High temperature oxidation behavior of austenitic stainless steel AISI 304 in steam of nanofluids contain nanoparticle ZrO2

DOE Office of Scientific and Technical Information (OSTI.GOV)

Prajitno, Djoko Hadi, E-mail: djokohp@batan.go.id; Syarif, Dani Gustaman, E-mail: djokohp@batan.go.id

2014-03-24

The objective of this study is to evaluate high temperature oxidation behavior of austenitic stainless steel SS 304 in steam of nanofluids contain nanoparticle ZrO{sub 2}. The oxidation was performed at high temperatures ranging from 600 to 800°C. The oxidation time was 60 minutes. After oxidation the surface of the samples was analyzed by different methods including, optical microscope, scanning electron microscope (SEM) and X-ray diffraction (XRD). X-ray diffraction examination show that the oxide scale formed during oxidation of stainless steel AISI 304 alloys is dominated by iron oxide, Fe{sub 2}O{sub 3}. Minor element such as Cr{sub 2}O{sub 3} ismore » also appeared in the diffraction pattern. Characterization by optical microscope showed that cross section microstructure of stainless steel changed after oxidized with the oxide scale on the surface stainless steels. SEM and x-ray diffraction examination show that the oxide of ZrO{sub 2} appeared on the surface of stainless steel. Kinetic rate of oxidation of austenite stainless steel AISI 304 showed that increasing oxidation temperature and time will increase oxidation rate.« less

Mechanistic insights into the oxidation behavior of Ni alloys in high-temperature CO 2

DOE PAGES

Oleksak, Richard P.; Baltrus, John P.; Nakano, Jinichiro; ...

2017-06-01

We present results of a Ni superalloy oxidized for short times in high purity CO 2 and similarly in Ar containing ≤ 1 ppb O 2. A detailed analysis of the oxidized surfaces reveals striking similarities for the two exposure environments, suggesting O 2 impurities control the oxidation process in high-temperature CO 2. Selective oxidation results in Cr-rich oxide layers grown by 2 outward diffusion, while Cr vacancies left in the metal contribute to significant void formation at the oxide/metal interface. Unlike for most of the alloy surface, the oxidation behavior of secondary phase metal carbides is considerably different inmore » the two environments.« less

Long Term Degradation of Resin for High Temperature Composites

NASA Technical Reports Server (NTRS)

Patekar, Kaustubh A.

2000-01-01

The durability of polymer matrix composites exposed to harsh environments is a major concern. Surface degradation and damage are observed in polyimide composites used in air at 125 to 300 C. It is believed that diffusion of oxygen into the material and oxidative chemical reactions in the matrix are responsible. Previous work has characterized and modeled diffusion behavior, and thermogravimetric analyses (TGAs) have been carried out in nitrogen, air, and oxygen to provide quantitative information on thermal and oxidative reactions. However, the model developed using these data was not able to capture behavior seen in isothermal tests, especially those of long duration. A test program that focuses on lower temperatures and makes use of isothermal tests was undertaken to achieve a better understanding of the degradation reactions under use conditions. A new low-cost technique was developed to collect chemical degradation data for isothermal tests lasting over 200 hr in the temperature range 125 to 300 C. Results indicate complex behavior not captured by the previous TGA tests, including the presence of weight-adding reactions. Weight gain reactions dominated in the 125 to 225 C temperature range, while weight loss reactions dominated beyond 225 C. The data obtained from isothermal tests was used to develop a new model of the material behavior. This model was able to fully capture the behavior seen in the tests up to 275 C. Correlation of the current model with both isothermal data at 300 C and high rate TGA test data is mediocre. At 300 C and above, the reaction mechanisms appear to change. Attempts (which failed) to measure non-oxidative degradation indicate that oxidative reactions dominate the degradation at low temperatures. Based on this work, long term isothermal testing in an oxidative atmosphere is recommended for studying the degradation behavior of this class of materials.

Oxidation behavior of U-Si compounds in air from 25 to 1000 C

NASA Astrophysics Data System (ADS)

Sooby Wood, E.; White, J. T.; Nelson, A. T.

2017-02-01

The air oxidation behavior of U3Si2, USi, and U3Si5 is studied from room temperature to 1000 C. The onsets of breakaway oxidation for each compound are identified during synthetic air ramps to 1000 C using thermogravimetric analysis. Isothermal air oxidation tests are performed below and above the breakaway oxidation onset to discern the oxidation kinetic behavior of these candidate accident tolerant fuel forms. Uranium metal is tested in the same manner to provide a reference for the oxidation behavior. Thermogravimetric, x-ray diffraction, and scanning electron microscopy analysis are presented here along with a discussion of the oxidation behavior of these materials and the impact of the lack of oxidation resistance to their deployment as accident tolerant nuclear fuels.

Oxidation Behavior of Titanium Carbonitride Coating Deposited by Atmospheric Plasma Spray Synthesis

NASA Astrophysics Data System (ADS)

Zhu, Lin; He, Jining; Yan, Dianran; Liao, Hanlin; Zhang, Nannan

2017-10-01

As a high-hardness and anti-frictional material, titanium carbonitride (TiCN) thick coatings or thin films are increasingly being used in many industrial fields. In the present study, TiCN coatings were obtained by atmospheric plasma spray synthesis or reactive plasma spray. In order to promote the reaction between the Ti particles and reactive gases, a home-made gas tunnel was mounted on a conventional plasma gun to perform the spray process. The oxidation behavior of the TiCN coatings under different temperatures in static air was carefully investigated. As a result, when the temperature was over 700 °C, the coatings suffered from serious oxidation, and finally they were entirely oxidized to the TiO2 phase at 1100 °C. The principal oxidation mechanism was clarified, indicating that the oxygen can permeate into the defects and react with TiCN at high temperatures. In addition, concerning the use of a TiCN coating in high-temperature conditions, the microhardness of the oxidized coatings at different treatment temperatures was also evaluated.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Zhou, Xiangwen; Contescu, Cristian I.; Zhao, Xi

Mmore » atrix graphite (G) with incompletely graphitized binder used in high-temperature gas-cooled reactors (HTGRs) is commonly suspected to exhibit lower oxidation resistance in air. In order to reveal the oxidation performance, the oxidation behavior of newly developed A3-3 G at the temperature range from 500 to 950°C in air was studied and the effect of oxidation on the compressive strength of oxidized G specimens was characterized. Results show that temperature has a significant influence on the oxidation behavior of G. The transition temperature between Regimes I and II is ~700°C and the activation energy ( E a ) in Regime I is around 185 kJ/mol, a little lower than that of nuclear graphite, which indicates G is more vulnerable to oxidation. Oxidation at 550°C causes more damage to compressive strength of G than oxidation at 900°C. Comparing with the strength of pristine G specimens, the rate of compressive strength loss is 77.3% after oxidation at 550°C and only 12.5% for oxidation at 900°C. icrostructure images of SE and porosity measurement by ercury Porosimetry indicate that the significant compressive strength loss of G oxidized at 550°C may be attributed to both the uniform pore formation throughout the bulk and the preferential oxidation of the binder.« less

Evaluation of hydrogen radical treatment for indium surface oxide removal and analysis of re-oxidation behavior

NASA Astrophysics Data System (ADS)

Furuyama, Kohta; Yamanaka, Kazuyuki; Higurashi, Eiji; Suga, Tadatomo

2018-02-01

Indium is a commonly used metal for sealing, bonding, and soldering due to its good malleability and ductility even at cryogenic temperatures. The effects of hydrogen radical treatment on indium surface oxide removal were evaluated by the spreading ratio test of indium balls (diameter, 300 µm purity, 99.99%). It was found that hydrogen radical treatment longer than 20 s at temperatures higher than 170 °C results in successful surface oxide removal. X-ray photoelectron spectroscopy analysis was carried out to study the re-oxidation behavior after treatment, and it was found that hydrogen radical treatment slows down the re-oxidation of indium compared with surface oxide removal realized by physical bombardment with an argon fast atom beam.

Oxidation behavior of TD-NiCr in a dynamic high temperature environment

NASA Technical Reports Server (NTRS)

Tenney, D. R.; Young, C. T.; Herring, H. W.

1974-01-01

The oxidation behavior of TD-NiCr has been studied in static and high-speed flowing air environments at 1100 and 1200 C. It has been found that the stable oxide morphologies formed on the specimens exposed to the static and dynamic environments were markedly different. The faceted crystal morphology characteristic of static oxidation was found to be unstable under high-temperature, high-speed flow conditions and was quickly replaced by a porous NiO 'mushroom' type structure. Also, it was found that the rate of formation of CrO3 from Cr2O3 was greatly enhanced by high gas velocity conditions. The stability of Cr2-O3 was found to be greatly improved by the presence of an outer NiO layer, even though the NiO layer was very porous. An oxidation model is proposed to explain the observed microstructures and overall oxidation behavior of TD-NiCr alloys.

Silicon Carbide Nanotube Oxidation at High Temperatures

NASA Technical Reports Server (NTRS)

Ahlborg, Nadia; Zhu, Dongming

2012-01-01

Silicon Carbide Nanotubes (SiCNTs) have high mechanical strength and also have many potential functional applications. In this study, SiCNTs were investigated for use in strengthening high temperature silicate and oxide materials for high performance ceramic nanocomposites and environmental barrier coating bond coats. The high · temperature oxidation behavior of the nanotubes was of particular interest. The SiCNTs were synthesized by a direct reactive conversion process of multiwall carbon nanotubes and silicon at high temperature. Thermogravimetric analysis (TGA) was used to study the oxidation kinetics of SiCNTs at temperatures ranging from 800degC to1300degC. The specific oxidation mechanisms were also investigated.

Oxidation behavior of U-Si compounds in air from 25 to 1000 C

DOE PAGES

Wood, E. Sooby; White, J. T.; Nelson, A. T.

2016-12-18

The air oxidation behavior of U 3Si 2, USi, and U 3Si 5 is studied from room temperature to 1000 C. Moreover, the onsets of breakaway oxidation for each compound are identified during synthetic air ramps to 1000 C using thermogravimetric analysis. Isothermal air oxidation tests are performed below and above the breakaway oxidation onset to discern the oxidation kinetic behavior of these candidate accident tolerant fuel forms. Uranium metal is tested in the same manner to provide a reference for the oxidation behavior. We present thermogravimetric, x-ray diffraction, and scanning electron microscopy analysis here along with a discussion ofmore » the oxidation behavior of these materials and the impact of the lack of oxidation resistance to their deployment as accident tolerant nuclear fuels.« less

Mechanical behavior of high strength ceramic fibers at high temperatures

NASA Technical Reports Server (NTRS)

Tressler, R. E.; Pysher, D. J.

1991-01-01

The mechanical behavior of commercially available and developmental ceramic fibers, both oxide and nonoxide, has been experimentally studied at expected use temperatures. In addition, these properties have been compared to results from the literature. Tensile strengths were measured for three SiC-based and three oxide ceramic fibers for temperatures from 25 C to 1400 C. The SiC-based fibers were stronger but less stiff than the oxide fibers at room temperature and retained more of both strength and stiffness to high temperatures. Extensive creep and creep-rupture experiments have been performed on those fibers from this group which had the best strengths above 1200 C in both single filament tests and tests of fiber bundles. The creep rates for the oxides are on the order of two orders of magnitude faster than the polymer derived nonoxide fibers. The most creep resistant filaments available are single crystal c-axis sapphire filaments. Large diameter CVD fabricated SiC fibers are the most creep and rupture resistant nonoxide polycrystalline fibers tested to date.

Melting behavior of mixed U-Pu oxides under oxidizing conditions

NASA Astrophysics Data System (ADS)

Strach, Michal; Manara, Dario; Belin, Renaud C.; Rogez, Jacques

2016-05-01

In order to use mixed U-Pu oxide ceramics in present and future nuclear reactors, their physical and chemical properties need to be well determined. The behavior of stoichiometric (U,Pu)O2 compounds is relatively well understood, but the effects of oxygen stoichiometry on the fuel performance and stability are often still obscure. In the present work, a series of laser melting experiments were carried out to determine the impact of an oxidizing atmosphere, and in consequence the departure from a stoichiometric composition on the melting behavior of six mixed uranium plutonium oxides with Pu content ranging from 14 to 62 wt%. The starting materials were disks cut from sintered stoichiometric pellets. For each composition we have performed two laser melting experiments in pressurized air, each consisting of four shots of different duration and intensity. During the experiments we recorded the temperature at the surface of the sample with a pyrometer. Phase transitions were qualitatively identified with the help of a reflected blue laser. The observed phase transitions occur at a systematically lower temperature, the lower the Pu content of the studied sample. It is consistent with the fact that uranium dioxide is easily oxidized at elevated temperatures, forming chemical species rich in oxygen, which melt at a lower temperature and are more volatile. To our knowledge this campaign is a first attempt to quantitatively determine the effect of O/M on the melting temperature of MOX.

Anomalous Micellization of Pluronic Block Copolymers

NASA Astrophysics Data System (ADS)

Leonardi, Amanda; Ryu, Chang Y.

2014-03-01

Poly(ethylene oxide) - poly(propylene oxide) - poly(ethylene oxide) (PEO-PPO-PEO) block copolymers, commercially known as Pluronics, are a unique family of amphiphilic triblock polymers, which self-assemble into micelles in aqueous solution. These copolymers have shown promise in therapeutic, biomedical, cosmetic, and nanotech applications. As-received samples of Pluronics contain low molecular weight impurities (introduced during the manufacturing and processing), that are ignored in most applications. It has been observed, however, that in semi-dilute aqueous solutions, at concentrations above 1 wt%, the temperature dependent micellization behavior of the Pluronics is altered. Anomalous behavior includes a shift of the critical micellization temperature and formation of large aggregates at intermediate temperatures before stable sized micelles form. We attribute this behavior to the low molecular weight impurities that are inherent to the Pluronics which interfere with the micellization process. Through the use of Dynamic Light Scattering and HPLC, we compared the anomalous behavior of different Pluronics of different impurity levels to their purified counterparts.

Oxidation characteristics of MgF2 in air at high temperature

NASA Astrophysics Data System (ADS)

Chen, H. K.; Jie, Y. Y.; Chang, L.

2017-02-01

High temperature oxidation properties of MgF2 in air were studied. The changes of phase composition, macro surface morphology, weight and elemental composition of MgF2 samples with temperature were investigated by using XRD, EDS and gravimetric analyses. The results show that the oxidation reaction of MgF2 converted to MgO occurred at high temperature, and the reaction was accelerated by the increase of temperature and the presence of impurities. This result clarifies the understanding of the high temperature oxidation behavior of MgF2 in air, and provides a theoretical basis for the reasonable application of MgF2 in optical coating materials, electronic ceramic materials and magnesium melt protection.

Influence of grain orientation on the incipient oxidation behavior of Haynes 230 at 900 °C

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wang, Xu, E-mail: xuw388@mail.usask.ca; Fan, Fan; Szpunar, Jerzy A.

Ni-based superalloy Haynes 230 is used in many applications such as very high temperature reactor (VHTR) or solid oxide fuel cells (SOFCs) where it is exposed to high temperature service environment. In order to improve the resistance for high temperature oxidation, the effect of crystallographic orientation on the early stage oxidation was investigated. It was demonstrated that different oxide thicknesses are formed on grains having different orientations. Comparison of electron backscatter diffraction (EBSD) orientation maps before and after oxidation at 900 °C indicates that grains near (111) orientation, especially with the deviation angle from <111> that is smaller than 20°,more » are more oxidation resistant than grains of other orientations. Correlation between the results of electron backscatter diffraction (EBSD) and atomic force microscopy (AFM) was used to compare the oxidation rate of grains having different crystallographic orientation. The oxidation rate was found to change with the crystallographic orientation as follows (111) < (110) < (100), also it was demonstrated that the oxidation rate changes are a nearly linear function of the angle of deviation from <111> direction. The morphology of surface oxide also depends on the orientation of grains. - Highlights: • Comparison of EBSD maps before and after oxidation allows to investigate the effect of orientation on oxidation in a more direct way; • Effect of crystallographic orientation on oxidation behavior of alloy 230 is studied by combination of EBSD and AFM; • Different thickness of oxide is formed on grain with different orientation and dependence of anisotropic oxidation behavior is discussed; • The morphology of grains is also orientation dependence.« less

Literature survey on oxidations and fatigue lives at elevated temperatures

NASA Technical Reports Server (NTRS)

Liu, H. W.; Oshida, Y.

1984-01-01

Nickel-base superalloys are the most complex and the most widely used for high temperature applications such as aircraft engine components. The desirable properties of nickel-base superalloys at high temperatures are tensile strength, thermomechanical fatigue resistance, low thermal expansion, as well as oxidation resistance. At elevated temperature, fatigue cracks are often initiated by grain boundary oxidation, and fatigue cracks often propagate along grain boundaries, where the oxidation rate is higher. Oxidation takes place at the interface between metal and gas. Properties of the metal substrate, the gaseous environment, as well as the oxides formed all interact to make the oxidation behavior of nickel-base superalloys extremely complicated. The important topics include general oxidation, selective oxidation, internal oxidation, grain boundary oxidation, multilayer oxide structure, accelerated oxidation under stress, stress-generation during oxidation, composition and substrate microstructural changes due to prolonged oxidation, fatigue crack initiation at oxidized grain boundaries and the oxidation accelerated fatigue crack propagation along grain boundaries.

Characterization and corrosion behavior of F6NM stainless steel treated in high temperature water

NASA Astrophysics Data System (ADS)

Li, Zheng-yang; Cai, Zhen-bing; Yang, Wen-jin; Shen, Xiao-yao; Xue, Guo-hong; Zhu, Min-hao

2018-03-01

F6NM martensitic stainless steel was exposed to 350 °C water condition for 500, 1500, and 2500 h to simulate pressurized water reactor (PWR) condition. The characterization and corrosion behavior of the oxide film were investigated. Results indicate that the exposed steel surface formed a double-layer oxide film. The outer oxide film is Fe-rich and contains two type oxide particles. However, the inner oxide film is Cr-rich, and two oxide films, whose thicknesses increase with increasing exposure time. The oxide film reduces the corrosion behavior because the outer oxide film has many crack and pores. Finally, the mechanism and factors affecting the formation of the oxide film were investigated.

Behavior of toxic metals and radionuclides during molten salt oxidation of chlorinated plastics.

PubMed

Yang, Hee-Chul; Cho, Yong-Jun; Eun, Hee-Chul; Yoo, Jae-Hyung; Kim, Joon-Hyung

2004-01-01

Molten salt oxidation is one of the promising alternatives to incineration for chlorinated organics without the emission of chlorinated organic pollutants. This study investigated the behavior of three hazardous metals (Cd, Pb, and Cr) and four radioactive metal surrogates (Cs, Ce, Gd, and Sm) in the molten Na2CO3 oxidation reactor during the destruction of PVC plastics. In the tested temperature ranges (1143 1223K) and NaCl content (0-10%), the impact of temperature on the retention of cadmium and lead in the molten salt reactor was very small, but that of the NaCl content for their retention was relatively higher. The influence of NaCl accumulation was, however, proven to be practically negligible due to the low-temperature operating characteristics of the molten salt oxidation system. Neither temperature increase nor chlorine accumulation in the MSO reactor reduced the retention of Cr, Ce, Gd, and Sm. Over 99.98% of these metals remained in the reactor. The influence of the temperature on the cesium behavior is relatively large for a chlorine addition, however, over 99.7% of cesium remained in the reactor throughout the entire test. The experimental metal entrainment rate and the entrained metal particle size distribution agree well with the theoretical equilibrium metal distributions.

Capacitive Behavior of Single Gallium Oxide Nanobelt

PubMed Central

Cai, Haitao; Liu, Hang; Zhu, Huichao; Shao, Pai; Hou, Changmin

2015-01-01

In this research, monocrystalline gallium oxide (Ga2O3) nanobelts were synthesized through oxidation of metal gallium at high temperature. An electronic device, based on an individual Ga2O3 nanobelt on Pt interdigital electrodes (IDEs), was fabricated to investigate the electrical characteristics of the Ga2O3 nanobelt in a dry atmosphere at room temperature. The current-voltage (I-V) and I/V-t characteristics show the capacitive behavior of the Ga2O3 nanobelt, indicating the existence of capacitive elements in the Pt/Ga2O3/Pt structure. PMID:28793506

High-temperature oxidation behavior and mechanism of a new type of wrought Ni-Fe-Cr-Al superalloy up to 1300 C

DOE Office of Scientific and Technical Information (OSTI.GOV)

Huang, J.; Fang, H.; Fu, X.

The oxidation behavior of a new type of wrought Ni-Fe-Cr-Al superalloys has been investigated systematically in the temperature range of 1,100 to 1,300 C. Results are compared with those of alloy 214, Inconel 600, and GH 3030. It is shown that the oxidation resistance of the new superalloys is excellent and much better than that of the comparison alloys. Scanning electron microscopy (SEM), electron probe microanalysis (EPMA), and X-ray diffraction (XRD) experiments reveal that the excellent oxidation resistance of the new superalloy is due to the formation of a dense, stable and continuous Al{sub 2}O{sub 3} and Cr{sub 2}O{sub 3}more » oxide layer at high temperatures. Differential thermal analysis (DTA) shows that the formation of Cr{sub 2}O{sub 3} and Al{sub 2}O{sub 3} oxide layers on the new superalloy reaches a maximum at 1,060 and 1,356 C, respectively. The Cr{sub 2}O{sub 3} layer peels off easily, and the single dense Al{sub 2}O{sub 3} layer remains, giving good oxidation resistance at temperatures higher than 1,150 C. In addition, the new superalloy possesses high mechanical strength at high temperatures. On-site tests showed that the new superalloy has ideal oxidation resistance and can be used at high temperatures up to 1,300 C in various oxidizing and corrosion atmospheres, such as those containing SO{sub 2}, CO{sub 2} etc., for long periods.« less

Incipient corrosion behavior of Haynes 230 under a controlled reducing atmosphere at high temperatures

NASA Astrophysics Data System (ADS)

Tung, Hsiao-Ming; Stubbins, James F.

2012-08-01

In situ thermogravimetry analysis (TGA) was used to investigate the incipient corrosion behavior of alloy 230 exposed under a reducing environment in a temperature range of 850-1000 °C. Both oxidation and loss of alloying elements of alloy 230 were observed to occur concurrently in these conditions. The surface oxide which formed on the substrate does not appear to be as effective in providing a protective layer during the incipient corrosion period.

Sliding durability of two carbide-oxide candidate high temperature fiber seal materials in air to 900 C

NASA Technical Reports Server (NTRS)

Dellacorte, Christopher; Steinetz, Bruce M.

1992-01-01

A test program to determine the friction and wear properties of two complex carbide oxide ceramic fibers for high temperature sliding seal applications is described. The fibers are based on Si, C, O, and Ti or Si, C, N, and O ceramic systems. Pin on disk tests using ceramic fiber covered pins and Inconel 718 disks, were conducted in air from 25 to 900 C to evaluate potential seal materials. This testing procedure was used in a previous study of oxide ceramic fibers which were found to exhibit wear behavior based predominantly on their mechanical properties. Like the oxide fibers tested previously, these carbide oxide ceramic fibers, show an increase in friction and wear with increased test temperature. At room temperature, the wear behavior seems to be based upon mechanical properties, namely tensile strength. At 500 and especially 900 C, the fibers wear by both mechanical fracture and by oxidative type wear. Based upon post test microscopic and x ray analyses, interaction between the fiber constituents and elements transferred from the counterface, namely Ni and Cr, may have occurred enhancing the tribochemical wear process. These results are interpreted.

Breakaway phenomenon of Zr-based alloys during a high-temperature oxidation

NASA Astrophysics Data System (ADS)

Baek, Jong Hyuk; Jeong, Yong Hwan

2008-01-01

The breakaway oxidation phenomena in Zr-based alloys were studied in the temperature range of 950-1200 °C for up to 36 000 s by using a modified thermo-gravimetric analyzer. After the oxidation tests, the oxidation behaviors, breakaway oxidation time, hydrogen pick-up contents, and oxidation rate constants of the alloys were systematically evaluated in this study. The breakaway oxidation time was shortened with an increase of the Sn content in the Zr alloys. A breakaway oxidation phenomenon could be caused by the transition of a tetragonal oxide phase into a monoclinic one, and the oxide transition could lead to form the oxide cracks in both the lateral and radial directions. The cracks within the oxide layer could result in catastrophic increase in the weight gain rates and rapid increase the hydrogen pick-up within the oxygen-stabilized α-Zr and prior β-Zr layers. The oxidation rate constants calculated from the post-breakaway data in the Zr alloys with breakaway oxidation behaviors matched well with the values from both the Baker-Just and Cathcart-Pawel correlations.

Detailed Multi-dimensional Modeling of Direct Internal Reforming Solid Oxide Fuel Cells.

PubMed

Tseronis, K; Fragkopoulos, I S; Bonis, I; Theodoropoulos, C

2016-06-01

Fuel flexibility is a significant advantage of solid oxide fuel cells (SOFCs) and can be attributed to their high operating temperature. Here we consider a direct internal reforming solid oxide fuel cell setup in which a separate fuel reformer is not required. We construct a multidimensional, detailed model of a planar solid oxide fuel cell, where mass transport in the fuel channel is modeled using the Stefan-Maxwell model, whereas the mass transport within the porous electrodes is simulated using the Dusty-Gas model. The resulting highly nonlinear model is built into COMSOL Multiphysics, a commercial computational fluid dynamics software, and is validated against experimental data from the literature. A number of parametric studies is performed to obtain insights on the direct internal reforming solid oxide fuel cell system behavior and efficiency, to aid the design procedure. It is shown that internal reforming results in temperature drop close to the inlet and that the direct internal reforming solid oxide fuel cell performance can be enhanced by increasing the operating temperature. It is also observed that decreases in the inlet temperature result in smoother temperature profiles and in the formation of reduced thermal gradients. Furthermore, the direct internal reforming solid oxide fuel cell performance was found to be affected by the thickness of the electrochemically-active anode catalyst layer, although not always substantially, due to the counter-balancing behavior of the activation and ohmic overpotentials.

Crystalline-like temperature dependence of the electrical characteristics in amorphous Indium-Gallium-Zinc-Oxide thin film transistors

NASA Astrophysics Data System (ADS)

Estrada, M.; Hernandez-Barrios, Y.; Cerdeira, A.; Ávila-Herrera, F.; Tinoco, J.; Moldovan, O.; Lime, F.; Iñiguez, B.

2017-09-01

A crystalline-like temperature dependence of the electrical characteristics of amorphous Indium-Gallium-Zinc-Oxide (a-IGZO) thin film transistors (TFTs) is reported, in which the drain current reduces as the temperature is increased. This behavior appears for values of drain and gate voltages above which a change in the predominant conduction mechanism occurs. After studying the possible conduction mechanisms, it was determined that, for gate and drain voltages below these values, hopping is the predominant mechanism with the current increasing with temperature, while for values above, the predominant conduction mechanism becomes percolation in the conduction band or band conduction and IDS reduces as the temperature increases. It was determined that this behavior appears, when the effect of trapping is reduced, either by varying the density of states, their characteristic energy or both. Simulations were used to further confirm the causes of the observed behavior.

Temperature and Strain-Rate Effects on Low-Cycle Fatigue Behavior of Alloy 800H

NASA Technical Reports Server (NTRS)

Rao, K. Bhanu Sankara; Schiffers, H.; Schuster, H.; Halford, G. R.

1996-01-01

The effects of strain rate (4 x 10(exp -6) to 4 x 10(exp -3)/s) and temperature on the Low-Cycle Fatigue (LCF) behavior of alloy 800H have been evaluated in the range 750 C to 950 C. Total axial strain controlled LCF tests were conducted in air at a strain amplitude of +/- 0.30 pct. LCF life decreased with decreasing strain rate and increasing temperature. The cyclic stress response behavior showed a marked variation with temperature and strain rate. The time- and temperature- dependent processes which influence the cyclic stress response and life have been identified and their relative importance assessed. Dynamic strain aging, time-dependent deformation, precipitation of parallel platelets of M(23)C6 on grain boundaries and incoherent ledges of twins, and oxidation were found to operate depending on the test conditions. The largest effect on life was shown by oxidation processes.

Steam Oxidation Testing in the Severe Accident Test Station

DOE Office of Scientific and Technical Information (OSTI.GOV)

Pint, Bruce A.

After the March 2011 accident at Fukushima Daiichi, Oak Ridge National Laboratory (ORNL) began conducting high temperature steam oxidation testing of candidate materials for accident tolerant fuel (ATF) cladding in August 2011 [1-11]. The ATF concept is to enhance safety margins in light water reactors (LWR) during severe accident scenarios by identifying materials with 100× slower steam oxidation rates compared to current Zr-based alloys. In 2012, the ORNL laboratory equipment was expanded and made available to the entire ATF community as the Severe Accident Test Station (SATS) [4,12]. Compared to the current UO2/Zr-based alloy fuel system, an ATF alternative wouldmore » significantly reduce the rate of heat and hydrogen generation in the core during a coolant-limited severe accident [13-14]. The steam oxidation behavior of candidate materials is a key metric in the evaluation of ATF concepts and also an important input into models [15-17]. However, initial modeling work of FeCrAl cladding has used incomplete information on the physical properties of FeCrAl. Also, the steam oxidation data being collected at 1200°-1700°C is unique as no prior work has considered steam oxidation of alloys at such high temperatures. Also, because many accident scenarios include steadily increasing temperatures, the required data are not traditional isothermal exposures but exposures with varying “ramp” rates. In some cases, the steam oxidation behavior has been surprising and difficult to interpret. Thus, more fundamental information continues to be collected. In addition, more work continues to focus on commercially-manufactured tube material. This report summarizes recent work to characterize the behavior of candidate alloys exposed to high temperature steam, evaluate steam oxidation behavior in various ramp scenarios and continue to collect integral data on FeCrAl compared to conventional Zr-based cladding.« less

The General Isothermal Oxidation Behavior of Cu-8Cr-4Nb

NASA Technical Reports Server (NTRS)

Thomas-Ogbuji, L. U.; Gray, Hugh R. (Technical Monitor)

2002-01-01

Oxidation kinetics of Cu-8Cr-4Nb was investigated by TGA (thermogravimetric) exposures between 500 and 900-C (at 25-50 C intervals) and the oxide scale morphologies examined by microscopy and micro-analysis. Because Cu-8Cr-4Nb is comprised of fine Cr2Nb precipitates in a Cu matrix, the results were interpreted by comparison with the behavior of copper (OFHC) and 'NARloy-Z' (a rival candidate material for thrust cell liner applications in advanced rocket engines) under the same conditions. While NARloy-Z and Cu exhibited identical oxidation behavior, Cu-8Cr-4Nb differed markedly in several respects: below approx. 700 C its oxidation rates were significantly lower than those of Cu; At higher temperatures its oxidation rates fell into two categories: an initial rate exceeding that of Cu, and a terminal rate comparable to that of Cu. Differences in oxide morphologies paralleled the kinetic differences at higher temperature: While NARloy-Z and Cu produced a uniform oxide scale of Cu2O inner layer and CuO outer layer, the inner (Cu2O) layer on Cu-8Cr-4Nb was stratified, with a highly porous/spongy inner stratum (responsible for the fast initial kinetics) and a dense/blocky outer stratum (corresponding to the slow terminal kinetics). Single and spinel oxides of Nb and Cr were found at the interface between the oxide scale and Cu-8Cr-4Nb substrate and it appears that these oxides were responsible for its suppressed oxidation rates at the intermediate temperatures. No difference was found between Cu-8Cr-4Nb oxidation in air and in oxygen at 1.0 atm.

Cyclic Oxidation and Hot Corrosion Behavior of Nickel-Iron-Based Superalloy

NASA Astrophysics Data System (ADS)

Chellaganesh, D.; Adam Khan, M.; Winowlin Jappes, J. T.; Sathiyanarayanan, S.

2018-01-01

The high temperature oxidation and hot corrosion behavior of nickel-iron-based superalloy are studied at 900 ° and 1000 °C. The significant role of alloying elements with respect to the exposed medium is studied in detail. The mass change per unit area was catastrophic for the samples exposed at 1000 °C and gradual increase in mass change was observed at 900 °C for both the environments. The exposed samples were further investigated with SEM, EDS and XRD analysis to study the metallurgical characteristics. The surface morphology has expressed the in situ nature of the alloy and its affinity toward the environment. The EDS and XRD analysis has evidently proved the presence of protective oxides formation on prolonged exposure at elevated temperature. The predominant oxide formed during the exposure at high temperature has a major contribution toward the protection of the samples. The nickel-iron-based superalloy is less prone to oxidation and hot corrosion when compared to the existing alloy in gas turbine engine simulating marine environment.

Reverse Stability Kinetics of Meat Pigment Oxidation in Aqueous Extract from Fresh Beef.

PubMed

Frelka, John C; Phinney, David M; Wick, Macdonald P; Heldman, Dennis R

2017-12-01

The use of kinetic models is an evolving approach to describing quality changes in foods during processes, including storage. Previous studies indicate that the oxidation rate of myoglobin is accelerated under frozen storage conditions, a phenomenon termed reverse stability. The goal of this study was to develop a model for meat pigment oxidation to incorporate the phenomenon of reverse stability. In this investigation, the model system was an aqueous extract from beef which was stored under a range of temperatures, both unfrozen and frozen. The kinetic analysis showed that in unfrozen solutions, the temperature dependence of oxidation rate followed Arrhenius kinetics. However, under in frozen solutions the rate of oxidation increased with decreasing temperature until reaching a local maximum around -20 °C. The addition of NaCl to the model system increased oxidation rates at all temperatures, even above the initial freezing temperature. This observation suggests that this reaction is dependent on the ionic strength of the solution as well as temperature. The mechanism of this deviant kinetic behavior is not fully understood, but this study shows that the interplay of temperature and composition on the rate of oxidation of meat pigments is complicated and may involve multiple mechanisms. A better understanding of the kinetics of quality loss in a meat system allows for a re-examination of the current recommendations for frozen storage. The deviant kinetic behavior observed in this study indicates that the relationship between quality loss and temperature in a frozen food is not as simple as once thought. Product-specific recommendations could be implemented in the future that would allow for a decrease in energy consumption without a significant loss of quality. © 2017 Institute of Food Technologists®.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wood, Elizabeth Sooby; Parker, Stephen Scott; Nelson, Andrew Thomas

The Fuel Cycle Research and Development program’s Advanced Fuels Campaign is currently supporting a range of experimental efforts aimed at the development and qualification of ‘accident tolerant’ nuclear fuel forms. One route to enhance the accident tolerance of nuclear fuel is to replace the zirconium alloy cladding, which is prone to rapid oxidation in steam at elevated temperatures, with a more oxidation-resistant cladding. Several cladding replacement solutions have been envisaged. The cladding can be completely replaced with a more oxidation resistant alloy, a layered approach can be used to optimize the strength, creep resistance, and oxidation tolerance of various materials,more » or the existing zirconium alloy cladding can be coated with a more oxidation-resistant material. Molybdenum is one candidate cladding material favored due to its high temperature creep resistance. However, it performs poorly under autoclave testing and suffers degradation under high temperature steam oxidation exposure. Development of composite cladding architectures consisting of a molybdenum core shielded by a molybdenum disilicide (MoSi 2) coating is hypothesized to improve the performance of a Mo-based cladding system. MoSi 2 was identified based on its high temperature oxidation resistance in O 2 atmospheres (e.g. air and “wet air”). However, its behavior in H 2O is less known. This report presents thermogravimetric analysis (TGA), scanning electron microscopy (SEM), and x-ray diffraction (XRD) results for MoSi 2 exposed to 670-1498 K water vapor. Synthetic air (80-20%, Ar-O 2) exposures were also performed, and those results are presented here for a comparative analysis. It was determined that MoSi 2 displays drastically different oxidation behavior in water vapor than in dry air. In the 670-1498 K temperature range, four distinct behaviors are observed. Parabolic oxidation is exhibited in only 670-773 K water vapor, a temperature range in which the material pests in dry O 2 environments. From 877-1084 K in water vapor, MoSi 2 undergoes rapid mass gain resulting in oxidation throughout the bulk of the sample at 980 K and 1084 K. The resulting material displays swelling and warping after the 980-1084 K exposures. A pre-passivation heat treatment performed at 1395 K was found capable of producing a coarse SiO 2 layer that limited pesting at lower temperatures in water vapor over the time periods investigated.« less

Crack healing in silicon nitride due to oxidation

NASA Technical Reports Server (NTRS)

Choi, Sung R.; Tikare, Veena; Pawlik, Ralph

1991-01-01

The crack healing behavior of a commercial, MgO-containing, hot pressed Si3N4 was studied as a function of temperature in oxidizing and inert annealing environments. Crack healing occurred at a temperature 800 C or higher due to oxidation regardless of crack size, which ranged from 100 microns (indentation crack) to 1.7 mm (SEPB precrack). The resulting strength and apparent fracture toughness increased at crack healing temperature by 100 percent and 300 percent, respectively. The oxide layer present in the crack plane was found to be highly fatigue resistant, indicating that the oxide is not solely silicate glass, but a mixture of glass, enstatite, and/or cristobalite that was insensitive to fatigue in a room temperature water environment.

Effect of the Mn oxidation state and lattice oxygen in Mn-based TiO2 catalysts on the low-temperature selective catalytic reduction of NO by NH3.

PubMed

Lee, Sang Moon; Park, Kwang Hee; Kim, Sung Su; Kwon, Dong Wook; Hong, Sung Chang

2012-09-01

TiO2-supported manganese oxide catalysts formed using different calcination temperatures were prepared by using the wet-impregnation method and were investigated for their activity in the low-temperature selective catalytic reduction (SCR) of NO by NH3 with respect to the Mn valence and lattice oxygen behavior. The surface and bulk properties of these catalysts were examined using Brunauer-Emmett-Teller (BET) surface area, X-ray diffraction (XRD), temperature-programmed reduction (TPR), and temperature-programmed desorption (TPD). Catalysts prepared using lower calcination temperatures, which contained Mn4+ displayed high SCR activity at low temperatures and possessed several acid sites and active oxygen. The TPD analysis determined that the Brönsted and Lewis acid sites in the Mn/TiO2 catalysts were important for the low-temperature SCR at 80-160 and 200-350 degrees C, respectively. In addition, the available lattice oxygen was important for attaining high NO to NO2 oxidation at low temperatures. Recently, various Mn catalysts have been evaluated as SCR catalysts. However, there have been no studies on the relationship of adsorption and desorption properties and behavior of lattice oxygen according to the valence state for manganese oxides (MnO(x)). Therefore, in this study, the catalysts were prepared by the wet-impregnation method at different calcination temperatures in order to show the difference of manganese oxidation state. These catalysts were then characterized using various physicochemical techniques, including BET, XRD, TPR, and TPD, to understand the structure, oxidation state, redox properties, and adsorption and desorption properties of the Mn/TiO2 catalysts.

Effects of Low-temperature Pre-oxidation on the Titanomagnetite Ore Structure and Reduction Behaviors in a Fluidized Bed

NASA Astrophysics Data System (ADS)

Adetoro, Ajala Adewole; Sun, Haoyan; He, Shengyi; Zhu, Qingshan; Li, Hongzhong

2018-04-01

With respect to high efficient utilization of low-grade iron ore resource, the behavior of low-temperature "973 K to 1123 K (700 °C to 850 °C)" oxidation, on the phase transition of SA TTM ore (South African titanomagnetite), and its effect on subsequent reduction was investigated. The results showed that hematite and rutile are the oxidation product below 1048 K (775 °C), while pseudobrookite is the stable phase above 1073 K (800 °C). With the increase in temperature and oxidation time, there is a competitive relationship between the amount of hematite and pseudobrookite generated. The reduction efficiency of SA TTM was significantly improved by oxidation pretreatment, primarily due to the dissociation of titania-ferrous oxides to more easily reducible hematite. But the generation of pseudobrookite phase decreases the amount of free hematite available for reduction, which weakens the improvement effect of pre-oxidation. The equilibrium relationship between the metallization degree and the gas reduction potential for TTM ore with pre-oxidation treatment has been built. Finally, the reduction metallization degree for the first and second step can be improved averagely by 16.67 and 3.45 pct, respectively, for sample pre-oxidized at 1098 K (825 °C) for 15 and 90 minutes, while 26.96 and 7.4 pct, improvement is achieved for sample pre-oxidized at a lower temperature of 1048 K (775 °C) for 120 minutes.

Influence of deformation behavior, oxydation, and temperature on the long time cyclic stress behavior of high temperature steels

NASA Technical Reports Server (NTRS)

Maile, K.

1982-01-01

The influence of different parameters on the creep-fatigue behavior of several steel alloys was investigated. The higher the temperature the lower the crack initiation value. Pauses during the cycle reduce the damage. Oxidation reduces and protective gas increases the lifetime. Prior loading and prior deformation reduce the lifetime. Short annealing slightly affects the cycle stress behavior. The test results do not satisfactorily agree with methods of extrapolation and damage accumulation.

Effect of Si Content on Oxide Formation on Surface of Molten Fe-Cr-C Alloy Bath During Oxygen Top Blowing

NASA Astrophysics Data System (ADS)

Mihara, Ryosuke; Gao, Xu; Kim, Sun-joong; Ueda, Shigeru; Shibata, Hiroyuki; Seok, Min Oh; Kitamura, Shin-ya

2018-02-01

Using a direct observation experimental method, the oxide formation behavior on the surface of Fe-Cr-5 mass pct C-Si alloy baths during decarburization by a top-blown Ar-O2 mixture was studied. The effects of the initial Si and Cr content of the alloy, temperature, and oxygen feed ratio on oxide formation were investigated. The results showed that, for alloys without Si, oxide particles, unstable oxide films, and stable oxide films formed sequentially. The presence of Si in the alloy changed the formation behavior of stable oxide film, and increased the crucial C content when stable oxide film started to form. Increasing the temperature, decreasing the initial Cr content, and increasing the ratio of the diluting gas decreased the critical C content at which a stable oxide film started to form. In addition, the P CO and a_{{{Cr}2 {O}3 }} values at which oxides started to form were estimated using Hilty's equation and the equilibrium relation to understand the formation conditions and the role of each parameter in oxide formation.

The curious case of exploding quantum dots: anomalous migration and growth behaviors of Ge under Si oxidation

PubMed Central

2013-01-01

We have previously demonstrated the unique migration behavior of Ge quantum dots (QDs) through Si3N4 layers during high-temperature oxidation. Penetration of these QDs into the underlying Si substrate however, leads to a completely different behavior: the Ge QDs ‘explode,’ regressing back almost to their origins as individual Ge nuclei as formed during the oxidation of the original nanopatterned SiGe structures used for their generation. A kinetics-based model is proposed to explain the anomalous migration behavior and morphology changes of the Ge QDs based on the Si flux generated during the oxidation of Si-containing layers. PMID:23618165

Analysis of the Negative-SET Behaviors in Cu/ZrO2/Pt Devices

NASA Astrophysics Data System (ADS)

Liu, Sen; Zhao, Xiaolong; Li, Qingjiang; Li, Nan; Wang, Wei; Liu, Qi; Xu, Hui

2016-12-01

Metal oxide-based electrochemical metallization memory (ECM) shows promising performance for next generation non-volatile memory. The negative-SET behavior has been observed in various oxide-based ECM devices. But the underlying mechanism of this behavior remains unaddressed and the role of the metal cation and oxygen vacancy in this behavior is unclear. In this work, we have observed two kinds of negative-SET (labeled as N-SET1 and N-SET2) behaviors in our Cu/ZrO2/Pt devices. Both the two behaviors can result in hard breakdown due to the high compliance current in reset process. The I-V characteristic shows that the two negative-SET behaviors have an obvious difference in operation voltage. Using four-probe resistance measurement method, the resistance-temperature characteristics of the ON-state after various negative-SET behaviors have been studied. The temperature dependence results demonstrate that the N-SET1 behavior is dominated by Cu conductive filament (CF) reformation caused by the Cu CF overgrowth phenomenon while the N-SET2 is related to the formation of oxygen vacancy CF. This work may provide a comprehensive understanding of the switching mechanism in oxide-based ECM devices.

Microstructure and surface chemistry of amorphous alloys important to their friction and wear behavior

NASA Technical Reports Server (NTRS)

Miyoshi, K.; Buckley, D. H.

1983-01-01

An investigation was conducted to examine the microstructure and surface chemistry of amorphous alloys, and their effects on tribological behavior. The results indicate that the surface oxide layers present on amorphous alloys are effective in providing low friction and a protective film against wear in air. Clustering and crystallization in amorphous alloys can be enhanced as a result of plastic flow during the sliding process at a low sliding velocity, at room temperature. Clusters or crystallines with sizes to 150 nm and a diffused honeycomb-shaped structure are produced on the wear surface. Temperature effects lead to drastic changes in surface chemistry and friction behavior of the alloys at temperatures to 750 C. Contaminants can come from the bulk of the alloys to the surface upon heating and impart to the surface oxides at 350 C and boron nitride above 500 C. The oxides increase friction while the boron nitride reduces friction drastically in vacuum.

Silicon carbide as an oxidation-resistant high-temperature material. 1: Oxidation and heat corrosion behavior

NASA Technical Reports Server (NTRS)

Schlichting, J.

1981-01-01

The oxidation and corrosion behavior of SiC (in the form of a SiC powder) and hot-pressed and reaction-bound material were studied. The excellent stability of SiC in an oxidizing atmosphere is due to the development of protective SiO2 coatings. Any changes in these protective layers (e.g., due to impurities, reaction with corrosive media, high porosity of SiC, etc.) lead in most cases to increased rates of oxidation and thus restrict the field of SiC application.

Room temperature ferromagnetic and semiconducting properties of graphene adsorbed with cobalt oxide using electrochemical method

NASA Astrophysics Data System (ADS)

Park, Chang-Soo; Lee, Kyung Su; Chu, Dongil; Lee, Juwon; Shon, Yoon; Kim, Eun Kyu

2017-12-01

We report the room temperature ferromagnetic properties of graphene adsorbed by cobalt oxide using electrochemical method. The cobalt oxide doping onto graphene was carried out in 0.1 M LiCoO2/DI-water solution. The doped graphene thin film was determined to be a single layer from Raman analysis. The CoO doped graphene has a clear ferromagnetic hysteresis at room temperature and showed a remnant magnetization, 128.2 emu/cm3. The temperature dependent conductivity of the adsorbed graphene showed the semiconducting behavior and a band gap opening of 0.12 eV.

Oxidation behaviors of porous Haynes 214 alloy at high temperatures

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wang, Yan, E-mail: wangyan@csu.edu.cn; Liu, Yong, E-mail: yonliu@csu.edu.cn; Tang, Huiping, E-mail: hptang@c-nin.com

The oxidation behaviors of porous Haynes 214 alloy at temperatures from 850 to 1000 °C were investigated. The porous alloys before and after the oxidation were examined by optical microscopy, scanning electron microscopy (SEM) and energy dispersive spectroscopy (EDS), X-ray diffraction (XRD) analyses, and X-ray photoelectron spectroscopy (XPS). The oxidation kinetics of the porous alloy approximately follows a parabolic rate law and exhibits two stages controlled by different oxidation courses. Complex oxide scales composed of Cr{sub 2}O{sub 3}, NiCr{sub 2}O{sub 4} and Al{sub 2}O{sub 3} are formed on the oxidized porous alloys, and the formation of Cr{sub 2}O{sub 3} onmore » its outer layer is promoted with the oxidation proceeding. The rough surface as well as the micropores in the microstructures of the porous alloy caused by the manufacturing process provides fast diffusion paths for oxygen so as to affect the formation of the oxide layers. Both the maximum pore size and the permeability of the porous alloys decrease with the increase of oxidation temperature and exposure time, which may limit its applications. - Highlights: • Two-stage oxidation kinetics controlled by different oxidation courses is showed. • Oxide scale mainly consists of Cr{sub 2}O{sub 3}, NiCr{sub 2}O{sub 4} and Al{sub 2}O{sub 3}. • Rough surface and micropores lead to the formation of uneven oxide structure. • Content of Cr{sub 2}O{sub 3} in the outer layer of the scale increases with time at 1000 °C. • Maximum pore size and permeability decrease with increasing temperature and time.« less

Detailed Multi‐dimensional Modeling of Direct Internal Reforming Solid Oxide Fuel Cells

PubMed Central

Tseronis, K.; Fragkopoulos, I.S.; Bonis, I.

2016-01-01

Abstract Fuel flexibility is a significant advantage of solid oxide fuel cells (SOFCs) and can be attributed to their high operating temperature. Here we consider a direct internal reforming solid oxide fuel cell setup in which a separate fuel reformer is not required. We construct a multidimensional, detailed model of a planar solid oxide fuel cell, where mass transport in the fuel channel is modeled using the Stefan‐Maxwell model, whereas the mass transport within the porous electrodes is simulated using the Dusty‐Gas model. The resulting highly nonlinear model is built into COMSOL Multiphysics, a commercial computational fluid dynamics software, and is validated against experimental data from the literature. A number of parametric studies is performed to obtain insights on the direct internal reforming solid oxide fuel cell system behavior and efficiency, to aid the design procedure. It is shown that internal reforming results in temperature drop close to the inlet and that the direct internal reforming solid oxide fuel cell performance can be enhanced by increasing the operating temperature. It is also observed that decreases in the inlet temperature result in smoother temperature profiles and in the formation of reduced thermal gradients. Furthermore, the direct internal reforming solid oxide fuel cell performance was found to be affected by the thickness of the electrochemically‐active anode catalyst layer, although not always substantially, due to the counter‐balancing behavior of the activation and ohmic overpotentials. PMID:27570502

Very Long Term Oxidation of Ti-48Al-2Cr-2Nb at 704 C In Air

NASA Technical Reports Server (NTRS)

Locci, I. E.; Brady, M. P.; MacKay, R. A.; Smith, J. W.

1997-01-01

Introduction Titanium aluminides are of great interest for intermediate-temperature (600 C - 850 C) aerospace and power generation applications because of their high specific properties. Replacement of conventional superalloys by titanium aluminides offers the potential of significant weight savings. Extensive development efforts over the past IO years have led to the identification of y (TiAl) + alpha(sub 2) (Ti3Al) alloys, such as the G.E. alloy Ti48Al-2Cr-2Nb (all composition in at. %), which offer a balance of room temperature mechanical properties and high-temperature strength retention. The two phase gamma + alpha(sub 2) class of titanium aluminides also offers superior oxidation and embrittlement resistance compared to the alpha(sub 2) and orthorhombic classes of titanium aluminides. However, environmental durability is still a major concern. Significant progress has recently been made in understanding the fundamental aspects of the oxidation behavior of binary gamma + alpha(sub 2) Ti-Al alloys. However, most of this work has concentrated on short term (less than 1000 hours), high temperature (900 C - 1000 C) exposures. Also little data are available in the literature regarding the oxidation behavior of the quaternary and higher order gamma + alpha(sub 2) engineering alloys. This is especially true for the very long-term, low temperature conditions likely to be experienced during engineering applications. The present work addresses this regime to fill this gap by characterizing the oxidation behavior of Ti48Al-2Cr-2Nb for periods up to 9000 h at 704 C in air.

Investigation on the oxidation behavior of AlCrVxN thin films by means of synchrotron radiation and influence on the high temperature friction

NASA Astrophysics Data System (ADS)

Tillmann, Wolfgang; Kokalj, David; Stangier, Dominic; Paulus, Michael; Sternemann, Christian; Tolan, Metin

2018-01-01

Friction minimization is an important topic which is pursued in research and industry. In addition to the use of lubricants, friction-reducing oxide phases can be utilized which occur during. These oxides are called Magnéli phases and especially vanadium oxides exhibit good friction reducing properties. Thereby, the lubrication effect can be traced back to oxygen deficiencies. AlCrN thin films are being used as coatings for tools which have to withstand high temperatures. A further improvement of AlCrN thin films concerning their friction properties is possible by incorporation of vanadium. This study analyzes the temperature dependent oxidation behavior of magnetron sputtered AlCrVN thin films with different vanadium contents up to 13.5 at.-% by means of X-ray diffraction and X-ray absorption near-edge spectroscopy. Up to 400 °C the coatings show no oxidation. A higher temperature of 700 °C leads to an oxidation and formation of Magnéli phases of the coatings with vanadium contents above 10.7 at.-%. Friction coefficients, measured by ball-on-disk test are correlated with the oxide formation in order to figure out the effect of vanadium oxides. At 700 °C a decrease of the friction coefficient with increasing vanadium content can be observed, due to the formation of VO2, V2O3 and the Magnéli phase V4O7.

The 100,000-hour cyclic oxidation behavior at 815C (1500 F) of 33 high-temperature alloys

NASA Technical Reports Server (NTRS)

Barrett, C. A.

1977-01-01

Commercial high-temperature Fe-, Ni-, and Co-base alloys were oxidized in air at 815 deg C for ten 1000-hour cycles. Specific weight change versus time curves were derived and the 10,000-hour surface oxides were analyzed by X-ray diffraction. The alloys were ranked by a combination of appearance and metal loss estimates derived from gravimetric data.

A Review of In Situ Observations of Crystallization and Growth in High Temperature Oxide Melts

NASA Astrophysics Data System (ADS)

Wang, Zhanjun; Sohn, Il

2018-05-01

This review summarizes the significant results of high-temperature confocal laser scanning microscopy (CLSM) and single hot thermocouple technology (SHTT) and its application in observing the crystallization and growth in high-temperature oxide melts from iron- and steel-making slags to continuous casting mold fluxes. Using in situ observations of CLSM and SHTT images of high-temperature molten oxides with time, temperature, and composition, the crystallization behavior, including crystal morphology, crystallization temperature, initial nucleation and growth rate, could be obtained. The broad range of applications using in situ observations during crystallization have provided a wealth of opportunities in pyrometallurgy and is provided in this review.

Effect of Prior Exposure at Elevated Temperatures on Tensile Properties and Stress-Strain Behavior of Three Oxide/Oxide Ceramic Matrix Composites

DTIC Science & Technology

2015-03-26

OF THREE OXIDE/OXIDE CERAMIC MATRIX COMPOSITES THESIS Christopher J. Hull, Captain, USAF AFIT- ENY -MS-15-M-228 DEPARTMENT OF THE AIR FORCE...Government and is not subject to copyright protection in the United States. AFIT- ENY -MS-15-M-228 EFFECT OF PRIOR EXPOSURE AT ELEVATED TEMPERATURES ON...BS Captain, USAF March 2015 DISTRIBUTION STATEMENT A: APPROVED FOR PUBLIC RELEASE; DISTRIBUTION UNLIMITED AFIT- ENY - MS-15-M-228 EFFECT OF

X-ray photoelectron spectroscopy study of the stability of Fomblin Z25 on the native oxide of aluminum

NASA Technical Reports Server (NTRS)

Herrera-Fierro, Pilar; Pepper, Stephen V.; Jones, William R.

1992-01-01

Thin films of Fomblin Z25, a perfluoropolyalkylether lubricant, were vapor deposited onto clean, oxidized aluminum, and onto sapphire surfaces, and their behavior at different temperatures was studied using X-ray photoelectron spectroscopy and temperature desorption spectroscopy (TDS). The interfacial fluid molecules decompose on the native oxide at room temperature, and continue to decompose at elevated temperatures, as previous studies had shown to occur on the clean metal. TDS indicated that different degradation mechanisms were operative for clean and oxidized aluminum. On sapphire substrates, no reaction was observed at room temperature. The native oxide of aluminum is neither passive nor protective towards Fomblin Z25. At higher temperatures (150 C), degradation of the polymer on sapphire produced a debris layer at the interface with a chemical composition similar to the one formed on aluminum oxide. Rubbing a Fomblin film on a single crystal sapphire also induced the decomposition of the lubricant in contact with the interface and the formation of a debris layer.

A study of the relationship between microstructure and oxidation effects in nuclear graphite at very high temperatures

NASA Astrophysics Data System (ADS)

Lo, I.-Hsuan; Tzelepi, Athanasia; Patterson, Eann A.; Yeh, Tsung-Kuang

2018-04-01

Graphite is used in the cores of gas-cooled reactors as both the neutron moderator and a structural material, and traditional and novel graphite materials are being studied worldwide for applications in Generation IV reactors. In this study, the oxidation characteristics of petroleum-based IG-110 and pitch-based IG-430 graphite pellets in helium and air environments at temperatures ranging from 700 to 1600 °C were investigated. The oxidation rates and activation energies were determined based on mass loss measurements in a series of oxidation tests. The surface morphology was characterized by scanning electron microscopy. Although the thermal oxidation mechanism was previously considered to be the same for all temperatures higher than 1000 °C, the significant increases in oxidation rate observed at very high temperatures suggest that the oxidation behavior of the selected graphite materials at temperatures higher than 1200 °C is different. This work demonstrates that changes in surface morphology and in oxidation rate of the filler particles in the graphite materials are more prominent at temperatures above 1200 °C. Furthermore, possible intrinsic factors contributing to the oxidation of the two graphite materials at different temperature ranges are discussed taking account of the dominant role played by temperature.

Selective Tuning of Elastin-like Polypeptide Properties via Methionine Oxidation.

PubMed

Petitdemange, Rosine; Garanger, Elisabeth; Bataille, Laure; Dieryck, Wilfrid; Bathany, Katell; Garbay, Bertrand; Deming, Timothy J; Lecommandoux, Sébastien

2017-02-13

We have designed and prepared a recombinant elastin-like polypeptide (ELP) containing precisely positioned methionine residues, and performed the selective and complete oxidation of its methionine thioether groups to both sulfoxide and sulfone derivatives. Since these oxidation reactions substantially increase methionine residue polarity, they were found to be a useful means to precisely adjust the temperature responsive behavior of ELPs in aqueous solutions. In particular, lower critical solution temperatures were found to be elevated in oxidized sample solutions, but were not eliminated. These transition temperatures were found to be further tunable by the use of solvents containing different Hofmeister salts. Overall, the ability to selectively and fully oxidize methionine residues in ELPs proved to be a convenient postmodification strategy for tuning their transition temperatures in aqueous media.

Oxidation kinetics of some Ni-Cr alloys.

PubMed

Baran, G

1983-01-01

Oxidation kinetics of four Ni-Cr alloys and a high-purity nickel standard was determined under isothermal conditions in an air atmosphere. In addition, weight gains of the alloys were measured during a simulated pre-oxidation treatment. The alloys' behavior suggests that mechanisms of oxidation vary with temperature and alloy composition.

Correlation between the microstructures of graphite oxides and their catalytic behaviors in air oxidation of benzyl alcohol.

PubMed

Geng, Longlong; Wu, Shujie; Zou, Yongcun; Jia, Mingjun; Zhang, Wenxiang; Yan, Wenfu; Liu, Gang

2014-05-01

A series of graphite oxide (GO) materials were obtained by thermal treatment of oxidized natural graphite powder at different temperatures (from 100 to 200 °C). The microstructure evolution (i.e., layer structure and surface functional groups) of the graphite oxide during the heating process is studied by various characterization means, including XRD, N2 adsorption, TG-DTA, in situ DRIFT, XPS, Raman, TEM and Boehm titration. The characterization results show that the structures of GO materials change gradually from multilayer sheets to a transparent ultrathin 2D structure of the carbon sheets. The concentration of surface COH and HOCO groups decrease significantly upon treating temperature increasing. Benzyl alcohol oxidation with air as oxidant source was carried out to detect the catalytic behaviors of different GO materials. The activities of GO materials decrease with the increase of treating temperatures. It shows that the structure properties, including ultrathin sheets and high specific surface area, are not crucial factors affecting the catalytic activity. The type and amount of surface oxygen-containing functional groups of GO materials tightly correlates with the catalytic performance. Carboxylic groups on the surface of GO should act as oxidative sites for benzyl alcohol and the reduced form could be reoxidized by molecular oxygen. Copyright © 2014 Elsevier Inc. All rights reserved.

Effect of ZrB2 addition on the oxidation behavior of Si-SiC-ZrB2 composites exposed at 1500°C in air.

PubMed

D'Amico, Claudio; Bianchi, Giovanni; Padovano, Elisa; Biamino, Sara; Aversa, Alberta; Badini, Claudio; Ortona, Alberto

2018-01-01

Silicon carbide ceramics obtained by reactive infiltration of silicon (SRI) have many industrial applications especially involving severe and high temperature conditions. In this study, the oxidation behavior in air of Si-SiC-ZrB 2 systems at a high temperature (1500°C) for dwelling times of up to 48 hours was examined. The oxidation process was analyzed on the basis of elemental maps and X-ray diffraction patterns taken, respectively, on the core and on the surface of the specimens, together with weight gains and the average thicknesses of the resulting scale. Further, flexural strength at room temperature was examined as a function of different oxidation times. The main chemical reactions and phase transformations involved in the oxidation process are reported. Several oxides were detected on the surface: zirconia, silica, zircon and 3-zirconium monoxide. All of the samples showed a parabolic oxidation kinetics, suggesting that the controlling mechanism was the diffusion; however, even after 48 hours, the oxidation process was not finished - indeed, all of the samples continued to gain weight. The oxidation of Si-SiC-ZrB 2 material produced via SRI was slower compared with previously investigated ZrB 2 -SiC composites processed with a different techniques and tested in similar conditions. The oxidation mechanism was found to be consistent with the convection cells model.

Elevated temperature mechanical behavior of monolithic and SiC whisker-reinforced silicon nitrides

NASA Technical Reports Server (NTRS)

Salem, Jonathan A.; Choi, Sung R.; Sanders, William A.; Fox, Dennis S.

1991-01-01

The mechanical behavior of a 30 volume percent SiC whisker reinforced silicon nitride and a similar monolithic silicon nitride were measured at several temperatures. Measurements included strength, fracture toughness, crack growth resistance, dynamic fatigue susceptibility, post oxidation strength, and creep rate. Strength controlling defects were determined with fractographic analysis. The addition of SiC whiskers to silicon nitride did not substantially improve the strength, fracture toughness, or crack growth resistance. However, the fatigue resistance, post oxidation strength, and creep resistance were diminished by the whisker addition.

10,000-Hour Cyclic Oxidation Behavior at 982 C (1800 F) of 68 High-Temperature Co-, Fe-, and Ni-Base Alloys

NASA Technical Reports Server (NTRS)

Barrett, Charles A.

1997-01-01

Sixty-eight high temperature Co-, Fe-, and Ni-base alloys were tested for 10-one thousand hour cycles in static air at 982 C (1800 F). The oxidation behavior of the test samples was evaluated by specific weight change/time data, x-ray diffraction of the post-test samples, and their final appearance. The gravimetric and appearance data were combined into a single modified oxidation parameter, KB4 to rank the cyclic oxidation resistance from excellent to catastrophic. The alloys showing the 'best' resistance with no significant oxidation attack were the alumina/aluminate spinel forming Ni-base turbine alloys: U-700, NASA-VIA and B-1900; the Fe-base ferritic alloys with Al: TRW-Valve, HOS-875, NASA-18T, Thermenol and 18SR; and the Ni-base superalloy IN-702.

Creep-Rupture and Fatigue Behavior of a Notched Oxide/Oxide Ceramic Matrix Composite at Elevated Temperature

DTIC Science & Technology

2008-06-01

99 xi List of Tables Table Page Table 1. Nextel 720 Properties (3M website...6 Table 2. Typical Properties for Alumina (Chawla, 1993) ................................................. 7 Table 3...Although material advances in the usage of superalloys have helped this increase in operating temperatures, cooling air is also a main driver of these

Comparison of isothermal and cyclic oxidation behavior of twenty-five commercial sheet alloys at 1150 C

NASA Technical Reports Server (NTRS)

Barrett, C. A.; Lowell, C. E.

1974-01-01

The cyclic and isothermal oxidation resistance of 25 high-temperature Ni-, Co-, and Fe-base sheet alloys after 100 hours in air at 1150 C was compared. The alloys were evaluated in terms of their oxidation, scaling, and vaporization rates and their tendency for scale spallation. These values were used to develop an oxidation rating parameter based on effective thickness change, as calculated from a mass balance. The calculated thicknesses generally agreed with the measured values, including grain boundary oxidation, to within a factor of 3. Oxidation behavior was related to composition, particularly Cr and Al content.

Oxidation of C/SiC Composites at Reduced Oxygen Partial Pressures

NASA Technical Reports Server (NTRS)

Opila, Elizabeth J.; Serra, Jessica

2009-01-01

Carbon-fiber reinforced SiC (C/SiC) composites are proposed for leading edge applications of hypersonic vehicles due to the superior strength of carbon fibers at high temperatures (greater than 1500 C). However, the vulnerability of the carbon fibers in C/SiC to oxidation over a wide range of temperatures remains a problem. Previous oxidation studies of C/SiC have mainly been conducted in air or oxygen, so that the oxidation behavior of C/SiC at reduced oxygen partial pressures of the hypersonic flight regime are less well understood. In this study, both carbon fibers and C/SiC composites were oxidized over a wide range of temperatures and oxygen partial pressures to facilitate the understanding and modeling of C/SiC oxidation kinetics for hypersonic flight conditions.

Wear of Selected Oxide Ceramics and Coatings

NASA Technical Reports Server (NTRS)

Miyoshi, K.; Sayir, A.; Farmer, S. C.

2005-01-01

The use of oxide ceramics and coatings for moving mechanical components operating in high-temperature, oxidizing environments creates a need to define the tribological performance and durability of these materials. Results of research focusing on the wear behavior and properties of Al2O3/ZrO2 (Y2O3) eutectics and coatings under dry sliding conditions are discussed. The importance of microstructure and composition on wear properties of directionally solidified oxide eutectics is illustrated. Wear data of selected oxide-, nitride-, and carbide-based ceramics and coatings are given for temperatures up to 973K in air.

Effect of zinc oxide nanoparticles on dielectric behavior of nematic liquid crystal

NASA Astrophysics Data System (ADS)

Sharma, Amit; Kumar, Pankaj; Malik, Praveen

2018-05-01

In this work, phase transition and dielectric behavior of nematic liquid crystal (NLC), E7 and zinc oxide (ZnO) nanoparticles (NPs) doped nematic liquid crystals are investigated. Effect of nano-particles dispersion is analyzed and compared with the dielectric behavior of E7 and E7-ZnO. Frequency dependent dielectric permittivity at various temperatures in nematic phase for E7 and E7-ZnO sample is also studied.

High-Temperature Oxidation Behavior of Al-Co-Cr-Ni-(Fe or Si) Multicomponent High-Entropy Alloys

NASA Astrophysics Data System (ADS)

Butler, T. M.; Alfano, J. P.; Martens, R. L.; Weaver, M. L.

2015-01-01

High-entropy alloys (HEAs) are a class of alloys that are being considered for a number of applications. In the present study, the microstructures and 1050°C oxidation behaviors of two HEAs, Al10Cr22.5Co22.5Ni22.5Fe22.5 (at.%) and Al20Cr25Co25Ni25Si5 have been investigated along with Al15Cr10Co35Ni35Si5, which is a high-temperature shape-memory alloy. Oxide formation occurred via selective oxidation in a manner that was consistent with the oxide formation model devised by Giggins and Pettit for model Ni-Cr-Al alloys. The lower Al content alloy formed an external Cr2O3 scale and an internal subscale consisting of Al2O3 and AlN precipitates. The higher Al content alloys exhibited smaller mass gains and formed external Al2O3 scales without any internal oxidation of the alloys.

Oxidation of Slurry Aluminide Coatings on Cast Stainless Steel Alloy CF8C-Plus at 800oC in Water Vapor

DOE Office of Scientific and Technical Information (OSTI.GOV)

Haynes, James A; Armstrong, Beth L; Dryepondt, Sebastien N

A new, cast austenitic stainless steel, CF8C-Plus, has been developed for a wide range of high temperature applications, including diesel exhaust components, turbine casings and turbocharger housings. CF8C-Plus offers significant improvements in creep rupture life and creep rupture strength over standard CF8C steel. However, at higher temperatures and in more aggressive environments, such as those containing significant water vapor, an oxidation-resistant protective coating will be necessary. The oxidation behavior of alloys CF8C and CF8C-Plus with various aluminide coatings were compared at 800oC in air plus 10 vol% water vapor. Due to their affordability, slurry aluminides were the primary coating systemmore » of interest, although chemical vapor deposition (CVD) and pack cementation coatings were also compared. Additionally, a preliminary study of the low cycle fatigue behavior of aluminized CF8C-Plus was conducted at 800oC. Each type of coating provided substantial improvements in oxidation behavior, with simple slurry aluminides showing very good oxidation resistance after 4,000 h testing in water vapor. Preliminary low cycle fatigue results indicated that thicker aluminide coatings degraded high temperature fatigue properties of CF8C-Plus, whereas thinner coatings did not. Results suggest that appropriately designed slurry aluminide coatings are a viable option for economical, long-term oxidation protection of austenitic stainless steels in water vapor.« less

SiC Fiber-Reinforced Celsian Composites

NASA Technical Reports Server (NTRS)

Bansal, Narottam P.

2003-01-01

Celsian is a promising matrix material for fiber-reinforced composites for high temperature structural applications. Processing and fabrication of small diameter multifilament silicon carbide tow reinforced celsian matrix composites are described. Mechanical and microstructural properties of these composites at ambient and elevated temperatures are presented. Effects of high-temperature exposures in air on the mechanical behavior of these composites are also given. The composites show mechanical integrity up to 1100 C but degrade at higher temperatures in oxidizing atmospheres. A model has been proposed for the degradation of these composites in oxidizing atmospheres at high temperatures.

Modification of tribology and high-temperature behavior of Ti 48Al 2Cr 2Nb intermetallic alloy by laser cladding

NASA Astrophysics Data System (ADS)

Liu, Xiu-Bo; Wang, Hua-Ming

2006-06-01

In order to improve the tribology and high-temperature oxidation properties of the Ti-48Al-2Cr-2Nb intermetallic alloy simultaneously, mixed NiCr-Cr 3C 2 precursor powders had been investigated for laser cladding treatment to modify wear and high-temperature oxidation resistance of the material. The alloy samples were pre-placed with NiCr-80, 50 and 20%Cr 3C 2 (wt.%), respectively, and laser treated at the same parameters, i.e., laser output power 2.8 kW, beam scanning speed 2.0 mm/s, beam dimension 1 mm × 18 mm. The treated samples underwent tests of microhardness, wear and high-temperature oxidation. The results showed that laser cladding with different constitution of mixed precursor NiCr-Cr 3C 2 powders improved surface hardness in all cases. Laser cladding with NiCr-50%Cr 3C 2 resulted in the best modification of tribology and high-temperature oxidation behavior. X-ray diffraction (XRD), optical microscope (OM), scanning electron microscopy (SEM) and energy-dispersive spectrometer (EDS) analyses indicated that the formation of reinforced Cr 7C 3, TiC and both continuous and dense Al 2O 3, Cr 2O 3 oxide scales were supposed to be responsible for the modification of the relevant properties. As a result, the present work had laid beneficial surface engineering foundation for TiAl alloy applied as future light weight and high-temperature structural candidate materials.

Very Long Term Oxidation of Titanium Aluminides Investigated

NASA Technical Reports Server (NTRS)

Locci, Ivan E.; Brady, Michael P.; Smialek, James L.; Retallick, William B.

2000-01-01

Titanium aluminides (TiAl) are of great interest for intermediate-temperature (600 to 850 C) aerospace and power-generation applications because they offer significant weight savings over today's nickel alloys. TiAl alloys are being investigated for low-pressure turbine blade applications, exhaust nozzle components, and compressor cases in advanced subsonic and supersonic engines. Significant progress has been made in understanding the fundamental aspects of the oxidation behavior of binary TiAl alloys. However, most of this work has concentrated on short term (<1000 hr), high-temperature (900 to 1000 C) exposures. Also, there is not much data available in the literature regarding the oxidation behavior of the quaternary and higher order engineering alloys. This is especially true for the very long term, low-temperature conditions likely to be experienced during aerospace applications. An investigation at the NASA Glenn Research Center at Lewis Field was undertaken to characterize the long-term oxidation behavior of various model and advanced titanium aluminides for periods up to 7000 hr at 704 C in air using a high-resolution field emission scanning electron microscope. Also, a unique surface treatment technique developed to improve the oxidation resistance of TiAl was evaluated. The alloys included in this investigation are listed in the table. The table also shows typical alloy compositions and the specific weight changes and scale thickness measured for each alloy after exposure to 700 C for 7000 hr in air.

Influences of superalloy composition and Pt content on the oxidation behavior of gamma–gamma prime NiPtAl bond coatings

DOE PAGES

Haynes, James A.; Unocic, Kinga A.; Lance, Michael J.; ...

2016-09-13

Here, the effects of superalloy composition and Pt content on the high-temperature oxidation behavior of γ–γ’ NiPtAl diffusion coatings were investigated over the temperature range of 1050–1150 °C. Simple NiPtAl diffusion coatings with 7 or 12 µm electroplated Pt thickness were evaluated in 1-h cycles in dry O 2 for up to 2500 cycles on four superalloys: directionally solidified (DS) alloy 142, 1st generation single-crystal (SX) alloy 1483, and 2nd generation SX alloys X4 and N5. Coatings on high-Hf alloy 142 experienced severe internal oxidation of Hf at all temperatures. Coatings on ~5 at.% Ti alloy 1483 were protective atmore » 1050 °C, but exhibited severe scale spallation at 1100 °C, with extensive formation of Ti- and Ni-rich oxides at the gas interface. Coatings with 7-µm Pt on X 4 were extremely protective at 1100 °C, but failed rapidly at 1150 °C, which also was associated with the formation of Ti-rich oxides. Increasing the coating Pt content on X 4 improved the 1150 °C oxidation behavior. Coatings on Ti-free N 5 showed the best performance at 1150 °C, especially with 12-µm Pt. Although γ–γ’ coatings can exhibit outstanding cyclic oxidation resistance with minimal Al depletion, they appear to be sensitive to substrate composition, as well as eventual Pt depletion due to interdiffusion.« less

Effect of Specimen Thickness on Mechanical Behavior of SiC/SiC Composites

NASA Technical Reports Server (NTRS)

Morscher, Gregory N.; Singh, Mrityunjay; Freedman, Marc

2004-01-01

Potential composite applications in aerospace and transportation application systems have different thickness requirements. For example, space applications such as nozzle ramps or heat exchangers use very thin (less than 1 mm) structures whereas turbine blades need very thick parts greater than or equal to cm). There has been little investigation into the effect of thickness on stress-strain behavior or elevated temperature tensile properties controlled by oxidation. In this study, composites consisting of woven Hi-NicalonTM fibers, a carbon interphase, and CVI Sic matrix were fabricated with different numbers of plies to provide variable thickness. The composites ranged from a single ply (approximately 0.4 mm) to thirty-six plies (approximately 1 cm). Tensile tests were performed at room temperature with acoustic emission used to monitor matrix crack behavior. Elevated temperature tensile stress-rupture tests were performed in air. Considerably different room and elevated temperature tensile behavior was observed that will be discussed with respect to the effect of thickness on matrix crack formation, matrix crack growth and oxidation diffusion kinetics.

