Corrosion Development of Carbon Steel Grids and Shear Connectors in Cracked Composite Beams Exposed to Wet–Dry Cycles in Chloride Environment

PubMed Central

Xue, Wen; Chen, Ju; Jiang, Ao-yu

2018-01-01

The corrosion development of the reinforcement and shear stud connectors in the cracked steel–concrete composite beams under the salt-fog wet–dry cycles is presented in this investigation. Seven identical composite beams with load-induced concrete cracks were exposed to an aggressive chloride environment. The reinforcement and shear connectors were retrieved after specimens underwent a specified number of wet–dry cycles to obtain the corrosion pattern and the cross-section loss at different exposure times and their evolutions. The crack map, the corrosion pattern and the cross-section loss were measured and presented. Based on the experimental results, the influence of crack characteristics, including crack widths, orientations and positions on the corrosion rate and distribution, were accessed. Moreover, the effects of the connecting weldments on the corrosion initiations and patterns were analyzed. It was shown that the corrosion rate would increase with the number of wet–dry cycles. The characteristics of load-induced cracks could have different influences on the steel grids and shear stud connectors. The corrosion tended to initiate from the connecting weldments, due to the potential difference with the parent steel and the aggressive exposure environment, leading to a preferential weldment attack. PMID:29565836

Fatigue Behavior of HY-130 Steel Weldments Containing Fabrication Discontinuities.

DTIC Science & Technology

1985-04-18

discontinuities to solutions for elliptical discontinuities. One such approach has been formalized in the ASME Section XI Boiler and Pressure Vessel Code [1... Boiler and Pressure Vessel Code , Section XI, "Rules for Inservice Inspection of Nuclear Reactor Coolant Systems," American Society of Mechanical

Apparatus for testing high pressure injector elements

NASA Technical Reports Server (NTRS)

Myers, William Neill (Inventor); Scott, Ewell M. (Inventor); Forbes, John C. (Inventor); Shadoan, Michael D. (Inventor)

1993-01-01

An apparatus for testing and evaluating the spray pattern of high pressure fuel injector elements for use in supplying fuel to combustion engines is presented. Prior art fuel injector elements were normally tested by use of low pressure apparatuses which did not provide a purge to prevent mist from obscuring the injector element or to prevent frosting of the view windows; could utilize only one fluid during each test; and had their viewing ports positioned one hundred eighty (180 deg) apart, thus preventing optimum use of laser diagnostics. The high pressure fluid injector test apparatus includes an upper hub, an upper weldment or housing, a first clamp and stud/nut assembly for securing the upper hub to the upper weldment, a standoff assembly within the upper weldment, a pair of window housings having view glasses within the upper weldment, an injector block assembly and purge plate within the upper weldment for holding an injector element to be tested and evaluated, a lower weldment or housing, a second clamp and stud/nut assembly for securing the lower weldment to the upper weldment, a lower hub, a third clamp and stud/nut assembly for securing the lower hub to the lower weldment, mechanisms for introducing fluid under high pressure for testing an injector element, and mechanisms for purging the apparatus to prevent frosting of view glasses within the window housings and to permit unobstructed viewing of the injector element.

Tritium Effects on Fracture Toughness of Stainless Steel Weldments

DOE Office of Scientific and Technical Information (OSTI.GOV)

MORGAN, MICHAEL; CHAPMAN, G. K.; TOSTEN, M. H.

2005-05-12

The effects of tritium on the fracture toughness properties of Type 304L and Type 21-6-9 stainless steel weldments were measured. Weldments were tritium-charged-and-aged and then tested in order to measure the effect of the increasing decay helium content on toughness. The results were compared to uncharged and hydrogen-charged samples. For unexposed weldments having 8-12 volume percent retained delta ferrite, fracture toughness was higher than base metal toughness. At higher levels of weld ferrite, the fracture toughness decreased to values below that of the base metal. Hydrogen-charged and tritium-charged weldments had lower toughness values than similarly charged base metals and toughnessmore » decreased further with increasing weld ferrite content. The effect of decay helium content was inconclusive because of tritium off-gassing losses during handling, storage and testing. Fracture modes were dominated by the dimpled rupture process in unexposed weldments. In hydrogen and tritium-exposed weldments, the fracture modes depended on the weld ferrite content. At high ferrite contents, hydrogen-induced transgranular fracture of the weld ferrite phase was observed.« less

Fundamental studies of hydrogen attack in carbon-0.5molybdenum steel and weldments applied in petroelum and petrochemical industries

NASA Astrophysics Data System (ADS)

Liu, Peng

High temperature hydrogen attack (HTHA) is a form of surface decarburization, internal decarburization, and/or intergranular cracking in steels exposed to high temperature (>400°F) and high hydrogen pressure. Hydrogen attack is an irreversible process which can cause permanent damage resulting in degradation of mechanical properties and failures such as leakage, bursting, fire, and/or explosion. The continuous progression of hydrogen attack in C-0.5Mo steel and weldments below the C-0.5Mo Nelson Curve has caused a significant concern for the integrity and serviceability of C-0.5Mo steel utilized for pressure vessels and piping in the petroleum refinery and petrochemical industries. A state-of-the-art literature review was implemented to provide a comprehensive overview of the published research efforts on hydrogen attack studies. The evolution of "Nelson Curves" for carbon steel, C-0.5Mo, and Cr-Mo steels was historically reviewed in regard to design applications and limitations. Testing techniques for hydrogen attack assessment were summarized under the categories of hydrogen exposure testing, mechanical evaluation, and dilatometric swelling testing. In accord with the demands of these industries, fundamental studies of hydrogen attack in C-0.5Mo steel and weldments were accomplished in terms of quantitative methodologies for hydrogen damage evaluation; hydrogen damage assessment of service exposed weldments and autoclave exposed materials; effects of carbon and alloying elements, heat treatments, hot and cold working, welding processes and postweld heat treatment (PWHT) on hydrogen attack susceptibility; development of continuous cooling transformation (CCT) diagrams for C-0.5Mo base metals and the coarse grained heat-affected zone (CGHAZ); carbide evaluation for the C-0.5Mo steel after service exposure and heat treatment; methane evolution by the reaction of hydrogen and carbides; hydrogen diffusion and methane pressure through the wall thickness of one-sided hydrogen exposure assembly; hydrogen attack mechanism and hydrogen attack limit modeling.

TRITIUM EFFECTS ON WELDMENT FRACTURE TOUGHNESS

DOE Office of Scientific and Technical Information (OSTI.GOV)

Morgan, M; Michael Tosten, M; Scott West, S

2006-07-17

The effects of tritium on the fracture toughness properties of Type 304L stainless steel and its weldments were measured. Fracture toughness data are needed for assessing tritium reservoir structural integrity. This report provides data from J-Integral fracture toughness tests on unexposed and tritium-exposed weldments. The effect of tritium on weldment toughness has not been measured until now. The data include tests on tritium-exposed weldments after aging for up to three years to measure the effect of increasing decay helium concentration on toughness. The results indicate that Type 304L stainless steel weldments have high fracture toughness and are resistant to tritiummore » aging effects on toughness. For unexposed alloys, weldment fracture toughness was higher than base metal toughness. Tritium-exposed-and-aged base metals and weldments had lower toughness values than unexposed ones but still retained good toughness properties. In both base metals and weldments there was an initial reduction in fracture toughness after tritium exposure but little change in fracture toughness values with increasing helium content in the range tested. Fracture modes occurred by the dimpled rupture process in unexposed and tritium-exposed steels and welds. This corroborates further the resistance of Type 304L steel to tritium embrittlement. This report fulfills the requirements for the FY06 Level 3 milestone, TSR15.3 ''Issue summary report for tritium reservoir material aging studies'' for the Enhanced Surveillance Campaign (ESC). The milestone was in support of ESC L2-1866 Milestone-''Complete an annual Enhanced Surveillance stockpile aging assessment report to support the annual assessment process''.« less

Apparatus for testing high pressure injector elements

NASA Technical Reports Server (NTRS)

Myers, William Neill (Inventor); Scott, Ewell M. (Inventor); Forbes, John C. (Inventor); Shadoan, Michael D. (Inventor)

1995-01-01

An apparatus for testing and evaluating the spray pattern of high pressure fuel injector elements for use in supplying fuel to combustion engines is presented. Prior art fuel injector elements were normally tested by use of low pressure apparatuses which did not provide a purge to prevent mist from obscuring the injector element or to prevent frosting of the view windows; could utilize only one fluid during each test; and had their viewing ports positioned one hundred eighty (180 deg) apart, thus preventing optimum use of laser diagnostics. The high pressure fluid injector test apparatus includes an upper hub, an upper weldment or housing, a first clamp and stud/nut assembly for securing the upper hub to the upper weldment, a standoff assembly within the upper weldment, a pair of window housings having view glasses within the upper weldment, an injector block assembly and purge plate within the upper weldment for holding an injector element to be tested and evaluated, a lower weldment or housing, a second clamp and stud/nut assembly for securing the lower weldment to the upper hub, a third clamp and stud/nut assembly for securing the lower hub to the lower weldment, mechanisms for introducing fluid under high pressure for testing an injector element, and mechanisms for purging the apparatus to prevent frosting of view glasses within the window housings and to permit unobstructed viewing of the injector element.

Effect of tritium and decay helium on the fracture toughness properties of stainless steel weldments

DOE Office of Scientific and Technical Information (OSTI.GOV)

Morgan, M. J.; West, S.; Tosten, M. H.

2008-07-15

J-Integral fracture toughness tests were conducted on tritium-exposed-and- aged Types 304L and 21-6-9 stainless steel weldments in order to measure the combined effects of tritium and its decay product, helium-3 on the fracture toughness properties. Initially, weldments have fracture toughness values about three times higher than base-metal values. Delta-ferrite phase in the weld microstructure improved toughness provided no tritium was present in the microstructure. After a tritium-exposure-and-aging treatment that resulted in {approx}1400 atomic parts per million (appm) dissolved tritium, both weldments and base metals had their fracture toughness values reduced to about the same level. The tritium effect was greatermore » in weldments (67 % reduction vs. 37% reduction) largely because the ductile discontinuous delta-ferrite phase was embrittled by tritium and decay helium. For both base metals and weldments, fracture toughness values decreased with increasing decay helium content in the range tested (50-800 appm). (authors)« less

TRITIUM AND DECAY HELIUM EFFECTS ON THE FRACTURE TOUGHNESS PROPERTIES OF STAINLESS STEEL WELDMENTS

DOE Office of Scientific and Technical Information (OSTI.GOV)

Morgan, M; Scott West, S; Michael Tosten, M

2007-08-31

J-Integral fracture toughness tests were conducted on tritium-exposed-and-aged Types 304L and 21-6-9 stainless steel weldments in order to measure the combined effects of tritium and its decay product, helium-3 on the fracture toughness properties. Initially, weldments have fracture toughness values about three times higher than base-metal values. Delta-ferrite phase in the weld microstructure improved toughness provided no tritium was present in the microstructure. After a tritium-exposure-and-aging treatment that resulted in {approx}1400 atomic parts per million (appm) dissolved tritium, both weldments and base metals had their fracture toughness values reduced to about the same level. The tritium effect was greater inmore » weldments (67 % reduction vs. 37% reduction) largely because the ductile discontinuous delta-ferrite interfaces were embrittled by tritium and decay helium. Fracture toughness values decreased for both base metals and weldments with increasing decay helium content in the range tested (50-200 appm).« less

Process for treating weldments

DOEpatents

Malik, R.K.

The tensile ducttility and impact strength of weldments of nickel-based and stainless steel alloys are improved to that of the unaffected base metal by subjecting the weldments to an elevated temperature at an isostatic pressure for a period of time sufficient to render the material in the weld more homogeneous.

Ballistic-Failure Mechanisms in Gas Metal Arc Welds of MIL A46100 Armor-Grade Steel: A Computational Investigation

DTIC Science & Technology

2014-06-12

distribution is unlimited. Ballistic-Failure Mechanisms in Gas Metal Arc Welds of Mil A46100 Armor-Grade Steel : A Computational Investigation The views...Welds of Mil A46100 Armor-Grade Steel : A Computational Investigation Report Title In our recent work, a multi-physics computational model for the...introduction of the sixth module in the present work in recognition of the fact that in thick steel GMAW weldments, the overall ballistic performance

Resistance Spot Welding of AA5052 Sheet Metal of Dissimilar Thickness

NASA Astrophysics Data System (ADS)

Mat Din, N. A.; Zuhailawati, H.; Anasyida, A. S.

2016-02-01

Resistance spot welding of dissimilar thickness of AA5052 aluminum alloy was performed in order to investigate the effect of metal thickness on the weldment strength. Resistance spot welding was done using a spot welder machine available in Coraza Systems Sdn Bhd using a hemispherical of chromium copper electrode tip with radius of 6.00 mm under 14 kA of current and 0.02 bar of pressure for all thickness combinations. Lap joint configuration was produced between 2.0 mm thick sheet and 1.2 - 3.2 mm thick sheet, respectively. Microstructure of joint showed asymmetrical nugget shape that was larger on the thicker side indicating larger molten metal volume. Joint 2.0 mm x 3.2 mm sheets has the lowest hardness in both transverse direction and through thickness direction because less heat left in the weld nugget. The microstructure shows that this joint has coarse grains of HAZ. As thickness of sheet metal increased, the failure load of the joints increased. However, there was no linear correlation established between joint strength and metal thickness due to different shape of fusion zone in dissimilar thickness sheet metal.

16 CFR Figure 2 to Subpart A of... - Cyclone Receiver Weldment

Code of Federal Regulations, 2010 CFR

2010-01-01

... 16 Commercial Practices 2 2010-01-01 2010-01-01 false Cyclone Receiver Weldment 2 Figure 2 to Subpart A of Part 1209 Commercial Practices CONSUMER PRODUCT SAFETY COMMISSION CONSUMER PRODUCT SAFETY ACT... to Subpart A of Part 1209—Cyclone Receiver Weldment EC03OC91.032 ...

16 CFR Figure 2 to Subpart A of... - Cyclone Receiver Weldment

Code of Federal Regulations, 2011 CFR

2011-01-01

... 16 Commercial Practices 2 2011-01-01 2011-01-01 false Cyclone Receiver Weldment 2 Figure 2 to Subpart A of Part 1209 Commercial Practices CONSUMER PRODUCT SAFETY COMMISSION CONSUMER PRODUCT SAFETY ACT... to Subpart A of Part 1209—Cyclone Receiver Weldment EC03OC91.032 ...

Microstructure and Corrosion Behavior of Laser Melted 304L SS Weldment in Nitric Acid Medium

NASA Astrophysics Data System (ADS)

Suresh, Girija; Kishor, P. S. V. R. A.; Dasgupta, Arup; Upadhyay, B. N.; Mallika, C.; Kamachi Mudali, U.

2017-02-01

The manuscript presents the effect of laser surface melting on the corrosion property of 304L SS weldment in nitric acid medium. 304L SS weldment was prepared by gas tungsten arc welding process and subsequently laser surface melted using Nd:YAG laser. The microstructure and corrosion resistance of laser surface melted 304L SS weldment was evaluated and compared with that of 304L SS as-weldment and 304L SS base. Microstructural evaluation was carried out using optical and scanning electron microscopes attached with energy-dispersive x-ray spectroscopy. Corrosion investigations were carried out in 4 and 8 M nitric acid by potentiodynamic polarization technique. From the results, it was found that laser surface melting of the weldment led to chemical and microstructural homogeneities, accompanied by a substantial decrease in delta ferrite content, that enhanced the corrosion resistance of the weldment in 4 and 8 M nitric acid. However, the enhancement in the corrosion resistance was not substantial. The presence of small amount of delta ferrite (2-4 wt.%) in the laser surface melted specimens was found to be detrimental in nitric acid. X-ray photoelectron spectroscopy studies were carried out to investigate the composition of the passive film.

Creep rupture testing of alloy 617 and A508/533 base metals and weldments.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Natesan, K.; Li, M.; Soppet, W.K.

2012-01-17

The NGNP, which is an advanced HTGR concept with emphasis on both electricity and hydrogen production, involves helium as the coolant and a closed-cycle gas turbine for power generation with a core outlet/gas turbine inlet temperature of 750-1000 C. Alloy 617 is a prime candidate for VHTR structural components such as reactor internals, piping, and heat exchangers in view of its resistance to oxidation and elevated temperature strength. However, lack of adequate data on the performance of the alloy in welded condition prompted to initiate a creep test program at Argonne National Laboratory. In addition, Testing has been initiated tomore » evaluate the creep rupture properties of the pressure vessel steel A508/533 in air and in helium environments. The program, which began in December 2009, was certified for quality assurance NQA-1 requirements during January and February 2010. Specimens were designed and fabricated during March and the tests were initiated in April 2010. During the past year, several creep tests were conducted in air on Alloy 617 base metal and weldment specimens at temperatures of 750, 850, and 950 C. Idaho National Laboratory, using gas tungsten arc welding method with Alloy 617 weld wire, fabricated the weldment specimens. Eight tests were conducted on Alloy 617 base metal specimens and nine were on Alloy 617 weldments. The creep rupture times for the base alloy and weldment tests were up to {approx}3900 and {approx}4500 h, respectively. The results showed that the creep rupture lives of weld specimens are much longer than those for the base alloy, when tested under identical test conditions. The test results also showed that the creep strain at fracture is in the range of 7-18% for weldment samples and were much lower than those for the base alloy, under similar test conditions. In general, the weldment specimens showed more of a flat or constant creep rate region than the base metal specimens. The base alloy and the weldment exhibited tertiary creep after 50-60% of the rupture life, irrespective of test temperature in the range of 750-950 C. The results showed that the stress dependence of the creep rate followed a power law for both base alloy and weldments. The data also showed that the stress exponent for creep is the same and one can infer that the same mechanism is operative in both base metal and weldments in the temperature range of the current study. SEM fractography analysis indicated that both base metal and weldment showed combined fracture modes consisting of dimple rupture and intergranular cracking. Intergranular cracking was more evident in the weldment specimens, which is consistent with the observation of lower creep ductility in the weldment than in the base metal.« less

Microstructure characterization and charpy toughness of P91 weldment for as-welded, post-weld heat treatment and normalizing & tempering heat treatment

NASA Astrophysics Data System (ADS)

Pandey, Chandan; Mahapatra, M. M.; Kumar, Pradeep; Giri, A.

2017-09-01

The effect of weld groove design and heat treatment on microstructure evolution and Charpy toughness of P91 pipe weldments was studied. The P91 pipe weldments were subjected to subcritical post weld heat treatment (760 °C-2 h) and normalizing/tempering conditions (normalized-1040 °C/40 min, air cooled; tempered 760 °C/2 h, air cooled) were employed. The influence of subsequent PWHT and N&T treatment on the microstructure of various zone of P91 pipe weldments were also investigated. The present investigation also described the effect of PWHT and N&T treatment on hardness, grain size, precipitate size, inter-particle spacing and fraction area of precipitates present in each zone of P91 pipe weldments. The result indicated great impact of heat treatment on the Charpy toughness and microstructure evolution of P91 weldments. The N&T treatment was found to be more effective heat treatment compared to subsequent PWHT. Charpy toughness value was found to be higher for narrow-groove design as compared to conventional V-groove design.

FINAL DESIGN REVIEW REPORT Subcritical Experiments Gen 2, 3-ft Confinement Vessel Weldment

DOE Office of Scientific and Technical Information (OSTI.GOV)

Romero, Christopher

A Final Design Review (FDR) of the Subcritical Experiments (SCE) Gen 2, 3-ft. Confinement Vessel Weldment was held at Los Alamos National Laboratory (LANL) on September 14, 2017. The review was a focused review on changes only to the confinement vessel weldment (versus a system design review). The changes resulted from lessons-learned in fabricating and inspecting the current set of confinement vessels used for the SCE Program. The baseline 3-ft. confinement vessel weldment design has successfully been used (to date) for three (3) high explosive (HE) over-tests, two (2) fragment tests, and five (5) integral HE experiments. The design teammore » applied lessons learned from fabrication and inspection of these vessel weldments to enhance fit-up, weldability, inspection, and fitness for service evaluations. The review team consisted of five (5) independent subject matter experts with engineering design, analysis, testing, fabrication, and inspection experience. The« less

Improved TIG weld joint strength in aluminum alloy 2219-T87 by filler metal substitution

NASA Technical Reports Server (NTRS)

Poorman, R. M.; Lovoy, C. V.

1972-01-01

The results of an investigation on weld joint characteristics of aluminum alloy 2219-T87 are given. Five different alloys were utilized as filler material. The mechanical properties of the joints were determined at ambient and cryogenic temperatures for weldments in the as-welded condition and also, for weldments after elevated temperature exposures. Other evaluations included hardness surveys, stress corrosion susceptibility, and to a limited extent, the internal metallurgical weld structures. The overall results indicate that M-943 filler weldments are superior in strength to weldments containing either the standard 2319 filler or fillers 2014, 2020, and a dual wire feed consisting of three parts 2319 and one part 5652. In addition, no deficiencies were evident in M-934 filler weldments with regard to ductility, joint strength after elevated temperature exposure, weld hardness, metallographic structures, or stress corrosion susceptibility.

Use of photostress to characterize the mechanical behavior of weldments

NASA Technical Reports Server (NTRS)

Gambrell, S. C., Jr.

1992-01-01

Welded aluminum is an important part of many space structures. Knowledge of the properties and behavior of weld material and the material surrounding the weld is important for modeling and design of the structures. Photoelastic coatings (Photostress) and strain gages were used to determine behavior of heat treated and as welded joints made from 2219T87 parent material and 2319 weld material subjected to tensile loads. TIG welds of 1/8, 1/2, and 1.4 inches thickness were investigated. Discontinuous yielding was observed in all tests and highly non-uniform behavior through the weld thickness was observed in joints having welds 1.4 inches thick. Joints having welds 1/8 and 1/2 inches thick had only small differences in behavior through the thickness of the weld. Joints in the 1/2 inch thick material contained distinct zones of constant strain within the normal strain gradient extending outward from the weld centerline. These zones had different thickness and locations. Points at the weld centerline, and for a distance of nearly one inch from the centerline, exhibited very nonlinear behavior during the first loading but exhibited near perfect strain hardening during the second loading.

Fabricating niobium test loops for the SP-100 space reactor

NASA Technical Reports Server (NTRS)

Bryhan, Anthony J.; Chan, Ricky C.

1993-01-01

This article describes the successful fabrication, operation, and evaluation of a series of niobium-alloy (Nb-1 Zr and PWC-11) thermal convection loops designed to contain and circulate molten lithium at 1,350 K. These loops were used to establish the fabrication variables of significance for a nuclear power supply for space. Approximately 200 weldments were evaluated for their tendency to be attacked by lithium as a function of varying atmospheric contamination. No attack occurred for any weldment free of contamination, with or without heat treatment, and no welds accidentally deviated from purity. The threshold oxygen content for weldment attack was determined to be 170-200 ppm. Attack varied directly with weldment oxygen and nitrogen contents.

Metallurgy and deformation of electron beam welded similar titanium alloys

NASA Astrophysics Data System (ADS)

Pasang, T.; Sabol, J. C.; Misiolek, W. Z.; Mitchell, R.; Short, A. B.; Littlefair, G.

2012-04-01

Butt welded joins were produced between commercially pure titanium and various titanium alloys using an electron beam welding technique. The materials used represent commercially pure grade, α-β alloy and β alloy. They were CP Ti, Ti-6Al-4V (Ti64) and Ti-5Al-5V-5Mo-3Cr (Ti5553), respectively. Grains were largest in the FZs of the different weldments, decreasing in size towards the heat affected zones (HAZs) and base metals. Hardness measurements taken across the traverse cross-sections of the weldments were constant from base metal-to-weld-to-base metal for CP Ti/CP Ti and Ti64/Ti64 welds, while the FZ of Ti5553/Ti5553 had a lower hardness compared with the base metal. During tensile testing the CP Ti/CP Ti weldments fractured at the base metal, whereas both the Ti64/Ti64 and Ti5553/Ti5553 broke at the weld zones. Fracture surface analysis suggested microvoid coalescence as the failure mechanism. The compositional analysis showed a relatively uniform distribution of solute elements from base metal-to-weld-to-base metal. CP Ti has always been known for its excellent weldability, Ti64 has good weldability and, preliminary results indicated that Ti5553 alloy is also weldable.

Investigations on Microstructure and Corrosion behavior of Superalloy 686 weldments by Electrochemical Corrosion Technique

NASA Astrophysics Data System (ADS)

Arulmurugan, B.; Manikandan, M.

2018-02-01

In the present study, microstructure and the corrosion behavior of Nickel based superalloy 686 and its weld joints has been investigated by synthetic sea water environment. The weldments were fabricated by Gas Tungsten Arc Welding (GTAW) and Pulsed Current Gas Tungsten Arc Welding (PCGTAW) techniques with autogenous mode and three different filler wires (ERNiCrMo-4, ERNiCrMo-10 and ERNiCrMo-14). Microstructure and Scanning electron microscope examination was carried out to evaluate the structural changes in the fusion zones of different weldments. Energy Dispersive X-ray Spectroscopy (EDS) analysis was carried out to evaluate the microsegregation of alloying elements in the different weld joints. Potentiodynamic polarization study was experimented on the base metal and weld joints in the synthetic sea water environment to evaluate the corrosion rate. Tafel’s interpolation technique was used to obtain the corrosion rate. The microstructure examination revealed that the fine equiaxed dendrites were observed in the pulsed current mode. EDS analysis shows the absence of microsegregation in the current pulsing technique. The corrosion rates of weldments are compared with the base metal. The results show that the fine microstructure with the absence of microsegregation in the PCGTA weldments shows improved corrosion resistance compared to the GTAW. Autogenous PCGTAW shows higher corrosion resistance irrespective of all weldments employed in the present study.

Atmosphere

NASA Astrophysics Data System (ADS)

Ghosh, D.; Mitra, S. K.

2014-05-01

This paper investigates the high-temperature corrosion behavior of microstructurally different regions of the weldment of 9 Cr-1 Mo steel used in thermal power plant boiler in SO2 + O2 environment. The weldment is produced by tungsten inert gas welding method, and the different regions of the weldment (weld metal, heat-affected zone, and base metal) are exposed in SO2 + O2 (ratio 2:1) environment at 973 K for 120 h. The reaction kinetics and corrosion growth rate of different regions of weldment in isothermal condition are evaluated. The post corroded scales of the different specimens are studied in SEM, EDS, and XRD. The results indicate that the weld metal shows higher corrosion rate followed by HAZ and base metal. The higher rate of corrosion of weldmetal is mainly attributed to the least protective inner scale of Cr2O3 with minimum Cr Content. This is due to the formation of delta ferrite, which leads to the precipitation of the Cr-based secondary phases and depletes the free Cr from the matrix. The thermal cycles during welding at high temperature are favorable for the formation of delta ferrite. On the other hand, in absence of delta ferrite, the base metal and HAZ regions of the weldment show lower corrosion rate than weld metal. The difference in corrosion rate in the three regions of the weldment is supplemented by post-corroded scale characterizations.

The Effect of Weld Metal Strength Mismatch on the Deformation and Fracture Behavior of Steel Butt Weldments

DTIC Science & Technology

1991-01-01

Society 6 of Mechanical Engineers (ASME) Boiler and Pressure Vessel Code [ 1980]. Their results are similar to those of Satoh and Toyoda, and are...E813-89. American Society of Mechanical Engineers, Boiler and Pressure Vessel Code , Section III, Nuclear Power Plant Components, 1980. American

The structural significance of HAZ sigma phase formation in welded 25%Cr super duplex pipework

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wiesner, C.S.; Garwood, S.J.; Bowden, P.L.

1993-12-31

The welding of 25%Cr duplex stainless steel can lead to the formation of sigma phase in both weld metal and heat affected zone (HAZ) regions. It has generally been accepted that this can be avoided by the adoption of appropriate welding procedure controls, generally aimed at reducing heat input and promoting rapid cooling rates. However, experience during pipe spool fabrication for the Marathon East Brae Project has shown that it is extremely difficult to satisfy a welding specification requiring sigma free HAZs. This has proved a particular problem with thin wall pipe welds made in the 2G/5G or 6G fixedmore » positions, where the joint geometry reduces heat flow away from the weld and welding conditions tend to result in the use of higher heat inputs. This paper examines the effect of sigma phase on the fracture toughness of 25%Cr super duplex steel (UNS S32760). It is shown that the CTOD toughness at {minus}20 C decreases as soon as any sigma phase is present and continues to decrease with increasing sigma levels. The toughness of the sigmatized specimens produced by heat treatment was shown to be conservative compared to the toughness measured in the HAZ of 14.2mm and 7.1mm thick pipe weldments, made with welding parameters chosen to enhance HAZ sigma phase formation. Based on the CTOD versus percent sigma level relationship derived from the laboratory specimens, fracture assessment calculations of tolerable flaw sizes were performed. These demonstrated that under the severest design conditions, assuming the maximum flaw sizes which could remain undetected in the pipework, sigma levels up to 2.5% can be tolerated safely. The conservatism of the fracture assessments for predicting the performance of weldments was demonstrated by full scale tensile testing of 2 inch nominal bore x 2.77 mm wall thickness pipe butt welds containing through-thickness circumferential fatigue cracks located in the sigmatized HAZ.« less

Radiation Tolerance of Controlled Fusion Welds in High Temperature Oxidation Resistant FeCrAl Alloys

DOE Office of Scientific and Technical Information (OSTI.GOV)

Gussev, Maxim N.; Field, Kevin G.

High temperature oxidation resistant iron-chromium-aluminum (FeCrAl) alloys are candidate alloys for nuclear applications due to their exceptional performance during off-normal conditions such as a loss-of-coolant accident (LOCA) compared to currently deployed zirconium-based claddings [1]. A series of studies have been completed to determine the weldability of the FeCrAl alloy class and investigate the weldment performance in the as-received (non-irradiated) state [2,3]. These initial studies have shown the general effects of composition and microstructure on the weldability of FeCrAl alloys. Given this, limited details on the radiation tolerance of FeCrAl alloys and their weldments exist. Here, the highest priority candidate FeCrAlmore » alloys and their weldments have been investigated after irradiation to enable a better understanding of FeCrAl alloy weldment performance within a high-intensity neutron field. The alloys examined include C35M (Fe-13%Cr-5% Al) and variants with aluminum (+2%) or titanium carbide (+1%) additions. Two different sub-sized tensile geometries, SS-J type and SS-2E (or SS-mini), were neutron irradiated in the High Flux Isotope Reactor to 1.8-1.9 displacements per atom (dpa) in the temperature range of 195°C to 559°C. Post irradiation examination of the candidate alloys was completed and included uniaxial tensile tests coupled with digital image correlation (DIC), scanning electron microscopy-electron back scattered diffraction analysis (SEM-EBSD), and SEM-based fractography. In addition to weldment testing, non-welded parent material was examined as a direct comparison between welded and non-welded specimen performance. Both welded and non-welded specimens showed a high degree of radiation-induced hardening near irradiation temperatures of 200°C, moderate radiation-induced hardening near temperatures of 360°C, and almost no radiation-induced hardening at elevated temperatures near 550°C. Additionally, low-temperature irradiations showed the non-welded specimens to exhibit strain-induced softening (decrease in the true stress level) with increasing plastic strain during tensile testing. Fracture for the weldments was found to occur exclusively within the fusion zone. The mechanical performance of the weldment was speculated to be directly linked to variances in the radiation-induced microstructure including the formation of dislocation loops and precipitation of the Cr-rich α' phase. The localized microstructural variation within the weldments, including grain size, was determined to play a significant role in the radiation-induced microstructure. The results summarized within highlight the need for additional data on the radiation tolerance of weldments as the mechanical performance of the fusion zone was shown to be the limiting factor in the overall performance of the weldments.« less

Optimization and Prediction of Angular Distortion and Weldment Characteristics of TIG Square Butt Joints

NASA Astrophysics Data System (ADS)

Narang, H. K.; Mahapatra, M. M.; Jha, P. K.; Biswas, P.

2014-05-01

Autogenous arc welds with minimum upper weld bead depression and lower weld bead bulging are desired as such welds do not require a second welding pass for filling up the upper bead depressions (UBDs) and characterized with minimum angular distortion. The present paper describes optimization and prediction of angular distortion and weldment characteristics such as upper weld bead depression and lower weld bead bulging of TIG-welded structural steel square butt joints. Full factorial design of experiment was utilized for selecting the combinations of welding process parameter to produce the square butts. A mathematical model was developed to establish the relationship between TIG welding process parameters and responses such as upper bead width, lower bead width, UBD, lower bead height (bulging), weld cross-sectional area, and angular distortions. The optimal welding condition to minimize UBD and lower bead bulging of the TIG butt joints was identified.

Effects of Cluster Porosity on the Tensile Properties of Butt-Weldments in T-1 Steel

DTIC Science & Technology

1974-11-01

i 12 Boiler and Pressure Vessel Code .19 In this code, the algebraic difference between the largest and smallest principal stresses is defined...Report U1LU- HN(J 7l-2()24 (University ot Illinois. 1971). "Nuclear Power Components.’* ASME Boiler and Pressure Vessel Code . Section HI. Subsections

Electron beam weld development on a Filter Pack Assembly

NASA Astrophysics Data System (ADS)

Dereskiewicz, J. P.

1994-06-01

A continuous electron beam welding procedure was developed to replace the manual gas tungsten arc welding procedure on the Filter Pack Assembly. A statistical study was used to evaluate the feasibility of electron beam welding 6061-T6 aluminum covers to A356 cast weldments throughout the joint tolerance range specified on product drawings. Peak temperature exposures were not high enough to degrade the heat sensitive electrical components inside the cast weldment. Actual weldments with alodine coating on the weld joint area were successfully cleaned using a nonmetallic fiberglass brush cleaning method.

Subtask 12B1: Welding development for V-Cr-Ti alloys

DOE Office of Scientific and Technical Information (OSTI.GOV)

King, J.F.; Goodwin, G.M.; Grossbeck, M.L.

1995-03-01

Development of the metallurgical and technological basis for the welding of thick sections of V-Cr-Ti alloys. The weldability and weldment properties of the V-5Cr-5Ti alloy have been evaluated. Results for the Sigmajig test of the vanadium alloy were similar to the cracking resistance of stainless steels, and indicates hot-cracking is unlikely to be a problem. Subsize Charpy test results for GTA weld metal in the as-welded condition have shown a significant reduction in toughness compared to the base metal. The weld metal toughness properties were restored to approximately that of the base metal after exposure to a PWHT 950{degrees}C. Themore » subsize Charpy toughness results for the EB weld metal from this same heat of vanadium alloy has shown significant improvement in properties compared to the GTA weld metal and the base metal. Further testing and analysis will be conducted to more fully characterize the properties of weld metal for each welding process and develop a basic understanding of the cause of the toughness decrease in the GTA welds. 5 figs., 1 tab.« less

Deformation During Friction Stir Welding

NASA Technical Reports Server (NTRS)

White, Henry J.

2002-01-01

Friction Stir Welding (FSW) is a solid state welding process that exhibits characteristics similar to traditional metal cutting processes. The plastic deformation that occurs during friction stir welding is due to the superposition of three flow fields: a primary rotation of a radially symmetric solid plug of metal surrounding the pin tool, a secondary uniform translation, and a tertiary ring vortex flow (smoke rings) surrounding the tool. If the metal sticks to the tool, the plug surface extends down into the metal from the outer edge of the tool shoulder, decreases in diameter like a funnel, and closes up beneath the pin. Since its invention, ten years have gone by and still very little is known about the physics of the friction stir welding process. In this experiment, an H13 steel weld tool (shoulder diameter, 0.797 in; pin diameter, 0.312 in; and pin length, 0.2506 in) was used to weld three 0.255 in thick plates. The deformation behavior during friction stir welding was investigated by metallographically preparing a plan view sections of the weldment and taking Vickers hardness test in the key-hole region.

Corrosion of 2205 Duplex Stainless Steel Weldment in Chloride Medium Containing Sulfate-Reducing Bacteria

NASA Astrophysics Data System (ADS)

Antony, P. J.; Singh Raman, R. K.; Kumar, Pradeep; Raman, R.

2008-11-01

Influence of changes in microstructure caused due to welding on microbiologically influenced corrosion of a duplex stainless steel was studied by exposing the weldment and parent metal to chloride medium containing sulfate-reducing bacteria (SRB). Identically prepared coupons (same area and surface finish) exposed to sterile medium were used as the control. Etching-type attack was observed in the presence of SRB, which was predominant in the heat-affected zone (HAZ) of the weldment. The anodic polarization studies indicated an increase in current density for coupon exposed to SRB-containing medium as compared to that obtained for coupon exposed to sterile medium. The scanning electron microscopy (SEM) observations after anodic polarization revealed that the attack was preferentially in the ferrite phase of HAZ of the weldment, whereas it was restricted to the austenite phase of the parent metal.

Significance of reheat cracks to the integrity of pressure vessels for light-water reactors

DOE Office of Scientific and Technical Information (OSTI.GOV)

Canonico, D.A.

1979-05-01

Reheat cracks manifest themselves as macroscopic defects detectable by nondestructive testing (NDT) procedures or as microscopic grain boundary decohesions (GBD) that are beyond the limit of detection by NDT. The significance of the microscopic cracks that may go undetected are discussed. The probability that GBD exist in the heat-affected zones (HAZ) of weldments of pressure vessel steels is high; particularly in SA508 Class 2 weldments. GBD reside in the coarse-grained region of the HAZ. The microstructure of this region tends to be a tempered martensite or lower bainite, a structure whose fracture toughness is superior to that of a highermore » temperature transformation product. This region should be less sensitive to irradiation embrittlement. Toughness data for this region in either the unirradiated or irradiated condition are sparse; however, those data that are available indicate that this area is superior in toughness to the base metal. A sample of the HAZ from the prolongation-weldment from the Heavy Section Steel Technology program Intermediate Test Vessel (ITV) No. 4 was examined by the Staatliche Materialpruefungsanstalt (MPA). They reported GBD 5 mm (0.2 in.) long. This prompted an examination of the HAZ from the ITV vessel that had been tested to failure at 24 C (75 F). During testing, the region of the weld which contained the flaw that initiated the failure was strained up to 0.5%. A metallographic examination of this region of the weldment revealed GBD, but none of the size reported by the MPA. Further, there was no evidence that the GBD had extended as a consequence of the tests. Fracture toughness tests were made of the HAZ of welds from ITV-4. The electron-beam welding procedure, which permits more accurate siting of the crack, was used. Fracture toughness values in excess of 220 MPa/m (200 ksi/in.) were obtained at -18 C (O F).« less

EFFECT OF TRITIUM AND DECAY HELIUM ON WELDMENT FRACTURE TOUGHNESS

DOE Office of Scientific and Technical Information (OSTI.GOV)

Morgan, M; Scott West, S; Michael Tosten, M

2006-09-26

The fracture toughness data collected in this study are needed to assess the long-term effects of tritium and its decay product on tritium reservoirs. The results show that tritium and decay helium have negative effects on the fracture toughness properties of stainless steel and its weldments. The data and report from this study has been included in a material property database for use in tritium reservoir modeling efforts like the Technology Investment Program ''Lifecycle Engineering for Tritium Reservoirs''. A number of conclusions can be drawn from the data: (1) For unexposed Type 304L stainless steel, the fracture toughness of weldmentsmore » was two to three times higher than the base metal toughness. (2) Tritium exposure lowered the fracture toughness properties of both base metals and weldments. This was characterized by lower J{sub Q} values and lower J-da curves. (3) Tritium-exposed-and-aged base metals and weldments had lower fracture toughness values than unexposed ones but still retained good toughness properties.« less

On dissimilar metal welding of AISI4140 and AISI410 by GTAW

NASA Astrophysics Data System (ADS)

Velu, M.; Dixit, Shantanu; Choure, Shubham

2017-11-01

This paper presents the results of metallurgical and mechanical examinations of Gas Tungsten Arc Welding of dissimilar steels AISI4140 and AISI410. Two different filler materials viz., ERNiCr3 and SS410 were used. The various properties of the weldments made using the fillers were compared to select the most appropriate one to get the sound joint. The ultimate tensile and yield strengths of the weldments of SS410 were greater than those of ERNiCr3. The fracture occurred at the weld in weldments made with ERNiCr3, whereas, in the base metal of AISI410 for weldments made with SS410. Microstructure of fusion zone of ERNiCr3 was fully austenitic. Microhardness values in the weld of SS410 were higher and fluctuating compared to those in the weld of ERNiCr3. From this research work, it shall be concluded that SS410 is the best filler material to weld these base materials.

Detection of lack of fusion using opaque additives

NASA Technical Reports Server (NTRS)

Cook, J. L.

1973-01-01

Reliable nondestructive inspection for incomplete weldment penetration and rapid oxidation of aluminum surfaces when exposed to the atmosphere are currently two major problems in welded aluminum spacecraft structure. Incomplete-penetration defects are extremely difficult to detect and can lead to catastrophic failure of the structure. The moisture absorbed by aluminum oxide on the surface can cause weldment porosity if the surface is not cleaned before welding. The approach employed in this program to solve both problems was to employ copper as a coating to prevent oxidation of the aluminum. Also, copper was used as an opaque additive in the weldment to enhance X-ray detection in the event of incomplete penetration.

The application of statistically designed experiments to resistance spot welding

NASA Technical Reports Server (NTRS)

Hafley, Robert A.; Hales, Stephen J.

1991-01-01

State-of-the-art Resistance Spot Welding (RSW) equipment has the potential to permit realtime monitoring of operations through advances in computerized process control. In order to realize adaptive feedback capabilities, it is necessary to establish correlations among process variables, welder outputs, and weldment properties. The initial step toward achieving this goal must involve assessment of the effect of specific process inputs and the interactions among these variables on spot weld characteristics. This investigation evaluated these effects through the application of a statistically designed experiment to the RSW process. A half-factorial, Taguchi L sub 16 design was used to understand and refine a RSW schedule developed for welding dissimilar aluminum-lithium alloys of different thickness. The baseline schedule had been established previously by traditional trial and error methods based on engineering judgment and one-factor-at-a-time studies. A hierarchy of inputs with respect to each other was established, and the significance of these inputs with respect to experimental noise was determined. Useful insight was gained into the effect of interactions among process variables, particularly with respect to weldment defects. The effects of equipment related changes associated with disassembly and recalibration were also identified. In spite of an apparent decrease in equipment performance, a significant improvement in the maximum strength for defect-free welds compared to the baseline schedule was achieved.

Mechanical properties of weldments in experimental Fe-12Mn-0.2Ti and Fe-12Mn-1Mo-0.2Ti alloys for cryogenic service

NASA Technical Reports Server (NTRS)

Stephens, J. R.; Witzke, W. R.; Devletian, J. H.

1981-01-01

Mechanical properties of weldments in two Fe-12Mn experimental alloys designed for cryogenic service were evaluated. Weldments were made using the GTA welding process. Tests to evaluate the weldments were conducted at -196 C and included: equivalent energy fracture toughness tests; autogenous transverse weld, notched transverse weld, and longitudinal weld tensile tests; and all-weld-metal tensile tests. The Fe-12Mn-0.2Ti and Fe-12Mn-1Mo-0.2Ti alloys proved weldable for cryogenic service, with weld metal and heat-affected zone properties comparable with those of the base metal. Optimum properties were achieved in the base alloys, weld metals, and heat-affected zones after a two-step heat treatment consisting of austenitizing at 900 C followed by tempering at 500 C. The Mo-containing alloy offered a marked improvement in cryogenic properties over those of the Mo-free alloy. Molybdenum increased the amount of retained austenite and reduced the amount of epsilon martensite observed in the microstructure of the two alloys.

2017 Accomplishments – Tritium Aging Studies on Stainless Steel Weldments and Heat-Affected Zones

DOE Office of Scientific and Technical Information (OSTI.GOV)

Morgan, Michael J.; Hitchcock, Dale; Krentz, Tim

In this study, the combined effects tritium and decay helium in forged and welded Types 304L and 21-6-9 stainless steels were studied. To measure these effects, fracture mechanic specimens were thermally precharged with tritium and aged for approximately 17 years to build in decay helium from tritium decay prior to testing. The results are compared to earlier measurements on the same alloys and weldments (4-5, 8-9). In support of Enhanced Surveillance, “Tritium Effects on Materials”, the fracture toughness properties of long-aged tritium-charged stainless-steel base metals and weldments were measured and compared to earlier measurements. The fracture-toughness data were measured bymore » thermally precharging as-forged and as-welded specimens with tritium gas at 34.5 MPa and 350°C and aging for approximately 17 years to build-in decay helium prior to testing. These data result from the longest aged specimens ever tested in the history of the tritium effects programs at Savannah River and the fracture toughness values measured were the lowest ever recorded for tritium-exposed stainless steel. For Type 21-6-9 stainless steel, fracture toughness values were reduced to less than 2-4% of the as-forged values to 41 lbs / in specimens that contained more than 1300 appm helium from tritium decay. The fracture toughness properties of long-aged weldments were also measured. The fracture toughness reductions were not as severe because the specimens did not retain as much tritium from the charging and aging as did the base metals. For Type 304L weldments, the specimens in this study contained approximately 600 appm helium and their fracture toughness values averaged 750 lbs / in. The results for other steels and weldments are reported and additional tests will be conducted during FY18.« less

Comparison between instrumented precracked Charpy and compact specimen tests of carbon steels

DOE Office of Scientific and Technical Information (OSTI.GOV)

Nanstad, R.K.

1980-01-01

The General Atomic Company High Temperature Gas-Cooled Reactor (HTGR) is housed within a prestressed concrete reactor vessel (PCRV). Various carbon steel structural members serve as closures at penetrations in the vessel. A program of testing and evaluation is underway to determine the need for reference fracture toughness (K/sub IR/) and indexing procedures for these materials as described in Appendix G to Section III, ASME Code for light water reactor steels. The materials of interest are carbon steel forgings (SA508, Class 1) and plates (SA537, Classes 1 and 2) as well as weldments of these steels. The fracture toughness behavior ismore » characterized with instrumented precracked Charpy V-votch specimens (PCVN) - slow-bend and dynamic - and compact specimens (10-mm and 25-mm thicknesses) using both linear elastic (ASTM E399) and elastic-plastic (equivalent Energy and J-Integral) analytical procedures. For the dynamic PCVN tests, force-time traces are analyzed according to the procedures of the Pressure Vessel Research Council (PVRC)/Metal Properties Council (MPC). Testing and analytical procedures are discussed and PCVN results are compared to those obtained with compact specimens.« less

Glass Coats For Hot Isostatic Pressing

NASA Technical Reports Server (NTRS)

Ecer, Gunes M.

1989-01-01

Surface voids sealed from pressurizing gas. Coating technique enables healing of surface defects by hot isostatic pressing (HIP). Internal pores readily closed by HIP, but surface voids like cracks and pores in contact with pressurizing gas not healed. Applied to casting or weldment as thick slurry of two glass powders: one melts at temperature slightly lower than used for HIP, and another melts at higher temperature. For example, powder is glass of 75 percent SiO2 and 25 percent Na2O, while other powder SiO2. Liquid component of slurry fugitive organic binder; for example, mixture of cellulose acetate and acetone. Easy to apply, separates voids from surrounding gas, would not react with metal part under treatment, and easy to remove after pressing.

Computer automation of ultrasonic testing. [inspection of ultrasonic welding

NASA Technical Reports Server (NTRS)

Yee, B. G. W.; Kerlin, E. E.; Gardner, A. H.; Dunmyer, D.; Wells, T. G.; Robinson, A. R.; Kunselman, J. S.; Walker, T. C.

1974-01-01

Report describes a prototype computer-automated ultrasonic system developed for the inspection of weldments. This system can be operated in three modes: manual, automatic, and computer-controlled. In the computer-controlled mode, the system will automatically acquire, process, analyze, store, and display ultrasonic inspection data in real-time. Flaw size (in cross-section), location (depth), and type (porosity-like or crack-like) can be automatically discerned and displayed. The results and pertinent parameters are recorded.

An experimental and computational investigation of dynamic ductile fracture in stainless steel welds

NASA Astrophysics Data System (ADS)

Kothnur, Vasanth Srinivasa

The high strain rate viscoplastic flow and fracture behavior of NITRONIC-50 and AL6XN stainless steel weldments are studied under dynamic loading conditions. The study is primarily motivated by interest in modeling the micromechanics of dynamic ductile failure in heterogeneous weldments. The high strain rate response of specimens machined from the parent, weld and heat-affected zones of NITRONIC-50 and AL6XN weldments is reported here on the basis of experiments conducted in a compression Kolsky bar configuration. The failure response of specimens prepared from the various material zones is investigated under high rate loading conditions in a tension Kolsky bar set-up. The microstructure of voided fracture process zones in these weldments is studied using X-ray Computed Microtomography. To model the preferential evolution of damage near the heat-affected zone, a finite deformation elastic-viscoplastic constitutive model for porous materials is developed. The evolution of the macroscopic flow response and the porous microstructure have been analysed in two distinctive regimes: pre-coalescence and post-coalescence. The onset of void coalescence is analyzed on the basis of upper-bound models to obtain the limit-loads needed to sustain a localized mode of plastic flow in the inter-void ligament. A finite element framework for the integration of the porous material response under high rate loading conditions is implemented as a user-subroutine in ABAQUS/Explicit. To address the effect of mesh sensitivity of numerical simulations of ductile fracture, a microstructural length scale is used to discretize finite element models of test specimens. Results from a detailed finite element study of the deformation and damage evolution in AL6XN weldments are compared with experimental observations.

Investigation of the Fracture Behavior of Scaled HY-130 Weldments

DTIC Science & Technology

1990-06-01

RESULTS OF EPFM ANALYSIS OF TFREE-POINT BEND SPECIMENS OF DIFFERENT SIZES ........... D-48 xi NAVSWC TR 90-360 TABLES 1 RESULTS OF DYNAMIC FRACTURE...characterize the critical loading needed to cause fracture of the welded joint. An example of such a measure of severity applicable to structures with...weldments. Application of the approach to two titanium alloys and the results of that hwvestigation will be presented in another report. The next four

Surface-crack growth: Models, experiments, and structures; Proceedings of the Symposium, Sparks, NV, Apr. 25, 1988

NASA Technical Reports Server (NTRS)

Reuter, Walter G. (Editor); Underwood, John H. (Editor); Newman, James C., Jr. (Editor)

1990-01-01

The present volume on surface-crack growth modeling, experimental methods, and structures, discusses elastoplastic behavior, the fracture analysis of three-dimensional bodies with surface cracks, optical measurements of free-surface effects on natural surfaces and through cracks, an optical and finite-element investigation of a plastically deformed surface flaw under tension, fracture behavior prediction for rapidly loaded surface-cracked specimens, and surface cracks in thick laminated fiber composite plates. Also discussed are a novel study procedure for crack initiation and growth in thermal fatigue testing, the growth of surface cracks under fatigue and monotonically increasing load, the subcritical growth of a surface flaw, surface crack propagation in notched and unnotched rods, and theoretical and experimental analyses of surface cracks in weldments.

Recent Aspects on the Effect of Inclusion Characteristics on the Intragranular Ferrite Formation in Low Alloy Steels: A Review

NASA Astrophysics Data System (ADS)

Mu, Wangzhong; Jönsson, Pär Göran; Nakajima, Keiji

2017-04-01

Intragranular ferrite (IGF), which nucleates from specific inclusion surfaces in low alloy steels, is the desired microstructure to improve mechanical properties of steel such as the toughness. This microstructure is especially important in the coarse grain heat affected zone (CGHAZ) of weldments. The latest review paper focusing on the role of non-metallic inclusions in the IGF formation in steels has been reported by Sarma et al. in 2009 (ISIJ int., 49(2009), 1063-1074). In recent years, large amount of papers have been presented to investigate different issues of this topic. This paper mainly highlights the frontiers of experimental and theoretical investigations on the effects of inclusion characteristics, such as the composition, size distribution and number density, on the IGF formation in low carbon low-alloyed steels, undertaken by the group of Applied Process Metallurgy, KTH Royal Institute of Technology. Related results reported in previous studies are also introduced. Also, plausible future work regarding various items of IGF formation is mentioned in each section. This work aims to give a better control of improving the steel quality during casting and in the heat affected zone (HAZ) of weldment, according to the concept of oxide metallurgy.

Considerations on repeated repairing of weldments in Inconel 718 alloy

NASA Technical Reports Server (NTRS)

Bayless, E. O.; Lovoy, C. V.; Mcilwain, M. C.; Munafo, P.

1981-01-01

The effects of repeated weld repairs on the metallurgical characteristics, high cycle fatigue (HCF), and tensile properties of Inconel 718 butt weld joints were determined. A 1/4 in thick plate and a 1/2 in thick plate were used as well as tungsten inert gas welding, and Inconel 718 filler wire. Weld panels were subjected to 2, 6, and 12 repeated repairs and were made in a highly restrained condition. Post weld heat treatments were also conducted with the welded panel in the highly restrained condition. Results indicate that no significant metallurgical anomaly is evident as a result of up to twelve repeated weld repairs. No degradation in fatigue life is noted for up to twelve repeated repairs. Tensile results from specimens which contained up to twelve repeated weld repairs revealed no significant degradation in UTS and YS. However, a significant decrease in elongation is evident with specimens (solution treated and age hardened after welding) which contained twelve repeated repairs. The elongation loss is attributed to the presence of a severe notch on each side (fusion line) of the repair weld bead reinforcement.

Galvanic Corrosion Behavior of Microwave Welded and Post-weld Heat-Treated Inconel-718 Joints

NASA Astrophysics Data System (ADS)

Bansal, Amit; Sharma, Apurbba Kumar; Kumar, Pradeep

2017-05-01

In the present study, corrosion behavior of microwave welded Inconel-718 at various conditions was investigated. Welding of Inconel-718 in 980 °C solution-treated condition was performed using microwave hybrid heating technique. The microwave welds were subjected to post-heat treatment for improving its microstructure and mechanical properties by solubilizing the Nb-enriched Laves phase. The microstructural features of the fabricated welds at various conditions were investigated through scanning electron microscopy. The electrochemical testing results revealed that Inconel-718 welds were galvanic corroded when they were anodically polarized in 3.5 wt.% NaCl solution at 28 °C. The difference in the corrosion potentials between the base metal (BM) and fusion zone (FZ) in an Inconel-718 weld was the main factor for galvanic corrosion. The highest corrosion was occurred in the as-welded/aged weldments, followed by 980 °C solution-treated and aged weldments, as-welded specimen, and 1080 °C solution-treated and aged (1080STA) weldments. The least galvanic corrosion was occurred in the 1080STA specimens due to almost uniform microstructure developed in the weldment after the treatment. Thus, it was possible to minimize the galvanic corrosion in the microwave welded Inconel-718 by 1080STA treatment which resulted in reducing the difference in corrosion potentials between the BM and the FZ.

Influence of Alloy Content and Prior Microstructure on Evolution of Secondary Phases in Weldments of 9Cr-Reduced Activation Ferritic-Martensitic Steel

NASA Astrophysics Data System (ADS)

Thomas Paul, V.; Sudha, C.; Saroja, S.

2015-08-01

9Cr-Reduced Activation Ferritic-Martensitic steels with 1 and 1.4 wt pct tungsten are materials of choice for the test blanket module in fusion reactors. The steels possess a tempered martensite microstructure with a decoration of inter- and intra-lath carbides, which undergoes extensive modification on application of heat. The change in substructure and precipitation behavior on welding and subsequent thermal exposure has been studied using both experimental and computational techniques. Changes i.e., formation of various phases, their volume fraction, size, and morphology in different regions of the weldment due to prolonged thermal exposure was influenced not only by the time and temperature of exposure but also the prior microstructure. Laves phase of type Fe2W was formed in the high tungsten steel, on aging the weldment at 823 K (550 °C). It formed in the fine-grained heat-affected zone (HAZ) at much shorter durations than in the base metal. The accelerated kinetics has been understood in terms of enhanced precipitation of carbides at lath/grain boundaries during aging and the concomitant depletion of carbon and chromium and enrichment of tungsten in the vicinity of the carbides. Therefore, the fine-grained HAZ in the weldment was identified as a region susceptible for failure during service.

Fatigue and Fracture-Toughness Characterization of SAW and SMA A537 Class I Ship-Steel Weldments.

DTIC Science & Technology

1981-12-01

Charpy criterion and proposed NDT-DT criterion of Rolfe . Recommendations are made and further research is suggested to help clarify the assessment of...acceptable performance at -60aF. Likewise, at -60OF the NDT and DT data for these weldments marginally exceed the criteria proposed by Rolfe when the...exceed the CVN values equivalent to the 5/8 DT values required by Rolfe . The 5/8-inch dynamic-tear specimen is not recommended as a quality-control test

Influence of laser beam incidence angle on laser lap welding quality of galvanized steels

NASA Astrophysics Data System (ADS)

Mei, Lifang; Yan, Dongbing; Chen, Genyu; Wang, Zhenhui; Chen, Shuixuan

2017-11-01

Based on the characteristics of laser welded structural parts of auto bodies, the influence of variation in laser beam incidence angle on the lap welding performance of galvanized auto-body sheets was studied. Lap welding tests were carried out on the galvanized sheets for auto-body application at different laser beam incidence angles by using the optimal welding parameters obtained through orthogonal experiment. The effects of incidence angle variation on seam appearance, cross-sectional shape, joint mechanical properties and microstructure of weldments were analyzed. In addition, the main factors influencing the value of incidence angle were investigated. According to the results, the weld seams had a good appearance as well as a fine, and uniform microstructure when the laser beam incidence angle was smaller than the critical incidence angle, and thus they could withstand great tensile and shear loads. Moreover, all tensile-shear specimens were fractured in the base material zone. When the laser beam incidence angle was larger than the critical incidence angle, defects like shrinkage and collapse tended to emerge, thereby resulting in the deteriorated weldability of specimens. Meanwhile, factors like the type and thickness of sheet, weld width as well as inter-sheet gap all had a certain effect on the value of laser beam incidence angle. When the sheet thickness was small and the weld width was narrow, the laser beam incidence angle could be increased appropriately. At the same time, small changes in the inter-sheet gap could greatly impact the value of incidence angle. When the inter-sheet gap was small, the laser beam incidence angle should not be too large.

Method and device for controlling plume during laser welding

DOEpatents

Fuerschbach, Phillip W.; Jellison, James L.; Keicher, David M.; Oberkampf, William L.

1991-01-01

A method and apparatus for enhancing the weldment of a laser welding system is provided. The laser weld plume control device includes a cylindrical body defining an upside-down cone cavity; the upper surface of the body circumscribes the base of the cone cavity, and the vertex of the cone cavity forms an orifice concentrically located with respect to the laser beam and the plume which forms as a result of the welding operation. According to the method of the invention, gas is directed radially inward through inlets in the upper surface of the body into and through channels in the wall of the body and finally through the orifice of the body, and downward onto the surface of the weldment. The gas flow is then converted by the orifice of the device from radial flow to an axisymmetric gas jet flowing away from the weldment surface in a direction perpendicular to the surface and opposite to that of the laser.

Pulsed Magnetic Welding for Advanced Core and Cladding Steel

DOE Office of Scientific and Technical Information (OSTI.GOV)

Cao, Guoping; Yang, Yong

2013-12-19

To investigate a solid-state joining method, pulsed magnetic welding (PMW), for welding the advanced core and cladding steels to be used in Generation IV systems, with a specific application for fuel pin end-plug welding. As another alternative solid state welding technique, pulsed magnetic welding (PMW) has not been extensively explored on the advanced steels. The resultant weld can be free from microstructure defects (pores, non-metallic inclusions, segregation of alloying elements). More specifically, the following objectives are to be achieved: 1. To design a suitable welding apparatus fixture, and optimize welding parameters for repeatable and acceptable joining of the fuel pinmore » end-plug. The welding will be evaluated using tensile tests for lap joint weldments and helium leak tests for the fuel pin end-plug; 2 Investigate the microstructural and mechanical properties changes in PMW weldments of proposed advanced core and cladding alloys; 3. Simulate the irradiation effects on the PWM weldments using ion irradiation.« less

Improving the corrosion properties of magnesium AZ31 alloy GTA weld metal using microarc oxidation process

NASA Astrophysics Data System (ADS)

Siva Prasad, M.; Ashfaq, M.; Kishore Babu, N.; Sreekanth, A.; Sivaprasad, K.; Muthupandi, V.

2017-05-01

In this work, the morphology, phase composition, and corrosion properties of microarc oxidized (MAO) gas tungsten arc (GTA) weldments of AZ31 alloy were investigated. Autogenous gas tungsten arc welds were made as full penetration bead-on-plate welding under the alternating-current mode. A uniform oxide layer was developed on the surface of the specimens with MAO treatment in silicate-based alkaline electrolytes for different oxidation times. The corrosion behavior of the samples was evaluated by potentiodynamic polarization and electrochemical impedance spectroscopy. The oxide film improved the corrosion resistance substantially compared to the uncoated specimens. The sample coated for 10 min exhibited better corrosion properties. The corrosion resistance of the coatings was concluded to strongly depend on the morphology, whereas the phase composition and thickness were concluded to only slightly affect the corrosion resistance.

High-Temperature Tensile Behaviors of Base Metal and Electron Beam-Welded Joints of Ni-20Cr-9Mo-4Nb Superalloy

NASA Astrophysics Data System (ADS)

Gupta, R. K.; Anil Kumar, V.; Sukumaran, Arjun; Kumar, Vinod

2018-05-01

Electron beam welding of Ni-20Cr-9Mo-4Nb alloy sheets was carried out, and high-temperature tensile behaviors of base metal and weldments were studied. Tensile properties were evaluated at ambient temperature, at elevated temperatures of 625 °C to 1025 °C, and at strain rates of 0.1 to 0.001 s-1. Microstructure of the weld consisted of columnar dendritic structure and revealed epitaxial mode of solidification. Weld efficiency of 90 pct in terms of strength (UTS) was observed at ambient temperature and up to an elevated temperature of 850 °C. Reduction in strength continued with further increase of test temperature (up to 1025 °C); however, a significant improvement in pct elongation is found up to 775 °C, which was sustained even at higher test temperatures. The tensile behaviors of base metal and weldments were similar at the elevated temperatures at the respective strain rates. Strain hardening exponent `n' of the base metal and weldment was 0.519. Activation energy `Q' of base metal and EB weldments were 420 to 535 kJ mol-1 determined through isothermal tensile tests and 625 to 662 kJ mol-1 through jump-temperature tensile tests. Strain rate sensitivity `m' was low (< 0.119) for the base metal and (< 0.164) for the weldment. The δ phase was revealed in specimens annealed at 700 °C, whereas, twins and fully recrystallized grains were observed in specimens annealed at 1025 °C. Low-angle misorientation and strain localization in the welds and the HAZ during tensile testing at higher temperature and strain rates indicates subgrain formation and recrystallization. Higher elongation in the weldment (at Test temperature > 775 °C) is attributed to the presence of recrystallized grains. Up to 700 °C, the deformation is through slip, where strain hardening is predominant and effect of strain rate is minimal. Between 775 °C to 850 °C, strain hardening is counterbalanced by flow softening, where cavitation limits the deformation (predominantly at lower strain rate). Above 925 °C, flow softening is predominant resulting in a significant reduction in strength. Presence of precipitates/accumulated strain at high strain rate results in high strength, but when the precipitates were coarsened at lower strain rates or precipitates were dissolved at a higher temperature, the result was a reduction in strength. Further, the accumulated strain assisted in recrystallization, which also resulted in a reduction in strength.

Microstructural Characterization of the Heat-Affected Zones in Grade 92 Steel Welds: Double-Pass and Multipass Welds

NASA Astrophysics Data System (ADS)

Xu, X.; West, G. D.; Siefert, J. A.; Parker, J. D.; Thomson, R. C.

2018-04-01

The microstructure in the heat-affected zone (HAZ) of multipass welds typical of those used in power plants and made from 9 wt pct chromium martensitic Grade 92 steel is complex. Therefore, there is a need for systematic microstructural investigations to define the different regions of the microstructure across the HAZ of Grade 92 steel welds manufactured using the traditional arc welding processes in order to understand possible failure mechanisms after long-term service. In this study, the microstructure in the HAZ of an as-fabricated two-pass bead-on-plate weld on a parent metal of Grade 92 steel has been systematically investigated and compared to a complex, multipass thick section weldment using an extensive range of electron and ion-microscopy-based techniques. A dilatometer has been used to apply controlled thermal cycles to simulate the microstructures in distinctly different regions in a multipass HAZ using sequential thermal cycles. A wide range of microstructural properties in the simulated materials were characterized and compared with the experimental observations from the weld HAZ. It has been found that the microstructure in the HAZ can be categorized by a combination of sequential thermal cycles experienced by the different zones within the complex weld metal, using the terminology developed for these regions based on a simpler, single-pass bead-on-plate weld, categorized as complete transformation, partial transformation, and overtempered.

Analysis of WC/Ni-Based Coatings Deposited by Controlled Short-Circuit MIG Welding

NASA Astrophysics Data System (ADS)

Vespa, P.; Pinard, P. T.; Gauvin, R.; Brochu, M.

2012-06-01

This study investigates the recently developed controlled short-circuit metal inert gas (CSC-MIG) welding system for depositing WC/Ni-based claddings on carbon steel substrates. WC/Ni-based coatings deposited by CSC-MIG were analyzed by optical light microscopy and scanning electron microscopy (SEM) equipped with energy dispersive spectroscopy (EDS) and electron backscatter diffraction (EBSD) capabilities. X-ray diffraction (XRD) and hardness measurements of depositions are also reported. The CSC-MIG welding system provides a significant amount of user control over the current waveform during welding and has lower heat input when compared with traditional MIG welding. Heat input for the analyzed coatings ranged from 10.1 to 108.7 J/mm. Metallurgically bonded coatings free from spatter and with 0.75% average porosity were produced. It was found that the detrimental decarburization of the WC particles seen in thermal spray systems does not occur when welding with the CSC-MIG. Precipitation of a reaction layer around the reinforcing phase was identified as WC; the average thickness of which increases from 3.8 to 7.2 μm for the low and high heat input condition, respectively. Precipitation of newly formed WC particles was observed; their size distribution increased from D 50 of 2.4 μm in the low heat input weldment to 6.75 μm in the high heat input weldment. The level of dilution of the reinforcing phase increases significantly with heat input. The hardness of the deposited coatings decreases from 587 HV10 to 410 HV10 when the energy input was increased from 10.1 to 108.7 J/mm.

