The effect of copper pre-cleaning on graphene synthesis.

PubMed

Kim, Soo Min; Hsu, Allen; Lee, Yi-Hsien; Dresselhaus, Mildred; Palacios, Tomás; Kim, Ki Kang; Kong, Jing

2013-09-13

Copper foil is the most common substrate to synthesize monolayer graphene by chemical vapor deposition (CVD). The surface morphology and conditions of the copper foil can be very different depending on the various suppliers or different batches. These surface properties of copper strongly affect the growth behavior of graphene, thus rendering the growth conditions irreproducible when different batches of Cu foil are used. Furthermore, the quality of the graphene is severely affected as well. In this work, we report a facile method of copper pre-cleaning to improve the graphene quality and the reproducibility of the growth process. We found that the commercial Ni etchant (based on nitric acid) or nitric acid is the most effective cleaning agent among various acidic or basic solutions. The graphene grown on thus-treated copper surfaces is very clean and mostly monolayer when observed under scanning electron microscopy (SEM) and optical imaging, as compared to the graphene grown on untreated copper foil. Different batches (but with the same catalog number) of copper foil from Alfa Aesar Company were examined to explore the effect of copper pre-cleaning; consistent growth results were obtained when pre-cleaning was used. This method overcomes a commonly encountered problem in graphene growth and could become one of the standard protocols for preparing the copper foil substrate for growing graphene or other 2D materials.

A dilute Cu(Ni) alloy for synthesis of large-area Bernal stacked bilayer graphene using atmospheric pressure chemical vapour deposition

DOE Office of Scientific and Technical Information (OSTI.GOV)

Madito, M. J.; Bello, A.; Dangbegnon, J. K.

2016-01-07

A bilayer graphene film obtained on copper (Cu) foil is known to have a significant fraction of non-Bernal (AB) stacking and on copper/nickel (Cu/Ni) thin films is known to grow over a large-area with AB stacking. In this study, annealed Cu foils for graphene growth were doped with small concentrations of Ni to obtain dilute Cu(Ni) alloys in which the hydrocarbon decomposition rate of Cu will be enhanced by Ni during synthesis of large-area AB-stacked bilayer graphene using atmospheric pressure chemical vapour deposition. The Ni doped concentration and the Ni homogeneous distribution in Cu foil were confirmed with inductively coupledmore » plasma optical emission spectrometry and proton-induced X-ray emission. An electron backscatter diffraction map showed that Cu foils have a single (001) surface orientation which leads to a uniform growth rate on Cu surface in early stages of graphene growth and also leads to a uniform Ni surface concentration distribution through segregation kinetics. The increase in Ni surface concentration in foils was investigated with time-of-flight secondary ion mass spectrometry. The quality of graphene, the number of graphene layers, and the layers stacking order in synthesized bilayer graphene films were confirmed by Raman and electron diffraction measurements. A four point probe station was used to measure the sheet resistance of graphene films. As compared to Cu foil, the prepared dilute Cu(Ni) alloy demonstrated the good capability of growing large-area AB-stacked bilayer graphene film by increasing Ni content in Cu surface layer.« less

A dilute Cu(Ni) alloy for synthesis of large-area Bernal stacked bilayer graphene using atmospheric pressure chemical vapour deposition

NASA Astrophysics Data System (ADS)

Madito, M. J.; Bello, A.; Dangbegnon, J. K.; Oliphant, C. J.; Jordaan, W. A.; Momodu, D. Y.; Masikhwa, T. M.; Barzegar, F.; Fabiane, M.; Manyala, N.

2016-01-01

A bilayer graphene film obtained on copper (Cu) foil is known to have a significant fraction of non-Bernal (AB) stacking and on copper/nickel (Cu/Ni) thin films is known to grow over a large-area with AB stacking. In this study, annealed Cu foils for graphene growth were doped with small concentrations of Ni to obtain dilute Cu(Ni) alloys in which the hydrocarbon decomposition rate of Cu will be enhanced by Ni during synthesis of large-area AB-stacked bilayer graphene using atmospheric pressure chemical vapour deposition. The Ni doped concentration and the Ni homogeneous distribution in Cu foil were confirmed with inductively coupled plasma optical emission spectrometry and proton-induced X-ray emission. An electron backscatter diffraction map showed that Cu foils have a single (001) surface orientation which leads to a uniform growth rate on Cu surface in early stages of graphene growth and also leads to a uniform Ni surface concentration distribution through segregation kinetics. The increase in Ni surface concentration in foils was investigated with time-of-flight secondary ion mass spectrometry. The quality of graphene, the number of graphene layers, and the layers stacking order in synthesized bilayer graphene films were confirmed by Raman and electron diffraction measurements. A four point probe station was used to measure the sheet resistance of graphene films. As compared to Cu foil, the prepared dilute Cu(Ni) alloy demonstrated the good capability of growing large-area AB-stacked bilayer graphene film by increasing Ni content in Cu surface layer.

All-inorganic large-area low-cost and durable flexible perovskite solar cells using copper foil as a substrate.

PubMed

Abdollahi Nejand, B; Nazari, P; Gharibzadeh, S; Ahmadi, V; Moshaii, A

2017-01-05

Here, a low-cost perovskite solar cell using CuI and ZnO as the respective inorganic hole and electron transport layers is introduced. Copper foil is chosen as a cheap and low-weight conductive substrate which has a similar work function to ITO. Besides, copper foil is an interesting copper atom source for the growth of the upper cuprous iodide layer on copper foil. A spray coating of a transparent silver nanowire electrode is used as a top contact. The prepared device shows a maximum power conversion efficiency of 12.80% and long-term durability providing an environmentally and market friendly perovskite solar cell.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Lula, J.W.

Copper foil adhesion to polyimide/glass prepreg was evaluated. Typical peel strength obtained between prepreg and the smooth side of the copper foil was 1 to 3 lb./in. width. Peel strength between prepreg and the rough side of the copper foil ranged between 6 and 7 lb./in. width. An alternate test for evaluating the integrity of multilayer printed wiring boards is described.

An Experimental Study on Micro Clinching of Metal Foils with Cutting by Laser Shock Forming.

PubMed

Wang, Xiao; Li, Cong; Ma, Youjuan; Shen, Zongbao; Sun, Xianqing; Sha, Chaofei; Gao, Shuai; Li, Liyin; Liu, Huixia

2016-07-13

This paper describes a novel technique for joining similar and dissimilar metal foils, namely micro clinching with cutting by laser shock forming. A series of experiments were conducted to study the deformation behavior of single layer material, during which many important process parameters were determined. The process window of the 1060 pure aluminum foils and annealed copper foils produced by micro clinching with cutting was analyzed. Moreover, similar material combination (annealed copper foils) and dissimilar material combination (1060 pure aluminum foils and 304 stainless steel foils) were successfully achieved. The effect of laser energy on the interlock and minimum thickness of upper foils was investigated. In addition, the mechanical strength of different material combinations joined by micro clinching with cutting was measured in single lap shearing tests. According to the achieved results, this novel technique is more suitable for material combinations where the upper foil is thicker than lower foil. With the increase of laser energy, the interlock increased while the minimum thickness of upper foil decreased gradually. The shear strength of 1060 pure aluminum foils and 304 stainless steel foils combination was three times as large as that of 1060 pure aluminum foils and annealed copper foils combination.

Thin-Film Solar Cells on Metal Foil Substrates for Space Power

NASA Technical Reports Server (NTRS)

Raffaelle, Ryne P.; Hepp, Aloysius F.; Hoffman, David J.; Dhere, N.; Tuttle, J. R.; Jin, Michael H.

