Physical deterioration of preservative treated poles and pilings exposed to salt water

Treesearch

Grant T. Kirker; Jessie Glaeser; Stan T. Lebow; Frederick Green III; Carol A. Clausen

2011-01-01

This report details the results of laboratory analyses of wooden pilings sent to the USDA Forest Products Laboratory in March 2011. These samples were removed from coastal wooden posts, poles, piles, and deck boards. A total of 22 samples, consisting of either core borings or surface fiber samples, were removed from four installations along the South Carolina coast....

Correlation between physicochemical properties of modified clinoptilolite and its performance in the removal of ammonia-nitrogen.

PubMed

Dong, Yingbo; Lin, Hai; He, Yinhai

2017-03-01

The physicochemical properties of the 24 modified clinoptilolite samples and their ammonia-nitrogen removal rates were measured to investigate the correlation between them. The modified clinoptilolites obtained by acid modification, alkali modification, salt modification, and thermal modification were used to adsorb ammonia-nitrogen. The surface area, average pore width, macropore volume, mecropore volume, micropore volume, cation exchange capacity (CEC), zeta potential, silicon-aluminum ratios, and ammonia-nitrogen removal rate of the 24 modified clinoptilolite samples were measured. Subsequently, the linear regression analysis method was used to research the correlation between the physicochemical property of the different modified clinoptilolite samples and the ammonia-nitrogen removal rate. Results showed that the CEC was the major physicochemical property affecting the ammonia-nitrogen removal performance. According to the impacts from strong to weak, the order was CEC > silicon-aluminum ratios > mesopore volume > micropore volume > surface area. On the contrary, the macropore volume, average pore width, and zeta potential had a negligible effect on the ammonia-nitrogen removal rate. The relational model of physicochemical property and ammonia-nitrogen removal rate of the modified clinoptilolite was established, which was ammonia-nitrogen removal rate = 1.415[CEC] + 173.533 [macropore volume] + 0.683 [surface area] + 4.789[Si/Al] - 201.248. The correlation coefficient of this model was 0.982, which passed the validation of regression equation and regression coefficients. The results of the significance test showed a good fit to the correlation model.

The improvement of laser induced damage resistance of optical workpiece surface by hydrodynamic effect polishing

NASA Astrophysics Data System (ADS)

Peng, Wenqiang; Guan, Chaoliang; Li, Shengyi; Wang, Zhuo

2016-10-01

Surface and subsurface damage in optical element will greatly decrease the laser induced damage threshold (LIDT) in the intense laser optical system. Processing damage on the workpiece surface can be inevitably caused when the material is removed in brittle or plastic mode. As a non-contact polishing technology, hydrodynamic effect polishing (HEP) shows very good performance on generating an ultra-smooth surface without damage. The material is removed by chemisorption between nanoparticle and workpiece surface in the elastic mode in HEP. The subsurface damage and surface scratches can be effectively removed after the polishing process. Meanwhile ultra-smooth surface with atomic level surface roughness can be achieved. To investigate the improvement of LIDT of optical workpiece, polishing experiment was conducted on a magnetorheological finishing (MRF) silica glass sample. AFM measurement results show that all the MRF directional plastic marks have been removed clearly and the root-mean-square (rms) surface roughness has decreased from 0.673nm to 0.177nm after HEP process. Laser induced damage experiment was conducted with laser pulse of 1064nm wavelength and 10ns time width. Compared with the original state, the LEDT of the silica glass sample polished by HEP has increased from 29.78J/cm2 to 45.47J/cm2. It demonstrates that LIDT of optical element treated by HEP can be greatly improved for ultra low surface roughness and nearly defect-free surface/subsurface.

Water-quality monitoring for a pilot piling removal field evaluation, Coal Creek Slough, Washington, 2008-09

USGS Publications Warehouse

Nilsen, Elena B.; Alvarez, David A.

2011-01-01

Significant Findings Water and sediment quality monitoring was conducted before and after the removal of a piling field located in Coal Creek Slough near Longview, Washington. Passive chemical samplers and continuous water-quality monitoring instruments were deployed at the piling removal site, Coal Creek Slough Site 1 (CCS1), and at a comparison site, Coal Creek Slough Site 2 (CCS2), before (2008) and after (2009) piling removal. Surface and subsurface (core) sediment samples were collected before and after piling removal and were analyzed for grain size, organic carbon content, and chemicals of concern. Significant findings from this study include: * Phenanthrene was the only compound detected in wood piling samples analyzed for a large suite of semivolatile organic compounds and polycyclic aromatic hydrocarbons (PAHs). Metals potentially associated with wood treatment were detected in the wood piling samples at low concentrations. * Organic carbon was slightly lower in core samples from CCS1 in pre-removal (2008) and post-removal (2009) samples than in surface samples from both sites in both years. * Grain-size class distributions were relatively uniform between sites and years. * Thirty-four out of 110 chemicals of concern were detected in sediments. Eight of those detected were anthropogenic waste indicator (AWI) compounds, 18 were PAHs, 4 were sterols, and 4 were metals potentially associated with wood treatment. * Nearly all reported concentrations of chemicals of concern in sediments are qualified as estimates, primarily due to interferences in extracts resulting from complex sample matrices. Indole, perylene, and fluoranthene are reported without qualification for some of the samples, and the metals are reported without qualification for all samples. * The highest frequency of detection of chemicals of concern was seen in the pre-removal surface samples at both sites. * AWI compounds were detected less frequently and at lower concentrations during the post-removal sampling compared to the pre-removal sampling. * Several PAHs were detected at relatively high concentrations in core samples, likely indicating historical sources. * Most commonly detected PAHs in sediments were 2,6-dimethylnaphthalene, fluoranthene, perylene, and pyrene. * Most commonly detected AWIs in sediments were 3-methyl-1h-indole (skatol), acetophenone, indole, phenol, and paracresol. * Sedimentary concentrations of perylene exceeded available sediment quality guidelines. Perylene is widespread in the environment and has large potential natural sources in addition to its anthropogenic sources. * Concentrations of metals did not exceed sediment quality guidelines. * Multiple organochlorine pesticides, both banned and currently used, were detected at each site using passive samplers. * Commonly detected pesticides included hexachlorobenzene, pentachloroanisole (a degradation product of pentachlorophenol), diazinon, cis-chlordane, endosulfan, DDD, and endosulfan sulfate. * PBDE concentrations detected in passive sampler extracts were less than the method detection limit at all sites with the exception of PBDE-99, detected at a concentration less than the reporting limit. * The fragrance galaxolide was detected at a concentration greater than the method detection limit. * Common PAHs, such as phenanthrene, fluoranthene, and pyrene, were detected in every passive sampler. * Dissolved oxygen concentration was slightly higher at site CCS1 compared to site CCS2 in both years. * Overall, there was no systematic increase in chemicals of concern at the restoration site during post-removal monitoring compared to conditions during pre-removal monitoring. Any immediate, short-duration effects of piling removal on water quality could not be determined because monitoring was not conducted during the removal.

Design of Microstructured Conducting Polymer Films for Enhanced Trace Explosives Detection

NASA Astrophysics Data System (ADS)

Laster, Jennifer S.

The detection of trace amounts of explosive material is critical to national security. Ion mobility spectrometer (IMS)-based contact sampling continues to be a common method employed for the detection of explosives in high security checkpoint applications, such as airport security. In this process a surface of interest, such as a passenger's hands or luggage, is probed by a swab or particle trap to collect and transfer residue to an IMS for analysis. The collection of residue on a sampling swab has been shown to be a limiting step in this detection process. As such, there is significant need to develop new materials with increased adhesion to explosive analytes and with superior particle removal abilities. Here, the design of novel sampling swabs is presented for the enhanced collection of trace explosive residue from surfaces. First, the influence of the swab microstructure on the ability to remove particles from representative substrates is demonstrated. Free-standing microstructured polypyrrole (PPy) films of a variety of dimensions and form factors are fabricated using a templated electropolymerization process. The removal of polystyrene fluorescent particles from an aluminum substrate of varying surface roughness is examined as a function of the polymer microstructure. PPy microstructured films display enhanced particle removal abilities compared to PPy non-structured and current commercial films. This increase in particle removal is attributed to the increased particle-swab contact from the microstructured films. Next, the influence of the surface chemistry of sampling swabs on the collection of a representative explosive analyte, trinitrotoluene (TNT) is explored. The surface chemistry of PPy films is modified by electropolymerizaton of an N-substituted pyrrole monomer. The surface chemistries examined include a methyl, carboxylic acid, and amino-phenyl functionality. The vapor deposition of TNT on the surface of the functionalized PPy films is quantified through ultraviolet-visible (UV-vis) absorption and compared to commercial swabbing materials of varying chemistry and surface roughness. The PPy modified films with potential sites for hydrogen bonding display the highest deposition of TNT, while the Teflon coated commercial films display the lowest interaction with TNT. Finally, the desorption and release of TNT from sampling swabs is studied as an effect of temperature and of applied bias. For successful analyte detection within an IMS, the residue collected on a sampling swab must be released from the swab, typically through a thermal desorption process. In this work the release of TNT from sampling swabs is determined through solid-phase microextraction-gas chromatography mass spectrometry (SPME-GCMS). The results of this thesis provide important information on the design considerations for the development of novel particle sampling swabs with increased performance.

Cytotoxicity of Light-Cured Dental Materials according to Different Sample Preparation Methods

PubMed Central

Lee, Myung-Jin; Kim, Mi-Joo; Kwon, Jae-Sung; Lee, Sang-Bae; Kim, Kwang-Mahn

2017-01-01

Dental light-cured resins can undergo different degrees of polymerization when applied in vivo. When polymerization is incomplete, toxic monomers may be released into the oral cavity. The present study assessed the cytotoxicity of different materials, using sample preparation methods that mirror clinical conditions. Composite and bonding resins were used and divided into four groups according to sample preparation method: uncured; directly cured samples, which were cured after being placed on solidified agar; post-cured samples were polymerized before being placed on agar; and “removed unreacted layer” samples had their oxygen-inhibition layer removed after polymerization. Cytotoxicity was evaluated using an agar diffusion test, MTT assay, and confocal microscopy. Uncured samples were the most cytotoxic, while removed unreacted layer samples were the least cytotoxic (p < 0.05). In the MTT assay, cell viability increased significantly in every group as the concentration of the extracts decreased (p < 0.05). Extracts from post-cured and removed unreacted layer samples of bonding resin were less toxic than post-cured and removed unreacted layer samples of composite resin. Removal of the oxygen-inhibition layer resulted in the lowest cytotoxicity. Clinicians should remove unreacted monomers on the resin surface immediately after restoring teeth with light-curing resin to improve the restoration biocompatibility. PMID:28772647

Adsorptive removal of microcystin-LR from surface and wastewater using tyre-based powdered activated carbon: Kinetics and isotherms.

PubMed

Mashile, Phodiso P; Mpupa, Anele; Nomngongo, Philiswa N

2018-04-01

Microcystin LR (MC-LR) is a highly toxic compound and it is known for its adverse health effect on both humans and animals. Due to the ineffectiveness of conventional water treatments methods, for the past decades, researchers have been developing cost-effective ways of removing MC-LR from water bodies. This study reports the application of powdered activated carbon (PAC) obtained from the waste tyre for the removal of MC-LR. The choice of the adsorbent was chosen due to its attractive properties. The prepared tyre-based PAC was found to have the large surface area (1111 m 2  g -1 ). The detection of MC-LR was achieved using high performance liquid chromatography (HPLC) coupled with a PDA detector. The experimental parameters (such as optimum pH, dosage and contact time) affecting the removal of MC-LR using tyre based-powdered activated carbon were optimized using response surface methodology (RSM). Maximum removal of MC-LR was achieved under the following optimum conditions; sample pH 4, carbon dosage concentration 10,000 mg L -1 and contact time of 34 min. Under optimum conditions, kinetic studies and adsorption isotherms reflected better fit for pseudo-second-order rate and Langmuir isotherm model, respectively. The optimized method was applied for the removal of MC-LR in wastewater sample. The effluent and influent sample contained initial concentrations ranging from 0.52 to 8.54 μg L -1 and the removal efficiency was 100%. Copyright © 2018 Elsevier Ltd. All rights reserved.

Laser-driven hydrothermal process studied with excimer laser pulses

NASA Astrophysics Data System (ADS)

Mariella, Raymond; Rubenchik, Alexander; Fong, Erika; Norton, Mary; Hollingsworth, William; Clarkson, James; Johnsen, Howard; Osborn, David L.

2017-08-01

Previously, we discovered [Mariella et al., J. Appl. Phys. 114, 014904 (2013)] that modest-fluence/modest-intensity 351-nm laser pulses, with insufficient fluence/intensity to ablate rock, mineral, or concrete samples via surface vaporization, still removed the surface material from water-submerged target samples with confinement of the removed material, and then dispersed at least some of the removed material into the water as a long-lived suspension of nanoparticles. We called this new process, which appears to include the generation of larger colorless particles, "laser-driven hydrothermal processing" (LDHP) [Mariella et al., J. Appl. Phys. 114, 014904 (2013)]. We, now, report that we have studied this process using 248-nm and 193-nm laser light on submerged concrete, quartzite, and obsidian, and, even though light at these wavelengths is more strongly absorbed than at 351 nm, we found that the overall efficiency of LDHP, in terms of the mass of the target removed per Joule of laser-pulse energy, is lower with 248-nm and 193-nm laser pulses than with 351-nm laser pulses. Given that stronger absorption creates higher peak surface temperatures for comparable laser fluence and intensity, it was surprising to observe reduced efficiencies for material removal. We also measured the nascent particle-size distributions that LDHP creates in the submerging water and found that they do not display the long tail towards larger particle sizes that we had observed when there had been a multi-week delay between experiments and the date of measuring the size distributions. This is consistent with transient dissolution of the solid surface, followed by diffusion-limited kinetics of nucleation and growth of particles from the resulting thin layer of supersaturated solution at the sample surface.

Genesis Ultrapure Water Megasonic Wafer Spin Cleaner

NASA Technical Reports Server (NTRS)

Allton, Judith H.; Stansbery, Eileen K.; Calaway, Michael J.; Rodriquez, Melissa C.

2013-01-01

A device removes, with high precision, the majority of surface particle contamination greater than 1-micron-diameter in size from ultrapure semiconductor wafer materials containing implanted solar wind samples returned by NASA's Genesis mission. This cleaning device uses a 1.5-liter/minute flowing stream of heated ultrapure water (UPW) with 1- MHz oscillating megasonic pulse energy focused at 3 to 5 mm away from the wafer surface spinning at 1,000 to 10,000 RPM, depending on sample size. The surface particle contamination is removed by three processes: flowing UPW, megasonic cavitations, and centripetal force from the spinning wafer. The device can also dry the wafer fragment after UPW/megasonic cleaning by continuing to spin the wafer in the cleaning chamber, which is purged with flowing ultrapure nitrogen gas at 65 psi (.448 kPa). The cleaner also uses three types of vacuum chucks that can accommodate all Genesis-flown array fragments in any dimensional shape between 3 and 100 mm in diameter. A sample vacuum chuck, and the manufactured UPW/megasonic nozzle holder, replace the human deficiencies by maintaining a consistent distance between the nozzle and wafer surface as well as allowing for longer cleaning time. The 3- to 5-mm critical distance is important for the ability to remove particles by megasonic cavitations. The increased UPW sonication time and exposure to heated UPW improve the removal of 1- to 5-micron-sized particles.

Particulate Removal Using a CO2 Composite Spray Cleaning System

NASA Technical Reports Server (NTRS)

Chen, Nicole; Lin, Ying; Jackson, David; Chung, Shirley

2016-01-01

The Planetary Protection surface cleanliness requirements for potential Mars Sample Return hardware that would come in contact with Martian samples may be stricter than previous missions. The Jet Propulsion Laboratory has developed a new technology that will enable us to remove sub-micron size particles from critical hardware surfaces. A hand-held CO2 composite cleaning system was tested to verify its cleaning capabilities. This convenient, portable device can be used in cleanrooms for cleaning after rework or during spacecraft integration and assembly. It is environmentally safe and easy to use. This cleaning concept has the potential to be further developed into a robotic cleaning device on a Mars Lander to be used to clean sample acquisition or sample handling devices in situ. Contaminants of known sizes and concentrations, such as fluorescent microspheres and spores were deposited on common spacecraft material surfaces. The cleaning efficiency results will be presented and discussed.

Improving the work function of the niobium surface of SRF cavities by plasma processing

DOE Office of Scientific and Technical Information (OSTI.GOV)

Tyagi, P. V.; Doleans, M.; Hannah, B.

2016-01-01

An in situ plasma processing technique using chemically reactive oxygen plasma to remove hydrocarbons from superconducting radio frequency cavity surfaces at room temperature was developed at the spallation neutron source, at Oak Ridge National Laboratory. To understand better the interaction between the plasma and niobium surface, surface studies on small samples were performed. In this article, we report the results from those surface studies. The results show that plasma processing removes hydrocarbons from top surface and improves the surface work function by 0.5₋1.0 eV. Improving the work function of RF surface of cavities can help to improve their operational performance.

Removal and deposition efficiencies of the long-lived 222Rn daughters during etching of germanium surfaces

NASA Astrophysics Data System (ADS)

Zuzel, G.; Wójcik, M.; Majorovits, B.; Lampert, M. O.; Wendling, P.

2012-06-01

Removal and deposition efficiencies of the long-lived 222Rn daughters during etching from and onto surfaces of standard and high purity germanium were investigated. The standard etching procedure of Canberra-France used during production of high purity n-type germanium diodes was applied to germanium discs, which have been exposed earlier to a strong radon source for deposition of its progenies. An uncontaminated sample was etched in a solution containing 210Pb, 210Bi and 210Po. All isotopes were measured before and after etching with appropriate detectors. In contrast to copper and stainless steel, they were removed from germanium very efficiently. However, the reverse process was also observed. Considerable amounts of radioactive lead, bismuth and polonium isotopes present initially in the artificially polluted etchant were transferred to the clean high purity surface during processing of the sample.

Performance and Surface Integrity of Ti6Al4V After Sinking EDM with Special Graphite Electrodes

NASA Astrophysics Data System (ADS)

Amorim, Fred L.; Stedile, Leandro J.; Torres, Ricardo D.; Soares, Paulo C.; Henning Laurindo, Carlos A.

2014-04-01

Titanium and its alloys have high chemical reactivity with most of the cutting tools. This makes it difficult to work with these alloys using conventional machining processes. Electrical discharge machining (EDM) emerges as an alternative technique to machining these materials. In this work, it is investigated the performance of three special grades of graphite as electrodes when ED-Machining Ti6Al4V samples under three different regimes. The main influences of electrical parameters are discussed for the samples material removal rate, volumetric relative wear and surface roughness. The samples surfaces were evaluated using SEM images, microhardness measurements, and x-ray diffraction. It was found that the best results for samples material removal rate, surface roughness, and volumetric relative wear were obtained for the graphite electrode with 10-μm particle size and negative polarity. For all samples machined by EDM and characterized by x-ray (XRD), it was identified the presence of titanium carbides. For the finish EDM regimes, the recast layer presents an increased amount of titanium carbides compared to semi-finish and rough regimes.

Non-invasive biomonitoring for PFRs and PBDEs: new insights in analysis of human hair externally exposed to selected flame retardants.

PubMed

Kucharska, Agnieszka; Covaci, Adrian; Vanermen, Guido; Voorspoels, Stefan

2015-02-01

In this study, we investigated the hypothesis whether externally adsorbed and internally deposited flame retardants (FRs) in hair could be distinguished. To this extent, hair samples collected from one volunteer were exposed under controlled conditions to phosphate FR (PFR) and polybrominated diphenyl ether (PBDE) standards to mimic external contamination. Afterwards, suitable washing procedures to selectively remove contaminants from the hair surface were investigated. The samples were measured by GC-(ECNI)-MS for PBDEs and LC-(ESI+)-MS/MS for PFRs. All investigated compounds were transferred onto the hair surface. One of the most important finding was that dust particles are not mandatory to transfer compounds on the hair surface and to be able to measure high levels of compounds in human hair. To assess different protocols to selectively remove external contamination, the exposed hair samples were washed in different media before analysis: water, methanol, hexane:dichloromethane (1:1, v/v), acetone and shampoo. Results indicated that there is no washing medium able to entirely and exclusively remove external contamination. Among investigated media, methanol removed a meaningful part of the external contamination (42-105%), but the removal efficiencies differed among compounds. We therefore concluded that hair should not be washed prior to analysis and in case of visible contamination (e.g. with cosmetic products), water would be the recommended agent. Organic solvents should not be used for the washing step. Although it is impossible to distinguish external from internal exposure, hair samples may be used as valuable biomarker of human exposure, providing a measure of integral exposure. To the best of our knowledge, this is the first study which has used externally exposed hair samples to PBDEs and PFRs. Copyright © 2014 Elsevier B.V. All rights reserved.

Role of surface energy and nano-roughness in the removal efficiency of bacterial contamination by nonwoven wipes from frequently touched surfaces

NASA Astrophysics Data System (ADS)

Edwards, Nicholas W. M.; Best, Emma L.; Connell, Simon D.; Goswami, Parikshit; Carr, Chris M.; Wilcox, Mark H.; Russell, Stephen J.

2017-12-01

Healthcare associated infections (HCAIs) are responsible for substantial patient morbidity, mortality and economic cost. Infection control strategies for reducing rates of transmission include the use of nonwoven wipes to remove pathogenic bacteria from frequently touched surfaces. Wiping is a dynamic process that involves physicochemical mechanisms to detach and transfer bacteria to fibre surfaces within the wipe. The purpose of this study was to determine the extent to which systematic changes in fibre surface energy and nano-roughness influence removal of bacteria from an abiotic polymer surface in dry wiping conditions, without liquid detergents or disinfectants. Nonwoven wipe substrates composed of two commonly used fibre types, lyocell (cellulosic) and polypropylene, with different surface energies and nano-roughnesses, were manufactured using pilot-scale nonwoven facilities to produce samples of comparable structure and dimensional properties. The surface energy and nano-roughness of some lyocell substrates were further adjusted by either oxygen (O2) or hexafluoroethane (C2F6) gas plasma treatment. Static adpression wiping of an inoculated surface under dry conditions produced removal efficiencies of between 9.4% and 15.7%, with no significant difference (p < 0.05) in the relative removal efficiencies of Escherichia coli, Staphylococcus aureus or Enterococcus faecalis. However, dynamic wiping markedly increased peak wiping efficiencies to over 50%, with a minimum increase in removal efficiency of 12.5% and a maximum increase in removal efficiency of 37.9% (all significant at p < 0.05) compared with static wiping, depending on fibre type and bacterium. In dry, dynamic wiping conditions, nonwoven wipe substrates with a surface energy closest to that of the contaminated surface produced the highest E. coli removal efficiency, while the associated increase in fibre nano-roughness abrogated this trend with S. aureus and E. faecalis.

Mini-implants for Orthodontic Anchorage: Surface Analysis after Redrilling and Sterilization - An in vitro Study.

PubMed

Gross, J M; Nascimento, G G; Araújo, V C; Bönecker, Mjs; Furuse, C

2016-04-01

This study aimed to investigate, in vitro, possible alterations on mini-implants surface after retrieval and if the cleaning process and sterilization can predispose damages. Two commercial mini-implants were tested for deformations after drilling and removing in artificial bone four times. Samples were analyzed by scanning electron microscopy, and surface alterations verified through thread and pitches deformation. To alterations caused by insertion/removal and the cleaning process and sterilization were verified in different procedures: Insertions and sterilization, only insertions, and only sterilization. Photomicrographs were analyzed in order to compare the surface characteristics. Head deformation was verified qualitatively. For a quantitative analysis, distances between threads were measured across the active part of the mini-implants. No deformation was observed in both groups. The cleaning and sterilization processes did not provoke alteration in both groups. Nevertheless, the presence of synthetic bone was noted in some samples. The mean distances between implant threads were similar after all steps in all regions in both groups. The results suggest that the tested mini-implants can be retrieved without damage of its surface after four cycles of insertion, removal, and sterilization. Orthodontic mini-implant, Redrilling, Sterilization. Mini-implants can be retrieved without damage to its surface after four cycles of insertion, removal, and sterilization in the same patient without representing a biological concern.

Sorption and speciation of iodine in groundwater system: The roles of organic matter and organic-mineral complexes.

PubMed

Li, Junxia; Zhou, Hailing; Wang, Yanxin; Xie, Xianjun; Qian, Kun

2017-06-01

Characterizing the properties of main host of iodine in soil/sediment and the geochemical behaviors of iodine species are critical to understand the mechanisms of iodine mobilization in groundwater systems. Four surface soil and six subsurface sediment samples were collected from the iodine-affected area of Datong basin in northern China to conduct batch experiments and to evaluate the effects of NOM and/or organic-mineral complexes on iodide/iodate geochemical behaviors. The results showed that both iodine contents and k f -iodate values had positive correlations with solid TOC contents, implying the potential host of NOM for iodine in soil/sediment samples. The results of chemical removal of easily extracted NOM indicated that the NOM of surface soils is mainly composed of surface embedded organic matter, while sediment NOM mainly occurs in the form of organic-mineral complexes. After the removal of surface sorbed NOM, the decrease in k f -iodate value of treated surface soils indicates that surface sorbed NOM enhances iodate adsorption onto surface soil. By contrast, k f -iodate value increases in several H 2 O 2 -treated sediment samples, which was considered to result from exposed rod-like minerals rich in Fe/Al oxyhydroxide/oxides. After chemical removal of organic-mineral complexes, the lowest k f -iodate value for both treated surface soils and sediments suggests the dominant role of organic-mineral complexes on controlling the iodate geochemical behavior. In comparison with iodate, iodide exhibited lower affinities on all (un)treated soil/sediment samples. The understanding of different geochemical behaviors of iodine species helps to explain the occurrence of high iodine groundwater with iodate and iodide as the main species in shallow (oxidizing conditions) and deep (reducing conditions) groundwater. Copyright © 2017 Elsevier B.V. All rights reserved.

Sorption and speciation of iodine in groundwater system: The roles of organic matter and organic-mineral complexes

NASA Astrophysics Data System (ADS)

Li, Junxia; Zhou, Hailing; Wang, Yanxin; Xie, Xianjun; Qian, Kun

2017-06-01

Characterizing the properties of main host of iodine in soil/sediment and the geochemical behaviors of iodine species are critical to understand the mechanisms of iodine mobilization in groundwater systems. Four surface soil and six subsurface sediment samples were collected from the iodine-affected area of Datong basin in northern China to conduct batch experiments and to evaluate the effects of NOM and/or organic-mineral complexes on iodide/iodate geochemical behaviors. The results showed that both iodine contents and kf-iodate values had positive correlations with solid TOC contents, implying the potential host of NOM for iodine in soil/sediment samples. The results of chemical removal of easily extracted NOM indicated that the NOM of surface soils is mainly composed of surface embedded organic matter, while sediment NOM mainly occurs in the form of organic-mineral complexes. After the removal of surface sorbed NOM, the decrease in kf-iodate value of treated surface soils indicates that surface sorbed NOM enhances iodate adsorption onto surface soil. By contrast, kf-iodate value increases in several H2O2-treated sediment samples, which was considered to result from exposed rod-like minerals rich in Fe/Al oxyhydroxide/oxides. After chemical removal of organic-mineral complexes, the lowest kf-iodate value for both treated surface soils and sediments suggests the dominant role of organic-mineral complexes on controlling the iodate geochemical behavior. In comparison with iodate, iodide exhibited lower affinities on all (un)treated soil/sediment samples. The understanding of different geochemical behaviors of iodine species helps to explain the occurrence of high iodine groundwater with iodate and iodide as the main species in shallow (oxidizing conditions) and deep (reducing conditions) groundwater.

Studies of EUV contamination mitigation

NASA Astrophysics Data System (ADS)

Graham, Samual, Jr.; Malinowski, Michael E.; Steinhaus, Chip; Grunow, Philip A.; Klebanoff, Leonard E.

2002-07-01

Carbon contamination removal was investigated using remote RF-O2, RF-H2, and atomic hydrogen experiments. Samples consisted of silicon wafers coated with 100 Angstrom sputtered carbon, as well as bare Si-capped Mo/Si optics. Samples were exposed to atomic hydrogen or RF plasma discharges at 100 W, 200 W, and 300 W. Carbon removal rate, optic oxidation rate, at-wavelength (13.4 nm) peak reflectance, and optic surface roughness were characterized. Data show that RF- O2 removes carbon at a rate approximately 6 times faster RF- H2 for a given discharge power. However, both cleaning techniques induce Mo/Si optic degradation through the loss of reflectivity associated with surface oxide growth for RF-O2 and an unknown mechanism with hydrogen cleaning. Atomic hydrogen cleaning shows carbon removal rates sufficient for use as an in-situ cleaning strategy for EUVoptics with less risk of optic degradation from overexposures than RF-discharge cleaning. While hydrogen cleaning (RF and atomic) of EUV optics has proven effective in carbon removal, attempts to dissociate hydrogen in co-exposures with EUV radiation have resulted in no detectable removal of carbon contamination.

Rapid extraction and assay of uranium from environmental surface samples

DOE Office of Scientific and Technical Information (OSTI.GOV)

Barrett, Christopher A.; Chouyyok, Wilaiwan; Speakman, Robert J.

Extraction methods enabling faster removal and concentration of uranium compounds for improved trace and low-level assay are demonstrated for standard surface sampling material in support of nuclear safeguards efforts, health monitoring, and other nuclear analysis applications. A key problem with the existing surface sampling swipes is the requirement for complete digestion of sample and sampling matrix. This is a time-consuming and labour-intensive process that limits laboratory throughput, elevates costs, and increases background levels. Various extraction methods are explored for their potential to quickly and efficiently remove different chemical forms of uranium from standard surface sampling material. A combination of carbonatemore » and peroxide solutions is shown to give the most rapid and complete form of uranyl compound extraction and dissolution. This rapid extraction process is demonstrated to be compatible with standard inductive coupled plasma mass spectrometry methods for uranium isotopic assay as well as screening techniques such as x-ray fluorescence. The general approach described has application beyond uranium to other analytes of nuclear forensic interest (e.g., rare earth elements and plutonium) as well as heavy metals for environmental and industrial hygiene monitoring.« less

Removal of organic pollutants and heavy metals in soils by electrokinetic remediation.

PubMed

Ricart, M T; Pazos, M; Gouveia, S; Cameselle, C; Sanroman, M A

2008-07-01

In this work, the feasibility of electrokinetic remediation for the restoration of polluted soil with organic and inorganic compounds had been development and evaluated using a model soil sample. The model soil was prepared with kaolinite clay artificially polluted in the laboratory with chromium and an azo dye: Reactive Black 5 (RB5). The electromigration of Cr in a spiked kaolinite sample was studied in alkaline conditions. Despite of the high pH registered in the kaolinite sample (around pH 9.5), Cr migrated towards the cathode and it was accumulated in the cathode chamber forming a white precipitate. The removal was not complete, and 23% of the initial Cr was retained into the kaolinite sample close to the cathode side. The azo dye RB5 could be effectively removed from kaolinite by electrokinetics and the complete cleanup of the kaolinite could be achieved in alkaline environment. In this condition, RB5 formed an anion that migrated towards the anode where it was accumulated and quickly degraded upon the electrode surface. The electrokinetic treatment of a kaolinite sample polluted with both Cr and RB5 yielded very good results. The removal of Cr was improved compared to the experiment where Cr was the only pollutant, and RB5 reached a removal as high as 95%. RB5 was removed by electromigration towards the anode, where the dye was degraded upon the surface of the electrode by electrochemical oxidation. Cr was transported towards the cathode by electromigration and electroosmosis. It is supposed that the interaction among RB5 and Cr into the kaolinite sample prevented premature precipitation and allow Cr to migrate and concentrate in the cathode chamber.

Genesis Solar Wind Collector Cleaning Assessment: Update on 60336 Sample Case Study

NASA Technical Reports Server (NTRS)

Goreva, Y. S.; Allums, K. K.; Gonzalez, C. P.; Jurewicz, A. J.; Burnett, D. S.; Allton, J. H.; Kuhlman, K. R.; Woolum, D.

2015-01-01

To maximize the scientific return of Genesis Solar Wind return mission it is necessary to characterize and remove a crash-derived particle and thin film surface contamination. A small subset of Genesis mission collector fragments are being subjected to extensive study via various techniques. Here we present an update on the sample 60336, a Czochralski silicon (Si-CZ) based wafer from the bulk array (B/C). This sample has undergone multiple cleaning steps (see the table below): UPW spin wash, aggressive chemical cleanings (including aqua regia, hot xylene and RCA1), as well as optical and chemical (EDS, ToF-SIMS) imaging. Contamination appeared on the surface of 60336 after the initial 2007 UPW cleaning. Aqua regia and hot xylene treatment (8/13/2013) did little to remove contaminants. The sample was UPW cleaned for the third time and imaged (9/16/13). The UPW removed the dark stains that were visible on the sample. However, some features, like "the Flounder" (a large, 100 micron feature in Fig. 1b) appeared largely intact, resisting all previous cleaning efforts. These features were likely from mobilized adhesive, derived from the Post-It notes used to stabilize samples for transport from Utah after the hard landing. To remove this contamination, an RCA step 1 organic cleaning (RCA1) was employed. Although we are still uncertain on the nature of the Flounder and why it is resistant to UPW and aqua regia/hot xylene treatment, we have found RCA1 to be suitable for its removal. It is likely that the glue from sticky pads used during collector recovery may have been a source for resistant organic contamination [9]; however [8] shows that UPW reaction with crash-derived organic contamination does not make particle removal more difficult.

Combined wet and dry cleaning of SiGe(001)

DOE Office of Scientific and Technical Information (OSTI.GOV)

Park, Sang Wook; Kaufman-Osborn, Tobin; Kim, Hyonwoong

Combined wet and dry cleaning via hydrofluoric acid (HF) and atomic hydrogen on Si{sub 0.6}Ge{sub 0.4}(001) surface was studied at the atomic level using ultrahigh vacuum scanning tunneling microscopy (STM), scanning tunneling spectroscopy (STS), and x-ray photoelectron spectroscopy to understand the chemical transformations of the surface. Aqueous HF removes native oxide, but residual carbon and oxygen are still observed on Si{sub 0.6}Ge{sub 0.4}(001) due to hydrocarbon contamination from post HF exposure to ambient. The oxygen contamination can be eliminated by shielding the sample from ambient via covering the sample in the HF cleaning solution until the sample is introduced tomore » the vacuum chamber or by transferring the sample in an inert environment; however, both processes still leave carbon contaminant. Dry in-situ atomic hydrogen cleaning above 330 °C removes the carbon contamination on the surface consistent with a thermally activated atomic hydrogen reaction with surface hydrocarbon. A postdeposition anneal at 550 °C induces formation of an atomically flat and ordered SiGe surface observed by STM. STS verifies that the wet and dry cleaned surface has an unpinned Fermi level with no states between the conduction and valence band edge comparable to sputter cleaned SiGe surfaces.« less

Evaluation of vacuum filter sock surface sample collection method for Bacillus spores from porous and non-porous surfaces.

PubMed

Brown, Gary S; Betty, Rita G; Brockmann, John E; Lucero, Daniel A; Souza, Caroline A; Walsh, Kathryn S; Boucher, Raymond M; Tezak, Matthew S; Wilson, Mollye C

2007-07-01

Vacuum filter socks were evaluated for recovery efficiency of powdered Bacillus atrophaeus spores from two non-porous surfaces, stainless steel and painted wallboard and two porous surfaces, carpet and bare concrete. Two surface coupons were positioned side-by-side and seeded with aerosolized Bacillus atrophaeus spores. One of the surfaces, a stainless steel reference coupon, was sized to fit into a sample vial for direct spore removal, while the other surface, a sample surface coupon, was sized for a vacuum collection application. Deposited spore material was directly removed from the reference coupon surface and cultured for enumeration of colony forming units (CFU), while deposited spore material was collected from the sample coupon using the vacuum filter sock method, extracted by sonication and cultured for enumeration. Recovery efficiency, which is a measure of overall transfer effectiveness from the surface to culture, was calculated as the number of CFU enumerated from the filter sock sample per unit area relative to the number of CFU enumerated from the co-located reference coupon per unit area. The observed mean filter sock recovery efficiency from stainless steel was 0.29 (SD = 0.14, n = 36), from painted wallboard was 0.25 (SD = 0.15, n = 36), from carpet was 0.28 (SD = 0.13, n = 40) and from bare concrete was 0.19 (SD = 0.14, n = 44). Vacuum filter sock recovery quantitative limits of detection were estimated at 105 CFU m(-2) from stainless steel and carpet, 120 CFU m(-2) from painted wallboard and 160 CFU m(-2) from bare concrete. The method recovery efficiency and limits of detection established in this work provide useful guidance for the planning of incident response environmental sampling for biological agents such as Bacillus anthracis.

Examination of Surface Deposits on Oldbury Reactor Core Graphite to Determine the Concentration and Distribution of 14C.

PubMed

Payne, Liam; Heard, Peter J; Scott, Thomas B

2016-01-01

Pile Grade A graphite was used as a moderator and reflector material in the first generation of UK Magnox nuclear power reactors. As all of these reactors are now shut down there is a need to examine the concentration and distribution of long lived radioisotopes, such as 14C, to aid in understanding their behaviour in a geological disposal facility. A selection of irradiated graphite samples from Oldbury reactor one were examined where it was observed that Raman spectroscopy can distinguish between underlying graphite and a surface deposit found on exposed channel wall surfaces. The concentration of 14C in this deposit was examined by sequentially oxidising the graphite samples in air at low temperatures (450°C and 600°C) to remove the deposit and then the underlying graphite. The gases produced were captured in a series of bubbler solutions that were analysed using liquid scintillation counting. It was observed that the surface deposit was relatively enriched with 14C, with samples originating lower in the reactor exhibiting a higher concentration of 14C. Oxidation at 600°C showed that the remaining graphite material consisted of two fractions of 14C, a surface associated fraction and a graphite lattice associated fraction. The results presented correlate well with previous studies on irradiated graphite that suggest there are up to three fractions of 14C; a readily releasable fraction (corresponding to that removed by oxidation at 450°C in this study), a slowly releasable fraction (removed early at 600°C in this study), and an unreleasable fraction (removed later at 600°C in this study).

Examination of Surface Deposits on Oldbury Reactor Core Graphite to Determine the Concentration and Distribution of 14C

PubMed Central

Payne, Liam; Heard, Peter J.; Scott, Thomas B.

2016-01-01

Pile Grade A graphite was used as a moderator and reflector material in the first generation of UK Magnox nuclear power reactors. As all of these reactors are now shut down there is a need to examine the concentration and distribution of long lived radioisotopes, such as 14C, to aid in understanding their behaviour in a geological disposal facility. A selection of irradiated graphite samples from Oldbury reactor one were examined where it was observed that Raman spectroscopy can distinguish between underlying graphite and a surface deposit found on exposed channel wall surfaces. The concentration of 14C in this deposit was examined by sequentially oxidising the graphite samples in air at low temperatures (450°C and 600°C) to remove the deposit and then the underlying graphite. The gases produced were captured in a series of bubbler solutions that were analysed using liquid scintillation counting. It was observed that the surface deposit was relatively enriched with 14C, with samples originating lower in the reactor exhibiting a higher concentration of 14C. Oxidation at 600°C showed that the remaining graphite material consisted of two fractions of 14C, a surface associated fraction and a graphite lattice associated fraction. The results presented correlate well with previous studies on irradiated graphite that suggest there are up to three fractions of 14C; a readily releasable fraction (corresponding to that removed by oxidation at 450°C in this study), a slowly releasable fraction (removed early at 600°C in this study), and an unreleasable fraction (removed later at 600°C in this study). PMID:27706228

Protein-functionalized magnetic iron oxide nanoparticles: time efficient potential-water treatment

NASA Astrophysics Data System (ADS)

Okoli, Chuka; Boutonnet, Magali; Järås, Sven; Rajarao-Kuttuva, Gunaratna

2012-10-01

Recent advances in nanoscience suggest that the existing issues involving water quality could be resolved or greatly improved using nanomaterials, especially magnetic iron oxide nanoparticles. Magnetic nanoparticles have been synthesized for the development and use, in association with natural coagulant protein for water treatment. The nanoparticles size, morphology, structure, and magnetic properties were characterized by transmission electron microscope, X-ray diffraction, and superconducting quantum interference device magnetometry. Purified Moringa oleifera protein was attached onto microemulsions-prepared magnetic iron oxide nanoparticles (ME-MION) to form stable protein-functionalized magnetic nanoparticles (PMO+ME-MION). The turbidity removal efficiency in both synthetic and surface water samples were investigated and compared with the commonly used synthetic coagulant (alum) as well as PMO. More than 90 % turbidity could be removed from the surface waters within 12 min by magnetic separation of PMO+ME-MION; whereas gravimetrically, 70 % removal in high and low turbid waters can be achieved within 60 min. In contrast, alum requires 180 min to reduce the turbidity of low turbid water sample. These data support the advantage of separation with external magnetic field (magnetophoresis) over gravitational force. Time kinetics studies show a significant enhancement in ME-MION efficiency after binding with PMO implying the availability of large surface of the ME-MION. The coagulated particles (impurities) can be removed from PMO+ME-MION by washing with mild detergent or cleaning solution. To our knowledge, this is the first report on surface water turbidity removal using protein-functionalized magnetic nanoparticle.

Removal of dust particles from metal-mirror surfaces by excimer-laser radiation

NASA Astrophysics Data System (ADS)

Mann, Klaus R.; Wolff-Rottke, B.; Mueller, F.

1995-07-01

The effect of particle desorption from Al mirror surfaces by the influence of pulsed UV laser radiation has been studied. The investigations are closely related to the demands of astronomers, who are looking for a more effective way of cleaning the Al coatings of future very large telescope mirrors. A systematic parameter study has been performed in order to determine the irradiation conditions which yield the highest dust removal efficiency (i.e. reflectivity increase) on contaminated samples, taking particularly into account laser-induced damage and degradation effects of coating and substrate. The particle removal rate increases with increasing laser fluence, being limited however by the damage threshold of the coating. Therefore, parameters influencing the damage threshold of metal coatings like wavelength, pulse width, and number of pulses have been studied in detail. Data indicate that on Al coated BK7 and Zerodur samples KrF laser radiation yields the optimum result, with cleaning efficiencies comparable to polymer film stripping. The initial reflectivity of the clean coating can nearly be reinstalled, in particular when an additional solvent film on the sample surface is applied. Hence, laser desorption seems to be a viable method of cleaning large Al mirrors for telescopes.

Characteristics of the surface chemistry of linden pyrochar after removal of labile organic matter

NASA Astrophysics Data System (ADS)

Valeeva, A. A.; Smirnova, E. V.; Giniyatullin, K. G.; Vorobev, V. V.; Biktasheva, L. R.; Grachev, A. N.

2018-01-01

The changes of chemical properties of the pyrochar surface were studied in the laboratory experiment that simulated pedogenic transformation of pyrochar under the influence of soil biota. The native pyrochar samples were obtained by pyrolysis of linden wood residues at the temperature of 250°C, 450°C and 650°C. Their modified samples were obtained by removing an easily degradable pool of organic substances that can be used by microorganisms during the first months after application to the soil. In low-temperature linden pyrochar (250°C and 450°C) dominated carboxylic and phenolic surface groups, in high-temperature (650°C) - lactonic groups. After removal of readily decomposable organic substances the acidity of the phenolic and lactonic groups in pyrochar of low-temperature pyrolysis sharply decreased. Characteristic feature of all studied samples is the presence in IR spectra of absorption bands of gyroxyl, carbonyl, methylene groups and organosilicon polymers. The feature of IR spectra of linden pyrochar (250°C and 450°C) is the presence of absorption bands of the stretching vibrations of the tertiary alcohols and phenols C-O group.

Impact of an Environmental Cleaning Intervention on the Presence of Methicillin-Resistant Staphylococcus aureus and Vancomycin-Resistant Enterococci on Surfaces in Intensive Care Unit Rooms

PubMed Central

Goodman, Eric R.; Platt, Richard; Bass, Richard; Onderdonk, Andrew B.; Yokoe, Deborah S.; Huang, Susan S.

2009-01-01

OBJECTIVES To evaluate the adequacy of discharge room cleaning and the impact of a cleaning intervention on the presence of methicillin-resistant Staphylococcus aureus (MRSA) and vancomycin-resistant enterococci (VRE) on environmental surfaces in intensive care unit (ICU) rooms. DESIGN Prospective environmental study. SETTING AND SAMPLE Convenience sample of ICU rooms in an academic hospital. METHODS AND INTERVENTION The intervention consisted of (1) a change from the use of pour bottles to bucket immersion for applying disinfectant to cleaning cloths, (2) an educational campaign, and (3) feedback regarding adequacy of discharge cleaning. Cleaning of 15 surfaces was evaluated by inspecting for removal of a preapplied mark, visible only with an ultraviolet lamp (“black light”). Six surfaces were cultured for MRSA or VRE contamination. Outcomes of mark removal and culture positivity were evaluated by χ2 testing and generalized linear mixed models, clustering by room. RESULTS The black-light mark was removed from 44% of surfaces at baseline, compared with 71% during the intervention (P <.001). The intervention increased the likelihood of removal of black-light marks after discharge cleaning (odds ratio, 4.4; P < .001), controlling for ICU type (medical vs surgical) and type of surface. The intervention reduced the likelihood of an environmental culture positive for MRSA or VRE (proportion of cultures positive, 45% at baseline vs 27% during the intervention; adjusted odds ratio, 0.4; P = .02). Broad, flat surfaces were more likely to be cleaned than were doorknobs and sink or toilet handles. CONCLUSIONS Increasing the volume of disinfectant applied to environmental surfaces, providing education for Environmental Services staff, and instituting feedback with a black-light marker improved cleaning and reduced the frequency of MRSA and VRE contamination. PMID:18624666

DOE Office of Scientific and Technical Information (OSTI.GOV)

Leishear, R.; Thaxton, D.; Minichan, R.

A sampling tool was required to evaluate residual activity ({mu}Curies per square foot) on the inner wall surfaces of underground nuclear waste storage tanks. The tool was required to collect a small sample from the 3/8 inch thick tank walls. This paper documents the design, testing, and deployment of the remotely operated sampling device. The sampler provides material from a known surface area to estimate the overall surface contamination in the tank prior to closure. The sampler consisted of a sampler and mast assembly mast assembly, control system, and the sampler, or end effector, which is defined as the operatingmore » component of a robotic arm. The mast assembly consisted of a vertical 30 feet long, 3 inch by 3 inch, vertical steel mast and a cantilevered arm hinged at the bottom of the mast and lowered by cable to align the attached sampler to the wall. The sampler and mast assembly were raised and lowered through an opening in the tank tops, called a riser. The sampler is constructed of a mounting plate, a drill, springs to provide a drive force to the drill, a removable sampler head to collect the sample, a vacuum pump to draw the sample from the drill to a filter, and controls to operate the system. Once the sampler was positioned near the wall, electromagnets attached it to the wall, and the control system was operated to turn on the drill and vacuum to remove and collect a sample from the wall. Samples were collected on filters in removable sampler heads, which were readily transported for further laboratory testing.« less

Evaluation of polyacrylonitrile electrospun nano-fibrous mats as leukocyte removal filter media.

PubMed

Pourbaghi, Raha; Zarrebini, Mohammad; Semnani, Dariush; Pourazar, Abbasali; Akbari, Nahid; Shamsfar, Reihaneh

2018-07-01

Removal of leukocytes from blood products is the most effective means for elimination of undesirable side effects and prevention of possible reactions in recipients. Micro-fibrous mats are currently used for removal of leukocytes from blood. In this study, samples of electrospun nano-fibrous mats were produced. The performance of the produced electrospun nano-fibrous mats as means of leukocytes removal from fresh whole blood was both evaluated and compared with that of commercially available micro-fibrous mats. In order to produce the samples, polyacrylonitrile (PAN) nano-fibrous mats were made under different electrospinning conditions. Mean fiber diameter, pore characterization and surface roughness of the PAN nano-fibrous mats were determined using image processing technique. In order to evaluate the surface tension of the fabricated mats, water contact angle was measured. The leukocyte removal performance, erythrocytes recovery percent and hemolysis rate of the nano-fibrous mats were compared. The effectiveness of nano-fibrous mats in removing leukocyte was established using both scanning electron microscope and optical microscope. Results showed that for given weight, the fabricated nano-fibrous mats were not only more efficient but also more cost-effective than their commercial counterparts. Results confirmed that changes in mean fiber diameter, the number of layer and weight of each layer in the absence of any chemical reaction or physical surface modification, the fabricated nano-fibrous mats were able to remove 5-log of leukocytes. © 2017 Wiley Periodicals, Inc. J Biomed Mater Res Part B: Appl Biomater, 106B: 1759-1769, 2018. © 2017 Wiley Periodicals, Inc.

Removal of heavy metal ions by biogenic hydroxyapatite: Morphology influence and mechanism study

NASA Astrophysics Data System (ADS)

Wang, Dandan; Guan, Xiaomei; Huang, Fangzhi; Li, Shikuo; Shen, Yuhua; Chen, Jun; Long, Haibo

2016-08-01

Based on the synthesis of hydroxyapatite (HA) with different morphologies, such as nanorod-like, flower-like and sphere-like assembled HA nanorods, a new strategy has been developed for the removal of heavy metal ions such as Pb2+, Cu2+, Mn2+, Zn2+. The dependence of removal efficiency on the morphology and the suspended concentration of trapping agent, the removal time and selectivity were evaluated and discussed. The experimental results proved that the removal capacity of flower-like assembled HA nanorods (NAFL-HA) was the best, and the maximum removal ratio for Pb2+ ion was 99.97%. The mechanism of Pb2+ removal was studied in detail, noting that some metal ions were completely incorporated into hydroxyapatitie to produce Pb-HA. It reveals that the metal ions capture by HA is mainly controlled by sample surface adsorption and co-precipitation, which are directly controlled by sample morphology.

The possibly important role played by Ga{sub 2}O{sub 3} during the activation of GaN photocathode

DOE Office of Scientific and Technical Information (OSTI.GOV)

Fu, Xiaoqian, E-mail: ise-fuxq@ujn.edu.cn, E-mail: 214808748@qq.com; Institute of Electronic Engineering and Optoelectronic Technology, Nanjing University of Science and Technology, Nanjing 210094; Wang, Honggang

2015-08-14

Three different chemical solutions are used to remove the possible contamination on GaN surface, while Ga{sub 2}O{sub 3} is still found at the surface. After thermal annealing at 710 °C in the ultrahigh vacuum (UHV) chamber and activated with Cs/O, all the GaN samples are successfully activated to the effective negative electron affinity (NEA) photocathodes. Among all samples, the GaN sample with the highest content of Ga{sub 2}O{sub 3} after chemical cleaning obtains the highest quantum efficiency. By analyzing the property of Ga{sub 2}O{sub 3}, the surface processing results, and electron affinity variations during Cs and Cs/O{sub 2} deposition on GaNmore » of other groups, it is suggested that before the adsorption of Cs, Ga{sub 2}O{sub 3} is not completely removed from GaN surface in our samples, which will combine with Cs and lead to a large decrease in electron affinity. Furthermore, the effective NEA is formed for GaN photocathode, along with the surface downward band bending. Based on this assumption, a new dipole model Ga{sub 2}O{sub 3}-Cs is suggested, and the experimental effects are explained and discussed.« less

Characterization of the March 2017 tank 10 surface sample (combination of HTF-10-17-30 AND HTF-10-17-31) and variable depth sample (combination of HTF-10-17-32 and HTF-10-17-33)

DOE Office of Scientific and Technical Information (OSTI.GOV)

Reboul, S. H.

Two surface samples (HTF-10-17-30 and HTF-10-17-31) and two variable depth samples (HTF-10-17-32 and HTF-10-17-33) were collected from SRS Tank 10 during March 2017 and submitted to SRNL for characterization. At SRNL, the two surface samples were combined in one container, the two variable depth samples (VDSs) were combined in another container, and then the two composite samples were each characterized by a series of physical, ionic, radiological, and elemental analysis methods. The surface sample composite was characterized primarily for Tank Farm corrosion control purposes, while the VDS composite was characterized primarily for Tank Closure Cesium Removal (TCCR) purposes.

Shear test of composite bonded to dentin: Er:YAG laser versus dental handpiece preparations

NASA Astrophysics Data System (ADS)

Visuri, Steven R.; Gilbert, Jeremy L.; Walsh, Joseph T., Jr.; Wigdor, Harvey A.

1995-05-01

The erbium:YAG laser coupled with a cooling stream of water appears to be an effective means of removing dental hard tissues. However, before the procedure is deemed clinically viable, there are several important issues of safety and efficacy that need to be explored. In this study we investigated the surface that remains following laser ablation of dentin and compared the results to the use of a dental handpiece. Specifically, we studied the effect the laser radiation had on the bonding of composite to dentin. The crowns of extracted human molars were removed revealing the underlying dentin. An additional thickness of material was removed with either a dental handpiece or an Er:YAG laser by raster scanning the samples under a fixed handpiece or laser. Comparable surface roughnesses were achieved. A cylinder of composite was bonded onto the prepared surfaces following the manufacturer's directions. The dentin-composite bond was then shear stressed to failure on a universal testing apparatus and the maximum load recorded. Preliminary results indicated that laser irradiated samples had improved bond strengths. SEM photographs of the surfaces were also taken to compare the two methods of tooth preparation.

Improvement of oxygen-containing functional groups on olive stones activated carbon by ozone and nitric acid for heavy metals removal from aqueous phase.

PubMed

Bohli, Thouraya; Ouederni, Abdelmottaleb

2016-08-01

Recently, modification of surface structure of activated carbons in order to improve their adsorption performance toward especial pollutants has gained great interest. Oxygen-containing functional groups have been devoted as the main responsible for heavy metal binding on the activated carbon surface; their introduction or enhancement needs specific modification and impregnation methods. In the present work, olive stones activated carbon (COSAC) undergoes surface modifications in gaseous phase using ozone (O3) and in liquid phase using nitric acid (HNO3). The activated carbon samples were characterized using N2 adsorption-desorption isotherm, SEM, pHpzc, FTIR, and Boehm titration. The activated carbon parent (COSAC) has a high surface area of 1194 m(2)/g and shows a predominantly microporous structure. Oxidation treatments with nitric acid and ozone show a decrease in both specific surface area and micropore volumes, whereas these acidic treatments have led to a fixation of high amount of surface oxygen functional groups, thus making the carbon surface more hydrophilic. Activated carbon samples were used as an adsorbent matrix for the removal of Co(II), Ni(II), and Cu(II) heavy metal ions from aqueous solutions. Adsorption isotherms were obtained at 30 °C, and the data are well fitted to the Redlich-Peterson and Langmuir equation. Results show that oxidized COSACs, especially COSAC(HNO3), are capable to remove more Co(II), Cu(II), and Ni(II) from aqueous solution. Nitric acid-oxidized olive stones activated carbon was tested in its ability to remove metal ions from binary systems and results show an important maximum adsorbed amount as compared to single systems.

Qualitative Time-of-Flight Secondary Ion Mass Spectrometry Analysis of Root Dentin Irrigated with Sodium Hypochlorite, EDTA, or Chlorhexidine.

PubMed

Kolosowski, Kamil P; Sodhi, Rana N S; Kishen, Anil; Basrani, Bettina R

2015-10-01

Sodium hypochlorite (NaOCl), chelating agents, and chlorhexidine (CHX), which are commonly used irrigants during endodontic treatment, have the potential to alter the physical and chemical properties of the dentin structure. The aim of this study was to use time-of-flight secondary ion mass spectrometry to qualitatively evaluate the chemical characteristics of dentin surface and compare it with dentin exposed to NaOCl, EDTA, or CHX. Four blocks of dentin from a root of a human maxillary molar were embedded in resin and trimmed with a microtome to expose the dentin. Samples were randomly assigned to 4 treatment groups: (1) no irrigation treatment (sample A), (2) 2.5% NaOCl (sample B), (3) 17% EDTA (sample C), and (4) 2% CHX (sample D). Dentin surfaces were analyzed by time-of-flight secondary ion mass spectrometry, which allowed characterization of dentin surface chemistry by both imaging and mass spectroscopic analysis obtained in high mass and spatial resolution modes. Sample A revealed intense peaks characteristics of hydroxyapatite in addition to Na(+), K(+), CH4N(+), CN(-), CNO(-), Mg(+), F(-), and HCO2(-) peaks. Sample B showed severely decreased CH4N(+) and increased intensity of Cl(-). Sample C lacked Ca(+) and Mg(+) and showed decreased PO2(-) and PO3(-). Sample D exhibited a distinct presence of CHX. The spectral image of sample A displayed even distribution of Na(+) and Ca(+) on a smeared surface. The surfaces of samples B and D had patent dentinal tubules, whereas sample D showed an intense CHX signal. Sample C had some patent dentinal tubules and lacked Ca(+). NaOCl removed protein components from the dentin matrix, EDTA removed calcium and magnesium ions from the dentin, and CHX formed an adsorbed layer on the dentin surface. Copyright © 2015 American Association of Endodontists. Published by Elsevier Inc. All rights reserved.

X-Ray Photoelectron Spectroscopy and Tribology Studies of Annealed Fullerene-like WS2 Nanoparticles

NASA Astrophysics Data System (ADS)

Kopnov, F.; Tenne, R.; Späth, B.; Jägermann, W.; Cohen, H.; Feldman, Y.; Zak, A.; Moshkovich, A.; Rapoport, L.

The temporal chemical changes occurring at the surface of fullerene-like (IF) nanoparticles of WS2 were investigated using X-ray photo-electron spectroscopy (XPS) and compared to those of bulk powder (2H) of the same material. It is possible to follow the long term (surface oxidation and carbonization) occurring at defects on the outermost surface (0001) layer of the fullerene-like nanoparticles. Similar but perhaps more distinctive changes are observed on the prismatic (hk0) surfaces of the 2H powder. Vacuum annealing is shown to remove most of these changes and bring the surface close to its stoichiometric composition. In accordance with previous measurements, further evidence is obtained for the existence of water molecules which are entrapped in the hollow core and interstitial defects of the fullerene-like nanoparticles during the synthesis. They are also shown to be removed by the vacuum annealing process. Chemically resolved electrical measurements (CREM) in the XPS show that the vacuum annealed IF samples become more intrinsic. Finally, tribological measurements show that the vacuum annealed IF samples perform better as an additive to oil than the non-annealed IF samples and the bulk (2H) platelets powder.

Preparation of Ti/IrO2 Anode with Low Iridium Content by Thermal Decomposition Process: Electrochemical removal of organic pollutants in water

NASA Astrophysics Data System (ADS)

Yaqub, Asim; Isa, Mohamed Hasnain; Ajab, Huma; Kutty, S. R. M.; Ezechi, Ezerie H.; Farooq, Robina

2018-04-01

In this study IrO2 (Iridium oxide) was coated onto a titanium plate anode from a dilute (50 mg/10 ml) IrCl3×H2O salt solution. Coating was done at high temperature (550∘C) using thermal decomposition. Surface morphology and characteristics of coated surface of Ti/IrO2 anode were examined by FESEM and XRD. The coated anode was applied for electrochemical removal of organic pollutants from synthetic water samples in 100 mL compartment of batch electrochemical cell. About 50% COD removal was obtained at anode prepared with low Ir content solution while 72% COD removal was obtained with anode prepared at high Ir content. Maximum COD removal was obtained at 10 mA/cm2 current density.

Removal of dust particles from metal mirror surfaces by excimer laser radiation

DOE Office of Scientific and Technical Information (OSTI.GOV)

Mann, K.; Wolff-Rottke, B.; Mueller, F.

1995-12-31

The effect of particle desorption from Al mirror surfaces by the influence of pulsed UV laser radiation has been studied. The investigations are closely related to the demands of astronomers, who are looking for a more effective way of cleaning the Al coatings of future very large telescope (VLT) mirrors. A systematic parameter study has been performed in order to determine the irradiation conditions which yield the highest dust removal efficiency (i.e. reflectivity increase) on contaminated samples, taking particularly into account laser induced damage and degradation effects of coating and substrate. The particle removal rate increases with increasing laser fluence,more » being limited however by the damage threshold of the coating. Therefore, parameters influencing the damage threshold of metal coatings like wavelength, pulse width and number of pulses have been studied in detail. Data indicate that on Al coated BK7 and Zerodur samples KrF laser radiation yields the optimum result, with cleaning efficiencies comparable to polymer film stripping. The initial reflectivity of the clean coating can nearly be reinstalled, in particular when an additional solvent film on the sample surface is applied. Hence, laser desorption seems to be a viable method of cleaning large Al mirrors for telescopes.« less

Chemistry and Formation of the Beilby Layer During Polishing of Fused Silica Glass

DOE PAGES

Suratwala, Tayyab; Steele, William; Wong, Lana; ...

2015-05-19

The chemical characteristics and the proposed formation mechanisms of the modified surface layer (called the Beilby layer) on polished fused silica glasses are described. Fused silica glass samples were polished using different slurries, polyurethane pads, and at different rotation rates. The concentration profiles of several key contaminants, such as Ce, K, and H, were measured in the near surface layer of the polished samples using Secondary Ion Mass Spectroscopy (SIMS). The penetration of K, originating from KOH used for pH control during polishing, decreased with increase in polishing material removal rate. In contrast, penetration of the Ce and H increasedmore » with increase in polishing removal rate. In addition, Ce penetration was largely independent of the other polishing parameters (e.g., particle size distribution and the properties of the polishing pad). The resulting K concentration depth profiles are described using a two-step diffusion process: (1) steady-state moving boundary diffusion (due to material removal during polishing) followed by (2) simple diffusion during ambient postpolishing storage. Using known alkali metal diffusion coefficients in fused silica glass, this diffusion model predicts concentration profiles that are consistent with the measured data at various polishing material removal rates. On the other hand, the observed Ce profiles are inconsistent with diffusion based transport. Rather we propose that Ce penetration is governed by the ratio of Ce–O–Si and Si–O–Si hydrolysis rates; where this ratio increases with interface temperature (which increases with polishing material removal rate) resulting in greater Ce penetration into the Beilby layer. Calculated Ce surface concentrations using this mechanism are in good agreement to the observed change in measured Ce surface concentrations with polishing material removal rate. In conclusion, these new insights into the chemistry of the Beilby layer, combined together with details of the single particle removal function during polishing, are used to develop a more detailed and quantitative picture of the polishing process and the formation of the Beilby layer.« less

Flower-, wire-, and sheet-like MnO2-deposited diatomites: Highly efficient absorbents for the removal of Cr(VI).

PubMed

Du, Yucheng; Wang, Liping; Wang, Jinshu; Zheng, Guangwei; Wu, Junshu; Dai, Hongxing

2015-03-01

Flower-, wire-, and sheet-like MnO2-deposited diatomites have been prepared using a hydrothermal method with Mn(Ac)2, KMnO4 and/or MnSO4 as Mn source and diatomite as support. Physical properties of the materials were characterized by means of numerous analytical techniques, and their behaviors in the adsorption of chromium(VI) were evaluated. It is shown that the MnO2-deposited diatomite samples with different morphologies possessed high surface areas and abundant surface hydroxyl groups (especially the wire-like MnO2/diatomite sample). The wire-like MnO2/diatomite sample showed the best performance in the removal of Cr(VI), giving the maximum Cr(VI) adsorption capacity of 101 mg/g. Copyright © 2014. Published by Elsevier B.V.

Removal of bacterial fecal indicators, coliphages and enteric adenoviruses from waters with high fecal pollution by slow sand filtration.

PubMed

Bauer, Rosalie; Dizer, Halim; Graeber, Ingeborg; Rosenwinkel, Karl-Heinz; López-Pila, Juan M

2011-01-01

The aim of the present study was to estimate the performance of slow sand filtration (SSF) facilities, including the time needed for reaching stabilization (maturation), operated with surface water bearing high fecal contamination, representing realistic conditions of rivers in many emerging countries. Surface water spiked with wastewater was infiltrated at different pore water velocities (PWV) and samples were collected at different migration distances. The samples were analyzed for phages and to a lesser extent for fecal bacteria and enteric adenoviruses. At the PWV of 50 cm/d, at which somatic phages showed highest removal, their mean log(10) removal after 90 cm migration was 3.2. No substantial differences of removal rates were observed at PWVs between 100 and 900 cm/d (2.3 log(10) mean removal). The log(10) mean removal of somatic phages was less than the observed for fecal bacteria and tended more towards that of enteric adenoviruses This makes somatic phages a potentially better process indicator than Escherichia coli for the removal of viruses in SSF. We conclude that SSF, and by inference in larger scale river bank filtration (RBF), is an excellent option as a component in multi-barrier systems for drinking water treatment also in areas where the sources of raw water are considerably fecally polluted, as often found in many emerging countries. Copyright © 2010 Elsevier Ltd. All rights reserved.

Loss and replacement of small particles on the contact surfaces of footwear during successive exposures.

PubMed

Stoney, David A; Bowen, Andrew M; Stoney, Paul L

2016-12-01

On the contact surfaces of footwear loosely, moderately and strongly held particle fractions were separated and analyzed in an effort to detect different particle signals. Three environmental exposure sites were chosen to have different, characteristic particle types (soil minerals). Shoes of two types (work boots and tennis shoes) were tested, accumulating particles by walking 250m in each environment. Some shoes were exposed to only one environment; others were exposed to all three, in one of six different sequences. Sampling methods were developed to separate particles from the contact surface of the shoe based on how tightly they were held to the sole. Loosely held particles were removed by walking on paper, moderately held particles were removed by electrostatic lifting, and the most tightly held particles were removed by moist swabbing. The resulting numbers and types of particles were determined using forensic microscopy. Particle profiles from the different fractions were compared to test the ability to objectively distinguish the order of exposure to the three environments. Without exception, the samples resulting from differential sampling are dominated by the third site in the sequential footwear exposures. No noticeable differences are seen among the differential samplings of the loosely, moderately and strongly held particles: the same overwhelming presence of the third site is seen. It is clear from these results (1) that the third (final) exposure results in the nearly complete removal of any particles from prior exposures, and (2) that under the experimental conditions loosely, moderately and strongly held particles are affected similarly, without any detectable enrichment of the earlier exposures among the more tightly held particles. These findings have significant implications for casework, demonstrating that particles on the contact surfaces of footwear are rapidly lost and replaced. Copyright © 2016 Elsevier Ireland Ltd. All rights reserved.

Uranium mobility during interaction of rhyolitic obsidian, perlite and felsite with alkaline carbonate solution: T = 120° C, P = 210 kg/cm2

USGS Publications Warehouse

Zielinski, Robert A.

1979-01-01

Well-characterized samples of rhyolitic obsidian, perlite and felsite from a single lava flow are leached of U by alkaline oxidizing solutions under open-system conditions. Pressure, temperature, flow rate and solution composition are held constant in order to evaluate the relative importance of differences in surface area and crystallinity. Under the experimental conditions U removal from crushed glassy samples proceeds by a mechanism of glass dissolution in which U and silica are dissolved in approximately equal weight fractions. The rate of U removal from crushed glassy samples increases with decreasing average grain size (surface area). Initial rapid loss of a small component (≈ 2.5%) of the total U from crushed felsite. followed by much slower U loss, reflects variable rates of attack of numerous uranium sites. The fractions of U removed during the experiment ranged from 3.2% (felsite) to 27% (perlite). An empirical method for evaluating the relative rate of U loss from contemporaneous volcanic rocks is presented which incorporates leaching results and rock permeability data.

The synthetic evaluation of CuO-MnOx-modified pinecone biochar for simultaneous removal formaldehyde and elemental mercury from simulated flue gas.

PubMed

Yi, Yaoyao; Li, Caiting; Zhao, Lingkui; Du, Xueyu; Gao, Lei; Chen, Jiaqiang; Zhai, Yunbo; Zeng, Guangming

2018-02-01

A series of low-cost Cu-Mn-mixed oxides supported on biochar (CuMn/HBC) synthesized by an impregnation method were applied to study the simultaneous removal of formaldehyde (HCHO) and elemental mercury (Hg 0 ) at 100-300° C from simulated flue gas. The metal loading value, Cu/Mn molar ratio, flue gas components, reaction mechanism, and interrelationship between HCHO removal and Hg 0 removal were also investigated. Results suggested that 12%CuMn/HBC showed the highest removal efficiency of HCHO and Hg 0 at 175° C corresponding to 89%and 83%, respectively. The addition of NO and SO 2 exhibited inhibitive influence on HCHO removal. For the removal of Hg 0 , NO showed slightly positive influence and SO 2 had an inhibitive effect. Meanwhile, O 2 had positive impact on the removal of HCHO and Hg 0 . The samples were characterized by SEM, XRD, BET, XPS, ICP-AES, FTIR, and H 2 -TPR. The sample characterization illustrated that CuMn/HBC possessed the high pore volume and specific surface area. The chemisorbed oxygen (O β ) and the lattice oxygen (O α ) which took part in the removal reaction largely existed in CuMn/HBC. What is more, MnO 2 and CuO (or Cu 2 O) were highly dispersed on the CuMn/HBC surface. The strong synergistic effect between Cu-Mn mixed oxides was critical to the removal reaction of HCHO and Hg 0 via the redox equilibrium of Mn 4+ + Cu + ↔ Mn 3+ + Cu 2+ .

Unburnt carbon from coal fly ashes as a precursor of activated carbon for nitric oxide removal.

PubMed

Rubio, Begoña; Izquierdo, M Teresa; Mayoral, M Carmen; Bona, M Teresa; Andres, Jose M

2007-05-08

The aim of this work is to evaluate the characteristics of an activated carbon obtained from unburnt carbon in coal fly ashes to be used in the removal of NO. Carbon-rich fraction was obtained by mechanical sieving of fly ashes. The mineral matter was removed by conventional HCl and HF demineralization procedure. Activation was carried out with steam at 900 degrees C in order to develop porosity onto the sample. Characterization of samples was performed by several techniques with a main objective: to follow the mineral matter content, composition and distribution on the samples in order to better understand how to remove it from unburnt carbon in fly ashes. To study the use of this unburnt carbon as a precursor for the preparation of activated carbons for gas cleaning, the NO removal by ammonia using activated carbon as a catalyst at low temperature was performed. Results show a good performance of activated carbon in this reaction that is in relationship with BET surface area.

Surface reconstruction from scattered data through pruning of unstructured grids

NASA Technical Reports Server (NTRS)

Maksymiuk, C. M.; Merriam, M. L.

1991-01-01

This paper describes an algorithm for reconstructing a surface from a randomly digitized object. Scan data (treated as a cloud of points) is first tesselated out to its convex hull using Delaunay triangulation. The line-of-sight between each surface point and the scanning device is traversed, and any tetrahedra which are pierced by it are removed. The remaining tetrahedra form an approximate solid model of the scanned object. Due to the inherently limited resolution of any scan, this algorithm requires two additional procedures to produce a smooth, polyhedral surface: one process removes long, narrow tetrahedra which span indentations in the surface between digitized points; the other smooths sharp edges. The results for a moderately resolved sample body and a highly resolved aircraft are displayed.

Study on Electro-Polishing Process by Niobium-Plate Sample With Artificial Pits

DOE Office of Scientific and Technical Information (OSTI.GOV)

T. Saeki, H. Hayano, S. Kato, M. Nishiwaki, M. Sawabe, W.A. Clemens, R.L. Geng, R. Manus, P.V. Tyagi

2011-07-01

The Electro-polishing (EP) process is the best candidate of final surface-treatment for the production of ILC cavities. Nevertheless, the development of defects on the inner-surface of the Superconducting RF cavity during EP process has not been studied by experimental method. We made artificial pits on the surface of a Nb-plate sample and observed the development of the pit-shapes after each step of 30um-EP process where 120um was removed by EP in total. This article describes the results of this EP-test of Nb-sample with artificial pits.

A method for determining average damage depth of sawn crystalline silicon wafers

DOE Office of Scientific and Technical Information (OSTI.GOV)

Sopori, B.; Devayajanam, S.; Basnyat, P.

2016-04-01

The depth of surface damage (or simply, damage) in crystalline silicon wafers, caused by wire sawing of ingots, is determined by performing a series of minority carrier lifetime (MCLT) measurements. Samples are sequentially etched to remove thin layers from each surface and MCLT is measured after each etch step. The thickness-removed (..delta..t) at which the lifetime reaches a peak value corresponds to the damage depth. This technique also allows the damage to be quantified in terms of effective surface recombination velocity (Seff). To accomplish this, the MCLT data are converted into an Seff vs ..delta..t plot, which represents a quantitativemore » distribution of the degree of damage within the surface layer. We describe a wafer preparation procedure to attain reproducible etching and MCLT measurement results. We also describe important characteristics of an etchant used for controllably removing thin layers from the wafer surfaces. Some typical results showing changes in the MCLT vs ..delta..t plots for different cutting parameters are given.« less

Molecular-level removal of proteinaceous contamination from model surfaces and biomedical device materials by air plasma treatment.

PubMed

Banerjee, K K; Kumar, S; Bremmell, K E; Griesser, H J

2010-11-01

Established methods for cleaning and sterilising biomedical devices may achieve removal of bioburden only at the macroscopic level while leaving behind molecular levels of contamination (mainly proteinaceous). This is of particular concern if the residue might contain prions. We investigated at the molecular level the removal of model and real-life proteinaceous contamination from model and practical surfaces by air plasma (ionised air) treatment. The surface-sensitive technique of X-ray photoelectron spectroscopy (XPS) was used to assess the removal of proteinaceous contamination, with the nitrogen (N1s) photoelectron signal as its marker. Model proteinaceous contamination (bovine serum albumin) adsorbed on to a model surface (silicon wafer) and the residual proteinaceous contamination resulting from incubating surgical stainless steel (a practical biomaterial) in whole human blood exhibited strong N1s signals [16.8 and 18.5 atomic percent (at.%), respectively] after thorough washing. After 5min air plasma treatment, XPS detected no nitrogen on the sample surfaces, indicating complete removal of proteinaceous contamination, down to the estimated XPS detection limit 10ng/cm(2). Applying the same plasma treatment, the 7.7at.% nitrogen observed on a clinically cleaned dental bur was reduced to a level reflective of new, as-received burs. Contact angle measurements and atomic force microscopy also indicated complete molecular-level removal of the proteinaceous contamination upon air plasma treatment. This study demonstrates the effectiveness of air plasma treatment for removing proteinaceous contamination from both model and practical surfaces and offers a method for ensuring that no molecular residual contamination such as prions is transferred upon re-use of surgical and dental instruments. Crown Copyright © 2010. Published by Elsevier Ltd. All rights reserved.

Mesoporous carbon-supported Pd nanoparticles with high specific surface area for cyclohexene hydrogenation: Outstanding catalytic activity of NaOH-treated catalysts

NASA Astrophysics Data System (ADS)

Puskás, R.; Varga, T.; Grósz, A.; Sápi, A.; Oszkó, A.; Kukovecz, Á.; Kónya, Z.

2016-06-01

Extremely high specific surface area mesoporous carbon-supported Pd nanoparticle catalysts were prepared with both impregnation and polyol-based sol methods. The silica template used for the synthesis of mesoporous carbon was removed by both NaOH and HF etching. Pd/mesoporous carbon catalysts synthesized with the impregnation method has as high specific surface area as 2250 m2/g. In case of NaOH-etched impregnated samples, the turnover frequency of cyclohexene hydrogenation to cyclohexane at 313 K was obtained 14 molecules • site- 1 • s- 1. The specific surface area of HF-etched samples was higher compared to NaOH-etched samples. However, catalytic activity was 3-6 times higher on NaOH-etched samples compared to HF-etched samples, which can be attributed to the presence of sodium and surface hydroxylgroups of the catalysts etched with NaOH solution.

Speedy Acquisition of Surface-Contamination Samples

NASA Technical Reports Server (NTRS)

Puleo, J. R.; Kirschner, L. E.

1982-01-01

Biological contamination of large-area surfaces can be determined quickly, inexpensively, and accurately with the aid of a polyester bonded cloth. Cloth is highly effective in removing microbes from a surface and releasing them for biological assay. In releasing contaminants, polyester bonded cloth was found to be superior to other commercial cleanroom cloths, including spun-bound polyamid cloths and cellulose cloths.

Removal of the long-lived {sup 222}Rn daughters from steel and germanium surfaces

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wojcik, Marcin; Zuzel, Grzegorz; Majorovits, Bela

Removal of the long-lived {sup 222}Rn daughters ({sup 210}Pb, {sup 210}Bi and {sup 210}Po) from stainless steel and germanium surfaces was investigated. As cleaning technique etching was applied to samples in a form of discs exposed earlier to a strong radon source. Reduction of the {sup 210}Pb activity was tested using a HPGe spectrometer, for {sup 210}Bi a beta spectrometer and for {sup 210}Po an alpha spectrometer was used. According to the conducted measurements all the isotopes were removed very efficiently from germanium. Results obtained for stainless steel were worse but still better than those achieved for copper.

Groundwater monitoring system

DOEpatents

Ames, Kenneth R.; Doesburg, James M.; Eschbach, Eugene A.; Kelley, Roy C.; Myers, David A.

1987-01-01

A groundwater monitoring system includes a bore, a well casing within and spaced from the bore, and a pump within the casing. A water impermeable seal between the bore and the well casing prevents surface contamination from entering the pump. Above the ground surface is a removable operating means which is connected to the pump piston by a flexible cord. A protective casing extends above ground and has a removable cover. After a groundwater sample has been taken, the cord is disconnected from the operating means. The operating means is removed for taking away, the cord is placed within the protective casing, and the cover closed and locked. The system is thus protected from contamination, as well as from damage by accident or vandalism.

Effect of Er:YAG laser-activated irrigation solution on Enterococcus Faecalis biofilm in an ex-vivo root canal model.

PubMed

Sahar-Helft, Sharonit; Stabholtz, Adam; Moshonov, Joshua; Gutkin, Vitaly; Redenski, Idan; Steinberg, Doron

2013-07-01

Abstract Objective: The purpose of this study was to evaluate mineral content and surface morphology of root canals coated with Enterococcus faecalis biofilm after treatment with several endodontic irrigation solutions, with and without Er:YAG laser-activated irrigation (LAI). LAI has been introduced as a powerful method for root canal irrigation resulting in smear-layer removal from the root canal wall. Distal and palatal roots from 60 freshly extracted human molars were used in this study. The coronal of each tooth was removed. Roots were split longitudinally and placed in an ultrasonic bath to remove the smear layer, creating conditions for the formation of E. faecalis biofilm. After incubation, the two halves were reassembled in impression material to simulate clinical conditions. Specimens were divided into two main groups: roots rinsed with irrigation solutions and roots subjected to laser irradiation combined with irrigation solutions. Solutions tested were 2% chlorhexidine and 17% ethylenediaminetetraacetic acid (EDTA) and saline. Surface morphology: 17% EDTA irrigant solution combined with Er:YAG laser showed the best results for removing bacteria from the root canal walls. Chemical analysis: all samples treated with combined laser irradiation and irrigation solution had low surface levels of Ca compared with samples treated with irrigation alone. The Ca/P ratio was highest in the laser-EDTA group. Overall, mineral changes caused by laser with irrigation solutions were minimal, and statistically nonsignificant. In vitro irrigation solutions, combined with Er:YAG laser irradiation, were effective in removing E. faecalis biofilm from root canal walls. Irrigation solutions without laser irradiation were less effective, leaving a layer of biofilm on the dentin surface.

