temperature hydrogen attack: Topics by Science.gov

Sample records for temperature hydrogen attack

Hydrogen attack - Influence of hydrogen sulfide. [on carbon steel

NASA Technical Reports Server (NTRS)

Eliezer, D.; Nelson, H. G.

1978-01-01

An experimental study is conducted on 12.5-mm-thick SAE 1020 steel (plain carbon steel) plate to assess hydrogen attack at room temperature after specimen exposure at 525 C to hydrogen and a blend of hydrogen sulfide and hydrogen at a pressure of 3.5 MN/sq m for exposure times up to 240 hr. The results are discussed in terms of tensile properties, fissure formation, and surface scales. It is shown that hydrogen attack from a high-purity hydrogen environment is severe, with the formation of numerous methane fissures and bubbles along with a significant reduction in the room-temperature tensile yield and ultimate strengths. However, no hydrogen attack is observed in the hydrogen/hydrogen sulfide blend environment, i.e. no fissure or bubble formation occurred and the room-temperature tensile properties remained unchanged. It is suggested that the observed porous discontinuous scale of FeS acts as a barrier to hydrogen entry, thus reducing its effective equilibrium solubility in the iron lattice. Therefore, hydrogen attack should not occur in pressure-vessel steels used in many coal gasification processes.
Fundamental studies of hydrogen attack in carbon-0.5molybdenum steel and weldments applied in petroelum and petrochemical industries

NASA Astrophysics Data System (ADS)

Liu, Peng

High temperature hydrogen attack (HTHA) is a form of surface decarburization, internal decarburization, and/or intergranular cracking in steels exposed to high temperature (>400°F) and high hydrogen pressure. Hydrogen attack is an irreversible process which can cause permanent damage resulting in degradation of mechanical properties and failures such as leakage, bursting, fire, and/or explosion. The continuous progression of hydrogen attack in C-0.5Mo steel and weldments below the C-0.5Mo Nelson Curve has caused a significant concern for the integrity and serviceability of C-0.5Mo steel utilized for pressure vessels and piping in the petroleum refinery and petrochemical industries. A state-of-the-art literature review was implemented to provide a comprehensive overview of the published research efforts on hydrogen attack studies. The evolution of "Nelson Curves" for carbon steel, C-0.5Mo, and Cr-Mo steels was historically reviewed in regard to design applications and limitations. Testing techniques for hydrogen attack assessment were summarized under the categories of hydrogen exposure testing, mechanical evaluation, and dilatometric swelling testing. In accord with the demands of these industries, fundamental studies of hydrogen attack in C-0.5Mo steel and weldments were accomplished in terms of quantitative methodologies for hydrogen damage evaluation; hydrogen damage assessment of service exposed weldments and autoclave exposed materials; effects of carbon and alloying elements, heat treatments, hot and cold working, welding processes and postweld heat treatment (PWHT) on hydrogen attack susceptibility; development of continuous cooling transformation (CCT) diagrams for C-0.5Mo base metals and the coarse grained heat-affected zone (CGHAZ); carbide evaluation for the C-0.5Mo steel after service exposure and heat treatment; methane evolution by the reaction of hydrogen and carbides; hydrogen diffusion and methane pressure through the wall thickness of one-sided hydrogen exposure assembly; hydrogen attack mechanism and hydrogen attack limit modeling.
Hydrogen attack in Cr-Mo steels. [3Cr-1. 5Mo and 2. 25Cr-1Mo steels

DOE Office of Scientific and Technical Information (OSTI.GOV)

Ruoff, S.; Stone, D.; Wanagel, J.

Experiments conducted upon 3Cr-1.5Mo steel at elevated temperatures (600 C), and high pressure hydrogen (2000 psi), have shown a greater resistence to hydrogen attack compared with similar studies of 2.25Cr-lMo steels. Hydrogen exposure tests with and without an applied stress have been performed on both types of steels. Results of similar conditions show clear evidence of hydrogen attack in 2.25Cr-lMo steel, however, for the 3Cr-1.5Mo steel with exposure time up to 80 days without an applied stress no evidence of hydrogen attack is observed. For stress-rupture tests using stresses of 14 and 16 ksi, the 3Cr-1.5Mo steel showed no effectsmore » of hydrogen attack, and no damage was observed using a SEM.« less
Fractography of the high temperature hydrogen attack of a medium carbon steel

NASA Technical Reports Server (NTRS)

Melson, H. G.; Moorhead, R. D.

1975-01-01

Microscopic fracture processes were studied which are associated with hydrogen attack of a medium carbon steel in a well-controlled, high-temperature, high-purity hydrogen environment. Exposure to a hydrogen pressure and temperature of 3.5 MN/m2 and 575 C was found to degrade room temperature tensile properties with increasing exposure time. After 408 hr, yield and ultimate strengths were reduced by more than 40 percent and elongation was reduced to less than 2 percent. Initial fissure formation was found to be associated with manganese rich particles, most probably manganese oxide, aligned in the microstructure during the rolling operation. Fissure growth was found to be associated with a reduction in carbide content of the microstructure and was inhibited by the depletion of carbon. The interior surfaces of sectioned fissures or bubbles exhibit both primary and secondary cracking by intergranular separation. The grain surfaces were rough and rounded, suggesting a diffusion-associated separation process. Specimens that failed at room temperature after exposure to hydrogen were found to exhibit mixed mode fracture having varying amounts of intergranular separation, dimple formation, and cleavage, depending on exposure time.
Fractography of the high temperature hydrogen attack of a medium carbon steel

NASA Technical Reports Server (NTRS)

Nelson, H. G.; Moorhead, R. D.

1976-01-01

Results are reported for an experimental study of the microscopic fracture processes associated with hydrogen attack of a commercially produced plain carbon steel in a well-controlled high-temperature hydrogen environment of high purity. In the experiments, sheet samples were exposed to laboratory-grade hydrogen at a pressure of 3.5 MN/sq m and a temperature of 575 C. The fractography of gas-filled fissures and failed tension specimens is analyzed in an effort to identify any predominant microstructural defect associated with fissure formation, the prevalent modes of fracture, and the contribution of gas-filled fissures to the overall failure process. It is found that the tensile properties of the examined steel were significantly degraded after as few as 136 hr of exposure to a high-purity hydrogen atmosphere at 575 C; that the yield strength, ultimate strength, and elongation at fracture were all reduced progressively with increasing exposure time; and that the yield and ultimate strengths were reduced more than 40% after 408 hr while elongation was reduced to less than 2%.
Effect of hydrogen on the strength and microstructure of selected ceramics

NASA Technical Reports Server (NTRS)

Herbell, Thomas P.; Eckel, Andrew J.; Hull, David R.; Misra, Ajay K.

1990-01-01

Ceramics in monolithic form and as composite constituents in the form of fibers, matrices, and coatings are currently being considered for a variety of high-temperature applications in aeronautics and space. Many of these applications involve exposure to a hydrogen-containing environment. The compatibility of selected ceramics in gaseous high-temperature hydrogen is assessed. Environmental stability regimes for the long term use of ceramic materials are defined by the parameters of temperature, pressure, and moisture content. Thermodynamically predicted reactions between hydrogen and several monolithic ceramics are compared with actual performance in a controlled environment. Morphology of hydrogen attack and the corresponding strength degradation is reported for silicon carbide, silicon nitride, alumina, magnesia, and mullite.
Ultrasonic and metallographic studies on AISI 4140 steel exposed to hydrogen at high pressure and temperature

NASA Astrophysics Data System (ADS)

Oruganti, Malavika

This thesis conducts an investigation to study the effects of hydrogen exposure at high temperature and pressure on the behavior of AISI 4140 steel. Piezoelectric ultrasonic technique was primarily used to evaluate surface longitudinal wave velocity and defect geometry variations, as related to time after exposure to hydrogen at high temperature and pressure. Critically refracted longitudinal wave technique was used for the former and pulse-echo technique for the latter. Optical microscopy and scanning electron microscopy were used to correlate the ultrasonic results with the microstructure of the steel and to provide better insight into the steel behavior. The results of the investigation indicate that frequency analysis of the defect echo, determined using the pulse-echo technique at regular intervals of time, appears to be a promising tool for monitoring defect growth induced by a high temperature and high pressure hydrogen-related attack.
Effect of deoxidation practice and heat treatment on the hydrogen attack of carbon steels

NASA Astrophysics Data System (ADS)

López, Hugo F.

1987-11-01

The hydrogen attack (HA) kinetics of an electroslag refined (ESR) and a rare earth metal (REM)-treated steel in the Q. and T. condition were investigated by a highly sensitive dilatometer. Measured activation energies for bubble growth of 108 to 203 kJ/mol and pressure exponents of 0.9 to 1.6 are rationalized in terms of surface or grain boundary self-diffusion of iron as the rate controlling mechanisms depending on the external hydrogen pressure and temperature. Comparisons of the HA susceptibility of these steels with published work show that although the HA resistance of the ESR steel is not influenced by the heat treatment, the REM steel shows a significant decrease in the rate of sample expansion. SEM observations indicate that the improvement in the HA resistance of the REM steel is related to the presence of a very low density of methane bubbles.
Wall-temperature effects on the aerodynamics of a hydrogen-fueled transport concept in Mach 8 blowdown and shock tunnels

NASA Technical Reports Server (NTRS)

Penland, J. A.; Marcum, D. C., Jr.; Stack, S. H.

1983-01-01

Results are presented from two separate tests on the same blended wing-body hydrogen fueled transport model at a Mach number of about 8 and a range of Reynolds numbers (based on theoretical body length) of 0.597 x 10 to the 6th power to about 156.22 x 10 to the 6th power. Tests were made in conventional hypersonic blowdown tunnel and a hypersonic shock tunnel at angles of attack of -2 deg to about 8 deg, with an extensive study made at a constant angle of attack of 3 deg. The model boundary-layer flow varied from laminar at the lower Reynolds numbers to predominantly turbulent at the higher Reynolds numbers. Model wall temperatures and stream static temperatures varied widely between the two tests, particularly at the lower Reynolds numbers. These temperature differences resulted in marked variations of the axial-force coefficients between the two tests, due in part to the effects of induced pressure and viscous interaction variations. The normal-force coefficient was essentially independent of Reynolds number. Analysis of results utilized current theoretical computer programs and basic boundary-layer theory.
Effect of Reynolds number variation on aerodynamics of a hydrogen-fueled transport concept at Mach 6

NASA Technical Reports Server (NTRS)

Penland, Jim A.; Marcum, Don C., Jr.

1987-01-01

Two separate tests have been made on the same blended wing-body hydrogen-fueled transport model at a Mach number of about 6 and a range of Reynolds number (based on theoretical body length) of 1.577 to 55.36 X 10 to the 6th power. The results of these tests, made in a conventional hypersonic blowdown tunnel and a hypersonic shock tunnel, are presented through a range of angle of attack from -1 to 8 deg, with an extended study at a constant angle of attack of 3 deg. The model boundary layer flow appeared to be predominately turbulent except for the low Reynolds number shock tunnel tests. Model wall temperatures varied considerably; the blowdown tunnel varied from about 255 F to 340 F, whereas the shock tunnel had a constant 70 F model wall temperature. The experimental normal-force coefficients were essentially independent of Reynolds number. A current theoretical computer program was used to study the effect of Reynolds number. Theoretical predictions of normal-force coefficients were good, particularly at anticipated cruise angles of attack, that is 2 to 5 deg. Axial-force coefficients were generally underestimated for the turbulent skin friction conditions, and pitching-moment coefficients could not be predicted reliably.
The hydrogen embrittlement of titanium-based alloys

NASA Astrophysics Data System (ADS)

Tal-Gutelmacher, Ervin; Eliezer, Dan

2005-09-01

Titanium-based alloys provide an excellent combination of a high strength/weight ratio and good corrosion behavior, which makes these alloys among the most important advanced materials for a variety of aerospace, marine, industrial, and commercial applications. Although titanium is considered to be reasonably resistant to chemical attack, severe problems can arise when titanium-based alloys come in contact with hydrogen-containing environments, where they can pick up large amounts of hydrogen, especially at elevated temperatures. The severity and the extent of the hydrogen interaction with titanium-based alloys are directly related to the microstructure and composition of the titanium alloys. This paper addresses the hydrogen embrittlement of titanium-based alloys. The hydrogen-titanium interaction is reviewed, including the solubility of hydrogen in α and β phases of titanium and hydride formation. Also, the paper summarizes the detrimental effects of hydrogen in different titanium alloys.
Chemical structural analysis of diamondlike carbon films: I. Surface growth model

NASA Astrophysics Data System (ADS)

Takabayashi, Susumu; Ješko, Radek; Shinohara, Masanori; Hayashi, Hiroyuki; Sugimoto, Rintaro; Ogawa, Shuichi; Takakuwa, Yuji

2018-02-01

The surface growth mechanisms of diamondlike carbon (DLC) films has been clarified. DLC films were synthesized in atmospheres with a fixed methane-to-argon ratio at different temperatures up to 700 °C by the photoemission-assisted glow discharge of photoemission-assisted plasma-enhanced chemical vapor deposition. The electrical resistivity of the films decreased logarithmically as the synthesis temperature was increased. Conversely, the dielectric constant of the films increased and became divergent at high temperature. However, the very high electrical resistivity of the film synthesized at 150 °C was retained even after post-annealing treatments at temperatures up to 500 °C, and divergence of the dielectric constant was not observed. Such films exhibited excellent thermal stability and retained large amounts of hydrogen, even after post-annealing treatments. These results suggest that numerous hydrogen atoms were incorporated into the DLC films during synthesis at low temperatures. Hydrogen atoms terminate carbon dangling bonds in the films to restrict π-conjugated growth. During synthesis at high temperature, hydrogen was desorbed from the interior of the growing films and π-conjugated conductive films were formed. Moreover, hydrogen radicals were chemisorbed by carbon atoms at the growing DLC surface, leading to removal of carbon atoms from the surface as methane gas. The methane molecules decomposed into hydrocarbons and hydrogen radicals through the attack of electrons above the surface. Hydrogen radicals contributed to the etching reaction cycle of the film; the hydrocarbon radicals were polymerized by reacting with other radicals and the methane source. The polymer radicals remained above the film, preventing the supply of the methane source and disrupting the action of argon ions. At high temperatures, the resultant DLC films were rough and thin.
Complexes and saddle point structures, vibrational frequencies and relative energies of intermediates for CH2Br + HBr «-» CH3Br + Br

NASA Astrophysics Data System (ADS)

Espinosa-Garcia, J.

Ab initio molecular orbital theory was used to study parts of the reaction between the CH2Br radical and the HBr molecule, and two possibilities were analysed: attack on the hydrogen and attack on the bromine of the HBr molecule. Optimized geometries and harmonic vibrational frequencies were calculated at the second-order Moller-Plesset perturbation theory levels, and comparison with available experimental data was favourable. Then single-point calculations were performed at several higher levels of calculation. In the attack on the hydrogen of HBr, two stationary points were located on the direct hydrogen abstraction reaction path: a very weak hydrogen bonded complex of reactants, C···HBr, close to the reactants, followed by the saddle point (SP). The effects of level of calculation (method + basis set), spin projection, zeropoint energy, thermal corrections (298K), spin-orbit coupling and basis set superposition error (BSSE) on the energy changes were analysed. Taking the reaction enthalpy (298K) as reference, agreement with experiment was obtained only when high correlation energy and large basis sets were used. It was concluded that at room temperature (i.e., with zero-point energy and thermal corrections), when the BSSE was included, the complex disappears and the activation enthalpy (298K) ranges from 0.8kcal mol-1 to 1.4kcal mol-1 above the reactants, depending on the level of calculation. It was concluded also that this result is the balance of a complicated interplay of many factors, which are affected by uncertainties in the theoretical calculations. Finally, another possible complex (X complex), which involves the alkyl radical being attracted to the halogen end of HBr (C···BrH), was explored also. It was concluded that this X complex does not exist at room temperature.
Comparative structural and electronic studies of hydrogen interaction with isolated versus ordered silicon nanoribbons grown on Ag(110)

NASA Astrophysics Data System (ADS)

Dávila, M. E.; Marele, A.; De Padova, P.; Montero, I.; Hennies, F.; Pietzsch, A.; Shariati, M. N.; Gómez-Rodríguez, J. M.; Le Lay, G.

2012-09-01

We have investigated the geometry and electronic structure of two different types of self-aligned silicon nanoribbons (SiNRs), forming either isolated SiNRs or a self-assembled 5 × 2/5 × 4 grating on an Ag(110) substrate, by scanning tunnelling microscopy and high resolution x-ray photoelectron spectroscopy. At room temperature we further adsorb on these SiNRs either atomic or molecular hydrogen. The hydrogen absorption process and hydrogenation mechanism are similar for isolated or 5 × 2/5 × 4 ordered SiNRs and are not site selective; the main difference arises from the fact that the isolated SiNRs are more easily attacked and destroyed faster. In fact, atomic hydrogen strongly interacts with any Si atoms, modifying their structural and electronic properties, while molecular hydrogen has first to dissociate. Hydrogen finally etches the Si nanoribbons and their complete removal from the Ag(110) surface could eventually be expected.
Hydrogen storage in graphite nanofibers: effect of synthesis catalyst and pretreatment conditions.

PubMed

Lueking, Angela D; Yang, Ralph T; Rodriguez, Nelly M; Baker, R Terry K

2004-02-03

A series of graphite nanofibers (GNFs) that were subjected to various pretreatments were used to determine how modifications in the carbon structure formed during either synthesis or pretreatment steps results in active or inactive materials for hydrogen storage. The nanofibers possessing a herringbone structure and a high degree of defects were found to exhibit the best performance for hydrogen storage. These materials were exposed to several pretreatment procedures, including oxidative, reductive, and inert environments. Significant hydrogen storage levels were found for several in situ pretreatments. Examination of the nanofibers by high-resolution transmission electron microscopy (TEM) after pretreatment and subsequent hydrogen storage revealed the existence of edge attack and an enhancement in the generation of structural defects. These findings suggest that pretreatment in certain environments results in the creation of catalytic sites that are favorable toward hydrogen storage. The best pretreatment resulted in a 3.8% hydrogen release after exposure at 69 bar and room temperature.
The stress corrosion resistance and the cryogenic temperature mechanical properties of annealed Nitronic 60 bar material

NASA Technical Reports Server (NTRS)

Montano, J. W. L.

1977-01-01

Ambient and cryogenic temperature mechanical properties and the ambient temperature stress corrosion properties of annealed, straightened, and centerless ground Nitronic 60 stainless steel alloy bar material are presented. The mechanical properties of longitudinal specimens were evaluated at test temperatures from ambient to liquid hydrogen. The tensile test data indicated increasing strength with decreasing temperature to -196 C. Below liquid nitrogen temperature the smooth tensile and notched tensile strengths decreased slightly while the elongation and reduction of area decreased drastically. The Charpy V-notched impact energy decreased steadily with decreasing test temperature. Stress corrosion tests were performed on longitudinal tensile specimens and transverse C-ring specimens exposed to: alternate immersion in a 3.5% NaCl bath; humidity cabinet; and a 5% salt spray atmosphere. The longitudinal tensile specimens experienced no corrosive attack. Approximately 3/4 of the transverse C-rings exposed to alternate immersion and to salt spray experienced a pitting attack on the top and bottom ends. Additional stress corrosion tests were performed on transverse tensile specimens. No failures occurred in the 90% stressed specimens exposed for 90 days in the alternate immersion and salt spray environments
Prediction of Failure Due to Thermal Aging, Corrosion and Environmental Fracture in Amorphous and Titanium Alloys

DOE Office of Scientific and Technical Information (OSTI.GOV)

Farmer, J C

2003-04-15

DARPA is exploring a number of advanced materials for military applications, including amorphous metals and titanium-based alloys. Equipment made from these materials can undergo degradation due to thermal aging, uniform corrosion, pitting, crevice corrosion, denting, stress corrosion cracking, corrosion fatigue, hydrogen induced cracking and microbial influenced corrosion. Amorphous alloys have exceptional resistance to corrosion, due in part to the absence of grain boundaries, but can undergo crystallization and other phase instabilities during heating and welding. Titanium alloys are extremely corrosion resistant due to the formation of a tenacious passive film of titanium oxide, but is prone to hydrogen absorption inmore » crevices, and hydrogen induced cracking after hydrogen absorption. Accurate predictions of equipment reliability, necessary for strategic planning, requires integrated models that account for all relevant modes of attack, and that can make probabilistic predictions. Once developed, model parameters must be determined experimentally, and the validity of models must be established through careful laboratory and field tests. Such validation testing requires state-of-the-art surface analytical techniques, as well as electrochemical and fracture mechanics tests. The interaction between those processes that perturb the local environment on a surface and those that alter metallurgical condition must be integrated in predictive models. The material and environment come together to drive various modes of corrosive attack (Figure 1). Models must be supported through comprehensive materials testing capabilities. Such capabilities are available at LLNL and include: the Long Term Corrosion Test Facility (LTCTF) where large numbers of standard samples can be exposed to realistic test media at several temperature levels; a reverse DC machine that can be used to monitor the propagation of stress corrosion cracking (SCC) in situ; and banks of potentiostats with temperature controlled cells for potentiostatic and potentiodynamic testing (Figure 2).« less
An experimental investigation of the internal methane pressure in hydrogen attack

NASA Technical Reports Server (NTRS)

Natan, M.; Johnson, H. H.

1983-01-01

An experimental investigation of the internal methane pressure that is the driving force for bubble growth in hydrogen attack (HA) was done on pure iron (204 ppm C) and on two low carbon steels of slightly different compositions. The methane content N (c.c gas/g. material) in attacked specimens was measured by a vacuum extraction technique. The total void volume V (c.c) was determined from density measurements before and after HA exposure. The two values, N and V, were then used in an equation of state to calculate an average methane pressure P for the attack stages beyond a density loss (d.l.) greater than 0.05 pct. It was determined that N and P depend on hydrogen exposure conditions and the presence of traces of strong carbide forming alloying elements (in steel). They are independent of specimen size and grain size over a limited range. P varies as the bubble volume increases, showing a generally decreasing trend which brings it to values lower than calculated equilibrium pressures, although well within the same order of magnitude. Possible reasons for this behavior are discussed.
Chemical corrosion by chlorides on ancient-like bronzes and treatment by hydrogen glow discharge plasma

NASA Astrophysics Data System (ADS)

Papadopoulou, O.; Novakovic, J.; Vassiliou, P.; Filippaki, E.; Bassiakos, Y.

2013-12-01

Three representative ancient-like bronzes are employed for the chemical synthesis of Cu2(OH)3Cl rich patinas in order to study the influence of the alloying elements in the evolution of the chloride attack and to further conduct stabilization treatment via Hydrogen Glow Discharge Plasma (HGDP) at low temperature and pressure. The corrosion behavior of specimens having Sn and Pb as main alloying elements is governed by a decuprification mechanism and by the formation of Sn-Pb-O enriched barrier layers. In the case of the Zn containing alloy, dezincification is more pronounced at the corrosion initial stages, and copper species predominate the corrosion products evolution. A three-hour HGDP treatment leads to Cu+ production and metallic Cu, Sn, Zn, and Pb redeposition, as a result of metal cation reduction. This process is accompanied by partial removal of Cl species, O diminution, and change in coloration. The further increase of the Cl/O atomic ratio measured on the post-treated surfaces leads to the formation of nantokite and thus to the conclusion that the stabilization of objects with extensive Cl attack is not feasible by HGDP without preliminary chemical treatment.
Environmental Durability of Coated GRCop-84 Copper Alloys

NASA Technical Reports Server (NTRS)

Raj, Sai V.; Robinson, C.; Barrett, C.; Humphrey, D.

2005-01-01

An advanced Cu-8(at.%)Cr-4%Nb alloy developed at NASA's Glenn Research Center, and designated as GRCop-84, is currently being considered for use as liners in combustor chambers and nozzle ramps in NASA s future generations of reusable launch vehicles (RLVs). However, past experience has shown that unprotected copper alloys undergo an environmental attack called "blanching" in rocket engines using liquid hydrogen as fuel and liquid oxygen as the oxidizer. Potential for sulfidation attack of the liners in hydrocarbon-fueled engines is also of concern. As a result, protective overlay coatings alloys are being developed for GRCop-84. The oxidation behavior of several new coating alloys has been evaluated. GRCop-84 specimens were coated with several copper and nickel-based coatings, where the coatings were deposited by either vacuum plasma spraying or cold spraying techniques. Coated and uncoated specimens were thermally cycled in a furnace at different temperatures in order to evaluate the performance of the coatings. Additional studies were conducted in a high pressure burner rig using a hydrocarbon fuel and subjected to a high heat flux hydrogen-oxygen combustion flame in NASA s Quick Access Rocket Exhaust (QARE) rig. The performance of these coatings are discussed.

The stress corrosion resistance and the cryogenic temperature mechanical properties of hot rolled Nitronic 32 bar material

NASA Technical Reports Server (NTRS)

Montano, J. W. L.

1977-01-01

The ambient and cryogenic temperature mechanical properties and the ambient temperature stress corrosion properties of hot rolled and centerless ground Nitronic 32 stainless steel bar material are presented. The mechanical properties of longitudinal specimens were evaluated at test temperatures from ambient to liquid hydrogen. The tensile test data indicated increasing smooth tensile strength with decreasing temperature to liquid hydrogen temperature. However, below -200 F (-129.0 C) the notched tensile strength decreased slightly and below -320 F (-196.0 C) the decrease was significant. The elongation and reduction of area decreased drastically at temperatures below -200 F (-129.0 C). The Charpy V-notched impact energy decreased steadily with decreasing test temperature. Stress corrosion tests were performed on longitudinal tensile specimens stressed to 0, 75, and 90 percent of the 0.2 percent yield strength and on transverse 'C'-ring specimens stressed to 75 and 90 percent of the yield strength and exposed to: alternate immersion in a 3.5 percent NaCl bath, humidity cabinet environment, and a 5 percent salt spray atmosphere. The longitudinal tensile specimens experienced no corrosive attack; however, the 'C'-rings exposed to the alternate immersion and to the salt spray experienced some shallow etching and pitting, respectively. Small cracks appeared in two of the 'C'-rings after one month exposure to the salt spray.
Tribological properties of alumina-boria-silicate fabric from 25 to 850 C

NASA Technical Reports Server (NTRS)

Dellacorte, Christopher

1988-01-01

Demanding tribological properties are required of the materials used for the sliding seal between the sidewalls and the lower wall of the variable area hypersonic engine. Temperatures range from room temperature and below to operating temperatures of 1000 C in an environment of air, hydrogen, and water vapor. Candidate sealing materials for this application are an alumina-boria-silicate, ceramic, fabric rope sliding against the engine walls which may be made from copper- or nickel-based alloys. Using a pin-on-disk tribometer, the friction and wear properties of some of these potential materials and possible lubrication methods are evaluated. The ceramic fabric rope displayed unacceptably high friction coefficients (0.6 to 1.3) and, thus, requires lubrication. Sputtered thin films of gold, silver, and CaF2 reduced the friction by a factor of two. Sprayed coatings of boride nitride did not effectively lubricate the fabric. Static heat treatment tests at 950 C indicate that the fabric is chemically attacked by large quantities of silver, CaF2, and boron nitride. Sputtered films or powder impregnation of the fabric with gold may provide adequate lubrication up to 1000 C without showing any chemical attack.
NiAl Coatings Investigated for Use in Reusable Launch Vehicles

NASA Technical Reports Server (NTRS)

Raj, Sai V.; Ghosn, Louis J.; Barrett, Charles A.

2003-01-01

As part of its major investment in the area of advanced space transportation, NASA is developing new technologies for use in the second- and third-generation designs of reusable launch vehicles. Among the prototype rocket engines being considered for these launch vehicles are those designed to use liquid hydrogen as the fuel and liquid oxygen as the oxidizer. Advanced copper alloys, such as copper-chromium-niobium (Cu-8(at.%)Cr- 4(at.%)Nb, also referred to as GRCop-84), which was invented at the NASA Glenn Research Center, are being considered for use as liner materials in the combustion chambers and nozzle ramps of these engines. However, previous experience has shown that, in rocket engines using liquid hydrogen and liquid oxygen, copper alloys are subject to a process called blanching, where the material undergoes environmental attack under the action of the combustion gases. In addition, the copper alloy liners undergo thermomechanical fatigue, which often results in an initially square cooling channel deforming into a dog-house shape. Clearly, there is an urgent need to develop new coatings to protect copper liners from environmental attack inside rocket chambers and to lower the temperature of the liners to reduce the probability of deformation and failure by thermomechanical fatigue.
Hydrogen atom abstraction from aldehydes - OH + H2CO and O + H2CO

NASA Technical Reports Server (NTRS)

Dupuis, M.; Lester, W. A., Jr.

1984-01-01

The essential features of the potential energy surfaces governing hydrogen abstraction from formaldehyde by oxygen atom and hydroxyl radical have been characterized with ab inito multiconfiguration Hartree-Fock (MCHF) and configuration interaction (CI) wave functions. The results are consistent with a very small activation energy for the OH + H2CO reaction, and an activation energy of a few kcal/mol for the O + H2CO reaction. In the transition state structure of both systems, the attacking oxygen atom is nearly collinear with the attacked CH bond.
The effect of climate variability on urinary stone attacks: increased incidence associated with temperature over 18 °C: a population-based study.

PubMed

Park, Hyoung Keun; Bae, Sang Rak; Kim, Satbyul E; Choi, Woo Suk; Paick, Sung Hyun; Ho, Kim; Kim, Hyeong Gon; Lho, Yong Soo

2015-02-01

The aim of this study was to evaluate the effect of seasonal variation and climate parameters on urinary tract stone attack and investigate whether stone attack is increased sharply at a specific point. Nationwide data of total urinary tract stone attack numbers per month between January 2006 and December 2010 were obtained from the Korean Health Insurance Review and Assessment Service. The effects of climatic factors on monthly urinary stone attack were assessed using auto-regressive integrated moving average (ARIMA) regression method. A total of 1,702,913 stone attack cases were identified. Mean monthly and monthly average daily urinary stone attack cases were 28,382 ± 2,760 and 933 ± 85, respectively. The stone attack showed seasonal trends of sharp incline in June, a peak plateau from July to September, and a sharp decline after September. The correlation analysis showed that ambient temperature (r = 0.557, p < 0.001) and relative humidity (r = 0.513, p < 0.001) were significantly associated with urinary stone attack cases. However, after adjustment for trends and seasonality, ambient temperature was the only climate factor associated with the stone attack cases in ARIMA regression test (p = 0.04). Threshold temperature was estimated as 18.4 °C. Risk of urinary stone attack significantly increases 1.71% (1.02-2.41 %, 95% confidence intervals) with a 1 °C increase of ambient temperature above the threshold point. In conclusion, monthly urinary stone attack cases were changed according to seasonal variation. Among the climates variables, only temperature had consistent association with stone attack and when the temperature is over 18.4 °C, urinary stone attack would be increased sharply.
Relation of Temperature and Humidity to the Risk of Recurrent Gout Attacks

PubMed Central

Neogi, Tuhina; Chen, Clara; Niu, Jingbo; Chaisson, Christine; Hunter, David J.; Choi, Hyon; Zhang, Yuqing

2014-01-01

Gout attack risk may be affected by weather (e.g., because of volume depletion). We therefore examined the association of temperature and humidity with the risk of recurrent gout attacks by conducting an internet-based case-crossover study in the United States (in 2003–2010) among subjects with a diagnosis of gout who had 1 or more attacks during 1 year of follow-up. We examined the association of temperature and humidity over the prior 48 hours with the risk of gout attacks using a time-stratified approach and conditional logistic regression. Among 632 subjects with gout, there was a significant dose-response relationship between mean temperature in the prior 48 hours and the risk of subsequent gout attack (P = 0.01 for linear trend). Higher temperatures were associated with approximately 40% higher risk of gout attack compared with moderate temperatures. There was a reverse J-shaped relationship between mean relative humidity and the risk of gout attacks (P = 0.03 for quadratic trend). The combination of high temperature and low humidity had the greatest association (odds ratio = 2.04, 95% confidence interval: 1.26, 3.30) compared with moderate temperature and relative humidity. Thus, high ambient temperature and possibly extremes of humidity were associated with an increased risk of gout attack, despite the likelihood that individuals are often in climate-controlled indoor environments. PMID:24993733
Dissolution of spent nuclear fuel in carbonate-peroxide solution

NASA Astrophysics Data System (ADS)

Soderquist, Chuck; Hanson, Brady

2010-01-01

This study shows that spent UO2 fuel can be completely dissolved in a room temperature carbonate-peroxide solution apparently without attacking the metallic Mo-Tc-Ru-Rh-Pd fission product phase. In parallel tests, identical samples of spent nuclear fuel were dissolved in nitric acid and in an ammonium carbonate, hydrogen peroxide solution. The resulting solutions were analyzed for strontium-90, technetium-99, cesium-137, europium-154, plutonium, and americium-241. The results were identical for all analytes except technetium, where the carbonate-peroxide dissolution had only about 25% of the technetium that the nitric acid dissolution had.
The effects of stress, anxiety, and outdoor temperature on the frequency and severity of Raynaud's attacks: the Raynaud's Treatment Study.

PubMed

Brown, K M; Middaugh, S J; Haythornthwaite, J A; Bielory, L

2001-04-01

It was expected that stress and anxiety would be related to Raynaud's phenomenon (RP) attack characteristics when mild outdoor temperatures produced partial or no digital vasoconstriction. Hypotheses were that in warmer temperature categories, compared to those below 40 degrees F, higher stress or anxiety would be associated with more frequent, severe, and painful attacks. The Raynaud's Treatment Study recruited 313 participants with primary RP. Outcomes were attack rate, severity, and pain. Predictors were average daily outdoor temperature, stress, anxiety, age, gender, and a stress-by-temperature or an anxiety-by-temperature interaction. Outcomes were tested separately in multiple linear regression models. Stress and anxiety were tested in separate models. Stress was not a significant predictor of RP attack characteristics. Higher anxiety was related to more frequent attacks above 60 degrees F. It was also related to greater attack severity at all temperatures, and to greater pain above 60 degrees F and between 40 degrees and 49.9 degrees F.
The crevice corrosion behavior of chromium stainless steel and nickel base alloys in a reverse osmosis plant utilizing seawater

DOE Office of Scientific and Technical Information (OSTI.GOV)

Al-Odwani, A.; Carew, J.; Al-Hashem, A.

1999-11-01

The crevice corrosion tests were performed on UNS S31603, UNS S31703, UNS S31726, UNS S31254, UNS N08904, UNS N625, UNS N825 and UNS N276 was investigated in seawater and neutral brine solution using a multiple crevice washer assembly. PTFE multiple-crevice washers were bolted to both sides of the test specimens with PTFE bolts and nuts. The specimens were exposed to seawater flowing at a rate of 100 L/h for periods of 3,000 h and 6,000 h. Duplicate specimens were immersed in a plexiglass cell containing the flowing seawater at a temperature of 30 C. The results showed that all themore » tested coupons were susceptible to some degree of crevice corrosion attack. However, the stainless steels were the most severely affected. The degree of crevice corrosion attack for the nickel base alloys decreased as the percentage of molybdenum content in the alloys increased. Destruction of the passive layer by the concentration of chloride or acidity and reduction of hydrogen ions at the crevices is believed to be the cause of the crevice attack.« less
Effects of Vaporized Decontamination Systems on Selected Building Interior Materials: Vaporized Hydrogen Peroxide

DTIC Science & Technology

2009-01-01

surfaces in buildings following a terrorist attack using CB agents. Vaporized hydrogen peroxide ( VHP ) and Cl02 are decontamination technologies that...decontaminant. The focus of this technical report is the evaluation of the building interior materials and the Steris VHP technology. 15. SUBJECT...TERMS Material Compatibility VHP vaporized hydrogen peroxide 16. SECURITY CLASSIFICATION OF: a. REPORT U b. ABSTRACT U c. THIS PAGE U 17
Effects of ambient temperature on stroke hospital admissions: Results from a time-series analysis of 104,432 strokes in Guangzhou, China.

PubMed

Guo, Pi; Zheng, Murui; Feng, Wenru; Wu, Jiagang; Deng, Changyu; Luo, Ganfeng; Wang, Li; Pan, Bingying; Liu, Huazhang

2017-02-15

Stroke is a main cause of death and public health burden in China. The evidence on the burden of different strokes attack attribute to ambient temperature in China is limited. This study aimed to show the characteristics of stroke attack and the attributable risk due to temperature based on hospital admission data in Guangzhou, one of the most developed cities in China. From January 1, 2013 to December 31, 2015, 104,432 stroke hospitalizations in Guangzhou residents from 67 hospitals for stroke sentinel surveillance were registered. Characteristics of hospital admissions by gender, age group, calendar year and stroke subtype were analyzed, and distributed lag non-linear models were applied to evaluate the effects of temperature on stroke attack admissions. Stroke attack admissions increased from 31,851 to 36,755 through 2013 to 2015, increasing by 15.4%. An increasing trend in the risk of stroke attack with age was observed, irrespectively of stroke subtype and calendar year. People with hypertension were more likely to have an associated stroke than people without that. The effects of cold temperature on attack admissions for CBI and ICH strokes were significant. Overall, the percentages of CBI and ICH attack admissions attribute to cold temperature were 9.06% (95% CI: 1.84, 15.00) and 15.09% (95% CI: 5.86, 21.96), respectively. Besides, elderly people were more vulnerable to cold temperature than the young. Measures should be taken to increase public awareness about the ill effects of cold temperature on stroke attack, and educate the public about self-protection. Copyright © 2016 Elsevier B.V. All rights reserved.
High-temperature oxidation/corrosion of iron-based superalloys

NASA Technical Reports Server (NTRS)

Lemkey, F. D.; Smeggil, J. G.; Bailey, R. S.; Schuster, J. C.; Nowotny, H.

1987-01-01

The oxidation and sulfidation of several novel iron-base superalloys were evaluated in high-temperature cyclic tests. The experimental austenitic alloys examined were modifications of NASAUT-4GA which were developed for Stirling-engine application. The weight gains and resulting surface scales were measured and analyzed. Mixed oxide scales were found to form on all specimens exposed above 871 C. The build-up of these scales led to a depletion of Mn and Cr in a zone adjacent to the oxides. In addition, the initial oxidation of the Fe-rich alloy was inhibited by a thin but tenacious Si layer which formed at the interface between oxides and the parent layer. Sulfidation tests using Na2SO4 coatings resulted in the formation of a protective spinel and alpha-Fe2O3 phases. Preferential attack of the carbide phase by hydrogen was not observed after 350 h at 871 C.
Localized corrosion of 316L stainless steel in tritiated water containing aggressive radiolytic and decomposition products at different temperatures

NASA Astrophysics Data System (ADS)

Bellanger, G.

2008-02-01

Tritium is one of the more important radionuclides used in nuclear industry as plutonium and uranium. The tritium in tritiated water always causes difficulties in nuclear installations, including equipment corrosion. Moreover, with tritiated water there are, in addition, the radiolytic and decomposition products such as hydrogen peroxide formed during decay, chloride ions produced by degradation of organic seals and oils used for tightness and pumping, and acid pH produced by excitation of nitrogen in air by the β - particle. Highly concentrated tritiated water releases energy and its temperature is about 80 °C, moreover heating is necessary in the tritium processes. These conditions highly facilitate the corrosion of stainless steels by pitting and crevice attack. Corrosion tests were performed by electrochemical analysis methods and by visual inspection of the surface of stainless steel.
Melatonin affects the order, dynamics and hydration of brain membrane lipids

NASA Astrophysics Data System (ADS)

Akkas, Sara B.; Inci, Servet; Zorlu, Faruk; Severcan, Feride

2007-05-01

The brain is especially susceptible to free radical attack since it is rich in polyunsaturated fatty acids and consumes very high amounts of oxygen. Melatonin is a non-enzymatic amphiphilic antioxidant hormone that is widely used in medicine for protective and treatment purposes in cases of oxidative stress. In the present work, the effects of the clinically used dose of melatonin (a single intraperitoneal dose of 100 mg/kg) on rat brain homogenate were investigated as a function of temperature using Fourier transform infrared spectroscopy. The results showed that the lipid to protein ratio decreases in the melatonin treated brain samples. Moreover, it is revealed that melatonin disorders and decreases the dynamics of lipids and induces a strengthening in the hydrogen bonding between the functional groups of both melatonin and the polar parts of lipids and/or water at physiological temperatures.
NTREES Testing and Operations Status

NASA Technical Reports Server (NTRS)

Emrich, Bill

2007-01-01

Nuclear Thermal Rockets or NTR's have been suggested as a propulsion system option for vehicles traveling to the moon or Mars. These engines are capable of providing high thrust at specific impulses at least twice that of today's best chemical engines. The performance constraints on these engines are mainly the result of temperature limitations on the fuel coupled with a limited ability to withstand chemical attack by the hot hydrogen propellant. To operate at maximum efficiency, fuel forms are desired which can withstand the extremely hot, hostile environment characteristic of NTR operation for at least several hours. The simulation of such an environment would require an experimental device which could simultaneously approximate the power, flow, and temperature conditions which a nuclear fuel element (or partial element) would encounter during NTR operation. Such a simulation would allow detailed studies of the fuel behavior and hydrogen flow characteristics under reactor like conditions to be performed. Currently, the construction of such a simulator has been completed at the Marshall Space Flight Center, and will be used in the future to evaluate a wide variety of fuel element designs and the materials of which they are fabricated. This present work addresses the operational status of the Nuclear Thermal Rocket Element Environmental Simulator or NTREES and some of the design considerations which were considered prior to and during its construction.
Kinetic model of water disinfection using peracetic acid including synergistic effects.

PubMed

Flores, Marina J; Brandi, Rodolfo J; Cassano, Alberto E; Labas, Marisol D

2016-01-01

The disinfection efficiencies of a commercial mixture of peracetic acid against Escherichia coli were studied in laboratory scale experiments. The joint and separate action of two disinfectant agents, hydrogen peroxide and peracetic acid, were evaluated in order to observe synergistic effects. A kinetic model for each component of the mixture and for the commercial mixture was proposed. Through simple mathematical equations, the model describes different stages of attack by disinfectants during the inactivation process. Based on the experiments and the kinetic parameters obtained, it could be established that the efficiency of hydrogen peroxide was much lower than that of peracetic acid alone. However, the contribution of hydrogen peroxide was very important in the commercial mixture. It should be noted that this improvement occurred only after peracetic acid had initiated the attack on the cell. This synergistic effect was successfully explained by the proposed scheme and was verified by experimental results. Besides providing a clearer mechanistic understanding of water disinfection, such models may improve our ability to design reactors.
Thermal acclimation of interactions: differential responses to temperature change alter predator-prey relationship.

PubMed

Grigaltchik, Veronica S; Ward, Ashley J W; Seebacher, Frank

2012-10-07

Different species respond differently to environmental change so that species interactions cannot be predicted from single-species performance curves. We tested the hypothesis that interspecific difference in the capacity for thermal acclimation modulates predator-prey interactions. Acclimation of locomotor performance in a predator (Australian bass, Macquaria novemaculeata) was qualitatively different to that of its prey (eastern mosquitofish, Gambusia holbrooki). Warm (25°C) acclimated bass made more attacks than cold (15°C) acclimated fish regardless of acute test temperatures (10-30°C), and greater frequency of attacks was associated with increased prey capture success. However, the number of attacks declined at the highest test temperature (30°C). Interestingly, escape speeds of mosquitofish during predation trials were greater than burst speeds measured in a swimming arena, whereas attack speeds of bass were lower than burst speeds. As a result, escape speeds of mosquitofish were greater at warm temperatures (25°C and 30°C) than attack speeds of bass. The decline in the number of attacks and the increase in escape speed of prey means that predation pressure decreases at high temperatures. We show that differential thermal responses affect species interactions even at temperatures that are within thermal tolerance ranges. This thermal sensitivity of predator-prey interactions can be a mechanism by which global warming affects ecological communities.
Thermal acclimation of interactions: differential responses to temperature change alter predator–prey relationship

PubMed Central

Grigaltchik, Veronica S.; Ward, Ashley J. W.; Seebacher, Frank

2012-01-01

Different species respond differently to environmental change so that species interactions cannot be predicted from single-species performance curves. We tested the hypothesis that interspecific difference in the capacity for thermal acclimation modulates predator–prey interactions. Acclimation of locomotor performance in a predator (Australian bass, Macquaria novemaculeata) was qualitatively different to that of its prey (eastern mosquitofish, Gambusia holbrooki). Warm (25°C) acclimated bass made more attacks than cold (15°C) acclimated fish regardless of acute test temperatures (10–30°C), and greater frequency of attacks was associated with increased prey capture success. However, the number of attacks declined at the highest test temperature (30°C). Interestingly, escape speeds of mosquitofish during predation trials were greater than burst speeds measured in a swimming arena, whereas attack speeds of bass were lower than burst speeds. As a result, escape speeds of mosquitofish were greater at warm temperatures (25°C and 30°C) than attack speeds of bass. The decline in the number of attacks and the increase in escape speed of prey means that predation pressure decreases at high temperatures. We show that differential thermal responses affect species interactions even at temperatures that are within thermal tolerance ranges. This thermal sensitivity of predator–prey interactions can be a mechanism by which global warming affects ecological communities. PMID:22859598
Gas phase chemistry of N-benzylbenzamides with silver(I) cations: characterization of benzylsilver cation.

PubMed

Sun, Hezhi; Jin, Zhe; Quan, Hong; Sun, Cuirong; Pan, Yuanjiang

2015-03-07

The benzylsilver cation which emerges from the collisional dissociation of silver(I)-N-benzylbenzamide complexes was characterized by deuterium-labeling experiments, theoretical calculations, breakdown curves and substituent effects. The nucleophilic attack of the carbonyl oxygen on an α-hydrogen results in the generation of the benzylsilver cation, which is competitive to the AgH loss with the α-hydrogen.
Expert systems for superalloy studies

NASA Technical Reports Server (NTRS)

Workman, Gary L.; Kaukler, William F.

1990-01-01

There are many areas in science and engineering which require knowledge of an extremely complex foundation of experimental results in order to design methodologies for developing new materials or products. Superalloys are an area which fit well into this discussion in the sense that they are complex combinations of elements which exhibit certain characteristics. Obviously the use of superalloys in high performance, high temperature systems such as the Space Shuttle Main Engine is of interest to NASA. The superalloy manufacturing process is complex and the implementation of an expert system within the design process requires some thought as to how and where it should be implemented. A major motivation is to develop a methodology to assist metallurgists in the design of superalloy materials using current expert systems technology. Hydrogen embrittlement is disasterous to rocket engines and the heuristics can be very complex. Attacking this problem as one module in the overall design process represents a significant step forward. In order to describe the objectives of the first phase implementation, the expert system was designated Hydrogen Environment Embrittlement Expert System (HEEES).

Core Body and Skin Temperature in Type 1 Narcolepsy in Daily Life; Effects of Sodium Oxybate and Prediction of Sleep Attacks.

PubMed

van der Heide, Astrid; Werth, Esther; Donjacour, Claire E H M; Reijntjes, Robert H A M; Lammers, Gert Jan; Van Someren, Eus J W; Baumann, Christian R; Fronczek, Rolf

2016-11-01

Previous laboratory studies in narcolepsy patients showed altered core body and skin temperatures, which are hypothesised to be related to a disturbed sleep wake regulation. In this ambulatory study we assessed temperature profiles in normal daily life, and whether sleep attacks are heralded by changes in skin temperature. Furthermore, the effects of three months of treatment with sodium oxybate (SXB) were investigated. Twenty-five narcolepsy patients and 15 healthy controls were included. Core body, proximal and distal skin temperatures, and sleep-wake state were measured simultaneously for 24 hours in ambulatory patients. This procedure was repeated in 16 narcolepsy patients after at least 3 months of stable treatment with SXB. Increases in distal skin temperature and distal-to-proximal temperature gradient (DPG) strongly predicted daytime sleep attacks (P < 0.001). As compared to controls, patients had a higher proximal and distal skin temperature in the morning, and a lower distal skin temperature during the night (all P < 0.05). Furthermore, they had a higher core body temperature during the first part of the night (P < 0.05), which SXB decreased (F = 4.99, df = 1, P = 0.03) to a level similar to controls. SXB did not affect skin temperature. This ambulatory study demonstrates that daytime sleep attacks were preceded by clear changes in distal skin temperature and DPG. Furthermore, changes in core body and skin temperature in narcolepsy, previously only studied in laboratory settings, were partially confirmed. Treatment with SXB resulted in a normalisation of the core body temperature profile. Future studies should explore whether predictive temperature changes can be used to signal or even prevent sleep attacks. © 2016 Associated Professional Sleep Societies, LLC.
Core Body and Skin Temperature in Type 1 Narcolepsy in Daily Life; Effects of Sodium Oxybate and Prediction of Sleep Attacks

PubMed Central

van der Heide, Astrid; Werth, Esther; Donjacour, Claire E.H.M.; Reijntjes, Robert H.A.M.; Lammers, Gert Jan; Van Someren, Eus J.W.; Baumann, Christian R.; Fronczek, Rolf

2016-01-01

Study Objectives: Previous laboratory studies in narcolepsy patients showed altered core body and skin temperatures, which are hypothesised to be related to a disturbed sleep wake regulation. In this ambulatory study we assessed temperature profiles in normal daily life, and whether sleep attacks are heralded by changes in skin temperature. Furthermore, the effects of three months of treatment with sodium oxybate (SXB) were investigated. Methods: Twenty-five narcolepsy patients and 15 healthy controls were included. Core body, proximal and distal skin temperatures, and sleep-wake state were measured simultaneously for 24 hours in ambulatory patients. This procedure was repeated in 16 narcolepsy patients after at least 3 months of stable treatment with SXB. Results: Increases in distal skin temperature and distal-to-proximal temperature gradient (DPG) strongly predicted daytime sleep attacks (P < 0.001). As compared to controls, patients had a higher proximal and distal skin temperature in the morning, and a lower distal skin temperature during the night (all P < 0.05). Furthermore, they had a higher core body temperature during the first part of the night (P < 0.05), which SXB decreased (F = 4.99, df = 1, P = 0.03) to a level similar to controls. SXB did not affect skin temperature. Conclusions: This ambulatory study demonstrates that daytime sleep attacks were preceded by clear changes in distal skin temperature and DPG. Furthermore, changes in core body and skin temperature in narcolepsy, previously only studied in laboratory settings, were partially confirmed. Treatment with SXB resulted in a normalisation of the core body temperature profile. Future studies should explore whether predictive temperature changes can be used to signal or even prevent sleep attacks. Citation: van der Heide A, Werth E, Donjacour CE, Reijntjes RH, Lammers GJ, Van Someren EJ, Baumann CR, Fronczek R. Core body and skin temperature in type 1 narcolepsy in daily life; effects of sodium oxybate and prediction of sleep attacks. SLEEP 2016;39(11):1941–1949. PMID:27568803
[The association between emergency clinic visits for asthmatic attacks and fluctuating environmental factors].

PubMed

Shimizu, S; Kagawa, J; Ishiguro, M

2001-07-01

The number of nocturnal visits of asthmatic attack patients to the emergency room of Yokohama Medical Association's Clinic from January 1990 to December 1991 was compared to daily levels of air pollution (NO, NO2, SO2 and SPM) and weather (temperature and relative humidity) variables measured in Yokohama City. Trend-cycle components (Trend) that control for the weekly effects, other irregular variance for asthmatic attack incidence and environmental parameter measurements were estimated from the original data series using the method of Akaike and Ishiguro (1980). The rate of increase for each environmental parameter was then calculated from its trend-cycle components. We classified the data into four stages on the basis of rising and falling temperature and humidity. For each stage of temperature and humidity, fluctuation we estimated correlations between the number of asthmatic attack visits and original data series measurements, estimated trend-cycle components, and calculated rates of increase for each of the air pollutants. The daily number of asthmatic attack visits was negatively correlated to the daily mean values of all air pollutants, but positively correlated to the daily mean temperature and relative humidity. The trend-cycle components of the air pollutants were also negatively correlated to the frequencies of asthmatic attacks (p < 0.01 for all pollutants except NO2). In contrast, the number of asthmatic attack visits were in general positively correlated with increasing levels of pollutants. Furthermore, when both temperature and relative humidity decreased, significant correlations (r > 0.31, p < 0.001) between the number of asthmatic attacks and increased rates of all air pollutants were observed (r: NO2 > NO > SO2 > SPM).
Promoting the ambient-condition stability of Zr-doped barium cerate: Toward robust solid oxide fuel cells and hydrogen separation in syngas

NASA Astrophysics Data System (ADS)

Yang, Ying; Zeng, Yimin; Amirkhiz, Babak S.; Luo, Jing-Li; Yan, Ning

2018-02-01

Increasing the stability of perovskite proton conductor against atmospheric CO2 and moisture attack at ambient conditions might be equally important as that at the elevated service temperatures. It can ease the transportation and storage of materials, potentially reducing the maintenance cost of the integral devices. In this work, we initially examined the surface degradation behaviors of various Zr-doped barium cerates (BaCe0.7Zr0.1Y0.1Me0.1O3) using XRD, SEM, STEM and electron energy loss spectroscopy. Though that the typical lanthanide (Y, Yb and Gd) and In incorporated Zr-doped cerates well resisted CO2-induced carbonation in air at elevated temperatures, they were unfortunately vulnerable at ambient conditions, suffering slow decompositions at the surface. Conversely, Sn doped samples (BCZYSn) were robust at both conditions yet showed high protonic conductivity. Thanks to that, the anode supported solid oxide fuel cells equipped with BCZYSn electrolyte delivered a maximum power density of 387 mW cm-2 at 600 °C in simulated coal-derived syngas. In the hydrogen permeation test using BCZYSn based membrane, the H2 flux reached 0.11 mL cm-2 min-1 at 850 °C when syngas was the feedstock. Both devices demonstrated excellent stability in the presence of CO2 in the syngas.
Composition and method for hydrogen storage

NASA Technical Reports Server (NTRS)

Mao, Wendy L. (Inventor); Mao, Ho-Kwang (Inventor)

2004-01-01

A method for hydrogen storage includes providing water and hydrogen gas to a containment volume, reducing the temperature of the water and hydrogen gas to form a hydrogen clathrate at a first cryogenic temperature and a first pressure and maintaining the hydrogen clathrate at second cryogenic temperature within a temperature range of up to 250 K to effect hydrogen storage. The low-pressure hydrogen hydrate includes H.sub.2 O molecules, H.sub.2 molecules and a unit cell including polyhedron cages of hydrogen-bonded frameworks of the H.sub.2 O molecules built around the H.sub.2 molecules.
Low-pressure hydrogenation of carbon dioxide catalyzed by an iron pincer complex exhibiting noble metal activity.

PubMed

Langer, Robert; Diskin-Posner, Yael; Leitus, Gregory; Shimon, Linda J W; Ben-David, Yehoshoa; Milstein, David

2011-10-10

A highly active iron catalyst for the hydrogenation of carbon dioxide and bicarbonates works under remarkably low pressures and achieves activities similar to some of the best noble metal catalysts. A mechanism is proposed involving the direct attack of an iron trans-dihydride on carbon dioxide, followed by ligand exchange and dihydrogen coordination. Copyright © 2011 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.
Integrated Temperature and Hydrogen Sensors with MEMS Technology

PubMed Central

Jiang, Hongchuan; Huang, Min; Yu, Yibing; Tian, Xiaoyu; Zhang, Wanli; Zhang, Jianfeng; Huang, Yifan; Yu, Kun

2017-01-01

In this work, a PdNi thin film hydrogen gas sensor with integrated Pt thin film temperature sensor was designed and fabricated using the micro-electro-mechanical system (MEMS) process. The integrated sensors consist of two resistors: the former, based on Pt film, is used as a temperature sensor, while the latter had the function of hydrogen sensing and is based on PdNi alloy film. The temperature coefficient of resistance (TCR) in both devices was measured and the output response of the PdNi film hydrogen sensor was calibrated based on the temperature acquired by the Pt temperature sensor. The SiN layer was deposited on top of Pt film to inhibit the hydrogen diffusion and reduce consequent disturbance on temperature measurement. The TCR of the PdNi film and the Pt film was about 0.00122/K and 0.00217/K, respectively. The performances of the PdNi film hydrogen sensor were investigated with hydrogen concentrations from 0.3% to 3% on different temperatures from 294.7 to 302.2 K. With the measured temperature of the Pt resistor and the TCR of the PdNi film, the impact of the temperature on the performances of the PdNi film hydrogen sensor was reduced. The output response, response time and recovery time of the PdNi film hydrogen sensors under the hydrogen concentration of 0.5%, 1.0%, 1.5% and 2.0% were measured at 313 K. The output response of the PdNi thin film hydrogen sensors increased with increasing hydrogen concentration while the response time and recovery time decreased. A cycling test between pure nitrogen and 3% hydrogen concentration was performed at 313 K and PdNi thin film hydrogen sensor demonstrated great repeatability in the cycling test. PMID:29301220
Hydrogen Production from Nuclear Energy via High Temperature Electrolysis

DOE Office of Scientific and Technical Information (OSTI.GOV)

James E. O'Brien; Carl M. Stoots; J. Stephen Herring

2006-04-01

This paper presents the technical case for high-temperature nuclear hydrogen production. A general thermodynamic analysis of hydrogen production based on high-temperature thermal water splitting processes is presented. Specific details of hydrogen production based on high-temperature electrolysis are also provided, including results of recent experiments performed at the Idaho National Laboratory. Based on these results, high-temperature electrolysis appears to be a promising technology for efficient large-scale hydrogen production.
Low temperature fluid blender

NASA Technical Reports Server (NTRS)

Repas, G. A.

1971-01-01

Blender supplies hydrogen at temperatures from 289 deg K to 367 deg K. Hydrogen temperature is controlled by using blender to combine flow from liquid hydrogen tank /276 deg K/ and gaseous hydrogen cylinder /550 deg K/. Blenders are applicable where flow of controlled low-temperature fluid is desired.
Host selection and lethality of attacks by sea lampreys (Petromyzon marinus) in laboratory studies

USGS Publications Warehouse

Swink, William D.

2003-01-01

Parasitic-phase sea lampreys (Petromyzon marinus) are difficult to study in the wild. A series of laboratory studies (1984-1995) of single attacks on lake trout (Salvelinus namaycush), rainbow trout (Oncorhynchus mykiss), and burbot (Lota lota) examined host size selection; determined the effects of host size, host species, host strain, and temperature on host mortality; and estimated the weight of hosts killed per lamprey. Rainbow trout were more able and burbot less able to survive attacks than lake trout. Small sea lampreys actively selected the larger of two small hosts; larger sea lampreys attacked larger hosts in proportion to the hosts' body sizes, but actively avoided shorter hosts (a?? 600 mm) when larger were available. Host mortality was significantly less for larger (43-44%) than for smaller hosts (64%). However, the yearly loss of hosts per sea lamprey was less for small hosts (range, 6.8-14.2 kg per sea lamprey) than larger hosts (range, 11.4-19.3 kg per sea lamprey). Attacks at the lower of two temperature ranges (6.1-11.8A?C and 11.1-15.0A?C) did not significantly reduce the percentage of hosts killed (54% vs. 69%, p > 0.21), but longer attachment times at lower temperatures reduced the number of hosts attacked (33 vs. 45), and produced the lowest loss of hosts (6.6 kg per sea lamprey). Low temperature appeared to offset other factors that increase host mortality. Reanalysis of 789 attacks pooled from these studies, using forward stepwise logistic regression, also identified mean daily temperature as the dominant factor affecting host mortality. Observations in Lakes Superior, Huron, and Ontario support most laboratory results.
Thermodynamic Evaluation of Hydrogen Absorption by Niobium During SRF Fabrication

NASA Astrophysics Data System (ADS)

Ricker, R. E.; Myneni, G. R.

2011-03-01

The properties and performance of the ultra high purity Nb used to fabricate superconducting radio frequency (SRF) particle accelerator cavities have been found to vary with processing conditions. One hypothesis for these variations is that hydrogen, absorbed during processing, is responsible for this behavior. The key assumption behind this hypothesis is that niobium can absorb hydrogen from one or more of the processing environments. This paper reviews work examining the validity of this assumption. It was determined that Nb will spontaneously react with water producing adsorbed atomic hydrogen that is readily absorbed into the metal. The passivating oxide film normally prevents this reaction, but this film is frequently removed during processing and it is attacked by the fluoride ion used in the polishing solutions for SRF cavities. However, during electropolishing that cathodic reduction of hydrogen is transferred to the auxiliary electrode and this should suppress hydrogen absorption.
Influence of high pressure hydrogen environment on creep deformation of Mo-Re, Haynes 188, and NARloy-Z alloys

NASA Technical Reports Server (NTRS)

Sastry, S. M. L.; Yang, Charles C.; Ouyang, Shewang; Jerina, K. L.; Schwartz, D. S.

1994-01-01

The present study focuses on the investigation of the influence of hydrogen on the mechanical properties of three types of alloys at elevated temperatures. The reasons for the consideration of hydrogen effects are the potential use of hydrogen as a coolant in gas-cooled reactors and fuel in advanced hypersonic vehicles. The materials used in hydrogen atmosphere must not be embrittled by hydrogen at ambient temperature and should have good strength in hydrogen atmosphere at elevated temperature. The paucity of information concerning the mechanical performance in hydrogen atmosphere at elevated temperature has been a limiting factor in the selection and design of structural components for operation in hydrogen environment.
High Pressure Hydrogen Pressure Relief Devices: Accelerated Life Testing and Application Best Practices

DOE Office of Scientific and Technical Information (OSTI.GOV)

Burgess, Robert M.; Post, Matthew B.; Buttner, William J.

Pressure relief devices (PRDs ) are used to protect high pressure systems from burst failure caused by overpressurization. Codes and standards require the use of PRDs for the safe design of many pressurized systems. These systems require high reliability due to the risks associated with a burst failure. Hydrogen service can increase the risk of PRD failure due to material property degradation caused by hydrogen attack. The National Renewable Energy Laboratory (NREL) has conducted an accelerated life test on a conventional spring loaded PRD. Based on previous failures in the field, the nozzles specific to these PRDs are of particularmore » interest. A nozzle in a PRD is a small part that directs the flow of fluid toward the sealing surface to maintain the open state of the valve once the spring force is overcome. The nozzle in this specific PRD is subjected to the full tensile force of the fluid pressure. These nozzles are made from 440C material, which is a type of hardened steel that is commonly chosen for high pressure applications because of its high strength properties. In a hydrogen environment, however, 440C is considered a worst case material since hydrogen attack results in a loss of almost all ductility and thus 440C is prone to fatigue and material failure. Accordingly, 440C is not recommended for hydrogen service. Conducting an accelerated life test on a PRD with 440C material provides information on necessary and sufficient conditions required to produce crack initiation and failure. The accelerated life test also provides information on other PRD failure modes that are somewhat statistically random in nature.« less
Hydrogen/Chlorine exchange reactions of gaseous carbanions.

PubMed

Chen, Hao; Cooks, R Graham; Meurer, Eduardo C; Eberlin, Marcos N

2005-12-01

Gas-phase reactions of three typical carbanions CH(2)NO(2)(-), CH(2)CN(-), and CH(2)S(O)CH(3)(-) with the chloromethanes CH(2)Cl(2), CHCl(3), and CCl(4), examined by tandem mass spectrometry, show a novel hydrogen/chlorine exchange reaction. For example, reaction between the nitromethyl anion CH(2)NO(2)(-) and carbon tetrachloride CCl(4) forms the ion CHClNO(2)(-). The suggested reaction mechanism involves nucleophilic attack by CH(2)NO(2)(-) at the chlorine of CCl(4) followed by proton transfer within the resulting complex [CH(2)ClNO(2) + CCl(3)(-)] to form CHClNO(2)(-) and CHCl(3). Two other carbanions CH(2)CN(-) and CH(2)S(O)CH(3)(-) also undergo the novel hydrogen/chlorine exchange reactions with CCl(4) but to a much smaller extent, their higher nucleophilicities favoring competitive nucleophilic attack reactions. Proton abstraction is the exclusive pathway in the reactions of these carbanions with CHCl(3). While CH(2)CN(-) and CH(2)S(O)CH(3)(-) promote mainly proton abstraction and nucleophilic displacement in reactions with CH(2)Cl(2), CH(2)NO(2)(-) does not react.
Hydrogen absorption and its effect on magnetic properties of Nd2Fe14B

NASA Astrophysics Data System (ADS)

Bezdushnyi, R.; Damianova, R.; Tereshina, I. S.; Pankratov, N. Yu.; Nikitin, S. A.

2018-05-01

Magnetic properties of hydrides of the intermetallic compound Nd2Fe14BHx are investigated in the temperature range covering the Curie temperatures (TC) of the compounds (up to 670 K). The temperature dependencies of magnetization are measured under continuous control of hydrogen content in the investigated samples. The dependencies of Curie and spin-reorientation transition (TSR) temperatures on the hydrogen concentration are studied in detail. The dependence of hydrogen concentration on pressure at a constant temperature (near TC) and on the temperature at various pressures are obtained. We attempted to estimate the contributions of the unit cell volume increase upon hydrogenation and the electronic structure change in the variation of TC of the hydrogenated Nd2Fe14 B .
Structural flexibility of the sulfur mustard molecule at finite temperature from Car-Parrinello molecular dynamics simulations.

PubMed

Lach, Joanna; Goclon, Jakub; Rodziewicz, Pawel

2016-04-05

Sulfur mustard (SM) is one of the most dangerous chemical compounds used against humans, mostly at war conditions but also in terrorist attacks. Even though the sulfur mustard has been synthesized over a hundred years ago, some of its molecular properties are not yet resolved. We investigate the structural flexibility of the SM molecule in the gas phase by Car-Parrinello molecular dynamics simulations. Thorough conformation analysis of 81 different SM configurations using density functional theory is performed to analyze the behavior of the system at finite temperature. The conformational diversity is analyzed with respect to the formation of intramolecular blue-shifting CH⋯S and CH⋯Cl hydrogen bonds. Molecular dynamics simulations indicate that all structural rearrangements between SM local minima are realized either in direct or non-direct way, including the intermediate structure in the last case. We study the lifetime of the SM conformers and perform the population analysis. Additionally, we provide the anharmonic dynamical finite temperature IR spectrum from the Fourier Transform of the dipole moment autocorrelation function to mimic the missing experimental IR spectrum. Copyright © 2015 Elsevier B.V. All rights reserved.
Silicon Carbide-Based Hydrogen Gas Sensors for High-Temperature Applications

PubMed Central

Kim, Seongjeen; Choi, Jehoon; Jung, Minsoo; Joo, Sungjae; Kim, Sangchoel

2013-01-01

We investigated SiC-based hydrogen gas sensors with metal-insulator-semiconductor (MIS) structure for high temperature process monitoring and leak detection applications in fields such as the automotive, chemical and petroleum industries. In this work, a thin tantalum oxide (Ta2O5) layer was exploited with the purpose of sensitivity improvement, because tantalum oxide has good stability at high temperature with high permeability for hydrogen gas. Silicon carbide (SiC) was used as a substrate for high-temperature applications. We fabricated Pd/Ta2O5/SiC-based hydrogen gas sensors, and the dependence of their I-V characteristics and capacitance response properties on hydrogen concentrations were analyzed in the temperature range from room temperature to 500 °C. According to the results, our sensor shows promising performance for hydrogen gas detection at high temperatures. PMID:24113685
Silicon carbide-based hydrogen gas sensors for high-temperature applications.

PubMed

Kim, Seongjeen; Choi, Jehoon; Jung, Minsoo; Joo, Sungjae; Kim, Sangchoel

2013-10-09

We investigated SiC-based hydrogen gas sensors with metal-insulator-semiconductor (MIS) structure for high temperature process monitoring and leak detection applications in fields such as the automotive, chemical and petroleum industries. In this work, a thin tantalum oxide (Ta2O5) layer was exploited with the purpose of sensitivity improvement, because tantalum oxide has good stability at high temperature with high permeability for hydrogen gas. Silicon carbide (SiC) was used as a substrate for high-temperature applications. We fabricated Pd/Ta2O5/SiC-based hydrogen gas sensors, and the dependence of their I-V characteristics and capacitance response properties on hydrogen concentrations were analyzed in the temperature range from room temperature to 500 °C. According to the results, our sensor shows promising performance for hydrogen gas detection at high temperatures.
Fabrication method for a room temperature hydrogen sensor

NASA Technical Reports Server (NTRS)

Shukla, Satyajit V. (Inventor); Cho, Hyoung (Inventor); Seal, Sudipta (Inventor); Ludwig, Lawrence (Inventor)

2011-01-01

A sensor for selectively determining the presence and measuring the amount of hydrogen in the vicinity of the sensor. The sensor comprises a MEMS device coated with a nanostructured thin film of indium oxide doped tin oxide with an over layer of nanostructured barium cerate with platinum catalyst nanoparticles. Initial exposure to a UV light source, at room temperature, causes burning of organic residues present on the sensor surface and provides a clean surface for sensing hydrogen at room temperature. A giant room temperature hydrogen sensitivity is observed after making the UV source off. The hydrogen sensor of the invention can be usefully employed for the detection of hydrogen in an environment susceptible to the incursion or generation of hydrogen and may be conveniently used at room temperature.
Synthesis of Ni/Graphene Nanocomposite for Hydrogen Storage.