Effect of oxide layer formation on deformation of aluminum alloys under fire conditions

DOE PAGES

Yilmaz, Nadir; Vigil, Francisco M.; Tolendino, Greg; ...

2015-05-14

The purpose of this study is to investigate the structural behavior of aluminum alloys used in the aerospace industry when exposed to conditions similar to those of an accident scenario, such as a fuel fire. This study focuses on the role that the aluminum oxide layer plays in the deformation and the strength of the alloy above melting temperature. To replicate some of the thermal and atmospheric conditions that the alloys might experience in an accident scenario, aluminum rod specimens were subjected to temperatures near to or above their melting temperature in air, nitrogen, and vacuum environments. The characteristics ofmore » their deformation, such as geometry and rate of deformation, were observed. Tests were conducted by suspending aluminum rods vertically from an enclosure. This type of experiment was performed in two different environments: air and nitrogen. The change in environments allowed the effects of the oxide layer on the material strength to be analyzed by inhibiting the growth of the oxide layer. Observations were reported from imaging taken during the experiment showing creep behavior of aluminum alloys at elevated temperatures and time to failure. In addition, an example of tensile load–displacement data obtained in air and vacuum was reported to understand the effect of oxide layer on aluminum deformation and strength.« less

Resistance to High-Temperature Oxidation and Wear of Various Ferrous Alloys Used in Rolling Mills

NASA Astrophysics Data System (ADS)

Delaunois, Fabienne; Stanciu, Victor Ioan; Sinnaeve, Mario

2018-03-01

Various materials are commonly used to manufacture work rolls for hot rolling mills, such as ICDP (Indefinite Chill Double Pour) cast irons, high-chromium white cast irons, and high speed steels (HSS). Various chemical compositions and microstructures are studied in order to optimize the in-use behavior of those grades of rolls. In this paper, six grades of ferrous alloys (an ICDP cast iron; an ICDP cast iron enriched in vanadium, niobium, and molybdenum; a HSS; a graphitic HSS; a high-chromium white cast iron (Hi-Cr); and a niobium-molybdenum-doped high-chromium white cast iron) were investigated. High-temperature oxidation tests with gravimetric means at 575 °C in water vapor atmosphere and sliding wear tests were carried out. The oxidation kinetics was followed during oxidation test. The microstructure was observed by optical and scanning electron microscopies. The oxides formed on the surface of the samples were analyzed by XRD and EDS. The thickness of the oxide scales and the mass gain were measured after oxidation test. The results showed that the behavior of all the grades differed. The oxide scale of HSS and HSS-G grades was fine and their friction coefficient was low. The weight gain after oxidation test of HSS was high. Hi-Cr and M-Hi-Cr grades presented highly porous oxide layer and an important increase of the friction coefficient during wear test. ICDP and M-ICDP had intermediate behavior.

[Oxidation behavior and kinetics of representative VOCs emitted from petrochemical industry over CuCeOx composite oxides].

PubMed

Chen, Chang-Wei; Yu, Yan-Ke; Chen, Jin-Sheng; He, Chi

2013-12-01

CuCeOx composite catalysts were synthesized via coprecipitation (COP-CuCeO,) and incipient impregnation (IMP-CuCeOx) methods, respectively. The physicochemical properties of the samples were characterized by XRD, low-temperature N2 sorption, H2-TPR and O2-TPD. The influences of reactant composition and concentration, reaction space velocity, O2 content, H2O concentration, and catalyst type on the oxidation behaviors of benzene, toluene, and n-hexane emitted from petrochemical industry were systematically investigated. In addition, the related kinetic parameters were model fitted. Compared with IMP-CuCeOx, COP-CuCeOx had well-dispersed active phase, better low-temperature reducibility, and more active surface oxygen species. The increase of reactant concentration was unfavorable for toluene oxidation, while the opposite phenomenon could be observed in n-hexane oxidation. The inlet concentration of benzene was irrelevant to its conversion under high oxidation rate. The introduction of benzene obviously inhibited the oxidation of toluene and n-hexane, while the presence of toluene had a positive effect on beuzene conversion. The presence of n-hexane could promote the oxidation of toluene, while toluene had a negative influence on e-hexane oxidation. Both low space velocity and high oxygen concentration were beneficial for the oxidation process, and the variation of oxygen content had negligible effect on n-hexane and henzene oxidation. The presence of H2O noticeably inhibited the oxidation of toluene, while significantly accelerated the oxidation procedure of henzene and n-hexane. COP-CuCeOx had superior catalytic performance for toluene and benzene oxidation, while IMP-CuCeOx showed higher n-hexane oxidation activity under dry condition. The oxidation behaviors under different conditions could be well fitted and predicted by the pseudo first-order kinetic model.

Understanding the low temperature electrical properties of nanocrystalline tin oxide for gas sensor applications

NASA Astrophysics Data System (ADS)

Drake, Christina Hartsell

Nanocrystalline metal/metal oxide is an important class of transparent and electronic materials due to its potential use in many applications, including gas sensors. At the nanoscale, many of the phenomena observed that give nanocrystalline semiconducting oxide enhanced performance as a gas sensor material over other conventional engineering materials is still poorly understood. This study is aimed at understanding the low temperature electrical and chemical properties of nanocrystalline SnO2 that makes it suitable for room temperature gas detectors. Studies were carried out in order to understand how various synthesis methods affect the surfaces on the nano-oxides, interactions of a target gas (in this study hydrogen) with different surface species, and changes in the electrical properties as a function of dopants and grain size. A correlation between the surface reactions and the electrical response of doped nanocrystalline metal-oxide-semiconductors exposed to a reducing gas is established using Fourier Transform Infrared (FTIR) Spectroscopy attached to a specially built custom designed catalytic cell. First principle calculations of oxygen vacancy concentrations from absorbance spectra are presented. FTIR is used for effectively screening of these nanostructures for gas sensing applications. The effect of processing temperature on the microstructural evolution and on the electronic properties of nanocrystalline trivalent doped-SnO 2 is also presented. This study includes the effect of dopants (In and Ce) on the growth of nano-SnO2, as well as their effects on the electronic properties and gas sensor behavior of the nanomaterial at room temperature. Band bending affects are also investigated for this system and are related to enhanced low temperature gas sensing. The role and importance of oxygen vacancies in the electronic and chemical behavior of surface modified nanocrystalline SnO2 are explored in this study. A generalized explanation for the low temperature gas sensor behavior of nanocrystalline oxide is presented that can be generalized to other nano-oxide systems and be useful in specific engineering of other nanomaterials. Deeper understanding of how nano-oxides react chemically and electronically would be extremely beneficial to issues present in current low cost, low temperature sensor technology. Ability to exactly monitor and then engineer the chemistry of nanostructures in the space charge region as well as the surface is also of great significance. Knowledge of the mechanisms responsible for enhanced sensor response in this material system could viably be applied to other material systems for sensor applications.

The influence of oxidation time on the properties of oxidized zinc films

NASA Astrophysics Data System (ADS)

Rambu, A. P.

2012-09-01

The effect of oxidation time on the structural characteristics and electronic transport mechanism of zinc oxide thin films prepared by thermal oxidation, have been investigated. Zinc metallic films were deposited by thermal evaporation under vacuum, the subsequent oxidation of Zn films being carried out in open atmosphere. XRD and AFM analysis indicate that obtained films posses a polycrystalline structure, the crystallites having a preferential orientation. Structural analysis reveals that microstructure of the films (crystallite size, surface roughness, internal stress) is depending on the oxidation time of metallic films. The electrical behavior of ZnO films was investigated, during a heat treatment (two heating/cooling cycles). It was observed that after the first heating, the temperature dependences of electrical conductivity become reversible. Mott variable range hopping model was proposed to analyze the temperature dependence of the electrical conductivity, in low temperature ranges. Values of some characteristic parameters were calculated.

Coverage-Dependent Anchoring of 4,4'-Biphenyl Dicarboxylic Acid to CoO(111) Thin Films.

PubMed

Mohr, Susanne; Schmitt, Tobias; Döpper, Tibor; Xiang, Feifei; Schwarz, Matthias; Görling, Andreas; Schneider, M Alexander; Libuda, Jörg

2017-05-02

We investigated the adsorption behavior of 4,4'-biphenhyl dicarboxylic acid (BDA) on well-ordered CoO(111) films grown on Ir(100) as a function of coverage and temperature using time-resolved and temperature-programmed infrared reflection absorption spectroscopy (TR-IRAS, TP-IRAS) in combination with density functional theory (DFT) and scanning tunneling microscopy (STM) under ultrahigh vacuum (UHV) conditions. To compare the binding behavior of BDA as a function of the oxide film thickness, three different CoO(111) film thicknesses were explored: films of about 20 bilayers (BLs) (approximately 5 nm), 2 BLs, and 1 BL. The two carboxylic acid groups of BDA offer two potential anchoring points to the oxide surface. At 150 K, intact BDA adsorbs on 20 BL thick oxide films in planar geometry with the phenyl rings aligned parallel to the surface. With decreasing oxide film thickness, we observe an increasing tendency for deprotonation and the formation of flat-lying BDA molecules anchored as dicarboxylates. After saturation of the first monolayer, intact BDA multilayers grow with molecules aligned parallel to the surface. The BDA multilayer desorbs at around 360 K. Completely different growth behavior is observed if BDA is deposited above the multilayer desorption temperature. Initially, doubly deprotonated dicarboxylates are formed by adopting a flat-lying orientation. With increasing exposure, however, the adsorbate layer transforms into upright standing monocarboxylates. A sharp OH stretching band (3584 cm -1 ) and a blue-shifted CO stretching band (1759 cm -1 ) indicate weakly interacting apical carboxylic acid groups at the vacuum interface. The anchored monocarboxylate phase slowly desorbs in a temperature range of up to 470 K. At higher temperature, a flat-lying doubly deprotonated BDA is formed, which desorbs and decomposes in a temperature range of up to 600 K.

Correlation between the oxide impedance and corrosion behavior of Zr-Nb-Sn-Fe-Cu alloys

NASA Astrophysics Data System (ADS)

Park, Sang-Yoon; Lee, Myung-Ho; Jeong, Yong-Hwan; Jung, Youn-Ho

2004-12-01

The correlation between the oxide impedance and corrosion behavior of two series of Zr-Nb-Sn-Fe-Cu alloys was evaluated. Corrosion tests were performed in a 70 ppm LiOH aqueous solution at 360°C for 300 days. The results of the corrosion tests revealed that the corrosion behavior of the alloys depended on the Nb and Sn content. The impedance characteristics for the pre- and post-transition oxide layers formed on the surface of the alloys were investigated in sulfuric acid at room temperature. From the results, a pertinent equivalent circuit model was preferably established, explaining the properties of double oxide layers. The impedance of the oxide layers correlated with the corrosion behavior; better corrosion resistance always showed higher electric resistance for the inner layers. It is thus concluded that a pertinent equivalent circuit model would be useful for evaluating the long-term corrosion behavior of Zr-Nb-Sn-Fe-Cu alloys.

In situ surface and interface study of crystalline (3×1)-O on InAs

NASA Astrophysics Data System (ADS)

Qin, Xiaoye; Wang, Wei-E.; Rodder, Mark S.; Wallace, Robert M.

2016-07-01

The oxidation behavior of de-capped InAs (100) exposed to O2 gas at different temperatures is investigated in situ with high resolution of monochromatic x-ray photoelectron spectroscopy and low energy electron diffraction. The oxide chemical states and structure change dramatically with the substrate temperature. A (3 × 1) crystalline oxide layer on InAs is generated in a temperature range of 290-330 °C with a coexistence of In2O and As2O3. The stability of the crystalline oxide upon the atomic layer deposition (ALD) of HfO2 is studied as well. It is found that the generated (3 × 1) crystalline oxide is stable upon ALD HfO2 growth at 100 °C.

Intense photoluminescence from amorphous tantalum oxide films

NASA Astrophysics Data System (ADS)

Zhu, Minmin; Zhang, Zhengjun; Miao, Wei

2006-07-01

Tantalum oxide films were deposited on silicon substrates at a temperature of ˜450°C by heating a pure tantalum foil in a rough vacuum. The films were amorphous in structure and consisted of fully oxidized Ta2O5 and (TaOx, x <2.5) suboxides. This feature resulted in strong visible light emission from the films further oxidized in the air at temperatures of 200-300°C. The mechanism for this photoluminescence behavior of the amorphous tantalum oxide films was also investigated and discussed. This study suggests that wide-band-gap materials could act as effective visible light emitters and provides a simple route to synthesize such materials.

Corrosion Behavior of FBR Structural Materials in High Temperature Supercritical Carbon Dioxide

NASA Astrophysics Data System (ADS)

Furukawa, Tomohiro; Inagaki, Yoshiyuki; Aritomi, Masanori

A key problem in the application of a supercritical carbon dioxide (CO2) turbine cycle to a fast breeder reactor (FBR) is the corrosion of structural material by supercritical CO2 at high temperature. In this study, corrosion test of high-chromium martensitic steel (12Cr-steel) and FBR grade type 316 stainless steel (316FR), which are candidate materials for FBRs, were performed at 400-600°C in supercritical CO2 pressurized at 20MPa. Corrosion due to the high temperature oxidation in exposed surface was measured up to approximately 2000h in both steels. In the case of 12Cr-steel, the weight gain showed parabolic growth with exposure time at each temperature. The oxidation coefficient could be estimated by the Arrhenius function. The specimens were covered by two successive oxide layers, an Fe-Cr-O layer (inside) and an Fe-O layer (outside). A partial thin oxide diffusion layer appeared between the base metal and the Fe-Cr-O layer. The corrosion behavior was equivalent to that in supercritical CO2 at 10MPa, and no effects of CO2 pressure on oxidation were observed in this study. In the case of 316FR specimens, the weight gain was significantly lower than that of 12Cr-steel. Dependency of neither temperature nor exposed time on oxidation was not observed, and the value of all tested specimens was within 2g/m2. Nodule shape oxides which consisted of two structures, Fe-Cr-O and Fe-O were observed on the surface of the 316FR specimen. Carburizing, known as a factor in the occurrence of breakaway corrosion and/or the degradation of ductility, was observed on the surface of both steels.

Comparative study of the oxidation of NiAl(100) by molecular oxygen and water vapor using ambient-pressure X-ray photoelectron spectroscopy

DOE PAGES

Liu, Qianqian; Qin, Hailang; Boscoboinik, Jorge Anibal; ...

2016-10-11

The oxidation behavior of NiAl(100) by molecular oxygen and water vapor under a near-ambient pressure of 0.2 Torr is monitored using ambient-pressure X-ray photoelectron spectroscopy. O 2 exposure leads to the selective oxidation of Al at temperatures ranging from 40 to 500 °C. By contrast, H 2O exposure results in the selective oxidation of Al at 40 and 200 °C, and increasing the oxidation temperature above 300 °C leads to simultaneous formation of both Al and Ni oxides. Furthermore, these results demonstrate that the O 2 oxidation forms a nearly stoichiometric Al 2O 3 structure that provides improved protection tomore » the metallic substrate by barring the outward diffusion of metals. By contrast, the H 2O oxidation results in the formation of a defective oxide layer that allows outward diffusion of Ni at elevated temperatures for simultaneous NiO formation.« less

Comparative study of the oxidation of NiAl(100) by molecular oxygen and water vapor using ambient-pressure X-ray photoelectron spectroscopy

DOE Office of Scientific and Technical Information (OSTI.GOV)

Liu, Qianqian; Qin, Hailang; Boscoboinik, Jorge Anibal

The oxidation behavior of NiAl(100) by molecular oxygen and water vapor under a near-ambient pressure of 0.2 Torr is monitored using ambient-pressure X-ray photoelectron spectroscopy. O 2 exposure leads to the selective oxidation of Al at temperatures ranging from 40 to 500 °C. By contrast, H 2O exposure results in the selective oxidation of Al at 40 and 200 °C, and increasing the oxidation temperature above 300 °C leads to simultaneous formation of both Al and Ni oxides. Furthermore, these results demonstrate that the O 2 oxidation forms a nearly stoichiometric Al 2O 3 structure that provides improved protection tomore » the metallic substrate by barring the outward diffusion of metals. By contrast, the H 2O oxidation results in the formation of a defective oxide layer that allows outward diffusion of Ni at elevated temperatures for simultaneous NiO formation.« less

Behavior of oxide film at the interface between particles in sintered Al powders by pulse electric-current sintering

NASA Astrophysics Data System (ADS)

Xie, Guoqiang; Ohashi, Osamu; Song, Minghui; Furuya, Kazuo; Noda, Tetsuji

2003-03-01

The microstructure of the bonding interfaces between particles in aluminum (Al) powder sintered specimens by the pulse electric-current sintering (PECS) process was observed, using conventional transmission electron microscopy (CTEM) and high-resolution transmission electron microscopy (HRTEM). The behavior of oxide film at the interface between Al particles and its effect on properties of the sintered specimens were investigated. The results showed there were two kinds of bonding interfaces in the sintered specimens, namely, the direct metal/metal bonding and the metal/oxide film layer/metal bonding interface. By increasing the fraction of the direct metal/metal bonding interfaces, the tensile strength of the sintered specimens increased, and the electrical resistivity decreased. By increasing the loading pressure at higher sintering temperatures or increasing the sintering temperature under loading pressure, the breakdown of oxide film was promoted. The broken oxide film debris was dispersed in aluminum metal near the bonding interfaces between particles.

Microstructure investigations of U3Si2 implanted by high-energy Xe ions at 600 °C

NASA Astrophysics Data System (ADS)

Miao, Yinbin; Harp, Jason; Mo, Kun; Kim, Yeon Soo; Zhu, Shaofei; Yacout, Abdellatif M.

2018-05-01

The microstructure investigations on a high-energy Xe-implanted U3Si2 pellet were performed. The promising accident tolerant fuel (ATF) candidate, U3Si2, was irradiated by 84 MeV Xe ions at 600 °C at Argonne Tandem Linac Accelerator System (ATLAS). The characterizations of the Xe implanted sample were conducted using advanced transmission electron microscopy (TEM) techniques. An oxidation layer was observed on the sample surface after irradiation under the ∼10-5 Pa vacuum. The study on the oxidation layer not only unveils the readily oxidation behavior of U3Si2 under high-temperature irradiation conditions, but also develops an understanding of its oxidation mechanism. Intragranular Xe bubbles with bimodal size distribution were observed within the Xe deposition region of the sample induced by 84 MeV Xe ion implantation. At the irradiation temperature of 600 °C, the gaseous swelling strain contributed by intragranular bubbles was found to be insignificant, indicating an acceptable fission gas behavior of U3Si2 as a light water reactor (LWR) fuel operating at such a temperature.

Thermal behavior of metal carboxylates—II. Lead formate

NASA Astrophysics Data System (ADS)

Baraldi, Pietro

Experimental data obtained by i.r. emission spectrometry indicate that the thermal behavior of lead formate is complex. By heating in air, after a phase transition at 115°C, decomposition takes place which may lead directly to metal and oxide or to carbonate, to a basic carbonate and finally to oxide. Under vacuum the same transformations occur at higher temperatures and lead to metal.

A statistical analysis of elevated temperature gravimetric cyclic oxidation data of 36 Ni- and Co-base superalloys based on an oxidation attack parameter

NASA Technical Reports Server (NTRS)

Barrett, Charles A.

1992-01-01

A large body of high temperature cyclic oxidation data generated from tests at NASA Lewis Research Center involving gravimetric/time values for 36 Ni- and Co-base superalloys was reduced to a single attack parameter, K(sub a), for each run. This K(sub a) value was used to rank the cyclic oxidation resistance of each alloy at 1000, 1100, and 1150 C. These K(sub a) values were also used to derive an estimating equation using multiple linear regression involving log(sub 10)K(sub a) as a function of alloy chemistry and test temperature. This estimating equation has a high degree of fit and could be used to predict cyclic oxidation behavior for similar alloys and to design an optimum high strength Ni-base superalloy with maximum high temperature cyclic oxidation resistance. The critical alloy elements found to be beneficial were Al, Cr, and Ta.

An XPS study of the stability of Fomblin Z25 on the native oxide of aluminum. [x ray photoelectron spectroscopy

NASA Technical Reports Server (NTRS)

Herrera-Fierro, Pilar; Pepper, Stephen V.; Jones, William R.

1991-01-01

Thin films of Fomblin Z25, a perfluoropolyalkylether lubricant, were vapor deposited onto clean, oxidized aluminum and sapphire surfaces, and their behavior at different temperatures was studied using x ray photoelectron spectroscopy (XPS) and thermal desorption spectroscopy (TDS). It was found that the interfacial fluid molecules decompose on the native oxide at room temperature, and continue to decompose at elevated temperatures, as previous studies had shown to occur on clean metal. TDS indicated that different degradation mechanisms were operative for clean and oxidized aluminum. On sapphire substrates, no reaction was observed at room temperature. Our conclusion is that the native oxide of aluminum is neither passive nor protective towards Fomblin Z25. At high temperatures (150 C) degradation of the polymer on sapphire produced a debris layer at the interface with a chemical composition similar to the one formed on aluminum oxide. Rubbing a Fomblin film on a single crystal sapphire also induced the decomposition of the lubricant in contact with the interface and the formulation of a debris layer.

Surface spectroscopy studies of the oxidation behavior of uranium

NASA Astrophysics Data System (ADS)

Bloch, J.; Atzmony, U.; Dariel, M. P.; Mintz, M. H.; Shamir, N.

1982-02-01

Auger electron spectroscopy (AES) and X-ray photoelectron spectroscopy (XPS) techniques were utilized to study the oxidation behavior of clean uranium surfaces, at very low pressures of various atmospheres (UHV, H 2, O 2, and CO 2), at room temperature. Both for O 2 and CO 2, a precursor chemisorbed oxygen species has been identified at the very initial stage of the oxidation reaction. This chemisorbed oxygen transforms to the oxide form at a rate which depends on the pressure of the oxidizing atmosphere. Residual gaseous carbon compounds which are present even under UHV conditions result in the simultaneous formation of surface carbide which accompanies the initial stage of oxidation. This carbide however decomposes later as oxidation proceeds. Adventitious hydrocarbon adsorption occurs on the formed oxide layer.

Biobased, environmentally friendly lubricants for processing plants

USDA-ARS?s Scientific Manuscript database

Vegetable oil based lubricants have excellent lubricity, biodegradability, good viscosity temperature characteristics and low evaporation loss, but poor thermos-oxidative stability and cold flow properties. This paper presents a systematic approach to improve the oxidative and cold flow behavior of...

Effect of Alloying Additions on Oxidation Behaviors of Ni-Fe Based Superalloy for Ultra-Supercritical Boiler Applications

NASA Astrophysics Data System (ADS)

Lu, Jintao; Yang, Zhen; Zhao, Xinbao; Yan, Jingbo; Gu, Y.

A new kind of Ni-Fe-based superalloy is designed recently for 750 °C-class A-USC boiler tube. The oxidation behavior of the designed alloys with various combinations of anti-oxidation additions, Cr, Al and Si, was investigated at 750 °C and 850 °C, respectively. The results indicated that the oxidation rate of tested alloys decreased with the increase of the sum of additions. Cr addition may drop the relative constant of parabolic rate greatly when temperature is raised. But the oxide scale, mainly consisted of NiCr spinel at 750 °C and NiCrMn spinel at 850 °C, was similar while the Cr content is in a range of 20-25 wt.% at tested temperatures. Al addition, however, showed the best effective to reduce the oxidation rates. Internal Al-rich oxide was observed at the scale/metal interface for alloys added with high content of Al and was increased with Al content increase. Very tiny difference between the oxide scales of the Si-added alloys was identified when Si content varies among 0.02-0.05 wt.%. Basing on these results, this presentation discussed the optimum combination of anti-oxidation additions as well as oxidation mechanisms in the designed Ni-Fe-base superalloy.

Oxidation-resisting technology of W-Re thermocouples and their industrial applications

NASA Astrophysics Data System (ADS)

Wang, K.; Dai, M.; Dong, J.; Wang, L.; Wang, T.

2013-09-01

We use DSC/TG, SEM and EPMA approaches to investigate the high temperature oxidation behaviors of the Type C W-Re thermocouple wires and W-Re powders which the wires were made from. To solve the oxidization of W-Re thermocouples the chemical method, other than the commonly used physical method, i.e. vacuum-pumping method, was developed. Several solid-packed techniques such as stuffing with inert material, chemical deoxidizing, gas-absorbing and sealing were employed to prevent the W-Re thermocouples from oxidizing. Based on comprehensive consideration of various parameters in process industries, a series of industrial W-Re thermocouples has been successfully used in oxidizing and reducing atmospheres, high temperature alkali and other harsh environments. The service life is 6 to 12 months in strong oxidizing atmosphere of Cr2O3-Al2O3 brick kiln and 2 to 3 months in high temperature alkali and in reducing atmosphere of CO.

The effect of molten salt on high temperature behavior of stainless steel and titanium alloy with the presence of water vapor

NASA Astrophysics Data System (ADS)

Baharum, Azila; Othman, Norinsan Kamil; Salleh, Emee Marina

2018-04-01

The high temperature oxidation experiment was conducted to study the behavior of titanium alloy Ti6A14V and stainless steel 316 in Na2SO4-50%NaCl + Ar-20%O2 (molten salt) and Na2SO4-50%NaCl + Ar-20%O2 + 12% H2O (molten salt + water vapor) environment at 900°C for 30 hours using horizontal tube furnace. The sample then was investigated using weight change measurement analysis and X-ray diffraction (XRD) analysis to study the weight gained and the phase oxidation that occurred. The weight gained of the titanium alloy was higher in molten salt environment compared to stainless steel due to the rapid growth in the oxide scale but showed almost no change of weight gained upon addition of water vapor. This is due to the alloy was fully oxidized. Stainless steel showed more protection and better effect in molten salt environment compared to mixed environment showed by slower weight gain and lower oxidation rate. Meanwhile, the phase oxidation test of the samples showed that the titanium alloy consist of multi oxide layer of rutile (TiO2) and Al2O3 on the surface of the exposed sample. While stainless steel show the formation of both protective Cr-rich oxide and non-protective Fe-rich oxide layer. This can be concluded that stainless steel is better compared to Ti alloy due to slow growing of chromia oxide. Therefore it is proven that stainless steel has better self-protection upon high temperature exposure.

Effect of SiC Content on the Ablation and Oxidation Behavior of ZrB2-Based Ultra High Temperature Ceramic Composites

PubMed Central

Hu, Ping; Gui, Kaixuan; Yang, Yang; Dong, Shun; Zhang, Xinghong

2013-01-01

The ablation and oxidation of ZrB2-based ultra high temperature ceramic (UHTC) composites containing 10%, 15% and 30% v/v SiC were tested under different heat fluxes in a high frequency plasma wind tunnel. Performance was significantly affected by the surface temperature, which was strongly dependent on the composition. Composites containing 10% SiC showed the highest surface temperature (>2300 °C) and underwent a marked degradation under both conditions. In contrast, composites with 30% SiC exhibited the lowest surface temperature (<2000 °C) and demonstrated excellent ablation resistance. The surface temperature of UHTCs in aerothermal testing was closely associated with the dynamic evolution of the surface and bulk oxide properties, especially for the change in chemical composition on the exposed surface, which was strongly dependent on the material composition and testing parameters (i.e., heat flux, enthalpy, pressure and test time), and in turn affected its oxidation performance. PMID:28809239

Effect of SiC Content on the Ablation and Oxidation Behavior of ZrB₂-Based Ultra High Temperature Ceramic Composites.

PubMed

Hu, Ping; Gui, Kaixuan; Yang, Yang; Dong, Shun; Zhang, Xinghong

2013-04-29

The ablation and oxidation of ZrB₂-based ultra high temperature ceramic (UHTC) composites containing 10%, 15% and 30% v/v SiC were tested under different heat fluxes in a high frequency plasma wind tunnel. Performance was significantly affected by the surface temperature, which was strongly dependent on the composition. Composites containing 10% SiC showed the highest surface temperature (>2300 °C) and underwent a marked degradation under both conditions. In contrast, composites with 30% SiC exhibited the lowest surface temperature (<2000 °C) and demonstrated excellent ablation resistance. The surface temperature of UHTCs in aerothermal testing was closely associated with the dynamic evolution of the surface and bulk oxide properties, especially for the change in chemical composition on the exposed surface, which was strongly dependent on the material composition and testing parameters ( i.e. , heat flux, enthalpy, pressure and test time), and in turn affected its oxidation performance.

Effects of High-Temperature Preoxidation on the Titanomagnetite Ore Structure and Reduction Behaviors in Fluidized Bed

NASA Astrophysics Data System (ADS)

Sun, Haoyan; Adetoro, Ajala Adewole; Pan, Feng; Wang, Zhen; Zhu, Qingshan

2017-06-01

The oxidation behaviors of South Africa (SA) titanomagnetite (TTM) and its effects on the gas solid reduction in the fluidized bed were investigated on the basis of the two-stage short process of direct reduction-electric arc furnace (DR-EAF) melting separation. The results showed that the oxidation phase transformations in the high-temperature range from 1073 K to 1223 K (800 °C to 950 °C) can be divided into two typical processes: with the fast generation of pseudobrookite and with the maghemite generation at the initial stage. The reduction efficiency for SA TTM was improved by the preoxidation treatment, mainly because of the dissociation of titania-ferrous oxides to the easy reducible hematite. However, at a preoxidation temperature higher than 1173 K (900 °C), the improving effect became weak, due to high-temperature sintering and the larger crystallite size of oxidation products. There is an extreme value of the preoxidation influence, and the optimum preoxidation time is different for various temperatures. The reduction metallization degree of SA TTM can be relatively improved by 14.5 and 4.5 pct for the first and second reduction steps, respectively, by 1173 K (900 °C) preoxidation with an optimum time of 30 minutes. Finally, the equilibrium relationship between the metallization degree and the gas reduction potential for TTM ore with preoxidation treatment was built.

Electron transport in reduced graphene oxides in high electric field

NASA Astrophysics Data System (ADS)

Jian, Wen-Bin; Lai, Jian-Jhong; Wang, Sheng-Tsung; Tsao, Rui-Wen; Su, Min-Chia; Tsai, Wei-Yu; Rosenstein, Baruch; Zhou, Xufeng; Liu, Zhaoping

Due to a honeycomb structure, charge carriers in graphene exhibit quasiparticles of linear energy-momentum dispersion and phenomena of Schwinger pair creation may be explored. Because graphene is easily broken in high electric fields, single-layer reduced graphene oxides (rGO) are used instead. The rGO shows a small band gap while it reveals a graphene like behavior in high electric fields. Electron transport in rGO exhibits two-dimensional Mott's variable range hopping. The temperature behavior of resistance in low electric fields and the electric field behavior of resistance at low temperatures are all well explained by the Mott model. At temperatures higher than 200 K, the electric field behavior does not agree with the model while it shows a power law behavior with an exponent of 3/2, being in agreement with the Schwinger model. Comparing with graphene, the rGO is more sustainable to high electric field thus presenting a complete high-electric field behavior. When the rGO is gated away from the charge neutral point, the turn-on electric field of Schwinger phenomena is increased. A summary figure is given to present electric field behaviors and power law variations of resistances of single-layer rGO, graphene, and MoS2.

Behavior of an improved Zr fuel cladding with oxidation resistant coating under loss-of-coolant accident conditions

NASA Astrophysics Data System (ADS)

Park, Dong Jun; Kim, Hyun Gil; Jung, Yang Il; Park, Jung Hwan; Yang, Jae Ho; Koo, Yang Hyun

2016-12-01

This study investigates protective coatings for improving the high temperature oxidation resistance of Zr fuel claddings for light water nuclear reactors. FeCrAl alloy and Cr layers were deposited onto Zr plates and tubes using cold spraying. For the FeCrAl/Zr system, a Mo layer was introduced between the FeCrAl coating and the Zr matrix to prevent inter-diffusion at high temperatures. Both the FeCrAl and Cr coatings improved the oxidation resistance compared to that of the uncoated Zr alloy when exposed to a steam environment at 1200 °C. The ballooning behavior and mechanical properties of the coated cladding samples were studied under simulated loss-of-coolant accident conditions. The coated samples showed higher burst temperatures, lower circumferential strain, and smaller rupture openings compared to the uncoated Zr. Although 4-point bend tests of the coated samples showed a small increase in the maximum load, ring compression tests of a sectioned sample showed increased ductility.

Wear Behavior and Mechanism of a Cr-Mo-V Cast Hot-Working Die Steel

NASA Astrophysics Data System (ADS)

Wei, M. X.; Wang, S. Q.; Zhao, Y. T.; Chen, K. M.; Cui, X. H.

2011-06-01

The wear behavior and mechanisms of a Cr-Mo-V cast hot-working die steel with three microstructures (tempered martensite, troostite, and sorbite) were studied systematically through the dry-sliding wear tests within a normal load range of 50 to 300 N and an ambient temperature range of 298 K to 673 K (25 °C to 400 °C) by a pin-on-disk high-temperature wear machine. Five different mechanisms were observed in the experiments, namely adhesive, abrasive, mild oxidative, oxidative, and extrusive wear; one or more of those mechanisms would be dominant within particular ranges of load and temperature. The transition of wear mechanisms depended on the formation of tribo-oxides, which was related closely to load and temperature, and their delamination, which was mainly influenced by the matrix. By increasing the load and ambient temperature, the protective effect of tribo-oxides first strengthened, then decreased, and in some cases disappeared. Under a load ranging 50 to 300 N at 298 K (25 °C) and a load of 50 N at 473 K (200 °C), adhesive wear was the dominant wear mechanism, and abrasive wear appeared simultaneously. The wear was of mild oxidative type under a load ranging 100 to 300 N at 473 K (200 °C) and a load ranging 50 to 150 N at 673 K (400 °C) for tempered martensite and tempered troostite as well as under a load of 100 N at 473 K (200 °C) and a load ranging 50 to 100 N at 673 K (400 °C) for tempered sorbite. At the load of 200 N or greater, or the temperatures above 673 K (400 °C), oxidative wear (beyond mild oxidative wear) prevailed. When the highest load of 300 N at 673 K (400 °C) was applied, extrusive wear started to dominate for the tempered sorbite.

Modified fused silicide coatings for tantalum (Ta-10W) reentry heat shields

NASA Technical Reports Server (NTRS)

Packer, C. M.; Perkins, R. A.

1973-01-01

Results are presented of a program of research to develop a reliable, high performance, fused slurry silicide coating for the Ta-10W alloy. The effort was directed toward developing new and improved formulations for use at 2600 to 2800 F (1700 to 1811 K) in an atmospheric reentry thermal protection system with a 100-mission capability. Based on a thorough characterization of isothermal and cyclic oxidation behavior, bend transition temperatures, room- and elevated-temperature tensile properties, and creep behavior, a 2.5 Mn-33Ti-64.5Si coating (designated MTS) provides excellent protection for the Ta-10W alloy in simulated reentry environments. An extensive analysis of the oxidation behavior and characteristics of the MTS coating in terms of fundamental mechanisms also is presented.

Kinetics of Cyclic Oxidation and Cracking and Finite Element Analysis of MA956 and Sapphire/MA956 Composite System

NASA Technical Reports Server (NTRS)

Lee, Kang N.; Arya, Vinod K.; Halford, Gary R.; Barrett, Charles A.

1996-01-01

Sapphire fiber-reinforced MA956 composites hold promise for significant weight savings and increased high-temperature structural capability, as compared to unreinforced MA956. As part of an overall assessment of the high-temperature characteristics of this material system, cyclic oxidation behavior was studied at 1093 C and 1204 C. Initially, both sets of coupons exhibited parabolic oxidation kinetics. Later, monolithic MA956 exhibited spallation and a linear weight loss, whereas the composite showed a linear weight gain without spallation. Weight loss of the monolithic MA956 resulted from the linking of a multiplicity of randomly oriented and closely spaced surface cracks that facilitated ready spallation. By contrast, cracking of the composite's oxide layer was nonintersecting and aligned nominally parallel with the orientation of the subsurface reinforcing fibers. Oxidative lifetime of monolithic MA956 was projected from the observed oxidation kinetics. Linear elastic, finite element continuum, and micromechanics analyses were performed on coupons of the monolithic and composite materials. Results of the analyses qualitatively agreed well with the observed oxide cracking and spallation behavior of both the MA956 and the Sapphire/MA956 composite coupons.

Oxide Morphology of a FeCrAl Alloy, Kanthal APMT, following Extended Aging at 300-600C

DOE Office of Scientific and Technical Information (OSTI.GOV)

Li, Nan; Parker, Stephen Scott; Wood, Elizabeth Sooby

Iron-chromium-aluminum (FeCrAl) alloys are of interest to the nuclear materials community due to their resistance to high temperature steam oxidation under accident conditions. The present work investigates oxide formation at temperatures relevant to light water reactor cladding operation following extended aging to assess growth kinetics, chemical composition, and microstructure of oxide formation on a commercial FeCrAl alloy, Fe-21wt.%Cr-5wt.%Al-3wt.%Mo (Kanthal APMT). Aging treatments were performed for 100-1000 hours in stagnant air at 300, 400, 500, and 600 °C, respectively. Oxide growth behavior under the investigated conditions follows a logarithmic time dependence. When the oxidization temperature is 400 °C or below, themore » oxide is amorphous. At 500 °C, isolated crystalline regions start to appear during short period aging time and expand with extended exposures. Crystalline α-Al2O3 oxide film develops at 600 °C and the correlated logarithmic rate constant decreases significantly, indicating enhanced oxidation resistance of the formed oxide film. In addition, Mo segregation at grain boundaries has been observed when the aging temperature exceeds 500 °C. The results of this study can be viewed as an upper bounding result for potential oxide coarsening during reactor operation.« less

Predicting Thermal Behavior of Secondary Organic Aerosols

EPA Science Inventory

Volume concentrations of steady-state secondary organic aerosol (SOA) were measured in 139 steadystate single precursor hydrocarbon oxidation experiments after passing through a temperature controlled inlet tube. Higher temperatures resulted in greater loss of particle volume, wi...

Oxidation of ZrB2-SiC

NASA Technical Reports Server (NTRS)

Opila, Elizabeth J.; Halbig, Michael C.

2001-01-01

In this paper the oxidation behavior of ZrB2-20 vol% SiC is examined. Samples were exposed in stagnant air in a zirconia furnace (Deltech, Inc.) at temperatures of 1327, 1627, and 1927 C for ten ten-minute cycles. Samples were removed from the furnace after one, five, and ten cycles. Oxidized material was characterized by mass change when possible, x-ray diffraction (XRD), scanning electron microscopy (SEM), and energy dispersive spectroscopy (EDS). Oxidation kinetics, oxide scale development, and matrix recession were monitored as a function of time and temperature. Oxidation and recession rates of ZrB2 - 20 vol% SiC were adequately modeled by parabolic kinetics. Oxidation rates of this material are rapid, allowing only very short-term application in air or other high oxygen partial pressure environments.

The catalytic behavior of precisely synthesized Pt–Pd bimetallic catalysts for use as diesel oxidation catalysts

DOE PAGES

Wong, Andrew P.; Kyriakidou, Eleni A.; Toops, Todd J.; ...

2016-04-17

The demands of stricter diesel engine emission regulations have created challenges for current exhaust systems. With advances in low-temperature internal combustion engines and their operations, advances must also be made in vehicle exhaust catalysts. Most current diesel oxidation catalysts use heavy amounts of precious group metals (PGMs) for hydrocarbon (HC), CO, and NO oxidation. These catalysts are expensive and are most often synthesized with poor bimetallic interaction and dispersion. In this paper, the goal was to study the effect of aging on diesel emission abatement of Pt–Pd bimetallic nanoparticles precisely prepared with different morphologies: well dispersed core–shell vs. well dispersedmore » homogeneously alloyed vs. poorly dispersed, poorly alloyed particles. Alumina and silica supports were studied. Particle morphology and dispersion were analyzed before and after hydrothermal treatments by XRD, EDX, and STEM. Reactivity as a function of aging was measured in simulated diesel engine exhaust. While carefully controlled bimetallic catalyst nanoparticle structure has a profound influence on initial or low temperature catalytic activity, the differences in behavior disappear with higher temperature aging as thermodynamic equilibrium is achieved. The metallic character of Pt-rich alumina-supported catalysts is such that behavior rather closely follows the Pt–Pd metal phase diagram. Nanoparticles disparately composed as well-dispersed core–shell (via seq-SEA), well-dispersed homogeneously alloyed (via co-SEA), and poorly dispersed, poorly alloyed (via co-DI) end up as well alloyed, large particles of almost the same size and activity. With Pd-rich systems, the oxidation of Pd also figures into the equilibrium, such that Pd-rich oxide phases appear in the high temperature forms along with alloyed metal cores. Finally, the small differences in activity after high temperature aging can be attributed to the synthesis methods, sequential SEA and co-DI which give rise, after aging, to a bimetallic surface enriched in Pd.« less

Oxidation Characterization of Hafnium-Based Ceramics Fabricated by Hot Pressing and Electric Field-Assisted Sintering

NASA Technical Reports Server (NTRS)

Gasch, Matt; Johnson, Sylvia; Marschall, Jochen

2010-01-01

Ceramic borides, such as hafnium diboride (HfB2) and zirconium diboride (ZrB2), are members of a family of materials with extremely high melting temperatures referred to as Ultra High Temperature Ceramics (UHTCs). UHTCs constitute a class of promising materials for use in high temperature applications, such as sharp leading edges on future-generation hypersonic flight vehicles, because of their high melting points. The controlled development of microstructure has become important to the processing of UHTCs, with the prospect of improving their mechanical and thermal properties. The improved oxidation resistance of HfB2 has also become important if this material is to be successfully used at temperatures above 2000 C. Furthermore, the use of UHTCs on the leading edges of vehicles traveling at hypersonic speeds will mean exposure to a mixed oxidation environment comprised of both molecular and atomic oxygen. The current study has investigated the high-temperature oxidation behavior of HfB2-based materials in a pure O2 environment, as well as in environments containing different levels of dissociated oxygen (O/O2). Materials were processed by two techniques: conventional hot pressing (HP) and electric field-assisted sintering (FAS). Their oxidation behavior was evaluated in both a tube furnace at 1250 C for 3 hours and in a simulated re-entry environment in the Advanced Heating Facility (AHF) arcjet at NASA Ames Research Center, during a 10-minute exposure to a cold wall heat flux of 250W/sq cm and stagnation pressure of 0.1-0.2 atm. The microstructure of the different materials was characterized before and after oxidation using scanning electron microscopy (SEM).

Oxidation Behavior of Carbon Steel: Effect of Formation Temperature and pH of the Environment

NASA Astrophysics Data System (ADS)

Dubey, Vivekanand; Kain, Vivekanand

2017-11-01

The nature of surface oxide formed on carbon steel piping used in nuclear power plants affects flow-accelerated corrosion. In this investigation, carbon steel specimens were oxidized in an autoclave using demineralized water at various temperatures (150-300 °C) and at pH levels (neutral, 9.5). At low temperatures (< 240 °C), weight loss of specimens due to dissolution of iron in water occurred to a greater extent than weight gain due to oxide formation. With the increase in temperature, the extent of iron dissolution reduced and weight gain due to oxide formation increased. A similar trend was observed with the increase in pH as was observed with the increase in temperature. XRD and Raman spectroscopy confirmed the formation of magnetite. The oxide film formed by precipitation process was negligible at temperatures from 150 to 240 °C compared to that at higher temperatures (> 240 °C) as confirmed by scanning electron microscopy. Electrochemical impedance measurement followed by Mott-Schottky analysis indicated an increase in defect density with exposure duration at 150 °C at neutral pH but a low and stable defect density in alkaline environment. The defect density of the oxide formed at neutral pH at 150-300 °C was always higher than that formed in alkaline environment as reported in the literature.

Covalent modification and exfoliation of graphene oxide using ferrocene

NASA Astrophysics Data System (ADS)

Avinash, M. B.; Subrahmanyam, K. S.; Sundarayya, Y.; Govindaraju, T.

2010-09-01

Large scale preparation of single-layer graphene and graphene oxide is of great importance due to their potential applications. We report a simple room temperature method for the exfoliation of graphene oxide using covalent modification of graphene oxide with ferrocene to obtain single-layer graphene oxide sheets. The samples were characterized by FESEM, HRTEM, AFM, EDAX, FT-IR, Raman and Mössbauer spectroscopic studies. HRTEM micrograph of the covalently modified graphene oxide showed increased interlayer spacing of ~2.4 nm due to ferrocene intercalation. The presence of single-layer graphene oxide sheets were confirmed by AFM studies. The covalently modified ferrocene-graphene oxide composite showed interesting magnetic behavior.Large scale preparation of single-layer graphene and graphene oxide is of great importance due to their potential applications. We report a simple room temperature method for the exfoliation of graphene oxide using covalent modification of graphene oxide with ferrocene to obtain single-layer graphene oxide sheets. The samples were characterized by FESEM, HRTEM, AFM, EDAX, FT-IR, Raman and Mössbauer spectroscopic studies. HRTEM micrograph of the covalently modified graphene oxide showed increased interlayer spacing of ~2.4 nm due to ferrocene intercalation. The presence of single-layer graphene oxide sheets were confirmed by AFM studies. The covalently modified ferrocene-graphene oxide composite showed interesting magnetic behavior. Electronic supplementary information (ESI) available: Magnetic data; AFM images; TEM micrographs; and Mössbauer spectroscopic data. See DOI: 10.1039/c0nr00024h

Tensile behavior of glass/ceramic composite materials at elevated temperatures

NASA Technical Reports Server (NTRS)

Mandell, J. F.; Grande, D. H.; Jacobs, J.

1987-01-01

This paper describes the tensile behavior of high-temperature composite materials containing continuous Nicalon ceramic fiber reinforcement and glass and glass/ceramic matrices. The longitudinal properties of these materials can approach theoretical expectations for brittle matrix composites, failing at a strength and ultimate strain level consistent with those of the fibers. The brittle, high-modulus matrices result in a nonlinear stress-strain curve due to the onset of stable matrix cracking at 10 to 30 percent of the fiber strain to failure, and at strains below this range in off-axis plies. Current fibers and matrices can provide attractive properties well above 1000 C, but composites experience embrittlement in oxidizing atmospheres at 800 to 1000 C due to oxidation of a carbon interface reaction layer.The oxidation effect greatly increases the interface bond strength, causing composite embrittlement.

Synthesis and characterization of nickel oxide particulate annealed at different temperatures

NASA Astrophysics Data System (ADS)

Sharma, Khem Raj; Thakur, Shilpa; Negi, N. S.

2018-04-01

Nickel oxide has been synthesized by solution combustion technique. The nickel oxide ceramic was annealed at 600°C and 1000°C for 2 hours. Structural, electrical, dielectric and magnetic properties were analyzed which are strongly dependent upon the synthesis method. Structural properties were examined by X-ray diffractometer (XRD), which confirmed the purity and cubic phase of nickel oxide. XRD data reveals the increase in crystallite size and decrease in full width half maximum (FWHM) as the annealing temperature increases. Electrical conductivity is found to increase from 10-6 to 10-5 (Ω-1cm-1) after annealing. Dielectric constant is observed to increase from 26 to 175 when the annealing temperature is increased from 600°C to 1000°C. Low value of coercive field is found which shows weak ferromagnetic behavior of NiO. It is observed that all the properties of NiO particulate improve with increasing annealing temperature.

Bipolar resistive switching in room temperature grown disordered vanadium oxide thin-film devices

NASA Astrophysics Data System (ADS)

Wong, Franklin J.; Sriram, Tirunelveli S.; Smith, Brian R.; Ramanathan, Shriram

2013-09-01

We demonstrate bipolar switching with high OFF/ON resistance ratios (>104) in Pt/vanadium oxide/Cu structures deposited entirely at room temperature. The SET (RESET) process occurs when negative (positive) bias is applied to the top Cu electrode. The vanadium oxide (VOx) films are amorphous and close to the vanadium pentoxide stoichiometry. We also investigated Cu/VOx/W structures, reversing the position of the Cu electrode, and found the same polarity dependence with respect to the top and bottom electrodes, which suggests that the bipolar nature is linked to the VOx layer itself. Bipolar switching can be observed at 100 °C, indicating that it not due to a temperature-induced metal-insulator transition of a vanadium dioxide second phase. We discuss how ionic drift can lead to the bipolar electrical behavior of our junctions, similar to those observed in devices based on several other defective oxides. Such low-temperature processed oxide switches could be of relevance to back-end or package integration processing schemes.

Electronic Structure at Oxide Interfaces

DTIC Science & Technology

2014-06-01

of materials with desired correlated electron properties such as ferromagnetism with a high Curie temperature, high transition temperature...approximation and therefore the canonical Mott picture is unable to account for the insulating behavior of these materials . We resolve this apparent...the two materials . LaTiO3 shows insulating behavior with a small excitation gap set by Ti d-d transitions and a wide energy separation between Ti d

Estimation of ring tensile properties of steam oxidized Zircaloy-4 fuel cladding under simulated LOCA condition

NASA Astrophysics Data System (ADS)

Shriwastaw, R. S.; Sawarn, Tapan K.; Banerjee, Suparna; Rath, B. N.; Dubey, J. S.; Kumar, Sunil; Singh, J. L.; Bhasin, Vivek

2017-09-01

The present study involves the estimation of ring tensile properties of Indian Pressurised Heavy Water Reactor (IPHWR) fuel cladding made of Zircaloy-4, subjected to experiments under a simulated loss-of-coolant-accident (LOCA) condition. Isothermal steam oxidation experiments were conducted on clad tube specimens at temperatures ranging from 900 to 1200 °C at an interval of 50 °C for different soaking periods with subsequent quenching in water at ambient temperature. The specimens, which survived quenching, were then subjected to ambient temperature ring tension test (RTT). The microstructure was correlated with the mechanical properties. The yield strength (YS) and ultimate tensile strength (UTS) increased initially with rise in oxidation temperature and time duration but then decreased with further increase in oxidation. Ductility is adversely affected with rising oxidation temperature and longer holding time. A higher fraction of load bearing phase and lower oxygen content in it ensures higher residual ductility. Cladding shows almost zero ductility behavior in RIT when load bearing phase fraction is less than 0.72 and its average oxygen concentration is greater than 0.58 wt%.

Oxidation of C/SiC Composites at Reduced Oxygen Partial Pressures

NASA Technical Reports Server (NTRS)

Opila, E. J.; Serra, J. L.

2007-01-01

T-300 carbon fibers and T-300 carbon fiber reinforced silicon carbide composites (C/SiC) were oxidized in flowing reduced oxygen partial pressure environments at a total pressure of one atmosphere (0.5 atm O2, 0.05 atm O2 and 0.005 atm O2, balance argon). Experiments were conducted at four temperatures (816deg, 1149deg, 1343deg, and 1538 C). The oxidation kinetics were monitored using thermogravimetric analysis. T-300 fibers were oxidized to completion for times between 0.6 and 90 h. Results indicated that fiber oxidation kinetics were gas phase diffusion controlled. Oxidation rates had an oxygen partial pressure dependence with a power law exponent close to one. In addition, oxidation rates were only weakly dependent on temperature. The C/SiC coupon oxidation kinetics showed some variability, attributed to differences in the number and width of cracks in the SiC seal coat. In general, weight losses were observed indicating oxidation of the carbon fibers dominated the oxidation behavior. Low temperatures and high oxygen pressures resulted in the most rapid consumption of the carbon fibers. At higher temperatures, the lower oxidation rates were primarily attributed to crack closure due to SiC thermal expansion, rather than oxidation of SiC since these reduced rates were observed even at the lowest oxygen partial pressures where SiC oxidation is minimal.

High temperature behavior of B2-based ruthenium aluminide systems

NASA Astrophysics Data System (ADS)

Cao, Fang

Ru-modified NiAl-based bond coats have the potential to improve the durability of Superalloy-Thermal Barrier Coating systems (TBCs) for advanced gas turbine engines. A fundamental understanding of the high temperature mechanical behavior across the Ni-Al-Ru B2 phase field can provide direction for the development of these new bond coats for TBCs. The purpose of this study has been to describe the fundamental processes of creep deformation in single phase B2 Ru-Al-Ni ternary alloys which would form the basis for the bond coats. To accomplish this, five ternary alloys with compositions located within the B2 field across the NiAl-RuAl phase region were fabricated and investigated. Special emphasis was placed on characterizing creep deformation and describing the operative creep mechanisms in these alloys. At room temperature, brittle failure was observed in the Ni-rich alloys in compression, while improved strength and ductility were displayed in two Ru-rich ternary alloys at temperatures up to 700°C. Exceptional creep strength was observed in these alloys, as compared to other high melting temperature B2 intermetallics. A continuous increase of the melting temperature and creep resistance with the increasing of the Ru/Ni ratio in these alloys was observed. Post-creep dislocation analyses identified the presence of <100> and <110> edge dislocations in the Ni-rich alloys, while uniformly distributed jogged <100> screw dislocations predominated in the Ru-rich ternary alloys. A transition of the creep mechanism from viscous glide controlled to jogged screw motion in these Ru-Al-Ni ternary B2 alloys with increasing Ru/Ni ratio is demonstrated by the characteristics of the creep deformation process, stress change creep tests, post-creep dislocation analyses, and numerical modeling. Additionally, the knowledge of the cyclic oxidation behavior of ruthenium aluminide-based alloy is essential, as many high-temperature applications for which this intermetallic might be utilized undergo repeated severe thermal cycling. Thus the second portion of this thesis focuses on the characterization of the cyclic oxidation properties of RuAl-based alloys. The cyclic oxidation behavior of six RuAl-based alloys was studied in air over the temperature range of 1000°C to 1300°C. Oxidation kinetics have been shown to be influenced by microstructure as well as the addition of platinum.

Oxidation effects on the mechanical properties of SiC fiber-reinforced reaction-bonded silicon nitride matrix composites

NASA Technical Reports Server (NTRS)

Bhatt, Ramakrishna T.

1989-01-01

The room temperature mechanical properties of SiC fiber reinforced reaction bonded silicon nitride composites were measured after 100 hrs exposure at temperatures to 1400 C in nitrogen and oxygen environments. The composites consisted of approx. 30 vol percent uniaxially aligned 142 micron diameter SiC fibers in a reaction bonded Si3N4 matrix. The results indicate that composites heat treated in a nitrogen environment at temperatures to 1400 C showed deformation and fracture behavior equivalent to that of the as-fabricated composites. Also, the composites heat treated in an oxidizing environment beyond 400 C yielded significantly lower tensile strength values. Specifically in the temperature range from 600 to 1000 C, composites retained approx. 40 percent of their as-fabricated strength, and those heat treated in the temperatures from 1200 to 1400 C retained 70 percent. Nonetheless, for all oxygen heat treatment conditions, composite specimens displayed strain capability beyond the matrix fracture stress; a typical behavior of a tough composite.

Oxidation of U-20 at% Zr alloy in air at 423 1063 K

NASA Astrophysics Data System (ADS)

Matsui, Tsuneo; Yamada, Takanobu; Ikai, Yasushi; Naito, Keiji

1993-01-01

The oxidation behavior of U 0.80Zr 0.20 alloy (two-phase mixture of U and UZr 2 below 878 K and single solid solution above 1008 K) was studied by thermogravimetry in the temperature range from 423 to 1063 K in air. During oxidation in the low temperature region (423-503 K), the sample kept its initial shape (a rectangular rod) and the surface of the sample was covered by a black thin adherent UO2 + x oxide layer. On the other hand, by oxidation in the middle temperature region, the sample broke to several pieces of thin plates and blocks, and fine powder at 643-723 K and entirely to fine powder at 775-878 K, all of which were analyzed to be a mixture of U 3O 8 and ZrO 2. By oxidation in the high temperature region (1008-1063 K) the sample broke to very fine powder, which consisted of U 3O 8 and ZrO 2. Based on the sample shape, the oxide phase identified after oxidation and the slope value of the bilogarithmic plots of the weight gain against time, the oxidation kinetics was analyzed with a paralinear equation in the low temperature region below 503 K and a linear equation in the middle and high temperature regions above 643 K. Oxidation rates of U 0.80Zr 0.20 (two-phase mixture) in the low and middle temperature regions were smaller than those of uranium metal. A discontinuity in the plot of the linear oxidation rate constant versus reciprocal temperature was found to be present between 723 and 838 K, similarly to the case of uranium metal previously reported. The linear rate constants of single-phase solid solution in the high temperature region above 1008 K seemed to be a little smaller than those estimated by the extrapolation of the values in the middle temperature region.

A Comparative Study of Cyclic Oxidation and Sulfates-Induced Hot Corrosion Behavior of Arc-Sprayed Ni-Cr-Ti Coatings at Moderate Temperatures

NASA Astrophysics Data System (ADS)

Guo, Wenmin; Wu, Yuping; Zhang, Jianfeng; Hong, Sheng; Chen, Liyan; Qin, Yujiao

2015-06-01

The cyclic oxidation and sulfates-induced hot corrosion behaviors of a Ni-43Cr-0.3Ti arc-sprayed coating at 550-750 °C were characterized and compared in this study. In general, all the oxidation and hot corrosion kinetic curves of the coating followed a parabolic law, i.e., the weight of the specimens showed a rapid growth initially and then reached the gradual state. However, the initial stage of the hot corrosion process was approximately two times longer than that of the oxidation process, indicating a longer preparation time required for the formation of a protective scale in the former process. At 650 °C, the parabolic rate constant for the hot corrosion was 7.2 × 10-12 g2/(cm4·s), approximately 1.7 times higher than that for the oxidation at the same temperature. The lower parabolic rate constant for the oxidation was mainly attributed to the formation of a protective oxide scale on the surface of corroded specimens, which was composed of a mixture of NiO, Cr2O3, and NiCr2O4. However, as the liquid molten salts emerged during the hot corrosion, these protective oxides would be dissolved and the coating was corrupted acceleratedly.

Thermal-Mechanical Stability of Single Crystal Oxide Refractive Concentrators for High-Temperature Solar Thermal Propulsion

NASA Technical Reports Server (NTRS)

Zhu, Dongming; Jacobson, Nathan S.; Miller, Robert A.

1999-01-01

Single crystal oxides such as yttria-stabilized zirconia (Y2O3-ZrO2), yttrium aluminum garnet (Y3Al5O12, or YAG), magnesium oxide (MgO) and sapphire (Al2O3) are candidate refractive secondary concentrator materials for high temperature solar propulsion applications. However, thermo-mechanical reliability of these components in severe thermal environments during the space mission sun/shade transition is of great concern. Simulated mission tests are important for evaluating these candidate oxide materials under a variety of transient and steady-state heat flux conditions, and thus provide vital information for the component design. In this paper, a controlled heat flux thermal shock test approach is established for the single crystal oxide materials using a 3.0 kW continuous wave CO2 laser, with a wavelength 10.6 micron. Thermal fracture behavior and failure mechanisms of these oxide materials are investigated and critical temperature gradients are determined under various temperature and heating conditions. The test results show that single crystal sapphire is able to sustain the highest temperature gradient and heating-cooling rate, and thus exhibit the best thermal shock resistance, as compared to the yttria-stabilized zirconia, yttrium aluminum garnet and magnesium oxide.

Thermal-Mechanical Stability of Single Crystal Oxide Refractive Concentrators for High-Temperature Solar Thermal Propulsion

NASA Technical Reports Server (NTRS)

Zhu, Dongming; Jacobson, Nathan S.; Miller, Robert A.

1999-01-01

Single crystal oxides such as yttria-stabilized zirconia (Y2O3-ZrO2), yttrium aluminum garnet (Y3Al5O12, or YAG), magnesium oxide (MgO) and sapphire (Al2O3) are candidate refractive secondary concentrator materials for high temperature solar propulsion applications. However, thermo-mechanical reliability of these components in severe thermal environments during the space mission sun/shade transition is of great concern. Simulated mission tests are important for evaluating these candidate oxide materials under a variety of transient and steady-state heat flux conditions, and thus provide vital information for the component design. In this paper, a controlled heat flux thermal shock test approach is established for the single crystal oxide materials using a 3.0 kW continuous wave CO2 laser, with a wavelength 10.6 micron. Thermal fracture behavior and failure mechanisms of these oxide materials are investigated and critical temperature gradients are determined under various temperature and heating conditions. The test results show that single crystal sapphire is able to sustain the highest temperature gradient and heating-cooling rate, and thus exhibit the best thermal shock resistance, as compared to the yttria-stabilized zirconia, yttrium aluminum garnet, and magnesium oxide.

A novel approach to model the transient behavior of solid-oxide fuel cell stacks

NASA Astrophysics Data System (ADS)

Menon, Vikram; Janardhanan, Vinod M.; Tischer, Steffen; Deutschmann, Olaf

2012-09-01

This paper presents a novel approach to model the transient behavior of solid-oxide fuel cell (SOFC) stacks in two and three dimensions. A hierarchical model is developed by decoupling the temperature of the solid phase from the fluid phase. The solution of the temperature field is considered as an elliptic problem, while each channel within the stack is modeled as a marching problem. This paper presents the numerical model and cluster algorithm for coupling between the solid phase and fluid phase. For demonstration purposes, results are presented for a stack operated on pre-reformed hydrocarbon fuel. Transient response to load changes is studied by introducing step changes in cell potential and current. Furthermore, the effect of boundary conditions and stack materials on response time and internal temperature distribution is investigated.

Characterization of Thermal Stability and High-Temperature Tribological Behavior of Electroless Ni-B Coating

NASA Astrophysics Data System (ADS)

Pal, Soupitak; Sarkar, Rohit; Jayaram, Vikram

2018-05-01

A preliminary study has been conducted using sequences of isothermal heat treatments and unidirectional high-temperature wear test following ball-on-flat geometry against an alumina counterface, to assess thermal stability and high-temperature tribological properties of the crystalline electroless Ni-B coating, a potential candidate for high-temperature solid lubricant coating. Isothermal heat treatment of 450 °C/15 h causes a significant amount of B diffusion into the Fe substrate without altering the coating's through-thickness hardness and nanostructure. At room temperature, a very low wear rate is observed, which increases up to two orders of magnitude above a testing temperature of 100 °C. Room-temperature wear behavior is mostly governed by oxidative wear, where friction-induced heating produces a thick oxide scale on the wear track, which subsequently decreases the wear rate by preventing direct contact between the coating and counterface. In the case of wear tests above 100 °C, removal of the same oxide layer occurs through local plastic deformation, essentially plastic ratcheting at the contacting region by flow softening of the contacting surface layer due to a local rise in temperature. Worn track morphology shows similarity with the severe wear seen in steel-steel contacts. Experimental observations have been explained and validated using the concept of contact point flash temperature. A quantitative assessment of contact point flash temperature has been carried out adopting the methodology, proposed by Ashby et al. The effects of applied normal load, test geometry, choice of counterface material, and testing temperatures on the transition of wear mechanism are critically discussed.

Effect of Surface Preparation on the 815°C Oxidation of Single-Crystal Nickel-Based Superalloys

NASA Astrophysics Data System (ADS)

Sudbrack, Chantal K.; Beckett, Devon L.; MacKay, Rebecca A.

2015-11-01

A primary application for single-crystal superalloys has been jet engine turbine blades, where operation temperatures reach well above 1000°C. The NASA Glenn Research Center is considering use of single-crystal alloys for future, lower temperature application in the rims of jet engine turbine disks. Mechanical and environmental properties required for potential disk rim operation at 815°C are being examined, including the oxidation and corrosion behavior, where there is little documentation at intermediate temperatures. In this study, single-crystal superalloys, LDS-1101+Hf and CMSX-4+Y, were prepared with different surface finishes and compared after isothermal and cyclic oxidation exposures. Surface finish has a clear effect on oxide formation at 815°C. Machined low-stress ground surfaces after exposure for 440 h produce thin Al2O3 external scales, which is consistent with higher temperature oxidation, whereas polished surfaces with a mirror finish yield much thicker NiO external scales with subscale of Cr2O3-spinel-Al2O3, which may offer less reliable oxidation resistance. Additional experiments separate the roles of cold-work, localized deformation, and the extent of polishing and surface roughness on oxide formation.

A high-throughput investigation of Fe-Cr-Al as a novel high-temperature coating for nuclear cladding materials.

PubMed

Bunn, Jonathan Kenneth; Fang, Randy L; Albing, Mark R; Mehta, Apurva; Kramer, Matthew J; Besser, Matthew F; Hattrick-Simpers, Jason R

2015-07-10

High-temperature alloy coatings that can resist oxidation are urgently needed as nuclear cladding materials to mitigate the danger of hydrogen explosions during meltdown. Here we apply a combination of computationally guided materials synthesis, high-throughput structural characterization and data analysis tools to investigate the feasibility of coatings from the Fe–Cr–Al alloy system. Composition-spread samples were synthesized to cover the region of the phase diagram previous bulk studies have identified as forming protective oxides. The metallurgical and oxide phase evolution were studied via in situ synchrotron glancing incidence x-ray diffraction at temperatures up to 690 K. A composition region with an Al concentration greater than 3.08 at%, and between 20.0 at% and 32.9 at% Cr showed the least overall oxide growth. Subsequently, a series of samples were deposited on stubs and their oxidation behavior at 1373 K was observed. The continued presence of a passivating oxide was confirmed in this region over a period of 6 h.

Oxide Morphology of a FeCrAl Alloy, Kanthal APMT, Following Extended Aging in Air at 300 °C to 600 °C

NASA Astrophysics Data System (ADS)

Li, Nan; Parker, Stephen S.; Wood, Elizabeth S.; Nelson, Andrew T.

2018-05-01

Iron-chromium-aluminum (FeCrAl) alloys are of interest to the nuclear materials community due to their resistance to high-temperature steam oxidation under accident conditions. The present work investigates oxide formation at temperatures relevant to light water reactor cladding operation following extended aging to assess growth kinetics, chemical composition, and microstructure of oxide formation on a commercial FeCrAl alloy, Fe-21 wt pct Cr-5 wt pct Al-3 wt pct Mo (Kanthal APMT). Aging treatments were performed for 100 to 1000 hours in stagnant air at 300 °C, 400 °C, 500 °C, and 600 °C, respectively. Oxide growth behavior under the investigated conditions follows a logarithmic time dependence. When the oxidization temperature is 400 °C or below, the oxide is amorphous. At 500 °C, isolated crystalline regions start to appear during short period aging time and expand with extended exposures. Crystalline α-Al2O3 oxide film develops at 600 °C and the correlated logarithmic rate constant decreases significantly, indicating enhanced oxidation resistance of the formed oxide film. In addition, Mo segregation at grain boundaries has been observed when the aging temperature exceeds 500 °C. The results of this study can be viewed as an upper bounding result for potential oxide coarsening during reactor operation.

Oxide Morphology of a FeCrAl Alloy, Kanthal APMT, Following Extended Aging in Air at 300 °C to 600 °C

NASA Astrophysics Data System (ADS)

Li, Nan; Parker, Stephen S.; Wood, Elizabeth S.; Nelson, Andrew T.

2018-07-01

Iron-chromium-aluminum (FeCrAl) alloys are of interest to the nuclear materials community due to their resistance to high-temperature steam oxidation under accident conditions. The present work investigates oxide formation at temperatures relevant to light water reactor cladding operation following extended aging to assess growth kinetics, chemical composition, and microstructure of oxide formation on a commercial FeCrAl alloy, Fe-21 wt pct Cr-5 wt pct Al-3 wt pct Mo (Kanthal APMT). Aging treatments were performed for 100 to 1000 hours in stagnant air at 300 °C, 400 °C, 500 °C, and 600 °C, respectively. Oxide growth behavior under the investigated conditions follows a logarithmic time dependence. When the oxidization temperature is 400 °C or below, the oxide is amorphous. At 500 °C, isolated crystalline regions start to appear during short period aging time and expand with extended exposures. Crystalline α-Al2O3 oxide film develops at 600 °C and the correlated logarithmic rate constant decreases significantly, indicating enhanced oxidation resistance of the formed oxide film. In addition, Mo segregation at grain boundaries has been observed when the aging temperature exceeds 500 °C. The results of this study can be viewed as an upper bounding result for potential oxide coarsening during reactor operation.

Effect of temperature and dissolved oxygen on stress corrosion cracking behavior of P92 ferritic-martensitic steel in supercritical water environment

NASA Astrophysics Data System (ADS)

Zhang, Z.; Hu, Z. F.; Zhang, L. F.; Chen, K.; Singh, P. M.

2018-01-01

The effect of temperature and dissolved oxygen (DO) on stress corrosion cracking (SCC) of P92 martensitic steel in supercritical water (SCW) was investigated using slow strain rate test (SSRT) and fractography analysis. The SSRT was carried out at temperatures of 400, 500, 600 °C in deaerated supercritical water and at DO contents of 0, 200, 500 ppb at the temperature of 600 °C, respectively. The results of SSRT show that the decrease of ductility at the temperature of 400 °C may be related to the dynamic strain aging (DSA) of P92 steel. The degradation of the mechanical properties in SCW is the joint effect of temperature and SCC. Compared with the effect of temperature, DO in SCW has no significant effect on the SCC susceptibility of P92 steel. The observation of oxide layer shows that large numbers of pores are nucleated in the oxide layer, which is related to vacancy accumulation and hydrogen generated in the oxide layer. Under the combined action of the growth stress and tensile stress, micro cracks, nucleated from the pores in the oxide layer, are easily propagated intergranularly outward to the surface of specimen, and fewer cracks can extend inward along the intrinsic pores to the inner oxide/metal interface, which is the reason for the exfoliation of oxide films.

Cyclic Oxidation Testing and Modelling: A NASA Lewis Perspective

NASA Technical Reports Server (NTRS)

Smialek, J. L.; Nesbitt, J. A.; Barrett, C. A.; Lowell, C. E.

2000-01-01

The Materials Division of the NASA Lewis Research Center has been heavily involved in the cyclic oxidation of high temperature materials for 30 years. Cyclic furnace and burner rig apparati have been developed, refined, and replicated to provide a large scale facility capable of evaluating many materials by a standard technique. Material behavior is characterized by weight change data obtained throughout the test, which has been modelled in a step-wise process of scale growth and spallation. This model and a coupled diffusion model have successfully described cyclic behavior for a number of systems and have provided insights regarding life prediction and variations in the spalling process. Performance ranking and mechanistic studies are discussed primarily for superalloys and coating alloys. Similar cyclic oxidation studies have been performed on steels, intermetallic compounds, thermal barrier coatings, ceramics, and ceramic composites. The most common oxidation test was performed in air at temperatures ranging from 800 deg. to 1600 C, for times up to 10000 h, and for cycle durations of 0.1 to 1000 h. Less controlled, but important, test parameters are the cooling temperature and humidity level. Heating and cooling rates are not likely to affect scale spallation. Broad experience has usually allowed for considerable focus and simplification of these test parameters, while still revealing the principal aspects of material behavior and performance. Extensive testing has been performed to statistically model the compositional effects of experimental alloys and to construct a comprehensive database of complex commercial alloys.

Thermal and Irradiation Creep Behavior of a Titanium Aluminide in Advanced Nuclear Plant Environments

NASA Astrophysics Data System (ADS)

Magnusson, Per; Chen, Jiachao; Hoffelner, Wolfgang

2009-12-01

Titanium aluminides are well-accepted elevated temperature materials. In conventional applications, their poor oxidation resistance limits the maximum operating temperature. Advanced reactors operate in nonoxidizing environments. This could enlarge the applicability of these materials to higher temperatures. The behavior of a cast gamma-alpha-2 TiAl was investigated under thermal and irradiation conditions. Irradiation creep was studied in beam using helium implantation. Dog-bone samples of dimensions 10 × 2 × 0.2 mm3 were investigated in a temperature range of 300 °C to 500 °C under irradiation, and significant creep strains were detected. At temperatures above 500 °C, thermal creep becomes the predominant mechanism. Thermal creep was investigated at temperatures up to 900 °C without irradiation with samples of the same geometry. The results are compared with other materials considered for advanced fission applications. These are a ferritic oxide-dispersion-strengthened material (PM2000) and the nickel-base superalloy IN617. A better thermal creep behavior than IN617 was found in the entire temperature range. Up to 900 °C, the expected 104 hour stress rupture properties exceeded even those of the ODS alloy. The irradiation creep performance of the titanium aluminide was comparable with the ODS steels. For IN617, no irradiation creep experiments were performed due to the expected low irradiation resistance (swelling, helium embrittlement) of nickel-base alloys.

Ce(x)O(y)⁻ (x = 2-3) + D₂O reactions: stoichiometric cluster formation from deuteroxide decomposition and anti-Arrhenius behavior.

PubMed

Felton, Jeremy A; Ray, Manisha; Waller, Sarah E; Kafader, Jared O; Jarrold, Caroline Chick

2014-10-30

Reactions between small cerium oxide cluster anions and deuterated water were monitored as a function of both water concentration and temperature in order to determine the temperature dependence of the rate constants. Sequential oxidation reactions of the Ce(x)O(y)⁻ (x = 2, 3) suboxide cluster anions were found to exhibit anti-Arrhenius behavior, with activation energies ranging from 0 to -18 kJ mol⁻¹. Direct oxidation of species up to y = x was observed, after which, -OD abstraction and D₂O addition reactions were observed. However, the stoichiometric Ce₂O₄⁻ and Ce₃O₆⁻ cluster anions also emerge in reactions between D₂O and the respective precursors, Ce₂O₃D⁻ and Ce₃O₅D₂⁻. Ce₂O₄⁻ and Ce₃O₆⁻ product intensities diminish relative to deuteroxide complex intensities with increasing temperature. The kinetics of these reactions are compared to the kinetics of the previously studied Mo(x)O(y)⁻ and W(x)O(y)⁻ reactions with water, and the possible implications for the reaction mechanisms are discussed.