Low-cost adsorbent prepared from sewage sludge and corn stalk for the removal of COD in leachate.

PubMed

He, Ying; Liao, Xiaofeng; Liao, Li; Shu, Wei

2014-01-01

Sewage sludge (SS) with corn stalk (CS) was used to prepare SS-based activated carbon (SAC) by pyrolysis with ZnCl2. The effects of mixing ratio on surface area and pore size distribution, elemental composition, surface chemistry, and morphology were investigated. The results demonstrated that the addition of CS into SS samples improved the surface area (from 92 to 902 m(2)/g) and the microporosity (from 1.2 to 4.1%) of the adsorbents and, therefore, enhancing the adsorption performance. The removal of leachate chemical oxygen demand (COD) was also determined. It was found that the COD removal rate reached 85% at pH 4 with the SAC (90 wt% CS) dosage of 2% (g/mL) and an adsorption time of 40 min. The adsorption experimental data were fitted by both Langmuir and Freundlich adsorption isotherms. Long-chain alkanes and refractory organics were found in raw leachate, but could be removed by SAC largely.

Evaluation of the potentials of humic acid removal in water by gas phase surface discharge plasma.

PubMed

Wang, Tiecheng; Qu, Guangzhou; Ren, Jingyu; Yan, Qiuhe; Sun, Qiuhong; Liang, Dongli; Hu, Shibin

2016-02-01

Degradation of humic acid (HA), a predominant type of natural organic matter in ground water and surface waters, was conducted using a gas phase surface discharge plasma system. HA standard and two surface waters (Wetland, and Weihe River) were selected as the targets. The experimental results showed that about 90.9% of standard HA was smoothly removed within 40 min's discharge plasma treatment at discharge voltage 23.0 kV, and the removal process fitted the first-order kinetic model. Roles of some active species in HA removal were studied by evaluating the effects of solution pH and OH radical scavenger; and the results presented that O3 and OH radical played significant roles in HA removal. Scanning electron microscope (SEM) and FTIR analysis showed that HA surface topography and molecular structure were changed during discharge plasma process. The mineralization of HA was analyzed by UV-Vis spectrum, dissolved organic carbon (DOC), specific UV absorbance (SUVA), UV absorption ratios, and excitation-emission matrix (EEM) fluorescence. The formation of disinfection by-products during HA sample chlorination was also identified, and CHCl3 was detected as the main disinfection by-product, but discharge plasma treatment could suppress its formation to a certain extent. In addition, approximately 82.3% and 67.9% of UV254 were removed for the Weihe River water and the Wetland water after 40 min of discharge plasma treatment. Copyright © 2015 Elsevier Ltd. All rights reserved.

Mathematical estimation of the level of microbial contamination on spacecraft surfaces by volumetric air sampling

NASA Technical Reports Server (NTRS)

Oxborrow, G. S.; Roark, A. L.; Fields, N. D.; Puleo, J. R.

1974-01-01

Microbiological sampling methods presently used for enumeration of microorganisms on spacecraft surfaces require contact with easily damaged components. Estimation of viable particles on surfaces using air sampling methods in conjunction with a mathematical model would be desirable. Parameters necessary for the mathematical model are the effect of angled surfaces on viable particle collection and the number of viable cells per viable particle. Deposition of viable particles on angled surfaces closely followed a cosine function, and the number of viable cells per viable particle was consistent with a Poisson distribution. Other parameters considered by the mathematical model included deposition rate and fractional removal per unit time. A close nonlinear correlation between volumetric air sampling and airborne fallout on surfaces was established with all fallout data points falling within the 95% confidence limits as determined by the mathematical model.

Removing Contamination-Induced Reconstruction Artifacts from Cryo-electron Tomograms

PubMed Central

Fernandez, Jose-Jesus; Laugks, Ulrike; Schaffer, Miroslava; Bäuerlein, Felix J.B.; Khoshouei, Maryam; Baumeister, Wolfgang; Lucic, Vladan

2016-01-01

Imaging of fully hydrated, vitrified biological samples by electron tomography yields structural information about cellular protein complexes in situ. Here we present a computational procedure that removes artifacts of three-dimensional reconstruction caused by contamination present in samples during imaging by electron microscopy. Applying the procedure to phantom data and electron tomograms of cellular samples significantly improved the resolution and the interpretability of tomograms. Artifacts caused by surface contamination associated with thinning by focused ion beam, as well as those arising from gold fiducial markers and from common, lower contrast contamination, could be removed. Our procedure is widely applicable and is especially suited for applications that strive to reach a higher resolution and involve the use of recently developed, state-of-the-art instrumentation. PMID:26743046

Synthesis and Characterization of Mixed Iron-Manganese Oxide Nanoparticles and Their Application for Efficient Nickel Ion Removal from Aqueous Samples

PubMed Central

Serra, Antonio; Monteduro, Anna Grazia; Padmanabhan, Sanosh Kunjalukkal; Licciulli, Antonio; Bonfrate, Valentina; Salvatore, Luca; Calcagnile, Lucio

2017-01-01

Mixed iron-manganese oxide nanoparticles, synthesized by a simple procedure, were used to remove nickel ion from aqueous solutions. Nanostructures, prepared by using different weight percents of manganese, were characterized by transmission electron microscopy, selected area diffraction, X-ray diffraction, Raman spectroscopy, and vibrating sample magnetometry. Adsorption/desorption isotherm curves demonstrated that manganese inclusions enhance the specific surface area three times and the pores volume ten times. This feature was crucial to decontaminate both aqueous samples and food extracts from nickel ion. Efficient removal of Ni2+ was highlighted by the well-known dimethylglyoxime test and by ICP-MS analysis and the possibility of regenerating the nanostructure was obtained by a washing treatment in disodium ethylenediaminetetraacetate solution. PMID:28804670

Analysis of flow dynamics through small diameter gas sampling systems

NASA Technical Reports Server (NTRS)

Brown, K. G.

1984-01-01

The removal of gas material through a capillary opening in a surface is analyzed. The gas, from which the sample is removed, is moving past the surface at supersonic velocities. A variety of possible conditions of temperature, pressure and composition are discussed in an effort to emulate conditions that might be found at the surface of a vehicle traversing the altitude range 100-50 km, or might exist at the surface of a model in the stream of a high enthalpy wind tunnel. Aspects discussed include: (1) the throughput of the capillary for conditions of different lengths and different L/a (length/radius) ratios; (2) the total throughput when the surface in question contains many hundreds of these capillaries; (3) the effect of the capillaries upon the composition of the analyzed gas; (4) the effect of the capillary or capillaries upon the gas stream itself; and (5) the implications of the calculations upon the possible implementation of this type of device as an inlet for a mass spectrometer to be developed for analyzing the upper atmosphere.

The effect of root surface conditioning on smear layer removal in periodontal regeneration (a scanning electron microscopic study)

NASA Astrophysics Data System (ADS)

Fidyawati, D.; Soeroso, Y.; Masulili, S. L. C.

2017-08-01

The role of root surface conditioning treatment on smear layer removal of human teeth is affected by periodontitis in periodontal regeneration. The objective of this study is to analyze the smear layer on root surface conditioned with 2.1% minocycline HCl ointment (Periocline), and 24% EDTA gel (Prefgel). A total of 10 human teeth indicated for extraction due to chronic periodontitis were collected and root planed. The teeth were sectioned in thirds of the cervical area, providing 30 samples that were divided into three groups - minocycline ointment treatment, 24% EDTA gel treatment, and saline as a control. The samples were examined by scanning electron microscope. No significant differences in levels of smear layer were observed between the minocycline group and the EDTA group (p=0.759). However, there were significant differences in the level of smear layer after root surface treatment in the minocycline and EDTA groups, compared with the control group (p=0.00). There was a relationship between root surface conditioning treatment and smear layer levels following root planing.

Vacuum probe surface sampler

NASA Technical Reports Server (NTRS)

Zahlava, B. A. (Inventor)

1973-01-01

A vacuum probe surface sampler is described for rapidly sampling relatively large surface areas which possess relatively light loading densities of micro-organism, drug particles or the like. A vacuum head with a hollow handle connected to a suitable vacuum source is frictionally attached to a cone assembly terminating in a flared tip adapted to be passed over the surface to be sampled. A fine mesh screen carried by the vacuum head provides support for a membrane filter which collects the microorganisms or other particles. The head assembly is easily removed from the cone assembly without contacting the cone assembly with human hands.

Pigment identification in artwork using graphite furnace atomic absorption spectrometry.

PubMed

Goltz, D M; Coombs, J; Marion, C; Cloutis, E; Gibson, J; Attas, M; Choo-Smith, L-P; Collins, C

2004-06-17

The use of a sampling technique is described for the identification of metals from inorganic pigments in paint. The sampling technique involves gently contacting a cotton swab with the painted surface to physically remove a minute quantity ( approximately 1-2mug) of pigment. The amount of material removed from the painted surface is invisible to the unaided eye and does not cause any visible effect to the painted surface. The cotton swab was then placed in a 1.5ml polystyrene beaker containing HNO(3) to extract pigment metals prior to analysis using graphite furnace atomic absorption spectrometry (GFAAS). GFAAS is well suited for identifying pigment metals since it requires small samples and many pigments consist of main group elements (e.g. Al) as well as transition metals (e.g. Zn, Fe and Cd). Using Cd (cadmium red) as the test element, the reproducibility of sampling a paint surface with the cotton swab was approximately 13% in either a water or oil medium. To test the feasibility of cotton sampling for pigment identification, samples were obtained from paintings (watercolour and oil) of a local collection. Raman spectra provided complementary information to the GFAAS, which together are essential for positive identification of some pigments. For example, GFAAS indicated the presence of Cu, but the Raman spectra positively identified the modern copper pigment phthalocyanine green (Cu(C(32)Cl(16)N(8)). Both Raman spectroscopy and GFAAS were useful for identifying ZnO as a white pigment.

Paint removal from aluminum and composite substrate of aircraft by laser ablation using TEA CO2 lasers

NASA Astrophysics Data System (ADS)

Tsunemi, Akira; Endo, Akira; Ichishima, Daiji

1998-09-01

A high power TEA CO2 laser was applied to strip paints from the surface of aircraft. For our experimental samples, aluminum and fiber-reinforced composite substrate were painted as the completely same way as normal aircraft. As a result of delicate control of the irradiation parameters, the surfaces of not only aluminum substrate but also composite substrate were clearly exposed without any damages. Removed materials were found out to be effectively collected by a combination of a micro filter and activated carbon powder.

Detection of a wide variety of human and veterinary fluoroquinolone antibiotics in municipal wastewater and wastewater-impacted surface water.

PubMed

He, Ke; Soares, Ana Dulce; Adejumo, Hollie; McDiarmid, Melissa; Squibb, Katherine; Blaney, Lee

2015-03-15

As annual sales of antibiotics continue to rise, the mass of these specially-designed compounds entering municipal wastewater treatment systems has also increased. Of primary concern here is that antibiotics can inhibit growth of specific microorganisms in biological processes of wastewater treatment plants (WWTPs) or in downstream ecosystems. Growth inhibition studies with Escherichia coli demonstrated that solutions containing 1-10 μg/L of fluoroquinolones can inhibit microbial growth. Wastewater samples were collected on a monthly basis from various treatment stages of a 30 million gallon per day WWTP in Maryland, USA. Samples were analyzed for the presence of 11 fluoroquinolone antibiotics. At least one fluoroquinolone was detected in every sample. Ofloxacin and ciprofloxacin exhibited detection frequencies of 100% and 98%, respectively, across all sampling sites. Concentrations of fluoroquinolones in raw wastewater were as high as 1900 ng/L for ciprofloxacin and 600 ng/L for ofloxacin. Difloxacin, enrofloxacin, fleroxacin, moxifloxacin, norfloxacin, and orbifloxacin were also detected at appreciable concentrations of 9-170 ng/L. The total mass concentration of fluoroquinolones in raw wastewater was in the range that inhibited E. coli growth, suggesting that concerns over antibiotic presence in wastewater and wastewater-impacted surface water are valid. The average removal efficiency of fluoroquinolones during wastewater treatment was approximately 65%; furthermore, the removal efficiency for fluoroquinolones was found to be negatively correlated to biochemical oxygen demand removal and positively correlated to phosphorus removal. Copyright © 2014 Elsevier B.V. All rights reserved.

Mass removal by oxidation and sublimation of porous graphite during fiber laser irradiation

NASA Astrophysics Data System (ADS)

Phillips, Grady T.; Bauer, William A.; Fox, Charles D.; Gonzales, Ashley E.; Herr, Nicholas C.; Gosse, Ryan C.; Perram, Glen P.

2017-01-01

The various effects of laser heating of carbon materials are key to assessing laser weapon effectiveness. Porous graphite plates, cylinders, and cones with densities of 1.55 to 1.82 g/cm3 were irradiated by a 10-kW fiber laser at 0.075 to 3.525 kW/cm2 for 120 s to study mass removal and crater formation. Surface temperatures reached steady state values as high as 3767 K. The total decrease in sample mass ranged from 0.06 to 6.29 g, with crater volumes of 0.52 to 838 mm3, and penetration times for 12.7-mm-thick plates as short as 38 s. Minor contaminants in the graphite samples produced calcium and iron oxide to be redeposited on the graphite surface. Dramatic graphite crystalline structures are also produced at higher laser irradiances. Significantly increased porosity of the sample is observed even outside the laser-irradiated region. Total mass removed increases with deposited laser energy at a rate of 4.83 g/MJ for medium extruded graphite with an apparent threshold of 0.15 MJ. At ˜3.5 kW/cm2, the fractions of the mass removed from the cylindrical samples in the crater, surrounding trench, and outer region of decreased porosity are 38%, 47%, and 15%, respectively. Graphite is particularly resistant to damage by high power lasers. The new understanding of graphite combustion and sublimation during laser irradiation is vital to the more complex behavior of carbon composites.

Further contributions to the understanding of nitrogen removal in waste stabilization ponds.

PubMed

Bastos, R K X; Rios, E N; Sánchez, I A

2018-06-01

A set of experiments were conducted in Brazil in a pilot-scale waste stabilization pond (WSP) system (a four-maturation-pond series) treating an upflow anaerobic sludge blanket (UASB) reactor effluent. Over a year and a half the pond series was monitored under two flow rate conditions, hence also different hydraulic retention times and surface loading rates. On-site and laboratory trials were carried out to assess: (i) ammonia losses by volatilization using acrylic capture chambers placed at the surface of the ponds; (ii) organic nitrogen sedimentation rates using metal buckets placed at the bottom of the ponds for collecting settled particulate matter; (iii) nitrogen removal by algal uptake based on the nitrogen content of the suspended particulate matter in samples from the ponds' water column. In addition, nitrification and denitrification rates were measured in laboratory-based experiments using pond water and sediment samples. The pond system achieved high nitrogen removal (69% total nitrogen and 92% ammonia removal). The average total nitrogen removal rates varied from 10,098 to 3,849 g N/ha·d in the first and the last ponds, respectively, with the following fractions associated with the various removal pathways: (i) 23.5-45.6% sedimentation of organic nitrogen; (ii) 13.1-27.8% algal uptake; (iii) 1.2-3.1% ammonia volatilization; and (iv) 0.15-0.34% nitrification-denitrification.

Static and dynamic removal of aquatic natural organic matter by carbon nanotubes.

PubMed

Ajmani, Gaurav S; Cho, Hyun-Hee; Abbott Chalew, Talia E; Schwab, Kellogg J; Jacangelo, Joseph G; Huang, Haiou

2014-08-01

Carbon nanotubes (CNTs) were investigated for their capability and mechanisms to simultaneously remove colloidal natural organic matter (NOM) and humic substances from natural surface water. Static removal testing was conducted via adsorption experiments while dynamic removal was evaluated by layering CNTs onto substrate membranes and filtering natural water through the CNT-layered membranes. Analyses of treated water samples showed that removal of humic substances occurred via adsorption under both static and dynamic conditions. Removal of colloidal NOM occurred at a moderate level of 36-66% in static conditions, independent of the specific surface area (SSA) of CNTs. Dynamic removal of colloidal NOM increased from approximately 15% with the unmodified membrane to 80-100% with the CNT-modified membranes. Depth filtration played an important role in colloidal NOM removal. A comparison of the static and dynamic removal of humic substances showed that equilibrium static removal was higher than dynamic (p < 0.01), but there was also a significant linear relationship between static and dynamic removal (p < 0.05). Accounting for contact time of CNTs with NOM during filtration, it appeared that CNT mat structure was an important determinant of removal efficiencies for colloidal NOM and humic substances during CNT membrane filtration. Copyright © 2014 Elsevier Ltd. All rights reserved.

Capability of microalgae-based wastewater treatment systems to remove emerging organic contaminants: a pilot-scale study.

PubMed

Matamoros, Víctor; Gutiérrez, Raquel; Ferrer, Ivet; García, Joan; Bayona, Josep M

2015-05-15

The effect of hydraulic retention time (HRT) and seasonality on the removal efficiency of 26 organic microcontaminants from urban wastewater was studied in two pilot high-rate algal ponds (HRAPs). The targeted compounds included pharmaceuticals and personal care products, fire retardants, surfactants, anticorrosive agents, pesticides and plasticizers, among others. The pilot plant, which was fed at a surface loading rate of 7-29 g of COD m(-2)d(-1), consisted of a homogenisation tank and two parallel lines, each one with a primary settler and an HRAP with a surface area of 1.5 m(2) and a volume of 0.5 m(3). The two HRAPs were operated with different HRTs (4 and 8 d). The removal efficiency ranged from negligible removal to more than 90% depending on the compound. Microcontaminant removal efficiencies were enhanced during the warm season, while the HRT effect on microcontaminant removal was only noticeable in the cold season. Our results suggest that biodegradation and photodegradation are the most important removal pathways, whereas volatilization and sorption were solely achieved for hydrophobic compounds (log Kow>4) with a moderately high Henry's law constant values (11-12 Pa m(-3)mol(-1)) such as musk fragrances. Whereas acetaminophen, ibuprofen and oxybenzone presented ecotoxicological hazard quotients (HQs) higher than 1 in the influent wastewater samples, the HQs for the effluent water samples were always below 1. Copyright © 2015 Elsevier B.V. All rights reserved.

Paraffin wax removal from metal injection moulded cocrmo alloy compact by solvent debinding process

NASA Astrophysics Data System (ADS)

Dandang, N. A. N.; Harun, W. S. W.; Khalil, N. Z.; Ahmad, A. H.; Romlay, F. R. M.; Johari, N. A.

2017-10-01

One of the most crucial and time consuming phase in metal injection moulding (MIM) process is “debinding”. These days, in metal injection moulding process, they had recounted that first debinding practice was depend on thermal binder degradation, which demanding more than 200 hours for complete removal of binder. Fortunately, these days world had introduced multi-stage debinding techniques to simplified the debinding time process. This research study variables for solvent debinding which are temperature and soaking time for samples made by MIM CoCrMo powder. Since wax as the key principal in the binder origination, paraffin wax will be removed together with stearic acid from the green bodies. Then, debinding process is conducted at 50, 60 and 70°C for 30-240 minutes. It is carried out in n-heptane solution. Percentage weight loss of the binder were measured. Lastly, scanning electron microscope (SEM) analysis and visual inspection were observed for the surface of brown compact. From the results, samples debound at 70°C exhibited a significant amount of binder loss; nevertheless, sample collapse, brittle surface and cracks were detected. But, at 60°C temperature and time of 4 hours proven finest results as it shows sufficient binder loss, nonappearance of surface cracks and easy to handle. Overall, binder loss is directly related to solvent debinding temperature and time.

Survival of biofilm-forming Salmonella on stainless steel bolt threads under dry conditions.

PubMed

Morita, Yukio; Komoda, Emiko; Ono, Kazuaki; Kumagai, Susumu

2011-01-01

We examined the survival of two biofilm-forming strains and two biofilm-deficient strains of non typhoid Salmonella (NTS) on stainless steel bolt threads under dry conditions. Five µL of tryptone soya broth or egg yolke mulsion containing NTS strains at a concentration of 9 log cfu/mL was dropped onto the thread surfaces of hexagonal bolts. After inoculation, the bolts were screwed into the nuts, and then removed (Separate type) or not removed (Unit type). The two types of samples were kept in a dry environment (20.0-25.0°C, 2-15% humidity) and bacteria on the surfaces were periodically counted. Biofilm-forming strains were recovered from all samples after 336 days of incubation, but biofilm-deficient strains were isolated from only two of 8 samples after 336 days. This finding demonstrates that NTS can survive for approximately one year on bolt threads, providing direct evidence of the potential risk of constructions having crevices or uneven surfaces as possible contamination sources. The risk of cross-contamination may be higher for biofilm-forming strains than for biofilm-deficient strains.

Removal of bromide and iodide anions from drinking water by silver-activated carbon aerogels.

PubMed

Sánchez-Polo, M; Rivera-Utrilla, J; Salhi, E; von Gunten, U

2006-08-01

The aim of this study is to analyze the use of Ag-doped activated carbon aerogels for bromide and iodide removal from drinking water and to study how the activation of Ag-doped aerogels affects their behavior. It has been observed that the carbonization treatment and activation process of Ag-doped aerogels increased the surface area value ( [Formula: see text] ), whereas the volume of meso-(V(2)) and macropores (V(3)) decreased slightly. Chemical characterization of the materials revealed that carbonization and especially activation process considerably increased the surface basicity of the sample. Original sample (A) presented acidic surface properties (pH(PZC)=4.5) with 21% surface oxygen, whereas the sample that underwent activation showed mainly basic surface chemical properties (pH(PZC)=9.5) with only 6% of surface oxygen. Carbonization and especially, activation process considerable increased the adsorption capacity of bromide and iodide ions. This would mainly be produced by (i) an increase in the microporosity of the sample, which increases Ag-adsorption sites available to halide anions, and (ii) a rise of the basicity of the sample, which produces an increase in attractive electrostatic interactions between the aerogel surface, positively charged at the working pH (pH(solution)

The Influence of the Support Structure on Residual Stress and Distortion in SLM Inconel 718 Parts

NASA Astrophysics Data System (ADS)

Mishurova, Tatiana; Cabeza, Sandra; Thiede, Tobias; Nadammal, Naresh; Kromm, Arne; Klaus, Manuela; Genzel, Christoph; Haberland, Christoph; Bruno, Giovanni

2018-07-01

The effect of support structure and of removal from the base plate on the residual stress state in selective laser melted IN718 parts was studied by means of synchrotron X-ray diffraction. The residual stresses in subsurface region of two elongated prisms in as-built condition and after removal from the base plate were determined. One sample was directly built on a base plate and another one on a support structure. Also, the distortion on the top surface due to stress release was measured by contact profilometry. High tensile residual stress values were found, with pronounced stress gradient along the hatching direction. In the sample on support, stress redistribution took place after removal from the base plate, as opposed to simple stress relaxation for the sample without support. The sample on support structure showed larger distortion compared to sample without support. We conclude that the use of a support decreases stress values but stress-relieving heat treatments are still needed.

The Influence of the Support Structure on Residual Stress and Distortion in SLM Inconel 718 Parts

NASA Astrophysics Data System (ADS)

Mishurova, Tatiana; Cabeza, Sandra; Thiede, Tobias; Nadammal, Naresh; Kromm, Arne; Klaus, Manuela; Genzel, Christoph; Haberland, Christoph; Bruno, Giovanni

2018-05-01

The effect of support structure and of removal from the base plate on the residual stress state in selective laser melted IN718 parts was studied by means of synchrotron X-ray diffraction. The residual stresses in subsurface region of two elongated prisms in as-built condition and after removal from the base plate were determined. One sample was directly built on a base plate and another one on a support structure. Also, the distortion on the top surface due to stress release was measured by contact profilometry. High tensile residual stress values were found, with pronounced stress gradient along the hatching direction. In the sample on support, stress redistribution took place after removal from the base plate, as opposed to simple stress relaxation for the sample without support. The sample on support structure showed larger distortion compared to sample without support. We conclude that the use of a support decreases stress values but stress-relieving heat treatments are still needed.

Understanding how surface chemistry and topography enhance fog harvesting based on the superwetting surface with patterned hemispherical bulges.

PubMed

Zhong, Lieshuang; Zhu, Hai; Wu, Yang; Guo, Zhiguang

2018-09-01

The Namib Desert beetle-Stenocara can adapt to the arid environment by its fog harvesting ability. A series of samples with different topography and wettability that mimicked the elytra of the beetle were fabricated to study the effect of these factors on fog harvesting. The superhydrophobic bulgy sample harvested 1.5 times the amount of water than the sample with combinational pattern of hydrophilic bulgy/superhydrophobic surrounding and 2.83 times than the superhydrophobic surface without bulge. These bulges focused the droplets around them which endowed droplets with higher velocity and induced the highest dynamic pressure atop them. Superhydrophobicity was beneficial for the departure of harvested water on the surface of sample. The bulgy topography, together with surface wettability, dominated the process of water supply and water removal. Copyright © 2018 Elsevier Inc. All rights reserved.

Surface Cleaning Techniques: Ultra-Trace ICP-MS Sample Preparation and Assay of HDPE

DOE Office of Scientific and Technical Information (OSTI.GOV)

Overman, Nicole R.; Hoppe, Eric W.; Addleman, Raymond S.

2013-06-01

The world’s most sensitive radiation detection and assay systems depend upon ultra-low background (ULB) materials to reduce unwanted radiological backgrounds. Herein, we evaluate methods to clean HDPE, a material of interest to ULB systems and the means to provide rapid assay of surface and bulk contamination. ULB level material and ultra-trace level detection of actinide elements is difficult to attain, due to the introduction of contamination from sample preparation equipment such as pipette tips, sample vials, forceps, etc. and airborne particulate. To date, literature available on the cleaning of such polymeric materials and equipment for ULB applications and ultra-trace analysesmore » is limited. For these reasons, a study has been performed to identify an effective way to remove surface contamination from polymers in an effort to provide improved instrumental detection limits. Inductively Coupled Plasma Mass Spectroscopy (ICP-MS) was utilized to assess the effectiveness of a variety of leachate solutions for removal of inorganic uranium and thorium surface contamination from polymers, specifically high density polyethylene (HDPE). HDPE leaching procedures were tested to optimize contaminant removal of thorium and uranium. Calibration curves for thorium and uranium ranged from 15 ppq (fg/mL) to 1 ppt (pg/mL). Detection limits were calculated at 6 ppq for uranium and 7 ppq for thorium. Results showed the most effective leaching reagent to be clean 6 M nitric acid for 72 hour exposures. Contamination levels for uranium and thorium found in the leachate solutions were significant for ultralow level radiation detection applications.« less

Quantification of Staphylococcus aureus adhesion to equine bone surfaces passivated with Plasmalyte and hyperimmune plasma.

PubMed

Bauer, Sandra M; Santschi, Elizabeth M; Fialkowski, James; Clayton, Murray K; Proctor, Richard A

2004-01-01

To quantify the adhesion of Staphylococcus aureus to 4 equine bone surfaces passivated in a balanced polyionic solution (Plasmalyte) or hyperimmune equine plasma (Polymune plasma). In vitro comparative study. Third metacarpal bone (MC3) surface explants from 9 equine cadavers. Approximately 1 cm(2) sections of periosteum were removed from MC3 and stapled to sterile stainless steel screens. Three bone surface explants were cut using a surgical saw to present 1 cm(2) surfaces of subperiosteal bone, cut cortical bone, or endosteum. Duplicate explants of each surface were immersed for 1 hour in Plasmalyte or hyperimmune equine plasma. Each explant was then placed in a well of a 6-well sterile tissue culture plate with the surface of interest exposed. Each surface was inoculated with approximately 100 colony-forming units of S. aureus in 10 microL of Mueller Hinton broth and incubated for 6 hours at 37 degrees C. After gentle rinsing to remove non-adherent bacteria, samples were sonicated for 5 minutes at 60 kHz to loosen adhered bacteria. The number of adherent bacteria was determined by serial dilutions and incubation of the sonicate. Scanning electron microscopy (SEM) was performed on samples identically treated from an additional horse to confirm bacterial removal by sonication from all surfaces and support quantitative culture results. Less S. aureus adhered to periosteum than to cortical bone, cut cortical bone, and endosteal surfaces, which were all similar. Exposure of all surfaces to hyperimmune plasma reduced S. aureus adherence compared with Plasmalyte exposure; SEM supported these conclusions. Less bacteria adhere to periosteum than other bone surfaces. Hyperimmune plasma reduces bacterial adhesion to all bone tissue surfaces. Understanding the factors that affect bacterial adhesion to bone will facilitate development of improved intraoperative lavage solutions to reduce the morbidity and mortality associated with postoperative infection.

Chemically modified maize cobs waste with enhanced adsorption properties upon methyl orange and arsenic.

PubMed

Elizalde-González, María P; Mattusch, J; Wennrich, R

2008-07-01

The surface chemistry of maize naturasorbent was altered in this work by the modifying agents: phosphoric acid and different amines (triethanolamine, diethylenetriamine and 1,4-diaminobutane). Removal of methyl orange (25 mg l(-1)) was <50% by maize corn cobs modified by phosphorylation and higher by the quaternized samples: 68% with the 1,4-diaminobutane and 73% with the diethylenetriamine modificators. Adsorption of arsenite by the samples modified with phosphoric acid/ammonia was 11 microg g(-1), which corresponds to 98% removal from a 550 microg As l(-1) solution for an adsorbent dose of 50 mg ml(-1). The samples modified by phosphoric acid/urea removed 0.4 microg g(-1) arsenate from a 300 mug As l(-1) solution. Adsorption of methyl orange, arsenite and arsenate was superior by the chemically modified maize cobs judged against the initial naturasorbent. For comparison, removal by the commercial anion exchanger was 100% for methyl orange, 45% (5 microg g(-1)) for arsenite and 99% (5 microg g(-1)) for arsenate.

The effects of moderate coal cleaning on the microbial removal of organic sulfur. [Quarterly] technical report, December 1, 1991--February 29, 1992

DOE Office of Scientific and Technical Information (OSTI.GOV)

Srivastava, V.J.

The purpose of this project is to investigate the possibilities of developing an integrated physical/chemical/microbial process for the pre-combustion removal of sulfur from coal. Microorganisms are capable of specifically cleaving carbon-sulfur bonds and removing substantial amounts of organic sulfur from coal; however, the removal of organic sulfur form coal by microorganisms is hampered by the fact that, as a solid substrate, it is difficult to bring microorganisms in contact with the entirety of a coal sample. This study will examine the suitability of physically/chemically treated coal samples for subsequent biodesulfurization. During the current quarter, chemical comminution and combined chemical treatment/explosivemore » comminution experiments have been performed to generate coal samples with increased surface area and porosity. Ammonia vapor was found to be the most effective chemical comminution agent and the optimum conditions for combined chemical treatment/explosive comminution have not yet been determined.« less

A pitfall of muting and removing bad traces in surface-wave analysis

NASA Astrophysics Data System (ADS)

Hu, Yue; Xia, Jianghai; Mi, Binbin; Cheng, Feng; Shen, Chao

2018-06-01

Multi-channel analysis of surface/Love wave (MASW/MALW) has been widely used to construct the shallow shear (S)-wave velocity profile. The key step in surface-wave analysis is to generate accurate dispersion energy and pick the dispersive curves for inversion along the peaks of dispersion energy at different frequencies. In near-surface surface-wave acquisition, bad traces are very common and inevitable due to the imperfections in the recording instruments or others. The existence of bad traces will cause some artifacts in the dispersion energy image. To avoid the interference of bad traces on the surface-wave analysis, the bad traces should be alternatively muted (zeroed) or removed (deleted) from the raw surface-wave data before dispersion measurement. Most geophysicists and civil engineers, however, are not aware of the differences and implications between muting and removing of bad traces in surface-wave analysis. A synthetic test and a real-world example demonstrate the potential pitfalls of applying muting and removing on bad traces when using different dispersion-imaging methods. We implement muting and removing on bad traces respectively before dispersion measurement, and compare the influence of the two operations on three dispersion-imaging methods, high-resolution linear Radon transform (HRLRT), f-k transformation, and phase shift method. Results indicate that when using the HRLRT to generate the dispersive energy, muting bad traces will cause an even more complicated and discontinuous dispersive energy. When f-k transformation is utilized to conduct dispersive analysis, bad traces should be muted instead of removed to generate an accurate dispersion image to avoid the uneven sampling problem in the Fourier transform. As for the phase shift method, the difference between the two operations is slight, but we suggest that removal should be chosen because the integral for the phase-shift operator of the zeroed traces would bring in the sloped aliasing. This study provides a pre-process guidance for the real-world surface-wave data processing when the recorded shot gather contains inevitable bad traces.

Microbiota in experimental periodontitis and peri-implantitis in dogs.

PubMed

Charalampakis, Georgios; Abrahamsson, Ingemar; Carcuac, Olivier; Dahlén, Gunnar; Berglundh, Tord

2014-09-01

To analyze the microbial profile around teeth and implants following ligature removal in experimental periodontitis and peri-implantitis in dogs. Four implants with similar geometry and with two different surface characteristics (implant A: turned/implant B: TiUnite; NobelBiocare AB) were placed pairwise in the right side of the mandible 3 months after tooth extraction in five dogs. Experimental periodontitis and peri-implantitis were initiated 3 months later by ligature placement around implants and mandibular premolars and plaque formation. The ligatures were removed after 10 weeks. Microbial samples were obtained using paper points immediately after ligature removal, at 10 and 25 weeks after ligature removal. The microbiological analysis was performed by "checkerboard" DNA-DNA hybridization, including a panel of 16 bacterial species. The amount of bone loss that occurred during the period following ligature removal was significantly larger at implants with a modified surface than at implants with a turned surface and at teeth. The microbiological analysis revealed that the total bacterial load increased during the period following ligature removal and established an anaerobic Gram-negative microflora. It is suggested that the large variation in regard to the microbial profiles makes interpretation of a correlation between disease progression and microbial profiles difficult. © 2013 John Wiley & Sons A/S. Published by John Wiley & Sons Ltd.

Investigation of HCl-based surface treatment for GaN devices

DOE Office of Scientific and Technical Information (OSTI.GOV)

Okada, Hiroshi, E-mail: okada@ee.tut.ac.jp; Department of Electrical and Electronic Information Engineering, Toyohashi University of Technology, 1-1 Hibarigaoka, Tempaku-cho, Toyohashi 441-8580; Shinohara, Masatohi

2016-02-01

Surface treatments of GaN in HCl-based solutions are studied by X-ray photoelectron spectroscopy (XPS) and electrical characterization of fabricated GaN surfaces. A dilute-HCl treatment (HCl:H{sub 2}O=1:1) at room temperature and a boiled-HCl treatment (undiluted HCl) at 108°C are made on high-temperature annealed n-GaN. From the XPS study, removal of surface oxide by the dilute-HCl treatment was found, and more thoroughly oxide-removal was confirmed in the boiled-HCl treatment. Effect of the surface treatment on electrical characteristics on AlGaN/GaN transistor is also studied by applying treatment processes prior to the surface SiN deposition. Increase of drain current is found in boiled-HCl treatedmore » samples. The results suggest that the boiled-HCl treatment is effective for GaN device fabrication.« less

Nanoconfinement platform for nanostructure quantification via grazing-transmission X-ray scattering

DOEpatents

Black, Charles T.; Yager, Kevin G.

2017-01-31

A nano-confinement platform that may allow improved quantification of the structural order of nanometer-scale systems. Sample-holder `chips` are designed for the GTSAXS experimental geometry. The platform involves fabricated nanostructured sample holders on and in one or more corners of a substrate support where the sample material of interest is positioned at the corner of the substrate support. In an embodiment, the substrate material making up the substrate support beneath the sample-holding area is removed. A scattering x-ray sample platform includes a substrate support arranged in a parallelepiped form, having a substantially flat base and a substantially flat top surface, the top surface being substantially parallel with the base, the parallelepiped having a plurality of corners. At least one corner of the substrate support has a sample holding area formed in the top surface of the substrate support and within a predetermined distance from the corner. The sample holding area includes a regular array of nano-wells formed in the top surface of the substrate support.

Preparation of Magnetic Sorbent with Surface Modified by C18for Removal of Selected Organic Pollutants from Aqueous Samples

NASA Astrophysics Data System (ADS)

Kuráň, Pavel; Pilnaj, Dominik; Ciencialová, Lucie; Pšenička, Martin

2017-12-01

Magnetic sorbents have great potential in environmental applications due to their simple synthesis and separation in magnetic field, usability in heterogeneous systems and low toxicity. Possible syntheses, surface modifications and characteristics were described by Li et al 2013. This type of solid-phase extraction is being successfully used in various fields as health care, microbiology, biotechnologies or sample preconcentration in analytical chemistry. In this preliminary study we report on the preparation and application of magnetically separable sorbent with surface modified by C18 alkyl chain for purification of water contaminated by environmentally hazardous organic compounds. Magnetic cores were co-precipitated from Fe2+ and Fe3+ chlorides in alkalic aqueous solution. Surface of synthetized Fe3O4 was modified with SiO2 by tetraethylorthosilicate to assure physico-chemical stability. Furthermore, Fe3O4/SiO2 complex has been treated by C18 functional group, which provides good affinity towards hydrophobic substances in water. Efficiency of sorption under various conditions has been examined on benzene, toluene, ethylbenzene and xylenes (BTEX), compounds found in petroleum products which contaminate air, soil and groundwater near of store tanks. Sorption kinetics was followed by gas chromatography with mass spectrometry. The preliminary sorption kinetics data and efficiency of BTEX removal point at the possible application of prepared magnetic sorbent for BTEX removal, especially for ethylbenzene and xylenes.

Revisiting Mn and Fe removal in humic rich estuaries

NASA Astrophysics Data System (ADS)

Oldham, Véronique E.; Miller, Megan T.; Jensen, Laramie T.; Luther, George W.

2017-07-01

Metal removal by estuarine mixing has been studied for several decades, but few studies emphasize dissolved metal speciation and organic ligand complexation. Findings from the last decade indicate that metal-humic complexation can be significant for dissolved metals including Cu(II), Al(III) and Fe(III), but little consideration is given to the precipitation of these complexes with humic material at pH < 2. Given that total soluble metal analysis involves an acidification step for sample preservation, we show that Mn and other metal concentrations may have been underestimated in estuaries, especially when humic substance concentrations are high. A competitive ligand assay of selected samples from our study site, a coastal waterway bordered by wetlands (Broadkill River, DE), showed that Mn(III)-humic complexation is significant, and that some Mn(III)-L complexes precipitate during acidification. In the oxygenated surface waters of the Broadkill River, total dissolved Mn (dMnT) was up to 100% complexed to ambient ligands as Mn(III)-L, and we present evidence for humic-type Mn(III)-L complexes. The Mn(III) complexes were kinetically stabilized against Fe(II) reduction, even when [Fe(II)] was 17 times higher than [dMnT]. Unlike typical oceanic surface waters, [Fe(II)] > [Fe(III)-L] in surface waters, which may be attributed to high rates of photoreduction of Fe(III)-L complexes. Total [Mn(III)-L] ranged from 0.22 to 8.4 μM, in excess of solid MnOx (below 0.28 μM in all samples). Filtration of samples through 0.02 μm filters indicated that all Mn(III)-L complexes pass through the filters and were not colloidal species in contrast to dissolved Fe. Incubation experiments indicated that the reductive dissolution of solid MnOx by ambient ligands may be responsible for Mn(III) formation in this system. Unlike previous studies of estuarine mixing, which demonstrated metal removal during mixing, we show significant export of dMn and dissolved Fe (dFe) in the summer and fall of 2015. Thus, we propose that estuarine removal should be considered seasonal for dMn and dFe, with export in the summer and fall and removal during the winter.

Atomic Oxygen Treatment Technique for Removal of Smoke Damage from Paintings

NASA Technical Reports Server (NTRS)

Rutledge, S. K.; Banks, B. A.

1997-01-01

Soot deposits that can accumulate on surfaces of a painting during a fire can be difficult to clean from some types of paintings without damaging the underlying paint layers. A non-contact technique has been developed which can remove the soot by allowing a gas containing atomic oxygen to flow over the surface and chemically react with the soot to form carbon monoxide and carbon dioxide. The reaction is limited to the surface, so the underlying paint is not touched. The process can be controlled so that the cleaning can be stopped once the paint surface is reached. This paper describes the smoke exposure and cleaning of untreated canvas, acrylic gesso, and sections of an oil painting using this technique. The samples were characterized by optical microscopy and reflectance spectroscopy.

Surface microroughness of ion-beam etched optical surfaces

DOE Office of Scientific and Technical Information (OSTI.GOV)

Savvides, N.

2005-03-01

Ion-beam etching (IBE) and ion-beam figuring techniques using low-energy ion-beam sources have been applied for more than ten years in the fabrication and finishing of extremely smooth high-performance optics. We used optical interferometric techniques and atomic force microscopy to study the evolution of the surface root-mean-square (rms) microroughness, Rq, as a function of depth of a material removed (0-3000 nm) by a broad ion-beam source (Ar{sup +} ions of energy 600 eV and ion current density of 1 mA cm{sup -2}). Highly polished samples of fused silica and Zerodur (Rq{approx}3.5 A) showed a small decrease in microroughness (to 2.5 A)more » after 3000-nm IBE removal while an ultrapolished single-crystal sapphire sample (Rq{approx}1 A rms) retained its very low microroughness during IBE. Power spectral density functions over the spatial frequency interval of measurement (f=5x10{sup -3}-25 {mu}m{sup -1}) indicate that the IBE surfaces have minimal subsurface damage and low optical scatter.« less

Extraction of Thermal Performance Values from Samples in the Lunar Dust Adhesion Bell Jar

NASA Technical Reports Server (NTRS)

Gaier, James R.; Siamidis, John; Larkin, Elizabeth M. G.

2008-01-01

A simulation chamber has been developed to test the performance of thermal control surfaces under dusty lunar conditions. The lunar dust adhesion bell jar (LDAB) is a diffusion pumped vacuum chamber (10(exp -8) Torr) built to test material samples less than about 7 cm in diameter. The LDAB has the following lunar dust simulant processing capabilities: heating and cooling while stirring in order to degas and remove adsorbed water; RF air-plasma for activating the dust and for organic contaminant removal; RF H/He-plasma to simulate solar wind; dust sieving system for controlling particle sizes; and a controlled means of introducing the activated dust to the samples under study. The LDAB is also fitted with an in situ Xe arc lamp solar simulator, and a cold box that can reach 30 K. Samples of thermal control surfaces (2.5 cm diameter) are introduced into the chamber for calorimetric evaluation using thermocouple instrumentation. The object of this paper is to present a thermal model of the samples under test conditions and to outline the procedure to extract the absorptance, emittance, and thermal efficiency from the pristine and sub-monolayer dust covered samples.

Extraction of Thermal Performance Values from Samples in the Lunar Dust Adhesion Bell Jar

NASA Technical Reports Server (NTRS)

Gaier, James R.; Siamidis, John; Larkin, Elizabeth M.G.

2008-01-01

A simulation chamber has been developed to test the performance of thermal control surfaces under dusty lunar conditions. The lunar dust adhesion bell jar (LDAB) is a diffusion pumped vacuum chamber (10-8 Torr) built to test material samples less than about 7 cm in diameter. The LDAB has the following lunar dust stimulant processing capabilities: heating and cooling while stirring in order to degas and remove absorbed water; RF air-plasma for activating the dust and for organic contaminant removal; RF H/He-plasma to simulate solar wind; dust sieving system for controlling particle sizes; and a controlled means of introducing the activated dust to the samples under study. The LDAB is also fitted with an in situ Xe arc lamp solar simulator, and a cold box that can reach 30 K. Samples of thermal control surfaces (2.5 cm diameter) are introduced into the chamber for calorimetric evaluation using thermocouple instrumentation. The object of this paper is to present a thermal model of the samples under test conditions, and to outline the procedure to extract the absorptance, emittance, and thermal efficiency from the pristine and sub-monolayer dust covered samples

Extraction of Thermal Performance Values from Samples in the Lunar Dust Adhesion Bell Jar

NASA Technical Reports Server (NTRS)

Gaier, James R.; Siamidis, John; Larkin, Elizabeth M. G.

2010-01-01

A simulation chamber has been developed to test the performance of thermal control surfaces under dusty lunar conditions. The lunar dust adhesion bell jar (LDAB) is a diffusion pumped vacuum chamber (10(exp -8) Torr) built to test material samples less than about 7 cm in diameter. The LDAB has the following lunar dust simulant processing capabilities: heating and cooling while stirring in order to degas and remove adsorbed water; RF air-plasma for activating the dust and for organic contaminant removal; RF H/He-plasma to simulate solar wind; dust sieving system for controlling particle sizes; and a controlled means of introducing the activated dust to the samples under study. The LDAB is also fitted with an in situ Xe arc lamp solar simulator, and a cold box that can reach 30 K. Samples of thermal control surfaces (2.5 cm diameter) are introduced into the chamber for calorimetric evaluation using thermocouple instrumentation. The object of this paper is to present a thermal model of the samples under test conditions and to outline the procedure to extract the absorptance, emittance, and thermal efficiency from the pristine and sub-monolayer dust covered samples.

Correlating Cleaning Thoroughness with Effectiveness and Briefly Intervening to Affect Cleaning Outcomes: How Clean Is Cleaned?

PubMed Central

Hosford, Eve; Ong, Ana; Richesson, Douglas; Fraser, Susan; Kwak, Yoon; Miller, Sonia; Julius, Michael; McGann, Patrick; Lesho, Emil

2016-01-01

Objectives The most efficient approach to monitoring and improving cleaning outcomes remains unresolved. We sought to extend the findings of a previous study by determining whether cleaning thoroughness (dye removal) correlates with cleaning efficacy (absence of molecular or cultivable biomaterial) and whether one brief educational intervention improves cleaning outcomes. Design Before-after trial. Setting Newly built community hospital. Intervention 90 minute training refresher with surface-specific performance results. Methods Dye removal, measured by fluorescence, and biomaterial removal and acquisition, measured with culture and culture-independent PCR-based assays, were clandestinely assessed for eight consecutive months. At this midpoint, results were presented to the cleaning staff (intervention) and assessments continued for another eight consecutive months. Results 1273 surfaces were sampled before and after terminal room cleaning. In the short-term, dye removal increased from 40.3% to 50.0% (not significant). For the entire study period, dye removal also improved but not significantly. After the intervention, the number of rooms testing positive for specific pathogenic species by culturing decreased from 55.6% to 36.6% (not significant), and those testing positive by PCR fell from 80.6% to 53.7% (P = 0.016). For nonspecific biomaterial on surfaces: a) removal of cultivable Gram-negatives (GN) trended toward improvement (P = 0.056); b) removal of any cultivable growth was unchanged but acquisition (detection of biomaterial on post-cleaned surfaces that were contaminant-free before cleaning) worsened (P = 0.017); c) removal of PCR-based detection of bacterial DNA improved (P = 0.046), but acquisition worsened (P = 0.003); d) cleaning thoroughness and efficacy were not correlated. Conclusion At this facility, a minor intervention or minimally more aggressive cleaning may reduce pathogen-specific contamination, but not without unintended consequences. PMID:27196635

Correlating Cleaning Thoroughness with Effectiveness and Briefly Intervening to Affect Cleaning Outcomes: How Clean Is Cleaned?

PubMed

Clifford, Robert; Sparks, Michael; Hosford, Eve; Ong, Ana; Richesson, Douglas; Fraser, Susan; Kwak, Yoon; Miller, Sonia; Julius, Michael; McGann, Patrick; Lesho, Emil

2016-01-01

The most efficient approach to monitoring and improving cleaning outcomes remains unresolved. We sought to extend the findings of a previous study by determining whether cleaning thoroughness (dye removal) correlates with cleaning efficacy (absence of molecular or cultivable biomaterial) and whether one brief educational intervention improves cleaning outcomes. Before-after trial. Newly built community hospital. 90 minute training refresher with surface-specific performance results. Dye removal, measured by fluorescence, and biomaterial removal and acquisition, measured with culture and culture-independent PCR-based assays, were clandestinely assessed for eight consecutive months. At this midpoint, results were presented to the cleaning staff (intervention) and assessments continued for another eight consecutive months. 1273 surfaces were sampled before and after terminal room cleaning. In the short-term, dye removal increased from 40.3% to 50.0% (not significant). For the entire study period, dye removal also improved but not significantly. After the intervention, the number of rooms testing positive for specific pathogenic species by culturing decreased from 55.6% to 36.6% (not significant), and those testing positive by PCR fell from 80.6% to 53.7% (P = 0.016). For nonspecific biomaterial on surfaces: a) removal of cultivable Gram-negatives (GN) trended toward improvement (P = 0.056); b) removal of any cultivable growth was unchanged but acquisition (detection of biomaterial on post-cleaned surfaces that were contaminant-free before cleaning) worsened (P = 0.017); c) removal of PCR-based detection of bacterial DNA improved (P = 0.046), but acquisition worsened (P = 0.003); d) cleaning thoroughness and efficacy were not correlated. At this facility, a minor intervention or minimally more aggressive cleaning may reduce pathogen-specific contamination, but not without unintended consequences.

RF plasma cleaning of silicon substrates with high-density polyethylene contamination

NASA Astrophysics Data System (ADS)

Cagomoc, Charisse Marie D.; De Leon, Mark Jeffry D.; Ebuen, Anna Sophia M.; Gilos, Marlo Nicole R.; Vasquez, Magdaleno R., Jr.

2018-01-01

Upon contact with a polymeric material, microparticles from the polymer may adhere to a silicon (Si) substrate during device processing. The adhesion contaminates the surface and, in turn, leads to defects in the fabricated Si-based microelectronic devices. In this study, Si substrates with artificially induced high-density polyethylene (HDPE) contamination was exposed to 13.56 MHz radio frequency (RF) plasma utilizing argon and oxygen gas admixtures at a power density of 5.6 W/cm2 and a working pressure of 110 Pa for up to 6 min of treatment. Optical microscopy studies revealed the removal of up to 74% of the polymer contamination upon plasma exposure. Surface free energy (SFE) increased owing to the removal of contaminants as well as the formation of polar groups on the Si surface after plasma treatment. Atomic force microscopy scans showed a decrease in surface roughness from 12.25 nm for contaminated samples to 0.77 nm after plasma cleaning. The smoothening effect can be attributed to the removal of HDPE particles from the surface. In addition, scanning electron microscope images showed that there was a decrease in the amount of HDPE contaminants adhering onto the surface after plasma exposure.

Suspect screening and target quantification of human pharmaceutical residues in the surface water of Wuhan, China, using UHPLC-Q-Orbitrap HRMS.

PubMed

Asghar, Muhammad Ali; Zhu, Qingxin; Sun, Shutang; Peng, Yue'e; Shuai, Qin

2018-04-20

In this study we developed a systematic method for suspect screening and target quantification of the human pharmaceutical residues in water, via solid phase extraction (SPE) followed by liquid chromatography-high resolution mass spectrometry (LC-HRMS). We then proceeded to study the occurrences and distribution of the pharmaceuticals in the surface waters of Wuhan, China, by analyzing water samples from lakes, rivers and municipal sewage. Initially, 33 human pharmaceuticals were identified from East Lake without using purchasing standards. Of these, 29 were later confirmed by using standards, and quantified using the aforementioned SPE pretreatment method and LC-HRMS analysis in full MS scan mode. The 29 compounds included 8 antibiotics, 9 metabolites, and 12 miscellaneous pharmaceuticals. The highest proportions of pharmaceutical residues were detected downstream of the Yangtze River and in the lakes close to the central city. Metformin, cotinine, and trans-3-hydroxy cotinine, were frequently encountered in all the surface water samples. High concentrations (>120 ng/l) of caffeine, metformin, theobromine, and valsartan were detected in the surface water samples; the removal rates of these compounds in the municipal sewage treatment plant were also high. In contrast, although the concentrations of 4-AAA and metoprolol acid in the surface water were high, the removal rates of these residues in the sewage treatment plant were low. Copyright © 2018. Published by Elsevier B.V.

A comparative study on laser induced shock cleaning of radioactive contaminants in air and water

NASA Astrophysics Data System (ADS)

Kumar, Aniruddha; Prasad, Manisha; Bhatt, R. B.; Behere, P. G.; Biswas, D. J.

2018-03-01

Efficient removal of Uranium-di-oxide (UO2) particulates from stainless steel surface was effected by Nd-YAG laser induced plasma shock waves in air as well as in water environment. The propagation velocity of the generated shock wave was measured by employing the photo-acoustic probe deflection method. Monitoring of the alpha activity of the sample with a ZnS (Ag) scintillation detector before and after the laser exposure allowed the estimation of decontamination efficiency defined as the percentage removal of the initial activity. Experiments were carried out to study the effect of laser pulse energy, number of laser exposures, orientation of the sample, the separation between the substrate surface and the onset point of the shock wave on the de-contamination efficiency. The most optimised cleaning was found to occur when the laser beam impinged normally on the sample that was immersed in water and placed at a distance of ∼0.7 mm from the laser focal spot. Analysis of the cleaned surface by optical microscopes established that laser induced shock cleaning in no way altered the surface property. The shock force generated in both air and water has been estimated theoretically and has been found to exceed the Van der Waal's binding force for spherical contaminant particulate.

Enhanced Cleaning of Genesis Solar Wind Sample 61348 for Film Residue Removal

NASA Technical Reports Server (NTRS)

Allums, K. K.; Gonzalez, C. P.; Kuhlman, K. R.; Allton, J. H.

2015-01-01

The Genesis mission returned to Earth on September 8, 2004, experiencing a nonnominal reentry. During the recovery of the collector materials from the capsule, many of the collector fragments were placed on the adhesive protion of post-it notes to prevent the fragments from moving during transport back to Johnson Space Center. This unknowingly provided an additional contaminate that would prove difficult to remove with the limited chemistries allowed in the Genesis Curation Laboratory. Generally when collector material samples are prepared for allocation to PIs, the samples are cleaned front side only with Ultra-Pure Water (UPW) via megasonic dispersion to the collector surface to remove crash debris and contamination. While this cleaning method works well on samples that were not placed on post-its during recovery, it has caused movement of the residue on the back of the sample to be deposited on the front in at least two examples. Therefore, samples placed on the adhesive portion on post-it note, require enhanced cleaning methods since post-it residue has proved resistant to UPW cleaning.

Color and Surface Chemistry Changes of Pine Wood Flour after Extraction and Delignification

Treesearch

Yao Chen; Mandla A. Tshabalala; Jianmin Gao; Nicole M. Stark; Yongming Fan

2014-01-01

A detailed study was undertaken to examine the color and chemistry changes of pine wood flour when its extractives are removed and when it is delignified. The solvent systems employed were toluene/ethanol (TE), acetone/water (AW), and hot-water (HW), while sodium chlorite/acetic acid were used for delignification (i.e., lignin removal (LR)). Samples were analyzed by...

Radioactivity decontamination of materials commonly used as surfaces in general-purpose radioisotope laboratories.

PubMed

Leonardi, Natalia M; Tesán, Fiorella C; Zubillaga, Marcela B; Salgueiro, María J

2014-12-01

In accord with as-low-as-reasonably-achievable and good-manufacturing-practice concepts, the present study evaluated the efficiency of radioactivity decontamination of materials commonly used in laboratory surfaces and whether solvent spills on these materials affect the findings. Four materials were evaluated: stainless steel, a surface comprising one-third acrylic resin and two-thirds natural minerals, an epoxy cover, and vinyl-based multipurpose flooring. Radioactive material was eluted from a (99)Mo/(99m)Tc generator, and samples of the surfaces were control-contaminated with 37 MBq (100 μL) of this eluate. The same procedure was repeated with samples of surfaces previously treated with 4 solvents: methanol, methyl ethyl ketone, acetone, and ethanol. The wet radioactive contamination was allowed to dry and then was removed with cotton swabs soaked in soapy water. The effectiveness of decontamination was defined as the percentage of activity removed per cotton swab, and the efficacy of decontamination was defined as the total percentage of activity removed, which was obtained by summing the percentages of activity in all the swabs required to complete the decontamination. Decontamination using our protocol was most effective and most efficacious for stainless steel and multipurpose flooring. Moreover, treatment with common organic solvents seemed not to affect the decontamination of these surfaces. Decontamination of the other two materials was less efficient and was interfered with by the organic solvents; there was also great variability in the overall results obtained for these other two materials. In expanding our laboratory, it is possible for us to select those surface materials on which our decontamination protocol works best. © 2014 by the Society of Nuclear Medicine and Molecular Imaging, Inc.

The (001) 3C SiC surface termination and band structure after common wet chemical etching procedures, stated by XPS, LEED, and HREELS

NASA Astrophysics Data System (ADS)

Tengeler, Sven; Kaiser, Bernhard; Ferro, Gabriel; Chaussende, Didier; Jaegermann, Wolfram

2018-01-01

The (001) surface of cubic silicon carbide (3C SiC) after cleaning, Ar sputtering and three different wet chemical etching procedures was thoroughly investigated via (angle resolved) XPS, HREELS, and LEED. While Ar sputtering was found to be unsuitable for surface preparation, all three employed wet chemical etching procedures (piranha/NH4F, piranha/HF, and RCA) provide a clean surface. HF as oxide removal agent tends to result in fluorine traces on the sample surface, despite thorough rinsing. All procedures yield a 1 × 1 Si-OH/C-H terminated surface. However, the XPS spectra reveal some differences in the resulting surface states. NH4F for oxide removal produces a flat band situation, whereas the other two procedures result in a slight downward (HF) or upward (RCA) band bending. Because the band bending is small, it can be concluded that the number of unsaturated surface defects is low.

Investigation of argon ion sputtering on the secondary electron emission from gold samples

NASA Astrophysics Data System (ADS)

Yang, Jing; Cui, Wanzhao; Li, Yun; Xie, Guibai; Zhang, Na; Wang, Rui; Hu, Tiancun; Zhang, Hongtai

2016-09-01

Secondary electron (SE) yield, δ, is a very sensitive surface property. The values of δ often are not consistent for even identical materials. The influence of surface changes on the SE yield was investigated experimentally in this article. Argon ion sputtering was used to remove the contamination from the surface. Surface composition was monitored by X-ray photoelectron spectroscopy (XPS) and surface topography was scanned by scanning electron microscope (SEM) and atomic force microscope (AFM) before and after every sputtering. It was found that argon sputtering can remove contamination and roughen the surface. An ;equivalent work function; is presented in this thesis to establish the relationship between SE yield and surface properties. Argon ion sputtering of 1.5keV leads to a significant increase of so called ;work function; (from 3.7 eV to 6.0 eV), and a decrease of SE yield (from 2.01 to 1.54). These results provided a new insight into the influence of surface changes on the SE emission.

Surface Optical Property Measurements on Bark and Leaf Samples

DTIC Science & Technology

1990-12-31

individually positionable in sample measurement position. 100% Value Absolute, or in comparison to high-reflectance evaporated gold reference sample...evaporated gold on a smooth fused silica substrate. The absolute 100% measurement requires removing the sample from the measurement position and...choice is evaporated gold on a polished glass substrate. As- already noted, SOC uses two instruments to cover the full spectral region from 0.2 to 40.0

In-situ monitoring of etching of bovine serum albumin using low-temperature atmospheric plasma jet

NASA Astrophysics Data System (ADS)

Kousal, J.; Shelemin, A.; Kylián, O.; Slavínská, D.; Biederman, H.

2017-01-01

Bio-decontamination of surfaces by means of atmospheric pressure plasma is nowadays extensively studied as it represents promising alternative to commonly used sterilization/decontamination techniques. The non-equilibrium atmospheric pressure plasmas were already reported to be highly effective in removal of a wide range of biological residual from surfaces. Nevertheless the kinetics of removal of biological contamination from surfaces is still not well understood as the majority of performed studies were based on ex-situ evaluation of etching rates, which did not allow investigating details of plasma action on biomolecules. This study therefore presents a real-time, in-situ ellipsometric characterization of removal of bovine serum albumin (BSA) from surfaces by low-temperature atmospheric plasma jet operated in argon. Non-linear and at shorter distances between treated samples and nozzle of the plasma jet also non-monotonic dependence of the removal rate on the treatment duration was observed. According to additional measurements focused on the determination of chemical changes of treated BSA as well as temperature measurements, the observed behavior is most likely connected with two opposing effects: the formation of a thin layer on the top of BSA deposit enriched in inorganic compounds, whose presence causes a gradual decrease of removal efficiency, and slight heating of BSA that facilitates its degradation and volatilization induced by chemically active radicals produced by the plasma.

Adsorption characteristics of selected hydrophilic and hydrophobic micropollutants in water using activated carbon.

PubMed

Nam, Seung-Woo; Choi, Dae-Jin; Kim, Seung-Kyu; Her, Namguk; Zoh, Kyung-Duk

2014-04-15

In this study, we investigated adsorption characteristics of nine selected micropollutants (six pharmaceuticals, two pesticides, and one endocrine disruptor) in water using an activated carbon. The effects of carbon dosage, contact time, pH, DOM (dissolved organic matter), and temperature on the adsorption removal of micropollutants were examined. Increasing carbon dosage and contact time enhanced the removal of micropollutants. Sorption coefficients of hydrophilic compounds (caffeine, acetaminophen, sulfamethoxazole, and sulfamethazine) fit a linear isotherm and hydrophobic compounds (naproxen, diclofenac, 2, 4-D, triclocarban, and atrazine) fit a Freundlich isotherm. The removal of hydrophobic pollutants and caffeine were independent of pH changes, but acetaminophen, sulfamethazine, and sulfamethoxazole were adsorbed by mainly electrostatic interaction with activated carbon and so were affected by pH. The decrease in adsorption removal in surface water samples was observed and this decrease was more significant for hydrophobic than hydrophilic compounds. The decline in the adsorption capacity in surface water samples is caused by the competitive inhibition of DOM with micropollutants onto activated carbon. Low temperature (5°C) also decreased the adsorption removal of micropollutants, and affected hydrophobic compounds more than hydrophilic compounds. The results obtained in this study can be applied to optimize the adsorption capacities of micropollutants using activated carbon in water treatment process. Copyright © 2014 Elsevier B.V. All rights reserved.

Thermal emittance enhancement of graphite-copper composites for high temperature space based radiators

NASA Technical Reports Server (NTRS)

Rutledge, Sharon K.; Forkapa, Mark J.; Cooper, Jill M.

1991-01-01

Graphite-copper composites are candidate materials for space based radiators. The thermal emittance of this material, however, is a factor of two lower than the desired emittance for these systems of greater than or equal to 0.85. Arc texturing was investigated as a surface modification technique for enhancing the emittance of the composite. Since the outer surface of the composite is copper, and samples of the composite could not be readily obtained for testing, copper was used for optimization testing. Samples were exposed to various frequencies and currents of arcs during texturing. Emittances near the desired goal were achieved at frequencies less than 500 Hz. Arc current did not appear to play a major role under 15 amps. Particulate carbon was observed on the surface, and was easily removed by vibration and handling. In order to determine morphology adherence, ultrasonic cleaning was used to remove the loosely adherent material. This reduced the emittance significantly. Emittance was found to increase with increasing frequency for the cleaned samples up to 500 Hz. The highest emittance achieved on these samples over the temperature range of interest was 0.5 to 0.6, which is approximately a factor of 25 increase over the untextured copper emittance.

Ultra-high adsorption capacity of MgO/SiO2 composites with rough surfaces for Congo red removal from water.

PubMed

Hu, Mengqing; Yan, Xinlong; Hu, Xiaoyan; Zhang, Jiajin; Feng, Rui; Zhou, Min

2018-01-15

Due to its high isoelectric point, relative safety and low environmental toxicity, magnesium oxide has attracted much attention for its role in the removal of toxic dyes from wastewater. Herein, MgO-SiO 2 composites with rough surfaces were synthesized by a one-step method. The as-prepared composites were characterized for the adsorption of Congo red from water using adsorption kinetics and isotherms. The adsorption capacity of the 20% MgO-SiO 2 sample could be as high as ∼4000mg/g at 25°C, which is the highest value reported to date. The adsorption process of Congo red on the as-synthesized samples obeyed the Langmuir adsorption model. The MgO-SiO 2 composite sample could be regenerated by calcination, and the regeneration efficiency remained for up to 5 cycles of the regeneration. Copyright © 2017 Elsevier Inc. All rights reserved.

Dependence of Tritium Release from Stainless Steel on Temperature and Water Vapor

DOE Office of Scientific and Technical Information (OSTI.GOV)

Shmayda, W. T.; Sharpe, M.; Boyce, A. M.

The impact of water vapor and temperature on the release of tritium from stainless steel was studied. Degreased stainless steel samples loaded with tritium at room temperature following a 24-h degassing in vacuum at room temperature were subjected to increasing temperatures or humidity. In general, increasing either the sample temperature or the humidity causes an increased quantity of tritium to be removed. Increasing the temperature to 300°C in a dry gas stream results in a significant release of tritium and is therefore an effective means for reducing the tritium inventory in steel. For humid purges at 30°C, a sixfold increasemore » in humidity results in a tenfold increase in the peak outgassing rate. Increasing the humidity from 4 parts per million (ppm) to 1000 ppm when the sample temperature is 100°C causes a significant increase in the tritium outgassing rate. Finally, a simple calculation shows that only 15% of the activity present in the sample was removed in these experiments, suggesting that the surface layer of adsorbed water participates in regulating tritium desorption from the surface.« less

Dependence of Tritium Release from Stainless Steel on Temperature and Water Vapor

DOE PAGES

Shmayda, W. T.; Sharpe, M.; Boyce, A. M.; ...

2015-09-15

The impact of water vapor and temperature on the release of tritium from stainless steel was studied. Degreased stainless steel samples loaded with tritium at room temperature following a 24-h degassing in vacuum at room temperature were subjected to increasing temperatures or humidity. In general, increasing either the sample temperature or the humidity causes an increased quantity of tritium to be removed. Increasing the temperature to 300°C in a dry gas stream results in a significant release of tritium and is therefore an effective means for reducing the tritium inventory in steel. For humid purges at 30°C, a sixfold increasemore » in humidity results in a tenfold increase in the peak outgassing rate. Increasing the humidity from 4 parts per million (ppm) to 1000 ppm when the sample temperature is 100°C causes a significant increase in the tritium outgassing rate. Finally, a simple calculation shows that only 15% of the activity present in the sample was removed in these experiments, suggesting that the surface layer of adsorbed water participates in regulating tritium desorption from the surface.« less

The MOF+ Technique: A Significant Synergic Effect Enables High Performance Chromate Removal.

PubMed

Luo, Ming Biao; Xiong, Yang Yang; Wu, Hui Qiong; Feng, Xue Feng; Li, Jian Qiang; Luo, Feng

2017-12-18

A significant synergic effect between a metal-organic framework (MOF) and Fe 2 SO 4 , the so-called MOF + technique, is exploited for the first time to remove toxic chromate from aqueous solutions. The results show that relative to the pristine MOF samples (no detectable chromate removal), the MOF + method enables super performance, giving a 796 Cr mg g -1 adsorption capacity. The value is almost eight-fold higher than the best value of established MOF adsorbents, and the highest value of all reported porous adsorbents for such use. The adsorption mechanism, unlike the anion-exchange process that dominates chromate removal in all other MOF adsorbents, as unveiled by X-ray photoelectron spectroscopy (XPS), scanning electron microscopy (SEM), and transmission electron microscopy (TEM), is due to the surface formation of Fe 0.75 Cr 0.25 (OH) 3 nanospheres on the MOF samples. © 2017 Wiley-VCH Verlag GmbH & Co. KGaA, Weinheim.

Development of activated carbon derived from banana peel for CO2 removal

NASA Astrophysics Data System (ADS)

Borhan, Azry; Thangamuthu, Subhashini; Taha, Mohd Faisal; Ramdan, Amira Nurain

2015-08-01

This research work highlights on the constraints involved in the preparation of the banana peel bio-sorbent, such as impregnation ratio, activation temperature and period of activation for reducing carbon dioxide (CO2) in the atmosphere. Micromeritics ASAP 2020 and Field Emission Scanning Electron Microscope (FESEM) were used in identifying the best sample preparation method with the largest surface area which directly contributes to the effectiveness of adsorbent in removing CO2. Sample A10 was identified to yield activated carbon with the largest surface area (260.3841 m2/g), total pore volume (0.01638 cm3/g) and pore diameter (0.2508 nm). Through nitrogen adsorption-desorption isotherm analysis, the existence of sub-micropores was proven when a combination of Type-I and Type-II isotherms were exhibited by the activated carbon produced. The results from the final adsorption test found that the material synthesized from the above mentioned parameter is capable of removing up to 1.65% wt of CO2 through adsorption at 25°C, suggesting that it can be effectively used as an adsorption material.

Surface properties and water treatment capacity of surface engineered silica coated with 3-(2-aminoethyl) aminopropyltrimethoxysilane

NASA Astrophysics Data System (ADS)

Majewski, Peter; Keegan, Alexandra

2012-01-01

This study's focus was on the water-based, one-pot preparation and characterisation of silica particles coated with 3-(2-aminoethyl)aminopropyltrimethoxysilane (Diamo) and the efficiency of the material in removing the pathogens Escherichia coli, Pseudomonas aeruginosa, Mycobacterium immunogenum, Vibrio cholerae, poliovirus, and Cryptosporidium parvum. The water-based processing resulted in Diamo coated silica particles with significantly increased positive surface charge as determined by zeta potential measurements. In addition, X-ray photoelectron spectrometry of pure and Diamo coated silica confirmed the presence of Diamo on the surface of the particles. Thermogravimetric measurements and chemical analysis of the silica indicated a surface concentration of amine groups of about 1 mmol/gsilica. Water treatment tests with the pathogens showed that a dose of about 10 g appeared to be sufficient to remove pathogens from pure water samples which were spiked with pathogen concentrations between about 102 and 104 cfu/mL.

Restoration of high-resolution AFM images captured with broken probes

NASA Astrophysics Data System (ADS)

Wang, Y. F.; Corrigan, D.; Forman, C.; Jarvis, S.; Kokaram, A.

2012-03-01

A type of artefact is induced by damage of the scanning probe when the Atomic Force Microscope (AFM) captures a material surface structure with nanoscale resolution. This artefact has a dramatic form of distortion rather than the traditional blurring artefacts. Practically, it is not easy to prevent the damage of the scanning probe. However, by using natural image deblurring techniques in image processing domain, a comparatively reliable estimation of the real sample surface structure can be generated. This paper introduces a novel Hough Transform technique as well as a Bayesian deblurring algorithm to remove this type of artefact. The deblurring result is successful at removing blur artefacts in the AFM artefact images. And the details of the fibril surface topography are well preserved.

Environmental cell assembly for use in for use in spectroscopy and microscopy applications

DOEpatents

Stowe, Ashley Clinton; Smyrl, Norman; Hallman, Jr., Russell L.

2014-09-02

An environmental cell assembly for use in microscopy and spectroscopy applications, including: an environmentally sealed body assembly configured to selectively hold and contain a sample; a plurality of ports manufactured into one or more surfaces of the body assembly for one or more of evacuating the body assembly and injecting a gas into or removing a gas from the body assembly; a port manufactured into a surface of the body assembly for receiving a translating stage configured to move the sample within the body assembly; and a port manufactured into a surface of the body assembly for receiving one or more lenses utilized in a microscopy or spectroscopy application; wherein the one or more lenses are disposed adjacent the sample without intervening structures disposed there between. The cell assembly also includes a port manufactured into a surface of the body assembly for retaining a window and providing visualization of the sample.

Multiscale responses of soil stability and invasive plants to removal of non-native grazers from an arid conservation reserve

USGS Publications Warehouse

Beever, E.A.; Huso, M.; Pyke, D.A.

2006-01-01

Disturbances and ecosystem recovery from disturbance both involve numerous processes that operate on multiple spatial and temporal scales. Few studies have investigated how gradients of disturbance intensity and ecosystem responses are distributed across multiple spatial resolutions and also how this relationship changes through time during recovery. We investigated how cover of non-native species and soil-aggregate stability (a measure of vulnerability to erosion by water) in surface and subsurface soils varied spatially during grazing by burros and cattle and whether patterns in these variables changed after grazer removal from Mojave National Preserve, California, USA. We compared distance from water and number of ungulate defecations - metrics of longer-term and recent grazing intensity, respectively, - as predictors of our response variables. We used information-theoretic analyses to compare hierarchical linear models that accounted for important covariates and allowed for interannual variation in the disturbance-response relationship at local and landscape scales. Soil stability was greater under perennial vegetation than in bare interspaces, and surface soil stability decreased with increasing numbers of ungulate defecations. Stability of surface samples was more affected by time since removal of grazers than was stability of subsurface samples, and subsurface soil stability in bare spaces was not related to grazing intensity, time since removal, or any of our other predictors. In the high rainfall year (2003) after cattle had been removed for 1-2 years, cover of all non-native plants averaged nine times higher than in the low-rainfall year (2002). Given the heterogeneity in distribution of large-herbivore impacts that we observed at several resolutions, hierarchical analyses provided a more complete understanding of the spatial and temporal complexities of disturbance and recovery processes in arid ecosystems. ?? 2006 Blackwell Publishing Ltd.

Multi-scale responses of soil stability and invasive plants to removal of non-native grazers from an arid conservation reserve

USGS Publications Warehouse

Beever, Erik A.; Huso, Manuela M. P.; Pyke, David A.

2006-01-01

Disturbances and ecosystem recovery from disturbance both involve numerous processes that operate on multiple spatial and temporal scales. Few studies have investigated how gradients of disturbance intensity and ecosystem responses are distributed across multiple spatial resolutions and also how this relationship changes through time during recovery. We investigated how cover of non-native species and soil-aggregate stability (a measure of vulnerability to erosion by water) in surface and subsurface soils varied spatially during grazing by burros and cattle and whether patterns in these variables changed after grazer removal from Mojave National Preserve, California, USA. We compared distance from water and number of ungulate defecations — metrics of longer-term and recent grazing intensity, respectively, — as predictors of our response variables. We used information-theoretic analyses to compare hierarchical linear models that accounted for important covariates and allowed for interannual variation in the disturbance–response relationship at local and landscape scales. Soil stability was greater under perennial vegetation than in bare interspaces, and surface soil stability decreased with increasing numbers of ungulate defecations. Stability of surface samples was more affected by time since removal of grazers than was stability of subsurface samples, and subsurface soil stability in bare spaces was not related to grazing intensity, time since removal, or any of our other predictors. In the high rainfall year (2003) after cattle had been removed for 1–2 years, cover of all non-native plants averaged nine times higher than in the low-rainfall year (2002). Given the heterogeneity in distribution of large-herbivore impacts that we observed at several resolutions, hierarchical analyses provided a more complete understanding of the spatial and temporal complexities of disturbance and recovery processes in arid ecosystems.

Nb2O5 nanowires in-situ grown on carbon fiber: A high-efficiency material for the photocatalytic reduction of Cr(VI).

PubMed

Du, Yucheng; Zhang, Shihao; Wang, Jinshu; Wu, Junshu; Dai, Hongxing

2018-04-01

Niobium oxide nanowire-deposited carbon fiber (CF) samples were prepared using a hydrothermal method with amorphous Nb 2 O 5 ·nH 2 O as precursor. The physical properties of the samples were characterized by means of numerous techniques, including X-ray diffraction (XRD), energy-dispersive spectroscopy (EDS), scanning electron microscopy (SEM), transmission electron microscopy (TEM), selected-area electron diffraction (SAED), UV-visible spectroscopy (UV-vis), N 2 adsorption-desorption, Fourier transform infrared spectroscopy (FT-IR), and X-ray photoelectron spectroscopy. The efficiency for the removal of Cr(VI) was determined. Parameters such as pH value and initial Cr(VI) concentration could influence the Cr(VI) removal efficiency or adsorption capacity of the Nb 2 O 5 /carbon fiber sample obtained after hydrothermal treatment at 160°C for 14hr. The maximal Cr(VI) adsorption capacity of the Nb 2 O 5 nanowire/CF sample was 115mg/g. This Nb 2 O 5 /CF sample also showed excellent photocatalytic activity and stability for the reduction of Cr(VI) under UV-light irradiation: the Cr(VI) removal efficiency reached 99.9% after UV-light irradiation for 1hr and there was no significant decrease in photocatalytic performance after the use of the sample for 10 repeated cycles. Such excellent Cr(VI) adsorption capacity and photocatalytic performance was related to its high surface area, abundant surface hydroxyl groups, and good UV-light absorption ability. Copyright © 2017. Published by Elsevier B.V.

Laser cleaning of the contaminations on the surface of tire mould

NASA Astrophysics Data System (ADS)

Ye, Yayun; Jia, Baoshen; Chen, Jing; Jiang, Yilan; Tang, Hongping; Wang, Haijun; Luan, Xiaoyu; Liao, Wei; Zhang, Chuanchao; Yao, Caizhen

2017-07-01

During the manufacturing of tires, surface pollutants on tire mould will lead to the production of unqualified tires. Tire moulds need to be regularly cleaned. Laser cleaning is recognized as a non-destructive, effective, precise and environmental friendly method. In this paper, laser cleaning was used to remove contaminants on tire mould surface. First, laser induced damage experiments were performed. The results showed that the roughness and hardness of the cast steel sample surface seldom changed under the energy range of 140.1-580.2 mJ laser irradiation 1 pulse and the energy range of 44.7-168.9 mJ laser irradiation 100 pulses. In the laser cleaning experiments, the cleaning thresholds and the optimal cleaning parameters were obtained. Results indicated that laser cleaning was safe and effective for tire mould contamination removal.

Cleaning and disinfection in home care: A comparison of 2 commercial products with potentially different consequences for respiratory health.

PubMed

Goodyear, Nancy; Markkanen, Pia; Beato-Melendez, Christian; Mohamed, Hagir; Gore, Rebecca; Galligan, Catherine; Sama, Susan; Quinn, Margaret

2018-04-01

Home care aides perform personal care and homemaking services in client homes, including cleaning and disinfection (C&D). Although C&D are performed to remove soil and dust, they are increasingly performed for infection prevention. Many C&D products contain respiratory irritants. The objective of this study was to evaluate 2 commercial products for C&D effectiveness on common household surfaces in seniors' homes. Two C&D visits were conducted in 46 seniors' homes. One visit applied a bleach-containing cleaning product and the other applied an environmentally preferable product. Before and after C&D, the study team performed organic soil bioluminometer measurements on surfaces and collected cotton swab and wipe samples for total bacteria count, Staphylococcus aureus, and Clostridium difficile identification. Both products removed microorganisms from tested surfaces. S aureus was found in 7 households, 1 strain of which was methicillin-resistant. Both products removed S aureus from all surfaces. Bleach-containing products removed somewhat more soil than environmentally preferable products, although results were statistically significant for only 1 surface. The study showed similar, not identical, C&D performance for 2 cleaning products with potentially different consequences for respiratory health. Additional research is needed to develop robust recommendations for safe, effective C&D in home care. Copyright © 2018 Association for Professionals in Infection Control and Epidemiology, Inc. Published by Elsevier Inc. All rights reserved.

Analysis of Leading Edge and Trailing Edge Cover Glass Samples Before and After Treatment with Advanced Satellite Contamination Removal Techniques

DTIC Science & Technology

1993-04-01

surface analysis, 40 contamination control, ANCC ( Aerogel Mesh Contamination Collector) iPRICECODE 17. SECURITY CLASSIFICATION 1 & SECURITY CLASSIFICATION...operational parameter space (temperature, vibration, radiation, vacuum and micrometorite environments). One embodiment of this device, the Aerogel Mesh...Lippey and Dan Demeo of Hughes Aircraft Corporation for their kind hospitality and research collaboration on the contamination removal phase of this work

Efficacy of a Sonicating Swab for Removal and Capture of Listeria monocytogenes in Biofilms on Stainless Steel

PubMed Central

Branck, Tobyn A.; Hurley, Matthew J.; Prata, Gianna N.; Crivello, Christina A.