PubMed

Zhou, Chunyu; Szpunar, Jerzy A; Cui, Xiaoyu

2016-06-22

We have designed a Ni-graphene composite for hydrogen storage with Ni nanoparticles of 10 nm in size, uniformly dispersed over a graphene substrate. This system exhibits attractive features like high gravimetric density, ambient conditions, and low activation temperature for hydrogen release. When charged at room temperature and an atmospheric hydrogen pressure of 1 bar, it could yield a hydrogen capacity of 0.14 wt %. When hydrogen pressure increased to 60 bar, the sorbent had a hydrogen gravimetric density of 1.18 wt %. The hydrogen release could occur at an operating temperature below 150 °C and completes at 250 °C.

Purification of Hydrogen

DOEpatents

Newton, A S

1950-12-05

Disclosed is a process for purifying hydrogen containing various gaseous impurities by passing the hydrogen over a large surface of uranium metal at a temperature above the decomposition temperature of uranium hydride, and below the decomposition temperature of the compounds formed by the combination of the uranium with the impurities in the hydrogen.
LARGE-SCALE HYDROGEN PRODUCTION FROM NUCLEAR ENERGY USING HIGH TEMPERATURE ELECTROLYSIS

DOE Office of Scientific and Technical Information (OSTI.GOV)

James E. O'Brien

2010-08-01

Hydrogen can be produced from water splitting with relatively high efficiency using high-temperature electrolysis. This technology makes use of solid-oxide cells, running in the electrolysis mode to produce hydrogen from steam, while consuming electricity and high-temperature process heat. When coupled to an advanced high temperature nuclear reactor, the overall thermal-to-hydrogen efficiency for high-temperature electrolysis can be as high as 50%, which is about double the overall efficiency of conventional low-temperature electrolysis. Current large-scale hydrogen production is based almost exclusively on steam reforming of methane, a method that consumes a precious fossil fuel while emitting carbon dioxide to the atmosphere. Demandmore » for hydrogen is increasing rapidly for refining of increasingly low-grade petroleum resources, such as the Athabasca oil sands and for ammonia-based fertilizer production. Large quantities of hydrogen are also required for carbon-efficient conversion of biomass to liquid fuels. With supplemental nuclear hydrogen, almost all of the carbon in the biomass can be converted to liquid fuels in a nearly carbon-neutral fashion. Ultimately, hydrogen may be employed as a direct transportation fuel in a “hydrogen economy.” The large quantity of hydrogen that would be required for this concept should be produced without consuming fossil fuels or emitting greenhouse gases. An overview of the high-temperature electrolysis technology will be presented, including basic theory, modeling, and experimental activities. Modeling activities include both computational fluid dynamics and large-scale systems analysis. We have also demonstrated high-temperature electrolysis in our laboratory at the 15 kW scale, achieving a hydrogen production rate in excess of 5500 L/hr.« less
An numerical analysis of high-temperature helium reactor power plant for co-production of hydrogen and electricity

NASA Astrophysics Data System (ADS)

Dudek, M.; Podsadna, J.; Jaszczur, M.

2016-09-01

In the present work, the feasibility of using a high temperature gas cooled nuclear reactor (HTR) for electricity generation and hydrogen production are analysed. The HTR is combined with a steam and a gas turbine, as well as with the system for heat delivery for medium temperature hydrogen production. Industrial-scale hydrogen production using copper-chlorine (Cu-Cl) thermochemical cycle is considered and compared with high temperature electrolysis. Presented cycle shows a very promising route for continuous, efficient, large-scale and environmentally benign hydrogen production without CO2 emissions. The results show that the integration of a high temperature helium reactor, with a combined cycle for electric power generation and hydrogen production, may reach very high efficiency and could possibly lead to a significant decrease of hydrogen production costs.
Effects of Internal and External Hydrogen on Inconel 718

NASA Technical Reports Server (NTRS)

Walter, R. J.; Frandsen, J. D.

1999-01-01

Internal hydrogen embrittlement (IHE) and hydrogen environment embrittlement (HEE) tensile and bend crack growth tests were performed on Inconel 718. For the IHE tests, the specimens were precharged to approximately 90 ppm hydrogen by exposure to 34.5 MPa H2 at 650 C. The HEE tests were performed in 34.5 MPa H2. Parameters evaluated were test temperature, strain rate for smooth and notch specimen geometries. The strain rate effect was very significant at ambient temperature for both IHE and HEE and decreased with increasing temperatures. For IHE, the strain rate effect was neglible at 260'C, and for HEE the strain rate effect was neglible at 400 C. At low temperatures, IHE was more severe than HEE, and at high temperatures HEE was more severe than IHE with a cross over temperature about 350 C. At 350 C, the equilibrium hydrogen concentration in Inconel 718 is about 50% lower than the hydrogen content of the precharged IHE specimens. Dislocation hydrogen sweeping of surface absorbed hydrogen was the likely transport mechanism for increasing the hydrogen concentration in the HEE tests sufficiently to produce the same degree of embrittlement as that of the more highly hydrogen charged IHE specimens. The main IHE fracture characteristic was formation of large, brittle flat facets, which decreased with increasing test temperature. The IHE fracture matrix surrounding the large facets ranged between brittle fine faceted to microvoid ductility depending upon strain rate, specimen geometry as well as temperature. The HEE fractures were characteristically fine featured, transgranular and brittle with a significant portion forming a "saw tooth" crystallographic pattern. Both IHE and HEE fractures were predominantly along the {1 1 1) slip and twin boundaries. With respect to embrittlement mechanism, it was postulated that dislocation hydrogen sweeping and hydrogen enhanced localized plasticity were active in HEE and IHE for concentrating hydrogen along (1 1 1) slip and twin planes. Final brittle failure occurred by hydrogen induced planer decohesion.
Trials of flexible pipe in sour service reveal degradation

DOE Office of Scientific and Technical Information (OSTI.GOV)

Al-Maslamani, M.J.

Field trials on flexible pipe offshore Qatar have shown that, under sour conditions, the layered, composite material can suffer severe degradation leading to failure. The failure demonstrates the significant effects of stress level, environmental aggressiveness, and localized hard zones in promoting sulfide stress cracking. Permeability of the sour gas through the composite layer of the flexible pipe resulted in varying degrees of sulfide attack and hydrogen embrittlement, depending on the susceptibility of the multilayered material. In the trials, the material was used as a gas-lift line in a sour-oil field in the Arabian Gulf. Flexible pipes have been used successfullymore » for transporting methanol, benzene, and gas condensates in wet sweet environments at temperatures of up to 80 C. Little or no information, however, has been available as to its corrosion resistance in sour-service wells containing 6% CO{sub 2} with 3% H{sub 2}S partial pressures and at moderate temperatures. The paper discusses an underwater survey to evaluate the damage, visual inspection, mechanical tests, metallographic exam, and trial results.« less
77 FR 73282 - Airworthiness Directives; The Boeing Company Airplanes

Federal Register 2010, 2011, 2012, 2013, 2014

2012-12-10

... system for the angle of attack sensor, the total air temperature, and the pitot probes. We are issuing this AD to prevent ice from forming on air data system sensors and consequent loss of or misleading... angle of attack sensor, the total air temperature, and the pitot probes. Actions Since Issuance of NPRM...
Aerothermal tests of a 12.5 percent cone at Mach 6.7 for various Reynolds numbers, angles of attack and nose shapes. [conducted in Langley 8-foot high temperature tunnel

NASA Technical Reports Server (NTRS)

Nowak, R. J.; Albertson, C. W.; Hunt, L. R.

1984-01-01

The effects of free-stream unit Reynolds number, angle of attack, and nose shape on the aerothermal environment of a 3-ft basediameter, 12.5 deg half-angle cone were investigated in the Langley 8-foot high temperature tunnel at Mach 6.7. The average total temperature was 3300 R, the freestream unit Reynolds number ranged from 400,000 to 1,400,000 per foot, and the angle of attack ranged from 0 deg to 10 deg. Three nose configurations were tested on the cone: a 3-in-radius tip, a 1-in-radius tip on an ogive frustum, and a sharp tip on an ogive frustum. Surface-pressure and cold-wall heating-rate distributions were obtained for laminar, transitional temperature in the shock layer were obtained. The location of the start of transition moved forward both on windward and leeward sides with increasing free-stream Reynolds numbers, increasing angle of attack, and decreasing nose bluntness.
Behavior of hydrogen in alpha-iron at lower temperatures

NASA Technical Reports Server (NTRS)

Weizer, V. G.

1973-01-01

Evidence is presented that the low temperature anomalies in the hydrogen occlusive behavior of alpha iron can be explained by means of a molecular occlusion theory. This theory proposes that the stable state of the absorbed hydrogen changes from atomic at high temperatures to molecular as the temperature is lowered below a critical value. Theories proposing to explain the anomalous behavior as being due to the capture, at lower temperatures, of hydrogen in traps are shown to be unacceptable.
Method for charging a hydrogen getter

DOEpatents

Tracy, C. Edwin; Keyser, Matthew A.; Benson, David K.

1998-01-01

A method for charging a sample of either a permanent or reversible getter material with a high concentration of hydrogen while maintaining a base pressure below 10.sup.-4 torr at room temperature involves placing the sample of hydrogen getter material in a chamber, activating the sample of hydrogen getter material, overcharging the sample of getter material through conventional charging techniques to a high concentration of hydrogen, and then subjecting the sample of getter material to a low temperature vacuum bake-out process. Application of the method results in a reversible hydrogen getter which is highly charged to maximum capacities of hydrogen and which concurrently exhibits minimum hydrogen vapor pressures at room temperatures.
Finite-Temperature Hydrogen Adsorption/Desorption Thermodynamics Driven by Soft Vibration Modes

DOE Office of Scientific and Technical Information (OSTI.GOV)

Woo, Sung-Jae; Lee, Eui-Sup; Yoon, Mina

2013-01-01

It is widely accepted that room-temperature hydrogen storage on nanostructured or porous materials requires enhanced dihydrogen adsorption. In this work we reveal that room-temperature hydrogen storage is possible not only by the enhanced adsorption, but also by making use of the vibrational free energy from soft vibration modes. These modes exist for example in the case of metallo-porphyrin-incorporated graphenes (M-PIGs) with out-of-plane ( buckled ) metal centers. There, the in-plane potential surfaces are flat because of multiple-orbital-coupling between hydrogen molecules and the buckled-metal centers. This study investigates the finite-temperature adsorption/desorption thermodynamics of hydrogen molecules adsorbed on M-PIGs by employing first-principlesmore » total energy and vibrational spectrum calculations. Our results suggest that the current design strategy for room-temperature hydrogen storage materials should be modified by explicitly taking finite-temperature vibration thermodynamics into account.« less
Influence of hydrogen effusion from hydrogenated silicon nitride layers on the regeneration of boron-oxygen related defects in crystalline silicon

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wilking, S., E-mail: Svenja.Wilking@uni-konstanz.de; Ebert, S.; Herguth, A.

The degradation effect boron doped and oxygen-rich crystalline silicon materials suffer from under illumination can be neutralized in hydrogenated silicon by the application of a regeneration process consisting of a combination of slightly elevated temperature and carrier injection. In this paper, the influence of variations in short high temperature steps on the kinetics of the regeneration process is investigated. It is found that hotter and longer firing steps allowing an effective hydrogenation from a hydrogen-rich silicon nitride passivation layer result in an acceleration of the regeneration process. Additionally, a fast cool down from high temperature to around 550 °C seems tomore » be crucial for a fast regeneration process. It is suggested that high cooling rates suppress hydrogen effusion from the silicon bulk in a temperature range where the hydrogenated passivation layer cannot release hydrogen in considerable amounts. Thus, the hydrogen content of the silicon bulk after the complete high temperature step can be increased resulting in a faster regeneration process. Hence, the data presented here back up the theory that the regeneration process might be a hydrogen passivation of boron-oxygen related defects.« less
Study on the hydrogenation of Zircaloy-4

NASA Astrophysics Data System (ADS)

da Silva Dupim, Ivaldete; Moreira, João M. L.; Silva, Selma Luiza; Silva, Cecilia Chaves Guedes e.; Nunes, Oswaldo; Gomide, Ricardo Gonçalves

2012-08-01

In this article we investigate producing Zirconium powder from discarded Zircaloy-4 material through the hydride-dehydride method. We restrict our study to the first part of the method, namely the hydrogenation process. Differential thermal analyses of the hydrogenation process of the Zircaloy-4 show that no hydrogen absorption occurs at temperatures below 573 K and hydrogen gas pressure of 25 kPa. When the system temperature is raised to around 770 K, with the same gas pressure, the protecting oxide layer of the specimens can be overcome and they are quickly hydrogenated. The bulk of the reaction occurs in about 5 min with the precipitation of Zirconium hydrides in the Zr-δ and Zr-ɛ phases. Once the temperature passes 573 K, the incubation time to initiate the reaction is short (about 5 min). Tests in a tube furnace system with larger samples, hydrogen pressure varying from 30 to 180 kPa, and temperature from 700 to 833.15 K, show that the specimens are fully hydrogenated and can be easily pulverized. The results indicate that the hydrogenation of the Zircaloy-4 chips can be successfully undertaken at temperatures around 770 K and hydrogen gas pressure as low as 30 kPa.
Experimental study of catalytic hydrogenation by using an in-situ hydrogen measuring technique. Final report

DOE Office of Scientific and Technical Information (OSTI.GOV)

Chiang, S.H.; Klinzing, G.E.; Cheng, Y.S.

1984-12-01

An in-situ technique for measuring hydrogen concentration (partial pressure) had been previously used to measure static properties (hydrogen solubilities, vapor pressures of hydrocarbons, etc.). Because of its good precision (2% relative error) and relatively short respond time (9.7 to 2.0 seconds at 589 to 728K), the technique was successfully applied to a dynamic study of hydrogenation reactions in this work. Furthermore, the technique is to be tested for industrial uses. Hydrogen/1-methylnaphthalene system was experimentally investigated in a one-liter autoclave equipped with a magnetically driven stirrer and temperature controlling devices. Catalytic hydrogenation of 1-methylnaphthalene was studied in the presence of sulfidedmore » Co-Mo-Al2O3 catalyst. In addition, the vapor/liquid equilibrium relationship was determined by using this technique. Hydrogenation reaction runs were performed at temperatures of 644.1, 658.0 and 672.0K and pressures up to 9.0 MPa. The ring hydrogenation, resulting in 1- and 5-methyltetralin, was found to be the dominant reaction. This is in agreement with cited literature. Effects of hydrogen partial pressure, operating temperature, as well as presulfided catalyst are also investigated and discussed in this work. The vapor pressure of 1-methylnaphthalene was measured over a temperature range of 555.2 to 672.0K. The results are in good agreement with literature data. Measurements for hydrogen solubility in 1-methylnaphthalene were conducted over temperature and pressure range of 598 to 670K and 5.2 to 8.8 MPa, respectively. Similar to previously reported results, the hydrogen solubility increases with increasing temperature when total pressure is held constant. A linear relation is found between the hydrogen solubility and hydrogen partial pressure. 21 refs., 13 figs., 10 tabs.« less
Two-step gasification of cattle manure for hydrogen-rich gas production: Effect of biochar preparation temperature and gasification temperature.

PubMed

Xin, Ya; Cao, Hongliang; Yuan, Qiaoxia; Wang, Dianlong

2017-10-01

Two-step gasification process was proposed to dispose cattle manure for hydrogen rich gas production. The effect of temperature on product distribution and biochar properties were first studied in the pyrolysis-carbonization process. The steam gasification of biochar derived from different pyrolysis-carbonization temperatures was then performed at 750°C and 850°C. The biochar from the pyrolysis-carbonization temperatures of 500°C had high carbon content and low volatiles content. According to the results of gasification stage, the pyrolysis-carbonization temperature of 500°C and the gasification temperature of 850°C were identified as the suitable conditions for hydrogen production. We obtained 1.61m 3 /kg of syngas production, 0.93m 3 /kg of hydrogen yield and 57.58% of hydrogen concentration. This study shows that two-step gasification is an efficient waste-to-hydrogen energy process. Copyright © 2017 Elsevier Ltd. All rights reserved.
Hydrogenation apparatus

DOEpatents

Friedman, Joseph [Encino, CA; Oberg, Carl L [Canoga Park, CA; Russell, Larry H [Agoura, CA

1981-01-01

Hydrogenation reaction apparatus comprising a housing having walls which define a reaction zone and conduits for introducing streams of hydrogen and oxygen into the reaction zone, the oxygen being introduced into a central portion of the hydrogen stream to maintain a boundary layer of hydrogen along the walls of the reaction zone. A portion of the hydrogen and all of the oxygen react to produce a heated gas stream having a temperature within the range of from 1100.degree. to 1900.degree. C., while the boundary layer of hydrogen maintains the wall temperature at a substantially lower temperature. The heated gas stream is introduced into a hydrogenation reaction zone and provides the source of heat and hydrogen for a hydrogenation reaction. There also is provided means for quenching the products of the hydrogenation reaction. The present invention is particularly suitable for the hydrogenation of low-value solid carbonaceous materials to provide high yields of more valuable liquid and gaseous products.
Hydrogenation apparatus

DOEpatents

Friedman, J.; Oberg, C. L.; Russell, L. H.

1981-06-23

Hydrogenation reaction apparatus is described comprising a housing having walls which define a reaction zone and conduits for introducing streams of hydrogen and oxygen into the reaction zone, the oxygen being introduced into a central portion of the hydrogen stream to maintain a boundary layer of hydrogen along the walls of the reaction zone. A portion of the hydrogen and all of the oxygen react to produce a heated gas stream having a temperature within the range of from 1,100 to 1,900 C, while the boundary layer of hydrogen maintains the wall temperature at a substantially lower temperature. The heated gas stream is introduced into a hydrogenation reaction zone and provides the source of heat and hydrogen for a hydrogenation reaction. There also is provided means for quenching the products of the hydrogenation reaction. The present invention is particularly suitable for the hydrogenation of low-value solid carbonaceous materials to provide high yields of more valuable liquid and gaseous products. 2 figs.
Method for charging a hydrogen getter

DOEpatents

Tracy, C.E.; Keyser, M.A.; Benson, D.K.

1998-09-15

A method for charging a sample of either a permanent or reversible getter material with a high concentration of hydrogen while maintaining a base pressure below 10{sup {minus}4} torr at room temperature involves placing the sample of hydrogen getter material in a chamber, activating the sample of hydrogen getter material, overcharging the sample of getter material through conventional charging techniques to a high concentration of hydrogen, and then subjecting the sample of getter material to a low temperature vacuum bake-out process. Application of the method results in a reversible hydrogen getter which is highly charged to maximum capacities of hydrogen and which concurrently exhibits minimum hydrogen vapor pressures at room temperatures. 9 figs.
Thermodynamics and vibrational study of hydrogenated carbon nanotubes: A DFT study

NASA Astrophysics Data System (ADS)

Khalil, Rana M. Arif; Hussain, Fayyaz; Rana, Anwar Manzoor; Imran, Muhammad

2018-02-01

Thermodynamic stability of the hydrogenated carbon nanotubes has been explored in the chemisorption limit. Statistical physics and density functional theory calculations have been used to predict hydrogen release temperatures at standard pressure in zigzag and armchair carbon nanotubes. It is found that hydrogen release temperatures decrease with increase in diameters of hydrogenated zigzag carbon nanotubes (CNTs) but opposite trend is noted in armchair CNTs at standard pressure of 1 bar. The smaller diameter hydrogenated zigzag CNTs have large values of hydrogen release temperature due to the stability of Csbnd H bonds. The vibrational density of states for hydrogenated carbon nanotubes have been calculated to confirm the Csbnd H stretching mode caused by sp3 hybridization.
Elastomer Reinforced with Carbon Nanotubes

NASA Technical Reports Server (NTRS)

Hudson, Jared L.; Krishnamoorti, Ramanan

2009-01-01

Elastomers are reinforced with functionalized, single-walled carbon nanotubes (SWNTs) giving them high-breaking strain levels and low densities. Cross-linked elastomers are prepared using amine-terminated, poly(dimethylsiloxane) (PDMS), with an average molecular weight of 5,000 daltons, and a functionalized SWNT. Cross-link densities, estimated on the basis of swelling data in toluene (a dispersing solvent) indicated that the polymer underwent cross-linking at the ends of the chains. This thermally initiated cross-linking was found to occur only in the presence of the aryl alcohol functionalized SWNTs. The cross-link could have been via a hydrogen-bonding mechanism between the amine and the free hydroxyl group, or via attack of the amine on the ester linage to form an amide. Tensile properties examined at room temperature indicate a three-fold increase in the tensile modulus of the elastomer, with rupture and failure of the elastomer occurring at a strain of 6.5.
DOE Office of Scientific and Technical Information (OSTI.GOV)

Pandey, Ravindra; Usui, Kota; Livingstone, Ruth A.

Ice-nucleating organisms play important roles in the environment. With their ability to induce ice formation at temperatures just below the ice melting point, bacteria such as Pseudomonas syringae attack plants through frost damage using specialized ice-nucleating proteins. Besides the impact on agriculture and microbial ecology, airborne P. syringae can affect atmospheric glaciation processes, with consequences for cloud evolution, precipitation, and climate. Biogenic ice nucleation is also relevant for artificial snow production and for biomimetic materials for controlled interfacial freezing. We use interface-specific sum frequency generation (SFG) spectroscopy to show that hydrogen bonding at the water-bacteria contact imposes structural ordering onmore » the adjacent water network. Experimental SFG data and molecular dynamics simulations demonstrate that ice active sites within P. syringae feature unique hydrophilic-hydrophobic patterns to enhance ice nucleation. Finally, the freezing transition is further facilitated by the highly effective removal of latent heat from the nucleation site, as apparent from time-resolved SFG spectroscopy.« less

Activation energy for diamond growth from the carbon-hydrogen gas system at low substrate temperatures

NASA Astrophysics Data System (ADS)

Stiegler, J.; Lang, T.; von Kaenel, Y.; Michler, J.; Blank, E.

1997-01-01

The growth kinetics of diamond films deposited at low substrate temperatures (600-400 °C) from the carbon-hydrogen gas system have been studied. When the substrate temperature alone was varied, independently of all other process parameters in the microwave plasma reactor, an activation energy in the order of 7 kcal/mol was observed. This value did not change with different carbon concentrations in hydrogen. It is supposed that growth kinetics in this temperature range are controlled by a single chemical reaction, probably the abstraction of surface bonded hydrogen by gas phase atomic hydrogen.
Temperature- and composition-dependent hydrogen diffusivity in palladium from statistically-averaged molecular dynamics

DOE Office of Scientific and Technical Information (OSTI.GOV)

Zhou, Xiaowang; Heo, Tae Wook; Wood, Brandon C.

Solid-state hydrogen storage materials undergo complex phase transformations whose kinetics is often limited by hydrogen diffusion. Among metal hydrides, palladium hydride undergoes a diffusional phase transformation upon hydrogen uptake, during which the hydrogen diffusivity varies with hydrogen composition and temperature. Here we perform robust statistically-averaged molecular dynamics simulations to obtain a well-converged analytical expression for hydrogen diffusivity in bulk palladium that is valid throughout all stages of the reaction. Our studies confirm significant dependence of the diffusivity on composition and temperature that elucidate key trends in the available experimental measurements. Whereas at low hydrogen compositions, a single process dominates, atmore » high hydrogen compositions, diffusion is found to exhibit behavior consistent with multiple hopping barriers. Further analysis, supported by nudged elastic band computations, suggests that the multi-barrier diffusion can be interpreted as two distinct mechanisms corresponding to hydrogen-rich and hydrogen-poor local environments.« less
Temperature- and composition-dependent hydrogen diffusivity in palladium from statistically-averaged molecular dynamics

DOE PAGES

Zhou, Xiaowang; Heo, Tae Wook; Wood, Brandon C.; ...

2018-03-09

Solid-state hydrogen storage materials undergo complex phase transformations whose kinetics is often limited by hydrogen diffusion. Among metal hydrides, palladium hydride undergoes a diffusional phase transformation upon hydrogen uptake, during which the hydrogen diffusivity varies with hydrogen composition and temperature. Here we perform robust statistically-averaged molecular dynamics simulations to obtain a well-converged analytical expression for hydrogen diffusivity in bulk palladium that is valid throughout all stages of the reaction. Our studies confirm significant dependence of the diffusivity on composition and temperature that elucidate key trends in the available experimental measurements. Whereas at low hydrogen compositions, a single process dominates, atmore » high hydrogen compositions, diffusion is found to exhibit behavior consistent with multiple hopping barriers. Further analysis, supported by nudged elastic band computations, suggests that the multi-barrier diffusion can be interpreted as two distinct mechanisms corresponding to hydrogen-rich and hydrogen-poor local environments.« less
SSH2S: Hydrogen storage in complex hydrides for an auxiliary power unit based on high temperature proton exchange membrane fuel cells

NASA Astrophysics Data System (ADS)

Baricco, Marcello; Bang, Mads; Fichtner, Maximilian; Hauback, Bjorn; Linder, Marc; Luetto, Carlo; Moretto, Pietro; Sgroi, Mauro

2017-02-01

The main objective of the SSH2S (Fuel Cell Coupled Solid State Hydrogen Storage Tank) project was to develop a solid state hydrogen storage tank based on complex hydrides and to fully integrate it with a High Temperature Proton Exchange Membrane (HT-PEM) fuel cell stack. A mixed lithium amide/magnesium hydride system was used as the main storage material for the tank, due to its high gravimetric storage capacity and relatively low hydrogen desorption temperature. The mixed lithium amide/magnesium hydride system was coupled with a standard intermetallic compound to take advantage of its capability to release hydrogen at ambient temperature and to ensure a fast start-up of the system. The hydrogen storage tank was designed to feed a 1 kW HT-PEM stack for 2 h to be used for an Auxiliary Power Unit (APU). A full thermal integration was possible thanks to the high operation temperature of the fuel cell and to the relative low temperature (170 °C) for hydrogen release from the mixed lithium amide/magnesium hydride system.
Proximal detection of energetic materials on fabrics by UV-Raman spectroscopy

NASA Astrophysics Data System (ADS)

Chirico, R.; Almaviva, S.; Colao, F.; Fiorani, L.; Nuvoli, M.; Schweikert, W.; Schnürer, F.; Cassioli, L.; Grossi, S.; Mariani, L.; Angelini, F.; Menicucci, I.; Palucci, A.

2014-05-01

In the last decades there have been several terroristic attacks with improvised explosive devices (IED) that have raised the need for new instrumentation, for homeland security applications, to obtain a reliable and effective fight against terrorism. Public transportation has been around for about 150 years, but terroristic attacks against buses, trains, subways, etc., is a relatively recent phenomenon [1]. Since 1970, transportation has been an increasingly attractive target for terrorists. Most of the attacks to transport infrastructures take place in countries where public transportation is the primary way to move. Terrorists prefer to execute a smaller-scale attack with certainty of success rather than a complex and demanding operation to cause massive death and destruction. [1]. Many commonly available materials, such as fertilizer, gunpowder, and hydrogen peroxide, can be used as explosives and other materials, such as nails, glass, or metal fragments, can be used to increase the amount of shrapnel propelled by the explosion. The majority of substances that are classified as chemical explosives generally contain oxygen, nitrogen and oxidable elements such as carbon and hydrogen [2]. The most common functional group in military explosives is NO2. That functionality can be attached to oxygen (ONO2) in the nitrate esters (PETN), to carbon (C-NO2) in the nitroarenes (TNT) and nitroalkanes (Nitromethane), and to nitrogen (N-NO2) as in the nitramines (RDX). Some organic peroxides, such as TATP and HMTD, are popular amongst terrorists because they are powerful initiators that can be easily prepared from easily available ingredients. Azides are also powerful primary explosives commonly used as initiators (commercial detonators) in civilian and military operations, therefore they could be potentially used by terrorists as initiators for IEDs.
Complex hydrides for hydrogen storage

DOEpatents

Zidan, Ragaiy

2006-08-22

A hydrogen storage material and process of forming the material is provided in which complex hydrides are combined under conditions of elevated temperatures and/or elevated temperature and pressure with a titanium metal such as titanium butoxide. The resulting fused product exhibits hydrogen desorption kinetics having a first hydrogen release point which occurs at normal atmospheres and at a temperature between 50.degree. C. and 90.degree. C.
Electrocatalytic Hydrogenation of Phenol over Platinum and Rhodium: Unexpected Temperature Effects Resolved

DOE Office of Scientific and Technical Information (OSTI.GOV)

Singh, Nirala; Song, Yang; Gutiérrez, Oliver Y.

2016-11-04

Both electrocatalytic hydrogenation (ECH) and thermal hydrogenation (TH) of phenol by Pt and Rh show a roll-over in rate with increasing temperature without changing the principal reaction pathways. The negative effect of temperature for aqueous-phase phenol H2 and electrocatalytic hydrogenation on Pt and Rh is deduced to be due to the unexpected buildup of dehydrogenated phenol adsorbates, which block active sites. Rates of ECH and TH increase similarly with increasing hydrogen chemical potential whether induced by applied potential or H2 pressure, both via increasing H coverage, and indirectly by removing site blockers, a very strong effect at high temperature. Thismore » enables unprecedented rates in the TH of phenol at these temperatures.« less
Effect of hydrogen on the integrity of aluminium–oxide interface at elevated temperatures

PubMed Central

Li, Meng; Xie, De-Gang; Ma, Evan; Li, Ju; Zhang, Xi-Xiang; Shan, Zhi-Wei

2017-01-01

Hydrogen can facilitate the detachment of protective oxide layer off metals and alloys. The degradation is usually exacerbated at elevated temperatures in many industrial applications; however, its origin remains poorly understood. Here by heating hydrogenated aluminium inside an environmental transmission electron microscope, we show that hydrogen exposure of just a few minutes can greatly degrade the high temperature integrity of metal–oxide interface. Moreover, there exists a critical temperature of ∼150 °C, above which the growth of cavities at the metal–oxide interface reverses to shrinkage, followed by the formation of a few giant cavities. Vacancy supersaturation, activation of a long-range diffusion pathway along the detached interface and the dissociation of hydrogen-vacancy complexes are critical factors affecting this behaviour. These results enrich the understanding of hydrogen-induced interfacial failure at elevated temperatures. PMID:28218260
Inverse Temperature Dependence of Nuclear Quantum Effects in DNA Base Pairs

PubMed Central

2016-01-01

Despite the inherently quantum mechanical nature of hydrogen bonding, it is unclear how nuclear quantum effects (NQEs) alter the strengths of hydrogen bonds. With this in mind, we use ab initio path integral molecular dynamics to determine the absolute contribution of NQEs to the binding in DNA base pair complexes, arguably the most important hydrogen-bonded systems of all. We find that depending on the temperature, NQEs can either strengthen or weaken the binding within the hydrogen-bonded complexes. As a somewhat counterintuitive consequence, NQEs can have a smaller impact on hydrogen bond strengths at cryogenic temperatures than at room temperature. We rationalize this in terms of a competition of NQEs between low-frequency and high-frequency vibrational modes. Extending this idea, we also propose a simple model to predict the temperature dependence of NQEs on hydrogen bond strengths in general. PMID:27195654
Internal hydrogen-induced subcritical crack growth in austenitic stainless steels

NASA Astrophysics Data System (ADS)

Huang, J. H.; Altstetter, C. J.

1991-11-01

The effects of small amounts of dissolved hydrogen on crack propagation were determined for two austenitic stainless steel alloys, AISI 301 and 310S. In order to have a uniform distribution of hydrogen in the alloys, they were cathodically charged at high temperature in a molten salt electrolyte. Sustained load tests were performed on fatigue precracked specimens in air at 0 ‡C, 25 ‡C, and 50 ‡C with hydrogen contents up to 41 wt ppm. The electrical potential drop method with optical calibration was used to continuously monitor the crack position. Log crack velocity vs stress intensity curves had definite thresholds for subcritical crack growth (SCG), but stage II was not always clearly delineated. In the unstable austenitic steel, AISI 301, the threshold stress intensity decreased with increasing hydrogen content or increasing temperature, but beyond about 10 wt ppm, it became insensitive to hydrogen concentration. At higher concentrations, stage II became less distinct. In the stable stainless steel, subcritical crack growth was observed only for a specimen containing 41 wt ppm hydrogen. Fractographic features were correlated with stress intensity, hydrogen content, and temperature. The fracture mode changed with temperature and hydrogen content. For unstable austenitic steel, low temperature and high hydrogen content favored intergranular fracture while microvoid coalescence dominated at a low hydrogen content. The interpretation of these phenomena is based on the tendency for stress-induced phase transformation, the different hydrogen diffusivity and solubility in ferrite and austenite, and outgassing from the crack tip. After comparing the embrittlement due to internal hydrogen with that in external hydrogen, it is concluded that the critical hydrogen distribution for the onset of subcritical crack growth is reached at a location that is very near the crack tip.
Sorption of hydrogen by silica aerogel at low-temperatures

NASA Astrophysics Data System (ADS)

Dolbin, A. V.; Khlistyuck, M. V.; Esel'son, V. B.; Gavrilko, V. G.; Vinnikov, N. A.; Basnukaeva, R. M.; Martsenuk, V. E.; Veselova, N. V.; Kaliuzhnyi, I. A.; Storozhko, A. V.

2018-02-01

The programmed thermal desorption method is used at temperatures of 7-95 K to study the sorption and subsequent desorption of hydrogen by a sample of silica aerogel. Physical sorption of hydrogen owing to the weak van-der-Waals interaction of hydrogen molecules with the silicon dioxide walls of the pores of the sample was observed over the entire temperature range. The total capacity of the aerogel sample for hydrogen was ˜1.5 mass %. It was found that when the sample temperature was lowered from 95 to 60 K, the characteristic sorption times for hydrogen by the silica aerogel increase; this is typical of thermally activated diffusion (Ea ≈ 408 K). For temperatures of 15-45 K the characteristic H2 sorption times depended weakly on temperature, presumably because of the predominance of a tunnel mechanism for diffusion over thermally activated diffusion. Below 15 K the characteristic sorption times increase somewhat as the temperature is lowered; this may be explained by the formation of a monolayer of H2 molecules on the surface of the aerogel grains.
Advances in catalysts for internal reforming in high temperature fuel cells

NASA Astrophysics Data System (ADS)

Dicks, A. L.

Catalytic steam reforming of natural gas is an attractive method of producing the hydrogen required by the present generation of fuel cells. The molten carbonate (MCFC) and solid oxide (SOFC) fuel cells operate at high enough temperatures for the endothermic steam reforming reaction to be carried out within the stack. For the MCFC, the conventional anodes have insufficient activity to catalyse the steam reforming of natural gas. For these cells, internal reforming can be achieved only with the addition of a separate catalyst, preferably located in close proximity to the anode. However, in the so-called `Direct Internal Reforming' configuration, attack from alkali in the MCFC may severely limit catalyst lifetime. In the case of the state-of-the-art SOFC, natural gas can be reformed directly on the nickel cermet anode. However, in the SOFC, temperature variations in the cell caused by the reforming reaction may limit the amount of internal reforming that can be allowed in practice. In addition, some external pre-reforming may be desirable to remove high molecular weight hydrocarbons from the fuel gas, which would otherwise crack to produce elemental carbon. Degradation of the SOFC anode may also be a problem when internal reforming is carried out. This has prompted several research groups to investigate the use of alternative anode materials.
Liquid metal hydrogen barriers

DOEpatents

Grover, George M.; Frank, Thurman G.; Keddy, Edward S.

1976-01-01

Hydrogen barriers which comprise liquid metals in which the solubility of hydrogen is low and which have good thermal conductivities at operating temperatures of interest. Such barriers are useful in nuclear fuel elements containing a metal hydride moderator which has a substantial hydrogen dissociation pressure at reactor operating temperatures.
Method of generating hydrogen-storing hydride complexes

DOEpatents

None, None

2013-05-14

A ternary hydrogen storage system having a constant stoichiometric molar ratio of LiNH.sub.2:MgH.sub.2:LiBH.sub.4 of 2:1:1. It was found that the incorporation of MgH.sub.2 particles of approximately 10 nm to 20 nm exhibit a lower initial hydrogen release temperature of 150.degree. C. Furthermore, it is observed that the particle size of LiBNH quaternary hydride has a significant effect on the hydrogen sorption concentration with an optimum size of 28 nm. The as-synthesized hydrides exhibit two main hydrogen release temperatures, one around 160.degree. C. and the other around 300.degree. C., with the main hydrogen release temperature reduced from 310.degree. C. to 270.degree. C., while hydrogen is first reversibly released at temperatures as low as 150.degree. C. with a total hydrogen capacity of 6 wt. % to 8 wt. %. Detailed thermal, capacity, structural and microstructural properties have been demonstrated and correlated with the activation energies of these materials.
Hydrogen-storing hydride complexes

DOEpatents

Srinivasan, Sesha S [Tampa, FL; Niemann, Michael U [Venice, FL; Goswami, D Yogi [Tampa, FL; Stefanakos, Elias K [Tampa, FL

2012-04-10

A ternary hydrogen storage system having a constant stoichiometric molar ratio of LiNH.sub.2:MgH.sub.2:LiBH.sub.4 of 2:1:1. It was found that the incorporation of MgH.sub.2 particles of approximately 10 nm to 20 nm exhibit a lower initial hydrogen release temperature of 150.degree. C. Furthermore, it is observed that the particle size of LiBNH quaternary hydride has a significant effect on the hydrogen sorption concentration with an optimum size of 28 nm. The as-synthesized hydrides exhibit two main hydrogen release temperatures, one around 160.degree. C. and the other around 300.degree. C., with the main hydrogen release temperature reduced from 310.degree. C. to 270.degree. C., while hydrogen is first reversibly released at temperatures as low as 150.degree. C. with a total hydrogen capacity of 6 wt. % to 8 wt. %. Detailed thermal, capacity, structural and microstructural properties have been demonstrated and correlated with the activation energies of these materials.
Inactivation of possible micromycete food contaminants using the low-temperature plasma and hydrogen peroxide

NASA Astrophysics Data System (ADS)

Čeřovský, M.; Khun, J.; Rusová, K.; Scholtz, V.; Soušková, H.

2013-09-01

The inhibition effect of hydrogen peroxide aerosol, low-temperature plasma and their combinations has been studied on several micromycetes spores. The low-temperature plasma was generated in corona discharges in the open air apparatus with hydrogen peroxide aerosol. Micromycete spores were inoculated on the surface of agar plates, exposed solely to the hydrogen peroxide aerosol, corona discharge or their combination. After incubation the diameter of inhibition zone was measured. The solely positive corona discharge exhibits no inactivation effect, the solely negative corona discharge and solely hydrogen peroxide aerosol exhibit the inactivation effect, however their combinations exhibit to be much more effective. Low-temperature plasma and hydrogen peroxide aerosol present a possible alternative method of microbial decontamination of food, food packages or other thermolabile materials.
Fast detection and low power hydrogen sensor using edge-oriented vertically aligned 3-D network of MoS2 flakes at room temperature

NASA Astrophysics Data System (ADS)

Agrawal, A. V.; Kumar, R.; Venkatesan, S.; Zakhidov, A.; Zhu, Z.; Bao, Jiming; Kumar, Mahesh; Kumar, Mukesh

2017-08-01

The increased usage of hydrogen as a next generation clean fuel strongly demands the parallel development of room temperature and low power hydrogen sensors for their safety operation. In this work, we report strong evidence for preferential hydrogen adsorption at edge-sites in an edge oriented vertically aligned 3-D network of MoS2 flakes at room temperature. The vertically aligned edge-oriented MoS2 flakes were synthesised by a modified CVD process on a SiO2/Si substrate and confirmed by Scanning Electron Microscopy. Raman spectroscopy and PL spectroscopy reveal the signature of few-layer MoS2 flakes in the sample. The sensor's performance was tested from room temperature to 150 °C for 1% hydrogen concentration. The device shows a fast response of 14.3 s even at room temperature. The sensitivity of the device strongly depends on temperature and increases from ˜1% to ˜11% as temperature increases. A detail hydrogen sensing mechanism was proposed based on the preferential hydrogen adsorption at MoS2 edge sites. The proposed gas sensing mechanism was verified by depositing ˜2-3 nm of ZnO on top of the MoS2 flakes that partially passivated the edge sites. We found a decrease in the relative response of MoS2-ZnO hybrid structures. This study provides a strong experimental evidence for the role of MoS2 edge-sites in the fast hydrogen sensing and a step closer towards room temperature, low power (0.3 mW), hydrogen sensor development.
An effective temperature compensation approach for ultrasonic hydrogen sensors

NASA Astrophysics Data System (ADS)

Tan, Xiaolong; Li, Min; Arsad, Norhana; Wen, Xiaoyan; Lu, Haifei

2018-03-01

Hydrogen is a kind of promising clean energy resource with a wide application prospect, which will, however, cause a serious security issue upon the leakage of hydrogen gas. The measurement of its concentration is of great significance. In a traditional approach of ultrasonic hydrogen sensing, a temperature drift of 0.1 °C results in a concentration error of about 250 ppm, which is intolerable for trace amount of gas sensing. In order to eliminate the influence brought by temperature drift, we propose a feasible approach named as linear compensation algorithm, which utilizes the linear relationship between the pulse count and temperature to compensate for the pulse count error (ΔN) caused by temperature drift. Experimental results demonstrate that our proposed approach is capable of improving the measurement accuracy and can easily detect sub-100 ppm of hydrogen concentration under variable temperature conditions.
DOE Office of Scientific and Technical Information (OSTI.GOV)

King, Sean W., E-mail: sean.king@intel.com; Davis, Robert F.; Carter, Richard J.

The desorption kinetics of molecular hydrogen (H{sub 2}) from silicon (001) surfaces exposed to aqueous hydrogen fluoride and remote hydrogen plasmas were examined using temperature programmed desorption. Multiple H{sub 2} desorption states were observed and attributed to surface monohydride (SiH), di/trihydride (SiH{sub 2/3}), and hydroxide (SiOH) species, subsurface hydrogen trapped at defects, and hydrogen evolved during the desorption of surface oxides. The observed surface hydride species were dependent on the surface temperature during hydrogen plasma exposure with mono, di, and trihydride species being observed after low temperature exposure (150 °C), while predominantly monohydride species were observed after higher temperature exposure (450 °C).more » The ratio of surface versus subsurface H{sub 2} desorption was also found to be dependent on the substrate temperature with 150 °C remote hydrogen plasma exposure generally leading to more H{sub 2} evolved from subsurface states and 450 °C exposure leading to more H{sub 2} desorption from surface SiH{sub x} species. Additional surface desorption states were observed, which were attributed to H{sub 2} desorption from Si (111) facets formed as a result of surface etching by the remote hydrogen plasma or aqueous hydrogen fluoride treatment. The kinetics of surface H{sub 2} desorption were found to be in excellent agreement with prior investigations of silicon surfaces exposed to thermally generated atomic hydrogen.« less
Operational characteristics of the J-PARC cryogenic hydrogen system for a spallation neutron source

DOE Office of Scientific and Technical Information (OSTI.GOV)

Tatsumoto, Hideki; Ohtsu, Kiichi; Aso, Tomokazu

2014-01-29

The J-PARC cryogenic hydrogen system provides supercritical hydrogen with the para-hydrogen concentration of more than 99 % and the temperature of less than 20 K to three moderators so as to provide cold pulsed neutron beams of a higher neutronic performance. Furthermore, the temperature fluctuation of the feed hydrogen stream is required to be within ± 0.25 K. A stable 300-kW proton beam operation has been carried out since November 2012. The para-hydrogen concentrations were measured during the cool-down process. It is confirmed that para-hydrogen always exists in the equilibrium concentration because of the installation of an ortho-para hydrogen convertor.more » Propagation characteristics of temperature fluctuation were measured by temporarily changing the heater power under off-beam condition to clarify the effects of a heater control for thermal compensation on the feed temperature fluctuation. The experimental data gave an allowable temperature fluctuation of ± 1.05 K. It is clarified through a 286-kW and a 524-kW proton beam operations that the heater control would be applicable for the 1-MW proton beam operation by extrapolating from the experimental data.« less

Integrated multi-channel nano-engineered optical hydrogen and temperature sensor detection systems for launch vehicles

NASA Astrophysics Data System (ADS)

Alam, M. Z.; Moreno, J.; Aitchison, J. S.; Mojahedi, M.; Kazemi, A. A.

2008-08-01

Launch vehicles and other satellite users need launch services that are highly reliable, less complex, easier to test, and cost effective. Being a very small molecule, hydrogen is prone to leakage through seals and micro-cracks. Hydrogen detection in space application is very challenging; public acceptance of hydrogen fuel would require the integration of a reliable hydrogen safety sensor. For detecting leakage of cryogenic fluids in spaceport facilities, launch vehicle industry and aerospace agencies are currently relying heavily on the bulky mass spectrometers, which fill one or more equipment racks, and weigh several hundred kilograms. Therefore, there is a critical need for miniaturized sensors and instruments suitable for use in space applications. This paper describes a novel multi-channel integrated nano-engineered optical sensor to detect hydrogen and monitor the temperature. The integrated optic sensor is made of multi-channel waveguide elements that measure hydrogen concentration in real Time. Our sensor is based on the use of a high index waveguide with a Ni/Pd overlay to detect hydrogen. When hydrogen is absorbed into the Ni/Pd alloy there is a change in the absorption of the material and the optical signal in the waveguide is increased. Our design uses a thin alloy (few nanometers thick) overlay which facilitates the absorption of the hydrogen and will result in a response time of approximately few seconds. Like other Pd/Pd-Ni based sensors the device response varies with temperature and hence the effects of temperature variations must be taken into account. One solution to this problem is simultaneous measurement of temperature in addition to hydrogen concentration at the same vicinity. Our approach here is to propose a temperature sensor that can easily be integrated on the same platform as the hydrogen sensor reported earlier by our group. One suitable choice of material system is silicon on insulator (SOI). Here, we propose a micro ring resonators (MRR) based temperature sensor designed on SOI that measures temperature by monitoring the output optical power.
Process for hydrogenating coal and coal solvents

DOEpatents

Tarrer, Arthur R.; Shridharani, Ketan G.

1983-01-01

A novel process is described for the hydrogenation of coal by the hydrogenation of a solvent for the coal in which the hydrogenation of the coal solvent is conducted in the presence of a solvent hydrogenation catalyst of increased activity, wherein the hydrogenation catalyst is produced by reacting ferric oxide with hydrogen sulfide at a temperature range of 260.degree. C. to 315.degree. C. in an inert atmosphere to produce an iron sulfide hydrogenation catalyst for the solvent. Optimally, the reaction temperature is 275.degree. C. Alternately, the reaction can be conducted in a hydrogen atmosphere at 350.degree. C.
Nanodiamond for hydrogen storage: temperature-dependent hydrogenation and charge-induced dehydrogenation.

PubMed

Lai, Lin; Barnard, Amanda S

2012-02-21

Carbon-based hydrogen storage materials are one of hottest research topics in materials science. Although the majority of studies focus on highly porous loosely bound systems, these systems have various limitations including use at elevated temperature. Here we propose, based on computer simulations, that diamond nanoparticles may provide a new promising high temperature candidate with a moderate storage capacity, but good potential for recyclability. The hydrogenation of nanodiamonds is found to be easily achieved, in agreement with experiments, though we find the stability of hydrogenation is dependent on the morphology of nanodiamonds and surrounding environment. Hydrogenation is thermodynamically favourable even at high temperature in pure hydrogen, ammonia, and methane gas reservoirs, whereas water vapour can help to reduce the energy barrier for desorption. The greatest challenge in using this material is the breaking of the strong covalent C-H bonds, and we have identified that the spontaneous release of atomic hydrogen may be achieved through charging of hydrogenated nanodiamonds. If the degree of induced charge is properly controlled, the integrity of the host nanodiamond is maintained, which indicates that an efficient and recyclable approach for hydrogen release may be possible. This journal is © The Royal Society of Chemistry 2012
Hydrogen Production and Delivery | Hydrogen and Fuel Cells | Hydrogen and

Science.gov Websites

degrees Celsius. Ultra-high temperatures are required for thermochemical reaction cycles to produce for the environmentally benign production of hydrogen. Very high reaction rates at these elevated temperatures give rise to very fast reaction rates, which significantly enhance production rates and more than
Protection-against-water-attack determined difference between strengths of backbone hydrogen bonds in kinesin’s neck zipper region

NASA Astrophysics Data System (ADS)

Qin, Jing-Yu; Geng, Yi-Zhao; Lü, Gang; Ji, Qing; Fang, Hai-Ping

2018-02-01

Not Available Project supported by the National Natural Science Foundation of China (Grant No. 11605038) and the Open Project Program of State Key Laboratory of Theoretical Physics, Institute of Theoretical Physics, Chinese Academy of Sciences, China (Grant No. Y5KF211CJ1).
Conceptual Launch Vehicles Using Metallic Hydrogen Propellant

NASA Astrophysics Data System (ADS)

Cole, John W.; Silvera, Isaac F.; Foote, John P.

2008-01-01

Solid molecular hydrogen is predicted to transform into an atomic solid with metallic properties under pressures >4.5 Mbar. Atomic metallic hydrogen is predicted to be metastable, limited by some critical temperature and pressure, and to store very large amounts of energy. Experiments may soon determine the critical temperature, critical pressure, and specific energy availability. It is useful to consider the feasibility of using metastable atomic hydrogen as a rocket propellant. If one assumes that metallic hydrogen is stable at usable temperatures and pressures, and that it can be affordably produced, handled, and stored, then it may be a useful rocket propellant. Assuming further that the available specific energy can be determined from the recombination of the atoms into molecules (216 MJ/kg), then conceptual engines and launch vehicle concepts can be developed. Under these assumptions, metallic hydrogen would be a revolutionary new rocket fuel with a theoretical specific impulse of 1700 s at a chamber pressure of 100 atm. A practical problem that arises is that rocket chamber temperatures may be too high for the use of this pure fuel. This paper examines an engine concept that uses liquid hydrogen or water as a diluent coolant for the metallic hydrogen to reduce the chamber temperature to usable values. Several launch vehicles are then conceptually developed. Results indicate that if metallic hydrogen is experimentally found to have the properties assumed in this analysis, then there are significant benefits. These benefits become more attractive as the chamber temperatures increase.
Non-equilibrium hydrogen ionization in 2D simulations of the solar atmosphere

NASA Astrophysics Data System (ADS)

Leenaarts, J.; Carlsson, M.; Hansteen, V.; Rutten, R. J.

2007-10-01

Context: The ionization of hydrogen in the solar chromosphere and transition region does not obey LTE or instantaneous statistical equilibrium because the timescale is long compared with important hydrodynamical timescales, especially of magneto-acoustic shocks. Since the pressure, temperature, and electron density depend sensitively on hydrogen ionization, numerical simulation of the solar atmosphere requires non-equilibrium treatment of all pertinent hydrogen transitions. The same holds for any diagnostic application employing hydrogen lines. Aims: To demonstrate the importance and to quantify the effects of non-equilibrium hydrogen ionization, both on the dynamical structure of the solar atmosphere and on hydrogen line formation, in particular Hα. Methods: We implement an algorithm to compute non-equilibrium hydrogen ionization and its coupling into the MHD equations within an existing radiation MHD code, and perform a two-dimensional simulation of the solar atmosphere from the convection zone to the corona. Results: Analysis of the simulation results and comparison to a companion simulation assuming LTE shows that: a) non-equilibrium computation delivers much smaller variations of the chromospheric hydrogen ionization than for LTE. The ionization is smaller within shocks but subsequently remains high in the cool intershock phases. As a result, the chromospheric temperature variations are much larger than for LTE because in non-equilibrium, hydrogen ionization is a less effective internal energy buffer. The actual shock temperatures are therefore higher and the intershock temperatures lower. b) The chromospheric populations of the hydrogen n = 2 level, which governs the opacity of Hα, are coupled to the ion populations. They are set by the high temperature in shocks and subsequently remain high in the cool intershock phases. c) The temperature structure and the hydrogen level populations differ much between the chromosphere above photospheric magnetic elements and above quiet internetwork. d) The hydrogen n = 2 population and column density are persistently high in dynamic fibrils, suggesting that these obtain their visibility from being optically thick in Hα also at low temperature. Movie and Appendix A are only available in electronic form at http://www.aanda.org
Synthesis of hydrogen-carbon clathrate material and hydrogen evolution therefrom at moderate temperatures and pressures

DOEpatents

Lueking, Angela [State College, PA; Narayanan, Deepa [Redmond, WA

2011-03-08

A process for making a hydrogenated carbon material is provided which includes forming a mixture of a carbon source, particularly a carbonaceous material, and a hydrogen source. The mixture is reacted under reaction conditions such that hydrogen is generated and/or released from the hydrogen source, an amorphous diamond-like carbon is formed, and at least a portion of the generated and/or released hydrogen associates with the amorphous diamond-like carbon, thereby forming a hydrogenated carbon material. A hydrogenated carbon material including a hydrogen carbon clathrate is characterized by evolution of molecular hydrogen at room temperature at atmospheric pressure in particular embodiments of methods and compositions according to the present invention.
Gas-controlled dynamic vacuum insulation with gas gate

DOEpatents

Benson, David K.; Potter, Thomas F.

1994-06-07

Disclosed is a dynamic vacuum insulation comprising sidewalls enclosing an evacuated chamber and gas control means for releasing hydrogen gas into a chamber to increase gas molecule conduction of heat across the chamber and retrieving hydrogen gas from the chamber. The gas control means includes a metal hydride that absorbs and retains hydrogen gas at cooler temperatures and releases hydrogen gas at hotter temperatures; a hydride heating means for selectively heating the metal hydride to temperatures high enough to release hydrogen gas from the metal hydride; and gate means positioned between the metal hydride and the chamber for selectively allowing hydrogen to flow or not to flow between said metal hydride and said chamber.
Gas-controlled dynamic vacuum insulation with gas gate

DOEpatents

Benson, D.K.; Potter, T.F.

1994-06-07

Disclosed is a dynamic vacuum insulation comprising sidewalls enclosing an evacuated chamber and gas control means for releasing hydrogen gas into a chamber to increase gas molecule conduction of heat across the chamber and retrieving hydrogen gas from the chamber. The gas control means includes a metal hydride that absorbs and retains hydrogen gas at cooler temperatures and releases hydrogen gas at hotter temperatures; a hydride heating means for selectively heating the metal hydride to temperatures high enough to release hydrogen gas from the metal hydride; and gate means positioned between the metal hydride and the chamber for selectively allowing hydrogen to flow or not to flow between said metal hydride and said chamber. 25 figs.
Equilibrium and diffusion studies of metal-hydrogen systems

NASA Astrophysics Data System (ADS)

Maroevic, Petar

Several new methods and models have been developed pertaining to equilibrium properties of hydrogen in random binary substitutional alloys at room and lower temperatures, describing both statistics and kinetics of hydrogen in them. They represent a solution to the problem of the complete Fermi-Dirac description which is physically appropriate for these systems. Hydrogen diffusion which proceeds via lattice assisted quantum tunneling at room and lower temperatures requires a new and different description from the one based on the thermal hopping picture, which pertains only to relatively high temperatures. It is also shown that the analogs of the solution to the Fermi-Dirac problem of hydrogen can be successfully applied to the description of vacancies in a hydrogenated system, a phenomena known to occur due to high hydrogen-vacancy binding energies and the creation of hydrogen-vacancy clusters. The solution based on this model applies to much lower temperatures and higher concentrations than the tradition alone. This methodology has also been applied to the surface problem where very large vacancy and hydrogen concentrations occur. This is of special importance since mechanical properties are known to be greatly affected by the surface. As another consequence of hydrogen induced vacancies, hydrogen induced lattice migration (HILM) occurs. This has been demonstrated in our electrical resistivity study of palladium wires where recrystallization and annealing effects were observed upon hydrogen-heat-treatment (HHT).
Low temperature synthesis of hexagonal ZnO nanorods and their hydrogen sensing properties

NASA Astrophysics Data System (ADS)

Qurashi, Ahsanulhaq; Faiz, M.; Tabet, N.; Alam, Mir Waqas

2011-08-01

The growth of hexagonal ZnO nanorods was demonstrated by low temperature chemical synthesis approach. X-ray diffraction (XRD) analysis revealed a wurtzite hexagonal structure of the ZnO nanorods. The optical properties were measured by UV-vis spectrophotometer at room temperature. X-ray photoelectron spectroscopy (XPS) confirmed high purity of the ZnO nanorods. The hydrogen sensor made of the ZnO nanorods showed reversible response. The hydrogen gas tests were carried out in presence of ambient air and the influence of operation temperature on the hydrogen gas sensing property of ZnO nanorods was also investigated.
Stable catalyst layers for hydrogen permeable composite membranes

DOEpatents

Way, J. Douglas; Wolden, Colin A

2014-01-07

The present invention provides a hydrogen separation membrane based on nanoporous, composite metal carbide or metal sulfide coated membranes capable of high flux and permselectivity for hydrogen without platinum group metals. The present invention is capable of being operated over a broad temperature range, including at elevated temperatures, while maintaining hydrogen selectivity.
Adsorption and Desorption of Hydrogen by Gas-Phase Palladium Clusters Revealed by In Situ Thermal Desorption Spectroscopy.

PubMed

Takenouchi, Masato; Kudoh, Satoshi; Miyajima, Ken; Mafuné, Fumitaka

2015-07-02

Adsorption and desorption of hydrogen by gas-phase Pd clusters, Pdn(+), were investigated by thermal desorption spectroscopy (TDS) experiments and density functional theory (DFT) calculations. The desorption processes were examined by heating the clusters that had adsorbed hydrogen at room temperature. The clusters remaining after heating were monitored by mass spectrometry as a function of temperature up to 1000 K, and the temperature-programmed desorption (TPD) curve was obtained for each Pdn(+). It was found that hydrogen molecules were released from the clusters into the gas phase with increasing temperature until bare Pdn(+) was formed. The threshold energy for desorption, estimated from the TPD curve, was compared to the desorption energy calculated by using DFT, indicating that smaller Pdn(+) clusters (n ≤ 6) tended to have weakly adsorbed hydrogen molecules, whereas larger Pdn(+) clusters (n ≥ 7) had dissociatively adsorbed hydrogen atoms on the surface. Highly likely, the nonmetallic nature of the small Pd clusters prevents hydrogen molecule from adsorbing dissociatively on the surface.
Experience with flexible pipe in sour service environment: A case study (the Arabian Gulf)

DOE Office of Scientific and Technical Information (OSTI.GOV)

Al-Maslamani, M.J.

The suitability of a flexible pipe was evaluated on a trial basis for a lift gas line in a sour oil field in the State of Qatar, in the Arabian Gulf. Flexible pipes have been successfully used in the oil and gas industries for transportation of methanol, benzene and gas condensates in wet sweet environment at temperatures of up to 80 C. However, there is little or no information available as to its corrosion resistance in sour service wells containing 6% CO{sub 2} with 3% mole H{sub 2}S and at moderate temperatures. The present experience with a flexible pipe inmore » the gas field of Qatar has shown that under sour service conditions, the layered, composite material can suffer severe degradation leading to failure. A detailed inspection and failure analysis of the flexible pipe forms the basis of this paper. The failure demonstrates the significant effects of stress level, environmental aggressiveness, and localized hard zones in promoting Sulfide Stress Cracking (SSC). Permeability of this sour gas through the composite layer of the flexible pipe resulted in varying degree of sulfide attack and hydrogen embrittlement depending on the susceptibility of the multi layered material.« less
Effects of reducing temperatures on the hydrogen storage capacity of double-walled carbon nanotubes with Pd loading.

PubMed

Sheng, Qu; Wu, Huimin; Wexler, David; Liu, Huakun

2014-06-01

The effects of different temperatures on the hydrogen sorption characteristics of double-walled carbon nanotubes (DWCNTs) with palladium loading have been investigated. When we use different temperatures, the particle sizes and specific surface areas of the samples are different, which affects the hydrogen storage capacity of the DWCNTs. In this work, the amount of hydrogen storage capacity was determined (by AMC Gas Reactor Controller) to be 1.70, 1.85, 2.00, and 1.93 wt% for pristine DWCNTS and for 2%Pd/DWCNTs-300 degrees C, 2%Pd/DWCNTs-400 degrees C, and 2%Pd/DWCNTs-500 degrees C, respectively. We found that the hydrogen storage capacity can be enhanced by loading with 2% Pd nanoparticles and selecting a suitable temperature. Furthermore, the sorption can be attributed to the chemical reaction between atomic hydrogen and the dangling bonds of the DWCNTs.
Analysis of Material Sample Heated by Impinging Hot Hydrogen Jet in a Non-Nuclear Tester

NASA Technical Reports Server (NTRS)

Wang, Ten-See; Foote, John; Litchford, Ron

2006-01-01

A computational conjugate heat transfer methodology was developed and anchored with data obtained from a hot-hydrogen jet heated, non-nuclear materials tester, as a first step towards developing an efficient and accurate multiphysics, thermo-fluid computational methodology to predict environments for hypothetical solid-core, nuclear thermal engine thrust chamber. The computational methodology is based on a multidimensional, finite-volume, turbulent, chemically reacting, thermally radiating, unstructured-grid, and pressure-based formulation. The multiphysics invoked in this study include hydrogen dissociation kinetics and thermodynamics, turbulent flow, convective and thermal radiative, and conjugate heat transfers. Predicted hot hydrogen jet and material surface temperatures were compared with those of measurement. Predicted solid temperatures were compared with those obtained with a standard heat transfer code. The interrogation of physics revealed that reactions of hydrogen dissociation and recombination are highly correlated with local temperature and are necessary for accurate prediction of the hot-hydrogen jet temperature.
High-temperature effect of hydrogen on sintered alpha-silicon carbide

NASA Technical Reports Server (NTRS)

Hallum, G. W.; Herbell, T. P.

1986-01-01

Sintered alpha-silicon carbide was exposed to pure, dry hydrogen at high temperatures for times up to 500 hr. Weight loss and corrosion were seen after 50 hr at temperatures as low as 1000 C. Corrosion of SiC by hydrogen produced grain boundary deterioration at 1100 C and a mixture of grain and grain boundary deterioration at 1300 C. Statistically significant strength reductions were seen in samples exposed to hydrogen for times greater than 50 hr and temperatures above 1100 C. Critical fracture origins were identified by fractography as either general grain boundary corrision at 1100 C or as corrosion pits at 1300 C. A maximum strength decrease of approximately 33 percent was seen at 1100 and 1300 C after 500 hr exposure to hydrogen. A computer assisted thermodynamic program was also used to predict possible reaction species of SiC and hydrogen.
Effect of high-temperature hydrogen exposure on sintered alpha-SiC

NASA Technical Reports Server (NTRS)

Hallum, Gary W.; Herbell, Thomas P.

1988-01-01

Sintered alpha-silicon carbide was exposed to pure, dry hydrogen at high temperatures for times up to 500 hr. Weight loss and corrosion were seen after 50 hr at temperatures as low as 1000 C. Corrosion of SiC by hydrogen produced grain boundary deterioration at 1100 C and a mixture of grain and grain boundary deterioration at 1300 C. Statistically significant strength reductions were seen in samples exposed to hydrogen for times greater than 50 hr and temperatures above 1100 C. Critical fracture origins were identified by fractography as either general grain boundary corrosion at 1100 C or as corrosion pits at 1300 C. A maximum strength decrease of approximately 33 percent was seen at 1100 and 1300 C after 500 hr exposure to hydrogen. A computer assisted thermodynamic program was also used to predict possible reaction species of SiC and hydrogen.
On the nature of low temperature internal friction peaks in metallic glasses

DOE Office of Scientific and Technical Information (OSTI.GOV)

Khonik, V.A.; Spivak, L.V.

Low temperature (30 < T < 300 K) internal friction in a metallic glass Ni{sub 60}Nb{sub 40} subjected to preliminary inhomogeneous deformation by cold rolling, homogeneous tensile deformation or electrolytic charging with hydrogen is investigated. Cold rolling or hydrogenation result in appearance of similar internal friction peaks and hysteresis damping. Homogeneous deformation has no influence on low temperature internal friction. The phenomenon of microplastic deformation during hydrogenation of weakly stressed samples is revealed. It is argued that microplastic deformation of metallic glasses during hydrogenation without external stress takes place too. Plastic flow both on cold rolling and hydrogenation occurs viamore » formation and motion of dislocation-like defects which are the reason of the observed anelastic anomalies. It is concluded that low temperature internal friction peaks described in the literature for as-cast, cold deformed and hydrogenated samples have common dislocation-like origin.« less

Seasonal Terpene Variation in Needles of Pinus radiata (Pinales: Pinaceae) Trees Attacked by Tomicus piniperda (Coleoptera: Scolytinae) and the Effect of Limonene on Beetle Aggregation

PubMed Central

Romón, Pedro; Aparicio, Domitila; Palacios, Francisco; Iturrondobeitia, Juan Carlos; Hance, Thierry

2017-01-01

Abstract Concentrations of four monoterpenes were determined in needles of Pinus radiata (D.Don) (Pinales: Pinaceae) trees that were attacked or nonattacked by Tomicus piniperda (L.) (Coleoptera: Scolytinae). Compounds were identified and quantified by gas chromatography–mass spectrometry. The mean ambient temperature was obtained using climate-recording data loggers. The effect of limonene on field aggregation was also evaluated at three limonene release rates using Lindgren attractant-baited traps and trap logs. Attacked trees produced less α-pinene in March, July, and November than nonattacked trees, less β-pinene in July and November, and less limonene from May to November. Limonene reduced the attraction of T. piniperda to attractant-baited traps and trap logs. Results were linked to better responses to high temperatures, with respect to terpene contents, by the nonattacked trees after the spring attack. PMID:29117373
Thermodynamics and Transport Phenomena in High Temperature Steam Electrolysis Cells

DOE Office of Scientific and Technical Information (OSTI.GOV)

James E. O'Brien

2012-03-01

Hydrogen can be produced from water splitting with relatively high efficiency using high temperature electrolysis. This technology makes use of solid-oxide cells, running in the electrolysis mode to produce hydrogen from steam, while consuming electricity and high temperature process heat. The overall thermal-to-hydrogen efficiency for high temperature electrolysis can be as high as 50%, which is about double the overall efficiency of conventional low-temperature electrolysis. Current large-scale hydrogen production is based almost exclusively on steam reforming of methane, a method that consumes a precious fossil fuel while emitting carbon dioxide to the atmosphere. An overview of high temperature electrolysis technologymore » will be presented, including basic thermodynamics, experimental methods, heat and mass transfer phenomena, and computational fluid dynamics modeling.« less
Gas-phase Reactivity of meta-Benzyne Analogs Toward Small Oligonucleotides of Differing Lengths

NASA Astrophysics Data System (ADS)

Widjaja, Fanny; Max, Joann P.; Jin, Zhicheng; Nash, John J.; Kenttämaa, Hilkka I.

2017-07-01

The gas-phase reactivity of two aromatic carbon-centered σ,σ-biradicals ( meta-benzyne analogs) and a related monoradical towards small oligonucleotides of differing lengths was investigated in a Fourier-transform ion cyclotron resonance (FT-ICR) mass spectrometer coupled with laser-induced acoustic desorption (LIAD). The mono- and biradicals were positively charged to allow for manipulation in the mass spectrometer. The oligonucleotides were evaporated into the gas phase as intact neutral molecules by using LIAD. One of the biradicals was found to be unreactive. The reactive biradical reacts with dinucleoside phosphates and trinucleoside diphosphates mainly by addition to a nucleobase moiety followed by cleavage of the glycosidic bond, leading to a nucleobase radical (e.g., base-H) abstraction. In some instances, after the initial cleavage, the unquenched radical site of the biradical abstracts a hydrogen atom from the neutral fragment, which results in a net nucleobase abstraction. In sharp contrast, the related monoradical mainly undergoes facile hydrogen atom abstraction from the sugar moiety. As the size of the oligonucleotides increases, the rate of hydrogen atom abstraction from the sugar moiety by the monoradical was found to increase due to the presence of more hydrogen atom donor sites, and it is the only reaction observed for tetranucleoside triphosphates. Hence, the monoradical only attacks sugar moieties in these substrates. The biradical also shows significant attack at the sugar moiety for tetranucleoside triphosphates. This drastic change in reactivity indicates that the size of the oligonucleotides plays a key role in the outcome of these reactions. This finding is attributed to more compact conformations in the gas phase for the tetranucleoside triphosphates than for the smaller oligonucleotides, which result from stronger stabilizing interactions between the nucleobases.
Hydrogen-atmosphere induction furnace has increased temperature range

NASA Technical Reports Server (NTRS)

Caves, R. M.; Gresslin, C. H.

1966-01-01

Improved hydrogen-atmosphere induction furnace operates at temperatures up to 5,350 deg F. The furnace heats up from room temperature to 4,750 deg F in 30 seconds and cools down to room temperature in 2 minutes.
Mixture including hydrogen and hydrocarbon having pressure-temperature stability

NASA Technical Reports Server (NTRS)

Mao, Wendy L. (Inventor); Mao, Ho-Kwang (Inventor)

2009-01-01

The invention relates to a method of storing hydrogen that employs a mixture of hydrogen and a hydrocarbon that can both be used as fuel. In one embodiment, the method involves maintaining a mixture including hydrogen and a hydrocarbon in the solid state at ambient pressure and a temperature in excess of about 10 K.
Mixture including hydrogen and hydrocarbon having pressure-temperature stability

DOEpatents

Mao, Wendy L [Washington, DC; Mao, Ho-Kwang [Washington, DC

2009-08-18

The invention relates to a method of storing hydrogen that employs a mixture of hydrogen and a hydrocarbon that can both be used as fuel. In one embodiment, the method involves maintaining a mixture including hydrogen and a hydrocarbon in the solid state at ambient pressure and a temperature in excess of about 10 K.
Exospheric hydrogen above St-Santin /France/

NASA Technical Reports Server (NTRS)

Derieux, A.; Lejeune, G.; Bauer, P.

