Enhancement in visible light photocatalytic activity by embedding Cu nanoparticles over CuS/MCM-41 nanocomposite

NASA Astrophysics Data System (ADS)

Sohrabnezhad, Sh.; Karamzadeh, M.

2017-07-01

This article indicate the biogenic synthesis of copper nanoparticles (Cu NPs) using the borage flowers extract of Borago officinalis over CuS/MCM-41 nanocomposite (NC). No external reducing was utilized in the developed method. The CuS-MCM-41 NC was used as stabilizing agent. The synthesis of CuS nanostructure in MCM-41 material has been realized by hydrothermal method. Their physiochemical properties have been characterized by X-ray diffraction, transmission electron microscopy (TEM), UV-Visible diffuse reflectance spectroscopy, and Fourier transform infrared spectroscopy. On the basis of TEM images, a layer of Cu NPs has been located over CuS/MCM-41 NC with average diameter of 60-80 nm. The results revealed the spherical nature of the prepared Cu NPs with diameter less than 10 nm. The DR spectra of Cu NPs in MCM-41 and CuS-MCM-41 NCs showed surface plasmon resonance bands at 570 and 500-600 nm, respectively. The photocatalytic activity was evaluated under visible light irradiation using the photocatalytic degradation of methylene blue (MB) as a model reaction. The prepared Cu/CuS/MCM-41 nanocomposite microspheres showed higher photodegradation ability for MB than CuS/MCM-41. The degradation of MB achieved up to 80% after 60 min and the nanocomposite could be recycled and reused.

Direct synthesis of Cu{sub 2}O-RGO nanocomposite on Cu foil by thermal evaporation method and its field emission study

DOE Office of Scientific and Technical Information (OSTI.GOV)

Bansode, Sanjeewani; Khare, Ruchita; Harpale, Kashmira

2015-06-24

In this work, a facile one step thermal evaporation method for deposition of Cu{sub 2}O nanoparticles on RGO sheets to form Cu{sub 2}O-RGO nanocomposite is discussed. To the best of our knowledge, this is the first report on Cu{sub 2}O-RGO nanocomposite, directly grown on Cu foil by a simple thermal evaporation route. The as –prepared nanocomposite exhibits well dispersed Cu{sub 2}O nanoparticles distributed all over the graphene sheet. Field emission properties of the nanocomposite were investigated at a base pressure of 1*10{sup −8} torr. The turn on field, required to draw emission current density of 0.1µA/cm2, was found to bemore » 3.8V/µm with a maximum emission current density of 80 µA/cm2 at an applied field of 6.8 V/µm. Moreover, the nanocomposite shows fairly good emission stability without significant degradation of emission current. The FE results seem to be encouraging, indicative of potential candidature of the Cu{sub 2}O-RGO nanocomposite emitter as an electron source for practical applications in vacuum nanoelectronic devices.« less

Effect of CNTs dispersion on the thermal and mechanical properties of Cu/CNTs nanocomposites

DOE Office of Scientific and Technical Information (OSTI.GOV)

Muhsan, Ali Samer, E-mail: alisameer2007@gmail.com, E-mail: faizahmad@petronas.com.my; Ahmad, Faiz, E-mail: alisameer2007@gmail.com, E-mail: faizahmad@petronas.com.my; Yusoff, Puteri Sri Melor Megat Bt, E-mail: puteris@petronas.com.my

2014-10-24

Modified technique of metal injection molding (MIM) was used to fabricate multiwalled carbon nanotube (CNT) reinforced Cu nanocomposites. The effect of adding different amount of CNTs (0-10 vol.%) on the thermal and mechanical behaviour of the fabricated nanocomposites is presented. Scanning electron microscope analysis revealed homogenous dispersion of CNTs in Cu matrices at different CNTs contents. The experimentally measured thermal conductivities of Cu/CNTs nanocomposites showed extraordinary increase (76% higher than pure sintered Cu) with addition of 10 vol.% CNTs. As compared to the pure sintered Cu, increase in modulus of elasticity (Young's modulus) of Cu/CNTs nanocomposites sintered at 1050°C formore » 2.5 h was measured to be 48%. However, in case of 7.5 vol.% CNTs, Young's modulus was increased significantly about 51% compared to that of pure sintered Cu.« less

Effect of implanted Cu/low-density polyethylene nanocomposite on the morphology of endometrium in the mouse.

PubMed

Xia, Xianping; Xie, Changsheng; Zhu, Changhong; Cai, Shuizhou; Yang, Xiangliang

2007-08-01

To investigate the damage of endometrium caused by the implanted Cu/low-density polyethylene (LDPE) nanocomposite and the contraceptive effect of this novel copper-containing intrauterine device material. Experimental animal study. TongJi Medical College of Huazhong University of Science and Technology. Sixty healthy female mice. Twenty mice received no implants, 20 mice received the Cu/LDPE nanocomposite, and 20 mice received bulk copper. Morphologic features of the endometrium, contraceptive effect, and surface condition of the implanted implants. The contraceptive effect of both the Cu/LDPE nanocomposite and bulk copper is 100%, the damage of the endometrium caused by the Cu/LDPE nanocomposite is much less than that caused by bulk copper, and the surface of the implanted Cu/LDPE nanocomposite is much smoother and much softer than that of the implanted bulk copper. The contraceptive effect of the Cu/LDPE nanocomposite is comparable with that of bulk copper, and the damage of the endometrium caused by the Cu/LDPE nanocomposite is much less than that caused by bulk copper. The endometrium injury is related to the surface condition of the implanted intrauterine device material.

ZnO/Cu nanocomposite: a platform for direct electrochemistry of enzymes and biosensing applications.

PubMed

Yang, Chi; Xu, Chunxiang; Wang, Xuemei

2012-03-06

Unique structured nanomaterials can facilitate the direct electron transfer between redox proteins and the electrodes. Here, in situ directed growth on an electrode of a ZnO/Cu nanocomposite was prepared by a simple corrosion approach, which enables robust mechanical adhesion and electrical contact between the nanostructured ZnO and the electrodes. This is great help to realize the direct electron transfer between the electrode surface and the redox protein. SEM images demonstrate that the morphology of the ZnO/Cu nanocomposite has a large specific surface area, which is favorable to immobilize the biomolecules and construct biosensors. Using glucose oxidase (GOx) as a model, this ZnO/Cu nanocomposite is employed for immobilization of GOx and the construction of the glucose biosensor. Direct electron transfer of GOx is achieved at ZnO/Cu nanocomposite with a high heterogeneous electron transfer rate constant of 0.67 ± 0.06 s(-1). Such ZnO/Cu nanocomposite provides a good matrix for direct electrochemistry of enzymes and mediator-free enzymatic biosensors.

Will ethylene oxide sterilization influence the application of novel Cu/LDPE nanocomposite intrauterine devices?

PubMed

Xia, Xianping; Wang, Yun; Cai, Shuizhou; Xie, Changsheng; Zhu, Changhong

2009-01-01

Copper/low-density polyethylene (Cu/LDPE) nanocomposite intrauterine device (IUD) is an implanted medicinal device that must be sterilized before use. Sterilization processes act either chemically or physically, leading to a lethal change in the structure or function of organic macromolecules in microorganisms. Given the nature of their action, sterilization might also attack the macromolecules of polymers by the same mechanisms, resulting in changes in surface functional groups and in the internal structure of the polymer. If sterilization leads to changes in surface functional groups and in the internal structure of the LDPE matrix, which will influence the mechanical property and cupric ions release rate of novel Cu/LDPE nanocomposite IUDs, potential clinical application will be limited. Therefore, it is necessary to study the influence of ethylene oxide sterilization on the potential clinical application of novel Cu/LDPE nanocomposite IUDs. The influence of ethylene oxide sterilization on the internal structure, surface functional groups, mechanical property and cupric ions release rate of novel Cu/LDPE nanocomposite IUDs was studied using differential scanning calorimetry, attenuated total reflection Fourier transform infrared spectroscopy, tensile testing and absorbance measurement. Ethylene oxide sterilization did not have any influence on the internal structure, surface functional groups, mechanical property and cupric ions release rate of novel Cu/LDPE nanocomposite intrauterine devices. Ethylene oxide sterilization will not affect the potential application of novel Cu/LDPE nanocomposite IUDs.

Preparation and electromagnetic wave absorption of RGO/Cu nanocomposite

NASA Astrophysics Data System (ADS)

Zhang, Hui; Tian, Xingyou; Zhang, Xian; Li, Shikuo; Shen, Yuhua; Xie, Anjian

2017-09-01

We use a facile pyrolysis method to prepare reduced graphene oxide and copper nanocomposite (RGO/Cu) based on it. The product shows an outstanding wave absorption properties. The maximum reflection loss is up to-50.7 dB at 3.8 GHz. The reflection loss of-10 dB (90% power absorption) corresponds to a bandwidth of 11.2 GHz (3.4-14.6 GHz range) for the layer thickness of 2-5 mm. Therefore, it is suggested that the RGO/Cu nanocomposite is also a new kind of lightweight and high-performance EM wave absorbing material.

Electrochemical preparation of poly(methylene blue)/graphene nanocomposite thin films

DOE Office of Scientific and Technical Information (OSTI.GOV)

Erçarıkcı, Elif; Dağcı, Kader; Topçu, Ezgi

2014-07-01

Highlights: • Poly(MB)/graphene thin films are prepared by a simple electrochemical approach. • Graphene layers in the film show a broad band in visible region of absorbance spectra. • Morphology of composite films indicates both disordered and ordered regions. • XRD reveals that nanocomposite films include rGO layers after electropolymerization process. • Chemically prepared graphene is better than electrochemically prepared graphene for electrooxidation of nitrite. - Abstract: Poly(methylene blue)/graphene nanocomposite thin films were prepared by electropolymerization of methylene blue in the presence of graphene which have been synthesized by two different methods of a chemical oxidation process and an electrochemicalmore » approach. Synthesized nanocomposite thin films were characterized by using cyclic voltammetry, UV–vis. absorption spectroscopy, powder X-ray diffraction, and scanning tunneling microscopy techniques. Electrocatalytical properties of prepared poly(methylene blue)/graphene nanocomposite films were compared toward electrochemical oxidation of nitrite. Under optimized conditions, electrocatalytical effect of nanocomposite films of chemically prepared graphene through electrochemical oxidation of nitrite was better than that of electrochemically prepared graphene.« less

Decreasing Ni, Cu, Cd, and Zn heavy metal magnetite-bentonite nanocomposites and adsorption isotherm study

NASA Astrophysics Data System (ADS)

Eskandari, M.; Zakeri Khatir, M.; Khodadadi Darban, A.; Meshkini, M.

2018-04-01

This present study was conducted to investigate the effect of magnetite-bentonite nanocomposite on heavy metal removal from an effluent. For this purpose, magnetite-bentonite nanocomposite was prepared through the chemical method and characterized using x-ray diffraction (XRD) and scanning electron microscopy (SEM) techniques, followed by studying the effect of produced nanocomposite on the removal of Ni2+, Cu2+, Cd2+, and Zn2+ heavy metal ions. The results showed that adsorption capacity of magnetite-bentonite nanocomposites for the studied ions is in the order of Zn2+ > Cd2+ > Cu2+ > Ni2+. Adsorption isotherms were drawn for Ni2+, Cu2+, Cd2+, and Zn2+ cations and found that cations adsorption on nanocomposite fit into Langmuir model.

X-ray absorption investigation of the electronic structure of the CuI@SWCNT nanocomposite

NASA Astrophysics Data System (ADS)

Generalov, A. V.; Brzhezinskaya, M. M.; Vinogradov, A. S.; Püttner, R.; Chernysheva, M. V.; Lukashin, A. V.; Eliseev, A. A.

2011-03-01

The Cu 2 p, I 3 d, and C 1 sX-ray absorption spectra of the CuI@SWCNT nanocomposite prepared by filling single-walled carbon nanotubes (SWCNTs) with the CuI melt by the capillary technique have been measured with a high-energy resolution using the equipment of the Russian-German beamline at the BESSY electron storage ring. In order to characterize the electronic structure of the nanocomposite and possible changes in the atomic and electronic structures of CuI and SWCNTs in the CuI@SWCNT nanocomposite, the spectra obtained have been analyzed in the framework of the quasi-molecular approach by comparing with the spectra of the pristine (CuI and SWCNT) and reference (CuO) systems. It has been revealed that the encapsulation of the CuI compound inside SWCNTs is accompanied by changes in the electronic structure of CuI and SWCNTs due to the chemical interaction between the filler and carbon nanotubes and the change in the atomic structure of CuI.

Free standing CuO-MnO2 nanocomposite for room temperature ammonia sensing

NASA Astrophysics Data System (ADS)

Bhuvaneshwari, S.; Papachan, Seethal; Gopalakrishnan, N.

2017-05-01

CuO nanostructures and CuO-MnO2 nanocomposite were successfully synthesized using hydrothermal method without any aid of growth controlling agents. The synthesized CuO nanostructures have monoclinic structure. The XRD pattern of CuO-MnO2 observed with mixed phases of monoclinic CuO and birnessite-type MnO2 which confirms the formation of nanocomposite. SEM images revealed the turmeric-like morphology for CuO and intercalated sheets with flowers on the surface for CuO-MnO2. The length and breadth of turmeric-like structure is about 642.2 nm and 141.8 nm, respectively. The band gap of 1.72 eV for CuO nanostructure and 1.9 eV for CuO-MnO2 nanocomposite were observed from the absorption spectra. The free standing devices of CuO-MnO2 showed nearly a 3 fold increase sensing response to ammonia at room temperature when compared to the constituent CuO. The composite sensor showed response time of 120 s and recovered within 600 s. This enhanced response can be asserted to the peculiar morphology of the composite that provides more adsorption site for gas diffusion to take place.

Study of GO-Cu2O and RGO-Cu nanocomposite monolayer sheets prepared by modified Langmuir Blodgett route

NASA Astrophysics Data System (ADS)

Botcha, V. Divakar; Sutar, D. S.; Major, S. S.

2018-07-01

The modified Langmuir-Blodgett (MLB) technique has been improvised and extended to transfer GO-Cu2O nanocomposite monolayer sheets, by introducing Cu2+ ions into the subphase at room temperature. Morphological studies of as-transferred sheets revealed the presence of closely spaced GO monolayer sheets, with slightly enhanced roughness. XPS studies of as-transferred sheets confirmed the presence of copper, either as metallic Cu or Cu2O, along with significant Cu(OH)2 component, but TEM results confirmed the formation of Cu2O nanocrystallites of size (7 ± 2) nm, distributed uniformly over GO sheets. After heat treatment in vacuum at 400 °C, the nanocomposite sheets were covered with a uniform distribution of larger size nanoparticles. Based on Raman, XPS and TEM studies it has been confirmed that heat treatment at 400 °C in vacuum results in the formation of agglomerated Cu nanoparticles of size (23 ± 9) nm distributed uniformly over reduced graphene oxide (RGO) sheets. The electrical characterization of nanocomposite sheets on SiO2/Si in back-gated FET geometry revealed that the electrical conductivity of as-transferred GO-Cu2O sheets was similar to that usually observed for GO monolayer sheets. The RGO-Cu sheets also displayed electrical conductivity and field effect mobility values comparable to those reported for RGO sheets obtained by chemical/thermal reduction, and was unaffected by the presence of Cu nanoparticles.

Laser ablation of Au-CuO core-shell nanocomposite in water for optoelectronic devices

NASA Astrophysics Data System (ADS)

Ismail, Raid A.; Abdul-Hamed, Ryam S.

2017-12-01

Core-shell gold-copper oxide Au-CuO nanocomposites were synthesized using laser ablation of CuO target in colloidal solution of Au nanoparticles (NPs). The effect of laser fluence on the structural, morphological, electrical, and optical properties of Au-CuO nanocomposites was investigated using x-ray diffraction (XRD), atomic force microscope (AFM), scanning electron microscope (SEM), transmission electron microscope (TEM), photoluminescence (PL), Fourier transformed infrared spectroscopy (FTIR), Hall measurement, and UV-vis spectroscopy. X-ray diffraction results confirm the formation of polycrystalline Au-CuO NPs with monoclinic structure. The optical energy gap for CuO was 4 eV and for the Au-CuO core-shell nanocomposites was found to be in the range of 3.4-3.7 eV. SEM and TEM investigations revealed that the structure and morphology of Au-CuO core-shell nanocomposites were strongly depending on the laser fluence. A formation of Au-CuO nanospheres and platelets structures was observed. The photoluminescence data showed an emission of broad visible peaks between 407 and 420 nm. The effect of laser fluence on the dark and illuminated I-V characteristics of Au-CuO/n-Si heterojunction photodetectors was investigated and analyzed. The experimental data demonstrated that the photodetector prepared at optimum laser fluence exhibited photosensitivity of 0.6 AW-1 at 800 nm.

Cooperative cytotoxic activity of Zn and Cu in bovine serum albumin-conjugated ZnS/CuS nano-composites in PC12 cancer cells

NASA Astrophysics Data System (ADS)

Wang, Hua-Jie; Yu, Xue-Hong; Wang, Cai-Feng; Cao, Ying

2013-11-01

Series of self-assembled and mono-dispersed bovine serum albumin (BSA)-conjugated ZnS/CuS nano-composites with different Zn/Cu ratios had been successfully synthesized by a combination method of the biomimetic synthesis and ion-exchange strategy under the gentle conditions. High-resolution transmission electron microscopy observation, Fourier transform infrared spectra and zeta potential analysis demonstrated that BSA-conjugated ZnS/CuS nano-composites with well dispersity had the hierarchical structure and BSA was a key factor to control the morphology and surface electro-negativity of final products. The real-time monitoring by atomic absorption spectroscopy and powder X-ray diffraction revealed that the Zn/Cu ratio of nano-composites could be controlled by adjusting the ion-exchange time. In addition, the metabolic and morphological assays indicated that the metabolic proliferation and spread of rat pheochromocytoma (PC12) cells could be inhibited by nano-composites, with the high anti-cancer activity at a low concentration (4 ppm). What were more important, Zn and Cu in nano-composites exhibited a positive cooperativity at inhibiting cancer cell functions. The microscope observation and biochemical marker analysis clearly revealed that the nano-composites-included lipid peroxidation and disintegration of membrane led to the death of PC12 cells. Summarily, the present study substantiated the potential of BSA-conjugated ZnS/CuS nano-composites as anti-cancer drug.

Optimization of photoelectrochemical performance in Pt-modified p-Cu2O/n-Cu2O nanocomposite

NASA Astrophysics Data System (ADS)

Wang, Yichen; Lou, Zirui; Niu, Wenzhe; Ye, Zhizhen; Zhu, Liping

2018-04-01

As it is expected to be one of the most promising materials for utilizing solar energy, Cu2O has attracted considerable attention with respect to the achievement of solar energy conversion. Until now, the photocurrent densities of all planar structure of the Cu2O photocathode have not even come close to the theoretical value of -14.7 mA cm-2 due to the incompatible light absorption and charge carrier diffusion lengths. Here, we have fabricated p-n Cu2O homojunction nanocomposite by multiple steps of electrochemical deposition processing with the optimization of deposition periods. The p-Cu2O/n-Cu2O nanocomposite fabricated by optimized pH (4.9) and deposition time (4 min) exhibited double the photocurrent density of that of the bare p-Cu2O photocathode. And the highest photocurrent density of nanostructured p-n Cu2O nanorod homojunction photocathode with a p-Cu2O blocking layer reached -10.0 mA cm-2 at 0 V versus the reversible hydrogen electrode under simulated AM 1.5G illumination (100 mW cm-2).

Synthesis of ZnO/CuO and TiO{sub 2}/CuO nanocomposites for light and ultrasound assisted degradation of a textile dye in aqueous solution

DOE Office of Scientific and Technical Information (OSTI.GOV)

Muzakki, Afifah; Shabrany, Hesni; Saleh, Rosari, E-mail: rosari.saleh@gmail.com, E-mail: rosari.saleh@ui.ac.id

2016-04-19

ZnO/CuO and TiO2/CuO nanocomposites with different Zn/Cu and Ti/Cu ratios were prepared using sol-gel method. The obtained composite samples were used as catalyst. Methylene blue was used as a model of textile dye to evaluate their photocatalytic, sonocatalytic and photosonocatalytic activities. X-ray diffraction and energy dispersive X- ray analysis confirmed that only monoclinic CuO and hexagonal wurtzite ZnO structures are present in ZnO/CuO nanocomposites, while in TiO2/CuO nanocomposites monoclinic CuO and anatase TiO2 structures were observed. The degradation of methylene blue indicated that the incorporation of CuO in ZnO/CuO and TiO2/CuO nanocomposites exhibited an appreciable higher photocatalytic activity, which wasmore » mainly attributed to the extended photoresponding range and more light energy could be utilized than pure ZnO and TiO2.« less

Methods of making non-covalently bonded carbon-titania nanocomposite thin films and applications of the same

DOEpatents

Liang, Yu Teng; Vijayan, Baiju K.; Gray, Kimberly A.; Hersam, Mark C.

2016-07-19

In one aspect, a method of making non-covalently bonded carbon-titania nanocomposite thin films includes: forming a carbon-based ink; forming a titania (TiO.sub.2) solution; blade-coating a mechanical mixture of the carbon-based ink and the titania solution onto a substrate; and annealing the blade-coated substrate at a first temperature for a first period of time to obtain the carbon-based titania nanocomposite thin films. In certain embodiments, the carbon-based titania nanocomposite thin films may include solvent-exfoliated graphene titania (SEG-TiO.sub.2) nanocomposite thin films, or single walled carbon nanotube titania (SWCNT-TiO.sub.2) nanocomposite thin films.

Synthesis and characterization of Chitosan-CuO-MgO polymer nanocomposites

NASA Astrophysics Data System (ADS)

Praffulla, S. R.; Bubbly, S. G.

2018-05-01

In the present work, we have synthesized Chitosan-CuO-MgO nanocomposites by incorporating CuO and MgO nanoparticles in chitosan matrix. Copper oxide and magnesium oxide nanoparticles synthesized by precipitation method were characterized by X-ray diffraction and the diffraction patterns confirmed the monoclinic and cubic crystalline structures of CuO and MgO nanoparticles respectively. Chitosan-CuO-MgO composite films were prepared using solution- cast method with different concentrations of CuO and MgO nanoparticles (15 - 50 wt % with respect to chitosan) and characterized by XRD, FTIR and UV-Vis spectroscopy. The X-ray diffraction pattern shows that the crystallinity of the chitosan composite increases with increase in nanoparticle concentration. FTIR spectra confirm the chemical interaction between chitosan and metal oxide nanoparticles (CuO and MgO). UV absorbance of chitosan nanocomposites were up to 17% better than pure chitosan, thus confirming its UV shielding properties. The mechanical and electrical properties of the prepared composites are in progress.

Rapid fabrication of hierarchically structured supramolecular nanocomposite thin films in one minute

DOEpatents

Xu, Ting; Kao, Joseph

2016-11-08

Functional nanocomposites containing nanoparticles of different chemical compositions may exhibit new properties to meet demands for advanced technology. It is imperative to simultaneously achieve hierarchical structural control and to develop rapid, scalable fabrication to minimize degradation of nanoparticle properties and for compatibility with nanomanufacturing. The assembly kinetics of supramolecular nanocomposite in thin films is governed by the energetic cost arising from defects, the chain mobility, and the activation energy for inter-domain diffusion. By optimizing only one parameter, the solvent fraction in the film, the assembly kinetics can be precisely tailored to produce hierarchically structured thin films of supramolecular nanocomposites in approximately one minute. Moreover, the strong wavelength dependent optical anisotropy in the nanocomposite highlights their potential applications for light manipulation and information transmission. The present invention opens a new avenue in designing manufacture-friendly continuous processing for the fabrication of functional nanocomposite thin films.

Deposition of nanocomposite Cu-TiO2 using heterogeneous colliding plasmas

NASA Astrophysics Data System (ADS)

Pandey, Pramod K.; Thareja, Raj K.; Singh, Ravi Pratap; Costello, John T.

2018-03-01

The formation of CuTiO2 nanocomposites has been observed in an experiment in which laser plasma plumes of Cu and Ti collide and stagnate in an oxygen atmosphere. The inherent advantage of this technique lies in its simplicity and flexibility where laser, target composition and geometry along with ambient atmosphere are all controllable parameters through which the stoichiometry of the deposited nanocomposites may be selected. The experiment has been performed at three oxygen ambient pressures 10-4, 10-2, 100 mbar and we observe its effect on stoichiometry, and morphology of the deposited nanocomposites. Here, we show how the stoichiometry of deposited nanocomposites can be readily controlled by changing just one parameter, namely the ambient oxygen pressure. The different peaks of photoluminescence spectra λ =390{ nm}( {E=3.18{ eV}} ) corresponding to the anatase phase of TiO2, along with the peaks at λ = 483 nm ( E = 2.56 eV) and 582 nm ( E = 2.13 eV) of deposited nanocomposites, shows the doping/blending effect on the band gaps which may potentially be of value in solar cell technology. The technique can, in principle, be extended to include nanocomposites of other materials making it potentially more widely applicable.

Effect of annealing temperatures on the morphology and structural properties of PVDF/MgO nanocomposites thin films

NASA Astrophysics Data System (ADS)

Rozana, M. D.; Arshad, A. N.; Wahid, M. H. M.; Habibah, Z.; Sarip, M. N.; Rusop, M.

2018-05-01

This study investigates the effect of annealing on the topography, morphology and crystal phases of poly(vinylideneflouride)/Magnesium Oxide (MgO) nanocomposites thin films via AFM, FESEM and ATR-FTIR. The nanocomposites thin films were annealed at temperatures ranging from 70°C to 170°C. The annealed PVDF/MgO nanocomposites thin films were then cooled at room temperature before removal from the oven. This is to restructure the crystal lattice and to reduce imperfection for the PVDF/MgO nanocomposites thin films. PVDF/MgO nanocomposites thin films with annealing temperatures of 70°C, 90°C and 110°C showed uniform distribution of MgO nanoparticles, relatively low average surface roughness and no visible of defects. High application of annealing temperature on PVDF/MgO nanocomposites thin films caused tear-like defects on the thin films surface as observed by FESEM. The PVDF/MgO nanocomposites thin films annealed at 70°C was found to be a favourable film to be utilized in this study due to its enhanced β-crystalites of PVDF as evident in ATR-FTIR spectra.

IDM release behavior and surface characteristics of the novel Cu/IDM/LDPE nanocomposite for intrauterine device.

PubMed

Yang, Zhihong; Xie, Changsheng; Xiang, Hua; Feng, Jinqing; Xia, Xianping; Cai, Shuizhou

2009-03-01

Copper/indomethacin/low-density polyethylene (Cu/IDM/LDPE) nanocomposite was prepared as a novel material for intra-uterine device (IUD). IDM release profile of the nanocomposite was investigated by using spectrophotometer. The results show that IDM release rate of Cu/IDM/LDPE nanocomposite is higher in simulated uterine solution than that in methanol, confirming that the release process of IDM is dominated mainly by pore diffusion. The decrease in copper particle size and the increase in copper mass content all accelerate IDM release, indicating that IDM release rate can be adjusted by changing copper loading or copper particle size. The surface of the incubated nanocomposite was characterized by X-ray diffraction, scanning electron microscopy and energy dispersive X-ray microanalysis. A few deposits composed of P, Cl, Ca, Cu and O were observed on the nanocomposite surface, which may be related to the presence of IDM particles with large particle size.

Graphene-Decorated Nanocomposites for Printable Electrodes in Thin Wafer Devices

NASA Astrophysics Data System (ADS)

Bakhshizadeh, N.; Sivoththaman, S.

2017-12-01

Printable electrodes that induce less stress and require lower curing temperatures compared to traditional screen-printed metal pastes are needed in thin wafer devices such as future solar cells, and in flexible electronics. The synthesis of nanocomposites by incorporating graphene nanopowders as well as silver nanowires into epoxy-based electrically conductive adhesives (ECA) is examined to improve electrical conductivity and to develop alternate printable electrode materials that induce less stress on the wafer. For the synthesized graphene and Ag nanowire-decorated ECA nanocomposites, the curing kinetics were studied by dynamic and isothermal differential scanning calorimetry measurements. Thermogravimetric analysis on ECA, ECA-AG and ECA/graphene nanopowder nanocomposites showed that the temperatures for onset of decomposition are higher than their corresponding glass transition temperature ( T g) indicating an excellent thermal resistance. Printed ECA/Ag nanowire nanocomposites showed 90% higher electrical conductivity than ECA films, whereas the ECA/graphene nanocomposites increased the conductivity by over two orders of magnitude. Scanning electron microscopy results also revealed the effect of fillers morphology on the conductivity improvement and current transfer mechanisms in nanocomposites. Residual stress analysis performed on Si wafers showed that the ECA and nanocomposite printed wafers are subjected to much lower stress compared to those printed with metallic pastes. The observed parameters of low curing temperature, good thermal resistance, reasonably high conductivity, and low residual stress in the ECA/graphene nanocomposite makes this material a promising alternative in screen-printed electrode formation in thin substrates.

A Facile One-Pot Synthesis of Au/Cu2O Nanocomposites for Nonenzymatic Detection of Hydrogen Peroxide

NASA Astrophysics Data System (ADS)

Chen, Ting; Tian, Liangliang; Chen, Yuan; Liu, Bitao; Zhang, Jin

2015-06-01

Au/Cu2O nanocomposites were successfully synthesized by a facile one-pot redox reaction without additional reducing agent under room temperature. The morphologies and structures of the as-prepared products were characterized by scanning electron microscopy (SEM), transmission electron microscopy (TEM), and X-ray diffraction (XRD). The electrocatalytic performance of Au/Cu2O nanocomposites towards hydrogen peroxide was evaluated by cyclic voltammetry (CV) and chronoamperometry (CA). The prepared Au/Cu2O nanocomposite electrode showed a wide linear range from 25 to 11.2 mM ( R = 0.9989) with a low detection limit of 1.05 μM ( S/ N = 3) and high sensitivity of 292.89 mA mM-1 cm-2. The enhanced performance for H2O2 detection can be attributed to the introduction of Au and the synergistic effect between Au and Cu2O. It is demonstrated that the Au/Cu2O nanocomposites material could be a promising candidate for H2O2 detection.

Study on swift heavy ions induced modifications of Ag-ZnO nanocomposite thin film

NASA Astrophysics Data System (ADS)

Singh, S. K.; Singhal, R.; Siva Kumar, V. V.

2017-03-01

In the present work, swift heavy ion (SHI) irradiation induced modifications in structural and optical properties of Ag-ZnO nanocomposite thin films have been investigated. Ag-ZnO nanocomposite (NCs) thin films were synthesized by RF magnetron sputtering technique and irradiated with 100 MeV Ag7+ ions at three different fluences 3 × 1012, 1 × 1013 and 3 × 1013 ions/cm2. Rutherford Backscattering Spectrometry revealed Ag concentration to be ∼8.0 at.%, and measured thickness of the films was ∼55 nm. Structural properties of pristine and irradiated films have been analyzed by X-ray diffraction analysis and found that variation in crystallite size of the film with ion irradiation. X-ray photoelectron spectroscopy (XPS) indicates the formation of Ag-ZnO nanocomposite thin film with presence of Ag, Zn and O elements. Oxidation state of Ag and Zn also estimated by XPS analysis. Surface plasmon resonance (SPR) of Ag nanoparticle has appeared at ∼475 nm in the pristine thin film, which is blue shifted by ∼30 nm in film irradiated at fluence of 3 × 1012 ions/cm2 and completely disappeared in film irradiated at higher fluences, 1 × 1013 and 3 × 1013 ions/cm2. A marginal change in the optical band gap of Ag-ZnO nanocomposite thin film is also found with increasing ion fluence. Surface morphology of pristine and irradiated films have been studied using Atomic Force Microscopy (AFM). Raman and Photo-luminance (PL) spectra of nanocomposite thin films have been investigated to understand the ion induced modifications such as lattice defects and disordering in the nanocomposite thin film.

Microstructure and properties of Cu-Sn-Zn-TiO 2 nano-composite coatings on mild steel

DOE Office of Scientific and Technical Information (OSTI.GOV)

Gao, Weidong; Cao, Di; Jin, Yunxue

Cu-Sn-Zn coatings have been widely used in industry for their unique properties, such as good conductivity, high corrosion resistance and excellent solderability. To further improve the mechanical performance of Cu-Sn-Zn coatings, powder-enhanced method was applied and Cu-Sn-Zn-TiO 2 nano-composite coatings with different TiO 2 concentration were fabricated. The microstructure of Cu-Sn-Zn-TiO 2 nano-composite coatings were investigated by X-ray diffraction (XRD) and Scanning Electron Microscopy (SEM). The mechanical properties of coatings including microhardness and wear resistance were studied. The results indicate that the incorporation of TiO 2 nanoparticle can significantly influence the properties of Cu-Sn-Zn coatings. The microhardness of Cu-Sn-Zn coatingmore » was increased to 383 HV from 330 HV with 1 g/L TiO 2 addition. Also, the corrosion resistance of coating was enhanced. The effects of TiO 2 nanoparticle concentration on the microstructure, mechanical properties and corrosion resistance of Cu-Sn-Zn-TiO 2 nano-composite coatings were discussed.« less

Microstructure and properties of Cu-Sn-Zn-TiO 2 nano-composite coatings on mild steel

DOE PAGES

Gao, Weidong; Cao, Di; Jin, Yunxue; ...

2018-04-18

Cu-Sn-Zn coatings have been widely used in industry for their unique properties, such as good conductivity, high corrosion resistance and excellent solderability. To further improve the mechanical performance of Cu-Sn-Zn coatings, powder-enhanced method was applied and Cu-Sn-Zn-TiO 2 nano-composite coatings with different TiO 2 concentration were fabricated. The microstructure of Cu-Sn-Zn-TiO 2 nano-composite coatings were investigated by X-ray diffraction (XRD) and Scanning Electron Microscopy (SEM). The mechanical properties of coatings including microhardness and wear resistance were studied. The results indicate that the incorporation of TiO 2 nanoparticle can significantly influence the properties of Cu-Sn-Zn coatings. The microhardness of Cu-Sn-Zn coatingmore » was increased to 383 HV from 330 HV with 1 g/L TiO 2 addition. Also, the corrosion resistance of coating was enhanced. The effects of TiO 2 nanoparticle concentration on the microstructure, mechanical properties and corrosion resistance of Cu-Sn-Zn-TiO 2 nano-composite coatings were discussed.« less

Heterojunction CuO-TiO2 nanocomposite synthesis for significant photocatalytic hydrogen production

NASA Astrophysics Data System (ADS)

Manjunath, K.; Souza, V. S.; Ramakrishnappa, T.; Nagaraju, G.; Scholten, J. D.; Dupont, J.

2016-11-01

Effective and low-cost photocatalysts have been synthesized by a simple hydrothermal process. In this process, the two CuO and TiO2 bound one over the other and formed a heterojunction CuO-TiO2 nanocomposite. CuO serves as electron reservoir by receiving electrons from TiO2, which suppresses the recombination of e-/h+ and transfers the received electron to split water, which results in enhanced H2 production. Heterojunction CuO-TiO2 nanocomposite material recorded a maximum of 9284 μmolg-1 H2 production for 2.5 h. The recorded result is 15 times higher than bare TiO2 and 16 times higher than bare CuO. The synthesized materials were characterized and analyzed using various analytical techniques such as XRD, FTIR, UV-vis spectra and the morphology was studied using SEM, TEM, and HRTEM images.

Nano CaCO₃ imprinted starch hybrid polyethylhexylacrylate\\polyvinylalcohol nanocomposite thin films.

PubMed

Prusty, Kalyani; Swain, Sarat K

2016-03-30

Starch hybrid polyethylhexylacrylate (PEHA)/polyvinylalcohol (PVA) nanocomposite thin films are prepared by different composition of nano CaCO3 in aqueous medium. The chemical interaction of nano CaCO3 with PEHA in presence of starch and PVA is investigated by Fourier transforms infrared spectroscopy (FTIR). X-ray diffraction (XRD) is used in order to study the change in crystallite size and d-spacing during the formation of nanocomposite thin film. The surface morphology of nanofilms is studied by scanning electron microscope (SEM). The topology and surface roughness of the films is noticed by atomic force microscope (AFM). The tensile strength, thermal stability and thermal conductivity of films are increased with increase in concentrations of CaCO3 nanopowder. The chemical resistance and biodegradable properties of the nanocomposite thin films are also investigated. The growth of bacteria and fungi in starch hybrid PEHA film is reduced substantially with imprint of nano CaCO3. Copyright © 2015 Elsevier Ltd. All rights reserved.

Nitrate removal by Fe0/Pd/Cu nano-composite in groundwater.

PubMed

Liu, Hongyuan; Guo, Min; Zhang, Yan

2014-01-01

Nitrate pollution in groundwater shows a great threat to the safety of drinking water. Chemical reduction by zero-valent iron is being considered as a promising technique for nitrate removal from contaminated groundwater. In this paper, Fe0/Pd/Cu nano-composites were prepared by the liquid-phase reduction method, and batch experiments of nitrate reduction by the prepared Fe0/Pd/Cu nano-composites under various operating conditions were carried out. It has been found that nano-Fe0/Pd/Cu composites processed dual functions: catalytic reduction and chemical reduction. The introduction of Pd and Cu not only improved nitrate removal rate, but also reduced the generation of ammonia. Nitrate removal rate was affected by the amount of Fe0/Pd/Cu, initial nitrate concentration, solution pH, dissolved oxygen (DO), reaction temperature, the presence of anions, and organic pollutant. Moreover, nitrate reduction by Fe0/Pd/Cu composites followed the pseudo-first-order reaction kinetics. The removal rate of nitrate and total nitrogen were about 85% and 40.8%, respectively, under the reaction condition of Fe-6.0%Pd-3.0%Cu amount of 0.25 g/L, pH value of 7.1, DO of 0.42 mg/L, and initial nitrate concentration of 100 mg/L. Compared with the previous studies with Fe0 alone or Fe-Cu, nano-Fe-6%Pd-3%Cu composites showed a better selectivity to N2.

A high-performance nonenzymatic glucose sensor made of CuO-SWCNT nanocomposites.

PubMed

Quoc Dung, Nguyen; Patil, Dewyani; Jung, Hyuck; Kim, Dojin

2013-04-15

Nanocomposites of CuO and single-wall carbon nanotubes (SWCNTs) were synthesized using an arc-discharging graphite rod that contained copper wires. Simultaneous arc discharges produced a CuO-SWCNT composite network. The crystalline structure and morphology of the CuO-SWCNT composite films were investigated using XRD, Raman spectroscopy, FE-SEM and TEM. The electrochemical properties were investigated by cyclic voltammogram and amperometric measurements in a 0.1 M NaOH solution. The CuO content in the CuO-SWCNT nanocomposites was optimized for nonenzymatic glucose detection. The glucose sensing properties of the optimized CuO-SWCNT electrode showed good stability, selectivity, and linear glucose detection that ranged from 0.05 to 1800 μM with a higher sensitivity of 1610 μA cm⁻² mM⁻¹, a quick response time of 1-2 s, and the lowest limit of detection at 50 nM. The sensing performance was better than the pure CuO and SWCNT sensors, and the synergetic effect of the composite sensor was attributed to the high conductivity network of highly porous nanowires. The sensor also showed a good response in a human serum sample, which proves its high potential towards a commercial nonenzymatic glucose sensor. Copyright © 2012 Elsevier B.V. All rights reserved.

Dye sensitized solar cells using catalytically active CuO-ZnO nanocomposite synthesized by single step method

NASA Astrophysics Data System (ADS)

Abraham, Nelsa; Rufus, Alex; Unni, C.; Philip, Daizy

2018-07-01

In the present paper we report a low cost, single step preparation method for the synthesis of CuO-ZnO nanocomposite through simple co-precipitation technique using oxalic acid. To have a better idea about the deviations brought about by the inclusion of CuO in ZnO lattice, pure ZnO nanoparticles synthesized from 0.1 M solutions were also investigated. X-ray diffraction studies showed that the composite contains only hexagonal wurtzite ZnO and monoclinic CuO structures. The magnetic studies of CuO-ZnO heterostructures were also conducted in order to elucidate the source of the ferromagnetism observed at room temperature. The catalytic efficiency of the as prepared nanocomposite was estimated by the degradation of methylene blue and eosin yellowish which also shows its suitability as a promising candidate in waste water treatment. The effect of chenodeoxycholic acid as a co-adsorbent in the performance of dye sensitized solar cells fabricated using the synthesized ZnO and the nanocomposite was also studied and significant improvement in photovoltaic performance has been obtained for nanocomposite based solar cell.

Poly(vinyl acetate)/clay nanocomposite materials for organic thin film transistor application.

PubMed

Park, B J; Sung, J H; Park, J H; Choi, J S; Choi, H J

2008-05-01

Nanocomposite materials of poly(vinyl acetate) (PVAc) and organoclay were fabricated, in order to be utilized as dielectric materials of the organic thin film transistor (OTFT). Spin coating condition of the nanocomposite solution was examined considering shear viscosity of the composite materials dissolved in chloroform. Intercalated structure of the PVAc/clay nanocomposites was characterized using both wide-angle X-ray diffraction and TEM. Fracture morphology of the composite film on silicon wafer was also observed by SEM. Dielectric constant (4.15) of the nanocomposite materials shows that the PVAc/clay nanocomposites are applicable for the gate dielectric materials.

The role of surface/interfacial Cu{sup 2+} sites in the photocatalytic activity of coupled CuO-TiO{sub 2} nanocomposites.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Li, G.; Dimitrijevic, N. M.; Chen, L.

Coupled CuO-TiO{sub 2} nanocomposite photocatalysts were prepared by a deposition precipitation method and were characterized with a variety of techniques. Electron paramagnetic resonance (EPR) spectroscopy was employed to study the local structures of surface/interfacial Cu{sup 2+}+ sites using Cu{sup 2+} as a sensitive paramagnetic probe. The addition of bulk CuO to TiO{sub 2} led to decreased photocatalytic efficiency in the degradation of methylene blue. However, doping with a very small amount of CuO (0.1 wt % copper loading) significantly enhanced the photocatalytic activity of TiO{sub 2}. EPR study of the TiO{sub 2} surface revealed the presence of both highly dispersedmore » CuO clusters and substitutional Cu{sup 2+} sites (Ti-O-Cu linkages) at 0.1 wt % copper loading. The data suggest that the Ti-O-Cu linkages contributed to the improved photooxidative activity of the 0.1% CuO-TiO{sub 2} nanocomposite. In contrast, at higher loadings the bulk form of CuO created charge recombination centers lowering the photoactivity of the composites.« less

Fabrication, characterization of two nano-composite CuO-ZnO working electrodes for dye-sensitized solar cell.

PubMed

Habibi, Mohammad Hossein; Karimi, Bahareh; Zendehdel, Mahmoud; Habibi, Mehdi

2013-12-01

Two kind of CuO-ZnO nanocomposite working electrodes were synthesized by sol-gel technology and applied in dye-sensitized solar cells (DSSCs). Their characteristics were studied by field emission scanning electron microscopy (FESEM), X-ray diffraction (XRD) and UV-Vis diffuse reflectance spectrum (DRS). CuO-ZnO nanocomposite thin films were prepared doctor blade technique on the fluorine-doped tin oxide (FTO) and used as working electrodes in dye sensitized solar cells (DSSC). Their photovoltaic behavior were compared with standard using D35 dye and an electrolyte containing [Co(bpy)3](PF6)2, [Co(pby)3](PF6)3, LiClO4, and 4-tert-butylpyridine (TBP). The ranges of short-circuit current (JSC) from 0.18 to 0.21 (mA/cm(2)), open-circuit voltage (VOC) from 0.24 to 0.55V, and fill factor from 0.34 to 0.39 were obtained for the DSSCs made using the working electrodes. The efficiency of the working electrodes after the addition of TBL was more than doubled. The light scattering and carrier transport properties of these composites promote the performance of dye-sensitized solar cells (DSSCs). Copyright © 2013 Elsevier B.V. All rights reserved.

A facile one-pot hydrothermal approach for the preparation of CuO/rGO nanocomposites with different morphologies

NASA Astrophysics Data System (ADS)

Ajit, Akshata V.; Gawli, Yogesh P.; Ethiraj, Anita Sagadevan

2018-05-01

Graphene-based metal oxides such as Cu2O, SnO2, CuO, Fe3O4, MnO2 are promising candidates for many applications because of their advantageous properties. Amongst all, CuO has been widely studied because of its excellent electrocatalytic activity. Although many methodologies have been developed for the synthesis of CuO/graphene nanostructures with different morphologies including nanorods, nanoparticles, nanosheets, flower, urchin; not many investigations have been done on one pot synthesis method for CuO/reduced graphene oxide (rGO) nanocomposites to achieve different morphologies. Therefore in the present work effort has been made to synthesize various CuO-rGO nanocomposites via surfactant (CTAB) assisted hydrothermal method. Detailed study was performed to monitor the effect of various reaction parameters like temperature, reaction time, reactant concentration on the synthesized nanocomposites. Several analytical tools, including XRD, SEM, FTIR and UV-Vis spectroscopy have been utilized to characterize the samples. XRD results showed formation of monoclinic structure of CuO along with presence of rGO. Calculated optical bandgap studies indicate decrease in the bandgap of synthesized CuO (Eg=4.5eV-4.34eV) with increase in temperature from 120°C to 180°C. Our results clearly demonstrate that reaction parameters play a key role to bring out the optical and morphological changes in the CuO-rGO nanocomposites.

Preparation, characterization and application of dispersible and spherical Nano-SiO2@Copolymer nanocomposite in leather tanning

NASA Astrophysics Data System (ADS)

Pan, Hui; Li, Guang-Long; Liu, Rui-Qi; Wang, Su-Xia; Wang, Xiao-Dong

2017-12-01

Dispersible and spherical silica nanoparticles (nano-SiO2) were prepared with tetraethyl silicate and different surface-modifiers via a simple method. The silica nanoparticles surface-modified with methacryloxy (propyl) trimethoxysilane (denoted as MPS-SiO2), dimethyl diallyl ammoniumchloride (denoted as DMDAAC-SiO2) and poly (methacrylic acid) (denoted as PMAA-SiO2) which are known as hydrophobic, amphiphilic and hydrophilic modifiers, respectively, exhibited excellent dispersibility in various solvents or polymer matrix. The obtained bare silica nanoparticles, MPS-SiO2, DMDAAC-SiO2 and PMAA-SiO2 were characterized by Fourier transform infrared spectra (FTIR), thermogravimetric analysis (TGA), transmission electron microscope (TEM) and scanning electron microscope (SEM). A series of nanocomposites (denoted as SiO2/P, MPS-SiO2/P, DMDAAC-SiO2/P and PMAA-SiO2/P, respectively) were also prepared with the bare or surface-modified silica nanoparticles and methacrylic acid-co-acrylamide-co-acrylonitrile-co-salicylic acid tetrabasic copolymer (denoted as PMAAS) and applied in leather tanning. Compared with those of the leather tanned with the commercial acrylic resin (CHINATAN OM) and pure tetrabasic copolymer tanning agents, the physical and mechanical properties, rheological properties and thermal stabilities of the leather treated with SiO2/P, MPS-SiO2/P, DMDAAC-SiO2/P or PMAA-SiO2/P founded to be improved in a significant way. Moreover, the highest shrinkage temperature of the wet-white sheepskin tanned with PMAA-SiO2/P reached to 76 °C and the thickness increase reached to 105%.

In Situ Ramp Anneal X-ray Diffraction Study of Atomic Layer Deposited Ultrathin TaN and Ta 1-x Al x N y Films for Cu Diffusion Barrier Applications

DOE Office of Scientific and Technical Information (OSTI.GOV)

Consiglio, S.; Dey, S.; Yu, K.

2016-01-01

Ultrathin TaN and Ta 1-xAl xN y films with x = 0.21 to 0.88 were deposited by atomic layer deposition (ALD) and evaluated for Cu diffusion barrier effectiveness compared to physical vapor deposition (PVD) grown TaN. Cu diffusion barrier effectiveness was investigated using in-situ ramp anneal synchrotron X-ray diffraction (XRD) on Cu/1.8 nm barrier/Si stacks. A Kissinger-like analysis was used to assess the kinetics of Cu 3Si formation and determine the effective activation energy (E a) for Cu silicidation. Compared to the stack with a PVD TaN barrier, the stacks with the ALD films exhibited a higher crystallization temperature (Tmore » c) for Cu silicidation. The Ea values of Cu 3Si formation for stacks with the ALD films were close to the reported value for grain boundary diffusion of Cu whereas the Ea of Cu 3Si formation for the stack with PVD TaN is closer to the reported value for lattice diffusion. For 3 nm films, grazing incidence in-plane XRD showed evidence of nanocrystallites in an amorphous matrix with broad peaks corresponding to high density cubic phase for the ALD grown films and lower density hexagonal phase for the PVD grown film further elucidating the difference in initial failure mechanisms due to differences in barrier crystallinity and associated phase.« less

Synergetic Effect of Graphene and MWCNTs on Microstructure and Mechanical Properties of Cu/Ti3SiC2/C Nanocomposites

NASA Astrophysics Data System (ADS)

Jiang, Xiaosong; Song, Tingfeng; Shao, Zhenyi; Liu, Wanxia; Zhu, Degui; Zhu, Minhao

2017-11-01

Multi-walled carbon nanotubes (MWCNTs) and graphenes have been taken for novel reinforcements due to their unique structure and performance. However, MWCNTs or graphenes reinforced copper matrix composites could not catch up with ideal value due to reinforcement dispersion in metal matrix, wettability to metal matrix, and composite material interface. Taking advantage of the superior properties of one-dimensional MWCNTs and two-dimensional graphenes, complementary performance and structure are constructed to create a high contact area between MWCNTs and graphenes to the Cu matrix. Mechanical alloying, hot pressing, and hot isostatic pressing techniques are used to fabricate Cu matrix self-lubricating nanocomposites. Effects of MWCNTs and graphenes on mechanical properties and microstructures of Cu/Ti3SiC2/C nanocomposites are studied. The fracture and strengthening mechanisms of Cu/Ti3SiC2/C nanocomposites are explored on the basis of structure and composition of Cu/Ti3SiC2/C nanocomposites with formation and function of interface.

Novel Preparation of Nano-Composite CuO-Cr2O3 Using Ctab-Template Method and Efficient for Hydrogenation of Biomass-Derived Furfural

NASA Astrophysics Data System (ADS)

Yan, Kai; Wu, Xu; An, Xia; Xie, Xianmei

2013-02-01

A simple route to fabricate nano-composite oxides CuO-Cr2O3 using hexadecyltrimethylammonium bromide (CTAB)-templated Cu-Cr hydrotalcite as the precursor is presented. This novel method is based on CTAB-templating effect for mesostructure directing and using the cheap metal nitrate, followed by removal of CTAB. It was indicated that the nano-composite CuO-Cr2O3 was formed during the removal of CTAB. X-ray diffraction (XRD) and transitional electronic microscopy (TEM) revealed nice nano-composite oxides CuO-Cr2O3 were formed with high crystallinity. N2 adsorption and desorption indicated that a high surface area of 170.5 m2/g with a pore size of 2.7 nm of the nano-composite CuO-Cr2O3 was facilely resulted. The as-synthesized nano-composite oxides CuO-Cr2O3 display good catalytic activities for hydrogenation of furfural to furfuryl alcohol, whereas 86% selectivity was achieved at 75% conversion of furfural.

Optical, mechanical and structural properties of PMMA/SiO2 nanocomposite thin films

NASA Astrophysics Data System (ADS)

Soni, Gyanesh; Srivastava, Subodh; Soni, Purushottam; Kalotra, Pankaj; Vijay, Y. K.

2018-01-01

We have fabricated PMMA/SiO2 nanocomposite flexible thin films of 60 μm thicknesses by using solution casting method in the presence of transverse electric field. In this paper, we have investigated the effect of SiO2 nanoparticle (NP) loading on optical and mechanical properties of the composite thin film. The SEM images show that nanocomposite thin films have a smoother and uniform morphology. The transmittance peak near 1103 cm-1 in FT-IR spectrum confirms the presence of SiO2 NPs in the composite thin film. It is observed that optical bandgap decreases with an increase in the SiO2 NP concentration. Dynamic mechanical analysis shows that presence of SiO2 NP enhances the mechanical strength of the composite thin film.

Optical properties of diamond like carbon nanocomposite thin films

NASA Astrophysics Data System (ADS)

Alam, Md Shahbaz; Mukherjee, Nillohit; Ahmed, Sk. Faruque

2018-05-01

The optical properties of silicon incorporated diamond like carbon (Si-DLC) nanocomposite thin films have been reported. The Si-DLC nanocomposite thin film deposited on glass and silicon substrate by radio frequency plasma enhanced chemical vapor deposition (RF-PECVD) process. Fourier transformed infrared spectroscopic analysis revealed the presence of different bonding within the deposited films and deconvolution of FTIR spectra gives the chemical composition i.e., sp3/sp2 ratio in the films. Optical band gap calculated from transmittance spectra increased from 0.98 to 2.21 eV with a variation of silicon concentration from 0 to 15.4 at. %. Due to change in electronic structure by Si incorporation, the Si-DLC film showed a broad photoluminescence (PL) peak centered at 467 nm, i.e., in the visible range and its intensity was found to increase monotonically with at. % of Si.

Two-dimensional Ag/SiO2 and Cu/SiO2 nanocomposite surface-relief grating couplers and their vertical input coupling properties

NASA Astrophysics Data System (ADS)

Wang, Jun; Mu, Xiaoyu; Wang, Gang; Liu, Changlong

2017-11-01

By etching two SiO2 optical waveguide slabs separately implanted with 90 keV Ag ions and 60 keV Cu ions at the same dose of 6 × 1016 cm-2, two-dimensional Ag/SiO2 and Cu/SiO2 nanocomposite surface-relief grating couplers with 600-nm periodicity and 100-nm thickness were fabricated, and their structural and vertical input coupling properties were investigated. Experimental results revealed that the two couplers could convert light beams at wavelengths of 620-880 nm into guided waves with different efficiencies, highlighting the special importance of metal nanoparticles (NPs). Further discussions also revealed that owing to the introduction of periodically distributed metal NPs, the periodical phase modification of the transmitted beam was enhanced drastically, and the nanocomposite veins could behave as efficient light scatterers. As a result, the two couplers were much larger in coupling efficiency than the NP-free one with identical morphological parameters. The above findings may be useful to construct thin and short but efficient surface-relief grating couplers on glass optical waveguides.