2017-01-01

ABSTRACT Listeria monocytogenes is of great concern in food processing facilities because it persists in biofilms, facilitating biotransfer. Stainless steel is commonly used for food contact surfaces and transport containers. L. monocytogenes biofilms on stainless steel served as a model system for surface sampling, to test the performance of a sonicating swab in comparison with a standard cotton swab. Swab performance and consistency were determined using total viable counts. Stainless steel coupons sampled with both types of swabs were examined using scanning electron microscopy, to visualize biofilms and surface structures (i.e., polishing grooves and scratches). Laser scanning confocal microscopy was used to image and to quantitate the biofilms remaining after sampling with each swab type. The total viable counts were significantly higher (P ≤ 0.05) with the sonicating swab than with the standard swab in each trial. The sonicating swab was more consistent in cell recovery than was the standard swab, with coefficients of variation ranging from 8.9% to 12.3% and from 7.1% to 37.6%, respectively. Scanning electron microscopic imaging showed that biofilms remained in the polished grooves of the coupons sampled with the standard swab but were noticeably absent with the sonicating swab. Percent area measurements of biofilms remaining on the stainless steel coupons showed significantly (P ≤ 0.05) less biofilm remaining when the sonicating swab was used (median, 1.1%), compared with the standard swab (median, 70.4%). The sonicating swab provided greater recovery of cells, with more consistency, than did the standard swab, and it is employs sonication, suction, and scrubbing. IMPORTANCE Inadequate surface sampling can result in foodborne illness outbreaks from biotransfer, since verification of sanitization protocols relies on surface sampling and recovery of microorganisms for detection and enumeration. Swabbing is a standard method for microbiological sampling of surfaces. Although swabbing offers portability and ease of use, there are limitations, such as high user variability and low recovery rates, which can be attributed to many different causes. This study demonstrates some benefits that a sonicating swab has over a standard swab for removal and collection of microbiological samples from a surface, to provide better verification of surface cleanliness and to help decrease the potential for biotransfer of pathogens into foods. PMID:28314729

Efficacy of a Sonicating Swab for Removal and Capture of Listeria monocytogenes in Biofilms on Stainless Steel.

PubMed

Branck, Tobyn A; Hurley, Matthew J; Prata, Gianna N; Crivello, Christina A; Marek, Patrick J

2017-06-01

Listeria monocytogenes is of great concern in food processing facilities because it persists in biofilms, facilitating biotransfer. Stainless steel is commonly used for food contact surfaces and transport containers. L. monocytogenes biofilms on stainless steel served as a model system for surface sampling, to test the performance of a sonicating swab in comparison with a standard cotton swab. Swab performance and consistency were determined using total viable counts. Stainless steel coupons sampled with both types of swabs were examined using scanning electron microscopy, to visualize biofilms and surface structures (i.e., polishing grooves and scratches). Laser scanning confocal microscopy was used to image and to quantitate the biofilms remaining after sampling with each swab type. The total viable counts were significantly higher ( P ≤ 0.05) with the sonicating swab than with the standard swab in each trial. The sonicating swab was more consistent in cell recovery than was the standard swab, with coefficients of variation ranging from 8.9% to 12.3% and from 7.1% to 37.6%, respectively. Scanning electron microscopic imaging showed that biofilms remained in the polished grooves of the coupons sampled with the standard swab but were noticeably absent with the sonicating swab. Percent area measurements of biofilms remaining on the stainless steel coupons showed significantly ( P ≤ 0.05) less biofilm remaining when the sonicating swab was used (median, 1.1%), compared with the standard swab (median, 70.4%). The sonicating swab provided greater recovery of cells, with more consistency, than did the standard swab, and it is employs sonication, suction, and scrubbing. IMPORTANCE Inadequate surface sampling can result in foodborne illness outbreaks from biotransfer, since verification of sanitization protocols relies on surface sampling and recovery of microorganisms for detection and enumeration. Swabbing is a standard method for microbiological sampling of surfaces. Although swabbing offers portability and ease of use, there are limitations, such as high user variability and low recovery rates, which can be attributed to many different causes. This study demonstrates some benefits that a sonicating swab has over a standard swab for removal and collection of microbiological samples from a surface, to provide better verification of surface cleanliness and to help decrease the potential for biotransfer of pathogens into foods. Copyright © 2017 American Society for Microbiology.

Partitioning of Antibiotic Resistance Genes and Fecal Indicators Varies Intra and Inter-Storm during Combined Sewer Overflows

PubMed Central

Eramo, Alessia; Delos Reyes, Hannah; Fahrenfeld, Nicole L.

2017-01-01

Combined sewer overflows (CSOs) degrade water quality through the release of microbial contaminants in CSO effluent. Improved understanding of the partitioning of microbial contaminants onto settleable particles can provide insight into their fate in end-of-pipe treatment systems or following release during CSO events. Sampling was performed across the hydrograph for three storm events as well as during baseflow and wet weather in three surface waters impacted by CSO. qPCR was performed for select antibiotic resistance genes (ARG) and a marker gene for human fecal indicator organisms (BacHum) in samples processed the partitioning of microbial contaminants on settleable particles versus suspended in the aqueous phase. Amplicon sequencing was performed on both fractions of storm samples to further define the timing and partitioning of microbial contaminants released during CSO events. Samples collected at the CSO outfall exhibited microbial community signatures of wastewater at select time points early or late in the storm events. CSOs were found to be a source of ARG. In surrounding surface waters, sul1 was higher in samples from select locations during wet weather compared to baseflow. Otherwise, ARG concentrations were variable with no differences between baseflow and wet weather conditions. The majority of ARG at the CSO outfall were observed on the attached fraction of samples: 64–79% of sul1 and 59–88% of tet(G). However, the timing of peak ARG and human fecal indicator marker gene BacHum did not necessarily coincide with observation of the microbial signature of wastewater in CSO effluent. Therefore, unit processes that remove settleable particles (e.g., hydrodynamic separators) operated throughout a CSO event would achieve up to (0.5–0.9)-log removal of ARG and fecal indicators by removing the attached fraction of measured genes. Secondary treatment would be required if greater removal of these targets is needed. PMID:29104562

Effect of probiotics on patulin removal from synbiotic apple juice.

PubMed

Zoghi, Alaleh; Khosravi-Darani, Kianoush; Sohrabvandi, Sara; Attar, Hosein; Alavi, Sayed Abolhasan

2017-06-01

Studies have reported the occurrence of the mycotoxin patulin in apple products. The aim of this study was to produce synbiotic apple juice and investigate the detoxification of patulin by Lactobacillus acidophilus and Lactobacillus plantarum as probiotic strains. The impact of seven process variables on efficiency of toxin removal was investigated using Plackett-Burman design and presence of the surface-layer proteins as binding site of probiotics to patulin was confirmed during 6 weeks of cold storage. Results showed that the removal of patulin by probiotic bacteria from apple juice depends significantly (P < 0.05) on the fructooligosaccharide content (as a prebiotic), concentration of patulin and the addition of ascorbic acid. Sodium dodecyl sulfate polyacrylamide gel electrophoresis of cell surface proteins of probiotic strains revealed that surface layer proteins have an important role in patulin removal from apple juice. In the best conditions, 91.23% of initial patulin concentration was removed from juice during 6 weeks refrigerated storage. No significant difference was observed in organoleptic properties of the synbiotic apple juice and raw sample. In the best condition reported in this study, contaminated synbiotic apple juice by patulin will be safe for consumers after the first day of probiotic inoculation. © 2016 Society of Chemical Industry. © 2016 Society of Chemical Industry.

Analysis and comparison of focused ion beam milling and vibratory polishing sample surface preparation methods for porosity study of U-Mo plate fuel for research and test reactors.

PubMed

Westman, Bjorn; Miller, Brandon; Jue, Jan-Fong; Aitkaliyeva, Assel; Keiser, Dennis; Madden, James; Tucker, Julie D

2018-07-01

Uranium-Molybdenum (U-Mo) low enriched uranium (LEU) fuels are a promising candidate for the replacement of high enriched uranium (HEU) fuels currently in use in a high power research and test reactors around the world. Contemporary U-Mo fuel sample preparation uses focused ion beam (FIB) methods for analysis of fission gas porosity. However, FIB possess several drawbacks, including reduced area of analysis, curtaining effects, and increased FIB operation time and cost. Vibratory polishing is a well understood method for preparing large sample surfaces with very high surface quality. In this research, fission gas porosity image analysis results are compared between samples prepared using vibratory polishing and FIB milling to assess the effectiveness of vibratory polishing for irradiated fuel sample preparation. Scanning electron microscopy (SEM) imaging was performed on sections of irradiated U-Mo fuel plates and the micrographs were analyzed using a fission gas pore identification and measurement script written in MatLab. Results showed that the vibratory polishing method is preferentially removing material around the edges of the pores, causing the pores to become larger and more rounded, leading to overestimation of the fission gas porosity size. Whereas, FIB preparation tends to underestimate due to poor micrograph quality and surface damage leading to inaccurate segmentations. Despite the aforementioned drawbacks, vibratory polishing remains a valid method for porosity analysis sample preparation, however, improvements should be made to reduce the preferential removal of material surrounding pores in order to minimize the error in the porosity measurements. Copyright © 2018 Elsevier Ltd. All rights reserved.

Evaluation of Various Cleaning Methods to Remove Bacillus Spores from Spacecraft Hardware Materials

NASA Technical Reports Server (NTRS)

Venkateswaran, Kasthuri; Chung, Shirley; Allton, Judith; Kern, Roger

2004-01-01

A detailed study was made of the biological cleaning effectiveness, defined in terms of the ability to remove bacterial spores, of a number of methods used to clean hardware surfaces. Aluminum (Al 6061) and titanium (Ti 6Al-4V) were chosen for the study as they were deemed the two materials most likely to be used in spacecraft extraterrestrial sampler construction. None of the cleaning protocols tested completely removed viable spores from the surface of the aluminum. In contrast, titanium was capable of being cleaned to sterility by two methods, the JPL standard and the commercial SAMS cleaning process. Further investigation showed that the passivation step employed in the JPL standard method is an effective surface sterilant on both metals but not compatible with aluminum. It is recommended that titanium (Ti 6Al-4V) be considered superior to aluminum (Al 6061) for use in spacecraft sampling hardware, both for its potential to be cleaned to sterilization and for its ability to withstand the most effective cleaning protocols.

Selenium mobilization during a flood experiment in a contaminated wetland: Stewart Lake Waterfowl Management Area, Utah

USGS Publications Warehouse

Naftz, D.L.; Yahnke, J.; Miller, J.; Noyes, S.

2005-01-01

Constructed and natural wetlands can accumulate elevated levels of Se; however, few data are available on cost-effective methods for remobilization and removal of Se from these areas. A field experiment was conducted to assess the effectiveness of flooding on the removal of Se from dry surface sediments. The 83-m2 flood-experiment plot contained 10 monitoring wells, a water-quality minimonitor (continuous measurement of pH, specific conductance, water temperature, and dissolved O2), a down-hole Br electrode, and 2 pressure transducers. Flooding was initiated on August 27, 2002, and a Br tracer was added to water delivered through a pipeline to the flood plot during the first 1.2 h. Standing water depth in the flood plot was maintained at 0.3 m through September 1, 2002. The Br tracer data indicate a dual porosity system that includes fracture (mud cracks) and matrix flow components. Mean vertical water velocities for the matrix flow component were estimated to range from 0.002 to 0.012 m/h. Dissolved (less than 0.45 ??m) Se increased from pre-flood concentrations of less than 10 ??g/L to greater than 800 ??g/L during flooding in samples from deep (2.0 m below land surface) ground water. Selenium concentrations exceeded 5500 ??g/L in samples from shallow (0.8 m below land surface) ground water. Ratios of Se to Br in water samples indicate that Se moved conservatively during the experiment and was derived from leaching of near-surface sediments. Cumulative Se flux to the deep ground water during the experiment ranged from 9.0 to 170 mg/m2. Pre- and post-flood surface soil sampling indicated a mean Se flux of 720 mg/m2 through the top 15 cm of soil. Ground-water samples collected 8 months after termination of the flood experiment contained Se concentrations of less than 20 ??g/L. The minimonitor data indicate a rapid return to chemically reducing conditions in the deep ground water, limiting the mobility of the Se dissolved in the water pulse introduced during the flood experiment. Ratios of Se to Br in deep ground-water samples collected 8 months after the experiment confirmed the removal of Se from the aqueous phase. Based on the median Se flux rate estimated during the experiment of 0.65 mg/h/m2 (n = 52), 7 flooding cycles would be required to meet the 4 ??g/g remediation goal in surface soils from the SLWMA wetland.

Fate of Nutrients in Shallow Groundwater Receiving Treated Septage, Malibu, CA

PubMed Central

Izbicki, John A

2014-01-01

Treated wastewater discharged from more than 400 onsite wastewater treatment systems (OWTS) near the Civic Center area of Malibu, California, 40 km west of downtown Los Angeles, composes 28% of the recharge to a 3.4 km2 alluvial aquifer. On the basis of δ18O and δD data, the fraction of wastewater in some samples was >70%. Ammonium and nitrate concentrations in water from 15 water-table wells sampled in July 2009 and April 2010 ranged from <0.01 to 12 milligrams per liter as nitrogen (mg/L as N), and from <0.01 to 11 mg/L as N, respectively. Chemical and isotopic data (δ15N of ammonium and nitrate, and δ18O of nitrate) show two processes remove nitrogen discharged from OWTS. Where groundwater was reducing, sorption of ammonium resulted in 30 to 50% nitrogen removal. Where groundwater was initially oxic, nitrification with subsequent denitrification as reducing conditions developed, resulted in up to 60% nitrogen removal. Nitrogen removal through sorption dominated during the cooler April sample period, and denitrification dominated during the warmer July sample period. The combination of mixing and nitrogen removal due to denitrification, sorption, and volatilization produces a δ15N apparent fractionation factor (εapp = −5), that can be explained using laboratory-derived fractionation factors (ε) for the individual processes. Phosphate concentrations ranged from < 0.04 to 2 mg/L as phosphorous. Sorption to iron oxides on the surfaces of mineral grains at near-neutral pH's removed some phosphate; however, little removal occurred at more alkaline pH's (>7.3). PMID:24902718

Fate of nutrients in shallow groundwater receiving treated septage, Malibu, CA

USGS Publications Warehouse

Izbicki, John

2014-01-01

Treated wastewater discharged from more than 400 onsite wastewater treatment systems (OWTS) near the Civic Center area of Malibu, California, 40 km west of downtown Los Angeles, composes 28% of the recharge to a 3.4 km2 alluvial aquifer. On the basis of δ18O and δD data, the fraction of wastewater in some samples was >70%. Ammonium and nitrate concentrations in water from 15 water-table wells sampled in July 2009 and April 2010 ranged from <0.01 to 12 milligrams per liter as nitrogen (mg/L as N), and from <0.01 to 11 mg/L as N, respectively. Chemical and isotopic data (δ15N of ammonium and nitrate, and δ18O of nitrate) show two processes remove nitrogen discharged from OWTS. Where groundwater was reducing, sorption of ammonium resulted in 30 to 50% nitrogen removal. Where groundwater was initially oxic, nitrification with subsequent denitrification as reducing conditions developed, resulted in up to 60% nitrogen removal. Nitrogen removal through sorption dominated during the cooler April sample period, and denitrification dominated during the warmer July sample period. The combination of mixing and nitrogen removal due to denitrification, sorption, and volatilization produces a δ15N apparent fractionation factor (εapp= -5), that can be explained using laboratory-derived fractionation factors (ε) for the individual processes. Phosphate concentrations ranged from <0.04 to 2 mg/L as phosphorous. Sorption to iron oxides on the surfaces of mineral grains at near-neutral pH's removed some phosphate; however, little removal occurred at more alkaline pH's (>7.3).

Assessment of personal airborne exposures and surface contamination from x-ray vaporization of beryllium targets at the National Ignition Facility.

PubMed

Paik, Samuel Y; Epperson, Patrick M; Kasper, Kenneth M

2017-06-01

This article presents air and surface sampling data collected over the first two years since beryllium was introduced as a target material at the National Ignition Facility. Over this time, 101 experiments with beryllium-containing targets were executed. The data provides an assessment of current conditions in the facility and a baseline for future impacts as new, reduced regulatory limits for beryllium are being proposed by both the Occupational Safety and Health Administration and Department of Energy. This study also investigates how beryllium deposits onto exposed surfaces as a result of x-ray vaporization and the effectiveness of simple decontamination measures in reducing the amount of removable beryllium from a surface. Based on 1,961 surface wipe samples collected from entrant components (equipment directly exposed to target debris) and their surrounding work areas during routine reconfiguration activities, only one result was above the beryllium release limit of 0.2 µg/100 cm 2 and 27 results were above the analytical reporting limit of 0.01 µg/100 cm 2 , for a beryllium detection rate of 1.4%. Surface wipe samples collected from the internal walls of the NIF target chamber, however, showed higher levels of beryllium, with beryllium detected on 73% and 87% of the samples during the first and second target chamber entries (performed annually), respectively, with 23% of the samples above the beryllium release limit during the second target chamber entry. The analysis of a target chamber wall panel exposed during the first 30 beryllium-containing experiments (cumulatively) indicated that 87% of the beryllium contamination remains fixed onto the surface after wet wiping the surface and 92% of the non-fixed contamination was removed by decontaminating the surface using a dry wipe followed by a wet wipe. Personal airborne exposures assessed during access to entrant components and during target chamber entry indicated that airborne beryllium was not present in workers' breathing zones. All the data thus far have shown that beryllium has been effectively managed to prevent exposures to workers during routine and non-routine work.

Assessment of personal airborne exposures and surface contamination from x-ray vaporization of beryllium targets at the National Ignition Facility

DOE PAGES

Paik, Samuel Y.; Epperson, Patrick M.; Kasper, Kenneth M.

2017-02-28

Here, this article presents air and surface sampling data collected over the first two years since beryllium was introduced as a target material at the National Ignition Facility. Over this time, 101 experiments with beryllium-containing targets were executed. The data provides an assessment of current conditions in the facility and a baseline for future impacts as new, reduced regulatory limits for beryllium are being proposed by both the Occupational Safety and Health Administration and Department of Energy. This study also investigates how beryllium deposits onto exposed surfaces as a result of x-ray vaporization and the effectiveness of simple decontamination measuresmore » in reducing the amount of removable beryllium from a surface. Based on 1,961 surface wipe samples collected from entrant components (equipment directly exposed to target debris) and their surrounding work areas during routine reconfiguration activities, only one result was above the beryllium release limit of 0.2 µg/100 cm 2 and 27 results were above the analytical reporting limit of 0.01 µg/100 cm 2, for a beryllium detection rate of 1.4%. Surface wipe samples collected from the internal walls of the NIF target chamber, however, showed higher levels of beryllium, with beryllium detected on 73% and 87% of the samples during the first and second target chamber entries (performed annually), respectively, with 23% of the samples above the beryllium release limit during the second target chamber entry. The analysis of a target chamber wall panel exposed during the first 30 beryllium-containing experiments (cumulatively) indicated that 87% of the beryllium contamination remains fixed onto the surface after wet wiping the surface and 92% of the non-fixed contamination was removed by decontaminating the surface using a dry wipe followed by a wet wipe. Personal airborne exposures assessed during access to entrant components and during target chamber entry indicated that airborne beryllium was not present in workers' breathing zones. Finally, all the data thus far have shown that beryllium has been effectively managed to prevent exposures to workers during routine and non-routine work.« less

Removal of both N-nitrosodimethylamine and trihalomethanes precursors in a single treatment using ion exchange resins.

PubMed

Beita-Sandí, Wilson; Karanfil, Tanju

2017-11-01

Drinking water utilities are relying more than ever on water sources impacted by wastewater effluents. Disinfection/oxidation of these waters during water treatment may lead to the formation of several disinfection by-products, including the probable human carcinogen N-nitrosodimethylamine (NDMA) and the regulated trihalomethanes (THMs). In this study, the potential of ion exchange resins to control both NDMA and THMs precursors in a single treatment is presented. Two ion exchange resins were examined, a cation exchange resin (Plus) to target NDMA precursors and an anion exchange resin (MIEX) for THMs precursors control. We applied the resins, individually and combined, in the treatment of surface and wastewater effluent samples. The treatment with both resins removed simultaneously NDMA (43-85%) and THMs (39-65%) precursors. However, no removal of NDMA precursors was observed in the surface water with low initial NDMA FP (14 ng/L). The removals of NDMA FP and THMs FP with Plus and MIEX resins applied alone were (49-90%) and (41-69%), respectively. These results suggest no interaction between the resins, and thus the feasibility of effectively controlling NDMA and THMs precursors concomitantly. Additionally, the effects of the wastewater impact and the natural attenuation of precursors were studied. The results showed that neither the wastewater content nor the attenuation of the precursor affected the removals of NDMA and THMs precursors. Finally, experiments using a wastewater effluent sample showed that an increase in the calcium concentration resulted in a reduction in the removal of NDMA precursors of about 50%. Copyright © 2017 Elsevier Ltd. All rights reserved.

XPS studies of nitrogen doping niobium used for accelerator applications

NASA Astrophysics Data System (ADS)

Yang, Ziqin; Lu, Xiangyang; Tan, Weiwei; Zhao, Jifei; Yang, Deyu; Yang, Yujia; He, Yuan; Zhou, Kui

2018-05-01

Nitrogen doping study on niobium (Nb) samples used for the fabrication of superconducting radio frequency (SRF) cavities was carried out. The samples' surface treatment was attempted to replicate that of the Nb SRF cavities, which includes heavy electropolishing (EP), nitrogen doping and the subsequent EP with different amounts of material removal. The surface chemical composition of Nb samples with different post treatments has been studied by XPS. The chemical composition of Nb, O, C and N was presented before and after Gas Cluster Ion Beam (GCIB) etching. No signals of poorly superconducting nitrides NbNx was found on the surface of any doped Nb sample with the 2/6 recipe before GCIB etching. However, in the depth range greater than 30 nm, the content of N element is below the XPS detection precision scope even for the Nb sample directly after nitrogen doping treatment with the 2/6 recipe.

Catchment-Scale Sampling Reveals the Consistent Function of the Sediment-Water Interface to Remove Landscape Scale Dissolved Organic Carbon Properties

NASA Astrophysics Data System (ADS)

Lee-Cullin, J. A.; Zarnetske, J. P.; Wiewiora, E.; Ruhala, S.; Hampton, T. B.

2016-12-01

Dissolved organic carbon (DOC) is a critical component to biogeochemical cycling and water quality in surface waters. As DOC moves through stream networks, from headwaters to higher order streams, the sediment-water interface (SWI), where streams and groundwater readily interact, exerts a strong influence on DOC concentrations and compositional characteristics (i.e., molecular properties). Few studies examine SWI patterns at larger spatial scales, instead focusing primarily on site-level studies because sampling in the SWI is methodologically time and labor intensive. It is presently unknown how land use and landcover influence the fate of DOC in the SWI and therefore the function of the SWI on catchment-scale DOC conditions. Here, we performed a catchment-scale, high spatial-resolution SWI sampling campaign to test how landscape pattern DOC signatures are propagated into the stream and groundwater, and to assess the fate of these signatures when DOC travels through the SWI. We sampled across 39 sites composed of first-, second-, and third-order locations in a lowland, third-order catchment composed of diverse landscape units and properties, including wetland, upland forest, and agriculture. At each of these locations, surface water, groundwater, and SWI water were collected, including six discrete depths across the SWI. The major land use and landcover properties were also determined for each of these locations. We developed two simple generalized linear models to identify the landscape properties with greatest explanatory power for DOC conditions - one for stream water and one for groundwater. The correlation between landscape properties and surface water DOC characteristics was stronger than between landscape properties and groundwater DOC characteristics. To test if the DOC properties from surface and groundwater were preserved or removed by the SWI, the resulting best-fit models for each water source were used to predict the DOC conditions across the SWI. The models were unable to predict SWI DOC conditions, indicating that the landscape signature present in both the surface water and groundwater is removed by processes occurring in the SWI. Overall, this suggests that the SWI functions as and effective zone for processing the landscape-derived DOC signatures.

Catchment-Scale Sampling Reveals the Consistent Function of the Sediment-Water Interface to Remove Landscape Scale Dissolved Organic Carbon Properties

NASA Astrophysics Data System (ADS)

Lee-Cullin, J. A.; Zarnetske, J. P.; Wiewiora, E.; Ruhala, S.; Hampton, T. B.

2017-12-01

Dissolved organic carbon (DOC) is a critical component to biogeochemical cycling and water quality in surface waters. As DOC moves through stream networks, from headwaters to higher order streams, the sediment-water interface (SWI), where streams and groundwater readily interact, exerts a strong influence on DOC concentrations and compositional characteristics (i.e., molecular properties). Few studies examine SWI patterns at larger spatial scales, instead focusing primarily on site-level studies because sampling in the SWI is methodologically time and labor intensive. It is presently unknown how land use and landcover influence the fate of DOC in the SWI and therefore the function of the SWI on catchment-scale DOC conditions. Here, we performed a catchment-scale, high spatial-resolution SWI sampling campaign to test how landscape pattern DOC signatures are propagated into the stream and groundwater, and to assess the fate of these signatures when DOC travels through the SWI. We sampled across 39 sites composed of first-, second-, and third-order locations in a lowland, third-order catchment composed of diverse landscape units and properties, including wetland, upland forest, and agriculture. At each of these locations, surface water, groundwater, and SWI water were collected, including six discrete depths across the SWI. The major land use and landcover properties were also determined for each of these locations. We developed two simple generalized linear models to identify the landscape properties with greatest explanatory power for DOC conditions - one for stream water and one for groundwater. The correlation between landscape properties and surface water DOC characteristics was stronger than between landscape properties and groundwater DOC characteristics. To test if the DOC properties from surface and groundwater were preserved or removed by the SWI, the resulting best-fit models for each water source were used to predict the DOC conditions across the SWI. The models were unable to predict SWI DOC conditions, indicating that the landscape signature present in both the surface water and groundwater is removed by processes occurring in the SWI. Overall, this suggests that the SWI functions as and effective zone for processing the landscape-derived DOC signatures.

Effect of rotary cutting instruments on the resin-tooth interfacial ultra structure: An in vivo study.

PubMed

Sherawat, Sudhir; Tewari, Sanjay; Duhan, Jigyasa; Gupta, Alpa; Singla, Rakesh

2014-12-01

To evaluate the effect of cutting teeth with different types of burs at various speeds on surface topography of tooth surface and interfacial gap formation at resin-tooth interface. The human molars were divided into seven groups: Diamond bur in airrotor (DA) & micromotor (DM), crosscut carbide bur in airrotor (CCA) & micromotor (CCM), plain carbide bur in airrotor (CA) & micromotor (CM) and #600-grit silicon carbide paper (SiC). In five samples from each group Class II box-only cavities were restored. The occlusal surface of four teeth per group was flattened. Two out of four teeth were acid etched. Teeth were subjected for scanning electron microscopy (SEM). Interfacial gap was observed in all groups with no significant difference. SEM observations revealed CA, CCA & DA were coarser than CM, CCM, DM and SiC. SEM of etched tooth surfaces revealed complete removal of amorphous smear layer in CA & CM, partial removal in CCA, CCM, DA & DM and no removal in SiC. Selecting an appropriate bur and its speed may not play an important role in bonding in terms of interfacial gap formation. Variable changes were observed in surface topography with different burs before and after acid etching. Key words:Surface topography, resin-tooth interface, interfacial gap, bonding.

Effect of rotary cutting instruments on the resin-tooth interfacial ultra structure: An in vivo study

PubMed Central

Sherawat, Sudhir; Tewari, Sanjay; Duhan, Jigyasa; Singla, Rakesh

2014-01-01

Objectives: To evaluate the effect of cutting teeth with different types of burs at various speeds on surface topography of tooth surface and interfacial gap formation at resin-tooth interface. Material and Methods: The human molars were divided into seven groups: Diamond bur in airrotor (DA) & micromotor (DM), crosscut carbide bur in airrotor (CCA) & micromotor (CCM), plain carbide bur in airrotor (CA) & micromotor (CM) and #600-grit silicon carbide paper (SiC). In five samples from each group Class II box-only cavities were restored. The occlusal surface of four teeth per group was flattened. Two out of four teeth were acid etched. Teeth were subjected for scanning electron microscopy (SEM). Results: Interfacial gap was observed in all groups with no significant difference. SEM observations revealed CA, CCA & DA were coarser than CM, CCM, DM and SiC. SEM of etched tooth surfaces revealed complete removal of amorphous smear layer in CA & CM, partial removal in CCA, CCM, DA & DM and no removal in SiC. Conclusions: Selecting an appropriate bur and its speed may not play an important role in bonding in terms of interfacial gap formation. Variable changes were observed in surface topography with different burs before and after acid etching. Key words:Surface topography, resin-tooth interface, interfacial gap, bonding. PMID:25674310

Post-treatment of molasses wastewater by electrocoagulation and process optimization through response surface analysis.

PubMed

Tsioptsias, C; Petridis, D; Athanasakis, N; Lemonidis, I; Deligiannis, A; Samaras, P

2015-12-01

Molasses wastewater is a high strength effluent of food industry such as distilleries, sugar and yeast production plants etc. It is characterized by a dark brown color and exhibits a high content in substances of recalcitrant nature such as melanoidins. In this study, electrocoagulation (EC) was studied as a post treatment step for biologically treated molasses wastewater with high nitrogen content obtained from a baker's yeast industry. Iron and copper electrodes were used in various forms; the influence and interaction of current density, molasses wastewater dilution, and reaction time, on COD, color, ammonium and nitrate removal rates and operating cost were studied and optimized through Box Behnken's response surface analysis. Reaction time varied from 0.5 to 4 h, current density varied from 5 to 40 mA/cm(2) and dilution from 0 to 90% (v/v expressed as water concentration). pH, conductivity and temperature measurements were also carried out during each experiment. From preliminary experiments, it was concluded that the application of aeration and sample dilution, considerably influenced the kinetics of the process. The obtained results showed that COD removal varied between 10 and 54%, corresponding to an operation cost ranging from 0.2 to 33 euro/kg COD removed. Significant removal rates were obtained for nitrogen as nitrate and ammonium (i.e. 70% ammonium removal). A linear relation of COD and ammonium to the design parameters was observed, while operation cost and nitrate removal responded in a curvilinear function. A low ratio of electrode surface to treated volume was used, associated to a low investment cost; in addition, iron wastes could be utilized as low cost electrodes i.e. iron fillings from lathes, aiming to a low operation cost due to electrodes replacement. In general, electrocoagulation proved to be an effective and low cost process for biologically treated molasses-wastewater treatment for additional removal of COD and nitrogen content and color reduction. Treated effluent samples with good quality were produced by EC, with COD, NH4-N and NO3-N concentrations of 180, 52 and 2 mg/l respectively. Response surface analysis revealed that optimized conditions could be established under moderate molasses wastewater dilution, (e.g. 45%), at 3.5 h treatment time and 33 mA/cm(2) current density. Copyright © 2015 Elsevier Ltd. All rights reserved.

Mechanical Abrasion as a Low Cost Technique for Contamination-Free Sample Acquisition from a Category IVA Clean Platform

NASA Technical Reports Server (NTRS)

Dolgin, B.; Yarbrough, C.; Carson, J.; Troy, R.

2000-01-01

The proposed Mars Sample Transfer Chain Architecture provides Planetary Protection Officers with clean samples that are required for the eventual release from confinement of the returned Martian samples. At the same time, absolute cleanliness and sterility requirement is not placed of any part of the Lander (including the deep drill), Mars Assent Vehicle (MAV), any part of the Orbiting Sample container (OS), Rover mobility platform, any part of the Minicorer, Robotic arm (including instrument sensors), and most of the caching equipment on the Rover. The removal of the strict requirements in excess of the Category IVa cleanliness (Pathfinder clean) is expected to lead to significant cost savings. The proposed architecture assumes that crosscontamination renders all surfaces in the vicinity of the rover(s) and the lander(s) contaminated. Thus, no accessible surface of Martian rocks and soil is Earth contamination free. As a result of the latter, only subsurface samples (either rock or soil) can be and will be collected for eventual return to Earth. Uncontaminated samples can be collected from a Category IVa clean platform. Both subsurface soil and rock samples can be maintained clean if they are collected by devices that are self-contained and clean and sterile inside only. The top layer of the sample is removed in a manner that does not contaminate the collection tools. Biobarrier (e.g., aluminum foil) covering the moving parts of these devices may be used as the only self removing bio-blanket that is required. The samples never leave the collection tools. The lids are placed on these tools inside the collection device. These single use tools with the lid and the sample inside are brought to Earth in the OS. The lids have to be designed impenetrable to the Earth organisms. The latter is a well established art.

Microwave-induced activation of additional active edge sites on the MoS2 surface for enhanced Hg0 capture

NASA Astrophysics Data System (ADS)

Zhao, Haitao; Mu, Xueliang; Yang, Gang; Zheng, Chengheng; Sun, Chenggong; Gao, Xiang; Wu, Tao

2017-10-01

In recent years, significant effort has been made in the development of novel materials for the removal of mercury from coal-derived flue gas. In this research, microwave irradiation was adopted to induce the creation of additional active sites on the MoS2 surface. The results showed that Hg0 capture efficiency of the adsorbent containing MoS2 nanosheets being microwave treated was as high as 97%, while the sample prepared via conventional method only showed an efficiency of 94% in its first 180 min testing. After the adsorbent was treated by microwave irradiation for 3 more times, its mercury removal efficiency was still noticeably higher than that of the sample prepared via conventional method. Characterization of surface structure of the MoS2 containing material together with DFT study further revealed that the (001) basal planes of MoS2 crystal structure were cracked into (100) edge planes (with an angle of approximately 75°) under microwave treatment, which subsequently resulted in the formation of additional active edge sites on the MoS2 surface and led to the improved performance on Hg0 capture.

Ultrafiltration and nanofiltration membrane fouling by natural organic matter: Mechanisms and mitigation by pre-ozonation and pH.

PubMed

Yu, Wenzheng; Liu, Teng; Crawshaw, John; Liu, Ting; Graham, Nigel

2018-08-01

The fouling of ultrafiltration (UF) and nanofiltration (NF) membranes during the treatment of surface waters continues to be of concern and the particular role of natural organic matter (NOM) requires further investigation. In this study the effect of pH and surface charge on membrane fouling during the treatment of samples of a representative surface water (Hyde Park recreational lake) were evaluated, together with the impact of pre-ozonation. While biopolymers in the surface water could be removed by the UF membrane, smaller molecular weight (MW) fractions of NOM were poorly removed, confirming the importance of membrane pore size. For NF membranes the removal of smaller MW fractions (800 Da-10 kDa) was less than expected from their pore size; however, nearly all of the hydrophobic, humic-type substances could be removed by the hydrophilic NF membranes for all MW distributions (greater than 90%). The results indicated the importance of the charge and hydrophilic nature of the NOM. Thus, the hydrophilic NF membrane could remove the hydrophobic organic matter, but not the hydrophilic substances. Increasing charge effects (more negative zeta potentials) with increasing solution pH were found to enhance organics removal and reduce fouling (flux decline), most likely through greater membrane surface repulsion. Pre-ozonation of the surface water increased the hydrophilic fraction and anionic charge of NOM and altered their size distributions. This resulted in a decreased fouling (less flux decline) for the UF and smaller pore NF, but a slight increase in fouling for the larger pore NF. The differences in the NF behavior are believed to relate to the relative sizes of ozonated organic fractions and the NF pores; a similar size of ozonated organic fractions and the NF pores causes significant membrane fouling. Copyright © 2018 The Authors. Published by Elsevier Ltd.. All rights reserved.

Description, dissection, and subsampling of Apollo 14 core sample 14230

NASA Technical Reports Server (NTRS)

Fryxell, R.; Heiken, G.

1971-01-01

Core sample 14230, collected at Triplet Crater near the Fra Mauro landing site of the Apollo 14 mission, was dissected in greater detail than any previous core. Sediment from the actual lunar surface was missing, and 6.7 grams of sediment were removed from the base of the core for a portion of the biotest prime sample. Upper and lower portions of the original 70.7-gram core (12.5 centimeters long) were fractured excessively but not mixed stratigraphically. Three major morphologic units and 11 subdivisions were recognized. Dissection provided 55 subsamples in addition to three others made by removing longitudinal sections of the core impregnated with n-butyl methacrylate for use as a permanent documentary record and for studies requiring particles of known orientation.

Decontaminating Solar Wind Samples with the Genesis Ultra-Pure Water Megasonic Wafer Spin Cleaner

NASA Technical Reports Server (NTRS)

Calaway, Michael J.; Rodriquez, M. C.; Allton, J. H.; Stansbery, E. K.

2009-01-01

The Genesis sample return capsule, though broken during the landing impact, contained most of the shattered ultra-pure solar wind collectors comprised of silicon and other semiconductor wafers materials. Post-flight analysis revealed that all wafer fragments were littered with surface particle contamination from spacecraft debris as well as soil from the impact site. This particulate contamination interferes with some analyses of solar wind. In early 2005, the Genesis science team decided to investigate methods for removing the surface particle contamination prior to solar wind analysis.

Effects of orbital exposure on Halar during the LDEF mission

NASA Technical Reports Server (NTRS)

Brower, William E., Jr.; Holla, Harish; Bauer, Robert A.

1992-01-01

Thermomechanical Analysis (TMA), Differential Scanning Calorimetry (DSC), and Thermogravimetric Analysis (TGA) were performed on samples of Halar exposed on the LDEF Mission for 6 years in orbit and unexposed Halar control samples. Sections 10-100 microns thick were removed from the exposed surface down to a depth of 1,000 microns through the 3 mm thick samples. The TMA and DSC results, which arise from the entire slice and not just its surface, showed no differences between the LDEF and the control samples. TMA scans were run from ambient to 300 C; results were compared by a tabulation of the glass transition temperatures. DSC scans were run from ambient to 700 C; the enthalpy of melting was compared for the samples as a function of section depth with the sample. The TGA results, which arise from the surface of the sample initially, showed a sharp increase in the topmost 50 micron section (the exposed, discolored side) in the weight loss of 170 C in oxygen. This weight loss dropped to bulk values in the range of depth of 50-200 microns. The control sample showed only a slight increase in weight loss as the top surface was approached. The LDEF Halar sample appears to be mechanically undamaged, with a surface layer which oxidizes faster as a result of orbital exposure.

Application of magnetic ionomer for development of very fast and highly efficient uptake of triazo dye Direct Blue 71 form different water samples.

PubMed

Khani, Rouhollah; Sobhani, Sara; Beyki, Mostafa Hossein; Miri, Simin

2018-04-15

This research focuses on removing Direct Blue 71 (DB 71) from aqueous solution in an efficient and very fast route by ionic liquid mediated γ-Fe 2 O 3 magnetic ionomer. 2-hydroxyethylammonium sulphonate immobilized on γ-Fe 2 O 3 nanoparticles (γ-Fe 2 O 3 -2-HEAS) was used for this purpose. The influence of shaking time, medium pH, the concentration of sorbent and NaNO 3 on removal was evaluated to greatly influence removal extent. The optimal removal conditions were determined by response surface methodology based on the four-variable central composite design to obtain maximum removal efficiency and determine the significance and interaction effect of the variables on the removal of target triazo dye. The results have shown that an amount of 98.2% as % removal under the optimum conditions. The adsorption kinetics and isotherms were well fitted to a pseudo-second order model and Freundlich model, respectively. Based on these models, the maximum dye adsorption capacity (Q m ) of 47.60mgg -1 was obtained. Finally, the proposed nano-adsorbent was applied satisfactorily for removal of target triazo dye from different water samples. Copyright © 2017 Elsevier Inc. All rights reserved.

A Study of an Optical Lunar Surface Communications Network with High Bandwidth Direct to Earth Link

NASA Technical Reports Server (NTRS)

Wilson, K.; Biswas, A.; Schoolcraft, J.

2011-01-01

A lunar surface systems study explores the application of optical communications to support a high bandwidth data link from a lunar relay satellite and from fixed lunar assets. The results show that existing 1-m ground stations could provide more than 99% coverage of the lunar terminal at 100Mb/s data rates from a lunar relay satellite and in excess of 200Mb/s from a fixed terminal on the lunar surface. We have looked at the effects of the lunar regolith and its removal on optical samples. Our results indicate that under repeated dust removal episodes sapphire rather than fused silica would be a more durable material for optical surfaces. Disruption tolerant network protocols can minimize the data loss due to link dropouts. We report on the preliminary results of the DTN protocol implemented over the optical carrier.

Image simulation and surface reconstruction of undercut features in atomic force microscopy

NASA Astrophysics Data System (ADS)

Qian, Xiaoping; Villarrubia, John; Tian, Fenglei; Dixson, Ronald

2007-03-01

CD-AFMs (critical dimension atomic force microscopes) are instruments with servo-control of the tip in more than one direction. With appropriately "boot-shaped" or flared tips, such instruments can image vertical or even undercut features. As with any AFM, the image is a dilation of the sample shape with the tip shape. Accurate extraction of the CD requires a correction for the tip effect. Analytical methods to correct images for the tip shape have been available for some time for the traditional (vertical feedback only) AFMs, but were until recently unavailable for instruments with multi-dimensional feedback. Dahlen et al. [J. Vac. Sci. Technol. B23, pp. 2297-2303, (2005)] recently introduced a swept-volume approach, implemented for 2-dimensional (2D) feedback. It permits image simulation and sample reconstruction, techniques previously developed for the traditional instruments, to be extended for the newer tools. We have introduced [X. Qian and J. S. Villarrubia, Ultramicroscopy, in press] an alternative dexel-based method, that does the same in either 2D or 3D. This paper describes the application of this method to sample shapes of interest in semiconductor manufacturing. When the tip shape is known (e.g., by prior measurement using a tip characterizer) a 3D sample surface may be reconstructed from its 3D image. Basing the CD measurement upon such a reconstruction is shown here to remove some measurement artifacts that are not removed (or are incompletely removed) by the existing measurement procedures.

Surface science analysis of GaAs photocathodes following sustained electron beam delivery

DOE Office of Scientific and Technical Information (OSTI.GOV)

Carlos Hernandez-Garcia, Fay Hannon, Marcy Stutzman, V. Shutthanandan, Z. Zhu, M. Nandasri, S. V. Kuchibhatla, S. Thevuthasan, W. P. Hess

2012-06-01

Degradation of the photocathode materials employed in photoinjectors represents a challenge for sustained operation of nuclear physics accelerators and high power Free Electron Lasers (FEL). Photocathode quantum efficiency (QE) degradation is due to residual gasses in the electron source vacuum system being ionized and accelerated back to the photocathode. These investigations are a first attempt to characterize the nature of the photocathode degradation, and employ multiple surface and bulk analysis techniques to investigate damage mechanisms including sputtering of the Cs-oxidant surface monolayer, other surface chemistry effects, and ion implantation. Surface and bulk analysis studies were conducted on two GaAs photocathodes,more » which were removed from the JLab FEL DC photoemission gun after delivering electron beam, and two control samples. The analysis techniques include Helium Ion Microscopy (HIM), Rutherford Backscattering Spectrometry (RBS), Atomic Force Microscopy (AFM) and Secondary Ion Mass Spectrometry (SIMS). In addition, two high-polarization strained superlattice GaAs photocathode samples, one removed from the Continuous Electron Beam Accelerator Facility (CEBAF) photoinjector and one unused, were also analyzed using Transmission Electron Microscopy (TEM) and SIMS. It was found that heat cleaning the FEL GaAs wafer introduces surface roughness, which seems to be reduced by prolonged use. The bulk GaAs samples retained a fairly well organized crystalline structure after delivering beam but shows evidence of Cs depletion on the surface. Within the precision of the SIMS and RBS measurements the data showed no indication of hydrogen implantation or lattice damage from ion back bombardment in the bulk GaAs wafers. In contrast, SIMS and TEM measurements of the strained superlattice photocathode show clear crystal damage in the wafer from ion back bombardment.« less

DOE Office of Scientific and Technical Information (OSTI.GOV)

Paik, Samuel Y.; Epperson, Patrick M.; Kasper, Kenneth M.

Here, this article presents air and surface sampling data collected over the first two years since beryllium was introduced as a target material at the National Ignition Facility. Over this time, 101 experiments with beryllium-containing targets were executed. The data provides an assessment of current conditions in the facility and a baseline for future impacts as new, reduced regulatory limits for beryllium are being proposed by both the Occupational Safety and Health Administration and Department of Energy. This study also investigates how beryllium deposits onto exposed surfaces as a result of x-ray vaporization and the effectiveness of simple decontamination measuresmore » in reducing the amount of removable beryllium from a surface. Based on 1,961 surface wipe samples collected from entrant components (equipment directly exposed to target debris) and their surrounding work areas during routine reconfiguration activities, only one result was above the beryllium release limit of 0.2 µg/100 cm 2 and 27 results were above the analytical reporting limit of 0.01 µg/100 cm 2, for a beryllium detection rate of 1.4%. Surface wipe samples collected from the internal walls of the NIF target chamber, however, showed higher levels of beryllium, with beryllium detected on 73% and 87% of the samples during the first and second target chamber entries (performed annually), respectively, with 23% of the samples above the beryllium release limit during the second target chamber entry. The analysis of a target chamber wall panel exposed during the first 30 beryllium-containing experiments (cumulatively) indicated that 87% of the beryllium contamination remains fixed onto the surface after wet wiping the surface and 92% of the non-fixed contamination was removed by decontaminating the surface using a dry wipe followed by a wet wipe. Personal airborne exposures assessed during access to entrant components and during target chamber entry indicated that airborne beryllium was not present in workers' breathing zones. Finally, all the data thus far have shown that beryllium has been effectively managed to prevent exposures to workers during routine and non-routine work.« less

USGS/EPA collection protocol for bacterial pathogens in soil

USGS Publications Warehouse

Griffin, Dale W.; Shaefer, F.L.; Charlena Bowling,; Dino Mattorano,; Tonya Nichols,; Erin Silvestri,

2014-01-01

This Sample Collection Procedure (SCP) describes the activities and considerations for the collection of bacterial pathogens from representative surface soil samples (0-5 cm). This sampling depth can be reached without the use of a drill rig, direct-push technology, or other mechanized equipment. This procedure can be used in most soil types but is limited to sampling at or near the ground surface. This protocol has components for two different types of sampling applications: (1) typical sampling, when there is no suspicion of contamination (e.g., surveillance or background studies); and (2) in response to known or suspected accidental contamination (e.g., the presence of animal carcasses). This protocol does not cover sampling in response to a suspected bioterrorist or intentional release event. Surface material is removed to the required depth (0-5 cm) and clean trowel or 50 ml sample tube is used to collect the sample. Sample containers are sealed, bagged, and shipped to the laboratory for analysis. Associated documentation, including a Field Data Log and Chain-of-Custody are also included in this document.

Spectrometry and filtering with high rejection of stray light

DOEpatents

Ferrell, Thomas L.; Thundat, Thomas G.

2004-12-14

A microoptoelectromechanical integrated spectrometer with a photonic element assembly having metal foil removably disposed on a first transparent substrate surface, the substrate having no foil on any other surface. A means is provided for directing source photons that are reflected from or transmitted through a sample, over a range of angles of incidence, into the transparent substrate and onto the metal foil such that source photons are incident at the Brewsters angle. A means is also provided for detecting an induced exponential field in the metal foil. A means is also provided for relating the induced exponential field to a known exponential field for the sample and determining the identity of the sample. The spectrometer performs ultraviolet-to-visible-to-infrared spectroscopy using photon tunneling and surface plasmon excitation.

On the measurement of austenite in supermartensitic stainless steel by X-ray diffraction

DOE Office of Scientific and Technical Information (OSTI.GOV)

Tolchard, Julian Richard, E-mail: tolchard@material.ntnu.no; Sømme, Astri; Solberg, Jan Ketil

2015-01-15

Sections of a 13Cr supermartensitic stainless steel were investigated to determine the optimum sample preparation for measurement of the austenite content by X-ray diffraction. The surface of several samples was mechanically ground or polished using media of grit sizes in the range 1–120 μm. The strained surface layer was afterwards removed stepwise by electropolishing, and the austenite content measured at each step. It was found that any level of mechanical grinding or polishing results in a reduction of the measured austenite fraction relative to the true bulk value, and that coarser grinding media impart greater damage and greater reduction inmore » the measured austenite content. The results thus highlight the importance of the electropolishing step in preparation of such samples, but suggest that the American Society for Testing and Materials standard E975-03 substantially overestimates the amount of material which needs to be removed to recover the true “bulk” content. - Highlights: • Quantitative Rietveld analysis of austenite/martensite ratio in supermartensitic stainless steels • Critical evaluation of sample preparation for residual austenite measurements by X-ray diffraction • Highlighting of the importance of electropolishing as a final preparation step.« less

Highly efficient removal of pathogenic bacteria with magnetic graphene composite.

PubMed

Zhan, Sihui; Zhu, Dandan; Ma, Shuanglong; Yu, Wenchao; Jia, Yanan; Li, Yi; Yu, Hongbing; Shen, Zhiqiang

2015-02-25

Magnetic Fe3O4/graphene composite (abbreviated as G-Fe3O4) was synthesized successfully by solvothermal method to effectively remove both bacteriophage and bacteria in water, which was tested by HRTEM, XRD, BET, XPS, FTIR, CV, magnetic property and zeta-potential measurements. Based on the result of HRTEM, the single-sheet structure of graphene oxide and the monodisperse Fe3O4 nanoparticles on the surface of graphene can be observed obviously. The G-Fe3O4 composite were attractive for removing a wide range of pathogens including not only bacteriophage ms2, but also various bacteria such as S. aureus, E. coli, Salmonella, E. Faecium, E. faecalis, and Shigella. The removal efficiency of E. coli for G-Fe3O4 composite can achieve 93.09%, whereas it is only 54.97% with pure Fe3O4 nanoparticles. Moreover, a detailed verification test of real water samples was conducted and the removal efficiency of bacteria in real water samples with G-Fe3O4 composite can also reach 94.8%.

Preparation and performance study of MgFe2O4/metal-organic framework composite for rapid removal of organic dyes from water

NASA Astrophysics Data System (ADS)

Tian, Huairu; Peng, Jun; Lv, Tingting; Sun, Chen; He, Hua

2018-01-01

In present study, a stable and magnetic metal-organic framework (MOF) material was synthesized by simple solvothermal method as adsorbent to rapid removal of two organic dyes, the Rhodamine B (RB) and Rhodamine 6G (Rh6G), in water samples. The prepared material showed great characteristics of large surface area (519.86 m2 g-1), excellent magnetic responsivity (35.00 emu g-1) and rapid removal (within 5 min). Maximum adsorption capacities of the magnetic material toward RB and Rh6G were up to 219.78 and 306.75 mg g-1, respectively. Adsorption kinetics suggested the adsorption process met the pseudo-second-order kinetic model. The prepared material could be reused at least 10 times by washing with acetonitrile solution, the relative standard deviation (RSD) of these ten cycles removal efficiency was 4.8%. In conclusion, good chemical inertness, a mechanical/water stability and super-hydrophilicity feature made this MOF a promising adsorbent for targets removal from environmental water sample.

Removal of polychlorinated naphthalenes by desulfurization and emissions of polychlorinated naphthalenes from sintering plant

PubMed Central

Wang, Mengjing; Liu, Wenbin; Hou, Meifang; Li, Qianqian; Han, Ying; Liu, Guorui; Li, Haifeng; Liao, Xiao; Chen, Xuebin; Zheng, Minghui

2016-01-01

The sintering flue gas samples were collected at the inlets and outlets of the desulfurization systems to evaluate the influence of the systems on PCNs emission concentrations, profiles, and emission factors. The PCNs concentrations at the inlets and outlets were 27888–153672 pg m−3 and 11988–42245 pg m−3,respectively. Desulfurization systems showed excellent removal for PCNs, and the removal efficiencies of PCNs increase with increasing chlorination level. Lower chlorinated homologs are more sensitive to the desulfurization process than higher ones. High levels of PCNs were also detected in the gypsum (11600–29720 pg g−1) and fly ash samples (4946–64172 pg g−1). The annual total emissions of PCNs released to flue gas and gypsum from the sintering plants were about 394 kg, 48.5% of which was in gypsum. The surface area of the fly ash samples increased significantly from the first to the fourth stage of the series-connected electrostatic precipitator, accompanying obvious rising of concentration of PCNs in the fly ash samples. PMID:27197591

Ion beam figuring of high-slope surfaces based on figure error compensation algorithm.

PubMed

Dai, Yifan; Liao, Wenlin; Zhou, Lin; Chen, Shanyong; Xie, Xuhui

2010-12-01

In a deterministic figuring process, it is critical to guarantee high stability of the removal function as well as the accuracy of the dwell time solution, which directly influence the convergence of the figuring process. Hence, when figuring steep optics, the ion beam is required to keep a perpendicular incidence, and a five-axis figuring machine is typically utilized. In this paper, however, a method for high-precision figuring of high-slope optics is proposed with a linear three-axis machine, allowing for inclined beam incidence. First, the changing rule of the removal function and the normal removal rate with the incidence angle is analyzed according to the removal characteristics of ion beam figuring (IBF). Then, we propose to reduce the influence of varying removal function and projection distortion on the dwell time solution by means of figure error compensation. Consequently, the incident ion beam is allowed to keep parallel to the optical axis. Simulations and experiments are given to verify the removal analysis. Finally, a figuring experiment is conducted on a linear three-axis IBF machine, which proves the validity of the method for high-slope surfaces. It takes two iterations and about 9 min to successfully figure a fused silica sample, whose aperture is 21.3 mm and radius of curvature is 16 mm. The root-mean-square figure error of the convex surface is reduced from 13.13 to 5.86 nm.

Pharmaceuticals and personal care products (PPCPs) in surface and treated waters of Louisiana, USA and Ontario, Canada.

PubMed

Boyd, Glen R; Reemtsma, Helge; Grimm, Deborah A; Mitra, Siddhartha

2003-07-20

A newly developed analytical method was used to measure concentrations of nine pharmaceuticals and personal care products (PPCPs) in samples from two surface water bodies, a sewage treatment plant effluent and various stages of a drinking water treatment plant in Louisiana, USA, and from one surface water body, a drinking water treatment plant and a pilot plant in Ontario, Canada. The analytical method provides for simultaneous extraction and quantification of the following broad range of PPCPs and endocrine-disrupting chemicals: naproxen; ibuprofen; estrone; 17beta-estradiol; bisphenol A; clorophene; triclosan; fluoxetine; and clofibric acid. Naproxen was detected in Louisiana sewage treatment plant effluent at 81-106 ng/l and Louisiana and Ontario surface waters at 22-107 ng/l. Triclosan was detected in Louisiana sewage treatment plant effluent at 10-21 ng/l. Of the three surface waters sampled, clofibric acid was detected in Detroit River water at 103 ng/l, but not in Mississippi River or Lake Pontchartrain waters. None of the other target analytes were detected above their method detection limits. Based on results at various stages of treatment, conventional drinking-water treatment processes (coagulation, flocculation and sedimentation) plus continuous addition of powdered activated carbon at a dosage of 2 mg/l did not remove naproxen from Mississippi River waters. However, chlorination, ozonation and dual media filtration processes reduced the concentration of naproxen below detection in Mississippi River and Detroit River waters and reduced clofibric acid in Detroit River waters. Results of this study demonstrate that existing water treatment technologies can effectively remove certain PPCPs. In addition, our study demonstrates the importance of obtaining data on removal mechanisms and byproducts associated with PPCPs and other endocrine-disrupting chemicals in drinking water and sewage treatment processes.

Decontamination of clothing and building materials associated with the clandestine production of methamphetamine.

PubMed

Serrano, Kate A; Martyny, John W; Kofford, Shalece; Contreras, John R; Van Dyke, Mike V

2012-01-01

This study was designed to determine how easily methamphetamine can be removed from clothing and building materials, utilizing different cleaning materials and methods. The study also addressed the penetration of methamphetamine into drywall and the ability of paints to encapsulate the methamphetamine on drywall. Clothing and building materials were contaminated in a stainless steel chamber by aerosolizing methamphetamine in a beaker heater. The amount of methamphetamine surface contamination was determined by sampling a grid pattern on the material prior to attempting to clean the materials. After cleaning, the materials were again sampled, and the degree of decontamination noted. We found that household clothing and response gear worn by first responders was easily decontaminated using a household detergent in a household washing machine. A single wash removed over 95% of the methamphetamine from these materials. The study also indicated that methamphetamine-contaminated, smooth non-porous surfaces can be easily cleaned to below detectable levels using only mild cleaners. More porous surfaces such as plywood and drywall were unlikely to be decontaminated to below regulatory levels even with three washes using a mild cleaner. This may be due to methamphetamine penetration into the paint on these surfaces. Evaluation of methamphetamine contamination on drywall indicated that approximately 40% of the methamphetamine was removed using a wipe, while another 60% remained in the paint layer. Stronger cleaners such as those with active ingredients including sodium hypochlorite or quaternary ammonia and commercial decontamination agents were more effective than mild detergent-based cleaners and may reduce methamphetamine contamination to below regulatory levels. Results from the encapsulation studies indicate that sprayed on oil-based paint will encapsulate methamphetamine on drywall and plywood surfaces up to 4.5 months, while latex paints were less effective.

Effect of CO₂ flow rate on the Pinang frond-based activated carbon for methylene blue removal.

PubMed

Herawan, S G; Ahmad, M A; Putra, A; Yusof, A A

2013-01-01

Activated carbons are regularly used the treatment of dye wastewater. They can be produced from various organics materials having high level of carbon content. In this study, a novel Pinang frond activated carbon (PFAC) was produced at various CO₂ flow rates in the range of 150-600 mL/min at activation temperature of 800°C for 3 hours. The optimum PFAC sample is found on CO₂ flow rate of 300 mL/min which gives the highest BET surface area and pore volume of 958 m²/g and 0.5469 mL/g, respectively. This sample shows well-developed pore structure with high fixed carbon content of 79.74%. The removal of methylene blue (MB) by 95.8% for initial MB concentration of 50 mg/L and 72.6% for 500 mg/L is achieved via this sample. The PFAC is thus identified to be a suitable adsorbent for removing MB from aqueous solution.

Dimerization Products of Chloroprene are Background Contaminants Emitted from ALTEF (Polyvinylidene Difluoride) Gas Sampling Bags.

PubMed

Kwak, Jae; Fan, Maomian; Martin, Jennifer A; Ott, Darrin K; Grigsby, Claude C

2017-01-01

Gas sampling bags have been used for collecting air samples. Tedlar bags are most commonly used, but bleed background chemicals such as N,N-dimethylacetamide and phenol. It is often necessary to remove the contaminant by flushing the bags with pure nitrogen or air. In this study, we identified four chloroprene dimerization products as background contaminants emitted from ALTEF bags that are made of a proprietary polyvinylidene difluoride (PVDF). No monomer chloroprene was detected in the bags analyzed. All of the dimers gradually increased once bags were filled with nitrogen due to diffusion from the bag surface. Flushing the bags with nitrogen reduced their concentrations, but was not effective for removing the contaminants. When the bags that had been flushed with nitrogen 5 times were left for 24 h, they increased again, indicating that the dimers were constantly emitted from the ALTEF bag surface. To our knowledge, these compounds have never been demonstrated in ALTEF or other PVDF bags. Our finding indicates that ALTEF might be incorporated with Neoprene (chloroprene-based polymer) during its manufacturing process.

Development of activated carbon derived from banana peel for CO{sub 2} removal

DOE Office of Scientific and Technical Information (OSTI.GOV)

Borhan, Azry; Thangamuthu, Subhashini; Ramdan, Amira Nurain

This research work highlights on the constraints involved in the preparation of the banana peel bio-sorbent, such as impregnation ratio, activation temperature and period of activation for reducing carbon dioxide (CO{sub 2}) in the atmosphere. Micromeritics ASAP 2020 and Field Emission Scanning Electron Microscope (FESEM) were used in identifying the best sample preparation method with the largest surface area which directly contributes to the effectiveness of adsorbent in removing CO{sub 2}. Sample A10 was identified to yield activated carbon with the largest surface area (260.3841 m{sup 2}/g), total pore volume (0.01638 cm{sup 3}/g) and pore diameter (0.2508 nm). Through nitrogen adsorption-desorption isothermmore » analysis, the existence of sub-micropores was proven when a combination of Type-I and Type-II isotherms were exhibited by the activated carbon produced. The results from the final adsorption test found that the material synthesized from the above mentioned parameter is capable of removing up to 1.65% wt of CO{sub 2} through adsorption at 25°C, suggesting that it can be effectively used as an adsorption material.« less

A new technique for Auger analysis of surface species subject to electron-induced desorption.

NASA Technical Reports Server (NTRS)

Pepper, S. V.

1973-01-01

A method is presented to observe surface species subject to electron-induced desorption by Auger electron spectroscopy. The surface to be examined is moved under the electron beam at constant velocity, establishing a time-independent condition and eliminating the time response of the electron spectrometer as a limiting factor. The dependence of the Auger signal on the sample velocity, incident electron current, beam diameter, and desorption cross section is analyzed. It is shown that it is advantageous to analyze the moving sample with a high beam current, in contrast to the usual practice of using a low beam current to minimize desorption from a stationary sample. The method is illustrated by the analysis of a friction transfer film of PTFE, in which the fluorine is removed by electron-induced desorption. The method is relevant to surface studies in the field of lubrication and catalysis.

Scalable free energy calculation of proteins via multiscale essential sampling

NASA Astrophysics Data System (ADS)

Moritsugu, Kei; Terada, Tohru; Kidera, Akinori

2010-12-01

A multiscale simulation method, "multiscale essential sampling (MSES)," is proposed for calculating free energy surface of proteins in a sizable dimensional space with good scalability. In MSES, the configurational sampling of a full-dimensional model is enhanced by coupling with the accelerated dynamics of the essential degrees of freedom. Applying the Hamiltonian exchange method to MSES can remove the biasing potential from the coupling term, deriving the free energy surface of the essential degrees of freedom. The form of the coupling term ensures good scalability in the Hamiltonian exchange. As a test application, the free energy surface of the folding process of a miniprotein, chignolin, was calculated in the continuum solvent model. Results agreed with the free energy surface derived from the multicanonical simulation. Significantly improved scalability with the MSES method was clearly shown in the free energy calculation of chignolin in explicit solvent, which was achieved without increasing the number of replicas in the Hamiltonian exchange.

Mechanism of nitrogen removal in wastewater lagoon: a case study.

PubMed

Vendramelli, Richard A; Vijay, Saloni; Yuan, Qiuyan

2017-06-01

Ammonia being a nutrient facilitates the growth of algae in wastewater and causes eutrophication. Nitrate poses health risk if it is present in drinking water. Hence, nitrogen removal from wastewater is required. Lagoon wastewater treatment systems have become common in Canada these days. The study was conducted to understand the nitrogen removal mechanisms from the existing wastewater treatment lagoon system in the town of Lorette, Manitoba. The lagoon system consists of two primary aerated cells and two secondary unaerated cells. Surface samples were collected periodically from lagoon cells and analysed from 5 May 2015 to 9 November 2015. The windward and leeward sides of the ponds were sampled and the results were averaged. It was found that the free ammonia volatilization to the atmosphere is responsible for most of the ammonia removal. Ammonia and nitrate assimilation into biomass and biological growth in the cells appears to be the other mechanisms of nitrogen removal over the monitoring period. Factors affecting the nitrogen removal efficiency were found to be pH, temperature and hydraulic residence time. Also, the ammonia concentration in the effluent from the wastewater treatment lagoon was compared with the regulatory standard.

Removal of pollutants with determination of power consumption from landfill leachate wastewater using an electrocoagulation process: optimization using response surface methodology (RSM)

NASA Astrophysics Data System (ADS)

Asaithambi, Perumal; Beyene, Dejene; Aziz, Abdul Raman Abdul; Alemayehu, Esayas

2018-05-01

Treatment of landfill leachate wastewater by electrocoagulation process using an aluminium electrode was investigated in a batch electrochemical cell reactor. Response surface methodology based on central composite design was used to optimize the operating parameters for the removal of % color and % total organic carbon (TOC) together with power consumption from landfill leachate. Effects of three important independent parameters such as current density ( X 1), inter-electrode distance ( X 2) and solution pH ( X 3) of the landfill leachate sample on the % color and % TOC removal with power consumption were investigated. A quadratic model was used to predict the % color and % TOC removal with power consumption in different experimental conditions. The significance of each independent variable was calculated by analysis of variance. In order to achieve the maximum % color and % TOC removal with minimum of power consumption, the optimum conditions were about current density ( X 1)—5.25 A/dm2, inter-electrode distance ( X 2)—1 cm and initial solution of effluent pH ( X 3)—7.83, with the yield of color removal of 74.57%, and TOC removal of 51.75% with the power consumption of 14.80 kWh/m3. Electrocoagulation process could be applied to remove pollutants from industrial effluents and wastewater.

Chemical mechanisms of photocatalytic de-soiling and de-polluting processes in indoor environments and urban surfaces

NASA Astrophysics Data System (ADS)

Sleiman, M.; Rosseler, O.; Montesinos, N.; Litter, M.; Bikiel, D.; Kirchstetter, T.; Bluhm, H.; Ahmed, M.; Salmeron, M.; Destaillats, H.

2013-12-01

Photocatalysis has been postulated as a promising approach for the de-pollution of indoor air and urban atmospheres, and for self-cleaning surfaces. Building materials and coatings containing nano-sized TiO2 photocatalytic functionalities are gaining market share, including self-cleaning building envelope materials (coatings, mortar, plaster, architectural fabrics and tiles) and indoor air purifiers. While many studies have reported good performance of photocatalysis in the removal of organic pollutants from indoor air, more information is needed to understand secondary emissions of potentially harmful byproducts from photocatalytic air cleaners. This presentation will describe analytical methods and experimental results from room-sized chamber experiments using a realistic challenge VOC mixture at low ppb levels. We will also present results from separate studies that used synchrotron-based surface spectroscopic and mass spectrometric methods to better understand the photocatalytic mechanisms that regulate the de-soiling and de-polluting activity. Two photocatalytic processes were studied: de-noxification (NOx removal) and de-soiling (removal of deposited black carbon or soot). Ambient pressure XPS was used to study surface and gas-phase species formed during adsorption of NO2 on TiO2 and subsequent UV irradiation at λ = 365 nm. The results illustrate how NOx chemistry on TiO2 surfaces can be affected by the presence of water vapor, heteroatoms present as impurities, and carbonaceous soiling. The reactivity of NOx and NO3- on surfaces leads to reduced adsorbed and gas-phase nitrogenated species. These processes need to be considered in the engineering of depolluting materials and incorporated into atmospheric models. De-soiling properties were investigated by analyzing soot oxidation on TiO2 surfaces. Model soot samples were used as surrogates of urban grime. Using laser desorption coupled with time-of-flight (TOF) mass spectrometry synchrotron ionization, we investigated the mechanisms of photocatalytic soot removal under UVA irradiation. Ancillary reflectance measurements were performed to determine the efficiency and kinetics of soot removal.

Additive Manufacturing for Superalloys - Producibility and Cost Validation (Preprint)

DTIC Science & Technology

2011-03-01

evaluated in this study were: Shaped Metal Deposition (SMD, 3D Weld Deposition) Laser Powder Deposition (LPD) Electron Beam Wire Deposition (EBWD...envelope and would be removed during subsequent machining. Radiographic inspection also revealed fine random internal micro porosity in some of the...successfully fabricated the required deposition samples for Task 2 (see Figure 4). A surface examination revealed some surface cracks and porosity , but all

Analysis of leading edge and trailing edge cover glass samples before and after treatment with advanced satellite contamination removal techniques

NASA Technical Reports Server (NTRS)

Hotaling, S. P.

1993-01-01

Two samples from Long Duration Exposure Facility (LDEF) experiment M0003-4 were analyzed for molecular and particulate contamination prior to and following treatment with advanced satellite contamination removal techniques (CO2 gas/solid jet spray and oxygen ion beam). The pre- and post-cleaning measurements and analyses are presented. The jet spray removed particulates in seconds. The low energy reactive oxygen ion beam removed 5,000 A of photo polymerized organic hydrocarbon contamination in less than 1 hour. Spectroscopic analytical techniques were applied to the analysis of cleaning efficiency including: Fourier transform infrared, Auger, x ray photoemissions, energy dispersive x ray, and ultraviolet/visible. The results of this work suggest that the contamination studied here was due to spacecraft self-contamination enhanced by atomic oxygen plasma dynamics and solar UV radiation. These results also suggest the efficacy for the jet spray and ion beam contamination control technologies for spacecraft optical surfaces.

Application of statistical experimental methodology to optimize bioremediation of n-alkanes in aquatic environment.

PubMed

Zahed, Mohammad Ali; Aziz, Hamidi Abdul; Mohajeri, Leila; Mohajeri, Soraya; Kutty, Shamsul Rahman Mohamed; Isa, Mohamed Hasnain

2010-12-15

Response surface methodology (RSM) was employed to optimize nitrogen and phosphorus concentrations for removal of n-alkanes from crude oil contaminated seawater samples in batch reactors. Erlenmeyer flasks were used as bioreactors; each containing 250 mL dispersed crude oil contaminated seawater, indigenous acclimatized microorganism and different amounts of nitrogen and phosphorus based on central composite design (CCD). Samples were extracted and analyzed according to US-EPA protocols using a gas chromatograph. During 28 days of bioremediation, a maximum of 95% total aliphatic hydrocarbons removal was observed. The obtained Model F-value of 267.73 and probability F<0.0001 implied the model was significant. Numerical condition optimization via a quadratic model, predicted 98% n-alkanes removal for a 20-day laboratory bioremediation trial using nitrogen and phosphorus concentrations of 13.62 and 1.39 mg/L, respectively. In actual experiments, 95% removal was observed under these conditions. Copyright © 2010 Elsevier B.V. All rights reserved.

Effect of Atmospheric Pressure Plasma Treatment on Surface Characteristics and Adhesive Bond Quality of Peel Ply Prepared Composites

NASA Astrophysics Data System (ADS)

Tracey, Ashley C.

The purpose of this research was to investigate if atmospheric pressure plasma treatment could modify peel ply prepared composite surfaces to create strong adhesive bonds. Two peel ply surface preparation composite systems previously shown to create weak bonds (low fracture energy and adhesion failure) that were potential candidates for plasma treatment were Toray T800/3900-2 carbon fiber reinforced polymer (CFRP) prepared with Precision Fabrics Group, Inc. (PFG) 52006 nylon peel ply and Hexcel T300/F155 CFRP prepared with PFG 60001 polyester peel ply. It was hypothesized that atmospheric pressure plasma treatment could functionalize and/or remove peel ply remnants left on the CFRP surfaces upon peel ply removal. Surface characterization measurements and double cantilever beam (DCB) testing were used to determine the effects of atmospheric pressure plasma treatment on surface characteristics and bond quality of peel ply prepared CFRP composites. Previous research showed that Toray T800/3900-2 carbon fiber reinforced epoxy composites prepared with PFG 52006 peel ply and bonded with Cytec MetlBond 1515-3M structural film adhesive failed in adhesion at low fracture energies when tested in the DCB configuration. Previous research also showed that DCB samples made of Hexcel T300/F155 carbon fiber reinforced epoxy composites prepared with PFG 60001 peel ply and bonded with Henkel Hysol EA 9696 structural film adhesive failed in adhesion at low fracture energies. Recent research suggested that plasma treatment could be able to activate these "un-bondable" surfaces and result in good adhesive bonds. Nylon peel ply prepared 177 °C cure and polyester peel ply prepared 127 °C cure CFRP laminates were treated with atmospheric pressure plasma after peel ply removal prior to bonding. Atmospheric pressure plasma treatment was capable of significantly increasing fracture energies and changing failure modes. For Toray T800/3900-2 laminates prepared with PFG 52006 and bonded with MetlBond 1515-3M, plasma treatment increased fracture energies from 460 J/m 2. Atmospheric pressure plasma treatment also increased fracture energies of Hexcel T300/F155 laminates prepared with PFG 60001 and bonded with EA 9696 from 1500 J/m2. It was demonstrated that atmospheric pressure plasma treatment was able to transform poor bonding surfaces into acceptable ones by reversing the negative effects of incorrect peel ply usage. To determine if the primary reason for adhesion was functionalization or removal, a number of experiments were performed. Surface characteristics of peel ply only and plasma treated samples were determined using contact angle (CA) measurements, FTIR spectroscopy, X-ray photoelectron spectroscopy (XPS), and scanning electron microscopy (SEM). CA was used to assess solid surface energy that was useful to determine wetting of the adhesive on the adherend, one requirement of adhesion. FTIR and XPS were used to analyze composite surface chemistry, including the identification of functional groups that were a product of atmospheric pressure plasma treatment, as well as contaminants that can inhibit adhesive bonding. SEM was used to capture surface morphology to identify peel ply remnants and whether these remnants were physically removed or modified due to plasma treatment. This research supported that atmospheric pressure plasma treatment resulted in adhesion primarily due to functionalization of peel ply remnants, though a removal mechanism was not disproven. It was also shown that surface energy exhibited potential for predicting adhesion. Lastly, this research indicated that plasma treatment is a robust surface preparation, as strong bonds were observed up to 30 days after treatment.

Mercury removal from coal combustion flue gas by modified fly ash.

PubMed

Xu, Wenqing; Wang, Hairui; Zhu, Tingyu; Kuang, Junyan; Jing, Pengfei

2013-02-01

Fly ash is a potential alternative to activated carbon for mercury adsorption. The effects of physicochemical properties on the mercury adsorption performance of three fly ash samples were investigated. X-ray fluorescence spectroscopy, X-ray photoelectron spectroscopy, and other methods were used to characterize the samples. Results indicate that mercury adsorption on fly ash is primarily physisorption and chemisorption. High specific surface areas and small pore diameters are beneficial to efficient mercury removal. Incompletely burned carbon is also an important factor for the improvement of mercury removal efficiency, in particular. The C-M bond, which is formed by the reaction of C and Ti, Si and other elements, may improve mercury oxidation. The samples modified with CuBr2, CuCl2 and FeCl3 showed excellent performance for Hg removal, because the chlorine in metal chlorides acts as an oxidant that promotes the conversion of elemental mercury (Hg0) into its oxidized form (Hg2+). Cu2+ and Fe3+ can also promote Hg0 oxidation as catalysts. HCl and O2 promote the adsorption of Hg by modified fly ash, whereas SO2 inhibits the Hg adsorption because of competitive adsorption for active sites. Fly ash samples modified with CuBr2, CuCl2 and FeCl3 are therefore promising materials for controlling mercury emissions.

Effect of Na+ impregnated activated carbon on the adsorption of NH4(+)-N from aqueous solution.

PubMed

Shi, Mo; Wang, Zhengfang; Zheng, Zheng

2013-08-01

Two kinds of activated carbons modified by Na+ impregnation after pre-treatments involving oxidation by nitric acid or acidification by hydrochloric acid (denoted as AC/N-Na and AC/HCl-Na, respectively), were used as adsorbents to remove NH4(+)-N. The surface features of samples were investigated by BET, SEM, XRD and FT-IR. The adsorption experiments were conducted in equilibrium and kinetic conditions. Influencing factors such as initial solution pH and initial concentration were investigated. A possible mechanism was proposed. Results showed that optimal NH4(+)-N removal efficiency was achieved at a neutral pH condition for the modified ACs. The Langmuir isotherm adsorption equation provided a better fit than other models for the equilibrium study. The adsorption kinetics followed both the pseudo second-order kinetics model and intra-particle kinetic model. Chemical surface analysis indicated that Na+ ions form ionic bonds with available surface functional groups created by pre-treatment, especially oxidation by nitric acid, thus increasing the removal efficiency of the modified ACs for NH4(+)-N. Na(+)-impregnated ACs had a higher removal capability in removing NH4(+)-N than unmodified AC, possibly resulting from higher numbers of surface functional groups and better intra-particle diffusion. The good fit of Langmuir isotherm adsorption to the data indicated the presence of monolayer NH4(+)-N adsorption on the active homogenous sites within the adsorbents. The applicability of pseudo second-order and intra-particle kinetic models revealed the complex nature of the adsorption mechanism. The intra-particle diffusion model revealed that the adsorption process consisted not only of surface adsorption but also intra-particle diffusion.

Comparison of methods for the removal of organic carbon and extraction of chromium, iron and manganese from an estuarine sediment standard and sediment from the Calcasieu River estuary, Louisiana, U.S.A.

USGS Publications Warehouse

Simon, N.S.; Hatcher, S.A.; Demas, C.

1992-01-01

U.S. National Bureau of Standards (NBS) estuarine sediment 1646 from the Chesapeake Bay, Maryland, and surface sediment collected at two sites in the Calcasieu River estuary, Louisiana, were used to evaluate the dilute hydrochloric acid extraction of Cr, Fe and Mn from air-dried and freeze-dried samples that had been treated by one of three methods to remove organic carbon. The three methods for the oxidation and removal of organic carbon were: (1) 30% hydrogen peroxide; (2) 30% hydrogen peroxide plus 0.25 mM pyrophosphate; and (3) plasma oxidation (low-temperature ashing). There was no statistically significant difference at the 95% confidence level between air- and freeze-dried samples with respect to the percent of organic carbon removed by the three methods. Generally, there was no statistically significant difference at the 95% confidence level between air- and freeze-dried samples with respect to the concentration of Cr, Fe and Mn that was extracted, regardless of the extraction technique that was used. Hydrogen peroxide plus pyrophosphate removed the most organic carbon from sediment collected at the site in the Calcasieu River that was upstream from industrial outfalls. Plasma oxidation removed the most organic carbon from the sediment collected at a site in the Calcasieu River close to industrial outfalls and from the NBS estuarine sediment sample. Plasma oxidation merits further study as a treatment for removal of organic carbon. Operational parameters can be chosen to limit the plasma oxidation of pyrite which, unlike other Fe species, will not be dissolved by dilute hydrochloric acid. Preservation of pyrite allows the positive identification of Fe present as pyrite in sediments. ?? 1992.

Ion beam machining error control and correction for small scale optics.

PubMed

Xie, Xuhui; Zhou, Lin; Dai, Yifan; Li, Shengyi

2011-09-20

Ion beam figuring (IBF) technology for small scale optical components is discussed. Since the small removal function can be obtained in IBF, it makes computer-controlled optical surfacing technology possible to machine precision centimeter- or millimeter-scale optical components deterministically. Using a small ion beam to machine small optical components, there are some key problems, such as small ion beam positioning on the optical surface, material removal rate, ion beam scanning pitch control on the optical surface, and so on, that must be seriously considered. The main reasons for the problems are that it is more sensitive to the above problems than a big ion beam because of its small beam diameter and lower material ratio. In this paper, we discuss these problems and their influences in machining small optical components in detail. Based on the identification-compensation principle, an iterative machining compensation method is deduced for correcting the positioning error of an ion beam with the material removal rate estimated by a selected optimal scanning pitch. Experiments on ϕ10 mm Zerodur planar and spherical samples are made, and the final surface errors are both smaller than λ/100 measured by a Zygo GPI interferometer.

Preparation of dumbbell manganese dioxide/gelatin composites and their application in the removal of lead and cadmium ions.