1975-01-01

The temperature and hydrogen concentration of the exosphere was determined using incoherent scatter measurements performed above St. Santin from 1969 to 1972. The hydrogen concentration was deduced from measurements of the number density of positive hydrogen and oxygen ions. A statistical analysis is given of the hydrogen concentration as a function of the exospheric temperature and the diurnal variation of the hydrogen concentration is investigated for a few selected days of good quality observation. The data averaged with respect to the exospheric temperature without consideration of the local time exhibits a distribution consistent with a constant effective Jeans escape flux of about 9 x 10 to the 7 cu cm/s. The local time variation exhibits a maximum to minimum concentration ratio of at least 3.5.
Method for determining hydrogen mobility as a function of temperature in superconducting niobium cavities

DOEpatents

May, Robert [Virginia Beach, VA

2008-03-11

A method for determining the mobility of hydrogen as a function of temperature in superconducting niobium cavities comprising: 1) heating a cavity under test to remove free hydrogen; 2) introducing hydrogen-3 gas into the cavity; 3) cooling the cavity to allow absorption of hydrogen-3; and 4) measuring the amount of hydrogen-3 by: a) cooling the cavity to about 4.degree. K while flowing a known and regulated amount of inert carrier gas such as argon or helium into the cavity; b) allowing the cavity to warm at a stable rate from 4.degree. K to room temperature as it leaves the chamber; and c) directing the exit gas to an ion chamber radiation detector.
Hydrogen Permeability of Incoloy 800H, Inconel 617, and Haynes 230 Alloys

DOE Office of Scientific and Technical Information (OSTI.GOV)

Pattrick Calderoni

A potential issue in the design of the NGNP reactor and high-temperature components is the permeation of fission generated tritium and hydrogen product from downstream hydrogen generation through high-temperature components. Such permeation can result in the loss of fission-generated tritium to the environment and the potential contamination of the helium coolant by permeation of product hydrogen into the coolant system. The issue will be addressed in the engineering design phase, and requires knowledge of permeation characteristics of the candidate alloys. Of three potential candidates for high-temperature components of the NGNP reactor design, the hydrogen permeability has been documented well onlymore » for Incoloy 800H, but at relatively high partial pressures of hydrogen. Hydrogen permeability data have been published for Inconel 617, but only in two literature reports and for partial pressures of hydrogen greater than one atmosphere, far higher than anticipated in the NGNP reactor. The hydrogen permeability of Haynes 230 has not been published. To support engineering design of the NGNP reactor components, the hydrogen permeability of Inconel 617 and Haynes 230 were determined using a measurement system designed and fabricated at the Idaho National Laboratory. The performance of the system was validated using Incoloy 800H as reference material, for which the permeability has been published in several journal articles. The permeability of Incoloy 800H, Inconel 617 and Haynes 230 was measured in the temperature range 650 to 950 °C and at hydrogen partial pressures of 10-3 and 10-2 atm, substantially lower pressures than used in the published reports. The measured hydrogen permeability of Incoloy 800H and Inconel 617 were in good agreement with published values obtained at higher partial pressures of hydrogen. The hydrogen permeability of Inconel 617 and Haynes 230 were similar, about 50% greater than for Incoloy 800H and with similar temperature dependence.« less
Fundamental Pathways for the Adsorption and Transport of Hydrogen on TiO2 Surfaces: Origin for Effective Sensing at about Room Temperature.

PubMed

Wang, Zhuo; Xia, Xiaohong; Guo, Meilan; Shao, Guosheng

2016-12-28

Effective detection of hydrogen at lowered temperature is highly desirable in promoting safety in using this abundant gas as a clean energy source. Through first-principle calculations in the framework of density functional theory, we find that the high-energy (002) surface for rutile TiO 2 is significantly more effective in adsorbing hydrogen atoms through dissociating hydrogen molecules. The pathways for the dissociation of hydrogen molecules and sequential migration of hydrogen atoms are identified through searching along various transitional states. Pathways of low potential barriers indicate promise for hydrogen sensing, even close to room temperature. This has been proven through sensors made of thin films of well-aligned rutile nanorods, wherein the high-energy (002) surface dictates the top surface of the active layer of the sensors.
Bacterial extracellular lignin peroxidase

DOEpatents

Crawford, Donald L.; Ramachandra, Muralidhara

1993-01-01

A newly discovered lignin peroxidase enzyme is provided. The enzyme is obtained from a bacterial source and is capable of degrading the lignin portion of lignocellulose in the presence of hydrogen peroxide. The enzyme is extracellular, oxidative, inducible by lignin, larch wood xylan, or related substrates and capable of attacking certain lignin substructure chemical bonds that are not degradable by fungal lignin peroxidases.
Selective C-O Hydrogenolysis and Decarboxylation of Biomass-Derived Heterocyclic Compounds over Heterogeneous Catalysts

NASA Astrophysics Data System (ADS)

Chia, Mei

The catalytic deoxygenation of biomass-derived compounds through selective C-O hydrogenolysis, catalytic transfer hydrogenation and lactonization, and decarboxylation to value-added chemicals over heterogeneous catalysts was examined under liquid phase reaction conditions. The reactions studied involve the conversion or production of heterocyclic compounds, specifically, cyclic ethers, lactones, and 2-pyrones. A bimetallic RhRe/C catalyst was found to be selective for the hydrogenolysis of secondary C-O bonds for a broad range cyclic ethers and polyols. Results from experimentally-observed reactivity trends, NH3 temperature-programmed desorption, fructose dehydration reaction studies, and first-principles density functional theory (DFT) calculations are consistent with the hypothesis of a bifunctional catalyst which facilitates acid-catalyzed ring-opening and dehydration coupled with metal-catalyzed hydrogenation. C-O hydrogenolysis and fructose dehydration activities were observed to decrease with an increase in reduction temperature and a decrease in the number of surface metallic Re atoms measured by in situ X-ray absorption spectroscopy. No C-O hydrogenolysis activity was detected over RhRe/C under water-free conditions. The activation of water molecules by Re atoms on the surface of metallic Rh is suggested to result in the formation of Bronsted acidity over RhRe/C. The catalytic transfer hydrogenation and lactonization of levulinic acid and its esters to gamma-valerolactone was accomplished through the Meerwein-Ponndorf-Verley reaction over metal oxide catalysts using secondary alcohols as the hydrogen donor. ZrO2 was a highly active material for CTH under batch and continuous flow reaction conditions; the initial activity of the catalyst was repeatedly regenerable by calcination in air, with no observable loss in catalytic activity. Lastly, the 2-pyrone, triacetic acid lactone, is shown to be a promising biorenewable platform chemical from which a wide range of chemical intermediates and end products can be obtained using heterogeneous catalysts or by thermal decomposition. Mechanistic insights from experimentally-observed reactivity trends and results from DFT calculations indicate that 2-pyrones undergo reactions unique to their structure such as keto-enol tautomerization, retro Diels-Alder, and nucleophilic attack by water. Ring-opening and decarboxylation reactions were found to be governed by key structural features such as the degree of saturation in the ring (e.g., C4=C5 bond), nature of the solvent, and presence of an acid catalyst.
Coolant-side heat-transfer rates for a hydrogen-oxygen rocket and a new technique for data correlation

NASA Technical Reports Server (NTRS)

Schacht, R. L.; Quentmeyer, R. J.

1973-01-01

An experimental investigation was conducted to determine the coolant-side, heat transfer coefficients for a liquid cooled, hydrogen-oxygen rocket thrust chamber. Heat transfer rates were determined from measurements of local hot gas wall temperature, local coolant temperature, and local coolant pressure. A correlation incorporating an integration technique for the transport properties needed near the pseudocritical temperature of liquid hydrogen gives a satisfactory prediction of hot gas wall temperatures.
Hydrogenation and hydrogen intercalation of hexagonal boron nitride on Ni(1 1 1): reactivity and electronic structure

NASA Astrophysics Data System (ADS)

Späth, F.; Gebhardt, J.; Düll, F.; Bauer, U.; Bachmann, P.; Gleichweit, C.; Görling, A.; Steinrück, H.-P.; Papp, C.

2017-09-01

We investigate the reactivity of hexagonal boron nitride (h-BN) on a Ni(1 1 1) single crystal towards atomic hydrogen over a wide exposure range. Near edge x-ray absorption fine structure and x-ray photoelectron spectroscopy (XPS) show that for low hydrogen exposures hydrogenation of the h-BN sheet is found. In contrast, intercalation of hydrogen between h-BN and the Ni(1 1 1) substrate occurs for high exposures. For intermediate regimes, a mixture of intercalation and hydrogenation is observed. From temperature-programmed desorption and temperature-programmed XPS experiments, we conclude that the hydrogen covalently bound to h-BN is rather stable with a desorption temperature of 600 K, while intercalated hydrogen is desorbing already at 390 K. Further insight into the structural arrangements and the thermodynamics of the system is obtained by comparing our experimental results with extensive density-functional theory calculations. Together with ultraviolet photoelectron spectroscopy measurements, the calculations provide detailed insight into the influence of hydrogenation on the electronic structure of h-BN.
Design of hydrogen vent line for the cryogenic hydrogen system in J-PARC

NASA Astrophysics Data System (ADS)

Tatsumoto, Hideki; Aso, Tomokazu; Kato, Takashi; Ohtsu, Kiichi; Hasegawa, Shoichi; Maekawa, Fujio; Futakawa, Masatoshi

2009-02-01

As one of the main experimental facilities in J-PARC, an intense spallation neutron source (JSNS) driven by a 1-MW proton beam selected supercritical hydrogen at a temperature of 20 K and a pressure of 1.5 MPa as a moderator material. Moderators are controlled by a cryogenic hydrogen system that has a hydrogen relief system, which consists of high and low pressure stage of manifolds, a hydrogen vent line and a stack, in order to release hydrogen to the outside safely. The design of the hydrogen vent line should be considered to prevent purge nitrogen gas in the vent line from freezing when releasing the cryogenic hydrogen, to prevent moisture in the stack placed in an outdoor location from freezing, and to inhibit large piping temperature reduction at a building wall penetration. In this work, temperature change behaviors in the hydrogen vent line were analyzed by using a CFD code, STAR-CD. We determined required sizes of the vent line based on the analytical results and its layout in the building.
Anisotropic Azimuthal Power and Temperature distribution on FuelRod. Impact on Hydride Distribution

DOE Office of Scientific and Technical Information (OSTI.GOV)

Motta, Arthur; Ivanov, Kostadin; Arramova, Maria

2015-04-29

The degradation of the zirconium cladding may limit nuclear fuel performance. In the high temperature environment of a reactor, the zirconium in the cladding corrodes, releasing hydrogen in the process. Some of this hydrogen is absorbed by the cladding in a highly inhomogeneous manner. The distribution of the absorbed hydrogen is extremely sensitive to temperature and stress concentration gradients. The absorbed hydrogen tends to concentrate near lower temperatures. This hydrogen absorption and hydride formation can cause cladding failure. This project set out to improve the hydrogen distribution prediction capabilities of the BISON fuel performance code. The project was split intomore » two primary sections, first was the use of a high fidelity multi-physics coupling to accurately predict temperature gradients as a function of r, θ , and z, and the second was to use experimental data to create an analytical hydrogen precipitation model. The Penn State version of thermal hydraulics code COBRA-TF (CTF) was successfully coupled to the DeCART neutronics code. This coupled system was verified by testing and validated by comparison to FRAPCON data. The hydrogen diffusion and precipitation experiments successfully calculated the heat of transport and precipitation rate constant values to be used within the hydrogen model in BISON. These values can only be determined experimentally. These values were successfully implemented in precipitation, diffusion and dissolution kernels that were implemented in the BISON code. The coupled output was fed into BISON models and the hydrogen and hydride distributions behaved as expected. Simulations were conducted in the radial, axial and azimuthal directions to showcase the full capabilities of the hydrogen model.« less
Ignition and flame characteristics of cryogenic hydrogen releases

DOE PAGES

Panda, Pratikash P.; Hecht, Ethan S.

2017-01-01

In this work, under-expanded cryogenic hydrogen jets were investigated experimentally for their ignition and flame characteristics. The test facility described herein, was designed and constructed to release hydrogen at a constant temperature and pressure, to study the dispersion and thermo-physical properties of cryogenic hydrogen releases and flames. In this study, a non-intrusive laser spark focused on the jet axis was used to measure the maximum ignition distance. The radiative power emitted by the corresponding jet flames was also measured for a range of release scenarios from 37 K to 295 K, 2–6 bar abs through nozzles with diameters from 0.75more » to 1.25 mm. The maximum ignition distance scales linearly with the effective jet diameter (which scales as the square root of the stagnant fluid density). A 1-dimensional (stream-wise) cryogenic hydrogen release model developed previously at Sandia National Laboratories (although this model is not yet validated for cryogenic hydrogen) was exercised to predict that the mean mole fraction at the maximum ignition distance is approximately 0.14, and is not dependent on the release conditions. The flame length and width were extracted from visible and infra-red flame images for several test cases. The flame length and width both scale as the square root of jet exit Reynolds number, as reported in the literature for flames from atmospheric temperature hydrogen. As shown in previous studies for ignited atmospheric temperature hydrogen, the radiative power from the jet flames of cold hydrogen scales as a logarithmic function of the global flame residence time. The radiative heat flux from jet flames of cold hydrogen is higher than the jet flames of atmospheric temperature hydrogen, for a given mass flow rate, due to the lower choked flow velocity of low-temperature hydrogen. Lastly, this study provides critical information with regard to the development of models to inform the safety codes and standards of hydrogen infrastructure.« less
Self-absorption characteristics of measured laser-induced plasma line shapes

NASA Astrophysics Data System (ADS)

Parigger, C. G.; Surmick, D. M.; Gautam, G.

2017-02-01

The determination of electron density and temperature is reported from line-of-sight measurements of laser-induced plasma. Experiments are conducted in standard ambient temperature and pressure air and in a cell containing ultra-high-pure hydrogen slightly above atmospheric pressure. Spectra of the hydrogen Balmer series lines can be measured in laboratory air due to residual moisture following optical breakdown generated with 13 to 14 nanosecond, pulsed Nd:YAG laser radiation. Comparisons with spectra obtained in hydrogen gas yields Abel-inverted line shape appearances that indicate occurrence of self-absorption. The electron density and temperature distributions along the line of sight show near-spherical rings, expanding at or near the speed of sound in the hydrogen gas experiments. The temperatures in the hydrogen studies are obtained using Balmer series alpha, beta, gamma profiles. Over and above the application of empirical formulae to derive the electron density from hydrogen alpha width and shift, and from hydrogen beta width and peak-separation, so-called escape factors and the use of a doubling mirror are discussed.
Evaluation of electrolytic tilt sensors for measuring model angle of attack in wind tunnel tests

NASA Technical Reports Server (NTRS)

Wong, Douglas T.

1992-01-01

The results of a laboratory evaluation of electrolytic tilt sensors as potential candidates for measuring model attitude or angle of attack in wind tunnel tests are presented. The performance of eight electrolytic tilt sensors was compared with that of typical servo accelerometers used for angle-of-attack measurements. The areas evaluated included linearity, hysteresis, repeatability, temperature characteristics, roll-on-pitch interaction, sensitivity to lead-wire resistance, step response time, and rectification. Among the sensors being evaluated, the Spectron model RG-37 electrolytic tilt sensors have the highest overall accuracy in terms of linearity, hysteresis, repeatability, temperature sensitivity, and roll sensitivity. A comparison of the sensors with the servo accelerometers revealed that the accuracy of the RG-37 sensors was on the average about one order of magnitude worse. Even though a comparison indicates that the cost of each tilt sensor is about one-third the cost of each servo accelerometer, the sensors are considered unsuitable for angle-of-attack measurements. However, the potential exists for other applications such as wind tunnel wall-attitude measurements where the errors resulting from roll interaction, vibration, and response time are less and sensor temperature can be controlled.
Stability of a non-orthogonal stagnation flow to three dimensional disturbances

NASA Technical Reports Server (NTRS)

Lasseigne, D. G.; Jackson, T. L.

1991-01-01

A similarity solution for a low Mach number nonorthogonal flow impinging on a hot or cold plate is presented. For the constant density case, it is known that the stagnation point shifts in the direction of the incoming flow and that this shift increases as the angle of attack decreases. When the effects of density variations are included, a critical plate temperature exists; above this temperature the stagnation point shifts away from the incoming stream as the angle is decreased. This flow field is believed to have application to the reattachment zone of certain separated flows or to a lifting body at a high angle of attack. Finally, the stability of this nonorthogonal flow to self similar, 3-D disturbances is examined. Stability properties of the flow are given as a function of the parameters of this study; ratio of the plate temperature to that of the outer potential flow and angle of attack. In particular, it is shown that the angle of attack can be scaled out by a suitable definition of an equivalent wavenumber and temporal growth rate, and the stability problem for the nonorthogonal case is identical to the stability problem for the orthogonal case.

Inactivation of possible micromycete food contaminants using the low-temperature plasma and hydrogen peroxide

DOE Office of Scientific and Technical Information (OSTI.GOV)

Čeřovský, M., E-mail: scholtz@aldebaran.cz; Khun, J.; Rusová, K.

2013-09-15

The inhibition effect of hydrogen peroxide aerosol, low-temperature plasma and their combinations has been studied on several micromycetes spores. The low-temperature plasma was generated in corona discharges in the open air apparatus with hydrogen peroxide aerosol. Micromycete spores were inoculated on the surface of agar plates, exposed solely to the hydrogen peroxide aerosol, corona discharge or their combination. After incubation the diameter of inhibition zone was measured. The solely positive corona discharge exhibits no inactivation effect, the solely negative corona discharge and solely hydrogen peroxide aerosol exhibit the inactivation effect, however their combinations exhibit to be much more effective. Low-temperaturemore » plasma and hydrogen peroxide aerosol present a possible alternative method of microbial decontamination of food, food packages or other thermolabile materials.« less
Electrical properties of lanthanum chromite based ceramics in hydrogen and oxidizing atmospheres at high temperatures

NASA Astrophysics Data System (ADS)

Schmidt, V. H.

1981-06-01

Several results regarding the effect of hydrogen on lanthanum chromite were determined. Thermally-activated diffusion of hydrogen through La(Mg)CrO3 was found with a high activation energy. It was found that its electrical conductivity drops drastically, especially at low temperature, after exposure to hydrogen at high temperature. Also, the curvature of most of the conductivity plots, as well as the inability to observe the Hall effect, lends support to the proposal by Karim and Aldred that the small-polaron model which predicts thermally activated mobility is applicable to doped lanthanum chromite. From differential thermal analysis, an apparent absorption of hydrogen near 3000 C was noticed. Upon cooling the lanthanum chromite in hydrogen and subsequently reheating it in air, desorption occurred near 1700 C. The immediate purpose of this study was to determine whether hydrogen has a deleterious effect on lanthanum chromite in solid oxide fuel cells.
Oxidation resistant organic hydrogen getters

DOEpatents

Shepodd, Timothy J [Livermore, CA; Buffleben, George M [Tracy, CA

2008-09-09

A composition for removing hydrogen from an atmosphere, comprising a mixture of a polyphenyl ether and a hydrogenation catalyst, preferably a precious metal catalyst, and most preferably Pt. This composition is stable in the presence of oxygen, will not polymerize or degrade upon exposure to temperatures in excess of 200.degree. C., or prolonged exposure to temperatures in the range of 100-300.degree. C. Moreover, these novel hydrogen getter materials can be used to efficiently removing hydrogen from mixtures of hydrogen/inert gas (e.g., He, Ar, N.sub.2), hydrogen/ammonia atmospheres, such as may be encountered in heat exchangers, and hydrogen/carbon dioxide atmospheres. Water vapor and common atmospheric gases have no adverse effect on the ability of these getter materials to absorb hydrogen.
Anhydrous hydrogen fluoride electrolyte battery. [Patent application

DOEpatents

Not Available

1972-06-26

It is an object of the invention to provide a primary cell or battery using ammonium fluoride--anhydrous hydrogen fluoride electrolyte having improved current and power production capabilities at low temperatures. It is operable at temperatures substantially above the boiling point of hydrogen fluoride. (GRA)
Method for absorbing hydrogen using an oxidation resisant organic hydrogen getter

DOEpatents

Shepodd, Timothy J [Livermore, CA; Buffleben, George M [Tracy, CA

2009-02-03

A composition for removing hydrogen from an atmosphere, comprising a mixture of a polyphenyl ether and a hydrogenation catalyst, preferably a precious metal catalyst, and most preferably platinum, is disclosed. This composition is stable in the presence of oxygen, will not polymerize or degrade upon exposure to temperatures in excess of 200.degree. C., or prolonged exposure to temperatures in the range of 100-300.degree. C. Moreover, these novel hydrogen getter materials can be used to efficiently remove hydrogen from mixtures of hydrogen/inert gas (e.g., He, Ar, N.sub.2), hydrogen/ammonia atmospheres, such as may be encountered in heat exchangers, and hydrogen/carbon dioxide atmospheres. Water vapor and common atmospheric gases have no adverse effect on the ability of these getter materials to absorb hydrogen.
Materials for the scavenging of hydrogen at high temperatures

DOEpatents

Shepodd, T.J.; Phillip, B.L.

1997-12-30

A hydrogen getter composition is described comprising a double or triple bonded hydrocarbon with a high melting point useful for removing hydrogen gas, to partial pressures below 0.01 torr, from enclosed spaces and particularly from vessels used for transporting or containing fluids at elevated temperatures. The hydrogen getter compositions disclosed herein and their reaction products will neither melt nor char at temperatures in excess of 100 C. They possess significant advantages over conventional hydrogen getters, namely low risk of fire or explosion, no requirement for high temperature activation or operation, the ability to absorb hydrogen even in the presence of contaminants such as water, water vapor, common atmospheric gases and oil mists and are designed to be disposed within the confines of the apparatus. These getter materials can be mixed with binders, such as fluoropolymers, which permit the getter material to be fabricated into useful shapes and/or impart desirable properties such as water repellency or impermeability to various gases. 7 figs.
Materials for the scavanging of hydrogen at high temperatures

DOEpatents

Shepodd, Timothy J.; Phillip, Bradley L.

1997-01-01

A hydrogen getter composition comprising a double or triple bonded hydrocarbon with a high melting point useful for removing hydrogen gas, to partial pressures below 0.01 torr, from enclosed spaces and particularly from vessels used for transporting or containing fluids at elevated temperatures. The hydrogen getter compositions disclosed herein and their reaction products will neither melt nor char at temperatures in excess of 100.degree. C. They possess significant advantages over conventional hydrogen getters, namely low risk of fire or explosion, no requirement for high temperature activation or operation, the ability to absorb hydrogen even in the presence of contaminants such as water, water vapor, common atmospheric gases and oil mists and are designed to be disposed within the confines of the apparatus. These getter materials can be mixed with binders, such as fluropolymers, which permit the getter material to be fabricated into useful shapes and/or impart desirable properties such as water repellency or impermeability to various gases.
Materials for the scavanging of hydrogen at high temperatures

DOEpatents

Shepodd, Timothy J.; Phillip, Bradley L.

1997-01-01

A hydrogen getter composition comprising a double or triple bonded hydrocarbon with a high melting point useful for removing hydrogen gas, to partial pressures below 0.01 torr, from enclosed spaces and particularly from vessels used for transporting or containing fluids at elevated temperatures. The hydrogen getter compostions disclosed herein and their reaction products will neither melt nor char at temperatures in excess of 100C. They possess significant advantages over conventional hydrogen getters, namely low risk of fire or explosion, no requirement for high temperature activation or operation, the ability to absorb hydrogen even in the presence of contaminants such as water, water vapor, common atmospheric gases and oil mists and are designed to be disposed within the confines of the apparatus. These getter materials can be mixed with binders, such as fluropolymers, which permit the getter material to be fabricated into useful shapes and/or impart desirable properties such as water repellency or impermeability to various gases.
Materials for the scavenging of hydrogen at high temperatures

DOEpatents

Shepodd, T.J.; Phillip, B.L.

1997-04-29

A hydrogen getter composition is described comprising a double or triple bonded hydrocarbon with a high melting point useful for removing hydrogen gas, to partial pressures below 0.01 torr, from enclosed spaces and particularly from vessels used for transporting or containing fluids at elevated temperatures. The hydrogen getter compositions disclosed herein and their reaction products will neither melt nor char at temperatures in excess of 100C. They possess significant advantages over conventional hydrogen getters, namely low risk of fire or explosion, no requirement for high temperature activation or operation, the ability to absorb hydrogen even in the presence of contaminants such as water, water vapor, common atmospheric gases and oil mists and are designed to be disposed within the confines of the apparatus. These getter materials can be mixed with binders, such as fluoropolymers, which permit the getter material to be fabricated into useful shapes and/or impart desirable properties such as water repellency or impermeability to various gases. 7 figs.
Hydrogen isotope fractionation during lipid biosynthesis by Haloarcula marismortui

NASA Astrophysics Data System (ADS)

Dirghangi, Sitindra S.; Pagani, Mark

2013-10-01

We studied the controls on the fractionation of hydrogen isotopes during lipid biosynthesis by Haloarcula marismortui, a halophilic archaea, in pure culture experiments by varying organic substrate, the hydrogen isotope composition (D/H) of water, temperature, and salinity. Cultures were grown on three substrates: succinate, pyruvate and glycerol with known hydrogen isotope compositions, and in water with different hydrogen isotopic compositions. All culture series grown on a particular substrate show strong correlations between δDarchaeol and δDwater. However, correlations are distinctly different for cultures grown on different substrates. Our results indicate that the metabolic pathway of substrate exerts a fundamental influence on the δD value of lipids, likely by influencing the D/H composition of NADPH (nicotinamide adenine dinucleotide phosphate), the reducing agent that contributes hydrogen to carbon atoms during lipid biosynthesis. Temperature and salinity have smaller, but similar effects on δDlipid, primarily due to the way temperature and salinity influence growth rate, as well as temperature effects on the activity of enzymes.
Ice-nucleating bacteria control the order and dynamics of interfacial water

DOE PAGES

Pandey, Ravindra; Usui, Kota; Livingstone, Ruth A.; ...

2016-04-22

Ice-nucleating organisms play important roles in the environment. With their ability to induce ice formation at temperatures just below the ice melting point, bacteria such as Pseudomonas syringae attack plants through frost damage using specialized ice-nucleating proteins. Besides the impact on agriculture and microbial ecology, airborne P. syringae can affect atmospheric glaciation processes, with consequences for cloud evolution, precipitation, and climate. Biogenic ice nucleation is also relevant for artificial snow production and for biomimetic materials for controlled interfacial freezing. We use interface-specific sum frequency generation (SFG) spectroscopy to show that hydrogen bonding at the water-bacteria contact imposes structural ordering onmore » the adjacent water network. Experimental SFG data and molecular dynamics simulations demonstrate that ice active sites within P. syringae feature unique hydrophilic-hydrophobic patterns to enhance ice nucleation. Finally, the freezing transition is further facilitated by the highly effective removal of latent heat from the nucleation site, as apparent from time-resolved SFG spectroscopy.« less
Ice-nucleating bacteria control the order and dynamics of interfacial water

PubMed Central

Pandey, Ravindra; Usui, Kota; Livingstone, Ruth A.; Fischer, Sean A.; Pfaendtner, Jim; Backus, Ellen H. G.; Nagata, Yuki; Fröhlich-Nowoisky, Janine; Schmüser, Lars; Mauri, Sergio; Scheel, Jan F.; Knopf, Daniel A.; Pöschl, Ulrich; Bonn, Mischa; Weidner, Tobias

2016-01-01

Ice-nucleating organisms play important roles in the environment. With their ability to induce ice formation at temperatures just below the ice melting point, bacteria such as Pseudomonas syringae attack plants through frost damage using specialized ice-nucleating proteins. Besides the impact on agriculture and microbial ecology, airborne P. syringae can affect atmospheric glaciation processes, with consequences for cloud evolution, precipitation, and climate. Biogenic ice nucleation is also relevant for artificial snow production and for biomimetic materials for controlled interfacial freezing. We use interface-specific sum frequency generation (SFG) spectroscopy to show that hydrogen bonding at the water-bacteria contact imposes structural ordering on the adjacent water network. Experimental SFG data and molecular dynamics simulations demonstrate that ice-active sites within P. syringae feature unique hydrophilic-hydrophobic patterns to enhance ice nucleation. The freezing transition is further facilitated by the highly effective removal of latent heat from the nucleation site, as apparent from time-resolved SFG spectroscopy. PMID:27152346
The Experimental Evidence in Support of Glycosylation Mechanisms at the SN1-SN2 Interface.

PubMed

Adero, Philip Ouma; Amarasekara, Harsha; Wen, Peng; Bohé, Luis; Crich, David

2018-05-30

A critical review of the state-of-the-art evidence in support of the mechanisms of glycosylation reactions is provided. Factors affecting the stability of putative oxocarbenium ions as intermediates at the S N 1 end of the mechanistic continuum are first surveyed before the evidence, spectroscopic and indirect, for the existence of such species on the time scale of glycosylation reactions is presented. Current models for diastereoselectivity in nucleophilic attack on oxocarbenium ions are then described. Evidence in support of the intermediacy of activated covalent glycosyl donors is reviewed, before the influences of the structure of the nucleophile, of the solvent, of temperature, and of donor-acceptor hydrogen bonding on the mechanism of glycosylation reactions are surveyed. Studies on the kinetics of glycosylation reactions and the use of kinetic isotope effects for the determination of transition-state structure are presented, before computational models are finally surveyed. The review concludes with a critical appraisal of the state of the art.
Effect of oxygen vacancies and phases on catalytic properties of hydrogen-treated nanoceria particles

NASA Astrophysics Data System (ADS)

Lan, Yuan-Pei; Sohn, Hong Yong

2018-03-01

Nanoceria powder was treated by hydrogen or air at different temperatures and atmospheres, and the phases, oxygen vacancies, catalytic properties of the treated samples were investigated. After treating, the crystallites on the ceria surface were fused, and the SEM and TEM images indicated that the particle size increased with treatment temperature. Both Raman and XPS spectra showed the oxygen vacancies in nanoceria increased with treatment temperature in hydrogen, and at the same temperature CeO2 treated in hydrogen had a higher Ce3+ fraction than that treated in air. The nanoceria after being treated in hydrogen at 900 °C contained the Ce2O3 phase together with CeO2 which was revealed by XRD and TEM results. Oxygen vacancies were found to enhance CO conversion, but the high temperature needed to generate the oxygen vacancies caused the fusion of the crystallites on the ceria surface and thus its area decreased, which resulted in lower catalytic activity. The catalytic activity of nanoceria treated in hydrogen at 900 °C measured higher than that of the ceria powders treated at 700 °C in hydrogen or 900 °C in air, which indicated that the Ce2O3 phase present in the treated nanoceria particles enhanced the catalytic activity.
Variations of the Hydrogen Bonding and of the Hydrogen Bonded Network in Ethanol-Water Mixtures on Cooling.

PubMed

Pothoczki, Szilvia; Pusztai, Laszlo; Bako, Imre

2018-06-12

Molecular dynamics computer simulations have been conducted for ethanol-water liquid mixtures in the water-rich side of the composition range, with 10, 20 and 30 mol % of the alcohol, at temperatures between room temperature and the experimental freezing point of the given mixture. All-atom type (OPLS) interatomic potentials have been assumed for ethanol, in combination with two kinds of rigid water models (SPC/E and TIP4P/2005). Both combinations have provided excellent reproductions of the experimental X-ray total structure factors at each temperature; this yielded a strong basis for further structural analyses. Beyond partial radial distribution functions, various descriptors of hydrogen bonded assemblies, as well as of the hydrogen bonded network have been determined. A clear tendency was observed towards that an increasing proportion of water molecules participate in hydrogen bonding with exactly 2 donor- and 2 acceptor sites as temperature decreases. Concerning larger assemblies held together by hydrogen bonding, the main focus was put on the properties of cyclic entities: it was found that, similarly to methanol-water mixtures, the number of hydrogen bonded rings has increased with lowering temperature. However, for ethanol-water mixtures the dominance of not the six-, but of the five-fold rings could be observed.
Effect of species, life stage, and water temperature on the toxicity of hydrogen peroxide to fish

USGS Publications Warehouse

Rach, J.J.; Schreier, Theresa M.; Howe, G.E.; Redman, S.D.

1997-01-01

Hydrogen peroxide is a drug of low regulatory priority status that is effective in treating fish and fish eggs infected by fungi. However, only limited information is available to guide fish culturists in administering hydrogen peroxide to diseased fish. Laboratory tests were conducted to determine (1) the sensitivity of brown trout Salmo trutta, lake trout Salvelinus namaycush, fathead minnow Pimephales promelas, walleye Stizostedion vitreum, channel catfish Ictalurus punctatus, and bluegill Lepomis, machrochirus to hydrogen peroxide treatments; (2) the sensitivity of various life stages of rainbow trout Oncorhynchus mykiss to hydrogen peroxide treatments; and (3) the effect of water temperature on the acute toxicity of hydrogen peroxide to three fish species. Fish were exposed to hydrogen peroxide concentrations ranging from 100 to 5,000 mu L/L (ppm) for 15-min or 45-min treatments every other day for four consecutive treatments to determine the sensitivity of various species and life stages of fish. Except for walleye, most species of fish tested (less than or equal to 2 g) tolerated hydrogen peroxide of 1,000 mu L/L or greater. Walleyes were sensitive to hydrogen peroxide concentrations as low as 100 mu L/L. A correlation was found between the toxicity of hydrogen peroxide and the life stages of rainbow trout; larger fish were more sensitive. Generally, the toxicity of hydrogen peroxide increased for all species as water temperature increased. The results of these experiments demonstrate that it is important to consider the effects of species, life stage, and water temperature when conducting hydrogen peroxide treatments.
Atomic and molecular hydrogen gas temperatures in a low-pressure helicon plasma

NASA Astrophysics Data System (ADS)

Samuell, Cameron M.; Corr, Cormac S.

2015-08-01

Neutral gas temperatures in hydrogen plasmas are important for experimental and modelling efforts in fusion technology, plasma processing, and surface modification applications. To provide values relevant to these application areas, neutral gas temperatures were measured in a low pressure (< 10 mTorr) radiofrequency helicon discharge using spectroscopic techniques. The atomic and molecular species were not found to be in thermal equilibrium with the atomic temperature being mostly larger then the molecular temperature. In low power operation (< 1 kW), the molecular hydrogen temperature was observed to be linearly proportional to the pressure while the atomic hydrogen temperature was inversely proportional. Both temperatures were observed to rise linearly with input power. For high power operation (5-20 kW), the molecular temperature was found to rise with both power and pressure up to a maximum of approximately 1200 K. Spatially resolved measurements near a graphite target demonstrated localised cooling near the sample surface. The temporal evolution of the molecular gas temperature during a high power 1.1 ms plasma pulse was also investigated and found to vary considerably as a function of pressure.
Corrosion Performance of Inconel 625 in High Sulphate Content

NASA Astrophysics Data System (ADS)

Ismail, Azzura

2016-05-01

Inconel 625 (UNS N06625) is a type of nickel-chromium-molybdenum alloy with excellent corrosion resistance in a wide range of corrosive media, being especially resistant to pitting and crevice corrosion. However, in aggressive environment, Inconel 625 will suffer corrosion attack like other metals. This research compared the corrosion performance of Inconel 625 when exposed to higher sulphate content compared to real seawater. The results reveal that Inconel 625 is excellent in resist the corrosion attack in seawater. However, at increasing temperature, the corrosion resistance of this metal decrease. The performance is same in seawater with high sulphate content at increasing temperature. It can be concluded that sulphate promote perforation on Inconel 625 and become aggressive agents that accelerate the corrosion attack.
Performance assessment of low pressure nuclear thermal propulsion

NASA Technical Reports Server (NTRS)

Gerrish, Harrold P., Jr.; Doughty, Glen E.

1993-01-01

An increase in Isp for nuclear thermal propulsion systems is desirable for reducing the propellant requirements and cost of future applications, such as the Mars Transfer Vehicle. Several previous design studies have suggested that the Isp could be increased substantially with hydrogen dissociation/recombination. Hydrogen molecules (H2), at high temperatures and low pressures, will dissociate to monatomic hydrogen (H). The reverse process (i.e., formation of H2 from H) is exothermic. The exothermic energy in a nozzle increases the kinetic energy and therefore, increases the Isp. The low pressure nuclear thermal propulsion system (LPNTP) system is expected to maximize the hydrogen dissociation/recombination and Isp by operating at high chamber temperatures and low chamber pressures. The process involves hydrogen flow through a high temperature, low pressure fission reactor, and out a nozzle. The high temperature (approximately 3000 K) of the hydrogen in the reactor is limited by the temperature limits of the reactor material. The minimum chamber pressure is about 1 atm because lower pressures decrease the engines thrust to weight ratio below acceptable limits. This study assumes that hydrogen leaves the reactor and enters the nozzle at the 3000 K equilibrium dissociation level. Hydrogen dissociation in the reactor does not affect LPNTP performance like dissociation in traditional chemical propulsion systems, because energy from the reactor resupplies energy lost due to hydrogen dissociation. Recombination takes place in the nozzle due primarily to a drop in temperature as the Mach number increases. However, as the Mach number increases beyond the nozzle throat, the static pressure and density of the flow decreases and minimizes the recombination. The ideal LPNTP Isp at 3000 K and 10 psia is 1160 seconds due to the added energy from fast recombination rates. The actual Isp depends on the finite kinetic reaction rates which affect the amount of monatomic hydrogen recombination before the flow exits the nozzle. A LPNTP system has other technical issues (e.g. flow instability and two-phase flow) besides hydrogen dissociation/recombination which affect the systems practicality. In this study, only the effects of hydrogen dissociation/recombination are examined.
Metallic Hydrogen - Potentially a High Energy Rocket Propellant

NASA Technical Reports Server (NTRS)

Cole, John; Silvera, Ike

2007-01-01

Pure metallic hydrogen is predicted to have a specific impulse (Isp) of 1700 seconds, but the reaction temperature is too high for current engine materials. Diluting metallic hydrogen with liquid hydrogen can reduce the reaction temperature to levels compatible with current material limits and still provide an Isp greater than 900 s. Metallic hydrogen has not yet been produced on earth, but experimental techniques exist that may change this situation. This paper will provide a brief description of metallic hydrogen and the status of experiments that may soon produce detectable quantities of this material in the lab. Also provided are some characteristics for diluted metallic hydrogen engines and launch vehicles.

Process for hydrogenation of hydrocarbon tars

DOEpatents

Dolbear, Geoffrey E.

1978-07-18

Hydrocarbon tars of high asphaltene content such as tars obtained from pyrolysis of coal are dissolved in a solvent formed from the hydrogenation of the coal tars, and the resultant mixture hydrogenated in the presence of a catalyst at a pressure from about 1500 to 5000 psig at a temperature from about 500.degree. F to about the critical temperature of the solvent to form a light hydrocarbon as a solvent for the tars. Hydrogen content is at least three times the amount of hydrogen consumed.
Mechanical properties of turbine blade alloys in hydrogen at elevated temperatures

NASA Technical Reports Server (NTRS)

Deluca, D. P.

1981-01-01

The mechanical properties of single crystal turbine blade alloys in a gaseous hydrogen environment were determined. These alloys are proposed for use in space propulsion systems in pure or partial high pressure hydrogen environments at elevated temperatures. Mechanical property tests included: tensile, creep, low fatigue (LCF), and crack growth. Specimens were in both transverse and longitudinal directions relative to the casting solidification direction. Testing was conducted on solid specimens exposed to externally pressurized environments of gaseous hydrogen and hydrogen-enriched steam.
H2 spillover enhanced hydrogenation capability of TiO2 used for photocatalytic splitting of water: a traditional phenomenon for new applications.

PubMed

Zhu, Yingming; Liu, Dongsheng; Meng, Ming

2014-06-07

Black TiO2 was usually obtained via hydrogenation at high pressure and high temperature. Herein, we reported a facile hydrogenation of TiO2 in the presence of a small amount of Pt at relatively low temperature and atmospheric pressure. The hydrogen spillover from Pt to TiO2 accounts well for the greatly enhanced hydrogenation capability. The as-synthesized Pt/TiO2 exhibits remarkably improved photocatalytic activity for water splitting.
Quantum rotation and translation of hydrogen molecules encapsulated inside C₆₀: temperature dependence of inelastic neutron scattering spectra.

PubMed

Horsewill, A J; Goh, K; Rols, S; Ollivier, J; Johnson, M R; Levitt, M H; Carravetta, M; Mamone, S; Murata, Y; Chen, J Y-C; Johnson, J A; Lei, X; Turro, N J

2013-09-13

The quantum dynamics of a hydrogen molecule encapsulated inside the cage of a C60 fullerene molecule is investigated using inelastic neutron scattering (INS). The emphasis is on the temperature dependence of the INS spectra which were recorded using time-of-flight spectrometers. The hydrogen endofullerene system is highly quantum mechanical, exhibiting both translational and rotational quantization. The profound influence of the Pauli exclusion principle is revealed through nuclear spin isomerism. INS is shown to be exceptionally able to drive transitions between ortho-hydrogen and para-hydrogen which are spin-forbidden to photon spectroscopies. Spectra in the temperature range 1.6≤T≤280 K are presented, and examples are given which demonstrate how the temperature dependence of the INS peak amplitudes can provide an effective tool for assigning the transitions. It is also shown in a preliminary investigation how the temperature dependence may conceivably be used to probe crystal field effects and inter-fullerene interactions.
A ketone/alcohol polymer for cycle of electrolytic hydrogen-fixing with water and releasing under mild conditions

PubMed Central

Kato, Ryo; Yoshimasa, Keisuke; Egashira, Tatsuya; Oya, Takahiro; Oyaizu, Kenichi; Nishide, Hiroyuki

2016-01-01

Finding a safe and efficient carrier of hydrogen is a major challenge. Recently, hydrogenated organic compounds have been studied as hydrogen storage materials because of their ability to stably and reversibly store hydrogen by forming chemical bonds; however, these compounds often suffer from safety issues and are usually hydrogenated with hydrogen at high pressure and/or temperature. Here we present a ketone (fluorenone) polymer that can be moulded as a plastic sheet and fixes hydrogen via a simple electrolytic hydrogenation at −1.5 V (versus Ag/AgCl) in water at room temperature. The hydrogenated alcohol derivative (the fluorenol polymer) reversibly releases hydrogen by heating (80 °C) in the presence of an aqueous iridium catalyst. Both the use of a ketone polymer and the efficient hydrogen fixing with water as a proton source are completely different from other (de)hydrogenated compounds and hydrogenation processes. The easy handling and mouldable polymers could suggest a pocketable hydrogen carrier. PMID:27687772
Effect of voids on Arrhenius relationship between H-solubility and temperature in nickel

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wu, Q.Y.; Sun, X.K.; Hu, Z.Q.

1997-01-15

Many investigations about the states of hydrogen in voids within metals have been carried out over the past years. These probable states of hydrogen in the voids are directly relevant to hydrogen embrittlement mechanisms. Therefore, a knowledge of the states of hydrogen in the voids is important to an understanding of hydrogen-related degradation of material properties. Some results show that hydrogen exists as a molecule in the voids, while others suggest it is in the chemisorbed state on the internal surface of the voids. The results of Sung-Man lee et al. suggested that hydrogen in the voids in nickel existsmore » both in the gaseous and chemisorbed stats, and most of the hydrogen trapped in the voids seems to be present as a chemisorbed state in 1 atm. hydrogen pressure in the temperature range of 350--582 C. But there is no quantitative description concerning the effects of the voids on the solubility of hydrogen in materials. The purpose of this work is to describe quantitatively the effects of the voids on hydrogen solubility in nickel, considering hydrogen exists as gaseous and chemisorbed states in the voids, and the very weak physical adsorption above room temperature is neglected.« less
Characteristics of hydrogen produced by partial oxidation and auto-thermal reforming in a small methanol reformer

NASA Astrophysics Data System (ADS)

Horng, Rong-Fang; Chou, Huann-Ming; Lee, Chiou-Hwang; Tsai, Hsien-Te

This paper investigates experimentally, the transient characteristics of a small methanol reformer using partial oxidation (POX) and auto-thermal reforming (ATR) for fuel cell applications. The parameters varied were heating temperature, methanol supply rate, steady mode shifting temperature, O 2/C (O 2/CH 3OH) and S/C (H 2O/CH 3OH) molar ratios with the main aim of promoting a rapid response and a high flow rate of hydrogen. The experiments showed that a high steady mode shifting temperature resulted in a faster temperature rise at the catalyst outlet and vice versa and that a low steady mode shifting temperature resulted in a lower final hydrogen concentration. However, when the mode shifting temperature was too high, the hydrogen production response was not necessarily improved. It was subsequently shown that the optimum steady mode shifting temperature for this experimental set-up was approximately 75 °C. Further, the hydrogen concentration produced by the auto-thermal process was as high as 49.12% and the volume flow rate up to 23.0 L min -1 compared to 40.0% and 20.5 L min -1 produced by partial oxidation.
DOE Office of Scientific and Technical Information (OSTI.GOV)

Panda, Pratikash P.; Hecht, Ethan S.

In this work, under-expanded cryogenic hydrogen jets were investigated experimentally for their ignition and flame characteristics. The test facility described herein, was designed and constructed to release hydrogen at a constant temperature and pressure, to study the dispersion and thermo-physical properties of cryogenic hydrogen releases and flames. In this study, a non-intrusive laser spark focused on the jet axis was used to measure the maximum ignition distance. The radiative power emitted by the corresponding jet flames was also measured for a range of release scenarios from 37 K to 295 K, 2–6 bar abs through nozzles with diameters from 0.75more » to 1.25 mm. The maximum ignition distance scales linearly with the effective jet diameter (which scales as the square root of the stagnant fluid density). A 1-dimensional (stream-wise) cryogenic hydrogen release model developed previously at Sandia National Laboratories (although this model is not yet validated for cryogenic hydrogen) was exercised to predict that the mean mole fraction at the maximum ignition distance is approximately 0.14, and is not dependent on the release conditions. The flame length and width were extracted from visible and infra-red flame images for several test cases. The flame length and width both scale as the square root of jet exit Reynolds number, as reported in the literature for flames from atmospheric temperature hydrogen. As shown in previous studies for ignited atmospheric temperature hydrogen, the radiative power from the jet flames of cold hydrogen scales as a logarithmic function of the global flame residence time. The radiative heat flux from jet flames of cold hydrogen is higher than the jet flames of atmospheric temperature hydrogen, for a given mass flow rate, due to the lower choked flow velocity of low-temperature hydrogen. Lastly, this study provides critical information with regard to the development of models to inform the safety codes and standards of hydrogen infrastructure.« less
System Evaluation and Economic Analysis of a HTGR Powered High-Temperature Electrolysis Hydrogen Production Plant

DOE Office of Scientific and Technical Information (OSTI.GOV)

Michael G. McKellar; Edwin A. Harvego; Anastasia A. Gandrik

2010-10-01

A design for a commercial-scale high-temperature electrolysis (HTE) plant for hydrogen production has been developed. The HTE plant is powered by a high-temperature gas-cooled reactor (HTGR) whose configuration and operating conditions are based on the latest design parameters planned for the Next Generation Nuclear Plant (NGNP). The current HTGR reference design specifies a reactor power of 600 MWt, with a primary system pressure of 7.0 MPa, and reactor inlet and outlet fluid temperatures of 322°C and 750°C, respectively. The power conversion unit will be a Rankine steam cycle with a power conversion efficiency of 40%. The reference hydrogen production plantmore » operates at a system pressure of 5.0 MPa, and utilizes a steam-sweep system to remove the excess oxygen that is evolved on the anode (oxygen) side of the electrolyzer. The overall system thermal-to-hydrogen production efficiency (based on the higher heating value of the produced hydrogen) is 40.4% at a hydrogen production rate of 1.75 kg/s and an oxygen production rate of 13.8 kg/s. An economic analysis of this plant was performed with realistic financial and cost estimating assumptions. The results of the economic analysis demonstrated that the HTE hydrogen production plant driven by a high-temperature helium-cooled nuclear power plant can deliver hydrogen at a cost of $3.67/kg of hydrogen assuming an internal rate of return, IRR, of 12% and a debt to equity ratio of 80%/20%. A second analysis shows that if the power cycle efficiency increases to 44.4%, the hydrogen production efficiency increases to 42.8% and the hydrogen and oxygen production rates are 1.85 kg/s and 14.6 kg/s respectively. At the higher power cycle efficiency and an IRR of 12% the cost of hydrogen production is $3.50/kg.« less
A STUDY OF THE EFFECT OF SUBSTITUENTS AND OF SOLVENT ON THE REACTIVITY OF THE NORMAL AND ABNORMAL POSITIONS OF UNSYMMETRICAL ORGANIC EPOXIDES

DTIC Science & Technology

determined by a kinetic study of the reactions of m-chloro- and 3,4-dimethylbenzylamine with styrene oxide in ethanol at 3 temperatures. The results...and o-methyl-styrene oxide with benzylamine in ethanol showed that the beta-methyl group reduces the rate of attack at both positions very...considerably, while the alpha-methyl group reduces the rate of normal attack slightly and that of abnormal attack considerably, and the o-methyl group has surprisingly little effect of the rate of attack at either position. (Author)
Large scale production of densified hydrogen to the triple point and below

NASA Astrophysics Data System (ADS)

Swanger, A. M.; Notardonato, W. U.; E Fesmire, J.; Jumper, K. M.; Johnson, W. L.; Tomsik, T. M.

2017-12-01

Recent demonstration of advanced liquid hydrogen storage techniques using Integrated Refrigeration and Storage technology at NASA Kennedy Space Center led to the production of large quantities of densified liquid and slush hydrogen in a 125,000 L tank. Production of densified hydrogen was performed at three different liquid levels and LH2 temperatures were measured by twenty silicon diode temperature sensors. Overall densification performance of the system is explored, and solid mass fractions are calculated. Experimental data reveal hydrogen temperatures dropped well below the triple point during testing, and were continuing to trend downward prior to system shutdown. Sub-triple point temperatures were seen to evolve in a time dependent manner along the length of the horizontal, cylindrical vessel. The phenomenon, observed at two fill levels, is detailed herein. The implications of using IRAS for energy storage, propellant densification, and future cryofuel systems are discussed.
Large Scale Production of Densified Hydrogen to the Triple Point and Below

NASA Technical Reports Server (NTRS)

Swanger, A. M.; Notardonato, W. U.; Fesmire, J. E.; Jumper, K. M.; Johnson, W. L.; Tomsik, T. M.

2017-01-01

Recent demonstration of advanced liquid hydrogen storage techniques using Integrated Refrigeration and Storage technology at NASA Kennedy Space Center led to the production of large quantities of densified liquid and slush hydrogen in a 125,000 L tank. Production of densified hydrogen was performed at three different liquid levels and LH2 temperatures were measured by twenty silicon diode temperature sensors. Overall densification performance of the system is explored, and solid mass fractions are calculated. Experimental data reveal hydrogen temperatures dropped well below the triple point during testing, and were continuing to trend downward prior to system shutdown. Sub-triple point temperatures were seen to evolve in a time dependent manner along the length of the horizontal, cylindrical vessel. The phenomenon, observed at two fill levels, is detailed herein. The implications of using IRAS for energy storage, propellant densification, and future cryofuel systems are discussed.
A general ligand design for gold catalysis allowing ligand-directed anti-nucleophilic attack of alkynes.

PubMed

Wang, Yanzhao; Wang, Zhixun; Li, Yuxue; Wu, Gongde; Cao, Zheng; Zhang, Liming

2014-04-07

Most homogenous gold catalyses demand ≥ 0.5 mol% catalyst loading. Owing to the high cost of gold, these reactions are unlikely to be applicable in medium- or large-scale applications. Here we disclose a novel ligand design based on the privileged (1,1'-biphenyl)-2-ylphosphine framework that offers a potentially general approach to dramatically lowering catalyst loading. In this design, an amide group at the 3'-position of the ligand framework directs and promotes nucleophilic attack at the ligand gold complex-activated alkyne, which is unprecedented in homogenous gold catalysis considering the spatial challenge of using ligand to reach anti-approaching nucleophile in a linear P-Au-alkyne centroid structure. With such a ligand, the gold(I) complex becomes highly efficient in catalysing acid addition to alkynes, with a turnover number up to 99,000. Density functional theory calculations support the role of the amide moiety in directing the attack of carboxylic acid via hydrogen bonding.
A General Ligand Design for Gold Catalysis allowing Ligand-Directed Anti Nucleophilic Attack of Alkynes

PubMed Central

Wang, Yanzhao; Wang, Zhixun; Li, Yuxue; Wu, Gongde; Cao, Zheng; Zhang, Liming

2014-01-01

Most homogenous gold catalyses demand ≥0.5 mol % catalyst loading. Due to the high cost of gold, these reactions are unlikely to be applicable in medium or large scale applications. Here we disclose a novel ligand design based on the privileged biphenyl-2-phosphine framework that offers a potentially general approach to dramatically lowering catalyst loading. In this design, an amide group at the 3’ position of the ligand framework directs and promotes nucleophilic attack at the ligand gold complex-activated alkyne, which is unprecedented in homogeneous gold catalysis considering the spatial challenge of using ligand to reach antiapproaching nucleophile in a linear P-Au-alkyne centroid structure. With such a ligand, the gold(I) complex becomes highly efficient in catalyzing acid addition to alkynes, with a turnover number up to 99,000. Density functional theory calculations support the role of the amide moiety in directing the attack of carboxylic acid via hydrogen bonding. PMID:24704803
Seasonal Terpene Variation in Needles of Pinus radiata (Pinales: Pinaceae) Trees Attacked by Tomicus piniperda (Coleoptera: Scolytinae) and the Effect of Limonene on Beetle Aggregation.

PubMed

Romón, Pedro; Aparicio, Domitila; Palacios, Francisco; Iturrondobeitia, Juan Carlos; Hance, Thierry; Goldarazena, Arturo

2017-09-01

Concentrations of four monoterpenes were determined in needles of Pinus radiata (D.Don) (Pinales: Pinaceae) trees that were attacked or nonattacked by Tomicus piniperda (L.) (Coleoptera: Scolytinae). Compounds were identified and quantified by gas chromatography-mass spectrometry. The mean ambient temperature was obtained using climate-recording data loggers. The effect of limonene on field aggregation was also evaluated at three limonene release rates using Lindgren attractant-baited traps and trap logs. Attacked trees produced less α-pinene in March, July, and November than nonattacked trees, less β-pinene in July and November, and less limonene from May to November. Limonene reduced the attraction of T. piniperda to attractant-baited traps and trap logs. Results were linked to better responses to high temperatures, with respect to terpene contents, by the nonattacked trees after the spring attack. © The Author 2017. Published by Oxford University Press on behalf of Entomological Society of America.
Catalytic two-stage coal hydrogenation and hydroconversion process

DOEpatents

MacArthur, James B.; McLean, Joseph B.; Comolli, Alfred G.

1989-01-01

A process for two-stage catalytic hydrogenation and liquefaction of coal to produce increased yields of low-boiling hydrocarbon liquid and gas products. In the process, the particulate coal is slurried with a process-derived liquid solvent and fed at temperature below about 650.degree. F. into a first stage catalytic reaction zone operated at conditions which promote controlled rate liquefaction of the coal, while simultaneously hydrogenating the hydrocarbon recycle oils at conditions favoring hydrogenation reactions. The first stage reactor is maintained at 650.degree.-800.degree. F. temperature, 1000-4000 psig hydrogen partial pressure, and 10-60 lb coal/hr/ft.sup.3 reactor space velocity. The partially hydrogenated material from the first stage reaction zone is passed directly to the close-coupled second stage catalytic reaction zone maintained at a temperature at least about 25.degree. F. higher than for the first stage reactor and within a range of 750.degree.-875.degree. F. temperature for further hydrogenation and thermal hydroconversion reactions. By this process, the coal feed is successively catalytically hydrogenated and hydroconverted at selected conditions, which results in significantly increased yields of desirable low-boiling hydrocarbon liquid products and minimal production of undesirable residuum and unconverted coal and hydrocarbon gases, with use of less energy to obtain the low molecular weight products, while catalyst life is substantially increased.
Thermal response to firefighting activities in residential structure fires: impact of job assignment and suppression tactic.

PubMed

Horn, Gavin P; Kesler, Richard M; Kerber, Steve; Fent, Kenneth W; Schroeder, Tad J; Scott, William S; Fehling, Patricia C; Fernhall, Bo; Smith, Denise L

2018-03-01

Firefighters' thermal burden is generally attributed to high heat loads from the fire and metabolic heat generation, which may vary between job assignments and suppression tactic employed. Utilising a full-sized residential structure, firefighters were deployed in six job assignments utilising two attack tactics (1. Water applied from the interior, or 2. Exterior water application before transitioning to the interior). Environmental temperatures decreased after water application, but more rapidly with transitional attack. Local ambient temperatures for inside operation firefighters were higher than other positions (average ~10-30 °C). Rapid elevations in skin temperature were found for all job assignments other than outside command. Neck skin temperatures for inside attack firefighters were ~0.5 °C lower when the transitional tactic was employed. Significantly higher core temperatures were measured for the outside ventilation and overhaul positions than the inside positions (~0.6-0.9 °C). Firefighters working at all fireground positions must be monitored and relieved based on intensity and duration. Practitioner Summary: Testing was done to characterise the thermal burden experienced by firefighters in different job assignments who responded to controlled residential fires (with typical furnishings) using two tactics. Ambient, skin and core temperatures varied based on job assignment and tactic employed, with rapid elevations in core temperature in many roles.
Influence of gaseous hydrogen on metals

NASA Technical Reports Server (NTRS)

Walter, R. J.; Chandler, W. T.

1973-01-01

Tensile, fracture toughness, threshold stress intensity for sustained-load crack growth, and cyclic and sustained load crack growth rate measurements were performed on a number of alloys in high-pressure hydrogen and helium environments. The results of tensile tests performed in 34.5 MN/m2 (5000 psi) hydrogen indicated that Inconel 625 was considerable embrittled at ambient temperature but was not embrittled at 144 K (-200 F). The tensile properties of AISI 321 stainless steel were slightly reduced at ambient temperature and 144 K (-200 F). The tensile properties of Ti-5Al-2.5 Sn ELI were essentially unaffected by hydrogen at 144 K (-200 F). OFHC copper was not embrittled by hydrogen at ambient temperature or at 144 K (-200 F).
Hydrogen gas sensors using a thin Ta2O5 dielectric film

NASA Astrophysics Data System (ADS)

Kim, Seongjeen

2014-12-01

A capacitive-type hydrogen gas sensor with a MIS (metal-insulator-semiconductor) structure was investigated for high-temperature applications. In this work, a tantalum oxide (Ta2O5) layer of tens of nanometers in thickness formed by oxidizing tantalum film in rapid thermal processing (RTP) was exploited with the purpose of sensitivity improvement. Silicon carbide (SiC), which is good even at high temperatures over 500 °C, was used as the substrate. We fabricated sensors composed of Pd/Ta2O5/SiC, and the dependences of the capacitance response properties and the I-V characteristics on the hydrogen concentration were analyzed from the temperature range of room temperature to 500 °C. As a result, our hydrogen sensor showed promising performance with respect to the sensitivity and the adaptability at high temperature.
Cold weather hydrogen generation system and method of operation

DOEpatents

Dreier, Ken Wayne; Kowalski, Michael Thomas; Porter, Stephen Charles; Chow, Oscar Ken; Borland, Nicholas Paul; Goyette, Stephen Arthur

2010-12-14

A system for providing hydrogen gas is provided. The system includes a hydrogen generator that produces gas from water. One or more heat generation devices are arranged to provide heating of the enclosure during different modes of operation to prevent freezing of components. A plurality of temperature sensors are arranged and coupled to a controller to selectively activate a heat source if the temperature of the component is less than a predetermined temperature.

Modelling of hydrogen transport in silicon solar cell structures under equilibrium conditions

NASA Astrophysics Data System (ADS)

Hamer, P.; Hallam, B.; Bonilla, R. S.; Altermatt, P. P.; Wilshaw, P.; Wenham, S.

2018-01-01

This paper presents a model for the introduction and redistribution of hydrogen in silicon solar cells at temperatures between 300 and 700 °C based on a second order backwards difference formula evaluated using a single Newton-Raphson iteration. It includes the transport of hydrogen and interactions with impurities such as ionised dopants. The simulations lead to three primary conclusions: (1) hydrogen transport across an n-type emitter is heavily temperature dependent; (2) under equilibrium conditions, hydrogen is largely driven by its charged species, with the switch from a dominance of negatively charged hydrogen (H-) to positively charged hydrogen (H+) within the emitter region critical to significant transport across the junction; and (3) hydrogen transport across n-type emitters is critically dependent upon the doping profile within the emitter, and, in particular, the peak doping concentration. It is also observed that during thermal processes after an initial high temperature step, hydrogen preferentially migrates to the surface of a phosphorous doped emitter, drawing hydrogen out of the p-type bulk. This may play a role in several effects observed during post-firing anneals in relation to the passivation of recombination active defects and even the elimination of hydrogen-related defects in the bulk of silicon solar cells.
The solubility of hydrogen in plutonium in the temperature range 475 to 825 degrees centigrade

DOE Office of Scientific and Technical Information (OSTI.GOV)

Allen, T.H.

1991-01-01

The solubility of hydrogen (H) in plutonium metal (Pu) was measured in the temperature range of 475 to 825{degree}C for unalloyed Pu (UA) and in the temperature range of 475 to 625{degree}C for Pu containing two-weight-percent gallium (TWP). For TWP metal, in the temperature range 475 to 600{degree}C, the saturated solution has a maximum hydrogen to plutonium ration (H/Pu) of 0.00998 and the standard enthalpy of formation ({Delta}H{degree}{sub f(s)}) is (-0.128 {plus minus} 0.0123) kcal/mol. The phase boundary of the solid solution in equilibrium with plutonium dihydride (PuH{sub 2}) is temperature independent. In the temperature range 475 to 625{degree}C, UAmore » metal has a maximum solubility at H/Pu = 0.011. The phase boundary between the solid solution region and the metal+PuH{sub 2} two-phase region is temperature dependent. The solubility of hydrogen in UA metal was also measured in the temperature range 650 to 825{degree}C with {Delta}H{degree}{sub f(s)} = (-0.104 {plus minus} 0.0143) kcal/mol and {Delta}S{degree}{sub f(s)} = 0. The phase boundary is temperature dependent and the maximum hydrogen solubility has H/Pu = 0.0674 at 825{degree}C. 52 refs., 28 figs., 9 tabs.« less
Micro-structured femtosecond laser assisted FBG hydrogen sensor.

PubMed

Karanja, Joseph Muna; Dai, Yutang; Zhou, Xian; Liu, Bin; Yang, Minghong

2015-11-30

We discuss hydrogen sensors based on fiber Bragg gratings (FBGs) micro-machined by femtosecond laser to form microgrooves and sputtered with Pd/Ag composite film. The atomic ratio of the two metals is controlled at Pd:Ag = 3:1. At room temperature, the hydrogen sensitivity of the sensor probe micro-machined by 75 mW laser power and sputtered with 520 nm of Pd/Ag film is 16.5 pm/%H. Comparably, the standard FBG hydrogen sensitivity becomes 2.5 pm/%H towards the same 4% hydrogen concentration. At an ambient temperature of 35°C, the processed sensor head has a dramatic rise in hydrogen sensitivity. Besides, the sensor shows good response and repeatability during hydrogen concentration test.
Rigidity and resistance of larval- and adult schistosomes-medium interface

DOE Office of Scientific and Technical Information (OSTI.GOV)

Migliardo, Federica, E-mail: fmigliardo@unime.it; Tallima, Hatem; El Ridi, Rashika

Graphical abstract: - Highlights: • Schistosoma larvae and worms are studied by neutron scattering. • Measurements on larvae were repeated after one day and by increasing temperature. • The flexibility properties of larvae and adult parasites are compared. • The parasite rigidity is related to their resistance to the hostile environment. • Insight into the parasite defense mechanisms to the immune system attack is achieved. - Abstract: Schistosomiasis is second only to malaria in prevalence and severity, and is still a major health problem in many tropical countries worldwide with about 200–300 million cases and with more than 800 millionmore » people at risk of infection. Based on these data, the World Health Organization recommends fostering research efforts for understanding at any level the mechanisms of the infection and then decreasing the social and economical impact of schistosomiasis. A key role is played by the parasite apical lipid membrane, which is entirely impervious to the surrounding elements of the immune system. We have previously demonstrated that the interaction between schistosomes and surrounding medium is governed by a parasite surface membrane sphingomyelin-based hydrogen barrier. In the present article, the elastic contribution to the total motion as a function of the exchanged wave-vector Q and the mean square displacement values for Schistosoma mansoni larvae and worms and Schistosomahaematobium worms have been evaluated by quasi elastic neutron scattering (QENS). The results point out that S. mansoni larvae show a smaller mean square displacement in comparison to S. mansoni and S. haematobium worms. These values increased by repeating the measurements after one day. These differences, which are analogous to those observed for the diffusion coefficient we previously evaluated, are interpreted in terms of rigidity of the parasite-medium interaction. S. mansoni larvae are the most rigid systems, while S. haematobium worms are the most flexible. In addition, temperature and hypoxia induce a weakening of the schistosome-medium interaction. These evidences are related to the strength of the hydrogen-bonded interaction between parasites and environment that we previously determined. We have shown that S. mansoni worms are characterized by a weakened interaction in respect to the larvae, while the S. haematobium worms more weakly interact with the surrounding medium than S. mansoni. The present QENS analysis allowed us to characterize the rigidity of larval- and adult S. mansoni and S. haematobium-host interface and to relate it to the parasite resistance to the hostile elements of the surrounding medium and to the immune effectors attack.« less
Corrosion of aluminum alloys by chlorinated hydrocarbon/methanol mixtures

NASA Technical Reports Server (NTRS)

De Forest, W. S.

1967-01-01

Laboratory investigations show that water-free mixtures of Freon MF /trichlorofluoromethane/ and methanol vigorously attack aluminum alloys which contain significant amounts of copper. Freon MF alone did not attack the aluminum alloys at room temperature. Pure methanol had only a slight corrosive effect on the alloy.
Effect of high-temperature water and hydrogen on the fracture behavior of a low-alloy reactor pressure vessel steel

NASA Astrophysics Data System (ADS)

Roychowdhury, S.; Seifert, H.-P.; Spätig, P.; Que, Z.

2016-09-01

Structural integrity of reactor pressure vessels (RPV) is critical for safety and lifetime. Possible degradation of fracture resistance of RPV steel due to exposure to coolant and hydrogen is a concern. In this study tensile and elastic-plastic fracture mechanics (EPFM) tests in air (hydrogen pre-charged) and EFPM tests in hydrogenated/oxygenated high-temperature water (HTW) was done, using a low-alloy RPV steel. 2-5 wppm hydrogen caused embrittlement in air tensile tests at room temperature (25 °C) and at 288 °C, effects being more significant at 25 °C and in simulated weld coarse grain heat affected zone material. Embrittlement at 288 °C is strain rate dependent and is due to localized plastic deformation. Hydrogen pre-charging/HTW exposure did not deteriorate the fracture resistance at 288 °C in base metal, for investigated loading rate range. Clear change in fracture morphology and deformation structures was observed, similar to that after air tests with hydrogen.
Electrical properties of lanthanum chromite based ceramics in hydrogen and oxidizing atmospheres at high temperatures. Final report

DOE Office of Scientific and Technical Information (OSTI.GOV)

Schmidt, V.H.

1981-06-01

Several results regarding the effect of hydrogen on lanthanum chromite were determined. Thermally-activated diffusion of hydrogen through La(Mg)CrO/sub 3/ was found with a high activation energy. It was found that its electrical conductivity drops drastically, especially at low temperature, after exposure to hydrogen at high temperature. Also, the curvature of most of the conductivity plots, as well as the inability to observe the Hall effect, lends support to the proposal by Karim and Aldred that the small-polaron model which predicts thermally activated mobility is applicable to doped lanthanum chromite. From differential thermal analysis an apparent absorption of hydrogen near 300/supmore » 0/C was noticed. Upon cooling the lanthanum chromite in hydrogen and subsequently reheating it in air, desorption occurred near 170/sup 0/C. The immediate purpose of this study was to determine whether hydrogen has a deleterious effect on lanthanum chromite in solid oxide fuel cells.« less
Hydrogen storage and evolution catalysed by metal hydride complexes.