Magnetite solubility and phase stability in alkaline media at elevated temperatures

DOE Office of Scientific and Technical Information (OSTI.GOV)

Ziemniak, S.E.; Jones, M.E.; Combs, K.E.S.

Magnetite, Fe{sub 3}O{sub 4}, is the dominant oxide constituent of the indigenous corrosion layers that form on iron base alloys in high purity, high temperature water. The apparent simultaneous stability of two distinct oxidation states of iron in this metal oxide is responsible for its unique solubility behavior. The present work was undertaken to extend the experimental and theoretical bases for estimating solubilities of an iron corrosion product (Fe{sub 3}O{sub 4}/Fe(OH){sub 2}) over a broader temperature range and in the presence of complexing, pH-controlling reagents. These results indicate that a surface layer of ferrous hydroxide controls magnetite solubility behavior atmore » low temperatures in much the same manner as a surface layer of nickel(II) hydroxide was previously reported to control the low temperature solubility behavior of NiO. The importance of Fe(III) ion complexes implies not only that most previously-derived thermodynamic properties of the Fe(OH){sub 3}{sup {minus}} ion are incorrect, but that magnetite phase stability probably shifts to favor a sodium ferric hydroxyphosphate compound in alkaline sodium phosphate solutions at elevated temperatures. The test methodology involved pumping alkaline solutions of known composition through a bed of Fe{sub 3}O{sub 4} granules and analyzing the emerging solution for Fe. Two pH-controlling reagents were tested: sodium phosphate and ammonia. Equilibria for the following reactions were described in thermodynamic terms: (a) Fe(OH){sub 2}/Fe{sub 3}O{sub 4} dissolution and transformation, (b) Fe(II) and Fe(III) ion hydroxocomplex formation (hydrolysis), (c) Fe(II) ion amminocomplex formation, and (d) Fe(II) and Fe(III) ion phosphatocomplex formation. 36 refs.« less

Investigation of the oxidation behavior of dispersion stabilized alloys when exposed to a dynamic high temperature environment

NASA Technical Reports Server (NTRS)

Tenney, D. R.

1974-01-01

The oxidation behavior of TD-NiCr and TD-NiCrAlY alloys have been studied at 2000 and 2200 F in static and high speed flowing air environments. The TD-NiCrAlY alloys preoxidized to produce an Al2O3 scale on the surface showed good oxidation resistance in both types of environments. The TD-NiCr alloy which had a Cr2O3 oxide scale after preoxidation was found to oxidize more than an order of magnitude faster under the dynamic test conditions than at comparable static test conditions. Although Cr2O3 normally provides good oxidation protection, it was rapidly lost due to formation of volatile CrO3 when exposed to the high speed air stream. The preferred oxide arrangement for the dynamic test consisted of an external layer of NiO with a porous mushroom type morphology, an intermediate duplex layer of NiO and Cr2O3, and a continuous inner layer of Cr2O3 in contact with the alloy substrate. An oxidation model has been developed to explain the observed microstructure and overall oxidation behavior of all alloys.

Effect of niobium alloying level on the oxidation behavior of titanium aluminides at 850°C

NASA Astrophysics Data System (ADS)

Banu, Alexandra; Marcu, Maria; Petrescu, Simona; Ionescu, Nicolae; Paraschiv, Alexandru

2016-12-01

This work addresses the alloying of titanium aluminides used in aircraft engine applications and automobiles. The oxidation resistance behavior of two titanium aluminides of α2 + γ(Ti3Al + TiAl) and orthorhombic Ti2NbAl, recognized as candidates for high-temperature applications, was investigated by exposure of the alloys for 100 h in air. Thus, oxidation resistance was expressed as the mass gain rate, whereas surface aspects were analyzed using scanning electron microscopy in conjunction with energy-dispersive X-ray spectroscopy, and the type of oxidation products was analyzed by X-ray diffraction and Raman spectroscopy. The orthorhombic Ti2NbAl alloy was embrittled, and pores and microcracks were formed as a result of oxygen diffusion through the external oxide layer formed during thermal oxidation for 100 h.

Processing, microstructure evolution and properties of nanoscale aluminum alloys

NASA Astrophysics Data System (ADS)

Han, Jixiong

In this project, phase transformations and precipitation behavior in age-hardenable nanoscale materials systems, using Al-Cu alloys as model materials, were first studied. The Al-Cu nanoparticles were synthesized by a Plasma Ablation process and found to contain a 2˜5 nm thick adherent aluminum oxide scale, which prevented further oxidation. On aging of the particles, a precipitation sequence consisting of, nearly pure Cu precipitates to the metastable theta' to equilibrium theta was observed, with all three forming along the oxide-particle interface. The structure of theta' and its interface with the Al matrix has been characterized in detail. Ultrafine Al-Cu nanoparticles (5˜25 nm) were also synthesized by inert gas condensation (IGC) and their aging behavior was studied. These particles were found to be quite stable against precipitation. Secondly, pure Al nanoparticles were prepared by the Exploding Wire process and their sintering and consolidation behavior were studied. It was found that nanopowders of Al could be processed to bulk structures with high hardness and density. Sintering temperature was found to have a dominant effect on density, hardness and microstructure. Sintering at temperatures >600°C led to breakup of the oxide scale, leading to an interesting nanocomposite composed of 100˜200 nm Al oxide dispersed in a bimodal nanometer-micrometer size Al matrix grains. Although there was some grain growth, the randomly dispersed oxide fragments were quite effective in pinning the Al grain boundaries, preventing excessive grain growth and retaining high hardness. Cold rolling and hot rolling were effective methods for attaining full densification and high hardness. Thirdly, the microstructure evolution and mechanical behavior of Al-Al 2O3 nanocomposites were studied. The composites can retain high strength at elevated temperature and thermal soaking has practically no detrimental effect on strength. Although the ductility of the composite remains quite low, there was substantial evidence for high localized plasticity. The strengthening mechanisms of the composite include: Orowan strengthening, grain size strengthening and Forest strengthening. Finally, the microstructure evolution and mechanical behavior of 2024Al-Al 2O3 nanocomposites were studied. This 2024Al-Al2O 3 composite exhibits similar thermal stability and high strength at elevated temperature as Al-Al2O3. On aging, the matrix of 2024Al-Al2O3 composites revealed a precipitation sequence of: alphaAl → GP/GPB → theta'/S' → theta/S. The strengthening mechanisms of the 2024Al-Al2O3 composites include precipitation strengthening, Orowan strengthening, grain size strengthening and Forest strengthening.

Oxidation of nickel-aluminum and iron-aluminum alloys

DOE Office of Scientific and Technical Information (OSTI.GOV)

Cathcart, J.V.

1984-01-01

The high-temperature oxidation behavior of several ordered alloys in the Ni-Al and Fe-Al systems is reviewed with special emphasis on Ni/sub 3/Al and NiAl. Ordering influences oxidation through its effect on the activities of the alloy components and by changing the point defect concentration in an alloy. Three categories of Ni-Al alloys are distinguished based on Al content and oxidation behavior. A characteristic feature of the oxidation of high-aluminum Ni-Al and Fe-Al alloys is the formation of voids in the substrate at the oxide-metal interface. The mechanism of void formation and its suppression by minor additions of oxygen-active elements aremore » discussed. A brief description of the effect of pre-oxidation on the reactions of Ni/sub 3/Al-base alloys in SO/sub 2//O/sub 2/ environments is also included.« less

Cyclic Oxidation Behavior of Simulated Post-Weld Heat-Treated P91

NASA Astrophysics Data System (ADS)

Rajendran Pillai, S.; Dayal, R. K.

2011-10-01

For long-term service life it is desirable that the high-temperature components posses slow-growing oxide scale. The growth and degradation of the oxide scale on P91 were studied by a thermal cycling method. The oxidation temperature was 780 °C and the duration of each cycle was 2 h. The mass gain and integrity of the scale was examined using a thermogravimetric balance. Any lack of integrity is monitored by the transient mass gain associated with the exposure of fresh surface. The scale retained the integrity throughout 100 cycles. Post-oxidation examination was carried out by scanning electron microscopy, energy dispersive spectroscopy and laser Raman spectroscopy. The nature of the scale was characterized and the reason for the compositional segregation is analyzed.

Exfoliation Propensity of Oxide Scale in Heat Exchangers Used for Supercritical CO2 Power Cycles

DOE Office of Scientific and Technical Information (OSTI.GOV)

Sabau, Adrian S; Shingledecker, John P.; Kung, Steve

2016-01-01

Supercritical CO2 (sCO2) Brayton cycle systems offer the possibility of improved efficiency in future fossil energy power generation plants operating at temperatures of 650 C and above. As there are few data on the oxidation/corrosion behavior of structural alloys in sCO2 at these temperatures, modeling to predict the propensity for oxide exfoliation is not well developed, thus hindering materials selection for these novel cycles. The ultimate goal of this effort is to provide needed data on scale exfoliation behavior in sCO2 for confident alloy selection. To date, a model developed by ORNL and EPRI for the exfoliation of oxide scalesmore » formed on boiler tubes in high-temperature, high-pressure steam has proven useful for managing exfoliation in conventional steam plants. A major input provided by the model is the ability to predict the likelihood of scale failure and loss based on understanding of the evolution of the oxide morphologies and the conditions that result in susceptibility to exfoliation. This paper describes initial steps taken to extend the existing model for exfoliation of steam-side oxide scales to sCO2 conditions. The main differences between high-temperature, high-pressure steam and sCO2 that impact the model involve (i) significant geometrical differences in the heat exchangers, ranging from standard pressurized tubes seen typically in steam-producing boilers to designs for sCO2 that employ variously-curved thin walls to create shaped flow paths for extended heat transfer area and small channel cross-sections to promote thermal convection and support pressure loads; (ii) changed operating characteristics with sCO2 due to the differences in physical and thermal properties compared to steam; and (iii) possible modification of the scale morphologies, hence properties that influence exfoliation behavior, due to reaction with carbon species from sCO2. The numerical simulations conducted were based on an assumed sCO2 operating schedule and several generic heat exchanger channel shapes and cross-sectional areas. Implications for the evolution of stresses in the oxide scales formed on sCO2 heat exchangers, and ensuing critical oxide thicknesses for exfoliation, were derived and compared with expectations for an equivalent conventional tubular heat exchanger in a steam cycle (for a given alloy).« less

Surface chemistry of rare-earth oxide surfaces at ambient conditions: reactions with water and hydrocarbons

NASA Astrophysics Data System (ADS)

Külah, Elçin; Marot, Laurent; Steiner, Roland; Romanyuk, Andriy; Jung, Thomas A.; Wäckerlin, Aneliia; Meyer, Ernst

2017-03-01

Rare-earth (RE) oxide surfaces are of significant importance for catalysis and were recently reported to possess intrinsic hydrophobicity. The surface chemistry of these oxides in the low temperature regime, however, remains to a large extent unexplored. The reactions occurring at RE surfaces at room temperature (RT) in real air environment, in particular, in presence of polycyclic aromatic hydrocarbons (PAHs), were not addressed until now. Discovering these reactions would shed light onto intermediate steps occurring in automotive exhaust catalysts before reaching the final high operational temperature and full conversion of organics. Here we first address physical properties of the RE oxide, nitride and fluoride surfaces modified by exposure to ambient air and then we report a room temperature reaction between PAH and RE oxide surfaces, exemplified by tetracene (C18H12) on a Gd2O3. Our study evidences a novel effect - oxidation of higher hydrocarbons at significantly lower temperatures (~300 K) than previously reported (>500 K). The evolution of the surface chemical composition of RE compounds in ambient air is investigated and correlated with the surface wetting. Our surprising results reveal the complex behavior of RE surfaces and motivate follow-up studies of reactions between PAH and catalytic surfaces at the single molecule level.

How the dispersion of magnesium oxide nanoparticles effects on the viscosity of water-ethylene glycol mixture: Experimental evaluation and correlation development

NASA Astrophysics Data System (ADS)

Afrand, Masoud; Abedini, Ehsan; Teimouri, Hamid

2017-03-01

In this paper, the effect of dispersion of magnesium oxide nanoparticles on viscosity of a mixture of water and ethylene glycol (50-50% vol.) was examined experimentally. Experiments were performed for various nanofluid samples at different temperatures and shear rates. Measurements revealed that the nanofluid samples with volume fractions of less than 1.5% had Newtonian behavior, while the sample with volume fraction of 3% showed non-Newtonian behavior. Results showed that the viscosity of nanofluids enhanced with increasing nanoparticles volume fraction and decreasing temperature. Results of sensitivity analysis revealed that the viscosity sensitivity of nanofluid samples to temperature at higher volume fractions is more than that of at lower volume fractions. Finally, because of the inability of the existing model to predict the viscosity of MgO/EG-water nanofluid, an experimental correlation has been proposed for predicting the viscosity of the nanofluid.

Oxidation Kinetics of a NiPtTi High Temperature Shape Memory Alloy

NASA Technical Reports Server (NTRS)

Smialek, James L.; Humphrey, Donald L.; Noebe, Ronald D.

2007-01-01

A high temperature shape memory alloy (HTSMA), Ni30Pt50Ti, with an M(sub s) near 600 C, was isothermally oxidized in air for 100 hr over the temperature range of 500 to 900 C. Parabolic kinetics were confirmed by log-log and parabolic plots and showed no indication of fast transient oxidation. The overall behavior could be best described by the Arrhenius relationship: k(sub p) = 1.64 x 10(exp 12)[(-250 kJ/mole)/RT] mg(sup 2)/cm(sup 4)hr. This is about a factor of 4 reduction compared to values measured here for a binary Ni47Ti commercial SMA. The activation energy agreed with most literature values for TiO2 scale growth measured for elemental Ti and other NiTi alloys. Assuming uniform alloy depletion of a 20 mil (0.5 mm) dia. HTSMA wire, approx. 1 percent Ti reduction is predicted after 20,000 hr oxidation at 500 C, but becomes much more serious at higher temperatures.

Oxidation behavior of NiCoCrAlY coatings deposited by double-Glow plasma alloying

NASA Astrophysics Data System (ADS)

Cui, Shiyu; Miao, Qiang; Liang, Wenping; Li, Baiqiang

2018-01-01

The NiCoCrAlY coatings were deposited on the Inconel 718 alloy substrates by a novel method called double-glow plasma alloying (DG). The phases and microstructure of the coatings were investigated by X-ray diffraction analysis while their chemical composition was analyzed using scanning electron microscopy. The morphology of the NiCoCrAlY coatings was typical of coatings formed by DG, with their structure consisting of uniform submicron-sized grains. Further, the coatings showed high adhesion strength (critical load >46 N). In addition, the oxidation characteristics of the coatings and the substrate were examined at three different temperatures (850, 950, and 1050 °C) using a muffle furnace. The coatings showed a lower oxidation rate, which was approximately one-tenth of that of the substrate. Even after oxidation for 100 h, the Al2O3 phase was the primary phase in the surface coating (850 °C), with the thickness of the oxide film increasing to 0.65 μm at 950 °C. When the temperature was increased beyond 1050 °C, the elemental Al and Ni were consumed in the formation of the oxide scale, which underwent spallation at several locations. The oxidation products of Cr, which were produced in large amounts and had a prism-like structure, controlled the subsequent oxidation behavior at the surface.

Property and Microstructural Characterization of Diboride Composites for High Temperature Aerospace Applications

NASA Technical Reports Server (NTRS)

Gusman, Michael I.; Stackpoole, Mairead; Ellerby, Donald T.; Johnson, Sylvia M.; Arnold, Jim (Technical Monitor)

2001-01-01

Previous work on refractory diboride composites has shown these systems to have potential for use in high temperature leading edge applications for reusable reentry vehicles. These composites, based on compositions of HfB2 or ZrB2 with SiC particulate reinforcements, have shown good oxidation resistance in reentry environments. In this work we are investigating the effects of composition and microstructure on properties. Preliminary studies of composite mechanical properties and oxidation behavior will be discussed.

The high temperature creep behavior of oxides and oxide fibers

NASA Technical Reports Server (NTRS)

Jones, Linda E.; Tressler, Richard E.

1991-01-01

A thorough review of the literature was conducted on the high-temperature creep behavior of single and polycrystalline oxides which potentially could serve as fiber reinforcements in ceramics or metal matrix applications. Sapphire when oriented with the basal plane perpendicular to the fiber axis (c-axis oriented) is highly creep resistant at temperatures in excess of 1600 C and applied loads of 100 MPa and higher. Pyramidal slip is preferentially activated in sapphire under these conditions and steady-state creep rates in the range of 10(exp -7) to 10 (exp -8)/s were reported. Data on the creep resistance of polycrystalline beryllia suggest that C-axiz oriented single crystal beryllia may be a viable candidate as a fiber reinforcement material; however, the issure of fabricability and moisture sensitivity must be addressed for this material. Yttrium aluminum garnet (YAG) also appears to be a fiber candidate material having a high resistance to creep which is due to it's complex crystal structure and high Peierl resistance. The high creep resistance of garnet suggests that there may be other complex ternary oxides such as single crystal mullite which may also be candidate materials for fiber reinforcements. Finally, CVD and single crystal SiC, although not oxides, do possess a high resistance to creep in the temperature range between 1550 and 1850 C and under stresses of 110 to 220 MPa. From a review of the literature, it appears that for high creep resistant applications sapphire, silicon carbide, yttrium aluminum garnet, mullite, and beryllia are desirable candidate materials which require further investigation.

High Temperature Corrosion and Heat Transfer Studies of Zirconium-Silicide Coatings for Light Water Reactor Cladding Applications

NASA Astrophysics Data System (ADS)

Yeom, Hwasung

Experimental results investigating the feasibility of zirconium-silicide coating for accident tolerance of LWR fuel cladding coating was presented. The oxidation resistance of ZrSi2 appeared to be superior to bare Zircaloy-4 in high temperature air. It was shown that micro- and nanostructures consisting of alternating SiO2 and ZrO2 evolved during transient oxidation of ZrSi2, which was explained by spinodal phase decomposition of Zr-Si-O oxide. Coating optimization regarding oxidation resistance was performed mainly using magnetron sputter deposition method. ZrSi 2 coatings ( 3.9 microm) showed improvement of almost two orders of magnitude when compared to bare Zircaloy-4 after air-oxidation at 700 °C for 20-hours. Pre-oxidation of ZrSi2 coating at 700 °C for 5 h significantly mitigated oxygen diffusion in air-oxidation tests at 1000 °C for 1-hour and 1200 °C for 10-minutes. The ZrSi2 coating with the pre-oxidation was found to be the best condition to prevent oxide formation in Zircaloy-4 substrate in the steam condition even if the top surface of the coating was degraded by formation of zirconium-rich oxide layer. Only the ZrSiO4 phase, formed by exposing the ZrSi2 coating at 1400 °C in air, allowed for immobilization of silicon species in the oxide scale in the aqueous environments. A quench test facility was designed and built to study transient boiling heat transfer of modified Zircaloy-4 surfaces (e.g., roughened surfaces, oxidized surfaces, ZrSi2 coated surfaces) at various system conditions (e.g., elevated pressures and water subcooling). The minimum film boiling temperature increased with increasing system pressure and water subcooling, consistent with past literature. Quenching behavior was affected by the types of surface modification regardless of the environmental conditions. Quenching heat transfer was improved by the ZrSi 2 coating, a degree of surface oxidation (deltaox = 3 to 50 microm), and surface roughening (Ra 20 microm). A plausible hypothesis based on transient heat conduction models for liquid-solid contact in quenching process was proposed to explain the enhanced quenching performance. The theoretical model incorporated localized temperature behavior on superheated surface and elucidated bubble dynamics qualitatively, and predicts minimum film boiling temperature of oxidized Zirc-4 surfaces, which were in good agreement with experimental data.

High-Temperature, Dual-Atmosphere Corrosion of Solid-Oxide Fuel Cell Interconnects

NASA Astrophysics Data System (ADS)

Gannon, Paul; Amendola, Roberta

2012-12-01

High-temperature corrosion of ferritic stainless steel (FSS) surfaces can be accelerated and anomalous when it is simultaneously subjected to different gaseous environments, e.g., when separating fuel (hydrogen) and oxidant (air) streams, in comparison with single-atmosphere exposures, e.g., air only. This so-called "dual-atmosphere" exposure is realized in many energy-conversion systems including turbines, boilers, gasifiers, heat exchangers, and particularly in intermediate temperature (600-800°C) planar solid-oxide fuel cell (SOFC) stacks. It is generally accepted that hydrogen transport through the FSS (plate or tube) and its subsequent integration into the growing air-side surface oxide layer can promote accelerated and anomalous corrosion—relative to single-atmosphere exposure—via defect chemistry changes, such as increased cation vacancy concentrations, decreased oxygen activity, and steam formation within the growing surface oxide layers. Establishment of a continuous and dense surface oxide layer on the fuel side of the FSS can inhibit hydrogen transport and the associated effects on the air side. Minor differences in FSS composition, microstructure, and surface conditions can all have dramatic influences on dual-atmosphere corrosion behaviors. This article reviews high-temperature, dual-atmosphere corrosion phenomena and discusses implications for SOFC stacks, related applications, and future research.

Cyclic oxidation behavior of plasma sprayed NiCrAlY/WC-Co/cenosphere coating

NASA Astrophysics Data System (ADS)

Mathapati, Mahantayya; Ramesh M., R.; Doddamani, Mrityunjay

2018-04-01

Components working at elevated temperature like boiler tubes of coal and gas fired power generation plants, blades of gas and steam turbines etc. experience degradation owing to oxidation. Oxidation resistance of such components can be increased by developing protective coatings. In the present investigation NiCrAlY-WC-Co/Cenosphere coating is deposited on MDN 321 steel substrate using plasma spray coating. Thermo cyclic oxidation behavior of coating and substrate is studied in static air at 600 °C for 20 cycles. The thermo gravimetric technique is used to approximate the kinetics of oxidation. X-Ray Diffraction (XRD), Scanning Electron Microscope (SEM), Energy Dispersive Spectroscopy (EDS) and X-ray mapping techniques are used to characterize the oxidized samples. NiCrAlY-WC-Co/Cenosphere coating exhibited lower oxidation rate in comparison to MDN 321 steel substrate. The lower oxidation rate of coating is attributed to formation of Al2O3, Cr2O3, NiO and CoWO4 oxides on the outermost surface.

Conductive multi-walled boron nitride nanotubes by catalytic etching using cobalt oxide.

PubMed

Kim, Do-Hyun; Jang, Ho-Kyun; Kim, Min-Seok; Kim, Sung-Dae; Lee, Dong-Jin; Kim, Gyu Tae

2017-01-04

Boron nitride nanotubes (BNNTs) are ceramic compounds which are hardly oxidized below 1000 °C due to their superior thermal stability. Also, they are electrically almost insulators with a large band gap of 5 eV. Thus, it is a challenging task to etch BNNTs at low temperature and to convert their electrical properties to a conductive behavior. In this study, we demonstrate that BNNTs can be easily etched at low temperature by catalytic oxidation, resulting in an electrically conductive behavior. For this, multi-walled BNNTs (MWBNNTs) impregnated with Co precursor (Co(NO 3 ) 2 ·6H 2 O) were simply heated at 350 °C under air atmosphere. As a result, diverse shapes of etched structures such as pits and thinned walls were created on the surface of MWBNNTs without losing the tubular structure. The original crystallinity was still kept in the etched MWBNNTs in spite of oxidation. In the electrical measurement, MWBNNTs with a large band gap were converted to electrical conductors after etching by catalytic oxidation. Theoretical calculations indicated that a new energy state in the gap and a Fermi level shift contributed to MWBNNTs being conductive.

High temperature oxidation behavior of interconnect coated with LSCF and LSM for solid oxide fuel cell by screen printing

NASA Astrophysics Data System (ADS)

Lee, Shyong; Chu, Chun-Lin; Tsai, Ming-Jui; Lee, Jye

2010-01-01

The current study examined the effect of La 0.6Sr 0.4Co 0.2Fe 0.8O 3 (LSCF) and La 0.7Sr 0.3MnO 3 (LSM) coatings on the electrical properties and oxidation resistance of Crofer22 APU at 800 °C hot air. LSCF and LSM were coated on Crofer22 APU by screen printing and sintered over temperatures ranging from 1000 to 1100 °C in N 2. The coated alloy was first checked for compositions, morphology and interface conditions and then treated in a simulated oxidizing environment at 800 °C for 200 h. After measuring the long-term electrical resistance, the area specific resistance (ASR) at 800 °C for the alloy coated with LSCF was less than its counterpart coated with LSM. This work used LSCF coating as a metallic interconnect to reduce working temperature for the solid oxide fuel cell.

New insight of high temperature oxidation on self-exfoliation capability of graphene oxide.

PubMed

Liu, Yuhang; Zeng, Jie; Han, Di; Wu, Kai; Yu, Bowen; Chai, Songgang; Chen, Feng; Fu, Qiang

2018-05-04

The preparation of graphene oxide (GO) via Hummers method is usually divided into two steps: low temperature oxidation at 35 °C (step I oxidation) and high temperature oxidation at 98 °C (step II oxidation). However, the effects of these two steps on the exfoliation capability and chemical structure of graphite oxide remain unclear. In this study, both the functional group content of graphite oxide and the entire evolution of interlayer spacing were investigated during the two steps. Step I oxidation is a slowly inhomogeneous oxidation step to remove unoxidized graphite flakes. The prepared graphite oxide can be easily self-exfoliated but contains a lot of organic sulfur. During the first 20 min of step II oxidation, the majority of organic sulfur can be efficiently removed and graphite oxide still remains a good exfoliation capability due to sharp increasing of carboxyl groups. However, with a longer oxidation time at step II oxidation, the decrease of organic sulfur content is slowed down apparently but without any carboxyl groups forming, then graphite oxide finally loses self-exfoliation capability. It is concluded that a short time of step II oxidation can produce purer and ultralarge GO sheets via self-exfoliation. The pure GO is possessed with better thermal stability and liquid crystal behavior. Besides, reduced GO films prepared from step II oxidation show better mechanical and electric properties after reducing compared with that obtained only via step I oxidation.

New insight of high temperature oxidation on self-exfoliation capability of graphene oxide

NASA Astrophysics Data System (ADS)

Liu, Yuhang; Zeng, Jie; Han, Di; Wu, Kai; Yu, Bowen; Chai, Songgang; Chen, Feng; Fu, Qiang

2018-05-01

The preparation of graphene oxide (GO) via Hummers method is usually divided into two steps: low temperature oxidation at 35 °C (step I oxidation) and high temperature oxidation at 98 °C (step II oxidation). However, the effects of these two steps on the exfoliation capability and chemical structure of graphite oxide remain unclear. In this study, both the functional group content of graphite oxide and the entire evolution of interlayer spacing were investigated during the two steps. Step I oxidation is a slowly inhomogeneous oxidation step to remove unoxidized graphite flakes. The prepared graphite oxide can be easily self-exfoliated but contains a lot of organic sulfur. During the first 20 min of step II oxidation, the majority of organic sulfur can be efficiently removed and graphite oxide still remains a good exfoliation capability due to sharp increasing of carboxyl groups. However, with a longer oxidation time at step II oxidation, the decrease of organic sulfur content is slowed down apparently but without any carboxyl groups forming, then graphite oxide finally loses self-exfoliation capability. It is concluded that a short time of step II oxidation can produce purer and ultralarge GO sheets via self-exfoliation. The pure GO is possessed with better thermal stability and liquid crystal behavior. Besides, reduced GO films prepared from step II oxidation show better mechanical and electric properties after reducing compared with that obtained only via step I oxidation.

Oxidation and thermal fatigue of coated and uncoated NX-188 nickel-base alloy in a high velocity gas stream

NASA Technical Reports Server (NTRS)

Johnson, J. R.; Young, S. G.

1972-01-01

A cast nickel-base superalloy, NX-188, coated and uncoated, was tested in a high-velocity gas stream for resistance to oxidation and thermal fatigue by cycling between room temperature and 980, 1040, and 1090 C. Contrary to the behavior of more conventional nickel-base alloys, uncoated NX-188 exhibited the greatest weight loss at the lowest test temperature. In general, on the basis of weight change and metallographic observations a coating consisting of vapor-deposited Fe-Cr-Al-Y over a chromized substrate exhibited the best overall performance in resistance to oxidation and thermal fatigue.

Furnace Cyclic Oxidation Behavior of Multicomponent Low Conductivity Thermal Barrier Coatings

NASA Astrophysics Data System (ADS)

Zhu, Dongming; Nesbitt, James A.; Barrett, Charles A.; McCue, Terry R.; Miller, Robert A.

2004-03-01

Ceramic thermal barrier coatings (TBCs) will play an increasingly important role in advanced gas turbine engines due to their ability to further increase engine operating temperatures and reduce cooling, thus helping achieve future engine low emission, high efficiency, and improved reliability goals. Advanced multicomponent zirconia (ZrO2)-based TBCs are being developed using an oxide defect clustering design approach to achieve the required coating low thermal conductivity and high-temperature stability. Although the new composition coatings were not yet optimized for cyclic durability, an initial durability screening of the candidate coating materials was conducted using conventional furnace cyclic oxidation tests. In this paper, furnace cyclic oxidation behavior of plasma-sprayed ZrO2-based defect cluster TBCs was investigated at 1163°C using 45 min hot-time cycles. The ceramic coating failure mechanisms were studied using scanning electron microscopy (SEM) combined with x-ray diffraction (XRD) phase analysis after the furnace tests. The coating cyclic lifetime is also discussed in relation to coating processing, phase structures, dopant concentration, and other thermo-physical properties.

Furnace Cyclic Oxidation Behavior of Multi-Component Low Conductivity Thermal Barrier Coatings

NASA Technical Reports Server (NTRS)

Zhu, Dong-Ming; Nesbitt, James A.; Barrett, Charles A.; McCue, Terry R.; Miller, Robert A.

2004-01-01

Ceramic thermal barrier coatings will play an increasingly important role in advanced gas turbine engines because of their ability to further increase engine operating temperatures and reduce cooling, thus helping achieve future engine low emission, high efficiency and improved reliability goals. Advanced multi-component zirconia-based thermal barrier coatings are being developed using an oxide defect clustering design approach to achieve the required coating low thermal conductivity and high temperature stability. Although the new composition coatings were not yet optimized for cyclic durability, an initial durability screening of the candidate coating materials was conducted using conventional furnace cyclic oxidation tests. In this paper, furnace cyclic oxidation behavior of plasma-sprayed zirconia-based defect cluster thermal barrier coatings was investigated at 1163 C using 45 min hot cycles. The ceramic coating failure mechanisms were studied using scanning electron microscopy (SEM) combined with X-ray diffraction (XRD) phase analysis after the furnace tests. The coating cyclic lifetime is also discussed in relation to coating processing, phase structures, dopant concentration, and other thermo-physical properties.

High-temperature oxidation kinetics of sponge-based E110 cladding alloy

DOE PAGES

Yan, Yong; Garrison, Benton E.; Howell, Mike; ...

2017-11-03

Two-sided oxidation experiments were recently conducted at 900°C–1200 °C in flowing steam with samples of sponge-based Zr-1Nb alloy E110. Although the old electrolytic E110 tubing exhibited a high degree of susceptibility to nodular corrosion and experienced breakaway oxidation rates in a relatively short time, the new sponge-based E110 demonstrated steam oxidation behavior comparable to Zircaloy-4. Sample weight gain and oxide layer thickness measurements were performed on oxidized E110 specimens and compared to oxygen pickup and oxide layer thickness calculations using the Cathcart-Pawel correlation. Our study shows that the sponge-based E110 follows the parabolic law at temperatures above 1015 °C. Atmore » or below 1015 °C, the oxidation rate was very low when compared to Zircaloy-4 and can be represented by a cubic expression. No breakaway oxidation was observed at 1000 °C for oxidation times up to 10,000 s. Arrhenius expressions are given to describe the parabolic rate constants at temperatures above 1015 °C and cubic rate constants are provided for temperatures below 1015 °C. The weight gains calculated by our equations are in excellent agreement with the measured sample weight gains at all test temperatures. In addition to the as-fabricated E110 cladding sample, prehydrided E110 cladding with hydrogen concentrations in the 100–150 wppm range was also investigated. The effect of hydrogen content on sponge-based E110 oxidation kinetics was minimal. No significant difference was found between as-fabricated and hydrided samples with regard to oxygen pickup and oxide layer thickness for hydrogen contents below 150 wppm.« less

High-temperature oxidation kinetics of sponge-based E110 cladding alloy

NASA Astrophysics Data System (ADS)

Yan, Yong; Garrison, Benton E.; Howell, Mike; Bell, Gary L.

2018-02-01

Two-sided oxidation experiments were recently conducted at 900°C-1200 °C in flowing steam with samples of sponge-based Zr-1Nb alloy E110. Although the old electrolytic E110 tubing exhibited a high degree of susceptibility to nodular corrosion and experienced breakaway oxidation rates in a relatively short time, the new sponge-based E110 demonstrated steam oxidation behavior comparable to Zircaloy-4. Sample weight gain and oxide layer thickness measurements were performed on oxidized E110 specimens and compared to oxygen pickup and oxide layer thickness calculations using the Cathcart-Pawel correlation. Our study shows that the sponge-based E110 follows the parabolic law at temperatures above 1015 °C. At or below 1015 °C, the oxidation rate was very low when compared to Zircaloy-4 and can be represented by a cubic expression. No breakaway oxidation was observed at 1000 °C for oxidation times up to 10,000 s. Arrhenius expressions are given to describe the parabolic rate constants at temperatures above 1015 °C and cubic rate constants are provided for temperatures below 1015 °C. The weight gains calculated by our equations are in excellent agreement with the measured sample weight gains at all test temperatures. In addition to the as-fabricated E110 cladding sample, prehydrided E110 cladding with hydrogen concentrations in the 100-150 wppm range was also investigated. The effect of hydrogen content on sponge-based E110 oxidation kinetics was minimal. No significant difference was found between as-fabricated and hydrided samples with regard to oxygen pickup and oxide layer thickness for hydrogen contents below 150 wppm.

High Temperature Oxidation of Hot-Dip Aluminized T92 Steels

NASA Astrophysics Data System (ADS)

Abro, Muhammad Ali; Hahn, Junhee; Lee, Dong Bok

2018-03-01

The T92 steel plate was hot-dip aluminized, and oxidized in order to characterize the high-temperature oxidation behavior of hot-dip aluminized T92 steel. The coating consisted of Al-rich topcoat with scattered Al3Fe grains, Al3Fe-rich upper alloy layer with scattered (Al, Al5Fe2, AlFe)-grains, and Al5Fe2-rich lower alloy layer with scattered (Al5Fe2, AlFe)-grains. Oxidation at 800 °C for 20 h formed (α-Al2O3 scale)/(AlFe layer)/(AlFe3 layer)/(α-Fe(Al) layer), while oxidation at 900 °C for 20 h formed (α-Al2O3 scale plus some Fe2O3)/(AlFe layer)/(AlFe3 layer)/(α-Fe(Al) layer) from the surface. During oxidation, outward migration of all substrate elements, inward diffusion of oxygen, and back and forth diffusion of Al occurred according to concentration gradients. Also, diffusion transformed and broadened AlFe and AlFe3 layers dissolved with some oxygen and substrate alloying elements. Hot-dip aluminizing improved the high-temperature oxidation resistance of T92 steel through preferential oxidation of Al at the surface.

High Temperature Oxidation of Hot-Dip Aluminized T92 Steels

NASA Astrophysics Data System (ADS)

Abro, Muhammad Ali; Hahn, Junhee; Lee, Dong Bok

2018-05-01

The T92 steel plate was hot-dip aluminized, and oxidized in order to characterize the high-temperature oxidation behavior of hot-dip aluminized T92 steel. The coating consisted of Al-rich topcoat with scattered Al3Fe grains, Al3Fe-rich upper alloy layer with scattered (Al, Al5Fe2, AlFe)-grains, and Al5Fe2-rich lower alloy layer with scattered (Al5Fe2, AlFe)-grains. Oxidation at 800 °C for 20 h formed (α-Al2O3 scale)/(AlFe layer)/(AlFe3 layer)/(α-Fe(Al) layer), while oxidation at 900 °C for 20 h formed (α-Al2O3 scale plus some Fe2O3)/(AlFe layer)/(AlFe3 layer)/(α-Fe(Al) layer) from the surface. During oxidation, outward migration of all substrate elements, inward diffusion of oxygen, and back and forth diffusion of Al occurred according to concentration gradients. Also, diffusion transformed and broadened AlFe and AlFe3 layers dissolved with some oxygen and substrate alloying elements. Hot-dip aluminizing improved the high-temperature oxidation resistance of T92 steel through preferential oxidation of Al at the surface.

Oxidation of nickel-aluminum and iron-aluminum alloys

DOE Office of Scientific and Technical Information (OSTI.GOV)

Cathcart, J.V.

1985-01-01

The high-temperature oxidation behavior of several ordered alloys in the Ni-Al and Fe-Al systems is reviewed with special emphasis on Ni/sub 3/Al and NiAl. Ordering influences oxidation through its effect on the activities of the alloy components and by changing the point defect concentration in an alloy. Three categories of Ni-Al alloys are distinguished based on Al content and oxidation behavior. A characteristic feature of the oxidation of high-aluminum Ni-Al and Fe-Al alloys is the formation of voids in the substrate at the oxidate-metal interface. The mechanism of void formation and its suppression by minor additions of oxygen-active elements ismore » discussed. A brief description of the effect of preoxidation on the reactions of Ni/sub 3/Al-base alloys in SO/sub 2//O/sub 2/ environments is also included. 51 references, 14 figures, 1 table.« less

Cyclic furnace oxidation of clad WI-52 systems at 1040 C and 1090 C

NASA Technical Reports Server (NTRS)

Gedwill, M. A.

1972-01-01

Cyclic furnace oxidation studies were conducted on the cobalt alloy WI-52 clad with Ni-30Cr, Fe-25Cr-4A1, and Ni-20Cr-4A1 foils (0.051 to 0.254 mm thick). Tests as long as 400 hours using 1- and 20-hour cycles showed that the Ni-Cr- and Fe-Cr-A1 claddings were about equally protective at both temperatures. The protective ability of these alloys was influenced by exposure temperature and cladding thickness. At both temperatures, they protected WI-52 about as well as, or better than, a widely used commercial aluminide coating. The Ni-Cr-Al claddings did not protect WI-52 nearly as well. Interdiffusion generally influenced the oxidation behavior of all clad WI-52 systems.

The evaluation of physical properties of injection molded systems based on poly(ethylene oxide) (PEO).

PubMed

Pajander, Jari; Rensonnet, Alexia; Hietala, Sami; Rantanen, Jukka; Baldursdottir, Stefania

2017-02-25

The effect of product design parameters on the formation and properties of an injection molded solid dosage form consisting of poly(ethylene oxide)s (PEO) and two different active pharmaceutical ingredients (APIs) was studied. The product design parameters explored were melting temperature and the duration of melting, API loading degree and the molecular weight (M w ) of PEO. The solid form composition of the model APIs, theophylline and carbamazepine, was of specific interest, and its possible impact on the in vitro drug release behavior. M w of PEO had the greatest impact on the release rate of both APIs. High M w resulted in slower API release rate. Process temperature had two-fold effect with PEO 300,000g/mol. Firstly, higher process temperature transformed the crystalline part of the polymer into metastable folded form (more folded crystalline regions) and less into the more stable extended form (more extended crystalline regions), which lead to enhanced theophylline release rate. Secondly, the higher process temperature seemed to induce carbamazepine polymorphic transformation from p-monoclinic form III (carbamazepine (M)) into trigonal form II (carbamazepine (T)). The results indicated that the actual content of carbamazepine (T) affected drug release behavior more than the magnitude of transformation. Copyright © 2016 Elsevier B.V. All rights reserved.

Electrical properties of aluminum-doped zinc oxide (AZO) nanoparticles synthesized by chemical vapor synthesis.

PubMed

Hartner, Sonja; Ali, Moazzam; Schulz, Christof; Winterer, Markus; Wiggers, Hartmut

2009-11-04

Aluminum-doped zinc oxide nanoparticles have been prepared by chemical vapor synthesis, which facilitates the incorporation of a higher percentage of dopant atoms, far above the thermodynamic solubility limit of aluminum. The electrical properties of aluminum-doped and undoped zinc oxide nanoparticles were investigated by impedance spectroscopy. The impedance is measured under hydrogen and synthetic air between 323 and 673 K. The measurements under hydrogen as well as under synthetic air show transport properties depending on temperature and doping level. Under hydrogen atmosphere, a decreasing conductivity with increasing dopant content is observed, which can be explained by enhanced scattering processes due to an increasing disorder in the nanocrystalline material. The temperature coefficient for the doped samples switches from positive temperature coefficient behavior to negative temperature coefficient behavior with increasing dopant concentration. In the presence of synthetic air, the conductivity firstly increases with increasing dopant content by six orders of magnitude. The origin of the increasing conductivity is the generation of free charge carriers upon dopant incorporation. It reaches its maximum at a concentration of 7.7% of aluminum, and drops for higher doping levels. In all cases, the conductivity under hydrogen is higher than under synthetic air and can be changed reversibly by changing the atmosphere.

Growth of tungsten oxide nanostructures by chemical solution deposition

NASA Astrophysics Data System (ADS)

Jin, L. H.; Bai, Y.; Li, C. S.; Wang, Y.; Feng, J. Q.; Lei, L.; Zhao, G. Y.; Zhang, P. X.

2018-05-01

Tungsten oxide nanostructures were fabricated on LaAlO3 (00l) substrates by a simple chemical solution deposition. The decomposition behavior and phase formation of ammonium tungstate precursor were characterized by thermal analysis and X-ray diffraction. Moreover, the morphology and chemical state of nanostructures were analyzed by scanning electron microscopy, atomic force microscopy and X-ray photoelectron spectra. The effects of crystallization temperature on the formation of nanodots and nanowires were investigated. The results indicated that the change of nanostructures had close relationship with the crystallization temperature during the chemical solution deposition process. Under higher crystallization temperature, the square-like dots transformed into the dome-like nanodots and nanowires. Moreover high density well-ordered nanodots could be obtained on the substrate with the further increase of crystallization temperature. It also suggested that this simple chemical solution process could be used to adjust the nanostructures of tungsten oxide compounds on substrate.

Surface chemistry, microstructure and friction properties of some ferrous-base metallic glasses at temperatures to 750 C

NASA Technical Reports Server (NTRS)

Miyoshi, K.; Buckley, D. H.

1982-01-01

X-ray photoelectron spectroscopy analysis, transmission electron microscopy, diffraction studies, and sliding friction experiments were conducted with ferrous-base metallic glasses in sliding contact with aluminum oxide at temperatures from room to 750 C in a vacuum of 30 nPa. The results indicate that there is a significant temperature influence on the friction properties, surface chemistry, and microstructure of metallic glasses. The relative concentrations of the various constituents at the surface of the sputtered specimens were very different from the normal bulk compositions. Contaminants can come from the bulk of the material to the surface upon heating and impart boric oxide and silicon oxide at 350 C and boron nitride above 500 C. The coefficient of friction increased with increasing temperature to 350 C. Above 500 C the coefficient of friction decreased rapidly. The segregation of contaminants may be responsible for the friction behavior.

Oxide inclusions in laser additive manufactured stainless steel and their effects on impact toughness and stress corrosion cracking behavior

NASA Astrophysics Data System (ADS)

Lou, Xiaoyuan; Andresen, Peter L.; Rebak, Raul B.

2018-02-01

Intergranular and intragranular Si and Mn rich oxide inclusions are present in laser additive manufactured austenitic stainless steel. The uniform oxide dispersions in additive manufactured material promoted early initiation of microvoids and reduced its impact toughness relative to powder metallurgy (hot isostatic pressing) and wrought materials. For stress corrosion cracking in high temperature water, the silica inclusions along the grain boundaries preferentially dissolved and appeared to accelerate oxidation and caused extensive crack branching.

High-Temperature Oxidation Behavior of Iridium-Rhenium Alloys

NASA Technical Reports Server (NTRS)

Reed, Brian D.

1995-01-01

The life-limiting mechanism for radiation-cooled rockets made from iridium-coated rhenium (Ir/Re) is the diffusion of Re into the Ir layer and the subsequent oxidation of the resulting Ir-Re alloy from the inner surface. In a previous study, a life model for Ir/Re rockets was developed. It incorporated Ir-Re diffusion and oxidation data to predict chamber lifetimes as a function of temperature and oxygen partial pressure. Oxidation testing at 1540 deg C suggested that a 20-wt percent Re concentration at the inner wall surface should be established as the failure criterion. The present study was performed to better define Ir-oxidation behavior as a function of Re concentration and to supplement the data base for the life model. Samples ranging from pure Ir to Ir-40 wt percent Re (Ir-40Re) were tested at 1500 deg C, in two different oxygen environments. There were indications that the oxidation rate of the Ir-Re alloy increased significantly when it went from a single-phase solid solution to a two-phase mixture, as was suggested in previous work. However, because of testing anomalies in this study, there were not enough dependable oxidation data to definitively raise the Ir/Re rocket failure criterion from 20-wt percent Re to a Re concentration corresponding to entry into the two-phase region.

Sensitive photo-thermal response of graphene oxide for mid-infrared detection

NASA Astrophysics Data System (ADS)

Bae, Jung Jun; Yoon, Jung Hyun; Jeong, Sooyeon; Moon, Byoung Hee; Han, Joong Tark; Jeong, Hee Jin; Lee, Geon-Woong; Hwang, Ha Ryong; Lee, Young Hee; Jeong, Seung Yol; Lim, Seong Chu

2015-09-01

This study characterizes the effects of incident infrared (IR) radiation on the electrical conductivity of graphene oxide (GO) and examines its potential for mid-IR detection. Analysis of the mildly reduced GO (m-GO) transport mechanism near room temperature reveals variable range hopping (VRH) for the conduction of electrons. This VRH behavior causes the m-GO resistance to exhibit a strong temperature dependence, with a large negative temperature coefficient of resistance of approximately -2 to -4% K-1. In addition to this hopping transport, the presence of various oxygen-related functional groups within GO enhances the absorption of IR radiation significantly. These two GO material properties are synergically coupled and provoke a remarkable photothermal effect within this material; specifically, a large resistance drop is exhibited by m-GO in response to the increase in temperature caused by the IR absorption. The m-GO bolometer effect identified in this study is different from that exhibited in vanadium oxides, which require added gold-black films that function as IR absorbers owing to their limited IR absorption capability.This study characterizes the effects of incident infrared (IR) radiation on the electrical conductivity of graphene oxide (GO) and examines its potential for mid-IR detection. Analysis of the mildly reduced GO (m-GO) transport mechanism near room temperature reveals variable range hopping (VRH) for the conduction of electrons. This VRH behavior causes the m-GO resistance to exhibit a strong temperature dependence, with a large negative temperature coefficient of resistance of approximately -2 to -4% K-1. In addition to this hopping transport, the presence of various oxygen-related functional groups within GO enhances the absorption of IR radiation significantly. These two GO material properties are synergically coupled and provoke a remarkable photothermal effect within this material; specifically, a large resistance drop is exhibited by m-GO in response to the increase in temperature caused by the IR absorption. The m-GO bolometer effect identified in this study is different from that exhibited in vanadium oxides, which require added gold-black films that function as IR absorbers owing to their limited IR absorption capability. Electronic supplementary information (ESI) available. See DOI: 10.1039/c5nr04039f

Effect of temperature on the passivation behavior of steel rebar

NASA Astrophysics Data System (ADS)

Chen, Shan-meng; Cao, Bei; Wu, Yin-shun; Ma, Ke

2014-05-01

Steel rebar normally forms an oxide or rusty skin before it is embedded into concrete and the passivation properties of this skin will be heavily influenced by temperature. To study the effect of temperature on the passivation properties of steel rebar under different surface conditions, we conducted scanning electron microscopy (SEM) observations and electrochemical measurements, such as measurements of the free corrosion potential and polarization curves of HPB235 steel rebar. These measurements identified three kinds of surfaces: polished, oxide skin, and rusty skin. Our results show that the passivation properties of all the surface types decrease with the increase of temperature. Temperature has the greatest effect on the rusty-skin rebar and least effect on the polished steel rebar, because of cracks and crevices on the mill scale on the steel rebar's surface. The rusty-skin rebar exhibits the highest corrosion rate because crevice corrosion can accelerate the corrosion of the steel rebar, particularly at high temperature. The results also indicate that the threshold temperatures of passivation for the oxide-skin rebar and the rusty-skin rebar are 37°C and 20°C, respectively.

Low-Temperature Photochemically Activated Amorphous Indium-Gallium-Zinc Oxide for Highly Stable Room-Temperature Gas Sensors.

PubMed

Jaisutti, Rawat; Kim, Jaeyoung; Park, Sung Kyu; Kim, Yong-Hoon

2016-08-10

We report on highly stable amorphous indium-gallium-zinc oxide (IGZO) gas sensors for ultraviolet (UV)-activated room-temperature detection of volatile organic compounds (VOCs). The IGZO sensors fabricated by a low-temperature photochemical activation process and exhibiting two orders higher photocurrent compared to conventional zinc oxide sensors, allowed high gas sensitivity against various VOCs even at room temperature. From a systematic analysis, it was found that by increasing the UV intensity, the gas sensitivity, response time, and recovery behavior of an IGZO sensor were strongly enhanced. In particular, under an UV intensity of 30 mW cm(-2), the IGZO sensor exhibited gas sensitivity, response time and recovery time of 37%, 37 and 53 s, respectively, against 750 ppm concentration of acetone gas. Moreover, the IGZO gas sensor had an excellent long-term stability showing around 6% variation in gas sensitivity over 70 days. These results strongly support a conclusion that a low-temperature solution-processed amorphous IGZO film can serve as a good candidate for room-temperature VOCs sensors for emerging wearable electronics.

Simulation of Fatigue Behavior of High Temperature Metal Matrix Composites

NASA Technical Reports Server (NTRS)

Tong, Mike T.; Singhal, Suren N.; Chamis, Christos C.; Murthy, Pappu L. N.

1996-01-01

A generalized relatively new approach is described for the computational simulation of fatigue behavior of high temperature metal matrix composites (HT-MMCs). This theory is embedded in a specialty-purpose computer code. The effectiveness of the computer code to predict the fatigue behavior of HT-MMCs is demonstrated by applying it to a silicon-fiber/titanium-matrix HT-MMC. Comparative results are shown for mechanical fatigue, thermal fatigue, thermomechanical (in-phase and out-of-phase) fatigue, as well as the effects of oxidizing environments on fatigue life. These results show that the new approach reproduces available experimental data remarkably well.

Negative Magnetoresistance in Amorphous Indium Oxide Wires

PubMed Central

Mitra, Sreemanta; Tewari, Girish C; Mahalu, Diana; Shahar, Dan

2016-01-01

We study magneto-transport properties of several amorphous Indium oxide nanowires of different widths. The wires show superconducting transition at zero magnetic field, but, there exist a finite resistance at the lowest temperature. The R(T) broadening was explained by available phase slip models. At low field, and far below the superconducting critical temperature, the wires with diameter equal to or less than 100 nm, show negative magnetoresistance (nMR). The magnitude of nMR and the crossover field are found to be dependent on both temperature and the cross-sectional area. We find that this intriguing behavior originates from the interplay between two field dependent contributions. PMID:27876859

The influences of fluorine and process variations on polysilicon film stress and MOSFET hot carrier effects

NASA Technical Reports Server (NTRS)

Lowry, Lynn E.; Macwilliams, Kenneth P.; Isaac, Mary

1991-01-01

The use of fluorinated gate oxides may provide an improvement in nMOSFET reliability by enhancing hot carrier resistance. In order to clarify the mechanisms by which polysilicon processing and fluorination influence the oxide behavior, a matrix of nMOSFET structures was prepared using various processing, doping, and implantation strategies. These structures were evaluated for crystalline morphology and chemical element distribution. Mechanical stress measurements were taken on the polysilicon films from room temperature to cryogenic temperature. These examinations showed that fluorination of a structure with randomly oriented polysilicon can reduce residual mechanical stress and improve hot carrier resistance at room temperature.

Phase Behavior and Equations of State of the Actinide Oxides

NASA Astrophysics Data System (ADS)

Chidester, B.; Pardo, O. S.; Panero, W. R.; Fischer, R. A.; Thompson, E. C.; Heinz, D. L.; Prescher, C.; Prakapenka, V. B.; Campbell, A.

2017-12-01

The distribution of the long-lived heat-producing actinide elements U and Th in the deep Earth has important implications for the dynamics of the mantle and possibly the energy budget of Earth's core. The low shear velocities of the Large Low-Shear Velocity Provinces (LLSVPs) on the core-mantle boundary suggests that these regions are at least partially molten and may contain concentrated amounts of the radioactive elements, as well as other large cations such as the rare Earth elements. As such, by exploring the phase behavior of actinide-bearing minerals at extreme conditions, some insight into the mineralogy, formation, and geochemical and geodynamical effects of these regions can be gained. We have performed in situ high-pressure, high-temperature synchrotron X-ray diffraction experiments and calculations on two actinide oxide materials, UO2 and ThO2, to determine their phase behavior at the extreme conditions of the lower mantle. Experiments on ThO2 reached 60 GPa and 2500 K, and experiments on UO2 reached 95 GPa and 2500 K. We find that ThO2 exists in the fluorite-type structure to 20 GPa at high temperatures, at which point it transforms to the high-pressure cotunnite-type structure and remains thus up to 60 GPa. At room temperature, an anomalous expansion of the fluorite structure is observed prior to the transition, and may signal anion sub-lattice disorder. Similarly, UO2 exists in the fluorite-type structure at ambient conditions and up to 28 GPa at high temperatures. Above these pressures, we have observed a previously unidentified phase of UO2 with a tetragonal structure as the lower-temperature phase and the cotunnite-type phase at higher temperatures. Above 78 GPa, UO2 undergoes another transition or possible dissociation into two separate oxide phases. These phase diagrams suggest that the actinides could exist as oxides in solid solution with other analogous phases (e.g. ZrO2) in the cotunnite-type structure throughout much of Earth's lower mantle.

High Temperature Oxidation of Superalloys and Intermetallic Compounds

DTIC Science & Technology

2010-02-28

such as nickel aluminides (NisAI and NiAl), iron aluminides (FeAl, and Fe3AI) and titanium aluminides (TiAl and Ti3AI) are a class of advanced...80um by YAI2 phase segregation at grain boundaries preventing grain growth [6,8], other work has suggested that oxidation of titanium aluminides ...strengthened Titanium aluminides of similar composition. In this work, a study of the oxidation behavior of ingot-metallurgy processes titanium

Effect of water vapor on evolution of a thick Pt-layer modified oxide on the NiCoCrAl alloy at high temperature

NASA Astrophysics Data System (ADS)

Song, Peng; He, Xuan; Xiong, Xiping; Ma, Hongqing; Song, Qunling; Lü, Jianguo; Lu, Jiansheng

2018-03-01

To investigate the effect of water vapor on the novel Pt-containing oxide growth behavior, Pt-addition within the oxide layer on the surface of NiCoCrAl coating and furnace cycle tests were carried out at 1050 °C in air and air plus water vapor. The thick Pt-containing oxide layer on NiCoCrAl exhibits a different oxidation growth behavior compared to the conventional Pt-diffusion metallic coatings. The Pt-containing oxide after oxidation in air plus water vapor showed a much thicker oxide layer compare to the ones without Pt addition, and also presented a much better coating adhesion. During the oxidation process in air, Pt promotes the spinel (NiCr2O4) formation. However, the Cr2O3 formed in air with water vapor and fixed Pt within the complex oxide layer. The water vapor promoted the Ni and Co outer-diffusion, and combined with Pt to form CoPt compounds on the surface of the NiCoCrAl coating system.

Characterization of strain relaxation behavior in Si1- x Ge x epitaxial layers by dry oxidation

NASA Astrophysics Data System (ADS)

Jang, Hyunchul; Kim, Byongju; Koo, Sangmo; Park, Seran; Ko, Dae-Hong

2017-11-01

We fabricated fully strained Si0.77Ge0.23 epitaxial layers on Si substrates and investigated their strain relaxation behaviors under dry oxidation and the effect of oxidation temperatures and times. After the oxidation process, a Ge-rich layer was formed between the oxide and the remaining Si0.77Ge0.23 layer. Using reciprocal space mapping measurements, we confirmed that the strain of the Si0.77Ge0.23 layers was efficiently relaxed after oxidation, with a maximum relaxation value of 70% after oxidation at 850 °C for 120 min. The surface of Si0.77Ge0.23 layer after strain relaxation by dry oxidation was smoother than a thick Si0.77Ge0.23 layer, which achieved a similar strain relaxation value by increasing the film thickness. Additionally, N2 annealing was performed in order to compare its effect on the relaxation compared to dry oxidation and to identify relaxation mechanisms, other than the thermally driven ones, occurring during dry oxidation.

Tribological behavior and self-healing functionality of TiNbCN-Ag coatings in wide temperature range

NASA Astrophysics Data System (ADS)

Bondarev, A. V.; Kiryukhantsev-Korneev, Ph. V.; Levashov, E. A.; Shtansky, D. V.

2017-02-01

Ag- and Nb-doped TiCN coatings with about 2 at.% of Nb and Ag contents varied between 4.0 and 15.1 at.% were designed as promising materials for tribological applications in a wide temperature range. We report on the structure, mechanical, and tribological properties of TiNbCN-Ag coatings fabricated by simultaneous co-sputtering of TiC0.5 + 10%Nb2C and Ag targets in comparison with those of Ag-free coating. The tribological characteristics were evaluated during constant-temperature tests both at room temperature and 300 °C, as well as during dynamic temperature ramp tests in the range of 25-700 °C. The coating structure and elemental composition were studied by means of X-ray diffraction, scanning and transmission electron microscopy, and glow discharge optical emission spectroscopy. The coating microstructures and elemental compositions inside wear tracks, as well as the wear products, were examined by scanning electron microscopy, energy-dispersive spectroscopy, and Raman spectroscopy. We demonstrate that simultaneous alloying with Nb and Ag permits to overcome the main drawbacks of TiCN coatings such as their relatively high values of friction coefficient at elevated temperatures and low oxidation resistance. It is shown that a relatively high amount of Ag (15 at.%) is required to provide enhanced tribological behavior in a wide temperature range of 25-700 °C. In addition, the prepared Ag-doped coatings demonstrated active oxidation protection and self-healing functionality due to the segregation of Ag metallic particles in damage areas such as cracks, pin-holes, or oxidation sites.

Effect of surface oxide films on the properties of pulse electric-current sintered metal powders

NASA Astrophysics Data System (ADS)

Xie, Guoqiang; Ohashi, Osamu; Yamaguchi, Norio; Wang, Airu

2003-11-01

Metallic powders with various thermodynamic stability oxide films (Ag, Cu, and Al powders) were sintered using a pulse electric-current sintering (PECS) process. Behavior of oxide films at powder surfaces and their effect on the sintering properties were investigated. The results showed that the sintering properties of metallic powders in the PECS process were subject to the thermodynamic stability of oxide films at particles surfaces. The oxide films at Ag powder surfaces are decomposed during sintering with the contact region between the particles being metal/metal bond. The oxide films at Cu powder surfaces are mainly broken via loading pressure at a low sintering temperature. At a high sintering temperature, they are mainly dissolved in the parent metal, and the contact regions turn into the direct metal/metal bonding. Excellent sintering properties can be received. The oxide films at Al powder surfaces are very stable, and cannot be decomposed and dissolved, but broken by plastic deformation of particles under loading pressure at experimental temperatures. The interface between particles is partially bonded via the direct metal/metal bonding making it difficult to achieve good sintered properties.

1.3 μm VCSELs: InGaAs/GaAs, GaInNAs/GaAs multiple quantum wells, and InAs/GaAs quantum dots — three candidates as active material

NASA Astrophysics Data System (ADS)

Gilet, Ph.; Pougeoise, E.; Grenouillet, L.; Grosse, Ph.; Olivier, N.; Poncet, S.; Chelnokov, A.; Gérard, J. M.; Stevens, R.; Hamelin, R.; Hammar, M.; Berggren, J.; Sundgren, P.

2007-02-01

In this article, we report our results on 1.3μm VCSELs for optical interconnection applications. Room temperature continuous-wave lasing operation is demonstrated for top emitting oxide-confined devices with three different active materials, highly strained InGaAs/GaAs(A) and GaInNAs/GaAs (B) multiple quantum wells (MQW) or InAs/GaAs (C) quantum dots (QD). Conventional epitaxial structures grown respectively by Metal Organic Vapour Phase Epitaxy (MOVPE), Molecular Beam Epitaxy (MBE) and MBE, contain fully doped GaAs/AlGaAs DBRs. All three epilayers are processed in the same way. Current and optical confinement are realized by selective wet oxidation. Circular apertures from 2 (micron)m to 16 (micron)m diameters are defined. At room temperature and in continuous wave operation, all three systems exhibit lasing operation at wavelengths above 1 275nm and reached 1 300nm for material (A). Typical threshold currents are in the range [1- 10]mA and are strongly dependent firstly on oxide diameter and secondly on temperature. Room temperature cw maximum output power corresponds respectively to 1.77mW, 0.5mW and 0.6mW. By increasing driving current, multimode operation occurs at different level depending on the oxide diameter. In case (A), non conventional modal behaviors will be presented and explained by the presence of specific oxide modes. Thermal behaviors of the different devices have been compared. In case (A) and (C) we obtain a negative T0. We will conclude on the different active materials in terms of performances with respect to 1300nm VCSEL applications.

COREST: A FORTRAN computer program to analyze paralinear oxidation behavior and its application to chromic oxide forming alloys

NASA Technical Reports Server (NTRS)

Barrett, C. E.; Presler, A. F.

1976-01-01

A FORTRAN computer program (COREST) was developed to analyze the high-temperature paralinear oxidation behavior of metals. It is based on a mass-balance approach and uses typical gravimetric input data. COREST was applied to predominantly Cr2O3-forming alloys tested isothermally for long times. These alloys behaved paralinearly above 1100 C as a result of simultaneous scale formation and scale vaporization. Output includes the pertinent formation and vaporization constants and kinetic values of interest. COREST also estimates specific sample weight and specific scale weight as a function of time. Most importantly, from a corrosion standpoint, it estimates specific metal loss.

Inhibited phase behavior of gas hydrates in graphene oxide: influences of surface and geometric constraints.

PubMed

Kim, Daeok; Kim, Dae Woo; Lim, Hyung-Kyu; Jeon, Jiwon; Kim, Hyungjun; Jung, Hee-Tae; Lee, Huen

2014-11-07

Porous materials have provided us unprecedented opportunities to develop emerging technologies such as molecular storage systems and separation mechanisms. Pores have also been used as supports to contain gas hydrates for the application in gas treatments. Necessarily, an exact understanding of the properties of gas hydrates in confining pores is important. Here, we investigated the formation of CO2, CH4 and N2 hydrates in non-interlamellar voids in graphene oxide (GO), and their thermodynamic behaviors. For that, low temperature XRD and P-T traces were conducted to analyze the water structure and confirm hydrate formation, respectively, in GO after its exposure to gaseous molecules. Confinement and strong interaction of water with the hydrophilic surface of graphene oxide reduce water activity, which leads to the inhibited phase behavior of gas hydrates.

Mechanism study on the sulfidation of ZnO with sulfur and iron oxide at high temperature

NASA Astrophysics Data System (ADS)

Han, Junwei; Liu, Wei; Zhang, Tianfu; Xue, Kai; Li, Wenhua; Jiao, Fen; Qin, Wenqing

2017-02-01

The mechanism of ZnO sulfidation with sulfur and iron oxide at high temperatures was studied. The thermodynamic analysis, sulfidation behavior of zinc, phase transformations, morphology changes, and surface properties were investigated by HSC 5.0 combined with FactSage 7.0, ICP, XRD, optical microscopy coupled with SEM-EDS, and XPS. The results indicate that increasing temperature and adding iron oxide can not only improve the sulfidation of ZnO but also promote the formation and growth of ZnS crystals. Fe2O3 captured the sulfur in the initial sulfidation process as iron sulfides, which then acted as the sulfurizing agent in the late period, thus reducing sulfur escape at high temperatures. The addition of carbon can not only enhance the sulfidation but increase sulfur utilization rate and eliminate the generation of SO2. The surfaces of marmatite and synthetic zinc sulfides contain high oxygen due to oxidation and oxygen adsorption. Hydroxyl easily absorbs on the surface of iron-bearing zinc sulfide (Zn1-xFexS). The oxidation of synthetic Zn1-xFexS is easier than marmatite in air.

Mechanism study on the sulfidation of ZnO with sulfur and iron oxide at high temperature

PubMed Central

Han, Junwei; Liu, Wei; Zhang, Tianfu; Xue, Kai; Li, Wenhua; Jiao, Fen; Qin, Wenqing

2017-01-01

The mechanism of ZnO sulfidation with sulfur and iron oxide at high temperatures was studied. The thermodynamic analysis, sulfidation behavior of zinc, phase transformations, morphology changes, and surface properties were investigated by HSC 5.0 combined with FactSage 7.0, ICP, XRD, optical microscopy coupled with SEM-EDS, and XPS. The results indicate that increasing temperature and adding iron oxide can not only improve the sulfidation of ZnO but also promote the formation and growth of ZnS crystals. Fe2O3 captured the sulfur in the initial sulfidation process as iron sulfides, which then acted as the sulfurizing agent in the late period, thus reducing sulfur escape at high temperatures. The addition of carbon can not only enhance the sulfidation but increase sulfur utilization rate and eliminate the generation of SO2. The surfaces of marmatite and synthetic zinc sulfides contain high oxygen due to oxidation and oxygen adsorption. Hydroxyl easily absorbs on the surface of iron-bearing zinc sulfide (Zn1−xFexS). The oxidation of synthetic Zn1−xFexS is easier than marmatite in air. PMID:28186156

Optical and dielectric properties of poly(vinyl-alcohol) - Cobalt oxide nanocomposite film

NASA Astrophysics Data System (ADS)

Das, Amit Kumar; Tripathi, Himadri Sekhar; Meikap, Ajit Kumar

2018-04-01

Highly crystalline cobalt oxide (Co3O4) have been synthesized via calcination method. The crystallite size of the nanoparticles is 28.5 nm. Two direct band gap of Co3O4 is observed. The temperature dependent dielectric spectroscopy of PVA-Co3O4 composite film shows ferroelectric behavior. The dielectric constant of the composite film is almost 2.5 times compare to pure PVA at a 1kHz frequency and room temperature. From the Nyquist plot grain and grain boundary effects are identified.

Molecular dynamics simulation study of hydrogen bonding in aqueous poly(ethylene oxide) solutions.

PubMed

Smith, G D; Bedrov, D; Borodin, O

2000-12-25

A molecular dynamics simulation study of hydrogen bonding in poly(ethylene oxide) (PEO)/water solutions was performed. PEO-water and water-water hydrogen bonding manifested complex dependence on both composition and temperature. Strong water clustering in concentrated solutions was seen. Saturation of hydrogen bonding at w(p) approximately equal to 0.5 and a dramatic decrease in PEO-water hydrogen bonding with increasing temperature, consistent with experimentally observed closed-loop phase behavior, were observed. Little tendency toward intermolecular bridging of PEO chains by water molecules was seen.

Synthesis, characterization, microstructure, optical and magnetic properties of strontium cobalt carbonate precursor and Sr2Co2O5 oxide material

NASA Astrophysics Data System (ADS)

Agilandeswari, K.; Ruban Kumar, A.

2014-04-01

Sr2Co2O5 ceramic synthesized by the coprecipitation of strontium cobalt carbonate method. XRD analysis shows the single phase strontianite precursor and decomposed oxide product as orthorhombic structure of Sr2Co2O5. Thermal analysis proves the Sr2Co2O5 phase formation temperature of 800 °C. SEM image indicates crystalline rod shaped carbonate precursor transformed to oxide as porous diffused sphere shape particles. Optical band gap it reveals the strontium cobalt carbonate precursor as insulating material and the Sr2Co2O5 as semiconducting nature. The room temperature magnetic study indicates the carbonate precursor as paramagnetic but its oxide Sr2Co2O5 as superparamagnetic behavior.

Development of Oxidation Protection Coatings for Gamma Titanium Aluminide Alloys

NASA Technical Reports Server (NTRS)

Wallace, T. A.; Bird, R. K.; Sankaran, S. N.

2003-01-01

Metallic material systems play a key role in meeting the stringent weight and durability requirements for reusable launch vehicle (RLV) airframe hot structures. Gamma titanium aluminides (gamma-TiAl) have been identified as high-payoff materials for high-temperature applications. The low density and good elevated temperature mechanical properties of gamma-TiAl alloys make them attractive candidates for durable lightweight hot structure and thermal protection systems at temperatures as high as 871 C. However, oxidation significantly degrades gamma-TiAl alloys under the high-temperature service conditions associated with the RLV operating environment. This paper discusses ongoing efforts at NASA Langley Research Center to develop durable ultrathin coatings for protecting gamma-TiAl alloys from high-temperature oxidation environments. In addition to offering oxidation protection, these multifunctional coatings are being engineered to provide thermal control features to help minimize heat input into the hot structures. This paper describes the coating development effort and discusses the effects of long-term high-temperature exposures on the microstructure of coated and uncoated gamma-TiAl alloys. The alloy of primary consideration was the Plansee alloy gamma-Met, but limited studies of the newer alloy gamma-Met-PX were also included. The oxidation behavior of the uncoated materials was evaluated over the temperature range of 704 C to 871 C. Sol-gel-based coatings were applied to the gamma-TiAl samples by dipping and spraying, and the performance evaluated at 871 C. Results showed that the coatings improve the oxidation resistance, but that further development is necessary.

Status of Chronic Oxidation Studies of Graphite

DOE Office of Scientific and Technical Information (OSTI.GOV)

Contescu, Cristian I.; Mee, Robert W.

Graphite will undergo extremely slow, but continuous oxidation by traces of moisture that will be present, albeit at very low levels, in the helium coolant of HTGR. This chronic oxidation may cause degradation of mechanical strength and thermal properties of graphite components if a porous oxidation layer penetrates deep enough in the bulk of graphite components during the lifetime of the reactor. The current research on graphite chronic oxidation is motivated by the acute need to understand the behavior of each graphite grade during prolonged exposure to high temperature chemical attack by moisture. The goal is to provide the elementsmore » needed to develop predictive models for long-time oxidation behavior of graphite components in the cooling helium of HTGR. The tasks derived from this goal are: (1) Oxidation rate measurements in order to determine and validate a comprehensive kinetic model suitable for prediction of intrinsic oxidation rates as a function of temperature and oxidant gas composition; (2) Characterization of effective diffusivity of water vapor in the graphite pore system in order to account for the in-pore transport of moisture; and (3) Development and validation of a predictive model for the penetration depth of the oxidized layer, in order to assess the risk of oxidation caused damage of particular graphite grades after prolonged exposure to the environment of helium coolant in HTGR. The most important and most time consuming of these tasks is the measurement of oxidation rates in accelerated oxidation tests (but still under kinetic control) and the development of a reliable kinetic model. This report summarizes the status of chronic oxidation studies on graphite, and then focuses on model development activities, progress of kinetic measurements, validation of results, and improvement of the kinetic models. Analysis of current and past results obtained with three grades of showed that the classical Langmuir-Hinshelwood model cannot reproduce all data collected so far. Starting from here we propose a modification of the LH model to include temperature activation of graphite surface as a Boltzmann activation function. The enhanced Boltzmann-Langmuir-Hinshelwood model (BLH) was tested successfully on three grades of graphite. The model is a robust, comprehensive mathematical function that allows better fitting of experimental results spanning a wide range of temperature and partial pressures of water vapor and hydrogen. However, the model did not fit satisfactorily the data extracted from the old report on graphite H-451 oxidation by water.« less

Trap States of the Oxide Thin Film Transistor

NASA Astrophysics Data System (ADS)

Yu, Kyeong Min; Yuh, Jin Tae; Park, Sang Hee Ko; Ryu, Min Ki; Yun, Eui Jung; Bae, Byung Seong

2013-10-01

We investigated the temperature dependent recovery of the threshold voltage shift observed in both ZnO and indium gallium zinc oxide (IGZO) thin film transistors (TFTs) after application of gate bias and light illumination. Two types of recovery were observed for both the ZnO and IGZO TFTs; low temperature recovery (below 110 °C) which is attributed to the trapped charge and high temperature recovery (over 110 °C) which is related to the annihilation of trap states generated during stresses. From a comparison study of the recovery rate with the analysis of hydrogen diffusion isochronal annealing, a similar behavior was observed for both TFT recovery and hydrogen diffusion. This result suggests that hydrogen plays an important role in the generation and annihilation of trap states in oxide TFTs under gate bias or light illumination stresses.

Corrosion and corrosion prevention in gas turbines

NASA Technical Reports Server (NTRS)

Mom, A. J. A.; Kolkman, H. J.

1985-01-01

The conditions governing the corrosion behavior in gas turbines are surveyed. Factors such as temperature, relative humidity, the presence of sulfur and nitrogen dioxide, and fuel quality are discussed. Electromechanical corrosion at relatively low temperature in compressors; oxidation; and hot corrosion (sulfidation) at high temperature in turbines are considered. Corrosion prevention by washing and rinsing, fueld additives, and corrosion resistant materials and coatings are reviewed.