PubMed

Wang, Xiu; Huang, Kai; Chen, Ying; Liu, Jiafa; Chen, Shan; Cao, Jianlei; Mei, Surong; Zhou, Yikai; Jing, Tao

2018-05-15

The nano-sized sorbents restrict their practical application in flow-through system due to excessive pressure. In this study, dumbbell MnO 2 /gelatin composites were synthesized based on the protein-assisted synthesis technology. Then they were immobilized on the amino-modified polymethyl methacrylate (PMMA) plate. SEM, TEM, XRD, XPS and FT-IR were employed to study the surface properties and the adsorption mechanism of MnO 2 /gelatin composites. Adsorption experiments for Pb(II) and Cd(II) ions were performed to study the adsorption isotherms, kinetics, and thermodynamics as well as the influencing factors. The maximum adsorption capacities of Pb(II) and Cd(II) ions were 318.7 mg g -1 and 105.1 mg g -1 respectively. The adsorption process met the pseudo-second-order kinetic model. Subsequently, MnO 2 /gelatin composites modified plates were used to remove the heavy metal ions in surface water and wastewater samples. The removal efficiencies of Pb(II) ion was changed from 83% (wastewater) to 100% (surface water), when the initial concentration was 10 mg L -1 . This device exhibited great application prospect in the removal of heavy metals taking advantage of its high removal efficiency, excellent stability and reusability and ease of operation. Copyright © 2018 Elsevier B.V. All rights reserved.

3D scanning electron microscopy applied to surface characterization of fluorosed dental enamel.

PubMed

Limandri, Silvina; Galván Josa, Víctor; Valentinuzzi, María Cecilia; Chena, María Emilia; Castellano, Gustavo

2016-05-01

The enamel surfaces of fluorotic teeth were studied by scanning electron stereomicroscopy. Different whitening treatments were applied to 25 pieces to remove stains caused by fluorosis and their surfaces were characterized by stereomicroscopy in order to obtain functional and amplitude parameters. The topographic features resulting for each treatment were determined through these parameters. The results obtained show that the 3D reconstruction achieved from the SEM stereo pairs is a valuable potential alternative for the surface characterization of this kind of samples. Copyright © 2016 Elsevier Ltd. All rights reserved.

Far-field optical imaging with subdiffraction resolution enabled by nonlinear saturation absorption

NASA Astrophysics Data System (ADS)

Ding, Chenliang; Wei, Jingsong

2016-01-01

The resolution of far-field optical imaging is required to improve beyond the Abbe limit to the subdiffraction or even the nanoscale. In this work, inspired by scanning electronic microscopy (SEM) imaging, in which carbon (or Au) thin films are usually required to be coated on the sample surface before imaging to remove the charging effect while imaging by electrons. We propose a saturation-absorption-induced far-field super-resolution optical imaging method (SAI-SRIM). In the SAI-SRIM, the carbon (or Au) layers in SEM imaging are replaced by nonlinear-saturation-absorption (NSA) thin films, which are directly coated onto the sample surfaces using advanced thin film deposition techniques. The surface fluctuant morphologies are replicated to the NSA thin films, accordingly. The coated sample surfaces are then imaged using conventional laser scanning microscopy. Consequently, the imaging resolution is greatly improved, and subdiffraction-resolved optical images are obtained theoretically and experimentally. The SAI-SRIM provides an effective and easy way to achieve far-field super-resolution optical imaging for sample surfaces with geometric fluctuant morphology characteristics.

Thermal management of VECSELs by front surface direct liquid cooling

NASA Astrophysics Data System (ADS)

Smyth, Conor J. C.; Mirkhanov, Shamil; Quarterman, Adrian H.; Wilcox, Keith G.

2016-03-01

Efficient thermal management is vital for VECSELs, affecting the output power and several aspects of performance of the device. Presently there exist two distinct methods of effective thermal management which both possess their merits and disadvantages. Substrate removal of the VECSEL gain chip has proved a successful method in devices emitting at a wavelength near 1μm. However for other wavelengths the substrate removal technique has proved less effective primarily due to the thermal impedance of the distributed Bragg reflectors. The second method of thermal management involves the use of crystalline heat spreaders bonded to the gain chip surface. Although this is an effective thermal management scheme, the disadvantages are additional loss and the etalon effect that filters the gain spectrum, making mode locking more difficult and normally resulting in multiple peaks in the spectrum. There are considerable disadvantages associated with both methods attributed to heatspreader cost and sample processing. It is for these reasons that a proposed alternative, front surface liquid cooling, has been investigated in this project. Direct liquid cooling involves flowing a temperature-controlled liquid over the sample's surface. In this project COMSOL was used to model surface liquid cooling of a VECSEL sample in order to investigate and compare its potential thermal management with current standard thermal management techniques. Based on modelling, experiments were carried out in order to evaluate the performance of the technique. While modelling suggests that this is potentially a mid-performance low cost alternative to existing techniques, experimental measurements to date do not reflect the performance predicted from modelling.

SPARCLE: Electrostatic Dust Control Tool Proof of Concept

NASA Technical Reports Server (NTRS)

Clark, P. E.; Curtis, S. A.; Minetto, F.; Marshall, J.; Nuth, J.; Calle, C.

2010-01-01

Successful exploration of most planetary surfaces, with their impact-generated dusty regoliths, will depend on the capabilities to keep surfaces free of the performance-compromising dust. Once in contact with surfaces, whether set in motion by natural or mechanical means, regolith fines, or dust, behave like abrasive Velcro, coating surfaces, clogging mechanisms, making movement progressively more difticult, and being almost impossible to remove by mechanical mcans (brushing). The successful dust removal strategy will deal with dust dynamics resulting from interaction between Van der Waals and Coulombic forces. Here, proof of concept for an electrostatically-based concept for dust control tool is described and demonstrated. A low power focused electron beam is used in the presence of a small electrical field to increase the negative charge to mass ratio of a dusty surface until dust repulsion and attraction to a lower potential surface, acting as a dust collector, occurred. Our goal is a compact device of less than 5 kg mass and using less than 5 watts of power to be operational in less than 5 years with heritage from ionic sweepers for active spacecraft potential control (e.g ., on POLAR). Rovers could be fitted with devices that could hamess the removal of dust for sampling as part of the extended exploration process on Mercury, Mars, asteroids or outer solar system satellites, as well as the Moon.

Investigation of a Potential Protective Mechanism Against Heparin-Induced Thrombocytopenia in Patients on Chronic Intermittent Hemodialysis

PubMed Central

Tanhehco, Yvette C.; Cuker, Adam; Rudnick, Michael; Sachais, Bruce S.

2015-01-01

BACKGROUND Heparin-induced thrombocytopenia (HIT) develops as a result of platelet (PLT) activation by anti-platelet factor 4 (PF4)/heparin complex antibodies. Despite repeated exposure to heparin, patients undergoing chronic intermittent hemodialysis (HD) rarely develop HIT. We investigated the possibility that HD decreases/removes PF4 from PLT surfaces and/or plasma, thereby disfavoring immune complex formation as a mechanism of protection against HIT. MATERIALS AND METHODS We enrolled 20 patients undergoing chronic HD at the Penn Presbyterian Medical Center. Blood samples were drawn before, during and after treatment in the presence and absence of heparin. PF4, PF4/heparin antibody, heparin, and P-selectin levels were measured. RESULTS No patients demonstrated clinical symptoms of HIT. PLT surface PF4 levels decreased and plasma PF4 levels increased concurrently with increase in plasma heparin concentration. In the absence of heparin, PLT surface and plasma PF4 levels were unchanged. Anti-PF4/heparin antibodies, which were non-functional by the serotonin release assay, were detectable in 8 patients. PLT surface P-selectin levels did not change during treatment. CONCLUSIONS Removal of PLT surface and/or plasma PF4 as a mechanism of protection against HIT in patients undergoing HD is not supported by the results of our study, although the transient decrease in PLT surface PF4 in the presence of large amounts of heparin remains a candidate mechanism. The small sample size, single type of dialyzer membrane, and early sampling time points may have led to the inability to detect changes in PF4 levels. Future studies should explore other potential protective mechanisms. PMID:23305841

Adsorption and removal of arsenic (V) using crystalline manganese (II,III) oxide: Kinetics, equilibrium, effect of pH and ionic strength.

PubMed

Babaeivelni, Kamel; Khodadoust, Amid P; Bogdan, Dorin

2014-01-01

Manganese (II,III) oxide (Mn3O4) crystalline powder was evaluated as a potential sorbent for removal of arsenic (V) from water. Adsorption isotherm experiments were carried out to determine the adsorption capacity using de-ionized (DI) water, a synthetic solution containing bicarbonate alkalinity, and two natual groundwater samples. Adsorption isotherm data followed the Langmuir and Freundlich equations, indicating favorable adsorption of arsenic (V) onto Mn3O4, while results from the Dubinin-Radushkevich equation were suggestive of chemisorption of arsenic (V). When normalized to the sorbent surface area, the maximum adsorption capacity of Mn3O4 for arsenic (V) was 101 μg m(-2), comparable to that of activated alumina. Arsenic (V) adsorption onto Mn3O4 followed pseudo-second-order kinetics. Adsorption of arsenic (V) was greatest at pH 2, while adsorption at pH 7-9 was within 91% of maximum adsorption, whereas adsorption decreased to 32% of maximum adsorption at pH 10. Surface charge analysis confirmed the adsorption of arsenic (V) onto the acidic surface of the Mn3O4 sorbent with a pHPZC of 7.32. The presence of coexisting ions bicarbonate and phosphate resulted in a decrease in arsenic (V) uptake. Comparable adsorption capacities were obtained for the synthetic solution and both groundwater samples. Overall, crystalline Mn3O4 was an effective and viable sorbent for removal of arsenic (V) from natural water, removing greater than 95% of arsenic (V) from a 1 mg L(-1) solution within 60 min of contact time.

Final report: survey and removal of radioactive surface contamination at environmental restoration sites, Sandia National Laboratories/New Mexico. Volume 2

DOE Office of Scientific and Technical Information (OSTI.GOV)

Lambert, K.A.; Mitchell, M.M.; Jean, D.

1997-09-01

This report contains the Appendices A-L including Voluntary Corrective Measure Plans, Waste Management Plans, Task-Specific Health and Safety Plan, Analytical Laboratory Procedures, Soil Sample Results, In-Situ Gamma Spectroscopy Results, Radionuclide Activity Summary, TCLP Soil Sample Results, Waste Characterization Memoranda, Waste Drum Inventory Data, Radiological Risk Assessment, and Summary of Site-Specific Recommendations.

The possibility of multi-layer nanofabrication via atomic force microscope-based pulse electrochemical nanopatterning

NASA Astrophysics Data System (ADS)

Kim, Uk Su; Morita, Noboru; Lee, Deug Woo; Jun, Martin; Park, Jeong Woo

2017-05-01

Pulse electrochemical nanopatterning, a non-contact scanning probe lithography process using ultrashort voltage pulses, is based primarily on an electrochemical machining process using localized electrochemical oxidation between a sharp tool tip and the sample surface. In this study, nanoscale oxide patterns were formed on silicon Si (100) wafer surfaces via electrochemical surface nanopatterning, by supplying external pulsed currents through non-contact atomic force microscopy. Nanoscale oxide width and height were controlled by modulating the applied pulse duration. Additionally, protruding nanoscale oxides were removed completely by simple chemical etching, showing a depressed pattern on the sample substrate surface. Nanoscale two-dimensional oxides, prepared by a localized electrochemical reaction, can be defined easily by controlling physical and electrical variables, before proceeding further to a layer-by-layer nanofabrication process.

Scanning electron microscopy investigation of PMMA removal by laser irradiation (Er:YAG) in comparison with an ultrasonic system and curettage in hip joint revision arthroplasty.

PubMed

Birnbaum, Klaus; Gutknecht, Norbert

2010-07-01

The cement often left in the femur socket during hip joint revision arthroplasty is usually removed by curettage. Another method for removing the cement is to use an ultrasonic system, and yet another alternative may be to use a laser system. The aim of these investigations was to determine the pulse rate and pulse energy of the Er:YAG laser for sufficient cement ablation. We also compared the results obtained using the laser with those obtained using an ultrasonic device or curettage by histological and scanning electron microscopy (SEM) investigation of the border zone between the polymethyl methacrylate (PMMA) and unfixed specimens of femoral bone. Therefore we prepared 30 unfixed human femur stems after hip joint replacement and prepared ten sagittal sections from each femur stem (in total 300 sections). Of these 300 specimens, 180 were treated with the Er:YAG laser, 60 with the ultrasonic system and 60 by curettage. The high pulse energy of 500 mJ and a pulse rate of 4 Hz provided the highest PMMA ablation rate, although the boundary surface between PMMA and femoral bone was not as fine-grained as found in samples treated at 15 Hz and 250 mJ. However, the treatment time for the same cement ablation rate with the latter settings was twice that at 4 Hz and 500 mJ. Compared to the boundary surfaces treated with the ultrasonic device or curettage, the laser-treated samples had a more distinct undifferentiated boundary surface between PMMA and femoral bone. After development of the Er:YAG-laser to provide higher pulse energies, it may in the future be an additional efficient method for the removal of PMMA in revision arthroplasty. The Er:YAG laser should be combined with an endoscopic and a rinsing suction system so that PMMA can be removed from the femoral shaft under direct vision.

NIOSH comments to DOL on the Occupational Safety and Health Administration's proposed rule on occupational exposure to asbestos, tremolite, anthophyllite, and actinolite by J. D. Millar, April 26, 1991

DOE Office of Scientific and Technical Information (OSTI.GOV)

Not Available

1991-04-26

The testimony contains the comments of NIOSH regarding the proposed rule on occupational exposure to asbestos (1332214), tremolite (14567738), anthophyllite (17068789), and actinolite (77536664). The testimony included a memorandum comparing NIOSH Method 7400 to OSHA Method ID 160, an evaluation of glove bag containment in asbestos removal, the limit of detection that was ascertained from the sampling strategies for three sets of samples, effectiveness of periodic cleaning of surfaces with a HEPA vacuum, an update on cancer mortality among chrysotile (12001295) asbestos miners, and the use of hand tools to remove built up roofing.

Monitoring the prevalence of nitrosamines in South African waters and their removal using cyclodextrin polyurethanes

NASA Astrophysics Data System (ADS)

Mhlongo, Sthembile H.; Mamba, Bhekie B.; Krause, Rui W.

The prevalence of nitrosamines, especially N-nitrosodimethylamine (NDMA), was monitored in three South African water supplies. NDMA a disinfection by-product (DBP) and potent carcinogen, has recently been detected in many drinking water supplies internationally. Besides direct industrial or human-derived contamination, nitrosodimethylamine can be formed through a chemical reaction between monochloroamine and an organic based compound such as dimethylamine which is frequently detected in surface water. It has been suggested that chloramination of surface waters with a high concentration of dissolved organic carbon (DOC) could result in elevated NDMA formation. Growing evidence suggests that NDMA occurs more frequently and at higher concentrations in drinking water systems that practise chloramination compared to systems that use chlorination. In gauging the extent of water contamination by nitrosamines in water distribution systems, especially NDMA, water samples collected from three different water treatment plants that practise chemical drinking water disinfection were qualitatively analysed for the presence of nitrosamines. Solid phase microextraction (SPME) was employed in the extraction of nitrosamines from the water samples and gas chromatography-mass spectrometry (GC-MS), was used in the analysis of the water samples. Trace amounts of NDMA were detected at one of the water treatment plants and in the distribution network. The application of water-insoluble cyclodextrin (CD) polymers in the removal of nitrosamines and potential amine precursors from the water samples was tested. Quantitative removal of NDMA (based on peak area) from the water samples was achieved which suggests that in the water treatment train the use of these nanosponges can be applied in the mitigation of trace contaminants such as NDMA.

Sample Preservation - The Key to a Successful Failure Analysis

DTIC Science & Technology

2008-09-01

Acidic Lemon Juice 3 Acidic Vinegar 4 Acidic Tomatoes 5 Acidic Human Skin 6 Acidic Milk 7 Neutral 8 Alkaline Sea Water 9 Alkaline Baking Soda...subsequently removed with alcohol when fractography is performed, although problems may exist with rough fracture surfaces. For these surfaces, a...cleaning Loosely adhering debris and dust Least Organic-solvent cleaning in ultrasonic bath  Toluene or xylene  Ketones  Alcohol  Oil and

Tribological dry sliding behavior of chopped carbon fiber reinforced polyetheretherketone

NASA Astrophysics Data System (ADS)

Chumaevskii, A. V.; Ivanov, A. N.; Filippov, A. V.; Rubtsov, V. E.; Kolubaev, E. A.

2017-12-01

Tribological tests on 3D printed pure polyetheretherketone and carbon fiber reinforced polyetheretherketone samples were carried out. The negative effect of carbon fiber sticking out of the matrix on wear and sliding process stability was revealed. These fibers may be too long and oriented to the worn surface in a manner that prevents their removal by wear so that the worn surface becomes irregular and the sliding process instable.

Ion beam methods applied to interior ballistic studies

DOE Office of Scientific and Technical Information (OSTI.GOV)

Niler, A.

1981-04-01

High temperature, pressure and velocity gases produced during the interior ballistic cycle of a gun firing are responsible for considerable damage to the steel surfaces of a gun bore. This damage is studied by exposing steel samples to the erosive flows of burning propellant gases in a modified 37mm gun chamber where pressures of 200 MPa and flame temperatures of 3000/sup 0/K are typical. Ion beam methods are used to characterize the composition of the steel surfaces by combined nuclear reaction (NR) and elastic backscattering (EBS) analysis and thin layer activation (TLA) is used to measure surface wear rates. Combinedmore » fits to the EBS and NR distributions yield concentrations and depth profiles of carbon, nitrogen and oxygen as well as iron and other heavier elements. Hydrogen concentrations have also been measured on some of the samples. The results of these experiments show the presence of two different erosion mechanisms. In one, the surface is softened by thermo-chemical processes prior to removal by the shear forces of the gas flow while in the other surface layer melting occurs prior to removal. TLA using the /sup 56/Fe(p,n)/sup 56/Co reaction has been used to measure wear from a 20 mm barrel and is being instrumented for larger barrels. EBS is being used to characterize the interfaces between steel substrates and coatings designed to reduce erosion.« less

Box/peanut and bar structures in edge-on and face-on nearby galaxies in the Sloan Digital Sky Survey - I. Catalogue

NASA Astrophysics Data System (ADS)

Yoshino, Akira; Yamauchi, Chisato

2015-02-01

We investigate box/peanut and bar structures in image data of edge-on and face-on nearby galaxies taken from the Sloan Digital Sky Survey (SDSS) to present catalogues containing the surface brightness parameters and the morphology classification. About 1700 edge-on galaxies and 2600 face-on galaxies are selected from SDSS DR7 in the g, r and i-bands. The images of each galaxy are fitted with the model of two-dimensional surface brightness of the Sérsic bulge and exponential disk. After removing some irregular data, the box/peanut, bar and other structures are easily distinguished by eye using residual (observed minus model) images. We find 292 box/peanut structures in the 1329 edge-on samples and 630 bar structures in 1890 face-on samples in the i-band, after removing some irregular data. The fraction of box/peanut galaxies is about 22 per cent against the edge-on samples, and that of bar galaxies is about 33 per cent (about 50 per cent if 629 elliptical galaxies are removed) against the face-on samples. Furthermore the strengths of the box/peanuts and bars are evaluated as strong, standard or weak. We find that the strength increases slightly with increasing B/T (bulge-to-total flux ratio), and that the fraction of box/peanuts is generally about a half of that of bars, irrespective of the strength and B/T. Our result supports the idea that a box/peanut is a bar seen edge-on.

Performance assessment of pilot horizontal sub-surface flow constructed wetlands for removal of diesel from wastewater by Scirpus grossus.

PubMed

Al-Baldawi, Israa Abdulwahab; Sheikh Abdullah, Siti Rozaimah; Anuar, Nurina; Suja, Fatihah; Idris, Mushrifah

2013-01-01

One of the appropriate development technology options for the treatment of wastewater contaminated with diesel is constructed wetlands (CWs). Throughout 72 days of exposure, sampling was carried out for monitoring of physical parameters, plant growth and the efficiency of total petroleum hydrocarbon (TPH) removal, as an indication for diesel contamination, to assess the pilot-scale performance. Four pilot CWs with a horizontal sub-surface flow system were applied using the bulrush of Scirpus grossus. The CWs were loaded with different diesel concentrations of 0, 0.1, 0.2 and 0.25% (Vdiesel/Vwater). The TPH removal efficiencies were 82, 71, and 67% at the end of 72 days for diesel concentrations of 0.1, 0.2, and 0.25% respectively. In addition, the high removal efficiency of total suspended solids and chemical oxygen demand (COD) were 100 and 75.4% respectively, for a diesel concentration of 0.1%. It was concluded that S. grossus is a potential plant that can be used in a well-operated CW for restoring 0.1% diesel-contaminated water.

Root surface temperature variation during mechanical removal of root canal filling material. An in vitro study.

PubMed

García-Cuerva, Martín; Horvath, Lucía; Pinasco, Laura; Ciparelli, Verónica; Gualtieri, Ariel; Casadoumecq, Ana C; Rodríguez, Pablo; Gonzalez-Zanotto, Carlos

2017-04-01

The aim of this study was to analyze in vitro temperature changes on the outer surface of the dental root during mechanical filling removal procedures. Thirty recently extracted single-rooted lower premolars were cut transversally at 16 mm from the apex in order to standardize sample length. Endodontic treatment was performed on them. The filling material was subsequently removed using Gates Glidden (G1, G2, G3); Peeso (P1, P2, P3) and PostecPlus FRC (FRC) reamers while temperatures were measured on the outer surface using a digital device with thermocouple at 0, 2, 4, 6, 8, 10 and 15 seconds. Temperatures were compared using repeated measures ANOVA followed by pairwise comparison with Tukey's test. All reamers caused significant temperature variation between different times (p<0.05). Pairwise comparisons indicated that temperature increased with time for all reamers (p<0.05). Significant differences in temperature were found between different reamers after 0, 2, 4, 6, 8,10 and 15 seconds (p<0.05). Temperature at the root surface increased considerably. Values higher than 50°C were recorded, the greatest increase from baseline being 16°C. Accordingly, if the procedure were begun at 37°C (physiological temperature), the temperature in the surrounding tissues - cementum, periodontium and bone - would rise to 53°C. An increase in 10°C above body temperature at the root surface may cause lesions in surrounding tissues. While removing filling material, it is essential to cool, control action time and use instruments in perfect condition, all of which may contribute to reducing the heat generated and transmitted to the outer root surface. Sociedad Argentina de Pediatría.

Adsorption and photocatalytic degradation of pharmaceuticals and pesticides by carbon doped-TiO2 coated on zeolites under solar light irradiation.

PubMed

An, Ye; de Ridder, David Johannes; Zhao, Chun; Schoutteten, Klaas; Bussche, Julie Vanden; Zheng, Huaili; Chen, Gang; Vanhaecke, Lynn

2016-01-01

To evaluate the performance of zeolite-supported carbon-doped TiO(2) composite catalysts toward target pollutants under solar light irradiation, the adsorption and photocatalytic degradation of 18 pharmaceuticals and pesticides with distinguishing features (molecular size and volume, and photolysis) were investigated using mordenite zeolites with SiO(2)/Al(2)O(3) ratios of 18 and 240. Different quantities of carbon-doped TiO(2) were coated on the zeolites, and then the finished composite catalysts were tested in demineralized, surface, and hospital wastewater samples, respectively. The composite photocatalysts were characterized by X-ray diffraction, field emission scanning electron microscopy, and surface area and porosity analyses. Results showed that a dispersed layer of carbon-doped TiO(2) is formed on the zeolite surface; this layer blocks the micropores of zeolites and reduces their surface area. However, these reductions did not significantly affect adsorption onto the zeolites. Our results demonstrated that zeolite-supported carbon-doped TiO(2) systems can effectively degrade 18 pharmaceuticals and pesticides in demineralized water under natural and simulated solar light irradiation. In surface and hospital wastewaters, zeolite-supported carbon-doped TiO(2) systems present excellent anti-interference capability against radical scavengers and competitive organics for pollutants removal, and higher pollutants adsorption on zeolites evidently enhances the removal rate of target pollutants in surface and hospital wastewater samples with a complicated matrix.

Laser cleaning of steel for paint removal

NASA Astrophysics Data System (ADS)

Chen, G. X.; Kwee, T. J.; Tan, K. P.; Choo, Y. S.; Hong, M. H.

2010-11-01

Paint removal is an important part of steel processing for marine and offshore engineering. For centuries, a blasting techniques have been widely used for this surface preparation purpose. But conventional blasting always has intrinsic problems, such as noise, explosion risk, contaminant particles, vibration, and dust. In addition, processing wastes often cause environmental problems. In recent years, laser cleaning has attracted much research effort for its significant advantages, such as precise treatment, and high selectivity and flexibility in comparison with conventional cleaning techniques. In the present study, we use this environmentally friendly technique to overcome the problems of conventional blasting. Processed samples are examined with optical microscopes and other surface characterization tools. Experimental results show that laser cleaning can be a good alternative candidate to conventional blasting.

Genesis Solar Wind Sample 61422: Experiment in Variation of Sequence of Cleaning Solvent for Removing Carbon-Bearing Contamination

NASA Technical Reports Server (NTRS)

Allton, J. H.; Kuhlman, K. R.; Allums, K. K.; Gonzalez, C. P.; Jurewicz, A. J. G.; Burnett, D. S.; Woolum, D. S.

2015-01-01

The recovered Genesis collector fragments are heavily contaminated with crash-derived particulate debris. However, megasonic treatment with ultra-pure-water (UPW; resistivity (is) greater than18 meg-ohm-cm) removes essentially all particulate contamination greater than 5 microns in size [e.g.1] and is thus of considerable importance. Optical imaging of Si sample 60336 revealed the presence of a large C-rich particle after UPW treatment that was not present prior to UPW. Such handling contamination is occasionally observed, but such contaminants are normally easily removed by UPW cleaning. The 60336 particle was exceptional in that, surprisingly, it was not removed by additional UPW or by hot xylene or by aqua regia treatment. It was eventually removed by treatment with NH3-H2O2. Our best interpretation of the origin of the 60336 particle was that it was adhesive from the Post-It notes used to stabilize samples for transport from Utah after the hard landing. It is possible that the insoluble nature of the 60336 particle comes from interaction of the Post-It adhesive with UPW. An occasional bit of Post-It adhesive is not a major concern, but C particulate contamination also occurs from the heat shield of the Sample Return Capsule (SRC) and this is mixed with inorganic contamination from the SRC and the Utah landing site. If UPW exposure also produced an insoluble residue from SRC C, this would be a major problem in chemical treatments to produce clean surfaces for analysis. This paper reports experiments to test whether particulate contamination was removed more easily if UPW treatment was not used.

Adsorption of basic Red 46 using sea mango (Cerbera odollam) based activated carbon

NASA Astrophysics Data System (ADS)

Azmi, Nur Azira Iqlima; Zainudin, Nor Fauziah; Ali, Umi Fazara Md

2015-05-01

Sea mango or Cerbera Odollam is another source of carbonaceous material that can be found abundantly in Malaysia. In this research, it is used as a new agricultural source of activated carbon. Sea mango activated carbon was prepared by chemical activation using potassium hydroxide (KOH). The sea mango was soaked in KOH at impregnation ratio of 1:1 and followed by carbonization at temperature of 600°C for 1 hour. The sample was then characterized using Scanning Electron Microscope (SEM) for surface morphology, while Brunauer-Emmett-Teller (BET) was used to study the surface area. The result shown that sea mango activated carbon (SMAC) developed new pores on its surface and the BET surface area measured was 451.87 m2/g. The SMAC performance was then tested for the removal of Basic Red 46 in batch process. The removal of Basic Red 46 (50 mg/L, natural pH, 0.1 g SMAC) was more than 99% in 15 minutes where it reached equilibrium in 30 minutes.

Post-processing of fused silica and its effects on damage resistance to nanosecond pulsed UV lasers.

PubMed

Ye, Hui; Li, Yaguo; Zhang, Qinghua; Wang, Wei; Yuan, Zhigang; Wang, Jian; Xu, Qiao

2016-04-10

HF-based (hydrofluoric acid) chemical etching has been a widely accepted technique to improve the laser damage performance of fused silica optics and ensure high-power UV laser systems at designed fluence. Etching processes such as acid concentration, composition, material removal amount, and etching state (etching with additional acoustic power or not) may have a great impact on the laser-induced damage threshold (LIDT) of treated sample surfaces. In order to find out the effects of these factors, we utilized the Taguchi method to determine the etching conditions that are helpful in raising the LIDT. Our results show that the most influential factors are concentration of etchants and the material etched away from the viewpoint of damage performance of fused silica optics. In addition, the additional acoustic power (∼0.6  W·cm^-2) may not benefit the etching rate and damage performance of fused silica. Moreover, the post-cleaning procedure of etched samples is also important in damage performances of fused silica optics. Different post-cleaning procedures were, thus, experiments on samples treated under the same etching conditions. It is found that the "spraying + rinsing + spraying" cleaning process is favorable to the removal of etching-induced deposits. Residuals on the etched surface are harmful to surface roughness and optical transmission as well as laser damage performance.

Endocrine disrupting chemicals in New Orleans surface waters and Mississippi Sound sediments.

PubMed

Wang, Guangdi; Ma, Peng; Zhang, Qiang; Lewis, John; Lacey, Michelle; Furukawa, Yoko; O'Reilly, S E; Meaux, Shelley; McLachlan, John; Zhang, Shaoyuan

2012-05-01

Endocrine disrupting compounds (EDCs), represented by steroid hormones, organochlorine pesticides (OCPs), polychlorinated biphenyls (PCBs), and bisphenol A have been determined in four sediment cores from the Gulf of Mexico, from New Orleans surface water (Lake Pontchartrain and Mississippi River), and from the influent and effluent of a New Orleans municipal sewage treatment plant. During the five-month monitoring of selected EDCs in the Mississippi River (MR) and Lake Pontchartrain (LP) in 2008, 21 of 29 OCPs in MR and 17 of 29 OCPs in LP were detected; bisphenol A was detected in all of the samples. Steroid hormones (estrone, 17β-estradiol and 17α-ethinylestradiol) were detected occasionally. Total EDC (OCPs + PCBs + steroid hormones + bisphenol A) concentrations in the two surface water samples were found to vary from 148 to 1112 ng L(-1). Strong correlation of the distribution of total OCPs, total PCBs and total EDCs between solid and water phases was found in LP, while moderate or no correlation existed in MR. OCPs, PCBs, steroid hormones, and bisphenol A were all detected in the ocean sediments, and total EDCs were measured in the range of 77 to 1796 ng g(-1) dry sediment weight. The EDCs were also found in untreated and treated municipal sewage samples with a removal efficiency of 83% for OCPs but no removal efficiency for 17α-ethinylestradiol.

Removal of heavy metals from artificial metals contaminated water samples based on micelle-templated silica modified with pyoverdin I.

PubMed

Tansupo, Panadda; Worakarn, Chamonkolpradit; Saksit, Chanthai; Ruangviriyachai, Chalerm

2009-01-01

The micelle-templated silica (MTS) was firstly chemically modified with 3-glycidoxypropyl-trimethoxysilane (GPTMS) before immobilized with pyoverdin I. The characteristics of pyoverdin I-anchored onto the modified MTS were investigated using fluorescence, infrared spectra and scanning electron microscopy. The specific surface area of all materials was calculated by Brunauer, Emmett and Teller (BET) method using nitrogen isotherm adsorption data. As the results, the surface area of commercial silica gel decreased from 609.2 to 405.4 m2/g, it indicated that the pyoverdin I could be immobilized onto the surface of silica solid support. This adsorbent was used for extraction of Fe(III), Cu(II), Zn(II), and Pb(II) in artificial metals contaminated water. Experimental conditions for effective adsorption of trace levels of metal ions were optimized with respect to different experimental parameters using batch procedure. The optimum pH value for the removal of metal ions simultaneously on this adsorbent was 4.0. Complete desorption of the adsorbed metal ions from the adsorbent was carried out using 0.25 mol/L of EDTA. The effect of different cations and anions on the adsorption of these metals on adsorbent was studied and the results showed that the proposed adsorbent could be applied to the highly saline samples and the sample which contains some transition metals.

Natural organic matters removal efficiency by coagulation

NASA Astrophysics Data System (ADS)

Sapingi, Mohd Sharizal Mohd; Pishal, Munirah; Murshed, Mohamad Fared

2017-10-01

The presence of Natural Organic Matter (NOM) in surface water results in unwanted characteristics in terms of color, odor, and taste. NOM content reaction with free chlorine in treated water lowers the water quality further. Chlorine is added for disinfection and produces undesirable disinfection by-products (DPBs). DBPs in drinking water are carcinogenic to consumers and may promote cancerous cell development in the human body. This study was performed to compare the coagulant efficiency of aluminum sulfate (Alum) and ferric chloride (FeCl3) on NOM removal (as in UV254 absorbance) and turbidity removal under three pH conditions (pH 6, pH 7, and sample actual pH). The three sampling points for these studies were Jalan Baru River, Kerian River, and Redac Pond. Additional sampling points, such as Lubuk Buntar and a tubewell located in the Civil Engineering School, were included to observe differences in characteristics. DOC, UV absorbance, and full wavelength were tested, after which samples treated with alum were also tested to further analyze the NOM content. Based on UV254 absorbance and DOC data, specific UV value was calculated to obtain vital synopsis of the characteristics of NOM content, as well as coagulation efficiency.

Auto-recognition of surfaces and auto-generation of material removal volume for finishing process

NASA Astrophysics Data System (ADS)

Kataraki, Pramod S.; Salman Abu Mansor, Mohd

2018-03-01

Auto-recognition of a surface and auto-generation of material removal volumes for the so recognised surfaces has become a need to achieve successful downstream manufacturing activities like automated process planning and scheduling. Few researchers have contributed to generation of material removal volume for a product but resulted in material removal volume discontinuity between two adjacent material removal volumes generated from two adjacent faces that form convex geometry. The need for limitation free material removal volume generation was attempted and an algorithm that automatically recognises computer aided design (CAD) model’s surface and also auto-generate material removal volume for finishing process of the recognised surfaces was developed. The surfaces of CAD model are successfully recognised by the developed algorithm and required material removal volume is obtained. The material removal volume discontinuity limitation that occurred in fewer studies is eliminated.

A Field-Based Cleaning Protocol for Sampling Devices Used in Life-Detection Studies

NASA Astrophysics Data System (ADS)

Eigenbrode, Jennifer; Benning, Liane G.; Maule, Jake; Wainwright, Norm; Steele, Andrew; Amundsen, Hans E. F.

2009-06-01

Analytical approaches to extant and extinct life detection involve molecular detection often at trace levels. Thus, removal of biological materials and other organic molecules from the surfaces of devices used for sampling is essential for ascertaining meaningful results. Organic decontamination to levels consistent with null values on life-detection instruments is particularly challenging at remote field locations where Mars analog field investigations are carried out. Here, we present a seven-step, multi-reagent decontamination method that can be applied to sampling devices while in the field. In situ lipopolysaccharide detection via low-level endotoxin assays and molecular detection via gas chromatography-mass spectrometry were used to test the effectiveness of the decontamination protocol for sampling of glacial ice with a coring device and for sampling of sediments with a rover scoop during deployment at Arctic Mars-analog sites in Svalbard, Norway. Our results indicate that the protocols and detection technique sufficiently remove and detect low levels of molecular constituents necessary for life-detection tests.

Method for removing tilt control in adaptive optics systems

DOEpatents

Salmon, Joseph Thaddeus

1998-01-01

A new adaptive optics system and method of operation, whereby the method removes tilt control, and includes the steps of using a steering mirror to steer a wavefront in the desired direction, for aiming an impinging aberrated light beam in the direction of a deformable mirror. The deformable mirror has its surface deformed selectively by means of a plurality of actuators, and compensates, at least partially, for existing aberrations in the light beam. The light beam is split into an output beam and a sample beam, and the sample beam is sampled using a wavefront sensor. The sampled signals are converted into corresponding electrical signals for driving a controller, which, in turn, drives the deformable mirror in a feedback loop in response to the sampled signals, for compensating for aberrations in the wavefront. To this purpose, a displacement error (gradient) of the wavefront is measured, and adjusted by a modified gain matrix, which satisfies the following equation: G'=(I-X(X.sup.T X).sup.-1 X.sup.T)G(I-A)

A field-based cleaning protocol for sampling devices used in life-detection studies.

PubMed

Eigenbrode, Jennifer; Benning, Liane G; Maule, Jake; Wainwright, Norm; Steele, Andrew; Amundsen, Hans E F

2009-06-01

Analytical approaches to extant and extinct life detection involve molecular detection often at trace levels. Thus, removal of biological materials and other organic molecules from the surfaces of devices used for sampling is essential for ascertaining meaningful results. Organic decontamination to levels consistent with null values on life-detection instruments is particularly challenging at remote field locations where Mars analog field investigations are carried out. Here, we present a seven-step, multi-reagent decontamination method that can be applied to sampling devices while in the field. In situ lipopolysaccharide detection via low-level endotoxin assays and molecular detection via gas chromatography-mass spectrometry were used to test the effectiveness of the decontamination protocol for sampling of glacial ice with a coring device and for sampling of sediments with a rover scoop during deployment at Arctic Mars-analog sites in Svalbard, Norway. Our results indicate that the protocols and detection technique sufficiently remove and detect low levels of molecular constituents necessary for life-detection tests.

Influence of 300°C thermal conversion of Fe-Ce hydrous oxides prepared by hydrothermal precipitation on the adsorptive performance of five anions: Insights from EXAFS/XANES, XRD and FTIR (companion paper).

PubMed

Chubar, Natalia; Gerda, Vasyl; Banerjee, Dipanjan

2017-04-01

In this work, we report atomic-scale reconstruction processes in Fe-Ce oxide-based composites (hydrothermally precipitated at Fe-to-Ce dosage ratios of 1:0, 2:1, 1:1, 1:2, and 0:1), upon treatment at 300°C. The structural changes are correlated with the adsorptive removal of arsenate, phosphate, fluoride, bromide, and bromate. The presence of the carbonate-based Ce-component and surface sulfate in precursor samples creates favorable conditions for phase transformation, resulting in the formation of novel (unknown) layered compounds of Fe and Ce. These compounds are of the layered double hydroxide type, with sulfate in the interlayer space. In spite of general awareness of the importance of surface area in adsorptive removal, the increase in surface area upon thermal treatment did not increase adsorption of the studied anions. However, EXAFS simulations and the adsorption tests provided evidence of regularities between local structures of Fe in composites obtained at 80 and 300°C and adsorption performance of most studied anions. The best adsorption of tetrahedral anions was demonstrated by samples whose simulated outer Fe shells resulted from oscillations from both O and Fe atoms. In contrast, the loss of extended x-ray absorption fine structure was correlated with the decrease of adsorptive removal. Both Fe K-edge and Ce L 3 -edge EXAFS suggested the formation of solid solutions. For the first time, the utilization of extended x-ray absorption fine structure is suggested as a methodological approach (first expressed in the companion paper) to estimate the surface reactivity of inorganic materials intended for use as anion exchange adsorbents. Copyright © 2016 Elsevier Inc. All rights reserved.

Influence of Superhydrophobic Properties on Deicing

NASA Astrophysics Data System (ADS)

Nazhipkyzy, M.; Mansurov, Z. A.; Amirfazli, A.; Esbosin, A.; Temirgaliyeva, T. S.; Lesbayev, B. T.; Aliyev, E. T.; Prikhodko, N. G.

2016-11-01

Nowadays the creation of anti-icing, or deicing, surfaces is one of the most important problems, as such surfaces are widely used in aeronautics, wind turbines, and telecommunication antennas. In this paper, we focus mainly on reducing the ice adhesion forces and easy ice removal, once ice has formed. Removal of a liquid from a surface can be provided by modification of the surface wettability by means of applying superhydrophobic coatings. Such coatings are water-resistant, i.e., are characterized by low water adhesion forces. To study the impact of superhydrophobic coatings, tests were performed on the surface of a wing in a wind tunnel. By spraying Teflon and polyphenylene sulfide (PPS) on the wing, we obtained a superhydrophobic film. This film has a structure that provides superhydrophobic properties, so that the wetting angle is above 140°. A comparison of the resulting surface with a clean Teflon one shows that adhesion of the Teflon + PPS mixture to an aluminum surface is five times higher. We also investigate the degree of ice formation on the surfaces of simple and superhydrophobic aircraft wings at a temperature of -18°C. It was shown that ice was formed on a simple wing within 40 s and on a superhydrophobic wing within 25 s. When the simple wing with a mass of 23 g was inserted into the wind tunnel, its mass reached 50 g, and for a superhydrophobic wing with a mass of 26 g the latter reached 42 g. The sample of the airfoil wing we prepared has a low adhesion, which helps in easy ice removal.

Biofilm monitoring coupon system and method of use

NASA Technical Reports Server (NTRS)

Sauer, Richard L. (Inventor); Flanagan, David T. (Inventor)

1991-01-01

An apparatus and method is disclosed for biofilm monitoring of a water distribution system which includes the mounting of at least one fitting in a wall port of a manifold in the water distribution system with a passage through the fitting in communication. The insertion of a biofilm sampling member is through the fitting with planar sampling surfaces of different surface treatment provided on linearly arrayed sample coupons of the sampling member disposed in the flow stream in edge-on parallel relation to the direction of the flow stream of the manifold under fluid-tight sealed conditions. The sampling member is adapted to be aseptically removed from or inserted in the fitting and manifold under a positive pressure condition and the fitting passage sealed immediately thereafter by appropriate closure means so as to preclude contamination of the water distribution system through the fitting. The apparatus includes means for clamping the sampling member and for establishing electrical continuity between the sampling surfaces and the system for minimizing electropotential effects. The apparatus may also include a plurality of fittings and sampling members mounted on the manifold to permit extraction of the sampling members in a timed sequence throughout the monitoring period.

Processing of Novel Nanoparticle Dispersion Strengthened Ceramics for Improved Mechanical Performance

DTIC Science & Technology

1992-12-14

the composite . The top and bottom surfaces of each disc were removed to eliminate any reaction layer, and the discs were machined ’ to produce bars...l.It is postulated that during grinding of the composite , compressive stresses and machining flaws are introduced into the surface. The compressive...two materials considered would react differently to the annealing step. It can be expected that machining flaws will heal in the composite samples

Use of molecular oxygen to reduce EUV-induced carbon contamination of optics

NASA Astrophysics Data System (ADS)

Malinowski, Michael E.; Grunow, Philip A.; Steinhaus, Chip; Clift, W. Miles; Klebanoff, Leonard E.

2001-08-01

Carbon deposition and removal experiments on Mo/Si multilayer mirror (MLM) samples were performed using extreme ultraviolet (EUV) light on Beamline 12.0.1.2 of the Advanced Light Source, Lawrence Berkeley National Laboratory (LBNL). Carbon (C) was deposited onto Mo/Si multilayer mirror (MLM) samples when hydrocarbon vapors where intentionally introduced into the MLM test chamber in the presence of EUV at 13.44 nm (92.3eV). The carbon deposits so formed were removed by molecular oxygen + EUV. The MLM reflectivities and photoemission were measured in-situ during these carbon deposition and cleaning procedures. Auger Electron Spectroscopy (AES) sputter-through profiling of the samples was performed after experimental runs to help determine C layer thickness and the near-surface compositional-depth profiles of all samples studied. EUV powers were varied from ~0.2mW/mm2 to 3mW/mm2(at 13.44 nm) during both deposition and cleaning experiments and the oxygen pressure ranged from ~5x10-5 to 5x10-4 Torr during the cleaning experiments. C deposition rates as high as ~8nm/hr were observed, while cleaning rates as high as ~5nm/hr could be achieved when the highest oxygen pressure were used. A limited set of experiments involving intentional oxygen-only exposure of the MLM samples showed that slow oxidation of the MLM surface could occur.

A rop net and removable walkway used to quantitatively sample fishes over wetland surfaces in the dwarf mangrove of the Southern Everglades

USGS Publications Warehouse

Lorenz, J.J.; McIvor, C.C.; Powell, G.V.N.; Frederick, P.C.

1997-01-01

We describe a 9 m2 drop net and removable walkways designed to quantify densities of small fishes in wetland habitats with low to moderate vegetation density. The method permits the collection of small, quantitative, discrete samples in ecologically sensitive areas by combining rapid net deployment from fixed sites with the carefully contained use of the fish toxicant rotenone. This method requires very little contact with the substrate, causes minimal alteration to the habitat being sampled, samples small fishes in an unbiased manner, and allows for differential sampling of microhabitats within a wetland. When used in dwarf red mangrove (Rhizophora mangle) habitat in southern Everglades National Park and adjacent areas (September 1990 to March 1993), we achieved high recovery efficiencies (78–90%) for five common species <110 mm in length. We captured 20,193 individuals of 26 species. The most abundant fishes were sheepshead minnowCyprinodon variegatus, goldspotted killifishFloridichthys carpio, rainwater killifishLucania parva, sailfin mollyPoecilia latipinna, and the exotic Mayan cichlidCichlasoma urophthalmus. The 9 m2 drop net and associated removable walkways are versatile and can be used in a variety of wetland types, including both interior and coastal wetlands with either herbaceous or woody vegetation.

X-ray photoelectron spectroscopy study of chemically-etched Nd-Ce-Cu-O surfaces

NASA Technical Reports Server (NTRS)

Vasquez, R. P.; Gupta, A.; Kussmaul, A.

1991-01-01

Acetic acid, Br2, and HCl solutions are investigated for removing insulating species from Nd(1.85)Ce(0.15)CuO(4-delta) (NCCO) thin film surfaces. X-ray photoelectron spectroscopy (XPS) shows that the HCl etch is most effective, yielding O 1s spectra comparable to those obtained from samples cleaned in vacuum and a clear Fermi edge in the valence band region. Reduction and oxidation reversibly induces and eliminates, respectively, Fermi level states for undoped samples, but has no clearly observable effect on the XPS spectra for doped samples. Reactivity to air is much less for NCCO compared to hole superconductors, which is attributed to the lack of reactive alkaline earth elements in NCCO.

Removal of Organophosphorus Pesticides from Aqueous Solution by Magnetic Fe3O4/Red Mud-Nanoparticles.

PubMed

Aydin, Senar

2016-12-01

  The aim of this study was to investigate the usability of magnetic Fe3O4/red mud nanoparticles (NPs) for the removal of organophosphorus pesticides from water samples. The effect of various experimental parameters such as red mud amount in Fe3O4/red mud-NPs, pH, contact time, initial pesticide concentrations and adsorbent dose was studied in order to find the optimum conditions for their removal in a batch process. The Fe3O4/red mud-NPs were characterized by using TGA, SEM, XRD, VSM, and determination of the BET surface area. After the regenerated Fe3O4/red mud-NPs were used three times, the sorption capacity and the magnetic separability were observed to be unaffected. Freundlich model described the sorption process better than Langmuir isotherm and the pseudo second-order kinetic model was determined as the best-fit model. The film diffusion mechanism was found to be a main rate control mechanism. The Fe3O4/red mud-NPs satisfactorily removed the OPPS from real water samples.

Coal fly ash based carbons for SO2 removal from flue gases.

PubMed

Rubio, B; Izquierdo, M T

2010-07-01

Two different coal fly ashes coming from the burning of two coals of different rank have been used as a precursor for the preparation of steam activated carbons. The performance of these activated carbons in the SO(2) removal was evaluated at flue gas conditions (100 degrees C, 1000 ppmv SO(2), 5% O(2), 6% H(2)O). Different techniques were used to determine the physical and chemical characteristics of the samples in order to explain the differences found in their behaviour. A superior SO(2) removal capacity was shown by the activated carbon obtained using the fly ash coming from a sub-bituminous-lignite blend. Experimental results indicated that the presence of higher amount of certain metallic oxides (Ca, Fe) in the carbon-rich fraction of this fly ash probably has promoted a deeper gasification in the activation with steam. A more suitable surface chemistry and textural properties have been obtained in this case which explains the higher efficiency shown by this sample in the SO(2) removal. Copyright (c) 2010 Elsevier Ltd. All rights reserved.

Surface Cleaning of Iron Artefacts by Lasers

NASA Astrophysics Data System (ADS)

Koh, Y. S.; Sárady, I.

In this paper the general method and ethics of the laser cleaning technique for conservation are presented. The results of two experiments are also presented; experiment 1 compares cleaning of rust by an Nd:YAG laser and micro-blasting whilst experiment 2 deals with removing the wax coating from iron samples by a TEA CO2 laser. The first experiment showed that cleaning with a pulsed laser and higher photon energy obtained a better surface structure than micro blasting. The second experiment showed how differences in energy density affect the same surface.

Effect of a microstructure and surface hydrogen alloying of a VT6 alloy on diffusion welding

NASA Astrophysics Data System (ADS)

Senkevich, K. S.; Skvortsova, S. V.; Kudelina, I. M.; Knyazev, M. I.; Zasypkin, V. V.

2014-01-01

The effect of a structural type (lamellar, fine, gradient) and additional surface alloying with hydrogen on the diffusion bonding of titanium alloy VT6 samples is studied. It is shown that the surface alloying of VT6 alloy parts with hydrogen allows one to decrease the diffusion welding temperature by 50-100°C, to obtain high-quality pore-free bonding, and to remove the "structural" boundary between materials to be welded that usually forms during welding of titanium alloys with a lamellar structure.

Sorption potential of alkaline treated straw and a soil for sulfonylurea herbicide removal from aqueous solutions: An environmental management strategy.

PubMed

Cara, Irina-Gabriela; Rusu, Bogdan-George; Raus, Lucian; Jitareanu, Gerard

2017-11-01

The adsorption potential of alkaline treated straw (wheat and corn) in mixture with soil, has been investigated for the removal of sulfonylurea molecules from an aqueous solutions. The surface characteristics were investigated by scanning electron microscopy and Fourier Transform Infrared - FTIR, while the adsorbent capacity was evaluated using batch sorption tests and liquid chromatography coupled with mass spectrometry. Surface analysis of alkaline treated straw samples by scanning electron microscopy - SEM showed the increasing of the surface roughness improving their functional surface activity. An increase (337.22 mg g -1 ) of adsorption capacity of sulfonylurea molecules was obtained for all studied straw. The Langmuir isotherm model was the best model for the mathematical description of the adsorption process indicating the forming of a surface sorption monolayer with a finite number of identical sites. The kinetics of sulfonylurea herbicide followed the pseudo-second order mechanism corresponding to strong chemical interactions. The results sustained that the alkaline treated straw have biosorption characteristics, being suitable adsorbent materials. Copyright © 2017 Elsevier Ltd. All rights reserved.

The analysis of tire rubber traces collected after braking incidents using Pyrolysis-GasChromatography/Mass Spectrometry.

PubMed

Sarkissian, Garry

2007-09-01

Automobile tire marks can routinely be found at the scenes of crime, particularly hit-and-run accidents and are left on road surfaces because of sudden braking or the wheels spinning. The tire marks are left due to the friction between the tire rubber and the solid road surface, and do not always demonstrate the tire tread pattern. However, the tire mark will contain traces of the tire. In this study, Pyrolysis Gas Chromatography/Mass Spectrometry was used to analyze 12 tires from different manufacturer's and their traces collected after braking incidents. Tire marks were left on a conglomerate road surface with sudden braking. The samples were pyrolysed without removal of contaminant in a micro-furnace type pyrolyser. Quantitative and qualitative analysis were performed on all the samples. All 12 samples were distinguished from each other. Each of the tire traces were identified as coming from there original source.

Biosorptive removal of inorganic arsenic species and fluoride from aqueous medium by the stem of Tecomella undulate.

PubMed

Brahman, Kapil Dev; Kazi, Tasneem Gul; Baig, Jameel Ahmed; Afridi, Hassan Imran; Arain, Sadaf Sadia; Saraj, Saima; Arain, Muhammad B; Arain, Salma Aslam

2016-05-01

Simultaneous removal of fluoride (F(-)), inorganic arsenic species, As(III) and As(V), from aqueous samples has been performed using an economic indigenous biosorbent (Stem of Tecomella undulata). The inorganic As species in water samples before and after biosorption were determined by cloud point and solid phase extraction methods, while F(-) was determined by ion chromatography. Batch experiments were carried out to evaluate the equilibrium adsorption isotherm studies for As(III), As(V) and F(-) in aqueous solutions. Several parameters of biosorption were optimized such as pH, biomass dosage, analytes concentration, time and temperature. The surface of biosorbent was characterized by SEM and FTIR. The FTIR study indicated the presence of carbonyl and amine functional groups which may have important role in the sorption/removal of these ions. Thermodynamic and kinetic study indicated that the biosorption of As(III), As(V) and F(-) were spontaneous, exothermic and followed by pseudo-second-order. Meanwhile, the interference study revealed that there was no significant effect of co-existing ions for the removal of inorganic As species and F(-) from aqueous samples (p > 0.05). It was observed that the indigenous biosorbent material simultaneously adsorbed As(III) (108 μg g(-1)), As(V) (159 μg g(-1)) and F(-) (6.16 mg g(-1)) from water at optimized conditions. The proposed biosorbent was effectively regenerated and efficiently used for several experiments, to remove the As(III), As(V) and F(-) from real water sample collected from endemic area of Pakistan. Copyright © 2016 Elsevier Ltd. All rights reserved.

In-situ preparation of functionalized molecular sieve material and a methodology to remove template

NASA Astrophysics Data System (ADS)

Yadav, Rekha; Ahmed, Maqsood; Singh, Arvind Kumar; Sakthivel, Ayyamperumal

2016-03-01

A series of diaminosilane-functionalized silicoaluminophosphate molecular sieve (SAPO-37) was prepared by in-situ synthesis, and a novel method was developed for the selective removal of structure directing agent (SDA)/template from the functionalized SAPO-37.The complete removal of the SDA was evident according to FT-IR, TGA, 13C MAS-NMR and elemental analysis. The developed method was found to be efficient for removal of template from microporous molecular sieve viz., SAPO-37 and can be applied for other microporous molecular sieves such as SAPO-5, SAPO-40, etc. The powder XRD pattern of the template-removed samples showed a highly crystalline SAPO-37 phase. Argentometric titration revealed that more than 90% of diamine functionality exposed on the surface was accessible for catalytic applications. The resultant materials showed promising activity for ring opening of epoxide with aniline to yield β-amino-alcohol.

In-situ preparation of functionalized molecular sieve material and a methodology to remove template.

PubMed

Yadav, Rekha; Ahmed, Maqsood; Singh, Arvind Kumar; Sakthivel, Ayyamperumal

2016-03-10

A series of diaminosilane-functionalized silicoaluminophosphate molecular sieve (SAPO-37) was prepared by in-situ synthesis, and a novel method was developed for the selective removal of structure directing agent (SDA)/template from the functionalized SAPO-37.The complete removal of the SDA was evident according to FT-IR, TGA, (13)C MAS-NMR and elemental analysis. The developed method was found to be efficient for removal of template from microporous molecular sieve viz., SAPO-37 and can be applied for other microporous molecular sieves such as SAPO-5, SAPO-40, etc. The powder XRD pattern of the template-removed samples showed a highly crystalline SAPO-37 phase. Argentometric titration revealed that more than 90% of diamine functionality exposed on the surface was accessible for catalytic applications. The resultant materials showed promising activity for ring opening of epoxide with aniline to yield β-amino-alcohol.

Possible overestimation of surface disinfection efficiency by assessment methods based on liquid sampling procedures as demonstrated by in situ quantification of spore viability.

PubMed

Grand, I; Bellon-Fontaine, M-N; Herry, J-M; Hilaire, D; Moriconi, F-X; Naïtali, M

2011-09-01

The standard test methods used to assess the efficiency of a disinfectant applied to surfaces are often based on counting the microbial survivors sampled in a liquid, but total cell removal from surfaces is seldom achieved. One might therefore wonder whether evaluations of microbial survivors in liquid-sampled cells are representative of the levels of survivors in whole populations. The present study was thus designed to determine the "damaged/undamaged" status induced by a peracetic acid disinfection for Bacillus atrophaeus spores deposited on glass coupons directly on this substrate and to compare it to the status of spores collected in liquid by a sampling procedure. The method utilized to assess the viability of both surface-associated and liquid-sampled spores included fluorescence labeling with a combination of Syto 61 and Chemchrome V6 dyes and quantifications by analyzing the images acquired by confocal laser scanning microscopy. The principal result of the study was that the viability of spores sampled in the liquid was found to be poorer than that of surface-associated spores. For example, after 2 min of peracetic acid disinfection, less than 17% ± 5% of viable cells were detected among liquid-sampled cells compared to 79% ± 5% or 47% ± 4%, respectively, when the viability was evaluated on the surface after or without the sampling procedure. Moreover, assessments of the survivors collected in the liquid phase, evaluated using the microscopic method and standard plate counts, were well correlated. Evaluations based on the determination of survivors among the liquid-sampled cells can thus overestimate the efficiency of surface disinfection procedures.

Possible Overestimation of Surface Disinfection Efficiency by Assessment Methods Based on Liquid Sampling Procedures as Demonstrated by In Situ Quantification of Spore Viability ▿

PubMed Central

Grand, I.; Bellon-Fontaine, M.-N.; Herry, J.-M.; Hilaire, D.; Moriconi, F.-X.; Naïtali, M.

2011-01-01

The standard test methods used to assess the efficiency of a disinfectant applied to surfaces are often based on counting the microbial survivors sampled in a liquid, but total cell removal from surfaces is seldom achieved. One might therefore wonder whether evaluations of microbial survivors in liquid-sampled cells are representative of the levels of survivors in whole populations. The present study was thus designed to determine the “damaged/undamaged” status induced by a peracetic acid disinfection for Bacillus atrophaeus spores deposited on glass coupons directly on this substrate and to compare it to the status of spores collected in liquid by a sampling procedure. The method utilized to assess the viability of both surface-associated and liquid-sampled spores included fluorescence labeling with a combination of Syto 61 and Chemchrome V6 dyes and quantifications by analyzing the images acquired by confocal laser scanning microscopy. The principal result of the study was that the viability of spores sampled in the liquid was found to be poorer than that of surface-associated spores. For example, after 2 min of peracetic acid disinfection, less than 17% ± 5% of viable cells were detected among liquid-sampled cells compared to 79% ± 5% or 47% ± 4%, respectively, when the viability was evaluated on the surface after or without the sampling procedure. Moreover, assessments of the survivors collected in the liquid phase, evaluated using the microscopic method and standard plate counts, were well correlated. Evaluations based on the determination of survivors among the liquid-sampled cells can thus overestimate the efficiency of surface disinfection procedures. PMID:21742922

Removal of {sup 222}Rn daughters from metal surfaces

DOE Office of Scientific and Technical Information (OSTI.GOV)

Zuzel, G.; Wojcik, M.; Majorovits, B.

Removal of the long-lived {sup 222}Rn daughters ({sup 210}Pb, {sup 210}Bi and {sup 210}Po) from copper, stainless steel and germanium surfaces was investigated. As cleaning techniques etching and electro-polishing was applied to samples in a form of discs exposed earlier to a strong radon source. Reduction of the {sup 210}Pb activity was tested using a HPGe spectrometer, for {sup 210}Bi a beta spectrometer and for {sup 210}Po an alpha spectrometer was used. According to the conducted measurements electro-polishing was always more efficient compared to etching and in case of copper the activity reduction factors for {sup 210}Pb, {sup 210}Bi andmore » {sup 210}Po were between 200 and 400. Etching does not remove {sup 210}Po from copper but works very efficiently from germanium. Results obtained for {sup 210}Pb and {sup 210}Bi for etched stainless steel were worse but still slightly better than those achieved for copper.« less

Removal of Long-Lived Radon Daughters by Electropolishing Thin Layers of Stainless Steel

NASA Astrophysics Data System (ADS)

White, James; Schnee, Richard; Bunker, Raymond; Bowles, Michael; Cushman, Priscilla; Epland, Matthew; Pepin, Mark; Guiseppe, Vince

2012-10-01

Long-lived alpha and beta emitters in the Radon decay chain on detector surfaces may be limiting background in many experiments attempting to detect dark matter or neutrinoless double beta decay. To screen detector surfaces for this radioactive contamination, a low-radiation, multi-wire proportional chamber (the BetaCage) is under construction. Removal of Pb-210 implanted on its 25-micron stainless steel wires without causing significant variation in the diameter of the wires is critical to the BetaCage's ultimate sensitivity. An apparatus to perform electropolishing trials to remove roughly a micron of material has been assembled. These trials have shown promising results. Stainless steel square samples implanted with Pb-210 have shown counts with a reduction factor greater than 10 after electropolishing according to gamma assay. Furthermore, alpha counting has produced similar results, with a reduction factor greater than 100. Lastly, the diameters of wires after electropolishing have remained sufficiently uniform, with reduction in thickness consistent with expectations.

SPARCLE: Space Plasma Alleviation of Regolith Concentrations in the Lunar Environment

NASA Astrophysics Data System (ADS)

Clark, P. E.; Keller, J. W.; Curtis, S. A.; Nuth, J. A.; Stubbs, T. J.; Farrell, W. M.

2006-05-01

The return of robotic devices and humans to the Moon will occur in the near future. Based on our previous experience, surface dust is a major problem requiring a solution: During Apollo landings, extensive locally- induced stirring of the regolith caused dust to be suspended long enough to come into contact with conducting surfaces. Dust behaved like abrasive Velcro: it adhered to everything and attempts to remove it by simply brushing did not remove fines (<10) and resulted in severe abrasion. Lunar fines, because of their electrostatic charging, were relatively difficult to collect in sample bags along with other size range particles. Within hours, seals were broken, samples contaminated, and portions of the samples, especially fines, lost. Because of this difficulty, details on lunar dust are relatively sparse. Obviously, the strategies initially implemented to deal with lunar dust failed. A major technological challenge will be developing a dust mitigation strategy. A currently proposed strategy based increased magnetic susceptibility in lunar fines may not work uniformly well for fines of non-mare, or non-lunar, composition. Based on dust behavior already observed on previous missions, we believe the successful strategy will deal with dust dynamics resulting from interaction between mechanical and electrostatic forces. We are planning test and develop an electrostatically-based device to modulate the electrical potential of conducting surfaces, hence to self clean exposed surfaces while collecting dust samples. It would scan a surface constantly to control its potential, and a plate of the opposite potential. As a first step, an experimental low mass, power, and volume device with complimentary electron and ion guns with specially designed self-cleaning nozzles are being designed for to test our concept and develop a working charging and discharging strategy in the lunar environment. Meanwhile, a laboratory simulation will act as a feasibility study for a laboratory breadboard self-cleaning device based on the use of combined electron or ion beams. The compact device would act as plasma dust sweeper.

Characterizing the rapid spread of porcine epidemic diarrhea virus (PEDV) through an animal food manufacturing facility.

PubMed

Schumacher, Loni L; Huss, Anne R; Cochrane, Roger A; Stark, Charles R; Woodworth, Jason C; Bai, Jianfa; Poulsen, Elizabeth G; Chen, Qi; Main, Rodger G; Zhang, Jianqiang; Gauger, Phillip C; Ramirez, Alejandro; Derscheid, Rachel J; Magstadt, Drew M; Dritz, Steve S; Jones, Cassandra K

2017-01-01

New regulatory and consumer demands highlight the importance of animal feed as a part of our national food safety system. Porcine epidemic diarrhea virus (PEDV) is the first viral pathogen confirmed to be widely transmissible in animal food. Because the potential for viral contamination in animal food is not well characterized, the objectives of this study were to 1) observe the magnitude of virus contamination in an animal food manufacturing facility, and 2) investigate a proposed method, feed sequencing, to decrease virus decontamination on animal food-contact surfaces. A U.S. virulent PEDV isolate was used to inoculate 50 kg swine feed, which was mixed, conveyed, and discharged into bags using pilot-scale feed manufacturing equipment. Surfaces were swabbed and analyzed for the presence of PEDV RNA by quantitative real-time polymerase chain reaction (qPCR). Environmental swabs indicated complete contamination of animal food-contact surfaces (0/40 vs. 48/48, positive baseline samples/total baseline samples, positive subsequent samples/total subsequent samples, respectively; P < 0.05) and near complete contamination of non-animal food-contact surfaces (0/24 vs. 16/18, positive baseline samples/total baseline samples, positive subsequent samples/total subsequent samples, respectively; P < 0.05). Flushing animal food-contact surfaces with low-risk feed is commonly used to reduce cross-contamination in animal feed manufacturing. Thus, four subsequent 50 kg batches of virus-free swine feed were manufactured using the same system to test its impact on decontaminating animal food-contact surfaces. Even after 4 subsequent sequences, animal food-contact surfaces retained viral RNA (28/33 positive samples/total samples), with conveying system being more contaminated than the mixer. A bioassay to test infectivity of dust from animal food-contact surfaces failed to produce infectivity. This study demonstrates the potential widespread viral contamination of surfaces in an animal food manufacturing facility and the difficulty of removing contamination using conventional feed sequencing, which underscores the importance for preventing viruses from entering and contaminating such facilities.

Algorithm for ion beam figuring of low-gradient mirrors.

PubMed

Jiao, Changjun; Li, Shengyi; Xie, Xuhui

2009-07-20

Ion beam figuring technology for low-gradient mirrors is discussed. Ion beam figuring is a noncontact machining technique in which a beam of high-energy ions is directed toward a target workpiece to remove material in a predetermined and controlled fashion. Owing to this noncontact mode of material removal, problems associated with tool wear and edge effects, which are common in conventional contact polishing processes, are avoided. Based on the Bayesian principle, an iterative dwell time algorithm for planar mirrors is deduced from the computer-controlled optical surfacing (CCOS) principle. With the properties of the removal function, the shaping process of low-gradient mirrors can be approximated by the linear model for planar mirrors. With these discussions, the error surface figuring technology for low-gradient mirrors with a linear path is set up. With the near-Gaussian property of the removal function, the figuring process with a spiral path can be described by the conventional linear CCOS principle, and a Bayesian-based iterative algorithm can be used to deconvolute the dwell time. Moreover, the selection criterion of the spiral parameter is given. Ion beam figuring technology with a spiral scan path based on these methods can be used to figure mirrors with non-axis-symmetrical errors. Experiments on SiC chemical vapor deposition planar and Zerodur paraboloid samples are made, and the final surface errors are all below 1/100 lambda.

Phase aberration compensation of digital holographic microscopy based on least squares surface fitting

NASA Astrophysics Data System (ADS)

Di, Jianglei; Zhao, Jianlin; Sun, Weiwei; Jiang, Hongzhen; Yan, Xiaobo

2009-10-01

Digital holographic microscopy allows the numerical reconstruction of the complex wavefront of samples, especially biological samples such as living cells. In digital holographic microscopy, a microscope objective is introduced to improve the transverse resolution of the sample; however a phase aberration in the object wavefront is also brought along, which will affect the phase distribution of the reconstructed image. We propose here a numerical method to compensate for the phase aberration of thin transparent objects with a single hologram. The least squares surface fitting with points number less than the matrix of the original hologram is performed on the unwrapped phase distribution to remove the unwanted wavefront curvature. The proposed method is demonstrated with the samples of the cicada wings and epidermal cells of garlic, and the experimental results are consistent with that of the double exposure method.

Efficacy of detergents in removing Salmonella and Shigella spp. from the surface of fresh produce.

PubMed

Raiden, Renee M; Sumner, Susan S; Eifert, Joseph D; Pierson, Merle D

2003-12-01

Fresh produce has been implicated in several foodborne disease outbreaks. Produce surfaces can be primary sites of contamination during production and handling. One approach to reduce contamination is to treat fresh produce with rinsing agents. In this study, different detergent agents were used at 22 and 40 degrees C to determine their efficacy in removing Salmonella and Shigella spp. from the surfaces of strawberries, tomatoes, and green-leaf lettuce. Produce was inoculated at 22 degrees C with a cocktail of nalidixic acid-resistant organisms (6 to 6.5 log CFU/ml). After air drying for 1 h, samples were rinsed with either 0.1% Tween 80, 0.1% sodium lauryl sulfate (SLS), or water (control) at 22 or 40 degrees C. Rinse solutions were spiral plated onto tryptic soy agar supplemented with 50 mg of nalidixic acid per liter. In trials involving strawberries and lettuce, Salmonella and Shigella were removed at levels of 4 and 3 log CFU/ml, respectively, except from Salmonella-inoculated strawberries rinsed with SLS, for which minimal removal rates were 1.5 log CFU/ml at 22 degrees C and < 1 log CFU/ml at 40 degrees C. When whole strawberries were analyzed after rinsing with SLS, few organisms were recovered. This result suggests that SLS may have a lethal or sublethal effect on Salmonella, especially when a 40 degrees C solution is used. Salmonella and Shigella removal rates for tomatoes were 1 and 1.5 log CFU/ml lower, respectively, than those for strawberries or lettuce. Overall, detergents were no more effective in removing organisms from produce than water was. The detergents examined would not constitute effective overall produce rinse treatments.

Bacterial Immobilization for Imaging by Atomic Force Microscopy

DOE Office of Scientific and Technical Information (OSTI.GOV)

Allison, David P; Sullivan, Claretta; Mortensen, Ninell P

2011-01-01

AFM is a high-resolution (nm scale) imaging tool that mechanically probes a surface. It has the ability to image cells and biomolecules, in a liquid environment, without the need to chemically treat the sample. In order to accomplish this goal, the sample must sufficiently adhere to the mounting surface to prevent removal by forces exerted by the scanning AFM cantilever tip. In many instances, successful imaging depends on immobilization of the sample to the mounting surface. Optimally, immobilization should be minimally invasive to the sample such that metabolic processes and functional attributes are not compromised. By coating freshly cleaved micamore » surfaces with porcine (pig) gelatin, negatively charged bacteria can be immobilized on the surface and imaged in liquid by AFM. Immobilization of bacterial cells on gelatin-coated mica is most likely due to electrostatic interaction between the negatively charged bacteria and the positively charged gelatin. Several factors can interfere with bacterial immobilization, including chemical constituents of the liquid in which the bacteria are suspended, the incubation time of the bacteria on the gelatin coated mica, surface characteristics of the bacterial strain and the medium in which the bacteria are imaged. Overall, the use of gelatin-coated mica is found to be generally applicable for imaging microbial cells.« less

Synthesis of activated carbon from oil fly ash for removal of H2S from gas stream

NASA Astrophysics Data System (ADS)

Aslam, Zaheer; Shawabkeh, Reyad A.; Hussein, Ibnelwaleed A.; Al-Baghli, Nadhir; Eic, Mladen

2015-02-01

Activated carbon (AC) is made from waste oil fly ash (OFA) which is produced in large quantities from power generation plants through combustion of heavy fuel oil. OFA contains ∼80% carbon that makes it suitable for producing AC by physicochemical treatments using a mixture of HNO3, H2SO4, and H3PO4 acids to remove non-carbonaceous impurities. The acid treated OFA is then activated by CO2 at 990 °C. The physico-chemical treatments of OFA have increased the surface area from 4 to 375 m2/g. Surface morphology and pore volume of AC are characterized by combined SEM and EDX techniques. Elemental analysis shows that sulfur content is reduced from 7.1 wt% in untreated OFA to 0.51 wt% for the treated OFA. The AC is further treated with HNO3 and NH4OH solutions in order to attach the carboxylic and amine groups on the surface, respectively. FTIR characterization is used to confirm the presence of the functional groups on the surface of AC at different stages of its development. The performance of functionalized AC samples is tested for the removal of H2S from a synthetic natural gas by carrying out breakthrough experiments. The results from these tests have shown maximum adsorption capacity of 0.3001 mg/g for NH4OH functionalized activated carbon with 86.43% regeneration efficiency. The ammonium hydroxide treated AC is found to be more effective for H2S removal than acid treated AC as confirmed by breakthrough experiments. The results indicate that the presence of more acidic functionalities on the surface reduces the H2S adsorption efficiency from the gas mixture.

New materials based on polylactide modified with silver and carbon ions

NASA Astrophysics Data System (ADS)

Kurzina, I. A.; Pukhova, I. V.; Botvin, V. V.; Davydova, D. V.; Filimoshkin, A. G.; Savkin, K. P.; Oskomov, K. V.; Oks, E. M.

2015-11-01

An integrated study of poly-L-lactide (PL) synthesis and the physicochemical properties of film surfaces, both modified by silver and carbon ion implantation and also unmodified PL surfaces, has been carried out. Surface modification was done using aMevva-5.Ru metal ion source with ion implantation doses of 1.1014, 1.1015 and 1.1016 ion/cm2. Material characterization was done using NMR, IRS, XPS and AFM. The molecular weight (MW), micro-hardness, surface resistivity, and limiting wetting angle of both un-implanted and implanted samples were measured. The results reveal that degradation of PL macromolecules occurs during ion implantation, followed by CO or CO2 removal and MW decrease. With increasing implantation dose, the glycerol wettability of the PL surface increases but the water affinity decreases (hydrophobic behavior). After silver and carbon ion implantation into the PL samples, the surface resistivity is reduced by several orders of magnitude and a tendency to micro-hardness reductionis induced.

Control of the Pore Texture in Nanoporous Silicon via Chemical Dissolution.

PubMed

Secret, Emilie; Wu, Chia-Chen; Chaix, Arnaud; Galarneau, Anne; Gonzalez, Philippe; Cot, Didier; Sailor, Michael J; Jestin, Jacques; Zanotti, Jean-Marc; Cunin, Frédérique; Coasne, Benoit

2015-07-28

The surface and textural properties of porous silicon (pSi) control many of its physical properties essential to its performance in key applications such as optoelectronics, energy storage, luminescence, sensing, and drug delivery. Here, we combine experimental and theoretical tools to demonstrate that the surface roughness at the nanometer scale of pSi can be tuned in a controlled fashion using partial thermal oxidation followed by removal of the resulting silicon oxide layer with hydrofluoric acid (HF) solution. Such a process is shown to smooth the pSi surface by means of nitrogen adsorption, electron microscopy, and small-angle X-ray and neutron scattering. Statistical mechanics Monte Carlo simulations, which are consistent with the experimental data, support the interpretation that the pore surface is initially rough and that the oxidation/oxide removal procedure diminishes the surface roughness while increasing the pore diameter. As a specific example considered in this work, the initial roughness ξ ∼ 3.2 nm of pSi pores having a diameter of 7.6 nm can be decreased to 1.0 nm following the simple procedure above. This study allows envisioning the design of pSi samples with optimal surface properties toward a specific process.

Role of Pb for Ag growth on H-passivated Si(1 0 0) surfaces

NASA Astrophysics Data System (ADS)

Mathew, S.; Satpati, B.; Joseph, B.; Dev, B. N.

2005-08-01

We have deposited Ag on hydrogen passivated Si(1 0 0) surfaces under high vacuum conditions at room temperature. The deposition, followed by annealing at 250 °C for 30 min, produced silver islands of an average lateral size 36±14 nm. Depositing a small amount of Pb prior to Ag deposition reduced the average island size to 14±5 nm. A small amount of Pb, initially present at the Ag-Si interface, is found to be segregating to the surface of Ag after annealing. Both these aspects, namely, reduction of the island size and Pb floating on the Ag surface conform to the surfactant action of Pb. Samples have been characterized by transmission electron microscopy (TEM) and Rutherford backscattering spectroscopy (RBS). A selective etching process that preferentially removes Pb, in conjunction with RBS, was used to detect surface segregation of Pb involving depth scales below the resolution of conventional RBS. The annealing and etching process leaves only smaller Ag islands on the surface with complete removal of Pb. Ag growth in the presence of Pb leads to smaller Ag islands with a narrower size distribution.

Adsorption, oxidation, and reduction behavior of arsenic in the removal of aqueous As(III) by mesoporous Fe/Al bimetallic particles.

PubMed

Cheng, Zihang; Fu, Fenglian; Dionysiou, Dionysios D; Tang, Bing

2016-06-01

In this study, mesoporous iron/aluminum (Fe/Al) bimetallic particles were synthesized and employed for the removal of aqueous As(III). Scanning electron microscopy and energy dispersive spectroscopy (SEM-EDS), Brunauer-Emmett-Teller (BET) analysis method, Vibrating-sample magnetometry (VSM), X-ray photoelectron spectroscopy (XPS), and Fourier transform infrared spectroscopy (FTIR) were employed to characterize the Fe/Al bimetals before and after reaction with As(III). The physical properties, compositions, and structures of Fe/Al bimetallic particles as well as the As(III) removal mechanism were investigated. The characterization of the bimetallic particles after the reaction has revealed the removal of As(III) is a complex process including surface adsorption and oxidation, and intraparticle reduction. The good As(III) removal capability and stability of the Fe/Al bimetallic particles exhibited its great potential as an effective and environmental friendly agent for As(III) removal from water. Copyright © 2016 Elsevier Ltd. All rights reserved.

Surface cleaning for negative electron affinity GaN photocathode

NASA Astrophysics Data System (ADS)

Qiao, Jianliang; Yin, Yingpeng; Gao, Youtang; Niu, Jun; Qian, Yunsheng; Chang, Benkang

2012-10-01

In the preparation process for negative electron affinity (NEA) GaN photocathode, the surface cleanness is very important to activation, it influences the sensitivity and stability of NEA GaN photocathode. The traditional corrosion methods based on oxidizing and dissolving can't remove oxygen (O) and carbon (C) on GaN surface effectively. How to get an ideal atom clean surface is still an important question at present. The cleaning techniques for GaN photocathode was studied by using NEA photocathode activation system and XPS surface analysis system. The experiment sample is p-type GaN doped with Mg, doped concentration is 1.37×1017 cm-3, the transfer rate is 3.08 cm2/V-S, and the thickness of activation layer is 0.51 μm, the substrate is 300 μm thick sapphire. The sample was dealed with chemical cleaning depuration at first. And to get the atom clean surface, the vacuum heat cleaning process was needed. The methods of chemical cleaning and the vacuum heating cleaning were given in detail. According to the X-ray photoelectron spectroscopy of GaN surface after chemical cleaning and the vacuum degree curve of the activation chamber during the heat cleaning, the cleaning effect and the cleaning mechanism were discussed. After the effective chemical cleaning and the heating of 700 Centigrade degree about 20 minutes in ultrahigh vacuum system, the oxides and carbon contaminants on cathode surface can be removed effectively, and the ideal atom clean surface can be obtained. The purpose of heating depuration process is that not only to get the atom clean GaN surface, but also to guarantee the contents of Ga, N on GaN surface stabilize and to keep the system ultra-high vacuum degree. Because of the volatilization of oxide and carbon impurity on the cathode surface, the vacuum degree curve drops with the rising of temperature on the whole.

Repercussion of noni mouthwash on surface characterization of Nickel-Titanium archwire.

PubMed

Dilipkumar, Dhivya; Dhinahar, S; Deenadayalan, P; Tandon, Akshay; Suresh, Poonkuzhali

2017-01-01

Maintaining oral hygiene is very important during orthodontic therapy mouthwashes are prescribed as an adjunct to improve patient's oral hygiene. Commercially available mouthwashes e.g. Chlorhexidine, Listerine, fluoride containing mouthwashes have shown to alter the surface characteristics of orthodontic wires. Hence the purpose of the study was to evaluate the effect of Noni mouthwash on surface quality and compositional changes of Nickel Titanium orthodontic wires. In this in vitro study pre-formed 0.014 inch NiTi arch wire was used. The study comprised of two samples, one control and one test sample which were 25mm in length. Control sample was stored at room temperature without any manipulation while test sample was immersed in Noni mouthwash solution for 1.5 hours, after which the test specimen was removed from the mouthwash solution and rinsed with distilled water. Both control and test samples were sent for scanning electron microscopy analysis, to qualitatively characterize the topography of the wire surface. Electron dispersion spectrum analysis was done to evaluate the various components of both the wires. No significant difference in the average surface roughness for both wire samples was observed. There was no significant difference seen in the composition of wire after immersion in Noni mouthwash. Noni mouthwash did not have significant influence on the surface roughness or altered the composition of the Ni-Ti wire. Hence Noni mouthwash may be prescribed as a natural, non-destructive prophylactic agent for orthodontic patients.