PubMed

Fukuzumi, Shunichi; Suenobu, Tomoyoshi

2013-01-07

The storage and evolution of hydrogen are catalysed by appropriate metal hydride complexes. Hydrogenation of carbon dioxide by hydrogen is catalysed by a [C,N] cyclometalated organoiridium complex, [Ir(III)(Cp*)(4-(1H-pyrazol-1-yl-κN(2))benzoic acid-κC(3))(OH(2))](2)SO(4) [Ir-OH(2)](2)SO(4), under atmospheric pressure of H(2) and CO(2) in weakly basic water (pH 7.5) at room temperature. The reverse reaction, i.e., hydrogen evolution from formate, is also catalysed by [Ir-OH(2)](+) in acidic water (pH 2.8) at room temperature. Thus, interconversion between hydrogen and formic acid in water at ambient temperature and pressure has been achieved by using [Ir-OH(2)](+) as an efficient catalyst in both directions depending on pH. The Ir complex [Ir-OH(2)](+) also catalyses regioselective hydrogenation of the oxidised form of β-nicotinamide adenine dinucleotide (NAD(+)) to produce the 1,4-reduced form (NADH) under atmospheric pressure of H(2) at room temperature in weakly basic water. In weakly acidic water, the complex [Ir-OH(2)](+) also catalyses the reverse reaction, i.e., hydrogen evolution from NADH to produce NAD(+) at room temperature. Thus, interconversion between NADH (and H(+)) and NAD(+) (and H(2)) has also been achieved by using [Ir-OH(2)](+) as an efficient catalyst and by changing pH. The iridium hydride complex formed by the reduction of [Ir-OH(2)](+) by H(2) and NADH is responsible for the hydrogen evolution. Photoirradiation (λ > 330 nm) of an aqueous solution of the Ir-hydride complex produced by the reduction of [Ir-OH(2)](+) with alcohols resulted in the quantitative conversion to a unique [C,C] cyclometalated Ir-hydride complex, which can catalyse hydrogen evolution from alcohols in a basic aqueous solution (pH 11.9). The catalytic mechanisms of the hydrogen storage and evolution are discussed by focusing on the reactivity of Ir-hydride complexes.
Hydrogen production by high-temperature water splitting using electron-conducting membranes

DOEpatents

Lee, Tae H.; Wang, Shuangyan; Dorris, Stephen E.; Balachandran, Uthamalingam

2004-04-27

A device and method for separating water into hydrogen and oxygen is disclosed. A first substantially gas impervious solid electron-conducting membrane for selectively passing hydrogen is provided and spaced from a second substantially gas impervious solid electron-conducting membrane for selectively passing oxygen. When steam is passed between the two membranes at disassociation temperatures the hydrogen from the disassociation of steam selectively and continuously passes through the first membrane and oxygen selectively and continuously passes through the second membrane, thereby continuously driving the disassociation of steam producing hydrogen and oxygen.
Molecular dynamics simulation study of hydrogen bonding in aqueous poly(ethylene oxide) solutions.

PubMed

Smith, G D; Bedrov, D; Borodin, O

2000-12-25

A molecular dynamics simulation study of hydrogen bonding in poly(ethylene oxide) (PEO)/water solutions was performed. PEO-water and water-water hydrogen bonding manifested complex dependence on both composition and temperature. Strong water clustering in concentrated solutions was seen. Saturation of hydrogen bonding at w(p) approximately equal to 0.5 and a dramatic decrease in PEO-water hydrogen bonding with increasing temperature, consistent with experimentally observed closed-loop phase behavior, were observed. Little tendency toward intermolecular bridging of PEO chains by water molecules was seen.
Hydrogen halide cleaning of powder metallurgy nickel-20 chromium-3 thoria.

NASA Technical Reports Server (NTRS)

Herbell, T. P.

1972-01-01

The Cr2O3 content of powder metallurgy nickel-20 chromium-3 thoria was reduced with atmospheres consisting of hydrogen plus hydrogen chloride (HCl) or hydrogen bromide (HBr). The nonthoria oxygen content or 'oxygen excess' was reduced from an initial amount of greater than 50,000 ppm to less than 100 ppm. Low temperatures were effective, but lowest oxygen levels were achieved with the highest cleaning temperature of 1200 C.
Iron-rich clay minerals on Mars - Potential sources or sinks for hydrogen and indicators of hydrogen loss over time

NASA Technical Reports Server (NTRS)

Burt, D. M.

1989-01-01

Although direct evidence is lacking, indirect evidence suggests that iron-rich clay minerals or poorly-ordered chemical equivalents are widespread on the Martian surface. Such clays can act as sources or sinks for hydrogen ('hydrogen sponges'). Ferrous clays can lose hydrogen and ferric clays gain it by the coupled substitution Fe(3+)O(Fe(2+)OH)-1, equivalent to minus atomic H. This 'oxy-clay' substitution involves only proton and electron migration through the crystal structure, and therefore occurs nondestructively and reversibly, at relatively low temperatures. The reversible, low-temperature nature of this reaction contrasts with the irreversible nature of destructive dehydroxylation (H2O loss) suffered by clays heated to high temperatures. In theory, metastable ferric oxy-clays formed by dehydrogenation of ferrous clays over geologic time could, if exposed to water vapor, extract the hydrogen from it, releasing oxygen.
Optimization of hydrogen and syngas production from PKS gasification by using coal bottom ash.

PubMed

Shahbaz, Muhammad; Yusup, Suzana; Inayat, Abrar; Patrick, David Onoja; Pratama, Angga; Ammar, Muhamamd

2017-10-01

Catalytic steam gasification of palm kernel shell is investigated to optimize operating parameters for hydrogen and syngas production using TGA-MS setup. RSM is used for experimental design and evaluating the effect of temperature, particle size, CaO/biomass ratio, and coal bottom ash wt% on hydrogen and syngas. Hydrogen production appears highly sensitive to all factors, especially temperature and coal bottom ash wt%. In case of syngas, the order of parametric influence is: CaO/biomass>coal bottom ash wt%>temperature>particle size. The significant catalytic effect of coal bottom ash is due to the presence of Fe 2 O 3 , MgO, Al 2 O 3 , and CaO. A temperature of 692°C, coal bottom ash wt% of 0.07, CaO/biomass of 1.42, and particle size of 0.75mm are the optimum conditions for augmented yield of hydrogen and syngas. The production of hydrogen and syngas is 1.5% higher in the pilot scale gasifier as compared to TGA-MS setup. Copyright © 2017 Elsevier Ltd. All rights reserved.
Device for staged carbon monoxide oxidation

DOEpatents

Vanderborgh, Nicholas E.; Nguyen, Trung V.; Guante, Jr., Joseph

1993-01-01

A method and apparatus for selectively oxidizing carbon monoxide in a hydrogen rich feed stream. The method comprises mixing a feed stream consisting essentially of hydrogen, carbon dioxide, water and carbon monoxide with a first predetermined quantity of oxygen (air). The temperature of the mixed feed/oxygen stream is adjusted in a first the heat exchanger assembly (20) to a first temperature. The mixed feed/oxygen stream is sent to reaction chambers (30,32) having an oxidation catalyst contained therein. The carbon monoxide of the feed stream preferentially absorbs on the catalyst at the first temperature to react with the oxygen in the chambers (30,32) with minimal simultaneous reaction of the hydrogen to form an intermediate hydrogen rich process stream having a lower carbon monoxide content than the feed stream. The elevated outlet temperature of the process stream is carefully controlled in a second heat exchanger assembly (42) to a second temperature above the first temperature. The process stream is then mixed with a second predetermined quantity of oxygen (air). The carbon monoxide of the process stream preferentially reacts with the second quantity of oxygen in a second stage reaction chamber (56) with minimal simultaneous reaction of the hydrogen in the process stream. The reaction produces a hydrogen rich product stream having a lower carbon monoxide content than the process stream. The product stream is then cooled in a third heat exchanger assembly (72) to a third predetermined temperature. Three or more stages may be desirable, each with metered oxygen injection.
Physical and thermal strain of firefighters according to the firefighting tactics used to suppress wildfires.

PubMed

Rodríguez-Marroyo, J A; Villa, J G; López-Satue, J; Pernía, R; Carballo, B; García-López, J; Foster, C

2011-11-01

The aim of this study was to analyse the physiological strain of firefighters, using heart rate (HR) and core temperature, during real wildfire suppression according to the type of attack performed (direct, indirect or mixed). Three intensity zones were established according to the HR corresponding to the ventilatory threshold (VT) and respiratory compensation threshold (RCT): zone 1, RCT. The exercise workload (training impulse (TRIMP)), the physiological strain index (PSI) and the cumulative heat strain index(CHSI) were calculated using the time spent in each zone, and the HR and core temperature, respectively. Significantly higher mean HR, time spent in Z2 and Z3 and TRIMP h(-1) were found in direct and mixed versus indirect attacks. The highest PSI and CHSI were observed in the direct attack. In conclusion, exercise strain and combined thermal strain, but not core temperature during wildfire suppression, are related to the type of attack performed. STATEMENT OF RELEVANCE: Our findings demonstrated that wildfire firefighting is associated with high physiological demands, which vary significantly depending on the tactics chosen for performing the task. These results should be kept in mind when planning programmes to improve wildland firefighters' physical fitness, which will allow improvement in their performance.
Conversion rate of para-hydrogen to ortho-hydrogen by oxygen: implications for PHIP gas storage and utilization.

PubMed

Wagner, Shawn

2014-06-01

To determine the storability of para-hydrogen before reestablishment of the room temperature thermal equilibrium mixture. Para-hydrogen was produced at near 100% purity and mixed with different oxygen quantities to determine the rate of conversion to the thermal equilibrium mixture of 75: 25% (ortho: para) by detecting the ortho-hydrogen (1)H nuclear magnetic resonance using a 9.4 T imager. The para-hydrogen to ortho-hydrogen velocity constant, k, near room temperature (292 K) was determined to be 8.27 ± 1.30 L/mol · min(-1). This value was calculated utilizing four different oxygen fractions. Para-hydrogen conversion to ortho-hydrogen by oxygen can be minimized for long term storage with judicious removal of oxygen contamination. Prior calculated velocity rates were confirmed demonstrating a dependence on only the oxygen concentration.
Method of gettering hydrogen under conditions of low pressure

DOEpatents

Mendelsohn, M.H.; Gruen, D.M.

1983-08-09

A ternary intermetallic compound having the formula Zr(V[sub 1[minus]x]Cr[sub x])[sub 2] where x is in the range of 0.01 to 0.90 is capable of reversibly sorbing hydrogen at temperatures ranging from room temperature to 200 C, at pressures down to 10[sup [minus]6] Torr. The compound is suitable for use as a hydrogen getter in low pressure, high temperature applications such as magnetic confinement fusion devices. 3 figs.
Effect of fermentation temperature on hydrogen production from cow waste slurry by using anaerobic microflora within the slurry.

PubMed

Yokoyama, Hiroshi; Waki, Miyoko; Moriya, Naoko; Yasuda, Tomoko; Tanaka, Yasuo; Haga, Kiyonori

2007-02-01

We examined hydrogen production from a dairy cow waste slurry (13.4 g of volatile solids per liter) by batch cultures in a temperature range from 37 to 85 degrees C, using microflora naturally present within the slurry. Without the addition of seed bacteria, hydrogen was produced by simply incubating the slurry, using the microflora within the slurry. Interestingly, two peaks of fermentation temperatures for hydrogen production from the slurry were observed at 60 and 75 degrees C (392 and 248 ml H2 per liter of slurry, respectively). After the termination of the hydrogen evolution, the microflora cultured at 60 degrees C displayed hydrogen-consuming activity, but hydrogen-consuming activity of the microflora cultured at 75 degrees C was not detected, at least for 24 days. At both 60 and 75 degrees C, the main by-product was acetate, and the optimum pH of the slurry for hydrogen production was around neutral. Bacteria related to hydrogen-producing moderate and extreme thermophiles, Clostridium thermocellum and Caldanaerobacter subterraneus, were detected in the slurries cultured at 60 and 75 degrees C, respectively, by denaturing gradient gel electrophoresis analyses, using the V3 region of 16S rDNA.
Organic metamorphism in the California petroleum basins; Chapter B, Insights from extractable bitumen and saturated hydrocarbons

USGS Publications Warehouse

Price, Leigh C.

2000-01-01

Seventy-five shales from the Los Angeles, Ventura, and Southern San Joaquin Valley Basins were extracted and analyzed. Samples were chosen on the basis of ROCK-EVAL analyses of a much larger sample base. The samples ranged in burial temperatures from 40 ? to 220 ? C, and contained hydrogen-poor to hydrogen-rich organic matter (OM), based on OM visual typing and a correlation of elemental kerogen hydrogen to carbon ratios with ROCK-EVAL hydrogen indices. By extractable bitumen measurements, rocks with hydrogen- poor OM in the Los Angeles Basin began mainstage hydrocarbon (HC) generation by 90 ? C. The HC concentrations maximized by 165 ? C, and beyond 165 ? C, HC and bitumen concentrations and ROCK-EVAL hydrogen indices all began decreasing to low values reached by 220 ? C, where HC generation was largely complete. Rocks with hydrogen-poor OM in the Southern San Joaquin Valley Basin commenced mainstage HC generation at 135 ? C and HC concentrations maximized by 180 ? C. Above 180 ? C, HC and bitumen concentrations and ROCK-EVAL hydrogen indices all decreased to low values reached by 214 ? C, again the process of HC generation being largely complete. In both cases, bell-shaped HC-generation curves were present versus depth (burial temperature). Mainstage HC generation had not yet begun in Ventura Basin rocks with hydrogen-poor OM by 140 ? C. The apparent lower temperature for initiation of mainstage generation in the Los Angeles Basin is attributed to very recent cooling in that basin from meteoric-water flow. Thus, HC generation there most probably occurred at higher burial temperatures. In contrast, mainstage HC generation, and all aspects of organic metamorphism, were strongly suppressed in rocks with hydrogen-rich OM at temperatures as high as 198 ? C. For example, shales from the Wilmington field (Los Angeles Basin) from 180 ? to 198 ? C retained ROCK-EVAL hydrogen indices of 550- 700 and had saturated-HC coefficients of only 4-15 mg/g organic carbon. The rocks with hydrogen-rich OM were subjected to the same burial conditions as the rocks with hydrogenpoor OM. We attribute this suppression of organic metamorphism in this study primarily to much stronger bonds in the hydrogen-rich OM compared to the bonds in hydrogen-poor OM. Trends in bitumen compositions (qualitative characteristics) versus burial temperature were also very different for rocks with hydrogen-poor OM compared to that in rocks with hydrogen- rich OM. This observation demonstrated that the two OM types also had significantly different reaction pathways, in addition to different reaction kinetics. Strong exploration implications arise from these observations. Above 40?C, but before mainstage HC generation, a lowtemperature (pre-mainstage) HC generation occurred in all rocks, and all OM types, studied. This low-temperature generation resulted in significant qualitative changes in the bitumen and HCS (hydrocarbons) from rocks of all OM types, especially in rocks with hydrogen-rich OM, from 40 ? to 70 ? C. This, and previous studies, document that very high carbon-normalized concentrations of indigenous bitumen and HCS occur in late Neogene immature rocks of any OM type in all southern California basins. This characteristic is attributed to the low-temperature generation occurring in both sulfur-poor and sulfur-rich kerogens, which originally had unusually high concentrations of weak (15-40 Kcal/mole) bonds. These observations and considerations have marked relevance to exploration regarding the possible formation of commercial oil deposits at immature ranks in these basins. Other significant geochemical observations also result from this study.
Hydrogen isotope separation using molecular sieve of synthetic zeolite 3A

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kotoh, K.; Kimura, K.; Nakamura, Y.

2008-07-15

It is known that hydrogen isotope molecules can be adsorbed easily onto synthetic zeolite 4A, 5A, and 13X at the liquid-nitrogen temperature of 77.4 K. We show here that hydrogen and deuterium are not adsorptive onto zeolite 3A at the same temperature. This phenomenon is explained by assuming the molecular sieve function in zeolite-3A-crystalline lattice structure. From a series of pseudo-isobaric experiments, it is also shown that the sieving phenomenon appears in a range above 77.4 K. This behavior is interpreted as resulting on the dependence of sieve's mesh size on temperature, where the sieving effect is considered to appearmore » at a certain temperature. In this interpretation, an isotopic difference between hydrogen and deuterium is suggested to exist in the sieving effect appearance temperatures. This is endorsed in the result of pseudo-isobaric experiments. This temperature deference is very significant because that indicates the possibility of an effective method of hydrogen isotope separation. This possibility is verified through an experimental series of adsorption-desorption with a mixture of H{sub 2} and D{sub 2}, where the gas samples adsorbed through the sieve operated at intentionally selected temperatures are isolated and then analyzed. The result demonstrates remarkable values of isotope separation factor. (authors)« less

Large Scale Production of Densified Hydrogen Using Integrated Refrigeration and Storage

NASA Technical Reports Server (NTRS)

Notardonato, William U.; Swanger, Adam Michael; Jumper, Kevin M.; Fesmire, James E.; Tomsik, Thomas M.; Johnson, Wesley L.

2017-01-01

Recent demonstration of advanced liquid hydrogen storage techniques using Integrated Refrigeration and Storage (IRAS) technology at NASA Kennedy Space Center led to the production of large quantities of solid densified liquid and slush hydrogen in a 125,000 L tank. Production of densified hydrogen was performed at three different liquid levels and LH2 temperatures were measured by twenty silicon diode temperature sensors. System energy balances and solid mass fractions are calculated. Experimental data reveal hydrogen temperatures dropped well below the triple point during testing (up to 1 K), and were continuing to trend downward prior to system shutdown. Sub-triple point temperatures were seen to evolve in a time dependent manner along the length of the horizontal, cylindrical vessel. Twenty silicon diode temperature sensors were recorded over approximately one month for testing at two different fill levels (33 67). The phenomenon, observed at both two fill levels, is described and presented detailed and explained herein., and The implications of using IRAS for energy storage, propellant densification, and future cryofuel systems are discussed.
Influence of temperature changes on migraine occurrence in Germany

NASA Astrophysics Data System (ADS)

Scheidt, Jörg; Koppe, Christina; Rill, Sven; Reinel, Dirk; Wogenstein, Florian; Drescher, Johannes

2013-07-01

Many factors trigger migraine attacks. Weather is often reported to be one of the most common migraine triggers. However, there is little scientific evidence about the underlying mechanisms and causes. In our pilot study, we used smartphone apps and a web form to collect around 4,700 migraine messages in Germany between June 2011 and February 2012. Taking interdiurnal temperature changes as an indicator for changes in the prevailing meteorological conditions, our analyses were focused on the relationship between temperature changes and the frequency of occurrence of migraine attacks. Linear trends were fitted to the total number of migraine messages with respect to temperature changes. Statistical and systematic errors were estimated. Both increases and decreases in temperature lead to a significant increase in the number of migraine messages. A temperature increase (decrease) of 5 °C resulted in an increase of 19 ± 7 % (24 ± 8 %) in the number of migraine messages.
Fractographic analysis of gaseous hydrogen induced cracking in 18Ni maraging steel

NASA Technical Reports Server (NTRS)

Gangloff, R. P.; Wei, R. P.

1978-01-01

Electron microscope fractographic analysis supplemented an extensive study of the kinetics of gaseous hydrogen assisted cracking in 18Ni maraging steel. Temperature determined the crack path morphology in each steel which, in turn, was directly related to the temperature dependence of the crack growth rate. Crack growth in the low temperature regime proceeded along prior austenite grain boundaries. Increasing the temperature above a critical value produced a continuously increasing proportion of transgranular quasi-cleavage associated with lath martensite boundaries. The amount of transgranular cracking was qualitatively correlated with the degree of temperature-induced deviation from Arrhenius behavior. Fractographic observations are interpreted in terms of hypothesized mechanisms for gaseous hydrogen embrittlement. It is concluded that hydrogen segregation to prior austenite and lath martensite boundaries must be considered as a significant factor in developing mechanisms for gaseous embrittlement of high strength steels.
Method to Improve Indium Bump Bonding via Indium Oxide Removal Using a Multi-Step Plasma Process

NASA Technical Reports Server (NTRS)

Dickie, Matthew R. (Inventor); Nikzad, Shouleh (Inventor); Greer, H. Frank (Inventor); Jones, Todd J. (Inventor); Vasquez, Richard P. (Inventor); Hoenk, Michael E. (Inventor)

2012-01-01

A process for removing indium oxide from indium bumps in a flip-chip structure to reduce contact resistance, by a multi-step plasma treatment. A first plasma treatment of the indium bumps with an argon, methane and hydrogen plasma reduces indium oxide, and a second plasma treatment with an argon and hydrogen plasma removes residual organics. The multi-step plasma process for removing indium oxide from the indium bumps is more effective in reducing the oxide, and yet does not require the use of halogens, does not change the bump morphology, does not attack the bond pad material or under-bump metallization layers, and creates no new mechanisms for open circuits.
Searching for magnetism in hydrogenated graphene: using highly hydrogenated graphene prepared via Birch reduction of graphite oxides.

PubMed

Eng, Alex Yong Sheng; Poh, Hwee Ling; Šaněk, Filip; Maryško, Miroslav; Matějková, Stanislava; Sofer, Zdeněk; Pumera, Martin

2013-07-23

Fully hydrogenated graphene (graphane) and partially hydrogenated graphene materials are expected to possess various fundamentally different properties from graphene. We have prepared highly hydrogenated graphene containing 5% wt of hydrogen via Birch reduction of graphite oxide using elemental sodium in liquid NH3 as electron donor and methanol as proton donor in the reduction. We also investigate the influence of preparation method of graphite oxide, such as the Staudenmaier, Hofmann or Hummers methods on the hydrogenation rate. A control experiment involving NaNH2 instead of elemental Na was also performed. The materials were characterized in detail by electron microscopy, infrared spectroscopy, X-ray photoelectron spectroscopy, Raman spectroscopy both at room and low temperatures, X-ray fluorescence spectroscopy, inductively coupled plasma optical emission spectroscopy, combustible elemental analysis and electrical resistivity measurements. Magnetic measurements are provided of bulk quantities of highly hydrogenated graphene. In the whole temperature range up to room temperature, the hydrogenated graphene exhibits a weak ferromagnetism in addition to a contribution proportional to field that is caused not only by diamagnetism but also likely by an antiferromagnetic influence. The origin of the magnetism is also determined to arise from the hydrogenated graphene itself, and not as a result of any metallic impurities.
Measurement of hydrogen solubility and desorption rate in V-4Cr-4Ti and liquid lithium-calcium alloys

DOE Office of Scientific and Technical Information (OSTI.GOV)

Park, J.H.; Erck, R.; Park, E.T.

1997-04-01

Hydrogen solubility in V-4Cr-4Ti and liquid lithium-calcium was measured at a hydrogen pressure of 9.09 x 10{sup {minus}4} torr at temperatures between 250 and 700{degrees}C. Hydrogen solubility in V-4Cr-4Ti and liquid lithium decreased with temperature. The measured desorption rate of hydrogen in V-4Cr-4Ti is a thermally activated process; the activation energy is 0.067 eV. Oxygen-charged V-4Cr-4Ti specimens were also investigated to determine the effect of oxygen impurity on hydrogen solubility and desorption in the alloy. Oxygen in V-4Cr-4Ti increases hydrogen solubility and desorption kinetics. To determine the effect of a calcium oxide insulator coating on V-4Cr-4Ti, hydrogen solubility in lithium-calciummore » alloys that contained 0-8.0 percent calcium was also measured. The distribution ratio R of hydrogen between liquid lithium or lithium-calcium and V-4Cr-4Ti increased as temperature decreased (R {approx} 10 and 100 at 700 and 250{degrees}C, respectively). However at <267{degrees}C, solubility data could not be obtained by this method because of the slow kinetics of hydrogen permeation through the vanadium alloy.« less
Hydrogen storage and hydrolysis properties of core-shell structured Mg-MFx (M=V, Ni, La and Ce) nano-composites prepared by arc plasma method

NASA Astrophysics Data System (ADS)

Mao, Jianfeng; Zou, Jianxin; Lu, Chong; Zeng, Xiaoqin; Ding, Wenjiang

2017-10-01

In this work, core-shell structured Mg-MFx (M = V, Ni, La and Ce) nano-composites are prepared by using arc plasma method. The particle size distribution, phase components, microstructures, hydrogen sorption properties of these composites and hydrolysis properties of their corresponding hydrogenated powders are carefully investigated. It is shown that the addition of MFx through arc plasma method can improve both the hydrogen absorption kinetics of Mg and the hydrolysis properties of corresponding hydrogenated powders. Among them, the Mg-NiF2 composite shows the best hydrogen absorption properties at relatively low temperatures, which can absorb 3.26 wt% of H2 at 373 K in 2 h. Such rapid hydrogen absorption rate is mainly due to the formation of Mg2Ni and MgF2 on Mg particles during arc evaporation and condensation. In contrast, measurements also show that the hydrogenated Mg-VF3 composite has the lowest peak desorption temperature and the fastest hydrolysis rate among all the hydrogenated Mg-MFx composites. The less agglomeration tendency of Mg particles and VO2 covered on MgH2 particles account for the reduced hydrogen desorption temperature and enhanced hydrolysis rate.
Significant Quantum Effects in Hydrogen Activation

DOE PAGES

Kyriakou, Georgios; Davidson, Erlend R. M.; Peng, Guowen; ...

2014-03-31

Dissociation of molecular hydrogen is an important step in a wide variety of chemical, biological, and physical processes. Due to the light mass of hydrogen, it is recognized that quantum effects are often important to its reactivity. However, understanding how quantum effects impact the reactivity of hydrogen is still in its infancy. Here, we examine this issue using a well-defined Pd/Cu(111) alloy that allows the activation of hydrogen and deuterium molecules to be examined at individual Pd atom surface sites over a wide range of temperatures. Experiments comparing the uptake of hydrogen and deuterium as a function of temperature revealmore » completely different behavior of the two species. The rate of hydrogen activation increases at lower sample temperature, whereas deuterium activation slows as the temperature is lowered. Density functional theory simulations in which quantum nuclear effects are accounted for reveal that tunneling through the dissociation barrier is prevalent for H 2 up to ~190 K and for D 2 up to ~140 K. Kinetic Monte Carlo simulations indicate that the effective barrier to H 2 dissociation is so low that hydrogen uptake on the surface is limited merely by thermodynamics, whereas the D 2 dissociation process is controlled by kinetics. These data illustrate the complexity and inherent quantum nature of this ubiquitous and seemingly simple chemical process. Here, examining these effects in other systems with a similar range of approaches may uncover temperature regimes where quantum effects can be harnessed, yielding greater control of bond-breaking processes at surfaces and uncovering useful chemistries such as selective bond activation or isotope separation.« less
Highly hydrogenated graphene via active hydrogen reduction of graphene oxide in the aqueous phase at room temperature.

PubMed

Sofer, Zdeněk; Jankovský, Ondřej; Šimek, Petr; Soferová, Lýdie; Sedmidubský, David; Pumera, Martin

2014-02-21

Hydrogenated graphene and graphane are in the forefront of graphene research. Hydrogenated graphene is expected to exhibit ferromagnetism, tunable band gap, fluorescence, and high thermal and low electrical conductivity. Currently available techniques for fabrication of highly hydrogenated graphene use either a liquid ammonia (-33 °C) reduction pathway using alkali metals or plasma low pressure or ultra high pressure hydrogenation. These methods are either technically challenging or pose inherent risks. Here we wish to demonstrate that highly hydrogenated graphene can be prepared at room temperature in the aqueous phase by reduction of graphene oxide by nascent hydrogen generated by dissolution of metal in acid. Nascent hydrogen is known to be a strong reducing agent. We studied the influence of metal involved in nascent hydrogen generation and characterized the samples in detail. The resulting reduced graphenes and hydrogenated graphenes were characterized in detail. The resulting hydrogenated graphene had the chemical formula C1.16H1O0.66. Such simple hydrogenation of graphene is of high importance for large scale safe synthesis of hydrogenated graphene.
High performance hydrogen storage from Be-BTB metal-organic framework at room temperature.

PubMed

Lim, Wei-Xian; Thornton, Aaron W; Hill, Anita J; Cox, Barry J; Hill, James M; Hill, Matthew R

2013-07-09

The metal-organic framework beryllium benzene tribenzoate (Be-BTB) has recently been reported to have one of the highest gravimetric hydrogen uptakes at room temperature. Storage at room temperature is one of the key requirements for the practical viability of hydrogen-powered vehicles. Be-BTB has an exceptional 298 K storage capacity of 2.3 wt % hydrogen. This result is surprising given that the low adsorption enthalpy of 5.5 kJ mol(-1). In this work, a combination of atomistic simulation and continuum modeling reveals that the beryllium rings contribute strongly to the hydrogen interaction with the framework. These simulations are extended with a thermodynamic energy optimization (TEO) model to compare the performance of Be-BTB to a compressed H2 tank and benchmark materials MOF-5 and MOF-177 in a MOF-based fuel cell. Our investigation shows that none of the MOF-filled tanks satisfy the United States Department of Energy (DOE) storage targets within the required operating temperatures and pressures. However, the Be-BTB tank delivers the most energy per volume and mass compared to the other material-based storage tanks. The pore size and the framework mass are shown to be contributing factors responsible for the superior room temperature hydrogen adsorption of Be-BTB.
DOE Office of Scientific and Technical Information (OSTI.GOV)

Huang, Huogen; Chen, Liang

Ti-Zr-Ni quasicrystals have been demonstrated to store a large number of hydrogen atoms, which implies strong potential application in hydrogen energy field for them. However, the desorption of hydrogen atoms in the quasicrystals is quite difficult, with the indication of high desorption temperature and slow desorption rate. The shortage limits their use in the field to a large extent. But this kind of quasicrystals might be used in nuclear fusion energy field, because tritium as a coral fuel for nuclear fusion needs tight storage. However, equilibrium pressure at room temperature of Ti-Zr-Ni quasicrystals, important for their application in fusion energymore » field, has not been clear yet. In this work, we designed a gas-solid reaction system with the pressure resolution of 10{sup −8}Pa and carried out hydrogen desorption investigation at different temperatures on Ti{sub 36}Zr{sub 40}Ni{sub 20}Pd{sub 4} icosahedral quasicrystal. Based on three Pressure-Composition-Temperature desorption curves, we speculate according to Van’t Hoff theory about hydrogen storage that its equilibrium pressure at room temperature could be at the magnitude of 10{sup −6}Pa, displaying good stability of hydrogen in the quasicrystal and also implying application prospects in fusion energy field for quasicrystals of this type.« less
Hydrogen production with coal using a pulverization device

DOEpatents

Paulson, Leland E.

1989-01-01

A method for producing hydrogen from coal is described wherein high temperature steam is brought into contact with coal in a pulverizer or fluid energy mill for effecting a steam-carbon reaction to provide for the generation of gaseous hydrogen. The high temperature steam is utilized to drive the coal particles into violent particle-to-particle contact for comminuting the particulates and thereby increasing the surface area of the coal particles for enhancing the productivity of the hydrogen.
High temperature decomposition of hydrogen peroxide

NASA Technical Reports Server (NTRS)

Parrish, Clyde F. (Inventor)

2005-01-01

Nitric oxide (NO) is oxidized into nitrogen dioxide (NO2) by the high temperature decomposition of a hydrogen peroxide solution to produce the oxidative free radicals, hydroxyl and hydroperoxyl. The hydrogen peroxide solution is impinged upon a heated surface in a stream of nitric oxide where it decomposes to produce the oxidative free radicals. Because the decomposition of the hydrogen peroxide solution occurs within the stream of the nitric oxide, rapid gas-phase oxidation of nitric oxide into nitrogen dioxide occurs.
High Temperature Decomposition of Hydrogen Peroxide

NASA Technical Reports Server (NTRS)

Parrish, Clyde F. (Inventor)

2004-01-01

Nitric oxide (NO) is oxidized into nitrogen dioxide (NO2) by the high temperature decomposition of a hydrogen peroxide solution to produce the oxidative free radicals, hydroxyl and hydropemxyl. The hydrogen peroxide solution is impinged upon a heated surface in a stream of nitric oxide where it decomposes to produce the oxidative free radicals. Because the decomposition of the hydrogen peroxide solution occurs within the stream of the nitric oxide, rapid gas-phase oxidation of nitric oxide into nitrogen dioxide occurs.
Positron Spectroscopy of Nanodiamonds after Hydrogen Sorption

PubMed Central

Laptev, Roman; Abzaev, Yuri; Lider, Andrey; Ivashutenko, Alexander

2018-01-01

The structure and defects of nanodiamonds influence the hydrogen sorption capacity. Positronium can be used as a sensor for detecting places with the most efficient capture of hydrogen atoms. Hydrogenation of carbon materials was performed from gas atmosphere. The concentration of hydrogen absorbed by the sample depends on the temperature and pressure. The concentration 1.2 wt % is achieved at the temperature of 243 K and the pressure of 0.6 MPa. The hydrogen saturation of nanodiamonds changes the positron lifetime. Increase of sorption cycle numbers effects the positron lifetime, as well as the parameters of the Doppler broadening of annihilation line. The electron-positron annihilation being a sensitive method, it allows detecting the electron density fluctuation of the carbon material after hydrogen saturation. PMID:29324712
DOE Office of Scientific and Technical Information (OSTI.GOV)

Sun, Pei; Fang, Z. Zak; Koopman, Mark

Hydrogen has been investigated for decades as a temporary alloying element to refine the microstructure of Ti-6Al-4V, and is now being used in a novel powder metallurgy method known as "hydrogen sintering and phase transformation". Pseudo-binary phase diagrams of (Ti-6Al-4V)-xH have been studied and developed, but are not well established due to methodological limitations. In this paper, in situ studies of phase transformations during hydrogenation and dehydrogenation of (Ti-6Al-4V)-xH alloys were conducted using high-energy synchrotron X-ray diffraction (XRD), thermogravimetric analysis (TGA) and differential scanning calorimetry (DSC). The eutectoid phase transformation of β ↔ α + δ was observed in themore » (Ti-6Al-4V)-xH alloy via in situ synchrotron XRD at 211 °C with a hydrogen concentration of 37.5 at.% (measured using TGA-DSC). The relationships of hydrogen composition to partial pressure and temperature were investigated in the temperature range 450-900°C. Based on these results, a partial pseudo-binary phase diagram of (Ti-6Al-4V)-xH is proposed for hydrogen compositions up to 60 at.% in the temperature range 100-900°C. Using the data collected in real time under controlled parameters of temperature, composition and hydrogen partial pressure, this work characterizes relevant phase transformations and microstructural evolution for practical titanium-hydrogen technologies of Ti-6Al-4V.« less
The role of Hydrogen and Creep in Intergranular Stress Corrosion Cracking of Alloy 600 and Alloy 690 in PWR Primary Water Environments ? a Review

DOE Office of Scientific and Technical Information (OSTI.GOV)

Rebak, R B; Hua, F H

2004-07-12

Intergranular attack (IGA) and intergranular stress corrosion cracking (IGSCC) of Alloy 600 in PWR steam generator environment has been extensively studied for over 30 years without rendering a clear understanding of the essential mechanisms. The lack of understanding of the IGSCC mechanism is due to a complex interaction of numerous variables such as microstructure, thermomechanical processing, strain rate, water chemistry and electrochemical potential. Hydrogen plays an important role in all these variables. The complexity, however, significantly hinders a clearer and more fundamental understanding of the mechanism of hydrogen in enhancing intergranular cracking via whatever mechanism. In this work, an attemptmore » is made to review the role of hydrogen based on the current understanding of grain boundary structure and chemistry and intergranular fracture of nickel alloys, effect of hydrogen on electrochemical behavior of Alloy 600 and Alloy 690 (e.g. the passive film stability, polarization behavior and open-circuit potential) and effect of hydrogen on PWSCC behavior of Alloy 600 and Alloy 690. Mechanistic studies on the PWSCC are briefly reviewed. It is concluded that further studies on the role of hydrogen on intergranular cracking in both inert and primary side environments are needed. These studies should focus on the correlation of the results obtained at different laboratories by different methods on materials with different metallurgical and chemical parameters.« less
Hydrogen Storage in metal-modified single-walled carbon nanotubes

DOE Office of Scientific and Technical Information (OSTI.GOV)

Dr. Ahn

2004-04-30

It has been known for over thirty years that potassium-intercalated graphites can readily adsorb and desorb hydrogen at {approx}1 wt% at 77 K. These levels are much higher than can be attained in pure graphite, owing to a larger thermodynamic enthalpy of adsorption. This increased enthalpy may allow hydrogen sorption at higher temperatures. Potassium has other beneficial effects that enable the design of a new material: (a) Increased adsorption enthalpy in potassium-intercalated graphite compared to pure graphite reduces the pressure and increases the temperature required for a given fractional coverage of hydrogen adsorption. We expect the same effects in potassium-intercalatedmore » SWNTs. (b) As an intercalant, potassium separates c-axis planes in graphite. Potassium also separates the individual tubes of SWNTs ropes producing swelling and increased surface area. Increased surface area provides more adsorption sites, giving a proportionately higher capacity. The temperature of adsorption depends on the enthalpy of adsorption. The characteristic temperature is roughly the adsorption enthalpy divided by Boltzmann's constant, k{sub B}. For the high hydrogen storage capacity of SWNTs to be achieved at room temperature, it is necessary to increase the enthalpy of adsorption. Our goal for this project was to use metal modifications to the carbon surface of SWNTs in order to address both enhanced adsorption and surface area. For instance, the enthalpy of sorption of hydrogen on KC8 is 450 meV/H{sub 2}, whereas it is 38 meV/H{sub 2} for unmodified SWNTs. By adsorption thermodynamics we expect approximately that the same performance of SWNTs at 77 K will be achieved at a temperature of [450/38] 77 K = 900 K. This is a high temperature, so we expect that adsorption on nearly all the available sites for hydrogen will occur at room temperature under a much lower pressure. This pressure can be estimated conveniently, since the chemical potential of hydrogen is approximately proportional to the logarithm of the pressure. Using 300 K for room temperature, the 100 bar pressure requirement is reduced to exp(-900/300) 100 bar = 5 bar at room temperature. This is in the pressure range used for prior experimental work such as that of Colin and Herold in the late 1960's and early 1970's.« less
Survey of Hydrogen Combustion Properties

NASA Technical Reports Server (NTRS)

Drell, Isadore L; Belles, Frank E

1958-01-01

This literature digest of hydrogen-air combustion fundamentals presents data on flame temperature, burning velocity, quenching distance, flammability limits, ignition energy, flame stability, detonation, spontaneous ignition, and explosion limits. The data are assessed, recommended values are given, and relations among various combustion properties are discussed. New material presented includes: theoretical treatment of variation in spontaneous ignition lag with temperature, pressure, and composition, based on reaction kinetics of hydrogen-air composition range for 0.01 to 100 atmospheres and initial temperatures of 0 degrees to 1400 degrees k.
Supercritical water gasification of landfill leachate for hydrogen production in the presence and absence of alkali catalyst.

PubMed

Weijin, Gong; Binbin, Li; Qingyu, Wang; Zuohua, Huang; Liang, Zhao

2018-03-01

Gasification of landfill leachate in supercritical water using batch-type reactor is investigated. Alkali such as NaOH, KOH, K 2 CO 3 , Na 2 CO 3 is used as catalyst. The effect of temperature (380-500 °C), retention time (5-25 min), landfill leachate concentration (1595 mg L -1 -15,225 mg L -1 ), catalyst adding amount (1-10 wt%) on hydrogen mole fraction, hydrogen yield, carbon gasification rate, COD, TOC, TN removal efficiency are investigated. The results showed that gaseous products mainly contained hydrogen, methane, carbon dioxide and carbon monoxide without addition of catalyst. However, the main gaseous products are hydrogen and methane with addition of NaOH, KOH, K 2 CO 3 , Na 2 CO 3 . In the absence of alkali catalyst, the effect of temperature on landfill leachate gasification is positive. Hydrogen mole fraction, hydrogen yield, carbon gasification ratio increase with temperature, which maximum value being 55.6%, 107.15 mol kg -1 , 71.96% is obtained at 500 °C, respectively. Higher raw landfill leachate concentration leads to lower hydrogen production and carbon gasification rate. The suitable retention time is suggested to be 15 min for higher hydrogen production and carbon gasification rate. COD, TOC and TN removal efficiency also increase with increase of temperature, decrease of landfill leachate concentration. In the presence of catalyst, the hydrogen production is obviously promoted by addition of alkali catalyst. the effect of catalysts on hydrogen production is in the following order: NaOH ＞ KOH ＞ Na 2 CO 3  ＞ K 2 CO 3 . The maximum hydrogen mole fraction and hydrogen yield being 74.40%, 70.05 mol kg -1 is obtained with adding amount of 5 wt% NaOH at 450 °C, 28 MPa, 15 min. Copyright © 2017. Published by Elsevier Ltd.

Fracture toughness of Alloy 690 and EN52 weld in air and water

DOE Office of Scientific and Technical Information (OSTI.GOV)

Brown, C.M.; Mills, W.J.

1999-06-01

The effect of low and high temperature water with high hydrogen on the fracture toughness of Alloy 690 and its weld, EN52, was characterized using elastic-plastic J{sub IC} methodology. While both materials display excellent fracture resistance in air and elevated temperature (>93 C) water, a dramatic degradation in toughness is observed in 54 C water. The loss of toughness is associated with a hydrogen-induced intergranular cracking mechanism where hydrogen is picked up from the water. Comparison of the cracking behavior in low temperature water with that for hydrogen-precharged specimens tested in air indicates that the critical local hydrogen content requiredmore » to cause low temperature embrittlement is on the order of 120 to 160 ppm. Loading rate studies show that the cracking resistance is significantly improved at rates above ca. 1000 MPa{radical}m/h because there is insufficient time to produce grain boundary embrittlement. Electron fractographic examinations were performed to correlate cracking behavior with microstructural features and operative fracture mechanics.« less
Fracture toughness of alloy 690 and EN52 welds in air and water

NASA Astrophysics Data System (ADS)

Brown, C. M.; Mills, W. J.

2002-06-01

The effect of low- and high-temperature water with high hydrogen on the fracture toughness of alloy 690 and its weld, EN52, was characterized using elastic-plastic J IC methodology. While both materials display excellent fracture resistance in air and elevated-temperature (>93 °C) water, a dramatic degradation in toughness is observed in 54 °C water. The loss of toughness is associated with a hydrogen-induced intergranular cracking mechanism, where hydrogen is picked up from the water. Comparison of the cracking behavior in low-temperature water with that for hydrogen-precharged specimens tested in air indicates that the critical local hydrogen content required to cause low-temperature embrittlement is on the order of 120 to 160 ppm. Loading-rate studies show that cracking resistance is improved at rates above ˜ 1000 MPa √m/h, because there is insufficient time to produce grain-boundary embrittlement. Electron fractographic examinations were performed to correlate cracking behavior with microstructural features and operative fracture mechanisms.
Determination of diffusion coefficients of hydrogen and deuterium in Zr-2.5%Nb pressure tube material using hot vacuum extraction-quadrupole mass spectrometry

NASA Astrophysics Data System (ADS)

Shrivastava, Komal Chandra; Kulkarni, A. S.; Ramanjaneyulu, P. S.; Sunil, Saurav; Saxena, M. K.; Singh, R. N.; Tomar, B. S.; Ramakumar, K. L.

2015-06-01

The diffusion coefficients of hydrogen and deuterium in Zr-2.5%Nb alloy were measured in the temperature range 523 to 673 K, employing hot vacuum extraction-quadrupole mass spectrometry (HVE-QMS). One end of the Zr-2.5%Nb alloy specimens was charged electrolytically with the desired hydrogen isotope. After annealing at different temperatures for a predetermined time, the specimens were cut into thin slices, which were analyzed for their H2/D2 content using the HVE-QMS technique. The depth profile data were fitted into the equation representing the solution of Fick's second law of diffusion. The activation energy of hydrogen/deuterium diffusion was obtained from the Arrhenius relation between the diffusion coefficient and temperature. The temperature dependent diffusion coefficient can be represented as DH = 1.41 × 10-7 exp(-36,000/RT) and DD = 6.16 × 10-8 exp(-35,262/RT) for hydrogen and deuterium, respectively.
Conceptual Design of Low-Temperature Hydrogen Production and High-Efficiency Nuclear Reactor Technology

NASA Astrophysics Data System (ADS)

Fukushima, Kimichika; Ogawa, Takashi

Hydrogen, a potential alternative energy source, is produced commercially by methane (or LPG) steam reforming, a process that requires high temperatures, which are produced by burning fossil fuels. However, as this process generates large amounts of CO2, replacement of the combustion heat source with a nuclear heat source for 773-1173K processes has been proposed in order to eliminate these CO2 emissions. In this paper, a novel method of nuclear hydrogen production by reforming dimethyl ether (DME) with steam at about 573K is proposed. From a thermodynamic equilibrium analysis of DME steam reforming, the authors identified conditions that provide high hydrogen production fraction at low pressure and temperatures of about 523-573K. By setting this low-temperature hydrogen production process upstream from a turbine and nuclear reactor at about 573K, the total energy utilization efficiency according to equilibrium mass and heat balance analysis is about 50%, and it is 75%for a fast breeder reactor (FBR), where turbine is upstream of the reformer.
High speed hydrogen/graphite interaction

NASA Technical Reports Server (NTRS)

Kelly, A. J.; Hamman, R.; Sharma, O. P.; Harrje, D. T.

1974-01-01

Various aspects of a research program on high speed hydrogen/graphite interaction are presented. Major areas discussed are: (1) theoretical predictions of hydrogen/graphite erosion rates; (2) high temperature, nonequilibrium hydrogen flow in a nozzle; and (3) molecular beam studies of hydrogen/graphite erosion.
Hydrogen separation process

DOEpatents

Mundschau, Michael [Longmont, CO; Xie, Xiaobing [Foster City, CA; Evenson, IV, Carl; Grimmer, Paul [Longmont, CO; Wright, Harold [Longmont, CO

2011-05-24

A method for separating a hydrogen-rich product stream from a feed stream comprising hydrogen and at least one carbon-containing gas, comprising feeding the feed stream, at an inlet pressure greater than atmospheric pressure and a temperature greater than 200.degree. C., to a hydrogen separation membrane system comprising a membrane that is selectively permeable to hydrogen, and producing a hydrogen-rich permeate product stream on the permeate side of the membrane and a carbon dioxide-rich product raffinate stream on the raffinate side of the membrane. A method for separating a hydrogen-rich product stream from a feed stream comprising hydrogen and at least one carbon-containing gas, comprising feeding the feed stream, at an inlet pressure greater than atmospheric pressure and a temperature greater than 200.degree. C., to an integrated water gas shift/hydrogen separation membrane system wherein the hydrogen separation membrane system comprises a membrane that is selectively permeable to hydrogen, and producing a hydrogen-rich permeate product stream on the permeate side of the membrane and a carbon dioxide-rich product raffinate stream on the raffinate side of the membrane. A method for pretreating a membrane, comprising: heating the membrane to a desired operating temperature and desired feed pressure in a flow of inert gas for a sufficient time to cause the membrane to mechanically deform; decreasing the feed pressure to approximately ambient pressure; and optionally, flowing an oxidizing agent across the membrane before, during, or after deformation of the membrane. A method of supporting a hydrogen separation membrane system comprising selecting a hydrogen separation membrane system comprising one or more catalyst outer layers deposited on a hydrogen transport membrane layer and sealing the hydrogen separation membrane system to a porous support.
MEMS based highly sensitive dual FET gas sensor using graphene decorated Pd-Ag alloy nanoparticles for H2 detection.

PubMed

Sharma, Bharat; Kim, Jung-Sik

2018-04-12

A low power, dual-gate field-effect transistor (FET) hydrogen gas sensor with graphene decorated Pd-Ag for hydrogen sensing applications was developed. The FET hydrogen sensor was integrated with a graphene-Pd-Ag-gate FET (GPA-FET) as hydrogen sensor coupled with Pt-gate FET as a reference sensor on a single sensor platform. The sensing gate electrode was modified with graphene by an e-spray technique followed by Pd-Ag DC/MF sputtering. Morphological and structural properties were studied by FESEM and Raman spectroscopy. FEM simulations were performed to confirm the uniform temperature control at the sensing gate electrode. The GPA-FET showed a high sensing response to hydrogen gas at the temperature of 25~254.5 °C. The as-proposed FET H 2 sensor showed the fast response time and recovery time of 16 s, 14 s, respectively at the operating temperature of 245 °C. The variation in drain current was positively related with increased working temperature and hydrogen concentration. The proposed dual-gate FET gas sensor in this study has potential applications in various fields, such as electronic noses and automobiles, owing to its low-power consumption, easy integration, good thermal stability and enhanced hydrogen sensing properties.
Resistivity behavior of hydrogen and liquid silane at high shock compression

NASA Astrophysics Data System (ADS)

Wang, Yi-Gao; Liu, Fu-Sheng; Liu, Qi-Jun

2018-07-01

To study the electrical properties of hydrogen rich compounds under extreme conditions, the electrical resistivity of density hydrogen and silane fluid was measured, respectively. The hydrogen sample was prepared by compressing pure hydrogen gas to 10 MPa in a coolant target system at the temperature of 77 K. The silane sample can be obtained with the same method. High-pressure and high-temperature experiments were performed using a two-stage light-gas gun. The electrical resistivity of the sample decreased with increasing pressure and temperature as expected. A minimum electrical resistivity value of 0.3 × 10-3 Ω cm at 138 GPa and 4100 K was obtained for silane. The minimum resistivity of hydrogen in the state of 102 GPa and 4300 K was 0.35 Ω cm. It showed that the measured electrical resistivity of the shock-compressed hydrogen was an order of magnitude higher than fluid silane at 50-90 GPa. However, beyond 100 GPa, the resistivity difference between silane and hydrogen was very minor. The carriers in the sample were hydrogen, and the concentration of hydrogen atoms in these two substances was close to each other. These results supported the theoretical prediction that silane was interpreted simply in terms of chemical decomposition into silicon nanoparticles and fluid hydrogen, and electrical conduction flows predominately dominated by the fluid hydrogen. In addition, the results also supported the theory of "chemical precompression", the existence of Sisbnd H bond helped to reduce the pressure of hydrogen metallization. These findings could lead the way for further metallic phases of hydrogen-rich materials and experimental studies.
Revisited reaction-diffusion model of thermal desorption spectroscopy experiments on hydrogen retention in material

DOE Office of Scientific and Technical Information (OSTI.GOV)

Guterl, Jerome, E-mail: jguterl@ucsd.edu; Smirnov, R. D.; Krasheninnikov, S. I.

Desorption phase of thermal desorption spectroscopy (TDS) experiments performed on tungsten samples exposed to flux of hydrogen isotopes in fusion relevant conditions is analyzed using a reaction-diffusion model describing hydrogen retention in material bulk. Two regimes of hydrogen desorption are identified depending on whether hydrogen trapping rate is faster than hydrogen diffusion rate in material during TDS experiments. In both regimes, a majority of hydrogen released from material defects is immediately outgassed instead of diffusing deeply in material bulk when the evolution of hydrogen concentration in material is quasi-static, which is the case during TDS experiments performed with tungsten samplesmore » exposed to flux of hydrogen isotopes in fusion related conditions. In this context, analytical expressions of the hydrogen outgassing flux as a function of the material temperature are obtained with sufficient accuracy to describe main features of thermal desorption spectra (TDSP). These expressions are then used to highlight how characteristic temperatures of TDSP depend on hydrogen retention parameters, such as trap concentration or activation energy of detrapping processes. The use of Arrhenius plots to characterize retention processes is then revisited when hydrogen trapping takes place during TDS experiments. Retention processes are also characterized using the shape of desorption peaks in TDSP, and it is shown that diffusion of hydrogen in material during TDS experiment can induce long desorption tails visible aside desorption peaks at high temperature in TDSP. These desorption tails can be used to estimate activation energy of diffusion of hydrogen in material.« less
Dedicated nuclear facilities for electrolytic hydrogen production

NASA Technical Reports Server (NTRS)

Foh, S. E.; Escher, W. J. D.; Donakowski, T. D.

1979-01-01

An advanced technology, fully dedicated nuclear-electrolytic hydrogen production facility is presented. This plant will produce hydrogen and oxygen only and no electrical power will be generated for off-plant use. The conceptual design was based on hydrogen production to fill a pipeline at 1000 psi and a 3000 MW nuclear base, and the base-line facility nuclear-to-shaftpower and shaftpower-to-electricity subsystems, the water treatment subsystem, electricity-to-hydrogen subsystem, hydrogen compression, efficiency, and hydrogen production cost are discussed. The final conceptual design integrates a 3000 MWth high-temperature gas-cooled reactor operating at 980 C helium reactor-out temperature, direct dc electricity generation via acyclic generators, and high-current density, high-pressure electrolyzers based on the solid polymer electrolyte approach. All subsystems are close-coupled and optimally interfaced and pipeline hydrogen is produced at 1000 psi. Hydrogen costs were about half of the conventional nuclear electrolysis process.
Thermodynamic equilibrium calculations of hydrogen production from the combined processes of dimethyl ether steam reforming and partial oxidation

NASA Astrophysics Data System (ADS)

Semelsberger, Troy A.; Borup, Rodney L.

Thermodynamic analyses of producing a hydrogen-rich fuel-cell feed from the combined processes of dimethyl ether (DME) partial oxidation and steam reforming were investigated as a function of oxygen-to-carbon ratio (0.00-2.80), steam-to-carbon ratio (0.00-4.00), temperature (100 °C-600 °C), pressure (1-5 atm) and product species. Thermodynamically, dimethyl ether processed with air and steam generates hydrogen-rich fuel-cell feeds; however, the hydrogen concentration is less than that for pure DME steam reforming. Results of the thermodynamic processing of dimethyl ether indicate the complete conversion of dimethyl ether to hydrogen, carbon monoxide and carbon dioxide for temperatures greater than 200 °C, oxygen-to-carbon ratios greater than 0.00 and steam-to-carbon ratios greater than 1.25 at atmospheric pressure (P = 1 atm). Increasing the operating pressure has negligible effects on the hydrogen content. Thermodynamically, dimethyl ether can produce concentrations of hydrogen and carbon monoxide of 52% and 2.2%, respectively, at a temperature of 300 °C, and oxygen-to-carbon ratio of 0.40, a pressure of 1 atm and a steam-to-carbon ratio of 1.50. The order of thermodynamically stable products (excluding H 2, CO, CO 2, DME, NH 3 and H 2O) in decreasing mole fraction is methane, ethane, isopropyl alcohol, acetone, n-propanol, ethylene, ethanol and methyl-ethyl ether; trace amounts of formaldehyde, formic acid and methanol are observed. Ammonia and hydrogen cyanide are also thermodynamically favored products. Ammonia is favored at low temperatures in the range of oxygen-to-carbon ratios of 0.40-2.50 regardless of the steam-to-carbon ratio employed. The maximum ammonia content (i.e., 40%) occurs at an oxygen-to-carbon ratio of 0.40, a steam-to-carbon ratio of 1.00 and a temperature of 100 °C. Hydrogen cyanide is favored at high temperatures and low oxygen-to-carbon ratios with a maximum of 3.18% occurring at an oxygen-to-carbon ratio of 0.40 and a steam-to-carbon ratio of 0.00 in the temperature range of 400 °C-500 °C. Increasing the system pressure shifts the equilibrium toward ammonia and hydrogen cyanide.
Process for manufacture of thick film hydrogen sensors

DOEpatents

Perdieu, Louisa H.

2000-09-09

A thick film process for producing hydrogen sensors capable of sensing down to a one percent concentration of hydrogen in carrier gasses such as argon, nitrogen, and air. The sensor is also suitable to detect hydrogen gas while immersed in transformer oil. The sensor includes a palladium resistance network thick film printed on a substrate, a portion of which network is coated with a protective hydrogen barrier. The process utilizes a sequence of printing of the requisite materials on a non-conductive substrate with firing temperatures at each step which are less than or equal to the temperature at the previous step.
Influence of Hydrogen on Atomized Titanium Powders Sintering

NASA Astrophysics Data System (ADS)

Senkevich, K. S.

2018-07-01

The aim of this work is to study the effect of hydrogen reversible alloying (thermohydrogen processing, THP) on low-temperature sintering of atomized titanium powders. It is stated that alloying with 0.2 to 0.8 wt pct of hydrogen beneficially affects titanium powders sintering. The effect is caused by phase transformations occurring upon hydrogen saturation of powders and dehydrogenation, which substantially intensifies sintering at temperatures from 800 °C to 900 °C. The role of certain THP stages (sintering in hydrogenated state and upon dehydrogenation) on formation of sintered contacts in porous materials is shown.
Influence of Hydrogen on Atomized Titanium Powders Sintering

NASA Astrophysics Data System (ADS)

Senkevich, K. S.

2018-05-01

The aim of this work is to study the effect of hydrogen reversible alloying (thermohydrogen processing, THP) on low-temperature sintering of atomized titanium powders. It is stated that alloying with 0.2 to 0.8 wt pct of hydrogen beneficially affects titanium powders sintering. The effect is caused by phase transformations occurring upon hydrogen saturation of powders and dehydrogenation, which substantially intensifies sintering at temperatures from 800 °C to 900 °C. The role of certain THP stages (sintering in hydrogenated state and upon dehydrogenation) on formation of sintered contacts in porous materials is shown.
Transition of the Laminar Boundary Layer on a Delta Wing with 74 degree Sweep in Free Flight at Mach Numbers from 2.8 to 5.3

NASA Technical Reports Server (NTRS)

Chapman, Gary T.

1961-01-01

The tests were conducted at Mach numbers from 2.8 to 5.3, with model surface temperatures small compared to boundary-layer recovery temperature. The effects of Mach number, temperature ratio, unit Reynolds number, leading-edge diameter, and angle of attack were investigated in an exploratory fashion. The effect of heat-transfer condition (i.e., wall temperature to total temperature ratio) and Mach number can not be separated explicitly in free-flight tests. However, the data of the present report, as well as those of NACA TN 3473, were found to be more consistent when plotted versus temperature ratio. Decreasing temperature ratio increased the transition Reynolds number. The effect of unit Reynolds number was small as was the effect of leading-edge diameter within the range tested. At small values of angle of attack, transition moved forward on the windward surface and rearward on the leeward surface. This trend was reversed at high angles of attack (6 deg to 18 deg). Possible reasons for this are the reduction of crossflow on the windward side and the influence of the lifting vortices on the leeward surface. When the transition results on the 740 delta wing were compared to data at similar test conditions for an unswept leading edge, the results bore out the results of earlier research at nearly zero heat transfer; namely, sweep causes a large reduction in the transition Reynolds number.
Concept study of a hydrogen containment process during nuclear thermal engine ground testing

NASA Astrophysics Data System (ADS)

Wang, Ten-See; Stewart, Eric T.; Canabal, Francisco

A new hydrogen containment process was proposed for ground testing of a nuclear thermal engine. It utilizes two thermophysical steps to contain the hydrogen exhaust. First, the decomposition of hydrogen through oxygen-rich combustion at higher temperature; second, the recombination of remaining hydrogen with radicals at low temperature. This is achieved with two unit operations: an oxygen-rich burner and a tubular heat exchanger. A computational fluid dynamics methodology was used to analyze the entire process on a three-dimensional domain. The computed flammability at the exit of the heat exchanger was less than the lower flammability limit, confirming the hydrogen containment capability of the proposed process.
Deposition of device quality low H content, amorphous silicon films

DOEpatents

Mahan, A.H.; Carapella, J.C.; Gallagher, A.C.

1995-03-14

A high quality, low hydrogen content, hydrogenated amorphous silicon (a-Si:H) film is deposited by passing a stream of silane gas (SiH{sub 4}) over a high temperature, 2,000 C, tungsten (W) filament in the proximity of a high temperature, 400 C, substrate within a low pressure, 8 mTorr, deposition chamber. The silane gas is decomposed into atomic hydrogen and silicon, which in turn collides preferably not more than 20--30 times before being deposited on the hot substrate. The hydrogenated amorphous silicon films thus produced have only about one atomic percent hydrogen, yet have device quality electrical, chemical, and structural properties, despite this lowered hydrogen content. 7 figs.
Deposition of device quality low H content, amorphous silicon films

DOEpatents

Mahan, Archie H.; Carapella, Jeffrey C.; Gallagher, Alan C.

1995-01-01

A high quality, low hydrogen content, hydrogenated amorphous silicon (a-Si:H) film is deposited by passing a stream of silane gas (SiH.sub.4) over a high temperature, 2000.degree. C., tungsten (W) filament in the proximity of a high temperature, 400.degree. C., substrate within a low pressure, 8 mTorr, deposition chamber. The silane gas is decomposed into atomic hydrogen and silicon, which in turn collides preferably not more than 20-30 times before being deposited on the hot substrate. The hydrogenated amorphous silicon films thus produced have only about one atomic percent hydrogen, yet have device quality electrical, chemical, and structural properties, despite this lowered hydrogen content.
Numerical Analysis of Plasma Transport in Tandem Volume Magnetic Multicusp Ion Sources

DTIC Science & Technology

1992-03-01

the results of the model are qualitatively correct. Boltzmann Equation, Ion Sources, Plasma Simulation, Electron Temperature, Plasma Density, Ion Temperature, Hydrogen Ions, Magnetic Filters, Hydrogen Plasma Chemistry .
Atomic hydrogen storage method and apparatus

NASA Technical Reports Server (NTRS)

Woollam, J. A. (Inventor)

1978-01-01

Atomic hydrogen, for use as a fuel or as an explosive, is stored in the presence of a strong magnetic field in exfoliated layered compounds such as molybdenum disulfide or an elemental layer material such as graphite. The compound is maintained at liquid helium temperatures and the atomic hydrogen is collected on the surfaces of the layered compound which are exposed during delamination (exfoliation). The strong magnetic field and the low temperature combine to prevent the atoms of hydrogen from recombining to form molecules.

Atomic hydrogen storage method and apparatus

NASA Technical Reports Server (NTRS)

Woollam, J. A. (Inventor)

1980-01-01

Atomic hydrogen, for use as a fuel or as an explosive, is stored in the presence of a strong magnetic field in exfoliated layered compounds such as molybdenum disulfide or an elemental layer material such as graphite. The compounds maintained at liquid helium temperatures and the atomic hydrogen is collected on the surfaces of the layered compound which are exposed during delamination (exfoliation). The strong magnetic field and the low temperature combine to prevent the atoms of hydrogen from recombining to form molecules.
Atomic hydrogen storage. [cryotrapping and magnetic field strength

NASA Technical Reports Server (NTRS)

Woollam, J. A. (Inventor)

1980-01-01

Atomic hydrogen, for use as a fuel or as an explosive, is stored in the presence of a strong magnetic field in exfoliated layered compounds such as molybdenum disulfide or an elemental layer material such as graphite. The compound is maintained at liquid temperatures and the atomic hydrogen is collected on the surfaces of the layered compound which are exposed during delamination (exfoliation). The strong magnetic field and the low temperature combine to prevent the atoms of hydrogen from recombining to form molecules.
High temperature decomposition of hydrogen peroxide

NASA Technical Reports Server (NTRS)

Parrish, Clyde F. (Inventor)

2004-01-01

Nitric oxide (NO) is oxidized into nitrogen dioxide (NO.sub.2) by the high temperature decomposition of a hydrogen peroxide solution to produce the oxidative free radicals, hydroxyl and hydroperoxyl. The hydrogen peroxide solution is impinged upon a heated surface in a stream of nitric oxide where it decomposes to produce the oxidative free radicals. Because the decomposition of the hydrogen peroxide solution occurs within the stream of the nitric oxide, rapid gas-phase oxidation of nitric oxide into nitrogen dioxide occurs.
High temperature decomposition of hydrogen peroxide

NASA Technical Reports Server (NTRS)

Parrish, Clyde F. (Inventor)

2011-01-01

Nitric oxide (NO) is oxidized into nitrogen dioxide (NO.sub.2) by the high temperature decomposition of a hydrogen peroxide solution to produce the oxidative free radicals, hydroxyl and hydroperoxyl. The hydrogen peroxide solution is impinged upon a heated surface in a stream of nitric oxide where it decomposes to produce the oxidative free radicals. Because the decomposition of the hydrogen peroxide solution occurs within the stream of the nitric oxide, rapid gas-phase oxidation of nitric oxide into nitrogen dioxide occurs.
Detection of Micro-Leaks Through Complex Geometries Under Mechanical Load and at Cryogenic Temperature

NASA Technical Reports Server (NTRS)

Rivers, H. Kevin; Sikora, J. G.; Sankaran, S. N.

2001-01-01

Polymer Matrix Composite (PMC) hydrogen tanks have been proposed as an enabling technology for reducing the weight of Single-Stage-to-Orbit reusable launch vehicles where structural mass has a large impact on vehicle performance. A key development issue of these lightweight structures is the leakage of hydrogen through the composite material. The rate of hydrogen leakage can be a function of the material used, method of 6 fabrication used to manufacture the tank, mechanical load the tank must react, internal damage-state of the material, and the temperatures at which the tank must operate. A method for measuring leakage through a geometrically complex structure at cryogenic temperature and under mechanical load was developed, calibrated and used to measure hydrogen leakage through complex X-33 liquid-hydrogen tank structure sections.
The use of a very high temperature nuclear reactor in the manufacture of synthetic fuels

NASA Technical Reports Server (NTRS)

Farbman, G. H.; Brecher, L. E.

1976-01-01

The three parts of a program directed toward creating a cost-effective nuclear hydrogen production system are described. The discussion covers the development of a very high temperature nuclear reactor (VHTR) as a nuclear heat and power source capable of producing the high temperature needed for hydrogen production and other processes; the development of a hydrogen generation process based on water decomposition, which can utilize the outputs of the VHTR and be integrated with many different ultimate hydrogen consuming processes; and the evaluation of the process applications of the nuclear hydrogen systems to assess the merits and potential payoffs. It is shown that the use of VHTR for the manufacture of synthetic fuels appears to have a very high probability of making a positive contribution to meeting the nation's energy needs in the future.
Width-Increased Dual-Pump Enhanced Coherent Anti-Stokes Raman Spectroscopy (WIDECARS)

NASA Technical Reports Server (NTRS)

Tedder, Sarah A.; Wheeler, Jeffrey L.; Danehy, Paul M.

2010-01-01

WIDECARS is a dual-pump coherent anti-Stokes Raman Spectroscopy technique that is capable of simultaneously measuring temperature and species mole fractions of N2, O2, H2, C2H4, CO, and CO2. WIDECARS is designed for measurements of all the major species (except water) in supersonic combustion flows fueled with hydrogen and hydrogen/ethylene mixtures. The two lowest rotational energy levels of hydrogen detectable by WIDECARS are H2 S(3) and H2 S(4). The detection of these lines gives the system the capability to measure temperature and species concentrations in regions of the flow containing pure hydrogen fuel at room temperature.
Thermal conductivity of gaseous and liquid hydrogen

NASA Technical Reports Server (NTRS)

Diller, D. E.; Roder, H. M.

1971-01-01

Normal and para-hydrogen conductivity measurements at temperatures from 200 to 17 deg K, at densities up to 2.6 times critical density, and at pressures to 15 MN/sq m are made. Using new calorimeter, data are analyzed as functions of density at fixed temperatures and of temperature at fixed densities
Behavior of tritium permeation induced by water corrosion of alpha iron around room temperature

DOE Office of Scientific and Technical Information (OSTI.GOV)

Otsuka, T.; Hashizume, K.

2015-03-15

Tritium (T) permeation leakage to surroundings is a great safety concern in fission and fusion reactor systems. T permeation potentially occurs from T contaminated water through cooling tubes or storage tank made of metals which dissolve some T evolved by water corrosion. In order to understand behaviors of hydrogen uptake and permeation in pure α-iron (αFe) during water corrosion around room temperature, hydrogen permeation experiments for an αFe membrane have been conducted by means of tritium tracer techniques. The present study suggests that hydrogen produced by water corrosion of αFe is trapped in product oxide layers to delay hydrogen uptakemore » in αFe for a moment. However, the oxide layers do not work as a sufficient barrier for hydrogen uptake. Some of hydrogen dissolved in αFe normally diffuses and permeates through the bulk in the early stage of permeation. In a later stage, hydrogen permeation could be apparently stopped by the disappearance of concentration difference of tritium. Hydrogen partial pressure at the water/αFe interface could be ranged from 0.7 to 9.5 kPa around room temperature.« less
Metastable Metal Hydrides for Hydrogen Storage

DOE PAGES

Graetz, Jason

2012-01-01

The possibility of using hydrogen as a reliable energy carrier for both stationary and mobile applications has gained renewed interest in recent years due to improvements in high temperature fuel cells and a reduction in hydrogen production costs. However, a number of challenges remain and new media are needed that are capable of safely storing hydrogen with high gravimetric and volumetric densities. Metal hydrides and complex metal hydrides offer some hope of overcoming these challenges; however, many of the high capacity “reversible” hydrides exhibit a large endothermic decomposition enthalpy making it difficult to release the hydrogen at low temperatures. Onmore » the other hand, the metastable hydrides are characterized by a low reaction enthalpy and a decomposition reaction that is thermodynamically favorable under ambient conditions. The rapid, low temperature hydrogen evolution rates that can be achieved with these materials offer much promise for mobile PEM fuel cell applications. However, a critical challenge exists to develop new methods to regenerate these hydrides directly from the reactants and hydrogen gas. This spotlight paper presents an overview of some of the metastable metal hydrides for hydrogen storage and a few new approaches being investigated to address the key challenges associated with these materials.« less
New insights into designing metallacarborane based room temperature hydrogen storage media.

PubMed

Bora, Pankaj Lochan; Singh, Abhishek K

2013-10-28

Metallacarboranes are promising towards realizing room temperature hydrogen storage media because of the presence of both transition metal and carbon atoms. In metallacarborane clusters, the transition metal adsorbs hydrogen molecules and carbon can link these clusters to form metal organic framework, which can serve as a complete storage medium. Using first principles density functional calculations, we chalk out the underlying principles of designing an efficient metallacarborane based hydrogen storage media. The storage capacity of hydrogen depends upon the number of available transition metal d-orbitals, number of carbons, and dopant atoms in the cluster. These factors control the amount of charge transfer from metal to the cluster, thereby affecting the number of adsorbed hydrogen molecules. This correlation between the charge transfer and storage capacity is general in nature, and can be applied to designing efficient hydrogen storage systems. Following this strategy, a search for the best metallacarborane was carried out in which Sc based monocarborane was found to be the most promising H2 sorbent material with a 9 wt.% of reversible storage at ambient pressure and temperature.
Low-temperature (120 °C) growth of nanocrystalline silicon films prepared by plasma enhanced chemical vapor deposition from SiCl 4/H 2 gases: Microstructure characterization

NASA Astrophysics Data System (ADS)

Zhang, L.; Gao, J. H.; Xiao, J. Q.; Wen, L. S.; Gong, J.; Sun, C.