2004-01-01

Photovoltaic arrays have played a key role in power generation in space. The current technology will continue to evolve but is limited in the important mass specific power metric (MSP or power/weight ratio) because it is based on bulk crystal technology. The objective of this research is to continue development of an innovative photovoltaic technology for satellite power sources that could provide up to an order of magnitude saving in both weight and cost, and is inherently radiation-tolerant through use of thin film technology and thin foil substrates such as 5-mil thick stainless steel foil or 1-mil thick Ti. Current single crystal technology for space power can cost more than $300 per watt at the array level and weigh more than 1 kg/sq m equivalent to specific power of approx. 65 W/kg. Thin film material such as CuIn(1-x),Ga(x)S2, (CIGS2), CuIn(1-x), G(x)Se(2-y),S(y), (CIGSS) or amorphous hydrogenated silicon (a-Si:H) may be able to reduce both the cost and mass per unit area by an order of magnitude. Manufacturing costs for solar arrays are an important consideration for total spacecraft budget. For a medium sized 5kW satellite, for example, the array manufacturing cost alone may exceed $2 million. Moving to thin film technology could reduce this expense to less than $500 K. Previous work at FSEC demonstrated the potential of achieving higher efficiencies from CIGSS thin film solar cells on 5-mil thick stainless steel foil as well as initial stages of facility augmentation for depositing thin film solar cells on larger (6"x 4") substrates. This paper presents further progress in processing on metal foil substrates. Also, previous work at DayStar demonstrated the feasibility of flexible-thin-film copper-indium-gallium-diselenide (CIGS) solar cells with a power-to-weight ratio in excess of 1000 W/kg. We will comment on progress on the critical issue of scale-up of the solar cell absorber deposition process. Several important technical issues need to be resolved to realize the benefits of lightweight technologies for solar arrays, such as: monolithic interconnects, lightweight array structures, and new ultra-light support and deployment mechanisms. Once the technology has gained spaceflight certification it should find rapid acceptance in specific satellite markets.

Rayleigh--Taylor spike evaporation

DOE Office of Scientific and Technical Information (OSTI.GOV)

Schappert, G. T.; Batha, S. H.; Klare, K. A.

2001-09-01

Laser-based experiments have shown that Rayleigh--Taylor (RT) growth in thin, perturbed copper foils leads to a phase dominated by narrow spikes between thin bubbles. These experiments were well modeled and diagnosed until this '' spike'' phase, but not into this spike phase. Experiments were designed, modeled, and performed on the OMEGA laser [T. R. Boehly, D. L. Brown, R. S. Craxton , Opt. Commun. 133, 495 (1997)] to study the late-time spike phase. To simulate the conditions and evolution of late time RT, a copper target was fabricated consisting of a series of thin ridges (spikes in cross section) 150more » {mu}m apart on a thin flat copper backing. The target was placed on the side of a scale-1.2 hohlraum with the ridges pointing into the hohlraum, which was heated to 190 eV. Side-on radiography imaged the evolution of the ridges and flat copper backing into the typical RT bubble and spike structure including the '' mushroom-like feet'' on the tips of the spikes. RAGE computer models [R. M. Baltrusaitis, M. L. Gittings, R. P. Weaver, R. F. Benjamin, and J. M. Budzinski, Phys. Fluids 8, 2471 (1996)] show the formation of the '' mushrooms,'' as well as how the backing material converges to lengthen the spike. The computer predictions of evolving spike and bubble lengths match measurements fairly well for the thicker backing targets but not for the thinner backings.« less

An Experimental Study on Micro Clinching of Metal Foils with Cutting by Laser Shock Forming

PubMed Central

Wang, Xiao; Li, Cong; Ma, Youjuan; Shen, Zongbao; Sun, Xianqing; Sha, Chaofei; Gao, Shuai; Li, Liyin; Liu, Huixia

2016-01-01

This paper describes a novel technique for joining similar and dissimilar metal foils, namely micro clinching with cutting by laser shock forming. A series of experiments were conducted to study the deformation behavior of single layer material, during which many important process parameters were determined. The process window of the 1060 pure aluminum foils and annealed copper foils produced by micro clinching with cutting was analyzed. Moreover, similar material combination (annealed copper foils) and dissimilar material combination (1060 pure aluminum foils and 304 stainless steel foils) were successfully achieved. The effect of laser energy on the interlock and minimum thickness of upper foils was investigated. In addition, the mechanical strength of different material combinations joined by micro clinching with cutting was measured in single lap shearing tests. According to the achieved results, this novel technique is more suitable for material combinations where the upper foil is thicker than lower foil. With the increase of laser energy, the interlock increased while the minimum thickness of upper foil decreased gradually. The shear strength of 1060 pure aluminum foils and 304 stainless steel foils combination was three times as large as that of 1060 pure aluminum foils and annealed copper foils combination. PMID:28773692

Atmospheric Pressure Plasma Jet as a Dry Alternative to Inkjet Printing in Flexible Electronics

NASA Technical Reports Server (NTRS)

Gandhiraman, Ram Prasad; Lopez, Arlene; Koehne, Jessica; Meyyappan, M.

2016-01-01

We have developed an atmospheric pressure plasma jet printing system that works at room temperature to 50 deg C unlike conventional aerosol assisted techniques which require a high temperature sintering step to obtain desired thin films. Multiple jets can be configured to increase throughput or to deposit multiple materials, and the jet(s) can be moved across large areas using a x-y stage. The plasma jet has been used to deposit carbon nanotubes, graphene, silver nanowires, copper nanoparticles and other materials on substrates such as paper, cotton, plastic and thin metal foils.

Fragmentation of copper current collectors in Li-ion batteries during spherical indentation

NASA Astrophysics Data System (ADS)

Wang, Hsin; Watkins, Thomas R.; Simunovic, Srdjan; Bingham, Philip R.; Allu, Srikanth; Turner, John A.

2017-10-01

Large, areal, brittle fracture of copper current collector foils has been observed by 3D x-ray computed tomography (XCT) of a spherically indented Li-ion cell. This fracture is hidden and non-catastrophic to a degree because the graphite layers deform plastically, and hold the materials together so that the cracks in the foils cannot be seen under optical and electron microscopy. The cracking of copper foils could not be immediately confirmed when the cell is opened for post-mortem examination. However, 3D XCT on the indented cell reveals ;mud cracks; within the copper layer and an X-ray radiograph on a single foil of the Cu anode shows clearly that the copper foil has broken into multiple pieces. This failure mode of anodes in Li-ion cell has very important implications on the behavior of Li-ion cells under mechanical abuse conditions. The fragmentation of current collectors in the anode must be taken into consideration for the electrochemical responses which may lead to capacity loss and affect thermal runaway behavior of the cells.

Electron emission from condensed phase material induced by fast protons.

PubMed

Shinpaugh, J L; McLawhorn, R A; McLawhorn, S L; Carnes, K D; Dingfelder, M; Travia, A; Toburen, L H

2011-02-01

Monte Carlo track simulation has become an important tool in radiobiology. Monte Carlo transport codes commonly rely on elastic and inelastic electron scattering cross sections determined using theoretical methods supplemented with gas-phase data; experimental condensed phase data are often unavailable or infeasible. The largest uncertainties in the theoretical methods exist for low-energy electrons, which are important for simulating electron track ends. To test the reliability of these codes to deal with low-energy electron transport, yields of low-energy secondary electrons ejected from thin foils have been measured following passage of fast protons. Fast ions, where interaction cross sections are well known, provide the initial spectrum of low-energy electrons that subsequently undergo elastic and inelastic scattering in the material before exiting the foil surface and being detected. These data, measured as a function of the energy and angle of the emerging electrons, can provide tests of the physics of electron transport. Initial measurements from amorphous solid water frozen to a copper substrate indicated substantial disagreement with MC simulation, although questions remained because of target charging. More recent studies, using different freezing techniques, do not exhibit charging, but confirm the disagreement seen earlier between theory and experiment. One now has additional data on the absolute differential electron yields from copper, aluminum and gold, as well as for thin films of frozen hydrocarbons. Representative data are presented.

Electron emission from condensed phase material induced by fast protons†

PubMed Central

Shinpaugh, J. L.; McLawhorn, R. A.; McLawhorn, S. L.; Carnes, K. D.; Dingfelder, M.; Travia, A.; Toburen, L. H.