A comparison of root surface instrumentation using manual, ultrasonic and rotary instruments: an in vitro study using scanning electron microscopy.

PubMed

Marda, Preeti; Prakash, Shobha; Devaraj, C G; Vastardis, S

2012-01-01

The commonly accepted idea concerning root planing is that excessive removal of cementum is not necessary for removal of endotoxins. The ideal instrument should enable the removal of all extraneous substances from the root surfaces, without causing any iatrogenic effects. To compare the remaining calculus, loss of tooth substance, and roughness of root surface after root planing with Gracey curette, ultrasonic instrument (Slimline insert FSI-SLI-10S), and DesmoClean rotary bur. The efficiency of calculus removal, the amount of lost tooth substance, and root surface roughness resulting from the use of hand curette, ultrasonic instrument, and rotary bur on 36 extracted mandibular incisors were examined by SEM. We used three indices to measure the changes: Remaining calculus index (RCI), Loss of tooth substance index (LTSI), and Roughness loss of tooth substance index (RLTSI). Twelve samples were treated with each instrument. The time required for instrumentation was also noted. Kruskal-Wallis ANOVA was used for multiple group comparisons and the Mann-Whitney test for group-wise comparisons. Analysis was carried out with SPSS software (version 13). The RCI and LTSI showed nonsignificant differences between the three groups. RLTSI showed a significant difference between Slimline and hand curette as well as Slimline and Desmo-Clean. Slimline showed the least mean scores for RCI, LTSI, and RLTSI. Thus, even though the difference was not statistically significant, Slimline insert was shown to be better than the other methods as assessed by the indices scores and the instrumentation time.

Sources of fatty acids in Lake Michigan surface microlayers and subsurface waters

NASA Astrophysics Data System (ADS)

Meyers, Philip A.; Owen, Robert M.

1980-11-01

Fatty acid and organic carbon contents have been measured in the particulate and dissolved phases of surface microlayer and subsurface water samples collected from Lake Michigan. Concentrations are highest close to fluvial sources and lowest in offshore areas, yet surface/subsurface fractionation is lowest near river mouths and highest in open lake locations. These gradients plus accompanying fatty acid compositional changes indicate that river-borne organic materials are important constituents of coastal Lake Michigan microlayers and that sinking and turbulent resuspension of particulates affect surface film characteristics. Lake neuston and plankton contribute organic components which partially replace potamic materials removed by sinking.

Measurement of efficiency in calculus removal with a frequency-doubled Alexandrite laser on pigs' jaws

NASA Astrophysics Data System (ADS)

Pilgrim, Christian G.; Rechmann, Peter; Goldin, Dan S.; Hennig, Thomas

2000-03-01

Periodontal therapy aims in a most sufficient cleaning of tooth surfaces from supra- and subgingival calculus. As a standard dental procedure teeth are treated with ultrasonic devices. The competence of the frequency doubled Alexandrite laser for a highly effective and selective removal of calculus has been repeatedly proved. Aim of the study presented here was to determine the efficiency at simulated clinical conditions of the frequency doubled Alexandrite laser (laboratory prototype, q-switched, fiber guided, wavelength 377 nm, pulse duration 1 microsecond, pulse repetition rate 70 Hz, water cooling) by quantifying it's calculus removing efficiency. The evaluated data were compared to those obtained with an ultrasonic calculus remover. In the first part of the study sample material consisted of 23 pigs' jaws. They were divided into two groups. The teeth of one group were cleaned on their buccal surfaces using an ultrasonic device (Sonosoft Lux, KaVo, Biberach, Germany; tip #9). Than hand-guided cleaning was performed until no further improvement in cleanness was visible. Cleaning time was measured. Photographic documentation was taken before and after the treatment. The teeth in the second group were cleaned engaging a frequency doubled Alexandrite laser. Treatment time was measured and photographs were taken in the same way. In the second part of the study 21 surfaces of human teeth set up in an artificial pocket model were treated with both systems again. Measurements followed the same protocol. The results strongly support the use of the frequency doubled Alexandrite laser for calculus removal.

Focused-ion-beam-inflicted surface amorphization and gallium implantation--new insights and removal by focused-electron-beam-induced etching.

PubMed

Roediger, P; Wanzenboeck, H D; Waid, S; Hochleitner, G; Bertagnolli, E

2011-06-10

Recently focused-electron-beam-induced etching of silicon using molecular chlorine (Cl(2)-FEBIE) has been developed as a reliable and reproducible process capable of damage-free, maskless and resistless removal of silicon. As any electron-beam-induced processing is considered non-destructive and implantation-free due to the absence of ion bombardment this approach is also a potential method for removing focused-ion-beam (FIB)-inflicted crystal damage and ion implantation. We show that Cl(2)-FEBIE is capable of removing FIB-induced amorphization and gallium ion implantation after processing of surfaces with a focused ion beam. TEM analysis proves that the method Cl(2)-FEBIE is non-destructive and therefore retains crystallinity. It is shown that Cl(2)-FEBIE of amorphous silicon when compared to crystalline silicon can be up to 25 times faster, depending on the degree of amorphization. Also, using this method it has become possible for the first time to directly investigate damage caused by FIB exposure in a top-down view utilizing a localized chemical reaction, i.e. without the need for TEM sample preparation. We show that gallium fluences above 4 × 10(15) cm(-2) result in altered material resulting from FIB-induced processes down to a depth of ∼ 250 nm. With increasing gallium fluences, due to a significant gallium concentration close beneath the surface, removal of the topmost layer by Cl(2)-FEBIE becomes difficult, indicating that gallium serves as an etch stop for Cl(2)-FEBIE.

Towards defect free EUVL reticles: carbon and particle removal by single dry cleaning process and pattern repair by HIM

NASA Astrophysics Data System (ADS)

Koster, N. B.; Molkenboer, F. T.; van Veldhoven, E.; Oostrom, S.

2011-04-01

We report on our findings on EUVL reticle contamination removal, inspection and repair. We show that carbon contamination can be removed without damage to the reticle by our plasma process. Also organic particles, simulated by PSL spheres, can be removed from both the surface of the absorber as well as from the bottom of the trenches. The particles shrink in size during the plasma treatment until they are vanished. The determination of the necessary cleaning time for PSL spheres was conducted on Ru coated samples and the final experiment was performed on our dummy reticle. Finally we show that the Helium Ion Microscope in combination with a Gas Injection System is capable of depositing additional lines and squares on the reticle with sufficient resolution for pattern repair.

A statistical experiment design approach for optimizing biodegradation of weathered crude oil in coastal sediments.

PubMed

Mohajeri, Leila; Aziz, Hamidi Abdul; Isa, Mohamed Hasnain; Zahed, Mohammad Ali

2010-02-01

This work studied the bioremediation of weathered crude oil (WCO) in coastal sediment samples using central composite face centered design (CCFD) under response surface methodology (RSM). Initial oil concentration, biomass, nitrogen and phosphorus concentrations were used as independent variables (factors) and oil removal as dependent variable (response) in a 60 days trial. A statistically significant model for WCO removal was obtained. The coefficient of determination (R(2)=0.9732) and probability value (P<0.0001) demonstrated significance for the regression model. Numerical optimization based on desirability function were carried out for initial oil concentration of 2, 16 and 30 g per kg sediment and 83.13, 78.06 and 69.92 per cent removal were observed respectively, compare to 77.13, 74.17 and 69.87 per cent removal for un-optimized results.

Standard Operating Procedure for Surface Paint Sample Collection using a Modified Wood Drill Bit with a Variable Speed Portable Electric Drill

EPA Science Inventory

This standard operating procedure (SOP) describes a new, rapid, and relatively inexpensive way to remove a precise area of paint from the substrate of building structures in preparation for quantitative analysis. This method has been applied successfully in the laboratory, as we...

DEVELOPMENT OF A SAMPLING PROCEDURE FOR LARGE NITROGEN- AND SULFUR-BEARING AEROSOLS

EPA Science Inventory

A single-stage impactor was modified to utilize a removable TFE impaction surface mounted on the end of an annular denuder. hen used with a polycarbonate filter coated with silicone oil, its cut point was 2.5 um and bounce was <1% for 8-um particles. ignificant bounce occurred wi...

Spore trap analysis and MSQPCR in evaluating mold burden: a flooded gymnasium case study

EPA Science Inventory

A school gymnasium was accidentally flooded by the fire-suppression sprinkler system. The surface water was removed but after 25 days, the school decided to evaluate whether there was any mold growth in the gymnasium. Thirty, five-minute air samples (75 m3 air) were collected w...

Effect of sonic vibration of an ultrasonic toothbrush on the removal of Streptococcus mutans biofilm from enamel surface.

PubMed

Hashizume, Lina Naomi; Dariva, Alessandra

2015-12-01

To evaluate in vitro the effect of sonic vibration of an ultrasonic toothbrush in the removal of Streptococcus mutans (S. mutans) biofilm from human enamel. S. mutans dental biofilm was formed in vitro on human enamel blocks coated by salivary pellicle. The blocks were incubated with a suspension of S. mutans at 37°C for 24 or 72 hours. The blocks were divided to one of three conditions according to the different toothbrush action modes: ultrasound plus sonic vibration (U+SV), ultrasound-only (U) and no ultrasound and no sonic vibration (control). Samples were exposed to each mode for 3 minutes with the toothbrush bristles placed 5 mm away from the enamel block surface. The samples were observed by scanning electron microscopy (SEM) and quantification of S. mutans was performed. U+SV showed lower bacterial counts compared to U and control on the 72 hour-biofilm (P < 0.05). The SEM analysis revealed that U+SV and U disrupted the S. mutans chains in the 24- and 72-hour biofilm.

Suitability of pharmaceuticals and personal care products (PPCPs) and artificial sweeteners (ASs) as wastewater indicators in the Pearl River Delta, South China.

PubMed

Yang, Yuan-Yuan; Liu, Wang-Rong; Liu, You-Sheng; Zhao, Jian-Liang; Zhang, Qian-Qian; Zhang, Min; Zhang, Jin-Na; Jiang, Yu-Xia; Zhang, Li-Juan; Ying, Guang-Guo

2017-07-15

Wastewater indicator is a useful tool for evaluating the wastewater impact on natural water, but there is little information about the suitability of wastewater indicators for different regions. This study aimed to select suitable wastewater indicators in the Pearl River Delta region, south China by screening a range of wastewater related organic compounds. The screening campaign was carried out by investigating the occurrence and removal efficiencies of 93 pharmaceuticals and personal care products (PPCPs) and 5 artificial sweeteners (ASs) in nine wastewater treatment plants (WWTPs) located in the region, and the occurrence of these target compounds in the contaminated and clean surface water of the Pearl River. An ideal wastewater indicator should be hydrophilic, source-specific for domestic wastewater, ubiquitous in contaminated surface water with detection frequency (DF) >80% and absent in background water samples. For liable indicators, high removal rates (>90%) should be observed in WWTPs and they should be detected in all the influent samples at concentrations fifty times higher than their limits of quantification. For conservative indicators, low removal rates (<50%) should be observed in WWTPs and they should be detected in all the effluent samples at concentrations fifty times higher than their limits of quantification. Based on the above criteria, sucralose and fluconazole were selected as conservative indicators in the region, while cyclamate, saccharin, methyl paraben, ethyl paraben, propyl paraben, paracetamol, salicylic acid and caffeine were selected as liable indicators. Copyright © 2017 Elsevier B.V. All rights reserved.

Optimization technique for rolled edge control process based on the acentric tool influence functions.

PubMed

Du, Hang; Song, Ci; Li, Shengyi; Xu, Mingjin; Peng, Xiaoqiang

2017-05-20

In the process of computer controlled optical surfacing (CCOS), the uncontrollable rolled edge restricts further improvements of the machining accuracy and efficiency. Two reasons are responsible for the rolled edge problem during small tool polishing. One is that the edge areas cannot be processed because of the orbit movement. The other is that changing the tool influence function (TIF) is difficult to compensate for in algorithms, since pressure step appears in the local pressure distribution at the surface edge. In this paper, an acentric tool influence function (A-TIF) is designed to remove the rolled edge after CCOS polishing. The model of A-TIF is analyzed theoretically, and a control point translation dwell time algorithm is used to verify that the full aperture of the workpiece can be covered by the peak removal point of the tool influence functions. Thus, surface residual error in the full aperture can be effectively corrected. Finally, the experiments are carried out. Two fused silica glass samples of 100  mm×100  mm are polished by traditional CCOS and the A-TIF method, respectively. The rolled edge was clearly produced in the sample polished by the traditional CCOS, while residual errors do not show this problem the sample polished by the A-TIF method. Therefore, the rolled edge caused by the traditional CCOS process is successfully suppressed during the A-TIF process. The ability to suppress the rolled edge of the designed A-TIF has been confirmed.

[Parameters optimization and cleaning efficiency evaluation of attrition scrubbing remediation of Pb-contaminated soil].

PubMed

Yang, Wen; Huang, Jin-lou; Peng, Hui-qing; Li, Si-tuo

2013-09-01

Attrition scrubbing was used to remediate lead contaminated-site soil, and the main purpose was to remove fine particles and lead contaminants from the surface of sand. The optimal parameters of attrition scrubbing were determined by orthogonal experiment, and three soil samples with different lead concentration were subjected to attrition scrubbing experiments. The results showed that the optimal scrubbing parameters were: a solid ratio of 70% dry matter, a temperature of 25 degrees C, an attrition time of 30 min, and an attrition speed of 1200 r x min(-1). Before attrition scrubbing, the screening and analysis of soil showed that in all three soil samples, lead was mainly enriched on sand and fine particles, and the distribution of lead was highly correlated to the organic matter. After attrition scrubbing, the washing efficiency of the original state lead contaminated sand soil in triplicates was 67.61%, 31.71% and 41.01%, respectively, which indicates that attrition scrubbing can remove part of the fine soil and lead contaminants from the surface of sand, to accomplish the purpose of pollutants enrichment. Scanning electron microscopy (SEM) analysis showed that the sand surface became smooth after attrition scrubbing. The results above show that attrition scrubbing has a good washing effect for the remediation of lead contaminated sand soil.

Surface passivation and aging of InGaAs/InP heterojunction phototransistors

NASA Astrophysics Data System (ADS)

Park, Min-Su; Razaei, Mohsen; Barnhart, Katie; Tan, Chee Leong; Mohseni, Hooman

2017-06-01

We report the effect of different surface treatment and passivation techniques on the stability of InGaAs/InP heterojunction phototransistors (HPTs). An In0.53Ga0.47As surface passivated with aqueous ammonium sulfide ((NH4)2S), aluminum oxide (Al2O3) grown by atomic layer deposition (ALD), and their combination is evaluated by using Raman spectroscopy and X-ray photoelectron spectroscopy (XPS). All samples were kept in the air ambient, and their performances were periodically measured to investigate their long-term stability. Raman spectroscopy revealed that the peak intensity of the GaAs-like longitudinal optical phonon of all passivated samples is decreased compared with that of the control sample. This is attributable to the diminution of the carriers near the passivated surfaces, which was proven by extracted surface potential (Vs). The Vs of all passivated samples was decreased to less than half of that for the control sample. XPS evaluation of As3d spectra showed that arsenic oxides (As2O3 and As2O5) on the surfaces of the samples can be removed by passivation. However, both Raman and XPS spectra show that the (NH4)2S passivated sample reverts back over time and will resemble the untreated control sample. When capped with ALD-grown Al2O3, passivated samples irrespective of the pretreatment show no degradation over the measured time of 4 weeks. Similar conclusions are made from our experimental measurement of the performance of differently passivated HPTs. The ALD-grown Al2O3 passivated devices show an improved optical gain at low optical powers and long-term stability.

Validation of Sampling Protocol and the Promulgation of Method Modifications for the Characterization of Energetic Residues on Military Testing and Training Ranges

DTIC Science & Technology

2009-06-01

Figure 2. Examples of surface vegetation at a firing point (inset) and near the crater of an 81-mm mortar projectile low-order detonation on an artillery... mortar impact range.......................... 7 Figure 3. Fort Richardson and surrounding areas...crater where an 81-mm mortar projectile had low-ordered on an impact range. If vegetation is removed or avoided during sampling, energetic residue

Comparison of the impact of scaler material composition on polished titanium implant abutment surfaces.

PubMed

Hasturk, Hatice; Nguyen, Daniel Huy; Sherzai, Homa; Song, Xiaoping; Soukos, Nikos; Bidlack, Felicitas B; Van Dyke, Thomas E

2013-08-01

The purpose of this study was to compare the impact of the removal of biofilm with hand scalers of different material composition on the surface of implant abutments by assessing the surface topography and residual plaque after scaling using scanning electron microscopy (SEM). Titanium implant analogs from 3 manufacturers (Straumann USA LLC, Andover, Maine, Nobel BioCare USA LLC, Yorba Linda, Cali, Astra Tech Implant Systems, Dentsply, Mölndal, Sweden) were mounted in stone in plastic vials individually with authentic prosthetic abutments. Plaque samples were collected from a healthy volunteer, inoculated into growth medium and incubated with the abutments anaerobically for 1 week. A blinded, calibrated hygienist performed scaling to remove the biofilm using 6 implant scalers (in triplicate), 1 scaler for 1 abutment. The abutments were mounted on an imaging stand and processed for SEM. Images were captured in 3 randomly designated areas of interest on each abutment. Analysis of the implant polished abutment surface and plaque area measurements were performed using ImageJ image analysis software. Surface alterations were characterized by the number, length, depth and the width of the scratches observed. Glass filled resin scalers resulted in significantly more and longer scratches on all 3 abutment types compared to other scalers, while unfilled resin scalers resulted in the least surface change (p < 0.05). Filled resin-graphite reinforced scalers, carbon fiber reinforced resin scalers and titanium scalers resulted in more superficial scratches compared to glass filled resin, as well as more scratches than unfilled resin. No statistically significant differences were found between scalers and abutments with regard to plaque removal. The impact of scalers on implant abutment surfaces varies between abutment types presumably due to different surface characteristics with no apparent advantage of one abutment type over the other with regard to resistance to surface damage. Unfilled resin was found consistently to be the least damaging to abutment surfaces, although all scalers of all compositions caused detectable surface changes to polished surfaces of implant abutments.

Magnetic hydroxyapatite nanoparticles: an efficient adsorbent for the separation and removal of nitrate and nitrite ions from environmental samples.

PubMed

Ghasemi, Ensieh; Sillanpää, Mika

2015-01-01

A novel type of magnetic nanosorbent, hydroxyapatite-coated Fe2O3 nanoparticles was synthesized and used for the adsorption and removal of nitrite and nitrate ions from environmental samples. The properties of synthesized magnetic nanoparticles were characterized by scanning electron microscopy, Fourier transform infrared spectroscopy, and X-ray powder diffraction. After the adsorption process, the separation of γ-Fe2O3@hydroxyapatite nanoparticles from the aqueous solution was simply achieved by applying an external magnetic field. The effects of different variables on the adsorption efficiency were studied simultaneously using an experimental design. The variables of interest were amount of magnetic hydroxyapatite nanoparticles, sample volume, pH, stirring rate, adsorption time, and temperature. The experimental parameters were optimized using a Box-Behnken design and response surface methodology after a Plackett-Burman screening design. Under the optimum conditions, the adsorption efficiencies of magnetic hydroxyapatite nanoparticles adsorbents toward NO3(-) and NO2(-) ions (100 mg/L) were in the range of 93-101%. The results revealed that the magnetic hydroxyapatite nanoparticles adsorbent could be used as a simple, efficient, and cost-effective material for the removal of nitrate and nitrite ions from environmental water and soil samples. © 2014 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

A method to calibrate phase fluctuation in polarization-sensitive swept-source optical coherence tomography

NASA Astrophysics Data System (ADS)

Lu, Zenghai; Kasaragod, Deepa K.; Matcher, Stephen J.

2011-06-01

A phase fluctuation calibration method is presented for polarization-sensitive swept-source optical coherence tomography (PS-SS-OCT) using continuous polarization modulation. The method consists of the generation of a continuous triggered tone-burst waveform rather than an asynchronous waveform by use of a function generator and the removal of the global phases of the measured Jones matrices by use of matrix normalization. This could remove the use of auxiliary optical components for the phase fluctuation compensation in the system, which reduces the system complexity. Phase fluctuation calibration is necessary to obtain the reference Jones matrix by averaging the measured Jones matrices at sample surfaces. Measurements on an equine tendon sample were made by the PS-SS-OCT system to validate the proposed method.

Revisiting the iron pools in cucumber roots: identification and localization.

PubMed

Kovács, Krisztina; Pechoušek, Jiří; Machala, Libor; Zbořil, Radek; Klencsár, Zoltán; Solti, Ádám; Tóth, Brigitta; Müller, Brigitta; Pham, Hong Diep; Kristóf, Zoltán; Fodor, Ferenc

2016-07-01

Fe deficiency responses in Strategy I causes a shift from the formation of partially removable hydrous ferric oxide on the root surface to the accumulation of Fe-citrate in the xylem. Iron may accumulate in various chemical forms during its uptake and assimilation in roots. The permanent and transient Fe microenvironments formed during these processes in cucumber which takes up Fe in a reduction based process (Strategy I) have been investigated. The identification of Fe microenvironments was carried out with (57)Fe Mössbauer spectroscopy and immunoblotting, whereas reductive washing and high-resolution microscopy was applied for the localization. In plants supplied with (57)Fe(III)-citrate, a transient presence of Fe-carboxylates in removable forms and the accumulation of partly removable, amorphous hydrous ferric oxide/hydroxyde have been identified in the apoplast and on the root surface, respectively. The latter may at least partly be the consequence of bacterial activity at the root surface. Ferritin accumulation did not occur at optimal Fe supply. Under Fe deficiency, highly soluble ferrous hexaaqua complex is transiently formed along with the accumulation of Fe-carboxylates, likely Fe-citrate. As (57)Fe-citrate is non-removable from the root samples of Fe deficient plants, the major site of accumulation is suggested to be the root xylem. Reductive washing results in another ferrous microenvironment remaining in the root apoplast, the Fe(II)-bipyridyl complex, which accounts for ~30 % of the total Fe content of the root samples treated for 10 min and rinsed with CaSO4 solution. When (57)Fe(III)-EDTA or (57)Fe(III)-EDDHA was applied as Fe-source higher soluble ferrous Fe accumulation was accompanied by a lower total Fe content, confirming that chelates are more efficient in maintaining soluble Fe in the medium while less stable natural complexes as Fe-citrate may perform better in Fe accumulation.

Mechanic and surface properties of central-venous port catheters after removal: A comparison of polyurethane and silicon rubber materials.

PubMed

Braun, Ulrike; Lorenz, Edelgard; Weimann, Christiane; Sturm, Heinz; Karimov, Ilham; Ettl, Johannes; Meier, Reinhard; Wohlgemuth, Walter A; Berger, Hermann; Wildgruber, Moritz

2016-12-01

Central venous port devices made of two different polymeric materials, thermoplastic polyurethane (TPU) and silicone rubber (SiR), were compared due their material properties. Both naïve catheters as well as catheters after removal from patients were investigated. In lab experiments the influence of various chemo-therapeutic solutions on material properties was investigated, whereas the samples after removal were compared according to the implanted time in patient. The macroscopic, mechanical performance was assessed with dynamic, specially adapted tests for elasticity. The degradation status of the materials was determined with common tools of polymer characterisation, such as infrared spectroscopy, molecular weight measurements and various methods of thermal analysis. The surface morphology was analysed using scanning electron microscopy. A correlation between material properties and clinical performance was proposed. The surface morphology and chemical composition of the polyurethane catheter materials can potentially result in increased susceptibility of the catheter to bloodstream infections and thrombotic complications. The higher mechanic failure, especially with increasing implantation time of the silicone catheters is related to the lower mechanical performance compared to the polyurethane material as well as loss of barium sulphate filler particles near the surface of the catheter. This results in preformed microscopic notches, which act as predetermined sites of fracture. Copyright © 2016 Elsevier Ltd. All rights reserved.

Comparative study of pulsed laser cleaning applied to weathered marble surfaces

NASA Astrophysics Data System (ADS)

Ortiz, P.; Antúnez, V.; Ortiz, R.; Martín, J. M.; Gómez, M. A.; Hortal, A. R.; Martínez-Haya, B.

2013-10-01

The removal of unwanted matter from surface stones is a demanding task in the conservation of cultural heritage. This paper investigates the effectiveness of near-infrared (IR) and ultraviolet (UV) laser pulses for the cleaning of surface deposits, iron oxide stains and different types of graffiti (black, red and green sprays and markers, and black cutting-edge ink) on dolomitic white marble. The performance of the laser techniques is compared to common cleaning methods on the same samples, namely pressurized water and chemical treatments. The degree of cleaning achieved with each technique is assessed by means of colorimetric measurements and X-ray microfluorescence. Eventual morphological changes induced on the marble substrate are monitored with optical and electronic microscopy. It is found that UV pulsed laser ablation at 266 nm manages to clean all the stains except the cutting-edge ink, although some degree of surface erosion is produced. The IR laser pulses at 1064 nm can remove surface deposits and black spray acceptably, but a yellowing is observed on the stone surface after treatment. An economic evaluation shows that pulsed laser cleaning techniques are advantageous for the rapid cleaning of small or inaccessible surface areas, although their extensive application becomes expensive due to the long operating times required.

Adsorption of basic Red 46 using sea mango (Cerbera odollam) based activated carbon

DOE Office of Scientific and Technical Information (OSTI.GOV)

Azmi, Nur Azira Iqlima; Zainudin, Nor Fauziah; Ali, Umi Fazara Md

Sea mango or Cerbera Odollam is another source of carbonaceous material that can be found abundantly in Malaysia. In this research, it is used as a new agricultural source of activated carbon. Sea mango activated carbon was prepared by chemical activation using potassium hydroxide (KOH). The sea mango was soaked in KOH at impregnation ratio of 1:1 and followed by carbonization at temperature of 600°C for 1 hour. The sample was then characterized using Scanning Electron Microscope (SEM) for surface morphology, while Brunauer-Emmett-Teller (BET) was used to study the surface area. The result shown that sea mango activated carbon (SMAC)more » developed new pores on its surface and the BET surface area measured was 451.87 m{sup 2}/g. The SMAC performance was then tested for the removal of Basic Red 46 in batch process. The removal of Basic Red 46 (50 mg/L, natural pH, 0.1 g SMAC) was more than 99% in 15 minutes where it reached equilibrium in 30 minutes.« less

Perchlorate: Health Effects and Technologies for Its Removal from Water Resources

PubMed Central

Srinivasan, Asha; Viraraghavan, Thiruvenkatachari

2009-01-01

Perchlorate has been found in drinking water and surface waters in the United States and Canada. It is primarily associated with release from defense and military operations. Natural sources include certain fertilizers and potash ores. Although it is a strong oxidant, perchlorate is very persistent in the environment. At high concentrations perchlorate can affect the thyroid gland by inhibiting the uptake of iodine. A maximum contaminant level has not been set, while a guidance value of 6 ppb has been suggested by Health Canada. Perchlorate is measured in environmental samples primarily by ion chromatography. It can be removed from water by anion exchange or membrane filtration. Biological and chemical processes are also effective in removing this species from water. PMID:19440526

Characterization of Uranium Contamination, Transport, and Remediation at Rocky Flats - Across Remediation into Post-Closure

NASA Astrophysics Data System (ADS)

Janecky, D. R.; Boylan, J.; Murrell, M. T.

2009-12-01

The Rocky Flats Site is a former nuclear weapons production facility approximately 16 miles northwest of Denver, Colorado. Built in 1952 and operated by the Atomic Energy Commission and then Department of Energy, the Site was remediated and closed in 2005, and is currently undergoing long-term surveillance and monitoring by the DOE Office of Legacy Management. Areas of contamination resulted from roughly fifty years of operation. Of greatest interest, surface soils were contaminated with plutonium, americium, and uranium; groundwater was contaminated with chlorinated solvents, uranium, and nitrates; and surface waters, as recipients of runoff and shallow groundwater discharge, have been contaminated by transport from both regimes. A region of economic mineralization that has been referred to as the Colorado Mineral Belt is nearby, and the Schwartzwalder uranium mine is approximately five miles upgradient of the Site. Background uranium concentrations are therefore elevated in many areas. Weapons-related activities included work with enriched and depleted uranium, contributing anthropogenic content to the environment. Using high-resolution isotopic analyses, Site-related contamination can be distinguished from natural uranium in water samples. This has been instrumental in defining remedy components, and long-term monitoring and surveillance strategies. Rocky Flats hydrology interlinks surface waters and shallow groundwater (which is very limited in volume and vertical and horizontal extent). Surface water transport pathways include several streams, constructed ponds, and facility surfaces. Shallow groundwater has no demonstrated connection to deep aquifers, and includes natural preferential pathways resulting primarily from porosity in the Rocky Flats alluvium, weathered bedrock, and discontinuous sandstones. In addition, building footings, drains, trenches, and remedial systems provide pathways for transport at the site. Removal of impermeable surfaces (buildings, roads, and so on) during the Site closure efforts resulted in major changes to surface and shallow groundwater flow. Consistent with previous documentation of uranium operations and contamination, only very small amounts of highly enriched uranium are found in a small number of water samples, generally from the former Solar Ponds complex and central Industrial Area. Depleted uranium is more widely distributed at the site, and water samples exhibit the full range of depleted plus natural uranium mixtures. However, one third of the samples are found to contain only natural uranium, and three quarters of the samples are found to contain more than 90% natural uranium - substantial fractions given that the focus of these analyses was on evaluating potentially contaminated waters. Following site closure, uranium concentrations have increased at some locations, particularly for surface water samples. Overall, isotopic ratios at individual locations have been relatively consistent, indicating that the increases in concentrations are due to decreases in dilution flow following removal of impermeable surfaces and buildings.

Pegasus International, Inc. coating removal systems

DOE Office of Scientific and Technical Information (OSTI.GOV)

NONE

1998-02-01

The Pegasus Coating Removal System (PCRS) was demonstrated at Florida International University (FIU) where it was being evaluated for efficiency and cost. In conjunction with the FIU testing demonstration, a human factors assessment was conducted to assess the hazards and associated safety and health issues of concern for workers utilizing this technology. The PCRS is a chemical paste that is applied to the surface using a brush, roller, or airless sprayer. After the type of PCRS, thickness, and dwell time have been determined, a laminated backed material is placed on top of the chemical paste to slow down the dryingmore » process and to provide a mechanism to strip-off the chemical. After the dwell time is reached, the chemical substrate can be removed. Scrapers may be used to break-loose the layers as necessary or to break-loose the layers that are not removed when the laminated paper is picked up. Residue may also be cleaned off of the surface with a damp sponge with an agitating motion, absorbent sponges, or a vacuum, as needed. The paint and removal agent is then placed in drums for disposal at a later time. During the assessment sampling was conducted for organic vapors and general observational techniques were conducted for ergonomics. Recommendations for improved worker safety and health during application and removal of the PCRS include: (1) work practices that reflect avoidance of exposure or reducing the risk of exposure; (2) assuring all PPE and equipment are compatible with the chemicals being used; (3) work practices that reduce the worker`s need to walk on the slippery surface caused by the chemical or the use of special anti-slip soles; (4) careful control of overspray (if a spray application is used); and (5) the use of ergonomically designed long-handled tools to apply and remove the chemical (to alleviate some of the ergonomic concerns).« less

Method for removing tilt control in adaptive optics systems

DOEpatents

Salmon, J.T.

1998-04-28

A new adaptive optics system and method of operation are disclosed, whereby the method removes tilt control, and includes the steps of using a steering mirror to steer a wavefront in the desired direction, for aiming an impinging aberrated light beam in the direction of a deformable mirror. The deformable mirror has its surface deformed selectively by means of a plurality of actuators, and compensates, at least partially, for existing aberrations in the light beam. The light beam is split into an output beam and a sample beam, and the sample beam is sampled using a wavefront sensor. The sampled signals are converted into corresponding electrical signals for driving a controller, which, in turn, drives the deformable mirror in a feedback loop in response to the sampled signals, for compensating for aberrations in the wavefront. To this purpose, a displacement error (gradient) of the wavefront is measured, and adjusted by a modified gain matrix, which satisfies the following equation: G{prime} = (I{minus}X(X{sup T} X){sup {minus}1}X{sup T})G(I{minus}A). 3 figs.

Creation of fluorocarbon barriers on surfaces of starch-based products through cold plasma treatment

NASA Astrophysics Data System (ADS)

Han, Yousoo

Two kinds of starch foam trays (starch and aspen-starch foam trays) were produced using a lab model baking machine. Surfaces of the trays were treated with CF4 and SF6 plasma to create fluorine-rich layers on the surfaces, which might show strong water resistance. The plasma parameters, such like RF power, gas pressure and reaction time, were varied to evaluate the effects of each parameter on fluorination of surfaces. The atomic concentrations of fluorine, oxygen and carbon on samples' surfaces were earned from ESCA (electron spectroscopy for chemical analysis) and contact angles of sample surfaces were measured for hydrophobicity. For water resistance of plasma treated surfaces, liquid water uptake and water vapor uptake test were performed. Also, equilibrium moisture contents of unmodified and plasma treated samples were measured to evaluate biodegradability of plasma treated samples. Fluorine-rich barriers were created on sample surfaces treated with CF 4 and SF6 plasma. The fluorine atomic concentrations of treated sample surfaces were ranged from 34.4% to 64.4% (CF4 treatment) and 43.6% to 57.9% (SF6 treatment). It was found at both plasma gases that plasma parameters affected total fluorine concentration and carbon-peak shapes in ESCA surveys, which imply different distributions of mono- or multi-fluoro carbon's contents. In various reaction times, it was found that total fluorine contents were decreased after a critical point as the reaction time was prolonged, which may imply that a dominant mechanism has been changed from deposition or functionalization to etching. Oxygen atomic concentration was decreased at sample surfaces treated by both plasmas. In the case of SF6 plasma, it was proved that the removal of oxygen surely occurred because there was no addition of sulfur species. Plasma treated sample surfaces had high contact angles with distilled water up to 150° and the high values of angles have been kept constant up to for 15 minutes. Fluorine-rich barriers created by plasma showed lower water liquid and vapor permeability than untreated surfaces did. Plasma treated samples had similar moisture contents with untreated samples at all relative humidity tested. AFM and SEM images were taken for sample surfaces' morphology and topography.

One-year Surveillance of Human Enteric Viruses in Raw and Treated Wastewaters, Downstream River Waters, and Drinking Waters.

PubMed

Iaconelli, M; Muscillo, M; Della Libera, S; Fratini, M; Meucci, L; De Ceglia, M; Giacosa, D; La Rosa, G

2017-03-01

Human enteric viruses are a major cause of waterborne diseases, and can be transmitted by contaminated water of all kinds, including drinking and recreational water. The objectives of the present study were to assess the occurrence of enteric viruses (enterovirus, norovirus, adenovirus, hepatitis A and E virus) in raw and treated wastewaters, in rivers receiving wastewater discharges, and in drinking waters. Wastewater treatment plants' (WWTP) pathogen removal efficiencies by adenovirus quantitative real-time PCR and the presence of infectious enterovirus, by cell culture assays, in treated wastewaters and in surface waters were also evaluated. A total of 90 water samples were collected: raw and treated wastewaters (treated effluents and ultrafiltered water reused for industrial purposes), water from two rivers receiving treated discharges, and drinking water. Nested PCR assays were used for the identification of viral DNA/RNA, followed by direct amplicon sequencing. All raw sewage samples (21/21), 61.9 % of treated wastewater samples (13/21), and 25 % of ultrafiltered water samples (3/12) were contaminated with at least one viral family. Multiple virus families and genera were frequently detected. Mean positive PCRs per sample decreased significantly from raw to treated sewage and to ultrafiltered waters. Moreover, quantitative adenovirus data showed a reduction in excess of 99 % in viral genome copies following wastewater treatment. In surface waters, 78.6 % (22/28) of samples tested positive for one or more viruses by molecular methods, but enterovirus-specific infectivity assays did not reveal infectious particles in these samples. All drinking water samples tested negative for all viruses, demonstrating the effectiveness of treatment in removing viral pathogens from drinking water. Integrated strategies to manage water from all sources are crucial to ensure water quality.

Development and evaluation of a gas chromatographic method for the determination of triazine herbicides in natural water samples

USGS Publications Warehouse

Steinheimer, T.R.; Brooks, M.G.

1984-01-01

A multi-residue method is described for the determination of triazine herbicides in natural water samples. The technique uses solvent extraction followed by gas chromatographic separation and detection employing nitrogen-selective devices. Seven compounds can be determined simultaneously at a nominal detection limit of 0.1 ??g/L in a 1-litre sample. Three different natural water samples were used for error analysis via evaluation of recovery efficiencies and estimation of overall method precision. As an alternative to liquid-liquid partition (solvent extraction) for removal of compounds of interest from water, solid-phase extraction (SPE) techniques employing chromatographic grade silicas with chemically modified surfaces have been examined. SPE is found to provide rapid and efficient concentration with quantitative recovery of some triazine herbicides from natural water samples. Concentration factors of 500 to 1000 times are obtained readily by the SPE technique.A multi-residue method is described for the determination of triazine herbicides in natural water samples. The technique uses solvent extraction followed by gas chromatographic separation and detection employing nitrogen-selective devices. Seven compounds can be determined simultaneously at a nominal detection limit of 0. 1 mu g/L in a 1-litre sample. As an alternative to liquid-liquid partition (solvent extraction) for removal of compounds of interest from water, solid-phase extraction (SPE) techniques employing chromatographic grade silicas with chemically modified surfaces have been examined. SPE is found to provide rapid and efficient concentration with quantitative recovery of some triazine herbicides from natural water samples. Concentration factors of 500 to 1000 times are obtained readily by the SPE technique.

Non-iterative determination of the stress-density relation from ramp wave data through a window

NASA Astrophysics Data System (ADS)

Dowling, Evan; Fratanduono, Dayne; Swift, Damian

2017-06-01

In the canonical ramp compression experiment, a smoothly-increasing load is applied the surface of the sample, and the particle velocity history is measured at interfaces two or more different distances into the sample. The velocity histories are used to deduce a stress-density relation by correcting for perturbations caused by reflected release waves, usually via the iterative Lagrangian analysis technique of Rothman and Maw. We previously described a non-iterative (recursive) method of analysis, which was more stable and orders of magnitude faster than iteration, but was subject to the limitation that the free surface velocity had to be sampled at uniform intervals. We have now developed more general recursive algorithms suitable for analyzing ramp data through a finite-impedance window. Free surfaces can be treated seamlessly, and the need for uniform velocity sampling has been removed. These calculations require interpolation of partially-released states using the partially-constructed isentrope, making them slower than the previous free-surface scheme, but they are still much faster than iterative analysis. This work was performed under the auspices of the U.S. Department of Energy by Lawrence Livermore National Laboratory under Contract DE-AC52-07NA27344.

Year-long evaluation on the occurrence and fate of pharmaceuticals, personal care products, and endocrine disrupting chemicals in an urban drinking water treatment plant.

PubMed

Padhye, Lokesh P; Yao, Hong; Kung'u, Francis T; Huang, Ching-Hua

2014-03-15

The occurrence and removal of thirty representative pharmaceutical and personal care products (PPCPs) and endocrine disrupting chemicals (EDCs) in an urban drinking water treatment plant (DWTP) were investigated for a period of one year to evaluate current system's treatment efficacy and assess occurrence of PPCPs and EDCs in finished drinking water. Results showed that the average total PPCPs and EDCs concentration in the surface water source was around 360 ng/L (median concentration = 340 ng/L) with 57% coefficient of variation (CV). The median concentrations of most of the individual PPCPs and EDCs in the surface water were below 15 ng/L except for N,N-diethyltoluamide (DEET) and nonylphenol, which were at 122 and 83 ng/L, respectively. The compounds DEET, nonylphenol, ibuprofen, triclosan, atrazine, tris(2-chloroethyl)-phosphate (TCEP), bisphenol-A, and caffeine (in the order of decreasing median concentration) were among twenty compounds detected at least once in the surface water, while all of the above detected compounds, except two, were also detected in the finished drinking water. The average total PPCPs and EDCs concentration in the finished drinking water was around 98 ng/L (median concentration = 96 ng/L) with 66% CV. The median concentrations of most detected PPCPs and EDCs in drinking water were below 5 ng/L except for DEET and nonylphenol, which were at 12 and 20 ng/L, respectively. There was a strong correlation (r = 0.97) between PPCPs and EDCs' concentrations in the source water and in the drinking water over the one-year study period when data points from two sampling events with unusual removals were excluded. Individual water treatment unit processes showed greater temporal variations of PPCPs and EDCs removal efficiencies than the overall treatment processes. The removal efficiencies also varied greatly among different PPCPs and EDCs. The average removal for total PPCPs and EDCs was 76 ± 18% at the DWTP, with ozonation showing the highest removal efficiency. Based on the similar occurrence and removal trends observed as that of total PPCPs and EDCs in this study, DEET and nonylphenol can be considered as potential indicator compounds for predicting the occurrence and removal of total PPCPs and EDCs in surface water. No strong correlations could be found between total PPCPs and EDCs removal and the removal of suspended solids, turbidity, or organic carbon. Copyright © 2013 Elsevier Ltd. All rights reserved.

Preparation and Characterization of Activated Cow Bone Powder for the Adsorption of Cadmium from Palm Oil Mill Effluent

NASA Astrophysics Data System (ADS)

AbdulRahman, A.; Latiff, A. A. A.; Daud, Z.; Ridzuan, M. B.; D, N. F. M.; Jagaba, A. H.

2016-07-01

Several studies have been conducted on the removal of heavy metals from palm oil mill effluent. In this study, cow bones were developed as an adsorbent for the removal of cadmium II from POME. A batch experiment was conducted to investigate the effectiveness of the prepared activated cow bone powder for the sorption of cadmium II from raw POME. The experiment was carried out under fixed conditions using 100mg/L raw POME combined with different adsorbent dosage of CBP of 184.471 Ra(nm) surface roughness. The equilibrium adsorption capacity of the hydrophobic CBP of average contact angle 890 was determined from the relationship between the initial and equilibrium liquid phase concentrations of POME. The optimum adsorption of cadmium II on CBP was at 10g adsorbent dosage for sample 1 and 2 at 97.8% and 96.93% respectively. The least uptake was at 30g adsorbent weight for both samples at average of 95.1% for both samples. The effective removal of cadmium ion showed that CBP has a great potential for the treatment of heavy metal in POME.

The behaviour of linear alkyl benzene sulphonate under direct discharge conditions in Vientiane, Lao PDR.

PubMed

Whelan, M J; Van Egmond, R; Guymer, I; Lacoursière, J O; Vought, L M B; Finnegan, C; Fox, K K; Sparham, C; O'Connor, S; Vaughan, M; Pearson, J M

2007-12-01

Direct discharge of untreated sewage to surface waters is a common practice in many parts of the world. However, relatively little is known about the behaviour of synthetic organic pollutants under these conditions. This paper describes a sampling campaign designed to track changes in water quality in a surface water system in Vientiane (Lao PDR) receiving significant quantities of untreated waste water. The study was based on following in-channel transport using a fluorescent tracer injected as a pulse, with a focus on the anionic surfactant linear alkylbenzene sulphonate (LAS) and ammonia. Water samples were collected at a number of stations with sampling times estimated to coincide with solute time-of-travel. The reduction in LAS concentration with flow-time could be approximated by first-order kinetics with a half life of about 7 h. Free ammonia concentrations decreased more slowly than LAS and remained above the level believed to be toxic for sensitive aquatic species along the entire channel. Changes in the ratios of LAS alkyl chain homologues to total LAS concentrations suggest a preferential removal of longer chain lengths. The role of biodegradation in the removal of LAS was confirmed by the presence of LAS metabolites (sulphophenylcarboxylates, SPCs) which increased systematically (as a fraction of LAS remaining) with flow-time.

Electron spectroscopy imaging and surface defect configuration of zinc oxide nanostructures under different annealing ambient

NASA Astrophysics Data System (ADS)

Ann, Ling Chuo; Mahmud, Shahrom; Bakhori, Siti Khadijah Mohd

2013-01-01

In this study, electron spectroscopy imaging was used to visualize the elemental distribution of zinc oxide nanopowder. Surface modification in zinc oxide was done through annealing treatment and type of surface defect was also inferred from the electron spectroscopy imaging investigation. The micrographs revealed the non-stoichiometric distribution of the elements in the unannealed samples. Annealing the samples in nitrogen and oxygen ambient at 700 °C would alter the density of the elements in the samples as a result of removal or absorption of oxygen. The electrical measurement showed that nitrogen annealing treatment improved surface electrical conductivity, whereas oxygen treatment showed an adverse effect. Observed change in the photoluminescence green emission suggested that oxygen vacancies play a significant role as surface defects. Structural investigation carried out through X-ray diffraction revealed the polycrystalline nature of both zinc oxide samples with hexagonal phase whereby annealing process increased the crystallinity of both zinc oxide specimens. Due to the different morphologies of the two types of zinc oxide nanopowders, X-ray diffraction results showed different stress levels in their structures and the annealing treatment give significant effect to the structural stress. Electron spectroscopy imaging was a useful technique to identify the elemental distribution as well as oxygen defect in zinc oxide nanopowder.

Angular analysis of the cyclic impacting oscillations in a robotic grinding process

NASA Astrophysics Data System (ADS)

Rafieian, Farzad; Girardin, François; Liu, Zhaoheng; Thomas, Marc; Hazel, Bruce

2014-02-01

In a robotic machining process, a light-weight cutter or grinder is usually held by an articulated robot arm. Material removal is achieved by the rotating cutting tool while the robot end effector ensures that the tool follows a programmed trajectory in order to work on complex curved surfaces or to access hard-to-reach areas. One typical application of such process is maintenance and repair work on hydropower equipment. This paper presents an experimental study of the dynamic characteristics of material removal in robotic grinding, which is unlike conventional grinding due to the lower structural stiffness of the tool-holder robot. The objective of the study is to explore the cyclic nature of this mechanical operation to provide the basis for future development of better process control strategies. Grinding tasks that minimize the number of iterations to converge to the target surface can be better planned based on a good understanding and modeling of the cyclic material removal mechanism. A single degree of freedom dynamic analysis of the process suggests that material removal is performed through high-frequency impacts that mainly last for only a small fraction of the grinding disk rotation period. To detect these discrete cutting events in practice, a grinder is equipped with a rotary encoder. The encoder's signal is acquired through the angular sampling technique. A running cyclic synchronous average is applied to the speed signal to remove its non-cyclic events. The measured instantaneous rotational frequency clearly indicates the impacting nature of the process and captures the transient response excited by these cyclic impacts. The technique also locates the angular positions of cutting impacts in revolution cycles. It is thus possible to draw conclusions about the cyclic nature of dynamic changes in impact-cutting behavior when grinding with a flexible robot. The dynamics of the impacting regime and transient responses to impact-cutting excitations captured synchronously using the angular sampling technique provide feedback that can be used to regulate the material removal process. The experimental results also make it possible to correlate the energy required to remove a chip of metal through impacting with the measured drop in angular speed during grinding.

REE in the Great Whale River estuary, northwest Quebec

NASA Technical Reports Server (NTRS)

Goldstein, Steven J.; Jacobsen, Stein B.

1988-01-01

A report on REE concentrations within the estuary of the Great Whale River in northwest Quebec and in Hudson Bay is given, showing concentrations which are less than those predicted by conservative mixing of seawater and river water, indicating removal of REE from solution. REE removal is rapid, occurring primarily at salinities less than 2 percent and ranges from about 70 percent for light REE to no more than 40 percent for heavy REE. At low salinity, Fe removal is essentially complete. The shape of Fe and REE vs. salinity profiles is not consistent with a simple model of destabilization and coagulation of Fe and REE-bearing colloidal material. A linear relationship between the activity of free ion REE(3+) and pH is consistent with a simple ion-exchange model for REE removal. Surface and subsurface samples of Hudson Bay seawater show high REE and La/Yb concentrations relative to average seawater, with the subsurface sample having a Nd concentration of 100 pmol/kg and an epsilon(Nd) of -29.3; characteristics consistent with river inputs of Hudson Bay. This indicates that rivers draining the Canadian Shield are a major source of nonradiogenic Nd and REE to the Atlantic Ocean.

Identifying removable radioactivity on the surface of cats during the first week after treatment with iodine 131.

PubMed

Chalmers, H J; Scrivani, Peter V; Dykes, Nathan L; Erb, Hollis N; Hobbs, J M; Hubble, Lorna J

2006-01-01

Because radioiodine (1-131) is excreted in urine and saliva, treated cats can accumulate I-131 on their coats from contacting soiled litter and grooming. This could result in removable radioactivity, which is a potential source of human exposure to radiation and specifically to internal contamination. The purpose of this study was to determine if there is removable radioactivity on cats treated with I-131. Daily wipe tests were performed for 7 days at two sites (both flanks, one site; and all four paws, one site) on six hyperthyroid cats treated with I-131. A y counter was used to determine the counts per minute (cpm) of the samples, which were converted to disintegrations per minute (dpm) to estimate activity. The results were compared to the New York State limits of removable activity for a non-controlled area (<1000dpm/100 cm2) to determine if the amount of removable activity was acceptable for a member of the public. The median value of removable activity was 241 dpm (range from 34 to 4184 dpm) for the flanks, and 308 dpm (range from 60 to 1890 dpm) for the paws. The amount of removable radioactivity on the surface of hospitalized cats treated with I-131 during the first week after treatment, occasionally and without obvious pattern, exceeded the New York State limit. Sporadic activity as high as 4148 dpm was found. It is prudent to advise owners to observe routine hygiene when handling cats after discharge to minimize the risk of internal contamination.

Surface characterization of retinal tissues for the enhancement of vitreoretinal surgical methods

NASA Astrophysics Data System (ADS)

Valentin-Rodriguez, Celimar

Diabetic retinopathy is the most common ophthalmic complication of diabetes and the leading cause of blindness among adults, ages 30 to 70. Surgery to remove scar tissue in the eye is the only corrective treatment once the retina is affected. Visual recovery is often hampered by retinal trauma during surgery and by low patient compliance. Our work in this project aimed to improve vitreoretinal surgical methods from information gathered by sensitive surface analysis of pre-retinal tissues found at the vitreoretinal interface. Atomic force microscopy characterization of human retinal tissues revealed that surgically excised inner limiting membrane (ILM) has a heterogeneous surface and is mainly composed of globular and fibrous structures. ILM tissues also show low adhesion for clean unmodified surfaces as opposed to those with functional groups attractive to those on the ILM surface, due to their charge. Based on these observations, layer-by-layer films with embedded gold nanoparticles with a positive outer charge were designed. These modifications increased the adhesion between surgical instruments and ILM by increasing the roughness and tuning the film surface charge. These films proved to be stable under physiological conditions. Finally, the effect of vital dyes on the topographical characteristics of ILMs was characterized and new imaging modes to further reveal ILM topography were utilized. Roughness and adhesion force data suggest that second generation dyes have no effect on the surface nanostructure of ILMs, but increase adhesion at the tip sample interface. This project clearly illustrates that physicochemical information from tissues can be used to rationally re-design surgical procedures, in this case for tissue removal purposes. This rational design method can be applied to other soft tissue excision procedures as is the case of cataract surgery or laparoscopic removal of endometrial tissue.

Sample mounting and transfer for coupling an ultrahigh vacuum variable temperature beetle scanning tunneling microscope with conventional surface probes

DOE Office of Scientific and Technical Information (OSTI.GOV)

Nafisi, Kourosh; Ranau, Werner; Hemminger, John C.

2001-01-01

We present a new ultrahigh vacuum (UHV) chamber for surface analysis and microscopy at controlled, variable temperatures. The new instrument allows surface analysis with Auger electron spectroscopy, low energy electron diffraction, quadrupole mass spectrometer, argon ion sputtering gun, and a variable temperature scanning tunneling microscope (VT-STM). In this system, we introduce a novel procedure for transferring a sample off a conventional UHV manipulator and onto a scanning tunneling microscope in the conventional ''beetle'' geometry, without disconnecting the heating or thermocouple wires. The microscope, a modified version of the Besocke beetle microscope, is mounted on a 2.75 in. outer diameter UHVmore » flange and is directly attached to the base of the chamber. The sample is attached to a tripod sample holder that is held by the main manipulator. Under UHV conditions the tripod sample holder can be removed from the main manipulator and placed onto the STM. The VT-STM has the capability of acquiring images between the temperature range of 180--500 K. The performance of the chamber is demonstrated here by producing an ordered array of island vacancy defects on a Pt(111) surface and obtaining STM images of these defects.« less

Recovery, Transportation and Acceptance to the Curation Facility of the Hayabusa Re-Entry Capsule

NASA Technical Reports Server (NTRS)

Abe, M.; Fujimura, A.; Yano, H.; Okamoto, C.; Okada, T.; Yada, T.; Ishibashi, Y.; Shirai, K.; Nakamura, T.; Noguchi, T.;

Mathematical Modeling on the Growth and Removal of Non-metallic Inclusions in the Molten Steel in a Two-Strand Continuous Casting Tundish

NASA Astrophysics Data System (ADS)

Ling, Haitao; Zhang, Lifeng; Li, Hong

2016-10-01

In the current study, mathematical models were developed to predict the transient concentration and size distribution of inclusions in a two-strand continuous casting tundish. The collision and growth of inclusions were considered. The contribution of turbulent collision and Stokes collision was evaluated. The removal of inclusions from the top surface was modeled by considering the properties of inclusions and the molten steel, such as the wettability, density, size, and interfacial tension. The effect of composition of inclusions on the collision of inclusions was included through the Hamaker constant. Meanwhile, the effect of the turbulent fluctuation velocity on the removal of inclusions at the top surface was also studied. Inclusions in steel samples were detected using automatic SEM Scanning so that the amount, morphology, size, and composition of inclusions were achieved. In the simulation, the size distribution of inclusions at the end steel refining was used as the initial size distribution of inclusions at tundish inlet. The equilibrium time when the collision and coalescence of inclusions reached the steady state was equal to 3.9 times of the mean residence time. When Stokes collision, turbulent collision, and removal by floating were included, the removal fraction of inclusions was 16.4 pct. Finally, the removal of solid and liquid inclusions, such as Al2O3, SiO2, and 12CaO·7Al2O3, at the interface between the molten steel and slag was studied. Compared with 12CaO·7Al2O3 inclusions, the silica and alumina inclusions were much easier to be removed from the molten steel and their removal fractions were 36.5 and 39.2 pct, respectively.

Statistical optimization of the phytoremediation of arsenic by Ludwigia octovalvis- in a pilot reed bed using response surface methodology (RSM) versus an artificial neural network (ANN).

PubMed

Titah, Harmin Sulistiyaning; Halmi, Mohd Izuan Effendi Bin; Abdullah, Siti Rozaimah Sheikh; Hasan, Hassimi Abu; Idris, Mushrifah; Anuar, Nurina

2018-06-07

In this study, the removal of arsenic (As) by plant, Ludwigia octovalvis, in a pilot reed bed was optimized. A Box-Behnken design was employed including a comparative analysis of both Response Surface Methodology (RSM) and an Artificial Neural Network (ANN) for the prediction of maximum arsenic removal. The predicted optimum condition using the desirability function of both models was 39 mg kg -1 for the arsenic concentration in soil, an elapsed time of 42 days (the sampling day) and an aeration rate of 0.22 L/min, with the predicted values of arsenic removal by RSM and ANN being 72.6% and 71.4%, respectively. The validation of the predicted optimum point showed an actual arsenic removal of 70.6%. This was achieved with the deviation between the validation value and the predicted values being within 3.49% (RSM) and 1.87% (ANN). The performance evaluation of the RSM and ANN models showed that ANN performs better than RSM with a higher R 2 (0.97) close to 1.0 and very small Average Absolute Deviation (AAD) (0.02) and Root Mean Square Error (RMSE) (0.004) values close to zero. Both models were appropriate for the optimization of arsenic removal with ANN demonstrating significantly higher predictive and fitting ability than RSM.

Surface polishing of niobium for superconducting radio frequency (SRF) cavity applications

DOE Office of Scientific and Technical Information (OSTI.GOV)

Zhao, Liang

2014-08-01

Niobium cavities are important components in modern particle accelerators based on superconducting radio frequency (SRF) technology. The interior of SRF cavities are cleaned and polished in order to produce high accelerating field and low power dissipation on the cavity wall. Current polishing methods, buffered chemical polishing (BCP) and electro-polishing (EP), have their advantages and limitations. We seek to improve current methods and explore laser polishing (LP) as a greener alternative of chemical methods. The topography and removal rate of BCP at different conditions (duration, temperature, sample orientation, flow rate) was studied with optical microscopy, scanning electron microscopy (SEM), and electronmore » backscatter diffraction (EBSD). Differential etching on different crystal orientations is the main contributor to fine grain niobium BCP topography, with gas evolution playing a secondary role. The surface of single crystal and bi-crystal niobium is smooth even after heavy BCP. The topography of fine grain niobium depends on total removal. The removal rate increases with temperature and surface acid flow rate within the rage of 0~20 °C, with chemical reaction being the possible dominate rate control mechanism. Surface flow helps to regulate temperature and avoid gas accumulation on the surface. The effect of surface flow rate on niobium EP was studied with optical microscopy, atomic force microscopy (AFM), and power spectral density (PSD) analysis. Within the range of 0~3.7 cm/s, no significant difference was found on the removal rate and the macro roughness. Possible improvement on the micro roughness with increased surface flow rate was observed. The effect of fluence and pulse accumulation on niobium topography during LP was studied with optical microscopy, SEM, AFM, and PSD analysis. Polishing on micro scale was achieved within fluence range of 0.57~0.90 J/cm2, with pulse accumulation adjusted accordingly. Larger area treatment was proved possible by overlapping laser tracks at proper ratio. Comparison of topography and PSD indicates that LP smooths the surface in a way similar to EP. The optimized LP parameters were applied to different types of niobium surfaces representing different stages in cavity fabrication. LP reduces the sharpness on rough surfaces effectively, while doing no harm to smooth surfaces. Secondary ion mass spectrometer (SIMS) analysis showed that LP reduces the oxide layer slightly and no contamination occurred from LP. EBSD showed no significant change on crystal structure after LP.« less

Multi-phase classification by a least-squares support vector machine approach in tomography images of geological samples

NASA Astrophysics Data System (ADS)

Khan, Faisal; Enzmann, Frieder; Kersten, Michael

2016-03-01

Image processing of X-ray-computed polychromatic cone-beam micro-tomography (μXCT) data of geological samples mainly involves artefact reduction and phase segmentation. For the former, the main beam-hardening (BH) artefact is removed by applying a best-fit quadratic surface algorithm to a given image data set (reconstructed slice), which minimizes the BH offsets of the attenuation data points from that surface. A Matlab code for this approach is provided in the Appendix. The final BH-corrected image is extracted from the residual data or from the difference between the surface elevation values and the original grey-scale values. For the segmentation, we propose a novel least-squares support vector machine (LS-SVM, an algorithm for pixel-based multi-phase classification) approach. A receiver operating characteristic (ROC) analysis was performed on BH-corrected and uncorrected samples to show that BH correction is in fact an important prerequisite for accurate multi-phase classification. The combination of the two approaches was thus used to classify successfully three different more or less complex multi-phase rock core samples.

Atomic Layer-Deposited TiO2 Coatings on NiTi Surface

NASA Astrophysics Data System (ADS)

Vokoun, D.; Racek, J.; Kadeřávek, L.; Kei, C. C.; Yu, Y. S.; Klimša, L.; Šittner, P.

2018-02-01

NiTi shape-memory alloys may release poisonous Ni ions at the alloys' surface. In an attempt to prepare a well-performing surface layer on an NiTi sample, the thermally grown TiO2 layer, which formed during the heat treatment of NiTi, was removed and replaced with a new TiO2 layer prepared using the atomic layer deposition (ALD) method. Using x-ray photoelectron spectroscopy, it was found that the ALD layer prepared at as low a temperature as 100 °C contained Ti in oxidation states + 4 and + 3. As for static corrosion properties of the ALD-coated NiTi samples, they further improved compared to those covered by thermally grown oxide. The corrosion rate of samples with thermally grown oxide was 1.05 × 10-5 mm/year, whereas the corrosion rate of the ALD-coated samples turned out to be about five times lower. However, cracking of the ALD coating occurred at about 1.5% strain during the superelastic mechanical loading in tension taking place via the propagation of a localized martensite band.

Removal of terrestrial DOC in aquatic ecosystems of a temperate river network

USGS Publications Warehouse

Wollheim, W.M.; Stewart, R. J.; Aiken, George R.; Butler, Kenna D.; Morse, Nathaniel B.; Salisbury, J.

2015-01-01

Surface waters play a potentially important role in the global carbon balance. Dissolved organic carbon (DOC) fluxes are a major transfer of terrestrial carbon to river systems, and the fate of DOC in aquatic systems is poorly constrained. We used a unique combination of spatially distributed sampling of three DOC fractions throughout a river network and modeling to quantify the net removal of terrestrial DOC during a summer base flow period. We found that aquatic reactivity of terrestrial DOC leading to net loss is low, closer to conservative chloride than to reactive nitrogen. Net removal occurred mainly from the hydrophobic organic acid fraction, while hydrophilic and transphilic acids showed no net change, indicating that partitioning of bulk DOC into different fractions is critical for understanding terrestrial DOC removal. These findings suggest that river systems may have only a modest ability to alter the amounts of terrestrial DOC delivered to coastal zones.

Atmospheric particulate matter in proximity to mountaintop coal mines: Sources and potential environmental and human health impacts

USGS Publications Warehouse

Kurth, Laura; Kolker, Allan; Engle, Mark A.; Geboy, Nicholas J.; Hendryx, Michael; Orem, William H.; McCawley, Michael; Crosby, Lynn M.; Tatu, Calin A.; Varonka, Matthew S.; DeVera, Christina A.

2015-01-01

Mountaintop removal mining (MTM) is a widely used approach to surface coal mining in the US Appalachian region whereby large volumes of coal overburden are excavated using explosives, removed, and transferred to nearby drainages below MTM operations. To investigate the air quality impact of MTM, the geochemical characteristics of atmospheric particulate matter (PM) from five surface mining sites in south central West Virginia, USA, and five in-state study control sites having only underground coal mining or no coal mining whatsoever were determined and compared. Epidemiologic studies show increased rates of cancer, respiratory disease, cardiovascular disease, and overall mortality in Appalachian surface mining areas compared to Appalachian non-mining areas. In the present study, 24-h coarse (>2.5 µm) and fine (≤2.5 µm) PM samples were collected from two surface mining sites in June 2011 showed pronounced enrichment in elements having a crustal affinity (Ga, Al, Ge, Rb, La, Ce) contributed by local sources, relative to controls. Follow-up sampling in August 2011 lacked this enrichment, suggesting that PM input from local sources is intermittent. Using passive samplers, dry deposition total PM elemental fluxes calculated for three surface mining sites over multi-day intervals between May and August 2012 were 5.8 ± 1.5 times higher for crustal elements than at controls. Scanning microscopy of 2,249 particles showed that primary aluminosilicate PM was prevalent at surface mining sites compared to secondary PM at controls. Additional testing is needed to establish any link between input of lithogenic PM and disease rates in the study area.

Atmospheric particulate matter in proximity to mountaintop coal mines: sources and potential environmental and human health impacts.

PubMed

Kurth, Laura; Kolker, Allan; Engle, Mark; Geboy, Nicholas; Hendryx, Michael; Orem, William; McCawley, Michael; Crosby, Lynn; Tatu, Calin; Varonka, Matthew; DeVera, Christina

2015-06-01

Mountaintop removal mining (MTM) is a widely used approach to surface coal mining in the US Appalachian region whereby large volumes of coal overburden are excavated using explosives, removed, and transferred to nearby drainages below MTM operations. To investigate the air quality impact of MTM, the geochemical characteristics of atmospheric particulate matter (PM) from five surface mining sites in south central West Virginia, USA, and five in-state study control sites having only underground coal mining or no coal mining whatsoever were determined and compared. Epidemiologic studies show increased rates of cancer, respiratory disease, cardiovascular disease, and overall mortality in Appalachian surface mining areas compared to Appalachian non-mining areas. In the present study, 24-h coarse (>2.5 µm) and fine (≤2.5 µm) PM samples were collected from two surface mining sites in June 2011 showed pronounced enrichment in elements having a crustal affinity (Ga, Al, Ge, Rb, La, Ce) contributed by local sources, relative to controls. Follow-up sampling in August 2011 lacked this enrichment, suggesting that PM input from local sources is intermittent. Using passive samplers, dry deposition total PM elemental fluxes calculated for three surface mining sites over multi-day intervals between May and August 2012 were 5.8 ± 1.5 times higher for crustal elements than at controls. Scanning microscopy of 2,249 particles showed that primary aluminosilicate PM was prevalent at surface mining sites compared to secondary PM at controls. Additional testing is needed to establish any link between input of lithogenic PM and disease rates in the study area.

Characterization of coal gasification slag-based activated carbon and its potential application in lead removal.

PubMed

Xu, Yiting; Chai, Xiaoli

2018-02-01

Highly porous activated carbons were prepared from a coal gasification slag (CGS) precursor, by KOH activation to remove Pb 2+ from aqueous solution. The effects of pretreatment methods and activation parameters on the properties of the activated carbon were investigated, such as KOH/CGS mass ratio, activation temperature and activation time. The results showed that the maximum Brunauer-Emmett-Teller surface area and total pore volume with the value of 2481 m 2  g -1 and of 1.711 cc g -1 were obtained at a KOH/CGS ratio of 3.0 by physical mixing, an activation temperature of 750°C and an activation time of 80 min. SEM, FTIR and EA analyses indicated that pronounced pores existed on the exterior surface of the activated samples, and the contents of H and O decreased due to the loss of surface chemical groups during activation. Experimental data for the Pb 2+ adsorption were fitted well by Freundlich equation and a pseudo-second-order model with a maximum experimental adsorption capacity of 141 mg/g. All of the results indicated that CGS could be a promising material to prepare porous activated carbon for Pb 2+ removal from wastewater.

Biotite weathering in a natural forest setting near Derome, Sweden

NASA Astrophysics Data System (ADS)

Balogh-Brunstad, Z.; Negrich, K.; Hassenkam, T.; Wallander, H.; Stipp, S. L.

2011-12-01

Chemical weathering is a key process in non-nitrogen nutrient acquisition by microbes, fungi and plants. Biotite is commonly the major source of potassium, magnesium and iron. A unique opportunity arose to study natural weathering of biotite by mixed conifer and hardwood forest vegetation and associated microbes and fungi at an abandoned mine site. After the mining stopped over 30 years ago biotite was left behind in piles and the forest vegetation progressively colonized the site. Samples were collected from the top 40 cm of the biotite piles in a vicinity of pine, spruce and birch trees and included some young seedlings. Macroscopic observations documented abundant hyphal growth between the sheets of biotite. We hypothesized that fungal hyphae grow between the sheets to explore the nutrient source and weather the biotite leaving hyphal-sized etched channels on the basal surfaces. Biotite surfaces were examined with atomic force microscopy (AFM) and environmental scanning electron microscopy (ESEM) in their natural state and after removing the biological material from the mineral surfaces. The ESEM images show extensive hyphal colonization and patchy biofilm cover of the entire biotite surface on and within the sheets and at the edges of the particles. Fungal hyphae did not attach strongly to the basal surfaces of the biotite flakes as a result of small particles on the surfaces and the uneven micro-topography. The AFM images illustrate a complex microbial community around the fungal hyphae and detailed fungal morphology. High resolution AFM images show unique globular features of diameter 10-100 nm on all biofilm surfaces. However, removal of the biological material resulted in smooth and un-etched surfaces indicating that either our removal techniques are too invasive and destroy the surface layers of interest, or the etching of the basal surface is not the main mechanism for chemical weathering and base-cation nutrient immobilization in this natural setting. Species-specific interactions at the biofilm-microbe-fungus-mineral interface and spatial distribution in the biotite pile are under further investigation.

Computer Controlled Optical Surfacing With Orbital Tool Motion

NASA Astrophysics Data System (ADS)

Jones, Robert A.

1985-10-01

Asymmetric aspheric optical surfaces are very difficult to fabricate using classical techniques and laps the same size as the workpiece. Opticians can produce such surfaces by grinding and polishing, using small laps with orbital tool motion. However, hand correction is a time consuming process unsuitable for large optical elements. Itek has developed Computer Controlled Optical Surfacing (CCOS) for fabricating such aspheric optics. Automated equipment moves a nonrotating orbiting tool slowly over the workpiece surface. The process corrects low frequency surface errors by figuring. The velocity of the tool assembly over the workpiece surface is purposely varied. Since the amount of material removal is proportional to the polishing or grinding time, accurate control over material removal is achieved. The removal of middle and high frequency surface errors is accomplished by pad smoothing. For a soft pad material, the pad will compress to fit the workpiece surface producing greater pressure and more removal at the surface high areas. A harder pad will ride on only the high regions resulting in removal only for those locations.

Synoptic Sampling to Determine Distributed Groundwater-Surface Water Nitrate Loading and Removal Potential Along a Lowland River

NASA Astrophysics Data System (ADS)

Pai, Henry; Villamizar, Sandra R.; Harmon, Thomas C.

2017-11-01

Delineating pollutant reactive transport pathways that connect local land use patterns to surface water is an important goal. This work illustrates high-resolution river mapping of salinity or specific conductance (SC) and nitrate (NO3-) as a potential part of achieving this goal. We observed longitudinal river SC and nitrate distributions using high-resolution synoptic in situ sensing along the lower Merced River (38 river km) in Central California (USA) from 2010 to 2012. We calibrated a distributed groundwater-surface water (GW-SW) discharge model for a conservative solute using 13 synoptic SC sampling events at flows ranging from 1.3 to 31.6 m3 s-1. Nitrogen loads ranged from 0.3 to 1.6 kg N d-1 and were greater following an extended high flow period during a wet winter. Applying the distributed GW-SW discharge estimates to a simplistic reactive nitrate transport model, the model reproduced observed river nitrate distribution well (RRMSE = 5-21%), with dimensionless watershed-averaged nitrate removal (kt) ranging from 0 to 0.43. Estimates were uncertain due to GW nitrate data variability, but the resulting range was consistent with prior removal estimates. At the segment scale, estimated GW-SW nitrate loading ranged from 0 to 17 g NO3- s-1 km-1. Local loading peaked near the middle of the study reach, a location that coincides with a shallow clay lens and with confined animal feed operations in close proximity to the river. Overall, the results demonstrate the potential for high-resolution synoptic monitoring to support GW-SW modeling efforts aimed at understanding and managing nonpoint source pollution.

Recoveries of trace pseudoephedrine and methamphetamine residues from impermeable household surfaces: implications for sampling methods used during remediation of clandestine methamphetamine laboratories.

PubMed

Abdullah, A F Lim; Miskelly, Gordon M

2010-04-15

Evaluation of the risk posed by contaminants present during and after decontamination of clandestine methamphetamine laboratories requires a connection between the levels of contaminants measured and those actually present at the scene. The recoveries of pseudoephedrine and methamphetamine from glass, stainless steel, and a range of impermeable surfaces likely to be found in a clandestine laboratory were examined, using GC-MS of derivatized samples as the analytical method. When surfaces had been cleaned prior to drug deposition, wiping with water-dampened filter paper can recover 60-80% of pseudoephedrine immediately after deposition, and at least 50% of the pseudoephedrine still present on a surface after 2 days when deposited at a surface concentration of 2.5 microg/100 cm(2). Wiping with methanol-dampened filter paper could recover 60-90% of the methamphetamine immediately after deposition, and could recover at least 50-60% of the methamphetamine still present after 2 days when 0.6 microg/100 cm(2) was initially deposited on the surface. Recoveries were lower for surfaces that had not been pre-cleaned. Methamphetamine and pseudoephedrine showed significant volatility in both the free base and hydrochloride forms, with experiments in an enclosed format showing up to half the recovered drug being present on a glass plate held about 4mm above a substrate contaminated with one of the drugs at the above surface concentrations after 2 days. It is therefore important to remove any visible bulk contaminants and remove obvious pseudoephedrine or methamphetamine-contaminated surfaces prior to heating, ventilation or sealing of a clandestine laboratory to avoid redistribution of material around the site. A revised method for pseudoephedrine analysis was developed that could also detect the pseudoephedrine-formaldehyde adduct that can form from trace pseudoephedrine present at clandestine laboratories. (c) 2009 Elsevier B.V. All rights reserved.

Implementation of a best management practice (BMP) system for a clay mining facility in Taiwan.

PubMed

Lin, Jen-Yang; Chen, Yen-Chang; Chen, Walter; Lee, Tsu-Chuan; Yu, Shaw L

2006-01-01

The present paper describes the planning and implementation of a best management practice (BMP) system for a clay mining facility in Northern Taiwan. It is a challenge to plan and design BMPs for mitigating the impact of clay mining operations due to the fact that clay mining drainage typically contains very high concentrations of suspended solids (SS), Fe-ions, and [H+] concentrations. In the present study, a field monitoring effort was conducted to collect data for runoff quality and quantity from a clay mining area in Northern Taiwan. A BMP system including holding ponds connected in series was designed and implemented and its pollutant removal performance was assessed. The assessment was based on mass balance computations and an analysis of the relationship between BMP design parameters such as pond depth, detention time, surface loading rate, etc. and the pollutant removal efficiency. Field sampling results showed that the surface-loading rate is exponential related to the removing rate. The results provide the basis for a more comprehensive and efficient BMP implementation plan for clay mining operations.

ROPEC - ROtary PErcussive Coring Drill for Mars Sample Return

NASA Technical Reports Server (NTRS)

Chu, Philip; Spring, Justin; Zacny, Kris

2014-01-01

The ROtary Percussive Coring Drill is a light weight, flight-like, five-actuator drilling system prototype designed to acquire core material from rock targets for the purposes of Mars Sample Return. In addition to producing rock cores for sample caching, the ROPEC drill can be integrated with a number of end effectors to perform functions such as rock surface abrasion, dust and debris removal, powder and regolith acquisition, and viewing of potential cores prior to caching. The ROPEC drill and its suite of end effectors have been demonstrated with a five degree of freedom Robotic Arm mounted to a mobility system with a prototype sample cache and bit storage station.

226Ra, 210Pb, 210Bi and 210Po deposition and removal from surfaces and liquids.

PubMed

Wójcik, M; Zuzel, G

Deposition of 226 Ra from water on nylon was investigated. Measurements performed for different pH and different radium concentrations in the water gave similar absolute activities deposited on the foil surface. Obtained results were used to estimate the amount of 226 Ra plated-out on the nylon scintillator vessel in the solar neutrino experiment BOREXINO during filling of the detector. Another problem studied in the frame of BOREXINO was the removal of 210 Pb from its organic liquid scintillator by applying distillation and water extraction. After several tests had been performed for both methods it was found that after the water extraction the initial lead content in the scintillator sample was reduced only accordingly to the ratio of the volumes of the applied liquids (simple dilution). In contrast to this, distillation was very effective providing in the best case a 210 Pb reduction factor higher than 100. Removal efficiencies of the long-lived 222 Rn daughters during etching from surfaces of standard and high purity germanium were investigated in the frame of the GERDA experiment, which aims to search for neutrino-less double beta decay of 76 Ge. The standard etching procedure of Canberra used during production of high purity n-type germanium diodes was applied to germanium discs, which had been exposed earlier to a strong 222 Rn source for its progenies deposition. In contrast to copper and stainless steel, 210 Pb, 210 Bi and 210 Po was removed from germanium very efficiently. An evidence of a reverse process was also observed-the isotopes were transferred from the etchant to the clean germanium surface.

Characterizing the rapid spread of porcine epidemic diarrhea virus (PEDV) through an animal food manufacturing facility

PubMed Central

Schumacher, Loni L.; Huss, Anne R.; Cochrane, Roger A.; Stark, Charles R.; Woodworth, Jason C.; Bai, Jianfa; Poulsen, Elizabeth G.; Chen, Qi; Main, Rodger G.; Zhang, Jianqiang; Gauger, Phillip C.; Ramirez, Alejandro; Derscheid, Rachel J.; Magstadt, Drew M.; Dritz, Steve S.

2017-01-01

New regulatory and consumer demands highlight the importance of animal feed as a part of our national food safety system. Porcine epidemic diarrhea virus (PEDV) is the first viral pathogen confirmed to be widely transmissible in animal food. Because the potential for viral contamination in animal food is not well characterized, the objectives of this study were to 1) observe the magnitude of virus contamination in an animal food manufacturing facility, and 2) investigate a proposed method, feed sequencing, to decrease virus decontamination on animal food-contact surfaces. A U.S. virulent PEDV isolate was used to inoculate 50 kg swine feed, which was mixed, conveyed, and discharged into bags using pilot-scale feed manufacturing equipment. Surfaces were swabbed and analyzed for the presence of PEDV RNA by quantitative real-time polymerase chain reaction (qPCR). Environmental swabs indicated complete contamination of animal food-contact surfaces (0/40 vs. 48/48, positive baseline samples/total baseline samples, positive subsequent samples/total subsequent samples, respectively; P < 0.05) and near complete contamination of non-animal food-contact surfaces (0/24 vs. 16/18, positive baseline samples/total baseline samples, positive subsequent samples/total subsequent samples, respectively; P < 0.05). Flushing animal food-contact surfaces with low-risk feed is commonly used to reduce cross-contamination in animal feed manufacturing. Thus, four subsequent 50 kg batches of virus-free swine feed were manufactured using the same system to test its impact on decontaminating animal food-contact surfaces. Even after 4 subsequent sequences, animal food-contact surfaces retained viral RNA (28/33 positive samples/total samples), with conveying system being more contaminated than the mixer. A bioassay to test infectivity of dust from animal food-contact surfaces failed to produce infectivity. This study demonstrates the potential widespread viral contamination of surfaces in an animal food manufacturing facility and the difficulty of removing contamination using conventional feed sequencing, which underscores the importance for preventing viruses from entering and contaminating such facilities. PMID:29095859

Remotely operable sample-taking appliance, especially for ascertaining radioactivity profiles in contaminated material surfaces

DOE Office of Scientific and Technical Information (OSTI.GOV)

Hanulik, J.

1983-09-20

A sample-taking appliance comprises several sensors arranged on a turntable like sensor carrier in such a manner that the application areas of the small sensor sponges decrease stepwise from the first to the last sensor. By simple rotation of the turntable the sensors can be brought successively into a working position. The sensor carrier is preferably accommodated in a housing which is open at the bottom and which is raisable and lowerable in the frame of the appliance by, for example, a threaded spindle. The threaded spindle is driven by an electric motor. For each sampling the sensor carrier ismore » lowered until the cell voltage corresponds to a predetermined desired value. This produces sufficiently precise and reproductible measured values of the electrolytic current for ascertaining the removed layer thickness. The appliance makes it possible to take material samples even from locations of high radiation loading. The material layers removed as samples lie concentrically above each other so that the graduation of the application areas comes into full effect and the material samples taken by the small sponges and the radioactivity contained therein are not falsified.« less

Patterned CoCrMo and Al2 O3 surfaces for reduced free wear debris in artificial joint arthroplasty.

