have been synthesized from a simple electrospinning and sintering procedure. For the first time, p-type nanofibers have been electrospun onto a conductive fluorine doped tin oxide (FTO) surface. The properties of the NiO nanofibers have been directly compared to that of bulk NiO nanopowder. We have observed a p-type photocurrent for a NiO photocathode fabricated on an FTO substrate. PMID:28344222

Electrospun PVA/HAp nanocomposite nanofibers: biomimetics of mineralized hard tissues at a lower level of complexity.

PubMed

Kim, Gyeong-Man; Asran, Ashraf Sh; Michler, Georg H; Simon, Paul; Kim, Jeong-Sook

2008-12-01

Based on the biomimetic approaches the present work describes a straightforward technique to mimic not only the architecture (the morphology) but also the chemistry (the composition) of the lowest level of the hierarchical organization of bone. This technique uses an electrospinning (ES) process with polyvinyl alcohol (PVA) and hydroxyapatite (HAp) nanoparticles. To determine morphology, crystalline structures and thermal properties of the resulting electrospun fibers with the pure PVA and PVA/HAp nanocomposite (NC) before electrospinning various techniques were employed, including transmission electron microscopy (TEM), high-resolution TEM (HR-TEM), scanning electron microscopy (SEM), x-ray diffraction (XRD), differential scanning calorimetry (DSC) and thermogravimetric analysis (TGA). In addition, FT-IR spectroscopy was carried out to analyze the complex structural changes upon undergoing electrospinning as well as interactions between HAp and PVA. The morphological and crystallographic investigations revealed that the rod-like HAp nanoparticles exhibit a nanoporous morphology and are embedded within the electrospun fibers. A large number of HAp nanorods are preferentially oriented parallel to the longitudinal direction of the electrospun PVA fibers, which closely resemble the naturally mineralized hard tissues of bones. Due to abundant OH groups present in PVA and HAp nanorods, they strongly interact via hydrogen bonding within the electrospun PVA/HAp NC fibers, which results in improved thermal properties. The unique physiochemical features of the electrospun PVA/HAp NC nanofibers prepared by the ES process will open up a wide variety of future applications related to hard tissue replacement and regeneration (bone and dentin), not limited to coating implants.

Improved conversion efficiency in dye-sensitized solar cells based on electrospun Al-doped ZnO nanofiber electrodes prepared by seed layer treatment

DOE Office of Scientific and Technical Information (OSTI.GOV)

Yun Sining, E-mail: alexsyun1974@yahoo.com.c; Lim, Sangwoo

2011-02-15

The application of electrospun nanofibers in electronic devices is limited due to their poor adhesion to conductive substrates. To improve this, a seed layer (SD) is introduced on the FTO substrate before the deposition of the electrospun composite nanofibers. This facilitates the release of interfacial tensile stress during calcination and enhances the interfacial adhesion of the AZO nanofiber films with the FTO substrate. Dye-sensitized solar cells (DSSC) based on these AZO nanofiber photoelectrodes have been fabricated and investigated. An energy conversion efficiency ({eta}) of 0.54-0.55% has been obtained under irradiation of AM 1.5 simulated sunlight (100 mW/cm{sup 2}), indicating amore » massive improvement of {eta} in the AZO nanofiber film DSSCs after SD-treatment of the FTO substrate as compared to those with no treatment. The SD-treatment has been demonstrated to be a simple and facile method to solve the problem of poor adhesion between electrospun nanofibers and the conductive substrate. -- Graphical abstract: The poor adhesion between electrospun nanofibers and substrate is improved by a simple and facile seed layer (SD) treatment. The energy conversion efficiency of AZO nanofiber-based DSSCs has been greatly increased by SD-treatment of the FTO substrate. Display Omitted Research highlights: {yields} A simple and facile method (SD-treatment) has been demonstrated. {yields} The poor adhesion between electrospun nanofibers and substrate is improved by the SD-treatment. {yields} The {eta} of AZO nanofiber-based DSSCs has been greatly improved by SD-treatment of the FTO substrate.« less

Polymer-based protein engineering grown ferrocene-containing redox polymers improve current generation in an enzymatic biofuel cell.

PubMed

Campbell, Alan S; Murata, Hironobu; Carmali, Sheiliza; Matyjaszewski, Krzysztof; Islam, Mohammad F; Russell, Alan J

2016-12-15

Enzymatic biofuel cells (EBFCs) are capable of generating electricity from physiologically present fuels making them promising power sources for the future of implantable devices. The potential application of such systems is limited, however, by inefficient current generation. Polymer-based protein engineering (PBPE) offers a unique method to tailor enzyme function through tunable modification of the enzyme surface with functional polymers. In this study, we report on the modification of glucose oxidase (GOX) with ferrocene-containing redox polymers to increase current generation efficiency in an enzyme-modified anode. Poly(N-(3-dimethyl(ferrocenyl)methylammonium bromide)propyl acrylamide) (pFcAc) was grown from covalently attached, water-soluble initiator molecules on the surface of GOX in a "grafting-from" approach using atom transfer radical polymerization (ATRP). The covalently-coupled ferrocene-containing polymers on the enzyme surface promoted the effective "wiring" of the GOX active site to an external electrode. The resulting GOX-pFcAc conjugates generated over an order of magnitude increase in current generation efficiency and a 4-fold increase in maximum EBFC power density (≈1.7µWcm(-2)) with similar open circuit voltage (0.27V) compared to native GOX when physically adsorbed onto paddle-shaped electrodes made up of electrospun polyacrylonitrile fibers coated with gold nanoparticles and multi-wall carbon nanotubes. The formation of electroactive enzyme-redox polymer conjugates using PBPE represents a powerful new tool for the improvement of mediated enzyme-based bioelectronics without the need for free redox mediators or anode/cathode compartmentalization. Copyright © 2016 The Authors. Published by Elsevier B.V. All rights reserved.

Nanofiber Orientation and Surface Functionalization Modulate Human Mesenchymal Stem Cell Behavior In Vitro

PubMed Central

Kolambkar, Yash M.; Bajin, Mehmet; Wojtowicz, Abigail; Hutmacher, Dietmar W.; García, Andrés J.

2014-01-01

Electrospun nanofiber meshes have emerged as a new generation of scaffold membranes possessing a number of features suitable for tissue regeneration. One of these features is the flexibility to modify their structure and composition to orchestrate specific cellular responses. In this study, we investigated the effects of nanofiber orientation and surface functionalization on human mesenchymal stem cell (hMSC) migration and osteogenic differentiation. We used an in vitro model to examine hMSC migration into a cell-free zone on nanofiber meshes and mitomycin C treatment to assess the contribution of proliferation to the observed migration. Poly (ɛ-caprolactone) meshes with oriented topography were created by electrospinning aligned nanofibers on a rotating mandrel, while randomly oriented controls were collected on a stationary collector. Both aligned and random meshes were coated with a triple-helical, type I collagen-mimetic peptide, containing the glycine-phenylalanine-hydroxyproline-glycine-glutamate-arginine (GFOGER) motif. Our results indicate that nanofiber GFOGER peptide functionalization and orientation modulate cellular behavior, individually, and in combination. GFOGER significantly enhanced the migration, proliferation, and osteogenic differentiation of hMSCs on nanofiber meshes. Aligned nanofiber meshes displayed increased cell migration along the direction of fiber orientation compared to random meshes; however, fiber alignment did not influence osteogenic differentiation. Compared to each other, GFOGER coating resulted in a higher proliferation-driven cell migration, whereas fiber orientation appeared to generate a larger direct migratory effect. This study demonstrates that peptide surface modification and topographical cues associated with fiber alignment can be used to direct cellular behavior on nanofiber mesh scaffolds, which may be exploited for tissue regeneration. PMID:24020454

The formation of web-like connection among electrospun chitosan/PVA fiber network by the reinforcement of ellipsoidal calcium carbonate.

PubMed

Sambudi, Nonni Soraya; Kim, Minjeong G; Park, Seung Bin

2016-03-01

The electrospun fibers consist of backbone fibers and nano-branch network are synthesized by loading of ellipsoidal calcium carbonate in the mixture of chitosan/poly(vinyl alcohol) (PVA) followed by electrospinning. The synthesized ellipsoidal calcium carbonate is in submicron size (730.7±152.4 nm for long axis and 212.6±51.3 nm for short axis). The electrospun backbone fibers experience an increasing in diameter by loading of calcium carbonate from 71.5±23.4 nm to 281.9±51.2 nm. The diameters of branch fibers in the web-network range from 15 nm to 65 nm with most distributions of fibers are in 30-35 nm. Calcium carbonate acts as reinforcing agent to improve the mechanical properties of fibers. The optimum value of Young's modulus is found at the incorporation of 3 wt.% of calcium carbonate in chitosan/PVA fibers, which is enhanced from 15.7±3 MPa to 432.4±94.3 MPa. On the other hand, the ultimate stress of fibers experiences a decrease. This result shows that the fiber network undergoes changes from flexible to more stiff by the inclusion of calcium carbonate. The thermal analysis results show that the crystallinity of polymer is changed by the existence of calcium carbonate in the fiber network. The immersion of fibers in simulated body fluid (SBF) results in the formation of apatite on the surface of fibers. Copyright © 2015 Elsevier B.V. All rights reserved.

Synthesis and photocatalytic activity of electrospun niobium oxide nanofibers

DOE Office of Scientific and Technical Information (OSTI.GOV)

Qi, Shishun; Zuo, Ruzhong, E-mail: piezolab@hfut.edu.cn; Liu, Yi

2013-03-15

Graphical abstract: Different morphologies are obtained for the electrospun niobium oxide nanofibers with different phase structures. The nanofibers of the two phase structures present different band gap value and the light absorption. Hexagonal phase nanofibers show better photocatalytic activity compared with the orthorhombic nanofibers. Highlights: ► Niobium oxide nanofibers of two phase structures were fabricated by electrospinning. ► Photocatalytic properties of the niobium oxide nanofibers were first explored. ► Nanofibers of different phase structures showed different photocatalytic activities. ► Reasons for the differences in the photocatalysis were carefully discussed. - Abstract: Niobium oxide (Nb{sub 2}O{sub 5}) nanofibers have been synthesizedmore » by sol–gel based electrospinning technique. Pure hexagonal phase (H-Nb{sub 2}O{sub 5}) and orthorhombic phase (O-Nb{sub 2}O{sub 5}) nanofibers were obtained by thermally annealing the electrospun Nb{sub 2}O{sub 5}/polyvinylpyrrolidone composite fibers in air at 500 °C and 700 °C, respectively. The fibers were characterized using the X-ray diffraction, scanning electron microscopy, specific surface area analyzer and UV–vis diffuse reflectance spectroscopy. Photocatalytic activities of the obtained nanofibers were evaluated depending on the degradation of methyl orange. The results indicate that the heat-treatment temperature, the crystalline structure and the morphology affected the physical and chemical properties of the as-prepared Nb{sub 2}O{sub 5} nanofibers. The H-Nb{sub 2}O{sub 5} nanofibers obtained at lower temperature showed better potential for the application as a promising photocatalyst.« less

Characterization of electrospun lignin based carbon fibers

DOE Office of Scientific and Technical Information (OSTI.GOV)

Poursorkhabi, Vida; Mohanty, Amar; Misra, Manjusri

2015-05-22

The production of lignin fibers has been studied in order to replace the need for petroleum based precursors for carbon fiber production. In addition to its positive environmental effects, it also benefits the economics of the industries which cannot take advantage of carbon fiber properties because of their high price. A large amount of lignin is annually produced as the byproduct of paper and growing cellulosic ethanol industry. Therefore, finding high value applications for this low cost, highly available material is getting more attention. Lignin is a biopolymer making about 15 – 30 % of the plant cell walls andmore » has a high carbon yield upon carbonization. However, its processing is challenging due to its low molecular weight and also variations based on its origin and the method of separation from cellulose. In this study, alkali solutions of organosolv lignin with less than 1 wt/v% of poly (ethylene oxide) and two types of lignin (hardwood and softwood) were electrospun followed by carbonization. Different heating programs for carbonization were tested. The carbonized fibers had a smooth surface with an average diameter of less than 5 µm and the diameter could be controlled by the carbonization process and lignin type. Scanning electron microscopy (SEM) was used to study morphology of the fibers before and after carbonization. Thermal conductivity of a sample with amorphous carbon was 2.31 W/m.K. The electrospun lignin carbon fibers potentially have a large range of application such as in energy storage devices and water or gas purification systems.« less

Inhibitor of PI3K/Akt Signaling Pathway Small Molecule Promotes Motor Neuron Differentiation of Human Endometrial Stem Cells Cultured on Electrospun Biocomposite Polycaprolactone/Collagen Scaffolds.

PubMed

Ebrahimi-Barough, Somayeh; Hoveizi, Elham; Yazdankhah, Meysam; Ai, Jafar; Khakbiz, Mehrdad; Faghihi, Faezeh; Tajerian, Roksana; Bayat, Neda

2017-05-01

Small molecules as useful chemical tools can affect cell differentiation and even change cell fate. It is demonstrated that LY294002, a small molecule inhibitor of phosphatidylinositol 3-kinase (PI3K)/Akt signal pathway, can inhibit proliferation and promote neuronal differentiation of mesenchymal stem cells (MSCs). The purpose of this study was to investigate the differentiation effect of Ly294002 small molecule on the human endometrial stem cells (hEnSCs) into motor neuron-like cells on polycaprolactone (PCL)/collagen scaffolds. hEnSCs were cultured in a neurogenic inductive medium containing 1 μM LY294002 on the surface of PCL/collagen electrospun fibrous scaffolds. Cell attachment and viability of cells on scaffolds were characterized by scanning electron microscope (SEM) and 3-(4,5-dimethylthiazoyl-2-yl)2,5-diphenyltetrazolium bromide (MTT) assay. The expression of neuron-specific markers was assayed by real-time PCR and immunocytochemistry analysis after 15 days post induction. Results showed that attachment and differentiation of hEnSCs into motor neuron-like cells on the scaffolds with Ly294002 small molecule were higher than that of the cells on tissue culture plates as control group. In conclusion, PCL/collagen electrospun scaffolds with Ly294002 have potential for being used in neural tissue engineering because of its bioactive and three-dimensional structure which enhances viability and differentiation of hEnSCs into neurons through inhibition of the PI3K/Akt pathway. Thus, manipulation of this pathway by small molecules can enhance neural differentiation.

Periodontal ligament cellular structures engineered with electrospun poly(DL-lactide-co-glycolide) nanofibrous membrane scaffolds.

PubMed

Inanç, Bülend; Arslan, Y Emre; Seker, Sükran; Elçin, A Eser; Elçin, Y Murat

2009-07-01

Periodontal tissue engineering is expected to overcome the limitations associated with the existing regenerative techniques for the treatment of periodontal defects involving alveolar bone, cementum, and periodontal ligament. Cell-based tissue engineering approaches involve the utilization of in vitro expanded cells with regenerative capacity and their delivery to the appropriate sites via biomaterial scaffolds. The aim of this study was to establish living periodontal ligament cell-containing structures on electrospun poly(DL-lactic-co-glycolic acid) (PLGA) nanofiber membrane scaffolds, assess their viability and characteristics, and engineer multilayered structures amenable to easy handling. Human periodontal ligament (hPDL) cells were expanded in explant culture and then characterized morphologically and immunohistochemically. PLGA nanofiber membranes were prepared by the electrospinning process; mechanical tensile properties were determined, surface topography, nanofiber size, and porosity status were investigated with SEM. Cells were seeded on the membranes at approximately 50,000 cell/cm(2) and cultured for 21 days either in expansion or in osteogenic induction medium. Cell adhesion and viability were demonstrated using SEM and MTT, respectively, and osteogenic differentiation was determined with IHC and immunohistomorphometric evaluation of osteopontin, osteocalcin, and bone sialoprotein marker expression. At days 3, 6, 9, and 12 additional cell/membrane layers were deposited on the existing ones and multilayered hybrid structures were established. Results indicate the feasibility of periodontal ligament cell-containing tissue-like structures engineering with PDL cells and electrospun nanofiber PLGA scaffolds supporting cell adhesion, viability and osteogenic differentiation properties of cells in hybrid structures amenable to macroscopic handling.

The surface grafting of graphene oxide with poly(ethylene glycol) as a reinforcement for poly(lactic acid) nanocomposite scaffolds for potential tissue engineering applications.

PubMed

Zhang, Chunmei; Wang, Liwei; Zhai, Tianliang; Wang, Xinchao; Dan, Yi; Turng, Lih-Sheng

2016-01-01

Graphene oxide (GO) was incorporated into poly(lactic acid) (PLA) as a reinforcing nanofiller to produce composite nanofibrous scaffolds using the electrospinning technique. To improve the dispersion of GO in PLA and the interfacial adhesion between the filler and matrix, GO was surface-grafted with poly(ethylene glycol) (PEG). Morphological, thermal, mechanical, and wettability properties, as well as preliminary cytocompatibility with Swiss mouse NIH 3T3 cells of PLA, PLA/GO, and PLA/GO-g-PEG electrospun nanofibers, were characterized. Results showed that the average diameter of PLA/GO-g-PEG electrospun nanofibers decreased with filler content. Both GO and GO-g-PEG improved the thermal stability of PLA, but GO-g-PEG was more effective. The water contact angle test of the nanofiber mats showed that the addition of GO in PLA did not change the surface wettability of the materials, but PLA/GO-g-PEG samples exhibited improved wettability with lower water contact angles. The tensile strength of the composite nanofiber mats was improved with the addition of GO, and it was further enhanced when GO was surface grafted with PEG. This suggested that improved interfacial adhesion between GO and PLA was achieved by grafting PEG onto the GO. The cell viability and proliferation results showed that the cytocompatibility of PLA was not compromised with the addition of GO and GO-g-PEG. With enhanced mechanical properties as well as good wettability and cytocompatibility, PLA/GO-g-PEG composite nanofibers have the potential to be used as scaffolds in tissue engineering. Copyright © 2015 Elsevier Ltd. All rights reserved.

A high-performance, flexible and robust metal nanotrough-embedded transparent conducting film for wearable touch screen panels

NASA Astrophysics Data System (ADS)

Im, Hyeon-Gyun; An, Byeong Wan; Jin, Jungho; Jang, Junho; Park, Young-Geun; Park, Jang-Ung; Bae, Byeong-Soo

2016-02-01

We report a high-performance, flexible and robust metal nanotrough-embedded transparent conducting hybrid film (metal nanotrough-GFRHybrimer). Using an electro-spun polymer nanofiber web as a template and vacuum-deposited gold as a conductor, a junction resistance-free continuous metal nanotrough network is formed. Subsequently, the metal nanotrough is embedded on the surface of a glass-fabric reinforced composite substrate (GFRHybrimer). The monolithic composite structure of our transparent conducting film allows simultaneously high thermal stability (24 h at 250 °C in air), a smooth surface topography (Rrms < 1 nm) and excellent opto-electrical properties. A flexible touch screen panel (TSP) is fabricated using the transparent conducting films. The flexible TSP device stably operates on the back of a human hand and on a wristband.We report a high-performance, flexible and robust metal nanotrough-embedded transparent conducting hybrid film (metal nanotrough-GFRHybrimer). Using an electro-spun polymer nanofiber web as a template and vacuum-deposited gold as a conductor, a junction resistance-free continuous metal nanotrough network is formed. Subsequently, the metal nanotrough is embedded on the surface of a glass-fabric reinforced composite substrate (GFRHybrimer). The monolithic composite structure of our transparent conducting film allows simultaneously high thermal stability (24 h at 250 °C in air), a smooth surface topography (Rrms < 1 nm) and excellent opto-electrical properties. A flexible touch screen panel (TSP) is fabricated using the transparent conducting films. The flexible TSP device stably operates on the back of a human hand and on a wristband. Electronic supplementary information (ESI) available. See DOI: 10.1039/c5nr07657a

Antifungal nanofibers made by controlled release of sea animal derived peptide

NASA Astrophysics Data System (ADS)

Viana, Juliane F. C.; Carrijo, Jéssica; Freitas, Camila G.; Paul, Arghya; Alcaraz, Jarib; Lacorte, Cristiano C.; Migliolo, Ludovico; Andrade, César A.; Falcão, Rosana; Santos, Nuno C.; Gonçalves, Sónia; Otero-González, Anselmo J.; Khademhosseini, Ali; Dias, Simoni C.; Franco, Octávio L.

2015-03-01

Candida albicans is a common human-pathogenic fungal species with the ability to cause several diseases including surface infections. Despite the clear difficulties of Candida control, antimicrobial peptides (AMPs) have emerged as an alternative strategy for fungal control. In this report, different concentrations of antifungal Cm-p1 (Cencritchis muricatus peptide 1) were electrospun into nanofibers for drug delivery. The nanofibers were characterized by mass spectrometry confirming the presence of the peptide on the scaffold. Atomic force microscopy and scanning electronic microscopy were used to measure the diameters, showing that Cm-p1 affects fiber morphology as well as the diameter and scaffold thickness. The Cm-p1 release behavior from the nanofibers demonstrated peptide release from 30 min to three days, leading to effective yeast control in the first 24 hours. Moreover, the biocompatibility of the fibers were evaluated through a MTS assay as well as ROS production by using a HUVEC model, showing that the fibers do not affect cell viability and only nanofibers containing 10% Cm-p1-PVA improved ROS generation. In addition, the secretion of pro-inflammatory cytokines IL-6 and TNF-α by the HUVECs was also slightly modified by the 10% Cm-p1-PVA nanofibers. In conclusion, the electrospinning technique applied here allowed for the manufacture of biodegradable biomimetic nanofibrous extracellular membranes with the ability to control fungal infection.Candida albicans is a common human-pathogenic fungal species with the ability to cause several diseases including surface infections. Despite the clear difficulties of Candida control, antimicrobial peptides (AMPs) have emerged as an alternative strategy for fungal control. In this report, different concentrations of antifungal Cm-p1 (Cencritchis muricatus peptide 1) were electrospun into nanofibers for drug delivery. The nanofibers were characterized by mass spectrometry confirming the presence of the peptide on the scaffold. Atomic force microscopy and scanning electronic microscopy were used to measure the diameters, showing that Cm-p1 affects fiber morphology as well as the diameter and scaffold thickness. The Cm-p1 release behavior from the nanofibers demonstrated peptide release from 30 min to three days, leading to effective yeast control in the first 24 hours. Moreover, the biocompatibility of the fibers were evaluated through a MTS assay as well as ROS production by using a HUVEC model, showing that the fibers do not affect cell viability and only nanofibers containing 10% Cm-p1-PVA improved ROS generation. In addition, the secretion of pro-inflammatory cytokines IL-6 and TNF-α by the HUVECs was also slightly modified by the 10% Cm-p1-PVA nanofibers. In conclusion, the electrospinning technique applied here allowed for the manufacture of biodegradable biomimetic nanofibrous extracellular membranes with the ability to control fungal infection. Electronic supplementary information (ESI) available. See DOI: 10.1039/c5nr00767d

Human dental pulp stem cell adhesion and detachment in polycaprolactone electrospun scaffolds under direct perfusion

PubMed Central

Paim, A.; Braghirolli, D.I.; Cardozo, N.S.M.; Pranke, P.; Tessaro, I.C.

2018-01-01

Cell adhesion in three-dimensional scaffolds plays a key role in tissue development. However, stem cell behavior in electrospun scaffolds under perfusion is not fully understood. Thus, an investigation was made on the effect of flow rate and shear stress, adhesion time, and seeding density under direct perfusion in polycaprolactone electrospun scaffolds on human dental pulp stem cell detachment. Polycaprolactone scaffolds were electrospun using a solvent mixture of chloroform and methanol. The viable cell number was determined at each tested condition. Cell morphology was analyzed by confocal microscopy after various incubation times for static cell adhesion with a high seeding density. Scanning electron microscopy images were obtained before and after perfusion for the highest flow rate tested. The wall pore shear stress was calculated for all tested flow rates (0.005–3 mL/min). An inversely proportional relationship between adhesion time with cell detachment under perfusion was observed. Lower flow rates and lower seeding densities reduced the drag of cells by shear stress. However, there was an operational limit for the lowest flow rate that can be used without compromising cell viability, indicating that a flow rate of 0.05 mL/min might be more suitable for the tested cell culture in electrospun scaffolds under direct perfusion. PMID:29590258

Cellulose acetate based 3-dimensional electrospun scaffolds for skin tissue engineering applications.

PubMed

Atila, Deniz; Keskin, Dilek; Tezcaner, Ayşen

2015-11-20

Skin defects that are not able to regenerate by themselves are among the major problems faced. Tissue engineering approach holds promise for treating such defects. Development of tissue-mimicking-scaffolds that can promote healing process receives an increasing interest in recent years. In this study, 3-dimensional electrospun cellulose acetate (CA) pullulan (PULL) scaffolds were developed for the first time. PULL was intentionally used to obtain 3D structures with adjustable height. It was removed from the electrospun mesh to increase the porosity and biostability. Different ratios of the polymers were electrospun and analyzed with respect to degradation, porosity, and mechanical properties. It has been observed that fiber diameter, thickness and porosity of scaffolds increased with increased PULL content, on the other hand this resulted with higher degradation of scaffolds. Mechanical strength of scaffolds was improved after PULL removal suggesting their suitability as cell carriers. Cell culture studies were performed with the selected scaffold group (CA/PULL: 50/50) using mouse fibroblastic cell line (L929). In vitro cell culture tests showed that cells adhered, proliferated and populated CA/PULL (50/50) scaffolds showing that they are cytocompatible. Results suggest that uncrosslinked CA/PULL (50/50) electrospun scaffolds hold potential for skin tissue engineering applications. Copyright © 2015 Elsevier Ltd. All rights reserved.

Multilayered Electrospun Scaffolds for Tendon Tissue Engineering

PubMed Central

Chainani, Abby; Hippensteel, Kirk J.; Kishan, Alysha; Garrigues, N. William; Ruch, David S.; Guilak, Farshid

2013-01-01

Full-thickness rotator cuff tears are one of the most common causes of shoulder pain in people over the age of 65. High retear rates and poor functional outcomes are common after surgical repair, and currently available extracellular matrix scaffold patches have limited abilities to enhance new tendon formation. In this regard, tissue-engineered scaffolds may provide a means to improve repair of rotator cuff tears. Electrospinning provides a versatile method for creating nanofibrous scaffolds with controlled architectures, but several challenges remain in its application to tissue engineering, such as cell infiltration through the full thickness of the scaffold as well as control of cell growth and differentiation. Previous studies have shown that ligament-derived extracellular matrix may enhance differentiation toward a tendon or ligament phenotype by human adipose stem cells (hASCs). In this study, we investigated the use of tendon-derived extracellular matrix (TDM)-coated electrospun multilayered scaffolds compared to fibronectin (FN) or phosphate-buffered saline (PBS) coating for use in rotator cuff tendon tissue engineering. Multilayered poly(ɛ-caprolactone) scaffolds were prepared by sequentially collecting electrospun layers onto the surface of a grounded saline solution into a single scaffold. Scaffolds were then coated with TDM, FN, or PBS and seeded with hASCs. Scaffolds were maintained without exogenous growth factors for 28 days in culture and evaluated for protein content (by immunofluorescence and biochemical assay), markers of tendon differentiation, and tensile mechanical properties. The collagen content was greatest by day 28 in TDM-scaffolds. Gene expression of type I collagen, decorin, and tenascin C increased over time, with no effect of scaffold coating. Sulfated glycosaminoglycan and dsDNA contents increased over time in culture, but there was no effect of scaffold coating. The Young's modulus did not change over time, but yield strain increased with time in culture. Histology demonstrated cell infiltration through the full thickness of all scaffolds and immunofluorescence demonstrated greater expression of type I, but not type III collagen through the full thickness of the scaffold in TDM-scaffolds compared to other treatment groups. Together, these data suggest that nonaligned multilayered electrospun scaffolds permit tenogenic differentiation by hASCs and that TDM may promote some aspects of this differentiation. PMID:23808760

Sustained delivery of siRNA/mesoporous silica nanoparticle (siRNA/MSN) complexes from nanofiber scaffolds for long-term gene silencing.

PubMed

Pinese, Coline; Lin, Junquan; Milbreta, Ulla; Li, Mingqiang; Wang, Yucai; Leong, Kam W; Chew, Sing Yian

2018-06-08

A low toxicity and efficient delivery system is needed to deliver small interfering RNAs (siRNA) in vitro and in vivo. The use of mesoporous silica nanoparticles (MSN) is becoming increasingly common due to its biocompatibility, tunable pore size and customizable properties. However, bolus delivery of siRNA/MSN complexes remains suboptimal, especially when a sustained and long-term administration is required. Here, we utilized electrospun scaffolds for sustained delivery of siRNA/MSN-PEI through surface adsorption and nanofiber encapsulation. As a proof-of-concept, we targeted collagen type I expression to modulate fibrous capsule formation. Surface adsorption of siRNA/MSN-PEI provided sustained availability of siRNA for at least 30 days in vitro. As compared to conventional bolus delivery, such scaffold-mediated transfection provided more effective gene silencing (p < 0.05). On the contrary, a longer sustained release was attained (at least 5 months) when siRNA/MSN-PEI complexes were encapsulated within the electrospun fibers. In vivo subcutaneous implantation and biodistribution analysis of these scaffolds revealed that siRNA remained localized up to ∼290 μm from the implants. Finally, a fibrous capsule reduction of ∼45.8 % was observed after 4 weeks in vivo as compared to negative scrambled siRNA treatment. Taken together, these results demonstrate the efficacy of scaffold-mediated sustained delivery of siRNA/MSN-PEI for long-term non-viral gene silencing applications. The bolus delivery of siRNA/ Mesoporous Silica Nanoparticles (MSN) complexes shows high efficiency to silence protein agonists of tumoral processes as cancer treatments. However, in tissue engineering area, scaffold mediated delivery is desired to achieve a local and sustained release of therapeutics. We showed the feasibility and the efficacy of siRNA/MSN delivered from electrospun scaffolds through surface adsorption and nanofiber encapsulation. We showed that this method enhances siRNA transfection efficiency and sustained targeted proteins silencing in vitro and in vivo. As a proof of concept, in this study, we targeted collagen type I expression to modulate fibrous capsule formation. However this platform can be applied to the release and transfection of siRNA or miRNA in cancer and tissue engineering applications. Copyright © 2018 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

Graphene-loaded nanofiber-modified electrodes for the ultrasensitive determination of dopamine.

PubMed

Rodthongkum, Nadnudda; Ruecha, Nipapan; Rangkupan, Ratthapol; Vachet, Richard W; Chailapakul, Orawon

2013-12-04

A novel and highly sensitive electrochemical system based on electrospun graphene/polyaniline/polystyrene (G/PANI/PS) nanofiber-modified screen-printed carbon electrodes has been developed for dopamine (DA) determination. A dramatic increase (9 times) in the current signal for the redox reaction of a standard, ferri/ferrocyanide [Fe(CN)6](3-/4-) couple was found when compared to an unmodified electrode. This modified electrode also exhibited favorable electron transfer kinetics and excellent electrocatalytic activity toward the oxidation of DA. When used together with square wave voltammetry (SWV), DA can be selectively determined in the presence of the common interferents (i.e. ascorbic acid and uric acid). Under optimal conditions, a very low limit of detection (0.05 nM) and limit of quantification (0.30 nM) were achieved for DA. In addition, a wide dynamic range of 0.1 nM to 100 μM was found for this electrode system. Finally, the system can be successfully applied to determine DA in complex biological environment (e.g. human serum, urine) with excellent reproducibility. Copyright © 2013 Elsevier B.V. All rights reserved.

Isotropic Versus Bipolar Functionalized Biomimetic Artificial Basement Membranes and Their Evaluation in Long-Term Human Cell Co-Culture.

PubMed

Rossi, Angela; Wistlich, Laura; Heffels, Karl-Heinz; Walles, Heike; Groll, Jürgen

2016-08-01

In addition to dividing tissues into compartments, basement membranes are crucial as cell substrates and to regulate cellular behavior. The development of artificial basement membranes is indispensable for the ultimate formation of functional engineered tissues; however, pose a challenge due to their complex structure. Herein, biodegradable electrospun polyester meshes are presented, exhibiting isotropic or bipolar bioactivation as a biomimetic and biofunctional model of the natural basement membrane. In a one-step preparation process, reactive star-shaped prepolymer additives, which generate a hydrophilic fiber surface, are electrospun with cell-adhesion-mediating peptides, derived from major components of the basement membrane. Human skin cells adhere to the functionalized meshes, and long-term co-culture experiments confirm that the artificial basement membranes recapitulate and preserve tissue specific functions. Several layers of immortalized human keratinocytes grow on the membranes, differentiating toward the surface and expressing typical epithelial markers. Fibroblasts migrate into the reticular lamina mimicking part of the mesh. Both cells types begin to produce extracellular matrix proteins and to remodel the initial membrane. It is shown at the example of skin that the artificial basement membrane design provokes biomimetic responses of different cell types and can thus be used as basis for the future development of basement membrane containing tissues. © 2016 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Highly conductive electrospun carbon nanofiber/MnO2 coaxial nano-cables for high energy and power density supercapacitors

NASA Astrophysics Data System (ADS)

Zhi, Mingjia; Manivannan, Ayyakkannu; Meng, Fanke; Wu, Nianqiang

2012-06-01

This paper presents highly conductive carbon nanofiber/MnO2 coaxial cables in which individual electrospun carbon nanofibers are coated with an ultrathin hierarchical MnO2 layer. In the hierarchical MnO2 structure, an around 4 nm thick sheath surrounds the carbon nanofiber (CNF) in a diameter of 200 nm, and nano-whiskers grow radically outward from the sheath in view of the cross-section of the coaxial cables, giving a high specific surface area of MnO2. The CNFs are synthesized by electrospinning a precursor containing iron acetylacetonate (AAI). The addition of AAI not only enlarges the specific surface area of the CNF but also greatly enhances their electronic conductivity, which leads to a dramatic improvement in the specific capacitance and the rate capability of the CNF/MnO2 electrode. The AAI-CNF/MnO2 electrode shows a specific capacitance of 311 F g-1 for the whole electrode and 900 F g-1 for the MnO2 shell at a scan rate of 2 mV s-1. Good cycling stability, high energy density (80.2 Wh kg-1) and high power density (57.7 kW kg-1) are achieved. This work indicates that high electronic conductivity of the electrode material is crucial to achieving high power and energy density for pseudo-supercapacitors.

Novel poly(ε-caprolactone)/gelatin wound dressings prepared by emulsion electrospinning with controlled release capacity of Ketoprofen anti-inflammatory drug.

PubMed

Basar, A O; Castro, S; Torres-Giner, S; Lagaron, J M; Turkoglu Sasmazel, H

2017-12-01

In the present study, a single and binary Ketoprofen-loaded mats of ultrathin fibers were developed by electrospinning and their physical properties and drug release capacity was analyzed. The single mat was prepared by solution electrospinning of poly(ε-caprolactone) (PCL) with Ketoprofen at a weight ratio of 5wt%. This Ketoprofen-containing PCL solution was also used as the oil phase in a 7:3 (wt/wt) emulsion with gelatin dissolved in acidified water. The resultant stable oil-in-water (O/W) emulsion of PCL-in-gelatin, also containing Ketoprofen at 5wt%, was electrospun to produce the binary mat. Cross-linking process was performed by means of glutaraldehyde vapor on the electrospun binary mat to prevent dissolution of the hydrophilic gelatin phase. The performed characterization indicated that Ketoprofen was successfully embedded in the single and binary electrospun mats, i.e. PCL and PCL/gelatin, and both mats showed high hydrophobicity but poor thermal resistance. In vitro release studies interestingly revealed that, in comparison to the single PCL electrospun mat, the binary PCL/gelatin mat significantly hindered Ketoprofen burst release and exhibited a sustained release capacity of the drug for up to 4days. In addition, the electrospun Ketoprofen-loaded mats showed enhanced attachment and proliferation of L929 mouse fibroblast cells, presenting the binary mat the highest cell growth yield due to its improved porosity. The here-developed electrospun materials clearly show a great deal of potential as novel wound dressings with an outstanding controlled capacity to release drugs. Copyright © 2017 Elsevier B.V. All rights reserved.

Conductive cable fibers with insulating surface prepared by co-axial electrospinning of multi-walled nanotubes and cellulose

PubMed Central

Miyauchi, Minoru; Miao, Jianjun; Simmons, Trevor J.; Lee, Jong-Won; Doherty, Thomas V.; Dordick, Jonathan S.; Linhardt, Robert J.