Achieving 3-D Nanoparticle Assembly in Nanocomposite Thin Films via Kinetic Control

DOE Office of Scientific and Technical Information (OSTI.GOV)

Huang, Jingyu; Xiao, Yihan; Xu, Ting

Nanocomposite thin films containing well-ordered nanoparticle (NP) assemblies are ideal candidates for the fabrication of metamaterials. Achieving 3-D assembly of NPs in nanocomposite thin films is thermodynamically challenging as the particle size gets similar to that of a single polymer chain. The entropic penalties of polymeric matrix upon NP incorporation leads to NP aggregation on the film surface or within the defects in the film. Controlling the kinetic pathways of assembly process provides an alternative path forward by arresting the system in nonequilibrium states. Here, we report the thin film 3-D hierarchical assembly of 20 nm NPs in supramolecules withmore » a 30 nm periodicity. By mediating the NP diffusion kinetics in the supramolecular matrix, surface aggregation of NPs was suppressed and NPs coassemble with supramolecules to form new 3-D morphologies in thin films. Lastly, the present studies opened a viable route to achieve designer functional composite thin films via kinetic control.« less

Achieving 3-D Nanoparticle Assembly in Nanocomposite Thin Films via Kinetic Control

DOE Office of Scientific and Technical Information (OSTI.GOV)

Huang, Jingyu; Xiao, Yihan; Xu, Ting

Nanocomposite thin films containing well-ordered nanoparticle (NP) assemblies are ideal candidates for the fabrication of metamaterials. Achieving 3-D assembly of NPs in nanocomposite thin films is thermodynamically challenging as the particle size gets similar to that of a single polymer chain. The entropic penalties of polymeric matrix upon NP incorporation leads to NP aggregation on the film surface or within the defects in the film. Controlling the kinetic pathways of assembly process provides an alternative path forward by arresting the system in nonequilibrium states. Here, we report the thin film 3-D hierarchical assembly of 20 nm NPs in supramolecules withmore » a 30 nm periodicity. By mediating the NP diffusion kinetics in the supramolecular matrix, surface aggregation of NPs was suppressed and NPs coassemble with supramolecules to form new 3-D morphologies in thin films. The present studies opened a viable route to achieve designer functional composite thin films via kinetic control.« less

Achieving 3-D Nanoparticle Assembly in Nanocomposite Thin Films via Kinetic Control

DOE PAGES

Huang, Jingyu; Xiao, Yihan; Xu, Ting

2017-02-20

Nanocomposite thin films containing well-ordered nanoparticle (NP) assemblies are ideal candidates for the fabrication of metamaterials. Achieving 3-D assembly of NPs in nanocomposite thin films is thermodynamically challenging as the particle size gets similar to that of a single polymer chain. The entropic penalties of polymeric matrix upon NP incorporation leads to NP aggregation on the film surface or within the defects in the film. Controlling the kinetic pathways of assembly process provides an alternative path forward by arresting the system in nonequilibrium states. Here, we report the thin film 3-D hierarchical assembly of 20 nm NPs in supramolecules withmore » a 30 nm periodicity. By mediating the NP diffusion kinetics in the supramolecular matrix, surface aggregation of NPs was suppressed and NPs coassemble with supramolecules to form new 3-D morphologies in thin films. Lastly, the present studies opened a viable route to achieve designer functional composite thin films via kinetic control.« less

Compositional ratio effect on the surface characteristics of CuZn thin films

NASA Astrophysics Data System (ADS)

Choi, Ahrom; Park, Juyun; Kang, Yujin; Lee, Seokhee; Kang, Yong-Cheol

2018-05-01

CuZn thin films were fabricated by RF co-sputtering method on p-type Si(100) wafer with various RF powers applied on metallic Cu and Zn targets. This paper aimed to determine the morphological, chemical, and electrical properties of the deposited CuZn thin films by utilizing a surface profiler, atomic force microscopy (AFM), X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), Auger electron spectroscopy (AES), UV photoelectron spectroscopy (UPS), and a 4-point probe. The thickness of the thin films was fixed at 200 ± 8 nm and the roughness of the thin films containing Cu was smaller than pure Zn thin films. XRD studies confirmed that the preferred phase changed, and this tendency is dependent on the ratio of Cu to Zn. AES spectra indicate that the obtained thin films consisted of Cu and Zn. The high resolution XPS spectra indicate that as the content of Cu increased, the intensities of Zn2+ decreased. The work function of CuZn thin films increased from 4.87 to 5.36 eV. The conductivity of CuZn alloy thin films was higher than pure metallic thin films.

Nonenzymatic amperometric determination of glucose by CuO nanocubes-graphene nanocomposite modified electrode.

PubMed

Luo, Liqiang; Zhu, Limei; Wang, Zhenxin

2012-12-01

Here, we report a nonenzymatic amperometric glucose sensor based on copper oxide (CuO) nanocubes-graphene nanocomposite modified glassy carbon electrode (CuO-G-GCE). In this case, the graphene sheets were cast on the GCE directly. CuO nanocubes were obtained by oxidizing electrochemically deposited Cu on the graphene. The morphology of CuO-G nanocomposite was characterized by scanning electron microscopy. The CuO-G-GCE-based sensor exhibited excellent electrocatalytic activity and high stability for glucose oxidation. Under optimized conditions, the linearity between the current response and the glucose concentration was obtained in the range of 2μM to 4mM with a detection limit of 0.7μM (S/N=3), and a high sensitivity of 1360μAmM(-1)cm(-2). The proposed electrode showed a fast response time (less than 5s) and a good reproducibility. The as-made sensor was applied to determine the glucose levels in clinic human serum samples with satisfactory results. In addition, the effects of common interfering species, including ascorbic acid, uric acid, dopamine and other carbohydrates, on the amperometric response of the sensor were investigated and discussed in detail. Copyright © 2012 Elsevier B.V. All rights reserved.

Photocatalytic properties and selective antimicrobial activity of TiO2(Eu)/CuO nanocomposite

NASA Astrophysics Data System (ADS)

Michal, Robert; Dworniczek, Ewa; Caplovicova, Maria; Monfort, Olivier; Lianos, Panagiotis; Caplovic, Lubomir; Plesch, Gustav

2016-05-01

TiO2(Eu)/CuO nanocomposites were prepared by precipitation method. The anatase nanocrystallites with a size of 26 nm exhibited well crystallized and characteristical dipyramidal morphology and {1 0 1} and {0 0 1} faceting. Transmission electron microscopy photographs with atomic resolution showed that the Eu(III) dopants were bounded on surface of titania. In the composites, the CuO nanocrystals exhibiting a monoclinic tenorite structure with a size in the range from 2 to 5 nm were grafted to the surface of titania. The influence of copper(II) oxide led to distinct selectivity in the photocatalytic and antimicrobial properties of the investigated TiO2(Eu)/CuO nanocomposites. While the presence of CuO nanocrystals strongly increased the photocatalytic production of hydrogen by ethanol reforming, it decreased the activity in photoinduced total mineralization of phenol comparing with non-modified TiO2(Eu). In investigated TiO2(Eu)/CuO powders, the photoinduced antimicrobial activity against membranes of Enterococcus species was influenced by the selective binding of CuO to the surface of the microorganism leading to distinct selectivity in their action. The activity against Enterococcus faecalis was higher than against Enterococcus faecium.

Direct laser sintered WC-10Co/Cu nanocomposites

NASA Astrophysics Data System (ADS)

Gu, Dongdong; Shen, Yifu

2008-04-01

In the present work, the direct metal laser sintering (DMLS) process was used to prepare the WC-Co/Cu nanocomposites in bulk form. The WC reinforcing nanoparticles were added in the form of WC-10 wt.% Co composite powder. The microstructural features and mechanical properties of the laser-sintered sample were characterized by X-ray diffraction (XRD), atomic force microscope (AFM), scanning electron microscope (SEM), energy dispersive X-ray spectroscope (EDX), and nanoindentation tester. It showed that the original nanometric nature of the WC reinforcing particulates was well retained without appreciable grain growth after laser processing. A homogeneous distribution of the WC reinforcing nanoparticles with a coherent particulate/matrix interfacial bonding was obtained in the laser-sintered structure. The 94.3% dense nanocomposites have a dynamic nanohardness of 3.47 GPa and a reduced elastic modulus of 613.42 GPa.

A comparative study of heterostructured CuO/CuWO4 nanowires and thin films

NASA Astrophysics Data System (ADS)

Polyakov, Boris; Kuzmin, Alexei; Vlassov, Sergei; Butanovs, Edgars; Zideluns, Janis; Butikova, Jelena; Kalendarev, Robert; Zubkins, Martins

2017-12-01

A comparative study of heterostructured CuO/CuWO4 core/shell nanowires and double-layer thin films was performed through X-ray diffraction, confocal micro-Raman spectroscopy and electron (SEM and TEM) microscopies. The heterostructures were produced using a two-step process, starting from a deposition of amorphous WO3 layer on top of CuO nanowires and thin films by reactive DC magnetron sputtering and followed by annealing at 650 °C in air. The second step induced a solid-state reaction between CuO and WO3 oxides through a thermal diffusion process, revealed by SEM-EDX analysis. Morphology evolution of core/shell nanowires and double-layer thin films upon heating was studied by electron (SEM and TEM) microscopies. A formation of CuWO4 phase was confirmed by X-ray diffraction and confocal micro-Raman spectroscopy.

Synthesis and characterization of new nanocomposites films using alanine-Cu-functionalized graphene oxide as nanofiller and PVA as polymeric matrix for improving of their properties

NASA Astrophysics Data System (ADS)

Abdolmaleki, Amir; Mallakpour, Shadpour; Karshenas, Azam

2017-09-01

In the synthesis of polymer-graphene nanocomposites, for improving properties of nanocomposites, two factors dispersion and strong interfacial interactions between graphene and the polymer, are essential. In the present work, poly(vinyl alcohol) PVA/GO-Cu-alanine nanocomposite films were manufactured using concentrations 0, 1, 3 and 5 wt% of GO-Cu-alanine in water solution. For this purpose, L-alanine amino acid was located on the surface and edges of GO through copper(II) ion as a coordinating function. Then, flexible PVA/GO-Cu-alanine nanocomposite films were fabricated using GO-Cu-alanine as filler and PVA as matrix. Due to the existence of affective interaction between GO-Cu-alanine and PVA matrix, the acquired PVA/GO-Cu-alanine nanocomposites demonstrated great thermal and mechanical properties. Properties of manufactured materials were characterized by Fourier transform infrared, X-ray photoelectron spectroscopies (XPS), X-ray diffraction (XRD), Thermal gravimetric analysis, elemental analysis, field emission scanning electron microscopy, transmission electron microscopy and energy dispersive X-ray spectroscopy (EDX).

Passive optical limiting studies of nanostructured Cu doped ZnO-PVA composite thin films

NASA Astrophysics Data System (ADS)

Tamgadge, Y. S.; Sunatkari, A. L.; Talwatkar, S. S.; Pahurkar, V. G.; Muley, G. G.

2016-01-01

We prepared undoped and Cu doped ZnO semiconducting nanoparticles (NPs) by chemical co-precipitation method and obtained Cu doped ZnO-polyvinyl alcohol (PVA) nanocomposite thin films by spin coating to investigate third order nonlinear optical and optical limiting properties under cw laser excitation. Powder samples of NPs were characterized by X-ray diffraction (XRD), field emission scanning electron microscopy (FE-SEM), energy dispersive spectroscopy, transmission electron microscopy, ultraviolet-visible (UV-vis) and Fourier transform infrared spectroscopy. XRD pattern and FE-SEM micrograph revealed the presence of hexagonal wurtzite phase ZnO NPs having uniform morphology with average particle size of 20 nm. The presence of excitons and absorption peaks in the range 343-360 nm, revealed by UV-vis study, were attributed to excitons in n = 1 quantum state. Third order NLO properties of all composite thin films were investigated by He-Ne continuous wave (cw) laser of wavelength 632.8 nm using Z-scan technique. Thermally stimulated enhanced values of nonlinear refraction and absorption coefficients were obtained which may be attributed to self-defocusing effect, reverse saturable absorption, weak free carrier absorption and surface states properties originated from thermo optic effect. Optical limiting properties have been studied using cw diode laser of wavelength 808 nm and results are presented.

Switchable 3-0 magnetoelectric nanocomposite thin film with high coupling.

PubMed

McDannald, Austin; Ye, Linghan; Cantoni, Claudia; Gollapudi, Sreenivasulu; Srinivasan, Gopalan; Huey, Bryan D; Jain, Menka

2017-03-02

A mixed precursor solution method was used to deposit 3-0 nanocomposite thin films of PbZr 0.52 Ti 0.48 O 3 (PZT) and CoFe 2 O 4 (CFO). The piezoelectric behavior of PZT and magnetostrictive behavior of CFO allow for magnetoelectric (ME) coupling through strain transfer between the respective phases. High ME coupling is desired for many applications including memory devices, magnetic field sensors, and energy harvesters. The spontaneous phase separation in the 3-0 nanocomposite film was observed, with 25 nm CFO particle or nanophases distributed in discrete layers through the thickness of the PZT matrix. Magnetic-force microscopy images of the nanocomposite thin film under opposite magnetic poling conditions revealed in-plane pancake-like regions of higher concentration of the CFO nanoparticles. The constraints on the size and distribution of the CFO nanoparticles created a unique distribution in a PZT matrix and achieved values of ME coupling of 3.07 V cm -1 Oe -1 at a DC bias of 250 Oe and 1 kHz, increasing up to 25.0 V cm -1 Oe -1 at 90 kHz. Piezo-force microscopy was used to investigate the ferroelectric domain structure before and after opposite magnetic poling directions. It was found that in this nanocomposite, the polarization of the ferroelectric domains switched direction as a result of switching the direction of the magnetization by magnetic fields.

Preparation of Cu2O-Reduced Graphene Nanocomposite Modified Electrodes towards Ultrasensitive Dopamine Detection

PubMed Central

He, Quanguo; Liu, Jun; Liu, Xiaopeng; Li, Guangli; Deng, Peihong; Liang, Jing

2018-01-01

Cu2O-reduced graphene oxide nanocomposite (Cu2O-RGO) was used to modify glassy carbon electrodes (GCE), and applied for the determination of dopamine (DA). The microstructure of Cu2O-RGO nanocomposite material was characterized by scanning electron microscope. Then the electrochemical reduction condition for preparing Cu2O-RGO/GCE and experimental conditions for determining DA were further optimized. The electrochemical behaviors of DA on the bare electrode, RGO- and Cu2O-RGO-modified electrodes were also investigated using cyclic voltammetry in phosphate-buffered saline solution (PBS, pH 3.5). The results show that the oxidation peaks of ascorbic acid (AA), dopamine (DA), and uric acid (UA) could be well separated and the peak-to-peak separations are 204 mV (AA-DA) and 144 mV (DA-UA), respectively. Moreover, the linear response ranges for the determination of 1 × 10−8 mol/L~1 × 10−6 mol/L and 1 × 10−6 mol/L~8 × 10−5 mol/L with the detection limit 6.0 × 10−9 mol/L (S/N = 3). The proposed Cu2O-RGO/GCE was further applied to the determination of DA in dopamine hydrochloride injections with satisfactory results. PMID:29329206

Possibility to Use Hydrothermally Synthesized CuFeS2 Nanocomposite as an Acceptor in Hybrid Solar Cell

NASA Astrophysics Data System (ADS)

Sil, Sayantan; Dey, Arka; Halder, Soumi; Datta, Joydeep; Ray, Partha Pratim

2018-01-01

Here we have approached the plausible use of CuFeS2 nanocomposite as an acceptor in organic-inorganic hybrid solar cell. To produce CuFeS2 nanocomposite, hydrothermal strategy was employed. The room-temperature XRD pattern approves the synthesized material as CuFeS2 with no phase impurity (JCPDS Card no: 37-0471). The elemental composition of the material was analyzed from the TEM-EDX data. The obtained selected area electron diffraction (SAED) planes harmonized with the XRD pattern of the synthesized product. Optical band gap (4.14 eV) of the composite from UV-Vis analysis depicts that the synthesized material is belonging to wide band gap semiconductor family. The HOMO (- 6.97 eV) and LUMO (- 2.93 eV) positions from electrochemical study reveal that there is a possibility of electron transfer from MEH-PPV to CuFeS2. The optical absorption and photoluminescence spectra of MEH-PPV:CuFeS2 (donor:acceptor) composite were recorded sequentially by varying weight ratios. The monotonic blue shifting of the absorption peak position indicated the interaction between donor and acceptor materials. The possibility of electron transfer from donor (MEH-PPV) to acceptor (CuFeS2) was approved with photoluminescence analysis. Subsequently, we have fabricated a hybrid solar cell by incorporating CuFeS2 nanocomposite with MEH-PPV in open atmosphere and obtained 0.3% power conversion efficiency.

Epitaxial YBa2Cu3O7-x nanocomposite films and coated conductors from BaMO3 (M = Zr, Hf) colloidal solutions

NASA Astrophysics Data System (ADS)

Obradors, X.; Puig, T.; Li, Z.; Pop, C.; Mundet, B.; Chamorro, N.; Vallés, F.; Coll, M.; Ricart, S.; Vallejo, B.; Pino, F.; Palau, A.; Gázquez, J.; Ros, J.; Usoskin, A.

2018-04-01

Superconducting nanocomposites are the best material choice to address the performance required in power applications and magnets working under high magnetic fields. However, it is still challenging to sort out how to achieve the highest superconducting performance using attractive and competitive manufacturing processes. Colloidal solutions have been recently developed as a novel and very promising low cost route to manufacture nanocomposite coated conductors. Well dispersed and stabilized preformance nanoparticle solutions are first prepared with high concentrations and then mixed with the YBa2Cu3O7 metalorganic precursor solutions to generate colloidal solutions to grow the nanocomposite films. Here we demonstrate, for the first time, that non-reactive BaZrO3 and BaHfO3 perovskite preformed nanoparticles are suitable for growing high quality thin and thick films, and coated conductors with a homogeneous distribution and controlled particle size using this fabrication method. Additionally, we extend the nanoparticle content of the nanocomposites up to 20%-25% mol without any degradation of the superconducting properties. Thick nanocomposite films, up to 0.8 μm, have been prepared with a single deposition of low-fluorine solutions using an ink jet printing dispenser and we demonstrate that the preformed nanoparticles display only a very limited coarsening during the growth process and so high critical current densities J c (B) under high magnetic fields. These films show the highest critical currents achieved so far based on the colloidal solution approach, I c = 220 A/cm-w at 77 K and self-field, and they still have a high potential for further increase in the film thickness. Finally, we also show that nanocomposite YBa2Cu3O7-BaZrO3 coated conductors based on an alternating beam assisted deposited YSZ buffer layer on stainless steel metallic substrates can be developed based on these novel colloidal solutions. Non-reactive preformed oxide perovskite

Investigation of the nanostructure and wear properties of physical vapor deposited CrCuN nanocomposite coatings

NASA Astrophysics Data System (ADS)

Baker, M. A.; Kench, P. J.; Tsotsos, C.; Gibson, P. N.; Leyland, A.; Matthews, A.

2005-05-01

This article presents results on CrCuN nanocomposite coatings grown by physical vapor deposition. The immiscibility of Cr (containing a supersaturation of nitrogen) and Cu offers the potential of depositing a predominantly metallic (and therefore tough) nanocomposite, composed of small Cr(N) metallic and/or β-Cr2N ceramic grains interdispersed in a (minority) Cu matrix. A range of CrCuN compositions have been deposited using a hot-filament enhanced unbalanced magnetron sputtering system. The stoichiometry and nanostructure have been studied by x-ray photoelectron spectroscopy, transmission electron microscopy, scanning electron microscopy, and x-ray diffraction. Hardness, wear resistance, and impact resistance have been determined by nanoindentation, reciprocating-sliding, and ball-on-plate high-cycle impact. Evolution of the nanostructure as a function of composition and correlations of the nanostructure and mechanical properties of the CrCuN coatings are discussed. A nanostructure comprised of 1-3 nm α-Cr(N) and β-Cr2N grains separated by intergranular regions of Cu gives rise to a coating with significantly enhanced resistance to impact wear.

Dielectric property study of poly(4-vinylphenol)-graphene oxide nanocomposite thin film

NASA Astrophysics Data System (ADS)

Roy, Dhrubojyoti

2018-05-01

Thin film capacitor device having a sandwich structure of indium tin oxide (ITO)-coated glass/polymer or polymer nanocomposite /silver has been fabricated and their dielectric and leakage current properties has been studied. The dielectric properties of the capacitors were characterized for frequencies ranging from 1 KHz to 1 MHz. 5 wt% Poly(4-vinylphenol)(PVPh)-Graphene (GO) nanocomposite exhibited an increase in dielectric constant to 5.6 and small rise in dielectric loss to around˜0.05 at 10 KHz w.r.t polymer. The DC conductivity measurements reveal rise of leakage current in nanocomposite.

Interpreting Neutron Reflectivity Profiles of Diblock Copolymer Nanocomposite Thin Films Using Hybrid Particle-Field Simulations

DOE Office of Scientific and Technical Information (OSTI.GOV)

Mahalik, Jyoti P.; Dugger, Jason W.; Sides, Scott W.

Mixtures of block copolymers and nanoparticles (block copolymer nanocomposites) are known to microphase separate into a plethora of microstructures, depending on the composition, length scale and nature of interactions among its different constituents. Theoretical and experimental works on this class of nanocomposites have already high-lighted intricate relations among chemical details of the polymers, nanoparticles, and various microstructures. Confining these nanocomposites in thin films yields an even larger array of structures, which are not normally observed in the bulk. In contrast to the bulk, exploring various microstructures in thin films by the experimental route remains a challenging task. Here in thismore » work, we construct a model for the thin films of lamellar forming diblock copolymers containing spherical nanoparticles based on a hybrid particle-field approach. The model is benchmarked by comparison with the depth profiles obtained from the neutron reflectivity experiments for symmetric poly(deuterated styrene-b-n butyl methacrylate) copolymers blended with spherical magnetite nanoparticles covered with hydrogenated poly(styrene) corona. We show that the model based on a hybrid particle-field approach provides details of the underlying microphase separation in the presence of the nanoparticles through a direct comparison to the neutron reflectivity data. This work benchmarks the application of the hybrid particle-field model to extract the interaction parameters for exploring different microstructures in thin films containing block copolymers and nanocomposites.« less

Interpreting Neutron Reflectivity Profiles of Diblock Copolymer Nanocomposite Thin Films Using Hybrid Particle-Field Simulations

DOE PAGES

Mahalik, Jyoti P.; Dugger, Jason W.; Sides, Scott W.; ...

2018-04-10

Mixtures of block copolymers and nanoparticles (block copolymer nanocomposites) are known to microphase separate into a plethora of microstructures, depending on the composition, length scale and nature of interactions among its different constituents. Theoretical and experimental works on this class of nanocomposites have already high-lighted intricate relations among chemical details of the polymers, nanoparticles, and various microstructures. Confining these nanocomposites in thin films yields an even larger array of structures, which are not normally observed in the bulk. In contrast to the bulk, exploring various microstructures in thin films by the experimental route remains a challenging task. Here in thismore » work, we construct a model for the thin films of lamellar forming diblock copolymers containing spherical nanoparticles based on a hybrid particle-field approach. The model is benchmarked by comparison with the depth profiles obtained from the neutron reflectivity experiments for symmetric poly(deuterated styrene-b-n butyl methacrylate) copolymers blended with spherical magnetite nanoparticles covered with hydrogenated poly(styrene) corona. We show that the model based on a hybrid particle-field approach provides details of the underlying microphase separation in the presence of the nanoparticles through a direct comparison to the neutron reflectivity data. This work benchmarks the application of the hybrid particle-field model to extract the interaction parameters for exploring different microstructures in thin films containing block copolymers and nanocomposites.« less

Electrochemical and physical properties of electroplated CuO thin films.

PubMed

Dhanasekaran, V; Mahalingam, T

2013-01-01

Cupric oxide thin films have been prepared on ITO glass substrates from an aqueous electrolytic bath containing CuSO4 and tartaric acid. Growth mechanism has been analyzed using cyclic voltammetry. The role of pH on the structural, morphological, compositional, electrical and optical properties of CuO films is investigated. The structural studies revealed that the deposited films are polycrystalline in nature with a cubic structure. The preferential orientation of CuO thin films is found to be along (111) plane. X-ray line profile analysis has been carried out to determine the microstructural parameters of CuO thin films. The pyramid shaped grains are observed from SEM and AFM images. The optical band gap energy and electrical activation energy is found to be 1.45 and 0.37 eV, respectively. Also, the optical constants of CuO thin films such as refractive index (n), complex dielectric constant (epsilon) extinction coefficient (k) and optical conductivity (sigma) are evaluated.

Solid-phase microextraction of methadone in urine samples by electrochemically co-deposited sol-gel/Cu nanocomposite fiber.

PubMed

Mohammadiazar, Sirwan; Hasanli, Fateme; Maham, Mehdi; Payami Samarin, Somayeh

2017-08-01

Electrochemically co-deposited sol-gel/Cu nanocomposites have been introduced as a novel, simple and single-step technique for preparation of solid-phase microextraction (SPME) coating to extract methadone (MDN) (a synthetic opioid) in urine samples. The porous surface structure of the sol-gel/Cu nanocomposite coating was revealed by scanning electron microscopy. Direct immersion SPME followed by HPLC-UV determination was employed. The factors influencing the SPME procedure, such as the salt content, desorption solvent type, pH and equilibration time, were optimized. The best conditions were obtained with no salt content, acetonitrile as desorption solvent type, pH 9 and 10 min equilibration time. The calibration graphs for urine samples showed good linearity. The detection limit was about 0.2 ng mL -1 . Also, the novel method for preparation of nanocomposite fiber was compared with previously reported techniques for MDN determination. The results show that the novel nanocomposite fiber has relatively high extraction efficiency. Copyright © 2016 John Wiley & Sons, Ltd.

To study the effect of calcinations durations and temperature on optical and structural properties of MgO-CuO nanocomposites

NASA Astrophysics Data System (ADS)

Kumar, Rajesh; Praveen, Sharma, Ashwani; Parmar, R.; Dahiya, S.; Kishor, N.

2016-05-01

The MgO-CuO nanocomposites has been synthesized by a sol-gel techniques based on precursor polyvinyl alcohol (PVA). In this work appropriate concentration of cupric nitrate, Magnisium nitrate and PVA are mixed with 50:50 ethanol water followed by heated to 80°C to form a homogeneous gel solution. The obtained gel was slowly heated at 100°C to evaporate the solvent to form a hard homogeneous gel. The hard gel was calcinated at temperature 600°C for 4 hrs and 6 hrs thereafter, crushed the material in agate-motar so that it is converted into fine powder form. The prepared nanocomposites have been characterized using X-Ray Diffraction (XRD), FTIR, UV-VIS spectroscopy, SEM etc. The size of MgO-CuO nanocomposites heated at 600°C for 4 hours and 6 hours evaluated by Debye Scherrer formula are 17.1 nm and 21.2 nm respectively and results show that Size of MgO-CuO nanocomposites increases with increase of calcinations durations. IR spectra is also used to determine purity of samples. Absorption spectra confirm the synthesis of nanomaterials. SEM images give the indication of morphology of the nanocomposites.

Thermal conversion of Cu4O3 into CuO and Cu2O and the electrical properties of magnetron sputtered Cu4O3 thin films

NASA Astrophysics Data System (ADS)

Murali, Dhanya S.; Aryasomayajula, Subrahmanyam

2018-03-01

Among the three oxides of copper (CuO, Cu2O, and Cu4O3), Cu4O3 phase (paramelaconite is a natural, and very scarce mineral) is very difficult to synthesize. It contains copper in both + 1 and + 2 valence states, with an average composition Cu2 1+Cu2 2+O3. We have successfully synthesized Cu4O3 phase at room temperature (300 K) by reactive DC magnetron sputtering by controlling the oxygen flow rate (Murali and Subrahmanyam in J Phys D Appl Phys 49:375102, 2016). In the present communication, Cu4O3 thin films are converted to CuO phases by annealing in the air at 680 K and to Cu2O phase when annealed in argon at 720 K; these phase changes are confirmed by temperature-dependent Raman spectroscopy studies. Probably, this is the first report of the conversion of Cu4O3-CuO and Cu2O by thermal annealing. The temperature-dependent (300-200 K) electrical transport properties of Cu4O3 thin films show that the charge transport above 190 K follows Arrhenius-type behavior with activation energy of 0.14 eV. From photo-electron spectroscopy and electrical transport measurements of Cu4O3 thin films, a downward band bending is observed at the surface of the thin film, which shows its p-type semiconducting nature. The successful preparation of phase pure p-type semiconducting Cu4O3 could provide opportunities to further explore its potential applications.

Design of binary SnO{sub 2}-CuO nanocomposite for efficient photocatalytic degradation of malachite green dye

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kumar, Aniket; Rout, Lipeeka; Achary, L. Satish Kumar

2016-04-13

Semiconductor mediated photocatalysis has got enormous consideration as it has shown immense potential in addressing the overall energy and environmental issues. To overcome the earlier drawbacks concerning quick charge recombination and limited visible-light absorption of semiconductor photocatalysts, numerous methods have been produced in the past couple of decades and the most broadly utilized one is to develop the photocatalytic heterojunctions. In our work, a series of SnO{sub 2}-CuO nanocomposites of different compositions were synthesized by a combustion method and have been investigated in detail by various characterization techniques, such as wide angle X-ray diffraction (XRD), UV-vis spectroscopy, transmission electron microscopymore » (TEM), and field emission scanning electron microscopy (FE-SEM). The results revealed that the crystal structure and optical properties of the nanocomposites were almost same for all the compositions. FE-SEM images showed that the shape of SnO{sub 2}-CuO was spherical in nature and the 1: 1 Sn/Cu sample had a well-proportioned morphology. The malachite green dye was used for the photocatalytic studies in a photoreactor and monitored with a UV-visible spectrometer for different composition ratio of metal (Sn: Cu) such as 1:1, 1:2, 2:1, 1:0.5 and 0.5:1. The 1:1 ratio nanocomposite showed excellent photocatalytic degradation of 96 % compared to pure SnO{sub 2} and CuO. The mechanism of degradation and charge separation ability of the nanocomposite are also explored using photocurrent measurement study.« less

Se@SiO2-FA-CuS nanocomposites for targeted delivery of DOX and nano selenium in synergistic combination of chemo-photothermal therapy.

PubMed

Wang, Yeying; Liu, Xijian; Deng, Guoying; Sun, Jian; Yuan, Haikuan; Li, Qi; Wang, Qiugeng; Lu, Jie

2018-02-08

In this study, a versatile tumor-targeted and multi-stimuli-responsive drug delivery vehicle (Se particle@porous silica-folic acid-copper sulfide/doxorubicin (Se@SiO 2 -FA-CuS/DOX)) was fabricated for combined photothermal therapy with chemotherapy in cancer treatment. Due to excellent targeting ability, the Se@SiO 2 -FA-CuS/DOX nanocomposites actively accumulated in tumor tissues and thus provided photothermal therapy under NIR irradiation and chemotherapy through the release of DOX and Se. Owing to the synergistic effect of chemotherapy (Se and DOX) and photothermal therapy, the Se@SiO 2 -FA-CuS/DOX nanocomposites could efficiently inhibit cancer cells both in vitro and in vivo and even completely eliminate tumors. Moreover, as the toxicity of DOX could be reduced by Se, the treatment using Se@SiO 2 -FA-CuS/DOX nanocomposites exhibited no appreciable adverse reactions. Thus, the Se@SiO 2 -FA-CuS/DOX nanocomposites have great potential as a multifunctional nanoplatform in future clinical applications.

Antibacterial effect of visible light reactive TiO2/Ag nanocomposite thin film on the orthodontic appliances.

PubMed

Yun, Kwidug; Oh, Gyejeong; Vang, Mongsook; Yang, Hongso; Lim, Hyunpil; Koh, Jeongtae; Jeong, Woonjo; Yoon, Dongjoo; Lee, Kyungku; Lee, Kwangmin; Park, Sangwon

2011-08-01

This study evaluated the antibacterial effect of a visible light reactive TiO2/Ag nanocomposite thin film on dental orthodontic wire (STS 304 wire). The growth of S. mutans and A. actinomycetemcomitans was suppressed on the specimens coated with TiO2/Ag compared to the uncoated specimens. The antibacterial effect of the TiO2/Ag nanocomposite thin film was improved under visible light irradiation.

Room temperature magneto-transport properties of nanocomposite Fe-In2O3 thin films

NASA Astrophysics Data System (ADS)

Tambasov, Igor A.; Gornakov, Kirill O.; Myagkov, Victor G.; Bykova, Liudmila E.; Zhigalov, Victor S.; Matsynin, Alexey A.; Yozhikova, Ekaterina V.

2015-12-01

A ferromagnetic Fe-In2O3 nanocomposite thin film has been synthesized by the thermite reaction Fe2O3+In→Fe-In2O3. Measurements of the Hall carrier concentration, Hall mobility and magnetoresistance have been conducted at room temperature. The nanocomposite Fe-In2O3 thin film had n=1.94·1020 cm-3, μ=6.45 cm2/Vs and negative magnetoresistance. The magnetoresistance for 8.8 kOe was ~-0.22%.The negative magnetoresistance was well described by the weak localization and model proposed by Khosla and Fischer.

Thin-film transistors with a graphene oxide nanocomposite channel.

PubMed

Jilani, S Mahaboob; Gamot, Tanesh D; Banerji, P

2012-12-04

Graphene oxide (GO) and graphene oxide-zinc oxide nanocomposites (GO-ZnO) were used as channel materials on SiO(2)/Si to fabricate thin-film transistors (TFT) with an aluminum source and drain. Pure GO-based TFT showed poor field-effect characteristics. However, GO-ZnO-nanocomposite-based TFT showed better field-effect performance because of the anchoring of ZnO nanostructures in the GO matrix, which causes a partial reduction in GO as is found from X-ray photoelectron spectroscopic data. The field-effect mobility of charge carriers at a drain voltage of 1 V was found to be 1.94 cm(2)/(V s). The transport of charge carriers in GO-ZnO was explained by a fluctuation-induced tunneling mechanism.

Thermally tunable VO2-SiO2 nanocomposite thin-film capacitors

NASA Astrophysics Data System (ADS)

Sun, Yifei; Narayanachari, K. V. L. V.; Wan, Chenghao; Sun, Xing; Wang, Haiyan; Cooley, Kayla A.; Mohney, Suzanne E.; White, Doug; Duwel, Amy; Kats, Mikhail A.; Ramanathan, Shriram

2018-03-01

We present a study of co-sputtered VO2-SiO2 nanocomposite dielectric thin-film media possessing continuous temperature tunability of the dielectric constant. The smooth thermal tunability is a result of the insulator-metal transition in the VO2 inclusions dispersed within an insulating matrix. We present a detailed comparison of the dielectric characteristics of this nanocomposite with those of a VO2 control layer and of VO2/SiO2 laminate multilayers of comparable overall thickness. We demonstrated a nanocomposite capacitor that has a thermal capacitance tunability of ˜60% between 25 °C and 100 °C at 1 MHz, with low leakage current. Such thermally tunable capacitors could find potential use in applications such as sensing, thermal cloaks, and phase-change energy storage devices.

Photoexcited Carrier Dynamics of Cu 2S Thin Films

DOE PAGES

Riha, Shannon C.; Schaller, Richard D.; Gosztola, David J.; ...

2014-11-11

Copper sulfide is a simple binary material with promising attributes for low-cost thin film photovoltaics. However, stable Cu 2S-based device efficiencies approaching 10% free from cadmium have yet to be realized. In this paper, transient absorption spectroscopy is used to investigate the dynamics of the photoexcited state of isolated Cu 2S thin films prepared by atomic layer deposition or vapor-based cation exchange of ZnS. While a number of variables including film thickness, carrier concentration, surface oxidation, and grain boundary passivation were examined, grain structure alone was found to correlate with longer lifetimes. A map of excited state dynamics is deducedmore » from the spectral evolution from 300 fs to 300 μs. Finally, revealing the effects of grain morphology on the photophysical properties of Cu 2S is a crucial step toward reaching high efficiencies in operationally stable Cu 2S thin film photovoltaics.« less

Superconducting properties of Nb-Cu nano-composites and nano-alloys

DOE Office of Scientific and Technical Information (OSTI.GOV)

Parab, Pradnya, E-mail: pradnyaprb@gmail.com; Kumar, Sanjeev; Bhui, Prabhjyot

The evolution of the superconducting transition temperature (T{sub c}) in nano-composite and nano-alloys of Nb-Cu, grown by DC magnetron co-sputtering are investigated. Microstructure of these films depends less strongly on the ratio of Nb:Cu but more on the growth temperature. At higher growth temperature, phase separated granular films of Nb and Cu were formed which showed superconducting transition temperatures (T{sub c}) of ~ 7.2±0.5 K, irrespective of the composition. Our results show that this is primarily influenced by the microstructure of the films determined during growth which rules out the superconducting proximity effect expected in these systems. At room temperaturemore » growth, films with nano-scale alloying were obtained at the optimal compositional range of 45-70 atomic% (At%) of Nb. These were also superconducting with a T{sub c} of 3.2 K.« less

Sol-gel deposited Cu2O and CuO thin films for photocatalytic water splitting.

PubMed

Lim, Yee-Fun; Chua, Chin Sheng; Lee, Coryl Jing Jun; Chi, Dongzhi

2014-12-21

Cu2O and CuO are attractive photocatalytic materials for water splitting due to their earth abundance and low cost. In this paper, we report the deposition of Cu2O and CuO thin films by a sol-gel spin-coating process. Sol-gel deposition has distinctive advantages such as low-cost solution processing and uniform film formation over large areas with a precise stoichiometry and thickness control. Pure-phase Cu2O and CuO films were obtained by thermal annealing at 500 °C in nitrogen and ambient air, respectively. The films were successfully incorporated as photocathodes in a photoelectrochemical (PEC) cell, achieving photocurrents of -0.28 mA cm(-2) and -0.35 mA cm(-2) (for Cu2O and CuO, respectively) at 0.05 V vs. a reversible hydrogen electrode (RHE). The Cu2O photocurrent was enhanced to -0.47 mA cm(-2) upon incorporation of a thin layer of a NiOx co-catalyst. Preliminary stability studies indicate that CuO may be more stable than Cu2O as a photocathode for PEC water-splitting.

Interfacial magnetism and exchange coupling in BiFeO3-CuO nanocomposite.

PubMed

Chakrabarti, Kaushik; Sarkar, Babusona; Ashok, Vishal Dev; Das, Kajari; Chaudhuri, Sheli Sinha; De, S K

2013-12-20

Ferromagnetic BiFeO3 nanocrystals of average size 9 nm were used to form a composite with antiferromagnetic CuO nanosheets, with the composition (x)BiFeO3/(100-x)CuO, x = 0, 20, 40, 50, 60, 80 and 100. The dispersion of BiFeO3 nanocrystals into the CuO matrix was confirmed by x-ray diffraction and transmission electron microscopy. The ferromagnetic ordering as observed in pure BiFeO3 occurs mainly due to the reduction in the particle size as compared to the wavelength (62 nm) of the spiral modulated spin structure of the bulk BiFeO3. Surface spin disorder of BiFeO3 nanocrystals gives rise to an exponential behavior of magnetization with temperature. Strong magnetic exchange coupling between the BiFeO3 nanocrystal and the CuO matrix induces an interfacial superparamagnetic phase with a blocking temperature of about 80 K. Zero field and field cooled magnetizations are analyzed by a ferromagnetic core and disordered spin shell model. The temperature dependence of the calculated saturation magnetization exhibits three magnetic contributions in three temperature regimes. The BiFeO3/CuO nanocomposites reveal an exchange bias effect below 170 K. The maximum exchange bias field HEB is 1841 Oe for x = 50 at 5 K under field cooling of 50 kOe. The exchange bias coupling results in an increase of coercivity of 1934 Oe at 5 K. Blocked spins within an interfacial region give rise to a remarkable exchange bias effect in the nanocomposite due to strong magnetic exchange coupling between the BiFeO3 nanocrystals and the CuO nanosheets.

Structural and optical properties of ITO and Cu doped ITO thin films

NASA Astrophysics Data System (ADS)

Chakraborty, Deepannita; Kaleemulla, S.; Rao, N. Madhusudhana; Subbaravamma, K.; Rao, G. Venugopal

2018-04-01

(In0.95Sn0.05)2O3 and (In0.90Cu0.05Sn0.05)2O3 thin films were coated onto glass substrate by electron beam evaporation technique. The structural and optical properties of ITO and Cu doped ITO thin films have been studied by X-ray diffractometer (XRD) and UV-Vis-NIR spectrophotometer. The crystallite size obtained for ITO and Cu doped ITO thin films was in the range of 24 nm to 22 nm. The optical band gap of 4 eV for ITO thin film sample has been observed. The optical band gap decreases to 3.85 eV by doping Cu in ITO.

Mechanical comparison of a polymer nanocomposite to a ceramic thin-film anti-reflective filter.

PubMed

Druffel, Thad; Geng, Kebin; Grulke, Eric

2006-07-28

Thin-film filters on optical components have been in use for decades and, for those industries utilizing a polymer substrate, the mismatch in mechanical behaviour has caused problems. Surface damage including scratches and cracks induces haze on the optical filter, reducing the transmission of the optical article. An in-mold anti-reflective (AR) filter incorporating 1/4-wavelength thin films based on a polymer nanocomposite is outlined here and compared with a traditional vacuum deposition AR coating. Nanoindentation and nanoscratch techniques are used to evaluate the mechanical properties of the thin films. Scanning electron microscopy (SEM) images of the resulting indentations and scratches are then compared to the force deflection curves to further explain the phenomena. The traditional coatings fractured by brittle mechanisms during testing, increasing the area of failure, whereas the polymer nanocomposite gave ductile failure with less surface damage.

Graphene Oxide/Poly(3-hexylthiophene) Nanocomposite Thin-Film Phototransistor for Logic Circuit Applications

NASA Astrophysics Data System (ADS)

Mansouri, S.; Coskun, B.; El Mir, L.; Al-Sehemi, Abdullah G.; Al-Ghamdi, Ahmed; Yakuphanoglu, F.

2018-04-01

Graphene is a sheet-structured material that lacks a forbidden band, being a good candidate for use in radiofrequency applications. We have elaborated graphene-oxide-doped poly(3-hexylthiophene) nanocomposite to increase the interlayer distance and thereby open a large bandgap for use in the field of logic circuits. Graphene oxide/poly(3-hexylthiophene) (GO/P3HT) nanocomposite thin-film transistors (TFTs) were fabricated on silicon oxide substrate by spin coating method. The current-voltage ( I- V) characteristics of TFTs with various P3HT compositions were studied in the dark and under light illumination. The photocurrent, charge carrier mobility, subthreshold voltage, density of interface states, density of occupied states, and I ON/ I OFF ratio of the devices strongly depended on the P3HT weight ratio in the composite. The effects of white-light illumination on the electrical parameters of the transistors were investigated. The results indicated that GO/P3HT nanocomposite thin-film transistors have high potential for use in radiofrequency applications, and their feasibility for use in digital applications has been demonstrated.

Carbon nanotubes/fluorinated polymers nanocomposite thin films for electrical contacts lubrication

NASA Astrophysics Data System (ADS)

Benedetto, A.; Viel, P.; Noël, S.; Izard, N.; Chenevier, P.; Palacin, S.

2007-09-01

The need to operate in extreme environmental conditions (ultra high vacuum, high temperatures, aerospatial environment, …) and the miniaturization toward micro electromechanical systems is demanding new materials in the field of low-level electrical contacts lubrication. Dry and chemically immobilized lubrication is expected to be an alternative to the traditional wet lubricants oils. With the goal to conciliate electrical conductivity and lubricant properties we designed nanocomposite thin films composed of a 2D carbon nanotubes network embedded in an organic matrix. The nanotubes networks were deposited on gold surfaces modified by electrochemical cathodic grafting of poly(acrylonitrile). The same substrate served for covalently bonding the low-friction organic matrix. Three different matrixes were tested: a perfluorinated oligomer chemically grafted and two different polyfluorinated acrylates electrochemically grafted. The nanocomposite thin films have been characterized by ATR FT-IR, XPS and Raman spectroscopy. We measured the effects of the different matrixes and the nanotubes addition on the tribological properties and on the contact resistances of the films.

A novel electrochemical sensor based on Cu3P@NH2-MIL-125(Ti) nanocomposite for efficient electrocatalytic oxidation and sensitive detection of hydrazine

NASA Astrophysics Data System (ADS)

Wang, Minghua; Yang, Longyu; Hu, Bin; Liu, Yongkang; Song, Yingpan; He, Linghao; Zhang, Zhihong; Fang, Shaoming

2018-07-01

A novel electrocatalyst based on amine-functionalized Ti-based metal-organic framework (NH2-MIL-125(Ti)) embedded with Cu3P nanocrystals (denoted by Cu3P@NH2-MIL-125(Ti)) was synthesized and used for electrocatalytic oxidation and detection of hydrazine in aqueous solution. A series of Cu3P@NH2-MIL-125(Ti) nanocomposites were obtained by adding Cu3P nanoparticles into the preparation system of NH2-MIL-125(Ti), with the Cu3P nanocrystals derived from the phospatization of Cu(OH)2 at high temperature. Based on the detailed characterizations and analysis of the chemical and physical performances of the series of Cu3P@NH2-MIL-125(Ti) nanocomposites at dosages of Cu3P nanocrystals at 5, 20, 50, and 100 mg, the good synergic effect between the Cu3P (50 mg) and the NH2-MIL-125(Ti) endows the as-prepared Cu3P50@NH2-MIL-125(Ti) nanocomposite with the excellent electrocatalytic activity toward the electrocatalytic oxidation of hydrazine. The Cu3P50@NH2-MIL-125(Ti)-based electrochemical sensor exhibited a detection limit of 79 nM (S/N = 3) within a wider linear range from 5 μM to 7.5 mM. Moreover, the developed sensor exhibited high selectivity toward the detection of hydrazine with the addition of certain common interferents and good applicability in real samples. All of these results imply that the Cu3P50@NH2-MIL-125(Ti) nanocomposite could be promising for detecting hydrazine and offer potential applications in the field of electroanalytical chemistry.

A GREEN CHEMISTRY APPROACH TO PREPARATION OF CORE (FE OR CU)-SHELL (NOBLE METALS) NANOCOMPOSITES USING AQUEOUS ASCORBIC ACID

EPA Science Inventory

A greener method to fabricate novel core (Fe or Cu)-shell (noble metals) nanocomposites of transition metals such as Fe and Cu and noble metals such as Au, Pt, Pd, and Ag using aqueous ascorbic acid is described. Transition metal salts such as Cu and Fe were reduced using ascor...

Optical, structural and electrochromic behavior studies on nanocomposite thin film of aniline, o-toluidine and WO3

NASA Astrophysics Data System (ADS)

Najafi-Ashtiani, Hamed; Bahari, Ali

2016-08-01

In the field of materials for electrochromic (EC) applications much attention was paid to the derivatives of aniline. We report on the optical, structural and electrochromic properties of electrochromic thin film based on composite of WO3 nanoparticles and copolymer of aniline and o-toluidine prepared by electrochemical polymerization method on fluorine doped tin oxide (FTO) coated glass. The thin film was studied by X-ray diffraction (XRD) and Fourier transforms infrared (FTIR) spectroscopy. The morphology of prepared thin film was characterized by field emission scanning electron microscopy (FESEM), atomic force microscopy (AFM) and the thermal gravimetric analysis (TGA) as well. The optical spectra of nanocomposite thin film were characterized in the 200-900 nm wavelength range and EC properties of nanocomposite thin film were studied by cyclic voltammetry (CV). The calculation of optical band gaps of thin film exhibited that the thin film has directly allowed transition with the values of 2.63 eV on first region and 3.80 eV on second region. Dispersion parameters were calculated based on the single oscillator model. Finally, important parameters such as dispersion energy, oscillator energy and lattice dielectric constant were determined and compared with the data from other researchers. The nonlinear optical properties such as nonlinear optical susceptibility, nonlinear absorption coefficient and nonlinear refractive index were extracted. The obtained results of nanocomposite thin film can be useful for the optoelectronic applications.

Self-assembled Co-BaZrO 3 nanocomposite thin films with ultra-fine vertically aligned Co nanopillars

DOE PAGES

Huang, Jijie; Li, Leigang; Lu, Ping; ...

2017-05-11

A simple one-step pulsed laser deposition (PLD) method has been applied to grow self-assembled metal-oxide nanocomposite thin films. The as-deposited Co-BaZrO 3 films show high epitaxial quality with ultra-fine vertically aligned Co nanopillars (diameter <5 nm) embeded in BZO matrix. The diameter of the nanopillars can be further tuned by varying the deposition frequency. The metal and oxide phases grow separately without inter-diffusion or mixing. Taking advantage of this unique structure, a high saturation magnetization of ~1375 emu/cm 3 in the Co- BaZrO 3 nanocomposites has been achieved and further confirmed by Lorentz microscopy imaging in TEM. Furthermore, the coercivitymore » values of this nanocomposite thin films range from 600 Oe (20 Hz) to 1020 Oe (2 Hz), which makes the nanocomposite an ideal candidate for high-density perpendicular recording media.« less

Biocide immobilized OMMT-carbon dot reduced Cu2O nanohybrid/hyperbranched epoxy nanocomposites: Mechanical, thermal, antimicrobial and optical properties.

PubMed

De, Bibekananda; Gupta, Kuldeep; Mandal, Manabendra; Karak, Niranjan

2015-11-01

The present work demonstrated a transparent thermosetting nanocomposite with antimicrobial and photoluminescence attributes. The nanocomposites are fabricated by incorporation of different wt.% (1, 2 and 3) of a biocide immobilized OMMT-carbon dot reduced Cu2O nanohybrid (MITH-NH) in the hyperbranched epoxy matrix. MITH-NH is obtained by immobilization of 2-methyl-4-isothiazolin-3-one hydrochloride (MITH) at room temperature using sonication on OMMT-carbon dot reduced Cu2O nanohybid. The nanohybrid is prepared by reduction of cupric acetate using carbon dot as the reducing agent in the presence of OMMT at 70°C. The significant improvements in tensile strength (~2 fold), elongation at break (3 fold), toughness (4 fold) and initial thermal degradation temperature (30°C) of the pristine hyperbranched epoxy system are achieved by incorporation of 3wt.% of MITH-NH in it. The nanocomposites exhibit strong antimicrobial activity against Staphylococcus aureus, Bacillus subtilis, Klebsiella pneumoniae and Pseudomonas aeruginosa bacteria and Candida albicans, a fungus. The nanocomposite also shows significant activity against biofilm formation compared to the pristine thermoset. Further, the nanocomposite films emit different colors on exposure of different wavelengths of UV light. The properties of these nanocomposites are also compared with the same nanohybrid without OMMT. Copyright © 2015. Published by Elsevier B.V.

Fabrication of mesoporous iron (Fe) doped copper sulfide (CuS) nanocomposite in the presence of a cationic surfactant via mild hydrothermal method for supercapacitors

NASA Astrophysics Data System (ADS)

Brown, J. William; Ramesh, P. S.; Geetha, D.

2018-02-01

We report fabrication of mesoporous Fe doped CuS nanocomposites with uniform mesoporous spherical structures via a mild hydrothermal method employing copper nitrate trihydrate (Cu (NO3).3H2O), Thiourea (Tu,Sc(NH2)2 and Iron tri nitrate (Fe(No3)3) as initial materials with cationic surfactant cetyltrimethylamoniame bromide (CTAB) as stabilizer/size controller and Ethylene glycol as solvent at 130 °C temperature. The products were characterized by XRD, SEM/EDX, TEM, FTIR and UV analysis. X-ray diffraction (XRD) spectra confirmed the Fe doped CuS nanocomposites which are crystalline in nature. EDX and XRD pattern confirmed that the product is hexagonal CuS phase. Fe doped spherical structure of CuS with grain size of 21 nm was confirmed by XRD pattern. Fe doping was identified by energy dispersive spectrometry (EDS). The Fourier-transform infrared (FTIR) spectroscopy results revealed the occurrence of active functional groups required for the reduction of copper ions. Studies showed that after a definite time relining on the chosen copper source, the obtained Fe-CuS nanocomposite shows a tendency towards self-assembly and creating mesoporous like nano and submicro structures by TEM/SAED. The achievable mechanism of producing this nanocomposite was primarily discussed. The electrochemical study confirms the pseudocapacitive nature of the CuS and Fe-CuS electrodes. The CuS and Fe-CuS electrode shows a specific capacitance of about 328.26 and 516.39 Fg-1 at a scan rate of 5 mVs-1. As the electrode in a supercapacitor, the mesoporous nanostructured Fe-CuS shows excellent capacitance characteristics.

Conductivity and dielectric behaviour of PEO-based solid nanocomposite polymer electrolytes

NASA Astrophysics Data System (ADS)

Ibrahim, Suriani; Mohd Yasin, Siti Mariah; Nee, Ng Meng; Ahmad, Roslina; Johan, Mohd Rafie

2012-03-01

In this research, thin films of poly(ethylene oxide) (PEO) blend with lithium hexafluorophosphate (LiPF) salt and ethylene carbonate (EC) as plasticiser and carbon nanotube (CNT) as filler, are prepared using solution casting method. The conductivity and dielectric response of the nanocomposite polymer electrolyte systems are studied within the broad frequency range of 5 Hz-5 MHz and within a temperature range of 298-373 K. The conductivity-temperature plots are observed to be of Arrhenius nature. The dielectric behaviour is analysed using the dielectric permittivity (ɛr and ɛi), loss tangent (tanδ) and electric modulus (Mi and Mr) of the samples. It is observed that the dielectric permittivity rises sharply towards low frequencies due to electrode polarisation effects. The maxima of the loss tangent (tanδ) shifts towards higher frequencies and the height of the peak increases with increasing temperature.

Thin film lithium-based batteries and electrochromic devices fabricated with nanocomposite electrode materials

DOEpatents

Gillaspie, Dane T; Lee, Se-Hee; Tracy, C. Edwin; Pitts, John Roland

2014-02-04

Thin-film lithium-based batteries and electrochromic devices (10) are fabricated with positive electrodes (12) comprising a nanocomposite material composed of lithiated metal oxide nanoparticles (40) dispersed in a matrix composed of lithium tungsten oxide.

Laser sintered thin layer graphene and cubic boron nitride reinforced nickel matrix nanocomposites

NASA Astrophysics Data System (ADS)

Hu, Zengrong; Tong, Guoquan

2015-10-01

Laser sintered thin layer graphene (Gr)-cubic boron nitride (CBN)-Ni nanocomposites were fabricated on AISI 4140 plate substrate. The composites fabricating process, composites microstructure and mechanical properties were studied. Scanning electron microscopy (SEM), X-ray diffraction (XRD) and Raman spectroscopy were employed to study the micro structures and composition of the composites. XRD and Raman tests proved that graphene and CBN were dispersed in the nanocomposites. Nanoindentation test results indicate the significant improvements were achieved in the composites mechanical properties.

Chemical Bath Deposition of p-Type Transparent, Highly Conducting (CuS)x:(ZnS)1-x Nanocomposite Thin Films and Fabrication of Si Heterojunction Solar Cells.

PubMed

Xu, Xiaojie; Bullock, James; Schelhas, Laura T; Stutz, Elias Z; Fonseca, Jose J; Hettick, Mark; Pool, Vanessa L; Tai, Kong Fai; Toney, Michael F; Fang, Xiaosheng; Javey, Ali; Wong, Lydia Helena; Ager, Joel W

2016-03-09

P-type transparent conducting films of nanocrystalline (CuS)x:(ZnS)1-x were synthesized by facile and low-cost chemical bath deposition. Wide angle X-ray scattering (WAXS) and high resolution transmission electron microscopy (HRTEM) were used to evaluate the nanocomposite structure, which consists of sub-5 nm crystallites of sphalerite ZnS and covellite CuS. Film transparency can be controlled by tuning the size of the nanocrystallites, which is achieved by adjusting the concentration of the complexing agent during growth; optimal films have optical transmission above 70% in the visible range of the spectrum. The hole conductivity increases with the fraction of the covellite phase and can be as high as 1000 S cm(-1), which is higher than most reported p-type transparent materials and approaches that of n-type transparent materials such as indium tin oxide (ITO) and aluminum doped zinc oxide (AZO) synthesized at a similar temperature. Heterojunction p-(CuS)x:(ZnS)1-x/n-Si solar cells were fabricated with the nanocomposite film serving as a hole-selective contact. Under 1 sun illumination, an open circuit voltage of 535 mV was observed. This value compares favorably to other emerging heterojunction Si solar cells which use a low temperature process to fabricate the contact, such as single-walled carbon nanotube/Si (370-530 mV) and graphene/Si (360-552 mV).