Limit load solution for electron beam welded joints with single edge weld center crack in tension

NASA Astrophysics Data System (ADS)

Lu, Wei; Shi, Yaowu; Li, Xiaoyan; Lei, Yongping

2012-05-01

Limit loads are widely studied and several limit load solutions are proposed to some typical geometry of weldments. However, there are no limit load solutions exist for the single edge crack weldments in tension (SEC(T)), which is also a typical geometry in fracture analysis. The mis-matching limit load for thick plate with SEC(T) are investigated and the special limit load solutions are proposed based on the available mis-matching limit load solutions and systematic finite element analyses. The real weld configurations are simplified as a strip, and different weld strength mis-matching ratio M, crack depth/width ratio a/ W and weld width 2H are in consideration. As a result, it is found that there exists excellent agreement between the limit load solutions and the FE results for almost all the mis-matching ration M, a/ W and ligament-to-weld width ratio ( W-a)/ H. Moreover, useful recommendations are given for evaluating the limit loads of the EBW structure with SEC(T). For the EBW joints with SEC(T), the mis-matching limit loads can be obtained assuming that the components are wholly made of base metal, when M changing from 1.6 to 0.6. When M decreasing to 0.4, the mis-matching limit loads can be obtained assuming that the components are wholly made of base metal only for large value of ( W-a)/ H. The recommendations may be useful for evaluating the limit loads of the EBW structures with SEC(T). The engineering simplifications are given for assessing the limit loads of electron beam welded structure with SEC(T).

Microstructural Influence on Mechanical Properties in Plasma Microwelding of Ti6Al4V Alloy

NASA Astrophysics Data System (ADS)

Baruah, M.; Bag, S.

2016-11-01

The complexity of joining Ti6Al4V alloy enhances with reduction in sheet thickness. The present work puts emphasis on microplasma arc welding (MPAW) of 500-μm-thick Ti6Al4V alloy in butt joint configuration. Using controlled and regulated arc current, the MPAW process is specifically designed to use in joining of thin sheet components over a wide range of process parameters. The weld quality is assessed by carefully controlling the process parameters and by reducing the formation of oxides. The combined effect of welding speed and current on the weld joint properties is evaluated for joining of Ti6Al4V alloy. The macro- and microstructural characterizations of the weldment by optical microscopy as well as the analysis of mechanical properties by microtensile and microhardness test have been performed. The weld joint quality is affected by specifically designed fixture that controls the oxidation of the joint and introduces high cooling rate. Hence, the solidified microstructure of welded specimen influences the mechanical properties of the joint. The butt joint of titanium alloy by MPAW at optimal process parameters is of very high quality, without any internal defects and with minimum residual distortion.

Fiber laser welding of austenitic steel and commercially pure copper butt joint

NASA Astrophysics Data System (ADS)

Kuryntsev, S. V.; Morushkin, A. E.; Gilmutdinov, A. Kh.

2017-03-01

The fiber laser welding of austenitic stainless steel and commercially pure copper in butt joint configuration without filler or intermediate material is presented. In order to melt stainless steel directly and melt copper via heat conduction a defocused laser beam was used with an offset to stainless steel. During mechanical tests the weld seam was more durable than heat affected zone of copper so samples without defects could be obtained. Three process variants of offset of the laser beam were applied. The following tests were conducted: tensile test of weldment, intermediate layer microhardness, optical metallography, study of the chemical composition of the intermediate layer, fractography. Measurements of electrical resistivity coefficients of stainless steel, copper and copper-stainless steel weldment were made, which can be interpreted or recalculated as the thermal conductivity coefficient. It shows that electrical resistivity coefficient of cooper-stainless steel weldment higher than that of stainless steel. The width of intermediate layer between stainless steel and commercially pure copper was 41-53 μm, microhardness was 128-170 HV0.01.

Effect of filler metals on the mechanical properties of Inconel 625 and AISI 904L dissimilar weldments using gas tungsten arc welding

NASA Astrophysics Data System (ADS)

Senthur Prabu, S.; Devendranath Ramkumar, K.; Arivazhagan, N.

2017-11-01

In the present research work, dissimilar welding between Inconel 625 super alloy and AISI 904L super austenitic stainless steel using manual multi-pass continuous current gas tungsten arc (CCGTA) welding process employed with ERNiCrMo-4 and ERNiCrCoMo-1 fillers were performed to determine the mechanical properties and weldability. Tensile test results corroborated that the fracture had occurred at the parent metal of AISI 904L irrespective of filler used for all the trials. The presence of the macro and micro void coalescence in the fibrous matrix characterised for ductile mode of fracture. The hardness values at the weld interface of Inconel 625 side were observed to be higher for ERNiCrMo-4 filler due to the presence of strengthening elements such as W, Mo, Ni and Cr. The impact test accentuated that the weldments using ERNiCrMo-4 filler offered better impact toughness (41J) at room temperature. Bend test results showed that the weldments using these fillers exhibited good ductility without cracks.

Determination of a temperature sensor location for monitoring weld pool size in GMAW

DOE Office of Scientific and Technical Information (OSTI.GOV)

Boo, K.S.; Cho, H.S.

1994-11-01

This paper describes a method of determining the optimal sensor location to measure weldment surface temperature, which has a close correlation with weld pool size in the gas metal arc (GMA) welding process. Due to the inherent complexity and nonlinearity in the GMA welding process, the relationship between the weldment surface temperature and the weld pool size varies with the point of measurement. This necessitates an optimal selection of the measurement point to minimize the process nonlinearity effect in estimating the weld pool size from the measured temperature. To determine the optimal sensor location on the top surface of themore » weldment, the correlation between the measured temperature and the weld pool size is analyzed. The analysis is done by calculating the correlation function, which is based upon an analytical temperature distribution model. To validate the optimal sensor location, a series of GMA bead-on-plate welds are performed on a medium-carbon steel under various welding conditions. A comparison study is given in detail based upon the simulation and experimental results.« less

Microstructure-dependent fracture toughness (JIC) variations in dissimilar pipe welds for pressure vessel system of nuclear plants

NASA Astrophysics Data System (ADS)

Rathod, Dinesh W.; Pandey, Sunil; Singh, P. K.; Kumar, Suranjit

2017-09-01

In present study, dissimilar metal weld (DMW) joints between SA508Gr.3cl.1 ferritic steel and SS304LN pipes were prepared using Inconel 82/182, and Inconel 52/152 consumables. Metallurgical properties and their influence on fracture toughness of weldment regions and interfacial regions could play a significant role in integrity assessment of these joints. Ni-based consumables exhibit complex metallurgical properties at interfacial regions. The metallurgical characterization and fracture toughness studies of Inconel 82/182 and Inconel 52/152 joints have been carried out for determining the optimum consumable for DMW joint requirements and the effect of microstructure on fracture toughness in weldment regions. The present codes and procedures for integrity assessment of DMW joints have not given due considerations of metallurgical properties. The requirements for metallurgical properties by considering their effect on fracture toughness properties in integrity assessment have been discussed for reliable analysis. Inconel 82/182 is preferred over Inconel 52/152 joints owing to favorable metallurgical and fracture toughness properties across the interfacial and weldment regions.

Optimization of process parameters in welding of dissimilar steels using robot TIG welding

NASA Astrophysics Data System (ADS)

Navaneeswar Reddy, G.; VenkataRamana, M.

2018-03-01

Robot TIG welding is a modern technique used for joining two work pieces with high precision. Design of Experiments is used to conduct experiments by varying weld parameters like current, wire feed and travelling speed. The welding parameters play important role in joining of dissimilar stainless steel SS 304L and SS430. In this work, influences of welding parameter on Robot TIG Welded specimens are investigated using Response Surface Methodology. The Micro Vickers hardness tests of the weldments are measured. The process parameters are optimized to maximize the hardness of the weldments.

Evaluation of ultrasonics and optimized radiography for 2219-T87 aluminum weldments

NASA Technical Reports Server (NTRS)

Clotfelter, W. N.; Hoop, J. M.; Duren, P. C.

1975-01-01

Ultrasonic studies are described which are specifically directed toward the quantitative measurement of randomly located defects previously found in aluminum welds with radiography or with dye penetrants. Experimental radiographic studies were also made to optimize techniques for welds of the thickness range to be used in fabricating the External Tank of the Space Shuttle. Conventional and innovative ultrasonic techniques were applied to the flaw size measurement problem. Advantages and disadvantages of each method are discussed. Flaw size data obtained ultrasonically were compared to radiographic data and to real flaw sizes determined by destructive measurements. Considerable success was achieved with pulse echo techniques and with 'pitch and catch' techniques. The radiographic work described demonstrates that careful selection of film exposure parameters for a particular application must be made to obtain optimized flaw detectability. Thus, film exposure techniques can be improved even though radiography is an old weld inspection method.

Development of references of anomalies detection on P91 material using Self-Magnetic Leakage Field (SMLF) technique

NASA Astrophysics Data System (ADS)

Husin, Shuib; Afiq Pauzi, Ahmad; Yunus, Salmi Mohd; Ghafar, Mohd Hafiz Abdul; Adilin Sekari, Saiful

2017-10-01

This technical paper demonstrates the successful of the application of self-magnetic leakage field (SMLF) technique in detecting anomalies in weldment of a thick P91 materials joint (1 inch thickness). Boiler components such as boiler tubes, stub boiler at penthouse and energy piping such as hot reheat pipe (HRP) and H-balance energy piping to turbine are made of P91 material. P91 is ferromagnetic material, therefore the technique of self-magnetic leakage field (SMLF) is applicable for P91 in detecting anomalies within material (internal defects). The technique is categorized under non-destructive technique (NDT). It is the second passive method after acoustic emission (AE), at which the information on structures radiation (magnetic field and energy waves) is used. The measured magnetic leakage field of a product or component is a magnetic leakage field occurring on the component’s surface in the zone of dislocation stable slipbands under the influence of operational (in-service) or residual stresses or in zones of maximum inhomogeneity of metal structure in new products or components. Inter-granular and trans-granular cracks, inclusion, void, cavity and corrosion are considered types of inhomogeneity and discontinuity in material where obviously the output of magnetic leakage field will be shown when using this technique. The technique does not required surface preparation for the component to be inspected. This technique is contact-type inspection, which means the sensor has to touch or in-contact to the component’s surface during inspection. The results of application of SMLF technique on the developed P91 reference blocks have demonstrated that the technique is practical to be used for anomaly inspection and detection as well as identification of anomalies’ location. The evaluation of this passive self-magnetic leakage field (SMLF) technique has been verified by other conventional non-destructive tests (NDTs) on the reference blocks where simulated defects/anomalies have been developed inside at the weldment. The results from the inspection test showed that the signatures of magnetic leakage field gradient distribution prove that the peak is found on the location of defect/anomaly in the reference block. It is in agreement with the evidence of anomaly that seen in the radiography test film (RT).

X-ray online detection for laser welding T-joint of Al-Li alloy

NASA Astrophysics Data System (ADS)

Zhan, Xiaohong; Bu, Xing; Qin, Tao; Yu, Haisong; Chen, Jie; Wei, Yanhong

2017-05-01

In order to detect weld defects in laser welding T-joint of Al-Li alloy, a real-time X-ray image system is set up for quality inspection. Experiments on real-time radiography procedure of the weldment are conducted by using this system. Twin fillet welding seam radiographic arrangement is designed according to the structural characteristics of the weldment. The critical parameters including magnification times, focal length, tube current and tube voltage are studied to acquire high quality weld images. Through the theoretical and data analysis, optimum parameters are settled and expected digital images are captured, which is conductive to automatic defect detection.

Design, properties, and weldability of advanced oxidation-resistant FeCrAl alloys

DOE PAGES

Gussev, M. N.; Field, K. G.; Yamamoto, Y.

2017-05-05

FeCrAl alloys are promising as corrosion- and oxidation-resistance materials for extreme high-temperature applications. However, further alloy design and improvement requires a delicate balance between workability, weldability, propensity for '-phase formation, among other factors. Here, a series of advanced oxidant resistant FeCrAl alloys were produced and investigated. Variants with Al (+2%), Nb (+1%), and TiC (0.1, 0.3, and 1%) additions over the reference alloy (Fe-13%Cr-5%Al) were characterized in detail before and after controlled laser beam welding using tensile tests with digital image correlation, SEM-EBSD analysis, and fractography. All investigated alloys demonstrated yield stress in the weldment over 500 MPa; no welding-inducedmore » cracking was observed. However, it was shown that the increase in the Al-content over 5% was detrimental leading to a brittle fracture mechanism and decreased ductility in the weldment. At the same time, Nb and TiC additions were beneficial for preventing grain growth and reducing local softening (yield stress reduction) in the heat-affected zone. The 1% TiC addition also effectively refined grain size in the weldment.« less

Design, properties, and weldability of advanced oxidation-resistant FeCrAl alloys

DOE Office of Scientific and Technical Information (OSTI.GOV)

Gussev, M. N.; Field, K. G.; Yamamoto, Y.

FeCrAl alloys are promising as corrosion- and oxidation-resistance materials for extreme high-temperature applications. However, further alloy design and improvement requires a delicate balance between workability, weldability, propensity for '-phase formation, among other factors. Here, a series of advanced oxidant resistant FeCrAl alloys were produced and investigated. Variants with Al (+2%), Nb (+1%), and TiC (0.1, 0.3, and 1%) additions over the reference alloy (Fe-13%Cr-5%Al) were characterized in detail before and after controlled laser beam welding using tensile tests with digital image correlation, SEM-EBSD analysis, and fractography. All investigated alloys demonstrated yield stress in the weldment over 500 MPa; no welding-inducedmore » cracking was observed. However, it was shown that the increase in the Al-content over 5% was detrimental leading to a brittle fracture mechanism and decreased ductility in the weldment. At the same time, Nb and TiC additions were beneficial for preventing grain growth and reducing local softening (yield stress reduction) in the heat-affected zone. The 1% TiC addition also effectively refined grain size in the weldment.« less

Tensile Property of ANSI 304 Stainless Steel Weldments Subjected to Cavitation Erosion Based on Treatment of Laser Shock Processing.

PubMed

Zhang, Lei; Liu, Yue-Hua; Luo, Kai-Yu; Zhang, Yong-Kang; Zhao, Yong; Huang, Jian-Yun; Wu, Xu-Dong; Zhou, Chuang

2018-05-16

Tensile property was one important index of mechanical properties of ANSI 304 stainless steel laser weldments subjected to cavitation erosion (CE). Laser shock processing (LSP) was utilized to strengthen the CE resistance, and the tensile property and fracture morphology were analyzed through three replicated experiment times. Results showed tensile process of treated weldments was composed of elastic deformation, plastic deformation, and fracture. The elastic limit, elastic modulus, elongation, area reduction, and ultimate tensile strength of tensile sample after CE were higher in view of LSP. In the fracture surface, the fiber zone, radiation zone and shear lip zone were generated, and those were more obvious through LSP. The number and size of pores in the fracture surface were smaller, and the fracture surface was smoother and more uniform. The dimples were elongated along the unified direction due to effects of LSP, and the elongated direction was in agreement with the crack propagation direction. Their distribution and shape were uniform with deeper depth. It could be reflected that the tensile property was improved by LSP and the CE resistance was also enhanced.

Acoustic emission investigation of cold cracking in gas metal-arc welding of AISI 4340 steel

DOE Office of Scientific and Technical Information (OSTI.GOV)

Fang, C.K.; Kannatey-Asibu, E. Jr.; Barber, J.R.

1995-06-01

Acoustic emission (AE) has been used to investigate the propagation of a finite crack in a weldment subjected to nonuniform longitudinal residual stresses during gas metal arc welding (GMAW). Cold cracking in selected weldments was accelerated using the electrochemical method to cathodically charge the weldments with hydrogen in order to induce hydrogen embrittlement. Cold cracking was observed about 40 min after charging in the specimen subjected to hydrogen embrittlement, while it was observed two days after welding for the one that was left in the atmosphere. The AE signals were generated as the specimen cracked and were recorded, and themore » effects from structure and instrumentation were removed from the measured signals by deconvolution in the frequency domain. Most of the high-amplitude signal components were found to be clustered in the frequency range below 200 kHz. The experimentally obtained spectrum was compared with theoretical results derived in earlier work, and reasonable agreement with theoretical surface displacement in both time and frequency domains was obtained. The envelopes for both spectra were found to decrease with increasing frequency, while the fluctuations in each curve diminished at high frequencies.« less

Tensile Property of ANSI 304 Stainless Steel Weldments Subjected to Cavitation Erosion Based on Treatment of Laser Shock Processing

PubMed Central

Zhang, Lei; Liu, Yue-Hua; Luo, Kai-Yu; Zhang, Yong-Kang; Zhao, Yong; Huang, Jian-Yun; Wu, Xu-Dong; Zhou, Chuang

2018-01-01

Tensile property was one important index of mechanical properties of ANSI 304 stainless steel laser weldments subjected to cavitation erosion (CE). Laser shock processing (LSP) was utilized to strengthen the CE resistance, and the tensile property and fracture morphology were analyzed through three replicated experiment times. Results showed tensile process of treated weldments was composed of elastic deformation, plastic deformation, and fracture. The elastic limit, elastic modulus, elongation, area reduction, and ultimate tensile strength of tensile sample after CE were higher in view of LSP. In the fracture surface, the fiber zone, radiation zone and shear lip zone were generated, and those were more obvious through LSP. The number and size of pores in the fracture surface were smaller, and the fracture surface was smoother and more uniform. The dimples were elongated along the unified direction due to effects of LSP, and the elongated direction was in agreement with the crack propagation direction. Their distribution and shape were uniform with deeper depth. It could be reflected that the tensile property was improved by LSP and the CE resistance was also enhanced. PMID:29772661

Microstructural characterization of dissimilar welds between Incoloy 800H and 321 Austenitic Stainless Steel

DOE Office of Scientific and Technical Information (OSTI.GOV)

Sayiram, G., E-mail: sayiram.g@vit.ac.in; Arivazhagan, N.

2015-04-15

In this work, the microstructural character of dissimilar welds between Incoloy 800H and 321 Stainless Steel has been discussed. The microscopic examination of the base metals, fusion zones and interfaces was characterized using an optical microscope and scanning electron microscopy. The results revealed precipitates of Ti (C, N) in the austenitic matrix along the grain boundaries of the base metals. Migration of grain boundaries in the Inconel 82 weld metal was very extensive when compared to Inconel 617 weldment. Epitaxial growth was observed in the 617 weldment which increases the strength and ductility of the weld metal. Unmixed zone nearmore » the fusion line between 321 Stainless Steel and Inconel 82 weld metal was identified. From the results, it has been concluded that Inconel 617 filler metal is a preferable choice for the joint between Incoloy 800H and 321 Stainless Steel. - Highlights: • Failure mechanisms produced by dissimilar welding of Incoloy 800H to AISI 321SS • Influence of filler wire on microstructure properties • Contemplative comparisons of metallurgical aspects of these weldments • Microstructure and chemical studies including metallography, SEM–EDS • EDS-line scan study at interface.« less

Effect of Measured Welding Residual Stresses on Crack Growth

NASA Technical Reports Server (NTRS)

Hampton, Roy W.; Nelson, Drew; Doty, Laura W. (Technical Monitor)

1998-01-01

Welding residual stresses in thin plate A516-70 steel and 2219-T87 aluminum butt weldments were measured by the strain-gage hole drilling and X-ray diffraction methods. The residual stress data were used to construct 3D strain fields which were modeled as thermally induced strains. These 3D strain fields were then analyzed with the WARP31) FEM fracture analysis code in order to predict their effect on fatigue and on fracture. For analyses of fatigue crack advance and subsequent verification testing, fatigue crack growth increments were simulated by successive saw-cuts and incremental loading to generate, as a function of crack length, effects on crack growth of the interaction between residual stresses and load induced stresses. The specimen experimental response was characterized and compared to the WARM linear elastic and elastic-plastic fracture mechanics analysis predictions. To perform the fracture analysis, the plate material's crack tearing resistance was determined by tests of thin plate M(T) specimens. Fracture analyses of these specimen were performed using WARP31D to determine the critical Crack Tip Opening Angle [CTOA] of each material. These critical CTOA values were used to predict crack tearing and fracture in the weldments. To verify the fracture predictions, weldment M(T) specimen were tested in monotonic loading to fracture while characterizing the fracture process.

Influence of low nickel (0.09 wt%) content on microstructure and toughness of P91 steel welds

NASA Astrophysics Data System (ADS)

Arivazhagan, B.; Vasudevan, M.; Kamaraj, M.

2015-05-01

Modified 9Cr-1Mo (P91) steel is widely used as a high temperature structural material in the fabrication of power plant components. Alloying elements significantly influences the microstructure and mechanical properties of P91 steel weldments. The alloying elements manganese and nickel significantly influence the lower critical phase transformation temperature (AC1) as well as tempering response of welds. In the existing published information there was wide spread use of high Mn+Ni filler wire. In the present study, weldment preparation was completed using GTA filler wire having low Nickel content (Mn+Ni of 0.58 wt% including nickel content of 0.09 wt%). Microstructure and mechanical properties characterization was done. There is a requirement on minimum toughness of 47 Joules for P91 steel tempered welds at room temperature. Microstructural observation revealed that the GTA welds have low δ-ferrite content (<0.5%) in the martensite matrix. In the as-weld condition, the toughness was 28 Joules whereas after PWHT at 760 °C-2 h it was 115 Joules. In the present study, toughness of low nickel weld was higher due to low δ-ferrite content (<0.5%), multipass grain refinement and weld metal deposition of single pass per layer of weldment.

Impact of neutron irradiation on mechanical performance of FeCrAl alloy laser-beam weldments

NASA Astrophysics Data System (ADS)

Gussev, M. N.; Cakmak, E.; Field, K. G.

2018-06-01

Oxidation-resistant iron-chromium-aluminum (FeCrAl) alloys demonstrate better performance in Loss-of-Coolant Accidents, compared with austenitic- and zirconium-based alloys. However, further deployment of FeCrAl-based materials requires detailed characterization of their performance under irradiation; moreover, since welding is one of the key operations in fabrication of light water reactor fuel cladding, FeCrAl alloy weldment performance and properties also should be determined prior to and after irradiation. Here, advanced C35M alloy (Fe-13%Cr-5%Al) and variants with aluminum (+2%) or titanium carbide (+1%) additions were characterized after neutron irradiation in Oak Ridge National Laboratory's High Flux Isotope Reactor at 1.8-1.9 dpa in a temperature range of 195-559 °C. Specimen sets included as-received (AR) materials and specimens after controlled laser-beam welding. Tensile tests with digital image correlation (DIC), scanning electron microscopy-electron back scatter diffraction analysis, fractography, and x-ray tomography analysis were performed. DIC allowed for investigating local yield stress in the weldments, deformation hardening behavior, and plastic anisotropy. Both AR and welded material revealed a high degree of radiation-induced hardening for low-temperature irradiation; however, irradiation at high-temperatures (i.e., 559 °C) had little overall effect on the mechanical performance.

Non Destructive Analysis of Fsw Welds using Ultrasonic Signal Analysis

NASA Astrophysics Data System (ADS)

Pavan Kumar, T.; Prabhakar Reddy, P.

2017-08-01

Friction Stir Welding is an evolving metal joining technique and is mostly used in joining materials which cannot be easily joined by other available welding techniques. It is a technique which can be used for welding dissimilar materials also. The strength of the weld joint is determined by the way in which these material are mixing with each other, since we are not using any filler material for the welding process the intermixing has a significant importance. The complication with the friction stir welding process is that there are many process parameters which effect this intermixing process such as tool geometry, rotating speed of the tool, transverse speed etc., In this study an attempt is made to compare the material flow and weld quality of various weldments by changing the parameters. Ultrasonic signal Analysis is used to characterize the microstructure of the weldments. use of ultrasonic waves is a non destructive, accurate and fast way of characterization of microstructure. In this method the relationship between the ultrasonic measured parameters and microstructures are evaluated using background echo and backscattered signal process techniques. The ultrasonic velocity and attenuation measurements are dependent on the elastic modulus and any change in the microstructure is reflected in the ultrasonic velocity. An insight into material flow is essential to determine the quality of the weld. Hence an attempt is made in this study to know the relationship between tool geometry and the pattern of material flow and resulting weld quality the experiments are conducted to weld dissimilar aluminum alloys and the weldments are characterized using and ultra Sonic signal processing. Characterization is also done using Scanning Electron Microscopy. It is observed that there is a good correlation between the ultrasonic signal processing results and Scanning Electron Microscopy on the observed precipitates. Tensile tests and hardness tests are conducted on the weldments and compared for determining the weld quality.

Electron Beam Welding of Gear Wheels by Splitted Beam

NASA Astrophysics Data System (ADS)

Dřímal, Daniel

2014-06-01

This contribution deals with the issue of electron beam welding of high-accurate gear wheels composed of a spur gearing and fluted shaft joined with a face weld for automotive industry. Both parts made of the high-strength low-alloy steel are welded in the condition after final machining and heat treatment, performed by case hardening, whereas it is required that the run-out in the critical point of weldment after welding, i. e. after the final operation, would be 0.04 mm max.. In case of common welding procedure, cracks were formed in the weld, initiated by spiking in the weld root. Crack formation was prevented by the use of an interlocking joint with a rounded recess and suitable welding parameters, eliminating crack initiation by spiking in the weld root. Minimisation of the welding distortions was achieved by the application of tack welding with simultaneous splitting of one beam into two parts in the opposite sections of circumferential face weld attained on the principle of a new system of controlled deflection with digital scanning of the beam. This welding procedure assured that the weldment temperature after welding would not be higher than 400 °C. Thus, this procedure allowed achieving the final run-outs in the critical point of gearwheels within the maximum range up to 0.04 mm, which is acceptable for the given application. Accurate optical measurements did not reveal any changes in the teeth dimensions.

Titanium Alloys Thin Sheet Welding with the Use of Concentrated Solar Energy

NASA Astrophysics Data System (ADS)

Pantelis, D. I.; Kazasidis, M.; Karakizis, P. N.

2017-12-01

The present study deals with the welding of titanium alloys thin sheets 1.3 mm thick, with the use of concentrated solar energy. The experimental part of the work took place at a medium size solar furnace at the installation of the Centre National de la Recherche Scientifique, at Odeillo, in Southern France, where similar and dissimilar defect-free welds of titanium Grades 4 and 6 were achieved, in the butt joint configuration. After the determination of the appropriate welding conditions, the optimum welded structures were examined and characterized microstructurally, by means of light optical microscopy, scanning electron microscopy, and microhardness testing. In addition, test pieces extracted from the weldments were tested under uniaxial tensile loading aiming to the estimation of the strength and the ductility of the joint. The analysis of the experimental results and the recorded data led to the basic concluding remarks which demonstrate increased hardness distribution inside the fusion area and severe loss of ductility, but adequate yield and tensile strength of the welds.

The influence of process parameters on porosity formation in hybrid LASER-GMA welding of AA6082 aluminum alloy

NASA Astrophysics Data System (ADS)

Ascari, Alessandro; Fortunato, Alessandro; Orazi, Leonardo; Campana, Giampaolo

2012-07-01

This paper deals with an experimental campaign carried out on AA6082 8 mm thick plates in order to investigate the role of process parameters on porosity formation in hybrid LASER-GMA welding. Bead on plate weldments were obtained on the above mentioned aluminum alloy considering the variation of the following process parameters: GMAW current (120 and 180 A for short-arc mode, 90 and 130 A for pulsed-arc mode), arc transfer mode (short-arc and pulsed-arc) and mutual distance between arc and LASER sources (0, 3 and 6 mm). Porosities occurring in the fused zone were observed by means of X-ray inspection and measured exploiting an image analysis software. In order to understand the possible correlation between process parameters and porosity formation an analysis of variance statistical approach was exploited. The obtained results pointed out that GMAW current is significant on porosity formation, while the distance between the sources do not affect this aspect.

Fracture toughness determination using spiral-grooved cylindrical specimen and pure torsional loading

DOEpatents

Wang, Jy-An; Liu, Kenneth C.

2003-07-08

A method for determining fracture toughness K.sub.IC of materials ranging from metallic alloys, brittle ceramics and their composites, and weldments. A cylindrical specimen having a helical V-groove with a 45.degree. pitch is subjected to pure torsion. This loading configuration creates a uniform tensile-stress crack-opening mode, and a transverse plane-strain state along the helical groove. The full length of the spiral groove is equivalent to the thickness of a conventional compact-type specimen. K.sub.IC values are determined from the fracture torque and crack length measured from the test specimen using a 3-D finite element program (TOR3D-KIC) developed for the purpose. In addition, a mixed mode (combined tensile and shear stress mode) fracture toughness value can be determined by varying the pitch of the helical groove. Since the key information needed for determining the K.sub.IC value is condensed in the vicinity of the crack tip, the specimen can be significantly miniaturized without the loss of generality.

Experimental Investigations on Formability of Aluminum Tailor Friction Stir Welded Blanks in Deep Drawing Process

NASA Astrophysics Data System (ADS)

Kesharwani, R. K.; Panda, S. K.; Pal, S. K.

2015-02-01

In the present work, tailor friction stir welded blanks (TFSWBs) were fabricated successfully using 2.0-mm-thick AA5754-H22 and AA5052-H32 sheet metals with optimized tool design and process parameters. Taguchi L9 orthogonal array has been used to design the friction stir welding experiments, and the Grey relational analysis has been applied for the multi objective optimization in order to maximize the weld strength and total elongation reducing the surface roughness and energy consumption. The formability of the TFSWBs and parent materials was evaluated and compared in terms of limiting drawing ratio (LDR) using a conventional circular die. It was found that the formability of the TFSWBs was comparable with that of both the parent materials without failure in the weldment. A modified conical tractrix die (MCTD) was proposed to enhance the LDR of the TFSWBs. It was found that the formability was improved by 27% using the MCTD.

Fatigue behavior of 5Ni-Cr-Mo-V steel weldments containing fabrication discontinuities

NASA Technical Reports Server (NTRS)

Gill, Steven J.; Hauser, Joseph A., II; Crooker, Thomas W.; Kruse, Brian J.; Menon, Ravi

1988-01-01

The applicability of linear elastic fracture mechanics to characterize the fatigue behavior of high-strength steel weldments containing lack-of-penetration (LOP) and slag/lack-of-fusion (S/LOF) discontinuities is explored. Full penetration, double-V butt welds with reinforcements removed were tested under zero-to-tension axial loading. Various filler metals and welding techniques were used. Both sound welds and welds containing discontinuities were cycled to failure. Where possible, cycles to crack initiation were estimated by strain gage measurements. The fracture mechanics approach was successful in correlating the fatigue lifetimes of specimens containing single LOP discontinuities of varying size. However, the fatigue behavior of specimens containing multiple S/LOF discontinuities proved to be much more complex and difficult to analyze.

Microstructural evolution in ultra-low-carbon steel weldments—Part I: Controlled thermal cycling and continuous cooling transformation diagram of the weld metal

NASA Astrophysics Data System (ADS)

Fonda, R. W.; Spanos, G.

2000-09-01

The transformation behavior and microstructural evolution of the as-deposited weld metal from an ultra-low-carbon (ULC) weldment were characterized by dilatometry, optical microscopy, transmission electron microscopy, and microhardness measurements. These results were used to construct a continuous cooling transformation (CCT) diagram for this weld metal. The major microconstituents observed in this ULC weldment were (in order of decreasing cooling rate) coarse autotempered martensite, fine lath martensite, lath ferrite, and degenerate lath ferrite. No polygonal ferrite was observed. These results were also used to develop criteria to differentiate between the two predominant microstructures in these ULC steels, lath martensite, and lath ferrite, which can look quite similar but have very different properties.

Effects of Laser Shock Processing on Morphologies and Mechanical Properties of ANSI 304 Stainless Steel Weldments Subjected to Cavitation Erosion

PubMed Central

Zhang, Lei; Lu, Jin-Zhong; Zhang, Yong-Kang; Ma, Hai-Le; Luo, Kai-Yu; Dai, Feng-Ze

2017-01-01

Effects of laser shock processing (LSP) on the cavitation erosion resistance of laser weldments were investigated by optical microscope (OM), scanning electron microscope (SEM) observations, roughness tester, micro hardness tester, and X-ray diffraction (XRD) technology. The morphological microstructures were characterized. Cumulative mass loss, incubation period, erosion rate, and damaged surface areas were monitored during cavitation erosion. Surface roughness, micro-hardness, and residual stress were measured in different zones. Results showed that LSP could improve the damage of morphological microstructures and mechanical properties after cavitation erosion. The compressive residual stresses were generated during the process of LSP, which was an effective guarantee for the improvement of the above mentioned properties. PMID:28772652

SCC Initiation Behavior of Alloy 182 in PWR Primary Water

DOE Office of Scientific and Technical Information (OSTI.GOV)

Toloczko, Mychailo B.; Zhai, Ziqing; Bruemmer, Stephen M.

SCC initiation behavior of 15% cold forged specimens cut from four different alloy 182 weldments was investigated in 360°C simulated PWR primary water under constant load at the yield stress using direct current potential drop to perform in-situ monitoring of SCC initiation time. Within each weldment, one or more specimens underwent SCC initiation within 24 hours of reaching full load while some specimens had much longer initiation times, in a few cases exceeding 2500 hours. Detailed examinations were conducted on these specimens with a focus on different microstructural features such as preexisting defects, grain orientation and second phases, highlighting anmore » important role of microstructure in crack initiation of alloy 182.« less

Process Model for Friction Stir Welding

NASA Technical Reports Server (NTRS)

Adams, Glynn

1996-01-01

Friction stir welding (FSW) is a relatively new process being applied for joining of metal alloys. The process was initially developed by The Welding Institute (TWI) in Cambridge, UK. The FSW process is being investigated at NASA/MSEC as a repair/initial weld procedure for fabrication of the super-light-weight aluminum-lithium shuttle external tank. The FSW investigations at MSFC were conducted on a horizontal mill to produce butt welds of flat plate material. The weldment plates are butted together and fixed to a backing plate on the mill bed. A pin tool is placed into the tool holder of the mill spindle and rotated at approximately 400 rpm. The pin tool is then plunged into the plates such that the center of the probe lies at, one end of the line of contact, between the plates and the shoulder of the pin tool penetrates the top surface of the weldment. The weld is produced by traversing the tool along the line of contact between the plates. A lead angle allows the leading edge of the shoulder to remain above the top surface of the plate. The work presented here is the first attempt at modeling a complex phenomenon. The mechanical aspects of conducting the weld process are easily defined and the process itself is controlled by relatively few input parameters. However, in the region of the weld, plasticizing and forging of the parent material occurs. These are difficult processes to model. The model presented here addresses only variations in the radial dimension outward from the pin tool axis. Examinations of the grain structure of the weld reveal that a considerable amount of material deformation also occurs in the direction parallel to the pin tool axis of rotation, through the material thickness. In addition, measurements of the axial load on the pin tool demonstrate that the forging affect of the pin tool shoulder is an important process phenomenon. Therefore, the model needs to be expanded to account for the deformations through the material thickness and the forging affect of the shoulder. The energy balance at the boundary of the plastic region with the environment required that energy flow away from the boundary in both radial directions. One resolution to this problem may be to introduce a time dependency into the process model, allowing the energy flow to oscillate across this boundary. Finally, experimental measurements are needed to verify the concepts used here and to aid in improving the model.

Quality Enhancement of Ultrasonic TOFD Signals from Carbon Steel Weld Pad with Notches.

PubMed

Manjula, K; Vijayarekha, K; Venkatraman, B

2018-03-01

Welding is an integral part of component fabrication in industry. Even though the science and art of welding are more than 100 years old, defects continue to occur during welding. Codes of practice require that the welds be tested and evaluated. Conventionally ultrasonic testing has been widely applied in industry for the detection and evaluation of the flaws/defects in the weldments. With advances in sensor and signal analysis technologies, the last two decades have seen extensive developments in the field of ultrasonic testing. We have advanced techniques such as Time of Flight Diffraction (TOFD) which has better probability of detection for linear defects. A major irritant during the application of TOFD, especially for the testing of carbon steel weldments, is the presence of noise. A variety of approaches has been used internationally for the suppression of such noise and each has its own merits and demerits. This paper focuses on a method of enhancing the TOFD A-scan signals in carbon steel weldments by suppressing the noise from them using the discrete wavelet transform (DWT). The analysis clearly indicates that the DWT gives better signal-to-noise ratio improvement using higher-order wavelet filters with 4-level DWT decomposition. However the computational cost of this signal enhancement depends on the wavelet filter chosen along with the chosen level of DWT decomposition. Copyright © 2017 Elsevier B.V. All rights reserved.

Investigation of galvanic corrosion in laser-welded stainless steel sheets

NASA Astrophysics Data System (ADS)

Kwok, Chi-Tat; Fong, Siu Lung; Cheng, Fai Tsun; Man, Hau-Chung

2004-10-01

In the present study, bead-on-plate specimens of 1-mm sheets of austenitic and duplex stainless steels were fabricated by laser penetration welding with a 2.5-kW CW Nd:YAG laser. The galvanic corrosion behavior of laser-weldment (LW) against as-received (AR) specimens with an area rato of 1:1 in 3.5% NaCL solution was studied by means of a zero-resistance ammeter. The free corrosion potentials of as-received specimens were found to be considerably higher than those of laser weldments, indicating that the weldments are more active and always act as anodes. The ranking of galvanic current densities (IG) of the couples in ascending order is: AR S31603-LW S31603 < AR S31803-LW S31803 < AR S32760-LW S32760 < AR S30400-LW S30400. For the galvanic couple between AR S30400 and LW S30400, the IG is the highest (78.6 nA/cm2) because large amount of δ-ferrite in the weld zone acts as active sites. On the other hand, the IG of the galvanic couple between AR S31603 and LW S31603 is the lowest (-26 nA/cm2) because no δ-ferrite is present after laser welding. The recorded IG of all couples revealed constantly low values (in the rnage of nA/cm2) and sometimes stayed negative, which indicated polarity reversal.

The use of supercomputer modelling of high-temperature failure in pipe weldments to optimize weld and heat affected zone materials property selection

NASA Astrophysics Data System (ADS)

Wang, Z. P.; Hayhurst, D. R.

1994-07-01

The creep deformation and damage evolution in a pipe weldment has been modeled by using the finite-element continuum damage mechanics (CDM) method. The finite-element CDM computer program DAMAGE XX has been adapted to run with increased speed on a Cray XMP/416 supercomputer. Run times are sufficiently short (20 min) to permit many parametric studies to be carried out on vessel lifetimes for different weld and heat affected zone (HAZ) materials. Finite-element mesh sensitivity was studied first in order to select a mesh capable of correctly predicting experimentally observed results using at least possible computer time. A study was then made of the effect on the lifetime of a butt welded vessel of each of the commomly measured material parameters for the weld and HAZ materials. Forty different ferritic steel welded vessels were analyzed for a constant internal pressure of 45.5 MPa at a temperature of 565 C; each vessel having the same parent pipe material but different weld and HAZ materials. A lifetime improvement has been demonstrated of 30% over that obtained for the initial materials property data. A methodology for weldment design has been established which uses supercomputer-based CDM analysis techniques; it is quick to use, provides accurate results, and is a viable design tool.

Experimental Investigation of Material Flows Within FSWs Using 3D Tomography

DOE Office of Scientific and Technical Information (OSTI.GOV)

Charles R. Tolle; Timothy A. White; Karen S. Miller

2008-06-01

There exists significant prior work using tracers or pre-placed hardened markers within friction stir welding (FSWing) to experimentally explore material flow within the FSW process. Our experiments replaced markers with a thin sheet of copper foil placed between the 6061 aluminum lap and butt joints that were then welded. The absorption characteristics of x-rays for copper and aluminum are significantly different allowing for non-destructive evaluation (NDE) methods such as x-ray computed tomography (CT) to be used to demonstrate the material movement within the weldment on a much larger scale than previously shown. 3D CT reconstruction of the copper components ofmore » the weldment allows for a unique view into the final turbulent state of the welding process as process parameters are varied. The x-ray CT data of a section of the weld region was collected using a cone-beam x-ray imaging system developed at the INL. Six-hundred projections were collected over 360-degrees using a 160-kVp Bremsstrahlung x-ray generator (25-micrometer focal spot) and amorphoussilicon x-ray detector. The region of the object that was imaged was about 3cm tall and 1.5cm x 1cm in cross section, and was imaged at a magnification of about 3.6x. The data were reconstructed on a 0.5x0.5x0.5 mm3 voxel grid. After reconstruction, the aluminum and copper could be easily discriminated using a gray level threshold allowing visualization of the copper components. Fractal analysis of the tomographic reconstructed material topology is investigated as a means to quantify macro level material flow based on process parameters. The results of multi-pass FSWs show increased refinement of the copper trace material. Implications of these techniques for quantifying process flow are discussed.« less

Study on Microstructure and Mechanical Properties of 304 Stainless Steel Joints by Tig-Mig Hybrid Welding

NASA Astrophysics Data System (ADS)

Ogundimu, Emmanuel O.; Akinlabi, Esther T.; Erinosho, Mutiu F.

Stainless steel is a family of Fe-based alloys having excellent resistance to corrosion and as such has been used imperatively for kitchen utensils, transportation, building constructions and much more. This paper presents the work conducted on the material characterizations of a tungsten inert gas (TIG)-metal inert gas (MIG) hybrid welded joint of type 304 austenitic stainless steel. The welding processes were conducted in three phases. The phases of welding employed are MIG welding using a current of 170A, TIG welding using a current of 190A, and a hybrid TIG-MIG welding with currents of 190/170A, respectively. The MIG, TIG, and hybrid TIG-MIG weldments were characterized with incomplete penetration, full penetration and excess penetration of weld. Intergranular austenite was created toward transition and heat affected zones. The thickness of the delta ferrite (δ-Fe) formed in the microstructures of the TIG weld is more than the thickness emerged in the microstructures of MIG and hybrid TIG-MIG welds. A TIG-MIG hybrid weld of specimen welded at the currents of 190/170A has the highest ultimate tensile strength value and percentage elongation of 397.72MPa and 35.7%. The TIG-MIG hybrid welding can be recommended for high-tech industrial applications such as nuclear, aircraft, food processing, and automobile industry.

Hybrid Laser-Arc Welding of 10-mm-Thick Cast Martensitic Stainless Steel CA6NM: As-Welded Microstructure and Mechanical Properties

NASA Astrophysics Data System (ADS)

Mirakhorli, Fatemeh; Cao, Xinjin; Pham, Xuan-Tan; Wanjara, Priti; Fihey, Jean-Luc

2016-07-01

Cast CA6NM martensitic stainless steel plates, 10 mm in thickness, were welded using hybrid laser-arc welding. The effect of different welding speeds on the as-welded joint integrity was characterized in terms of the weld bead geometry, defects, microstructure, hardness, ultimate tensile strength, and impact energy. Significant defects such as porosity, root humping, underfill, and excessive penetration were observed at a low welding speed (0.5 m/min). However, the underfill depth and excessive penetration in the joints manufactured at welding speeds above 0.75 m/min met the specifications of ISO 12932. Characterization of the as-welded microstructure revealed untempered martensite and residual delta ferrite dispersed at prior-austenite grain boundaries in the fusion zone. In addition, four different heat-affected zones in the weldments were differentiated through hardness mapping and inference from the Fe-Cr-Ni ternary phase diagram. The tensile fracture occurred in the base metal for all the samples and fractographic analysis showed that the crack path is within the martensite matrix, along primary delta ferrite-martensite interfaces and within the primary delta ferrite. Additionally, Charpy impact testing demonstrated slightly higher fracture energy values and deeper dimples on the fracture surface of the welds manufactured at higher welding speeds due to grain refinement and/or lower porosity.

Post-weld Tempered Microstructure and Mechanical Properties of Hybrid Laser-Arc Welded Cast Martensitic Stainless Steel CA6NM

NASA Astrophysics Data System (ADS)

Mirakhorli, Fatemeh; Cao, Xinjin; Pham, Xuan-Tan; Wanjara, Priti; Fihey, Jean-Luc

2016-12-01

Manufacturing of hydroelectric turbine components involves the assembly of thick-walled stainless steels using conventional multi-pass arc welding processes. By contrast, hybrid laser-arc welding may be an attractive process for assembly of such materials to realize deeper penetration depths, higher production rates, narrower fusion, and heat-affected zones, and lower distortion. In the present work, single-pass hybrid laser-arc welding of 10-mm thick CA6NM, a low carbon martensitic stainless steel, was carried out in the butt joint configuration using a continuous wave fiber laser at its maximum power of 5.2 kW over welding speeds ranging from 0.75 to 1.2 m/minute. The microstructures across the weldment were characterized after post-weld tempering at 873 K (600 °C) for 1 hour. From microscopic examinations, the fusion zone was observed to mainly consist of tempered lath martensite and some residual delta-ferrite. The mechanical properties were evaluated in the post-weld tempered condition and correlated to the microstructures and defects. The ultimate tensile strength and Charpy impact energy values of the fully penetrated welds in the tempered condition were acceptable according to ASTM, ASME, and industrial specifications, which bodes well for the introduction of hybrid laser-arc welding technology for the manufacturing of next generation hydroelectric turbine components.

Heat sink effects on weld bead: VPPA process

NASA Technical Reports Server (NTRS)

Steranka, Paul O., Jr.

1990-01-01

An investigation into the heat sink effects due to weldment irregularities and fixtures used in the variable polarity plasma arc (VPPA) process was conducted. A basic two-dimensional model was created to represent the net heat sink effect of surplus material using Duhamel's theorem to superpose the effects of an infinite number of line heat sinks of variable strength. Parameters were identified that influence the importance of heat sink effects. A characteristic length, proportional to the thermal diffusivity of the weldment material divided by the weld torch travel rate, correlated with heat sinking observations. Four tests were performed on 2219-T87 aluminum plates to which blocks of excess material were mounted in order to demonstrate heat sink effects. Although the basic model overpredicted these effects, it correctly indicated the trends shown in the experimental study and is judged worth further refinement.

Heat sink effects on weld bead: VPPA process

NASA Technical Reports Server (NTRS)

Steranka, Paul O., Jr.

1989-01-01

An investigation into the heat sink effects due to weldment irregularities and fixtures used in the variable polarity plasma arc (VPPA) process was conducted. A basic two-dimensional model was created to represent the net heat sink effect of surplus material using Duhamel's theorem to superpose the effects of an infinite number of line heat sinks of variable strength. Parameters were identified that influence the importance of heat sink effects. A characteristic length, proportional to the thermal diffusivity of the weldment material divided by the weld torch travel rate, correlated with heat sinking observations. Four tests were performed on 2219-T87 aluminum plates to which blocks of excess material were mounted in order to demonstrate heat sink effects. Although the basic model overpredicted these effects, it correctly indicated the trends shown in the experimental study and is judged worth further refinement.

Mechanical Behavior of Commercially Pure Titanium Weldments at Lower Temperatures

NASA Astrophysics Data System (ADS)

Gupta, R. K.; Anil Kumar, V.; Xavier, X. Roshan

2018-05-01

Commercially pure titanium is used for low-temperature applications due to good toughness attributed to single-phase microstructure (α). Electron beam welding (EBW) and gas tungsten arc welding (GTAW) processes have been used for welding two grades of commercially pure titanium (Grade 2 and Grade 4). Martensitic microstructure is found to be finer in the case of EBW joint as compared to GTAW joint due to faster rate of cooling in the former process. Weldments have been characterized to study the mechanical behavior at ambient (298 K) and cryogenic temperatures (20 and 77 K). Strength of weldments increases with the decrease in temperature, which is found to be more prominent in case of Grade 4 titanium as compared to Grade 2. Weld efficiency of Grade 4 is found to be higher at all the temperatures (ambient, 77 and 20 K). However, ultimate tensile strength/yield strength ratio is higher for Grade 2 as compared to Grade 4. % Elongation is found to increase/retained at cryogenic temperatures for Grade 2, and it is found to decrease for Grade 4. Electron backscattered diffraction analysis and transmission electron microscopy of deformed samples confirmed the presence of extensive twinning in Grade 2 and the presence of finer martensitic structure in Grade 4. Fractography analysis of tested specimens revealed the presence of cleavage facets in Grade 4 and dimples in specimens of Grade 2. Higher strength in Grade 4 is attributed to higher oxygen restricting the twin-assisted slip, which is otherwise prominent in Grade 2 titanium.

Fracture and crack growth resistance studies of 304 stainless steel weldments relating to retesting of cryogenic vessels

NASA Technical Reports Server (NTRS)

Hall, L. R.; Finger, R. W.

1972-01-01

Fracture and crack growth resistance characteristics of 304 stainless steel alloy weldments as relating to retesting of cryogenic vessels were examined. Welding procedures were typical of those used in full scale vessel fabrication. Fracture resistance survey tests were conducted in room temperature air, liquid nitrogen and liquid hydrogen. In air, both surface-flawed and center-cracked panels containing cracks in weld metal, fusion line, heat-affected zone, or parent metal were tested. In liquid nitrogen and liquid hydrogen, tests were conducted using center-cracked panels containing weld centerline cracks. Load-unload, sustained load, and cyclic load tests were performed in air or hydrogen gas, liquid nitrogen, and liquid hydrogen using surface-flawed specimens containing weld centerline cracks. Results were used to evaluate the effectiveness of periodic proof overloads in assuring safe and reliable operation of over-the-road cryogenic dewars.

Grain Refinement of AZ31 Magnesium Alloy Weldments by AC Pulsing Technique

NASA Astrophysics Data System (ADS)

Kishore Babu, N.; Cross, C. E.

2012-11-01

The current study has investigated the influence of alternating current pulsing on the structure and mechanical properties of AZ31 magnesium alloy gas tungsten arc (GTA) weldments. Autogenous full penetration bead-on-plate GTA welds were made under a variety of conditions including variable polarity (VP), variable polarity mixed (VPM), alternating current (AC), and alternating current pulsing (ACPC). AC pulsing resulted in significant refinement of weld metal when compared with the unpulsed conditions. AC pulsing leads to relatively finer and more equiaxed grain structure in GTA welds. In contrast, VP, VPM, and AC welding resulted in predominantly columnar grain structures. The reason for this grain refinement may be attributed to the periodic variations in temperature gradient and solidification rate associated with pulsing as well as weld pool oscillation observed in the ACPC welds. The observed grain refinement was shown to result in an appreciable increase in fusion zone hardness, tensile strength, and ductility.

Practicable methods for histological section thickness measurement in quantitative stereological analyses.

PubMed

Matenaers, Cyrill; Popper, Bastian; Rieger, Alexandra; Wanke, Rüdiger; Blutke, Andreas

2018-01-01

The accuracy of quantitative stereological analysis tools such as the (physical) disector method substantially depends on the precise determination of the thickness of the analyzed histological sections. One conventional method for measurement of histological section thickness is to re-embed the section of interest vertically to its original section plane. The section thickness is then measured in a subsequently prepared histological section of this orthogonally re-embedded sample. However, the orthogonal re-embedding (ORE) technique is quite work- and time-intensive and may produce inaccurate section thickness measurement values due to unintentional slightly oblique (non-orthogonal) positioning of the re-embedded sample-section. Here, an improved ORE method is presented, allowing for determination of the factual section plane angle of the re-embedded section, and correction of measured section thickness values for oblique (non-orthogonal) sectioning. For this, the analyzed section is mounted flat on a foil of known thickness (calibration foil) and both the section and the calibration foil are then vertically (re-)embedded. The section angle of the re-embedded section is then calculated from the deviation of the measured section thickness of the calibration foil and its factual thickness, using basic geometry. To find a practicable, fast, and accurate alternative to ORE, the suitability of spectral reflectance (SR) measurement for determination of plastic section thicknesses was evaluated. Using a commercially available optical reflectometer (F20, Filmetrics®, USA), the thicknesses of 0.5 μm thick semi-thin Epon (glycid ether)-sections and of 1-3 μm thick plastic sections (glycolmethacrylate/ methylmethacrylate, GMA/MMA), as regularly used in physical disector analyses, could precisely be measured within few seconds. Compared to the measured section thicknesses determined by ORE, SR measures displayed less than 1% deviation. Our results prove the applicability of SR to efficiently provide accurate section thickness measurements as a prerequisite for reliable estimates of dependent quantitative stereological parameters.

Practicable methods for histological section thickness measurement in quantitative stereological analyses

PubMed Central

Matenaers, Cyrill; Popper, Bastian; Rieger, Alexandra; Wanke, Rüdiger

2018-01-01

The accuracy of quantitative stereological analysis tools such as the (physical) disector method substantially depends on the precise determination of the thickness of the analyzed histological sections. One conventional method for measurement of histological section thickness is to re-embed the section of interest vertically to its original section plane. The section thickness is then measured in a subsequently prepared histological section of this orthogonally re-embedded sample. However, the orthogonal re-embedding (ORE) technique is quite work- and time-intensive and may produce inaccurate section thickness measurement values due to unintentional slightly oblique (non-orthogonal) positioning of the re-embedded sample-section. Here, an improved ORE method is presented, allowing for determination of the factual section plane angle of the re-embedded section, and correction of measured section thickness values for oblique (non-orthogonal) sectioning. For this, the analyzed section is mounted flat on a foil of known thickness (calibration foil) and both the section and the calibration foil are then vertically (re-)embedded. The section angle of the re-embedded section is then calculated from the deviation of the measured section thickness of the calibration foil and its factual thickness, using basic geometry. To find a practicable, fast, and accurate alternative to ORE, the suitability of spectral reflectance (SR) measurement for determination of plastic section thicknesses was evaluated. Using a commercially available optical reflectometer (F20, Filmetrics®, USA), the thicknesses of 0.5 μm thick semi-thin Epon (glycid ether)-sections and of 1–3 μm thick plastic sections (glycolmethacrylate/ methylmethacrylate, GMA/MMA), as regularly used in physical disector analyses, could precisely be measured within few seconds. Compared to the measured section thicknesses determined by ORE, SR measures displayed less than 1% deviation. Our results prove the applicability of SR to efficiently provide accurate section thickness measurements as a prerequisite for reliable estimates of dependent quantitative stereological parameters. PMID:29444158

Tensile Behavior of Electron Beam-Welded and Post-Weld Vacuum-Annealed Nb-10% Hf-1% Ti Refractory Alloy Weldments

NASA Astrophysics Data System (ADS)

Anil Kumar, V.; Gupta, R. K.; Venkateswaran, T.; Ram Kumar, P.

2018-02-01

Nb-10% Hf-1% Ti refractory alloy is a high performance material extensively used for high temperature applications. Electron beam welding is one of the most widely used techniques to join refractory and reactive alloys. Bigger sizes of nozzles for rocket propulsion applications can be either made through deep drawing and flow turning route or by roll bending and welding route both using sheets/plates as input material for fabrication. The latter is a more economical option for mass production of the hardware using such exotic and expensive alloys. In view of this, both as-welded (AW) coupon and weld plus post-weld vacuum-annealed (AW + VA) coupon have been prepared to study their mechanical behavior. It has been observed that tensile strength and ductility have not been reduced in both these conditions vis-à-vis the base metal, confirming weld efficiency of the alloy to be 100%. Microhardness is found to be 150-160 VHN in the base metal and 200-225 VHN in the weld fusion zone in AW condition, which became uniform (145-155 VHN) throughout the weldment in AW + VA condition. Microstructure of the weldment in AW condition is found to be consisting of grains solidified by epitaxial mode from base metal toward the weld centre. In AW + VA condition, improvement in tensile elongation is observed, which is found to be due to the presence of homogenized grains/more uniform microstructure near the heat-affected zone as compared to the steep gradient in grain size in different zones in the weld in AW condition.

Finite element modeling of residual stresses in electroslag butt welds

DOT National Transportation Integrated Search

2000-03-01

Shop fabricated electroslag (ES) welds used in bridge construction have had a history of low toughness in the fusion and heat affected zones. In addition, conventional inspection of ES weldments under shop fabrication conditions fail to consistently ...

Brittle-ductile transition of steel bridges, volume I : final report.

DOT National Transportation Integrated Search

1990-05-01

The transition behavior of bridge steels and weldments largely determines the ir toughness under : service loading rates and temperatures. Two aspects of the transition were investigated in this : project: The first was to develop a better understand...

Milder Etchant For Penetrant Inspection

NASA Technical Reports Server (NTRS)

O'Tousa, Joseph E.; Thomas, Clark S.

1990-01-01

New etching solution for chemical penetrant inspection of Inconel(R) 718 castings and weldments. Etchant does not introduce artifacts mistaken for defects. Applied by swabbing or by immersion. Used to detect unwanted residues of Nioro(R) (or equivalent) gold brazing alloy on type 347 stainless steel.

An air-bearing weight offload system for ground test of heavy LSS structures

NASA Technical Reports Server (NTRS)

Rice, R. B.

1989-01-01

The capability and use of the Gravity Offload Facility (GOF) are discussed. Briefly explained are the: truss and base casting; carriage assembly; carriage weldment; vertical lift axis control; lifting cylinder; payload gimbal; motion base layout; and control processor.

The microstructure and fracture behavior of the dissimilar alloy 690-SUS 304L joint with various Nb addition

NASA Astrophysics Data System (ADS)

Lee, H. T.; Jeng, S. L.; Kuo, T. Y.

2003-05-01

This study investigates the microstructure and fracture behavior of dissimilar weldments of alloy 690 and SUS 304L for various additions of niobium (0.1, 1.03, 2.49, and 3.35 wt pct) in the flux. With identical parameters and procedures, weldments were butt welded by the shielding metal arc welding (SMAW) process using three layers, with each layer being deposited in a single pass. The results indicate that the microstructure of the fusion zone was primarily dendritic and that the contents of Ni, Cr, and Fe within this zone remain relatively constant and resemble alloy 690. With Nb addition, it is noted that the microstructure changes from a cellular to columnar dendrite and equiaxed dendrite. Meanwhile, the dendrite arm spacing reduces and the secondary arms grow longer. Moreover, the composition of the interdendritic phase, whose precipitate volume percentage increases from 5 to 25 pct, changes from Al-Ti-O to Nb rich. The spread of the interdendritic phase is less in the root bead than in the cap bead due to the greater influence of base metal dilution in this region. Mechanical tests indicate that Nb addition increases the average hardness of the weldment and reduces its elongation prior to rupture. However, the tensile strength is essentially unchanged by Nb addition. It is found that the average hardness of the root bead is generally lower than the cap bead, and that the tensile specimens all rupture in the fusion zone, with the fracture surfaces exhibiting ductile features. It is noted that the cap bead tends to rupture interdendritically with increasing Nb addition. Finally, fractography shows that the dimples in the root become larger and shallower with Nb addition and are rich with an interdendritic phase.

Investigating the Effects of Pin Tool Design on Friction Stir Welded Ti-6Al-4V

NASA Technical Reports Server (NTRS)

Rubisoff, H. A.; Querin, J. A.; Schneider, Judy A.; Magee, D.

2009-01-01

Friction stir welding (FSWing), a solid state joining technique, uses a non-consumable rotating pin tool to thermomechanically join materials. Heating of the weldment caused by friction and deformation is a function of the interaction between the pin tool and the work piece. Therefore, the geometry of the pin tool is in part responsible for the resulting microstructure and mechanical properties. In this study microwave sintered tungsten carbide (WC) pin tools with tapers and flats were used to FSW Ti-6Al-4V. Transverse sections of welds were mechanically tested, and the microstructure was characterized using optical microscopy (OM) and scanning election microscopy (SEM). X-ray diffraction (XRD) and electron back-scatter diffraction (EBSD) were used to characterize the texture within the welds produced from the different pin tool designs.

SEM stereo-section fractography (SSF) observations

DOE Office of Scientific and Technical Information (OSTI.GOV)

Zhang, X.J.; Tregoning, R.L.; Armstrong, R.W.

1997-12-31

Cleavage initiation in engineering materials is governed by local microstructural inhomogeneities. These features are often the principal reason for the large scatter evident in fracture toughness measurements which, in extreme cases, can mask the fundamental relationship between cracking resistance and global material properties. The SEM stereo-section fractography (SSF) technique can be used to carefully evaluate these local inhomogeneities through simultaneous observation of both the fracture surface and the underlying microstructure. By sectioning the fracture surface close to the cleavage initiation site (within 10 {micro}m), and perpendicular to both the fracture surface and the precrack front, a direct correspondence between initiationmore » and the local microstructure can be established. Information obtained from this technique can provide quantitative input about important, local microstructural features which can then be used to calibrate or create realistic micromechanical models. A compendium of SSF results is presented herein for cleavage cracking in disparate materials (A533B steel plates, MIL-70S multi-pass weldments, and Ti6A14V forgings), under various testing conditions. In each case, the SSF technique was able to unambiguously identify the dominant, local features which triggered cleavage initiation.« less

SEM stereo-section fractography observations. Final report

DOE Office of Scientific and Technical Information (OSTI.GOV)

Zhang, X.J.; Tregoning, R.L.; Armstrong, R.W.

1998-05-01

Cleavage initiation in engineering materials is governed by local microstructural inhomogeneities. These features are often the principal reason for the large scatter evident in fracture toughness measurements which, in extreme cases, can mask the fundamental relationship between cracking resistance and global material properties. The SEM stereo-section fractography (SSF) technique can be used to carefully evaluate these local inhomogeneities through simultaneous observation of both the fracture surface and the underlying microstructure. By sectioning the fracture surface close to the cleavage initiation site (within 10 microns), and perpendicular to both the fracture surface and the pre crack front, a direct correspondence betweenmore » initiation and the local microstructure can be established. Information obtained from this technique can provide quantitative input about important, local microstructural features which can then be used to calibrate or create realistic micromechanical models. A compendium of SSF results is presented herein for cleavage cracking in disparate materials (A533B steel plates, MIL-70S multi-pass weldments, and Ti6A14V forgings), under various testing conditions. In each case, the SSF technique was able to unambiguously identify the dominant, local features which triggered cleavage initiation.« less

Effects of surface preparation on quality of aluminum alloy weldments

NASA Technical Reports Server (NTRS)

Kizer, D.; Saperstein, Z.

1968-01-01

Study of surface preparations and surface contamination effects on the welding of 2014 aluminum involves several methods of surface analysis to identify surface properties conducive to weld defects. These methods are radioactive evaporation, spectral reflectance mass spectroscopy, gas chromatography and spark emission spectroscopy.

Effects of high frequency current in welding aluminum alloy 6061

NASA Technical Reports Server (NTRS)

Fish, R. E.

1968-01-01

Uncontrolled high frequency current causes cracking in the heat-affected zone of aluminum alloy 6061 weldments during tungsten inert gas ac welding. Cracking developed when an improperly adjusted superimposed high frequency current was agitating the semimolten metal in the areas of grain boundary.

The effects of alloying elements on microstructures and mechanical properties of tungsten inert gas welded AZ80 magnesium alloys joint

NASA Astrophysics Data System (ADS)

Li, Hui; Zhang, Jiansheng; Ding, Rongrong

2017-11-01

The effects of alloying elements on the macrostructures, microstructures and tensile strength of AZ80 Mg alloy weldments were studied in the present study. The results indicate that with the decrease of Al element content of filler wire, the welding defects of seam are gradually eliminated and the β-Mg17Al12 phases at α-Mg boundaries are refined and become discontinuous, which are beneficial to the improvement of tensile strength. With AZ31 Mg alloy filler wire, the maximum tensile strength of AZ80 weldment is 220 MPa and fracture occurs at the welding seam of joint. It is experimentally proved that robust AZ80 Mg alloy joints can be obtained by tungsten inert gas (TIG) welding process with AZ31 Mg alloy filler wire. However, further study is required to improve the microstructures and reduce welding defects of joint in order to further improve the joining strength of AZ80 Mg alloy joint.

Development of electromagnetic welding facility of flat plates for nuclear industry

NASA Astrophysics Data System (ADS)

Kumar, Rajesh; Sahoo, Subhanarayan; Sarkar, Biswanath; Shyam, Anurag

2017-04-01

Electromagnetic pulse welding (EMPW) process, one of high speed welding process uses electromagnetic force from discharged current through working coil, which develops a repulsive force between the induced current flowing parallel and in opposite direction. For achieving the successful weldment using this process the design of working coil is the most important factor due to high magnetic field on surface of work piece. In case of high quality flat plate welding factors such as impact velocity, angle of impact standoff distance, thickness of flyer and overlap length have to be chosen carefully. EMPW has wide applications in nuclear industry, automotive industry, aerospace, electrical industries. However formability and weldability still remain major issues. Due to ease in controlling the magnetic field enveloped inside tubes, the EMPW has been widely used for tube welding. In case of flat components control of magnetic field is difficult. Hence the application of EMPW gets restricted. The present work attempts to make a novel contribution by investigating the effect of process parameters on welding quality of flat plates. The work emphasizes the approaches and engineering calculations required to effectively use of actuator in EMPW of flat components.

Study of the Performance of Stainless Steel A-TIG Welds

NASA Astrophysics Data System (ADS)

Shyu, S. W.; Huang, H. Y.; Tseng, K. H.; Chou, C. P.

2008-04-01

The purpose of the present work was to investigate the effect of oxide fluxes on weld morphology, arc voltage, mechanical properties, angular distortion and hot cracking susceptibility obtained with TIG welding, which applied to the welding of 5 mm thick austenitic stainless steel plates. A novel variant of the autogenous TIG welding process, oxide powders (Al2O3, Cr2O3, TiO2, SiO2 and CaO) was applied on a type 304 stainless steel through a thin layer of the flux to produce a bead on plate welds. The experimental results indicated that the increase in the penetration is significant with the use of Cr2O3, TiO2, and SiO2. A-TIG welding can increase the weld depth to bead-width ratio, and tends to reduce the angular distortion of the weldment. It was also found that A-TIG welding can increase the retained delta-ferrite content of stainless steel 304 welds and, in consequence, the hot-cracking susceptibility of as-welded is reduced. Physically constricting the plasma column and reducing the anode spot are the possible mechanism for the effect of certain flux on A-TIG penetration.

46 CFR 56.50-105 - Low-temperature piping.

Code of Federal Regulations, 2010 CFR

2010-10-01

... ASTM E 23 (incorporated by reference, see § 56.01-2), “Notched Bar Impact Testing of Metallic Materials”, Type A, Figure 4. The toughness testing requirements of subpart 54.05 of this subchapter shall be... testing of production weldments for low temperature piping systems and assemblies is not required. (3...

Saturn S-2 quality assurance techniques: Nondestructive testing processes. Volume 1: Requirements and procedures

NASA Technical Reports Server (NTRS)

Eller, H. H.; Sugg, F. E.

1970-01-01

The methods and procedures used to perform nondestructive testing inspections of the Saturn S-2 liquid hydrogen and liquid oxygen tank weldments during fabrication and after proof testing are described to document special skills developed during the program. All post-test inspection requirements are outlined including radiographic inspections procedures.

46 CFR 54.05-15 - Weldment toughness tests-procedure qualifications.

Code of Federal Regulations, 2010 CFR

2010-10-01

...) Plate for which Charpy V-notch impact testing is required in the parent material and for which V-notch minima are specified shall similarly have welding procedures qualified for toughness by Charpy V-notch testing. For these tests, the test plates shall be oriented with their final rolling direction parallel to...

A Review of Weldment Failure Modes and Weldability Testing Methods.