2011-01-01

Monte Carlo track simulation has become an important tool in radiobiology. Monte Carlo transport codes commonly rely on elastic and inelastic electron scattering cross sections determined using theoretical methods supplemented with gas-phase data; experimental condensed phase data are often unavailable or infeasible. The largest uncertainties in the theoretical methods exist for low-energy electrons, which are important for simulating electron track ends. To test the reliability of these codes to deal with low-energy electron transport, yields of low-energy secondary electrons ejected from thin foils have been measured following passage of fast protons. Fast ions, where interaction cross sections are well known, provide the initial spectrum of low-energy electrons that subsequently undergo elastic and inelastic scattering in the material before exiting the foil surface and being detected. These data, measured as a function of the energy and angle of the emerging electrons, can provide tests of the physics of electron transport. Initial measurements from amorphous solid water frozen to a copper substrate indicated substantial disagreement with MC simulation, although questions remained because of target charging. More recent studies, using different freezing techniques, do not exhibit charging, but confirm the disagreement seen earlier between theory and experiment. One now has additional data on the absolute differential electron yields from copper, aluminum and gold, as well as for thin films of frozen hydrocarbons. Representative data are presented. PMID:21183539

Fragmentation of copper current collectors in Li-ion batteries during spherical indentation

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wang, Hsin; Watkins, Thomas R.; Simunovic, Srdjan

Large, areal, brittle fracture of copper current collector foils was observed by 3D x-ray computed tomography (XCT) of a spherically indented Li-ion cell. This fracture was hidden and non-catastrophic to a degree because the graphite layers deformed plastically, and held the materials together so that the cracks in the foils could not be seen under optical and electron microscopy. 3D XCT on the indented cell showed “mud cracks” within the copper layer. The cracking of copper foils could not be immediately confirmed when the cell was opened for post-mortem examination. However, an X-ray radiograph on a single foil of themore » Cu anode showed clearly that the copper foil had broken into multiple pieces similar to the brittle cracking of a ceramic under indentation. This new failure mode of anodes on Li-ion cell has very important implications on the behavior of Li-ion cells under mechanical abuse conditions. Furthermore, the fragmentation of current collectors in the anode must be taken into consideration for the electrochemical responses which may lead to capacity loss and affect thermal runaway behavior of the cells.« less

Fragmentation of copper current collectors in Li-ion batteries during spherical indentation

DOE PAGES

Wang, Hsin; Watkins, Thomas R.; Simunovic, Srdjan; ...

2017-08-29

Large, areal, brittle fracture of copper current collector foils was observed by 3D x-ray computed tomography (XCT) of a spherically indented Li-ion cell. This fracture was hidden and non-catastrophic to a degree because the graphite layers deformed plastically, and held the materials together so that the cracks in the foils could not be seen under optical and electron microscopy. 3D XCT on the indented cell showed “mud cracks” within the copper layer. The cracking of copper foils could not be immediately confirmed when the cell was opened for post-mortem examination. However, an X-ray radiograph on a single foil of themore » Cu anode showed clearly that the copper foil had broken into multiple pieces similar to the brittle cracking of a ceramic under indentation. This new failure mode of anodes on Li-ion cell has very important implications on the behavior of Li-ion cells under mechanical abuse conditions. Furthermore, the fragmentation of current collectors in the anode must be taken into consideration for the electrochemical responses which may lead to capacity loss and affect thermal runaway behavior of the cells.« less

Bundled and densified carbon nanotubes (CNT) fabrics as flexible ultra-light weight Li-ion battery anode current collectors

NASA Astrophysics Data System (ADS)

Yehezkel, Shani; Auinat, Mahmud; Sezin, Nina; Starosvetsky, David; Ein-Eli, Yair

2016-04-01

Carbon nanotubes (CNT) fabrics were studied and evaluated as anode current collectors, replacing the traditional copper foil current collector in Li-ion batteries. Glavanostatic measurements reveal high values of irreversible capacities (as high as 28%), resulted mainly from the formation of the solid electrolyte interphase (SEI) layer at the CNT fabric surface. Various pre-treatments to the CNT fabric prior to active anode material loading have shown that the lowest irreversible capacity is achieved by immersing and washing the CNT fabric with iso-propanol (IPA), which dramatically modified the fabric surface. Additionally, the use of very thin CNT fabrics (5 μm) results in a substantial irreversible capacity minimization. A combination of IPA rinse action and utilization of the thinnest CNT fabric provides the lowest irreversible capacity of 13%. The paper describes innovative and rather simple techniques towards a complete implementation of CNT fabric as an anode current collector in Li-ion batteries, instead of the relatively heavy and expensive copper foil, enabling an improvement in the gravimetric and volumetric energy densities of such advanced batteries.

Single crystalline electronic structure and growth mechanism of aligned square graphene sheets

NASA Astrophysics Data System (ADS)

Yang, H. F.; Chen, C.; Wang, H.; Liu, Z. K.; Zhang, T.; Peng, H.; Schröter, N. B. M.; Ekahana, S. A.; Jiang, J.; Yang, L. X.; Kandyba, V.; Barinov, A.; Chen, C. Y.; Avila, J.; Asensio, M. C.; Peng, H. L.; Liu, Z. F.; Chen, Y. L.

2018-03-01

Recently, commercially available copper foil has become an efficient and inexpensive catalytic substrate for scalable growth of large-area graphene films for fundamental research and applications. Interestingly, despite its hexagonal honeycomb lattice, graphene can be grown into large aligned square-shaped sheets on copper foils. Here, by applying angle-resolved photoemission spectroscopy with submicron spatial resolution (micro-ARPES) to study the three-dimensional electronic structures of square graphene sheets grown on copper foils, we verified the high quality of individual square graphene sheets as well as their merged regions (with aligned orientation). Furthermore, by simultaneously measuring the graphene sheets and their substrate copper foil, we not only established the (001) copper surface structure but also discovered that the square graphene sheets' sides align with the ⟨110⟩ copper direction, suggesting an important role of copper substrate in the growth of square graphene sheets—which will help the development of effective methods to synthesize high-quality large-size regularly shaped graphene sheets for future applications. This work also demonstrates the effectiveness of micro-ARPES in exploring low-dimensional materials down to atomic thickness and sub-micron lateral size (e.g., besides graphene, it can also be applied to transition metal dichalcogenides and various van der Waals heterostructures)

Precise method to determine points on isentropic release curve on copper

NASA Astrophysics Data System (ADS)

Remiot, C.; Mexmain, J. M.; Bonnet, L.

1996-05-01

When a higher shock impedance foil (with several hundreds of μm in thickness) is set on the studied material surface, the release phase occurs by steps, whose duration of each plateau corresponds to a go and return of the shock wave in the foil. Step velocity levels can be easily measured by D.L.I. technique. The intermediate velocity values, connected with the knowledge of the foil Hugoniot, allow us to determine a few points on the isentropic release curve. The experiments have been achieved on a two stage light gas gun with a projectile velocity varying from 1400 to 3000 m/s. The caliber of the launcher is 30 mm. For this study concerning copper, the target is composed of a 2 mm thickness copper transmitter on which the sample is mechanically held. The tungsten (W) thick foil is, under pressure, sticked on the sample with UV stick-cord. The free surface velocity measurement accuracy of the tungsten foil is 0.4% for values between 1500 to 3500 m/s. The first shock in the sample is varying from 40 to 120 GPa and the mass velocity from 800 to 2000 m/s. By impedance matching between the copper sample and the tungsten thick foil, we deduce for each experiment three points on the copper isentropic release curve and the final free surface velocity. The accuracy we obtain is in order of 0.4 GPa for the pressure and 10 m/s for the mass velocity.

Frictional behavior of atomically thin sheets: hexagonal-shaped graphene islands grown on copper by chemical vapor deposition.