PubMed

Tarabolsi, Mohamad; Klassen, Thomas; Mantwill, Frank; Gärtner, Frank; Siegel, Frank; Schulz, Arndt-Peter

2013-12-01

Surface wear of corresponding tribological pairings is still a major problem in the application of artificial joint surgery. This study aims at developing wear reduced surfaces to utilize them in total joint arthroplasty. Using a pico-second laser, samples of medical CoCrMo metal alloy and Al2 O3 ceramic were patterned by laser material removal. The subsequent tribological investigations employed a ring-on-disc method. The results showed that those samples with modified surfaces show less mass or volume loss than those with a regular, smooth surface. Using calf serum as lubricating medium, the volume loss of the structured CoCrMo samples was eight times lower than that of regular samples. By structuring Al2 O3 surfaces, the wear volume could be reduced by 4.5 times. The results demonstrate that defined surface channels or pits enable the local sedimentation of wear debris. Thus, the amount of free debris could be reduced. Fewer abrasives in the lubricated so-called three-body-wear between the contact surfaces should result in less surface damage. Apart from direct influences on the wear behavior, less amounts of free debris of artificial joints should also be beneficial for avoiding undesired reactions with the surrounding soft tissues. The results from this study are very promising. Future investigations should involve the use of simulators meeting the natural conditions in the joint and in vivo studies with living organisms. Copyright © 2013 Wiley Periodicals, Inc., a Wiley Company.

Adsorption-regeneration by heterogeneous Fenton process using modified carbon and clay materials for removal of indigo blue.

PubMed

Almazán-Sánchez, Perla Tatiana; Solache-Ríos, Marcos J; Linares-Hernández, Ivonne; Martínez-Miranda, Verónica

2016-01-01

Indigo blue dye is mainly used in dyeing of denim clothes and its presence in water bodies could have adverse effects on the aquatic system; for this reason, the objective of this study was to promote the removal of indigo blue dye from aqueous solutions by iron and copper electrochemically modified clay and activated carbon and the saturated materials were regenerated by a Fenton-like process. Montmorillonite clay was modified at pH 2 and 7; activated carbon at pH 2 and pH of the system. The elemental X-ray dispersive spectroscopy analysis showed that the optimum pH for modification of montmorillonite with iron and copper was 7 and for activated carbon was 2. The dye used in this work was characterized by infrared. Unmodified and modified clay samples showed the highest removal efficiencies of the dye (90-100%) in the pH interval from 2 to 10 whereas the removal efficiencies decrease as pH increases for samples modified at pH 2. Unmodified clay and copper-modified activated carbon at pH 2 were the most efficient activated materials for the removal of the dye. The adsorption kinetics data of all materials were best adjusted to the pseudo-second-order model, indicating a chemisorption mechanism and the adsorption isotherms data showed that the materials have a heterogeneous surface. The iron-modified clay could be regenerated by a photo-Fenton-like process through four adsorption-regeneration cycles, with 90% removal efficiency.

Investigation of off-site airborne transport of lead from a superfund removal action site using lead isotope ratios and concentrations

USGS Publications Warehouse

Pribil, Michael J.; Maddaloni, Mark A.; Staiger, Kimberly; Wilson, Eric; Magriples, Nick; Ali, Mustafa; Santella, Dennis

2014-01-01

Lead (Pb) concentration and Pb isotopic composition of surface and subsurface soil samples were used to investigate the potential for off-site air transport of Pb from a former white Pb processing facility to neighboring residential homes in a six block area on Staten Island, NY. Surface and subsurface soil samples collected on the Jewett White Pb site were found to range from 1.122 to 1.138 for 206Pb/207Pb and 2.393 to 2.411 for 208Pb/207Pb. The off-site surface soil samples collected from residential backyards, train trestle, near site grass patches and background areas varied from 1.144 to 1.196 for 206Pb/207Pb and 2.427 to 2.464 for 208Pb/207Pb. Two soil samples collected along Richmond Terrace, where Jewett site soils accumulated after major rain events, varied from 1.136 to 1.147 for 206Pb/207Pb and 2.407 to 2.419 for 208Pb/207Pb. Lead concentration for on-site surface soil samples ranged from 450 to 8000 ug/g, on-site subsurface soil samples ranged from 90,000 to 240,000 ug/g and off-site samples varied from 380 to 3500 ug/g. Lead concentration and isotopic composition for the Staten Island off-site samples were similar to previously published data for other northeastern US cities and reflect re-suspension and re-mobilization of local accumulated Pb. The considerable differences in both the Pb isotopic composition and Pb concentration of on-site and off-site samples resulted in the ability to geochemically trace the transport of particulate Pb. Data in this study indicate minimal off-site surface transport of Pb from the Jewett site into the neighboring residential area.

Evaluation of the Effects of Er,Cr:YSGG Laser, Ultrasonic Scaler and Curette on Root Surface Profile Using Surface Analyser and Scanning Electron Microscope: An In Vitro Study.

PubMed

Arora, Shipra; Lamba, Arundeep Kaur; Faraz, Farrukh; Tandon, Shruti; Ahad, Abdul

2016-01-01

Introduction: The periodontal therapy is primarily targeted at removal of dental plaque and plaque retentive factors. Although the thorough removal of adherent plaque, calculus and infected root cementum is desirable, it is not always achieved by conventional modalities. To accomplish more efficient results several alternative devices have been used. Lasers are one of the most promising modalities for nonsurgical periodontal treatment as they can achieve excellent tissue ablation with strong bactericidal and detoxification effects. Methods: Thirty freshly extracted premolars were selected and decoronated. The mesial surface of each root was divided vertically into four approximately equal parts. These were distributed into four group based on the root surface treatment. Part A (n = 30) was taken as control and no instrumentation was performed. Part B (n = 30) was irradiated by Erbium, Chromium doped Yttrium Scandium Gallium Garnet (Er,Cr:YSGG) laser. Part C (n = 30) was treated by piezoelectric ultrasonic scaler. Part D (n = 30) was treated by Gracey curette. The surface roughness was quantitatively analyzed by profilometer using roughness average (Ra) value, while presence of smear layer, cracks, craters and melting of surface were analyzed using scanning electron microscope (SEM). The means across the groups were statistically compared with control using Dunnett test. Results: Among the test groups, Er,Cr:YSGG laser group showed maximum surface roughness (mean Ra value of 4.14 μm) as compared to ultrasonic scaler (1.727 μm) and curette group (1.22 μm). However, surface with smear layer were found to be maximum (50%) in curette treated samples and minimum (20%) in laser treated ones. Maximum cracks (83.34%) were produced by ultrasonic scaler, and minimum (43.33%) by curettes. Crater formation was maximum (50%) in laser treated samples and minimum (3.33%) in curette treated ones. 63.33% samples treated by laser demonstrated melting of root surface, followed by ultrasonic scaler and curettes. Conclusion: Er,Cr:YSGG laser produced maximum microstructural changes on root surface that can influence the attachment of soft periodontal tissues as well as plaque and calculus deposition. In vivo studies are needed to validate these results and to evaluate their clinical effects.

Biomass removal and its effect on productivity of an artificially regenerated forest stand in the Missouri ozarks

Treesearch

Flex Jr. Ponder

2007-01-01

Intensive harvesting, which removes a greater proportion of the forest biomass than conventional harvesting and the associated nutrients, may cause a decline in forest productivity. Planted seedling response to three biomass removal levels (1. removal of boles only=OM1, 2. all surface organic matter removed, forest floor not removed=OM2, and 3. removal of all surface...

An on-line SPE-HPLC method for effective sample preconcentration and determination of fenoxycarb and cis, trans-permethrin in surface waters.

PubMed

Šatínský, Dalibor; Naibrtová, Linda; Fernández-Ramos, Carolina; Solich, Petr

2015-09-01

A new on-line SPE-HPLC method using fused-core columns for on-line solid phase extraction and large volume sample injection for increasing the sensitivity of detection was developed for the determination of insecticides fenoxycarb and cis-, trans-permethrin in surface waters. The separation was carried out on fused-core column Phenyl-Hexyl (100×4.6 mm), particle size 2.7 µm with mobile phase acetonitrile:water in gradient mode at flow rate 1.0 mL min(-1), column temperature 45°C. Large volume sample injection (1500 µL) to the extraction dimension using short precolumn Ascentis Express RP C-18 (5×4.6 mm); fused-core particle size 2.7 µm allowed effective sample preconcentration and efficient ballast sample matrix removal. The washing mobile phase consisting of a mixture of acetonitrile:water; 30:70, (v/v) was pumped at flow rate of 0.5 mL min(-1) through the extraction precolumn to the waste. Time of the valve switch for transferring the preconcentrated sample zone from the extraction to the separation column was set at 3rd min. Elution of preconcentrated insecticides from the extraction precolumn and separation on the analytical column was performed in gradient mode. Linear gradient elution started from 40% of acetonitrile at time of valve switch from SPE column (3rd min) to 95% of acetonitrile at 7th min. Synthetic dye sudan I was chosen as an internal standard. UV detection at wavelength 225 nm was used and the method reached the limits of detection (LOD) at ng mL(-1) levels for both insecticides. The method showing on-line sample pretreatment and preconcentration with highly sensitive determination of insecticides was applied for monitoring of fenoxycarb and both permethrin isomers in different surface water samples in Czech Republic. The time of whole analysis including on-line extraction, interferences removal, chromatography separation and system equilibration was less than 8 min. Copyright © 2015 Elsevier B.V. All rights reserved.

Isotope exchange in oxide-containing catalyst

NASA Technical Reports Server (NTRS)

Brown, Kenneth G. (Inventor); Upchurch, Billy T. (Inventor); Hess, Robert V. (Inventor); Miller, Irvin M. (Inventor); Schryer, David R. (Inventor); Sidney, Barry D. (Inventor); Wood, George M. (Inventor); Hoyt, Ronald F. (Inventor)

1989-01-01

A method of exchanging rare-isotope oxygen for common-isotope oxygen in the top several layers of an oxide-containing catalyst is disclosed. A sample of an oxide-containing catalyst is exposed to a flowing stream of reducing gas in an inert carrier gas at a temperature suitable for the removal of the reactive common-isotope oxygen atoms from the surface layer or layers of the catalyst without damaging the catalyst structure. The reduction temperature must be higher than any at which the catalyst will subsequently operate. Sufficient reducing gas is used to allow removal of all the reactive common-isotope oxygen atoms in the top several layers of the catalyst. The catalyst is then reoxidized with the desired rare-isotope oxygen in sufficient quantity to replace all of the common-isotope oxygen that was removed.

Molecular Grafting of Fluorinated and Nonfluorinated Alkylsiloxanes on Various Ceramic Membrane Surfaces for the Removal of Volatile Organic Compounds Applying Vacuum Membrane Distillation.

PubMed

Kujawa, Joanna; Al-Gharabli, Samer; Kujawski, Wojciech; Knozowska, Katarzyna

2017-02-22

Four main tasks were presented: (i) ceramic membrane functionalization (TiO 2 5 kDa and 300 kDa), (ii) extended material characterization (physicochemistry and tribology) of pristine and modified ceramic samples, (iii) evaluation of chemical and mechanical stability, and finally (iv) assessment of membrane efficiency in vacuum membrane distillation applied for volatile organic compounds (VOCs) removal from water. Highly efficient molecular grafting with four types of perfluoroalkylsilanes and one nonfluorinated agent was developed. Materials with controllable tribological and physicochemical properties were achieved. The most meaningful finding is associated with the applicability of fluorinated and nonfluorinated grafting agents. The results of contact angle, hysteresis of contact angle, sliding angle, and critical surface tension as well as Young's modulus, nanohardness, and adhesion force for grafting by these two modifiers are comparable. This provides insight into the potential applicability of environmental friendly hydrophobic and superhydrophobic surfaces. The achieved hydrophobic membranes were very effective in the removal of VOCs (butanol, methyl-tert-butyl ether, and ethyl acetate) from binary aqueous solutions in vacuum membrane distillation. The correlation between membrane effectiveness and separated solvent polarity was compared in terms of material properties and resistance to the wetting (kinetics of wetting and in-depth liquid penetration). Material properties were interpreted considering Zisman theory and using Kao diagram. The significant influence of surface chemistry on the membrane performance was noticed (5 kDa, influence of hydrophobic nanolayer and separation controlled by solution-diffusion model; 300 kDa, no impact of surface chemistry and separation controlled by liquid-vapor equilibrium).

Fluid surface compensation in digital holographic microscopy for topography measurement

NASA Astrophysics Data System (ADS)

Lin, Li-Chien; Tu, Han-Yen; Lai, Xin-Ji; Wang, Sheng-Shiun; Cheng, Chau-Jern

2012-06-01

A novel technique is presented for surface compensation and topography measurement of a specimen in fluid medium by digital holographic microscopy (DHM). In the measurement, the specimen is preserved in a culture dish full of liquid culture medium and an environmental vibration induces a series of ripples to create a non-uniform background on the reconstructed phase image. A background surface compensation algorithm is proposed to account for this problem. First, we distinguish the cell image from the non-uniform background and a morphological image operation is used to reduce the noise effect on the background surface areas. Then, an adaptive sampling from the background surface is employed, taking dense samples from the high-variation area while leaving the smooth region mostly untouched. A surface fitting algorithm based on the optimal bi-cubic functional approximation is used to establish a whole background surface for the phase image. Once the background surface is found, the background compensated phase can be obtained by subtracting the estimated background from the original phase image. From the experimental results, the proposed algorithm performs effectively in removing the non-uniform background of the phase image and has the ability to obtain the specimen topography inside fluid medium under environmental vibrations.

Presence of biofilm containing viable multiresistant organisms despite terminal cleaning on clinical surfaces in an intensive care unit.

PubMed

Vickery, K; Deva, A; Jacombs, A; Allan, J; Valente, P; Gosbell, I B

2012-01-01

Despite recent attention to surface cleaning and hand hygiene programmes, multiresistant organisms (MROs) continue to be isolated from the hospital environment. Biofilms, consisting of bacteria embedded in exopolymeric substances (EPS) are difficult to remove due to their increased resistance to detergents and disinfectants, and periodically release free-swimming planktonic bacteria back into the environment which may may act as an infection source. To establish whether reservoirs of MROs exist in the environment as biofilms. Following terminal cleaning, equipment and furnishings were removed aseptically from an intensive care unit (ICU) and subjected to culture and scanning electron microscopy (SEM). Samples were placed in 5 mL of tryptone soya broth, sonicated for 5 min before plate culture on horse blood agar, Brillance MRSA and Brilliance VRE agar plates. Samples for SEM were fixed in 3% glutaraldehyde and hexamethyldisilizane (HMDS) prior to sputter-coating with gold and examination in an electron microscope. Biofilm was demonstrated visually on the sterile supply bucket, the opaque plastic door, the venetian blind cord, and the sink rubber, whereas EPS alone was seen on the curtain. Viable bacteria were grown from three samples, including MRSA from the venetian blind cord and the curtain. Biofilm containing MROs persist on clinical surfaces from an ICU despite terminal cleaning, suggesting that current cleaning practices are inadequate to control biofilm development. The presence of MROs being protected within these biofilms may be the mechanism by which MROs persist within the hospital environment. Copyright © 2011 The Healthcare Infection Society. Published by Elsevier Ltd. All rights reserved.

Degradation of radiator performance on Mars due to dust

NASA Technical Reports Server (NTRS)

Gaier, James R.; Perez-Davis, Marla E.; Rutledge, Sharon K.; Forkapa, Mark

1992-01-01

An artificial mineral of the approximate elemental composition of Martian soil was manufactured, crushed, and sorted into four different size ranges. Dust particles from three of these size ranges were applied to arc-textured Nb-1 percent Zr and Cu radiator surfaces to assess their effect on radiator performance. Particles larger than 75 microns did not have sufficient adhesive forces to adhere to the samples at angles greater than about 27 deg. Pre-deposited dust layers were largely removed by clear wind velocities greater than 40 m/s, or by dust-laden wind velocities as low as 25 m/s. Smaller dust grains were more difficult to remove. Abrasion was found to be significant only in high velocity winds (89 m/s or greater). Dust-laden winds were found to be more abrasive than clear wind. Initially dusted samples abraded less than initially clear samples in dust laden wind. Smaller dust particles of the simulant proved to be more abrasive than large. This probably indicates that the larger particles were in fact agglomerates.

Carborane-Based Metal-Organic Framework with High Methane and Hydrogen Storage Capacities

DTIC Science & Technology

2013-01-01

guest solvent molecules were removed via supercritical CO2 (see the Supporting Information for activation details),30,31 the samples were further...unique geometry of the carborane unit, NU-135 has a very high volumetric BET surface area of ca. 1900 m2/cm3. CH4, CO2 , and H2 adsorption isotherms...NU-135 has a very high volumetric BET surface area of ca. 1900 m2/cm3. CH4, CO2 , and H2 adsorption isotherms were measured over a broad range of

Carbon protrusions on PTFE surface prepared by ion irradiation and chemical defluorination

NASA Astrophysics Data System (ADS)

Kobayashi, T.; Iwaki, M.

2006-01-01

A surface of PTFE was covered with small protrusions by ion-beam irradiation. In this study, we converted PTFE protrusions into carbon protrusions by a defluorination (carbonization) process using sodium vapor. The morphology, composition and structure were analyzed by SEM-EDX, Raman spectroscopy and TEM. The irradiated PTFE sheets were packed in evacuated glass tubes with a sodium block and kept at 473 K for 2-48 h. The samples were then rinsed in HCl and distilled water to remove NaF precipitates. The EDX measurement showed that the NaF precipitates were completely removed by washing, and the percentage of carbon atoms was controlled from 60% to 99% by the treatment. Raman spectra showed that graphite structures grow during the defluorination process. TEM micrographs showed that the protrusions have a bubble structure and are covered with a thin wall. The carbonized protrusions were conductive and grew perpendicular to the substrate.

Cleaning of optical surfaces by capacitively coupled RF discharge plasma

DOE Office of Scientific and Technical Information (OSTI.GOV)

Yadav, P. K., E-mail: praveenyadav@rrcat.gov.in; Rai, S. K.; Nayak, M.

2014-04-24

In this paper, we report cleaning of carbon capped molybdenum (Mo) thin film by in-house developed radio frequency (RF) plasma reactor, at different powers and exposure time. Carbon capped Mo films were exposed to oxygen plasma for different durations at three different power settings, at a constant pressure. After each exposure, the thickness of the carbon layer and the roughness of the film were determined by hard x-ray reflectivity measurements. It was observed that most of the carbon film got removed in first 15 minutes exposure. A high density layer formed on top of the Mo film was also observedmore » and it was noted that this layer cannot be removed by successive exposures at different powers. A significant improvement in interface roughness with a slight improvement in top film roughness was observed. The surface roughness of the exposed and unexposed samples was also confirmed by atomic force microscopy measurements.« less

Molecular Structures of Al/Si and Fe/Si Coprecipitates and the Implication for Selenite Removal

PubMed Central

Chan, Ya-Ting; Kuan, Wen-Hui; Tzou, Yu-Min; Chen, Tsan-Yao; Liu, Yu-Ting; Wang, Ming-Kuang; Teah, Heng-Yi

2016-01-01

Aluminum and iron oxides have been often used in the coagulation processes during water purification due to their unique surface properties toward anions. In the presence of silica, the coprecipitation of Al/Si or Fe/Si might decrease the efficiency of wastewater purification and reuse. In this study, surface properties and molecular structures of Al/Si and Fe/Si coprecipitates were characterized using spectroscopic techniques. Also, the selenite removal efficiency of Al/Si and Fe/Si coprecipitates in relation to their surface and structural properties was investigated. While dissolved silicate increased with increasing pH from Fe/Si coprecipitates, less than 7% of silicate was discernible from Al/Si samples over the range from acidic to alkaline conditions. Our spectroscopic results showed that the associations between Al and Si were relatively stronger than that between Fe and Si in coprecipitates. In Al/Si coprecipitates, core-shell structures were developed with AlO6/AlO4 domains as the shells and Si frameworks polymerized from the SiO2 as the cores. However, Si framework remained relatively unchanged upon coprecipitation with Fe hydroxides in Fe/Si samples. The Si core with Al shell structure of Al/Si coprecipitates shielded the negative charges from SiO2 and thereby resulted in a higher adsorption capacity of selenite than Fe/Si coprecipitates. PMID:27095071

Health and safety plan for the removal action at the former YS-860 Firing Ranges, Oak Ridge Y-12 Plant, Oak Ridge, Tennessee

DOE Office of Scientific and Technical Information (OSTI.GOV)

NONE

1998-04-28

This health and safety plan sets forth the requirements and procedures to protect the personnel involved in the Lead Source Removal Project at the Former YS-86O Firing Ranges. This project will be conducted in a manner that ensures the protection of the safety and health of workers, the public, and the environment. The purpose of this removal action is to address lead contaminated soil and reduce a potential risk to human health and the environment. This site is an operable unit within the Upper East Fork Poplar Creek watershed. The removal action will contribute to early source actions within themore » watershed. The project will accomplish this through the removal of lead-contaminated soil in the target areas of the two small arms firing ranges. This plan covers the removal actions at the Former YS-86O Firing Ranges. These actions involve the excavation of lead-contaminated soils, the removal of the concrete trench and macadam (asphalt) paths, verification/confirmation sampling, grading and revegetation. The primary hazards include temperature extremes, equipment operation, noise, potential lead exposure, uneven and slippery working surfaces, and insects.« less

Characterization of E coli biofim formations on baby spinach leaf surfaces using hyperspectral fluorescence imaging

NASA Astrophysics Data System (ADS)

Cho, Hyunjeong; Baek, Insuck; Oh, Mirae; Kim, Sungyoun; Lee, Hoonsoo; Kim, Moon S.

2017-05-01

Bacterial biofilm formed by pathogens on fresh produce surfaces is a food safety concern because the complex extracellular matrix in the biofilm structure reduces the reduction and removal efficacies of washing and sanitizing processes such as chemical or irradiation treatments. Therefore, a rapid and nondestructive method to identify pathogenic biofilm on produce surfaces is needed to ensure safe consumption of fresh, raw produce. This research aimed to evaluate the feasibility of hyperspectral fluorescence imaging for detecting Escherichia.coli (ATCC 25922) biofilms on baby spinach leaf surfaces. Samples of baby spinach leaves were immersed and inoculated with five different levels (from 2.6x104 to 2.6x108 CFU/mL) of E.coli and stored at 4°C for 24 h and 48 h to induce biofilm formation. Following the two treatment days, individual leaves were gently washed to remove excess liquid inoculums from the leaf surfaces and imaged with a hyperspectral fluorescence imaging system equipped with UV-A (365 nm) and violet (405 nm) excitation sources to evaluate a spectral-image-based method for biofilm detection. The imaging results with the UV-A excitation showed that leaves even at early stages of biofilm formations could be differentiated from the control leaf surfaces. This preliminary investigation demonstrated the potential of fluorescence imaging techniques for detection of biofilms on leafy green surfaces.

Preparation and characterisation of core-shell CNTs@MIPs nanocomposites and selective removal of estrone from water samples.

PubMed

Gao, Ruixia; Su, Xiaoqian; He, Xiwen; Chen, Langxing; Zhang, Yukui

2011-01-15

This paper reports the preparation of carbon nanotubes (CNTs) functionalized with molecularly imprinted polymers (MIPs) for advanced removal of estrone. CNTs@Est-MIPs nanocomposites with a well-defined core-shell structure were obtained using a semi-covalent imprinting strategy, which employed a thermally reversible covalent bond at the surface of silica-coated CNTs for a large-scale production. The morphology and structure of the products were characterised by transmission electron microscopy and Fourier transform infrared spectroscopy. The adsorption properties were demonstrated by equilibrium rebinding experiments and Scatchard analysis. The results demonstrate that the imprinted nanocomposites possess favourable selectivity, high capacity and fast kinetics for template molecule uptake, yielding an adsorption capacity of 113.5 μmol/g. The synthetic process is quite simple, and the different batches of synthesized CNTs@Est-MIPs nanocomposites showed good reproducibility in template binding. The feasibility of removing estrogenic compounds from environmental water using the CNTs@Est-MIPs nanocomposites was demonstrated using water samples spiked with estrone. Copyright © 2010 Elsevier B.V. All rights reserved.

Amperometric micro pH measurements in oxygenated saliva.

PubMed

Chaisiwamongkhol, Korbua; Batchelor-McAuley, Christopher; Compton, Richard G

2017-07-24

An amperometric micro pH sensor has been developed based on the chemical oxidation of carbon fibre surfaces (diameter of 9 μm and length of ca. 1 mm) to enhance the population of surface quinone groups for the measurement of salivary pH. The pH analysis utilises the electrochemically reversible two-electron, two-proton behaviour of surface quinone groups on the micro-wire electrodes. A Nernstian response is observed across the pH range 2-8 which is the pH range of many biological fluids. We highlight the measurement of pH in small volumes of biological fluids without the need for oxygen removal and specifically the micro pH electrode is examined by measuring the pH of commercial synthetic saliva and authentic human saliva samples. The results correspond well with those obtained by using commercial glass pH electrodes on large volume samples.

Surface modification and characterization of basalt fibers as potential reinforcement of concretes

NASA Astrophysics Data System (ADS)

Iorio, M.; Santarelli, M. L.; González-Gaitano, G.; González-Benito, J.

2018-01-01

Basalt fibers were surface treated with silane coupling agents as a method to enhance the adhesion and durability of fiber-matrix interfaces in concrete based composite materials. In particular, this work has been focused on the study of basalt fibers chemical coatings with aminosilanes and their subsequent characterization. Surface treatments were carried out after removing the original sizing applied by manufacturer and pretreating them with an activation process of surface silanol regeneration. Different samples were considered to make convenient comparisons: as received fibers (commercial), calcinated fibers (without commercial sizing), activated samples (calcinated fibers subjected to an acid process for hydroxyl regeneration), and silanized fibers with γ-aminopropiltriethoxysilane, γ-aminopropilmethyldiethoxysilane and a mixture of 50% by weight of both silanes. A deep characterization was carried out in terms of structure using X-ray diffraction, XRD, and Fourier transform infrared spectroscopy, FTIR, thermal properties by thermogravimetric analysis, TGA, coupled with single differential thermal analysis, SDTA, and morphology by scanning electron microscopy, SEM, and atomic force microscopy, AFM.

Pollutant loads of surface runoff in Wuhan City Zoo, an urban tourist area.

PubMed

Zhao, Jian-wei; Shan, Bao-qing; Yin, Cheng-qing

2007-01-01

The pollutant loads of surface runoff in an urban tourist area have been investigated for two years in the Wuhan City Zoo, China. Eight sampling sites, including two woodlands, three animal yards, two roofs and one road, were selected for sampling and study. The results indicate that pollutants ranked in a predictable order of decreasing load (e.g. animal yard > roof > woodland > road), with animal yards acting as the key pollution source in the zoo. Pollutants were transported mainly by particulate form in runoff. Particulate nitrogen and particulate phosphorous accounted on average for 61%, 78% of total pollutant, respectively, over 13 monitored rainfall events. These results indicate the treatment practices should be implemented to improve particulate nutrient removal. Analysis of the M(V) curve indicate that no first flush effect existed in the surface runoff from pervious areas (e.g. woodland, animal ground yard), whereas a first flush effect was evident in runoff from impervious surfaces (e.g. animal cement yard, roof, road).

Performance of conventional multi-barrier drinking water treatment plants for the removal of four artificial sweeteners.

PubMed

Scheurer, Marco; Storck, Florian R; Brauch, Heinz-J; Lange, Frank T

2010-06-01

Due to incomplete removal of artificial sweeteners in wastewater treatment plants some of these compounds end up in receiving surface waters, which are used for drinking water production. The sum of removal efficiency of single treatment steps in multi-barrier treatment systems affects the concentrations of these compounds in the provided drinking water. This is the first systematic study revealing the effectiveness of single treatment steps in laboratory experiments and in waterworks. Six full-scale waterworks using surface water influenced raw water were sampled up to ten times to study the fate of acesulfame, saccharin, cyclamate and sucralose. For the most important treatment technologies the results were confirmed by laboratory batch experiments. Saccharin and cyclamate proved to play a minor role for drinking water treatment plants as they were eliminated by nearly 100% in all waterworks with biologically active treatment units like river bank filtration (RBF) or artificial groundwater recharge. Acesulfame and sucralose were not biodegraded during RBF and their suitability as wastewater tracers under aerobic conditions was confirmed. Sucralose proved to be persistent against ozone and its transformation was < 20% in lab and field investigations. Remaining traces were completely removed by subsequent granular activated carbon (GAC) filters. Acesulfame readily reacts with ozone (pseudo first-order rate constant k = 1.3 x 10(-3) s(-1) at 1 mg L(-1) ozone concentration). However, the applied ozone concentrations and contact times under typical waterworks conditions only led to an incomplete removal (18-60%) in the ozonation step. Acesulfame was efficiently removed by subsequent GAC filters with a low throughput of less than 30 m(3) kg(-1), but removal strongly depended on the GAC preload. Thus, acesulfame was detected up to 0.76 microg L(-1) in finished water. 2010 Elsevier Ltd. All rights reserved.

Ultraviolet complex refractive index of Martian dust Laboratory measurements of terrestrial analogs

NASA Technical Reports Server (NTRS)

Egan, W. G.; Hilgeman, T.; Pang, K.

1975-01-01

The optical complex index of refraction of four candidate Martian surface materials has been determined between 0.185 and 0.4 microns using a modified Kubelka-Munk scattering theory. The cadidate materials were limonite, andesite, montmorillonite, and basalt. The effect of scattering has been removed from the results. Also presented are diffuse reflection and transmission data on these samples.

Examination of Surveyor 3 parts with the scanning electron microscope and electron microprobe

NASA Technical Reports Server (NTRS)

Chodos, A. A.; Devaney, J. R.; Evens, K. C.

1972-01-01

Two screws and two washers, several small chips of tubing, and a fiber removed from a third screw were examined with the scanning electron microscope and the electron microprobe. The purpose of the examination was to determine the nature of the material on the surface of these samples and to search for the presence of meteoritic material.

Radiological Scoping Survey of the Scotia Depot Scotia, New York

DOE Office of Scientific and Technical Information (OSTI.GOV)

E. N. Bailey

2005-02-05

At the request of the Defense Logistics Agency, the Oak Ridge Institute for Science and Education conducted radiological scoping surveys of the Scotia Depot during the period of September 24 through 27, 2007. The scoping survey included visual inspections and limited radiological surveys performed in accordance with area classification that included surface scans, total and removable activity measurements, and soil sampling.

Removal of BrO₃⁻ from drinking water samples using newly developed agricultural waste-based activated carbon and its determination by ultra-performance liquid chromatography-mass spectrometry.

PubMed

Naushad, Mu; Khan, Mohammad R; ALOthman, Zeid A; AlSohaimi, Ibrahim; Rodriguez-Reinoso, Francisco; Turki, Turki M; Ali, Rahmat

2015-10-01

Activated carbon was prepared from date pits via chemical activation with H3PO4. The effects of activating agent concentration and activation temperature on the yield and surface area were studied. The optimal activated carbon was prepared at 450 °C using 55 % H3PO4. The prepared activated carbon was characterized by Fourier transform infrared spectroscopy, scanning electron microscopy, thermogravimetric-differential thermal analysis, and Brunauer, Emmett, and Teller (BET) surface area. The prepared date pit-based activated carbon (DAC) was used for the removal of bromate (BrO3 (-)). The concentration of BrO3 (-) was determined by ultra-performance liquid chromatography-mass tandem spectrometry (UPLC-MS/MS). The experimental equilibrium data for BrO3 (-) adsorption onto DAC was well fitted to the Langmuir isotherm model and showed maximum monolayer adsorption capacity of 25.64 mg g(-1). The adsorption kinetics of BrO3 (-) adsorption was very well represented by the pseudo-first-order equation. The analytical application of DAC for the analysis of real water samples was studied with very promising results.

Improvement of the enzymatic hydrolysis of furfural residues by pretreatment with combined green liquor and hydrogen peroxide.

PubMed

Yu, Hai-Long; Tang, Yong; Xing, Yang; Zhu, Li-Wei; Jiang, Jian-Xin

2013-11-01

A potential commercial pretreatment for furfural residues (FRs) was investigated by using a combination of green liquor and hydrogen peroxide (GL-H2O2). The results showed that 56.2% of lignin removal was achieved when the sample was treated with 0.6 g H2O2/g-DS (dry substrate) and 6 mL GL/g-DS at 80 °C for 3 h. After 96 h hydrolysis with 18 FPU/g-cellulose for cellulase, 27 CBU/g-cellulose for β-glucosidase, the glucose yield increased from 71.2% to 83.6%. Ethylenediaminetetraacetic acid was used to reduce the degradation of H2O2, the glucose yield increased to 90.4% after the addition of 1% (w/w). The untreated FRs could bind more easily to cellulase than pretreated FRs could. The structural changes on the surface of sample were characterized by X-ray photoelectron spectroscopy. The results indicated that the surface lignin could be effectively removed during pretreatment, thereby decreasing the enzyme-lignin binding activity. Moreover, the carbonyl from lignin plays an important role in cellulase binding. Copyright © 2013 Elsevier Ltd. All rights reserved.

Mobile system for microwave removal of concrete surfaces

DOEpatents

White, Terry L.; Bigelow, Timothy S.; Schaich, Charles R.; Foster, Jr., Don

1997-01-01

A method and apparatus for the microwave removal of contaminated concrete surfaces. The apparatus comprises a housing adapted to pass over a support surface. The housing includes a waveguide for directing microwave energy to the surface at an angle maximizing absorption of microwave energy by the surface. The apparatus is further provided with a source of microwave energy operably associated with the waveguide, wherein the microwave energy has a frequency of between about 10.6 GHz and about 24 GHz and acts to remove the uppermost layer from the surface. The apparatus further includes a debris containment assembly comprising a vacuum assembly operably associated with the housing. The vacuum assembly is adapted to remove debris from the area adjacent the surface.

Mobile system for microwave removal of concrete surfaces

DOEpatents

White, T.L.; Bigelow, T.S.; Schaich, C.R.; Foster, D. Jr.

1997-06-03

A method and apparatus are disclosed for the microwave removal of contaminated concrete surfaces. The apparatus comprises a housing adapted to pass over a support surface. The housing includes a waveguide for directing microwave energy to the surface at an angle maximizing absorption of microwave energy by the surface. The apparatus is further provided with a source of microwave energy operably associated with the waveguide, wherein the microwave energy has a frequency of between about 10.6 GHz and about 24 GHz and acts to remove the uppermost layer from the surface. The apparatus further includes a debris containment assembly comprising a vacuum assembly operably associated with the housing. The vacuum assembly is adapted to remove debris from the area adjacent the surface. 7 figs.

Sample introduction apparatus for a flow cytometer

DOEpatents

Van den Engh, Ger

1998-01-01

A sample introduction system for a flow cytometer allows easy change of sample containers such as test tubes and facilitates use in high pressure environments. The sample container includes a cap having a pressure supply chamber and a sample container attachment cavity. A sample container may be automatically positioned into the attachment cavity so as to sealably engage the end of the sample container as its outer surface. This positioning may be accomplished through some sample introduction mechanism. To facilitate cleaning HPLC tubing and fittings may be used in a manner which facilitates removable of the entire tubing from both the nozzle container and other sample container cap to permit its replacement to avoid contamination. The sample container support may include horizontal stops which loosely limit the movement of the sample container and thus avoid further stresses upon it.

Sample introduction system for a flow cytometer

DOEpatents

Van den Engh, Ger

1997-01-01

A sample introduction system for a flow cytometer allows easy change of sample containers such as test tubes and facilitates use in high pressure environments. The sample container includes a cap having a pressure supply chamber and a sample container attachment cavity. A sample container may be automatically positioned into the attachment cavity so as to sealably engage the end of the sample container as its outer surface. This positioning may be accomplished through some sample introduction mechanism. To facilitate cleaning, HPLC tubing and fittings may be used in a manner which facilitates removing of the entire tubing from both the nozzle container and other sample container cap to permit its replacement to avoid contamination. The sample container support may include horizontal stops which loosely limit the movement of the sample container and thus avoid further stresses upon it.

Sample introduction apparatus for a flow cytometer

DOEpatents

Van den Engh, G.

1998-03-10

A sample introduction system for a flow cytometer allows easy change of sample containers such as test tubes and facilitates use in high pressure environments. The sample container includes a cap having a pressure supply chamber and a sample container attachment cavity. A sample container may be automatically positioned into the attachment cavity so as to sealably engage the end of the sample container as its outer surface. This positioning may be accomplished through some sample introduction mechanism. To facilitate cleaning HPLC tubing and fittings may be used in a manner which facilitates removable of the entire tubing from both the nozzle container and other sample container cap to permit its replacement to avoid contamination. The sample container support may include horizontal stops which loosely limit the movement of the sample container and thus avoid further stresses upon it. 3 figs.

Sample introduction system for a flow cytometer

DOEpatents

Engh, G. van den

1997-02-11

A sample introduction system for a flow cytometer allows easy change of sample containers such as test tubes and facilitates use in high pressure environments. The sample container includes a cap having a pressure supply chamber and a sample container attachment cavity. A sample container may be automatically positioned into the attachment cavity so as to sealably engage the end of the sample container as its outer surface. This positioning may be accomplished through some sample introduction mechanism. To facilitate cleaning, HPLC tubing and fittings may be used in a manner which facilitates removing of the entire tubing from both the nozzle container and other sample container cap to permit its replacement to avoid contamination. The sample container support may include horizontal stops which loosely limit the movement of the sample container and thus avoid further stresses upon it. 3 figs.

Potential exposures associated with indoor marijuana growing operations.

PubMed

Martyny, John W; Serrano, Kate A; Schaeffer, Joshua W; Van Dyke, Mike V

2013-01-01

We entered a total of 30 indoor marijuana grow operations (IMGO) with law enforcement investigators in order to determine potential exposures to first responders. Samples for airborne fungal spores, volatile organic compounds, carbon dioxide, carbon monoxide, and delta-9-tetrahydrocannabinol (THC) were obtained as well as the identification of chemicals utilized in the IMGO. The chemicals utilized within the IMGOs were primarily pesticides and fertilizers with none showing high toxicity. Although several of the IMGOs had CO2 enrichment processes involving combustion, CO levels were not elevated. THC levels were identified on surfaces within the IMGOs and on the hands of the investigators. Surface levels ranged from <0.1 μg /100 cm(2) to 2000 μg /100 cm(2) with a geometric mean of 0.37 μg /100 cm(2). THC levels on the hands of officers ranged from <0.10 μg /wipe to 2900 μg /wipe with a geometric mean of 15 μg /wipe. These levels were not considered to be elevated to the point of causing a toxic exposure to responders. A total of 407 fungal spore samples were taken using both slit impactor plates and 400-hole impactors. Both methods identified elevated fungal spore levels, especially during the removal of plants from some of the IMGOs. After plant removal, spore counts increased to levels above 50,000 spores/m(3) with one sample over 500,000 spores/m(3). In addition, we found that there was a shift in species between indoor and outdoor samples with Cladosporium sp. the predominant outdoor species and Penicillium sp. the predominant indoor species. We concluded that the potential increase in fungal spore concentrations associated with the investigation and especially removal of the marijuana plants could potentially expose responders to levels of exposure consistent with those associated with mold remediation processes and that respiratory protection is advisable.

Summary of Surface Swipe Sampling for Beryllium on Lead Bricks and Shielding

DOE Office of Scientific and Technical Information (OSTI.GOV)

Paik, S Y; Barron, D A

2011-08-03

Approximately 25,000 lbs of lead bricks at Site 300 were assessed by the Site 300 Industrial Hygienis tand Health Physicist for potential contamination of beryllium and radiation for reuse. These lead bricks and shielding had been used as shielding material during explosives tests that included beryllium and depleted uranium. Based on surface swipe sampling that was performed between July 26 and October 11, 2010, specifically for beryllium, the use of a spray encapsulant was found to be an effective means to limit removable surface contamination to levels below the DOE release limit for beryllium, which is 0.2 mcg/100 cm{sup 2}.more » All the surface swipe sampling data for beryllium and a timeline of when the samples were collected (and a brief description) are presented in this report. On December 15, 2010, the lead bricks and shielding were surveyed with an ion chamber and indicated dose rates less than 0.05 mrem per hour on contact. This represents a dose rate consistent with natural background. An additional suevey was performed on February 8, 2011, using a GM survey instrument to estimate total activity on the lead bricks and shielding, confirming safe levels of radioactivity. The vendor is licensed to possess and work with radioactive material.« less

Controlled study of mold growth and cleaning procedure on treated and untreated wet gypsum wallboard in an indoor environment.

PubMed

Krause, Michael; Geer, William; Swenson, Lonie; Fallah, Payam; Robbins, Coreen

2006-08-01

The basis for some common gypsum wallboard mold remediation practices was examined. The bottom inch of several gypsum wallboard panels was immersed in bottled drinking water; some panels were coated and others were untreated. The panels were examined and tested for a period of 8 weeks. This study investigated: (a) whether mold growth, detectable visually or with tape lift samples, occurs within 1 week on wet gypsum wallboard; (b) the types, timing, and extent of mold growth on wet gypsum wallboard; (c) whether mold growth is present on gypsum wallboard surfaces 6 inches from visible mold growth; (d) whether some commonly used surface treatments affect the timing of occurrence and rate of mold growth; and (e) if moldy but dried gypsum wallboard can be cleaned with simple methods and then sealed with common surface treatments so that residual mold particles are undetectable with typical surface sampling techniques. Mold growth was not detected visually or with tape lift samples after 1 week on any of the wallboard panels, regardless of treatment, well beyond the 24-48 hours often mentioned as the incubation period. Growth was detected at 2 weeks on untreated gypsum. Penicillium, Cladosporium, and Acremonium were early colonizers of untreated panels. Aspergillus, Epicoccum, Alternaria, and Ulocladium appeared later. Stachybotrys was not found. Mold growth was not detected more than 6 inches beyond the margin of visible mold growth, suggesting that recommendations to remove gypsum wallboard more than 1 foot beyond visible mold are excessive. The surface treatments resulted in delayed mold growth and reduced the area of mold growth compared with untreated gypsum wallboard. Results showed that simple cleaning of moldy gypsum wallboard was possible to the extent that mold particles beyond "normal trapping" were not found on tape lift samples. Thus, cleaning is an option in some situations where removal is not feasible or desirable. In cases where conditions are not similar to those of this study, or where large areas may be affected, a sample area could be cleaned and tested to verify that the cleaning technique is sufficient to reduce levels to background or normal trapping. These results are generally in agreement with laboratory studies of mold growth on, and cleaning of, gypsum wallboard.

Sorption of tetracycline on biochar derived from rice straw under different temperatures

PubMed Central

Wang, Hua; Chu, Yixuan; Huang, Fang; Song, Yali; Xue, Xiangdong

2017-01-01

Biochars produced from the pyrolysis of waste biomass under limited oxygen conditions could serve as adsorbents in environmental remediation processes. Biochar samples derived from rice straw that were pyrolyzed at 300 (R300), 500 (R500) and 700°C (R700) were used as adsorbents to remove tetracycline from an aqueous solution. Both the Langmuir and Freundlich models fitted the adsorption data well (R2 > 0.919). The adsorption capacity increased with pyrolysis temperature. The R500 and R700 samples exhibited relative high removal efficiencies across a range of initial tetracycline concentrations (0.5mg/L-32mg/L) with the maximum (92.8%–96.7%) found for adsorption on R700 at 35°C. The relatively high surface area of the R700 sample and π–π electron-donor acceptor contributed to the high adsorption capacities. A thermodynamic analysis indicated that the tetracycline adsorption process was spontaneous and endothermic. The pH of solution was also found to influence the adsorption processes; the maximum adsorption capacity occurred at a pH of 5.5. These experimental results highlight that biochar derived from rice straw is a promising candidate for low-cost removal of tetracycline from water. PMID:28792530

Occurrence of neonicotinoid insecticides in finished drinking water and fate during drinking water treatment

USGS Publications Warehouse

Klarich, Kathryn L.; Pflug, Nicholas C.; DeWald, Eden M.; Hladik, Michelle L.; Kolpin, Dana W.; Cwiertny, David M.; LeFevre, Gergory H.

2017-01-01

Neonicotinoid insecticides are widespread in surface waters across the agriculturally-intensive Midwestern US. We report for the first time the presence of three neonicotinoids in finished drinking water and demonstrate their general persistence during conventional water treatment. Periodic tap water grab samples were collected at the University of Iowa over seven weeks in 2016 (May-July) after maize/soy planting. Clothianidin, imidacloprid, and thiamethoxam were ubiquitously detected in finished water samples and ranged from 0.24-57.3 ng/L. Samples collected along the University of Iowa treatment train indicate no apparent removal of clothianidin and imidacloprid, with modest thiamethoxam removal (~50%). In contrast, the concentrations of all neonicotinoids were substantially lower in the Iowa City treatment facility finished water using granular activated carbon (GAC) filtration. Batch experiments investigated potential losses. Thiamethoxam losses are due to base-catalyzed hydrolysis at high pH conditions during lime softening. GAC rapidly and nearly completely removed all three neonicotinoids. Clothianidin is susceptible to reaction with free chlorine and may undergo at least partial transformation during chlorination. Our work provides new insights into the persistence of neonicotinoids and their potential for transformation during water treatment and distribution, while also identifying GAC as an effective management tool to lower neonicotinoid concentrations in finished drinking water.

Surface quality of silicon wafer improved by hydrodynamic effect polishing

NASA Astrophysics Data System (ADS)

Peng, Wenqiang; Guan, Chaoliang; Li, Shengyi

2014-08-01

Differing from the traditional pad polishing, hydrodynamic effect polishing (HEP) is non-contact polishing with the wheel floated on the workpiece. A hydrodynamic lubricated film is established between the wheel and the workpiece when the wheel rotates at a certain speed in HEP. Nanoparticles mixed with deionized water are employed as the polishing slurry, and with action of the dynamic pressure, nanoparticles with high chemisorption due to the high specific surface area can easily reacted with the surface atoms forming a linkage with workpiece surface. The surface atoms are dragged away when nanoparticles are transported to separate by the flow shear stress. The development of grand scale integration put extremely high requirements on the surface quality on the silicon wafer with surface roughness at subnanometer and extremely low surface damage. In our experiment a silicon sample was processed by HEP, and the surface topography before and after polishing was observed by the atomic force microscopy. Experiment results show that plastic pits and bumpy structures on the initial surface have been removed away clearly with the removal depth of 140nm by HEP process. The processed surface roughness has been improved from 0.737nm RMS to 0.175nm RMS(10μm×10μm) and the section profile shows peaks of the process surface are almost at the same height. However, the machining ripples on the wheel surface will duplicate on the silicon surface under the action of the hydrodynamic effect. Fluid dynamic simulation demonstrated that the coarse surface on the wheel has greatly influence on the distribution of shear stress and dynamic pressure on the workpiece surface.

Modelling of discrete TDS-spectrum of hydrogen desorption

NASA Astrophysics Data System (ADS)

Rodchenkova, Natalia I.; Zaika, Yury V.

2015-12-01

High concentration of hydrogen in metal leads to hydrogen embrittlement. One of the methods to evaluate the hydrogen content is the method of thermal desorption spectroscopy (TDS). As the sample is heated under vacuumization, atomic hydrogen diffuses inside the bulk and is desorbed from the surface in the molecular form. The extraction curve (measured by a mass-spectrometric analyzer) is recorded. In experiments with monotonous external heating it is observed that background hydrogen fluxes from the extractor walls and fluxes from the sample cannot be reliably distinguished. Thus, the extraction curve is doubtful. Therefore, in this case experimenters use discrete TDS-spectrum: the sample is removed from the analytical part of the device for the specified time interval, and external temperature is then increased stepwise. The paper is devoted to the mathematical modelling and simulation of experimental studies. In the corresponding boundary-value problem with nonlinear dynamic boundary conditions physical- chemical processes in the bulk and on the surface are taken into account: heating of the sample, diffusion in the bulk, hydrogen capture by defects, penetration from the bulk to the surface and desorption. The model aimed to analyze the dynamics of hydrogen concentrations without preliminary artificial sample saturation. Numerical modelling allows to choose the point on the extraction curve that corresponds to the initial quantity of the surface hydrogen, to estimate the values of the activation energies of diffusion, desorption, parameters of reversible capture and hydride phase decomposition.

In vitro corrosion behaviour and microhardness of high-copper amalgams with platinum and indium.

PubMed

Ilikli, B G; Aydin, A; Işimer, A; Alpaslan, G

1999-02-01

Samples prepared from Luxalloy, GS-80, Permite-C and Logic and polished after 24 h by traditional methods were stored in polypropylene tubes containing phosphate-buffered saline solutions (pH 3.5 and 6.5) and distilled water. The amounts of mercury, silver, tin, copper, zinc, platinum and indium in the test solutions were determined at the first, second, eighth, 52nd and 78th week by atomic absorption spectrometry. At the end of the eighth week the amalgam samples were removed from solutions and evaluated by Rockwell Super Scial Microhardness tester. Statistically significant low amounts of metal ions were measured for Permite-C containing indium and Logic containing platinum. The microhardness test results showed that there were statistically significant increases in the microhardness of Permite-C and Logic. As a result it was shown that the amalgam samples were affected from corrosion conditions to different degrees. Sample of the Logic group that was stored in distilled water, showed smoother surface properties than other amalgam samples containing high copper. However, it was observed that samples of Permite-C group had the smoothest surface properties.

Exposures of tungsten nanostructures to divertor plasmas in DIII-D

DOE PAGES

Rudakov, D. L.; Wong, C. P. C.; Doerner, R. P.; ...

2016-01-22

Tungsten nanostructures (W-fuzz) prepared in the PISCES-A linear device have been found to survive direct exposure to divertor plasmas in DIII-D. W-fuzz was exposed in the lower divertor of DIII-D using the divertor material evaluation system. Two samples were exposed in lower single null (LSN) deuterium H-mode plasmas. The first sample was exposed in three discharges terminated by vertical displacement event disruptions, and the second in two discharges near the lowered X-point. More recently, three samples were exposed near the lower outer strike point in predominantly helium H-mode LSN plasmas. In all cases, the W-fuzz survived plasma exposure with littlemore » obvious damage except in the areas where unipolar arcing occurred. In conclusion, arcing is effective in W-fuzz removal, and it appears that surfaces covered with W-fuzz can be more prone to arcing than smooth W surfaces.« less

Picosecond laser micromachining prior to FIB milling for electronic microscopy sample preparation

NASA Astrophysics Data System (ADS)

Sikora, Aurélien; Fares, Lahouari; Adrian, Jérôme; Goubier, Vincent; Delobbe, Anne; Corbin, Antoine; Sentis, Marc; Sarnet, Thierry

2017-10-01

In order to check the manufacturing quality of electronic components using electron microscopy, the area of interest must be exposed. This requires the removal of a large quantity of matter without damaging the surrounding area. This step can be accomplished using ion milling but the processing can last a few hours. In order to accelerate the preparation of the samples, picosecond laser micromachining prior to Focused Ion Beam polishing is envisioned. Laser ablation allows the fast removal of matter but induces damages around the ablated area. Therefore the process has to be optimized in order to limit the size of both the heat affected zone and induced dislocation zone. For this purpose, cavities have been engraved in silicon and in electronic components, using a linearly polarized picosecond laser (∼50 ps) at three different wavelengths (343, 515 and 1030 nm). Results showed that the cross sectional shapes and the surface topologies can be tuned by the laser fluence and the number of pulses. Clear cross sections of bumps and cavity openings, exposing multilayer interfaces, are demonstrated. The silicon removal rates, tuned by the applied energy density, have been measured. Removal rates achieved at 200 kHz were typically hundred times higher than those achieved by ion milling and the best efficiency was obtained at 343 nm.

Space environmental effects on silvered Teflon thermal control surfaces

NASA Technical Reports Server (NTRS)

Hemminger, C. S.; Stuckey, W. K.; Uht, J. C.

1991-01-01

Cumulative space environment effects on Ag/fluorinated ethylene propylene (FEP) were a function of exposure orientation. Samples from nineteen silvered Teflon (Ag/FEP) thermal control surfaces recovered from the Long Duration Exposure Facility (LDEF) were analyzed to determine changes in this material as a function of position on the spacecraft. Although solar absorptance and infrared emittance of measured thermal blanket specimens are relatively unchanged from control specimen values, significant changes in surface morphology, composition and chemistry were observed. Researchers hypothesize that the FEP surfaces on LDEF were degraded by ultraviolet radiation exposure at all orientations, but that the damaged material had been removed by erosion from the blankets exposed to atomic oxygen flux and that contamination is masking the damage on trays flanking the trailing edge.

Material for surface-enhanced Raman spectroscopy, and SER sensors and method for preparing same

NASA Technical Reports Server (NTRS)

Farquharson, Stuart (Inventor); Nelson, Chad (Inventor); Lee, Yuan-Hsiang (Inventor)

2003-01-01

Metal-doped sol-gel materials, suitable for use as sensors for surface-enhanced Raman spectroscopic analysis for trace chemical detection, are produced by effecting gelation and solvent removal of a doped sol-gel under mild temperature conditions. At least in certain instances reaction and drying will desirably be effected in an oxygen-starved environment. The metal of the sol-gel material functions, when irradiated, to produce a plasmon field for interaction with molecules of an analyte in contact therewith, increasing by orders of magnitude Raman photons that are generate by excitation radiation, and the method allows matching of the metal and metal particle size to a wavelength of light (or incident radiation, e.g., laser radiation) to generate surface plasmons. The porosity of the sol-gel material dramatically increases the surface area, and thereby the amount of metal exposed for analyte interaction. The sensors provided may be in the form of glass vials, fiber optics, multi-well micro-sample plates, etc., having surface coatings of the doped sol-gel material, to provide sampling systems for use in a Raman instrument.

Mechanisms for parasites removal in a waste stabilisation pond.

PubMed

Reinoso, Roberto; Blanco, Saúl; Torres-Villamizar, Linda A; Bécares, Eloy

2011-04-01

A waste stabilisation pond (WSP) system formed by two anaerobic ponds, a facultative pond and a maturation pond was studied from December 2003 to September 2004 in north-western Spain in order to evaluate its efficiency in the removal of faecal indicator bacteria (total coliforms, Escherichia coli, faecal streptococci), coliphages, helminth eggs and protozoan (oo)cysts (Cryptosporidium and Giardia). Furthermore, sediment samples were collected from the bottom of the ponds to assess the settling rates and thus determine the main pathogen removal mechanisms in the WSPs system. The overall removal ranged from 1.4 log units for coliphages in the cold period to 5.0 log units for E. coli in the hot period. Cryptosporidium oocysts were reduced by an average of 96%, Giardia cysts by 98% and helminth eggs by 100%. The anaerobic ponds showed significantly higher surface removal rates (4.6, 5.2 and 3.7 log (oo)cysts/eggs removed m(-2) day(-1), respectively) than facultative and maturation ponds. Sunlight and water physicochemical conditions were the main factors influencing C. parvum oocysts removal both in the anaerobic and maturation ponds, whereas other factors like predation or natural mortality were more important in the facultative pond. Sedimentation, the most commonly proposed mechanism for cyst removal had, therefore, a negligible influence in the studied ponds.

Reactivity of clay minerals with acids and alkalies

USGS Publications Warehouse

Carroll, Dorothy; Starkey, Harry C.

1971-01-01

One-g samples of a montmorillonite, a metabentonite, an illite, two kaolinites, and three halloysites were treated with 50 ml of hydrochloric acid (6⋅45 N, 1:1), acetic acid (4⋅5 N, 1:3), sodium hydroxide (2⋅8 N), sodium chloride solution (pH 6⋅10; Na = 35‰; Cl = 21⋅5‰), and natural sea water (pH 7⋅85; Na = 35⋅5‰; Cl = 21⋅ 5‰) for a 10-day period in stoppered plastic vials. The supernatant solutions were removed from the clay minerals and analyzed for SiO2, Al2O3, CaO, MgO, Na2O, and K2O. All the solutions removed some SiO2, Al2O3, and Fe2O3 from the samples, but the quantities were small. Sodium hydroxide attacked the kaolin group minerals more strongly than it did montmorillonite, metabentonite, or illite. Halloysite was more strongly attacked by hydrochloric acid than was any of the other experimental minerals. Hydrochloric acid removed iron oxide coatings from soil clay minerals, but acetic acid did not remove them completely. The samples most strongly attacked by HCl and NaOH were examined by X-ray diffraction. Acid treatment did not destroy the structure of the clays, but the halloysite structure was partially destroyed. Sodium hydroxide attacked the halloysite structure, as shown by chemical analysis and X-ray diffraction. These experiments show that treatment in dilute acids has no harmful effect in the preparation of clays for X-ray diffraction. Acetic acid is preferred to hydrochloric acid for this purpose. Hydrochloric acid cleans clay minerals by removing free iron oxide from the surface; acetic acid is less effective.

Effect of ND:YAG laser irradiation and root planing on the root surface: structural and thermal effects.

PubMed

Wilder-Smith, P; Arrastia, A M; Schell, M J; Liaw, L H; Grill, G; Berns, M W

1995-12-01

Effects of ND:YAG laser irradiation on untreated and root planed tooth roots were investigated to determine whether a cleaning effect and/or removal of smear layer could be achieved without concomitant microstructural or thermal damage. Sixty (60) healthy extracted teeth were either untreated, irradiated only, root planed only, or irradiated and root planed. Intra-pulpal and surface temperatures were monitored during irradiation, then SEM was performed. Smear layer elimination was achieved without inducing hard tissue microstructural damage at 5W, using pulse durations and intervals of 0.1 s, a fluence of 0.77 J/cm2, and a total energy density of approximately 700 J/cm2. However, these results were not consistent in all samples. At these parameters, intra-pulpal temperature increases of 9 to 22 degrees C and surface temperature increases of 18 to 36 degrees C were recorded. Thus, despite their effectiveness for smear layer removal, these parameters may not be appropriate for clinical use as an adjunct to conventional periodontal therapy.

Nanoscale Trapping and Squeeze-Out of Confined Alkane Monolayers.

PubMed

Gosvami, N N; O'Shea, S J

2015-12-01

We present combined force curve and conduction atomic force microscopy (AFM) data for the linear alkanes CnH2n+2 (n = 10, 12, 14, 16) confined between a gold-coated AFM tip and a graphite surface. Solvation layering is observed in the force curves for all liquids, and conduction AFM is used to study in detail the removal of the confined (mono)layer closest to the graphite surface. The squeeze-out behavior of the monolayer can be very different depending upon the temperature. Below the monolayer melting transition temperatures the molecules are in an ordered state on the graphite surface, and fast and complete removal of the confined molecules is observed. However, above the melting transition temperature the molecules are in a disordered state, and even at large applied pressure a few liquid molecules are trapped within the tip-sample contact zone. These findings are similar to a previous study for branched alkanes [ Gosvami Phys. Rev. Lett. 2008, 100, 076101 ], but the observation for the linear alkane homologue series demonstrates clearly the dependence of the squeeze-out and trapping on the state of the confined material.

Graphene nanocomposites as thermal interface materials for cooling energy devices

NASA Astrophysics Data System (ADS)

Dmitriev, A. S.; Valeev, A. R.

2017-11-01

The paper describes the technology of creating samples of graphene nanocomposites based on graphene flakes obtained by splitting graphite with ultrasound of high power. Graphene nanocomposites in the form of samples are made by the technology of weak sintering at high pressure (200-300 bar) and temperature up to 150 0 C, and also in the form of compositions with polymer matrices. The reflection spectra in the visible range and the near infrared range for the surface of nanocomposite samples are studied, the data of optical and electronic spectroscopy of such samples are givenIn addition, data on the electrophysical and thermal properties of the nanocomposites obtained are presented. Some analytical models of wetting and spreading over graphene nanocomposite surfaces have been constructed and calculated, and their effective thermal conductivity has been calculated and compared with the available experimental data. Possible applications of graphene nanocomposites for use as thermal interface materials for heat removal and cooling for power equipment, as well as microelectronics and optoelectronics devices are described.

Organofunctionalized Amazon smectite for dye removal from aqueous medium--kinetic and thermodynamic adsorption investigations.

PubMed

Guerra, Denis L; Silva, Weber L L; Oliveira, Helen C P; Viana, Rúbia R; Airoldi, Claudio

2011-02-15

The objective of this study is to examine the adsorption behavior of Sumifix Brilliant Orange 3R textile dye from aqueous solution on smectite sample, an abundant Amazon clay. The original smectite clay mineral has been collected from Amazon region, Brazil. The compound 2-aminomethylpyridine was anchored onto smectite surface by heterogeneous route. The ability of these materials to remove the Sumifix Brilliant Orange 3R textile dye from aqueous solution was followed by a series of adsorption isotherms, using a batchwise process. The maximum number of moles adsorbed was determined to be 1.26 and 2.07 mmol g(-1) for natural and modified clay samples, respectively. The energetic effects caused by dye cations adsorption were determined through calorimetric titrations. Thermodynamics indicated the existence of favorable conditions for such dye-nitrogen interactions. Copyright © 2010. Published by Elsevier B.V.

[Adsorption mechanism of furfural onto modified rice husk charcoals].

PubMed

Deng, Yong; Wang, Xianhua; Li, Yunchao; Shao, Jing'ai; Yang, Haiping; Chen, Hanping

2015-10-01

To evaluate the absorptive characteristics of furfural onto biomass charcoals derived from rice husk pyrolysis, we studied the information of the structure and surface chemistry properties of the rice husk charcoals modified by thermal treatment under nitrogen and carbon dioxide flow and adsorption mechanism of furfural. The modified samples are labeled as RH-N2 and RH-CO2. Fresh rice husk charcoal sample (RH-450) and modified samples were characterized by elemental analysis, nitrogen adsorption-desorption isotherms, Fourier-transform infrared spectroscopy and Boehm titration. The results show that fresh rice husk charcoal obtained at 450 degrees C had a large number of organic groups on its surface and poor pore structure. After the modification under nitrogen and carbon dioxide flow, oxygenic organics in rice husk charcoals decompose further, leading to the reduction of acidic functional groups on charcoals surface, and the increase of the pyrone structures of the basic groups. Meanwhile, pore structure was improved significantly and the surface area was increased, especially for the micropores. This resulted in the increase of π-π dispersion between the surfaces of rice husk charcoals and furfural molecular. With making comprehensive consideration of π-π dispersion and pore structure, the best removal efficiency of furfural was obtained by rice husk charcoal modified under carbon dioxide flow.

Superparamagnetic iron oxide coated on the surface of cellulose nanospheres for the rapid removal of textile dye under mild condition

NASA Astrophysics Data System (ADS)

Qin, Yunfeng; Qin, Zongyi; Liu, Yannan; Cheng, Miao; Qian, Pengfei; Wang, Qian; Zhu, Meifang

2015-12-01

Magnetic composite nanoparticles (MNPs) were prepared by anchoring iron oxide (Fe3O4) on the surface of carboxyl cellulose nanospheres through a facile chemical co-precipitation method. The as-prepared MNPs were characterized by atomic force microscopy, transmission electron microscopy, Fourier transform infrared spectroscopy, wide-angle X-ray diffraction measurement, thermal gravity analysis and vibrating sample magnetometry. These MNPs were of a generally spherical shape with a narrow size distribution, and exhibited superparamagnetic behaviors with high saturation magnetization. High efficient removal of Navy blue in aqueous solution was demonstrated at room temperature in a Fenton-like system containing the MNPs and H2O2, which benefited from small particle size, large surface area, high chemical activity, and good dispersibility of the MNPs. The removal efficiency of Navy blue induced by the MNPs prepared at a weight ratio of cellulose to iron of 1:2 were 90.6% at the first minute of the degradation reaction, and 98.0% for 5 min. Furthermore, these MNPs could be efficiently recycled and reused by using an external magnetic field. The approach presented in this paper promotes the use of renewable natural resources as templates for the preparation and stabilization of various inorganic nanomaterials for the purpose of catalysis, magnetic resonance imaging, biomedical and other potential applications.

Improving material removal determinacy based on the compensation of tool influence function

NASA Astrophysics Data System (ADS)

Zhong, Bo; Chen, Xian-hua; Deng, Wen-hui; Zhao, Shi-jie; Zheng, Nan

2018-03-01

In the process of computer-controlled optical surfacing (CCOS), the key of correcting the surface error of optical components is to ensure the consistency between the simulated tool influence function and the actual tool influence function (TIF). The existing removal model usually adopts the fixed-point TIF to remove the material with the planning path and velocity, and it considers that the polishing process is linear and time invariant. However, in the actual polishing process, the TIF is a function related to the feed speed. In this paper, the relationship between the actual TIF and the feed speed (i.e. the compensation relationship between static removal and dynamic removal) is determined by experimental method. Then, the existing removal model is modified based on the compensation relationship, to improve the conformity between simulated and actual processing. Finally, the surface error modification correction test are carried out. The results show that the fitting degree of the simulated surface and the experimental surface is better than 88%, and the surface correction accuracy can be better than 1/10 λ (Λ=632.8nm).

Design of equipment for lunar dust removal

NASA Technical Reports Server (NTRS)

Belden, Lacy; Cowan, Kevin; Kleespies, Hank; Ratliff, Ryan; Shah, Oniell; Shelburne, Kevin

1991-01-01

NASA has a long range goal of constructing a fully equipped, manned lunar base on the near side of the moon by the year 2015. During the Apollo Missions, lunar dust coated and fouled equipment surfaces and mechanisms exposed to the lunar environment. In addition, the atmosphere and internal surfaces of the lunar excursion module were contaminated by lunar dust which was brought in on articles passed through the airlock. Consequently, the need exists for device or appliance to remove lunar dust from surfaces of material objects used outside of the proposed lunar habitat. Additionally, several concepts were investigated for preventing the accumulation of lunar dust on mechanisms and finished surfaces. The character of the dust and the lunar environment present unique challenges for the removal of contamination from exposed surfaces. In addition to a study of lunar dust adhesion properties, the project examines the use of various energy domains for removing the dust from exposed surfaces. Also, prevention alternatives are examined for systems exposed to lunar dust. A concept utilizing a pressurized gas is presented for dust removal outside of an atmospherically controlled environment. The concept consists of a small astronaut/robotic compatible device which removes dust from contaminated surfaces by a small burst of gas.

Human health impacts of drinking water (surface and ground) pollution Dakahlyia Governorate, Egypt

NASA Astrophysics Data System (ADS)

Mandour, R. A.

2012-09-01

This study was done on 30 drinking tap water samples (surface and ground) and 30 urine samples taken from patients who attended some of Dakahlyia governorate hospitals. These patients were complaining of poor-quality tap water in their houses, which was confirmed by this study that drinking water is contaminated with trace elements in some of the studied areas. The aim of this study was to determine the relationship between the contaminant drinking water (surface and ground) in Dakahlyia governorate and its impact on human health. This study reports the relationship between nickel and hair loss, obviously shown in water and urine samples. Renal failure cases were related to lead and cadmium contaminated drinking water, where compatibilities in results of water and urine samples were observed. Also, liver cirrhosis cases were related to iron-contaminated drinking water. Studies of these diseases suggest that abnormal incidence in specific areas is related to industrial wastes and agricultural activities that have released hazardous and toxic materials in the drinking water and thereby led to its contamination in these areas. We conclude that trace elements should be removed from drinking water for human safety.

Regolith Volatile Recovery at Simulated Lunar Environments

NASA Technical Reports Server (NTRS)

Kleinhenz, Julie; Paulsen, Gale; Zacny, Kris; Schmidt, Sherry; Boucher, Dale

2016-01-01

Lunar Polar Volatiles: Permanently shadowed craters at the lunar poles contain water, 5 wt according to LCROSS. Interest in water for ISRU applications. Desire to ground truth water using surface prospecting e.g. Resource Prospector and RESOLVE. How to access subsurface water resources and accurately measure quantity. Excavation operations and exposure to lunar environment may affect the results. Volatile capture tests: A series a ground based dirty thermal vacuum tests are being conducted to better understand the subsurface sampling operations. Sample removal and transfer. Volatiles loss during sampling operations. Concept of operations, Instrumentation. This presentation is a progress report on volatiles capture results from these tests with lunar polar drill prototype hardware.

Grinding model and material removal mechanism of medical nanometer zirconia ceramics.

PubMed

Zhang, Dongkun; Li, Changhe; Jia, Dongzhou; Wang, Sheng; Li, Runze; Qi, Xiaoxiao

2014-01-01

Many patents have been devoted to developing medical nanometer zirconia ceramic grinding techniques that can significantly improve both workpiece surface integrity and grinding quality. Among these patents is a process for preparing ceramic dental implants with a surface for improving osseo-integration by sand abrasive finishing under a jet pressure of 1.5 bar to 8.0 bar and with a grain size of 30 µm to 250 µm. Compared with other materials, nano-zirconia ceramics exhibit unmatched biomedical performance and excellent mechanical properties as medical bone tissue and dentures. The removal mechanism of nano-zirconia materials includes brittle fracture and plastic removal. Brittle fracture involves crack formation, extension, peeling, and chipping to completely remove debris. Plastic removal is similar to chip formation in metal grinding, including rubbing, ploughing, and the formation of grinding debris. The materials are removed in shearing and chipping. During brittle fracture, the grinding-led transverse and radial extension of cracks further generate local peeling of blocks of the material. In material peeling and removal, the mechanical strength and surface quality of the workpiece are also greatly reduced because of crack extension. When grinding occurs in the plastic region, plastic removal is performed, and surface grinding does not generate grinding fissures and surface fracture, producing clinically satisfactory grinding quality. With certain grinding conditions, medical nanometer zirconia ceramics can be removed through plastic flow in ductile regime. In this study, we analyzed the critical conditions for the transfer of brittle and plastic removal in nano-zirconia ceramic grinding as well as the high-quality surface grinding of medical nanometer zirconia ceramics by ELID grinding.

Application of chitosan/polyacrylamide nanofibres for removal of chromate and phosphate in water

NASA Astrophysics Data System (ADS)

Nthumbi, Richard M.; Catherine Ngila, J.; Moodley, Brenda; Kindness, Andrew; Petrik, Leslie

Water pollution is an intractable environmental problem in South Africa. Management of the water resource is vital in order to address the water scarcity issues. Research on remediation of contaminated water has focused mainly on the removal of heavy metals such as Pb, Cd, Zn, Hg and Cu and neglected other inorganic pollutants. In this work we focus on the removal of anions, namely chromate and phosphate. Chromium is extensively used in the textile, leather and metallurgy industries and contaminates surface water and groundwater when inadequately treated industrial effluents are discharged. Chromium has been associated with irregular sugar metabolism, nosebleeds and ulcers, and it is also carcinogenic. The phosphate ion is an essential micronutrient responsible for healthy plant growth. However, excess phosphate intake stimulates rapid growth of photosynthetic algae and cyanobacteria, resulting in eutrophication. This phenomenon (algal bloom) causes other organisms to die due to reduced oxygen in the water. In order to offer remediation measures, this study reports the use of electrospun nanofibres for the removal of chromate and phosphate anions. Adsorption experiments were carried out using nanofibres electrospun from chitosan and polyacrylamide polymer blends, cross-linked with glutaraldehyde. Quantification of chromium was done using ICP-OES while UV-Vis spectrophotometry was used for the determination of phosphates. Batch adsorption experiments were done to determine optimum adsorption parameters such as pH, contact time, temperature and initial analyte concentration. Removal of the ions using a flow-adsorption technique through a micro-column was performed. The experimental data obtained were analysed using Langmuir and Freundlich models to study the adsorption mechanisms. The nanofibres had an adsorption capacity for Cr(VI) and PO43- of 0.26 mg g-1 and 392 mg g-1, respectively, and removal efficiencies of 93% and 97.4%, in the same order, in synthetic water samples and environmental water samples. It was observed that both chromium(VI) and phosphate adsorption followed pseudo-second-order kinetics. During the regeneration process, it was established that Cr(VI) was reduced to Cr(III) at the surface of the sorbent. This reaction offers the advantage of reducing the toxicity of chromium(VI) in water. The results of this work have potential applications in the removal of these anions in contaminated drinking water thus improving its quality for human consumption.

Modification of the surface properties of glass-ceramic materials at low-pressure RF plasma stream

NASA Astrophysics Data System (ADS)

Tovstopyat, Alexander; Gafarov, Ildar; Galeev, Vadim; Azarova, Valentina; Golyaeva, Anastasia

2018-05-01

The surface roughness has a huge effect on the mechanical, optical, and electronic properties of materials. In modern optical systems, the specifications for the surface accuracy and smoothness of substrates are becoming even more stringent. Commercially available pre-polished glass-ceramic substrates were treated with the radio frequency (RF) inductively coupled (13.56 MHz) low-pressure plasma to clean the surface of the samples and decrease the roughness. Optical emission spectroscopy was used to investigate the plasma stream parameters and phase-shifted interferometry to investigate the surface of the specimen. In this work, the dependence of RF inductively coupled plasma on macroscopic parameters was investigated with the focus on improving the surfaces. The ion energy, sputtering rate, and homogeneity were investigated. The improvements of the glass-ceramic surfaces from 2.6 to 2.2 Å root mean square by removing the "waste" after the previous operations had been achieved.

Direct measurement of surface carbon concentrations. [in lunar soil

NASA Technical Reports Server (NTRS)

Filleux, C.; Tombrello, T. A.; Burnett, D. S.

1977-01-01

Measurements of surface concentrations of carbon in lunar soils and soil breccias provide information on the origin of carbon in the regolith. The reaction C-12 (d, p sub zero) is used to measure 'surface' and 'volume' concentrations in lunar samples. This method has a depth resolution of 1 micron, which permits only a 'surface' and a 'volume' component to be measured. Three of four Apollo 16 double drive tube samples show a surface carbon concentration of about 8 by 10 to the 14th power/sq cm, whereas the fourth sample gave 4 by 10 to the 14th power/sq cm. It can be convincingly shown that the measured concentration does not originate from fluorocarbon or hydrocarbon contaminants. Surface adsorbed layers of CO or CO2 are removed by a sputter cleaning procedure using a 2-MeV F beam. It is shown that the residual C concentration of 8 by 10 to the 14th power/sq cm cannot be further reduced by increased F fluence, and it is therefore concluded that it is truly lunar. If one assumes that the measured surface C concentration is a steady-state concentration determined only by a balance between solar-wind implantation and sputtering, a sputter erosion rate of 0.1 A/yr is obtained. However, it would be more profitable to use an independently derived sputter erosion rate to test the hypothesis of a solar-wind origin of the surface carbon.

Surface decontamination compositions and methods

DOEpatents

Wright,; Karen, E [Idaho Falls, ID; Cooper, David C [Idaho Falls, ID; Peterman, Dean R [Idaho Falls, ID; Demmer, Ricky L [Idaho Falls, ID; Tripp, Julia L [Pocatello, ID; Hull, Laurence C [Idaho Falls, ID

2011-03-29

Clay-based compositions capable of absorbing contaminants from surfaces or objects having surface faces may be applied to a surface and later removed, the removed clay-based compositions absorbing at least a portion of the contaminant from the surface or object to which it was applied.

Photovoltaic cell and production thereof

DOEpatents

Narayanan, Srinivasamohan [Gaithersburg, MD; Kumar, Bikash [Bangalore, IN

2008-07-22

An efficient photovoltaic cell, and its process of manufacture, is disclosed wherein the back surface p-n junction is removed from a doped substrate having an oppositely doped emitter layer. A front surface and edges and optionally the back surface periphery are masked and a back surface etch is performed. The mask is not removed and acts as an anti-reflective coating, a passivating agent, or both. The photovoltaic cell retains an untextured back surface whether or not the front is textured and the dopant layer on the back surface is removed to enhance the cell efficiency. Optionally, a back surface field is formed.

Engineering Surfaces for Enhanced Nucleation and Droplet Removal During Dropwise Condensation

NASA Astrophysics Data System (ADS)

Dutta, Sanmitra; Khan, Sameera; Anand, Sushant

2017-11-01

Condensation plays critical role in numerous industrial applications, such as condensers, HVAC,etc In the most applications, fast formation (i.e. high nucleation) and subsequent removal of water droplets is critical for enhancing the efficiencies of their associated systems. Significant focus has been placed on the aspect of droplet removal from surfaces. This has led to, development of superhydrophobic surfaces with special textures on which droplets are self-removed after coalescence. However,because of their inherent low surface energy, nucleation energy barriers are also high on such surfaces. In contrast to conventional superhydrophobic surfaces, here we show that surfaces can be engineered such that the simultaneous benefits of high nucleation rates and fast droplet removal can be obtained during the condensation process.These benefits are obtained by impregnating a superhydrophobic surface with an oil that despite its defect-free interface provides low nucleation energy barrier during condensation. At the same time, the oil facilitates high droplet shedding rates by providing a lubricating layer below the droplets due to which droplets have negligible contact angle hysteresis. We provide a guide to choose oils that lead to enhanced nucleation, and provide experimental evidence supporting the proposed guide. We discuss the importance of different oil properties in affecting the droplet growth and subsequent removal of water droplets.

Dwell Time and Surface Parameter Effects on Removal of Silicone Oil From D6ac Steel Using TCA

NASA Technical Reports Server (NTRS)

Boothe, R. E.

2003-01-01

This study was conducted to evaluate the impact of dwell time, surface roughness, and the surface activation state on 1,1,1-trichloroethane's (TCA's) effectiveness for removing silicone oil from D6ac steel. Silicone-contaminated test articles were washed with TCA solvent, and then the surfaces were analyzed for residue, using Fourier transform infrared spectroscopy. The predominant factor affecting the ability to remove the silicone oil was surface roughness.

An overland flow sampler for use in vegetative filters

Treesearch

D. Eisenhauer; M. Helmers; J. Brothers; M. Dosskey; T. Franti; A. Boldt; B. Strahm

2002-01-01

Vegetative filters (VF) are used to remove contaminants from agricultural runoff and improve surface water quality. Techniques are needed to quantify the performance of VF in realistic field settings. The goal of this project was to develop and test a relatively simple and low cost method for sampling overland flow in a VF. The 0.3 m wide sampler has the capacity to...

Cleaning of titanium substrates after application in a bioreactor.

PubMed

Fingerle, Mathias; Köhler, Oliver; Rösch, Christina; Kratz, Fabian; Scheibe, Christian; Davoudi, Neda; Müller-Renno, Christine; Ziegler, Christiane; Huster, Manuel; Schlegel, Christin; Ulber, Roland; Bohley, Martin; Aurich, Jan C

2015-03-10

Plain and microstructured cp-titanium samples were studied as possible biofilm reactor substrates. The biofilms were grown by exposition of the titanium samples to bacteria in a flow cell. As bacteria the rod shaped gram negative Pseudomonas fluorescens and the spherical gram negative Paracoccus seriniphilus were chosen. Afterward, the samples were cleaned in subsequent steps: First, with a standard solvent based cleaning procedure with acetone, isopropanol, and ultrapure water and second by oxygen plasma sputtering. It will be demonstrated by means of x-ray photoelectron spectroscopy, fluorescence microscopy, and confocal laser scanning microscopy that oxygen plasma cleaning is a necessary and reliant tool to fully clean and restore titanium surfaces contaminated with a biofilm. The microstructured surfaces act beneficial to biofilm growth, while still being fully restorable after biofilm contamination. Scanning electron microscopy images additionally show, that the plasma process does not affect the microstructures. The presented data show the importance of the cleaning procedure. Just using solvents does not remove the biofilm and all its components reliably while a cleaning process by oxygen plasma regenerates the surfaces.