DTIC Science & Technology

1994-01-01

tearing ...................................... 9 4a. Macrostructure of reheat cracking in a chromium -molybdenum.vanadium steel ................ 10 4b...Figure 5. Schematic of the subscale varesatrai teSL 12 all1൒ 2.5cm rl SPOT WELD TOP VIEW SPECIMEN • GTAW TORCH F 4 -DIE BLOCK SIDE VIEW FORCE Figure

Stress-Intensity Factors for Three-Point Bend Specimens by Boundary Collocation

DTIC Science & Technology

1965-12-01

ref. 5) and by Kies, Smith, Romine, and Bernstein (ref. 6). Limited results of an analytical study by H. F. Bueckner have been published by Wundt (ref...Weldments. Fracture Toughness Testing and Its Applications, STP No. 381, ASTM, 1965, pp. 328-356. 7. Wundt , B. M.: A Unified Interpretation of Room

Life Assessment for Cr-Mo Steel Dissimilar Joints by Various Filler Metals Using Accelerated Creep Testing

NASA Astrophysics Data System (ADS)

Petchsang, S.; Phung-on, I.; Poopat, B.

2016-12-01

Accelerated creep rupture tests were performed on T22/T91 dissimilar metal joints to determine the fracture location and rupture time of different weldments. Four configurations of deposited filler metal were tested using gas tungsten arc welding to estimate the service life for Cr-Mo steel dissimilar joints at elevated temperatures in power plants. Results indicated that failure in all configurations occurred in the tempered original microstructure and tempered austenite transformation products (martensite or bainite structure) as type IV cracking at the intercritical area of the heat-affected zone (ICHAZ) for both T22 and T91 sides rather than as a consequence of the different filler metals. Creep damage occurred with the formation of precipitations and microvoids. The correlation between applied stress and the Larson-Miller parameter (PLM) was determined to predict the service life of each material configuration. Calculated time-to-failure based on the PLM and test results for both temperature and applied stress parameters gave a reasonable fit. The dissimilar joints exhibited lower creep rupture compared to the base material indicating creep degradation of the weldment.

Modeling Long-term Creep Performance for Welded Nickel-base Superalloy Structures for Power Generation Systems

DOE Office of Scientific and Technical Information (OSTI.GOV)

Shen, Chen; Gupta, Vipul; Huang, Shenyan

The goal of this project is to model long-term creep performance for nickel-base superalloy weldments in high temperature power generation systems. The project uses physics-based modeling methodologies and algorithms for predicting alloy properties in heterogeneous material structures. The modeling methodology will be demonstrated on a gas turbine combustor liner weldment of Haynes 282 precipitate-strengthened nickel-base superalloy. The major developments are: (1) microstructure-property relationships under creep conditions and microstructure characterization (2) modeling inhomogeneous microstructure in superalloy weld (3) modeling mesoscale plastic deformation in superalloy weld and (4) a constitutive creep model that accounts for weld and base metal microstructure and theirmore » long term evolution. The developed modeling technology is aimed to provide a more efficient and accurate assessment of a material’s long-term performance compared with current testing and extrapolation methods. This modeling technology will also accelerate development and qualification of new materials in advanced power generation systems. This document is a final technical report for the project, covering efforts conducted from October 2014 to December 2016.« less

Microstructure, Composition, and Impact Toughness Across the Fusion Line of High-Strength Bainitic Steel Weldments

NASA Astrophysics Data System (ADS)

Lan, Liangyun; Kong, Xiangwei; Chang, Zhiyuan; Qiu, Chunlin; Zhao, Dewen

2017-09-01

This paper analyzed the evolution of microstructure, composition, and impact toughness across the fusion line of high-strength bainitic steel weldments with different heat inputs. The main purpose was to develop a convenient method to evaluate the HAZ toughness quickly. The compositions of HAZ were insensitive to higher contents of alloy elements ( e.g., Ni, Mo) in the weld metal because their diffusion distance is very short into the HAZ. The weld metal contained predominantly acicular ferrite at any a heat input, whereas the main microstructures in the HAZ changed from lath martensite/bainite to upper bainite with the increasing heat input. The evolution of HAZ toughness in relation to microstructural changes can be revealed clearly combined with the impact load curve and fracture morphology, although the results of impact tests do not show an obvious change with heat input because the position of Charpy V notch contains the weld metal, HAZ as well as a part of base metal. As a result, based on the bead-on-plate welding tests, the welding parameter affecting the HAZ toughness can be evaluated rapidly.

Study on underclad cracking in nuclear reactor vessel steels

DOE Office of Scientific and Technical Information (OSTI.GOV)

Horiya, T.; Takeda, T.; Yamato, K.

1985-02-01

Susceptibility to underclad cracking in nuclear reactor vessel steels, such as SA533 Grade B Class 1 and SA508 Class 2, was studied in detail. A convenient simulation test method using simulated HAZ specimens of small size has been developed for quantitative evaluation of susceptibility to underclad cracks. The method can predict precisely the cracking behavior in weldments of steels with relative low crack susceptibility. The effect of chemical compositions on susceptibility to the cracking was examined systematically using the developed simulation test method and the following index was obtained from the test results: U = 20(V) + 7(C) + 4(Mo)more » + (Cr) + (Cu) - 0.5(Mn) + 1.5 log(X) X = Al . . . Al/2N less than or equal to 1 X = 2N . . . Al/2N > 1 It was confirmed that the new index (U) is useful for the prediction of crack susceptibility of the nuclear vessel steels; i.e., no crack initiation is detected in weldments in the roller bend test for steels having U value below 0.90.« less

Effect of zirconium addition on welding of aluminum grain refined by titanium plus boron

NASA Astrophysics Data System (ADS)

Zaid, A. I. O.

2014-06-01

Aluminum oxidizes freely in ordinary atmosphere which makes its welding difficult and weak, particularly it solidifies in columnar structure with large grains. Therefore, it is anticipated that the effect of addition of some grain refiners to its melt before solidification is worth while investigating as it may enhance its weldabilty and improve its mechanical strength. In this paper, the effect of addition of zirconium at a weight of 0.1% (which corresponds to the peretictic limit on the aluminum-zirconium base phase diagram) to commercially pure aluminum, grain refined by Ti+B on its weldability, using gas tungsten arc welding, GTAW, method which was formerly known as TIG. A constant current level of 30 AC Ampere was used because it removes the oxides during the welding process. Metallographic examination of the weldments of the different combinations of Al with Al and Al with its microalloys: in the heat affected zone, HAZ, and away from it was carried out and examined for HAZ width, porosity, cracks and microhardness. It was found that grain refining by Ti+B or Zr resulted in enhancement of the weldment.

Method for welding an article and terminating the weldment within the perimeter of the article

NASA Technical Reports Server (NTRS)

Snyder, John H. (Inventor); Smashey, Russell W. (Inventor); Boerger, Eric J. (Inventor); Borne, Bruce L. (Inventor)

2000-01-01

An article is welded, as in weld repair of a defect, by positioning a weld lift-off block at a location on the surface of the article adjacent to the intended location of the end of the weldment on the surface of the article. The weld lift-off block has a wedge shape including a base contacting the surface of the article, and an upper face angled upwardly from the base from a base leading edge. A weld pool is formed on the surface of the article by directly heating the surface of the article using a heat source. The heat source is moved relative to the surface of the article and onto the upper surface of the weld lift-off block by crossing the leading edge of the wedge, without discontinuing the direct heating of the article by the heat source. The heating of the article with the heat source is discontinued only after the heat source is directly heating the upper face of the weld lift-off block, and not the article.

Benefit of computer-aided detection analysis for the detection of subsolid and solid lung nodules on thin- and thick-section CT.

PubMed

Godoy, Myrna C B; Kim, Tae Jung; White, Charles S; Bogoni, Luca; de Groot, Patricia; Florin, Charles; Obuchowski, Nancy; Babb, James S; Salganicoff, Marcos; Naidich, David P; Anand, Vikram; Park, Sangmin; Vlahos, Ioannis; Ko, Jane P

2013-01-01

The objective of our study was to evaluate the impact of computer-aided detection (CAD) on the identification of subsolid and solid lung nodules on thin- and thick-section CT. For 46 chest CT examinations with ground-glass opacity (GGO) nodules, CAD marks computed using thin data were evaluated in two phases. First, four chest radiologists reviewed thin sections (reader(thin)) for nodules and subsequently CAD marks (reader(thin) + CAD(thin)). After 4 months, the same cases were reviewed on thick sections (reader(thick)) and subsequently with CAD marks (reader(thick) + CAD(thick)). Sensitivities were evaluated. Additionally, reader(thick) sensitivity with assessment of CAD marks on thin sections was estimated (reader(thick) + CAD(thin)). For 155 nodules (mean, 5.5 mm; range, 4.0-27.5 mm)-74 solid nodules, 22 part-solid (part-solid nodules), and 59 GGO nodules-CAD stand-alone sensitivity was 80%, 95%, and 71%, respectively, with three false-positives on average (0-12) per CT study. Reader(thin) + CAD(thin) sensitivities were higher than reader(thin) for solid nodules (82% vs 57%, p < 0.001), part-solid nodules (97% vs 81%, p = 0.0027), and GGO nodules (82% vs 69%, p < 0.001) for all readers (p < 0.001). Respective sensitivities for reader(thick), reader(thick) + CAD(thick), reader(thick) + CAD(thin) were 40%, 58% (p < 0.001), and 77% (p < 0.001) for solid nodules; 72%, 73% (p = 0.322), and 94% (p < 0.001) for part-solid nodules; and 53%, 58% (p = 0.008), and 79% (p < 0.001) for GGO nodules. For reader(thin), false-positives increased from 0.64 per case to 0.90 with CAD(thin) (p < 0.001) but not for reader(thick); false-positive rates were 1.17, 1.19, and 1.26 per case for reader(thick), reader(thick) + CAD(thick), and reader(thick) + CAD(thin), respectively. Detection of GGO nodules and solid nodules is significantly improved with CAD. When interpretation is performed on thick sections, the benefit is greater when CAD marks are reviewed on thin rather than thick sections.

UAH mathematical model of the variable polarity plasma ARC welding system calculation

NASA Technical Reports Server (NTRS)

Hung, R. J.

1994-01-01

Significant advantages of Variable Polarity Plasma Arc (VPPA) welding process include faster welding, fewer repairs, less joint preparation, reduced weldment distortion, and absence of porosity. A mathematical model is presented to analyze the VPPA welding process. Results of the mathematical model were compared with the experimental observation accomplished by the GDI team.

Cutting Tool For Shaving Weld Beads

NASA Technical Reports Server (NTRS)

Hoffman, David S.; Mcferrin, David C.; Daniel, Ronald L., Jr.; Coby, John B., Jr.; Dawson, Sidney G.

1995-01-01

Cutting tool proposed for use in shaving weld beads flush with adjacent surfaces of weldments. Modified version of commercial pneumatically driven rotary cutting tool, cutting wheel of which turns at speeds sufficient for machining nickel alloys, titanium, and stainless steels. Equipped with forward-mounted handle and rear-mounted skid plate to maximize control and reduce dependence on skill of technician.

46 CFR 54.05-15 - Weldment toughness tests-procedure qualifications.

Code of Federal Regulations, 2012 CFR

2012-10-01

... the weld metal. (2) Three specimens with the notch centered on the fusion line between parent plate and weld. (The fusion line may be identified by etching the specimen with a mild reagent.) (3) Three specimens with the notch centered in the heat affected zone, 1 mm from the fusion line. (4) Same as...

46 CFR 54.05-15 - Weldment toughness tests-procedure qualifications.

Code of Federal Regulations, 2011 CFR

2011-10-01

... the weld metal. (2) Three specimens with the notch centered on the fusion line between parent plate and weld. (The fusion line may be identified by etching the specimen with a mild reagent.) (3) Three specimens with the notch centered in the heat affected zone, 1 mm from the fusion line. (4) Same as...

46 CFR 54.05-15 - Weldment toughness tests-procedure qualifications.

Code of Federal Regulations, 2013 CFR

2013-10-01

... the weld metal. (2) Three specimens with the notch centered on the fusion line between parent plate and weld. (The fusion line may be identified by etching the specimen with a mild reagent.) (3) Three specimens with the notch centered in the heat affected zone, 1 mm from the fusion line. (4) Same as...

46 CFR 54.05-15 - Weldment toughness tests-procedure qualifications.

Code of Federal Regulations, 2014 CFR

2014-10-01

... the weld metal. (2) Three specimens with the notch centered on the fusion line between parent plate and weld. (The fusion line may be identified by etching the specimen with a mild reagent.) (3) Three specimens with the notch centered in the heat affected zone, 1 mm from the fusion line. (4) Same as...

Microstructure and fatigue resistance of high strength dual phase steel welded with gas metal arc welding and plasma arc welding processes

NASA Astrophysics Data System (ADS)

Ahiale, Godwin Kwame; Oh, Yong-Jun; Choi, Won-Doo; Lee, Kwang-Bok; Jung, Jae-Gyu; Nam, Soo Woo

2013-09-01

This study presents the microstructure and high cycle fatigue performance of lap shear joints of dual phase steel (DP590) welded using gas metal arc welding (GMAW) and plasma arc welding (PAW) processes. High cycle fatigue tests were conducted on single and double lap joints under a load ratio of 0.1 and a frequency of 20 Hz. In order to establish a basis for comparison, both weldments were fabricated to have the same weld depth in the plate thickness. The PAW specimens exhibited a higher fatigue life, a gentle S-N slope, and a higher fatigue limit than the GMAW specimens. The improvement in the fatigue life of the PAW specimens was primarily attributed to the geometry effect that exhibited lower and wider beads resulting in a lower stress concentration at the weld toe where cracks initiate and propagate. Furthermore, the microstructural constituents in the heat-affected zone (HAZ) of the PAW specimens contributed to the improvement. The higher volume fraction of acicular ferrite in the HAZ beneath the weld toe enhanced the PAW specimen's resistance to fatigue crack growth. The double lap joints displayed a higher fatigue life than the single lap joints without changing the S-N slope.

Influence of M-TIG and A-TIG Welding Process on Microstructure and Mechanical Behavior of 409 Ferritic Stainless Steel

NASA Astrophysics Data System (ADS)

Vidyarthy, R. S.; Dwivedi, D. K.; Vasudevan, M.

2017-03-01

The current study investigates the effects of activating flux tungsten inert gas welding (A-TIG) and multipass tungsten inert gas welding (M-TIG) on the weld morphology, angular distortion, microstructures and mechanical properties when welding 8-mm-thick 409 ferritic stainless steel (FSS). SiO2 was used as activating flux for A-TIG welding, while SUPERTIG ER309L was used as filler for M-TIG welding. Bead-on-plate weld trials were carried out to obtain the full penetration by using different combinations of flux coating density, welding speed and welding current. An optical microscope, field emission scanning microscope (FESEM), and x-ray diffractometer were used for the metallurgical characterizations. Vickers hardness, tensile test, Charpy toughness test, and creep behavior test were carried out to evaluate the mechanical properties of the base and weld metals. Experimental results indicate that the A-TIG process can increase the joint penetration and tends to reduce the angular distortion of the 409 FSS weldment. The A-TIG welded joint also exhibited greater mechanical strength. However, a critically low Charpy toughness was measured for the A-TIG weld fusion zone, which was later sufficiently improved after post weld heat treatment (PWHT). It was concluded that PWHT is mandatory for A-TIG welded 409 FSS.

Comparing Production and Placement of Warm-Mix Asphalt to Traditional Hot-Mix Asphalt for Constructing Airfield Pavements

DTIC Science & Technology

2013-08-01

Sasobit® STA 0+35 cross-section layer thicknesses as constructed............................... 36  Figure 50. Evotherm ™ center-line layer thicknesses...as constructed. ................................................ 37  Figure 51. Evotherm ™ STA 0+15 cross-section layer thicknesses as constructed...37  Figure 52. Evotherm ™ STA 0+25 cross-section layer thicknesses as constructed. .......................... 38  Figure 53

Factors Influencing the Microstructural and Mechanical Properties of ULCB Steel Weldments

DTIC Science & Technology

1991-12-01

18 3. Molybdenum.................................... 19 4. Chromium ...................................... 19 5...WELDING METHODS UTILIZED IN ANALYSIS 1. Tungsten Inert Gas (TIG) Tungsten inert gas welding, also known as gas tungsten arc welding ( GTAW ), produces a weld...Abson, Pargeter, 1986, p.166). The role of molybdenum and chromium is not fully understood but the formation of molybdenum or chromium carbides may

Microstructure and Hydrogen-Induced Failure Mechanisms in Fe and Ni Alloy Weldments

NASA Astrophysics Data System (ADS)

Fenske, J. A.; Robertson, I. M.; Ayer, Raghavan; Hukle, Martin; Lillig, Dan; Newbury, Brian

2012-09-01

The microstructure and fracture morphology of AISI 8630-IN625 and ASTM A182-F22-IN625 dissimilar metal weld interfaces were compared and contrasted as a function of postweld heat treatment (PWHT) duration. For both systems, the microstructure along the weld interface consisted of a coarse grain heat-affected zone in the Fe-base metal followed by discontinuous martensitic partially mixed zones and a continuous partially mixed zone on the Ni side of the fusion line. Within the partially mixed zone on the Ni side, there exists a 200-nm-wide transition zone within a 20- μm-wide planar solidification region followed by a cellular dendritic region with Nb-Mo-rich carbides decorating the dendrite boundaries. Although there were differences in the volume of the partially mixed zones, the major difference in the metal weld interfaces was the presence of M7C3 precipitates in the planar solidification region, which had formed in AISI 8630-IN625 but not in ASTM A182-F22-IN625. These precipitates make the weldment more susceptible to hydrogen embrittlement and provide a low energy fracture path between the discontinuous partially mixed zones.

In vitro mesenchymal stem cell responses on laser-welded NiTi alloy.

PubMed

Chan, C W; Hussain, I; Waugh, D G; Lawrence, J; Man, H C

2013-04-01

The biocompatibility of NiTi after laser welding was studied by examining the in vitro (mesenchymal stem cell) MSC responses at different sets of time varying from early (4 to 12h) to intermediate phases (1 and 4 days) of cell culture. The effects of physical (surface roughness and topography) and chemical (surface Ti/Ni ratio) changes as a consequence of laser welding in different regions (WZ, HAZ, and BM) on the cell morphology and cell coverage were studied. The results in this research indicated that the morphology of MSCs was affected primarily by the topographical factors in the WZ: the well-defined and directional dendritic pattern and the presence of deeper grooves. The morphology of MSCs was not significantly modulated by surface roughness. Despite the possible initial Ni release in the medium during the cell culture, no toxic effect seemed to cause to MSCs as evidenced by the success of adhesion and spreading of the cells onto different regions in the laser weldment. The good biocompatibility of the NiTi laser weldment has been firstly reported in this study. Copyright © 2012 Elsevier B.V. All rights reserved.

First Annual Progress Report on Radiation Tolerance of Controlled Fusion Welds in High Temperature Oxidation Resistant FeCrAl Alloys

DOE Office of Scientific and Technical Information (OSTI.GOV)

Field, Kevin G.; Gussev, Maxim N.; Hu, Xunxiang

2015-12-01

The present report summarizes and discusses the first year efforts towards developing a modern, nuclear grade FeCrAl alloy designed to have enhanced radiation tolerance and weldability under the Department of Energy (DOE) Nuclear Energy Enabling Technologies (NEET) program. Significant efforts have been made within the first year of this project including the fabrication of seven candidate FeCrAl alloys with well controlled chemistry and microstructure, the microstructural characterization of these alloys using standardized and advanced techniques, mechanical properties testing and evaluation of base alloys, the completion of welding trials and production of weldments for subsequent testing, the design of novel tensilemore » specimen geometry to increase the number of samples that can be irradiated in a single capsule and also shorten the time of their assessment after irradiation, the development of testing procedures for controlled hydrogen ingress studies, and a detailed mechanical and microstructural assessment of weldments prior to irradiation or hydrogen charging. These efforts and research results have shown promise for the FeCrAl alloy class as a new nuclear grade alloy class.« less

Performance of repair welds on aged Cr-Mo piping girth welds

NASA Astrophysics Data System (ADS)

Viswanathan, R.; Gandy, D. W.

1999-10-01

This article documents the results of an industry survey of weld repair practices and describes the results of experimental evaluations performed on service-aged 21/4 Cr-1Mo steel piping using SMAW with both conventional postweld heat treatments and temper bead repair techniques. The overall results of this program provide substantial evidence that service-aged piping systems can be successfully weld repaired with and without postweld heat treatments and that life extension by several decades is achievable under the right design and repair conditions. Weld repairs performed on degraded exservice welds resulted in restoration or improvement of tensile and creep properties. Microhardness test results within the heat-affected zone of each weldment indicated that the temper bead weld repairs produced only slightly higher peak hardness values than those measured for the fully postweld heat treated repairs. Finally, in terms of toughness, temper bead weld repairs consistently produced higher impact properties than those measured for the postweld heat treated weldments. Gas tungsten arc weld repairs with postweld heat treatment resulted in the best combination of tensile strength, uniform microhardness distribution across the weld, Charpy toughness, and creep rupture life.

Effects of porosity on weld-joint tensile strength of aluminum alloys

NASA Technical Reports Server (NTRS)

Lovoy, C. V.

1974-01-01

Tensile properties in defect-free weldments of aluminum alloys 2014-T6 and 2219-T87 (sheet and plate) are shown to be related to the level or concentration of induced simulated porosity. The scatter diagram shows that the ultimate tensile strength of the weldments displays the most pronounced linear relationship with the level of porosity. The relationships between yield strength or elongation and porosity are either trivial or inconsequential in the lower and intermediate levels of porosity content. In highly concentrated levels of porosity, both yield strength and elongation values decrease markedly. Correlation coefficients were obtained by simple straight line regression analysis between the variables of ultimate tensile strength and pore level. The coefficients were greater, indicating a better correlation, using a pore area accumulation concept or pore volume accumulation than the accumulation of the pore diameters. These relationships provide a useful tool for assessing the existing aerospace radiographic acceptance standards with respect to permissible porosity. In addition, these relationships, in combination with known design load requirements, will serve as an engineering guideline in determining when a weld repair is necessary based on accumulative pore level as detected by radiographic techniques.

A three-dimensional thermal finite element analysis of AISI 304 stainless steel and copper dissimilar weldment

NASA Astrophysics Data System (ADS)

Singh, Gurdeep; Saxena, Ravindra K.; Pandey, Sunil

2018-04-01

The aim of this study to developed a 3-D thermal finite element model for dissimilar material welding of AISI-304 stainless steel and copper. Welding of similar material is widely studied using experimental and numerical methods but the problem becomes trivial for the welding of dissimilar materials especially in ferrous and nonferrous materials. Finite element analysis of dissimilar material welding is a cost-effective method for the understanding and analysis of the process. The finite element analysis has been performed to predict the heat affected zone and temperature distribution in AISI-304 stainless steel and copper dissimilar weldment using MSC Marc 2017®. Due to the difference in physical properties of these materials the behavior of heat affected zone and temperature distribution are perceived to be different. To verify the accuracy of the thermal finite element model, the welding process was simulated with butt-welded joints having same dimensions and parameters from Attarha and Far [1]. It is found from the study that the heat affected zone is larger in copper weld pads than in AISI 304 stainless steel due to large difference in thermal conductivity of these two weld pads.

PERFORMANCE IMPROVEMENT OF CREEP-RESISTANT FERRITIC STEEL WELDMENTS THROUGH THERMO-MECHANICAL TREATMENT AND ALLOY DESIGN

DOE Office of Scientific and Technical Information (OSTI.GOV)

Yamamoto, Yukinori; Babu, Prof. Sudarsanam Suresh; Shassere, Benjamin

Two different approaches have been proposed for improvement of cross-weld creep properties of the high temperature ferrous structural materials for fossil-fired energy applications. The traditional creep strength-enhanced ferritic (CSEF) steel weldments suffer from Type IV failures which occur at the fine-grained heat affected zone (FGHAZ). In order to minimize the premature failure at FGHAZ in the existing CSEF steels, such as modified 9Cr-1Mo ferritic-martensitic steels (Grade 91), a thermo-mechanical treatment consisting of aus-forging/rolling and subsequent aus-aging is proposed which promotes the formation of stable MX carbonitrides prior to martensitic transformation. Such MX remains undissolved during welding process, even in FGHAZ,more » which successfully improves the cross-weld creep properties. Another approach is to develop a new fully ferrtic, creep-resistant FeCrAl alloy which is essentially free from Type IV failure issues. Fe-30Cr-3Al base alloys with minor alloying additions were developed which achieved a combination of good oxidation/corrosion resistance and improved tensile and creep performance comparable or superior to Grade 92 steel.« less

Gas Metal Arc Welding Parameters Effect on Properties of Tailored Orbital Weld of SS304 and BS1387

NASA Astrophysics Data System (ADS)

Ayof, M. N.; Hussein, N. I. S.; Noh, M. Z. Mohd

2017-09-01

Dissimilar material pipes in a power plant boiler water piping system are used to transmit water at various temperatures, either in extremely high temperature water or room temperature water. In this study, tailored orbital welding of dissimilar material of Stainless Steel (SS) 304 and British Steel (BS) 1387 were performed by Gas Metal Arc Welding (GMAW) with automated fixed nozzle-rotational jig. This study focused on GMAW parameters variation effects on mechanical properties of SS304 and BS1387 dissimilar material tailored orbital welding. The weldment quality was tested by performing non-destructive dye penetrant test. The tensile strength and microhardness were studied to verify the influence of welding parameters variations. Design of Experiment (DOE) was employed to generate process parameter using Response Surface Methodology (RSM) method. Welding parameters that were arc current, arc voltage and travel speed as input response, whilst, tensile strength and microhardness as output response. Results from non-destructive test showed no major defect occurred. The tensile strength and microhardness increased when arc current and voltage increased and travel speed decreased. Microhardness at weldment was higher than base material.

Zone compensated multilayer laue lens and apparatus and method of fabricating the same

DOEpatents

Conley, Raymond P.; Liu, Chian Qian; Macrander, Albert T.; Yan, Hanfei; Maser, Jorg; Kang, Hyon Chol; Stephenson, Gregory Brian

2015-07-14

A multilayer Laue Lens includes a compensation layer formed in between a first multilayer section and a second multilayer section. Each of the first and second multilayer sections includes a plurality of alternating layers made of a pair of different materials. Also, the thickness of layers of the first multilayer section is monotonically increased so that a layer adjacent the substrate has a minimum thickness, and the thickness of layers of the second multilayer section is monotonically decreased so that a layer adjacent the compensation layer has a maximum thickness. In particular, the compensation layer of the multilayer Laue lens has an in-plane thickness gradient laterally offset by 90.degree. as compared to other layers in the first and second multilayer sections, thereby eliminating the strict requirement of the placement error.

Real time computer controlled weld skate

NASA Technical Reports Server (NTRS)

Wall, W. A., Jr.

1977-01-01

A real time, adaptive control, automatic welding system was developed. This system utilizes the general case geometrical relationships between a weldment and a weld skate to precisely maintain constant weld speed and torch angle along a contoured workplace. The system is compatible with the gas tungsten arc weld process or can be adapted to other weld processes. Heli-arc cutting and machine tool routing operations are possible applications.

Preliminary Analysis of the General Performance and Mechanical Behavior of Irradiated FeCrAl Base Alloys and Weldments

DOE Office of Scientific and Technical Information (OSTI.GOV)

Gussev, Maxim N.; Field, Kevin G.; Briggs, Samuel A.

The iron-based, iron-chromium-aluminum (FeCrAl) alloys are promising, robust materials for deployment in current and future nuclear power plants. This class of alloys demonstrates excellent performance in a range of environments and conditions, including high-temperature steam (>1000°C). Furthermore, these alloys have the potential to have prolonged survival under loss-of-coolant accident (LOCA) conditions compared to the more traditional cladding materials that are either Zr-based alloys or austenitic steels. However, one of the issues associated with FeCrAl alloys is cracking during welding. The present project investigates the possibility of mitigating welding-induced cracking via alloying and precise structure control of the weldments; in themore » frame work of the project, several advanced alloys were developed and are being investigated prior to and after neutron irradiation to provide insight into the radiation tolerance and mechanical performance of the weldments. The present report provides preliminary results on the post-irradiation characterization and mechanical tests performed during United States Fiscal Year (FY) 2016. Chapter 1 provides a general introduction, and Chapter 2 describes the alloy compositions, welding procedure, specimen geometry and manufacturing parameters. Also, a brief discussion of the irradiation at the High Flux Isotope Reactor (HFIR) is provided. Chapter 3 is devoted to the analysis of mechanical tests performed at the hot cell facility; tensile curves and mechanical properties are discussed in detail focusing on the irradiation temperature. Limited fractography results are also presented and analyzed. The discussion highlights the limitations of the testing within a hot cell. Chapter 4 underlines the advantages of in-situ testing and discusses the preliminary results obtained with newly developed miniature specimens. Specimens were moved to the Low Activation Materials Development and Analysis (LAMDA) laboratory and prepared for mechanical tests. Tensile tests were conducted at LAMDA using a modern digital image correlation approach allowing for strain distribution analysis. Plastic strain initiation and necking are discussed in detail; a concept of strain rate maps is also introduced and discussed. Follow-on SEM-EBSD and FIBTEM analysis is planned.« less

Layer Additive Production or Manufacturing of Thick Sections of Ti-6Al-4V by Selective Electron Beam Melting (SEBM)

NASA Astrophysics Data System (ADS)

Sun, Y. Y.; Gulizia, S.; Fraser, D.; Oh, C. H.; Lu, S. L.; Qian, M.

2017-10-01

Selective electron beam melting (SEBM) is an established layer additive manufacturing or production process for small-to-medium-sized components of Ti-6Al-4V. Current literature data on SEBM of Ti-6Al-4V are, however, based principally on thin-section (<1″; mostly <0.5″) samples or components. In this research, 34-mm-thick (1.34″) Ti-6Al-4V block samples were produced through use of default Arcam SEBM parameters and characterized versus section thickness. High densities (99.4-99.8%) were achieved across different thick sections, but markedly inhomogeneous microstructures also developed. Nonetheless, the tensile properties measured from 27 different thickness-width positions all clearly satisfied the minimum requirements for mill-annealed Ti-6Al-4V. SEBM produced highly dense thick sections of Ti-6Al-4V with good tensile properties. Large lack-of-fusion defects (80-250 µm) were found to be mainly responsible for variations in tensile properties.

A process model for the heat-affected zone microstructure evolution in duplex stainless steel weldments: Part I. the model

NASA Astrophysics Data System (ADS)

Hemmer, H.; Grong, Ø.

1999-11-01

The present investigation is concerned with modeling of the microstructure evolution in duplex stainless steels under thermal conditions applicable to welding. The important reactions that have been modeled are the dissolution of austenite during heating, subsequent grain growth in the delta ferrite regime, and finally, the decomposition of the delta ferrite to austenite during cooling. As a starting point, a differential formulation of the underlying diffusion problem is presented, based on the internal-state variable approach. These solutions are later manipulated and expressed in terms of the Scheil integral in the cases where the evolution equation is separable or can be made separable by a simple change of variables. The models have then been applied to describe the heat-affected zone microstructure evolution during both thick-plate and thin-plate welding of three commercial duplex stainless steel grades: 2205, 2304, and 2507. The results may conveniently be presented in the form of novel process diagrams, which display contours of constant delta ferrite grain size along with information about dissolution and reprecipitation of austenite for different combinations of weld input energy and peak temperature. These diagrams are well suited for quantitative readings and illustrate, in a condensed manner, the competition between the different variables that lead to structural changes during welding of duplex stainless steels.

Metallurgical and mechanical properties of laser welded high strength low alloy steel

PubMed Central

Oyyaravelu, Ramachandran; Kuppan, Palaniyandi; Arivazhagan, Natarajan

2016-01-01

The study aimed at investigating the microstructure and mechanical properties of Neodymium-Doped Yttrium Aluminum Garnet (Nd:YAG) laser welded high strength low alloy (HSLA) SA516 grade 70 boiler steel. The weld joint for a 4 mm thick plate was successfully produced using minimum laser power of 2 kW by employing a single pass without any weld preheat treatment. The micrographs revealed the presence of martensite phase in the weld fusion zone which could be due to faster cooling rate of the laser weldment. A good correlation was found between the microstructural features of the weld joints and their mechanical properties. The highest hardness was found to be in the fusion zone of cap region due to formation of martensite and also enrichment of carbon. The hardness results also showed a narrow soft zone at the heat affected zone (HAZ) adjacent to the weld interface, which has no effect on the weld tensile strength. The yield strength and ultimate tensile strength of the welded joints were 338 MPa and 549 MPa, respectively, which were higher than the candidate metal. These tensile results suggested that the laser welding process had improved the weld strength even without any weld preheat treatment and also the fractography of the tensile fractured samples showed the ductile mode of failure. PMID:27222751

Friction Stir Welding of Thick Section Aluminum for Military Vehicle Applications

DTIC Science & Technology

2012-12-01

Friction Stir Welding of Thick Section Aluminum for Military Vehicle Applications by Brian Thompson, Kevin Doherty, Craig Niese, Mike Eff...International Symposium on Friction Stir Welding (9ISFSW), Huntsville, AL, 15–17 May 2012. Approved for public release...Aberdeen Proving Ground, MD 21005-5069 ARL-RP-417 December 2012 Friction Stir Welding of Thick Section Aluminum for Military

Crack Initiation and Propagation Properties of HY 130 Steel Weldments Following Temper Embrittlement.

DTIC Science & Technology

1982-09-01

mechanics ( EPFM ) may be applied to engineering problems to determine material properties related to crack initiation and propagation. Specifically, these...Introduction The application of linear elastic fracture mechanics (LEFM) to engineering fracture analyses has become increasingly widespread and the use...structures to which the particular material was to be applied. The advent of elastic-plastic fracture mechanics ( EPFM ) has proven valuable because a

Current issues and problems in welding science

NASA Astrophysics Data System (ADS)

David, S. A.; Debroy, T.

1992-07-01

Recent advances in welding science are examined with consideration given to the progress made in understanding physical processes of welding and in understanding weldment microstructure and properties and the correlation between microstructure and properties of the welds. Particular attention is given to the methods used for intelligent control and automation of welding. Also discussed are issues and problems that were brought to the surface by technological advances and interdisciplinary research on welding.

Dye penetrant indications caused by superficial surface defects in 2014 aluminum alloy welds.

NASA Technical Reports Server (NTRS)

Hocker, R. G.; Wilson, K. R.

1971-01-01

Demonstration that dye penetrant indications on the heat-affected zone of 2014-T6 aluminum GMA weldments are frequently caused by superficial surface conditions and are less than 0.007 in. deep. The following methods are suggested for minimization of these surface defects: stabilization of the arc, application of dc ?GTA' welding procedures, reduction of the caustic etch time, and use of fine grain materials.

High Strength Steel Weldment Reliability: Weld Metal Hydrogen Trapping.

DTIC Science & Technology

1998-02-01

Reliability : Weld Metal Hydrogen Trapping submitted to : United States Army Research Office Materials Science Division P.O. Box 12211 Research Triangle...Conf. Proc. of Welding and Related Technologies for the XXIth Century, November 1998, Kiev, Ukraine : "Hydrogen Assisted Cracking in...appendices (see appendix IV). Next TTCP workshop will be held from 6th to 8th October 1998, at CANMET , Ottawa, Ontario, Canada. 20 III. Figures 18

Creep properties of PWC-11 base metal and weldments as affected by heat treatment

NASA Technical Reports Server (NTRS)

Titran, R. H.; Moore, T. J.; Grobstein, T. L.

1986-01-01

In a preliminary study using single specimens for each condition, PWC-11 (a niobium-base alloy with a nominal composition of Nb-1%Zr-0.1%C) was creep tested at 1350 K and 40 MPa. Base metal specimens and specimens with transverse electron beam welds were tested with and without a 1000 hr, 1350 K aging treatment prior to testing. In the annealed condition (1 hr at 1755 K + 2 hr at 1475 K), the base metal exhibited superior creep strength compared to the nonaged condition, reaching 1 percent strain in 3480 hr. A 1000 hr, 1350 K aging treatment prior to creep testing had a severe detrimental effect on creep strength of the base metal and transverse electron beam weldments, reducing the time to attain 1 percent strain by an order of magnitude. Extrapolated temperature compensated creep rates indicate that the present heat of PWC-11 may be four times as creep resistant as similarly tested Nb-1%Zr. The extrapolated stress to achieve 1 percent creep strain in 7 yr at 1350 K is 2.7 MPa for annealed Nb-1%Zr and 12 MPa for annealed and aged PWC-11 base metal with and without a transverse electron beam weld.

A study of mechanical properties for aluminum GMA weldments

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kluken, A.O.; Bjoerneklett, B.

1997-02-01

Medium- to high-strength aluminum alloys represent an attractive alternative to steel as a material for critical structural members. One area of great interest for their use is the transportation industry due to the increasing demands for less environmental impact through improved fuel efficiency, weight reductions, and increased load capacity. Fabrication of structural bodies involves, in most instances, the application of a joining process. Load-carrying members must be joined together or nonload-carrying parts attached to the primary structure. Although adhesive bonding, laser beam welding and friction stir welding are attractive processes for joining of aluminum, gas metal arc welding (GMAW) ismore » by far the most widely used process at present. Fusion welding of a heat-treatable aluminum alloy represents an additional local heat treatment of material that previously has been processed through tight temperature control to obtain the desired mechanical properties. Hence, great attention must be given to selection of alloy and temper condition, welding parameters, and postweld aging procedures for a given application. The objective of this investigation was to establish mechanical property data, i.e., tensile strength and impact toughness, for Al-Mg-Si and Al-Zn-Mg gas metal arc weldments applicable to the automotive and shipbuilding industries.« less

Microstructural characterization of weld joints of 9Cr reduced activation ferritic martensitic steel fabricated by different joining methods

DOE Office of Scientific and Technical Information (OSTI.GOV)

Thomas Paul, V.; Saroja, S.; Albert, S.K.

This paper presents a detailed electron microscopy study on the microstructure of various regions of weldment fabricated by three welding methods namely tungsten inert gas welding, electron beam welding and laser beam welding in an indigenously developed 9Cr reduced activation ferritic/martensitic steel. Electron back scatter diffraction studies showed a random micro-texture in all the three welds. Microstructural changes during thermal exposures were studied and corroborated with hardness and optimized conditions for the post weld heat treatment have been identified for this steel. Hollomon–Jaffe parameter has been used to estimate the extent of tempering. The activation energy for the tempering processmore » has been evaluated and found to be corresponding to interstitial diffusion of carbon in ferrite matrix. The type and microchemistry of secondary phases in different regions of the weldment have been identified by analytical transmission electron microscopy. - Highlights: • Comparison of microstructural parameters in TIG, electron beam and laser welds of RAFM steel • EBSD studies to illustrate the absence of preferred orientation and identification of prior austenite grain size using phase identification map • Optimization of PWHT conditions for indigenous RAFM steel • Study of kinetics of tempering and estimation of apparent activation energy of the process.« less

Recent Developments and Research Progress on Friction Stir Welding of Titanium Alloys: An Overview

NASA Astrophysics Data System (ADS)

Karna, Sivaji; Cheepu, Muralimohan; Venkateswarulu, D.; Srikanth, V.

2018-03-01

Titanium and its alloys are joined by various welding processes. However, Fusion welding of titanium alloys resulted solidification problems like porosity, segregation and columnar grains. The problems occurred in conventional welding processes can be resolved using a solid state welding i.e. friction stir welding. Aluminium and Magnesium alloys were welded by friction stir welding. However alloys used for high temperature applications such as titanium alloys and steels are arduous to weld using friction stir welding process because of tool limitations. Present paper summarises the studies on joining of Titanium alloys using friction stir welding with different tool materials. Selection of tool material and effect of welding conditions on mechanical and microstructure properties of weldments were also reported. Major advantage with friction stir welding is, we can control the welding temperature above or below β-transus temperature by optimizing the process parameters. Stir zone in below beta transus condition consists of bi-modal microstructure and microstructure in above β-transus condition has large prior β- grains and α/β laths present in the grain. Welding experiments conducted below β- transus condition has better mechanical properties than welding at above β-transus condition. Hardness and tensile properties of weldments are correlated with the stir zone microstructure.

Gas turbine bucket wall thickness control

DOEpatents

Stathopoulos, Dimitrios; Xu, Liming; Lewis, Doyle C.

2002-01-01

A core for use in casting a turbine bucket including serpentine cooling passages is divided into two pieces including a leading edge core section and a trailing edge core section. Wall thicknesses at the leading edge and the trailing edge of the turbine bucket can be controlled independent of each other by separately positioning the leading edge core section and the trailing edge core section in the casting die. The controlled leading and trailing edge thicknesses can thus be optimized for efficient cooling, resulting in more efficient turbine operation.

Thick crystalline films on foreign substrates

DOEpatents

Smith, Henry I.; Atwater, Harry A.; Geis, Michael W.

1986-01-01

To achieve a uniform texture, large crystalline grains or, in some cases, a single crystalline orientation in a thick (>1 .mu.m) film on a foreign substrate, the film is formed so as to be thin (<1 .mu.m) in a certain section. Zone-melting recrystallization is initiated in the thin section and then extended into the thick section. The method may employ planar constriction patterns of orientation filter patterns.

Thick crystalline films on foreign substrates

DOEpatents

Smith, H.I.; Atwater, H.A.; Geis, M.W.

1986-03-18

To achieve a uniform texture, large crystalline grains or, in some cases, a single crystalline orientation in a thick (>1 [mu]m) film on a foreign substrate, the film is formed so as to be thin (<1 [mu]m) in a certain section. Zone-melting recrystallization is initiated in the thin section and then extended into the thick section. The method may employ planar constriction patterns of orientation filter patterns. 2 figs.

Origins of Line Defects in Self-Reacting Friction Stir Welds and Their Impact on Weld Quality

NASA Technical Reports Server (NTRS)

Schneider, Judy; Nunes, Arthur C., Jr.

2016-01-01

Friction stir welding (FSWing) is a solid state joining technique which reduces the occurrence of typical defects formed in fusion welds, especially of highly alloyed metals. Although the process is robust for aluminum alloys, occasional reductions in the strength of FSWs have been observed. Shortly after the NASA-MSFC implemented a variation of FSW called self-reacting (SR), low strength properties were observed. At that time, this reduction in strength was attributed to a line defect. At that time, the limited data suggested that the line defect was related to the accumulation of native oxides that form on the weld lands and faying surfaces. Through a series of improved cleaning methods, tool redesign, and process parameter modifications, the reduction in the strength of the SR-FSWs was eliminated. As more data has been collected, the occasional reduction in the strength of SR-FSW still occurs. These occasional reductions indicate a need to reexamine the underlying causes. This study builds off a series of self reacting (SR)-FSWs that were made in 3 different thickness panels of AA2219 (0.95, 1.27 and 1.56 cm) at 2 different weld pitches. A bead on plate SR-FSW was also made in the 1.56 cm thick panel to understand the contribution of the former faying surfaces. Copper tracer studies were used to understand the flow lines associated with the weld tool used. The quality of the SR-FSWs was evaluated from tensile testing at room temperature. Reductions in the tensile strength were observed in some weldments, primarily at higher weld pitch or tool rotations. This study explores possible correlations between line defects and the reduction of strength in SR-FSWs. Results from this study will assist in a better understand of the mechanisms responsible for reduced tensile strength and provide methodology for minimizing their occurrence.

Global and Local Mechanical Properties of Autogenously Laser Welded Ti-6Al-4V

NASA Astrophysics Data System (ADS)

Cao, Xinjin; Kabir, Abu Syed H.; Wanjara, Priti; Gholipour, Javad; Birur, Anand; Cuddy, Jonathan; Medraj, Mamoun

2014-03-01

Ti-6Al-4V sheets, 3.2-mm in thickness, were butt welded using a continuous wave 4 kW Nd:YAG laser welding system. The effect of two main process parameters, laser power and welding speed, on the joint integrity was characterized in terms of the joint geometry, defects, microstructure, hardness, and tensile properties. In particular, a digital image correlation technique was used to determine the local tensile properties of the welds. It was determined that a wide range of heat inputs can be used to fully penetrate the Ti-6Al-4V butt joints during laser welding. At high laser power levels, however, significant defects such as underfill and porosity, can occur and cause marked degradation in the joint integrity and performance. At low welding speeds, however, significant porosity occurs due to its growth and the potential collapse of instable keyholes. Intermediate to relatively high levels of heat input allow maximization of the joint integrity and performance by limiting the underfill and porosity defects. In considering the effect of the two main defects on the joint integrity, the underfill defect was found to be more damaging to the mechanical performance of the weldment than the porosity. Specifically, it was determined that the maximum tolerable underfill depth for Ti-6Al-4V is approximately 6 pct of the workpiece thickness, which is slightly stricter than the value of 7 pct specified in AWS D17.1 for fusion welding in aerospace applications. Hence, employing optimized laser process parameters allows the underfill depth to be maintained within the tolerable limit (6 pct), which in turn prevents degradation in both the weld strength and ductility. To this end, the ability to maintain weld ductility in Ti-6Al-4V by means of applying a high energy density laser welding process presents a significant advantage over conventional arc welding for the assembly of aerospace components.

Performance of Underwater Weldments

DTIC Science & Technology

1990-09-05

gas or cathodic overprotection remains to be investigation. Subcritical crack propagation from corrosion fatigue must be considered. Crack propagation...toughness = .83 c. There is no redundancy so 1.8 times maximum stress or 1.0 times yield stress. Since the yield stress of the parent plate is being used...on the stress is required even though the stress will now be below yield strength in the parent plate. Since K is directly proportional to the stress

Study of Residual Stresses and Distortion in Structural Weldments in High-Strength Steels.

DTIC Science & Technology

1982-11-30

02139 II. CONTROLLING OFFICE NAME AND ADDRESS 12. REPORT DATE Department of the Navy November 30, 1982 Office of Naval Research 13. NUMBER OF PAGES...Arlington, Virginia 22217 14. MONITORING AGENCY NAME & ADDRESS(if different from Controlling Office) 15. SECURITY CLASS. (of this report) Unclassified 15a...a residual stress field were calculated. Finally, results from all of the afLrementioned analyses were compared with data obtained from experimental

Lamb wave scattering by a surface-breaking crack in a plate

NASA Technical Reports Server (NTRS)

Datta, S. K.; Al-Nassar, Y.; Shah, A. H.

1991-01-01

An NDE method based on finite-element representation and modal expansion has been developed for solving the scattering of Lamb waves in an elastic plate waveguide. This method is very powerful for handling discontinuities of arbitrary shape, weldments of different orientations, canted cracks, etc. The advantage of the method is that it can be used to study the scattering of Lamb waves in anisotropic elastic plates and in multilayered plates as well.

Corrosion-Fatigue of a Composite Laser Weldment

DTIC Science & Technology

1989-07-01

interaction of the bolt metal with the salt water solution. 43 Two specimen grips and two pins were machined from type 431 stainless steel and then heat...presented as follows. Body- centered cubic or tetragonal steels , namely ferrite and martensite , allow rapid movement of 5 hydrogen and solubility of...hydrogen is low. High strength martensitic steels are very susceptible to becoming embrittled by the diffusion of hydrogen down a stress gradient to a

Effects of Preheat on Weldments of NICOP Steel.

DTIC Science & Technology

1983-09-01

copper in this low alloy steel . Taken into solid solution in the austenite phase , the copper can precipitate as fine... low alloy steel was intro- duced which contains 1.0-1.3% copper with a maximum of 0.07% carbon. This steel is designated as AST4 A710 grade A for... ferrite has formed, some copper may precipitate as a fine epsilon copper phase in the ferrite as the solubility of

AN EXPERIMENTAL EVALUATION OF THREE METHODS FOR INCREASING THE LEADING EDGE THICKNESS OF SUPERCAVITATING PROPELLERS.

DTIC Science & Technology

An experimental investigation of three methods of increasing the leading-edge thickness of supercavitating propeller sections was conducted. The...addition of a parabolic thickness to both the face and back of the section. Five supercavitating propeller models incorporating these three methods of

Microstructure Characterization and Stress Corrosion Evaluation of Autogenous and Hybrid Friction Stir Welded Al-Cu-Li 2195 Alloy

NASA Technical Reports Server (NTRS)

Li, Zhixian; Arbegast, William J.; Meletis, Efstathios I.

1997-01-01

Friction stir welding process is being evaluated for application on the Al-Cu-Li 2195 Super-Light Weight External Tank of the Space Transportation System. In the present investigation Al-Cu-Li 2195 plates were joined by autogenous friction stir welding (FSW) and hybrid FSW (friction stir welding over existing variable polarity plasma arc weld). Optical microscopy and transmission electron microscopy (TEM) were utilized to characterize microstructures of the weldments processed by both welding methods. TEM observations of autogenous FSW coupons in the center section of the dynamically-recrystallized zone showed an equiaxed recrystallized microstructure with an average grain size of approx. 3.8 microns. No T(sub 1), precipitates were present in the above-mentioned zone. Instead, T(sub B) and alpha precipitates were found in this zone with a lower population. Alternate immersion, anodic polarization, constant load, and slow strain tests were carried out to evaluate the general corrosion and stress-corrosion properties of autogenous and hybrid FSW prepared coupons. The experimental results will be discussed.

Artifacts in slab average-intensity-projection images reformatted from JPEG 2000 compressed thin-section abdominal CT data sets.

PubMed

Kim, Bohyoung; Lee, Kyoung Ho; Kim, Kil Joong; Mantiuk, Rafal; Kim, Hye-ri; Kim, Young Hoon

2008-06-01

The objective of our study was to assess the effects of compressing source thin-section abdominal CT images on final transverse average-intensity-projection (AIP) images. At reversible, 4:1, 6:1, 8:1, 10:1, and 15:1 Joint Photographic Experts Group (JPEG) 2000 compressions, we compared the artifacts in 20 matching compressed thin sections (0.67 mm), compressed thick sections (5 mm), and AIP images (5 mm) reformatted from the compressed thin sections. The artifacts were quantitatively measured with peak signal-to-noise ratio (PSNR) and a perceptual quality metric (High Dynamic Range Visual Difference Predictor [HDR-VDP]). By comparing the compressed and original images, three radiologists independently graded the artifacts as 0 (none, indistinguishable), 1 (barely perceptible), 2 (subtle), or 3 (significant). Friedman tests and exact tests for paired proportions were used. At irreversible compressions, the artifacts tended to increase in the order of AIP, thick-section, and thin-section images in terms of PSNR (p < 0.0001), HDR-VDP (p < 0.0001), and the readers' grading (p < 0.01 at 6:1 or higher compressions). At 6:1 and 8:1, distinguishable pairs (grades 1-3) tended to increase in the order of AIP, thick-section, and thin-section images. Visually lossless threshold for the compression varied between images but decreased in the order of AIP, thick-section, and thin-section images (p < 0.0001). Compression artifacts in thin sections are significantly attenuated in AIP images. On the premise that thin sections are typically reviewed using an AIP technique, it is justifiable to compress them to a compression level currently accepted for thick sections.

Comparative evaluation of physicians' pulmonary nodule detection with reduced slice thickness at CT screening

NASA Astrophysics Data System (ADS)

Sinsuat, Marodina; Shimamura, Ichiro; Saita, Shinsuke; Kubo, Mitsuru; Kawata, Yoshiki; Niki, Noboru; Ohmatsu, Hironobu; Kakinuma, Ryutaro; Eguchi, Kenji; Kaneko, Masahiro; Tominaga, Keigo; Moriyama, Noriyuki

2008-03-01

With thin and thick section Multi-slice CT images at lung cancer screening, we have statistically and quantitatively shown and evaluated the diagnostic capabilities of these slice thicknesses on physicians' pulmonary nodule diagnosis. To comparatively evaluate the 2 mm and 10 mm slice thicknesses, MSCT images of 360 people were read by six physicians. The reading criteria consisted of nodule for further examination (NFE), nodule for no further examination (NNFE) and no abnormality (NA) case. For reading results evaluation; firstly, cross-tabulation was carried out to roughly analyze the diagnoses based on whole lung field and each lung lobes. Secondly, from semi-automated extraction result of the nodule, detailed quantitative analysis was carried out to determine the diagnostic capabilities of two slice thicknesses. Finally, using the reading results of 2 mm thick image as the gold standard, the diagnostic capabilities were analyzed through the features and locations of pulmonary nodules. The study revealed that both slice thicknesses can depict lung cancer. Thin section may not be effective to diagnose nodules of <=3 mm in size and nodules of <= 5mm in size for thick section. Though thick section is less tiring for reading physicians, it is not good at depicting nodules located at the border of lung upper lobe and which have a pixel size distance of <=5 from the chest wall. The information presented may serve as a useful reference to determine in which particular pulmonary nodule condition the two slice thicknesses can be effectively used for early detection of lung cancer.

Modeling the curing process of thick-section autoclave cured composites

NASA Technical Reports Server (NTRS)

Loos, A. C.; Dara, P. H.

1985-01-01

Temperature gradients are significant during cure of large area, thick-section composites. Such temperature gradients result in nonuniformly cured parts with high void contents, poor ply compaction, and variations in the fiber/resin distribution. A model was developed to determine the temperature distribution in thick-section autoclave cured composites. Using the model, long with temperature measurements obtained from the thick-section composites, the effects of various processing parameters on the thermal response of the composites were examined. A one-dimensional heat transfer model was constructed for the composite-tool assembly. The governing differential equations and associated boundary conditions describing one-dimensional unsteady heat-conduction in the composite, tool plate, and pressure plate are given. Solution of the thermal model was obtained using an implicit finite difference technique.

Tensile strength of simulated and welded butt joints in W-Cu composite sheet

NASA Technical Reports Server (NTRS)

Moore, Thomas J.; Watson, Gordon K.

1994-01-01

The weldability of W-Cu composite sheet was investigated using simulated and welded joints. The welded joints were produced in a vacuum hot press. Tensile test results showed that simulated joints can provide strength and failure mode data which can be used in joint design for actual weldments. Although all of the welded joints had flaws, a number of these joints were as strong as the W-Cu composite base material.

Investigation of Weld Pool Structure and Property Control in Pulsed Arc Welding.

DTIC Science & Technology

1981-03-04

noted, elsewhere, freezing rate in the trailing and transverse directions show similarly contrasting behavior (6 𔄁 ). The movement of the solidus and...rise to low freezing eutectics and, hence, should be kept to the lowest possible level.1 3 󈧒 Solidification Cracking in Stainless Steel Welds It has...been observed 1 5 that hot cracking in austenitic stainless steel weldments is reduced or prevented when a small amount of delta ferrite is present

Prevention of Hydrogen-Induced Cracking in HY-130 Weldments.

DTIC Science & Technology

1977-09-30

cubic delta ferrite at the melting point (1538 C). The solu- bility increases from about k.9 to 8.3 ppm when delta ferrite transforms to * 3 The H... ferrite at 912 C. The solubility in ferrite then de- creases to less than 0.5 ppm at ambient temperature. This theory postulates that atomic...content than the dark- etching bands, and thus correspond to the regions last to freeze between the dendritic arms in the original ingot. During

Ship Structure Committee Publications: A Special Bibliography.

DTIC Science & Technology

1983-01-01

structural surfaces, even more so when the surfaces were machined after straining. damage; heavy weather damage to the forefoot and forward weather deck...One of the striking ORDER FROM: NTIS inadequacies of the impact test was the failure to show a difference between AD-72963 steels A and C, a...weldment in the range of 40 deg to 0 deg F. The effects of various types of defects, including arc strikes , Contract NObs-50238 porosity, and partial

Microstructural Characterization of HSLA-100 GMA-Weldments

DTIC Science & Technology

1987-09-01

Intermeiate Oxygen Regime ----------- 66 D.) Schematic CCT Diagram - --------------- 66 9 ACKNOWLEDGEMENTS I wish to express my appreciation to my thesis...have been observed in this research [review Figures 31 (a), (b) and 35 (a)]. Figure 38 (d) shows a schematic CCT diagram reported by Glover (Ref. 5) and...Regime B.) High Ox. gen Regime C. )Interme late Oxygen Regime D.1 Schematic CCT Diagram 66 LIST OF REFERENCES 1. Anderson, T.L., Hyatt J A West, J.C

Study of Residual Stresses and Distortion in Structural Weldments in High-Strength Steels.

DTIC Science & Technology

1981-11-30

diagram of the material under consideration which is either known experimentally or can be derived from the TTT diagram. Using the CCT diagram and the...strains are incorporated into the finite element program ADINA replacing the conventional thermal strains, T TH e i" I Computed CCT Diagram . Experimentally...derived CCT diagrams exist today for several steel alloys, enabling one to predict the microstructure [history during the cooling stage of the

Mechanical Properties and Seawater Behavior of Nitronic 50 (22Cr-13Ni- 5Mn) Plate

DTIC Science & Technology

1976-01-01

Bal - balance misc - miscellaneous cfh - cubic feet per hour mpy - mils per year c/m - cycles per minute my - millivolts CVN - Charpy V-notch No...High-Cycle Fatigue Specimens F_gure 6 - Drawings; Low-Cycle Fatigue Specimens Figure 7 - Curve; Charpy V-Notch Impact Toughness Versus Temperature...for Nitronic 50 Base Plate FiGure 8 - Curve; Charpy V-Notch Toughness Versus Tempera- ture for Nitrcnic 50 Weldments Figure 9 - Photographs; Fracture

The Effect of Welding Process on the Microstructure of HY-130 Steel Weldments

DTIC Science & Technology

1988-12-01

low -carbon, high-strength, low - alloy (HSLA) steels (C below 0.07 per- cent), the weld metal changed from coarse polygonal ferrite to...17. Ricks. R. A., Barritte, G. S., and Howell, P. R., "The Influence of Second Phase Particles on Diffusional Phase Transformations in Steels ... phase , austenite, may transform to mar- tensite on rapid cooling. The martensite has the exact same composi- tion as the austenite (up to two

Fatigue Characterization of Fabricated Ship Details for Design.

DTIC Science & Technology

1982-08-01

than the ques- tion of brittle fracture. Such cracking has been found in the forepeak region, bottom amidships, at the bulwark at both ends of the...results of the laboratory studies are presented in the Appendices. 1.3 References 1.1 Vedeler, G. "To What Extent Do Brittle Fracture and Fatigue...Civil Engineering. Appre- ciation is extended to Mr. John R. Williams who prepared the weldments, to Mr. Glen Lafenhagen who assisted in the fatigue

Dissimilar welding of nickel-based Alloy 690 to SUS 304L with Ti addition

NASA Astrophysics Data System (ADS)

Lee, H. T.; Jeng, S. L.; Yen, C. H.; Kuo, T. Y.

2004-10-01

This study investigates the effects of Ti addition on the weldability, microstructure and mechanical properties of a dissimilar weldment of Alloy 690 and SUS 304L. Shielding metal arc welding (SMAW) is employed to butt-weld two plates with three welding layers, where each layer is deposited in a single pass. To investigate the effects of Ti addition, the flux coatings of the electrodes used in the welding process are modified by varying additions of either a Ti-Fe compound or a Ti powder. The results indicate that the microstructure of the fusion zone (FZ) is primarily dendritic. With increasing Ti content, it is noted that the microstructure changes from a columnar dendritic to an equiaxed dendritic, in which the primary dendrite arm spacing (PDAS) becomes shorter. Furthermore, it is observed that the amount of Al-Ti oxide phase increases in the inter-dendritic region, while the amount of Nb-rich phase decreases. Moreover, the average hardness of the FZ increases slightly. The results indicate that Ti addition prompts a significant increase in the elongation of the weldment (i.e. 36.5%, Ti: 0.41 wt%), although the tensile strength remains relatively unchanged. However, at an increased Ti content of 0.91 wt%, an obvious reduction in the tensile strength is noted, which can be attributed to a general reduction in the weldability of the joint.

Correlation Between Intercritical Heat-Affected Zone and Type IV Creep Damage Zone in Grade 91 Steel

NASA Astrophysics Data System (ADS)

Wang, Yiyu; Kannan, Rangasayee; Li, Leijun

2018-04-01

A soft zone in Cr-Mo steel weldments has been reported to accompany the infamous Type IV cracking, the highly localized creep damage in the heat-affected zone of creep-resistant steels. However, the microstructural features and formation mechanism of this soft zone are not well understood. In this study, using microhardness profiling and microstructural verification, the initial soft zone in the as-welded condition was identified to be located in the intercritical heat-affected zone of P91 steel weldments. It has a mixed structure, consisting of Cr-rich re-austenitized prior austenite grains and fine Cr-depleted, tempered martensite grains retained from the base metal. The presence of these further-tempered retained grains, originating from the base metal, is directly responsible for the hardness reduction of the identified soft zone in the as-welded condition. The identified soft zone exhibits a high location consistency at three thermal stages. Local chemistry analysis and thermodynamic calculation show that the lower chromium concentrations inside these retained grains thermodynamically decrease their potentials for austenitic transformation during welding. Heterogeneous grain growth is observed in the soft zone during postweld heat treatment. The mismatch of strengths between the weak Cr-depleted grains and strong Cr-rich grains enhances the creep damage. Local deformation of the weaker Cr-depleted grains accelerates the formation of creep cavities.

Improved method for sectioning pectoral spines of catfish for age determination

USGS Publications Warehouse

Blouin, Marc A.; Hall, Glenda R.

1990-01-01

The advantages of this method are: (1) spine sections are clear, with uniform thickness and little tissue damage; (2) no time-consuming procedures are necessary; (3) the original spine remains intact for future sectioning; and (4) the thick, single blade does not warp.

Assessment of experimental d-PIGE γ-ray production cross sections for 12C, 14N and 16O and comparison with absolute thick target yields

NASA Astrophysics Data System (ADS)

Csedreki, L.; Halász, Z.; Kiss, Á. Z.

2016-08-01

Measured differential cross sections for deuteron induced γ-ray emission from the reactions 12C(d,pγ)13C, (Eγ = 3089 keV), 14N(d,pγ)15N (Eγ = 8310 keV) and 16O(d,pγ)17O (Eγ = 871 keV) available in the literature were assessed. In order to cross check the assessed γ-ray production cross section data, thick target γ-yields calculated from the differential cross sections were compared with available measured thick target yields. Recommended differential cross section data for each reaction were deduced for particle induced γ-ray emission (PIGE) applications.

Effect of PWHT on Microstructure, Mechanical and Corrosion Behaviour of Gas Tungsten Arc Welds of IN718 Superalloys

NASA Astrophysics Data System (ADS)

Dilkush; Mohammed, Raffi; Madhusudhan Reddy, G.; Srinivasa Rao, K.

2018-03-01

The present work aims to improve corrosion resistance and mechanical behavior of the welds with suitable post weld heat treatment i.e. direct aging and solutionizing treatments (980STA, 1080STA). Gas tungsten arc welding (GTAW) has been performed on Inconel 718 (IN718) nickel based super alloy plates with 3mm thickness. The structural –property relationship of the post weld heat treated samples is judged by correlating the microstructural changes with observed mechanical behavior and pitting corrosion resistance of the welds As-recevied, direct aging (DA), 980STA,1080STA were studied. Welds were characterized for microstructure changes with scanning electron microscopy (SEM) and optical microscopy (OM).Vickers micro- hardness tester was used to measure the hardness of the weldments. Potential-dynamic polarization testing was carried out to study the pitting corrosion resistance in 3.5%NaCl (Sodium chloride) solution at 30°C.Results of the present study established that post weld heat treatments resulted in promoting the element segregation diffusion and resolve them from brittle laves particles in the matrix. Increased precipitation of strengthening phases lead to a significant increase in fusion zone hardness of 1080STA post weld heat treated condition compared to as welded, direct aged, 980STA conditions. Due to significant changes in the microstructural behavior of 1080STA condition resulted in superior pitting corrosion resistance than 980STA, direct aged and as- recevied conditions of IN718 GTA welds

Thin walled channel

DOE Office of Scientific and Technical Information (OSTI.GOV)

Crowther, R.L.; Johansson, E.B.

1988-06-07

A fuel assembly is described comprising fuel rods positioned in a spaced array by upper and lower tie-plates, an open ended flow channel surrounding the array for conducting coolant upward about the fuel rods, the open ended channel having a polygon shaped cross section with flat side sections connected between the corner sections; means separate from the channel connecting the upper and lower tie-plates together and maintaining the fuel rods in spaced array independent of the flow channel, improvement in the flow channel comprising: four corners having a first thickness; four sides having a second and reduced thickness from themore » corner thickness, the sides welded to the corner sections.« less

Beam Splitter For Welding-Torch Vision System

NASA Technical Reports Server (NTRS)

Gilbert, Jeffrey L.

1991-01-01

Compact welding torch equipped with along-the-torch vision system includes cubic beam splitter to direct preview light on weldment and to reflect light coming from welding scene for imaging. Beam splitter integral with torch; requires no external mounting brackets. Rugged and withstands vibrations and wide range of temperatures. Commercially available, reasonably priced, comes in variety of sizes and optical qualities with antireflection and interference-filter coatings on desired faces. Can provide 50 percent transmission and 50 percent reflection of incident light to exhibit minimal ghosting of image.

Detection of lack of fusion using opaque additives, phase 2

NASA Technical Reports Server (NTRS)

Cook, J. L.

1973-01-01

Plasma-sprayed copper coatings were developed to protect the aluminum surfaces of spacecraft structures from oxidation, as well as to provide a means of reliable nondestructive X-ray inspection of possible incomplete weldment penetration. Sixty day storage tests of coated aluminum samples indicated the promise of long-term oxidation protection, but revealed no advantage in detecting penetration defects. Delta-scan techniques were used, and peen plating as a means of applying copper to the aluminum surface was investigated.

Mechanical, Corrosion, and Fatigue Properties of 15-5 PH, Inconel 718, and Rene 41 Weldments

DTIC Science & Technology

1975-05-01

TUCUMvARI (PGH 2) It was originally developed for high - temperature use by Armco Steel Corporation. 2 High strength is obtained by the precipitation...Rene 41 was developed by General Electric Company as a high - temperature turbine alloy. It is a nickel-base alloy, high in chromium, cobalt, and... molybdenum . Its high strength comes from the precipitation of a gamma-prime phase consisting of Ni3AI and Ni5Ti, and from the solid solution effects of

Oxygen-Free Welding Contact Tips

NASA Technical Reports Server (NTRS)

Pike, James F.

1993-01-01

Contact tips for gas/metal arc welding (GMAW) fabricated from oxygen-free copper. Prototype tips tested in robotic welding, for which application intended. Reduces electrical erosion, increases electrical conductivity, and reduces mechanical wear. Productivity of robotic welding increases while time during welding interrupted for removal and replacement of contact tips minimal. Improves alignment of joints and filler metal, reducing rate of rejection and repair of unacceptable weldments. Utility extends beyond aerospace industry to mass production of various types of hardware, including heavy off-highway construction equipment.