PubMed

Egberts, Philip; Han, Gang Hee; Liu, Xin Z; Johnson, A T Charlie; Carpick, Robert W

2014-05-27

Single asperity friction experiments using atomic force microscopy (AFM) have been conducted on chemical vapor deposited (CVD) graphene grown on polycrystalline copper foils. Graphene substantially lowers the friction force experienced by the sliding asperity of a silicon AFM tip compared to the surrounding oxidized copper surface by a factor ranging from 1.5 to 7 over loads from the adhesive minimum up to 80 nN. No damage to the graphene was observed over this range, showing that friction force microscopy serves as a facile, high contrast probe for identifying the presence of graphene on Cu. Consistent with studies of epitaxially grown, thermally grown, and mechanically exfoliated graphene films, the friction force measured between the tip and these CVD-prepared films depends on the number of layers of graphene present on the surface and reduces friction in comparison to the substrate. Friction results on graphene indicate that the layer-dependent friction properties result from puckering of the graphene sheet around the sliding tip. Substantial hysteresis in the normal force dependence of friction is observed with repeated scanning without breaking contact with a graphene-covered region. Because of the hysteresis, friction measured on graphene changes with time and maximum applied force, unless the tip slides over the edge of the graphene island or contact with the surface is broken. These results also indicate that relatively weak binding forces exist between the copper foil and these CVD-grown graphene sheets.

Method and apparatus for coating thin foil with a boron coating

DOE Office of Scientific and Technical Information (OSTI.GOV)

Lacy, Jeffrey L.

An apparatus and a process is disclosed for applying a boron coating to a thin foil. Preferably, the process is a continuous, in-line process for applying a coating to a thin foil comprising wrapping the foil around a rotating and translating mandrel, cleaning the foil with glow discharge in an etching chamber as the mandrel with the foil moves through the chamber, sputtering the foil with boron carbide in a sputtering chamber as the mandrel moves through the sputtering chamber, and unwinding the foil off the mandrel after it has been coated. The apparatus for applying a coating to amore » thin foil comprises an elongated mandrel. Foil preferably passes from a reel to the mandrel by passing through a seal near the initial portion of an etching chamber. The mandrel has a translation drive system for moving the mandrel forward and a rotational drive system for rotating mandrel as it moves forward. The etching chamber utilizes glow discharge on a surface of the foil as the mandrel moves through said etching chamber. A sputtering chamber, downstream of the etching chamber, applies a thin layer comprising boron onto the surface of the foil as said mandrel moves through said sputtering chamber. Preferably, the coated foil passes from the mandrel to a second reel by passing through a seal near the terminal portion of the sputtering chamber.« less

Atomic Layer Deposition of MnS: Phase Control and Electrochemical Applications

DOE Office of Scientific and Technical Information (OSTI.GOV)

Riha, Shannon C.; Koegel, Alexandra A.; Meng, Xiangbo

Manganese sulfide (MnS) thin films were synthesized via atomic layer deposition (ALD) using gaseous manganese bis(ethylcyclopentadienyl) and hydrogen sulfide as precursors. At deposition temperatures ≤150 °C phase-pure r-MnS thin films were deposited, while at temperatures >150 °C, a mixed phase, consisting of both r- and a-MnS resulted. In situ quartz crystal microbalance (QCM) studies validate the self-limiting behavior of both ALD half-reactions and, combined with quadrupole mass spectrometry (QMS) allow the derivation of a self-consistent reaction mechanism. Lastly, MnS thin films were deposited on copper foil and tested as a Li-ion battery anode. The MnS coin cells showed exceptional cyclemore » stability and near-theoretical capacity.« less

Atomic Layer Deposition of MnS: Phase Control and Electrochemical Applications

DOE PAGES

Riha, Shannon C.; Koegel, Alexandra A.; Meng, Xiangbo; ...

2016-01-19

Manganese sulfide (MnS) thin films were synthesized via atomic layer deposition (ALD) using gaseous manganese bis(ethylcyclopentadienyl) and hydrogen sulfide as precursors. At deposition temperatures ≤150 °C phase-pure r-MnS thin films were deposited, while at temperatures >150 °C, a mixed phase, consisting of both r- and a-MnS resulted. In situ quartz crystal microbalance (QCM) studies validate the self-limiting behavior of both ALD half-reactions and, combined with quadrupole mass spectrometry (QMS) allow the derivation of a self-consistent reaction mechanism. Lastly, MnS thin films were deposited on copper foil and tested as a Li-ion battery anode. The MnS coin cells showed exceptional cyclemore » stability and near-theoretical capacity.« less

Studies of PMMA sintering foils with and without coating by magnetron sputtering Pd

NASA Astrophysics Data System (ADS)

Cutroneo, M.; Mackova, A.; Torrisi, L.; Vad, K.; Csik, A.; Ando', L.; Svecova, B.

2017-09-01

Polymethylmethacrylate thin foils were prepared by using physical and chemical processes aimed at changing certain properties. The density and the optical properties were changed obtaining clear and opaque foils. DC magnetron sputtering method was used to cover the foils with thin metallic palladium layers. The high optical absorbent foils were obtained producing microstructured PMMA microbeads with and without thin metallic coatings. Rutherford Backscattering Spectroscopy, optical investigation and microscopy were employed to characterize the prepared foils useful in the field study of laser-matter interaction.

Integral window/photon beam position monitor and beam flux detectors for x-ray beams

DOEpatents

Shu, Deming; Kuzay, Tuncer M.

1995-01-01

A monitor/detector assembly in a synchrotron for either monitoring the position of a photon beam or detecting beam flux may additionally function as a vacuum barrier between the front end and downstream segment of the beamline in the synchrotron. A base flange of the monitor/detector assembly is formed of oxygen free copper with a central opening covered by a window foil that is fused thereon. The window foil is made of man-made materials, such as chemical vapor deposition diamond or cubic boron nitrate and in certain configurations includes a central opening through which the beams are transmitted. Sensors of low atomic number materials, such as aluminum or beryllium, are laid on the window foil. The configuration of the sensors on the window foil may be varied depending on the function to be performed. A contact plate of insulating material, such as aluminum oxide, is secured to the base flange and is thereby clamped against the sensor on the window foil. The sensor is coupled to external electronic signal processing devices via a gold or silver lead printed onto the contact plate and a copper post screw or alternatively via a copper screw and a copper spring that can be inserted through the contact plate and coupled to the sensors. In an alternate embodiment of the monitor/detector assembly, the sensors are sandwiched between the window foil of chemical vapor deposition diamond or cubic boron nitrate and a front foil made of similar material.

Solution-processed p-type copper(I) thiocyanate (CuSCN) for low-voltage flexible thin-film transistors and integrated inverter circuits

NASA Astrophysics Data System (ADS)

Petti, Luisa; Pattanasattayavong, Pichaya; Lin, Yen-Hung; Münzenrieder, Niko; Cantarella, Giuseppe; Yaacobi-Gross, Nir; Yan, Feng; Tröster, Gerhard; Anthopoulos, Thomas D.

2017-03-01

We report on low operating voltage thin-film transistors (TFTs) and integrated inverters based on copper(I) thiocyanate (CuSCN) layers processed from solution at low temperature on free-standing plastic foils. As-fabricated coplanar bottom-gate and staggered top-gate TFTs exhibit hole-transporting characteristics with average mobility values of 0.0016 cm2 V-1 s-1 and 0.013 cm2 V-1 s-1, respectively, current on/off ratio in the range 102-104, and maximum operating voltages between -3.5 and -10 V, depending on the gate dielectric employed. The promising TFT characteristics enable fabrication of unipolar NOT gates on flexible free-standing plastic substrates with voltage gain of 3.4 at voltages as low as -3.5 V. Importantly, discrete CuSCN transistors and integrated logic inverters remain fully functional even when mechanically bent to a tensile radius of 4 mm, demonstrating the potential of the technology for flexible electronics.

Gas Suppression via Copper Interlayers in Magnetron Sputtered Al-Cu2O Multilayers.

PubMed

Kinsey, Alex H; Slusarski, Kyle; Sosa, Steven; Weihs, Timothy P

2017-07-05

The use of thin-foil, self-propagating thermite reactions to bond components successfully depends on the ability to suppress gas generation and avoid pore formation during the exothermic production of brazes. To study the mechanisms of vapor production in diluted thermites, thin film multilayer Al-Cu-Cu 2 O-Cu foils are produced via magnetron sputtering, where the Cu layer thickness is systematically increased from 0 to 100 nm in 25 nm increments. The excess Cu layers act as diffusion barriers, limiting the transport of oxygen from the oxide to the Al fuel, as determined by slow heating differential scanning calorimetry experiments. Furthermore, by adding excess Cu to the system, the temperature of the self-propagating thermite reactions drops below the boiling point of Cu, eliminating the metal vapor production. It is determined that Cu vapor production can be eliminated by increasing the Cu interlayer thickness above 50 nm. However, the porous nature of the final products suggests that only metal vapor production is suppressed via dilution. Gas generation via oxygen release is still capable of producing a porous reaction product.