2010-01-01

A core-sheath of multi-walled carbon nanotube (MWNT)-cellulose fibers of diameters from several hundreds nm to several µm were prepared by co-axial electrospinning from a non-valatile, non-flammable ionic liquid (IL) solvent, 1-methyl-3-methylimidazolium acetate ([EMIM][Ac]). MWNTs were dispersed in IL to form a gel solution. This gel core solution was electrospun surrounded by a sheath solution of cellulose disolved in the same IL. Electrospun fibers were collected in a coagulation bath containing ethanol-water to completely remove the IL and dried to form a core-sheath MWNT-cellulose fibers having a cable structure with a conductive core and insulating sheath. Enzymatic treatment of a portion of a mat of these fibers with cellulase selectively removed the cellulose sheath exposing the MWNT core for connection to an electrode. These MWNT-cellulose fiber mats demonstrated excellent conductivity due to a conductive pathway of bundleled MWNTs. Fiber mat conductivity increased with increasing ratio of MWNT in the fibers with a maximum conductivity of 10.7 S/m obtained at 45 wt% MWNT loading. PMID:20690644

Conductive cable fibers with insulating surface prepared by coaxial electrospinning of multiwalled nanotubes and cellulose.

PubMed

Miyauchi, Minoru; Miao, Jianjun; Simmons, Trevor J; Lee, Jong-Won; Doherty, Thomas V; Dordick, Jonathan S; Linhardt, Robert J

2010-09-13

Core-sheath multiwalled carbon nanotube (MWNT)-cellulose fibers of diameters from several hundreds of nanometers to several micrometers were prepared by coaxial electrospinning from a nonvolatile, nonflammable ionic liquid (IL) solvent, 1-methyl-3-methylimidazolium acetate ([EMIM][Ac]). MWNTs were dispersed in IL to form a gel solution. This gel core solution was electrospun surrounded by a sheath solution of cellulose dissolved in the same IL. Electrospun fibers were collected in a coagulation bath containing ethanol-water to remove the IL completely and dried to form core-sheath MWNT-cellulose fibers having a cable structure with a conductive core and insulating sheath. Enzymatic treatment of a portion of a mat of these fibers with cellulase selectively removed the cellulose sheath exposing the MWNT core for connection to an electrode. These MWNT-cellulose fiber mats demonstrated excellent conductivity because of a conductive pathway of bundled MWNTs. Fiber mat conductivity increased with increasing ratio of MWNT in the fibers with a maximum conductivity of 10.7 S/m obtained at 45 wt % MWNT loading.

Junction-Free Electrospun Ag Fiber Electrodes for Flexible Organic Light-Emitting Diodes.

PubMed

Choi, Junhee; Shim, Yong Sub; Park, Cheol Hwee; Hwang, Ha; Kwack, Jin Ho; Lee, Dong Jun; Park, Young Wook; Ju, Byeong-Kwon

2018-02-01

Fabrication of junction-free Ag fiber electrodes for flexible organic light-emitting diodes (OLEDs) is demonstrated. The junction-free Ag fiber electrodes are fabricated by electrospun polymer fibers used as an etch mask and wet etching of Ag thin film. This process facilitates surface roughness control, which is important in transparent electrodes based on metal wires to prevent electrical instability of the OLEDs. The transmittance and resistance of Ag fiber electrodes can be independently adjusted by controlling spinning time and Ag deposition thickness. The Ag fiber electrode shows a transmittance of 91.8% (at 550 nm) at a sheet resistance of 22.3 Ω □ -1 , leading to the highest OLED efficiency. In addition, Ag fiber electrodes exhibit excellent mechanical durability, as shown by measuring the change in resistance under repeatable mechanical bending and various bending radii. The OLEDs with Ag fiber electrodes on a flexible substrate are successfully fabricated, and the OLEDs show an enhancement of EQE (≈19%) compared to commercial indium tin oxide electrodes. © 2017 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Electrospun polyvinylpyrrolidone (PVP)/green tea extract composite nanofiber mats and their antioxidant activities

NASA Astrophysics Data System (ADS)

Pusporini, Pusporini; Edikresnha, Dhewa; Sriyanti, Ida; Suciati, Tri; Miftahul Munir, Muhammad; Khairurrijal, Khairurrijal

2018-05-01

Electrospinning was employed to make PVP (polyvinylpyrrolidone)/GTE (green tea extract) composite nanofiber mats. The electrospun PVP nanofiber mat as well as the PVP/GTE nanofiber mats were uniform. The average fiber diameter of PVP/GTE composite nanofiber mat decreased with increasing the GTE weight fraction (or decreasing the PVP weight fraction) in the PVP/GTE solution because the PVP/GTE solution concentration decreased. Then, the broad FTIR peak representing the stretching vibrations of O–H in hydroxyl groups of phenols and the stretching of N–H in amine groups of the GTE paste shifted to higher wavenumbers in the PVP/GTE composite nanofiber mats. These peak shifts implied that PVP and catechins of GTE in the PVP/GTE composite nanofiber mats had intermolecular interactions via hydrogen bonds between carbonyl groups of PVP and hydroxyl groups of catechins in GTE. Lastly, the antioxidant activity of the PVP/GTE composite nanofiber mat increased with reducing the average fiber diameter because the amount of catechins in the composite nanofiber mat increased with the increase of surface area due to the reduction of the average fiber diameter.

κ-Carrageenan Enhances the Biomineralization and Osteogenic Differentiation of Electrospun Polyhydroxybutyrate and Polyhydroxybutyrate Valerate Fibers.

PubMed

Goonoo, Nowsheen; Khanbabaee, Behnam; Steuber, Marc; Bhaw-Luximon, Archana; Jonas, Ulrich; Pietsch, Ullrich; Jhurry, Dhanjay; Schönherr, Holger

2017-05-08

Novel electrospun materials for bone tissue engineering were obtained by blending biodegradable polyhydroxybutyrate (PHB) or polyhydroxybutyrate valerate (PHBV) with the anionic sulfated polysaccharide κ-carrageenan (κ-CG) in varying ratios. In both systems, the two components phase separated as shown by FTIR, DSC and TGA. According to the contact angle data, κ-CG was localized preferentially at the fiber surface in PHBV/κ-CG blends in contrast to PHB/κ-CG, where the biopolymer was mostly found within the fiber. In contrast to the neat polyester fibers, the blends led to the formation of much smaller apatite crystals (800 nm vs 7 μm). According to the MTT assay, NIH3T3 cells grew in higher density on the blend mats in comparison to neat polyester mats. The osteogenic differentiation potential of the fibers was determined by SaOS-2 cell culture for 2 weeks. Alizarin red-S staining suggested an improved mineralization on the blend fibers. Thus, PHBV/κ-CG fibers resulted in more pronounced bioactive and osteogenic properties, including fast apatite-forming ability and deposition of nanosized apatite crystals.

Prevention of peritendinous adhesions with electrospun ibuprofen-loaded poly(L-lactic acid)-polyethylene glycol fibrous membranes.

PubMed

Liu, Shen; Hu, Changmin; Li, Fengfeng; Li, Xu-jun; Cui, Wenguo; Fan, Cunyi

2013-02-01

Physical barriers are commonly used to reduce peritendinous adhesion after injury. However, the inflammatory response to surgery cannot be prevented. This study was designed to evaluate the ability of ibuprofen-loaded poly(l-lactic acid)-polyethylene glycol (PELA) diblock copolymer fibrous membranes in preventing adhesion formation and reduce inflammation. Electrospun PELA fibrous membranes underwent mechanical testing and were characterized by morphology, surface wettability, drug release, and degradation. Results of an in vitro drug release study showed that a burst release was followed by sustained release from fibrous membranes with high initial ibuprofen content. Fewer L929 mouse fibroblasts adhered to and proliferated on the ibuprofen-loaded PELA fibrous membrane compared with tissue culture plates or PELA fibrous membrane without ibuprofen. In a chicken model of flexor digitorum profundus tendon surgery, the ibuprofen-loaded PELA fibrous membranes prevented tissue adhesion and significantly reduced inflammation. Taken together, these results demonstrate that ibuprofen-loaded PELA fibrous membranes prevent peritendinous adhesion formation better than membranes that do not contain ibuprofen, through anti-adhesion and anti-inflammatory actions.

The application of electrospun titania nanofibers in dye-sensitized solar cells.

PubMed

Krysova, Hana; Zukal, Arnost; Trckova-Barakova, Jana; Chandiran, Aravind Kumar; Nazeeruddin, Mohammad Khaja; Grätzel, Michael; Kavan, Ladislav

2013-01-01

Titania nanofibers were fabricated using the industrial Nanospider(TM) technology. The preparative protocol was optimized by screening various precursor materials to get pure anatase nanofibers. Composite films were prepared by mixing a commercial paste of nanocrystalline anatase particles with the electrospun nanofibers, which were shortened by milling. The composite films were sensitized by Ru-bipyridine dye (coded C106) and the solar conversion efficiency was tested in a dye-sensitized solar cell filled with iodide-based electrolyte solution (coded Z960). The solar conversion efficiency of a solar cell with the optimized composite electrode (η = 7.53% at AM 1.5 irradiation) outperforms that of a solar cell with pure nanoparticle film (η = 5.44%). Still larger improvement was found for lower light intensities. At 10% sun illumination, the best composite electrode showed η = 7.04%, referenced to that of pure nanoparticle film (η = 4.69%). There are non-monotonic relations between the film's surface area, dye sorption capacity and solar performance of nanofiber-containing composite films, but the beneficial effect of the nanofiber morphology for enhancement of the solar efficiency has been demonstrated.

A highly flexible piezoelectret-fiber pressure sensor based on highly aligned P(VDF-TrFE) electrospun fibers

NASA Astrophysics Data System (ADS)

Ke, Jun-Yi; Chu, Hsin-Jung; Hsu, Yu-Hsiang; Lee, Chih-Kung

2017-04-01

P(VDF-TrFE) is a ferroelectric material having a strong piezoelectric effect, a good chemical stability, chemical resistance and biocompatibility. Therefore, it is suitable for the development of flexible pressure sensors in biological applications. Using electrospinning method and a drum collector, P(VDF-TrFE) nanofibers are aligned and formed an ultrathin film sheet with a thickness of 15 to 30 μm. A 140 °C annealing process and a corona discharge poling process are conducted to increase the performance of β phase piezoelectricity. Based on this technology, a highly flexible piezoelectret pressure sensor is developed for measuring muscle movement on the surface of human body. The orientation of electrospun P(VDFTrFE) fibers and poling direction are studied to enhance the sensitivity of the piezoelectret-fiber pressure sensor. Preliminary study shows that the sensitivity of piezoelectret-fiber pressure sensor can be 110.37 pC/Pa with a high signal to noise ratio. Sensor design, experimental studies, and biological application are detailed in this paper.

Highly Efficient Electronic Sensitization of Non-oxidized Graphene Flakes on Controlled Pore-loaded WO3 Nanofibers for Selective Detection of H2S Molecules

PubMed Central

Choi, Seon–Jin; Choi, Chanyong; Kim, Sang-Joon; Cho, Hee-Jin; Hakim, Meggie; Jeon, Seokwoo; Kim, Il–Doo

2015-01-01

Tailoring of semiconducting metal oxide nanostructures, which possess controlled pore size and concentration, is of great value to accurately detect various volatile organic compounds in exhaled breath, which act as potential biomarkers for many health conditions. In this work, we have developed a very simple and robust route for controlling both the size and distribution of spherical pores in electrospun WO3 nanofibers (NFs) via a sacrificial templating route using polystyrene colloids with different diameters (200 nm and 500 nm). A tentacle-like structure with randomly distributed pores on the surface of electrospun WO3 NFs were achieved, which exhibited improved surface area as well as porosity. Porous WO3 NFs with enhanced surface area exhibited high gas response (Rair/Rgas = 43.1 at 5 ppm) towards small and light H2S molecules. In contrast, porous WO3 NFs with maximized pore diameter showed a high response (Rair/Rgas = 2.8 at 5 ppm) towards large and heavy acetone molecules. Further enhanced sensing performance (Rair/Rgas = 65.6 at 5 ppm H2S) was achieved by functionalizing porous WO3 NFs with 0.1 wt% non-oxidized graphene (NOGR) flakes by forming a Schottky barrier (ΔΦ = 0.11) at the junction between the WO3 NFs (Φ = 4.56 eV) and NOGR flakes (Φ = 4.67 eV), which showed high potential for the diagnosis of halitosis. PMID:25626399

Electrospinning chitosan/poly(ethylene oxide) solutions with essential oils: Correlating solution rheology to nanofiber formation.

PubMed

Rieger, Katrina A; Birch, Nathan P; Schiffman, Jessica D

2016-03-30

Electrospinning hydrophilic nanofiber mats that deliver hydrophobic agents would enable the development of new therapeutic wound dressings. However, the correlation between precursor solution properties and nanofiber morphology for polymer solutions electrospun with or without hydrophobic oils has not yet been demonstrated. Here, cinnamaldehyde (CIN) and hydrocinnamic alcohol (H-CIN) were electrospun in chitosan (CS)/poly(ethylene oxide) (PEO) nanofiber mats as a function of CS molecular weight and degree of acetylation (DA). Viscosity stress sweeps determined how the oils affected solution viscosity and chain entanglement (Ce) concentration. Experimentally, the maximum polymer:oil mass ratio electrospun was 1:3 and 1:6 for CS/PEO:CIN and:H-CIN, respectively; a higher chitosan DA increased the incorporation of H-CIN only. The correlations determined for electrospinning plant-derived oils could potentially be applied to other hydrophobic molecules, thus broadening the delivery of therapeutics from electrospun nanofiber mats. Copyright © 2015 Elsevier Ltd. All rights reserved.

Molecular orientation in aligned electrospun polyimide nanofibers by polarized FT-IR spectroscopy.

PubMed

Yang, Haoqi; Jiang, Shaohua; Fang, Hong; Hu, Xiaowu; Duan, Gaigai; Hou, Haoqing

2018-07-05

Quantitative explanation on the improved mechanical properties of aligned electrospun polyimide (PI) nanofibers as the increased imidization temperatures is highly required. In this work, polarized FT-IR spectroscopy is applied to solve this problem. Based on the polarized FT-IR spectroscopy and the molecular model in the fibers, the length of the repeat unit of PI molecule, the angle between the fiber axis and the symmetric stretching direction of carbonyl group on the imide ring, and the angle between the PI molecular axis and fiber axis are all investigated. The Mark-Howink equation is used to calculate the number-average molar mass of PI molecules. The orientation states of PI molecules in the electrospun nanofibers are studied from the number-average molar mass of PI molecules and the average fiber diameter. Quantitative analysis of the orientation factor of PI molecules in the electrospun nanofibers is performed by polarized FT-IR spectroscopy. Copyright © 2018 Elsevier B.V. All rights reserved.

Biomimetic and bioactive nanofibrous scaffolds from electrospun composite nanofibers

PubMed Central

Zhang, YZ; Su, B; Venugopal, J; Ramakrishna, S; Lim, CT

2007-01-01

Electrospinning is an enabling technology that can architecturally (in terms of geometry, morphology or topography) and biochemically fabricate engineered cellular scaffolds that mimic the native extracellular matrix (ECM). This is especially important and forms one of the essential paradigms in the area of tissue engineering. While biomimesis of the physical dimensions of native ECM’s major constituents (eg, collagen) is no longer a fabrication-related challenge in tissue engineering research, conveying bioactivity to electrospun nanofibrous structures will determine the efficiency of utilizing electrospun nanofibers for regenerating biologically functional tissues. This can certainly be achieved through developing composite nanofibers. This article gives a brief overview on the current development and application status of employing electrospun composite nanofibers for constructing biomimetic and bioactive tissue scaffolds. Considering that composites consist of at least two material components and phases, this review details three different configurations of nanofibrous composite structures by using hybridizing basic binary material systems as example. These are components blended composite nanofiber, core-shell structured composite nanofiber, and nanofibrous mingled structure. PMID:18203429

Prediction of thermal conductivity of polyvinylpyrrolidone (PVP) electrospun nanocomposite fibers using artificial neural network and prey-predator algorithm.

PubMed

Khan, Waseem S; Hamadneh, Nawaf N; Khan, Waqar A

2017-01-01

In this study, multilayer perception neural network (MLPNN) was employed to predict thermal conductivity of PVP electrospun nanocomposite fibers with multiwalled carbon nanotubes (MWCNTs) and Nickel Zinc ferrites [(Ni0.6Zn0.4) Fe2O4]. This is the second attempt on the application of MLPNN with prey predator algorithm for the prediction of thermal conductivity of PVP electrospun nanocomposite fibers. The prey predator algorithm was used to train the neural networks to find the best models. The best models have the minimal of sum squared error between the experimental testing data and the corresponding models results. The minimal error was found to be 0.0028 for MWCNTs model and 0.00199 for Ni-Zn ferrites model. The predicted artificial neural networks (ANNs) responses were analyzed statistically using z-test, correlation coefficient, and the error functions for both inclusions. The predicted ANN responses for PVP electrospun nanocomposite fibers were compared with the experimental data and were found in good agreement.

Synthesis and characterization of curcumin loaded PLA-Hyperbranched polyglycerol electrospun blend for wound dressing applications.

PubMed

Perumal, Govindaraj; Pappuru, Sreenath; Chakraborty, Debashis; Maya Nandkumar, A; Chand, Dillip Kumar; Doble, Mukesh

2017-07-01

This study is aimed to develop curcumin (Cur) incorporated electrospun nanofibers of a blend of poly (lactic acid) (PLA) and hyperbranched polyglycerol (HPG) for wound healing applications. Both the polymers are synthesized and fabricated by electrospinning technique. The produced nanofibers were characterized by Scanning Electron Microscopy (SEM), X-Ray Diffraction (XRD), Fourier Transform Infrared Spectroscopy (FT-IR), Differential Scanning Colorimetry (DSC) and Thermogravimetric Analysis (TGA). Electrospun scaffolds (PLA/HPG/Cur) exhibits very high hydrophilicity, high swelling and drug uptake and promotes better cell viability, adhesion and proliferation when compared to PLA/Cur electrospun nanofibers. Biodegradation study revealed that the morphology of the nanofibers were unaffected even after 14days immersion in Phosphate Buffered Saline. In vitro scratch assay indicates that migration of the cells in the scratch treated with PLA/HPG/Cur is complete within 36h. These results suggest that PLA/HPG/Cur nanofibers can be a potential wound patch dressing for acute and chronic wound applications. Copyright © 2017 Elsevier B.V. All rights reserved.

Combining cell sheet technology and electrospun scaffolding for engineered tubular, aligned, and contractile blood vessels.

PubMed

Rayatpisheh, Shahrzad; Heath, Daniel E; Shakouri, Amir; Rujitanaroj, Pim-On; Chew, Sing Yian; Chan-Park, Mary B

2014-03-01

Herein we combine cell sheet technology and electrospun scaffolding to rapidly generate circumferentially aligned tubular constructs of human aortic smooth muscles cells with contractile gene expression for use as tissue engineered blood vessel media. Smooth muscle cells cultured on micropatterned and N-isopropylacrylamide-grafted (pNIPAm) polydimethylsiloxane (PDMS), a small portion of which was covered by aligned electrospun scaffolding, resulted in a single sheet of unidirectionally aligned cells. Upon cooling to room temperature, the scaffold, its adherent cells, and the remaining cell sheet detached and were collected on a mandrel to generating tubular constructs with circumferentially aligned smooth muscle cells which possess contractile gene expression and a single layer of electrospun scaffold as an analogue to a small diameter blood vessel's internal elastic lamina (IEL). This method improves cell sheet handling, results in rapid circumferential alignment of smooth muscle cells which immediately express contractile genes, and introduction of an analogue to small diameter blood vessel IEL. Copyright © 2013 Elsevier Ltd. All rights reserved.

Scaffold permeability as a means to determine fiber diameter and pore size of electrospun fibrinogen.

PubMed

Sell, Scott; Barnes, Catherine; Simpson, David; Bowlin, Gary

2008-04-01

The purpose of this study was to construct a flowmeter that could accurately measure the hydraulic permeability of electrospun fibrinogen scaffolds, providing insight into the transport properties of electrospun scaffolds while making the measurement of their topographical features (fiber diameter and pore size) more accurate. Three different concentrations of fibrinogen were used (100, 120, and 150 mg/mL) to create scaffolds with three different fiber diameters and pore sizes. The fiber diameters and pore sizes of the electrospun scaffolds were first analyzed with scanning electron microscopy and image analysis software. The permeability of each scaffold was measured with the flowmeter and used to calculate permeability-based fiber diameters and pore sizes, which were compared to values obtained through image analysis. Permeability measurement revealed scaffold permeability to increase with fibrinogen concentration, much like average fiber diameter and pore size. Comparison between the two measurement methods demonstrated the efficacy of the flowmeter as a way to measure scaffold features. Copyright 2007 Wiley Periodicals, Inc.

Living nanofiber yarn-based woven biotextiles for tendon tissue engineering using cell tri-culture and mechanical stimulation.

PubMed

Wu, Shaohua; Wang, Ying; Streubel, Philipp N; Duan, Bin

2017-10-15

Non-woven nanofibrous scaffolds have been developed for tendon graft application by using electrospinning strategies. However, electrospun nanofibrous scaffolds face some obstacles and limitations, including suboptimal scaffold structure, weak tensile and suture-retention strengths, and compact structure for cell infiltration. In this work, a novel nanofibrous, woven biotextile, fabricated based on electrospun nanofiber yarns, was implemented as a tissue engineered tendon scaffold. Based on our modified electrospinning setup, polycaprolactone (PCL) nanofiber yarns were fabricated with reproducible quality, and were further processed into plain-weaving fabrics interlaced with polylactic acid (PLA) multifilaments. Nonwoven nanofibrous PCL meshes with random or aligned fiber structures were generated using typical electrospinning as comparative counterparts. The woven fabrics contained 3D aligned microstructures with significantly larger pore size and obviously enhanced tensile mechanical properties than their nonwoven counterparts. The biological results revealed that cell proliferation and infiltration, along with the expression of tendon-specific genes by human adipose derived mesenchymal stem cells (HADMSC) and human tenocytes (HT), were significantly enhanced on the woven fabrics compared with those on randomly-oriented or aligned nanofiber meshes. Co-cultures of HADMSC with HT or human umbilical vein endothelial cells (HUVEC) on woven fabrics significantly upregulated the functional expression of most tenogenic markers. HADMSC/HT/HUVEC tri-culture on woven fabrics showed the highest upregulation of most tendon-associated markers than all the other mono- and co-culture groups. Furthermore, we conditioned the tri-cultured constructs with dynamic conditioning and demonstrated that dynamic stretch promoted total collagen secretion and tenogenic differentiation. Our nanofiber yarn-based biotextiles have significant potential to be used as engineered scaffolds to synergize the multiple cell interaction and mechanical stimulation for promoting tendon regeneration. Tendon grafts are essential for the treatment of various tendon-related conditions due to the inherently poor healing capacity of native tendon tissues. In this study, we combined electrospun nanofiber yarns with textile manufacturing strategies to fabricate nanofibrous woven biotextiles with hierarchical features, aligned fibrous topography, and sufficient mechanical properties as tendon tissue engineered scaffolds. Comparing to traditional electrospun random or aligned meshes, our novel nanofibrous woven fabrics possess strong tensile and suture-retention strengths and larger pore size. We also demonstrated that the incorporation of tendon cells and vascular cells promoted the tenogenic differentiation of the engineered tendon constructs, especially under dynamic stretch. This study not only presents a novel tissue engineered tendon scaffold fabrication technique but also provides a useful strategy to promote tendon differentiation and regeneration. Copyright © 2017 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

Investigating the potential of electrospun gelatin and collagen scaffolds for tissue engineering applications

NASA Astrophysics Data System (ADS)

Sisson, Kristin M.

Electrospinning provides an avenue to explore tissue engineering with the ability to produce nano- and micro-sized fibers in a non-woven construct with properties ideal for a tissue engineered scaffold including: small diameter fibers, which create a large surface to volume ratio, and an interconnected porous network that enables cell migration, good mechanical integrity and a three-dimensional structure. A tissue engineered scaffold also must be biocompatible, biodegradable, non-toxic and able to be sterilized. All of these requirements can be satisfied by choosing an appropriate polymer and solvent system for electrospinning. The main objective of this research is to create a non-toxic, flat, bone tissue engineered scaffold to place into a non-immune compromised mouse. The current bone tissue repair and replacement methodologies include using metal and ceramic replacements or autologous and autogenous bone grafts. Each of these has its own set of disadvantages. Autologous grafts are bone harvested in one location in a patient and used in another location. This procedure is expensive, often results in pain and infection at the replacement site, and the actual harvesting procedure can cause problems for the patient. Autogenous grafts are bone harvested in one patient and used in another patient. The shortcomings include low donor availability and the possibility of rejection of the implant. The other options include using metal and ceramics to create replacement bone. However, metals provide good mechanical stability but can fail due to infection and also have poor integration into natural tissue. Ceramics, on the other hand, are brittle and have very low tensile strength. The natural extracellular matrix (ECM) of bone consists mainly of collagen type I. Electrospun fiber diameters closely resemble those of the natural ECM of bone. Thus, electrospinning a natural polymer like collagen type I for bone tissue engineering could make sense. Applications for these electrospun tissue engineered scaffolds include flat bone repair (skull, scapula, pelvis and sternum) or replacement applications. In order to meet the main objective, several critical milestones must be completed. The first is to develop an electrospinning system that uses less toxic solvents. Until recently, fluorinated solvents have been used to electrospin collagen and gelatin. These fluorinated solvents are cytotoxic and, even with vacuum drying and extensive washing, these toxic solvents may remain in the electrospun scaffolds. A solvent system using less toxic, non-fluorinated solvents to electrospin collagen and gelatin is necessary. Due to the high expense of collagen type I, gelatin is being used as a material substitute since gelatin is simply denatured collagen. Gelatin, like collagen, will dissolve in aqueous media unless it is crosslinked. The chemical generally used for crosslinking gelatin is glutaraldehyde, which is considered toxic. Therefore, the second objective is to find a less toxic method to crosslink the electrospun gelatin while maintaining the fiber morphology. The new crosslinking methods must also prove to be biocompatible in vivo. Another important objective is to investigate cell penetration as a function of fiber size, which is directly proportional to pore size. The final objective involves growing bone cells such as MG63 (osteoblast-like) in the electrospun scaffolds and compare to two-dimensional culture.

Electrospun nanofibers: Formation, characterization, and evaluation for nerve tissue engineering applications

NASA Astrophysics Data System (ADS)

Zander, Nicole E.

The effects of fiber alignment and surface chemistry, including the covalent attachment and physical adsorption of the extracellular matrix (ECM) proteins laminin and collagen, on the neurite outgrowth of neuron-like PC12 cells were examined. Neuron-like PC12 cells responded to fiber orientation, and were successfully contact-guided by aligned electrospun nanofibers. In addition, fibers with attached protein, either physically adsorbed or covalently attached, improved neurite outgrowth lengths. Furthermore, aligning the fibers and attaching the ECM protein laminin, in particular, significantly improved neurite outgrowth over randomly oriented fibers with laminin. Since this research suggested that protein concentration on the fibers was the dominant driving force for improved neurite outgrowth, the effect of protein concentration, incorporated onto the surface of the nanofibers, on neurite outgrowth was examined. Two ways to control protein concentration on the fibers were explored—the variation of the fiber-protein reaction time and the variation of the protein soaking solution concentration. In addition, analytical methods to quantify the concentration of protein, as well as the protein coverage, on the surface of the fibers were developed. Although most of the fiber mats had multilayer protein coverage, and hence physically adsorbed proteins which could potentially mean a loss in bioactivity, the neuron-like PC12 cell neurites responded in a dose-dependent manner with increased neurite lengths on scaffolds with higher protein concentrations. The work was extended further by forming protein gradients on the fiber mats in hopes of locally directing neurite outgrowth and orientation. Fiber mats with both linear gradients (continuous change in protein concentration) and step gradients (six regions of uniform protein coverage, with protein concentration increasing from region to region) were fabricated and analyzed. The step gradients formed in the aligned fiber direction showed the most promise for use in cell culture assays. While surface chemistry and topography are important, porosity of the scaffold is also critical to control cellular infiltration and tissue formation. To enhance the porosity of our electrospun nanofiber scaffolds and improve the infiltration of cells, two methods were explored to control porosity. In the first method, the scaffold polymer polycaprolactone was co-electrospun with a sacrificial polymer polyethylene oxide, which was removed after the bi-component fiber mat was formed. In doing so, the void space was increased. In the second method, the spinning solution concentration of polycaprolactone was varied to control fiber diameter and porosity. The second method proved to be more effective at improving the cellular infiltration of PC12 cells. Two orders of magnitude range of fiber diameters were achieved, and nearly full infiltration of PC12 cells was observed for the mats with the highest porosity. The pore sizes of these mats were on the order of the size of the cell bodies (approximately 6-10 µm). Although the majority of this work focuses on using conventional electrospinning to generate solid-core fibers, core-shell fibers, have many applications in tissue engineering, among other fields. We explored an efficient way to generate these fibers from an emulsion solution using a conventional electrospinning apparatus. We characterized the fibers using an atomic force microscope (AFM) elastic modulus mapping technique, along with AFM phase imaging, angle-resolved x-ray photoelectron spectroscopy and thermal gravimetric analysis, to determine the chemical and molar composition of the core and shell layers. This work presents novel analytical techniques for the characterization of core-shell nanofibers in order to better predict and understand their material properties. (Abstract shortened by UMI.).

Study on structure, mechanical property and cell cytocompatibility of electrospun collagen nanofibers crosslinked by common agents.

PubMed

Luo, Xueshi; Guo, Zhenzhao; He, Ping; Chen, Tian; Li, Lihua; Ding, Shan; Li, Hong

2018-07-01

Collagen electrospun scaffolds properly reproduce the framework of the extracellular matrix (ECM) of tissues that are natural with the fibrous morphology of the protein by coupling large biomimetism of the biological material. However, traditional solvents employed for collagen electrospinning lead to poor mechanical attributes and bad hydro-stability. In this work, by N-(3-dimethylaminopropyl)-N'-ethylcarbodiimide hydrochloride with N-hydroxysulfosuccinimide (EDC-NHS), glutaraldehyde (GTA) and genipin (GP) respectively, electrospun collagen fibers cross-linked, effectively stabilized the fiber morphology over 2months and improved the mechanical properties in both dry and wet state, especially EDC-NHS with large ultimate tensile stress and ε b . The secondary structure of collagen structure still remained and had no obvious difference among various crosslinked samples according to FTIR. On the cell assessment, electrospun collagen fibers crosslinked by EDC-NHS, GTA and GP, were found to support cell adhesion, spreading and proliferation of MC3T3-E1. By contrast, GTA was more effective in preserving explicit fibrous morphology with a relatively lower cell viability both in FBS and BSA soaked mats. Interestingly, GP also had the similar cytocompatibility of MC3T3-E1 as EDC-NHS did. The study proved the feasibility of chemical crosslinker to electrospun collagen for biomedical application. Copyright © 2018. Published by Elsevier B.V.

Effect of clay content on morphology and processability of electrospun keratin/poly(lactic acid) nanofiber.

PubMed

Isarankura Na Ayutthaya, Siriorn; Tanpichai, Supachok; Sangkhun, Weradesh; Wootthikanokkhan, Jatuphorn

2016-04-01

This research work has concerned the development of volatile organic compounds (VOCs) removal filters from biomaterials, based on keratin extracted from chicken feather waste and poly(lactic acid) (PLA) (50/50%w/w) blend. Clay (Na-montmorillonite) was also added to the blend solution prior to carrying out an electro-spinning process. The aim of this study was to investigate the effect of clay content on viscosity, conductivity, and morphology of the electrospun fibers. Scanning electron micrographs showed that smooth and bead-free fibers were obtained when clay content used was below 2 pph. XRD patterns of the electrospun fibers indicated that the clay was intercalated and exfoliated within the polymers matrix. Percentage crystallinity of keratin in the blend increased after adding the clay, as evidenced from FTIR spectra and DSC thermograms. Transmission electron micrographs revealed a kind of core-shell structure with clay being predominately resided within the keratin rich shell and at the interfacial region. Filtration performance of the electrospun keratin/PLA fibers, described in terms of pressure drop and its capability of removing methylene blue, were also explored. Overall, our results demonstrated that it was possible to improve process-ability, morphology and filtration efficiency of the electrospun keratin fibers by adding a suitable amount of clay. Copyright © 2016 Elsevier B.V. All rights reserved.

Understanding Polymorphism Formation in Electrospun Fibers of Immiscible Poly(vinylidene fluoride) Blends

DOE Office of Scientific and Technical Information (OSTI.GOV)

G Zhong; L Zhang; R Su

2011-12-31

Effects of electric poling, mechanical stretching, and dipolar interaction on the formation of ferroelectric ({beta} and/or {gamma}) phases in poly(vinylidene fluoride) (PVDF) have been studied in electrospun fibers of PVDF/polyacrylonitrile (PAN) and PVDF/polysulfone (PSF) blends with PVDF as the minor component, using wide-angle X-ray diffraction and Fourier transform infrared techniques. Experimental results of as-electrospun neat PVDF fibers (beaded vs. bead-free) showed that mechanical stretching during electrospinning, rather than electric poling, was effective to induce ferroelectric phases. For as-electrospun PVDF blend fibers with the non-polar PSF matrix, mechanical stretching during electrospinning again was capable of inducing some ferroelectric phases in additionmore » to the major paraelectric ({alpha}) phase. However, after removing the mechanical stretching in a confined melt-recrystallization process, only the paraelectric phase was obtained. For as-electrospun PVDF blend fibers with the polar (or ferroelectric) PAN matrix, strong intermolecular interactions between polar PAN and PVDF played an important role in the ferroelectric phase formation in addition to the mechanical stretching effect during electrospinning. Even after the removal of mechanical stretching through the confined melt-recrystallization process, a significant amount of ferroelectric phases persisted. Comparing the ferroelectric phase formation between PVDF/PSF and PVDF/PAN blend fibers, we concluded that the local electric field-dipole interactions were the determining factor for the nucleation and growth of polar PVDF phases.« less

Oil-in-water emulsion impregnated electrospun poly(ethylene terephthalate) fiber mat as a novel tool for optical fiber cleaning.

PubMed

Devlaminck, Dries J G; Rahman, Md Mahbubor; Dash, Mamoni; Samal, Sangram Keshari; Watté, Jan; Van Vlierberghe, Sandra; Dubruel, Peter

2018-06-15

The complete removal of remaining polymer debris after stripping of optical fiber cables is essential for high precision connection between two fibers. It can be anticipated that electrospun porous membranes as cleaning wipes are able to trap and retain polymer debris within their pores. Impregnation of an oil-in-water emulsion as cleaning agent lowers the interfacial tension between debris and the optical fiber thereby enabling the straightforward removal of polymer debris from the optical fiber. Electrospun membranes of poly(ethylene terephthalate) (PET) and cellulose acetate (CA) were obtained with fiber diameters of 0.430 μm and 2 μm respectively. The oil-in-water emulsion was formulated with 10 wt% medium chain triglyceride (MCT) and 10 wt% Tween 80 surfactant in an aqueous phosphate buffer solution. In a scoring range from 0 to 5 for which the score 0 indicated superior cleaning and the score 5 referred to the least efficient cleaning, the electrospun fiber mats (without emulsion) scored within the range of 2-4 while emulsion impregnated electrospun fiber mats revealed the best score of 0. A drastic improvement was thus clearly evident from the obtained results when the cleaning emulsion was applied. The materials developed herein thus represent a new class of soft cleaning agents for optical fibers. Copyright © 2018 Elsevier Inc. All rights reserved.