Flaw Growth of 6Al-4V Titanium in a Freon TF Environment

NASA Technical Reports Server (NTRS)

Tiffany, C. F.; Masters, J. N.; Bixler, W. D.

1969-01-01

The plane strain threshold stress intensity and sustained stress flaw growth rates were experimentally determined for 6AI-4V S.T.A. titanium forging and weldments in environments of Freon TF at room temperature. Sustained load tests of surface flawed specimens were conducted with the experimental approach based on linear elastic fracture mechanics. It was concluded that sustained stress flaw growth rates, in conjunction with threshold stress intensities, can be used in assessing the service life of pressure vessels.

Determination of design allowable properties. Fracture of 2219-T87 aluminum alloy

NASA Technical Reports Server (NTRS)

Engstrom, W. L.

1972-01-01

A literature survey was conducted to provide a comprehensive report of available valid data on tensile properties, fracture toughness, fatigue crack propagation, and sustained load behavior of 2219-T87 aluminum alloy base metal and weldments, as applicable to manned spacecraft tankage. Most of the data found were from tests conducted at room temperature, -320 F and -423 F. Data are presented in graphical and tabular form, and areas in which data are lacking are established.

Factors Influencing the Microstructure and Mechanical Properties of Ultra Low Carbon Bainitic 100 Tungsten Inert Gas Multipass Weldments

DTIC Science & Technology

1992-09-01

Optical macrograph of flat-etched sample 75B3-8 ........................ 30 Figure 4.15 Constitutional supercooling in alloy solidification ... alloying elements such as Mn, Mo, Ni and Cr are added to increase the strength and hardenability of the steel. However, substantial limitations on...0.9 Carbon Equivalent CE = C + Mn + Si + Ni + Cu + Cr + Mo + V 6 15 5 Figure 2.1 Graville Diagram (Blicharski et al, 1989, p.318) 3 B. ULTRA LOW

Identification and Characterization of Intercritical Heat-Affected Zone in As-Welded Grade 91 Weldment

NASA Astrophysics Data System (ADS)

Wang, Yiyu; Kannan, Rangasayee; Li, Leijun

2016-12-01

A metallurgical method is proposed for locating the intercritical heat-affected zone in the as-welded Grade 91 steel. New austenitic grains, preferentially formed along the original prior austenite grain boundaries, are characterized to contain finer M23C6 carbides and higher strain levels than the original prior austenite grains. Kurdjumov-Sachs Group 1 variant pairs, with a low misorientation of 7 deg within a martensitic block, are identified as the dominant variants in the new PAGs.

Proceedings of the Joint Seminar; Hydrogen Management in Steel Weldments, Melbourne, Australia, 23rd October 1996.

DTIC Science & Technology

1997-01-01

Cr-Mo quenched and tempered (Q&T) steel . Both A723 Grade 1 and Grade 2 compositions were evaluated to determine the effects of strength, composition ...15] Craig, B., "Limitations of Alloying to Improve the Threshold for Hydrogen Stress Cracking of Steels ", Hydrogen Effects on Material Behavior ...considered are as follows: 1. Hydrogen mass transfer in steels and welded joints: analytical equipment; effect of element composition of weld metal and

STEM Tomography Imaging of Hypertrophied Golgi Stacks in Mucilage-Secreting Cells.

PubMed

Kang, Byung-Ho

2016-01-01

Because of the weak penetrating power of electrons, the signal-to-noise ratio of a transmission electron micrograph (TEM) worsens as section thickness increases. This problem is alleviated by the use of the scanning transmission electron microscopy (STEM). Tomography analyses using STEM of thick sections from yeast and mammalian cells are of higher quality than are bright-field (BF) images. In this study, we compared regular BF tomograms and STEM tomograms from 500-nm thick sections from hypertrophied Golgi stacks of alfalfa root cap cells. Due to their thickness and intense heavy metal staining, BF tomograms of the thick sections suffer from poor contrast and high noise levels. We were able to mitigate these drawbacks by using STEM tomography. When we performed STEM tomography of densely stained chloroplasts of Arabidopsis cotyledon, we observed similar improvements relative to BF tomograms. A longer time is required to collect a STEM tilt series than similar BF TEM images, and dynamic autofocusing required for STEM imaging often fails at high tilt angles. Despite these limitations, STEM tomography is a powerful method for analyzing structures of large or dense organelles of plant cells.

A Review on Inertia and Linear Friction Welding of Ni-Based Superalloys

NASA Astrophysics Data System (ADS)

Chamanfar, Ahmad; Jahazi, Mohammad; Cormier, Jonathan

2015-04-01

Inertia and linear friction welding are being increasingly used for near-net-shape manufacturing of high-value materials in aerospace and power generation gas turbines because of providing a better quality joint and offering many advantages over conventional fusion welding and mechanical joining techniques. In this paper, the published works up-to-date on inertia and linear friction welding of Ni-based superalloys are reviewed with the objective to make clarifications on discrepancies and uncertainties reported in literature regarding issues related to these two friction welding processes as well as microstructure, texture, and mechanical properties of the Ni-based superalloy weldments. Initially, the chemical composition and microstructure of Ni-based superalloys that contribute to the quality of the joint are reviewed briefly. Then, problems related to fusion welding of these alloys are addressed with due consideration of inertia and linear friction welding as alternative techniques. The fundamentals of inertia and linear friction welding processes are analyzed next with emphasis on the bonding mechanisms and evolution of temperature and strain rate across the weld interface. Microstructural features, texture development, residual stresses, and mechanical properties of similar and dissimilar polycrystalline and single crystal Ni-based superalloy weldments are discussed next. Then, application of inertia and linear friction welding for joining Ni-based superalloys and related advantages over fusion welding, mechanical joining, and machining are explained briefly. Finally, present scientific and technological challenges facing inertia and linear friction welding of Ni-based superalloys including those related to modeling of these processes are addressed.

Microstructural characterization of an SA508–309L/308L–316L domestic dissimilar metal welded safe-end joint

DOE Office of Scientific and Technical Information (OSTI.GOV)

Ming, Hongliang; Zhang, Zhiming; Wang, Jianqiu, E-mail: wangjianqiu@imr.ac.cn

2014-11-15

The microstructure of an SA508–309L/308L–316L domestic dissimilar metal welded safe-end joint was characterized in this work by optical microscopy, scanning electron microscopy (with electron back scattering diffraction) and micro-hardness testing. Epitaxial growth and competitive growth are evident in the 308L–316L fusion boundary regions. A martensite layer, carbon-depleted zones, and type-II and type-I boundaries are found in the SA508–309L fusion boundary regions, while only martensite and austenite mixed zones are observed in the SA508–308L fusion boundary regions. The microstructure near the fusion boundary and the microstructure transition in the SA508 heat affected zone are quite complex. Both for SA508–309L/308L and 308L–316L,more » the highest residual strain is located on the outside of the weldment. The residual strain and the grain boundary character distribution change with increasing distance from the fusion boundary in the heat affected zone of 316L. Micro-hardness measurements also reveal non-uniform mechanical properties across the weldment. - Highlights: • The microstructure of SA508 HAZ, especially near the FB, is very complex. • The outside of the dissimilar metal welded joint has the highest residual. • The micro-hardness distributions along the DMWJ are non-uniform.« less

Low-Cycle Fatigue Behavior of 10CrNi3MoV High Strength Steel and Its Undermatched Welds

PubMed Central

Liu, Xuesong; Berto, Filippo

2018-01-01

The use of high strength steel allows the design of lighter, more slender and simpler structures due to high strength and favorable ductility. Nevertheless, the increase of yield strength does not guarantee the corresponding improvement of fatigue resistance, which becomes a major concern for engineering structure design, especially for the welded joints. The paper presents a comparison of the low cycle fatigue behaviors between 10CrNi3MoV high strength steel and its undermatched weldments. Uniaxial tension tests, Push-pull, strain-controlled fatigue tests were conducted on base metal and weldments in the strain range of 0.2–1.2%. The monotonic and cyclic stress-strain curves, stress-life, strain-life and energy-life in terms of these materials were analyzed for fatigue assessment of materials discrepancy. The stress-life results of base metal and undermatched weld metal exhibit cyclic softening behaviors. Furthermore, the shapes of 10CrNi3MoV steel hysteresis loops show a satisfactory Masing-type behavior, while the weld metal shows a non-Masing type behavior. Strain, plastic and total strain energy density amplitudes against the number of reversals to failure results demonstrate that the undermatched weld metal presents a higher resistance to fatigue crack initiation than 10CrNi3MoV high strength steel. Finally, fatigue fracture surfaces of specimens were compared by scanning electron microscopy to identify the differences of crack initiation and the propagation between them. PMID:29695140

Low-Cycle Fatigue Behavior of 10CrNi3MoV High Strength Steel and Its Undermatched Welds.

PubMed

Song, Wei; Liu, Xuesong; Berto, Filippo; Razavi, S M J

2018-04-24

The use of high strength steel allows the design of lighter, more slender and simpler structures due to high strength and favorable ductility. Nevertheless, the increase of yield strength does not guarantee the corresponding improvement of fatigue resistance, which becomes a major concern for engineering structure design, especially for the welded joints. The paper presents a comparison of the low cycle fatigue behaviors between 10CrNi3MoV high strength steel and its undermatched weldments. Uniaxial tension tests, Push-pull, strain-controlled fatigue tests were conducted on base metal and weldments in the strain range of 0.2⁻1.2%. The monotonic and cyclic stress-strain curves, stress-life, strain-life and energy-life in terms of these materials were analyzed for fatigue assessment of materials discrepancy. The stress-life results of base metal and undermatched weld metal exhibit cyclic softening behaviors. Furthermore, the shapes of 10CrNi3MoV steel hysteresis loops show a satisfactory Masing-type behavior, while the weld metal shows a non-Masing type behavior. Strain, plastic and total strain energy density amplitudes against the number of reversals to failure results demonstrate that the undermatched weld metal presents a higher resistance to fatigue crack initiation than 10CrNi3MoV high strength steel. Finally, fatigue fracture surfaces of specimens were compared by scanning electron microscopy to identify the differences of crack initiation and the propagation between them.

Optimization to Develop Multiple Response Microstructure and Hardness of Ductile Iron Casting by using GRA

NASA Astrophysics Data System (ADS)

Kabnure, Bahubali Bhupal; Shinde, Vasudev Dhondiram; Kolhapure, Rakesh Ramchandra

2018-05-01

Ductile irons are important engineering materials because of its high strength to weight ratio and castability. The ductile iron castings are used widely for automobile applications due to their wide spectrum of property range. Weight reduction is important in automobile to improve its fuel efficiency which can be achieved by thinning down the casting sections without altering its functionality. Generally, automobile castings are having varying section thickness. Varying thickness castings offers different cooling rates while solidification of the casting. The solidification cooling rate decides the final microstructure of the cast components. Cooling rate was found to affect directly the amount of pearlite and ultimately the as cast properties in varying thickness ductile iron castings. In view of this, the automobile impeller casting is selected for study in the present work as it consists of varying section thickness in which small sections are connected to central hub. The casting solidification simulations were performed and analyzed. The solidification cooling rates were analyzed further to correlate the experimental processing parameters. The samples from poured castings were analyzed for microstructure and hardness at different section thickness. Multiple response optimization of microstructure and hardness was carried out by combined Taguchi and Grey Relational Analysis (GRA). Contribution of input variables on the output variables is attained using ANOVA.

Probing neutron-skin thickness with total reaction cross sections

NASA Astrophysics Data System (ADS)

Horiuchi, W.; Suzuki, Y.; Inakura, T.

2014-01-01

We analyze total reaction cross sections, σR, to explore their sensitivity to the neutron-skin thickness of nuclei. We cover 91 nuclei of O, Ne, Mg, Si, S, Ca, and Ni isotopes. The cross sections are calculated in the Glauber theory using the density distributions obtained with the Skyrme-Hartree-Fock method in three-dimensional coordinate space. Defining a reaction radius, aR=√σR/π , to characterize the nuclear size and target (proton or 12C) dependence, we find an empirical formula for expressing aR with the point matter radius and the skin thickness, and assess two practical ways of determining the skin thickness from proton-nucleus σR values measured at different energies or from σR values measured for different targets.

The cutting of ultrathin sections with the thickness less than 20 nm from biological specimens embedded in resin blocks.

PubMed

Nebesářová, Jana; Hozák, Pavel; Frank, Luděk; Štěpan, Petr; Vancová, Marie

2016-06-01

Low voltage electron microscopes working in transmission mode, like LVEM5 (Delong Instruments, Czech Republic) working at accelerating voltage 5 kV or scanning electron microscope working in transmission mode with accelerating voltage below 1 kV, require ultrathin sections with the thickness below 20 nm. Decreasing of the primary electron energy leads to enhancement of image contrast, which is especially useful in the case of biological samples composed of elements with low atomic numbers. As a result treatments with heavy metals, like post-fixation with osmium tetroxide or ultrathin section staining, can by omitted. The disadvantage is reduced penetration ability of incident electrons influencing the usable thickness of the specimen resulting in the need of ultrathin sections of under 20 nm thickness. In this study we want to answer basic questions concerning the cutting of extremely ultrathin sections: Is it possible routinely and reproducibly to cut extremely thin sections of biological specimens embedded in commonly used resins with contemporary ultramicrotome techniques and under what conditions? Microsc. Res. Tech. 79:512-517, 2016. © 2016 Wiley Periodicals, Inc. © 2016 Wiley Periodicals, Inc.

Microstructural Evolution in Friction Stir Welding of Ti-6Al-4V

NASA Technical Reports Server (NTRS)

Rubisoff, H.; Querin, J.; Magee, D.; Schneider, J.

2008-01-01

Friction stir welding (FSW) is a thermo-mechanical process that utilizes a nonconsumable rotating pin tool to consolidate a weld joint. In the conventional FSW process, the pin tool is responsible for generating both the heat required to soften the material and the forces necessary to deform and combine the weld seam. As such, the geometry of the pin tool is important to the quality of the weld and the process parameters required to produce the weld. Because the geometry of the pin tool is limitless, a reduced set of pin tools was formed to systematically study their effect on the weldment with respect to mechanical properties and resultant microstructure. In this study 0deg, 15deg, 30deg, 45deg, and 60deg tapered, microwave sintered, tungsten carbide (WC) pin tools were used to FSW Ti-6Al-4V. Transverse sections of the weld were used to test for mechanical properties and to document the microstructure using optical microscopy. X-ray diffraction (XRD) was also used to characterize the microstructure in the welds. FSW results for the 45deg and 60deg pin tools are reported in this paper.

Ultrasonic Inspection Of Thick Sections

NASA Technical Reports Server (NTRS)

Friant, C. L.; Djordjevic, B. B.; O'Keefe, C. V.; Ferrell, W.; Klutz, T.

1993-01-01

Ultrasonics used to inspect large, relatively thick vessels for hidden defects. Report based on experiments in through-the-thickness transmission of ultrasonic waves in both steel and filament-wound composite cases of solid-fuel rocket motors.

Measured and calculated fast neutron spectra in a depleted uranium and lithium hydride shielded reactor

NASA Technical Reports Server (NTRS)

Lahti, G. P.; Mueller, R. A.

1973-01-01

Measurements of MeV neutron were made at the surface of a lithium hydride and depleted uranium shielded reactor. Four shield configurations were considered: these were assembled progressively with cylindrical shells of 5-centimeter-thick depleted uranium, 13-centimeter-thick lithium hydride, 5-centimeter-thick depleted uranium, 13-centimeter-thick lithium hydride, 5-centimeter-thick depleted uranium, and 3-centimeter-thick depleted uranium. Measurements were made with a NE-218 scintillation spectrometer; proton pulse height distributions were differentiated to obtain neutron spectra. Calculations were made using the two-dimensional discrete ordinates code DOT and ENDF/B (version 3) cross sections. Good agreement between measured and calculated spectral shape was observed. Absolute measured and calculated fluxes were within 50 percent of one another; observed discrepancies in absolute flux may be due to cross section errors.

Comparison of removed dentin thickness with hand and rotary instruments

PubMed Central

Shahriari, Shahriar; Abedi, Hasan; Hashemi, Mahdi; Jalalzadeh, Seyed Mohsen

2009-01-01

INTRODUCTION: The aim of this study was to evaluate the amount of dentine removed after canal preparation using stainless steel (SS) hand instruments or rotary ProFile instruments. MATERIALS AND METHODS: Thirty-six extracted human teeth with root canal curvatures less than 30º were embedded in clear polyester resin. The roots were cut horizontally at apical 2, 4 and 7 mm. Dentin thickness was measured at each section and the sections were accurately reassembled using a muffle. Root canals were randomly prepared by SS hand instruments or rotary ProFile instruments. Root sections were again separated, and the remaining dentin thickness was measured. Mann-Whitney U and t tests were performed for analytic comparison of the results. RESULTS: The thickness of removed dentin was significantly different between the two used methods (P<0.05). Significantly greater amounts of dentin was removed mesially in all sections in hand instrumentation group (P<0.001). CONCLUSION: ProFile rotary instrumentation prepares root canals with a greater conservation of tooth structure. PMID:23940489

MR imaging detection of cerebral microbleeds: effect of susceptibility-weighted imaging, section thickness, and field strength.

PubMed

Nandigam, R N K; Viswanathan, A; Delgado, P; Skehan, M E; Smith, E E; Rosand, J; Greenberg, S M; Dickerson, B C

2009-02-01

The emergence of cerebral microbleeds (CMB) as common MR imaging findings raises the question of how MR imaging parameters influence CMB detection. To evaluate the effects of modified gradient recalled-echo (GRE) MR imaging methods, we performed an analysis of sequence, section thickness, and field strength on CMB imaging properties and detection in subjects with cerebral amyloid angiopathy (CAA), a condition associated with microhemorrhage. Multiple MR images were obtained from subjects with probable CAA, with varying sequences (GRE versus susceptibility-weighted imaging [SWI]), section thicknesses (1.2-1.5 versus 5 mm), and magnetic field strengths (1.5T versus 3T). Individual CMB were manually identified and analyzed for contrast index (lesion intensity normalized to normal-appearing white matter signal intensity) and diameter. CMB counts were compared between 1.5T thick-section GRE and thin-section SWI for 3 subjects who underwent both protocols in the same scanning session. With other parameters constant, use of SWI, thinner sections, and a higher field strength yielded medium-to-large gains in CMB contrast index (CI; Cohen d 0.71-1.87). SWI was also associated with small increases in CMB diameter (Cohen d <0.3). Conventional thick-section GRE identified only 33% of CMB (103 of 310) seen on thin-section SWI. Lesions prospectively identified on GRE had significantly greater CI and diameter measured on the GRE image than those not prospectively identified. The examined alternatives to conventional GRE MR imaging yield substantially improved CMB contrast and sensitivity for detection. Future studies based on these techniques will most likely yield even higher prevalence estimates for CMB.

MR Imaging Detection of Cerebral Microbleeds: Effect of Susceptibility-Weighted Imaging, Section Thickness, and Field Strength

PubMed Central

Nandigam, R.N.K.; Viswanathan, A.; Delgado, P.; Skehan, M.E.; Smith, E.E.; Rosand, J.; Greenberg, S.M.; Dickerson, B.C.

2009-01-01

BACKGROUND AND PURPOSE: The emergence of cerebral microbleeds (CMB) as common MR imaging findings raises the question of how MR imaging parameters influence CMB detection. To evaluate the effects of modified gradient recalled-echo (GRE) MR imaging methods, we performed an analysis of sequence, section thickness, and field strength on CMB imaging properties and detection in subjects with cerebral amyloid angiopathy (CAA), a condition associated with microhemorrhage. MATERIALS AND METHODS: Multiple MR images were obtained from subjects with probable CAA, with varying sequences (GRE versus susceptibility-weighted imaging [SWI]), section thicknesses (1.2–1.5 versus 5 mm), and magnetic field strengths (1.5T versus 3T). Individual CMB were manually identified and analyzed for contrast index (lesion intensity normalized to normal-appearing white matter signal intensity) and diameter. CMB counts were compared between 1.5T thick-section GRE and thin-section SWI for 3 subjects who underwent both protocols in the same scanning session. RESULTS: With other parameters constant, use of SWI, thinner sections, and a higher field strength yielded medium-to-large gains in CMB contrast index (CI; Cohen d 0.71–1.87). SWI was also associated with small increases in CMB diameter (Cohen d <0.3). Conventional thick-section GRE identified only 33% of CMB (103 of 310) seen on thin-section SWI. Lesions prospectively identified on GRE had significantly greater CI and diameter measured on the GRE image than those not prospectively identified. CONCLUSIONS: The examined alternatives to conventional GRE MR imaging yield substantially improved CMB contrast and sensitivity for detection. Future studies based on these techniques will most likely yield even higher prevalence estimates for CMB. PMID:19001544

Friction Stir Welding of Tapered Thickness Welds Using an Adjustable Pin Tool

NASA Technical Reports Server (NTRS)

Adams, Glynn; Venable, Richard; Lawless, Kirby

2003-01-01

Friction stir welding (FSW) can be used for joining weld lands that vary in thickness along the length of the weld. An adjustable pin tool mechanism can be used to accomplish this in a single-pass, full-penetration weld by providing for precise changes in the pin length relative to the shoulder face during the weld process. The difficulty with this approach is in accurately adjusting the pin length to provide a consistent penetration ligament throughout the weld. The weld technique, control system, and instrumentation must account for mechanical and thermal compliances of the tooling system to conduct tapered welds successfully. In this study, a combination of static and in-situ measurements, as well as active control, is used to locate the pin accurately and maintain the desired penetration ligament. Frictional forces at the pin/shoulder interface were a source of error that affected accurate pin position. A traditional FSW pin tool design that requires a lead angle was used to join butt weld configurations that included both constant thickness and tapered sections. The pitch axis of the tooling was fixed throughout the weld; therefore, the effective lead angle in the tapered sections was restricted to within the tolerances allowed by the pin tool design. The sensitivity of the FSW process to factors such as thickness offset, joint gap, centerline offset, and taper transition offset were also studied. The joint gap and the thickness offset demonstrated the most adverse affects on the weld quality. Two separate tooling configurations were used to conduct tapered thickness welds successfully. The weld configurations included sections in which the thickness decreased along the weld, as well as sections in which the thickness increased along the weld. The data presented here include weld metallography, strength data, and process load data.

Fracture Characteristics of Structural Steels and Weldments

DTIC Science & Technology

1975-11-01

CARACTERISTICS 0F.$ýTRUCTURAL TEL/ - "AD E NTSA .INAL 1 A7 sk S. CONTRACT OR GRANT NUMBER(&) Y.2G. im 9. PERFORMING ORGANIZATION NAME AND ADDRESS -017...36, T- 1,and HY-Y130 Steel and AX. Il 30 15 I Tensile F~racture Surface of A-36 Steel, 12x 31 16 Dimple Rupture in A-6Sel 0X 31 17 Plastic ...sites and the relative plasticity of thle The objective of this study was to use a scanning metal. If many fracture icleation sites initiate mticro

Region-specific tritium enrichment, and not differential beta-absorption, is the major cause of 'quenching' in film autoradiography.

PubMed

McEachron, D L; Nissanov, J; Tretiak, O J

1997-06-01

Tritium quenching refers to the situation in which estimates of tritium content generated by film autoradiography depend on the chemical composition of the tissue as well as on the concentration of the radioisotope. When analysing thin brain sections, for example, regions rich in lipid content generate reduced optical densities on x-ray film compared with lipid-poor regions even when the total tissue concentration of tritium in those regions is identical. We hypothesize that the dried thickness of regions within sections depends upon the relative concentrations and types of lipid within the regions. Areas low in white matter dry thinner than areas high in white matter, leading to a relative enrichment of tritium in the thinner regions. To test this model, a series of brain pastes were made with different concentrations of grey and white matter and impregnated with equal amounts of tritium. The thickness of dried sections was compared with percentage of white matter and apparent radioactive content as determined by autoradiogram analysis. The results demonstrated that thickness increased, and apparent radioactivity decreased, with higher percentages of white matter. In the second experiment, thickness measurements from dried sections were successfully used to correct the apparent radioisotope content of autoradiograms created from tritium containing white- and grey-matter tissue slices. We conclude that within-section thickness variation is the major physical cause for 'tritium quenching'.

Thick-target transmission method for excitation functions of interaction cross sections

NASA Astrophysics Data System (ADS)

Aikawa, M.; Ebata, S.; Imai, S.

2016-09-01

We propose a method, called as thick-target transmission (T3) method, to obtain an excitation function of interaction cross sections. In an ordinal experiment to measure the excitation function of interaction cross sections by the transmission method, we need to change the beam energy for each cross section. In the T3 method, the excitation function is derived from the beam attenuations measured at the targets of different thicknesses without changing the beam energy. The advantage of the T3 method is the simplicity and availability for radioactive beams. To confirm the availability, we perform a simulation for the 12C + 27Al system with the PHITS code instead of actual experiments. Our results have large uncertainties but well reproduce the tendency of the experimental data.

Antibody incubation at 37°C improves fluorescent immunolabeling in free-floating thick tissue sections.

PubMed

Xiao, Xia; Feng, Ya-Ping; Du, Bin; Sun, Han-Ru; Ding, You-Quan; Qi, Jian-Guo

2017-03-01

Fluorescent immunolabeling and imaging in free-floating thick (50-60 μm) tissue sections is relatively simple in practice and enables design-based non-biased stereology, or 3-D reconstruction and analysis. This method is widely used for 3-D in situ quantitative biology in many areas of biological research. However, the labeling quality and efficiency of standard protocols for fluorescent immunolabeling of these tissue sections are not always satisfactory. Here, we systematically evaluate the effects of raising the conventional antibody incubation temperatures (4°C or 21°C) to mammalian body temperature (37°C) in these protocols. Our modification significantly enhances the quality (labeling sensitivity, specificity, and homogeneity) and efficiency (antibody concentration and antibody incubation duration) of fluorescent immunolabeling of free-floating thick tissue sections.

Experimental Study of the Oxidation, Ignition, and Soot Formation Characteristics of Jet Fuel

DTIC Science & Technology

2010-09-29

section and controls the heat flux applied to six heated zones along the 4.11 m long driven section, and 2.5 cm thick mineral wool insulation that...The mixing manifold was insulated with 1.1 cm thick silicon foam rubber insulation, and the mixing vessel was insulated with 2.5 cm- thick mineral ... wool insulation. Experimental work for a number of compounds with variation in manifold and tank heating showed no observable difference in measured

Properties of Urea-Doped Ice in the CRREL Test Basin,

DTIC Science & Technology

1983-03-01

thickness versus initial ice thickness at start of warm-up ................ 7 9. Thin sections of urea-doped ice...following section ) on the mechanical properties of the tank, essential for achieving an ice sheet of uni- the model ice was investigated. In particular...Figure 1. elastic foundation: Measurements ~i 7 A 1 f 2 Temperature As mentioned in the preceding section , water and temperature was measured with a 1/50

49 CFR 192.109 - Nominal wall thickness (t) for steel pipe.

Code of Federal Regulations, 2011 CFR

2011-10-01

... 49 Transportation 3 2011-10-01 2011-10-01 false Nominal wall thickness (t) for steel pipe. 192.109 Section 192.109 Transportation Other Regulations Relating to Transportation (Continued) PIPELINE AND... Nominal wall thickness (t) for steel pipe. (a) If the nominal wall thickness for steel pipe is not known...

49 CFR 192.109 - Nominal wall thickness (t) for steel pipe.

Code of Federal Regulations, 2014 CFR

2014-10-01

... 49 Transportation 3 2014-10-01 2014-10-01 false Nominal wall thickness (t) for steel pipe. 192.109 Section 192.109 Transportation Other Regulations Relating to Transportation (Continued) PIPELINE AND... Nominal wall thickness (t) for steel pipe. (a) If the nominal wall thickness for steel pipe is not known...

49 CFR 192.109 - Nominal wall thickness (t) for steel pipe.

Code of Federal Regulations, 2013 CFR

2013-10-01

... 49 Transportation 3 2013-10-01 2013-10-01 false Nominal wall thickness (t) for steel pipe. 192.109 Section 192.109 Transportation Other Regulations Relating to Transportation (Continued) PIPELINE AND... Nominal wall thickness (t) for steel pipe. (a) If the nominal wall thickness for steel pipe is not known...

49 CFR 192.109 - Nominal wall thickness (t) for steel pipe.

Code of Federal Regulations, 2010 CFR

2010-10-01

... 49 Transportation 3 2010-10-01 2010-10-01 false Nominal wall thickness (t) for steel pipe. 192.109 Section 192.109 Transportation Other Regulations Relating to Transportation (Continued) PIPELINE AND... Nominal wall thickness (t) for steel pipe. (a) If the nominal wall thickness for steel pipe is not known...

49 CFR 192.109 - Nominal wall thickness (t) for steel pipe.

Code of Federal Regulations, 2012 CFR

2012-10-01

... 49 Transportation 3 2012-10-01 2012-10-01 false Nominal wall thickness (t) for steel pipe. 192.109 Section 192.109 Transportation Other Regulations Relating to Transportation (Continued) PIPELINE AND... Nominal wall thickness (t) for steel pipe. (a) If the nominal wall thickness for steel pipe is not known...

SWI or T2*: which MRI sequence to use in the detection of cerebral microbleeds? The Karolinska Imaging Dementia Study.

PubMed

Shams, S; Martola, J; Cavallin, L; Granberg, T; Shams, M; Aspelin, P; Wahlund, L O; Kristoffersen-Wiberg, M

2015-06-01

Cerebral microbleeds are thought to have potentially important clinical implications in dementia and stroke. However, the use of both T2* and SWI MR imaging sequences for microbleed detection has complicated the cross-comparison of study results. We aimed to determine the impact of microbleed sequences on microbleed detection and associated clinical parameters. Patients from our memory clinic (n = 246; 53% female; mean age, 62) prospectively underwent 3T MR imaging, with conventional thick-section T2*, thick-section SWI, and conventional thin-section SWI. Microbleeds were assessed separately on thick-section SWI, thin-section SWI, and T2* by 3 raters, with varying neuroradiologic experience. Clinical and radiologic parameters from the dementia investigation were analyzed in association with the number of microbleeds in negative binomial regression analyses. Prevalence and number of microbleeds were higher on thick-/thin-section SWI (20/21%) compared with T2*(17%). There was no difference in microbleed prevalence/number between thick- and thin-section SWI. Interrater agreement was excellent for all raters and sequences. Univariate comparisons of clinical parameters between patients with and without microbleeds yielded no difference across sequences. In the regression analysis, only minor differences in clinical associations with the number of microbleeds were noted across sequences. Due to the increased detection of microbleeds, we recommend SWI as the sequence of choice in microbleed detection. Microbleeds and their association with clinical parameters are robust to the effects of varying MR imaging sequences, suggesting that comparison of results across studies is possible, despite differing microbleed sequences. © 2015 by American Journal of Neuroradiology.

Ground penetrating radar survey of pavement thickness on Mn/Road sections : final report

DOT National Transportation Integrated Search

1994-11-01

The research shows that highway speed horn antenna ground penetrating radar equipment and automated analysis software can accurately measure asphalt thickness. To accurately measure concrete and base thickness, lower speed ground coupled equipment al...

Brain BLAQ: Post-hoc thick-section histochemistry for localizing optogenetic constructs in neurons and their distal terminals

PubMed Central

Kupferschmidt, David A.; Cody, Patrick A.; Lovinger, David M.; Davis, Margaret I.

2015-01-01

Optogenetic constructs have revolutionized modern neuroscience, but the ability to accurately and efficiently assess their expression in the brain and associate it with prior functional measures remains a challenge. High-resolution imaging of thick, fixed brain sections would make such post-hoc assessment and association possible; however, thick sections often display autofluorescence that limits their compatibility with fluorescence microscopy. We describe and evaluate a method we call “Brain BLAQ” (Block Lipids and Aldehyde Quench) to rapidly reduce autofluorescence in thick brain sections, enabling efficient axon-level imaging of neurons and their processes in conventional tissue preparations using standard epifluorescence microscopy. Following viral-mediated transduction of optogenetic constructs and fluorescent proteins in mouse cortical pyramidal and dopaminergic neurons, we used BLAQ to assess innervation patterns in the striatum, a region in which autofluorescence often obscures the imaging of fine neural processes. After BLAQ treatment of 250–350 μm-thick brain sections, axons and puncta of labeled afferents were visible throughout the striatum using a standard epifluorescence stereomicroscope. BLAQ histochemistry confirmed that motor cortex (M1) projections preferentially innervated the matrix component of lateral striatum, whereas medial prefrontal cortex projections terminated largely in dorsal striosomes and distinct nucleus accumbens subregions. Ventral tegmental area dopaminergic projections terminated in a similarly heterogeneous pattern within nucleus accumbens and ventral striatum. Using a minimal number of easily manipulated and visualized sections, and microscopes available in most neuroscience laboratories, BLAQ enables simple, high-resolution assessment of virally transduced optogenetic construct expression, and post-hoc association of this expression with molecular markers, physiology and behavior. PMID:25698938

Effect of dropped plies on the strength of graphite-epoxy laminates

NASA Technical Reports Server (NTRS)

Curry, James M.; Johnson, Eric R.; Starnes, James H., Jr.

1987-01-01

The reduction in the compressive and tensile strengths of graphite-epoxy laminates with thickness discontinuities due to dropped plies was studied by experiment and analysis. The specimens were fabricated with all the dropped plies lumped together in the center of a sixteen-ply quasi-isotropic layup, such that one surface was flat and the slope of the opposite surface changed abruptly at the dropped ply location to accommodate the thickness change. Even though the thick and thin sections are symmetrically laminated, there exists bending-extension coupling due to the geometric eccentricity of the middle planes of the thick and thin sections. Experiments were conducted on fifty-four specimens that differed in the configuration of the dropped plies only. The strength of a laminate with dropped plies is less than the strength of its thin section, and the compressive strength of a laminate with dropped plies is less than its tensile strength. The reduction in strength is directly related to the axial stiffness change between the thick and thin sections. To examine the mechanism of failure, the three-dimensional state of stress in the dropped ply region was evaluated by the finite element method. A tensile interlaminar criterion predicted the correct location of failure, but underestimated the failure load.

An in vitro study of mesiobuccal root thickness of maxillary first molars.

PubMed

Mohammadzadeh Akhlaghi, Nahid; Ravandoust, Yasaman; Najafi, Mohammad; Dadresanfar, Bahareh

2012-01-01

Understanding the internal anatomy of root canal system can significantly influence outcomes of root canal treatment. The aim of this in vitro study was to measure the thickness of mesiobuccal root at different levels in maxillary first molars. In this cross-sectional study, forty extracted human maxillary first molars were radiographed; accordingly, the mesial and distal root thicknesses of mesiobuccal (MB) roots were measured at four parallel horizontal levels. The samples were sectioned at the measured levels and then sections were scanned and saved in the computer. Buccal (B), Palatal (P), Mesial (M) and Distal (D) aspects of root thicknesses in single-canalled roots were measured. In two-canalled mesiobuccal roots, Distobuccal (DB) and Distopalatal (DP) aspects were evaluated alongside other measurements. Average radicular thickness in each aspect and each level was compared using ANOVA and t-test. A total of 25 had two canals and 15 had one canal in MB root. In single-canalled roots M and D aspects were the thinnest whereas in two-canalled samples, the thicknesses of DP and DB aspects were significantly less than others (P<0.001). The B and P had the greatest thicknesses in all the samples. The results showed that special attention should be paid to "danger zone" areas of mesiobuccal maxillary first molar roots in order to avoid technical mishaps.

Stress measurement in thick plates using nonlinear ultrasonics

DOE Office of Scientific and Technical Information (OSTI.GOV)

Abbasi, Zeynab, E-mail: zabbas5@uic.edu, E-mail: dozevin@uic.edu; Ozevin, Didem, E-mail: zabbas5@uic.edu, E-mail: dozevin@uic.edu

2015-03-31

In this paper the interaction between nonlinear ultrasonic characteristics and stress state of complex loaded thick steel plates using fundamental theory of nonlinear ultrasonics is investigated in order to measure the stress state at a given cross section. The measurement concept is based on phased array placement of ultrasonic transmitter-receiver to scan three angles of a given cross section using Rayleigh waves. The change in the ultrasonic data in thick steel plates is influenced by normal and shear stresses; therefore, three measurements are needed to solve the equations simultaneously. Different thickness plates are studied in order to understand the interactionmore » of Rayleigh wave penetration depth and shear stress. The purpose is that as the thickness becomes smaller, the shear stress becomes negligible at the angled measurement. For thicker cross section, shear stress becomes influential if the depth of penetration of Rayleigh wave is greater than the half of the thickness. The influences of plate thickness and ultrasonic frequency on the identification of stress tensor are numerically studied in 3D structural geometry and Murnaghan material model. The experimental component of this study includes uniaxial loading of the plate while measuring ultrasonic wave at three directions (perpendicular, parallel and angled to the loading direction). Instead of rotating transmitter-receiver pair for each test, a device capable of measuring the three angles is designed.« less

Transverse-Weld Tensile Properties of a New Al-4Cu-2Si Alloy as Filler Metal

NASA Astrophysics Data System (ADS)

Sampath, K.

2009-12-01

AA2195, an Al-Cu-Li alloy in the T8P4 age-hardened condition, is a candidate aluminum armor for future combat vehicles, as this material offers higher static strength and ballistic protection than current aluminum armor alloys. However, certification of AA2195 alloy for armor applications requires initial qualification based on the ballistic performance of welded panels in the as-welded condition. Currently, combat vehicle manufacturers primarily use gas metal arc welding (GMAW) process to meet their fabrication needs. Unfortunately, a matching GMAW consumable electrode is currently not commercially available to allow effective joining of AA2195 alloy. This initial effort focused on an innovative, low-cost, low-risk approach to identify an alloy composition suitable for effective joining of AA2195 alloy, and evaluated transverse-weld tensile properties of groove butt joints produced using the identified alloy. Selected commercial off-the-shelf (COTS) aluminum alloy filler wires were twisted to form candidate twisted filler rods. Representative test weldments were produced using AA2195 alloy, candidate twisted filler rods and gas tungsten arc welding (GTAW) process. Selected GTA weldments produced using Al-4wt.%Cu-2wt.%Si alloy as filler metal consistently provided transverse-weld tensile properties in excess of 275 MPa (40 ksi) UTS and 8% El (over 25 mm gage length), thereby showing potential for acceptable ballistic performance of as-welded panels. Further developmental work is required to evaluate in detail GMAW consumable wire electrodes based on the Al-Cu-Si system containing 4.2-5.0 wt.% Cu and 1.6-2.0 wt.% Si.

Creep of A508/533 Pressure Vessel Steel

DOE Office of Scientific and Technical Information (OSTI.GOV)

Richard Wright

2014-08-01

ABSTRACT Evaluation of potential Reactor Pressure Vessel (RPV) steels has been carried out as part of the pre-conceptual Very High Temperature Reactor (VHTR) design studies. These design studies have generally focused on American Society of Mechanical Engineers (ASME) Code status of the steels, temperature limits, and allowable stresses. Initially, three candidate materials were identified by this process: conventional light water reactor (LWR) RPV steels A508 and A533, 2¼Cr-1Mo in the annealed condition, and Grade 91 steel. The low strength of 2¼Cr-1Mo at elevated temperature has eliminated this steel from serious consideration as the VHTR RPV candidate material. Discussions with themore » very few vendors that can potentially produce large forgings for nuclear pressure vessels indicate a strong preference for conventional LWR steels. This preference is based in part on extensive experience with forging these steels for nuclear components. It is also based on the inability to cast large ingots of the Grade 91 steel due to segregation during ingot solidification, thus restricting the possible mass of forging components and increasing the amount of welding required for completion of the RPV. Grade 91 steel is also prone to weld cracking and must be post-weld heat treated to ensure adequate high-temperature strength. There are also questions about the ability to produce, and very importantly, verify the through thickness properties of thick sections of Grade 91 material. The availability of large components, ease of fabrication, and nuclear service experience with the A508 and A533 steels strongly favor their use in the RPV for the VHTR. Lowering the gas outlet temperature for the VHTR to 750°C from 950 to 1000°C, proposed in early concept studies, further strengthens the justification for this material selection. This steel is allowed in the ASME Boiler and Pressure Vessel Code for nuclear service up to 371°C (700°F); certain excursions above that temperature are allowed by Code Case N-499-2 (now incorporated as an appendix to Section III Division 5 of the Code). This Code Case was developed with a rather sparse data set and focused primarily on rolled plate material (A533 specification). Confirmatory tests of creep behavior of both A508 and A533 are described here that are designed to extend the database in order to build higher confidence in ensuring the structural integrity of the VHTR RPV during off-normal conditions. A number of creep-rupture tests were carried out at temperatures above the 371°C (700°F) Code limit; longer term tests designed to evaluate minimum creep behavior are ongoing. A limited amount of rupture testing was also carried out on welded material. All of the rupture data from the current experiments is compared to historical values from the testing carried out to develop Code Case N-499-2. It is shown that the A508/533 basemetal tested here fits well with the rupture behavior reported from the historical testing. The presence of weldments significantly reduces the time to rupture. The primary purpose of this report is to summarize and record the experimental results in a single document.« less

Influence of Casting Section Thickness on Fatigue Strength of Austempered Ductile Iron

NASA Astrophysics Data System (ADS)

Olawale, J. O.; Ibitoye, S. A.

2017-10-01

The influence of casting section thickness on fatigue strength of austempered ductile iron was investigated in this study. ASTM A536 65-45-12 grade of ductile iron was produced, machined into round samples of 10, 15, 20 and 25 mm diameter, austenitized at a temperature of 820 °C, quenched into an austempering temperature (TA) of 300 and 375 °C and allowed to be isothermally transformed at these temperatures for a fixed period of 2 h. From the samples, fatigue test specimens were machined to conform to ASTM E-466. Scanning electron microscopy (SEM) and x-ray diffraction (XRD) methods were used to characterize microstructural morphology and phase distribution of heat-treated samples. The fatigue strength decreases as the section thickness increases. The SEM image and XRD patterns show a matrix of acicular ferrite and carbon-stabilized austenite with ferrite coarsening and volume fraction of austenite reducing as the section thickness increases. The study concluded that the higher the value of carbon-stabilized austenite the higher the fatigue strength while it decreases as the ausferrite structure becomes coarse.

Economical Fabrication of Thick-Section Ceramic Matrix Composites

NASA Technical Reports Server (NTRS)

Babcock, Jason; Ramachandran, Gautham; Williams, Brian; Benander, Robert

2010-01-01

A method was developed for producing thick-section [>2 in. (approx.5 cm)], continuous fiber-reinforced ceramic matrix composites (CMCs). Ultramet-modified fiber interface coating and melt infiltration processing, developed previously for thin-section components, were used for the fabrication of CMCs that were an order of magnitude greater in thickness [up to 2.5 in. (approx.6.4 cm)]. Melt processing first involves infiltration of a fiber preform with the desired interface coating, and then with carbon to partially densify the preform. A molten refractory metal is then infiltrated and reacts with the excess carbon to form the carbide matrix without damaging the fiber reinforcement. Infiltration occurs from the inside out as the molten metal fills virtually all the available void space. Densification to <5 vol% porosity is a one-step process requiring no intermediate machining steps. The melt infiltration method requires no external pressure. This prevents over-infiltration of the outer surface plies, which can lead to excessive residual porosity in the center of the part. However, processing of thick-section components required modification of the conventional process conditions, and the means by which the large amount of molten metal is introduced into the fiber preform. Modification of the low-temperature, ultraviolet-enhanced chemical vapor deposition process used to apply interface coatings to the fiber preform was also required to accommodate the high preform thickness. The thick-section CMC processing developed in this work proved to be invaluable for component development, fabrication, and testing in two complementary efforts. In a project for the Army, involving SiC/SiC blisk development, nominally 0.8 in. thick x 8 in. diameter (approx. 2 cm thick x 20 cm diameter) components were successfully infiltrated. Blisk hubs were machined using diamond-embedded cutting tools and successfully spin-tested. Good ply uniformity and extremely low residual porosity (<2 percent) were achieved, the latter being far lower than that achieved with SiC matrix composites fabricated via CVI or PIP. The pyrolytic carbon/zirconium nitride interface coating optimized in this work for use on carbon fibers was incorporated in the SiC/SiC composites and yielded a >41 ksi (approx. 283 MPa) flexural strength.

The aerodynamic characteristics of eight very thick airfoils from tests in the variable density wind tunnel

NASA Technical Reports Server (NTRS)

Jacobs, Eastman N

1932-01-01

Report presents the results of wind tunnel tests on a group of eight very thick airfoils having sections of the same thickness as those used near the roots of tapered airfoils. The tests were made to study certain discontinuities in the characteristic curves that have been obtained from previous tests of these airfoils, and to compare the characteristics of the different sections at values of the Reynolds number comparable with those attained in flight. The discontinuities were found to disappear as the Reynolds number was increased. The results obtained from the large-scale airfoil, a symmetrical airfoil having a thickness ratio of 21 per cent, has the best general characteristics.

Cutting work in thick section cryomicrotomy.

PubMed

Saubermann, A J; Riley, W D; Beeuwkes, R

1977-09-01

The forces during cryosectioning were measured using miniature strain gauges attached to a load cell fitted to the drive arm of the Porter-Blum MT-2 cryomicrotome. Work was calculated and the data normalized to a standard (1 mm X 1 mm X 0.5 micrometer) section. Thermal energy generated was also calculated. Five parameters were studied: cutting angle, thickness, temperature, hardness, and block shape. Force patterns could be divided into three major groups thought to represent cutting (Type I), large fracture planes greater than 10 micrometer in length (Type II), and small fracture planes less than 10 micrometer in length (Type III). Type I and Type II produced satisfactory sections. Work in cutting ranged from an average of 78.4 muJ to 568.8 muJ. Cutting angle and temperature had the greatest effect on sectioning. Heat generated would be sufficient to cause through-section melting for 0.5 micrometer thick sections assuming the worst possible case, namely that all heat went into the section without loss. Presence of a Type II pattern (large fracture pattern) is thought to be presumptive evidence against thawing.

Rotating disk electrodes to assess river biofilm thickness and elasticity.

PubMed

Boulêtreau, Stéphanie; Charcosset, Jean-Yves; Gamby, Jean; Lyautey, Emilie; Mastrorillo, Sylvain; Azémar, Frédéric; Moulin, Frédéric; Tribollet, Bernard; Garabetian, Frédéric

2011-01-01

The present study examined the relevance of an electrochemical method based on a rotating disk electrode (RDE) to assess river biofilm thickness and elasticity. An in situ colonisation experiment in the River Garonne (France) in August 2009 sought to obtain natural river biofilms exhibiting differentiated architecture. A constricted pipe providing two contrasted flow conditions (about 0.1 and 0.45 m s(-1) in inflow and constricted sections respectively) and containing 24 RDE was immersed in the river for 21 days. Biofilm thickness and elasticity were quantified using an electrochemical assay on 7 and 21 days old RDE-grown biofilms (t(7) and t(21), respectively). Biofilm thickness was affected by colonisation length and flow conditions and ranged from 36 ± 15 μm (mean ± standard deviation, n = 6) in the fast flow section at t(7) to 340 ± 140 μm (n = 3) in the slow flow section at t(21). Comparing the electrochemical signal to stereomicroscopic estimates of biofilms thickness indicated that the method consistently allowed (i) to detect early biofilm colonisation in the river and (ii) to measure biofilm thickness of up to a few hundred μm. Biofilm elasticity, i.e. biofilm squeeze by hydrodynamic constraint, was significantly higher in the slow (1300 ± 480 μm rpm(1/2), n = 8) than in the fast flow sections (790 ± 350 μm rpm(1/2), n = 11). Diatom and bacterial density, and biofilm-covered RDE surface analyses (i) confirmed that microbial accrual resulted in biofilm formation on the RDE surface, and (ii) indicated that thickness and elasticity represent useful integrative parameters of biofilm architecture that could be measured on natural river assemblages using the proposed electrochemical method. Copyright © 2010 Elsevier Ltd. All rights reserved.

Enamel thickness variation of deciduous first and second upper molars in modern humans and Neanderthals.

PubMed

Fornai, Cinzia; Benazzi, Stefano; Svoboda, Jiří; Pap, Ildikó; Harvati, Katerina; Weber, Gerhard W

2014-11-01

Enamel thickness and dental tissue proportions have been recognized as effective taxonomic discriminators between Neanderthal and modern humans teeth. However, most of the research on this topic focused on permanent teeth, and little information is available for the deciduous dentition. Moreover, although worn teeth are more frequently found than unworn teeth, published data for worn teeth are scarce and methods for the assessment of their enamel thickness need to be developed. Here, we addressed this issue by studying the 2D average enamel thickness (AET) and 2D relative enamel thickness (RET) of Neanderthal and modern humans unworn to moderately worn upper first deciduous molars (dm(1)s) and upper second deciduous molars (dm(2)s). In particular, we used 3D μCT data to investigate the mesial section for dm(1)s and both mesial and buccal sections for dm(2)s. Our results confirmed previous findings of an Neanderthal derived condition of thin enamel, and thinner enamel in dm(1)s than dm(2)s in both Neanderthal and modern humans. We demonstrated that the Neanderthal 2D RET indices are significantly lower than those of modern humans at similar wear stages in both dm(1)s and dm(2)s (p < 0.05). The discriminant analysis showed that using 2D RET from dm(1) and dm(2) sections at different wear stages up to 93% of the individuals are correctly classified. Moreover, we showed that the dm(2) buccal sections, although non-conventionally used, might have an advantage on mesial sections since they distinguish as well as mesial sections but tend to be less worn. Therefore, the 2D analysis of enamel thickness is suggested as a means for taxonomic discrimination between modern humans and Neanderthal unworn to moderately worn upper deciduous molars. Copyright © 2014 Elsevier Ltd. All rights reserved.

Use of apparent thickness for preprocessing of low-frequency electromagnetic data in inversion-based multibarrier evaluation workflow

NASA Astrophysics Data System (ADS)

Omar, Saad; Omeragic, Dzevat

2018-04-01

The concept of apparent thicknesses is introduced for the inversion-based, multicasing evaluation interpretation workflow using multifrequency and multispacing electromagnetic measurements. A thickness value is assigned to each measurement, enabling the development of two new preprocessing algorithms to remove casing collar artifacts. First, long-spacing apparent thicknesses are used to remove, from the pipe sections, artifacts ("ghosts") caused by the transmitter crossing a casing collar or corrosion. Second, a collar identification, localization, and assignment algorithm is developed to enable robust inversion in collar sections. Last, casing eccentering can also be identified on the basis of opposite deviation of short-spacing phase and magnitude apparent thicknesses from the nominal value. The proposed workflow can handle an arbitrary number of nested casings and has been validated on synthetic and field data.

Probing Neutron-Skin Thickness of Unstable Nuclei with Total Reaction Cross Sections

NASA Astrophysics Data System (ADS)

Horiuchi, Wataru; Suzuki, Yasuyuki; Inakura, Tsunenori

We present our recent analysis of the total reaction cross sections, σR, of unstable nuclei and discuss their sensitivity to the neutron-skin thickness. The σR is calculated with the Glauber model using projectile densities obtained with the Skyrme-Hartree-Fock method on the three-dimensional coordinate space. We cover 91 nuclei of O, Ne, Mg, Si, S, Ca, and Ni isotopes. Defining a reaction radius, aR = √{σ R/π } , to characterize the nuclear size and target (proton or 12C) dependence, we see the 12C target probes the matter radius while the proton target is sensitive to the skin-thickness. We find an empirical formula for expressing aR with the point matter radius and the skin thickness, which can be used to determine the skin thickness.

Retrieval of the atmospheric compounds using a spectral optical thickness information

DOE Office of Scientific and Technical Information (OSTI.GOV)

Ioltukhovski, A.A.

A spectral inversion technique for retrieval of the atmospheric gases and aerosols contents is proposed. This technique based upon the preliminary measurement or retrieval of the spectral optical thickness. The existence of a priori information about the spectral cross sections for some of the atmospheric components allows to retrieve the relative contents of these components in the atmosphere. Method of smooth filtration makes possible to estimate contents of atmospheric aerosols with known cross sections and to filter out other aerosols; this is done independently from their relative contribution to the optical thickness.

An evaluation of three helicopter rotor sections

NASA Technical Reports Server (NTRS)

Hicks, R. M.; Collins, L. J.

1985-01-01

Three helicopter rotor sections were tested in the NASA Ames Research Center 2- by 2-Foot Transonic Wind Tunnel over a Mach range from 0.2 to 0.88. The sections tested had maximum thickness/chord ratios of 0.078, 0.09, and 0.10. The thickest section was of early technology and had been tested previously in other wind tunnels. This section was included in the investigation to establish a basis for comparing the two thinner sections, which were of recent design. The results of the investigation showed that the pitching-moment characteristics for the three airfoil sections were acceptable. The drag divergence Mach numbers for the three sections were 0.80, 0.825, and 0.845 in order of decreasing thickness.

Propagation of thickness shear waves in a periodically corrugated quartz crystal plate and its application exploration in acoustic wave filters.

PubMed

Li, Peng; Cheng, Li

2017-05-01

The propagation of thickness shear waves in a periodically corrugated quartz crystal plate is investigated in the present paper using a power series expansion technique. In the proposed simulation model, an equivalent continuity of shear stress moment is introduced as an approximation to handle sectional interfaces with abrupt thickness changes. The Bloch theory is applied to simulate the band structures for three different thickness variation patterns. It is shown that the power series expansion method exhibits good convergence and accuracy, in agreement with results by finite element method (FEM). A broad stop band can be obtained in the power transmission spectra owing to the trapped thickness shear modes excited by the thickness variation, whose physical mechanism is totally different from the well-known Bragg scattering effect and is insensitive to the structural periodicity. Based on the observed energy trapping phenomenon, an acoustic wave filter is proposed in a quartz plate with sectional decreasing thickness, which inhibits wave propagation in different regions. Copyright © 2017 Elsevier B.V. All rights reserved.

A comparison between destructive and non-destructive techniques in determining coating thickness

NASA Astrophysics Data System (ADS)

Haider, F. I.; Suryanto; Ani, M. H.; Mahmood, M. H.

2018-01-01

Measuring coating thickness is an important part in research works related to coating applications. In general, techniques for measuring coating thickness may be divided into destructive and non-destructive methods which are commonly used depending on the applications. The objective of this study is to compare two methods measuring the coating thickness of electroplating copper coating on the austenitic stainless-steel substrate. The electroplating was carried out in a solution containing 200 g/L CuSO4, 100 g/L H2SO4 at room temperature and current of 40mA/cm2 during 20, 40, 60, 80 and 100 mins as coating periods. And the coating thickness was measured by two methods, cross sectional analysis as a destructive technique and weight gain as a non-destructive technique. The results show that at 20 mins coating time interval, the thickness measured by cross sectional method was 16.67 μm and by weight gain method was 17.37 μm, with difference of 0.7 μm and percentage error of 4.11%. This error increased to 5.27% at 100mins time interval, where the values of the thickness measured by cross sectional and weight gain were 86.33 μm and 81.9 μm respectively, and the difference was 4.43 μm. Moreover, though the weight gain method is fast and gives the indication for the termination of a coating process, information regarding the uniformity, porosity and the presence of cracks cannot be obtained. On the other hand, determining the coating thickness using destructive method will damage the sample.

Evaluation of various hot mix asphalt pavement thicknesses over rubblized concrete pavement.

DOT National Transportation Integrated Search

2011-07-01

In 1999, the Wisconsin DOT constructed two test sections as part of a rubblized PCC pavement project on I-39 to evaluate whether : increased HMA thickness could extend the pavement system's service life. Design thicknesses of the control and test sec...

System for measuring film thickness

DOEpatents

Batishko, Charles R.; Kirihara, Leslie J.; Peters, Timothy J.; Rasmussen, Donald E.

1990-01-01

A system for determining the thicknesses of thin films of materials exhibiting fluorescence in response to exposure to excitation energy from a suitable source of such energy. A section of film is illuminated with a fixed level of excitation energy from a source such as an argon ion laser emitting blue-green light. The amount of fluorescent light produced by the film over a limited area within the section so illuminated is then measured using a detector such as a photomultiplier tube. Since the amount of fluorescent light produced is a function of the thicknesses of thin films, the thickness of a specific film can be determined by comparing the intensity of fluorescent light produced by this film with the intensity of light produced by similar films of known thicknesses in response to the same amount of excitation energy. The preferred embodiment of the invention uses fiber optic probes in measuring the thicknesses of oil films on the operational components of machinery which are ordinarily obscured from view.

Preliminary Investigation in the NACA Low-Turbulence Tunnel of Low-drag Airfoil Sections Suitable for Admitting Air at the Leading Edge

NASA Technical Reports Server (NTRS)

von Doenhoff, Albert E.; Horton, Elmer A.

1942-01-01

An investigation was carried out in the NACA low-turbulence tunnel to develop low-drag airfoil sections suitable for admitting air at the leading edge. A thickness distribution having the desired type of pressure distribution was found from tests of a flexible model. Other airfoil shapes were derived from this original shape by varying the thickness, the camper, the leading-edge radius, and the size of the leading-edge opening. Data are presented giving the characteristics of the airfoil shapes in the range of lift coefficients for high-speed and cruising flight. Shapes have been developed which show no substantial increases in drag over that of the same position along the chord. Many of these shapes appear to have higher critical compressibility speeds than plain airfoils of the same thickness. Low-drag airfoil sections have been developed with openings in the leading edge as large as 41.5 percent of the maximum thickness. The range of lift coefficients for low drag in several cases is nearly as large as that of the corresponding plain airfoil sections. Preliminary measurements of maximum lift characteristics indicate that nose-opening sections of the type herein considered may not produce any marked effects on the maximum lift coefficient.

Estimating pore and cement volumes in thin section

USGS Publications Warehouse

Halley, R.B.

1978-01-01

Point count estimates of pore, grain and cement volumes from thin sections are inaccurate, often by more than 100 percent, even though they may be surprisingly precise (reproducibility + or - 3 percent). Errors are produced by: 1) inclusion of submicroscopic pore space within solid volume and 2) edge effects caused by grain curvature within a 30-micron thick thin section. Submicroscopic porosity may be measured by various physical tests or may be visually estimated from scanning electron micrographs. Edge error takes the form of an envelope around grains and increases with decreasing grain size and sorting, increasing grain irregularity and tighter grain packing. Cements are greatly involved in edge error because of their position at grain peripheries and their generally small grain size. Edge error is minimized by methods which reduce the thickness of the sample viewed during point counting. Methods which effectively reduce thickness include use of ultra-thin thin sections or acetate peels, point counting in reflected light, or carefully focusing and counting on the upper surface of the thin section.

CHARACTERIZATION OF DEFECTS IN ALLOY 152, 52 AND 52M WELDS

DOE Office of Scientific and Technical Information (OSTI.GOV)

Bruemmer, Stephen M.; Toloczko, Mychailo B.; Olszta, Matthew J.

2009-08-27

Defect distributions have been documented by optical metallography, scanning electron microscopy and electron backscatter diffraction in alloy 152 and 52 mockups welds, alloy 52 and 52M overlay mockups and an alloy 52M inlay. Primary defects were small cracks at grain boundaries except for more extensive cracking in the dilution zone of an alloy 52 overlay on 304SS. Detailed characterizations of the dilution zone cracks were performed by analytical transmission electron microscopy identifying grain boundary titanium-nitride precipitation associated with the intergranular separations. I. INTRODUCTION Weldments continue to be a primary location of stress-corrosion cracking (SCC) in light-water reactor systems. While problemsmore » related to heat-affected-zone (HAZ) sensitization and intergranular (IG) SCC of austenitic stainless alloys in boiling-water reactors (BWRs) have been significantly reduced, SCC has now been observed in HAZs of non-sensitized materials and in dissimilar metal welds where Ni-base alloy weld metals are used. IGSCC in weld metals has been observed in both BWRs and pressurized water reactors (PWRs) with recent examples for PWR pressure vessel penetrations producing the most concern. This has led to the replacement of alloy 600/182/82 welds with higher Cr, more corrosion-resistant replacement materials (alloy 690/152/52/52M). Complicating this issue has been a known susceptibility to cracking during welding [1-7] of these weld metals. There is a critical need for an improved understanding of the weld metal metallurgy and defect formation in Ni-base alloy welds to effectively assess long-term performance. A series of macroscopic to microscopic examinations were performed on available mockup welds made with alloy 52 or alloy 152 plus selected overlay and inlay mockups. The intent was to expand our understanding of weld metal structures in simulated LWR service components with a focus on as-welded defects. Microstructural features, defect distributions, defect characteristics and weld residual strains were examined by optical metallography, scanning electron microscopy, electron backscatter diffraction and transmission electron microscopy. Industry-supplied mock-up welds were characterized including alloy 52 and 152 weldments, alloy 52M overlay and inlay welds, and an alloy 52 overlay. II. WELDMENTS II.A. Alloy 52 and 152 Weld Mockups The alloy 52 and 152 weld mockups were fabricated by MHI for the Kewaunee reactor and were obtained from the EPRI NDE Center. The mockups were U-groove welds joining two plates of 304SS as shown in Figure 1. Alloy 152 butter (heat 307380) was placed on the U-groove surface for both mockups by shielded metal arc welding (SMAW). For the alloy 152 weld mockup, the alloy 152 fill (heat 307380) was also applied using SMAW while for the alloy 52 weld mockup, the alloy 52 fill (heat NX2686JK) was applied using gas tungsten arc welding (GTAW). Welding parameters for the fill materials were substantially different with the alloy 152 SMAW having a deposition speed of 4-25 cm/min with a current of 95-145 A and the alloy 52 GTAW having a deposition speed of 4-10 cm/min with a current of 150-300 A. One prominent feature in these mockup welds is the presence of a crack starting at the 304SS butt joint at the bottom of the U-groove and extending up into the weld. It appears that the 304SS plate on either side of the butt joint acted as an anchor for the weld resulting in a stress rise across the slit that drove crack formation and extension up into the fill weld. As will be shown in the next section, the extent of the cracking around this stress riser was much greater in the MHI 52 weld mockup.« less

Correlation between Macular Thickness and Visual Field in Early Open Angle Glaucoma: A Cross-Sectional Study.

PubMed

Fallahi Motlagh, Behzad; Sadeghi, Ali

2017-01-01

The aim of this study was to correlate macular thickness and visual field parameters in early glaucoma. A total of 104 eyes affected with early glaucoma were examined in a cross-sectional, prospective study. Visual field testing using both standard automated perimetry (SAP) and shortwave automated perimetry (SWAP) was performed. Global visual field parameters, including mean deviation (MD) and pattern standard deviation (PSD), were recorded and correlated with spectral domain optical coherence tomography (SD-OCT)-measured macular thickness and asymmetry. Average macular thickness correlated significantly with all measures of visual field including MD-SWAP (r = 0.42), MD-SAP (r = 0.41), PSD-SWAP (r = -0.23), and PSD-SAP (r = -0.21), with P-values <0.001 for all correlations. The mean MD scores (using both SWAP and SAP) were significantly higher in the eyes with thin than in those with intermediate average macular thickness. Intraeye (superior macula thickness - inferior macula thickness) asymmetries correlated significantly with both PSD-SWAP (r = 0.63, P < 0.001) and PSD-SAP (r = 0.26, P = 0.01) scores. This study revealed a significant correlation between macular thickness and visual field parameters in early glaucoma. The results of this study should make macular thickness measurements even more meaningful to glaucoma specialists.

An improved diffusion welding technique for TD-NiCr

NASA Technical Reports Server (NTRS)

Holko, K. H.

1973-01-01

An improved diffusion welding technique has been developed for TD-NiCr sheet. In the most preferred form, the improved technique consists of diffusion welding 320-grit sanded plus chemically polished surfaces of unrecrystallized TD-NiCr at 760 C under 140 MN/m2 pressure for 1hr followed by postheating at 1180 C for 2hr. Compared to previous work, this improved technique has the advantages of shorter welding time, lower welding temperature, lower welding pressure, and a simpler and more reproducible surface preparation procedure. Weldments were made that had parent-metal creep-rupture shear strength at 1100 C.

Extended electrode technique. [gas metal arc welding of metal plates

NASA Technical Reports Server (NTRS)

Schaper, V. D.; Pollack, A.

1972-01-01

The extended electrode technique is a unique welding process which utilizes manual gas-metal-arc (GMAW) semi-automatic equipment and close, square butt joints to effectively produce a weld. The technique takes advantage of the resistance heating of the electode extension to effect the root pass. Weldments as large as 72-X30-X2-inch have been fabricated with this technique under normal shipyard welding conditions. Mechanical properties and explosion bulge tests indicate that satisfactory results are obtained with this process. Potential savings of approximately 50 percent can be achieved in flat welding and repair of heavy structural steel members.

Inertial Weldment of Rhenium and Inconel 718

NASA Technical Reports Server (NTRS)

Cavender, D. P.; Courtright, Z. S.; Hostetter, G.; Laiman, M.

2018-01-01

Inertia welding has been found to be a successful method for joining pure rhenium to Inconel 718, and with additional experimentation, this process may have great potential for rocket nozzle applications. Refractory metals are ideally suited to this application, where high temperatures and oxidizing environment survivability is required, but not all of the thruster must be made of these materials, only the areas that require them. A bolted joint between the two metals is not ideal, especially for small thrusters where the mess of a bolted join will come at a steep price. A welded joint would be preferred for flight thrusters.

Fractography of modern engineering materials: composites and metals

DOE Office of Scientific and Technical Information (OSTI.GOV)

Masters, J.E.; Au, J.J.

1987-01-01

The fractographic analysis of fracture surfaces in composites and metals is discussed in reviews and reports of recent theoretical and experimental investigations. Topics addressed include fracture-surface micromorphology in engineering solids, SEM fractography of pure and mixed-mode interlaminar fractures in graphite/epoxy composites, determination of crack propagation directions in graphite/epoxy structures, and the fracture surfaces of irradiated composites. Consideration is given to fractographic feature identification and characterization by digital imaging analysis, fractography of pressure-vessel steel weldments, the micromechanisms of major/minor cycle fatigue crack growth in Inconel 718, and fractographic analysis of hydrogen-assisted cracking in alpha-beta Ti alloys.

Investigation on microstructure and mechanical properties on pulsed current gas tungsten arc welded super alloy 617

NASA Astrophysics Data System (ADS)

Mageshkumar, K.; Kuppan, P.; Arivazhagan, N.

2017-11-01

The present research work investigates the metallurgical and mechanical properties of weld joint fabricated by alloy 617 by pulsed current gas tungsten arc welding (PCGTAW) technique. Welding was done by ERNiCrCoMo-1 filler wire. Optical and Scanning Electron Microscope (SEM) revealed the fine equiaxed dendritic in the fusion zone. Electron Dispersive Spectroscopy (EDS) demonstrates the presence of Mo-rich secondary phases in the grain boundary regions. Tensile test shows improved mechanical properties compared to the continuous current mode. Bend test didn’t indicate the presence of defects in the weldments.