Lead zirconate titanate thin films directly on copper electrodes for ferroelectric, dielectric and piezoelectric applications

NASA Astrophysics Data System (ADS)

Kingon, Angus I.; Srinivasan, Sudarsan

2005-03-01

Replacement of noble metal electrodes by base metals significantly lowers the cost of ferroelectric, piezoelectric and dielectric devices. Here, we demonstrate that it is possible to process lead zirconate (Pb(Zr0.52Ti0.48)O3, or PZT) thin films directly on base metal copper foils. We explore the impact of the oxygen partial pressure during processing, and demonstrate that high-quality films and interfaces can be achieved through control of the oxygen partial pressure within a narrow window predicted by thermodynamic stability considerations. This demonstration has broad implications, opening up the possibility of the use of low-cost, high-conductivity copper electrodes for a range of Pb-based perovskite materials, including PZT films in embedded printed circuit board applications for capacitors, varactors and sensors; multilayer PZT piezoelectric stacks; and multilayer dielectric and electrostrictive devices based on lead magnesium niobate-lead titanate. We also point out that the capacitors do not fatigue on repeated switching, unlike those with Pt noble metal electrodes. Instead, they appear to be fatigue-resistant, like capacitors with oxide electrodes. This may have implications for ferroelectric non-volatile memories.

Method of making porous conductive supports for electrodes. [by electroforming and stacking nickel foils

NASA Technical Reports Server (NTRS)

Schaer, G. R. (Inventor)

1973-01-01

Porous conductive supports for electrochemical cell electrodes are made by electroforming thin corrugated nickel foil, and by stacking pieces of the corrugated foil alternatively with pieces of thin flat nickel foil. Corrugations in successive corrugated pieces are oriented at different angles. Adjacent pieces of foil are bonded by heating in a hydrogen atmosphere and then cutting the stack in planes perpendicular to the foils.

Metal-assisted exfoliation (MAE): green, roll-to-roll compatible method for transferring graphene to flexible substrates

NASA Astrophysics Data System (ADS)

Zaretski, Aliaksandr V.; Moetazedi, Herad; Kong, Casey; Sawyer, Eric J.; Savagatrup, Suchol; Valle, Eduardo; O'Connor, Timothy F.; Printz, Adam D.; Lipomi, Darren J.

2015-01-01

Graphene is expected to play a significant role in future technologies that span a range from consumer electronics, to devices for the conversion and storage of energy, to conformable biomedical devices for healthcare. To realize these applications, however, a low-cost method of synthesizing large areas of high-quality graphene is required. Currently, the only method to generate large-area single-layer graphene that is compatible with roll-to-roll manufacturing destroys approximately 300 kg of copper foil (thickness = 25 μm) for every 1 g of graphene produced. This paper describes a new environmentally benign and scalable process of transferring graphene to flexible substrates. The process is based on the preferential adhesion of certain thin metallic films to graphene; separation of the graphene from the catalytic copper foil is followed by lamination to a flexible target substrate in a process that is compatible with roll-to-roll manufacturing. The copper substrate is indefinitely reusable and the method is substantially greener than the current process that uses relatively large amounts of corrosive etchants to remove the copper. The sheet resistance of the graphene produced by this new process is unoptimized but should be comparable in principle to that produced by the standard method, given the defects observable by Raman spectroscopy and the presence of process-induced cracks. With further improvements, this green, inexpensive synthesis of single-layer graphene could enable applications in flexible, stretchable, and disposable electronics, low-profile and lightweight barrier materials, and in large-area displays and photovoltaic modules.

Method for fabrication of ceramic dielectric films on copper foils

DOEpatents

Ma, Beihai; Narayanan, Manoj; Dorris, Stephen E.; Balachandran, Uthamalingam

2015-03-10

The present invention provides a method for fabricating a ceramic film on a copper foil. The method comprises applying a layer of a sol-gel composition onto a copper foil. The sol-gel composition comprises a precursor of a ceramic material suspended in 2-methoxyethanol. The layer of sol-gel is then dried at a temperature up to about 250.degree. C. The dried layer is then pyrolyzed at a temperature in the range of about 300 to about 450.degree. C. to form a ceramic film from the ceramic precursor. The ceramic film is then crystallized at a temperature in the range of about 600 to about 750.degree. C. The drying, pyrolyzing and crystallizing are performed under a flowing stream of an inert gas. In some embodiments an additional layer of the sol-gel composition is applied onto the ceramic film and the drying, pyrolyzing and crystallizing steps are repeated for the additional layer to build up a thicker ceramic layer on the copper foil. The process can be repeated one or more times if desired.

Positron annihilation lifetime spectroscopy study of Kapton thin foils

NASA Astrophysics Data System (ADS)

Kanda, G. S.; Ravelli, L.; Löwe, B.; Egger, W.; Keeble, D. J.

2016-01-01

Variable energy positron annihilation lifetime spectroscopy (VE-PALS) experiments on polyimide material Kapton are reported. Thin Kapton foils are widely used in a variety of mechanical, electronic applications. PALS provides a sensitive probe of vacancy-related defects in a wide range of materials, including open volume in polymers. Varying the positron implantation energy enables direct measurement of thin foils. Thin Kapton foils are also commonly used to enclose the positron source material in conventional PALS measurements performed with unmoderated radionuclide sources. The results of depth-profiled positron lifetime measurements on 7.6 μm and 25 μm Kapton foils are reported and determine a dominant 385(1) ps lifetime component. The absence of significant nanosecond lifetime component due to positronium formation is confirmed.

Oxidation-assisted graphene heteroepitaxy on copper foil.

PubMed

Reckinger, Nicolas; Tang, Xiaohui; Joucken, Frédéric; Lajaunie, Luc; Arenal, Raul; Dubois, Emmanuel; Hackens, Benoît; Henrard, Luc; Colomer, Jean-François

2016-11-10

We propose an innovative, easy-to-implement approach to synthesize aligned large-area single-crystalline graphene flakes by chemical vapor deposition on copper foil. This method doubly takes advantage of residual oxygen present in the gas phase. First, by slightly oxidizing the copper surface, we induce grain boundary pinning in copper and, in consequence, the freezing of the thermal recrystallization process. Subsequent reduction of copper under hydrogen suddenly unlocks the delayed reconstruction, favoring the growth of centimeter-sized copper (111) grains through the mechanism of abnormal grain growth. Second, the oxidation of the copper surface also drastically reduces the nucleation density of graphene. This oxidation/reduction sequence leads to the synthesis of aligned millimeter-sized monolayer graphene domains in epitaxial registry with copper (111). The as-grown graphene flakes are demonstrated to be both single-crystalline and of high quality.

Novel technique of making thin target foil of high density material via rolling method

NASA Astrophysics Data System (ADS)

Gupta, C. K.; Rohilla, Aman; Singh, R. P.; Singh, Gurjot; Chamoli, S. K.

2018-05-01

The conventional rolling method fails to yield good quality thin foils of thicknesses less than 2 mg/cm2 for high density materials with Z ≥ 70 (e.g. gold, lead). A special and improved technique has been developed to obtain such low thickness good quality gold foils by rolling method. Using this technique thin gold foils of thickness in the range of 0.850-2.5 mg/cm2 were obtained in the present work. By making use of alcohol during rolling, foils of thickness 1 mg/cm2 can be obtained in shorter time with less effort.

Novel p-n heterojunction copper phosphide/cuprous oxide photocathode for solar hydrogen production.