Catalytic property of fiber media supported palladium containing alloy nanoparticles and electrospun ceramic fibers biodurability study

NASA Astrophysics Data System (ADS)

Shin, Hyeon Ung

The nanoscale of the supporting fibers may provide enhancements such as restricting the migration of metal catalyst particles. In this work, palladium nanoparticle doped alumina fibers were electrospun into template submicron fibers. These fibers were calcined at temperatures between 650°C and 1150°C to vary the crystal structures of the calcined fibers with the Pd particle size. Higher calcination temperatures led to higher reaction temperatures from 250 to about 450°C for total conversion, indicating the effective reactivity of the fiber-supported catalysts decreased with increase in calcination temperature. Pd-Au alloy nanoparticle doped titania fibers were also fabricated using an electrospinning method and assembled into a fibrous porous medium structure by a vacuum molding process. In reactor tests, the fiber media with Pd-Au alloy nanoparticle catalyst had greater reactivity in conversion of NO and CO gases than that of fiber media with Pd monometallic catalyst alone, attributed to a lower activation energy of the Pd-Au catalyst particles. In carbon monoxide oxidation reaction tests, the results showed that the performance was optimal for a catalyst of composition Pd2Au1 molar ratio that was active at 125°C, which had higher dispersion of active components and better catalytic performance compared to monometallic particle Au/TiO 2 and Pd/TiO2 fiber media. Moreover, the improved reaction activity of Pd2Au1/TiO2 fiber medium was attributed to a decreased in the activation energy. Further experiments were conducted using the electrospun ceramic fibers biodurability study. The properties of nano-sized fiber structures have attracted the attention of recent research on ceramic nanostructures as nonwoven media for applications in hazardous chemical and high temperature environments. However, health and safety concerns of micro and nano scale ceramic materials have not been fully investigated. Little is known about the physicochemical effects of the properties of small alumina fibers, including fiber sizes, surface morphologies, crystalline, phases, and surface areas with respect to submicron sized alumina fibers formed by calcination of electrospun polymeric fibers. Therefore, in this work, sub-micron sized alumina fibers were fabricated by electrospinning and calcination of a polymer template fiber. In the calcination step, different controlled temperature heating cycles were conducted to obtain fibers of different crystalline structures. Their biodurabilities were evaluated in two types of artificial lung fluids (i.e., mimicking the airway and alveolar macrophages). Though the variation in the soak temperature, their dissolution half times were not significantly affected. The solubility half-times of the alumina fibers were shortest for fibers calcined at the fastest temperature ramp rate (though soak temperature did not have an effect).

Electrospinning of poly(glycerol sebacate)-based nanofibers for nerve tissue engineering.

PubMed

Hu, Jue; Kai, Dan; Ye, Hongye; Tian, Lingling; Ding, Xin; Ramakrishna, Seeram; Loh, Xian Jun

2017-01-01

Nerve tissue engineering (TE) requires biomimetic scaffolds providing essential chemical and topographical cues for nerve regeneration. Poly(glycerol sebacate) (PGS) is a biodegradable and elastic polymer that has gained great interest as a TE scaffolding biomaterial. However, uncured PGS is difficult to be electrospun into nanofibers. PGS would, therefore, require the addition of electrospinning agents. In this study, we modified PGS by using atom transfer radical polymerization (ATRP) to synthesize PGS-based copolymers with methyl methacrylate (MMA). The synthesized PGS-PMMA copolymer showed a molecular weight of 82kDa and a glass transition temperature of 115°C. More importantly, the PGS-PMMA could be easily electrospun into nanofiber with a fiber diameter of 167±33nm. Blending gelatin into PGS-PMMA nanofibers was found to increase its hydrophilicity and biocompatibility. Rat PC12 cells were seeded onto the PGS-PMMA/gelatin nanofibers to investigate their potential for nerve regeneration. It was found that gelatin-containing PGS-based nanofibers promoted cell proliferation. The elongated cell morphology observed on such nanofibers indicated that the scaffolds could induce the neurite outgrowth of the nerve stem cells. Overall, our study suggested that the synthesis of PGS-based copolymers might be a promising approach to enhance their processability, and therefore advancing bioscaffold engineering for various TE applications. Copyright © 2016 Elsevier B.V. All rights reserved.

New Amniotic Membrane Based Biocomposite for Future Application in Reconstructive Urology

PubMed Central

Tworkiewicz, Jakub; Kowalczyk, Tomasz; van Breda, Shane V.; Tyloch, Dominik; Kloskowski, Tomasz; Bodnar, Magda; Skopinska-Wisniewska, Joanna; Marszałek, Andrzej; Frontczak-Baniewicz, Malgorzata; Kowalewski, Tomasz A.; Drewa, Tomasz

2016-01-01

Objective Due to the capacity of the amniotic membrane (Am) to support re-epithelisation and inhibit scar formation, Am has a potential to become a considerable asset for reconstructive urology i.e., reconstruction of ureters and urethrae. The application of Am in reconstructive urology is limited due to a poor mechanical characteristic. Am reinforcement with electrospun nanofibers offers a new strategy to improve Am mechanical resistance, without affecting its unique bioactivity profile. This study evaluated biocomposite material composed of Am and nanofibers as a graft for urinary bladder augmentation in a rat model. Material and Methods Sandwich-structured biocomposite material was constructed from frozen Am and covered on both sides with two-layered membranes prepared from electrospun poly-(L-lactide-co-E-caprolactone) (PLCL). Wistar rats underwent hemicystectomy and bladder augmentation with the biocomposite material. Results Immunohistohemical analysis (hematoxylin and eosin [H&E], anti-smoothelin and Masson’s trichrome staining [TRI]) revealed effective regeneration of the urothelial and smooth muscle layers. Anti-smoothelin staining confirmed the presence of contractile smooth muscle within a new bladder wall. Sandwich-structured biocomposite graft material was designed to regenerate the urinary bladder wall, fulfilling the requirements for normal bladder tension, contraction, elasticity and compliance. Mechanical evaluation of regenerated bladder wall conducted based on Young’s elastic modulus reflected changes in the histological remodeling of the augmented part of the bladder. The structure of the biocomposite material made it possible to deliver an intact Am to the area for regeneration. An unmodified Am surface supported regeneration of the urinary bladder wall and the PLCL membranes did not disturb the regeneration process. Conclusions Am reinforcement with electrospun nanofibers offers a new strategy to improve Am mechanical resistance without affecting its unique bioactivity profile. PMID:26766636

Electrospun Nanofiber Scaffolds and Their Hydrogel Composites for the Engineering and Regeneration of Soft Tissues.

PubMed

Manoukian, Ohan S; Matta, Rita; Letendre, Justin; Collins, Paige; Mazzocca, Augustus D; Kumbar, Sangamesh G

2017-01-01

Electrospinning has emerged as a simple, elegant, and scalable technique that can be used to fabricate polymeric nanofibers. Pure polymers as well as blends and composites of both natural and synthetic ones have been successfully electrospun into nanofiber matrices for many biomedical applications. Tissue-engineered medical implants, such as polymeric nanofiber scaffolds, are potential alternatives to autografts and allografts, which are short in supply and carry risks of disease transmission. These scaffolds have been used to engineer various soft tissues, including connective tissues, such as skin, ligament, and tendon, as well as nonconnective ones, such as vascular, muscle, and neural tissue. Electrospun nanofiber matrices show morphological similarities to the natural extracellular matrix (ECM), characterized by ultrafine continuous fibers, high surface-to-volume ratios, high porosities, and variable pore-size distributions. The physiochemical properties of nanofiber matrices can be controlled by manipulating electrospinning parameters so that they meet the requirements of a specific application.Nanostructured implants show improved biological performance over bulk materials in aspects of cellular infiltration and in vivo integration, taking advantage of unique quantum, physical, and atomic properties. Furthermore, the topographies of such scaffolds has been shown to dictate cellular attachment, migration, proliferation, and differentiation, which are critical in engineering complex functional tissues with improved biocompatibility and functional performance. This chapter discusses the use of the electrospinning technique in the fabrication of polymer nanofiber scaffolds utilized for the regeneration of soft tissues. Selected scaffolds will be seeded with human mesenchymal stem cells (hMSCs), imaged using scanning electron and confocal microscopy, and then evaluated for their mechanical properties as well as their abilities to promote cell adhesion, proliferation , migration, and differentiation.

Effect of Processing Parameters on the Morphology of PVDF Electrospun Nanofiber

NASA Astrophysics Data System (ADS)

Zulfikar, M. A.; Afrianingsih, I.; Nasir, M.; Alni, A.

2018-03-01

Electrospinning is a process that produces continuous polymer fibers with diameters in the submicron range through the action of an external electric field imposed on a polymer solution or melt. Because of the tiny diameter in several hundreds of nanometers and the high porosity, electrospun membranes show potential applications in extensive areas such as filtration systems, biomedical tissue templates, drug delivery membranes, and so on. In the electrospinning process, some parameters such as polymer concentration, feeding rate of the polymer solution, additives, humidity, viscosity, surface tension, applied voltage, and nozzle-to ground collector distance will affect the fiber diameter and morphology. In this work, we have evaluated the effects of two processing parameters including the flow rate of the polymer solution and nozzle-to ground collector distance, on the morphology of the fibers formed. The solutions used in the electrospinning experiments were prepared using Poly(vinylidene fluoride) (PVDF). This material was dissolved in N,N-dimethylformamide (DMF) to make solutions with concentrations of 20 wt%. These solutions was electrospun using a 5 mL plastic syringe with an 8 gauge stainless needle at an applied voltage of 20.0 kV, a flow rate of 0.02-0.04 mL/min and nozzle-to ground collector distance of 12 and 15 cm. Electrospinning of PVDF polymer solution was performed in horizontal alignment having a grounded aluminum foil which serves as a collector. The nanofibers obtained were characterized by polarizing optical microscope. We find that the low flow rate of the polymer solution and nozzle-to ground collector distance are strongly correlated with the formation of bead defects in the fibers.

Sustained release of bactericidal concentrations of penicillin in the pleural space via an antibiotic-eluting pigtail catheter coated with electrospun nanofibers: results from in vivo and in vitro studies.

PubMed

Chao, Yin-Kai; Lee, Cheng-Hung; Liu, Kuo-Sheng; Wang, Yi-Chuan; Wang, Chih-Wei; Liu, Shih-Jung

2015-01-01

Inadequate intrapleural drug concentrations caused by poor penetration of systemic antibiotics into the pleural cavity is a major cause of treatment failure in empyema. Herein, we describe a novel antibiotic-eluting pigtail catheter coated with electrospun nanofibers used for the sustained release of bactericidal concentrations of penicillin in the pleural space. Electrospun nanofibers prepared using polylactide-polyglycolide copolymer and penicillin G sodium dissolved in 1,1,1,3,3,3-hexafluoro-2-propanol were used to coat the surface of an Fr6 pigtail catheter. The in vitro patterns of drug release were tested by placing the catheter in phosphate-buffered saline. In vivo studies were performed using rabbits treated with penicillin either intrapleurally (Group 1, 20 mg delivered through the catheter) or systemically (Group 2, intramuscular injection, 10 mg/kg). Penicillin concentrations in the serum and pleural fluid were then measured and compared. In vitro studies revealed a burst release of penicillin (10% of the total dose) occurring in the first 24 hours, followed by a sustained release in the subsequent 30 days. Intrapleural drug levels were significantly higher in Group 1 than in Group 2 (P<0.001). In the former, penicillin concentrations remained above the minimum inhibitory concentration breakpoint throughout the entire study period. In contrast, serum penicillin levels were significantly higher in Group 2 than in Group 1 (P<0.001). Notably, all Group 2 rabbits showed signs of systemic toxicity (paralytic ileus and weight loss). We conclude that our antibiotic-eluting catheter may serve as a novel therapeutic option to treat empyema.

* Hierarchically Structured Electrospun Scaffolds with Chemically Conjugated Growth Factor for Ligament Tissue Engineering.

PubMed

Pauly, Hannah M; Sathy, Binulal N; Olvera, Dinorath; McCarthy, Helen O; Kelly, Daniel J; Popat, Ketul C; Dunne, Nicholas J; Haut Donahue, Tammy Lynn

2017-08-01

The anterior cruciate ligament (ACL) of the knee is vital for proper joint function and is commonly ruptured during sports injuries or car accidents. Due to a lack of intrinsic healing capacity and drawbacks with allografts and autografts, there is a need for a tissue-engineered ACL replacement. Our group has previously used aligned sheets of electrospun polycaprolactone nanofibers to develop solid cylindrical bundles of longitudinally aligned nanofibers. We have shown that these nanofiber bundles support cell proliferation and elongation and the hierarchical structure and material properties are similar to the native human ACL. It is possible to combine multiple nanofiber bundles to create a scaffold that attempts to mimic the macroscale structure of the ACL. The goal of this work was to develop a hierarchical bioactive scaffold for ligament tissue engineering using connective tissue growth factor (CTGF)-conjugated nanofiber bundles and evaluate the behavior of mesenchymal stem cells (MSCs) on these scaffolds in vitro and in vivo. CTGF was immobilized onto the surface of individual nanofiber bundles or scaffolds consisting of multiple nanofiber bundles. The conjugation efficiency and the release of conjugated CTGF were assessed using X-ray photoelectron spectroscopy, assays, and immunofluorescence staining. Scaffolds were seeded with MSCs and maintained in vitro for 7 days (individual nanofiber bundles), in vitro for 21 days (scaled-up scaffolds of 20 nanofiber bundles), or in vivo for 6 weeks (small scaffolds of 4 nanofiber bundles), and ligament-specific tissue formation was assessed in comparison to non-CTGF-conjugated control scaffolds. Results showed that CTGF conjugation encouraged cell proliferation and ligament-specific tissue formation in vitro and in vivo. The results suggest that hierarchical electrospun nanofiber bundles conjugated with CTGF are a scalable and bioactive scaffold for ACL tissue engineering.

Superhydrophobic materials for drug delivery

NASA Astrophysics Data System (ADS)

Yohe, Stefan Thomas

Superhydrophobicity is a property of material surfaces reflecting the ability to maintain air at the solid-liquid interface when in contact with water. These surfaces have characteristically high apparent contact angles, by definition exceeding 150°, as a result of the composite material-air surface formed under an applied water droplet. Superhydrophobic surfaces were first discovered on naturally occurring substrates, and have subsequently been fabricated in the last several decades to harness these favorable surface properties for a number of emerging applications, including their use in biomedical settings. This work describes fabrication and characterization of superhydrophobic 3D materials, as well as their use as drug delivery devices. Superhydrophobic 3D materials are distinct from 2D superhydrophobic surfaces in that air is maintained not just at the surface of the material, but also within the bulk. When the superhydrophobic 3D materials are submerged in water, water infiltrates slowly and continuously as a new water-air-material interface is formed with controlled displacement of air. Electrospinning and electrospraying are used to fabricate superhydrophobic 3D materials utilizing blends of the biocompatible polymers poly(epsilon-caprolactone) and poly(caprolactone-co-glycerol monostearate) (PGC-C18). PGC-C18 is significantly more hydrophobic than PCL (contact angle of 116° versus 83° for flat materials), and further additions of PGC-C18 into electrospun meshes and electrosprayed coatings affords increased stability of the entrapped air layer. For example, PCL meshes alone (500 mum thick) take 10 days to fully wet, and with 10% or 30% PGC-C18 addition wetting rates are dramatically slowed to 60% wetted by 77 days and 4% by 75 days, respectively. Stability of the superhydrophobic materials can be further probed with a variety of physio-chemical techniques, including pressure, surfactant containing solutions, and solvents of varying surface tension. Superhydrophobicity is shown to be enhanced with further increases in PGC-C18 content and surface roughness (a decrease in fiber size). We demonstrate the utility of superhydrophobicity as a method for drug delivery. When the camptothecin derivatives SN-38 and CPT-11 are encapsulated within electrospun meshes, changes in air layer stability (due to changes in PGC-C18 content) dictate the rate of drug release by controlling the rate in which water can permeate into the porous 3D electrospun structure. Drug release can be tuned from 2 weeks to >10 weeks from 300 mum meshes, and meshes effectively kill a variety of cancer cell lines (lung, colon, breast) when utilized in a cytotoxicity assay. After determining that air could be used to control the rate of drug release, superhydrophobic 3D materials are explored for three applications. First, meshes are considered as a potential combination reinforcement-drug delivery device for use in resectable colorectal cancer. Second, removal of the air layer in superhydrophobic meshes is used as a method to trigger drug release. The pressure generated from high-intensity focused ultrasound (0.75-4.25 MPa) can remove the air layer spatially and temporally, allowing drug release to be controlled with application of a sufficient treatment. Third, "connective" electrosprayed coatings are deposited on chemically distinct material surfaces, which are both three-dimensional and mechanically robust. In summary, superhydrophobic 3D materials are fabricated and characterized, and are utilized as drug delivery devices. Controlled air removal from these materials offers an entirely new strategy for drug delivery, and is promising for the applications considered in this work as well as many others.

Suspended, Shrinkage-Free, Electrospun PLGA Nanofibrous Scaffold for Skin Tissue Engineering.

PubMed

Ru, Changhai; Wang, Feilong; Pang, Ming; Sun, Lining; Chen, Ruihua; Sun, Yu

2015-05-27

Electrospinning is a technique for creating continuous nanofibrous networks that can architecturally be similar to the structure of extracellular matrix (ECM). However, the shrinkage of electrospun mats is unfavorable for the triggering of cell adhesion and further growth. In this work, electrospun PLGA nanofiber assemblies are utilized to create a scaffold. Aided by a polypropylene auxiliary supporter, the scaffold is able to maintain long-term integrity without dimensional shrinkage. This scaffold is also able to suspend in cell culture medium; hence, keratinocyte cells seeded on the scaffold are exposed to air as required in skin tissue engineering. Experiments also show that human skin keratinocytes can proliferate on the scaffold and infiltrate into the scaffold.

A high efficiency microfluidic-based photocatalytic microreactor using electrospun nanofibrous TiO2 as a photocatalyst

NASA Astrophysics Data System (ADS)

Meng, Zhaoxu; Zhang, Xu; Qin, Jianhua

2013-05-01

We present a novel microfluidic-based photocatalytic microreactor by using electrospun nanofibrous TiO2 as a photocatalyst for the first time. The microreactor exhibits not only a simple fabrication process, but also much higher photocatalytic activity than that achieved by a TiO2 film microreactor.We present a novel microfluidic-based photocatalytic microreactor by using electrospun nanofibrous TiO2 as a photocatalyst for the first time. The microreactor exhibits not only a simple fabrication process, but also much higher photocatalytic activity than that achieved by a TiO2 film microreactor. Electronic supplementary information (ESI) available. See DOI: 10.1039/c3nr00775h

Incorporation of ciprofloxacin/laponite in polycaprolactone electrospun nanofibers: drug release and antibacterial studies

NASA Astrophysics Data System (ADS)

Kalwar, Kaleemullah; Zhang, Xuan; Aqeel Bhutto, Muhammad; Dali, Li; Shan, Dan

2017-12-01

Electrospun nanofibers with sustained drug release are a challenge but it can be improved by using hydrophobic polymer. Polycaprolactone (PCL) is a hydrophobic and biocompatible polymer. In this work, we have proposed a drug release mechanism by preparation of ciprofloxacin (Cip)/Laponite (LAP) complex and then incorporation in PCL nanofibers through electrospinning technique. In addition, drug incorporation was confirmed by FTIR and morphology of electrospun nanofibers was revealed by SEM. Drug loading was measured by using spectrophotometer. PCL/LAP/Cip NFs proved sustained drug release as compared to PCL NFs and PCL/Cip NFs. Furthermore, PCL/LAP/Cip NFs were used as antimicrobial agent and higher effect measured.

Polarized emission from CsPbBr3 nanowire embedded-electrospun PU fibers

NASA Astrophysics Data System (ADS)

Güner, Tuğrul; Topçu, Gökhan; Savacı, Umut; Genç, Aziz; Turan, Servet; Sari, Emre; Demir, Mustafa M.

2018-04-01

Interest in all-inorganic halide perovskites has been increasing dramatically due to their high quantum yield, band gap tunability, and ease of fabrication in compositional and geometric diversity. In this study, we synthesized several hundreds of nanometer long and ˜4 nm thick CsPbBr 3 nanowires (NWs). They were then integrated into electrospun polyurethane (PU) fibers to examine the polarization behavior of the composite fiber assembly. Aligned electrospun fibers containing CsPbBr 3 NWs showed a remarkable increase in the degree of polarization from 0.17-0.30. This combination of NWs and PU fibers provides a promising composite material for various applications such as optoelectronic devices and solar cells.

A high efficiency microfluidic-based photocatalytic microreactor using electrospun nanofibrous TiO2 as a photocatalyst.

PubMed

Meng, Zhaoxu; Zhang, Xu; Qin, Jianhua

2013-06-07

We present a novel microfluidic-based photocatalytic microreactor by using electrospun nanofibrous TiO2 as a photocatalyst for the first time. The microreactor exhibits not only a simple fabrication process, but also much higher photocatalytic activity than that achieved by a TiO2 film microreactor.

Electrospun zein fibers using glyoxal as the cross-linking reagent

USDA-ARS?s Scientific Manuscript database

Glyoxal has been used to provide zein electrospun fibers that are resistant to dissolution by known zein solvents. Durable fibers with diameters between 0.2 and 0.7 micrometers could be produced. The reaction between zein and glyoxal was carried out in acetic acid at temperatures between 25 and 60...

A review of evolution of electrospun tissue engineering scaffold: From two dimensions to three dimensions.

PubMed

Ngadiman, Nor Hasrul Akhmal; Noordin, M Y; Idris, Ani; Kurniawan, Denni

2017-07-01

The potential of electrospinning process to fabricate ultrafine fibers as building blocks for tissue engineering scaffolds is well recognized. The scaffold construct produced by electrospinning process depends on the quality of the fibers. In electrospinning, material selection and parameter setting are among many factors that contribute to the quality of the ultrafine fibers, which eventually determine the performance of the tissue engineering scaffolds. The major challenge of conventional electrospun scaffolds is the nature of electrospinning process which can only produce two-dimensional electrospun mats, hence limiting their applications. Researchers have started to focus on overcoming this limitation by combining electrospinning with other techniques to fabricate three-dimensional scaffold constructs. This article reviews various polymeric materials and their composites/blends that have been successfully electrospun for tissue engineering scaffolds, their mechanical properties, and the various parameters settings that influence the fiber morphology. This review also highlights the secondary processes to electrospinning that have been used to develop three-dimensional tissue engineering scaffolds as well as the steps undertaken to overcome electrospinning limitations.

Preliminary investigation of airgap electrospun silk-fibroin-based structures for ligament analogue engineering.

PubMed

Sell, S A; McClure, M J; Ayres, C E; Simpson, D G; Bowlin, G L

2011-01-01

The process of electrospinning has proven to be highly beneficial for use in a number of tissue-engineering applications due to its ease of use, flexibility and tailorable properties. There have been many publications on the creation of aligned fibrous structures created through various forms of electrospinning, most involving the use of a metal target rotating at high speeds. This work focuses on the use of a variation known as airgap electrospinning, which does not use a metal collecting target but rather a pair of grounded electrodes equidistant from the charged polymer solution to create highly aligned 3D structures. This study involved a preliminary investigation and comparison of traditionally and airgap electrospun silk-fibroin-based ligament constructs. Structures were characterized with SEM and alignment FFT, and underwent porosity, permeability, and mechanical anisotropy evaluation. Preliminary cell culture with human dermal fibroblasts was performed to determine the degree of cellular orientation and penetration. Results showed airgap electrospun structures to be anisotropic with significantly increased porosity and cellular penetration compared to their traditionally electrospun counterparts.

Mechanical and transport properties of layer-by-layer electrospun composite proton exchange membranes for fuel cell applications.

PubMed

Mannarino, Matthew M; Liu, David S; Hammond, Paula T; Rutledge, Gregory C

2013-08-28

Composite membranes composed of highly conductive and selective layer-by-layer (LbL) films and electrospun fiber mats were fabricated and characterized for mechanical strength and electrochemical selectivity. The LbL component consists of a proton-conducting, methanol-blocking poly(diallyl dimethyl ammonium chloride)/sulfonated poly(2,6-dimethyl-1,4-phenylene oxide) (PDAC/sPPO) thin film. The electrospun fiber component consists of poly(trimethyl hexamethylene terephthalamide) (PA 6(3)T) fibers in a nonwoven mat of 60-90% porosity. The bare mats were annealed to improve their mechanical properties, which improvements are shown to be retained in the composite membranes. Spray LbL assembly was used as a means for the rapid formation of proton-conducting films that fill the void space throughout the porous electrospun matrix and create a fuel-blocking layer. Coated mats as thin as 15 μm were fabricated, and viable composite membranes with methanol permeabilities 20 times lower than Nafion and through-plane proton selectivity five and a half times greater than Nafion are demonstrated. The mechanical properties of the spray coated electrospun mats are shown to be superior to the LbL-only system and possess intrinsically greater dimensional stability and lower mechanical hysteresis than Nafion under hydrated conditions. The composite proton exchange membranes fabricated here were tested in an operational direct methanol fuel cell. The results show the potential for higher open circuit voltages (OCV) and comparable cell resistances when compared to fuel cells based on Nafion.

Study of epithelial differentiation and protein expression of keratinocyte-mesenchyme stem cell co-cultivation on electrospun nylon/B. vulgaris extract composite scaffold.

PubMed

Hosseinzadeh, Simzar; Soleimani, Masoud; Vossoughi, Manuchehr; Ranjbarvan, Parviz; Hamedi, Shokoh; Zamanlui, Soheila; Mahmoudifard, Matin

2017-06-01

Employing of the composite electrospun scaffold containing herbal extract in conjugation with co-culturing of cells can open up new window to the design of efficient biomaterials for skin tissue regeneration. Here, we introduce the synergistic effect of composite electrospun nanofibrous scaffold of nylon66 loaded with Beta vulgaris (B. vulgaris) (extract of beet roots, a plants whose widely used in Iranian folk medicine as wound healing medicine) and co-culture of mesenchymal stem-cells (MSCs)-human keratinocyte (H-keratino) differentiation towards epithelial lineage. In vitro biocompatibility was examined through MTT assay and epithelial differentiation checked by real-time PCR and immunocytochemistry (ICC) assay after co-culturing of MSCs and H-keratino on proposed scaffold. Significant enhancement in cell proliferation was detected after cell culturing on the composite type of electrospun scaffold containing B. vulgaris. Moreover, after 14days of co-culturing process, gene expression results revealed that both composite and non-composite nylon66 electrospun scaffold promote epithelial differentiation compared to mono-cell culturing of H-keratino in terms of several markers as Cytokeratin 10, Cytokeratin 14 and Involucrin and ICC of some dermal proteins like Cytokeratin 14 and Loricrin. To the best of our knowledge, findings of this study will introduce new way for the generation of novel biomaterials for the development of current skin tissue engineering. Copyright © 2017. Published by Elsevier B.V.

Ceria-based electrospun fibers for renewable fuel production via two-step thermal redox cycles for carbon dioxide splitting.

PubMed

Gibbons, William T; Venstrom, Luke J; De Smith, Robert M; Davidson, Jane H; Jackson, Gregory S

2014-07-21

Zirconium-doped ceria (Ce(1-x)Zr(x)O2) was synthesized through a controlled electrospinning process as a promising approach to cost-effective, sinter-resistant material structures for high-temperature, solar-driven thermochemical redox cycles. To approximate a two-step redox cycle for solar fuel production, fibrous Ce(1-x)Zr(x)O2 with relatively low levels of Zr-doping (0 < x < 0.1) were cycled in an infrared-imaging furnace with high-temperature (up to 1500 °C) partial reduction and lower-temperature (∼800 °C) reoxidation via CO2 splitting to produce CO. Increases in Zr content improve reducibility and sintering resistance, and, for x≤ 0.05, do not significantly slow reoxidation kinetics for CO production. Cycle stability of the fibrous Ce(1-x)Zr(x)O2 (with x = 0.025) was assessed for a range of conditions by measuring rates of O2 release during reduction and CO production during reoxidation and by assessing post-cycling fiber crystallite sizes and surface areas. Sintering increases with reduction temperature but occurs primarily along the fiber axes. Even after 108 redox cycles with reduction at 1400 °C and oxidation with CO2 at 800 °C, the fibers maintain their structure with surface areas of ∼0.3 m(2) g(-1), higher than those observed in the literature for other ceria-based structures operating at similarly high temperature conditions. Total CO production and peak production rate stabilize above 3.0 mL g(-1) and 13.0 mL min(-1) g(-1), respectively. The results show the potential for electrospun oxides as sinter-resistant material structures with adequate surface area to support rapid CO2 splitting in solar thermochemical redox cycles.

Efficient protein immobilization on polyethersolfone electrospun nanofibrous membrane via covalent binding for biosensing applications.

PubMed

Mahmoudifard, Matin; Soudi, Sara; Soleimani, Masoud; Hosseinzadeh, Simzar; Esmaeili, Elaheh; Vossoughi, Manouchehr

2016-01-01

In this paper we introduce novel strategy for antibody immobilization using high surface area electrospun nanofibrous membrane based on ethyl-3-(3-dimethylaminopropyl)-carbodiimide/N-hydroxysuccinimide (EDC/NHS) coupling chemistry. To present the high performance of proposed biosensors, anti-staphylococcus enterotoxin B (anti-SEB) was used as a model to demonstrate the utility of our proposed system. Polymer solution of polyethersolfone was used to fabricate fine nanofibrous membrane. Moreover, industrial polyvinylidene fluoride membrane and conventional microtiter plate were also used to compare the efficiency of antibody immobilization. Scanning electron microscopy images were taken to study the morphology of the membranes. The surface activation of nanofibrous membrane was done with the help of O2 plasma. PES nanofibrous membrane with carboxyl functional groups for covalent attachment of antibodies were treated by EDC/NHS coupling agent. The quantity of antibody immobilization was measured by enzyme-linked immuno sorbent assay (ELISA) method. Attenuated total reflectance Fourier transform infrared spectroscopy (ATR-FTIR) spectroscopy was performed to confirm the covalent immobilization of antibody on membrane. Atomic force microscopy, scanning electron microscopy and invert fluorescence microscopy were used to analyze the antibody distribution pattern on solid surfaces. Results show that oxygen plasma treatment effectively increased the amount of antibody immobilization through EDC/NHS coupling chemistry. It was found that the use of nanofibrous membrane causes the improved detection signal of ELISA based biosensors in comparison to the standard assay carried out in the 96-well microtiter plate. This method has the potential to improve the ELISA-based biosensor and we believe that this technique can be used in various biosensing methods. Copyright © 2015. Published by Elsevier B.V.

PLGA/nHA hybrid nanofiber scaffold as a nanocargo carrier of insulin for accelerating bone tissue regeneration

NASA Astrophysics Data System (ADS)

Haider, Adnan; Gupta, Kailash Chandra; Kang, Inn-Kyu

2014-06-01

The development of tissue engineering in the field of orthopedic surgery is booming. Two fields of research in particular have emerged: approaches for tailoring the surface properties of implantable materials with osteoinductive factors as well as evaluation of the response of osteogenic cells to these fabricated implanted materials (hybrid material). In the present study, we chemically grafted insulin onto the surface of hydroxyapatite nanorods (nHA). The insulin-grafted nHAs (nHA-I) were dispersed into poly(lactide-co-glycolide) (PLGA) polymer solution, which was electrospun to prepare PLGA/nHA-I composite nanofiber scaffolds. The morphology of the electrospun nanofiber scaffolds was assessed by field emission scanning electron microscopy (FESEM). After extensive characterization of the PLGA/nHA-I and PLGA/nHA composite nanofiber scaffolds by Fourier transform infrared spectroscopy (FTIR), X-ray diffraction spectroscopy (XRD), X-ray photoelectron spectroscopy (XPS), energy-dispersive X-ray spectrometry (EDS), and transmission electron microscopy (TEM), the PLGA/nHA-I and PLGA/nHA (used as control) composite nanofiber scaffolds were subjected to cell studies. The results obtained from cell adhesion, alizarin red staining, and Von Kossa assay suggested that the PLGA/nHA-I composite nanofiber scaffold has enhanced osteoblastic cell growth, as more cells were proliferated and differentiated. The fact that insulin enhanced osteoblastic cell proliferation will open new possibilities for the development of artificial scaffolds for bone tissue regeneration.

Multifunctional and biologically active matrices from multicomponent polymeric solutions

NASA Technical Reports Server (NTRS)

Kiick, Kristi L. (Inventor); Yamaguchi, Nori (Inventor); Rabolt, John (Inventor); Casper, Cheryl (Inventor)

2012-01-01

A functionalized electrospun matrix for the controlled-release of biologically active agents, such as growth factors, is presented. The functionalized matrix comprises a matrix polymer, a compatibilizing polymer and a biomolecule or other small functioning molecule. In certain aspects the electrospun polymer fibers comprise at least one biologically active molecule functionalized with low molecular weight heparin.

Improved mechanical and electrical properties in electrospun polyimide/multiwalled carbon nanotubes nanofibrous composites

DOE Office of Scientific and Technical Information (OSTI.GOV)

Zha, Jun-Wei; Sun, Fang; Wang, Si-Jiao

2014-10-07

Highly aligned polyimide (PI) and PI/multi-walled carbon nanotubes (PI/MWCNTs) nanofibrous composites by incorporating poly(ethylene oxide) as the dispersing medium were fabricated using electrospinning technique. The morphology, mechanical, and electrical properties of the electrospun nanofibrous composites were investigated. Scanning electron microscope showed that the functionalized MWCNTs (f-MWCNTs) were well dispersed and oriented along the nanofiber axis. Analysis of electrical properties indicated a remarkable improvement on the alternating current conductivity by introduction of the aligned f-MWCNTs. Besides, with addition of 3 vol. % f-MWCNTs, the obvious enhancement of tensile modulus and strength was achieved. Thus, the electrospun PI/MWCNTs nanofibrous composites have greatmore » potential applications in multifunctional engineering materials.« less

Hot-pressed polymer nanofiber supported graphene membrane for high-performance nanofiltration.

PubMed

Wang, Zhao; Sahadevan, Rajesh; Yeh, Che-Ning; Menkhaus, Todd J; Huang, Jiaxing; Fong, Hao

2017-08-04

Graphene oxide (GO) sheets can be readily surface-overlaid on hot-pressed electrospun polyacrylonitrile (PAN) nanofiber membrane to form a continuous and crack-free layer; upon thermal reduction at 150 °C for 12 h, the resulting reduced GO (rGO) layer can reject ∼90% MgSO 4 with high water flux (due to the size exclusion mechanism), making the prepared PAN-rGO membranes promising nanofiltration media for water purification. It is important to note that no delamination of GO/rGO sheet layers has been observed throughout this study. We highlight that a simple processing method (i.e., hot pressing) is critical for the successful preparation of 2D materials (e.g., GO/rGO) based membranes/media. It is envisioned that the reported study can benefit many groups working on various membrane applications of 2D materials; in other words, the hot-pressed electrospun nanofiber membranes could be generally utilized as an innovative type of platform to support various 2D sheets for different separation applications such as highly efficient and cost-effective removal of dissolved components (e.g., organic molecules) and even (hydrated) ions from water.

The Electrospun Ceramic Hollow Nanofibers

PubMed Central

Davoudpour, Yalda; Habibi, Youssef; Elbahri, Mady

2017-01-01

Hollow nanofibers are largely gaining interest from the scientific community for diverse applications in the fields of sensing, energy, health, and environment. The main reasons are: their extensive surface area that increases the possibilities of engineering, their larger accessible active area, their porosity, and their sensitivity. In particular, semiconductor ceramic hollow nanofibers show greater space charge modulation depth, higher electronic transport properties, and shorter ion or electron diffusion length (e.g., for an enhanced charging–discharging rate). In this review, we discuss and introduce the latest developments of ceramic hollow nanofiber materials in terms of synthesis approaches. Particularly, electrospinning derivatives will be highlighted. The electrospun ceramic hollow nanofibers will be reviewed with respect to their most widely studied components, i.e., metal oxides. These nanostructures have been mainly suggested for energy and environmental remediation. Despite the various advantages of such one dimensional (1D) nanostructures, their fabrication strategies need to be improved to increase their practical use. The domain of nanofabrication is still advancing, and its predictable shortcomings and bottlenecks must be identified and addressed. Inconsistency of the hollow nanostructure with regard to their composition and dimensions could be one of such challenges. Moreover, their poor scalability hinders their wide applicability for commercialization and industrial use. PMID:29120403

Porous Carbon Nanofibers from Electrospun Biomass Tar/Polyacrylonitrile/Silver Hybrids as Antimicrobial Materials.