Optimized postweld heat treatment procedures for 17-4 PH stainless steels

DOE Office of Scientific and Technical Information (OSTI.GOV)

Bhaduri, A.K.; Sujith, S.; Srinivasan, G.

1995-05-01

The postweld heat treatment (PWHT) procedures for 17-4 PH stainless steel weldments of matching chemistry was optimized vis-a-vis its microstructure prior to welding based on microstructural studies and room-temperature mechanical properties. The 17-4 PH stainless steel was welded in two different prior microstructural conditions (condition A and condition H 1150) and then postweld heat treated to condition H900 or condition H1150, using different heat treatment procedures. Microstructural investigations and room-temperature tensile properties were determined to study the combined effects of prior microstructural and PWHT procedures.

The aerodynamic properties of thick aerofoils suitable for internal bracing

NASA Technical Reports Server (NTRS)

Norton, F H

1920-01-01

The object of this investigation was to determine the characteristics of various types of wings having sufficient depth to entirely inclose the wing bracing, and also to provide data for the further design of such sections. This type of wing is of interest because it eliminates the resistance of the interplane bracing, a portion of the airplane that sometimes absorbs one-quarter of the total power required to fly, and because these wings may be made to give a very high maximum lift. Results of the investigation of the following subjects are given: (1) effect of changing the upper and lower camber of thick aerofoils of uniform section; (2) effect of thickening the center and thinning the tips of a thin aerofoil; (3) effect of adding a convex lower surface to a tapered section; (4) effect of changing the mean thickness with constant center and tip sections; and (5) effect of varying the chord along the span.

Nearshore sediment thickness, Fire Island, New York

USGS Publications Warehouse

Locker, Stanley D.; Miselis, Jennifer L.; Buster, Noreen A.; Hapke, Cheryl J.; Wadman, Heidi M.; McNinch, Jesse E.; Forde, Arnell S.; Stalk, Chelsea A.

2017-04-03

Investigations of coastal change at Fire Island, New York (N.Y.), sought to characterize sediment budgets and determine geologic framework controls on coastal processes. Nearshore sediment thickness is critical for assessing coastal system sediment availability, but it is largely unquantified due to the difficulty of conducting geological or geophysical surveys across the nearshore. This study used an amphibious vessel to acquire chirp subbottom profiles. These profiles were used to characterize nearshore geology and provide an assessment of nearshore sediment volume. Two resulting sediment-thickness maps are provided: total Holocene sediment thickness and the thickness of the active shoreface. The Holocene sediment section represents deposition above the maximum flooding surface that is related to the most recent marine transgression. The active shoreface section is the uppermost Holocene sediment, which is interpreted to represent the portion of the shoreface thought to contribute to present and future coastal behavior. The sediment distribution patterns correspond to previously defined zones of erosion, accretion, and stability along the island, demonstrating the importance of sediment availability in the coastal response to storms and seasonal variability. The eastern zone has a thin nearshore sediment thickness, except for an ebb-tidal deposit at the wilderness breach caused by Hurricane Sandy. Thicker sediment is found along a central zone that includes shoreface-attached sand ridges, which is consistent with a stable or accretional coastline in this area. The thickest overall Holocene section is found in the western zone of the study, where a thicker lower section of Holocene sediment appears related to the westward migration of Fire Island Inlet over several hundred years.

Summary Report on the High-Speed Characteristics of Six Model Wings Having NACA 65sub1-Series Sections

NASA Technical Reports Server (NTRS)

Hamilton, William T; Nelson, Warren H

1947-01-01

A summary of the results of wind-tunnel tests to determine the high-speed aerodynamic characteristics of six model wings having NACA 65sub1-series sections is presented in this report. The 8-percent-thick wings were superior to the 10-percent and 12-percent-thick wings from the standpoint of power economy during level flight for Mach numbers above 0.76. However, airplanes that are to fly at Mach numbers below 0.76 will gain aerodynamically if the percentage thickness of the wing and the aspect ratio are both increased. The lift-curve slopes for the 8-percent-thick wings at 0.85 Mach number were roughly twice their low-speed values.

14 CFR 23.1191 - Firewalls.

Code of Federal Regulations, 2010 CFR

2010-01-01

... corrosion. (f) Compliance with the criteria for fireproof materials or components must be shown as follows... this section: (1) Stainless steel sheet, 0.015 inch thick. (2) Mild steel sheet (coated with aluminum or otherwise protected against corrosion) 0.018 inch thick. (3) Terne plate, 0.018 inch thick. (4...

Microstructure and Mechanical Properties of Narrow Gap Laser-Arc Hybrid Welded 40 mm Thick Mild Steel.

PubMed

Zhang, Chen; Li, Geng; Gao, Ming; Zeng, XiaoYan

2017-01-26

Both laser-arc hybrid welding and narrow gap welding have potential for the fabrication of thick sections, but their combination has been seldom studied. In this research, 40 mm thick mild steel was welded by narrow gap laser-arc hybrid welding. A weld with smooth layer transition, free of visible defects, was obtained by nine passes at a 6 mm width narrow gap. The lower part of the weld has the lowest mechanical properties because of the lowest amount of acicular ferrite, but its ultimate tensile strength and impact absorbing energy is still 49% and 60% higher than those of base metal, respectively. The microhardness deviation of all filler layers along weld thickness direction is no more than 15 HV 0.2 , indicating that no temper softening appeared during multiple heat cycles. The results provide an alternative technique for improving the efficiency and quality of welding thick sections.

Microstructure and Mechanical Properties of Narrow Gap Laser-Arc Hybrid Welded 40 mm Thick Mild Steel

PubMed Central

Zhang, Chen; Li, Geng; Gao, Ming; Zeng, XiaoYan

2017-01-01

Both laser-arc hybrid welding and narrow gap welding have potential for the fabrication of thick sections, but their combination has been seldom studied. In this research, 40 mm thick mild steel was welded by narrow gap laser-arc hybrid welding. A weld with smooth layer transition, free of visible defects, was obtained by nine passes at a 6 mm width narrow gap. The lower part of the weld has the lowest mechanical properties because of the lowest amount of acicular ferrite, but its ultimate tensile strength and impact absorbing energy is still 49% and 60% higher than those of base metal, respectively. The microhardness deviation of all filler layers along weld thickness direction is no more than 15 HV0.2, indicating that no temper softening appeared during multiple heat cycles. The results provide an alternative technique for improving the efficiency and quality of welding thick sections. PMID:28772469

Compression testing of thick-section composite materials

NASA Astrophysics Data System (ADS)

Camponeschi, Eugene T., Jr.

A compression test fixture suitable for testing of composites up to 1 inch in thickness has been developed with a view to the characterization of the effects of constituents, fiber orientation, and thickness, on the compressive response of composites for naval applications. The in-plane moduli, compression strength, failure mechanisms, and both in-plane and through-thickness Poisson's ratios are shown to be independent of material thickness. The predominant failure mechanisms for both materials, namely kink bands and delaminations, are identical to those reported for composite one-tenth the thickness of those presently tested.

Transmission of Gamma Rays Through Large Thickness of Heavy Materials

DTIC Science & Technology

1950-06-09

succession ot thick- nesaes of material. In this way a rather complete history of the attenuated beam is obtained. The formulation in Section II gives the...vi e -e yfv •-v) ’ q I The quantitiee v and v in this expression are the v 0 and v1 respectively of Section II. It follows that the number of

Model-based cartilage thickness measurement in the submillimeter range

DOE Office of Scientific and Technical Information (OSTI.GOV)

Streekstra, G. J.; Strackee, S. D.; Maas, M.

2007-09-15

Current methods of image-based thickness measurement in thin sheet structures utilize second derivative zero crossings to locate the layer boundaries. It is generally acknowledged that the nonzero width of the point spread function (PSF) limits the accuracy of this measurement procedure. We propose a model-based method that strongly reduces PSF-induced bias by incorporating the PSF into the thickness estimation method. We estimated the bias in thickness measurements in simulated thin sheet images as obtained from second derivative zero crossings. To gain insight into the range of sheet thickness where our method is expected to yield improved results, sheet thickness wasmore » varied between 0.15 and 1.2 mm with an assumed PSF as present in the high-resolution modes of current computed tomography (CT) scanners [full width at half maximum (FWHM) 0.5-0.8 mm]. Our model-based method was evaluated in practice by measuring layer thickness from CT images of a phantom mimicking two parallel cartilage layers in an arthrography procedure. CT arthrography images of cadaver wrists were also evaluated, and thickness estimates were compared to those obtained from high-resolution anatomical sections that served as a reference. The thickness estimates from the simulated images reveal that the method based on second derivative zero crossings shows considerable bias for layers in the submillimeter range. This bias is negligible for sheet thickness larger than 1 mm, where the size of the sheet is more than twice the FWHM of the PSF but can be as large as 0.2 mm for a 0.5 mm sheet. The results of the phantom experiments show that the bias is effectively reduced by our method. The deviations from the true thickness, due to random fluctuations induced by quantum noise in the CT images, are of the order of 3% for a standard wrist imaging protocol. In the wrist the submillimeter thickness estimates from the CT arthrography images correspond within 10% to those estimated from the anatomical sections. We present a method that yields virtually unbiased thickness estimates of cartilage layers in the submillimeter range. The good agreement of thickness estimates from CT images with estimates from anatomical sections is promising for clinical application of the method in cartilage integrity staging of the wrist and the ankle.« less

Leveraging Clinical Imaging Archives for Radiomics: Reliability of Automated Methods for Brain Volume Measurement.

PubMed

Adduru, Viraj R; Michael, Andrew M; Helguera, Maria; Baum, Stefi A; Moore, Gregory J

2017-09-01

Purpose To validate the use of thick-section clinically acquired magnetic resonance (MR) imaging data for estimating total brain volume (TBV), gray matter (GM) volume (GMV), and white matter (WM) volume (WMV) by using three widely used automated toolboxes: SPM ( www.fil.ion.ucl.ac.uk/spm/ ), FreeSurfer ( surfer.nmr.mgh.harvard.edu ), and FSL (FMRIB software library; Oxford Centre for Functional MR Imaging of the Brain, Oxford, England, https://fsl.fmrib.ox.ac.uk/fsl ). Materials and Methods MR images from a clinical archive were used and data were deidentified. The three methods were applied to estimate brain volumes from thin-section research-quality brain MR images and routine thick-section clinical MR images acquired from the same 38 patients (age range, 1-71 years; mean age, 22 years; 11 women). By using these automated methods, TBV, GMV, and WMV were estimated. Thin- versus thick-section volume comparisons were made for each method by using intraclass correlation coefficients (ICCs). Results SPM exhibited excellent ICCs (0.97, 0.85, and 0.83 for TBV, GMV, and WMV, respectively). FSL exhibited ICCs of 0.69, 0.51, and 0.60 for TBV, GMV, and WMV, respectively, but they were lower than with SPM. FreeSurfer exhibited excellent ICC of 0.63 only for TBV. Application of SPM's voxel-based morphometry on the modulated images of thin-section images and interpolated thick-section images showed fair to excellent ICCs (0.37-0.98) for the majority of brain regions (88.47% [306924 of 346916 voxels] of WM and 80.35% [377 282 of 469 502 voxels] of GM). Conclusion Thick-section clinical-quality MR images can be reliably used for computing quantitative brain metrics such as TBV, GMV, and WMV by using SPM. © RSNA, 2017 Online supplemental material is available for this article.

Final Report: Characterization of Canister Mockup Weld Residual Stresses

DOE Office of Scientific and Technical Information (OSTI.GOV)

Enos, David; Bryan, Charles R.

2016-12-01

Stress corrosion cracking (SCC) of interim storage containers has been indicated as a high priority data gap by the Department of Energy (DOE) (Hanson et al., 2012), the Electric Power Research Institute (EPRI, 2011), the Nuclear Waste Technical Review Board (NWTRB, 2010a), and the Nuclear Regulatory Commission (NRC, 2012a, 2012b). Uncertainties exist in terms of the environmental conditions that prevail on the surface of the storage containers, the stress state within the container walls associated both with weldments as well as within the base metal itself, and the electrochemical properties of the storage containers themselves. The goal of the workmore » described in this document is to determine the stress states that exists at various locations within a typical storage canister by evaluating the properties of a full-diameter cylindrical mockup of an interim storage canister. This mockup has been produced using the same manufacturing procedures as the majority of the fielded spent nuclear fuel interim storage canisters. This document describes the design and procurement of the mockup and the characterization of the stress state associated with various portions of the container. It also describes the cutting of the mockup into sections for further analyses, and a discussion of the potential impact of the results from the stress characterization effort.« less

A model for heat and mass input control in GMAW

DOE Office of Scientific and Technical Information (OSTI.GOV)

Smartt, H.B.; Einerson, C.J.

1993-05-01

This work describes derivation of a control model for electrode melting and heat and mass transfer from the electrode to the work piece in gas metal arc welding (GMAW). Specifically, a model is developed which allows electrode speed and welding speed to be calculated for given values of voltage and torch-to-base metal distance, as a function of the desired heat and mass input to the weldment. Heat input is given on a per unit weld length basis, and mass input is given in terms of transverse cross-sectional area added to the weld bead (termed reinforcement). The relationship to prior workmore » is discussed. The model was demonstrated using a computer-controlled welding machine and a proportional-integral (PI) controller receiving input from a digital filter. The difference between model-calculated welding current and measured current is used as controller feedback. The model is calibrated for use with carbon steel welding wire and base plate with Ar-CO[sub 2] shielding gas. Although the system is intended for application during spray transfer of molten metal from the electrode to the weld pool, satisfactory performance is also achieved during globular and streaming transfer. Data are presented showing steady-state and transient performance, as well as resistance to external disturbances.« less

Characterization of Al-Cu-Li Alloy 2090 Near Net Shape Extrusion

NASA Technical Reports Server (NTRS)

Birt, M. J.; Domack, M. S.; Hafley, R. A.; Pollock, W. D.

1998-01-01

Aluminum-lithium (Al-Li) alloys near net shape extrusions are being evaluated for potential application in launch vehicle structures. The objective of this study was to determine tensile and fracture properties, corrosion resistance, and weldability of integrally stiffened panels of Al-Cu-Li alloy 2090 in the T8 temper. The microstructure was pre-dominantly unrecrystallized. Texture analyses revealed the presence of fiber components in the stiffeners and a combination of fiber and rolling components in the skin. Variations in grain morphology and texture through the extruded cross section were correlated with the tensile, fracture, and corrosion behavior. Tensile strengths at room and cryogenic temperatures of the 2090 extrusions were similar to other 2090 product forms and were higher than 2219-T87, the primary structural material in the Space Shuttle external tank; however, ductilities were lower. The fracture resistance of the 2090 extrusion was lower than 2219-T87 plate at room temperature. At cryogenic temperatures, tensile ductility and fracture behavior of the 2090 extrusion were similar to other 2090 product forms but were lower than 2219-T87 plate. The exfoliation and stress corrosion resistance of the 2090 extrusion compared favorably with the characteristics of other 2090 product forms. The weldability and weldment properties of the extrusions were similar to 2090 and 2219 plates.

Extraction efficiency and implications for absolute quantitation of propranolol in mouse brain, liver and kidney thin tissue sections using droplet-based liquid microjunction surface sampling-HPLC ESI-MS/MS

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kertesz, Vilmos; Weiskittel, Taylor M.; Vavek, Marissa

Currently, absolute quantitation aspects of droplet-based surface sampling for thin tissue analysis using a fully automated autosampler/HPLC-ESI-MS/MS system are not fully evaluated. Knowledge of extraction efficiency and its reproducibility is required to judge the potential of the method for absolute quantitation of analytes from thin tissue sections. Methods: Adjacent thin tissue sections of propranolol dosed mouse brain (10- μm-thick), kidney (10- μm-thick) and liver (8-, 10-, 16- and 24- μm-thick) were obtained. Absolute concentration of propranolol was determined in tissue punches from serial sections using standard bulk tissue extraction protocols and subsequent HPLC separations and tandem mass spectrometric analysis. Thesemore » values were used to determine propranolol extraction efficiency from the tissues with the droplet-based surface sampling approach. Results: Extraction efficiency of propranolol using 10- μm-thick brain, kidney and liver thin tissues using droplet-based surface sampling varied between ~45-63%. Extraction efficiency decreased from ~65% to ~36% with liver thickness increasing from 8 μm to 24 μm. Randomly selecting half of the samples as standards, precision and accuracy of propranolol concentrations obtained for the other half of samples as quality control metrics were determined. Resulting precision ( ±15%) and accuracy ( ±3%) values, respectively, were within acceptable limits. In conclusion, comparative quantitation of adjacent mouse thin tissue sections of different organs and of various thicknesses by droplet-based surface sampling and by bulk extraction of tissue punches showed that extraction efficiency was incomplete using the former method, and that it depended on the organ and tissue thickness. However, once extraction efficiency was determined and applied, the droplet-based approach provided the required quantitation accuracy and precision for assay validations. Furthermore, this means that once the extraction efficiency was calibrated for a given tissue type and drug, the droplet-based approach provides a non-labor intensive and high-throughput means to acquire spatially resolved quantitative analysis of multiple samples of the same type.« less

Extraction efficiency and implications for absolute quantitation of propranolol in mouse brain, liver and kidney thin tissue sections using droplet-based liquid microjunction surface sampling-HPLC ESI-MS/MS

DOE PAGES

Kertesz, Vilmos; Weiskittel, Taylor M.; Vavek, Marissa; ...

2016-06-22

Currently, absolute quantitation aspects of droplet-based surface sampling for thin tissue analysis using a fully automated autosampler/HPLC-ESI-MS/MS system are not fully evaluated. Knowledge of extraction efficiency and its reproducibility is required to judge the potential of the method for absolute quantitation of analytes from thin tissue sections. Methods: Adjacent thin tissue sections of propranolol dosed mouse brain (10- μm-thick), kidney (10- μm-thick) and liver (8-, 10-, 16- and 24- μm-thick) were obtained. Absolute concentration of propranolol was determined in tissue punches from serial sections using standard bulk tissue extraction protocols and subsequent HPLC separations and tandem mass spectrometric analysis. Thesemore » values were used to determine propranolol extraction efficiency from the tissues with the droplet-based surface sampling approach. Results: Extraction efficiency of propranolol using 10- μm-thick brain, kidney and liver thin tissues using droplet-based surface sampling varied between ~45-63%. Extraction efficiency decreased from ~65% to ~36% with liver thickness increasing from 8 μm to 24 μm. Randomly selecting half of the samples as standards, precision and accuracy of propranolol concentrations obtained for the other half of samples as quality control metrics were determined. Resulting precision ( ±15%) and accuracy ( ±3%) values, respectively, were within acceptable limits. In conclusion, comparative quantitation of adjacent mouse thin tissue sections of different organs and of various thicknesses by droplet-based surface sampling and by bulk extraction of tissue punches showed that extraction efficiency was incomplete using the former method, and that it depended on the organ and tissue thickness. However, once extraction efficiency was determined and applied, the droplet-based approach provided the required quantitation accuracy and precision for assay validations. Furthermore, this means that once the extraction efficiency was calibrated for a given tissue type and drug, the droplet-based approach provides a non-labor intensive and high-throughput means to acquire spatially resolved quantitative analysis of multiple samples of the same type.« less

Microstructural and mechanical characterization of CO{sub 2} laser and gas tungsten arc welds of an Al-Li-Cu alloy 2195

DOE Office of Scientific and Technical Information (OSTI.GOV)

Hou, K.H.; Baeslack, W.A. III; Szabo, A.

1994-12-31

Lithium-containing aluminum alloys offer an attractive combination of low density and high strength and stiffness and have been the focus of vigorous research for their promising aerospace applications. To achieve the full potential advantages in using these alloys, the integrity of welded joints, both n the fusion zone and the heat-affected zone, must be ensured. In the present study, Weldalite{sup TM} 049 (designated as alloy 2195) with nominal composition of Al-1.0Li-4.0Cu-0.4Mg0.4Ag-0.14Zr (wt%) was welded autogenously using the gas tungsten-arc (GTA) and CO{sub 2} laser beam (LB) welding processes. The average ultimate tensile strengths for as-welded, 160{degrees}C/16 h-aged, and 190{degrees}C/16 h-agedmore » GTA welds were 296.4 MPa, 304.6 MPa, and 336.8 MPa, and corresponded to joint efficiencies of 61.4%, 48.1% and 56.0%, respectively. Porosity was found occasionally in the laser welds and slightly affected the performance of the aluminum weldments. For laser welds, average ultimate tensile strengths and corresponding joint efficiencies for a-welded, 160{degrees}C/16 h-aged, and 190{degrees}C/16 h-aged weldments were 293.2 MPa (60.8%) 305.9 MPa (48.3%), and 331.0 MPa (55.0%), respectively. Scanning electron fractography revealed that failure of the GTA and LB tensile specimens occurred either within the weld metal or along the fusion boundary. The latter was related to the existence of an equiaxed band along the fusion boundary.« less

Creep Strength of Nb-1Zr for SP-100 Applications

NASA Astrophysics Data System (ADS)

Horak, James A.; Egner, Larry K.

1994-07-01

Power systems that are used to provide electrical power in space are designed to optimize conversion of thermal energy to electrical energy and to minimize the mass and volume that must be launched. Only refractory metals and their alloys have sufficient long-term strength for several years of uninterrupted operation at the required temperatures of 1200 K and above. The high power densities and temperatures at which these reactors must operate require the use of liquid-metal coolants. The alloy Nb-1 wt % Zr (Nb-lZr), which exhibits excellent corrosion resistance to alkali liquid-metals at high temperatures, is being considered for the fuel cladding, reactor structural, and heat-transport systems for the SP-100 reactor system. Useful lifetime of this system is limited by creep deformation in the reactor core. Nb-lZr sheet procured to American Society for Testing and Materials (ASTM) specifications for reactor grade and commercial grade has been processed by several different cold work and annealing treatments to attempt to produce the grain structure (size, shape, and distribution of sizes) that provides the maximum creep strength of this alloy at temperatures from 1250 to 1450 K. The effects of grain size, differences in oxygen concentrations, tungsten concentrations, and electron beam and gas tungsten arc weldments on creep strength were studied. Grain size has a large effect on creep strength at 1450 K but only material with a very large grain size (150 μm) exhibits significantly higher creep strength at 1350 K. Differences in oxygen or tungsten concentrations did not affect creep strength, and the creep strengths of weldments were equal to, or greater than, those for base metal.

Effect of long-term aging on microstructure and local behavior in the heat-affected zone of a Ni–Cr–Mo–V steel welded joint

DOE Office of Scientific and Technical Information (OSTI.GOV)

Zhu, Ming-Liang, E-mail: mlzhu@ecust.edu.cn; Wang, De-Qiang; Xuan, Fu-Zhen

2014-01-15

Evolution of microstructure, micro-hardness and micro-tensile strength behavior was investigated in the heat-affected zone of a Ni–Cr–Mo–V steel welded joint after the artificial aging at 350 °C for 3000 h. After detailed characterization of microstructures in optical microscopy, scanning electron microscopy and transmission electron microscopy, it is revealed that the change of martensite–bainite constituent promotes more homogeneous microstructure distribution. The aging treatment facilitates redistribution of carbon and chromium elements along the welded joint, and the micro-hardness is increased slightly through the welds due to enrichment of carbon. The types of precipitates in the weldment mainly include M{sub 3}C, MC, M{submore » 2}C and M{sub 23}C{sub 6}. The carbides in base metal, weld metal and coarse-grained heat-affected zone are prone to change from ellipsoidal to platelet form whereas more uniform spherical carbides are observed in the fine-grained zone. Precipitation and coarsening of M{sub 23}C{sub 6} near the fusion line, and formation of MC and M{sub 2}C, are responsible for the tensile strength decrease and its smooth distribution in the aged heat-affected zone. This implies that the thermal aging can relieve strength mismatch in the weldments. - Highlights: • Microstructure homogeneity improved in HAZ after long-term aging. • Tensile strength decreased in HAZ due to precipitation and coarsening of M{sub 23}C{sub 6}. • Strength mismatch in NiCrMoV steel welds was relieved after aging at 350 °C × 3000 h.« less

Preparation of high-quality ultrathin transmission electron microscopy specimens of a nanocrystalline metallic powder.

PubMed

Riedl, Thomas; Gemming, Thomas; Mickel, Christine; Eymann, Konrad; Kirchner, Alexander; Kieback, Bernd

2012-06-01

This article explores the achievable transmission electron microscopy specimen thickness and quality by using three different preparation methods in the case of a high-strength nanocrystalline Cu-Nb powder alloy. Low specimen thickness is essential for spatially resolved analyses of the grains in nanocrystalline materials. We have found that single-sided as well as double-sided low-angle Ar ion milling of the Cu-Nb powders embedded into epoxy resin produced wedge-shaped particles of very low thickness (<10 nm) near the edge. By means of a modified focused ion beam lift-out technique generating holes in the lamella interior large micrometer-sized electron-transparent regions were obtained. However, this lamella displayed a higher thickness at the rim of ≥30 nm. Limiting factors for the observed thicknesses are discussed including ion damage depths, backscattering, and surface roughness, which depend on ion type, energy, current density, and specimen motion. Finally, sections cut by ultramicrotomy at low stroke rate and low set thickness offered vast, several tens of square micrometers uniformly thin regions of ∼10-nm minimum thickness. As major drawbacks, we have detected a thin coating on the sections consisting of epoxy deployed as the embedding material and considerable nanoscale thickness variations. Copyright © 2011 Wiley Periodicals, Inc.

Ballistic-Failure Mechanisms in Gas Metal Arc Welds of Mil A46100 Armor-Grade Steel: A Computational Investigation

NASA Astrophysics Data System (ADS)

Grujicic, M.; Snipes, J. S.; Galgalikar, R.; Ramaswami, S.; Yavari, R.; Yen, C.-F.; Cheeseman, B. A.

2014-09-01

In our recent work, a multi-physics computational model for the conventional gas metal arc welding (GMAW) joining process was introduced. The model is of a modular type and comprises five modules, each designed to handle a specific aspect of the GMAW process, i.e.: (i) electro-dynamics of the welding-gun; (ii) radiation-/convection-controlled heat transfer from the electric-arc to the workpiece and mass transfer from the filler-metal consumable electrode to the weld; (iii) prediction of the temporal evolution and the spatial distribution of thermal and mechanical fields within the weld region during the GMAW joining process; (iv) the resulting temporal evolution and spatial distribution of the material microstructure throughout the weld region; and (v) spatial distribution of the as-welded material mechanical properties. In the present work, the GMAW process model has been upgraded with respect to its predictive capabilities regarding the spatial distribution of the mechanical properties controlling the ballistic-limit (i.e., penetration-resistance) of the weld. The model is upgraded through the introduction of the sixth module in the present work in recognition of the fact that in thick steel GMAW weldments, the overall ballistic performance of the armor may become controlled by the (often inferior) ballistic limits of its weld (fusion and heat-affected) zones. To demonstrate the utility of the upgraded GMAW process model, it is next applied to the case of butt-welding of a prototypical high-hardness armor-grade martensitic steel, MIL A46100. The model predictions concerning the spatial distribution of the material microstructure and ballistic-limit-controlling mechanical properties within the MIL A46100 butt-weld are found to be consistent with prior observations and general expectations.

Effect of Repair Welding on Electrochemical Corrosion and Stress Corrosion Cracking Behavior of TIG Welded AA2219 Aluminum Alloy in 3.5 Wt Pct NaCl Solution

NASA Astrophysics Data System (ADS)

Venugopal, A.; Sreekumar, K.; Raja, V. S.

2010-12-01

The stress corrosion cracking (SCC) behavior of AA2219 aluminum alloy in the as-welded (AW) and repair-welded (RW) conditions was examined and compared with that of the base metal (BM) in 3.5 wt pct NaCl solution using the slow strain rate technique (SSRT). The reduction in ductility was used as a parameter to evaluate the SCC susceptibility of both BM and welded joints. The results show that the ductility ratio ( ɛ NaCl/( ɛ air)) of the BM was close to one (0.97) and reduced to 0.9 for the AW joint. This value further reduced to 0.77 after carrying out one repair welding operation. However, the RW specimen exhibited higher ductility than the single-weld specimens even in 3.5 wt pct NaCl solution. SSRT results obtained using pre-exposed samples followed by post-test metallographic observations clearly showed localized pitting corrosion along the partially melted zone (PMZ), signifying that the reduction in ductility ratio of both the AW and RW joints was more due to mechanical overload failure, caused by the localized corrosion and a consequent reduction in specimen thickness, than due to SCC. Also, the RW joint exhibited higher ductility than the AW joint both in air and the environment, although SCC index (SI) for the former is lower than that of the latter. Fractographic examination of the failed samples, in general, revealed a typical ductile cracking morphology for all the base and welded joints, indicating the good environmental cracking resistance of this alloy. Microstructural examination and polarization tests further demonstrate grain boundary melting along the PMZ, and that provided the necessary electrochemical condition for the preferential cracking on that zone of the weldment.

Rehabilitative ultrasound imaging of the supraspinatus muscle: Intra- and interrater reliability of thickness and cross-sectional area.

PubMed

Schneebeli, Alessandro; Egloff, Michele; Giampietro, Amelia; Clijsen, Ron; Barbero, Marco

2014-04-01

To examine intra- and interrater reliability of thickness and cross-sectional area (CSA) measurements of the supraspinatus muscle using rehabilitative ultrasound imaging (RUSI). Two physical therapists acquired b-mode images of the supraspinatus muscles in twenty-five healthy subjects. Thickness and CSA were measured. Intra- and interrater reliability were examined. Intrarater reliability for thickness was high, (ICC1.1 0.91) for rater 1 and (ICC1.1 0.92) for rater 2. Intrarater reliability for CSA was also high, (ICC1.1 0.90) for rater 1 and (ICC1.1 0.85) for rater 2. Interrater reliability for the thickness was high, (ICC3.1 0.86). For CSA, interrater reliability was moderate, (ICC3.1 0.70). Supraspinatus muscle thickness and CSA can be reliably measured by physical therapists in healthy subjects. These findings confirm that RUSI has an interesting potential for physiotherapy clinical practice, especially to assess morphometric changes in skeletal muscles. Further research is needed in subjects with shoulder disorders. Copyright © 2013 Elsevier Ltd. All rights reserved.

High resolution ultrasonography of the tibial nerve in diabetic peripheral neuropathy.

PubMed

Singh, Kunwarpal; Gupta, Kamlesh; Kaur, Sukhdeep

2017-12-01

High-resolution ultrasonography of the tibial nerve is a fast and non invasive tool for diagnosis of diabetic peripheral neuropathy. Our study was aimed at finding out the correlation of the cross sectional area and maximum thickness of nerve fascicles of the tibial nerve with the presence and severity of diabetic peripheral neuropathy. 75 patients with type 2 diabetes mellitus clinically diagnosed with diabetic peripheral neuropathy were analysed, and the severity of neuropathy was determined using the Toronto Clinical Neuropathy Score. 58 diabetic patients with no clinical suspicion of diabetic peripheral neuropathy and 75 healthy non-diabetic subjects were taken as controls. The cross sectional area and maximum thickness of nerve fascicles of the tibial nerves were calculated 3 cm cranial to the medial malleolus in both lower limbs. The mean cross sectional area (22.63 +/- 2.66 mm 2 ) and maximum thickness of nerve fascicles (0.70 mm) of the tibial nerves in patients with diabetic peripheral neuropathy compared with both control groups was significantly larger, and statistically significant correlation was found with the Toronto Clinical Neuropathy Score ( p < 0.001). The diabetic patients with no signs of peripheral neuropathy had a larger mean cross sectional area (14.40 +/- 1.72 mm 2 ) and maximum thickness of nerve fascicles of the tibial nerve (0.40 mm) than healthy non-diabetic subjects (12.42 +/- 1.01 mm 2 and 0.30 mm respectively). The cross sectional area and maximum thickness of nerve fascicles of the tibial nerve is larger in diabetic patients with or without peripheral neuropathy than in healthy control subjects, and ultrasonography can be used as a good screening tool in these patients.

Ultimate strength capacity of a square hollow section filled with fibrous foamed concrete

NASA Astrophysics Data System (ADS)

Amirah Azra Khairuddin, Siti; Rahman, Norashidah Abd; Jamaluddin, Norwati; Jaini, Zainorizuan Mohd; Ali, Noorwirdawati

2017-11-01

Concrete-filled sections used as building columns have become popular due to their architectural and structural elements. In recent years, there has been a renewed call for the improvement of materials used as concrete to fill the composite columns. Among these materials, foamed concrete has received great attention due to its structural characteristics and its potential as a construction material used in hollow sections. However, its behaviors as infill material in a hollow section, such as its strength and failure mode, should be investigated. In this study, experimental research was conducted to compare the experimental and theoretical values of its ultimate strength capacity. Eight specimens of hollow steel sections with two different thicknesses were filled with fibrous foamed concrete and then subjected to compression load. The obtained results were compared with those obtained from a hollow section with the same thicknesses, but were filled with normal foamed concrete. Results show that the ultimate strength capacity of the experimental value is the same as that of the theoretical value based on Eurocode 4. The largest percentage values between theoretical and experimental results for thicknesses of 2 and 4 mm are 58% and 55%, respectively.

Cross section of α-induced reactions on iridium isotopes obtained from thick target yield measurement for the astrophysical γ process

NASA Astrophysics Data System (ADS)

Szücs, T.; Kiss, G. G.; Gyürky, Gy.; Halász, Z.; Fülöp, Zs.; Rauscher, T.

2018-01-01

The stellar reaction rates of radiative α-capture reactions on heavy isotopes are of crucial importance for the γ process network calculations. These rates are usually derived from statistical model calculations, which need to be validated, but the experimental database is very scarce. This paper presents the results of α-induced reaction cross section measurements on iridium isotopes carried out at first close to the astrophysically relevant energy region. Thick target yields of 191Ir(α,γ)195Au, 191Ir(α,n)194Au, 193Ir(α,n)196mAu, 193Ir(α,n)196Au reactions have been measured with the activation technique between Eα = 13.4 MeV and 17 MeV. For the first time the thick target yield was determined with X-ray counting. This led to a previously unprecedented sensitivity. From the measured thick target yields, reaction cross sections are derived and compared with statistical model calculations. The recently suggested energy-dependent modification of the α + nucleus optical potential gives a good description of the experimental data.

Determination of the effective sample thickness via radiative capture

DOE PAGES

Hurst, A. M.; Summers, N. C.; Szentmiklosi, L.; ...

2015-09-14

Our procedure for determining the effective thickness of non-uniform irregular-shaped samples via radiative capture is described. In this technique, partial γ-ray production cross sections of a compound nucleus produced in a neutron-capture reaction are measured using Prompt Gamma Activation Analysis and compared to their corresponding standardized absolute values. For the low-energy transitions, the measured cross sections are lower than their standard values due to significant photoelectric absorption of the γ rays within the bulk-sample volume itself. Using standard theoretical techniques, the amount of γ-ray self absorption and neutron self shielding can then be calculated by iteratively varying the sample thicknessmore » until the observed cross sections converge with the known standards. The overall attenuation provides a measure of the effective sample thickness illuminated by the neutron beam. This procedure is illustrated through radiative neutron capture using powdered oxide samples comprising enriched 186W and 182W from which their tungsten-equivalent effective thicknesses are deduced to be 0.077(3) mm and 0.042(8) mm, respectively.« less

A framework for comparing structural and functional measures of glaucomatous damage

PubMed Central

Hood, Donald C.; Kardon, Randy H.

2007-01-01

While it is often said that structural damage due to glaucoma precedes functional damage, it is not always clear what this statement means. This review has two purposes: first, to show that a simple linear relationship describes the data relating a particular functional test (standard automated perimetry (SAP)) to a particular structural test (optical coherence tomography (OCT)); and, second, to propose a general framework for relating structural and functional damage, and for evaluating if one precedes the other. The specific functional and structural tests employed are described in Section 2. To compare SAP sensitivity loss to loss of the retinal nerve fiber layer (RNFL) requires a map that relates local field regions to local regions of the optic disc as described in Section 3. When RNFL thickness in the superior and inferior arcuate sectors of the disc are plotted against SAP sensitivity loss (dB units) in the corresponding arcuate regions of the visual field, RNFL thickness becomes asymptotic for sensitivity losses greater than about 10 dB. These data are well described by a simple linear model presented in Section 4. The model assumes that the RNFL thickness measured with OCT has two components. One component is the axons of the retinal ganglion cells and the other, the residual, is everything else (e.g. glial cells, blood vessels). The axon portion is assumed to decrease in a linear fashion with losses in SAP sensitivity (in linear units); the residual portion is assumed to remain constant. Based upon severe SAP losses in anterior ischemic optic neuropathy (AION), the residual RNFL thickness in the arcuate regions is, on average, about one-third of the premorbid (normal) thickness of that region. The model also predicts that, to a first approximation, SAP sensitivity in control subjects does not depend upon RNFL thickness. The data (Section 6) are, in general, consistent with this prediction showing a very weak correlation between RNFL thickness and SAP sensitivity. In Section 7, the model is used to estimate the proportion of patients showing statistical abnormalities (worse than the 5th percentile) on the OCT RNFL test before they show abnormalities on the 24-2 SAP field test. Ignoring measurement error, the patients with a relatively thick RNFL, when healthy, will be more likely to show significant SAP sensitivity loss before statistically significant OCT RNFL loss, while the reverse will be true for those who start with an average or a relatively thin RNFL when healthy. Thus, it is important to understand the implications of the wide variation in RNFL thickness among control subjects. Section 8 describes two of the factors contributing to this variation, variations in the position of blood vessels and variations in the mapping of field regions to disc sectors. Finally, in Sections 7 and 9, the findings are related to the general debate in the literature about the relationship between structural and functional glaucomatous damage and a framework is proposed for understanding what is meant by the question, ‘Does structural damage precede functional damage in glaucoma?’ An emphasis is placed upon the need to distinguish between “statistical” and “relational” meanings of this question. PMID:17889587

Differential cross sections in a thick brane world scenario

NASA Astrophysics Data System (ADS)

Pedraza, Omar; Arceo, R.; López, L. A.; Cerón, V. E.

2018-04-01

The elastic differential cross section is calculated at low energies for the elements He and Ne using an effective 4D electromagnetic potential coming from the contribution of the massive Kaluza-Klein modes of the 5D vector field in a thick brane scenario. The length scale is adjusted in the potential to compare with known experimental data and to set bounds for the parameter of the model.

Method and apparatus for determining weldability of thin sheet metal

DOEpatents

Goodwin, Gene M.; Hudson, Joseph D.

1988-01-01

A fixture is provided for testing thin sheet metal specimens to evaluate hot-cracking sensitivity for determining metal weldability on a heat-to-heat basis or through varying welding parameters. A test specimen is stressed in a first direction with a load selectively adjustable over a wide range and then a weldment is passed along over the specimen in a direction transverse to the direction of strain to evaluate the hot-cracking characteristics of the sheet metal which are indicative of the weldability of the metal. The fixture provides evaluations of hot-cracking sensitivity for determining metal weldability in a highly reproducible manner with minimum human error.

Reactor Materials Program - Baseline Material Property Handbook - Mechanical Properties of 1950's Vintage Stainless Steel Weldment Components, Task Number 89-23-A-1

DOE Office of Scientific and Technical Information (OSTI.GOV)

Stoner, K.J.

1999-11-05

The Process Water System (primary coolant) piping of the nuclear production reactors constructed in the 1950''s at Savannah River Site is comprised primarily of Type 304 stainless steel with Type 308 stainless steel weld filler. A program to measure the mechanical properties of archival PWS piping and weld materials (having approximately six years of service at temperatures between 25 and 100 degrees C) has been completed. The results from the mechanical testing has been synthesized to provide a mechanical properties database for structural analyses of the SRS piping.

Use of photostress and strain gages to analyze behavior of weldments

NASA Astrophysics Data System (ADS)

Gambrell, S. C., Jr.

1993-09-01

Tensile and pure bending tests were conducted on specimens having welded joints made from 2219-T87 aluminum alloy and 2319 filler. Data were collected using photoelastic coatings and strain gages. Stress-strain relationships and contraction ratios were determined at several points in a grid covering the weld material and heat affected zone. Material behavior was nonlinear and nonuniform at all points in the grid and contraction ratios did not conform to those predicted by Chakrabarty's plasticity theory. Yielding in joints made using four new welding procedures was examined. None of the new procedures produced more uniform yielding in the joint.

Antenatal Sonographic Diagnosis and Clinical Significance of Placenta Previa Accreta after Cesarean Section.

PubMed

Liu, Zhen-Zhen; Wei, Yao; Wang, Ruo-Jiao; Xu, Wen; Shi, Zhi-Min; Dai, Qing

2017-10-30

Objective To investigate the clinical and antenatal sonographic characteristics of placenta previa accreta after cesarean section. Methods The data of 21 inpatients diagnosed as placenta previa accreta after cesarean section in PUMC Hospital from 2006 to 2016 were retrospectively reviewed. The clinical and ultrasound features were recorded and compared among three placental accreta groups,including placenta accrete group(n=5),increta group(n=12),and percreta group(n=4). The relationship between the placental thickness at the uterine anterior lower segment level and the blood loss of the following cesarean section was tested. Results Of 21 patients,placenta previa was diagnosed by ultrasound in 20 cases(95.2%) and placenta previa accreta was diagnosed in 9 cases(42.9%). Antenatal ultrasound findings included following signs:loss of "clear zone"(15/18,83.3%),myometrial thinning(12/18,66.7%),abnormal placental lacunae(12/19,63.2%),bladder wall interruption(2/18,11.1%),and uterovesical hypervascularity(4/9,44.4%). Myometrial thinning(J-T=64.000,P=0.036),abnormal placental lacunae(J-T=74.500,P=0.032) and the placental thickness at the uterine anterior lower segment level(U=83.000,P=0.010) showed significant difference among different placenta accreta groups. Placental thickness at the uterine anterior lower segment level showed linear correlation with the blood loss of the following cesarean section(r=0.669,P=0.002). The blood loss of the following cesarean section showed significant difference among different placenta accreta groups(U=118.500,P=0.000). Conclusions The clinical and sonographic manifestations of placenta previa accreta after cesarean section show a spectrum of demographic characteristics. The measurement of thickness of placenta at the anterior lower segment may help the evaluation of the clinical prognosis of this special pathology.

Human Chorioretinal Layer Thicknesses Measured in Macula-wide, High-Resolution Histologic Sections

PubMed Central

Messinger, Jeffrey D.; Sloan, Kenneth R.; Mitra, Arnab; McGwin, Gerald; Spaide, Richard F.

2011-01-01

Purpose. To provide a comprehensive description of chorioretinal layer thicknesses in the normal human macula, including two-layer pairs that can produce a combined signal in some optical coherence tomography (OCT) devices (ganglion cell [GCL] and inner plexiform [IPL] layers and outer plexiform [OPL] and outer nuclear [ONL] layers). Methods. In 0.8-μm-thick, macula-wide sections through the foveola of 18 donors (age range, 40–92 years), 21 layers were measured at 25 locations by a trained observer and validated by a second observer. Tissue volume changes were assessed by comparing total retinal thickness in ex vivo OCT and in sections. Results. Median tissue shrinkage was 14.5% overall and 29% in the fovea. Histologic laminar boundaries resembled those in SD-OCT scans, but the shapes of the foveolar OPL and ONL differed. Histologic GCL, IPL, and OPLHenle were thickest at 0.8. to 1, 1.5, and 0.4 mm eccentricity, respectively. ONL was thickest in an inward bulge at the foveal center. At 1 mm eccentricity, GCL, INL, and OPLHenle represented 17.3% to 21.1%, 18.0% to 18.5%, and 14.2% to 16.6% of total retinal thickness, respectively. In donors ≥70 years of age, the RPE and choroid were 17.1% and 29.6% thinner and OPLHenle was 20.8% thicker than in donors <70 years. Conclusions. In this study, the first graphic representation and thickness database of chorioretinal layers in normal macula were generated. Newer OCT systems can separate GCL from IPL and OPLHenle from ONL, with good agreement for the proportion of retinal thickness occupied by OPLHenle in OCT and histology. The thickening of OPLHenle in older eyes may reflect Müller cell hypertrophy associated with rod loss. PMID:21421869

DOE Office of Scientific and Technical Information (OSTI.GOV)

Tomlinson, Kurt; Seagle, C. T.; Huang, H.

A measurement instrument utilizing dual, chromatic, confocal, distance sensors has been jointly developed by General Atomics (GA) and Sandia National Laboratories (SNL) for thickness and flatness measurement of target components used in dynamic materials properties (DMP) experiments on the SNL Z-Machine (Z). Compared to previous methods used in production of these types of targets, the tool saves time and yields a 4x reduction in thickness uncertainty which is one of the largest sources of error in equation of state (EOS) measurements critical to supporting the NNSA’s Stockpile Stewardship program and computer modeling of high energy density experiments. It has numerousmore » differences from earlier instruments operating on the dual confocal sensor principle to accommodate DMP components including larger lateral travel, longer working distance, ability to measure flatness in addition to thickness, built-in thickness calibration standards for quickly checking calibration before and after each measurement, and streamlined operation. Thickness and flatness of 0.2mm-3.3mm thick sections of diamond machined copper and aluminum can be measured to “sub-micron” accuracy. Sections up to 6mm thick can be measured with as-yet undermined accuracy. Furthermore, samples must have one surface which is flat to within 300µm, lateral dimensions of no more than 50mm x 50mm, and height less than 40mm.« less

Enhanced Dual Confocal Measurement System

DOE PAGES

Tomlinson, Kurt; Seagle, C. T.; Huang, H.; ...

2017-11-29

A measurement instrument utilizing dual, chromatic, confocal, distance sensors has been jointly developed by General Atomics (GA) and Sandia National Laboratories (SNL) for thickness and flatness measurement of target components used in dynamic materials properties (DMP) experiments on the SNL Z-Machine (Z). Compared to previous methods used in production of these types of targets, the tool saves time and yields a 4x reduction in thickness uncertainty which is one of the largest sources of error in equation of state (EOS) measurements critical to supporting the NNSA’s Stockpile Stewardship program and computer modeling of high energy density experiments. It has numerousmore » differences from earlier instruments operating on the dual confocal sensor principle to accommodate DMP components including larger lateral travel, longer working distance, ability to measure flatness in addition to thickness, built-in thickness calibration standards for quickly checking calibration before and after each measurement, and streamlined operation. Thickness and flatness of 0.2mm-3.3mm thick sections of diamond machined copper and aluminum can be measured to “sub-micron” accuracy. Sections up to 6mm thick can be measured with as-yet undermined accuracy. Furthermore, samples must have one surface which is flat to within 300µm, lateral dimensions of no more than 50mm x 50mm, and height less than 40mm.« less

Does cortical bone thickness in the last sacral vertebra differ among tail types in primates?

PubMed

Nishimura, Abigail C; Russo, Gabrielle A

2017-04-01

The external morphology of the sacrum is demonstrably informative regarding tail type (i.e., tail presence/absence, length, and prehensility) in living and extinct primates. However, little research has focused on the relationship between tail type and internal sacral morphology, a potentially important source of functional information when fossil sacra are incomplete. Here, we determine if cortical bone cross-sectional thickness of the last sacral vertebral body differs among tail types in extant primates and can be used to reconstruct tail types in extinct primates. Cortical bone cross-sectional thickness in the last sacral vertebral body was measured from high-resolution CT scans belonging to 20 extant primate species (N = 72) assigned to tail type categories ("tailless," "nonprehensile short-tailed," "nonprehensile long-tailed," and "prehensile-tailed"). The extant dataset was then used to reconstruct the tail types for four extinct primate species. Tailless primates had significantly thinner cortical bone than tail-bearing primates. Nonprehensile short-tailed primates had significantly thinner cortical bone than nonprehensile long-tailed primates. Cortical bone cross-sectional thickness did not distinguish between prehensile-tailed and nonprehensile long-tailed taxa. Results are strongly influenced by phylogeny. Corroborating previous studies, Epipliopithecus vindobonensis was reconstructed as tailless, Archaeolemur edwardsi as long-tailed, Megaladapis grandidieri as nonprehensile short-tailed, and Palaeopropithecus kelyus as nonprehensile short-tailed or tailless. Results indicate that, in the context of phylogenetic clade, measures of cortical bone cross-sectional thickness can be used to allocate extinct primate species to tail type categories. © 2017 Wiley Periodicals, Inc.

Versatile technique for assessing thickness of 2D layered materials by XPS

NASA Astrophysics Data System (ADS)

Zemlyanov, Dmitry Y.; Jespersen, Michael; Zakharov, Dmitry N.; Hu, Jianjun; Paul, Rajib; Kumar, Anurag; Pacley, Shanee; Glavin, Nicholas; Saenz, David; Smith, Kyle C.; Fisher, Timothy S.; Voevodin, Andrey A.

2018-03-01

X-ray photoelectron spectroscopy (XPS) has been utilized as a versatile method for thickness characterization of various two-dimensional (2D) films. Accurate thickness can be measured simultaneously while acquiring XPS data for chemical characterization of 2D films having thickness up to approximately 10 nm. For validating the developed technique, thicknesses of few-layer graphene (FLG), MoS2 and amorphous boron nitride (a-BN) layer, produced by microwave plasma chemical vapor deposition (MPCVD), plasma enhanced chemical vapor deposition (PECVD), and pulsed laser deposition (PLD) respectively, were accurately measured. The intensity ratio between photoemission peaks recorded for the films (C 1s, Mo 3d, B 1s) and the substrates (Cu 2p, Al 2p, Si 2p) is the primary input parameter for thickness calculation, in addition to the atomic densities of the substrate and the film, and the corresponding electron attenuation length (EAL). The XPS data was used with a proposed model for thickness calculations, which was verified by cross-sectional transmission electron microscope (TEM) measurement of thickness for all the films. The XPS method determines thickness values averaged over an analysis area which is orders of magnitude larger than the typical area in cross-sectional TEM imaging, hence provides an advanced approach for thickness measurement over large areas of 2D materials. The study confirms that the versatile XPS method allows rapid and reliable assessment of the 2D material thickness and this method can facilitate in tailoring growth conditions for producing very thin 2D materials effectively over a large area. Furthermore, the XPS measurement for a typical 2D material is non-destructive and does not require special sample preparation. Therefore, after XPS analysis, exactly the same sample can undergo further processing or utilization.

Versatile technique for assessing thickness of 2D layered materials by XPS

DOE PAGES

Zemlyanov, Dmitry Y.; Jespersen, Michael; Zakharov, Dmitry N.; ...

2018-02-07

X-ray photoelectron spectroscopy (XPS) has been utilized as a versatile method for thickness characterization of various two-dimensional (2D) films. Accurate thickness can be measured simultaneously while acquiring XPS data for chemical characterization of 2D films having thickness up to approximately 10 nm. For validating the developed technique, thicknesses of few-layer graphene (FLG), MoS 2 and amorphous boron nitride (a-BN) layer, produced by microwave plasma chemical vapor deposition (MPCVD), plasma enhanced chemical vapor deposition (PECVD), and pulsed laser deposition (PLD) respectively, were accurately measured. The intensity ratio between photoemission peaks recorded for the films (C 1s, Mo 3d, B 1s) andmore » the substrates (Cu 2p, Al 2p, Si 2p) is the primary input parameter for thickness calculation, in addition to the atomic densities of the substrate and the film, and the corresponding electron attenuation length (EAL). The XPS data was used with a proposed model for thickness calculations, which was verified by cross-sectional transmission electron microscope (TEM) measurement of thickness for all the films. The XPS method determines thickness values averaged over an analysis area which is orders of magnitude larger than the typical area in cross-sectional TEM imaging, hence provides an advanced approach for thickness measurement over large areas of 2D materials. The study confirms that the versatile XPS method allows rapid and reliable assessment of the 2D material thickness and this method can facilitate in tailoring growth conditions for producing very thin 2D materials effectively over a large area. Furthermore, the XPS measurement for a typical 2D material is non-destructive and does not require special sample preparation. Furthermore, after XPS analysis, exactly the same sample can undergo further processing or utilization.« less

Versatile technique for assessing thickness of 2D layered materials by XPS.

PubMed

Zemlyanov, Dmitry Y; Jespersen, Michael; Zakharov, Dmitry N; Hu, Jianjun; Paul, Rajib; Kumar, Anurag; Pacley, Shanee; Glavin, Nicholas; Saenz, David; Smith, Kyle C; Fisher, Timothy S; Voevodin, Andrey A

2018-03-16

X-ray photoelectron spectroscopy (XPS) has been utilized as a versatile method for thickness characterization of various two-dimensional (2D) films. Accurate thickness can be measured simultaneously while acquiring XPS data for chemical characterization of 2D films having thickness up to approximately 10 nm. For validating the developed technique, thicknesses of few-layer graphene (FLG), MoS 2 and amorphous boron nitride (a-BN) layer, produced by microwave plasma chemical vapor deposition (MPCVD), plasma enhanced chemical vapor deposition (PECVD), and pulsed laser deposition (PLD) respectively, were accurately measured. The intensity ratio between photoemission peaks recorded for the films (C 1s, Mo 3d, B 1s) and the substrates (Cu 2p, Al 2p, Si 2p) is the primary input parameter for thickness calculation, in addition to the atomic densities of the substrate and the film, and the corresponding electron attenuation length (EAL). The XPS data was used with a proposed model for thickness calculations, which was verified by cross-sectional transmission electron microscope (TEM) measurement of thickness for all the films. The XPS method determines thickness values averaged over an analysis area which is orders of magnitude larger than the typical area in cross-sectional TEM imaging, hence provides an advanced approach for thickness measurement over large areas of 2D materials. The study confirms that the versatile XPS method allows rapid and reliable assessment of the 2D material thickness and this method can facilitate in tailoring growth conditions for producing very thin 2D materials effectively over a large area. Furthermore, the XPS measurement for a typical 2D material is non-destructive and does not require special sample preparation. Therefore, after XPS analysis, exactly the same sample can undergo further processing or utilization.

Versatile technique for assessing thickness of 2D layered materials by XPS

DOE Office of Scientific and Technical Information (OSTI.GOV)

Zemlyanov, Dmitry Y.; Jespersen, Michael; Zakharov, Dmitry N.

X-ray photoelectron spectroscopy (XPS) has been utilized as a versatile method for thickness characterization of various two-dimensional (2D) films. Accurate thickness can be measured simultaneously while acquiring XPS data for chemical characterization of 2D films having thickness up to approximately 10 nm. For validating the developed technique, thicknesses of few-layer graphene (FLG), MoS 2 and amorphous boron nitride (a-BN) layer, produced by microwave plasma chemical vapor deposition (MPCVD), plasma enhanced chemical vapor deposition (PECVD), and pulsed laser deposition (PLD) respectively, were accurately measured. The intensity ratio between photoemission peaks recorded for the films (C 1s, Mo 3d, B 1s) andmore » the substrates (Cu 2p, Al 2p, Si 2p) is the primary input parameter for thickness calculation, in addition to the atomic densities of the substrate and the film, and the corresponding electron attenuation length (EAL). The XPS data was used with a proposed model for thickness calculations, which was verified by cross-sectional transmission electron microscope (TEM) measurement of thickness for all the films. The XPS method determines thickness values averaged over an analysis area which is orders of magnitude larger than the typical area in cross-sectional TEM imaging, hence provides an advanced approach for thickness measurement over large areas of 2D materials. The study confirms that the versatile XPS method allows rapid and reliable assessment of the 2D material thickness and this method can facilitate in tailoring growth conditions for producing very thin 2D materials effectively over a large area. Furthermore, the XPS measurement for a typical 2D material is non-destructive and does not require special sample preparation. Furthermore, after XPS analysis, exactly the same sample can undergo further processing or utilization.« less

Effects of neuromuscular joint facilitation on bridging exercises with respect to deep muscle changes.

PubMed

Zhou, Bin; Huang, QiuChen; Zheng, Tao; Huo, Ming; Maruyama, Hitoshi

2015-05-01

[Purpose] This study examined the effects of neuromuscular joint facilitation on bridging exercises by assessing the cross-sectional area of the multifidus muscle and thickness of the musculus transversus abdominis. [Subjects] Twelve healthy men. [Methods] Four exercises were evaluated: (a) supine resting, (b) bridging resistance exercise involving posterior pelvic tilting, (c) bridging resistance exercise involving anterior pelvic tilting, and (d) bridging resistance exercise involving neuromuscular joint facilitation. The cross-sectional area of the multifidus muscle and thickness of the musculus transversus abdominis were measured during each exercise. [Results] The cross-sectional area of the multifidus muscle and thickness of the musculus transversus abdominis were significantly greater in the neuromuscular joint facilitation group than the others. [Conclusion] Neuromuscular joint facilitation intervention improves the function of deep muscles such as the multifidus muscle and musculus transversus abdominis. Therefore, it can be recommended for application in clinical treatments such as that for back pain.

Stopping cross sections of He + ions in bismuth

NASA Astrophysics Data System (ADS)

Kuldeep; Jain, Animesh K.

1985-06-01

The stopping cross sections, ɛ( E), of He + ions in bismuth have been measured by Rutherford backscattering spectrometry (RBS) at incident energies ranging from E = 1.6-3.4 MeV. The energy loss of He + ions and thicknesses of the bismuth films deposited on aluminium substrates were determined from the RBS spectra at each energy for scattering angles of 130° and 165°. The film thicknesses of some of the samples were also measured by weighing and the results compared with those from RBS. Parameters for energy dependence of stopping cross section in the Varelas-Biersack interpolation formula have been obtained for bismuth from a fit to all the available experimental data. Accuracy of our method based on RBS is demonstrated by measurements on copper, for which ɛ( E) is already well studied. It is also shown that reliable ɛ( E) values may be obtained even on samples with non-uniform film thickness.

Assessment of cross-sectional thickness and activity of masseter, anterior temporalis and orbicularis oris muscles in oral submucous fibrosis patients and healthy controls: an ultrasonography and electromyography study

PubMed Central

Bhowate, R R; Sharda, N

2014-01-01

Objectives: Oral submucous fibrosis (OSMF) is an insidious chronic disease that is associated with significant functional morbidity and an increased risk for malignancy. It initially affects the lamina propria of the oral mucosa, and, as the disease progresses, it involves the submucosa and deeper tissue, including muscles of the oral cavity, resulting in loss of fibroelasticity. OSMF is a pre-malignant condition mainly caused by areca nut chewing. The aim of this study was to find out the involvement of muscles of mastication and facial expression in patients with OSMF by assessing the cross-sectional thickness and activity of the masseter, anterior temporalis and orbicularis oris muscles by ultrasonography and electromyography and comparing with healthy controls and also to find out any correlation between the ultrasonographic cross-sectional thicknesses of the masseter, anterior temporalis and orbicularis oris muscles with electromyographic activity. Methods: 40 patients with OSMF were included in the study group, and the patients were divided into four groups on the basis of interincisal mouth opening, i.e. Group I (mouth opening >35 mm), Group II (mouth opening between 30 and 35 mm), Group III (mouth opening between 20 and 30 mm) and Group IV (mouth opening <20 mm). Ultrasonographic cross-sectional thickness and electromyographic activity (amplitude and duration) of the masseter, anterior temporalis and orbicualris oris muscles were recorded in patients with OSMF and 20 controls. Intergroup comparison of ultrasonographic cross-sectional thickness and activity (amplitude and duration) was done, and Pearson's correlation coefficient was applied to find out any relation between ultrasonographic and electromyographic findings. Results: Thickness and activity of the masseter muscle was significantly reduced in Group IV (mouth opening <20 mm) when compared with the control group. The anterior temporalis and orbicularis oris muscles remained unaffected. A positive correlation was observed between the thicknesses of the masseter muscle and the amplitude in Groups I, II and III; the anterior temporalis muscle in Group II and the control group; and the orbicularis oris muscle in Groups II, III and IV. Conclusions: It was concluded that, among the muscles studied, there was an early involvement of the masseter muscle in patients with OSMF compared with that of other muscles. PMID:24720604

Assessment of cross-sectional thickness and activity of masseter, anterior temporalis and orbicularis oris muscles in oral submucous fibrosis patients and healthy controls: an ultrasonography and electromyography study.

PubMed

Kant, P; Bhowate, R R; Sharda, N

2014-01-01

Oral submucous fibrosis (OSMF) is an insidious chronic disease that is associated with significant functional morbidity and an increased risk for malignancy. It initially affects the lamina propria of the oral mucosa, and, as the disease progresses, it involves the submucosa and deeper tissue, including muscles of the oral cavity, resulting in loss of fibroelasticity. OSMF is a pre-malignant condition mainly caused by areca nut chewing. The aim of this study was to find out the involvement of muscles of mastication and facial expression in patients with OSMF by assessing the cross-sectional thickness and activity of the masseter, anterior temporalis and orbicularis oris muscles by ultrasonography and electromyography and comparing with healthy controls and also to find out any correlation between the ultrasonographic cross-sectional thicknesses of the masseter, anterior temporalis and orbicularis oris muscles with electromyographic activity. 40 patients with OSMF were included in the study group, and the patients were divided into four groups on the basis of interincisal mouth opening, i.e. Group I (mouth opening >35 mm), Group II (mouth opening between 30 and 35 mm), Group III (mouth opening between 20 and 30 mm) and Group IV (mouth opening <20 mm). Ultrasonographic cross-sectional thickness and electromyographic activity (amplitude and duration) of the masseter, anterior temporalis and orbicualris oris muscles were recorded in patients with OSMF and 20 controls. Intergroup comparison of ultrasonographic cross-sectional thickness and activity (amplitude and duration) was done, and Pearson's correlation coefficient was applied to find out any relation between ultrasonographic and electromyographic findings. Thickness and activity of the masseter muscle was significantly reduced in Group IV (mouth opening <20 mm) when compared with the control group. The anterior temporalis and orbicularis oris muscles remained unaffected. A positive correlation was observed between the thicknesses of the masseter muscle and the amplitude in Groups I, II and III; the anterior temporalis muscle in Group II and the control group; and the orbicularis oris muscle in Groups II, III and IV. It was concluded that, among the muscles studied, there was an early involvement of the masseter muscle in patients with OSMF compared with that of other muscles.

Calculation of linearized supersonic flow over slender cones of arbitrary cross section

NASA Technical Reports Server (NTRS)

Mascitti, V. R.

1972-01-01

Supersonic linearized conical-flow theory is used to determine the flow over slender pointed cones having horizontal and vertical planes of symmetry. The geometry of the cone cross sections and surface velocities are expanded in Fourier series. The symmetry condition permits the uncoupling of lifting and nonlifting solutions. The present method reduces to Ward's theory for flow over a cone of elliptic cross section. Results are also presented for other shapes. Results by this method diverge for cross-sectional shapes where the maximum thickness is large compared with the minimum thickness. However, even for these slender-body shapes, lower order solutions are good approximations to the complete solution.

Test Methods for Composites: A Status Report. Volume 2. Compression Test Methods

DTIC Science & Technology

1993-06-01

glass and Kevlar fibers in a phenolic matrix) were relatively thick (24 plies), and more importantly, failed at very low compressive strength levels...ICH LAMINATE SPECIMEN TEST METHOD ........................................ 29 2.4 RECOMMENDATIONS...Thickness in the Middle of the Gage Section, for Four Laminate Thicknesses [711 ................... 143 52. Axial Stress Distributions in an AS4/3502 Carbon

Preparation of iridium targets by electrodeposition for neutron capture cross section measurements

DOE PAGES

Bond, Evelyn M.; Moody, W. Allen; Arnold, Charles; ...

2016-03-01

Here, the preparation of 191Ir and 193Ir electrodeposits for neutron capture cross-section measurements at the detector for advanced neutron capture experiments located at the at Los Alamos Neutron Science Center is described. The electrodeposition of iridium in the desired thickness of 0.4–1 mg/cm 2 is challenging. Better yields and thicknesses were obtained using electrodeposition from isopropyl alcohol solutions than from ammonium sulfate solutions. 191Ir and 193Ir targets were initially prepared using the standard single-sided electrodeposition cell. Iridium electrodepositions using a double-sided electrodeposition cell were developed and were optimized, resulting in thick, uniform iridium deposits. LA UR 15-22475.

Obsidian hydration dates glacial loading?

USGS Publications Warehouse

Friedman, I.; Pierce, K.L.; Obradovich, J.D.; Long, W.D.

1973-01-01

Three different groups of hydration rinds have been measured on thin sections of obsidian from Obsidian Cliff, Yellowstone National Park, Wyoming . The average thickness of the thickest (oldest) group of hydration rinds is 16.3 micrometers and can be related to the original emplacement of the flow 176,000 years ago (potassium-argon age). In addition to these original surfaces, most thin sections show cracks and surfaces which have average hydration rind thicknesses of 14.5 and 7.9 micrometers. These later two hydration rinds compare closely in thickness with those on obsidian pebbles in the Bull Lake and Pinedale terminal moraines in the West Yellowstone Basin, which are 14 to 15 and 7 to 8 micrometers thick, respectively. The later cracks are thought to have been formed by glacial loading during the Bull Lake and Pinedale glaciations, when an estimated 800 meters of ice covered the Obsidian Cliff flow.

Obsidian hydration dates glacial loading?

PubMed

Friedman, I; Pierce, K L; Obradovich, J D; Long, W D

1973-05-18

Three different groups of hydration rinds have been measured on thin sections of obsidian from Obsidian Cliff, Yellowstone National Park, Wyoming. The average thickness of the thickest (oldest) group of hydration rinds is 16.3 micrometers and can be related to the original emplacement of the flow 176,000 years ago (potassium-argon age). In addition to these original surfaces, most thin sections show cracks and surfaces which have average hydration rind thicknesses of 14.5 and 7.9 micrometers. These later two hydration rinds compare closely in thickness with those on obsidian pebbles in the Bull Lake and Pinedale terminal moraines in the West Yellowstone Basin, which are 14 to 15 and 7 to 8 micrometers thick, respectively. The later cracks are thought to have been formed by glacial loading during the Bull Lake and Pinedale glaciations, when an estimated 800 meters of ice covered the Obsidian Cliff flow.

Penetration of immunoreagents in Vibratome-sectioned brain: a light and electron microscopic study.

PubMed

Piekut, D T; Casey, S M

1983-05-01

Immunocytochemical studies on the localization of peptides at the ultrastructural level have most frequently involved the application of the peroxidase--antiperoxidase (PAP) method of immunocytochemistry and the use of the preembedding or postembedding staining procedures. The present study was designed to determine the depth of penetration of Vibratome tissue sections by immunoreagents used in the preembedding method in which immunostaining of unembedded fixed tissue sections is accomplished prior to tissue dehydration and embedment. Our data indicate that penetration of immunoreagents is restricted to the superficial 8-9 micrometers of a 80-micrometers thick Vibratome tissue section of hypothalamus of brain using antisera generated against arginine vasopressin. The final immunoreaction product visualized in a Vibratome tissue section may reflect only a fraction of the amount of hormone contained within the thickness of the tissue section.