Giant Paramagnetism of Copper Nanoparticles in Nanocomposites Cu@C

NASA Astrophysics Data System (ADS)

Sharoyan, Eduard; Mirzakhanyan, Armen; Gyulasaryan, Harutyun; Manukyan, Aram; Estiphanos, Medhanie; Goff, Michael; Bernal, Oscar; Kocharian, Armen

The copper nanoparticles in nanocomposites Cu@C, encapsulated in graphitized carbon shell was obtained by the solid-phase pyrolysis method of polycrystalline phthalocyanine (CuPc, Pc =C32N8H16) . The average sizes of the nanoparticles are in the range of 2-6 nm. Magnetic measurements were carried out by vibrational magnetometer in the temperature range 10-300 K. At low temperatures (<70K) we observed a giant paramagnetism, apparently due to the (ballistic) conduction electron (large orbital magnetism). The values of the specific susceptibility at T = 10K with magnetic specific susceptibility of 510-5 emu/gOe order. This work was supported by the RA MES State Committee of Science, in the frames of the research project SCS-13-1C090. The work at California State University was supported by the National Science Foundation-Partnerships for Research and Education in Materials under Grant DMR-1523588.

Effect of substrate on texture and mechanical properties of Mg-Cu-Zn thin films

NASA Astrophysics Data System (ADS)

Eshaghi, F.; Zolanvari, A.

2018-04-01

In this work, thin films of Mg-Cu-Zn with 60 nm thicknesses have been deposited on the Si(100), Al, stainless steel, and Cu substrates using DC magnetron sputtering. FESEM images displayed uniformity of Mg-Cu-Zn particles on the different substrates. AFM micrograph revealed the roughness of thin film changes due to the different kinds of the substrates. XRD measurements showed the existence of strong Mg (002) reflections and weak Mg (101) peaks. Residual stress and adhesion force have been measured as the mechanical properties of the Mg-Cu-Zn thin films. The residual stresses of thin films which have been investigated by X-ray diffraction method revealed that the thin films sputtered on the Si and Cu substrates endure minimum and maximum stresses, respectively, during the deposition process. However, the force spectroscopy analysis indicated that the films grew on the Si and Cu experienced maximum and minimum adhesion force. The texture analysis has been done using XRD instrument to make pole figures of Mg (002) and Mg (101) reflections. ODFs have been calculated to evaluate the distribution of the orientations within the thin films. It was found that the texture and stress have an inverse relation, while the texture and the adhesion force of the Mg-Cu-Zn thin films have direct relation. A thin film that sustains the lowest residual stresses and highest adhesive force had the strongest {001} basal fiber texture.

Self-Assembled Formation of Well-Aligned Cu-Te Nano-Rods on Heavily Cu-Doped ZnTe Thin Films

NASA Astrophysics Data System (ADS)

Liang, Jing; Cheng, Man Kit; Lai, Ying Hoi; Wei, Guanglu; Yang, Sean Derman; Wang, Gan; Ho, Sut Kam; Tam, Kam Weng; Sou, Iam Keong

2016-11-01

Cu doping of ZnTe, which is an important semiconductor for various optoelectronic applications, has been successfully achieved previously by several techniques. However, besides its electrical transport characteristics, other physical and chemical properties of heavily Cu-doped ZnTe have not been reported. We found an interesting self-assembled formation of crystalline well-aligned Cu-Te nano-rods near the surface of heavily Cu-doped ZnTe thin films grown via the molecular beam epitaxy technique. A phenomenological growth model is presented based on the observed crystallographic morphology and measured chemical composition of the nano-rods using various imaging and chemical analysis techniques. When substitutional doping reaches its limit, the extra Cu atoms favor an up-migration toward the surface, leading to a one-dimensional surface modulation and formation of Cu-Te nano-rods, which explain unusual observations on the reflection high energy electron diffraction patterns and apparent resistivity of these thin films. This study provides an insight into some unexpected chemical reactions involved in the heavily Cu-doped ZnTe thin films, which may be applied to other material systems that contain a dopant having strong reactivity with the host matrix.

Cu(In,Ga)S2, Thin-Film Solar Cells Prepared by H2S Sulfurization of CuGa-In Precursor

NASA Technical Reports Server (NTRS)

Dhere, Neelkanth G.; Kulkarni, Shashank R.; Chavan, Sanjay S.; Ghongadi, Shantinath R.

2005-01-01

Thin-film CuInS2 solar cell is the leading candidate for space power because of bandgap near the optimum value for AM0 solar radiation outside the earth's atmosphere, excellent radiation hardness, and freedom from intrinsic degradation mechanisms unlike a-Si:H cells. Ultra-lightweight thin-film solar cells deposited on flexible polyimide plastic substrates such as Kapton(trademark), Upilex(trademark), and Apical(trademark) have a potential for achieving specific power of 1000 W/kg, while the state-of-art specific power of the present day solar cells is 66 W/kg. This paper describes the preparation of Cu-rich CuIn(sub 1-x)Ga(sub x)S(sub 2) (CIGS2) thin films and solar cells by a process of sulfurization of CuGa-In precursor similar to that being used for preparation of large-compact-grain CuIn(sub 1-x)Ga(sub x)Se2 thin films and efficient solar cells at FSEC PV Materials Lab.

One-pot synthesis of silica-hybridized Ag{sub 2}S–CuS nanocomposites with tunable nonlinear optical properties

DOE Office of Scientific and Technical Information (OSTI.GOV)

Ann Mary, K.A.; Unnikrishnan, N.V., E-mail: nvu100@yahoo.com; Philip, Reji

2015-10-15

Highlights: • Silica modified QDs of CuS and Ag{sub 2}S is developed at room temperature. • Formation of Ag{sub 2}S/CuS nanocomposites is confirmed from XRD and FFT of HRTEM images. • The concentration dependent growth of silica modified QDs is discussed. • Nonlinear absorption observed in ns excitations is dominated by SA and ESA. • Tuning of optical limiting efficiency is achieved with relative Ag{sub 2}S content. - Abstract: In the present work we report a simple, facile route developed for preparing silica hybridized copper sulfide and silver sulfide quantum dots at room temperature. By adjusting the concentration of themore » precursors, Ag{sub 2}S can form Ag{sub 2}S–CuS nanocomposites which are self regulated in one pot. Their crystalline, structural and optical properties have been investigated in detail, and the optical limiting nature is studied from fluence-dependent transmittance measurements employing short (5 ns) laser pulses at 532 nm. Ag{sub 2}S nanoparticles are found to have large third order nonlinear optical coefficients with a relatively lower optical limiting threshold of 1.7 J cm{sup −2}, while the nonlinearity of the nanocomposites is found to lie in between that of Ag{sub 2}S and CuS nanoparticles. These results suggest pathways for designing good quality optical limiters with tunable optical limiting efficiencies by varying the constituent nanocrystal compositions.« less

Fabrication of high-quality single-crystal Cu thin films using radio-frequency sputtering.

PubMed

Lee, Seunghun; Kim, Ji Young; Lee, Tae-Woo; Kim, Won-Kyung; Kim, Bum-Su; Park, Ji Hun; Bae, Jong-Seong; Cho, Yong Chan; Kim, Jungdae; Oh, Min-Wook; Hwang, Cheol Seong; Jeong, Se-Young

2014-08-29

Copper (Cu) thin films have been widely used as electrodes and interconnection wires in integrated electronic circuits, and more recently as substrates for the synthesis of graphene. However, the ultra-high vacuum processes required for high-quality Cu film fabrication, such as molecular beam epitaxy (MBE), restricts mass production with low cost. In this work, we demonstrated high-quality Cu thin films using a single-crystal Cu target and radio-frequency (RF) sputtering technique; the resulting film quality was comparable to that produced using MBE, even under unfavorable conditions for pure Cu film growth. The Cu thin film was epitaxially grown on an Al2O3 (sapphire) (0001) substrate, and had high crystalline orientation along the (111) direction. Despite the 10(-3) Pa vacuum conditions, the resulting thin film was oxygen free due to the high chemical stability of the sputtered specimen from a single-crystal target; moreover, the deposited film had >5× higher adhesion force than that produced using a polycrystalline target. This fabrication method enabled Cu films to be obtained using a simple, manufacturing-friendly process on a large-area substrate, making our findings relevant for industrial applications.

Growth of <111>-oriented Cu layer on thin TaWN films

NASA Astrophysics Data System (ADS)

Takeyama, Mayumi B.; Sato, Masaru

2017-07-01

In this study, we examine the growth of a <111>-oriented Cu layer on a thin TaWN ternary alloy barrier for good electromigration reliability. The strongly preferentially oriented Cu(111) layer is observed on a thin TaWN barrier even in the as-deposited Cu (100 nm)/TaWN (5 nm)/Si system. Also, this system tolerates annealing at 700 °C for 1 h without silicide reaction. It is revealed that the TaWN film is one of the excellent barriers with thermal stability and low resistivity. Simultaneously, the TaWN film is a candidate for a superior underlying material to achieve the Cu(111) preferential orientation.

Hydrothermal synthesis of graphene oxide/multiwalled carbon nanotube/Fe3O4 ternary nanocomposite for removal of Cu (II) and methylene blue

NASA Astrophysics Data System (ADS)

Long, Zhihang; Zhan, Yingqing; Li, Fei; Wan, Xinyi; He, Yi; Hou, Chunyan; Hu, Hai

2017-09-01

In this work, highly activated graphene oxide/multiwalled carbon nanotube/Fe3O4 ternary nanocomposite adsorbent was prepared from a simple hydrothermal route by using ferrous sulfate as precursor. For this purpose, the graphene oxide/multiwalled carbon nanotube architectures were formed through the π-π attractions between them, followed by attaching Fe3O4 nanoparticles onto their surface. The structure and composition of as-prepared ternary nanocomposite were characterized by XRD, FTIR, XPS, SEM, TEM, Raman, TGA, and BET. It was found that the resultant porous graphene oxide/multiwalled carbon nanotube/Fe3O4 ternary nanocomposite with large surface area could effectively prevent the π-π stacking interactions between graphene oxide nanosheets and greatly improve sorption sites on the surfaces. Thus, owing to the unique ternary nanocomposite architecture and synergistic effect among various components, as-prepared ternary nanocomposite exhibited high separation efficiency when they were used to remove the Cu (II) and methylene blue from aqueous solutions. Furthermore, the adsorption isotherms of ternary nanocomposite structures for Cu (II) and methylene blue removal fitted the Langmuir isotherm model. This work demonstrated that the graphene oxide/multiwalled carbon nanotube/Fe3O4 ternary nanocomposite was promising as an efficient adsorbent for heavy metal ions and organic dye removal from wastewater in low concentration.

Nanocomposite thin films for triggerable drug delivery.

PubMed

Vannozzi, Lorenzo; Iacovacci, Veronica; Menciassi, Arianna; Ricotti, Leonardo

2018-05-01

Traditional drug release systems normally rely on a passive delivery of therapeutic compounds, which can be partially programmed, prior to injection or implantation, through variations in the material composition. With this strategy, the drug release kinetics cannot be remotely modified and thus adapted to changing therapeutic needs. To overcome this issue, drug delivery systems able to respond to external stimuli are highly desirable, as they allow a high level of temporal and spatial control over drug release kinetics, in an operator-dependent fashion. Areas covered: On-demand drug delivery systems actually represent a frontier in this field and are attracting an increasing interest at both research and industrial level. Stimuli-responsive thin films, enabled by nanofillers, hold a tremendous potential in the field of triggerable drug delivery systems. The inclusion of responsive elements in homogeneous or heterogeneous thin film-shaped polymeric matrices strengthens and/or adds intriguing properties to conventional (bare) materials in film shape. Expert opinion: This Expert Opinion review aims to discuss the approaches currently pursued to achieve an effective on-demand drug delivery, through nanocomposite thin films. Different triggering mechanisms allowing a fine control on drug delivery are described, together with current challenges and possible future applications in therapy and surgery.

Cu-Doped ZnO Thin Films Grown by Co-deposition Using Pulsed Laser Deposition for ZnO and Radio Frequency Sputtering for Cu

NASA Astrophysics Data System (ADS)

Shin, Hyun Wook; Son, Jong Yeog

2018-05-01

Cu-doped ZnO (CZO) thin films were fabricated on single-crystalline (0001) Al2O3 substrates by co-deposition using pulsed laser deposition for ZnO and radio frequency sputtering for Cu. CZO thin films with 0-20% molar concentrations are obtained by adjusting the deposition rates of ZnO and Cu. The CZO thin films exhibit room temperature ferromagnetism, and CZO with 5% Cu molar concentration has maximum remanent magnetization, which is consistent with theoretical results.

Studies on temperature coefficient of resistivity of Cu2Se - V2O5 nanocomposite

NASA Astrophysics Data System (ADS)

Sairam, S.; Rai, Ranjan; Molli, Muralikrishna

2018-05-01

Nanocomposite of Copper Selenide in Vanadium Pentoxide (Cu2Se-V2O5) was prepared and characterized using XRD for phase analysis, SEM for morphology, and EDAX for elemental analysis. Electrical resistivity measurement was carried out using van der Pauw method as a function of temperature from 35 °C to 170 °C for 5 mol% Cu2Se - 95 mol%V2O5 composite. The temperature coefficient of resistivity was found to be -1.8% per °C.

Dynamic Mechanical Characterization of Thin Film Polymer Nanocomposites

NASA Technical Reports Server (NTRS)

Herring, Helen M.; Gates, Thomas S. (Technical Monitor)

2003-01-01

Many new materials are being produced for aerospace applications with the objective of maximizing certain ideal properties without sacrificing others. Polymer composites in various forms and configurations are being developed in an effort to provide lighter weight construction and better thermal and electrical properties and still maintain adequate strength and stability. To this end, thin film polymer nanocomposites, synthesized for the purpose of influencing electrical conductivity using metal oxide particles as filler without incurring losses in mechanical properties, were examined to determine elastic modulus and degree of dispersion of particles. The effects of various metal oxides on these properties will be discussed.

Synthesis, morphological, electromechanical characterization of (CaMgFex)Fe1-xTi3O12-δ/PDMS nanocomposite thin films for energy storage application

NASA Astrophysics Data System (ADS)

Tripathy, Ashis; Sharma, Priyaranjan; Sahoo, Narayan

2018-03-01

At the present time, flexible and stretchable electronics has intended to use the new cutting-edge technologies for advanced electronic application. Currently, Polymers are being employed for such applications but they are not effective due to their low dielectric constant. To enhance the dielectric properties of polymer for energy storage application, it is necessary to add ceramic material of high dielectric constant to synthesize a polymer-ceramic composite. Therefore, a novel attempt has been made to enhance the dielectric properties of the Polydimethylsiloxane (PDMS) polymer by adding (CaMgFex)Fe1-xTi3O12-δ(0nanocomposite ceramic powder. The newly developed CMFTO2/PDMS composite based thin film shows a higher dielectric constant (ε‧) value (~350), extremely low tangent loss (tanδ) (< 0.002) and excellent flexibility (static modulus ≈ 0.27 MPa and elongation > 90%), which can make it a potential material for advanced flexible electronic devices, energy storage and biomedical applications.

Characterization of Cu buffer layers for growth of L10-FeNi thin films

NASA Astrophysics Data System (ADS)

Mizuguchi, M.; Sekiya, S.; Takanashi, K.

2010-05-01

A Cu(001) layer was fabricated on a Au(001) layer to investigate the use of Cu as a buffer layer for growing L10-FeNi thin films. The epitaxial growth of a Cu buffer layer was observed using reflection high-energy electron diffraction. The flatness of the layer improved drastically with an increase in the substrate temperature although the layer was an alloy (AuCu3). An FeNi thin film was epitaxially grown on the AuCu3 buffer layer by alternate monatomic layer deposition and the formation of an L10-FeNi ordered alloy was expected. The AuCu3 buffer layer is thus a promising candidate material for the growth of L10-FeNi thin films.

Influences of annealing temperature on sprayed CuFeO2 thin films

NASA Astrophysics Data System (ADS)

Abdelwahab, H. M.; Ratep, A.; Abo Elsoud, A. M.; Boshta, M.; Osman, M. B. S.

2018-06-01

Delafossite CuFeO2 thin films were successfully prepared onto quartz substrates using simple spray pyrolysis technique. Post annealing under nitrogen atmosphere for 2 h was necessary to form delafossite CuFeO2 phase. The effect of alteration in annealing temperature (TA) 800, 850 and 900 °C was study on structural, morphology and optical properties. The XRD results for thin film annealed at TA = 850 °C show single phase CuFeO2 with rhombohedral crystal system and R 3 bar m space group with preferred orientation along (0 1 2). The prepared copper iron oxide thin films have an optical transmission ranged ∼40% in the visible region. The optical direct optical band gap of the prepared thin films was ranged ∼2.9 eV.

Nonenzymatic detection of glucose using BaCuO2 thin layer

NASA Astrophysics Data System (ADS)

Ito, Takeshi; Asada, Tsuyoshi; Asai, Naoto; Shimizu, Tomohiro; Shingubara, Shoso

2017-01-01

A BaCuO2 thin layer was deposited on a glassy carbon electrode and used for the direct oxidation of glucose. The crystalline, electrochemical, and physicochemical properties that depend on the deposition temperature and deposition time were studied. X-ray diffraction (XRD) analysis showed that the thin layer was amorphous even at 400 °C. The current density of the glucose oxidation using the thin layer deposited at 200 °C was higher than those at other deposition temperatures. Under this condition, the current density increased with the glucose concentration and deposition time. These results indicate that a BaCuO2 thin layer has potential for measuring the blood glucose level without enzymes.

Mechanical properties and microstructures of Al-Cu Thin films with various heat treatments

NASA Astrophysics Data System (ADS)

Joo, Young-Chang

1998-10-01

The relationship between microstructure and mechanical properties has been investigated in Al-Cu thin films. The Cu content in Al-Cu samples used in this study ranges from 0 to 2 wt.% and substrate curvature measurement was used to measure film stress. In thin films, the constraints on the film by the substrate influence the microstructure and mechanical properties. Al-Cu thin films cooled from high temperatures have a large density of dislocations due to the plastic deformation caused by the thermal mismatch between the film and substrate. The high density of dislocations in the thin film enables precipitates to form inside the grain even during a very rapid quenching. The presence of a large density of dislocations and precipitates will in turn cause precipitation hardening of the Al-Cu films. The precipitation hardening is dominant at lower temperatures, and solid solution hardening is observed at higher temperatures in the tensile regime. Pure Al films showed the same values of tensile and compressive yield stresses at a given temperature during stress-temperature cycling.

Analysis of LDPE-ZnO-clay nanocomposites using novel cumulative rheological parameters

NASA Astrophysics Data System (ADS)

Kracalik, Milan

2017-05-01

Polymer nanocomposites exhibit complex rheological behaviour due to physical and also possibly chemical interactions between individual phases. Up to now, rheology of dispersive polymer systems has been usually described by evaluation of viscosity curve (shear thinning phenomenon), storage modulus curve (formation of secondary plateau) or plotting information about dumping behaviour (e.g. Van Gurp-Palmen-plot, comparison of loss factor tan δ). On the contrary to evaluation of damping behaviour, values of cot δ were calculated and called as "storage factor", analogically to loss factor. Then values of storage factor were integrated over specific frequency range and called as "cumulative storage factor". In this contribution, LDPE-ZnO-clay nanocomposites with different dispersion grades (physical networks) have been prepared and characterized by both conventional as well as novel analysis approach. Next to cumulative storage factor, further cumulative rheological parameters like cumulative complex viscosity, cumulative complex modulus or cumulative storage modulus have been introduced.

Carbon tolerance of Ni-Cu and Ni-Cu/YSZ sub-μm sized SOFC thin film model systems

NASA Astrophysics Data System (ADS)

Götsch, Thomas; Schachinger, Thomas; Stöger-Pollach, Michael; Kaindl, Reinhard; Penner, Simon

2017-04-01

Thin films of YSZ, unsupported Ni-Cu 1:1 alloy phases and YSZ-supported Ni-Cu 1:1 alloy solutions have been reproducibly prepared by magnetron sputter deposition on Si wafers and NaCl(001) single crystal facets at two selected substrate temperatures of 298 K and 873 K. Subsequently, the layer properties of the resulting sub-μm thick thin films as well as the tendency towards carbon deposition following treatment in pure methane at 1073 K has been tested comparatively. Well-crystallized structures of cubic YSZ, cubic NiCu and cubic NiCu/YSZ have been obtained following deposition at 873 K on both substrates. Carbon is deposited on all samples following the trend Ni-Cu (1:1) = Ni-Cu (1:1)/YSZ > pure YSZ, indicating that at least the 1:1 composition of layered Ni-Cu alloy phases is not able to suppress the carbon deposition completely, rendering it unfavorable for usage as anode component in sub-μm sized fuel cells. It is shown that surfaces with a high Cu/Ni ratio nevertheless prohibit any carbon deposition.

Energy band engineering and controlled p-type conductivity of CuAlO2 thin films by nonisovalent Cu-O alloying

NASA Astrophysics Data System (ADS)

Yao, Z. Q.; He, B.; Zhang, L.; Zhuang, C. Q.; Ng, T. W.; Liu, S. L.; Vogel, M.; Kumar, A.; Zhang, W. J.; Lee, C. S.; Lee, S. T.; Jiang, X.

2012-02-01

The electronic band structure and p-type conductivity of CuAlO2 films were modified via synergistic effects of energy band offset and partial substitution of less-dispersive Cu+ 3d10 with Cu2+ 3d9 orbitals in the valence band maximum by alloying nonisovalent Cu-O with CuAlO2 host. The Cu-O/CuAlO2 alloying films show excellent electronic properties with tunable wide direct bandgaps (˜3.46-3.87 eV); Hall measurements verify the highest hole mobilities (˜11.3-39.5 cm2/Vs) achieved thus far for CuAlO2 thin films and crystals. Top-gate thin film transistors constructed on p-CuAlO2 films were presented, and the devices showed pronounced performance with Ion/Ioff of ˜8.0 × 102 and field effect mobility of 0.97 cm2/Vs.

Graphene stabilized ultra-small CuNi nanocomposite with high activity and recyclability toward catalysing the reduction of aromatic nitro-compounds

NASA Astrophysics Data System (ADS)

Fang, Hao; Wen, Ming; Chen, Hanxing; Wu, Qingsheng; Li, Weiying

2015-12-01

Nowadays, it is of great significance and a challenge to design a noble-metal-free catalyst with high activity and a long lifetime for the reduction of aromatic nitro-compounds. Here, a 2D structured nanocomposite catalyst with graphene supported CuNi alloy nanoparticles (NPs) is prepared, and is promising for meeting the requirements of green chemistry. In this graphene/CuNi nanocomposite, the ultra-small CuNi nanoparticles (~2 nm) are evenly anchored on graphene sheets, which is not only a breakthrough in the structures, but also brings about an outstanding performance in activity and stability. Combined with a precise optimization of the alloy ratios, the reaction rate constant of graphene/Cu61Ni39 reached a high level of 0.13685 s-1, with a desirable selectivity as high as 99% for various aromatic nitro-compounds. What's more, the catalyst exhibited a unprecedented long lifetime because it could be recycled over 25 times without obvious performance decay or even a morphology change. This work showed the promise and great potential of noble-metal-free catalysts in green chemistry.Nowadays, it is of great significance and a challenge to design a noble-metal-free catalyst with high activity and a long lifetime for the reduction of aromatic nitro-compounds. Here, a 2D structured nanocomposite catalyst with graphene supported CuNi alloy nanoparticles (NPs) is prepared, and is promising for meeting the requirements of green chemistry. In this graphene/CuNi nanocomposite, the ultra-small CuNi nanoparticles (~2 nm) are evenly anchored on graphene sheets, which is not only a breakthrough in the structures, but also brings about an outstanding performance in activity and stability. Combined with a precise optimization of the alloy ratios, the reaction rate constant of graphene/Cu61Ni39 reached a high level of 0.13685 s-1, with a desirable selectivity as high as 99% for various aromatic nitro-compounds. What's more, the catalyst exhibited a unprecedented long lifetime

Pd-Cu/poly(o-Anisidine) nanocomposite as an efficient catalyst for formaldehyde oxidation

DOE Office of Scientific and Technical Information (OSTI.GOV)

Hosseini, Sayed Reza, E-mail: r.hosseini@umz.ac.ir; Raoof, Jahan-Bakhsh; Ghasemi, Shahram

Highlights: • o-Anisidine monomer was electro-polymerized at the pCPE surface in acid medium. • Palladium/copper NPs were prepared by galvanic replacement method at the POA/pCPE. • Pd-Cu NPs showed excellent electrocatalytic activity towards formaldehyde oxidation. • The bimetallic Pd-Cu NPs/POA nanocomposite showed satisfactory long-term stability. - Abstract: In this work, for the first time, the electrocatalytic oxidation of formaldehyde in 0.5 M sulfuric acid solution at spherical bimetallic palladium-copper nanoparticles (Pd-Cu NPs) deposited on the poly (o-Anisidine) film modified electrochemically pretreated carbon paste electrode (POA/pCPE) has been investigated. Highly porous POA film prepared by electropolymerization onto the pCPE was usedmore » as a potent support for deposition of the Pd-Cu NPs. The Pd-Cu NPs were prepared through spontaneous and irreversible reaction via galvanic replacement between Pd{sup II} ions and the Cu{sup 0} particles. The prepared Pd-Cu NPs were characterized by scanning electron microscopy, energy dispersive spectroscopy and electrochemical methods. The obtained results showed that the utilization of Cu nanoparticles and pretreatment technique enhances the electrocatalytic activity of the modified electrode towards formaldehyde oxidation. The influence of several parameters on formaldehyde oxidation as well as stability of the Pd-Cu/POA/pCPE has been investigated.« less

Chitosan Membrane Embedded With ZnO/CuO Nanocomposites for the Photodegradation of Fast Green Dye Under Artificial and Solar Irradiation

PubMed Central

Alzahrani, Eman

2018-01-01

Fast Green (FCF) dye is commonly used in both cytology and histology applications. Previous studies have found that it can cause mutagenic and tumorigenic effects in experimental human and animal populations. It can also be a source of skin, eye, respiratory, and digestive irritation. The purpose of this study was to examine the use of thin film membranes to degrade FCF. A thin film membrane of chitosan (CS) was fabricated and subsequently filled with zinc oxide nanoparticles (ZnO) or ZnO/CuO-heterostructured nanocomposites. The CS membrane was used as a matrix, and the nanomaterials were used as photocatalysts. The prepared membranes were characterised by four analytical techniques: atomic force microscopy, scanning electron microscopy, X-ray diffraction, and energy-dispersive X-ray analyses. The photocatalytic activity of the fabricated membranes was evaluated by performing experiments in which aqueous solutions of FCF dye that contained the fabricated membrane were irradiated with solar light or UV light. The photodegradation percentage was spectrophotometrically determined by monitoring the maximum wavelengths (λmax) of FCF at 623 nm for different irradiation times. The decolourisation percentages of the dye under solar light were 57.90% and 60.23% using the CS-ZnO and CS-ZnO/CuO membranes, respectively. When UV light irradiation was employed as the source of irradiation, the photodegradation percentages of FCF were 71.45% and 91.21% using the CS-ZnO and CS-ZnO/CuO membranes, respectively. These results indicated that the best photocatalytic system for the degradation of FCF dye was CS-ZnO/CuO membrane in combination with UV light irradiation. The study also found that it was easy to separate the prepared membranes after the reaction without the need for a centrifuge or magnet. The results demonstrate the potential for CS-ZnO and CS-ZnO/CuO membranes for use as effective sorbents during the process of photodegradation of harmful dyes within waste water

Surface chirality of CuO thin films.

PubMed

Widmer, Roland; Haug, Franz-Josef; Ruffieux, Pascal; Gröning, Oliver; Bielmann, Michael; Gröning, Pierangelo; Fasel, Roman

2006-11-01

We present X-ray photoelectron spectroscopy (XPS) and X-ray photoelectron diffraction (XPD) investigations of CuO thin films electrochemically deposited on an Au(001) single-crystal surface from a solution containing chiral tartaric acid (TA). The presence of enantiopure TA in the deposition process results in a homochiral CuO surface, as revealed by XPD. On the other hand, XPD patterns of films deposited with racemic tartaric acid or the "achiral" meso-tartaric acid are completely symmetric. A detailed analysis of the experimental data using single scattering cluster calculations reveals that the films grown with l(+)-TA exhibit a CuO(1) orientation, whereas growth in the presence of d(-)-TA results in a CuO(11) surface orientation. A simple bulk-truncated model structure with two terminating oxygen layers reproduces the experimental XPD data. Deposition with alternating enantiomers of tartaric acid leads to CuO films of alternating chirality. Enantiospecifity of the chiral CuO surfaces is demonstrated by further deposition of CuO from a solution containing racemic tartaric acid. The pre-deposited homochiral films exhibit selectivity toward the same enantiomeric deposition pathway.

A multi-step reaction model for ignition of fully-dense Al-CuO nanocomposite powders

NASA Astrophysics Data System (ADS)

Stamatis, D.; Ermoline, A.; Dreizin, E. L.

2012-12-01

A multi-step reaction model is developed to describe heterogeneous processes occurring upon heating of an Al-CuO nanocomposite material prepared by arrested reactive milling. The reaction model couples a previously derived Cabrera-Mott oxidation mechanism describing initial, low temperature processes and an aluminium oxidation model including formation of different alumina polymorphs at increased film thicknesses and higher temperatures. The reaction model is tuned using traces measured by differential scanning calorimetry. Ignition is studied for thin powder layers and individual particles using respectively the heated filament (heating rates of 103-104 K s-1) and laser ignition (heating rate ∼106 K s-1) experiments. The developed heterogeneous reaction model predicts a sharp temperature increase, which can be associated with ignition when the laser power approaches the experimental ignition threshold. In experiments, particles ignited by the laser beam are observed to explode, indicating a substantial gas release accompanying ignition. For the heated filament experiments, the model predicts exothermic reactions at the temperatures, at which ignition is observed experimentally; however, strong thermal contact between the metal filament and powder prevents the model from predicting the thermal runaway. It is suggested that oxygen gas release from decomposing CuO, as observed from particles exploding upon ignition in the laser beam, disrupts the thermal contact of the powder and filament; this phenomenon must be included in the filament ignition model to enable prediction of the temperature runaway.

Fe3O4@mSiO2-FA-CuS-PEG nanocomposites for magnetic resonance imaging and targeted chemo-photothermal synergistic therapy of cancer cells.

PubMed

Gao, Zhifang; Liu, Xijian; Deng, Guoying; Zhou, Feng; Zhang, Lijuan; Wang, Qian; Lu, Jie

2016-09-14

In this work, a new multifunctional nanoplatform (Fe3O4@mSiO2-FA-CuS-PEG nanocomposite) for magnetic resonance imaging (MRI) and targeted chemo-photothermal therapy, was firstly fabricated on the basis of magnetic mesoporous silica nanoparticles (Fe3O4@mSiO2), on which folic acid (FA) was grafted as the targeting reagent, CuS nanocrystals were attached as the photothermal agent, and polyethylene glycol (PEG) was coupled to improve biocompatibility. The characterization results demonstrated that the fabricated Fe3O4@mSiO2-FA-CuS-PEG nanocomposites not only showed strong magnetism and excellent MRI performance, but also had a high doxorubicin (DOX, an anticancer drug) loading capacity (22.1%). The loaded DOX can be sustainably released, which was apt to be controlled by pH adjustment and near infrared (NIR) laser irradiation. More importantly, targeted delivery of the DOX-loaded Fe3O4@mSiO2-FA-CuS-PEG nanocomposites could be accomplished in HeLa cells via the receptor-mediated endocytosis pathway, and this exhibited synergistic effect of chemotherapy and photothermal therapy against HeLa cells under irradiation with a 915 nm laser. Therefore, the fabricated multifunctional Fe3O4@mSiO2-FA-CuS-PEG nanocomposite has a great potential in image-guided therapy of cancers.

Thermoelectric properties of CuS/Ag{sub 2}S nanocomposites synthesed by modified polyol method

DOE Office of Scientific and Technical Information (OSTI.GOV)

Tarachand,, E-mail: tarachand@csr.res.in; Sharma, Vikash; Ganesan, V.

This is the report on successful synthesis of Ag doped CuS nanostructures by modified polyol method. The resulting samples were characterized by powder X-ray diffraction (XRD), energy dispersive X-ray (EDX), atomic force microscopy (AFM) and dynamic light scattering (DLS). Particle size of pure CuS nanoparticles (NPs) was 17 nm, 38 nm and 97 nm as determined from Scherrer formula, AFM and DLS, respectively. Introduction of Ag led to formation of CuS/Ag{sub 2}S composites. A transition at 55 K in thermopower is ascribed to structural transformation from hexagonal to orthorhombic structure. Further, their thermoelectric properties exhibit remarkable change owing to Agmore » doping in CuS nanostructures. The power factor improves with increasing Ag content. They reveal that CuS/Ag{sub 2}S nanocomposites are some of the potential candidates for generation of thermoelectricity in future.« less

Novel combination of zero-valent Cu and Ag nanoparticles @ cellulose acetate nanocomposite for the reduction of 4-nitro phenol.

PubMed

Khan, Farman Ullah; Asimullah; Khan, Sher Bahadar; Kamal, Tahseen; Asiri, Abdullah M; Khan, Ihsan Ullah; Akhtar, Kalsoom

2017-09-01

A very simple and low-cost procedure has been adopted to synthesize efficient copper (Cu), silver (Ag) and copper-silver (Cu-Ag) mixed nanoparticles on the surface of pure cellulose acetate (CA) and cellulose acetate-copper oxide nanocomposite (CA-CuO). All nanoparticles loaded onto CA and CA-CuO presented excellent catalytic ability, but Cu-Ag nanoparticles loaded onto CA-CuO (Cu 0 -Ag 0 /CA-CuO) exhibited outstanding catalytic efficiency to convert 4-nitrophenol (4-NP) into 4-aminophenol (4-AP) in the presence of NaBH 4 . Additionally, the Cu 0 -Ag 0 /CA-CuO can be easily recovered by removing the sheet from the reaction media, and can be recycled several times, maintaining high catalytic ability for four cycles. Copyright © 2017 Elsevier B.V. All rights reserved.

Synthesis and characterization of ZnO–CuO nanocomposites powder by modified perfume spray pyrolysis method and its antimicrobial investigation

NASA Astrophysics Data System (ADS)

Saravanakkumar, D.; Sivaranjani, S.; Kaviyarasu, K.; Ayeshamariam, A.; Ravikumar, B.; Pandiarajan, S.; Veeralakshmi, C.; Jayachandran, M.; Maaza, M.

2018-03-01

Pure ZnO, ZnO–CuO nanocomposites can be synthesized by using a modified perfume spray pyrolysis method (MSP). The crystallite size of the nanoparticles (NPs) has been observed by X-ray diffraction pattern and is nearly 36 nm. Morphological studies have been analyzed by using Field Emission Scanning Electron Microscopy (FESEM) and its elemental analysis was reported by Elemental X-ray Analysis (EDX); these studies confirmed that ZnO and CuO have hexagonal structure and monoclinic structure respectively. Fourier Transform Infrared (FTIR) spectra revealed that the presence of functional frequencies of ZnO and CuO were observed at 443 and 616 cm‑1. The average bandgap value at 3.25 eV using UV–vis spectra for the entitled composite has described a blue shift that has been observed here. The antibacterial study against both gram positive and negative bacteria has been studied by the disc diffusion method. To the best of our knowledge, it is the first report on ZnO–CuO nanocomposite synthesized by a modified perfume spray pyrolysis method.

Graphene stabilized ultra-small CuNi nanocomposite with high activity and recyclability toward catalysing the reduction of aromatic nitro-compounds.

PubMed

Fang, Hao; Wen, Ming; Chen, Hanxing; Wu, Qingsheng; Li, Weiying

2016-01-07

Nowadays, it is of great significance and a challenge to design a noble-metal-free catalyst with high activity and a long lifetime for the reduction of aromatic nitro-compounds. Here, a 2D structured nanocomposite catalyst with graphene supported CuNi alloy nanoparticles (NPs) is prepared, and is promising for meeting the requirements of green chemistry. In this graphene/CuNi nanocomposite, the ultra-small CuNi nanoparticles (∼2 nm) are evenly anchored on graphene sheets, which is not only a breakthrough in the structures, but also brings about an outstanding performance in activity and stability. Combined with a precise optimization of the alloy ratios, the reaction rate constant of graphene/Cu61Ni39 reached a high level of 0.13685 s(-1), with a desirable selectivity as high as 99% for various aromatic nitro-compounds. What's more, the catalyst exhibited a unprecedented long lifetime because it could be recycled over 25 times without obvious performance decay or even a morphology change. This work showed the promise and great potential of noble-metal-free catalysts in green chemistry.

Sulvanite (Cu 3VS 4) nanocrystals for printable thin film photovoltaics

DOE PAGES

Chen, Ching -Chin; Stone, Kevin H.; Lai, Cheng -Yu; ...

2017-09-21

Copper Vanadium Sulfide (Cu 3VS 4), also known as sulvanite, has recently emerged as a suitable absorber material for thin film photovoltaics. The synthesis of Cu 3VS 4 nanocrystals via a rapid solvothermal route is reported for the first time. The phase purity of the Cu 3VS 4 nanocrystals has been confirmed by X-ray powder diffraction (XRD) and Raman spectroscopy, while the nanoparticle size, of about 10 nm, was evaluated by transmission electron microscopy (TEM). Successful ligand exchange with sulfide, an inorganic ligand, demonstrated that the nanoparticles are amenable to surface modifications, key element in solution processing. Further annealing ofmore » as-synthesized nanocrystals under a sulfur/argon atmosphere at 600 °C, rendered highly crystalline Cu 3VS 4 powders exhibiting an impurity that could be potentially mitigated by annealing temperature optimization. Furthermore, Cu 3VS 4, formed solely from Earth-abundant elements, could provide an inexpensive, reliable approach to fabricating solution processed thin film photovoltaic absorbers.« less

Sulvanite (Cu 3VS 4) nanocrystals for printable thin film photovoltaics

DOE Office of Scientific and Technical Information (OSTI.GOV)

Chen, Ching -Chin; Stone, Kevin H.; Lai, Cheng -Yu

Copper Vanadium Sulfide (Cu 3VS 4), also known as sulvanite, has recently emerged as a suitable absorber material for thin film photovoltaics. The synthesis of Cu 3VS 4 nanocrystals via a rapid solvothermal route is reported for the first time. The phase purity of the Cu 3VS 4 nanocrystals has been confirmed by X-ray powder diffraction (XRD) and Raman spectroscopy, while the nanoparticle size, of about 10 nm, was evaluated by transmission electron microscopy (TEM). Successful ligand exchange with sulfide, an inorganic ligand, demonstrated that the nanoparticles are amenable to surface modifications, key element in solution processing. Further annealing ofmore » as-synthesized nanocrystals under a sulfur/argon atmosphere at 600 °C, rendered highly crystalline Cu 3VS 4 powders exhibiting an impurity that could be potentially mitigated by annealing temperature optimization. Furthermore, Cu 3VS 4, formed solely from Earth-abundant elements, could provide an inexpensive, reliable approach to fabricating solution processed thin film photovoltaic absorbers.« less

The Cu2ZnSnSe4 thin films solar cells synthesized by electrodeposition route

NASA Astrophysics Data System (ADS)

Li, Ji; Ma, Tuteng; Wei, Ming; Liu, Weifeng; Jiang, Guoshun; Zhu, Changfei

2012-06-01

An electrodeposition route for preparing Cu2ZnSnSe4 thin films for thin film solar cell absorber layers is demonstrated. The Cu2ZnSnSe4 thin films are prepared by co-electrodeposition Cu-Zn-Sn metallic precursor and subsequently annealing in element selenium atmosphere. The structure, composition and optical properties of the films were investigated by X-ray diffraction (XRD), Raman spectrometry, energy dispersive spectrometry (EDS) and UV-VIS absorption spectroscopy. The Cu2ZnSnSe4 thin film with high crystalline quality was obtained, the band gap and absorption coefficient were 1.0 eV and 10-4 cm-1, which is quite suitable for solar cells fabrication. A solar cell with the structure of ZnO:Al/i-ZnO/CdS/Cu2ZnSnSe4/Mo/glass was fabricated and achieved an conversion efficiency of 1.7%.

Characterization of Hybrid Ferroelectric/HTS Thin Films for Tunable Microwave Components

NASA Technical Reports Server (NTRS)

Winters, M. D.; Mueller, C. H.; Bhasin, K. B.; Miranda, F. A.

1996-01-01

Since the discovery of High-Temperature-Superconductors (HTS) in 1986, a diversity of HTS-based microwave components has been demonstrated. Because of their low conductor losses, HTS-based components are very attractive for integration into microwave circuits for space communication systems. Recent advancements have made deposition of ferroelectric thin films onto HTS thin films possible. Due to the sensitivity of the ferroelectric's dielectric constant (epsilon(sub r)) to an externally applied electric field (E), ferroelectric/superconducting structures could be used in the fabrication of low loss, tunable microwave components. In this paper, we report on our study of Ba(0.5)Sr(0.5)TiO3/YBa2Cu3O(7-delta) and Ba(0.08)Sr(0.92)TiO3/YBa2Cu3O(7-delta) ferroelectric/superconducting thin films on lanthanum aluminate (LaAlO3) substrates. For the (Ba:Sr, 0.50:0.50) epitaxial sample, a epsilon(sub r) of 425 and a loss tangent (tan delta) of 0.040 were measured at 298 K, 1.0 MHz, and zero applied E. For the same sample, a epsilon(sub r) of 360 and tan delta of 0.036 were obtained at 77 K, 1.0 MHz, and zero applied E. Variations in epsilon(sub r) from 180 to 360 were observed over an applied E range of 0V/cm less than or equal to E less than or equal to 5.62 x 10(exp 4) V/cm with little change in tan delta. However, the range of epsilon(sub r) variation for the polycrystalline (Ba:Sr, 0.08:0.92) sample over 0V/cm less than or equal to E less than or equal to 4.00 x 10(exp 4) V/cm was only 3.6 percent while tan delta increased markedly. These results indicate that a lack of epitaxy between the ferroelectric and superconducting layers decreases tuning and increases microwave losses.

Modification of Optical, Structural and Dielectric Properties of MeV Ions Irradiated PS/Cu Nanocomposites.

PubMed

Gavade, Chaitali; Singh, N L; Khanna, P K; Shah, Sunil

2015-12-01

In order to study structural, thermal, optical and dielectric behaviors of composites, the films of Cu/polystyrene nanocomposites were synthesized at different concentrations of Cu-nanoparticles. These polymer nanocomposites were irradiated with carbon (85 MeV) and silicon (120 MeV) ions at different fluences. The samples were characterized using different techniques viz: X-ray diffraction, UV-visible spectroscopy, differential scanning calorimetry, and impedance gain phase analyzer. A noticeable increase in the intensity of X-ray diffraction peaks was observed after irradiation with 120 MeV Si-ions, which may be attributed to radiation-induced cross-linking in polymer. Optical properties like band gap was estimated for pure polymer and nanocomposite films from their optical absorption spectra in the wavelength region 200-800 nm. It was found that the band gap value shifted to lower energy (from 4.38 eV to 3.40 eV) on doping with silver nanoparticles and also upon irradiation. Differential scanning calorimetry analysis revealed an increase in the glass transition temperature upon irradiation, which may be attributed to cross linking of polymer chain due to ion beam irradiation which is also corroborated with XRD analysis. Dependence of dielectric properties on frequency, ions and filler concentration was studied. The results revealed the enhancement in dielectric properties after doping nanoparticles and also upon irradiation. It was observed that the effect of Si-beam is more effectual than the C-beam because of large electronic energy loss of heavy ion.

n-Type Conductivity of Cu2O Thin Film Prepared in Basic Aqueous Solution Under Hydrothermal Conditions

NASA Astrophysics Data System (ADS)

Ursu, Daniel; Miclau, Nicolae; Miclau, Marinela

2018-03-01

We report for the first time in situ hydrothermal synthesis of n-type Cu2O thin film using strong alkaline solution. The use of copper foil as substrate and precursor material, low synthesis temperature and short reaction time represent the arguments of a new, simple, inexpensive and high field synthesis method for the preparation of n-type Cu2O thin film. The donor concentration of n-type Cu2O thin film obtained at 2 h of reaction time has increased two orders of magnitude than previous reported values. We have demonstrated n-type conduction in Cu2O thin film prepared in strong alkaline solution, in the contradiction with the previous works. Based on experimental results, the synthesis mechanism and the origin of n-type photo-responsive behavior of Cu2O thin film were discussed. We have proposed that the unexpected n-type character could be explained by H doping of Cu2O thin film in during of the hydrothermal synthesis that caused the p-to-n conductivity-type conversion. Also, this work raises new questions about the origin of n-type conduction in Cu2O thin film, the influence of the synthesis method on the nature of the intrinsic defects and the electrical conduction behavior.

Chemical bath deposition of Cu{sub 3}BiS{sub 3} thin films

DOE Office of Scientific and Technical Information (OSTI.GOV)

Deshmukh, S.G., E-mail: deshmukhpradyumn@gmail.com; Vipul, Kheraj, E-mail: vipulkheraj@gmail.com; Panchal, A.K.

2016-05-06

First time, copper bismuth sulfide (Cu{sub 3}BiS{sub 3}) thin films were synthesized on the glass substrate using simple, low-cost chemical bath deposition (CBD) technique. The synthesized parameters such as temperature of bath, pH and concentration of precursors were optimized for the deposition of uniform, well adherent Cu{sub 3}BiS{sub 3} thin films. The optical, surface morphology and structural properties of the Cu{sub 3}BiS{sub 3} thin films were studied using UV-VIS-NIR spectra, scanning electron microscopy (SEM) and X-ray diffraction (XRD). The as- synthesized Cu{sub 3}BiS{sub 3} film exhibits a direct band gap 1.56 to 1.58 eV having absorption coefficient of the ordermore » of 10{sup 5} cm{sup −1}. The XRD declares the amorphous nature of the films. SEM images shows films were composed of close-packed fine spherical nanoparticles of 70-80 nm in diameter. The chemical composition of the film was almost stoichiometric. The optical study indicates that the Cu{sub 3}BiS{sub 3} films can be applied as an absorber layer for thin film solar cells.« less

Structural and optical studies on antimony and zinc doped CuInS2 thin films

NASA Astrophysics Data System (ADS)

Ben Rabeh, M.; Chaglabou, N.; Kanzari, M.; Rezig, B.

2009-11-01

The influence of Zn and Sb impurities on the structural, optical and electrical properties of CuInS2 thin films on corning 7059 glass substrates was studied. Undoped and Zn or Sb doped CuInS2 thin films were deposited by thermal evaporation method and annealed in vacuum at temperature of 450 ∘C Undoped thin films were grown from CuInS2 powder using resistively heated tungsten boats. Zn species was evaporated from a thermal evaporator all together to the CuInS2 powder and Sb species was mixed in the starting powders. The amount of the Zn or Sb source was determined to be in the range 0-4 wt% molecular weight compared with the CuInS2 alloy source. The films were studied by means of X-ray diffraction (XRD), Optical reflection and transmission and resistance measurements. The films thicknesses were in the range 450-750 nm. All the Zn: CuInS2 and Sb: CuInS2 thin films have relatively high absorption coefficient between 104 cm-1 and 105 cm-1 in the visible and the near-IR spectral range. The bandgap energies are in the range of 1.472-1.589 eV for Zn: CuInS2 samples and 1.396-1.510 eV for the Sb: CuInS2 ones. The type of conductivity of these films was determined by the hot probe method. Furthermore, we found that Zn and Sb-doped CuInS2 thin films exhibit P type conductivity and we predict these species can be considered as suitable candidates for use as acceptor dopants to fabricate CuInS2-based solar cells.

Electric Transport Phenomena of Nanocomposite Organic Polymer Thin Films

NASA Astrophysics Data System (ADS)

Jira, Nicholas C.; Sabirianov, Ildar; Ilie, Carolina C.

We discuss herein the nanocomposite organic thin film diodes for the use of plasmonic solar cells. This experimental work follows the theoretical calculations done for plasmonic solar cells using the MNPBEM toolbox for MatLab. These calculations include dispersion curves and amount of light scattering cross sections for different metallic nanoparticles. This study gives us clear ideas on what to expect from different metals, allowing us to make the best choice on what to use to obtain the best results. One specific technique for light trapping in thin films solar cells utilizes metal nanoparticles on the surface of the semiconductor. The characteristics of the metal, semiconductor interface allows for light to be guided in between them causing it to be scattered, allowing for more chances of absorption. The samples were fabricated using organic thin films made from polymers and metallic nanoparticles, more specifically Poly(1-vinylpyrrolidone-co-2-dimethylaminoethyl methacrylate) copolymer and silver or gold nanoparticles. The two fabrication methods applied include spin coating and Langmuir-Blodgett technique. The transport properties are obtained by analyzing the I-V curves. We will also discuss the resistance, resistivity, conductance, density of charge carriers. SUNY Oswego SCAC Grant.

Physical Characterization of Cu-Ni-P Thin Films aiming at Cu/Cu-Ni-P Thermocouples

NASA Astrophysics Data System (ADS)

Tomachevski, F.; Sparvoli, M.; dos Santos Filho, S. G.

2015-03-01

Cu-Ni-P thin films have a high-thermoelectric power, which allows the fabrication of very sensitive heat-flux sensors based on planar technology. In this work, (100) silicon surfaces were pre-activated in a diluted hydrofluoric acid solution containing PdCl2. Following, Cu-Ni-P thin films were chemically deposited using an alkaline chemical bath containing 15 g/l NiSO4.6H2O; 0.2 g/l CuSO4.5H2O; 15 g/l Na2HPO2.H2O and 60 g/l Na3C6H5O7.2H2O at temperature of 80 °C where NH4OH was added until pH was 8.0. It was noteworthy that the stoichiometric percentages of Ni and Cu vary substantially for immersion times in the range of 1 to 3 min and they become almost stable at 50% and 35%, respectively, when the immersion time is higher than 3 min. In addition, the percentage of P remains almost constant around 1718 % for all the immersion times studied. On the other hand, the sheet resistance also varies substantially for immersion times in the range of 1 to 3 min. Based on the surface morphology, smaller grains with size in the range of 0.02 to 0.1 μm are initially grown on the silicon surface and exposed regions of silicon without deposits are also observed for immersion times in the range of 1 to 3min. Therefore, the discontinuities and non uniformities of the films are promoting, respectively, the observed behaviours of sheet resistance and stoichiometry.

The effect of thin film morphology on the electrochemical performance of Cu-Sn anode for lithium rechargeable batteries.

PubMed

Polat, B D; Keleş, O

2014-05-01

We investigate the anode performance of non ordered and ordered nanostructured Cu-Sn thin films deposited via electron beam deposition technique. The ordered nanostructured Cu-Sn thin film having nano-porosities was fabricated using an oblique (co)deposition technique. Our results showed that the nano structured Cu-Sn thin film containing Cu-Sn nanorods had higher initial anodic capacity (790 mA h g(-)) than that of the non ordered thin film (330 mA h g(-)). But the capacity of the ordered nanostructured Cu-Sn thin film diminished after the first cycle and a steady state capacity value around 300 mA h g(-) is sustainable in following up to 80th cycle, which is attributed to the composition and morphology of the thin film. The presence of copper containing Sn nanorods leading to form nano-porosities as interstitial spaces among them, enhanced lithium ions movement within thin film and increased the thin film tolerance against the stress generated because of the drastic volume change occurred during lithiation-delithiation processes; hence, homogenously distributed porosities increased the cycle life of the thin film.

Very high commutation quality factor and dielectric tunability in nanocomposite SrTiO 3 thin films with T c enhanced to >300 °C

DOE PAGES

Sangle, Abhijeet L.; Lee, Oon Jew; Kursumovic, Ahmed; ...

2018-02-05

We report on nanoengineered SrTiO 3–Sm2O 3 nanocomposite thin films with the highest reported values of commutation quality factor (CQF or K-factor) of >2800 in SrTiO 3 at room temperature. The films also had a large tunability of dielectric constant (49%), low tangent loss (tan δ = 0.01) and a Curie temperature for SrTiO 3 > 300 °C, making them very attractive for tunable RF applications. The enhanced properties originate from the unique nanostructure in the films, with <20 nm diameter strain-controlling Sm 2O 3 nanocolumns embedded in a SrTiO 3 matrix. Very large out-of-plane strains (up to 2.6%) andmore » high tetragonality (c/a) (up to 1.013) were induced in the SrTiO 3. Finally, the K-factor was further enhanced by adding 1 at% Sc 3+ (acceptor) dopant in SrTiO 3 to a value of 3300 with the tangent loss being ≤0.01 up to 1000 kV cm -1.« less

Very high commutation quality factor and dielectric tunability in nanocomposite SrTiO 3 thin films with T c enhanced to >300 °C

DOE Office of Scientific and Technical Information (OSTI.GOV)

Sangle, Abhijeet L.; Lee, Oon Jew; Kursumovic, Ahmed

We report on nanoengineered SrTiO 3–Sm2O 3 nanocomposite thin films with the highest reported values of commutation quality factor (CQF or K-factor) of >2800 in SrTiO 3 at room temperature. The films also had a large tunability of dielectric constant (49%), low tangent loss (tan δ = 0.01) and a Curie temperature for SrTiO 3 > 300 °C, making them very attractive for tunable RF applications. The enhanced properties originate from the unique nanostructure in the films, with <20 nm diameter strain-controlling Sm 2O 3 nanocolumns embedded in a SrTiO 3 matrix. Very large out-of-plane strains (up to 2.6%) andmore » high tetragonality (c/a) (up to 1.013) were induced in the SrTiO 3. Finally, the K-factor was further enhanced by adding 1 at% Sc 3+ (acceptor) dopant in SrTiO 3 to a value of 3300 with the tangent loss being ≤0.01 up to 1000 kV cm -1.« less

Highly recyclable and ultra-rapid catalytic reduction of organic pollutants on Ag-Cu@ZnO bimetal nanocomposite synthesized via green technology

NASA Astrophysics Data System (ADS)

Gangarapu, Manjari; Sarangapany, Saran; Suja, Devipriya P.; Arava, Vijaya Bhaskara Rao

2018-04-01

In this study, synthesis of Ag-Cu alloy bimetal nanoparticles anchored on high surface and porous ZnO using a facile, greener and low-cost aqeous bark extract of Aglaia roxburghiana for highly active, ultra-rapid and stable catalyst is performed. The nanocomposite was scrupulously characterized using UV-Vis spectrophotometer, X-ray diffraction, Raman spectrophotometer, high-resolution transmission electron microscope, selected area (electron) diffraction, scanning electron microscope with energy dispersive X-ray spectroscopy, and Fourier-transform infrared spectroscopy. The catalytic activity of the green synthesized Ag-Cu bimetal nanocomposite was evaluated in the reduction of 4-nitrophenol (4-NP), methylene blue (MB) and rhodamine B (Rh B) dyes. The different types of dye exhibited very high and effective catalytic activity within few seconds. The theoretical investigations reveal that the unique synergistic effect of Ag-Cu nanoparticles and immobilization over ZnO assists in the reduction of 4-NP, MB and Rh B. Loading and leaching of metal nanoparticles were obtained using inductively coupled plasma atomic emission spectroscopy. Moreover, the stable and efficient recyclability of nanocomposite by centrifugation after completion of the reaction was demonstrated. The results lead to the design different possible bimetal on ZnO with boosting and an effective catalyst for the environmental applications.