Evaluation of the Effect of Sulfur on the Performance of Nickel/Gadolinium‐Doped Ceria Based Solid Oxide Fuel Cell Anodes

PubMed Central

Yurkiv, Vitaliy; Costa, Rémi; Schiller, Günter; Friedrich, K. Andreas

2016-01-01

Abstract The focus of this study is the measurement and understanding of the sulfur poisoning phenomena of Ni/gadolinium‐doped ceria (CGO) based solid oxide fuel cells (SOFC). Cells with Ni/CGO10 and NiCu5/CGO40 anodes were characterized by using impedance spectroscopy at different temperatures and H2/H2O fuel ratios. The short‐term sulfur poisoning behavior was investigated systematically at temperatures of 800–950 °C, current densities of 0–0.75 A cm−2, and H2S concentrations of 1–20 ppm. A sulfur poisoning mitigation effect was observed at high current loads and temperatures. The poisoning behavior was reversible for short exposure times. It was observed that the sulfur‐affected processes exhibited significantly different relaxation times that depend on the Gd content in the CGO phase. Moreover, it was demonstrated that the capacitance of Ni/CGO10 anodes is strongly dependent on the temperature and gas‐phase composition, which reflects a changing Ce3+/Ce4+ ratio. PMID:27863123

Comparison of the oxidation rate and degree of graphitization of selected IG and NBG nuclear graphite grades

NASA Astrophysics Data System (ADS)

Chi, Se-Hwan; Kim, Gen-Chan

2008-10-01

The oxidation rate and degree of graphitization (DOG) were determined for some selected nuclear graphite grades (i.e., IG-110, IG-430, NBG-18, NBG-25) and compared in view of their filler coke type (i.e., pitch or petroleum coke) and the physical property of the grades. Oxidation rates were determined at six temperatures between 600 and 960 °C in air by using a three-zone vertical tube furnace at a 10 l/min air flow rate. The specimens were a cylinder with a 25.4 mm diameter and a 25.4 mm length. The DOG was determined based on the lattice parameter c determined from an X-ray diffraction (XRD). Results showed that, even though the four examined nuclear graphite grades showed a highly temperature-sensitive oxidation behavior through out the test temperature range of 600-950 °C, the differences between the grades were not significant. The oxidation rates determined for a 5-10% weight loss at the six temperatures were nearly the same except for 702 and 808 °C, where the pitch coke graphites showed an apparent decrease in their oxidation rate, more so than the petroleum coke graphites. These effects of the coke type reduced or nearly disappeared with an increasing temperature. The average activation energy determined for 608-808 °C was 161.5 ± 7.3 kJ/mol, showing that the dominant oxidation reaction occurred by a chemical control. A relationship between the oxidation rate and DOG was not observed.

Microstructure and high-temperature oxidation resistance of TiN/Ti3Al intermetallic matrix composite coatings on Ti6Al4V alloy surface by laser cladding

NASA Astrophysics Data System (ADS)

Zhang, Xiaowei; Liu, Hongxi; Wang, Chuanqi; Zeng, Weihua; Jiang, Yehua

2010-11-01

A high-temperature oxidation resistant TiN embedded in Ti3Al intermetallic matrix composite coating was fabricated on titanium alloy Ti6Al4V surface by 6kW transverse-flow CO2 laser apparatus. The composition, morphology and microstructure of the laser clad TiN/Ti3Al intermetallic matrix composite coating were characterized by optical microscopy (OM), scanning electron microscopy (SEM), X-ray diffraction (XRD) and energy dispersive spectrometer (EDS). In order to evaluate the high-temperature oxidation resistance of the composite coatings and the titanium alloy substrate, isothermal oxidation test was performed in a conventional high-temperature resistance furnace at 600°C and 800°C respectively. The result shows that the laser clad intermetallic composite coating has a rapidly solidified fine microstructure consisting of TiN primary phase (granular-like, flake-like, and dendrites), and uniformly distributed in the Ti3Al matrix. It indicates that a physical and chemical reaction between the Ti powder and AlN powder occurred completely under the laser irradiation. In addition, the microhardness of the TiN/Ti3Al intermetallic matrix composite coating is 844HV0.2, 3.4 times higher than that of the titanium alloy substrate. The high-temperature oxidation resistance test reveals that TiN/Ti3Al intermetallic matrix composite coating results in the better modification of high-temperature oxidation behavior than the titanium substrate. The excellent high-temperature oxidation resistance of the laser cladding layer is attributed to the formation of the reinforced phase TiN and Al2O3, TiO2 hybrid oxide. Therefore, the laser cladding TiN/Ti3Al intermetallic matrix composite coating is anticipated to be a promising oxidation resistance surface modification technique for Ti6Al4V alloy.

On the use of thermal NF3 as the fluorination and oxidation agent in treatment of used nuclear fuels

NASA Astrophysics Data System (ADS)

Scheele, Randall; McNamara, Bruce; Casella, Andrew M.; Kozelisky, Anne

2012-05-01

This paper presents results of our investigation on the use of nitrogen trifluoride as a fluorination or fluorination/oxidation agent for separating valuable constituents from used nuclear fuels by exploiting the different volatilities of the constituent fission product and actinide fluorides. Our thermodynamic calculations show that nitrogen trifluoride has the potential to produce volatile fission product and actinide fluorides from oxides and metals that can form volatile fluorides. Simultaneous thermogravimetric and differential thermal analyses show that the oxides of lanthanum, cerium, rhodium, and plutonium are fluorinated but do not form volatile fluorides when treated with nitrogen trifluoride at temperatures up to 550 °C. However, depending on temperature, volatile fluorides or oxyfluorides can form from nitrogen trifluoride treatment of the oxides of niobium, molybdenum, ruthenium, tellurium, uranium, and neptunium. Thermoanalytical studies demonstrate near-quantitative separation of uranium from plutonium in a mixed 80% uranium and 20% plutonium oxide. Our studies of neat oxides and metals suggest that the reactivity of nitrogen trifluoride may be adjusted by temperature to selectively separate the major volatile fuel constituent uranium from minor volatile constituents, such as Mo, Tc, Ru and from the non-volatile fuel constituents based on differences in their reaction temperatures and kinetic behaviors. This reactivity is novel with respect to that reported for other fluorinating reagents F2, BrF5, ClF3.

Rapidly reversible redox transformation in nanophase manganese oxides at room temperature triggered by changes in hydration

PubMed Central

Birkner, Nancy; Navrotsky, Alexandra

2014-01-01

Chemisorption of water onto anhydrous nanophase manganese oxide surfaces promotes rapidly reversible redox phase changes as confirmed by calorimetry, X-ray diffraction, and titration for manganese average oxidation state. Surface reduction of bixbyite (Mn2O3) to hausmannite (Mn3O4) occurs in nanoparticles under conditions where no such reactions are seen or expected on grounds of bulk thermodynamics in coarse-grained materials. Additionally, transformation does not occur on nanosurfaces passivated by at least 2% coverage of what is likely an amorphous manganese oxide layer. The transformation is due to thermodynamic control arising from differences in surface energies of the two phases (Mn2O3 and Mn3O4) under wet and dry conditions. Such reversible and rapid transformation near room temperature may affect the behavior of manganese oxides in technological applications and in geologic and environmental settings. PMID:24733903

Tensile properties of V-5Cr-5Ti alloy after exposure in air environment

DOE Office of Scientific and Technical Information (OSTI.GOV)

Natesan, K.; Soppet, W.K.

1997-04-01

Oxidation studies were conducted on V-5Cr-5Ti alloy specimens in an air environment to evaluate the oxygen uptake behavior of the alloy as a function of temperature and exposure time. The oxidation rates, calculated from parabolic kinetic measurements of thermogravimetric testing and confirmed by microscopic analysis of cross sections of exposed specimens, were 5, 17, and 27 {mu}m per year after exposure at 300, 400, and 500{degrees}C, respectively. Uniaxial tensile tests were conducted at room temperature and at 500{degrees}C on preoxidized specimens of the alloy to examine the effects of oxidation and oxygen migration on tensile strength and ductility. Correlations weremore » developed between tensile strength and ductility of the oxidized alloy and microstructural characteristics such as oxide thickness, depth of hardened layer, depth of intergranular fracture zone, and transverse crack length.« less

Rapidly reversible redox transformation in nanophase manganese oxides at room temperature triggered by changes in hydration.

PubMed

Birkner, Nancy; Navrotsky, Alexandra

2014-04-29

Chemisorption of water onto anhydrous nanophase manganese oxide surfaces promotes rapidly reversible redox phase changes as confirmed by calorimetry, X-ray diffraction, and titration for manganese average oxidation state. Surface reduction of bixbyite (Mn2O3) to hausmannite (Mn3O4) occurs in nanoparticles under conditions where no such reactions are seen or expected on grounds of bulk thermodynamics in coarse-grained materials. Additionally, transformation does not occur on nanosurfaces passivated by at least 2% coverage of what is likely an amorphous manganese oxide layer. The transformation is due to thermodynamic control arising from differences in surface energies of the two phases (Mn2O3 and Mn3O4) under wet and dry conditions. Such reversible and rapid transformation near room temperature may affect the behavior of manganese oxides in technological applications and in geologic and environmental settings.

Low-Temperature Oxidation-Free Selective Laser Sintering of Cu Nanoparticle Paste on a Polymer Substrate for the Flexible Touch Panel Applications.

PubMed

Kwon, Jinhyeong; Cho, Hyunmin; Eom, Hyeonjin; Lee, Habeom; Suh, Young Duk; Moon, Hyunjin; Shin, Jaeho; Hong, Sukjoon; Ko, Seung Hwan

2016-05-11

Copper nanomaterials suffer from severe oxidation problem despite the huge cost effectiveness. The effect of two different processes for conventional tube furnace heating and selective laser sintering on copper nanoparticle paste is compared in the aspects of chemical, electrical and surface morphology. The thermal behavior of the copper thin films by furnace and laser is compared by SEM, XRD, FT-IR, and XPS analysis. The selective laser sintering process ensures low annealing temperature, fast processing speed with remarkable oxidation suppression even in air environment while conventional tube furnace heating experiences moderate oxidation even in Ar environment. Moreover, the laser-sintered copper nanoparticle thin film shows good electrical property and reduced oxidation than conventional thermal heating process. Consequently, the proposed selective laser sintering process can be compatible with plastic substrate for copper based flexible electronics applications.

Si-nanocrystal-based nanofluids for nanothermometry

NASA Astrophysics Data System (ADS)

Cardona-Castro, M. A.; Morales-Sánchez, A.; Licea-Jiménez, L.; Alvarez-Quintana, J.

2016-06-01

The measurement of local temperature in nanoscale volumes is becoming a technological frontier. Photoluminescent nanoparticles and nanocolloids are the natural choice for nanoscale temperature probes. However, the influence of a surrounding liquid on the cryogenic behavior of oxidized Si-nanocrystals (Si-NCs) has never been investigated. In this work, the photoluminescence (PL) of oxidized Si-NCs/alcohol based nanocolloids is measured as a function of the temperature and the molecule length of monohydric alcohols above their melting-freezing point. The results unveil a progressive blue shift on the emission peak which is dependent on the temperature as well as the dielectric properties of the surrounding liquid. Such an effect is analyzed in terms of thermal changes of the Si-NCs bandgap, quantum confinement and the polarization effects of the embedding medium; revealing an important role of the dielectric constant of the surrounding liquid. These results are relevant because they offer a general insight to the fundamental behavior of photoluminescent nanocolloids under a cooling process and moreover, enabling PL tuning based on the dielectric properties of the surrounding liquid. Hence, the variables required to engineer PL of nanofluids are properly identified for use as temperature sensors at the nanoscale.

Microgravity Processing of Oxide Superconductors

NASA Technical Reports Server (NTRS)

Olive, James R.; Hofmeister, William H.; Bayuzick, Robert J.; Vlasse, Marcus

1999-01-01

Considerable effort has been concentrated on the synthesis and characterization of high T(sub c) oxide superconducting materials. The YBaCuO system has received the most intense study, as this material has shown promise for the application of both thin film and bulk materials. There are many problems with the application of bulk materials- weak links, poor connectivity, small coherence length, oxygen content and control, environmental reactivity, phase stability, incongruent melting behavior, grain boundary contamination, brittle mechanical behavior, and flux creep. The extent to which these problems are intrinsic or associated with processing is the subject of controversy. This study seeks to understand solidification processing of these materials, and to use this knowledge for alternative processing strategies, which, at the very least, will improve the understanding of bulk material properties and deficiencies. In general, the phase diagram studies of the YBaCuO system have concentrated on solid state reactions and on the Y2BaCuO(x) + liquid yields YBa2Cu3O(7-delta) peritectic reaction. Little information is available on the complete melting relations, undercooling, and solidification behavior of these materials. In addition, rare earth substitutions such as Nd and Gd affect the liquidus and phase relations. These materials have promising applications, but lack of information on the high temperature phase relations has hampered research. In general, the understanding of undercooling and solidification of high temperature oxide systems lags behind the science of these phenomena in metallic systems. Therefore, this research investigates the fundamental melting relations, undercooling, and solidification behavior of oxide superconductors with an emphasis on improving ground based synthesis of these materials.

REACTIONS OF BERYLLIUM IN OXIDIZING ENVIRONMENTS

DOE Office of Scientific and Technical Information (OSTI.GOV)

Snyder, P.E.; Boes, D.J.

1964-05-01

To evaluate the potential health hazard of beryllium under certain circumstances, a study was made of the interaction of metallic beryllium with oxidizing environments. This study consisted of two parts. Beryllium was subjected to the action of hydrocarbon/hydrogen/oxygen flames at temperatures below and above the melting point. A determination was made of the amount of contamination by the oxide of the downstream flue gases. The experiments indicated that the oxidation rates and the contamination are relatively low below the melting point of beryllium (1283 deg C). Above this temperature, however, it was found that the molten metal burned rapidly whenmore » unprotected by an oxide layer. This caused a sharp increase in both rate of oxidation and in downstream contamination. The behavior of beryllium when surrounded by water substance was investigated. The experimental work was divided into two phases involving reaction in liquid water and in steam. In general, it was found that the oxide layer formed was at first tightly adherent and later became thick and porous. The time between these two conditions depended on temperature, decreasing sharply as the melting point was approached. Upon melting, the oxide layer tended to act as a crucible containing the liquid metal. Under suitable conditions, the liquid would break out of its cage and oxidize very rapidly. When this occurred, the surrounding steam was slightly contaminated with the oxide. (auth)« less

The catalytic removal of ammonia and nitrogen oxides from spacecabin atmospheres

NASA Technical Reports Server (NTRS)

Gully, A. J.; Graham, R. R.; Halligan, J. E.; Bentsen, P. C.

1973-01-01

Investigations were made on methods for the removal of ammonia and to a lesser extent nitrogen oxides in low concentrations from air. The catalytic oxidation of ammonia was studied over a temperature range of 250 F to 600 F and a concentration range 20 ppm to 500 ppm. Of the catalysts studied, 0.5 percent ruthenium supported on alumina was found to be superior. This material is active at temperatures as low as 250 F and was found to produce much less nitrous oxide than the other two active catalysts, platinum on alumina and Hopcalite. A quantitative design model was developed which will permit the performance of an oxidizer to be calculated. The ruthenium was found to be relatively insensitive to low concentrations of water and to oxygen concentration between 21 percent and 100 percent. Hydrogen sulfide was found to be a poison when injected in relatively large quantities. The adsorption of ammonia by copper sulfate treated silica gel was investigated at temperatures of 72 F and 100 F. A quantitative model was developed for predicting adsorption bed behavior.

High Temperature Oxidation Behavior of gamma-Ni+gamma'-Ni3Al Alloys and Coatings Modified with Pt and Reactive Elements

DOE Office of Scientific and Technical Information (OSTI.GOV)

Mu, Nan

2007-12-01

Materials for high-pressure turbine blades must be able to operate in the high-temperature gases (above 1000 C) emerging from the combustion chamber. Accordingly, the development of nickel-based superalloys has been constantly motivated by the need to have improved engine efficiency, reliability and service lifetime under the harsh conditions imposed by the turbine environment. However, the melting point of nickel (1455 C) provides a natural ceiling for the temperature capability of nickel-based superalloys. Thus, surface-engineered turbine components with modified diffusion coatings and overlay coatings are used. Theses coatings are capable of forming a compact and adherent oxide scale, which greatly impedesmore » the further transport of reactants between the high-temperature gases and the underlying metal and thus reducing attack by the atmosphere. Typically, these coatings contain β-NiAl as a principal constituent phase in order to have sufficient aluminum content to form an Al 2O 3 scale at elevated temperatures. The drawbacks to the currently-used {beta}-based coatings, such as phase instabilities, associated stresses induced by such phase instabilities, and extensive coating/substrate interdiffusion, are major motivations in this study to seek next-generation coatings. The high-temperature oxidation resistance of novel Pt + Hf-modified γ-Ni + γ-Ni 3Al-based alloys and coatings were investigated in this study. Both early-stage and 4-days isothermal oxidation behavior of single-phase γ-Ni and γ'-Ni 3Al alloys were assessed by examining the weight changes, oxide-scale structures, and elemental concentration profiles through the scales and subsurface alloy regions. It was found that Pt promotes Al 2O 3 formation by suppressing the NiO growth on both γ-Ni and γ'Ni 3Al single-phase alloys. This effect increases with increasing Pt content. Moreover, Pt exhibits this effect even at lower temperatures (~970 C) in the very early stage of oxidation. It was also inferred that Pt enhances the diffusive flux of aluminum from the substrate to the scale/alloy interface. Relatively low levels of hafnium addition to Pt-free γ'-Ni 3Al increased the extent of external NiO formation due to non-protective HfO 2 formation. Accordingly, this effect intensified with increasing Hf content from 0.2 to 0.5 at.%.« less

Initial oxidation behavior of Ni3Al (210) surface induced by supersonic oxygen molecular beam at room temperature

NASA Astrophysics Data System (ADS)

Xu, Ya; Sakurai, Junya; Teraoka, Yuden; Yoshigoe, Akitaka; Demura, Masahiko; Hirano, Toshiyuki

2017-01-01

The initial oxidation behavior of a clean Ni3Al (210) surface was studied at 300 K using a supersonic O2 molecular beam (O2 SSMB) having an O2 translational energy of 2.3 eV, and real-time photoemission spectroscopy performed with high-brilliance synchrotron radiation. The evolution behaviors of the O 1s, Ni 2p, Al 2p, and Ni 3p spectra were examined during irradiation with the O2 SSMB. The spectral analysis revealed that both the Al atoms and the Ni atoms on the surface were oxidized; however, the oxidation of Al progressed much faster than that of Ni. The oxidation of Al began to occur and AlOx was formed at an oxygen coverage of 0.26 monolayer (ML) (1 ML was defined as the atomic density of the Ni3Al (210) surface) and saturated at an oxygen coverage of 2.5 ML. In contrast, the oxidation of Ni commenced a little late at an oxygen coverage of 1.6 ML and slowly progressed to saturation, which occurred at an oxygen coverage of 4.89 ML.

Metal-like electrical conductivity in LaxSr2-xTiMoO6 oxides for high temperature thermoelectric power generation.

PubMed

Saxena, Mandvi; Maiti, Tanmoy

2017-05-09

Increasing electrical conductivity in oxides, which are inherently insulators, can be a potential route in developing oxide-based thermoelectric power generators with higher energy conversion efficiency. In the present work, environmentally friendly non-toxic double perovskite La x Sr 2-x TiMoO 6 (LSTM) ceramics were synthesized using a solid-state reaction route by optimizing the sintering temperature and atmosphere for high temperature thermoelectric applications. Rietveld refinement of XRD data confirmed a single-phase solid solution with a cubic structure in these double perovskites with the space-group Pm3[combining macron]m. SEM studies showed a highly dense microstructure in these ceramics. High electrical conductivity on the order of 10 5 S m -1 and large carrier concentration (∼10 22 cm -3 ) were obtained in these materials. The temperature-dependent electrical conductivity measurement showed that the LSTM ceramics exhibit a semiconductor to metal transition. Thermopower (S) measurements demonstrated the conductivity switching from a p-type to n-type behavior at higher temperature. A temperature dependent Seebeck coefficient was further explained using a model for coexistence of both types of charge carriers in these oxides. A conductivity mechanism of these double perovskites was found to be governed by a small polaron hopping model.

Hot corrosion behavior of platinum-modified nickel- and cobalt-based alloys and coatings

NASA Astrophysics Data System (ADS)

Deodeshmukh, Vinay Prakash

High temperature degradation by hot corrosion (650-1000°C) and/or oxidation (>1000°C) can severely reduce the longevity of advanced gas turbine engine components. The protection of high-temperature components against hot corrosion or oxidation is typically conferred by the application of either a diffusion or overlay metallic coating that is able to form a continuous, adherent, and slow-growing oxide scale. There are currently no coatings that provide adequate protection to both hot corrosion and oxidation. Indeed, there is a particular need for such protective coatings because many advanced aero, marine, and industrial gas-turbines operate in both hot corrosion and oxidation regimes in their duty cycle. Recent work at Iowa State University (ISU) has showed that a wide range Pt+Hf-modified gamma'-Ni3Al + gamma-Ni alloy compositions form a very adherent and slow-growing Al 2O3 scale. In fact, the results reported suggest that Pt+Hf-modified gamma' + gamma coatings offer a viable superior alternative to beta-NiAl(Pt)-based coatings. The main thrust of this study was to assess and establish optimum target gamma' + gamma coating compositions for extending the service life of high-temperature gas turbine components exposed to hot corrosion and oxidation conditions. Both high temperature hot-corrosion (HTHC-900°C) and low temperature hot-corrosion (LTHC-705°C) behaviors of the Pt+Hf-modified gamma' + gamma alloys were assessed. The salt used to bring about hot corrosion was Na 2SO4. Quite interestingly, it was found that the HTHC resistance of gamma' + gamma alloys improved with up to about 10 at.% Pt addition, but then decreased significantly with increasing Pt content up to 30 at.% (the maximum level studied); however, under LTHC conditions the resistance of gamma' + gamma alloys improved with increasing Pt content up to 30 at.%. To further improve hot corrosion resistance of Pt+Hf-modified gamma' + gamma alloys, the effects of systematic additions of Cr, Si, and Cr+Si were assessed. The effects pre-oxidation treatments were also studied to further improve the hot corrosion resistance. In addition, high-temperature oxidation behavior of various modified of gamma' + gamma alloys was studied in air at 1150°C under both isothermal and cyclic oxidation conditions. Certain modified versions of gamma' + gamma coating composition(s) exhibited excellent resistance to both hot corrosion and oxidation. Finally, the HTHC and LTHC resistance of novel Pt+Hf-modified gamma' + gamma-based diffusion coatings using a pack cementation process developed at ISU were studied and compared with state-of-the-art commercial coatings. It was found that the Pt+Hf-modified gamma' + gamma coating exhibited superior resistance to both types of hot corrosion with the preoxidation treatment; while, only Pt-modified beta exhibited excellent LTHC resistance with no pre-oxidation treatment. This study also involved evaluating the hot corrosion resistance of various commercially available Pt-modified beta-NiAl diffusion aluminides and CoCrAlY-based overlay coatings for marine gas turbine engine components under both HTHC and LTHC conditions. The Al-Pt-rich beta aluminide exhibited improved resistance to both types of hot corrosion compared to the various Ni-rich beta aluminide and CoCrAlY coatings.

Effect of negative bias on TiAlSiN coating deposited on nitrided Zircaloy-4

NASA Astrophysics Data System (ADS)

Jun, Zhou; Zhendong, Feng; Xiangfang, Fan; Yanhong, Liu; Huanlin, Li

2018-01-01

TiAlSiN coatings were deposited on the nitrided Zircaloy-4 by multi-arc ion plating at -100 V, -200 V and -300 V. In this study, the high temperature oxidation behavior of coatings was tested by a box-type resistance furnace in air for 3 h at 800 °C; the macro-morphology of coatings was observed and analyzed by a zoom-stereo microscope; the micro-morphology of coatings was analyzed by a scanning electron microscopy (SEM), and the chemical elements of samples were analyzed by an energy dispersive spectroscopy(EDS); the adhesion strength of the coating to the substrate was measured by an automatic scratch tester; and the phases of coatings were analyzed by an X-ray diffractometer(XRD). Results show that the coating deposited at -100 V shows better high temperature oxidation resistance behavior, at the same time, Al elements contained in the coating is of the highest amount, meanwhile, the adhesion strength of the coating to the substrate is the highest, which is 33N. As the bias increases, high temperature oxidation resistance behavior of the coating weakens first and then increases, the amount of large particles on the surface of the coating increases first and then decreases whereas the density of the coating decreases first and then increases, and adhesion strength of the coating to the substrate increases first and then weakens. The coating's quality is relatively poor when the bias is -200 V.

MoSi 2 Oxidation in 670-1498 K Water Vapor

DOE Office of Scientific and Technical Information (OSTI.GOV)

Sooby Wood, Elizabeth; Parker, Stephen S.; Nelson, Andrew T.

Molybdenum disilicide (MoSi 2) has well documented oxidation resistance at high temperature (T > 1273 K) in dry O 2 containing atmospheres due to the formation of a passive SiO 2 surface layer. But, its behavior under atmospheres where water vapor is the dominant species has received far less attention. Oxidation testing of MoSi 2 was performed at temperatures ranging from 670–1498 K in both 75% water vapor and synthetic air (Ar-O2, 80%–20%) containing atmospheres. Here the thermogravimetric and microscopy data describing these phenomena are presented. Over the temperature range investigated, MoSi 2 displays more mass gain in water vapormore » than in air. The oxidation kinetics observed in water vapor differ from that of the air samples. Two volatile oxides, MoO 2(OH) 2 and Si(OH) 4, are thought to be the species responsible for the varied kinetics, at 670–877 K and at 1498 K, respectively. Finally, we observed an increase in oxidation (140–300 mg/cm 2) from 980–1084 K in water vapor, where passivation is observed in air.« less

MoSi 2 Oxidation in 670-1498 K Water Vapor

DOE PAGES

Sooby Wood, Elizabeth; Parker, Stephen S.; Nelson, Andrew T.; ...

2016-03-08

Molybdenum disilicide (MoSi 2) has well documented oxidation resistance at high temperature (T > 1273 K) in dry O 2 containing atmospheres due to the formation of a passive SiO 2 surface layer. But, its behavior under atmospheres where water vapor is the dominant species has received far less attention. Oxidation testing of MoSi 2 was performed at temperatures ranging from 670–1498 K in both 75% water vapor and synthetic air (Ar-O2, 80%–20%) containing atmospheres. Here the thermogravimetric and microscopy data describing these phenomena are presented. Over the temperature range investigated, MoSi 2 displays more mass gain in water vapormore » than in air. The oxidation kinetics observed in water vapor differ from that of the air samples. Two volatile oxides, MoO 2(OH) 2 and Si(OH) 4, are thought to be the species responsible for the varied kinetics, at 670–877 K and at 1498 K, respectively. Finally, we observed an increase in oxidation (140–300 mg/cm 2) from 980–1084 K in water vapor, where passivation is observed in air.« less

Novel Iron-based ternary amorphous oxide semiconductor with very high transparency, electronic conductivity, and mobility

DOE PAGES

Malasi, A.; Taz, H.; Farah, A.; ...

2015-12-16

We report that ternary metal oxides of type (Me) 2O 3 with the primary metal (Me) constituent being Fe (66 atomic (at.) %) along with the two Lanthanide elements Tb (10 at.%) and Dy (24 at.%) can show excellent semiconducting transport properties. Thin films prepared by pulsed laser deposition at room temperature followed by ambient oxidation showed very high electronic conductivity (>5 × 10 4 S/m) and Hall mobility (>30 cm 2/V-s). These films had an amorphous microstructure which was stable to at least 500 °C and large optical transparency with a direct band gap of 2.85 ± 0.14 eV.more » This material shows emergent semiconducting behavior with significantly higher conductivity and mobility than the constituent insulating oxides. In conclusion, since these results demonstrate a new way to modify the behaviors of transition metal oxides made from unfilled d- and/or f-subshells, a new class of functional transparent conducting oxide materials could be envisioned.« less

Effects of Some Light Alloying Elements on the Oxidation Behavior of Fe and Ni-Cr Based Alloys During Air Plasma Spraying

NASA Astrophysics Data System (ADS)

Zeng, Zhensu; Kuroda, Seiji; Kawakita, Jin; Komatsu, Masayuki; Era, Hidenori

2010-01-01

The oxidation behavior of iron binary powders with addition of Si (1, 4 wt.%) and B (1, 3 wt.%) and that of a Ni-Cr based alloy powder with Si (4.3 wt.%), B (3.0 wt.%), and C (0.8 wt.%) additions during atmosphere plasma spray (APS) have been investigated. Analysis of the chemical composition and phases of oxides in the captured in-flight particles and deposited coatings was carried out. The results show that the addition of Si and B to iron effectively reduced the oxygen contents in the coatings, especially during the in-flight period at higher particles temperature. Ni-Cr based alloy powder with Si, B, and C additions reduced the oxidation of the base alloys significantly. Preferential oxidation and subsequent vaporization of Si, B, and C from the surface of the sprayed particles are believed to play a major role in controlling oxidation in the APS process.

Aging Behavior and Performance Projections for a Polysulfide Elastomer

DOE Office of Scientific and Technical Information (OSTI.GOV)

Celina, Mathias C.; Giron, Nicholas Henry; Quintana, Adam

The accelerated aging behavior and aging state of a 30 year old field retrieved polysulfide elastomer was examined. The material is used as an environmental thread sealant for a stainless steel bolt in a steel threaded insert in an aluminum assembly. It is a two component curable polysulfide elastomer that is commercially available in a similar formulation as was applied 30 years ago. The primary goal of this study was to establish if aging over 30 years under moderate aging conditions (mostly ambient temperature and humidity) resulted in significant property changes, or if accelerated aging could identify developing aging pathwaysmore » which would prevent the extended use of this material. The aging behavior of this material was examined in three ways: A traditional accelerated thermo-oxidative aging study between 95 to 140°C which focused on physical and chemical properties changes, an evaluation of the underlying oxidation rates between RT and 125°C, and an assessment of the aging state of a small 30 year old sample. All three data sets were used to establish aging characteristics, their time evolution, and to extrapolate the observed behavior to predict performance limits at RT. The accelerated aging study revealed a relatively high average activation energy of ~130 kJ/mol which gives overconfident performance predictions. Oxidation rates showed a decreasing behavior with aging time and a lower E a of ~84 kJ/mol from time - temperature superposition , but also predicted sufficient additional performance at RT. Consistent with these projections for extended RT performance, only small changes were observed for the 30 year old material. Extrapolations using this partially aged material also predict ongoing use as a viable option. Unexpected RT degradation could only develop into a concern should the oxidation rate not trend lower over time as was observed at elevated temperature. Considering all data acquired in this limited aging study , there are no immediately apparent concerns with this material for ongoing use. ACKNOWLEDGEMENTS We thank Lisa Deibler for providing us with a small sample of field aged and new commercial material.« less

Release kinetics of vanadium from vanadium (III, IV and V) oxides: Effect of pH, temperature and oxide dose.

PubMed

Hu, Xingyun; Yue, Yuyan; Peng, Xianjia

2018-05-01

Batch experiments were performed to derive the rate laws for the proton-promoted dissolution of the main vanadium (III, IV and V) oxides at pH 3.1-10.0. The release rates of vanadium are closely related to the aqueous pH, and several obvious differences were observed in the release behavior of vanadium from the dissolution of V 2 O 5 and vanadium(III, IV) oxides. In the first 2hr, the release rates of vanadium from V 2 O 3 were r=1.14·([H + ]) 0.269 at pH 3.0-6.0 and r=0.016·([H + ]) -0.048 at pH 6.0-10.0; the release rates from VO 2 were r=0.362·([H + ]) 0.129 at pH 3.0-6.0 and r=0.017·([H + ]) -0.097 at pH 6.0-10.0; and the release rates from V 2 O 5 were r=0.131·([H + ]) -0.104 at pH 3.1-10.0. The release rates of vanadium from the three oxides increased with increasing temperature, and the effect of temperature was different at pH 3.8, pH 6.0 and pH 7.7. The activation energies of vanadium (III, IV and V) oxides (33.4-87.5kJ/mol) were determined at pH 3.8, pH6.0 and pH 7.7, showing that the release of vanadium from dissolution of vanadium oxides follows a surface-controlled reaction mechanism. The release rates of vanadium increased with increasing vanadium oxides dose, albeit not proportionally. This study, as part of a broader study of the release behavior of vanadium, can help to elucidate the pollution problem of vanadium and to clarify the fate of vanadium in the environment. Copyright © 2017. Published by Elsevier B.V.

The Synthesis and Thermoelectric Properties of p-Type Li1- x NbO2-Based Compounds

NASA Astrophysics Data System (ADS)

Rahman, Jamil Ur; Meang, Eun-Ji; Van Nguyen, Du; Seo, Won-Seon; Hussain, Ali; Kim, Myong Ho; Lee, Soonil

2017-03-01

We investigated the thermoelectric (TE) properties of a p-type oxide material (Li1- x NbO2, with x = 0-0.6). The composition was synthesized via a solid-state reaction method under a reducing atmosphere. The charge transport properties were determined through the electrical conductivity and Seebeck coefficient measurements. The electrical conductivity was non-monotonically varied with x value and showed metallic behavior with increased temperature and above 650 K temperature independent behavior dominated by extrinsic conduction. On the other hand, the Seebeck coefficient was increased with an increase in the temperature, and decreased gradually with an increase in the Li vacancy concentration by both synthesis and gradual phase transition to a Li-rich Li3NbO4 phase with temperature and appeared as an n-type TE at x = 0.6 under high temperatures, which was attributed to an Nb substitution into the Li site. The thermal conductivity was monotonically reduced with the increase in temperature due to the cation disorder defects and second phases. The Li vacancy induced Li1- x NbO2-based compounds under low oxygen partial pressure show promise as a candidate p-type material for thermoelectric applications, particularly for co-processing with n-type oxide thermoelectric materials fabricated under conditions of low oxygen partial pressure.

Material Problems in Using High-Temperature Thermocouples

NASA Astrophysics Data System (ADS)

Edler, F.

2011-08-01

The material compatibility and thermal stability of ceramic-composite coatings of different oxide ceramics deposited on alumina tubes to prevent the reduction of the alumina were investigated in the high-temperature range between 1750 °C and 1850 °C. It turned out that the coatings were thermally unstable and did not provide adequate protection against the reduction of the alumina tubes. The oxide ceramics formed eutectic compositions with low melting temperatures and were also prone to reduction to elementary metals by carbon. A new type of high-temperature thermocouple on the basis of refractory and noble metals was tested in the temperature range between 1325 °C and 1800 °C. Two metal-sheathed prototypes were constructed. The thermoelectric behavior of the tungsten5%rhenium/iridium thermocouples (W5%Re/Ir) was investigated by different high-temperature exposures, and the thermoelectric stability was checked by repeated measurements at the ice point.

Oxidation Studies of SiAlON/MgAlON Ceramics with Fe2O3 and CaO Impurities, Part I: Kinetics

NASA Astrophysics Data System (ADS)

Li, Peng; Zhang, Mei; Teng, Lidong; Seetharaman, Seshadri

2013-02-01

T he oxidation behaviors of composites SiAlON/MgAlON phases (β-SiAlON, 15R-SiAlON and MgAlON) synthesized from the residue during the leaching treatment of salt cake and corresponding synthetic samples were investigated in air by thermogravimetric measurements. Combined kinetics, viz. linear law + arctan law + parabolic law, are used to describe the kinetics of oxidation in isothermal mode. The oxidation studies reveal the effects of impurities, namely, Fe2O3 and CaO, present in the salt cake residue. The addition of Fe2O3 results in a lower activation energy and more aggressive oxidation. The addition of CaO caused the shrinkage during the synthesis and liquid formation during the oxidation above 1673 K (1400 °C). The impurities of CaO and Fe2O3 in the leaching residue can result in an aggressive oxidation at low temperature and a protective oxidation at temperatures above the eutectic point.

Unified high-temperature behavior of thin-gauge superalloys

NASA Astrophysics Data System (ADS)

England, Raymond Oliver

This research proposes a methodology for accelerated testing in the area of high-temperature creep and oxidation resistance for thin-gauge superalloy materials. Traditional long-term creep (stress-relaxation) and oxidation tests are completed to establish a baseline. The temperature range used in this study is between 1200 and 1700°F. The alloys investigated are Incoloy MA 956, Waspaloy, Haynes 214, Haynes 242, Haynes 230, and Incoloy 718. The traditional creep test involves loading the specimens to a constant test mandrel radius of curvature, and measuring the retained radius of curvature as a function of time. The accelerated creep test uses a servohydraulic test machine to conduct single specimen, variable strain-rate load relaxation experiments. Standard metallographic evaluations are used to determine extent and morphology of attack in the traditional oxidation tests, while the accelerated oxidation test utilizes thermogravimetric analysis to obtain oxidation rate data. The traditional long-term creep testing indicates that the mechanically-alloyed material Incoloy MA 956 and Haynes alloy 214 may be suitable for long-term, high-temperature (above 1400°F) structural applications. The accelerated creep test produced a continuous linear function of log stress versus strain rate which can be used to calculate creep rate. The long-term and traditional oxidation tests indicate that Al2O3 scale formers such as Incoloy MA 956 and Haynes 214 are much more resistant to high-temperature oxidation than Cr2O3 scale formers such as Waspaloy. Both accelerated tests can be completed within roughly one day, and can evaluate multiple test temperatures using standardized single specimens. These simple experiments can be correlated with traditional long-term tests which require years to complete.

Influence of experimental parameters on iron oxide nanoparticle properties synthesized by thermal decomposition: size and nuclear magnetic resonance studies

NASA Astrophysics Data System (ADS)

Belaïd, Sarah; Stanicki, Dimitri; Vander Elst, Luce; Muller, Robert N.; Laurent, Sophie

2018-04-01

A study of the experimental conditions to synthesize monodisperse iron oxide nanocrystals prepared from the thermal decomposition of iron(III) acetylacetonate was carried out in the presence of surfactants and a reducing agent. The influence of temperature, synthesis time and surfactant amounts on nanoparticle properties is reported. This investigation combines relaxometric characterization and size properties. The relaxometric behavior of the nanomaterials depends on the selected experimental parameters. The synthesis of iron oxide nanoparticles with a high relaxivity and a high saturation magnetization can be obtained with a short reaction time at high temperature. Moreover, the influence of surfactant concentrations determines the optimal value in order to produce iron oxide nanoparticles with a narrow size distribution. The optimized synthesis is rapid, robust and reproductive, and produces nearly monodisperse magnetic nanocrystals.

Thermoelectric Properties of the Perovskite-Type Oxide SrTi1-xNbxO3 Synthesized by Solid-State Reaction Method

NASA Astrophysics Data System (ADS)

Khan, Tamal Tahsin; Ur, Soon-Chul

2018-05-01

The perovskite-type oxide materials SrTi1-xNbxO3 (X = .02, 0.03, 0.04, 0.05 and 0.06) were synthesized by the conventional solid-state reaction method and the thermoelectric properties in terms of Nb doping at the B-site in the oxides were investigated in this study. The formation of single phase cubic perovskite structure was confirmed by the powder X-ray diffraction analysis. Negative conduction is shown in this materials system. The absolute value of Seebeck coefficient increased with increasing temperature over the measured temperature. The electrical conductivity decreased monotonically with increasing temperature, showing degenerating conduction behavior. The thermal conductivity, k, generally decreased with increasing temperature. The power factor increased with increasing Nb-doping level up to 5.0 mol% and hence the dimensionless figure of merit ZT, increased up to 5.0 mol%. The maximum ZT value was observed for SrTi0.95Nb0.05O3 at 873 K.

Carrier-selective interlayer materials for silicon solar cell contacts

NASA Astrophysics Data System (ADS)

Xue, Muyu; Islam, Raisul; Chen, Yusi; Chen, Junyan; Lu, Ching-Ying; Mitchell Pleus, A.; Tae, Christian; Xu, Ke; Liu, Yi; Kamins, Theodore I.; Saraswat, Krishna C.; Harris, James S.

2018-04-01

This work presents titanium oxide (TiOx) and nickel oxide (NiOx) as promising carrier-selective interlayer materials for metal-interlayer-semiconductor contacts for silicon solar cells. The electron-conducting, hole-blocking behavior of TiOx and the opposite carrier-selective behavior of NiOx are investigated using the transmission-line-method. The Fermi level depinning effect and the tunneling resistance are demonstrated to be dependent on the interlayer oxide thickness and annealing temperature. NiOx is furthermore experimentally demonstrated to be capable of improving the effective minority carrier lifetime by quasi-steady-state photoconductance method. Our study demonstrates that TiOx and NiOx can be effective carrier-selective materials for Si solar cells and provides a framework for characterizing carrier-selective contacts.

Temperature-dependent photoluminescence of CuAlO2 single crystals fabricated by using a flux self-removal method

NASA Astrophysics Data System (ADS)

Nam, Y. S.; Yoon, J. S.; Ju, H. L.; Chang, S. K.; Baek, K. S.

2014-10-01

The temperature-dependent behavior of p-type transparent semiconducting oxide CuAlO2 single crystals prepared by using a flux self-removal method in alumina crucibles was investigated through transmittance and photoluminescence (PL) measurements at temperatures from 12 K to room temperature. The low-temperature (12 K) PL spectrum shows two weak, broad emission peaks, one at 3.52 eV and the other at 3.08 eV, which we assign to excitonic emission and to defectrelated emission originating from copper vacancies. The positions of the PL peaks as functions of temperature exhibit a normal behavior satisfying the standard Varshini law, and the Debye temperature is found to be θ D = 610 ± 80 K. The exciton-binding energy of the CuAlO2 single crystal is estimated to be 49 meV from the PL intensity change with temperature.

Development of Brazing Technology for Use in High- Temperature Gas Separation Equipment

DOE Office of Scientific and Technical Information (OSTI.GOV)

Weil, K.S.; Hardy, J.S.; Kim, J.Y.

2003-04-23

The development of high-temperature electrochemical devices such as oxygen and hydrogen separators, fuel gas reformers, solid oxide fuel cells, and chemical sensors is part of a rapidly expanding segment of the solid state technology market. These devices employ an ionic conducting ceramic as the active membrane that establishes the electrochemical potential of the device, either under voltage (i.e. to carry out gas separation) or under chemical gradient (to develop an electrical potential and thereby generate electrical power). Because the device operates under an ionic gradient that develops across the electrolyte, hermiticity across this layer is paramount. That is, not onlymore » must this thin ceramic membrane be dense with no interconnected porosity, but it must be connected to the rest of the device, typically constructed from a heat resistant alloy, with a high-temperature, gas-tight seal. A significant engineering challenge in fabricating these devices is how to effectively join the thin electrochemically active membrane to the metallic body of the device such that the resulting seal is hermetic, rugged, and stable during continuous high temperature operation. Active metal brazing is the typical method of joining ceramic and metal engineering components. It employs a braze alloy that contains one or more reactive elements, often titanium, which will chemically reduce the ceramic faying surface and greatly improve its wetting behavior and adherence with the braze. However, recent studies of these brazes for potential use in fabricating high-temperature electrochemical devices revealed problems with interfacial oxidation and subsequent joint failure [1,2]. Specifically, it was found that the introduction of the ceramic electrolyte and/or heat resistant metal substrate dramatically affects the inherent oxidation behavior of the braze, often in a deleterious manner. These conclusions pointed to the need for an oxidation resistant, high-temperature ceramic-to-metal braze and consequently lead to the development of the novel reactive air brazing (RAB) concept. The goal in RAB is to reactively modify one or both oxide faying surfaces with an oxide compound dissolved in a molten noble metal alloy such that the newly formed surface is readily wetted by the remaining liquid filler material. In many respects, this concept is similar to active metal brazing, except that joining can be conducted in air and the final joint will be resistant to oxidation at high temperature. Potentially, there are a number of metal oxide-noble metal systems that can be considered for RAB, including Ag-CuO, Ag-V2O5, and Pt-Nb2O5. Our current interest is in determining whether the Ag-CuO system is suitable for air brazing functional ceramic-to-metal joints such as those needed in practical electrochemical devices. In a series of studies, the wetting behavior of the Ag-CuO braze was investigated with respect to a number of potential hydrogen separation, oxygen separation, and fuel cell electrolyte membrane materials and heat resistant metal systems, including: alumina, (La0.6Sr0.4)(Co0.2Fe0.8)O3, (La0.8Sr0.2)FeO3, YSZ, fecralloy, and Crofer-22APU. Selected findings from these studies as well as from our work on joint strength and durability during high-temperature exposure testing will be discussed.« less

Creep performance of oxide ceramic fiber materials at elevated temperature in air and in steam

NASA Astrophysics Data System (ADS)

Armani, Clinton J.

Structural aerospace components that operate in severe conditions, such as extreme temperatures and detrimental environments, require structural materials that have superior long-term mechanical properties and that are thermochemically stable over a broad range of service temperatures and environments. Ceramic matrix composites (CMCs) capable of excellent mechanical performance in harsh environments are prime candidates for such applications. Oxide ceramic materials have been used as constituents in CMCs. However, recent studies have shown that high-temperature mechanical performance of oxide-oxide CMCs deteriorate in a steam-rich environment. The degradation of strength at elevated temperature in steam has been attributed to the environmentally assisted subcritical crack growth in the oxide fibers. Furthermore, oxide-oxide CMCs have shown significant increases in steady-state creep rates in steam. The present research investigated the effects of steam on the high-temperature creep and monotonic tension performance of several oxide ceramic materials. Experimental facilities were designed and configured, and experimental methods were developed to explore the influence of steam on the mechanical behaviors of ceramic fiber tows and of ceramic bulk materials under temperatures in the 1100--1300°C range. The effects of steam on creep behavior of Nextel(TM)610 and Nextel(TM)720 fiber tows were examined. Creep rates at elevated temperatures in air and in steam were obtained for both types of fibers. Relationships between creep rates and applied stresses were modeled and underlying creep mechanisms were identified. For both types of fiber tows, a creep life prediction analysis was performed using linear elastic fracture mechanics and a power-law crack velocity model. These results have not been previously reported and have critical design implications for CMC components operating in steam or near the recommended design limits. Predictions were assessed and validated via comparisons with experimental results. Additionally, the utility of the Monkman-Grant relationship to predicting creep-rupture life of the fiber tows at elevated temperature in air and in steam was demonstrated. Furthermore, the effects of steam on the compressive creep performance of bulk ceramic materials were also studied. Performance of fine grained, polycrystalline alumina (Al2O3) was investigated at 1100 and 1300°C in air and in steam. To evaluate the effect of silica doping during material processing both undoped and silica doped polycrystalline alumina specimens were tested. Finally, compressive creep performance of yttrium aluminum garnet (YAG, Y3Al5O12) was evaluated at 1300°C in air and in steam. Both undoped and silica doped YAG specimens were included in the study. YAG is being considered as the next-generation oxide fiber material. However, before considerable funding and effort are invested in a fiber development program, it is necessary to evaluate the creep performance of YAG at elevated temperature in steam. Results of this research demonstrated that both the undoped YAG and the silica doped YAG exhibited exceptional creep resistance at 1300°C in steam for grain sizes ˜1 microm. These results supplement the other promising features of YAG that make it a strong candidate material for the next generation ceramic fiber.

Defect and adsorbate induced ferromagnetic spin-order in magnesium oxide nanocrystallites

NASA Astrophysics Data System (ADS)

Kumar, Ashok; Kumar, Jitendra; Priya, Shashank

2012-05-01

We report the correlation between d0 ferromagnetism, photoluminescence (PL), and adsorbed hydrogen (H-) species in magnesium oxide (MgO) nanocrystallites. Our study suggests that the oxygen vacancies, namely singly ionized anionic vacancies (F+) and dimers (F22+) induce characteristic photoluminescence and the room-temperature ferromagnetic spin-order. Nanocrystallites with low population of oxygen vacancies have revealed diamagnetic behavior. Intriguingly, on adsorption of hydrogen (H-) species in the MgO nanocrystallites, ferromagnetic behavior was either enhanced (in the case of highly oxygen deficient nanocrystallites) or begun to percolate (in the case of nanocrystallite with low population density of oxygen vacancies).

Low Temperature Film Growth of the Oxides of Zinc, Aluminum, and Vanadium (and Related Systems, Oxides of Gold and Germanium, Nitrides of Aluminum and Tungsten) by Reactive Sputter Deposition.

DTIC Science & Technology

1988-02-01

the optical behavior of the material in its preswitched, or A Perkin-Elmer Model 330 UV - Visible -IR double beam ,% spectrophotometer with a specular...S ~ * ." at.* U a * . a. *%~ ~9g 0 ~ --- a.. ’ a * ~ .r~vaa- *a,~ * ~ * ~****.,*a,* *** UV - Visible -IR Optical Behavior of Sputter Deposited Gee x...Films deposited in 0 to 60% Ar were nominally germania. However, transmission in the UV - visible , the strength of the 245nm defect center, the optical

Temperature-Dependent Effects on the Mechanical Behavior and Deformation Substructure of Haynes 188 Under Low-Cycle Fatigue

NASA Technical Reports Server (NTRS)

1996-01-01

The mechanical behavior of a cobalt-nickel-chromium-tungsten superalloy, Haynes 188, is being critically examined at the NASA Lewis Research Center. This dynamic, strain-aging (DSA) alloy is used for combustor liners in many military and commercial aircraft turbine engines and for the liquid oxygen posts in the main injectors of the space shuttle main engine. Its attractive features include a good combination of high monotonic yield and tensile strength, and excellent fabricability, weldability, and resistance to high-temperature oxidation for prolonged exposures.

Very High Output Thermoelectric Devices Based on ITO Nanocomposites

NASA Technical Reports Server (NTRS)

Fralick, Gustave; Gregory, Otto J.

2009-01-01

A material having useful thermoelectric properties was synthesized by combining indium-tin-oxide (ITO) with a NiCoCrAlY alloy/alumina cermet. This material had a very large Seebeck coefficient with electromotive-force-versustemperature behavior that is considered to be excellent with respect to utility in thermocouples and other thermoelectric devices. When deposited in thin-film form, ceramic thermocouples offer advantages over precious-metal (based, variously, on platinum or rhodium) thermocouples that are typically used in gas turbines. Ceramic thermocouples exhibit high melting temperatures, chemical stability at high temperatures, and little or no electromigration. Oxide ceramics also resist oxidation better than metal thermocouples, cost substantially less than precious-metal thermocouples, and, unlike precious-metal thermocouples, do not exert catalytic effects.

Inhibition effect in supercritical water oxidation of hydroquinone

DOE Office of Scientific and Technical Information (OSTI.GOV)

Thammanayakatip, C.; Oshima, Yoshito; Koda, Seiichiro

1998-05-01

In the oxidation reactions of hydroquinone under a supercritical conditions (temperature of 683 K and pressure of 24.5 MPa), the conversion was found to become saturated despite the very fast initial reaction. This behavior was quite different from that under a subcritical condition (temperature of 633 K and pressure of 24.5 MPa). Under both conditions, p-benzoquinone was found to be an important intermediate. The yield of CO{sub 2} was very small, which indicates a strong inhibition effect of hydroquinone and/or its derivatives. These inhibition phenomena should be taken into account very carefully in the application of supercritical water oxidation formore » treating waste organic materials where a complete decomposition is very important.« less

Processing, Structure and High Temperature Oxidation Properties of Polymer-Derived and Hafnium Oxide Based Ceramic Systems

NASA Astrophysics Data System (ADS)

Terauds, Kalvis

Demands for hypersonic aircraft are driving the development of ultra-high temperature structural materials. These aircraft, envisioned to sustain Mach 5+, are expected to experience continuous temperatures of 1200--1800°C on the aircraft surface and temperatures as high as 2800°C in combustion zones. Breakthroughs in the development of fiber based ceramic matrix composites (CMCs) are opening the door to a new class of high-tech UHT structures for aerospace applications. One limitation with current carbon fiber or silicon carbide fiber based CMC technology is the inherent problem of material oxidation, requiring new approaches for protective environmental barrier coatings (EBC) in extreme environments. This thesis focuses on the development and characterization of SiCN-HfO2 based ceramic composite EBC systems to be used as a protective layer for silicon carbide fiber based CMCs. The presented work covers three main architectures for protection (i) multilayer films, (ii) polymer-derived HfSiCNO, and (iii) composite SiCN-HfO 2 infiltration. The scope of this thesis covers processing development, material characterization, and high temperature oxidation behavior of these three SiCN-HfO2 based systems. This work shows that the SiCN-HfO 2 composite materials react upon oxidation to form HfSiO4, offering a stable EBC in streaming air and water vapor at 1600°C.

SiC Nanoparticles Toughened-SiC/MoSi2-SiC Multilayer Functionally Graded Oxidation Protective Coating for Carbon Materials at High Temperatures

NASA Astrophysics Data System (ADS)

Abdollahi, Alireza; Ehsani, Naser; Valefi, Zia; Khalifesoltani, Ali

2017-05-01

A SiC nanoparticle toughened-SiC/MoSi2-SiC functionally graded oxidation protective coating on graphite was prepared by reactive melt infiltration (RMI) at 1773 and 1873 K under argon atmosphere. The phase composition and anti-oxidation behavior of the coatings were investigated. The results show that the coating was composed of MoSi2, α-SiC and β-SiC. By the variations of Gibbs free energy (calculated by HSC Chemistry 6.0 software), it could be suggested that the SiC coating formed at low temperatures by solution-reprecipitation mechanism and at high temperatures by gas-phase reactions and solution-reprecipitation mechanisms simultaneously. SiC nanoparticles could improve the oxidation resistance of SiC/MoSi2-SiC multiphase coating. Addition of SiC nanoparticles increases toughness of the coating and prevents spreading of the oxygen diffusion channels in the coating during the oxidation test. The mass loss and oxidation rate of the SiC nanoparticle toughened-SiC/MoSi2-SiC-coated sample after 10-h oxidation at 1773 K were only 1.76% and 0.32 × 10-2 g/cm3/h, respectively.

Influence of temperature on oxidation mechanisms of fiber-textured AlTiTaN coatings.

PubMed

Khetan, Vishal; Valle, Nathalie; Duday, David; Michotte, Claude; Delplancke-Ogletree, Marie-Paule; Choquet, Patrick

2014-03-26

The oxidation kinetics of AlTiTaN hard coatings deposited at 265 °C by DC magnetron sputtering were investigated between 700 and 950 °C for various durations. By combining dynamic secondary ion mass spectrometry (D-SIMS), X-ray diffraction (XRD), and transmission electron microscopy (TEM) investigations of the different oxidized coatings, we were able to highlight the oxidation mechanisms involved. The TEM cross-section observations combined with XRD analysis show that a single amorphous oxide layer comprising Ti, Al, and Ta formed at 700 °C. Above 750 °C, the oxide scale transforms into a bilayer oxide comprising an Al-rich upper oxide layer and a Ti/Ta-rich oxide layer at the interface with the coated nitride layer. From the D-SIMS analysis, it could be proposed that the oxidation mechanism was governed primarily by inward diffusion of O for temperatures of ≤700 °C, while at ≥750 °C, it is controlled by outward diffusion of Al and inward diffusion of O. Via a combination of structural and chemical analysis, it is possible to propose that crystallization of rutile lattice favors the outward diffusion of Al within the AlTiTa mixed oxide layer with an increase in the temperature of oxidation. The difference in the mechanisms of oxidation at 700 and 900 °C also influences the oxidation kinetics with respect to oxidation time. Formation of a protective alumina layer decreases the rate of oxidation at 900 °C for long durations of oxidation compared to 700 °C. Along with the oxidation behavior, the enhanced thermal stability of AlTiTaN compared to that of the TiAlN coating is illustrated.

The effect of thermal pre-treatment of titanium hydride (TiH2) powder in argon condition

NASA Astrophysics Data System (ADS)

Franciska P., L.; Erryani, Aprilia; Annur, Dhyah; Kartika, Ika

2018-04-01

Titanium hydride (TiH2) powders are used to enhance the foaming process in the formation of a highly porous metallic material with a cellular structure. But, the low temperature of hydrogen release is one of its problems. The present study, different thermal pre-treatment temperatures were employed to investigate the decomposition behavior of TiH2 to retard or delay a hydrogen gas release process during foaming. As a foaming agent, TiH2 was subjected to various heat treatments prior at 450 and 500°C during 2 hours in argon condition. To study the formation mechanism, the thermal behavior of titanium hydride and hydrogen release are investigated by thermogravimetric analysis (TGA) and differential thermal analysis (DTA). The morphology of pre-treated titanium hydride powders were examined using Scanning Electron Microscope (SEM) while unsure mapping and elemental composition of the pre-treated powders processed by Energy Dispersive Spectroscopy (EDS). To study the phase formation was characterized by X-ray diffraction analysis (XRD). In accordance with the results, an increase in pre-treatment temperature of TiH2 to higher degrees are changing the process of releasing hydrogen from titanium hydride powder. DTA/TGA results showed that thermal pre-treatment TiH2 at 450°C, released the hydrogen gas at 560°C in heat treatment when foaming process. Meanwhile, thermal pre-treatment in TiH2 at 500°C, released the hydrogen gas at 670°C when foaming process. There is plenty of direct evidence for the existence of oxide layers that showed by EDS analysis obtained in SEM. As oxygen is a light element and qualitative proof shows that the higher pre-treatment temperature produces more and thicker oxygen layers on the surface of the TiH2 powder particles. It might the thickness of oxide layer are different from different pre-treatment temperatures, which leading to the differences in the decomposition temperature. But from SEM result that oxidation of the powder does not change the powder morphology. The oxidation process also confirmed by XRD result, which showed higher thermal pre-treatment TiH2, more oxide higher peak is formed. The oxide layer of TiH2 particles is responsible for the observed shift in decomposition temperature and can prepare the stable foam that stabilizes forming of cell walls and avoid their collapse at higher temperatures.

Oxidation behavior of grain boundary engineered alloy 690 in supercritical water environment

NASA Astrophysics Data System (ADS)

Xu, P.; Zhao, L. Y.; Sridharan, K.; Allen, T. R.

2012-03-01

Nickel-base alloy is an important structural material that is known for its exceptional high temperature oxidation resistance. Oxidation in this alloy at high temperatures occurs to a greater extent along the grain boundaries. Grain boundary engineering (GBE) was applied to modify the grain boundary characteristics of this alloy to affect its oxidation resistance. Specimens with both low level and high level cold works showed a high fraction of special grain boundaries, and were tested for supercritical water oxidation resistance at 500 °C and 24 MPa. Both GBE and as-received samples exhibited mass gain followed by mass loss during 10 weeks of exposure, but the normalized mass change was small and less than 0.12 mg/cm2. GBE samples showed better oxide layer retention compared to the as-received sample. XRD results indicate that nickel oxide, chromium oxide, and spinel oxide were the three main types of oxides that form on as-received and GBE alloy 690. Three distinct regions were identified on the oxidized surface: a flat region with oxide flakes aligning relatively parallel to the surface, a rough region with polygon-type oxide particles randomly distributed on the surface, and a region with aggregated oxide flakes perpendicular to the surface. The flat region of oxidation consisted of (1 1 1) orientated oxide spinel flakes formed on (1 1 1) oriented alloy 690 grains. The flat oxide region was thinner and showed better oxide adhesion compared to the rough region. Chromium oxidation was found only at random grain boundaries, leading to formation of thick Cr2O3 layer on the surface and chromium depletion underneath. None of this oxidation was found at low angle or special boundaries. The chromium oxidation was attributed to fast chromium diffusion through random boundaries and mechanically deformed regions such as scratches left after polishing. It is envisioned that the oxidation behavior of alloy 690 in supercritical water can be tailored by microstructure engineering that involves changes in grain orientation and grain boundary character distribution.

A molecular beam mass spectrometric study of the formation and photolysis of C(lc)lO dimer

NASA Technical Reports Server (NTRS)

Greene, Frank T.; Robaugh, David A.

1992-01-01

A study of the chlorine oxides present at temperatures and pressures typical of the Antarctic stratosphere was carried out. A series of low temperature flow reactors was constructed and used in conjunction with molecular beam mass spectrometric techniques to identify species and characterize their kinetic behavior at temperatures of -20 to -70 C and pressures of from 30 to 130 Torr. It was found that the gas phase chlorine-oxygen system was quite complex at low temperatures. ClO dimer was identified and found to be thermodynamically very stable under stratospheric conditions. It was also found that any system which contained ClO also contained a larger oxide. The oxide was identified as Cl2O3. A survey of possible higher oxides, which have been postulated as possible chlorine sinks in the stratosphere, was also carried out. The rate of formation of ClO dimer was measured as a function of temperature and pressure. Measurements were made of both the decay of ClO and the formation of the dimer. By comparing these rates it was determined that virtually all of the ClO was converted to the dimer under stratospheric conditions, and that the other ClO reactions were not important under these conditions.

A review on chemiresistive room temperature gas sensors based on metal oxide nanostructures, graphene and 2D transition metal dichalcogenides.

PubMed

Joshi, Nirav; Hayasaka, Takeshi; Liu, Yumeng; Liu, Huiliang; Oliveira, Osvaldo N; Lin, Liwei

2018-03-10

Room-temperature (RT) gas sensing is desirable for battery-powered or self-powered instrumentation that can monitor emissions associated with pollution and industrial processes. This review (with 171 references) discusses recent advances in three types of porous nanostructures that have shown remarkable potential for RT gas sensing. The first group comprises hierarchical oxide nanostructures (mainly oxides of Sn, Ni, Zn, W, In, La, Fe, Co). The second group comprises graphene and its derivatives (graphene, graphene oxides, reduced graphene oxides, and their composites with metal oxides and noble metals). The third group comprises 2D transition metal dichalcogenides (mainly sulfides of Mo, W, Sn, Ni, also in combination with metal oxides). They all have been found to enable RT sensing of gases such as NOx, NH 3 , H 2 , SO 2 , CO, and of vapors such as of acetone, formaldehyde or methanol. Attractive features also include high selectivity and sensitivity, long-term stability and affordable costs. Strengths and limitations of these materials are highlighted, and prospects with respect to the development of new materials to overcome existing limitations are discussed. Graphical Abstract The review summarizes the most significant progresses related to room temperature gas sensing by using hierarchical oxide nanostructures, graphene and its derivatives and 2D transition metal dichalcogenides, highlighting the peculiar gas sensing behavior with enhanced selectivity, sensitivity and long-term stability.

Low temperature oxidation of benzene and toluene in mixture with n-decane

PubMed Central

Herbinet, Olivier; Husson, Benoit; Ferrari, Maude; Glaude, Pierre-Alexandre; Battin-Leclerc, Frédérique

2013-01-01

The oxidation of two blends, benzene/n-decane and toluene/n-decane, was studied in a jet-stirred reactor with gas chromatography analysis (temperatures from 500 to 1100 K, atmospheric pressure, stoichiometric mixtures). The studied hydrocarbon mixtures contained 75% of aromatics in order to highlight the chemistry of the low-temperature oxidation of these two aromatic compounds which have a very low reactivity compared to large alkanes. The difference of behavior between the two aromatic reactants is highly pronounced concerning the formation of derived aromatic products below 800 K. In the case of benzene, only phenol could be quantified. In the case of toluene, significant amounts of benzaldehyde, benzene, and cresols were also formed, as well as several heavy aromatic products such as bibenzyl, phenylbenzylether, methylphenylbenzylether, and ethylphenylphenol. A comparison with results obtained with neat n-decane showed that the reactivity of the alkane is inhibited by the presence of benzene and, to a larger extent, toluene. An improved model for the oxidation of toluene was developed based on recent theoretical studies of the elementary steps involved in the low-temperature chemistry of this molecule. Simulations using this model were successfully compared with the obtained experimental results. PMID:23762017

Novel gradient-diameter magnetic nanowire arrays with unconventional magnetic anisotropy behaviors.

PubMed

Wang, Jing; Zuo, Zhili; Huang, Liang; Warsi, Muhammad Asif; Xiao, John Q; Hu, Jun

2018-06-21

Fe-Co-Ni gradient-diameter magnetic nanowire arrays were fabricated via direct-current electrodeposition into a tapered anodic aluminium oxide template. In contrast to the magnetic behaviors of uniform-diameter nanowire arrays, these arrays exhibited tailorable magnetic anisotropy that can be used to switch magnetic nanowires easily and unconventional temperature-dependent coercivity with much better thermal stability.

Windows(Registered Trademark)-Based Software Models Cyclic Oxidation Behavior

NASA Technical Reports Server (NTRS)

Smialek, J. L.; Auping, J. V.

2004-01-01

Oxidation of high-temperature aerospace materials is a universal issue for combustion-path components in turbine or rocket engines. In addition to the question of the consumption of material due to growth of protective scale at use temperatures, there is also the question of cyclic effects and spallation of scale on cooldown. The spallation results in the removal of part of the protective oxide in a discontinuous step and thereby opens the way for more rapid oxidation upon reheating. In experiments, cyclic oxidation behavior is most commonly characterized by measuring changes in weight during extended time intervals that include hundreds or thousands of heating and cooling cycles. Weight gains occurring during isothermal scale-growth processes have been well characterized as being parabolic or nearly parabolic functions of time because diffusion controls reaction rates. In contrast, the net weight change in cyclic oxidation is the sum of the effects of the growth and spallation of scale. Typically, the net weight gain in cyclic oxidation is determined only empirically (that is, by measurement), with no unique or straightforward mathematical connection to either the rate of growth or the amount of metal consumed. Thus, there is a need for mathematical modeling to infer spallation mechanisms. COSP is a computer program that models the growth and spallation processes of cyclic oxidation on the basis of a few elementary assumptions that were discussed in COSP: A Computer Model of Cyclic Oxidation, Oxidation of Metals, vol. 36, numbers 1 and 2, 1991, pages 81-112. Inputs to the model include the selection of an oxidation-growth law and a spalling geometry, plus oxide-phase, growth-rate, cycle-duration, and spall-constant parameters. (The spalling fraction is often shown to be a constant factor times the existing amount of scale.) The output of COSP includes the net change in weight, the amounts of retained and spalled oxide, the total amounts of oxygen and metal consumed, and the terminal rates of weight loss and metal consumption.

Muon Sites in Transition Metal Oxides.

NASA Astrophysics Data System (ADS)

Chan, Kwaichow Benjamin

Muon behavior in a selected series of transition -metal oxides has been investigated by the Muon Spin Rotation (muSR) technique. The materials studied are the corundum structured oxides (M_2 O_3: M = Fe, Cr, V, Ti) and the high-Tc superconducting oxides in Y-Ba-Cu-O system. The muon is first implanted into the oxide crystalline and its subsequent behavior in the presence of magnetic field is monitored through counting the positron emitted by the decayed muon. The muon is found to behave like a free muon and to become localized at low temperatures and diffusional at higher temperatures. The location of the muon is important for interpreting the muSR data. To identify muon sites, a combination of electrostatic potential and magnetic dipolar field calculation is used. Dipole -field calculation allows matching the experimental results to the calculated values if the origin of the magnetic field is dominantly dipolar as in the case of V _2O_3 and Cr _2O_3. In the potential model, in addition to the coulombic interaction, the muon is assumed to form a muon-oxygen bond in analogy to the hydroxyl bond (OH)^-. Morse potential is used to simulate the mu^+ -O^= bonding. The potential minima found are then assigned as muon sites. A set of muon sites thus found in these oxides are their implications are presented. The inadequacies of the classical model and a more realistic model for predicting muon sites are also discussed.

High-temperature investigation on morphology, phase and size of iron/iron-oxide core–shell nanoclusters for radiation nanodetector

NASA Astrophysics Data System (ADS)

Khanal, Lokendra Raj; Williams, Thomas; Qiang, You

2018-06-01

Iron/iron-oxide (Fe–Fe3O4) core–shell nanoclusters (NCs) synthesized by a cluster deposition technique were subjected to a study of their high temperature structural and morphological behavior. Annealing effects have been investigated up to 800 °C in vacuum, oxygen and argon environments. The ~18 nm average size of the as-prepared NCs increases slowly in temperatures up to 500 °C in all three environments. The size increases abruptly in the argon environment but slowly in vacuum and oxygen when annealed at 800 °C. The x-ray diffraction (XRD) studies have shown that the iron core remains in the core–shell NCs only when they were annealed in the vacuum. A dramatic change in the surface morphology, an island like structure and/or a network like pattern, was observed at the elevated temperature. The as-prepared and annealed samples were analyzed using XRD, scanning electron microscopy and imageJ software for a close inspection of the temperature aroused properties. This work presents the temperature induced size growth mechanism, oxidation kinetics and phase transformation of the NCs accompanied by cluster aggregation, particle coalescence, and diffusion.

High-Temperature Behavior of a NiCr-Coated T91 Boiler Steel in the Platen Superheater of Coal-Fired Boiler

NASA Astrophysics Data System (ADS)

Chatha, Sukhpal Singh; Sidhu, Hazoor S.; Sidhu, Buta S.

2013-06-01

Ni-20Cr coating was deposited on T91 boiler tube steel by high-velocity oxy-fuel (HVOF) process to enhance high-temperature oxidation resistance. High-temperature performance of bare, as well as HVOF-coated steel specimens was evaluated for 1500 h under in the platen superheater zone of coal-fired boiler, where the temperature was around 900 °C. Experiments were carried out for 15 cycles, each of 100-h duration followed by 1-h cooling at ambient temperature. The extent of degradation of the specimens was assessed by the thickness loss and depth of internal corrosion attack. Ni-20Cr-coated steel performed better than the uncoated steel in actual boiler environment. The improved degradation resistance of Ni-20Cr coating can be attributed to the presence of Cr2O3 in the top oxide scale and dense microstructure.

Room-temperature ferroelectricity of SrTiO{sub 3} films modulated by cation concentration

DOE Office of Scientific and Technical Information (OSTI.GOV)

Yang, Fang; Zhang, Qinghua; Yang, Zhenzhong

2015-08-24

The room-temperature ferroelectricity of SrTiO{sub 3} is promising for oxide electronic devices controlled by multiple fields. An effective way to control the ferroelectricity is highly demanded. Here, we show that the off-centered antisite-like defects in SrTiO{sub 3} films epitaxially grown on Si (001) play the determinative role in the emergence of room-temperature ferroelectricity. The density of these defects changes with the film cation concentration sensitively, resulting in a varied coercive field of the ferroelectric behavior. Consequently, the room-temperature ferroelectricity of SrTiO{sub 3} films can be effectively modulated by tuning the temperature of metal sources during the molecular beam epitaxy growth.more » Such an easy and reliable modulation of the ferroelectricity enables the flexible engineering of multifunctional oxide electronic devices.« less

OXIDATION OF INCONEL 718 IN AIR AT TEMPERATURES FROM 973K TO 1620K.

DOE Office of Scientific and Technical Information (OSTI.GOV)

GREENE,G.A.; FINFROCK,C.C.

2000-10-01

As part of the APT project, it was necessary to quantify the release of tungsten from the APT spallation target during postulated accident conditions in order to develop accident source terms for accident consequence characterization. Experiments with tungsten rods at high temperatures in a flowing steam environment characteristic of postulated accidents revealed that considerable vaporization of the tungsten occurred as a result of reactions with the steam and that the aerosols which formed were readily transported away from the tungsten surfaces, thus exposing fresh tungsten to react with more steam. The resulting tungsten release fractions and source terms were undesirablemore » and it was decided to clad the tungsten target with Inconel 718 in order to protect it from contact with steam during an accident and mitigate the accident source term and the consequences. As part of the material selection criteria, experiments were conducted with Inconel 718 at high temperatures to evaluate the rate of oxidation of the proposed clad material over as wide a temperature range as possible, as well as to determine the high-temperature failure limit of the material. Samples of Inconel 718 were inserted into a preheated furnace at temperatures ranging from 973 K to 1620 K and oxidized in air for varying periods of time. After oxidizing in air at a constant temperature for the prescribed time and then being allowed to cool, the samples would be reweighed to determine their weight gain due to the uptake of oxygen. From these weight gain measurements, it was possible to identify three regimes of oxidation for Inconel 718: a low-temperature regime in which the samples became passivated after the initial oxidation, an intermediate-temperature regime in which the rate of oxidation was limited by diffusion and exhibited a constant parabolic rate dependence, and a high-temperature regime in which material deformation and damage accompanied an accelerated oxidation rate above the parabolic regime. At temperatures below 1173 K, the rate of oxidation of the Inconel 718 surface was found to decrease markedly with time; the parabolic oxidation rate coefficient was not a constant but decreased with time. This was taken to indicate that the oxide film on the surface was having a passivating effect on oxygen transport through the oxide to the underlying metal. For temperatures in the range 1173 K to 1573 K, the time-dependent rate of oxidation as determined once again by weight-gain measurements was found to display the classical parabolic rate behavior, indicating that the rate of transport of reactants through the oxide was controlled by diffusion through the growing oxide layer. Parabolic rate coefficients were determined by least-squares analysis of time-dependent mass-gain data at 1173 K, 1273 K, 1373 K, 1473 K and 1573 K. At temperatures above 1540 K, post test examination of the oxidized samples revealed that the Inconel 718 began to lose strength and to deform. At 1540 K, samples which were suspended from their ends during testing began to demonstrate axial curvature as they lost strength and bowed under their own weight. As the temperatures of the tests were increased, rivulets were seen to appear on the surfaces of the test specimens; damage became severe at 1560 K. Although melting was never observed in any of these tests even up to. 1620 K, it was concluded from these data that the Inconel 718 clad should not be expected to protect the underlying tungsten at temperatures above 1540 K.« less

High-temperature oxidation of advanced FeCrNi alloy in steam environments

NASA Astrophysics Data System (ADS)

Elbakhshwan, Mohamed S.; Gill, Simerjeet K.; Rumaiz, Abdul K.; Bai, Jianming; Ghose, Sanjit; Rebak, Raul B.; Ecker, Lynne E.