Accurate Rapid Lifetime Determination on Time-Gated FLIM Microscopy with Optical Sectioning

PubMed Central

Silva, Susana F.; Domingues, José Paulo

2018-01-01

Time-gated fluorescence lifetime imaging microscopy (FLIM) is a powerful technique to assess the biochemistry of cells and tissues. When applied to living thick samples, it is hampered by the lack of optical sectioning and the need of acquiring many images for an accurate measurement of fluorescence lifetimes. Here, we report on the use of processing techniques to overcome these limitations, minimizing the acquisition time, while providing optical sectioning. We evaluated the application of the HiLo and the rapid lifetime determination (RLD) techniques for accurate measurement of fluorescence lifetimes with optical sectioning. HiLo provides optical sectioning by combining the high-frequency content from a standard image, obtained with uniform illumination, with the low-frequency content of a second image, acquired using structured illumination. Our results show that HiLo produces optical sectioning on thick samples without degrading the accuracy of the measured lifetimes. We also show that instrument response function (IRF) deconvolution can be applied with the RLD technique on HiLo images, improving greatly the accuracy of the measured lifetimes. These results open the possibility of using the RLD technique with pulsed diode laser sources to determine accurately fluorescence lifetimes in the subnanosecond range on thick multilayer samples, providing that offline processing is allowed. PMID:29599938

Accurate Rapid Lifetime Determination on Time-Gated FLIM Microscopy with Optical Sectioning.

PubMed

Silva, Susana F; Domingues, José Paulo; Morgado, António Miguel

2018-01-01

Time-gated fluorescence lifetime imaging microscopy (FLIM) is a powerful technique to assess the biochemistry of cells and tissues. When applied to living thick samples, it is hampered by the lack of optical sectioning and the need of acquiring many images for an accurate measurement of fluorescence lifetimes. Here, we report on the use of processing techniques to overcome these limitations, minimizing the acquisition time, while providing optical sectioning. We evaluated the application of the HiLo and the rapid lifetime determination (RLD) techniques for accurate measurement of fluorescence lifetimes with optical sectioning. HiLo provides optical sectioning by combining the high-frequency content from a standard image, obtained with uniform illumination, with the low-frequency content of a second image, acquired using structured illumination. Our results show that HiLo produces optical sectioning on thick samples without degrading the accuracy of the measured lifetimes. We also show that instrument response function (IRF) deconvolution can be applied with the RLD technique on HiLo images, improving greatly the accuracy of the measured lifetimes. These results open the possibility of using the RLD technique with pulsed diode laser sources to determine accurately fluorescence lifetimes in the subnanosecond range on thick multilayer samples, providing that offline processing is allowed.

Carbon analyses of IDP's sectioned in sulfur and supported on beryllium films

NASA Technical Reports Server (NTRS)

Bradley, J. P.; Keller, L.; Thomas, K. L.; Vanderwood, T. B.; Brownlee, D. E.

1993-01-01

Carbon is the only major element in interplanetary dust whose abundance, distribution and chemical state are not well understood. Information about carbon could clarify the relationship between the various classes of IDP's, conventional meteorites, and sources (e.g., comets vs. asteroids). To date, the most reliable estimates of C abundance in Interplanetary Dust Particles (IDP's) have been obtained by analyzing particles on thick-flat Be substrates using thin-window energy-dispersive spectroscopy in the SEM. These estimates of C abundance are valid only if C is homogeneously distributed, because detected C x-rays originate from the outer 0.1 micrometers of the particle. An alternative and potentially more accurate method of measuring C abundances is to analyze multiple thin sections (each less than 0.1 less than 0.1 micrometers thick) of IDP's. These efforts however, have been stymied because of a lack of a suitable non-carbonaceous embedding medium and the availability of C-free conductive substrates. We have embedded and thin-sectioned IDP's in glassy sulfur, and transferred the thin sections to Be support films approximately 25 nm thick. The sections were then analyzed in a 200 KeV analytical TEM. S sublimes rapidly under vacuum in the TEM, leaving non-embedded sections supported on Be. Apart from quantitative C (and O) analyses, S sectioning dramatically expands the range of analytical measurements that can be performed on a single IDP.

Asphaltic concrete overlays of rigid and flexible pavements : final report.

DOT National Transportation Integrated Search

1980-10-01

This study evaluated the effect of a given thickness of asphaltic concrete overlay in rehabilitating 53 test sections conforming to the experiment design. This factorial design specified various levels of traffic intensity and overlay thickness for b...

Implementation and thickness optimization of perpetual pavements in Ohio.

DOT National Transportation Integrated Search

2015-06-01

This report documents the performance of perpetual pavement structures constructed by the Ohio Department of Transportation. : Three perpetual pavement test sections on U.S. Route 23 in Delaware, Ohio (DEL-23) were constructed with AC thicknesses 11 ...

A comparative analysis of 7.0-Tesla magnetic resonance imaging and histology measurements of knee articular cartilage in a canine posterolateral knee injury model: a preliminary analysis.

PubMed

Pepin, Scott R; Griffith, Chad J; Wijdicks, Coen A; Goerke, Ute; McNulty, Margaret A; Parker, Josh B; Carlson, Cathy S; Ellermann, Jutta; LaPrade, Robert F

2009-11-01

There has recently been increased interest in the use of 7.0-T magnetic resonance imaging for evaluating articular cartilage degeneration and quantifying the progression of osteoarthritis. The purpose of this study was to evaluate articular cartilage cross-sectional area and maximum thickness in the medial compartment of intact and destabilized canine knees using 7.0-T magnetic resonance images and compare these results with those obtained from the corresponding histologic sections. Controlled laboratory study. Five canines had a surgically created unilateral grade III posterolateral knee injury that was followed for 6 months before euthanasia. The opposite, noninjured knee was used as a control. At necropsy, 3-dimensional gradient echo images of the medial tibial plateau of both knees were obtained using a 7.0-T magnetic resonance imaging scanner. Articular cartilage area and maximum thickness in this site were digitally measured on the magnetic resonance images. The proximal tibias were processed for routine histologic analysis with hematoxylin and eosin staining. Articular cartilage area and maximum thickness were measured in histologic sections corresponding to the sites of the magnetic resonance slices. The magnetic resonance imaging results revealed an increase in articular cartilage area and maximum thickness in surgical knees compared with control knees in all specimens; these changes were significant for both parameters (P <.05 for area; P <.01 for thickness). The average increase in area was 14.8% and the average increase in maximum thickness was 15.1%. The histologic results revealed an average increase in area of 27.4% (P = .05) and an average increase in maximum thickness of 33.0% (P = .06). Correlation analysis between the magnetic resonance imaging and histology data revealed that the area values were significantly correlated (P < .01), but the values for thickness obtained from magnetic resonance imaging were not significantly different from the histology sections (P > .1). These results demonstrate that 7.0-T magnetic resonance imaging provides an alternative method to histology to evaluate early osteoarthritic changes in articular cartilage in a canine model by detecting increases in articular cartilage area. The noninvasive nature of 7.0-T magnetic resonance imaging will allow for in vivo monitoring of osteoarthritis progression and intervention in animal models and humans for osteoarthritis.

Production and cross-sectional characterization of aligned co-electrospun hollow microfibrous bulk assemblies

DOE Office of Scientific and Technical Information (OSTI.GOV)

Zhou, Feng-Lei; The School of Materials, The University of Manchester, Manchester M13 9PL; CRUK-EPSRC Cancer Imaging Centre in Cambridge and Manchester

2015-11-15

The development of co-electrospun (co-ES) hollow microfibrous assemblies of an appreciable thickness is critical for many practical applications, including filtration membranes and tissue-mimicking scaffolds. In this study, thick uniaxially aligned hollow microfibrous assemblies forming fiber bundles and strips were prepared by co-ES of polycaprolactone (PCL) and polyethylene oxide (PEO) as shell and core materials, respectively. Hollow microfiber bundles were deposited on a fixed rotating disc, which resulted in non-controllable cross-sectional shapes on a macroscopic scale. In comparison, fiber strips were produced with tuneable thickness and width by additionally employing an x–y translation stage in co-ES. Scanning electron microscopy (SEM) imagesmore » of cross-sections of fiber assemblies were analyzed to investigate the effects of production time (from 0.5 h to 12 h), core flow rate (from 0.8 mL/h to 2.0 mL/h) and/or translation speed (from 0.2 mm/s to 5 mm/s) on the pores and porosity. We observed significant changes in pore size and shape with core flow rate but the influence of production time varied; five strips produced under the same conditions had reasonably good size and porosity reproducibility; pore sizes didn't vary significantly from strip bottom to surface, although the porosity gradually decreased and then returned to the initial level. - Highlights: • Hollow microfibrous assemblies based on co-electrospinning are demonstrated. • The thickness and width of co-electrospun strips were controllable. • Cross-sections of fibres had non-normally distributed pore sizes and shapes. • Cross-sections were significantly influenced by production time and flow rate. • Co-electrospun strips had reasonably good reproducible cross-sections.« less

Ultrasound evaluation of intrinsic plantar muscles and fascia in hallux valgus

PubMed Central

Lobo, César Calvo; Marín, Alejandro Garrido; Sanz, David Rodríguez; López, Daniel López; López, Patricia Palomo; Morales, Carlos Romero; Corbalán, Irene Sanz

2016-01-01

Abstract A cross-sectional area (CSA) and thickness reduction of the abductor hallucis (AbH) is shown in subjects with hallux valgus (HV). To date, other soft-tissue structures have not been researched in relation with HV. The aim of this study was to compare the CSA and thickness of the intrinsic plantar muscles and fascia (PF) between feet with and without HV. Therefore, a cross-sectional and case-control study was performed using B-mode with an iU22 Philips ultrasound system and a 5 to 17-MHz transducer. The CSA and thickness were measured for the AbH, flexor digitorum brevis (FDB) and flexor hallucis brevis (FHB), and also the thickness for the anterior, middle, and posterior PF portions. A convenience sample of 40 feet, 20 with HV and 20 without HV, was recruited from a clinical and research center. A multivariate regression analysis using linear regression was performed to evaluate the ultrasound imaging measurements (α = 0.05). Consequently, statistically significant differences were observed between the groups (P < 0.05) for the AbH and FHB thickness, and CSA reduction, and also the plantar fascia thickness increase in favor of the HV group. On the contrary, the FDB thickness and CSA did not show statistically significant differences (P ≥ 0.05). In conclusion, the CSA and thickness of the AbH and FHB intrinsic plantar muscles are reduced, whereas the thickness of the anterior, middle, and posterior PF portions are increased, in subjects with HV compared with those without HV. PMID:27828846

Ultrasound evaluation of intrinsic plantar muscles and fascia in hallux valgus: A case-control study.

PubMed

Lobo, César Calvo; Marín, Alejandro Garrido; Sanz, David Rodríguez; López, Daniel López; López, Patricia Palomo; Morales, Carlos Romero; Corbalán, Irene Sanz

2016-11-01

A cross-sectional area (CSA) and thickness reduction of the abductor hallucis (AbH) is shown in subjects with hallux valgus (HV). To date, other soft-tissue structures have not been researched in relation with HV. The aim of this study was to compare the CSA and thickness of the intrinsic plantar muscles and fascia (PF) between feet with and without HV. Therefore, a cross-sectional and case-control study was performed using B-mode with an iU22 Philips ultrasound system and a 5 to 17-MHz transducer. The CSA and thickness were measured for the AbH, flexor digitorum brevis (FDB) and flexor hallucis brevis (FHB), and also the thickness for the anterior, middle, and posterior PF portions. A convenience sample of 40 feet, 20 with HV and 20 without HV, was recruited from a clinical and research center. A multivariate regression analysis using linear regression was performed to evaluate the ultrasound imaging measurements (α = 0.05). Consequently, statistically significant differences were observed between the groups (P < 0.05) for the AbH and FHB thickness, and CSA reduction, and also the plantar fascia thickness increase in favor of the HV group. On the contrary, the FDB thickness and CSA did not show statistically significant differences (P ≥ 0.05). In conclusion, the CSA and thickness of the AbH and FHB intrinsic plantar muscles are reduced, whereas the thickness of the anterior, middle, and posterior PF portions are increased, in subjects with HV compared with those without HV.

Nonequal iteration directional filters permit selective clearance of ripples in passband circuits

NASA Technical Reports Server (NTRS)

Kurpis, G. P.

1970-01-01

Modified directional filter is comprised of alternate pairs of dielectric and air gap filter sections with unequal electrical lengths. Filter provides more flexibility in choosing dielectric material thickness and permits switching from specially ground to standard thicknesses.

Asphaltic concrete overlays of rigid and flexible pavements : interim report No. 1.

DOT National Transportation Integrated Search

1977-09-01

This study evaluated the effect of a given thickness of asphaltic concrete overlay in rehabilitating 53 test sections conforming to the experiment design. This factorial design specified various levels of traffic intensity and overlay thickness for b...

Nanoscale size effects on the mechanical properties of platinum thin films and cross-sectional grain morphology

NASA Astrophysics Data System (ADS)

Abbas, K.; Alaie, S.; Ghasemi Baboly, M.; Elahi, M. M. M.; Anjum, D. H.; Chaieb, S.; Leseman, Z. C.

2016-01-01

The mechanical behavior of polycrystalline Pt thin films is reported for thicknesses of 75 nm, 100 nm, 250 nm, and 400 nm. These thicknesses correspond to transitions between nanocrystalline grain morphology types as found in TEM studies. Thinner samples display a brittle behavior, but as thickness increases the grain morphology evolves, leading to a ductile behavior. During evolution of the morphology, dramatic differences in elastic moduli (105-160 GPa) and strengths (560-1700 MPa) are recorded and explained by the variable morphology. This work suggests that in addition to the in-plane grain size of thin films, the transitions in cross-sectional morphologies of the Pt films significantly affect their mechanical behavior.

Optimization of a Widefield Structured Illumination Microscope for Non-Destructive Assessment and Quantification of Nuclear Features in Tumor Margins of a Primary Mouse Model of Sarcoma

PubMed Central

Fu, Henry L.; Mueller, Jenna L.; Javid, Melodi P.; Mito, Jeffrey K.; Kirsch, David G.; Ramanujam, Nimmi; Brown, J. Quincy

2013-01-01

Cancer is associated with specific cellular morphological changes, such as increased nuclear size and crowding from rapidly proliferating cells. In situ tissue imaging using fluorescent stains may be useful for intraoperative detection of residual cancer in surgical tumor margins. We developed a widefield fluorescence structured illumination microscope (SIM) system with a single-shot FOV of 2.1×1.6 mm (3.4 mm2) and sub-cellular resolution (4.4 µm). The objectives of this work were to measure the relationship between illumination pattern frequency and optical sectioning strength and signal-to-noise ratio in turbid (i.e. thick) samples for selection of the optimum frequency, and to determine feasibility for detecting residual cancer on tumor resection margins, using a genetically engineered primary mouse model of sarcoma. The SIM system was tested in tissue mimicking solid phantoms with various scattering levels to determine impact of both turbidity and illumination frequency on two SIM metrics, optical section thickness and modulation depth. To demonstrate preclinical feasibility, ex vivo 50 µm frozen sections and fresh intact thick tissue samples excised from a primary mouse model of sarcoma were stained with acridine orange, which stains cell nuclei, skeletal muscle, and collagenous stroma. The cell nuclei were segmented using a high-pass filter algorithm, which allowed quantification of nuclear density. The results showed that the optimal illumination frequency was 31.7 µm−1 used in conjunction with a 4×0.1 NA objective ( = 0.165). This yielded an optical section thickness of 128 µm and an 8.9×contrast enhancement over uniform illumination. We successfully demonstrated the ability to resolve cell nuclei in situ achieved via SIM, which allowed segmentation of nuclei from heterogeneous tissues in the presence of considerable background fluorescence. Specifically, we demonstrate that optical sectioning of fresh intact thick tissues performed equivalently in regards to nuclear density quantification, to physical frozen sectioning and standard microscopy. PMID:23894357

Atomic-scale bonding of bulk metallic glass to crystalline aluminum

NASA Astrophysics Data System (ADS)

Liu, K. X.; Liu, W. D.; Wang, J. T.; Yan, H. H.; Li, X. J.; Huang, Y. J.; Wei, X. S.; Shen, J.

2008-08-01

A Ti40Zr25Cu12Ni3Be20 bulk metallic glass (BMG) was welded to a crystalline aluminum by the parallel plate explosive welding method. Experimental evidence and numerical simulation show that atomic-scale bonding between the BMG and the crystalline aluminum can be achieved, and the weldment on the BMG side can retain its amorphous state without any indication of crystallization in the welding process. Nanoindentation tests reveal that the interface of the explosive joints exhibits a significant increase in hardness compared to the matrix on its two sides. The joining of BMG and crystalline materials opens a window to the applications of BMGs in engineering.

Friction plug welding

NASA Technical Reports Server (NTRS)

Takeshita, Riki (Inventor); Hibbard, Terry L. (Inventor)

2001-01-01

Friction plug welding (FPW) usage is advantageous for friction stir welding (FSW) hole close-outs and weld repairs in 2195 Al--Cu--Li fusion or friction stir welds. Current fusion welding methods of Al--Cu--Li have produced welds containing varied defects. These areas are found by non-destructive examination both after welding and after proof testing. Current techniques for repairing typically small (<0.25) defects weaken the weldment, rely heavily on welders' skill, and are costly. Friction plug welding repairs increase strength, ductility and resistance to cracking over initial weld quality, without requiring much time or operator skill. Friction plug welding while pulling the plug is advantageous because all hardware for performing the weld can be placed on one side of the workpiece.

Assesment of influncing factors on mechanical and electrical properties of Al/Cu joints

NASA Astrophysics Data System (ADS)

Selvaraj, R. Meby; Hynes, N. Rajesh Jesudoss

2018-05-01

Joining of dissimilar materials opens up challenging opportunities in todays technology. Al/Cu weldments are used in applications that demands corrosion resistance, thermal and electrical conducting properties. In dissimilar joining mechanical and thermal properties result in large stress gradients during heating. The Al-Cu joints are lighter, cheaper and have conductivity equal to copper alloy. The main scope of this study is to assess the influencing factors of Al/Cu joints in mechanical and electrical properties. It includes the influence of the dilution between the base metals, influence of physical properties, influence of welding parameters, influence of filler metal, influence of heat treatment, and influence of electrical properties

Friction Stir Welding of Steel Alloys

NASA Technical Reports Server (NTRS)

Ding, R. Jeffrey; Munafo, Paul M. (Technical Monitor)

2001-01-01

The friction stir welding process has been developed primarily for the welding of aluminum alloys. Other higher melting allows such, as steels are much more difficult to join. Special attention must be given to pin tool material selection and welding techniques. This paper addresses the joining of steels and other high melting point materials using the friction stir welding process. Pin tool material and welding parameters will be presented. Mechanical properties of weldments will also be presented. Significance: There are many applications for the friction stir welding process other than low melting aluminum alloys. The FSW process can be expanded for use with high melting alloys in the pressure vessel, railroad and ship building industries.

The effects of multiple repairs on Inconel 718 weld mechanical properties

NASA Technical Reports Server (NTRS)

Russell, C. K.; Nunes, A. C., Jr.; Moore, D.

1991-01-01

Inconel 718 weldments were repaired 3, 6, 9, and 13 times using the gas tungsten arc welding process. The welded panels were machined into mechanical test specimens, postweld heat treated, and nondestructively tested. Tensile properties and high cycle fatigue life were evaluated and the results compared to unrepaired weld properties. Mechanical property data were analyzed using the statistical methods of difference in means for tensile properties and difference in log means and Weibull analysis for high cycle fatigue properties. Statistical analysis performed on the data did not show a significant decrease in tensile or high cycle fatigue properties due to the repeated repairs. Some degradation was observed in all properties, however, it was minimal.

Weldability of a high entropy CrMnFeCoNi alloy

DOE PAGES

Wu, Zhenggang; David, Stan A.; Feng, Zhili; ...

2016-07-19

We present the high-entropy alloys are unique alloys in which five or more elements are all in high concentrations. In order to determine its potential as a structural alloy, a model face-centered-cubic CrMnFeCoNi alloy was selected to investigate its weldability. Welds produced by electron beam welding show no cracking. The grain structures within the fusion zone (FZ) are controlled by the solidification behavior of the weld pool. The weldment possesses mechanical properties comparable to those of the base metal (BM) at both room and cryogenic temperatures. Finally, compared with the BM, deformation twinning was more pronounced in the FZ ofmore » the tested alloy.« less

Orbital- to Sub-Orbital-Scale Cyclicity in Seismic Reflections and Sediment Character in Early to Middle Pleistocene Mudstone, Santa Barbara Basin, California

NASA Astrophysics Data System (ADS)

Peterson, C. D.; Behl, R. J.; Nicholson, C.; Lisiecki, L. E.; Sorlien, C. C.

2009-12-01

High-resolution seismic reflection records and well logs from the Santa Barbara Channel suggest that large parts of the Pleistocene succession records climate variability on orbital to sub-orbital scales with remarkable sensitivity, much like the well-studied sediments of the last glacial cycle (ODP Site 893). Spectral analysis of seismic reflection data and gamma ray logs from stratigraphically similar Pleistocene sections finds similar cyclic character and shifts through the section. This correlation suggests that acoustic impedance and physical properties of sediment are linked by basin-scale, likely climatically-driven, oscillations in lithologic composition and fabric during deposition, and that seismic profiling can provide a method for remote identification and correlation of orbital- and sub-orbital-scale sedimentary cyclicity. Where it crops out along the northern shelf of the central Santa Barbara Channel, the early to middle Pleistocene succession (~1.8-1.2 Ma) is a bathyal hemipelagic mudstone with remarkably rhythmic planar bedding, finely laminated fabric, and well-preserved foraminifera, none of which have been significantly altered, or obscured by post-depositional diagenesis or tectonic deformation. Unlike the coarser, turbiditic successions in the central Ventura and Los Angeles basins, this sequence has the potential to record Quaternary global climate change at high resolution. Seismic reflection data (towed chirp) collected on the R/V Melville 2008 Cruise (MV08) penetrate 10's of meters below seafloor into a ~1 km-long sequence of south-dipping seismic reflectors. Sampling parallel to the seafloor permits acquisition of consistent signal amplitude for similar reflectors without spreading loss. Based on established age ranges for this section, sedimentation rates may range from 0.4 to 1.4 meters/kyr, therefore suggesting that the most powerful cycles are orbital- to sub-orbital-scale. Discrete sets of cycles with high power show an abrupt shift to shorter wavelengths midway through the section. Deep in the section, the strongest cycles indicated by spectral analysis are 50 and 16 meters thick, whereas up section, the strongest cycles are 20 and 12 meters thick. Nearby industry boreholes that penetrate a stratigraphically similar, 1500-meter-thick mudstone section, provide logs of natural gamma ray intensity with a higher sample interval (15 cm), allowing resolution and analysis of even higher frequency lithologic cycles. The strongest cycle deep in the section is 100 meters thick, and up section, the strongest cycle is 12 meters thick. This abrupt decrease in dominant cycle thickness midway through both the seismic and gamma ray records perhaps indicates a basin-wide shift in sedimentation. With improved chronostratigraphy based on Sr-isotope ratios and biostratigraphy, and comparison with paleoclimate proxy data, we will test if seismically resolved lithologic oscillations can be reliably interpreted as representing climatically driven Milankovitch cycles. This method may be used to evaluate the age and paleoceanographic potential of sedimentary strata before a coring vessel is deployed.

Assessment of capillary dropout in the superficial retinal capillary plexus by optical coherence tomography angiography in the early stage of diabetic retinopathy.

PubMed

Shen, Ceying; Yan, Shu; Du, Min; Zhao, Hong; Shao, Ling; Hu, Yibo

2018-05-08

To assess capillary dropout in the superficial retinal capillary plexus (SCP) by optical coherence tomography angiography (OCTA) in the early stage of diabetic retinopathy (DR). This study was a cross-sectional observational study. Patients that underwent OCTA examinations in our hospital between November 2015 and May 2016 were included in the study. The subjects were divided into two groups: A) normal controls (41 eyes of 41 subjects) and B) the DR patients (49 eyes of 49 patients with mild non-proliferative DR (NPDR)). The retinal thickness and SCP vessel density were analyzed using built-in software in nine sections of the macular area; whole scan area; fovea; parafovea; and sub-sections of the parafovea, superior-hemi, inferior-hemi, temporal, superior, nasal, and inferior. The correlation between vessel density and retinal thickness was also analyzed. The SCP density was significantly lower (P < 0.05) in mild NPDR patients than in normal controls in all areas, with the exception of the fovea (P > 0.05). In the parafovea, superior-hemi, inferior-hemi, temporal, and nasal sectors of group B, the SCP density was negatively correlated with the corresponding retinal thickness (P < 0.05). Specifically, as the SCP density decreased, retinal thickness increased. In the early stage of NPDR, retinal capillary dropout and retinal thickness changes can be clearly captured and analyzed by OCTA. The results confirm a negative correlation between vessel density and retinal thickness in diabetic patients. This noninvasive technique could be applied for DR detection and monitoring. Further study with a larger sample size is warranted.

Quadriceps Function and Knee Joint Ultrasonography after ACL Reconstruction.

PubMed

Pamukoff, Derek N; Montgomery, Melissa M; Moffit, Tyler J; Vakula, Michael N

2018-02-01

Individuals with anterior cruciate ligament reconstruction (ACLR) are at greater risk for knee osteoarthritis, partially because of chronic quadriceps dysfunction. Articular cartilage is commonly assessed using magnetic resonance imaging and radiography, but these methods are expensive and lack portability. Ultrasound imaging may provide a cost-effective and portable alternative for imaging the femoral cartilage. The purpose of this study was to compare ultrasonography of the femoral cartilage between the injured and uninjured limbs of individuals with unilateral ACLR, and to examine the association between quadriceps function and ultrasonographic measures of femoral cartilage. Bilateral femoral cartilage thickness and quadriceps function were assessed in 44 individuals with unilateral ACLR. Quadriceps function was assessed using peak isometric strength, and early (RTD100) and late (RTD200) rate of torque development. Cartilage thickness at the medial femoral condyle (P < 0.001) and femoral cartilage cross-sectional area (P = 0.007) were smaller in the injured compared with the uninjured limb. After accounting for time since ACLR, quadriceps peak isometric strength was associated with cartilage thickness at the medial femoral condyle (r = 0.35, P = 0.02) and femoral cartilage cross-sectional area (r = 0.28, P = 0.04). RTD100 and RTD200 were not associated with femoral cartilage thickness or cross-sectional area. Individuals with ACLR have thinner cartilage in their injured limb compared with uninjured limb, and cartilage thickness is associated with quadriceps function. These results indicate that ultrasonography may be useful for monitoring cartilage health and osteoarthritis progression after ACLR.

Design study of an entry probe spectro-reflectometer

NASA Technical Reports Server (NTRS)

Sill, G. T.; Fink, U.

1986-01-01

A wind tunnel was built to simulate the rapid movement of an entry probe through the Jupiter atmosphere. Wind speeds range from 1 to 50 meters per second in a closed system. Wind velocity and temperature probes as well as a cryogenically cooled cold finger can be placed in the 6 inch diameter viewing section. The initial testing of the wind tunnel involved running sectional profiles through the observation port of air currents of 0.1 to 3.0 atmosphere. The velocity profile was very uniform throughout the cross section of the experimental port, with the exception of the wall effects. The deposition of cooled volatiles using the wind tunnel was not performed. However, measurements of the deposition of H2O ice on a cryogenically cooled thickness modulator were made under ambient conditions, namely room temperature and pressure. In the Frost Depositon Test Facility, ice deposition was measured at thicknesses of about a half millimeter and frost was produced whose thickness reflectivity could easily be measured by reflectance spectroscopy.

49 CFR 178.345-2 - Material and material thickness.

Code of Federal Regulations, 2011 CFR

2011-10-01

... 49 Transportation 3 2011-10-01 2011-10-01 false Material and material thickness. 178.345-2 Section... HAZARDOUS MATERIALS SAFETY ADMINISTRATION, DEPARTMENT OF TRANSPORTATION (CONTINUED) SPECIFICATIONS FOR PACKAGINGS Specifications for Containers for Motor Vehicle Transportation § 178.345-2 Material and material...

49 CFR 178.345-2 - Material and material thickness.

Code of Federal Regulations, 2014 CFR

2014-10-01

... 49 Transportation 3 2014-10-01 2014-10-01 false Material and material thickness. 178.345-2 Section... HAZARDOUS MATERIALS SAFETY ADMINISTRATION, DEPARTMENT OF TRANSPORTATION (CONTINUED) SPECIFICATIONS FOR PACKAGINGS Specifications for Containers for Motor Vehicle Transportation § 178.345-2 Material and material...

49 CFR 178.345-2 - Material and material thickness.

Code of Federal Regulations, 2012 CFR

2012-10-01

... 49 Transportation 3 2012-10-01 2012-10-01 false Material and material thickness. 178.345-2 Section... HAZARDOUS MATERIALS SAFETY ADMINISTRATION, DEPARTMENT OF TRANSPORTATION (CONTINUED) SPECIFICATIONS FOR PACKAGINGS Specifications for Containers for Motor Vehicle Transportation § 178.345-2 Material and material...

49 CFR 178.345-2 - Material and material thickness.

Code of Federal Regulations, 2013 CFR

2013-10-01

... 49 Transportation 3 2013-10-01 2013-10-01 false Material and material thickness. 178.345-2 Section... HAZARDOUS MATERIALS SAFETY ADMINISTRATION, DEPARTMENT OF TRANSPORTATION (CONTINUED) SPECIFICATIONS FOR PACKAGINGS Specifications for Containers for Motor Vehicle Transportation § 178.345-2 Material and material...

NDE and DE of PWSCC Found in the J-Groove Weld of a Removed-From-Service Control Rod Drive Mechanism

DOE Office of Scientific and Technical Information (OSTI.GOV)

Cumblidge, Stephen E.; Doctor, Steven R.; Schuster, George J.

2008-01-01

Studies conducted at the Pacific Northwest National Laboratory (PNNL) in Richland, Washington focused on assessing the effectiveness of nondestructive examination (NDE) techniques for inspecting control rod drive mechanism (CRDM) nozzles and J-groove weldments. The primary objective of this work is to provide information to the United States Nuclear Regulatory Commission (US NRC) on the effectiveness of NDE methods as related to the in-service inspection of CRDM nozzles and J-groove weldments, and to enhance the knowledge base of primary water stress corrosion cracking (PWSCC) through destructive characterization of the CRDM assemblies. Two CRDM assemblies were removed from service, decontaminated, and thenmore » used in a series of laboratory NDE and DE measurements; this report addresses the following questions: 1) What did each NDE technique detect?, 2) What did each NDE technique miss?, 3) How accurately did each NDE technique characterize the detected flaws?, and finally 4) What were the basis for the NDE techniques performance? Two CRDM assemblies including the CRDM nozzle, the J-groove weld, buttering, and a portion of the ferritic head material were selected for this study. This paper focuses on a CRDM assembly that contained suspected PWSCC, based on in-service inspection data and through-wall leakage. The laboratory NDE measurements used to examine the CRDM assembly followed standard industry techniques for conducting in-service inspections of CRDM nozzles and the crown of the J-groove welds and buttering. These techniques included eddy current testing, time of flight diffraction ultrasound, and penetrant testing. In addition, other laboratory-based NDE methods were employed to conduct inspections of the CRDM assembly with particular emphasis on inspecting the J-groove weld and buttering. These techniques included volumetric ultrasonic inspection of the J-groove weld metal, visual testing via replicant material of the J-groove weld and high resolution photography of the J-groove weld crown and buttering. The results from these NDE studies were used to guide the development of the destructive characterization plan. The NDE studies found several crack-like indications. The NDE and DE studies determined that one of these was a through-weld radially-oriented PWSCC crack in the wetted surface of the J-groove weld, located at the transition point between the weld and the buttering. The crack was 6 mm long on the surface and quickly grew to 25 mm long at a depth of 8 mm, covering the length of the weld between the penetration tube and the carbon steel. The NDE studies found that only ET was able to detect the through-weld crack. The crack was oriented poorly for the ultrasonic testing, and was too tight for accurate PT or VT. The ET voltage response of the flaw was 30% that of a deep EDM notch. The DE performed on the crack consisted of slicing the crack into thin sections, polishing the sections, and then using optical and scanning electron microscopy (SEM) to characterize the crack. DE shows the crack was PWSCC and that it initiated on the wetted surface, grew and expanded through the weld metal, and exited into the annulus. The SEM examinations showed the crack followed the weld grain boundaries as it progressed through the weld. The crack was branched and discontinuous along its length.« less

Analysis of thick brain sections by obverse-reverse computer microscopy: application of a new, high clarity Golgi-Nissl stain.

PubMed

Glaser, E M; Van der Loos, H

1981-08-01

Exceptionally clear Golgi-Nissl sections of 300 micron thickness have been morphometrically studied by light microscopy using oil immersion objectives. The clarity results from a new variation of a staining procedure that combines Golgi and Nissl images in one section. A viewing technique has been developed that permits a histologic preparation to be examined from its obverse (or normally viewed) side and its reverse (or under) side. The technique was designed for use with a computer microscope but can be employed with any light microscope whose stage position can be measured within 100 micron. Sections thicker than 300 micron can be studied dependent on the working distance of the objective lens, provided that the clarity of the material permits it.

Free Vibrations of Nonthin Elliptic Cylindrical Shells of Variable Thickness

NASA Astrophysics Data System (ADS)

Grigorenko, A. Ya.; Efimova, T. L.; Korotkikh, Yu. A.

2017-11-01

The problem of the free vibrations of nonthin elliptic cylindrical shells of variable thickness under various boundary conditions is solved using the refined Timoshenko-Mindlin theory. To solve the problem, an effective numerical approach based on the spline-approximation and discrete-orthogonalization methods is used. The effect of the cross-sectional shape, thickness variation law, material properties, and boundary conditions on the natural frequency spectrum of the shells is analyzed.

Tests on thirteen navy type model propellers

NASA Technical Reports Server (NTRS)

Durand, W F

1927-01-01

The tests on these model propellers were undertaken for the purpose of determining the performance coefficients and characteristics for certain selected series of propellers of form and type as commonly used in recent navy designs. The first series includes seven propellers of pitch ratio varying by 0.10 to 1.10, the area, form of blade, thickness, etc., representing an arbitrary standard propeller which had shown good results. The second series covers changes in thickness of blade section, other things equal, and the third series, changes in blade area, other things equal. These models are all of 36-inch diameter. Propellers A to G form the series on pitch ratio, C, N. I. J the series on thickness of section, and K, M, C, L the series on area. (author)

Extended methods using thick-targets for nuclear reaction data of radioactive isotopes

NASA Astrophysics Data System (ADS)

Ebata, Shuichiro; Aikawa, Masayuki; Imai, Shotaro

2017-09-01

The nuclear transmutation is a technology to dispose of radioactive wastes. However, we do not have enough basic data for its developments, such as thick-target yields (TTY) and the interaction cross sections for radioactive material. We suggest two methods to estimate the TTY using inverse kinematics and to obtain the excitation function of the interaction cross sections which is named the thick-target transmission (T3) method. We deduce the energy-dependent conversion relation between the TTYs of the original system and its inverse kinematics, which can be replaced to a constant coefficient in the high energy region. Furthermore we show the usefulness of the T3 method to investigate the excitation function of the 12C + 27Al reaction in the simulation.

Thickness dependence of scattering cross-sections in quantitative scanning transmission electron microscopy.

PubMed

Martinez, G T; van den Bos, K H W; Alania, M; Nellist, P D; Van Aert, S

2018-04-01

In quantitative scanning transmission electron microscopy (STEM), scattering cross-sections have been shown to be very sensitive to the number of atoms in a column and its composition. They correspond to the integrated intensity over the atomic column and they outperform other measures. As compared to atomic column peak intensities, which saturate at a given thickness, scattering cross-sections increase monotonically. A study of the electron wave propagation is presented to explain the sensitivity of the scattering cross-sections. Based on the multislice algorithm, we analyse the wave propagation inside the crystal and its link to the scattered signal for the different probe positions contained in the scattering cross-section for detector collection in the low-, middle- and high-angle regimes. The influence to the signal from scattering of neighbouring columns is also discussed. Copyright © 2018 Elsevier B.V. All rights reserved.

Matrix Sublimation/Recrystallization for Imaging Proteins by Mass Spectrometry at High Spatial Resolution

PubMed Central

Yang, Junhai; Caprioli, Richard M.

2011-01-01

We have employed matrix deposition by sublimation for protein image analysis on tissue sections using a hydration/recrystallization process that produces high quality MALDI mass spectra and high spatial resolution ion images. We systematically investigated different washing protocols, the effect of tissue section thickness, the amount of sublimated matrix per unit area and different recrystallization conditions. The results show that an organic solvent rinse followed by ethanol/water rinses substantially increased sensitivity for the detection of proteins. Both the thickness of tissue section and amount of sinapinic acid sublimated per unit area have optimal ranges for maximal protein signal intensity. Ion images of mouse and rat brain sections at 50, 20 and 10 µm spatial resolution are presented and are correlated with H&E stained optical images. For targeted analysis, histology directed imaging can be performed using this protocol where MS analysis and H&E staining are performed on the same section. PMID:21639088

A Lifting Ball Valve for cryogenic fluid applications

NASA Astrophysics Data System (ADS)

Cardin, Joseph M.; Reinicke, Robert H.; Bruneau, Stephen D.

1993-11-01

Marotta Scientific Controls, Inc. has designed a Lifting Ball Valve (LBV) capable of both flow modulation and tight shutoff for cryogenic and other applications. The LBV features a thin-walled visor valving element that lifts off the seal with near axial motion before rotating completely out of the flow path. This is accomplished with a simple, robust mechanism that minimizes cost and weight. Conventional spherical rotating seats ar plagued by leakage due to 'scuffing' as the seal and seat slide against one another while opening. Cryogenic valves, which typically utilize plastic seals, are particularly susceptible to this type of damage. The seat in the LBV lifts off the seal without 'scuffing' making it immune to this failure mode. In addition, the LBV lifting mechanism is capable of applying the very high seating loads required to seal at cryogenic temperatures. These features make the LBV ideally suited for cryogenic valve applications. Another major feature of the LBV is the fact that the visor rotates completely out of the flow path. This allows for a smaller, lighter valve for a given flow capacity, especially for line sizes above one inch. The LBV is operated by a highly integrated 'wetted' DC brushless motor. The motor rotor is 'wetted' ion that it is immersed in the fluid. To ensure compatibility, the motor rotor is encased in a thin-walled CRES weldment. The motor stator is outside the fluid containment weldment and therefore is not in direct contact with the fluid. To preclude the potential for external leakage there are no static or dynamic seals or bellows across the pressure boundary. The power required to do the work of operating the valving mechanism is transmitted across the pressure boundary by electromagnetic interaction between the motor rotor and the stator. Commutation of the motor is accomplished using the output of a special 'wetted' resolver. This paper describes the design, operation, and element testing of the LBV.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wang, Yiyu; Kannan, Rangasayee; Li, Leijun, E-mail

Non-equilibrium microstructure of the heat-affected zone (HAZ) in the as-welded modified 9Cr–1Mo–V–Nb pipe steel (P91) weldment deposited by gas tungsten arc welding (GTAW) and flux core arc welding (FCAW) has been characterized by field-emission scanning electron microscope (FESEM) and electron backscatter diffraction (EBSD). The heterogeneous structures in the sub-layers of the as-welded HAZ are attributable to phase transformations caused by the welding thermal cycles and the local structure variations in the as-received base metal. Coarse-grained heat-affected zone (CGHAZ) has a prior austenite grain (PAG) size of 20 μm. Fine uniformly-distributed precipitates and a higher fraction of MX carbonitrides are observedmore » in the CGHAZ. Fine-grained heat-affected zone (FGHAZ) consists of the finest grains (1.22 μm measured by EBSD, 5 μm PAG size), coarse undissolved M{sub 23}C{sub 6} carbides within the PAG boundaries and fine nucleated M{sub 23}C{sub 6} particles within the martensite laths. Inter-critical heat-affected zone (ICHAZ) consists of partially austenitized grains and over-tempered martensite laths. EBSD kernel average misorientation (KAM) map in the FGHAZ close to the ICHAZ illustrates the greatest local strain variations with a moderate normalized KAM value of 0.92°. The majority (88.1%) of the matrix grains in the CGHAZ are classified as deformed grains by EBSD grain average misorientation (GAM) evaluation. The FGHAZ close to the ICHAZ has the most recrystallized grains with an area fraction of 14.4%. The highest density variation of precipitates within grains in the FGHAZ originates from the inhomogeneous chemistry in the base metal. - Highlights: •A comprehensive characterization of the as-welded HAZ of P91 weldment is conducted. •Structural features in the each layer of the HAZ are quantified by EBSD. •Structural heterogenities in HAZ are due to welding cycle and base metal structure. •FGHAZ contains the finest grain structure and largest precipitate density variation.« less

Grainstones and cementstone mounds: The Trogkofel summit section (Lower Permian, Carnic Alps, Austria).

NASA Astrophysics Data System (ADS)

Schaffhauser, M.; Sanders, D.; Krainer, K.

2009-04-01

In the Carnic Alps, Austria, an Artinskian succession 400 m thick of shallow-water bioclastic limestones and of mounds composed of ?Archaeolithophyllum, Archaeolithoporella and abundant fibrous cementstone (after former aragonite) records deposition along a "grainstone-dominated" platform margin. The section was taken along the route through the east-facing cliff of Trogkofel. The Trogkofel Limestone (Artinskian pro parte) is excellently exposed and preserved the most complete along this route, but no section has hitherto been logged. The total thickness of the Trogkofel Limestone probably is about 550 meters; the summit section comprises its upper 400 meters. The section consists mainly of shallow-water bioclastic limestones (grainstones, packstones, rudstones) intercalated with cementstone mounds. Both the bioclastic limestones and the mounds typically are thick-bedded to, more commonly, unbedded. Throughout the section, intervals a few tens of meters in thickness dominated by bioclastic limestones change vertically with intervals dominated by cementstone mounds. Up-section, no clear-cut trend with respect to prevalent facies, mean depositional water depth, and energy index is obvious. Furthermore, no lime-muddy, meter-scale peritidal cycles, and no teepee structures and no pisolite levels were identified; thin intervals of fenestral lime mudstones and/or of cryptmicrobially-laminated limestones are very rare. The bioclastic limestones commonly weather out unstratified, or show subhorizontal stratification or, more rarely, low-angle cross-stratification. In the upper 100 meters of section, grainstones to fine-grained rudstones rich in keystone vugs are prevalent. The cementstone mounds comprise intervals up to a few meters in thickness; the biogenic component is characterized by foliose crusts pertaining to ?Archaeolithophyllum hidensis and Archaeolithoporella, overgrown by Tubiphytes and fenestrate bryozoans. The ?Archaeolithophyllum-Archaeolithoporella crusts are overgrown by abundant, thick fringes and botryoids of fibrous cement that is interpreted as calcitized aragonite cement. In addition, brachiopods, crustose red algae, and a few solitary and colonial rugose corals are typical. By volume, the former aragonite cement comprises the majority of the mounds. Intrinsic pores within the cementstone fabrics typically are filled by micropeloidal grainstone and/or by lime mudstone. The Trogkofel Limestone is locally dolomitized. Replacement dolomites show a wide range of crystal shapes and textures, but overall comprise (a) finely-crystalline, limpid dolostone of xenotopic or hypidiotopic fabrics that broadly mimick the texture of replaced sediment and cements, (b) coarse-crystalline fabrics of hypidiotopic to idiotopic, limpid or optically zoned dolomite, and (c) replacement saddle dolomite. The Trogkofel Limestone is riddled by karstic dykes and caverns that are mainly filled by, both or either of, geopetally-laminated red lime mudstone, terrigenous red sandstones, or thick fringes of fibrous cement. In the karstic cavity fills, packages of convolute geopetal lamination and brecciated internal sediments (internal seismites) overlain by infills with non-convolute lamination, fracture of fibrous cements, and dykes filled by multi-phase fracture breccias record tectonism during or after deposition of the Trogkofel Limestone. The Trogkofel Limestone is capped by a truncation surface which, in turn, is overlain by an interval of extremely poorly sorted, thick-bedded breccias with a former matrix of lime mudstone ("Trogkofel Breccia"). Both the components and the matrix of the Trogkofel Breccia are dolomitized. We interpret the facies and facies architecture of the eastern cliff section of Trogkofel as succession from the seaward side of a "grainstone-dominated" platform margin with cementstone mounds. The lack of clear-cut vertical trends in prevalent facies suggests that the platform margin developed mainly by aggradation. The timing and processes of replacement dolomitization(s) to date are poorly constrained. The presence of saddle dolomite nevertheless indicates passage of dolomitizing fluids of more than 90-100°C.

46 CFR 56.85-10 - Preheating.

Code of Federal Regulations, 2012 CFR

2012-10-01

.... (9) Heating rate for furnace, gas, electric resistance, and other surface heating methods must not... thickness in inches for thickness over 2 inches. (10) Heating route for induction heating must not exceed... still air. When furnace cooling is used, the pipe sections must be cooled in the furnace to 1000 °F and...

46 CFR 56.85-10 - Preheating.

Code of Federal Regulations, 2010 CFR

2010-10-01

.... (9) Heating rate for furnace, gas, electric resistance, and other surface heating methods must not... thickness in inches for thickness over 2 inches. (10) Heating route for induction heating must not exceed... still air. When furnace cooling is used, the pipe sections must be cooled in the furnace to 1000 °F and...

46 CFR 56.85-10 - Preheating.

Code of Federal Regulations, 2014 CFR

2014-10-01

.... (9) Heating rate for furnace, gas, electric resistance, and other surface heating methods must not... thickness in inches for thickness over 2 inches. (10) Heating route for induction heating must not exceed... still air. When furnace cooling is used, the pipe sections must be cooled in the furnace to 1000 °F and...

46 CFR 56.85-10 - Preheating.

Code of Federal Regulations, 2013 CFR

2013-10-01

.... (9) Heating rate for furnace, gas, electric resistance, and other surface heating methods must not... thickness in inches for thickness over 2 inches. (10) Heating route for induction heating must not exceed... still air. When furnace cooling is used, the pipe sections must be cooled in the furnace to 1000 °F and...

46 CFR 56.85-10 - Preheating.

Code of Federal Regulations, 2011 CFR

2011-10-01

.... (9) Heating rate for furnace, gas, electric resistance, and other surface heating methods must not... thickness in inches for thickness over 2 inches. (10) Heating route for induction heating must not exceed... still air. When furnace cooling is used, the pipe sections must be cooled in the furnace to 1000 °F and...

Application of the Program Profile for the Design of Low-Speed, Low- Observable Configuration Airfoils

DTIC Science & Technology

1992-12-01

112 61 . Airfoil T503 - t/c = 3.79% .... ........... .. 113 62. Airfoil T503 Leading-Edge - t/c = 3.79% ..... ... 114 63. Pressure...points on C unit circle, 6 slope of airfoil surface near trailing edge 61 boundary-layer displacement thickness 62 boundary-layer momentum thickness 63...equivalent thickness NACA 4-digit airfoils . 4 II. Theory Potential-Flow Design Method This section will overview the basic theory used in PROFILE. Eppler

Anisotropic fibrous thermal insulator of relatively thick cross section and method for making same

DOEpatents

Reynolds, Carl D.; Ardary, Zane L.

1979-01-01

The present invention is directed to an anisotropic thermal insulator formed of carbon-bonded organic or inorganic fibers and having a thickness or cross section greater than about 3 centimeters. Delaminations and deleterious internal stresses generated during binder curing and carbonizing operations employed in the fabrication of thick fibrous insulation of thicknesses greater than 3 centimeters are essentially obviated by the method of the present invention. A slurry of fibers, thermosetting resin binder and water is vacuum molded into the selected insulator configuration with the total thickness of the molded slurry being less than about 3 centimeters, the binder is thermoset to join the fibers together at their nexaes, and then the binder is carbonized to form the carbon bond. A second slurry of the fibers, binder and water is then applied over the carbonized body with the vacuum molding, binder thermosetting and carbonizing steps being repeated to form a layered insulator with the binder providing a carbon bond between the layers. The molding, thermosetting and carbonizing steps may be repeated with additional slurries until the thermal insulator is of the desired final thickness. An additional feature of the present invention is provided by incorporating opacifying materials in any of the desired layers so as to provide different insulating properties at various temperatures. Concentration and/or type of additive can be varied from layer-to-layer.

Congo red staining on 1 micron de-plasticized sections for detection of lesions in Alzheimer's disease and related disorders.

PubMed

Snow, A D; Mar, H; Nochlin, D; Wight, T N

1989-01-01

Neuritic plaques (NPs), neurofibrillary tangles (NFTs) and congophilic angiopathy (CA), the three characteristic lesions in Alzheimer's disease, are easily detected in paraffin sections using light microscopy and specific staining methods including Congo red and Thioflavin S. Identification of these lesions in plastic thick sections (1 micron) is more tedious and relies essentially on morphological criteria. This causes investigators to subsequently analyze large numbers of thin sections under the electron microscope. Since many researchers use electron microscopy for various aspects of Alzheimer's disease and related research, it would be advantageous to have a rapid method enabling the investigator to quickly and reliably identify in thick sections the characteristic NPs, NFTs and/or CA, which can then be used for further analysis at the ultrastructural level. In this context, the present study describes a dependable technique for identifying NPs, NFTs and/or CA in Alzheimer's disease and related disorders and involves Congo red staining on one micron sections after plastic removal.

Longitudinal and cross-sectional structural magnetic resonance imaging correlates of AV-1451 uptake.

PubMed

Das, Sandhitsu R; Xie, Long; Wisse, Laura E M; Ittyerah, Ranjit; Tustison, Nicholas J; Dickerson, Bradford C; Yushkevich, Paul A; Wolk, David A

2018-06-01

We examined the relationship between in vivo estimates of tau deposition as measured by 18 F-AV-1451 tau positron emission tomography imaging and cross-sectional cortical thickness, as well as rates of antecedent cortical thinning measured from magnetic resonance imaging in individuals with and without evidence of cerebral amyloid in 63 participants from the Alzheimer's Disease Neuroimaging Initiative study, including 32 cognitively normal individuals (mean age 74 years), 27 patients with mild cognitive impairment (mean age 76.8 years), and 4 patients diagnosed with Alzheimer's disease (mean age 80 years). We hypothesized that structural measures would correlate with 18 F-AV-1451 in a spatially local manner and that this correlation would be stronger for longitudinal compared to cross-sectional measures of cortical thickness and in those with cerebral amyloid versus those without. Cross-sectional and longitudinal estimates of voxelwise atrophy were made from whole brain maps of cortical thickness and rates of thickness change. In amyloid-β-positive individuals, the correlation of voxelwise atrophy across the whole brain with a summary measure of medial temporal lobe (MTL) 18 F-AV-1451 uptake demonstrated strong local correlations in the MTL with longitudinal atrophy that was weaker in cross-sectional analysis. Similar effects were seen in correlations between 31 bilateral cortical regions of interest. In addition, several nonlocal correlations between atrophy and 18 F-AV-1451 uptake were observed, including association between MTL atrophy and 18 F-AV-1451 uptake in parietal lobe regions of interest such as the precuneus. Amyloid-β-negative individuals only showed weaker correlations in data uncorrected for multiple comparisons. While these data replicate previous reports of associations between 18 F-AV-1451 uptake and cross-sectional structural measures, the current results demonstrate a strong relationship with longitudinal measures of atrophy. These data support the notion that in vivo measures of tau pathology are tightly linked to the rate of neurodegenerative change. Copyright © 2018 Elsevier Inc. All rights reserved.

Dual-Beam Sample Preparation | Materials Science | NREL

Science.gov Websites

images showing cutting of trenches to remove a wafer section and transferring that section to a grid post section and transferring that section to a grid post. Here the wafer section is lifted out and seen from , extracted from the wafer then transferred and welded to a TEM grid post. Final thinning down to a thickness

Research on the Cross Section Precision of High-strength Steel Tube with Rectangular Section in Rotary Draw Bending

NASA Astrophysics Data System (ADS)

Yang, Hongliang; Zhao, Hao; Xing, Zhongwen

2017-11-01

For the demand of energy conservation and security improvement, high-strength steel (HSS) is increasingly being used to produce safety related automotive components. However, cross-section distortion occurs easily in bending of HSS tube with rectangular section (RS), affecting the forming precision. HSS BR1500HS tube by rotary draw bending is taken as the study object and a description method of cross-section distortion is proposed in this paper. The influence on cross-section precision of geometric parameters including cross-section position, thickness of tube, bend radius etc. are studied by experiment. Besides, simulation of the rotary draw bending of HSS tube with rectangular section by ABAQUS are carried out and compared to the experiment. The results by simulation agree well with the experiment and show that the cross-section is approximately trapezoidal after distortion; the maximum of distortion exists at 45 ∼ 60° of the bending direction; and the absolute and relative distortion values increase with the decreasing of tube thickness or bending radius. Therefore, the results can provide a reference for the design of geometric parameters of HSS tube with rectangular section in rotary draw bending.

Multi-depth valved microfluidics for biofilm segmentation

NASA Astrophysics Data System (ADS)

Meyer, M. T.; Subramanian, S.; Kim, Y. W.; Ben-Yoav, H.; Gnerlich, M.; Gerasopoulos, K.; Bentley, W. E.; Ghodssi, R.

2015-09-01

Bacterial biofilms present a societal challenge, as they occur in the majority of infections but are highly resistant to both immune mechanisms and traditional antibiotics. In the pursuit of better understanding biofilm biology for developing new treatments, there is a need for streamlined, controlled platforms for biofilm growth and evaluation. We leverage advantages of microfluidics to develop a system in which biofilms are formed and sectioned, allowing parallel assays on multiple sections of one biofilm. A microfluidic testbed with multiple depth profiles was developed to accommodate biofilm growth and sectioning by hydraulically actuated valves. In realization of the platform, a novel fabrication technique was developed for creating multi-depth microfluidic molds using sequentially patterned photoresist separated and passivated by conformal coatings using atomic layer deposition. Biofilm thickness variation within three separately tested devices was less than 13% of the average thickness in each device, while variation between devices was 23% of the average thickness. In a demonstration of parallel experiments performed on one biofilm within one device, integrated valves were used to trisect the uniform biofilms with one section maintained as a control, and two sections exposed to different concentrations of sodium dodecyl sulfate. The technology presented here for multi-depth microchannel fabrication can be used to create a host of microfluidic devices with diverse architectures. While this work focuses on one application of such a device in biofilm sectioning for parallel experimentation, the tailored architectures enabled by the fabrication technology can be used to create devices that provide new biological information.

Stagnancy of the pygmy dipole resonance

NASA Astrophysics Data System (ADS)

Sun, Xu-Wei; Chen, Jing; Lu, Ding-Hui

2018-01-01

The pygmy dipole resonance (PDR) of nickel isotopes is studied using the deformed random phase approximation method. The isoscalar character of the pygmy resonance is confirmed, and the correlation between the pygmy resonance and neutron skin thickness is discussed. Our investigation shows a linear correlation between PDR integral cross section and neutron skin thickness when the excess neutrons lie in pf orbits, with a correlation rate of about 0.27 fm-1. However, in more neutron-rich nickel isotopes, the growth of the pygmy dipole resonance is stagnant. Although the neutron skin thickness increases, the whole skin is not active. There is an inertial part in the nuclei 70-78Ni which does not participate in the pygmy resonance actively and as a result, contributes little to the photo-absorption cross section. Supported by National Science Foundation of China

Examination of the influence of coatings on thin superalloy sections. Volume 2: Detailed procedures and data. [corrosion resistance

NASA Technical Reports Server (NTRS)

Kaufman, M.

1974-01-01

The effects of an aluminide coating, Codep B-1, and of section thickness were investigated on two cast nickel base superalloys, Rene 80 and Rene 120. Cast section thicknesses ranged from 0.038 cm to 0.15 cm. Simulated engine exposures for 1000 hours at 899C or 982C in a jet fuel burner rig with cyclic air cooling were studied, as were the effects of surface machining before coating and re-machining and re-coating after exposures. The properties evaluated included tensile at room temperature., 871C and 982C, stress rupture at 760C, 871C, 982C and 1093C, high cycle mechanical fatigue at room temperature., and thermal fatigue with a 1093C peak temperature. Thin sections had tensile strengths similar to standard size bars up to 871C and lower strengths at 982C and above, with equivalent elongation, and stress rupture life was lower for thin sections at all test conditions. The aluminide coating lowered tensile and rupture strengths up to 871C, with greater effects on thinner specimens. Elevated temperature exposure lowered tensile and rupture strengths of thinner specimens at the lower test temperatures. Surface machining had little effect on properties, but re-machining after exposure reduced thickness and increased metallurgical changes enough to lower properties at most test conditions.

Sedimentary processes and architecture of Upper Cretaceous deep-sea channel deposits: a case from the Skole Nappe, Polish Outer Carpathians

NASA Astrophysics Data System (ADS)

Łapcik, Piotr

2018-02-01

Deep-sea channels are one of the architectonic elements, forming the main conduits for sand and gravel material in the turbidite depositional systems. Deep-sea channel facies are mostly represented by stacking of thick-bedded massive sandstones with abundant coarse-grained material, ripped-up clasts, amalgamation and large scale erosional structures. The Manasterz Quarry of the Ropianka Formation (Upper Cretaceous, Skole Nappe, Carpathians) contains a succession of at least 31 m of thick-bedded high-density turbidites alternated with clast-rich sandy debrites, which are interpreted as axial deposits of a deep-sea channel. The section studied includes 5 or 6 storeys with debrite basal lag deposits covered by amalgamated turbidite fills. The thickness of particular storeys varies from 2.5 to 13 m. Vertical stacking of similar facies through the whole thickness of the section suggest a hierarchically higher channel-fill or a channel complex set, with an aggradation rate higher than its lateral migration. Such channel axis facies cannot aggrade without simultaneous aggradation of levee confinement, which was distinguished in an associated section located to the NW from the Manasterz Quarry. Lateral offset of channel axis facies into channel margin or channel levee facies is estimated at less than 800 m. The Manasterz Quarry section represents mostly the filling and amalgamation stage of channel formation. The described channel architectural elements of the Ropianka Formation are located within the so-called Łańcut Channel Zone, which was previously thought to be Oligocene but may have been present already in the Late Cretaceous.

Cortical Thickness and Anxiety Symptoms Among Cognitively Normal Elderly Persons: The Mayo Clinic Study of Aging.

PubMed

Pink, Anna; Przybelski, Scott A; Krell-Roesch, Janina; Stokin, Gorazd B; Roberts, Rosebud O; Mielke, Michelle M; Spangehl, Kathleen A; Knopman, David S; Jack, Clifford R; Petersen, Ronald C; Geda, Yonas E

2017-01-01

The authors conducted a cross-sectional study to investigate the association between anxiety symptoms and cortical thickness, as well as amygdalar volume. A total of 1,505 cognitively normal participants, aged ≥70 years, were recruited from the Mayo Clinic Study of Aging in Olmsted County, Minnesota, on whom Beck Anxiety Inventory and 3T brain MRI data were available. Even though the effect sizes were small in this community-dwelling group of participants, anxiety symptoms were associated with reduced global cortical thickness and reduced thickness within the frontal and temporal cortex. However, after additionally adjusting for comorbid depressive symptoms, only the association between anxiety symptoms and reduced insular thickness remained significant.

Damage assessment and residual compression strength of thick composite plates with through-the-thickness reinforcements

NASA Technical Reports Server (NTRS)

Smith, Barry T.

1990-01-01

Damage in composite materials was studied with through-the-thickness reinforcements. As a first step it was necessary to develop new ultrasonic imaging technology to better assess internal damage of the composite. A useful ultrasonic imaging technique was successfully developed to assess the internal damage of composite panels. The ultrasonic technique accurately determines the size of the internal damage. It was found that the ultrasonic imaging technique was better able to assess the damage in a composite panel with through-the-thickness reinforcements than by destructively sectioning the specimen and visual inspection under a microscope. Five composite compression-after-impact panels were tested. The compression-after-impact strength of the panels with the through-the-thickness reinforcements was almost twice that of the comparable panel without through-the-thickness reinforcement.

Confocal microscopy of thick tissue sections: 3D visualizaiton of rat kidney glomeruli

EPA Science Inventory

Confocal laser scanning microscopy (CLSM) as a technique capable of generating serial sections of whole-mount tissue and then reassembling the computer-acquired images as a virtual 3-dimentional structure. In many ways CLSM offers an alternative to traditional sectioning approac...

Confocal Microscopy of thick tissue sections: 3D Visualization of rat kidney glomeruli

EPA Science Inventory

Confocal laser scanning microscopy (CLSM) as a technique capable of generating serial sections of whole-mount tissue and then reassembling the computer-acquired images as a virtual 3-dimentional structure. In many ways CLSM offers an alternative to traditional sectioning approac...

Characterisation of metallic glass incorporated Zircaloy-2 weldments

NASA Astrophysics Data System (ADS)

Mishra, S.; Savalia, R. T.; Bhanumurthy, K.; Dey, G. K.; Banerjee, S.

1995-12-01

In this study the effect of incorporation of Zr based Fe and Ni bearing metallic glass in spot welds in Zircaloy components has been examined. A comparison of strength and microstructure of the welded joint with and without glass has been carried out. The welded joint with metallic glass has been found to be stronger than the one without metallic glass. The microstructure of the welded region with metallic glass has been found to comprise a large region having martensite. This large martensitic region has also been found to have considerable amount of excess solute (Fe, Ni). The higher strength of the weld with metallic glass seems to originate due to solid solution strengthening, small grain size and the presence of martensitic structure over a large region.

Study of austenitic stainless steel welded with low alloy steel filler metal. [tensile and impact strength tests

NASA Technical Reports Server (NTRS)

Burns, F. A.; Dyke, R. A., Jr.

1979-01-01

The tensile and impact strength properties of 316L stainless steel plate welded with low alloy steel filler metal were determined. Tests were conducted at room temperature and -100 F on standard test specimens machined from as-welded panels of various chemical compositions. No significant differences were found as the result of variations in percentage chemical composition on the impact and tensile test results. The weldments containing lower chromium and nickel as the result of dilution of parent metal from the use of the low alloy steel filler metal corroded more severely in a marine environment. The use of a protective finish, i.e., a nitrile-based paint containing aluminum powder, prevented the corrosive attack.

Hot cracking susceptibility of fillers 52 and 82 in alloy 690 welding

NASA Astrophysics Data System (ADS)

Wu, Weite; Tsai, C. H.

1999-02-01

The hot cracking susceptibility of fillers 52 and 82 in a alloy 690 weldment is analyzed by the Varestraint test. Weld characteristics, microstructure, hardness distribution, and thermal analysis of the two filler metals are also examined. The weld metal of both fillers develops an extremely dense oxide layer. A stainless steel brush cannot remove the oxide layer, and a grinder may be needed between weld passes to assure a sound weld. Differential temperature analysis (DTA) shows that filler 82 has a lower melting point and a wider melting/solidification temperature differential (Δ T). These characteristics correlate with greater hot cracking susceptibility of filler 82 than 52 in Varestraint tests. The hot cracks are intergranular and are caused by elements segregating in grain boundies.

Features of residual stresses in duplex stainless steel butt welds

NASA Astrophysics Data System (ADS)

Um, Tae-Hwan; Lee, Chin-Hyung; Chang, Kyong-Ho; Nguyen Van Do, Vuong

2018-04-01

Duplex stainless steel finds increasing use as an alternative to austenitic stainless steel, particularly where chloride or sulphide stress corrosion cracking is of primary concern, due to the excellent combination of strength and corrosion resistance. During welding, duplex stainless steel does not create the same magnitude or distribution of weld-induced residual stresses as those in welded austenitic stainless steel due to the different physical and mechanical properties between them. In this work, an experimental study on the residual stresses in butt-welded duplex stainless steel is performed utilizing the layering technique to investigate the characteristics of residual stresses in the weldment. Three-dimensional thermos-mechanical-metallurgical finite element analysis is also performed to confirm the residual stress measurements.

Microstructure, Properties and Weldability of Duplex Stainless Steel 2101

NASA Astrophysics Data System (ADS)

Ma, Li; Hu, Shengsun; Shen, Junqi

2017-01-01

The continuous development of duplex stainless steels (DSSs) is due to their excellent corrosion resistance in aggressive environments and their mechanical strength, which is usually twice of conventional austenitic stainless steels (ASSs). In this paper, a designed lean duplex stainless steel 2101, with the alloy design of reduced nickel content and increased additions of manganese and nitrogen, is studied by being partly compared with typical ASS 304L steels. The microstructure, mechanical properties, impact toughness, corrosion resistance and weldability of the designed DSS 2101 were conducted. The results demonstrated that both 2101 steel and its weldment show excellent mechanical properties, impact toughness and corrosion resistance, so DSS 2101 exhibits good comprehensive properties and can be used to replace 304L in numerous applications.

Optimization of Performance of Arc Welding Using Fluxes in Welded Ship Structures from HY-100 and HY-130 KPSI.

DTIC Science & Technology

1981-09-01

production and formulation for several decades. NMgO + NCaO + NMnO + NFeO + NAI 20 3Basicity = NSiO 2 + NTi0 2 + NZr0 2 + NA1 203 This differs from the widely...20 3 100 (CaO-SiO, )(40) slag CaO/SiO 2 0.15 none 2600 NCaO /NSiO2 0.17 8% FeSi 1900 16% FeSi 1700 32% FeSi 1400 52 I Table 8 (continued). Islag Ca0...SiO~e .79 none 1200 NCaO /NSiOz .84 2% FeSi 1000 4% FeSi 900 16% FeSi 500 32% FeSi 500 Mechanical Property Tests Mechanical property weldments were

Corrosion behavior of stainless steel weldments in physiological solutions

NASA Astrophysics Data System (ADS)

Farooq, A.; Azam, M.; Deen, K. M.

2018-01-01

In this study corrosion behavior of TIG welded 316L stainless steel plates in simulated biological solutions is investigated. The mechanical testing results showed slight decrease in ductility after welding and the fracture surface represented mixed cleavage and inclusions containing dimple structure. The heat affected and weld zone (WZ) demonstrated higher corrosion potential and relatively large pitting tendency than base metal (BM) in both Hank’s and Ringer’s solution. The formation of delta (δ) ferrite in the heat affected and WZ decreased the corrosion resistance as confirmed from potentiodynamic Tafel scans. The decrease in pitting resistance and lower protection tendency of the WZ compared to BM and heat affected zone was also quantified from the cyclic polarization trends.

Handling Heavenly Jewels - 35 Years of Antarctic Meteorite Processing at Johnson Space Center

NASA Technical Reports Server (NTRS)

Satterwhite, C. E.; McBridge, K. M.; Harrington, R.; Schwarz, C. M.