PubMed

Chen, Ying-Chu; Chen, Zhong-Bo; Hsu, Yu-Kuei

2018-08-01

A Copper phosphide (Cu 3 P) micro-rod (MR) array, with coverage by an n-Cu 2 O thin layer by electrodeposition as a photocathode, has been directly fabricated on copper foil via simple electro-oxidation and phosphidation for photoelectrochemical (PEC) hydrogen production. The morphology, structure, and composition of the Cu 3 P/Cu 2 O heterostructure are systematically analyzed using a scanning electron microscope (SEM), X-ray diffraction and X-ray photoelectron spectra. The PEC measurements corroborate that the p-Cu 3 P/n-Cu 2 O heterostructural photocathode illustrates efficient charge separation and low charge transfer resistance to achieve the highest photocurrent of 430 μA cm -2 that is greater than other transition metal phosphide materials. In addition, a detailed energy diagram of the p-Cu 3 P/n-Cu 2 O heterostructure was investigated using Mott-Schottky analysis. Our study paves the way to explore phosphide-based materials in a new class for solar energy applications. Copyright © 2018 Elsevier Inc. All rights reserved.

Excitation functions of heavy ion induced nuclear reactions between 16O ion beam and natural copper: Measurements, analysis and its applicability in TLA study

NASA Astrophysics Data System (ADS)

Chowdhury, D. P.; Guin, R.; Saha, S. K.; Sudersanan, M.

2003-11-01

Experimental cross sections of a number of reaction channels of 16O ion induced reactions on natural copper target have been determined at different energies in the range of 50-110 MeV of 16O projectile by stacked foil activation technique. The cross sections have been compared with theoretical calculations using the computer code ALICE-91. The experimental values compared reasonably well with the corresponding theoretical estimates. The results indicate no significant role of incomplete fusion process in the 16O induced reactions on natural copper in the energy range of ⩽7 MeV/nucleon. As heavy ion beam produces an extremely narrow layer of activities in the surface of a material, these reactions could be useful for thin layer activation (TLA) study. The purpose of this work is to apply heavy ion activation in TLA technique for the study of surface wear with increased sensitivity.

Method for laser welding ultra-thin metal foils

DOEpatents

Pernicka, J.C.; Benson, D.K.; Tracy, C.E.

1996-03-26

A method for simultaneously cutting and welding ultra-thin foils having a thickness of less than 0.002 inches wherein two ultra-thin films are stacked and clamped together. A pulsed laser such as of the Neodymium: YAG type is provided and the beam of the laser is directed onto the stacked films to cut a channel through the films. The laser is moved relative to the stacked foils to cut the stacked foils at successive locations and to form a plurality of connected weld beads to form a continuous weld. 5 figs.

Method for laser welding ultra-thin metal foils

DOEpatents

Pernicka, John C.; Benson, David K.; Tracy, C. Edwin

1996-01-01

A method for simultaneously cutting and welding ultra-thin foils having a thickness of less than 0.002 inches wherein two ultra-thin films are stacked and clamped together. A pulsed laser such as of the Neodymium: YAG type is provided and the beam of the laser is directed onto the stacked films to cut a channel through the films. The laser is moved relative to the stacked foils to cut the stacked foils at successive locations and to form a plurality of connected weld beads to form a continuous weld.

Tungsten foil laminate for structural divertor applications - Joining of tungsten foils

NASA Astrophysics Data System (ADS)

Reiser, Jens; Rieth, Michael; Möslang, Anton; Dafferner, Bernhard; Hoffmann, Jan; Mrotzek, Tobias; Hoffmann, Andreas; Armstrong, D. E. J.; Yi, Xiaoou

2013-05-01

This paper is the fourth in our series on tungsten laminates. The aim of this paper is to discuss laminate synthesis, meaning the joining of tungsten foils. It is obvious that the properties of the tungsten laminate strongly depend on the combination of (i) interlayer and (ii) joining technology, as this combination defines (i) the condition of the tungsten foil after joining (as-received or recrystallised) as well as (ii) the characteristics of the interface between the tungsten foil and the interlayer (wettability or diffusion leading to a solid solution or the formation of intermetallics). From the example of tungsten laminates joined by brazing with (i) an eutectic silver copper brazing filler, (ii) copper, (iii) titanium, and (iv) zirconium, the microstructure will be discussed, with special focus on the interface. Based on our assumptions of the mechanism of the extraordinary ductility of tungsten foil we present three syntheses strategies and make recommendations for the synthesis of high temperature tungsten laminates.

Simultaneous laser cutting and welding of metal foil to edge of a plate

DOEpatents

Pernicka, John C.; Benson, David K.; Tracy, C. Edwin

1996-01-01

A method of welding an ultra-thin foil to the edge of a thicker sheet to form a vacuum insulation panel comprising the steps of providing an ultra-thin foil having a thickness less than 0.002, providing a top plate having an edge and a bottom plate having an edge, clamping the foil to the edge of the plate wherein the clamps act as heat sinks to distribute heat through the foil, providing a laser, moving the laser relative to the foil and the plate edges to form overlapping weld beads to weld the foil to the plate edges while simultaneously cutting the foil along the weld line formed by the overlapping beads.

Copper vapor-assisted growth of hexagonal graphene domains on silica islands

DOE Office of Scientific and Technical Information (OSTI.GOV)

Li, Jun; Que, Yande; Jiang, Lili

2016-07-11

Silica (SiO{sub 2}) islands with a dendritic structure were prepared on polycrystalline copper foil, using silane (SiH{sub 4}) as a precursor, by annealing at high temperature. Assisted by copper vapor from bare sections of the foil, single-layer hexagonal graphene domains were grown directly on the SiO{sub 2} islands by chemical vapor deposition. Scanning electron microscopy, atomic force microscopy, Raman spectra, and X-ray photoelectron spectroscopy confirm that hexagonal graphene domains, each measuring several microns, were synthesized on the silica islands.

Piezoelectric characterization of Pb(Zr,Ti)O3 thin films deposited on metal foil substrates by dip coating

NASA Astrophysics Data System (ADS)

Hida, Hirotaka; Hamamura, Tomohiro; Nishi, Takahito; Tan, Goon; Umegaki, Toshihito; Kanno, Isaku

2017-10-01

We fabricated the piezoelectric bimorphs composed of Pb(Zr,Ti)O3 (PZT) thin films on metal foil substrates. To efficiently inexpensively manufacture piezoelectric bimorphs with high flexibility, 1.2-µm-thick PZT thin films were directly deposited on both surfaces of 10- and 20-µm-thick bare stainless-steel (SS) foil substrates by dip coating with a sol-gel solution. We confirmed that the PZT thin films deposited on the SS foil substrates at 500 °C or above have polycrystalline perovskite structures and the measured relative dielectric constant and dielectric loss were 323-420 and 0.12-0.17, respectively. The PZT bimorphs were demonstrated by comparing the displacements of the cantilever specimens driven by single- and double-side PZT thin films on the SS foil substrates under the same applied voltage. We characterized the piezoelectric properties of the PZT bimorphs and the calculated their piezoelectric coefficient |e 31,f| to be 0.3-0.7 C/m2.

Scanning electron microscopy imaging of dislocations in bulk materials, using electron channeling contrast.

PubMed

Crimp, Martin A

2006-05-01

The imaging and characterization of dislocations is commonly carried out by thin foil transmission electron microscopy (TEM) using diffraction contrast imaging. However, the thin foil approach is limited by difficult sample preparation, thin foil artifacts, relatively small viewable areas, and constraints on carrying out in situ studies. Electron channeling imaging of electron channeling contrast imaging (ECCI) offers an alternative approach for imaging crystalline defects, including dislocations. Because ECCI is carried out with field emission gun scanning electron microscope (FEG-SEM) using bulk specimens, many of the limitations of TEM thin foil analysis are overcome. This paper outlines the development of electron channeling patterns and channeling imaging to the current state of the art. The experimental parameters and set up necessary to carry out routine channeling imaging are reviewed. A number of examples that illustrate some of the advantages of ECCI over thin foil TEM are presented along with a discussion of some of the limitations on carrying out channeling contrast analysis of defect structures. Copyright (c) 2006 Wiley-Liss, Inc.