2012-01-01

Hydrogenated nanocrystalline silicon (nc-Si:H) films were prepared using diluted tetrachlorosilane (SiCl4) with various hydrogen flow rates (Hf) by plasma enhanced chemical vapor deposition (PECVD) at a constant substrate temperature (Ts) as low as 120 °C. Raman spectroscopy, transmission electron microscopy (TEM), X-ray photoelectron spectroscopy (XPS), infrared spectra (IR) and spectroscopic ellipsometry (SE) were employed to investigate the microstructure and hydrogen bonding of the nc-Si:H films. Our results showed that the microstructure and hydrogen content of the films could be effectively tailored by the hydrogen flow rates, and a distinct transition from amorphous to nanocrystalline phase was observed with an increase of Hf. At an optimal preparation condition, a deposition rate was as high as 3.7 nm/min and the crystallinity reached up to 64.1%. In addition, the effect of hydrogen on the low-temperature growth of nc-Si:H film was proposed in relation to the surface reaction of radicals and the hydrogen diffusion in the surface growing region.
New insights into designing metallacarborane based room temperature hydrogen storage media

DOE Office of Scientific and Technical Information (OSTI.GOV)

Bora, Pankaj Lochan; Singh, Abhishek K.

Metallacarboranes are promising towards realizing room temperature hydrogen storage media because of the presence of both transition metal and carbon atoms. In metallacarborane clusters, the transition metal adsorbs hydrogen molecules and carbon can link these clusters to form metal organic framework, which can serve as a complete storage medium. Using first principles density functional calculations, we chalk out the underlying principles of designing an efficient metallacarborane based hydrogen storage media. The storage capacity of hydrogen depends upon the number of available transition metal d-orbitals, number of carbons, and dopant atoms in the cluster. These factors control the amount of chargemore » transfer from metal to the cluster, thereby affecting the number of adsorbed hydrogen molecules. This correlation between the charge transfer and storage capacity is general in nature, and can be applied to designing efficient hydrogen storage systems. Following this strategy, a search for the best metallacarborane was carried out in which Sc based monocarborane was found to be the most promising H{sub 2} sorbent material with a 9 wt.% of reversible storage at ambient pressure and temperature.« less
Hydrogen Cyanide Produced by Pseudomonas chlororaphis O6 Exhibits Nematicidal Activity against Meloidogyne hapla

PubMed Central

Kang, Beom Ryong; Anderson, Anne J.; Kim, Young Cheol

2018-01-01

Root-knot nematodes (Meloidogyne spp.) are parasites that attack many field crops and orchard trees, and affect both the quantity and quality of the products. A root-colonizing bacterium, Pseudomonas chlororaphis O6, possesses beneficial traits including strong nematicidal activity. To determine the molecular mechanisms involved in the nematicidal activity of P. chlororaphis O6, we constructed two mutants; one lacking hydrogen cyanide production, and a second lacking an insecticidal toxin, FitD. Root drenching with wild-type P. chlororaphis O6 cells caused juvenile mortality in vitro and in planta. Efficacy was not altered in the fitD mutant compared to the wild-type but was reduced in both bioassays for the mutant lacking hydrogen cyanide production. The reduced number of galls on tomato plants caused by the wild-type strain was comparable to that of a standard chemical nematicide. These findings suggest that hydrogen cyanide-producing root colonizers, such as P. chlororaphis O6, could be formulated as “green” nematicides that are compatible with many crops and offer agricultural sustainability. PMID:29422786
DOE Office of Scientific and Technical Information (OSTI.GOV)

Podlivaev, A. I., E-mail: AIPodlivayev@mephi.ru; Openov, L. A.

The initial stage of hydrogen desorption from fully hydrogenated carbon nanotubes (3.0) and (2.2) is numerically studied by the molecular dynamics method. The temperature dependence of the desorption rate is directly determined at T = 1800–2500 K. The characteristic desorption times are determined at temperatures outside this range by extrapolation. It is shown that hydrogen desorption leads to the appearance of electronic states in the band gap.
Hydrogen content and mechanical stress in glow discharge amorphous silicon

NASA Astrophysics Data System (ADS)

Paduschek, P.; Eichinger, P.; Kristen, G.; Mitlehner, H.

1982-08-01

The hydrogen content of plasma deposited amorphous silicon thin films on silicon has been determined as a function of annealing parameters (200-700°C, 12 h) using the proton-proton scattering method. It is shown that hydrogen is released with an activation energy of 1.3 eV. Different deposition temperatures are compared with respect to the hydrogen evolution. The mechanical stress of the layers on silicon substrates has been measured by interferometric techniques for each annealing step. As the hydrogen content decreases monotonically with rising annealing temperature the mechanical stress converts from compressive to tensile. While only a weak correlation exists between the total hydrogen content and the mechanical stress, the bound hydrogen as determined by IR absorption displays a linear relation with the measured mechanical stress.
Evaluation of Structural Isomers, Molecular Interactions, Reactivity Descriptors, and Vibrational Analysis of Tretinoin.

PubMed

Karthick, T; Tandon, Poonam; Singh, Swapnil

2017-01-01

Tretinoin is known to be a pharmaceutical drug for treating acne vulgaris, keratosis pilaris, and acute promyelocytic leukemia. In order to reveal the possible conformers of tretinoin, the energies of all the conformers through rotational bonds have been evaluated by systematic rotor search analysis. The intramolecular interactions ranging from strong hydrogen bonds to weak van der Waals forces present in tretinoin have been distinguished with the help of electron density mapping and wavefunction analysis. The global reactivity descriptors and Fukui functions of tretinoin have been calculated and discussed. The sites suitable for electrophilic attack and nucleophilic attack have been identified with the help of Hirshfeld partitioning. The vibrational spectroscopic signature of tretinoin and mixed mode band assignments have been elucidated with the help of experimental and simulated spectra.
Pd/Ag coated fiber Bragg grating sensor for hydrogen monitoring in power transformers.

PubMed

Ma, G M; Jiang, J; Li, C R; Song, H T; Luo, Y T; Wang, H B

2015-04-01

Compared with conventional DGA (dissolved gas analysis) method for on-line monitoring of power transformers, FBG (fiber Bragg grating) hydrogen sensor represents marked advantages over immunity to electromagnetic field, time-saving, and convenience to defect location. Thus, a novel FBG hydrogen sensor based on Pd/Ag (Palladium/Silver) along with polyimide composite film to measure dissolved hydrogen concentration in large power transformers is proposed in this article. With the help of Pd/Ag composite coating, the enhanced performance on mechanical strength and sensitivity is demonstrated, moreover, the response time and sensitivity influenced by oil temperature are solved by correction lines. Sensitivity measurement and temperature calibration of the specific hydrogen sensor have been done respectively in the lab. And experiment results show a high sensitivity of 0.055 pm/(μl/l) with instant response time about 0.4 h under the typical operating temperature of power transformers, which proves a potential utilization inside power transformers to monitor the health status by detecting the dissolved hydrogen concentration.
Direct Evidence for Solid-like Hydrogen in a Nanoporous Carbon Hydrogen Storage Material at Supercritical Temperatures

DOE Office of Scientific and Technical Information (OSTI.GOV)

Ting, Valeska P.; Ramirez-Cuesta, Anibal J.; Bimbo, Nuno

Here in this paper we report direct physical evidence that confinement of molecular hydrogen (H 2) in an optimized nanoporous carbon results in accumulation of hydrogen with characteristics commensurate with solid H 2 at temperatures up to 67 K above the liquid vapor critical temperature of bulk H 2. This extreme densification is attributed to confinement of 112 molecules in the optimally sized micropores, and occurs at pressures as low as 0.02 MPa. The quantities of contained, solid-like H 2 increased with pressure and were directly evaluated using in situ inelastic neutron scattering and confirmed by analysis of gas sorptionmore » isotherms. The demonstration of the existence of solid-like H 2 challenges the existing assumption that supercritical hydrogen confined in nanopores has an upper limit of liquid H 2 density. Thus, this insight offers opportunities for the development of more accurate models for the evaluation and design of nanoporous materials for high capacity adsorptive hydrogen storage.« less
Direct Evidence for Solid-like Hydrogen in a Nanoporous Carbon Hydrogen Storage Material at Supercritical Temperatures

DOE PAGES

Ting, Valeska P.; Ramirez-Cuesta, Anibal J.; Bimbo, Nuno; ...

2015-07-14

Here in this paper we report direct physical evidence that confinement of molecular hydrogen (H 2) in an optimized nanoporous carbon results in accumulation of hydrogen with characteristics commensurate with solid H 2 at temperatures up to 67 K above the liquid vapor critical temperature of bulk H 2. This extreme densification is attributed to confinement of 112 molecules in the optimally sized micropores, and occurs at pressures as low as 0.02 MPa. The quantities of contained, solid-like H 2 increased with pressure and were directly evaluated using in situ inelastic neutron scattering and confirmed by analysis of gas sorptionmore » isotherms. The demonstration of the existence of solid-like H 2 challenges the existing assumption that supercritical hydrogen confined in nanopores has an upper limit of liquid H 2 density. Thus, this insight offers opportunities for the development of more accurate models for the evaluation and design of nanoporous materials for high capacity adsorptive hydrogen storage.« less

Defense Against Chip Cloning Attacks Based on Fractional Hopfield Neural Networks.

PubMed

Pu, Yi-Fei; Yi, Zhang; Zhou, Ji-Liu

2017-06-01

This paper presents a state-of-the-art application of fractional hopfield neural networks (FHNNs) to defend against chip cloning attacks, and provides insight into the reason that the proposed method is superior to physically unclonable functions (PUFs). In the past decade, PUFs have been evolving as one of the best types of hardware security. However, the development of the PUFs has been somewhat limited by its implementation cost, its temperature variation effect, its electromagnetic interference effect, the amount of entropy in it, etc. Therefore, it is imperative to discover, through promising mathematical methods and physical modules, some novel mechanisms to overcome the aforementioned weaknesses of the PUFs. Motivated by this need, in this paper, we propose applying the FHNNs to defend against chip cloning attacks. At first, we implement the arbitrary-order fractor of a FHNN. Secondly, we describe the implementation cost of the FHNNs. Thirdly, we propose the achievement of the constant-order performance of a FHNN when ambient temperature varies. Fourthly, we analyze the electrical performance stability of the FHNNs under electromagnetic disturbance conditions. Fifthly, we study the amount of entropy of the FHNNs. Lastly, we perform experiments to analyze the pass-band width of the fractor of an arbitrary-order FHNN and the defense against chip cloning attacks capability of the FHNNs. In particular, the capabilities of defense against chip cloning attacks, anti-electromagnetic interference, and anti-temperature variation of a FHNN are illustrated experimentally in detail. Some significant advantages of the FHNNs are that their implementation cost is considerably lower than that of the PUFs, their electrical performance is much more stable than that of the PUFs under different temperature conditions, their electrical performance stability of the FHNNs under electromagnetic disturbance conditions is much more robust than that of the PUFs, and their amount of entropy is significantly higher than that of the PUFs with the same rank circuit scale.
Thermionic cogeneration burner design

NASA Astrophysics Data System (ADS)

Miskolczy, G.; Goodale, D.; Moffat, A. L.; Morgan, D. T.

Since thermionic converters receive heat at very high temperatures (approximately 1800 K) and reject heat at moderately high temperatures (approximately 800 K), they are useful for cogeneration applications involving high temperature processes. The electric power from thermionic converters is produced as a high amperage, low-voltage direct current. An ideal cogeneration application would be to utilize the reject heat at the collector temperature and the electricity without power conditioning. A cogeneration application in the edible oil industry fulfills both of these requirements since both direct heat and hydrogen gas are required in the hydrogenation of the oils. In this application, the low-voltage direct current would be used in a hydrogen electrolyzer.
Application of low-temperature plasma for the synthesis of hydrogenated graphene (graphane)

NASA Astrophysics Data System (ADS)

Shavelkina, M. B.; Amirov, R. H.; Katarzhis, V. A.; Kiselev, V. I.

2017-12-01

The possibility of a direct synthesis of hydrogenated graphene in decomposition of methane by means of low-temperature plasma was investigated. A DC plasma torch with an expanding channel-anode, a vortex gas supply and a self-setting arc length was used as a generator of low-temperature plasma. Argon was used as the plasma-forming gas. The temperatures of argon plasma and with methane addition to it were determined on the basis of spectral measurements. The synthesis products were characterized by electron microscopy and thermogravimetry. The effect of hydrogenated graphene as a nanomodifier on the properties of the cubic boron nitride based functional ceramics was investigated.
Thermodynamic Calculations of Hydrogen-Oxygen Detonation Parameters for Various Initial Pressures

NASA Technical Reports Server (NTRS)

Bollinger, Loren E.; Edse, Rudolph

1961-01-01

Composition, temperature, pressure and density behind a stable detonation wave and its propagation rate have been calculated for seven hydrogen-oxygen mixture at 1, 5, 25 and 100 atm initial pressure, and at an initial temperature of 40C. For stoichiometric mixtures that calculations also include an initial temperature of 200C. According to these calculations the detonation velocities of hydrogen-oxygen mixtures increase with increasing initial pressure, but decrease slightly when the initial temperature is raised from 40 to 200 C. The calculated detonation velocities agree satisfactorily with values determined experimentally. These values will be published in the near future.
Warm Pre-Strain: Strengthening the Metastable 304L Austenitic Stainless Steel without Compromising Its Hydrogen Embrittlement Resistance

PubMed Central

Wang, Yanfei; Zhou, Zhiling; Wu, Weijie; Gong, Jianming

2017-01-01

Plastic pre-strains were applied to the metastable 304L austenitic stainless steel at both room temperature (20 °C) and higher temperatures (i.e., 50, 80 and 100 °C), and then the hydrogen embrittlement (HE) susceptibility of the steel was evaluated by cathodically hydrogen-charging and tensile testing. The 20 °C pre-strain greatly strengthened the steel, but simultaneously significantly increased the HE susceptibility of the steel, since α′ martensite was induced by the pre-strain, causing the pre-existence of α′ martensite, which provided “highways” for hydrogen to transport deep into the steel during the hydrogen-charging. Although the warm pre-strains did not strengthen the steel as significantly as the 20 °C pre-strain, they retained the HE resistance of the steel. This is because the higher temperatures, particularly 80 and 100 °C, suppressed the α′ martensite transformation during the pre-straining. Pre-strain at a temperature slightly higher than room temperature has a potential to strengthen the metastable 304L austenitic stainless steel without compromising its initial HE resistance. PMID:29160830
In-situ formation of solidified hydrogen thin-membrane targets using a pulse tube cryocooler

NASA Astrophysics Data System (ADS)

Astbury, S.; Bedacht, S.; Brummitt, P.; Carroll, D.; Clarke, R.; Crisp, S.; Hernandez-Gomez, C.; Holligan, P.; Hook, S.; Merchan, J. S.; Neely, D.; Ortner, A.; Rathbone, D.; Rice, P.; Schaumann, G.; Scott, G.; Spindloe, C.; Spurdle, S.; Tebartz, A.; Tomlinson, S.; Wagner, F.; Borghesi, M.; Roth, M.; Tolley, M. K.

2016-04-01

An account is given of the Central Laser Facility's work to produce a cryogenic hydrogen targetry system using a pulse tube cryocooler. Due to the increasing demand for low Z thin laser targets, CLF (in collaboration with TUD) have been developing a system which allows the production of solid hydrogen membranes by engineering a design which can achieve this remotely; enabling the gas injection, condensation and solidification of hydrogen without compromising the vacuum of the target chamber. A dynamic sealing mechanism was integrated which allows targets to be grown and then remotely exposed to open vacuum for laser interaction. Further research was conducted on the survivability of the cryogenic targets which concluded that a warm gas effect causes temperature spiking when exposing the solidified hydrogen to the outer vacuum. This effect was shown to be mitigated by improving the pumping capacity of the environment and reducing the minimum temperature obtainable on the target mount. This was achieved by developing a two-stage radiation shield encased with superinsulating blanketing; reducing the base temperature from 14 ± 0.5 K to 7.2 ± 0.2 K about the coldhead as well as improving temperature control stability following the installation of a high-performance temperature controller and sensor apparatus. The system was delivered experimentally and in July 2014 the first laser shots were taken upon hydrogen targets in the Vulcan TAP facility.
Thin-film fiber optic hydrogen and temperature sensor system

DOEpatents

Nave, Stanley E.

1998-01-01

The invention discloses a sensor probe device for monitoring of hydrogen gas concentrations and temperatures by the same sensor probe. The sensor probe is constructed using thin-film deposition methods for the placement of a multitude of layers of materials sensitive to hydrogen concentrations and temperature on the end of a light transparent lens located within the sensor probe. The end of the lens within the sensor probe contains a lens containing a layer of hydrogen permeable material which excludes other reactive gases, a layer of reflective metal material that forms a metal hydride upon absorbing hydrogen, and a layer of semi-conducting solid that is transparent above a temperature dependent minimum wavelength for temperature detection. The three layers of materials are located at the distal end of the lens located within the sensor probe. The lens focuses light generated by broad-band light generator and connected by fiber-optics to the sensor probe, onto a reflective metal material layer, which passes through the semi-conducting solid layer, onto two optical fibers located at the base of the sensor probe. The reflected light is transmitted over fiberoptic cables to a spectrometer and system controller. The absence of electrical signals and electrical wires in the sensor probe provides for an elimination of the potential for spark sources when monitoring in hydrogen rich environments, and provides a sensor free from electrical interferences.
Thin-film fiber optic hydrogen and temperature sensor system

DOEpatents

Nave, S.E.

1998-07-21

The invention discloses a sensor probe device for monitoring of hydrogen gas concentrations and temperatures by the same sensor probe. The sensor probe is constructed using thin-film deposition methods for the placement of a multitude of layers of materials sensitive to hydrogen concentrations and temperature on the end of a light transparent lens located within the sensor probe. The end of the lens within the sensor probe contains a lens containing a layer of hydrogen permeable material which excludes other reactive gases, a layer of reflective metal material that forms a metal hydride upon absorbing hydrogen, and a layer of semi-conducting solid that is transparent above a temperature dependent minimum wavelength for temperature detection. The three layers of materials are located at the distal end of the lens located within the sensor probe. The lens focuses light generated by broad-band light generator and connected by fiber-optics to the sensor probe, onto a reflective metal material layer, which passes through the semi-conducting solid layer, onto two optical fibers located at the base of the sensor probe. The reflected light is transmitted over fiber optic cables to a spectrometer and system controller. The absence of electrical signals and electrical wires in the sensor probe provides for an elimination of the potential for spark sources when monitoring in hydrogen rich environments, and provides a sensor free from electrical interferences. 3 figs.
Trapping of hydrogen atoms in X-irradiated salts at room temperature and the decay kinetics

NASA Technical Reports Server (NTRS)

May, C. E.; Philipp, W. H.; Marsik, S. J.

1974-01-01

The salts (hypophosphites, formates, a phosphite, a phosphate, and an oxalate) were X-irradiated, whereby hydrogen formed chemically by a radiolytic process becomes trapped in the solid. By room temperature vacuum extraction, the kinetics for the evolution of this trapped hydrogen was studied mass spectrometrically. All salts except two exhibited second-order kinetics. The two exceptions (NaH2PO2(H2O) and K2HPO4) showed first-order kinetics. Based on experimental results, the escape of hydrogen involves three steps: the diffusion of hydrogen atoms from the bulk to the surface, association of these atoms on the surface (rate controlling step for second-order hydrogen evolution), and the desorption of molecular hydrogen from the surface. The hydrogen does not escape if the irradiated salt is stored in air, apparently because adsorbed air molecules occupy surface sites required in the escape mechanism.
Inverted Fuel Cell: Room-Temperature Hydrogen Separation from an Exhaust Gas by Using a Commercial Short-Circuited PEM Fuel Cell without Applying any Electrical Voltage.

PubMed

Friebe, Sebastian; Geppert, Benjamin; Caro, Jürgen

2015-06-26

A short-circuited PEM fuel cell with a Nafion membrane has been evaluated in the room-temperature separation of hydrogen from exhaust gas streams. The separated hydrogen can be recovered or consumed in an in situ olefin hydrogenation when the fuel cell is operated as catalytic membrane reactor. Without applying an outer electrical voltage, there is a continuous hydrogen flux from the higher to the lower hydrogen partial pressure side through the Nafion membrane. On the feed side of the Nafion membrane, hydrogen is catalytically split into protons and electrons by the Pt/C electrocatalyst. The protons diffuse through the Nafion membrane, the electrons follow the short-circuit between the two brass current collectors. On the cathode side, protons and electrons recombine, and hydrogen is released. © 2015 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.
Temperature-mediated development thresholds of Sparganothis sulfureana (Lepidoptera: Tortricidae) in cranberries

USDA-ARS?s Scientific Manuscript database

Larvae of Sparganothis sulfureana Clemens, frequently attack cranberries, often resulting in economic damage to the crop. Because temperature dictates insect growth rate, development can be accurately estimated based on daily temperature measurements. To better predict S. sulfureana development acro...
The Economic Potential of Nuclear-Renewable Hybrid Energy Systems Producing Hydrogen

DOE Office of Scientific and Technical Information (OSTI.GOV)

Ruth, Mark; Cutler, Dylan; Flores-Espino, Francisco

This report is one in a series of reports that Idaho National Laboratory and the Joint Institute for Strategic Energy Analysis are publishing that address the technical and economic aspects of nuclear-renewable hybrid energy systems (N-R HESs). This report discusses an analysis of the economic potential of a tightly coupled N-R HES that produces electricity and hydrogen. Both low and high temperature electrolysis options are considered in the analysis. Low-temperature electrolysis requires only electricity to convert water to hydrogen. High temperature electrolysis requires less electricity because it uses both electricity and heat to provide the energy necessary to electrolyze water.more » The study finds that, to be profitable, the examined high-temperature electrosis and low-temperature electrosis N-R HES configurations that produce hydrogen require higher electricity prices, more electricity price volatility, higher natural gas prices, or higher capacity payments than the reference case values of these parameters considered in this analysis.« less
Aircraft-Fuel-Tank Design for Liquid Hydrogen

NASA Technical Reports Server (NTRS)

Reynolds, T W

1955-01-01

Some of the considerations involved in the design of aircraft fuel tanks for liquid hydrogen are discussed herein. Several of the physical properties of metals and thermal insulators in the temperature range from ambient to liquid-hydrogen temperatures are assembled. Calculations based on these properties indicate that it is possible to build a large-size liquid-hydrogen fuel tank which (1) will weigh less then 15 percent of the fuel weight, (2) will have a hydrogen vaporization rate less than 30 percent of the cruise fuel-flow rate, and (3) can be held in a stand-by condition and readied for flight in a short time.
Process for reproducibly preparing titanium subhydride

DOEpatents

Carlson, Richard S.

1982-01-01

Titanium subhydride is produced in a reactor by heating a selected amount of finely divided titanium compound at a selected temperature for a selected period of time under dynamic vacuum conditions. Hydrogen is removed substantially uniformly from each powder grain and there is produced a subhydride of substantially uniform titanium-hydrogen composition. Selection of the amount, temperature and time produces a subhydride of selected titanium-hydrogen composition.
Pressure and temperature fluctuation simulation of J-PARC cryogenic hydrogen system

NASA Astrophysics Data System (ADS)

Tatsumoto, H.; Ohtsu, K.; Aso, T.; Kawakami, Y.

2015-12-01

The J-PARC cryogenic hydrogen system provides supercritical cryogenic hydrogen to the moderators at a pressure of 1.5 MPa and temperature of 18 K and removes 3.8 kW of nuclear heat from the 1 MW proton beam operation. We prepared a heater for thermal compensation and an accumulator, with a bellows structure for volume control, to mitigate the pressure fluctuation caused by switching the proton beam on and off. In this study, a 1-D simulation code named DiSC-SH2 was developed to understand the propagation of pressure and temperature propagations through the hydrogen loop due to on and off switching of the proton beam. We confirmed that the simulated dynamic behaviors in the hydrogen loop for 300-kW and 500-kW proton beam operations agree well with the experimental data under the same conditions.
Silicon Carbide-Based Hydrogen and Hydrocarbon Gas Detection

NASA Technical Reports Server (NTRS)

Hunter, Gary W.; Neudeck, Philip G.; Chen, Liang-Yu; Knight, D.; Liu, C. C.; Wu, Q. H.R

1995-01-01

Hydrogen and hydrocarbon detection in aeronautical applications is important for reasons of safety and emissions control. The use of silicon carbide as a semiconductor in a metal-semiconductor or metal-insulator-semiconductor structure opens opportunities to measure hydrogen and hydrocarbons in high temperature environments beyond the capabilities of silicon-based devices. The purpose of this paper is to explore the response and stability of Pd-SiC Schottky diodes as gas sensors in the temperature range from 100 to 400 C. The effect of heat treating on the diode properties as measured at 100 C is explored. Subsequent operation at 400 C demonstrates the diodes' sensitivity to hydrogen and hydrocarbons. It is concluded that the Pd-SiC Schottky diode has potential as a hydrogen and hydrocarbon sensor over a wide range of temperatures but further studies are necessary to determine the diodes' long term stability.
Hydrogen production from coal using a nuclear heat source

NASA Technical Reports Server (NTRS)

Quade, R. N.

1976-01-01

A strong candidate for hydrogen production in the intermediate time frame of 1985 to 1995 is a coal-based process using a high-temperature gas-cooled reactor (HTGR) as a heat source. Expected process efficiencies in the range of 60 to 70% are considerably higher than all other hydrogen production processes except steam reforming of a natural gas. The process involves the preparation of a coal liquid, hydrogasification of that liquid, and steam reforming of the resulting gaseous or light liquid product. A study showing process efficiency and cost of hydrogen vs nuclear reactor core outlet temperature has been completed, and shows diminishing returns at process temperatures above about 1500 F. A possible scenario combining the relatively abundant and low-cost Western coal deposits with the Gulf Coast hydrogen users is presented which provides high-energy density transportation utilizing coal liquids and uranium.
Method for destroying halocarbon compositions using a critical solvent

DOEpatents

Ginosar, Daniel M.; Fox, Robert V.; Janikowski, Stuart K.

2006-01-10

A method for destroying halocarbons. Halocarbon materials are reacted in a dehalogenation process wherein they are combined with a solvent in the presence of a catalyst. A hydrogen-containing solvent is preferred which functions as both a solvating agent and hydrogen donor. To augment the hydrogen donation capacity of the solvent if needed (or when non-hydrogen-containing solvents are used), a supplemental hydrogen donor composition may be employed. In operation, at least one of the temperature and pressure of the solvent is maintained near, at, or above a critical level. For example, the solvent may be in (1) a supercritical state; (2) a state where one of the temperature or pressure thereof is at or above critical; or (3) a state where at least one of the temperature and pressure thereof is near-critical. This system provides numerous benefits including improved reaction rates, efficiency, and versatility.
Hydrogenation of GaSb/GaAs quantum rings

DOE Office of Scientific and Technical Information (OSTI.GOV)

Hodgson, P. D., E-mail: pdhodgson@hotmail.co.uk; Hayne, M.; Zhuang, Q. D.

2014-08-25

We present the results of photoluminescence measurements on hydrogenated type-II GaSb/GaAs quantum dot/ring (QD/QR) samples at temperatures ranging from 4.2 K to 400 K. Hydrogenation is found to suppress optically induced charge depletion (associated with the presence of carbon acceptors in this system). A redshift of the QD\\QR emission energy of a few tens of meV is observed at temperatures ≥300 K, consistent with a reduction in average occupancy by ∼1 hole. These effects are accompanied by a reduction in PL intensity post-hydrogenation. We conclude that although hydrogenation may have neutralized the carbon acceptors, multiple hole occupancy of type-II GaSb/GaAs QD/QRs is verymore » likely a precondition for intense emission, which would make extending the wavelength significantly beyond 1300 nm at room temperature difficult.« less
Continuous Hydrogen Production from Agricultural Wastewaters at Thermophilic and Hyperthermophilic Temperatures.

PubMed

Ramos, Lucas Rodrigues; Silva, Edson Luiz

2017-06-01

The objective of this study was to investigate the effects of hydraulic retention time (HRT) (8 to 0.5 h) and temperature (55 to 75 °C) in two anaerobic fluidized bed reactors (AFBR) using cheese whey (AFBR-CW = 10,000 mg sugars L -1 ) and vinasse (AFBR-V = 10,000 mg COD L -1 ) as substrates. Decreasing the HRT to 0.5 h increased the hydrogen production rates in both reactors, with maximum values of 5.36 ± 0.81 L H 2 h -1 L -1 in AFBR-CW and 0.71 ± 0.16 L H 2 h -1 L -1 in AFBR-V. The optimal conditions for hydrogen production were the HRT of 4 h and temperature of 65 °C in AFBR-CW, observing maximum hydrogen yield (HY) of 5.51 ± 0.37 mmol H 2 g COD -1 . Still, the maximum HY in AFBR-V was 1.64 ± 0.22 mmol H 2 g COD -1 at 4 h and 55 °C. However, increasing the temperature to 75 °C reduced the hydrogen production in both reactors. Methanol and butyric, acetic, and lactic acids were the main metabolites at temperatures of 55 and 65 °C, favoring the butyric and acetic metabolic pathways of hydrogen production. The increased productions of lactate, propionate, and methanol at 75 °C indicate that the hydrogen-producing bacteria in the thermophilic inoculum were inhibited under hyperthermophilic conditions.

Method of making alkali metal hydrides

DOE Office of Scientific and Technical Information (OSTI.GOV)

Pecharsky, Vitalij K.; Gupta, Shalabh; Pruski, Marek

A method is provided for making alkali metal hydrides by mechanochemically reacting alkali metal and hydrogen gas under mild temperature (e.g room temperature) and hydrogen pressure conditions without the need for catalyst, solvent, and intentional heating or cooling.
Nonequilibrium phase coexistence and criticality near the second explosion limit of hydrogen combustion

NASA Astrophysics Data System (ADS)

Newcomb, Lucas B.; Alaghemandi, Mohammad; Green, Jason R.

2017-07-01

While hydrogen is a promising source of clean energy, the safety and optimization of hydrogen technologies rely on controlling ignition through explosion limits: pressure-temperature boundaries separating explosive behavior from comparatively slow burning. Here, we show that the emergent nonequilibrium chemistry of combustible mixtures can exhibit the quantitative features of a phase transition. With stochastic simulations of the chemical kinetics for a model mechanism of hydrogen combustion, we show that the boundaries marking explosive domains of kinetic behavior are nonequilibrium critical points. Near the pressure of the second explosion limit, these critical points terminate the transient coexistence of dynamical phases—one that autoignites and another that progresses slowly. Below the critical point temperature, the chemistry of these phases is indistinguishable. In the large system limit, the pseudo-critical temperature converges to the temperature of the second explosion limit derived from mass-action kinetics.
Hydrogen generation at ambient conditions: application in fuel cells.

PubMed

Boddien, Albert; Loges, Björn; Junge, Henrik; Beller, Matthias

2008-01-01

The efficient generation of hydrogen from formic acid/amine adducts at ambient temperature is demonstrated. The highest catalytic activity (TOF up to 3630 h(-1) after 20 min) was observed in the presence of in situ generated ruthenium phosphine catalysts. Compared to the previously known methods to generate hydrogen from liquid feedstocks, the systems presented here can be operated at room temperature without the need for any high-temperature reforming processes, and the hydrogen produced can then be directly used in fuel cells. A variety of Ru precursors and phosphine ligands were investigated for the decomposition of formic acid/amine adducts. These catalytic systems are particularly interesting for the generation of H2 for new applications in portable electric devices.
Aerodynamic characteristics of the North American Rockwell space shuttle delta-wing orbiter (110C) alone and with belly-mounted external oxygen/hydrogen tanks (M equals 0.6 to 5.0)

NASA Technical Reports Server (NTRS)

Allen, E. C.

1972-01-01

Experimental aerodynamic investigations were conducted at the MSFC 14 x 14 inch trisonic wind tunnel on a .0044 scale model of the space shuttle orbiter, 110C. The test configurations included the orbiter alone and with external oxygen/hydrogen belly tanks. The six component aerodynamic force and moment data obtained cover a Mach number range from 0.6 to 4.96 at angles of attack from 10 to 60 deg at 0 deg sideslip angle and -10 to 10 deg at -6 deg sideslip angle. Reynolds number per unit length varied somewhat with Mach number but was a nominal 6.8 million per foot.
Storage and release of hydrogen cyanide in a chelicerate (Oribatula tibialis)

PubMed Central

Brückner, Adrian; Raspotnig, Günther; Wehner, Katja; Meusinger, Reinhard; Norton, Roy A.; Heethoff, Michael

2017-01-01

Cyanogenesis denotes a chemical defensive strategy where hydrogen cyanide (HCN, hydrocyanic or prussic acid) is produced, stored, and released toward an attacking enemy. The high toxicity and volatility of HCN requires both chemical stabilization for storage and prevention of accidental self-poisoning. The few known cyanogenic animals are exclusively mandibulate arthropods (certain myriapods and insects) that store HCN as cyanogenic glycosides, lipids, or cyanohydrins. Here, we show that cyanogenesis has also evolved in the speciose Chelicerata. The oribatid mite Oribatula tibialis uses the cyanogenic aromatic ester mandelonitrile hexanoate (MNH) for HCN storage, which degrades via two different pathways, both of which release HCN. MNH is emitted from exocrine opisthonotal oil glands, which are potent organs for chemical defense in most oribatid mites. PMID:28289203
High capacity hydrogen storage nanocomposite materials

DOEpatents

Zidan, Ragaiy; Wellons, Matthew S.

2017-12-12

A novel hydrogen absorption material is provided comprising a mixture of a lithium hydride with a fullerene. The subsequent reaction product provides for a hydrogen storage material which reversibly stores and releases hydrogen at temperatures of about 270.degree. C.
High capacity hydrogen storage nanocomposite materials

DOEpatents

Zidan, Ragaiy; Wellons, Matthew S

2015-02-03

A novel hydrogen absorption material is provided comprising a mixture of a lithium hydride with a fullerene. The subsequent reaction product provides for a hydrogen storage material which reversibly stores and releases hydrogen at temperatures of about 270.degree. C.
Enhanced thermophilic fermentative hydrogen production from cassava stillage by chemical pretreatments.

PubMed

Wang, Wen; Luo, Gang; Xie, Li; Zhou, Qi

2013-01-01

Acid and alkaline pretreatments for enhanced hydrogen production from cassava stillage were investigated in the present study. The result showed that acid pretreatment was suitable for enhancement of soluble carbohydrate while alkaline pretreatment stimulated more soluble total organic carbon production from cassava stillage. Acid pretreatment thereby has higher capacity to promote hydrogen production compared with alkaline pretreatment. Effects of pretreatment temperature, time and acid concentration on hydrogen production were also revealed by response surface methodology. The results showed that the increase of all factors increased the soluble carbohydrate production, whereas hydrogen production was inhibited when the factors exceeded their optimal values. The optimal conditions for hydrogen production were pretreatment temperature 89.5 °C, concentration 1.4% and time 69 min for the highest hydrogen production of 434 mL, 67% higher than raw cassava stillage.
Hydrogenation of carbonaceous materials

DOEpatents

Friedman, Joseph; Oberg, Carl L.; Russell, Larry H.

1980-01-01

A method for reacting pulverized coal with heated hydrogen-rich gas to form hydrocarbon liquids suitable for conversion to fuels wherein the reaction involves injection of pulverized coal entrained in a minimum amount of gas and mixing the entrained coal at ambient temperature with a separate source of heated hydrogen. In accordance with the present invention, the hydrogen is heated by reacting a small portion of the hydrogen-rich gas with oxygen in a first reaction zone to form a gas stream having a temperature in excess of about 1000.degree. C. and comprising a major amount of hydrogen and a minor amount of water vapor. The coal particles then are reacted with the hydrogen in a second reaction zone downstream of the first reaction zone. The products of reaction may be rapidly quenched as they exit the second reaction zone and are subsequently collected.
Thermal properties of hydrogenated liquid natural rubber

DOE Office of Scientific and Technical Information (OSTI.GOV)

Jamaluddin, Naharullah; Abdullah, Ibrahim; Yusoff, Siti Fairus M.

Natural rubber (NR) was modified to form liquid natural rubber (LNR) via photooxidative degradation. Hydrogenated liquid natural rubber (HLNR) was synthesized by using diimide as source of hydrogen which the diimide is produced by thermolysis of p-toluenesulfonyl hydrazide (TSH). The structure of HLNR was characterized by determining the changes of main peaks in Fourier Transform infrared and nuclear magnetic resonance spectra after hydrogenation. Thermogravimetric analysis showed that the HLNR had higher decomposition temperature compared to LNR and the decomposition temperature is directly proportional to the percentage of conversion.
Thermal properties of hydrogenated liquid natural rubber

NASA Astrophysics Data System (ADS)

Jamaluddin, Naharullah; Abdullah, Ibrahim; Yusoff, Siti Fairus M.

2015-09-01

Natural rubber (NR) was modified to form liquid natural rubber (LNR) via photooxidative degradation. Hydrogenated liquid natural rubber (HLNR) was synthesized by using diimide as source of hydrogen which the diimide is produced by thermolysis of p-toluenesulfonyl hydrazide (TSH). The structure of HLNR was characterized by determining the changes of main peaks in Fourier Transform infrared and nuclear magnetic resonance spectra after hydrogenation. Thermogravimetric analysis showed that the HLNR had higher decomposition temperature compared to LNR and the decomposition temperature is directly proportional to the percentage of conversion.
Diffusion of hydrogen in a hydrogen-saturated tungsten

NASA Astrophysics Data System (ADS)

Krstic, Predrag; Kaganovich, Igor

2015-11-01

Hydrogen diffusion in monoscrystalline tungsten is studied by molecular dynamics with BOP potential in function of hydrogen concentration and temperature. Tungsten surface is prepared by cumulative irradiation of the 25 eV deuterium atoms at various fluences. The diffusion coefficients for T>500K and various D concentrations were calculated from the average slope of the mean square displacements of deuterium as functions of time. The accumulation of deuterium suppresses its diffusion at all temperatures. The results are in a reasonable agreement with the existing experiments. Supported by the LDRD of PPPL.
Impact of temperature and substrate concentration on degradation rates of acetate, propionate and hydrogen and their links to microbial community structure.

PubMed

Zhao, Jing; Westerholm, Maria; Qiao, Wei; Yin, Dongmin; Bi, Shaojie; Jiang, Mengmeng; Dong, Renjie

2018-05-01

The present study investigates the conversion of acetate, propionate and hydrogen consumption linked to the microbial community structure and related to temperature and substrate concentration. Biogas reactors were continuously fed with coffee powder (20 g-COD/L) or acetate (20, 40, and 60 g-COD/L) and operated for 193 days at 37 °C or 55 °C conditions. Starting HRT was 23 days which was then reduced to 7 days. The kinetics of acetate and propionate degradation and hydrogen consumption rates were measured in batch assays. At HRT 7 days, the degradation rate of propionate was higher in thermophilic batches, while acetate degradation rate was higher at mesophilic conditions. The gaseous hydrogen consumption in acetate reactors increased proportionally with temperature and substrate concentration, while the dissolved hydrogen was not affected. The relative high abundance of hydrogentrophic methanogens indicated that the methanogenesis was directed towards the syntrophic acetate oxidation pathway at high acetate concentration and high temperature. Copyright © 2018 Elsevier Ltd. All rights reserved.
Catalytic decomposition of methanol for onboard hydrogen generation

NASA Technical Reports Server (NTRS)

Brabbs, T.

1978-01-01

The steam reformation of an equimolar mixture of methanol and water on a copper chromite catalyst was studied at three furnace temperatures and at feed space velocities from 800 to 2600 per hour. The hydrogen space velocity could be related to the reactor temperature by the equation Sv = A exp (-omega T), where A and omega are constants determined for each value of alpha and T is temperature. At a methanol conversion of 0.87 and a reactor temperature of 589 K, the extrapolated value of the hydrogen space velocity was 9400 per hour. This velocity was used to estimate the size of an onboard hydrogen reactor for automotive applications. Such a reactor would need only about 0.8 liter of catalyst to produce 7630 STP liters (1.5 lb) of hydrogen per hour. This quantity of catalyst would fit into nine tubes 17.8 centimeters along and 2.54 centimeters in inside diameter, which is smaller than most mufflers. The reactor products would contain 12 to 13 percent more chemical energy than the incoming methanol and water.
Low temperature IR spectroscopic study of torsional vibrations of taurine

NASA Astrophysics Data System (ADS)

Bajaj, Naini; Bhatt, Himal; Vishwakarma, S. R.; Thomas, Susy; Murli, C.; Deo, M. N.

2018-04-01

The hydrogen bonding network in amino acids can give information about the structural stability under varying thermodynamic conditions such as temperature and pressure. We have carried out low temperature IR spectroscopic studies on Taurine, an amino acid with various bio-chemical applications in physiology and synthesis, in order to observe the behaviour of torsional modes, i.e. τ(CSH) and τ(NH3), which are very sensitive to the hydrogen bonding interactions. It was observed that the CSH torsional mode showed splitting at low temperature of nearly 250 K and the bandwidth shows linear temperature dependence, which can be attributed to anharmonicity. Another torsional mode, τ(NH3) showed no splitting, but the bandwidth has non-linear temperature dependence. This can be due to orientational changes at low temperature. These observations are strong evidences for a hydrogen bond reorientation induced phase transition at 250 K.
Ethanol accumulation during severe drought may signal tree vulnerability to detection and attack by bark beetles

Treesearch

Rick G. Kelsey; D. Gallego; F.J. Sánchez-Garcia; J.A. Pajares

2014-01-01

Tree mortality from temperature-driven drought is occurring in forests around the world, often in conjunction with bark beetle outbreaks when carbon allocation to tree defense declines. Physiological metrics for detecting stressed trees with enhanced vulnerability prior to bark beetle attacks remain elusive. Ethanol, water, monoterpene concentrations, and composition...
Acid-catalyzed hydrogenation during kerosene hydrodewaxing over H/ZSM-5

DOE Office of Scientific and Technical Information (OSTI.GOV)

Longstaff, D.C.; Hanson, F.V.

1996-11-01

Hydrogen addition to the products derived from cracking kerosene over H/ZSM-5 was observed at hydrogen pressures between 4.1-8.7 MPa and at 373-390{degrees}C. At low pressures, kerosene cracking over H/ZSM-5 yielded typical cracked products: aromatics, as well as low molecular weight saturates and olefins. Endothermic reactor temperature profiles were also observed, indicative of cracking reactions. At high hydrogen partial pressures product selectivity was altered in that kerosene cracking gave high yields of low molecular weight paraffins and low yields of olefins and aromatics. Reactor temperature profiles were exothermic, indicative of hydrocracking reactions. A mechanism for acid catalyzed hydrogenation is suggested. Althoughmore » hydrogenation was not observed at lower hydrogen pressures, hydrogen proved beneficial in maintaining catalyst activity at a stable level. Lost catalyst activity was restored by maintaining the catalyst under static hydrogen at 1.4 MPa and 370{degrees}C for 16h. 36 refs., 14 figs., 3 tabs.« less
Investigation of nose bluntness and angle of attack effects on slender bodies in viscous hypersonic flows

NASA Technical Reports Server (NTRS)

Sehgal, A. K.; Tiwari, S. N.; Singh, D. J.

1991-01-01

Hypersonic flows over cones and straight biconic configurations are calculated for a wide range of free stream conditions in which the gas behind the shock is treated as perfect. Effect of angle of attack and nose bluntness on these slender cones in air is studied extensively. The numerical procedures are based on the solution of complete Navier-Stokes equations at the nose section and parabolized Navier-Stokes equations further downstream. The flow field variables and surface quantities show significant differences when the angle of attack and nose bluntness are varied. The complete flow field is thoroughly analyzed with respect to velocity, temperature, pressure, and entropy profiles. The post shock flow field is studied in detail from the contour plots of Mach number, density, pressure, and temperature. The effect of nose bluntness for slender cones persists as far as 200 nose radii downstream.
Planar ultra thin glass seals with optical fiber interface for monitoring tamper attacks on security eminent components

NASA Astrophysics Data System (ADS)

Thiel, M.; Flachenecker, G.; Schade, W.; Gorecki, C.; Thoma, A.; Rathje, R.

2017-11-01

Optical seals consisting of waveguide Bragg grating sensor structures in ultra thin glass transparencies have been developed to cover security relevant objects for detection of unauthorized access. For generation of optical signature in the seals, femtosecond laser pulses were used. The optical seals were connected with an optical fiber to enable external read out of the seal. Different attack scenarios for getting undetected access to the object, covered by the seal, were proven and evaluated. The results presented here, verify a very high level of security. An unauthorized detaching and subsequent replacement by original or copy of the seals for tampering would be accompanied with a very high technological effort, posing a substantial barrier towards an attacker. Additionally, environmental influences like temperature effects have a strong but reproducible influence on signature, which in context of a temperature reference database increases the level of security significantly.
Innovative techniques for the production of energetic radicals for lunar processing including cold plasma processing of local planetary ores

NASA Technical Reports Server (NTRS)

Bullard, D.; Lynch, D. C.

1992-01-01

Hydrogen reduction of ilmenite has been studied by a number of investigators as a potential means for recovery of oxygen from lunar soil. Interest in this process has always rested with the simplicity of the flow diagram and the utilization of established technology. Effective utilization of hydrogen in the reduction process at temperatures of 1200 C and below has always been disappointing and, as such, has led other investigators to focus attention on other systems. Effective utilization of hydrogen in the reduction of ilmenite can be significantly enhanced in the presence of a non-equilibrium hydrogen plasma. Ilmenite at solid specimen temperatures of 600 C to 970 C were reacted in a hydrogen plasma. Those experiments revealed that hydrogen utilization can be significantly enhanced. At a specimen temperature of 850 C the fraction of H2 reacted was 24 percent compared to the 7 percent theoretical limit calculated with thermodynamic theory for the same temperature. An added advantage for a hydrogen plasma involves further reduction of TiO2. Reduction of the iron oxide in ilmenite yields TiO2 and metallic iron as by products. Titanium forms a number of oxides including TiO, Ti2O3, Ti3O5 and the Magneli oxides (Ti4O7 to Ti50O99). In conventional processing of ilmenite with hydrogen it is possible to reduce TiO2 to Ti7O13 within approximately an hour, but with poor utilization of hydrogen on the order of one mole of H2 per thousand. In the cold or non-equilibrium plasma TiO2 can be rapidly reduced to Ti2O3 with hydrogen utilization exceeding 10 percent. Based on design considerations of the plasma reactor greater utilization of the hydrogen in the reduction of TiO2 is possible.

Cyclic Oxidation and Hot Corrosion of NiCrY-Coated Disk Superalloy

NASA Technical Reports Server (NTRS)

Gabb, Tim; Miller, R. A.; Sudbrack, C. K.; Draper, S. L.; Nesbitt, J.; Telesman, J.; Ngo, V.; Healy, J.

2015-01-01

Powder metallurgy disk superalloys have been designed for higher engine operating temperatures through improvement of their strength and creep resistance. Yet, increasing disk application temperatures to 704 C and higher could enhance oxidation and activate hot corrosion in harmful environments. Protective coatings could be necessary to mitigate such attack. Cylindrical coated specimens of disk superalloys LSHR and ME3 were subjected to thermal cycling to produce cyclic oxidation in air at a maximum temperature of 760 C. The effects of substrate roughness and coating thickness on coating integrity after cyclic oxidation were considered. Selected coated samples that had cyclic oxidation were then subjected to accelerated hot corrosion tests. The effects of this cyclic oxidation on resistance to subsequent hot corrosion attack were examined.
Was Ferrocyanide a Prebiotic Reagent?

NASA Technical Reports Server (NTRS)

Keefe, Anthony D.; Miller, Stanley L.

1996-01-01

Hydrogen cyanide is the starting material for a diverse array of prebiotic syntheses, including those of amino acids and purines. Hydrogen cyanide also reacts with ferrous ions to give ferrocyanide, and so it is possible that ferrocyanide was common in the early ocean. This can only be true if the hydrogen cyanide concentration was high enough and the rate of reaction of cyanide with ferrous ions was fast enough. We show experimentally that the rate of formation of ferrocyanide is rapid even at low concentrations of hydrogen cyanide in the pH range 6-8, and therefore an equilibrium calculation is valid. The equilibrium concentrations of ferrocyanide are calculated as a function of hydrogen cyanide concentration, pH and temperature. The steady state concentration of hydrogen cyanide depends on the rate of synthesis by electric discharges and ultraviolet light and the rate of hydrolysis, which depends on pH and temperature. Our conclusions show that ferrocyanide was a major species in the prebiotic ocean only at the highest production rates of hydrogen cyanide in a strongly reducing atmosphere and at temperatures of 0 C or less, although small amounts would have been present at lower hydrogen cyanide production rates. The prebiotic application of ferrocyanide as a source of hydrated electrons, as a photochemical replication process, and in semi-permeable membranes is discussed.
Hydrogen desorption using honeycomb finned heat exchangers integrated in adsorbent storage systems

DOE Office of Scientific and Technical Information (OSTI.GOV)

Corgnale, Claudio; Hardy, Bruce; Chahine, Richard

One of the main technical hurdles associated with adsorbent based hydrogen storage systems is relative to their ability to discharge hydrogen effectively, as dictated by fuel cell requirements. In this study, a new honeycomb finned heat exchanger concept was examined to evaluate its potential as a heat transfer system for hydrogen desorption. A bench scale 0.5 L vessel was equipped with the proposed heat exchanger, filled with MOF-5® adsorbent material. The heating power, required to desorb hydrogen, was provided by a 100 W electric heater placed in the center of the honeycomb structure. Two desorption tests, at room temperature andmore » under cryogenic temperatures, were carried out to evaluate the hydrogen desorption performance of the proposed system under different operating conditions. The bench scale vessel performance was verified from both an experimental and a modeling point of view, demonstrating the ability to desorb about 45% of the adsorbed hydrogen in reduced time and applying low heating power. Further modeling analyses were also carried out showing the potential of the proposed system to reach high hydrogen discharging rates at cryogenic temperature conditions and operating pressures between 100 bar and 5 bar. The proposed adsorption system also demonstrated to be able to discharge all the available hydrogen in less than 500 s operating at cryogenic conditions and with a nominal heating power of 100 W.« less
Hydrogen desorption using honeycomb finned heat exchangers integrated in adsorbent storage systems

DOE PAGES

Corgnale, Claudio; Hardy, Bruce; Chahine, Richard; ...

2018-03-01

One of the main technical hurdles associated with adsorbent based hydrogen storage systems is relative to their ability to discharge hydrogen effectively, as dictated by fuel cell requirements. In this study, a new honeycomb finned heat exchanger concept was examined to evaluate its potential as a heat transfer system for hydrogen desorption. A bench scale 0.5 L vessel was equipped with the proposed heat exchanger, filled with MOF-5® adsorbent material. The heating power, required to desorb hydrogen, was provided by a 100 W electric heater placed in the center of the honeycomb structure. Two desorption tests, at room temperature andmore » under cryogenic temperatures, were carried out to evaluate the hydrogen desorption performance of the proposed system under different operating conditions. The bench scale vessel performance was verified from both an experimental and a modeling point of view, demonstrating the ability to desorb about 45% of the adsorbed hydrogen in reduced time and applying low heating power. Further modeling analyses were also carried out showing the potential of the proposed system to reach high hydrogen discharging rates at cryogenic temperature conditions and operating pressures between 100 bar and 5 bar. The proposed adsorption system also demonstrated to be able to discharge all the available hydrogen in less than 500 s operating at cryogenic conditions and with a nominal heating power of 100 W.« less
Thermal stability of some aircraft turbine fuels derived from oil shale and coal

NASA Technical Reports Server (NTRS)

Reynolds, T. W.

1977-01-01

Thermal stability breakpoint temperatures are shown for 32 jet fuels prepared from oil shale and coal syncrudes by various degrees of hydrogenation. Low severity hydrotreated shale oils, with nitrogen contents of 0.1 to 0.24 weight percent, had breakpoint temperatures in the 477 to 505 K (400 to 450 F) range. Higher severity treatment, lowering nitrogen levels to 0.008 to 0.017 weight percent, resulted in breakpoint temperatures in the 505 to 533 K (450 to 500 F) range. Coal derived fuels showed generally increasing breakpoint temperatures with increasing weight percent hydrogen, fuels below 13 weight percent hydrogen having breakpoints below 533 K (500 F). Comparisons are shown with similar literature data.
Liquid Transfer Cryogenic Test Facility: Initial hydrogen and nitrogen no-vent fill data

NASA Astrophysics Data System (ADS)

Moran, Matthew E.; Nyland, Ted W.; Papell, S. Stephen

1990-03-01

The Liquid Transfer Cryogenic Test Facility is a versatile testbed for ground-based cryogenic fluid storage, handling, and transfer experimentation. The test rig contains two well instrumented tanks, and a third interchangeable tank, designed to accommodate liquid nitrogen or liquid hydrogen testing. The internal tank volumes are approx. 18, 5, and 1.2 cu. ft. Tank pressures can be varied from 2 to 30 psia. Preliminary no vent fill tests with nitrogen and hydrogen were successfully completed with the test rig. Initial results indicate that no vent fills of nitrogen above 90 percent full are achievable using this test configuration, in a 1-g environment, and with inlet liquid temperatures as high as 143 R, and an average tank wall temperature of nearly 300 R. This inlet temperature corresponds to a saturation pressure of 19 psia for nitrogen. Hydrogen proved considerably more difficult to transfer between tanks without venting. The highest temperature conditions resulting in a fill level greater than 90 percent were with an inlet liquid temperature of 34 R, and an estimated tank wall temperature of slightly more than 100 R. Saturation pressure for hydrogen at this inlet temperature is 10 psia. All preliminary no vent fill tests were performed with a top mounted full cone nozzle for liquid injection. The nozzle produces a 120 degree conical droplet spray at a differential pressure of 10 psi. Pressure in the receiving tank was held to less than 30 psia for all tests.
Liquid Transfer Cryogenic Test Facility: Initial hydrogen and nitrogen no-vent fill data

NASA Technical Reports Server (NTRS)

Moran, Matthew E.; Nyland, Ted W.; Papell, S. Stephen

1990-01-01

The Liquid Transfer Cryogenic Test Facility is a versatile testbed for ground-based cryogenic fluid storage, handling, and transfer experimentation. The test rig contains two well instrumented tanks, and a third interchangeable tank, designed to accommodate liquid nitrogen or liquid hydrogen testing. The internal tank volumes are approx. 18, 5, and 1.2 cu. ft. Tank pressures can be varied from 2 to 30 psia. Preliminary no vent fill tests with nitrogen and hydrogen were successfully completed with the test rig. Initial results indicate that no vent fills of nitrogen above 90 percent full are achievable using this test configuration, in a 1-g environment, and with inlet liquid temperatures as high as 143 R, and an average tank wall temperature of nearly 300 R. This inlet temperature corresponds to a saturation pressure of 19 psia for nitrogen. Hydrogen proved considerably more difficult to transfer between tanks without venting. The highest temperature conditions resulting in a fill level greater than 90 percent were with an inlet liquid temperature of 34 R, and an estimated tank wall temperature of slightly more than 100 R. Saturation pressure for hydrogen at this inlet temperature is 10 psia. All preliminary no vent fill tests were performed with a top mounted full cone nozzle for liquid injection. The nozzle produces a 120 degree conical droplet spray at a differential pressure of 10 psi. Pressure in the receiving tank was held to less than 30 psia for all tests.
Demonstrated survivability of a high temperature optical fiber cable on a 1500 pound thrust rocket chamber

NASA Technical Reports Server (NTRS)

Sovie, Amy L.

1992-01-01

A demonstration of the ability of an existing optical fiber cable to survive the harsh environment of a rocket engine was performed at the NASA Lewis Research Center. The intent of this demonstration was to prove the feasibility of applying fiber optic technology to rocket engine instrumentation systems. Extreme thermal transient tests were achieved by wrapping a high temperature optical fiber, which was cablized for mechanical robustness, around the combustion chamber outside wall of a 1500 lb Hydrogen-Oxygen rocket engine. Additionally, the fiber was wrapped around coolant inlet pipes which were subject to near liquid hydrogen temperatures. Light from an LED was sent through the multimode fiber, and output power was monitored as a function of time while the engine was fired. The fiber showed no mechanical damage after 419 firings during which it was subject to transients from 30 K to 350 K, and total exposure time to near liquid hydrogen temperatures in excess of 990 seconds. These extreme temperatures did cause attenuation greater than 3 dB, but the signal was fully recovered at room temperature. This experiment demonstrates that commercially available optical fiber cables can survive the environment seen by a typical rocket engine instrumentation system, and disclose a temperature-dependent attenuation observed during exposure to near liquid hydrogen temperatures.
Alternative Fuels Data Center: Hydrogen Production and Distribution

Science.gov Websites

created by reacting natural gas with high-temperature steam. The carbon monoxide is reacted with water to synthesis gas can also be created by reacting coal or biomass with high-temperature steam and oxygen in a : Renewable liquid fuels, such as ethanol, are reacted with high-temperature steam to produce hydrogen near
Plasma parameter diagnosis using hydrogen emission spectra of a quartz-chamber 2.45 GHz ECRIS at Peking University

NASA Astrophysics Data System (ADS)

Wu, WenBin; Ren, HaiTao; Peng, ShiXiang; Xu, Yuan; Wen, JiaMei; Zhang, Tao; Zhang, JingFeng; Zhang, AiLin; Sun, Jiang; Guo, ZhiYu; Chen, JiaEr

2018-04-01

A quartz-chamber 2.45 GHz electron cyclotron resonance ion source (ECRIS) was designed for diagnostic purposes at Peking University [Patent Number: ZL 201110026605.4]. This ion source can produce a maximum 84 mA hydrogen ion beam at 50 kV with a duty factor of 10%. The root-mean-square (RMS) emittance of this beam is less than 0.12π mm mrad. In our initial work, the electron temperature and electron density inside the plasma chamber had been measured with the line intensity ratio of noble gases. Based on these results, the atomic and molecular emission spectra of hydrogen were applied to determine the dissociation degree of hydrogen and the vibrational temperature of hydrogen molecules in the ground state, respectively. Measurements were performed at gas pressures from 4×10-4 to 1×10-3 Pa and at input peak RF power ranging from 1000 to 1800 W. The dissociation degree of hydrogen in the range of 0.5%-10% and the vibrational temperature of hydrogen molecules in the ground state in the range of 3500-8500 K were obtained. The plasma processes inside this ECRIS chamber were discussed based on these results.
Performance assessment of low pressure nuclear thermal propulsion

NASA Technical Reports Server (NTRS)

Gerrish, H. P., Jr.; Doughty, G. E.

1993-01-01

A low pressure nuclear thermal propulsion (LPNTP) system, which takes advantage of hydrogen dissociation/recombination, was proposed as a means of increasing engine specific impulse (Isp). The effect of hydrogen dissociation/recombination on LPNTP Isp is examined. A two-dimensional computer model was used to show that the optimum chamber pressure is approximately 100 psia (at a chamber temperature of 3,000 K), with an Isp approximately 15 s higher than at 1,000 psia. At high chamber temperatures and low chamber pressures, the increase in Isp is due to both lower average molecular weights caused by dissociation and added kinetic energy from monatomic hydrogen recombination. Monatomic hydrogen recombination increases the Isp more then hydrogen dissociation. Variations in the mole fraction of monatomic hydrogen are similar to variations in static pressure along the axial nozzle position. Most recombination occurs close to the nozzle throat. Practical variations in nozzle geometry have minimal impact on recombination. Other models which can simulate a wider range of nozzle designs should be used in the future. The uncertainty of the hydrogen kinetic reaction rates at high temperatures (approximately 3,000 K) affects the accuracy of the analysis and should be verified with simple bench tests.
Development of optical diagnostics for performance evaluation of arcjet thrusters

NASA Technical Reports Server (NTRS)

Cappelli, Mark A.

1995-01-01

Laser and optical emission-based measurements have been developed and implemented for use on low-power hydrogen arcjet thrusters and xenon-propelled electric thrusters. In the case of low power hydrogen arcjets, these laser induce fluorescence measurements constitute the first complete set of data that characterize the velocity and temperature field of such a device. The research performed under the auspices of this NASA grant includes laser-based measurements of atomic hydrogen velocity and translational temperature, ultraviolet absorption measurements of ground state atomic hydrogen, Raman scattering measurements of the electronic ground state of molecular hydrogen, and optical emission based measurements of electronically excited atomic hydrogen, electron number density, and electron temperature. In addition, we have developed a collisional-radiative model of atomic hydrogen for use in conjunction with magnetohydrodynamic models to predict the plasma radiative spectrum, and near-electrode plasma models to better understand current transfer from the electrodes to the plasma. In the final year of the grant, a new program aimed at developing diagnostics for xenon plasma thrusters was initiated, and results on the use of diode lasers for interrogating Hall accelerator plasmas has been presented at recent conferences.
Metallic hydrogen

NASA Astrophysics Data System (ADS)

Silvera, Isaac F.; Dias, Ranga

2018-06-01

Hydrogen is the simplest and most abundant element in the Universe. There are two pathways for creating metallic hydrogen under high pressures. Over 80 years ago Wigner and Huntington predicted that if solid molecular hydrogen was sufficiently compressed in the T = 0 K limit, molecules would dissociate to form atomic metallic hydrogen (MH). We have observed this transition at a pressure of 4.95 megabars. MH in this form has probably never existed on Earth or in the Universe; it may be a room temperature superconductor and is predicted to be metastable. If metastable it will have an important technological impact. Liquid metallic hydrogen can also be produced at intermediate pressures and high temperatures and is believed to make up ~90% of the planet Jupiter. We have observed this liquid–liquid transition, also known as the plasma phase transition, at pressures of ~1–2 megabar and temperatures ~1000–2000 K. However, in this paper we shall focus on the Wigner–Huntington transition. We shall discuss the methods used to observe metallic hydrogen at extreme conditions of static pressure in the laboratory, extending our understanding of the phase diagram of the simplest atom in the periodic table.
Investigation of combustion characteristics of methane-hydrogen fuels

NASA Astrophysics Data System (ADS)

Vetkin, A. V.; Suris, A. L.; Litvinova, O. A.

2015-01-01

Numerical investigations of combustion characteristics of methane-hydrogen fuel used at present in tube furnaces of some petroleum refineries are carried out and possible problems related to change-over of existing furnaces from natural gas to methane-hydrogen fuel are analyzed. The effect of the composition of the blended fuel, associated temperature and emissivity of combustion products, temperature of combustion chamber walls, mean beam length, and heat release on variation in the radiation heat flux is investigated. The methane concentration varied from 0 to 100%. The investigations were carried out both at arbitrary given gas temperatures and at effective temperatures determined based on solving a set of equations at various heat-release rates of the combustion chamber and depended on the adiabatic combustion temperature and the temperature at the chamber output. The approximation dependence for estimation of the radiation heat exchange rate in the radiant chamber of the furnace at change-over to fuel with a greater hydrogen content is obtained. Hottel data were applied in the present work in connection with the impossibility to use approximated formulas recommended by the normative method for heat calculation of boilers to determine the gas emissivity, which are limited by the relationship of partial pressures of water steam and carbon dioxide in combustion products . The effect of the methane-hydrogen fuel on the equilibrium concentration of nitrogen oxides is also investigated.
Method of treating intermetallic alloy hydrogenation/oxidation catalysts for improved impurity poisoning resistance, regeneration and increased activity

DOEpatents

Wright, Randy B.

1992-01-01

Alternate, successive high temperature oxidation and reduction treatments, in either order, of intermetallic alloy hydrogenation and intermetallic alloy oxidation catalysts unexpectedly improves the impurity poisoning resistance, regeneration capacity and/or activity of the catalysts. The particular alloy, and the final high temperature treatment given alloy (oxidation or reduction) will be chosen to correspond to the function of the catalyst (oxidation or hydrogenation).
A theoretical study of the hydrogen-storage potential of (H2)4CH4 in metal organic framework materials and carbon nanotubes.

PubMed

Li, Q; Thonhauser, T

2012-10-24

The hydrogen-methane compound (H(2))(4)CH(4)-or for short H4M-is one of the most promising hydrogen-storage materials. This van der Waals compound is extremely rich in molecular hydrogen: 33.3 mass%, not including the hydrogen bound in CH(4); including it, we reach even 50.2 mass%. Unfortunately, H4M is not stable under ambient pressure and temperature, requiring either low temperature or high pressure. In this paper, we investigate the properties and structure of the molecular and crystalline forms of H4M, using ab initio methods based on van der Waals DFT (vdW-DF). We further investigate the possibility of creating the pressures required to stabilize H4M through external agents such as metal organic framework (MOF) materials and carbon nanotubes, with very encouraging results. In particular, we find that certain MOFs can create considerable pressure for H4M in their cavities, but not enough to stabilize it at room temperature, and moderate cooling is still necessary. On the other hand, we find that all the investigated carbon nanotubes can create the high pressures required for H4M to be stable at room temperature, with direct implications for new and exciting hydrogen-storage applications.
Hydrogen environment embrittlement

NASA Technical Reports Server (NTRS)

Gray, H. R.

1972-01-01

Hydrogen embrittlement is classified into three types: internal reversible hydrogen embrittlement, hydrogen reaction embrittlement, and hydrogen environment embrittlement. Characteristics of and materials embrittled by these types of hydrogen embrittlement are discussed. Hydrogen environment embrittlement is reviewed in detail. Factors involved in standardizing test methods for detecting the occurrence of and evaluating the severity of hydrogen environment embrittlement are considered. The effect of test technique, hydrogen pressure, purity, strain rate, stress concentration factor, and test temperature are discussed. Additional research is required to determine whether hydrogen environment embrittlement and internal reversible hydrogen embrittlement are similar or distinct types of embrittlement.
Three-dimensional fuel pin model validation by prediction of hydrogen distribution in cladding and comparison with experiment

DOE Office of Scientific and Technical Information (OSTI.GOV)

Aly, A.; Avramova, Maria; Ivanov, Kostadin

To correctly describe and predict this hydrogen distribution there is a need for multi-physics coupling to provide accurate three-dimensional azimuthal, radial, and axial temperature distributions in the cladding. Coupled high-fidelity reactor-physics codes with a sub-channel code as well as with a computational fluid dynamics (CFD) tool have been used to calculate detailed temperature distributions. These high-fidelity coupled neutronics/thermal-hydraulics code systems are coupled further with the fuel-performance BISON code with a kernel (module) for hydrogen. Both hydrogen migration and precipitation/dissolution are included in the model. Results from this multi-physics analysis is validated utilizing calculations of hydrogen distribution using models informed bymore » data from hydrogen experiments and PIE data.« less
Simulation of Liquid Level, Temperature and Pressure Inside a 2000 Liter Liquid Hydrogen Tank During Truck Transportation

NASA Astrophysics Data System (ADS)

Takeda, Minoru; Nara, Hiroyuki; Maekawa, Kazuma; Fujikawa, Shizuichi; Matsuno, Yu; Kuroda, Tsuneo; Kumakura, Hiroaki

Hydrogen is an ultimate energy source because only water is produced after the chemical reaction of hydrogen and oxygen. In the near future, a large amount of hydrogen, produced using sustainable/renewable energy, is expected to be consumed. Since liquid hydrogen (LH2) has the advantage of high storage efficiency, it is expected to be the ultimate medium for the worldwide storage and transportation of large amounts of hydrogen. To make a simulation model of the sloshing of LH2 inside a 2000 liter tank, simulation analyses of LH2 surface oscillation, temperature and pressure inside the tank during a truck transportation have been carried out using a multipurpose software ANSYS CFX. Numerical results are discussed in comparison with experimental results.
Measurements of the structure of an ionizing shock wave in a hydrogen-helium mixture

NASA Technical Reports Server (NTRS)

Leibowitz, L. P.

1972-01-01

Shock structure during ionization of a hydrogen-helium mixture was studied using hydrogen line and continuum emission measurements. A reaction scheme is proposed which includes hydrogen dissociation and a two-step excitation-ionization mechanism for hydrogen ionization by atom-atom and atom-electron collisions. Agreement was achieved between numerical calculations and measurements of emission intensity as a function of time for shock velocities from 13 to 20 km/sec in a 0.208 H2 - 0.792 He mixture. The electron temperature was found to be significantly different from the heavy particle temperature during much of the ionization process. Similar time histories for H beta and continuum emission indicate upper level populations of hydrogen in equilibrium with the electron concentration during the relaxation process.

Measurements of the structure of an ionizing shock wave in a hydrogen-helium mixture.

NASA Technical Reports Server (NTRS)

Leibowitz, L. P.