PubMed

Song, Kunlin; Wu, Qinglin; Zhang, Zhen; Ren, Suxia; Lei, Tingzhou; Negulescu, Ioan I; Zhang, Quanguo

2015-07-15

A novel route to fabricate low-cost porous carbon nanofibers (CNFs) using biomass tar, polyacrylonitrile (PAN), and silver nanoparticles has been demonstrated through electrospinning and subsequent stabilization and carbonization processes. The continuous electrospun nanofibers had average diameters ranging from 392 to 903 nm. The addition of biomass tar resulted in increased fiber diameters, reduced thermal stabilities, and slowed cyclization reactions of PAN in the as-spun nanofibers. After stabilization and carbonization, the resultant CNFs showed more uniformly sized and reduced average diameters (226-507 nm) compared to as-spun nanofibers. The CNFs exhibited high specific surface area (>400 m(2)/g) and microporosity, attributed to the combined effects of phase separations of the tar and PAN and thermal decompositions of tar components. These pore characteristics increased the exposures and contacts of silver nanoparticles to the bacteria including Gram-positive Staphylococcus aureus and Gram-negative Escherichia coli, leading to excellent antimicrobial performances of as-spun nanofibers and CNFs. A new strategy is thus provided for utilizing biomass tar as a low-cost precursor to prepare functional CNFs and reduce environmental pollutions associated with direct disposal of tar as an industrial waste.

Preparation and characterization of electrospun alginate/PLA nanofibers as tissue engineering material by emulsion eletrospinning.

PubMed

Xu, Weihong; Shen, Renzhe; Yan, Yurong; Gao, Jie

2017-01-01

Scaffolds made by biomaterials offer favorite environment for cell grow and show a wide potential application in tissue engineering. Novel biocompatibility materials polylatic acid (PLA) nanofiber membranes with favorable biocompatibility and good mechanical strength could serve as an innovative tissue engineering scaffold. Sodium alginate (SA) could be used in biomedical areas because of its anti-bacterial property, hydrophilicity and biocompatibility. In this article, we chose PLA as continuous phase and SA as dispersion phase to prepare a W/O emulsion and then electrospun it to get a SA/PLA composite nanofiber membranes. The CLSM images illustrated that the existence of SA was located on the surface of composite fibers and the FTIR results confirmed the result. A calcium ion replacement step was used as an after-treatment for SA/PLA nanofiber membranes in order to anchor the alginic ion in a form of gelated calcium alginate (CA). The single fiber tensile test shows a good mechanical property of CA/PLA nanofiber membranes, and the nanofiber membranes are beneficial for cell proliferation and differentiation owing to MTT array as well as Alizarin red S (ARS) staining test. Copyright © 2016 Elsevier Ltd. All rights reserved.

Improving agar electrospinnability with choline-based deep eutectic solvents.

PubMed

Sousa, Ana M M; Souza, Hiléia K S; Uknalis, Joseph; Liu, Shih-Chuan; Gonçalves, Maria P; Liu, LinShu

2015-09-01

Very recently our group has produced novel agar-based fibers by an electrospinning technique using water as solvent and polyvinyl alcohol (PVA) as co-blending polymer. Here, we tested the deep eutectic solvent (DES), (2-hydroxyethyl)trimethylammonium chloride/urea prepared at 1:2 molar ratio, as an alternative solvent medium for agar electrospinning. The electrospun materials were collected with an ethanol bath adapted to a previous electrospinning set-up. One weight percent agar-in-DES showed improved viscoelasticity and hence, spinnability, when compared to 1 wt% agar-in-water and pure agar nanofibers were successfully electrospun if working above the temperature of sol-gel transition (∼80 °C). By changing the solvent medium we decreased the PVA concentration (5 wt% starting solution) and successfully produced composite fibers with high agar contents (50/50 agar/PVA). Best composite fibers were formed with the 50/50 and 30/70 agar/PVA solutions. These fibers were mechanically resistant, showed tailorable surface roughness and diverse size distributions, with most of the diameters falling in the sub-micron range. Both nano and micro forms of agar fibers (used separately or combined) may have potential for the design of new and highly functional agar-based materials. Published by Elsevier B.V.

Effects of the glycerophosphate-polylactic copolymer formation on electrospun fibers

NASA Astrophysics Data System (ADS)

Shen, Wen; Zhang, Guanghua; Li, YaLi; Fan, Guodong

2018-06-01

Poly-lactic (PLA) porous fibers are widely used in tissue engineering scaffolds and many other fields. Non-solvent induced phase separation is one of the best way for preparation of porous fiber. It is difficult to obtain the PLA electrospun porous fibers by phase separation. In this paper, glycerophosphate-polylactic copolymer (GP-PLA) are synthesized with sodium glyceryl phosphate and L-lactide to produce porous fibers. Furthermore, the Gel permeation chromatography (GPC), FT-IR and 1H-NMR are applied for characterizing the obtained copolymers. Thermogravimetric (TG) measurements indicate that the thermal stability of GP-PLA is lower than that of linear PLA. Under 30% humidity, porous GP-PLA fibers are obtained by electrospinning method, the scanning electron microscopy (SEM) refers that through the modification of the molecular structure, GP-PLA fibers are more porous under the same condition. The water contact angle is increased coming with the increase of GP contents. Hydrophilic porous GP-PLA fibers are obtained via solvent phase separation. The relationship between hydrophilicity and surface morphology of materials is further explained by Atomic Force Microscope (AFM). GP-PLA has a potential application in the field of scaffold for tissue engineering.

Novel electrospun gas diffusion layers for polymer electrolyte membrane fuel cells: Part I. Fabrication, morphological characterization, and in situ performance

NASA Astrophysics Data System (ADS)

Chevalier, S.; Lavielle, N.; Hatton, B. D.; Bazylak, A.

2017-06-01

In this first of a series of two papers, we report an in-depth analysis of the impact of the gas diffusion layer (GDL) structure on the polymer electrolyte membrane (PEM) fuel cell performance through the use of custom GDLs fabricated in-house. Hydrophobic electrospun nanofibrous gas diffusion layers (eGDLs) are fabricated with controlled fibre diameter and alignment. The eGDLs are rendered hydrophobic through direct surface functionalization, and this molecular grafting is achieved in the absence of structural alteration. The fibre diameter, chemical composition, and electrical conductivity of the eGDL are characterized, and the impact of eGDL structure on fuel cell performance is analysed. We observe that the eGDL facilitates higher fuel cell power densities compared to a commercial GDL (Toray TGP-H-60) at highly humidified operating conditions. The ohmic resistance of the fuel cell is found to significantly increase with increasing inter-fiber distance. It is also observed that the addition of a hydrophobic treatment enhances membrane hydration, and fibres perpendicularly aligned to the channel direction may enhance the contact area between the catalyst layer and the GDL.

Fabrication, biocompatibility, and tissue engineering substrate analysis of polyvinyl alcohol-gelatin core-shell electrospun nanofibers

NASA Astrophysics Data System (ADS)

Merkle, Valerie Marie

Cardiovascular disease is the leading cause of death in the United States with approximately 49% of the cardiovascular related deaths attributed to coronary heart disease (CHD). CHD is the accumulation of plaque resulting in the narrowing of the vessel lumen and a decrease in blood flow to the downstream heart muscle. In order to restore blood flow, arterial by-pass procedures can be undertaken. However, the patient's own arteries/veins may not be suitable for use as a vessel replacement, and synthetic grafts lack the compliancy and durability needed for these small diameter locations (< 5 mm). Therefore, the goal of this research is to develop a nanofibrous material that can be used in vascular applications such as this. In this study, we fabricate coaxial electrospun nanofibers with gelatin in the shell and polyvinyl alcohol (PVA) in the core using 1 Gelatin: 1 PVA and 3 Gelatin: 1 PVA mass ratios. Gelatin, derived from collagen, is highly bioactive while PVA, a synthetic polymer, has appealing mechanical properties. Therefore, by combining these materials in a core-shell structure, we hypothesize that the resulting nanofibers will have enhanced mechanical properties, cellular growth and migration, as well as minimal platelet deposition and activation compared to scaffolds composed solely of gelatin or PVA. First, the coaxial scaffolds exhibited an enhanced Young's modulus and ultimate strength compared to scaffolds composed of PVA or gelatin alone. Endothelial cells had high proliferation and migration on the coaxial electrospun scaffolds with higher migration seen on the stiffer, coaxial scaffolds. The smooth muscle cells had less proliferation and lower migration rates on the coaxial scaffolds than the endothelial cells. Using a modified prothrombinase assay, the coaxial scaffolds had minimal platelet activation. Lastly, when pre-seeding the coaxial scaffolds with endothelial cells or smooth muscle cells, the platelet deposition decreased in comparison to platelet deposition with no cell pre-seeding. Overall, the 1 Gel: 1 PVA coaxial scaffolds promoted endothelial cell growth and migration, minimized smooth muscle cell growth and migration, and had minimal platelet activation. Therefore, the 1 Gel: 1 PVA coaxial nanofibers are an intriguing material for use in vascular applications.

Engineering ear-shaped cartilage using electrospun fibrous membranes of gelatin/polycaprolactone.

PubMed

Xue, Jixin; Feng, Bei; Zheng, Rui; Lu, Yang; Zhou, Guangdong; Liu, Wei; Cao, Yilin; Zhang, Yanzhong; Zhang, Wen Jie

2013-04-01

Tissue engineering approach continuously requires for emerging strategies to improve the efficacy in repairing and regeneration of tissue defects. Previously, we developed a sandwich model strategy for cartilage engineering, using the combination of acellular cartilage sheets (ACSs) and chondrocytes. However, the process for the preparation of ACSs is complicated, and it is also difficult to obtain large ACSs. The aim of this study was to engineer cartilage with precise three-dimensional (3-D) structures by applying electrospun fibrous membranes of gelatin/polycaprolactone (GT/PCL). We first prepared the electrospun GT/PCL membranes into rounded shape, and then seeded chondrocytes in the sandwich model. After in vitro and in vivo cultivation, the newly formed cartilage-like tissues were harvested. Macroscopic observations and histological analysis confirmed that the engineering of cartilage using the electrospun GT/PCL membranes was feasible. An ear-shaped cartilage was then constructed in the sandwich model, with the help of an ear-shaped titanium alloy mold. After 2 weeks of culture in vitro and 6 weeks of subcutaneous incubation in vivo, the ear-shaped cartilage largely maintained their original shape, with a shape similarity up to 91.41% of the titanium mold. In addition, the engineered cartilage showed good elasticity and impressive mechanical strength. These results demonstrated that the engineering of 3-D cartilage in a sandwich model using electrospun fibrous membranes was a facile and effective approach, which has the potential to be applied for the engineering of other tissues with complicated 3-D structures. Copyright © 2012 Elsevier Ltd. All rights reserved.

Electrospun oriented gelatin-hydroxyapatite fiber scaffolds for bone tissue engineering.

PubMed

Salifu, Ali A; Lekakou, Constantina; Labeed, Fatima H

2017-07-01

Tissue engineering of human fetal osteoblast cells was investigated on gelatin-hydroxyapatite (HA), crosslinked, electrospun oriented fiber scaffolds at the different HA concentrations of 0, 10, 20, and 25 wt % in the dry fibers and different fiber diameter, pore size and porosity of scaffolds. Rheological tests and proton nuclear magnetic resonance spectroscopy were conducted for all solutions used for electrospinning. It was found that 25 wt % HA-gelatin scaffolds electrospun at 20 kV led to the greatest cell attachment, cell proliferation and extracellular matrix (ECM) production while fiber orientation improved the mechanical properties, where crosslinked electrospun 25 wt % HA-gelatin fiber scaffolds yielded a Young's modulus in the range of 0.5-0.9 GPa and a tensile strength in the range of 4-10 MPa in the fiber direction for an applied voltage of 20-30 kV, respectively, in the electrospinning of scaffolds. Biological characterization of cell seeded scaffolds yielded the rate of cell growth and ECM (collagen and calcium) production by the cells as a function of time; it included cell seeding efficiency tests, alamar blue cell proliferation assay, alkaline phosphate (ALP) assay, collagen assay, calcium colorimetric assay, fluorescence microscopy for live and dead cells, and scanning electron microscopy for cell culture from 1 to 18 days. After 18 days, cells seeded and grown on the 25 wt % HA-gelatin scaffold, electrospun at 20 kV, reached production of collagen at 370 μg/L and calcium production at 0.8 mM. © 2016 Wiley Periodicals, Inc. J Biomed Mater Res Part A: 105A: 1911-1926, 2017. © 2017 Wiley Periodicals, Inc.

Nanoscale Metal Oxide Semiconductors for Gas Sensing

NASA Technical Reports Server (NTRS)

Hunter, Gary W.; Evans, Laura; Xu, Jennifer C.; VanderWal, Randy L.; Berger, Gordon M.; Kulis, Michael J.

2011-01-01

A report describes the fabrication and testing of nanoscale metal oxide semiconductors (MOSs) for gas and chemical sensing. This document examines the relationship between processing approaches and resulting sensor behavior. This is a core question related to a range of applications of nanotechnology and a number of different synthesis methods are discussed: thermal evaporation- condensation (TEC), controlled oxidation, and electrospinning. Advantages and limitations of each technique are listed, providing a processing overview to developers of nanotechnology- based systems. The results of a significant amount of testing and comparison are also described. A comparison is made between SnO2, ZnO, and TiO2 single-crystal nanowires and SnO2 polycrystalline nanofibers for gas sensing. The TECsynthesized single-crystal nanowires offer uniform crystal surfaces, resistance to sintering, and their synthesis may be done apart from the substrate. The TECproduced nanowire response is very low, even at the operating temperature of 200 C. In contrast, the electrospun polycrystalline nanofiber response is high, suggesting that junction potentials are superior to a continuous surface depletion layer as a transduction mechanism for chemisorption. Using a catalyst deposited upon the surface in the form of nanoparticles yields dramatic gains in sensitivity for both nanostructured, one-dimensional forms. For the nanowire materials, the response magnitude and response rate uniformly increase with increasing operating temperature. Such changes are interpreted in terms of accelerated surface diffusional processes, yielding greater access to chemisorbed oxygen species and faster dissociative chemisorption, respectively. Regardless of operating temperature, sensitivity of the nanofibers is a factor of 10 to 100 greater than that of nanowires with the same catalyst for the same test condition. In summary, nanostructure appears critical to governing the reactivity, as measured by electrical resistance of these SnO2 nanomaterials towards reducing gases. With regard to the sensitivity of the different nascent nanostructures, the electrospun nanofibers appear preferable

Dimensional stability and electrochemical behaviour of ZrO2 incorporated electrospun PVdF-HFP based nanocomposite polymer membrane electrolyte for Li-ion capacitors

PubMed Central

Solarajan, Arun Kumar; Murugadoss, Vignesh; Angaiah, Subramania

2017-01-01

Different weight percentages of ZrO2 (0, 3, 5, 7 and 10 wt%) incorporated electrospun PVDF-HFP nanocomposite polymer membranes (esCPMs) were prepared by electrospinning technique. They were activated by soaking in 1 M LiPF6 containing 1:1 volume ratio of EC : DMC (ethylene carbonate:dimethyl carbonate) to get electrospun nanocomposite polymer membrane electrolytes (esCPMEs). The influence of ZrO2 on the physical, mechanical and electrochemical properties of esCPM was studied in detail. Finally, coin type Li-ion capacitor cell was assembled using LiCo0.2Mn1.8O4 as the cathode, Activated carbon as the anode and the esCPME containing 7 wt% of ZrO2 as the separator, which delivered a discharge capacitance of 182.5 Fg−1 at the current density of 1Ag−1 and retained 92% of its initial discharge capacitance even after 2,000 cycles. It revealed that the electrospun PVdF-HFP/ZrO2 based nanocomposite membrane electrolyte could be used as a good candidate for high performance Li-ion capacitors. PMID:28397783

Dimensional stability and electrochemical behaviour of ZrO2 incorporated electrospun PVdF-HFP based nanocomposite polymer membrane electrolyte for Li-ion capacitors.

PubMed

Solarajan, Arun Kumar; Murugadoss, Vignesh; Angaiah, Subramania

2017-04-11

Different weight percentages of ZrO 2 (0, 3, 5, 7 and 10 wt%) incorporated electrospun PVDF-HFP nanocomposite polymer membranes (esCPMs) were prepared by electrospinning technique. They were activated by soaking in 1 M LiPF 6 containing 1:1 volume ratio of EC : DMC (ethylene carbonate:dimethyl carbonate) to get electrospun nanocomposite polymer membrane electrolytes (esCPMEs). The influence of ZrO 2 on the physical, mechanical and electrochemical properties of esCPM was studied in detail. Finally, coin type Li-ion capacitor cell was assembled using LiCo 0.2 Mn 1.8 O 4 as the cathode, Activated carbon as the anode and the esCPME containing 7 wt% of ZrO 2 as the separator, which delivered a discharge capacitance of 182.5 Fg -1 at the current density of 1Ag -1 and retained 92% of its initial discharge capacitance even after 2,000 cycles. It revealed that the electrospun PVdF-HFP/ZrO 2 based nanocomposite membrane electrolyte could be used as a good candidate for high performance Li-ion capacitors.

Tunable Mechanics in Electrospun Composites via Hierarchical Organization.

PubMed

Wanasekara, Nandula D; Matolyak, Lindsay E; Korley, LaShanda T J

2015-10-21

Design strategies from nature provide vital clues for the development of synthetic materials with tunable mechanical properties. Employing the concept of hierarchy and controlled percolation, a new class of polymer nanocomposites containing a montmorillonite (MMT)-reinforced electrospun poly(vinyl alcohol) (PVA) filler embedded within a polymeric matrix of either poly(vinyl acetate) (PVAc) or ethylene oxide-epichlorohydrin copolymer (EO-EPI) were developed to achieve a tunable mechanical response upon exposure to specific stimuli. Mechanical response and switching times upon hydration were shown to be dependent on the weight-fraction of MMT in the PVA electrospun fibers and type of composite matrix. PVA/MMT.PVAc composite films retained excellent two-way switchability for all MMT fractions; however, the switching time upon hydration was decreased dramatically as the MMT content was increased due to the highly hydrophilic nature of MMT. Additionally, for the first time, significant two-way switchability of PVA/MMT.EO-EPI composites was achieved for higher weight fractions (12 wt %) of MMT. An extensive investigation into the effects of fiber diameter, crystallinity, and MMT content revealed that inherent rigidity of MMT platelets plays an important role in controlling the mechanical response of these hierarchical electrospun composites.

Incorporation of T4 bacteriophage in electrospun fibres.

PubMed

Korehei, R; Kadla, J

2013-05-01

Antibacterial food packaging materials, such as bacteriophage-activated electrospun fibrous mats, may address concerns triggered by waves of bacterial food contamination. To address this, we investigated several efficient methods for incorporating T4 bacteriophage into electrospun fibrous mats. The incorporation of T4 bacteriophage using simple suspension electrospinning led to more than five orders of magnitude decrease in bacteriophage activity. To better maintain bacteriophage viability, emulsion electrospinning was developed where the T4 bacteriophage was pre-encapsulated in an alginate reservoir via an emulsification process and subsequently electrospun into fibres. This resulted in an increase in bacteriophage viability, but there was still two orders of magnitude drop in activity. Using a coaxial electrospinning process, full bacteriophage activity could be maintained. In this process, a core/shell fibre structure was formed with the T4 bacteriophage being directly incorporated into the fibre core. The core/shell fibre encapsulated bacteriophage exhibited full bacteriophage viability after storing for several weeks at +4°C. Coaxial electrospinning was shown to be capable of encapsulating bacteriophages with high loading capacity, high viability and long storage time. These results are significant in the context of controlling and preventing bacterial infections in perishable foods during storage. © 2013 The Society for Applied Microbiology.

Engineering functional and histological regeneration of vascularized skeletal muscle.

PubMed

Gilbert-Honick, Jordana; Iyer, Shama R; Somers, Sarah M; Lovering, Richard M; Wagner, Kathryn; Mao, Hai-Quan; Grayson, Warren L

2018-05-01

Tissue engineering strategies to treat patients with volumetric muscle loss (VML) aim to recover the structure and contractile function of lost muscle tissue. Here, we assessed the capacity of novel electrospun fibrin hydrogel scaffolds seeded with murine myoblasts to regenerate the structure and function of damaged muscle within VML defects to the mouse tibialis anterior muscle. The electrospun fibrin scaffolds provide pro-myogenic alignment and stiffness cues, myomimetic hierarchical structure, suturability, and scale-up capabilities. Myoblast-seeded scaffolds enabled remarkable muscle regeneration with high myofiber and vascular densities after 2 and 4 weeks, mimicking that of native skeletal muscle, while acellular scaffolds lacked muscle regeneration. Both myoblast-seeded and acellular scaffolds fully recovered muscle contractile function to uninjured values after 2 and 4 weeks. Electrospun scaffolds pre-vascularized with co-cultured human endothelial cells and human adipose-derived stem cells implanted into VML defects for 2 weeks anastomosed with host vasculature and were perfused with host red blood cells. These data demonstrate the significant potential of electrospun fibrin scaffolds seeded with myoblasts to fully regenerate the structure and function of volumetric muscle defects and these scaffolds offer a promising treatment option for patients with VML. Copyright © 2018 Elsevier Ltd. All rights reserved.

Electrospun nanofibrous scaffolds of segmented polyurethanes based on PEG, PLLA and PTMC blocks: Physico-chemical properties and morphology.

PubMed

Trinca, Rafael Bergamo; Abraham, Gustavo A; Felisberti, Maria Isabel

2015-11-01

Biocompatible polymeric scaffolds are crucial for successful tissue engineering. Biomedical segmented polyurethanes (SPUs) are an important and versatile class of polymers characterized by a broad spectrum of compositions, molecular architectures, properties and applications. Although SPUs are versatile materials that can be designed by different routes to cover a wide range of properties, they have been infrequently used for the preparation of electrospun nanofibrous scaffolds. This study reports the preparation of new electrospun polyurethane scaffolds. The segmented polyurethanes were synthesized using low molar masses macrodyols (poly(ethylene glycol), poly(l-lactide) and poly(trimethylene carbonate)) and 1,6-hexane diisocyanate and 1,4-butanodiol as isocyanate and chain extensor, respectively. Different electrospinning parameters such as solution properties and processing conditions were evaluated to achieve smooth, uniform bead-free fibers. Electrospun micro/nanofibrous structures with mean fiber diameters ranging from 600nm to 770nm were obtained by varying the processing conditions. They were characterized in terms of thermal and dynamical mechanical properties, swelling degree and morphology. The elastomeric polyurethane scaffolds exhibit interesting properties that could be appropriate as biomimetic matrices for soft tissue engineering applications. Copyright © 2015 Elsevier B.V. All rights reserved.

Recent advances of basic materials to obtain electrospun polymeric nanofibers for medical applications

NASA Astrophysics Data System (ADS)

Manea, L. R.; Hristian, L.; Leon, A. L.; Popa, A.

2016-08-01

The most important applications of electrospun polymeric nanofibers are by far those from biomedical field. From the biological point of view, almost all the human tissues and organs consist of nanofibroas structures. The examples include the bone, dentine, cartilage, tendons and skin. All these are characterized through different fibrous structures, hierarchically organized at nanometer scale. Electrospinning represents one of the nanotechnologies that permit to obtain such structures for cell cultures, besides other technologies, such as selfassembling and phase separation technologies. The basic materials used to produce electrospun nanofibers can be natural or synthetic, having polymeric, ceramic or composite nature. These materials are selected depending of the nature and structure of the tissue meant to be regenerated, namely: for the regeneration of smooth tissues regeneration one needs to process through electrospinning polymeric basic materials, while in order to obtain the supports for the regeneration of hard tissues one must mainly use ceramic materials or composite structures that permit imbedding the bioactive substances in distinctive zones of the matrix. This work presents recent studies concerning basic materials used to obtain electrospun polymeric nanofibers, and real possibilities to produce and implement these nanofibers in medical bioengineering applications.

Colon-specific pulsatile drug release provided by electrospun shellac nanocoating on hydrophilic amorphous composites

PubMed Central

Yu, Deng-Guang; Wang, Ke; Liu, Ping; Chen, Xiaohong

2018-01-01

Background Colon-specific pulsatile drug release, as a combined drug controlled-release model, is a useful drug delivery manner for a series of diseases. New nanomedicines and related preparation methods are highly desired. Methods With diclofenac sodium (DS) as a model drug, a new type of structural nanocomposite (SC), in which composite polyvinylpyrrolidone (PVP)–DS core was coated by shellac, was fabricated via modified coaxial electrospinning. For comparison, traditional PVP–DS monolithic hydrophilic nanocomposites (HCs) were generated using a traditional blending process. Scanning electron microscopy (SEM), transmission electron microscopy (TEM), X-ray diffraction (XRD), attenuated total reflectance-Fourier transform infrared (ATR-FTIR), water contact angle (WCA), and in vitro dissolution and ex vivo permeation tests were conducted to characterize the composites. Results SEM images demonstrated that both composites were linear nanofibers with smooth surface morphology and cross sections. TEM disclosed that the SCs had a thin shellac sheath layer of approximately 12 nm. XRD and ATR-FTIR results demonstrated that the crystalline DS was converted into amorphous composites with PVP because of favorable secondary interactions. WCA and in vitro dissolution tests demonstrated that the sheath shellac layers in SC could resist acid conditions and provide typical colon-specific pulsatile release, rather than a pulsatile release of HC under acid conditions. Ex vivo permeation results demonstrated that the SCs were able to furnish a tenfold drug permeation rate than the DS particles on the colon membrane. Conclusion A new SC with a shellac coating on hydrophilic amorphous nanocomposites could furnish a colon-specific pulsatile drug release profile. The modified coaxial process can be exploited as a useful tool to create nanocoatings. PMID:29713169

Colon-specific pulsatile drug release provided by electrospun shellac nanocoating on hydrophilic amorphous composites.

PubMed

Yang, Yao-Yao; Liu, Zhe-Peng; Yu, Deng-Guang; Wang, Ke; Liu, Ping; Chen, Xiaohong

2018-01-01

Colon-specific pulsatile drug release, as a combined drug controlled-release model, is a useful drug delivery manner for a series of diseases. New nanomedicines and related preparation methods are highly desired. With diclofenac sodium (DS) as a model drug, a new type of structural nanocomposite (SC), in which composite polyvinylpyrrolidone (PVP)-DS core was coated by shellac, was fabricated via modified coaxial electrospinning. For comparison, traditional PVP-DS monolithic hydrophilic nanocomposites (HCs) were generated using a traditional blending process. Scanning electron microscopy (SEM), transmission electron microscopy (TEM), X-ray diffraction (XRD), attenuated total reflectance-Fourier transform infrared (ATR-FTIR), water contact angle (WCA), and in vitro dissolution and ex vivo permeation tests were conducted to characterize the composites. SEM images demonstrated that both composites were linear nanofibers with smooth surface morphology and cross sections. TEM disclosed that the SCs had a thin shellac sheath layer of approximately 12 nm. XRD and ATR-FTIR results demonstrated that the crystalline DS was converted into amorphous composites with PVP because of favorable secondary interactions. WCA and in vitro dissolution tests demonstrated that the sheath shellac layers in SC could resist acid conditions and provide typical colon-specific pulsatile release, rather than a pulsatile release of HC under acid conditions. Ex vivo permeation results demonstrated that the SCs were able to furnish a tenfold drug permeation rate than the DS particles on the colon membrane. A new SC with a shellac coating on hydrophilic amorphous nanocomposites could furnish a colon-specific pulsatile drug release profile. The modified coaxial process can be exploited as a useful tool to create nanocoatings.

Highly porous 3D nanofiber scaffold using an electrospinning technique.

PubMed

Kim, Geunhyung; Kim, WanDoo

2007-04-01

A successful 3D tissue-engineering scaffold must have a highly porous structure and good mechanical stability. High porosity and optimally designed pore size provide structural space for cell accommodation and migration and enable the exchange of nutrients between the scaffold and environment. Poly(epsilon-carprolactone) fibers were electrospun using an auxiliary electrode and chemical blowing agent (BA), and characterized according to porosity, pore size, and their mechanical properties. We also investigated the effect of the BA on the electrospinning processability. The growth characteristic of human dermal fibroblasts cells cultured in the webs showed the good adhesion with the blown web relative to a normal electrospun mat. The blown nanofiber web had good tensile properties and high porosity compared to a typical electrospun nanofiber scaffold. (c) 2006 Wiley Periodicals, Inc.

Electrospun nanofibers for neural tissue engineering

NASA Astrophysics Data System (ADS)

Xie, Jingwei; MacEwan, Matthew R.; Schwartz, Andrea G.; Xia, Younan

2010-01-01

Biodegradable nanofibers produced by electrospinning represent a new class of promising scaffolds to support nerve regeneration. We begin with a brief discussion on the electrospinning of nanofibers and methods for controlling the structure, porosity, and alignment of the electrospun nanofibers. The methods include control of the nanoscale morphology and microscale alignment of the nanofibers, as well as the fabrication of macroscale, three-dimensional tubular structures. We then highlight recent studies that utilize electrospun nanofibers to manipulate biological processes relevant to nervous tissue regeneration, including stem cell differentiation, guidance of neurite extension, and peripheral nerve injury treatments. The main objective of this feature article is to provide valuable insights into methods for investigating the mechanisms of neurite growth on novel nanofibrous scaffolds and optimization of the nanofiber scaffolds and conduits for repairing peripheral nerve injuries.

Electrospun Nanofiber-Coated Membrane Separators for Lithium-Ion Batteries

NASA Astrophysics Data System (ADS)

Lee, Hun

Lithium-ion batteries are widely used as a power source for portable electronic devices and hybrid electric vehicles due to their excellent energy and power densities, long cycle life, and enhanced safety. A separator is considered to be the critical component in lithium-ion rechargeable batteries. The separator is placed between the positive and negative electrodes in order to prevent the physical contact of electrodes while allowing the transportation of ions. In most commercial lithium-ion batteries, polyolefin microporous membranes are commonly used as the separator due to their good chemical stability and high mechanical strength. However, some of their intrinsic natures, such as low electrolyte uptake, poor adhesion property to the electrodes, and low ionic conductivity, can still be improved to achieve higher performance of lithium-ion batteries. In order to improve these intrinsic properties, polyolefin microporous membranes can be coated with nanofibers by using electrospinning technique. Electrospinning is a simple and efficient method to prepare nanofibers which can absorb a significant amount of liquid electrolyte to achieve low internal resistance and battery performance. This research presents the preparation and investigation of composite membrane separators prepared by coating nanofibers onto polyolefin microporous membranes via electrospinning technique. Polyvinylidene fluoride polymers and copolymers were used for the preparation of electrospun nanofiber coatings because they have excellent electrochemical stability, good adhesion property, and high temperature resistance. The nanofiber coatings prepared by electrospinning form an interconnected and randomly orientated structure on the surface of the polyolefin microporous membranes. The size of the nanofibers is on a scale that does not interfere with the micropores in the membrane substrates. The resultant nanofiber-coated membranes have the potential to combine advantages of both the polyolefin separator membranes and the nanoscale fibrous polymer coatings. The polyolefin microporous membranes serve as the supporting substrate which provides the required mechanical strength for the assembling process of lithium-ion batteries. The electrospun nanofiber coatings improve the wettability of the composite membrane separators to the liquid electrolyte, which is desirable for the lithium-ion batteries with high kinetics and good cycling performance. The results show that the nanofiber-coated membranes have enhanced adhesion properties to the battery electrode which can help prevent the formation of undesirable gaps between the separators and electrodes during prolonged charge-discharge cycles, especially in large-format batteries. The improvement on adhesive properties of nanofiber-coated membranes was evaluated by peel test. Nanofiber coatings applied to polyolefin membrane substrates improve the adhesion of separator membranes to battery electrodes. Electrolyte uptakes, ionic conductivities and interfacial resistances of the nanofiber-coated membrane separators were studied by soaking the membrane separators with a liquid electrolyte solution of 1 M lithium hexafluorophosphate dissolved in ethylene carbonate/dimethylcarbonate/ethylmethyl carbonate (1:1:1 vol). The nanofiber coatings on the surface of the membrane substrates increase the electrolyte uptake capacity due to the high surface area and capillary effect of nanofibers. The nanofiber-coated membranes soaked in the liquid electrolyte solution exhibit high ionic conductivities and low interfacial resistances to the lithium electrode. The cells containing LiFePO 4 cathode and the nanofiber-coated membranes as the separator show high discharge specific capacities and good cycling stability at room temperature. The nanofiber coatings on the membrane substrates contribute to high ionic conductivity and good electrochemical performance in lithium-ion batteries. Therefore, these nanofiber-coated composite membranes can be directly used as novel battery separators for high performance of lithium-ion batteries. Coating polyolefin microporous membranes with electrospun nanofibers is a promising approach to obtain highperformance separators for advanced lithium-ion batteries.

In vitro and in vivo evaluation of a small-caliber coaxial electrospun vascular graft loaded with heparin and VEGF.

PubMed

Hu, Yun-Tao; Pan, Xu-Dong; Zheng, Jun; Ma, Wei-Guo; Sun, Li-Zhong

2017-08-01

To date, clinically available expanded polytetrafluoro-ethylene (ePTFE) vascular grafts are suboptimal for reconstructing small caliber (D < 6 mm) arteries, owing to thrombosis in early and restenosis in late stage. Our aim in this preliminary study was to fabricate a nano-fibrous vascular graft which was biofunctionalized with VEGF 165 and heparin. The short term performance was evaluated both in vitro and in vivo. Four-mm caliber grafts were prepared by the coaxial-elctrospun technique, which consisted of poly(l-lactide-co-caprolactone) [P(LLA-CL)] collagen and elastin. Heparin and endothelial cell growth factor-165 (VEGF 165 ) were encapsulated in the core of the fibrous. Controlled release of the heparin and VEGF 165 were evaluated for 28 days. Endothelial cells were cultured on the electrospun grafts or ePTFE grafts as controls. The cellular adhesion, proliferation and morphology were examined. Electrospun or ePTFE grafts were randomly implanted into a rabbit infrarenal aortic replacement model (n = 30) for 28 days without any antiplatelet therapy. At the termination, all grafts were examined by Doppler ultrasound and then evaluated with histology and scanning electron microscopy. The cumulative release amount of heparin (6.93 ± 1.03 mg) and VEGF 165 (22.17 ± 5.56 μg) during 28 days were measured. Endothelial cells cultured on electrospun grafts showed significantly higher attachment efficiency and proliferation compared to the ePTFE ones (P < 0.001). At 2 h more ECs had attached to the P(LLA-CL)/Collagen/Elatin grafts (83.26 ± 8.02%) compared to P(LLA-CL) (67.07 ± 4.16%) and ePTFE (46.87 ± 8.85%). ECs proliferated faster on VEGF loaded grafts (O.D = 2.9 ± 1.2, n = 12) compared to ePTFE (O.D = 1.7 ± 1.0, n = 12). The patency was significantly higher in electrospun grafts (86.6%) than ePTFE grafts (40.0%) (P = 0.021). Correspondingly, the microscope images of electrospun implants showed little thrombus when compared with the ePTFE implants. Biofunctionalized electrospun graft showed surgical properties, hemocompatibility and higher short-term patency compared with the ePTFE grafts. Despite good early performances, profound study should be designed for long-term evaluation. Copyright © 2017 IJS Publishing Group Ltd. Published by Elsevier Ltd. All rights reserved.