Patterning of Thick Parylene Films by Oxygen Plasma for Application as Exploding Foil Initiator Flyer Material

DTIC Science & Technology

2009-09-01

exploding foil initiator ( EFI ) type fuzes are being explored to...Acronyms Au gold Cr chromium Cu copper EFI exploding foil initiator BOE buffered oxide etch MEMS microelectromechanical systems RIE reactive ion...Patterning of Thick Parylene Films by Oxygen Plasma for Application as Exploding Foil Initiator Flyer Material by Eugene Zakar and Michael

My Spring with Graphene

DOE Office of Scientific and Technical Information (OSTI.GOV)

O'Leary, Timothy Sean

2015-06-08

Graphene is a two-dimensional structure, one atom thick, with many uses in the world of technology. It has many useful electrical properties, is a very strong and durable material, and can be used to protect different types of substances. The world would be able to use these properties to further the strength of cars, protect metals from oxidation, increase computer speeds, use to improve superconductors, and whatever future uses that scientist invent or discover. We sought to optimize the growth and transfer of graphene. We grew graphene on copper foils by heating the foil in a furnace, and having variousmore » gases flow through a tube, where the copper foil was placed. We varied some of the concentrations of gases, along with having different times for heating the copper foil, different times for graphene growth, or a combination of the two. The focus of our experiment was to specifically grow monolayer single crystal graphene, which means that we do not want multiplayers of graphene, and do not want multiple crystals growing to form a bigger crystal. Our goal was to grow large single crystals from the growth experiment. We used a few different types of transfer methods that ranged from: using heat and pressure to press the graphene on different materials, using a polymer to cover the graphene with a method to destroy the copper, but leave the graphene and polymer intact, and using a type of heat tape with a combination of varying pressures to transfer the graphene, and then destroy the copper foil. To discover if we grew graphene we used different techniques involving lasers and microscopes to take different types of measurements. Discovering the best way of growing and transferring graphene will help with managing the cost of the future uses of graphene.« less

Wideband characterization of printed circuit board materials up to 50 ghz

NASA Astrophysics Data System (ADS)

Rakov, Aleksei

A traveling-wave technique developed a few years ago in the Missouri S&T EMC Laboratory has been employed until now for characterization of PCB materials over a broad frequency range up to 30 GHz. This technique includes measuring S-parameters of the specially designed PCB test vehicles. An extension of the frequency range of printed circuit board laminate dielectric and copper foil characterization is an important problem. In this work, a new PCB test vehicle design for operating up to 50 GHz has been proposed. As the frequency range of measurements increases, the analysis of errors and uncertainties in measuring dielectric properties becomes increasingly important. Formulas for quantification of two major groups of errors, repeatability (manufacturing variability) and reproducibility (systematic) errors, in extracting dielectric constant (DK) and dissipation factor (DK) have been derived, and computations for a number of cases are presented. Conductor (copper foil) surface roughness of PCB interconnects is an important factor, which affects accuracy of DK and DF measurements. This work describes a new algorithm for semi-automatic characterization of copper foil profiles on optical or scanning electron microscopy (SEM) pictures of signal traces. The collected statistics of numerous copper foil roughness profiles allows for introducing a new metric for roughness characterization of PCB interconnects. This is an important step to refining the measured DK and DF parameters from roughness contributions. The collected foil profile data and its analysis allow for developing "design curves", which could be used by SI engineers and electronics developers in their designs.

Simultaneous laser cutting and welding of metal foil to edge of a plate

DOEpatents

Pernicka, J.C.; Benson, D.K.; Tracy, C.E.

1996-03-19

A method is described for welding an ultra-thin foil to the edge of a thicker sheet to form a vacuum insulation panel comprising the steps of providing an ultra-thin foil having a thickness less than 0.002, providing a top plate having an edge and a bottom plate having an edge, clamping the foil to the edge of the plate wherein the clamps act as heat sinks to distribute heat through the foil, providing a laser, moving the laser relative to the foil and the plate edges to form overlapping weld beads to weld the foil to the plate edges while simultaneously cutting the foil along the weld line formed by the overlapping beads. 7 figs.

Calibration of a thin metal foil for infrared imaging video bolometer to estimate the spatial variation of thermal diffusivity using a photo-thermal technique.

PubMed

Pandya, Shwetang N; Peterson, Byron J; Sano, Ryuichi; Mukai, Kiyofumi; Drapiko, Evgeny A; Alekseyev, Andrey G; Akiyama, Tsuyoshi; Itomi, Muneji; Watanabe, Takashi

2014-05-01

A thin metal foil is used as a broad band radiation absorber for the InfraRed imaging Video Bolometer (IRVB), which is a vital diagnostic for studying three-dimensional radiation structures from high temperature plasmas in the Large Helical Device. The two-dimensional (2D) heat diffusion equation of the foil needs to be solved numerically to estimate the radiation falling on the foil through a pinhole geometry. The thermal, physical, and optical properties of the metal foil are among the inputs to the code besides the spatiotemporal variation of temperature, for reliable estimation of the exhaust power from the plasma illuminating the foil. The foil being very thin and of considerable size, non-uniformities in these properties need to be determined by suitable calibration procedures. The graphite spray used for increasing the surface emissivity also contributes to a change in the thermal properties. This paper discusses the application of the thermographic technique for determining the spatial variation of the effective in-plane thermal diffusivity of the thin metal foil and graphite composite. The paper also discusses the advantages of this technique in the light of limitations and drawbacks presented by other calibration techniques being practiced currently. The technique is initially applied to a material of known thickness and thermal properties for validation and finally to thin foils of gold and platinum both with two different thicknesses. It is observed that the effect of the graphite layer on the estimation of the thermal diffusivity becomes more pronounced for thinner foils and the measured values are approximately 2.5-3 times lower than the literature values. It is also observed that the percentage reduction in thermal diffusivity due to the coating is lower for high thermal diffusivity materials such as gold. This fact may also explain, albeit partially, the higher sensitivity of the platinum foil as compared to gold.

Calibration of a thin metal foil for infrared imaging video bolometer to estimate the spatial variation of thermal diffusivity using a photo-thermal technique

DOE Office of Scientific and Technical Information (OSTI.GOV)

Pandya, Shwetang N., E-mail: pandya.shwetang@LHD.nifs.ac.jp; Sano, Ryuichi; Peterson, Byron J.

A thin metal foil is used as a broad band radiation absorber for the InfraRed imaging Video Bolometer (IRVB), which is a vital diagnostic for studying three-dimensional radiation structures from high temperature plasmas in the Large Helical Device. The two-dimensional (2D) heat diffusion equation of the foil needs to be solved numerically to estimate the radiation falling on the foil through a pinhole geometry. The thermal, physical, and optical properties of the metal foil are among the inputs to the code besides the spatiotemporal variation of temperature, for reliable estimation of the exhaust power from the plasma illuminating the foil.more » The foil being very thin and of considerable size, non-uniformities in these properties need to be determined by suitable calibration procedures. The graphite spray used for increasing the surface emissivity also contributes to a change in the thermal properties. This paper discusses the application of the thermographic technique for determining the spatial variation of the effective in-plane thermal diffusivity of the thin metal foil and graphite composite. The paper also discusses the advantages of this technique in the light of limitations and drawbacks presented by other calibration techniques being practiced currently. The technique is initially applied to a material of known thickness and thermal properties for validation and finally to thin foils of gold and platinum both with two different thicknesses. It is observed that the effect of the graphite layer on the estimation of the thermal diffusivity becomes more pronounced for thinner foils and the measured values are approximately 2.5–3 times lower than the literature values. It is also observed that the percentage reduction in thermal diffusivity due to the coating is lower for high thermal diffusivity materials such as gold. This fact may also explain, albeit partially, the higher sensitivity of the platinum foil as compared to gold.« less

Brazing Inconel 625 Using the Copper Foil

NASA Astrophysics Data System (ADS)

Chen, Wen-Shiang; Wang, Cheng-Yen; Shiue, Ren-Kae

2013-12-01

Brazing Inconel 625 (IN-625) using the copper foil has been investigated in this research. The brazed joint is composed of nanosized CrNi3 precipitates and Cr/Mo/Nb/Ni quaternary compound in the Cu/Ni-rich matrix. The copper filler 50 μm in thickness is enough for the joint filling. However, the application of Cu foil 100 μm in thickness has little effect on the shear strength of the brazed joint. The specimen brazed at 1433 K (1160 °C) for 1800 seconds demonstrates the best shear strength of 470 MPa, and its fractograph is dominated by ductile dimple fracture with sliding marks. Decreasing the brazing temperature slightly decreases the shear strength of the brazed joint due to the presence of a few isolated solidification shrinkage voids smaller than 15 μm. Increasing the brazing temperature, especially for the specimen brazed at 1473 K (1200 °C), significantly deteriorates the shear strength of the joint below 260 MPa because of coalescence of isothermal solidification shrinkage voids in the joint. The Cu foil demonstrates potential in brazing IN-625 for industrial application.