2011-01-01

The ANSMET program began in 1976, and since that time more than 18,000 meteorites have been processed in the Meteorite Processing Lab at Johnson Space Center in Houston, TX[1]. The meteorites are collected and returned to JSC on a freezer truck and remain frozen until they are initially processed. Initial Processing of Meteorites: Initial processing involves drying the meteorites in a nitrogen glove box for 24 to 48 hours, photographing, measuring, weighing and writing a description of the interior and exterior. The meteorite is broken and a representative sample is sent to the Smithsonian Institution for classification. Newsletter & Requests: Once initial processing has been complete and the meteorites have been classified, the information is published in the Antarctic Meteorite Newsletter[2,3]. The newsletter is published twice yearly and is sent electronically to researchers around the world and is also available on line. Researchers are asked to fill out a request form and submit it to the Meteorite Working Group secretary. All sample requests will be reviewed by either the meteorite curator or the Meteorite Working Group de-pending on the type of meteorite and the research being conducted. Processing for Sample Requests: In the meteorite processing lab, meteorite samples are prepared several different ways. Most samples are prepared as chips obtained by use of stainless steel chisels in a chipping bowl or rock splitter. In special situations where a researcher needs a slab the meteorite samples can be bandsawed in a dry nitrogen glove box with a diamond blade, no liquids are ever introduced into the cabinet. The last type of sample preparation is thin/thick sections. The meteorite thin section lab at JSC can prepare standard 30-micron thin sections, thick sections of variable thickness (100 to 200 microns), or demountable sections using superglue. Information for researchers: It is important that re-searchers fill the sample request form completely, in order to make sure the meteorite is processed correctly[4]. Re-searchers should list any special requirements on the form, i.e. packaging of samples (poly vs. stainless), thick sections and thickness needed, superglue needed, interior chips, exterior chips, fusion crust, contamination issues, all concerns should be listed so processing can be done accurately and any concerns the researcher has can be addressed be-fore the meteorites are broken.

Characterization of essential oil distribution in the root cross-section of Valeriana officinalis L. s.l. by using histological imaging techniques.

PubMed

Penzkofer, Michael; Baron, Andrea; Naumann, Annette; Krähmer, Andrea; Schulz, Hartwig; Heuberger, Heidi

2018-01-01

The essential oil is an important compound of the root and rhizome of medicinally used valerian ( Valeriana officinalis L. s.l.), with a stated minimum content in the European pharmacopoeia. The essential oil is located in droplets, of which the position and distribution in the total root cross-section of different valerian varieties, root thicknesses and root horizons are determined in this study using an adapted fluorescence-microscopy and automatic imaging analysis method. The study was initiated by the following facts:A probable negative correlation between essential oil content and root thickness in selected single plants (elites), observed during the breeding of coarsely rooted valerian with high oil content.Higher essential oil content after careful hand-harvest and processing of the roots. In preliminary tests, the existence of oil containing droplets in the outer and inner regions of the valerian roots was confirmed by histological techniques and light-microscopy, as well as Fourier-transform infrared spectroscopy. Based on this, fluorescence-microscopy followed by image analysis of entire root cross-sections, showed that a large number of oil droplets (on average 43% of total oil droplets) are located close to the root surface. The remaining oil droplets are located in the inner regions (parenchyma) and showed varying density gradients from the inner to the outer regions depending on genotype, root thickness and harvesting depth. Fluorescence-microscopy is suitable to evaluate prevalence and distribution of essential oil droplets of valerian in entire root cross-sections. The oil droplet density gradient varies among genotypes. Genotypes with a linear rather than an exponential increase of oil droplet density from the inner to the outer parenchyma can be chosen for better stability during post-harvest processing. The negative correlation of essential oil content and root thickness as observed in our breeding material can be counteracted through a selection towards generally high oil droplet density levels, and large oil droplet sizes independent of root thickness.

A novel protocol for generating intact, whole-head spider cephalothorax tissue sections.

PubMed

Long, Skye M

2018-04-01

The diversity of spider behavior and sensory systems provides an excellent opportunity for comparative studies of the relationship between the brain and behavior. However, the morphology of spiders poses a challenge for histologists since the spider cephalothorax contains heterogeneous tissues and has both tough external and internal sclerotized regions. Unlike the heads of insects, the cephalothorax is highly pressurized, which can cause tissues to shift during processing and can reduce tissue cohesion in thick sections. This work describes a novel protocol for producing thick whole-head sections for morphological study by softening the exoskeleton and stabilizing friable tissue, without freezing or dehydration. It also presents an effective whole-head DiI staining method that uses minimal dehydration and highlights neural structures.

The transonic multi-foil Augmentor-Wing

NASA Technical Reports Server (NTRS)

Farbridge, J. E.; Smith, R. C.

1977-01-01

The paper describes the development of a transonic blown multi-foil Augmentor-Wing airfoil section that has a thickness/chord (t/c) value of 0.18. In comparison with an unblown single-foil supercritical section of the same overall t/c the new multi-foil section is characterized by an increased drag rise Mach number, increased buffet boundaries, and a reduction in 'effective' drag due to blowing. Potential advantages of the Augmentor-Wing are considered and the testing of three high-speed models in a trisonic pressurized wind tunnel (possessing a two-dimensional transonic insert) is discussed. The data indicate that a very thick wing is feasible since separations toward the rear of the main foil can be controlled both by shroud location and augmentor blowing.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Thangadurai, P.; Lumelsky, Yulia; Silverstein, Michael S.

Transmission electron microscopy (TEM) cross-section specimens of PMMA in contact with gold and Si were prepared by focused ion beam (FIB) and compared with plan-view PMMA specimens prepared by a dip-coating technique. The specimens were characterized by TEM and electron energy loss spectroscopy (EELS). In the cross-section specimens, the thin films of PMMA were located in a Si-PMMA-Au multilayer. Different thicknesses of PMMA films were spin-coated on the Si substrates. The thickness of the TEM specimens prepared by FIB was estimated using EELS to be 0.65 of the plasmon mean-free-path. Along the PMMA-Au interface, Au particle diffusion into the PMMAmore » was observed, and the size of the Au particles was in the range of 2-4 nm. Dip-coating of PMMA directly on Cu TEM grids resulted in thin specimens with a granular morphology, with a thickness of 0.58 of the plasmon mean-free-path. The dip-coated specimens were free from ion milling induced artifacts, and thus serve as control specimens for comparison with the cross-sectioned specimens prepared by FIB.« less

Self-heating forecasting for thick laminate specimens in fatigue

NASA Astrophysics Data System (ADS)

Lahuerta, F.; Westphal, T.; Nijssen, R. P. L.

2014-12-01

Thick laminate sections can be found from the tip to the root in most common wind turbine blade designs. Obtaining accurate and reliable design data for thick laminates is subject of investigations, which include experiments on thick laminate coupons. Due to the poor thermal conductivity properties of composites and the material self-heating that occurs during the fatigue loading, high temperature gradients may appear through the laminate thickness. In the case of thick laminates in high load regimes, the core temperature might influence the mechanical properties, leading to premature failures. In the present work a method to forecast the self-heating of thick laminates in fatigue loading is presented. The mechanical loading is related with the laminate self-heating, via the cyclic strain energy and the energy loss ratio. Based on this internal volumetric heat load a thermal model is built and solved to obtain the temperature distribution in the transient state. Based on experimental measurements of the energy loss factor for 10mm thick coupons, the method is described and the resulting predictions are compared with experimental surface temperature measurements on 10 and 30mm UD thick laminate specimens.

Turbine airfoil having outboard and inboard sections

DOEpatents

Mazzola, Stefan; Marra, John J

2015-03-17

A turbine airfoil usable in a turbine engine and formed from at least an outboard section and an inboard section such that an inner end of the outboard section is attached to an outer end of the inboard section. The outboard section may be configured to provide a tip having adequate thickness and may extend radially inward from the tip with a generally constant cross-sectional area. The inboard section may be configured with a tapered cross-sectional area to support the outboard section.

Development of Comprehensive Low-Volume Pavement Design

DOT National Transportation Integrated Search

2000-07-01

Historically, "low-volume" pavements (less than 500 ADT) in Arkansas were typically constructed using a "standard" section, i.e. a double surface treatment over a specified thickness of granular base. Subsequent analysis indicated these sections were...

78 FR 76035 - Airworthiness Directives; Maule Aerospace Technology, Inc. Airplanes

Federal Register 2010, 2011, 2012, 2013, 2014

2013-12-16

... precision machined step wedge made of 4340 steel (or similar steel with equivalent sound velocity) or at... unless an alternative instrument calibration procedure is used to set the sound velocity. 6. Obtain a... reflection of the thick section. If the digital display does not agree with the thickest thickness, follow...

16 CFR 1201.4 - Test procedures.

Code of Federal Regulations, 2011 CFR

2011-01-01

... (but are not limited to): Nominal thickness or thicknesses, method of manufacture (in appropriate cases... rigidity. (ii) The structural framing shall be welded or securely bolted at the corners and braced by one... figure 5 on this section. The bag shall be filled with No. 71/2 chilled lead shot to a total weight of...

16 CFR § 1201.4 - Test procedures.

Code of Federal Regulations, 2013 CFR

2013-01-01

... (but are not limited to): Nominal thickness or thicknesses, method of manufacture (in appropriate cases... rigidity. (ii) The structural framing shall be welded or securely bolted at the corners and braced by one... figure 5 on this section. The bag shall be filled with No. 71/2 chilled lead shot to a total weight of...

16 CFR 1201.4 - Test procedures.

Code of Federal Regulations, 2014 CFR

2014-01-01

... (but are not limited to): Nominal thickness or thicknesses, method of manufacture (in appropriate cases... rigidity. (ii) The structural framing shall be welded or securely bolted at the corners and braced by one... figure 5 on this section. The bag shall be filled with No. 71/2 chilled lead shot to a total weight of...

DYNAMIC PROPERTIES OF SHOCK LOADED THIN URANIUM FOILS

DOE Office of Scientific and Technical Information (OSTI.GOV)

Robbins, D. L.; Kelly, A. M.; Alexander, D. J.

A series of spall experiments has been completed with thin depleted uranium targets, nominally 0.1 mm thick. The first set of uranium spall targets was cut and ground to final thickness from electro-refined, high-purity, cast uranium. The second set was rolled to final thickness from low purity uranium. The impactors for these experiments were laser-launched 0.05-mm thick copper flyers, 3 mm in diameter. Laser energies were varied to yield a range of flyer impact velocities. This resulted in varying degrees of damage to the uranium spall targets, from deformation to complete spall or separation at the higher velocities. Dynamic measurementsmore » of the uranium target free surface velocities were obtained with dual velocity interferometers. Uranium targets were recovered and sectioned after testing. Free surface velocity profiles were similar for the two types of uranium, but spall strengths (estimated from the magnitude of the pull-back signal) are higher for the high-purity cast uranium. Velocity profiles and microstructural evidence of spall from the sectioned uranium targets are presented.« less

Microstructural Characteristics and Mechanical Properties of Friction Stir Welded Thick 5083 Aluminum Alloy

NASA Astrophysics Data System (ADS)

Imam, Murshid; Sun, Yufeng; Fujii, Hidetoshi; Ma, Ninshu; Tsutsumi, Seiichiro; Murakawa, Hidekazu

2017-01-01

Joining thick sections of aluminum alloys by friction stir welding (FSW) in a single pass needs to overcome many challenges before it comes to full-scale industrial use. Important parameters controlling the structure-properties relationships both across weld cross-section and through thickness direction were investigated through mechanical testing, electron backscatter diffraction technique, transmission electron microscopy, and occurrence of serrated plastic flow. The evolution of the properties in the weld cross-section shows that the presence of undissolved and fragmented Al_6MnFe particles cause discrepancies in establishing the Hall-Petch relationship, and derive the strengthening from the Orowan strengthening mechanism. A `stop action' friction stir weld has been prepared to understand the role of geometrical features of the tool probe in the development of the final microstructure after complete weld. Sectioning through the `stop action' weld with the probe in situ displays the individual effect of thread and flat on the grain structure formation. The material at the thread surface experiences more severe deformation than the material at flat surface. Both the high-angle boundaries and mean grain size are found to be higher at the thread surface. The strain hardening capacity, stress serration amplitude, and frequency are observed to be higher in the stir zone than other weld regions.

Suspended-Bed Reactor preliminary design, /sup 233/U--/sup 232/Th cycle. Final report (revised)

DOE Office of Scientific and Technical Information (OSTI.GOV)

Karam, R.A.; Alapour, A.; Lee, C.C.

1977-11-01

The preliminary design Suspended-Bed Reactor is described. Coated particles about 2 mm in diameter are used as the fuel. The coatings consist of three layers: (1) low density pyrolytic graphite, 70 ..mu.. thick, (2) silicon carbide pressure vessel, 30 ..mu.. thick, and (3) ZrC layer, 50 ..mu.. thick, to protect the pressure vessel from moisture and oxygen. The fuel kernel can be either uranium-thorium dicarbide or metal. The coated particles are suspended by helium gas (coolant) in a cluster of pressurized tubes. The upward flow of helium fluidizes the coated particles. As the flow rate increases, the bed of particlesmore » is lifted upward to the core section. The particles are restrained at the upper end of the core by a suitable screen. The overall particle density in the core is just enough for criticality condition. Should the helium flow cease, the bed in the core section will collapse, and the particles will flow downward into the section where the increased physical spacings among the tubes brings about a safe shutdown. By immersing this section of the tubes in a large graphite block to serve as a heat sink, dissipation of decay heat becomes manageable. This eliminates the need for emergency core cooling systems.« less

Peripapillary retinal nerve fiber layer thickness in a population of 6-year-old children: findings by optical coherence tomography.

PubMed

Huynh, Son C; Wang, Xiu Ying; Rochtchina, Elena; Mitchell, Paul

2006-09-01

To study the distribution of retinal nerve fiber layer (RNFL) thickness by ocular and demographic variables in a population-based study of young children. Population-based cross-sectional study. One thousand seven hundred sixty-five of 2238 (78.9%) eligible 6-year-old children participated in the Sydney Childhood Eye Study between 2003 and 2004. Mean age was 6.7 years (50.9% boys). Detailed examination included cycloplegic autorefraction and measurement of axial length. Retinal nerve fiber layer scans using an optical coherence tomographer were performed with a circular scan pattern of 3.4-mm diameter. Multivariate analyses were performed to examine the distribution of RNFL parameters with gender, ethnicity, axial length, and refraction. Peripapillary RNFL thickness and RNFL(estimated integral) (RNFL(EI)), which measures the total cross-sectional area of ganglion cell axons converging onto the optic nerve head. Peripapillary RNFL thickness and RNFL(EI) were normally distributed. The mean+/-standard deviation RNFL average thickness was 103.7+/-11.4 microm and RNFL(EI) was 1.05+/-0.12 mm2. Retinal nerve fiber layer thickness was least for the temporal quadrant (75.7+/-14.7 microm), followed by the nasal (81.7+/-19.6 microm), inferior (127.8+/-20.5 microm), and superior (129.5+/-20.6 microm) quadrants. Multivariate adjusted RNFL average thickness was marginally greater in boys than in girls (104.7 microm vs. 103.2 microm; P = 0.007) and in East Asian than in white children (107.7 microm vs. 102.7 microm; P<0.0001). The RNFL was thinner with greater axial length (P(trend)<0.0001) and less positive spherical equivalent refractions (P(trend) = 0.004). Retinal nerve fiber layer average thickness and RNFL(EI) followed a normal distribution. Retinal nerve fiber layer thickness varied marginally with gender, but differences were more marked between white and East Asian children. Retinal nerve fiber layer thinning was associated with increasing axial length and less positive refractions.

Advanced characterization techniques in understanding the roles of nickel in enhancing strength and toughness of submerged arc welding high strength low alloy steel multiple pass welds in the as-welded condition

NASA Astrophysics Data System (ADS)

Sham, Kin-Ling

Striving for higher strength along with higher toughness is a constant goal in material properties. Even though nickel is known as an effective alloying element in improving the resistance of a steel to impact fracture, it is not fully understood how nickel enhances toughness. It was the goal of this work to assist and further the understanding of how nickel enhanced toughness and maintained strength in particular for high strength low alloy (HSLA) steel submerged arc welding multiple pass welds in the as-welded condition. Using advanced analytical techniques such as electron backscatter diffraction, x-ray diffraction, electron microprobe, differential scanning calorimetry, and thermodynamic modeling software, the effect of nickel was studied with nickel varying from one to five wt. pct. in increments of one wt. pct. in a specific HSLA steel submerged arc welding multiple pass weldment. The test matrix of five different nickel compositions in the as-welded and stress-relieved condition was to meet the targeted mechanical properties with a yield strength greater than or equal to 85 ksi, a ultimate tensile strength greater than or equal to 105 ksi, and a nil ductility temperature less than or equal to -140 degrees F. Mechanical testing demonstrated that nickel content of three wt. pct and greater in the as-welded condition fulfilled the targeted mechanical properties. Therefore, one, three, and five wt. pct. nickel in the as-welded condition was further studied to determine the effect of nickel on primary solidification mode, nickel solute segregation, dendrite thickness, phase transformation temperatures, effective ferrite grain size, dislocation density and strain, grain misorientation distribution, and precipitates. From one to five wt. pct nickel content in the as-welded condition, the primary solidification was shown to change from primary delta-ferrite to primary austenite. The nickel partitioning coefficient increased and dendrite/cellular thickness was refined. Austenite decomposition temperatures into different ferrite products were also suppressed to refine the effective ferrite grain size with increasing nickel. Finally, dislocation density and strain increased and a more preferred orientation behavior was observed. At five wt. pct nickel, a precipitate in the form of MnNi3 or FeNi3 was observed. Its presence in both inter and intragranular regions enhanced strength and toughness by limiting the ferrite grain size and precipitation strengthening.

Application of Composite Mechanics to Composites Enhanced Concrete Structures

NASA Technical Reports Server (NTRS)

Chamis, Christos C.; Gotsis, Pascal K.

2006-01-01

A new and effective method is described to design composites to repair damage or enhance the overload strength of concrete infrastructures. The method is based on composite mechanics which is available in computer codes. It is used to simulate structural sections made from reinforced concrete which are typical in infrastructure as well as select reinforced concrete structures. The structural sections are represented by a number of layers through the thickness where different layers are used in concrete, and for the composite. The reinforced concrete structures are represented with finite elements where the element stiffness parameters are from the structural sections which are represented by composite mechanics. The load carrying capability of the structure is determined by progressive structural fracture. Results show up to 40 percent improvements for damage and for overload enhancement with relatively small laminate thickness for the structural sections and up to three times for the composite enhanced select structures (arches and domes).

Printed circuit board impedance matching step for microwave (millimeter wave) devices

DOEpatents

Pao, Hsueh-Yuan; Aguirre, Jerardo; Sargis, Paul

2013-10-01

An impedance matching ground plane step, in conjunction with a quarter wave transformer section, in a printed circuit board provides a broadband microwave matching transition from board connectors or other elements that require thin substrates to thick substrate (>quarter wavelength) broadband microwave (millimeter wave) devices. A method of constructing microwave and other high frequency electrical circuits on a substrate of uniform thickness, where the circuit is formed of a plurality of interconnected elements of different impedances that individually require substrates of different thicknesses, by providing a substrate of uniform thickness that is a composite or multilayered substrate; and forming a pattern of intermediate ground planes or impedance matching steps interconnected by vias located under various parts of the circuit where components of different impedances are located so that each part of the circuit has a ground plane substrate thickness that is optimum while the entire circuit is formed on a substrate of uniform thickness.

The mathematical cell model reconstructed from interference microscopy data

NASA Astrophysics Data System (ADS)

Rogotnev, A. A.; Nikitiuk, A. S.; Naimark, O. B.; Nebogatikov, V. O.; Grishko, V. V.

2017-09-01

The mathematical model of cell dynamics is developed to link the dynamics of the phase cell thickness with the signs of the oncological pathology. The measurements of irregular oscillations of cancer cells phase thickness were made with laser interference microscope MIM-340 in order to substantiate this model. These data related to the dynamics of phase thickness for different cross-sections of cells (nuclei, nucleolus, and cytoplasm) allow the reconstruction of the attractor of dynamic system. The attractor can be associated with specific types of collective modes of phase thickness responsible for the normal and cancerous cell dynamics. Specific type of evolution operator was determined using an algorithm of designing of the mathematical cell model and temporal phase thickness data for cancerous and normal cells. Qualitative correspondence of attractor types to the cell states was analyzed in terms of morphological signs associated with maximum value of mean square irregular oscillations of phase thickness dynamics.

Early detection of macular and peripapillary changes with spectralis optical coherence tomography in patients with prediabetes.

PubMed

Şahin, Muhammed; Şahin, Alparslan; Kılınç, Faruk; Karaalp, Ümit; Yüksel, Harun; Özkurt, Zeynep Gürsel; Türkcü, Fatih Mehmet; Çaça, İhsan

2018-02-01

To compare the retina ganglion cell complex (GCC) layer and peripapillary nerve fibre layer thickness (pRNFL) in patients with prediabetes and healthy subjects analysed by spectral domain optical coherence tomography (SD-OCT). This cross-sectional and comparative study included prediabetic patients and healthy subjects. All participants underwent SD-OCT measurement of pRNFL thickness, and GCC thickness. A total of 30 eyes of the 30 patients with prediabetes and 30 eyes of 30 controls were included. The overall calculated pRNFL thicknesses were similar between the prediabetic and control subjects. The GCC thickness was significantly lower in all quadrants of the inner macula, and outer nasal quadrant in the prediabetes group when compared to the control group. Our study demonstrated that inner macular GCC thickness was significantly thinner in prediabetic subjects. As a result neurodegeneration may play role in the thinning of GCC.

A transmission electron microscopy study of the deformation behavior underneath nanoindents in nanoscale Al-TiN multilayered composites

NASA Astrophysics Data System (ADS)

Bhattacharyya, D.; Mara, N. A.; Dickerson, P.; Hoagland, R. G.; Misra, A.

2010-05-01

Nanoscale multilayered Al-TiN composites were deposited using the dc magnetron sputtering technique in two different layer thickness ratios, Al : TiN = 1 : 1 and Al : TiN = 9 : 1. The Al layer thickness varied from 2 nm to 450 nm. The hardness of the samples was tested by nanoindentation using a Berkovich tip. Cross-sectional transmission electron microscopy (TEM) was carried out on samples extracted with focused ion beam from below the nanoindents. The results of the hardness tests on the Al-TiN multilayers with two different thickness ratios are presented, together with observations from the cross-sectional TEM studies of the regions underneath the indents. These studies revealed remarkable strength in the multilayers, as well as some very interesting deformation behavior in the TiN layers at extremely small length scales, where the hard TiN layers undergo co-deformation with the Al layers.

Preparation of 7Be targets for nuclear astrophysics research

NASA Astrophysics Data System (ADS)

Maugeri, E. A.; Heinitz, S.; Dressler, R.; Barbagallo, M.; Kivel, N.; Schumann, D.; Ayranov, M.; Musumarra, A.; Gai, M.; Colonna, N.; Paul, M.; Halfon, S.; Cosentino, L.; Finocchiaro, P.; Pappalardo, A.

2017-02-01

This work describes the preparation of three 7Be targets which were used in two independent measurements of the 7Be(n,α)4He cross section in the energy range of interest for the Big-Bang nucleosynthesis at the n\\_TOF-CERN facility and at Soreq-SARAF . A more precise value of this cross section could shed light on the long lasting "Cosmological Lithium problem". Two methods for target preparation were used. A target was obtained by deposition and subsequent air-drying of (24.50± 0.54) GBq of Be(NO3)2 droplets precisely positioned onto a stretched low density polyethylene film 0.635 μm thick. The thickness of the deposited Be(NO3)2 layer was deduced using Monte-Carlo simulations to be 0.36 μm. The energy loss of 8500 keV alpha particles passing through the target obtained by air-drying of 7Be(NO3)2 droplets was estimated to be 88 keV . Two other targets were prepared via molecular plating onto ~ 5 μm and 1 mm thick aluminium backings, respectively. The first was obtained by molecular plating (24.47± 0.53) GBq of 7Be, resulting in a deposited layer of Be(OH)2, 1.04 μm thick. The second molecular plated target was obtained depositing (3.95± 0.08) GBq of 7Be. The mean energy loss of 8500 keV alpha particles, passing through the molecular plated target with 5 μm thick aluminium backings was estimated as 814 keV . The energy loss by 8500 keV alpha particles in all the obtained targets is considered tolerable for the envisaged cross section measurements. The preparation and characterization of the targets is here described.

Isostasy-controlled thinning-upward cycles in the Mediterranean?; a comparison with the Zechstein salt giant

NASA Astrophysics Data System (ADS)

Van den Belt, Frank J. G.; De Boer, Poppe L.

2014-05-01

The desiccated deep-basin model, originally developed for the Mediterranean salt giant, deviated significantly from existing models and it has never been satisfactorily translated into a general concept. With time, however, Mediterranean models evolved towards moderate basin depths and the view that deposition took place in a flooded basin has gained reputation. These new insights have bridged the gap with general evaporite models and open possibilities of integrating concepts developed for other salt giants into the model. Recent modelling work (Van den Belt & De Boer, 2012) based on the Zechstein salt basin has shown that the thickness and composition of subsequent evaporite cycles can be explained by a model that involves a repetition of a three-stage process of 1) progressive narrowing of an ocean corridor in response to sulphate-platform progradation, resulting in 2) brine concentration and rapid infilling of the basin with halite and potash salts, the load of which causes 3) isostatic creation of accommodation space for the next cycle. Isostatic theory predicts that each cycle has approximately half the thickness of the previous one, e.g. 1.0 > 0.50 > 0.25 > 0.125 followed by a number of (coalesced) smaller cycles with a joint thickness of 0.125. The sequence in the basin centre then adds up to 2, which is two times the original basin depth. For the Zechstein case actual cycle thickness well matches these predicted values with cycle thicknesses of about 1.06 > 0.54 > 0.18 > 0.10 and 0.12. The cycle build-up of the Mediterranean salt giant is less well known, because of limited deep drilling. There are at least two cycles, a thin upper overlying a thick lower unit, but comparison of Zechstein patterns with Mediterranean sections has shown that more cycles may be present. Typical cycle boundaries include K/Mg-salt interbeds in halite units, and halite interbeds in sulphate units. Interestingly, analysis has shown that such indicators in Mediterranean sections indicate that cycles may indeed be stacked according to the 50% thickness rule. Examples are the K-salt halfway up the Sicilian section and the regular halite interbeds in the Upper Evaporite of the Western Mediterranean. In addition, the Lago Mare clays that define the top of the Mediterranean section are reminiscent of the Zechstein claystone cap. If the proposed mechanism indeed applies to the Mediterranean it would point at an initial basin depth of about 600-700 for the Western Mediterranean. Van den Belt & De Boer (2012) Utrecht Studies in Earth Sciences, v. 21, p. 59-65.

Preferential reduction of quadriceps over respiratory muscle strength and bulk after lung transplantation for cystic fibrosis.

PubMed

Pinet, C; Scillia, P; Cassart, M; Lamotte, M; Knoop, C; Mélot, C; Estenne, M

2004-09-01

In the absence of complications, recipients of lung transplants for cystic fibrosis have normal pulmonary function but the impact of the procedure on the strength and bulk of respiratory and limb muscles has not been studied. Twelve stable patients who had undergone lung transplantation for cystic fibrosis 48 months earlier (range 8-95) and 12 normal subjects matched for age, height, and sex were studied. The following parameters were measured: standard lung function, peak oxygen uptake by cycle ergometry, diaphragm surface area by computed tomographic (CT) scanning, diaphragm and abdominal muscle thickness by ultrasonography, twitch transdiaphragmatic and gastric pressures, quadriceps isokinetic strength, and quadriceps cross section by CT scanning, and lean body mass. Diaphragm mass was computed from diaphragm surface area and thickness. Twitch transdiaphragmatic and gastric pressures, diaphragm mass, and abdominal muscle thickness were similar in the two groups but quadriceps strength and cross section were decreased by nearly 30% in the patients. Patients had preserved quadriceps strength per unit cross section but reduced quadriceps cross section per unit lean body mass. The cumulative dose of corticosteroids was an independent predictor of quadriceps atrophy. Peak oxygen uptake showed positive correlations with quadriceps strength and cross section in the two groups, but peak oxygen uptake per unit quadriceps strength or cross section was reduced in the patient group. The diaphragm and abdominal muscles have preserved strength and bulk in patients transplanted for cystic fibrosis but the quadriceps is weak due to muscle atrophy. This atrophy is caused in part by corticosteroid therapy and correlates with the reduction in exercise capacity.

Identification of third-order (approx. 10{sup 6} yrs) and fourth-order (approx. 10{sup 5}/10{sup 4} yrs) stratigraphic cycles in the South Addition, West Cameron Lease Area, Louisiana offshore

DOE Office of Scientific and Technical Information (OSTI.GOV)

Lowrie, A.; Meeks, P.; Hoffman, K.

In the highly explored South Addition of the West Cameron Lease Area, Louisiana offshore, interpretation of a six-mile ({approx}10 km) seismic section across a single intraslope basin yielded 20 sediment packages. Several interpretive tools were necessary. Seismic stratigraphy indicated that the shallower zone was an outer shelf marked by 8 major sea level oscillations. In the portion between 1 and 3 seconds, seismic stratigraphy and paleontology led to the interpretation of depositional environments such as upper slope, and paleobathymetrically deeper intervals with descent through the section. The intraslope basin, while small, may be viewed as a micro-continental margin. Each seamore » level oscillation cycle apparently made a distinct progradational unit, decipherable in the seismic data. Fourth order cycles have been provisionally interpreted, throughout most of the entire 3.7 second section. Such precision is possible only in explored basins with excellent seismic data. The sequence thickness showed a seven-fold variability, from 0.08 to 0.58 seconds. The shallower section, deposited along an outer shelf, has an average individual sequence thickness of 0.13 seconds. Individual seismic sequences in the deeper section, interpreted to have been deposited on an upper slope, have average thicknesses of 0.25 seconds. The thinner sequences of the shallower section are compatible with the notion that the outer shelf was a bypass zone during a glacial epoch. The thicker sequences of the deeper section are the result of deposition onto an aggrading upper slope within an intraslope basin during a highstand.« less

Contraction-free, fume-fixed longitudinal sections of fresh frozen muscle

NASA Technical Reports Server (NTRS)

Riley, Danny A.; Slocum, Glenn R.

1988-01-01

Contraction damage occurring when longitudinal frozen sections of fresh unfixed muscles are thawed on microscope slides has limited histological examination of this tissue mainly to cross sections. Longitudinally oriented sections are advantageous for investigating properties that vary along the length of the muscle fibers. A fume fixation technique has been developed for preventing contraction of thick longitudinal frozen sections. The technique is compatible with histochemical staining of enzymes.

Surface figure control for coated optics

DOEpatents

Ray-Chaudhuri, Avijit K.; Spence, Paul A.; Kanouff, Michael P.

2001-01-01

A pedestal optical substrate that simultaneously provides high substrate dynamic stiffness, provides low surface figure sensitivity to mechanical mounting hardware inputs, and constrains surface figure changes caused by optical coatings to be primarily spherical in nature. The pedestal optical substrate includes a disk-like optic or substrate section having a top surface that is coated, a disk-like base section that provides location at which the substrate can be mounted, and a connecting cylindrical section between the base and optics or substrate sections. The optic section has an optical section thickness.sup.2 /optical section diameter ratio of between about 5 to 10 mm, and a thickness variation between front and back surfaces of less than about 10%. The connecting cylindrical section may be attached via three spaced legs or members. However, the pedestal optical substrate can be manufactured from a solid piece of material to form a monolith, thus avoiding joints between the sections, or the disk-like base can be formed separately and connected to the connecting section. By way of example, the pedestal optical substrate may be utilized in the fabrication of optics for an extreme ultraviolet (EUV) lithography imaging system, or in any optical system requiring coated optics and substrates with reduced sensitivity to mechanical mounts.

49 CFR 178.45 - Specification 3T seamless steel cylinder.

Code of Federal Regulations, 2011 CFR

2011-10-01

..., and service pressure. A DOT 3T cylinder is a seamless steel cylinder with a minimum water capacity of...) Wall thickness. The minimum wall thickness must be such that the wall stress at the minimum specified... the physical tests required in paragraphs (j) and (k) of this section. A wall stress of more than 90...

The Achilles Tendon in Healthy Subjects: An Anthropometric and Ultrasound Mapping Study.

PubMed

Patel, Nick N; Labib, Sameh A

Ultrasonography is an inexpensive, fast, and reliable imaging technique widely used to assess the Achilles tendon. Although significant data exists regarding pathologic tendon changes, ultrasound data from healthy individuals are more limited. We aimed to better characterize ultrasound Achilles tendon measurements in healthy individuals and identify important correlating factors. The information collected included patient demographics, body habitus, activity level, foot dominance, and resting ankle angle. Ultrasound analysis was performed bilaterally on the Achilles tendons of 50 subjects using a high-frequency transducer to measure tendon width, thickness, cross-sectional area, and length. Males had a significantly larger mean tendon length, width, thickness, and cross-sectional area. No statistically significant difference was found in any tendon dimension between the white and black participants. Similarly, no difference was found in any tendon parameter when comparing right versus left leg dominance. Healthy subjects had a mean ankle resting angle of 45.1° ± 24° with no statistically significant difference between right and left ankles. Considering all individuals, each tendon parameter (tendon length, width, thickness, and cross-sectional area) correlated positively with subject height, weight, tibia length, and foot size. Only the Achilles cross-sectional area correlated significantly with the activity level. The resting angle of the ankle correlated positively with both tendon length and thickness. In conclusion, we found significant variations in Achilles tendon anatomy in the healthy adult population. We have thoroughly characterized significant correlations between healthy tendon dimensions and various body habitus, activity levels, and ankle parameters. Greater knowledge of the normal Achilles tendon anatomy and characterization of its variations in the healthy population will potentially allow for better pathologic diagnosis and surgical repair. Copyright © 2017 The American College of Foot and Ankle Surgeons. Published by Elsevier Inc. All rights reserved.

Evaluation of two 3D virtual computer reconstructions for comparison of cleft lip and palate to normal fetal microanatomy.

PubMed

Landes, Constantin A; Weichert, Frank; Geis, Philipp; Helga, Fritsch; Wagner, Mathias

2006-03-01

Cleft lip and palate reconstructive surgery requires thorough knowledge of normal and pathological labial, palatal, and velopharyngeal anatomy. This study compared two software algorithms and their 3D virtual anatomical reconstruction because exact 3D micromorphological reconstruction may improve learning, reveal spatial relationships, and provide data for mathematical modeling. Transverse and frontal serial sections of the midface of 18 fetal specimens (11th to 32nd gestational week) were used for two manual segmentation approaches. The first manual segmentation approach used bitmap images and either Windows-based or Mac-based SURFdriver commercial software that allowed manual contour matching, surface generation with average slice thickness, 3D triangulation, and real-time interactive virtual 3D reconstruction viewing. The second manual segmentation approach used tagged image format and platform-independent prototypical SeViSe software developed by one of the authors (F.W.). Distended or compressed structures were dynamically transformed. Registration was automatic but allowed manual correction, such as individual section thickness, surface generation, and interactive virtual 3D real-time viewing. SURFdriver permitted intuitive segmentation, easy manual offset correction, and the reconstruction showed complex spatial relationships in real time. However, frequent software crashes and erroneous landmarks appearing "out of the blue," requiring manual correction, were tedious. Individual section thickness, defined smoothing, and unlimited structure number could not be integrated. The reconstruction remained underdimensioned and not sufficiently accurate for this study's reconstruction problem. SeViSe permitted unlimited structure number, late addition of extra sections, and quantified smoothing and individual slice thickness; however, SeViSe required more elaborate work-up compared to SURFdriver, yet detailed and exact 3D reconstructions were created.

Cross-sectional anatomy, computed tomography and magnetic resonance imaging of the head of common dolphin (Delphinus delphis) and striped dolphin (Stenella coeruleoalba).

PubMed

Alonso-Farré, J M; Gonzalo-Orden, M; Barreiro-Vázquez, J D; Barreiro-Lois, A; André, M; Morell, M; Llarena-Reino, M; Monreal-Pawlowsky, T; Degollada, E

2015-02-01

Computed tomography (CT) and low-field magnetic resonance imaging (MRI) were used to scan seven by-caught dolphin cadavers, belonging to two species: four common dolphins (Delphinus delphis) and three striped dolphins (Stenella coeruleoalba). CT and MRI were obtained with the animals in ventral recumbency. After the imaging procedures, six dolphins were frozen at -20°C and sliced in the same position they were examined. Not only CT and MRI scans, but also cross sections of the heads were obtained in three body planes: transverse (slices of 1 cm thickness) in three dolphins, sagittal (5 cm thickness) in two dolphins and dorsal (5 cm thickness) in two dolphins. Relevant anatomical structures were identified and labelled on each cross section, obtaining a comprehensive bi-dimensional topographical anatomy guide of the main features of the common and the striped dolphin head. Furthermore, the anatomical cross sections were compared with their corresponding CT and MRI images, allowing an imaging identification of most of the anatomical features. CT scans produced an excellent definition of the bony and air-filled structures, while MRI allowed us to successfully identify most of the soft tissue structures in the dolphin's head. This paper provides a detailed anatomical description of the head structures of common and striped dolphins and compares anatomical cross sections with CT and MRI scans, becoming a reference guide for the interpretation of imaging studies. © 2014 Blackwell Verlag GmbH.

Optically Sectioned Imaging of Microvasculature of In-Vivo and Ex-Vivo Thick Tissue Models with Speckle-illumination HiLo Microscopy and HiLo Image Processing Implementation in MATLAB Architecture

NASA Astrophysics Data System (ADS)

Suen, Ricky Wai

The work described in this thesis covers the conversion of HiLo image processing into MATLAB architecture and the use of speckle-illumination HiLo microscopy for use of ex-vivo and in-vivo imaging of thick tissue models. HiLo microscopy is a wide-field fluorescence imaging technique and has been demonstrated to produce optically sectioned images comparable to confocal in thin samples. The imaging technique was developed by Jerome Mertz and the Boston University Biomicroscopy Lab and has been implemented in our lab as a stand-alone optical setup and a modification to a conventional fluorescence microscope. Speckle-illumination HiLo microscopy combines two images taken under speckle-illumination and standard uniform-illumination to generate an optically sectioned image that reject out-of-focus fluorescence. The evaluated speckle contrast in the images is used as a weighting function where elements that move out-of-focus have a speckle contrast that decays to zero. The experiments shown here demonstrate the capability of our HiLo microscopes to produce optically-sectioned images of the microvasculature of ex-vivo and in-vivo thick tissue models. The HiLo microscope were used to image the microvasculature of ex-vivo mouse heart sections prepared for optical histology and the microvasculature of in-vivo rodent dorsal window chamber models. Studies in label-free surface profiling with HiLo microscopy is also presented.

Thick-target-method study of Mα β x-ray production cross sections of Pb and Bi impacted by positrons up to 9 keV

NASA Astrophysics Data System (ADS)

Wu, Y.; Liang, Y.; Xu, M. X.; Yuan, Y.; Chang, C. H.; Qian, Z. C.; Wang, B. Y.; Kuang, P.; Zhang, P.

2018-03-01

Atomic M -shell x-ray production cross sections induced by positrons near the threshold energy have been presented in this paper. In the experiment, online monitoring technology, which utilizes a high-purity germanium detector to record the annihilation photons emitted from the pure thick target impacted by positrons, was developed to obtain the accurate number of the incident positrons. The effects of the multiple scattering of incident positrons, from the bremsstrahlung and annihilation photons and other secondary particles on the experimental characteristic x-ray yield, were eliminated by Monte Carlo simulation in combination with theoretical integral calculation. The Tikhonov regularization method was adopted to handle the ill-posed inverse problem involved in the thick-target method, i.e., x-ray production cross sections by the corrected characteristic x-ray yield. Experimental results of Mα β x-ray production cross sections for Pb and Bi impacted by 6-9-keV positrons were compared with the corresponding values predicted by the distorted-wave Born approximation (DWBA). Good agreement was found between the two. Moreover, we have presented the experimental results on the ratios of the Mα β x-ray production cross sections by electron impact in the literature to that by 6-9-keV positron impact in this work. They were also in accordance with the theoretical ratios calculated by the predictions of DWBA theory.

Spatial distribution of sediment storage types and quantification of valley fill deposits in an alpine basin, Reintal, Bavarian Alps, Germany

NASA Astrophysics Data System (ADS)

Schrott, Lothar; Hufschmidt, Gabi; Hankammer, Martin; Hoffmann, Thomas; Dikau, Richard

2003-09-01

Spatial patterns of sediment storage types and associated volumes using a novel approach for quantifying valley fill deposits are presented for a small alpine catchment (17 km 2) in the Bavarian Alps. The different sediment storage types were analysed with respect to geomorphic coupling and sediment flux activity. The most landforms in the valley in terms of surface area were found to be talus slopes (sheets and cones) followed by rockfall deposits and alluvial fans and plains. More than two-thirds of the talus slopes are relict landforms, completely decoupled from the geomorphic system. Notable sediment transport is limited to avalanche tracks, debris flows, and along floodplains. Sediment volumes were calculated using a combination of polynomial functions of cross sections, seismic refraction, and GIS modelling. A total of, 66 seismic refraction profiles were carried out throughout the valley for a more precise determination of sediment thicknesses and to check the bedrock data generated from geomorphometric analysis. We calculated the overall sediment volume of the valley fill deposits to be 0.07 km 3. This corresponds to a mean sediment thickness of 23.3 m. The seismic refraction data showed that large floodplains and sedimentation areas, which have been developed through damming effects from large rockfalls, are in general characterised by shallow sediment thicknesses (<20 m). By contrast, the thickness of several talus slopes is more than twice as much. For some locations (e.g., narrow sections of valley), the polynomial-generated cross sections resulted in overestimations of up to one order of magnitude; whereas in sections with a moderate valley shape, the modelled cross sections are in good accordance with the obtained seismic data. For the quantification of valley fill deposits, a combined application of bedrock data derived from polynomials and geophysical prospecting is highly recommended.

Dark adaptation in relation to choroidal thickness in healthy young subjects: a cross-sectional, observational study.

PubMed

Munch, Inger Christine; Altuntas, Cigdem; Li, Xiao Qiang; Jackson, Gregory R; Klefter, Oliver Niels; Larsen, Michael

2016-07-11

Dark adaptation is an energy-requiring process in the outer retina nourished by the profusely perfused choroid. We hypothesized that variations in choroidal thickness might affect the rate of dark adaptation. Cross-sectional, observational study of 42 healthy university students (mean age 25 ± 2.0 years, 29 % men) who were examined using an abbreviated automated dark adaptometry protocol with a 2° diameter stimulus centered 5° above the point of fixation. The early, linear part of the rod-mediated dark adaptation curve was analyzed to extract the time required to reach a sensitivity of 5.0 × 10(-3) cd/m2 (time to rod intercept) and the slope (rod adaptation rate). The choroid was imaged using enhanced-depth imaging spectral-domain optical coherence tomography (EDI-OCT). The time to the rod intercept was 7.3 ± 0.94 (range 5.1 - 10.2) min. Choroidal thickness 2.5° above the fovea was 348 ± 104 (range 153-534) μm. There was no significant correlation between any of the two measures of rod-mediated dark adaptation and choroidal thickness (time to rod intercept versus choroidal thickness 0.072 (CI95 -0.23 to 0.38) min/100 μm, P = 0.64, adjusted for age and sex). There was no association between the time-to-rod-intercept or the dark adaptation rate and axial length, refraction, gender or age. Choroidal thickness, refraction and ocular axial length had no detectable effect on rod-mediated dark adaptation in healthy young subjects. Our results do not support that variations in dark adaptation can be attributed to variations in choroidal thickness.

PULSED EDDY CURRENT THICKNESS MEASUREMENT OF SELECTIVE PHASE CORROSION ON NICKEL ALUMINUM BRONZE VALVES

DOE Office of Scientific and Technical Information (OSTI.GOV)

Krause, T. W.; Harlley, D.; Babbar, V. K.

Nickel Aluminum Bronze (NAB) is a material with marine environment applications that under certain conditions can undergo selective phase corrosion (SPC). SPC involves the removal of minority elements while leaving behind a copper matrix. Pulsed eddy current (PEC) was evaluated for determination of SPC thickness on a NAB valve section with access from the surface corroded side. A primarily linear response of PEC amplitude, up to the maximum available SPC thickness of 4 mm was observed. The combination of reduced conductivity and permeability in the SPC phase relative to the base NAB was used to explain the observed sensitivity ofmore » PEC to SPC thickness variations.« less

Innovative Tools Advance Revolutionary Weld Technique

NASA Technical Reports Server (NTRS)

2009-01-01

The iconic, orange external tank of the space shuttle launch system not only contains the fuel used by the shuttle s main engines during liftoff but also comprises the shuttle s backbone, supporting the space shuttle orbiter and solid rocket boosters. Given the tank s structural importance and the extreme forces (7.8 million pounds of thrust load) and temperatures it encounters during launch, the welds used to construct the tank must be highly reliable. Variable polarity plasma arc welding, developed for manufacturing the external tank and later employed for building the International Space Station, was until 1994 the best process for joining the aluminum alloys used during construction. That year, Marshall Space Flight Center engineers began experimenting with a relatively new welding technique called friction stir welding (FSW), developed in 1991 by The Welding Institute, of Cambridge, England. FSW differs from traditional fusion welding in that it is a solid-state welding technique, using frictional heat and motion to join structural components without actually melting any of the material. The weld is created by a shouldered pin tool that is plunged into the seam of the materials to be joined. The tool traverses the line while rotating at high speeds, generating friction that heats and softens but does not melt the metal. (The heat produced approaches about 80 percent of the metal s melting temperature.) The pin tool s rotation crushes and stirs the plasticized metal, extruding it along the seam as the tool moves forward. The material cools and consolidates, resulting in a weld with superior mechanical properties as compared to those weld properties of fusion welds. The innovative FSW technology promises a number of attractive benefits. Because the welded materials are not melted, many of the undesirables associated with fusion welding porosity, cracking, shrinkage, and distortion of the weld are minimized or avoided. The process is more energy efficient, safe (no toxic smoke or shielding gas, liquid metal splatter, arcing, dangerous voltage, or radiation), and environmentally sound (no consumables, fumes, or noise) than fusion welding. Under computer control, an automated FSW machine can create welds with high reproducibility, improving efficiency and overall quality of manufactured materials. The process also allows for welding dissimilar metals as well as those metals considered to be "unweldable" such as the 7xxx series aluminum alloys. Its effectiveness and versatility makes FSW useful for aerospace, rail, automotive, marine, and military applications. A downside to FSW, however, is the keyhole opening left in the weld when the FSW pin tool exits the weld joint. This is a significant problem when using the FSW process to join circumferential structures such as pipes and storage containers. Furthermore, weld joints that taper in material thickness also present problems when using the conventional FSW pin tool, because the threaded pin rotating within the weld joint material is a fixed length. There must be capability for the rotating pin to both increase and decrease in length in real time while welding the tapered material. (Both circumferential and tapered thickness weldments are found in the space shuttle external tank.) Marshall engineers addressed both the keyhole and tapered material thickness problems by developing the auto-adjustable pin tool. This unique piece of equipment automatically withdraws the pin into the tool s shoulder for keyhole closeout. In addition, the auto-adjustable pin tool retracts, or shortens, the rotating pin while welding a weld joint that tapers from one thickness to a thinner thickness. This year, the impact of the Marshall innovation was recognized with an "Excellence in Technology Transfer Award" from the Federal Laboratory Consortium.

Weld procedure produces quality welds for thick sections of Hastelloy-X

NASA Technical Reports Server (NTRS)

Flens, F. J.; Fletcher, C. W.; Glasier, L. F., Jr.

1967-01-01

Welding program produces premium quality, multipass welds in heavy tube sections of Hastelloy-X. It develops semiautomatic tungsten/inert gas procedures, weld wire procurement specifications material weld properties, welder-operator training, and nondestructive testing inspection techniques and procedures.

Lithostratigraphic description, sedimentological characteristics and depositional environments of rocks penetrated by Illela borehole, Sokoto Basin, NW Nigeria: A connection between Gulf of Guinea Basins

NASA Astrophysics Data System (ADS)

Toyin, A.; Adekeye, O. A.; Bale, R. B.; Sanni, Z. J.; Jimoh, O. A.

2016-09-01

The basal unit of the succession in the Illela borehole belongs to the Dange Formation comprising thick calcareous and variably coloured dark-greyish shale of 36.30 m thick which is overlain by a 31.44 m thick limestone of Kalambaina Formation with 1.7 m thick shaly-limestone inclusive. The uppermost part of the section belongs to the Gwandu Formation which has intercalation of silty-clay, muddy siltstones with well lithified ironstone capping the borehole section. The limestone/carbonate microfacie as deduced from their salient lithologic, sedimentologic and paleontologic features are comparable to standard microfacie (SMF) types 9 and 10, i.e. bioclastic wackestone/bioclastic micrite and packstone-wackestone respectively. Diagenetically, syndepositional and early diagenesis have taken place particularly cementation and replacement in the carbonate rocks and these have greatly affected the reservoir potential negatively. The matrix/grain relationships indicate a shallow marine environment of deposition. The borehole section is delineated into upper foraminifera and lower ostracod biostratigraphic units as no formal biostratigraphic zonation could be attempted due to low diversity of both benthic foraminifera, marine ostracods and the absence of planktonic foraminifera. The similarity of the ostracod assemblages between this study area, Illela borehole, West Africa, North Africa (Libya), Mali and Niger Republic) and South-Western Nigeria (West Africa) suggests that a marine connection exists between the Gulf of Guinea and the Sokoto Basin via the area occupied by the River Niger during the Paleocene.

Effect of proof testing on the flaw growth characteristics of 304 stainless steel. [crack propagation in welded joints

NASA Technical Reports Server (NTRS)

Finger, R. W.

1974-01-01

The effects of proof overload frequency and magnitude on the cyclic crack growth rates of 304 stainless steel weldments were investigated. The welding procedure employed was typical of those used on over-the-road cryogenic vessels. Tests were conducted at room temperature with an overload ratio of 1.50 to determine the effect of overload frequency. Effect of overload magnitude was determined from tests where a room temperature overload was applied between blocks of 1000 cycles applied at 78 K (-320 F). The cyclic stress level used in all tests was typical of the nominal membrane stress generally encountered in full scale vessels. Test results indicate that judicious selection of proof overload frequency and magnitude can reduce crack growth rates for cyclic stress levels.

Hot cracking susceptibility of fillers 52 and 82 in alloy 690 welding

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wu, W.; Tsai, C.H.

1999-02-01

The hot cracking susceptibility of fillers 52 and 82 in a alloy 690 weldment is analyzed by the Varestraint test. Weld characteristics, microstructure, hardness distribution, and thermal analysis of the two filler metals are also examined. The weld metal of both fillers develops an extremely dense oxide layer. A stainless steel brush cannot remove the oxide layer, and a grinder may be needed between weld passes to assure a sound weld. Differential temperature analysis (DTA) shows that filler 82 has a lower melting point and a wider melting/solidification temperature differential ({Delta} T). These characteristics correlate with greater hot cracking susceptibilitymore » of filler 82 than 52 in Varestraint tests. The hot cracks are intergranular and are caused by elements segregating in grain boundaries.« less

Status Report on Irradiation Capsules Containing Welded FeCrAl Specimens for Radiation Tolerance Evaluation

DOE Office of Scientific and Technical Information (OSTI.GOV)

Field, Kevin G.; Howard, Richard H.

2016-02-26

This status report provides the background and current status of a series of irradiation capsules, or “rabbits”, that were designed and built to test the contributions of microstructure, composition, damage dose, and irradiation temperature on the radiation tolerance of candidate FeCrAl alloys being developed to have enhanced weldability and radiation tolerance. These rabbits will also test the validity of using an ultra-miniature tensile specimen to assess the mechanical properties of irradiated FeCrAl base metal and weldments. All rabbits are to be irradiated in the High Flux Isotope Reactor (HFIR) at Oak Ridge National Laboratory (ORNL) to damage doses up tomore » ≥15 dpa at temperatures between 200-550°C.« less

The effect of inhibitor sodium nitrate on pitting corrosion of dissimilar material weldment joint of stainless steel AISI 304 and mild steel SS 400

DOE Office of Scientific and Technical Information (OSTI.GOV)

Hilca, B. R., E-mail: bangkithilca@yahoo.com; Triyono, E-mail: triyonomesin@uns.ac.id

This study experimentally evaluated the effect of Sodium Nitrate inhibitor (NaNO{sub 3}) of 0.1%, 0.3%, and 0.5% on NaCl 3.5% toward pitting corrosion of dissimilar metal welding joint between stainless steel AISI 304 and mild steel SS 400. Electrochemical corrosion was tested using potentiodynamic polarization. Further the Scanning Electron Microscope (SEM) conducted to analyze the specimen. Chemical composition analysis used Energy Dispersive X-ray Spectrometry (EDS). The highest efficiency of sodium nitrate for ER 308 attained 63.8% and 64.89%for ER 309L. The specimen surface which observed through SEM showed decrease of pitting corrosion respectively with the addition of sodium nitrate contentmore » as inhibitor.« less

Quantitative methods in fractography; Proceedings of the Symposium on Evaluation and Techniques in Fractography, Atlanta, GA, Nov. 10, 1988

DOE Office of Scientific and Technical Information (OSTI.GOV)

Strauss, B.M.; Putatunda, S.K.

1990-01-01

Papers are presented on the application of quantitative fractography and computed tomography to fracture processes in materials, the relationships between fractographic features and material toughness, the quantitative analysis of fracture surfaces using fractals, and the analysis and interpretation of aircraft component defects by means of quantitative fractography. Also discussed are the characteristics of hydrogen-assisted cracking measured by the holding-load and fractographic method, a fractographic study of isolated cleavage regions in nuclear pressure vessel steels and their weld metals, a fractographic and metallographic study of the initiation of brittle fracture in weldments, cracking mechanisms for mean stress/strain low-cycle multiaxial fatigue loadings,more » and corrosion fatigue crack arrest in Al alloys.« less

Thermo-mechanical process for treatment of welds

DOE Office of Scientific and Technical Information (OSTI.GOV)

Malik, R K

1980-03-01

Benefits from thermo-mechanical processing (TMP) of austenitic stainless steel weldments, analogous to hot isostatic pressing (HIP) of castings, most likely result from compressive plastic deformation, enhanced diffusion, and/or increased dislocation density. TMP improves ultrasonic inspectability of austenitic stainless steel welds owing to: conversion of cast dendrites into equiaxed austenitic grains, reduction in size and number of stringers and inclusions, and reduction of delta ferrite content. TMP induces structural homogenization and healing of void-type defects and thus contributes to an increase in elongation, impact strength, and fracture toughness as well as a significant reduction in data scatter for these properties. Anmore » optimum temperature for TMP or HIP of welds is one which causes negligible grain growth and an acceptable reduction in yield strength, and permits healing of porosity.« less

Microstructure and hydrogen induced failure mechanisms in iron-nickel weldments

NASA Astrophysics Data System (ADS)

Fenske, Jamey Alan

A recent series of inexplicable catastrophic failures of specific subsea dissimilar metal Fe-Ni butter welds has illuminated a fundamental lack of understanding of both the microstructure created along the fusion line as well as its impact on the hydrogen susceptibility of these interfaces. In order to remedy this, the present work compares and contrasts the microstructure and hydrogen-induced fracture morphology of AISI 8630-IN 625 and F22-IN 625 dissimilar metal weld interfaces as a function of post-weld heat treatment duration. A variety of techniques were used to study details of both the microstructure and fracture morphology including optical microscopy, scanning electron microscopy, secondary ion mass spectrometry, transmission electron microscopy, electron backscatter diffraction, and energy dispersive x-ray spectroscopy. For both systems, the microstructure along the weld interface consisted of a coarse grain heat-affected zone in the Fe-base metal followed by discontinuous martensitic partially-mixed zones and a continuous partially-mixed zone on the Ni-side of the fusion line. Within the partially mixed zone on the Ni-side there exists a 200 nm-wide transition zone within a 20 mum-wide planar solidification region followed by a cellular dendritic region with Nb-Mo rich carbides decorating the dendrite boundaries. The size, area fraction and composition of the discontinuous PMZ were determined to be controlled by uneven mixing in the liquid weld pool influenced by convection currents produced from the welding procedure. The virgin martensitic microstructure produced in these regions is formed as consequence of a both the local composition and the post-weld heat treatment. The local higher Ni content results in these regions being retransformed into austenite during the post-weld heat treatment and then virgin martensite while cooling to room temperature. Although there were differences in the volume of the discontinuous partially mixed-zones, the major difference in the weld metal interfaces was the presence of M 7C3 precipitates in the planar solidification region. The formation of these precipitates, which were found in what was previously referred to as the "featureless-zone," were determined to be dependent on the carbon content of the Fe-base metal and the duration of the post-weld heat treatment. A high density of these ordered 100 nm-long by 10 nm-wide needle-like precipitates were found in the AISI 8630-IN 625 weldment in the 10 hour post-weld heat treatment condition while only the initial stages of their nucleation were evident in the F22-IN 625 15 hour post-weld heat treatment specimen. The study of the fractured specimens revealed that the M7C 3 carbides play a key role in the susceptibility to hydrogen embrittlement of the Fe-Ni butter weldments. The fractures initially nucleate along the isolated Fe-base metal -- discontinuous partially mixed zone interfaces. The M7C3 carbides accumulate hydrogen and then provide a low energy fracture path between the discontinuous partially mixed zones leading to catastrophic failure. The result is a fracture morphology that alternates between flat regions produced by fracture along the discontinuous partially mixed zones and cleavage-like fracture regions produced by fracture along the ordered carbide matrix interfaces.

Mathematical Model of Stress-Strain State of Curved Tube of Non-Circular Cross-Section with Account of Technological Wall Thickness Variation

NASA Astrophysics Data System (ADS)

Pirogov, S. P.; Ustinov, N. N.; Smolin, N. I.

2018-05-01

A mathematical model of the stress-strain state of a curved tube of a non-circular cross-section is presented, taking into account the technological wall thickness variation. On the basis of the semi-membrane shell theory, a system of linear differential equations describing the deformation of a tube under the effect of pressure is obtained. To solve the boundary value problem, the method of shooting is applied. The adequacy of the proposed mathematical model is verified by comparison with the experimental data and the results of the calculation of tubes by the energy method.

Characterization of annular two-phase gas-liquid flows in microgravity

NASA Technical Reports Server (NTRS)

Bousman, W. Scott; Mcquillen, John B.

1994-01-01

A series of two-phase gas-liquid flow experiments were developed to study annular flows in microgravity using the NASA Lewis Learjet. A test section was built to measure the liquid film thickness around the perimeter of the tube permitting the three dimensional nature of the gas-liquid interface to be observed. A second test section was used to measure the film thickness, pressure drop and wall shear stress in annular microgravity two-phase flows. Three liquids were studied to determine the effects of liquid viscosity and surface tension. The result of this study provide insight into the wave characteristics, pressure drop and droplet entrainment in microgravity annular flows.

Recent Advances in the Development of Thick-Section Melt-Infiltrated C/SiC Composites

NASA Technical Reports Server (NTRS)

Babcock, Jason R.; Ramachandran, Gautham; Williams, Brian E.; Effinger, Michael R.

2004-01-01

Using a pressureless melt infiltration and in situ reaction process to form the silicon carbide (SiC) matrix, Ultramet has been developing a means to rapidly fabricate ceramic matrix composites (CMCs) targeting thicker sections. The process also employs a unique route for the application of oxide fiber interface coatings designed to protect the fiber and impart fiber-matrix debond. Working toward a 12 inch diameter, 2.5 inch thick demonstrator component, the effect of various processing parameters on room temperature flexure strength is being studied with plans for more extensive elevated temperature mechanical strength evaluation to follow this initial optimization process.

Photochemistry on ultrathin metal films: Strongly enhanced cross sections for NO2 on Ag /Si(100)

NASA Astrophysics Data System (ADS)

Wesenberg, Claudia; Autzen, Olaf; Hasselbrink, Eckart

2006-12-01

The surface photochemistry of NO2 on ultrathin Ag(111) films (5-60nm ) on Si(100) substrates has been studied. NO2, forming N2O4 on the surface, dissociates to release NO and NO2 into the gas phase with translational energies exceeding the equivalent of the sample temperature. An increase of the photodesorption cross section is observed for 266nm light when the film thickness is decreased below 30nm despite the fact that the optical absorptivity decreases. For 4.4nm film thickness this increase is about threefold. The data are consistent with a similar effect for 355nm light. The reduced film thickness has no significant influence on the average translation energy of the desorbing molecules or the branching into the different channels. The increased photodesorption cross section is interpreted to result from photon absorption in the Si substrate producing electrons with no or little momenta parallel to the surface at energies where this is not allowed in Ag. It is suggested that these electrons penetrate through the Ag film despite the gap in the surface projected band structure.

In Situ Monitoring of Particle Consolidation During Low Pressure Cold Spray by Ultrasonic Techniques

NASA Astrophysics Data System (ADS)

Maev, R. Gr.; Titov, S.; Leshchynsky, V.; Dzhurinskiy, D.; Lubrick, M.

2011-06-01

This study attempts to test the viability of the examination of the cold spray process using acoustic methods, specifically in situ testing during the actual spray process itself. Multiple composites studied by flat and multi-channel transducers as well as the results of actual online measurements are presented. It is shown that the final thickness as well as the dynamics of buildup can be evaluated (including plotting rates of buildup). Cross sections of the coating thickness are also easy to obtain and show true profiles of the coating. The data can also be used to generate real estimates for nozzle speed and spray diameter. Finally, comparisons of real thickness and acoustically estimated thickness show a close linear relationship. The data clearly show that online acoustic measurement is a viable method for estimating thickness buildup.

Spanwise transition section for blended wing-body aircraft

NASA Technical Reports Server (NTRS)

Hawley, Arthur V. (Inventor)

1999-01-01

A blended wing-body aircraft includes a central body, a wing, and a transition section which interconnects the body and the wing on each side of the aircraft. The two transition sections are identical, and each has a variable chord length and thickness which varies in proportion to the chord length. This enables the transition section to connect the thin wing to the thicker body. Each transition section has a negative sweep angle.

Cross-Sectional Elasticity Imaging of Arterial Wall by Comparing Measured Change in Thickness with Model Waveform

NASA Astrophysics Data System (ADS)

Tang, Jiang; Hasegawa, Hideyuki; Kanai, Hiroshi

2005-06-01

For the assessment of the elasticity of the arterial wall, we have developed the phased tracking method [H. Kanai et al.: IEEE Trans. Ultrason. Ferroelectr. Freq. Control 43 (1996) 791] for measuring the minute change in thickness due to heartbeats and the elasticity of the arterial wall with transcutaneous ultrasound. For various reasons, for example, an extremely small deformation of the wall, the minute change in wall thickness during one heartbeat is largely influenced by noise in these cases and the reliability of the elasticity distribution obtained from the maximum change in thickness deteriorates because the maximum value estimation is largely influenced by noise. To obtain a more reliable cross-sectional image of the elasticity of the arterial wall, in this paper, a matching method is proposed to evaluate the waveform of the measured change in wall thickness by comparing the measured waveform with a template waveform. The maximum deformation, which is used in the calculation of elasticity, was determined from the amplitude of the matched model waveform to reduce the influence of noise. The matched model waveform was obtained by minimizing the difference between the measured and template waveforms. Furthermore, a random error, which was obtained from the reproducibility among the heartbeats of the measured waveform, was considered useful for the evaluation of the reliability of the measured waveform.

Gynecological and obstetrical outcomes after laparoscopic repair of a cesarean scar defect in a series of 38 women.

PubMed

Donnez, Olivier; Donnez, Jacques; Orellana, Renan; Dolmans, Marie-Madeleine

2017-01-01

To evaluate gynecological and obstetrical outcomes, as well as remaining myometrial thickness, after laparoscopic repair of a cesarean scar. Observational study and prospective evaluation of the remaining myometrium before and after repair. Academic department in a university hospital. A series of 38 symptomatic women with cesarean scar defects and remaining myometrial thickness of less than 3 mm, according to magnetic resonance imaging. Laparoscopic repair of the defect. Increase in myometrial thickness at the site of cesarean section, gynecological and obstetrical outcomes, and histological analysis of the defect after excision. The mean thickness of the myometrium increased significantly from 1.43 ± 0.7 mm before surgery to 9.62 ± 1.8 mm after surgery. All but three patients were free of symptoms. Among the 18 women with infertility, eight (44%) became pregnant and delivered healthy babies by cesarean section at 38-39 weeks of gestation. Histological analysis, performed in all 38 cases, revealed the presence of endometriosis in eight women (21.1%). Muscle fiber density was significantly lower compared with adjacent myometrium. In symptomatic women with residual myometrial thickness of less than 3 mm who wish to conceive, laparoscopic repair could be considered an appropriate approach. Copyright © 2016 American Society for Reproductive Medicine. Published by Elsevier Inc. All rights reserved.

Process stability during fiber laser-arc hybrid welding of thick steel plates

NASA Astrophysics Data System (ADS)

Bunaziv, Ivan; Frostevarg, Jan; Akselsen, Odd M.; Kaplan, Alexander F. H.

2018-03-01

Thick steel plates are frequently used in shipbuilding, pipelines and other related heavy industries, and are usually joined by arc welding. Deep penetration laser-arc hybrid welding could increase productivity but has not been thoroughly investigated, and is therefore usually limited to applications with medium thickness (5-15 mm) sections. A major concern is process stability, especially when using modern welding consumables such as metal-cored wire and advanced welding equipment. High speed imaging allows direct observation of the process so that process behavior and phenomena can be studied. In this paper, 45 mm thick high strength steel was welded (butt joint double-sided) using the fiber laser-MAG hybrid process utilizing a metal-cored wire without pre-heating. Process stability was monitored under a wide range of welding parameters. It was found that the technique can be used successfully to weld thick sections with appropriate quality when the parameters are optimized. When comparing conventional pulsed and the more advanced cold metal transfer pulse (CMT+P) arc modes, it was found that both can provide high quality welds. CMT+P arc mode can provide more stable droplet transfer over a limited range of travel speeds. At higher travel speeds, an unstable metal transfer mechanism was observed. Comparing leading arc and trailing arc arrangements, the leading arc configuration can provide higher quality welds and more stable processing at longer inter-distances between the heat sources.