1973-01-01

Shock structure during ionization of a hydrogen-helium mixture has been followed using hydrogen line and continuum emission measurements. A reaction scheme is proposed which includes hydrogen dissociation and a two-step excitation-ionization mechanism for hydrogen ionization by atom-atom and atom-electron collisions. Agreement has been achieved between numerical calculations and measurements of emission intensity as a function of time for shock velocities from 13 to 20 km/sec in a 0.208 H2-0.792 He mixture. The electron temperature was found to be significantly different from the heavy particle temperature during much of the ionization process. Similar time histories for H beta and continuum emission indicate upper level populations of hydrogen in equilibrium with the electron concentration during the relaxation process.
Ice method for production of hydrogen clathrate hydrates

DOEpatents

Lokshin, Konstantin [Santa Fe, NM; Zhao, Yusheng [Los Alamos, NM

2008-05-13

The present invention includes a method for hydrogen clathrate hydrate synthesis. First, ice and hydrogen gas are supplied to a containment volume at a first temperature and a first pressure. Next, the containment volume is pressurized with hydrogen gas to a second higher pressure, where hydrogen clathrate hydrates are formed in the process.
Investigation of hydrogen bubbles behavior in tungsten by high-flux hydrogen implantation

NASA Astrophysics Data System (ADS)

Zhao, Jiangtao; Meng, Xuan; Guan, Xingcai; Wang, Qiang; Fang, Kaihong; Xu, Xiaohui; Lu, Yongkai; Gao, Jun; Liu, Zhenlin; Wang, Tieshan

2018-05-01

Hydrogen isotopes retention and bubbles formation are critical issues for tungsten as plasma-facing material in future fusion reactors. In this work, the formation and growing up behavior of hydrogen bubbles in tungsten were investigated experimentally. The planar TEM samples were implanted by 6.0keV hydrogens to a fluence of 3.38 ×1018 H ṡ cm-2 at room temperature, and well-defined hydrogen bubbles were observed by TEM. It was demonstrated that hydrogen bubbles formed when exposed to a fluence of 1.5 ×1018 H ṡ cm-2 , and the hydrogen bubbles grew up with the implantation fluence. In addition, the bubbles' size appeared larger with higher beam flux until saturated at a certain flux, even though the total fluence was kept the same. Finally, in order to understand the thermal annealing effect on the bubbles behavior, hydrogen-implanted samples were annealed at 400, 600, 800, and 1000 °C for 3 h. It was obvious that hydrogen bubbles' morphology changed at temperatures higher than 800 °C.
Spectroscopic and Computational Investigations of a Mononuclear Manganese(IV)-Oxo Complex Reveal Electronic Structure Contributions to Reactivity

DOE PAGES

Leto, Domenick F.; Massie, Allyssa A.; Rice, Derek B.; ...

2016-11-01

The mononuclear Mn(IV)-oxo complex [Mn IV(O)(N4py)] 2+, where N4py is the pentadentate ligand N,N-bis(2-pyridylmethyl)-N-bis(2-pyridyl)methylamine, we propose to attack C–H bonds by an excited-state reactivity pattern [Cho, K.-B.; Shaik, S.; Nam, W. J. Phys. Chem. Lett. 2012, 3, 2851-2856 (DOI: 10.1021/jz301241z)]. In this model, a 4E excited state is utilized to provide a lower-energy barrier for hydrogen-atom transfer. This proposal is intriguing, as it offers both a rationale for the relatively high hydrogen-atom-transfer reactivity of [Mn IV(O)(N4py)] 2+ and a guideline for creating more reactive complexes through ligand modification. Here we employ a combination of electronic absorption and variable-temperature magnetic circularmore » dichroism (MCD) spectroscopy to experimentally evaluate this excited-state reactivity model. Using these spectroscopic methods, in conjunction with time-dependent density functional theory (TD-DFT) and complete-active space self-consistent-field calculations (CASSCF), we define the ligand-field and charge-transfer excited states of [MnIV(O)(N4py)]2+. Through a graphical analysis of the signs of the experimental C-term MCD signals, we unambiguously assign a low-energy MCD feature of [Mn IV(O)(N4py)] 2+ as the 4E excited state predicted to be involved in hydrogen-atom-transfer reactivity. The CASSCF calculations predict enhanced Mn III-oxyl character on the excited-state 4E surface, consistent with previous DFT calculations. Potential-energy surfaces, developed using the CASSCF methods, are used to determine how the energies and wave functions of the ground and excited states evolved as a function of Mn=O distance. Furthermore, the unique insights into ground- and excited-state electronic structure offered by these spectroscopic and computational studies are harmonized with a thermodynamic model of hydrogen-atom-transfer reactivity, which predicts a correlation between transition-state barriers and driving force« less
Spectroscopic and Computational Investigations of a Mononuclear Manganese(IV)-Oxo Complex Reveal Electronic Structure Contributions to Reactivity

DOE Office of Scientific and Technical Information (OSTI.GOV)

Leto, Domenick F.; Massie, Allyssa A.; Rice, Derek B.

The mononuclear Mn(IV)-oxo complex [Mn IV(O)(N4py)] 2+, where N4py is the pentadentate ligand N,N-bis(2-pyridylmethyl)-N-bis(2-pyridyl)methylamine, we propose to attack C–H bonds by an excited-state reactivity pattern [Cho, K.-B.; Shaik, S.; Nam, W. J. Phys. Chem. Lett. 2012, 3, 2851-2856 (DOI: 10.1021/jz301241z)]. In this model, a 4E excited state is utilized to provide a lower-energy barrier for hydrogen-atom transfer. This proposal is intriguing, as it offers both a rationale for the relatively high hydrogen-atom-transfer reactivity of [Mn IV(O)(N4py)] 2+ and a guideline for creating more reactive complexes through ligand modification. Here we employ a combination of electronic absorption and variable-temperature magnetic circularmore » dichroism (MCD) spectroscopy to experimentally evaluate this excited-state reactivity model. Using these spectroscopic methods, in conjunction with time-dependent density functional theory (TD-DFT) and complete-active space self-consistent-field calculations (CASSCF), we define the ligand-field and charge-transfer excited states of [MnIV(O)(N4py)]2+. Through a graphical analysis of the signs of the experimental C-term MCD signals, we unambiguously assign a low-energy MCD feature of [Mn IV(O)(N4py)] 2+ as the 4E excited state predicted to be involved in hydrogen-atom-transfer reactivity. The CASSCF calculations predict enhanced Mn III-oxyl character on the excited-state 4E surface, consistent with previous DFT calculations. Potential-energy surfaces, developed using the CASSCF methods, are used to determine how the energies and wave functions of the ground and excited states evolved as a function of Mn=O distance. Furthermore, the unique insights into ground- and excited-state electronic structure offered by these spectroscopic and computational studies are harmonized with a thermodynamic model of hydrogen-atom-transfer reactivity, which predicts a correlation between transition-state barriers and driving force« less
Engineering Design Elements of a Two-Phase Thermosyphon to Trannsfer NGNP Nuclear Thermal Energy to a Hydrogen Plant

DOE Office of Scientific and Technical Information (OSTI.GOV)

Piyush Sabharwal

2009-07-01

Two hydrogen production processes, both powered by a Next Generation Nuclear Plant (NGNP), are currently under investigation at Idaho National Laboratory. The first is high-temperature steam electrolysis, which uses both heat and electricity; the second is thermo-chemical production through the sulfur iodine process primarily using heat. Both processes require a high temperature (>850°C) for enhanced efficiency; temperatures indicative of the NGNP. Safety and licensing mandates prudently dictate that the NGNP and the hydrogen production facility be physically isolated, perhaps requiring separation of over 100 m.
Studies of the use of high-temperature nuclear heat from an HTGR for hydrogen production

NASA Technical Reports Server (NTRS)

Peterman, D. D.; Fontaine, R. W.; Quade, R. N.; Halvers, L. J.; Jahromi, A. M.

1975-01-01

The results of a study which surveyed various methods of hydrogen production using nuclear and fossil energy are presented. A description of these methods is provided, and efficiencies are calculated for each case. The process designs of systems that utilize the heat from a general atomic high temperature gas cooled reactor with a steam methane reformer and feed the reformer with substitute natural gas manufactured from coal, using reforming temperatures, are presented. The capital costs for these systems and the resultant hydrogen production price for these cases are discussed along with a research and development program.
Application of TAED/H2O2 system for low temperature bleaching of crude cellulose extracted from jute fiber

NASA Astrophysics Data System (ADS)

Wen, Zuoqiang; Zou, Linbo; Wang, Weiming

2018-03-01

Tetraacetylethylenediamine (TAED) activated hydrogen peroxide system had been applied for bleaching of crude cellulose extracted from jute fiber. Comparing with conventional hydrogen peroxide bleaching system, those results showed that bleaching temperature and time could be effectively reduced, and a preferable whiteness could be produced under faint alkaline condition. And the optimum conditions for activated bleaching system could be summarized as molar ratio of H2O2/TAED 1:0.7, pH 8, pure hydrogen peroxide 0.09 mol/L, temperature 70 °C and time 60min.
Vibrational Study of Melatonin and its Radioprotective Activity towards Hydroxyl Radical

NASA Astrophysics Data System (ADS)

Singh, Gurpreet; Kaur, Sarvpreet; Saini, G. S. S.

2011-12-01

Vibrational study of Melatonin (N-acetyl 5-methoxytrypatamin) was done using FTIR and Raman spectroscopy. DFT calculations were employed to the structural analysis of melatonin and to the end products. The theoretical calculations confirmed the different observed vibrational modes. The optimized structure energy calculations of the different end products confirmed the most probable site of the hydroxyl radical attack is the hydrogen attached to nitrogen present in the indole ring.
Change in the microstructure and mechanical properties of drawn pearlitic steel with low-temperature aging

NASA Astrophysics Data System (ADS)

Hirakami, D.; Ushioda, K.; Manabe, T.; Noguchi, K.; Takai, K.; Hata, Y.; Hata, S.; Nakashima, H.

2017-07-01

Hydrogen embrittlement is a serious problem in high-strength steels. Drawn pearlitic steel shows excellent resistance to hydrogen embrittlement despite its high strength, and aging treatment at a low temperature can simultaneously improve its strength and hydrogen-embrittlement resistance. To clarify the mechanism for this we have used thermal desorption analysis (TDA) and the newly developed precession electron diffraction analysis method in the transmission electron microscope. After aging at 100 °C for 10 min, the amount of hydrogen seen amount on the TDA curve reduced at around 100 °C. In contrast, when aging was performed at 300 °C, the hydrogen amount further reduced at around 100 °C and the unevenly deformed lamellar ferrite zone was locally recovered. For the samples that were aged at the low temperature, we confirmed that their yield strength and relaxation stress ratios increased simultaneously with improvement in the hydrogen-embrittlement property. We infer that segregation of carbon or formation of very fine carbide in dislocations during aging is the cause of these behaviors.
Analytical chemical kinetic investigation of the effects of oxygen, hydrogen, and hydroxyl radicals on hydrogen-air combustion

NASA Technical Reports Server (NTRS)

Carson, G. T., Jr.

1974-01-01

Quantitative values were computed which show the effects of the presence of small amounts of oxygen, hydrogen, and hydroxyl radicals on the finite-rate chemical kinetics of premixed hydrogen-air mixtures undergoing isobaric autoignition and combustion. The free radicals were considered to be initially present in hydrogen-air mixtures at equivalence ratios of 0.2, 0.6, 1.0, and 1.2. Initial mixture temperatures were 1100 K, 1200 K, and 1500 K, and pressures were 0.5, 1.0, 2.0, and 4.0 atm. Of the radicals investigated, atomic oxygen was found to be the most effective for reducing induction time, defined as the time to 5 percent of the total combustion temperature rise. The reaction time, the time between 5 percent and 95 percent of the temperature rise, is not decreased by the presence of free radicals in the initial hydrogen-air mixture. Fuel additives which yield free radicals might be used to effect a compact supersonic combustor design for efficient operation in an otherwise reaction-limited combustion regime.
Minimising hydrogen sulphide generation during steam assisted production of heavy oil

PubMed Central

Montgomery, Wren; Sephton, Mark A.; Watson, Jonathan S.; Zeng, Huang; Rees, Andrew C.

2015-01-01

The majority of global petroleum is in the form of highly viscous heavy oil. Traditionally heavy oil in sands at shallow depths is accessed by large scale mining activities. Recently steam has been used to allow heavy oil extraction with greatly reduced surface disturbance. However, in situ thermal recovery processes can generate hydrogen sulphide, high levels of which are toxic to humans and corrosive to equipment. Avoiding hydrogen sulphide production is the best possible mitigation strategy. Here we use laboratory aquathermolysis to reproduce conditions that may be experienced during thermal extraction. The results indicate that hydrogen sulphide generation occurs within a specific temperature and pressure window and corresponds to chemical and physical changes in the oil. Asphaltenes are identified as the major source of sulphur. Our findings reveal that for high sulphur heavy oils, the generation of hydrogen sulphide during steam assisted thermal recovery is minimal if temperature and pressure are maintained within specific criteria. This strict pressure and temperature dependence of hydrogen sulphide release can allow access to the world's most voluminous oil deposits without generating excessive amounts of this unwanted gas product. PMID:25670085
Minimising hydrogen sulphide generation during steam assisted production of heavy oil

NASA Astrophysics Data System (ADS)

Montgomery, Wren; Sephton, Mark A.; Watson, Jonathan S.; Zeng, Huang; Rees, Andrew C.

2015-02-01

The majority of global petroleum is in the form of highly viscous heavy oil. Traditionally heavy oil in sands at shallow depths is accessed by large scale mining activities. Recently steam has been used to allow heavy oil extraction with greatly reduced surface disturbance. However, in situ thermal recovery processes can generate hydrogen sulphide, high levels of which are toxic to humans and corrosive to equipment. Avoiding hydrogen sulphide production is the best possible mitigation strategy. Here we use laboratory aquathermolysis to reproduce conditions that may be experienced during thermal extraction. The results indicate that hydrogen sulphide generation occurs within a specific temperature and pressure window and corresponds to chemical and physical changes in the oil. Asphaltenes are identified as the major source of sulphur. Our findings reveal that for high sulphur heavy oils, the generation of hydrogen sulphide during steam assisted thermal recovery is minimal if temperature and pressure are maintained within specific criteria. This strict pressure and temperature dependence of hydrogen sulphide release can allow access to the world's most voluminous oil deposits without generating excessive amounts of this unwanted gas product.
Minimising hydrogen sulphide generation during steam assisted production of heavy oil.

PubMed

Montgomery, Wren; Sephton, Mark A; Watson, Jonathan S; Zeng, Huang; Rees, Andrew C

2015-02-11

The majority of global petroleum is in the form of highly viscous heavy oil. Traditionally heavy oil in sands at shallow depths is accessed by large scale mining activities. Recently steam has been used to allow heavy oil extraction with greatly reduced surface disturbance. However, in situ thermal recovery processes can generate hydrogen sulphide, high levels of which are toxic to humans and corrosive to equipment. Avoiding hydrogen sulphide production is the best possible mitigation strategy. Here we use laboratory aquathermolysis to reproduce conditions that may be experienced during thermal extraction. The results indicate that hydrogen sulphide generation occurs within a specific temperature and pressure window and corresponds to chemical and physical changes in the oil. Asphaltenes are identified as the major source of sulphur. Our findings reveal that for high sulphur heavy oils, the generation of hydrogen sulphide during steam assisted thermal recovery is minimal if temperature and pressure are maintained within specific criteria. This strict pressure and temperature dependence of hydrogen sulphide release can allow access to the world's most voluminous oil deposits without generating excessive amounts of this unwanted gas product.
Selection And Evaluation Of An Alloy For Nozzle Application

NASA Technical Reports Server (NTRS)

Pandey, A. B.; Shah, S.; Shadoan, M.; Lyles, Garry (Technical Monitor)

2003-01-01

The present work includes results on material characterization conducted under COBRA Hydrogen Cooled Nozzle Program and was funded by NASA MSFC. The nozzle requires a material that has high strength at ambient and high (up to l200 F) temperatures in air and hydrogen. Presently, a precipitation hardened steel; A-286 is used in nozzles for Space Shuttle Engines. The A-286 alloy has limited hydrogen compatibility and weldability. The present work focused on selection and characterization of JBK-75 alloy that has significantly higher capability in hydrogen and weldability in addition to other attributes. The alloy was evaluated at different temperatures and environments. Tungsten Inert Gas (TIG) and Electron Beam welding techniques were used to evaluate the weldability of material. Brazing was also conducted on the alloy and evaluated. The characterization of base JBK-75 alloy, welded and brazed alloy included tensile properties, low cycle fatigue and crack growth resistance at different temperatures in air and hydrogen environments. The results indicated that JBK-75 has excellent tensile and fatigue properties in air and hydrogen. The welded and brazed alloy also showed very good properties.
Methods and systems for the production of hydrogen

DOEpatents

Oh, Chang H [Idaho Falls, ID; Kim, Eung S [Ammon, ID; Sherman, Steven R [Augusta, GA

2012-03-13

Methods and systems are disclosed for the production of hydrogen and the use of high-temperature heat sources in energy conversion. In one embodiment, a primary loop may include a nuclear reactor utilizing a molten salt or helium as a coolant. The nuclear reactor may provide heat energy to a power generation loop for production of electrical energy. For example, a supercritical carbon dioxide fluid may be heated by the nuclear reactor via the molten salt and then expanded in a turbine to drive a generator. An intermediate heat exchange loop may also be thermally coupled with the primary loop and provide heat energy to one or more hydrogen production facilities. A portion of the hydrogen produced by the hydrogen production facility may be diverted to a combustor to elevate the temperature of water being split into hydrogen and oxygen by the hydrogen production facility.
Hydrogen Annealing Of Single-Crystal Superalloys

NASA Technical Reports Server (NTRS)

Smialek, James L.; Schaeffer, John C.; Murphy, Wendy

1995-01-01

Annealing at temperature equal to or greater than 2,200 degrees F in atmosphere of hydrogen found to increase ability of single-crystal superalloys to resist oxidation when subsequently exposed to oxidizing atmospheres at temperatures almost as high. Supperalloys in question are principal constituents of hot-stage airfoils (blades) in aircraft and ground-based turbine engines; also used in other high-temperature applications like chemical-processing plants, coal-gasification plants, petrochemical refineries, and boilers. Hydrogen anneal provides resistance to oxidation without decreasing fatigue strength and without need for coating or reactive sulfur-gettering constituents. In comparison with coating, hydrogen annealing costs less. Benefits extend to stainless steels, nickel/chromium, and nickel-base alloys, subject to same scale-adhesion and oxidation-resistance considerations, except that scale is chromia instead of alumina.
High-pressure modulation of the structure of the bacterial photochemical reaction center at physiological and cryogenic temperatures

NASA Astrophysics Data System (ADS)

Timpmann, Kõu; Kangur, Liina; Lõhmus, Ants; Freiberg, Arvi

2017-07-01

The optical absorption and fluorescence response to external high pressure of the reaction center membrane chromoprotein complex from the wild-type non-sulfur photosynthetic bacterium Rhodobacter sphaeroides was investigated using the native pigment cofactors as local molecular probes of the reaction center structure at physiological (ambient) and cryogenic (79 K) temperatures. In detergent-purified complexes at ambient temperature, abrupt blue shift and accompanied broadening of the special pair band was observed at about 265 MPa. These reversible in pressure features were assigned to a pressure-induced rupture of a lone hydrogen bond that binds the photo-chemically active L-branch primary electron donor bacteriochlorophyll cofactor to the surrounding protein scaffold. In native membrane-protected complexes the hydrogen bond rupture appeared significantly restricted and occurred close to about 500 MPa. The free energy change associated with the rupture of the special pair hydrogen bond in isolate complexes was estimated to be equal to about 12 kJ mol-1. In frozen samples at cryogenic temperatures the hydrogen bond remained apparently intact up to the maximum utilized pressure of 600 MPa. In this case, however, heterogeneous spectral response of the cofactors from the L-and M-branches was observed due to anisotropic build-up of the protein structure. While in solid phase, the special pair fluorescence as a function of pressure exactly followed the respective absorption spectrum at a constant Stokes shift, at ambient temperature, the two paths began to deviate strongly from one other at the hydrogen bond rupture pressure. This effect was tentatively interpreted by different emission properties of hydrogen-bound and hydrogen-unbound special pair exciton states.
Mechanisms Underpinning Degradation of Protective Oxides and Thermal Barrier Coatings in High Hydrogen Content (HHC) - Fueled Turbines

DOE Office of Scientific and Technical Information (OSTI.GOV)

Mumm, Daniel

2013-08-31

The overarching goal of this research program has been to evaluate the potential impacts of coal-derived syngas and high-hydrogen content fuels on the degradation of turbine hot-section components through attack of protective oxides and thermal barrier coatings. The primary focus of this research program has been to explore mechanisms underpinning the observed degradation processes, and connections to the combustion environments and characteristic non-combustible constituents. Based on the mechanistic understanding of how these emerging fuel streams affect materials degradation, the ultimate goal of the program is to advance the goals of the Advanced Turbine Program by developing materials design protocols leadingmore » to turbine hot-section components with improved resistance to service lifetime degradation under advanced fuels exposures. This research program has been focused on studying how: (1) differing combustion environments – relative to traditional natural gas fired systems – affect both the growth rate of thermally grown oxide (TGO) layers and the stability of these oxides and of protective thermal barrier coatings (TBCs); and (2) how low levels of fuel impurities and characteristic non-combustibles interact with surface oxides, for instance through the development of molten deposits that lead to hot corrosion of protective TBC coatings. The overall program has been comprised of six inter-related themes, each comprising a research thrust over the program period, including: (i) evaluating the role of syngas and high hydrogen content (HHC) combustion environments in modifying component surface temperatures, heat transfer to the TBC coatings, and thermal gradients within these coatings; (ii) understanding the instability of TBC coatings in the syngas and high hydrogen environment with regards to decomposition, phase changes and sintering; (iii) characterizing ash deposition, molten phase development and infiltration, and associated corrosive/thermo-chemical attack mechanisms; (iv) developing a mechanics-based analysis of the driving forces for crack growth and delamination, based on molten phase infiltration, misfit upon cooling, and loss of compliance; (v) understanding changes in TGO growth mechanisms associated with these emerging combustion product streams; and (vi) identifying degradation resistant alternative materials (including new compositions or bi-layer concepts) for use in mitigating the observed degradation modes. To address the materials stability concerns, this program integrated research thrusts aimed at: (1) Conducting tests in simulated syngas and HHC environments to evaluate materials evolution and degradation mechanisms; assessing thermally grown oxide development unique to HHC environmental exposures; carrying out high-resolution imaging and microanalysis to elucidate the evolution of surface deposits (molten phase formation and infiltration); exploring thermo-chemical instabilities; assessing thermo-mechanical drivers and thermal gradient effects on degradation; and quantitatively measuring stress evolution due to enhanced sintering and thermo-chemical instabilities induced in the coating. (2) Executing experiments to study the melting and infiltration of simulated ash deposits, and identifying reaction products and evolving phases associated with molten phase corrosion mechanisms; utilizing thermal spray techniques to fabricate test coupons with controlled microstructures to study mechanisms of instability and degradation; facilitating thermal gradient testing; and developing new materials systems for laboratory testing; (3) Correlating information on the resulting combustion environments to properly assess materials exposure conditions and guide the development of lab-scale simulations of material exposures; specification of representative syngas and high-hydrogen fuels with realistic levels of impurities and contaminants, to explore differences in heat transfer, surface degradation, and deposit formation; and facilitating combustion rig testing of materials test coupons.« less
A statistical mechanical theory for a two-dimensional model of water

PubMed Central

Urbic, Tomaz; Dill, Ken A.

2010-01-01

We develop a statistical mechanical model for the thermal and volumetric properties of waterlike fluids. Each water molecule is a two-dimensional disk with three hydrogen-bonding arms. Each water interacts with neighboring waters through a van der Waals interaction and an orientation-dependent hydrogen-bonding interaction. This model, which is largely analytical, is a variant of the Truskett and Dill (TD) treatment of the “Mercedes-Benz” (MB) model. The present model gives better predictions than TD for hydrogen-bond populations in liquid water by distinguishing strong cooperative hydrogen bonds from weaker ones. We explore properties versus temperature T and pressure p. We find that the volumetric and thermal properties follow the same trends with T as real water and are in good general agreement with Monte Carlo simulations of MB water, including the density anomaly, the minimum in the isothermal compressibility, and the decreased number of hydrogen bonds for increasing temperature. The model reproduces that pressure squeezes out water’s heat capacity and leads to a negative thermal expansion coefficient at low temperatures. In terms of water structuring, the variance in hydrogen-bonding angles increases with both T and p, while the variance in water density increases with T but decreases with p. Hydrogen bonding is an energy storage mechanism that leads to water’s large heat capacity (for its size) and to the fragility in its cagelike structures, which are easily melted by temperature and pressure to a more van der Waals-like liquid state. PMID:20550408

A statistical mechanical theory for a two-dimensional model of water

NASA Astrophysics Data System (ADS)

Urbic, Tomaz; Dill, Ken A.

2010-06-01

We develop a statistical mechanical model for the thermal and volumetric properties of waterlike fluids. Each water molecule is a two-dimensional disk with three hydrogen-bonding arms. Each water interacts with neighboring waters through a van der Waals interaction and an orientation-dependent hydrogen-bonding interaction. This model, which is largely analytical, is a variant of the Truskett and Dill (TD) treatment of the "Mercedes-Benz" (MB) model. The present model gives better predictions than TD for hydrogen-bond populations in liquid water by distinguishing strong cooperative hydrogen bonds from weaker ones. We explore properties versus temperature T and pressure p. We find that the volumetric and thermal properties follow the same trends with T as real water and are in good general agreement with Monte Carlo simulations of MB water, including the density anomaly, the minimum in the isothermal compressibility, and the decreased number of hydrogen bonds for increasing temperature. The model reproduces that pressure squeezes out water's heat capacity and leads to a negative thermal expansion coefficient at low temperatures. In terms of water structuring, the variance in hydrogen-bonding angles increases with both T and p, while the variance in water density increases with T but decreases with p. Hydrogen bonding is an energy storage mechanism that leads to water's large heat capacity (for its size) and to the fragility in its cagelike structures, which are easily melted by temperature and pressure to a more van der Waals-like liquid state.
A statistical mechanical theory for a two-dimensional model of water.

PubMed

Urbic, Tomaz; Dill, Ken A

2010-06-14

We develop a statistical mechanical model for the thermal and volumetric properties of waterlike fluids. Each water molecule is a two-dimensional disk with three hydrogen-bonding arms. Each water interacts with neighboring waters through a van der Waals interaction and an orientation-dependent hydrogen-bonding interaction. This model, which is largely analytical, is a variant of the Truskett and Dill (TD) treatment of the "Mercedes-Benz" (MB) model. The present model gives better predictions than TD for hydrogen-bond populations in liquid water by distinguishing strong cooperative hydrogen bonds from weaker ones. We explore properties versus temperature T and pressure p. We find that the volumetric and thermal properties follow the same trends with T as real water and are in good general agreement with Monte Carlo simulations of MB water, including the density anomaly, the minimum in the isothermal compressibility, and the decreased number of hydrogen bonds for increasing temperature. The model reproduces that pressure squeezes out water's heat capacity and leads to a negative thermal expansion coefficient at low temperatures. In terms of water structuring, the variance in hydrogen-bonding angles increases with both T and p, while the variance in water density increases with T but decreases with p. Hydrogen bonding is an energy storage mechanism that leads to water's large heat capacity (for its size) and to the fragility in its cagelike structures, which are easily melted by temperature and pressure to a more van der Waals-like liquid state.
Low-temperature hydrogen production from water and methanol using Pt/α-MoC catalysts

NASA Astrophysics Data System (ADS)

Lin, Lili; Zhou, Wu; Gao, Rui; Yao, Siyu; Zhang, Xiao; Xu, Wenqian; Zheng, Shijian; Jiang, Zheng; Yu, Qiaolin; Li, Yong-Wang; Shi, Chuan; Wen, Xiao-Dong; Ma, Ding

2017-03-01

Polymer electrolyte membrane fuel cells (PEMFCs) running on hydrogen are attractive alternative power supplies for a range of applications, with in situ release of the required hydrogen from a stable liquid offering one way of ensuring its safe storage and transportation before use. The use of methanol is particularly interesting in this regard, because it is inexpensive and can reform itself with water to release hydrogen with a high gravimetric density of 18.8 per cent by weight. But traditional reforming of methanol steam operates at relatively high temperatures (200-350 degrees Celsius), so the focus for vehicle and portable PEMFC applications has been on aqueous-phase reforming of methanol (APRM). This method requires less energy, and the simpler and more compact device design allows direct integration into PEMFC stacks. There remains, however, the need for an efficient APRM catalyst. Here we report that platinum (Pt) atomically dispersed on α-molybdenum carbide (α-MoC) enables low-temperature (150-190 degrees Celsius), base-free hydrogen production through APRM, with an average turnover frequency reaching 18,046 moles of hydrogen per mole of platinum per hour. We attribute this exceptional hydrogen production—which far exceeds that of previously reported low-temperature APRM catalysts—to the outstanding ability of α-MoC to induce water dissociation, and to the fact that platinum and α-MoC act in synergy to activate methanol and then to reform it.
Low-temperature hydrogen production from water and methanol using Pt/α-MoC catalysts.

PubMed

Lin, Lili; Zhou, Wu; Gao, Rui; Yao, Siyu; Zhang, Xiao; Xu, Wenqian; Zheng, Shijian; Jiang, Zheng; Yu, Qiaolin; Li, Yong-Wang; Shi, Chuan; Wen, Xiao-Dong; Ma, Ding

2017-04-06

Polymer electrolyte membrane fuel cells (PEMFCs) running on hydrogen are attractive alternative power supplies for a range of applications, with in situ release of the required hydrogen from a stable liquid offering one way of ensuring its safe storage and transportation before use. The use of methanol is particularly interesting in this regard, because it is inexpensive and can reform itself with water to release hydrogen with a high gravimetric density of 18.8 per cent by weight. But traditional reforming of methanol steam operates at relatively high temperatures (200-350 degrees Celsius), so the focus for vehicle and portable PEMFC applications has been on aqueous-phase reforming of methanol (APRM). This method requires less energy, and the simpler and more compact device design allows direct integration into PEMFC stacks. There remains, however, the need for an efficient APRM catalyst. Here we report that platinum (Pt) atomically dispersed on α-molybdenum carbide (α-MoC) enables low-temperature (150-190 degrees Celsius), base-free hydrogen production through APRM, with an average turnover frequency reaching 18,046 moles of hydrogen per mole of platinum per hour. We attribute this exceptional hydrogen production-which far exceeds that of previously reported low-temperature APRM catalysts-to the outstanding ability of α-MoC to induce water dissociation, and to the fact that platinum and α-MoC act in synergy to activate methanol and then to reform it.
Liquid Fuel Production from Biomass via High Temperature Steam Electrolysis

DOE Office of Scientific and Technical Information (OSTI.GOV)

Grant L. Hawkes; Michael G. McKellar

2009-11-01

A process model of syngas production using high temperature electrolysis and biomass gasification is presented. Process heat from the biomass gasifier is used to heat steam for the hydrogen production via the high temperature steam electrolysis process. Hydrogen from electrolysis allows a high utilization of the biomass carbon for syngas production. Oxygen produced form the electrolysis process is used to control the oxidation rate in the oxygen-fed biomass gasifier. Based on the gasifier temperature, 94% to 95% of the carbon in the biomass becomes carbon monoxide in the syngas (carbon monoxide and hydrogen). Assuming the thermal efficiency of the powermore » cycle for electricity generation is 50%, (as expected from GEN IV nuclear reactors), the syngas production efficiency ranges from 70% to 73% as the gasifier temperature decreases from 1900 K to 1500 K. Parametric studies of system pressure, biomass moisture content and low temperature alkaline electrolysis are also presented.« less
Method of treating intermetallic alloy hydrogenation/oxidation catalysts for improved impurity poisoning resistance, regeneration and increased activity

DOEpatents

Wright, R.B.

1992-01-14

Alternate, successive high temperature oxidation and reduction treatments, in either order, of intermetallic alloy hydrogenation and intermetallic alloy oxidation catalysts unexpectedly improves the impurity poisoning resistance, regeneration capacity and/or activity of the catalysts. The particular alloy, and the final high temperature treatment given alloy (oxidation or reduction) will be chosen to correspond to the function of the catalyst (oxidation or hydrogenation). 23 figs.
Magnesium Nanoparticles for Hydrogen Storage: Structure, Kinetics and Thermodynamics

NASA Astrophysics Data System (ADS)

Pasquini, L.; Brighi, M.; Montone, A.; Vittori Antisari, M.; Dam, B.; Palmisano, V.; Bonetti, E.

2012-08-01

Magnesium nanoparticles coated by a native oxide shell and decorated by palladium clusters were synthesized by the inert gas condensation technique. The kinetics and thermodynamics of hydrogen sorption were investigated by Sieverts measurements at high temperature and by optical hydrogenography close to ambient temperature. The structure and morphology of the nanoparticles were studied by electron microscopy and X-ray diffraction both in the as-prepared state and after hydrogen sorption cycles.
Diffusive Gas Loss from Silica Glass Ampoules at Elevated Temperatures

NASA Technical Reports Server (NTRS)

Palosz, W.

1998-01-01

Changes in the pressure of hydrogen, helium and neon due to diffusion through the wall of silica crystal growth ampoules at elevated temperatures were determined experimentally. We show that, while both He- and Ne-losses closely follow conventional model of diffusive gas permeation through the wall, hydrogen losses, in particular at low fill pressures, can be much larger. This is interpreted in terms of the high solubility of hydrogen in silica glasses.
Influence of gaseous hydrogen on the mechanical properties of incoloy 903. [gas-metal interactions/iron alloys

NASA Technical Reports Server (NTRS)

1975-01-01

Solid specimens of the alloy Inconel 903 (iron based alloy) were exposed to four gaseous environments and high temperatures. Air, pure helium, pure hydrogen, and hydrogen and water vapor combined were the gaseous environments employed, and the temperature was 1400 F. Various mechanical property tests (low cycle fatigue, creep-rupture, tensile properties) were performed on the alloy. Results indicate that the hydrogen and water vapor environment cause a sharp reduction in the mechanical properties of the alloy. Photographs of the test equipment used and the microstructure of the tested alloy are included.
Methods of using ionic liquids having a fluoride anion as solvents

DOEpatents

Pagoria, Philip [Livermore, CA; Maiti, Amitesh [San Ramon, CA; Gash, Alexander [Brentwood, CA; Han, Thomas Yong [Pleasanton, CA; Orme, Christine [Oakland, CA; Fried, Laurence [Livermore, CA

2011-12-06

A method in one embodiment includes contacting a strongly hydrogen bonded organic material with an ionic liquid having a fluoride anion for solubilizing the strongly hydrogen bonded organic material; and maintaining the ionic liquid at a temperature of about 90.degree. C. or less during the contacting. A method in another embodiment includes contacting a strongly hydrogen bonded organic material with an ionic liquid having an acetate or formate anion for solubilizing the strongly hydrogen bonded organic material; and maintaining the ionic liquid at a temperature of less than about 90.degree. C. during the contacting.
Method for preparing hydride configurations and reactive metal surfaces

DOEpatents

Silver, Gary L.

1988-08-16

A method for preparing highly hydrogen-reactive surfaces on metals which normally require substantial heating, high pressures, or an extended induction period, which involves pretreatment of said surfaces with either a non-oxidizing acid or hydrogen gas to form a hydrogen-bearing coating on said surfaces, and subsequently heating said coated metal in the absence of moisture and oxygen for a period sufficient to decompose said coating and cooling said metal to room temperature. Surfaces so treated will react almost instantaneously with hydrogen gas at room temperature and low pressure. The method is particularly applicable to uranium, thorium, and lanthanide metals.
Mechanical properties of several nickel alloys in hydrogen at elevated temperatures

NASA Technical Reports Server (NTRS)

Warren, J. R.; Harris, J. A., Jr.; Vanwanderham, M. C.

1977-01-01

Tests were performed to determine low cycle fatigue and crack growth rate properties of one iron-base and two forms of one cast nickel-base alloy. The alloys were tested in various forms and/or heat-treat conditions that are proposed for use in a high-pressure hydrogen or a hydrogen-water vapor environment. Some general conclusions can be made comparing the results of tests in a hydrogen environment with those in a hydrogen-water vapor environment. The hydrogen-water vapor environment caused a 50 percent average reduction in fatigue life, indicating extreme degradation when compared with tests conducted in air, for Incoloy 903 at 1033 K (1400 F). Crack growth rates increased significantly for all materials with increasing test temperature. A very significant increase (three orders of magnitude) in crack growth rate occurred for Incoloy 903 tested in the hydrogen-water vapor environment when compared with testing done in hydrogen along at 922 K (1200 F).
Rhodium dihydride (RhH2) with high volumetric hydrogen density

PubMed Central

Li, Bing; Ding, Yang; Kim, Duck Young; Ahuja, Rajeev; Zou, Guangtian; Mao, Ho-Kwang

2011-01-01

Materials with very high hydrogen density have attracted considerable interest due to a range of motivations, including the search for chemically precompressed metallic hydrogen and hydrogen storage applications. Using high-pressure synchrotron X-ray diffraction technique and theoretical calculations, we have discovered a new rhodium dihydride (RhH2) with high volumetric hydrogen density (163.7 g/L). Compressing rhodium in fluid hydrogen at ambient temperature, the fcc rhodium metal absorbs hydrogen and expands unit-cell volume by two discrete steps to form NaCl-typed fcc rhodium monohydride at 4 GPa and fluorite-typed fcc RhH2 at 8 GPa. RhH2 is the first dihydride discovered in the platinum group metals under high pressure. Our low-temperature experiments show that RhH2 is recoverable after releasing pressure cryogenically to 1 bar and is capable of retaining hydrogen up to 150 K for minutes and 77 K for an indefinite length of time. PMID:22039219
Process for recovering evolved hydrogen enriched with at least one heavy hydrogen isotope

DOEpatents

Tanaka, John; Reilly, Jr., James J.

1978-01-01

This invention relates to a separation means and method for enriching a hydrogen atmosphere with at least one heavy hydrogen isotope by using a solid titaniun alloy hydride. To this end, the titanium alloy hydride containing at least one metal selected from the group consisting of vanadium, chromium, manganese, molybdenum, iron, cobalt and nickel is contacted with a circulating gaseous flow of hydrogen containing at least one heavy hydrogen isotope at a temperature in the range of -20.degree. to +40.degree. C and at a pressure above the dissociation pressure of the hydrided alloy selectively to concentrate at least one of the isotopes of hydrogen in the hydrided metal alloy. The contacting is continued until equilibrium is reached, and then the gaseous flow is isolated while the temperature and pressure of the enriched hydride remain undisturbed selectively to isolate the hydride. Thereafter, the enriched hydrogen is selectively recovered in accordance with the separation factor (S.F.) of the alloy hydride employed.
Tailoring Thermodynamics and Kinetics for Hydrogen Storage in Complex Hydrides towards Applications.

PubMed

Liu, Yongfeng; Yang, Yaxiong; Gao, Mingxia; Pan, Hongge

2016-02-01

Solid-state hydrogen storage using various materials is expected to provide the ultimate solution for safe and efficient on-board storage. Complex hydrides have attracted increasing attention over the past two decades due to their high gravimetric and volumetric hydrogen densities. In this account, we review studies from our lab on tailoring the thermodynamics and kinetics for hydrogen storage in complex hydrides, including metal alanates, borohydrides and amides. By changing the material composition and structure, developing feasible preparation methods, doping high-performance catalysts, optimizing multifunctional additives, creating nanostructures and understanding the interaction mechanisms with hydrogen, the operating temperatures for hydrogen storage in metal amides, alanates and borohydrides are remarkably reduced. This temperature reduction is associated with enhanced reaction kinetics and improved reversibility. The examples discussed in this review are expected to provide new inspiration for the development of complex hydrides with high hydrogen capacity and appropriate thermodynamics and kinetics for hydrogen storage. © 2015 The Chemical Society of Japan & Wiley-VCH Verlag GmbH & Co. KGaA, Weinheim.
Surface compositional variations of Mo-47Re alloy as a function of temperature

NASA Technical Reports Server (NTRS)

Hoekje, S. J.; Outlaw, R. A.; Sankaran, S. N.

1993-01-01

Molybdenum-rhenium alloys are candidate materials for the National Aero-Space Plane (NASP) as well as for other applications in generic hypersonics. These materials are expected to be subjected to high-temperature (above 1200 C) casual hydrogen (below 50 torr), which could potentially degrade the material strength. Since the uptake of hydrogen may be controlled by the contaminant surface barriers, a study of Mo-47Re was conducted to examine the variations in surface composition as a function of temperature from 25 C to 1000 C. Pure molybdenum and rhenium were also examined and the results compared with those for the alloy. The analytical techniques employed were Auger electron spectroscopy, electron energy loss spectroscopy, ion scattering spectroscopy, and x ray photoelectron spectroscopy. The native surface was rich in metallic oxides that disappeared at elevated temperatures. As the temperature increased, the carbon and oxygen disappeared by 800 C and the surface was subsequently populated by the segregation of silicon, presumably from the grain boundaries. The alloy readily chemisorbed oxygen, which disappeared with heating. The disappearance temperature progressively increased for successive dosings. When the alloy was exposed to 800 torr of hydrogen at 900 C for 1 hour, no hydrogen interaction was observed.
Chemical structural analysis of diamondlike carbon films: II. Raman analysis

NASA Astrophysics Data System (ADS)

Takabayashi, Susumu; Ješko, Radek; Shinohara, Masanori; Hayashi, Hiroyuki; Sugimoto, Rintaro; Ogawa, Shuichi; Takakuwa, Yuji

2018-02-01

The chemical structure of diamondlike carbon (DLC) films, synthesized by photoemission-assisted glow discharge, has been analyzed by Raman spectroscopy. Raman analysis in conjunction with the sp2 cluster model clarified the film structure. The sp2 clusters in DLC films synthesized at low temperature preferred various aliphatic structures. Sufficient argon-ion assist allowed for formation of less strained DLC films containing large amounts of hydrogen. As the synthesis temperature was increased, thermal desorption of hydrogen left carbon dangling bonds with active unpaired electrons in the films, and the reactions that followed created strained films containing aromatic sp2 clusters. In parallel, the desorption of methane molecules from the growing surface by chemisorption of hydrogen radicals prevented the action of argon ions, promoting internal strain of the films. However, in synthesis at very high temperature, where sp2 clusters are sufficiently dominant, the strain was dissolved gradually. In contrast, the DLC films synthesized at low temperature were more stable than other films synthesized at the same temperature because of stable hydrogen-carbon bonds in the films.
Hydrogen loading system development and evaluation of tritiated substrates to optimize performance in tritium based betavoltaics

NASA Astrophysics Data System (ADS)

Adams, Thomas E.

State-of-the-art hydrogen loading system onto thin metallic films based on differential pressure in calibrated chambers has been developed for conditions pressures and temperatures up to 69 bar and 500°C, respectively. Experiments on hydrogen loading on to palladium films of thickness 50 and 250 nm were conducted at pressure ranging from 0.2 bar to 10 bar at temperature 310°C. For first time film hydrogen loading was carried out at 1 bar and at room temperature which temperature. Beta flux exiting surface of metal tritide films has been modeled with MC-SET (Monte Carlo Simulation of Electron Trajectories in solids). Surface beta flux simulations have been improved to account for density changes from tritium loading and decay. Simulation results indicate a 300 nm slab of MgT2 has a surface flux three times higher than in ScT2, and six times higher than in TiT2. Commercial betavoltaic cells were tested at different temperature environment for their evaluation and characterization.
Temperature Stratification in a Cryogenic Fuel Tank

NASA Technical Reports Server (NTRS)

Daigle, Matthew John; Smelyanskiy, Vadim; Boschee, Jacob; Foygel, Michael Gregory

2013-01-01

A reduced dynamical model describing temperature stratification effects driven by natural convection in a liquid hydrogen cryogenic fuel tank has been developed. It accounts for cryogenic propellant loading, storage, and unloading in the conditions of normal, increased, and micro- gravity. The model involves multiple horizontal control volumes in both liquid and ullage spaces. Temperature and velocity boundary layers at the tank walls are taken into account by using correlation relations. Heat exchange involving the tank wall is considered by means of the lumped-parameter method. By employing basic conservation laws, the model takes into consideration the major multi-phase mass and energy exchange processes involved, such as condensation-evaporation of the hydrogen, as well as flows of hydrogen liquid and vapor in the presence of pressurizing helium gas. The model involves a liquid hydrogen feed line and a tank ullage vent valve for pressure control. The temperature stratification effects are investigated, including in the presence of vent valve oscillations. A simulation of temperature stratification effects in a generic cryogenic tank has been implemented in Matlab and results are presented for various tank conditions.
Microstructural studies of hydrogen damage in metastable stainless steels. Ph.D. Thesis

DOE Office of Scientific and Technical Information (OSTI.GOV)

Chen, S.

1994-12-31

The primary objective of this dissertation is to determine the role of microstructure in hydrogen-induced damage in austenitic stainless steels. Specific attention was focused on the interactions between hydrogen and the austenitic grain, twin boundaries and the matrix, and the associated phase transformations. An experimental program of research was conducted to determine the phase transformation and cracking path in hydrogen charged stainless steels. Normal-purity AISI 304 (Fe18CrYNi) and high-purity 305 (Fe18Cr12Ni) solution-annealet stainless steels were examined. The steels were cathodically charged with hydrogen at 1, 10 and 100 mA/sq cm at room temperature for 5 min. to 32 hours, inmore » an 1N H2SO4 solution with 0.25 g/l of NaAsO2 added as a hydrogen recombination poison. Resultant changes in microstructure and hydrogen damage due to charging and subsequent room temperature aging were studied by x-ray diffraction, optical microscope (in the Nomarski mode), scanning electron microscopy (SEM) and transmission electron microscopy (TEM). A new phase in 305 stainless steel was observed, and was identified as an epsilon(*) (hcp) hydride due to hydrogen charging. Two new phases in 304 stainless steel were found as gamma(*) (fcc) and epsilon(*) hydrides from hydrogen charging. The hydride formation mechanisms during charging were: (1) gamma yields gamma(*) hydride and (2) gamma yields epsilon yields epsilon(*) hydride. These hydrides are unstable and decomposed during room temperature aging in air. The decomposition mechanisms were: (1) epsilon(*) hydride (hcp) yields expanded epsilon (hcp) phase yields a (bcc) phase; (2) gamma(*) hydride yields gamma phase. The grain and twin boundary cracks were the results of charging and identified as the preferred cracking sites. Transgranular crack initiation and growth accompanied the decomposition of hydrides and were controlled by hydrogen outgassing during room temperature aging.« less

Hydrogen mobility in the lightest reversible metal hydride, LiBeH 3

DOE PAGES

Mamontov, Eugene; Kolesnikov, Alexander I.; Sampath, Sujatha; ...

2017-11-24

Lithium-beryllium metal hydrides, which are structurally related to their parent compound, BeH 2, offer the highest hydrogen storage capacity by weight among the metal hydrides (15.93 wt. % of hydrogen for LiBeH 3). Challenging synthesis protocols have precluded conclusive determination of their crystallographic structure to date, but here we analyze directly the hydrogen hopping mechanisms in BeH 2 and LiBeH 3 using quasielastic neutron scattering, which is especially sensitive to single-particle dynamics of hydrogen. We find that, unlike its parent compound BeH 2, lithium-beryllium hydride LiBeH 3 exhibits a sharp increase in hydrogen mobility above 265 K, so dramatic thatmore » it can be viewed as melting of hydrogen sublattice. We perform comparative analysis of hydrogen jump mechanisms observed in BeH 2 and LiBeH 3 over a broad temperature range. As microscopic diffusivity of hydrogen is directly related to its macroscopic kinetics, a transition in LiBeH 3 so close to ambient temperature may offer a straightforward and effective mechanism to influence hydrogen uptake and release in this very lightweight hydrogen storage compound.« less
Hydrogen mobility in the lightest reversible metal hydride, LiBeH 3

DOE Office of Scientific and Technical Information (OSTI.GOV)

Mamontov, Eugene; Kolesnikov, Alexander I.; Sampath, Sujatha

Lithium-beryllium metal hydrides, which are structurally related to their parent compound, BeH 2, offer the highest hydrogen storage capacity by weight among the metal hydrides (15.93 wt. % of hydrogen for LiBeH 3). Challenging synthesis protocols have precluded conclusive determination of their crystallographic structure to date, but here we analyze directly the hydrogen hopping mechanisms in BeH 2 and LiBeH 3 using quasielastic neutron scattering, which is especially sensitive to single-particle dynamics of hydrogen. We find that, unlike its parent compound BeH 2, lithium-beryllium hydride LiBeH 3 exhibits a sharp increase in hydrogen mobility above 265 K, so dramatic thatmore » it can be viewed as melting of hydrogen sublattice. We perform comparative analysis of hydrogen jump mechanisms observed in BeH 2 and LiBeH 3 over a broad temperature range. As microscopic diffusivity of hydrogen is directly related to its macroscopic kinetics, a transition in LiBeH 3 so close to ambient temperature may offer a straightforward and effective mechanism to influence hydrogen uptake and release in this very lightweight hydrogen storage compound.« less
Cryogenic temperature effects on sting-balance deflections in the National Transonic Facility

NASA Technical Reports Server (NTRS)

Popernack, Thomas G., Jr.; Adcock, Jerry B.

1990-01-01

An investigation was conducted at the National Transonic Facility (NTF) to document the change in sting-balance deflections from ambient to cryogenic temperatures. Space limitations in some NTF models do not allow the use of on-board angle of attack instrumentation. In order to obtain angle of attack data, pre-determined sting-balance bending data must be combined with arc sector angle measurements. Presently, obtaining pretest sting-balance data requires several cryogenic cycles and cold loadings over a period of several days. A method of reducing the calibration time required is to obtain only ambient temperature sting-balance bending data and correct for changes in material properties at cryogenic temperatures. To validate this method, two typical NTF sting-balance combinations were tested. The test results show excellent agreement with the predicted values and the repeatability of the data was 0.01 degree.
Kinetics and the mass transfer mechanism of hydrogen sulfide removal by biochar derived from rice hull.

PubMed

Shang, Guofeng; Liu, Liang; Chen, Ping; Shen, Guoqing; Li, Qiwu

2016-05-01

The biochar derived from rice hull was evaluated for its abilities to remove hydrogen sulfide (H2S) from gas phase. The surface area and pH of the biochar were compared. The biochar derived from rice hull was evaluated for its abilities to remove hydrogen sulfide (H2S) from gas phase. The surface area and pH of the biochar were compared. The different pyrolysis temperature has great influence on the adsorption of H2S. At the different pyrolysis temperature, the H2S removal efficiency of rice hull-derived biochar was different. The adsorption capacities of biochar were 2.09 mg·g(-1), 2.65 mg·g(-1), 16.30 mg·g(-1), 20.80 mg·g(-1), and 382.70 mg·g(-1), which their pyrolysis temperatures were 100 °C, 200 °C, 300 °C, 400 °C and 500 °C respectively. Based on the Yoon-Nelson model, it analyzed the mass transfer mechanism of hydrogen sulfide adsorption by biochar. The paper focuses on the biochar derived from rice hull-removed hydrogen sulfide (H2S) from gas phase. The surface area and pH of the biochar were compared. The different pyrolysis temperatures have great influence on the adsorption of H2S. At the different pyrolysis temperatures, the H2S removal efficiency of rice hull-derived biohar was different. The adsorption capacities of biochar were 2.09, 2.65, 16.30, 20.80, and 382.70 mg·g(-1), and their pyrolysis temperatures were 100, 200, 300, 400, and 500 °C, respectively. Based on the Yoon-Nelson model, the mass transfer mechanism of hydrogen sulfide adsorption by biochar was analyzed.
Magnetic behavior of R2Fe14B hydrides (R = Gd, Tb, Dy, Ho and Er)

NASA Astrophysics Data System (ADS)

Zhang, L. Y.; Pourarian, F.; Wallace, W. E.

1988-01-01

R 2Fe 14B systems, with R = Gd, Tb, By, HoandEr were hydrogenated to the composition R 2Fe 14BH x where x ranges from 3.7 to 5.4. The pressure-composition isotherms (PCIs) of the hydrides showed only a solid solution behavior. No plateau pressure region was observed between room temperature and 300° C and at pressures down to 10 -2 atm. The absorbed hydrogen leads to an increase of 2.6 to 3.4% in unit cell volume, without a change in crystal structure. Magnetic characteristics of the present compounds were investigated over the temperature range 4.2 to 1100 K and at applied field up to 20 kOe. Saturation magnetization, Ms, and magnetic ordering temperature, Tc, were enhanced upon hydrogenation. Tc, is found to be dependent on the hydriding composition. Hydrogen induces a spin-reorientation effect (SR) in Gd- and Dy-containing compounds, while it has a marked influence in raising the spin-reorientation temperature, TSR, in the Er 2Fe 14B compound. The hydride involving Tb appears to remain uniaxial to the lowest temperature studied. In all cases the anisotropy fields, HA/' were significally reduced by hydrogen absorption. These varied magnetic behaviors can be ascribed to the effects: (1) variations in the interatomic distances, (2) strengthening the 3d-3d and weakening the 4f-3d exchange interactions and (3) the interstitial site occupations of hydrogen in the lattice. The spin-reorientation phenomena observed for Gd 2Fe 14BH x suggest that there is competition among the 6 Fe sublattices in regard to the sign and temperature coefficient of anisotropy.
Alterations in brain temperatures as a possible cause of migraine headache.

PubMed

Horváth, Csilla

2014-05-01

Migraine is a debilitating disease with a recurring generally unilateral headache and concomitant symptoms of nausea, vomiting and photo- and/or phonophobia that affects some 11-18% of the population. Most of the mechanisms previously put forward to explain the attacks have been questioned or give an explanation only some of the symptoms. Moreover, the best drugs for treatment are still the 20-year-old triptans, which have serious limitations as regards both efficacy and tolerability. As the dura and some cranial vessels are the only intracranial structures capable of pain sensations, a vascular theory of migraine emerged, but has been debated. Recent theories identified the hyperexcitability of structures involved in pain transmission, such as the trigeminal system or the cortex, or an abnormal modulatory function of the brainstem. However, there is ongoing scientific debate concerning these theories, neither of which is fully capable of explaining the occurrence of a migraine attack. The present article puts forward a hypothesis of the possibility of abnormal temperature regulation in certain regions or the overall brain in migraineurs, the attack being a defense mechanism to prevent neuronal damage. Few examinations have been made of temperature regulation in the human brain. It lacks the carotid rete, a vascular heat exchanger that serves in many animals to provide constant brain temperature. The human brain contains a high density of neurons with a considerable energy demand that is converted to heat. The human brain has a higher temperature than other parts of the body and needs continuous cooling. Recent studies revealed unexpectedly great variations in temperature of various structures of the brain and considerable changes in response to functional activation. There is various evidence in support of the hypothesis that accumulated heat in some structure or the overall brain may be behind the symptoms observed, such as a platelet abnormality, a decreased serotonin content, and dural "inflammation" including vasodilation and brainstem activation. The hypothesis postulates that a migraine attack serves to restore the brain temperature. Abnormally low temperatures in the brain can also result in headache. Surprisingly, no systematic examination of brain temperature changes in migraineurs has been published. Certain case reports support the present hypothesis. Various noninvasive technologies (e.g. MR) capable of monitoring brain temperature are available. If a systematic examination of local brain temperature revealed abnormalities in structures presumed to be involved in migraine, that would increase our understanding of the disease and trigger the development of improved treatment. Copyright © 2014 Elsevier Ltd. All rights reserved.
Role of Hydrogen Bonding on Nonlinear Mechano-Optical Behavior of L-Phenylalanine-based Poly(ester urea)s.

NASA Astrophysics Data System (ADS)

Chen, Keke; Yu, Jiayi; Guzman, Gustavo; Es-Haghi, S. Shams; Becker, Matthew L.; Cakmak, Miko

The uniaxial mechano-optical behavior of a series of amorphous L-phenylalanine-based poly(ester urea) (PEU) films was studied in the rubbery state using a custom real-time measurement system. When the materials were subjected to deformation at temperatures near the glass transition temperature (Tg) , the photoelastic behavior was manifested by a small increase in birefringence with a significant increase in true stress. At temperatures above Tg, PEUs with a shorter diol chain length exhibited a liquid-liquid (Tll) transition at about 1.06 Tg (K), above which the material transforms from a heterogeneous ``liquid of fixed-structure'' to a ``true liquid'' state. The initial photoelastic behavior disappears with increasing temperature, as the initial slope of the stress optical curves becomes temperature independent. Fourier transform infrared spectra of PEUs revealed that the average strength of hydrogen bonding diminishes with increasing temperature. For PEUs with the longest diol chain length, the area associated with N-H stretching region exhibits a linear temperature dependence. The presence of hydrogen bonding enhances the ``stiff'' segmental correlations between adjacent chains in the PEU structure. As a result, the photoelastic constant decreases with increasing hydrogen bonding strength. This work was supported by the Ohio Department of Development's Innovation Platform Program and The National Science Foundation.
On the temperature dependence of H-U{sub iso} in the riding hydrogen model

DOE Office of Scientific and Technical Information (OSTI.GOV)

Lübben, Jens; Volkmann, Christian; Grabowsky, Simon

The temperature dependence of hydrogen U{sub iso} and parent U{sub eq} in the riding hydrogen model is investigated by neutron diffraction, aspherical-atom refinements and QM/MM and MO/MO cluster calculations. Fixed values of 1.2 or 1.5 appear to be underestimated, especially at temperatures below 100 K. The temperature dependence of H-U{sub iso} in N-acetyl-l-4-hydroxyproline monohydrate is investigated. Imposing a constant temperature-independent multiplier of 1.2 or 1.5 for the riding hydrogen model is found to be inaccurate, and severely underestimates H-U{sub iso} below 100 K. Neutron diffraction data at temperatures of 9, 150, 200 and 250 K provide benchmark results for thismore » study. X-ray diffraction data to high resolution, collected at temperatures of 9, 30, 50, 75, 100, 150, 200 and 250 K (synchrotron and home source), reproduce neutron results only when evaluated by aspherical-atom refinement models, since these take into account bonding and lone-pair electron density; both invariom and Hirshfeld-atom refinement models enable a more precise determination of the magnitude of H-atom displacements than independent-atom model refinements. Experimental efforts are complemented by computing displacement parameters following the TLS+ONIOM approach. A satisfactory agreement between all approaches is found.« less
Composition for use in high-temperature hydrogen-fluorine environments and method for making the composition

DOEpatents

Kovach, L.; Holcombe, C.E.

1980-08-22

The present invention relates to a composition particularly suitable for use as structural components subject to high-temperature environments containing gaseous hydrogen and fluorine. The composition of the present invention consists essentially of lanthanum hexaboride-molybdenum diboride with dispersed silicon. The composition is formed by hot pressing a powder mixture of lanthanum hexaboride as the major constituent and molybdenum disilicide. This composition exhibits substantial resistance to thermal shock and corrosion in environments containing hydrogen and fluorine gases at material surface temperatures up to about 1850/sup 0/K. Upon exposure of the hot-pressed composition to high-temperature environments containing fluorine gases, a highly protective layer of lanthanum trifluoride containing dispersed molybdenum is formed on exposed surfaces of the composition.
Composition for use in high-temperature hydrogen-fluorine environments and method for making the composition

DOEpatents

Kovach, Louis; Holcombe, Cressie E.

1982-01-01

The present invention relates to a composition particularly suitable for as structural components subject to high-temperature environments containing gaseous hydrogen and fluorine. The composition of the present invention consists essentially of lanthanum hexaboride-molybdenum diboride with dispersed silicon. The composition is formed by hot pressing a powder mixture of lanthanum hexaboride as the major constituent and molybdenum disilicide. This composition exhibits substantial resistance to thermal shock and corrosion in environments containing hydrogen and fluorine gases at material surface temperatures up to about 1850.degree. K. Upon exposure of the hot-pressed composition to high-temperature environments containing fluorine gases, a highly protective layer of lanthanum trifluoride containing dispersed molybdenum is formed on exposed surfaces of the composition.
Radiation-induced segregation at grain boundaries in AL-6XN stainless steels irradiated by hydrogen ions

NASA Astrophysics Data System (ADS)

Long, Yunxiang; Zheng, Zhongcheng; Guo, Liping; Zhang, Weiping; Shen, Zhenyu; Tang, Rui

2018-04-01

The effect of high concentration of hydrogen on the segregation of radiation-induced segregation (RIS) in AL-6XN stainless steels has been investigated by transmission electron microscopy (TEM) with energy-dispersive X-ray spectroscopy. Specimens were irradiated with 100 keV H2+ ions from 1 dpa to 5 dpa at 380 °C to investigated the dose dependence of grain boundary RIS. A specimen was irradiated to 5 dpa at 290 °C to study the effect of irradiation temperature. The trends of Cr depletion and Ni enrichment with irradiation dose is similar to that of other austenitic steels reported in the literatures, but the higher concentration of hydrogen made the RIS profile wider. An abnormal phenomenon that the degree of RIS increased with decreasing irradiation temperature was found, indicating that with the retention of hydrogen in the steels, temperature dependence of RIS is dominated by the quantity of retained hydrogen, rather than by thermal segregation processes.
High-Temperature Proton-Conducting Ceramics Developed

NASA Technical Reports Server (NTRS)

Sayir, Ali; Dynys, Frederick W.; Berger, M. H.

2005-01-01

High-temperature protonic conductors (HTPC) are needed for hydrogen separation, hydrogen sensors, fuel cells, and hydrogen production from fossil fuels. The HTPC materials for hydrogen separation at high temperatures are foreseen to be metal oxides with the perovskite structure A(sup 2+)B(sup 4+)C(sup 2-, sub 3) and with the trivalent cation (M(sup 3+)) substitution at the B(sup 4+)-site to introduce oxygen vacancies. The high affinity for hydrogen ions (H(sup +)) is advantageous for protonic transport, but it increases the reactivity toward water (H2O) and carbon dioxide (CO2), which can lead to premature membrane failure. In addition, there are considerable technological challenges related to the processing of HTPC materials. The high melting point and multi-cation chemistry of HTPC materials creates difficulties in in achieving high-density, single-phase membranes by solid-state sintering. The presence of secondary phases and grain-boundary interfaces are detrimental to the protonic conduction and environmental stability of polycrystalline HTPC materials.
Acceptorless dehydrogenation of small molecules through cooperative base metal catalysis

PubMed Central

West, Julian G.; Huang, David; Sorensen, Erik J.

2015-01-01

The dehydrogenation of unactivated alkanes is an important transformation both in industrial and biological systems. Recent efforts towards this reaction have revolved around high temperature, organometallic C–H activation by noble metal catalysts that produce alkenes and hydrogen gas as the sole products. Conversely, natural desaturase systems proceed through stepwise hydrogen atom transfer at physiological temperature; however, these transformations require a terminal oxidant. Here we show combining tetra-n-butylammonium decatungstate (TBADT) and cobaloxime pyridine chloride (COPC) can catalytically dehydrogenate unactivated alkanes and alcohols under near-UV irradiation at room temperature with hydrogen as the sole by-product. This noble metal-free process follows a nature-inspired pathway of high- and low-energy hydrogen atom abstractions. The hydrogen evolution ability of cobaloximes is leveraged to render the system catalytic, with cooperative turnover numbers up to 48 and yields up to 83%. Our results demonstrate how cooperative base metal catalysis can achieve transformations previously restricted to precious metal catalysts. PMID:26656087
Cyclic Oxidation and Hot Corrosion of NiCrY-Coated Disk Superalloys

NASA Technical Reports Server (NTRS)

Gabb, Timothy P.; Miller, Robert A.; Sudbrack, Chantal K.; Draper, Susan L.; Nesbitt, James A.; Rogers, Richard B.; Telesman, Ignacy; Ngo, Vanda; Healy, Jonathan

2016-01-01

Powder metallurgy disk superalloys have been designed for higher engine operating temperatures through improvement of their strength and creep resistance. Yet, increasing disk application temperatures to 704 degrees Centigrade and higher could enhance oxidation and activate hot corrosion in harmful environments. Protective coatings could be necessary to mitigate such attack. Cylindrical coated specimens of disk superalloys LSHR and ME3 were subjected to thermal cycling to produce cyclic oxidation in air at a maximum temperature of 760 degrees Centigrade. The effects of substrate roughness and coating thickness on coating integrity after cyclic oxidation were considered. Selected coated samples that had cyclic oxidation were then subjected to accelerated hot corrosion tests. This cyclic oxidation did not impair the coating's resistance to subsequent hot corrosion pitting attack.
High-power CW laser using hydrogen-fluorine reaction

NASA Technical Reports Server (NTRS)

Moynihan, P. I.

1975-01-01

Continuous-wave laser has been proposed based on reaction of hydrogen and fluorine. Hydrogen is produced by dissociation of hydrazine, which can be stored as liquid in light containers at room temperature.
Low temperature, low pressure hydrogen gettering

DOEpatents

Anderson, D. Richard; Courtney, Robert L.; Harrah, Larry A.

1976-06-15

The invention relates to the gettering of hydrogen and its isotopes, the gettering materials being painted or coated onto, or otherwise disposed in an area or volume from which hydrogen is to be removed.
Predictions of glass transition temperature for hydrogen bonding biomaterials.

PubMed

van der Sman, R G M

2013-12-19

We show that the glass transition of a multitude of mixtures containing hydrogen bonding materials correlates strongly with the effective number of hydroxyl groups per molecule, which are available for intermolecular hydrogen bonding. This correlation is in compliance with the topological constraint theory, wherein the intermolecular hydrogen bonds constrain the mobility of the hydrogen bonded network. The finding that the glass transition relates to hydrogen bonding rather than free volume agrees with our recent finding that there is little difference in free volume among carbohydrates and polysaccharides. For binary and ternary mixtures of sugars, polyols, or biopolymers with water, our correlation states that the glass transition temperature is linear with the inverse of the number of effective hydroxyl groups per molecule. Only for dry biopolymer/sugar or sugar/polyol mixtures do we find deviations due to nonideal mixing, imposed by microheterogeneity.
Large enhancement of X-ray excited luminescence in Ga-doped ZnO nanorod arrays by hydrogen annealing

NASA Astrophysics Data System (ADS)

Li, Qianli; Liu, Xiaoliln; Gu, Mu; Li, Fengrui; Zhang, Juannan; Wu, Qiang; Huang, Shiming; Liu, Si

2018-03-01

Highly c-axis oriented and densely packed ZnO:Ga nanorod arrays were fabricated on ZnO-seeded substrates by hydrothermal method, and the effect of hydrogen annealing on their morphology, structure and luminescence properties was investigated in detail. Under ultraviolet or X-ray excitation, an intense ultraviolet luminescence appeared in the hydrogen-annealed samples owing to the formation of a shallow hydrogen donor state, which can sharply activate the reconbination radiation. The luminescence intensity increased with the annealing temperature, and then decreased at a higher temperature due to the dissociation of the hydrogen ion. The optimum concentration and time of hydrogen annealing were acquired simultaneously. It is expected that the ZnO:Ga nanorod array is a promising candidate for application in ultrafast and high-spatial-resolution X-ray imaging detector.
Optimization Study of Hydrogen Gas Adsorption on Zig-zag Single-walled Carbon Nanotubes: The Artificial Neural Network Analysis

NASA Astrophysics Data System (ADS)

Nasruddin; Lestari, M.; Supriyadi; Sholahudin

2018-03-01

The use of hydrogen gas in fuel cell technology has a huge opportunity to be applied in upcoming vehicle technology. One of the most important problems in fuel cell technology is the hydrogen storage. The adsorption of hydrogen in carbon-based materials attracts a lot of attention because of its reliability. This study investigated the adsorption of hydrogen gas in Single-walled Carbon Nano Tubes (SWCNT) with chilarity of (0, 12), (0, 15), and (0, 18) to find the optimum chilarity. Artificial Neural Networks (ANN) can be used to predict the hydrogen storage capacity at different pressure and temperature conditions appropriately, using simulated series of data. The Artificial Neural Network is modeled as a predictor of the hydrogen adsorption capacity which provides solutions to some deficiencies in molecular dynamics (MD) simulations. In a previous study, ANN configurations have been developed for 77k, 233k, and 298k temperatures in hydrogen gas storage. To prepare this prediction, ANN is modeled to find out the configurations that exist in the set of training and validation of specified data selection, the distance between data, and the number of neurons that produce the smallest error. This configuration is needed to make an accurate artificial neural network. The configuration of neural network was then applied to this research. The neural network analysis results show that the best configuration of artificial neural network in hydrogen storage is at 233K temperature i.e. on SWCNT with chilarity of (0.12).
On-Board Hydrogen Gas Production System For Stirling Engines

DOEpatents

Johansson, Lennart N.

2004-06-29

A hydrogen production system for use in connection with Stirling engines. The production system generates hydrogen working gas and periodically supplies it to the Stirling engine as its working fluid in instances where loss of such working fluid occurs through usage through operation of the associated Stirling engine. The hydrogen gas may be generated by various techniques including electrolysis and stored by various means including the use of a metal hydride absorbing material. By controlling the temperature of the absorbing material, the stored hydrogen gas may be provided to the Stirling engine as needed. A hydrogen production system for use in connection with Stirling engines. The production system generates hydrogen working gas and periodically supplies it to the Stirling engine as its working fluid in instances where loss of such working fluid occurs through usage through operation of the associated Stirling engine. The hydrogen gas may be generated by various techniques including electrolysis and stored by various means including the use of a metal hydride absorbing material. By controlling the temperature of the absorbing material, the stored hydrogen gas may be provided to the Stirling engine as needed.