KF addition to Cu2SnS3 thin films prepared by sulfurization process

NASA Astrophysics Data System (ADS)

Nakashima, Mitsuki; Fujimoto, Junya; Yamaguchi, Toshiyuki; Sasano, Junji; Izaki, Masanobu

2017-04-01

Cu2SnS3 thin films were fabricated by sulfurization with KF addition and applied to photovoltaic devices. Two methods, two-stage annealing and the use of four-layer precursors, were employed, and the quantity of NaF and KF and the annealing temperature were changed. By electron probe microanalysis (EPMA), the Cu/Sn mole ratio was found to range from 0.81 to 1.51. The X-ray diffraction (XRD) patterns and Raman spectra indicated that the fabricated thin films had a monoclinic Cu2SnS3 structure. The Cu2SnS3 thin films fabricated by two-stage annealing had a close-packed structure and a pinhole-free surface morphology. The best solar cell in this study showed V oc of 293 mV, which surpassed the previously reported value.

Growth and characterization of sol-gel derived CuGaO2 semiconductor thin films for UV photodetector application

NASA Astrophysics Data System (ADS)

Tsay, Chien-Yie; Chen, Ching-Lien

2017-06-01

In this study, a p-type wide-bandgap oxide semiconductor CuGaO2 thin film was grown on quartz substrate by sol-gel method. The authors report the influence of annealing temperature on the phase transformation, structural features, and electrical properties of sol-gel derived Cu-Ga-O thin films. At relatively low annealing temperatures (≤900 °C), the films are a mixture of CuGa2O4, CuGaO2, and CuO phases. At relatively high annealing temperatures (≥925 °C), the majority phase in the films is delafossite CuGaO2. All as-prepared Cu-Ga-O thin films exhibited p-type conductivity, as confirmed by Hall measurements. The mean electrical resistivity of the Cu-Ga-O films decreased from 3.54×104 Ω-cm to 1.35×102 Ω-cm and then increased slightly to 3.51×102 Ω-cm when the annealing temperature was increased from 850 °C to 950 °C. We found that annealing the Cu-based oxide thin films at 925 °C produced nearly phase-pure CuGaO2 thin films with good densification. Such thin films exhibited the best electrical properties: a mean electrical resistivity of 1.35×102 Ω-cm, and a mean hole concentration of 1.60×1016 cm-3. In addition, we also fabricated and characterized MSM-type CuGaO2 UV photodetectors on quartz substrates.

Manipulation of ZnO composition affecting electrical properties of MEH-PPV: ZnO nanocomposite thin film via spin coating for OLEDs application

NASA Astrophysics Data System (ADS)

Azhar, N. E. A.; Shariffudin, S. S.; Alrokayan, Salman A. H.; Khan, Haseeb A.; Rusop, M.

2018-05-01

Recent investigations of the promising materials for optoelectronic have been demonstrated by introducing n-type inorganic material into conjugated polymer. Morphology, optical and electrical of nanocomposites thin films based on poly[2-methoxy-5-(2'-ethyl-hexyloxy)-1,4-phenylene vinylene] (MEH-PPV) and zinc oxide (ZnO) nanotetrapods with various ZnO composition (0 wt% to 0.4 wt%) have been investigated. The MEH-PPV: ZnO nanocomposite thin film was deposited using spin-coating method. Surface morphology was characterized using field emission scanning electron microscopy and shows the uniform dispersion of MEH-PPV and ZnO phases for sample deposited at 0.2 wt%. The photoluminescence (PL) spectra shows the visible emission intensities increased when the ZnO composition increased. The current-voltage (I-V) measurement shows the highest conductivity of nanocomposite thin film deposited at 0.2 wt% of ZnO is 7.40 × 10-1 S. cm-1. This study will provide better performance and suitable for optoelectronic device especially OLEDs application.

Controlled electrodeposition of Cu-Ga from a deep eutectic solvent for low cost fabrication of CuGaSe2 thin film solar cells.

PubMed

Steichen, Marc; Thomassey, Matthieu; Siebentritt, Susanne; Dale, Phillip J

2011-03-14

The electrochemical deposition of Ga and Cu-Ga alloys from the deep eutectic solvent choline chloride/urea (Reline) is investigated to prepare CuGaSe(2) (CGS) semiconductors for their use in thin film solar cells. Ga electrodeposition is difficult from aqueous solution due to its low standard potential and the interfering hydrogen evolution reaction (HER). Ionic liquid electrolytes offer a better thermal stability and larger potential window and thus eliminate the interference of solvent breakdown reactions during Ga deposition. We demonstrate that metallic Ga can be electrodeposited from Reline without HER interference with high plating efficiency on Mo and Cu electrodes. A new low cost synthetic route for the preparation of CuGaSe(2) absorber thin films is presented and involves the one-step electrodeposition of Cu-Ga precursors from Reline followed by thermal annealing. Rotating disk electrode (RDE) cyclic voltammetry (CV) is used in combination with viscosity measurements to determine the diffusion coefficients of gallium and copper ions in Reline. The composition of the codeposited Cu-Ga precursor layers can be controlled to form Cu/Ga thin films with precise stoichiometry, which is important for achieving good optoelectronic properties of the final CuGaSe(2) absorbers. The morphology, the chemical composition and the crystal structure of the deposited thin films are analysed by scanning electron microscopy/energy dispersive X-ray spectroscopy (SEM/EDX) and X-ray diffraction (XRD). Annealing of the Cu-Ga films in a selenium atmosphere allowed the formation of high quality CuGaSe(2) absorber layers. Completed CGS solar cells achieved a 4.1% total area power conversion efficiency.

Theoretical studies on the possible sensitizers of DSSC: Nanocomposites of graphene quantum dot hybrid phthalocyanine/tetrabenzoporphyrin/tetrabenzotriazaporphyrins/cis-tetrabenzodiazaporphyrins/tetrabenzomonoazaporphyrins and their Cu-metallated macrocycles

NASA Astrophysics Data System (ADS)

Gao, Feng; Yang, Chuan-Lu; Wang, Mei-Shan; Ma, Xiao-Guang; Liu, Wen-Wang

2018-04-01

The feasibility of nanocomposites of cir-coronene graphene quantum dot (GQD) with phthalocyanine, tetrabenzoporphyrin, tetrabenzotriazaporphyrins, cis-tetrabenzodiazaporphyrins, tetrabenzomonoazaporphyrins and their Cu-metallated macrocycles as a sensitizer of dye-sensitized solar cells (DSSC) are investigated. Based on the first principles density functional theory (DFT), the geometrical structures of the separate GQD and 10 macrocycles, and their hybridized nanocomposites are fully optimized. The energy stabilities of the obtained structures are confirmed by harmonic frequency analysis. The optical absorptions of the optimized structures are calculated with time-dependent DFT. The feasibility of the nanocomposites as the sensitizer of DSSC is examined by the charge spatial separation, the electron transfer, the molecular orbital energy levels of the nanocomposites and the electrolyte, and the conduction band minimum of TiO2 electrode. The results demonstrate that all the nanocomposites have enhanced absorptions in the visible light range, and their molecular orbital energies satisfy the requirement of sensitizers. However, only two of the ten considered nanocomposites demonstrate significantly charge spatial separation. The GQD-Cu-TBP is identified as the most favorable candidate sensitizer of DSSC by the most enhanced in optical absorption, obvious charge spatial separation, suitable LUMO energy levels and driving force for electron transfer, and low recombination rate of electron and hole.

Synthesis of high-oxidation Y-Ba-Cu-O phases in superoxygenated thin films

NASA Astrophysics Data System (ADS)

Zhang, H.; Gauquelin, N.; McMahon, C.; Hawthorn, D. G.; Botton, G. A.; Wei, J. Y. T.

2018-03-01

It is known that solid-state reaction in high-pressure oxygen can stabilize high-oxidation phases of Y-Ba-Cu-O superconductors in powder form. We extend this superoxygenation concept of synthesis to thin films which, due to their large surface-to-volume ratio, are more reactive thermodynamically. Epitaxial thin films of YBa2Cu3O7 -δ grown by pulsed laser deposition are annealed at up to 700 atm O2 and 900 ∘C , in conjunction with Cu enrichment by solid-state diffusion. The films show the clear formation of Y2Ba4Cu7O15 -δ and Y2Ba4Cu8O16 as well as regions of YBa2Cu5O9 -δ and YBa2Cu6O10 -δ phases, according to scanning transmission electron microscopy, x-ray diffraction, and x-ray absorption spectroscopy. Similarly annealed YBa2Cu3O7 -δ powders show no phase conversion. Our results demonstrate a route of synthesis towards discovering more complex phases of cuprates and other superconducting oxides.

Photocatalytic dye degradation with copper-titanium dioxide nanocomposites under sunlight and visible light irradiation

NASA Astrophysics Data System (ADS)

Qayyum Khan, Abdul; Yuan, Shuai; Niu, Sheng; Liu, Fengjiang; Feng, Guang; Jiang, Mengci; Zeng, Heping

2018-01-01

Photocatalytic methalyne blue dye degradation was carried out with copper (Cu)-titanium dioxide (TiO2) nanocomposites under sunlight and visible light irradiation. The Cu-TiO2 nanocomposites were fabricated via femtosecond laser ablation of pressed targets in water. The current method provides a facile route for Cu-TiO2 nanocomposites preparation, which is free from impurities on the catalysts surface. The Cu-TiO2 nanocomposites (with Cu content of 5 wt%) have shown 3 folds faster dye degradation kinetics compared with TiO2 nanoparticles under sunlight irradiation. While under visible light irradiation, the same nanocomposites exhibited 2.6 folds faster kinetics compared with TiO2 nanoparticles. The faster light harvesting efficiency of the catalysts is attributed to more hydroxyl radical generation.

Magazine Exposure, Tanned Women Stereotypes, and Tanning Attitudes

PubMed Central

Lee, Seungyoon; Wilson, Kari

2010-01-01

This study investigated whether magazine exposure is related to stereotypical beliefs about tanned women. A survey of White college women (n = 205) assessed their exposure to beauty/fashion and health/fitness magazines. Outcome variables were the beliefs that tanned women are fashionable, fit, and shallow. Attention to the tanned women’s images in health magazines positively predicted the belief that tanned women are fit and that tanned women are shallow; in contrast, attention to the images in beauty magazine negatively predicted the belief that tanned women are fit. Number of beauty magazines women read negatively predicted the belief that tanned women are shallow. The belief that tanned women are fit was unrelated, but the belief that tanned women are shallow was negatively related, with tanning attitudes. PMID:20573553

Magazine exposure, tanned women stereotypes, and tanning attitudes.

PubMed

Cho, Hyunyi; Lee, Seungyoon; Wilson, Kari

2010-09-01

This study investigated whether magazine exposure is related to stereotypical beliefs about tanned women. A survey of White college women (n=205) assessed their exposure to beauty/fashion and health/fitness magazines. Outcome variables were the beliefs that tanned women are fashionable, fit, and shallow. Attention to the tanned women's images in health magazines positively predicted the belief that tanned women are fit and that tanned women are shallow; in contrast, attention to the images in beauty magazine negatively predicted the belief that tanned women are fit. Number of beauty magazines women read negatively predicted the belief that tanned women are shallow. The belief that tanned women are fit was unrelated, but the belief that tanned women are shallow was negatively related, with tanning attitudes. Copyright © 2010 Elsevier Ltd. All rights reserved.

Cu-doped CdS and its application in CdTe thin film solar cell

DOE Office of Scientific and Technical Information (OSTI.GOV)

Deng, Yi; College of Electronic and Information Engineering, Hankou University, Wuhan, Hubei 430212; Yang, Jun

2016-01-15

Cu is widely used in the back contact formation of CdTe thin film solar cells. However, Cu is easily to diffuse from the back contact into the CdTe absorber layer and even to the cell junction interface CdS/CdTe. This phenomenon is generally believed to be the main factor affecting the CdTe solar cell stability. In this study Cu was intentionally doped in CdS thin film to study its effect on the microstructural, optical and electrical properties of the CdS material. Upon Cu doping, the V{sub Cd{sup −}} and the surface-state-related photoluminescence emissions were dramatically decreased/quenched. The presence of Cu atommore » hindered the recrystallization/coalescence of the nano-sized grains in the as-deposited CdS film during the air and the CdCl{sub 2} annealing. CdTe thin film solar cell fabricated with Cu-doped CdS window layers demonstrated much decreased fill factor, which was induced by the increased space-charge recombination near the p-n junction and the worsened junction crystalline quality. Temperature dependent current-voltage curve measurement indicated that the doped Cu in the CdS window layer was not stable at both room and higher temperatures.« less

Stress and plasticity in Cu thin films

NASA Astrophysics Data System (ADS)

Weihnacht, Volker; Brückner, Winfried

1999-11-01

Aim of the work was to get more detailed knowledge about the processes of plasticity in thin Cu films. For this purpose, stress measurements and microstructural investigations have been done on 535nm thick Cu films on oxidized Si substrates. The film stress was measured by wafer-curvature technique using a home-made laser-optical apparatus. This apparatus allowed four-point bending experiments additionally to thermal cycling. It turned out that applied bending strains even higher than 0.5% did not leave significant plastic strains after relief of bending stress. It is concluded, that the elastic interaction of parallel dislocations at the film-substrate interface may play an important role in strain hardening even after small plastic strains.

Cu2SixSn1-xS3 Thin Films Prepared by Reactive Magnetron Sputtering For Low-Cost Thin Film Solar Cells

NASA Astrophysics Data System (ADS)

Yan, Chang; Liu, Fang-Yang; Lai, Yan-Qing; Li, Jie; Liu, Ye-Xiang

2011-10-01

We report the preparation of Cu2SixSn1-xS3 thin films for thin film solar cell absorbers using the reactive magnetron co-sputtering technique. Energy dispersive spectrometer and x-ray diffraction analyses indicate that Cu2Si1-xSnxS3 thin films can be synthesized successfully by partly substituting Si atoms for Sn atoms in the Cu2SnS3 lattice, leading to a shrinkage of the lattice, and, accordingly, by 2θ shifting to larger values. The blue shift of the Raman peak further confirms the formation of Cu2SixSn1-xS3. Environmental scanning electron microscope analyses reveal a polycrystalline and homogeneous morphology with a grain size of about 200-300 nm. Optical measurements indicate an optical absorption coefficient of higher than 104 cm-1 and an optical bandgap of 1.17±0.01 eV.

Observations on Si-based micro-clusters embedded in TaN thin film deposited by co-sputtering with oxygen contamination

DOE Office of Scientific and Technical Information (OSTI.GOV)

Lee, Young Mi; Jung, Min-Sang; Choi, Duck-Kyun, E-mail: duck@hanyang.ac.kr, E-mail: mcjung@oist.jp

2015-08-15

Using scanning electron microscopy (SEM) and high-resolution x-ray photoelectron spectroscopy with the synchrotron radiation we investigated Si-based micro-clusters embedded in TaSiN thin films having oxygen contamination. TaSiN thin films were deposited by co-sputtering on fixed or rotated substrates and with various power conditions of TaN and Si targets. Three types of embedded micro-clusters with the chemical states of pure Si, SiO{sub x}-capped Si, and SiO{sub 2}-capped Si were observed and analyzed using SEM and Si 2p and Ta 4f core-level spectra were derived. Their different resistivities are presumably due to the different chemical states and densities of Si-based micro-clusters.

A comparison study of Co and Cu doped MgO diluted magnetic thin films

NASA Astrophysics Data System (ADS)

Sarıtaş, S.; ćakıcı, T.; Muǧlu, G. Merhan; Kundakcı, M.; Yıldırım, M.

2017-02-01

Transition metal-doped MgO diluted magnetic thin films are appropriate candidates for spintronic applications and designing magnetic devices and sensors. Therefore, MgO:Co and MgO:Cu films were deposited on glass substrates by Chemical Spray Pyrolysis (CSP) method different thin film deposition parameters. Deposited different transition metal doped MgO thin films were compared in terms of optic and structural properties. Comparison optic analysis of the films was investigated spectral absorption and transmittance measurements by UV-Vis double beam spectrophotometer technique. Comparison structural analysis of the thin films was examined by using XRD, Raman Analysis, SEM, EDX and AFM techniques. The transition metal-doped; MgO:Co and MgO:Cu thin films maybe have potential applications in spintronics and magnetic data storage.

Investigation of thin film solar cells based on Cu2S and ternary compounds such as CuInS2

NASA Technical Reports Server (NTRS)

Loferski, J. J.

1975-01-01

Production and characterization in thin film form of Cu2S and related Cu compounds such as CuInS2 for photovoltaic cells are examined. The low cost process technology being reported, namely the sulfurization method, is capable of producing films on various substrates. Cathodoluminescence is being used as a diagnostic tool to identify Cu(x)S and CuInS2 compounds. Also, single crystals of CuInS2 are being prepared and it is contemplated that p-n junctions will be made in such crystals.

Measuring nonsolar tanning behavior: indoor and sunless tanning.

PubMed

Lazovich, Deann; Stryker, Jo Ellen; Mayer, Joni A; Hillhouse, Joel; Dennis, Leslie K; Pichon, Latrice; Pagoto, Sherry; Heckman, Carolyn; Olson, Ardis; Cokkinides, Vilma; Thompson, Kevin

2008-02-01

To develop items to measure indoor tanning and sunless tanning that can be used to monitor trends in population surveys or to assess changes in behavior in intervention studies. A group of experts on indoor tanning convened in December 2005, as part of a national workshop to review the state of the evidence, define measurement issues, and develop items for ever tanned indoors, lifetime frequency, and past-year frequency for both indoor tanning and sunless tanning. Each item was subsequently assessed via in-person interviews for clarity, specificity, recall, and appropriateness of wording. Universities in Tennessee and Virginia, a medical center in Massachusetts, and a high school in New Hampshire. The study population comprised 24 adults and 7 adolescents. Participants understood indoor tanning to represent tanning from beds, booths, and lamps that emit artificial UV radiation, rather than sunless tanning, even though both can be obtained from a booth. Two items were required to distinguish manually applied from booth-applied sunless tanning products. Frequency of use was easier for participants to recall in the past year than for a lifetime. While indoor tanning items may be recommended with confidence for clarity, sunless tanning items require additional testing. Memory aids may be necessary to facilitate recall of lifetime use of nonsolar tanning. In addition, studies that assess reliability and validity of these measures are needed. Since study participants were primarily young and female, testing in other populations should also be considered.

Optical and microwave detection using Bi-Sr-Ca-Cu-O thin films

NASA Technical Reports Server (NTRS)

Grabow, B. E.; Sova, R. M.; Boone, B. G.; Moorjani, K.; Kim, B. F.; Bohandy, J.; Adrian, F.; Green, W. J.

1990-01-01

Recent progress at the Johns Hopkins University Applied Physics Laboratory (JHU/APL) in the development of optical and microwave detectors using high temperature superconducting thin films is described. Several objectives of this work have been accomplished, including: deposition of Bi-Sr-Ca-Cu-O thin films by laser abation processing (LAP); development of thin film patterning techniques, including in situ masking, wet chemical etching and laser patterning; measurements of bolometric and non-bolometric signatures in patterned Bi-Sr-Ca-Cu-O films using optical and microwave sources, respectively; analysis and design of an optimized bolometer through computer simulation, and investigation of its use in a Fourier transform spectrometer. The focus here is primarily on results from the measurement of the bolometric and non-bolometric response.

Optical and microwave detection using Bi-Sr-Ca-Cu-O thin films

NASA Technical Reports Server (NTRS)

Grabow, B. E.; Sova, R. M.; Boone, B. G.; Moorjani, K.; Kim, B. F.; Bohandy, J.; Adrian, F.; Green, W. J.

1991-01-01

Recent progress at the Johns Hopkins University Applied Physics Laboratory (JHU/APL) in the development of optical and microwave detectors using high temperature superconducting thin films is described. Several objectives of this work have been accomplished, including: deposition of Bi-Sr-Ca-Cu-O thin films by laser abation processing (LAP); development of thin film patterning techniques, including in situ masking, wet chemical etching, and laser patterning; measurements of bolometric and non-bolometric signatures in patterned Bi-Sr-Ca-Cu-O films using optical and microwave sources, respectively; analysis and design of an optimized bolometer through computer simulation; and investigation of its use in a Fourier transform spectrometer. The focus here is primarily on results from the measurement of the bolometric and non-bolometric response.

Preparation of CuO/ZnO nanocomposite and its application as a cysteine/homocysteine colorimetric and fluorescence detector.

PubMed

Šimšíková, Michaela; Čechal, Jan; Zorkovská, Anna; Antalík, Marián; Šikola, Tomáš

2014-11-01

Cysteine and homocysteine play a crucial role in many biological functions but abnormal levels of these amino acids may lead to various forms of pathogenesis. Therefore, selective and easy-to-use methods for the detection of cysteine and homocysteine are essential for the early diagnosis of developing diseases. In this paper we report on a rapid, straightforward and highly selective method for the detection of cysteine (Cys) and homocysteine (Hcy) which uses a CuO/ZnO nanocomposite as a dual colorimetric and fluorometric assay. The presence of Cys and Hcy in a solution of these nanorods (NRs) induces a change in its color from light blue to dark grey which is visible to the naked eye. This is accompanied by a blue shift in the absorption spectra from 725 nm to 650 nm and a decrease in the intensity of CuO/ZnO nanocomposite emission. These changes are ascribed to the reduction of Cu(II) to Cu(0), and the oxidation of cysteine (homocysteine) and subsequent formation of the disulfide bond. This novel assay method does not respond to any other amino-acid which is present in living organisms; therefore the selective determination of cysteine (homocysteine) with a lower analyte limit of 40 μM (4.8 μg mL(-1)) can be carried out in aqueous solutions without the need for any sophisticated instrumentation, fluorophore molecules or complicated procedures. Copyright © 2014 Elsevier B.V. All rights reserved.

Amorphization reaction in thin films of elemental Cu and Y

NASA Astrophysics Data System (ADS)

Johnson, R. W.; Ahn, C. C.; Ratner, E. R.

1989-10-01

Compositionally modulated thin films of Cu and Y were prepared in an ultrahigh-vacuum dc ion-beam deposition chamber. The amorphization reaction was monitored by in situ x-ray-diffraction measurements. Growth of amorphous Cu1-xYx is observed at room temperature with the initial formation of a Cu-rich amorphous phase. Further annealing in the presence of unreacted Y leads to Y enrichment of the amorphous phase. Growth of crystalline CuY is observed for T=469 K. Transmission-electron-microscopy measurements provide real-space imaging of the amorphous interlayer and growth morphology. Models are developed, incorporating metastable interfacial and bulk free-energy diagrams, for the early stage of the amorphization reaction.

Low-Temperature Atomic Layer Deposition of CuSbS2 for Thin-Film Photovoltaics.

PubMed

Riha, Shannon C; Koegel, Alexandra A; Emery, Jonathan D; Pellin, Michael J; Martinson, Alex B F

2017-02-08

Copper antimony sulfide (CuSbS 2 ) has been gaining traction as an earth-abundant absorber for thin-film photovoltaics given its near ideal band gap for solar energy conversion (∼1.5 eV), large absorption coefficient (>10 4 cm -1 ), and elemental abundance. Through careful in situ analysis of the deposition conditions, a low-temperature route to CuSbS 2 thin films via atomic layer deposition has been developed. After a short (15 min) postprocess anneal at 225 °C, the ALD-grown CuSbS 2 films were crystalline with micron-sized grains, exhibited a band gap of 1.6 eV and an absorption coefficient >10 4 cm -1 , as well as a hole concentration of 10 15 cm -3 . Finally, the ALD-grown CuSbS 2 films were paired with ALD-grown TiO 2 to form a photovoltaic device. This photovoltaic device architecture represents one of a very limited number of Cd-free CuSbS 2 PV device stacks reported to date, and it is the first to demonstrate an open-circuit voltage on par with CuSbS 2 /CdS heterojunction PV devices. While far from optimized, this work demonstrates the potential for ALD-grown CuSbS 2 thin films in environmentally benign photovoltaics.

Low-temperature atomic layer deposition of CuSbS 2 for thin-film photovoltaics

DOE PAGES

Riha, Shannon C.; Koegel, Alexandra A.; Emery, Jonathan D.; ...

2017-01-24

Copper antimony sulfide (CuSbS 2) has been gaining traction as an earth-abundant absorber for thin-film photovoltaics given its near ideal band gap for solar energy conversion (~1.5 eV), large absorption coefficient (>10 4 cm –1), and elemental abundance. Through careful in situ analysis of the deposition conditions, a low-temperature route to CuSbS 2 thin films via atomic layer deposition has been developed. After a short (15 min) post process anneal at 225 °C, the ALD-grown CuSbS 2 films were crystalline with micron-sized grains, exhibited a band gap of 1.6 eV and an absorption coefficient >10 4 cm –1, as wellmore » as a hole concentration of 10 15 cm –3. Finally, the ALD-grown CuSbS 2 films were paired with ALD-grown TiO 2 to form a photovoltaic device. This photovoltaic device architecture represents one of a very limited number of Cd-free CuSbS 2 PV device stacks reported to date, and it is the first to demonstrate an open-circuit voltage on par with CuSbS 2/CdS heterojunction PV devices. As a result, while far from optimized, this work demonstrates the potential for ALD-grown CuSbS 2 thin films in environmentally benign photovoltaics.« less

Performance enhancement in Sb doped Cu(InGa)Se2 thin film solar cell by e-beam evaporation

NASA Astrophysics Data System (ADS)

Chen, Jieyi; Shen, Honglie; Zhai, Zihao; Li, Yufang; Yi, Yunge

2018-03-01

To investigate the effects of Sb doping on the structural and electrical properties of Cu(InGa)Se2 (CIGS) thin films and solar cells, CIGS thin films, prepared by e-beam evaporation on soda-lime glass, were doped with lower and upper Sb layers in the precursor stacks respectively. Change of structure and introduction of stress were observed in the CIGS thin films with upper Sb layer in stack through XRD and Raman measurement. Both crystalline quality and compactness of CIGS thin films were improved by the doping of upper Sb layer in stack and the CIGS thin film showed an optimal structural property with 20 nm Sb layer. Movement of Fermi level of the surface of CIGS thin film after doping of upper Sb layer in stack and electrons transfer between Cu/Cu+ redox couple and CIGS thin films, which provided probability for the substitution of Sb for Cu sites at the surface of CIGS thin films, were proposed to explain the migration of Cu from the surface to the bulk of CIGS thin films. The larger barrier at the CIGS/CdS interface after doping of upper Sb layer in stack made contribution to the increase of VOC of CIGS solar cells. The efficiency of CIGS solar cell was improved from 3.3% to 7.2% after doping with 20 nm upper Sb. Compared to the CIGS solar cell with lower Sb layer in stack, in which an additional Cu2-xSe phase was found, the CIGS solar cell with upper Sb layer in stack possessed a higher efficiency.

The effect of stoichiometry on Cu-Zn ordering kinetics in Cu2ZnSnS4 thin films

NASA Astrophysics Data System (ADS)

Rudisch, Katharina; Davydova, Alexandra; Platzer-Björkman, Charlotte; Scragg, Jonathan

2018-04-01

Cu-Zn disorder in Cu2ZnSnS4 (CZTS) may be responsible for the large open circuit voltage deficit in CZTS based solar cells. In this study, it was investigated how composition-dependent defect complexes influence the order-disorder transition. A combinatorial CZTS thin film sample was produced with a cation composition gradient across the sample area. The graded sample was exposed to various temperature treatments and the degree of order was analyzed with resonant Raman spectroscopy for various compositions ranging from E- and A-type to B-, F-, and C-type CZTS. We observe that the composition has no influence on the critical temperature of the order-disorder transition, but strongly affects the activation energy. Reduced activation energy is achieved with compositions with Cu/Sn > 2 or Cu/Sn < 1.8 suggesting an acceleration of the cation ordering in the presence of vacancies or interstitials. This is rationalized with reference to the effect of point defects on exchange mechanisms. The implications for reducing disorder in CZTS thin films are discussed in light of the new findings.

Dielectric spectroscopy of Ag-starch nanocomposite films

NASA Astrophysics Data System (ADS)

Meena; Sharma, Annu

2018-04-01

In the present work Ag-starch nanocomposite films were fabricated via chemical reduction route. The formation of Ag nanoparticles was confirmed using transmission electron microscopy (TEM). Further the effect of varying concentration of Ag nanoparticles on the dielectric properties of starch has been studied. The frequency response of dielectric constant (ε‧), dielectric loss (ε″) and dissipation factor tan(δ) has been studied in the frequency range of 100 Hz to 1 MHz. Dielectric data was further analysed using Cole-Cole plots. The dielectric constant of starch was found to be 4.4 which decreased to 2.35 in Ag-starch nanocomposite film containing 0.50 wt% of Ag nanoparticles. Such nanocomposites with low dielectric constant have potential applications in microelectronic technologies.

SEMICONDUCTOR TECHNOLOGY: TaN wet etch for application in dual-metal-gate integration technology

NASA Astrophysics Data System (ADS)

Yongliang, Li; Qiuxia, Xu

2009-12-01

Wet-etch etchants and the TaN film method for dual-metal-gate integration are investigated. Both HF/HN O3/H2O and NH4OH/H2O2 solutions can etch TaN effectively, but poor selectivity to the gate dielectric for the HF/HNO3/H2O solution due to HF being included in HF/HNO3/H2O, and the fact that TaN is difficult to etch in the NH4OH/H2O2 solution at the first stage due to the thin TaOxNy layer on the TaN surface, mean that they are difficult to individually apply to dual-metal-gate integration. A two-step wet etching strategy using the HF/HNO3/H2O solution first and the NH4OH/H2O2 solution later can fully remove thin TaN film with a photo-resist mask and has high selectivity to the HfSiON dielectric film underneath. High-k dielectric film surfaces are smooth after wet etching of the TaN metal gate and MOSCAPs show well-behaved C-V and Jg-Vg characteristics, which all prove that the wet etching of TaN has little impact on electrical performance and can be applied to dual-metal-gate integration technology for removing the first TaN metal gate in the PMOS region.

Processing, electrical and microwave properties of sputtered Tl-Ca-Ba-Cu-O superconducting thin films

NASA Technical Reports Server (NTRS)

Subramanyam, G.; Kapoor, V. J.; Chorey, C. M.; Bhasin, K. B.

1993-01-01

A reproducible fabrication process has been established for TlCaBaCuO thin films on LaAlO3 substrates by RF magnetron sputtering and post-deposition processing methods. Electrical transport properties of the thin films were measured on patterned four-probe test devices. Microwave properties of the films were obtained from unloaded Q measurements of all-superconducting ring resonators. This paper describes the processing, electrical and microwave properties of Tl2Ca1Ba2Cu2O(x) 2122-plane phase thin films.

An Innovative Electrolysis Approach for the Synthesis of Metal Matrix Bulk Nanocomposites: A Case Study on Copper-Niobium System

NASA Astrophysics Data System (ADS)

Shokrvash, Hussein; Rad, Rahim Yazdani; Massoudi, Abouzar

2018-04-01

Design and synthesis of a prototype Cu-Nb nanocomposite are presented. Oxygen-free Cu-Nb nanocomposites were prepared using an electrolysis facility with special emphasis on the cathodic deoxidation of Cu and nanometric Nb2O5 blends in a molten NaCl-CaCl2 electrolyte. The as-prepared nanocomposites were characterized by X-ray diffraction and energy-dispersive X-ray spectroscopy. The elemental analysis of the Cu matrix and Nb phase revealed the high solubility of Nb in the Cu structure (0.85 at. pct) and Cu in the Nb structure (10.59 at. pct) over short synthesis times (4-5 hours). Furthermore, precise analysis using field emission scanning electron microscopy and transmission electron microscopy confirmed the unique structure and nanocomposite morphology of the Cu-Nb nanocomposite. The successful synthesis of Cu-Nb nanocomposites offers a new conceptual and empirical outlook on the generation of bulk nanostructures of immiscible bimetals using electro-synthesis.

Phase Competition Induced Bio-Electrochemical Resistance and Bio-Compatibility Effect in Nanocrystalline Zr x -Cu100-x Thin Films.

PubMed

Badhirappan, Geetha Priyadarshini; Nallasivam, Vignesh; Varadarajan, Madhuri; Leobeemrao, Vasantha Priya; Bose, Sivakumar; Venugopal, Elakkiya; Rajendran, Selvakumar; Angleo, Peter Chrysologue

2018-07-01

Nano-crystalline Zrx-Cu100-x (x = 20-100 at.%) thin films with thickness ranging from 50 to 185 nm were deposited by magnetron co-sputtering with individual Zr and Cu targets. The as-sputtered thin films were characterized by Field Emission Scanning Electron Microscope (FE-SEM), Atomic Force Microscopy (AFM) and Glancing Incidence X-ray Diffraction (GIXRD) for structural and morphological properties. The crystallite size was found to decrease from 57 nm to 37 nm upon increasing the Zr content from 20 to 30 at.% with slight increase in the lattice strain from 0.17 to 0.33%. Further, increase in Zr content to 40 at.% leads to increase in the crystallite size to 57 nm due to stabilization of C10Zr7 phase along with the presence of nanocrystalline Cu-Zr phase. A bimodal distribution of grain size was observed from FE-SEM micrograph was attributed to the highest surface roughness in Zr30Cu70 thin films comprised of Cu10Zr7, Cu9Zr2, Cu-Zr intermetallic phases. In-vitro electrochemical behaviors of nano-crystalline Zrx-Cu100-x thin films in simulated body fluid (SBF) were investigated using potentiodynamic polarization studies. Electrochemical impedance spectroscopy (EIS) data fitting by equivalent electrical circuit fit model suggests that inner bulk layer contributes to high bio-corrosion resistance in Zrx-Cu100-x thin films with increase in Zr content. The results of cyto-compatibility assay suggested that Zr-Cu thin film did not introduce cytotoxicity to osteoblast cells, indicating its suitability as a bio-coating for minimally invasive medical devices.

State Indoor Tanning Laws and Adolescent Indoor Tanning

PubMed Central

Guy, Gery P.; Berkowitz, Zahava; Jones, Sherry Everett; O’Malley Olsen, Emily; Miyamoto, Justin N.; Michael, Shannon L.; Saraiya, Mona

2014-01-01

Objectives. Recently, several state indoor tanning laws, including age restrictions, were promulgated to reduce indoor tanning among minors. We examined the effects of these laws on adolescent indoor tanning. Methods. We used nationally representative data from the 2009 and 2011 national Youth Risk Behavior Surveys (n = 31 835). Using multivariable logistic regression, we examined the association between state indoor tanning laws and indoor tanning among US high school students. Results. Female students in states with indoor tanning laws were less likely to engage in indoor tanning than those in states without any laws. We observed a stronger association among female students in states with systems access, parental permission, and age restriction laws than among those in states without any laws. We found no significant association among female students in states with only systems access and parental permission laws or among male students. Conclusions. Indoor tanning laws, particularly those including age restrictions, may be effective in reducing indoor tanning among female high school students, for whom rates are the highest. Such reductions have the potential to reduce the health and economic burden of skin cancer. PMID:24524515

Eradication of multi-drug resistant bacteria by a novel Zn-doped CuO nanocomposite.

PubMed

Malka, Eyal; Perelshtein, Ilana; Lipovsky, Anat; Shalom, Yakov; Naparstek, Livnat; Perkas, Nina; Patick, Tal; Lubart, Rachel; Nitzan, Yeshayahu; Banin, Ehud; Gedanken, Aharon

2013-12-09

Zinc-doped copper oxide nanoparticles are synthesized and simultaneously deposited on cotton fabric using ultrasound irradiation. The optimization of the processing conditions, the specific reagent ratio, and the precursor concentration results in the formation of uniform nanoparticles with an average size of ≈30 nm. The antibacterial activity of the Zn-doped CuO Cu₀.₈₈Zn₀.₁₂O in a colloidal suspension or deposited on the fabric is tested against Escherichia coli (Gram negative) and Staphylococcus aureus (Gram positive) bacteria. A substantial enhancement of 10,000 times in the antimicrobial activity of the Zn-CuO nanocomposite compared to the pure CuO and ZnO nanoparticles (NPs) is observed after 10 min exposure to the bacteria. Similar activities are observed against multidrug-resistant bacteria (MDR), (i.e., Methicillin-resistant S. aureus and MDR E. coli) further emphasizing the efficacy of this composite. Finally, the mechanism for this enhanced antibacterial activity is presented. Copyright © 2013 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Preparation and characterization of Cu2SnS3 thin films by electrodeposition

NASA Astrophysics Data System (ADS)

Patel, Biren; Narasimman, R.; Pati, Ranjan K.; Mukhopadhyay, Indrajit; Ray, Abhijit

2018-05-01

Cu2SnS3 thin films were electrodeposited on F:SnO2/Glass substrates at room temperature by using aqueous solution. Copper and tin were first electrodeposited from single bath and post annealed in the presence of sulphur atmosphere to obtain the Cu2SnS3 phase. The Cu2SnS3 phase with preferred orientation along the (112) crystal direction grows to greater extent by the post annealing of the film. Raman analysis confirms the monoclinic crystal structure of Cu2SnS3 with principle mode of vibration as A1 (symmetric breathing mode) corresponding to the band at 291 cm-1. It also reveals the benign coexistence of orthorhombic Cu3SnS4 and Cu2SnS7 phases. Optical properties of the film show direct band gap of 1.25 eV with a high absorption coefficient of the order of 104 cm-1 in the visible region. Photo activity of the electrodeposited film was established in two electrode photoelectro-chemical cell, where an open circuit voltage of 91.6 mV and a short circuit current density of 10.6 µA/cm2 were recorded. Fabrication of Cu2SnS3 thin film heterojunction solar cell is underway.

Friendly tanning: young adults' engagement with friends around indoor tanning.

PubMed

Rodríguez, Vivian M; Daniel, Casey L; Welles, Brooke Foucault; Geller, Alan C; Hay, Jennifer L

2017-08-01

Indoor tanning (IT), particularly during early adulthood, increases risk for melanoma and is exceedingly common among youth. Social influence, including social norms, promotes IT but little is known about young adults' engagement with friends around tanning. We examined IT behaviors and tanning-related communication with friends at three universities. Of 837 participants, 261 (31%) reported ever tanning (90% female, 85% White). Of those, 113 (43%) were former tanners and 148 (57%) current tanners. Current tanners reported more social tanning and discussions with friends about tanning, more frequent outdoor tanning, high propensity to tan, and greater lifetime IT exposure than former tanners. Risks-to-benefits discussion ratios were greater for former tanners. In adjusted analyses, current tanners were more likely to make plans to tan and to talk about tanning benefits with friends. Findings confirm IT is a social experience. Future work should examine social tanning's role in the promotion and reduction of IT among youth.

Spatial and temporal distribution of Mesozoic adakitic rocks along the Tan-Lu fault, Eastern China: Constraints on the initiation of lithospheric thinning

NASA Astrophysics Data System (ADS)

Gu, Hai-Ou; Xiao, Yilin; Santosh, M.; Li, Wang-Ye; Yang, Xiaoyong; Pack, Andreas; Hou, Zhenhui

2013-09-01

The Mesozoic tectonics in East China is characterized by significant lithospheric thinning of the North China Craton, large-scale strike-slip movement along the Tan-Lu fault, and regional magmatism with associated metallogeny. Here we address the possible connections between these three events through a systematic investigation of the geochemistry, zircon geochronology and whole rock oxygen isotopes of the Mesozoic magmatic rocks distributed along the Tan-Lu fault in the Shandong province. The characteristic spatial and temporal distributions of high-Mg adakitic rocks along the Tan-Lu fault with emplacement ages of 134-128 Ma suggest a strong structural control for the emplacement of these intrusions, with magma generation possibly associated with the subduction of the Pacific plate in the early Cretaceous. The low-Mg adakitic rocks (127-120 Ma) in the Su-Lu orogenic belt were formed later than the high-Mg adakitic rocks, whereas in the Dabie orogenic belt, most of the low-Mg adakitic rocks (143-129 Ma) were generated earlier than the high-Mg adakitic rocks. Based on available data, we suggest that the large scale strike-slip tectonics of the Tan-Lu fault in the Mesozoic initiated cratonic destruction at the south-eastern margin of the North China Craton, significantly affecting the lower continental crust within areas near the fault. This process resulted in crustal fragments sinking into the asthenosphere and reacting with peridotites, which increased the Mg# of the adakitic melts, generating the high-Mg adakitic rocks. The gravitationally unstable lower continental crust below the Tan-Lu fault in the Su-Lu orogenic belt triggered larger volume delamination of the lower continental crust or foundering of the root.

A novel highly selective and sensitive detection of serotonin based on Ag/polypyrrole/Cu2O nanocomposite modified glassy carbon electrode.

PubMed

Selvarajan, S; Suganthi, A; Rajarajan, M

2018-06-01

A silver/polypyrrole/copper oxide (Ag/PPy/Cu 2 O) ternary nanocomposite was prepared by sonochemical and oxidative polymerization simple way, in which Cu 2 O was decorated with Ag nanoparticles, and covered by polyprrole (PPy) layer. The as prepared materials was characterized by UV-vis-spectroscopy (UV-vis), FT-IR, X-ray diffraction (XRD), thermo-gravimetric analysis (TGA), scanning electron microscopy (SEM) with EDX, high resolution transmission electron microscopy (HR-TEM) and X-ray photoelectron spectroscopy (XPS). Sensing of serotonin (5HT) was evaluated electrocatalyst using polypyrrole/glassy carbon electrode (PPy/GCE), polypyrrole/copper oxide/glassy carbon electrode (PPy/Cu 2 O/GCE) and silver/polypyrrole/copper oxide/glassy carbon electrode (Ag/PPy/Cu 2 O/GCE). The Ag/PPy/Cu 2 O/GCE was electrochemically treated in 0.1MPBS solution through cyclic voltammetry (CV) and differential pulse voltammetry (DPV). The peak current response increases linearly with 5-HT concentration from 0.01 to 250 µmol L -1 and the detection limit was found to be 0.0124 μmol L -1 . It exhibits high electrocatalytic activity, satisfactory repeatability, stability, fast response and good selectivity against potentially interfering species, which suggests its potential in the development of sensitive, selective, easy-operation and low-cost serotonin sensor for practical routine analyses. The proposed method is potential to expand the possible applied range of the nanocomposite material for detection of various concerned electro active substances. Copyright © 2018 Elsevier B.V. All rights reserved.

Indoor Tanning

MedlinePlus

... proof that indoor tanning is safer than tanning outdoors. Indoor tanning systems give concentrated UV exposure regardless ... For example, it’s essential for promoting good bone health. While UV ... a tan to get that benefit. According to the Surgeon General, fair and light- ...

Epitaxial thin films of Dirac semimetal antiperovskite Cu3PdN

NASA Astrophysics Data System (ADS)

Quintela, C. X.; Campbell, N.; Shao, D. F.; Irwin, J.; Harris, D. T.; Xie, L.; Anderson, T. J.; Reiser, N.; Pan, X. Q.; Tsymbal, E. Y.; Rzchowski, M. S.; Eom, C. B.

2017-09-01

The growth and study of materials showing novel topological states of matter is one of the frontiers in condensed matter physics. Among this class of materials, the nitride antiperovskite Cu3PdN has been proposed as a new three-dimensional Dirac semimetal. However, the experimental realization of Cu3PdN and the consequent study of its electronic properties have been hindered due to the difficulty of synthesizing this material. In this study, we report fabrication and both structural and transport characterization of epitaxial Cu3PdN thin films grown on (001)-oriented SrTiO3 substrates by reactive magnetron sputtering and post-annealed in NH3 atmosphere. The structural properties of the films, investigated by x-ray diffraction and scanning transmission electron microscopy, establish single phase Cu3PdN exhibiting cube-on-cube epitaxy (001)[100]Cu3PdN||(001)[100]SrTiO3. Electrical transport measurements of as-grown samples show metallic conduction with a small temperature coefficient of the resistivity of 1.5 × 10-4 K-1 and a positive Hall coefficient. Post-annealing in NH3 results in the reduction of the electrical resistivity accompanied by the Hall coefficient sign reversal. Using a combination of chemical composition analyses and ab initio band structure calculations, we discuss the interplay between nitrogen stoichiometry and magneto-transport results in the framework of the electronic band structure of Cu3PdN. Our successful growth of thin films of antiperovskite Cu3PdN opens the path to further investigate its physical properties and their dependence on dimensionality, strain engineering, and doping.

Contextual Factors, Indoor Tanning, and Tanning Dependence in Young Women

PubMed Central

Heckman, Carolyn J.; Darlow, Susan D.; Kloss, Jacqueline D.; Munshi, Teja; Manne, Sharon L.

2015-01-01

Objectives The study's purpose was to investigate the association of contextual factors such as cost, tanning accessibility, regulations, or marketing and indoor tanning or tanning dependence. Methods One hundred thirty-nine college-aged female indoor tanners completed a questionnaire between 2009 and 2011. Results Higher scores on tanning dependence and assessment in the spring/summer (versus the fall/winter) were associated with more frequent indoor tanning in the last 30 days (ps < .05). More frequent indoor tanning, greater session length, and more trouble paying for tanning were associated with higher scores on tanning dependence (ps < .05). Conclusions Public health research and practice could benefit from attention to such contextual factors as tanning cost and regulations regarding session length. PMID:25741682

Facile fabrication of Cu(II)-porphyrin MOF thin films from tetrakis(4-carboxyphenyl)porphyrin and Cu(OH)2 nanoneedle array

NASA Astrophysics Data System (ADS)

La, Duong Duc; Thi, Hoai Phuong Nguyen; Kim, Yong Shin; Rananaware, Anushri; Bhosale, Sheshanath V.

2017-12-01

Herein, we report a facile synthetic protocol to grow thin films of Cu(II) tetrakis(4-carboxyphenyl)porphyrin (CuTCPP) metal-organic frameworks (MOF) from a tetrakis(4-carboxyphenyl)porphyrin (H2TCPP) solution and the copper hydroxide (Cu(OH)2) nanoneedle array formed on a Cu substrate at room temperature. The formations of Cu-centered TCPP ligands and crystalline platelet-like Cu MOFs were successfully probed by SEM, XRD, FTIR, UV-vis and XPS. The formation process from Cu(OH)2 was monitored by using SEM images obtained at different reaction times during the first 24 h, thus suggesting the reaction pathway of Cu(OH)2 dissolution followed by the reprecipitation of CuTCPP MOFs at a near surface. In addition, the CuTCPP MOFs exhibited a high specific surface area of 408 m2/g.

Improved tribological properties of the synthesized copper/carbon nanotube nanocomposites for rapeseed oil-based additives

NASA Astrophysics Data System (ADS)

Wang, Zhiqiang; Ren, Ruirui; Song, Haojie; Jia, Xiaohua

2018-01-01

Carbon nanotubes (CNTs) decorated with uniform copper nanoparticles (Cu NPs) were successfully prepared via a facile approach towards surface modification of CNTs with spontaneous polydopamine (PDA). The structures and morphologies of the nanocomposites were investigated by different kinds of techniques, including X-ray diffraction (XRD), transmission electron microscopy (TEM), and X-ray photoelectron spectroscopy (XPS). Cu/PDA/CNTs nanocomposites were fabricated by growing the Cu NPs with an average diameter of 5 nm on the surfaces of PDA-modified CNTs. The CNTs functionalized with PDA layer not only provide an anchoring platform for the Cu NPs immobilization, but also endow Cu/PDA/CNTs with good dispersion stability when Cu/PDA/CNTs nanocomposites were used as lubricant additive. The tribological performance of the nanocomposites as the rapeseed oil lubricant additive, as well as Cu NPs, CNTs, and Cu/CNTs, was also investigated using a MS-T3000 ball-on-disk tribometer. Results show that the 0.2 wt% Cu/PDA/CNTs nanoadditive simultaneously reduce the friction and wear by 33.5% and 23.7%, respectively, outperformed the tribological performance of Cu NPs, CNTs, and Cu/CNTs nanoadditives. In addition, the presence of active sites in Cu/PDA/CNTs was beneficial to reduce the time of running-in period, give rise to the fastest speed to be stable of the friction coefficient curve as compared to the other nanoadditives. X-ray photoelectron spectroscopy (XPS) and Raman spectroscopy of the worn surfaces lubricated by the soybean oil with Cu/PDA/CNTs nanocomposites showed that formation of low shear strength tribofilms containing Cu/PDA/CNTs nanocomposites and its self-lubricating property was key factor in reduction of the friction and protection against wear and deformation.

Nanocomposite synthesis and photoluminescence properties of MeV Au-ion beam modified Ni thin films

NASA Astrophysics Data System (ADS)

Siva, Vantari; Datta, Debi P.; Singh, Avanendra; Som, T.; Sahoo, Pratap K.

2016-01-01

We report on the synthesis and properties of nano-composites from thin Ni films on Silica matrix using Au-ion beam. When 2.2 MeV Au-ions are irradiated on 5 nm Ni film on Silica, the surface morphology changes drastically with ion fluence. In fact, within a fluence range of 5 × 1014-1 × 1016 ions/cm2, a sharp increase in surface roughness follows after an initial surface smoothening. The depth profiles extracted from Rutherford backscattering spectra demonstrates the diffusion of Ni and Au into the silica matrix. The photoluminescence spectra of the irradiated samples reveal the development of two bands centered at 3.3 eV and 2.66 eV, respectively. Deconvolution of those bands shows five different emission peaks, corresponding to different luminescence centers, which confirms the existence of Ni-Au nanocomposites in silica matrix. The optical and structural modifications are understood in terms of ion induced local heating and mass transport due to thermal spikes, which leads to nanocomposite formation in silica.

Effect of Annealing Temperature on Flowerlike Cu3BiS3 Thin Films Grown by Chemical Bath Deposition

NASA Astrophysics Data System (ADS)

Deshmukh, S. G.; Patel, S. J.; Patel, K. K.; Panchal, A. K.; Kheraj, Vipul

2017-10-01

For widespread application of thin-film photovoltaic solar cells, synthesis of inexpensive absorber material is essential. In this work, deposition of ternary Cu3BiS3 absorber material, which contains abundant and environmentally benign elements, was carried out on glass substrate. Flowerlike Cu3BiS3 thin films with nanoflakes as building block were formed on glass substrate by chemical bath deposition. These films were annealed at 573 K and 673 K in sulfur ambient for structural improvement. Their structure was characterized using Raman spectroscopy, as well as their surface morphological and optical properties. The x-ray diffraction profile of as-deposited Cu3BiS3 thin film revealed amorphous structure, which transformed to orthorhombic phase after annealing. The Raman spectrum exhibited a characteristic peak at 290 cm-1. Scanning electron microscopy of as-deposited Cu3BiS3 film confirmed formation of nanoflowers with diameter of around 1052 nm. Wettability testing of as-deposited Cu3BiS3 thin film demonstrated hydrophobic nature, which became hydrophilic after annealing. The measured ultraviolet-visible (UV-Vis) absorption spectra of the Cu3BiS3 thin films gave an absorption coefficient of 105 cm-1 and direct optical bandgap of about 1.42 eV after annealing treatment. Based on all these results, such Cu3BiS3 material may have potential applications in the photovoltaic field as an absorber layer.

Thin Cu film resistivity using four probe techniques: Effect of film thickness and geometrical shapes

NASA Astrophysics Data System (ADS)

Choudhary, Sumita; Narula, Rahul; Gangopadhyay, Subhashis

2018-05-01

Precise measurement of electrical sheet resistance and resistivity of metallic thin Cu films may play a significant role in temperature sensing by means of resistivity changes which can further act as a safety measure of various electronic devices during their operation. Four point probes resistivity measurement is a useful approach as it successfully excludes the contact resistance between the probes and film surface of the sample. Although, the resistivity of bulk samples at a particular temperature mostly depends on its materialistic property, however, it may significantly differ in the case of thin films, where the shape and thickness of the sample can significantly influence on it. Depending on the ratio of the film thickness to probe spacing, samples are usually classified in two segments such as (i) thick films or (ii) thin films. Accordingly, the geometric correction factors G can be related to the sample resistivity r, which has been calculated here for thin Cu films of thickness up to few 100 nm. In this study, various rectangular shapes of thin Cu films have been used to determine the shape induced geometric correction factors G. An expressions for G have been obtained as a function of film thickness t versus the probe spacing s. Using these expressions, the correction factors have been plotted separately for each cases as a function of (a) film thickness for fixed linear probe spacing and (b) probe distance from the edge of the film surface for particular thickness. Finally, we compare the experimental results of thin Cu films of various rectangular geometries with the theoretical reported results.

Colossal dielectric and electromechanical responses in self-assembled polymeric nanocomposites

NASA Astrophysics Data System (ADS)

Huang, Cheng; Zhang, Q. M.; Li, Jiang Yu; Rabeony, Manese

2005-10-01

An electroactive polymer nanocomposite, in which high dielectric constant copper phthalocyanine oligomer (o-CuPc) nanoparticles are incorporated into the block polyurethane (PU) matrix by the combination of "top down" and "bottom up" approaches, was realized. Such an approach enables the nanocomposite to exhibit colossal dielectric and electromechanical responses with very low volume fraction of the high dielectric constant o-CuPc nanofillers (˜3.5%) in the composite. In contrast, a simple blend of o-CuPc and PU composite with much higher o-CuPc content (˜16% of o-CuPc) shows much lower dielectric and electromechanical responses.

Microstructural and electrical properties of Al/n-type Si Schottky diodes with Au-CuPc nanocomposite films as interlayer

NASA Astrophysics Data System (ADS)

Reddy, P. R. Sekhar; Janardhanam, V.; Jyothi, I.; Chang, Han-Soo; Lee, Sung-Nam; Lee, Myung Sun; Reddy, V. Rajagopal; Choi, Chel-Jong

2017-11-01

Au-CuPc nanocomposite films were prepared by simultaneous evaporation of Au and CuPc with various Au and CuPc concentrations. Microstructural analysis of Au-CuPc films revealed elongated Au cluster formation from isolated Au nanoclusters with increasing Au concentration associated with coalescence of Au clusters. Au-CuPc films with different compositions were employed as interlayer in Al/n-Si Schottky diode. Barrier height and series resistance of the Al/n-Si Schottky diode with Au-CuPc interlayer decreased with increasing Au concentration. This could be associated with the enhancement of electron tunneling between neighboring clusters due to decrease in spacing of Au clusters and formation of conducting paths through the composite material. Interface state density of the Al/n-Si Schottky diode with Au-CuPc interlayer increased with increasing Au concentration. This might be because the inclusion of metal decreases the crystallinity and crystal size of the polymer matrix accompanied by the formation of local defect sites at the places of metal nucleation.

Laser Deposition of Polymer Nanocomposite Thin Films and Hard Materials and Their Optical Characterization

DTIC Science & Technology

2013-12-05

visible light on instruments such as microscope tips and micro- surgical tools. Hard carbon known as diamond-like carbon films produced by pulsed laser ...visible (610 nm) LED source and a supplemental infra-red 980-nm laser diode (for the studies of the upconversion fluorescence). The basic package...5/2013 Final Performance Report 15 Sep 2012- 14 Sep 2013 LASER DEPOSITION OF POLYMER NANOCOMPOSITE THIN FILMS AND HARD MATERIALS AND THEIR OPTICAL

Structural and magnetic analysis of Cu, Co substituted NiFe2O4 thin films

NASA Astrophysics Data System (ADS)

Sharma, Hakikat; Bala, Kanchan; Negi, N. S.