2017-12-01

Alloys of iron-chromium-nickel are being explored as alternative cladding materials to improve safety margins under severe accident conditions. Our research focuses on non-destructively investigating the oxidation behavior of the FeCrNi alloy "Alloy 33" using synchrotron-based methods. The evolution and structure of oxide layer formed in steam environments were characterized using X-ray diffraction, hard X-ray photoelectron spectroscopy, X-ray fluorescence methods and scanning electron microscopy. Our results demonstrate that a compact and continuous oxide scale was formed consisting of two layers, chromium oxide and spinel phase (FeCr2O4) oxides, wherein the concentration of the FeCr2O4 phase decreased from the surface to the bulk-oxide interface.

Effect of commercial metals (Al, Cu, carbon steel, and Zn) on the oxidation of soy-biodiesel

NASA Astrophysics Data System (ADS)

Díaz-Ballote, L.; Castillo-Atoche, A.; Maldonado, L.; Ruiz-Gómez, M. A.; Hernández, E.

2016-09-01

The effect of aluminum, copper, low carbon steel and zinc on the oxidation of biodiesel derived from soybean oil is studied using residual mass curves from thermogravimetry. Biodiesel is oxidized in the presence and absence of each metal in static conditions and exposed to ambient air. Oxidized biodiesel parameters are confirmed by viscosity measurements, nuclear magnetic resonance and Fourier transform infrared spectroscopy. The results showed that the metals do not negatively influence the oxidative stability of biodiesel and it can even be considered that they slightly inhibit the oxidation process. This behavior was ascribed to a depletion of dissolved oxygen in biodiesel due to oxidation of the metal and the low solubility of oxygen at high temperature.

Tribological Behavior of Mg97Zn1Y2 Alloy at Elevated Temperatures of 50-200 °C

NASA Astrophysics Data System (ADS)

An, J.; Feng, J. H.; Yan, X. H.; Li, R. G.

2017-10-01

The tribological behavior of Mg97Zn1Y2 alloy was investigated using a pin-on-disk wear machine at wear temperatures of 50-200 °C. Morphologies and chemical compositions of worn surfaces were analyzed using scanning electron microscope and energy-dispersive x-ray spectrometer. The microstructural evolution and hardness change in subsurfaces were examined by optical microscopy and hardness tester. The results showed that the wear temperature had significant influence on the coefficient of friction and wear rate. At wear temperatures of 50-200 °C, with increasing applied load, the coefficient of friction went down rapidly then turned to decrease slowly in the mild wear regime, and continuously decreased modestly until the largest applied load in the severe wear regime. Increasing wear temperature from 50 to 200 °C decreased the mild to severe wear transition load linearly from 120 to 60 N. In the mild wear regime, the main wear mechanisms were identified as abrasion + oxidation and delamination + surface oxidation at 50-150 °C, and delamination at 200 °C, while in the severe wear regime, the main wear mechanisms were identified as severe plastic deformation + spallation of oxide layer and surface melting at 50-150 °C, and severe plastic deformation and surface melting at 200 °C. The microstructural transformation from the deformed to the dynamically recrystallized (DRX), and hardness change from the strain hardening to softening were found in the subsurfaces before and after mild to severe transition. The DRX softening mechanism was determined for mild to severe wear transition at 50-200 °C. A wear transition map was constructed for Mg97Zn1Y2 alloy on applied load versus wear temperature.

Temperature-programmed reduction of Pt-Ir/. gamma. -Al/sub 2/O/sub 3/ catalysts

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wagstaff, N.; Prins, R.

1979-10-15

An intriguing feature of the evidence for the existence of Pt-Re clusters in the reduced state of the catalyst, Pt-Re/..gamma..-Al/sub 2/O/sub 3/ was the segregation of Pt and Re oxides observed after oxidation of the bimetallic clusters at temperatures above about 200/sup 0/C. Evidently, the oxide moieties are immiscible on the scale of the small clusters (up to 10 to 15 atoms) in the case of these metals. The present results for Pt-Ir/..gamma..-Al/sub 2/O/sub 3/ represent an example of a supported, highly dispersed system in which the intimacy of the metals remains intact even after fairly severe oxidation treatments. Studymore » of other bimetallic system on alumina by TPR should yield further valuable information on this interesting aspect of metal cluster behavior. 1 figure.« less

Comprehensive kinetic model for the low-temperature oxidation of hydrocarbons

DOE Office of Scientific and Technical Information (OSTI.GOV)

Gaffuri, P.; Faravelli, T.; Ranzi, E.

1997-05-01

The oxidation chemistry in the low- and intermediate-temperature regimes (600--900 K) is important and plays a significant role in the overall combustion process. Autoignition in diesel engines as well as end-gas autoignition and knock phenomena in s.i. engines are initiated at these low temperatures. The low-temperature oxidation chemistry of linear and branched alkanes is discussed with the aim of unifying their complex behavior in various experimental systems using a single detailed kinetic model. New experimental data, obtained in a pressurized flow reactor, as well as in batch- and jet-stirred reactors, are useful for a better definition of the region ofmore » cool flames and negative temperature coefficient (NTC) for pure hydrocarbons from propane up to isooctane. Thermochemical oscillations and the NTC region of the reaction rate of the low-temperature oxidation of n-heptane and isooctane in a jet-stirred flow reactor are reproduced quite well by the model, not only in a qualitative way but in terms of the experimental frequencies and intensities of cool flames. Very good agreement is also observed for fuel conversion and intermediate-species formation. Irrespective of the experimental system, the same critical reaction steps always control these phenomena. The results contribute to the definition of a limited set of fundamental kinetic parameters that should be easily extended to model heavier alkanes.« less

Influence of low concentration V and Co oxide doping on the dissolution behaviors of simplified nuclear waste glasses

DOE Office of Scientific and Technical Information (OSTI.GOV)

Lu, Xiaonan; Neeway, James J.; Ryan, Joseph V.

Transition metal oxides are commonly present in nuclear waste and they can alter the structure, property and especially dissolution behaviors of the glasses used for waste immobilization. In this paper, we investigated vanadium and cobalt oxide induced structural and properties changes, especially dissolution behaviors, of International Simple Glass (ISG), a model nuclear waste glass system. Static chemical durability tests were performed at 90 °C with a pH value of 7 and a surface-area-to-solution-volume of 200 m-1 for 112 days on three glasses: ISG, ISG doped with 0.5 mol% Co2O3, and ISG doped with 2.0 mol% V2O5. ICP-MS was used tomore » analyze the dissolved ion concentrations. It was found that doping with vanadium and cobalt oxide, even at the low doping concentration, significantly reduced the extent of the ISG glass dissolution. Differential Scanning Calorimetry (DSC) analysis showed that vanadium oxide doping reduced the glass transition temperature (Tg) while cobalt oxide did not significantly change the Tg of ISG. X-ray diffraction (XRD), Raman spectrometry and scanning electron microscopy (SEM) were used to analyze the glass samples before and after corrosion to understand the phase and microstructure changes.« less

High-temperature corrosion of iron-aluminum and iron-aluminum-yttrium alloys

NASA Astrophysics Data System (ADS)

Insoo, Kim

The high-temperature corrosion behavior of Fe3Al alloy has been investigated by conducting two studies: (1) corrosion of Fe 3Al and Fe3Al-Y alloys in oxidizing atmosphere and (2) corrosion of Fe3Al in mixed chlorine/oxygen environments. In the first study, oxidation of the two alloys, Fe-14.3 wt% Al and Fe-14.1 wt% Al-0.3 wt% Y, was carried out in the temperature range of 800 to 1100°C to investigate the general oxidation behavior of Fe3Al and the effect of yttrium on the oxidation of Fe3Al in terms of oxidation kinetics, oxide scale adhesion and microstructure. At lower temperatures (<1000°C), the oxidation rate of the two alloys was nearly identical, and the parabolic rate constant obtained as a function of temperature was Kp = 5128 exp[--39500 (cal/mol)/RT] mg2/cm4 h. At higher temperatures, however, yttrium-added Fe3Al alloy exhibited lower oxidation rate and much more improved oxide adhesion. The lower oxidation rate observed in Fe3Al-Y alloy seems to be due to the followings: (1) a decrease in aluminum diffusion through alumina scale and (2) modification of the scale growth mechanism from simultaneous countercurrent diffusion of aluminum and oxygen to predominant inward diffusion of oxygen, which generates less growth stress and thus prevents the formation of fast diffusion paths such as microcracks. The adhesion improvement of alumina scale formed on the Fe3Al-Y was attributed to the modification of alumina growth mechanism by the addition of Y to the Fe3Al alloy. The change of growth mechanism leads to the formation of pegs, decrease of the oxide growth stress, and decrease of voids formation, which enhances the adhesion of alumina scale to the Fe3Al alloy. The second study has focused on the corrosion of Fe3Al in the temperature range of 600--800°C in Cl2-Ar gas mixtures containing traces of oxygen as an impurity. Weight gain was observed during the corrosion of Fe3Al at 600°C in 0.25% Cl2-Ar, which is due to the formation of Fe2O3, while continuous weight loss of the specimen in 5% Cl2-Ar at 800°C was observed because of the formation of volatile metal chlorides, FeCl2, FeCl 3, and AlCl3. Meanwhile, three distinct stages of weight change during the corrosion of Fe3Al at 700°C in 1% Cl 2-Ar were observed: (1) weight gain, (2) linear weight loss, and (3) gradual decrease of weight loss. Initial weight gain is due to the formation of Fe2O3, and the weight loss in the subsequent two stages is due to the formation of volatile metal chlorides, FeCl 2, FeCl3, and AlCl3. Based on the kinetic and microstructural analyses, a reaction mechanism is proposed for each stage.

The Degradation Behavior of SiCf/SiO2 Composites in High-Temperature Environment

NASA Astrophysics Data System (ADS)

Yang, Xiang; Cao, Feng; Qing, Wang; Peng, Zhi-hang; Wang, Yi

2018-04-01

SiCf/SiO2 composites had been fabricated efficiently by Sol-Gel method. The oxidation behavior, thermal shock property and ablation behavior of SiCf/SiO2 composites was investigated. SiCf/SiO2 composites showed higher oxidation resistance in oxidation atmosphere, the flexural strength retention ratio was larger than 90.00%. After 1300 °C thermal shock, the mass retention ratio was 97.00%, and the flexural strength retention ratio was 92.60%, while after 1500 °C thermal shock, the mass retention ratio was 95.37%, and the flexural strength retention ratio was 83.34%. After 15 s ablation, the mass loss rate was 0.049 g/s and recession loss rate was 0.067 mm/s. The SiO2 matrix was melted in priority and becomes loosen and porous. With the ablation going on, the oxides were washed away by the shearing action of the oxyacetylene flame. The evaporation of SiO2 took away large amount of heat, which is also beneficial to the protection for SiCf/SiO2 composites.

Magnetoviscoelastic characteristics of superparamagnetic oxides (Fe, Ni) based ferrofluids

NASA Astrophysics Data System (ADS)

Katiyar, Ajay; Dhar, Purbarun; Nandi, Tandra; Das, Sarit K.

2017-08-01

Ferrofluids have been popular among the academic and scientific communities owing to their intelligent physical characteristics under external stimuli and are in fact among the first nanotechnology products to be employed in real world applications. However, studies on the magnetoviscoelastic behavior of concentrated ferrofluids, especially of superparamagnetic oxides of iron and nickel are rare. The present article comprises the formulation of magneto-colloids utilizing the three various metal oxides nanoparticles viz. Iron (II, III) oxide (Fe3O4), Iron (III) oxide (Fe2O3) and Nickel oxide (NiO) in oil. Iron (II, III) oxide based colloids demonstrate high magnetoviscous characteristics over the other oxides based colloids under external magnetic fields. The maximum magnitude of yield stress and viscosity is found to be 3.0 kPa and 2.9 kPa.s, respectively for iron (II, III) oxide based colloids at 2.6 vol% particle concentration and 1.2 T magnetic field. Experimental investigations reveal that the formulated magneto-nanocolloids are stable, even in high magnetic fields and almost reversible when exposed to rising and drop of magnetic fields of the same magnitude. Observations also reveal that the elastic behavior dominates over the viscous behavior with enhanced relaxation and creep characteristics under the magnetic field. The effect of temperature on viscosity and yield stress of magneto-nanocolloids under magnetic fields has also been discussed. Thus, the present findings have potential applications in various fields such as electromagnetic clutch and brakes of automotive, damping, sealing, optics, nanofinishing etc.

Composition-dependent damping and relaxation dynamics in miscible polymer blends above glass transition temperature by anelastic spectroscopy

NASA Astrophysics Data System (ADS)

Wu, Xuebang; Shang, Shuying; Xu, Qiaoling; Liu, Changsong; Zhu, Zhengang; Zhang, Guangzhao

2008-07-01

Anelastic spectroscopy is used to study the composition dependence of the damping and molecular relaxation dynamics in miscible poly(ethylene oxide) (PEO)/poly(methyl methacrylate) (PMMA) blends above the glass transition temperature. The ultrahigh damping peak of the relaxation type is shown to be associated with the liquid-liquid transition of PMMA. A higher PEO concentration leads to a higher damping performance and a lower transition temperature. The decreasing activation energy with increasing PEO concentration indicates a drastic increase in molecular mobility. Moreover, the relaxation time reveals a transition from the Vogel-Fulcher-Tamman behavior to the Arrhenius behavior due to the intermolecular guest-host interactions.

Interfacial engineering of solution-processed Ni nanochain-SiO x (x< 2) cermets towards thermodynamically stable, anti-oxidation solar selective absorbers

DOE Office of Scientific and Technical Information (OSTI.GOV)

Yu, Xiaobai; Wang, Xiaoxin; Zhang, Qinglin

Here, cermet solar thermal selective absorber coatings are an important component of high-efficiency concentrated solar power (CSP) receivers. The oxidation of the metal nanoparticles in cermet solar absorbers is a great challenge for vacuum-free operation. Recently, we have demonstrated that oxidation is kinetically retarded in solution processed, high-optical-performance Ni nanochain-SiO x cermet system compared to conventional Ni-Al 2O 3 system when annealed in air at 450–600 °C for several hours. However, for long-term, high-temperature applications in CSP systems, thermodynamically stable antioxidation behavior is highly desirable, which requires new mechanisms beyond kinetically reducing the oxidation rate. Towards this goal, in thismore » paper, we demonstrate that pre-operation annealing of Ni nanochain-SiO x cermets at 900 °C in N 2 forms the thermodynamically stable orthorhombic phase of NiSi at the Ni/SiO x interfaces, leading to self-terminated oxidation at 550 °C in air due to this interfacial engineering. In contrast, pre-operation annealing at a lower temperature of 750 °C in N 2 (as conducted in our previous work) cannot achieve interfacial NiSi formation directly, and further annealing in air at 450–600 °C for >4 h only leads to the formation of the less stable (metastable) hexagonal phase of NiSi. Therefore, the high-temperature pre-operation annealing is critical to form the desirable orthorhombic phase of NiSi at Ni/SiO x interfaces towards thermodynamically stable antioxidation behavior. Remarkably, with this improved interfacial engineering, the oxidation of 80-nm-diameter Ni nanochain-SiO x saturates after annealing at 550 °C in air for 12 h. Additional annealing at 550 °C in air for as long as 20 h (i.e., 32 h air annealing at >550 °C in total) has almost no further impact on the structural or optical properties of the coatings, the latter being very sensitive to any interfacial changes due to the localized surface plasmon resonances of the metal nanostructures. This phenomenon holds true for Ni nanoparticle diameter down to 40 nm in Ni-SiO x system, where the optical response remains stable for 53 h at 550 °C in air. The oxidation vs. time curve also shows saturation behavior deviating from the kinetic Deal-Grove oxidation model. These results strongly suggest a promising approach to thermodynamically stable, anti-oxidation Ni/SiO x cermet absorbers via interfacial engineering.« less

Interfacial engineering of solution-processed Ni nanochain-SiO x (x< 2) cermets towards thermodynamically stable, anti-oxidation solar selective absorbers

DOE PAGES

Yu, Xiaobai; Wang, Xiaoxin; Zhang, Qinglin; ...

2016-04-01

Here, cermet solar thermal selective absorber coatings are an important component of high-efficiency concentrated solar power (CSP) receivers. The oxidation of the metal nanoparticles in cermet solar absorbers is a great challenge for vacuum-free operation. Recently, we have demonstrated that oxidation is kinetically retarded in solution processed, high-optical-performance Ni nanochain-SiO x cermet system compared to conventional Ni-Al 2O 3 system when annealed in air at 450–600 °C for several hours. However, for long-term, high-temperature applications in CSP systems, thermodynamically stable antioxidation behavior is highly desirable, which requires new mechanisms beyond kinetically reducing the oxidation rate. Towards this goal, in thismore » paper, we demonstrate that pre-operation annealing of Ni nanochain-SiO x cermets at 900 °C in N 2 forms the thermodynamically stable orthorhombic phase of NiSi at the Ni/SiO x interfaces, leading to self-terminated oxidation at 550 °C in air due to this interfacial engineering. In contrast, pre-operation annealing at a lower temperature of 750 °C in N 2 (as conducted in our previous work) cannot achieve interfacial NiSi formation directly, and further annealing in air at 450–600 °C for >4 h only leads to the formation of the less stable (metastable) hexagonal phase of NiSi. Therefore, the high-temperature pre-operation annealing is critical to form the desirable orthorhombic phase of NiSi at Ni/SiO x interfaces towards thermodynamically stable antioxidation behavior. Remarkably, with this improved interfacial engineering, the oxidation of 80-nm-diameter Ni nanochain-SiO x saturates after annealing at 550 °C in air for 12 h. Additional annealing at 550 °C in air for as long as 20 h (i.e., 32 h air annealing at >550 °C in total) has almost no further impact on the structural or optical properties of the coatings, the latter being very sensitive to any interfacial changes due to the localized surface plasmon resonances of the metal nanostructures. This phenomenon holds true for Ni nanoparticle diameter down to 40 nm in Ni-SiO x system, where the optical response remains stable for 53 h at 550 °C in air. The oxidation vs. time curve also shows saturation behavior deviating from the kinetic Deal-Grove oxidation model. These results strongly suggest a promising approach to thermodynamically stable, anti-oxidation Ni/SiO x cermet absorbers via interfacial engineering.« less

Synthesis of highly efficient α-Fe{sub 2}O{sub 3} catalysts for CO oxidation derived from MIL-100(Fe)

DOE Office of Scientific and Technical Information (OSTI.GOV)

Cui, Lifeng; Zhao, Di; Yang, Yang

Mesoporous hollow α-Fe{sub 2}O{sub 3} bricks were synthesized via a hydrothermal method to create a precursor MIL-100(Fe) and a subsequent calcination process was applied to prepare the Fe{sub 2}O{sub 3} phase. Scanning electron microscopy (SEM) and transmission electron microscopy (TEM) results showed the morphology of hollow α-Fe{sub 2}O{sub 3} bricks which inherited from the MIL-100(Fe) template. The catalytic activities of hollow α-Fe{sub 2}O{sub 3} bricks for CO oxidation are studied in this work. Due to better low temperature reduction behavior, mesoporous hollow α-Fe{sub 2}O{sub 3} bricks obtained at calcination temperature of 430 °C displayed high catalytic activity and excellent stabilitymore » with a complete CO conversion temperature (T{sub 100}) of 255 °C. - Graphical abstract: Synthesis of highly efficient α-Fe{sub 2}O{sub 3} catalysts for CO oxidation derived from MIL-100(Fe). - Highlights: • α-Fe{sub 2}O{sub 3} is prepared by the thermolysis of a MIL-100(Fe) template. • The morphology of hollow α-Fe{sub 2}O{sub 3} bricks is inherited from MIL-100(Fe) template. • α-Fe{sub 2}O{sub 3} obtained at calcined temperature of 430 °C displays high activity • Enhanced activity is attributed to crystal plane and reduction behavior.« less

Oxidation behavior of multiwall carbon nanotubes with different diameters and morphology

NASA Astrophysics Data System (ADS)

Mazov, Ilya; Kuznetsov, Vladimir L.; Simonova, Irina A.; Stadnichenko, Andrey I.; Ishchenko, Arkady V.; Romanenko, Anatoly I.; Tkachev, Evgeniy N.; Anikeeva, Olga B.

2012-06-01

Multiwall carbon nanotubes (MWNT) with three medium diameters (20-22, 9-13, and 6-8 nm) and different morphology were chemically oxidized using concentrated nitric acid, mixture of nitric and sulfuric acids ("mélange" solution) and mixture of sulfuric acid and hydrogen peroxide ("piranha" solution). Influence of MWNT type and structure as well as type of oxidizer on the surface composition and structure of nanotubes after oxidation was investigated. Acid-base titration, X-ray photoelectron spectroscopy and thermal gravimetric analysis were used for quantitative and qualitative investigation of surface group composition of initial and oxidized nanotubes. Amount of oxygen-containing groups on the surface of oxidized MWNT depends on the type of initial MWNT. It was found that ratio of different oxygen containing groups is less dependent on the type of oxidizer. Electrophysical properties of initial and oxidized nanotubes were investigated in temperature range 4-293 K and main types of electrical conductivity were determined. It was shown that oxidation results in decrease in electrical conductivity of all samples with simultaneous change in the conductivity mechanism. Dispersive behavior of initial and oxidized nanotubes in different commonly used solvents was investigated. It was shown that oxidation leads to the improvement of sedimentation stability of MWNT in polar solvents.

The oxidation of TaBe sub 12 and NbBe sub 12 coatings on niobium

DOE Office of Scientific and Technical Information (OSTI.GOV)

Courtright, E.L.

1990-01-01

The oxidation behavior of tantalum and niobium beryllide coatings on niobium were evaluated. Intermetallic bond layers consisting of Ir{sub 3}Ta and Ir{sub 3}Nb were used to butter the large thermal expansion mismatch between the beryllide coatings and underlying niobium substrate. All coatings were applied by Triode Sputtering except for a final environmental protection layer of stabilized zirconia deposited by RF Diode using a ceramic target. Severe delamination and spalling occurred during cyclic oxidation exposure, even at temperatures as low as 925{degrees}C, indicating that the bond layer did not prevent the differential expansion stresses from reaching the delamination failure threshold, particularlymore » at the edges and corners. Hot pressed samples of the two beryllide compounds were also exposed to a similar cyclic oxidation history, but, in contrast to the coatings, exhibited excellent oxidation resistance to temperatures as high as 1370{degrees}C. 9 refs., 8 figs., 1 tab.« less

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kohnert, Aaron A.; Dasgupta, Dwaipayan; Wirth, Brian

In order to improve the accident tolerance of light water reactor (LWR) fuel, alternative cladding materials have been proposed to replace zirconium (Zr)-based alloys. Of these materials, there is a particular focus on iron-chromium-aluminum (FeCrAl) alloys due to much slower oxidation kinetics in high-temperature steam than Zr-alloys. This should decrease the energy release due to oxidation and allow the cladding to remain integral longer in the presence of high temperature steam, making accident mitigation more likely. As a continuation of the development for these alloys, the material response must be demonstrated to provide suitable radiation stability, in order to ensuremore » that there will not be significant dimensional changes (e.g., swelling), as well as quantifying the radiation hardening and radiation creep behavior. In this report, we describe the use of cluster dynamics modeling to evaluate the defect physics and damage accumulation behavior of FeCrAl alloys subjected to neutron irradiation, with a particular focus on irradiation-induced swelling and defect fluxes to dislocations that are required to model irradiation creep behavior.« less

Catalytic properties of new anode materials for solid oxide fuel cells operated under methane at intermediary temperature

NASA Astrophysics Data System (ADS)

Sauvet, A.-L.; Fouletier, J.

The recent trend in solid oxide fuel cell concerns the use of natural gas as fuel. Steam reforming of methane is a well-established process for producing hydrogen directly at the anode side. In order to develop new anode materials, the catalytic activities of several oxides for the steam reforming of methane were characterized by gas chromatography. We studied the catalytic activity as a function of steam/carbon ratios r. The methane and the steam content were varied between 5 and 30% and between 1.5 and 3.5%, respectively, corresponding to r-values between 0.07 and 0.7. Catalyst (ruthenium and vanadium)-doped lanthanum chromites substituted with strontium, gadolinium-doped ceria (Ce 0.9Gd 0.1O 2) referred as to CeGdO 2, praseodymium oxide, molybdenum oxide and copper oxide were tested. The working temperature was fixed at 850°C, except for 5% ruthenium-doped La 1- xSr xCrO 3 where the temperature was varied between 700 and 850°C. Two types of behavior were observed as a function of the activity of the catalyst. The higher steam reforming efficiency was observed with 5% of ruthenium above 750°C.

Combined high vacuum/high frequency fatigue tester

NASA Technical Reports Server (NTRS)

Honeycutt, C. R.; Martin, T. F.

1971-01-01

Apparatus permits application of significantly greater number of cycles or equivalent number of cycles in shorter time than conventional fatigue test machines. Environment eliminates problems associated with high temperature oxidation and with sensitivity of refractory alloy behavior to atmospheric contamination.

A Mechanistic-Based Healing Model for Self-Healing Glass Seals Used in Solid Oxide Fuel Cells

DOE Office of Scientific and Technical Information (OSTI.GOV)

Xu, Wei; Sun, Xin; Stephens, Elizabeth V.

The usage of self-healing glass as hermetic seals is a recent advancement in sealing technology development for the planar solid oxide fuel cells (SOFCs). Because of its capability of restoring the mechanical properties at elevated temperatures, the self-healing glass seal is expected to provide high reliability in maintaining the long-term structural integrity and functionality of SOFCs. In order to accommodate the design and to evaluate the effectiveness of such engineering seals under various thermo-mechanical operating conditions, computational modeling framework needs to be developed to accurately capture and predict the healing behavior of the glass material. In the present work, amore » mechanistic-based two-stage model was developed to study the stress and temperature-dependent crack healing of the self-healing glass materials. The model was first calibrated by experimental measurements combined with the kinetic Monte Carlo (kMC) simulation results and then implemented into the finite element analysis (FEA). The effects of various factors, i.e. stress, temperature, crack morphology, on the healing behavior of the glass were investigated and discussed.« less

pn junctions based on a single transparent perovskite semiconductor BaSnO3

NASA Astrophysics Data System (ADS)

Kim, Hoon Min; Kim, Useong; Park, Chulkwon; Kwon, Hyukwoo; Lee, Woongjae; Kim, Tai Hoon; Kim, Kee Hoon; Char, Kookrin; Mdpl, Department Of Physics; Astronomy Team; Censcmr, Department Of Physics; Astronomy Team

2014-03-01

Successful p doping of transparent oxide semiconductor will further increase its potential, especially in the area of optoelectronic applications. We will report our efforts to dope the BaSnO3 (BSO) with K by pulsed laser deposition. Although the K doped BSO exhibits rather high resistivity at room temperature, its conductivity increases dramatically at higher temperatures. Furthermore, the conductivity decreases when a small amount of oxygen was removed from the film, consistent with the behavior of p type doped oxides. We have fabricated pn junctions by using K doped BSO as a p type and La doped BSO as an n type material. I_V characteristics of these devices show the typical rectifying behavior of pn junctions. We will present the analysis of the junction properties from the temperature dependent measurement of their electrical properties, which shows that the I_V characteristics are consistent with the material parameters such as the carrier concentration, the mobility, and the bandgap. Our demonstration of pn junctions based on a single transparent perovskite semiconductor further enhances the potential of BSO system with high mobility and stability.

New Creep-Resistant Cast Alloys with Improved Oxidation Resistance in Water Vapor at 650–800°C

DOE PAGES

Dryepondt, Sebastien; Pint, Bruce A.; Maziasz, Philip J.

2015-08-13

Cast stainless steel CF8C-Plus (19wt%Cr/12%Ni) has excellent creep properties, but limited oxidation resistance above 700 C in environments containing H 2O. One strategy to improve the alloy oxidation performance is to increase the Cr and Ni concentration. Two new alloys, with, respectively, 21wt%Cr 15wt%Ni and 22wt%Cr 17.5wt%Ni were therefore developed and their long-term oxidation behaviors in humid air were compared with the oxidation behavior of five other cast alloys. Also, at 650 C and 700 C, all the alloys formed internal Cr-rich nodules, and outer nodules or layers rich in Fe and Ni, but they grew a protective Cr-rich innermore » layer over time. At 750 C, the lower alloyed steels such as CF8C-Plus showed large metal losses, but the two new alloys still exhibited a protective oxidation behavior. The 21Cr 15Ni alloy was severely oxidized in locations at 800 C, but that was not the case for the 22Cr 17.5Ni alloy. Thus, the two new modified alloys represent a potential operating temperature gain of, respectively, 50 C and 100 C in aggressive environments compared with the CF8C-Plus alloy.« less

Kinetic analysis of superparamagnetic iron oxide nanoparticles in the liver of body-temperature-controlled mice using dynamic susceptibility contrast magnetic resonance imaging and an empirical mathematical model.

PubMed

Murase, Kenya; Assanai, Purapan; Takata, Hiroshige; Matsumoto, Nozomi; Saito, Shigeyoshi; Nishiura, Motoko

2015-06-01

The purpose of this study was to develop a method for analyzing the kinetic behavior of superparamagnetic iron oxide nanoparticles (SPIONs) in the murine liver under control of body temperature using dynamic susceptibility contrast magnetic resonance imaging (DSC-MRI) and an empirical mathematical model (EMM). First, we investigated the influence of body temperature on the kinetic behavior of SPIONs in the liver by controlling body temperature using our temperature-control system. Second, we investigated the kinetic behavior of SPIONs in the liver when mice were injected with various doses of GdCl3, while keeping the body temperature at 36°C. Finally, we investigated it when mice were injected with various doses of zymosan, while keeping the body temperature at 36°C. We also investigated the effect of these substances on the number of Kupffer cells by immunohistochemical analysis using the specific surface antigen of Kupffer cells (CD68). To quantify the kinetic behavior of SPIONs in the liver, we calculated the upper limit of the relative enhancement (A), the rates of early contrast uptake (α) and washout or late contrast uptake (β), the parameter related to the slope of early uptake (q), the area under the curve (AUC), the maximum change of transverse relaxation rate (ΔR2) (ΔR2(max)), the time to ΔR2(max) (Tmax), and ΔR2 at the last time point (ΔR2(last)) from the time courses of ΔR2 using the EMM. The β and Tmax values significantly decreased and increased, respectively, with decreasing body temperature, suggesting that the phagocytic activity of Kupffer cells is significantly affected by body temperature. The AUC, ΔR2(max), and ΔR2(last) values decreased significantly with increasing dose of GdCl3, which was consistent with the change in the number of CD68-positive cells. They increased with increasing dose of zymosan, which was also consistent with the change in the number of CD68-positive cells. These results suggest that AUC, ΔR2(max), and ΔR2(last) reflect the number of Kupffer cells. In conclusion, we presented a method for analyzing the kinetic behavior of SPIONs in the liver using DSC-MRI and EMM, and investigated the influence of body temperature, GdCl3, and zymosan using body-temperature-controlled mice. The present study suggests that control of body temperature is essential for investigating the kinetic behavior of SPIONs in the liver and that our method will be applicable and useful for quantifying the responses of Kupffer cells to various drugs under control of body temperature. Copyright © 2015 Elsevier Inc. All rights reserved.

Tailoring oxidation of aluminum nanoparticles reinforced with carbon nanotubes

DOE Office of Scientific and Technical Information (OSTI.GOV)

Sharma, Manjula; Sharma, Vimal, E-mail: manjula.physics@gmail.com

2016-05-23

In this report, the oxidation temperature and reaction enthalpy of Aluminum (Al) nanoparticles has been controlled by reinforcing with carbon nanotubes. The physical mixing method with ultrasonication was employed to synthesize CNT/Al nanocomposite powders. The micro-morphology of nanoconmposite powders has been analysed by scanning electron microscopy, energy dispersive spectroscopy, Raman spectroscopy and X-ray diffraction techniques. The oxidation behavior of nanocomposite powders analyzed by thermogravimetry/differential scanning calorimertry showed improvement in the exothermic enthalpy. Largest exothermic enthalpy of-1251J/g was observed for CNT (4 wt%)/Al nanocomposite.

Synthesis and magnetic properties of single-crystalline Na2-xMn8O16 nanorods

PubMed Central

2011-01-01

The synthesis of single-crystalline hollandite-type manganese oxides Na2-xMn8O16 nanorods by a simple molten salt method is reported for the first time. The nanorods were characterized by powder X-ray diffraction, scanning electron microscopy, transmission electron microscopy, and a superconducting quantum interference device magnetometer. The magnetic measurements indicated that the nanorods showed spin glass behavior and exchange bias effect at low temperatures. The low-temperature magnetic behaviors can be explained by the uncompensated spins on the surface of the nanorods. PMID:21711626

High Temperature Mechanical Behavior of Polycrystalline Alumina from Mixed Nanometer and Micrometer Powders

NASA Technical Reports Server (NTRS)

Goldsby, Jon C.

2001-01-01

Sintered aluminum oxide materials were formed using commercial methods from mechanically mixed powders of nano-and micrometer alumina. The powders were consolidated at 1500 and 1600 C with 3.2 and 7.2 ksi applied stress in argon. The conventional micrometer sized powders failed to consolidate. While 100 percent nanometer-sized alumina and its mixture with the micrometer powders achieved less than 99 percent density. Preliminary high temperature creep behavior indicates no super-plastic strains. However high strains (less than 0.65 percent) were generated in the nanometer powder, due to cracks and linked voids initiated by cavitation.

Behavior of HfB2-SiC Materials in Simulated Re-Entry Environments

NASA Technical Reports Server (NTRS)

Ellerby, Don; Beckman, Sarah; Irby, Edward; Johnson, Sylvia M.; Gunsman, Michael; Gasch, Matthew; Ridge, Jerry; Martinez, Ed; Squire, Tom; Olejniczak, Joe

2003-01-01

The objectives of this research are to: 1) Investigate the oxidation/ablation behavior of HfB2/SiC materials in simulated re-entry environments; 2) Use the arc jet test results to define appropriate use environments for these materials for use in vehicle design. The parameters to be investigated include: surface temperature, stagnation pressure, duration, number of cycles, and thermal stresses.

Impact of Microstructure on MoS 2 Oxidation and Friction

DOE PAGES

Curry, John F.; Wilson, Mark A.; Luftman, Henry S.; ...

2017-07-31

In this work, we demonstrate the role of microstructure in the friction and oxidation behavior of the lamellar solid lubricant molybdenum disulfide (MoS 2). We report on systematic investigations of oxidation and friction for two MoS 2 films with distinctively different microstructures—amorphous and planar/highly-ordered—before and after exposure to atomic oxygen (AO) and high-temperature (250 °C) molecular oxygen. A combination of experimental tribology, molecular dynamics simulations, X-ray photoelectron spectroscopy (XPS), and high-sensitivity low-energy ion scattering (HS-LEIS) was used to reveal new insights about the links between structure and properties of these widely utilized low-friction materials. Initially, ordered MoS 2 films showedmore » a surprising resistance to both atomic and molecular oxygens (even at elevated temperature), retaining characteristic low friction after exposure to extreme oxidative environments. Finally, XPS shows comparable oxidation of both coatings via AO; however, monolayer resolved compositional depth profiles from HS-LEIS reveal that the microstructure of the ordered coatings limits oxidation to the first atomic layer.« less

Oxidation- and Creep-Enhanced Fatigue of Haynes 188 Alloy-Oxide Scale System Under Simulated Pulse Detonation Engine Conditions

NASA Technical Reports Server (NTRS)

Zhu, Dongming; Fox, Dennis S.; Miller, Robert A.

2002-01-01

The development of the pulse detonation engine (PDE) requires robust design of the engine components that are capable of enduring harsh detonation environments. In this study, a high cycle thermal fatigue test rig was developed for evaluating candidate PDE combustor materials using a CO2 laser. The high cycle thermal fatigue behavior of Haynes 188 alloy was investigated under an enhanced pulsed laser test condition of 30 Hz cycle frequency (33 ms pulse period, and 10 ms pulse width including 0.2 ms pulse spike). The temperature swings generated by the laser pulses near the specimen surface were characterized by using one-dimensional finite difference modeling combined with experimental measurements. The temperature swings resulted in significant thermal cyclic stresses in the oxide scale/alloy system, and induced extensive surface cracking. Striations of various sizes were observed at the cracked surfaces and oxide/alloy interfaces under the cyclic stresses. The test results indicated that oxidation and creep-enhanced fatigue at the oxide scale/alloy interface was an important mechanism for the surface crack initiation and propagation under the simulated PDE condition.

Impact of Microstructure on MoS 2 Oxidation and Friction

DOE Office of Scientific and Technical Information (OSTI.GOV)

Curry, John F.; Wilson, Mark A.; Luftman, Henry S.

In this work, we demonstrate the role of microstructure in the friction and oxidation behavior of the lamellar solid lubricant molybdenum disulfide (MoS 2). We report on systematic investigations of oxidation and friction for two MoS 2 films with distinctively different microstructures—amorphous and planar/highly-ordered—before and after exposure to atomic oxygen (AO) and high-temperature (250 °C) molecular oxygen. A combination of experimental tribology, molecular dynamics simulations, X-ray photoelectron spectroscopy (XPS), and high-sensitivity low-energy ion scattering (HS-LEIS) was used to reveal new insights about the links between structure and properties of these widely utilized low-friction materials. Initially, ordered MoS 2 films showedmore » a surprising resistance to both atomic and molecular oxygens (even at elevated temperature), retaining characteristic low friction after exposure to extreme oxidative environments. Finally, XPS shows comparable oxidation of both coatings via AO; however, monolayer resolved compositional depth profiles from HS-LEIS reveal that the microstructure of the ordered coatings limits oxidation to the first atomic layer.« less

Effects of lead on oxidation behavior of Alloy 690TT within a high temperature aqueous environment

NASA Astrophysics Data System (ADS)

Hou, Qiang; Liu, Zhiyong; Li, Chengtao; Li, Xiaogang

2017-12-01

The chemical compositions, phases and structures of two oxide films on Alloy 690TT following exposure for 4400 h in pure water with and without lead at 320 °C were studied by surface analysis techniques. The analysis of a lead-doped oxide film prepared by a focused ion beam (FIB) demonstrated that both Cr-rich and Ni-rich oxides were alternatively distributed within the outer layer, whereas the inner layer was porous and poorly protected, causing severe corrosion of the alloy and a thicker film was formed. A duplex film model was proposed for the effects discussion of lead on the oxidation mechanism.

Relative sliding durability of two candidate high temperature oxide fiber seal materials

NASA Technical Reports Server (NTRS)

Dellacorte, Christopher; Steinetz, Bruce M.

1991-01-01

A test program to determine the relative sliding durability of two candidate ceramic fibers for high temperature sliding seal applications is described. Pin on disk tests were used to evaluate potential seal materials. Friction during the tests and fiber wear, indicated by the extent of fibers broken in a test bundle or yarn, was measured at the end of a test. In general, friction and wear increase with test temperature. This may be due to a reduction in fiber strength, a change in the surface chemistry at the fiber/counterface interface due to oxidation, adsorption and/or desorption of surface species and, to a lesser extent, an increase in counterface surface roughness due to oxidation at elevated temperatures. The relative fiber durability correlates with tensile strength indicating that tensile data, which is more readily available than sliding durability data, may be useful in predicting fiber wear behavior under various conditions. A simple model developed using dimensional analysis shows that the fiber durability is related to a dimensionless parameter which represents the ratio of the fiber strength to the fiber stresses imposed by sliding.

Switching adhesion forces by crossing the metal–insulator transition in Magnéli-type vanadium oxide crystals

PubMed Central

Klemm, Matthias; Horn, Siegfried; Woydt, Mathias

2011-01-01

Summary Magnéli-type vanadium oxides form the homologous series VnO2 n -1 and exhibit a temperature-induced, reversible metal–insulator first order phase transition (MIT). We studied the change of the adhesion force across the transition temperature between the cleavage planes of various vanadium oxide Magnéli phases (n = 3 … 7) and spherical titanium atomic force microscope (AFM) tips by systematic force–distance measurements with a variable-temperature AFM under ultrahigh vacuum conditions (UHV). The results show, for all investigated samples, that crossing the transition temperatures leads to a distinct change of the adhesion force. Low adhesion corresponds consistently to the metallic state. Accordingly, the ability to modify the electronic structure of the vanadium Magnéli phases while maintaining composition, stoichiometry and crystallographic integrity, allows for relating frictional and electronic material properties at the nano scale. This behavior makes the vanadium Magnéli phases interesting candidates for technology, e.g., as intelligent devices or coatings where switching of adhesion or friction is desired. PMID:21977416

Using Temperature-Dependent Phenomena at Oxide Surfaces for Species Recognition in Chemical Sensing.

NASA Astrophysics Data System (ADS)

Semancik, Steve; Meier, Douglas; Evju, Jon; Benkstein, Kurt; Boger, Zvi; Montgomery, Chip

2006-03-01

Nanostructured films of SnO2 and TiO2 have been deposited on elements in MEMS arrays to fabricate solid state conductometric gas microsensors. The multilevel platforms within an array, called microhotplates, are individually addressable for localized temperature control and measurement of sensing film electrical conductance. Temperature variations of the microhotplates are employed in thermally-activated CVD oxide film growth, and for rapid temperature-programmed operation of the microsensors. Analytical information on environmental gas phase composition is produced temporally as purposeful thermal fluctuations provide energetic and kinetic control of surface reaction and adsorption/desorption phenomena. Resulting modulations of oxide adsorbate populations cause changing charge transfer behavior and measurable conductance responses. Rich data streams from different sensing films in the arrays have been analyzed by Artificial Neural Networks (ANN) to successfully recognize low concentration species in mixed gases. We illustrate capabilities of the approach and technology in the homeland security area, where dangerous chemicals (TICs, CWSs and CWAs) have been detected at 10-100 ppb levels in interference-spiked air backgrounds.

Wide gap active brazing of ceramic-to-metal-joints for high temperature applications

NASA Astrophysics Data System (ADS)

Bobzin, K.; Zhao, L.; Kopp, N.; Samadian Anavar, S.

2014-03-01

Applications like solid oxide fuel cells and sensors increasingly demand the possibility to braze ceramics to metals with a good resistance to high temperatures and oxidative atmospheres. Commonly used silver based active filler metals cannot fulfill these requirements, if application temperatures higher than 600°C occur. Au and Pd based active fillers are too expensive for many fields of use. As one possible solution nickel based active fillers were developed. Due to the high brazing temperatures and the low ductility of nickel based filler metals, the modification of standard nickel based filler metals were necessary to meet the requirements of above mentioned applications. To reduce thermally induced stresses wide brazing gaps and the addition of Al2O3 and WC particles to the filler metal were applied. In this study, the microstructure of the brazed joints and the thermo-chemical reactions between filler metal, active elements and WC particles were analyzed to understand the mechanism of the so called wide gap active brazing process. With regard to the behavior in typical application oxidation and thermal cycle tests were conducted as well as tensile tests.

Temperature-time dependent transmittance, sheet resistance and bonding energy of reduced graphene oxide on soda lime glass

NASA Astrophysics Data System (ADS)

Kumar, Raj; Kumar, R. Manoj; Bera, Parthasarathi; Ariharan, S.; Lahiri, Debrupa; Lahiri, Indranil

2017-12-01

Reduced graphene oxide coated soda lime glass can act as an alternative transparent/conducting electrode for many opto-electronic applications. However, bonding between the deposited reduced graphene oxide film and the glass substrate is important for achieving better stability of the coating and an extended device lifetime. In the present study, delamination energy of reduced graphene oxide on soda lime glass was quantified by using nanoscratch technique. Graphene oxide was deposited on soda lime glass by dip coating technique and was thermally reduced at different temperatures (100 °C, 200 °C, 300 °C, 400 °C and 500 °C) and treatment time (2 h, 3 h, 4 h, 5 h and 10 h) in Ar (95%) with H2 (5%) atmosphere. An inverse behavior of delamination energy with temperature and treatment time was observed, which could be correlated with the removal of oxygen functional groups. Sheet resistance of the film demonstrated a steady decay with increasing temperature and treatment time. Functional groups attached to the graphene planes have more influence on conductivity than groups attached to the edges. Removal of functional groups could also be related to optical transmittance of the samples. Knowledge generated in this study with respect to delamination energy, sheet resistance and optical transmittance could be extensively used for various opto-electronic applications.

Elevated Temperature Solid Particle Erosion Performance of Plasma-Sprayed Co-based Composite Coatings with Additions of Al2O3 and CeO2

NASA Astrophysics Data System (ADS)

Nithin, H. S.; Desai, Vijay; Ramesh, M. R.

2017-11-01

In this paper, investigation into solid particle erosion behavior of atmospheric plasma-sprayed composite coating of CoCrAlY reinforced with Al2O3 and CeO2 oxides on Superni 76 at elevated temperature of 600 °C is presented. Alumina particles are used as erodent at two impact angles of 30° and 90°. The microstructure, porosity, hardness, toughness and adhesion properties of the as-sprayed coatings are studied. The effects of temperature and phase transformation in the coatings during erosion process are analyzed using XRD and EDS techniques. Optical profilometer is used for accurate elucidation of erosion volume loss. CoCrAlY/CeO2 coating showed better erosion resistance with a volume loss of about 50% of what was observed in case of CoCrAlY/Al2O3/YSZ coating. Lower erosion loss is observed at 90° as compared to 30° impact angle. The erosion mechanism evaluated using SEM micrograph revealed that the coatings experienced ductile fracture exhibiting severe deformation with unusual oxide cracks. Reinforced metal oxides provide shielding effect for erodent impact, enabling better erosion resistance. The oxidation of the coating due to high-temperature exposure reforms erosion process into oxidation-modified erosion process.

Surface chemistry and corrosion behavior of Inconel 625 and 718 in subcritical, supercritical, and ultrasupercritical water

NASA Astrophysics Data System (ADS)

Rodriguez, David; Merwin, Augustus; Karmiol, Zachary; Chidambaram, Dev

2017-05-01

Corrosion behavior of Inconel 625 and 718 in subcritical, supercritical and ultrasupercritical water was studied as a function of temperature and time. The change in the chemistry of the as-received surface film on Inconel 625 and 718 after exposure to subcritical water at 325 °C and supercritical water at 425 °C and 527.5 °C for 2 h was studied. After exposure to 325 °C subcritical water, the CrO42- based film formed; however minor quantities of NiFexCr2-xO4 spinel compounds were observed. The oxide film formed on both alloys when exposed to supercritical water at 425 °C consisted of NiFexCr2-xO4 spinel. The surface films on both alloys were identified as NiFe2O4 when exposed to supercritical water at 527.5 °C. To characterize the fully developed oxide layer, studies were conducted at test solution temperatures of 527.5 and 600 °C. Samples were exposed to these temperatures for 24, 96, and 200 h. Surface chemistry was analyzed using X-ray diffraction, as well as Raman and X-ray photoelectron spectroscopies. Inconel 718 exhibited greater mass gain than Inconel 625 for all temperatures and exposure times. The differences in corrosion behavior of the two alloys are attributed to the lower content of chromium and increased iron content of Inconel 718 as compared to Inconel 625.

Chemical kinetic modeling of propene oxidation at low and intermediate temperatures

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wilk, R.D.; Cernansky, N.P.; Pitz, W.J.

1986-01-13

A detailed chemical kinetic mechanism for propene oxidation is developed and used to model reactions in a static reactor at temperatures of 590 to 740/sup 0/K, equivalence ratios of 0.8 to 2.0, and a pressure of 600 torr. Modeling of hydrocarbon oxidation in this temperature range is important for the validation of detailed models to be used for performing calculations related to automotive engine knock. The model predicted induction periods and species concentrations for all the species measured experimentally in a static reactor by Wilk, Cernansky, and Cohen. The detailed model predicted a temperature region of approximately constant induction periodmore » which corresponded very closely to the region of negative temperature coefficient behavior found in the experiment. Overall, the calculated concentrations of acetaldehyde, ethene, and methane were somewhat low compared to the experimental measurements, and the calculated concentrations of formaldehyde and methanol were high. The characteristic s-shape of the fuel concentration history was well predicted. The importance of OH+C/sub 3/H/sub 6/ and related rections in determining product distributions and the importance of consumption reactions for allyl radicals was demonstrated by the modeling calculations. 18 refs., 4 figs., 1 tab.« less

High-temperature oxidation of advanced FeCrNi alloy in steam environments

DOE PAGES

Elbakhshwan, Mohamed S.; Gill, Simerjeet K.; Rumaiz, Abdul K.; ...

2017-07-04

Alloys of iron-chromium-nickel are being explored as alternative cladding materials to improve safety margins under severe accident conditions. Here, our research focuses on non-destructively investigating the oxidation behavior of the FeCrNi alloy “Alloy 33” using synchrotron-based methods. The evolution and structure of oxide layer formed in steam environments were characterized using X-ray diffraction, hard X-ray photoelectron spectroscopy, X-ray fluorescence methods and scanning electron microscopy. In conclusion, our results demonstrate that a compact and continuous oxide scale was formed consisting of two layers, chromium oxide and spinel phase (FeCr 2O 4) oxides, wherein the concentration of the FeCr 2O 4 phasemore » decreased from the surface to the bulk-oxide interface.« less

Graphene Oxide-Promoted Reshaping and Coarsening of Gold Nanorods and Nanoparticles

PubMed Central

Pan, Hanqing; Low, Serena; Weerasuriya, Nisala; Shon, Young-Seok

2015-01-01

This paper describes thermally induced reshaping and coarsening behaviors of gold nanorods and nanoparticles immobilized on the surface of graphene oxide. Cetyltrimethylammonium bromide-stabilized gold nanorods with an aspect ratio of ~3.5 (54:15 nm) and glutathione-capped gold nanoparticles with an average core size of ~3 nm were synthesized and self-assembled onto the surface of graphene oxide. The hybrid materials were then heated at different temperatures ranging from 50 to 300 °C. The effects of heat treatments were monitored using UV–vis spectroscopy and transmission electron microscopy (TEM). These results were directly compared with those of heat-treated free-standing gold nanorods and nanoparticles without graphene oxide to understand the heat-induced morphological changes of the nanohybrids. The obtained results showed that the gold nanorods would undergo a complete reshaping to spherical particles at the temperature of 50 °C when they are assembled on graphene oxide. In comparison, the complete reshaping of free-standing gold nanorods to spherical particles would ultimately require a heating of the samples at 200 °C. In addition, the spherical gold nanoparticles immobilized on graphene oxide would undergo a rapid coarsening at the temperature of 100–150 °C, which was lower than the temperature (150–200 °C) required for visible coarsening of free-standing gold nanoparticles. The results indicated that graphene oxide facilitates the reshaping and coarsening of gold nanorods and nanoparticles, respectively, during the heat treatments. The stripping and spillover of stabilizing ligands promoted by graphene oxide are proposed to be the main mechanism for the enhancements in the heat-induced transformations of nanohybrids. PMID:25611371

Effects of Temperature and Environment on Creep Behavior of an Oxide-Oxide Ceramic Matrix Composite

DTIC Science & Technology

2007-03-01

Zelina, Dr. Ruth Sikorski, and Dr. Ron Kerans, whose sponsorship made my research possible; Dr. Robert Canfield and Dr. Som Soni, for their membership...on my thesis committee and discerning comments; Lt Joseph Broeckert, Lt Christina Falcone, Capt Christine Ladrido, and LT Robert Salvia, whose...Society for Testing and Materials (1997). 54. Raymer , D.P. Aircraft Design: A Conceptual Approach, 3rd Edition. Reston, VA: American Institute of

Effect of some nitrogen compounds thermal stability of jet A

NASA Technical Reports Server (NTRS)

Antoine, A. C.

1982-01-01

The effect of known concentrations of some nitrogen containing compounds on the thermal stability of a conventional fuel, namely, Jet A was investigated. The concentration range from 0.01 to 0.1 wt% nitrogen was examined. Solutions were made containing, individually, pyrrole, indole, quinoline, pyridine, and 4 ethylpyridine at 0.01, 0.03, 0.06, and 0.1 wt% nitrogen concentrations in Jet A. The measurements were all made by using a standard ASTM test for evaluating fuel thermal oxidation behavior, namely, ASTM D3241, 'thermal oxidation stability of turbine fuels (JFTOT procedure).' Measurements were made at two temperature settings, and 'breakpoint temperatures' were determined. The results show that the pyrrole and indole solutions have breakpoint temperatures substantially lower than those of the Jet A used.

Effect of oxidizer to fuel molar ratio on particle size and DC conductivity of CeO{sub 2} nanoparticles

DOE Office of Scientific and Technical Information (OSTI.GOV)

Harish, B. M.; Rajeeva, M. P.; Naveen, C. S.

2016-05-06

Cerium oxide nanoparticles were synthesized by solution combustion method with varying the oxidizer (cerium nitrate hexa hydrate) to fuel (Glycine) molar ratio. The prepared samples were characterized by UV-visible spectrometer, X-ray diffractometer (XRD), Scanning electron microscope (SEM) and Energy dispersive X-Ray analysis (EDAX). XRD pattern reveals the formation of cubic fluorite structure of CeO{sub 2}. It was observed that finest crystallites were found at extreme fuel-deficient condition and it is good enough to produce favorable powder characteristics. The average crystallite size was found to be 14.46 nm to 21.57 nm. The temperature dependent dc conductivity was carried out using Keithleymore » source meter between the temperature range from 300 K to 573 K. From this study it was found that the conductivity increases with increase of temperature due to semiconducting behavior of CeO{sub 2} and it decreases with particle size due to increase in the energy band gap.« less

Oxidation behavior and area specific resistance of La, Cu and B alloyed Fe-22Cr ferritic steels for solid oxide fuel cell interconnects

NASA Astrophysics Data System (ADS)

Swaminathan, Srinivasan; Ko, Yoon Seok; Lee, Young-Su; Kim, Dong-Ik

2017-11-01

Two Fe-22 wt% Cr ferritic stainless steels containing varying concentrations of La (0.14 or 0.52 wt%), Cu (0.17 or 1.74 wt%) and B (48 or 109 ppm) are investigated with respect to oxidation behavior and high temperature area specific resistance (ASR) of the surface oxide scales. To determine the oxidation resistance of developed steels, continuous isothermal oxidation is carried out at 800 °C in air, for 2000 h, and their thermally grown oxide scale is characterized using dynamic SIMS, SEM/EDX, XRD and GI-XRD techniques. To assess their electrical performance, the ASR measurement by four-point probe method is conducted at 800 °C in air, for 400 h. In higher La content steel, the La-oxides at the scale/alloy interface promotes the oxygen transport which resulted in sub-surface oxidation of Mn, Cr, Ti and Al. Moreover, the inward growth of oxides contributes to increase of Fe-Cr alloy protrusions within the scale, which reduced the ASR. In contrast, sub-surface oxidation is reduced in high Cu-alloyed steel by segregated Cu at the scale/alloy interface. Thus, addition of Cu is effective to oxidation resistance and also to better electrical performance. However, no obvious impact of B on the scale sequence and/or ASR is observed.

Phase evolution and thermal properties of yttria-stabilized hafnia nano-coatings deposited on alumina

NASA Astrophysics Data System (ADS)

Rubio, Ernesto Javier

High-temperature coatings are critical to the future power-generation systems and industries. Thermal barrier coatings (TBCs), which are usually the ceramic materials applied as thin coatings, protect engine components and allow further increase in engine temperatures for higher efficiency. Thus, the durability and reliability of the coating systems have to be more robust compared to current natural gas based engines. While a near and mid-term target is to develop TBC architecture with a 1300 °C surface temperature tolerance, a deeper understanding of the structure evolution and thermal behavior of the TBC-bond coat interface, specifically the thermally grown oxide (TGO), is of primary importance. In the present work, attention is directed towards yttria-stabilized hafnia (YSH) coatings on alumina (α-Al2O 3) to simulate the TBC-TGO interface and understand the phase evolution, microstructure and thermal oxidation of the coatings. YSH coatings were grown on α-Al2O3 substrates by sputter deposition by varying coating thickness in a wide range ˜30-1000 nm. The effect of coating thickness on the structure, morphology and the residual stress has been investigated using X-ray diffraction (XRD) and high resolution scanning electron microscopy (SEM). Thermal oxidation behavior of the coatings has been evaluated using the isothermal oxidation measurements under static conditions. X-ray diffraction analyses revealed the existence of monoclinic hafnia phase for relatively thin coatings indicating that the interfacial phenomena are dominant in phase stabilization. The evolution towards pure stabilized cubic phase of hafnia with the increasing coating thickness is observed. The SEM results indicate the changes in morphology of the coatings; the average grain size increases from 15 to 500 nm with increasing thickness. Residual stress was calculated employing XRD using the variable ψ-angle. Relation between residual stress and structural change is also studied. The results obtained on the thermal oxidation behavior indicate that the YSH coatings exhibit initial mass gain in the first 6 hours and sustained structure for extended hours of thermal treatment.

Temperature Dependence of Field-Effect Mobility in Organic Thin-Film Transistors: Similarity to Inorganic Transistors.

PubMed

Okada, Jun; Nagase, Takashi; Kobayashi, Takashi; Naito, Hiroyoshi

2016-04-01

Carrier transport in solution-processed organic thin-film transistors (OTFTs) based on dioctylbenzothienobenzothiophene (C8-BTBT) has been investigated in a wide temperature range from 296 to 10 K. The field-effect mobility shows thermally activated behavior whose activation energy becomes smaller with decreasing temperature. The temperature dependence of field-effect mobility found in C8-BTBT is similar to that of others materials: organic semiconducting polymers, amorphous oxide semiconductors and hydrogenated amorphous silicon. These results indicate that hopping transport between isoenergetic localized states becomes dominated in a low temperature regime in these materials.

Oxidation feature and diffusion mechanism of Zr-based metallic glasses near the glass transition point

NASA Astrophysics Data System (ADS)

Hu, Zheng; Lei, Xianqi; Wang, Yang; Zhang, Kun

2018-03-01

The oxidation behaviors of as-cast, pre-deformed, and crystallized Zr47.9Ti0.3Ni3.1Cu39.3Al9.4 metallic glasses (MGs) were studied near the glass transition point. The oxidation kinetics of the crystallized MGs followed a parabolic-rate law, and the as-cast and pre-deformed MGs exerted a typical two-stage behavior above the glass transition temperature (T g). Most interesting, pre-deformed treatment can significantly improve the oxidation rate of MGs, as the initial oxidation appeared earlier than for the as-cast MGs, and was accompanied by much thicker oxide scale. The EDS and XPS results showed that the metal Al acted as the preferred scavenger that absorbed intrinsic oxygen in the near-surface region of as-cast MGs. However, a homogeneous mixed layer without Al was observed in the pre-deformed MGs. We speculated the accelerated diffusion of other elements in the MGs was due to the local increase in the free volume and significant shear-induced dilation of the local structure. The results from this study demonstrate that MGs exhibit controllable atomic diffusion during the oxidation process, which can facilitate use in super-cooled liquid region applications.

Structural properties and gas sensing behavior of sol-gel grown nanostructured zinc oxide

DOE Office of Scientific and Technical Information (OSTI.GOV)

Rajyaguru, Bhargav; Gadani, Keval; Kansara, S. B.

2016-05-06

In this communication, we report the results of the studies on structural properties and gas sensing behavior of nanostructured ZnO grown using acetone precursor based modified sol-gel technique. Final product of ZnO was sintered at different temperatures to vary the crystallite size while their structural properties have been studied using X-ray diffraction (XRD) measurement performed at room temperature. XRD results suggest the single phasic nature of all the samples and crystallite size increases from 11.53 to 20.96 nm with increase in sintering temperature. Gas sensing behavior has been studied for acetone gas which indicates that lower sintered samples are moremore » capable to sense the acetone gas and related mechanism has been discussed in the light of crystallite size, crystal boundary density, defect mechanism and possible chemical reaction between gas traces and various oxygen species.« less

High Temperature Mechanical Behavior of UHTC Coatings for Thermal Protection of Re-Entry Vehicles

NASA Astrophysics Data System (ADS)

Pulci, G.; Tului, M.; Tirillò, J.; Marra, F.; Lionetti, S.; Valente, T.

2011-01-01

In this work, the high temperature mechanical properties of ultra high temperature ceramics (UHTC) coatings deposited by plasma spraying have been investigated; particularly the stress-strain relationship of ZrB2-based thick films has been evaluated by means of 4-point bending tests up to 1500 °C in air. Results show that at each investigated temperature (500, 1000, and 1500 °C) modulus of rupture (MOR) values are higher than the ones obtained at room temperature (RT); moreover at 1500 °C the UHTC coatings exhibit a marked plastic behavior, maintaining a flexural strength 25% higher compared to RT tested samples. The coefficient of linear thermal expansion (CTE) has been evaluated up to 1500 °C: obtained data are of primary importance for substrate selection, interface design and to analyze the thermo-mechanical behavior of coating-substrate coupled system. Finally, SEM-EDS analyses have been carried out on as-sprayed and tested materials in order to understand the mechanisms of reinforcement activated by high temperature exposure and to identify the microstructural modifications induced by the combination of mechanical loads and temperature in an oxidizing environment.

Encapsulation of Au Nanoparticles on a Silicon Wafer During Thermal Oxidation

PubMed Central

2013-01-01

We report the behavior of Au nanoparticles anchored onto a Si(111) substrate and the evolution of the combined structure with annealing and oxidation. Au nanoparticles, formed by annealing a Au film, appear to “float” upon a growing layer of SiO2 during oxidation at high temperature, yet they also tend to become partially encapsulated by the growing silica layers. It is proposed that this occurs largely because of the differential growth rates of the silica layer on the silicon substrate between the particles and below the particles due to limited access of oxygen to the latter. This in turn is due to a combination of blockage of oxygen adsorption by the Au and limited oxygen diffusion under the gold. We think that such behavior is likely to be seen for other metal–semiconductor systems. PMID:24163715

Investigation of Zircaloy-2 oxidation model for SFP accident analysis

NASA Astrophysics Data System (ADS)

Nemoto, Yoshiyuki; Kaji, Yoshiyuki; Ogawa, Chihiro; Kondo, Keietsu; Nakashima, Kazuo; Kanazawa, Toru; Tojo, Masayuki

2017-05-01

The authors previously conducted thermogravimetric analyses on Zircaloy-2 in air. By using the thermogravimetric data, an oxidation model was constructed in this study so that it can be applied for the modeling of cladding degradation in spent fuel pool (SFP) severe accident condition. For its validation, oxidation tests of long cladding tube were conducted, and computational fluid dynamics analyses using the constructed oxidation model were proceeded to simulate the experiments. In the oxidation tests, high temperature thermal gradient along the cladding axis was applied and air flow rates in testing chamber were controlled to simulate hypothetical SFP accidents. The analytical outputs successfully reproduced the growth of oxide film and porous oxide layer on the claddings in oxidation tests, and validity of the oxidation model was proved. Influence of air flow rate for the oxidation behavior was thought negligible in the conditions investigated in this study.

The effect of nanocrystalline silicon host on magnetic properties of encapsulated iron oxide nanoparticles.

PubMed

Granitzer, P; Rumpf, K; Gonzalez-Rodriguez, R; Coffer, J L; Reissner, M

2015-12-21

The purpose of this work is a detailed comparison of the fundamental magnetic properties of nanocomposite systems consisting of Fe3O4 nanoparticle-loaded porous silicon as well as silicon nanotubes. Such composite structures are of potential merit in the area of magnetically guided drug delivery. For magnetic systems to be utilized in biomedical applications, there are certain magnetic properties that must be fulfilled. Therefore magnetic properties of embedded Fe3O4-nanoparticles in these nanostructured silicon host matrices, porous silicon and silicon nanotubes, are investigated. Temperature-dependent magnetic investigations have been carried out for four types of iron oxide particle sizes (4, 5, 8 and 10 nm). The silicon host, in interplay with the iron oxide nanoparticle size, plays a sensitive role. It is shown that Fe3O4 loaded porous silicon and SiNTs differ significantly in their magnetic behavior, especially the transition between superparamagnetic behavior and blocked state, due to host morphology-dependent magnetic interactions. Importantly, it is found that all investigated samples meet the magnetic precondition of possible biomedical applications of exhibiting a negligible magnetic remanence at room temperature.

Kinetic and catalytic analysis of mesoporous metal oxides on the oxidation of Rhodamine B

NASA Astrophysics Data System (ADS)

Xaba, Morena S.; Noh, Ji-Hyang; Mokgadi, Keabetswe; Meijboom, Reinout

2018-05-01

In this study, we demonstrate the synthesis and catalytic activity of different mesoporous transition metal oxides, silica (SiO2), copper oxide (CuO), chromium oxide (Cr2O3), iron oxide (Fe2O3) cobalt oxide (Co3O4), cerium oxide (CeO2) and nickel oxide (NiO), on the oxidation of a pollutant dye, Rhodamine B (RhB). These metal oxides were synthesized by inverse micelle formation method and characterized by transmission electron microscopy (TEM), scanning electron microscopy (SEM), X-ray diffraction (XRD), adsorption-desorption isotherms (BET) and H2-temperature programmed reduction (TPR). UV-vis spectrophotometry was used to monitor the time-resolved absorbance of RhB at λmax = 554 nm. Mesoporous copper oxide was calcined at different final heating temperatures of 250, 350, 450 and 550 °C, and each mesoporous copper oxide catalyst showed unique physical properties and catalytic behavior. Mesoporous CuO-550 with the smallest characteristic path length δ, proved to be the catalyst of choice for the oxidation of RhB in aqueous media. We observed that the oxidation of RhB in aqueous media is dependent on the crystallite size and characteristic path length of the mesoporous metal oxide. The Langmuir-Hinshelwood model was used to fit the experimental data and to prove that the reaction occurs on the surface of the mesoporous CuO. The thermodynamic parameters, EA, ΔH#, ΔS# and ΔG# were calculated and catalyst recycling and reusability were demonstrated.

Oxidation behavior of Cr(III) during thermal treatment of chromium hydroxide in the presence of alkali and alkaline earth metal chlorides.

PubMed

Mao, Linqiang; Gao, Bingying; Deng, Ning; Liu, Lu; Cui, Hao

2016-02-01

The oxidation behavior of Cr(III) during the thermal treatment of chromium hydroxide in the presence of alkali and alkaline earth metal chlorides (NaCl, KCl, MgCl2, and CaCl2) was investigated. The amounts of Cr(III) oxidized at various temperatures and heating times were determined, and the Cr-containing species in the residues were characterized. During the transformation of chromium hydroxide to Cr2O3 at 300 °C approximately 5% of the Cr(III) was oxidized to form intermediate compounds containing Cr(VI) (i.e., CrO3), but these intermediates were reduced to Cr2O3 when the temperature was above 400 °C. Alkali and alkaline earth metals significantly promoted the oxidation of Cr(III) during the thermal drying process. Two pathways were involved in the influences the alkali and alkaline earth metals had on the formation of Cr(VI). In pathway I, the alkali and alkaline earth metals were found to act as electron transfer agents and to interfere with the dehydration process, causing more intermediate Cr(VI)-containing compounds (which were identified as being CrO3 and Cr5O12) to be formed. The reduction of intermediate compounds to Cr2O3 was also found to be hindered in pathway I. In pathway II, the alkali and alkaline earth metals were found to contribute to the oxidation of Cr(III) to form chromates. The results showed that the presence of alkali and alkaline earth metals significantly increases the degree to which Cr(III) is oxidized during the thermal drying of chromium-containing sludge. Copyright © 2015 Elsevier Ltd. All rights reserved.

Nanocrystalline coating design for extreme applications based on the concept of complex adaptive behavior

NASA Astrophysics Data System (ADS)

Fox-Rabinovich, G. S.; Veldhuis, S. C.; Dosbaeva, G. K.; Yamamoto, K.; Kovalev, A. I.; Wainstein, D. L.; Gershman, I. S.; Shuster, L. S.; Beake, B. D.

2008-04-01

The development of effective hard coatings for high performance dry machining, which is associated with high stress/temperatures during friction, is a major challenge. Newly developed synergistically alloyed nanocrystalline adaptive Ti0.2Al0.55Cr0.2Si0.03Y0.02N plasma vapor deposited hard coatings exhibit excellent tool life under conditions of high performance dry machining of hardened steel, especially under severe and extreme cutting conditions. The coating is capable of sustaining cutting speeds as high as 600 m/min. Comprehensive investigation of the microstructure and properties of the coating was performed. The structure of the coating before and after service has been characterized by high resolution transmission electron microscopy. Micromechanical characteristics of the coating have been investigated at elevated temperatures. Oxidation resistance of the coating has been studied by using thermogravimetry within a temperature range of 25-1100 °C in air. The coefficient of friction of the coatings was studied within a temperature range of 25-1200 °C. To determine the causes of excellent tool life and improved wear behavior of the TiAlCrSiYN coatings, its surface structure characteristics after service have been investigated by using x-ray photoelectron spectroscopy and extended energy-loss fine spectroscopy. One of the major features of this coating is the dynamic formation of the protective tribo-oxide films (dissipative structures) on the surface during friction with a sapphire and mullite crystal structure. Aluminum- and silicon-rich tribofilms with dangling bonds form on the surface as well. These tribofilms act in synergy and protect the surface so efficiently that it is able to sustain extreme operating conditions. Moreover, the Ti0.2Al0.55Cr0.2Si0.03Y0.02N coating possesses some features of a complex adaptive behavior because it has a number of improved characteristics (tribological adaptability, ultrafine nanocrystalline structure, hot hardness and plasticity, and oxidation stability) that work synergistically as a whole. Due to the complex adaptive behavior, this coating represents a higher ordered system that has an ability to achieve unattainable wear resistance under strongly intensifying and extreme tribological conditions.

Removal of Sulfur from CaF2 Containing Desulfurization Slag Exhausted from Secondary Steelmaking Process by Oxidation

NASA Astrophysics Data System (ADS)

Hiraki, Takehito; Kobayashi, Junichi; Urushibata, Satomi; Matsubae, Kazuyo; Nagasaka, Tetsuya

2012-08-01

The oxidation behavior of sulfur in desulfurization slag generated from the secondary steelmaking process with air has been investigated in the temperature range of 973 K to 1373 K (700 °C to 1100 °C). Although a high removal rate of sulfur is not achieved at temperatures lower than 1273 K (1000 °C) because of the formation of CaSO4, most of the sulfur is rapidly removed from slag as SO2 gas in the 1273 K to 1373 K (700 °C to 1100 °C) range. This finding indicates that the desulfurization slag generated from the secondary steelmaking process can be reused as a desulfurized flux through air oxidation, making it possible to reduce significantly the amount of desulfurization slag for disposal.

Improvement of Bipolar Switching Properties of Gd:SiOx RRAM Devices on Indium Tin Oxide Electrode by Low-Temperature Supercritical CO2 Treatment.

PubMed

Chen, Kai-Huang; Chang, Kuan-Chang; Chang, Ting-Chang; Tsai, Tsung-Ming; Liang, Shu-Ping; Young, Tai-Fa; Syu, Yong-En; Sze, Simon M

2016-12-01

Bipolar switching resistance behaviors of the Gd:SiO2 resistive random access memory (RRAM) devices on indium tin oxide electrode by the low-temperature supercritical CO2-treated technology were investigated. For physical and electrical measurement results obtained, the improvement on oxygen qualities, properties of indium tin oxide electrode, and operation current of the Gd:SiO2 RRAM devices were also observed. In addition, the initial metallic filament-forming model analyses and conduction transferred mechanism in switching resistance properties of the RRAM devices were verified and explained. Finally, the electrical reliability and retention properties of the Gd:SiO2 RRAM devices for low-resistance state (LRS)/high-resistance state (HRS) in different switching cycles were also measured for applications in nonvolatile random memory devices.

Evaluation of GeO desorption behavior in the metalGeO(2)Ge structure and its improvement of the electrical characteristics.

PubMed

Oniki, Yusuke; Koumo, Hideo; Iwazaki, Yoshitaka; Ueno, Tomo

2010-06-15

The relation between germanium monoxide (GeO) desorption and either improvement or deterioration in electrical characteristics of metalGeO(2)Ge capacitors fabricated by thermal oxidation has been investigated. In the metalGeO(2)Ge stack, two processes of GeO desorption at different sites and at different temperatures were observed by thermal desorption spectroscopy measurements. The electrical characteristics of as-oxidized metalGeO(2)Ge capacitors shows a large flat-band voltage shift and minority carrier generation due to the GeO desorption from the GeO(2)Ge interface during oxidation of Ge substrates. On the other hand, the electrical properties were drastically improved by a postmetallization annealing at low temperature resulting in a metal catalyzed GeO desorption from the top interface.

Characterization of an Ultra-High Temperature Ceramic Composite

NASA Technical Reports Server (NTRS)

Levine, Stanley R.; Opila, Elizabeth J.; Robinson, Raymond C.; Lorincz, Jonathan A.

2004-01-01

Ultra-high temperature ceramics (UHTC) are of interest for hypersonic vehicle leading edge applications. Monolithic UHTCs are of concern because of their low fracture toughness and brittle behavior. UHTC composites (UHTCC) are being investigated as a possible approach to overcome these deficiencies. In this study a small sample of a UHTCC was evaluated by limited mechanical property tests, furnace oxidation exposures, and oxidation exposures in a flowing environment generated by an oxy-acetylene torch. The composite was prepared from a carbon fiber perform using ceramic particulates and a pre-cerns about microcracking due to thermal expansion mismatch between the matrix and the carbon fiber reinforcements, and about the oxidation resistance of the HfB2-SiC coating layer and the composite constituents. However, positive performance in the torch test warrants further study of this concept.

Sensing temperature via downshifting emissions of lanthanide-doped metal oxides and salts. A review

NASA Astrophysics Data System (ADS)

Dramićanin, Miroslav D.

2016-12-01

Temperature is important because it has an effect on even the tiniest elements of daily life and is involved in a broad spectrum of human activities. That is why it is the most commonly measured physical quantity. Traditional temperature measurements encounter difficulties when used in some emerging technologies and environments, such as nanotechnology and biomedicine. The problem may be alleviated using optical techniques, one of which is luminescence thermometry. This paper reviews the state of luminescence thermometry and presents different temperature read-out schemes with an emphasis on those utilizing the downshifting emission of lanthanide-doped metal oxides and salts. The read-out schemes for temperature include those based on measurements of spectral characteristics of luminescence (band positions and shapes, emission intensity and ratio of emission intensities), and those based on measurements of the temporal behavior of luminescence (lifetimes and rise times). This review (with 140 references) gives the basics of the fundamental principles and theory that underlie the methods presented, and describes the methodology for the estimation of their performance. The major part of the text is devoted to those lanthanide-doped metal oxides and salts that are used as temperature probes, and to the comparison of their performance and characteristics.