Electrodynamic tailoring of self-assembled three-dimensional electrospun constructs

NASA Astrophysics Data System (ADS)

Reis, Tiago C.; Correia, Ilídio J.; Aguiar-Ricardo, Ana

2013-07-01

The rational design of three-dimensional electrospun constructs (3DECs) can lead to striking topographies and tailored shapes of electrospun materials. This new generation of materials is suppressing some of the current limitations of the usual 2D non-woven electrospun fiber mats, such as small pore sizes or only flat shaped constructs. Herein, we pursued an explanation for the self-assembly of 3DECs based on electrodynamic simulations and experimental validation. We concluded that the self-assembly process is driven by the establishment of attractive electrostatic forces between the positively charged aerial fibers and the already collected ones, which tend to acquire a negatively charged network oriented towards the nozzle. The in situ polarization degree is strengthened by higher amounts of clustered fibers, and therefore the initial high density fibrous regions are the preliminary motifs for the self-assembly mechanism. As such regions increase their in situ polarization electrostatic repulsive forces will appear, favoring a competitive growth of these self-assembled fibrous clusters. Highly polarized regions will evidence higher distances between consecutive micro-assembled fibers (MAFs). Different processing parameters - deposition time, electric field intensity, concentration of polymer solution, environmental temperature and relative humidity - were evaluated in an attempt to control material's design.The rational design of three-dimensional electrospun constructs (3DECs) can lead to striking topographies and tailored shapes of electrospun materials. This new generation of materials is suppressing some of the current limitations of the usual 2D non-woven electrospun fiber mats, such as small pore sizes or only flat shaped constructs. Herein, we pursued an explanation for the self-assembly of 3DECs based on electrodynamic simulations and experimental validation. We concluded that the self-assembly process is driven by the establishment of attractive electrostatic forces between the positively charged aerial fibers and the already collected ones, which tend to acquire a negatively charged network oriented towards the nozzle. The in situ polarization degree is strengthened by higher amounts of clustered fibers, and therefore the initial high density fibrous regions are the preliminary motifs for the self-assembly mechanism. As such regions increase their in situ polarization electrostatic repulsive forces will appear, favoring a competitive growth of these self-assembled fibrous clusters. Highly polarized regions will evidence higher distances between consecutive micro-assembled fibers (MAFs). Different processing parameters - deposition time, electric field intensity, concentration of polymer solution, environmental temperature and relative humidity - were evaluated in an attempt to control material's design. Electronic supplementary information (ESI) available. See DOI: 10.1039/c3nr01668d

Training High School Students in the Scientific Method via Hands On Projects in a Laboratory Environment

DTIC Science & Technology

2015-02-27

Poly(vinylidene Fluoride with Trifluoroethylene) P(VDF-TrFE) 75:25 Thin Films by Atomic Force Microscope Nanolithography, Scanning, (04 2012): 0...doi: 10.1002/sca.21024 William Serrano, Nicholas J. Pinto. Electrospun Fibers of Poly(Vinylidene Fluoride -Trifluoroethylene)/Poly (3-Hexylthiophene...Nicholas Pinto. Electrospun fibers of poly (vinylidene fluoride -trifluoroethylene)/ poly (3- hexylthiophene) blends from tetrahydrofuran, National

Electrospun poly-l-lactide scaffold for the controlled and targeted delivery of a synthetically obtained Diclofenac prodrug to treat actinic keratosis.

PubMed

Piccirillo, Germano; Bochicchio, Brigida; Pepe, Antonietta; Schenke-Layland, Katja; Hinderer, Svenja

2017-04-01

Actinic Keratosis' (AKs) are small skin lesions that are related to a prolonged sun-damage, which can develop into invasive squamous cell carcinoma (SCC) when left untreated. Effective, specific and well tolerable therapies to cure AKs are still of great interest. Diclofenac (DCF) is the current gold standard for the local treatment of AKs in terms of costs, effectiveness, side effects and tolerability. In this work, an electrospun polylactic acid (PLA) scaffold loaded with a synthetic DCF prodrug was developed and characterized. Specifically, the prodrug was successfully synthetized by binding DCF to a glycine residue via solid phase peptide synthesis (SPPS) and then incorporated in an electrospun PLA scaffold. The drug encapsulation was verified using multiphoton microscopy (MPM) and its scaffold release was spectrophotometrically monitored and confirmed with MPM. The scaffold was further characterized with scanning electron microscopy (SEM), tensile testing and contact angle measurements. Its biocompatibility was verified by performing a cell proliferation assay and compared to PLA scaffolds containing the same amount of DCF sodium salt (DCFONa). Finally, the effect of the electrospun scaffolds on human dermal fibroblasts (HDFs) morphology and metabolism was investigated by combining MPM with fluorescence lifetime imaging microscopy (FLIM). The obtained results suggest that the obtained scaffold could be suitable for the controlled and targeted delivery of the synthesized prodrug for the treatment of AKs. Electrospun scaffolds are of growing interest as materials for a controlled drug delivery. In this work, an electrospun polylactic acid scaffold containing a synthetically obtained Diclofenac prodrug is proposed as a novel substrate for the topical treatment of actinic keratosis. A controlled drug delivery targeted to the area of interest could enhance the efficacy of the therapy and favor the healing process. The prodrug was synthesized via solid phase, employing a clean and versatile approach to obtain Diclofenac derivatives. Here, we used multiphoton microscopy to image drug encapsulation within the fibrous scaffold and fluorescence lifetime imaging microscopy to investigate Diclofenac effects and potential mechanisms of action. Copyright © 2016 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

Preparation of collagen/polyurethane/knitted silk as a composite scaffold for tendon tissue engineering.

PubMed

Sharifi-Aghdam, Maryam; Faridi-Majidi, Reza; Derakhshan, Mohammad Ali; Chegeni, Arash; Azami, Mahmoud

2017-07-01

The main objective of this study was to prepare a hybrid three-dimensional scaffold that mimics natural tendon tissues. It has been found that a knitted silk shows good mechanical strength; however, cell growth on the bare silk is not desirable. Hence, electrospun collagen/polyurethane combination was used to cover knitted silk. A series of collagen and polyurethane solutions (4%-7% w/v) in aqueous acetic acid were prepared and electrospun. According to obtained scanning electron microscopy images from pure collagen and polyurethane nanofibers, concentration was set constant at 5% (w/v) for blend solutions of collagen/polyurethane. Afterward, blend solutions with the weight ratios of 75/25, 50/50 and 25/75 were electrospun. Scanning electron microscopy images demonstrated the smooth and uniform morphology for the optimized nanofibers. The least fibers diameter among three weight ratios was found for collagen/polyurethane (25/75) which was 100.86 ± 40 nm and therefore was selected to be electrospun on the knitted silk. Attenuated total reflectance-Fourier transform infrared spectra confirmed the chemical composition of obtained electrospun nanofibers on the knitted silk. Tensile test of the specimens including blend nanofiber, knitted silk and commercial tendon substitute examined and indicated that collagen/polyurethane-coated knitted silk has appropriate mechanical properties as a scaffold for tendon tissue engineering. Then, Alamar Blue assay of the L929 fibroblast cell line seeded on the prepared scaffolds demonstrated appropriate viability of the cells with a significant proliferation on the scaffold containing more collagen content. The results illustrate that the designed structure would be promising for being used as a temporary substitute for tendon repair.

Cytotoxicity associated with electrospun polyvinyl alcohol.

PubMed

Pathan, Saif G; Fitzgerald, Lisa M; Ali, Syed M; Damrauer, Scott M; Bide, Martin J; Nelson, David W; Ferran, Christiane; Phaneuf, Tina M; Phaneuf, Matthew D

2015-11-01

Polyvinyl alcohol (PVA) is a synthetic, water-soluble polymer, with applications in industries ranging from textiles to biomedical devices. Research on electrospinning of PVA has been targeted toward optimizing or finding novel applications in the biomedical field. However, the effects of electrospinning on PVA biocompatibility have not been thoroughly evaluated. In this study, the cytotoxicity of electrospun PVA (nPVA) which was not crosslinked after electrospinning was assessed. PVA polymers of several molecular weights were dissolved in distilled water and electrospun using the same parameters. Electrospun PVA materials with varying molecular weights were then dissolved in tissue culture medium and directly compared against solutions of nonelectrospun PVA polymer in human coronary artery smooth muscle cells and human coronary artery endothelial cells cultures. All nPVA solutions were cytotoxic at a threshold molar concentration that correlated with the molecular weight of the starting PVA polymer. In contrast, none of the nonelectrospun PVA solutions caused any cytotoxicity, regardless of their concentration in the cell culture. Evaluation of the nPVA material by differential scanning calorimetry confirmed that polymer degradation had occurred after electrospinning. To elucidate the identity of the nPVA component that caused cytotoxicity, nPVA materials were dissolved, fractionated using size exclusion columns, and the different fractions were added to HCASMC and human coronary artery endothelial cells cultures. These studies indicated that the cytotoxic component of the different nPVA solutions were present in the low-molecular-weight fraction. Additionally, the amount of PVA present in the 3-10 kg/mol fraction was approximately sixfold greater than that in the nonelectrospun samples. In conclusion, electrospinning of PVA resulted in small-molecular-weight fractions that were cytotoxic to cells. This result demonstrates that biocompatibility of electrospun biodegradable polymers should not be assumed on the basis of success of their nonelectrospun predecessors. © 2015 Wiley Periodicals, Inc.

Viability of HEK 293 cells on poly-β-hydroxybutyrate (PHB) biosynthesized from a mutant Azotobacter vinelandii strain. Cast film and electrospun scaffolds.

PubMed

Romo-Uribe, Angel; Meneses-Acosta, Angelica; Domínguez-Díaz, Maraolina

2017-12-01

Sterilization, cytotoxicity and cell viability are essential properties defining a material for medical applications and these characteristics were investigated for poly(β-hydroxybutyrate) (PHB) of 230kDa obtained by bacterial synthesis from a mutant strain of Azotobacter vinelandii. Cell viability was investigated for two types of PHB scaffolds, solution cast films and non-woven electrospun fibrous membranes, and the efficiency was compared against a culture dish. The biosynthesized PHB was sterilized by ultraviolet radiation and autoclave, it was found that the thermal properties and intrinsic viscosity remained unchanged indicating that the sterilization methods did not degrade the polymer. Sterilized scaffolds were then seeded with human embryonic kidney 293 (HEK 293) cells to evaluate the cytotoxic response. The cell viability of these cells was evaluated for up to six days, and the results showed that the cell morphology was normal, with no cytotoxic effects. The films and electrospun membranes exhibited over 95% cell viability whereas the viability in culture dishes reached only ca. 90%. The electrospun membrane, however, exhibited significantly higher cell density than the cast film suggesting that the fibrous morphology enables better nutrients transfer. The results indicate that the biosynthesized PHB stands UV and autoclave sterilization methods, it is biocompatible and non-toxic for cell growth of human cell lines. Furthermore, cell culture for up to 18 days showed that 62% and 90% of mass was lost for the film and fibrous electrospun scaffold, respectively. This is a favorable outcome for use in tissue engineering where material degradation, as tissue regenerates, is desirable. Copyright © 2017 Elsevier B.V. All rights reserved.

An anisotropically and heterogeneously aligned patterned electrospun scaffold with tailored mechanical property and improved bioactivity for vascular tissue engineering.

PubMed

Xu, He; Li, Haiyan; Ke, Qinfei; Chang, Jiang

2015-04-29

The development of vascular scaffolds with controlled mechanical properties and stimulatory effects on biological activities of endothelial cells still remains a significant challenge to vascular tissue engineering. In this work, we reported an innovative approach to prepare a new type of vascular scaffolds with anisotropically and heterogeneously aligned patterns using electrospinning technique with unique wire spring templates, and further investigated the structural effects of the patterned electrospun scaffolds on mechanical properties and angiogenic differentiation of human umbilical vein endothelial cells (HUVECs). Results showed that anisotropically aligned patterned nanofibrous structure was obtained by depositing nanofibers on template in a structurally different manner, one part of nanofibers densely deposited on the embossments of wire spring and formed cylindrical-like structures in the transverse direction, while others loosely suspended and aligned along the longitudinal direction, forming a three-dimensional porous microstructure. We further found that such structures could efficiently control the mechanical properties of electrospun vascular scaffolds in both longitudinal and transverse directions by altering the interval distances between the embossments of patterned scaffolds. When HUVECs were cultured on scaffolds with different microstructures, the patterned scaffolds distinctively promoted adhesion of HUVECs at early stage and proliferation during the culture period. Most importantly, cells experienced a large shape change associated with cell cytoskeleton and nuclei remodeling, leading to a stimulatory effect on angiogenesis differentiation of HUVECs by the patterned microstructures of electrospun scaffolds, and the scaffolds with larger distances of intervals showed a higher stimulatory effect. These results suggest that electrospun scaffolds with the anisotropically and heterogeneously aligned patterns, which could efficiently control the mechanical properties and bioactivities of the scaffolds, might have great potential in vascular tissue engineering application.

Image-based quantification of fiber alignment within electrospun tissue engineering scaffolds is related to mechanical anisotropy.

PubMed

Fee, Timothy; Downs, Crawford; Eberhardt, Alan; Zhou, Yong; Berry, Joel

2016-07-01

It is well documented that electrospun tissue engineering scaffolds can be fabricated with variable degrees of fiber alignment to produce scaffolds with anisotropic mechanical properties. Several attempts have been made to quantify the degree of fiber alignment within an electrospun scaffold using image-based methods. However, these methods are limited by the inability to produce a quantitative measure of alignment that can be used to make comparisons across publications. Therefore, we have developed a new approach to quantifying the alignment present within a scaffold from scanning electron microscopic (SEM) images. The alignment is determined by using the Sobel approximation of the image gradient to determine the distribution of gradient angles with an image. This data was fit to a Von Mises distribution to find the dispersion parameter κ, which was used as a quantitative measure of fiber alignment. We fabricated four groups of electrospun polycaprolactone (PCL) + Gelatin scaffolds with alignments ranging from κ = 1.9 (aligned) to κ = 0.25 (random) and tested our alignment quantification method on these scaffolds. It was found that our alignment quantification method could distinguish between scaffolds of different alignments more accurately than two other published methods. Additionally, the alignment parameter κ was found to be a good predictor the mechanical anisotropy of our electrospun scaffolds. The ability to quantify fiber alignment within and make direct comparisons of scaffold fiber alignment across publications can reduce ambiguity between published results where cells are cultured on "highly aligned" fibrous scaffolds. This could have important implications for characterizing mechanics and cellular behavior on aligned tissue engineering scaffolds. © 2016 Wiley Periodicals, Inc. J Biomed Mater Res Part A: 104A: 1680-1686, 2016. © 2016 Wiley Periodicals, Inc.

Electrospun poly(ε-caprolactone) matrices containing silver sulfadiazine complexed with β-cyclodextrin as a new pharmaceutical dosage form to wound healing: preliminary physicochemical and biological evaluation.

PubMed

Souza, Sarah Oliveira Lamas; Cotrim, Monique Alvarenga Pinto; Oréfice, Rodrigo Lambert; Carvalho, Suzana Gonçalves; Dutra, Jessyca Aparecida Paes; de Paula Careta, Francisco; Resende, Juliana Alves; Villanova, Janaina Cecília Oliveira

2018-05-10

Cooperation between researchers in the areas of medical, pharmaceutical and materials science has facilitated the development of pharmaceutical dosage forms that elicit therapeutic effects and protective action with a single product. In addition to optimizing pharmacologic action, such dosage forms provide greater patient comfort and increase success and treatment compliance. In the present work, we prepared semipermeable bioactive electrospun fibers for use as wound dressings containing silver sulfadiazine complexed with β-cyclodextrin in a poly(Ɛ-caprolactone) nanofiber matrix aiming to reduce the direct contact between silver and skin and to modulate the drug release. Wound dressings were prepared by electrospinning, and were subjected to ATR-FT-IR and TG/DTG assays to evaluate drug stability. The hydrophilicity of the fibrous nanostructure in water and PBS buffer was studied by goniometry. Electrospun fibers permeability and swelling capacity were assessed, and a dissolution test was performed. In vitro biological tests were realized to investigate the biological compatibility and antimicrobial activity. We obtained flexible matrices that were each approximately 1.0 g in weight. The electrospun fibers were shown to be semipermeable, with water vapor transmission and swelling indexes compatible with the proposed objective. The hydrophilicity was moderate. Matrices containing pure drug modulated drug release adequately during 24 h but presented a high hemolytic index. Complexation promoted a decrease in the hemolytic index and in the drug release but did not negatively impact antimicrobial activity. The drug was released predominantly by diffusion. These results indicate that electrospun PCL matrices containing β-cyclodextrin/silver sulfadiazine inclusion complexes are a promising pharmaceutical dosage form for wound healing.

Fabrication of AlN/BN bishell hollow nanofibers by electrospinning and atomic layer deposition

DOE Office of Scientific and Technical Information (OSTI.GOV)

Haider, Ali; Kayaci, Fatma; Uyar, Tamer

2014-09-01

Aluminum nitride (AlN)/boron nitride (BN) bishell hollow nanofibers (HNFs) have been fabricated by successive atomic layer deposition (ALD) of AlN and sequential chemical vapor deposition (CVD) of BN on electrospun polymeric nanofibrous template. A four-step fabrication process was utilized: (i) fabrication of polymeric (nylon 6,6) nanofibers via electrospinning, (ii) hollow cathode plasma-assisted ALD of AlN at 100 °C onto electrospun polymeric nanofibers, (iii) calcination at 500 °C for 2 h in order to remove the polymeric template, and (iv) sequential CVD growth of BN at 450 °C. AlN/BN HNFs have been characterized for their chemical composition, surface morphology, crystal structure, and internal nanostructuremore » using X-ray photoelectron spectroscopy, scanning electron microscopy, transmission electron microscopy, energy dispersive X-ray spectroscopy, and selected area electron diffraction. Measurements confirmed the presence of crystalline hexagonal BN and AlN within the three dimensional (3D) network of bishell HNFs with relatively low impurity content. In contrast to the smooth surface of the inner AlN layer, outer BN coating showed a highly rough 3D morphology in the form of BN nano-needle crystallites. It is shown that the combination of electrospinning and plasma-assisted low-temperature ALD/CVD can produce highly controlled multi-layered bishell nitride ceramic hollow nanostructures. While electrospinning enables easy fabrication of nanofibrous template, self-limiting reactions of plasma-assisted ALD and sequential CVD provide control over the wall thicknesses of AlN and BN layers with sub-nanometer accuracy.« less

All-textile flexible supercapacitors using electrospun poly(3,4-ethylenedioxythiophene) nanofibers

NASA Astrophysics Data System (ADS)

Laforgue, Alexis

Poly(3,4-ethylenedioxythiophene) (PEDOT) nanofibers were obtained by the combination of electrospinning and vapor-phase polymerization. The fibers had diameters around 350 nm, and were soldered at most intersections, providing a strong dimensional stability to the mats. The nanofiber mats demonstrated very high conductivity (60 ± 10 S cm -1, the highest value reported so far for polymer nanofibers) as well as improved electrochemical properties, due to the ultraporous nature of the electrospun mats. The mats were incorporated into all-textile flexible supercapacitors, using carbon cloths as the current collectors and electrospun polyacrylonitrile (PAN) nanofibrous membranes as the separator. The textile layers were stacked and embedded in a solid electrolyte containing an ionic liquid and PVDF-co-HFP as the host polymer. The resulting supercapacitors were totally flexible and demonstrated interesting and stable performances in ambient conditions.

Advances in skin regeneration: application of electrospun scaffolds.

PubMed

Norouzi, Mohammad; Boroujeni, Samaneh Moghadasi; Omidvarkordshouli, Noushin; Soleimani, Masoud

2015-06-03

The paucity of cellular and molecular signals essential for normal wound healing makes severe dermatological ulcers stubborn to heal. The novel strategies of skin regenerative treatments are focused on the development of biologically responsive scaffolds accompanied by cells and multiple biomolecules resembling structural and biochemical cues of the natural extracellular matrix (ECM). Electrospun nanofibrous scaffolds provide similar architecture to the ECM leading to enhancement of cell adhesion, proliferation, migration and neo tissue formation. This Review surveys the application of biocompatible natural, synthetic and composite polymers to fabricate electrospun scaffolds as skin substitutes and wound dressings. Furthermore, the application of biomolecules and therapeutic agents in the nanofibrous scaffolds viz growth factors, genes, antibiotics, silver nanoparticles, and natural medicines with the aim of ameliorating cellular behavior, wound healing, and skin regeneration are discussed. © 2015 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Electrospinning of PVC with natural rubber

NASA Astrophysics Data System (ADS)

Othman, Muhammad Hariz; Mohamed, Mahathir; Abdullah, Ibrahim

2013-11-01

Polyvinyl chloride (PVC) was mixed with natural rubbers which are liquid natural rubber (LNR), liquid epoxidised natural rubber (LENR) and liquid epoxidised natural rubber acrylate (LENRA) for a preparation of a fine non-woven fiber's mat. PVC and each natural rubbers(PVC:LENR, PVC:LNR and PVC:LENRA) were mixed based on ratio of 70:30. Electrospinning method was used to prepare the fiber. The results show that the spinnable concentration of PVC/ natural rubber/THF solution is 16 wt%. The morphology, diameter, structure and degradation temperature of electrospun fibers were investigated by scanning electron microscopy (SEM) and thermogravimetric analysis (TGA). SEM photos showed that the morphology and diameter of the fibers were mainly affected by the addition of natural rubber. TGA results suggested that PVC electrospun fiber has higher degradation temperature than those electrospun fibers that contain natural rubber.

Electrospun nanofibrous 3D scaffold for bone tissue engineering.

PubMed

Eap, Sandy; Ferrand, Alice; Palomares, Carlos Mendoza; Hébraud, Anne; Stoltz, Jean-François; Mainard, Didier; Schlatter, Guy; Benkirane-Jessel, Nadia

2012-01-01

Tissue engineering aims at developing functional substitutes for damaged tissues by mimicking natural tissues. In particular, tissue engineering for bone regeneration enables healing of some bone diseases. Thus, several methods have been developed in order to produce implantable biomaterial structures that imitate the constitution of bone. Electrospinning is one of these methods. This technique produces nonwoven scaffolds made of nanofibers which size and organization match those of the extracellular matrix. Until now, seldom electrospun scaffolds were produced with thickness exceeding one millimeter. This article introduces a new kind of electrospun membrane called 3D scaffold of thickness easily exceeding one centimeter. The manufacturing involves a solution of poly(ε-caprolactone) in DMF/DCM system. The aim is to establish parameters for electrospinning in order to characterize these 3D scaffolds and, establish whether such scaffolds are potentially interesting for bone regeneration.

Highly efficient hybrid energy generator: coupled organic photovoltaic device and randomly oriented electrospun poly(vinylidene fluoride) nanofiber.

PubMed

Park, Boongik; Lee, Kihwan; Park, Jongjin; Kim, Jongmin; Kim, Ohyun

2013-03-01

A hybrid architecture consisting of an inverted organic photovoltaic device and a randomly-oriented electrospun PVDF piezoelectric device was fabricated as a highly-efficient energy generator. It uses the inverted photovoltaic device with coupled electrospun PVDF nanofibers as tandem structure to convert solar and mechanical vibrations energy to electricity simultaneously or individually. The power conversion efficiency of the photovoltaic device was also significantly improved up to 4.72% by optimized processes such as intrinsic ZnO, MoO3 and active layer. A simple electrospinning method with the two electrode technique was adopted to achieve a high voltage of - 300 mV in PVDF piezoelectric fibers. Highly-efficient HEG using voltage adder circuit provides the conceptual possibility of realizing multi-functional energy generator whenever and wherever various energy sources are available.

In Vivo Evaluation of Electrospun Polycaprolactone Graft for Anterior Cruciate Ligament Engineering

PubMed Central

Arom, Gabriel A.; Nazemi, Azadeh N.; Yeranosian, Michael G.; Wu, Benjamin M.; McAllister, David R.

2015-01-01

The anterior cruciate ligament (ACL) is critical for the structural stability of the knee and its injury often requires surgical intervention. Because current reconstruction methods using autograft or allograft tissue suffer from donor-site morbidity and limited supply, there has been emerging interest in the use of bioengineered materials as a platform for ligament reconstruction. Here, we report the use of electrospun polycaprolactone (PCL) scaffolds as a candidate platform for ACL reconstruction in an in vivo rodent model. Electrospun PCL was fabricated and laser cut to facilitate induction of cells and collagen deposition and used to reconstruct the rat ACL. Histological analysis at 2, 6, and 12 weeks postimplantation revealed biological integration, minimal immune response, and the gradual infiltration of collagen in both the bone tunnel and intra-articular regions of the scaffold. Biomechanical testing demonstrated that the PCL graft failure load and stiffness at 12 weeks postimplantation (13.27±4.20N, 15.98±5.03 N/mm) increased compared to time zero testing (3.95±0.33N, 1.95±0.35 N/mm). Taken together, these results suggest that electrospun PCL serves as a biocompatible graft for ACL reconstruction with the capacity to facilitate collagen deposition. PMID:25412879

Electrospun Blends of Gelatin and Gelatin-dendrimer Conjugates as a Wound Dressing and Drug Delivery Platform

PubMed Central

Dongargaonkar, Alpana A.; Bowlin, Gary L.; Yang, Hu

2013-01-01

In this work, we report a new nanofiber construct based on electrospun blends of gelatin and gelatin-dendrimer conjugates. Highly branched star-shaped polyamidoamine (PAMAM) dendrimer G3.5 was covalently conjugated to gelatin via EDC/NHS chemistry. Blends of gelatin and gelatin-dendrimer conjugates mixed with various loading levels of silver acetate (0, 0.83, 1.65, and 3.30% w/w) were successfully electrospun into nanofiber constructs (NCs). The NCs were further converted into semi-interpenetrating networks (sIPNs) with photoreactive polyethylene glycol diacrylate (Mn=575 gmol-1) (PEG DA575). They were characterized in terms of fiber morphology, diameter, pore size, permeability, degradation, and mechanical properties. The resulting sIPN NCs retained nanofiber morphology, possessed similar fiber diameters to counterpart NCs, and gained improved structural stability. The sIPN NCs also showed good swelling capacity owing to porous structures and were permeable to aqueous solutions. Silvercontaining sIPN NCs allowed sustained silver release and showed antimicrobial activity against two common types of pathogens—Staphylococcus aureus and Pseudomonas aeruginosa. Incorporation of dendrimers into the gelatin nanofibers through covalent conjugation not only expands drug loading capacity of nanofiber constructs but provides tremendous flexibility for developing multifunctional electrospun dressing materials. PMID:24127747

Piezoelectric Response of Aligned Electrospun Polyvinylidene Fluoride/Carbon Nanotube Nanofibrous Membranes.

PubMed

Wu, Chang-Mou; Chou, Min-Hui; Zeng, Wun-Yuan

2018-06-10

Polyvinylidene fluoride (PVDF) shows piezoelectricity related to its β-phase content and mechanical and electrical properties influenced by its morphology and crystallinity. Electrospinning (ES) can produce ultrafine and well-aligned PVDF nanofibers. In this study, the effects of the presence of carbon nanotubes (CNT) and optimized ES parameters on the crystal structures and piezoelectric properties of aligned PVDF/CNT nanofibrous membranes were examined. The optimal β content and piezoelectric coefficient (d 33 ) of the aligned electrospun PVDF reached 88% and 27.4 pC/N; CNT addition increased the β-phase content to 89% and d 33 to 31.3 pC/N. The output voltages of piezoelectric units with aligned electrospun PVDF/CNT membranes increased linearly with applied loading and showed good stability during cyclic dynamic compression and tension. The sensitivities of the piezoelectric units with the membranes under dynamic compression and tension were 2.26 mV/N and 4.29 mV/%, respectively. In bending tests, the output voltage increased nonlinearly with bending angle because complicated forces were involved. The output of the aligned membrane-based piezoelectric unit with CNT was 1.89 V at the bending angle of 100°. The high electric outputs indicate that the aligned electrospun PVDF/CNT membranes are potentially effective for flexible wearable sensor application with high sensitivity.

Comparison of Adsorption/Desorption of Volatile Organic Compounds (VOCs) on Electrospun Nanofibers with Tenax TA for Potential Application in Sampling

PubMed Central

Chu, Lanling; Deng, Siwei; Zhao, Renshan; Deng, Jianjun; Kang, Xuejun

2016-01-01

The objective of this study was to compare the adsorption/desorption of target compounds on homemade electrospun nanofibers, polystyrene (PS) nanofibers, acrylic resin (AR) nanofibers and PS-AR composite nanofibers with Tenax TA. Ten volatile organic compounds (VOCs) were analyzed by preconcentration onto different sorbents followed by desorption (thermal and solvent orderly) and analysis by capillary gas chromatography. In comparison to Tenax TA, the electrospun nanofibers displayed a significant advantage in desorption efficiency and adsorption selectivity. Stability studies were conducted as a comparative experiment between PS-AR nanofibers and Tenax TA using toluene as the model compound. No stability problems were observed upon storage of toluene on both PS-AR nanofibers and Tenax TA over 60 hours period when maintained in an ultra-freezer (−80°C). The nanofibers provided slightly better stability for the adsorbed analytes than Tenax TA under other storage conditions. In addition, the nanofibers also provided slightly better precision than Tenax TA. The quantitative adsorption of PS-AR nanofibers exhibited a good linearity, as evidenced by the 0.988–0.999 range of regression coefficients (R). These results suggest that for VOCs sampling the electrospun nanofibers can be a potential ideal adsorbent. PMID:27776140

Incorporating Platelet-Rich Plasma into Electrospun Scaffolds for Tissue Engineering Applications

PubMed Central

Wolfe, Patricia S.; Ericksen, Jeffery J.; Simpson, David G.; Bowlin, Gary L.

2011-01-01

Platelet-rich plasma (PRP) therapy has seen a recent spike in clinical interest due to the potential that the highly concentrated platelet solutions hold for stimulating tissue repair and regeneration. The aim of this study was to incorporate PRP into a number of electrospun materials to determine how growth factors are eluted from the structures, and what effect the presence of these factors has on enhancing electrospun scaffold bioactivity. PRP underwent a freeze-thaw-freeze process to lyse platelets, followed by lyophilization to create a powdered preparation rich in growth factors (PRGF), which was subsequently added to the electrospinning process. Release of protein from scaffolds over time was quantified, along with the quantification of human macrophage and adipose-derived stem cell (ADSC) chemotaxis and proliferation. Protein assays demonstrated a sustained release of protein from PRGF-containing scaffolds at up to 35 days in culture. Scaffold bioactivity was enhanced as ADSCs demonstrated increased proliferation in the presence of PRGF, whereas macrophages demonstrated increased chemotaxis to PRGF. In conclusion, the work performed in this study demonstrated that the incorporation of PRGF into electrospun structures has a significant positive influence on the bioactivity of the scaffolds, and may prove beneficial in a number of tissue engineering applications. PMID:21679135

Post-processing optimization of electrospun submicron poly(3-hydroxybutyrate) fibers to obtain continuous films of interest in food packaging applications.

PubMed

Cherpinski, Adriane; Torres-Giner, Sergio; Cabedo, Luis; Lagaron, Jose M

2017-10-01

Polyhydroxyalkanoates (PHAs) are one of the most researched family of biodegradable polymers based on renewable materials due to their thermoplastic nature and moisture resistance. The present study was targeted to investigate the preparation and characterization of poly(3-hydroxybutyrate) (PHB) films obtained through the electrospinning technique. To convert them into continuous films and then to increase their application interest in packaging, the electrospun fiber mats were subsequently post-processed by different physical treatments. Thus, the effect of annealing time and cooling method on morphology, molecular order, thermal, optical, mechanical, and barrier properties of the electrospun submicron PHB fibers was studied. Annealing at 160°C, well below the homopolyester melting point, was found to be the minimum temperature at which homogeneous transparent films were produced. The film samples that were cooled slowly after annealing showed the lowest permeability to oxygen, water vapor, and limonene. The optimally post-processed electrospun PHB fibers exhibited similar rigidity to conventional compression-molded PHA films, but with enhanced elongation at break and toughness. Films made by this electrospinning technique have many potential applications, such as in the design of barrier layers, adhesive interlayers, and coatings for fiber- and plastic-based food packaging materials.

Increasing the pore sizes of bone-mimetic electrospun scaffolds comprised of polycaprolactone, collagen I and hydroxyapatite to enhance cell infiltration

PubMed Central

Phipps, Matthew C.; Clem, William C.; Grunda, Jessica M.; Clines, Gregory A.; Bellis, Susan L.

2012-01-01

Bone-mimetic electrospun scaffolds consisting of polycaprolactone (PCL), collagen I and nanoparticulate hydroxyapatite (HA) have previously been shown to support the adhesion, integrin-related signaling and proliferation of mesenchymal stem cells (MSCs), suggesting these matrices serve as promising degradable substrates for osteoregeneration. However, the small pore sizes in electrospun scaffolds hinder cell infiltration in vitro and tissue-ingrowth into the scaffold in vivo, limiting their clinical potential. In this study, three separate techniques were evaluated for their capability to increase the pore size of the PCL/col I/nanoHA scaffolds: limited protease digestion, decreasing the fiber packing density during electro-spinning, and inclusion of sacrificial fibers of the water-soluble polymer PEO. The PEO sacrificial fiber approach was found to be the most effective in increasing scaffold pore size. Furthermore, the use of sacrificial fibers promoted increased MSC infiltration into the scaffolds, as well as greater infiltration of endogenous cells within bone upon placement of scaffolds within calvarial organ cultures. These collective findings support the use of sacrificial PEO fibers as a means to increase the porosity of complex, bone-mimicking electrospun scaffolds, thereby enhancing tissue regenerative processes that depend upon cell infiltration, such as vascularization and replacement of the scaffold with native bone tissue. PMID:22014462

Cellularized cylindrical fiber/hydrogel composites for ligament tissue engineering.

PubMed

Thayer, Patrick S; Dimling, Anna F; Plessl, Daniel S; Hahn, Mariah R; Guelcher, Scott A; Dahlgren, Linda A; Goldstein, Aaron S

2014-01-13

Electrospun meshes suffer from poor cell infiltration and limited thickness, which restrict their use to thin tissue applications. Herein, we demonstrate two complementary processes to overcome these limitations and achieve elastomeric composites that may be suitable for ligament repair. First, C3H10T1/2 mesenchymal stem cells were incorporated into electrospun meshes using a hybrid electrospinning/electrospraying process. Second, electrospun meshes were rolled and formed into composites with an interpenetrating polyethylene glycol (PEG) hydrogel network. Stiffer composites were formed from poly(lactic-co-glycolic acid) (PLGA) meshes, while softer and more elastic composites were formed from poly(ester-urethane urea) (PEUUR) meshes. As-spun PLGA and PEUUR rolled meshes had tensile moduli of 19.2 ± 1.9 and 0.86 ± 0.34 MPa, respectively, which changed to 11.6 ± 4.8 and 1.05 ± 0.39 MPa with the incorporation of a PEG hydrogel phase. In addition, cyclic tensile testing indicated that PEUUR-based composites deformed elastically to at least 10%. Finally, C3H10T1/2 cells incorporated into electrospun meshes survived the addition of the PEG phase and remained viable for up to 5 days. These results indicate that the fabricated cellularized composites are support cyclic mechanical conditioning, and have potential application in ligament repair.

In vivo evaluation of electrospun polycaprolactone graft for anterior cruciate ligament engineering.

PubMed

Petrigliano, Frank A; Arom, Gabriel A; Nazemi, Azadeh N; Yeranosian, Michael G; Wu, Benjamin M; McAllister, David R

2015-04-01

The anterior cruciate ligament (ACL) is critical for the structural stability of the knee and its injury often requires surgical intervention. Because current reconstruction methods using autograft or allograft tissue suffer from donor-site morbidity and limited supply, there has been emerging interest in the use of bioengineered materials as a platform for ligament reconstruction. Here, we report the use of electrospun polycaprolactone (PCL) scaffolds as a candidate platform for ACL reconstruction in an in vivo rodent model. Electrospun PCL was fabricated and laser cut to facilitate induction of cells and collagen deposition and used to reconstruct the rat ACL. Histological analysis at 2, 6, and 12 weeks postimplantation revealed biological integration, minimal immune response, and the gradual infiltration of collagen in both the bone tunnel and intra-articular regions of the scaffold. Biomechanical testing demonstrated that the PCL graft failure load and stiffness at 12 weeks postimplantation (13.27±4.20N, 15.98±5.03 N/mm) increased compared to time zero testing (3.95±0.33N, 1.95±0.35 N/mm). Taken together, these results suggest that electrospun PCL serves as a biocompatible graft for ACL reconstruction with the capacity to facilitate collagen deposition.

Electrospun PVDF fibers and a novel PVDF/CoFe2O4 fibrous composite as nanostructured sorbent materials for oil spill cleanup

NASA Astrophysics Data System (ADS)

Dorneanu, Petronela Pascariu; Cojocaru, Corneliu; Olaru, Niculae; Samoila, Petrisor; Airinei, Anton; Sacarescu, Liviu

2017-12-01

In this work, pure polyvinylidene fluoride (PVDF) and PVDF/cobalt ferrite (CoFe2O4) magnetic fibrous composite were successfully prepared by electrospinning method for oil spill sorption applications. The pure spinel phase of CoFe2O4 and PVDF/CoFe2O4 composites were confirmed by X-ray diffraction analysis (XRD). Electrospun sorbent materials were characterized by scanning and transmission electron microscopy (SEM and TEM) as well as by contact angle measurements. In addition, the composite sorbent (PVDF/CoFe2O4) was characterized by magnetic measurements. It revealed good magnetic properties that are of real interest to facilitate the separation of the oil-loaded sorbent under the external magnetic field. Finally, the produced electrospun sorbents were tested for sorption of oily liquids, such as: decane, dodecane and commercial motor oils. We obtained good oil sorption capacity (between 9.751-23.615 g/g of pure PVDF) and (8.133-18.074 g/g for the magnetic composite) depending on the nature of oil tested. The present electrospun magnetic PVDF/CoFe2O4 fibrous composite could be potentially useful for the efficient removal of oil in water and recovery of sorbent material.