2016-05-01

In the present work we prepared NiFe2O4, Ni0.95Cu0.05Fe2O4 and Ni0.94Cu0.05Co0.01 Fe2O4 thin films by metallo-organic decomposition method (MOD) using spin coating technique. The thin films were analyzed by X-ray diffractometer (XRD) and Atomic force microscope (AFM) for structural studies. The XRD patterns confirmed the ferrite phase of thin films. From AFM, we analyzed surface morphology, calculated grain size (GS) and root mean square roughness (RMSR). Room temperature magnetic properties were investigated by vibrating sample magnetometer (VSM).

The Influence of channel length to the characteristics of CuPc based OFET thin films

NASA Astrophysics Data System (ADS)

Sujarwata; Handayani, L.; Mosik; Fianti

2018-03-01

The main focus of this research is to characterize organic field effect transistor (OFET) thin films based on CuPc with a bottom-contact structure and varied channel length. OFET was prepared by Si substrate cleaning in the ultrasonic cleaner first, then deposition of the source and drain electrodes on the substrate with vacuum evaporation at room temperature, and finally CuPc thin film deposition among the source, drain, and gate electrodes. The distance between source anddrain electrodes is the channel length of the CuPc thin film. In this research, the channel length was varied; 100 μm, 200 μm and 300 μm, with the same active areas of 2.9-3.42 V and different current, IDS. The result showed that the shorter channel length causes, the bigger IDS flowing on the OFET

Synthesis of three-dimensional mesoporous Cu-Al layered double hydroxide/g-C3N4 nanocomposites on Ni-foam for enhanced supercapacitors with excellent long-term cycling stability.

PubMed

Adhikari, Surya Prasad; Awasthi, Ganesh Prasad; Kim, Kyung-Suk; Park, Chan Hee; Kim, Cheol Sang

2018-03-26

In this study, a novel composite of Cu-Al layered double hydroxide (LDH) nanosheets and g-C3N4-covered Ni-foam was fabricated via a simple and facile two-step process. First, g-C3N4 sheets were deposited on Ni-foam by via electrodeposition method on a three-electrode system (Ni-foam@g-C3N4) and then, Cu-Al LDH nanosheets were grown on the Ni-foam via in situ redox reaction using a hydrothermal process (Ni-foam@Cu-Al LDH/g-C3N4). The FE-SEM image confirmed that the Cu-Al LDH nanosheets arose vertically and were anchored on the surface of electrodeposited g-C3N4 sheets, thus generating unique 3D porous interconnected networks. The electrochemical capacitive performances of the as-prepared samples were evaluated by cyclic volatammetry (CV), galvanostatic charge/discharge tests, and electrochemical impedance spectra (EIS) Nyquist plots. The specific capacitances of the Ni-foam@Cu-Al LDH/g-C3N4 nanocomposite measured from the CV curve (770.98 F g-1 at 50 mV s-1) and the galvanostatic charge/discharge curve (831.871 at 0.4 A g-1) were significantly higher than the others. Moreover, the Ni-foam@Cu-Al LDH/g-C3N4 nanocomposite revealed a remarkable high-current capacitive behavior and the capacitance retention could be maintained at 92.71% even after 5000 cycles of CV. Thus, the obtained results demonstrated that the as-prepared nanocomposite has great potential to be used as a novel supercapacitor electrode.

Chemical bath deposited and dip coating deposited CuS thin films - Structure, Raman spectroscopy and surface study

NASA Astrophysics Data System (ADS)

Tailor, Jiten P.; Khimani, Ankurkumar J.; Chaki, Sunil H.

2018-05-01

The crystal structure, Raman spectroscopy and surface microtopography study on as-deposited CuS thin films were carried out. Thin films deposited by two techniques of solution growth were studied. The thin films used in the present study were deposited by chemical bath deposition (CBD) and dip coating deposition techniques. The X-ray diffraction (XRD) analysis of both the as-deposited thin films showed that both the films possess covellite phase of CuS and hexagonal unit cell structure. The determined lattice parameters of both the films are in agreement with the standard JCPDS as well as reported data. The crystallite size determined by Scherrer's equation and Hall-Williamsons relation using XRD data for both the as-deposited thin films showed that the respective values were in agreement with each other. The ambient Raman spectroscopy of both the as-deposited thin films showed major emission peaks at 474 cm-1 and a minor emmision peaks at 265 cm-1. The observed Raman peaks matched with the covellite phase of CuS. The atomic force microscopy of both the as-deposited thin films surfaces showed dip coating thin film to be less rough compared to CBD deposited thin film. All the obtained results are presented and deliberated in details.

Pulsed Laser Deposition Growth of Delafossite (CuFeO2) thin films and multilayers

NASA Astrophysics Data System (ADS)

Joshi, Toyanath; Ferrari, Piero; Borisov, Pavel; Cabrera, Alejandro; Lederman, David

2014-03-01

Owing to its narrow band gap (<2 eV) and p-type conductivity delafossite CuFeO2 is attractive for applications in the field of solar energy conversion. Obtaining pure phase CuFeO2 thin films, however, is relatively difficult. It is necessary to maintain the lowest possible Cu valency (+1) in order to avoid forming the comparably stable spinel compound CuFe2O4. We present a systematic study of the pulsed laser deposition (PLD) growth conditions for epitaxial (00.1) oriented CuFeO2 thin films on Al2O3 (00.1) substrates. The secondary impurity phase, CuFe2O4, was removed completely by optimizing the growth conditions. RHEED, XRD and TEM showed that the pure phase delafossite films are highly epitaxial to the substrate. The chemical purity was verified by Raman and XPS. The indirect bandgap of 1.15 eV was measured using infrared reflectivity, and is in agreement with the CuFeO2 bulk value. Finally, we discuss the growth and structural characterization of delafossite multilayers, CuFeO2/CuGaO2. This work was supported by a Research Challenge Grant from the West Virginia Higher Education Policy Commission (HEPC.dsr.12.29) and the Microelectronics Advanced Research Corporation (Contract # 2013-MA-2382) at WVU.

Recrystallization method to selenization of thin-film Cu(In,Ga)Se.sub.2 for semiconductor device applications

DOEpatents

Albin, David S.; Carapella, Jeffrey J.; Tuttle, John R.; Contreras, Miguel A.; Gabor, Andrew M.; Noufi, Rommel; Tennant, Andrew L.

1995-07-25

A process for fabricating slightly Cu-poor thin-films of Cu(In,Ga)Se.sub.2 on a substrate for semiconductor device applications includes the steps of forming initially a slightly Cu-rich, phase separated, mixture of Cu(In,Ga)Se.sub.2 :Cu.sub.x Se on the substrate in solid form followed by exposure of the Cu(In,Ga)Se.sub.2 :Cu.sub.x Se solid mixture to an overpressure of Se vapor and (In,Ga) vapor for deposition on the Cu(In,Ga)Se.sub.2 :Cu.sub.x Se solid mixture while simultaneously increasing the temperature of the solid mixture toward a recrystallization temperature (about 550.degree. C.) at which Cu(In,Ga)Se.sub.2 is solid and Cu.sub.x Se is liquid. The (In,Ga) flux is terminated while the Se overpressure flux and the recrystallization temperature are maintained to recrystallize the Cu.sub.x Se with the (In, Ga) that was deposited during the temperature transition and with the Se vapor to form the thin-film of slightly Cu-poor Cu.sub.x (In,Ga).sub.y Se.sub.z. The initial Cu-rich, phase separated large grain mixture of Cu(In,Ga)Se.sub.2 :Cu.sub.x Se can be made by sequentially depositing or co-depositing the metal precursors, Cu and (In, Ga), on the substrate at room temperature, ramping up the thin-film temperature in the presence of Se overpressure to a moderate anneal temperature (about 450.degree. C.) and holding that temperature and the Se overpressure for an annealing period. A nonselenizing, low temperature anneal at about 100.degree. C. can also be used to homogenize the precursors on the substrates before the selenizing, moderate temperature anneal.

Synthesis and optical characterization of ternary chalcogenide Cu3BiS3 thin film by spin coating

NASA Astrophysics Data System (ADS)

Rawal, Neha; Hadi, Mohammed Kamal; Modi, B. P.

2017-05-01

In this work, ternary Chalcogenide Cu3BiS3(CBS) thin films have been prepared and modified by using spin coating technique. Lucratively, spin coating technique is easy going and simple though it hasn't given an enclosure and extensive focus of researches for Cu3BiS3 thin films formation. The surface smoothness and the homogeneity of the obtained thin films have been optimized throughout varying the annealing temperature, concentration and rotation speed. It had been found that as prepared films the value of the energy band gap is 1.4 eV, the absorption coefficient 105 cm-1. Each values of the EBG (Energy Band Gap) and AC (Absorption coefficient) was found in quite agreement with the published work of CBS thin film formation by other methods as CBD, dip coating etc. It signifies that Cu3BiS3 films can be used as an absorber layer for thin film solar cell.

Atomic and electronic structures of BaHfO3-doped TFA-MOD-derived YBa2Cu3O7-δ thin films

NASA Astrophysics Data System (ADS)

Molina-Luna, Leopoldo; Duerrschnabel, Michael; Turner, Stuart; Erbe, Manuela; Martinez, Gerardo T.; Van Aert, Sandra; Holzapfel, Bernhard; Van Tendeloo, Gustaaf

2015-11-01

Tailoring the properties of oxide-based nanocomposites is of great importance for a wide range of materials relevant for energy technology. YBa2Cu3O7-δ (YBCO) superconducting thin films containing nanosized BaHfO3 (BHO) particles yield a significant improvement of the magnetic flux pinning properties and a reduced anisotropy of the critical current density. These films were prepared by chemical solution deposition (CSD) on (100) SrTiO3 (STO) substrates yielding critical current densities up to 3.6 MA cm-2 at 77 K and self-field. Transport in-field J c measurements demonstrated a high pinning force maximum of around 6 GN/m3 for a sample annealed at T = 760 °C that has a doping of 12 mol% of BHO. This sample was investigated by scanning transmission electron microscopy (STEM) in combination with electron energy-loss spectroscopy (EELS) yielding strain and spectral maps. Spherical BHO nanoparticles of 15 nm in size were found in the matrix, whereas the particles at the interface were flat. A 2 nm diffusion layer containing Ti was found at the YBCO (BHO)/STO interface. Local lattice deformation mapping at the atomic scale revealed crystal defects induced by the presence of both sorts of BHO nanoparticles, which can act as pinning centers for magnetic flux lines. Two types of local lattice defects were identified and imaged: (i) misfit edge dislocations and (ii) Ba-Cu-Cu-Ba stacking faults (Y-248 intergrowths). The local electronic structure and charge transfer were probed by high energy resolution monochromated electron energy-loss spectroscopy. This technique made it possible to distinguish superconducting from non-superconducting areas in nanocomposite samples with atomic resolution in real space, allowing the identification of local pinning sites on the order of the coherence length of YBCO (˜1.5 nm) and the determination of 0.25 nm dislocation cores.

Phase and electrical properties of PZT thin films embedded with CuO nano-particles by a hybrid sol-gel route

NASA Astrophysics Data System (ADS)

Sreesattabud, Tharathip; Gibbons, Brady J.; Watcharapasorn, Anucha; Jiansirisomboon, Sukanda

2013-07-01

Pb(Zr0.52Ti0.48)O3 or PZT thin films embedded with CuO nano-particles were successfully prepared by a hybrid sol-gel process. In this process, CuO (0, 0.1, 0.2, 0.3, 0.4, 0.5 and 1 wt. %) nanopowder was suspended in an organometallic solution of PZT, and then coated on platinised silicon substrate using a spin-coating technique. The influence of CuO nano-particles' dispersion on the phase of PZT thin films was investigated. XRD results showed a perovskite phase in all films. At the CuO concentration of 0.4-1 wt. %, a second phase was observed. The addition of CuO nano-particles affected the orientation of PZT thin films. The addition was also found to reduce the ferroelectric properties of PZT thin films. However, at 0.2 wt. % CuO concentration, the film exhibited good ferroelectric properties similar to those of PZT films. In addition, the fatigue retention properties of the PZT/CuO system was observed, and it showed 14% fatigue at 108 switching bipolar pulse cycles while the fatigue in PZT thin films was found to be 17% at the same switching bipolar pulse cycles.

Electrochemical detection of nitrite on poly(pyronin Y)/graphene nanocomposites modified ITO substrate

NASA Astrophysics Data System (ADS)

Şinoforoğlu, Mehmet; Dağcı, Kader; Alanyalıoğlu, Murat; Meral, Kadem

2016-06-01

The present study reports on an easy preparation of poly(pyronin Y)/graphene (poly(PyY)/graphene) nanocomposites thin films on indium tin oxide coated glass substrates (ITO). The thin films of poly(PyY)/graphene nanocomposites are prepared by a novel method consisting of three steps; (i) preparation of graphene oxide (GO) thin films on ITO by spin-coating method, (ii) self-assembly of PyY molecules from aqueous solution onto the GO thin film, (iii) surface-confined electropolymerization (SCEP) of the adsorbed PyY molecules on the GO thin film. The as-prepared poly(PyY)/graphene nanocomposites thin films are characterized by using electroanalytical and spectroscopic techniques. Afterwards, the graphene-based polymeric dye thin film on ITO is used as an electrode in an electrochemical cell. Its performance is tested for electrochemical detection of nitrite. Under optimized conditions, the electrocatalytical effect of the nanocomposites thin film through electrochemical oxidation of nitrite is better than that of GO coated ITO.

Tuning Bandgap of p-Type Cu2Zn(Sn, Ge)(S, Se)4 Semiconductor Thin Films via Aqueous Polymer-Assisted Deposition.

PubMed

Yi, Qinghua; Wu, Jiang; Zhao, Jie; Wang, Hao; Hu, Jiapeng; Dai, Xiao; Zou, Guifu

2017-01-18

Bandgap engineering of kesterite Cu 2 Zn(Sn, Ge)(S, Se) 4 with well-controlled stoichiometric composition plays a critical role in sustainable inorganic photovoltaics. Herein, a cost-effective and reproducible aqueous solution-based polymer-assisted deposition approach is developed to grow p-type Cu 2 Zn(Sn, Ge)(S, Se) 4 thin films with tunable bandgap. The bandgap of Cu 2 Zn(Sn, Ge)(S, Se) 4 thin films can be tuned within the range 1.05-1.95 eV using the aqueous polymer-assisted deposition by accurately controlling the elemental compositions. One of the as-grown Cu 2 Zn(Sn, Ge)(S, Se) 4 thin films exhibits a hall coefficient of +137 cm 3 /C. The resistivity, concentration and carrier mobility of the Cu 2 ZnSn(S, Se) 4 thin film are 3.17 ohm·cm, 4.5 × 10 16 cm -3 , and 43 cm 2 /(V·S) at room temperature, respectively. Moreover, the Cu 2 ZnSn(S, Se) 4 thin film when used as an active layer in a solar cell leads to a power conversion efficiency of 3.55%. The facile growth of Cu 2 Zn(Sn, Ge)(S, Se) 4 thin films in an aqueous system, instead of organic solvents, provides great promise as an environmental-friendly platform to fabricate a variety of single/multi metal chalcogenides for the thin film industry and solution-processed photovoltaic devices.

Thermal stability of active/inactive nanocomposite anodes based on Cu2Sb in lithium-ion batteries

NASA Astrophysics Data System (ADS)

Allcorn, Eric; Kim, Sang-Ok; Manthiram, Arumugam

2015-12-01

Various active/inactive nanocomposites of Cu2Sb-Al2O3@C, Cu2Sb-TiC, and Cu2Sb-TiC@C have been synthesized by high energy mechanical milling and investigated by differential scanning calorimetry (DSC) to determine the lithiated phase stability and heat generation arising from these electrodes. The milling process reduces the Li3Sb phase stability, relative to the un-milled samples, to below ∼200 °C. However, the incorporation of the reinforcing, inactive phases Al2O3, TiC, and carbon black offer a slight improvement. DSC curves also show that the low-temperature heat generation in the SEI-layer reaction range is not noticeably altered by either the milling process or the addition of the inactive phases. A strong exothermic peak is observed at ∼200 °C for the 0% state of charge electrodes of Cu2Sb-Al2O3@C and Cu2Sb-TiC@C that was caused by the incorporation of carbon black into the composite. This peak was not present in the electrodes of milled Cu2Sb or Cu2Sb-TiC, suggesting that efforts to extend the cycle life of alloy anodes should avoid carbon black due to its destabilizing effects on delithiated electrodes. Fourier Transform infrared spectroscopy analysis indicates that the reaction arising from the incorporation of carbon black is tied to a low-temperature breakdown of the lithium salt LiPF6.

Effect of deposition time of sputtering Ag-Cu thin film on mechanical and antimicrobial properties

NASA Astrophysics Data System (ADS)

Purniawan, A.; Hermastuti, R.; Purwaningsih, H.; Atmono, T. M.

2018-04-01

Metallic implants are important components in biomedical treatment. However, post-surgery infection often occurs after installation of implant. The infections are usually treated by antibiotics, but it still causes several secondary problems. As a prevention treatment, the surgical instruments and implants must be in a sterile condition. This action is still not optimal too because the material still can attract the bacteria. From material science point of view, it can be anticipated by developing a type of material which has antibacterial properties or called antimicrobial material. Silver (Ag) and Copper (Cu) have antimicrobial properties to prevent the infection. In this research, the influence of deposition time of Ag-Cu thin film deposition process as antimicrobial material with Physical Vapor Deposition (PVD) RF Sputtering method was analyzed. Deposition time used were for 10, 15 and 20 minutes in Argon gas pressure around 3 x 10-2 mbar in during deposition process. The morphology and surface roughness of Ag-Cu thin film were characterized using SEM and AFM. Based on the results, the deposition time influences the quality morphology that the thin films have good homogeneity and complete structure for longer deposition time. In addition, from roughness measurement results show that increase deposition time decrease the roughness of thin film. Antimicrobial performance was analyzed using Kirby Bauer Test. The results show that all of sample have good antimicrobial inhibition. Adhesion quality was evaluated using Rockwell C Indentation Test. However, the results indicate that the Ag-Cu thin film has low adhesion strength.

Fabrication of Cu2SnS3 thin films by ethanol-ammonium solution process by doctor-blade technique

NASA Astrophysics Data System (ADS)

Wang, Yaguang; Li, Jianmin; Xue, Cong; Zhang, Yan; Jiang, Guoshun; Liu, Weifeng; Zhu, Changfei

2017-11-01

In the present study, a low-cost and simple method is applied to fabricate Cu2SnS3 (CTS) thin films. Namely CTS thin films are prepared by a doctor-blade method with a slurry dissolving the Cu2O and SnS powders obtained from CBD reaction solution into ethanol-ammonium solvents. Series of characterization methods including XRD, Raman spectra, SEM and UV-Vis analyses are introduced to investigate the phase structure, morphology and optical properties of CTS thin films. As a result, monoclinic CTS films have been obtained with the disappearance of binary phases CuS and SnS2 while increasing the annealing temperature and time, high quality monoclinic CTS thin films consisting of compact and large grains have been successfully prepared by this ethanol-ammonium method. Moreover, the secondary phase Cu2Sn3S7 is also observed during the annealing process. In addition, the post-annealed CTS film with a band-gap about 0.89 eV shows excellent absorbance between 400 and 1200 nm, which is proper for the bottom layer in multi-junction thin film solar cells.[Figure not available: see fulltext.

Ultrasonochemically conjugated metalloid/triblock copolymer nanocomposite and subsequent thin solid laminate growth for surface and interface studies.

PubMed

Veerapandian, Murugan; Yun, KyuSik

2010-09-07

Polymer and metalloid nanoparticles can be conjugated in a symphonized manner using ultrasonochemical force to obtain hybrid nanocomposites. The process is demonstrated using polymer poly(ethylene glycol) (PEG), metalloid SiO(2)@Ag, and triblock copolymer ABA. The acoustic microstreaming and cavitation force from the ultrasonics are crucial parameters that determine the harmonized PEG stabilization and ABA blending of the metalloid nanocomposites that are obtained. Surface plasmon resonance in the resulting hybrid systems are examined by UV-vis absorbance spectroscopy. The resulting PEG-stabilized SiO(2)-Ag conjugated with a triblock copolymer poly(p-dioxanone-co-caprolactone)-block-poly(ethylene oxide)-block-poly(p-dioxanone-co-caprolactone) (PPDO-co-PCL-b-PEG-b-PPDO-co-PCL/ABA) (PEG-SiO(2)@Ag/ABA) shows a red shift of 20 nm (410 nm) from its initial resonance at 390 nm (PEG-SiO(2)@Ag). Nanocomposite particles were then spin-coated on a glass substrate to obtain the growth of thin solid laminates (thickness 27 microm). Structural functionality was studied by FT-IR, (1)H NMR, and FT-Raman spectroscopy. Morphological properties were ensured from FE-SEM, HRTEM, AFM, and FIB-SEM. Identity and crystallinity of the prepared nanocomposite were confirmed by XRD analysis. A very low weight percentile loss of the fabricated nanocomposites ensures its high thermal stability. Fabricated nanocomposite laminate might have a role in coating, reinforcement, and resistance and as substrate additives for a variety of surface and interface studies. Further, the ultrasonochemical approach utilized here could also be a smart system to fabricate other heteronanostructures in a single platform.

Study of optical properties of vacuum evaporated carbon nanotube containing Se80Te16Cu4 thin films

NASA Astrophysics Data System (ADS)

Upadhyay, A. N.; Tiwari, R. S.; Singh, Kedar

2016-08-01

Thin films of Se80Te16Cu4 glassy alloy and 3 wt.% of carbon nanotubes (CNTs) containing Se80Te16Cu4 glassy composite were deposited on clean glass substrate by thermal evaporation technique. The scanning electron microscope and energy dispersive x-ray analysis were performed to investigate the surface morphology and elemental composition of as synthesised samples. The reflectance and transmittance spectra of as-deposited thin films were recorded (200-1100 nm) by using UV/VIS/NIR spectrophotometer. The optical band gap and optical constants such as absorption coefficient (α), refractive index (n) and extinction coefficient (k) of Se80Te16Cu4 and 3 wt.% CNTs-Se80Te16Cu4 glassy composite thin films were calculated. It is observed that optical properties alter due to CNTs incorporation in Se80Te16Cu4 glassy alloy. Effect on optical properties due to CNTs incorporation can be explained in terms of concentration of unsaturated bonds/defects in the localised states.

CuAlO2 and CuAl2O4 thin films obtained by stacking Cu and Al films using physical vapor deposition

NASA Astrophysics Data System (ADS)

Castillo-Hernández, G.; Mayén-Hernández, S.; Castaño-Tostado, E.; DeMoure-Flores, F.; Campos-González, E.; Martínez-Alonso, C.; Santos-Cruz, J.

2018-06-01

CuAlO2 and CuAl2O4 thin films were synthesized by the deposition of the precursor metals using the physical vapor deposition technique and subsequent annealing. Annealing was carried out for 4-6 h in open and nitrogen atmospheres respectively at temperatures of 900-1000 °C with control of heating and cooling ramps. The band gap measurements ranged from 3.3 to 4.5 eV. Electrical properties were measured using the van der Pauw technique. The preferred orientations of CuAlO2 and CuAl2O4 were found to be along the (1 1 2) and (3 1 1) planes, respectively. The phase percentages were quantified using a Rietveld refinement simulation and the energy dispersive X-ray spectroscopy indicated that the composition is very close to the stoichiometry of CuAlO2 samples and with excess of aluminum and deficiency of copper for CuAl2O4 respectively. High resolution transmission electron microscopy identified the principal planes in CuAlO2 and in CuAl2O4. Higher purities were achieved in nitrogen atmosphere with the control of the cooling ramps.

CuIn(S,Se)(2) thin films prepared from a novel thioacetic acid-based solution and their photovoltaic application.

PubMed

Xie, Yian; Liu, Yufeng; Wang, Yaoming; Zhu, Xiaolong; Li, Aimin; Zhang, Lei; Qin, Mingsheng; Lü, Xujie; Huang, Fuqiang

2014-04-28

Low-cost and high-yield preparation of CuInSe2 films is the bottleneck for promising CuInSe2-based thin film solar cells. Here, we developed a simple, safe and cost-effective method using thioacetic acid to fabricate the absorber films of CuIn(S,Se)2 (CISSe). Dissolution of Cu2O and In(OH)3 in thioacetic acid was attributed to the strong coordination ability of S. The adhesive precursor solution can be prepared without any heating, centrifugation and inert gas protection, superior to the previously reported methods. The precursor CISSe layer was easily deposited in air by spin coating to ensure low cost. Uniform and compact CISSe thin films with well-crystallized and pure-phased CISSe grains were obtained after one step annealing. The as-prepared CISSe thin films were successfully applied to solar cells and a energy conversion efficiency of 6.75% was achieved. This facile preparation provides a low-cost and easy method to fabricate Cu-based thin film solar cells.

Solution-Processed Cu2ZnSn(S,Se) 4 Thin-Film Solar Cells Using Elemental Cu, Zn, Sn, S, and Se Powders as Source.

PubMed

Guo, Jing; Pei, Yingli; Zhou, Zhengji; Zhou, Wenhui; Kou, Dongxing; Wu, Sixin

2015-12-01

Solution-processed approach for the deposition of Cu2ZnSn (S,Se)4 (CZTSSe) absorbing layer offers a route for fabricating thin film solar cell that is appealing because of simplified and low-cost manufacturing, large-area coverage, and better compatibility with flexible substrates. In this work, we present a simple solution-based approach for simultaneously dissolving the low-cost elemental Cu, Zn, Sn, S, and Se powder, forming a homogeneous CZTSSe precursor solution in a short time. Dense and compact kesterite CZTSSe thin film with high crystallinity and uniform composition was obtained by selenizing the low-temperature annealed spin-coated precursor film. Standard CZTSSe thin film solar cell based on the selenized CZTSSe thin film was fabricated and an efficiency of 6.4 % was achieved.

Support for indoor tanning policies among young adult women who indoor tan.

PubMed

Mays, Darren; Murphy, Sarah E; Bubly, Rachel; Atkins, Michael B; Tercyak, Kenneth P

2016-12-01

The purpose of this study to examine support for indoor tanning policies and correlates of policy support among young adult women who indoor tan. Non-Hispanic white women ages 18-30 who indoor tanned in the past year (n = 356, M 23.3 age, SD 3.1) recruited in the Washington, DC area from 2013 to 2016 completed measures of indoor tanning behaviors, attitudes, perceptions, beliefs, and policy support. Most women in the sample supported policies to prevent children under the age of 18 from indoor tanning (74.0 %) and stronger warnings about the risks of indoor tanning on tanning devices (77.6 %); only 10.1 % supported a total ban. In multivariable analyses, support for individual indoor tanning policies varied by demographics (e.g., age), frequent indoor tanning behavior, indoor tanning beliefs, and risk perceptions. Non-Hispanic white young adult women who indoor tan, the primary consumers of indoor tanning, and a high-risk population, largely support indoor tanning prevention policies implemented by many state governments and those currently under review for national enactment. Given low levels of support for a total indoor tanning ban, support for other potential policies (e.g., increasing the minimum age to 21) should be investigated to inform future steps to reduce indoor tanning and the associated health risks.

Laser additive manufacturing bulk graphene-copper nanocomposites.

PubMed

Hu, Zengrong; Chen, Feng; Lin, Dong; Nian, Qiong; Parandoush, Pedram; Zhu, Xing; Shao, Zhuqiang; Cheng, Gary J

2017-11-03

The exceptional mechanical properties of graphene make it an ideal nanofiller for reinforcing metal matrix composites (MMCs). In this work, graphene-copper (Gr-Cu) nanocomposites have been fabricated by a laser additive manufacturing process. Transmission electron microscopy (TEM), x-ray diffraction (XRD) and Raman spectroscopy were utilized to characterize the fabricated nanocomposites. The XRD, Raman spectroscopy, energy dispersive spectroscopy and TEM results demonstrated the feasibility of laser additive manufacturing of Gr-Cu nanocomposites. The microstructures were characterized by high resolution TEM and the results further revealed the interface between the copper matrix and graphene. With the addition of graphene, the mechanical properties of the composites were enhanced significantly. Nanoindentation tests showed that the average modulus value and hardness of the composites were 118.9 GPa and 3 GPa respectively; 17.6% and 50% increases were achieved compared with pure copper, respectively. This work demonstrates a new way to manufacture graphene copper nanocomposites with ultra-strong mechanical properties and provides alternatives for applications in electrical and thermal conductors.

Laser additive manufacturing bulk graphene-copper nanocomposites

NASA Astrophysics Data System (ADS)

Hu, Zengrong; Chen, Feng; Lin, Dong; Nian, Qiong; Parandoush, Pedram; Zhu, Xing; Shao, Zhuqiang; Cheng, Gary J.

2017-11-01

The exceptional mechanical properties of graphene make it an ideal nanofiller for reinforcing metal matrix composites (MMCs). In this work, graphene-copper (Gr-Cu) nanocomposites have been fabricated by a laser additive manufacturing process. Transmission electron microscopy (TEM), x-ray diffraction (XRD) and Raman spectroscopy were utilized to characterize the fabricated nanocomposites. The XRD, Raman spectroscopy, energy dispersive spectroscopy and TEM results demonstrated the feasibility of laser additive manufacturing of Gr-Cu nanocomposites. The microstructures were characterized by high resolution TEM and the results further revealed the interface between the copper matrix and graphene. With the addition of graphene, the mechanical properties of the composites were enhanced significantly. Nanoindentation tests showed that the average modulus value and hardness of the composites were 118.9 GPa and 3 GPa respectively; 17.6% and 50% increases were achieved compared with pure copper, respectively. This work demonstrates a new way to manufacture graphene copper nanocomposites with ultra-strong mechanical properties and provides alternatives for applications in electrical and thermal conductors.

Graphene Oxide-Copper Nanocomposite-Coated Porous CaP Scaffold for Vascularized Bone Regeneration via Activation of Hif-1α.

PubMed

Zhang, Wenjie; Chang, Qing; Xu, Ling; Li, Guanglong; Yang, Guangzheng; Ding, Xun; Wang, Xiansong; Cui, Daxiang; Jiang, Xinquan

2016-06-01

Graphene has been studied for its in vitro osteoinductive capacity. However, the in vivo bone repair effects of graphene-based scaffolds remain unknown. The aqueous soluble graphene oxide-copper nanocomposites (GO-Cu) are fabricated, which are used to coat porous calcium phosphate (CaP) scaffolds for vascularized bone regeneration. The GO-Cu nanocomposites, containing crystallized CuO/Cu2 O nanoparticles of ≈30 nm diameters, distribute uniformly on the surfaces of the porous scaffolds and maintain a long-term release of Cu ions. In vitro, the GO-Cu coating enhances the adhesion and osteogenic differentiation of rat bone marrow stem cells (BMSCs). It is also found that by activating the Erk1/2 signaling pathway, the GO-Cu nanocomposites upregulate the expression of Hif-1α in BMSCs, resulting in the secretion of VEGF and BMP-2 proteins. When transplanted into rat with critical-sized calvarial defects, the GO-Cu-coated calcium phosphate cement (CPC) scaffolds (CPC/GO-Cu) significantly promote angiogenesis and osteogenesis. Moreover, it is observed via histological sections that the GO-Cu nanocomposites are phagocytosed by multinucleated giant cells. The results suggest that GO-Cu nanocomposite coatings can be utilized as an attractive strategy for vascularized bone regeneration. © 2016 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Spray pyrolysis synthesized Cu(In,Al)(S,Se)2 thin films solar cells

NASA Astrophysics Data System (ADS)

Aamir Hassan, Muhammad; Mujahid, Mohammad; Woei, Leow Shin; Wong, Lydia Helena

2018-03-01

Cu(In,Al)(S,Se)2 thin films are prepared by the Spray pyrolysis of aqueous precursor solutions of copper, indium, aluminium and sulphur sources. The bandgap of the films was engineered by aluminium (Al) doping in CISSe films deposited on molybdenum (Mo) coated glass substrate. The as-sprayed thin films were selenized at 500 °C for 10 min. Cadmium sulphide (CdS) buffer layer was deposited by chemical bath deposition process. Solar cell devices were fabricated with configuration of glass/Mo/CIASSe/CdS/i-ZnO/AZO. The solar cell device containing thin film of Cu(In,Al)(S,Se)2 with our optimized composition shows j-V characteristics of Voc = 0.47 V, jsc = 21.19 mA cm-2, FF = 52.88% and power conversion efficiency of 5.27%, under AM 1.5, 100 mW cm-2 illumination.

CVD growth of large-grain graphene on Cu(111) thin films

NASA Astrophysics Data System (ADS)

Miller, David L.; Diederichsen, Kyle M.; Keller, Mark W.

2013-03-01

Chemical vapor deposition of graphene on polycrystalline Cu foils has produced high quality films with carrier mobility approaching that of exfoliated graphene. Growth on single-crystal films of Cu has received less attention, despite its potential advantages for graphene quality and its importance for eventual applications. This is likely due to the difficulty of obtaining large (>= 1 mm) grains in Cu thin films, as well as dewetting and roughening of Cu films at temperatures near the Cu melting point (1084 C). We found that 450 nm of Cu(111), epitaxially grown by sputtering onto Al2O3(0001), formed > 1 mm grains when annealed at 1065 C for 40 minutes in 40 Torr of Ar and 2.5 mTorr of H2. After this annealing, adding 3 mTorr of CH4 for 8 minutes produced a monolayer graphene film covering > 99 % of the Cu surface. Stopping growth after 4 minutes produced dendritic graphene islands with 6-fold symmetry and diameter of 20 μm to 100 μm . After growth, the Cu film remained smooth except for thermal grooving at grain boundaries and a few holes of diameter ~ 10 μm where Cu dewetted completely (~ 10 holes on each 5 mm x 6 mm chip).

Growth and characterization of chalcostibite CuSbSe2 thin films for photovoltaic application

NASA Astrophysics Data System (ADS)

Tiwari, Kunal J.; Vinod, Vijay; Subrahmanyam, A.; Malar, P.

2017-10-01

Bulk copper antimony selenide was synthesized using mechanical alloying from the elemental precursors. Phase formation in milled powders was studied using x-ray diffraction (XRD) and Raman spectroscopy studies. The synthesized bulk source after cold compaction was used as source material for thin film deposition by e-beam evaporation. Thin film deposition was carried out at various e-beam current values (Ib ∼30, 40 and 50 mA) and at a substrate temperature of 200 °C. Near stoichiometric CuSbSe2 thin films were obtained for Ib values closer to 50 mA and post annealing at a temperature of 380 °C for 1 h. Thin films deposited using above conditions were found to exhibit an absorption coefficient (α) values of >105 cm-1 and a band gap value ∼1.18 eV that is closer to the reported band gap for CuSbSe2 compound.

Solution-processable alumina: PVP nanocomposite dielectric layer for high-performance organic thin-film transistors

NASA Astrophysics Data System (ADS)

Lin, Hui; Kong, Xiao; Li, Yiran; Kuang, Peng; Tao, Silu

2018-03-01

In this article, we have investigated the effect of nanocomposite gate dielectric layer built by alumina (Al2O3) and poly(4-vinyphenol) (PVP) with solution method which could enhance the dielectric capability and decrease the surface polarity. Then, we used modify layer to optimize the surface morphology of dielectric layer to further improve the insulation capability, and finally we fabricated the high-performance and low-voltage organic thin-film transistors by using this nanocomposite dielectric layer. The result shows that the devices with Al2O3:10%PVP dielectric layer with a modified layer exhibited a mobility of 0.49 cm2/Vs, I on/Ioff ratio of 7.8 × 104, threshold voltage of - 1.2 V, sub-threshold swing of 0.3 V/dec, and operating voltage as low as - 4 V. The improvement of devices performance was owing to the good insulation capability, appropriate capacitance of dielectric layer, and preferable interface contact, smaller crystalline size of active layer.

CuSb(S,Se)2 thin film heterojunction photovoltaic devices

NASA Astrophysics Data System (ADS)

Welch, Adam W.

Thin film heterojunction solar cells based on CuSb(S,Se)2 absorbers are investigated for two primary reasons. First, antimony is more abundant and less expensive than elements used in current thin film photovoltaics, In, Ga, and Te, and so, successful integration of Sb based materials offers greater diversification and scalability of solar energy. Second, the CuSb(S,Se) 2 ternary is chemically, electronically, and optically similar to the well-known, high efficiency, CuIn(S,Se)2 based materials. It is therefore postulated that the copper antimony ternaries will have similar defect tolerant electronic transport that may allow for similar highly efficient photoconversion. However, CuSb(S,Se)2 forms a layered crystal structure, different from the tetrahedral coordination found in conventional solar absorbers, due to the non-bonding lone pair of electrons on the antimony site. Thus examination of 2D antimony ternaries will lend insight into the role of structure in photoconversion processes. To address these questions, the semiconductors of interest (CuSbS 2 & CuSbSe2) were first synthesized on glass by combinatorial methods, to more quickly optimize process condi- tions. Radio-frequency (RF) magnetron co-sputtering from Sb2(S,Se)3 and Cu 2(S,Se) targets were used, without rotation, to produce chemical and flux graded libraries which were then subjected to high throughput characterization of structure (XRD), composition (XRF), conductivity (4pp), and optical absorption (UV/Vis/NIR). This approach rapidly identified processes that generated phase pure material with tunable carrier concentration by applying excess Sb 2(S,Se)3 within a temperature window bound by the volatility of Sb2(S,Se)3 and stability of the ternary phase. The resulting phase pure thin films were then incor- porated into the traditional CuInGaSe2 (CIGS) substrate photovoltaic (PV) architecture, and the resulting device performance was correlated to gradients in composition, sputter flux, absorber

Effects of Si content on microstructure and mechanical properties of TiAlN/Si3N4-Cu nanocomposite coatings

NASA Astrophysics Data System (ADS)

Feng, Changjie; Hu, Shuilian; Jiang, Yuanfei; Wu, Namei; Li, Mingsheng; Xin, Li; Zhu, Shenglong; Wang, Fuhui

2014-11-01

TiAlN/Si3N4-Cu nanocomposite coatings of various Si content (0-5.09 at.%) were deposited on AISI-304 stainless steel by DC reactive magnetron sputtering technique. The chemical composition, microstructure, mechanical and tribological properties of these coatings were systematically investigated by means of X-ray diffraction (XRD), field emission scanning electron microscope (FESEM), nanoindentation tester, a home-made indentation system, a scratch tester and a wear tester. Results indicated that with increasing Si content in these coatings, a reduction of grain size and surface roughness, a transformation of the (1 1 1) preferred orientation was detected by XRD and FESEM. Furthermore the hardness of these coatings increase from 9.672 GPa to 18.628 GPa, and the elastic modulus reveal the rising trend that increase from 224.654 GPa to 251.933 GPa. However, the elastic modulus of TiAlN/Si3N4-Cu coating containing 3.39 at.% Si content dropped rapidly and changed to about 180.775 GPa. The H3/E2 ratio is proportional to the film resistance to plastic deformation. The H3/E2 ratio of the TiAlN/Si3N4-Cu coating containing 3.39 at.% Si content possess of the maximum of 0.11 GPa, and the indentation test indicate that few and fine cracks were observed from its indentation morphologies. The growth pattern of cracks is mainly bending growing. The present results show that the best toughness is obtained for TiAlN/Si3N4-Cu nanocomposite coating containing 3.39 at.% Si content. In addition, the TiAlN/Si3N4-Cu coating containing 3.39 at.% Si content also has good adhesion property and superior wear resistance, and the wear mechanism is mainly adhesion wear.

High absorption coefficients of the CuSb(Se,Te)2 and CuBi(S,Se)2 alloys enable high-efficient 100 nm thin-film photovoltaics

NASA Astrophysics Data System (ADS)

Chen, Rongzhen; Persson, Clas

2017-06-01

We demonstrate that the band-gap energies Eg of CuSb(Se,Te)2 and CuBi(S,Se)2 can be optimized for high energy conversion in very thin photovoltaic devices, and that the alloys then exhibit excellent optical properties, especially for tellurium rich CuSb(Se1-xTex)2. This is explained by multi-valley band structure with flat energy dispersions, mainly due to the localized character of the Sb/Bi p-like conduction band states. Still the effective electron mass is reasonable small: mc ≈ 0.25m0 for CuSbTe2. The absorption coefficient α(ω) for CuSb(Se1-xTex)2 is at ħω = Eg + 1 eV as much as 5-7 times larger than α(ω) for traditional thin-film absorber materials. Auger recombination does limit the efficiency if the carrier concentration becomes too high, and this effect needs to be suppressed. However with high absorptivity, the alloys can be utilized for extremely thin inorganic solar cells with the maximum efficiency ηmax ≈ 25% even for film thicknesses d ≈ 50 - 150 nm, and the efficiency increases to ˜30% if the Auger effect is diminished.

Decorating graphene oxide with CuO nanoparticles in a water-isopropanol system.

PubMed

Zhu, Junwu; Zeng, Guiyu; Nie, Fude; Xu, Xiaoming; Chen, Sheng; Han, Qiaofeng; Wang, Xin

2010-06-01

A facile chemical procedure capable of aligning CuO nanoparticles on graphene oxide (GO) in a water-isopropanol system has been described. Scanning electron microscopy (SEM) and transmission electron microscopy (TEM) observations indicate that the exfoliated GO sheets are decorated randomly by spindly or spherical CuO nanoparticle aggregates, forming well-ordered CuO:GO nanocomposites. A formation mechanism of these interesting nanocomposites is proposed as intercalation and adsorption of Cu2+ ions onto the GO sheets, followed by the nucleation and growth of the CuO crystallites, which in return resulted in the exfoliation of GO sheets. Moreover, the obtained nanocomposites exhibit a high catalytic activity for the thermal decomposition of ammonium perchlorate (AP), due to the concerted effect of CuO and GO.

Probing localized strain in solution-derived YB a2C u3O7 -δ nanocomposite thin films

NASA Astrophysics Data System (ADS)

Guzman, Roger; Gazquez, Jaume; Mundet, Bernat; Coll, Mariona; Obradors, Xavier; Puig, Teresa

2017-07-01

Enhanced pinning due to nanoscale strain is unique to the high-Tc cuprates, where pairing may be modified with lattice distortion. Therefore a comprehensive understanding of the defect landscape is required for a broad range of applications. However, determining the type and distribution of defects and their associated strain constitutes a critical task, and for this aim, real-space techniques for atomic resolution characterization are necessary. Here, we use scanning transmission electron microscopy (STEM) to study the atomic structure of individual defects of solution-derived YB a2C u3O7 (YBCO) nanocomposites, where the inclusion of incoherent secondary phase nanoparticles within the YBCO matrix dramatically increases the density of Y1B a2C u4O8 (Y124) intergrowths, the commonest defect in YBCO thin films. The formation of the Y124 is found to trigger a concatenation of strain-derived interactions with other defects and the concomitant nucleation of intrinsic defects, which weave a web of randomly distributed nanostrained regions that profoundly transform the vortex-pinning landscape of the YBCO nanocomposite thin films.

Electrical-transport properties and microwave device performance of sputtered TlCaBaCuO superconducting thin films

NASA Technical Reports Server (NTRS)

Subramanyam, G.; Kapoor, V. J.; Chorey, C. M.; Bhasin, K. B.

1992-01-01

The paper describes the processing and electrical transport measurements for achieving reproducible high-Tc and high-Jc sputtered TlCaBaCuO thin films on LaAlO3 substrates, for microelectronic applications. The microwave properties of TlCaBaCuO thin films were investigated by designing, fabricating, and characterizing microstrip ring resonators with a fundamental resonance frequency of 12 GHz on 10-mil-thick LaAlO3 substrates. Typical unloaded quality factors for a ring resonator with a superconducting ground plane of 0.3 micron-thickness and a gold ground plane of 1-micron-thickness were above 1500 at 65 K. Typical values of penetration depth at 0 K in the TlCaBaCuO thin films were between 7000 and 8000 A.

Method to produce catalytically active nanocomposite coatings

DOEpatents

Erdemir, Ali; Eryilmaz, Osman Levent; Urgen, Mustafa; Kazmanli, Kursat

2016-02-09

A nanocomposite coating and method of making and using the coating. The nanocomposite coating is disposed on a base material, such as a metal or ceramic; and the nanocomposite consists essentially of a matrix of an alloy selected from the group of Cu, Ni, Pd, Pt and Re which are catalytically active for cracking of carbon bonds in oils and greases and a grain structure selected from the group of borides, carbides and nitrides.

Preparation and characterization of a poly (1, 4-phenylenevinylene) derivative-based hybrid thin film nanocomposites with enhanced performance

NASA Astrophysics Data System (ADS)

Belhaj, Marwa; Jemmeli, Dhouha; Dridi, Cherif; Ben Salem, Balkiss; Jaballah, Najmeddine; Majdoub, Mustapha; Yatskiv, Roman; Grym, Jan

2018-05-01

In this study, a poly (1, 4-phenylenevinylene) derivative (PPV-C6) was synthesized via Gilch polycondensation, and its electrochemical and optical characteristics were determined by cyclic voltammetry analysis, ultraviolet-visible, and photoluminescence spectroscopy. The polymer exhibited semiconductor behavior with an optical band gap of about 2.02 eV. Thin-film hybrid nanocomposites were prepared based on PPV-C6 with a large range of concentrations of sol-gel synthesized surfactant-free ZnO nanoparticles (n-ZnO). We investigated the photophysical properties of nanocomposites with different weight ratios of n-ZnO. The optical absorption spectra of PPV-C6: n-ZnO nanocomposites exhibited moderate variation in terms of the optical band gap energy with respect to the pristine polymer. Photoluminescence spectra indicated that the optimum n-ZnO concentration was about 50 wt% to achieve photoluminescence quenching, which corresponded to the most homogeneous surface and efficient charge transfer due to optimal exciton dissociation. We established good correlations between the investigated properties.

Thermochemical and kinetic aspects of the sulfurization of Cu-Sb and Cu-Bi thin films

NASA Astrophysics Data System (ADS)

Colombara, Diego; Peter, Laurence M.; Rogers, Keith D.; Hutchings, Kyle

2012-02-01

CuSbS2 and Cu3BiS3 are being investigated as part of a search for new absorber materials for photovoltaic devices. Thin films of these chalcogenides were produced by conversion of stacked and co-electroplated metal precursor layers in the presence of elemental sulfur vapour. Ex-situ XRD and SEM/EDS analyses of the processed samples were employed to study the reaction sequence with the aim of achieving compact layer morphologies. A new “Time-Temperature-Reaction” (TTR) diagram and modified Pilling-Bedworth coefficients have been introduced for the description and interpretation of the reaction kinetics. For equal processing times, the minimum temperature required for CuSbS2 to appear is substantially lower than for Cu3BiS3, suggesting that interdiffusion across the interfaces between the binary sulfides is a key step in the formation of the ternary compounds. The effects of the heating rate and sulfur partial pressure on the phase evolution as well as the potential losses of Sb and Bi during the processes have been investigated experimentally and the results related to the equilibrium pressure diagrams obtained via thermochemical computation.

Method of fabricating high-efficiency Cu(In,Ga)(SeS).sub.2 thin films for solar cells

DOEpatents

Noufi, Rommel; Gabor, Andrew M.; Tuttle, John R.; Tennant, Andrew L.; Contreras, Miguel A.; Albin, David S.; Carapella, Jeffrey J.

1995-01-01

A process for producing a slightly Cu-poor thin film of Cu(In,Ga)(Se,S).sub.2 comprises depositing a first layer of (In,Ga).sub.x (Se,S).sub.y followed by depositing just enough Cu+(Se,S) or Cu.sub.x (Se,S) to produce the desired slightly Cu-poor material. In a variation, most, but not all, (about 90 to 99%) of the (In,Ga).sub.x (Se,S).sub.y is deposited first, followed by deposition of all the Cu+(Se,S) or Cu.sub.x (Se,S) to go near stoichiometric, possibly or even preferably slightly Cu-rich, and then in turn followed by deposition of the remainder (about 1 to 10%) of the (In,Ga).sub.x (Se,S).sub.y to end with a slightly Cu-poor composition. In yet another variation, a small portion (about 1 to 10%) of the (In,Ga).sub.x (Se,S).sub.y is first deposited as a seed layer, followed by deposition of all of the Cu+(Se,S) or Cu.sub.x (Se,S) to make a very Cu-rich mixture, and then followed deposition of the remainder of the (In,Ga).sub.x (Se,S).sub.y to go slightly Cu-poor in the final Cu(In,Ga)(Se,S).sub.2 thin film.

Method of fabricating high-efficiency Cu(In,Ga)(Se,S){sub 2} thin films for solar cells

DOEpatents

Noufi, R.; Gabor, A.M.; Tuttle, J.R.; Tennant, A.L.; Contreras, M.A.; Albin, D.S.; Carapella, J.J.

1995-08-15

A process for producing a slightly Cu-poor thin film of Cu(In,Ga)(Se,S){sub 2} comprises depositing a first layer of (In,Ga){sub x} (Se,S){sub y} followed by depositing just enough Cu+(Se,S) or Cu{sub x} (Se,S) to produce the desired slightly Cu-poor material. In a variation, most, but not all, (about 90 to 99%) of the (In,Ga){sub x} (Se,S){sub y} is deposited first, followed by deposition of all the Cu+(Se,S) or Cu{sub x} (Se,S) to go near stoichiometric, possibly or even preferably slightly Cu-rich, and then in turn followed by deposition of the remainder (about 1 to 10%) of the (In,Ga){sub x} (Se,S){sub y} to end with a slightly Cu-poor composition. In yet another variation, a small portion (about 1 to 10%) of the (In,Ga){sub x} (Se,S){sub y} is first deposited as a seed layer, followed by deposition of all of the Cu+(Se,S) or Cu{sub x} (Se,S) to make a very Cu-rich mixture, and then followed deposition of the remainder of the (In,Ga){sub x} (Se,S){sub y} to go slightly Cu-poor in the final Cu(In,Ga)(Se,S){sub 2} thin film. 5 figs.

Fabrication Processes and Mechanical Behavior of CNT/Metal Nanocomposites

DTIC Science & Technology

2013-12-01

process, were investigated and applied for fabrication of CNT/Cu and CNT/Ni nanocomposite powders. The spark plasma sintering process was applied... spark plasma sintering process to fabricate CNT/NiTi and CNT/Al-Cu nanocomposites. It is confirmed that the CNTs were homogeneously dispersed in NiTi...can be seen in Figure 1-1. The CNT/NiTi composite powders were consolidated by spark plasma sintering (SPS, Dr. Sinter Lab., Sumitomo). The CNT/NiTi

Controlled Synthesis of CuS/TiO2 Heterostructured Nanocomposites for Enhanced Photocatalytic Hydrogen Generation through Water Splitting.

PubMed

Chandra, Moumita; Bhunia, Kousik; Pradhan, Debabrata

2018-04-16

Photocatalytic hydrogen (H 2 ) generation through water splitting has attracted substantial attention as a clean and renewable energy generation process that has enormous potential in converting solar-to-chemical energy using suitable photocatalysts. The major bottleneck in the development of semiconductor-based photocatalysts lies in poor light absorption and fast recombination of photogenerated electron-hole pairs. Herein we report the synthesis of CuS/TiO 2 heterostructured nanocomposites with varied TiO 2 contents via simple hydrothermal and solution-based process. The morphology, crystal structure, composition, and optical properties of the as-synthesized CuS/TiO 2 hybrids are evaluated in detail. Controlling the CuS/TiO 2 ratio to an optimum value leads to the highest photocatalytic H 2 production rate of 1262 μmol h -1 g -1 , which is 9.7 and 9.3 times higher than that of pristine TiO 2 nanospindles and CuS nanoflakes under irradiation, respectively. The enhancement in the H 2 evolution rate is attributed to increased light absorption and efficient charge separation with an optimum CuS coverage on TiO 2 . The photoluminescence and photoelectrochemical measurements further confirm the efficient separation of charge carriers in the CuS/TiO 2 hybrid. The mechanism and synergistic role of CuS and TiO 2 semiconductors for enhanced photoactivity is further delineated.

Structure and photoelectrochemistry of silver-copper-indium-diselenide ((AgCu)InSe2) thin film

NASA Astrophysics Data System (ADS)

Zhang, Lin Rui; Li, Tong; Wang, Hao; Pang, Wei; Chen, Yi Chuan; Song, Xue Mei; Zhang, Yong Zhe; Yan, Hui

2018-02-01

In this work, silver (Ag) precursors with different thicknesses were sputtered on the surfaces of CuIn alloys, and (AgCu)InSe2 (ACIS) films were formed after selenization at 550 °C under nitrogen condition using a rapid thermal process furnace. The structure and electrical properties of the ACIS films were investigated. The result showed that the distribution of Ag+ ion was more uniform with increasing the thickness of Ag precursor, and the surface of the thin-film became more homogeneous and denser. When Ag/Cu ratio ≥0.249, the small grain particles disappeared. The band gap can be rationally controlled by adjusting Ag content. When (Ag + Cu)/In ratio ≥ 1.15, the surface of the ACIS thin-film mainly exhibited n-type semiconductor. Through the photoelectrochemistry measurement, it was observed that the incorporation of Ag+ ions could improve photocurrent by adjusting the band gap. With the Ag precursor thickness increased, the dark current decreased at the more negative potential.

Characterization of Cu2ZnSnS4 thin films prepared by photo-chemical deposition

NASA Astrophysics Data System (ADS)

Moriya, Katsuhiko; Watabe, Jyunichi; Tanaka, Kunihiko; Uchiki, Hisao

2006-09-01

Cu2ZnSnS4 (CZTS) thin films were prepared by post-annealing films of metal sulfides of Cu2S, ZnS and SnS2 precursors deposited on soda-lime glass substrates by photo-chemical deposition (PCD) from aqueous solution containing CuSO4, ZnSO4, SnSO4 and Na2S2O3. In this study, sulfurization was employed to prepare high quality CZTS thin films. Deposited films of metal sulfides were annealed in a furnace in an atmosphere of N2 or N2+H2S(5%) at the temperature of 300°, 400° or 500 °C. The sulfured films showed X-ray diffraction peaks from (112), (220), and (312) planes of CZTS and the peaks became sharp by an increase in the sulfurization temperature. CZTS thin film annealed in atmosphere of N2 was S-poor. After annealing atmosphere was changed from N2 into N2+H2S(5%), the decrease of a composi- tional ratio of sulfur could be suppressed.

Accumulation of Cr, Cd, Pb, Cu, and Zn by plants in tanning sludge storage sites: opportunities for contamination bioindication and phytoremediation.