The potential use of rainwater as alternative source of drinking water by using laterite soil as natural adsorbent

NASA Astrophysics Data System (ADS)

Omar, Khairunnisa Fakhriah Mohd; Palaniandy, Puganeshwary; Adlan, Mohd Nordin; Aziz, Hamidi Abdul; Subramaniam, Ambarasi

2017-10-01

Generally, the rainwater has low concentration of pollutants, whereby it is applicable for domestic water supply. Due to the low concentration of pollutants, further treatment such as adsorption is necessary to treat the harvested rainwater as an alternative source of drinking water supply. Therefore, this research has been carried out to determine the quality of rainwater from different types of locations, which are; rural residential area, urban residential area, agricultural area, industrial area, and open surface. The rainwater sampling was carried out from September 2014 to December 2015. The parameters that have been analysed during the sampling process are chemical oxygen demand (COD), turbidity, heavy metals, and Escherichia coli (E.coli). The sampling results show that the rainwater provides low concentration of contaminants. Thus, it has high potential to be used as alternative source of potable and non potable water supply with a suitable treatment. Due to that, an experimental work contained of 86 of designated experiments for a batch study has been carried out to determine the performance of laterite soil as an adsorbent to remove pollutants that present in the rainwater (i.e. zinc, manganese, and E.coli). The operating factors involved in the experimental works are pH, mass of adsorbents, contact time, initial concentration of zinc, manganese, and E.coli. In this study, the experimental data of the batch study was analysed by developing regression model equation and analysis of variance. Perturbation plots were analysed to determine the effectiveness of the operating factors by developing response surface model, resulting that the high removals of zinc, manganese, and E.coli are 95.8%, 94.05% and 100%, respectively. Overall, this research works found out that the rainwater has a good quality as alternative source of drinking water by providing a suitable treatment. The application of laterite soil as natural adsorbent shows that it has potential to be used as the response surface model provide a good removal for zinc, manganese, and E.coli.

Atomic Oxygen Treatment as a Method of Recovering Smoke Damaged Paintings. Revised

NASA Technical Reports Server (NTRS)

Rutledge, Sharon K.; Banks, Bruce A.; Forkapa, Mark; Stueber, Thomas; Sechkar, Edward; Malinowski, Kevin

1999-01-01

A noncontact technique is described that uses atomic oxygen, generated under low pressure in the presence of nitrogen, to remove soot and charred varnish from the surface of a painting. The process, which involves surface oxidation, permits control of the amount of surface material removed. The effectiveness of the process was evaluated by reflectance measurements from selected areas made during the removal of soot from acrylic gesso, ink on paper, and varnished oil paint substrates. For the latter substrate, treatment also involved the removal of damaged varnish and paint binder from the surface.

Near-ultraviolet removal rates for subgingival dental calculus at different irradiation angles.

PubMed

Schoenly, Joshua E; Seka, Wolf D; Rechmann, Peter

2011-07-01

The laser ablation rate of subgingival dental calculus irradiated at a 400-nm-wavelength, 7.4-mJ pulse energy, and 85- and 20-deg irradiation angles is measured using laser triangulation. Three-dimensional images taken before and after irradiation create a removal map with 6-μm axial resolution. Fifteen human teeth with subgingival calculus are irradiated in vitro under a cooling water spray with an ∼300-μm-diam, tenth-order super-gaussian beam. The average subgingival calculus removal rates for irradiation at 85 and 20 deg are 11.1±3.6 and 11.5±5.9 μm∕pulse, respectively, for depth removal and 4.5±1.7×10(5) and 4.8±2.3×10(5) μm(3)∕pulse, respectively, for volume removal. The ablation rate is constant at each irradiation site but varies between sites because of the large differences in the physical and optical properties of calculus. Comparison of the average depth- and volume-removal rates does not reveal any dependence on the irradiation angle and is likely due to the surface topology of subgingival calculus samples that overshadows any expected angular dependence.

Near-ultraviolet removal rates for subgingival dental calculus at different irradiation angles

NASA Astrophysics Data System (ADS)

Schoenly, Joshua E.; Seka, Wolf D.; Rechmann, Peter

2011-07-01

The laser ablation rate of subgingival dental calculus irradiated at a 400-nm-wavelength, 7.4-mJ pulse energy, and 85- and 20-deg irradiation angles is measured using laser triangulation. Three-dimensional images taken before and after irradiation create a removal map with 6-μm axial resolution. Fifteen human teeth with subgingival calculus are irradiated in vitro under a cooling water spray with an ~300-μm-diam, tenth-order super-Gaussian beam. The average subgingival calculus removal rates for irradiation at 85 and 20 deg are 11.1+/-3.6 and 11.5+/-5.9 μm/pulse, respectively, for depth removal and 4.5+/-1.7×105 and 4.8+/-2.3×105 μm3/pulse, respectively, for volume removal. The ablation rate is constant at each irradiation site but varies between sites because of the large differences in the physical and optical properties of calculus. Comparison of the average depth- and volume-removal rates does not reveal any dependence on the irradiation angle and is likely due to the surface topology of subgingival calculus samples that overshadows any expected angular dependence.

Isolating the effects of surface vasculature in infant neuroimaging using short-distance optical channels: a combination of local and global effects

PubMed Central

Emberson, Lauren L.; Crosswhite, Stephen L.; Goodwin, James R.; Berger, Andrew J.; Aslin, Richard N.

2016-01-01

Abstract. Functional near-infrared spectroscopy (fNIRS) records hemodynamic changes in the cortex arising from neurovascular coupling. However, (noninvasive) fNIRS recordings also record surface vascular signals arising from noncortical sources (e.g., in the skull, skin, dura, and other tissues located between the sensors and the brain). A current and important focus in the fNIRS community is determining how to remove these noncortical vascular signals to reduce noise and to prevent researchers from erroneously attributing responses to cortical sources. The current study is the first to test a popular method for removing signals from the surface vasculature (removing short, 1 cm, channel recordings from long, 3 cm, channel recordings) in human infants, a population frequently studied using fNIRS. We find evidence that this method does remove surface vasculature signals and indicates the presence of both local and global surface vasculature signals. However, we do not find that the removal of this information changes the statistical inferences drawn from the data. This latter result not only questions the importance of removing surface vasculature responses for empiricists employing this method, but also calls for future research using other tasks (e.g., ones with a weaker initial result) with this population and possibly additional methods for removing signals arising from the surface vasculature in infants. PMID:27158631

High-accuracy process based on the corrective calibration of removal function in the magnetorheological finishing

NASA Astrophysics Data System (ADS)

Zhong, Xianyun; Fan, Bin; Wu, Fan

2017-08-01

The corrective calibration of the removal function plays an important role in the magnetorheological finishing (MRF) high-accuracy process. This paper mainly investigates the asymmetrical characteristic of the MRF removal function shape and further analyzes its influence on the surface residual error by means of an iteration algorithm and simulations. By comparing the ripple errors and convergence ratios based on the ideal MRF tool function and the deflected tool function, the mathematical models for calibrating the deviation of horizontal and flowing directions are presented. Meanwhile, revised mathematical models for the coordinate transformation of an MRF machine is also established. Furthermore, a Ø140-mm fused silica plane and a Ø196 mm, f/1∶1, fused silica concave sphere samples are taken as the experiments. After two runs, the plane mirror final surface error reaches PV 17.7 nm, RMS 1.75 nm, and the polishing time is 16 min in total; after three runs, the sphere mirror final surfer error reaches RMS 2.7 nm and the polishing time is 70 min in total. The convergence ratios are 96.2% and 93.5%, respectively. The spherical simulation error and the polishing result are almost consistent, which fully validate the efficiency and feasibility of the calibration method of MRF removal function error using for the high-accuracy subaperture optical manufacturing.

Preparation and Cr(VI) removal performance of corncob activated carbon.

PubMed

Li, Hongyan; Gao, Pei; Cui, Jianguo; Zhang, Feng; Wang, Fang; Cheng, Jici

2018-05-12

Corncob activated carbon (CCAC) was prepared by a H 3 PO 4 activation method. The optimum conditions for the preparation of CCAC were determined by orthogonal experiments. The effects of pH, reaction time, CCAC dosage, and hexavalent chromium (Cr(VI)) concentrations on Cr(VI) removal by CCAC were studied. Corn straw activated carbon (CSAC) was also prepared using the optimum preparation conditions determined for CCAC. The properties of samples were characterized by Fourier transform infrared spectroscopy (FTIR), X-ray diffraction (XRD), Brunauer-Emmett-Teller (BET) analysis, scanning electron microscopy (SEM), and energy dispersive spectroscopy (EDS). The results showed that the optimum preparation conditions for CCAC were as follows: a mass of corncob of 10 g; a mass ratio of corncob to H 3 PO 4 of 1:2; a 5% H 3 BO 3 content of 10 mL; an impregnation time of 45 min; a carbonization temperature of 500 °C. The optimum conditions for the removal of Cr(VI) were as follows: pH < 9; temperature, 308 K; rotation speed, 150 r min -1 ; reaction time, 60 min; CCAC dosage, 1 g L -1 . The Cr(VI) removal rate was above 98%, and the maximum adsorption capacity of CCAC was 9.985 mg g -1 . The concentration of residual Cr(VI) in water was less than 0.05 mg L -1 . FTIR showed that the surfaces of the samples had more oxygen-containing functional groups, which promoted the adsorption. XRD showed that CCAC and CSAC had similar peaks and that these peaks promoted the adsorption of Cr(VI). BET indicated that the number of pores in the samples followed the order CCAC > CSAC > CAC. SEM showed that the CCAC surface had a more porous structure, which enhanced adsorption. EDS showed that the C contents of CCAC and CSAC were much higher than that of CAC. Cr(VI) adsorption on CCAC followed quasi-second-order kinetics and was in accordance with a Langmuir adsorption isotherm, with monolayer adsorption. The adsorption reaction was endothermic, where higher temperatures increased the degree of spontaneous reaction.

Surface modification to waveguides

DOEpatents

Timberlake, John R.; Ruzic, David N.; Moore, Richard L.; Cohen, Samuel A.; Manos, Dennis M.

1983-01-01

A method of treating the interior surfaces of a waveguide to improve power transmission comprising the steps of mechanically polishing to remove surface protrusions; electropolishing to remove embedded particles; ultrasonically cleaning to remove any residue; coating the interior waveguide surfaces with an alkyd resin solution or electrophoretically depositing carbon lamp black suspended in an alkyd resin solution to form a 1.mu. to 5.mu. thick film; vacuum pyrolyzing the film to form a uniform adherent carbon coating.

Approximal sealings on lesions in neighbouring teeth requiring operative treatment: an in vitro study.

PubMed

Cartagena, Alvaro; Bakhshandeh, Azam; Ekstrand, Kim Rud

2018-02-07

With this in vitro study we aimed to assess the possibility of precise application of sealant on accessible artificial white spot lesions (WSL) on approximal surfaces next to a tooth surface under operative treatment. A secondary aim was to evaluate whether the use of magnifying glasses improved the application precision. Fifty-six extracted premolars were selected, approximal WSL lesions were created with 15% HCl gel and standardized photographs were taken. The premolars were mounted in plaster-models in contact with a neighbouring molar with Class II/I-II restoration (Sample 1) or approximal, cavitated dentin lesion (Sample 2). The restorations or the lesion were removed, and Clinpro Sealant was placed over the WSL. Magnifying glasses were used when sealing half the study material. The sealed premolar was removed from the plaster-model and photographed. Adobe Photoshop was used to measure the size of WSL and sealed area. The degree of match between the areas was determined in Photoshop. Interclass agreement for WSL, sealed, and matched areas were found as excellent (κ = 0.98-0.99). The sealant covered 48-100% of the WSL-area (median = 93%) in Sample 1 and 68-100% of the WSL-area (median = 95%) in Sample 2. No statistical differences were observed concerning uncovered proportions of the WSL-area between groups with and without using magnifying glasses (p values ≥ .19). However, overextended sealed areas were more pronounced when magnification was used (p = .01). The precision did not differ between the samples (p = .31). It was possible to seal accessible approximal lesions with high precision. Use of magnifying glasses did not improve the precision.

The occurrence of antibiotics in an urban watershed: from wastewater to drinking water.

PubMed

Watkinson, A J; Murby, E J; Kolpin, D W; Costanzo, S D

2009-04-01

The presence of 28 antibiotics in three hospital effluents, five wastewater treatment plants (WWTPs), six rivers and a drinking water storage catchment were investigated within watersheds of South-East Queensland, Australia. All antibiotics were detected at least once, with the exception of the polypeptide bacitracin which was not detected at all. Antibiotics were found in hospital effluent ranging from 0.01-14.5 microg L(-1), dominated by the beta-lactam, quinolone and sulphonamide groups. Antibiotics were found in WWTP influent up to 64 microg L(-1), dominated by the beta-lactam, quinolone and sulphonamide groups. Investigated WWTPs were highly effective in removing antibiotics from the water phase, with an average removal rate of greater than 80% for all targeted antibiotics. However, antibiotics were still detected in WWTP effluents in the low ng L(-1) range up to a maximum of 3.4 microg L(-1), with the macrolide, quinolone and sulphonamide antibiotics most prevalent. Similarly, antibiotics were detected quite frequently in the low ng L(-1) range, up to 2 microg L(-1) in the surface waters of six investigated rivers including freshwater, estuarine and marine samples. The total investigated antibiotic concentration (TIAC) within the Nerang River was significantly lower (p<0.05) than all other rivers sampled. The absence of WWTP discharge to this river is a likely explanation for the significantly lower TIAC and suggests that WWTP discharges are a dominant source of antibiotics to investigated surface waters. A significant difference (p<0.001) was identified between TIACs at surface water sites with WWTP discharge compared to sites with no WWTP discharge, providing further evidence that WWTPs are an important source of antibiotics to streams. Despite the presence of antibiotics in surface waters used for drinking water extraction, no targeted antibiotics were detected in any drinking water samples.

Contamination levels of human pharmaceutical compounds in French surface and drinking water.

PubMed

Mompelat, S; Thomas, O; Le Bot, B

2011-10-01

The occurrence of 20 human pharmaceutical compounds and metabolites from 10 representative therapeutic classes was analysed from resource and drinking water in two catchment basins located in north-west France. 98 samples were analysed from 63 stations (surface water and drinking water produced from surface water). Of the 20 human pharmaceutical compounds selected, 16 were quantified in both the surface water and drinking water, with 22% of the values above the limit of quantification for surface water and 14% for drinking water). Psychostimulants, non-steroidal anti-inflammatory drugs, iodinated contrast media and anxiolytic drugs were the main therapeutic classes of human pharmaceutical compounds detected in the surface water and drinking water. The results for surface water were close to results from previous studies in spite of differences in prescription rates of human pharmaceutical compounds in different countries. The removal rate of human pharmaceutical compounds at 11 water treatment units was also determined. Only caffeine proved to be resistant to drinking water treatment processes (with a minimum rate of 5%). Other human pharmaceutical compounds seemed to be removed more efficiently (average elimination rate of over 50%) by adsorption onto activated carbon and oxidation/disinfection with ozone or chlorine (not taking account of the disinfection by-products). These results add to the increasing evidence of the occurrence of human pharmaceutical compounds in drinking water that may represent a threat to human beings exposed to a cocktail of human pharmaceutical compounds and related metabolites and by-products in drinking water.

Spectroscopic characterization of Greek dolomitic marble surface interacted with uranium and thorium in aqueous solutions

NASA Astrophysics Data System (ADS)

Godelitsas, A.; Kokkoris, M.; Chatzitheodoridis, E.; Misaelides, P.

2008-05-01

The surface of a typical Greek (Thassian) dolomitic marble was studied after interaction with U- and Th-containing aqueous solutions (1000 mg/L, free-drift experiments for 1 week at atmospheric PCO2), using 12C-RBS and Laser μ-Raman spectroscopy. Powder-XRD and SEM-EDS were also applied to investigate the phases deposited on the surface of the interacted samples. The obtained results indicated a considerable removal of U from the aqueous medium mainly due to massive surface precipitation of amorphous UO2-hydroxide phases forming a relatively thick (μm-sized) coating on the carbonate substrate. The interaction of Th with dolomitic marble surface is also intense leading to a formation of an amorphous Th-hydroxide layer of similar thickness but of significantly lower elemental atomic proportion.

Laser vaporization of trace explosives for enhanced non-contact detection

NASA Astrophysics Data System (ADS)

Furstenberg, Robert; Papantonakis, Michael; Kendziora, Christopher A.; Bubb, Daniel M.; Corgan, Jeffrey; McGill, R. Andrew

2010-04-01

Trace explosives contamination is found primarily in the form of solid particulates on surfaces, due to the low vapor pressure of most explosives materials. Today, the standard sampling procedure involves physical removal of particulate matter from surfaces of interest. A variety of collection methods have been used including air-jetting or swabbing surfaces of interest. The sampled particles are typically heated to generate vapor for analysis in hand held, bench top, or portal detection systems. These sampling methods are time-consuming (and hence costly), require a skilled technician for optimal performance, and are inherently non-selective, allowing non-explosives particles to be co-sampled and analyzed. This can adversely affect the sensitivity and selectivity of detectors, especially those with a limited dynamic range. We present a new approach to sampling solid particles on a solid surface that is targeted, non-contact, and which selectively enhances trace explosive signatures thus improving the selectivity and sensitivity of existing detectors. Our method involves the illumination of a surface of interest with infrared laser light with a wavelength that matches a distinctive vibrational mode of an explosive. The resonant coupling of laser energy results in rapid heating of explosive particles and rapid release of a vapor plume. Neighboring particles unrelated to explosives are generally not directly heated as their vibrational modes are not resonant with the laser. As a result, the generated vapor plume includes a higher concentration of explosives than if the particles were heated with a non-selective light source (e.g. heat lamp). We present results with both benchtop infrared lasers as well as miniature quantum cascade lasers.

Friction Stir Processing of Stainless Steel for Ascertaining Its Superlative Performance in Bioimplant Applications.

PubMed

Perumal, G; Ayyagari, A; Chakrabarti, A; Kannan, D; Pati, S; Grewal, H S; Mukherjee, S; Singh, S; Arora, H S

2017-10-25

Substrate-cell interactions for a bioimplant are driven by substrate's surface characteristics. In addition, the performance of an implant and resistance to degradation are primarily governed by its surface properties. A bioimplant typically degrades by wear and corrosion in the physiological environment, resulting in metallosis. Surface engineering strategies for limiting degradation of implants and enhancing their performance may reduce or eliminate the need for implant removal surgeries and the associated cost. In the current study, we tailored the surface properties of stainless steel using submerged friction stir processing (FSP), a severe plastic deformation technique. FSP resulted in significant microstructural refinement from 22 μm grain size for the as-received alloy to 0.8 μm grain size for the processed sample with increase in hardness by nearly 1.5 times. The wear and corrosion behavior of the processed alloy was evaluated in simulated body fluid. The processed sample demonstrated remarkable improvement in both wear and corrosion resistance, which is explained by surface strengthening and formation of a highly stable passive layer. The methylthiazol tetrazolium assay demonstrated that the processed sample is better in supporting cell attachment, proliferation with minimal toxicity, and hemolysis. The athrombogenic characteristic of the as-received and processed samples was evaluated by fibrinogen adsorption and platelet adhesion via the enzyme-linked immunosorbent assay and lactate dehydrogenase assay, respectively. The processed sample showed less platelet and fibrinogen adhesion compared with the as-received alloy, signifying its high thromboresistance. The current study suggests friction stir processing to be a versatile toolbox for enhancing the performance and reliability of currently used bioimplant materials.

Surface and subsurface cracks characteristics of single crystal SiC wafer in surface machining

NASA Astrophysics Data System (ADS)

Qiusheng, Y.; Senkai, C.; Jisheng, P.

2015-03-01

Different machining processes were used in the single crystal SiC wafer machining. SEM was used to observe the surface morphology and a cross-sectional cleavages microscopy method was used for subsurface cracks detection. Surface and subsurface cracks characteristics of single crystal SiC wafer in abrasive machining were analysed. The results show that the surface and subsurface cracks system of single crystal SiC wafer in abrasive machining including radial crack, lateral crack and the median crack. In lapping process, material removal is dominated by brittle removal. Lots of chipping pits were found on the lapping surface. With the particle size becomes smaller, the surface roughness and subsurface crack depth decreases. When the particle size was changed to 1.5µm, the surface roughness Ra was reduced to 24.0nm and the maximum subsurface crack was 1.2µm. The efficiency of grinding is higher than lapping. Plastic removal can be achieved by changing the process parameters. Material removal was mostly in brittle fracture when grinding with 325# diamond wheel. Plow scratches and chipping pits were found on the ground surface. The surface roughness Ra was 17.7nm and maximum subsurface crack depth was 5.8 µm. When grinding with 8000# diamond wheel, the material removal was in plastic flow. Plastic scratches were found on the surface. A smooth surface of roughness Ra 2.5nm without any subsurface cracks was obtained. Atomic scale removal was possible in cluster magnetorheological finishing with diamond abrasive size of 0.5 µm. A super smooth surface eventually obtained with a roughness of Ra 0.4nm without any subsurface crack.

Effectiveness of Commercial and Homemade Washing Agents in Removing Pesticide Residues on and in Apples.

PubMed

Yang, Tianxi; Doherty, Jeffery; Zhao, Bin; Kinchla, Amanda J; Clark, John M; He, Lili

2017-11-08

Removal of pesticide residues from fresh produce is important to reduce pesticide exposure to humans. This study investigated the effectiveness of commercial and homemade washing agents in the removal of surface and internalized pesticide residues from apples. Surface-enhanced Raman scattering (SERS) mapping and liquid chromatography tandem mass spectrometry (LC-MS/MS) methods were used to determine the effectiveness of different washing agents in removing pesticide residues. Surface pesticide residues were most effectively removed by sodium bicarbonate (baking soda, NaHCO 3 ) solution when compared to either tap water or Clorox bleach. Using a 10 mg/mL NaHCO 3 washing solution, it took 12 and 15 min to completely remove thiabendazole or phosmet surface residues, respectively, following a 24 h exposure to these pesticides, which were applied at a concentration of 125 ng/cm 2 . LC-MS/MS results showed, however, that 20% of applied thiabendazole and 4.4% of applied phosmet had penetrated into the apples following the 24 h exposure. Thiabendazole, a systemic pesticide, penetrated 4-fold deeper into the apple peel than did phosmet, a non-systemic pesticide, which led to more thiabendazole residues inside the apples, which could not be washed away using the NaHCO 3 washing solution. This study gives us the information that the standard postharvest washing method using Clorox bleach solution for 2 min is not an effective means to completely remove pesticide residues on the surface of apples. The NaHCO 3 method is more effective in removing surface pesticide residues on apples. In the presence of NaHCO 3 , thiabendazole and phosmet can degrade, which assists the physical removal force of washing. However, the NaHCO 3 method was not completely effective in removing residues that have penetrated into the apple peel. The overall effectiveness of the method to remove all pesticide residues diminished as pesticides penetrated deeper into the fruit. In practical application, washing apples with NaHCO 3 solution can reduce pesticides mostly from the surface. Peeling is more effective to remove the penetrated pesticides; however, bioactive compounds in the peels will become lost too.

Chemical Patterning by Mechanical Removal of Aqueous Polymers

NASA Astrophysics Data System (ADS)

Barnett, Katherine; Knoebel, Jodi; Davis, Robert C.

2006-10-01

We are developing a new method for micro and nanoscale patterning of lipids and proteins on solid surfaces. A layer of polyethylene glycol (PEG) teminated polyallyl amine (PAA) was initially applied to a mica surface. The PEG surface is a low adhesion surface for proteins. Following polymer deposition an Atomic Force Microscope (AFM) tip was used to remove the polymer layer in desired regions. AFM imaging of the surface after mechanical polymer removal shows squares of exposed MICA surrounded by the PEG surface. The clean mica regions are now available for specific adsorption of lipid or protein layers.

A new methodology for assessment of pectus excavatum correction after bar removal in Nuss procedure: Preliminary study.

PubMed

Gomes-Fonseca, João; Vilaça, João L; Henriques-Coelho, Tiago; Direito-Santos, Bruno; Pinho, António C M; Fonseca, Jaime C; Correia-Pinto, Jorge

2017-07-01

The objective is to present a new methodology to assess quantitatively the impact of bar removal on the anterior chest wall, among patients with pectus excavatum who have undergone the Nuss procedure, and present a preliminary study using this methodology. We propose to acquire, for each patient, the surface of the anterior chest wall using a three-dimensional laser scanner at subsequent time points (short term: before and after surgery; long term: follow-up visit, 6months, and 12months after surgery). After surfaces postprocessing, the changes are assessed by overlapping and measuring the distances between surfaces. In this preliminary study, three time points were acquired and two assessments were performed: before vs after bar removal (early) and before vs 2-8weeks after bar removal (interim). In 21 patients, the signed distances and volumes between surfaces were computed and the data analysis was performed. This methodology revealed useful for monitoring changes in the anterior chest wall. On average, the mean, maximum, and volume variations, in the early assessment, were -0.1±0.1cm, -0.6±0.2cm, and 47.8±22.2cm 3 , respectively; and, in the interim assessment, were -0.5±0.2cm, -1.3±0.4cm, and 122.1±47.3cm 3 , respectively (p<0.05). Data analysis revealed that the time the bar was in situ was inversely and significantly correlated with postretraction and was a relevant predictor of its decrease following surgery (p<0.05). Additionally, gender and age suggested influencing the outcome. This methodology is novel, objective and safe, helping on follow-up of pectus excavatum patients. Moreover, the preliminary study suggests that the time the bar was in situ may be the main determinant of the anterior chest wall retraction following bar removal. Further studies should continue to corroborate and reinforce the preliminary findings, by increasing the sample size and performing long-term assessments. III. Copyright © 2017 Elsevier Inc. All rights reserved.

The effect of vegetation and soil texture on the nature of organics in runoff from a catchment supplying water for domestic consumption.

PubMed

Awad, John; van Leeuwen, John; Abate, Dawit; Pichler, Markus; Bestland, Erick; Chittleborough, David J; Fleming, Nigel; Cohen, Jonathan; Liffner, Joel; Drikas, Mary

2015-10-01

The influence of vegetation and soil texture on the concentration and character of dissolved organic matter (DOM) present in runoff from the surface and sub-surface of zero order catchments of the Myponga Reservoir-catchment (South Australia) was investigated to determine the impacts of catchment characteristics and land management practices on the quality of waters used for domestic supply. Catchments selected have distinct vegetative cover (grass, native vegetation or pine) and contrasting texture of the surface soil horizon (sand or clay loam/clay). Water samples were collected from three slope positions (upper, middle, and lower) at soil depths of ~30 cm and ~60 cm in addition to overland flows. Filtered (0.45 μm) water samples were analyzed for dissolved organic carbon (DOC) and UV-visible absorbance and by F-EEM and HPSEC with UV and fluorescence detection to characterize the DOM. Surface and sub-surface runoff from catchments with clay soils and native vegetation or grass had lower DOC concentrations and lower relative abundances of aromatic, humic-like and high molecular weight organics than runoff from sandy soils with these vegetative types. Sub-surface flows from two catchments with Pinus radiata had similar DOC concentrations and DOM character, regardless of marked variation in surface soil texture. Runoff from catchments under native vegetation and grass on clay soils resulted in lower DOC concentrations and hence would be expected to have lower coagulant demand in conventional treatment for potable water supply than runoff from corresponding sandy soil catchments. However, organics in runoff from clay catchments would be more difficult to remove by coagulation. Surface waters from the native vegetation and grass catchments were generally found to have higher relative abundance of organic compounds amenable to removal by coagulation compared with sub-surface waters. Biophysical and land management practices combine to have a marked influence on the quality of source water used for domestic supply. Copyright © 2015 Elsevier B.V. All rights reserved.

Removal of hydrocarbon contaminant film from spacecraft optical surfaces using a radiofrequency-excited oxygen plasma.

NASA Technical Reports Server (NTRS)

Beverly, W. D.; Gillete, R. B.; Cruz, G. A.

1973-01-01

Results of a study on the feasibility of removing contaminant films from optical surfaces in vacuum, using an oxygen plasma, are discussed. Contaminant films were deposited onto optical surfaces from butadiene and methane gases at a pressure of about 4 torr in the presence of ultraviolet radiation. Optical surfaces evaluated included ultraviolet-reflecting mirrors, gratings, quartz disks, and spacecraft thermal control surfaces. In general, it was found that contaminants could be removed successfully from surfaces using an oxygen plasma. Exceptions were the white-paint thermal control surfaces, which, when contaminated, degraded further during exposure to the oxygen plasma.

Laser cleaning treatment of burnt paintings

NASA Astrophysics Data System (ADS)

Antonopoulou-Athera, N.; Chatzitheodoridis, E.; Doulgerides, M.; Evangelatos, Ch.; Serafetinides, A. A.; Terlixi, A.

2015-01-01

Three samples taken from two paintings partly burned by fire are investigated for cleaning with lasers. The paintings belong to the collection of the National Gallery of Athens and were made by the great Greek artist Konstantinos Parthenis. To remove the damaged surface and achieve an acceptable restoration result, the optimum combination of fluence and wavelength are sought. Seven different wavelengths with a set of fluences where used, i.e., the five harmonics of a Nd:YAG laser (1064, 532, 355, 266, and 213 nm), a TEA 10.6 μm CO2 and a free running laser Er:YAG 2.94 μm. Characterization was performed prior and after the cleaning process by optical and electron microscopy and analysis (SEM/BSE EDS), as well as X-Ray Diffraction (XRD). The results of this work indicate that the wavelength in the visible spectrum (532 nm) with fluences between 0.1-0.4J/cm2 show the optimum cleaning. The optical microscopy observation shows that with these laser parameters the burnt layer was preferentially removed, exposing the original colors that Parthenis had used in these paintings. Electron microscopy imaging and chemical analysis revealed that the original texture and materials of these samples are preserved after irradiation. Since the damage varies along the surface of the painting, more experiments should be performed in order to find and optimize the full cleaning and characterization process for the homogeneous cleaning of the whole surface of the painting.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Qiusheng, Y., E-mail: qsyan@gdut.edu.cn; Senkai, C., E-mail: senkite@sina.com; Jisheng, P., E-mail: panjisheng@gdut.edu.cn

Different machining processes were used in the single crystal SiC wafer machining. SEM was used to observe the surface morphology and a cross-sectional cleavages microscopy method was used for subsurface cracks detection. Surface and subsurface cracks characteristics of single crystal SiC wafer in abrasive machining were analysed. The results show that the surface and subsurface cracks system of single crystal SiC wafer in abrasive machining including radial crack, lateral crack and the median crack. In lapping process, material removal is dominated by brittle removal. Lots of chipping pits were found on the lapping surface. With the particle size becomes smaller,more » the surface roughness and subsurface crack depth decreases. When the particle size was changed to 1.5µm, the surface roughness Ra was reduced to 24.0nm and the maximum subsurface crack was 1.2µm. The efficiency of grinding is higher than lapping. Plastic removal can be achieved by changing the process parameters. Material removal was mostly in brittle fracture when grinding with 325# diamond wheel. Plow scratches and chipping pits were found on the ground surface. The surface roughness Ra was 17.7nm and maximum subsurface crack depth was 5.8 µm. When grinding with 8000# diamond wheel, the material removal was in plastic flow. Plastic scratches were found on the surface. A smooth surface of roughness Ra 2.5nm without any subsurface cracks was obtained. Atomic scale removal was possible in cluster magnetorheological finishing with diamond abrasive size of 0.5 µm. A super smooth surface eventually obtained with a roughness of Ra 0.4nm without any subsurface crack.« less

The effect of MTAD, an endodontic irrigant, on fibroblast attachment to periodontally affected root surfaces: A SEM analysis.

PubMed

Ghandi, Mostafa; Houshmand, Behzad; Nekoofar, Mohammad H; Tabor, Rachel K; Yadeghari, Zahra; Dummer, Paul M H

2013-03-01

Root surface debridement (RSD) is necessary to create an environment suitable for reattachment of the periodontium. Root surface conditioning may aid the formation of a biocompatible surface suitable for cell reattachment. BioPure™ MTAD (mixture of Doxycycline, citric acid and a detergent) is an endodontic irrigant with antibacterial properties and the ability to remove smear layer. It was hypothesized that MTAD may be useful for root surface conditioning. The efficacy of MTAD as a conditioner was measured by examining fibroblast attachment to root surfaces. Thirty-two specimens of human teeth with advanced periodontal disease were used. The surfaces were root planed until smooth. Half of the specimens were treated with 0.9% saline and the other samples with Biopure MTAD. As a negative control group, five further samples were left unscaled with surface calculus. Human gingival fibroblast cells HGF1-PI1 were cultured and poured over the tooth specimens and incubated. After fixation, the samples were sputter-coated with gold and examined with a SEM. The morphology and number of attached, fixed viable cells were examined. The data was analysed using the Mann-Whitney-U statistical test. There was no significant difference between the numbers of attached cells in the experimental group treated with MTAD and the control group treated with saline. Little or no attached cells were seen in the negative control group. RSD created an environment suitable for cell growth and attachment in a laboratory setting. The use of MTAD did not promote the attachment and growth of cells on the surface of human roots following RSD.

Apparatus for measuring surface particulate contamination

DOEpatents

Woodmansee, Donald E.

2002-01-01

An apparatus for measuring surface particulate contamination includes a tool for collecting a contamination sample from a target surface, a mask having an opening of known area formed therein for defining the target surface, and a flexible connector connecting the tool to the mask. The tool includes a body portion having a large diameter section defining a surface and a small diameter section extending from the large diameter section. A particulate collector is removably mounted on the surface of the large diameter section for collecting the contaminants. The tool further includes a spindle extending from the small diameter section and a spool slidingly mounted on the spindle. A spring is disposed between the small diameter section and the spool for biasing the spool away from the small diameter section. An indicator is provided on the spindle so as to be revealed when the spool is pressed downward to compress the spring.

Ion beam texturing

NASA Technical Reports Server (NTRS)

Hudson, W. R.

1976-01-01

A microscopic surface texture is created by sputter etching a surface while simultaneously sputter depositing a lower sputter yield material onto the surface. A xenon ion beam source has been used to perform this texturing process on samples as large as three centimeters in diameter. Ion beam textured surface structures have been characterized with SEM photomicrographs for a large number of materials including Cu, Al, Si, Ti, Ni, Fe, Stainless steel, Au, and Ag. Surfaces have been textured using a variety of low sputter yield materials - Ta, Mo, Nb, and Ti. The initial stages of the texture creation have been documented, and the technique of ion beam sputter removal of any remaining deposited material has been studied. A number of other texturing parameters have been studied such as the variation of the texture with ion beam power, surface temperature, and the rate of texture growth with sputter etching time.

Enhanced visible light-induced photocatalytic activity of surface-modified BiOBr with Pd nanoparticles

NASA Astrophysics Data System (ADS)

Meng, Xiangchao; Li, Zizhen; Chen, Jie; Xie, Hongwei; Zhang, Zisheng

2018-03-01

Palladium nanoparticles well-dispersed on BiOBr surfaces were successfully prepared via a two-step process, namely hydrothermal synthesis of BiOBr followed by photodeposition of palladium. Surface-exposed palladium nanoparticles may improve the harvesting capacity of visible light photons via the surface plasmonic resonance effect to produce extra electrons. Palladium is an excellent electron acceptor, and therefore favours the separation of photogenerated electron/hole pairs. As a result, palladium significantly improves the photocatalytic activity of BiOBr in the removal of organic pollutants (phenol) under visible light irradiation. In addition to as-prepared samples which were comprehensively characterized, the mechanism for the enhancement via the deposition of palladium nanoparticles was also proposed based on results. This work may serve as solid evidence to confirm that surface-deposited palladium nanoparticles are capable of improving photocatalytic activity, and that photodeposition may be an effective approach to load metal nanoparticles onto a surface.

A post-processing study on aluminum surface by fiber laser: Removing face milling patterns

NASA Astrophysics Data System (ADS)

Kayahan, Ersin

2018-05-01

The face milling process of the metal surface is a well-known machining process of using rotary cutters to remove material from a workpiece. Flat metal surfaces can be produced by a face milling process. However, in practice, visible, traced marks following the motion of points on the cutter's face are usually apparent. In this study, it was shown that milled patterns can be removed by means of 20 W fiber laser on the aluminum surface (AA7075). Experimental results also showed that roughened and hydrophobic surface can be produced with optimized laser parameters. It is a new approach to remove the patterns from the metal surface and can be explained through roughening by re-melting instead of ablation. The new method is a strong candidate to replace sandblasting the metal surface. It is also cheap and environmentally friendly.

Ni-Doping Effects on Oxygen Removal from an Orthorhombic Mo 2 C (001) Surface: A Density Functional Theory Study

DOE Office of Scientific and Technical Information (OSTI.GOV)

Zhou, Mingxia; Cheng, Lei; Choi, Jae-Soon

Density functional theory (DFT) calculations were used to investigate the effect of Ni dopants on the removal of chemisorbed oxygen (O*) from the Mo-terminated (T-Mo) and C-terminated (Tc) Mo2C(001) surfaces. The removal of adsorbed oxygen from the catalytic site is essential to maintain the long-term activity and selectivity of the carbide catalysts in the deoxygenation process related to bio-oil stabilization and upgrading. In this contribution, the computed reaction energetics and reaction barriers of O* removal were compared among undoped and Ni-doped Mo2C(001) surfaces. The DFT calculations indicate that selected Ni-doped surfaces such as Ni adsorbed on T-Mo and Tc Mo2C(001)more » surfaces enable weaker binding of important reactive intermediates (O*, OH*) compared to the undoped counterparts, which is beneficial for the O* removal from the catalyst surface. This study thus confirms the promoting effect of the Ni dopant on O* removal reaction on the T-Mo Mo2C(001) and Tc Mo2C(001) surfaces. This computational prediction has been confirmed by the temperature-programmed reduction profiles of Mo2C and Ni-doped Mo2C catalysts, which had been passivated and stored in an oxygen environment.« less

Effect of background colour on growth and adhesion strength of Ulva sporelings.

PubMed

Finlay, John A; Fletcher, Benjamin R; Callow, Maureen E; Callow, James A

2008-01-01

This study examined the effects of a range of black, grey and white substrata on the growth and attachment strength of Ulva sporelings on glass and polydimethylsiloxane (Silastic-T2) surfaces. The rate of development of sporelings was strongly influenced by the colour of the substratum on which they grew. On black backgrounds, sporelings grew slowly and germination was delayed. Laboratory screening methods for antifouling and fouling-release coatings that rely on the growth of Ulva sporelings can be compromised if samples are of different colours. Hydrodynamic removal of sporelings from coatings may also be affected by substratum colour, since smaller plants generate lower hydrodynamic forces making them more difficult to remove.

Techniques for improving material fidelity and contrast consistency in secondary electron mode helium ion microscope (HIM) imaging

NASA Astrophysics Data System (ADS)

Thompson, William; Stern, Lewis; Ferranti, Dave; Huynh, Chuong; Scipioni, Larry; Notte, John; Sanford, Colin

2010-06-01

Recent helium ion microscope (HIM) imaging studies have shown the strong sensitivity of HIM induced secondary electron (SE) yields [1] to the sample physical and chemical properties and to its surface topography. This SE yield sensitivity is due to the low recoil energy of the HIM initiated electrons and their resulting short mean free path. Additionally, a material's SE escape probability is modulated by changes in the material's work function and surface potential. Due to the escape electrons' roughly 2eV mean energy and their nanometer range mean free path, HIM SE mode image contrast has significant material and surface sensitivity. The latest generation of HIM has a 0.35 nanometer resolution specification and is equipped with a plasma cleaning process to mitigate the effects of hydrocarbon contamination. However, for surfaces that may have native oxide chemistries influencing the secondary electron yield, a new process of low energy, shallow angle argon sputtering, was evaluated. The intent of this work was to study the effect of removing pre-existing native oxides and any in-situ deposited surface contaminants. We will introduce the sputter yield predictions of two established computer models and the sputter yield and sample modification forecasts of the molecular dynamics program, Kalypso. We will review the experimental technique applied to copper samples and show the copper grain contrast improvement that resulted when argon cleaned samples were imaged in HIM SE mode.

Intensive care unit environmental surfaces are contaminated by multidrug-resistant bacteria in biofilms: combined results of conventional culture, pyrosequencing, scanning electron microscopy, and confocal laser microscopy.

PubMed

Hu, H; Johani, K; Gosbell, I B; Jacombs, A S W; Almatroudi, A; Whiteley, G S; Deva, A K; Jensen, S; Vickery, K

2015-09-01

Hospital-associated infections cause considerable morbidity and mortality, and are expensive to treat. Organisms causing these infections can be sourced from the inanimate environment around a patient. Could the difficulty in eradicating these organisms from the environment be because they reside in dry surface biofilms? The intensive care unit (ICU) of a tertiary referral hospital was decommissioned and the opportunity to destructively sample clinical surfaces was taken in order to investigate whether multidrug-resistant organisms (MDROs) had survived the decommissioning process and whether they were present in biofilms. The ICU had two 'terminal cleans' with 500 ppm free chlorine solution; items from bedding, surrounds, and furnishings were then sampled with cutting implements. Sections were sonicated in tryptone soya broth and inoculated on to chromogenic plates to demonstrate MDROs, which were confirmed with the Vitek2 system. Genomic DNA was extracted directly from ICU samples, and subjected to polymerase chain reaction (PCR) for femA to detect Staphylococcus aureus and the microbiome by bacterial tag-encoded FLX amplicon pyrosequencing. Confocal laser scanning microscopy (CLSM) and scanning electron microscopy (SEM) were performed on environmental samples. Multidrug-resistant bacteria were cultured from 52% (23/44) of samples cultured. S. aureus PCR was positive in 50%. Biofilm was demonstrated in 93% (41/44) of samples by CLSM and/or SEM. Pyrosequencing demonstrated that the biofilms were polymicrobial and contained species that had multidrug-resistant strains. Dry surface biofilms containing MDROs are found on ICU surfaces despite terminal cleaning with chlorine solution. How these arise and how they might be removed requires further study. Copyright © 2015 The Healthcare Infection Society. Published by Elsevier Ltd. All rights reserved.

Polycyclic Aromatic Hydrocarbon Distribution and Modification in the Sub-surface Plume Near the Deepwater Horizon Wellhead

NASA Astrophysics Data System (ADS)

Shiller, A. M.; Joung, D.; Wade, T.

2011-12-01

A significant concern associated with oil spills is the toxicity associated with the polycyclic aromatic hydrocarbon (PAH) component. Ratios of various PAH's have also been used as indicators of oil sources. During a late May/early June cruise, 57 samples for PAH analysis were collected in the vicinity of the Deepwater Horizon wellhead. Most samples were from the previously reported sub-surface oil plume, centered near 1100 m depth. PAH concentrations ranged up to 117 μg/L and rapidly diminished in the subsurface with distance from the wellhead. The Macondo well oil was observed to be rich in naphthalenes. Within a few km of the wellhead, the percentage of methyl-naphthalenes in the sub-surface plume was generally higher than in the source, suggesting preferential solubilization of this low molecular weight fraction. However, the percentage rapidly decreased away from the well also suggesting rapid destruction or removal of the naphthalenes. The pyrogenic index (Wang et al.) was <0.05 for all samples, indicating a petroleum origin. For a few samples, some other PAH ratios (e.g., MP/P and P/A ratios) suggested a combustion origin. However, these ratios also tended to vary both with percent methyl-naphthalenes and distance from the wellhead, suggesting anomalous ratios originating from solubilization/degradation effects. We also obtained a more limited set of surface water samples, generally avoiding the most contaminated areas as well as areas of oil burning. For these surface water samples, similar trends were observed as at depth, probably resulting from selective volatilization and photo-degradation. Overall, the data illustrate how environmental factors lead both to reduced concentrations and fractionation of the PAH's.

Space environmental effects on silvered Teflon thermal control surfaces

NASA Technical Reports Server (NTRS)

Hemminger, C. S.; Stuckey, W. K.; Uht, J. C.

1992-01-01

Cumulative space environmental effects on silver/fluorinated ethylene propylene (Ag/FEP) were a function of exposure orientation. Samples from nineteen silvered Teflon (Ag/FEP) thermal control surfaces recovered from the Long Duration Exposure Facility (LDEF) were analyzed to determine changes in this material as a function of position on the spacecraft. Although solar absorptance and infrared emittance of measured thermal blanket specimens are relatively unchanged from control specimen values, significant changes in surface morphology, composition, and chemistry were observed. We hypothesize that the FEP surfaces on the LDEF are degraded by UV radiation at all orientations, but that the damaged material has been removed by erosion from the blankets exposed to atomic oxygen flux and that contamination is masking the damage in some areas on the trays flanking the trailing edge.

Auger spectroscopic examination of MgF2-coated Al mirrors before and after UV irradiation

NASA Technical Reports Server (NTRS)

Heaney, J. B.; Herzig, H.; Osantowski, J. F.

1977-01-01

Magnesium fluoride protected Al films were studied since these mirrors are commonly used in astronomical instruments whenever a highly reflecting optical surface is required in the wavelength region from 1100 A to 2000 A. Freshly prepared samples of evaporated Al + 250-A thick MgF2 on glass were analyzed by Auger electron spectroscopy in conjunction with surface erosion by Ar(+) ion bombardment before and after UV irradiation. The analysis showed that a very thin layer of surface contamination and not bulk photolysis in the MgF2 film was reponsible for the irradiation-induced reflectance loss. Postirradiation polishing with a mild calcium carbonate abrasive can restore a mirror's reflectance by removing the photolyzed surface film without disturbing the MgF2 layer.

Surface modification to waveguides

DOEpatents

Timberlake, J.R.; Ruzic, D.N.; Moore, R.L.; Cohen, S.A.; Manos, D.M.

1982-06-16

A method is described for treating the interior surfaces of a waveguide to improve power transmission comprising the steps of mechanically polishing to remove surface protrusions; electropolishing to remove embedded particles; ultrasonically cleaning to remove any residue; coating the interior waveguide surfaces with an alkyd resin solution or electrophoretically depositing carbon lamp black suspended in an alkyd resin solution to form a 1..mu.. to 5..mu.. thick film; vacuum pyrolyzing the film to form a uniform adherent carbon coating.

An accessible micro-capillary electrophoresis device using surface-tension-driven flow

PubMed Central

Mohanty, Swomitra K.; Warrick, Jay; Gorski, Jack; Beebe, David J.

2010-01-01

We present a rapidly fabricated micro-capillary electrophoresis chip that utilizes surface-tension-driven flow for sample injection and extraction of DNA. Surface-tension-driven flow (i.e. passive pumping) injects a fixed volume of sample that can be predicted mathematically. Passive pumping eliminates the need for tubing, valves, syringe pumps, and other equipment typically needed for interfacing with microelectrophoresis chips. This method requires a standard micropipette to load samples before separation, and remove the resulting bands after analysis. The device was made using liquid phase photopolymerization to rapidly fabricate the chip without the need of special equipment typically associated with the construction of microelectrophoresis chips (e.g. cleanroom). Batch fabrication time for the device presented here was 1.5 h including channel coating time to suppress electroosmotic flow. Devices were constructed out of poly-isobornyl acrylate and glass. A standard microscope with a UV source was used for sample detection. Separations were demonstrated using Promega BenchTop 100 bp ladder in hydroxyl ethyl cellulose (HEC) and oligonucleotides of 91 and 118 bp were used to characterize sample injection and extraction of DNA bands. The end result was an inexpensive micro-capillary electrophoresis device that uses tools (e.g. micropipette, electrophoretic power supplies, and microscopes) already present in most labs for sample manipulation and detection, making it more accessible for potential end users. PMID:19425002

Dielectrophoretic sample preparation for environmental monitoring of microorganisms: Soil particle removal.

PubMed

Fatoyinbo, Henry O; McDonnell, Martin C; Hughes, Michael P

2014-07-01

Detection of pathogens from environmental samples is often hampered by sensors interacting with environmental particles such as soot, pollen, or environmental dust such as soil or clay. These particles may be of similar size to the target bacterium, preventing removal by filtration, but may non-specifically bind to sensor surfaces, fouling them and causing artefactual results. In this paper, we report the selective manipulation of soil particles using an AC electrokinetic microfluidic system. Four heterogeneous soil samples (smectic clay, kaolinitic clay, peaty loam, and sandy loam) were characterised using dielectrophoresis to identify the electrical difference to a target organism. A flow-cell device was then constructed to evaluate dielectrophoretic separation of bacteria and clay in a continous flow through mode. The average separation efficiency of the system across all soil types was found to be 68.7% with a maximal separation efficiency for kaolinitic clay at 87.6%. This represents the first attempt to separate soil particles from bacteria using dielectrophoresis and indicate that the technique shows significant promise; with appropriate system optimisation, we believe that this preliminary study represents an opportunity to develop a simple yet highly effective sample processing system.

Toward a solid-phase nucleic acid hybridization assay within microfluidic channels using immobilized quantum dots as donors in fluorescence resonance energy transfer.

PubMed

Chen, Lu; Algar, W Russ; Tavares, Anthony J; Krull, Ulrich J

2011-01-01

The optical properties and surface area of quantum dots (QDs) have made them an attractive platform for the development of nucleic acid biosensors based on fluorescence resonance energy transfer (FRET). Solid-phase assays based on FRET using mixtures of immobilized QD-oligonucleotide conjugates (QD biosensors) have been developed. The typical challenges associated with solid-phase detection strategies include non-specific adsorption, slow kinetics of hybridization, and sample manipulation. The new work herein has considered the immobilization of QD biosensors onto the surfaces of microfluidic channels in order to address these challenges. Microfluidic flow can be used to dynamically control stringency by adjustment of the potential in an electrokinetic-based microfluidics environment. The shearing force, Joule heating, and the competition between electroosmotic and electrophoretic mobilities allow the optimization of hybridization conditions, convective delivery of target to the channel surface to speed hybridization, amelioration of adsorption, and regeneration of the sensing surface. Microfluidic flow can also be used to deliver (for immobilization) and remove QD biosensors. QDs that were conjugated with two different oligonucleotide sequences were used to demonstrate feasibility. One oligonucleotide sequence on the QD was available as a linker for immobilization via hybridization with complementary oligonucleotides located on a glass surface within a microfluidic channel. A second oligonucleotide sequence on the QD served as a probe to transduce hybridization with target nucleic acid in a sample solution. A Cy3 label on the target was excited by FRET using green-emitting CdSe/ZnS QD donors and provided an analytical signal to explore this detection strategy. The immobilized QDs could be removed under denaturing conditions by disrupting the duplex that was used as the surface linker and thus allowed a new layer of QD biosensors to be re-coated within the channel for re-use of the microfluidic chip.

Photodegradation of dioxin in contaminated soil in the presence of solvents and nanoscale TiO2 particles.

PubMed

Binh, Nguyen Duy; Oanh, Nguyen Thi Kim; Parkpian, Preeda

2014-01-01

Decomposition of 2,3,7,8-Tetrachlorodibenzo-p-dioxin (2,3,7,8-TCDD) present in soil under ultraviolet (UV) illumination (350-400nm) was investigated using a combination of nontoxic solvents mixed in soil and nanoscale anatase TiO2 (nTiO2) distributed on 2mm top soil surface. Three types of UV-exposure experiments were conducted: intermittent exposure (8 h/day) for 90 days and 120 days, sequential intermittent (120 days) and continuous (24 h/day) for the next 55 days, and continuous exposure for 55 days. The influence of several factors on dioxin photodegradation efficiency was investigated, including the UV absorption by the targeted dioxin, presence of catalytic nTiO2 on soil surface, solvent evaporation rate, as well as vertical gradients of solvents added into the soil columns. Results of dioxin analysis for the soil samples collected at the end of every experiment condition show that the photodegradation enhanced by the nTiO2 presence on the soil surface considerably increased the dioxin removal. Higher removal efficiencies were found for treatments with 15%wt of nTiO2 mixed in the 2-mm surface soil as compared to the 5%wt nTiO2 treatments. The highest removal efficiency (79.6%) was for the sequential intermittent-continuous UV-exposure experiment with nTiO2. Dechlorinated products of 2,3,7,8-TCDD were generally not detected which suggests degradation of targeted dioxin by C-Cl cleavage was negligible. Further modifications to improve removal efficiencies were proposed. Large-scale engineered systems may employ this integrated treatment approach which can also incorporate the reuse of the top soil containing nTiO2 and solvent vapours. With the utilization of natural sunlight such systems would be promisingly suitable for tropical conditions.

The correlation between cellulose allomorphs (I and II) and conversion after removal of hemicellulose and lignin of lignocellulose.

PubMed

Song, Yanliang; Zhang, Jingzhi; Zhang, Xu; Tan, Tianwei

2015-10-01

H2SO4, NaOH and H3PO4 were applied to decompose lignocellulose samples (giant reeds, pennisetum and cotton stalks) to investigate the correlation between cellulose allomorphs (cellulose I and II) and conversion of cellulose. The effect of removal of hemicellulose and lignin on the surface morphology, crystallinity index (CrI), cellulose allomorphs (cellulose I and II), and enzymatic hydrolysis under different pretreatments was also studied. CrI caused by H3PO4 pretreatment reached 11.19%, 24.93% and 8.15% for the three samples, respectively. Corn stalk showed highest conversion of cellulose among three samples, irrespective of the pretreatment used. This accounted for the widely use of corn stalk as the renewable crop substrate to synthesize biofuels like ethanol. CrI of cellulose I (CrI-I) negatively affects cellulose conversion but CrI of cellulose II (CrI-II) positively affects cellulose conversion. It contributes to make the strategy to transform cellulose I to cellulose II and enhancing enzymatic hydrolysis of lignocellulose. Copyright © 2015 Elsevier Ltd. All rights reserved.

Use of atomic force microscopy in the forensic application of chronological order of toners and stamping inks in questioned documents.

PubMed

Kang, Tae-Yi; Lee, Joong; Park, Byung-Wook

2016-04-01

This paper describes the application of the atomic force microscopy (AFM) as a nano-indentation method and introduces a new method of identifying the chronological order of the application of the toner and stamping ink on the surface of documents by removing either of them. Various toners were used as samples for the AFM nano-indentation method. The chronological order of the application of the toner and stamping ink with either the toner placed over the stamping ink or the stamping ink placed over the toner, could be identified, regardless of the kinds of toners made by various companies. This paper provides the new approach for physically removing the toner and checking the material below it to identify questioned documents, which allows the method to be used to appraise documents forensically. Blind testing has shown that the method to analyze the chronological order of toner-printed documents and the seal stamping on them could accurately identify the order in all samples, while minimizing damage to the samples. Copyright © 2016 Elsevier Ireland Ltd. All rights reserved.

Removal of sulfa drugs by sewage treatment in aqueous solution systems: activated carbon treatment and ozone oxidation.

PubMed

Ogata, Fumihiko; Tominaga, Hisato; Kangawa, Moe; Inoue, Kenji; Kawasaki, Naohito

2012-01-01

This study investigates the activated carbon (AC) treatment and ozone oxidation of the sulfa drugs--sulfamethoxazole (SMX), sulfamonomethoxine (SMM), sulfadimidine (SDD), and sulfadimethoxine (SDM)--in aqueous solution systems. Three AC samples were prepared from Shirasagi (AC1 and AC2) and coal (AC3), and the surface functional groups, solution pH, specific surface areas, pore volumes, and morphologies of the three samples were evaluated. The specific surface areas were in the following order: AC1 (1391 m²/g) > AC2 (1053 m²/g) > AC3 (807 m²/g). The pore volume and mean pore diameter of AC3 were greater than those of AC1 and AC2. The concentration of sulfa drugs adsorbed onto the AC samples reached equilibrium within 150 h. Experimental data of the adsorption rate were fitted to a pseudo-second-order model. The amount of sulfa drugs adsorbed onto the AC samples was in the order of SDM < SMM < SDD < SMX; the mechanism of adsorption of the sulfa drugs onto the AC samples depended on the hydrophobicity of the AC surface. The adsorption isotherm data were fitted to Freundlich and Langmuir models. Ozone was generated from oxygen gas using an A-27 ozone generator, and the complete degradation of the sulfa drugs by ozone treatment at 60 mL/min was achieved within 50 min. Ozone treatment caused the structure of the sulfa drugs to decompose via ozone oxidation.

Adsorption Studies of Chromium(VI) on Activated Carbon Derived from Mangifera indica (Mango) Seed Shell

NASA Astrophysics Data System (ADS)

Mise, Shashikant; Patil, Trupti Nagendra

2015-09-01

The removal of chromium(VI) from synthetic sample by adsorption on activated carbon prepared from Mangifera indica (mango) seed shell have been carried out at room temperature 32 ± 1 °C. The removal of chromium(VI) from synthetic sample by adsorption on two types of activated carbon, physical activation and chemical activation (Calcium chloride and Sodium chloride), Impregnation Ratio's (IR) 0.25, 0.50, 0.75 for optimum time, optimum dosages and variation of pH were studied. It is observed that contact time differs for different carbons i.e. for physically and chemically activated carbons. The contact time decreases for chemically activated carbon compared to the physically activated carbon. It was observed that as dosage increases the adsorption increased along with the increase in impregnation ratio. It was also noted that as I.R. increases the surface area of Mangifera indica shell carbon increased. These dosage data were considered in the construction of isotherms and it was found that adsorption obeys Freundlich Isotherm and does not obey Langmuir Isotherm. The maximum removal of chromium (VI) was obtained in highly acidic medium at a pH of 1.50.

Bioremediation of hydrocarbons contaminating sewage effluent using man-made biofilms: effects of some variables.

PubMed

Al-Mailem, D M; Kansour, M K; Radwan, S S

2014-11-01

Biofilm samples were established on glass slides by submerging them in oil-free and oil-containing sewage effluent for a month. In batch cultures, such biofilms were effective in removing crude oil, pure n-hexadecane, and pure phenanthrene contaminating sewage effluent. The amounts of the removed hydrocarbons increased with increasing biofilm surface area exposed to the effluent. On the other hand, addition of the reducing agent thioglycollate dramatically inhibited the hydrocarbon bioremediation potential of the biofilms. The same biofilm samples removed contaminating hydrocarbons effectively in three successive batch bioremediation cycles but started to become less effective in the cycles thereafter, apparently due to mechanical biofilm loss during successive transfers. As major hydrocarbonoclastic bacteria, the biofilms harbored species belonging to the genera Pseudomonas, Microvirga, Zavarzinia, Mycobacterium, Microbacterium, Stenotrophomonas, Gordonia, Bosea, Sphingobium, Brachybacterium, and others. The nitrogen fixer Azospirillum brasilense and the microalga Ochromonas distigma were also present; they seemed to enrich the biofilms, with nitrogenous compounds and molecular oxygen, respectively, which are known to enhance microbiological hydrocarbon degradation. It was concluded that man-made biofilms based upon sewage microflora are promising tools for bioremediation of hydrocarbons contaminating sewage effluent.

3D surface coordinate inspection of formed sheet material parts using optical measurement systems and virtual distortion compensation

NASA Astrophysics Data System (ADS)

Weckenmann, Albert A.; Gall, P.; Gabbia, A.

2005-02-01

Modern forming technology allows the production of highly sophisticated free form sheet material components, affording great flexibility to the design and manufacturing processes across a wide range of industries. This increased design and manufacturing potential places an ever growing demand on the accompanying inspection metrology. As a consequence of their surface shape, these parts underlie a reversible geometrical deformation caused by variations of the material and the manufacturing process, as well as by gravity. This distortion is removed during the assembly process, usually performed in automated robotic processes. For this reason, the part's tolerated parameters have to be inspected in a defined state, simulating the assembly process' boundary conditions. Thus, the inspection process chain consists of six steps: picking the workpiece up, manual fixation of the workpiece, tactile measurement of the surface's coordinates using a defined measurement strategy, manual removal of the fixation and removal of the workpiece from the inspection area. These steps are both laborious and time consuming (for example, the inspection of a car door can take up to a working day to complete). Using optical measuring systems and virtual distortion compensation, this process chain can be dramatically shortened. Optical measuring systems provide as a measurement result a point cloud representing a sample of all nearest surfaces in the measuring range containing the measurand. From this data, a surface model of the measurand can be determined, independent of its position in the measuring range. For thin sheet material parts an approximating finite element model can be deduced from such a surface model. By means of pattern recognition, assembly relevant features of the measurand can be identified and located on this model. Together with the boundary conditions given by the assembly process, the shape of the surface in its assembled state can be calculated using the finite elements method. In application these methods culminate in a shortened inspection process chain (which can now also be automated): picking the workpiece up, placing it in the measuring range, optical measurement, virtual distortion compensation and removal of the workpiece from the inspection area. This work discusses the methodology of our approach in detail and also provides and analyses experimental results. The underlying research was greatfully funded by the German Research Foundation (DFG).

The Effects of Carbon Nanotube Reinforcement on Adhesive Joints for Naval Applications

DTIC Science & Technology

2009-12-01

ACRONYMS AND ABBREVIATIONS CNT Carbon Nanotube CoNap Cobalt Naphthenate DMA Dimethylaniline IR Infared MEKP Methyl Ethyl Ketone Peroxide... removed prior to use. The selection of cold rolled steel significantly reduced the surface preparation required for each sample. The steel was one...6% Cobalt Naphthenate (CoNap), as well as an accelerator, dimethylaniline (DMA), can be varied to control gel time of the resign based on ambient

Flocculent Settling of Food Wastes.

PubMed

Chowdhury, Mohammad Monirul Islam; Kim, Mingu; Haroun, Basem Mikhaeil; Nakhla, George; Keleman, Michael

2016-07-01

This study evaluated the flocculent settling in water and municipal wastewater (MWW) in a 10.6 ft deep column. A total of eight runs at three different testing conditions involving MWW alone, food waste (FW) alone, and FW in MWW (FW+MWW) were conducted. Total suspended solid (TSS), total BOD (TBOD), total COD (TCOD), total nitrogen (TN), and total phosphorous (TP) removal efficiencies after 3 hours of settling were 62%, 46%, 49%, 46% and 62% for FW, and 50%, 43%, 39%, 37% and 24% for MWW. Removal efficiencies of particulate COD (PCOD) and particulate BOD (PBOD) at the lowest surface overflow rate (SOR) of 1.1 m3/m2/hr corresponding to the longest settling time of 3 hours were 59% and 64% for FW, and 65% and 70% for FW with MWW samples. On the other hand, no significant variation between FW and FW with MWW was observed for PN removal after 3 hours of settling.

Microbiological Characterization of the International Space Station Water Processor Assembly External Filter Assembly S/N 01

NASA Technical Reports Server (NTRS)

Weir, Natalee; Wilson, Mark; Yoets, Airan; Yoets, Airan; Molina, Thomas; Bruce, Rebekah; Sitler, Glenn; Carter, Layne

2012-01-01

The External Filter Assembly (EFA) S/N 01 is a mesh screen filter with a pore size of approximately 300 micron that was installed in the International Space Station (ISS) Water Processor Assembly (WPA) between the Waste Tank and the Mostly Liquid Separator (MLS) on February 11, 2010 to protect clearances in the MLS solenoid valve SV_1121_3. A removal & replacement of the EFA Filter was performed on March 22, 2011 in response to increasing pressure across the Waste Tank solenoid valve SV_1121_1 and the EFA Filter. The EFA Filter was returned on ULF6 and received in the Boeing Huntsville Laboratory on June 13, 2011. The filter was aseptically removed from the housing, and the residual water was collected for enumeration and identification of bacteria and fungi. Swab samples of the filter surface were also collected for microbiological enumeration and identification. Sample analyses were performed by Boeing Huntsville Laboratory and NASA Johnson Space Center Microbiology for comparison. Photographic documentation of the EFA filter was performed using a stereo microscope and environmental scanning electron microscope. This paper characterizes the amount and types of microorganisms on the filter surface and in the residual water from the filter housing following 1 year of utilization in the ISS WPA.

Surface modification of a natural zeolite by treatment with cold oxygen plasma: Characterization and application in water treatment

NASA Astrophysics Data System (ADS)

De Velasco-Maldonado, Paola S.; Hernández-Montoya, Virginia; Montes-Morán, Miguel A.; Vázquez, Norma Aurea-Rangel; Pérez-Cruz, Ma. Ana

2018-03-01

In the present work the possible surface modification of natural zeolite using cold oxygen plasma was studied. The sample with and without treatment was characterized using nitrogen adsorption isotherms at -196 °C, FT-IR spectroscopy, SEM/EDX analysis and X-Ray Diffraction. Additionally, the two samples were used for the removal of lead and acid, basic, reactive and food dyes in batch systems. The natural zeolite was found to be a mesoporous material with a low specific surface area (23 m2/g). X-ray patterns confirmed that clinoptilolite was the main crystal structure present in the natural zeolite. The molecular properties of dyes and the zeolitic structure were studied using molecular simulation, with the purpose to understand the adsorption mechanism. The results pointed out that only the roughness of the clinoptilolite was affected by the plasma treatment, whereas the specific surface area, chemical functionality and crystal structure remained constant. Finally, adsorption results confirmed that the plasma treatment had no significant effects on the dyes and lead retention capacities of the natural zeolite.

The distribution of particulate material on Mars

NASA Technical Reports Server (NTRS)

Christensen, Philip R.

1991-01-01

The surface materials on Mars were extensively studied using a variety of spacecraft and Earth-based remote sensing observations. These measurements include: (1) diurnal thermal measurements, used to determine average particle size, rock abundance, and the presence of crusts; (2) radar observations, used to estimate the surface slope distributions, wavelength scale roughness, and density; (3) radio emission observations, used to estimate subsurface density; (4) broadband albedo measurements, used to study the time variation of surface brightness and dust deposition and removal; and (5) color observations, used to infer composition, mixing, and the presence of crusts. Remote sensing observations generally require some degree of modeling to interpret, making them more difficult to interpret than direct observations from the surface. They do, however, provide a means for examining the surface properties over the entire planet and a means of sampling varying depths within the regolith. Albedo and color observations only indicate the properties of the upper-most few microns, but are very sensitive to thin, sometimes emphemeral dust coatings. Thermal observations sample the upper skin depth, generally 2 to 10 cm. Rock abundance measurements give an indirect indication of surface mantling, where the absence of rocks suggests mantles of several meters. Finally, radar and radio emission data can penetrate several meters into the surface, providing an estimate of subsurface density and roughness.

Study of chemical and thermal treatment of kaolinite and its influence on the removal of contaminants from mining effluents.

PubMed

de Sales, Priscila F; Magriotis, Zuy M; Rossi, Marco Aurélio de L S; Tartuci, Letícia G; Papini, Rísia M; Viana, Paulo R M

2013-10-15

The effects of chemical and thermal treatments on the structure of kaolinite were examined, as well as the influence of those changes upon the removal of etheramine, a cationic collector used in the processing of iron ore. The materials were characterized using XRD, XRF, specific surface area (SBET), FTIR, zeta potential and a test for determination of acid sites. The effects of the treatments on the structure of kaolinite were evaluated using chemometric tools developed from principal components analysis algorithms and hierarchical components analysis. The parameters evaluated in the kinetic study of adsorption were contact time, initial concentration of etheramine, quantity of adsorbent and pH. The adsorption of etheramine in the samples subjected to chemical treatments could be explained by a pseudo-second order model, whilst for the sample subjected to thermal treatment, better fit was with the pseudo-first order model. With regard to adsorption isotherms, it was shown that for the three adsorbents used, adsorption followed the Langmuir model. The maximum quantities adsorbed were 27 mg g(-1), 29 mg g(-1) and 59 mg g(-1), respectively, for the samples subjected to acid, thermal and peroxide treatments. The treatment with peroxide was found to be the most suitable for removal of etheramine. Copyright © 2013 Elsevier Ltd. All rights reserved.

Expansible apparatus for removing the surface layer from a concrete object

DOEpatents

Allen, Charles H.

1979-01-01

A method and apparatus for removing the surface layer from a concrete object. The method consists of providing a hole having a circular wall in the surface layer of the object, the hole being at least as deep as the thickness of the surface layer to be removed, and applying an outward wedging pressure on the wall of the hole sufficient to spall the surface layer around the hole. By the proper spacing of an appropriate number of holes, it is possible to remove the entire surface layer from an object. The apparatus consists of an elongated tubular-shaped body having a relatively short handle with a solid wall at one end, the wall of the remainder of the body containing a plurality of evenly spaced longitudinal cuts to form a relatively long expandable section, the outer end of the expandable section having an expandable, wedge-shaped spalling edge extending from the outer surface of the wall, perpendicular to the longitudinal axis of the body, and expanding means in the body for outwardly expanding the expandable section and forcing the spalling edge into the wall of a hole with sufficient outward pressure to spall away the surface layer of concrete. The method and apparatus are particularly suitable for removing surface layers of concrete which are radioactively contaminated.

Synthesis and characterization of zeolite from coal fly ash

NASA Astrophysics Data System (ADS)

Liu, Yong; Luo, Qiong; Wang, Guodong; Li, Xianlong; Na, Ping

2018-05-01

Fly ash (FA) from coal-based thermal power plant was used to synthesize zeolite in NaOH solution with hydrothermal method in this work. Firstly, the effects of calcination and acid treatment on the removal of impurities in fly ash were studied. Then based on the pretreated FA, the effects of alkali concentration, reaction temperature and Si/Al ratio on the synthesis of zeolite were studied in detail. The mineralogy, morphology, thermal behavior, infrared spectrum and specific surface for the synthetic sample were investigated. The results indicated that calcination at 750 °C for 1.5 h can basically remove unburned carbon from FA, and 4 M hydrochloric acid treatment of calcined FA at 90 °C for 2 h will reduce the quality of about 34.3%wt, which are mainly iron, calcium and sulfur elements. The concentration of NaOH, reaction temperature and Si/Al ratio have important effect on the synthesis of zeolite. In this study, 0.5 M NaOH cannot obtain any zeolite. High temperature is beneficial to zeolite synthesis from FA, but easily lead to a variety of zeolites. The synthetic sample contains three kinds of zeolites such as zeolite P, sodalite and zeolite X, when the reaction conditions are 2 M NaOH and 120 °C for 24 h. In this research, quartz always exists in the synthetic sample, but will reduce with the increase of temperature. The synthetic zeolite has the specific surface area of about 42 m2 g‑1 and better thermal stability.

Effect of temperature on the release of hexadecane from soil by thermal treatment.

PubMed

Merino, Jerónimo; Bucalá, Verónica

2007-05-08

A natural organic soil (2.5% of total organic carbon) was artificially contaminated with hexadecane, and thermally treated under an inert medium up to different final temperatures (150-800 degrees C) for 30 min to simulate ex situ thermal process conditions. The experiments were conducted using a complete organic soil, instead of the clays or isolated soil fractions that are commonly used. Neat and contaminated samples were separately heated to understand the impact of the soil itself and the contaminant in the release of volatiles. The soil quality as well as the quality and amount of volatile compounds generated during the process were monitored. More than 80-88% of the initial hexadecane content in the soil matrix was recovered in liquids traps after the thermal treatment, therefore the contaminant could be recovered for further recycling. The high amount of hexadecane collected without suffering chemical transformations indicated that the main mechanism for the hexadecane removal was evaporation. The analysis of the light gases released from contaminated samples indicated negligible or null hexadecane pyrolysis reaction rates, confirming that the evaporation/desorption of the contaminant are the processes that governed the removal of the contaminant from the soil. For the soil tested, of a relatively low surface area, good removal efficiencies (higher than 99.9%) were detected at about 300 degrees C, being higher temperatures not necessary to significantly improve the contamination removal.

Effect of surface characteristics on retention and removal of Escherichia coli O157:H7 on surfaces of spinach

USDA-ARS?s Scientific Manuscript database

The topography and the spatial heterogeneity of produce surfaces may impact the attachment of microbial cells onto produce surfaces and affect disinfection efficacy. In this study, the effects of produce surface characteristics on the removal of bacteria were studied. Fresh spinach leaves were sp...

Optimal Magnetorheological Fluid for Finishing of Chemical-Vapor-Deposited Zinc Sulfide

NASA Astrophysics Data System (ADS)

Salzman, Sivan

Magnetorheological finishing (MRF) of polycrystalline, chemical-vapor- deposited zinc sulfide (ZnS) optics leaves visible surface artifacts known as "pebbles". These artifacts are a direct result of the material's inner structure that consists of cone-like features that grow larger (up to a few millimeters in size) as deposition takes place, and manifest on the top deposited surface as "pebbles". Polishing the pebble features from a CVD ZnS substrate to a flat, smooth surface to below 10 nm root-mean-square is challenging, especially for a non-destructive polishing process such as MRF. This work explores ways to improve the surface finish of CVD ZnS processed with MRF through modification of the magnetorheological (MR) fluid's properties. A materials science approach is presented to define the anisotropy of CVD ZnS through a combination of chemical and mechanical experiments and theoretical predictions. Magnetorheological finishing experiments with single crystal samples of ZnS, whose cuts and orientations represent most of the facets known to occur in the polycrystalline CVD ZnS, were performed to explore the influence of material anisotropy on the material removal rate during MRF. By adjusting the fluid's viscosity, abrasive type concentration, and pH to find the chemo-mechanical conditions that equalize removal rates among all single crystal facets during MRF, we established an optimized, novel MR formulation to polish CVD ZnS without degrading the surface finish of the optic.

[Preparation of titanium dioxide particles and properties for flue gas desulfurization].

PubMed

Luo, Yonggang; Li, Daji; Huang, Zhen

2003-01-01

Under different sintering temperatures(340 degrees C, 440 degrees C, 540 degrees C, 640 degrees C), four TiO2 particles were prepared. The crystal types of all four samples were found to possess anatase structures by XRD. It was obtained by N2 experimental adsorption at low temperature (77K) that their surface areas and average pore size were between 79 and 124 m2/g, 56.8 and 254.8 A respectively. The pore structure of TiO2 particles was characterized by scanning electron microscope (SEM). The tests of adsorption dynamics for FGD and the performance of SO2 removal were investigated in a fixed-bed system for different samples. The results show that SG540 sample which made at 540 degrees C sintering temperature had the most quality among the four samples. It can adsorb SO2 of 38.9 mg for one gram SG540 sample. Different operating conditions for SG540 such as adsorption temperature, SO2 concentration in flue gas and the superficial velocity of flue gas were investigated. TiO2 particles for FGD had more efficiency than other physical sorbents such as active carbon and zeolite. The mechanism for SO2 removal was demonstrated by infrared (IR) spectroscopy and desorption test results to be mainly physical adsorption.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Andersson, Gunther G., E-mail: gunther.andersson@flinders.edu.au, E-mail: vladimir.golovko@canterbury.ac.nz, E-mail: greg.metha@adelaide.edu.au; Al Qahtani, Hassan S.; Golovko, Vladimir B., E-mail: gunther.andersson@flinders.edu.au, E-mail: vladimir.golovko@canterbury.ac.nz, E-mail: greg.metha@adelaide.edu.au

Chemically made, atomically precise phosphine-stabilized clusters Au{sub 9}(PPh{sub 3}){sub 8}(NO{sub 3}){sub 3} were deposited on titania and silica from solutions at various concentrations and the samples heated under vacuum to remove the ligands. Metastable induced electron spectroscopy was used to determine the density of states at the surface, and X-ray photoelectron spectroscopy for analysing the composition of the surface. It was found for the Au{sub 9} cluster deposited on titania that the ligands react with the titania substrate. Based on analysis using the singular value decomposition algorithm, the series of MIE spectra can be described as a linear combination ofmore » 3 base spectra that are assigned to the spectra of the substrate, the phosphine ligands on the substrate, and the Au clusters anchored to titania after removal of the ligands. On silica, the Au clusters show significant agglomeration after heat treatment and no interaction of the ligands with the substrate can be identified.« less

UMTRA project water sampling and analysis plan, Durango, Colorado

DOE Office of Scientific and Technical Information (OSTI.GOV)

Not Available

1994-01-01

Surface remedial action has been completed at the Uranium Mill Tailings Remedial Action Project in Durango, Colorado. Contaminated soil and debris have been removed from the former processing site and placed in the Bodo Canyon disposal cell. Ground water at the former uranium mill/tailings site and raffinate pond area has been contaminated by the former milling operations. The ground water at the disposal site was not impacted by the former milling operations at the time of the cell`s construction. Activities for fiscal 1994 involve ground water sampling and site characterization of the disposal site.

Spatial distribution of pollen grains and spores in surface sediments of Guanabara Bay, Rio de Janeiro, Brazil.

PubMed

Barreto, Cintia F; Vilela, Claudia G; Baptista-Neto, José A; Barth, Ortrud M

2012-09-01

Aiming to investigate the deposition of pollen grains and spores in Guanabara Bay, Rio de Janeiro State, 61 surface sediment samples were analyzed. The results showed that the current deposition of palynomorphs in surface sediments of Guanabara Bay represents the regional vegetation of this hydrographic basin. The differential distribution of palynomorphs followed a pattern influenced by bathymetry, tidal currents speed, discharge of numerous rivers, and by human activity. The dominance of representatives of Field Vegetation reflects the changes of the original flora caused by intense human activities in the region. The continued presence and richness of pollen types of rain forest in the samples indicates that their source area might be the vegetation from riparian border of rivers in the western sector of the Bay, where the mangrove vegetation is being preserved. The large amount of damaged palynomorphs may be related to abrasion that occurs during river transport, indicating removal or reworking from their areas of origin.

An Investigation of the Wear on Silicon Surface at High Humidity.

PubMed

Wang, Xiaodong; Guo, Jian; Xu, Lin; Cheng, Guanggui; Qian, Linmao

2018-06-16

Using an atomic force microscope (AFM), the wear of monocrystalline silicon (covered by a native oxide layer) at high humidity was investigated. The experimental results indicated that tribochemistry played an important role in the wear of the silicon at different relative humidity levels (RH = 60%, 90%). Since the tribochemical reactions were facilitated at 60% RH, the wear of silicon was serious and the friction force was around 1.58 μN under the given conditions. However, the tribochemical reactions were restrained when the wear pair was conducted at high humidity. As a result, the wear of silicon was very slight and the friction force decreased to 0.85 μN at 90% RH. The slight wear of silicon at high humidity was characterized by etching tests. It was demonstrated that the silicon sample surface was partly damaged and the native oxide layer on silicon sample surface had not been totally removed during the wear process. These results may help us optimize the tribological design of dynamic microelectromechanical systems working in humid conditions.

Sample processing approach for detection of ricin in surface samples.

PubMed

Kane, Staci; Shah, Sanjiv; Erler, Anne Marie; Alfaro, Teneile

2017-12-01

With several ricin contamination incidents reported over the past decade, rapid and accurate methods are needed for environmental sample analysis, especially after decontamination. A sample processing method was developed for common surface sampling devices to improve the limit of detection and avoid false negative/positive results for ricin analysis. Potential assay interferents from the sample matrix (bleach residue, sample material, wetting buffer), including reference dust, were tested using a Time-Resolved Fluorescence (TRF) immunoassay. Test results suggested that the sample matrix did not cause the elevated background fluorescence sometimes observed when analyzing post-bleach decontamination samples from ricin incidents. Furthermore, sample particulates (80mg/mL Arizona Test Dust) did not enhance background fluorescence or interfere with ricin detection by TRF. These results suggested that high background fluorescence in this immunoassay could be due to labeled antibody quality and/or quantity issues. Centrifugal ultrafiltration devices were evaluated for ricin concentration as a part of sample processing. Up to 30-fold concentration of ricin was observed by the devices, which serve to remove soluble interferents and could function as the front-end sample processing step to other ricin analytical methods. The procedure has the potential to be used with a broader range of environmental sample types and with other potential interferences and to be followed by other ricin analytical methods, although additional verification studies would be required. Published by Elsevier B.V.