A high-performance polydimethylsiloxane electrospun membrane for cell culture in lab-on-a-chip.

PubMed

Moghadas, Hajar; Saidi, Mohammad Said; Kashaninejad, Navid; Nguyen, Nam-Trung

2018-03-01

Thin porous membranes are important components in a microfluidic device, serving as separators, filters, and scaffolds for cell culture. However, the fabrication and the integration of these membranes possess many challenges, which restrict their widespread applications. This paper reports a facile technique to fabricate robust membrane-embedded microfluidic devices. We integrated an electrospun membrane into a polydimethylsiloxane (PDMS) device using the simple plasma-activated bonding technique. To increase the flexibility of the membrane and to address the leakage problem, the electrospun membrane was fabricated with the highest weight ratio of PDMS to polymethylmethacrylate (i.e., 6:1 w/w). The membrane-integrated microfluidic device could withstand a flow rate of up to 50  μ l/min. As a proof of concept, we demonstrated that such a compartmentalized microfluidic platform could be successfully used for cell culture with the capability of providing a more realistic in vivo -like condition. Human lung cancer epithelial cells (A549) were seeded on the membrane from the top microchannel, while the continuous flow of the culture medium through the bottom microchannel provided a shear-free cell culture condition. The tortuous micro-/nanofibers of the membrane immobilized the cells within the hydrophobic micropores and with no need of extracellular matrix for cell adhesion and cell growth. The hydrophobic surface conditions of the membrane were suitable for anchorage-independent cell types. To further extend the application of the device, we qualitatively showed that rinsing the membrane with ethanol prior to cell seeding could temporarily render the membrane hydrophilic and the platform could also be used for anchorage-dependent cells. Due to the three-dimensional (3D) topography of the membranes, three different configurations were observed, including individual single cells, monolayer cells, and 3D cell clusters. This cost-effective and robust compartmentalized microfluidic device may open up new avenues in translational medicine and pharmacodynamics research.

Bilateral PLA/alginate membranes for the prevention of postsurgical adhesions.

PubMed

Kessler, Martina; Esser, Eva; Groll, Jürgen; Tessmar, Jörg

2016-11-01

A bilateral barrier membrane for the prevention of postsurgical adhesions was developed. Thereby, a smooth PLA side was supposed to keep the affected tissues glidingly separated, while a mucoadhesive side made of alginate was meant to keep the barrier resident on the site of injury so that suturing becomes redundant or at least the membrane stays long enough to facilitate surgical handling. Because hydrophilic alginate and lipophilic PLA films show only low cohesion, solution electrospun meshes of PLA and PLA-PEG-PLA triblock copolymers with varying poly(ethylene glycol) [PEG] content were investigated as cohesion promoter to avoid an easy separation of the functionally different layers. Using direct electrospinning onto the PLA film, a modified contact surface of the mesh was created, which allowed the tested alginate solutions (3%, 5%) to infiltrate to different extents. Thereby, an increasing content of hydrophilic PEG within the mesh copolymer and a lower alginate concentration facilitated the infiltration. As a result, the PLA film with a PLA35k-PEG10k-PLA35k (racemic PLA chains) mesh and an alginate layer cast from a 3% alginate solution appeared to be the most effective combination as examined by means of a t peel test, a mucoadhesion test, a tensile test and optical evaluations. © 2015 Wiley Periodicals, Inc. J Biomed Mater Res Part B: Appl Biomater, 104B: 1563-1570, 2016. © 2015 Wiley Periodicals, Inc.

A Comparison of Electrospun Polymers Reveals Poly(3-Hydroxybutyrate) Fiber as a Superior Scaffold for Cardiac Repair

PubMed Central

Castellano, Delia; Blanes, María; Marco, Bruno; Cerrada, Inmaculada; Ruiz-Saurí, Amparo; Pelacho, Beatriz; Araña, Miriam; Montero, Jose A.; Cambra, Vicente; Prosper, Felipe

2014-01-01

The development of biomaterials for myocardial tissue engineering requires a careful assessment of their performance with regards to functionality and biocompatibility, including the immune response. Poly(3-hydroxybutyrate) (PHB), poly(e-caprolactone) (PCL), silk, poly-lactic acid (PLA), and polyamide (PA) scaffolds were generated by electrospinning, and cell compatibility in vitro, and immune response and cardiac function in vitro and in vivo were compared with a noncrosslinked collagen membrane (Col) control material. Results showed that cell adhesion and growth of mesenchymal stem cells, cardiomyocytes, and cardiac fibroblasts in vitro was dependent on the polymer substrate, with PHB and PCL polymers permitting the greatest adhesion/growth of cells. Additionally, polymer substrates triggered unique expression profiles of anti- and pro-inflammatory cytokines in human peripheral blood mononuclear cells. Implantation of PCL, silk, PLA, and PA patches on the epicardial surface of healthy rats induced a classical foreign body reaction pattern, with encapsulation of polymer fibers and induction of the nonspecific immune response, whereas Col and PHB patches were progressively degraded. When implanted on infarcted rat heart, Col, PCL, and PHB reduced negative remodeling, but only PHB induced significant angiogenesis. Importantly, Col and PHB modified the inflammatory response to an M2 macrophage phenotype in cardiac tissue, indicating a more beneficial reparative process and remodeling. Collectively, these results identify PHB as a superior substrate for cardiac repair. PMID:24564648

Quantitative Comparison of Enzyme Immobilization Strategies for Glucose Biosensing in Real-Time Using Fast-Scan Cyclic Voltammetry Coupled with Carbon-Fiber Microelectrodes.

PubMed

Smith, Samantha K; Lugo-Morales, Leyda Z; Tang, C; Gosrani, Saahj P; Lee, Christie A; Roberts, James G; Morton, Stephen W; McCarty, Gregory S; Khan, Saad A; Sombers, Leslie A

2018-05-22

Electrochemical monitoring of non-electroactive species requires a biosensor that is stable and selective, with sensitivity to physiological concentrations of targeted analytes. We have combined glucose oxidase-modified carbon-fiber microelectrodes with fast-scan cyclic voltammetry for real-time measurements of glucose fluctuations in brain tissue. Work presented herein quantitatively compares three approaches to enzyme immobilization on the microelectrode surface-physical adsorption, hydrogel entrapment, and entrapment in electrospun nanofibers. The data suggest that each of these methods can be used to create functional microbiosensors. Immobilization of glucose oxidase by physical adsorption generates a biosensor with poor sensitivity to glucose and unstable performance. Entrapment of glucose oxidase in poly(vinyl alcohol) nanofibers generates microbiosensors that are effective for glucose measurements over a large linear range, and that may be particularly useful when targeting glucose concentrations in excess of 3 mm, such as in blood. Hydrogel entrapment is the most effective in terms of sensitivity and stability. These microbiosensors can be used for simultaneous monitoring of glucose and dopamine in real time. The findings outlined herein should be applicable to other oxidase enzymes, and thus they are broadly important for the development of new tools for real-time measurements of fluctuating molecules that are not inherently electroactive. © 2018 Wiley-VCH Verlag GmbH & Co. KGaA, Weinheim.

Biochemical profiling of rat embryonic stem cells grown on electrospun polyester fibers using synchrotron infrared microspectroscopy.

PubMed

Doncel-Pérez, Ernesto; Ellis, Gary; Sandt, Christophe; Shuttleworth, Peter S; Bastida, Agatha; Revuelta, Julia; García-Junceda, Eduardo; Fernández-Mayoralas, Alfonso; Garrido, Leoncio

2018-06-01

Therapeutic options for spinal cord injuries are severely limited; current treatments only offer symptomatic relief and rehabilitation focused on educating the individual on how to adapt to their new situation to make best possible use of their remaining function. Thus, new approaches are needed, and interest in the development of effective strategies to promote the repair of neural tracts in the central nervous system inspired us to prepare functional and highly anisotropic polymer scaffolds. In this work, an initial assessment of the behavior of rat neural progenitor cells (NPCs) seeded on poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) fiber scaffolds using synchrotron-based infrared microspectroscopy (SIRMS) is described. Combined with a modified touch imprint cytology sample preparation method, this application of SIRMS enabled the biochemical profiles of NPCs on the coated polymer fibers to be determined. The results showed that changes in the lipid and amide I-II spectral regions are modulated by the type and coating of the substrate used and the culture time. SIRMS studies can provide valuable insight into the early-stage response of NPCs to the morphology and surface chemistry of a biomaterial, and could therefore be a useful tool in the preparation and optimization of cellular scaffolds. Graphical abstract Synchrotron IR microspectroscopy can provide insight into the response of neural progenitor cells to synthetic scaffolds.

A flexible electrostatic kinetic energy harvester based on electret films of electrospun nanofibers

NASA Astrophysics Data System (ADS)

Lu, Y.; Capo-Chichi, M.; Leprince-Wang, Y.; Basset, P.

2018-01-01

This paper reports a paper-based electrostatic kinetic energy harvester (e-KEH) implementing multilayered electret films based on electrospun nanofibrous material. It is the first time that a fully flexible electret-based e-KEH is reported. The proposed electret, PVDF-PTFD nanofibrous covered by Parylene C, has a faster stabilization of surface potential than a planar thin film of Parylene C, and a higher stability of charge storage. With a maximum force of 0.5 N and a 3-layer electret, the device capacitance increases from 25 to 100 pF during a pressing operation. Working with the optimal resistive load of 16 MΩ, the device pressed manually delivers a peak instantaneous power up to 45.6 μW and an average energy of 54 nJ/stroke, corresponding to a peak instantaneous power density of 7.3 μW cm-2 and an average energy density of 8.6 nJ cm-2/stroke. Within 450 manual strokes, a 10 nF capacitor is charged up to 8.5 V by the prototype through a full-wave diode bridge. On a 1 μF capacitor, the energy delivery of 9.9 nJ/stroke has been obtained with a 10 Hz pressing movement excited by a vibrator with a maximum force of 0.5 N.

Improved capacitance characteristics of electrospun ACFs by pore size control and vanadium catalyst.

PubMed

Im, Ji Sun; Woo, Sang-Wook; Jung, Min-Jung; Lee, Young-Seak

2008-11-01

Nano-sized carbon fibers were prepared by using electrospinning, and their electrochemical properties were investigated as a possible electrode material for use as an electric double-layer capacitor (EDLC). To improve the electrode capacitance of EDLC, we implemented a three-step optimization. First, metal catalyst was introduced into the carbon fibers due to the excellent conductivity of metal. Vanadium pentoxide was used because it could be converted to vanadium for improved conductivity as the pore structure develops during the carbonization step. Vanadium catalyst was well dispersed in the carbon fibers, improving the capacitance of the electrode. Second, pore-size development was manipulated to obtain small mesopore sizes ranging from 2 to 5 nm. Through chemical activation, carbon fibers with controlled pore sizes were prepared with a high specific surface and pore volume, and their pore structure was investigated by using a BET apparatus. Finally, polyacrylonitrile was used as a carbon precursor to enrich for nitrogen content in the final product because nitrogen is known to improve electrode capacitance. Ultimately, the electrospun activated carbon fibers containing vanadium show improved functionality in charge/discharge, cyclic voltammetry, and specific capacitance compared with other samples because of an optimal combination of vanadium, nitrogen, and fixed pore structures.

Enhancement of stem cell differentiation to osteogenic lineage on hydroxyapatite-coated hybrid PLGA/gelatin nanofiber scaffolds.

PubMed

Sanaei-Rad, Parisa; Jafarzadeh Kashi, Tahereh-Sadat; Seyedjafari, Ehsan; Soleimani, Masoud

2016-11-01

A combination of polymeric materials and bioceramics has recently received a great deal of attention for bone tissue engineering applications. In the present study, hybrid nanofibrous scaffolds were fabricated from PLGA and gelatin via electrospinning and then were coated with hydroxyapatite (HA). They were then characterized and used in stem cell culture studies for the evaluation of their biological behavior and osteogenic differentiation in vitro. This study showed that all PLGA, hybrid PLGA/gelatin and HA-PLGA/gelatin scaffolds were composed of ultrafine fibers with smooth morphology and interconnected pores. The MTT assay confirmed that the scaffolds can support the attachment and proliferation of stem cells. During osteogenic differentiation, bone-related gene expression, ALP activity and biomineralization on HA-PLGA/gelatin scaffolds were higher than those observed on other scaffolds and TCPS. PLGA/gelatin electrospun scaffolds also showed higher values of these markers than TCPS. Taking together, it was shown that nanofibrous structure enhanced osteogenic differentiation of adipose-tissue derived stem cells. Furthermore, surface-coated HA stimulated the effect of nanofibers on the commitment of stem cells toward osteolineage. In conclusion, HA-PLGA/gelatin electrospun scaffolds were demonstrated to have significant potential for bone tissue engineering applications. Copyright © 2016 International Alliance for Biological Standardization. Published by Elsevier Ltd. All rights reserved.

Electrospun nylon 6/zinc doped hydroxyapatite membrane for protein separation: Mechanism of fouling and blocking model.

PubMed

Esfahani, Hamid; Prabhakaran, Molamma P; Salahi, Esmaeil; Tayebifard, Ali; Rahimipour, Mohamad Reza; Keyanpour-Rad, Mansour; Ramakrishna, Seeram

2016-02-01

Development of composite nanofibrous membrane via electrospinning a polymer with ceramic nanoparticles (NPs) for application in protein separation systems is explored during this study. Positively charged zinc doped hydroxyapatite (xZH) NPs were prepared in three different compositions via chemical precipitation method. Herein, we created a positively charged surface containing nanoparticles on electrospun Nylon-6 nanofibers (NFs) to improve the separation and selectivity properties for adsorption of negatively charged protein, namely bovine serum albumin (BSA). The decline in permeate flux was analyzed using the framework of classical blocking models and fitting, demonstrated that the transition of fouling mechanisms was dominated during the filtration process. The standard blocking model provided the best fit of the experimental results during the mid-filtration period. The membrane decorated by NPs containing 4at.% zinc cations not only provided maximum BSA separation but also capable of separating higher amounts of BSA molecules (even after 1h filtration) than the pure Nylon membrane. Protein separation was achieved through this membrane with the incorporation of NPs that had high zeta potential (+5.9±0.2mV) and lower particle area (22,155nm(2)). The developed membrane has great potential to act as a high efficiency membrane for capturing BSA. Copyright © 2015 Elsevier B.V. All rights reserved.

Multicomponent amorphous nanofibers electrospun from hot aqueous solutions of a poorly soluble drug.

PubMed

Yu, Deng-Guang; Gao, Li-Dong; White, Kenneth; Branford-White, Christopher; Lu, Wei-Yue; Zhu, Li-Min

2010-11-01

To design and fabricate multicomponent amorphous electrospun nanofibers for synergistically improving the dissolution rate and permeation profiles of poorly water-soluble drugs. Nanofibers were designed to be composed of a poorly water soluble drug, helicid, a hydrophilic polymer polyvinylpyrrolidone as filament-forming matrix, sodium dodecyl sulfate as transmembrane enhancer and mannitol as taste masking agent, and were prepared from hot aqueous co-dissolving solutions of them. An elevated temperature electrospinning process was developed to fabricate the composite nanofibers, which were characterized using FESEM, DSC, XRD, ATR-FTIR, in vitro dissolution and permeation tests. The composite nanofibers were homogeneous with smooth surfaces and uniform structure, and the components were combined together in an amorphous state because of the favorable interactions such as hydrogen bonding, electrostatic interaction and hydrophobic interactions among them. In vitro dissolution and permeation tests demonstrated that the composite nanofibers had a dissolution rate over 26-fold faster than that of crude helicid particles and a 10-fold higher permeation rate across sublingual mucosa. A new type of amorphous material in the form of nanofibers was prepared from hot aqueous solutions of multiple ingredients using an electrospinning process. The amorphous nanofibers were able to improve the dissolution rate and permeation rate of helicid.

Nonenzymatic glucose sensor based on renewable electrospun Ni nanoparticle-loaded carbon nanofiber paste electrode.

PubMed

Liu, Yang; Teng, Hong; Hou, Haoqing; You, Tianyan

2009-07-15

A novel nonenzymatic glucose sensor was developed based on the renewable Ni nanoparticle-loaded carbon nanofiber paste (NiCFP) electrode. The NiCF nanocomposite was prepared by combination of electrospinning technique with thermal treatment method. The scanning electron microscopy (SEM) and transmission electron microscopy (TEM) images showed that large amounts of spherical nanoparticles were well dispersed on the surface or embedded in the carbon nanofibers. And the nanoparticles were composed of Ni and NiO, as revealed by energy dispersive X-ray spectroscopy (EDX) and X-ray powder diffraction (XRD). In application to nonenzymatic glucose determination, the renewable NiCFP electrodes, which were constructed by simply mixing the electrospun nanocomposite with mineral oil, exhibited strong and fast amperometric response without being poisoned by chloride ions. Low detection limit of 1 microM with wide linear range from 2 microM to 2.5 mM (R=0.9997) could be obtained. The current response of the proposed glucose sensor was highly sensitive and stable, attributing to the electrocatalytic performance of the firmly embedded Ni nanoparticles as well as the chemical inertness of the carbon-based electrode. The good analytical performance, low cost and straightforward preparation method made this novel electrode material promising for the development of effective glucose sensor.

Effect of a room-temperature ionic liquid on the structure and properties of electrospun poly(vinylidene fluoride) nanofibers.

PubMed

Xing, Chenyang; Guan, Jipeng; Li, Yongjin; Li, Jingye

2014-03-26

Novel anti-static nanofibers based on blends of poly(vinylidene fluoride) (PVDF) and a room-temperature ionic liquid (RTIL), 1-butyl-3-methylimidazolium hexafluorophosphate [BMIM][PF6], were fabricated using an electrospinning approach. The effects of the RTIL on the morphology, crystal structure, and physical properties of the PVDF nanofibers were investigated. Incorporation of RTIL leads to an increase in the mean fiber diameter and the rough fiber surface of the PVDF/RTIL composite nanofibers compared with the neat PVDF nanofibers. The PVDF in the PVDF/RTIL nanofibers exhibits an extremely high content (almost 100%) of β crystals, in contrast to the dominance of PVDF γ crystals in bulk melt-blended PVDF/RTIL blends. Nonwoven fabrics produced from the electrospun PVDF/RTIL composite nanofibers show better stretchability and higher electrical conductivity than those made from neat PVDF without RTIL, and are thus excellent antielectrostatic fibrous materials. In addition, RTIL greatly improved the hydrophobicity of the PVDF fibers, enabling them to effectively separate a mixture of tetrachloromethane (CCl4) and water. The extremely high β content, excellent antielectrostatic properties, better stretchability, and hydrophobicity of the present PVDF/RTIL nanofibers make them a promising candidate for micro- and nanoscale electronic device applications.

Next Generation of Electrospun Textiles for Chemical and Biological Protection and Air Filtration

DTIC Science & Technology

2009-09-01

these products were comparable to results reported for reactions of potassium 2,3-butanedione monooximate with GD, which produced 31P resonances at...Next Generation of Electrospun Textiles for Chemical and Biological Protection and Air Filtration by Liang Chen B.S. in Chemical Physics, University... of Science and Technology of China, 2001 M.S. in Chemistry, Brown University, 2004 M.S.C.E.P. in Chemical Engineering, Massachusetts Institute of

Processing, Properties and Morphology of Optical Limiting Silk Membranes

DTIC Science & Technology

2006-02-28

Christopher Brewer, Donald Ott, Polymer, 45 8451 (2004). 2. Electrospun Bombyx mori Gland Silk, S. Putthanarat, R.K. Eby, W. Kataphinan, S. Jones, R...Science, The University of Akron, Akron, OH. 3. American Physical Society (APS) meeting, March 2005, "Electrospun liquid silk from the gland of Bombyx Mori ...provide a good compatible matrix. They have previously demonstrated that GFP molecules can be incorporated into cast membranes of silk from B. mori

Electrospinning of PVC with natural rubber

DOE Office of Scientific and Technical Information (OSTI.GOV)

Othman, Muhammad Hariz; Abdullah, Ibrahim; Mohamed, Mahathir

Polyvinyl chloride (PVC) was mixed with natural rubbers which are liquid natural rubber (LNR), liquid epoxidised natural rubber (LENR) and liquid epoxidised natural rubber acrylate (LENRA) for a preparation of a fine non-woven fiber’s mat. PVC and each natural rubbers(PVC:LENR, PVC:LNR and PVC:LENRA) were mixed based on ratio of 70:30. Electrospinning method was used to prepare the fiber. The results show that the spinnable concentration of PVC/ natural rubber/THF solution is 16 wt%. The morphology, diameter, structure and degradation temperature of electrospun fibers were investigated by scanning electron microscopy (SEM) and thermogravimetric analysis (TGA). SEM photos showed that the morphologymore » and diameter of the fibers were mainly affected by the addition of natural rubber. TGA results suggested that PVC electrospun fiber has higher degradation temperature than those electrospun fibers that contain natural rubber.« less

High-sensitivity acoustic sensors from nanofibre webs.

PubMed

Lang, Chenhong; Fang, Jian; Shao, Hao; Ding, Xin; Lin, Tong

2016-03-23

Considerable interest has been devoted to converting mechanical energy into electricity using polymer nanofibres. In particular, piezoelectric nanofibres produced by electrospinning have shown remarkable mechanical energy-to-electricity conversion ability. However, there is little data for the acoustic-to-electric conversion of electrospun nanofibres. Here we show that electrospun piezoelectric nanofibre webs have a strong acoustic-to-electric conversion ability. Using poly(vinylidene fluoride) as a model polymer and a sensor device that transfers sound directly to the nanofibre layer, we show that the sensor devices can detect low-frequency sound with a sensitivity as high as 266 mV Pa(-1). They can precisely distinguish sound waves in low to middle frequency region. These features make them especially suitable for noise detection. Our nanofibre device has more than five times higher sensitivity than a commercial piezoelectric poly(vinylidene fluoride) film device. Electrospun piezoelectric nanofibres may be useful for developing high-performance acoustic sensors.

High-sensitivity acoustic sensors from nanofibre webs

PubMed Central

Lang, Chenhong; Fang, Jian; Shao, Hao; Ding, Xin; Lin, Tong

2016-01-01

Considerable interest has been devoted to converting mechanical energy into electricity using polymer nanofibres. In particular, piezoelectric nanofibres produced by electrospinning have shown remarkable mechanical energy-to-electricity conversion ability. However, there is little data for the acoustic-to-electric conversion of electrospun nanofibres. Here we show that electrospun piezoelectric nanofibre webs have a strong acoustic-to-electric conversion ability. Using poly(vinylidene fluoride) as a model polymer and a sensor device that transfers sound directly to the nanofibre layer, we show that the sensor devices can detect low-frequency sound with a sensitivity as high as 266 mV Pa−1. They can precisely distinguish sound waves in low to middle frequency region. These features make them especially suitable for noise detection. Our nanofibre device has more than five times higher sensitivity than a commercial piezoelectric poly(vinylidene fluoride) film device. Electrospun piezoelectric nanofibres may be useful for developing high-performance acoustic sensors. PMID:27005010

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wingert, Matthew C.; Jiang, Zhang; Chen, Renkun

Here, electrospun polymer nanofibers have garnered significant interest due to their strong size-dependent material properties, such as tensile moduli, strength, toughness, and glass transition temperatures. These properties are closely correlated with polymer chain dynamics. In most applications, polymers usually exhibit viscoelastic behaviors such as stress relaxation and creep, which are also determined by the motion of polymer chains. However, the size-dependent viscoelasticity has not been studied previously in polymer nanofibers. Here, we report the first experimental evidence of significant size-dependent stress relaxation in electrospun Nylon-11 nanofibers as well as size-dependent viscosity of the confined amorphous regions. In conjunction with themore » dramatically increasing stiffness of nano-scaled fibers, this strong relaxation enables size-tunable properties which break the traditional damping-stiffness tradeoff, qualifying electrospun nanofibers as a promising set of size-tunable materials with an unusual and highly desirable combination of simultaneously high stiffness and large mechanical energy dissipation.« less

Bladder tissue engineering using biocompatible nanofibrous electrospun constructs: feasibility and safety investigation.

PubMed

Shakhssalim, Nasser; Dehghan, Mohammad Mehdi; Moghadasali, Reza; Soltani, Mohammad Hossein; Shabani, Iman; Soleimani, Masoud

2012-01-01

To investigate the feasibility and safety of using biocompatible, nanofibrous electrospun polycaprolactone (PCL) and combination of polylactic acid (PLLA) and PCL mats in a canine model. Plasma-treated electrospun unseeded mats were implanted in three dogs. The first dog was sacrificed after 3 months and the second and third ones after 4 months, and then, the graft was examined macroscopically with subsequent morphological and histochemical evaluation. Both films showed high levels of cell infiltration and tissue formation, but body response to PLLA/PCL mat in comparison to PCL mat was very low. All three implantation models showed the same light microscopic morphology, immunohistochemistry, and scanning electron microscopy results; nevertheless, only the PCL/PLLA model showed favorable clinical results. Based on these data, nanofibrous PLLA/PCL scaffolding could be a suitable material for the bladder tissue engineering; however, it deserves further investigations.

Electrospun nanofibers: Work for medicine?

NASA Astrophysics Data System (ADS)

Liao, Susan; Chan, Casey K.; Ramakrishna, S.

2010-03-01

Attempts have been made to fabricate nanofibrous scaffolds to mimic the chemical composition and structural properties of the extracellular matrix (ECM) for tissue/organ replacement. Nanofiber scaffolds with various patterns have been successfully produced from synthetic and natural polymers through a relatively simple technique of electrospinning. The resulting patterns can mimic some of the diverse tissue-specific orientation and three-dimensional (3D) fibrous structures. Studies on cell-nanofiber interactions, including studies on stem cells, have revealed the importance of nanotopography on cell adhesion, proliferation and differentiation. Furthermore, clinical application of electrospun nanofibers including wound healing, tissue regeneration, drug delivery and stem cell therapy are highly feasible due to the ease and flexibility of fabrication of making nanofiber with this cost-effective method using electrospinning. In this review, we have highlighted the current state of the art and provided future perspectives on electrospun nanofiber in medical applications.

Delivery of Therapeutic Proteins Using Electrospun Fibers-Recent Developments and Current Challenges.

PubMed

Seif, Salem; Planz, Viktoria; Windbergs, Maike

2017-10-01

Proteins play a vital role within the human body by regulating various functions and even serving as structural constituent of many body parts. In this context, protein-based therapeutics have attracted a lot of attention in the last few decades as potential treatment of different diseases. Due to the steadily increasing interest in protein-based therapeutics, different dosage forms were investigated for delivering such complex macromolecules to the human body. Here, electrospun fibers hold a great potential for embedding proteins without structural damage and for controlled release of the protein for therapeutic applications. This review provides a comprehensive overview of the current state of protein-based carrier systems using electrospun fibers, with special emphasis on discussing their potential and key challenges in developing such therapeutic strategies, along with a prospective view of anticipated future directions. © 2017 Deutsche Pharmazeutische Gesellschaft.

Fluorescent composite scaffolds made of nanodiamonds/polycaprolactone

NASA Astrophysics Data System (ADS)

Cao, Li; Hou, Yanwen; Lafdi, Khalid; Urmey, Kirk

2015-11-01

Polycaprolactone (PCL) has been widely studied for biological applications. Biodegradable PCL fibrous scaffold can work as an appropriate substrate for tissue regeneration. In this letter, fluorescent nanodiamonds (FNDs) were prepared after surface passivation with octadecylamine. The FNDs were then mixed with PCL polymer and subsequently electrospun into FNDs/PCL fibrous scaffolds. The obtained scaffolds not only exhibited photoluminescence, but also showed reinforced mechanical strength. Toxicity study indicated FNDs/PCL scaffolds were nontoxic. This biocompatible fluorescent composite fibrous scaffold can support in vitro cell growth and also has the potential to act as an optical probe for tissue engineering application in vitro and in vivo.

A high-performance, flexible and robust metal nanotrough-embedded transparent conducting film for wearable touch screen panels.

PubMed

Im, Hyeon-Gyun; An, Byeong Wan; Jin, Jungho; Jang, Junho; Park, Young-Geun; Park, Jang-Ung; Bae, Byeong-Soo

2016-02-21

We report a high-performance, flexible and robust metal nanotrough-embedded transparent conducting hybrid film (metal nanotrough-GFRHybrimer). Using an electro-spun polymer nanofiber web as a template and vacuum-deposited gold as a conductor, a junction resistance-free continuous metal nanotrough network is formed. Subsequently, the metal nanotrough is embedded on the surface of a glass-fabric reinforced composite substrate (GFRHybrimer). The monolithic composite structure of our transparent conducting film allows simultaneously high thermal stability (24 h at 250 °C in air), a smooth surface topography (Rrms < 1 nm) and excellent opto-electrical properties. A flexible touch screen panel (TSP) is fabricated using the transparent conducting films. The flexible TSP device stably operates on the back of a human hand and on a wristband.

Biomechanical Comparison of Glutaraldehyde-Crosslinked Gelatin Fibrinogen Electrospun Scaffolds to Porcine Coronary Arteries

PubMed Central

Tamimi, E.; Ardila, D. C.; Haskett, D. G.; Doetschman, T.; Slepian, M. J.; Kellar, R. S.; Vande Geest, J. P.

2016-01-01

Cardiovascular disease (CVD) is the leading cause of death for Americans. As coronary artery bypass graft surgery (CABG) remains a mainstay of therapy for CVD and native vein grafts are limited by issues of supply and lifespan, an effective readily available tissue-engineered vascular graft (TEVG) for use in CABG would provide drastic improvements in patient care. Biomechanical mismatch between vascular grafts and native vasculature has been shown to be the major cause of graft failure, and therefore, there is need for compliance-matched biocompatible TEVGs for clinical implantation. The current study investigates the biaxial mechanical characterization of acellular electrospun glutaraldehyde (GLUT) vapor-crosslinked gelatin/fibrinogen cylindrical constructs, using a custom-made microbiaxial optomechanical device (MOD). Constructs crosslinked for 2, 8, and 24 hrs are compared to mechanically characterized porcine left anterior descending coronary (LADC) artery. The mechanical response data were used for constitutive modeling using a modified Fung strain energy equation. The results showed that constructs crosslinked for 2 and 8 hrs exhibited circumferential and axial tangential moduli (ATM) similar to that of the LADC. Furthermore, the 8-hrs experimental group was the only one to compliance-match the LADC, with compliance values of 0.0006±0.00018 mm Hg−1 and 0.00071±0.00027 mm Hg−1, respectively. The results of this study show the feasibility of meeting mechanical specifications expected of native arteries through manipulating GLUT vapor crosslinking time. The comprehensive mechanical characterization of cylindrical biopolymer constructs in this study is an important first step to successfully develop a biopolymer compliance-matched TEVG. PMID:26501189

Electrospinning of nanofibers from non-polymeric systems: polymer-free nanofibers from cyclodextrin derivatives

NASA Astrophysics Data System (ADS)

Celebioglu, Asli; Uyar, Tamer

2012-01-01

High molecular weight polymers and high polymer concentrations are desirable for the electrospinning of nanofibers since polymer chain entanglements and overlapping are important for uniform fiber formation. Hence, the electrospinning of nanofibers from non-polymeric systems such as cyclodextrins (CDs) is quite a challenge since CDs are cyclic oligosaccharides. Nevertheless, in this study, we have successfully achieved the electrospinning of nanofibers from chemically modified CDs without using a carrier polymer matrix. Polymer-free nanofibers were electrospun from three different CD derivatives, hydroxypropyl-β-cyclodextrin (HPβCD), hydroxypropyl-γ-cyclodextrin (HPγCD) and methyl-β-cyclodextrin (MβCD) in three different solvent systems, water, dimethylformamide (DMF) and dimethylacetamide (DMAc). We observed that the electrospinning of these CDs is quite similar to polymeric systems in which the solvent type, the solution concentration and the solution conductivity are some of the key factors for obtaining uniform nanofibers. Dynamic light scattering (DLS) measurements indicated that the presence of considerable CD aggregates and the very high solution viscosity were playing a key role for attaining nanofibers from CD derivatives without the use of any polymeric carrier. The electrospinning of CD solutions containing urea yielded no fibers but only beads or splashes since urea caused a notable destruction of the self-associated CD aggregates in their concentrated solutions. The structural, thermal and mechanical characteristics of the CD nanofibers were also investigated. Although the CD derivatives are amorphous small molecules, interestingly, we observed that these electrospun CD nanofibers/nanowebs have shown some mechanical integrity by which they can be easily handled and folded as a free standing material.

Matrigel immobilization on the shish-kebab structured poly(ɛ-caprolactone) nanofibers for skin tissue engineering

NASA Astrophysics Data System (ADS)

Jing, Xin; Mi, Hao-Yang; Peng, Xiang-Fang; Turng, Lih-Sheng

2016-03-01

Surface properties of tissue engineering scaffolds such as topography, hydrophilicity, and functional groups play a vital role in cell adhesion, migration, proliferation, and apoptosis. First, poly(ɛ-caprolactone) (PCL) shish-kebab scaffolds (PCL-SK), which feature a three-dimensional structure comprised of electrospun PCL nanofibers covered by periodic, self-induced PCL crystal lamellae on the surface, was created to mimic the nanotopography of native collagen fibrils in the extracellular matrix (ECM). Second, matrigel was covalently immobilized on the surface of alkaline hydrolyzed PCL-SK scaffolds to enhance their hydrophilicity. This combined approach not only mimics the nanotopography of native collagen fibrils, but also simulates the surface features of collagen fibrils for cell growth. To investigate the viability of such scaffolds, HEF1 fibroblast cell assays were conducted and the results revealed that the nanotopography of the PCL-SK scaffolds facilitated cell adhesion and proliferation. The matrigel functionalization on PCL-SK scaffolds further enhanced cellular response, which suggested elevated biocompatibility and greater potential for skin tissue engineering applications.

Conversion of hydrophilic SiOC nanofibrous membrane to robust hydrophobic materials by introducing palladium

NASA Astrophysics Data System (ADS)

Wu, Nan; Wan, Lynn Yuqin; Wang, Yingde; Ko, Frank

2017-12-01

Hydrophobic ceramic nanofibrous membranes have wide applications in the fields of high-temperature filters, oil/water separators, catalyst supports and membrane reactors, for their water repellency property, self-cleaning capability, good environmental stability and long life span. In this work, we fabricated an inherently hydrophobic ceramic nanofiber membrane without any surface modification through pyrolysis of electrospun polycarbosilane nanofibers. The hydrophobicity was introduced by the hierarchical microstructure formed on the surface of the nanofibers and the special surface composition by the addition of trace amounts of palladium. Furthermore, the flexible ceramic mats demonstrated robust chemical resistance properties with consistent hydrophobicity over the entire pH value range and effective water-in-oil emulsion separation performance. Interestingly, a highly cohesive force was found between water droplet and the ceramic membranes, suggesting their great potentials in micro-liquid transportation. This work provides a new route for adjusting the composition of ceramic surface and flexible, recyclable and multifunctional ceramic fibrous membranes for utilization in harsh environments.

Droplet-based immunoassay on a 'sticky' nanofibrous surface for multiplexed and dual detection of bacteria using smartphones.