PubMed

Yuan, Yongqiang; Yu, Shen; Bañuelos, G S; He, Yunfeng

2016-11-01

Tanning sludge enriched with high concentrations of Cr and other metals has adverse effects on the environment. Plants growing in the metalliferous soils may have the ability to cope with high metal concentrations. This study focuses on potentials of using native plants for bioindication and/or phytoremediation of Cr-contaminated sites. In the study, we characterized plants and soils from six tanning sludge storage sites. Soil in these sites exhibited toxic levels of Cr (averaged 16,492 mg kg -1 ) and other metals (e.g., 48.3 mg Cu kg -1 , 2370 mg Zn kg -1 , 44.9 mg Pb kg -1 , and 0.59 mg Cd kg -1 ). Different metal tolerance and accumulation patterns were observed among the sampled plant species. Phragmites australis, Zephyranthes candida, Cynodon dactylon, and Alternanthera philoxeroides accumulated moderate-high concentrations of Cr and other metals, which could make them good bioindicators of heavy metal pollution. High Cr and other metal concentrations (e.g., Cd and Pb) were found in Chenopodium rubrum (372 mg Cr kg -1 ), Aster subulatus (310 mg Cr kg -1 ), and Brassica chinensis (300 mg Cr kg -1 ), being considered as metal accumulators. In addition, Nerium indicum and Z. candida were able to tolerate high concentrations of Cr and other metals, and they may be used as preferable pioneer species to grow or use for restoration in Cr-contaminated sites. This study can be useful for establishing guidelines to select the most suitable plant species to revegetate and remediate metals in tanning sludge-contaminated fields.

Tanning

MedlinePlus

... Spray tans, lotions, or gels use a color additive that makes your skin look tan called DHA. DHA is considered safe for use on the outside of your body by the U.S. Food and Drug Administration. You need to make sure ...

New strain states and radical property tuning of metal oxides using a nanocomposite thin film approach

DOE PAGES

MacManus-Driscoll, Judith; Suwardi, Ady; Kursumovic, Ahmed; ...

2015-05-05

Auxetic-like strain states were generated in self-assembled nanocomposite thin films of (Ba 0.6Sr 0.4TiO 3) 1–x – (Sm 2O 3) x(BSTO – SmO). A switch from auxetic-like to elastic-like strain behavior was observed for x > 0.50, when the SmO switched from being nanopillars in the BSTO matrix to being the matrix with BSTO nanopillars embedded in it. A simple model was adopted to explain how in-plane strain varies with x. At high x (0.75), strongly enhanced ferroelectric properties were obtained compared to pure BSTO films. Furthermore, the nanocomposite method represents a powerful new way to tune the properties ofmore » a wide range of strongly correlated metal oxides whose properties are very sensitive to strain.« less

Electromigration in epitaxial Cu(001) lines

NASA Astrophysics Data System (ADS)

Ramanath, G.; Kim, H.; Goindi, H. S.; Frederick, M. J.; Shin, C.-S.; Goswami, R.; Petrov, I.; Greene, J. E.

2002-04-01

We report the electromigration (EM) response of single-domain epitaxial Cu(001) lines on layers of Ta, TaN, and TiN. Epitaxial Cu(001) lines on nitride layers exhibit nearly two orders of magnitude higher mean-time-to-failure (MTTF) values than those on Ta, indicating the strong influence of the underlayer. The activation energy of EM for Cu on the nitrides is ˜0.8-1.2 eV, and that of Cu on Ta is ˜0.2 eV, for 200-300 °C. Our results also indicate that the MTTF values correlate inversely to the crystal quality of the Cu layers measured by X-ray diffraction. The EM resistance of epitaxial Cu lines with different crystal quality on TaN were measured to separate the effects of interface chemistry and crystal quality. While higher quality epitaxial films reveal a higher EM resistance, the magnitude of the change is smaller than that obtained by changing the interface chemistry. Epitaxial lines exhibit more than 3-4 orders of magnitude higher MTTF than polycrystalline lines on the same underlayer. Based upon our results, we propose that the Cu/underlayer interface chemistry and presence of grain boundary diffusion play important roles in unpassivated Cu films.

Spray-on tanning.

PubMed

Rogers, Cindy J

2005-01-01

The modern formulation of dihydroxyacetone (DHA), the only sunless tanning solution approved by the Food and Drug Administration (FDA), is combined with bronzers and moisturizers to deliver a cosmetically acceptable skin color and a natural-looking tan without ultraviolet (UV) exposure. Spray-on tanning products, which deliver this formulation evenly to achieve a full body tan, may be applied in a tanning booth, airbrushed on by a technician, or sprayed on at home, and they appear to offer a generally safe alternative for patients who seek a suntanned appearance.

Disentangling vortex pinning landscape in chemical solution deposited superconducting YBa2Cu3O7-x films and nanocomposites

NASA Astrophysics Data System (ADS)

Palau, A.; Vallès, F.; Rouco, V.; Coll, M.; Li, Z.; Pop, C.; Mundet, B.; Gàzquez, J.; Guzman, R.; Gutierrez, J.; Obradors, X.; Puig, T.

2018-07-01

In-field angular pinning performances at different temperatures have been analysed on chemical solution deposited (CSD) YBa2Cu3O7-x (YBCO) pristine films and nanocomposites. We show that with this analysis we are able to quantify the vortex pinning strength and energies, associated with different kinds of natural and artificial pinning defects, acting as efficient pinning centres at different regions of the H-T phase diagram. A good quantification of the variety of pinning defects active at different temperatures and magnetic fields provides a unique tool to design the best vortex pinning landscape under different operating conditions. We have found that by artificially introducing a unique defect in the YBCO matrix, the stacking faults, we are able to modify three different contributions to vortex pinning (isotropic-strong, anisotropic-strong, and isotropic-weak). The isotropic-strong contribution, widely studied in CSD YBCO nanocomposites, is associated with nanostrained regions induced at the partial dislocations surrounding the stacking faults. Moreover, the stacking fault itself acts as a planar defect which provides a very effective anisotropic-strong pinning at H//ab. Finally, the large presence of Cu-O cluster vacancies found in the stacking faults have been revealed as a source of isotropic-weak pinning sites, very active at low temperatures and high fields.

Deposition of ultra thin CuInS₂ absorber layers by ALD for thin film solar cells at low temperature (down to 150 °C).

PubMed

Schneider, Nathanaelle; Bouttemy, Muriel; Genevée, Pascal; Lincot, Daniel; Donsanti, Frédérique

2015-02-06

Two new processes for the atomic layer deposition of copper indium sulfide (CuInS₂) based on the use of two different sets of precursors are reported. Metal chloride precursors (CuCl, InCl₃) in combination with H2S imply relatively high deposition temperature (Tdep = 380 °C), and due to exchange reactions, CuInS₂ stoechiometry was only achieved by depositing In₂S3 layers on a CuxS film. However, the use of acac- metal precursors (Cu(acac)₂, In(acac)₃) allows the direct deposition of CuInS₂ at temperature as low as 150 °C, involving in situ copper-reduction, exchange reaction and diffusion processes. The morphology, crystallographic structure, chemical composition and optical band gap of thin films were investigated using scanning electronic microscope, x-ray diffraction under grazing incidence conditions, x-ray fluorescence, energy dispersive spectrometry, secondary ion mass spectrometry, x-ray photoelectron spectroscopy and UV-vis spectroscopy. Films were implemented as ultra-thin absorbers in a typical CIS-solar cell architecture and allowed conversion efficiencies up to 2.8%.

Preparation and characterization of chitosan-clay nanocomposites for the removal of Cu(II) from aqueous solution.

PubMed

Azzam, Eid M S; Eshaq, Gh; Rabie, A M; Bakr, A A; Abd-Elaal, Ali A; El Metwally, A E; Tawfik, Salah M

2016-08-01

In the present study, chitosan assembled on gold and silver nanoparticles were prepared and characterized by UV-vis, TEM, EDX and DLS techniques. The nanocomposites chitosan (Ch)/clay, chitosan (Ch)/AgNPs/clay and chitosan (Ch)/AuNPs/clay were prepared by solution mixing method and characterized by FTIR, XRD, and SEM techniques. The adsorption of copper(II) ions onto the prepared hybrid composites from an aqueous solution using batch adsorption was examined. The results showed that benefiting from the surface property of clay, the abundant amino and hydroxyl functional groups of chitosan, the adsorbent provides adequate and versatile adsorption for the Cu(II) ions under investigation. The batch adsorption experiments showed that the adsorption of the Cu(II) is considerably dependent on pH of milieu, the amount of adsorbent, and contact time. Batch adsorption studies revealed that the adsorption capacity of Cu(II) increased with increase in initial concentration and contact time with optimum pH in the range around neutral. The maximum uptake of Cu(II) ions by (Ch)/AgNPs/clay composite was found to be 181.5mg/g. The adsorption efficiency of Cu(II) ions by prepared (Ch)/AgNPs/clay and (Ch)/AuNPs/clay is bigger than that the individual chitosan (Ch)/clay composite which clarifies the role of metal nanoparticles in enhancement the adsorption characters. The study suggests that the (Ch)/AgNPs/clay hybrid composite is a promising nano-adsorbent for the removal of Cu(II) ions from aqueous solution. Copyright © 2016 Elsevier B.V. All rights reserved.

Tanning

MedlinePlus

... be dangerous and are not approved by the Food and Drug Administration (FDA). Sunless tanners have no known risk for skin cancer, but you do have to be careful. Most spray tans, lotions, and gels use DHA, a color additive that makes your skin look tan. DHA is ...

Killer tans: state, feds crack down on indoor tanning.

PubMed

Conde, Crystal

2010-05-01

The American Cancer Society says that using a tanning bed before age 35 increases a person's risk of developing melanoma by 75 percent. Physicians hope that recent actions by the FTC, along with TMA-supported state legislation placing age restrictions on minors' use of tanning beds, will spur the tanning industry to operate more responsibly and stop spreading false information to the public.

Ultrasensitive non-enzymatic glucose sensor based on three-dimensional network of ZnO-CuO hierarchical nanocomposites by electrospinning

PubMed Central

Zhou, Chunyang; Xu, Lin; Song, Jian; Xing, Ruiqing; Xu, Sai; Liu, Dali; Song, Hongwei

2014-01-01

Three-dimensional (3D) porous ZnO–CuO hierarchical nanocomposites (HNCs) nonenzymatic glucose electrodes with different thicknesses were fabricated by coelectrospinning and compared with 3D mixed ZnO/CuO nanowires (NWs) and pure CuO NWs electrodes. The structural characterization revealed that the ZnO–CuO HNCs were composed of the ZnO and CuO mixed NWs trunk (~200 nm), whose outer surface was attached with small CuO nanoparticles (NPs). Moreover, a good synergetic effect between CuO and ZnO was confirmed. The nonenzymatic biosensing properties of as prepared 3D porous electrodes based on fluorine doped tin oxide (FTO) were studied and the results indicated that the sensing properties of 3D porous ZnO–CuO HNCs electrodes were significantly improved and depended strongly on the thickness of the HNCs. At an applied potential of + 0.7 V, the optimum ZnO–CuO HNCs electrode presented a high sensitivity of 3066.4 μAmM−1cm−2, the linear range up to 1.6 mM, and low practical detection limit of 0.21 μM. It also showed outstanding long term stability, good reproducibility, excellent selectivity and accurate measurement in real serum sample. The formation of special hierarchical heterojunction and the well-constructed 3D structure were the main reasons for the enhanced nonenzymatic biosensing behavior. PMID:25488502

Tunable Core-Shell Single-Walled Carbon Nanotube-Cu2S Networked Nanocomposites as High-Performance Cathodes for Lithium-ion Batteries

DOE PAGES

Meng, Xiangbo; Riha, Shannon C.; Libera, Joseph A.; ...

2015-01-24

In this study, nanoscale copper(I) sulfide (n-Cu2S) was deposited over networks of single-walled carbon nanotubes (SWCNTs) by atomic layer deposition (ALD). This synthetic route provides a high degree of control for tuning the materials properties. The resulting core shell SWCNT-n-Cu2S composite structure ensures an intimate contact between the two components while maintaining a high porosity for efficient transport of charges. Indeed, electrochemical testing demonstrates that these nanocomposites are promising as cathodes in lithium-ion batteries (LIBs), exhibiting excellent stability over 200 discharge-charge cycles with a sustainable, high capacity of 260 mAh g(-1) (92% of the theoretical value in terms of Cu2S)more » and >99% Coulombic efficiency. This work establishes a general strategy for developing high-performance nanoscale electrode materials.« less

Optical and thermogravimetric analysis of Zn1-xCuxS/PVA nanocomposite films

NASA Astrophysics Data System (ADS)

Mohamed, Mohamed Bakr; Heiba, Zein K.; Imam, N. G.

2018-07-01

Cu doped ZnS nanoparticles with cubic blend structure had been prepared successfully through thermolysis route and then composited with poly vinyl alcohol using casting method. Zn1-xCuxS/PVA nanocomposites were characterized using different characterization techniques. The quantum dot nature of the ZnS:Cu phase was confirmed by transmission electron microscope technique. Thermal stability was studied by thermogravimetric analysis. The ultra violet measurements illustrated that addition of Zn1-xCuxS nanoparticles to PVA matrix increased the film absorbance. Furthermore, the energy gap and refractive index of the composites were obtained from ultra violet and photoluminescence spectrophotometers. The photoluminescence spectra of ZnS:Cu/PVA nanocomposite films demonstrated a quite broad emission peak at 435 nm with highest photoluminescence intensity in nanocomposite doped with 1% Cu.

Device level optimization of poly(vinylidene fluoride-trifluoroethylene)–zinc oxide polymer nanocomposite thin films for ferroelectric applications

DOE Office of Scientific and Technical Information (OSTI.GOV)

C K, Subash, E-mail: cksubash08@gmail.com; Valiyaneerilakkal, Uvais; Varghese, Soney

Polymer nanocomposite was prepared using poly(vinylidene fluoride-trifluoroethylene) and zinc oxide (ZnO) nanopowder, which are ferroelectric in nature. Nanocomposite was prepared in various concentrations(0.2, 0.4, 0.8, and 1 wt. %) using probe ultra-sonication, followed by spin coating and annealing at 120 °C for 2 h to improve the formation of β-phase. Metal-ferroelectric-metal capacitor was fabricated using this optimized thin film as a ferroelectric layer. Device level optimization was carried out by polarization-electric field (P-E) hysteresis studies of this film, which shows polarization enhancement of composite. Various characterization techniques like atomic force microscopy, Fourier transform infra-red spectroscopy (FT-IR), Differential scanning calorimetry, and X-ray diffractionmore » were used to study the β-phase formation of nancomposite. The capacitance–voltage (C-V) and current-voltage (I-V) characteristics were studied through varying frequency and temperature. C-V measurements show an increase of 79% in the capacitance of polymer nanocomposite, which can be used for the fabrication of ferroelectric devices.« less

Perceptions of tanning risk among melanoma patients with a history of indoor tanning.

PubMed

Nergard-Martin, Jennifer; Caldwell, Chauncey; Barr, Morgan; Dellavalle, Robert P; Solomon, James A

2018-01-01

A new US Food and Drug Administration (FDA) regulation classified tanning beds as class II, requiring indoor tanning facilities to inform users of the risk of skin cancer in efforts to reverse the growing trend in indoor tanning. However, little is known from the patient's perspective on whether knowledge of the risk of skin cancer development is a deterrent to indoor tanning. There also is conflicting literature regarding the relationship among frequency of indoor tanning, age at onset of melanoma diagnosis, and characteristics of diagnosis in melanoma patients with a history of indoor tanning. An international survey was conducted in patients 18 years and older who self-reported being diagnosed with melanoma after indoor tanning. The purpose of this study was to investigate the patients' perspective on indoor-tanning behaviors as associated with the severity of their melanomas and the time frame in which they were diagnosed as well as their perceived views on the safety of indoor tanning and the frequency in which they continue to tan indoors.

Indoor tanning and problem behavior.

PubMed

Bagdasarov, Zhanna; Banerjee, Smita; Greene, Kathryn; Campo, Shelly

2008-01-01

The authors examined factors predicting college students' use of tanning beds. Undergraduate students (N = 745) at a large Northeastern university participated in the study by answering a survey measuring tanning behavior and other psychosocial variables, including sensation seeking, self-esteem, tanning image beliefs, and friends' tanning bed use. All 3 systems from problem behavior theory predicted past tanning bed use and intention to use tanning beds. The authors observed a positive association between sensation seeking and intention to use tanning beds. Tanning image beliefs were positively associated with both past tanning behavior and intention to use tanning beds. Interventions focusing on friend and acquaintance social network influences may be more effective than health-risk campaigns in reducing tanning bed use.

Superconducting YBa2Cu3O7- δ Thin Film Detectors for Picosecond THz Pulses

NASA Astrophysics Data System (ADS)

Probst, P.; Scheuring, A.; Hofherr, M.; Wünsch, S.; Il'in, K.; Semenov, A.; Hübers, H.-W.; Judin, V.; Müller, A.-S.; Hänisch, J.; Holzapfel, B.; Siegel, M.

2012-06-01

Ultra-fast THz detectors from superconducting YBa2Cu3O7- δ (YBCO) thin films were developed to monitor picosecond THz pulses. YBCO thin films were optimized by the introduction of CeO2 and PrBaCuO buffer layers. The transition temperature of 10 nm thick films reaches 79 K. A 15 nm thick YBCO microbridge (transition temperature—83 K, critical current density at 77 K—2.4 MA/cm2) embedded in a planar log-spiral antenna was used to detect pulsed THz radiation of the ANKA storage ring. First time resolved measurements of the multi-bunch filling pattern are presented.

Effect of annealing atmosphere on properties of Cu2ZnSn(S,Se)4 thin films

NASA Astrophysics Data System (ADS)

Xue, Yuming; Yu, Bingbing; Li, Wei; Feng, Shaojun; Wang, Yukun; Huang, Shengming; Zhang, Chao; Qiao, Zaixiang

2017-12-01

Earth-abundant Cu2ZnSn(S,Se)4(CZTSSe) thin film photovoltaic absorber layers were fabricated by co-evaporated Cu, ZnS, SnS and Se sources in a vacuum chamber followed by annealing at tubular furnace for 30 min at 550 °C. In this paper, we investigated the metal elements with stoichiometric ratio film to study the effect of annealing conditions of Se, SnS + Se, S and SnS + S atmosphere on the structure, surface morphological, optical and electrical properties of Cu2ZnSn(S,Se)4 thin films respectively. These films were characterized by Inductively Coupled Plasma-Mass Spectrometer, scanning electron microscopy, X-ray diffraction to investigate the composition, morphological and crystal structural properties. The grain size of samples were found to increase after annealing. XRD patterns confirmed the formation of pure polycrystalline CZTSSe thin films at S atmosphere, the optical band gaps are 1.02, 1.05, 1.23, 1.35 eV for Se, SnS + Se, SnS + S and S atmosphere respectively.

High Tc superconducting IR detectors from Y-Ba-Cu-O thin films

NASA Technical Reports Server (NTRS)

Lindgren, M.; Ahlberg, H.; Danerud, M.; Larsson, A.; Eng, M.

1990-01-01

A thin-film high-Tc superconducting multielement optical detector made of Y-Ba-Cu-O has been designed and evaluated using optical pulses from a diode laser (830 nm) and a Q-switched CO2-laser (10.6 microns). Different thin films have been tested. A laser deposited film showed the strongest response amplitude for short pulses and responded to an ultrafast, 50 ps wide pulse. Comparisons between dR/dT and response as a function of temperature indicated, however, a bolometric response.

French teenagers and artificial tanning.

PubMed

Tella, E; Beauchet, A; Vouldoukis, I; Séi, J-F; Beaulieu, P; Sigal, M-L; Mahé, E

2013-03-01

Exposure to solar and artificial ultraviolet (UV) radiations is a major risk factor for skin cancers. France has enacted one of the strictest laws that, notably, restrict tanning-bed access to adults ≥18 years old. We evaluated artificial tanning behaviours of French teenagers (11-17 years old): sunless-tanning products, sunlamps and artificial tanning beds. An anonymous questionnaire evaluating sunburn history, skin phototype, behaviours with sunless-tanning products and indoor tanning, and parents' behaviours was distributed to students enrolled in two middle and high schools in Antony, a typical city of the middle class French population, located in the Paris suburbs. RESULTS Among 713 teenagers (mean age: 13.5 years: male/female: 1.1) responding, more than half declared that it was important to be tanned during the summer, 1% reported having already used tanning pills, 9.9% tanning creams and 1.4% indoor tanning. Female teenagers significantly more frequently resorted to indoor tanning (P = 0.02), cited the importance of being tanned all year long (P < 0.0001), used tanning pills (P < 0.0001) or tanning creams (P < 0.006), and their parents relied on indoor tanning (P < 0.0001). Profiles of tanning-pill and -cream users were similar. Mean ages for the two groups were comparable. French regulations for indoor tanning seem quite effective. Our analyses revealed a typical teenager profile with sun-exposure risk behaviours, for example, indoor tanning, and use of tanning pills or creams. They could be a selective target for sun-protection information campaigns. © 2012 The Authors. Journal of the European Academy of Dermatology and Venereology © 2012 European Academy of Dermatology and Venereology.

Measurement of Tanning Dependence

PubMed Central

Heckman, C.J.; Darlow, S.; Kloss, J.D.; Cohen-Filipic, J.; Manne, S.L.; Munshi, T.; Yaroch, A.L.; Perlis, C.

2014-01-01

Background Indoor tanning has been found to be addictive. However, the most commonly-used tanning dependence measures have not been well-validated. Objective The study’s purpose was to explore the psychometric characteristics of and compare the mCAGE (modified Cut-down, Annoyed, Guilty, Eye-opener Scale), mDSM-IV-TR (modified Diagnostic and Statistical Manual of Mental Disorders – Fourth Edition - Text Revised), and TAPS (Tanning Pathology Scale) measures of tanning dependence and provide recommendations for research and practice. Methods This study was a cross-sectional online survey with 18–25 year old female university students. The main outcome variable was tanning dependence measured by the mCAGE, mDSM-IV-TR, and TAPS. Results Internal consistency of the TAPS subscales was good but was poor for the mCAGE and mDSM-IV-TR, except when their items were combined. Agreement between the mCAGE and mDSM-IV-TR was fair. Factor analysis of the TAPS confirmed the current four-factor structure. All of the tanning dependence scales were significantly correlated with one another. Likewise, most of the tanning dependence scales were significantly correlated with other measures of tanning attitudes and behaviors. However, the tolerance to tanning TAPS subscale was not significantly correlated with any measure of tanning attitudes or behaviors and had the lowest subscale internal reliability and eigenvalues. Conclusion Based on the data and existing literature, we make recommendations for the continued use of tanning dependence measures. Intervention may be needed for the approximately 5% of college women who tend to be classified as tanning dependent across measures. Monitoring of individuals reporting tanning dependence symptoms is warranted. PMID:23980870

Structure and magnetic properties of spinel-perovskite nanocomposite thin films on SrTiO3 (111) substrates

NASA Astrophysics Data System (ADS)

Kim, Dong Hun; Yang, Junho; Kim, Min Seok; Kim, Tae Cheol

2016-09-01

Epitaxial CoFe2O4-BiFeO3 nanocomposite thin films were synthesized on perovskite structured SrTiO3 (001) and (111) substrates by combinatorial pulsed laser deposition and characterized using scanning electron microscopy, x-ray diffraction, and vibrating sample magnetometer. Triangular BiFeO3 nanopillars were formed in a CoFe2O4 matrix on (111) oriented SrTiO3 substrates, while CoFe2O4 nanopillars with rectangular or square top surfaces grew in a BiFeO3 matrix on (001) substrates. The magnetic hysteresis loops of nanocomposites on (111) oriented SrTiO3 substrates showed isotropic properties due to the strain relaxation while those of films on SrTiO3 (001) substrates exhibited a strong out-of-plane anisotropy originated from shape and strain effects.

Tanning Bed Perception Survey

PubMed Central

Mcquinn, Donna; Lohse, Christine; Hassani, John

2015-01-01

Objective: This study was intended to investigate the perception of tanning bed use among college students. Design: A 15-question survey was given to young adults regarding tanning perceptions. Setting: Rochester Community College in Rochester, Minnesota. Participants: Forty-four respondents between 18 and 51 years of age. Measurements: Data was collected via a self-reported questionnaire. Results: In this study, 50 percent of participants were not educated on the risks of melanoma, and 68 percent were not interested in receiving information on melanoma and completing a follow-up survey. More specifically, 63 percent versus 89 percent of participants with no tanning bed versus some tanning bed use did not want information regarding melanoma, respectively. This study also shows that more tanning bed users believe tanning helps prevent burning than non-tanning bed users. Fifty-seven percent of the 35 participants who had never used a tanning bed thought that they never prevent sunburn, while only 11 percent of the nine participants who had used a tanning bed in the past thought that they never prevent sunburn, which was statistically significant. PMID:25852811

Structural and magnetic analysis of Cu, Co substituted NiFe{sub 2}O{sub 4} thin films

DOE Office of Scientific and Technical Information (OSTI.GOV)

Sharma, Hakikat; Bala, Kanchan; Negi, N. S.

2016-05-23

In the present work we prepared NiFe{sub 2}O{sub 4}, Ni{sub 0.95}Cu{sub 0.05}Fe{sub 2}O{sub 4} and Ni{sub 0.94}Cu{sub 0.05}Co{sub 0.01} Fe{sub 2}O{sub 4} thin films by metallo-organic decomposition method (MOD) using spin coating technique. The thin films were analyzed by X-ray diffractometer (XRD) and Atomic force microscope (AFM) for structural studies. The XRD patterns confirmed the ferrite phase of thin films. From AFM, we analyzed surface morphology, calculated grain size (GS) and root mean square roughness (RMSR). Room temperature magnetic properties were investigated by vibrating sample magnetometer (VSM).

Deposition of Cu-doped PbS thin films with low resistivity using DC sputtering

NASA Astrophysics Data System (ADS)

Soetedjo, Hariyadi; Siswanto, Bambang; Aziz, Ihwanul; Sudjatmoko

2018-03-01

Investigation of the electrical resistivity of Cu-doped PbS thin films has been carried out. The films were prepared using a DC sputtering technique. The doping was achieved by introducing the Cu dopant plate material directly on the surface of the PbS sputtering target plate. SEM-EDX data shows the Cu concentration in the PbS film to be proportional to the Cu plate diameter. The XRD pattern indicates the film is in crystalline cubic form. The Hall effect measurement shows that Cu doping yields an increase in the carrier concentration to 3.55 × 1019 cm-3 and a significant decrease in electrical resistivity. The lowest resistivity obtained was 0.13 Ωcm for a Cu concentration of 18.5%. Preferential orientation of (1 1 1) and (2 0 0) occurs during deposition.

Indoor tanning promotions on social media in six US cities #UVTanning #tanning.

PubMed

Ricklefs, Christine A; Asdigian, Nancy L; Kalra, Heidi L; Mayer, Joni A; Dellavalle, Robert P; Holman, Dawn M; Crane, Lori A

2016-06-01

There is no research investigating indoor tanning advertising on social media. We assessed the use of social media to promote indoor tanning. We subscribed to social media platforms in six US cities and content-analyzed promotional messages received. We captured 662 messages on Twitter and Facebook, through salon emails, and in daily deal coupons. Salon postings were most frequent on Twitter and Facebook, with an average of 2-3 postings per week. National chains posted more frequently than local businesses. Forty percent of messages were devoid of tanning content and included photos, jokes, or popular references. Thirty percent mentioned price reductions, and 28 % referenced an upcoming holiday. Sunless tanning (17 %) was promoted more often than ultraviolet tanning (9 %). Tanning salons actively use social media as a strategy for maintaining relationships with customers and offer pricing deals that promote loyalty and high-frequency tanning.

Fabrication and chemical composition of RF magnetron sputtered Tl-Ca-Ba-Cu-O high Tc superconducting thin films

NASA Technical Reports Server (NTRS)

Subramanyam, G.; Radpour, F.; Kapoor, V. J.; Lemon, G. H.

1990-01-01

The preparation of TlCaBaCuO superconducting thin films on (100) SrTiO3 substrates is described, and the results of their characterization are presented. Sintering and annealing the thin films in a Tl-rich ambient yielded superconductivity with a Tc of 107 K. The results of an XPS study support two possible mechanisms for the creation of holes in the TlCaBaCuO compound: (1) partial substitution of Ca(2+) for Tl(3+), resulting in hole creation, and (2) charge transfer from Tl(3+) to the CuO layers, resulting in a Tl valence between +3 and +1.

A review on polyamide thin film nanocomposite (TFN) membranes: History, applications, challenges and approaches.

PubMed

Lau, W J; Gray, Stephen; Matsuura, T; Emadzadeh, D; Chen, J Paul; Ismail, A F

2015-09-01

This review focuses on the development of polyamide (PA) thin film nanocomposite (TFN) membranes for various aqueous media-based separation processes such as nanofiltration, reverse osmosis and forward osmosis since the concept of TFN was introduced in year 2007. Although the total number of published TFN articles falls far short of the articles of the well-known thin film composite (TFC) membranes, its growth rate is significant, particularly since 2012. Generally, by incorporating an appropriate amount of nanofiller into a thin selective PA layer of a composite membrane, one could produce TFN membranes with enhanced separation characteristics as compared to the conventional TFC membrane. For certain cases, the resulting TFN membranes demonstrate not only excellent antifouling resistance and/or greater antibacterial effect, but also possibly overcome the trade-off effect between water permeability and solute selectivity. Furthermore, this review attempts to give the readers insights into the difficulties of incorporating inorganic nanomaterials into the organic PA layer whose thickness usually falls in a range of several-hundred nanometers. It is also intended to show new possible approaches to overcome these challenges in TFN membrane fabrication. Copyright © 2015 Elsevier Ltd. All rights reserved.

Defect evolution and its impact on the ferromagnetism of Cu-doped ZnO nanocrystals upon thermal treatment: A positron annihilation study

NASA Astrophysics Data System (ADS)

Chen, Zhi-Yuan; Chen, Yuqian; Zhang, Q. K.; Qi, N.; Chen, Z. Q.; Wang, S. J.; Li, P. H.; Mascher, P.

2017-01-01

CuO/ZnO nanocomposites with 4 at. % CuO were annealed in air at various temperatures between 100 and 1200 °C to produce Cu-doped ZnO nanocrystals. X-ray diffraction shows that a CuO phase can be observed in the CuO/ZnO nanocomposites annealed at different temperatures, and the Cu-doped ZnO nanocrystals are identified to be of wurtzite structure. The main peak (101) appears at slightly lower diffraction angles with increasing annealing temperature from 400 up to 1200 °C, which confirms the successful doping of Cu into the ZnO lattice above 400 °C. Scanning electron microscopy indicates that most particles in the CuO/ZnO nanocomposites are isolated when annealing at 100-400 °C, but these particles have a tendency to form clusters or aggregates as the annealing temperature increases from 700 to 1000 °C. Positron annihilation measurements reveal a large number of vacancy defects in the interface region of the nanocomposites, and they are gradually recovered with increasing annealing temperature up to 1000 °C. Room-temperature ferromagnetism can be observed in the CuO/ZnO nanocomposites, and the magnetization decreases continuously with increasing annealing temperature. However, there may be several different origins of ferromagnetism in the CuO/ZnO nanocomposites. At low annealing temperatures, the ferromagnetism originates from the CuO nanograins, and the ferromagnetism of CuO nanograins decreases with an increase in the grain size after subsequent higher temperature annealing, which leads to the weakening of ferromagnetism in the CuO/ZnO nanocomposites. After annealing from 400 to 1000 °C, the ferromagnetism gradually vanishes. The ferromagnetism is probably induced by Cu substitution but is mediated by vacancy defects in the CuO/ZnO nanocomposites. The disappearance of ferromagnetism coincides well with the recovery of vacancy defects. It can be inferred that the ferromagnetism is mediated by vacancy defects that are distributed in the interface region.

Evidence for Cu2-xSe platelets at grain boundaries and within grains in Cu(In,Ga)Se2 thin films

NASA Astrophysics Data System (ADS)

Simsek Sanli, E.; Ramasse, Q. M.; Mainz, R.; Weber, A.; Abou-Ras, D.; Sigle, W.; van Aken, P. A.

2017-07-01

Cu(In,Ga)Se2 (CIGS)-based solar cells reach high power-conversion efficiencies of above 22%. In this work, a three-stage co-evaporation method was used for their fabrication. During the growth stages, the stoichiometry of the absorbers changes from Cu-poor ([Cu]/([In] + [Ga]) < 1) to Cu-rich ([Cu]/([In] + [Ga]) > 1) and finally becomes Cu-poor again when the growth process is completed. It is known that, according to the Cu-In-Ga-Se phase diagram, a Cu-rich growth leads to the presence of Cu2-xSe (x = 0-0.25), which is assumed to assist in recrystallization, grain growth, and defect annihilation in the CIGS layer. So far, Cu2-xSe precipitates with spatial extensions on the order of 10-100 nm have been detected only in Cu-rich CIGS layers. In the present work, we report Cu2-xSe platelets with widths of only a few atomic planes at grain boundaries and as inclusions within grains in a polycrystalline, Cu-poor CIGS layer, as evidenced by high-resolution scanning transmission electron microscopy (STEM). The chemistry of the Cu-Se secondary phase was analyzed by electron energy-loss spectroscopy, and STEM image simulation confirmed the identification of the detected phase. These results represent additional experimental evidence for the proposed topotactical growth model for Cu-Se-assisted CIGS thin-film formation under Cu-rich conditions.

Comparison of the effect of plasma treatment and gamma ray irradiation on PS-Cu nanocomposite films surface

NASA Astrophysics Data System (ADS)

Farag, O. F.

2018-06-01

Polystyrene-copper (PS-Cu) nanocomposite films were treated with DC N2 plasma and gamma rays irradiations. The plasma treatment of PS-Cu film surface was carried out at different treatment times, gas pressure 0.4 Torr and the applied power 3.5 W. On the other hand, the treatment with gamma rays irradiation were carried out at irradiation doses 10, 30 and 50 kGy. The induced changes in surface properties of PS-Cu films were investigated with UV-viss spectroscopy, scanning electron microscopy (SEM) and FTIR spectroscopy techniques. In addition, the wettability property, surface free energy, spreading coefficient and surface roughness of the treated samples were studied by measuring the contact angle. The UV-viss spectroscopy analysis revealed that the optical band gap decreases with increasing the treatment time and the irradiation dose for plasma and gamma treatments, respectively. SEM observations showed that the particle size of copper particles was increased with increasing the treatment time and the irradiation dose, but gamma treatment changes the copper particles size from nano scale to micro scale. The contact angle measurements showing that the wettability property, surface free energy, spreading coefficient and surface roughness of the treated PS-Cu samples were increased remarkably with increasing the treatment time and the irradiation dose for plasma and gamma treatments, respectively. The contact angle, surface free energy, spreading coefficient and surface roughness of the treated PS-Cu samples are more influenced by plasma treatment than gamma treatment.

A novel CuO-N-doped graphene nanocomposite-based hybrid electrode for the electrochemical detection of glucose

NASA Astrophysics Data System (ADS)

Felix, Sathiyanathan; Kollu, Pratap; Jeong, Soon Kwan; Grace, Andrews Nirmala

2017-10-01

We report a catalyst of N-doped graphene CuO nanocomposite, for the non-enzymatic electrocatalytic oxidation of glucose. The hybrid nanocomposite was synthesized by copper sulfate, cetyl ammonium bromide and graphite as starting materials. The synthesized composites were characterized with the techniques like X-ray diffraction, field emission scanning electron microscopy, transmission electron microscope to study the crystalline phase and morphological structure. Based on this composite, a non-enzymatic glucose sensor was constructed. Cyclic voltammetry and chronoamperometry methods were done to investigate the electrocatalytic properties of glucose in alkaline medium. For glucose detection, the fabricated sensor showed a linear response over a wide range of concentration from 3 to 1000 µM, with sensitivity of 2365.7 µA mM-1 cm-2 and a fast response time of 5 s. The designed sensor exhibited negligible current response to the normal concentration of common interferents in the presence of glucose. All these favorable advantages of the fabricated glucose sensor suggest that it may have good potential application in biological samples, food and other related areas.

Influence of support electrolytic in the electrodeposition of CuGaSe thin films

DOE PAGES

Fernandez, A. M.; Turner, J. A.; Lara-Lara, B.; ...

2016-11-02

CuGaSe 2 is an important thin film electronic material that possesses several attributes that make it appealing for solar energy conversion. Because of its properties it can be incorporated in to various devices, among the greatest highlights are photovoltaic cells, as well as its potential use as photocathodes for hydrogen production, via the photoelectrolysis. There are several methods of its preparation, most notably electrodeposition that has the potential for large areas and high volumes. Electrodeposition of ternary and/or quaternary semiconductors generally proceeds via the formation of a binary, which is subsequently reacted to form the ternary compound. Several conditions mustmore » be controlled to form binary compounds that include the use of complexing agents, buffers, temperature, etc. Here, we discuss the effect of anion composition in the electrolytic bath and the type of lithium salts, in order to manipulate the atomic concentration of CuGaSe 2 during the electrodeposition of thin films, yielding copper-rich, gallium-rich or stoichiometric thin films. Finally, we present the results of a study on the morphology and structure obtained using two types of substrates both before and after performing a heat treatment.« less

Influence of support electrolytic in the electrodeposition of CuGaSe thin films

DOE Office of Scientific and Technical Information (OSTI.GOV)

Fernandez, A. M.; Turner, J. A.; Lara-Lara, B.

CuGaSe 2 is an important thin film electronic material that possesses several attributes that make it appealing for solar energy conversion. Because of its properties it can be incorporated in to various devices, among the greatest highlights are photovoltaic cells, as well as its potential use as photocathodes for hydrogen production, via the photoelectrolysis. There are several methods of its preparation, most notably electrodeposition that has the potential for large areas and high volumes. Electrodeposition of ternary and/or quaternary semiconductors generally proceeds via the formation of a binary, which is subsequently reacted to form the ternary compound. Several conditions mustmore » be controlled to form binary compounds that include the use of complexing agents, buffers, temperature, etc. Here, we discuss the effect of anion composition in the electrolytic bath and the type of lithium salts, in order to manipulate the atomic concentration of CuGaSe 2 during the electrodeposition of thin films, yielding copper-rich, gallium-rich or stoichiometric thin films. Finally, we present the results of a study on the morphology and structure obtained using two types of substrates both before and after performing a heat treatment.« less

Effect of annealing on structure, morphology and optoelectronic properties of nanocrystalline CuO thin films

NASA Astrophysics Data System (ADS)

Jundale, D. M.; Pawar, S. G.; Patil, S. L.; Chougule, M. A.; Godse, P. R.; Patil, V. B.

2011-10-01

The nanocrystalline CuO thin films were prepared on glass substrates by the sol-gel method. The structural, morphological, electrical and optical properties of CuO thin films, submitted to an annealing treatment in the 400-700 °C ranges are studied by X-ray diffraction (XRD), Scanning Electron Microscopy (SEM), Four Probe Technique and UV-visible spectroscopic. XRD measurements show that all the films are crystallized in the monoclinic phase and present a random orientation. Four prominent peaks, corresponding to the (110) phase (2θ≈32.70°), (002) phase (2θ≈35.70°), (111) phase (2θ≈38.76°) and (202) phase (2θ≈49.06°) appear on the diffractograms. The crystallite size increases with increasing annealing temperature. These modifications influence the microstructure, electrical and optical properties. The optical band gap energy decreases with increasing annealing temperature. These mean that the optical quality of CuO films is improved by annealing.

Y1Ba2Cu3O(6+delta) growth on thin Y-enhanced SiO2 buffer layers on silicon

NASA Technical Reports Server (NTRS)

Robin, T.; Mesarwi, A.; Wu, N. J.; Fan, W. C.; Espoir, L.; Ignatiev, A.; Sega, R.

1991-01-01

SiO2 buffer layers as thin as 2 nm have been developed for use in the growth of Y1Ba2Cu3O(6+delta) thin films on silicon substrates. The SiO2 layers are formed through Y enhancement of silicon oxidation, and are highly stoichiometric. Y1Ba2Cu3O(6+delta) film growth on silicon with thin buffer layers has shown c orientation and Tc0 = 78 K.

'My friends love to tan': examining sensation seeking and the mediating role of association with friends who use tanning beds on tanning bed use intentions.

PubMed

Banerjee, Smita C; Greene, Kathryn; Bagdasarov, Zhanna; Campo, Shelly

2009-12-01

This paper explored how sensation seeking contributes to the likelihood of tanning bed use intentions both directly and indirectly through the way it shapes interaction with peers who use tanning beds and attitudes toward tanning bed. Eight hundred and ninety six (n = 896) male and female college students were recruited for the study. Measured variables included sensation seeking, association with friends who use tanning beds, attitudes toward tanning and tanning bed use intentions. Structural equation modeling was performed to test the hypotheses. In general, results supported the proposed hypotheses and documented that sensation seeking is indirectly associated with tanning bed use intentions through the mediation of association with peers who use tanning beds and attitudes toward tanning. The article discusses theoretical and methodological implications of the findings demonstrating the pathways of influence of sensation seeking on tanning bed use intentions.

Development of novel nano-composite membranes as introduction systems for mass spectrometers: Contrasting nano-composite membranes and conventional inlet systems

NASA Astrophysics Data System (ADS)

Miranda, Luis Diego

This dissertation presents the development of novel nano-composite membranes as introduction systems for mass spectrometers. These nano-composite membranes incorporate anodic aluminum oxide (AAO) membranes as templates that can be used by themselves or modified by a variety of chemical deposition processes. Two types of nano-composite membranes are presented. The first nano-composite membrane has carbon deposited within the pores of an AAO membrane. The second nano-composite membrane is made by coating an AAO membrane with a thin polymer film. The following chapters describe the transmission properties these nano-composite membranes and compare them to conventional mass spectrometry introduction systems. The nano- composite membranes were finally coupled to the inlet system of an underwater mass spectrometer revealing their utility in field deployments.

Direct Growth of CuO Nanorods on Graphitic Carbon Nitride with Synergistic Effect on Thermal Decomposition of Ammonium Perchlorate.

PubMed

Tan, Linghua; Xu, Jianhua; Li, Shiying; Li, Dongnan; Dai, Yuming; Kou, Bo; Chen, Yu

2017-05-02

Novel graphitic carbon nitride/CuO (g-C₃N₄/CuO) nanocomposite was synthesized through a facile precipitation method. Due to the strong ion-dipole interaction between copper ions and nitrogen atoms of g-C₃N₄, CuO nanorods (length 200-300 nm, diameter 5-10 nm) were directly grown on g-C₃N₄, forming a g-C₃N₄/CuO nanocomposite, which was confirmed via X-ray diffraction (XRD), transmission electron microscopy (TEM), field emission scanning electron microscopy (FESEM), and X-ray photoelectron spectroscopy (XPS). Finally, thermal decomposition of ammonium perchlorate (AP) in the absence and presence of the prepared g-C₃N₄/CuO nanocomposite was examined by differential thermal analysis (DTA), and thermal gravimetric analysis (TGA). The g-C₃N₄/CuO nanocomposite showed promising catalytic effects for the thermal decomposition of AP. Upon addition of 2 wt % nanocomposite with the best catalytic performance (g-C₃N₄/20 wt % CuO), the decomposition temperature of AP was decreased by up to 105.5 °C and only one decomposition step was found instead of the two steps commonly reported in other examples, demonstrating the synergistic catalytic activity of the as-synthesized nanocomposite. This study demonstrated a successful example regarding the direct growth of metal oxide on g-C₃N₄ by ion-dipole interaction between metallic ions, and the lone pair electrons on nitrogen atoms, which could provide a novel strategy for the preparation of g-C₃N₄-based nanocomposite.

A cross-sectional study examining the correlation between sunless tanning product use and tanning beliefs and behaviors.

PubMed

Sahn, Rachel E; McIlwain, Mary Jayne; Magee, Kristin H; Veledar, Emir; Chen, Suephy C

2012-04-01

To establish the effect of sunless tanning products on tanning behaviors and to determine characteristics of sunless tanning product users. A cross-sectional survey study conducted between May 30, 2007, and December 4, 2007. The Emory University campus and surrounding locations in Atlanta, Georgia. Four hundred fifteen community and university-affiliated women. Self-reported use of sunless tanning products and UV radiation tanning methods. Forty-eight percent of participants had used sunless tanning products, 70.6% had tanned in the sun, and 26.0% had used tanning beds at least once in the past year. Most participants (92.7%) believed that tanned skin is more attractive than untanned skin, and 79.2% reported feeling better about themselves when tan. Many sunless tanning product users reported decreased frequency of tanning in the sun (36.8%) or in tanning beds (38%) because of product use. Frequent users were more likely to have decreased their UV radiation exposure. Lighter complexion, frequent use of UV radiation tanning methods, feeling better about oneself when tan, and having a history of skin cancer were independently associated with sunless tanning product use. The desire for tanned skin remains strong despite growing awareness of the dangers of UV radiation exposure. In some women, sunless tanning product use is associated with decreased UV radiation tanning frequency, especially in women who use them repeatedly. Improvements in the appearance of sunless tanning product tans may allow wider acceptance by the public and further decreases in UV radiation tanning practices.

Microstructures and properties of superconducting Y-ErBaCuO thin films obtained from disordered Y-ErBaF2Cu films

NASA Technical Reports Server (NTRS)

Cikmach, P.; Diociaiuti, M.; Fontana, A.; Giovannella, C.; Iannuzzi, M.; Lucchini, C.; Merlo, V.; Messi, R.; Paoluzi, L.; Scopa, L.

1991-01-01

The preparation procedure used to obtain superconducting thin films by radio frequency magnetron sputtering of a single mosaic target is described in detail. The single mosaic target is composed of (Y-Er), BaF2, and Cu.

Unified equivalent circuit model for carbon nanotube-based nanocomposites.

PubMed

Zhao, Chaoyang; Yuan, Weifeng; Zhao, Yangzhou; Hu, Ning; Gu, Bin; Liu, Haidong; Alamusi

2018-07-27

Carbon nanotubes form a complex network in nanocomposites. In the network, the configuration of the nanotubes is various. A carbon nanotube may be curled or straight, and it may be parallel or crossed to another. As a result, carbon nanotube-based composites exhibit integrated characteristics of inductor, capacitor and resistor. In this work, it is hypothesised that carbon nanotube-based composites all adhere to a RLC interior circuit. To verify the hypothesis, three different composites, viz multi-walled carbon nanotube/polyvinylidene fluoride (MWCNT/PVDF), multi-walled carbon nanotube/epoxy (MWCNT/EP), multi-walled carbon nanotube/polydimethylsiloxane (MWCNT/PDMS) were fabricated and tested. The resistances and the dielectric loss tangent (tanδ) of the materials were measured in direct and alternating currents. The measurement shows that the value of tanδ is highly affected by the volume fraction of MWCNT in the composites. The experimental results prove that the proposed RLC equivalent circuit model can fully describe the electrical properties of the MWCNT network in nanocomposites. The RLC model provides a new route to detect the inductance and capacitance of carbon nanotubes. Moreover, the model also indicates that the carbon nanotube-based composite films may be used to develop wireless strain sensors.

Dramatically enhanced non-Ohmic properties and maximum stored energy density in ceramic-metal nanocomposites: CaCu3Ti4O12/Au nanoparticles

PubMed Central

2013-01-01

Non-Ohmic and dielectric properties of a novel CaCu3Ti4O12/Au nanocomposite were investigated. Introduction of 2.5 vol.% Au nanoparticles in CaCu3Ti4O12 ceramics significantly reduced the loss tangent while its dielectric permittivity remained unchanged. The non-Ohmic properties of CaCu3Ti4O12/Au (2.5 vol.%) were dramatically improved. A nonlinear coefficient of ≈ 17.7 and breakdown electric field strength of 1.25 × 104 V/m were observed. The maximum stored energy density was found to be 25.8 kJ/m3, which is higher than that of pure CaCu3Ti4O12 by a factor of 8. Au addition at higher concentrations resulted in degradation of dielectric and non-Ohmic properties, which is described well by percolation theory. PMID:24257060

The influence of different locations of sputter guns on the morphological and structural properties of Cu-In-Ga precursors and Cu(In,Ga)Se2 thin films

NASA Astrophysics Data System (ADS)

Wang, J.; Zhu, J.; He, Y. X.

2014-01-01

The influence of two different locations of sputter guns on the morphological and structural properties of Cu-In-Ga precursors and Cu(In,Ga)Se2 (CIGS) thin films was investigated. All the precursors contained cauliflower-like nodules, whereas smaller subnodules were observed on the background. All the precursors revealed apparent three-layered structures, and voids were observed at the CIGS/SLG interface of Sets 1 and 2 films rather than Set 3 film. EDS results indicated that all CIGS thin films were Cu-deficient. Based on the grazing incidence X-ray diffraction (GIXRD) patterns, as-selenized films showed peaks corresponding to the chalcopyrite-type CIGS structure. Depth-resolved Raman spectra showed the formation of a dominant CIGS phase inside the films for all the as-selenized samples investigated, and of an ordered vacancy compound (OVC) phase like Cu(In,Ga)3Se5 or Cu(In,Ga)2Se3.5 at the surface and/or CIGS/SLG interface region of Sets 2 and 3 films. No evidence was obtained on the presence of an OVC phase in Set 1 CIGS film, which may be speculated that long-time annealing is contributed to suppress the growth of OVC phases. The results of the present work suggest that the metallic precursors deposited with the upright-location sputter gun might be more appropriate to prepare CIGS thin films than those sputtered with the titled-location gun.

Development of sputtered CuSbS2 thin films grown by sequential deposition of binary sulfides

NASA Astrophysics Data System (ADS)

Medina-Montes, M. I.; Vieyra-Brito, O.; Mathews, N. R.; Mathew, X.

2018-05-01

In this work, CuSbS2 thin films were developed by annealing binary precursors deposited sequentially by rf magnetron sputtering. The recrystallization process was optimized and the films were extensively characterized using a number of tools such as XRD, Raman, SEM, energy dispersive x-ray spectroscopy, atomic force microscopy, Hall, UV–vis spectroscopy, Ellipsometry, Seebeck, and photoresponse. The influence of annealing temperature on the structure, morphology, elemental composition, optical and electrical properties are reported. Annealing below 350 °C resulted in famatinite (Cu3SbS4) and chalcostibite (CuSbS2) ternaries as well as binary phases. Phase-pure chalcostibite was obtained in the range of 350 °C–375 °C. At 400 °C, although CuSbS2 was predominant, tetrahedrite phase (Cu12Sb4S13) appeared as an additional phase. The elemental composition of the films was slightly sulfur deficient, and the atomic percentages of Cu, Sb and S showed a dependence on annealing temperature. The material properties of the phase-pure CuSbS2 thin films are: optical band gap in the range of 1.5–1.62 eV, absorption coefficient close to 105 cm‑1, atomic ratios of Cu/Sb ∼1 and (Cu + Sb)/S ∼1.2, crystal size 18.3–24.5 nm and grain size 50–300 nm. The films were photo-sensitive, showed p-type semiconductor behavior. Electrical resistivity, carrier density and hole mobility were 94–459 Ω cm, 1.6–7.0 × 1015 cm‑3 and 8.4–9.5 cm2 V‑1 s respectively.

Hydrothermal synthesis of bacterial cellulose-copper oxide nanocomposites and evaluation of their antimicrobial activity.

PubMed

Araújo, Inês M S; Silva, Robson R; Pacheco, Guilherme; Lustri, Wilton R; Tercjak, Agnieszka; Gutierrez, Junkal; Júnior, José R S; Azevedo, Francisco H C; Figuêredo, Girlene S; Vega, Maria L; Ribeiro, Sidney J L; Barud, Hernane S

2018-01-01

In this work, for the first time bacterial cellulose (BC) hydrogel membranes were used for the fabrication of antimicrobial cellulosic nanocomposites by hydrothermal deposition of Cu derivative nanoparticles (i.e.Cu(0) and CuxOy species). BC-Cu nanocomposites were characterized by FTIR, SEM, AFM, XRD and TGA, to study the effect of hydrothermal processing time on the final physicochemical properties of final products. XRD result show that depending on heating time (3-48h), different CuxOy phases were achieved. SEM and AFM analyses unveil the presence of the Cu(0) and copper CuxOy nanoparticles over BC fibrils while the surface of 3D network became more compact and smother for longer heating times. Furthermore, the increase of heating time placed deleterious effect on the structure of BC network leading to decrease of BC crystallinity as well as of the on-set degradation temperature. Notwithstanding, BC-Cu nanocomposites showed excellent antimicrobial activity against E. coli, S. aureus and Salmonella bacteria suggesting potential applications as bactericidal films. Copyright © 2017 Elsevier Ltd. All rights reserved.

Rheology of polyaniline-dinonylnaphthalene disulfonic acid (DNNDSA) montmorillonite clay nanocomposites in the sol state: shear thinning versus pseudo-solid behavior.

PubMed

Garai, Ashesh; Nandi, Arun K

2008-04-01

The melt rheology of polyaniline (PANI)-dinonylnaphthalenedisulfonic acid (DNNDSA) gel nanocomposites (GNCs) with organically modified (modified with cetyl trimethylammonium bromide)-montmorillonite (om-MMT) clay has been studied for three different clay concentrations at the temperature range 120-160 degrees C. Field emission scanning electron microscopy (FE-SEM), wide angle X-ray scattering (WAXS), differential scanning calorimetry (DSC) and dc-conductivity data (approximately 10(-3) S/cm) indicate that the PANI-DNNDSA melt is in sol state and it is not de-doped at that condition. The WAXS data indicate that in GNC-1 sol clay tactoids are in exfoliated state but in the other sols they are in intercalated state. The zero shear viscosity (eta0), storage modulus (G') and loss modulus (G") increase than that of pure gel in the GNCs. The pure sol and the sols of gel nanocomposites (GNCs) exhibit Newtonian behavior for low shear rate (< 6 x 10(-3) s(-1)) and power law variation for the higher shear rate region. The characteristic time (A) increase with increasing clay concentration and the power law index (n) decreases with increase in clay concentration in the GNCs indicating increased shear thinning for the clay addition. Thus the sols of om-clay nanocomposites of PANI-DNNDSA system are easily processible. The storage modulus (G') of GNC sols are higher than that of pure PANI-DNNDSA sol, GNC1 sol shows a maximum of 733% increase in storage modulus and the percent increase decreases with increase in temperature. Exfoliated nature of clay tactoids has been attributed for the above dramatic increase of G'. The PANI-DNNDSA sol nanocomposites behave as a pseudo-solid at higher frequency where G' and loss modulus (G") show a crossover point in the frequency sweep experiment at a fixed temperature. The crossover frequency decreases with increase in clay concentration and it increases with increase in temperature for GNC sols. The pseudo-solid behavior has been explained

Detection of Cu2Zn5SnSe8 and Cu2Zn6SnSe9 phases in co-evaporated Cu2ZnSnSe4 thin-films

NASA Astrophysics Data System (ADS)

Schwarz, Torsten; Marques, Miguel A. L.; Botti, Silvana; Mousel, Marina; Redinger, Alex; Siebentritt, Susanne; Cojocaru-Mirédin, Oana; Raabe, Dierk; Choi, Pyuck-Pa

2015-10-01

Cu2ZnSnSe4 thin-films for photovoltaic applications are investigated using combined atom probe tomography and ab initio density functional theory. The atom probe studies reveal nano-sized grains of Cu2Zn5SnSe8 and Cu2Zn6SnSe9 composition, which cannot be assigned to any known phase reported in the literature. Both phases are considered to be metastable, as density functional theory calculations yield positive energy differences with respect to the decomposition into Cu2ZnSnSe4 and ZnSe. Among the conceivable crystal structures for both phases, a distorted zinc-blende structure shows the lowest energy, which is a few tens of meV below the energy of a wurtzite structure. A band gap of 1.1 eV is calculated for both the Cu2Zn5SnSe8 and Cu2Zn6SnSe9 phases. Possible effects of these phases on solar cell performance are discussed.