Effect of pyrolysis temperature on chemical form, behavior and environmental risk of Zn, Pb and Cd in biochar produced from phytoremediation residue.

PubMed

Huang, Hui; Yao, Wenlin; Li, Ronghua; Ali, Amjad; Du, Juan; Guo, Di; Xiao, Ran; Guo, Zhanyu; Zhang, Zengqiang; Awasthi, Mukesh Kumar

2018-02-01

This study aimed to evaluate the chemical forms, behavior and environmental risk of heavy metal (HMs) Zn, Pb and Cd in phytoremediation residue (PMR) pyrolyzed at 350 °C, 550 °C and 750 °C, respectively. The behavior of HMs variation during the PMR pyrolysis process was analyzed and the potential HMs environmental risk of phytoremediation residue biochars (PMB) was assessed which was seldom investigated before. The results showed that the pyrolysis temperature increase decreased the soluble/exchangeable HMs fraction and alleviated the HMs bioavailability. When the temperature was over 550 °C, the adsorbed Zn(II), Pb(II) and Cd(II) were turned into oxides forms and concentrated in PMB with more stable forms exhibiting lower risk assessment code and potential ecological risk index. The ecotoxicity test showed higher pyrolysis temperature favored the reduction of PMB ecotoxicity. It is suggested that pyrolysis temperature above 550°C may be suitable for thermal treatment of PMR with acceptable environmental risk. Copyright © 2017 Elsevier Ltd. All rights reserved.

Coordinated Hard Sphere Mixture (CHaSM): A simplified model for oxide and silicate melts at mantle pressures and temperatures

NASA Astrophysics Data System (ADS)

Wolf, Aaron S.; Asimow, Paul D.; Stevenson, David J.

2015-08-01

We develop a new model to understand and predict the behavior of oxide and silicate melts at extreme temperatures and pressures, including deep mantle conditions like those in the early Earth magma ocean. The Coordinated Hard Sphere Mixture (CHaSM) is based on an extension of the hard sphere mixture model, accounting for the range of coordination states available to each cation in the liquid. By utilizing approximate analytic expressions for the hard sphere model, this method is capable of predicting complex liquid structure and thermodynamics while remaining computationally efficient, requiring only minutes of calculation time on standard desktop computers. This modeling framework is applied to the MgO system, where model parameters are trained on a collection of crystal polymorphs, producing realistic predictions of coordination evolution and the equation of state of MgO melt over a wide range of pressures and temperatures. We find that the typical coordination number of the Mg cation evolves continuously upward from 5.25 at 0 GPa to 8.5 at 250 GPa. The results produced by CHaSM are evaluated by comparison with predictions from published first-principles molecular dynamics calculations, indicating that CHaSM is accurately capturing the dominant physics controlling the behavior of oxide melts at high pressure. Finally, we present a simple quantitative model to explain the universality of the increasing Grüneisen parameter trend for liquids, which directly reflects their progressive evolution toward more compact solid-like structures upon compression. This general behavior is opposite that of solid materials, and produces steep adiabatic thermal profiles for silicate melts, thus playing a crucial role in magma ocean evolution.

Dynamic strain aging behavior of modified 9Cr-1Mo and reduced activation ferritic martensitic steels under low cycle fatigue

NASA Astrophysics Data System (ADS)

Mariappan, K.; Shankar, Vani; Sandhya, R.; Prasad Reddy, G. V.; Mathew, M. D.

2013-04-01

Influence of temperature and strain rate on low cycle fatigue (LCF) behavior of modified 9Cr-1Mo ferritic martensitic steel and 1.4W-0.06Ta reduced activation ferritic martensitic (RAFM) steel in normalized and tempered conditions was studied. Total strain controlled LCF tests between 300 and 873 K on modified 9Cr-1Mo steel and RAFM steel and at various strain rates on modified 9Cr-1Mo steel were performed at total strain amplitude of ±0.6%. Both the steels showed continuous cyclic softening at all temperatures. Whereas manifestations of dynamic strain aging (DSA) were observed in both the steels which decreased fatigue life at intermediate temperatures, at higher temperatures, oxidation played a crucial role in decreasing fatigue life.

Mechanism of sodium chloride in promoting reduction of high-magnesium low-nickel oxide ore

PubMed Central

Zhou, Shiwei; Wei, Yonggang; Li, Bo; Wang, Hua; Ma, Baozhong; Wang, Chengyan

2016-01-01

Sodium chloride has been proved that it is an effective promoter for the reduction of high-magnesium, low-nickel oxide ore. The aim of current work is to clarify the promotion behavior of sodium chloride in the roasting reduction process. The influence of moisture on the reduction of ore in the presence of sodium chloride is studied to get clear comprehension of promotion process. In the presence of moisture, the HCl is produced by pyrohydrolysis of sodium chloride for chlorinating nickel and iron oxides, moreover, interactions between metallic oxides and sodium chloride are also a way for chlorination at high temperature (>802 °C); subsequently, the metal chloride would be reduced by reductant. In the absence of moisture, the magnetic separation results show that the recoveries of iron and nickel have a significant increase; moreover, olivine structure would be destroyed gradually with the increase of roasting temperature in the action of sodium chloride, and the sodium chloride existed in high-magnesium, low-nickel oxide ore could make the NiO isolate from NiO-bearing minerals. The NiO reacts with Fe2O3 at high temperature to form NiFe2O4, which is conductive to the formation of Ni-Fe alloy during the reduction process. PMID:27374991

Mechanism of sodium chloride in promoting reduction of high-magnesium low-nickel oxide ore.

PubMed

Zhou, Shiwei; Wei, Yonggang; Li, Bo; Wang, Hua; Ma, Baozhong; Wang, Chengyan

2016-07-04

Sodium chloride has been proved that it is an effective promoter for the reduction of high-magnesium, low-nickel oxide ore. The aim of current work is to clarify the promotion behavior of sodium chloride in the roasting reduction process. The influence of moisture on the reduction of ore in the presence of sodium chloride is studied to get clear comprehension of promotion process. In the presence of moisture, the HCl is produced by pyrohydrolysis of sodium chloride for chlorinating nickel and iron oxides, moreover, interactions between metallic oxides and sodium chloride are also a way for chlorination at high temperature (>802 °C); subsequently, the metal chloride would be reduced by reductant. In the absence of moisture, the magnetic separation results show that the recoveries of iron and nickel have a significant increase; moreover, olivine structure would be destroyed gradually with the increase of roasting temperature in the action of sodium chloride, and the sodium chloride existed in high-magnesium, low-nickel oxide ore could make the NiO isolate from NiO-bearing minerals. The NiO reacts with Fe2O3 at high temperature to form NiFe2O4, which is conductive to the formation of Ni-Fe alloy during the reduction process.

Modeling of thermo-mechanical and irradiation behavior of mixed oxide fuel for sodium fast reactors

NASA Astrophysics Data System (ADS)

Karahan, Aydın; Buongiorno, Jacopo

2010-01-01

An engineering code to model the irradiation behavior of UO2-PuO2 mixed oxide fuel pins in sodium-cooled fast reactors was developed. The code was named fuel engineering and structural analysis tool (FEAST-OXIDE). FEAST-OXIDE has several modules working in coupled form with an explicit numerical algorithm. These modules describe: (1) fission gas release and swelling, (2) fuel chemistry and restructuring, (3) temperature distribution, (4) fuel-clad chemical interaction and (5) fuel-clad mechanical analysis. Given the fuel pin geometry, composition and irradiation history, FEAST-OXIDE can analyze fuel and cladding thermo-mechanical behavior at both steady-state and design-basis transient scenarios. The code was written in FORTRAN-90 program language. The mechanical analysis module implements the LIFE algorithm. Fission gas release and swelling behavior is described by the OGRES and NEFIG models. However, the original OGRES model has been extended to include the effects of joint oxide gain (JOG) formation on fission gas release and swelling. A detailed fuel chemistry model has been included to describe the cesium radial migration and JOG formation, oxygen and plutonium radial distribution and the axial migration of cesium. The fuel restructuring model includes the effects of as-fabricated porosity migration, irradiation-induced fuel densification, grain growth, hot pressing and fuel cracking and relocation. Finally, a kinetics model is included to predict the clad wastage formation. FEAST-OXIDE predictions have been compared to the available FFTF, EBR-II and JOYO databases, as well as the LIFE-4 code predictions. The agreement was found to be satisfactory for steady-state and slow-ramp over-power accidents.

Paired-pulse facilitation achieved in protonic/electronic hybrid indium gallium zinc oxide synaptic transistors

DOE Office of Scientific and Technical Information (OSTI.GOV)

Guo, Li Qiang, E-mail: guoliqiang@ujs.edu.cn; Ding, Jian Ning; Huang, Yu Kai

2015-08-15

Neuromorphic devices with paired pulse facilitation emulating that of biological synapses are the key to develop artificial neural networks. Here, phosphorus-doped nanogranular SiO{sub 2} electrolyte is used as gate dielectric for protonic/electronic hybrid indium gallium zinc oxide (IGZO) synaptic transistor. In such synaptic transistors, protons within the SiO{sub 2} electrolyte are deemed as neurotransmitters of biological synapses. Paired-pulse facilitation (PPF) behaviors for the analogous information were mimicked. The temperature dependent PPF behaviors were also investigated systematically. The results indicate that the protonic/electronic hybrid IGZO synaptic transistors would be promising candidates for inorganic synapses in artificial neural network applications.

Combinatorial assessment of the influence of composition and exposure time on the oxidation behavior and concurrent oxygeninduced phase transformations of binary Ti-x systems

NASA Astrophysics Data System (ADS)

Samimi, Peyman

The relatively low oxidation resistance and subsequent surface embrittlement have often limited the use of titanium alloys in elevated temperature structural applications. Although extensive effort is spent to investigate the high temperature oxidation performance of titanium alloys, the studies are often constrained to complex technical titanium alloys and neither the mechanisms associated with evolution of the oxide scale nor the effect of oxygen ingress on the microstructure of the base metal are well-understood. In addition lack of systematic oxidation studies across a wider domain of the alloy composition has complicated the determination of composition-mechanism-property relationships. Clearly, it would be ideal to assess the influence of composition and exposure time on the oxidation resistance, independent of experimental variabilities regarding time, temperature and atmosphere as the potential source of error. Such studies might also provide a series of metrics (e.g., hardness, scale, etc) that could be interpreted together and related to the alloy composition. In this thesis a novel combinatorial approach was adopted whereby a series of compositionally graded specimens, (Ti-xMo, Ti-xCr, Ti-xAl and Ti-xW) were prepared using Laser Engineered Net Shaping (LENS(TM)) technology and exposed to still-air at 650 °C. (Abstract shortened by ProQuest.).

A study to investigate the chemical stability of gallium phosphate oxide/gallium arsenide phosphide

NASA Technical Reports Server (NTRS)

Kuhlman, G. J.

1979-01-01

The elemental composition with depth into the oxide films was examined using secondary ion mass spectrometry. Results indicate that the layers are arsenic-deficient through the bulk of the oxide and arsenic-rich near both the oxide surface and the oxide-semiconductor interface region. Phosphorus is incorporated into the oxide in an approximately uniform manner. The MIS capacitor structures exhibited deep-depletion characteristics and hysteresis indicative of electron trapping at the oxide-semiconductor interface. Post-oxidation annealing of the films in argon or nitrogen generally results in slightly increased dielectric leakage currents and decreased C-V hysteresis effects, and is associated with arsenic loss at the oxide surface. The results of bias-temperature stress experiments indicate that the major instability effects are due to changes in the electron trapping behavior. No changes were observed in the elemental profiles following electrical stressing, indicating that the grown films are chemically stable under device operating conditions.

Inclusion Behavior During the Electron Beam Button Melting Test

NASA Astrophysics Data System (ADS)

Bellot, J. P.; Defay, B.; Jourdan, J.; Chapelle, P.; Jardy, A.

2012-10-01

The high mechanical performance of alloys developed for the manufacture of turbine disks depend upon the size and the number density of the inclusions. The electron beam button method has been practiced since the 1980s as a technique to quantify the cleanliness of the superalloys as well as to identify the nature and the size of the inclusions. The technique involves melting the sample into a hemispherical water-cooled crucible and the low density inclusions (mainly oxides) are concentrated by a combination of Marangoni and buoyancy forces into an area at the top surface of the button referred to as the raft. We have experimentally studied the behavior of oxide inclusions in special steels using both high definition video and infrared cameras. We have observed the inversion of the Marangoni effect due to the presence of sulfur, which leads to a positive temperature coefficient of the surface tension. A mathematical modeling has been carried out to simulate the turbulent fluid flow associated with the temperature field in the metallic pool of the button. The surface temperature profile has been successfully compared with the measured data. A post-processor numerical tool calculates the inclusion trajectories taking into account the turbulent fluctuation velocity by a stochastic approach. Hence, the behavior of a population of inclusions has been statistically studied, and the dependence of the capture efficiency on the inclusion size has been analyzed.

Growth behavior of anodic oxide formed by aluminum anodizing in glutaric and its derivative acid electrolytes

NASA Astrophysics Data System (ADS)

Nakajima, Daiki; Kikuchi, Tatsuya; Natsui, Shungo; Suzuki, Ryosuke O.

2014-12-01

The growth behavior of anodic oxide films formed via anodizing in glutaric and its derivative acid solutions was investigated based on the acid dissociation constants of electrolytes. High-purity aluminum foils were anodized in glutaric, ketoglutaric, and acetonedicarboxylic acid solutions under various electrochemical conditions. A thin barrier anodic oxide film grew uniformly on the aluminum substrate by glutaric acid anodizing, and further anodizing caused the film to breakdown due to a high electric field. In contrast, an anodic porous alumina film with a submicrometer-scale cell diameter was successfully formed by ketoglutaric acid anodizing at 293 K. However, the increase and decrease in the temperature of the ketoglutaric acid resulted in non-uniform oxide growth and localized pitting corrosion of the aluminum substrate. An anodic porous alumina film could also be fabricated by acetonedicarboxylic acid anodizing due to the relatively low dissociation constants associated with the acid. Acid dissociation constants are an important factor for the fabrication of anodic porous alumina films.

Experimental analysis of SiC-based refractory concrete in hybrid rocket nozzles

NASA Astrophysics Data System (ADS)

D'Elia, Raffaele; Bernhart, Gérard; Hijlkema, Jouke; Cutard, Thierry

2016-09-01

Hybrid propulsion represents a good alternative to the more widely used liquid and solid systems. This technology combines some important specifications of the latters, as the possibility of re-ignition, thrust modulation, a higher specific impulse than solid systems, a greater simplicity and a lower cost than liquid systems. Nevertheless the highly oxidizing environment represents a major problem as regards the thermo-oxidation and ablative behavior of nozzle materials. The main goal of this research is to characterize a silicon carbide based micro-concrete with a maximum aggregates size of 800 μm, in a hybrid propulsion environment. The nozzle throat has to resist to a highly oxidizing polyethylene/nitrous oxide hybrid environment, under temperatures up to 2900 K. Three tests were performed on concrete-based nozzles in HERA Hybrid Rocket Motor (HRM) test bench at ONERA. Pressure chamber evolution and observations before and after tests are used to investigate the ablated surface at nozzle throat. Ablation behavior and crack generation are discussed and some improvements are proposed.

Crystallization of copper metaphosphate glass

NASA Technical Reports Server (NTRS)

Bae, Byeong-Soo; Weinberg, Michael C.

1993-01-01

The effect of the valence state of copper in copper metaphosphate glass on the crystallization behavior and glass transition temperature has been investigated. The crystallization of copper metaphosphate is initiated from the surface and its main crystalline phase is copper metaphosphate (Cu(PO)3),independent of the (Cu sup 2+)/(Cu(total)). However, the crystal morphology, the relative crystallization rates, and their temperature dependences are affected by the (Cu sup 2+)/(Cu (total)) ratio in the glass. On the other hand, the totally oxidized glass crystallizes from all over the surface. The relative crystallization rate of the reduced glass to the totally oxidized glass is large at low temperature, but small at high temperature. The glass transition temperature of the glass increases as the (Cu sup 2+)/(Cu(total)) ratio is raised. It is also found that the atmosphere used during heat treatment does not influence the crystallization of the reduced glass, except for the formation of a very thin CuO surface layer when heated in air.

Probing and tuning the size, morphology, chemistry and structure of nanoscale cerium oxide

NASA Astrophysics Data System (ADS)

Kuchibhatla, Satyanarayana Vnt

Cerium oxide (ceria)-based materials in the nanoscale regime are of significant fundamental and technological interest. Nanoceria in pure and doped forms has current and potential use in solid oxide fuel cells, catalysis, UV-screening, chemical mechanical planarization, oxygen sensors, and bio-medical applications. The characteristic feature of Ce to switch between the +3 and +4 oxidation states renders oxygen buffering capability to ceria. The ease of this transformation was expected to be enhanced in the nanoceria. In most the practical scenarios, it is necessary to have a stable suspension of ceria nanoparticles (CNPs) over longer periods of time. However, the existing literature is confined to short term studies pertaining to synthesis and property evaluation. Having understood the need for a comprehensive understanding of the CNP suspensions, this dissertation is primarily aimed at understanding the behavior of CNPs in various chemical and physical environments. We have synthesized CNPs in the absence of any surfactants at room temperature and studied the aging characteristics. After gaining some understanding about the behavior of this functional oxide, the synthesis environment and aging temperature were varied, and their affects were carefully analyzed using various materials analysis techniques such as high resolution transmission electron microscopy (HRTEM), UV-Visible spectroscopy (UV-Vis), and X-ray photoelectron spectroscopy (XPS). When the CNPs were aged at room temperature in as-synthesized condition, they were observed to spontaneously assemble and evolve as fractal superoctahedral structures. The reasons for this unique polycrystalline morphology were attributed to the symmetry driven assembly of the individual truncated octahedral and octahedral seed of the ceria. HRTEM and Fast Fourier Transform (FFT) analyses were used to explain the agglomeration behavior and evolution of the octahedral morphology. Some of the observations were supported by molecular dynamic simulations. Poly (ethylene glycol) (PEG) and ethylene glycol (EG) were used to control the kinetics of this morphology evolution. The ability to control the agglomeration of CNPs in these media stems from the lower dielectric constant and an increased viscosity of the EG and PEG based solvents. CNPs when synthesized and aged in frozen conditions, i.e. in ice, were found to form one dimensional, high aspect ratio structures. A careful analysis has provided some evidence that the CNPs use the porous channels in ice as a template and undergo oriented attachment to form nanorods. When the aging treatment was done near freezing temperature in solution, the nanorods were not observed, confirming the role of channels in ice. When synthesized in aqueous media such as DI water, PEG and EG; CNPs were observed to exhibit a reversible oxidation state switching between +3 and +4. Band gap values were computed from the optical absorption data. The changes in the band gap values observed were attributed to the changes in the oxidation state of CNPs as opposed to the quantum confinement effects, as expected in other nanoparticle systems. The work presented in this dissertation demonstrates, with evidence, that in order to obtain a comprehensive understanding of the properties of nanoscale materials it is of paramount importance to monitor their behavior over relatively longer periods of time under various ambient environments. While the solution based techniques offer a versatility and low cost route to study the fundamental properties of nanomaterials, they suffer some inherent problems such as precursor contamination and uncontrolled chemical reactions. Especially when analyzing the behavior of ceria-based materials for applications like solid oxide fuel cells, a great control in the density and crystalline quality are desired. In order to achieve this, as a first step pure ceria thin films were synthesized using oxygen plasma assisted molecular beam epitaxy (OPA-MBE). The ceria films were analyzed using various in situ and ex situ techniques to study the crystal structure, growth mode and epitaxial quality of the films. The effect of substrate temperature on the crystalline quality of samaria doped ceria (SDC) films was studied because of its use as a potential alternative for yttria stabilized zirconia electrolyte material in low and intermediate temperature fuel cells.

Electrical transport properties in indium tin oxide films prepared by electron-beam evaporation

NASA Astrophysics Data System (ADS)

Liu, X. D.; Jiang, E. Y.; Zhang, D. X.

2008-10-01

Amorphous and polycrystalline indium tin oxide films have been prepared by electron-beam evaporation method. The amorphous films exhibit semiconductor behavior, while metallic conductivity is observed in the polycrystalline samples. The magnetoconductivities of the polycrystalline films are positive at low temperatures and can be well described by the theory of three-dimensional weak-localization effect. In addition, the electron phase-breaking rate is proportional to T3/2. Comparing the experimental results with theory, we find that the electron-electron scattering is the dominant destroyer of the constructive interference in the films. In addition, the Coulomb interaction is the main contribution to the nontrivial corrections for the electrical conductivity at low temperatures.

Creep and stress rupture of a mechanically alloyed oxide dispersion and precipitation strengthened nickel-base superalloy

NASA Technical Reports Server (NTRS)

Howson, T. E.; Tien, J. K.; Mervyn, D. A.

1980-01-01

The creep and stress rupture behavior of a mechanically alloyed oxide dispersion strengthened (ODS) and gamma-prime precipitation strengthened nickel-base alloy (alloy MA 6000E) was studied at intermediate and elevated temperatures. At 760 C, MA 6000E exhibits the high creep strength characteristic of nickel-base superalloys and at 1093 C the creep strength is superior to other ODS nickel-base alloys. The stress dependence of the creep rate is very sharp at both test temperatures and the apparent creep activation energy measured around 760 C is high, much larger in magnitude than the self-diffusion energy. Stress rupture in this large grain size material is transgranular and crystallographic cracking is observed. The rupture ductility is dependent on creep strain rate, but usually is low. These and accompanying microstructural results are discussed with respect to other ODS alloys and superalloys and the creep behavior is rationalized by invoking a recently-developed resisting stress model of creep in materials strengthened by second phase particles.

Effect of Electrode Configuration on Nitric Oxide Gas Sensor Behavior.

PubMed

Cui, Ling; Murray, Erica P

2015-09-23

The influence of electrode configuration on the impedancemetric response of nitric oxide (NO) gas sensors was investigated for solid electrochemical cells [Au/yttria-stabilized zirconia (YSZ)/Au)]. Fabrication of the sensors was carried out at 1050 °C in order to establish a porous YSZ electrolyte that enabled gas diffusion. Two electrode configurations were studied where Au wire electrodes were either embedded within or wrapped around the YSZ electrolyte. The electrical response of the sensors was collected via impedance spectroscopy under various operating conditions where gas concentrations ranged from 0 to 100 ppm NO and 1%-18% O₂ at temperatures varying from 600 to 700 °C. Gas diffusion appeared to be a rate-limiting mechanism in sensors where the electrode configuration resulted in longer diffusion pathways. The temperature dependence of the NO sensors studied was independent of the electrode configuration. Analysis of the impedance data, along with equivalent circuit modeling indicated the electrode configuration of the sensor effected gas and ionic transport pathways, capacitance behavior, and NO sensitivity.

Visualizing chemical states and defects induced magnetism of graphene oxide by spatially-resolved-X-ray microscopy and spectroscopy.

PubMed

Wang, Y F; Singh, Shashi B; Limaye, Mukta V; Shao, Y C; Hsieh, S H; Chen, L Y; Hsueh, H C; Wang, H T; Chiou, J W; Yeh, Y C; Chen, C W; Chen, C H; Ray, Sekhar C; Wang, J; Pong, W F; Takagi, Y; Ohigashi, T; Yokoyama, T; Kosugi, N

2015-10-20

This investigation studies the various magnetic behaviors of graphene oxide (GO) and reduced graphene oxides (rGOs) and elucidates the relationship between the chemical states that involve defects therein and their magnetic behaviors in GO sheets. Magnetic hysteresis loop reveals that the GO is ferromagnetic whereas photo-thermal moderately reduced graphene oxide (M-rGO) and heavily reduced graphene oxide (H-rGO) gradually become paramagnetic behavior at room temperature. Scanning transmission X-ray microscopy and corresponding X-ray absorption near-edge structure spectroscopy were utilized to investigate thoroughly the variation of the C 2p(π*) states that are bound with oxygen-containing and hydroxyl groups, as well as the C 2p(σ*)-derived states in flat and wrinkle regions to clarify the relationship between the spatially-resolved chemical states and the magnetism of GO, M-rGO and H-rGO. The results of X-ray magnetic circular dichroism further support the finding that C 2p(σ*)-derived states are the main origin of the magnetism of GO. Based on experimental results and first-principles calculations, the variation in magnetic behavior from GO to M-rGO and to H-rGO is interpreted, and the origin of ferromagnetism is identified as the C 2p(σ*)-derived states that involve defects/vacancies rather than the C 2p(π*) states that are bound with oxygen-containing and hydroxyl groups on GO sheets.

Visualizing chemical states and defects induced magnetism of graphene oxide by spatially-resolved-X-ray microscopy and spectroscopy

PubMed Central

Wang, Y. F.; Singh, Shashi B.; Limaye, Mukta V.; Shao, Y. C.; Hsieh, S. H.; Chen, L. Y.; Hsueh, H. C.; Wang, H. T.; Chiou, J. W.; Yeh, Y. C.; Chen, C. W.; Chen, C. H.; Ray, Sekhar C.; Wang, J.; Pong, W. F.; Takagi, Y.; Ohigashi, T.; Yokoyama, T.; Kosugi, N.

2015-01-01

This investigation studies the various magnetic behaviors of graphene oxide (GO) and reduced graphene oxides (rGOs) and elucidates the relationship between the chemical states that involve defects therein and their magnetic behaviors in GO sheets. Magnetic hysteresis loop reveals that the GO is ferromagnetic whereas photo-thermal moderately reduced graphene oxide (M-rGO) and heavily reduced graphene oxide (H-rGO) gradually become paramagnetic behavior at room temperature. Scanning transmission X-ray microscopy and corresponding X-ray absorption near-edge structure spectroscopy were utilized to investigate thoroughly the variation of the C 2p(π*) states that are bound with oxygen-containing and hydroxyl groups, as well as the C 2p(σ*)-derived states in flat and wrinkle regions to clarify the relationship between the spatially-resolved chemical states and the magnetism of GO, M-rGO and H-rGO. The results of X-ray magnetic circular dichroism further support the finding that C 2p(σ*)-derived states are the main origin of the magnetism of GO. Based on experimental results and first-principles calculations, the variation in magnetic behavior from GO to M-rGO and to H-rGO is interpreted, and the origin of ferromagnetism is identified as the C 2p(σ*)-derived states that involve defects/vacancies rather than the C 2p(π*) states that are bound with oxygen-containing and hydroxyl groups on GO sheets. PMID:26481557

Kinetic model to explain the effect of ocean warming and acidification on the Fe(II) oxidation rate in oligotrophic and eutrophic natural waters

NASA Astrophysics Data System (ADS)

González-Dávila, M.; Samperio-Ramos, G.; Santana-Casiano, J. M.; Gonzallez, A. G.; Pérez-Almeida, N.

2016-12-01

The speciation of inorganic Fe(II) as a function of the pH and temperature have been modeled in order to elucidate the inorganic Fe(II) redox behavior over a wide range of scenarios of acidification and global warming of the upper ocean, as well as, changes due to natural ambient fluctuations of pH and temperature. In addition, a kinetic modeling approach has been carried out to elucidate the fractional contribution of most kinetically active Fe(II) species to the overall oxidation rate to improve our future and present knowledge with respect to redox iron chemistry in the marine systems. The kinetic model considers the interactions of Fe(II) with the major ions in seawater, including phosphate and silicate and the competition with copper with the ROS. The model has been applied to the experimental results in order to describe the effect of temperature and pH in the speciation of Fe(II) and to compute the fractional contribution of each Fe(II)-specie to the overall oxidation rate. The oxidation rates (kapp) of nanomolar levels of Fe(II) have been studied in seawater enriched with nutrients (SWEN) in air saturated conditions. The nutrient effect (nitrate, phosphate and silicate), on the oxidation of Fe(II), has been evaluated as a function of pH (7.2-8.2), temperature (5-35 ºC) and salinity (10-37.09). The oxidation of Fe(II) was faster in the presence of nutrient with the change in the Fe(II) oxidation rates (Δlogkapp) more intensive at higher temperatures over the entire pH range studied. From the model it can be observed that the inorganic speciation of Fe(II) is controlled largely by pH, either in SW or in SWEN. A greater presence of Fe-nutrient reactive species (FeH3SiO4+ and FePO4-) in SWEN at higher temperatures explained the changes in the oxidation process. The individual oxidation rates by oxygen, for the Fe(II) most kinetically active species (Fe2+, FeOH+, Fe(OH)2, FeCO3(OH)-, FeCO3, Fe(CO3)22-, FeH3SiO3+, FePO4-), were fitted as a function of the temperature.

Evaluation of Cyclic Oxidation and Hot Corrosion Behavior of HVOF-Sprayed WC-Co/NiCrAlY Coating

NASA Astrophysics Data System (ADS)

Somasundaram, B.; Kadoli, Ravikiran; Ramesh, M. R.

2014-08-01

Corrosion of metallic structural materials at an elevated temperature in complex multicomponent gas environments are potential problems in many fossil energy systems, especially those using coal as a feedstock. Combating these problems involves a number of approaches, one of which is the use of protective coatings. The high velocity oxy fuel (HVOF) process has been used to deposit WC-Co/NiCrAlY composite powder on two types of Fe-based alloys. Thermocyclic oxidation behavior of coated alloys was investigated in the static air as well as in molten salt (Na2SO4-60%V2O5) environment at 700 °C for 50 cycles. The thermogravimetric technique was used to approximate the kinetics of oxidation. WC-Co/NiCrAlY coatings showed a lower oxidation rate in comparison to uncoated alloys. The oxidation resistance of WC-Co/NiCrAlY coatings can be ascribed to the oxide layer of Al2O3 and Cr2O3 formed on the outermost surface. Coated alloys extend a protective oxide scale composed of oxides of Ni and Cr that are known to impart resistance to the hot corrosion in the molten salt environment.

Interfacial engineering of solution-processed Ni nanochain-SiO{sub x} (x < 2) cermets towards thermodynamically stable, anti-oxidation solar selective absorbers

DOE Office of Scientific and Technical Information (OSTI.GOV)

Yu, Xiaobai; Wang, Xiaoxin; Liu, Jifeng, E-mail: Jifeng.Liu@dartmouth.edu

Cermet solar thermal selective absorber coatings are an important component of high-efficiency concentrated solar power (CSP) receivers. The oxidation of the metal nanoparticles in cermet solar absorbers is a great challenge for vacuum-free operation. Recently, we have demonstrated that oxidation is kinetically retarded in solution processed, high-optical-performance Ni nanochain-SiO{sub x} cermet system compared to conventional Ni-Al{sub 2}O{sub 3} system when annealed in air at 450–600 °C for several hours. However, for long-term, high-temperature applications in CSP systems, thermodynamically stable antioxidation behavior is highly desirable, which requires new mechanisms beyond kinetically reducing the oxidation rate. Towards this goal, in this paper, wemore » demonstrate that pre-operation annealing of Ni nanochain-SiO{sub x} cermets at 900 °C in N{sub 2} forms the thermodynamically stable orthorhombic phase of NiSi at the Ni/SiO{sub x} interfaces, leading to self-terminated oxidation at 550 °C in air due to this interfacial engineering. In contrast, pre-operation annealing at a lower temperature of 750 °C in N{sub 2} (as conducted in our previous work) cannot achieve interfacial NiSi formation directly, and further annealing in air at 450–600 °C for >4 h only leads to the formation of the less stable (metastable) hexagonal phase of NiSi. Therefore, the high-temperature pre-operation annealing is critical to form the desirable orthorhombic phase of NiSi at Ni/SiO{sub x} interfaces towards thermodynamically stable antioxidation behavior. Remarkably, with this improved interfacial engineering, the oxidation of 80-nm-diameter Ni nanochain-SiO{sub x} saturates after annealing at 550 °C in air for 12 h. Additional annealing at 550 °C in air for as long as 20 h (i.e., 32 h air annealing at >550 °C in total) has almost no further impact on the structural or optical properties of the coatings, the latter being very sensitive to any interfacial changes due to the localized surface plasmon resonances of the metal nanostructures. This phenomenon holds true for Ni nanoparticle diameter down to 40 nm in Ni-SiO{sub x} system, where the optical response remains stable for 53 h at 550 °C in air. The oxidation vs. time curve also shows saturation behavior deviating from the kinetic Deal-Grove oxidation model. These results strongly suggest a promising approach to thermodynamically stable, anti-oxidation Ni/SiO{sub x} cermet absorbers via interfacial engineering.« less

Estimation of Sintering Kinetics of Oxidized Magnetite Pellet Using Optical Dilatometer

NASA Astrophysics Data System (ADS)

Sandeep Kumar, T. K.; Viswanathan, Neelakantan Nurni; Ahmed, Hesham M.; Andersson, Charlotte; Björkman, Bo

2015-04-01

The quality of magnetite pellet is primarily determined by the physico-chemical changes the pellet undergoes as it makes excursion through the gaseous and thermal environment in the induration furnace. Among these physico-chemical processes, the oxidation of magnetite phase and the sintering of oxidized magnetite (hematite) and magnetite (non-oxidized) phases are vital. Rates of these processes not only depend on the thermal and gaseous environment the pellet gets exposed in the induration reactor but also interdependent on each other. Therefore, a systematic study should involve understanding these processes in isolation to the extent possible and quantify them seeking the physics. With this motivation, the present paper focusses on investigating the sintering kinetics of oxidized magnetite pellet. For the current investigation, sintering experiments were carried out on pellets containing more than 95 pct magnetite concentrate from LKAB's mine, dried and oxidized to completion at sufficiently low temperature to avoid sintering. The sintering behavior of this oxidized pellet is quantified through shrinkage captured by Optical Dilatometer. The extent of sintering characterized by sintering ratio found to follow a power law with time i.e., Kt n . The rate constant K for sintering was determined for different temperatures from isothermal experiments. The rate constant, K, varies with temperature as and the activation energy ( Q) and reaction rate constant ( K') are estimated. Further, the sintering kinetic equation was also extended to a non-isothermal environment and validated using laboratory experiments.

Development and Application of HVOF Sprayed Spinel Protective Coating for SOFC Interconnects

NASA Astrophysics Data System (ADS)

Thomann, O.; Pihlatie, M.; Rautanen, M.; Himanen, O.; Lagerbom, J.; Mäkinen, M.; Varis, T.; Suhonen, T.; Kiviaho, J.

2013-06-01

Protective coatings are needed for metallic interconnects used in solid oxide fuel cell (SOFC) stacks to prevent excessive high-temperature oxidation and evaporation of chromium species. These phenomena affect the lifetime of the stacks by increasing the area-specific resistance (ASR) and poisoning of the cathode. Protective MnCo2O4 and MnCo1.8Fe0.2O4 coatings were applied on ferritic steel interconnect material (Crofer 22 APU) by high velocity oxy fuel spraying. The substrate-coating systems were tested in long-term exposure tests to investigate their high-temperature oxidation behavior. Additionally, the ASRs were measured at 700 °C for 1000 h. Finally, a real coated interconnect was used in a SOFC single-cell stack for 6000 h. Post-mortem analysis was carried out with scanning electron microscopy. The deposited coatings reduced significantly the oxidation of the metal, exhibited low and stable ASR and reduced effectively the migration of chromium.

Oxidation kinetics of hydride-bearing uranium metal corrosion products

NASA Astrophysics Data System (ADS)

Totemeier, Terry C.; Pahl, Robert G.; Frank, Steven M.

The oxidation behavior of hydride-bearing uranium metal corrosion products from Zero Power Physics Reactor (ZPPR) fuel plates was studied using thermo-gravimetric analysis (TGA) in environments of Ar-4%O 2, Ar-9%O 2, and Ar-20%O 2. Ignition of corrosion product samples from two moderately corroded plates was observed between 125°C and 150°C in all environments. The rate of oxidation above the ignition temperature was found to be dependent only on the net flow rate of oxygen in the reacting gas. Due to the higher net oxygen flow rate, burning rates increased with increasing oxygen concentration. Oxidation rates below the ignition temperature were much slower and decreased with increasing test time. The hydride contents of the TGA samples from the two moderately corroded plates, determined from the total weight gain achieved during burning, were 47-61 wt% and 29-39 wt%. Samples from a lightly corroded plate were not reactive; X-ray diffraction (XRD) confirmed that they contained little hydride.

Elevated temperature tribology of cobalt and tantalum-based alloys

DOE PAGES

Scharf, T. W.; Prasad, S. V.; Kotula, P. G.; ...

2014-12-31

This paper describes the friction and wear behavior of a Co–Cr alloy sliding on a Ta–W alloy. Measurements were performed in a pin-on-flat configuration with a hemispherically tipped Co-base alloy pin sliding on a Ta–W alloy flat from ambient to 430°C. Focused ion beam-scanning electron microscopy (FIB-SEM) and cross-sectional transmission electron microscopy (TEM) were used to identify the friction-induced changes to the chemistry and crystal structure in the subsurface regions of wear tracks. During sliding contact, transfer of material varied as a function of the test temperature, either from pin-to-flat, flat-to-pin, or both, resulting in either wear loss and/or volumemore » gain. Friction coefficients (μ) and wear rates also varied as a function of test temperature. The lowest friction coefficient (μ=0.25) and wear rate (1×10 –4 mm 3/N•m) were observed at 430°C in argon atmosphere. This was attributed to the formation of a Co-base metal oxide layer (glaze), predominantly (Co, Cr)O with Rocksalt crystal structure, on the pin surface. Part of this oxide film transferred to the wear track on Ta–W, providing a self-mated oxide-on-oxide contact. Once the oxide glaze is formed, it is able to provide friction reduction for the entire temperature range of this study, ambient to 430°C. Furthermore, the results of this study indicate that glazing the surfaces of Haynes alloys with continuous layers of cobalt chrome oxide prior to wear could protect the cladded surfaces from damage.« less

Elevated temperature tribology of cobalt and tantalum-based alloys

DOE Office of Scientific and Technical Information (OSTI.GOV)

Scharf, T. W.; Prasad, S. V.; Kotula, P. G.

This paper describes the friction and wear behavior of a Co–Cr alloy sliding on a Ta–W alloy. Measurements were performed in a pin-on-flat configuration with a hemispherically tipped Co-base alloy pin sliding on a Ta–W alloy flat from ambient to 430°C. Focused ion beam-scanning electron microscopy (FIB-SEM) and cross-sectional transmission electron microscopy (TEM) were used to identify the friction-induced changes to the chemistry and crystal structure in the subsurface regions of wear tracks. During sliding contact, transfer of material varied as a function of the test temperature, either from pin-to-flat, flat-to-pin, or both, resulting in either wear loss and/or volumemore » gain. Friction coefficients (μ) and wear rates also varied as a function of test temperature. The lowest friction coefficient (μ=0.25) and wear rate (1×10 –4 mm 3/N•m) were observed at 430°C in argon atmosphere. This was attributed to the formation of a Co-base metal oxide layer (glaze), predominantly (Co, Cr)O with Rocksalt crystal structure, on the pin surface. Part of this oxide film transferred to the wear track on Ta–W, providing a self-mated oxide-on-oxide contact. Once the oxide glaze is formed, it is able to provide friction reduction for the entire temperature range of this study, ambient to 430°C. Furthermore, the results of this study indicate that glazing the surfaces of Haynes alloys with continuous layers of cobalt chrome oxide prior to wear could protect the cladded surfaces from damage.« less

Fretting Wear of Ti-48Al-2Cr-2Nb

NASA Technical Reports Server (NTRS)

Miyoshi, Kazuhisa; Lerch, Bradley A.; Draper, Susan L.

2001-01-01

An investigation was conducted to examine the wear behavior of gamma titanium aluminide (Ti-48Al-2Cr-2Nb in atomic percent) in contact with a typical nickel-base superalloy under repeated microscopic vibratory motion in air at temperatures from 296-823 K. The surface damage observed on the interacting surfaces of both Ti-48Al-2Cr-2Nb and superalloy consisted of fracture pits, oxides, metallic debris, scratches, craters, plastic deformation, and cracks. The Ti-48Al-2Cr-2Nb transferred to the superalloy at all fretting conditions and caused scuffing or galling. The increasing rate of oxidation at elevated temperatures led to a drop in Ti-48Al-2Cr-2Nb wear at 473 K. Mild oxidative wear was observed at 473 K. However, fretting wear increased as the temperature was increased from 473-823 K. At 723 and 823 K, oxide disruption generated cracks, loose wear debris, and pits on the Ti-48Al-2Cr-2Nb wear surface. Ti-48Al-2Cr-2Nb wear generally decreased with increasing fretting frequency. Both increasing slip amplitude and increasing load tended to produce more metallic wear debris, causing severe abrasive wear in the contacting metals. Keywords

Unusual Oxidative Limitations for Al-MAX Phases

NASA Technical Reports Server (NTRS)

Smialek, James L.

2017-01-01

Alumina-forming MAX phases are well-known for their excellent oxidation resistance, rivaling many metallic NiAl, NiCrAl, and FeCrAl counterparts and with upper temperature capability possible to approximately1400C. However a number of limitations have been emerging that need to be acknowledged to permit robust performance in demanding applications. Ti2AlC and Ti3AlC2 possess excellent scale adhesion, cyclic oxidation/moisture/volatility resistance, and TBC compatibility. However they are very sensitive to Al content and flux in order to maintain an exclusive Al2O3 scale without runaway oxidation of ubiquitous TiO2 transient scales. Accelerated oxidation has been shown to occur for Al-depleted, damaged, or roughened surfaces at temperatures less than 1200C. Conversely, Cr2AlC is less sensitive to transients, but exhibits volatile losses at 1200C or above if common Cr7C3 impurity phases are present. Poor scale adhesion is exhibited after oxidation at 1150C or above, where spallation occurs at the Cr7C3 (depletion zone) interface. Delayed spallation is significant and suggests a moisture-induced phenomenon similar to non-adherent metallic systems. Re-oxidation of this surface does not reproduce the initial pure Al2O3 behavior, but initiates a less-protective scale. Cr2AlC has also been shown to have good long term bonding with superalloys at 800C, but exhibits significant Beta-NiAl + Cr7C3 diffusion zones at 1100C and above. This may set limits on Cr2AlC as a high temperature TBC bond coat on Ni-based superalloys, while improving corrosion resistance in lower temperature applications.

Cyclic oxidation behavior of some plasma-sprayed coatings in Na2SO4-60%V2O5 environment

NASA Astrophysics Data System (ADS)

Singh, Harpreet; Prakash, Satya; Puri, Devendra; Phase, D. M.

2006-12-01

Cyclic oxidation behavior of plasma-sprayed NiCrAlY, Ni-20Cr, Ni3Al, and Stellite-6 coatings was investigated in an aggressive environment of Na2SO4-60%V2O5 by thermogravimetric techniques for 50 cycles. These coatings were deposited on a Ni-base superalloy, namely Superni 600; 10Fe-15.5Cr-0.5Mn-0.2C-Bal Ni (wt.%). X-ray diffraction, scanning electron microscopy/energy dispersive x-ray (SEM/EDX), and electron probe microanalyzer (EPMA) techniques were used to analyze the oxidation products. The uncoated superalloy suffered accelerated oxidation in the form of intense spallation of its oxide scale. After deposition of the NiCrAlY coating, the superalloy showed a minimum mass gain, whereas after application of the Stellite-6 coating, a maximum mass gain was observed among the coatings studied. All of the coatings were found to be useful in reducing the spallation of the substrate superalloy. Moreover, the coatings were successful in maintaining continuous surface contact with the base superalloy during the cyclic oxidation. The phases revealed for the oxidized coatings were mainly the oxides of chromium and/or aluminum and the spinels containing nickel-chromium/cobalt-chromium/nickel-aluminum mixed oxides, which are reported to be protective against high-temperature oxidation/hot corrosion.

Metal/silicon Interfaces and Their Oxidation Behavior - Photoemission Spectroscopy Analysis.

NASA Astrophysics Data System (ADS)

Yeh, Jyh-Jye

Synchrotron radiation photoemission spectroscopy was used to study Ni/Si and Au/Si interface properties on the atomic scale at room temperature, after high temperature annealing and after oxygen exposures. Room temperature studies of metal/Si interfaces provide background for an understanding of the interface structure after elevated temperature annealing. Oxidation studies of Si surfaces covered with metal overlayers yield insight about the effect of metal atoms in the Si oxidation mechanisms and are useful in the identification of subtle differences in bonding relations between atoms at the metal/Si interfaces. Core level and valence band spectra with variable surface sensitivities were used to study the interactions between metal, Si, and oxygen for metal coverages and oxide thickness in the monolayer region. Interface morphology at the initial stage of metal/Si interface formation and after oxidation was modeled on the basis of the evolutions of metal and Si signals at different probing depths in the photoemission experiment. Both Ni/Si and Au/Si interfaces formed at room temperature have a diffusive region at the interface. This is composed of a layer of metal-Si alloy, formed by Si outdiffusion into the metal overlayer, above a layer of interstitial metal atoms in the Si substrate. Different atomic structures of these two regions at Ni/Si interface can account for the two different growth orientations of epitaxial Ni disilicides on the Si(111) surface after thermal annealing. Annealing the Au/Si interface at high temperature depletes all the Au atoms except for one monolayer of Au on the Si(111) surface. These phenomena are attributed to differences in the metal-Si chemical bonding relations associated with specific atomic structures. After oxygen exposures, both the Ni disilicide surface and Au covered Si surfaces (with different coverages and surface orderings) show silicon in higher oxidation states, in comparison to oxidized silicon on a clean surface. Preferential Si dioxide growth on the Au/Si surface is related to the strong distortion of the Si lattice when Au-Si bonds are formed. In comparison, a monolayer of Ni on a Si surface, with its weaker Ni-Si bond, does not enhance oxide formation.

Magnetoimpedance behavior and its equivalent circuit analysis of Co/Cu/Co/Py pseudo-spin-valve with a nano-oxide layer

NASA Astrophysics Data System (ADS)

Chien, Wei-Chih; Yao, Yeong-Der; Wu, Jiann-Kuo; Lo, Chi-Kuen; Hung, Ruei-Feng; Lan, M. D.; Lin, Pang

2009-02-01

Magnetoimpedance behaviors and thermal effects of a Co/Cu/Co/Py pseudo-spin-valve (PSV) with a nano-oxide layer (NOL) were studied. The PSV can be regarded as a combination of resistances, inductances, and capacitances. In addition, equivalent circuit theory can be used to analyze the ac behavior of this system. The imaginary part of the magnetoimpedance (magnetoreactance) ratio is more than 1700% at the resonance frequency (fr)=476 kHz at room temperature (RT). The dc magnetoresistance (MR) ratio decreases as the annealing temperature increases because the NOL is formed at the interface between the spacer and the magnetic layer. The NOL deteriorates the differential spin scattering and reduces the dc MR ratio. Impedance spectroscopy was utilized to analyze the capacitance effect from NOL after annealing. The effective capacitance of the PSV was 21.8 nF at RT and changed to 11.8 nF after annealing at 200 °C. The useful equivalent capacitor circuit not only is a nondestructive measurement technology but can also explain the experimental results and prove the formation of the NOL.

Transient deformational properties of high temperature alloys used in solid oxide fuel cell stacks

NASA Astrophysics Data System (ADS)

Molla, Tesfaye Tadesse; Kwok, Kawai; Frandsen, Henrik Lund

2017-05-01

Stresses and probability of failure during operation of solid oxide fuel cells (SOFCs) is affected by the deformational properties of the different components of the SOFC stack. Though the overall stress relaxes with time during steady state operation, large stresses would normally appear through transients in operation including temporary shut downs. These stresses are highly affected by the transient creep behavior of metallic components in the SOFC stack. This study investigates whether a variation of the so-called Chaboche's unified power law together with isotropic hardening can represent the transient behavior of Crofer 22 APU, a typical iron-chromium alloy used in SOFC stacks. The material parameters for the model are determined by measurements involving relaxation and constant strain rate experiments. The constitutive law is implemented into commercial finite element software using a user-defined material model. This is used to validate the developed constitutive law to experiments with constant strain rate, cyclic and creep experiments. The predictions from the developed model are found to agree well with experimental data. It is therefore concluded that Chaboche's unified power law can be applied to describe the high temperature inelastic deformational behaviors of Crofer 22 APU used for metallic interconnects in SOFC stacks.

Effects of point defect concentrations of the reactive element oxides on the oxidation kinetics of pure Ni and Ni-Cr alloys

NASA Astrophysics Data System (ADS)

Yan, Ruey-Fong

The addition of some reactive element oxides, e.g. Ysb2Osb3 or ZrOsb2, has significant effects, e.g. improvement in scale adhesion and reduction in oxidation rate, on the oxidation behavior of chromia and alumina scale forming alloys at high temperatures. However, there is little agreement about how a small addition of an oxygen-active element can cause such profound effects. It was the goal of this project to study the growth kinetics of an oxide scale when different reactive-element oxides were added to pure Ni and Ni-Cr alloys and, consequently, to aid in clarifying the mechanism of reactive element effects. The oxidation kinetics were measured using a thermogravimetric analysis (TGA) method and the material characterization of oxide scale was conducted. The relationship between point defect structures and oxidation kinetics was discussed. The results in this research showed that Ysb2Osb3 and ZrOsb2 exhibited the reactive element effects on the oxidation behaviors of Ni and Ni-Cr alloys. In addition, the point defect concentrations of the reactive element oxide, Ysb2Osb3, were changed by doping of different valent oxides. The modification of point defect concentrations of the reactive element oxide dispersed phases did change the oxidation kinetics of the pure Ni and Ni-Cr alloys containing Ysb2Osb3. These results indicate that the transport properties of the reactive element oxide dispersed phases are one of the important factors in determining the growth rate of an oxide scale.

Behavior of tritium permeation induced by water corrosion of alpha iron around room temperature

DOE Office of Scientific and Technical Information (OSTI.GOV)

Otsuka, T.; Hashizume, K.

2015-03-15

Tritium (T) permeation leakage to surroundings is a great safety concern in fission and fusion reactor systems. T permeation potentially occurs from T contaminated water through cooling tubes or storage tank made of metals which dissolve some T evolved by water corrosion. In order to understand behaviors of hydrogen uptake and permeation in pure α-iron (αFe) during water corrosion around room temperature, hydrogen permeation experiments for an αFe membrane have been conducted by means of tritium tracer techniques. The present study suggests that hydrogen produced by water corrosion of αFe is trapped in product oxide layers to delay hydrogen uptakemore » in αFe for a moment. However, the oxide layers do not work as a sufficient barrier for hydrogen uptake. Some of hydrogen dissolved in αFe normally diffuses and permeates through the bulk in the early stage of permeation. In a later stage, hydrogen permeation could be apparently stopped by the disappearance of concentration difference of tritium. Hydrogen partial pressure at the water/αFe interface could be ranged from 0.7 to 9.5 kPa around room temperature.« less

Assessment of Titanium Aluminide Alloys for High-Temperature Nuclear Structural Applications

NASA Astrophysics Data System (ADS)

Zhu, Hanliang; Wei, Tao; Carr, David; Harrison, Robert; Edwards, Lyndon; Hoffelner, Wolfgang; Seo, Dongyi; Maruyama, Kouichi

2012-12-01

Titanium aluminide (TiAl) alloys exhibit high specific strength, low density, good oxidation, corrosion, and creep resistance at elevated temperatures, making them good candidate materials for aerospace and automotive applications. TiAl alloys also show excellent radiation resistance and low neutron activation, and they can be developed to have various microstructures, allowing different combinations of properties for various extreme environments. Hence, TiAl alloys may be used in advanced nuclear systems as high-temperature structural materials. Moreover, TiAl alloys are good materials to be used for fundamental studies on microstructural effects on irradiation behavior of advanced nuclear structural materials. This article reviews the microstructure, creep, radiation, and oxidation properties of TiAl alloys in comparison with other nuclear structural materials to assess the potential of TiAl alloys as candidate structural materials for future nuclear applications.

Advanced smart tungsten alloys for a future fusion power plant

NASA Astrophysics Data System (ADS)

Litnovsky, A.; Wegener, T.; Klein, F.; Linsmeier, Ch; Rasinski, M.; Kreter, A.; Tan, X.; Schmitz, J.; Mao, Y.; Coenen, J. W.; Bram, M.; Gonzalez-Julian, J.

2017-06-01

The severe particle, radiation and neutron environment in a future fusion power plant requires the development of advanced plasma-facing materials. At the same time, the highest level of safety needs to be ensured. The so-called loss-of-coolant accident combined with air ingress in the vacuum vessel represents a severe safety challenge. In the absence of a coolant the temperature of the tungsten first wall may reach 1200 °C. At such a temperature, the neutron-activated radioactive tungsten forms volatile oxide which can be mobilized into atmosphere. Smart tungsten alloys are being developed to address this safety issue. Smart alloys should combine an acceptable plasma performance with the suppressed oxidation during an accident. New thin film tungsten-chromium-yttrium smart alloys feature an impressive 105 fold suppression of oxidation compared to that of pure tungsten at temperatures of up to 1000 °C. Oxidation behavior at temperatures up to 1200 °C, and reactivity of alloys in humid atmosphere along with a manufacturing of reactor-relevant bulk samples, impose an additional challenge in smart alloy development. First exposures of smart alloys in steady-state deuterium plasma were made. Smart tungsten-chroimium-titanium alloys demonstrated a sputtering resistance which is similar to that of pure tungsten. Expected preferential sputtering of alloying elements by plasma ions was confirmed experimentally. The subsequent isothermal oxidation of exposed samples did not reveal any influence of plasma exposure on the passivation of alloys.

Nonequilibrium synthesis of NbAl3 and Nb-Al-V alloys by laser cladding. II - Oxidation behavior

NASA Technical Reports Server (NTRS)

Haasch, R. T.; Tewari, S. K.; Sircar, S.; Loxton, C. M.; Mazumder, J.

1992-01-01

Isothermal oxidation behaviors of NbAl3 alloy synthesized by laser cladding were investigated at temperatures between 800 and 1400 C, and the effect of vanadium microalloying on the oxidation of the laser-clad alloy was examined. The oxidation kinetics of the two alloys were monitored using thermal gravimetric weight gain data, and the bulk and surface chemistries were analyzed using XRD and XPS, respectively. It was found that NbAl3 did not form an exclusive layer of protective Al2O3. The oxidation products at 800 C were found to be a mixture of Nb2O5 and Al2O3. At 1200 C, a mixture of NbAlO4, Nb2O5, and Al2O3 formed; and at 1400 C, a mixture of NbAlO4, Al2O3, NbO2, NbO(2.432), and Nb2O5 formed. The addition of V led to a dramatic increase of the oxidation rate, which may be related to the formation of (Nb, V)2O5 and VO2, which grows in preference to protective Al2O3.

In-situ XPS analysis of oxidized and reduced plasma deposited ruthenium-based thin catalytic films

NASA Astrophysics Data System (ADS)

Balcerzak, Jacek; Redzynia, Wiktor; Tyczkowski, Jacek

2017-12-01

A novel in-situ study of the surface molecular structure of catalytically active ruthenium-based films subjected to the oxidation (in oxygen) and reduction (in hydrogen) was performed in a Cat-Cell reactor combined with a XPS spectrometer. The films were produced by the plasma deposition method (PEMOCVD). It was found that the films contained ruthenium at different oxidation states: metallic (Ru0), RuO2 (Ru+4), and other RuOx (Ru+x), of which content could be changed by the oxidation or reduction, depending on the process temperature. These results allow to predict the behavior of the Ru-based catalysts in different redox environments.

Modeling Oxidation Induced Stresses in Thermal Barrier Coatings

NASA Technical Reports Server (NTRS)

Ferguson, B. L.; Freborg, A. M.; Petrus, G. J.; Brindley, William J.

1998-01-01

The use of thermal barrier coatings (TBC's) in gas turbines has increased dramatically in recent years, due mainly to the need for component protection from ever increasing service temperatures. Oxidation of the bond coat has been identified as an important contributing factor to spallation of the ceramic top coat during service. Additional variables found to influence TBC thermal cycle life include bond coat coefficient of thermal expansion, creep behavior of both the ceramic and bond coat layers, and modulus of elasticity. The purpose of this work was to characterize the effects of oxidation on the stress states within the TBC system, as well as to examine the interaction of oxidation with other factors affecting TBC life.

Structural studies on carbon materials for advanced space technology. Part 1: Structure and oxidation behavior of some carbon/carbon composite materials

NASA Technical Reports Server (NTRS)

Fischbach, D. B.; Uptegrove, D. R.; Srinivasagopalan, S.

1974-01-01

The microstructure and some microstructural effects of oxidation have been investigated for laminar carbon fiber cloth/cloth binder matrix composite materials. It was found that cloth wave is important in determining the macrostructure of the composites X-ray diffraction analysis showed that the composites were more graphitic than the constituent fiber phases, indicating a graphitic binder matrix phase. Various tests which were conducted to investigate specific properties of the material are described. It was learned that under the moderate temperature and oxidant flow conditions studied, C-700, 730 materials exhibit superior oxidation resistance primarily because of the inhibiting influence of the graphitized binder matrix.

Oxidation kinetics of CVD silicon carbide and silicon nitride

NASA Technical Reports Server (NTRS)

Fox, Dennis S.

1992-01-01

The long-term oxidation behavior of pure, monolithic CVD SiC and Si3N4 is studied, and the isothermal oxidation kinetics of these two materials are obtained for the case of 100 hrs at 1200-1500 C in flowing oxygen. Estimates are made of lifetimes at the various temperatures investigated. Parabolic rate constants for SiC are within an order of magnitude of shorter exposure time values reported in the literature. The resulting silica scales are in the form of cristobalite, with cracks visible after exposure. The oxidation protection afforded by silica for these materials is adequate for long service times under isothermal conditions in 1-atm dry oxygen.

Issues Concerning the Oxidation of Ni(Pt)Ti Shape Memory Alloys

NASA Technical Reports Server (NTRS)

Smialek, James

2011-01-01

The oxidation behavior of the Ni-30Pt-50Ti high temperature shape memory alloy is compared to that of conventional NiTi nitinol SMAs. The oxidation rates were 1/4 those of NiTi under identical conditions. Ni-Ti-X SMAs are dominated by TiO2 scales, but, in some cases, the activation energy diverges for unexplained reasons. Typically, islands of metallic Ni or Pt(Ni) particles are embedded in lower scale layers due to rapid selective growth of TiO2 and low oxygen potential within the scale. The blocking effect of Pt-rich particles and lower diffusivity of Pt-rich depletion zones are proposed to account for the reduction in oxidation rates.

Comparison of Ductile-to-Brittle Transition Behavior in Two Similar Ferritic Oxide Dispersion Strengthened Alloys.

PubMed

Chao, Jesus; Rementeria, Rosalia; Aranda, Maria; Capdevila, Carlos; Gonzalez-Carrasco, Jose Luis

2016-07-29

The ductile-to-brittle transition (DBT) behavior of two similar Fe-Cr-Al oxide dispersion strengthened (ODS) stainless steels was analyzed following the Cottrell-Petch model. Both alloys were manufactured by mechanical alloying (MA) but by different forming routes. One was manufactured as hot rolled tube, and the other in the form of hot extruded bar. The two hot forming routes considered do not significantly influence the microstructure, but cause differences in the texture and the distribution of oxide particles. These have little influence on tensile properties; however, the DBT temperature and the upper shelf energy (USE) are significantly affected because of delamination orientation with regard to the notch plane. Whereas in hot rolled material the delaminations are parallel to the rolling surface, in the hot extruded material, they are randomly oriented because the material is transversally isotropic.

Scale Adhesion, Sulfur Content, and TBC Failure on Single Crystal Superalloys

NASA Technical Reports Server (NTRS)

Smialek, James L.

2002-01-01

This paper summarizes the main effects of sulfur impurity content on the cyclic oxidation resistance of single crystal superalloys, with emphasis on scale and TBC adhesion. Eleven hundred degrees C cyclic oxidation of PWA 1480 produces scale spallation leading to a weight loss of more than 30 Mg/sq cm after 500 one-hr cycles for a sulfur content of 6 ppmw. The sulfur content was reduced to levels below 0.1 ppmw by hydrogen annealing, resulting in weight gains of only 0.5 to 1.0 Mg/sq cm after 1000 one-hr cycles. Samples were produced with various sulfur contents by adjusting the annealing temperature, time, and sample thickness (i.e., diffusion product Dt/L(exp 2)). The subsequent cyclic oxidation behavior, mapped over a sulfur content/thickness diagram, shows a transition to adherent behavior at sulfur levels equivalent to 1 monolayer of total segregation. Additional information is contained in the original extended abstract.

Comparison of Ductile-to-Brittle Transition Behavior in Two Similar Ferritic Oxide Dispersion Strengthened Alloys

PubMed Central

Chao, Jesus; Rementeria, Rosalia; Aranda, Maria; Capdevila, Carlos; Gonzalez-Carrasco, Jose Luis

2016-01-01

The ductile-to-brittle transition (DBT) behavior of two similar Fe-Cr-Al oxide dispersion strengthened (ODS) stainless steels was analyzed following the Cottrell–Petch model. Both alloys were manufactured by mechanical alloying (MA) but by different forming routes. One was manufactured as hot rolled tube, and the other in the form of hot extruded bar. The two hot forming routes considered do not significantly influence the microstructure, but cause differences in the texture and the distribution of oxide particles. These have little influence on tensile properties; however, the DBT temperature and the upper shelf energy (USE) are significantly affected because of delamination orientation with regard to the notch plane. Whereas in hot rolled material the delaminations are parallel to the rolling surface, in the hot extruded material, they are randomly oriented because the material is transversally isotropic. PMID:28773764

Interfacial control of oxygen vacancy doping and electrical conduction in thin film oxide heterostructures

DOE PAGES

Veal, Boyd W.; Kim, Seong Keun; Zapol, Peter; ...

2016-06-10

Oxygen vacancies in proximity to surfaces and heterointerfaces in oxide thin film heterostructures have major effects on properties, resulting, for example, in emergent conduction behavior, large changes in metal-insulator transition temperatures, or enhanced catalytic activity. Here in this paper, we report the discovery of a means of reversibly controlling the oxygen vacancy concentration and distribution in oxide heterostructures consisting of electronically conducting In 2O 3 films grown on ionically conducting Y 2O 3-stabilized ZrO 2 substrates. Oxygen ion redistribution across the heterointerface is induced using an applied electric field oriented in the plane of the interface, resulting in controlled oxygenmore » vacancy (and hence electron) doping of the film and possible orders-of-magnitude enhancement of the film's electrical conduction. The reversible modified behavior is dependent on interface properties and is attained without cation doping or changes in the gas environment.« less

Visible photoassisted room-temperature oxidizing gas-sensing behavior of Sn2S3 semiconductor sheets through facile thermal annealing.

PubMed

Liang, Yuan-Chang; Lung, Tsai-Wen; Wang, Chein-Chung

2016-12-01

Well-crystallized Sn 2 S 3 semiconductor thin films with a highly (111)-crystallographic orientation were grown using RF sputtering. The surface morphology of the Sn 2 S 3 thin films exhibited a sheet-like feature. The Sn 2 S 3 crystallites with a sheet-like surface had a sharp periphery with a thickness in a nanoscale size, and the crystallite size ranged from approximately 150 to 300 nm. Postannealing the as-synthesized Sn 2 S 3 thin films further in ambient air at 400 °C engendered roughened and oxidized surfaces on the Sn 2 S 3 thin films. Transmission electron microscopy analysis revealed that the surfaces of the Sn 2 S 3 thin films transformed into a SnO 2 phase, and well-layered Sn 2 S 3 -SnO 2 heterostructure thin films were thus formed. The Sn 2 S 3 -SnO 2 heterostructure thin film exhibited a visible photoassisted room-temperature gas-sensing behavior toward low concentrations of NO 2 gases (0.2-2.5 ppm). By contrast, the pure Sn 2 S 3 thin film exhibited an unapparent room-temperature NO 2 gas-sensing behavior under illumination. The suitable band alignment at the interface of the Sn 2 S 3 -SnO 2 heterostructure thin film and rough surface features might explain the visible photoassisted room-temperature NO 2 gas-sensing responses of the heterostructure thin film on exposure to NO 2 gas at low concentrations in this work.

Temperature Dependent Electrical and Micromechanical Properties of Lanthanum Titanate with Additions of Yttria

NASA Technical Reports Server (NTRS)

Goldsby, Jon C.

2003-01-01

Lanthanum titanate (La2Ti2O7) a layered distorted perovskite (1) with space group Pna2(sub 1) has been shown to have potential as a high temperature piezoelectric (2). However this highly refractory oxide compound must be consolidated at relatively high temperatures approximately 1400 C. Commercial La2Ti207 powders were mechanically alloyed with additions of Y2O3 to lower the consolidation temperature by 300 C and to provide post processing mechanical stability. Temperature dependent electrical, elastic and anelastic behavior were selected as nondestructive means of evaluating the effects of yttria on the properties of this ferroceramic material.

Phase relations in iron-rich systems and implications for the earth's core

NASA Technical Reports Server (NTRS)

Anderson, William W.; Svendsen, Bob; Ahrens, Thomas J.

1987-01-01

Recent experimental data concerning the properties of iron, iron sulfide, and iron oxide at high pressures are combined with theoretical arguments to constrain the probable behavior of the Fe-rich portions of the Fe-O and Fe-S phase diagrams. Phase diagrams are constructed for the Fe-S-O system at core pressures and temperatures. These properties are used to evaluate the current temperature distribution and composition of the core.

Corrosion Behavior Of Potential Structural Materials For Use In Nitrate Salts Based Solar Thermal Power Plants

NASA Astrophysics Data System (ADS)

Summers, Kodi

The increasing global demand for electricity is straining current resources of fossil fuels and placing increased pressure on the environment. The implementation of alternative sources of energy is paramount to satisfying global electricity demand while reducing reliance on fossil fuels and lessen the impact on the environment. Concentrated solar power (CSP) plants have the ability to harness solar energy at an efficiency not yet achieved by other technologies designed to convert solar energy to electricity. The problem of intermittency in power production seen with other renewable technologies can be virtually eliminated with the use of molten salt as a heat transfer fluid in CSP plants. Commercial and economic success of CSP plants requires operating at maximum efficiency and capacity which requires high temperature and material reliability. This study investigates the corrosion behavior of structural alloys and electrochemical testing in molten nitrate salts at three temperatures common to CSP plants. Corrosion behavior was evaluated using gravimetric and inductively-coupled plasma optical emission spectroscopy (ICP-OES) analysis. Surface morphology was studied using scanning electron microscopy. Surface oxide structure and chemistry was characterized using X-ray diffraction, Raman spectroscopy, energy dispersive spectroscopy, and X-ray photoelectron spectroscopy. Electrochemical behavior of candidate structural alloys Alloy 4130, austenitic stainless steel 316, and super-austenitic Incoloy 800H was evaluated using potentiodynamic polarization characteristics. It was observed that electrochemical evaluation of these candidate materials correlates well with the corrosion behavior observed from gravimetric and ICP-OES analysis. This study identifies that all three alloys exhibited acceptable corrosion in 300°C molten salt while elevated salt temperatures require the more corrosion resistant alloys, stainless steel 316 and 800H. Characterization of the sample surfaces revealed the presence of spinels at lower temperatures, while Fe2O3 was the dominant iron oxide at higher temperatures for each alloy. It is recommended that accelerated corrosion testing be investigated further to evaluate alloys in other molten salt systems considered for utilization in concentrated solar power plants.

Evaluation of GeO desorption behavior in the metal∕GeO2∕Ge structure and its improvement of the electrical characteristics

PubMed Central

Oniki, Yusuke; Koumo, Hideo; Iwazaki, Yoshitaka; Ueno, Tomo

2010-01-01

The relation between germanium monoxide (GeO) desorption and either improvement or deterioration in electrical characteristics of metal∕GeO2∕Ge capacitors fabricated by thermal oxidation has been investigated. In the metal∕GeO2∕Ge stack, two processes of GeO desorption at different sites and at different temperatures were observed by thermal desorption spectroscopy measurements. The electrical characteristics of as-oxidized metal∕GeO2∕Ge capacitors shows a large flat-band voltage shift and minority carrier generation due to the GeO desorption from the GeO2∕Ge interface during oxidation of Ge substrates. On the other hand, the electrical properties were drastically improved by a postmetallization annealing at low temperature resulting in a metal catalyzed GeO desorption from the top interface. PMID:20644659

Response of Cr and Cr-Al coatings on Zircaloy-2 to high temperature steam

NASA Astrophysics Data System (ADS)

Zhong, Weicheng; Mouche, Peter A.; Heuser, Brent J.

2018-01-01

The oxidation behavior of chromium (Cr) and chromium-aluminum (CrAl) coatings with various compositions deposited on Zircaloy-2 to 700 °C high-temperature steam (HTS) exposure has been investigated. CrAl coatings with higher Al compositions demonstrate lower oxidation weight gain. A layer of γ-alumina developed on the CrAl coatings with Al composition over 43 at%, while Al2O3 and Cr2O3 developed on CrAl coatings with Al composition below 33 at%. Oxidation of Zircaloy-2 substrate was inhibited by the 1um coatings to 20 h HTS exposure. Coating constituent elements diffused into the substrate and formed intermetallic phases with the Zircaloy substrate. Thicker layers of intermetallic phases developed on the coatings with higher Al composition. The intermetallic phases included Fe and Ni, indicating the dissolution of second phase particles (SPPs) during HTS exposure.

Low temperature formation of higher-k cubic phase HfO{sub 2} by atomic layer deposition on GeO{sub x}/Ge structures fabricated by in-situ thermal oxidation

DOE Office of Scientific and Technical Information (OSTI.GOV)

Zhang, R., E-mail: zhang@mosfet.t.u-tokyo.ac.jp; Department of Information Science and Electronic Engineering, Zhejiang University, 38 Zheda Road, Hangzhou 310027; Huang, P.-C.

2016-02-01

We have demonstrated a low temperature formation (300 °C) of higher-k HfO{sub 2} using atomic layer deposition (ALD) on an in-situ thermal oxidation GeO{sub x} interfacial layer. It is found that the cubic phase is dominant in the HfO{sub 2} film with an epitaxial-like growth behavior. The maximum permittivity of 42 is obtained for an ALD HfO{sub 2} film on a 1-nm-thick GeO{sub x} form by the in-situ thermal oxidation. It is suggested from physical analyses that the crystallization of cubic phase HfO{sub 2} can be induced by the formation of six-fold crystalline GeO{sub x} structures in the underlying GeO{sub x}more » interfacial layer.« less

A Finite Length Cylinder Model for Mixed Oxide-Ion and Electron Conducting Cathodes Suited for Intermediate-Temperature Solid Oxide Fuel Cells

DOE PAGES

Jin, Xinfang; Wang, Jie; Jiang, Long; ...

2016-03-25

A physics-based model is presented to simulate the electrochemical behavior of mixed ion and electron conducting (MIEC) cathodes for intermediate-temperature solid oxide fuel cells. Analytic solutions for both transient and impedance models based on a finite length cylinder are derived. These solutions are compared to their infinite length counterparts. The impedance solution is also compared to experimental electrochemical impedance spectroscopy data obtained from both a traditional well-established La 0.6Sr 0.4Co 0.2Fe 0.8O 3-δ (LSCF) cathode and a new SrCo 0.9Nb 0.1O 3-δ (SCN) porous cathode. Lastly, the impedance simulations agree well with the experimental values, demonstrating that the new modelsmore » can be used to extract electro-kinetic parameters of MIEC SOFC cathodes.« less

Influence of Surface Finishing on the Oxidation Behaviour of VPS MCrAlY Coatings

NASA Astrophysics Data System (ADS)

Fossati, Alessio; di Ferdinando, Martina; Bardi, Ugo; Scrivani, Andrea; Giolli, Carlo

2012-03-01

CoNiCrAlY coatings were produced by means of the vacuum plasma spraying (VPS) process onto CMSX-4 single crystal nickel superalloy disk substrates. As-sprayed samples were annealed at high temperatures in low vacuum. Three kinds of finishing processes were carried out, producing three types of samples: as-sprayed, mechanically smoothed by grinding, ground and PVD coated by using aluminum targets in an oxygen atmosphere. Samples were tested under isothermal conditions, in air, at 1000 °C, and up to 5000 h. Morphological, microstructural and compositional analyses were performed on the coated samples in order to assess the high temperature oxidation behavior provided by the three different surface finishing processes. Several differences were observed: grinding operations decrease the oxidation resistance, whereas the PVD process can increase the performances over longer time with respect of the as-sprayed samples.

Room temperature synthesis of Cu₂O nanospheres: optical properties and thermal behavior.

PubMed

Nunes, Daniela; Santos, Lídia; Duarte, Paulo; Pimentel, Ana; Pinto, Joana V; Barquinha, Pedro; Carvalho, Patrícia A; Fortunato, Elvira; Martins, Rodrigo

2015-02-01

The present work reports a simple and easy wet chemistry synthesis of cuprous oxide (Cu2O) nanospheres at room temperature without surfactants and using different precursors. Structural characterization was carried out by X-ray diffraction, transmission electron microscopy, and scanning electron microscopy coupled with focused ion beam and energy-dispersive X-ray spectroscopy. The optical band gaps were determined from diffuse reflectance spectroscopy. The photoluminescence behavior of the as-synthesized nanospheres showed significant differences depending on the precursors used. The Cu2O nanospheres were constituted by aggregates of nanocrystals, in which an on/off emission behavior of each individual nanocrystal was identified during transmission electron microscopy observations. The thermal behavior of the Cu2O nanospheres was investigated with in situ X-ray diffraction and differential scanning calorimetry experiments. Remarkable structural differences were observed for the nanospheres annealed in air, which turned into hollow spherical structures surrounded by outsized nanocrystals.