PubMed

Nicolini, Ariana M; Fronczek, Christopher F; Yoon, Jeong-Yeol

2015-05-15

We have developed a rapid, sensitive, and specific droplet-based immunoassay for the detection of Escherichia coli and Salmonella within a single-pipetted sample. Polycaprolactone (PCL) electrospun fibers on indium-tin-oxide (ITO) glass provide a sufficient surface to render a non-slip droplet condition, and while the PCL fibers lend a local hydrophilicity (contact angle θ=74°) for sufficient sub-micron particle adhesion, air pockets within the fibers lend an apparent hydrophobicity. Overall, the contact angle of water on this electrospun surface is 119°, and the air pockets cause the droplet to be completely immobile and resistant to movement, protecting it from external vibration. By using both anti-E. coli conjugated, 510 nm diameter green fluorescent particles (480 nm excitation and 520 nm emission) and anti-Salmonella conjugated, 400 nm diameter red fluorescent particles (640 nm excitation and 690 nm emission), we can detect multiple targets in a single droplet. Using appropriate light sources guided by fiber optics, we determined a detection limit of 10(2) CFU mL(-1). Immunoagglutination can be observed under a fluorescence microscope. Fluorescence detection (at the emission wavelength) of immunoagglutination was maximum at 90° from the incident light, while light scattering (at the excitation wavelength) was still present and behaved similarly, indicating the ability of double detection, greatly improving credibility and reproducibility of the assay. A power function (light intensity) simulation of elastic Mie scatter confirmed that both fluorescence and light scattering were present. Due to the size of the fluorescent particles relative to their incident excitation wavelengths, Mie scatter conditions were observed, and fluorescence signals show a similar trend to light scattering signals. Smartphone detection was included for true portable detection, in which the high contact angle pinning of the droplet makes this format re-usable and re-configurable. Copyright © 2014 Elsevier B.V. All rights reserved.

Development and Characterization of a Hybrid Atmospheric Pressure Plasma Electrospinning System for Nanofiber Enhancement

NASA Astrophysics Data System (ADS)

Nowak, Joshua Michael

A hybrid atmospheric pressure-electrospinning plasma system was developed to be used for the production of nanofibers and enhance their performance for various applications. Electrospun nanofibers are excellent candidates for protective clothing in the field of chemical and biological warfare defense; however, nanofibers are structurally weak and easily abrade and tear. They can be strengthened through the support of a substrate fabric, but they do not adhere well to substrates. Through the use of the developed hybrid system with either pure He or He/O2 (99/1) feed gas, adherence to the substrate along with abrasion and flex resistance were improved. The plasma source was diagnosed electrically, thermally, and optically. An equivalent circuit model was developed for non-thermal, highly collisional plasmas that can solve for average electron temperature and electron number density. The obtained temperatures (~ 3eV) correlate very well with the results of a neutral Bremsstrahlung continuum matching technique that was also employed. Using the temperatures and number densities obtained from the circuit model and the optical spectroscopy, a global chemical kinetics code was written in order to solve for radical and ion concentrations. This code shows that there are significant concentrations of oxygen radicals present. The XPS analysis confirmed that there was an increase of surface oxygen from 11.1% up to 16.6% for the He/O2 plasma and that the C-O bonding, which was not present in the control samples, has increased to 45.4%. The adhesive strength to the substrate has a significant increase of 81% for helium plasma and 144% for He/O2 plasma; however, these values remain below the desired values for protective clothing applications. The hybrid system displayed the ability to oxygenate nanofibers as they are being electrospun and shows the feasibility of making other surface modifications. The developed circuit model and chemical kinetics code both show promise as tools for deterministic atmospheric pressure plasma research in the field of surface modifications.

Culture of human anulus fibrosus cells on polyamide nanofibers: extracellular matrix production.

PubMed

Gruber, Helen E; Hoelscher, Gretchen; Ingram, Jane A; Hanley, Edward N

2009-01-01

Studies were approved by the authors' Human Subjects Institutional Review Board. Human anulus cells were tested for growth and extracellular matrix (ECM) production in vitro. To investigate cell attachment, cell proliferation, and ECM production of human intervertebral disc anulus cells seeded onto randomly oriented electrospun polyamide nanofibers. Because nanofibrillar matrices have the potential to promote microenvironments, which may mimic in vivo conditions and resemble connective tissue, their utilization opens new avenues for cell-based tissue engineering applications for disc cells. Anulus cells were isolated from 4 cervical spine surgical disc specimens, expanded, and seeded into either routine plastic culture (control) or a nanofiber surface of randomly oriented electrospun polyamide nanofibers (Ultra-Web-coated culture dish, Corning) with a positive charge or without a charge. Cells were cultured for 9 days, digital images captured, cells harvested, embedded in paraffin, and examined for production of extracellular matrix (ECM). Additional anulus cultures were tested to quantitatively assess total proteoglycan production and cell proliferation under control or nanofiber cultures. Cells attached well and exhibited cell extensions within the nanofiber layers; cells on the charged nanofiber surface deposited greater amounts of chondroitin sulfate than of type II collagen than cells cultured on the uncharged nanofiber surface. Results showed that culture of anulus cells on nanofibers was permissive for secretion and assembly of type II collagen and chondroitin sulfate. Significantly greater total proteoglycan formation was present after culture on the nanofiber with added charge conditions {control, 0.6116 microg/mL +/- 0.186 [4] [mean +/- sem(n)] vs. 1.201 +/- 0.2509 [4], P < 0.05}. Cell proliferation, however, did not differ among treatment groups. Culture of anulus cells on nanofibers was found to be permissive for secretion and assembly of type II collagen and chondroitin sulfate, and culture on nanofibers with added charge significantly increased total proteoglycan production. These novel findings point to the need for further examination of nanofibrillar 3D culture of anulus cells for tissue engineering applications.

Electrospun Poly(L-lactide)/Poly(ε-caprolactone) Blend Nanofibrous Scaffold: Characterization and Biocompatibility with Human Adipose-Derived Stem Cells

PubMed Central

Liao, Guiying; Peng, Ejun; Wu, Bolin; Wang, Yuxi; Zeng, Xiaoyong; Xie, Xiaolin

2013-01-01

The essence of tissue engineering is the fabrication of autologous cells or induced stem cells in naturally derived or synthetic scaffolds to form specific tissues. Polymer is thought as an appealing source of cell-seeded scaffold owing to the diversity of its physicochemical property and can be electrospun into nano-size to mimic natural structure. Poly (L-lactic acid) (PLLA) and poly (ε-caprolactone) (PCL) are both excellent aliphatic polyester with almost “opposite” characteristics. The controlling combination of PLLA and PCL provides varying properties and makes diverse applications. Compared with the copolymers of the same components, PLLA/PCL blend demonstrates its potential in regenerative medicine as a simple, efficient and scalable alternative. In this study, we electrospun PLLA/PCL blends of different weight ratios into nanofibrous scaffolds (NFS) and their properties were detected including morphology, porosity, degradation, ATR-FTIR analysis, stress-stain assay, and inflammatory reaction. To explore the biocompatibility of the NFS we synthesized, human adipose-derived stem cells (hASCs) were used to evaluate proliferation, attachment, viability and multi-lineage differentiation. In conclusion, the electrospun PLLA/PCL blend nanofibrous scaffold with the indicated weight ratios all supported hASCs well. However, the NFS of 1/1 weight ratio showed better properties and cellular responses in all assessments, implying it a biocompatible scaffold for tissue engineering. PMID:23990941

Fabrication and characterization of polycaprolactone-graphene powder electrospun nanofibers

NASA Astrophysics Data System (ADS)

Ginestra, Paola; Ghazinejad, Maziar; Madou, Marc; Ceretti, Elisabetta

2016-09-01

Porous fibrous membranes having multiple scales geometries and tailored properties have become attractive microfabrication materials in recent years. Due to the feasibility of incorporating graphene in electrospun nanofibres and the growing interest on these nanomaterials, the present paper focuses on the electrospinning of Poly (ɛ-Caprolactone) (PCL) solutions in the presence of different amounts of Graphene platelets. Electrospinning is a process whereby ultrafine fibers are formed in a high-voltage electrostatic field. The morphological appearance, fiber diameter, and structure of PCL nanofibers produced by the electrospinning process were studied in the presence of different concentration of graphene. Moreover, the effect of a successful incorporation of graphene nanosheets into PCL polymer nanofibers was analyzed. Scanning electron microscope micrographs of the electrospun fibers showed that the average fiber diameter increases in the presence of graphene. Furthermore, the intrinsic properties developed due to the interactions of graphene and PCL improved the mechanical properties of the nanofibers. The results reveal the effect of various graphene concentrations on PCL and the strong interfacial interactions between the graphene platelets phase and the polymer matrix. The functional complexity of the electrospun fibers provides significant advantages over other techniques and shows the promise of these fibers for many applications including air/water filters, sensors, organic solar cells, smart textiles, biocompatible scaffolds for tissue engineering and load-bearing applications. Optimizing deposition efficiency, however, is a necessary milestone for the widespread use of this technique.

Development of Oromucosal Dosage Forms by Combining Electrospinning and Inkjet Printing.

PubMed

Palo, Mirja; Kogermann, Karin; Laidmäe, Ivo; Meos, Andres; Preis, Maren; Heinämäki, Jyrki; Sandler, Niklas

2017-03-06

Printing technology has been shown to enable flexible fabrication of solid dosage forms for personalized drug therapy. Several methods can be applied for tailoring the properties of the printed pharmaceuticals. In this study, the use of electrospun fibrous substrates in the fabrication of inkjet-printed dosage forms was investigated. A single-drug formulation with lidocaine hydrochloride (LH) and a combination drug system containing LH and piroxicam (PRX) for oromucosal administration were prepared. The LH was deposited on the electrospun and cross-linked gelatin substrates by inkjet printing, whereas PRX was incorporated within the substrate fibers during electrospinning. The solid state analysis of the electrospun substrates showed that PRX was in an amorphous state within the fibers. Furthermore, the results indicated the entrapment and solidification of the dissolved LH within the fibrous gelatin matrix. The printed drug amount (2-3 mg) was in good correlation with the theoretical dose calculated based on the printing parameters. However, a noticeable degradation of the printed LH was detected after a few months. An immediate release (over 85% drug release after 8 min) of both drugs from the printed dosage forms was observed. In conclusion, the prepared electrospun gelatin scaffolds were shown to be suitable substrates for inkjet printing of oromucosal formulations. The combination of electrospinning and inkjet printing allowed the preparation of a dual drug system.

Braided and Stacked Electrospun Nanofibrous Scaffolds for Tendon and Ligament Tissue Engineering

PubMed Central

Rothrauff, Benjamin B.; Lauro, Brian B.; Yang, Guang; Debski, Richard E.; Musahl, Volker

2017-01-01

Tendon and ligament injuries are a persistent orthopedic challenge given their poor innate healing capacity. Nonwoven electrospun nanofibrous scaffolds composed of polyesters have been used to mimic the mechanics and topographical cues of native tendons and ligaments. However, nonwoven nanofibers have several limitations that prevent broader clinical application, including poor cell infiltration, as well as tensile and suture-retention strengths that are inferior to native tissues. In this study, multilayered scaffolds of aligned electrospun nanofibers of two designs–stacked or braided–were fabricated. Mechanical properties, including structural and mechanical properties and suture-retention strength, were determined using acellular scaffolds. Human bone marrow-derived mesenchymal stem cells (MSCs) were seeded on scaffolds for up to 28 days, and assays for tenogenic differentiation, histology, and biochemical composition were performed. Braided scaffolds exhibited improved tensile and suture-retention strengths, but reduced moduli. Both scaffold designs supported expression of tenogenic markers, although the effect was greater on braided scaffolds. Conversely, cell infiltration was superior in stacked constructs, resulting in enhanced cell number, total collagen content, and total sulfated glycosaminoglycan content. However, when normalized against cell number, both designs modulated extracellular matrix protein deposition to a similar degree. Taken together, this study demonstrates that multilayered scaffolds of aligned electrospun nanofibers supported tenogenic differentiation of seeded MSCs, but the macroarchitecture is an important consideration for applications of tendon and ligament tissue engineering. PMID:28071988

Braided and Stacked Electrospun Nanofibrous Scaffolds for Tendon and Ligament Tissue Engineering.

PubMed

Rothrauff, Benjamin B; Lauro, Brian B; Yang, Guang; Debski, Richard E; Musahl, Volker; Tuan, Rocky S

2017-05-01

Tendon and ligament injuries are a persistent orthopedic challenge given their poor innate healing capacity. Nonwoven electrospun nanofibrous scaffolds composed of polyesters have been used to mimic the mechanics and topographical cues of native tendons and ligaments. However, nonwoven nanofibers have several limitations that prevent broader clinical application, including poor cell infiltration, as well as tensile and suture-retention strengths that are inferior to native tissues. In this study, multilayered scaffolds of aligned electrospun nanofibers of two designs-stacked or braided-were fabricated. Mechanical properties, including structural and mechanical properties and suture-retention strength, were determined using acellular scaffolds. Human bone marrow-derived mesenchymal stem cells (MSCs) were seeded on scaffolds for up to 28 days, and assays for tenogenic differentiation, histology, and biochemical composition were performed. Braided scaffolds exhibited improved tensile and suture-retention strengths, but reduced moduli. Both scaffold designs supported expression of tenogenic markers, although the effect was greater on braided scaffolds. Conversely, cell infiltration was superior in stacked constructs, resulting in enhanced cell number, total collagen content, and total sulfated glycosaminoglycan content. However, when normalized against cell number, both designs modulated extracellular matrix protein deposition to a similar degree. Taken together, this study demonstrates that multilayered scaffolds of aligned electrospun nanofibers supported tenogenic differentiation of seeded MSCs, but the macroarchitecture is an important consideration for applications of tendon and ligament tissue engineering.

Double-grooved nanofibre surfaces with enhanced anisotropic hydrophobicity.

PubMed

Liang, Meimei; Chen, Xin; Xu, Yang; Zhu, Lei; Jin, Xiangyu; Huang, Chen

2017-11-02

This study reports a facile method for fabricating double-grooved fibrous surfaces. The primary grooves of the surface are formed by aligned fibres, while the secondary grooves are achieved by oriented nanogrooves on the fibre surface. Investigation into the formation mechanism reveals that the nanogrooves can be readily tailored through adjusting the solvent ratio and relative humidity. With this understanding, a variety of polymers have been successfully electrospun into fibres having the same nanogrooved feature. These fibres show high resemblance to natural hierarchical structures, and thereby endowing the corresponding double-grooved surface with enhanced anisotropic hydrophobicity. A water droplet at a parallel direction to the grooves exhibits a much higher contact angle and a lower roll-off angle than the droplet at a perpendicular direction. The application potential of such anisotropic hydrophobicity has been demonstrated via a fog collection experiment, in which the double-grooved surface can harvest the largest amount of water. Moreover, the fabrication method requires neither post-treatment nor sophisticated equipment, making us anticipate that the double-grooved surface would be competitive in areas where a highly ordered surface, a large surface area and an anisotropic hydrophobicity are preferred.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Li, Maoying; Zhang, Zhenyi; Cao, Tieping

Graphical abstract: Nanofibers and nanoribbons of poly (methyl methacrylate)/Eu{sup 3+} ions composites were successfully prepared by using a simple electrospinning technique. And the photoluminescence properties of the above PMMA/Eu{sup 3+} ions composites were studied. Highlights: Black-Right-Pointing-Pointer Nanofibers and nanoribbons of PMMA/Eu{sup 3+} ions composites are fabricated by electrospinning. Black-Right-Pointing-Pointer Photoluminescence properties of as-electrospun PMMA/Eu{sup 3+} ions composites are studied. Black-Right-Pointing-Pointer The ratios of electric- and magnetic-dipole transitions are enhanced by increasing electrospinning voltage. -- Abstract: Nanofibers and nanoribbons of poly (methyl methacrylate) (PMMA)/Eu{sup 3+} ions composites with different concentration of Eu{sup 3+} ions were successfully prepared by using a simplemore » electrospinning technique. From the results of scanning electron microscopy and energy-dispersive X-ray spectroscopy, we found that the morphology of the as-electrospun PMMA/Eu{sup 3+} ions composites could be changed from fiber to ribbon structure by adjusting the concentration of Eu{sup 3+} ions in the electrospun precursor solution. The coordination between the Eu{sup 3+} ions and PMMA molecules were investigated by Fourier transform infrared spectroscopy and differential thermal analysis. The photoluminescence (PL) properties of the as-electrospun PMMA/Eu{sup 3+} ions composites were studied in comparison to those of the Eu(NO{sub 3}){sub 3} powder. It was showed that the {sup 5}D{sub 0}-{sup 7}F{sub J} (J = 0, 1, 2, 3, 4) emission appeared in the PL spectra of the as-electrospun PMMA/Eu{sup 3+} ions composites, whereas the {sup 5}D{sub 0}-{sup 7}F{sub 0} emission was completely absent in the PL spectra of Eu(NO{sub 3}){sub 3} powder due to the different local environments surrounding Eu{sup 3+} ions. It was interesting to note that the intensity ratios of the electric-dipole and magnetic-dipole transitions for the PMMA/Eu{sup 3+} ions composites could be enhanced significantly by increasing electrospinning voltage.« less

Engineered Polymer Composites Through Electrospun Nanofiber Coating of Fiber Tows

NASA Technical Reports Server (NTRS)

Kohlman, Lee W.; Bakis, Charles; Williams, Tiffany S.; Johnston, James C.; Kuczmarski, Maria A.; Roberts, Gary D.

2014-01-01

Composite materials offer significant weight savings in many aerospace applications. The toughness of the interface of fibers crossing at different angles often determines failure of composite components. A method for toughening the interface in fabric and filament wound components using directly electrospun thermoplastic nanofiber on carbon fiber tow is presented. The method was first demonstrated with limited trials, and then was scaled up to a continuous lab scale process. Filament wound tubes were fabricated and tested using unmodified baseline towpreg material and nanofiber coated towpreg.

Synthesis and Electrochemical Property of LiMn2O4 Porous Hollow Nanofiber as Cathode for Lithium-Ion Batteries.

PubMed

Duan, Lianfeng; Zhang, Xueyu; Yue, Kaiqiang; Wu, Yue; Zhuang, Jian; Lü, Wei

2017-12-01

The LiMn 2 O 4 hollow nanofibers with a porous structure have been synthesized by modified electrospinning techniques and subsequent thermal treatment. The precursors were electrospun directly onto the fluorine-doped tin oxide (FTO) glass. The heating rate and FTO as substrate play key roles on preparing porous hollow nanofiber. As cathode materials for lithium-ion batteries (LIBs), LiMn 2 O 4 hollow nanofibers showed the high specific capacity of 125.9 mAh/g at 0.1 C and a stable cycling performance, 105.2 mAh/g after 400 cycles. This unique structure could relieve the structure expansion effectively and provide more reaction sites as well as shorten the diffusion path for Li + for improving electrochemical performance for LIBs.

Atmospheric Pressure Non-Equilibrium Plasma as a Green Tool to Crosslink Gelatin Nanofibers

NASA Astrophysics Data System (ADS)

Liguori, Anna; Bigi, Adriana; Colombo, Vittorio; Focarete, Maria Letizia; Gherardi, Matteo; Gualandi, Chiara; Oleari, Maria Chiara; Panzavolta, Silvia

2016-12-01

Electrospun gelatin nanofibers attract great interest as a natural biomaterial for cartilage and tendon repair despite their high solubility in aqueous solution, which makes them also difficult to crosslink by means of chemical agents. In this work, we explore the efficiency of non-equilibrium atmospheric pressure plasma in stabilizing gelatin nanofibers. We demonstrate that plasma represents an innovative, easy and environmentally friendly approach to successfully crosslink gelatin electrospun mats directly in the solid state. Plasma treated gelatin mats display increased structural stability and excellent retention of fibrous morphology after immersion in aqueous solution. This method can be successfully applied to induce crosslinking both in pure gelatin and genipin-containing gelatin electrospun nanofibers, the latter requiring an even shorter plasma exposure time. A complete characterization of the crosslinked nanofibres, including mechanical properties, morphological observations, stability in physiological solution and structural modifications, has been carried out in order to get insights on the occurring reactions triggered by plasma.

Rational design of nanofiber scaffolds for orthopedic tissue repair and regeneration

PubMed Central

Ma, Bing; Xie, Jingwei; Jiang, Jiang; Shuler, Franklin D; Bartlett, David E

2013-01-01

This article reviews recent significant advances in the design of nanofiber scaffolds for orthopedic tissue repair and regeneration. It begins with a brief introduction on the limitations of current approaches for orthopedic tissue repair and regeneration. It then illustrates that rationally designed scaffolds made up of electrospun nanofibers could be a promising solution to overcome the problems that current approaches encounter. The article also discusses the intriguing properties of electrospun nanofibers, including control of composition, structures, orders, alignments and mechanical properties, use as carriers for topical drug and/or gene sustained delivery, and serving as substrates for the regulation of cell behaviors, which could benefit musculoskeletal tissue repair and regeneration. It further highlights a few of the many recent applications of electrospun nanofiber scaffolds in repairing and regenerating various orthopedic tissues. Finally, the article concludes with perspectives on the challenges and future directions for better design, fabrication and utilization of nanofiber scaffolds for orthopedic tissue engineering. PMID:23987110

Preparation and characterization of kefiran electrospun nanofibers.

PubMed

Esnaashari, Seyedeh Sara; Rezaei, Sasan; Mirzaei, Esmaeil; Afshari, Hamed; Rezayat, Seyed Mahdi; Faridi-Majidi, Reza

2014-09-01

In this study, we report the first successful production of kefiran nanofibers through electrospinning process using distilled water as solvent. For this purpose, kefiran was extracted from cultured kefir grains, and homogenous kefiran solutions with different concentrations were prepared and then electrospun to obtain uniform nanofibers. The effect of main process parameters, including applied voltage, tip-to-collector distance, and feeding rate, on diameter and morphology of produced nanofibers, was studied. Scanning electron microscopy (SEM) and attenuated total reflectance Fourier transform infrared (ATR-FTIR) spectroscopy were used to characterize electrospun mats. Rheological behavior of the kefiran solution was evaluated via a cone and plate rheometer too. The results exhibited that diameter of kefiran nanofibers increased with increasing polymer concentration, applied voltage, and polymer feeding rate, while tip-to-collector distance did not have significant effect on nanofiber diameter. ATR-FTIR spectra showed that kefiran has maintained its molecular structure during electrospinning process. Flow curves also demonstrated shear thinning behavior for kefiran solutions. Copyright © 2014 Elsevier B.V. All rights reserved.

Recent progress concerning the production of controlled highly oriented electrospun nanofibrous arrays

NASA Astrophysics Data System (ADS)

Manea, L. R.; Hristian, L.; Leon, A. L.; Popa, A.

2016-08-01

Among the foreground domains of all the research-development programs at national and international level, a special place is occupied by that concerning the nanosciences, nanotechnologies, new materials and technologies. Electrospinning found a well-deserved place in this space, offering the preparation of nanomaterials with distinctive properties and applications in medicine, environment, photonic sensors, filters, etc. These multiple applications are generated by the fact that the electrospinning technology makes available the production of nanofibers with controllable characteristics (length, porosity, density, and mechanical characteristics), complexity and architecture. The apparition of 3D printing technology favors the production of complex nanofibrous structures, controlled assembly, self-assembly of electrospun nanofibers for the production of scaffolds used in various medical applications. The architecture of fibrous deposits has a special influence on the subsequent development of the cells of the reconstructed organism. The present work proposes to study of recent progress concerning the production of controlled highly oriented electrospun nanofibrous arrays and progress in research on the production of complex 2D and 3D structures.

Synthesis of porous Co3O4/C nanoparticles as anode for Li-ion battery application

NASA Astrophysics Data System (ADS)

Yang, Qian; Feng, Chuanqi; Liu, Jianwen; Guo, Zaiping

2018-06-01

The porous Co3O4 with electrospun carbon (Co3O4/C) was synthesized simply through annealing the Co-based metal-organic-framework/polyacrylonitrile (ZIF-67/PAN) templates. The samples were characterized by X-ray diffraction (XRD), scanning electronic microscopy (SEM) and Brunauer-Emmett-Teller (BET) techniques. The content of electrospun carbon in Co3O4/C was tested by thermogravimetric analysis (TG). The Co3O4/C not only shows a remarkable capacity of 1024.1 mAh g-1 after 100 cycles but also behaves superior rate capability. The superior electrochemical properties could be attributed to the electrospun carbon, which serves as a buffer layer to slow down the volumetric stresses and provides conductive paths for fast Li+ diffusion and easy electric charge transfer. Therefore, superior performance of the Co3O4/C electrode makes it possible to be used as promising anode for lithium ion battery application.

Rapid prototyping of nanofluidic systems using size-reduced electrospun nanofibers for biomolecular analysis.

PubMed

Park, Seung-Min; Huh, Yun Suk; Szeto, Kylan; Joe, Daniel J; Kameoka, Jun; Coates, Geoffrey W; Edel, Joshua B; Erickson, David; Craighead, Harold G

2010-11-05

Biomolecular transport in nanofluidic confinement offers various means to investigate the behavior of biomolecules in their native aqueous environments, and to develop tools for diverse single-molecule manipulations. Recently, a number of simple nanofluidic fabrication techniques has been demonstrated that utilize electrospun nanofibers as a backbone structure. These techniques are limited by the arbitrary dimension of the resulting nanochannels due to the random nature of electrospinning. Here, a new method for fabricating nanofluidic systems from size-reduced electrospun nanofibers is reported and demonstrated. As it is demonstrated, this method uses the scanned electrospinning technique for generation of oriented sacrificial nanofibers and exposes these nanofibers to harsh, but isotropic etching/heating environments to reduce their cross-sectional dimension. The creation of various nanofluidic systems as small as 20 nm is demonstrated, and practical examples of single biomolecular handling, such as DNA elongation in nanochannels and fluorescence correlation spectroscopic analysis of biomolecules passing through nanochannels, are provided.

Antibacterial and Barrier Properties of Gelatin Coated by Electrospun Polycaprolactone Ultrathin Fibers Containing Black Pepper Oleoresin of Interest in Active Food Biopackaging Applications

PubMed Central

Castro-Mayorga, Jinneth Lorena

2018-01-01

The present study evaluated the effect of using electrospun polycaprolactone (PCL) as a barrier coating and black pepper oleoresin (OR) as a natural extract on the morphology, thermal, mechanical, antimicrobial, oxygen, and water vapor barrier properties of solvent cast gelatin (GEL). The antimicrobial activity of the developed multilayer system obtained by the so-called electrospinning coating technique was also evaluated against Staphylococcus aureus strains for 10 days. The results showed that the multilayer system containing PCL and OR increased the thermal resistance, elongated the GEL film, and significantly diminished its permeance to water vapor. Active multilayer systems stored in hermetically closed bottles increased their antimicrobial activity after 10 days by inhibiting the growth of Staphylococcus aureus. This study demonstrates that addition of electrospun PCL ultrathin fibers and OR improved the properties of GEL films, which promoted its potential use in active food packaging applications. PMID:29597268

Electrospun Collagen/Silk Tissue Engineering Scaffolds: Fiber Fabrication, Post-Treatment Optimization, and Application in Neural Differentiation of Stem Cells

NASA Astrophysics Data System (ADS)

Zhu, Bofan

Biocompatible scaffolds mimicking the locally aligned fibrous structure of native extracellular matrix (ECM) are in high demand in tissue engineering. In this thesis research, unidirectionally aligned fibers were generated via a home-built electrospinning system. Collagen type I, as a major ECM component, was chosen in this study due to its support of cell proliferation and promotion of neuroectodermal commitment in stem cell differentiation. Synthetic dragline silk proteins, as biopolymers with remarkable tensile strength and superior elasticity, were also used as a model material. Good alignment, controllable fiber size and morphology, as well as a desirable deposition density of fibers were achieved via the optimization of solution and electrospinning parameters. The incorporation of silk proteins into collagen was found to significantly enhance mechanical properties and stability of electrospun fibers. Glutaraldehyde (GA) vapor post-treatment was demonstrated as a simple and effective way to tune the properties of collagen/silk fibers without changing their chemical composition. With 6-12 hours GA treatment, electrospun collagen/silk fibers were not only biocompatible, but could also effectively induce the polarization and neural commitment of stem cells, which were optimized on collagen rich fibers due to the unique combination of biochemical and biophysical cues imposed to cells. Taken together, electrospun collagen rich composite fibers are mechanically strong, stable and provide excellent cell adhesion. The unidirectionally aligned fibers can accelerate neural differentiation of stem cells, representing a promising therapy for neural tissue degenerative diseases and nerve injuries.

Effects of electric field on the maximum electro-spinning rate of silk fibroin solutions.

PubMed

Park, Bo Kyung; Um, In Chul

2017-02-01

Owing to the excellent cyto-compatibility of silk fibroin (SF) and the simple fabrication of nano-fibrous webs, electro-spun SF webs have attracted much research attention in numerous biomedical fields. Because the production rate of electro-spun webs is strongly dependent on the electro-spinning rate used, the electro-spinning rate becomes more important. In the present study, to improve the electro-spinning rate of SF solutions, various electric fields were applied during electro-spinning of SF, and its effects on the maximum electro-spinning rate of SF solution as well as diameters and molecular conformations of the electro-spun SF fibers were examined. As the electric field was increased, the maximum electro-spinning rate of the SF solution also increased. The maximum electro-spinning rate of a 13% SF solution could be increased 12×by increasing the electric field from 0.5kV/cm (0.25mL/h) to 2.5kV/cm (3.0mL/h). The dependence of the fiber diameter on the present electric field was not significant when using less-concentrated SF solutions (7-9% SF). On the other hand, at higher SF concentrations the electric field had a greater effect on the resulting fiber diameter. The electric field had a minimal effect of the molecular conformation and crystallinity index of the electro-spun SF webs. Copyright © 2016 Elsevier B.V. All rights reserved.

Comparative study of different techniques for the sterilization of poly-L-lactide electrospun microfibers: effectiveness vs. material degradation.

PubMed

Rainer, Alberto; Centola, Matteo; Spadaccio, Cristiano; Gherardi, Giovanni; Genovese, Jorge A; Licoccia, Silvia; Trombetta, Marcella

2010-02-01

Electrospinning of biopolymeric scaffolds is a new and effective approach for creating replacement tissues to repair defects and/or damaged tissues with direct clinical application. However, many hurdles and technical concerns regarding biological issues, such as cell retention and the ability to grow, still need to be overcome to gain full access to the clinical arena. Interaction with the host human tissues, immunogenicity, pathogen transmission as well as production costs, technical expertise, and good manufacturing and laboratory practice requirements call for careful consideration when aiming at the production of a material that is available off-the-shelf, to be used immediately in operative settings. The issue of sterilization is one of the most important steps for the clinical application of these scaffolds. Nevertheless, relatively few studies have been performed to systematically investigate how sterilization treatments may affect the properties of electrospun polymers for tissue engineering. This paper presents the results of a comparative study of different sterilization techniques applied to an electrospun poly-L-lactide scaffold: soaking in absolute ethanol, dry oven and autoclave treatments, UV irradiation, and hydrogen peroxide gas plasma treatment. Morphological and chemical characterization was coupled with microbiological sterility assay to validate the examined sterilization techniques in terms of effectiveness and modifications to the scaffold. The results of this study reveal that UV irradiation and hydrogen peroxide gas plasma are the most effective sterilization techniques, as they ensure sterility of the electrospun scaffolds without affecting their chemical and morphological features.

Nanostructured biomaterials from electrospun demineralized bone matrix: a survey of processing and crosslinking strategies.

PubMed

Leszczak, Victoria; Place, Laura W; Franz, Natalee; Popat, Ketul C; Kipper, Matt J

2014-06-25

In the design of scaffolds for tissue engineering biochemical function and nanoscale features are of particular interest. Natural polymers provide a wealth of biochemical function, but do not have the processability of synthetic polymers, limiting their ability to mimic the hierarchy of structures in the natural extracellular matrix. Thus, they are often combined with synthetic carrier polymers to enable processing. Demineralized bone matrix (DBM), a natural polymer, is allograft bone with inorganic material removed. DBM contains the protein components of bone, which includes adhesion ligands and osteoinductive signals, such as important growth factors. Herein we describe a novel method for tuning the nanostructure of DBM through electrospinning without the use of a carrier polymer. This work surveys solvents and solvent blends for electrospinning DBM. Blends of hexafluoroisopropanol and trifluoroacetic acid are studied in detail. The effects of DBM concentration and dissolution time on solution viscosity are also reported and correlated to observed differences in electrospun fiber morphology. We also present a survey of techniques to stabilize the resultant fibers with respect to aqueous environments. Glutaraldehyde vapor treatment is successful at maintaining both macroscopic and microscopic structure of the electrospun DBM fibers. Finally, we report results from tensile testing of stabilized DBM nanofiber mats, and preliminary evaluation of their cytocompatibility. The DBM nanofiber mats exhibit good cytocompatibility toward human dermal fibroblasts (HDF) in a 4-day culture; neither the electrospun solvents nor the cross-linking results in any measurable residual cytotoxicity toward HDF.

Electrospinning of Nanofibers for Energy Applications

PubMed Central

Sun, Guiru; Sun, Liqun; Xie, Haiming; Liu, Jia

2016-01-01

With global concerns about the shortage of fossil fuels and environmental issues, the development of efficient and clean energy storage devices has been drastically accelerated. Nanofibers are used widely for energy storage devices due to their high surface areas and porosities. Electrospinning is a versatile and efficient fabrication method for nanofibers. In this review, we mainly focus on the application of electrospun nanofibers on energy storage, such as lithium batteries, fuel cells, dye-sensitized solar cells and supercapacitors. The structure and properties of nanofibers are also summarized systematically. The special morphology of nanofibers prepared by electrospinning is significant to the functional materials for energy storage. PMID:28335256

Mechanism of Action of Electrospun Chitosan-Based Nanofibers against Meat Spoilage and Pathogenic Bacteria.

PubMed

Arkoun, Mounia; Daigle, France; Heuzey, Marie-Claude; Ajji, Abdellah

2017-04-06

This study investigates the antibacterial mechanism of action of electrospun chitosan-based nanofibers (CNFs), against Escherichia coli , Salmonella enterica serovar Typhimurium, Staphylococcus aureus and Listeria innocua , bacteria frequently involved in food contamination and spoilage. CNFs were prepared by electrospinning of chitosan and poly(ethylene oxide) (PEO) blends. The in vitro antibacterial activity of CNFs was evaluated and the susceptibility/resistance of the selected bacteria toward CNFs was examined. Strain susceptibility was evaluated in terms of bacterial type, cell surface hydrophobicity, and charge density, as well as pathogenicity. The efficiency of CNFs on the preservation and shelf life extension of fresh red meat was also assessed. Our results demonstrate that the antibacterial action of CNFs depends on the protonation of their amino groups, regardless of bacterial type and their mechanism of action was bactericidal rather than bacteriostatic. Results also indicate that bacterial susceptibility was not Gram-dependent but strain-dependent, with non-virulent bacteria showing higher susceptibility at a reduction rate of 99.9%. The susceptibility order was: E. coli > L. innocua > S. aureus > S. Typhimurium. Finally, an extension of one week of the shelf life of fresh meat was successfully achieved. These results are promising and of great utility for the potential use of CNFs as bioactive food packaging materials in the food industry, and more specifically in meat quality preservation.

Fabrication, Polarization of Electrospun Polyvinylidene Fluoride Electret Fibers and Effect on Capturing Nanoscale Solid Aerosols †

PubMed Central

Lolla, Dinesh; Lolla, Manideep; Abutaleb, Ahmed; Shin, Hyeon U.; Reneker, Darrell H.; Chase, George G.

2016-01-01

Electrospun polyvinylidene fluoride (PVDF) fiber mats with average fiber diameters (≈200 nm, ≈2000 nm) were fabricated by controlled electrospinning conditions. These fiber mats were polarized using a custom-made device to enhance the formation of the electret β-phase ferroelectric property of the fibers by simultaneous uniaxial stretching of the fiber mat and heating the mat to the Curie temperature of the PVDF polymer in a strong electric field of 2.5 kV/cm. Scanning electron microscopy, Fourier transform infrared spectroscopy, thermal gravimetric analysis, differential scanning calorimetry and Brunauer-Emmett-Teller (BET) surface area analyses were performed to characterize both the internal and external morphologies of the fiber mat samples to study polarization-associated changes. MATLAB simulations revealed the changes in the paths of the electric fields and the magnetic flux inside the polarization field with inclusion of the ferroelectric fiber mats. Both polarized and unpolarized fiber mats were challenged as filters against NaCl particles with average particle diameters of about 150 nm using a TSI 8130 to study capture efficiencies and relative pressure drops. Twelve filter experiments were conducted on each sample at one month time intervals between experiments to evaluate the reduction of the polarization enhancement over time. The results showed negligible polarization loss for the 200-nm fiber sample. The polarized mats had the highest filter efficiencies and lowest pressure drops. PMID:28773798

Improvement of sensitive CuO NFs-ITO nonenzymatic glucose sensor based on in situ electrospun fiber.