Advances in Low Carbon, High Strength Ferrous Alloys

DTIC Science & Technology

1993-04-01

35 TABLES 1. Specified chemical compositions and mechanical properties for GMAW/SAW/ GTAW wire electrodes, MIL-XXXS type, for welding...minimum service temperature of +300 F. The chromium and molybdenum additions improved hardenability and promoted the formation of mar- tensite in thick...alloying ele- ments ( chromium , nickel and molybdenum) are required, especially for thick sections. Production of high strength steel plate for military

DOE Office of Scientific and Technical Information (OSTI.GOV)

Schultz, A.W.; Leavitt, W.Z.

A preliminary study was conducted to determine the feasiblllty of uslng neutron radiography for examining ordnance materials. Depleted U and 4140 steel castings in various thicknesses were examined. In addition, a thin section of Be, a grasshopper and a cricket were radiographed to illustrate the ability of neutrons to determine defects in low-density materials. For uranium thicknesses up to 5 in., a contrast sensitivity between 1.5 and 7.5%o was obtained using thermal neutrons, In foil, and industrial x-ray film transfer techniques. For 6 in. of U, a contrast sensitivity between 6.3 and 12.5% was obtained. For U thicknesses up tomore » 6 in., a detail sensitivity of 2.1% was obtained. For thicknesses up to 4 in. of steel, a contrast sensitivity between 1.9 and 9.4% and a detail sensitivity between 0.8 and 3.1% were obtained. For 5.125 and 6 in. of steel, contrast sensitivities between 14.6 and 29.2% and 14.6 and 39.6%, respectively, and detail sensitivities of no less than 4.9% were obtained. Both a contrast and a detail sensitivity of about 5% were obtained in examining a thin section of Be. Recommendations for further studies are given. (auth)« less

Comparison of Lateral Abdominal Muscle Thickness and Cross Sectional Area of Multifidus in Adolescent Soccer Players with and without Low Back Pain: A Case Control Study.

PubMed

Noormohammadpour, Pardis; Hosseini Khezri, Alireza; Linek, Paweł; Mansournia, Mohammad Ali; Hassannejad, Alireza; Younesian, Ali; Farahbakhsh, Farzin; Kordi, Ramin

2016-12-01

Low back pain (LBP) is a common complaint amongst adolescent athletes. While different studies have shown association between LBP and trunk muscle thickness in the general population, few articles have studied it in adolescent athletes. The aim of this study is to compare lateral abdominal muscle thickness and function, and cross sectional area (CSA) of lumbar multifidus (LM) in adolescent soccer players with and without LBP. In total, 28 adolescent soccer players with and without LBP, from the premier league participated in this study. The thickness of external oblique, internal oblique and transversus abdominis and the CSA of the LM muscles at L4 level on both sides were measured at rest and contraction via ultrasound imaging (USI). In addition, leg length discrepancy, hamstring flexibility, active lumbar forward flexion, and isometric muscle endurance of trunk extensors were measured in both groups. (study design/setting: case control study). The mean (SD) age in LBP group and non-LBP group were 14.0 (1.1) and 14.1 (0.9) years, respectively. There was no significant difference in baseline characteristics of participants between groups. Findings showed no significant difference between LBP and non-LBP groups comparing all measured variables. The data obtained support that there is not a correlation between abdominal muscle thickness and CSA of the lumbar multifidi and LBP in adolescent soccer players. These findings suggest that other factors rather than the thickness of deep trunk muscles may play a more significant role in the etiology of LBP in adolescent soccer players.

KINKFOLD—an AutoLISP program for construction of geological cross-sections using borehole image data

NASA Astrophysics Data System (ADS)

Özkaya, Sait Ismail

2002-04-01

KINKFOLD is an AutoLISP program designed to construct geological cross-sections from borehole image or dip meter logs. The program uses the kink-fold method for cross-section construction. Beds are folded around hinge lines as angle bisectors so that bedding thickness remains unchanged. KINKFOLD may be used to model a wide variety of parallel fold structures, including overturned and faulted folds, and folds truncated by unconformities. The program accepts data from vertical or inclined boreholes. The KINKFOLD program cannot be used to model fault drag, growth folds, inversion structures or disharmonic folds where the bed thickness changes either because of deformation or deposition. Faulted structures and similar folds can be modelled by KINKFOLD by omitting dip measurements within fault drag zones and near axial planes of similar folds.

Grazing Incidence Cross-Sectioning of Thin-Film Solar Cells via Cryogenic Focused Ion Beam: A Case Study on CIGSe

DOE Office of Scientific and Technical Information (OSTI.GOV)

Sardashti, Kasra; Haight, Richard; Anderson, Ryan

2016-06-22

Cryogenic focused ion beam (Cryo-FIB) milling at near-grazing angles is employed to fabricate cross-sections on thin Cu(In,Ga)Se2 with >8x expansion in thickness. Kelvin probe force microscopy (KPFM) on sloped cross sections showed reduction in grain boundaries potential deeper into the film. Cryo Fib-KPFM enabled the first determination of the electronic structure of the Mo/CIGSe back contact, where a sub 100 nm thick MoSey assists hole extraction due to 45 meV higher work function. This demonstrates that CryoFIB-KPFM combination can reveal new targets of opportunity for improvement in thin-films photovoltaics such as high-work-function contacts to facilitate hole extraction through the backmore » interface of CIGS.« less

Performance of CAD/CAM fabricated fiber posts in oval-shaped root canals: An in vitro study.

PubMed

Tsintsadze, Nino; Juloski, Jelena; Carrabba, Michele; Tricarico, Marella; Goracci, Cecilia; Vichi, Alessandro; Ferrari, Marco; Grandini, Simone

2017-10-01

To assess the push-out strength, the cement layer thickness and the interfacial nanoleakage of prefabricated fiber posts, CAD/CAM fiber posts and metal cast posts cemented into oval-shaped root canals. Oval-shaped post spaces were prepared in 30 single-rooted premolars. Roots were randomly assigned to three groups (n=10), according to the post type to be inserted: Group 1: Prefabricated fiber post (D.T. Light-Post X-RO Illusion); Group 2: Cast metal post; Group 3: CAD/CAM-fabricated fiber post (experimental fiber blocks). In Group 3, post spaces were sprayed with scan powder (VITA), scanned with an inEos 4.2 scanner, and fiber posts were milled using an inLab MC XL CAD/CAM milling unit. All posts were cemented using Gradia Core dual-cure resin cement in combination with Gradia core self-etching bond (GC). After 24 hours, the specimens were sectioned perpendicular to the long axis into six 1 mm-thick sections, which were differentiated by the root level. Sections from six roots per group were used to measure the cement thickness and subsequently for the thin-slice push-out test, whereas the sections from the remaining four teeth were assigned to interfacial nanoleakage test. The cement thickness around the posts was measured in micrometers (µm) on the digital images acquired with a digital microscope using the Digimizer software. Thin-slice push-out test was conducted using a universal testing machine at the crosshead speed of 0.5 mm/minute and the bond strength was expressed in megaPascals (MPa). The interfacial nanoleakage was observed under light microscope and quantified by scoring the depth of silver nitrate penetration along the post-cement-dentin interfaces. The obtained results were statistically analyzed by Kruskal-Wallis ANOVA, followed by the Dunn's Multiple Range test for post hoc comparisons. The level of significance was set at P< 0.05. Statistically significant differences were found among the groups in push-out bond strength, cement thickness and interfacial nanoleakage (P< 0.05). CAD/CAM-fabricated fiber posts achieved retention that was comparable to that of cast metal posts and significantly higher than that of prefabricated fiber posts. The cement layer thickness around CAD/CAM-fabricated fiber posts was significantly lower than around prefabricated fiber posts, but higher than that around cast metal posts. Root level was not a significant factor for push-out strength in any of the groups, whereas it significantly affected cement layer thickness only in the prefabricated fiber post group. No differences were observed in interfacial nanoleakage between CAD/CAM fabricated and prefabricated fiber posts, while nanoleakage recorded in cast metal posts was significantly lower. CAD/CAM fabricated fiber posts could represent a valid alternative to traditionally used posts in the restoration of endodontically-treated teeth with oval or wide root canals, offering the advantages of better esthetics, retention, and cement thickness values that are comparable to cast post and cores.

Freezing without Ice Crystal Damage: Semithin and Ultrathin Frozen Sections of Ethanol-Infiltrated Tissue for Microscopy, with Applications to Immunocytochemistry

NASA Astrophysics Data System (ADS)

Christensen, A. Kent; Lowry, Terry B.

1995-10-01

Ethanol (ethyl alcohol) has long been a standard reagent used in preparing tissues for light and electron microscopy. After fixation, tissues are usually dehydrated with ethanol before being embedded in paraffin or plastic. In this study we show that the ethanol-infiltrated tissue can be frozen and sectioned directly without embedding. When tissue impregnated with ethanol is cooled below about [minus sign]117°C with liquid nitrogen, the ethanol solidifies without appreciable crystallization. The frozen tissue can then be sectioned in a commercial cryoultramicrotome that is set at [minus sign]155 to [minus sign]170°C to produce semithin frozen sections (0.5 to 3 [mu]m thick) for light microscopy or ultrathin frozen sections (50 to 100 nm thick) for electron microscopy. Sections are picked up and mounted on glass slides or EM grids by means that are in current use for ice ultrathin frozen sectioning. Because there is no apparent freezing damage, the morphology in these ethanol frozen sections of unembedded tissue appears generally quite good, often resembling that obtained by conventional EM techniques. Examples are provided that illustrate the use of this material for immunocytochemistry at the light and electron microscope levels.

Dental cementum in age estimation: a polarized light and stereomicroscopic study.

PubMed

Kasetty, Sowmya; Rammanohar, M; Raju Ragavendra, T

2010-05-01

Dental hard tissues are good candidates for age estimation as they are less destructive and procedures to determine age can be easily performed. Although cementum annulations and cementum thickness are important parameters in this regard, they are seldom used. This study was undertaken to review the methods, difficulties in execution of techniques, and accuracy of cementum thickness and annulations in estimating the age. Unstained and stained ground sections of tooth were used to measure cemental thickness and count cemental annulations based on which age was estimated and was compared with known age. Although there was positive relation between cemental thickness and annulations with age, only in 1-1.5% of cases, age could be predicted with accuracy.

Correlation of Paleocene Harmon and Hansen lignite beds, Adams, Billings, Bowman, Golden Valley, Hettinger, and Slope Counties, Williston Basin, North Dakota

DOE Office of Scientific and Technical Information (OSTI.GOV)

Keighin, C.W.; Flores, R.M.; Ochs, A.

In southwestern North Dakota, minable lignite beds in the Paleocene Fort Union Formation include the Harmon and Hansen beds in the Bowman-Gascoyne area. Data from more than 700 drill holes penetrating these beds was used to construct stratigraphic cross sections. The Harmon and Hansen beds are the thickest and most laterally persistent lignites found under < 150 ft of overburden. The Harmon coal bed is as much as 34 ft thick, and is often split by claystone interbeds of variable thickness. The Hansen coal bed typically occurs 10--100 ft below the Harmon coal bed; it rarely attains a thickness ofmore » 15 ft, and averages 4 ft in thickness.« less

Mediterranean diet, micronutrients and macronutrients, and MRI measures of cortical thickness.

PubMed

Staubo, Sara C; Aakre, Jeremiah A; Vemuri, Prashanthi; Syrjanen, Jeremy A; Mielke, Michelle M; Geda, Yonas E; Kremers, Walter K; Machulda, Mary M; Knopman, David S; Petersen, Ronald C; Jack, Clifford R; Roberts, Rosebud O

2017-02-01

The Mediterranean diet (MeDi) is associated with reduced risk of cognitive impairment, but it is unclear whether it is associated with better brain imaging biomarkers. Among 672 cognitively normal participants (mean age, 79.8 years, 52.5% men), we investigated associations of MeDi score and MeDi components with magnetic resonance imaging measures of cortical thickness for the four lobes separately and averaged (average lobar). Higher MeDi score was associated with larger frontal, parietal, occipital, and average lobar cortical thickness. Higher legume and fish intakes were associated with larger cortical thickness: legumes with larger superior parietal, inferior parietal, precuneus, parietal, occipital, lingual, and fish with larger precuneus, superior parietal, posterior cingulate, parietal, and inferior parietal. Higher carbohydrate and sugar intakes were associated with lower entorhinal cortical thickness. In this sample of elderly persons, higher adherence to MeDi was associated with larger cortical thickness. These cross-sectional findings require validation in prospective studies. Copyright © 2016 the Alzheimer's Association. Published by Elsevier Inc. All rights reserved.

Finite plate thickness effects on the Rayleigh-Taylor instability in elastic-plastic materials

NASA Astrophysics Data System (ADS)

Polavarapu, Rinosh; Banerjee, Arindam

2017-11-01

The majority of theoretical studies have tackled the Rayleigh-Taylor instability (RTI) problem in solids using an infinitely thick plate. Recent theoretical studies by Piriz et al. (PRE 95, 053108, 2017) have explored finite thickness effects. We seek to validate this recent theoretical estimate experimentally using our rotating wheel RTI experiment in an accelerated elastic-plastic material. The test section consists of a container filled with air and mayonnaise (a non-Newtonian emulsion) with an initial perturbation between two materials. The plate thickness effects are studied by varying the depth of the soft-solid. A set of experiments is run by employing different initial conditions with different container dimensions. Additionally, the effect of acceleration rate (driving pressure rise time) on the instability threshold with reference to the finite thickness will also be inspected. Furthermore, the experimental results are compared to the analytical strength models related to finite thickness effects on RTI. Authors acknowledge financial support from DOE-SSAA Grant # DE-NA0003195 and LANL subcontract #370333.

Handling Golgi-impregnated tissue for light microscopy.

PubMed

Berbel, P J; Fairén, A

1983-08-08

The use of cyanocrylic glue to fix pieces of Golgi-stained nervous tissue on a paraffin blank is proposed for obtaining thick sections of unembedded tissue with a sliding microtome. This procedure makes correct orientation of the tissue easy during sectioning and makes it possible to obtain tissue sections quickly. The sections are flat-mounted using epoxy resin, resulting in permanent preparations with excellent optical properties and enabling further thin-sectioning for light and electron microscopic studies.

Lameness in dairy cattle: A debilitating disease or a disease of debilitated cattle? A cross-sectional study of lameness prevalence and thickness of the digital cushion.

PubMed

Bicalho, R C; Machado, V S; Caixeta, L S

2009-07-01

Lameness is the most significant challenge for the dairy industry to overcome, given its obvious disruption of animal welfare and severe economic losses. Sole ulcers and white line abscesses are ubiquitous chronic diseases with the highest associated economic losses among all foot lesions. Their underlying causes are still not fully understood. An observational cross-sectional study was carried out to investigate the association between claw horn lesions and the thickness of the digital cushion.The thickness of the digital cushion was evaluated by ultrasonographic examination of the sole at the typical ulcer site. A total of 501 lactating Holstein dairy cows were enrolled in the study. The prevalence of sole ulcers was 4.2 and 27.8% for parity 1 and parity >1, respectively.The prevalence of white line disease was 1.0 and 6.5% for parity 1 and >1, respectively. The prevalence of lameness (visual locomotion score > or = 3) was 19.8 and 48.2% for parity 1 and >1, respectively. The prevalence of sole ulcers and white line diseases was significantly associated with thickness of the digital cushion; cows in the upper quartile of digital cushion thickness had an adjusted prevalence of lameness 15 percentage points lower than the lower quartile. Body condition scores were positively associated with digital cushion thickness.The mean gray value of the sonographic image of the digital cushion had a negative linear association with digital cushion thickness (R2 = 0.14), indicating that the composition of the digital cushion may have changed with its thickness. Furthermore, digital cushion thickness decreased steadily from the first month of lactation and reached a nadir 120 d after parturition.These results support the concept that sole ulcers and white line abscesses are related to contusions within the claw horn capsule and such contusions are a consequence of the lesser capacity of the digital cushion to dampen the pressure exerted by the third phalanx on the soft tissue beneath.

Thick sequences of silicate and carbonate rocks of sedimentary origin in North America an interim report

USGS Publications Warehouse

Love, John David

1956-01-01

Thick sequences of silicate and carbonate rocks of sedimentary origin have been investigated in 64 areas in North America. The areas containing the thickest and most homogeneous stratigraphic sections more than 1,000 feet thick, buried at depths greater than 10,000 feet are: 1. Uinta Basin, Utah, where the Mancos shale is 1,300 to 5,000 feet thick, the Weber sandstone is 1,000 to 1,600 feet thick, and Mississippian limestones are 1,000 to 1,500 feet thick. 2. Washakie Basin, Wyoming, and Sand Wash Ba.sin, Colorado, where the Lewis shale is 1,000 to 2,000 feet thick and the Cody-Mancos shale is 4,500 to 5,500 feet thick. 3. Green River Basin, Wyoming, where the Cody-Hilliard-Baxter-Mancos shale sequence averages more than 3,000 feet, the siltstone and shale of the Chugwater formation totals 1,000 feet, and the Madison limestone ranges from 1,000 to 1,400 feet thick. 4. Red Desert (Great Divide) Basin, Wyoming, where the Cody shale is 4,000 feet thick. 5. Hanna Basin, Wyoming, where the Steele shale is 4,500 feet thick. 6. Wind River Basin, Wyoming, where the Cody shale is 3,600 to 5,000 feet thick. Geochemical characteristics of these rocks in these areas are poorly known but are being investigated. A summary of the most pertinent recent ana1yses is presented.

A study of static stability of airships

NASA Technical Reports Server (NTRS)

Rizzo, Frank

1924-01-01

The first section deals with the theoretical side of statical stability of airships in general. The second section deals with preliminary tests of the model and experiments for the determination of effects due to change of tail area, aspect ratio, tail form, and tail thickness.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Bond, Evelyn M.; Moody, W. Allen; Arnold, Charles

Here, the preparation of 191Ir and 193Ir electrodeposits for neutron capture cross-section measurements at the detector for advanced neutron capture experiments located at the at Los Alamos Neutron Science Center is described. The electrodeposition of iridium in the desired thickness of 0.4–1 mg/cm 2 is challenging. Better yields and thicknesses were obtained using electrodeposition from isopropyl alcohol solutions than from ammonium sulfate solutions. 191Ir and 193Ir targets were initially prepared using the standard single-sided electrodeposition cell. Iridium electrodepositions using a double-sided electrodeposition cell were developed and were optimized, resulting in thick, uniform iridium deposits. LA UR 15-22475.

Probing heat transfer, fluid flow and microstructural evolution during fusion welding of alloys

NASA Astrophysics Data System (ADS)

Zhang, Wei

The composition, geometry, structure and properties of the welded joints are affected by the various physical processes that take place during fusion welding. Understanding these processes has been an important goal in the contemporary welding research to achieve structurally sound and reliable welds. In the present thesis research, several important physical processes including the heat transfer, fluid flow and microstructural evolution in fusion welding were modeled based on the fundamentals of transport phenomena and phase transformation theory. The heat transfer and fluid flow calculation is focused on the predictions of the liquid metal convection in the weld pool, the temperature distribution in the entire weldment, and the shape and size of the fusion zone (FZ) and heat affected zone (HAZ). The modeling of microstructural evolution is focused on the quantitative understanding of phase transformation kinetics during welding of several important alloys under both low and high heating and cooling conditions. Three numerical models were developed in the present thesis work: (1) a three-dimensional heat transfer and free surface flow model for the gas metal arc (GMA) fillet welding considering the complex weld joint geometry, (2) a phase transformation model based on the Johnson-Mehl-Avrami (JMA) theory, and (3) a one-dimensional numerical diffusion model considering multiple moving interfaces. To check the capabilities of the developed models, several cases were investigated, in which the predictions from the models were compared with the experimental results. The cases studied are the follows. For the modeling of heat transfer and fluid flow, the welding processes studied included gas tungsten arc (GTA) linear welding, GTA transient spot welding, and GMA fillet welding. The calculated weldment geometry and thermal cycles was validated against the experimental data under various welding conditions. For the modeling of microstructural evolution, the welded materials investigated included AISI 1005 low-carbon steel, 1045 medium-carbon steel, 2205 duplex stainless steel (DSS) and Ti-6Al-4V alloy. The calculated phase transformation kinetics were compared with the experimental results obtained using an x-ray diffraction technique by Dr. John W. Elmer of Lawrence Livermore National Laboratory. (Abstract shortened by UMI.)

Two-photon coincident emission from thick targets for 70-keV incident electrons

NASA Astrophysics Data System (ADS)

Liu, J.; Kahler, D. L.; Quarles, C. A.

1993-04-01

Two-photon coincidence yields have been measured in thick targets of C, Al, Ag, and Ta for 70 keV incident electrons and photons radiated at +/-45° to the incident beam. A theoretical model, which is more rigorous, has been developed to simulate the two-photon processes of coherent thick-target double bremsstrahlung (TTDB) and the incoherent emission of two single-bremsstrahlung (SBSB) photons in a thick-target environment. The model is based on an integration of the thin-target cross sections over the target thickness taking into account electron energy loss, electron backscattering, and photon attenuation. It predicts a yield that is much lower than that of the previous model. The prediction of the model fits the present experimental data well by adjusting the relative weight of the two competing processes, and we find that TTDB dominates at low Z and incoherent SBSB dominates at higher Z.

Texture Adaption in Dysphagia: Acceptability Differences Between Thickened and Naturally Thick Beverages.

PubMed

Gerschke, Marco; Seehafer, Peggy

The aim of the study was to investigate differences in the acceptability between thickened and naturally viscous beverages. This was an exploratory, cross-sectional study. One hundred twenty-eight healthy volunteers rated overall liking/disliking of a selection of each of three thickened drinks and three beverages of natural viscosity pre- and postconsumption. Mean ratings were subjected to statistical analysis done with t tests. Although all naturally thick beverages evoked good expectations, there were significant differences in expected acceptance of thickened fluids concerning the kind of beverage. Postconsumption of naturally thick beverages were rated significantly better than thickened. The findings suggest an alternative offer of naturally thick drinks and waiver of thickening water when viscosity adaption is needed. The sufficient and safe oral fluid intake in dysphagia requires compliance to dietetic recommendations. Naturally thick beverages can contribute to increase the appeal of texture-modified diet.

Effect of shape and thickness of asbestos bundles and fibres on EDS microanalysis: A Monte Carlo simulation

NASA Astrophysics Data System (ADS)

Moro, D.; Valdre, G.

2016-02-01

Quantitative microanalysis of tiny asbestos mineral fibres by scanning electron microscopy equipped with energy-dispersive X-ray spectroscopy (SEM-EDS) still represents a complex analytical issue. This complexity arises from the variable fibre shape and small thickness (< 5 μm) compared with the penetration of the incident electron beam. Here, we present the results of Monte Carlo simulations of chrysotile, crocidolite and amosite fibres (and bundles of fibres) of circular and square section and thicknesses from 0.1 μm to 10 μm, to investigate the effect of shape and thickness on SEM-EDS microanalysis. The influence of shape and thickness on the simulated spectrum was investigated for electron beam energies of 5, 15 and 25 keV, respectively. A strong influence of the asbestos bundles and fibres shape and thickness on the detected EDS X-ray intensity was observed. The X-ray intensity trends as a function of fibre thickness showed a non-linear dependence for all the elements and minerals. In general, the X-ray intensities showed a considerable reduction for thicknesses below about 5 μm at 5 keV, 2 μm at 15 keV, and 5 μm at 25 keV. Correction parameters, k-ratios, for the asbestos fibre thickness effect, are reported.

Impacts of age and sex on retinal layer thicknesses measured by spectral domain optical coherence tomography with Spectralis.

PubMed

Nieves-Moreno, María; Martínez-de-la-Casa, José M; Morales-Fernández, Laura; Sánchez-Jean, Rubén; Sáenz-Francés, Federico; García-Feijoó, Julián

2018-01-01

To examine differences in individual retinal layer thicknesses measured by spectral domain optical coherence tomography (SD-OCT) (Spectralis®) produced with age and according to sex. Cross-sectional, observational study. The study was conducted in 297 eyes of 297 healthy subjects aged 18 to 87 years. In one randomly selected eye of each participant the volume and mean thicknesses of the different macular layers were measured by SD-OCT using the instrument's macular segmentation software. Volume and mean thickness of macular retinal nerve fiber layer (mRNFL), ganglion cell layer (GCL), inner plexiform layer (IPL), inner nuclear layer (INL), outer plexiform layer (OPL), outer nuclear layer (ONL), retinal pigmentary epithelium (RPE) and photoreceptor layer (PR). Retinal thickness was reduced by 0.24 μm for every one year of age. Age adjusted linear regression analysis revealed mean GCL, IPL, ONL and PR thickness reductions and a mean OPL thickness increase with age. Women had significantly lower mean GCL, IPL, INL, ONL and PR thicknesses and volumes and a significantly greater mRNFL volume than men. The thickness of most retinal layers varies both with age and according to sex. Longitudinal studies are needed to determine the rate of layer thinning produced with age.

49 CFR 178.47 - Specification 4DS welded stainless steel cylinders for aircraft use.

Code of Federal Regulations, 2010 CFR

2010-10-01

... both with a water capacity of not over 100 pounds and a service pressure of at least 500 but not over... (b) of this section. (f) Wall thickness. The minimum wall thickness must be such that the wall stress...) Calculation for sphere must be made by the formula: S = PD / 4tE Where: S = Wall stress in psi; P = Test...

FIBER AND INTEGRATED OPTICS: Waveguide characteristics of real optical strip waveguides

NASA Astrophysics Data System (ADS)

Shmal'ko, A. V.; Frolov, V. V.

1990-01-01

A study is reported of the influence of the parameters of real thin-film optical strip waveguides on their waveguide characteristics (propagation constants, localization of the mode field, etc.) allowing for the presence of transition layers in a transverse cross section of the base planar waveguide, for the real geometry of this section (which is nearly trapezoidal), and for the thickness of the guiding strip. Analytic expressions are obtained for the optical confinement coefficient and the effective mode format of a weakly guiding symmetric strip waveguide. It is shown that the coefficient representing the fundamental E11x(y) mode is practically independent of the relative thickness t /h (h is the thickness of the base planar waveguide) of the guiding strip provided t /h>=0.5. The corrections to the normalized effective refractive indices of the base planar and strip waveguides are found in order to allow for the real geometry and for the refractive index profile in the strip waveguide.

Geologic interpretation of gravity data from the Date Creek basin and adjacent areas, west-central Arizona

USGS Publications Warehouse

Otton, James K.; Wynn, Jeffrey C.

1978-01-01

A gravity survey of the Date Creek Basin and adjacent areas was conducted in June 1977 to provide information for the interpretation of basin geology. A comparison of facies relations in the locally uraniferous Chapin Wash Formation and the position of the Anderson mine gravity anomaly in the Date Creek Basin suggested that a relationship between gravity lows and the development of thick lacustrine sections in the region might exist. A second-order residual gravity map derived from the complete Bouguer gravity map for the survey area (derived from survey data and pre-existing U.S. Department of Defense data) shows an excellent correspondence between gravity lows and sediment-filled basins and suggests considerable variation in basin-fill thickness. Using the Anderson mine anomaly as a model, gravity data and facies relations suggest that the southeastern flank of the Aguila Valley gravity low and the gravity low at the western end of the Hassayampa Plain are likely areas for finding thick sections of tuffaceous lacustrine rocks.

Heavy-section welding with very high power laser beams: the challenge

NASA Astrophysics Data System (ADS)

Goussain, Jean-Claude; Becker, Ahim; Chehaibou, A.; Leca, P.

1997-08-01

The 45 kW CO2 laser system of Institut de Soudure was used to evaluate and explore the possibilities offered by the high power laser beams for welding different materials in various thickness and in different welding positions. Stainless steels, low carbon steels, aluminum and titanium alloys were studied. Butt joints in 10 to 35 mm thick plates were achieved and evaluated by radiographic, metallurgical and mechanical tests. Gaps and alignment tolerances were determined with and without filler wire in order to obtain acceptable welds concerning the weld geometry, the aspect on front and end root sides. The main problem raised by heavy section welding concerns weld porosity in the weld which increases drastically with the thickness of the weld. Indications are given on their origin and the way to proceed in order to better control them. Lastly some large parts, recently welded on the system, are presented and discussed before drawing some conclusions on the prospects of very high power laser welding.

Cometary particles - Thin sectioning and electron beam analysis

NASA Technical Reports Server (NTRS)

Bradley, J. P.; Brownlee, D. E.

1986-01-01

Thin sections (500 to 1000 angstroms thick) of individual micrometeorites (5 to 15 micrometers) have been prepared with an ultramicrotome equipped with a diamond knife. Electron microscope examination of these sections has revealed the internal structures of chondritic micrometeorites, and a subset of highly porous, fragile particles has been identified. Delicate meteoritic materials such as these are characteristic of debris from cometary meteors.

Confined Impinging Jets in Porous Media

NASA Astrophysics Data System (ADS)

Buonomo, B.; Cirillo, L.; Manca, O.; Mansi, N.; Nardini, S.

2016-09-01

Impinging jets are adopted in drying of textiles, paper, cooling of gas turbine components, freezing of tissue in cryosurgery and manufacturing, electronic cooling. In this paper an experimental investigation is carried out on impinging jets in porous media with the wall heated from below with a uniform heat flux. The fluid is air. The experimental apparatus is made up of a fun systems, a test section, a tube, to reduce the section in a circular section. The tube is long 1.0 m and diameter of 0.012 m. The test section has a diameter of 0.10 m and it has the thickness of 10, 20 and 40 mm. In the test section the lower plate is in aluminum and is heated by an electrical resistance whereas the upper plate is in Plexiglas. The experiments are carried out employing a aluminum foam 40 PPI at three thickness as the test section. Results are obtained in a Reynolds number range from 5100 to 15300 and wall heat flux range from 510 W/m2 to 1400 W/m2. Results are given in terms of wall temperature profiles, local and average Nusselt numbers, pressure drops, friction factor and Richardson number.

Retinal Thickness Analysis by Race, Gender, and Age Using Stratus OCT™

PubMed Central

Kashani, Amir H.; Zimmer-Galler, Ingrid E.; Shah, Syed Mahmood; Dustin, Laurie; Do, Diana V.; Eliott, Dean; Haller, Julia A.; Nguyen, Quan Dong

2010-01-01

PURPOSE To detect differences in retinal thickness among patients of different race, gender and age using Stratus OCT™. DESIGN Cross-sectional study. METHODS In a multicenter, university-based study, 126 patients with no history of ocular disease were enrolled (78 diabetics without retinopathy and 48 nondiabetics). Optical coherence tomography measurements were performed using Stratus OCT™. Statistical comparisons of centerpoint foveal thickness and mean foveal thickness were made using generalized estimating equations adjusting for diabetic status, race, age, and gender. RESULTS The study population consisted of 36% males, 39% Caucasians, 33% African Americans, and 28% Hispanics. Mean foveal thickness was 191.6±2.7µm and 194.5±2.7µm for diabetics and nondiabetics, respectively (P=0.49). Mean foveal thickness in males was significantly larger than in females (201.8±2.7µm and 186.9±2.6µm, respectively; P<0.001). Mean foveal thickness was 200.2±2.7µm for Caucasians, 181.0±3.7µm for African Americans, and 194.7±3.9µm for Hispanics. Mean foveal thickness was significantly less for African Americans than Caucasians (P <0.0001) or Hispanics (P=0.005). Centerpoint foveal thickness and mean foveal thickness showed a significant increase with age. CONCLUSIONS There are statistically significant differences in retinal thickness between subjects of different race, gender, and age. When compared to Caucasians and Hispanics, African-American race is a predictor of decreased mean foveal thickness; and male sex (regardless of race) is a significant predictor of increased mean foveal thickness. Mean foveal thickness is similar among diabetics and nondiabetics when data are controlled for age, race, and sex. These results suggest that studies comparing OCT measurements should carefully control for age, race, and gender-based variations in retinal thickness. PMID:20042179

Normative values for optical coherence tomography parameters in healthy children and interexaminer agreement for choroidal thickness measurements.

PubMed

Turan, Kadriye Erkan; Sekeroglu, Hande Taylan; Baytaroglu, Ata; Bezci, Figen; Karahan, Sevilay

2018-01-01

To (a) determine the normative values for optical coherence tomography (OCT) parameters such as central macular thickness, retinal nerve fiber layer thickness, and choroidal thickness in healthy children; (b) investigate the relationships of these parameters with axial length, central corneal thickness, refractive errors, and intraocular pressure; and (c) determine interexaminer agreement for choroidal thickness measurements. In this cross-sectional study, 120 healthy children aged 8-15 years underwent detailed ophthalmological examination and OCT measurements. Choroidal thickness was measured at three separate locations by two independent examiners. The mean global retinal nerve fiber layer thickness was 98.75 ± 9.45 μm (79.0-121.0). The mean central macular thickness was 232.29 ± 29.37 μm (190.0-376.0). The mean subfoveal choroidal thickness obtained by examiner 1 was 344.38 ± 68.83 μm and that obtained by examiner 2 was 344.04 ± 68.92 μm. Interexaminer agreement was between 99.6%-99.8% for choroidal thickness at three separate locations. Central macular thickness increased with axial length (r=0.245, p=0.007). Choroidal thickness increased with age (r=0.291, p=0.001) and decreased with axial length (r=-0.191, p=0.037). Global retinal nerve fiber layer thickness decreased with axial length (r=-0.247, p=0.007) and increased with central corneal thickness (r=0.208, p=0.022). Global retinal nerve fiber layer thickness positively correlated with choroidal thickness (r=0.354, p<0.001). Global retinal nerve fiber layer thickness (r=0.223, p=0.014) and choroidal thickness (r=0.272, p=0.003) increased with the spherical equivalent (D). Optical coherence tomography parameters showed a wide range of variability in children. Retinal nerve fiber layer thickness, central macular thickness, and choroidal thickness were found to be either inter-related or correlated with age, central corneal thickness, axial length, and refractive errors. Furthermore, manual measurements of choroidal thickness showed high interexaminer agreement. Because normative values for optical coherence tomography parameters differed in children, the measurements should be interpreted according to an age-appropriate database.

Life prediction and constitutive models for engine hot section anisotropic materials

NASA Technical Reports Server (NTRS)

Swanson, G. A.

1984-01-01

The development of directionally solidified and single crystal alloys is perhaps the most important recent advancement in hot section materials technology. The objective is to develop knowledge that enables the designer to improve anisotropic gas turbine parts to their full potential. Two single crystal alloys selected were PWA 1480 and Alloy 185. The coatings selected were an overlay coating, PWA 286, and an aluminide diffusion coating, PWA 273. The constitutive specimens were solid and cylindrical; the fatigue specimens were hollow and cylindrical. Two thicknesses of substrate are utilized. Specimens of both thickness (0.4 and 1.5 mm) will be coated and then tested for tensile, creep, and fatigue properties.

Joining thick section aluminum to steel with suppressed FeAl intermetallic formation via friction stir dovetailing

DOE Office of Scientific and Technical Information (OSTI.GOV)

Reza-E-Rabby, Md.; Ross, Kenneth; Overman, Nicole R.

A new solid-phase technique called friction stir dovetailing (FSD) has been developed for joining thick section aluminum to steel. In FSD, mechanical interlocks are formed at the aluminum-steel interface and are reinforced by metallurgical bonds where intermetallic growth has been uniquely suppressed. Lap shear testing shows superior strength and extension at failure compared to popular friction stir approaches where metallurgical bonding is the only joining mechanism. High resolution microscopy revealed the presence of a 40-70 nm interlayer having a composition of 76.4 at% Al, 18.4 at% Fe, and 5.2 at% Si, suggestive of limited FeAl3 intermetallic formation.

Shear-horizontal vibration modes of an oblate elliptical cylinder and energy trapping in contoured acoustic wave resonators.

PubMed

He, Huijing; Yang, Jiashi; Kosinski, John A

2012-08-01

We study shear-horizontal free vibrations of an elastic cylinder with an oblate elliptical cross section and a traction-free surface. Exact vibration modes and frequencies are obtained. The results show the existence of thickness-shear and thickness-twist modes. The energy-trapping behavior of these modes is examined. Trapped modes are found wherein the vibration energy is largely confined to the central portion of the cross section and little vibration energy is found at the edges. It is also shown that face-shear modes are not allowed in such a cylinder. The results are useful for the understanding of the energy trapping phenomenon in contoured acoustic wave resonators.

Collection, processing, and interpretation of ground-penetrating radar data to determine sediment thickness at selected locations in Deep Creek Lake, Garrett County, Maryland, 2007

USGS Publications Warehouse

Banks, William S.L.; Johnson, Carole D.

2011-01-01

This investigation focused on selected regions of the study area, particularly in the coves where sediment accumulations were presumed to be thickest. GPR was the most useful tool for interpreting sediment thickness, especially in these shallow coves. The radar profiles were interpreted for two surfaces of interest-the water bottom, which was defined as the "2007 horizon," and the interface between Lake sediments and the original Lake bottom, which was defined as the "1925 horizon"-corresponding to the year the Lake was impounded. The ground-penetrating radar data were interpreted on the basis of characteristics of the reflectors. The sediments that had accumulated in the impounded Lake were characterized by laminated, parallel reflections, whereas the subsurface below the original Lake bottom was characterized by more discontinuous and chaotic reflections, often with diffractions indicating cobbles or boulders. The reflectors were picked manually along the water bottom and along the interface between the Lake sediments and the pre-Lake sediments. A simple graphic approach was used to convert traveltimes to depth through water and depth through saturated sediments using velocities of the soundwaves through the water and the saturated sediments. Nineteen cross sections were processed and interpreted in 9 coves around Deep Creek Lake, and the difference between the 2007 horizon and the 1925 horizon was examined. In most areas, GPR data indicate a layer of sediment between 1 and 7 feet thick. When multiple cross sections from a single cove were compared, the cross sections indicated that sediment thickness decreased toward the center of the Lake.

Experimental Studies on Geocells and Mat Systems for Stabilization of Unpaved Shoulders and Temporary Roads

NASA Astrophysics Data System (ADS)

Guo, Jun

Geosynthetics have been used to improve the performance of geomaterials, especially when weak soil exists in roadway applications. In this study, two types of geosynthetic materials, geocell and a mat system, were studied for their applications for unpaved roads and shoulders. The study of geocell was focused on its application for unpaved shoulders. The ability of geocell to improve different geomaterials over intermediate strength subgrade and its possible effect on vegetation were investigated. The study of the mat system was focused on investigating the performance of the mat system over soft and intermediate subgrade with different strengths under cyclic loading to simulate temporary roadway conditions. In the study of geocell for the application for unpaved shoulders, six large scale plate loading tests were conducted on a single type of geocell on target 5% CBR subgrade to investigate the benefits of geocell reinforcement on different base course and topsoil combinations. Different base course and topsoil combinations were investigated including: 200-mm thick unreinforced aggregate, 200-mm thick soil-aggregate mixture (50% aggregate and 50% top soil) with and without geocell reinforcement, 200-mm thick geocell-reinforced topsoil, 50-mm thick aggregate over 150-mm soil-aggregate mixture (50% aggregate and 50% top soil), and 50-mm thick top soil over 150-mm thick geocell-reinforced soil-aggregate mixture (50% aggregate and 50% top soil). Earth pressure cells were install at the interface between subgrade and base course to monitor the load distribution. The cyclic plate loading tests showed that geocell effectively reduced the permanent deformation and the geocell-reinforced soil-aggregate mixture slightly outperformed the unreinforced aggregate at the same thickness. The plate loading tests also suggested the topsoil cover resulted in large permanent deformations. A one-year long outdoor field vegetation test was conducted on base courses with different combinations of aggregate and topsoil including: 200-mm thick unreinforced topsoil, 200-mm thick soil-aggregate mixture (50% aggregate and 50% topsoil), 50-mm thick aggregate over 150-mm soil-aggregate mixture (50% aggregate and 50% topsoil), and 50-mm thick topsoil over 150-mm reinforced soil-aggregate mixture (50% aggregate and 50% topsoil) to investigate the possible effect of geocell on shoulder vegetation established mainly by tall fescue grass and perennial ryegrass. One control (unreinforced) section and one geocell-reinforced section were prepared for each base course combination with a surface area of 1.5 m by 1.5 m. During the one-year test period, soil moisture temperature and volumetric moisture content were monitored. Weather data, such as precipitation and air temperature, were obtain from the nearby weather station at the Lawrence airport. Vegetation growth was evaluated by grass leaf blade length, root length, and grass density. Vegetation biomass was obtained at the end of the test. The test results showed no definite evidence of geocell influencing the vegetation in unpaved shoulders. In the study of the mat system, six large-scale cyclic plate loading tests were conducted on a single type of polyethylene mat system with anchorage to study its performance over soft and intermediate subgrade with the CBR ranging from 1% to 4%. For the comparison purposes, test sections with and without the mat system were prepared and evaluated. For the test section with 1% CBR subgrade, an aggregate base course was used for the test section without the mat system to enable the cyclic plate loading test. The size of the mat system under the investigation was 1.92 m by 1.92 m. A cyclic load at the magnitude of 40 kN was applied through a 300 mm diameter loading plate with a thin rubber pad to simulate a vehicle tire. Earth pressure cells were installed at the interface between the mat system and the subgrade to monitor the load distribution. Loading plate displacements were measured by the displacement transducer inside the actuator. Test results concluded that the mat system was more effective over the intermediate subgrade than the soft subgrade and when large permanent deformations were allowed.

Retinal thickness on Stratus optical coherence tomography in people with diabetes and minimal or no diabetic retinopathy.

PubMed

Bressler, Neil M; Edwards, Allison R; Antoszyk, Andrew N; Beck, Roy W; Browning, David J; Ciardella, Antonio P; Danis, Ronald P; Elman, Michael J; Friedman, Scott M; Glassman, Adam R; Gross, Jeffrey G; Li, Helen K; Murtha, Timothy J; Stone, Thomas W; Sun, Jennifer K

2008-05-01

To evaluate optical coherence tomography (OCT) thickness of the macula in people with diabetes but minimal or no retinopathy and to compare these findings with published normative data in the literature from subjects reported to have no retinal disease. Cross-sectional study. In a multicenter community- and university-based practices setting, 97 subjects with diabetes with no or minimal diabetic retinopathy and no central retinal thickening on clinical examination and a center point thickness of 225 microm or less on OCT (Stratus OCT; Carl Zeiss Meditec, Dublin, California, USA) were recruited. Electronic Early Treatment of Diabetic Retinopathy Study best-corrected visual acuity, seven-field stereoscopic color fundus photographs, and Stratus OCT fast macular scan were noted. Main outcome measures were central subfield (CSF) thickness measured on Stratus OCT. On average, CSF thickness was 201 +/- 22 microm. CSF thickness was significantly greater in retinas from men than retinas from women (mean +/- standard deviation, 209 +/- 18 microm vs 194 +/- 23 microm; P < .001). After adjusting for gender, no additional factors were found to be associated significantly with CSF thickness (P > .10). CSF thicknesses on Stratus OCT in people with diabetes and minimal or no retinopathy are similar to thicknesses reported from a normative database of people without diabetes. CSF thickness is greater in men than in women, consistent with many, but not all, previous reports. Studies involving comparisons of retinal thickness with expected norms should consider different mean values for women and men.

Prenatal factors associated with the neonatal line thickness in human deciduous incisors.

PubMed

Kurek, M; Żądzińska, E; Sitek, A; Borowska-Strugińska, B; Rosset, I; Lorkiewicz, W

2015-06-01

The neonatal line (NNL) is used to distinguish developmental events observed in enamel which occurred before and after birth. However, there are few studies reporting relationship between the characteristics of the NNL and factors affecting prenatal conditions. The aim of the study was to determine prenatal factors that may influence the NNL thickness in human deciduous teeth. The material consisted of longitudinal ground sections of 60 modern human deciduous incisors obtained from full-term healthy children with reported birth histories and prenatal factors. All teeth were sectioned in the labio-lingual plane using diamond blade (Buechler IsoMet 1000). Final specimens were observed using scanning electron microscopy at magnifications 320×. For each tooth, linear measurements of the NNL thickness were taken on its labial surface at the three levels from the cemento-enamel junction. The difference in the neonatal line thickness between tooth types and between males and females was statistically significant. A multiple regression analyses confirmed influence of two variables on the NNL thickness standardised on tooth type and the children's sex (z-score values). These variables are the taking of an antispasmodic medicine by the mother during pregnancy and the season of the child's birth. These two variables together explain nearly 17% of the variability of the NNL. Children of mothers taking a spasmolytic medicine during pregnancy were characterised by a thinner NNL compared with children whose mothers did not take such medication. Children born in summer and spring had a thinner NNL than children born in winter. These results indicate that the prenatal environment significantly contributes to the thickness of the NNL influencing the pace of reaching the post-delivery homeostasis by the newborn's organism. Copyright © 2014 Elsevier GmbH. All rights reserved.

Evidence for tectonic, lithologic, and thermal controls on fracture system geometries in an andesitic high-temperature geothermal field

NASA Astrophysics Data System (ADS)

Massiot, Cécile; Nicol, Andrew; McNamara, David D.; Townend, John

2017-08-01

Analysis of fracture orientation, spacing, and thickness from acoustic borehole televiewer (BHTV) logs and cores in the andesite-hosted Rotokawa geothermal reservoir (New Zealand) highlights potential controls on the geometry of the fracture system. Cluster analysis of fracture orientations indicates four fracture sets. Probability distributions of fracture spacing and thickness measured on BHTV logs are estimated for each fracture set, using maximum likelihood estimations applied to truncated size distributions to account for sampling bias. Fracture spacing is dominantly lognormal, though two subordinate fracture sets have a power law spacing. This difference in spacing distributions may reflect the influence of the andesitic sequence stratification (lognormal) and tectonic faults (power law). Fracture thicknesses of 9-30 mm observed in BHTV logs, and 1-3 mm in cores, are interpreted to follow a power law. Fractures in thin sections (˜5 μm thick) do not fit this power law distribution, which, together with their orientation, reflect a change of controls on fracture thickness from uniform (such as thermal) controls at thin section scale to anisotropic (tectonic) at core and BHTV scales of observation. However, the ˜5% volumetric percentage of fractures within the rock at all three scales suggests a self-similar behavior in 3-D. Power law thickness distributions potentially associated with power law fluid flow rates, and increased connectivity where fracture sets intersect, may cause the large permeability variations that occur at hundred meter scales in the reservoir. The described fracture geometries can be incorporated into fracture and flow models to explore the roles of fracture connectivity, stress, and mineral precipitation/dissolution on permeability in such andesite-hosted geothermal systems.

Imaging retinal nerve fiber bundles using optical coherence tomography with adaptive optics.

PubMed

Kocaoglu, Omer P; Cense, Barry; Jonnal, Ravi S; Wang, Qiang; Lee, Sangyeol; Gao, Weihua; Miller, Donald T

2011-08-15

Early detection of axonal tissue loss in retinal nerve fiber layer (RNFL) is critical for effective treatment and management of diseases such as glaucoma. This study aims to evaluate the capability of ultrahigh-resolution optical coherence tomography with adaptive optics (UHR-AO-OCT) for imaging the RNFL axonal bundles (RNFBs) with 3×3×3μm(3) resolution in the eye. We used a research-grade UHR-AO-OCT system to acquire 3°×3° volumes in four normal subjects and one subject with an arcuate retinal nerve fiber layer defect (n=5; 29-62years). Cross section (B-scans) and en face (C-scan) slices extracted from the volumes were used to assess visibility and size distribution of individual RNFBs. In one subject, we reimaged the same RNFBs twice over a 7month interval and compared bundle width and thickness between the two imaging sessions. Lastly we compared images of an arcuate RNFL defect acquired with UHR-AO-OCT and commercial OCT (Heidelberg Spectralis). Individual RNFBs were distinguishable in all subjects at 3° retinal eccentricity in both cross-sectional and en face views (width: 30-50μm, thickness: 10-15μm). At 6° retinal eccentricity, RNFBs were distinguishable in three of the five subjects in both views (width: 30-45μm, thickness: 20-40μm). Width and thickness RNFB measurements taken 7months apart were strongly correlated (p<0.0005). Mean difference and standard deviation of the differences between the two measurement sessions were -0.1±4.0μm (width) and 0.3±1.5μm (thickness). UHR-AO-OCT outperformed commercial OCT in terms of clarity of the microscopic retina. To our knowledge, these are the first measurements of RNFB cross section reported in the living human eye. Copyright © 2011 Elsevier Ltd. All rights reserved.

Imaging retinal nerve fiber bundles using optical coherence tomography with adaptive optics

PubMed Central

Kocaoglu, Omer P.; Cense, Barry; Jonnal, Ravi S.; Wang, Qiang; Lee, Sangyeol; Gao, Weihua; Miller, Donald T.

2011-01-01

Early detection of axonal tissue loss in retinal nerve fiber layer (RNFL) is critical for effective treatment and management of diseases such as glaucoma. This study aims to evaluate the capability of ultrahigh-resolution optical coherence tomography with adaptive optics (UHR-AO-OCT) for imaging the RNFL axonal bundles (RNFBs) with 3×3×3 μm3 resolution in the eye. We used a research-grade UHR-AO-OCT system to acquire 3°×3° volumes in four normal subjects and one subject with an arcuate retinal nerve fiber layer defect (n=5; 29–62yrs). Cross section (B-scans) and en face (C-scan) slices extracted from the volumes were used to assess visibility and size distribution of individual RNFBs. In one subject, we reimaged the same RNFBs twice over a seven month interval and compared bundle width and thickness between the two imaging sessions. Lastly we compared images of an arcuate RNFL defect acquired with UHR-AO-OCT and commercial OCT (Heidelberg Spectralis). Individual RNFBs were distinguishable in all subjects at 3° retinal eccentricity in both cross-sectional and en face views (width: 30–50μm, thickness: 10–15μm). At 6° retinal eccentricity, RNFBs were distinguishable in three of the five subjects in both views (width: 30–45μm, thickness: 20–40μm). Width and thickness RNFB measurements taken seven months apart were strongly correlated (p<0.0005). Mean difference and standard deviation of the differences between the two measurement sessions were −0.1±4.0 μm (width) and 0.3±1.5 μm (thickness). UHR-AO-OCT outperformed commercial OCT in terms of clarity of the microscopic retina. To our knowledge, these are the first measurements of RNFB cross section reported in the living human eye. PMID:21722662

Electron Microscopy of Ultrathin Sections of Sporosarcina ureae

PubMed Central

Mazanec, K.; Kocur, M.; Martinec, T.

1965-01-01

Mazanec, K. (J. E. Purkyně University, Brno, Czechoslovakia), M. Kocur, and T. Martinec. Electron microscopy of ultrathin sections of Sporosarcina ureae. J. Bacteriol. 90:808–816. 1965.—Ultrathin sections of Sporosarcina ureae cells were studied by means of electron microscopy. The cell wall consists of several layers and is 340 A thick. The cytoplasm is of globular structure and includes ribosomelike structures, occasional mesosomes, and inclusions not precisely identifiable. The nuclear area has various shapes and is formed by filaments 10 to 20 A thick which proceed in various directions. Cell division occurs similarly to that of sarcinate. Both synchronic and asynchronic cell division was observed. The spores of S. ureae consist of an outer coat having several layers, a cortex, a spore wall, and cytoplasm. The results of the present investigation substantiate our previous suggestion that S. ureae should be transferred from the family Micrococcaceae to the family Bacillaceae. Images PMID:16562085

Micromorphological investigations of the Late Quaternary loess-paleosol sequences of the Kashmir Valley, India

NASA Astrophysics Data System (ADS)

Dar, Reyaz Ahmad; Chandra, Rakesh; Romshoo, Shakil Ahmad; Kowser, Nazia

2015-11-01

The loess-paleosol sequences of the Karewa Group preserve a valuable repository of the Late Quaternary climatic changes and the landscape evolution history of the Karewa Basin of Kashmir Valley in their lithological and pedogenic records. Three representative loess-paleosol sections at Shankerpora (SP), Khan Sahib (KS) and Pattan (PT) localities were chosen for detailed lithostratigraphic fieldwork and micromorphological observations of thin sections. Lithostratigraphic analysis revealed lateral and vertical variation in thickness and number of paleosol profiles from south-west to north-west of the Karewa Basin suggesting the availability of land-surface for periodic loess deposition. The SP section is marked by 6 (SP-S6, S7, S8, S9, S10, S12), KS section by 3 (KS-S2, S4, S5) and PT section by 2 (PT-S1, S3) thick mature paleosol profiles. Theses paleosols have well developed 'Ah' and 'Btk' horizons representing prolonged land-surface stability when pedogenic processes outpace loess deposition. On the other hand comparatively thin to thick paleosol profiles represent weak to moderate pedogenic maturity indicating short stratigraphic breaks with rapid loess deposition. Micromorphological observations of thin sections suggested that clay illuviation and CaCO3 accumulation have operated within the paleosol profiles. CaCO3 features are often associated with clay coatings suggesting decalcification of carbonates followed by clay illuviation. Pedogenic CaCO3 probably resulted from the precipitation of the soil solution near the average depth of wetting front. The pedogenic CaCO3, illuvial clay, mottles, iron manganese features, pedal microstructure and blocky aggregates reveal variation in the pedogenic maturity among and within the loess-paleosol sections. The morphological (both micro- and macro-morphological) attributes of loess-paleosols suggest variation of climatic conditions during the Late Quaternary period in the Karewa Basin of Kashmir Valley, India.

Numerical natural rubber curing simulation, obtaining a controlled gradient of the state of cure in a thick-section part

NASA Astrophysics Data System (ADS)

El Labban, A.; Mousseau, P.; Bailleul, J. L.; Deterre, R.

2007-04-01

Although numerical simulation has proved to be a useful tool to predict the rubber vulcanization process, few applications in the process control have been reported. Because the end-use rubber properties depend on the state of cure distribution in the parts thickness, the prediction of the optimal distribution remains a challenge for the rubber industry. The analysis of the vulcanization process requires the determination of the thermal behavior of the material and the cure kinetics. A nonisothermal vulcanization model with nonisothermal induction time is used in this numerical study. Numerical results are obtained for natural rubber (NR) thick-section part curing. A controlled gradient of the state of cure in the part thickness is obtained by a curing process that consists not only in mold heating phase, but also a forced convection mold cooling phase in order to stop the vulcanization process and to control the vulcanization distribution. The mold design that allows this control is described. In the heating phase, the state of cure is mainly controlled by the chemical kinetics (the induction time), but in the cooling phase, it is the heat diffusion that controls the state of cure distribution. A comparison among different cooling conditions is shown and a good state of cure gradient control is obtained.

Determination of integral cross sections of 3H in Al foils monitors irradiated by protons with energies ranging from 40 to 2600 MeV

NASA Astrophysics Data System (ADS)

Titarenko, Yu. E.; Batyaev, V. F.; Chauzova, M. V.; Chauzova, M. V.; Kashirin, I. A.; Malinovskiy, S. V.; Pavlov, K. V.; Rogov, V. I.; Titarenko, A. Yu.; Zhivun, V. M.; Mashnik, S. G.; Stankovskiy, A. Yu.

2016-05-01

The results of 3H production in Al foil monitors (˜ 59 mg/cm2 thickness) are presented. These foils have been irradiated in 15×15 mm polyethylene bags of ˜ 14 mg/cm2 thickness together with foils of Cr (˜ 395 mg/cm2 thickness) and 56Fe (˜ 332 mg/cm2 thickness) by protons of different energies in a range of 0.04 - 2.6 GeV. The diameters of all the foils were 10.5 mm. The irradiations were carried out at the ITEP accelerator U-10 under the ISTC Project # 3266 in 2006-2009. 3H has been extracted from Al foils using an A307 Sample Oxidizer. An ultra low level liquid scintillation spectrometer Quantulus1220 was used to measure the 3H β-spectra and the SpectraDec software package was applied for spectra processing, deconvolution and 3H activity determination. The values of the Al (p, x)3H reaction cross sections obtained in these experiments are compared with data measured at other labs and with results of simulations by the MCNP6 radiation transport code using the CEM03.03 event generator.

Thickness Distribution of Glenohumeral Joint Cartilage.

PubMed

Schleich, Christoph; Bittersohl, Bernd; Antoch, Gerald; Krauspe, Rüdiger; Zilkens, Christoph; Kircher, Jörn

2017-04-01

High-resolution 3-dimensional cartilage-specific magnetic resonance imaging (MRI) was performed at 3 T to test the following hypotheses: (1) there is a nonuniform cartilage thickness distribution both on the proximal humerus and on the glenoid surface and (2) the glenohumeral joint as a combined system is congruent with the level of the joint cartilage surface without substantial radial mismatch. Inclusion of 38 volunteers (19 females, mean age 24.34 ± 2.22 years; range 21-29 years) in a prospective study. Measurements of: cartilage thickness in 3 regions and 3 zones; radius of both circles (glenoid and humeral cartilage) for congruency calculation using 3-T MRI with 3-dimensional dual-echo steady-state sequence with water excitation. A homogenous mean cartilage thickness (1.2-1.5 mm) and slightly higher values for the glenoidal articulating surface radii both in the mid-paracoronar section (2.4 vs. 2.1 cm, P < 0.001) and in the mid-paraaxial section (2.4 vs. 2.1 cm, P < 0.001) compared with the humeral side were observed. The concept of a radial mismatch between the humeral head and the glenoid in healthy human subjects can be confirmed. This study provides normative data for the comparison of joint cartilage changes at the shoulder for future studies.

Determination of integral cross sections of 3 H in Al foils monitors irradiated by protons with energies ranging from 40 to 2600 MeV

DOE PAGES

Titarenko, Yu. E.; Batyaev, V. F.; Chauzova, M. V.; ...

2016-01-01

Our results of 3H production in Al foil monitors (~ 59 mg/cm 2 thickness) are presented. We irradiated these foils in 15×15 mm polyethylene bags of ~ 14 mg/cm 2 thickness together with foils of Cr (~ 395 mg/cm 2 thickness) and 56Fe (~ 332 mg/cm 2 thickness) by protons of different energies in a range of 0.04 – 2.6 GeV. The diameters of all the foils were 10.5 mm. The irradiations were carried out at the ITEP accelerator U–10 under the ISTC Project # 3266 in 2006–2009. 3H has been extracted from Al foils using an A307 Sample Oxidizer.more » We then used an ultra low level liquid scintillation spectrometer Quantulus1220 to measure the 3H β–spectra and the SpectraDec software package was applied for spectra processing, deconvolution and 3H activity determination. The values of the Al (p, x) 3H reaction cross sections obtained in these experiments are compared with data measured at other labs and with results of simulations by the MCNP6 radiation transport code using the CEM03.03 event generator.« less

Thickness Distribution of Glenohumeral Joint Cartilage

PubMed Central

Schleich, Christoph; Bittersohl, Bernd; Antoch, Gerald; Krauspe, Rüdiger; Zilkens, Christoph; Kircher, Jörn

2016-01-01

High-resolution 3-dimensional cartilage-specific magnetic resonance imaging (MRI) was performed at 3 T to test the following hypotheses: (1) there is a nonuniform cartilage thickness distribution both on the proximal humerus and on the glenoid surface and (2) the glenohumeral joint as a combined system is congruent with the level of the joint cartilage surface without substantial radial mismatch. Inclusion of 38 volunteers (19 females, mean age 24.34 ± 2.22 years; range 21-29 years) in a prospective study. Measurements of: cartilage thickness in 3 regions and 3 zones; radius of both circles (glenoid and humeral cartilage) for congruency calculation using 3-T MRI with 3-dimensional dual-echo steady-state sequence with water excitation. A homogenous mean cartilage thickness (1.2-1.5 mm) and slightly higher values for the glenoidal articulating surface radii both in the mid-paracoronar section (2.4 vs. 2.1 cm, P < 0.001) and in the mid-paraaxial section (2.4 vs. 2.1 cm, P < 0.001) compared with the humeral side were observed. The concept of a radial mismatch between the humeral head and the glenoid in healthy human subjects can be confirmed. This study provides normative data for the comparison of joint cartilage changes at the shoulder for future studies. PMID:28345405

Impact of Age and Aerobic Exercise Training on Conduit Artery Wall Thickness: Role of the Shear Pattern.

PubMed

Tanahashi, Koichiro; Kosaki, Keisei; Sawano, Yuriko; Yoshikawa, Toru; Tagawa, Kaname; Kumagai, Hiroshi; Akazawa, Nobuhiko; Maeda, Seiji

2017-01-01

Hemodynamic shear stress is the frictional force of blood on the arterial wall. The shear pattern in the conduit artery affects the endothelium and may participate in the development and progression of atherosclerosis. We investigated the role of the shear pattern in age- and aerobic exercise-induced changes in conduit artery wall thickness via cross-sectional and interventional studies. In a cross-sectional study, we found that brachial shear rate patterns and brachial artery intima-media thickness (IMT) correlated with age. Additionally, brachial artery shear rate patterns were associated with brachial artery IMT in 102 middle-aged and older individuals. In an interventional study, 39 middle-aged and older subjects were divided into 2 groups: control and exercise. The exercise group completed 12 weeks of aerobic exercise training. Aerobic exercise training significantly increased the antegrade shear rate and decreased the retrograde shear rate and brachial artery IMT. Moreover, changes in the brachial artery antegrade shear rate and the retrograde shear rate correlated with the change in brachial artery IMT. The results of the present study indicate that changes in brachial artery shear rate patterns may contribute to age- and aerobic exercise training-induced changes in brachial artery wall thickness. © 2017 S. Karger AG, Basel.

Mach Number effects on turbulent superstructures in wall bounded flows

NASA Astrophysics Data System (ADS)

Kaehler, Christian J.; Bross, Matthew; Scharnowski, Sven

2017-11-01

Planer and three-dimensional flow field measurements along a flat plat boundary layer in the Trisonic Wind Tunnel Munich (TWM) are examined with the aim to characterize the scaling, spatial organization, and topology of large scale turbulent superstructures in compressible flow. This facility is ideal for this investigation as the ratio of boundary layer thickness to test section spanwise extent ratio is around 1/25, ensuring minimal sidewall and corner effects on turbulent structures in the center of the test section. A major difficulty in the experimental investigation of large scale features is the mutual size of the superstructures which can extend over many boundary layer thicknesses. Using multiple PIV systems, it was possible to capture the full spatial extent of large-scale structures over a range of Mach numbers from Ma = 0.3 - 3. To calculate the average large-scale structure length and spacing, the acquired vector fields were analyzed by statistical multi-point methods that show large scale structures with a correlation length of around 10 boundary layer thicknesses over the range of Mach numbers investigated. Furthermore, the average spacing between high and low momentum structures is on the order of a boundary layer thicknesses. This work is supported by the Priority Programme SPP 1881 Turbulent Superstructures of the Deutsche Forschungsgemeinschaft.

Welding of gamma titanium aluminide alloys

NASA Technical Reports Server (NTRS)

Smashey, Russell W. (Inventor); Snyder, John H. (Inventor); Kelly, Thomas J. (Inventor); Sheranko, Ronald L. (Inventor)

1998-01-01

An article made of a gamma titanium aluminide alloy is welded, as for example in the weld repair of surface cracks, by removing foreign matter from the area to be welded, first stress relieving the article, cooling the entire article to a welding temperature of from about 1000.degree. F. to about 1400.degree. F., welding a preselected region in an inert atmosphere at the welding temperature, and second stress relieving the article. Welding is preferably accomplished by striking an arc in the preselected region so as to locally melt the alloy in the preselected region, providing a filler metal having the same composition as the gamma titanium aluminide alloy of the article, and feeding the filler metal into the arc so that the filler metal is melted and fused with the article to form a weldment upon solidification.

Exploratory study of friction welds in Udimet 700 and TD-Nickel bar

NASA Technical Reports Server (NTRS)

Moore, T. J.

1971-01-01

Friction welded butt joints were made in both Udimet 700 and TD-Nickel bar. Also, dissimilar metal friction welds were made between these materials. Friction welding of Udimet 700 shows great promise because the welds were found to be as strong as the parent metal in stress rupture and tensile tests at 760 and 980 C. The weld line was not detectable metallographically in the heat treated condition. Friction welding for TD-Nickel, however, holds little if any promise. TD-Nickel friction weldments could support only 9 percent as much stress as the base metal for a 10-hour stress-rupture life at 1090 C. Dissimilar Udimet 700/TD-Nickel friction welds could sustain only 15 percent as much stress as the TD-Nickel parent metal for a 10-hour rupture life at 930 C.

Microstructural dependence of Barkhausen noise and magnetic relaxation in the weld HAZ of an RPV steel

NASA Astrophysics Data System (ADS)

Park, Duck-Gun; Kim, Cheol Gi; Hong, Jun-Hwa

2000-06-01

Magnetic Barkhausen noise and permeability spectra have been measured to characterize different microstructure regions such as coarse-grain region, fine-grain region, intercritical structure (composed of tempered martensite and bainite) within the heat-affected zone (HAZ) of SA508-3 steel weldments using simulated HAZ microstructure sample. The intercritical region and coarse-grained region can be distinguished from the BNE and relaxation frequency. The BNE was decreased in the martensite regions and increased in the bainite regions by the post-weld heat treatment (PWHT). The change of relaxation frequency also showed similar trends, but the rate of change was less than that of BNE. The behavior of BNE and permeability spectra on the corresponding microstructure can be explained in terms of carbide morphology and residual stress related with domain wall motion.

Effect of Cr Contents and Heat Treating on Reverted Austenite in Maraging Steel Weldments

NASA Astrophysics Data System (ADS)

Kim, S. W.; Lee, H. W.

2018-05-01

By conducting flux cored arc welding (FCAW) on maraging steels with Cr contents of 1.4 and 5.2 wt%, this study observed the effects of Cr content and heat treating on reverted austenite formation in welded maraging steel. Aging treatment was carried out at the temperatures of 450, 480 and 530 °C for 3 h in each condition. As the aging temperature increased, reverted austenite was formed along the interdendritic and intercellular grain boundaries, and the proportion of reverted austenite increased with increasing Cr addition. The aging process led to the segregation of Ti and Mo along the interdendritic and intercellular grain boundaries. Some of the welded specimens were subjected to solution heat treatment at 820 and 1250 °C for 1 h after welding, resulting in a decrease in reverted austenite fraction.

Microstructural evolution and precipitation behavior in heat affected zone of Inconel 625 and AISI 904L dissimilar welds

NASA Astrophysics Data System (ADS)

Senthur Prabu, S.; Devendranath Ramkumar, K.; Arivazhagan, N.

2017-11-01

In the present investigation an attempt has been made to join the dissimilar combination of Inconel 625 super alloy and super austenitic stainless steel (AISI 904L) using manual multi-pass continuous current gas tungsten arc (CCGTA) welding processes. Two different filler wires such as ERNiCrMo-4 and ERNiCrCoMo-1 have been used to compare the metallurgical properties of these welded joints. Both optical microscopy and scanning electron microscopy techniques were adopted to disseminate the microstructure traits of these weldments. Formation of secondary phases at the HAZ and weld interface of AISI 904L was witnessed while using the ERNiCrCoMo-1 filler, along with Solidification Grain Boundary (SGB) and Migrated Grain Boundary (MGB) were also observed at the weld zone.