TEM/STEM study of Zircaloy-2 with protective FeAl(Cr) layers under simulated BWR environment and high-temperature steam exposure

NASA Astrophysics Data System (ADS)

Park, Donghee; Mouche, Peter A.; Zhong, Weicheng; Mandapaka, Kiran K.; Was, Gary S.; Heuser, Brent J.

2018-04-01

FeAl(Cr) thin-film depositions on Zircaloy-2 were studied using transmission electron microscopy (TEM) and scanning transmission electron microscopy (STEM) with respect to oxidation behavior under simulated boiling water reactor (BWR) conditions and high-temperature steam. Columnar grains of FeAl with Cr in solid solution were formed on Zircaloy-2 coupons using magnetron sputtering. NiFe2O4 precipitates on the surface of the FeAl(Cr) coatings were observed after the sample was exposed to the simulated BWR environment. High-temperature steam exposure resulted in grain growth and consumption of the FeAl(Cr) layer, but no delamination at the interface. Outward Al diffusion from the FeAl(Cr) layer occurred during high-temperature steam exposure (700 °C for 3.6 h) to form a 100-nm-thick alumina oxide layer, which was effective in mitigating oxidation of the Zircaloy-2 coupons. Zr intermetallic precipitates formed near the FeAl(Cr) layer due to the inward diffusion of Fe and Al. The counterflow of vacancies in response to the Al and Fe diffusion led to porosity within the FeAl(Cr) layer.

First-principles study on oxidation effects in uranium oxides and high-pressure high-temperature behavior of point defects in uranium dioxide

NASA Astrophysics Data System (ADS)

Geng, Hua Y.; Song, Hong X.; Jin, K.; Xiang, S. K.; Wu, Q.

2011-11-01

Formation Gibbs free energy of point defects and oxygen clusters in uranium dioxide at high-pressure high-temperature conditions are calculated from first principles, using the LSDA+U approach for the electronic structure and the Debye model for the lattice vibrations. The phonon contribution on Frenkel pairs is found to be notable, whereas it is negligible for the Schottky defect. Hydrostatic compression changes the formation energies drastically, making defect concentrations depend more sensitively on pressure. Calculations show that, if no oxygen clusters are considered, uranium vacancy becomes predominant in overstoichiometric UO2 with the aid of the contribution from lattice vibrations, while compression favors oxygen defects and suppresses uranium vacancy greatly. At ambient pressure, however, the experimental observation of predominant oxygen defects in this regime can be reproduced only in a form of cuboctahedral clusters, underlining the importance of defect clustering in UO2+x. Making use of the point defect model, an equation of state for nonstoichiometric oxides is established, which is then applied to describe the shock Hugoniot of UO2+x. Furthermore, the oxidization and compression behavior of uranium monoxide, triuranium octoxide, uranium trioxide, and a series of defective UO2 at 0 K are investigated. The evolution of mechanical properties and electronic structures with an increase of the oxidation degree are analyzed, revealing the transition of the ground state of uranium oxides from metallic to Mott insulator and then to charge-transfer insulator due to the interplay of strongly correlated effects of 5f orbitals and the shift of electrons from uranium to oxygen atoms.

Evidence of alloy formation during reduction of platinized tin oxide surfaces

NASA Technical Reports Server (NTRS)

Gardner, Steven D.; Hoflund, Gar B.; Davidson, Mark R.; Schryer, David R.

1989-01-01

Ion scattering spectroscopy, Auger electron spectroscopy, and electron spectroscopy for chemical analysis have been used to examine a platinized tin oxide catalyst surface before, during, and after reduction by annealing under vacuum at 250 to 450 C. These techniques were then used to examine the reduced surface after a room-temperature, low-pressure oxygen exposure. The spectral results and the behavior of the reduced surface toward oxygen exposure both indicate that a Pt/Sn alloy is produced during reduction.

Fiber Strength of Hi Nicalon(TM) S After Oxidation and Scale Crystallization in Si(OH)4 Saturated Steam (Postprint)

DTIC Science & Technology

2017-02-06

conducted for the longest times because the fibers would completely oxidize. The SiO2 tube would warp during experiments run at temperatures over 1200° C ...Chollon, G.; Labrugere, C .; Lahaye, M.; Guette, A.; Bruneel, J . L.; Couzi, M.; Naslain, R.; Jiang, D. L., Characterization of Nearly Stoichiometric...Electron Beam Irradiation Curing - A Review. J . Ceram. Soc. Japan 2006, 114, 455-460. 8. Sauder, C .; Lamon, J ., Tensile Creep Behavior of SiC-Based Fibers

Practical field repair of fused slurry silicide coating for space shuttle t.p.s.

NASA Technical Reports Server (NTRS)

Reznik, B. D.

1971-01-01

Study of short-time high-temperature diffusion treatments as part of a program of development of methods of reapplying fused slurry silicide coating in the field. The metallographic structure and oxidation behavior of R512E applied to Cb-752 coated under simulated field repair conditions was determined. Oxidation testing in reduced pressure environment has shown that performance equivalent to furnace-processed specimens can be obtained in a two-minute diffusion at 2700 F.

Modulated Transport Behavior of Two-Dimensional Electron Gas at Ni-Doped LaAlO3/SrTiO3 Heterointerfaces.

PubMed

Yan, Hong; Zhang, Zhaoting; Wang, Shuanhu; Zhang, Hongrui; Chen, Changle; Jin, Kexin

2017-11-08

Modulating transport behaviors of two-dimensional electron gases are of critical importance for applications of the next-generation multifunctional oxide electronics. In this study, transport behaviors of LaAlO 3 /SrTiO 3 heterointerfaces modified through the Ni dopant and the light irradiation have been investigated. Through the Ni dopant, the resistances increase significantly and a resistance upturn phenomenon due to the Kondo effect is observed at T < 40 K. Under a 360 nm light irradiation, the interfaces exhibit a persistent photoconductivity and a suppressed Kondo effect at low temperature due to the increased mobility measured through the photo-Hall method. Moreover, the relative changes in resistance of interfaces induced by light are increased from 800 to 6600% at T = 12 K with increasing the substitution of Ni, which is discussed by the band bending and the lattice effect due to the Ni dopant. This work paves the way for better controlling the emerging properties of complex oxide heterointerfaces and would be helpful for photoelectric device applications based on all-oxides.

Thermodynamic analysis on heavy metals partitioning impacted by moisture during the MSW incineration

DOE Office of Scientific and Technical Information (OSTI.GOV)

Zhang Yanguo; Li Qinghai; Jia Jinyan

2012-12-15

Highlights: Black-Right-Pointing-Pointer Partitioning of HMs affected by moisture was investigated by thermodynamic analysis. Black-Right-Pointing-Pointer Increase in moisture and in temperature was opposite impact on HMs contribution. Black-Right-Pointing-Pointer The extent of temperature decreased by increase in moisture determines the impact. - Abstract: A thermodynamic calculation was carried out to predict the behavior and speciation of heavy metals (HMs), Pb, Zn, Cu, and Cd, during municipal solid waste (MSW) incineration with the different moisture levels. The calculation was based on the minimization of the total Gibbs free energy of the multi-components and multi-phases closed system reaching chemical equilibrium. The calculation also indicatedmore » the reaction directions and tendencies of HMs components. The impacts of chlorine additives (No PVC, 1%PVC, and 5%PVC) and moisture on the behavior of HMs were investigated at different temperature levels in the system (750 Degree-Sign C, 950 Degree-Sign C, and 1150 Degree-Sign C). Furthermore, because the incineration temperature falls down with the increase in moisture in waste, the co-influence of moisture and temperature in combusting MSW on the HMs was also studied with the given chlorine (as 1%PVC + 0.5%NaCl). The results showed that in the non-chlorine system, the impact of the moisture on Pb, Zn, and Cu was not significant, and the ratio of compound transformation was less than 10%, except the Cd compounds at 950 Degree-Sign C and 1150 Degree-Sign C. In the system with low chlorine (as 1%PVC) at constant temperature, the chlorides of HMs (Cd, Pb, Zn, and Cu) transferred to oxides, and when the content of chlorine rose up (as 5%PVC), the ratio of the chlorides of HMs (Cd, Pb, Zn, and Cu) transferring to oxides fell down noticeably. When the moisture varied together with the temperature, the Zn and Cu compounds transferred from chlorides to oxides with increase in moisture as well as decrease in temperature. At the temperature of 700-1000 Degree-Sign C, the impact of temperature on Pb and Cd was little and the moisture was the main factor; while at the temperature of 1000-1200 Degree-Sign C, the impact of increase in moisture and decrease in temperature on Pb and Cd was almost equal and reversed.« less

Thermal annealing behavior of nano-size metal-oxide particles synthesized by ion implantation in Fe-Cr alloy

NASA Astrophysics Data System (ADS)

Zheng, C.; Gentils, A.; Ribis, J.; Borodin, V. A.; Descoins, M.; Mangelinck, D.; Dalle, F.; Arnal, B.; Delauche, L.

2017-05-01

Oxide dispersion strengthened (ODS) steels are promising structural materials for the next generation nuclear reactors, as well as fusion facilities. The detailed understanding of the mechanisms involved in the precipitation of nano-oxides during ODS steel production would strongly contribute to the improvement of the mechanical properties and the optimization of manufacturing of ODS steels, with a potentially strong economic impact for their industrialization. A useful tool for the experimental study of nano-oxide precipitation is ion implantation, a technique that is widely used to synthesize precipitate nanostructures in well-controlled conditions. Earlier, we have demonstrated the feasibility of synthesizing aluminum-oxide particles in the high purity Fe-10Cr alloy by consecutive implantation with Al and O ions at room temperature. This paper describes the effects of high-temperature annealing after the ion implantation stage on the development of the aluminum based oxide nanoparticle system. Using transmission electron microscopy and atom probe tomography experiments, we demonstrate that post-implantation heat treatment induces the growth of the nano-sized oxides in the implanted region and nucleation of new oxide precipitates behind the implantation zone as a result of the diffusion driven broadening of implant profiles. A tentative scenario for the development of metal-oxide nano-particles at both ion implantation and heat treatment stages is suggested based on the experimental observations.

Oxidative damage and brain concentrations of free amino acid in chicks exposed to high ambient temperature.

PubMed

Chowdhury, Vishwajit S; Tomonaga, Shozo; Ikegami, Taro; Erwan, Edi; Ito, Kentaro; Cockrem, John F; Furuse, Mitsuhiro

2014-03-01

High ambient temperatures (HT) reduce food intake and body weight in young chickens, and HT can cause increased expression of hypothalamic neuropeptides. The mechanisms by which HT act, and the effects of HT on cellular homeostasis in the brain, are however not well understood. In the current study lipid peroxidation and amino acid metabolism were measured in the brains of 14 d old chicks exposed to HT (35 °C for 24- or 48-h) or to control thermoneutral temperature (CT; 30 °C). Malondialdehyde (MDA) was measured in the brain to determine the degree of oxidative damage. HT increased body temperature and reduced food intake and body weight gain. HT also increased diencephalic oxidative damage after 48 h, and altered some free amino acid concentrations in the diencephalon. Diencephalic MDA concentrations were increased by HT and time, with the effect of HT more prominent with increasing time. HT altered cystathionine, serine, tyrosine and isoleucine concentrations. Cystathionine was lower in HT birds compared with CT birds at 24h, whilst serine, tyrosine and isoleucine were higher at 48 h in HT birds. An increase in oxidative damage and alterations in amino acid concentrations in the diencephalon may contribute to the physiological, behavioral and thermoregulatory responses of heat-exposed chicks. Copyright © 2013 Elsevier Inc. All rights reserved.

Mercury emissions and species during combustion of coal and waste

DOE Office of Scientific and Technical Information (OSTI.GOV)

Hong Yao; Guangqian Luo; Minghou Xu

2006-10-15

The behaviors of mercury evolution for three types of coal and three types of dried sewage sludge are studied using a thermogravimetric (TG) analyzer. The mercury speciations in the flue gas from coal and sludge combustion are also analyzed by implementing a horizontal electrically heated tube furnace. Furthermore, the kinetic calculations of mercury oxidizing processes are carried out using the software package CHEMKIN in order to interpret the homogeneous mechanism of mercury oxidization. The results obtained show that the sulfur content in the sludge inhibits the evolution of mercury at low temperature if the Cl concentration is high enough. Chlorinemore » enhances mercury evolution in the coal combustion, whereas there is no relationship when the Cl concentration is high. Fixed carbon content plays a role in depression of the mercury evolution. Formation of oxidized mercury (HgCl{sub 2}) does not relate to the chlorine concentration in the raw coal and sludge. Whereas the ash and sulfur content in the sludge affects the Hg oxidization, kinetic calculations show that HgCl, Cl{sub 2}, and HOCl formation is important in producing the oxidized mercury during combustion of coal and sludge at 873 K. A suitable temperature for Hg oxidization when Cl{sub 2} is the oxidization resource is 700-1200 K. 32 refs., 10 figs., 5 tabs.« less

Oxidation State Discrimination in the Atomic Layer Deposition of Vanadium Oxides

DOE PAGES

Weimer, Matthew S.; Kim, In Soo; Guo, Peijun; ...

2017-06-02

We describe the use of a vanadium 3+ precursor for atomic layer deposition (ALD) of thin films that span the common oxidation states of vanadium oxides. Self-limiting surface synthesis of V 2O 3, VO 2, and V 2O 5 are realized via four distinct reaction mechanisms accessed via judicious choice of oxygen ALD partners. In situ quartz crystal microbalance and quadrupole mass spectrometry were used to study the reaction mechanism of the vanadium precursor with O 3, H 2O 2, H 2O/O 2, and H 2O 2/H 2. A clear distinction between non-oxidative protic ligand exchange and metal oxidation ismore » demonstrated through sequential surface reactions with different non-metal precursors. This synergistic effect, provides greater control of the resultant metal species in the film, as well as reactive surface species during growth. In an extension of this approach, we introduce oxidation state control through reducing equivalents of H 2 gas. When H 2 is dosed after H 2O 2 during growth, amorphous films of VO 2 are deposited that are readily crystallized with a low temperature anneal. These VO 2 films show a temperature dependent Raman spectroscopy response in the expected range and consistent with the well-known phase-change behavior of VO 2.« less

Microstructural effects on the room and elevated temperature low cycle fatigue behavior of Waspaloy. M.S. Thesis Final Report

NASA Technical Reports Server (NTRS)

Lerch, B. A.

1982-01-01

Longitudinal specimens of Waspaloy containing either coarse grains with small gamma or fine grains with large gamma were tested in air at a frequency of 0.33 Hz or 0.50 Hz. The coarse grained structures exhibited planar slip on (III) planes and precipitate shearing at all temperatures. Cracks initiated by a Stage 1 mechanism and propagated by a striation forming mechanism. At 700 C and 800 C, cleavage and intergranular cracking were observed. Testing at 500 C, 700 C, and 800 C caused precipitation of grain boundary carbides. At 700 C, carbides precipitated on slip bands. The fine grained structures exhibited planar slip on (111) planes. Dislocations looped the large gamma precipitates. This structure led to stress saturation and propagation was observed. Increasing temperatures resulted in increased specimen oxidation for both heat treatments. Slip band and grain boundary oxidation were observed. At 800 C, oxidized grain boundaries were cracked by intersecting slip bands which resulted in intergranular failure. The fine specimens had crack initiation later in the fatigue life, but with more rapid propagation crack propagation.

Comparative investigation of five nanoparticles in flow of viscous fluid with Joule heating and slip due to rotating disk

NASA Astrophysics Data System (ADS)

Qayyum, Sumaira; Khan, Muhammad Ijaz; Hayat, Tasawar; Alsaedi, Ahmed

2018-04-01

Present article addresses the comparative study for flow of five water based nanofluids. Flow in presence of Joule heating is generated by rotating disk with variable thickness. Nanofluids are suspension of Silver (Ag), Copper (Cu), Copper oxide (CuO), Aluminum oxide or Alumina (Al2O3), Titanium oxide or titania (TiO2) and water. Boundary layer approximation is applied to partial differential equations. Using Von Karman transformations the partial differential equations are converted to ordinary differential equations. Convergent series solutions are obtained. Graphical results are presented to examine the behaviors of axial, radial and tangential velocities, temperature, skin friction and Nusselt number. It is observed that radial, axial and tangential velocities decay for slip parameters. Axial velocity decays for larger nanoparticle volume fraction. Effect of nanofluids on velocities dominant than base material. Temperature rises for larger Eckert number and temperature of silver water nanofluid is more because of its higher thermal conductivity. Surface drag force reduces for higher slip parameters. Transfer of heat is more for larger disk thickness index.

Lithium alloy negative electrodes

NASA Astrophysics Data System (ADS)

Huggins, Robert A.

The 1996 announcement by Fuji Photo Film of the development of lithium batteries containing convertible metal oxides has caused a great deal of renewed interest in lithium alloys as alternative materials for use in the negative electrode of rechargeable lithium cells. The earlier work on lithium alloys, both at elevated and ambient temperatures is briefly reviewed. Basic principles relating thermodynamics, phase diagrams and electrochemical properties under near-equilibrium conditions are discussed, with the Li-Sn system as an example. Second-phase nucleation, and its hindrance under dynamic conditions plays an important role in determining deviations from equilibrium behavior. Two general types of composite microstructure electrodes, those with a mixed-conducting matrix, and those with a solid electrolyte matrix, are discussed. The Li-Sn-Si system at elevated temperatures, and the Li-Sn-Cd at ambient temperatures are shown to be examples of mixed-conducting matrix microstructures. The convertible oxides are an example of the solid electrolyte matrix type. Although the reversible capacity can be very large in this case, the first cycle irreversible capacity required to convert the oxides to alloys may be a significant handicap.

A Deterministic Interfacial Cyclic Oxidation Spalling Model. Part 1; Model Development and Parametric Response

NASA Technical Reports Server (NTRS)

Smialek, James L.

2002-01-01

An equation has been developed to model the iterative scale growth and spalling process that occurs during cyclic oxidation of high temperature materials. Parabolic scale growth and spalling of a constant surface area fraction have been assumed. Interfacial spallation of the only the thickest segments was also postulated. This simplicity allowed for representation by a simple deterministic summation series. Inputs are the parabolic growth rate constant, the spall area fraction, oxide stoichiometry, and cycle duration. Outputs include the net weight change behavior, as well as the total amount of oxygen and metal consumed, the total amount of oxide spalled, and the mass fraction of oxide spalled. The outputs all follow typical well-behaved trends with the inputs and are in good agreement with previous interfacial models.

Crack healing behavior of hot pressed silicon nitride due to oxidation

NASA Technical Reports Server (NTRS)

Choi, S. R.; Tikare, V.

1992-01-01

It is shown that limited oxidation of an MgO-containing, hot-pressed silicon nitride ceramic at 800 deg C and above results in increased strength due to crack healing. Slight oxidation of the surface produces enstatite and cristobalite which fills in cracks. More extensive oxidation leads to strength degradation due to the formation of new flaws by the evolution of N2 gas at the surface. The apparent fracture toughness also increased at 800 deg C and above due to oxidation. Bonds formed between the two surfaces of the crack during oxidation leads to a reduction in stress intensity at the crack tip, suggesting that valid high-temperature toughness values cannot be obtained in an air environment. The increase in strength due to crack healing by oxidation can be achieved without compromising the fatigue properties of the silicon nitride ceramic.

Comparison of Graphite Fabric Reinforced PMR-15 and Avimid N Composites After Long Term Isothermal Aging at Various Temperatures

NASA Technical Reports Server (NTRS)

Bowles, Kenneth J.; McCorkle, Linda; Ingrahm, Linda

1998-01-01

Extensive effort is currently being expended to demonstrate the feasibility of using high-performance, polymer-matrix composites as engine structural materials over the expected operating lifetime of the aircraft, which can extend from 18,000 to 30,000 hr. The goal is to develop light-weight, high-strength, and high-modulus materials for use in higher temperature sections of advanced 21 st century aircraft propulsion systems. To accomplish this goal, it is necessary to pursue the development of thermal and mechanical durability models for graphite-fiber-reinforced, polymer-matrix composites. Numerous investigations have been reported regarding the thermo-oxidative stability (TOS) of the polyimide PMR-15 (1-5). A significant amount of this work has been directed at edge and geometry effects, reinforcement fiber influences, and empirical modeling of high-temperature weight loss behavior. It is yet to be determined if the information obtained from the PMR-15 composite tests is applicable to other polyimide-matrix composites. The condensation-curing polymer Avimid N is another advanced composite material often considered for structural applications at high temperatures. Avimid N has better thermo-oxidative stability than PMR-15 (6), but the latter is more easily processed. The most comprehensive study of the thermo-oxidative stability of Avimid N neat resin and composites at 371 (infinity)C is found in Salin and Seferis (7). The purposes of the work described herein were to compare the thermal aging behavior of these two matrix polymers and to determine the reasons for and the consequences of the difference in thermal durability. These results might be of some use in improving future polymer development through the incorporation of the desirable characteristics of both polyimides.

Biodiesel: Characterization by DSC and P-DSC

NASA Astrophysics Data System (ADS)

Chiriac, Rodica; Toche, François; Brylinski, Christian

Thermal analytical methods such as differential scanning calorimetry (DSC) have been successfully applied to neat petrodiesel and engine oils in the last 25 years. This chapter shows how DSC and P-DSC (pressurized DSC) techniques can be used to compare, characterize, and predict some properties of alternative non-petroleum fuels, such as cold flow behavior and oxidative stability. These two properties are extremely important with respect to the operability, transport, and long-term storage of biodiesel fuel. It is shown that the quantity of unsaturated fatty acids in the fuel composition has an important impact on both properties. In addition, it is shown that the impact of fuel additives on the oxidative stability or the cold flow behavior of biodiesel can be studied by means of DSC and P-DSC techniques. Thermomicroscopy can also be used to study the cold flow behavior of biodiesel, giving information on the size and the morphology of crystals formed at low temperature.

Anomalous magnetic behavior in nanocomposite materials of reduced graphene oxide-Ni/NiFe{sub 2}O{sub 4}

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kollu, Pratap, E-mail: pk419@cam.ac.uk, E-mail: anirmalagrace@vit.ac.in, E-mail: dhirenb@iitb.ac.in; Prathapani, Sateesh; Varaprasadarao, Eswara K.

2014-08-04

Magnetic Reduced Graphene Oxide-Nickel/NiFe{sub 2}O{sub 4} (RGO-Ni/NF) nanocomposite has been synthesized by one pot solvothermal method. Respective phase formations and their purities in the composite are confirmed by High Resolution Transmission Electron Microscope and X Ray Diffraction, respectively. For the RGO-Ni/NF composite material finite-size effects lead to the anomalous magnetic behavior, which is corroborated in temperature and field dependent magnetization curves. Here, we are reporting the behavior of higher magnetization values for Zero Field Cooled condition to that of Field Cooled for the RGO-Ni/NF nanocomposite. Also, the observed negative and positive moments in Hysteresis loops at relatively smaller applied fieldsmore » (100 Oe and 200 Oe) are explained on the basis of surface spin disorder.« less

In situ high temperature oxidation analysis of Zircaloy-4 using acoustic emission coupled with thermogravimetry

NASA Astrophysics Data System (ADS)

Omar, Al Haj; Véronique, Peres; Eric, Serris; François, Grosjean; Jean, Kittel; François, Ropital; Michel, Cournil

2015-06-01

Zircaloy-4 oxidation behavior at high temperature (900 °C), which can be reached in case of severe accidental situations in nuclear pressurised water reactor, was studied using acoustic emission analysis coupled with thermogravimetry. Two different atmospheres were used to study the oxidation of Zircaloy-4: (a) helium and pure oxygen, (b) helium and oxygen combined with slight addition of air. The experiments with 20% of oxygen confirm the dependence on oxygen anions diffusion in the oxide scale. Under a mixture of oxygen and air in helium, an acceleration of the corrosion was observed due to the detrimental effect of nitrogen. The kinetic rate increased significantly after a kinetic transition (breakaway). This acceleration was accompanied by an acoustic emission activity. Most of the acoustic emission bursts were recorded after the kinetic transition (post-transition) or during the cooling of the sample. The characteristic features of the acoustic emission signals appear to be correlated with the different populations of cracks and their occurrence in the ZrO2 layer or in the α-Zr(O) layer. Acoustic events were recorded during the isothermal dwell time at high temperature under air. They were associated with large cracks in the zirconia porous layer. Acoustic events were also recorded during cooling after oxidation tests both under air or oxygen. For the latter, cracks were observed in the oxygen enriched zirconium metal phase and not in the dense zirconia layer after 5 h of oxidation.

Thermal properties of rare earth cobalt oxides and of La1- x Gd x CoO3 solid solutions

NASA Astrophysics Data System (ADS)

Orlov, Yu. S.; Dudnikov, V. A.; Gorev, M. V.; Vereshchagin, S. N.; Solov'ev, L. A.; Ovchinnikov, S. G.

2016-05-01

Powder X-ray diffraction data for the crystal structure, phase composition, and molar specific heat for La1‒ x Gd x CoO3 cobaltites in the temperature range of 300-1000 K have been analyzed. The behavior of the volume thermal expansion coefficient in cobaltites with isovalent doping in the temperature range of 100-1000 K is studied. It is found that the β( T) curve exhibits two peaks at some doping levels. The rate of the change in the occupation number for the high-spin state of cobalt ions is calculated for the compounds under study taking into account the spin-orbit interaction. With the Birch-Murnaghan equation of state, it is demonstrated that the low-temperature peak in the thermal expansion shifts with the growth of the pressure toward higher temperatures and at pressure P ˜ 7 GPa coincides with the second peak. The similarity in the behavior of the thermal expansion coefficient in the La1- x Gd x CoO3 compounds with the isovalent substitution and the undoped LnCoO3 compound (Ln is a lanthanide) is considered. For the whole series of rare earth cobalt oxides, the nature of two specific features in the temperature dependence of the specific heat and thermal expansion is revealed and their relation to the occupation number for the high-spin state of cobalt ions and to the insulator-metal transition is established.

Rheological study of the effect of polyethylene oxide (PEO) homopolymer on the gelation of PEO-PPO-PEO triblock copolymer in aqueous solution

NASA Astrophysics Data System (ADS)

Li, Xiaolei; Hyun, Kyu

2018-05-01

The effects of polyethylene oxide (PEO) homopolymer on the gelation behavior of a PEO100-PPO65-PEO100 triblock copolymer (Pluronic F127) were explored in aqueous solution under non-isothermal and isothermal conditions. Under non-isothermal conditions (temperature sweep test), two transition points were observed on increasing temperature, that is, at lower and upper gelation temperatures (LTgel and UTgel, respectively). Between LTgel and UTgel, F127 aqueous solutions maintained a hard gel state. Both molecular weight (MW) and PEO concentration affected these two gelation temperatures. In particular, relative molecular weight (MWrel ≡ molecular weight of PEO homopolymer/PEO segment of F127) affected LTgel. LTgel decreased on increasing PEO concentration at MWrel values of <1, but increased on increasing PEO concentration at MWrel values of >1. On the other hand, UTgel decreased with increasing PEO concentration regardless of MWrel. Under isothermal conditions (fixed temperature between LTgel and UTgel), the effects of PEO homopolymer on the mechanical properties of F127 hard gel were systemically investigated using small and large amplitude oscillatory shear tests. In the linear viscoelastic regime, total intra-cycle stress and elastic intra-cycle stress were similar, and viscous response increased on increasing PEO concentration. However, at large strain amplitudes, hard gels showed intra-cycle stiffening but inter-cycle softening behavior. In addition, on increasing PEO concentrations, viscous nonlinearities underwent strain-rate thickening followed by strain-rate thinning.

Synthesis and ferroelectric properties of La-substituted PZFNT

NASA Astrophysics Data System (ADS)

Singh, Pratibha; Singh, Sangeeta; Juneja, J. K.; Prakash, Chandra; Raina, K. K.; Kumar, Vinod; Pant, R. P.

2010-01-01

In this paper we are reporting a systematic study on ferroelectric properties of lanthanum (La) substituted modified lead zirconate titanate (PLZFNT) ceramics which were fabricated by mixed oxide process. La contents were varied in between 0 and 0.01 in steps of 0.0025. The X-ray diffraction study shows single phase for all samples. Silver electrode was deposited on flat surfaces of sintered discs for P-E (polarization vs. electric field) measurements. All compositions exhibited well-defined ferroelectric behavior at room temperature. Hysteresis loops were also recorded at different temperatures for all the compositions which showed typical variation of ferroelectric nature. The PLZFNT composition with 1 mol% of La showed the best retention behavior. The results are discussed.

The corrosion behavior of Alloy 52 weld metal in cyclic hydrogenated and oxygenated water chemistry in high temperature aqueous environment

NASA Astrophysics Data System (ADS)

Xu, Jian; Shoji, Tetsuo

2015-06-01

The corrosion behavior of Alloy 52 weld metal in cyclic hydrogenated and oxygenated water chemistry in high temperature water is studied by in situ monitoring corrosion potential (Ecorr), contact electric resistance (CER) and electrochemical impedance measurements (EIS), and ex situ scanning electron microscopy (SEM) and X-ray photoelectron spectroscopy (XPS) analysis. The Ecorr and film resistance show large change when the environment is changed from hydrogenated water to oxygenated water and changeable with changing environment while the morphology and composition only show obvious distinction in the first cycle. The main factor controlling the electric/electrochemical properties of the oxide film is Ecorr.

Effect of Nanoscale Fillers on the Local Mechanical Behavior of Polymer Nanocomposites

DTIC Science & Technology

2009-12-01

the interparticle spacing can be related to the particle volume fraction, vp, and the particle diameter, d, by [2] r = d 6v„ d) I I (b) Figure...VGCNFs), namely as- fabricated (PR-24-XT PS), high temperature hear treated (PR-24-XT-HHT-LD), and high temperature hear treated and oxidatively...Therefore, hear treatment had a severe effect on the fracture toughness of composites with embedded VGCNFs. This agrees with composite level

Tensile properties of V-Cr-Ti alloys after exposure in oxygen-containing environments

DOE Office of Scientific and Technical Information (OSTI.GOV)

Natesan, K.; Soppet, W.K.

A systematic study was conducted to evaluate the oxidation kinetics of V-4Cr-4Ti (44 alloy) and V-5Cr-5Ti alloys (55 alloy) and to establish the role of oxygen ingress on the tensile behavior of the alloys at room temperature and at 500 C. The oxidation rate of the 44 alloy is slightly higher than that of the 55 alloy. The oxidation process followed parabolic kinetics. Maximum engineering stress for 55 alloy increased with an increase in oxidation time at 500 C. The maximum stress values for 55 alloy were higher at room temperature than ta 500 C for the same oxidation treatment.more » Maximum engineering stresses for 44 alloy were substantially lower than those for 55 alloy in the same oxidation {approx}500 h exposure in air at 500 C; the same values were 4.8 and 6.1%, respectively, at 500 C after {approx}2060 h oxidation in air at 500 C. Maximum engineering stress for 44 alloy at room temperature was 421.6--440.6 MPa after {approx}250 h exposure at 500 C in environments with a pO{sub 2} range of 1 {times} 10{sup {minus}6} to 760 torr. The corresponding uniform and total elongation values were 11--14.4% and 14.5--21.7%, respectively. Measurements of crack depths in various specimens showed that depth is independent of pO{sub 2} in the preexposure environment and was of 70--95 {micro}m after 250--275 h exposure at 500 C.« less

MTDATA and the Prediction of Phase Equilibria in Oxide Systems: 30 Years of Industrial Collaboration

NASA Astrophysics Data System (ADS)

Gisby, John; Taskinen, Pekka; Pihlasalo, Jouni; Li, Zushu; Tyrer, Mark; Pearce, Jonathan; Avarmaa, Katri; Björklund, Peter; Davies, Hugh; Korpi, Mikko; Martin, Susan; Pesonen, Lauri; Robinson, Jim

2017-02-01

This paper gives an introduction to MTDATA, Phase Equilibrium Software from the National Physical Laboratory (NPL), and describes the latest advances in the development of a comprehensive database of thermodynamic parameters to underpin calculations of phase equilibria in large oxide, sulfide, and fluoride systems of industrial interest. The database, MTOX, has been developed over a period of thirty years based upon modeling work at NPL and funded by industrial partners in a project co-ordinated by Mineral Industry Research Organisation. Applications drawn from the fields of modern copper scrap smelting, high-temperature behavior of basic oxygen steelmaking slags, flash smelting of nickel, electric furnace smelting of ilmenite, and production of pure TiO2 via a low-temperature molten salt route are discussed along with calculations to assess the impact of impurities on the uncertainty of fixed points used to realize the SI unit of temperature, the kelvin.

Studies of Oxidation of the Cu(100) Surface Using Low Energy Positrons

NASA Astrophysics Data System (ADS)

Fazleev, N. G.; Maddox, W. B.; Nadesalingam, M.; Rajeshwar, K.; Weiss, A. H.

2009-03-01

Changes in the surface of an oxidized Cu(100) single crystal resulting from vacuum annealing have been investigated using positron annihilation induced Auger electron spectroscopy (PAES). PAES measurements show a large increase in the intensity of the positron annihilation induced Cu M2,3VV Auger peak as the sample is subjected to a series of isochronal anneals in vacuum up to annealing temperature 300° C. The intensity then decreases monotonically as the annealing temperature is increased to ˜600° C. Experimental PAES results are analyzed by performing calculations of positron surface states and annihilation probabilities of surface-trapped positrons with relevant core electrons taking into account the charge redistribution at the surface, surface reconstructions, and electron-positron correlations effects. Possible explanation for the observed behavior of the intensity of positron annihilation induced Cu M2,3VV Auger peak with changes of the annealing temperature is proposed.

Studies of oxidation of the Cu(100) surface using low energy positrons.

NASA Astrophysics Data System (ADS)

Maddox, W. B.; Fazleev, N. G.; Weiss, A. H.

2009-03-01

Changes in the surface of an oxidized Cu(100) single crystal resulting from vacuum annealing have been investigated using positron annihilation induced Auger electron spectroscopy (PAES). PAES measurements show a large increase in the intensity of the positron annihilation induced Cu M2,3VV Auger peak as the sample is subjected to a series of isochronal anneals in vacuum up to annealing temperature 300^o C. The intensity then decreases monotonically as the annealing temperature is increased to ˜600^o C. Experimental PAES results are analyzed by performing calculations of positron surface states and annihilation probabilities of surface-trapped positrons with relevant core electrons taking into account the charge redistribution at the surface, surface reconstructions, and electron-positron correlations effects. Possible explanation for the observed behavior of the intensity of positron annihilation induced Cu M2,3VV Auger peak with changes of the annealing temperature is proposed.

2D- and 3D SIMS investigations on hot-pressed steel powder HS 6-5-3-8.

PubMed

Rosner, M; Pöckl, G; Danninger, H; Hutter, H

2002-10-01

Processing of steel with powder metallurgical methods such as sintering or hot-pressing have proven to be a powerful tool for the production of industrial parts and for components in the automotive industry. Series of steel-powders (HS 6-5-3-8) produced by gas atomization has been hot-pressed in a graphite tube at temperatures from 820 degrees C to 1050 degrees C. The samples have been characterized with a Secondary Electron Microscope (SEM) due to their porosity and then investigated with 2D- and 3D- SIMS. The spatial distribution of the non-metallic impurities and the covering oxide layer of the single particles has been traced dependent to the pressing temperature. Powders pressed at temperatures higher than 880 degrees C exhibited different precipitation behavior of the impurities and an excessive loss of the covering oxide layer of the single powder particles.

Ab initio Investigation of Helium in Vanadium Oxide Nanoclusters

NASA Astrophysics Data System (ADS)

Danielson, Thomas; Tea, Eric; Hin, Celine

Nanostructured ferritic alloys (NFAs) are strong candidate materials for the next generation of fission reactors and future fusion reactors. They are characterized by a large number density of oxide nanoclusters dispersed throughout a BCC iron matrix, where current oxide nanoclusters are primarily comprised of Y-Ti-O compounds. The oxide nanoclusters provide the alloy with high resistance to neutron irradiation, high yield strength and high creep strength at the elevated temperatures of a reactor environment. In addition, the oxide nanoclusters serve as trapping sites for transmutation product helium providing substantially increased resistance to catastrophic cracking and embrittlement. Although the mechanical properties and radiation resistance of the existing NFAs is promising, the problem of forming large scale reactor components continues to present a formidable challenge due to the high hardness and unpredictable fracture behavior of the alloys. An alternative alloy has been previously proposed and fabricated where vanadium is added in order to form vanadium oxide nanoclusters that serve as deflection sites for crack propagation. Although experiments have shown evidence that the fracture behavior of the alloys is improved, it is unknown whether or not the vanadium oxide nanoclusters are effective trapping sites for helium. We present results obtained using density functional theory investigating the thermodynamic stability of helium with the vanadium oxide matrix to make a comparison of trapping effectiveness to traditional Y-Ti-O compounds.

Ligand-hole localization in oxides with unusual valence Fe

PubMed Central

Chen, Wei-Tin; Saito, Takashi; Hayashi, Naoaki; Takano, Mikio; Shimakawa, Yuichi

2012-01-01

Unusual high-valence states of iron are stabilized in a few oxides. A-site-ordered perovskite-structure oxides contain such iron cations and exhibit distinct electronic behaviors at low temperatures, e.g. charge disproportionation (4Fe4+ → 2Fe3+ + 2Fe5+) in CaCu3Fe4O12 and intersite charge transfer (3Cu2+ + 4Fe3.75+ → 3Cu3+ + 4Fe3+) in LaCu3Fe4O12. Here we report the synthesis of solid solutions of CaCu3Fe4O12 and LaCu3Fe4O12 and explain how the instabilities of their unusual valence states of iron are relieved. Although these behaviors look completely different from each other in simple ionic models, they can both be explained by the localization of ligand holes, which are produced by the strong hybridization of iron d and oxygen p orbitals in oxides. The localization behavior in the charge disproportionation of CaCu3Fe4O12 is regarded as charge ordering of the ligand holes, and that in the intersite charge transfer of LaCu3Fe4O12 is regarded as a Mott transition of the ligand holes. PMID:22690318

Emerging Applications of Liquid Metals Featuring Surface Oxides

PubMed Central

2014-01-01

Gallium and several of its alloys are liquid metals at or near room temperature. Gallium has low toxicity, essentially no vapor pressure, and a low viscosity. Despite these desirable properties, applications calling for liquid metal often use toxic mercury because gallium forms a thin oxide layer on its surface. The oxide interferes with electrochemical measurements, alters the physicochemical properties of the surface, and changes the fluid dynamic behavior of the metal in a way that has, until recently, been considered a nuisance. Here, we show that this solid oxide “skin” enables many new applications for liquid metals including soft electrodes and sensors, functional microcomponents for microfluidic devices, self-healing circuits, shape-reconfigurable conductors, and stretchable antennas, wires, and interconnects. PMID:25283244

Directed-Assembly of Carbon Nanotubes on Soft Substrates for Flexible Biosensor Array

NASA Astrophysics Data System (ADS)

Lee, Hyoung Woo; Koh, Juntae; Lee, Byung Yang; Kim, Tae Hyun; Lee, Joohyung; Hong, Seunghun; Yi, Mihye; Jhon, Young Min

2009-03-01

We developed a method to selectively assemble and align carbon nanotubes (CNTs) on soft substrates for flexible biosensors. In this strategy, thin oxide layer was deposited on soft substrates via low temperature plasma enhanced chemical vapor deposition, and linker-free assembly process was applied onto the oxide surface where the assembly of carbon nanotubes was guided by methyl-terminated molecular patterns on the oxide surface. The electrical characterization of the fabricated CNT devices exhibited typical p-type gating effect and 1/f noise behavior. The bare oxide regions near CNTs were functionalized with glutamate oxidase to fabricate selective biosensors to detect two forms of glutamate substances existing in different situations: L-glutamic acid, a neuro-transmitting material, and monosodium glutamate, a food additive.

Behavior of oxidized platinum nanoparticles on an aligned carbon nanotube forest

DOE Office of Scientific and Technical Information (OSTI.GOV)

Matsuda, Keita, E-mail: matsuda.keita@c.mbox.nagoya-u.ac.jp; Norimatsu, Wataru; Arai, Shigeo

2016-10-14

We observed and analyzed the behavior of platinum nanoparticles (PtNPs) supported on aligned-carbon nanotubes (CNTs) at high temperatures by X-ray photoelectron spectroscopy and high-resolution transmission electron microscope observations. We found that the PtNPs moved toward the inner-side along each CNT on which they were deposited. The mechanism of this behavior is related to the redox reaction of Pt with the carbon atoms in the CNT. We also performed in-situ observation of this process at a high temperature using an environmental transmission electron microscope under an oxygen atmosphere. We found that the PtNPs penetrated down into a high-density aligned CNT forestmore » along the tube axis and that the PtNPs changed their shape to fit the structure of the CNTs during their movement.« less

Kinetic and catalytic analysis of mesoporous Co3O4 on the oxidation of morin

NASA Astrophysics Data System (ADS)

Xaba, Morena. S.; Meijboom, Reinout

2017-11-01

Herein we report on the synthesis, characterization and catalytic evaluation of mesoporous cobalt oxides on the oxidation of morin. These mesoporous cobalt oxides were synthesized using an inverse surfactant micelle method, they are connected, well-defined with intra-particle voids. These materials were calcined to different final heating temperatures of 150, 250, 350, 450 and 550 °C, and each mesoporous cobalt oxide catalyst showed unique physical properties and catalytic behavior. Morin oxidation was used as a model reaction in the presence of hydrogen peroxide to evaluate the kinetic and catalytic activity of calcined mesoporous cobalt oxides. The adsorption-desorption equilibrium rate constants of morin and hydrogen peroxide were found to be inversely proportional to the crystallite size of the mesoporous cobalt oxide, and the characteristic path length in which the mass transfer takes place was found to be directly proportional to the crystallite size. The materials were characterized using powder X-Ray Diffraction (p-XRD), N2-sorption isotherms (BET), hydrogen temperature programmed reduction (H2-TPR) and High Resolution-Transmission Electron Microscopy (HR-TEM). UV-vis spectrophotometry was used to monitor the time-resolved absorbance of morin at λmax = 410 nm. The surface reaction in this system is described in terms of the well-established Langmuir-Hinshelwood model. The thermodynamic parameters, EA, ΔH#, ΔS# and ΔG# were calculated and catalyst recycling and reusability is demonstrated.

Plasma electrolytic oxidation of Titanium Aluminides

NASA Astrophysics Data System (ADS)

Morgenstern, R.; Sieber, M.; Grund, T.; Lampke, T.; Wielage, B.

2016-03-01

Due to their outstanding specific mechanical and high-temperature properties, titanium aluminides exhibit a high potential for lightweight components exposed to high temperatures. However, their application is limited through their low wear resistance and the increasing high-temperature oxidation starting from about 750 °C. By the use of oxide ceramic coatings, these constraints can be set aside and the possible applications of titanium aluminides can be extended. The plasma electrolytic oxidation (PEO) represents a process for the generation of oxide ceramic conversion coatings with high thickness. The current work aims at the clarification of different electrolyte components’ influences on the oxide layer evolution on alloy TNM-B1 (Ti43.5Al4Nb1Mo0.1B) and the creation of compact and wear resistant coatings. Model experiments were applied using a ramp-wise increase of the anodic potential in order to show the influence of electrolyte components on the discharge initiation and the early stage of the oxide layer growth. The production of PEO layers with technically relevant thicknesses close to 100 μm was conducted in alkaline electrolytes with varying amounts of Na2SiO3·5H2O and K4P2O7 under symmetrically pulsed current conditions. Coating properties were evaluated with regard to morphology, chemical composition, hardness and wear resistance. The addition of phosphates and silicates leads to an increasing substrate passivation and the growth of compact oxide layers with higher thicknesses. Optimal electrolyte compositions for maximum coating hardness and thickness were identified by statistical analysis. Under these conditions, a homogeneous inner layer with low porosity can be achieved. The frictional wear behavior of the compact coating layer is superior to a hard anodized layer on aluminum.

The isothermal-oxidation behavior of several nickel-base single-crystal superalloys with and without coatings

DOE Office of Scientific and Technical Information (OSTI.GOV)

Goebel, M.; Rahmel, A.; Schuetze, M.

1993-04-01

Several commercial single-crystal superalloys (CMSX-2, CMSX-3, CMSX-4, CMSX-6, SRR 99) and some laboratory versions of one of them (CMSX-4) with various Y-additions were investigated concerning their oxidation resistance in air at temperatures between 800 and 1,200[degrees]C. The investigations also included two materials (CMSX-6, SRR 99) with an RT-22 coating. Weight change was recorded for times of up to 1,000 hr (in some cases up to 1,600 hr). Oxidized coatings and substrates were characterized by metallography, SEM, and microprobe analysis. Most of the alloys showed good oxidation resistance up to 1,000[degrees]C, while there was complete spalling during cooling after oxidation atmore » 1,150[degrees]C and 1,200[degrees]C for the uncoated and Y-free alloys. Coated alloys were superior, however the best behavior was shown by a laboratory version of CMSX-4 containing between 10 and 60 ppm Y. Interdiffusion at 1,000[degrees]C is tolerable for the coated alloys, but there was extremely rapid degradation of the coating by interdiffusion at 1,200[degrees]C. 20 refs., 26 figs., 6 tabs.« less

Oxidation of Boron Nitride in Composites

NASA Technical Reports Server (NTRS)

Jacobson, Nathan S.

1998-01-01

Boron nitride (BN) is a prime candidate for fiber coatings in silicon carbide (SiC) fiber-reinforced SiC matrix composites. The properties of BN allow the fiber to impart beneficial composite properties to the matrix, even at elevated temperatures. The problem with BN is that it is readily attacked by oxygen. Although BN is an internal component of the composite, a matrix crack or pore can create a path for hot oxygen to attack the BN. This type of attack is not well understood. A variety of phenomena have been observed. These include borosilicate glass formation, volatilization of the BN, and under some conditions, preservation of the BN. In this study at the NASA Lewis Research Center, a series of BN materials and BN-containing model composites were methodically examined to understand the various issues dealing with the oxidation of BN in composites. Initial studies were done with a series of monolithic BN materials prepared by hot pressing and chemical vapor deposition (CVD). From these studies, we found that BN showed a strong orientation effect in oxidation and was extremely sensitive to the presence of water vapor in the environment. In addition, CVD material deposited at a high temperature showed much better oxidation behavior than CVD material deposited at a lower temperature.

Ultraviolet Light-Assisted Copper Oxide Nanowires Hydrogen Gas Sensor

NASA Astrophysics Data System (ADS)

Sihar, Nabihah; Tiong, Teck Yaw; Dee, Chang Fu; Ooi, Poh Choon; Hamzah, Azrul Azlan; Mohamed, Mohd Ambri; Majlis, Burhanuddin Yeop

2018-05-01

We fabricated copper oxide nanowires (CuO NWs) ultraviolet (UV) light-assisted hydrogen gas sensor. The fabricated sensor shows promising sensor response behavior towards 100 ppm of H2 at room temperature and elevated temperature at 100 °C when exposed to UV light (3.0 mW/cm2). One hundred-cycle device stability test has been performed, and it is found that for sample elevated at 100 °C, the UV-activated sample achieved stability in the first cycle as compared to the sample without UV irradiation which needed about 10 cycles to achieve stability at the initial stage, whereas the sample tested at room temperature was able to stabilize with the aid of UV irradiation. This indicates that with the aid of UV light, after some "warming up" time, it is possible for the conventional CuO NW sensor which normally work at elevated temperature to function at room temperature because UV source is speculated to play a dominant role to increase the interaction of the surface of CuO NWs and hydrogen gas molecules absorbed after the light exposure.

Application of Reactive Transport Modeling to Heap Bioleaching of Copper

NASA Astrophysics Data System (ADS)

Liu, W.

2017-12-01

Copper heap bioleaching is a complex industrial process that utilizes oxidative chemical leaching and microbial activities to extract copper from packed ore beds. Mathematical modelling is an effective tool for identifying key factors that determine the leaching performance. HeapSim is a modelling tool that incorporates all fundamental processes that occur in a heap under leach, such as the movement of leaching solution, chemical reaction kinetics, heat transfer, and microbial activities, to predict the leaching behavior of a heap. In this study, the HeapSim model was applied to simulate chalcocite heap bioleaching at Quebrada Blanca mine located in the Northern Chile. The main findings were that the model could be satisfactorily calibrated and validated to simulate chalcocite leaching. Heap temperature was sensitive to the changes in the raffinate temperature, raffinate flow rate, and the extent of pyrite oxidation. At high flow rates, heap temperature was controlled by the raffinate temperature. In contrast, heat removal by the raffinate solution flow was insignificant at low flow rates, leading to the accumulation of heat generated by pyrite reaction and therefore an increase in heap temperature.

Ultraviolet Light-Assisted Copper Oxide Nanowires Hydrogen Gas Sensor.

PubMed

Sihar, Nabihah; Tiong, Teck Yaw; Dee, Chang Fu; Ooi, Poh Choon; Hamzah, Azrul Azlan; Mohamed, Mohd Ambri; Majlis, Burhanuddin Yeop

2018-05-15

We fabricated copper oxide nanowires (CuO NWs) ultraviolet (UV) light-assisted hydrogen gas sensor. The fabricated sensor shows promising sensor response behavior towards 100 ppm of H 2 at room temperature and elevated temperature at 100 °C when exposed to UV light (3.0 mW/cm 2 ). One hundred-cycle device stability test has been performed, and it is found that for sample elevated at 100 °C, the UV-activated sample achieved stability in the first cycle as compared to the sample without UV irradiation which needed about 10 cycles to achieve stability at the initial stage, whereas the sample tested at room temperature was able to stabilize with the aid of UV irradiation. This indicates that with the aid of UV light, after some "warming up" time, it is possible for the conventional CuO NW sensor which normally work at elevated temperature to function at room temperature because UV source is speculated to play a dominant role to increase the interaction of the surface of CuO NWs and hydrogen gas molecules absorbed after the light exposure.

Friction and wear of some ferrous-base metallic glasses

NASA Technical Reports Server (NTRS)

Miyoshi, K.; Buckley, D. H.

1983-01-01

Sliding friction experiments, X-ray photoelectron spectroscopy (XPS) analysis, and electron microscopy and diffraction studies were conducted with ferrous base metallic glasses (amorphous alloys) in contact with aluminum oxide at temperatures to 750 C in a vacuum. Sliding friction experiments were also conducted in argon and air atmospheres. The results of the investigation indicate that the coefficient of friction increases with increasing temperature to 350 C in vacuum. The increase in friction is due to an increase in adhesion resulting from surface segregation of boric oxide and/or silicon oxide to the surface of the foil. Above 500 C the coefficient of friction decreased rapidly. The decrease correlates with the segregation of boron nitride to the surface. Contaminants can come from the bulk of the material to the surface upon heating and impart boric oxide and/or silicon oxide at 350 C and boron nitride above 500 C. The segregation of contaminants is responsible for the friction behavior. The amorphous alloys have superior wear resistance to crystalline 304 stainless steel. The relative concentrations of the various constituents at the surfaces of the amorphous alloys are very different from the nominal bulk compositions.

Friction and wear of some ferrous-base metallic glasses

NASA Technical Reports Server (NTRS)

Miyoshi, K.; Buckley, D. H.

1984-01-01

Sliding friction experiments, X-ray photoelectron spectroscopy (XPS) analysis, and electron microscopy and diffraction studies were conducted with ferrous base metallic glasses (amorphous alloys) in contact with aluminium oxide at temperatures to 750 C in a vacuum. Sliding friction experiments were also conducted in argon and air atmospheres. The results of the investigation indicate that the coefficient of friction increases with increasing temperature to 350 C in vacuum. The increase in friction is due to an increase in adhesion resulting from surface segregation of boric oxide and/or silicon oxide to the surface of the foil. Above 500 C the coefficient of friction decreased rapidly. The decrease correlates with the segregation of boron nitride to the surface. Contaminants can come from the bulk of the material to the surface upon heating and impart boric oxide and/or silicon oxide at 350 C and boron nitride above 500 C. The segregation of contaminants is responsible for the friction behavior. The amorphous alloys have superior wear resistance to crystalline 304 stainless steel. The relative concentrations of the various constituents at the surfaces of the amorphous alloys are very different from the nominal bulk compositions.

DSC studies to evaluate the impact of bio-oil on cold flow properties and oxidation stability of bio-diesel.

PubMed

Garcia-Perez, Manuel; Adams, Thomas T; Goodrum, John W; Das, K C; Geller, Daniel P

2010-08-01

This paper describes the use of Differential Scanning Calorimetry (DSC) to evaluate the impact of varying mix ratios of bio-oil (pyrolysis oil) and bio-diesel on the oxidation stability and on some cold flow properties of resulting blends. The bio-oils employed were produced from the semi-continuous Auger pyrolysis of pine pellets and the batch pyrolysis of pine chips. The bio-diesel studied was obtained from poultry fat. The conditions used to prepare the bio-oil/bio-diesel blends as well as some of the fuel properties of these blends are reported. The experimental results suggest that the addition of bio-oil improves the oxidation stability of the resulting blends and modifies the crystallization behavior of unsaturated compounds. Upon the addition of bio-oil an increase in the oxidation onset temperature, as determined by DSC, was observed. The increase in bio-diesel oxidation stability is likely to be due to the presence of hindered phenols abundant in bio-oils. A relatively small reduction in DSC characteristic temperatures which are associated with cold flow properties was also observed but can likely be explained by a dilution effect. (c) 2010 Elsevier Ltd. All rights reserved.

Microstructure and high temperature oxidation resistance of Ti-Ni gradient coating on TA2 titanium alloy fabricated by laser cladding

NASA Astrophysics Data System (ADS)

Liu, Fencheng; Mao, Yuqing; Lin, Xin; Zhou, Baosheng; Qian, Tao

2016-09-01

To improve the high temperature oxidation resistance of TA2 titanium alloy, a gradient Ni-Ti coating was laser cladded on the surface of the TA2 titanium alloy substrate, and the microstructure and oxidation behavior of the laser cladded coating were investigated experimentally. The gradient coating with a thickness of about 420-490 μm contains two different layers, e.g. a bright layer with coarse equiaxed grain and a dark layer with fine and columnar dendrites, and a transition layer with a thickness of about 10 μm exists between the substrate and the cladded coating. NiTi, NiTi2 and Ni3Ti intermetallic compounds are the main constructive phases of the laser cladded coating. The appearance of these phases enhances the microhardness, and the dense structure of the coating improves its oxidation resistance. The solidification procedure of the gradient coating is analyzed and different kinds of solidification processes occur due to the heat dissipation during the laser cladding process.

A study of early corrosion behaviors of FeCrAl alloys in liquid lead-bismuth eutectic environments

NASA Astrophysics Data System (ADS)

Lim, Jun; Nam, Hyo On; Hwang, Il Soon; Kim, Ji Hyun

2010-12-01

Lead and lead-bismuth eutectic (LBE) alloy have been increasingly receiving attention as heavy liquid metal coolants (HLMC) for future nuclear energy systems. The compatibility of structural materials and components with lead-bismuth eutectic liquid at high temperature is one of key issues for the commercialization of lead fast reactors. In the present study, the corrosion behaviors of iron-based alumina-forming alloys (Kanthal-AF®, PM2000, MA956) were investigated by exposing to stagnant LBE environments at 500 °C and 550 °C for up to 500 h. After exposures, the thickness and chemistry of the oxide layer on the specimens were analyzed by scanning electron microscopy, scanning transmission electron microscopy and energy dispersive X-ray spectroscopy. As a result, the oxide characteristics and the corrosion resistance were compared. In this study, it was shown that the corrosion resistance of FeCrAl ODS steels (PM2000, MA956) are superior to that of FeCrAl ferritic steel (Kanthal-AF®) in higher temperature LBE.

Sintering behavior of ultrafine silicon carbide powders obtained by vapor phase reaction

NASA Technical Reports Server (NTRS)

Okabe, Y.; Miyachi, K.; Hojo, J.; Kato, A.

1984-01-01

The sintering behavior of ultrafine SiC powder with average particle size of about 0.01-0.06 microns produced by a vapor phase reaction of the Me4Si-H2 system was studied at the temperature range of 1400-2050 deg. It was found that the homogeneous dispersion of C on SiC particles is important to remove the surface oxide layer effectively. B and C and inhibitive effect on SiC grain growth.

Universal Responses of Cyclic-Oxidation Models Studied

NASA Technical Reports Server (NTRS)

Smialek, James L.

2003-01-01

Oxidation is an important degradation process for materials operating in the high-temperature air or oxygen environments typical of jet turbine or rocket engines. Reaction of the combustion gases with the component material forms surface layer scales during these oxidative exposures. Typically, the instantaneous rate of reaction is inversely proportional to the existing scale thickness, giving rise to parabolic kinetics. However, more realistic applications entail periodic startup and shutdown. Some scale spallation may occur upon cooling, resulting in loss of the protective diffusion barrier provided by a fully intact scale. Upon reheating, the component will experience accelerated oxidation due to this spallation. Cyclic-oxidation testing has, therefore, been a mainstay of characterization and performance ranking for high-temperature materials. Models simulate this process by calculating how a scale spalls upon cooling and regrows upon heating (refs. 1 to 3). Recently released NASA software (COSP for Windows) allows researchers to specify a uniform layer or discrete segments of spallation (ref. 4). Families of model curves exhibit consistent regularity and trends with input parameters, and characteristic features have been empirically described in terms of these parameters. Although much insight has been gained from experimental and model curves, no equation has been derived that can describe this behavior explicitly as functions of the key oxidation parameters.

Cycle oxidation behavior and anti-oxidation mechanism of hot-dipped aluminum coating on TiBw/Ti6Al4V composites with network microstructure.

PubMed

Li, X T; Huang, L J; Wei, S L; An, Q; Cui, X P; Geng, L

2018-04-10

Controlled and compacted TiAl 3 coating was successfully fabricated on the network structured TiBw/Ti6Al4V composites by hot-dipping aluminum and subsequent interdiffusion treatment. The network structure of the composites was inherited to the TiAl 3 coating, which effectively reduces the thermal stress and avoids the cracks appeared in the coating. Moreover, TiB reinforcements could pin the TiAl 3 coating which can effectively improve the bonding strength between the coating and composite substrate. The cycle oxidation behavior of the network structured coating on 873 K, 973 K and 1073 K for 100 h were investigated. The results showed the coating can remarkably improve the high temperature oxidation resistance of the TiBw/Ti6Al4V composites. The network structure was also inherited to the Al 2 O 3 oxide scale, which effectively decreases the tendency of cracking even spalling about the oxide scale. Certainly, no crack was observed in the coating after long-term oxidation due to the division effect of network structured coating and pinning effect of TiB reinforcements. Interfacial reaction between the coating and the composite substrate occurred and a bilayer structure of TiAl/TiAl 2 formed next to the substrate after oxidation at 973 K and 1073 K. The anti-oxidation mechanism of the network structured coating was also discussed.

Dynamic oxidation behavior at 1000 and 1100 C of four nickel-base cast alloys, NASA-TRW VIA, B-1900, 713C, and 738X

NASA Technical Reports Server (NTRS)

Sanders, W. A.

1974-01-01

The superalloys NASA-TRW VIA, B-1900, 713C, and 738X were tested cyclically and isothermally for resistance to oxidation in high velocity gas streams for 100 hours at specimen temperatures of 1000 C and 1100 C. Alloys VIA and B-1900, which were the most oxidation resistant, displayed slight and very similar weight changes and metal losses. Alloy 713C also sustained only slight metal losses, but it exhibited some tendency to spall. Alloy 738X was found to be the most susceptible to cyclic oxidation; this resulted in heavy spalling, which in turn caused high weight losses and high metal losses. Oxidation test results are related to the amounts of chromium aluminum, and the refractory metals in the alloys investigated.

Oxidation of Uncoated and Aluminized 9-12% Cr Boiler Steels at 550-650 °C

NASA Astrophysics Data System (ADS)

Metsäjoki, J.; Huttunen-Saarivirta, E.; Lepistö, T.

2011-03-01

In this paper, oxidation behavior of 9-12% Cr steels P91 and HCM12A is studied in air and in a mixture of air and water vapor. Comparison is made between these steels in uncoated condition and coated with aluminum diffusion coating by a slurry method. Oxidation tests were carried out at 550, 600, and 650 °C for a discontinued duration of 1000 h; every 250 h the specimens were slowly cooled to room temperature and weighed. SEM + EDS and XRD characterization were performed after 500 and 1000 h. The results showed that oxidation rate of uncoated P91 and HCM12A was significantly higher in the mixture of air and water vapor than in air. Oxidation resistance of the studied materials improved substantially when they were aluminized.

Mineralization of aniline in aqueous solution by electrochemical activation of persulfate.

PubMed

Chen, Wen-Shing; Huang, Chi-Pin

2015-04-01

Oxidative degradation of aniline in aqueous solution was carried out by coupling electrolysis with persulfate oxidation, in which a synergistic effect occurred. Experiments were performed under a batch-wise mode to evaluate the influence of various operation parameters on the electrolytic behavior, such as acidity of aqueous solution, temperature, electrode potential, persulfate anion concentration and nitrogen/oxygen gas dosage. The aniline pollutants could be almost entirely mineralized by means of electro-activated persulfate oxidation, wherein sulfate radicals were presumed to be principal oxidizing agents. Besides, electrogenerated hydrogen peroxide originated from cathodic reduction of oxygen, supplied chiefly by anodic oxidation of water, would contribute partially for decomposition of aniline. On the whole, the electro-activated persulfate process is a very promising method for treatment of aniline in wastewater. Copyright © 2014 Elsevier Ltd. All rights reserved.

Melting relations in the iron-sulfur system at ultra-high pressures - Implications for the thermal state of the earth

NASA Technical Reports Server (NTRS)

Williams, Quentin; Jeanloz, Raymond

1990-01-01

The melting temperatures of FeS-troilite and of a 10-wt-pct sulfur iron alloy have been measured to pressures of 120 and 90 GPa, respectively. The results document that FeS melts at a temperature of 4100 (+ or - 300) K at the pressure of the core-mantle boundary. Eutecticlike behavior persists in the iron-sulfur system to the highest pressures of measurements, in marked contrast to the solid-solutionlike behavior observed at high pressures in the iron-iron oxide system. Iron with 10-wt-pct sulfur melts at a similar temperature as FeS at core-mantle boundary conditions. If the sole alloying elements of iron within the core are sulfur and oxygen and the outer core is entirely liquid, the minimum temperature at the top of the outer core is 4900 (+ or - 400) K. Calculations of mantle geotherms dictate that there must be a temperature increase of between 1000 and 2000 K across thermal boundary layers within the mantle. If D-double-prime is compositionally stratified, it could accommodate the bulk of this temperature jump.

Fatigue Behavior of an Advanced SiC/SiC Composite at Elevated Temperature in Air and in Steam

DTIC Science & Technology

2009-12-01

specimens tested in salt fog achieved fatigue run-out. However, a significant decrease in fatigue life was observed for fatigue stresses ≥ 100 MPa...fatigue stress level approached the proportional limit. The reduction is fatigue life was attributed to the increased matrix cracking near the...oxidation of any free silicon remaining after production using methods such as melt infiltration, and the SiC itself as temperatures near 1000 ºC. These

Electrochemical Behavior of TiO(x)C(y) as Catalyst Support for Direct Ethanol Fuel Cells at Intermediate Temperature: From Planar Systems to Powders.

PubMed

Calvillo, Laura; García, Gonzalo; Paduano, Andrea; Guillen-Villafuerte, Olmedo; Valero-Vidal, Carlos; Vittadini, Andrea; Bellini, Marco; Lavacchi, Alessandro; Agnoli, Stefano; Martucci, Alessandro; Kunze-Liebhäuser, Julia; Pastor, Elena; Granozzi, Gaetano

2016-01-13

To achieve complete oxidation of ethanol (EOR) to CO2, higher operating temperatures (often called intermediate-T, 150-200 °C) and appropriate catalysts are required. We examine here titanium oxycarbide (hereafter TiOxCy) as a possible alternative to standard carbon-based supports to enhance the stability of the catalyst/support assembly at intermediate-T. To test this material as electrocatalyst support, a systematic study of its behavior under electrochemical conditions was carried out. To have a clear description of the chemical changes of TiOxCy induced by electrochemical polarization of the material, a special setup that allows the combination of X-ray photoelectron spectroscopy and electrochemical measurements was used. Subsequently, an electrochemical study was carried out on TiOxCy powders, both at room temperature and at 150 °C. The present study has revealed that TiOxCy is a sufficiently conductive material whose surface is passivated by a TiO2 film under working conditions, which prevents the full oxidation of the TiOxCy and can thus be considered a stable electrode material for EOR working conditions. This result has also been confirmed through density functional theory (DFT) calculations on a simplified model system. Furthermore, it has been experimentally observed that ethanol molecules adsorb on the TiOxCy surface, inhibiting its oxidation. This result has been confirmed by using in situ Fourier transform infrared spectroscopy (FTIRS). The adsorption of ethanol is expected to favor the EOR in the presence of suitable catalyst nanoparticles supported on TiOxCy.

Effects of temperature on complexes I and II mediated respiration, ROS generation and oxidative stress status in isolated gill mitochondria of the mud crab Scylla serrata.

PubMed

Paital, Biswaranjan; Chainy, G B N

2014-04-01

Effects of fluctuations in habitat temperature (18-30°) on mitochondrial respiratory behavior and oxidative metabolic responses in the euryhaline ectotherm Scylla serrata are not fully understood. In the present study, effects of different temperatures ranging from 12 to 40°C on glutamate and succinate mediated mitochondrial respiration, respiratory control ratio (RCR), ATP generation rate, ratio for the utilization of phosphate molecules per atomic oxygen consumption (P/O), levels of lipid peroxidation and H2O2 in isolated gill mitochondria of S. serrata are reported. The pattern of variation in the studied parameters was similar for the two substrates at different temperatures. The values recorded for RCR (≥3) and P/O ratio (1.4-2.7) at the temperature range of 15-25°C were within the normal range reported for other animals (3-10 for RCR and 1.5-3 for P/O). Values for P/O ratio, ATP generation rate and RCR were highest at 18°C when compared to the other assay temperatures. However, at low and high extreme temperatures, i.e. at 12 and 40°C, states III and IV respiration rates were not clearly distinguishable from each other indicating that mitochondria were completely uncoupled. Positive correlations were noticed between temperature and the levels of both lipid peroxidation and H2O2. It is inferred that fluctuations on either side of ambient habitat temperature may adversely influence mitochondrial respiration and oxidative metabolism in S. serrata. The results provide baseline data to understand the impacts of acute changes in temperature on ectotherms inhabiting estuarine or marine environments. Copyright © 2014 Elsevier Ltd. All rights reserved.

DEVELOPMENT OF NIOBIUM-BASE ALLOYS. Period covered January 1, 1956 to March 1, 1957

DOE Office of Scientific and Technical Information (OSTI.GOV)

Begley, R.T. ed.

1957-11-01

The flow and fracture characteristics of commercial purity powder metallurgy niobium were investigated in the range 250 to --196 deg C. Niobium was found to undergo a ductile-brittle transition in the range --125 to --196 deg C, and the transition temperature range of niobium was found to be less affected by the presence of interstitial impurities than many other body-centered cubic metals. The creeprupture properties of powder metallurgy niobium were investigated at 982 and 1O93 deg C (1800 and 2OOO deg F), and the 100-hour rupture strength of commercial niobium in vacuum was determined to be sigdicantiy greater than unalloyedmore » molybdenum. The creep-rupture results suggest that small quantities of gaseous contaminants may be responslble for the high strength of commercial niobium at elevated temperatures. The oxidation behavior of nioblum was investigated in the temperature range 350 to 7OO C. At the higher temperatures, oxidation followed a linear rate law. Between 500 and 625 deg C, the rate of oxidation was found to be nearly independent of temperature. Oxygen and nitrogen contamination of welding atmospheres was studied to determine its effect on the weld properties of niobium. Nitrogen was establlshed to be very detrimental to the mechanical properties of niobium welds. High-purity niobium, having a hardness of less than 60 VPN, was produced by cage-zone refinieg techniques. (auth)« less

Oxidation Behavior of Carbon Fiber-Reinforced Composites

NASA Technical Reports Server (NTRS)

Sullivan, Roy M.

2008-01-01

OXIMAP is a numerical (FEA-based) solution tool capable of calculating the carbon fiber and fiber coating oxidation patterns within any arbitrarily shaped carbon silicon carbide composite structure as a function of time, temperature, and the environmental oxygen partial pressure. The mathematical formulation is derived from the mechanics of the flow of ideal gases through a chemically reacting, porous solid. The result of the formulation is a set of two coupled, non-linear differential equations written in terms of the oxidant and oxide partial pressures. The differential equations are solved simultaneously to obtain the partial vapor pressures of the oxidant and oxides as a function of the spatial location and time. The local rate of carbon oxidation is determined at each time step using the map of the local oxidant partial vapor pressure along with the Arrhenius rate equation. The non-linear differential equations are cast into matrix equations by applying the Bubnov-Galerkin weighted residual finite element method, allowing for the solution of the differential equations numerically.

Effects of oxygen content on the oxidation process of Si-containing steel during anisothermal heating

NASA Astrophysics Data System (ADS)

Yuan, Qing; Xu, Guang; Liang, Wei-cheng; He, Bei; Zhou, Ming-xing

2018-02-01

The oxidizing behavior of Si-containing steel was investigated in an O2 and N2 binary-component gas with oxygen contents ranging between 0.5vol% and 4.0vol% under anisothermal-oxidation conditions. A simultaneous thermal analyzer was employed to simulate the heating process of Si-containing steel in industrial reheating furnaces. The oxidation gas mixtures were introduced from the commencement of heating. The results show that the oxidizing rate remains constant in the isothermal holding process at high temperatures; therefore, the mass change versus time presents a linear law. A linear relation also exists between the oxidizing rate and the oxygen content. Using the linear regression equation, the oxidation rate at different oxygen contents can be predicted. In addition, the relationship between the total mass gain and the oxygen content is linear; thus, the total mass gain at oxygen contents between 0.5vol%-4.0vol% can be determined. These results enrich the theoretical studies of the oxidation process in Si-containing steels.

Formation of titanium diboride coatings during the anodic polarization of titanium in a chloride melt with a low boron oxide content

NASA Astrophysics Data System (ADS)

Elshina, L. A.; Malkov, V. B.; Molchanova, N. G.

2015-02-01

The corrosion-electrochemical behavior of titanium in a molten eutectic mixture of cesium and sodium chlorides containing up to 1 wt % boron oxide is studied in the temperature range 810-870 K in an argon atmosphere. The potential, the current, and the rate of titanium corrosion are determined. The optimum conditions of forming a dense continuous titanium diboride coating on titanium with high adhesion to the metallic base are found for the anodic activation of titanium in the molten electrolyte under study.

Magnetoelectric behavior of carbonyl iron mixed Mn oxide-coated ferrite nanoparticles

NASA Astrophysics Data System (ADS)

Ahad, Faris B. Abdul; Lee, Shang-Fan; Hung, Dung-Shing; Yao, Yeong-Der; Yang, Ruey-Bin; Lin, Chung-Kwei; Tsay, Chien-Yie

2010-05-01

The dielectric and magnetic properties of manganese oxide-coated Fe3O4 nanoparticles (NPs) were measured by the cavity perturbation method at x-band microwave frequencies ranging from 7-12.5 GHz with controlled external magnetic field up to 2.2 kOe at room temperature. Different ratios (5%, 10%, and 20% by weight) of coated NPs were prepared by sol-gel method then mixed with carbonyl iron powder in epoxy matrix. The saturation magnetization is inversely proportional to the NPs ratio in the mixture between 150 and 180 emu/g. The real part of the permittivity decreased with increasing NPs concentration, but the permittivity change by magnetic field increased. The tunability behavior is explained by insulator-ferromagnetic interface magnetoelectricity and the large surface volume ratio for the NPs.

Atomic layer deposition of Al{sub 2}O{sub 3} for single electron transistors utilizing Pt oxidation and reduction

DOE Office of Scientific and Technical Information (OSTI.GOV)

McConnell, Michael S., E-mail: mmcconn5@nd.edu; Schneider, Louisa C.; Karbasian, Golnaz

This work describes the fabrication of single electron transistors using electron beam lithography and atomic layer deposition to form nanoscale tunnel transparent junctions of alumina (Al{sub 2}O{sub 3}) on platinum nanowires using either water or ozone as the oxygen precursor and trimethylaluminum as the aluminum precursor. Using room temperature, low frequency conductance measurements between the source and drain, it was found that devices fabricated using water had higher conductance than devices fabricated with ozone. Subsequent annealing caused both water- and ozone-based devices to increase in conductance by more than 2 orders of magnitude. Furthermore, comparison of devices at low temperaturesmore » (∼4 K) showed that annealed devices displayed much closer to the ideal behavior (i.e., constant differential conductance) outside of the Coulomb blockade region and that untreated devices showed nonlinear behavior outside of the Coulomb blockade region (i.e., an increase in differential conductance with source-drain voltage bias). Transmission electron microscopy cross-sectional images showed that annealing did not significantly change device geometry, but energy dispersive x-ray spectroscopy showed an unusually large amount of oxygen in the bottom platinum layer. This suggests that the atomic layer deposition process results in the formation of a thin platinum surface oxide, which either decomposes or is reduced during the anneal step, resulting in a tunnel barrier without the in-series native oxide contribution. Furthermore, the difference between ozone- and water-based devices suggests that ozone promotes atomic layer deposition nucleation by oxidizing the surface but that water relies on physisorption of the precursors. To test this theory, devices were exposed to forming gas at room temperature, which also reduces platinum oxide, and a decrease in resistance was observed, as expected.« less

Calorimetric determination of energetics of solid solutions of UO 2+ x with CaO and Y 2O 3

NASA Astrophysics Data System (ADS)

Mazeina, Lena; Navrotsky, Alexandra; Greenblatt, Martha

2008-02-01

Quantitative study of thermodynamic properties of solid solutions of UO 2+ x with divalent and trivalent oxides is important for predicting the behavior of oxide fuel. Although early literature work measured vapor pressure in some of these solid solutions, direct calorimetric measurements of enthalpies of formation have been hampered by the refractory nature of such oxides. First measurements of the enthalpies of formation in the systems UO 2+ x-CaO and UO 2+ x-YO 1.5, obtained by high-temperature oxide melt solution calorimetry, are reported. Both systems show significantly negative (exothermic) heats of formation from binary oxides (UO 2, plus O 2 and CaO or YO 1.5, as well as from UO 2 plus UO 3 and CaO or YO 1.5), consistent with reported free energy measurements in the urania-yttria system. The energetic contributions of oxygen content (oxidation of U 4+) and of charge balanced ionic substitution as well as defect clustering are discussed. Behavior of urania-yttria is compared to that of corresponding systems in which the tetravalent ion is Ce, Zr, or Hf. The substantial additional stability in the solid solutions compared to pure UO 2+ x may retard, in both thermodynamic and kinetic sense, the oxidation and leaching of spent fuel to form aqueous U 6+ and solid uranyl phases.