Effects of discharge chamber length on the negative ion generation in volume-produced negative hydrogen ion source

DOE Office of Scientific and Technical Information (OSTI.GOV)

Chung, Kyoung-Jae; Jung, Bong-Ki; An, YoungHwa

2014-02-15

In a volume-produced negative hydrogen ion source, control of electron temperature is essential due to its close correlation with the generation of highly vibrationally excited hydrogen molecules in the heating region as well as the generation of negative hydrogen ions by dissociative attachment in the extraction region. In this study, geometric effects of the cylindrical discharge chamber on negative ion generation via electron temperature changes are investigated in two discharge chambers with different lengths of 7.5 cm and 11 cm. Measurements with a radio-frequency-compensated Langmuir probe show that the electron temperature in the heating region is significantly increased by reducingmore » the length of the discharge chamber due to the reduced effective plasma size. A particle balance model which is modified to consider the effects of discharge chamber configuration on the plasma parameters explains the variation of the electron temperature with the chamber geometry and gas pressure quite well. Accordingly, H{sup −} ion density measurement with laser photo-detachment in the short chamber shows a few times increase compared to the longer one at the same heating power depending on gas pressure. However, the increase drops significantly as operating gas pressure decreases, indicating increased electron temperatures in the extraction region degrade dissociative attachment significantly especially in the low pressure regime. It is concluded that the increase of electron temperature by adjusting the discharge chamber geometry is efficient to increase H{sup −} ion production as long as low electron temperatures are maintained in the extraction region in volume-produced negative hydrogen ion sources.« less
Hydrogen maser oscillation at 10 K

NASA Technical Reports Server (NTRS)

Crampton, S. B.; Jones, K. M.; Souza, S. P.

1984-01-01

A low temperature atomic hydrogen maser was developed using frozen atomic neon as the storage surface. The maser has been operated in the pulsed mode at temperatures from 6 K to 11 K and as a self-excited oscillator from 9 K to 10.5 K.
Hemicellulose conversion by anaerobic digestion

DOE Office of Scientific and Technical Information (OSTI.GOV)

Ghosh, S.; Henry, M.P.; Christopher, R.W.

1982-01-01

The digestibility of an aquatic biomass (water hyacinth), a land-based biomass (Coastal Bermuda grass), and a biomass-waste blend (a mixture of hyacinth, grass, MSW, and sludge) under various digestion conditions was studied. Anaerobic digestion of hemicellulose consists of the steps of enzymatic hydrolysis of hemicellulose to glucans, mannans, galactans, xylans, and arabans, and then to simple hexose and pentose sugars; production of C/sub 2/ and higher fatty acids from the simple sugars; conversion of higher fatty acids to acetate; and finally, production of methane and CO/sub 2/ from acetate, and CO/sub 2/ and hydrogen. The conversion of hemicellulose was highermore » under mesophilic conditions than those of cellulose or protein for all biomass test feeds, probably because the hemicellulose structure was more vulnerable to enzymatic attack than that of the lignocellulosic component. Cellulose conversion efficiencies at the mesophilic and thermophilic temperatures were about the same. However, hemicellulose was converted at a much lower efficiency than cellulose during thermophilic digestion - a situation that was the reverse of that observed at the mesophilic temperature. Cellulose was utilized in preference to hemicellulose during mesophilic digestion of nitrogen-supplemented Bermuda grass. It was speculated that Bermuda grass cellulose was converted at a higher efficiency than hemicellulose in the presence of external nitrogen because the metabolism of the breakdown product (glucose) of cellulose requires the least investment of enzymes and energy.« less
Enzyme dynamics and hydrogen tunnelling in a thermophilic alcohol dehydrogenase

NASA Astrophysics Data System (ADS)

Kohen, Amnon; Cannio, Raffaele; Bartolucci, Simonetta; Klinman, Judith P.; Klinman, Judith P.

1999-06-01

Biological catalysts (enzymes) speed up reactions by many orders of magnitude using fundamental physical processes to increase chemical reactivity. Hydrogen tunnelling has increasingly been found to contribute to enzyme reactions at room temperature. Tunnelling is the phenomenon by which a particle transfers through a reaction barrier as a result of its wave-like property. In reactions involving small molecules, the relative importance of tunnelling increases as the temperature is reduced. We have now investigated whether hydrogen tunnelling occurs at elevated temperatures in a biological system that functions physiologically under such conditions. Using a thermophilic alcohol dehydrogenase (ADH), we find that hydrogen tunnelling makes a significant contribution at 65°C this is analogous to previous findings with mesophilic ADH at 25°C ( ref. 5). Contrary to predictions for tunnelling through a rigid barrier, the tunnelling with the thermophilic ADH decreases at and below room temperature. These findings provide experimental evidence for a role of thermally excited enzyme fluctuations in modulating enzyme-catalysed bond cleavage.
Hydrogen desorption from hydrogen fluoride and remote hydrogen plasma cleaned silicon carbide (0001) surfaces

DOE Office of Scientific and Technical Information (OSTI.GOV)

King, Sean W., E-mail: sean.king@intel.com; Tanaka, Satoru; Davis, Robert F.

2015-09-15

Due to the extreme chemical inertness of silicon carbide (SiC), in-situ thermal desorption is commonly utilized as a means to remove surface contamination prior to initiating critical semiconductor processing steps such as epitaxy, gate dielectric formation, and contact metallization. In-situ thermal desorption and silicon sublimation has also recently become a popular method for epitaxial growth of mono and few layer graphene. Accordingly, numerous thermal desorption experiments of various processed silicon carbide surfaces have been performed, but have ignored the presence of hydrogen, which is ubiquitous throughout semiconductor processing. In this regard, the authors have performed a combined temperature programmed desorptionmore » (TPD) and x-ray photoelectron spectroscopy (XPS) investigation of the desorption of molecular hydrogen (H{sub 2}) and various other oxygen, carbon, and fluorine related species from ex-situ aqueous hydrogen fluoride (HF) and in-situ remote hydrogen plasma cleaned 6H-SiC (0001) surfaces. Using XPS, the authors observed that temperatures on the order of 700–1000 °C are needed to fully desorb C-H, C-O and Si-O species from these surfaces. However, using TPD, the authors observed H{sub 2} desorption at both lower temperatures (200–550 °C) as well as higher temperatures (>700 °C). The low temperature H{sub 2} desorption was deconvoluted into multiple desorption states that, based on similarities to H{sub 2} desorption from Si (111), were attributed to silicon mono, di, and trihydride surface species as well as hydrogen trapped by subsurface defects, steps, or dopants. The higher temperature H{sub 2} desorption was similarly attributed to H{sub 2} evolved from surface O-H groups at ∼750 °C as well as the liberation of H{sub 2} during Si-O desorption at temperatures >800 °C. These results indicate that while ex-situ aqueous HF processed 6H-SiC (0001) surfaces annealed at <700 °C remain terminated by some surface C–O and Si–O bonding, they may still exhibit significant chemical reactivity due to the creation of surface dangling bonds resulting from H{sub 2} desorption from previously undetected silicon hydride and surface hydroxide species.« less
The influence of weather on migraine – are migraine attacks predictable?

PubMed Central

Hoffmann, Jan; Schirra, Tonio; Lo, Hendra; Neeb, Lars; Reuter, Uwe; Martus, Peter

2015-01-01

Objective The study aimed at elucidating a potential correlation between specific meteorological variables and the prevalence and intensity of migraine attacks as well as exploring a potential individual predictability of a migraine attack based on meteorological variables and their changes. Methods Attack prevalence and intensity of 100 migraineurs were correlated with atmospheric pressure, relative air humidity, and ambient temperature in 4-h intervals over 12 consecutive months. For each correlation, meteorological parameters at the time of the migraine attack as well as their variation within the preceding 24 h were analyzed. For migraineurs showing a positive correlation, logistic regression analysis was used to assess the predictability of a migraine attack based on meteorological information. Results In a subgroup of migraineurs, a significant weather sensitivity could be observed. In contrast, pooled analysis of all patients did not reveal a significant association. An individual prediction of a migraine attack based on meteorological data was not possible, mainly as a result of the small prevalence of attacks. Interpretation The results suggest that only a subgroup of migraineurs is sensitive to specific weather conditions. Our findings may provide an explanation as to why previous studies, which commonly rely on a pooled analysis, show inconclusive results. The lack of individual attack predictability indicates that the use of preventive measures based on meteorological conditions is not feasible. PMID:25642431
Natural diatomite modified as novel hydrogen storage material

NASA Astrophysics Data System (ADS)

Jin, Jiao; Zheng, Chenghui; Yang, Huaming

2014-03-01

Natural diatomite, subjected to different modifications, is investigated for hydrogen adsorption capacities at room temperature. An effective metal-modified strategy is developed to disperse platinum (Pt) and palladium (Pd) nanoparticles on the surface of diatomite. Hydrogen adsorption capacity of pristine diatomite (diatomite) is 0.463 wt.% at 2.63 MPa and 298 K, among the highest of the known sorbents, while that of acid-thermally activated diatomite (A-diatomite) could reach up to 0.833 wt.% due to the appropriate pore properties by activation. By incorporation with a small amount of Pt and Pd ( 0.5 wt.%), hydrogen adsorption capacities are enhanced to 0.696 wt.% and 0.980 wt.%, respectively, indicating that activated diatomite shows interesting application in the field of hydrogen storage at room temperature.
Isothermal Decomposition of Hydrogen Peroxide Dihydrate

NASA Technical Reports Server (NTRS)

Loeffler, M. J.; Baragiola, R. A.

2011-01-01

We present a new method of growing pure solid hydrogen peroxide in an ultra high vacuum environment and apply it to determine thermal stability of the dihydrate compound that forms when water and hydrogen peroxide are mixed at low temperatures. Using infrared spectroscopy and thermogravimetric analysis, we quantified the isothermal decomposition of the metastable dihydrate at 151.6 K. This decomposition occurs by fractional distillation through the preferential sublimation of water, which leads to the formation of pure hydrogen peroxide. The results imply that in an astronomical environment where condensed mixtures of H2O2 and H2O are shielded from radiolytic decomposition and warmed to temperatures where sublimation is significant, highly concentrated or even pure hydrogen peroxide may form.
Temperature Dependence in the Terahertz Spectrum of Nicotinamide: Anharmonicity and Hydrogen-Bonded Network.

PubMed

Takahashi, Masae; Okamura, Nubuyuki; Fan, Xinyi; Shirakawa, Hitoshi; Minamide, Hiroaki

2017-04-06

We have investigated the terahertz-spectral property of nicotinamide focusing on the temperature dependence in the range of 14-300 K. We observed that almost all peaks in the terahertz spectrum of the nicotinamide crystal showed a remarkable shift with temperature, whereas the lowest-frequency peak at 34.8 cm -1 showed a negligible shift with temperature. By analyzing the terahertz spectrum with the dispersion-corrected density functional theory calculations, we found that the difference in the temperature dependence of the peak shift is well understood in terms of the presence/absence of stretching vibration of the intermolecular hydrogen bond in the mode and the change of cell parameters. The anharmonicity in the dissociation potential energy of very weak intermolecular hydrogen bonding causes the remarkable peak shift with temperature in the terahertz spectrum of nicotinamide. This finding suggests that the assignment and identification of peaks in the terahertz spectrum are systematically enabled by temperature-dependent measurements.
Pest Oxidation Regime in the Hi-Nicalon(Trademark)/BN/SiC Composite

NASA Technical Reports Server (NTRS)

Ogbuji, Linus U. J. T.

1998-01-01

SiC-SiC composites are prone to pest degradation at intermediate temperatures where the formation of a protective scale of silica by direct oxidation of SiC is too slow to offer effective protection from attack by ambient gases. The attack results in the removal of the BN interphase and its replacement by a borosilicate liquid (which dissolves and weakens the fiber) and finally by SiO2, (which embrittles the composite by bonding fiber to fiber or to matrix). This paper reports a study aimed at mapping out the temperature range of such pest degradation and the severity of its effect.
Modeling low-temperature serpentinization reactions to estimate molecular hydrogen production with implications for potential microbial life on Saturn's moon Enceladus.

NASA Astrophysics Data System (ADS)

Zwicker, Jennifer; Smrzka, Daniel; Taubner, Ruth-Sophie; Bach, Wolfgang; Rittmann, Simon; Schleper, Christa; Peckmann, Jörn

2017-04-01

Serpentinization of ultramafic rocks attracts much interest in research on the origin of life on Earth and the search for life on extraterrestrial bodies including icy moons like Enceladus. Serpentinization on Earth occurs in peridotite-hosted systems at slow-spreading mid-ocean ridges, and produces large amounts of molecular hydrogen and methane. These reduced compounds can be utilized by diverse chemosynthetic microbial consortia as a metabolic energy source. Although many hydrothermal vents emit hot and acidic fluids today, it is more likely that life originated in the Archean at sites producing much cooler and more alkaline fluids that allowed for the synthesis and stability of essential organic molecules necessary for life. Therefore, a detailed understanding of water-rock interaction processes during low-temperature serpentinization is of crucial importance in assessing the life-sustaining potential of these environments. In the course of serpentinization, the metasomatic hydration of olivine and pyroxene produces various minerals including serpentine minerals, magnetite, brucite, and carbonates. Hydrogen production only occurs if ferrous iron within iron-bearing minerals is oxidized and incorporated as ferric iron into magnetite. The PHREEQC code was used to model the pH- and temperature-dependent dissolution of olivine and pyroxene to form serpentine, magnetite and hydrogen under pressure and temperature conditions that may exist on Saturn's icy moon Enceladus. Various model setups at 25 and 50°C were run to assess the influence of environmental parameters on hydrogen production. The results reveal that hydrogen production rates depend on the composition of the initial mineral assemblage and temperature. The current assumption is that there is a gaseous phase between Enceladus' ice sheet and subsurface ocean. To test various scenarios, model runs were conducted with and without the presence of a gas phase. The model results show that hydrogen production is further dependent on carbon dioxide partial pressure within the gas phase. Moreover, no other gases apart from hydrogen, such as methane, were produced in any of the model runs. The combined results offer a constraint on hydrogen production over time, and may aid habitability assessments of extraterrestrial bodies where serpentinization could occur.
Hydrogen permeation behavior through F82H at high temperature

DOE Office of Scientific and Technical Information (OSTI.GOV)

Matsuda, S.; Katayama, K.; Shimozori, M.

2015-03-15

F82H is a primary candidate of structural material and coolant pipe material in a blanket of a fusion reactor. Understanding tritium permeation behavior through F82H is important. In a normal operation of a fusion reactor, the temperature of F82H will be controlled below 550 C. degrees because it is considered that F82H can be used up to 30,000 hours at 550 C. degrees. However, it is necessary to assume the situation where F82H is heated over 550 C. degrees in a severe accident. In this study, hydrogen permeation behavior through F82H was investigated in the temperature range from 500 tomore » 800 C. degrees. In some cases, water vapor was added in a sample gas to investigate an effect of water vapor on hydrogen permeation. The permeability of hydrogen in the temperature range from 500 to 700 C. degrees agreed well with the permeability reported by E. Serra et al. The degradation of the permeability by water vapor was not observed. After the hydrogen permeation reached in a steady state at 700 C. degrees, the F82H sample was heated to 800 C. degrees. The permeability of hydrogen through F82H sample which was once heated up to 800 C. degrees was lower than that of the original one. (authors)« less
Magnetic behavior of R 2Co 14B hydrides (R = La, Pr, Sm, Gd, Tb and Y)

NASA Astrophysics Data System (ADS)

Zhang, L. Y.; Pourarian, F.; Wallace, W. E.

1988-08-01

The structure and magnetic properties of R 2Co 14B sysstems(R = La, Pr, Nd, Sm, Gd, Tb and Y) and their hydrides were studied by means of bulk magnetometry. All R 2Co 14B hydrides presently studied occur in the tetragonal Nd 2Fe 14B-type crystal structure. The composition-temperature isotherms measured fro selected Gd- and Nd- containing systems exhibit some indication of a platuau pressure at higher hydrogen concentrations. Hydrogenation expands the unit volume, Vc, by 1.5 to 3.0%, depending on the nature of R and the content of hydrogen. It was found that introduction of hydrogen into the lattice decreases Ms of the Co sublittice. This is attributed to the effect of electron charge transfer from Hto Co-3d sublittice. Hydrogennation significantly decreases the anistropy fields, HA, and the spin-reorientation transition temperatur, TSR, for Prand Tb-based intermetallics. The results indicates that the hydrogen makes the compounds magnetically softer, which is attributed to the influence of hydrogen on both the 3d and R sublittices. Two types of spin-reorientation transition for the Nd 2Co 14B system were observed. Hydrogenaration reduces both the low transition temperature, TSR 1, and the high transition temperature, TSR 2, which is explained using the Boltich-Wallace mechanism.
The problems of using a high-temperature sodium coolant in nuclear power plants for the production of hydrogen and other innovative applications

NASA Astrophysics Data System (ADS)

Sorokin, A. P.; Alexeev, V. V.; Kuzina, Ju. A.; Konovalov, M. A.

2017-11-01

The intensity of the hydrogen sources arriving from the third contour of installation in second in comparison with the hydrogen sources on NPP BN-600 increases by two - three order at using of high-temperature nuclear power plants with the sodium coolant (HT-NPP) for drawing of hydrogen and other innovative applications (gasification and a liquefaction of coal, profound oil refining, transformation of biomass to liquid fuel, in the chemical industry, metallurgy, the food-processing industry etc.). For these conditions basic new technological solutions are offered. The main condition of their implementation is raise of hydrogen concentration in the sodium coolant on two - three order in comparison with the modern NPP, in a combination to hydrogen removal from sodium and its pumping out through membranes from vanadium or niobium. The researches with use diffusive model have shown possibility to expel a casium inflow in sodium through a leakproof shell of fuel rods if vary such parameters as a material of fuel rods shell, its thickness and maintenance time at design of fuel rods for high-temperature NPP. However maintenance of high-temperature NPP in the presence of casium in sodium is inevitable at loss of leakproof of a fuel rods shell. In these conditions for minimisation of casium diffusion in structural materials it is necessary to provide deep clearing of sodium from cesium.
Methanol-Water Aqueous-Phase Reforming with the Assistance of Dehydrogenases at Near-Room Temperature.

PubMed

Shen, Yangbin; Zhan, Yulu; Li, Shuping; Ning, Fandi; Du, Ying; Huang, Yunjie; He, Ting; Zhou, Xiaochun

2018-03-09

As an excellent hydrogen-storage medium, methanol has many advantages, such as high hydrogen content (12.6 wt %), low cost, and availability from biomass or photocatalysis. However, conventional methanol-water reforming usually proceeds at high temperatures. In this research, we successfully designed a new effective strategy to generate hydrogen from methanol at near-room temperature. The strategy involved two main processes: CH 3 OH→HCOOH→H 2 and NADH→HCOOH→H 2 . The first process (CH 3 OH→HCOOH→H 2 ) was performed by an alcohol dehydrogenase (ADH), an aldehyde dehydrogenase (ALDH), and an Ir catalyst. The second procedure (NADH→HCOOH→H 2 ) was performed by formate dehydrogenase (FDH) and the Ir catalyst. The Ir catalyst used was a previously reported polymer complex catalyst [Cp*IrCl 2 (ppy); Cp*=pentamethylcyclopentadienyl, ppy=polypyrrole] with high catalytic activity for the decomposition of formic acid at room temperature and is compatible with enzymes, coenzymes, and poisoning chemicals. Our results revealed that the optimum hydrogen generation rate could reach up to 17.8 μmol h -1 g cat -1 under weak basic conditions at 30 °C. This will have high impact on hydrogen storage, production, and applications and should also provide new inspiration for hydrogen generation from methanol. © 2018 Wiley-VCH Verlag GmbH & Co. KGaA, Weinheim.
Modeling of hydrogen effect on the superelastic behavior of Ni-Ti shape memory alloy wires

NASA Astrophysics Data System (ADS)

Lachiguer, Amani; Bouby, Céline; Gamaoun, Fehmi; Bouraoui, Tarak; Ben Zineb, Tarak

2016-11-01

Superelastic NiTi wires are widely used in orthodontic treatments, but sometimes fracture can be observed after few months of use in buccal cavity and attributed to the degradation of NiTi mechanical properties due to hydrogen absorption. In this paper, a modeling approach is proposed in order to describe the effect of hydrogen diffusion on the transformation properties of NiTi SMAs. In order to experimentally predict such effects, cathodic hydrogen charging was performed at a current density of 10 A/{m}2 for 6h, 24h, 48h and 72h in 0.9% NaCl aqueous solution at room temperature. Tensile tests were carried out shortly after hydrogen charging. The obtained stress-strain curves showed an increase of yield transformation stresses for forward and reverse martensitic transformations and a decrease of maximum transformation strain. Using Fick’s second law, the transformation temperatures variation can be expressed as a function of the mean concentration of absorbed hydrogen and then taked into account in the SMA constitutive model developed by Chemisky et al (2011). The numerical results are compared to the experimental ones to calibrate the proposed method. Simulations showed that hydrogen diffusion induces a shifting of transfomation temperatures, a decreasing of maximum transformation strain and an increasing of yield transfomation stresses.
Core thermal response and hydrogen generation of the N Reactor hydrogen mitigation design basis accident

DOE Office of Scientific and Technical Information (OSTI.GOV)

White, M.D.; Lombardo, N.J.; Heard, F.J.

1988-04-01

Calculations were performed to determine core heatup, core damage, and subsequent hydrogen production of a hypothetical loss-of-cooling accident at the Department of Energy's N Reactor. The thermal transient response of the reactor core was solved using the TRUMP-BD computer program. Estimates of whole-core thermal damage and hydrogen production were made by weighting the results of multiple half-length pressure tube simulations at various power levels. The Baker-Just and Wilson parabolic rate equations for the metal-water chemical reactions modeled the key phenomena of chemical energy and hydrogen evolution. Unlimited steam was assumed available for continuous oxidation of exposed Zircaloy-2 surfaces and formore » uranium metal with fuel cladding beyond the failure temperature (1038 C). Intact fuel geometry was modeled. Maximum fuel temperatures (1181 C) in the cooled central regions of the core were predicted to occur one-half hour into the accident scenario. Maximum fuel temperatures of 1447 C occurred in the core GSCS-regions at the end of the 10-h transient. After 10-h 26% of the fuel inventory was predicted to have failed. Peak hydrogen evolution equaled 42 g/s, while 10-h integrated hydrogen evolution equaled 167 kg. 12 refs., 12 figs., 2 tabs.« less
A phenology model for Sparganothis fruitworm in Cranberries

USDA-ARS?s Scientific Manuscript database

Larvae of Sparganothis sulfureana Clemens, frequently attack cranberries, often resulting in economic damage to the crop. Because temperature dictates insect growth rate, development can be accurately estimated based on daily temperature measurements. To better predict S. sulfureana development acro...
Molecular hydrogen in the vicinity of NGC 7538 IRS 1 and IRS 2 - Temperature and ortho-to-para ratio

NASA Technical Reports Server (NTRS)

Hoban, Susan; Reuter, Dennis C.; Mumma, Michael J.; Storrs, Alex D.

1991-01-01

Near-infrared spectroscopic observations of the active star-forming region near NGC 7538 IRS 1 and IRS 2 were made. The relative intensities of the v = 1-0 Q(1), Q(3), and Q(5) lines of molecular hydrogen are used to calculate a rotational excitation temperature. Comparison of the measured intensity of the Q(2) transition relative to the intensity of Q(1) and Q(3) permitted the retrieval of the ratio of ortho-to-para hydrogen. It is found that an ortho-to-para ratio of between 1.6 and 2.35 is needed to explain the Q-branch line intensity ratios, depending on the excitation model used. This range in ortho-to-para ratios implies a range of molecular hydrogen formation temperature of approximately 105 K to 140 K.
High-rate/high-temperature capability of a single-layer zicar-separator nickel-hydrogen cell

NASA Technical Reports Server (NTRS)

Wheeler, James R.

1995-01-01

A 50 Ampere-hour nickel-hydrogen cell with a single-layer Zircar separator stack design was fully charged and then discharged at a 2C current rate to an end voltage of 1 volt. This extreme test resulted in high temperatures which were recorded at three locations on the cell, i.e., the cell wall, the boss (barrel of the compression seal), and a terminal. The results provide new information about the high-temperature and high-discharge-rate capabilities of nickel-hydrogen cells. This information also adds to the growing data base for single-layer zirconium-oxide-cloth (Zircar) separator cell designs.

Magnetically Recoverable Supported Ruthenium Catalyst for Hydrogenation of Alkynes and Transfer Hydrogenation of Carbonyl Compounds

EPA Science Inventory

A ruthenium (Ru) catalyst supported on magnetic nanoparticles (NiFe2O4) has been successfully synthesized and used for hydrogenation of alkynes at room temperature as well as transfer hydrogenation of a number of carbonyl compounds under microwave irradiation conditions. The cata...
In situ probing of doping- and stress-mediated phase transitions in a single-crystalline VO2 nanobeam by spatially resolved Raman spectroscopy

NASA Astrophysics Data System (ADS)

Chang, Sung-Jin; Park, Jong Bae; Lee, Gaehang; Kim, Hae Jin; Lee, Jin-Bae; Bae, Tae-Sung; Han, Young-Kyu; Park, Tae Jung; Huh, Yun Suk; Hong, Woong-Ki

2014-06-01

We demonstrate an experimental in situ observation of the temperature-dependent evolution of doping- and stress-mediated structural phase transitions in an individual single-crystalline VO2 nanobeam on a Au-coated substrate under exposure to hydrogen gas using spatially resolved Raman spectroscopy. The nucleation temperature of the rutile R structural phase in the VO2 nanobeam upon heating under hydrogen gas was lower than that under air. The spatial structural phase evolution behavior along the length of the VO2 nanobeam under hydrogen gas upon heating was much more inhomogeneous than that along the length of the same nanobeam under air. The triclinic T phase of the VO2 nanobeam upon heating under hydrogen gas transformed to the R phase and this R phase was stabilized even at room temperature in air after sample cooling. In particular, after the VO2 nanobeam with the R phase was annealed at approximately 250 °C in air, it exhibited the monoclinic M1 phase (not the T phase) at room temperature during heating and cooling cycles. These results were attributed to the interplay between hydrogen doping and stress associated with nanobeam-substrate interactions. Our study has important implications for engineering metal-insulator transition properties and developing functional devices based on VO2 nanostructures through doping and stress.We demonstrate an experimental in situ observation of the temperature-dependent evolution of doping- and stress-mediated structural phase transitions in an individual single-crystalline VO2 nanobeam on a Au-coated substrate under exposure to hydrogen gas using spatially resolved Raman spectroscopy. The nucleation temperature of the rutile R structural phase in the VO2 nanobeam upon heating under hydrogen gas was lower than that under air. The spatial structural phase evolution behavior along the length of the VO2 nanobeam under hydrogen gas upon heating was much more inhomogeneous than that along the length of the same nanobeam under air. The triclinic T phase of the VO2 nanobeam upon heating under hydrogen gas transformed to the R phase and this R phase was stabilized even at room temperature in air after sample cooling. In particular, after the VO2 nanobeam with the R phase was annealed at approximately 250 °C in air, it exhibited the monoclinic M1 phase (not the T phase) at room temperature during heating and cooling cycles. These results were attributed to the interplay between hydrogen doping and stress associated with nanobeam-substrate interactions. Our study has important implications for engineering metal-insulator transition properties and developing functional devices based on VO2 nanostructures through doping and stress. Electronic supplementary information (ESI) available: Illustration, photograph, Raman data, and EDX spectra. See DOI: 10.1039/c4nr01118j
Percolation Features on Climate Network under Attacks of El Niño Events

NASA Astrophysics Data System (ADS)

Lu, Z.

2015-12-01

Percolation theory under different attacks is one of the main research areas in complex networks but never be applied to investigate climate network. In this study, for the first time we construct a climate network of surface air temperature field to analyze its percolation features. Here, we regard El Niño event as a kind of naturally attacks generated from Pacific Ocean to attack its upper climate network. We find that El Niño event leads an abrupt percolation phase transition to the climate network which makes it splitting and unstable suddenly. Comparing the results of the climate network under three different forms of attacks, including most connected attack (MA), localized attack (LA) and random attack (RA) respectively, it is found that both MA and LA lead first-order transition and RA leads second-order transition to the climate network. Furthermore, we find that most real attacks consist of all these three forms of attacks. With El Niño event emerging, the ratios of LA and MA increase and dominate the style of attack while RA decreasing. It means the percolation phase transition due to El Niño events is close to first-order transition mostly affected by LA and MA. Our research may help us further understand two questions from perspective of percolation on network: (1) Why not all warming in Pacific Ocean but El Niño events could affect the climate. (2) Why the climate affected by El Niño events changes abruptly.
Low temperature, low pressure hydrogen gettering

DOEpatents

Anderson, D.R.; Courtney, R.L.; Harrah, L.A.

1975-07-22

A system is described for the gettering of hydrogen and its isotopes. The gettering materials are painted or coated onto, or otherwise disposed in an area or volume from which hydrogen is to be removed. (auth)
Possible Role of Hydrogen in the Earth Core

NASA Astrophysics Data System (ADS)

Takahashi, E.; Imai, T.

2011-12-01

Possible role of hydrogen in the Earth core has been discussed by Stevenson (1977) and demonstrated experimentally by Fukai (1984), Okuchi (1997) and others. Planetary theory proposes a possibility of hydrogen incorporation in Earth's magma ocean from ambient solar nebula gas (Ikoma & Genda 2005, Genda & Ikoma 2008). More recently, migration of snow line during planet formation was examined (Min et al., 2010; Oka et al, 2011) and it was proposed that the Earth building material originally contained abundant water as ice and hydrous minerals. Therefore, it is very important to investigate the fate of water in the planet building process and clarify the role of hydrogen in the planetary core. Using SPring-8 synchrotron (NaCl capsule, LiAlH4 as hydrogen source), we determined the melting curve of FeH up to 20 GPa under hydrogen saturated conditions (Sakamaki, Takahashi et al, 2009). Observed melting point is below 1300C and has a very small dT/dP slope. By extrapolating the melting curve using Lindeman's law, we proposed that hydrogen could lower the melting temperature of the Earth core by more than 1500K than current estimate. Here we report our new experiments using SPring-8 synchrotron (single crystal diamond capsule, water as hydrogen source). Hydrogen concentration and melting temperature of FeHx that coexists with hydrous mantle minerals were determined at 15-20GPa and 1000-1600C. We show that 1) hydrogen concentration in FeHx at 1000C, coexisting with hydrous-B and ringwoodite is approximately X=0.6. 2) Upon heating, hydrous-B decomposes and hydrogen strongly partitions into FeHx (X=0.8~1.0) than ringwoodite. 3) FeHx that coexists with ringwoodite melts between ~1300C (solidus) and ~1600C (liquidus). Combined our new experiments with those by Sakamaki et al (2009) and Shibazaki et al (2009), partitioning of hydrogen between proto-core and primitive mantle is discussed. We propose that >90% of water in the source material may have entered the Earth core. Given large hydrogen concentration in the Earth core, temperature of the outermost core could be as low as that of lower mantle adiabat. Presence of the light element-rich layer at the top 300km layer of the outer core (Helffrich & Kaneshima, 2010) may be easily understood if there is no temperature gap between the core and the lower mantle.
Effects of hydrogen atom spin exchange collisions on atomic hydrogen maser oscillation frequency

NASA Technical Reports Server (NTRS)

Crampton, S. B.

1979-01-01

Frequency shifts due to collisions between hydrogen atoms in an atomic hydrogen maser frequency standard are studied. Investigations of frequency shifts proportional to the spin exchange frequency shift cross section and those proportional to the duration of exchange collisions are discussed. The feasibility of operating a hydrogen frequency standard at liquid helium temperatures is examined.
Hydrogen storage methods.

PubMed

Züttel, Andreas

2004-04-01

Hydrogen exhibits the highest heating value per mass of all chemical fuels. Furthermore, hydrogen is regenerative and environmentally friendly. There are two reasons why hydrogen is not the major fuel of today's energy consumption. First of all, hydrogen is just an energy carrier. And, although it is the most abundant element in the universe, it has to be produced, since on earth it only occurs in the form of water and hydrocarbons. This implies that we have to pay for the energy, which results in a difficult economic dilemma because ever since the industrial revolution we have become used to consuming energy for free. The second difficulty with hydrogen as an energy carrier is its low critical temperature of 33 K (i.e. hydrogen is a gas at ambient temperature). For mobile and in many cases also for stationary applications the volumetric and gravimetric density of hydrogen in a storage material is crucial. Hydrogen can be stored using six different methods and phenomena: (1) high-pressure gas cylinders (up to 800 bar), (2) liquid hydrogen in cryogenic tanks (at 21 K), (3) adsorbed hydrogen on materials with a large specific surface area (at T<100 K), (4) absorbed on interstitial sites in a host metal (at ambient pressure and temperature), (5) chemically bonded in covalent and ionic compounds (at ambient pressure), or (6) through oxidation of reactive metals, e.g. Li, Na, Mg, Al, Zn with water. The most common storage systems are high-pressure gas cylinders with a maximum pressure of 20 MPa (200 bar). New lightweight composite cylinders have been developed which are able to withstand pressures up to 80 MPa (800 bar) and therefore the hydrogen gas can reach a volumetric density of 36 kg.m(-3), approximately half as much as in its liquid state. Liquid hydrogen is stored in cryogenic tanks at 21.2 K and ambient pressure. Due to the low critical temperature of hydrogen (33 K), liquid hydrogen can only be stored in open systems. The volumetric density of liquid hydrogen is 70.8 kg.m(-3), and large volumes, where the thermal losses are small, can cause hydrogen to reach a system mass ratio close to one. The highest volumetric densities of hydrogen are found in metal hydrides. Many metals and alloys are capable of reversibly absorbing large amounts of hydrogen. Charging can be done using molecular hydrogen gas or hydrogen atoms from an electrolyte. The group one, two and three light metals (e.g. Li, Mg, B, Al) can combine with hydrogen to form a large variety of metal-hydrogen complexes. These are especially interesting because of their light weight and because of the number of hydrogen atoms per metal atom, which is two in many cases. Hydrogen can also be stored indirectly in reactive metals such as Li, Na, Al or Zn. These metals easily react with water to the corresponding hydroxide and liberate the hydrogen from the water. Since water is the product of the combustion of hydrogen with either oxygen or air, it can be recycled in a closed loop and react with the metal. Finally, the metal hydroxides can be thermally reduced to metals in a solar furnace. This paper reviews the various storage methods for hydrogen and highlights their potential for improvement and their physical limitations.
Hydrogen storage methods

NASA Astrophysics Data System (ADS)

Züttel, Andreas

Hydrogen exhibits the highest heating value per mass of all chemical fuels. Furthermore, hydrogen is regenerative and environmentally friendly. There are two reasons why hydrogen is not the major fuel of today's energy consumption. First of all, hydrogen is just an energy carrier. And, although it is the most abundant element in the universe, it has to be produced, since on earth it only occurs in the form of water and hydrocarbons. This implies that we have to pay for the energy, which results in a difficult economic dilemma because ever since the industrial revolution we have become used to consuming energy for free. The second difficulty with hydrogen as an energy carrier is its low critical temperature of 33 K (i.e. hydrogen is a gas at ambient temperature). For mobile and in many cases also for stationary applications the volumetric and gravimetric density of hydrogen in a storage material is crucial. Hydrogen can be stored using six different methods and phenomena: (1) high-pressure gas cylinders (up to 800 bar), (2) liquid hydrogen in cryogenic tanks (at 21 K), (3) adsorbed hydrogen on materials with a large specific surface area (at T<100 K), (4) absorbed on interstitial sites in a host metal (at ambient pressure and temperature), (5) chemically bonded in covalent and ionic compounds (at ambient pressure), or (6) through oxidation of reactive metals, e.g. Li, Na, Mg, Al, Zn with water. The most common storage systems are high-pressure gas cylinders with a maximum pressure of 20 MPa (200 bar). New lightweight composite cylinders have been developed which are able to withstand pressures up to 80 MPa (800 bar) and therefore the hydrogen gas can reach a volumetric density of 36 kg.m-3, approximately half as much as in its liquid state. Liquid hydrogen is stored in cryogenic tanks at 21.2 K and ambient pressure. Due to the low critical temperature of hydrogen (33 K), liquid hydrogen can only be stored in open systems. The volumetric density of liquid hydrogen is 70.8 kg.m-3, and large volumes, where the thermal losses are small, can cause hydrogen to reach a system mass ratio close to one. The highest volumetric densities of hydrogen are found in metal hydrides. Many metals and alloys are capable of reversibly absorbing large amounts of hydrogen. Charging can be done using molecular hydrogen gas or hydrogen atoms from an electrolyte. The group one, two and three light metals (e.g. Li, Mg, B, Al) can combine with hydrogen to form a large variety of metal-hydrogen complexes. These are especially interesting because of their light weight and because of the number of hydrogen atoms per metal atom, which is two in many cases. Hydrogen can also be stored indirectly in reactive metals such as Li, Na, Al or Zn. These metals easily react with water to the corresponding hydroxide and liberate the hydrogen from the water. Since water is the product of the combustion of hydrogen with either oxygen or air, it can be recycled in a closed loop and react with the metal. Finally, the metal hydroxides can be thermally reduced to metals in a solar furnace. This paper reviews the various storage methods for hydrogen and highlights their potential for improvement and their physical limitations.
Surface Treatment of Plastic Substrates using Atomic Hydrogen Generated on Heated Tungsten Wire at Low Temperatures

NASA Astrophysics Data System (ADS)

Heya, Akira; Matsuo, Naoto

2007-06-01

The surface properties of a plastic substrate were changed by a novel surface treatment called atomic hydrogen annealing (AHA). In this method, a plastic substrate was exposed to atomic hydrogen generated by cracking hydrogen molecules on heated tungsten wire. For the substrate, surface roughness was increased and halogen elements (F and Cl) were selectively etched by AHA. AHA was useful for pretreatment before film deposition on a plastic substrate because the changes in surface state relate to adhesion improvement. It is concluded that this method is a promising technique for preparing high-performance plastic substrates at low temperatures.
Behavior of implanted hydrogen in ferritic/martensitic steels under irradiation

NASA Astrophysics Data System (ADS)

Wan, F.; Takahashi, H.; Ohnuki, S.; Nagasaki, R.

1988-07-01

The aim of this study was to clarify the behavior of hydrogen under irradiation in ferritic/martensitic stainless steel Fe-10Cr-2Mo-1Ni. Hydrogen was implanted into the specimens by ion accelerator or chemical cathodic charging method, followed by electron irradiation in a HVEM at temperatures from room temperature to 773 K. Streaks in the electron diffraction patterns were observed only during electron irradiation at 623-723 K. From these results it is suggested that the occurrence of the streak pattern is due to the formation of radiation-induced complexes of Ni or Cr with hydrogen along <100> directions.
Solvent induced temperature dependencies of NMR parameters of hydrogen bonded anionic clusters

NASA Astrophysics Data System (ADS)

Golubev, Nikolai S.; Shenderovich, Ilja G.; Tolstoy, Peter M.; Shchepkin, Dmitry N.

2004-07-01

The solvent induced temperature dependence of NMR parameters (proton and fluorine chemical shifts, the two-bond scalar spin coupling constant across the hydrogen bridge, 2hJFF) for dihydrogen trifluoride anion, (FH) 2F -, in a polar aprotic solvent, CDF 3/CDF 2Cl, is reported and discussed. The results are interpreted in terms of a simple electrostatic model, accounting a decrease of electrostatic repulsion of two negatively charged fluorine atoms on placing into a dielectric medium. The conclusion is drawn that polar medium causes some contraction of hydrogen bonds in ionic clusters combined with a decrease of hydrogen bond asymmetry.
Emissions of nitrogen oxides from an experimental hydrogen-fueled gas turbine combustor

NASA Technical Reports Server (NTRS)

Norgren, C. T.; Ingebo, R. D.

1974-01-01

The effect of operating variables of a hydrogen fueled combustor on exhaust concentrations of total oxides of nitrogen was determined at inlet-air temperature levels up to 810 K, pressure of 414,000N/sa m, and reference velocity of 21.3 m/sec. The combustor, which was originally designed for hydrocarbon fuel produced a NO(x) concentration of 380 ppm with hydrogen at 810 K inlet-air temperature. A reduction in NO(x) of about 30 % was obtained by modification to a lean or rich primary zone. The lowest NO(x) levels obtained with hydrogen were equivalent to those of the reference combustor burning hydrocarbon fuels.
Hydrogen adsorption and diffusion, and subcritical-crack growth in high-strength steels and nickel base alloys

NASA Technical Reports Server (NTRS)

Wei, R. P.; Klier, K.; Simmons, G. W.

1974-01-01

Coordinated studies of the kinetics of crack growth and of hydrogen adsorption and diffusion were initiated to develop information that is needed for a clearer determination of the rate controlling process and possible mechanism for hydrogen enhanced crack growth, and for estimating behavior over a range of temperatures and pressures. Inconel 718 alloy and 18Ni(200) maraging steel were selected for these studies. 18Ni(250) maraging steel, 316 stainless steel, and iron single crystal of (111) orientation were also included in the chemistry studies. Crack growth data on 18Ni(250) maraging steel from another program are included for comparison. No sustained-load crack growth was observed for the Inconel 718 alloy in gaseous hydrogen. Gaseous hydrogen assisted crack growth in the 18Ni maraging steels were characterized by K-independent (Stage 2) extension over a wide range of hydrogen pressures (86 to 2000 torr or 12 kN/m2 to 266 kN/m2) and test temperatures (-60 C to +100 C). The higher strength 18Ni(250) maraging steel was more susceptible than the lower strength 200 grade. A transition temperature was observed, above which crack growth rates became diminishingly small.
Process for oxidation of hydrogen halides to elemental halogens

DOEpatents

Lyke, Stephen E.

1992-01-01

An improved process for generating an elemental halogen selected from chlorine, bromine or iodine, from a corresponding hydrogen halide by absorbing a molten salt mixture, which includes sulfur, alkali metals and oxygen with a sulfur to metal molar ratio between 0.9 and 1.1 and includes a dissolved oxygen compound capable of reacting with hydrogen halide to produce elemental halogen, into a porous, relatively inert substrate to produce a substrate-supported salt mixture. Thereafter, the substrate-supported salt mixture is contacted (stage 1) with a hydrogen halide while maintaining the substrate-supported salt mixture during the contacting at an elevated temperature sufficient to sustain a reaction between the oxygen compound and the hydrogen halide to produce a gaseous elemental halogen product. This is followed by purging the substrate-supported salt mixture with steam (stage 2) thereby recovering any unreacted hydrogen halide and additional elemental halogen for recycle to stage 1. The dissolved oxygen compound is regenerated in a high temperature (stage 3) and an optical intermediate temperature stage (stage 4) by contacting the substrate-supported salt mixture with a gas containing oxygen whereby the dissolved oxygen compound in the substrate-supported salt mixture is regenerated by being oxidized to a higher valence state.
South Pole Hydrogen Distribution for Present Lunar Conditions: Implications for Past Impacts

NASA Technical Reports Server (NTRS)

Elphic, R. C.; Paige, D. A.; Siegler, M. A.; Vasavada, A. R.; Eke, V. R.; Teodoro, L. F. A.; Lawrence, D. J.

2010-01-01

It has been known since the Lunar Prospector mission that the poles of the Moon evidently harbor enhanced concentrations of hydrogen [1,2]. The physical and chemical form of the hydrogen has been much debated. Using imagery from Clementine it was possible to roughly estimate permanently-shadowed regions (PSRs), and to perform image reconstructions of the Lunar Prospector epithermal neutron flux maps [3,4]. The hydrogen concentrations resulting from these reconstructions were consistent with a few weight percent water ice in selected locations. With the LCROSS impact, we now know that hydrogen in the form of ice does exist in lunar polar cold traps [5]. Armed with this information, and new data from LRO/Diviner, we can examine whether the pre-sent-day distribution of hydrogen in the form of water ice is consistent with a past large impact that delivered a large mass of volatiles to the lunar surface. These volatiles, mixed with solid impact ejecta, would then be lost from locations having high mean temperatures but would otherwise remain trapped in locations with sufficiently low mean annual temperatures [6]. The time scales for loss would depend on the location-dependent temperatures as well as impact history.
Dehydrogenation of goethite in Earth’s deep lower mantle

DOE Office of Scientific and Technical Information (OSTI.GOV)

Hu, Qingyang; Kim, Duck Young; Liu, Jin

2017-01-31

The cycling of hydrogen influences the structure, composition, and stratification of Earth’s interior. Our recent discovery of pyrite-structured iron peroxide (designated as the P phase) and the formation of the P phase from dehydrogenation of goethite FeO 2H implies the separation of the oxygen and hydrogen cycles in the deep lower mantle beneath 1,800 km. Here we further characterize the residual hydrogen, x, in the P-phase FeO 2Hx. Using a combination of theoretical simulations and high-pressure–temperature experiments, we calibrated the x dependence of molar volume of the P phase. Within the current range of experimental conditions, we observed a compositionalmore » range of P phase of 0.39 < x < 0.81, corresponding to 19–61% dehydrogenation. Increasing temperature and heating time will help release hydrogen and lower x, suggesting that dehydrogenation could be approaching completion at the high-temperature conditions of the lower mantle over extended geological time. Our observations indicate a fundamental change in the mode of hydrogen release from dehydration in the upper mantle to dehydrogenation in the deep lower mantle, thus differentiating the deep hydrogen and hydrous cycles.« less
Characterization and Modeling of Electrical Response of Electrode Catalyzed Reactions in AIGaN/GaN-Based Gas Sensors

NASA Astrophysics Data System (ADS)

Melby, Jacob H.

AlGaN/GaN high electron mobility transistors (HEMT) and AlGaN/GaN diodes have promise for use as hydrogen and hydrocarbon sensors for a variety of industrial, military, and commercial applications. These semiconductor-based sensors have a number of advantages over other sensor technologies, such as the ability to operate at high temperatures, in corrosive environments, or under ionizing radiation. The high sensitivity of these devices to hydrogen-containing gases is associated with polarization differences within the AlGaN/GaN heterostructure that give rise to the formation of a two-dimensional electron gas (2DEG); exposure of the device to hydrogen changes the density of the 2DEG, which can be detected in a HEMT or diode structure. Although sensitivity to a range of gases has been reported, the factors that influence the behavior of the sensors are not well studied. The overarching goals of the research that follows were to determine how gas exposure conditions affect sensor behavior, to characterize and model the relationship between the electrical response of the sensors and the external gaseous environment, and to investigate the effects of using different metal catalysts on sensor behavior. The heterostructures used in this work were grown via metalorganic vapor phase epitaxy (MOVPE). Schottky diode and transistor devices employing platinum-group (Pd, Pt, Rh, Ir, Ru, and Os) catalysts were fabricated to allow electrical sensitivity in the presence of hydrogen and hydrogen containing gases. The generation of atomic hydrogen on the catalyst surface results in the rapid formation of hydrogen dipoles at the metal-semiconductor interface, which produces a measurable electronic response. The electrical response of Pt-gated HEMT-based sensors were measured in a flowing gaseous stream consisting of hydrogen in a pure nitrogen diluent at ambient and elevated temperatures. The transistors exhibited excellent transfer characteristics for temperatures ranging from 25°C to 125°C. The absolute current change was measured as a function of hydrogen concentration and compared with simulated curves based on the Langmuir isotherm and four other modified isotherms at a sensor temperature of 125°C. The sensor response was found to monotonically increase for a wide range of hydrogen concentrations (500 ppb to 5 vol%). It was found that the Langmuir isotherm, which treats all hydrogen binding sites as equivalent, was inadequate to describe the sensor response. A simple two-state model involving two distinct hydrogen binding states that have previously been observed in surface studies was found to adequately describe the response of these sensors from 500 ppb to 5 vol% hydrogen in nitrogen. Other modified Langmuir models were also analyzed and compared with the two-state model. While the models based on modified isotherms all yielded good fits to the data, the simpler two-state model (based upon a weakly bound and strongly bound hydrogen atom) and the Sips model (with distribution of states skewed towards higher binding energies) more closely match results from surface studies of dissociative desorption of hydrogen on Pt. Either of these models should therefore serve as a reasonable foundation for understanding and modeling the response of AlGaN/GaN-based hydrogen sensors with Pt catalysts. The electrical response of a Pt-gated HEMT-based sensor was also measured in a flowing gaseous stream consisting of hydrogen in air at elevated temperatures. The sensor response was found to monotonically increase for a narrow range of hydrogen pressures (1000 ppm to 4 vol%). Oxygen is found to decrease sensor response magnitude and increase the sensor response time. A modified Langmuir isotherm was found to adequately describe the influence of oxygen on a Pt-gated HEMT-based sensor under a narrow range of conditions. Additional sensor measurements were conducted on AlGaN/GaN diode sensors employing a variety of platinum-group catalysts. The influence of oxygen on the sensor response was found to be highly dependent upon the chemistry of hydrogen-oxygen interaction on the catalyst interface. A sensor diode array was fabricated using a ternary Pdx CuyAu1-x-y composition spread alloy catalyst and tested in a flowing gaseous stream consisting of pure hydrogen in nitrogen at room temperature. The resulting diode sensitivity was mapped as a function of composition and revealed intriguing hot spots of hydrogen sensitivity. Numerous technological challenges prevented further exploration of the ternary alloy spread; however, the preliminary results of this structure suggest that a reduction in hydrogen binding energy on the surface can result in a substantial increase in hydrogen dipoles at the metal semiconductor interface. Sensitivity to methane and ethylene was demonstrated using AlGaN/GaN-based sensors. Detection of methane and ethylene require elevated temperatures to break the C-H bond and produce atomic hydrogen. The sensor response is significantly more complicated than hydrogen and not always well-behaved with respect to temperature and time. XPS measurements conducted at CMU indicate a buildup of carbon on the platinum surface upon hydrocarbon exposure, trending toward a saturated carbon content. Lastly, operation of a diode sensor was examined in-situ under high hydrostatic pressure (2000psi) in both pure water and helium. Numerous stability issues were addressed in the course of these experiments. The steady-state influence of hydrostatic pressures on the diode sensor was found to be negligible in the absence of hydrogen. Hydrogen sensitivity was demonstrated in pure water with a hydrogen overpressure for devices employing an epoxy membrane. The same diode device failed to detect a large methane overpressure in water at room temperature and water at 80°C.
Room temperature micro-hydrogen-generator

NASA Astrophysics Data System (ADS)

Gervasio, Don; Tasic, Sonja; Zenhausern, Frederic

A new compact and cost-effective hydrogen-gas generator has been made that is well suited for supplying hydrogen to a fuel-cell for providing base electrical power to hand-carried appliances. This hydrogen-generator operates at room temperature, ambient pressure and is orientation-independent. The hydrogen-gas is generated by the heterogeneous catalytic hydrolysis of aqueous alkaline borohydride solution as it flows into a micro-reactor. This reactor has a membrane as one wall. Using the membrane keeps the liquid in the reactor, but allows the hydrogen-gas to pass out of the reactor to a fuel-cell anode. Aqueous alkaline 30 wt% borohydride solution is safe and promotes long application life, because this solution is non-toxic, non-flammable, and is a high energy-density (≥2200 W-h per liter or per kilogram) hydrogen-storage solution. The hydrogen is released from this storage-solution only when it passes over the solid catalyst surface in the reactor, so controlling the flow of the solution over the catalyst controls the rate of hydrogen-gas generation. This allows hydrogen generation to be matched to hydrogen consumption in the fuel-cell, so there is virtually no free hydrogen-gas during power generation. A hydrogen-generator scaled for a system to provide about 10 W electrical power is described here. However, the technology is expected to be scalable for systems providing power spanning from 1 W to kW levels.
Pressure-tight closure for thermoelements

DOE Office of Scientific and Technical Information (OSTI.GOV)

Not Available

1937-06-14

The thermoelements were arranged in a pressure-tight housing for measuring temperatures on the inside of high-pressure hydrogenation equipment. Should the housing ever leak due to failure of the material or the grinding action of the high sand content of the coal paste, the stall was liable to be set on fire. If, in an installation protected in this manner, an element housing should leak, the pressure tight closure at one end of the housing prevented an escape of the gas and product and the stall could continue to run without danger. The final form of this closure was discussed inmore » detail in this report. In the development of this closure, particular value was attached to a compact construction. In the sealing for a 30-mm high pressure tube, four steel and four constantan wires were insulated and arranged pressure-tight. Each of the three fillers had a different purpose. The hard-rubber insert took the surface pressure, the rubber stopper provided a seal and the cast gypsum provided protection against heat should hot gas or product reach the closure in case of a leaky housing. Two drawings were given showing the thermoelement-closure, and the final form of the closure. The report discussed methods of evacuating from the thermohousings any accumulations of condensed water, which could damage insulation, or hydrogen, which continually diffused in small amounts during operation and which could attack the iron elements of the thermocouples. The pressure-tight closures for thermoelements had been successful at preventing fires due to leakage for more than nine months of operation. 2 sketches.« less
Nuclear spin polarized H and D by means of spin-exchange optical pumping

NASA Astrophysics Data System (ADS)

Stenger, Jörn; Grosshauser, Carsten; Kilian, Wolfgang; Nagengast, Wolfgang; Ranzenberger, Bernd; Rith, Klaus; Schmidt, Frank

1998-01-01

Optically pumped spin-exchange sources for polarized hydrogen and deuterium atoms have been demonstrated to yield high atomic flow and high electron spin polarization. For maximum nuclear polarization the source has to be operated in spin temperature equilibrium, which has already been demonstrated for hydrogen. In spin temperature equilibrium the nuclear spin polarization PI equals the electron spin polarization PS for hydrogen and is even larger than PS for deuterium. We discuss the general properties of spin temperature equilibrium for a sample of deuterium atoms. One result are the equations PI=4PS/(3+PS2) and Pzz=PSṡPI, where Pzz is the nuclear tensor polarization. Furthermore we demonstrate that the deuterium atoms from our source are in spin temperature equilibrium within the experimental accuracy.

Detecting Hydrogen Leaking Into A Purged Cavity

NASA Technical Reports Server (NTRS)

Stinson, William M.

1992-01-01

Hydrogen content of mixture of hydrogen and helium gases computed from measurements of pressure, density, and temperature of mixture. Here purpose is to estimate size of leak of combustible gas into cavity purged by pressurized inert gas.
Investigation of hydrogen evolution activity for the nickel, nickel-molybdenum nickel-graphite composite and nickel-reduced graphene oxide composite coatings

NASA Astrophysics Data System (ADS)

Jinlong, Lv; Tongxiang, Liang; Chen, Wang

2016-03-01

The nickel, nickel-molybdenum alloy, nickel-graphite and nickel-reduced graphene oxide composite coatings were obtained by the electrodeposition technique from a nickel sulfate bath. Nanocrystalline molybdenum, graphite and reduced graphene oxide in nickel coatings promoted hydrogen evolution reaction in 0.5 M H2SO4 solution at room temperature. However, the nickel-reduced graphene oxide composite coating exhibited the highest electrocatalytic activity for the hydrogen evolution reaction in 0.5 M H2SO4 solution at room temperature. A large number of gaps between 'cauliflower' like grains could decrease effective area for hydrogen evolution reaction in slight amorphous nickel-molybdenum alloy. The synergistic effect between nickel and reduced graphene oxide promoted hydrogen evolution, moreover, refined grain in nickel-reduced graphene oxide composite coating and large specific surface of reduced graphene oxide also facilitated hydrogen evolution reaction.
Tuning the Hydrogen Storage in Magnesium Alloys

NASA Astrophysics Data System (ADS)

Er, Suleyman; de Wijs, Gilles A.; Brocks, Geert

2011-03-01

We investigate the hydrogen storage properties of promising magnesium alloys. Mg H2 (7.6 wt % H) would be a very useful storage material if the (de)hydrogenation kinetics can be improved and the desorption temperature is markedly lowered. Using first principles calculations, we show that hydrides of Mg-transition metal (TM) alloys adopt a structure that promotes faster (de)hydrogenation kinetics, as is also observed in experiment. Within the lightweight TMs, the most promising alloying element is titanium. Alloying Mg with Ti alone, however, is not sufficient to decrease the stability of the hydride phases, which is necessary to reduce the hydrogen desorption temperature. We find that adding aluminium or silicon markedly destabilizes Mg-Ti hydrides and stabilizes Mg-Ti alloys. Finally, we show that controlling the structure of Mg-Ti-Al(Si) system by growing it as multilayers, has a beneficial influence on the thermodynamic properties and makes it a stronger candidate for hydrogen storage.
New porous water ice metastable at atmospheric pressure obtained by emptying a hydrogen-filled ice

PubMed Central

del Rosso, Leonardo; Celli, Milva; Ulivi, Lorenzo

2016-01-01

The properties of some forms of water ice reserve still intriguing surprises. Besides the several stable or metastable phases of pure ice, solid mixtures of water with gases are precursors of other ices, as in some cases they may be emptied, leaving a metastable hydrogen-bound water structure. We present here the first characterization of a new form of ice, obtained from the crystalline solid compound of water and molecular hydrogen called C0-structure filled ice. By means of Raman spectroscopy, we measure the hydrogen release at different temperatures and succeed in rapidly removing all the hydrogen molecules, obtaining a new form of ice (ice XVII). Its structure is determined by means of neutron diffraction measurements. Of paramount interest is that the emptied crystal can adsorb again hydrogen and release it repeatedly, showing a temperature-dependent hysteresis. PMID:27819265
Liquid Iron Alloys with Hydrogen at Outer Core Conditions by First Principles

NASA Astrophysics Data System (ADS)

Umemoto, K.; Hirose, K.

2015-12-01

Since the density of the outer core deduced from seismic data is about 10% lower than that of pure iron at core pressures and temperatures (P-T), it is widely believed that the outer core includes one or more light elements. Although intensive experimental and theoretical studies have been performed so far, the light element in the core has not yet been identified. Comparison of the density and sound velocity of liquid iron alloys with observations, such as the PREM, is a promising way to determine the species and quantity of light alloying component(s) in the outer core. Here we report the results of a first-principles molecular dynamics study on liquid iron alloyed with hydrogen, one of candidates of the light elements. Hydrogen had been much less studied than other candidates. However, hydrogen has been known to reduce the melting temperature of Fe-H solid [1]. Furthermore, very recently, Nomura et al. argued that the outer core may include 24 at.% H in order to be molten under relatively low temperature (< 3600 K) [2]. Since then hydrogen has attracted strong interests. We clarify the effects of hydrogen on density and sound velocity of liquid iron alloys under outer core P-T conditions. It is shown that ~1 wt% hydrogen can reproduce PREM density and sound velocity simultaneously very well. In addition, we show the presence of hydrogen rather reduces Gruneisen parameters. It indicates that, if hydrogen exists in the outer core, temperature profile of the outer core could be changed considerably from one estimated so far. [1] Sakamaki, K., E. Takahashi, Y. Nakajima, Y. Nishihara, K. Funakoshi, T. Suzuki, and Y. Fukai, Phys. Earth Planet. Inter., 174, 192-201 (2009). [2] Nomura, R., K. Hirose, K. Uesugi, Y. Ohishi, A. Tsuchiyama, A. Miyake, and Y. Ueno, Science 31, 522-525 (2014).
Butterfly valve with metal seals controls flow of hydrogen from cryogenic through high temperatures

NASA Technical Reports Server (NTRS)

Johnson, L. D.

1967-01-01

Butterfly valve with metal seals operates over a temperature range of minus 423 degrees to plus 440 degrees F with hydrogen as a medium and in a radiation environment. Media flow is controlled by an internal butterfly disk which is rotated by an actuation shaft.
METHOD OF MAKING DELTA ZIRCONIUM HYDRIDE MONOLITHIC MODERATOR PIECES

DOEpatents

Vetrano, J.B.

1962-01-23

A method is given for preparing large, sound bodies of delta zirconium hydride. The method includes the steps of heating a zirconium body to a temperature of not less than l000 deg C, providing a hydrogen atmosphere for the zirconium body at a pressure not greater than one atmosphere, reducing the temperature slowly to 800 deg C at such a rate that cracks do not form while maintaining the hydrogen pressure substantially constant, and cooling in an atmosphere of hydrogen. (AEC)
Thin film hydrogen sensor

DOEpatents

Cheng, Yang-Tse; Poli, Andrea A.; Meltser, Mark Alexander

1999-01-01

A thin film hydrogen sensor, includes: a substantially flat ceramic substrate with first and second planar sides and a first substrate end opposite a second substrate end; a thin film temperature responsive resistor on the first planar side of the substrate proximate to the first substrate end; a thin film hydrogen responsive metal resistor on the first planar side of the substrate proximate to the fist substrate end and proximate to the temperature responsive resistor; and a heater on the second planar side of the substrate proximate to the first end.
Synfuels from fusion: using the tandem mirror reactor and a thermochemical cycle to produce hydrogen

DOE Office of Scientific and Technical Information (OSTI.GOV)

Werner, R.W.

1982-11-01

This study is concerned with the following area: (1) the tandem mirror reactor and its physics; (2) energy balance; (3) the lithium oxide canister blanket system; (4) high-temperature blanket; (5) energy transport system-reactor to process; (6) thermochemical hydrogen processes; (7) interfacing the GA cycle; (8) matching power and temperature demands; (9) preliminary cost estimates; (10) synfuels beyond hydrogen; and (11) thermodynamics of the H/sub 2/SO/sub 4/-H/sub 2/O system. (MOW)
Hydride compositions

DOEpatents

Lee, Myung W.

1995-01-01

A composition for use in storing hydrogen, and a method for making the composition. The composition comprises a mixture of two or more hydrides, each hydride having a different series of hydrogen sorption isotherms that contribute to the overall isotherms of the mixture. The hydrides are chosen so that the isotherms of the mixture have regions wherein the hydrogen equilibrium pressure increases with increasing hydrogen, preferably linearly. The isotherms of the mixture can be adjusted by selecting hydrides with different isotherms and by varying the amounts of the individual hydrides, or both. Preferably, the mixture is made up of hydrides that have isotherms with substantially flat plateaus and in nearly equimolar amounts. The composition is activated by degassing, exposing to hydrogen and then heating at a temperature below the softening temperature of any of the. constituents so that their chemical and structural integrity is preserved. When the composition is used to store hydrogen, its hydrogen content can be found simply by measuring P.sub.H.sbsb.2 and determining H/M from the isothermic function of the composition.
Investigation of a para-ortho hydrogen reactor for application to spacecraft sensor cooling

NASA Technical Reports Server (NTRS)

Nast, T. C.

1983-01-01

The utilization of solid hydrogen in space for sensor and instrument cooling is a very efficient technique for long term cooling or for cooling at high heat rates. The solid hydrogen can provide temperatures as low as 7 to 8 K to instruments. Vapor cooling is utilized to reduce parasitic heat inputs to the 7 to 8 K stage and is effective in providing intermediate cooling for instrument components operating at higher temperatures. The use of solid hydrogen in place of helium may lead to weight reductions as large as a factor of ten and an attendent reduction in system volume. The results of an investigation of a catalytic reactor for use with a solid hydrogen cooling system is presented. Trade studies were performed on several configurations of reactor to meet the requirements of high reactor efficiency with low pressure drop. Results for the selected reactor design are presented for both liquid hydrogen systems operating at near atmospheric pressure and the solid hydrogen cooler operating as low as 1 torr.
Efficacy of ketanserin in the therapy of Raynaud's phenomenon: thermometric data.

PubMed

Arosio, E; Montesi, G; Zannoni, M; Perbellini, L; Paluani, F; Lechi, A

1991-05-01

After a two-week washout (WO) period with placebo 1 capsule/bid, 12 patients suffering from stable Raynaud's phenomenon were treated with ketanserin (K) 40 mg/bid for fifteen days. Blood pressure, heart rate, and laboratory parameters were evaluated at the end of each period. Patients used diary cards to record the number, duration, and intensity of attacks. Computerized thermometry of the fingers was evaluated at basal temperature after acclimatization, 23 degrees C for thirty minutes; after cold test, 10 degrees C for five minutes; and after thermal recovery, 23 degrees C for eighteen minutes. Results were analyzed statistically by use of Student's t-test for paired data (p less than 0.05). No marked changes were observed in the symptoms of the attacks, but K proved effective in significantly reducing the number and duration of daily attacks and in promoting their spontaneous regression. Thermometry revealed a parallel increase in temperatures, particularly basal and recovery values. The data suggest increased flow and decreased vasospasm following 5-HT2 receptor blockade.
Influence of hydrogen oxidation kinetics on hydrogen environment embrittlement

NASA Technical Reports Server (NTRS)

Walter, R. J.; Kendig, M. W.; Meisels, A. P.

1992-01-01

Results are presented from experiments performed to determine the roles of hydrogen absorption and hydrogen electron transfer on the susceptibility of Fe- and Ni-base alloys to ambient-temperature hydroen embrittlement. An apparent independence is noted between hydrogen environment embrittlement and internal hydrogen embrittlement. The experiments were performed on Inconel 718, Incoloy 903, and A286. The electrochemical results obtained indicate that Inconel 718 either adsorbs hydrogen more rapidly and/or the electrochemical oxidation of the adsorbed hydrogen occurred more rapidly than in the other two materials.
Surface characterisation of ethylene propylene diene rubber upon exposure to aqueous acidic solution

NASA Astrophysics Data System (ADS)

Mitra, Susanta; Ghanbari-Siahkali, Afshin; Kingshott, Peter; Hvilsted, Søren; Almdal, Kristoffer

2006-07-01

Two types of pure ethylene propylene diene rubbers were exposed to two different acids for varying period of time. Surface characterisation was carried out using X-ray photoelectron spectroscopy (XPS). Two EPDM rubbers selected for this study were comparable in co-monomer compositions but significantly different with respect to molar mass and the presence of long chain branching. Both rubbers contained 5-ethylidene-2-norbornene (ENB) as diene. Solution cast films of pure EPDM samples were exposed in two different acidic solutions, viz. chromosulphuric (Cr (VI)/H 2SO 4) and sulphuric acid (H 2SO 4) (20%, v/v) at ambient temperature from 1 to 12 weeks. XPS analysis indicated that several oxygenated species were formed on the surface of both rubbers after exposure. It was postulated from the XPS analyses that both aqueous acidic solutions attacked the olefinic double bonds (C dbnd C) of ENB. Furthermore, 20% Cr (VI)/H 2SO 4 also attacked the allylic carbon-hydrogen (C sbnd H) bonds of ENB resulting in more oxygenated species on the surface compared to 20% H 2SO 4 under identical conditions. Cr (VI) in the 20% Cr (VI)/H 2SO 4 was found to play an important role in alteration of surface chemistry. Studies using a model system consisting of EPDM mixed with Cr (VI) and Cr (III) salts revealed that the change of oxidation state from Cr (VI) to Cr (III) as a consequence of direct involvement of Cr (VI) in the chemical alteration of EPDM surfaces. Interestingly, the presence of long chain branching and molar mass did not significantly influence the chemical processes owing to the acid treatment.
Co-production of hydrogen and carbon nanotubes on nickel foam via methane catalytic decomposition

NASA Astrophysics Data System (ADS)

Ping, Dan; Wang, Chaoxian; Dong, Xinfa; Dong, Yingchao

2016-04-01

The co-production of COx-free hydrogen and carbon nanotubes (CNTs) was achieved on 3-dimensional (3D) macroporous nickel foam (NF) via methane catalytic decomposition (MCD) over nano-Ni catalysts using chemical vapor deposition (CVD) technique. By a simple coating of a NiO-Al2O3 binary mixture sol followed by a drying-calcination-reduction treatment, NF supported composite catalysts (denoted as NiyAlOx/NF) with Al2O3 transition-layer incorporated with well-dispersed nano-Ni catalysts were successfully prepared. The effects of Ni loading, calcination temperature and reaction temperature on the performance for simultaneous production of COx-free hydrogen and CNTs were investigated in detail. Catalysts before and after MCD were characterized by XRD, TPR, SEM, TEM, TG and Raman spectroscopy technology. Results show that increasing Ni loading, lowering calcination temperature and optimizing MCD reaction temperature resulted in high production efficiency of COx-free H2 and carbon, but broader diameter distribution of CNTs. Through detailed parameter optimization, the catalyst with a Ni/Al molar ratio of 0.1, calcination temperature of 550 °C and MCD temperature of 650 °C was favorable to simultaneously produce COx-free hydrogen with a growth rate as high as 10.3% and CNTs with uniform size on NF.
Ruthenium supported on magnetic nanoparticles: An efficient and recoverable catalyst for hydrogenation of alkynes and transfer hydrogenation of carbonyl compounds

EPA Science Inventory

Ruthenium supported on surface modified magnetic nanoparticles (NiFe2O4) has been successfully synthesized and applied for hydrogenation of alkynes at room temperature as well as transfer hydrogenation of a number of carbonyl compounds under microwave irradiation conditions. The ...
A fractal process of hydrogen diffusion in a-Si:H with exponential energy distribution

NASA Astrophysics Data System (ADS)

Hikita, Harumi; Ishikawa, Hirohisa; Morigaki, Kazuo

2017-04-01

Hydrogen diffusion in a-Si:H with exponential distribution of the states in energy exhibits the fractal structure. It is shown that a probability P(t) of the pausing time t has a form of tα (α: fractal dimension). It is shown that the fractal dimension α = Tr/T0 (Tr: hydrogen temperature, T0: a temperature corresponding to the width of exponential distribution of the states in energy) is in agreement with the Hausdorff dimension. A fractal graph for the case of α ≤ 1 is like the Cantor set. A fractal graph for the case of α > 1 is like the Koch curves. At α = ∞, hydrogen migration exhibits Brownian motion. Hydrogen diffusion in a-Si:H should be the fractal process.
Hydrogen production by high temperature water splitting using electron conducting membranes

DOEpatents

Balachandran, Uthamalingam; Wang, Shuangyan; Dorris, Stephen E.; Lee, Tae H.