Performance of vertical up-flow constructed wetlands on swine wastewater containing tetracyclines and tet genes.

PubMed

Huang, Xu; Liu, Chaoxiang; Li, Ke; Su, Jianqiang; Zhu, Gefu; Liu, Lin

2015-03-01

Antibiotics and antibiotic resistance genes (ARGs) pollution in animal feeding farms received more public attention recently. Livestock wastewater contains large quantities of antibiotics and ARGs even after traditional lagoon treatment. In this study, the performance of vertical up-flow constructed wetlands (VUF-CWs) on swine wastewater containing tetracycline compounds (TCs) and tet genes was evaluated based on three aspects, TCs and tet genes removal efficiencies, residual TCs and tet genes in soils and plants, and the effect of TCs accumulation on nutrients removal and tet genes development. High removal efficiencies (69.0-99.9%) were achieved for oxytetracycline (OTC), tetracycline (TC) and chlortetracycline (CTC) with or without OTC spiked in the influent additionally. TCs concentrations in surface soils increased at first two sampling periods and then decreased after plants were harvested. Satisfactory nutrients removal efficiencies were also obtained, but TN and NH4-N removal efficiencies were significantly negative correlated with total concentration of TCs (∑TCs) in the soils (p < 0.01). The absolute abundances of all the target genes (tetO, tetM, tetW, tetA, tetX and intI1) were greatly reduced with their log units ranging from 0.26 to 3.3. However, the relative abundances of tetO, tetM and tetX in some effluent samples were significantly higher than those in the influent (p < 0.05). The relative abundances of tet genes except for tetO were significantly correlated with ∑TCs in the soils (p < 0.05). In summary, the proposed VUF-CWs are effective alternative for the removal of TCs and tet genes. But it is of great importance to prevent large accumulation of TCs in the soils. Copyright © 2014 Elsevier Ltd. All rights reserved.

Surface active complexes formed between keratin polypeptides and ionic surfactants.

PubMed

Pan, Fang; Lu, Zhiming; Tucker, Ian; Hosking, Sarah; Petkov, Jordan; Lu, Jian R

2016-12-15

Keratins are a group of important proteins in skin and hair and as biomaterials they can provide desirable properties such as strength, biocompatibility, and moisture regaining and retaining. The aim of this work is to develop water-soluble keratin polypeptides from sheep wool and then explore how their surface adsorption behaves with and without surfactants. Successful preparation of keratin samples was demonstrated by identification of the key components from gel electrophoresis and the reproducible production of gram scale samples with and without SDS (sodium dodecylsulphate) during wool fibre dissolution. SDS micelles could reduce the formation of disulphide bonds between keratins during extraction, reducing inter-molecular crosslinking and improving keratin polypeptide solubility. However, Zeta potential measurements of the two polypeptide batches demonstrated almost identical pH dependent surface charge distributions with isoelectric points around pH 3.5, showing complete removal of SDS during purification by dialysis. In spite of different solubility from the two batches of keratin samples prepared, very similar adsorption and aggregation behavior was revealed from surface tension measurements and dynamic light scattering. Mixing of keratin polypeptides with SDS and C 12 TAB (dodecyltrimethylammonium bromide) led to the formation of keratin-surfactant complexes that were substantially more effective at reducing surface tension than the polypeptides alone, showing great promise in the delivery of keratin polypeptides via the surface active complexes. Neutron reflection measurements revealed the coexistence of surfactant and keratin polypeptides at the interface, thus providing the structural support to the observed surface tension changes associated with the formation of the surface active complexes. Copyright © 2016. Published by Elsevier Inc.

Selective removal of dental composite using a rapidly scanned carbon dioxide laser

NASA Astrophysics Data System (ADS)

Chan, Kenneth H.; Fried, Daniel

2011-03-01

Dental restorative materials are color matched to the tooth and are difficult to remove by mechanical means without excessive removal or damage to peripheral enamel and dentin. Lasers are ideally suited for selective ablation to minimize healthy tissue loss when replacing existing restorations, sealants or removing composite adhesives such as residual composite left after debonding orthodontic brackets. In this study a carbon dioxide laser operating at high laser pulse repetition rates integrated with a galvanometer based scanner was used to selectively remove composite from tooth surfaces. A diode array spectrometer was used to measure the plume emission after each laser pulse and determine if the ablated material was tooth mineral or composite. The composite was placed on tooth buccal and occlusal surfaces and the carbon dioxide laser was scanned across the surface to selectively remove the composite without excessive damage to the underlying sound enamel. The residual composite and the damage to the underlying enamel was evaluated using optical microscopy. The laser was able to rapidly remove the composites rapidly from both surfaces with minimal damage to the underlying sound enamel.

Rapid and Selective Removal of Composite From Tooth Surfaces With a 9.3 μm CO2 Laser Using Spectral Feedback

PubMed Central

Chan, Kenneth H.; Hirasuna, Krista; Fried, Daniel

2015-01-01

Objective Dental composite restorative materials are color matched to the tooth and are difficult to remove by mechanical means without excessive removal or damage to peripheral enamel and dentin. Lasers are ideally suited for selective ablation to minimize healthy tissue loss when replacing existing restorations, sealants, or removing composite adhesives such as residual composite left after debonding orthodontic brackets. Methods In this study, a carbon dioxide laser operating at 9.3-μm with a pulse duration of 10–20-microsecond and a pulse repetition rate of ~200 Hz was integrated with a galvanometer based scanner and used to selectively remove composite from tooth surfaces. Spectra of the plume emission were acquired after each laser pulse and used to differentiate between the ablation of dental enamel or composite. Microthermocouples were used to monitor the temperature rise in the pulp chamber during composite removal. The composite was placed on tooth buccal and occlusal surfaces and the carbon dioxide laser beam was scanned across the surface to selectively remove the composite without excessive damage to the underlying sound enamel. The residual composite and the damage to the underlying enamel was evaluated using optical microscopy. Results The laser was able to rapidly remove composite from tooth buccal and occlusal surfaces with minimal damage to the underlying sound enamel and without excessive heat accumulation in the tooth. Conclusion This study demonstrated that composite can be selectively removed from tooth surfaces at clinically relevant rates using a CO2 laser operating at 9.3-μm with high pulse repetition rates with minimal heat deposition and damage to the underlying enamel. PMID:21956630

The effect of different surface materials on runoff quality in permeable pavement systems.

PubMed

Li, Haiyan; Li, Zhifei; Zhang, Xiaoran; Li, Zhuorong; Liu, Dongqing; Li, Tanghu; Zhang, Ziyang

2017-09-01

To investigate the effect of different permeable pavement surface materials on the removal of pollutants from urban storm-runoff, six commonly surface materials (porous asphalt, porous concrete, cement brick, ceramic brick, sand base brick, and shale brick) were selected in this study and the research was carried out by column experiments. Except the concentrations of total suspended solids (TSS), chemical oxygen demand (COD), ammonia nitrogen (NH 4 -N), nitrate nitrogen (NO 3 -N), total nitrogen (TN), and total phosphorus (TP) in the influent and effluent that were measured, the removal mechanism of pollutants was discussed further. The results indicate that the surface materials influence the removal efficiency of pollutants greatly and have different effects on certain pollutant. Furthermore, the physical interception and adsorption would be the main mechanism for the removal of pollutants from runoff. For example, for all surface materials, the average removal efficiency of TSS is nearly about 90.0% because of physical interception. Due to the amount of iron oxide, the removal efficiency of COD, NO 3 -N, and TN of shale brick was 88.2, 35.1, and 17.5%, respectively. NH 4 -N and TN can be easily removed by porous asphalt due to the high content of organic matter. By lacking of useful adsorption sites, all the surface materials had little effect on the removal of TP from runoff. This research could offer useful guidelines for the better design of permeable pavement system and promote the insight into the removal mechanism of pollutants in permeable pavement system. Graphical abstract Different types of materials for the different types of pollutants in the runoff purification capacity were significantly different, overall, shale brick and porous asphalt Shale bricks and porous asphalt have a better purification effect according to the six kinds of materials.

Rapid and selective removal of composite from tooth surfaces with a 9.3 µm CO2 laser using spectral feedback.

PubMed

Chan, Kenneth H; Hirasuna, Krista; Fried, Daniel

2011-09-01

Dental composite restorative materials are color matched to the tooth and are difficult to remove by mechanical means without excessive removal or damage to peripheral enamel and dentin. Lasers are ideally suited for selective ablation to minimize healthy tissue loss when replacing existing restorations, sealants, or removing composite adhesives such as residual composite left after debonding orthodontic brackets. In this study, a carbon dioxide laser operating at 9.3-µm with a pulse duration of 10-20-microsecond and a pulse repetition rate of ∼200 Hz was integrated with a galvanometer based scanner and used to selectively remove composite from tooth surfaces. Spectra of the plume emission were acquired after each laser pulse and used to differentiate between the ablation of dental enamel or composite. Microthermocouples were used to monitor the temperature rise in the pulp chamber during composite removal. The composite was placed on tooth buccal and occlusal surfaces and the carbon dioxide laser beam was scanned across the surface to selectively remove the composite without excessive damage to the underlying sound enamel. The residual composite and the damage to the underlying enamel was evaluated using optical microscopy. The laser was able to rapidly remove composite from tooth buccal and occlusal surfaces with minimal damage to the underlying sound enamel and without excessive heat accumulation in the tooth. This study demonstrated that composite can be selectively removed from tooth surfaces at clinically relevant rates using a CO(2) laser operating at 9.3-µm with high pulse repetition rates with minimal heat deposition and damage to the underlying enamel. Copyright © 2011 Wiley-Liss, Inc.

Surface analysis of graphite fiber reinforced polyimide composites

NASA Technical Reports Server (NTRS)

Messick, D. L.; Progar, D. J.; Wightman, J. P.

1983-01-01

Several techniques have been used to establish the effect of different surface pretreatments on graphite-polyimide composites. Composites were prepared from Celion 6000 graphite fibers and the polyimide LARC-160. Pretreatments included mechanical abrasion, chemical etching and light irradiation. Scanning electron microscopy (SEM) and X-ray photoelectron spectroscopy (XPS) were used in the analysis. Contact angle of five different liquids of varying surface tensions were measured on the composites. SEM results showed polymer-rich peaks and polymer-poor valleys conforming to the pattern of the release cloth used durng fabrication. Mechanically treated and light irradiated samples showed varying degrees of polymer peak removal, with some degradation down to the graphite fibers. Minimal changes in surface topography were observed on concentrations of surface fluorine even after pretreatment. The light irradiation pretreatment was most effective at reducing surface fluorine concentrations whereas chemical pretreatment was the least effective. Critical surface tensions correlated directly with the surface fluorine to carbon ratios as calculated from XPS.

Bioactivity of Ti-6Al-4V alloy implants treated with ibandronate after the formation of the nanotube TiO2 layer.

PubMed

Moon, So-Hee; Lee, Seung-Jae; Park, Il-Song; Lee, Min-Ho; Soh, Yun-Jo; Bae, Tae-Sung; Kim, Hyung-Seop

2012-11-01

Nanostructure surface of titanium implants treated with anodic oxidation, heat, and bisphosphonates, has been introduced to improve osseointegration of the implants. However, no information could be found about the efficiency of these approaches on Ti-6Al-4V alloy surfaces. This study examined the drug loading capacity of anodized nanotubular Ti-6Al-4V alloy surfaces in vitro as well as the bone response to surface immobilized bisphosphonates (BPs) on anodized nanotubular Ti-6Al-4V alloy surface in tibiae of rats. Ti-6Al-4V alloy titanium was divided into two groups: (1) control group (nontreated); (2) test group (anodized, heat-, and bisphosphonate-treated group). In vitro, amount of the drug released from the both groups' specimens was examined; all samples were 1 × 2 cm in size. In vivo, the 10 implants were placed inside of tibias of five rats. After 4 weeks, the bone response of the implants was evaluated using a removal torque test, and measuring bone contact and bone area. In addition, the surfaces of the extracted implants were observed by FE-SEM and EDS. In vitro, the drug loading capacity of the Ti-6Al-4V alloy surfaces was enhanced by anodizing surface modification. The values of the removal torque, bone contact, and bone area were significantly higher in the test group (p < 0.05). Furthermore, according to the EDS analysis, the amounts of Ca and P on the surface of the extracted implants were higher in the test group. Within the limits of this experiment, results of this research demonstrated that bisphosphonate-treated Ti-6Al-4V alloy implants with nanotubular surfaces have positive effects in bone-to-implant contact. Copyright © 2012 Wiley Periodicals, Inc.

Surface studies of low molecular weight photolysis products from UV-ozone oxidised polystyrene

NASA Astrophysics Data System (ADS)

Davidson, M. R.; Mitchell, S. A.; Bradley, R. H.

2005-05-01

The production of low molecular weight oxidised material during UV-ozone treatment of polystyrene has been studied by XPS, GC-MS, FTIR and UV/visible spectroscopy. XPS analysis of the oxidised polystyrene surfaces before and after washing with water or methanol indicates that the removal of oxidation products and the surface that remains after washing is strongly dependent on the choice of solvent. Methanol washing removes a greater proportion of the more highly oxidised carbonyl and carboxyl groups resulting in a surface with a lower oxygen content than that remaining after water washing. Extended exposure to UV-ozone treatment reveals a two-stage oxidation process with mono-substituted benzene rings such as benzaldehyde, acetophenone and benzoic acid being produced at exposure times less than 15 min. Compounds, more typical of those formed via dehydration reactions of existing oxidised species, are produced at longer exposure times. UV-visible spectroscopy and Fourier transform infrared spectroscopy also confirm the presence of carboxylic acid, aromatic ketones and esters. Measurements of water contact angle on a 10 min treated surface reveals that methanol washing produces a more hydrophilic surface than water washing, the resulting water contact angles being 47° and 62° respectively. Ageing of methanol washed surfaces for 24 h leads to a recovery of the water contact angle back to 62° which suggests some form of post-washing surface relaxation process. Since XPS analyses show no increase in the oxygen concentration of the methanol washed surfaces after a 24 h ageing period, the increase in contact angle found with ageing is attributed to the reorientation of very near-surface functional groups i.e. within the XPS sampling depth.

ZERODUR - bending strength: review of achievements

NASA Astrophysics Data System (ADS)

Hartmann, Peter

2017-08-01

Increased demand for using the glass ceramic ZERODUR® with high mechanical loads called for strength data based on larger statistical samples. Design calculations for failure probability target value below 1: 100 000 cannot be made reliable with parameters derived from 20 specimen samples. The data now available for a variety of surface conditions, ground with different grain sizes and acid etched for full micro crack removal, allow stresses by factors four to ten times higher than before. The large sample revealed that breakage stresses of ground surfaces follow the three parameter Weibull distribution instead of the two parameter version. This is more reasonable considering that the micro cracks of such surfaces have a maximum depth which is reflected in the existence of a threshold breakage stress below which breakage probability is zero. This minimum strength allows calculating minimum lifetimes. Fatigue under load can be taken into account by using the stress corrosion coefficient for the actual environmental humidity. For fully etched surfaces Weibull statistics fails. The precondition of the Weibull distribution, the existence of one unique failure mechanism, is not given anymore. ZERODUR® with fully etched surfaces free from damages introduced after etching endures easily 100 MPa tensile stress. The possibility to use ZERODUR® for combined high precision and high stress application was confirmed by the successful launch and continuing operation of LISA Pathfinder the precursor experiment for the gravitational wave antenna satellite array eLISA.

Modification of tooth and enamel characteristics following the Er,Cr:YSGG laser treatment

NASA Astrophysics Data System (ADS)

Suhaimi, Fatanah M.; Aziz, N. Afifah; Jaafar, M. S.; Azizan, Nur Syazana; Zali, Nurulakma; Razak, N. A. Abd

2016-12-01

Lasers have been widely used in the dental field to treat a number of applications in dentistry. The main objective of this study is to analyse the modification of tooth composition following the Er,Cr:YSGG laser procedure. In this study, human premolar teeth were collected and prepared. The samples were sectioned and molded. 3M Unitek Transbond™ Plus Self Etching Primer adhesive materials were applied to the tooth surface. Er,Cr:YSGG laser with a wavelength of 2790 nm was used in this study to remove the adhesive materials on the enamel surface. The irradiation process was done with four different output powers that are 0.25, 0.5, 0.75, and 1.0 W. The change of tooth characteristics was analysed by observing the morphology of the enamel surface and the elemental composition usinga Field Emission Scanning Electron Microscope (FESEM) and Electron Dispersive X-ray Spectrometer (EDX). Calcium (Ca), phosphorus (P), sodium (Na), oxygen (O), and carbon (C) were the elementsidentified by EDX in the samples. Additionally, oxygen was the most abundant element found in the sample. The level of oxygen composition decreased after laser irradiation while the carbon element increased. Another element, calcium was found to be decreasing due to the process of applying adhesive materials on the enamel surface.

Surface properties of sprayed and electrodeposited ZnO rod layers

NASA Astrophysics Data System (ADS)

Gromyko, I.; Krunks, M.; Dedova, T.; Katerski, A.; Klauson, D.; Oja Acik, I.

2017-05-01

Herein we present a comparative study on as-deposited, two-month-stored, and heat-treated ZnO rods obtained by spray pyrolysis (SP) at 550 °C, and electrodeposition (ED) at 80 °C. The aim of the study is to establish the reason for different behaviour of wettability and photocatalytic activity (PA) of SP and ED rods. Samples were studied using XPS, SEM, XRD, Raman, contact angle (CA) measurements and photocatalytic oxidation of doxycycline. Wettability and PA are mainly controlled by surface composition rather than by morphology. The relative amount of hydroxyl groups on the surface of as-deposited ED rods is four times higher compared to as-deposited SP rods. Opposite to SP rods, ED rods contain oxygen vacancy defects (Vo). Therefore, as-deposited ED rods are superhydrophilic (CA ∼ 3°) and show highest PA among studied samples, being three times higher compared to SP rods (removing of 75% of doxycycline after 30 min). It was revealed that as-deposited ED rods are inclined to faster contamination. The amount of Cdbnd C groups on the surface of aged ED rods is six times higher compared to aged SP rods. Stored ED samples become hydrophobic (CA ∼ 120°) and PA decreases sharply while SP rods remain hydrophilic (CA ∼ 50°), being more resistive to the contamination.

Reconstruction of perfect ZnO nanowires facets with high optical quality

NASA Astrophysics Data System (ADS)

Zehani, E.; Hassani, S.; Lusson, A.; Vigneron, J.; Etcheberry, A.; Galtier, P.; Sallet, V.

2017-07-01

ZnO nanowires were grown on sapphire substrates using metalorganic chemical vapor deposition. The samples were subsequently annealed under zinc pressure in a vacuum-sealed ampoule, at temperature ranging from 500 to 800 °C. The originality and the main motivation to provide a zinc-rich atmosphere were to prevent the out-diffusion of zinc from the nanowires. In doing so, the perfect structural properties and the morphology of the nanowires are kept. Interestingly, photoluminescence experiments performed on nanowires annealed in a narrow window of temperature [580-620 °C] show a spectacular improvement of the optical quality, as transitions commonly observable in high quality bulk samples are found. In addition, the intensity of the so-called "surface excitons" (SX) is strongly decreased. To accurately investigate the chemical modifications of the surface, XPS experiments were carried out and show that zinc hydroxide species and/or Zn(OH)2 sublayer were partially removed from the surface. These results suggest that the annealing process in zinc vapor helps to properly reconstruct the surface of ZnO nanowires, and improves the optical quality of their core. Such a thermal treatment at moderate temperature should be beneficial to nanodevices involving surface reaction, e.g. gas sensors.

Aeolian removal of dust from radiator surfaces on Mars

NASA Technical Reports Server (NTRS)

Gaier, James R.; Perez-Davis, Marla E.; Rutledge, Sharon K.; Hotes, Deborah

1990-01-01

Simulated radiator surfaces made of arc-textured Cu and Nb-1 percent-Zr and ion beam textured graphite and C-C composite were fabricated and their integrated spectral emittance characterized from 300 to 3000 K. A thin layer of aluminum oxide, basalt, or iron (III) oxide dust was then deposited on them, and they were subjected to low pressure winds in the Martian Surface Wind Tunnel. It was found that dust deposited on simulated radiator surfaces may or may not seriously lower their integrated spectral emittance, depending upon the characteristics of the dust. With Al2O3 there is no appreciable degradation of emittance on a dusted sample, with basaltic dust there is a 10 to 20 percent degradation, and with Fe2O3 a 20 to 40 percent degradation. It was also found that very high winds on dusted highly textured surfaces can result in their abrasion. Degradation in emittance due to abrasion was found to vary with radiator material. Arc-textured Cu and Nb-1 percent Zr was found to be more susceptible to emittance degradation than graphite or C-C composite. The most abrasion occurred at low angles, peaking at the 22.5 deg test samples.

Enhanced Bone Bonding to Nanotextured Implant Surfaces at a Short Healing Period: A Biomechanical Tensile Testing in the Rat Femur.

PubMed

Coelho, Paulo G; Zavanelli, Ricardo A; Salles, Marcos B; Yeniyol, Sinem; Tovar, Nick; Jimbo, Ryo

2016-06-01

To compare the bone bonding capabilities of 2 different surface treatments at an early healing period. Titanium alloy (Ti6Al4V) custom-made rectangular plates (1.4 × 2.4 × 4 mm) were either dual acid etched (Ti6Al4V-DAE) or DAE/nanotextured blasted (Ti6Al4V-NTB). Implants were placed in the distal femurs of 10 Wistar rats and were allowed to heal for 9 days. After euthanasia, the bone immediately proximal and distal to the implant was removed to test the bone bonding force with a universal testing machine. Ultrastructure of the bone/implant interface was assessed by scanning electron microscopy. Ti6Al4V-NTB samples exhibited significantly greater bond strength than Ti6Al4V-DAE samples. Morphologically, the Ti6Al4V-NTB surfaces presented intimate interaction with bone, whereas little interaction between the Ti6Al4V-DAE surface and bone was observed. The results of this study indicated a significant increase in bone bonding for the DAE/nanotextured blasted surface, which is suggested to be the outcome of the nanotexturing.

Study of microtip-based extraction and purification of DNA from human samples for portable devices

NASA Astrophysics Data System (ADS)

Fotouhi, Gareth

DNA sample preparation is essential for genetic analysis. However, rapid and easy-to-use methods are a major challenge to obtaining genetic information. Furthermore, DNA sample preparation technology must follow the growing need for point-of-care (POC) diagnostics. The current use of centrifuges, large robots, and laboratory-intensive protocols has to be minimized to meet the global challenge of limited access healthcare by bringing the lab to patients through POC devices. To address these challenges, a novel extraction method of genomic DNA from human samples is presented by using heat-cured polyethyleneimine-coated microtips generating a high electric field. The microtip extraction method is based on recent work using an electric field and capillary action integrated into an automated device. The main challenges to the method are: (1) to obtain a stable microtip surface for the controlled capture and release of DNA and (2) to improve the recovery of DNA from samples with a high concentration of inhibitors, such as human samples. The present study addresses these challenges by investigating the heat curing of polyethyleneimine (PEI) coated on the surface of the microtip. Heat-cured PEI-coated microtips are shown to control the capture and release of DNA. Protocols are developed for the extraction and purification of DNA from human samples. Heat-cured PEI-coated microtip methods of DNA sample preparation are used to extract genomic DNA from human samples. It is discovered through experiment that heat curing of a PEI layer on a gold-coated surface below 150°C could inhibit the signal of polymerase chain reaction (PCR). Below 150°C, the PEI layer is not completely cured and dissolved off the gold-coated surface. Dissolved PEI binds with DNA to inhibit PCR. Heat curing of a PEI layer above 150°C on a gold-coated surface prevents inhibition to PCR and gel electrophoresis. In comparison to gold-coated microtips, the 225°C-cured PEI-coated microtips improve the recovery of DNA to 45% efficiency. Furthermore, the 225°C-cured PEI-coated microtips recover more DNA than gold-coated microtips when the surface is washed. Heat-cured (225°C) PEI-coated microtips are used for the recovery of human genomic DNA from whole blood. A washing protocol is developed to remove inhibiting particles bound to the PEI-coated microtip surface after DNA extraction. From 1.25 muL of whole blood, an average of 1.83 ng of human genomic DNA is captured, purified, and released using a 225°C-cured PEI-coated microtip in less than 30 minutes. The extracted DNA is profiled by short tandem repeat analysis (STR). For forensic and medical applications, genomic DNA is extracted from dried samples using heat-cured PEI-coated microtips that are integrated into an automated device. DNA extraction from dried samples is critical for forensics. The use of dried samples in the medical field is increasing because dried samples are convenient for storage, biosafety, and contamination. The main challenge is the time required to properly extract DNA in a purified form. Typically, a 1 hour incubation period is required to complete this process. Overnight incubation is sometimes necessary. To address this challenge, a pre-extraction washing step is investigated to remove inhibiting particles from dried blood spots (DBS) before DNA is released from dried form into solution for microtip extraction. The developed protocol is expanded to extract DNA from a variety of dried samples including nasal swabs, buccal swabs, and other forensic samples. In comparison to a commercial kit, the microtip-based extraction reduced the processing time from 1.5 hours to 30 minutes or less with an equivalent concentration of extracted DNA from dried blood spots. The developed assay will benefit genetic studies on newborn screening, forensic investigation, and POC diagnostics.

Evaluation of DSS-14 pedestal-review of top surface repair procedures

NASA Technical Reports Server (NTRS)

Oesterle, R. G.; Musser, D. W.; Salse, E. A. B.

1983-01-01

Proposed repair procedures for the top surface of the pedestal supporting the hydrostatic bearing runner for the 64m Antenna are presented. These procedures included: (1) removal of existing grout and concrete to approximately 8 in. below original concrete surface using a presplitting technique with expansive cement followed by secondary breaking; (2) preparation of exposed concrete surface including an epoxy bonding agent; and (3) replacement of material removed with 8 in. of new concrete surface including an epoxy bonding agent; and (4) replacement of material removed with 8 in. of new concrete and 4 in. of new grout.

Investigation into the effects of surface stripping ZnO nanosheets.

PubMed

Barnett, Chris J; Jackson, Georgina; Jones, Daniel R; Lewis, Aled R; Welsby, Kathryn; Evans, Jon E; McGettrick, James D; Watson, Trystan; Maffeis, Thierry G G; Dunstan, Peter R; Barron, Andrew R; Cobley, Richard J

2018-04-20

ZnO nanosheets are polycrystalline nanostructures that are used in devices including solar cells and gas sensors. However, for efficient and reproducible device operation and contact behaviour the conductivity characteristics must be controlled and surface contaminants removed. Here we use low doses of argon bombardment to remove surface contamination and make reproducible lower resistance contacts. Higher doses strip the surface of the nanosheets altering the contact type from near-ohmic to rectifying by removing the donor-type defects, which photoluminescence shows to be concentrated in the near-surface. Controlled doses of argon treatments allow nanosheets to be customised for device formation.

Investigation into the effects of surface stripping ZnO nanosheets

NASA Astrophysics Data System (ADS)

Barnett, Chris J.; Jackson, Georgina; Jones, Daniel R.; Lewis, Aled R.; Welsby, Kathryn; Evans, Jon E.; McGettrick, James D.; Watson, Trystan; Maffeis, Thierry G. G.; Dunstan, Peter R.; Barron, Andrew R.; Cobley, Richard J.

2018-04-01

ZnO nanosheets are polycrystalline nanostructures that are used in devices including solar cells and gas sensors. However, for efficient and reproducible device operation and contact behaviour the conductivity characteristics must be controlled and surface contaminants removed. Here we use low doses of argon bombardment to remove surface contamination and make reproducible lower resistance contacts. Higher doses strip the surface of the nanosheets altering the contact type from near-ohmic to rectifying by removing the donor-type defects, which photoluminescence shows to be concentrated in the near-surface. Controlled doses of argon treatments allow nanosheets to be customised for device formation.

Magnetism on a Boron-doped Si(111)-√ 3 × √ 3 Surface

NASA Astrophysics Data System (ADS)

Moon, Chang-Youn; Eom, Daejin; Koo, Ja-Yong

2018-03-01

We perform first-principles calculation to investigate the possible magnetism on the Si(111)-√ 3 × √ 3 surface, which is stabilized for highly boron-doped samples. When the silicon adatom on top of a boron atom is removed to form a defect structure, three silicon dangling bonds are exposed, generating half-filled doubly degenerate energy levels in the band gap, which stabilizes a local magnetic moment of 2 μ B . When many such defect structures are adjacent to one another, they are found to align antiferromagnetically. However, we demonstrate that the ferromagnetism can be stabilized by adjusting the number of electrons in the defects, suggesting a possibility towards spintronic applications for this unique silicon surface structure.

Investigations into the mechanism of material removal and surface modification at atomic scale on stainless steel using molecular dynamics simulation

NASA Astrophysics Data System (ADS)

Ranjan, Prabhat; Balasubramaniam, R.; Jain, V. K.

2018-06-01

A molecular dynamics simulation (MDS) has been carried out to investigate the material removal phenomenon of chemo-mechanical magnetorheological finishing (CMMRF) process. To understand the role of chemical assisted mechanical abrasion in CMMRF process, material removal phenomenon is subdivided into three different stages. In the first stage, new atomic bonds viz. Fe-O-Si is created on the surface of the workpiece (stainless steel). The second stage deals with the rupture of parent bonds like Fe-Fe on the workpiece. In the final stage, removal of material from the surface in the form of dislodged debris (cluster of atoms) takes place. Effects of process parameters like abrasive particles, depth of penetration and initial surface condition on finishing force, potential energy (towards secondary phenomenon such as chemical instability of the finished surface) and material removal at atomic scale have been investigated. It was observed that the type of abrasive particle is one of the important parameters to produce atomically smooth surface. Experiments were also conducted as per the MDS to generate defect-free and sub-nanometre-level finished surface (Ra value better than 0.2 nm). The experimental results reasonably agree well with the simulation results.

Model of the material removal function and an experimental study on a magnetorheological finishing process using a small ball-end permanent-magnet polishing head.

PubMed

Chen, Mingjun; Liu, Henan; Cheng, Jian; Yu, Bo; Fang, Zhen

2017-07-01

In order to achieve the deterministic finishing of optical components with concave surfaces of a curvature radius less than 10 mm, a novel magnetorheological finishing (MRF) process using a small ball-end permanent-magnet polishing head with a diameter of 4 mm is introduced. The characteristics of material removal in the proposed MRF process are studied. The model of the material removal function for the proposed MRF process is established based on the three-dimensional hydrodynamics analysis and Preston's equation. The shear stress on the workpiece surface is calculated by means of resolving the presented mathematical model using a numerical solution method. The analysis result reveals that the material removal in the proposed MRF process shows a positive dependence on shear stress. Experimental research is conducted to investigate the effect of processing parameters on the material removal rate and improve the surface accuracy of a typical rotational symmetrical optical component. The experimental results show that the surface accuracy of the finished component of K9 glass material has been improved to 0.14 μm (PV) from the initial 0.8 μm (PV), and the finished surface roughness Ra is 0.0024 μm. It indicates that the proposed MRF process can be used to achieve the deterministic removal of surface material and perform the nanofinishing of small curvature radius concave surfaces.

Ni-Doping Effects on Oxygen Removal from an Orthorhombic Mo 2C (001) Surface: A Density Functional Theory Study

DOE Office of Scientific and Technical Information (OSTI.GOV)

Zhou, Mingxia; Cheng, Lei; Choi, Jae-Soon

Density functional theory (DFT) calculations were used in this paper to investigate the effect of Ni dopants on the removal of chemisorbed oxygen (O*) from the Mo-terminated (T Mo) and C-terminated (T C) Mo 2C(001) surfaces. The removal of adsorbed oxygen from the catalytic site is essential to maintain the long-term activity and selectivity of the carbide catalysts in the deoxygenation process related to bio-oil stabilization and upgrading. In this contribution, the computed reaction energetics and reaction barriers of O* removal were compared among undoped and Ni-doped Mo 2C(001) surfaces. The DFT calculations indicate that selected Ni-doped surfaces such asmore » Ni adsorbed on T Mo and T C Mo 2C(001) surfaces enable weaker binding of important reactive intermediates (O*, OH*) compared to the undoped counterparts, which is beneficial for the O* removal from the catalyst surface. This study thus confirms the promoting effect of the Ni dopant on O* removal reaction on the T Mo Mo 2C(001) and T C Mo 2C(001) surfaces. Finally, this computational prediction has been confirmed by the temperature-programmed reduction profiles of Mo 2C and Ni-doped Mo 2C catalysts, which had been passivated and stored in an oxygen environment.« less

Ni-Doping Effects on Oxygen Removal from an Orthorhombic Mo 2C (001) Surface: A Density Functional Theory Study

DOE PAGES

Zhou, Mingxia; Cheng, Lei; Choi, Jae-Soon; ...

2017-12-22

Density functional theory (DFT) calculations were used in this paper to investigate the effect of Ni dopants on the removal of chemisorbed oxygen (O*) from the Mo-terminated (T Mo) and C-terminated (T C) Mo 2C(001) surfaces. The removal of adsorbed oxygen from the catalytic site is essential to maintain the long-term activity and selectivity of the carbide catalysts in the deoxygenation process related to bio-oil stabilization and upgrading. In this contribution, the computed reaction energetics and reaction barriers of O* removal were compared among undoped and Ni-doped Mo 2C(001) surfaces. The DFT calculations indicate that selected Ni-doped surfaces such asmore » Ni adsorbed on T Mo and T C Mo 2C(001) surfaces enable weaker binding of important reactive intermediates (O*, OH*) compared to the undoped counterparts, which is beneficial for the O* removal from the catalyst surface. This study thus confirms the promoting effect of the Ni dopant on O* removal reaction on the T Mo Mo 2C(001) and T C Mo 2C(001) surfaces. Finally, this computational prediction has been confirmed by the temperature-programmed reduction profiles of Mo 2C and Ni-doped Mo 2C catalysts, which had been passivated and stored in an oxygen environment.« less

Removal of Microbial Contamination from Surface by Plasma

NASA Astrophysics Data System (ADS)

Feng, Xinxin; Liu, Hongxia; Shen, Zhenxing; Wang, Taobo

2018-01-01

Microbial contamination is closely associated with human and environmental health, they can be tested on food surfaces, medical devices, packing material and so on. In this paper the removal of the microbial contamination from surface using plasma treatment is investigated. The Escherichia coli (E. coli) has been chosen as a bio-indicator enabling to evaluate the effect of plasma assisted microbial inactivation. Oxygen gas was as the working gas. The plasma RF power, plasma exposition time, gas flow and the concentration of organic pollutant were varied in order to see the effect of the plasma treatment on the Gram-negative germ removal. After the treatment, the microbial abatement was evaluated by the standard plate count method. This proved a positive effect of the plasma treatment on Gram-negative germ removal. The kinetics and mathematical model of removal were studied after plasma treatment, and then the removing course of E. coli was analyzed. This work is meaningful for deepening our understanding of the fundamental scientific principles regarding microbial contamination from surface by plasma.

Nitrogen removal in Northern peatlands treating mine wastewaters

NASA Astrophysics Data System (ADS)

Palmer, Katharina; Karlsson, Teemu; Turunen, Kaisa; Liisa Räisänen, Marja; Backnäs, Soile

2015-04-01

Natural peatlands can be used as passive purification systems for mine wastewaters. These treatment peatlands are well-suited for passive water treatment as they delay the flow of water, and provide a large filtration network with many adsorptive surfaces on plant roots or soil particles. They have been shown to remove efficiently harmful metals and metalloids from mine waters due to variety of chemical, physical and biological processes such as adsorption, precipitation, sedimentation, oxidation and reduction reactions, as well as plant uptake. Many factors affect the removal efficiency such as inflow water quality, wetland hydrology, system pH, redox potential and temperature, the nature of the predominating purification processes, and the presence of other components such as salts. However, less attention has been paid to nitrogen (N) removal in peatlands. Thus, this study aimed to assess the efficiency of N removal and seasonal variation in the removal rate in two treatment peatlands treating mine dewatering waters and process effluent waters. Water sampling from treatment peatland inflow and outflow waters as well as pore waters in peatland were conducted multiple times during 2012-2014. Water samples were analysed for total N, nitrate-N and ammonium-N. Additionally, an YSI EXO2 device was used for continuous nitrate monitoring of waters discharged from treatment peatlands to the recipient river during summer 2014. The results showed that the oxic conditions in upper peat layer and microbial activity in treatment peatlands allowed the efficient oxidation of ammonium-N to nitrite-N and further to nitrate-N during summer time. However, the slow denitrification rate restricts the N removal as not all of the nitrate produced during nitrification is denitrified. In summer time, the removal rate of total N varied between 30-99 % being highest in late summer. N removal was clearly higher for treatment peatland treating process effluent waters than for peatland treating dewatering waters probably due to more oxidizing conditions. During winter time there is not enough microbial activity to maintain oxidation of ammonium-N to nitrate-N. However, almost 20 % of N may be removed during winter season due to nitrate denitrification.

137Cs Results and Interpretation of Cesium Soil Data on the Upper Fortymile Wash Alluvial Fan, Amargosa Valley, Nevada.

NASA Astrophysics Data System (ADS)

Harrington, C.

2004-12-01

Studies using 137Cs were used to produce soil Cs profiles and to use them to determine erosion rates on interchannel divides of the Fortymile Wash alluvial fan over the last 50 years. Sample locations whose 137Cs profiles most resemble the reference-sample (stable surface) profiles are located on interchannel divide areas between distributary channels. These profiles are similar to the reference profiles that have low 137Cs values (in the range of 0.02 to 0.08 pCi/g) in the 3 to 6 cm layers. However, the surface layers (1-3 cm depth) typically have values much less than the reference samples from equivalent depths (range from 0.251 to 0.421 pCi/g). The data indicate that many of these interchannel divide areas have had part of the upper layer removed. Interchannel divide areas have the least likelihood of having been submerged during floods over the last fifty years. Thus, the loss of material from these otherwise stable surfaces appears to be due to eolian processes. Erosion of an interchannel divide area with little evidence of recent water movement is most easily explained by eolian removal. Evidence for wind erosion as the predominant process on the interchannel divide areas includes the lack of new or developing stream channels and the presence of modern coppice dunes near channels on interchannel divides. The presence of nearby Big Dune and other eolian deposits provides strong support for eolian erosion and transport. The amount of material removed from the interchannel divide areas was estimated by comparing the 137Cs value of the upper 3 cm layer to that of the reference value and calculating the thickness of the layer that would have to be removed to obtain the lower value. Applying this method across the interchannel divide sample locations indicates 1 to 2 cm of material has been removed from the interchannel divide surfaces in the last 50 years. This results in erosion rates that range from 0.02 to 0.04 cm/yr. These rates are similar to erosion rates of: (a) 0.019 cm/yr predicted to occur on farmland in Amargosa Valley (obtained from BSC 2004 [DIRS 169459], Section 6.4.2 by converting 0.19 kg/m2-yr using ash bulk density of 1 g/cm3; (b) 0.02 cm/yr estimated by the U.S. Department of Agriculture to have occurred on non-cultivated cropland and pastureland in Nevada (obtained from USDA 2000 [160548], Table 11 and calculated using 1 ton/acre-yr x 907 kg/ton x 2.47 x 10-4 acre/m x 0.001 m3/kg [bulk density] x 100 cm/m = 0.02 cm/yr). Overbank deposits on the interchannel divide areas indicative of periodic flooding are uncommon and restricted to narrow strips along the channel banks. The overbank and channel deposit samples have similar 137Cs signatures (the 3 to 6 cm layers and the 6 to 9 cm layers have nearly the same values in the 0.100-0.200 pCi/g range), indicating that the material from each environ was mixed during transport and deposited as a homogeneous sediment. The absence of many overbank deposits along the channel margins today indicates that flows sufficient to form extensive overbank flooding down Fortymile Wash and its distributary channels have not occurred in more than 50 years. Therefore, the channels currently transport most of their sediment load across the fan until it reaches the toe of the fan, where deposition occurs on the broad flats to the south or into the channel of the Amargosa River.

Influence of surface layer removal of shade guide tabs on the measured color by spectrophotometer and spectroradiometer.

PubMed

Kim, Jin-Cheol; Yu, Bin; Lee, Yong-Keun

2008-12-01

To determine the changes in color parameters of Vitapan 3D-Master shade guide tabs by a spectrophotometer (SP) or a spectroradiometer (SR), and by the removal of the surface layer of the tabs that was performed to make a flat measuring surface for the SP color measurement. Color of the shade tabs was measured before and after removing the surface layer of the tabs using SP and SR. Correlations between the color parameters between the original (OR) and the surface layer removed (RM) tabs and between the SP and the SR measurements were determined (alpha=0.05). Based on SP, the lightness, chroma, CIE a* and b* values measured after the surface layer removal were higher than those of the original tabs except a few cases. Based on SR, the chroma and CIE a* and b* values measured after surface layer removal were higher than those of the original tabs except a few cases; however, in case of the lightness, the changes varied by the shade designation. Type of instrument influenced the changes in color parameters based on paired t-test (p<0.05). The color parameters of the OR and RM tabs showed correlations based on both SP and SR measurements (r=0.952-0.997 and p<0.01); however, color difference between the SP-RM and SR-OR tabs was in the range of 18.1-27.0 DeltaE(ab)(*) units (mean: 23.3+/-2.2). When the color of tooth-shaped objects is measured with a spectrophotometer or a spectroradiometer, measurement protocols should be specified because color difference by the surface layer removal and the instrument was high.

Investigation of enteric adenovirus and poliovirus removal by coagulation processes and suitability of bacteriophages MS2 and φX174 as surrogates for those viruses.

PubMed

Shirasaki, N; Matsushita, T; Matsui, Y; Marubayashi, T; Murai, K

2016-09-01

We evaluated the removal of enteric adenovirus (AdV) type 40 and poliovirus (PV) type 1 by coagulation, using water samples from 13 water sources for drinking water treatment plants in Japan. The behaviors of two widely accepted enteric virus surrogates, bacteriophages MS2 and φX174, were compared with the behaviors of AdV and PV. Coagulation with polyaluminum chloride (PACl, basicity 1.5) removed AdV and PV from virus-spiked source waters: the infectious AdV and PV removal ratios evaluated by means of a plaque-forming-unit method were 0.1-1.4-log10 and 0.5-2.4-log10, respectively. A nonsulfated high-basicity PACl (basicity 2.1) removed infectious AdV and PV more efficiently than did other commercially available PACls (basicity 1.5-2.1), alum, and ferric chloride. The MS2 removal ratios tended to be larger than those of AdV and PV, partly because of differences in the hydrophobicities of the virus particles and the sensitivity of the virus to the virucidal activity of PACl; the differences in removal ratios were not due to differences in the surface charges of the virus particles. MS2, which was more hydrophobic than the other viruses, was inactivated during coagulation with PACl. Therefore, MS2 does not appear to be an appropriate surrogate for AdV and PV during coagulation. In contrast, because φX174, like AdV and PV, was not inactivated during coagulation, and because the hydrophobicity of φX174 was similar to or somewhat lower than the hydrophobicities of AdV and PV, the φX174 removal ratios tended to be similar to or somewhat smaller than those of the enteric viruses. Therefore, φX174 is a potential conservative surrogate for AdV and PV during coagulation. In summary, the surface hydrophobicity of virus particles and the sensitivity of the virus to the virucidal activity of the coagulant are probably important determinants of the efficiency of virus removal during coagulation. Copyright © 2016 Elsevier B.V. All rights reserved.

Validation of a liquid chromatography-tandem mass spectrometry method for the detection of nicotine biomarkers in hair and an evaluation of wash procedures for removal of environmental nicotine.

PubMed

Miller, Eleanor I; Murray, Gordon J; Rollins, Douglas E; Tiffany, Stephen T; Wilkins, Diana G

2011-07-01

The aim of this exploratory study was to develop and validate a liquid chromatography-tandem mass spectrometry (LC-MS-MS) method for the quantification of nicotine, eight nicotine metabolites, and two minor tobacco alkaloids in fortified analyte-free hair and subsequently apply this method to hair samples collected from active smokers. An additional aim of the study was to include an evaluation of different wash procedures for the effective removal of environmentally deposited nicotine from tobacco smoke. An apparatus was designed for the purpose of exposing analyte-free hair to environmental tobacco smoke in order to deposit nicotine onto the hair surface. A shampoo/water wash procedure was identified as the most effective means of removing nicotine. This wash procedure was utilized for a comparison of washed and unwashed heavy smoker hair samples. Analytes and corresponding deuterated internal standards were extracted using a cation-exchange solid-phase cartridge. LC-MS-MS was carried out using an Acquity™ UPLC(®) system (Waters) and a Quattro Premier XE™ triple quadrupole MS (Waters) operated in electrospray positive ionization mode, with multiple reaction monitoring data acquisition. The developed method was applied to hair samples collected from heavy smokers (n = 3) and low-level smokers (n = 3) collected through IRB-approved protocols. Nicotine, cotinine, and nornicotine were quantified in both the washed and unwashed hair samples collected from three heavy smokers, whereas 3-hydroxycotinine was quantified in only one unwashed sample and nicotine-1'-oxide in the washed and unwashed hair samples from two heavy smokers. In contrast, nicotine-1'-oxide was quantified in one of the three low-level smoker samples; nicotine was quantified in the other two low-level smoker samples. No other analytes were detected in the hair of the three low-level smokers.

Surface chemical modification of nanocrystals

DOE Office of Scientific and Technical Information (OSTI.GOV)

Helms, Brett Anthony; Milliron, Delia Jane; Rosen, Evelyn Louise

Nanocrystals comprising organic ligands at surfaces of the plurality of nanocrystals are provided. The organic ligands are removed from the surfaces of the nanocrystals using a solution comprising a trialkyloxonium salt in a polar aprotic solvent. The removal of the organic ligands causes the nanocrystals to become naked nanocrystals with cationic surfaces.

Process for non-contact removal of organic coatings from the surface of paintings

NASA Technical Reports Server (NTRS)

Banks, Bruce A. (Inventor); Rutledge, Sharon K. (Inventor)

1995-01-01

The present invention discloses a method of removing organic protective coatings from a painting. In the present invention degraded protective coatings such as lacquers, acrylics, natural resins, carbons, soot, and polyurethane are safely removed from the surface of a painting without contact to the surface of the painting. This method can be used for restoration of paintings when they have been damaged, through age, fire, etc.

Plasma cleaning of nanoparticles from EUV mask materials by electrostatics

NASA Astrophysics Data System (ADS)

Lytle, W. M.; Raju, R.; Shin, H.; Das, C.; Neumann, M. J.; Ruzic, D. N.

2008-03-01

Particle contamination on surfaces used in extreme ultraviolet (EUV) mask blank deposition, mask fabrication, and patterned mask handling must be avoided since the contamination can create significant distortions and loss of reflectivity. Particles on the order of 10nm are problematic during MLM mirror fabrication, since the introduced defects disrupt the local Bragg planes. The most serious problem is the accumulation of particles on surfaces of patterned blanks during EUV light exposure, since > 25nm particles will be printed without an out-of-focus pellicle. Particle contaminants are also a problem with direct imprint processes since defects are printed every time. Plasma Assisted Cleaning by Electrostatics (PACE) works by utilizing a helicon plasma as well as a pulsed DC substrate bias to charge particle and repel them electrostatically from the surface. Removal of this nature is a dry cleaning method and removes contamination perpendicular from the surface instead of rolling or sweeping the particles off the surface, a benefit when cleaning patterned surfaces where contamination can be rolled or trapped between features. Also, an entire mask can be cleaned at once since the plasma can cover the entire surface, thus there is no need to focus in on an area to clean. Sophisticated particle contamination detection system utilizing high power laser called DEFCON is developed to analyze the particle removal after PACE cleaning process. PACE has shown greater than 90 % particle removal efficiencies for 30 to 220 nm PSL particles on ruthenium capped quartz. Removal results for silicon surfaces and quartz surfaces show similar removal efficiencies. Results of cleaning 80 nm PSL spheres from silicon substrates will be shown.

Comparing population size estimators for plethodontid salamanders

USGS Publications Warehouse

Bailey, L.L.; Simons, T.R.; Pollock, K.H.

2004-01-01

Despite concern over amphibian declines, few studies estimate absolute abundances because of logistic and economic constraints and previously poor estimator performance. Two estimation approaches recommended for amphibian studies are mark-recapture and depletion (or removal) sampling. We compared abundance estimation via various mark-recapture and depletion methods, using data from a three-year study of terrestrial salamanders in Great Smoky Mountains National Park. Our results indicate that short-term closed-population, robust design, and depletion methods estimate surface population of salamanders (i.e., those near the surface and available for capture during a given sampling occasion). In longer duration studies, temporary emigration violates assumptions of both open- and closed-population mark-recapture estimation models. However, if the temporary emigration is completely random, these models should yield unbiased estimates of the total population (superpopulation) of salamanders in the sampled area. We recommend using Pollock's robust design in mark-recapture studies because of its flexibility to incorporate variation in capture probabilities and to estimate temporary emigration probabilities.

Anomalous optical surface absorption in nominally pure silicon samples at 1550 nm

NASA Astrophysics Data System (ADS)

Bell, Angus S.; Steinlechner, Jessica; Martin, Iain W.; Craig, Kieran; Cunningham, William; Rowan, Sheila; Hough, Jim; Schnabel, Roman; Khalaidovski, Alexander

2017-10-01

The announcement of the direct detection of gravitational waves (GW) by the LIGO and Virgo collaboration in February 2016 has removed any uncertainty around the possibility of GW astronomy. It has demonstrated that future detectors with sensitivities ten times greater than the Advanced LIGO detectors would see thousands of events per year. Many proposals for such future interferometric GW detectors assume the use of silicon test masses. Silicon has low mechanical loss at low temperatures, which leads to low displacement noise for a suspended interferometer mirror. In addition to the low mechanical loss, it is a requirement that the test masses have a low optical loss. Measurements at 1550 nm have indicated that material with a low enough bulk absorption is available; however there have been suggestions that this low absorption material has a surface absorption of  >100 ppm which could preclude its use in future cryogenic detectors. We show in this paper that this surface loss is not intrinsic but is likely to be a result of particular polishing techniques and can be removed or avoided by the correct polishing procedure. This is an important step towards high gravitational wave detection rates in silicon based instruments.

Enhancement of surface damage resistance by selective chemical removal of CeO2

NASA Astrophysics Data System (ADS)

Kamimura, Tomosumi; Motokoshi, Shinji; Sakamoto, Takayasu; Jitsuno, Takahisa; Shiba, Haruya; Akamatsu, Shigenori; Horibe, Hideo; Okamoto, Takayuki; Yoshida, Kunio

2005-02-01

The laser-induced damage threshold of polished fused silica surfaces is much lower than the damage threshod of its bulk. It is well known that contaminations of polished surface are one of the causes of low threshold of laser-induced surface damage. Particularly, polishing contamination such as cerium dioxide (CeO2) compound used in optical polishing process is embedded inside the surface layer, and cannot be removed by conventional cleaning. For the enhancement of surface damage resistance, various surface treatments have been applied to the removal of embedded polishing compound. In this paper, we propose a new method using slective chemical removal with high-temperature sulfuric acid (H2SO4). Sulfuric acid could dissolve only CeO2 from the fused silica surface. The surface roughness of fused silica treated H2SO4 was kept through the treatment process. At the wavelength of 355 nm, the surface damage threshold was drastically improved to the nearly same as bulk quality. However, the effect of our treatment was not observed at the wavelength of 1064 nm. The comparison with our previous results obtained from other surface treatments will be discussed.

Constructing a multidimensional free energy surface like a spider weaving a web.

PubMed

Chen, Changjun

2017-10-15

Complete free energy surface in the collective variable space provides important information of the reaction mechanisms of the molecules. But, sufficient sampling in the collective variable space is not easy. The space expands quickly with the number of the collective variables. To solve the problem, many methods utilize artificial biasing potentials to flatten out the original free energy surface of the molecule in the simulation. Their performances are sensitive to the definitions of the biasing potentials. Fast-growing biasing potential accelerates the sampling speed but decreases the accuracy of the free energy result. Slow-growing biasing potential gives an optimized result but needs more simulation time. In this article, we propose an alternative method. It adds the biasing potential to a representative point of the molecule in the collective variable space to improve the conformational sampling. And the free energy surface is calculated from the free energy gradient in the constrained simulation, not given by the negative of the biasing potential as previous methods. So the presented method does not require the biasing potential to remove all the barriers and basins on the free energy surface exactly. Practical applications show that the method in this work is able to produce the accurate free energy surfaces for different molecules in a short time period. The free energy errors are small in the cases of various biasing potentials. © 2017 Wiley Periodicals, Inc. © 2017 Wiley Periodicals, Inc.

The effect of ultrasonic post instrumentation on root surface temperature.

PubMed

Huttula, Andrew S; Tordik, Patricia A; Imamura, Glen; Eichmiller, Frederick C; McClanahan, Scott B

2006-11-01

This study measured root surface temperature changes when ultrasonic vibration, with and without irrigation, was applied to cemented endodontic posts. Twenty-six, extracted, single-rooted premolars were randomly divided into two groups. Root lengths were standardized, canals instrumented, obturated, and posts cemented into prepared spaces. Thermocouples were positioned at two locations on the proximal root surfaces. Samples were embedded in plaster and brought to 37 degrees C in a water bath. Posts were ultrasonically vibrated for 4 minutes while continuously measuring temperature. Two-way ANOVA compared effects of water coolant and thermocouple location on temperature change. Root surface temperatures were significantly higher (p < 0.001) when posts were instrumented dry. A trend for higher temperatures was observed at coronal thermocouples of nonirrigated teeth and at apical thermocouples of irrigated teeth (p = 0.057). Irrigation during post removal with ultrasonics had a significant impact on the temperature measured at the external root surface.

Cu(II) removal by Anoxybacillus flavithermus-iron oxide composites during the addition of Fe(II)aq

NASA Astrophysics Data System (ADS)

Franzblau, Rachel E.; Daughney, Christopher J.; Swedlund, Peter J.; Weisener, Christopher G.; Moreau, Magali; Johannessen, Bernt; Harmer, Sarah L.

2016-01-01

There is currently poor understanding of metal removal by composites of bacteria and iron oxide minerals, even though they commonly co-occur and are among the most important sorbents in near-surface fluid-rock environments. This study evaluated Cu removal by composites of Anoxybacillus flavithermus and iron oxide over time during the addition, oxidation, and hydrolysis of Fe(II)aq and precipitation of the mineral, in comparison to Cu removal in the two single-sorbent end-member systems. In the absence of iron oxide, Cu removal by A. flavithermus was well described by a previously published surface complexation model, after inclusion of additional reactions describing aqueous complexation by exudate ligands released by the bacteria. In the absence of bacterial cells, Cu removal by iron oxide synthesized in the presence of the bacterial exudate ligands demonstrated the formation of ternary surface complexes. Removal of Cu by the A. flavithermus-iron oxide composites was ca. 20% greater than the prediction based on assumption of additivity in the two end-member systems. This non-additive behavior was attributed to (1) progressive physical blockage of bacterial surface sites by the iron oxide particles, (2) physical blockage of adsorption sites as a result of self-aggregation of the iron oxide particles, and (3) the reduction of Cu(II) to Cu(I) at the bacterial cell surface, as demonstrated by X-ray absorption spectroscopy. The extent of reduction of Cu(II) to Cu(I) was proportional to the concentration of solid phase Fe(II), suggesting that iron oxidation and copper reduction are linked. This study has shown that Cu removal by bacteria-iron oxide composites is greatly affected by redox processes such as Cu(II) reduction on the cell surface both by other bacterial surface ligands and the oxidation of sorbed Fe(II), as well as Fe(II) redox interactions, and aging effects of the mineral (i.e. surface site masking).

Chemical Characterization and Removal of Carbon-14 from Irradiated Graphite II - 13023

DOE Office of Scientific and Technical Information (OSTI.GOV)

Dunzik-Gougar, Mary Lou; Cleaver, James; LaBrier, Daniel

2013-07-01

Approximately 250,000 tonnes of irradiated graphite waste exists worldwide and that quantity is expected to increase with decommissioning of Generation II reactors and deployment of Generation IV gas-cooled, graphite moderated reactors. This situation indicates the need for a graphite waste management strategy. Of greatest concern for long-term disposal of irradiated graphite is carbon-14 (C-14), with a half-life of 5730 years. Study of irradiated graphite from some nuclear reactors indicates C-14 is concentrated on the outer 5 mm of the graphite structure. The aim of the research presented last year and updated here is to identify the chemical form of C-14more » in irradiated graphite and develop a practical method by which C-14 can be removed. A nuclear-grade graphite, NBG-18, and a high-surface-area graphite foam, POCOFoam{sup R}, were exposed to liquid nitrogen (to increase the quantity of C-14 precursor) and neutron-irradiated (10{sup 13} neutrons/cm{sup 2}/s). Finer grained NBG-25 was not exposed to liquid nitrogen prior to irradiation at a neutron flux on the order of 10{sup 14} /cm{sup 2}/s. Characterization of pre- and post-irradiation graphite was conducted to determine the chemical environment and quantity of C-14 and its precursors via the use of surface sensitive characterization techniques. Scanning Electron Microscopy (SEM) was used to evaluate the morphological features of graphite samples. The concentration, chemical composition, and bonding characteristics of C-14 and its precursors were determined through X-ray Photoelectron Spectroscopy (XPS), Time-of-Flight Secondary Ion Mass Spectrometry (SIMS), and Energy Dispersive X-ray Analysis Spectroscopy (EDX). Results of post-irradiation characterization of these materials indicate a variety of surface functional groups containing carbon, oxygen, nitrogen and hydrogen. During thermal treatment, irradiated graphite samples are heated in the presence of an inert carrier gas (with or without oxidant gas), which carries off gaseous products released during treatment. Graphite gasification occurs via interaction with adsorbed oxygen complexes. Experiments in argon were performed at 900 deg. C and 1400 deg. C to evaluate the selective removal of C-14. Thermal treatment also was performed with the addition of 3 and 5 volume % oxygen at temperatures 700 deg. C and 1400 deg. C. Thermal treatment experiments were evaluated for the effective selective removal of C-14. Lower temperatures and oxygen levels correlated to more efficient C-14 removal. (authors)« less

Characterization of polymer decomposition products by laser desorption mass spectrometry

NASA Technical Reports Server (NTRS)

Pallix, Joan B.; Lincoln, Kenneth A.; Miglionico, Charles J.; Roybal, Robert E.; Stein, Charles; Shively, Jon H.

1993-01-01

Laser desorption mass spectrometry has been used to characterize the ash-like substances formed on the surfaces of polymer matrix composites (PMC's) during exposure on LDEF. In an effort to minimize fragmentation, material was removed from the sample surfaces by laser desorption and desorbed neutrals were ionized by electron impact. Ions were detected in a time-of-flight mass analyzer which allows the entire mass spectrum to be collected for each laser shot. The method is ideal for these studies because only a small amount of ash is available for analysis. Three sets of samples were studied including C/polysulfone, C/polyimide and C/phenolic. Each set contains leading and trailing edge LDEF samples and their respective controls. In each case, the mass spectrum of the ash shows a number of high mass peaks which can be assigned to fragments of the associated polymer. These high mass peaks are not observed in the spectra of the control samples. In general, the results indicate that the ash is formed from decomposition of the polymer matrix.

77 FR 22188 - Airworthiness Directives; Airbus Airplanes

Federal Register 2010, 2011, 2012, 2013, 2014

2012-04-13

... removing the labels if there is evidence of sealant damage or moisture ingress behind the labels. If... paint removal and cracking of the surface treatment. Before further flight after doing the detailed..., defects, and damage of the paint or surface protection, including paint removal and cracking, in...

Near-infrared image-guided laser ablation of dental decay

NASA Astrophysics Data System (ADS)

Tao, You-Chen; Fried, Daniel

2009-09-01

Image-guided laser ablation systems are now feasible for dentistry with the recent development of nondestructive high-contrast imaging modalities such as near-IR (NIR) imaging and optical coherence tomography (OCT) that are capable of discriminating between sound and demineralized dental enamel at the early stages of development. Our objective is to demonstrate that images of demineralized tooth surfaces have sufficient contrast to be used to guide a CO2 laser for the selective removal of natural and artificial caries lesions. NIR imaging and polarization-sensitive optical coherence tomography (PS-OCT) operating at 1310-nm are used to acquire images of natural lesions on extracted human teeth and highly patterned artificial lesions produced on bovine enamel. NIR and PS-OCT images are analyzed and converted to binary maps designating the areas on the samples to be removed by a CO2 laser to selectively remove the lesions. Postablation NIR and PS-OCT images confirmed preferential removal of demineralized areas with minimal damage to sound enamel areas. These promising results suggest that NIR and PS-OCT imaging systems can be integrated with a CO2 laser ablation system for the selective removal of dental caries.

Near-infrared image-guided laser ablation of dental decay

PubMed Central

Tao, You-Chen; Fried, Daniel

2009-01-01

Image-guided laser ablation systems are now feasible for dentistry with the recent development of nondestructive high-contrast imaging modalities such as near-IR (NIR) imaging and optical coherence tomography (OCT) that are capable of discriminating between sound and demineralized dental enamel at the early stages of development. Our objective is to demonstrate that images of demineralized tooth surfaces have sufficient contrast to be used to guide a CO2 laser for the selective removal of natural and artificial caries lesions. NIR imaging and polarization-sensitive optical coherence tomography (PS-OCT) operating at 1310-nm are used to acquire images of natural lesions on extracted human teeth and highly patterned artificial lesions produced on bovine enamel. NIR and PS-OCT images are analyzed and converted to binary maps designating the areas on the samples to be removed by a CO2 laser to selectively remove the lesions. Postablation NIR and PS-OCT images confirmed preferential removal of demineralized areas with minimal damage to sound enamel areas. These promising results suggest that NIR and PS-OCT imaging systems can be integrated with a CO2 laser ablation system for the selective removal of dental caries. PMID:19895146

Near-infrared image-guided laser ablation of dental decay.

PubMed

Tao, You-Chen; Fried, Daniel

2009-01-01

Image-guided laser ablation systems are now feasible for dentistry with the recent development of nondestructive high-contrast imaging modalities such as near-IR (NIR) imaging and optical coherence tomography (OCT) that are capable of discriminating between sound and demineralized dental enamel at the early stages of development. Our objective is to demonstrate that images of demineralized tooth surfaces have sufficient contrast to be used to guide a CO(2) laser for the selective removal of natural and artificial caries lesions. NIR imaging and polarization-sensitive optical coherence tomography (PS-OCT) operating at 1310-nm are used to acquire images of natural lesions on extracted human teeth and highly patterned artificial lesions produced on bovine enamel. NIR and PS-OCT images are analyzed and converted to binary maps designating the areas on the samples to be removed by a CO(2) laser to selectively remove the lesions. Postablation NIR and PS-OCT images confirmed preferential removal of demineralized areas with minimal damage to sound enamel areas. These promising results suggest that NIR and PS-OCT imaging systems can be integrated with a CO(2) laser ablation system for the selective removal of dental caries.

Influence of wavelength on the laser removal of lichens colonizing heritage stone

NASA Astrophysics Data System (ADS)

Sanz, M.; Oujja, M.; Ascaso, C.; Pérez-Ortega, S.; Souza-Egipsy, V.; Fort, R.; de los Rios, A.; Wierzchos, J.; Cañamares, M. V.; Castillejo, M.

2017-03-01

Laser irradiation of lichen thalli on heritage stones serves for the control of epilithic and endolithic biological colonizations. In this work we investigate rock samples from two quarries traditionally used as source of monumental stone, sandstone from Valonsadero (Soria, Spain) and granite from Alpedrete (Madrid, Spain), in order to find conditions for efficient laser removal of lichen thalli that ensure preservation of the lithic substrate. The samples presented superficial areas colonized by different types of crustose lichens, i.e. Candelariella vitellina, Aspicilia viridescens, Rhizocarpon disporum and Protoparmeliopsis muralis in Valonsadero samples and P. cf. bolcana and A. cf. contorta in Alpedrete samples. A comparative laser cleaning study was carried out on the mentioned samples with ns Q-switched Nd:YAG laser pulses of 1064 nm (fundamental radiation), 355 nm (3rd harmonic) and 266 nm (4th harmonic) and sequences of IR-UV pulses. A number of techniques such as UV-Vis absorption spectroscopy, stereomicroscopy, scanning electron microscopy (SEM) at low vacuum, SEM with backscattered electron imaging (SEM-BSE), electron dispersive spectroscopy (EDS) and FT-Raman spectroscopy were employed to determine the best laser irradiation conditions and to detect possible structural, morphological and chemical changes on the irradiated surfaces. The results show that the laser treatment does not lead to the complete removal of the studied lichen thalli, although clearly induces substantial damage, in the form of loss of the lichen upper cortex and damage to the algal layer. In the medium term these alterations could result in the destruction of the lichen thalli, thus providing a degree of control of the biodeterioration processes of the lithic substrate and reducing the chances of subsequent lichen recolonization.

Synthesis and characterization of low-cost activated carbon prepared from Malawian baobab fruit shells by H3PO4 activation for removal of Cu(II) ions: equilibrium and kinetics studies

NASA Astrophysics Data System (ADS)

Vunain, Ephraim; Kenneth, Davie; Biswick, Timothy

2017-12-01

In this study, low-cost activated carbon (AC) prepared from baobab fruit shells by chemical activation using phosphoric acid was evaluated for the removal of Cu(II) ions from aqueous solution. The prepared activated carbon samples were characterized using N2-adsorption-desorption isotherms, SEM, FTIR, EDX and XRD analysis. The sample activated at 700 °C was chosen as our optimized sample because its physicochemical properties and BET results were similar to those of a commercial sample. The N2-adsorption-desorption results of the optimized sample revealed a BET surface area of 1089 m2/g, micropore volume of 0.3764 cm3/g, total pore volume of 0.4330 cm3/g and pore size of 1.45 nm. Operational parameters such as pH, initial copper concentration, contact time, adsorbent dosage and temperature were studied in a batch mode. Equilibrium data were obtained by testing the adsorption data using three different isotherm models: Langmuir, Freundlich and Dubinin-Radushkevish (D-R) models. It was found that the adsorption of copper correlated well with the Langmuir isotherm model with a maximum monolayer adsorption capacity of 3.0833 mg/g. The kinetics of the adsorption process was tested through pseudo-first-order and pseudo-second-order models. The pseudo-second-order kinetic model provided the best correlation for the experimental data studied. The adsorption followed chemisorption process. The study provided an effective use of baobab fruit shells as a valuable source of adsorbents for the removal of copper ions from aqueous solution. This study could add economic value to baobab fruit shells in Malawi, reduce disposal problems, and offer an economic source of AC to the AC users.

Optimization of removal function in computer controlled optical surfacing

NASA Astrophysics Data System (ADS)

Chen, Xi; Guo, Peiji; Ren, Jianfeng

2010-10-01

The technical principle of computer controlled optical surfacing (CCOS) and the common method of optimizing removal function that is used in CCOS are introduced in this paper. A new optimizing method time-sharing synthesis of removal function is proposed to solve problems of the removal function being far away from Gaussian type and slow approaching of the removal function error that encountered in the mode of planet motion or translation-rotation. Detailed time-sharing synthesis of using six removal functions is discussed. For a given region on the workpiece, six positions are selected as the centers of the removal function; polishing tool controlled by the executive system of CCOS revolves around each centre to complete a cycle in proper order. The overall removal function obtained by the time-sharing process is the ratio of total material removal in six cycles to time duration of the six cycles, which depends on the arrangement and distribution of the six removal functions. Simulations on the synthesized overall removal functions under two different modes of motion, i.e., planet motion and translation-rotation are performed from which the optimized combination of tool parameters and distribution of time-sharing synthesis removal functions are obtained. The evaluation function when optimizing is determined by an approaching factor which is defined as the ratio of the material removal within the area of half of the polishing tool coverage from the polishing center to the total material removal within the full polishing tool coverage area. After optimization, it is found that the optimized removal function obtained by time-sharing synthesis is closer to the ideal Gaussian type removal function than those by the traditional methods. The time-sharing synthesis method of the removal function provides an efficient way to increase the convergence speed of the surface error in CCOS for the fabrication of aspheric optical surfaces, and to reduce the intermediate- and high-frequency error.

New biosorbent in removing some metals from industrial wastewater in El Mex Bay, Egypt

NASA Astrophysics Data System (ADS)

Abdallah, Maha Ahmed Mohamed; Mahmoud, Mohamed E.; Osman, Maher M.; Ahmed, Somaia B.

2017-07-01

Biosorption is an extensive technology applied for the removal of heavy metal ions and other pollutants from aqueous solutions. In the present study, the biosorption of cadmium, lead, chromium and mercury ions from polluted surface seawater in El-Max Bay was determined using hybrid active carbon sorbents. These sorbents were treated chemically by acid, base and redox reaction followed by surface loading of baker's yeast biomass for increasing their biosorption capacity and the highest metal uptake values. The surface function and morphology of the hybrid immobilized sorbents were studied by Fourier Transform Infrared analysis and scanning electron microscope imaging. Metal removal values proved that the vital role of baker's yeast as a significant high removable due to functional groups at baker's yeast cell wall surface that have the ability to forming various coordination complexes with metal ions. A noticeable increase in the removal of all studied metals was observed and reached to 100 %.

A comparative study with biologically and chemically synthesized nZVI: applications in Cr (VI) removal and ecotoxicity assessment using indigenous microorganisms from chromium-contaminated site.

PubMed

Ravikumar, K V G; Kumar, Deepak; Rajeshwari, A; Madhu, G M; Mrudula, P; Chandrasekaran, Natarajan; Mukherjee, Amitava

2016-02-01

In the present communication, we report a comparative study of Cr (VI) removal using biologically synthesized nano zero valent iron (BS-nZVI) and chemically synthesized nZVI (CS-nZVI), both immobilized in calcium alginate beads. The parameters like initial Cr (VI) concentration, nZVI concentration, and the contact time for Cr (VI) removal were optimized based on Box-Behnken design (BBD) by response surface modeling at a constant pH 7. Under the optimized conditions (concentration of nZVI = 1000 mg L(-1), contact time = ∼ 80 min, and initial concentration of Cr (VI) = 10 mg L(-1)), the Cr (VI) removal by the immobilized BS-nZVI and CS-nZVI alginate beads was 80.04 and 81.08 %, respectively. The adsorption of Cr (VI) onto the surface of alginate beads was confirmed by scanning electron microscopy with energy-dispersive x-ray spectroscopy (SEM-EDX), Fourier transform infrared spectroscopy (FT-IR), and Brunauer-Emmett-Teller (BET) analysis. The applicability of the process using both the sorbents was successfully test medium Cr (VI) spiked environmental water samples. In order to assess the ecotoxic effects of nZVI, the decline in cell viability, generation of intracellular reactive oxygen species (ROS), cell membrane damage, and biouptake was studied at 1000 mg L(-1) concentration, with five indigenous bacterial isolates from chromium-contaminated lake sediments and their consortium.

Response surface methodology approach for the optimisation of adsorption of hydrolysed polyacrylamide from polymer-flooding wastewater onto steel slag: a good option of waste mitigation.

PubMed

Zhu, Mijia; Yao, Jun; Qin, Zhonghai; Lian, Luning; Zhang, Chi

2017-08-01

Wastewater produced from polymer flooding in oil production features high viscosity and chemical oxygen demand because of the residue of high-concentration polymer hydrolysed polyacrylamide (HPAM). In this study, steel slag, a waste from steel manufacturing, was studied as a low-cost adsorbent for HPAM in wastewater. Optimisation of HPAM adsorption by steel slag was performed with a central composite design under response surface methodology (RSM). Results showed that the maximum removal efficiency of 89.31% was obtained at an adsorbent dosage of 105.2 g/L, contact time of 95.4 min and pH of 5.6. These data were strongly correlated with the experimental values of the RSM model. Single and interactive effect analysis showed that HPAM removal efficiency increased with increasing adsorbent dosage and contact time. Efficiency increased when pH was increased from 2.6 to 5.6 and subsequently decreased from 5.6 to 9.3. It was observed that removal efficiency significantly increased (from 0% to 86.1%) at the initial stage (from 0 min to 60 min) and increased gradually after 60 min with an adsorbent dosage of 105.2 g/L, pH of 5.6. The adsorption kinetics was well correlated with the pseudo-second-order equation. Removal of HPAM from the studied water samples indicated that steel slag can be utilised for the pre-treatment of polymer-flooding wastewater.

Hand hygiene using a new hand-cleansing formulation without sanitizers: Effect on Staphylococcus aureus removal and recovery of properties against skin damage.

PubMed

Asaoka, Kentaro; Endo, Shiro; Suzuki, Yuki; Komuro, Satoru; Nemoto, Tadanobu; Kaku, Mitsuo

2016-08-01

Staphylococcus aureus is known to form a biofilm and colonize on damaged skin of the hands. We investigated changes in the quantity of S aureus on the hands and changes in skin damage when using a hand-cleansing formulation with potassium oleate but without a sanitizer (formulation A), which is highly effective in removing S aureus biofilm and causes minimal skin damage. The participants (14 medical staff members) used 2 types of hand-cleansing formulations (formulations A and B), each for 4 weeks. S aureus of the hands was cultured from swab samples on agar plates. Surface of hands was measured using an ultraviolet light microscope. The quantity of S aureus after using formulation A for 4 weeks was 10(1.08 ± 0.05) CFU/mL, a statistically significant decrease from the quantity of S aureus (10(1.59 ± 0.19) CFU/mL) just before use (P = .029). Also, dryness of hand surfaces decreased. With formulation B, the quantity of S aureus did not significantly change from before to after use (P > .05). This presumably occurs because formulation A gently removes S aureus biofilm. Formulation A removed S aureus from the hands of participants, and skin damage on the hands improved. Copyright © 2016 Association for Professionals in Infection Control and Epidemiology, Inc. Published by Elsevier Inc. All rights reserved.

Evaluating Microbial Purification during Soil Treatment of Wastewater with Multicomponent Tracer and Surrogate Tests

USGS Publications Warehouse

Van Cuyk, S.; Siegrist, R.L.; Lowe, K.; Harvey, R.W.

2004-01-01

Soil treatment of wastewater has the potential to achieve high purification efficiency, yet the understanding and predictability of purification with respect to removal of viruses and other pathogens is limited. Research has been completed to quantify the removal of virus and bacteria through the use of microbial surrogates and conservative tracers during controlled experiments with three-dimensional pilot-scale soil treatment systems in the laboratory and during the testing of full-scale systems under field conditions. The surrogates and tracers employed included two viruses (MS-2 and PRID-1 bacteriophages), one bacterium (ice-nucleating active Pseudomonas), and one conservative tracer (bromide ion). Efforts have also been made to determine the relationship between viruses and fecal coliform bacteria in soil samples below the wastewater infiltrative surface, and the correlation between Escherichia coil concentrations measured in percolating soil solution as compared with those estimated from analyses of soil solids. The results suggest episodic breakthrough of virus and bacteria during soil treatment of wastewater and a 2 to 3 log (99-99.9%) removal of virus and near complete removal of fecal coliform bacteria during unsaturated flow through 60 to 90 cm of sandy medium. Results also suggest that the fate of fecal coliform bacteria may be indicative of that of viruses in soil media near the infiltrative surface receiving wastewater effluent. Concentrations of fecal coliform in percolating soil solution may be conservatively estimated from analysis of extracted soil solids.

Evaluation of various cleaning methods to remove bacillus spores from spacecraft hardware materials

NASA Technical Reports Server (NTRS)

Venkateswaran, Kasthuri; Chung, Shirley; Allton, Judith; Kern, Roger

2004-01-01

A detailed study was made of the biological cleaning effectiveness, defined in terms of the ability to remove bacterial spores, of a number of methods used to clean hardware surfaces. Aluminum (Al 6061) and titanium (Ti 6Al-4V) were chosen for the study as they were deemed the two materials most likely to be used in spacecraft extraterrestrial sampler construction. Metal coupons (1 cm x 2.5 cm) were precleaned and inoculated with 5.8 x 10(3) cultivable Bacillus subtilis spores, which are commonly found on spacecraft surfaces and in the assembly environments. The inoculated coupons were subsequently cleaned using: (1) 70% isopropyl alcohol wipe; (2) water wipe; (3) multiple-solvent flight-hardware cleaning procedures used at the Jet Propulsion Laboratory (JPL); (4) Johnson Space Center-developed ultrapure water rinse; and (5) a commercial, semi-aqueous, multiple-solvent (SAMS) cleaning process. The biological cleaning effectiveness was measured by agar plate assay, sterility test (growing in liquid media), and epifluorescent microscopy. None of the cleaning protocols tested completely removed viable spores from the surface of the aluminum. In contrast, titanium was capable of being cleaned to sterility by two methods, the JPL standard and the commercial SAMS cleaning process. Further investigation showed that the passivation step employed in the JPL standard method is an effective surface sterilant on both metals but not compatible with aluminum. It is recommended that titanium (Ti 6Al-4V) be considered superior to aluminum (Al 6061) for use in spacecraft sampling hardware, both for its potential to be cleaned to sterilization and for its ability to withstand the most effective cleaning protocols.

Hierarchically three-dimensional (3D) nanotubular sea urchin-shaped iron oxide and its application in heavy metal removal and solar-induced photocatalytic degradation.

PubMed

Lee, Soon Chang; Jeong, Yesul; Kim, Youn Jung; Kim, Hyeran; Lee, Hyun Uk; Lee, Young-Chul; Lee, Sang Moon; Kim, Hae Jin; An, Ha-Rim; Ha, Myoung Gyu; Lee, Go-Woon; Lee, Young-Seak; Lee, Gaehang

2018-04-23

In this study, hierarchically three-dimensional (3D) nanotubular sea urchin-shaped iron oxide nanostructures (3D-Fe 2 O 3 ) were synthesized by a facile and rapid ultrasound irradiation method. Additives, templates, inert gas atmosphere, pH regulation, and other complicated procedures were not required. Dense 3D-Fe 2 O 3 with a relatively large Brunauer-Emmett-Teller (BET) surface area of 129.4 m 2 /g was synthesized within 23 min, and the BET surface area was further improved to 282.7 m 2 /g by a post heat-treatment process. In addition, this post processing led to phase changes from maghemite (γ phase) to hematite (α phase) Fe 2 O 3 . Subsequent characterization suggested that the growth mechanism of the 3D-Fe 2 O 3 follows self-assembly and oriented attachment. The prepared 3D-Fe 2 O 3 was applied to wastewater purification. Ultrasound-irradiated 3D-Fe 2 O 3 can eliminate a As(V) and Cr(VI) from water with 25 times faster removal rate by using a one third smaller amount than commercial α-Fe 2 O 3 . This was attributed to the inter-particle pores and relatively positively charged surface of the nanostructure. In addition, post heat treatment on ultrasound-irradiated 3D-Fe 2 O 3 significantly influenced the photocatalytic degradation of methylene blue and phenol, with a 25 times higher removal efficiency than that of commercial α-Fe 2 O 3 , because of both high BET surface area and good crystallization of the prepared samples. Copyright © 2018 Elsevier B.V. All rights reserved.