PubMed

Liu, Guangyue; Zheng, Baozhan; Jiang, Yanshu; Cai, Yuqing; Du, Juan; Yuan, Hongyan; Xiao, Dan

2012-11-15

CuO nanofibers (NFs), prepared by electrospinning and calcination technologies, have been applied for the fabrication of glucose sensors with high sensitivity and selectivity. Cu(NO(3))(2) and polyvinylpyrrolidone (PVP) composite nanofibers were initially electrospun on the surface of indium tin oxide (ITO) glass, and then the CuO NFs-ITO electrode was formed simply by removing PVP through heat treatment. The structures and morphologies of CuO nanofibers were characterized by X-ray diffraction, scanning electron microscopy and thermogravimetric analysis. The direct electrocatalytic oxidation of glucose in alkaline medium at CuO NFs-ITO electrode has also been investigated in detail with cyclic voltammetry, chronoamperometry and electrochemical impedance spectroscopy. The effects of NaOH concentration, electrospinning time, Cu(NO(3))(2):PVP mass ratios and calcination temperature on the response to glucose were investigated. Under optimized experimental conditions, the CuO NFs-ITO electrode produced high and reproducible sensitivity to glucose of 873 μA mM(-1)cm(-2). Linear responses were obtained over a concentration range from 0.20 μM to 1.3mM with a detection limit of 40 nM (S/N=3). The CuO NFs-ITO electrode also has good selectivity, stability and fast amperometic sensing of glucose, thus it can be used for the future development of non-enzymatic glucose sensors. Copyright © 2012 Elsevier B.V. All rights reserved.

Evaluation of structural and mechanical properties of electrospun nano-micro hybrid of poly hydroxybutyrate-chitosan/silk scaffold for cartilage tissue engineering

PubMed Central

Karbasi, Saeed; Fekrat, Farnoosh; Semnani, Daryoush; Razavi, Shahnaz; Zargar, Elham Naghash

2016-01-01

Background: One of the new methods of scaffold fabrication is a nano-micro hybrid structure in which the properties of the scaffold are improved by introducing nanometer and micrometer structures. This method could be suitable for scaffold designing if some features improve. Materials and Methods: In this study, electrospun nanofibers of 9% weight solution of poly (3-hydroxybutyrate) (P3HB) and a 15% weight of chitosan by trifluoroacetic acid were coated on both the surface of a silk knitted substrate in the optimum condition to improve the mechanical properties of scaffolds for cartilage tissue engineering application. These hybrid nano-micro fibrous scaffolds were characterized by structural and mechanical evaluation methods. Results: Scanning electron microscopy values and porosity analysis showed that average diameter of nanofibers was 584.94 nm in electrospinning part and general porosity was more than 80%. Fourier transform infrared spectroscopy results indicated the presence of all elements without pollution. The tensile test also stated that by electrospinning, as well as adding chitosan, both maximum strength and maximum elongation increased to 187 N and 10 mm. It means that the microfibrous part of scaffold could affect mechanical properties of nano part of the hybrid scaffold, significantly. Conclusions: It could be concluded that P3HB-chitosan/silk hybrid scaffolds can be a good candidate for cartilage tissue engineering. PMID:28028520

Evaluation of structural and mechanical properties of electrospun nano-micro hybrid of poly hydroxybutyrate-chitosan/silk scaffold for cartilage tissue engineering.

PubMed

Karbasi, Saeed; Fekrat, Farnoosh; Semnani, Daryoush; Razavi, Shahnaz; Zargar, Elham Naghash

2016-01-01

One of the new methods of scaffold fabrication is a nano-micro hybrid structure in which the properties of the scaffold are improved by introducing nanometer and micrometer structures. This method could be suitable for scaffold designing if some features improve. In this study, electrospun nanofibers of 9% weight solution of poly (3-hydroxybutyrate) (P3HB) and a 15% weight of chitosan by trifluoroacetic acid were coated on both the surface of a silk knitted substrate in the optimum condition to improve the mechanical properties of scaffolds for cartilage tissue engineering application. These hybrid nano-micro fibrous scaffolds were characterized by structural and mechanical evaluation methods. Scanning electron microscopy values and porosity analysis showed that average diameter of nanofibers was 584.94 nm in electrospinning part and general porosity was more than 80%. Fourier transform infrared spectroscopy results indicated the presence of all elements without pollution. The tensile test also stated that by electrospinning, as well as adding chitosan, both maximum strength and maximum elongation increased to 187 N and 10 mm. It means that the microfibrous part of scaffold could affect mechanical properties of nano part of the hybrid scaffold, significantly. It could be concluded that P3HB-chitosan/silk hybrid scaffolds can be a good candidate for cartilage tissue engineering.

Electrospun Gelatin/β-TCP Composite Nanofibers Enhance Osteogenic Differentiation of BMSCs and In Vivo Bone Formation by Activating Ca (2+) -Sensing Receptor Signaling.

PubMed

Zhang, Xuehui; Meng, Song; Huang, Ying; Xu, Mingming; He, Ying; Lin, Hong; Han, Jianmin; Chai, Yuan; Wei, Yan; Deng, Xuliang

2015-01-01

Calcium phosphate- (CaP-) based composite scaffolds have been used extensively for the bone regeneration in bone tissue engineering. Previously, we developed a biomimetic composite nanofibrous membrane of gelatin/β-tricalcium phosphate (TCP) and confirmed their biological activity in vitro and bone regeneration in vivo. However, how these composite nanofibers promote the osteogenic differentiation of bone marrow mesenchymal stem cells (BMSCs) is unknown. Here, gelatin/β-TCP composite nanofibers were fabricated by incorporating 20 wt% β-TCP nanoparticles into electrospun gelatin nanofibers. Electron microscopy showed that the composite β-TCP nanofibers had a nonwoven structure with a porous network and a rough surface. Spectral analyses confirmed the presence and chemical stability of the β-TCP and gelatin components. Compared with pure gelatin nanofibers, gelatin/β-TCP composite nanofibers caused increased cell attachment, proliferation, alkaline phosphatase activity, and osteogenic gene expression in rat BMSCs. Interestingly, the expression level of the calcium-sensing receptor (CaSR) was significantly higher on the composite nanofibrous scaffolds than on pure gelatin. For rat calvarial critical sized defects, more extensive osteogenesis and neovascularization occurred in the composite scaffolds group compared with the gelatin group. Thus, gelatin/β-TCP composite scaffolds promote osteogenic differentiation of BMSCs in vitro and bone regeneration in vivo by activating Ca(2+)-sensing receptor signaling.

A facile growth process of CeO2-Co3O4 composite nanotubes and its catalytic stability for CO oxidation

NASA Astrophysics Data System (ADS)

Oh, Hyerim; Kim, Il Hee; Lee, Nam-Suk; Dok Kim, Young; Kim, Myung Hwa

2017-08-01

Hybrid cerium dioxide (CeO2)-cobalt oxide (Co3O4) composite nanotubes were successfully prepared by a combination of electrospinning and thermal annealing using CeO2 and Co3O4 precursors for the first time. Electrospun CeO2-Co3O4 composite nanotubes represent relatively porous surface texture with small dimensions between 80 and 150 nm in the outer diameter. The microscopic investigations indicate that the nanoparticle like crystalline structures of CeO2 and Co3O4 are homogenously distributed and continuously connected to form the shape of nanotube in the length of a few micrometers during thermal annealing. It is expected that the different evaporation behaviors of solvents and matrix polymer between the core and the shell in as-spun nanofibers in the course of thermal annealing could be reasonably responsible for the formation of well-defined CeO2/Co3O4 hybrid nanotubes. Additionally, the general catalytic activities of electrospun CeO2/Co3O4 hybrid nanotubes toward the oxidation of carbon monoxide (CO) were carefully examined by a continuous flow system, resulting in favorable catalytic activity as well as catalytic stability for CO oxidation between 150 °C and 200 °C without the deactivation of the catalyst with time stems from accumulation of reaction intermediates such as carbonate species.

Novel nanoporous sorbent for solid-phase extraction in petroleum fingerprinting

NASA Astrophysics Data System (ADS)

Alayande, S. Oluwagbemiga; Hlengilizwe, Nyoni; Dare, E. Olugbenga; Msagati, Titus A. M.; Akinlabi, A. Kehinde; Aiyedun, P. O.

2016-04-01

Sample preparation is crucial in the analysis of petroleum and its derivatives. In this study, developing affordable sorbent for petroleum fingerprinting analysis using polymer waste such expanded polystyrene was explored. The potential of electrospun expanded polystyrene (EPS) as a sorbent for the solid-phase extraction (SPE) technique was investigated, and its efficiency was compared with commercial cartridges such as alumina, silica and alumina/silica hybrid commercial for petroleum fingerprinting analysis. The chromatograms showed that the packed electrospun EPS fibre demonstrated excellent properties for SPE applications relative to the hybrid cartridges.

Artificial Polymeric Scaffolds as Extracellular Matrix Substitutes for Autologous Conjunctival Goblet Cell Expansion

PubMed Central

He, Min; Storr-Paulsen, Thomas; Wang, Annie L.; Ghezzi, Chiara E.; Wang, Siran; Fullana, Matthew; Karamichos, Dimitrios; Utheim, Tor P.; Islam, Rakibul; Griffith, May; Islam, M. Mirazul; Hodges, Robin R.; Wnek, Gary E.; Kaplan, David L.; Dartt, Darlene A.

2016-01-01

Purpose We fabricated and investigated polymeric scaffolds that can substitute for the conjunctival extracellular matrix to provide a substrate for autologous expansion of human conjunctival goblet cells in culture. Methods We fabricated two hydrogels and two silk films: (1) recombinant human collagen (RHC) hydrogel, (2) recombinant human collagen 2-methacryloylxyethyl phosphorylcholine (RHC-MPC) hydrogel, (3) arginine-glycine-aspartic acid (RGD) modified silk, and (4) poly-D-lysine (PDL) coated silk, and four electrospun scaffolds: (1) collagen, (2) poly(acrylic acid) (PAA), (3) poly(caprolactone) (PCL), and (4) poly(vinyl alcohol) (PVA). Coverslips and polyethylene terephthalate (PET) were used for comparison. Human conjunctival explants were cultured on scaffolds for 9 to 15 days. Cell viability, outgrowth area, and the percentage of cells expressing markers for stratified squamous epithelial cells (cytokeratin 4) and goblet cells (cytokeratin 7) were determined. Results Most of cells grown on all scaffolds were viable except for PCL in which only 3.6 ± 2.2% of the cells were viable. No cells attached to PVA scaffold. The outgrowth was greatest on PDL-silk and PET. Outgrowth was smallest on PCL. All cells were CK7-positive on RHC-MPC while 84.7 ± 6.9% of cells expressed CK7 on PDL-silk. For PCL, 87.10 ± 3.17% of cells were CK7-positive compared to PET where 67.10 ± 12.08% of cells were CK7-positive cells. Conclusions Biopolymer substrates in the form of hydrogels and silk films provided for better adherence, proliferation, and differentiation than the electrospun scaffolds and could be used for conjunctival goblet cell expansion for eventual transplantation once undifferentiated and stratified squamous cells are included. Useful polymer scaffold design characteristics have emerged from this study. PMID:27832279

Artificial Polymeric Scaffolds as Extracellular Matrix Substitutes for Autologous Conjunctival Goblet Cell Expansion.

PubMed

He, Min; Storr-Paulsen, Thomas; Wang, Annie L; Ghezzi, Chiara E; Wang, Siran; Fullana, Matthew; Karamichos, Dimitrios; Utheim, Tor P; Islam, Rakibul; Griffith, May; Islam, M Mirazul; Hodges, Robin R; Wnek, Gary E; Kaplan, David L; Dartt, Darlene A

2016-11-01

We fabricated and investigated polymeric scaffolds that can substitute for the conjunctival extracellular matrix to provide a substrate for autologous expansion of human conjunctival goblet cells in culture. We fabricated two hydrogels and two silk films: (1) recombinant human collagen (RHC) hydrogel, (2) recombinant human collagen 2-methacryloylxyethyl phosphorylcholine (RHC-MPC) hydrogel, (3) arginine-glycine-aspartic acid (RGD) modified silk, and (4) poly-D-lysine (PDL) coated silk, and four electrospun scaffolds: (1) collagen, (2) poly(acrylic acid) (PAA), (3) poly(caprolactone) (PCL), and (4) poly(vinyl alcohol) (PVA). Coverslips and polyethylene terephthalate (PET) were used for comparison. Human conjunctival explants were cultured on scaffolds for 9 to 15 days. Cell viability, outgrowth area, and the percentage of cells expressing markers for stratified squamous epithelial cells (cytokeratin 4) and goblet cells (cytokeratin 7) were determined. Most of cells grown on all scaffolds were viable except for PCL in which only 3.6 ± 2.2% of the cells were viable. No cells attached to PVA scaffold. The outgrowth was greatest on PDL-silk and PET. Outgrowth was smallest on PCL. All cells were CK7-positive on RHC-MPC while 84.7 ± 6.9% of cells expressed CK7 on PDL-silk. For PCL, 87.10 ± 3.17% of cells were CK7-positive compared to PET where 67.10 ± 12.08% of cells were CK7-positive cells. Biopolymer substrates in the form of hydrogels and silk films provided for better adherence, proliferation, and differentiation than the electrospun scaffolds and could be used for conjunctival goblet cell expansion for eventual transplantation once undifferentiated and stratified squamous cells are included. Useful polymer scaffold design characteristics have emerged from this study.

Biodegradable scaffolds designed to mimic fascia-like properties for the treatment of pelvic organ prolapse and stress urinary incontinence.

PubMed

Roman, Sabiniano; Mangir, Naside; Bissoli, Julio; Chapple, Christopher R; MacNeil, Sheila

2016-05-01

There is an urgent clinical need for better synthetic materials to be used in surgical support of the pelvic floor. The aim of the current study was to construct biodegradable synthetic scaffolds that mimic the three-dimensional architecture of human fascia, which can integrate better into host tissues both mechanically and biologically. Therefore, four different polylactic acid (PLA) scaffolds with various degrees of fibre alignment were electrospun by modifying the electrospinning parameters. Physical and mechanical properties were assessed using a BOSE electroforce tensiometer. The attachment, viability and extracellular matrix production of adipose-derived stem cells cultured on the polylactic acid scaffolds were evaluated. The bulk density of the scaffolds decreased as the proportion of aligned fibres increased. Scaffolds became stronger and stiffer with increasing amounts of aligned fibres as measured along the axis parallel to the fibre alignment. In addition, more total collagen was produced on scaffolds with aligned fibres and was organised in the direction of the aligned fibres. In conclusion, the electrospinning technique can be easily modified to develop biodegradable scaffolds with a spectrum of mechanical properties allowing extracellular matrix organisation towards human-like fascia. © The Author(s) 2016.

A combination of CoO and Co nanoparticles supported on electrospun carbon nanofibers as highly stable air electrodes

NASA Astrophysics Data System (ADS)

Alegre, Cinthia; Busacca, Concetta; Di Blasi, Orazio; Antonucci, Vincenzo; Aricò, Antonino Salvatore; Di Blasi, Alessandra; Baglio, Vincenzo

2017-10-01

Bifunctional materials able to catalyze both the oxygen reduction (ORR) and the oxygen evolution (OER) reactions in alkaline media are still a challenge for the progress of energy conversion and storage devices such as metal-air batteries or unitized regenerative fuel cells. In this work, carbon nanofibers synthesized by electrospinning are modified with a combination of cobalt oxide and metallic cobalt (CoO-Co/CNF) and studied as a bifunctional air electrode for metal-air batteries. The performance of CoO-Co/CNF for both reactions is compared with state-of-the-art catalysts such as Pt/C and IrO2. The combination of cobalt oxide and metallic cobalt, finely distributed on the surface of graphitic carbon nanofibers, leads to a bifunctional catalyst with a half-wave potential for the ORR slightly better than Pt/C and a reversibility (ΔEOER-ORR) of 809 mV. The stability of CoO-Co/CNF is assessed by means of different stress tests: polarizations at high electrochemical potentials (2 V vs. RHE), rapid charge-discharge cycles at ±80 mA cm-2 and long durability tests by charging for 12 h at 60 mA cm-2 and discharging for 8 h at -80 mA cm-2. CoO-Co/CNF shows a remarkable stability, maintaining, at least, an 82% of its performance for the ORR after the stress tests, even when cycled for more than 100 h.

Preparation of High Purity, High Molecular-Weight Chitin from Ionic Liquids for Use as an Adsorbate for the Extraction of Uranium from Seawater

DOE Office of Scientific and Technical Information (OSTI.GOV)

Rogers, Robin

Ensuring a domestic supply of uranium is a key issue facing the wider implementation of nuclear power. Uranium is mostly mined in Kazakhstan, Australia, and Canada, and there are few high-grade uranium reserves left worldwide. Therefore, one of the most appealing potential sources of uranium is the vast quantity dissolved in the oceans (estimated to be 4.4 billion tons worldwide). There have been research efforts centered on finding a means to extract uranium from seawater for decades, but so far none have resulted in an economically viable product, due in part to the fact that the materials that have beenmore » successfully demonstrated to date are too costly (in terms of money and energy) to produce on the necessary scale. Ionic Liquids (salts which melt below 100{degrees}C) can completely dissolve raw crustacean shells, leading to recovery of a high purity, high molecular weight chitin powder and to fibers and films which can be spun directly from the extract solution suggesting that continuous processing might be feasible. The work proposed here will utilize the unprecedented control this makes possible over the chitin fiber a) to prepare electrospun nanofibers of very high surface area and in specific architectures, b) to modify the fiber surfaces chemically with selective extractant capacity, and c) to demonstrate their utility in the direct extraction and recovery of uranium from seawater. This approach will 1) provide direct extraction of chitin from shellfish waste thus saving energy over the current industrial process for obtaining chitin; 2) allow continuous processing of nanofibers for very high surface area fibers in an economical operation; 3) provide a unique high molecular weight chitin not available from the current industrial process, leading to stronger, more durable fibers; and 4) allow easy chemical modification of the large surface areas of the fibers for appending uranyl selective functionality providing selectivity and ease of stripping. The resulting sorbent should prove economically feasible, as well as providing an overall net energy gain.« less

The design, characteristics, and application of polyurethane dressings using the electrospinning process

NASA Astrophysics Data System (ADS)

Kampeerapappun, Piyaporn

In general, a dressing is used to protect and help heal wounds. There are several types of dressings on the market such as hydrocolloid, hydrogel, and medicated dressings. One technique for making a dressing is electrospinning, which is a very simple procedure used to produce fibers. Due to much smaller fiber-diameters than produced with the conventional technique, the fibers from electrospinning have unique properties: high porosity and high surface areas, which are advantageous for wound healing. In this research, the fibers were electrospun using polyurethane, TecophilicRTM or TecoflexRTM, with various additives. First, multilayer transdermal electrospun dressings, four and five-layers, were developed that allowed for the controlled release of nitric oxide (NO) from a NO2 -/ascorbic acid system encapsulated in polymer nanofibers. The amount of NO released from each wound dressing was investigated. Both the four and five-layer dressings were tested for morphology of fibers, water absorption, nitrite distribution, NO release profile after sterilization by gamma radiation, and stability. In the case of the four-layer transdermal dressing, the dressing was tested in diabetic, periodontal, and cutaneous leishmaniasis patients. Furthermore, the color change of dressing was investigated. TecophilicRTM was also spun with an antimicrobial agent, which was added to the TecophilicRTM solution to electrospin an antimicrobial dressing. The morphology of fibers was tested using an optical microscope and the water absorption, uniformity, and percent extraction of dressing were also determined. In addition, the efficiency of the antimicrobial agent in the dressing was determined according to SN 195920-1994 and ASTM 2149-01. Another NO-releasing dressing was developed employing the NO donor molecules, sodium salt of linear polyethylenimine NONOates (LPEINO-Na) and calcium salt of linear polyethylenimine NONOates (LPEINO-Ca), which were electrospun with TecophilicRTM. The NO release profiles for the LPEINO fibers were generated using a nitric oxide analyzer (NOA) and distribution of the particles in the dressing was examined. Moreover, the amount of NO released after patch storage for 1 and 2 months was determined.

Calcium phosphate deposition rate, structure and osteoconductivity on electrospun poly(l-lactic acid) matrix using electrodeposition or simulated body fluid incubation

PubMed Central

He, Chuanglong; Jin, Xiaobing; Ma, Peter X.

2013-01-01

Mineralized nanofibrous scaffolds have been proposed as promising scaffolds for bone regeneration due to their ability to mimic both nanoscale architecture and chemical composition of natural bone extracellular matrix (ECM). In this study, a novel electrodeposition method was compared with an extensively explored simulated body fluid (SBF) incubation method in terms of the deposition rate, chemical composition, and morphology of calcium phosphate formed on electrospun fibrous thin matrices with a fiber diameter in the range from about 200 nm to about 1400 nm prepared using 6, 8, 10 and 12 wt% poly(l-lactic acid) (PLLA) solutions in a mixture of dichloromethane and acetone (2:1 in volume). The effects of the surface modification using the two mineralization techniques on osteoblastic cell (MC3T3-E1) proliferation and differentiation were also examined. It was found that electrodeposition was two to three orders of magnitude faster than the SBF method in mineralizing the fibrous matrices, reducing the mineralization time from about two weeks to an hour to achieve the same amounts of mineralization. The mineralization rate also varied with the fiber diameter but in opposite directions between the two mineralization methods. As a general trend, the increase of fiber diameter resulted in a faster mineralization rate for the electrodeposition method but a slower mineralization rate for the SBF incubation method. Using the electrodeposition method, one can control the chemical composition and morphology of the calcium phosphate by varying the electric deposition potential and electrolyte temperature to tune the mixture of dicalcium phosphate dihydrate (DCPD) and hydroxy apatite (HAp). Using the SBF method, one can only obtain a low crystallinity HAp. The mineralized electrospun PLLA fibrous matrices from either method similarly facilitate the proliferation and osteogenic differentiation of preosteoblastic MC3T3-E1 cells as compared to neat PLLA matrices. Therefore, the electrodeposition method can be utilized as a fast and versatile technique to fabricate mineralized nanofibrous scaffolds for bone tissue engineering. PMID:24012605

Matrigel immobilization on the shish-kebab structured poly(ε-caprolactone) nanofibers for skin tissue engineering

DOE Office of Scientific and Technical Information (OSTI.GOV)

Jing, Xin, E-mail: jingxinscut@gmail.com; Mi, Hao-Yang; Wisconsin Institutes for Discovery, University of Wisconsin-Madison, 53715

Surface properties of tissue engineering scaffolds such as topography, hydrophilicity, and functional groups play a vital role in cell adhesion, migration, proliferation, and apoptosis. First, poly(ε-caprolactone) (PCL) shish-kebab scaffolds (PCL-SK), which feature a three-dimensional structure comprised of electrospun PCL nanofibers covered by periodic, self-induced PCL crystal lamellae on the surface, was created to mimic the nanotopography of native collagen fibrils in the extracellular matrix (ECM). Second, matrigel was covalently immobilized on the surface of alkaline hydrolyzed PCL-SK scaffolds to enhance their hydrophilicity. This combined approach not only mimics the nanotopography of native collagen fibrils, but also simulates the surface featuresmore » of collagen fibrils for cell growth. To investigate the viability of such scaffolds, HEF1 fibroblast cell assays were conducted and the results revealed that the nanotopography of the PCL-SK scaffolds facilitated cell adhesion and proliferation. The matrigel functionalization on PCL-SK scaffolds further enhanced cellular response, which suggested elevated biocompatibility and greater potential for skin tissue engineering applications.« less

Hierarchically engineered fibrous scaffolds for bone regeneration

PubMed Central

Sachot, Nadège; Castaño, Oscar; Mateos-Timoneda, Miguel A.; Engel, Elisabeth; Planell, Josep A.

2013-01-01

Surface properties of biomaterials play a major role in the governing of cell functionalities. It is well known that mechanical, chemical and nanotopographic cues, for example, influence cell proliferation and differentiation. Here, we present a novel coating protocol to produce hierarchically engineered fibrous scaffolds with tailorable surface characteristics, which mimic bone extracellular matrix. Based on the sol–gel method and a succession of surface treatments, hollow electrospun polylactic acid fibres were coated with a silicon–calcium–phosphate bioactive organic–inorganic glass. Compared with pure polymeric fibres that showed a completely smooth surface, the coated fibres exhibited a nanostructured topography and greater roughness. They also showed improved hydrophilic properties and a Young's modulus sixfold higher than non-coated ones, while remaining fully flexible and easy to handle. Rat mesenchymal stem cells cultured on these fibres showed great cellular spreading and interactions with the material. This protocol can be transferred to other structures and glasses, allowing the fabrication of various materials with well-defined features. This novel approach represents therefore a valuable improvement in the production of artificial matrices able to direct stem cell fate through physical and chemical interactions. PMID:23985738

Fabrication of continuous electrospun filaments with potential for use as medical fibres.

PubMed

Mouthuy, Pierre-Alexis; Zargar, Nasim; Hakimi, Osnat; Lostis, Emilie; Carr, Andrew

2015-05-19

Soft tissue injuries represent a substantial and growing social and economic burden. Medical fibres are commonly used to repair these injuries during surgery. Patient's outcomes are, however, not promising with around 40% of surgical repairs failing within the first few months after surgery due to poor tissue regeneration. The application of nanofibrous filaments and yarns as medical fibres and scaffolds has been suggested to improve soft tissue regeneration and enhance the quality of the repair. However, due to a lack of robustness and reliability of the current fabrication methods, continuous nanofibrous filaments cannot be manufactured and scaled up in industrial settings and are not currently available for clinical use. We have developed a robust and automated method that enables the manufacture of continuous electrospun filaments and which has the potential to be integrated into existing textile production lines. The technology uses a wire guide to form submicrofibres in a dense, narrow mesh which can be detached as a long and continuous thread. The thread can then be stretched and used to create multifilament yarns which can imitate the hierarchical architecture of tissues such as tendons and ligaments. Electrospun polydioxanone yarns produced by this method showed improved cellular proliferation and adhesion when compared to medical monofilament fibres in current clinical use. In vivo, the electrospun yarns showed a good safety profile with mild foreign body reaction and complete degradation within 5 months after implantation. These results suggest that this filament collection method has the potential to become a useful platform for the fabrication of future medical textiles.

Fabrication and In Vitro/In Vivo Performance of Mucoadhesive Electrospun Nanofiber Mats Containing α-Mangostin.

PubMed

Samprasit, Wipada; Rojanarata, Theerasak; Akkaramongkolporn, Prasert; Ngawhirunpat, Tanasait; Kaomongkolgit, Ruchadaporn; Opanasopit, Praneet

2015-10-01

This study aimed to fabricate mucoadhesive electrospun nanofiber mats containing α-mangostin for the maintenance of oral hygiene and reduction of the bacterial growth that causes dental caries. Synthesized thiolated chitosan (CS-SH) blended with polyvinyl alcohol (PVA) was selected as the mucoadhesive polymer. α-Mangostin was incorporated into the CS-SH/PVA solution and electrospun to obtain nanofiber mats. Scanning electron microscopy, differential scanning calorimetry, X-ray diffraction, and tensile strength testing were used to characterize the mats. The swelling degree and mucoadhesion were also determined. The nanofiber mats were further evaluated regarding their α-mangostin content, in vitro α-mangostin release, antibacterial activity, cytotoxicity, in vivo performance, and stability. The results indicated that the mats were in the nanometer range. The α-mangostin was well incorporated into the mats, with an amorphous form. The mats showed suitable tensile strength, swelling, and mucoadhesive properties. The loading capacity increased when the initial amount of α-mangostin was increased. Rapid release of α-mangostin from the mats was achieved. Additionally, a fast bacterial killing rate occurred at the lowest concentration of nanofiber mats when α-mangostin was added to the mats. The mats were less cytotoxic after use for 72 h. Moreover, in vivo testing indicated that the mats could reduce the number of oral bacteria, with a good mouth feel. The mats maintained the amount of α-mangostin for 6 months. The results suggest that α-mangostin-loaded mucoadhesive electrospun nanofiber mats may be a promising material for oral care and the prevention of dental caries.

Layering PLGA-based electrospun membranes and cell sheets for engineering cartilage-bone transition.

PubMed

Mouthuy, P-A; El-Sherbini, Y; Cui, Z; Ye, H

2016-04-01

It is now widely acknowledged that implants that have been designed with an effort towards reconstructing the transition between tissues might improve their functionality and integration in vivo. This paper contributes to the development of improved treatment for articular cartilage repair by exploring the potential of the combination of electrospinning technology and cell sheet engineering to create cartilage tissue. Poly(lactic-co-glycolic acid) (PLGA) was used to create the electrospun membranes. The focus being on the cartilage-bone transition, collagen type I and hydroxyapatite (HA) were also added to the scaffolds to increase the histological biocompatibility. Human mesenchymal stem cells (hMSCs) were cultured in thermoresponsive dishes to allow non-enzymatic removal of an intact cell layer after reaching confluence. The tissue constructs were created by layering electrospun membranes with sheets of hMSCs and were cultured under chondrogenic conditions for up to 21 days. High viability was found to be maintained in the multilayered construct. Under chondrogenic conditions, reverse-transcription-polymerase chain reaction (RT-PCR) and immunohistochemistry have shown high expression levels of collagen type X, a form of collagen typically found in the calcified zone of articular cartilage, suggesting an induction of chondrocyte hypertrophy in the PLGA-based scaffolds. To conclude, this paper suggests that layering electrospun scaffolds and cell sheets is an efficient approach for the engineering of tissue transitions, and in particular the cartilage-bone transition. The use of PLGA-based scaffold might be particularly useful for the bone-cartilage reconstruction, since the differentiated tissue constructs seem to show characteristics of calcified cartilage. Copyright © 2013 John Wiley & Sons, Ltd.

Development of novel electrospun dual-drug fiber mats loaded with a combination of ampicillin and metronidazole.

PubMed

Schkarpetkin, Dennis; Reise, Markus; Wyrwa, Ralf; Völpel, Andrea; Berg, Albrecht; Schweder, Martina; Schnabelrauch, Matthias; Watts, David C; Sigusch, Bernd W

2016-08-01

Our study was performed with the aim of preparing electrospun polylactide fibers with a combination of ampicillin (AMP) and metronidazole (MNZ) and investigating their drug release behavior and the antibacterial effect on Aggregatibacter actinomycetemcomitans and other oral pathogens. AMP and MNZ were integrated as a combination in two separate fibers (dual fiber mats - DFW mix) of electrospun PLA fiber mats by means of multijet electrospinning and in a single fiber (single fiber mats - SFW mix). HPLC (high-performance liquid chromatography) was used to measure the released drug quantities. Agar diffusion tests were used to determine the antibacterial effect of the eluates on A. actinomycetemcomitans, Fusobacterium nucleatum, Porphyromonas gingivalis and Enterococcus faecalis. The neutral red test was made to examine the cytocompatibility of the eluates with human gingival fibroblasts (hGFs). The release of the active agents varied with the antibiotic concentrations initially used in the fiber mats, but also with the distribution of the active agents in one or two fibers. Of the total quantity of MNZ (AMP), the SFW mix fiber mats released >60% (>70%) within a span of 5min, and 76% (71%) after 96h. With these drug concentrations released by the fiber mats (≥5m%), an antibacterial effect was achieved on A. actinomycetemcomitans and on all other species tested. Fiber mats and their eluates have no cytotoxic influence on human gingival fibroblasts (hGFs). Electrospun AMP/MNZ-loaded polymer fibers are a potential drug delivery system for use in periodontal and endodontic infections. Copyright © 2016 The Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

BMFO-PVDF electrospun fiber based tunable metamaterial structures for electromagnetic interference shielding in microwave frequency region

NASA Astrophysics Data System (ADS)

Revathi, Venkatachalam; Dinesh Kumar, Sakthivel; Subramanian, Venkatachalam; Chellamuthu, Muthamizhchelvan

2015-11-01

Metamaterial structures are artificial structures that are useful in controlling the flow of electromagnetic radiation. In this paper, composite fibers of sub-micron thickness of barium substituted magnesium ferrite (Ba0.2Mg0.8Fe2O4) - polyvinylidene fluoride obtained by electrospinning is used as a substrate to design electromagnetic interference shielding structures. While electrospinning improves the ferroelectric properties of the polyvinylidene fluoride, the presence of barium magnesium ferrite modifies the magnetic property of the composite fiber. The dielectric and magnetic properties at microwave frequency measured using microwave cavity perturbation technique are used to design the reflection as well as absorption based tunable metamaterial structures for electromagnetic interference shielding in microwave frequency region. For one of the structures, the simulation indicates that single negative metamaterial structure becomes a double negative metamaterial under the external magnetic field.

Investigation of Natural Bombyx mori Silk Fibroin Proteins Using INS

NASA Astrophysics Data System (ADS)

Crain, Christopher; Strange, Nicholas; Larese, J. Z.

The mechanical properties of many protein comprised biomaterials are a direct reflection of non-covalent (i.e. weak) interacting ions such as F-actin in muscles, tubulin in the cytoskeleton of cells, viral capsids, and silk. Porter and Vollrath underscored the two main factors that are critical for understanding the high mechanical strength of silks: the nanoscale semi-crystalline folding structure, which gives it exceptional toughness and strength, and the degree of hydration of the disordered fraction, which acts to modify these properties. Understanding and controlling these two principal factors are the key to the functionality of protein elastomers, and render silk an ideal model protein for (bio)material design. We will describe our investigation of electrospun silk of the Bombyx mori (silk worm), using Inelastic Neutron Scattering (INS). These techniques were used to investigate the microscopic dynamics of the dry and hydrated protein.

Fabrication and characterization of electrospun cellulose/nano-hydroxyapatite nanofibers for bone tissue engineering.

PubMed

Ao, Chenghong; Niu, Yan; Zhang, Ximu; He, Xu; Zhang, Wei; Lu, Canhui

2017-04-01

Nanofibrous scaffolds from cotton cellulose and nano-hydroxyapatite (nano-HA) were electrospun for bone tissue engineering. The solution properties of cellulose/nano-HA spinning dopes and their associated electrospinnability were characterized. Morphological, thermal and mechanical properties of the electrospun cellulose/nano-HA nanocomposite nanofibers (ECHNN) were measured and the biocompatibility of ECHNN with human dental follicle cells (HDFCs) was evaluated. Scanning electron microscope (SEM) images indicated that the average diameter of ECHNN increased with a higher nano-HA loading and the fiber diameter distributions were well within the range of natural ECM (extra cellular matrix) fibers (50-500nm). The ECHNN exhibited extraordinary mechanical properties with a tensile strength and a Young's modulus up to 70.6MPa and 3.12GPa respectively. Moreover, it was discovered that the thermostability of the ECHNN could be enhanced with the incorporation of nano-HA. Cell culture experiments demonstrated that the ECHNN scaffolds were quite biocompatible for HDFCs attachment and proliferation, suggesting their great potentials as scaffold materials in bone tissue engineering. Copyright © 2017 Elsevier B.V. All rights reserved.

Current strategies for sustaining drug release from electrospun nanofibers

PubMed Central

Chou, Shih-Feng; Carson, Daniel; Woodrow, Kim A.

2017-01-01

Electrospun drug-eluting fibers are emerging as a novel dosage form for multipurpose prevention against sexually transmitted infections, including HIV, and unintended pregnancy. Previous work from our lab and others show the versatility of this platform to deliver large doses of physico-chemically diverse agents. However, there is still an unmet need to develop practical fiber formulations for water-soluble small molecule drugs needed at high dosing due to intrinsic low potency or desire for sustained prevention. To date, most sustained release fibers have been restricted to the delivery of biologics or hydrophobic small molecules at low drug loading of typically < 1 wt.%, which is often impractical for most clinical applications. For hydrophilic small molecule drugs, their high aqueous solubility and poor partitioning and incompatibility with insoluble polymers make long-term release even more challenging. Here we investigate several existing strategies to sustain release of hydrophilic small molecule drugs that are highly-loaded in electrospun fibers. In particular, we investigate what is known about the design constraints required to realize multi-day release from fibers fabricated from uniaxial and coaxial electrospinning. PMID:26363300