Electrical contacts to thin layers of Bi2Sr2CaCu2O8+δ

NASA Astrophysics Data System (ADS)

Suzuki, Shota; Taniguchi, Hiroki; Kawakami, Tsukasa; Cosset-Cheneau, Maxen; Arakawa, Tomonori; Miyasaka, Shigeki; Tajima, Setsuko; Niimi, Yasuhiro; Kobayashi, Kensuke

2018-05-01

Thin layers of Bi2Sr2CaCu2O8+δ (Bi2212) were fabricated using the mechanical exfoliation technique. Good electrical contacts to the thin Bi2212 films with low contact resistance were realized by depositing Ag and Au electrodes onto the Bi2212 films and annealing them with an oxygen flow at 350 °C for 30 min. We observed cross-section images of the Bi2212 thin film device using a transmission electron microscope to characterize the diffusion of Ag and Au atoms into the Bi2212 thin film.

Tanning Salon Compliance Rates in States With Legislation to Protect Youth Access to UV Tanning.

PubMed

Williams, Melissa S; Buhalog, Brittany; Blumenthal, Laura; Stratman, Erik J

2018-01-01

The US Food and Drug Administration has classified tanning beds as carcinogenic. Most states have enacted legislation to prevent or create barriers for minors accessing tanning establishments. Determining tanning salon compliance with legislation would provide an indication of the influence of legislation at preventing exposure to the carcinogen in minors. To investigate compliance rates in the 42 states and the District of Columbia with legislation restricting tanning bed use in minors and to identify differences in compliance based on population, regional location, salon ownership, age group being regulated, and time since the law was enacted. This investigation was a cross-sectional telephone survey conducted between February 1, 2015, and April 30, 2016, by callers posing as minors attempting to schedule a tanning appointment. The setting was tanning salons in the 42 states and the District of Columbia that currently have legislation restricting tanning bed use in minors. Included in the study were 427 tanning salons, 10 randomly selected from each state or territory with tanning legislation. Overall compliance of tanning salons with state tanning legislation and differences in compliance based on community population, regional location, independent vs chain tanning salon, age group being regulated, and time since the law was enacted. Of the 427 tanning salons surveyed, overall noncompliance with state legislation was 37.2% (n = 159). There were more noncompliant tanning salons in rural locations (45.5%; 95% CI, 37.5%-53.7%; P = .009), southern regions of the United States (49.4%; 95% CI, 41.4%-57.4%; P = .001), independently owned salons (43.9%; 95% CI, 37.3%-50.6%; P = .003), states with younger age groups being regulated (53.5%; 95% CI, 45.7%-61.2%; P < .001), and states with more than one tanning regulation (50.0%; 95% CI, 42.0%-58.0%; P < .001). No difference was found based on time since the law was enacted. Compliance with state

Reinforced fluropolymer nanocomposites with high-temperature superconducting Bi2Sr2CaCu2Oy

NASA Astrophysics Data System (ADS)

Jayasree, T. K.

2014-10-01

Bismuth Strontium Calcium Copper Oxide (Bi2Sr2CaCu2Oy)/Polyvinylidene fluoride (PVDF) nanocomposite was prepared and their thermal properties were analyzed. The composite consists of the polyvinylidene fluoride (PVDF) as an insulating polymer matrix, and homogenously distributed Bismuth strontium calcium copperoxide (2212) nanoparticles. SEM data shows flaky grains of the superconductor coated and linked by polymer. Differential scanning calorimetry (DSC) results indicated that the melting point was not affected significantly by the addition of BSCCO. However, the addition of superconducting ceramic resulted in an extra melting peak at a lower temperature (145°C). Thermogravimetric analysis of the samples shows that the onset decomposition temperature of the PVDF matrix was decreased by the addition of SC filler.

Preparation of CuIn{sub x}Ga{sub 1{minus}x}Se{sub 2} thin films on Si substrates

DOE Office of Scientific and Technical Information (OSTI.GOV)

Yamamoto, Yukio; Yamaguchi, Toshiyuki; Suzuki, Masayoshi

For fabricating efficient tandem solar cells, CuIn{sub x}Ga{sub 1{minus}x}Se{sub 2} thin films have been prepared on Si(100), Si(110) and Si(111) substrates in the temperature range (R.T.{approximately}400 C) by rf sputtering. From EPMA analysis, these sputtered thin films are found to be nearly stoichiometric over the whole substrate temperature range, irrespective of the azimuth plane of the Si substrate. XPS studies showed that the compositional depth profile in these thin films is uniform. X-ray diffraction analysis indicated that all the thin films had a chalcopyrite structure. CuIn{sub x}Ga{sub 1{minus}x}Se{sub 2} thin films were strongly oriented along the (112) plane with increasingmore » the substrate temperature, independent of the azimuth plane of the Si substrate, suggesting the larger grain growth.« less

Strong temperature-dependent crystallization, phase transition, optical and electrical characteristics of p-type CuAlO2 thin films.

PubMed

Liu, Suilin; Wu, Zhiheng; Zhang, Yake; Yao, Zhiqiang; Fan, Jiajie; Zhang, Yiqiang; Hu, Junhua; Zhang, Peng; Shao, Guosheng

2015-01-07

We report here a reliable and reproducible single-step (without post-annealing) fabrication of phase-pure p-type rhombohedral CuAlO2 (r-CuAlO2) thin films by reactive magnetron sputtering. The dependence of crystallinity and phase compositions of the films on the growth temperature was investigated, revealing that highly-crystallized r-CuAlO2 thin films could be in situ grown in a narrow temperature window of ∼940 °C. Optical and electrical property studies demonstrate that (i) the films are transparent in the visible light region, and the bandgaps of the films increased to ∼3.86 eV with the improvement of crystallinity; (ii) the conductance increased by four orders of magnitude as the film was evolved from the amorphous-like to crystalline structure. The predominant role of crystallinity in determining CuAlO2 film properties was demonstrated to be due to the heavy anisotropic characteristics of the O 2p-Cu 3d hybridized valence orbitals.

Cu doping concentration effect on the physical properties of CdS thin films obtained by the CBD technique

NASA Astrophysics Data System (ADS)

Albor Aguilera, M. L.; Flores Márquez, J. M.; Remolina Millan, A.; Matsumoto Kuwabara, Y.; González Trujillo, M. A.; Hernández Vásquez, C.; Aguilar Hernandez, J. R.; Hernández Pérez, M. A.; Courel-Piedrahita, M.; Madeira, H. T. Yee

2017-08-01

Cu(In, Ga)Se2 (CIGS) and Cu2ZnSnS4 (CZTS) semiconductors are direct band gap materials; when these types of material are used in solar cells, they provide efficiencies of 22.1% and 12.6%, respectively. Most traditional fabrication methods involve expensive vacuum processes including co-evaporation and sputtering techniques, where films and doping are conducted separately. On the other hand, the chemical bath deposition (CBD) technique allows an in situ process. Cu-doped CdS thin films working as a buffer layer on solar cells provide good performing devices and they may be deposited by low cost techniques such as chemical methods. In this work, Cu-doped CdS thin films were deposited using the CBD technique on SnO2:F (FTO) substrates. The elemental analysis and mapping reconstruction were conducted by EDXS. Morphological, optical and electrical properties were studied, and they revealed that Cu doping modified the CdS structure, band-gap value and the electrical properties. Cu-doped CdS films show high resistivity compared to the non-doped CdS. The appropriate parameters of Cu-doped CdS films were determined to obtain an adequate window or buffer layer on CIGS and CZTS photovoltaic solar cells.

Sequentially evaporated thin film YBa2Cu3O(7-x) superconducting microwave ring resonator

NASA Technical Reports Server (NTRS)

Rohrer, Norman J.; To, Hing Y.; Valco, George J.; Bhasin, Kul B.; Chorey, Chris; Warner, Joseph D.

1990-01-01

There is great interest in the application of thin film high temperature superconductors in high frequency electronic circuits. A ring resonator provides a good test vehicle for assessing the microwave losses in the superconductor and for comparing films made by different techniques. Ring resonators made of YBa2Cu3O(7-x) have been investigated on LaAlO3 substrates. The superconducting thin films were deposited by sequential electron beam evaporation of Cu, Y, and BaF2 with a post anneal. Patterning of the superconducting film was done using negative photolithography. A ring resonator was also fabricated from a thin gold film as a control. Both resonators had a gold ground plane on the backside of the substrate. The ring resonators' reflection coefficients were measured as a function of frequency from 33 to 37 GHz at temperatures ranging from 20 K to 68 K. The resonator exhibited two resonances which were at 34.5 and 35.7 GHz at 68 K. The resonant frequencies increased with decreasing temperature. The magnitude of the reflection coefficients was in the calculation of the unloaded Q-values. The performance of the evaporated and gold resonator are compared with the performance of a laser ablated YBa2Cu3O(7-x) resonator. The causes of the double resonance are discussed.

Toward quantifying the abuse liability of ultraviolet tanning: A behavioral economic approach to tanning addiction.

PubMed

Reed, Derek D; Kaplan, Brent A; Becirevic, Amel; Roma, Peter G; Hursh, Steven R

2016-07-01

Many adults engage in ultraviolet indoor tanning despite evidence of its association with skin cancer. The constellation of behaviors associated with ultraviolet indoor tanning is analogous to that in other behavioral addictions. Despite a growing literature on ultraviolet indoor tanning as an addiction, there remains no consensus on how to identify ultraviolet indoor tanning addictive tendencies. The purpose of the present study was to translate a behavioral economic task more commonly used in substance abuse to quantify the "abuse liability" of ultraviolet indoor tanning, establish construct validity, and determine convergent validity with the most commonly used diagnostic tools for ultraviolet indoor tanning addiction (i.e., mCAGE and mDSM-IV-TR). We conducted a between-groups study using a novel hypothetical Tanning Purchase Task to quantify intensity and elasticity of ultraviolet indoor tanning demand and permit statistical comparisons with the mCAGE and mDSM-IV-TR. Results suggest that behavioral economic demand is related to ultraviolet indoor tanning addiction status and adequately discriminates between potential addicted individuals from nonaddicted individuals. Moreover, we provide evidence that the Tanning Purchase Task renders behavioral economic indicators that are relevant to public health research. The present findings are limited to two ultraviolet indoor tanning addiction tools and a relatively small sample of high-risk ultraviolet indoor tanning users; however, these pilot data demonstrate the potential for behavioral economic assessment tools as diagnostic and research aids in ultraviolet indoor tanning addiction studies. © 2016 Society for the Experimental Analysis of Behavior.

Investigation of anticorrosion properties of nanocomposites of spray coated zinc oxide and titanium dioxide thin films on stainless steel (304L SS) in saline environment

NASA Astrophysics Data System (ADS)

P, Muhamed Shajudheen V.; S, Saravana Kumar; V, Senthil Kumar; Maheswari A, Uma; M, Sivakumar; Rani K, Anitha

2018-01-01

The present study reports the anticorrosive nature of nanocomposite thin films of zinc oxide and titanium dioxide on steel substrate (304L SS) using spray coating method. The morphology and chemical constituents of the nanocomposite thin film were characterized by field effect scanning electron microscopy and energy dispersive analysis of x-ray (EDAX) studies. From the EDAX studies, it was observed that nanocomposite coatings of desired stoichiometry can be synthesized using present coating technique. The cyclic voltametric techniques such as Tafel analysis and electrochemical impedance spectroscopy (EIS) analysis were conducted to study the anticorrosion properties of the coatings. The E corr values obtained from Tafel polarization curves of the sample coated with nanocomposites of ZnO and TiO2 in different ratios (5:1, 1:1 and 1:5) indicated that the corrosion resistance was improved compared to bare steel. The coating resistance values obtained from the Nyquist plot after fitting with equivalent circuit confirmed the improved anticorrosion performance of the coated samples. The sample coated with ZnO: TiO2 in the ratio 1:5 showed better corrosion resistance compared to other ratios. The Tafel and EIS studies were repeated after exposure to 5% NaCl for 390 h and the results indicated the anticorrosive nature of the coating in the aggressive environment. The root mean square deviation of surface roughness values calculated from the AFM images before and after salt spray indicated the stability of coating in the saline environment.

CuCr2O4@rGO Nanocomposites as High-Performance Cathode Catalyst for Rechargeable Lithium-Oxygen Batteries

NASA Astrophysics Data System (ADS)

Liu, Jiandi; Zhao, Yanyan; Li, Xin; Wang, Chunge; Zeng, Yaping; Yue, Guanghui; Chen, Qiang

2018-06-01

Rechargeable lithium-oxygen batteries have been considered as a promising energy storage technology because of their ultra-high theoretical energy densities which are comparable to gasoline. In order to improve the electrochemical properties of lithium-oxygen batteries (LOBs), especially the cycling performance, a high-efficiency cathode catalyst is the most important component. Hence, we aim to demonstrate that CuCr2O4@rGO (CCO@rGO) nanocomposites, which are synthesized using a facile hydrothermal method and followed by a series of calcination processes, are an effective cathode catalyst. The obtained CCO@rGO nanocomposites which served as the cathode catalyst of the LOBs exhibited an outstanding cycling performance for over 100 cycles with a fixed capacity of 1000 mAh g-1 at a current density of 200 mA g-1. The enhanced properties were attributed to the synergistic effect between the high catalytic efficiency of the spinel-structured CCO nanoparticles, the high specific surface area, and high conductivity of the rGO.[Figure not available: see fulltext.

Chemical spray pyrolyzed kesterite Cu2ZnSnS4 (CZTS) thin films

NASA Astrophysics Data System (ADS)

Khalate, S. A.; Kate, R. S.; Deokate, R. J.

2018-04-01

Pure kesterite phase thin films of Cu2ZnSnS4 (CZTS) were synthesized at different substrate temperatures using sulphate precursors by spray pyrolysis method. The significance of synthesis temperature on the structural, morphological and optical properties has been studied. The X-ray analysis assured that synthesized CZTS thin films showing pure kesterite phase. The value of crystallite size was found maximum at the substrate temperature 400 °C. At the same temperature, microstructural properties such as dislocation density, micro-strain and stacking fault probability were found minimum. The morphological examination designates the development of porous and uniform CZTS thin films. The synthesized CZTS thin films illustrate excellent optical absorption (105 cm-1) in the visible band and the optical band gap varies in the range of 1.489 eV to 1.499 eV.

Incorporation of layered double nanomaterials in thin film nanocomposite nanofiltration membrane for magnesium sulphate removal

NASA Astrophysics Data System (ADS)

Hanis Tajuddin, Muhammad; Yusof, Norhaniza; Salleh, Wan Norharyati Wan; Fauzi Ismail, Ahmad; Hanis Hayati Hairom, Nur; Misdan, Nurasyikin

2018-03-01

Thin film nanocomposite (TFN) membrane with copper-aluminium layered double hydroxides (LDH) incorporated into polyamide (PA) selective layer has been prepared for magnesium sulphate salt removal. 0, 0.05, 0.1, 0.15, 0.2 wt% of LDH were dispersed in the trimesoyl chloride (TMC) in n-hexane as organic solution and embedded into PA layer during interfacial polymerization with piperazine. The fabricated membranes were further characterized to evaluate its morphological structure and membrane surface hydrophilicity. The TFN membranes performance were evaluated with divalent salt magnesium sulphate (MgSO4) removal and compared with thin film composite (TFC). The morphological structures of TFN membranes were altered and the surface hydrophilicity were enhanced with addition of LDH. Incorporation of LDH has improved the permeate water flux by 82.5% compared to that of TFC membrane with satisfactory rejection of MgSO4. This study has experimentally validated the potential of LDH to improve the divalent salt separation performance for TFN membranes.

Back surface studies of Cu(In,Ga)Se2 thin film solar cells

NASA Astrophysics Data System (ADS)

Simchi, Hamed

Cu(In,Ga)Se2 thin film solar cells have attracted a lot of interest because they have shown the highest achieved efficiency (21%) among thin film photovoltaic materials, long-term stability, and straightforward optical bandgap engineering by changing relative amounts of present elements in the alloy. Still, there are several opportunities to further improve the performance of the Cu(In,Ga)Se2 devices. The interfaces between layers significantly affect the device performance, and knowledge of their chemical and electronic structures is essential in identifying performance limiting factors. The main goal of this research is to understand the characteristics of the Cu(In,Ga)Se2-back contact interface in order to design ohmic back contacts for Cu(In,Ga)Se2-based solar cells with a range of band gaps and device configurations. The focus is on developing either an opaque or transparent ohmic back contact via surface modification or introduction of buffer layers in the back surface. In this project, candidate back contact materials have been identified based on modeling of band alignments and surface chemical properties of the absorber layer and back contact. For the first time, MoO3 and WO 3 transparent back contacts were successfully developed for Cu(In,Ga)Se 2 solar cells. The structural, optical, and surface properties of MoO 3 and WO3 were optimized by controlling the oxygen partial pressure during reactive sputtering and post-deposition annealing. Valence band edge energies were also obtained by analysis of the XPS spectra and used to characterize the interface band offsets. As a result, it became possible to illuminate of the device from the back, resulting in a recently developed "backwall superstrate" device structure that outperforms conventional substrate Cu(In,Ga)Se2 devices in the absorber thickness range 0.1-0.5 microm. Further enhancements were achieved by introducing moderate amounts of Ag into the Cu(In,Ga)Se2 lattice during the co-evaporation method

Synthesis of KMnO4-treated magnetic graphene oxide nanocomposite (Fe3O4@GO/MnO x ) and its application for removing of Cu2+ ions from aqueous solution

NASA Astrophysics Data System (ADS)

Zhang, Huining; Chang, Qing; Jiang, Yu; Li, Huili; Yang, Yahong

2018-04-01

A magnetic KMnO4-treated graphene-oxide-based nanocomposite, Fe3O4@GO/MnO x , was synthesized through a facile hydrothermal technique. The properties of the Fe3O4@GO/MnO x nanocomposite were characterized by SEM, XRD and FTIR. Batch experiments showed that the maximum adsorption capacity calculated by the Langmuir model for Cu2+ was 62.65 mg g-1 at T = 303.15 K. Kinetics and XPS analysis also revealed that the mechanism of Cu2+ removal was mainly a chemical adsorption process involving both the MnO x particles and oxygen functional groups. The prepared Fe3O4@GO/MnO x was found to be an ideal adsorbent for the removal of Cu2+ ions due to the MnO x particle coating, and was easily separated using a magnetic field after utilization. Reusability studies imply that Fe3O4@GO/MnO x is a suitable material for heavy metal ion removal from aqueous solutions in real applications.

Nanocomposites of polyimide and mixed oxide nanoparticles for high performance nanohybrid gate dielectrics in flexible thin film transistors

NASA Astrophysics Data System (ADS)

Kim, Ju Hyun; Hwang, Byeong-Ung; Kim, Do-Il; Kim, Jin Soo; Seol, Young Gug; Kim, Tae Woong; Lee, Nae-Eung

2017-05-01

Organic gate dielectrics in thin film transistors (TFTs) for flexible display have advantages of high flexibility yet have the disadvantage of low dielectric constant (low- k). To supplement low- k characteristics of organic gate dielectrics, an organic/inorganic nanocomposite insulator loaded with high- k inorganic oxide nanoparticles (NPs) has been investigated but high loading of high- k NPs in polymer matrix is essential. Herein, compositing of over-coated polyimide (PI) on self-assembled (SA) layer of mixed HfO2 and ZrO2 NPs as inorganic fillers was used to make dielectric constant higher and leakage characteristics lower. A flexible TFT with lower the threshold voltage and high current on/off ratio could be fabricated by using the hybrid gate dielectric structure of the nanocomposite with SA layer of mixed NPs on ultrathin atomic-layer deposited Al2O3. [Figure not available: see fulltext.

Average current per vacuum-arc cathode spot and spot velocity in a magnetic field on a CuCr50/50 nanocomposite

NASA Astrophysics Data System (ADS)

Zabello, K. K.; Poluyanova, I. N.; Yakovlev, V. V.; Shkol'nik, S. M.

2017-11-01

It has been shown that such cathode spot characteristics as the average current per spot and its dependence on tangential magnetic-field induction B t and the spot velocity and its dependence on B t for two CuCr50/50 specimens with very different structures (nanocomposite and "solid-state sintered" composite) almost coincide if the surface of contacts has been totally remelted before measurements with the use of moderate arc currents in the process of conditioning.

Aqueous Solution-Phase Selenized CuIn(S,Se)2 Thin Film Solar Cells Annealed under Inert Atmosphere.

PubMed

Oh, Yunjung; Yang, Wooseok; Kim, Jimin; Woo, Kyoohee; Moon, Jooho

2015-10-14

A nonvacuum solution-based approach can potentially be used to realize low cost, roll-to-roll fabrication of chalcopyrite CuIn(S,Se)2 (CISSe) thin film solar cells. However, most solution-based fabrication methods involve highly toxic solvents and inevitably require sulfurization and/or postselenization with hazardous H2S/H2Se gases. Herein, we introduce novel aqueous-based Cu-In-S and Se inks that contain an amine additive for producing a high-quality absorber layer. CISSe films were fabricated by simple deposition of Cu-In-S ink and Se ink followed by annealing under an inert atmosphere. Compositional and phase analyses confirmed that our simple aqueous ink-based method facilitated in-site selenization of the CIS layer. In addition, we investigated the molecular structures of our aqueous inks to determine how crystalline chalcopyrite absorber layers developed without sulfurization and/or postselenization. CISSe thin film solar cells annealed at 550 °C exhibited an efficiency of 4.55% under AM 1.5 illumination. The low-cost, nonvacuum method to deposit chalcopyrite absorber layers described here allows for safe and simple processing of thin film solar cells.

Specific Effects of Oxygen Molecule and Plasma on Thin-Film Growth of Y-Ba-Cu-O and Bi-Sr-(Ca)-Cu-O Systems

NASA Astrophysics Data System (ADS)

Endo, Tamio; Horie, Munehiro; Hirate, Naoki; Itoh, Katsutoshi; Yamada, Satoshi; Tada, Masaki; Itoh, Ken-ichi; Sugiyama, Morihiro; Sano, Shinji; Watabe, Kinji

1998-07-01

Thin films of a-oriented YBa2Cu3Ox (YBCO), Ca-doped c-oriented Bi2(Sr,Ca)2CuOx and nondoped c-oriented Bi2Sr2CuOx (Bi2201) were prepared at low temperatures by ion beam sputtering with supply of oxygen molecules or plasma. The plasma enhances crystal growth of the a-YBCO and Ca-doped Bi2201 phases. This can be interpreted in terms of their higher surface energies. The growth and quality of nondoped Bi2201 are improved with the supply of oxygen molecules. This particular result could be interpreted by the collision process between the oxygen molecules and the sputtered particles.

Scanning Probe Microscopy on heterogeneous CaCu3Ti4O12 thin films

PubMed Central

2011-01-01

The conductive atomic force microscopy provided a local characterization of the dielectric heterogeneities in CaCu3Ti4O12 (CCTO) thin films deposited by MOCVD on IrO2 bottom electrode. In particular, both techniques have been employed to clarify the role of the inter- and sub-granular features in terms of conductive and insulating regions. The microstructure and the dielectric properties of CCTO thin films have been studied and the evidence of internal barriers in CCTO thin films has been provided. The role of internal barriers and the possible explanation for the extrinsic origin of the giant dielectric response in CCTO has been evaluated. PMID:21711646

Scanning Probe Microscopy on heterogeneous CaCu3Ti4O12 thin films

NASA Astrophysics Data System (ADS)

Fiorenza, Patrick; Lo Nigro, Raffaella; Raineri, Vito

2011-12-01

The conductive atomic force microscopy provided a local characterization of the dielectric heterogeneities in CaCu3Ti4O12 (CCTO) thin films deposited by MOCVD on IrO2 bottom electrode. In particular, both techniques have been employed to clarify the role of the inter- and sub-granular features in terms of conductive and insulating regions. The microstructure and the dielectric properties of CCTO thin films have been studied and the evidence of internal barriers in CCTO thin films has been provided. The role of internal barriers and the possible explanation for the extrinsic origin of the giant dielectric response in CCTO has been evaluated.

Scanning Probe Microscopy on heterogeneous CaCu3Ti4O12 thin films.

PubMed

Fiorenza, Patrick; Lo Nigro, Raffaella; Raineri, Vito

2011-02-04

The conductive atomic force microscopy provided a local characterization of the dielectric heterogeneities in CaCu3Ti4O12 (CCTO) thin films deposited by MOCVD on IrO2 bottom electrode. In particular, both techniques have been employed to clarify the role of the inter- and sub-granular features in terms of conductive and insulating regions. The microstructure and the dielectric properties of CCTO thin films have been studied and the evidence of internal barriers in CCTO thin films has been provided. The role of internal barriers and the possible explanation for the extrinsic origin of the giant dielectric response in CCTO has been evaluated.

Intrinsic stress response of low and high mobility solute additions to Cu thin films

NASA Astrophysics Data System (ADS)

Kaub, Tyler; Anthony, Ryan; Thompson, Gregory B.

2017-12-01

Thin film stress is frequently controlled through adjustments applied to the processing parameters used during film deposition. In this work, we explore how the use of solutes with different intrinsic growth properties influences the residual growth stress development for a common solvent Cu film. The findings demonstrated that the addition of a high atomic mobility solute, Ag, or a low atomic mobility solute, V, results in both alloy films undergoing grain refinement that scaled with increases in the solute content. This grain refinement was associated with solute segregation and was more pronounced in the Cu(Ag) system. The grain size reduction was also associated with an increase in the tensile stresses observed in both alloy sets. These findings indicate that solutes can be used to control the grain size under the same deposition conditions, as well as alter the stress evolution of a growing thin film.

Impacts of zeolite nanoparticles on substrate properties of thin film nanocomposite membranes for engineered osmosis

NASA Astrophysics Data System (ADS)

Salehi, Tahereh Mombeini; Peyravi, Majid; Jahanshahi, Mohsen; Lau, Woei-Jye; Rad, Ali Shokuhi

2018-04-01

In this work, microporous substrates modified by zeolite nanoparticles were prepared and used for composite membrane making with the aim of reducing internal concentration polarization (ICP) effect of membranes during engineered osmosis applications. Nanocomposite substrates were fabricated via phase inversion technique by embedding nanostructured zeolite (clinoptilolite) in the range of 0-0.6 wt% into matrix of polyethersulfone (PES) substrate. Of all the substrates prepared, the PES0.4 substrate (with 0.4 wt% zeolite) exhibited unique characteristics, i.e., increased surface porosity, lower structural parameter ( S) (from 0.78 to 0.48 mm), and enhanced water flux. The thin film nanocomposite (TFN) membrane made of this optimized substrate was also reported to exhibit higher water flux compared to the control composite membrane during forward osmosis (FO) and pressure-retarded osmosis (PRO) test, without compromising reverse solute flux. The water flux of such TFN membrane was 43% higher than the control TFC membrane (1.93 L/m2 h bar) with salt rejection recorded at 94.7%. An increment in water flux is ascribed to the reduction in structural parameter, leading to reduced ICP effect.

Optimized ultra-thin manganin alloy passivated fine-pitch damascene compatible bump-less Cu-Cu bonding at sub 200 °C for three-dimensional Integration applications

NASA Astrophysics Data System (ADS)

Panigrahi, Asisa Kumar; Hemanth Kumar, C.; Bonam, Satish; Ghosh, Tamal; Rama Krishna Vanjari, Siva; Govind Singh, Shiv

2018-02-01

Enhanced Cu diffusion, Cu surface passivation, and smooth surface at the bonding interface are the key essentials for high quality Cu-Cu bonding. Previously, we have demonstrated optimized 3 nm thin Manganin metal-alloy passivation from oxidation and also helps to reduce the surface roughness to about 0.8 nm which substantially led to high quality Cu-Cu bonding. In this paper, we demonstrated an ultra fine-pitch (<25 µm) Cu-Cu bonding using an optimized Manganin metal-alloy passivation. This engineered surface passivation approach led to high quality bonding at sub 200 °C temperature and 0.4 MPa. Very low specific contact resistance of 1.4 × 10-7 Ω cm2 and the defect free bonded interface is clear indication of high quality bonding for future multilayer integrations. Furthermore, electrical characterization of the bonded structure was performed under various robust conditions as per International Technology Roadmap for Semiconductors (ITRS Roadmap) in order to satisfy the stability of the bonded structure.

Filling of single-walled carbon nanotubes by CuI nanocrystals via capillary technique

NASA Astrophysics Data System (ADS)

Chernysheva, M. V.; Eliseev, A. A.; Lukashin, A. V.; Tretyakov, Yu. D.; Savilov, S. V.; Kiselev, N. A.; Zhigalina, O. M.; Kumskov, A. S.; Krestinin, A. V.; Hutchison, J. L.

2007-03-01

The present study is focused on the synthesis and investigation of the nanocomposite CuI@SWNT obtained by the filling of metallic single-walled carbon nanotubes (SWNTs) (inner diameter 1-1.4 nm) by wide-gap semiconducting CuI nanocrystals using so-called capillary technique. The method is based on the impregnation of pre-opened SWNTs by molten CuI in vacuum with subsequent slow cooling to room temperature. SWNTs and CuI@SWNT nanocomposites were studied by nitrogen capillary adsorption method, EDX microanalysis, HRTEM microscopy and Raman spectroscopy. The changing of electronic properties of CuI@SWNT as compare to row nanotubes was observed.

Competitive adsorption of Pb(II), Cu(II), and Zn(II) ions onto hydroxyapatite-biochar nanocomposite in aqueous solutions

NASA Astrophysics Data System (ADS)

Wang, Yu-Ying; Liu, Yu-Xue; Lu, Hao-Hao; Yang, Rui-Qin; Yang, Sheng-Mao

2018-05-01

A hydroxyapatite-biochar nanocomposite (HAP-BC) was successfully fabricated and its physicochemical properties characterized. The analyses showed that HAP nanoparticles were successfully loaded on the biochar surface. The adsorption of Pb(II), Cu(II), and Zn(II) by HAP-BC was systematically studied in single and ternary metal systems. The results demonstrated that pH affects the adsorption of heavy metals onto HAP-BC. Regarding the adsorption kinetics, the pseudo-second-order model showed the best fit for all three heavy metal ions on HAP-BC. In both single and ternary metal ion systems, the adsorption isotherm of Pb(II) by HAP-BC followed Langmuir model, while those of Cu(II) and Zn(II) fitted well with Freundlich model. The maximum adsorption capacity for each tested metal by HAP-BC was higher than that of pristine rice straw biochar (especially for Pb(II)) or those of other reported adsorbents. Therefore, HAP-BC could explore as a new material for future application in heavy metal removal.

Aerosol-assisted chemical vapor deposition of ultra-thin CuOx films as hole transport material for planar perovskite solar cells

NASA Astrophysics Data System (ADS)

Zhang, Zhixin; Chen, Shuqun; Li, Pingping; Li, Hongyi; Wu, Junshu; Hu, Peng; Wang, Jinshu

This paper reports on the fabrication of CuOx films to be used as hole transporting layer (HTL) in CH3NH3PbI3 perovskite solar cells (PSCs). Ultra-thin CuOx coatings were grown onto FTO substrates for the first time via aerosol-assisted chemical vapor deposition (AACVD) of copper acetylacetonate in methanol. After incorporating into the PSCs prepared at ambient air, a highest power conversion efficiency (PCE) of 8.26% with HTL and of 3.34% without HTL were achieved. Our work represents an important step in the development of low-cost CVD technique for fabricating ultra-thin metal oxide functional layers in thin film photovoltaics.

Direct Growth of CuO Nanorods on Graphitic Carbon Nitride with Synergistic Effect on Thermal Decomposition of Ammonium Perchlorate

PubMed Central

Tan, Linghua; Xu, Jianhua; Li, Shiying; Li, Dongnan; Dai, Yuming; Kou, Bo; Chen, Yu

2017-01-01

Novel graphitic carbon nitride/CuO (g-C3N4/CuO) nanocomposite was synthesized through a facile precipitation method. Due to the strong ion-dipole interaction between copper ions and nitrogen atoms of g-C3N4, CuO nanorods (length 200–300 nm, diameter 5–10 nm) were directly grown on g-C3N4, forming a g-C3N4/CuO nanocomposite, which was confirmed via X-ray diffraction (XRD), transmission electron microscopy (TEM), field emission scanning electron microscopy (FESEM), and X-ray photoelectron spectroscopy (XPS). Finally, thermal decomposition of ammonium perchlorate (AP) in the absence and presence of the prepared g-C3N4/CuO nanocomposite was examined by differential thermal analysis (DTA), and thermal gravimetric analysis (TGA). The g-C3N4/CuO nanocomposite showed promising catalytic effects for the thermal decomposition of AP. Upon addition of 2 wt % nanocomposite with the best catalytic performance (g-C3N4/20 wt % CuO), the decomposition temperature of AP was decreased by up to 105.5 °C and only one decomposition step was found instead of the two steps commonly reported in other examples, demonstrating the synergistic catalytic activity of the as-synthesized nanocomposite. This study demonstrated a successful example regarding the direct growth of metal oxide on g-C3N4 by ion-dipole interaction between metallic ions, and the lone pair electrons on nitrogen atoms, which could provide a novel strategy for the preparation of g-C3N4-based nanocomposite. PMID:28772844

Tensile Properties and Fracture Characteristics of Nanostructured Copper and Cu-SiC Nanocomposite Produced by Mechanical Milling and Spark Plasma Sintering Process

NASA Astrophysics Data System (ADS)

Akbarpour, M. R.

2018-03-01

The presence of large grains within nanometric and ultrafine grain matrix is an effective method in order to enhance strength while keeping the high ductility of metals. For this purpose, in this research, spark plasma sintering (SPS) was used to consolidate milled Cu and Cu-SiC powders. In SPS process, local sparks with high temperature between particles take place and locally lead to intense grain growth, and therefore, this method has the ability to produce bimodal grain structures in copper and copper-based composites. Microstructural and mechanical studies showed ≈ 185 and ≈ 437 nm matrix grain sizes, high tensile yield strength values of ≈ 188.4 and ≈ 296.9 MPa, and fracture strain values of 15.1 and 6.7% for sintered Cu and Cu-4 vol.% SiC nanocomposite materials, respectively. The presence of nanoparticles promoted the occurrence of static recrystallization and decreased the fraction of coarse grains in microstructure. The high tensile properties of the produced materials are attributed to fine grain size, homogenous dispersion of nanoparticles and retarded grain boundary migration during sintering.

Thermal-induced structural and optical investigations of Agsbnd ZnO nanocomposite thin films

NASA Astrophysics Data System (ADS)

Singh, S. K.; Singhal, R.

2018-07-01

In the present paper, we have successfully synthesized Agsbnd ZnO nanocomposite thin films by RF-magnetron sputtering technique at room temperature. Systematic investigations of thermal-induced structural and optical modifications in Agsbnd ZnO thin films have been observed and described. The Agsbnd ZnO thin films were annealed at three different temperatures of 300 °C, 400 °C and 500 °C in vacuum to prevent the oxidation of Ag. The presence and formation of Ag nanoparticles were estimated by transmission electron microscopy. X-ray diffraction analysis revealed the structural information about the crystalline quality of ZnO. The crystallinity as well as the crystallite size of the films have been found to be improved with annealing temperatures. The estimated crystallite size was ∼15.8 nm for as-deposited film and 19.0 nm for the film at a higher temperature. The chemical composition and structural analysis of as-deposited film were carried out by X-ray photoelectron spectroscopy. A very sharp absorption band appeared at ∼540 nm for Ag NPs that is associated with the surface plasmon resonance band of Ag. A noticeable red shift of about ∼12 nm has been recorded for films annealed at 500 °C. Atomic force microscopy has been utilized to examine the surface morphology of the as-deposited and annealed films. The grain size was found to be increase with increasing annealing temperature, while no significant changes were observed in the roughness of Agsbnd ZnO thin films. Raman spectroscopy revealed lattice defects and disordering in the films after the thermal annealing.

Influence of Cu-Ti thin film surface properties on antimicrobial activity and viability of living cells.

PubMed

Wojcieszak, Damian; Kaczmarek, Danuta; Antosiak, Aleksandra; Mazur, Michal; Rybak, Zbigniew; Rusak, Agnieszka; Osekowska, Malgorzata; Poniedzialek, Agata; Gamian, Andrzej; Szponar, Bogumila

2015-11-01

The paper describes properties of thin-film coatings based on copper and titanium. Thin films were prepared by co-sputtering of Cu and Ti targets in argon plasma. Deposited coatings consist of 90at.% of Cu and 10at.% of Ti. Characterization of the film was made on the basis of investigations of microstructure and physicochemical properties of the surface. Methods such as scanning electron microscopy, x-ray microanalysis, x-ray diffraction, x-ray photoelectron spectroscopy, atomic force microscopy, optical profilometry and wettability measurements were used to assess the properties of deposited thin films. An impact of Cu-Ti coating on the growth of selected bacteria and viability of the living cells (line L929, NCTC clone 929) was described in relation to the structure, surface state and wettability of the film. It was found that as-deposited films were amorphous. However, in such surroundings the nanocrystalline grains of 10-15nm and 25-35nm size were present. High surface active area with a roughness of 8.9nm, had an effect on receiving relatively high water contact angle value (74.1°). Such wettability may promote cell adhesion and result in an increase of the probability of copper ion transfer from the film surface into the cell. Thin films revealed bactericidal and fungicidal effects even in short term-contact. High activity of prepared films was directly related to high amount (ca. 51 %) of copper ions at 1+ state as x-ray photoelectron spectroscopy results have shown. Copyright © 2015 Elsevier B.V. All rights reserved.

Optical and electrical properties of p-type transparent conducting CuAlO2 thin film synthesized by reactive radio frequency magnetron sputtering technique

NASA Astrophysics Data System (ADS)

Saha, B.; Thapa, R.; Jana, S.; Chattopadhyay, K. K.

2010-10-01

Thin films of p-type transparent conducting CuAlO2 have been synthesized through reactive radio frequency magnetron sputtering on silicon and glass substrates at substrate temperature 300°C. Reactive sputtering of a target fabricated from Cu and Al powder (1:1.5) was performed in Ar+O2 atmosphere. The deposition parameters were optimized to obtain phase pure, good quality CuAlO2 thin films. The films were characterized by studying their structural, morphological, optical and electrical properties.

Heterojunction solar cell with 6% efficiency based on an n-type aluminum-gallium-oxide thin film and p-type sodium-doped Cu2O sheet

NASA Astrophysics Data System (ADS)

Minami, Tadatsugu; Nishi, Yuki; Miyata, Toshihiro

2015-02-01

In this paper, we describe efforts to enhance the efficiency of Cu2O-based heterojunction solar cells fabricated with an aluminum-gallium-oxide (Al-Ga-O) thin film as the n-type layer and a p-type sodium (Na)-doped Cu2O (Cu2O:Na) sheet prepared by thermally oxidizing copper sheets. The optimal Al content [X; Al/(Ga + Al) atomic ratio] of an AlX-Ga1-X-O thin-film n-type layer was found to be approximately 2.5 at. %. The optimized resistivity was approximately 15 Ω cm for n-type AlX-Ga1-X-O/p-type Cu2O:Na heterojunction solar cells. A MgF2/AZO/Al0.025-Ga0.975-O/Cu2O:Na heterojunction solar cell with 6.1% efficiency was fabricated using a 60-nm-thick n-type oxide thin-film layer and a 0.2-mm-thick Cu2O:Na sheet with the optimized resistivity.

Review of interventions to reduce ultraviolet tanning: Need for treatments targeting excessive tanning, an emerging addictive behavior.

PubMed

Stapleton, Jerod L; Hillhouse, Joel; Levonyan-Radloff, Kristine; Manne, Sharon L

2017-12-01

Millions of Americans engage in tanning each year, defined as intentional ultraviolet radiation (UVR) exposure in the form of sunbathing or the use of indoor tanning beds. An emerging body of research suggests that UVR has addictive properties and some tanners engage in excessive tanning. This article provides an overview of the evidence of tanning addiction and a systematic review of existing tanning interventions with the goal of evaluating their potential to impact addicted tanners. Our search identified 24 intervention studies that were summarized and discussed according to 3 primary themes. First, there is a dearth of tanning interventions that target excessive tanning or are designed as treatments for tanning addiction. Second, tanning interventions are primarily educational interventions designed to increase knowledge of the risks of tanning. Third, there are notable aspects of existing tanning interventions that are relevant to addiction science, including the use of brief motivational and cognitive-behavioral-based interventions. Future directions are considered including recommendations for utilizing the existing evidence base to formulate interventions targeting excessive tanners. (PsycINFO Database Record (c) 2017 APA, all rights reserved).

Thermoelectric and Transport Properties of Delafossite CuCrO2:Mg Thin Films Prepared by RF Magnetron Sputtering

PubMed Central

Sinnarasa, Inthuga; Thimont, Yohann; Presmanes, Lionel; Barnabé, Antoine; Tailhades, Philippe

2017-01-01

P-type Mg doped CuCrO2 thin films have been deposited on fused silica substrates by Radio-Frequency (RF) magnetron sputtering. The as-deposited CuCrO2:Mg thin films have been annealed at different temperatures (from 450 to 650 °C) under primary vacuum to obtain the delafossite phase. The annealed samples exhibit 3R delafossite structure. Electrical conductivity σ and Seebeck coefficient S of all annealed films have been measured from 40 to 220 °C. The optimized properties have been obtained for CuCrO2:Mg thin film annealed at 550 °C. At a measurement temperature of 40 °C, this sample exhibited the highest electrical conductivity of 0.60 S·cm−1 with a Seebeck coefficient of +329 µV·K−1. The calculated power factor (PF = σS²) was 6 µW·m−1·K−2 at 40 °C and due to the constant Seebeck coefficient and the increasing electrical conductivity with measurement temperature, it reached 38 µW·m−1·K−2 at 220 °C. Moreover, according to measurement of the Seebeck coefficient and electrical conductivity in temperature, we confirmed that CuCrO2:Mg exhibits hopping conduction and degenerates semiconductor behavior. Carrier concentration, Fermi level, and hole effective mass have been discussed. PMID:28654011

Room-temperature wide-range luminescence and structural, optical, and electrical properties of SILAR deposited Cu-Zn-S nano-structured thin films

NASA Astrophysics Data System (ADS)

Jose, Edwin; Kumar, M. C. Santhosh

2016-09-01

We report the deposition of nanostructured Cu-Zn-S composite thin films by Successive Ionic Layer Adsorption and Reaction (SILAR) method on glass substrates at room temperature. The structural, morphological, optical, photoluminescence and electrical properties of Cu-Zn-S thin films are investigated. The results of X-ray diffraction (XRD) and Raman spectroscopy studies indicate that the films exhibit a ternary Cu-Zn-S structure rather than the Cu xS and ZnS binary composite. Scanning electron microscope (SEM) studies show that the Cu-Zn-S films are covered well over glass substrates. The optical band gap energies of the Cu-Zn-S films are calculated using UV-visible absorption measurements, which are found in the range of 2.2 to 2.32 eV. The room temperature photoluminescence studies show a wide range of emissions from 410 nm to 565 nm. These emissions are mainly due to defects and vacancies in the composite system. The electrical studies using Hall effect measurements show that the Cu-Zn-S films are having p-type conductivity.

Development of Cu Clad Cu-Zr Based Metallic Glass and Its Solderability

NASA Astrophysics Data System (ADS)

Terajima, Takeshi; Kimura, Hisamichi; Inoue, Akihisa

Soldering is a candidate technique for joining metallic glasses. It can be processed far below the crystallization temperatures of the various metallic glasses so that there is no possibility of crystallization. However, wettability of Cu-Zr based metallic glass by Pb free solder is poor because a strong surface oxide film interferes direct contact between them. To overcome the problem, Cu thin film clad metallic glass was developed. It was preliminary produced by casting a melt of Cu36Zr48Al8Ag8 pre-alloy into Cu mold cavity, inside which Cu thin film with 2 mm in thickness was set on the wall. Cu36Zr48Al8Ag8 metallic glass, whose surface Cu thin film was welded to, was successfully produced. From the microstructure analyses, it was found that reaction layer was formed at the interface between Cu and Cu36Zr48Al8Ag8 metallic glass, however, there was no oxide in the Cu clad layer. Solderability to the metallic glass was drastically increased. The Cu clad layer played an important role to prevent the formation of surface oxide film and consequently improved the solderability.

Computational alloy design of (Co1-xNix)88Zr7B4Cu1 nanocomposite soft magnets

NASA Astrophysics Data System (ADS)

Dong, B.; Healy, J.; Lan, S.; Daniil, M.; Willard, M. A.

2018-05-01

The dependence of coercivity on composition is an important factor for establishing optimized soft magnetic properties. In this study, we have used the random anisotropy and coherent rotation models to estimate the variation of coercivity with composition in (Co1-xNix)88Zr7B4Cu1 nanocomposite alloys. Our calculations that the magnetoelastic anisotropy contribution to coercivity dominates for Ni rich compositions (x > 0.5). A small range of compositions (0.65 < x < 0.75) is predicted to result in low values of coercivity (<10 A/m). To validate this prediction, (Co1-xNix)88Zr7B4Cu1 nanocomposites in this range were prepared by melt spinning followed by 3600 s isothermal annealing at the primary crystallization peak temperature (˜673 K). Hysteresis loops were measured using vibrating sample magnetometry at room temperature and saturation magnetostriction was measured using a strain gage based magnetostrictometer. Moderately small coercivities (30-40 A/m) and magnetostrictions (3-4 ppm) were measured at for samples with 0.685 < x < 0.725. Our measured coercivity had a minimum value of 32 A/m at x = 0.725, a shift in composition of about 5 at% in the direction of higher Ni content and without the anticipated low value of coercivity. Several reasons for the inaccuracy of this approach are described, including: ignored contributions from amorphous phase (especially in magnetoealstic anisotropy), composition segregation during crystallization leading to unpredictable compositional shifts in prediction, and the general observation that the predictability of minimum coercivity from minimal combined anisotropies has unexplained deviation even in far less complicated materials.

Dilute electrodeposition of TiO2 and ZnO thin film memristors on Cu substrate

NASA Astrophysics Data System (ADS)

Fauzi, F. B.; Ani, M. H.; Herman, S. H.; Mohamed, M. A.

2018-03-01

Memristor has become one of the alternatives to replace the current memory technologies. Fabrication of titanium dioxide, TiO2 memristor has been extensively studied by using various deposition methods. However, recently more researches have been done to explore the compatibility of other transition metal oxide, TMO such as zinc oxide, ZnO to be used as the active layer of the memristor. This paper highlights the simple and easy-control electrodeposition to deposit titanium, Ti and zinc, Zn thin film at room temperature and subsequent thermal oxidation at 600 °C. Gold, Au was then sputtered as top electrode to create metal-insulator-metal, MIM sandwich of Au/TiO2-Cu2O-CuO/Cu and Au/ZnO-Cu2O-CuO/Cu memristors. The structural, morphological and memristive properties were characterized using Field Emission Scanning Electron Microscopy, FESEM, X-Ray Diffraction, XRD and current-voltage, I-V measurement. Both Au/TiO2-Cu2O-CuO/Cu and Au/ZnO-Cu2O-CuO/Cu memristivity were identified by the pinched hysteresis loop with resistive ratio of 1.2 and 1.08 respectively. Empirical study on diffusivity of Ti4+, Zn2+ and O2‑ ions in both metal oxides show that the metal vacancies were formed, thus giving rise to its memristivity. The electrodeposited Au/TiO2-Cu2O-CuO/Cu and Au/ZnO-Cu2O-CuO/Cu memristors demonstrate comparable performances to previous studies using other methods.

Tanning preparations.

PubMed

Levy, S B

2000-10-01

Increasing consumer awareness as to the hazards of UV light should fuel ongoing interest in self-tanning products. As a result of the benign toxicologic profile of DHA, products containing DHA represent a safe alternative to UV-induced tanning. The results obtained with these products depend on the final formulation, the individual application technique, and the consumer's complexion type. Greater experience in formulation combined with increasing sophistication on the part of the consumer should lead to continuing growth in interest and satisfaction with the use of DHA-containing sunless or self-tanning products. Individuals need to be informed that these products do not offer significant protection against UV-B. If formulated with standard sunscreens, consumers should be cautioned that the duration of UV protection is more short-lived than the color change.

Does the portrayal of tanning in Australian women's magazines relate to real women's tanning beliefs and behavior?

PubMed

Dixon, Helen G; Warne, Charles D; Scully, Maree L; Wakefield, Melanie A; Dobbinson, Suzanne J

2011-04-01

Content analysis data on the tans of 4,422 female Caucasian models sampled from spring and summer magazine issues were combined with readership data to generate indices of potential exposure to social modeling of tanning via popular women's magazines over a 15-year period (1987 to 2002). Associations between these indices and cross-sectional telephone survey data from the same period on 5,675 female teenagers' and adults' tanning attitudes, beliefs, and behavior were examined using logistic regression models. Among young women, greater exposure to tanning in young women's magazines was associated with increased likelihood of endorsing pro-tan attitudes and beliefs. Among women of all ages, greater exposure to tanned models via the most popular women's magazines was associated with increased likelihood of attempting to get a tan but lower likelihood of endorsing pro-tan attitudes. Popular women's magazines may promote and reflect real women's tanning beliefs and behavior.

Is initiating tanning bed use as a minor associated with increased risky tanning behaviors and burning? An exploratory study.

PubMed

Seidenberg, Andrew B; Noar, Seth M; Sontag, Jennah M

2017-12-01

Tanning bed use is most common among youth and young adults, and is associated with an increased risk of skin cancer. Recently, numerous states have adopted restrictions on minors' access to tanning beds; however, little has been reported on how such policies may impact tanning behaviors and burning. The purpose of this study was to examine the associations between age of indoor tanning initiation and risky tanning behaviors and burning. Female students (n=567) attending a large southeastern public university completed a questionnaire (spring of 2015) assessing tanning bed use history, including age of initiation. The analytic sample was limited to participants reporting past year indoor tanning (n=134). Multivariable logistic regression was used to compare the odds of risky tanning behaviors and burning among those initiating indoor tanning before and after their 18th birthday. Participants initiating indoor tanning as a minor had significantly (ps<0.05) greater odds of using a tanning bed 10 or more times in the previous year, typically indoor tanning for ≥10min, ever indoor tanning without wearing goggles, and ever fallen asleep inside a tanning bed. Further, those that initiated as a minor had significantly greater odds of ever burning from indoor tanning (p<0.05). Indoor tanning initiation as a minor was associated with several risky tanning behaviors and burning. Youth access restrictions may help reduce the harms caused by tanning beds. Copyright © 2017. Published by Elsevier Inc.

The mathematics of tanning

PubMed Central

Thingnes, Josef; Øyehaug, Leiv; Hovig, Eivind; Omholt, Stig W

2009-01-01

Background The pigment melanin is produced by specialized cells, called melanocytes. In healthy skin, melanocytes are sparsely spread among the other cell types in the basal layer of the epidermis. Sun tanning results from an UV-induced increase in the release of melanin to neighbouring keratinocytes, the major cell type component of the epidermis as well as redistribution of melanin among these cells. Here we provide a mathematical conceptualization of our current knowledge of the tanning response, in terms of a dynamic model. The resolution level of the model is tuned to available data, and its primary focus is to describe the tanning response following UV exposure. Results The model appears capable of accounting for available experimental data on the tanning response in different skin and photo types. It predicts that the thickness of the epidermal layer and how far the melanocyte dendrites grow out in the epidermal layers after UV exposure influence the tanning response substantially. Conclusion Despite the paucity of experimental validation data the model is constrained enough to serve as a foundation for the establishment of a theoretical-experimental research programme aimed at elucidating the more fine-grained regulatory anatomy underlying the tanning response. PMID:19505344

Chemical bath deposited (CBD) CuO thin films on n-silicon substrate for electronic and optical applications: Impact of growth time

NASA Astrophysics Data System (ADS)

Sultana, Jenifar; Paul, Somdatta; Karmakar, Anupam; Yi, Ren; Dalapati, Goutam Kumar; Chattopadhyay, Sanatan

2017-10-01

Thin film of p-type cupric oxide (p-CuO) is grown on silicon (n-Si) substrate by using chemical bath deposition (CBD) technique and a precise control of thickness from 60 nm to 178 nm has been achieved. The structural properties and stoichiometric composition of the grown films are observed to depend significantly on the growth time. The chemical composition, optical properties, and structural quality are investigated in detail by employing XRD, ellipsometric measurements and SEM images. Also, the elemental composition and the oxidation states of Cu and O in the grown samples have been studied in detail by XPS measurements. Thin film of 110 nm thicknesses exhibited the best performance in terms of crystal quality, refractive index, dielectric constant, band-gap, and optical properties. The study suggests synthesis route for developing high quality CuO thin film using CBD method for electronic and optical applications.

The W alloying effect on thermal stability and hardening of nanostructured Cu-W alloyed thin films.

PubMed

Zhao, J T; Zhang, J Y; Hou, Z Q; Wu, K; Feng, X B; Liu, G; Sun, J

2018-05-11

In order to achieve desired mechanical properties of alloys by manipulating grain boundaries (GBs) via solute decoration, it is of great significance to understand the underlying mechanisms of microstructural evolution and plastic deformation. In this work, nanocrystalline (NC) Cu-W alloyed films with W concentrations spanning from 0 to 40 at% were prepared by using magnetron sputtering. Thermal stability (within the temperature range of 200 °C-600 °C) and hardness of the films were investigated by using the x-ray diffraction, transmission electron microscope (TEM) and nanoindentation, respectively. The NC pure Cu film exhibited substantial grain growth upon all annealing temperatures. The Cu-W alloyed films, however, displayed distinct microstructural evolution that depended not only on the W concentration but also on the annealing temperature. At a low temperature of 200 °C, all the Cu-W alloyed films were highly stable, with unconspicuous change in grain sizes. At high temperatures of 400 °C and 600 °C, the microstructural evolution was greatly controlled by the W concentrations. The Cu-W films with low W concentration manifested abnormal grain growth (AGG), while the ones with high W concentrations showed phase separation. TEM observations unveiled that the AGG in the Cu-W alloyed thin films was rationalized by GB migration. Nanoindentation results showed that, although the hardness of both the as-deposited and annealed Cu-W alloyed thin films monotonically increased with W concentrations, a transition from annealing hardening to annealing softening was interestingly observed at the critical W addition of ∼25 at%. It was further revealed that an enhanced GB segregation associated with detwinning was responsible for the annealing hardening, while a reduced solid solution hardening for the annealing softening.