2006-08-08

A device and method for separating water into hydrogen and oxygen is disclosed. A first substantially gas impervious solid electron-conducting membrane for selectively passing protons or hydrogen is provided and spaced from a second substantially gas impervious solid electron-conducting membrane for selectively passing oxygen. When steam is passed between the two membranes at dissociation temperatures the hydrogen from the dissociation of steam selectively and continuously passes through the first membrane and oxygen selectively and continuously passes through the second membrane, thereby continuously driving the dissociation of steam producing hydrogen and oxygen. The oxygen is thereafter reacted with methane to produce syngas which optimally may be reacted in a water gas shift reaction to produce CO₂and H₂.
Emergence of a High-Temperature Superconductivity in Hydrogen Cycled pd Compounds as AN Evidence for Superstoihiometric H/d Sites

NASA Astrophysics Data System (ADS)

Lipson, Andrei; Castano, Carlos; Miley, George; Lipson, Andrei; Lyakhov, Boris; Mitin, Alexander

2006-02-01

Transport and magnetic properties of hydrogen cycled PdHx and Pd/PdO:Hx (x ~ (4/6) × 10-4) nano-composite consisting of a Pd matrix with hydrogen trapped inside dislocation cores have been studied. The results suggest emergence of a high-temperature superconductivity state of a condensed hydrogen phase confined inside deep dislocation cores in the Pd matrix. The possible role of hydrogen/deuterium filled dislocation nano-tubes is discussed. These dislocation cores could be considered as active centers of LENR triggering due to (i) short D-D separation distance (~Bohr radius); (ii) high-local D-loading in the Pd and the corresponding effective lattice compression; (iii) a large optic phonon energy resulting in a most effective lattice-nuclei energy transfer.
Chemistry of acetylene on platinum (111) and (100) surfaces

PubMed Central

Muetterties, E. L.; Tasi, M.-C.; Kelemen, S. R.

1981-01-01

An ultra-high vacuum experimental study of acetylene chemisorption on Pt(111) and Pt(100) and of the reaction of hydrogen with the acetylene adsorbate has established distinguishing features of carbon-hydrogen bond breaking and making processes as a function of pressure, temperature, and surface crystallography. The rates for both processes are substantially higher on the Pt(100) surface. Net acetylene-hydrogen processes, in the temperature range of 20°C to ≈130°C, are distinctly different on the two surfaces: on Pt(100) the net reaction is hydrogen exchange (1H-2H exchange) and on Pt(111) the only detectable reaction is hydrogenation. Stereochemical differences in the acetylene adsorbate structure are considered to be a contributing factor to the differences in acetylene chemistry on these two surfaces. Images PMID:16593110

Bond-center hydrogen in dilute Si1-xGex alloys: Laplace deep-level transient spectroscopy

NASA Astrophysics Data System (ADS)

Bonde Nielsen, K.; Dobaczewski, L.; Peaker, A. R.; Abrosimov, N. V.

2003-07-01

We apply Laplace deep-level transient spectroscopy in situ after low-temperature proton implantation into dilute Si1-xGex alloys and identify the deep donor state of hydrogen occupying a strained Si-Si bond-center site next to Ge. The activation energy of the electron emission from the donor is ˜158 meV when extrapolated to zero electrical field. We construct a configuration diagram of the Ge-strained site from formation and annealing data and deduce that alloying with ˜1% Ge does not significantly influence the low-temperature migration of hydrogen as compared to elemental Si. We observe two bond-center-type carbon-hydrogen centers and conclude that carbon impurities act as much stronger traps for hydrogen than the alloy Ge atoms.
Quantitative observations of hydrogen-induced, slow crack growth in a low alloy steel

NASA Technical Reports Server (NTRS)

Nelson, H. G.; Williams, D. P.

1973-01-01

Hydrogen-induced slow crack growth, da/dt, was studied in AISI-SAE 4130 low alloy steel in gaseous hydrogen and distilled water environments as a function of applied stress intensity, K, at various temperatures, hydrogen pressures, and alloy strength levels. At low values of K, da/dt was found to exhibit a strong exponential K dependence (Stage 1 growth) in both hydrogen and water. At intermediate values of K, da/dt exhibited a small but finite K dependence (Stage 2), with the Stage 2 slope being greater in hydrogen than in water. In hydrogen, at a constant K, (da/dt) sub 2 varied inversely with alloy strength level and varied essentially in the same complex manner with temperature and hydrogen pressure as noted previously. The results of this study provide support for most of the qualitative predictions of the lattice decohesion theory as recently modified by Oriani. The lack of quantitative agreement between data and theory and the inability of theory to explain the observed pressure dependence of slow crack growth are mentioned and possible rationalizations to account for these differences are presented.
First-principles study of the solid solution of hydrogen in lanthanum

DOE Office of Scientific and Technical Information (OSTI.GOV)

Schoellhammer, Gunther; Herzig, Peter; Wolf, Walter

2011-09-01

Results from first-principles investigations of the energetical, structural, electronic, and vibrational properties of model structures probing the metal-rich region of the lanthanum-hydrogen system, i.e., the region of the solid solution of hydrogen in lanthanum, are presented. We have studied the site preference and the ordering tendency of hydrogen atoms interstitially bonded in close-packed lanthanum. Spatially separated hydrogen atoms have turned out to exhibit an energetical preference for the occupation of octahedral interstitial sites at low temperature. Indications for a reversal of the site preference in favor of the occupation of tetrahedral interstitial sites at elevated temperature have been found. Linearmore » arrangements consisting of pairs of octahedrally and/or tetrahedrally coordinated hydrogen atoms collinearly bonded to a central lanthanum atom have turned out to be energetically favorable structure elements. Further stabilization is achieved if such hydrogen pairs are in turn linked together so that extended chains of La-H bonds are formed. Pair formation and chain linking counteract the energetical preference for octahedral coordination observed for separated hydrogen atoms.« less
Hydrogen storage material and process using graphite additive with metal-doped complex hydrides

DOEpatents

Zidan, Ragaiy [Aiken, SC; Ritter, James A [Lexington, SC; Ebner, Armin D [Lexington, SC; Wang, Jun [Columbia, SC; Holland, Charles E [Cayce, SC

2008-06-10

A hydrogen storage material having improved hydrogen absorbtion and desorption kinetics is provided by adding graphite to a complex hydride such as a metal-doped alanate, i.e., NaAlH.sub.4. The incorporation of graphite into the complex hydride significantly enhances the rate of hydrogen absorbtion and desorption and lowers the desorption temperature needed to release stored hydrogen.
Development of advanced material composites for use as internal insulation for LH2 tanks (gas layer concept)

NASA Technical Reports Server (NTRS)

Gille, J. P.

1972-01-01

A program is described that was conducted to develop an internal insulation system for potential application to the liquid hydrogen tanks of a reusable booster, where the tanks would be subjected to repeated high temperatures. The design of the internal insulation is based on a unique gas layer concept, in which capillary or surface tension effects are used to maintain a stable gas layer, within a cellular core structure, between the tank wall and the contained liquid hydrogen. Specific objectives were to select materials for insulation systems that would be compatible with wall temperatures of 350 F and 650 F during reentry into the earth's atmosphere, and to fabricate and test insulation systems under conditions simulating the operating environment. A materials test program was conducted to evaluate the properties of candidate materials at elevated temperatures and at the temperature of liquid hydrogen, and to determine the compatibility of the materials with a hydrogen atmosphere at the appropriate elevated temperature. The materials that were finally selected included Kapton polyimide films, silicone adhesives, fiber glass batting, and in the case of the 350 F system, Teflon film.
The Development of Silicon Carbide Based Hydrogen and Hydrocarbon Sensors

NASA Technical Reports Server (NTRS)

Liu, Chung-Chiun

1994-01-01

Silicon carbide is a high temperature electronic material. Its potential for development of chemical sensors in a high temperature environment has not been explored. The objective of this study is to use silicon carbide as the substrate material for the construction of chemical sensors for high temperature applications. Sensors for the detection of hydrogen and hydrocarbon are developed in this program under the auspices of Lewis Research Center, NASA. Metal-semiconductor or metal-insulator-semiconductor structures are used in this development. Specifically, using palladium-silicon carbide Schottky diodes as gas sensors in the temperature range of 100 to 400 C are designed, fabricated and assessed. The effect of heat treatment on the Pd-SiC Schottky diode is examined. Operation of the sensors at 400 C demonstrate sensitivity of the sensor to hydrogen and hydrocarbons. Substantial progress has been made in this study and we believe that the Pd-SiC Schottky diode has potential as a hydrogen and hydrocarbon sensor over a wide range of temperatures. However, the long term stability and operational life of the sensor need to be assessed. This aspect is an important part of our future continuing investigation.
Carbon-free H2 production from ammonia triggered at room temperature with an acidic RuO2/γ-Al2O3 catalyst.

PubMed

Nagaoka, Katsutoshi; Eboshi, Takaaki; Takeishi, Yuma; Tasaki, Ryo; Honda, Kyoko; Imamura, Kazuya; Sato, Katsutoshi

2017-04-01

Ammonia has been suggested as a carbon-free hydrogen source, but a convenient method for producing hydrogen from ammonia with rapid initiation has not been developed. Ideally, this method would require no external energy input. We demonstrate hydrogen production by exposing ammonia and O 2 at room temperature to an acidic RuO 2 /γ-Al 2 O 3 catalyst. Because adsorption of ammonia onto the catalyst is exothermic, the catalyst bed is rapidly heated to the catalytic ammonia autoignition temperature, and subsequent oxidative decomposition of ammonia produces hydrogen. A differential calorimeter combined with a volumetric gas adsorption analyzer revealed a large quantity of heat evolved both with chemisorption of ammonia onto RuO 2 and acidic sites on the γ-Al 2 O 3 and with physisorption of multiple ammonia molecules.
Long-term storage of nickel-hydrogen cells

NASA Technical Reports Server (NTRS)

Vaidyanathan, Hari

1987-01-01

Representative samples of nickel hydrogen cells for the INTELSAT program were used to evaluate the effects of prolonged storage under passive conditions such as open circuit discharged at 0 C, room temperature, and -20 C, and under quasidynamic conditions such as top-off charge and trickle charge. Cell capacity declines when cells are stored open-circuit discharged at room temperature, and a second plateau occurs in the discharge curve. Capacity loss was 47 percent for a cell with hydrogen precharge and 24.5 percent for one with no hydrogen precharge. Capacity recovery was observed following top-off charge storage of cells which had exhibited faded capacity as a result of passive storage at room temperature. Cells stored either at -20 C or on trickle charge maintained their capacity. At 0 C storage, the capacity of all three cells under tests was greater than 55 Ah (which exceeds the required minimum of 44 Ah) after 7 months.
Carbon-free H2 production from ammonia triggered at room temperature with an acidic RuO2/γ-Al2O3 catalyst

PubMed Central

Nagaoka, Katsutoshi; Eboshi, Takaaki; Takeishi, Yuma; Tasaki, Ryo; Honda, Kyoko; Imamura, Kazuya; Sato, Katsutoshi

2017-01-01

Ammonia has been suggested as a carbon-free hydrogen source, but a convenient method for producing hydrogen from ammonia with rapid initiation has not been developed. Ideally, this method would require no external energy input. We demonstrate hydrogen production by exposing ammonia and O2 at room temperature to an acidic RuO2/γ-Al2O3 catalyst. Because adsorption of ammonia onto the catalyst is exothermic, the catalyst bed is rapidly heated to the catalytic ammonia autoignition temperature, and subsequent oxidative decomposition of ammonia produces hydrogen. A differential calorimeter combined with a volumetric gas adsorption analyzer revealed a large quantity of heat evolved both with chemisorption of ammonia onto RuO2 and acidic sites on the γ-Al2O3 and with physisorption of multiple ammonia molecules. PMID:28508046
In situ study at high pressure and temperature of the environment of water in hydrous Na and Ca aluminosilicate melts and coexisting aqueous fluids

NASA Astrophysics Data System (ADS)

Le Losq, Charles; Dalou, Célia; Mysen, Bjorn O.

2017-07-01

The bonding and speciation of water dissolved in Na silicate and Na and Ca aluminosilicate melts were inferred from in situ Raman spectroscopy of the samples, in hydrothermal diamond anvil cells, while at crustal temperature and pressure conditions. Raman data were also acquired on Na silicate and Na and Ca aluminosilicate glasses, quenched from hydrous melts equilibrated at high temperature and pressure in a piston cylinder apparatus. In the hydrous melts, temperature strongly influences O-H stretching ν(O-H) signals, reflecting its control on the bonding of protons between different molecular complexes. Pressure and melt composition effects are much smaller and difficult to discriminate with the present data. However, the chemical composition of the melt + fluid system influences the differences between the ν(O-H) signals from the melts and the fluids and, hence, between their hydrogen partition functions. Quenching modifies the O-H stretching signals: strong hydrogen bonds form in the glasses below the glass transition temperature Tg, and this phenomenon depends on glass composition. Therefore, glasses do not necessarily record the O-H stretching signal shape in melts near Tg. The melt hydrogen partition function thus cannot be assessed with certainty using O-H stretching vibration data from glasses. From the present results, the ratio of the hydrogen partition functions of hydrous silicate melts and aqueous fluids mostly depends on temperature and the bulk melt + fluid system chemical composition. This implies that the fractionation of hydrogen isotopes between magmas and aqueous fluids in water-saturated magmatic systems with differences in temperature and bulk chemical composition will be different.
Analysis on Operating Parameter Design to Steam Methane Reforming in Heat Application RDE

NASA Astrophysics Data System (ADS)

Dibyo, Sukmanto; Sunaryo, Geni Rina; Bakhri, Syaiful; Zuhair; Irianto, Ign. Djoko

2018-02-01

The high temperature reactor has been developed with various power capacities and can produce electricity and heat application. One of heat application is used for hydrogen production. Most hydrogen production occurs by steam reforming that operated at high temperature. This study aims to analyze the feasibility of heat application design of RDE reactor in the steam methane reforming for hydrogen production using the ChemCAD software. The outlet temperature of cogeneration heat exchanger is analyzed to be applied as a feed of steam reformer. Furthermore, the additional heater and calculating amount of fuel usage are described. Results show that at a low mass flow rate of feed, its can produce a temperature up to 480°C. To achieve the temperature of steam methane reforming of 850°C the additional fired heater was required. By the fired heater, an amount of fuel usage is required depending on the Reformer feed temperature produced from the heat exchanger of the cogeneration system.
Design and optimization of hydrogen production from hydrothermally pretreated sugarcane bagasse using response surface methodology.

PubMed

Soares, Lais Américo; Braga, Juliana Kawanishi; Motteran, Fabrício; Sakamoto, Isabel Kimiko; Silva, Edson Luiz; Varesche, Maria Bernadete Amâncio

2017-07-01

Hydrogen production from hydrothermally pretreated (200 °C for 10 min at 16 bar) sugarcane bagasse was analyzed using response surface methodology. The yeast extract concentration and the temperature had a significant influence for hydrogen production (p-value 0.027 and 0.009, respectively). Maximum hydrogen production (17.7 mmol/L) was observed with 3 g/L yeast extract at 60 °C (C10). In this conditions were produced acetic acid (50.44 mg/L), butyric acid (209.71 mg/L), ethanol (38.4 mg/L), and methane (6.27 mmol/L). Lower hydrogen productions (3.5 mmol/L and 3.9 mmol/L) were observed under the conditions C7 (2 g/L of yeast extract, 35.8 °C) and C9 (1 g/L of yeast extract, 40 °C), respectively. The low yeast extract concentration and low temperature caused a negative effect on the hydrogen production. By means of denaturing gradient gel electrophoresis 20% of similarity was observed between the archaeal population of mesophilic (35 and 40 °C) and thermophilic (50, 60 and 64 °C) reactors. Likewise, similarity of 22% was noted between the bacterial population for the reactors with the lowest hydrogen production (3.5 mmol/L), at 35.8 °C and with the highest hydrogen production (17.7 mmol/L) at 60 °C demonstrating that microbial population modification was a function of incubation temperature variation.
The activity-composition relationship of oxygen and hydrogen isotopes in aqueous salt solutions: III. Vapor-liquid water equilibration of NaCl solutions to 350°C

NASA Astrophysics Data System (ADS)

Horita, Juske; Cole, David R.; Wesolowski, David J.

1995-03-01

The effect of dissolved NaCl on equilibrium oxygen and hydrogen isotope fractionation factors between liquid water and water vapor was precisely determined in the temperature range from 130-350°C, using two different types of apparatus with static or dynamic sampling techniques of the vapor phase. The magnitude of the oxygen and hydrogen isotope effects of NaCl is proportional to the molality of liquid NaCl solutions at a given temperature. Dissolved NaCl lowers appreciably the hydrogen isotope fractionation factor between liquid water and water vapor over the entire temperature range. NaCl has little effect on the oxygen isotope fractionation factor at temperatures below about 200°C, with the magnitude of the salt effect gradually increasing from 200-350°C. Our results are at notable variance with those of Truesdell (1974) and Kazahaya (1986), who reported large oxygen and hydrogen isotope effects of NaCl with very complex dependencies on temperature and NaCl molality. Our high-temperature results have been regressed along with our previous results between 50 and 100°C (Horita et al., 1993a) and the low-temperature literature data to simple equations which are valid for NaCl solutions from 0 to at least 5 molal NaCl in the temperature range from 10-350°C. Our preliminary results of oxygen isotope fractionation in the system CaCO3-water ± NaCl at 300°C and 1 kbar are consistent with those obtained from the liquid-vapor equilibration experiments, suggesting that the isotope salt effects are common to systems involving brines and any other coexisting phases or species (gases, minerals, dissolved species, etc.). The observed NaCl isotope effects at elevated temperatures should be taken into account in the interpretation of isotopic data of brine-dominated natural systems.
Hydrogen adsorption and diffusion, and subcritical-crack growth in high strength steels and nickel base alloys

NASA Technical Reports Server (NTRS)

Wei, R. P.; Klier, K.; Simmons, G. W.; Chornet, E.

1973-01-01

Embrittlement, or the enhancement of crack growth by gaseous hydrogen in high strength alloys, is of primary interest in selecting alloys for various components in the space shuttle. Embrittlement is known to occur at hydrogen gas pressures ranging from fractions to several hundred atmospheres, and is most severe in the case of martensitic high strength steels. Kinetic information on subcritical crack growth in gaseous hydrogen is sparse at this time. Corroborative information on hydrogen adsorption and diffusion is inadequate to permit a clear determination of the rate controlling process and possible mechanism in hydrogen enhanced crack growth, and for estimating behavior over a range of temperatures and pressures. Therefore, coordinated studies of the kinetics of crack growth, and adsorption and diffusion of hydrogen, using identical materials, have been initiated. Comparable conditions of temperature and pressure will be used in the chemical and mechanical experiments. Inconel 718 alloy and 18Ni(200) maraging steel have been selected for these studies. Results from these studies are expected to provide not only a better understanding of the gaseous hydrogen embrittlement phenomenon itself, but also fundamental information on hydrogen adsorption and diffusion, and crack growth information that can be used directly for design.
Low Cost Nuclear Thermal Rocket Cermet Fuel Element Environment Testing

NASA Technical Reports Server (NTRS)

Bradley, David E.; Mireles, Omar R.; Hickman, Robert R.

2011-01-01

Deep space missions with large payloads require high specific impulse (Isp) and relatively high thrust in order to achieve mission goals in reasonable time frames. Conventional, storable propellants produce average Isp. Nuclear thermal rockets (NTR) capable of high Isp thrust have been proposed. NTR employs heat produced by fission reaction to heat and therefore accelerate hydrogen which is then forced through a rocket nozzle providing thrust. Fuel element temperatures are very high (up to 3000K) and hydrogen is highly reactive with most materials at high temperatures. Data covering the effects of high temperature hydrogen exposure on fuel elements is limited. The primary concern is the mechanical failure of fuel elements which employ high-melting-point metals, ceramics or a combination (cermet) as a structural matrix into which the nuclear fuel is distributed. It is not necessary to include fissile material in test samples intended to explore high temperature hydrogen exposure of the structural support matrices. A small-scale test bed designed to heat fuel element samples via non-contact RF heating and expose samples to hydrogen is being developed to assist in optimal material and manufacturing process selection without employing fissile material. This paper details the test bed design and results of testing conducted to date.
Compact Fuel Element Environment Test

NASA Technical Reports Server (NTRS)

Bradley, D. E.; Mireles, O. R.; Hickman, R. R.; Broadway, J. W.

2012-01-01

Deep space missions with large payloads require high specific impulse (I(sub sp)) and relatively high thrust to achieve mission goals in reasonable time frames. Conventional, storable propellants produce average I(sub sp). Nuclear thermal rockets (NTRs) capable of high I(sub sp) thrust have been proposed. NTR employs heat produced by fission reaction to heat and therefore accelerate hydrogen, which is then forced through a rocket nozzle providing thrust. Fuel element temperatures are very high (up to 3,000 K) and hydrogen is highly reactive with most materials at high temperatures. Data covering the effects of high-temperature hydrogen exposure on fuel elements are limited. The primary concern is the mechanical failure of fuel elements that employ high melting point metals, ceramics, or a combination (cermet) as a structural matrix into which the nuclear fuel is distributed. It is not necessary to include fissile material in test samples intended to explore high-temperature hydrogen exposure of the structural support matrices. A small-scale test bed designed to heat fuel element samples via noncontact radio frequency heating and expose samples to hydrogen for typical mission durations has been developed to assist in optimal material and manufacturing process selection without employing fissile material. This Technical Memorandum details the test bed design and results of testing conducted to date.
Liquid Hydrogenation of Maleic Anhydride with Pd/C Catalyst at Low Pressure and Temperature in Batch Reactor.

PubMed

Kim, Ji Sun; Baek, Jae Ho; Ryu, Young Bok; Hong, Seong-Soo; Lee, Man Sig

2015-01-01

Succinic acid (SA) produced from hydrogenation of maleic anhydride (MAN) is used widely in manufacturing of pharmaceuticals, agrochemicals, surfactants and detergent, green solvent and biodegradable plastic. In this study, we performed that liquid hydrogenation of MAN to SA with 5 wt% Pd supported on activated carbon (Pd/C) at low pressure and temperature. The synthesis of SA was performed in aqueous solution while varying temperature, pressure, catalytic amount and agitation speed. We confirmed that the composition of the products consisting of SA, maleic acid (MA), fumaric acid (FA) and malic acid (MLA) depends on the process. The catalytic characteristics were analyzed by TGA, TEM.
Thermodynamic properties and theoretical rocket performance of hydrogen to 100,000 K and 1.01325 x 10 to the 8th power N/sq m

NASA Technical Reports Server (NTRS)

Patch, R. W.

1971-01-01

The composition and thermodynamic properties were calculated for 100 to 110,000 K and 1.01325 x 10 to the 2nd power to 1.01325 x 10 to the 8th power N/sq m for chemical equilibrium in the Debye-Huckel and ideal-gas approximations. Quantities obtained were the concentrations of hydrogen atoms, protons, free electrons, hydrogen molecules, negative hydrogen ions, hydrogen diatomic molecular ions, and hydrogen triatomic molecular ions, and the enthalpy, entropy, average molecular weight, specific heat at constant pressure, density, and isentropic exponent. Electronically excited states of H and H2 were included. Choked, isentropic, one-dimensional nozzle flow with shifting chemical equilibrium was calculated to the Debye-Huckel and ideal-gas approximations for stagnation temperatures from 2500 to 100,000 K. The mass flow per unit throat area and the sonic flow factor were obtained. The pressure ratio, temperature, velocity, and ideal and vacuum specific impulses at the throat and for pressure ratios as low as 0.000001 downstream were found. For high temperatures at pressures approaching 1.01325 x 10 to the 8th power N/sq m, the ideal-gas approximation was found to be inadequate for calculations of composition, precise thermodynamic properties, and precise nozzle flow. The greatest discrepancy in nozzle flow occurred in the exit temperature, which was as much as 21 percent higher when the Debye-Huckel approximation was used.
MD simulation study of the diffusion and local structure of n-alkanes in liquid and supercritical methanol at infinite dilution.

PubMed

Feng, Huajie; Gao, Wei; Su, Li; Sun, Zhenfan; Chen, Liuping

2017-06-01

The diffusion coefficients of 14 n-alkanes (ranging from methane to n-tetradecane) in liquid and supercritical methanol at infinite dilution (at a pressure of 10.5 MPa and at temperatures of 299 K and 515 K) were deduced via molecular dynamics simulations. Values for the radial distribution function, coordination number, and number of hydrogen bonds were then calculated to explore the local structure of each fluid. The flexibility of the n-alkane (as characterized by the computed dihedral distribution, end-to-end distance, and radius of gyration) was found to be a major influence and hydrogen bonding to be a minor influence on the local structure. Hydrogen bonding reduces the flexibility of the n-alkane, whereas increasing the temperature enhances its flexibility, with temperature having a greater effect than hydrogen bonding on flexibility. Graphical abstract The flexibility of the alkane is a major influence and the hydrogen bonding is a minor influence on the first solvation shell; the coordination numbers of long-chain n-alkanes in the first solvation shell are rather low.
3D-Printable Silicone Materials with Hydrogen Getter Capability

DOE PAGES

Ortiz-Acosta, Denisse; Moore, Tanya; Safarik, Douglas Joseph; ...

2018-03-01

Organic getters are used to reduce the amount of reactive hydrogen in applications such as nuclear plants and transuranic waste. Here, the present study examines the performance of getter loaded silicone elastomers in reducing reactive hydrogen gas from the gas phase and their capability of being 3D printed using direct ink writing techniques. The samples are placed in closed vessels and exposed to hydrogen atmosphere at pressures of 580 torr and 750 mtorr and at a temperature of 25 °C. The hydrogen consumption is measured as a function of time and normalized to getter concentration in the polymer. The performancemore » of the getter-loaded silicone elastomer containing 1,4-bis[phenylethynyl]benzene (DEB) as the organic getter and Pd/C catalyst (ratio of 3:1 DEB to catalyst) decreases with increasing the resin's curing temperature. Chemical analysis suggests that DEB reacts with the silicone resin at high temperatures. In addition, it is demonstrated that the increased surface area of 3D printed composites results in improved getter performance.« less

Symmetrical solid oxide fuel cells with impregnated SrFe0.75Mo0.25O3-δ electrodes

NASA Astrophysics Data System (ADS)

Meng, Xie; Liu, Xuejiao; Han, Da; Wu, Hao; Li, Junliang; Zhan, Zhongliang

2014-04-01

Here we report nominally symmetrical solid oxide fuel cells that feature thin La0.9Sr0.1Ga0.8Mg0.2O3-δ (LSGM) electrolytes and impregnated SrFe0.75Mo0.25O3-δ (SFMO)-LSGM composite electrodes. Operation on hydrogen fuels and air oxidants can produce maximum power densities of 0.39 W cm-2 at 650 °C and 0.97 W cm-2 at 800 °C. Impedance measurements indicate that the anode and the cathode polarizations are 0.22 and 0.04 Ω cm2 at 800 °C, respectively. Hydrogen partial pressure and temperature dependence of impedance data in humidified hydrogen shows that hydrogen oxidation kinetics is largely determined by hydrogen adsorption on the SFMO catalysts at high temperatures and charge transfer reactions along the SFMO|LSGM interfaces at low temperatures. Carbon tolerance of the present fuel cells is also examined in iso-octane fuels balanced by nitrogen at 800 °C that yields stable maximum power densities of 0.39 W cm-2.
3D-Printable Silicone Materials with Hydrogen Getter Capability

DOE Office of Scientific and Technical Information (OSTI.GOV)

Ortiz-Acosta, Denisse; Moore, Tanya; Safarik, Douglas Joseph

Organic getters are used to reduce the amount of reactive hydrogen in applications such as nuclear plants and transuranic waste. Here, the present study examines the performance of getter loaded silicone elastomers in reducing reactive hydrogen gas from the gas phase and their capability of being 3D printed using direct ink writing techniques. The samples are placed in closed vessels and exposed to hydrogen atmosphere at pressures of 580 torr and 750 mtorr and at a temperature of 25 °C. The hydrogen consumption is measured as a function of time and normalized to getter concentration in the polymer. The performancemore » of the getter-loaded silicone elastomer containing 1,4-bis[phenylethynyl]benzene (DEB) as the organic getter and Pd/C catalyst (ratio of 3:1 DEB to catalyst) decreases with increasing the resin's curing temperature. Chemical analysis suggests that DEB reacts with the silicone resin at high temperatures. In addition, it is demonstrated that the increased surface area of 3D printed composites results in improved getter performance.« less
Theoretical studies of the transition state structures and free energy barriers for base-catalyzed hydrolysis of amides

PubMed Central

Xiong, Ying; Zhan, Chang-Guo

2010-01-01

The transition state structures and free energy barriers for the rate-determining step (i.e. the formation of a tetrahedral intermediate) of base-catalyzed hydrolysis of a series of amides in aqueous solution have been studied by performing first-principle electronic structure calculations using a hybrid supermolecule-polarizable continuum approach. The calculated results and a revisit of recently reported experimental proton inventory data reveal that the favorable transition state structure optimized for the tetrahedral intermediate formation of hydroxide ion-catalyzed hydrolysis of formamide may have three solvating water molecules remaining on the attacking hydroxide oxygen and two additional water molecules attached to the carbonyl oxygen of formamide. The calculated results have also demonstrated interesting substituent effects on the optimized transition state geometries, on the transition-state stabilization, and on the calculated free energy barriers for the base-catalyzed hydrolysis of amides. When some or all of the hydrogen atoms of formamide are replaced by methyl groups, the total number of water molecules hydrogen-bonding with the attacking hydroxide in the transition state decreases from three for formamide to two for N-methylacetamide, N,N-dimethylformamide (DMF), and N,N-dimethylacetamide (DMA). The larger substituents of the amide hinder the solvent water molecules approaching the attacking hydroxide oxygen in the transition state and, therefore, destabilize the transition state structure and increase the free energy barrier. By using the optimized most favorable transition state structures, the calculated free energy barriers, i.e. 21.6 (or 21.7), 22.7, 23.1, and 26.0 kcal/mol for formamide, N-methylacetamide, DMF, and DMA, respectively, are in good agreement with the available experimental free energy barriers, i.e. 21.2, 21.5, 22.6, and 24.1 kcal/mol for formamide, N-methylacetamide, DMF, and DMA, respectively. PMID:17107116
Hydrogen storage in Earth's mantle and core

NASA Technical Reports Server (NTRS)

Prewitt, Charles T.

1994-01-01

Two different approaches to explaining how hydrogen might be stored in the mantle are illustrated by a number of papers published over the past 25-30 years, but there has been little attempt to provide objective comparisons of the two. One approach invokes the presence in the mantle of dense hydrous magnesium silicates (DHMS) stable at elevated pressures and temperatures. The other involves nominally anhydrous minerals (NAM) that contain hydrogen as a minor constituent on the ppm level. Experimental studies on DHMS indicate these phases may be stable to pressures and temperatures as high at 16 GPa and 1200 C. This temperature is lower than that indicated by a mantle geotherm at 16 GPa, but may be reasonable for a subducting slab. It is possible that other DHMS could be stable to even higher pressures, but little is known about maximum temperature limits. For NAM, small amounts of hydrogen (up to several hundred ppm) have been detected in olivine, orthopyroxene, clinopyroxene, and garnet recovered from xenoliths in kimberlites, eclogites, and alkali basalts; it has been demonstrated that synthetic wadsleyite and perovskite can accommodate significant amounts of hydrogen. A number of problems are associated with each possibility. For NAM originating in the mantle, one would like to assume that the hydrogen measured in samples recovered on Earth's surface was incorporated when the phase-crystallized at high temperatures and pressures, but it could have been introduced during transport to the surface. Major problems for the DHMS proponents are that none of these phases have been found as minerals and little is yet known about their stabilities in systems containing other cations such as Fe, Al, and Ca.
Hydrogen production by the solar-powered hybrid sulfur process: Analysis of the integration of the CSP and chemical plants in selected scenarios

NASA Astrophysics Data System (ADS)

Liberatore, Raffaele; Lanchi, Michela; Turchetti, Luca

2016-05-01

The Hybrid Sulfur (HyS) is a water splitting process for hydrogen production powered with high temperature nuclear heat and electric power; among the numerous thermo-chemical and thermo-electro-chemical cycles proposed in the literature, such cycle is considered to have a particularly high potential also if powered by renewable energy. SOL2HY2 (Solar to Hydrogen Hybrid Cycles) is a 3 year research project, co-funded by the Fuel Cells and Hydrogen Joint Undertaking (FCH JU). A significant part of the project activities are devoted to the analysis and optimization of the integration of the solar power plant with the chemical, hydrogen production plant. This work reports a part of the results obtained in such research activity. The analysis presented in this work builds on previous process simulations used to determine the energy requirements of the hydrogen production plant in terms of electric power, medium (<550°C) and high (>550°C) temperature heat. For the supply of medium temperature (MT) heat, a parabolic trough CSP plant using molten salts as heat transfer and storage medium is considered. A central receiver CSP (Concentrated Solar Power) plant is considered to provide high temperature (HT) heat, which is only needed for sulfuric acid decomposition. Finally, electric power is provided by a power block included in the MT solar plant and/or drawn from the grid, depending on the scenario considered. In particular, the analysis presented here focuses on the medium temperature CSP plant, possibly combined with a power block. Different scenarios were analysed by considering plants with different combinations of geographical location and sizing criteria.
Evidence of molecular hydrogen trapped in two-dimensional layered titanium carbide-based MXene

DOE PAGES

Osti, Naresh C.; Naguib, Michael; Tyagi, Madhusudan; ...

2017-07-17

Two-dimensional transition metal carbides and nitrides (MXenes) are one of the largest and fastest growing families of materials. The presence of molecular hydrogen at ambient conditions in a MXene (Ti 3C 2T x, where T x represents a surface terminating species, including O, OH, and F) material is revealed here by inelastic and elastic neutron scatterings. The inelastic neutron-scattering spectrum measured at 5 K shows a peak at 14.6 meV, presenting a clear indication of the presence of parahydrogen in the MXene synthesized using 48% hydrofluoric acid and annealed at 110°C in vacuum prior to the measurement. An increase inmore » the measurement temperature gradually reduces the peak intensity and increases the peak width due to the mobility of the molecular hydrogen in confinement. The presence of molecular hydrogen is confirmed further from the observed elastic intensity drop in a fixed energy-window scan of elastic intensity measurements in the temperature range of 10–35 K. Using milder etching conditions, ion intercalation, or an increase in the annealing temperature all result in the absence of the trapped hydrogen molecules in MXene. Here, the results of this paper can guide the development of MXene materials with desired properties and improve our understanding of the behavior of MXenes in applications ranging from supercapacitors to hydrogen evolution reaction catalysis and hydrogen storage.« less
Liquid-phase hydrogenation of citral over Pt/SiO{sub 2} catalysts. 1. Temperature effects on activity and selectivity

DOE Office of Scientific and Technical Information (OSTI.GOV)

Singh, U.K.; Vannice, M.A.

2000-04-01

Liquid-phase hydrogenation of citral (3,7-dimethyl-2,6-octadienal) over Pt/SiO{sub 2} catalysts was studied in the temperature and pressure ranges 298--423 K and 7--21 atm, respectively. The reaction kinetics were shown to be free of artifacts arising from transport limitations and poisoning effects. The reaction rate in hexane at the solvent exhibited an activity minimum at 373 K. The initial turnover frequency for citral disappearance over 1.44% Pt/SiO{sub 2} catalyst at 20 atm H{sub 2} pressure decreased from 0.19 s{sup {minus}1} at 298 K to 0.02 s{sup {minus}1} at 373 K, but exhibited normal Arrhenius behavior between 373 and 423 K with anmore » activation energy of 7 kcal/mol. Reaction at 298 K produced substantial deactivation, with the rate decreasing by more than an order of magnitude during the first 4 h of reaction; however, reaction at temperatures greater than 373 K exhibited negligible deactivation and a constant rate up to citral conversions greater than 70%. These unusual temperature effects were modeled using Langmuir-Hinshelwood kinetics invoking dissociative adsorption of hydrogen, competitive adsorption between hydrogen and the organic compounds, and addition of the second hydrogen atom to each reactant as the rate-determining step. Decomposition of the unsaturated alcohol (either geraniol or nerol) was proposed to occur concurrently with the hydrogenation steps to yield adsorbed CO and carbonaceous species which cause the deactivation, but at higher temperatures these species could be removed from the Pt surface by desorption or rapid hydrogenation, respectively. The activity minimum observed in the present study is attributed to the relative rates of the alcohol decomposition reaction and CO desorption, with the decomposition reaction having an activation barrier lower than that for CO desorption.« less
Steam gasification of waste tyre: Influence of process temperature on yield and product composition

DOE Office of Scientific and Technical Information (OSTI.GOV)

Portofino, Sabrina, E-mail: sabrina.portofino@enea.it; Donatelli, Antonio; Iovane, Pierpaolo

Highlights: ► Steam gasification of waste tyre as matter and energy recovery treatment. ► Process temperature affects products yield and gas composition. ► High temperature promotes hydrogen production. ► Char exploitation as activated carbon or carbon source. - Abstract: An experimental survey of waste tyre gasification with steam as oxidizing agent has been conducted in a continuous bench scale reactor, with the aim of studying the influence of the process temperature on the yield and the composition of the products; the tests have been performed at three different temperatures, in the range of 850–1000 °C, holding all the other operationalmore » parameters (pressure, carrier gas flow, solid residence time). The experimental results show that the process seems promising in view of obtaining a good quality syngas, indicating that a higher temperature results in a higher syngas production (86 wt%) and a lower char yield, due to an enhancement of the solid–gas phase reactions with the temperature. Higher temperatures clearly result in higher hydrogen concentrations: the hydrogen content rapidly increases, attaining values higher than 65% v/v, while methane and ethylene gradually decrease over the range of the temperatures; carbon monoxide and dioxide instead, after an initial increase, show a nearly constant concentration at 1000 °C. Furthermore, in regards to the elemental composition of the synthesis gas, as the temperature increases, the carbon content continuously decreases, while the oxygen content increases; the hydrogen, being the main component of the gas fraction and having a small atomic weight, is responsible for the progressive reduction of the gas density at higher temperature.« less
CARS Temperature Measurements in Turbulent and Supersonic Facilities

NASA Technical Reports Server (NTRS)

Jarrett, O., Jr.; Antcliff, R. R.; Smith, M. W.; Cutler, A. D.; Diskin, G. S.; Northam, G. B.

1991-01-01

This paper documents the development of the National Aeronautics and Space Administration s (NASA) Langley Research Center ( LaRC) Coherent Antistokes Raman Spectroscopy (CARS) systems for measurements of temperature in a turbulent subsonic or supersonic reacting hydrogen-air environment. Spectra data provides temperature data when compared to a precalculated library of nitrogen CARS spectra. Library validity was confirmed by comparing CARS temperatures derived through the library with three different techniques for determination of the temperature in hydrogen-air combustion and an electrically heated furnace. The CARS system has been used to survey temperature profiles in the simulated flow of a supersonic combustion ramjet (scramjet) model. Measurement results will be discussed.
Experimental and theoretical study of shuttle lee-side heat transfer rates

NASA Technical Reports Server (NTRS)

Mruk, G. K.; Bertin, J.; Lamb, J. P.

1975-01-01

The experimental program which was conducted in the Calspan 96-inch hypersonic shock tunnel to investigate what effect the windward surface temperature had on the heat transfer to the leeward surface of the space shuttle orbiter is discussed. Heat-transfer distributions, surface-pressure distributions, and schlieren photographs were obtained for an 0.01-scale model of the 139 configuration space shuttle orbiter at angles-of-attack of 30 and 40 deg. Similar data were obtained for an 0.01 scale wingless model of the 139 configuration at angles-of-attack of 30 and 90 deg. Data were obtained for Mach numbers from Reynolds numbers, and surface temperatures and compared with theoretical results.
System for thermochemical hydrogen production

DOEpatents

Werner, R.W.; Galloway, T.R.; Krikorian, O.H.

1981-05-22

Method and apparatus are described for joule boosting a SO/sub 3/ decomposer using electrical instead of thermal energy to heat the reactants of the high temperature SO/sub 3/ decomposition step of a thermochemical hydrogen production process driven by a tandem mirror reactor. Joule boosting the decomposer to a sufficiently high temperature from a lower temperature heat source eliminates the need for expensive catalysts and reduces the temperature and consequent materials requirements for the reactor blanket. A particular decomposer design utilizes electrically heated silicon carbide rods, at a temperature of 1250/sup 0/K, to decompose a cross flow of SO/sub 3/ gas.
Behavior of implanted hydrogen in thermally stimulated blistering in silicon

NASA Astrophysics Data System (ADS)

Aleksandrov, P. A.; Baranova, E. K.; Baranova, I. V.; Budaragin, V. V.; Litvinov, V. L.

2003-11-01

The processes of accumulation of ion implanted hydrogen in blisters in silicon and its release during the thermal treatment from 350 to 1020degreesC have been studied by optical techniques. It was established that accumulation of gaseous hydrogen inside blisters takes place at temperatures lower than similar to450-500degreesC and is accompanied by the growth of blister thickness and deformation of their caps. At higher temperatures the gaseous hydrogen goes out of the cavities dissolving in silicon. Due to the internal pressure dropping the elastically deformed top layer partially relaxes and the blister thickness decreases. Etching of the surface layer reveals the agglomerations of small voids (<0.3 mm) located in the place of blisters approximately at their depth. Proceeding from the fact that the processes in blistering are similar to those in ion cut, the following conclusions with respect to the latter were drawn. The exfoliation processes themselves occur at temperatures lower than similar to500degreesC. The exfoliation efficiency particularly at the higher temperatures is essentially dependent on the heating rate.
Effect of the culture media optimization, pH and temperature on the biohydrogen production and the hydrogenase activities by Klebsiella pneumoniae ECU-15.

PubMed

Xiao, Yan; Zhang, Xu; Zhu, Minglong; Tan, Wensong

2013-06-01

The low yield of the biohydrogen production is the main constraint for its industrialization process. In order to improve its production, medium compositions of the hydrogen fermentation by Klebsiella pneumoniae ECU-15 were optimized through the response surface methodology (RSM). Experimental results showed that the optimum hydrogen production of 5363.8 ml/L was obtained when the concentration of glucose, the ammonium sulfate and the trace elements were 35.62 g/L, 2.78 g/L and 23.15 ml/L at temperature 37.0°C, pH 6.0. H2 evolving hydrogenase was greatly enhanced by the optimization of the medium compositions. The activity of H2 evolving hydrogenase increased with the temperature, and decreased with the pH, while the activity of the uptake hydrogenase increased with the temperature and the pH. So the biohydrogen production process of the K. pneumoniae ECU-15 was the comprehensive results of the evolution hydrogen process and the uptake hydrogen process. Copyright © 2013 Elsevier Ltd. All rights reserved.
Sorption Properties of Iron-Magnesium and Nickel-Magnesium Mg2FeH6 and Mg2NiH4 Hydrides

NASA Astrophysics Data System (ADS)

Matysina, Z. A.; Zaginaichenko, S. Yu.; Shchur, D. V.; Gabdullin, M. T.

2016-06-01

Based on molecular-kinetic representations, theory of hydrogen absorption-desorption processes in binary Mg-Fe and Mg-Ni alloys is developed. Free energies of hydrides of these alloys are calculated. Equations of their thermodynamically equilibrium state determining the P-T-c diagrams are derived. A temperature dependence of the desorbed hydrogen concentration is established. A maximal desorption temperature is estimated. The state diagrams determining the concentration dependence of the maximal desorption temperature are constructed. Isopleths and isotherms of hydrogen solubility in the alloys are calculated. The possibility of manifestation of the hysteresis effect in hydrogen solubility isotherms is revealed and the decrease of the width and length of a hysteresis loop with increasing temperature is demonstrated together with the influence of the magnesium hydrate MgH2 in Mg2FeH6 samples and running of chemical reactions on the behavior of the isotherms and the occurrence of bends and jumps in them. All established functional dependences of the sorption properties of the examined alloys are compared with experimental data available from the literature.
Anaerobic fermentation combined with low-temperature thermal pretreatment for phosphorus-accumulating granular sludge: Release of carbon source and phosphorus as well as hydrogen production potential.

PubMed

Zou, Jinte; Li, Yongmei

2016-10-01

Releases of organic compounds and phosphorus from phosphorus-accumulating granular sludge (PGS) and phosphorus-accumulating flocculent sludge (PFS) during low-temperature thermal pretreatment and anaerobic fermentation were investigated. Meanwhile, biogas production potential and microbial community structures were explored. The results indicate that much more soluble chemical oxygen demand (SCOD) and phosphorus were released from PGS than from PFS via low-temperature thermal pretreatment because of the higher extracellular polymeric substances (EPS) content in PGS and higher ratio of phosphorus reserved in EPS. Furthermore, PGS contains more anaerobes and dead cells, resulting in much higher SCOD and volatile fatty acids release from PGS than those from PFS during fermentation. PGS fermentation facilitated the n-butyric acid production, and PGS exhibited the hydrogen production potential during fermentation due to the presence of hydrogen-producing bacteria. Therefore, anaerobic fermentation combined with low-temperature thermal pretreatment can facilitate the recovery of carbon and phosphorus as well as producing hydrogen from PGS. Copyright © 2016 Elsevier Ltd. All rights reserved.
Correlation of microstructure and thermo-mechanical properties of a novel hydrogen transport membrane

NASA Astrophysics Data System (ADS)

Zhang, Yongjun

A key part of the FutureGen concept is to support the production of hydrogen to fuel a "hydrogen economy," with the use of clean burning hydrogen in power-producing fuel cells, as well as for use as a transportation fuel. One of the key technical barriers to FutureGen deployment is reliable and efficient hydrogen separation technology. Most Hydrogen Transport Membrane (HTM) research currently focuses on separation technology and hydrogen flux characterization. No significant work has been performed on thermo-mechanical properties of HTMs. The objective of the thesis is to understand the structure-property correlation of HTM and to characterize (1) thermo mechanical properties under different reducing environments and thermal cycles (thermal shock), and (2) evaluate the stability of the novel HTM material. A novel HTM cermet bulk sample was characterized for its physical and mechanical properties at both room temperature and at elevated temperature up to 1000°C. Micro-structural properties and residual stresses were evaluated in order to understand the changing mechanism of the microstructure and its effects on the mechanical properties of materials. A correlation of the microstructural and thermo mechanical properties of the HTM system was established for both HTM and the substrate material. Mechanical properties of both selected structural ceramics and the novel HTM cermet bulk sample are affected mainly by porosity and microstructural features, such as grain size and pore size-distribution. The Young's Modulus (E-value) is positively correlated to the flexural strength for materials with similar crystallographic structure. However, for different crystallographic materials, physical properties are independent of mechanical properties. Microstructural properties, particularly, grain size and crystallographic structure, and thermodynamic properties are the main factors affecting the mechanical properties at both room and high temperatures. The HTM cermet behaves more like an elastic material at room temperature and as a ductile material at temperature above 850°C. The oxidation and the plasticity of Pd phase mainly affected the mechanical properties of HTM cermet at high temperature, also as a result of thermal cycling. Residual stress induced in the HTM by thermo cycles also plays a very critical role in defining the thermo-mechanical properties.
Hydrogen technology survey: Thermophysical properties

NASA Technical Reports Server (NTRS)

Mccarty, R. D.

1975-01-01

The thermodynamic functions, transport properties, and physical properties of both liquid and gaseous hydrogen are presented. The low temperature regime is emphasized. The tabulation of the properties of normal hydrogen in both Si and engineering units is given along with the tabulation of parahydrogen.
Low-cost, flexible battery packaging materials

NASA Astrophysics Data System (ADS)

Jansen, Andrew N.; Amine, Khalil; Newman, Aron E.; Vissers, Donald R.; Henriksen, Gary L.

2002-03-01

Considerable cost savings can be realized if the metal container used for lithium-based batteries is replaced with a flexible multi-laminate containment commonly used in the food packaging industry. This laminate structure must have air, moisture, and electrolyte barrier capabilities, be resistant to hydrogen-fluoride attack, and be heat-sealable. After extensive screening of commercial films, the polyethylene and polypropylene classes of polymers were found to have an adequate combination of mechanical, permeation, and seal-strength properties. The search for a better film and adhesive is ongoing.
Effect of hydrogen bonding on the vibrational dephasing time in glycerol

NASA Technical Reports Server (NTRS)

Dorsinville, R.; Franklin, W. M.; Ockman, N.; Alfano, R. R.

1982-01-01

The vibrational dephasing of the methyl CH2 symmetric stretch mode in glycerol was directly measured over an extended temperature range using picosecond coherent Raman pump and probe spectroscopy. The dephasing time was found to increase dramatically as the temperature of the supercooled liquid was lowered. This observation is attributed to the increased hydrogen bonding with decreasing temperature which hinders the dephasing of the CH2 vibration by reducing molecular motions.
Zirconium vanadium chromium alloy

DOEpatents

Mendelsohn, M.H.; Gruen, D.M.

1980-10-14

A ternary intermetallic compound having the formula Zr(V/sub 1-x/Cr/sub x/)/sub 2/ where x is in the range of 0.01 to 0.90 is capable of reversibly sorbing hydrogen at temperatures ranging from room temperature to 200/sup 0/C, at pressures down to 10/sup -6/ torr. The compound is suitable for use as a hydrogen getter in low pressure, high temperature applications such as magnetic confinement fusion devices.

Solar hydrogen generator

NASA Technical Reports Server (NTRS)

Sebacher, D. I.; Sabol, A. P. (Inventor)

1977-01-01

An apparatus, using solar energy to manufacture hydrogen by dissociating water molecules into hydrogen and oxygen molecules is described. Solar energy is concentrated on a globe containing water thereby heating the water to its dissociation temperature. The globe is pervious to hydrogen molecules permitting them to pass through the globe while being essentially impervious to oxygen molecules. The hydrogen molecules are collected after passing through the globe and the oxygen molecules are removed from the globe.
Hexagonal boron nitride nanoparticles decorated halloysite clay nanotubes as a potential hydrogen storage medium

DOE Office of Scientific and Technical Information (OSTI.GOV)

Muthu, R. Naresh, E-mail: rnaresh7708@gmail.com; Rajashabala, S.; Kannan, R.

2016-05-23

The light weight and compact hydrogen storage materials is still prerequisite for the carbon free hydrogen fuel cell technology. In this work, the hydrogen storage performance of acid treated halloysite clay nanotubes (A-HNTs) and hexagonal boron nitride (h-BN) nanoparticles decorated acid treated halloysite nanoclay composite (A-HNT-h-BN) are demonstrated, where facile ultrasonic technique is adopted for the synthesis of A-HNT-h-BN nanoclay composite. Hydrogen storage studies were carried out using Sieverts-like hydrogenation setup. The A-HNTs and A-HNT-h-BN nanoclay composite were analyzed by XRD, FTIR, HRTEM, EDX, CHNS-elemental analysis and TGA. The A-HNT-h-BN nanoclay composite shows superior storage capacity of 2.19 wt% atmore » 50 °C compared to the A-HNTs (0.58 wt%). A 100% desorption of stored hydrogen is noted in the temperature range of 138–175 °C. The average binding energy of hydrogen was found to be 0.34 eV for the prepared A-HNT-h-BN nanoclay composite. The excellent storage capability of A-HNT-h-BN nanoclay composite towards hydrogen at ambient temperature may find bright perspective in hydrogen fuel cell technology in near future.« less
Advancements in Dual-Pump Broadband CARS for Supersonic Combustion Measurements

NASA Technical Reports Server (NTRS)

Tedder, Sarah Augusta Umberger

2010-01-01

Space- and time-resolved measurements of temperature and species mole fractions of nitrogen, oxygen, and hydrogen were obtained with a dual-pump coherent anti-Stokes Raman spectroscopy (CARS) system in hydrogen-fueled supersonic combustion free jet flows. These measurements were taken to provide time-resolved fluid properties of turbulent supersonic combustion for use in the creation and verification of computational fluid dynamic (CFD) models. CFD models of turbulent supersonic combustion flow currently facilitate the design of air-breathing supersonic combustion ramjet (scramjet) engines. Measurements were made in supersonic axi-symmetric free jets of two scales. First, the measurement system was tested in a laboratory environment using a laboratory-scale burner (approx.10 mm at nozzle exit). The flow structures of the laboratory-burner were too small to be resolved with the CARS measurements volume, but the composition and temperature of the jet allowed the performance of the system to be evaluated. Subsequently, the system was tested in a burner that was approximately 6 times larger, whose length scales are better resolved by the CARS measurement volume. During both these measurements, weaknesses of the CARS system, such as sensitivity to vibrations and beam steering and inability to measure temperature or species concentrations in hydrogen fuel injection regions were indentified. Solutions were then implemented in improved CARS systems. One of these improved systems is a dual-pump broadband CARS technique called, Width Increased Dual-pump Enhanced CARS (WIDECARS). The two lowest rotational energy levels of hydrogen detectable by WIDECARS are H2 S(3) and H2 S(4). The detection of these lines gives the system the capability to measure temperature and species concentrations in regions of the flow containing pure hydrogen fuel at room temperature. WIDECARS is also designed for measurements of all the major species (except water) in supersonic combustion flows fueled with hydrogen and hydrogen/ethylene mixtures (N2, O2, H2, C2H4, CO, and CO2). This instrument can characterize supersonic combustion fueled with surrogate fuel mixtures of hydrogen and ethylene. This information can lead to a better understanding of the chemistry and performance of supersonic combustion fueled with cracked jet propulsion (JP)-type fuel.
Evaluation of hydrogen embrittlement and temper embrittlement by key curve method in instrumented Charpy test

NASA Astrophysics Data System (ADS)

Ohtsuka, N.; Shindo, Y.; Makita, A.

2010-06-01

Instrumented Charpy test was conducted on small sized specimen of 21/4Cr-1Mo steel. In the test the single specimen key curve method was applied to determine the value of fracture toughness for the initiation of crack extension with hydrogen free, KIC, and for hydrogen embrittlement cracking, KIH. Also the tearing modulus as a parameter for resistance to crack extension was determined. The role of these parameters was discussed at an upper shelf temperature and at a transition temperature. Then the key curve method combined with instrumented Charpy test was proven to be used to evaluate not only temper embrittlement but also hydrogen embrittlement.
Paracyclophane functionalized with Sc and Li for hydrogen storage

NASA Astrophysics Data System (ADS)

Sathe, Rohit Y.; Dhilip Kumar, T. J.

2018-01-01

Li and Sc metals functionalized on the delocalized π -electrons of benzene rings in [2,2]paracyclophane structure are studied for hydrogen storage efficiency by using the M06 DFT functional with 6-311G(d,p) basis set. It is found that Sc and Li functionalized [2,2]paracyclophane complexes can hold up to 10 H2 molecules and 8 H2 molecules by Kubas-Niu-Jena interaction and charge polarization mechanism with hydrogen weight percentage of 11.4 and 13.5, respectively. Molecular dynamics simulation at various temperatures showed appreciable thermal stability while the chemical potential calculation at room temperature reveals that Sc functionalized [2,2]paracyclophane system will be a promising hydrogen storage material.
Extended defects and hydrogen interactions in ion implanted silicon

NASA Astrophysics Data System (ADS)

Rangan, Sanjay

The structural and electrical properties of extended defects generated because of ion implantation and the interaction of hydrogen with these defects have been studied in this work. Two distinct themes have been studied, the first where defects are a detrimental and the second where they are useful. In the first scenario, transient enhanced diffusion of boron has been studied and correlated with defect evolution studies due to silicon and argon ion implants. Spreading resistance profiles (SRP) correlated with deep level transient spectroscopy (DLTS) measurements, reveal that a low anneal temperatures (<650°C) defect dissolution and defect injection dominates, resulting in increased junction depths. At higher anneal temperatures, however, repair dominates over defect injection resulting in shallower junctions. Hydrogenation experiments shows that hydrogen enhances dopant activation and reduces TED at low anneal temperatures (<550°C). At anneal temperatures >550°C, the effect of hydrogen is lost, due to its out-diffusion. Moreover, due to catastrophic out-diffusion of hydrogen, additional damage is created resulting in deeper junctions in hydrogenated samples, compared to the non-hydrogenated ones. Comparing defect evolution due to Si and Ar ion implants at different anneal temperatures, while the type of defects is the same in the two cases, their (defect) dissolution occurs at lower anneal temperatures (˜850°C) for Si implants. Dissolution for Ar implants seems to occur at higher anneal temperatures. The difference has been attributed to the increased number of vacancies created by Ar to that of silicon implant. In second aspect, nano-cavity formation due to vacancy agglomeration has been studied by helium ion implantation and furnace anneal, where the effect of He dose, implant energy and anneal time have been processing parameters that have been varied. Cavities are formed only when the localized concentration of He is greater than 3 x 1020 cm-3. While at high implant doses, a continuous cavity layer is formed, at low implant doses a discontinuous layer is observed. The formation of cavities at low doses has been observed for the first time. Variation of anneal times reveal that cavities are initially facetted (for short anneal times) and tend to become spherical when annealed for along time (300min). Also presented is the recipe for formation of multiple cavity layers and the electrical and optical properties of these cavities. Electrically, these cavities are metastable, with two strong minority carrier peaks formed by multiple defect levels. Photoluminescence measurements reveal a strong 0.8eV photon peak.
Effect of Hydrogen in Zinc Oxide Thin-Film Transistor Grown by Metal Organic Chemical Vapor Deposition

NASA Astrophysics Data System (ADS)

Jo, Jungyol; Seo, Ogweon; Jeong, Euihyuk; Seo, Hyunseok; Lee, Byeongon; Choi, Yearn-Ik

2007-04-01

We studied the transport characteristics of ZnO grown by metal organic chemical vapor deposition (MOCVD) at temperatures between 200 and 500 °C. The crystal quality, measured by X-ray diffraction, improved as the growth temperature increased. However, the mobility measured in the thin-film transistor (TFT) decreased in films grown at higher temperatures. In our experiments, a ZnO TFT grown at 250 °C showed good electrical characteristics, with a 13 cm2 V-1 s-1 mobility and a 103 on/off ratio. We conclude that hydrogen incorporated during MOCVD growth plays an important role in determining the transistor characteristics. This was supported by results of secondary ion mass spectroscopy (SIMS), where a higher hydrogen concentration was observed in films grown at lower temperatures.
Comment on "A hydrogen-rich early Earth atmosphere".

PubMed

Catling, David C

2006-01-06

Tian et al. (Reports, 13 May 2005, p. 1014) proposed a hydrogen-rich early atmosphere with slow hydrogen escape from a cold thermosphere. However, their model neglects the ultraviolet absorption of all gases other than H2. The model also neglects Earth's magnetic field, which affects the temperature and density of ions and promotes nonthermal escape of neutral hydrogen.
Metal-Borohydride-Modified Zr(BH4 )4 ⋅8 NH3 : Low-Temperature Dehydrogenation Yielding Highly Pure Hydrogen.

PubMed

Huang, Jianmei; Ouyang, Liuzhang; Gu, Qinfen; Yu, Xuebin; Zhu, Min

2015-10-12

Due to its high hydrogen density (14.8 wt %) and low dehydrogenation peak temperature (130 °C), Zr(BH4 )4 ⋅8 NH3 is considered to be one of the most promising hydrogen-storage materials. To further decrease its dehydrogenation temperature and suppress its ammonia release, a strategy of introducing LiBH4 and Mg(BH4 )2 was applied to this system. Zr(BH4 )4 ⋅8 NH3 -4 LiBH4 and Zr(BH4 )4 ⋅8 NH3 -2 Mg(BH4 )2 composites showed main dehydrogenation peaks centered at 81 and 106 °C as well as high hydrogen purities of 99.3 and 99.8 mol % H2 , respectively. Isothermal measurements showed that 6.6 wt % (within 60 min) and 5.5 wt % (within 360 min) of hydrogen were released at 100 °C from Zr(BH4 )4 ⋅8 NH3 -4 LiBH4 and Zr(BH4 )4 ⋅8 NH3 -2 Mg(BH4 )2 , respectively. The lower dehydrogenation temperatures and improved hydrogen purities could be attributed to the formation of the diammoniate of diborane for Zr(BH4 )4 ⋅8 NH3 -4 LiBH4 , and the partial transfer of NH3 groups from Zr(BH4 )4 ⋅8 NH3 to Mg(BH4 )2 for Zr(BH4 )4 ⋅8 NH3 -2 Mg(BH4 )2 , which result in balanced numbers of BH4 and NH3 groups and a more active H(δ+) ⋅⋅⋅(-δ) H interaction. These advanced dehydrogenation properties make these two composites promising candidates as hydrogen-storage materials. © 2015 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.
Method for low temperature catalytic production of hydrogen

DOEpatents

Mahajan, Devinder

2003-07-22

The invention provides a process for the catalytic production of a hydrogen feed by exposing a hydrogen feed to a catalyst which promotes a base-catalyzed water-gas-shift reaction in a liquid phase. The hydrogen feed can be provided by any process known in the art of making hydrogen gas. It is preferably provided by a process that can produce a hydrogen feed for use in proton exchange membrane fuel cells. The step of exposing the hydrogen feed takes place preferably from about 80.degree. C. to about 150.degree. C.
Tandem ring-closing metathesis/transfer hydrogenation: practical chemoselective hydrogenation of alkenes.

PubMed

Connolly, Timothy; Wang, Zhongyu; Walker, Michael A; McDonald, Ivar M; Peese, Kevin M

2014-09-05

An operationally simple chemoselective transfer hydrogenation of alkenes using ruthenium metathesis catalysts is presented. Of great practicality, the transfer hydrogenation reagents can be added directly to a metathesis reaction and effect hydrogenation of the product alkene in a single pot at ambient temperature without the need to seal the vessel to prevent hydrogen gas escape. The reduction is applicable to a range of alkenes and can be performed in the presence of aryl halides and benzyl groups, a notable weakness of Pd-catalyzed hydrogenations. Scope and mechanistic considerations are presented.
Rhenium-Oxygen Interactions at High Temperatures

NASA Technical Reports Server (NTRS)

Jacobson, Nathan S.; Myers, Dwight L.; Zhu, Dongming; Humphrey, Donald

2000-01-01

The reaction of pure rhenium metal with dilute oxygen/argon mixtures was studied from 600 to 1400 C. Temperature, oxygen pressure, and flow rates were systematically varied to determine the rate-controlling steps. At lower temperatures the oxygen/rhenium chemical reaction is rate limiting; at higher temperatures gas-phase diffusion of oxygen through the static boundary layer is rate limiting. At all temperatures post-reaction microstructures indicate preferential attack along certain crystallographic planes and defects.
Methods to Stabilize and Destabilize Ammonium Borohydride

DOE Office of Scientific and Technical Information (OSTI.GOV)

Nielsen, Thomas K.; Karkamkar, Abhijeet J.; Bowden, Mark E.

2013-01-21

Ammonium borohydride, NH4BH4, has a high hydrogen content of ρm = 24.5 wt% H2 and releases 18 wt% H2 below T = 160 °C. However, the half-life of bulk NH4BH4 at ambient temperatures, ~6 h, is insufficient for practical applications. The decomposition of NH4BH4 (ABH2) was studied at variable hydrogen and argon back pressures to investigate possible pressure mediated stabilization effects. The hydrogen release rate from solid ABH2 at ambient temperatures is reduced by ~16 % upon increasing the hydrogen back pressure from 5 to 54 bar. Similar results were obtained using argon pressure and the observed stabilization may bemore » explained by a positive volume of activation in the transition state leading to hydrogen release. Nanoconfinement in mesoporous silica, MCM-41, was investigated as alternative means to stabilize NH4BH4. However, other factors appear to significantly destabilize NH4BH4 and it rapidly decomposes at ambient temperatures into [(NH3)2BH2][BH4] (DADB) in accordance with the bulk reaction scheme. The hydrogen desorption kinetics from nanoconfined [(NH3)2BH2][BH4] is moderately enhanced as evidenced by a reduction in the DSC decomposition peak temperature of ΔT = -13 °C as compared to the bulk material. Finally, we note a surprising result, storage of DADB at temperature < -30 °C transformed, reversibly, the [(NH3)2BH2][BH4] into a new low temperature polymorph as revealed by both XRD and solid state MAS 11B MAS NMR. TA & AK are thankful for support from the US Department of Energy, Office of Basic Energy Sciences, Division of Chemical Sciences, Geosciences & Biosciences. A portion of the research was performed using EMSL, a national scientific user facility sponsored by the Department of Energy's Office of Biological and Environmental Research and located at Pacific Northwest National Laboratory (PNNL). PNNL is operated by Battelle.« less
Studies of the use of heat from high temperature nuclear sources for hydrogen production processes

NASA Technical Reports Server (NTRS)

Farbman, G. H.

1976-01-01

Future uses of hydrogen and hydrogen production processes that can meet the demand for hydrogen in the coming decades were considered. To do this, a projection was made of the market for hydrogen through the year 2000. Four hydrogen production processes were selected, from among water electrolysis, fossil based and thermochemical water decomposition systems, and evaluated, using a consistent set of ground rules, in terms of relative performance, economics, resource requirements, and technology status.
Hydrogen gas sensor and method of manufacture

DOEpatents

McKee, John M.

1991-01-01

A sensor for measuring the pressure of hydrogen gas in a nuclear reactor, and method of manufacturing the same. The sensor comprises an elongated tube of hydrogen permeable material which is connected to a pressure transducer through a feedthrough tube which passes through a wall at the boundary of the region in which hydrogen is present. The tube is pressurized and flushed with hydrogen gas at an elevated temperature during the manufacture of the sensor in order to remove all gasses other than hydrogen from the device.
Method of production of pure hydrogen near room temperature from aluminum-based hydride materials

DOEpatents

Pecharsky, Vitalij K.; Balema, Viktor P.

2004-08-10

The present invention provides a cost-effective method of producing pure hydrogen gas from hydride-based solid materials. The hydride-based solid material is mechanically processed in the presence of a catalyst to obtain pure gaseous hydrogen. Unlike previous methods, hydrogen may be obtained from the solid material without heating, and without the addition of a solvent during processing. The described method of hydrogen production is useful for energy conversion and production technologies that consume pure gaseous hydrogen as a fuel.
A ’Hydrogen Partitioning’ Model for Hydrogen Assisted Crack Growth.

DTIC Science & Technology

1984-09-01

the change in Stage II crack growth rate from Region A to Region C in the 18NI maraging steels . It cannot, however, explain the sudden drop off in...Neither partitioning of hydrogen nor adsorption equilibrium can account for the observed "high" temperature response of l8Ni maraging steel in hydrogen...ment and Stress Corrosion Cracking, American Society for Metals, Metals Park, OH, 1984, p. 103 (in press). 11. R. P. Wei: in Hydrogen Effects in
Palladium-Catalyzed Allylic C-H Bond Functionalization of Olefins

NASA Astrophysics Data System (ADS)

Liu, Guosheng; Wu, Yichen

Transition metal-mediated carbon-hydrogen bond cleavage and functionalization is a mechanistically interesting and synthetically attractive process. One of the important cases is the removal of a allylic hydrogen from an olefin by a PdII salt to yield a π-allylpalladium complex, followed by nucleophilic attack to efficient produce allylic derivatives. In contrast to the well-known allylic acetoxylation of cyclohexene, the reaction of open-chain olefins is fairly poor until recent several years. Some palladium catalytic systems have been reported to achieve allylic C-H functionalization, including acetoxylation, amination and alkylation of terminal alkenes. In the most of cases, ligand is crucial to the success of the transformation. This review surveys the recent development of palladium-catalyzed allylic C-H functionalziation of alkenes. These results promise a significant increase in the scope of olefin transformation.
A statistical analysis of elevated temperature gravimetric cyclic oxidation data of 36 Ni- and Co-base superalloys based on an oxidation attack parameter

NASA Technical Reports Server (NTRS)

Barrett, Charles A.

1992-01-01

A large body of high temperature cyclic oxidation data generated from tests at NASA Lewis Research Center involving gravimetric/time values for 36 Ni- and Co-base superalloys was reduced to a single attack parameter, K(sub a), for each run. This K(sub a) value was used to rank the cyclic oxidation resistance of each alloy at 1000, 1100, and 1150 C. These K(sub a) values were also used to derive an estimating equation using multiple linear regression involving log(sub 10)K(sub a) as a function of alloy chemistry and test temperature. This estimating equation has a high degree of fit and could be used to predict cyclic oxidation behavior for similar alloys and to design an optimum high strength Ni-base superalloy with maximum high temperature cyclic oxidation resistance. The critical alloy elements found to be beneficial were Al, Cr, and Ta.
Room-temperature ferromagnetism in hydrogenated ZnO nanoparticles

NASA Astrophysics Data System (ADS)

Xue, Xudong; Liu, Liangliang; Wang, Zhu; Wu, Yichu

2014-01-01

The effect of hydrogen doping on the magnetic properties of ZnO nanoparticles was investigated. Hydrogen was incorporated by annealing under 5% H2 in Ar ambient at 700 °C. Room-temperature ferromagnetism was induced in hydrogenated ZnO nanoparticles, and the observed ferromagnetism could be switched between "on" and "off" states through hydrogen annealing and oxygen annealing process, respectively. It was found that Zn vacancy and OH bonding complex (VZn + OH) was crucial to the observed ferromagnetism by using the X-ray photoelectron spectroscopy and positron annihilation spectroscopy analysis. Based on first-principles calculations, VZn + OH was favorable to be presented due to the low formation energy. Meanwhile, this configuration could lead to a magnetic moment of 0.57 μB. The Raman and photoluminescence measurements excluded the possibility of oxygen vacancy as the origin of the ferromagnetism.

Some links on this page may take you to non-federal websites. Their policies may differ from this site.