The chemical and catalytic properties of nanocrystalline metal oxides prepared through modified sol-gel synthesis

NASA Astrophysics Data System (ADS)

Carnes, Corrie Leigh

The goal of this research was to synthesize, characterize and study the chemical properties of nanocrystalline metal oxides. Nanocrystalline (NC) ZnO, CuO, NiO, Al2O3, and the binary Al2O 3/MgO and ZnO/CuO were prepared through modified sol gel methods. These NC metal oxides were studied in comparison to the commercial (CM) metal oxides. The samples were characterized by XRD, TGA, FTIR, BET, and TEM. The NC samples were all accompanied by a significant increase in surface area and decrease in crystallite size. Several chemical reactions were studied to compare the NC samples to the CM samples. One of the reactions involved a high temperature reaction between carbon tetrachloride and the oxide to form carbon dioxide and the corresponding metal chloride. A similar high temperature reaction was conducted between the metal oxide and hydrogen sulfide to form water and the corresponding metal sulfide. A room temperature gas phase adsorption was studied where SO2 was adsorbed onto the oxide. A liquid phase adsorption conducted at room temperature was the destructive adsorption of paraoxon (a toxic insecticide). In all reactions the NC samples exhibited greater activity, destroying or adsorbing a larger amount of the toxins compared to the CM samples. To better study surface area effects catalytic reactions were also studied. The catalysis of methanol was studied over the nanocrystalline ZnO, CuO, NiO, and ZnO/CuO samples in comparison to their commercial counterparts. In most cases the NC samples proved to be more active catalysts, having higher percent conversions and turnover numbers. A second catalytic reaction was also studied, this reaction was investigated to look at the support effects. The catalysis of cyclopropane to propane was studied over Pt and Co catalysts. These catalysts were supported onto NC and CM alumina by impregnation. By observing differences in the catalytic behavior, support effects have become apparent.

Four-probe electrical-transport measurements on single indium tin oxide nanowires between 1.5 and 300 K

NASA Astrophysics Data System (ADS)

Chiu, Shao-Pin; Chung, Hui-Fang; Lin, Yong-Han; Kai, Ji-Jung; Chen, Fu-Rong; Lin, Juhn-Jong

2009-03-01

Single-crystalline indium tin oxide (ITO) nanowires (NWs) were grown by the standard thermal evaporation method. The as-grown NWs were typically 100-300 nm in diameter and a few µm long. Four-probe submicron Ti/Au electrodes on individual NWs were fabricated by the electron-beam lithography technique. The resistivities of several single NWs have been measured from 300 down to 1.5 K. The results indicate that the as-grown ITO NWs are metallic, but disordered. The overall temperature behavior of resistivity can be described by the Bloch-Grüneisen law plus a low-temperature correction due to the scattering of electrons off dynamic point defects. This observation suggests the existence of numerous dynamic point defects in as-grown ITO NWs.

Two-dimensional electron gas in tricolor oxide interfaces

NASA Astrophysics Data System (ADS)

Cao, Yanwei; Kareev, Michael; Liu, Xiaoran; Middey, Srimanta; Meyers, Derek; Tchakhalian, Jak

2014-03-01

Understanding and manipulating spin of electrons in nanometer scale is the main challenge of current spintronics, recent emergent two-dimensional electron gas in oxide interface provides a good platform to investigate the spin behavior by covering an insulating magnetic oxide layer. In this work, take titanates as an example, ultra-thin tricolor (tri-compound) titanate superlattices ([LaTiO3/SrTiO3/YTiO3]) were grown in a layer-by-layer way by pulsed laser deposition. High sample quality and their electronic structures were characterized by the combination of in-situ photoelectron and ex-situ structure and surface morphology probes. Temperature-dependent sheet resistance indicates the presence of metallic interfaces in both [LaTiO3 /SrTiO3 ] and all the tricolor structures, whereas a [YTiO3 /SrTiO3] bi-layer shows insulating behavior. The tricolor titanate superlattices provide an opportunity to induce tunable spin-polarization into the two-dimensional electron gas (2DEG) with Mott carriers.

Crystallization, flow and thermal histories of lunar and terrestrial compositions

NASA Technical Reports Server (NTRS)

Uhlmann, D. R.

1979-01-01

Contents: a kinetic treatment of glass formation; effects of nucleating heterogeneities on glass formation; glass formation under continuous cooling conditions; crystallization statistics; kinetics of crystal nucleation; diffusion controlled crystal growth; crystallization of lunar compositions; crystallization between solidus and liquidus; crystallization on reheating a glass; temperature distributions during crystallization; crystallization of anorthite and anorthite-albite compositions; effect of oxidation state on viscosity; diffusive creep and viscous flow; high temperature flow behavior of glass-forming liquids, a free volume interpretation; viscous flow behavior of lunar compositions; thermal history of orange soil material; breccias formation by viscous sintering; viscous sintering; thermal histories of breccias; solute partitioning and thermal history of lunar rocks; heat flow in impact melts; and thermal histories of olivines.

Influence of Oxidation Treatments and Surface Finishing on the Electrochemical Behavior of Ni-20Cr HVOF Coatings

NASA Astrophysics Data System (ADS)

Ruiz-Luna, H.; Porcayo-Calderon, J.; Alvarado-Orozco, J. M.; Mora-García, A. G.; Martinez-Gomez, L.; Trápaga-Martínez, L. G.; Muñoz-Saldaña, J.

2017-12-01

The low-temperature electrochemical behavior of HVOF Ni-20Cr coatings was assessed. The coatings were evaluated in different conditions including as-sprayed, as-ground, and heat-treated in air and argon atmospheres. A detailed analysis of the coatings was carried out by means of XRD, SEM, and EPMA, prior and after the corrosion test. The corrosion rate was analyzed in a NaCl solution saturated with CO2. Results demonstrate that the use of a low-oxygen partial pressure favors the formation of a Cr2O3 layer on the surface of the coatings. According to the electrochemical results, the lower corrosion rates were obtained for the heat-treated coatings irrespective of the surface finishing, being the ground and argon heat-treated condition that shows the best corrosion performance. This behavior is due to the synergistic effect of the low-pressure heat treatment and the grinding processes. The grinding promotes a more homogeneous reaction area without surface heterogeneities such as voids, and the pre-oxidation treatment decreases the porosity content of the coating and also allows the growing of a Cr-rich oxide scale which acts as a barrier against the ions of the aqueous solution.

Investigation of the Origin of Catalytic Activity in Oxide-Supported Nanoparticle Gold

DOE Office of Scientific and Technical Information (OSTI.GOV)

Harrison, Ian

Since Haruta’s discovery in 1987 of the surprising catalytic activity of supported Au nanoparticles, we have seen a very large number of experimental and theoretical efforts to explain this activity and to fully understand the nature of the behavior of the responsible active sites. In 2011, we discovered that a dual catalytic site at the perimeter of ~3nm diameter Au particles supported on TiO 2 is responsible for oxidative catalytic activity. O 2 molecules bind with Au atoms and Ti4+ ions in the TiO 2 support and the weakened O-O bond dissociates at low temperatures, proceeding to produce O atomsmore » which act as oxidizing agents for the test molecule, CO. The papers supported by DOE have built on this finding and have been concerned with two aspects of the behavior of Au/TiO 2 catalysts: (1). Mechanistic behavior of dual catalytic sites in the oxidation of organic molecules such as ethylene and acetic acid; (2). Studies of the electronic properties of the TiO 2 (110) single crystal in relation to its participation in charge transfer at the occupied dual catalytic site. A total of 20 papers have been produced through DOE support of this work. The papers combine IR spectroscopic investigations of Au/TiO 2 catalysts with surface science on the TiO 2(110) and TiO 2 nanoparticle surfaces with modern density functional modeling. The primary goals of the work were to investigate the behavior of the dual Au/Ti 4+ site for the partial oxidation of alcohols to acids, the hydrogenation of aldehydes and ketones to alcohols, and the condensation of oxygenate intermediates- all processes related to the utilization of biomass in the production of useful chemical energy sources.« less

In situ characterization of catalytic activity of graphene stabilized small-sized Pd nanoparticles for CO oxidation

NASA Astrophysics Data System (ADS)

Mao, Bao-Hua; Liu, Chang-Hai; Gao, Xu; Chang, Rui; Liu, Zhi; Wang, Sui-Dong

2013-10-01

The room-temperature ionic liquid assisted sputtering method is utilized to achieve the Pd-nanoparticle (NP)-graphene hybrid. The supported Pd NPs possess uniformly small sizes of 1-2 nm, which create huge surface area with ultralow Pd consumption and high NP stability. The Pd-NP-graphene hybrid is in situ characterized by the ambient pressure X-ray photoelectron spectroscopy using synchrotron radiation, and the results demonstrate high catalytic activity of the hybrid for CO oxidation. The catalytic behavior is reproducible for several catalytic cycles. The present simple and clean approach is promising to produce metal-NP-based high-efficiency catalysts for CO oxidation.

Effects of hydrogen annealing, sulfur segregation and diffusion on the cyclic oxidation resistance of superalloys: A review

NASA Astrophysics Data System (ADS)

Smialek, J. L.; Jayne, D. T.; Schaeffer, J. C.; Murphy, W. H.

1994-12-01

This review is based on the phenomenon of improved oxide scale adhesion for desulfurized superalloys. The proposed adhesion mechanism involves sulfur interfacial segregation and scale-metal bond weakening. Sulfur surface segregation on superalloys is examined as a function of temperature and sulfur content, and is related to the classical behavior predicted by the McLean isotherm. Effective desulfurization to less than 1 ppmw can be accomplished by hydrogen annealing and is described by sulfur diffusion kinetics in nickel. Hydrogen annealing results in excellent cyclic oxidation resistance for a number of advanced superalloys. The concept of a critical sulfur content is discussed in terms of practical annealing conditions and section thicknesses.

Examination of oxide scales in the SEM using backscattered electron images

NASA Technical Reports Server (NTRS)

Price, C. W.; Wright, I. G.; Wallwork, G. R.

1973-01-01

The complementary use of the scanning electron microscope in the backscattered electron mode with the more usual secondary electron mode results in a significant increase in the versatility of the instrument, since regions of different chemical composition can be readily detected, and their morphology examined. The use of this technique to examine complex oxide scales formed on heat-resistant alloys is described, and in particular the location of thoria particles in the scale formed on a Ni-20 wt pct Cr-2.3 wt pct ThO2 alloy, and the examination of the behavior of yttrium during the high-temperature oxidation of a Co-Cr-Al-Y alloy are discussed.

Effects of hydrogen annealing, sulfur segregation and diffusion on the cyclic oxidation resistance of superalloys: A review

NASA Technical Reports Server (NTRS)

Smialek, J. L.; Jayne, D. T.; Schaeffer, J. C.; Murphy, W. H.

1994-01-01

This review is based on the phenomenon of improved oxide scale adhesion for desulfurized superalloys. The proposed adhesion mechanism involves sulfur interfacial segregation and scale-metal bond weakening. Sulfur surface segregation on superalloys is examined as a function of temperature and sulfur content, and is related to the classical behavior predicted by the McLean isotherm. Effective desulfurization to less than 1 ppmw can be accomplished by hydrogen annealing and is described by sulfur diffusion kinetics in nickel. Hydrogen annealing results in excellent cyclic oxidation resistance for a number of advanced superalloys. The concept of a critical sulfur content is discussed in terms of practical annealing conditions and section thicknesses.

Effects of Hydrogen Annealing, Sulfur Segregation and Diffusion on the Cyclic Oxidation Resistance of Superalloys: a Review

NASA Technical Reports Server (NTRS)

Smialek, J. L.; Jayne, D. T.; Schaeffer, J. C.; Murphy, W. H.

1994-01-01

This review is based on the phenomenon of improved oxide scale adhesion for desulfurized superalloys. The proposed adhesion mechanism involves sulfur interfacial segregation and scale-metal bond weakening. Sulfur surface segregation on superalloys is examined as a function of temperature and sulfur content and related to classical behavior predicted by the McLean isotherm. Effective desulfurization to less than 1 ppmw can be accomplished by hydrogen annealing and is governed by sulfur diffusion kinetics in nickel. Hydrogen annealing results in excellent cyclic oxidation resistance for a number of advanced superalloys. The concept of a critical sulfur content is discussed in terms of practical annealing conditions and section thicknesses.

Enhancement of thermoelectric power factor of Sr2CoMoO6 double perovskite by annealing in reducing atmosphere

NASA Astrophysics Data System (ADS)

Tanwar, Khagesh; Saxena, Mandvi; Maiti, Tanmoy

2017-10-01

In general, n-type thermoelectric materials are rather difficult to design. This study particularly pivoted on designing potential environmentally benign oxides based n-type thermoelectric material. We synthesized Sr2CoMoO6 (SCMO) polycrystalline ceramics via the solid-state synthesis route. XRD, SEM, and thermoelectric measurements were carried out for phase constitution, microstructure analysis, and to determine its potential for thermoelectric applications. As-sintered SCMO sample showed an insulator like behavior till 640 °C after which it exhibited an n-type non-degenerate semiconductor behavior followed by a p-n type conduction switching. To stabilize a high temperature n-type behavior, annealing of SCMO in reducing atmosphere (H2) at 1000 °C was carried out. After annealing, the SCMO demonstrated an n-type semiconductor behavior throughout the temperature range of measurement. The electrical conductivity (σ) and the power factor (S2σ) were found to be increased manifold in the annealed SCMO double perovskite.

Investigating NO2 gas sensing behavior of flower-like MoS2 and rGO based nano-composite

NASA Astrophysics Data System (ADS)

Kanaujiya, Neha; Anupam, Golimar, Kapil; Pandey, Prateek Chandra; Jyoti, Varma, G. D.

2018-05-01

In the present work, MoS2 nano-sheets with flower-like morphology have been synthesized by facile hydrothermal method. The nano-composite of MoS2 and reduced graphene oxide (rGO) nano-sheets has been synthesized to study the gas sensing behavior. The structural and morphological characteristics of the as prepared samples are investigated by X-ray diffraction (XRD) and Field emission scanning electron microscopy (FESEM) respectively. The gas sensing behavior of the as synthesized MoS2 and composite samples have been studied for different concentrations of NO2 at different temperatures. Improvement in sensing response of composite sample as compared to bare MoS2 sample has been observed. Percentage response of ˜ 23% has been observed at room temperature for 40ppm NO2. The detail correlation between gas sensing behavior and structural characteristics of the composite sample will be described and discussed in this paper.

Directed assembly of carbon nanotubes on soft substrates for use as a flexible biosensor array.

PubMed

Koh, Juntae; Yi, Mihye; Yang Lee, Byung; Kim, Tae Hyun; Lee, Joohyung; Jhon, Young Min; Hong, Seunghun

2008-12-17

We have developed a method to selectively assemble and align carbon nanotubes (CNTs) on soft substrates for use as flexible biosensors. In this strategy, a thin oxide layer was deposited on soft substrates via low temperature plasma enhanced chemical vapor deposition, and a linker-free assembly process was applied on the oxide surface where the assembly of carbon nanotubes was guided by methyl-terminated molecular patterns on the oxide surface. The electrical characterization of the fabricated CNT devices exhibited a typical p-type gating effect and 1/f noise behavior. The bare oxide regions near CNTs were functionalized with glutamate oxidase to fabricate selective biosensors to detect two forms of glutamate substances existing in different situations: L-glutamic acid, a neurotransmitting material, and monosodium glutamate, a food additive.

Impedance spectroscopy studies in cobalt ferrite-reduced graphene oxide nanocomposite

DOE Office of Scientific and Technical Information (OSTI.GOV)

Supriya, Sweety, E-mail: sweety@iitp.ac.in; Kumar, Sunil, E-mail: sunil.pph13@iitp.ac.in; Kar, Manoranjan, E-mail: mano@iitp.ac.in

2016-05-06

(1-x)Cobalt ferrite-(x)reduced graphene oxidenanocomposites with x=0, 0.1, 0.2 and 0.3 were prepared by the ultrasonic method. The crystal symmetry modification due to reduced graphene oxide and cobalt ferrite interaction has been studied by employing the X-ray diffraction technique. Morphology of the samples was studied by the Field emission scanning electron microscopy (FE-SEM). Study on electrical properties of the cobalt ferrite-reduced graphene oxide nanocomposites explores the possible application of these composites as anode material. Impedance decreases with an increase in frequency as well as temperature, which supports an increase in ac electrical conductivity. The modified Debye relaxation model can explain themore » behavior of impedance in cobalt ferrite-reduced graphene oxide nanocomposites.« less

Measurement of uptake and release of tritium by tungsten

DOE Office of Scientific and Technical Information (OSTI.GOV)

Nakayama, M.; Torikai, Y.; Saito, M.

2015-03-15

Tungsten is currently contemplated as plasma facing material for the divertor of future fusion machines. In this paper the uptake of tritium by tungsten and its release behavior have been investigated. Tungsten samples have been annealed at various temperatures and loaded at also different temperatures with deuterium containing 7.2 % tritium at a pressure of 1.2 kPa. A specific system was designed to assess the release of tritiated water and molecular tritium by the samples. Due to the rather low solubility of hydrogen isotopes in tungsten it is particularly important to be aware of the presence of hydrogen traps ormore » thin oxide films. As shown in this work, traps or oxide films may affect the retention capability of tungsten and lead to significantly modified release properties. It became clear that there were capture sites that had different thermal stability and different capture intensity in tungsten after polishing, or oxide films that were grown on the surface of tungsten and had barrier effects.« less

Wet chemical synthesis of zinc-iron oxide nanocomposite

NASA Astrophysics Data System (ADS)

Ito, Honami; Amagasa, Shota; Nishida, Naoki; Kobayashi, Yoshio; Yamada, Yasuhiro

2017-11-01

Zinc-iron oxide nanoparticles (ZnxFe3-xO4 and δ-ZnxFe1-xOOH) were successfully synthesized by room temperature chemical reaction of a solution containing ZnCl2 and FeCl2 in the presence of gelatin. The composition of products could be controlled by variation of the Zn/Fe mixture ratio of the starting material. ZnxFe3-xO4 nanoparticles were obtained from a solution with a high Zn/Fe ratio, whereas Zn-doped feroxyhyte ( δ-ZnxFe1-xOOH) nanoparticles were obtained from a solution with a low Zn/Fe ratio. The ZnxFe3-xO4 nanoparticles were spherical with diameters of approximately 10 nm, and the δ-ZnxFe1-xOOH particles were needle-like with lengths of approximately 100 nm. Mössbauer spectra measured at room temperature indicated superparamagnetic behavior of the nanoparticles, whereas the magnetic components were observed at low temperature. The Zn content of the intermediate species (( {Zn}^{ {II}}x {Fe}^{ {II}}_{1-x} {Fe}^{ {III}}2O4)) plays an important role in the oxidation process. When the Zn concentration was high, the content of Fe2+ in the intermediate species was small, and Zn2+ prevented further oxidation of the nanoparticles. When the starting material had low Zn concentration, the amount of Fe2+ in the intermediate species became large and was rapidly oxidized into δ-ZnxFe1-xOOH while rinsing under the ambient atmosphere.

Room temperature ferroelectricity in one-dimensional single chain molecular magnets [{M(Δ)M(Λ)}(ox)2(phen)2]n (M = Fe and Mn)

NASA Astrophysics Data System (ADS)

Bhatt, Pramod; Mukadam, M. D.; Meena, S. S.; Mishra, S. K.; Mittal, R.; Sastry, P. U.; Mandal, B. P.; Yusuf, S. M.

2017-03-01

The ferroelectric materials are mainly focused on pure inorganic oxides; however, the organic molecule based materials have recently attracted great attention because of their multifunctional properties. The mixing of oxalate and phenanthroline ligands with metal ions (Fe or Mn) at room temperature followed by hydrothermal treatment results in the formation of one-dimensional single chain molecular magnets which exhibit room temperature dielectric and ferroelectric behavior. The compounds are chiral in nature, and exhibit a ferroelectric behavior, attributed to the polar point group C2, in which they crystallized. The compounds are also associated with a dielectric loss and thus a relaxation process. The observed electric dipole moment, essential for a ferroelectricity, has been understood quantitatively in terms of lattice distortions at two different lattice sites within the crystal structure. The studied single chain molecular magnetic materials with room temperature ferroelectric and dielectric properties could be of great technological importance in non-volatile memory elements, and high-performance insulators.

Influence of strain rate and temperature on the mechanical behavior of iron aluminide-based alloys

DOE Office of Scientific and Technical Information (OSTI.GOV)

Gray, G.T.

Iron aluminides are receiving increasing attention as potential high temperature structural materials due to their excellent oxidation and sulfidation resistance. Although the influence of strain rate on the microstructure/property relationships of pure iron and a variety of iron alloys and steels has been extensively studied, the effect of strain rate on the stress-strain and deformation response of iron aluminides remains poorly understood. In this paper the influence of strain rate, varied between 0.001 and 10{sup 4} s{sup {minus}1}, and temperature, between 77 & 1073{degree}K, on the mechanical behavior of Fe-40Al-0.1B and Fe-16.12Al-5.44Cr-0.11Zr-0.13C-1.07Mo-006Y, called FAP-Y, (both in at.%) is presented. Themore » rate sensitivity and work hardening of Fe-40Al and the disordered alloy based on Fe-16% Al are discussed as a function of strain rate and temperature.« less

Tribological Behavior of IN718 Superalloy Coating Fabricated by Laser Additive Manufacturing

NASA Astrophysics Data System (ADS)

Zhang, Yaocheng; Pan, Qiyong; Yang, Li; Li, Ruifeng; Dai, Jun

2017-12-01

The tribological behavior of laser manufactured IN718 superalloy coating are investigated with different applied loads, sliding speeds and lubricating mediums. The wear resistance of laser manufactured IN718 coating is increased by heat treatment due to higher microhardness and homogeneous brittle phase distribution. The principal factors for the wear rate are applied load and lubricating medium. The worn surface of laser manufactured IN718 coating consists of the grooves, crack, wear debris and material delamination generated by the fatigue wear associated with adhesive wear and abrasive wear. The friction coefficients are influenced by the tribological noise decrescence by the tribo-oxidant and the liquid lubricant. The real contact temperature between coating sample and frictional counterpart is higher than the solid-solution temperature of IN718 superalloy, and the effect of surface contact temperature on the orientational microstructure and wear resistance for dry friction and wet friction process is indistinct.

Silicon nitride-aluminum oxide solid solution (SiAION) formation and densification by pressure sintering

NASA Technical Reports Server (NTRS)

Yeh, H. C.; Sanders, W. A.; Fiyalko, J. L.

1975-01-01

Stirred-ball-mill-blended Si3N4 and Al2O3 powders were pressure sintered in order to investigate the mechanism of solid solution formation and densification in the Si3N4-Al2O3 system. Powder blends with Si3N4:Al2O3 mole ratios of 4:1, 3:2, and 2:3 were pressure sintered at 27.6-MN/sq m pressure at temperatures to 17000 C (3090 F). The compaction behavior of the powder blends during pressure sintering was determined by observing the density of the powder compact as a function of temperature and time starting from room temperature. This information, combined with the results of X-ray diffraction and metallographic analyses regarding solutioning and phase transformation phenomena in the Si3N4-Al2O3 system, was used to describe the densification behavior.

High-temperature ultrasonic characterization of the mechanical and microstructural behavior of a fibrous composite with a magnesium lithium aluminum silicate glass-ceramic matrix

DOE Office of Scientific and Technical Information (OSTI.GOV)

Cutard, T.; Huger, M.; Fargeot, D.

The mechanical behavior and the microstructural modifications of a SiC-fiber-reinforced magnesium lithium aluminum silicate glass-ceramic (SiC/MASL) have been characterized by ultrasonic measurement of uniaxial Young`s modulus at high temperature. Under vacuum, long isothermal agings in the 750--1,000 C temperature range have shown matrix modifications in terms of crystallization of residual glassy phases, and of phase transformations in the Li{sub 2}O-Al{sub 2}O{sub 3}-SiO{sub 2} system. In air, long isothermal agings performed under the same conditions have led to the same matrix transformations but in competition with oxidation mechanisms of the carbon fiber-matrix interphase. All of these matrix and/or interface transformations havemore » been confirmed by X-ray diffraction analysis, scanning electron microscopy, scanning acoustic microscopy, and microindentation tests.« less

Development of aircraft brake materials. [evaluation of metal and ceramic materials in sliding tests simulation of aircraft braking

NASA Technical Reports Server (NTRS)

Ho, T. L.; Peterson, M. B.

1974-01-01

The requirements of brake materials were outlined and a survey made to select materials to meet the needs of high temperature brakes. A number of metals and ceramic materials were selected and evaluated in sliding tests which simulated aircraft braking. Nickel, molybdenum tungsten, Zr02, high temperature cements and carbons were tested. Additives were then incorporated into these materials to optimize their wear or strength behavior with particular emphasis on nickel and molybdenum base materials and a high temperature potassium silicate cement. Optimum materials were developed which improved wear behavior over conventional brake materials in the simulated test. The best materials are a nickel, aluminum oxide, lead tungstate composition containing graphite or molybdenum disulphite; a molybdenum base material containing LPA100 (an intermetallic compound of cobalt, molybdenum, and silicon); and a carbon material (P5).

Transverse susceptibility as a probe of the magnetocrystalline anisotropy-driven phase transition in Pr0.5Sr0.5CoO3

NASA Astrophysics Data System (ADS)

Frey Huls, N. A.; Bingham, N. S.; Phan, M. H.; Srikanth, H.; Stauffer, D. D.; Leighton, C.

2011-01-01

Half-doped Pr1-xSrxCoO3 (x=0.5) displays anomalous magnetism, most notably manifest in the field-cooled magnetization versus temperature curves under different applied cooling fields. Recently, an explanation was advanced that a magnetocrystalline anisotropy transition driven by a structural transition at 120 K is the origin of this behavior. In this paper, we further elucidate the nature of the magnetic anisotropy across the low-temperature phase transition in this material by means of transverse susceptibility (TS) measurements performed using a self-resonant tunnel diode oscillator. TS probes magnetic materials by means of a small radio frequency oriented transverse to a dc field that sweeps from positive to negative saturation. TS scans as a function of field clearly reveal peaks associated with the anisotropy (HK) and switching fields (HS). When peak position is examined as a function of temperature, ˜120 K the signature of a ferromagnetic-to-ferromagnetic phase transition is evident as a sharp feature in HK and a corresponding cusp in HS. A third TS peak (not previously observed in other classes of magnetic oxides such as manganites and spinel ferrites) is found to be correlated with the crossover field (Hcr) in the unconventional magnetization versus temperature [M(T)] behavior. We observe a strong temperature dependence of Hcr at ˜120 K using this technique, which suggests the magnetic-field-influenced magnetocrystalline anisotropy transition. We show the switching between the high-field magnetization state and the low-field magnetization state associated with the magnetocrystalline anisotropy transition is irreversible when the magnetic field is recycled. Finally, we demonstrate that the TS peak magnitude indicates easy axis switching associated with this phase transition, even in these polycrystalline samples. Our results further confirm that TS provides new insights into the magnetic behavior of complex oxides.

Real-time plasmon spectroscopy study of the solid-state oxidation and Kirkendall void formation in copper nanoparticles.

PubMed

Susman, Mariano D; Feldman, Yishai; Bendikov, Tatyana A; Vaskevich, Alexander; Rubinstein, Israel

2017-08-31

Oxidation and corrosion reactions have a major effect on the application of non-noble metals. Kinetic information and simple theoretical models are often insufficient for describing such processes in metals at the nanoscale, particularly in cases involving formation of internal voids (nano Kirkendall effect, NKE) during oxidation. Here we study the kinetics of solid-state oxidation of chemically-grown copper nanoparticles (NPs) by in situ localized surface plasmon resonance (LSPR) spectroscopy during isothermal annealing in the range 110-170 °C. We show that LSPR spectroscopy is highly effective in kinetic studies of such systems, enabling convenient in situ real-time measurements during oxidation. Change of the LSPR spectra throughout the oxidation follows a common pattern, observed for different temperatures, NP sizes and substrates. The well-defined initial Cu NP surface plasmon (SP) band red-shifts continuously with oxidation, while the extinction intensity initially increases to reach a maximum value at a characteristic oxidation time τ, after which the SP intensity continuously drops. The characteristic time τ is used as a scaling parameter for the kinetic analysis. Evolution of the SP wavelength and extinction intensity during oxidation at different temperatures follows the same kinetics when the oxidation time is normalized to τ, thus pointing to a general oxidation mechanism. The characteristic time τ is used to estimate the activation energy of the process, determined to be 144 ± 6 kJ mol -1 , similar to previously reported values for high-temperature Cu thermal oxidation. The central role of the NKE in the solid-state oxidation process is revealed by electron microscopy, while formation of Cu 2 O as the major oxidation product is established by X-ray diffraction, XPS, and electrochemical measurements. The results indicate a transition of the oxidation mechanism from a Valensi-Carter (VC) to NKE mechanism with the degree of oxidation. To interpret the optical evolution during oxidation, Mie scattering solutions for metal core-oxide shell spherical particles are computed, considering formation of Kirkendall voids. The model calculations are in agreement with the experimental results, showing that the large red-shift of the LSPR band during oxidation is the result of Kirkendall voiding, thus establishing the major role of the NKE in determining the optical behavior of such systems.

Proton Conduction in Grain-Boundary-Free Oxygen-Deficient BaFeO2.5+δ Thin Films

PubMed Central

Benes, Alexander; Molinari, Alan; Kruk, Robert; Brötz, Joachim; Chellali, Reda; Hahn, Horst

2017-01-01

Reduction of the operating temperature to an intermediate temperature range between 350 °C and 600 °C is a necessity for Solid Oxide Fuel/Electrolysis Cells (SOFC/SOECs). In this respect the application of proton-conducting oxides has become a broad area of research. Materials that can conduct protons and electrons at the same time, to be used as electrode catalysts on the air electrode, are especially rare. In this article we report on the proton conduction in expitaxially grown BaFeO2.5+δ (BFO) thin films deposited by pulsed laser deposition on Nb:SrTiO3 substrates. By using Electrochemical Impedance Spectroscopy (EIS) measurements under different wet and dry atmospheres, the bulk proton conductivity of BFO (between 200 °C and 300 °C) could be estimated for the first time (3.6 × 10−6 S cm−1 at 300 °C). The influence of oxidizing measurement atmosphere and hydration revealed a strong dependence of the conductivity, most notably at temperatures above 300 °C, which is in good agreement with the hydration behavior of BaFeO2.5 reported previously. PMID:29286321

Creep analysis of solid oxide fuel cell with bonded compliant seal design

NASA Astrophysics Data System (ADS)

Jiang, Wenchun; Zhang, Yucai; Luo, Yun; Gong, J. M.; Tu, S. T.

2013-12-01

Solid oxide fuel cell (SOFC) requires good sealant because it works in harsh conditions (high temperature, thermal cycle, oxidative and reducing gas environments). Bonded compliant seal (BCS) is a new sealing method for planar SOFC. It uses a thin foil metal to bond the window frame and cell, achieving the seal between window frame and cell. At high temperature, a comprehensive evaluation of its creep strength is essential for the adoption of BCS design. In order to characterize the creep behavior, the creep induced by thermal stresses in SOFC with BCS design is simulated by finite element method. The results show that the foil is compressed and large thermal stresses are generated. The initial peak thermal stress is located in the thin foil because the foil acts as a spring stores the thermal stresses by elastic and plastic deformation in itself. Serving at high temperature, initial thermal displacement is partially recovered because of the creep relaxation, which becomes a new discovered advantage for BCS design. It predicts that the failures are likely to happen in the middle of the cell edge and BNi-2 filler metal, because the maximum residual displacement and creep strain are located.

Electrical conductivity of oxidized-graphenic nanoplatelets obtained from bamboo: effect of the oxygen content

NASA Astrophysics Data System (ADS)

Gross, K.; Prías Barragán, J. J.; Sangiao, S.; De Teresa, J. M.; Lajaunie, L.; Arenal, R.; Ariza Calderón, H.; Prieto, P.

2016-09-01

The large-scale production of graphene and reduced-graphene oxide (rGO) requires low-cost and eco-friendly synthesis methods. We employed a new, simple, cost-effective pyrolytic method to synthetize oxidized-graphenic nanoplatelets (OGNP) using bamboo pyroligneous acid (BPA) as a source. Thorough analyses via high-resolution transmission electron microscopy and electron energy-loss spectroscopy provides a complete structural and chemical description at the local scale of these samples. In particular, we found that at the highest carbonization temperature the OGNP-BPA are mainly in a sp2 bonding configuration (sp2 fraction of 87%). To determine the electrical properties of single nanoplatelets, these were contacted by Pt nanowires deposited through focused-ion-beam-induced deposition techniques. Increased conductivity by two orders of magnitude is observed as oxygen content decreases from 17% to 5%, reaching a value of 2.3 × 103 S m-1 at the lowest oxygen content. Temperature-dependent conductivity reveals a semiconductor transport behavior, described by the Mott three-dimensional variable range hopping mechanism. From the localization length, we estimate a band-gap value of 0.22(2) eV for an oxygen content of 5%. This investigation demonstrates the great potential of the OGNP-BPA for technological applications, given that their structural and electrical behavior is similar to the highly reduced rGO sheets obtained by more sophisticated conventional synthesis methods.

Comparison of NBG-18, NBG-17, IG-110 and IG-11 oxidation kinetics in air

NASA Astrophysics Data System (ADS)

Lee, Jo Jo; Ghosh, Tushar K.; Loyalka, Sudarshan K.

2018-03-01

The oxidation rates of several nuclear-grade graphites, NBG-18, NBG-17, IG-110 and IG-11, were measured in air using thermogravimetry. Kinetic parameters and oxidation behavior for each grade were compared by coke type, filler grain size and microstructure. The thickness of the oxidized layer for each grade was determined by layer peeling and direct density measurements. The results for NBG-17 and IG-11 were compared with those available in the literature and our recently reported results for NBG-18 and IG-110 oxidation in air. The finer-grained graphites IG-110 and IG-11 were more oxidized than medium-grained NBG-18 and NBG-17 because of deeper oxidant penetration, higher porosity and higher probability of available active sites. Variation in experimental conditions also had a marked effect on the reported kinetic parameters by several studies. Kinetic parameters such as activation energy and transition temperature were sensitive to air flow rates as well as sample size and geometry.

Heat-induced redistribution of surface oxide in uranium

NASA Astrophysics Data System (ADS)

Swissa, Eli; Shamir, Noah; Mintz, Moshe H.; Bloch, Joseph

1990-09-01

The redistribution of oxygen and uranium metal at the vicinity of the metal-oxide interface of native and grown oxides due to vacuum thermal annealing was studied for uranium and uranium-chromium alloy using Auger depth profiling and metallographic techniques. It was found that uranium metal is segregating out through the uranium oxide layer for annealing temperatures above 450°C. At the same time the oxide is redistributed in the metal below the oxide-metal interface in a diffusion like process. By applying a diffusion equation of a finite source, the diffusion coefficients for the process were obtained from the oxygen depth profiles measured for different annealing times. An Arrhenius like behavior was found for the diffusion coefficient between 400 and 800°C. The activation energy obtained was Ea = 15.4 ± 1.9 kcal/mole and the pre-exponential factor, D0 = 1.1 × 10 -8cm2/ s. An internal oxidation mechanism is proposed to explain the results.

Property and microstructural nonuniformity in the yttrium-barium-copper-oxide superconductor determined from electrical, magnetic, and ultrasonic measurements. Ph.D. Thesis - Case Western Reserve Univ.

NASA Technical Reports Server (NTRS)

Roth, Don J.

1991-01-01

The purpose of this dissertation was the following: (1) to characterize the effect of pore fraction on a comprehensive set of electrical and magnetic properties for the yttrium-barium-copper-oxide (YBCO) high temperature ceramic superconductor; and (2) to determine the viability of using a room-temperature, nondestructive characterization method to aid in the prediction of superconducting (cryogenic) properties. The latter involved correlating ultrasonic velocity measurements at room temperature with property-affecting pore fraction and oxygen content variations. The use of ultrasonic velocity for estimating pore fraction in YBCO is presented, and other polycrystalline materials are reviewed, modeled, and statistically analyzed. This provides the basis for using ultrasonic velocity to interrogate microstructure. The effect of pore fraction (0.10-0.25) on superconductor properties of YBCO samples was characterized. Spatial (within-sample) variations in microstructure and superconductor properties were investigated, and the effect of oxygen content on elastic behavior was examined. Experimental methods used included a.c. susceptibility, electrical, and ultrasonic velocity measurements. Superconductor properties measured included transition temperature, magnetic transition width, transport and magnetic critical current density, magnetic shielding, a.c. loss, and sharpness of the voltage-current characteristics. An ultrasonic velocity image constructed from measurements at 1mm increments across a YBCO sample revealed microstructural variations that correlated with variations in magnetic shielding and a.c. loss behavior. Destructive examination using quantitative image analysis revealed pore fraction to be the varying microstructural feature.

Interactive effects of wildfire and permafrost on microbial communities and soil processes in an Alaskan black spruce forest.

Treesearch

Mark P. Waldrop; Jennifer W. Harden

2008-01-01

Boreal forests contain significant quantities of soil carbon that may be oxidized to CO2 given future increases in climate warming and wildfire behavior. At the ecosystem scale, decomposition and heterotrophic respiration are strongly controlled by temperature and moisture, but we questioned whether changes in microbial biomass, activity, or...

Evaluation of Ti-48Al-2Nb Under Fretting Conditions

NASA Technical Reports Server (NTRS)

Miyoshi, Kazuhisa; Lerch, Bradley A.; Draper, Susan L.; Raj, Sai V.

2001-01-01

An investigation was conducted to examine the fretting behavior of lambda-TiAl (Ti-48Al-2Cr-2Nb) in contact with a nickel-base superalloy (Inconel 718) in air at temperatures from 23 to 550 C. Fretting wear experiments were conducted with 9.4-mm-diameter hemispherical Inconel (IN) 718 pins in contact with Ti-48Al-2Cr-2Nb flats (and the reverse) at loads from 1 to 40 N and fretting frequencies from 50 to 160 Hz with slip amplitudes from 50 to 200 microns for 1 to 20 million fretting cycles. The results were similar for both combinations of pin and flat. Reference fretting wear experiments were also conducted with 9.4-mm-diameter hemispherical Ti-6Al-4V pins in contact with IN718 flats. The interfacial adhesive bonds between Ti-48Al-2Cr-2Nb and IN718 in contact were generally stronger than the cohesive bonds in the cohesively weaker Ti-48Al-2Cr-2Nb. The failed Ti-48Al-2Cr-2Nb subsequently transferred to the IN718 surface at any fretting condition. The wear scars produced on Ti-48Al-2Cr-2Nb contained metallic and oxide wear debris, scratches, plastically deformed asperities, cracks, and fracture pits. Oxide layers readily formed on the Ti-48Al-2Cr-2Nb surface at 550 C, but cracks easily occurred in the oxide layers. Factors including fretting frequency, temperature, slip amplitude, and load influenced the fretting behavior of Ti-48Al-2Cr-2Nb in contact with IN718. The wear volume loss of Ti-48Al-2Cr-2Nb generally decreased with increasing fretting frequency. The increasing rate of oxidation at elevated temperatures up to 200 C led to a drop in wear volume loss at 200 C. However, the fretting wear increased as the temperature was increased from 200 to 550 C. The highest temperatures of 450 and 550 C resulted in oxide film disruption with generation of cracks, loose wear debris, and pits on the Ti-48Al-2Cr-2Nb wear surface. The wear volume loss generally increased as the slip amplitude increased. The wear volume loss also generally increased as the load increased. Increasing slip amplitude and increasing load both tended to produce more metallic wear debris, causing severe abrasive wear in the contacting metals.

a Study of Nanocomposite Coatings on the Surface of Ship Exhaust Pipe

NASA Astrophysics Data System (ADS)

Shen, Yan; Sahoo, Prasanta K.; Pan, Yipeng

In order to improve the high temperature oxidation resistance of exhaust pipes, the nanocomposite coatings are carried out on the surface of exhaust pipe by pulsed current electrodeposition technology, and the microstructure and oxidation behavior of the nanocomposite coatings are investigated experimentally. This paper mainly focuses on the experimental work to determine the structural characteristics and oxidation resistance of nanocomposite coatings in presence of attapulgite and cerium oxide CeO2. The results show that the amount of the attapulgite-CeO2 has significant influence on the structural properties of nanocomposite coatings. The surface of coating becomes more compact and smooth with the increase of the amount of the attapulgite and CeO2. Furthermore, the anti-oxidation performances of the nanocomposite coatings formed with attapulgite and CeO2 were both better than those of the composite coatings formed without attapulgite and CeO2.

Water vapor effect on high-temperature oxidation behavior of Fe3Al intermetallics

PubMed Central

Chevalier, Sebastian; Juzon, Pitor; Przybylski, Kazimierz; Larpin, Jean-Pierre

2009-01-01

Fe3Al intermetallics (Fe3Al, Fe3Al-Zr, Fe3Al-Zr,Mo and Fe3Al-Zr, Mo, Nb) were oxidized at 950 °C in dry and humid (11 vol% water) synthetic air. Thermogravimetric measurements showed that the oxidation rates of the tested intermetallics were lower in humid air than in dry air (especially for Fe3Al-Zr, Mo and Fe3Al-Zr, Mo, Nb). The addition of small amounts of Zr, Mo or Nb improved the kinetics compared with that of the undoped Fe3Al. Fe3Al showed massive spallation, whereas Fe3Al-Zr, Fe3Al-Zr, Mo and Fe3Al-Zr, Mo, Nb produced a flat, adherent oxide layer. The rapid transformation of transient alumina into alpha alumina may explain the decrease in the oxidation rate in humid air. PMID:27877306

Study of the effects of gaseous environments on the hot corrosion of superalloy materials

NASA Technical Reports Server (NTRS)

Smeggil, J. G.; Bornstein, N. S.

1980-01-01

The effect of the gaseous corrodent NaCl on the high temperature oxidation and sodium sulfate induced hot corrosion behavior of alumina formers, chromia formers, and the superalloy B-1900 was examined. Isothermal experiments were conducted at 900 C and 1050 C in air in the presence and absence of NaCl vapors. Microstructural changes in oxide morphology and increased rates of oxidation were observed when NaCl(g) was present. It is hypothesized that the accelerated rates of oxidation are the result of removal of aluminum from the scale substrate interface and the weakening of the scale substrate bonds. The aluminum removed was redeposited on the surfaces in the form of alumina whiskers. For the superalloy B-1900, alumina whiskers are also formed, and the alloy oxidizes at catastrophic rates. In the case of Ni-25Cr alloy, NaCl vapors interact with the scale depleting it of chromium.

Estimation of Axial Fretting Fatigue Life at Elevated Temperatures Using Critical Distance Theory

NASA Astrophysics Data System (ADS)

Majzoobi, G. H.; Azhdarzadeh, P.

Fretting fatigue life is traditionally estimated by experiment. The objective of this work is to introduce a special approach for estimation of axial fretting fatigue life at elevated temperatures from plain fatigue test based on the critical distance theory. The method uses Fatemi-Socie parameter as a multiaxial criterion to compute the stress multiaxiality on focus path. This method considers only elastic behavior for materials, and two characteristic diagrams are obtained from plain fatigue tests on two U-shaped and V-shaped notched specimens. The results showed reasonable agreement between the predictions by the proposed method and the experiments for ambient temperature. For elevated temperatures, the results indicated that the predicted fretting fatigue life was considerably overestimated in the low cycle fatigue (LCF) regime and underestimated in the high cycle fatigue (HCF) region with respect to experimental measurements. The reason for such discrepancy is believed to be due to the complex behavior of AL 7075-T6, which exhibits at elevated temperatures because of the problems such as aging, oxidation and reduction of strength.

Thermomechanical Fatigue of Ductile Cast Iron and Its Life Prediction

NASA Astrophysics Data System (ADS)

Wu, Xijia; Quan, Guangchun; MacNeil, Ryan; Zhang, Zhong; Liu, Xiaoyang; Sloss, Clayton

2015-06-01

Thermomechanical fatigue (TMF) behaviors of ductile cast iron (DCI) were investigated under out-of-phase (OP), in-phase (IP), and constrained strain-control conditions with temperature hold in various temperature ranges: 573 K to 1073 K, 723 K to 1073 K, and 433 K to 873 K (300 °C to 800 °C, 450 °C to 800 °C, and 160 °C to 600 °C). The integrated creep-fatigue theory (ICFT) model was incorporated into the finite element method to simulate the hysteresis behavior and predict the TMF life of DCI under those test conditions. With the consideration of four deformation/damage mechanisms: (i) plasticity-induced fatigue, (ii) intergranular embrittlement, (iii) creep, and (iv) oxidation, as revealed from the previous study on low cycle fatigue of the material, the model delineates the contributions of these physical mechanisms in the asymmetrical hysteresis behavior and the damage accumulation process leading to final TMF failure. This study shows that the ICFT model can simulate the stress-strain response and life of DCI under complex TMF loading profiles (OP and IP, and constrained with temperature hold).

Electric field cycling behavior of ferroelectric hafnium oxide.

PubMed

Schenk, Tony; Schroeder, Uwe; Pešić, Milan; Popovici, Mihaela; Pershin, Yuriy V; Mikolajick, Thomas

2014-11-26

HfO2 based ferroelectrics are lead-free, simple binary oxides with nonperovskite structure and low permittivity. They just recently started attracting attention of theoretical groups in the fields of ferroelectric memories and electrostatic supercapacitors. A modified approach of harmonic analysis is introduced for temperature-dependent studies of the field cycling behavior and the underlying defect mechanisms. Activation energies for wake-up and fatigue are extracted. Notably, all values are about 100 meV, which is 1 order of magnitude lower than for conventional ferroelectrics like lead zirconate titanate (PZT). This difference is mainly atttributed to the one to two orders of magnitude higher electric fields used for cycling and to the different surface to volume ratios between the 10 nm thin films in this study and the bulk samples of former measurements or simulations. Moreover, a new, analog-like split-up effect of switching peaks by field cycling is discovered and is explained by a network model based on memcapacitive behavior as a result of defect redistribution.

Thermochemical and trace element behavior of coal gangue, agricultural biomass and their blends during co-combustion.

PubMed

Zhou, Chuncai; Liu, Guijian; Cheng, Siwei; Fang, Ting; Lam, Paul Kwan Sing

2014-08-01

The thermal decomposition behavior of coal gangue, peanut shell, wheat straw and their blends during combustion were determined via thermogravimetric analysis. The coal gangue/agricultural biomass blends were prepared in four weight ratios and oxidized under dynamic conditions from room temperature to 1000 °C by various heating rates. Kinetic models were carried out to evaluate the thermal reactivity. The overall mass balance was performed to assess the partition behavior of coal gangue, peanut shell and their blends during combustion in a fixed bed reactor. The decomposition processes of agricultural biomass included evaporation, release of volatile matter and combustion as well as char oxidation. The thermal reactivity of coal gangue could be improved through the addition of agricultural biomass in suitable proportion and subsequent appropriate heating rate during combustion. In combination with the heating value and base/acid ratio limitations, a blending ratio of 30% agricultural biomass is conservatively selected as optimum blending. Copyright © 2014 Elsevier Ltd. All rights reserved.

Effect of lattice-misfit strain on the process-induced imprint behavior in epitaxial Pb (Zr0.52Ti0.48)O3 thin films

NASA Astrophysics Data System (ADS)

Wu, Wenbin; Wang, Y.; Pang, G. K. H.; Wong, K. H.; Choy, C. L.

2004-08-01

The effect of lattice-misfit strain on the process-induced imprint behavior in Pb (Zr0.52Ti0.48)O3 (PZT) capacitors with Pt (top), and SrRuO3, La0.7Sr0.3MnO3 or LaNiO3 (bottom) electrodes has been studied. With the different oxide electrodes and by changing the deposition oxygen pressure, various lattice-misfit strains in the epitaxial PZT films have been produced. It was found that after in situ annealing at reduced oxygen pressures, the capacitors showed an increased voltage offset in the polarization-electric field hysteresis loops with increasing the misfit strain, irrelevant to the oxide electrodes employed, while lattice disorder at the bottom interface can effectively eliminate the voltage shift. Our results suggest that the imprint behavior is caused by oxygen loss via dislocations generated by the misfit strain relaxation at the growth temperature.

Studies of the oxidized Cu(100) surface using positron annihilation induced Auger electron spectroscopy

NASA Astrophysics Data System (ADS)

Maddox, W.; Fazleev, N. G.; Nadesalingam, M. P.; Weiss, A. H.

2008-03-01

We discuss recent progress in studies of an oxidized Cu(100) single crystal subjected to vacuum annealing over a temperature range from 293K to 1073K using positron annihilation induced Auger electron spectroscopy (PAES). The PAES measurements show a large monotonic increase in the intensity of the positron annihilation induced Cu M2,3 VV Auger peak as the sample is subjected to a series of isochronal anneals in vacuum up to annealing temperature 573 K. The intensity then decreases monotonically as the annealing temperature is increased to 873 K. Experimental PAES results are analyzed by performing calculations of positron surface states and annihilation probabilities of surface-trapped positrons with relevant core electrons taking into account the charge redistribution at the surface, surface reconstructions, and electron-positron correlations effects. The effects of oxygen adsorption and surface reconstruction on localization of positron surface state wave functions and annihilation characteristics are analyzed. Possible explanations are provided for the observed behavior of the intensity of positron annihilation induced Cu M2,3VV Auger peak with changes of the annealing temperature.

Elevated temperature mechanical properties and residual tensile properties of two cast superalloys and several nickel-base oxide dispersion strengthened alloys

NASA Technical Reports Server (NTRS)

Whittenberger, J. D.

1981-01-01

The elevated temperature tensile, stress-rupture and creep properties and residual tensile properties after creep straining have been determined for two cast superalloys and several wrought Ni-16Cr-4Al-yttria oxide dispersion strengthened (ODS) alloys. The creep behavior of the ODS alloys is similar to that of previously studied ODS nickel alloys. In general, the longitudinal direction is stronger than the long transverse direction, and creep is at least partially due to a diffusional creep mechanism as dispersoid-free zones were observed after creep-rupture testing. The tensile properties of the nickel-base superalloy B-1900 and cobalt-base superalloy MAR-M509 are not degraded by prior elevated temperature creep straining (at least up to 1 pct) between 1144 and 1366 K. On the other hand, the room temperature tensile properties of ODS nickel-base alloys can be reduced by prior creep strains of 0.5 pct or less between 1144 and 1477 K, with the long transverse direction being more susceptible to degradation than the longitudinal direction.

High-Temperature Wettability and Interactions between Y-Containing Ni-Based Alloys and Various Oxide Ceramics.

PubMed

Li, Jinpeng; Zhang, Huarui; Gao, Ming; Li, Qingling; Bian, Weidong; Tao, Tongxiang; Zhang, Hu

2018-05-07

To obtain appropriate crucible materials for vacuum induction melting of MCrAlY alloys, four different oxide ceramics, including MgO, Y₂O₃, Al₂O₃, and ZrO₂, with various microstructures were designed and characterized. The high-temperature wettability and interactions between Ni-20Co-20Cr-10Al-1.5Y alloys and oxide ceramics were studied by sessile drop experiments under vacuum. The results showed that all the systems exhibited non-wetting behavior. The contact angles were stable during the melting process of alloys and the equilibrium contact angles were 140° (MgO), 148° (Y₂O₃), 154° (Al₂O₃), and 157° (ZrO₂), respectively. The interfacial reaction between the ceramic substrates and alloys occurred at high temperature. Though the ceramics had different microstructures, similar continuous Y₂O₃ reaction layer with thicknesses of about 25 μm at the alloy-ceramic interface in MgO, Al₂O₃, and ZrO₂ systems formed. The average area percentage of oxides in the alloy matrices were 0.59% (MgO), 0.11% (Al₂O₃), 0.09% (ZrO₂), and 0.02% (Y₂O₃), respectively. The alloys, after reacting with MgO ceramic, had the highest inclusion content, while those with the lowest content were in the Y₂O₃ system. Y₂O₃ ceramic was the most beneficial for vacuum induction melting of high-purity Y-containing Ni-based alloys.

Superconductivity and non-Fermi liquid behavior near a nematic quantum critical point.

PubMed

Lederer, Samuel; Schattner, Yoni; Berg, Erez; Kivelson, Steven A

2017-05-09

Using determinantal quantum Monte Carlo, we compute the properties of a lattice model with spin [Formula: see text] itinerant electrons tuned through a quantum phase transition to an Ising nematic phase. The nematic fluctuations induce superconductivity with a broad dome in the superconducting [Formula: see text] enclosing the nematic quantum critical point. For temperatures above [Formula: see text], we see strikingly non-Fermi liquid behavior, including a "nodal-antinodal dichotomy" reminiscent of that seen in several transition metal oxides. In addition, the critical fluctuations have a strong effect on the low-frequency optical conductivity, resulting in behavior consistent with "bad metal" phenomenology.

Thermal behavior and catalytic activity in naphthalene destruction of Ce-, Zr- and Mn-containing oxide layers on titanium

NASA Astrophysics Data System (ADS)

Vasilyeva, Marina S.; Rudnev, Vladimir S.; Wiedenmann, Florian; Wybornov, Svetlana; Yarovaya, Tatyana P.; Jiang, Xin

2011-11-01

The present paper is devoted to studies of the composition and surface structure, including those after annealing at high temperatures, and catalytic activity in the reaction of naphthalene destruction of Ce-, Zr- and Mn-containing oxide layers on titanium obtained by means of the plasma electrolytic oxidation (PEO) method. The composition and structure of the obtained systems were investigated using the methods of X-ray phase and energy dispersive analysis and scanning electron microscopy (SEM). It was demonstrated that Ce- and Zr- containing structures had relatively high thermal stability: their element and phase compositions and surface structure underwent virtually no changes after annealing in the temperature range 600-800 °C. Annealing of Ce- and Zr-containing coatings in the temperature range 850-900 °C resulted in substantial changes of their surface composition and structure: a relatively homogeneous and porous surface becomes coated by large pole-like crystals. The catalytic studies showed rather high activity of Ce- and Zr-containing coatings in the reaction of naphthalene destruction at temperatures up to 850 °C. Mn-containing structures of the type MnOx + SiO2 + TiO2/Ti have a well-developed surface coated by “nano-whiskers”. The phase composition and surface structure of manganese-containing layers changes dramatically in the course of thermal treatment. After annealing above 600 °C nano-whiskers vanish with formation of molten structures on the surface. The Mn-containing oxide systems demonstrated lower conversion degrees than the Ce- and Zr-containing coatings, which can be attributed to substantial surface modification and formation of molten manganese silicates at high temperatures.

Surface characterizations of oxides synthesized by successive ionic layer deposition

NASA Astrophysics Data System (ADS)

Gilbert, Thomas I.

Successive ionic layer deposition (SILD) is an aqueous technique for depositing thin oxide films on a surface in a layer-by-layer fashion through a series of chemical reactions. This dissertation examines empirical aspects of the SILD technique by characterizing thin oxide films synthesized on model planar supports and then extends the SILD technique to synthesize supported oxide nanostructures on three dimensional supports of interest to catalysis. Atomic force microscopy, x-ray photoelectron spectroscopy, and scanning electron microscopy provided insight into the SILD of zirconia, alumina, and barium oxide thin films on silicon wafers. The SILD conditions that most affected the surface morphology of the thin oxide films were the selection of aqueous metal salt precursors comprising the SILD solutions and the total number of SILD cycles. Recent studies suggest that a highly dispersed phase of barium oxide supported on alumina interacts differently with NO2 than a bulk-like phase of barium oxide SILD was used to synthesize disperse nanoislands or rafts of barium oxide on larger rafts of alumina supported on a silicon wafer. The SILD method was then extended to deposit barium oxide on an alumina powder support comprised of dense 150 nm spherical crystallites fused together into 1-2 pm particles. Equally weight loaded samples of barium oxide on the fused alumina powder were prepared by SILD and wet impregnation. The NO2 storage behavior of the barium oxide, evaluated by thermogravimetric analysis during NO2 temperature programmed desorption (TPD) experiments, provided insight into the dispersion of barium oxide that resulted from each of the loading techniques. The highly dispersed barium oxide rafts synthesized by SILD on fused alumina released NO2 at temperatures below 500°C during TPD. By comparison, the barium oxide loaded by wet impregnation showed a higher temperature desorption feature above 500°C indicative of bulk-like barium oxide nanoparticles. The NO2 weight loss curves were also used to calculate the relative percentages of BaO in the dispersed phase and bulk-like phase for each loading technique. The ability of SILD to synthesize highly disperse and uniform, conformal oxide coatings on three dimensional supports provides fundamental insight into the interactions between catalysts and supports.

Modelling the influence of carbon content on material behavior during forging

NASA Astrophysics Data System (ADS)

Korpała, G.; Ullmann, M.; Graf, M.; Wester, H.; Bouguecha, A.; Awiszus, B.; Behrens, B.-A.; Kawalla, R.

2017-10-01

Nowadays the design of single process steps and even of whole process chains is realized by the use of numerical simulation, in particular finite element (FE) based methods. A detailed numerical simulation of hot forging processes requires realistic models, which consider the relevant material-specific parameters to characterize the material behavior, the surface phenomena, the dies as well as models for the machine kinematic. This data exists partial for several materials, but general information on steel groups depending on alloying elements are not available. In order to generate the scientific input data regarding to material modelling, it is necessary to take into account the mathematical functions for deformation behavior as well as recrystallization kinetic, which depends alloying elements, initial microstructure and reheating mode. Besides the material flow characterization, a detailed description of surface changes caused by oxide scale is gaining in importance, as these phenomena affect the material flow and the component quality. Experiments to investigate the influence of only one chemical element on the oxide scale kinetic and the inner structure at high temperatures are still not available. Most data concerning these characteristics is provided for the steel grade C45, so this steel will be used as basis for the tests. In order to identify the effect of the carbon content on the material and oxidation behavior, the steel grades C15 and C60 will be investigated. This paper gives first approaches with regard to the influence of the carbon content on the oxide scale kinetic and the flow stresses combined with the initial microstructure.

Alternating current transport and dielectric relaxation of nanocrystalline graphene oxide

NASA Astrophysics Data System (ADS)

Zedan, I. T.; El-Menyawy, E. M.

2018-07-01

Graphene oxide (GO) has been synthesized from natural graphite using modified Hummer's method and is subjected to sonication for 1 h. X-ray diffraction (XRD) showed that the prepared GO has nanocrystalline structure with particle size of about 5 nm and high-resolution transmission electron microscope showed that it had a layered structure. The nanocrystalline GO powder was pressed as a disk and the alternating current (AC) electrical conductivity, σAC, and dielectric properties have been investigated in the frequency range 50Hz-5 MHz and temperature range 298-523K using parallel plate spectroscopic technique. Analysis of σ AC as a function of frequency shows that the relation follows Jonscher's universal law with frequency exponent decreases with increasing temperature in which the correlated barrier hopping model is applicable to describe the behavior. The dielectric constant and dielectric loss are studied as functions of frequency and temperature. The dielectric modulus formalism is used for describing the relaxation process in which the relaxation time and its activation energy were evaluated.

Studies of Oxidation of the Cu(100) Surface Using Low Energy Positrons

DOE Office of Scientific and Technical Information (OSTI.GOV)

Fazleev, N. G.; Kazan State University, Kazan 420008; Maddox, W. B.

2009-03-10

Changes in the surface of an oxidized Cu(100) single crystal resulting from vacuum annealing have been investigated using positron annihilation induced Auger electron spectroscopy (PAES). PAES measurements show a large increase in the intensity of the positron annihilation induced Cu M{sub 2,3}VV Auger peak as the sample is subjected to a series of isochronal anneals in vacuum up to annealing temperature 300 deg. C. The intensity then decreases monotonically as the annealing temperature is increased to {approx}600 deg. C. Experimental PAES results are analyzed by performing calculations of positron surface states and annihilation probabilities of surface-trapped positrons with relevant coremore » electrons taking into account the charge redistribution at the surface, surface reconstructions, and electron-positron correlations effects. Possible explanation for the observed behavior of the intensity of positron annihilation induced Cu M{sub 2,3}VV Auger peak with changes of the annealing temperature is proposed.« less

Ba6-3 x Nd8+2 x Ti18O54 Tungsten Bronze: A New High-Temperature n-Type Oxide Thermoelectric

NASA Astrophysics Data System (ADS)

Azough, Feridoon; Freer, Robert; Yeandel, Stephen R.; Baran, Jakub D.; Molinari, Marco; Parker, Stephen C.; Guilmeau, Emmanuel; Kepaptsoglou, Demie; Ramasse, Quentin; Knox, Andy; Gregory, Duncan; Paul, Douglas; Paul, Manosh; Montecucco, Andrea; Siviter, Jonathan; Mullen, Paul; Li, Wenguan; Han, Guang; Man, Elena A.; Baig, Hasan; Mallick, Tapas; Sellami, Nazmi; Min, Gao; Sweet, Tracy

2016-03-01

Semiconducting Ba6-3 x Nd8+2 x Ti18O54 ceramics (with x = 0.00 to 0.85) were synthesized by the mixed oxide route followed by annealing in a reducing atmosphere; their high-temperature thermoelectric properties have been investigated. In conjunction with the experimental observations, atomistic simulations have been performed to investigate the anisotropic behavior of the lattice thermal conductivity. The ceramics show promising n-type thermoelectric properties with relatively high Seebeck coefficient, moderate electrical conductivity, and temperature-stable, low thermal conductivity; For example, the composition with x = 0.27 (i.e., Ba5.19Nd8.54Ti18O54) exhibited a Seebeck coefficient of S 1000K = 210 µV/K, electrical conductivity of σ 1000K = 60 S/cm, and thermal conductivity of k 1000K = 1.45 W/(m K), leading to a ZT value of 0.16 at 1000 K.

Oxidation behavior of V-Cr-Ti alloys in low-partial-pressure oxygen environments

DOE Office of Scientific and Technical Information (OSTI.GOV)

Natesan, K.; Uz, M.

A test program is in progress at Argonne National Laboratory to evaluate the effect of pO{sub 2} in the exposure environment on oxygen uptake, scaling kinetics, and scale microstructure in V-Cr-Ti alloys. The data indicate that the oxidation process follows parabolic kinetics in all of the environments used in the present study. From the weight change data, parabolic rate constants were evaluated as a function of temperature and exposure environment. The temperature dependence of the parabolic rate constants was described by an Arrhenius relationship. Activation energy for the oxidation process was fairly constant in the oxygen pressure range of 1more » {times} 10{sup {minus}6} to 1 {times} 10{sup {minus}1} torr for both the alloys. The activation energy for oxidation in air was significantly lower than in low-pO{sub 2} environments, and for oxidation in pure O{sub 2} at 760 torr was much lower than in low-pO{sub 2} environments. X-ray diffraction analysis of the specimens showed that VO{sub 2} was the dominant phase in low-pO{sub 2} environments, while V{sub 2}O{sub 5} was dominant in air and in pure oxygen at 76f0 torr.« less

Multilayer Regulation of Atomic Boron Nitride Films to Improve Oxidation and Corrosion Resistance of Cu.

PubMed

Ren, Siming; Cui, Mingjun; Pu, Jibin; Xue, Qunji; Wang, Liping

2017-08-16

The boron nitride (BN) monolayer (1L) with high impermeability and resistivity seems to hold promise as a long-term corrosion barrier for Cu under ambient condition, which is supported by recent researches. Here, we perform a complete study of the alternating temperature tests (the sample is exposed in air for 30 days and subsequently heated at 200 °C for 2 h) and electrochemical measurements on 1L and multilayer BN-coated Cu foils. Results imply that the BN-coated Cu foils are less oxidized than uncoated Cu foils after alternating temperature tests, regardless of the layers of BN. Particularly, the oxidation process proceeds slowly in multilayers because most of the underlying defects are covered with BN layers to suppress the oxygen diffusion in the vertical direction and the oxidation mainly occurs on the wrinkled region of BN films. Electrochemical analyses reveal that the BN layers provide an effective physical barrier against the corrosive medium and inhibit the electron diffusion because of their high electrical insulating behavior and the corrosion resistance of the samples increases with increasing BN layers. These findings indicate that BN films with adequate layers are good candidates for oxidation and corrosion protection at the atomic level, which is vital to many industrial and academic applications.

Melamine-Schiff base/manganese complex with denritic structure: An efficient catalyst for oxidation of alcohols and one-pot synthesis of nitriles.

PubMed

Kazemnejadi, Milad; Nikookar, Mahsa; Mohammadi, Mohammad; Shakeri, Alireza; Esmaeilpour, Mohsen

2018-05-18

Efficient and selective oxidation of alcohol to the corresponding carbonyl and/or nitrile was carried out by a new water-soluble melamine-based dendritic Mn(III) complex (Melamine-Mn (III)-Schiff base complex) in the presence of 2,4,6-trichloro-1,3,5-triazine (TCT) and O 2 at room temperature. Also, the oxidation of amine to the corresponding nitrile with high selectivity and conversion was performed at room temperature using the current method and high amounts of turnover frequencies (TOFs) were obtained for reactions. This system was also applicable for direct preparation of oxime through oxidation of alcohol. The catalyst was characterized by Fourier-transform infrared (FTIR), ultraviolet-visible (UV-Vis), thermogravimetric analysis (TGA), energy-dispersive X-ray (EDX), X-ray photoelectron spectroscopy (XPS), CHN and inductively coupled plasma (ICP) analyses. Also, oxidation/reduction behavior of the catalyst was studied by cyclic voltammetry (CV). Moreover, chemoselectivity of the catalyst was discussed with various combinations. The water-soluble catalyst could be recycled from the reaction mixture and reused for several times with a very low losing in efficiency. The recovered catalyst was also investigated with various analyses. Finally, gram scale preparation of nitrile was evaluated by present method. Copyright © 2018 Elsevier Inc. All rights reserved.

Fracture resistance of a TiB2 particle/SiC matrix composite at elevated temperature

NASA Technical Reports Server (NTRS)

Jenkins, Michael G.; Salem, Jonathan A.; Seshadri, Srinivasa G.

1988-01-01

The fracture resistance of a comercial TiB2 particle/SiC matrix composite was evaluated at temperatures ranging from 20 to 1400 C. A laser interferometric strain gauge (LISG) was used to continuously monitor the crack mouth opening displacement (CMOD) of the chevron-notched and straight-notched, three-point bend specimens used. Crack growth resistance curves (R-curves) were determined from the load versus displacement curves and displacement calibrations. Fracture toughness, work-of-fracture, and R-curve levels were found to decrease with increasing temperature. Microstructure, fracture surface, and oxidation coat were examined to explain the fracture behavior.

Fracture resistance of a TiB2 particle/SiC matrix composite at elevated temperature

NASA Technical Reports Server (NTRS)

Jenkins, Michael G.; Salem, Jonathan A.; Seshadri, Srinivasa G.

1989-01-01

The fracture resistance of a commercial TiB2 particle/SiC matrix composite was evaluated at temperatures ranging from 20 to 1400 C. A laser interferometric strain gauge (LiSG) was used to continuously monitor the crack mouth opening displacement (CMOD) of the chevron-notched and straight-notched, three-point bend specimens used. Crack growth resistance curves (R-curves) were determined from the load versus displacement curves and displacement calibrations. Fracture toughness, work-of-fracture, and R-curve levels were found to decrease with increasing temperature. Microstructure, fracture surface, and oxidation coat were examined to explain the fracture behavior.

Memory and learning behaviors mimicked in nanogranular SiO2-based proton conductor gated oxide-based synaptic transistors

NASA Astrophysics Data System (ADS)

Wan, Chang Jin; Zhu, Li Qiang; Zhou, Ju Mei; Shi, Yi; Wan, Qing

2013-10-01

In neuroscience, signal processing, memory and learning function are established in the brain by modifying ionic fluxes in neurons and synapses. Emulation of memory and learning behaviors of biological systems by nanoscale ionic/electronic devices is highly desirable for building neuromorphic systems or even artificial neural networks. Here, novel artificial synapses based on junctionless oxide-based protonic/electronic hybrid transistors gated by nanogranular phosphorus-doped SiO2-based proton-conducting films are fabricated on glass substrates by a room-temperature process. Short-term memory (STM) and long-term memory (LTM) are mimicked by tuning the pulse gate voltage amplitude. The LTM process in such an artificial synapse is due to the proton-related interfacial electrochemical reaction. Our results are highly desirable for building future neuromorphic systems or even artificial networks via electronic elements.In neuroscience, signal processing, memory and learning function are established in the brain by modifying ionic fluxes in neurons and synapses. Emulation of memory and learning behaviors of biological systems by nanoscale ionic/electronic devices is highly desirable for building neuromorphic systems or even artificial neural networks. Here, novel artificial synapses based on junctionless oxide-based protonic/electronic hybrid transistors gated by nanogranular phosphorus-doped SiO2-based proton-conducting films are fabricated on glass substrates by a room-temperature process. Short-term memory (STM) and long-term memory (LTM) are mimicked by tuning the pulse gate voltage amplitude. The LTM process in such an artificial synapse is due to the proton-related interfacial electrochemical reaction. Our results are highly desirable for building future neuromorphic systems or even artificial networks via electronic elements. Electronic supplementary information (ESI) available. See DOI: 10.1039/c3nr02987e

Temperature-Dependent Kinetic Study of Ammonia Oxidation Reaction on Gas Diffusion Electrodes in NH 3-Saturated 1 M KOH Solutions

DOE Office of Scientific and Technical Information (OSTI.GOV)

Liang, Z.; Song, L.; Ma, Z.

Ammonia oxidation reaction (AOR) is sluggish, especially at ambient temperature. To make kinetic study in electrochemical cell more informative and relevant to the catalysts’ performance in direct ammonia fuel cells (DAFCs) operating at about 100°C, it is desirable to study the AOR kinetics at elevated temperatures. However, ammonia evaporation accelerates with increasing temperature causing decrease of ammonia concentration with time. Here, we show a feasible solution to this issue - let argon gas bubble through concentrated ammonia before entering the electrochemical cell so that the solution can be kept ammonia saturated and oxygen free. Repeatable AOR polarization curves were obtainedmore » at temperatures up to 60°C. The AOR activities are characterized by the average currents at 0.5 V versus RHE measured at 20 mV s-1 in potential cycles below the potential of peak current. For PtIr/C, the PGM mass activities are 25 A g-1 at 25°C and 225 A g -1 at 60°C. The results for Pt/C and Ir/C and discussion of the causes for their distinct kinetic behavior will be presented at the meeting.« less

Crystal Structure and Transport Properties of Oxygen-Deficient Perovskite Sr 0.9Y 0.1CoO 3-δ

DOE PAGES

Yang, Tianrang; Mattick, Victoria F.; Chen, Yan; ...

2018-01-29

The present work reports a systematic study on temperature-dependent local crystal structure, oxygen stoichiometry, and electrical/electrochemical properties of an oxygen-deficient Sr 0.9Y 0.1CoO 3-δ (SYC10) perovskite using variable-temperature neutron diffraction (VTND), thermal gravimetric analysis, and electrical/electrochemical methods, respectively. The VTND reveals that the crystal symmetry of SYC10 remains P4/mmm tetragonal up to 900 °C. The tetragonal symmetry reflects the net effects of temperature and oxygen stoichiometry on crystal symmetry. The observed p-type electronic conductivity behavior originates from the charge-ordering between the two distinctive Co-sites. The partial oxide-ion conductivity and diffusivity obtained from oxygen permeation measurements are 2.3 × 10 –2more » S cm –1 and 7.98 × 10–8 cm 2/s at 800 °C in air, respectively. The electrochemical oxygen reduction reaction kinetics of the SYC10 cathode is primarily limited by the charge-transfer process at low temperatures (600–650 °C) and oxide-ion migration from the cathode into the electrolyte at high temperatures (700–800 °C).« less

Effect of shell thickness on the exchange bias blocking temperature and coercivity in Co-CoO core-shell nanoparticles

NASA Astrophysics Data System (ADS)

Thomas, S.; Reethu, K.; Thanveer, T.; Myint, M. T. Z.; Al-Harthi, S. H.

2017-08-01

The exchange bias blocking temperature distribution of naturally oxidized Co-CoO core-shell nanoparticles exhibits two distinct signatures. These are associated with the existence of two magnetic entities which are responsible for the temperature dependence of an exchange bias field. One is from the CoO grains which undergo thermally activated magnetization reversal. The other is from the disordered spins at the Co-CoO interface which exhibits spin-glass-like behavior. We investigated the oxide shell thickness dependence of the exchange bias effect. For particles with a 3 nm thick CoO shell, the predominant contribution to the temperature dependence of exchange bias is the interfacial spin-glass layer. On increasing the shell thickness to 4 nm, the contribution from the spin-glass layer decreases, while upholding the antiferromagnetic grain contribution. For samples with a 4 nm CoO shell, the exchange bias training was minimal. On the other hand, 3 nm samples exhibited both the training effect and a peak in coercivity at an intermediate set temperature Ta. This is explained using a magnetic core-shell model including disordered spins at the interface.