Spectroscopic investigation of the chemical and electronic properties of chalcogenide materials for thin-film optoelectronic devices

NASA Astrophysics Data System (ADS)

Horsley, Kimberly Anne

Chalcogen-based materials are at the forefront of technologies for sustainable energy production. This progress has come only from decades of research, and further investigation is needed to continue improvement of these materials. For this dissertation, a number of chalcogenide systems were studied, which have applications in optoelectronic devices, such as LEDs and Photovoltaics. The systems studied include Cu(In,Ga)Se2 (CIGSe) and CuInSe 2 (CISe) thin-film absorbers, CdTe-based photovoltaic structures, and CdTe-ZnO nanocomposite materials. For each project, a sample set was prepared through collaboration with outside institutions, and a suite of spectroscopy techniques was employed to answer specific questions about the system. These techniques enabled the investigation of the chemical and electronic structure of the materials, both at the surface and towards the bulk. CdS/Cu(In,Ga)Se2 thin-films produced from the roll-to-roll, ambient pressure, Nanosolar industrial line were studied. While record-breaking efficiency cells are usually prepared in high-vacuum (HV) or ultra-high vacuum (UHV) environments, these samples demonstrate competitive mass-production efficiency without the high-cost deposition environment. We found relatively low levels of C contaminants, limited Na and Se oxidation, and a S-Se intermixing at the CdS/CIGSe interface. The surface band gap compared closely to previously investigated CIGSe thin-films deposited under vacuum, illustrating that roll-to-roll processing is a promising and less-expensive alternative for solar cell production. An alternative deposition process for CuInSe2 was also studied, in collaboration with the University of Luxembourg. CuInSe2 absorbers were prepared with varying Cu content and surface treatments to investigate the potential to produce an absorber with a Cu-rich bulk and Cu-poor surface. This is desired to combine the bulk characteristics of reduced defects and larger grains in Cu-rich films, while maintaining

Enhancement of spin-Seebeck effect by inserting ultra-thin Fe{sub 70}Cu{sub 30} interlayer

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kikuchi, D., E-mail: d.kikuchi@imr.tohoku.ac.jp; WPI Advanced Institute for Materials Research, Tohoku University, Sendai 980-8577; Spin Quantum Rectification Project, ERATO, Japan Science and Technology Agency, Sendai 980-8577

2015-02-23

We report the longitudinal spin-Seebeck effects (LSSEs) for Pt/Fe{sub 70}Cu{sub 30}/BiY{sub 2}Fe{sub 5}O{sub 12} (BiYIG) and Pt/BiYIG devices. The LSSE voltage was found to be enhanced by inserting an ultra-thin Fe{sub 70}Cu{sub 30} interlayer. This enhancement decays sharply with increasing the Fe{sub 70}Cu{sub 30} thickness, suggesting that it is not due to bulk phenomena, such as a superposition of conventional thermoelectric effects, but due to interface effects related to the Fe{sub 70}Cu{sub 30} interlayer. Combined with control experiments using Pt/Fe{sub 70}Cu{sub 30} devices, we conclude that the enhancement of the LSSE voltage in the Pt/Fe{sub 70}Cu{sub 30}/BiYIG devices is attributedmore » to the improvement of the spin-mixing conductance at the Pt/BiYIG interfaces.« less

Watching reality television beauty shows is associated with tanning lamp use and outdoor tanning among college students.

PubMed

Fogel, Joshua; Krausz, Faye

2013-05-01

Ultraviolet radiation exposure through natural sunlight or tanning lamps is a risk factor for skin cancer. As the media can influence behavior, we studied whether watching reality television (TV) beauty shows is associated with tanning lamp use or outdoor tanning. College students (n = 576) were surveyed on their reality TV beauty show watching, their use of tanning lamps, and outdoor tanning behavior. We asked media attitude questions about connectivity with reality TV shows and Internet use of Facebook to discuss reality TV shows. Those who did versus did not watch reality TV beauty shows used tanning lamps (12.9% vs 3.7%, P < .001) and tanned outdoors (43.3% vs 28.7%, P < .001) at significantly greater percentages. Significant predictors of tanning lamp use included watching reality TV beauty shows (odds ratio [OR] 2.58, 95% confidence interval [CI] 1.11-6.00), increasing age (OR 1.17, 95% CI 1.04-1.32), and female sex (OR 10.16, 95% CI 3.29-31.41). Significant predictors of outdoor tanning included watching reality TV beauty shows (OR 2.11, 95% CI 1.33-3.34). The specific names of the reality TV beauty shows watched were not obtained and therefore we cannot determine if particular shows were more or less associated with this behavior. Watching reality TV beauty shows is associated with both tanning lamp use and outdoor tanning. Dermatologists should consider discussing the potential harmful aspects of tanning beds and outdoor tanning, especially with their patients who watch reality TV beauty shows. Copyright © 2012 American Academy of Dermatology, Inc. Published by Mosby, Inc. All rights reserved.

Achieving 14.4% Alcohol-Based Solution-Processed Cu(In,Ga)(S,Se)2 Thin Film Solar Cell through Interface Engineering.

PubMed

Park, Gi Soon; Chu, Van Ben; Kim, Byoung Woo; Kim, Dong-Wook; Oh, Hyung-Suk; Hwang, Yun Jeong; Min, Byoung Koun

2018-03-28

An optimization of band alignment at the p-n junction interface is realized on alcohol-based solution-processed Cu(In,Ga)(S,Se) 2 (CIGS) thin film solar cells, achieving a power-conversion-efficiency (PCE) of 14.4%. To obtain a CIGS thin film suitable for interface engineering, we designed a novel "3-step chalcogenization process" for Cu 2- x Se-derived grain growth and a double band gap grading structure. Considering S-rich surface of the CIGS thin film, an alternative ternary (Cd,Zn)S buffer layer is adopted to build favorable "spike" type conduction band alignment instead of "cliff" type. Suppression of interface recombination is elucidated by comparing recombination activation energies using a dark J- V- T analysis.

Pulsed photoinitiated fabrication of inkjet printed titanium dioxide/reduced graphene oxide nanocomposite thin films.

PubMed

Bourgeois, Briley; Luo, Sijun; Riggs, Brian; Ji, Yaping; Adireddy, Shiva; Schroder, Kurt; Farnsworth, Stan; Chrisey, Douglas; Escarra, Matthew

2018-08-03

This work reports a new technique for scalable and low-temperature processing of nanostructured TiO 2 thin films, allowing for practical manufacturing of TiO 2 -based devices such as perovskite solar cells at low-temperature or on flexible substrates. Dual layers of dense and mesoporous TiO 2 /graphitic oxide nanocomposite films are synthesized simultaneously using inkjet printing and pulsed photonic irradiation. Investigation of process parameters including precursor concentration (10-20 wt%) and exposure fluence (4.5-8.5 J cm -2 ) reveals control over crystalline quality, graphitic oxide phase, film thickness, dendrite density, and optical properties. Raman spectroscopy shows the E g peak, characteristic of anatase phase titania, increases in intensity with higher photonic irradiation fluence, suggesting increased crystallinity through higher fluence processing. Film thickness and dendrite density is shown to increase with precursor concentration in the printed ink. The dense base layer thickness was controlled between 20 and 80 nm. The refractive index of the films is determined by ellipsometry to be 1.92 ± 0.08 at 650 nm. Films exhibit an energy weighted optical transparency of 91.1%, in comparison to 91.3% of a thermally processed film, when in situ carbon materials were removed. Transmission and diffuse reflectance are used to determine optical band gaps of the films ranging from 2.98 to 3.38 eV in accordance with the photonic irradiation fluence and suggests tunability of TiO 2 phase composition. The sheet resistance of the synthesized films is measured to be 14.54 ± 1.11 Ω/□ and 28.90 ± 2.24 Ω/□ for films as-processed and after carbon removal, respectively, which is comparable to high temperature processed TiO 2 thin films. The studied electrical and optical properties of the light processed films show comparable results to traditionally processed TiO 2 while offering the distinct advantages of scalable manufacturing, low-temperature processing

Donor-acceptor pair recombination luminescence from monoclinic Cu{sub 2}SnS{sub 3} thin film

DOE Office of Scientific and Technical Information (OSTI.GOV)

Aihara, Naoya; Tanaka, Kunihiko, E-mail: tanaka@vos.nagaokaut.ac.jp; Uchiki, Hisao

2015-07-20

The defect levels in Cu{sub 2}SnS{sub 3} (CTS) were investigated using photoluminescence (PL) spectroscopy. A CTS thin film was prepared on a soda-lime glass/molybdenum substrate by thermal co-evaporation and sulfurization. The crystal structure was determined to be monoclinic, and the compositional ratios of Cu/Sn and S/Metal were determined to be 1.8 and 1.2, respectively. The photon energy of the PL spectra observed from the CTS thin film was lower than that previously reported. All fitted PL peaks were associated with defect related luminescence. The PL peaks observed at 0.843 and 0.867 eV were assigned to donor-acceptor pair recombination luminescence, the thermalmore » activation energies of which were determined to be 22.9 and 24.8 meV, respectively.« less

Indoor Tanning and Problem Behavior

ERIC Educational Resources Information Center

Bagdasarov, Zhanna; Banerjee, Smita; Greene, Kathryn; Campo, Shelly

2008-01-01

Objective: The authors examined factors predicting college students' use of tanning beds. Participants and Methods: Undergraduate students (N = 745) at a large Northeastern university participated in the study by answering a survey measuring tanning behavior and other psychosocial variables, including sensation seeking, self-esteem, tanning image…

State Indoor Tanning Laws and Prevalence of Indoor Tanning Among US High School Students, 2009-2015.

PubMed

Qin, Jin; Holman, Dawn M; Jones, Sherry Everett; Berkowitz, Zahava; Guy, Gery P

2018-07-01

To examine the association between state indoor tanning laws and indoor tanning behavior using nationally representative samples of US high school students younger than 18 years. We combined data from the 2009, 2011, 2013, and 2015 national Youth Risk Behavior Surveys (n = 41 313) to analyze the association between 2 types of state indoor tanning laws (age restriction and parental permission) and the prevalence of indoor tanning during the 12 months before the survey, adjusting for age, race/ethnicity, and survey year, and stratified by gender. Age restriction laws were associated with a 47% (P < .001) lower indoor tanning prevalence among female high school students. Parental permission laws were not found to be associated with indoor tanning prevalence among either female or male high school students. Age restriction laws could contribute to less indoor tanning, particularly among female high school students. Such reductions may reduce the health and economic burden of skin cancer.

Remarkable reduction in the threshold voltage of pentacene-based thin film transistors with pentacene/CuPc sandwich configuration

NASA Astrophysics Data System (ADS)

Li, Yi; Liu, Qi; Cai, Jing; Li, Yun; Shi, Yi; Wang, Xizhang; Hu, Zheng

2014-06-01

This study investigates the remarkable reduction in the threshold voltage (VT) of pentacene-based thin film transistors with pentacene/copper phthalocyanine (CuPc) sandwich configuration. This reduction is accompanied by increased mobility and lowered sub-threshold slope (S). Sandwich devices coated with a 5 nm layer of CuPc layer are compared with conventional top-contact devices, and results indicate that VT decreased significantly from -20.4 V to -0.2 V, that mobility increased from 0.18 cm2/Vs to 0.51 cm2/Vs, and that S was reduced from 4.1 V/dec to 2.9 V/dec. However, the on/off current ratio remains at 105. This enhanced performance could be attributed to the reduction in charge trap density by the incorporated CuPc layer. Results suggest that this method is simple and effectively generates pentacene-based organic thin film transistors with high mobility and low VT.

Materials science and integration bases for fabrication of (BaxSr1-x)TiO3 thin film capacitors with layered Cu-based electrodes

NASA Astrophysics Data System (ADS)

Fan, W.; Kabius, B.; Hiller, J. M.; Saha, S.; Carlisle, J. A.; Auciello, O.; Chang, R. P. H.; Ramesh, R.

2003-11-01

The synthesis and fundamental material properties of layered TiAl/Cu/Ta electrodes were investigated to achieve the integration of Cu electrodes with high-dielectric constant (κ) oxide thin films for application to the fabrication of high-frequency devices. The Ta layer is an excellent diffusion barrier to inhibit deleterious Cu diffusion into the Si substrate, while the TiAl layer provides an excellent barrier against oxygen diffusion into the Cu layer to inhibit Cu oxidation during the growth of the high-κ layer in an oxygen atmosphere. Polycrystalline (BaxSr1-x)TiO3 (BST) thin films were grown on the Cu-based bottom electrode by rf magnetron sputtering at temperatures in the range 400-600 °C in oxygen, to investigate the performance of BST/Cu-based capacitors. Characterization of the Cu-based layered structure using surface analytical methods showed that two amorphous oxide layers were formed on both sides of the TiAl barrier, such that the oxide layer on the free surface of the TiAl layer correlates with TiAlOx, while the oxide layer at the TiAl/Cu interface is an Al2O3-rich layer. This double amorphous barrier layer structure effectively prevents oxygen penetration towards the underlying Cu and Ta layers. The TiAlOx interfacial layer, which has a relatively low dielectric constant compared with BST, reduced the total capacitance of the BST thin film capacitors. In addition, the layered electrode-oxide interface roughening observed during the growth of BST films at high temperature, due to copper grain growth, resulted in large dielectric loss on the fabricated BST capacitors. These problems were solved by growing the BST layer at 450 °C followed by a rapid thermal annealing at 700 °C. This process significantly reduced the thickness of the TiAlOx layer and interface roughness resulting in BST capacitors exhibiting properties suitable for the fabrication of high-performance high-frequency devices. In summary, relatively high dielectric constant (280), low

Investigations of rapid thermal annealing induced structural evolution of ZnO: Ge nanocomposite thin films via GISAXS

DOE Office of Scientific and Technical Information (OSTI.GOV)

Ceylan, Abdullah, E-mail: aceylanabd@yahoo.com; Ozcan, Yusuf; Orujalipoor, Ilghar

2016-06-07

In this work, we present in depth structural investigations of nanocomposite ZnO: Ge thin films by utilizing a state of the art grazing incidence small angle x-ray spectroscopy (GISAXS) technique. The samples have been deposited by sequential r.f. and d.c. sputtering of ZnO and Ge thin film layers, respectively, on single crystal Si(100) substrates. Transformation of Ge layers into Ge nanoparticles (Ge-np) has been initiated by ex-situ rapid thermal annealing of asprepared thin film samples at 600 °C for 30, 60, and 90 s under forming gas atmosphere. A special attention has been paid on the effects of reactive and nonreactivemore » growth of ZnO layers on the structural evolution of Ge-np. GISAXS analyses have been performed via cylindrical and spherical form factor calculations for different nanostructure types. Variations of the size, shape, and distributions of both ZnO and Ge nanostructures have been determined. It has been realized that GISAXS results are not only remarkably consistent with the electron microscopy observations but also provide additional information on the large scale size and shape distribution of the nanostructured components.« less

Appearance motives to tan and not tan: evidence for validity and reliability of a new scale.

PubMed

Cafri, Guy; Thompson, J Kevin; Roehrig, Megan; Rojas, Ariz; Sperry, Steffanie; Jacobsen, Paul B; Hillhouse, Joel

2008-04-01

Risk for skin cancer is increased by UV exposure and decreased by sun protection. Appearance reasons to tan and not tan have consistently been shown to be related to intentions and behaviors to UV exposure and protection. This study was designed to determine the factor structure of appearance motives to tan and not tan, evaluate the extent to which this factor structure is gender invariant, test for mean differences in the identified factors, and evaluate internal consistency, temporal stability, and criterion-related validity. Five-hundred eighty-nine females and 335 male college students were used to test confirmatory factor analysis models within and across gender groups, estimate latent mean differences, and use the correlation coefficient and Cronbach's alpha to further evaluate the reliability and validity of the identified factors. A measurement invariant (i.e., factor-loading invariant) model was identified with three higher-order factors: sociocultural influences to tan (lower order factors: media, friends, family, significant others), appearance reasons to tan (general, acne, body shape), and appearance reasons not to tan (skin aging, immediate skin damage). Females had significantly higher means than males on all higher-order factors. All subscales had evidence of internal consistency, temporal stability, and criterion-related validity. This study offers a framework and measurement instrument that has evidence of validity and reliability for evaluating appearance-based motives to tan and not tan.

High-Resolution AES Mapping and TEM Study of Cu(In,Ga)Se2 Thin Film Growth: Preprint

DOE Office of Scientific and Technical Information (OSTI.GOV)

Perkins, C. L.; Yan, Y.; Jones, K.

2001-10-01

Presented at 2001 NCPV Program Review Meeting: TEM and high-resolution AES mapping data on CIGS samples. The chalcopyrite Cu(In,Ga)Se{sub 2} (CIGS) shows promise as an absorber layer in thin polycrystalline solar cells, however, details of the PVD growth of this complicated material remain in a developing stage. Previous workers have postulated the existence of a thin film of liquid Cu{sub x}Se on the growing CIGS film, and that this layer acts as a reservoir of copper as well as a layer in which rapid mass transport is possible. In this paper we present transmission electron microscopy (TEM) and high resolutionmore » Auger electron spectroscopy (AES) mapping data taken on samples that had their growth interrupted at a stage when Cu{sub x}Se was expected to be present. The AES maps show CIGS grains which are highly enriched in copper relative to the rest of the CIGS film, and that these same areas contain almost no indium, results consistent with the presence of CuxSe. Small-area diffraction analysis and energy dispersive spectroscopy (EDS) performed on these same samples independently confirm the presence of Cu{sub x}Se at the surface of growing CIGS films.« less

Teens and Tanning Knowledge and Attitudes

PubMed Central

Levine, Vicki J.; Steuer, Alexa B.; Sedwick, Carly

2009-01-01

Background: The incidence of skin cancer, including melanoma, continues to increase. Teenagers are especially vulnerable, as are young females. The incidence of melanoma among young women in their twenties and thirties has begun to increase again. These young people are also the population that frequent tanning salons. Objective: This voluntary, anonymous, New York University, Institutional Review Board-approved survey was given to students in grades 9 through 12 to ascertain their understanding of what causes skin cancers and the dangers of excessive sun exposure and tanning salons. Methods and materials: An Institutional Review Board-approved, 22-question survey was administered anonymously to more than 450 students with 368 returned responses. The survey was administered to students in grades 9 through 12 at two high schools in New York and New Jersey. Results: More than 80 percent of students view movie stars as tan and almost 60 percent see “tan” people as better looking. In addition, more than 90 percent believe that a tan does not prevent further damage to the skin (as opposed to the customary belief that a “base” tan can protect against extreme sun exposures, such as when on a tropical vacation). There appears to be a disconnect between knowledge and sun tanning behaviors. Most teenagers still believe that tans are attractive and teenage girls continue to use tanning salons and tan naturally. We need to address the connection between sun tanning in youth and skin cancers years later. Legislation to limit access of tanning salons to teenagers needs to be enacted. PMID:20967182

Visible light responsive Cu2MoS4 nanosheets incorporated reduced graphene oxide for efficient degradation of organic pollutant

NASA Astrophysics Data System (ADS)

Rameshbabu, R.; Vinoth, R.; Navaneethan, M.; Harish, S.; Hayakawa, Y.; Neppolian, B.

2017-10-01

Visible light active copper molybdenum sulfide (Cu2MoS4) nanosheets were successfully anchored on reduced graphene oxide (rGO) using facile hydrothermal method. During the hydrothermal reaction, reduction of graphene oxide into rGO and the formation of Cu2MoS4 nanosheets were successfully obtained. The charge transfer interaction between the rGO sheets and Cu2MoS4 nanosheets extended the absorption to visible region in comparison with bare Cu2MoS4 nanosheets i.e without rGO sheets. Furthermore, the notable photoluminescence quenching observed for Cu2MoS4/rGO nanocomposite revealed the effective role of rGO towards the significant inhibition of electron-hole pair recombination. The photocatalytic efficiencies of bare Cu2MoS4 and Cu2MoS4/rGO nanocomposite was evaluated for the degradation of methyl orange dye under visible irradiation (λ > 420 nm). A maximum photodegradation efficiency of 99% was achieved for Cu2MoS4/rGO nanocomposite, while only 64% photodegradation was noted for bare Cu2MoS4. The enhanced optical absorption in visible region, high surface area, and low charge carrier recombination in the presence of rGO sheets were the main reasons for the enhancement in photodegardation of MO dye. In addition, the resultant Cu2MoS4/rGO nanocomposite was found to be reusable for five successive cycles without significant loss in its photocatalytic performance.

Internet advertising of artificial tanning in Australia.

PubMed

Team, Victoria; Markovic, Milica

2006-08-01

Artificial tanning, defined as deliberate exposure to ultraviolet rays produced by artificial tanning devices, is a new and emerging public health issue in Australia and globally. Epidemiological research suggests that artificial tanning may contribute to the incidence of melanoma, nonmelanoma skin cancer as well as other health problems. Given that Australia has a high incidence of skin cancer, we have undertaken a study to explore how artificial tanning has been promoted to its users. The aim was to analyze the completeness and accuracy of information about artificial tanning. A content analysis of web sites of tanning salons and distributors of tanning equipment in Australia was conducted. A total of 22 web sites were analyzed. None of the solarium operators or distributors of equipment provided full information about the risks of artificial tanning. Fifty-nine percent of web advertisements had no information and 41% provided only partial information regarding the risks of artificial tanning. Pictures with the image of bronze-tanned bodies, predominantly women, were used by all web advertisers. In light of the success of sun-safety campaigns in Australia, the findings of future epidemiological research on the prevalence of artificial tanning and sociological and anthropological research on why people utilize artificial tanning should be a basis for developing effective targeted health promotion on the elimination of artificial tanning in the country.

Adolescent attitudes towards tanning: does age matter?

PubMed Central

Dennis, Leslie K.; Kancherla, Vijaya; Snetselaar, Linda G

2012-01-01

Adolescents seem to be obsessed with tanning. One third of both adolescents and adults report sunbathing. On average, about 20% of adolescents report ever-using of artificial UV tanning devices with 15% currently using them. Tanning attitudes appear similar for adolescents and adults. The top three reasons for tanning included beliefs that a tan makes them more comfortable socializing with friends, looks better and is attractive. The top reason for using artificial UV tanning devices is also aesthetics, followed by relaxation. Other reasons for using artificial UV tanning devices include vacation preparation and to gain a protective base. Attitudes related to appearance that result in more frequent tanning may be difficult to change. PMID:22707979

Adolescent attitudes towards tanning: does age matter?

PubMed

Dennis, Leslie K; Kancherla, Vijaya; Snetselaar, Linda G

2009-12-01

Adolescents seem to be obsessed with tanning. One third of both adolescents and adults report sunbathing. On average, about 20% of adolescents report ever-using of artificial UV tanning devices with 15% currently using them. Tanning attitudes appear similar for adolescents and adults. The top three reasons for tanning included beliefs that a tan makes them more comfortable socializing with friends, looks better and is attractive. The top reason for using artificial UV tanning devices is also aesthetics, followed by relaxation. Other reasons for using artificial UV tanning devices include vacation preparation and to gain a protective base. Attitudes related to appearance that result in more frequent tanning may be difficult to change.

Fabrication of nanocrystal ink based superstrate-type CuInS₂ thin film solar cells.

PubMed

Cho, Jin Woo; Park, Se Jin; Kim, Woong; Min, Byoung Koun

2012-07-05

A CuInS₂ (CIS) nanocrystal ink was applied to thin film solar cell devices with superstrate-type configuration. Monodispersed CIS nanocrystals were synthesized by a colloidal synthetic route and re-dispersed in toluene to form an ink. A spray method was used to coat CIS films onto conducting glass substrates. Prior to CIS film deposition, TiO₂ and CdS thin films were also prepared as a blocking layer and a buffer layer, respectively. We found that both a TiO₂ blocking layer and a CdS buffer layer are necessary to generate photoresponses in superstrate-type devices. The best power conversion efficiency (∼1.45%) was achieved by the CIS superstrate-type thin film solar cell device with 200 and 100 nm thick TiO₂ and CdS films, respectively.

Evidence for filamentary superconductivity up to 220 K in oriented multiphase Y-Ba-Cu-O thin films

NASA Astrophysics Data System (ADS)

Schönberger, R.; Otto, H. H.; Brunner, B.; Renk, K. F.

1991-02-01

We report on the observation of filamentary superconductivity up to 220 K in multiphase Y-Ba-Cu-O materials that are deposited as highly oriented thin films on (110)-SrTiO 3 substrates by laser ablation from ceramic targets. The high temperature zero resistivity states are reproducible after temperature cycling down to 80 K for samples treated by a special oxygenation and ozonization process at 340 K and measured in a pure oxygen atmosphere. Our results on thin films confirm former experiments of J.T. Chen and co-workers obtained on ceramic samples with preferred crystallite orientation. A close connection between superconductivity and structural instabilities of most likely ferroic nature, which are observed more often for YBa 2Cu 3O 7 in a narrow temperature range near 220 K, is suggested.

Development of biodegradable metaloxide/polymer nanocomposite films based on poly-ε-caprolactone and terephthalic acid.

PubMed

Varaprasad, Kokkarachedu; Pariguana, Manuel; Raghavendra, Gownolla Malegowd; Jayaramudu, Tippabattini; Sadiku, Emmanuel Rotimi

2017-01-01

The present investigation describes the development of metal-oxide polymer nanocomposite films from biodegradable poly-ε-caprolactone, disposed poly(ethylene terephthalate) oil bottles monomer and zinc oxide-copper oxide nanoparticles. The terephthalic acid and zinc oxide-copper oxide nanoparticles were synthesized by using a temperature-dependent precipitation technique and double precipitation method, respectively. The terephthalic acid synthesized was confirmed by FTIR analysis and furthermore, it was characterized by thermal analysis. The as-prepared CuO-ZnO nanoparticles structure was confirmed by XRD analysis and its morphology was analyzed by SEM/EDS and TEM. Furthermore, the metal-oxide polymer nanocomposite films have excellent mechanical properties, with tensile strength and modulus better than pure films. The metal-oxide polymer nanocomposite films that were successfully developed show a relatively brighter colour when compared to CuO film. These new metal-oxide polymer nanocomposite films can replace many non-degradable plastics. The new metal-oxide polymer nanocomposite films developed are envisaged to be suitable for use in industrial and domestic packaging applications. Copyright © 2016 Elsevier B.V. All rights reserved.

Multi-functional properties of CaCu3Ti4O12 thin films

NASA Astrophysics Data System (ADS)

Felix, A. A.; Rupp, J. L. M.; Varela, J. A.; Orlandi, M. O.

2012-09-01

In this work, electric transport properties of CaCu3Ti4O12 (CCTO) thin films were investigated for resistive switching, rectifying and gas sensor applications. Single phase CCTO thin films were produced by polymeric precursor method (PPM) on different substrates and their electrical properties were studied. Films produced on LNO/Si substrates have symmetrical non-ohmic current-voltage characteristics, while films deposited on Pt/Si substrates have a highly asymmetrical non-ohmic behavior which is related to a metal-semiconductor junction formed at the CCTO/Pt interface. In addition, results confirm that CCTO has a resistive switching response which is enhanced by Schottky contacts. Sensor response tests revealed that CCTO films are sensitive to oxygen gas and exhibit n-type conductivity. These results demonstrate the versatility of CCTO thin film prepared by the PPM method for gas atmosphere or bias dependent resistance applications.

Positron Annihilation Spectroscopy as a Novel Interfacial Probe for Thin Polymeric Films and Nano-Composites

NASA Astrophysics Data System (ADS)

Awad, Somia; Chen, Hongmin; Maina, Grace; Lee, L. James; Gu, Xiaohong; Jean, Y. C.

2010-03-01

Positron annihilation spectroscopy (PAS) has been developed as a novel probe to characterize the sub-nanometer defect, free volume, profile from the surface, interfaces, and to the bulk in polymeric materials when a variable mono-energy slow positron beam is used. Free-volume hole sizes, fractions, and distributions are measurable as a function of depth at the high precision. PAS has been successfully used to study the interfacial properties of polymeric nanocomposites at different chemical bonding. In nano-scale thin polymeric films, such as in PS/SiO2, and PU/ZnO, significant variations of Tg as a function of depth and of wt% oxide are observed. Variations of Tg are dependent on strong or weak interactions between polymers and nano-scale oxides surfaces.

Greener Route for Synthesis of aryl and alkyl-14H-dibenzo [a.j] xanthenes using Graphene Oxide-Copper Ferrite Nanocomposite as a Recyclable Heterogeneous Catalyst

NASA Astrophysics Data System (ADS)

Kumar, Aniket; Rout, Lipeeka; Achary, Lakkoji Satish Kumar; Dhaka, Rajendra. S.; Dash, Priyabrat

2017-02-01

A facile, efficient and environmentally-friendly protocol for the synthesis of xanthenes by graphene oxide based nanocomposite (GO-CuFe2O4) has been developed by one-pot condensation route. The nanocomposite was designed by decorating copper ferrite nanoparticles on graphene oxide (GO) surface via a solution combustion route without the use of template. The as-synthesized GO-CuFe2O4 composite was comprehensively characterized by XRD, FTIR, Raman, SEM, EDX, HRTEM with EDS mapping, XPS, N2 adsorption-desorption and ICP-OES techniques. This nanocomposite was then used in an operationally simple, cost effective, efficient and environmentally benign synthesis of 14H-dibenzo xanthene under solvent free condition. The present approach offers several advantages such as short reaction times, high yields, easy purification, a cleaner reaction, ease of recovery and reusability of the catalyst by a magnetic field. Based upon various controlled reaction results, a possible mechanism for xanthene synthesis over GO-CuFe2O4 catalyst was proposed. The superior catalytic activity of the GO-CuFe2O4 nanocomposite can be attributed to the synergistic interaction between GO and CuFe2O4 nanoparticles, high surface area and presence of small sized CuFe2O4 NPs. This versatile GO-CuFe2O4 nanocomposite synthesized via combustion method holds great promise for applications in wide range of industrially important catalytic reactions.

Dielectric and relaxation properties of poly(o-anisidine)/graphene nanocomposite

NASA Astrophysics Data System (ADS)

Sangamithirai, D.; Narayanan, V.; Stephen, A.

2016-05-01

Poly(o-anisidine)/graphene (POA/GR) nanocomposite was synthesized via chemical oxidative polymerization of o-anisidine in the presence of graphene sheets in acidic medium. The electrical properties of the nanocomposite are studied using AC impedance spectroscopic technique. It has been found that the room temperature electrical conductivity value enhanced from 1.28 × 10-6 S cm-1 to 4.47 × 10-4 S cm-1 on addition of 10 wt % of graphene into the polymer. An analysis of real and imaginary parts of dielectric permittivity reveals that both ɛ` and ɛ״ increases with the decrease of frequency at all temperature levels. Frequency dependence of dielectric loss (tan δ) spectrum indicates that hopping frequency increases with temperature and the relaxation time decreases from 2.67 × 10-5 to 7.28 × 10-6 sec.

Magnetic field-directed hybrid anisotropic nanocomposites.

PubMed

Gong, Maogang; Zhang, Jingming; Ren, Shenqiang

2018-08-24

A facile bottom-up approach is developed to grow magnetic metallic Cu/FeCo (core/shell) nanowires, where their distribution and orientation can be controlled by magnetic field. The nanocomposites consisting of a ferroelectric polymer matrix and magnetic nanowire arrays exhibit the orientation-controlled anisotropy and interfacial magnetoelectric coupling effect.

Polyethylene organo-clay nanocomposites: the role of the interface chemistry on the extent of clay intercalation/exfoliation.

PubMed

Mainil, Michaël; Alexandre, Michaël; Monteverde, Fabien; Dubois, Philippe

2006-02-01

High density polyethylene (HDPE)/clay nanocomposites have been prepared using three different functionalized polyethylene compatibilizers: an ethylene/vinyl acetate copolymer, a polyethylene grafted with maleic anhydride functions and a (styrene-b-ethylene/butylene-b-styrene) block copolymer. The nanocomposites were prepared via two different routes: (1) the dispersion in HDPE of a masterbatch prepared from the compatibilizer and the clay or (2) the direct melt blending of the three components. For each compatibilizer, essentially intercalated nanocomposites were formed as determined by X-ray diffraction and transmission electron microscopy. With the ethylene/vinyl acetate copolymer, a significant delamination of the intercalated clay in thin stacks was observed. This dispersion of thin intercalated stacks within the polymer matrix allowed increasing significantly the stiffness and the flame resistance of the nanocomposite. A positive effect of shear rate and blending time has also been put into evidence, especially for the process based on the masterbatch preparation, improving both the formation of thin stacks of intercalated clay and the mechanical properties and the flame resistance of the formed nanocomposites.

Room-temperature Domain-epitaxy of Copper Iodide Thin Films for Transparent CuI/ZnO Heterojunctions with High Rectification Ratios Larger than 109

NASA Astrophysics Data System (ADS)

Yang, Chang; Kneiß, Max; Schein, Friedrich-Leonhard; Lorenz, Michael; Grundmann, Marius

2016-02-01

CuI is a p-type transparent conductive semiconductor with unique optoelectronic properties, including wide band gap (3.1 eV), high hole mobility (>40 cm2 V-1 s-1 in bulk), and large room-temperature exciton binding energy (62 meV). The difficulty in epitaxy of CuI is the main obstacle for its application in advanced solid-state electronic devices. Herein, room-temperature heteroepitaxial growth of CuI on various substrates with well-defined in-plane epitaxial relations is realized by reactive sputtering technique. In such heteroepitaxial growth the formation of rotation domains is observed and hereby systematically investigated in accordance with existing theoretical study of domain-epitaxy. The controllable epitaxy of CuI thin films allows for the combination of p-type CuI with suitable n-type semiconductors with the purpose to fabricate epitaxial thin film heterojunctions. Such heterostructures have superior properties to structures without or with weakly ordered in-plane orientation. The obtained epitaxial thin film heterojunction of p-CuI(111)/n-ZnO(00.1) exhibits a high rectification up to 2 × 109 (±2 V), a 100-fold improvement compared to diodes with disordered interfaces. Also a low saturation current density down to 5 × 10-9 Acm-2 is formed. These results prove the great potential of epitaxial CuI as a promising p-type optoelectronic material.

Quantifying point defects in Cu 2 ZnSn(S,Se) 4 thin films using resonant x-ray diffraction

DOE PAGES

Stone, Kevin H.; Christensen, Steven T.; Harvey, Steven P.; ...

2016-10-17

Cu 2ZnSn(S,Se)4 is an interesting, earth abundant photovoltaic material, but has suffered from low open circuit voltage. To better understand the film structure, we have measured resonant x-ray diffraction across the Cu and Zn K-edges for the device quality thin films of Cu 2ZnSnS4 (8.6% efficiency) and Cu 2ZnSn(S,Se)4 (3.5% efficiency). This approach allows for the confirmation of the underlying kesterite structure and quantification of the concentration of point defects and vacancies on the Cu, Zn, and Sn sublattices. Rietveld refinement of powder diffraction data collected at multiple energies is used to determine that there exists a high level ofmore » Cu Zn and Zn Cu defects on the 2c and 2d Wyckoff positions. We observe a significantly lower concentration of Zn Sn defects and Cu or Zn vacancies.« less

UV tanning advertisements in high school newspapers.

PubMed

Freeman, Scott; Francis, Shayla; Lundahl, Kristy; Bowland, Terri; Dellavalle, Robert P

2006-04-01

To examine the increasing use of UV tanning parlors by adolescents, despite the World Health Organization recommendation that no one under the age of 18 years use UV tanning devices. We examined tanning advertisements in a sample of public high school newspapers published between 2001 and 2005 in 3 Colorado counties encompassing the Denver metropolitan area. Tanning advertisements appeared in newspapers from 11 (48%) of 23 schools. Newspaper issues (N = 131) contained 40 advertisements placed by 18 tanning parlors. Advertisements commonly offered discounts (19 of 40) including unlimited tanning offers (15 of 40). Thirteen advertisements featured non-UV tanning treatments, and 2 advertisements mentioned parental consent or accompaniment for UV tanning. UV radiation, a classified carcinogen, is commonly and specifically marketed to adolescents through high school newspaper advertising. Public health skin cancer prevention policies should include the prohibition of UV tanning advertising to minors.

Indoor Tanning Dependence in Young Adult Women.

PubMed

Mays, Darren; Atkins, Michael B; Ahn, Jaeil; Tercyak, Kenneth P

2017-11-01

Background: There is mounting evidence that young people can develop a dependence on indoor tanning, but research on factors associated with indoor tanning dependence remains limited. Methods: This cross-sectional study investigated factors associated with indoor tanning dependence in a community sample of 389 non-Hispanic white young adult women ages 18 to 30 who had indoor tanned ≥1 time in the past year. Participants completed measures of indoor tanning dependence, including the modified CAGE and modified Diagnostic and Statistical Manual for Mental Disorders-IV psychiatric screening assessments, indoor tanning behavior and beliefs, and behavioral and psychiatric comorbidity. Results: Overall, 22.6% of the sample screened positive for indoor tanning dependence. In multivariable analyses, indoor tanning dependence was associated with younger age of indoor tanning initiation [adjusted odds ratio (aOR) = 0.79; P = 0.017], indoor tanning ≥20 times in the past year (aOR = 3.03; P = 0.015), stronger beliefs about the benefits of tanning (aOR = 2.15; P = 0.004), greater perceived susceptibility to indoor tanning risks (aOR = 2.72; P < 0.001), stronger beliefs about physical appearance (aOR = 1.73; P = 0.037), and depressive symptoms (aOR = 3.79; P < 0.001). Conclusions: Indoor tanning dependence among young, non-Hispanic white women is associated with behaviors that increase the risk of skin cancer, beliefs favoring the perceived benefits of tanning, and comorbid risks such as stronger beliefs about physical appearance and depressed mood. Impact: Comprehensive skin cancer prevention efforts should address indoor tanning dependence among young women and its leading risk factors. Cancer Epidemiol Biomarkers Prev; 26(11); 1636-43. ©2017 AACR . ©2017 American Association for Cancer Research.

Ultrahigh-Performance Cu2ZnSnS4 Thin Film and Its Application in Microscale Thin-Film Lithium-Ion Battery: Comparison with SnO2.

PubMed

Lin, Jie; Guo, Jianlai; Liu, Chang; Guo, Hang

2016-12-21

To develop a high-performance anode for thin-film lithium-ion batteries (TFBs, with a total thickness on the scale of micrometers), a Cu 2 ZnSnS 4 (CZTS) thin film is fabricated by magnetron sputtering and exhibits an ultrahigh performance of 950 mAh g -1 even after 500 cycles, which is the highest among the reported CZTS for lithium storage so far. The characterization and electrochemical tests reveal that the thin-film structure and additional reactions both contribute to the excellent properties. Furthermore, the microscale TFBs with effective footprints of 0.52 mm 2 utilizing the CZTS thin film as anode are manufactured by microfabrication techniques, showing superior capability than the analogous TFBs with the SnO 2 thin film as anode. This work demonstrates the advantages of exploiting thin-film electrodes and novel materials into micropower sources by electronic manufacture methods.

Effect of reinforcing particle type on morphology and age-hardening behavior of Al–4.5 wt.% Cu based nanocomposites synthesized through mechanical milling

DOE Office of Scientific and Technical Information (OSTI.GOV)

Mostaed, A., E-mail: alimostaed@yahoo.com; Saghafian, H.; Mostaed, E.

2013-02-15

The effects of reinforcing particle type (SiC and TiC) on morphology and precipitation hardening behavior of Al–4.5%Cu based nanocomposites synthesized via mechanical milling were investigated in the current work. In order to study the microstructure and morphology of mechanically milled powder, X-ray diffraction technique, scanning electron microscopy and high resolution transmission electron microscopy were utilized. Results revealed that at the early stages of mechanical milling, when reinforcing particles are polycrystal, the alloying process is enhanced more in the case of using the TiC particles as reinforcement. But, at the final stages of mechanical milling, when reinforcing particles are single crystal,more » the alloying process is enhanced more in the case of using the SiC ones. Transmission electron microscopy results demonstrated that Al–4.5 wt.%Cu based nanocomposite powders were synthesized and confirmed that the mutual diffusion of aluminum and copper occurs through the interfacial plane of (200). The hardness results showed that not only does introducing 4 vol.% of reinforcing particles (SiC or TiC) considerably decrease the porosity of the bulk composite samples, but also it approximately doubles the hardness of Al–4.5 wt.%Cu alloy (53.4 HB). Finally, apart from TEM and scanning electron microscopy observation which are localized, a decline in hardness in the TiC and SiC contained samples, respectively, after 1.5 and 2 h aging time at 473 K proves the fact that the size of SiC particles is smaller than the size of the TiC ones. - Highlights: ► HRTEM results show mutual diffusion of Al and Cu occurs through the (200) planes. ► TiC particles enhance alloying process more than the SiC ones at the early stages of MM. ► SiC particles enhance alloying process more than the TiC ones at the final stages of MM.« less

The Effects of Film Thickness and Evaporation Rate on Si-Cu Thin Films for Lithium Ion Batteries.

PubMed

Polat, B Deniz; Keles, Ozgul

2015-12-01

The reversible cyclability of Si based composite anodes is greatly improved by optimizing the atomic ratio of Si/Cu, the thickness and the evaporation rates of films fabricated by electron beam deposition method. The galvanostatic test results show that 500 nm thick flim, having 10%at. Cu-90%at. Si, deposited with a moderate evaporation rate (10 and 0.9 Å/s for Si and Cu respectively) delivers 2642.37 mAh g(-1) as the first discharge capacity with 76% Coulombic efficiency. 99% of its initial capacity is retained after 20 cycles. The electron conductive pathway and high mechanical tolerance induced by Cu atoms, the low electrical resistivity of the film due to Cu3Si particles, and the homogeneously distributed nano-sized/amorphous particles in the composite thin film could explain this outstanding electrochemical performance of the anode.

Non-conventional photocathodes based on Cu thin films deposited on Y substrate by sputtering

NASA Astrophysics Data System (ADS)

Perrone, A.; D'Elia, M.; Gontad, F.; Di Giulio, M.; Maruccio, G.; Cola, A.; Stankova, N. E.; Kovacheva, D. G.; Broitman, E.

2014-07-01

Copper (Cu) thin films were deposited on yttrium (Y) substrate by sputtering. During the deposition, a small central area of the Y substrate was shielded to avoid the film deposition and was successively used to study its photoemissive properties. This configuration has two advantages: the cathode presents (i) the quantum efficiency and the work function of Y and (ii) high electrical compatibility when inserted into the conventional radio-frequency gun built with Cu bulk. The photocathode was investigated by scanning electron microscopy to determine surface morphology. X-ray diffraction and atomic force microscopy studies were performed to compare the structure and surface properties of the deposited film. The measured electrical resistivity value of the Cu film was similar to that of high purity Cu bulk. Film to substrate adhesion was also evaluated using the Daimler-Benz Rockwell-C adhesion test method. Finally, the photoelectron performance in terms of quantum efficiency was obtained in a high vacuum photodiode cell before and after laser cleaning procedures. A comparison with the results obtained with a twin sample prepared by pulsed laser deposition is presented and discussed.

Thin films composed of multiwalled carbon nanotubes, gold nanoparticles and myoglobin for humidity detection at room temperature.

PubMed

Qi, Zhi-mei; Wei, Mingdeng; Honma, Itaru; Zhou, Haoshen

2007-02-02

Optically transparent and electrically conductive nanocomposite thin films consisting of multiwalled carbon nanotubes (MWCNTs), gold nanoparticles (GNPs) and myoglobin molecules that glue GNPs and MWCNTs together are fabricated for the first time on glass substrates from aqueous solution. The nanocomposite thin film is capable of varying its resistance, impedance or optical transmittance at room temperature in response to changes in ambient humidity. The conductometric sensitivity to relative humidity (RH) of the nanocomposite thin film is compared with those of the pure and Mb-functionalized MWCNT layers. The pure MWCNT layer shows a small increase in its resistance with increasing RH due to the effect of p-type semiconducting nanotubes present in the film. In contrast, a four times higher sensitivity to RH is observed for both the nanocomposite and Mb-functionalized MWCNT thin films. The sensitivity enhancement is attributable to swelling of the thin films induced by water absorption in the presence of Mb molecules, which increases the inter-nanotube spacing and thereby causes a further increase of the film resistance. A humidity change as low as DeltaRH=0.3 % has been readily detected by conductometry using the nanocomposite thin film.

Complementary Characterization of Cu(In,Ga)Se₂ Thin-Film Photovoltaic Cells Using Secondary Ion Mass Spectrometry, Auger Electron Spectroscopy, and Atom Probe Tomography.

PubMed

Jang, Yun Jung; Lee, Jihye; Jeong, Jeung-Hyun; Lee, Kang-Bong; Kim, Donghwan; Lee, Yeonhee

2018-05-01

To enhance the conversion performance of solar cells, a quantitative and depth-resolved elemental analysis of photovoltaic thin films is required. In this study, we determined the average concentration of the major elements (Cu, In, Ga, and Se) in fabricated Cu(In,Ga)Se2 (CIGS) thin films, using inductively coupled plasma atomic emission spectroscopy, X-ray fluorescence, and wavelengthdispersive electron probe microanalysis. Depth profiling results for CIGS thin films with different cell efficiencies were obtained using secondary ion mass spectrometry and Auger electron spectroscopy to compare the atomic concentrations. Atom probe tomography, a characterization technique with sub-nanometer resolution, was used to obtain three-dimensional elemental mapping and the compositional distribution at the grain boundaries (GBs). GBs are identified by Na increment accompanied by Cu depletion and In enrichment. Segregation of Na atoms along the GB had a beneficial effect on cell performance. Comparative analyses of different CIGS absorber layers using various analytical techniques provide us with understanding of the compositional distributions and structures of high efficiency CIGS thin films in solar cells.

Scalable fabrication of SnO2 thin films sensitized with CuO islands for enhanced H2S gas sensing performance

NASA Astrophysics Data System (ADS)

Van Toan, Nguyen; Chien, Nguyen Viet; Van Duy, Nguyen; Vuong, Dang Duc; Lam, Nguyen Huu; Hoa, Nguyen Duc; Van Hieu, Nguyen; Chien, Nguyen Duc

2015-01-01

The detection of H2S, an important gaseous molecule that has been recently marked as a highly toxic environmental pollutant, has attracted increasing attention. We fabricate a wafer-scale SnO2 thin film sensitized with CuO islands using microelectronic technology for the improved detection of the highly toxic H2S gas. The SnO2-CuO island sensor exhibits significantly enhanced H2S gas response and reduced operating temperature. The thickness of CuO islands strongly influences H2S sensing characteristics, and the highest H2S gas response is observed with 20 nm-thick CuO islands. The response value (Ra/Rg) of the SnO2-CuO island sensor to 5 ppm H2S is as high as 128 at 200 °C and increases nearly 55-fold compared with that of the bare SnO2 thin film sensor. Meanwhile, the response of the SnO2-CuO island sensor to H2 (250 ppm), NH3 (250 ppm), CO (250 ppm), and LPG (1000 ppm) are low (1.3-2.5). The enhanced gas response and selectivity of the SnO2-CuO island sensor to H2S gas is explained by the sensitizing effect of CuO islands and the extension of electron depletion regions because of the formation of p-n junctions.

[What nosographic framework for excessive tanning?].

PubMed

Petit, A; Karila, L; Lejoyeux, M

2014-04-01

Socially valorised tanning, like other forms of behaviour, can take on an addictive aspect. Excessive tanning, defined by the presence of impulsivity and repetition of tanning that leads to personal distress, is a psychiatric disorder that has only recently been recognized. This finding is based on the observations of many dermatologists who report an addictive relationship in their patients with tanning cabins despite announcement of the diagnosis of malignant melanoma. This article attempts to synthesize the existing literature on excessive tanning and addiction to investigate possible associations. This review focuses on the prevalence, clinical features, aetiology, and treatment of this disorder. The literature review was conducted from 1983 to 2012, using PubMed, Google Scholar, EMBASE, and PsycInfo, using the following keywords alone or combined: Tanning, Addiction, Sunbeds, Skin cancer prevention, and Treatment. We investigated different models to determine how excessive tanning met these criteria. Excessive Tanning was described in the 2000s by an American dermatologist, Carolyn Heckman. Wartham et al. were the first to have proposed a theoretical framework for addiction to sunbathing, as well as two scales (m CAGE and m DSM IV) for the diagnosis and to assess the degree of addiction. These diagnostic criteria describe the craving like-symptoms, the feeling of losing control, or the continuation of the behavior despite knowledge of negative consequences. Excessive Tanning is not present in the classifications of the DSM or ICD, but may be related to Addiction, Obsessive-Compulsive Disorder, Impulse control disorders, Anorexia, or Body Dysmorphic Disorder. Excessive tanning can be included in the spectrum of behavioural addictions due its clinical characteristics in common with classics addictive disorders. They are a variety of other models, which may offer an explanation for or insight into tanning behaviour. Further studies must be controlled, notably on

Strengthening of Aluminum Wires Treated with A206/Alumina Nanocomposites.

PubMed

Florián-Algarín, David; Marrero, Raúl; Li, Xiaochun; Choi, Hongseok; Suárez, Oscar Marcelo

2018-03-10

This study sought to characterize aluminum nanocomposite wires that were fabricated through a cold-rolling process, having potential applications in TIG (tungsten inert gas) welding of aluminum. A206 (Al-4.5Cu-0.25Mg) master nanocomposites with 5 wt % γAl₂O₃ nanoparticles were first manufactured through a hybrid process combining semi-solid mixing and ultrasonic processing. A206/1 wt % γAl₂O₃ nanocomposites were fabricated by diluting the prepared master nanocomposites with a monolithic A206 alloy, which was then added to a pure aluminum melt. The fabricated Al-γAl₂O₃ nanocomposite billet was cold-rolled to produce an Al nanocomposite wire with a 1 mm diameter and a transverse area reduction of 96%. Containing different levels of nanocomposites, the fabricated samples were mechanically and electrically characterized. The results demonstrate a significantly higher strength of the aluminum wires with the nanocomposite addition. Further, the addition of alumina nanoparticles affected the wires' electrical conductivity compared with that of pure aluminum and aluminum-copper alloys. The overall properties of the new material demonstrate that these wires could be an appealing alternative for fillers intended for aluminum welding.

Strengthening of Aluminum Wires Treated with A206/Alumina Nanocomposites

PubMed Central

Marrero, Raúl; Li, Xiaochun; Choi, Hongseok

2018-01-01

This study sought to characterize aluminum nanocomposite wires that were fabricated through a cold-rolling process, having potential applications in TIG (tungsten inert gas) welding of aluminum. A206 (Al-4.5Cu-0.25Mg) master nanocomposites with 5 wt % γAl2O3 nanoparticles were first manufactured through a hybrid process combining semi-solid mixing and ultrasonic processing. A206/1 wt % γAl2O3 nanocomposites were fabricated by diluting the prepared master nanocomposites with a monolithic A206 alloy, which was then added to a pure aluminum melt. The fabricated Al–γAl2O3 nanocomposite billet was cold-rolled to produce an Al nanocomposite wire with a 1 mm diameter and a transverse area reduction of 96%. Containing different levels of nanocomposites, the fabricated samples were mechanically and electrically characterized. The results demonstrate a significantly higher strength of the aluminum wires with the nanocomposite addition. Further, the addition of alumina nanoparticles affected the wires’ electrical conductivity compared with that of pure aluminum and aluminum–copper alloys. The overall properties of the new material demonstrate that these wires could be an appealing alternative for fillers intended for aluminum welding. PMID:29534441

A longitudinal test of the Comprehensive Indoor Tanning Expectations Scale: The importance of affective beliefs in predicting indoor tanning behavior.

PubMed

Myrick, Jessica Gall; Noar, Seth M; Kelley, Dannielle; Zeitany, Alexandra E; Morales-Pico, Brenda M; Thomas, Nancy E

2017-01-01

In order to better understand drivers of dangerous indoor tanning behaviors, researchers developed the Comprehensive Indoor Tanning Expectations scale. To examine the longitudinal effectiveness of Comprehensive Indoor Tanning Expectations, we surveyed young women in the Southeastern United States at two time points ( N = 553). The scale demonstrated strong test-retest reliability. Participants who believed indoor tanning would improve their mood and afford social approval were significantly more likely to tan 6 months later, while participants who believed indoor tanning leads to psychological/physical discomfort were significantly less likely to tan 6 months later. Knowing the psychological bases for indoor tanning can inform intervention and message design.

Optimization of high quality Cu2ZnSnS4 thin film by low cost and environment friendly sol-gel technique for thin film solar cells applications

NASA Astrophysics Data System (ADS)

Chaudhari, J. J.; Joshi, U. S.

2018-05-01

In this study kesterite Cu2ZnSnS4 (CZTS) thin films suitable for absorber layer in thin film solar cells (TFSCs) were successfully fabricated on glass substrate by sol-gel method. The effects of complexing agent on formation of CZTS thin films have been investigated. X-ray diffraction (XRD) analysis confirms formation of polycrystalline CZTS thin films with single phase kesterite structure. XRD and Raman spectroscopy analysis of CZTS thin films with optimized concentration of complexing agent confirmed formation of kesterite phase in CZTS thin films. The direct optical band gap energy of CZTS thin films is found to decrease from 1.82 to 1.50 eV with increase of concentration of complexing agent triethanolamine. Morphological analysis of CZTS thin films shows smooth, uniform and densely packed CZTS grains and increase in the grain size with increase of concentration of complexing agent. Hall measurements revealed that concentration of charge carrier increases and resistivity decreases in CZTS thin films as amount of complexing agent increases.

Thin films of the Bi2Sr2Ca2Cu3O(x) superconductor

NASA Technical Reports Server (NTRS)

Mei, YU; Luo, H. L.; Hu, Roger

1990-01-01

Using RF sputtering technique, thin films of near single phase Bi2Sr2Ca2Cu3O(x) were successfully prepared on SrTiO3(100), MgO(100), and LaAlO3(012) substrates. Zero resistance of these films occurred in the range of 90-105 K.

Nanocomposite copolymer thin-film sensor for detection of escherichia coli

NASA Astrophysics Data System (ADS)

Mathur, Prafull; Misra, S. C. K.; Yadav, Maneesha; Bawa, S. S.; Gupta, A. K.

2006-01-01

The majority of human diseases associated with microbial contaminated water are infectious in nature and the associated pathogen includes bacteria, fungi, viruses and protozoa. Water contaminated with bacteria can cause a number of food-borne and water-borne diseases. The waterborne transmission is highly effective means of spreading infectious agents to a large portion of population; this includes water and milk too. Waterborne infections are recognized as resulting either from ingestion of contaminated water or ice, food items, which have, came into contact with microbial contaminated water (occurring through bathing and recreational activities) etc. The detection of E. coli in food and water is normally carried out by culturing methods, which normally take 3-6 days, These methods are complicated and time-consuming in spite of their correctness, and cannot easily meet inspection demands on E. coli. Hence, an establishment of rapid detection methods for E. coli is strongly required. We have developed highly sensitive and cost effective solid sate sensors prepared from vacuum evaporated thin films of nanocomposite copolymer detection of presence of E. coli vapors in the air within 20 seconds. These sensors operate at room temperature. The preparation, optical, electrical, and structural characterization and behavioral acceptance test on the microorganism sensing properties of these sensors are reported here.

Processing approach towards the formation of thin-film Cu(In,Ga)Se2

DOEpatents

Beck, Markus E.; Noufi, Rommel

2003-01-01

A two-stage method of producing thin-films of group IB-IIIA-VIA on a substrate for semiconductor device applications includes a first stage of depositing an amorphous group IB-IIIA-VIA precursor onto an unheated substrate, wherein the precursor contains all of the group IB and group IIIA constituents of the semiconductor thin-film to be produced in the stoichiometric amounts desired for the final product, and a second stage which involves subjecting the precursor to a short thermal treatment at 420.degree. C.-550.degree. C. in a vacuum or under an inert atmosphere to produce a single-phase, group IB-III-VIA film. Preferably the precursor also comprises the group VIA element in the stoichiometric amount desired for the final semiconductor thin-film. The group IB-IIIA-VIA semiconductor films may be, for example, Cu(In,Ga)(Se,S).sub.2 mixed-metal chalcogenides. The resultant supported group IB-IIIA-VIA semiconductor film is suitable for use in photovoltaic applications.

Photoinduced Br Desorption from CsBr Thin Films Grown on Cu(100)

DOE Office of Scientific and Technical Information (OSTI.GOV)