Preparation and comparative testing of advanced diamond-like carbon foils for tandem accelerators and time-of-flight spectrometers

NASA Astrophysics Data System (ADS)

Liechtenstein, V. Kh.; Ivkova, T. M.; Olshanski, E. D.; Baranov, A. M.; Repnow, R.; Hellborg, R.; Weller, R. A.; Wirth, H. L.

1999-12-01

The sputter preparation technique for thin diamond-like carbon (DLC) foils, advantageously used for ion-beam stripping and timing in accelerator experiments, has been optimized to improve the quality and the performance of the foils. Irradiation lifetimes of 5 μg/cm 2 DLC foils prepared by this technique have been compared with those for foils of approximately the same thickness, prepared by laser plasma ablation and for ethylene cracked foils when bombarded by 11 MeV Cu - - and Au --ion beams of ˜1 μA beam current at the Heidelberg MP-tandem. Standard carbon arc-evaporated foils were used as references. In these experiments, DLC stripper foils appeared to have a mean lifetime approximately two times longer than ethylene-cracked foils regardless of ion species, and compared favorably with foils prepared by laser ablation method. All these foils lasted at least, 10 times longer than standard carbon foils, when irradiated in the MP terminal. Approximately, the same improvement factor was confirmed with 3 μg/cm 2 DLC stripper foils irradiated with 2.3 MeV Ni-beams at the Pelletron accelerator in Lund. Unlike standard carbon foils, most of the advanced lifetime foils exhibited thinning during long irradiation, under clean vacuum. This suggests that sputtering of the foil by the heavy-ion beam might be a dominant process, responsible for the observed failure of these long-lived strippers. Along with specifically corrugated self-supporting DLC beam strippers, we succeeded in the fabrication of very smooth and ultra thin (˜0.5 μg/cm 2) DLC foils, mounted on grids and used as start foils for the ToF spectrometers applied in ion beam analysis.

Method of forming a thin unbacked metal foil

DOEpatents

Duchane, David V.; Barthell, Barry L.

1984-01-01

In a method of forming a thin (<2 .mu.m) unbacked metal foil having a desired curviplanar shape, a soluble polymeric film, preferably comprising polyvinyl alcohol, is formed on a supporting structure having a shape that defines the desired shape of the foil product. A layer of metal foil is deposited onto one side of the soluble film, preferably by vacuum vapor deposition. The metallized film is then immersed in a suitable solvent to dissolve the film and thereby leave the metal foil as an unbacked metal foil element mounted on the supporting structure. Aluminum foils less than 0.2 .mu.m (2,000 .ANG.) thick and having an areal density of less than 54 .mu.g/cm.sup.2 have been obtained.

Ultrafast proton radiography of the magnetic fields generated by a laser-driven coil current

DOE PAGES

Gao, Lan; Ji, Hantao; Fiksel, Gennady; ...

2016-04-15

Magnetic fields generated by a current flowing through a U-shaped coil connecting two copper foils were measured using ultrafast proton radiography. Two ~ 1.25 kJ, 1-ns laser pulses propagated through laser entrance holes in the front foil and were focused to the back foil with an intensity of ~ 3 x 10 16 W/cm 2. The intense laser-solid interaction induced a high voltage between the copper foils and generated a large current in the connecting coil. The proton data show ~ 40-50 T magnetic fields at the center of the coil ~ 3-4 ns after laser irradiation. In conclusion, themore » experiments provide significant insight for future target designs that aim to develop a powerful source of external magnetic fields for various applications in high-energy-density science.« less

200 kj copper foil fuses. Final report

DOE Office of Scientific and Technical Information (OSTI.GOV)

McClenahan, C.R.; Goforth, J.H.; Degnan, J.H.

1980-04-01

A 200-kJ, 50-kV capacitor bank has been discharged into 1-mil-thick copper foils immersed in fine glass beads. These foils ranged in length from 27 to 71 cm and in width from 15 to 40 cm. Voltage spikes of over 250 kV were produced by the resulting fuse behavior of the foil. Moreover, the current turned off at a rate that was over 6 times the initial bank dI/dt. Full widths at half maxima for the voltage and dI/dt spikes were about 0.5 microsec, with some as short as 300 nanosec. Electrical breakdown was prevented in all but one size fuzemore » with maximum applied fields of 7 kV/cm. Fuses that were split into two parallel sections have been tested, and the effects relative to one-piece fuses are much larger than would be expected on the basis of inductance differences alone. A resistivity model for copper foil fuses, which differs from previous work in that it includes a current density dependence, has been devised. Fuse behavior is predicted with reasonable accuracy over a wide range of foil sizes by a quasi-two-dimensional fuse code that incorporates this resistivity model. A variation of Maisonnier's method for predicting optimum fuze size has been derived. This method is valid if the risetime of the bank exceeds 3 microsec, in which case it can be expected to be applicable over a wide range of peak current densities.« less

Shock compression response of highly reactive Ni + Al multilayered thin foils

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kelly, Sean C.; Thadhani, Naresh N., E-mail: naresh.thadhani@mse.gatech.edu

2016-03-07

The shock-compression response of Ni + Al multilayered thin foils is investigated using laser-accelerated thin-foil plate-impact experiments over the pressure range of 2 to 11 GPa. The foils contain alternating Ni and Al layers (parallel but not flat) of nominally 50 nm bilayer spacing. The goal is to determine the equation of state and shock-induced reactivity of these highly reactive fully dense thin-foil materials. The laser-accelerated thin-foil impact set-up involved combined use of photon-doppler-velocimetry to monitor the acceleration and impact velocity of an aluminum flyer, and VISAR interferometry was used to monitor the back free-surface velocity of the impacted Ni + Al multilayered target. The shock-compressionmore » response of the Ni + Al target foils was determined using experimentally measured parameters and impedance matching approach, with error bars identified considering systematic and experimental errors. Meso-scale CTH shock simulations were performed using real imported microstructures of the cross-sections of the multilayered Ni + Al foils to compute the Hugoniot response (assuming no reaction) for correlation with their experimentally determined equation of state. It was observed that at particle velocities below ∼150 m/s, the experimentally determined equation of state trend matches the CTH-predicted inert response and is consistent with the observed unreacted state of the recovered Ni + Al target foils from this velocity regime. At higher particle velocities, the experimentally determined equation of state deviates from the CTH-predicted inert response. A complete and self-sustained reaction is also seen in targets recovered from experiments performed at these higher particle velocities. The deviation in the measured equation of state, to higher shock speeds and expanded volumes, combined with the observation of complete reaction in the recovered multilayered foils, confirmed via microstructure characterization, is indicative of the occurrence of shock-induced chemical reaction occurring in the time-scale of the high-pressure state. TEM characterization of recovered shock-compressed (unreacted) Ni + Al multilayered foils exhibits distinct features of constituent mixing revealing jetted layers and inter-mixed regions. These features were primarily observed in the proximity of the undulations present in the alternating layers of the Ni + Al starting foils, suggesting the important role of such instabilities in promoting shock-induced intermetallic-forming reactions in the fully dense highly exothermic multilayered thin foils.« less

Electron Emission from Amorphous Solid Water Induced by Passage of Energetic Protons and Fluorine Ions

PubMed Central

Toburen, L. H.; McLawhorn, S. L.; McLawhorn, R. A.; Carnes, K. D.; Dingfelder, M.; Shinpaugh, J. L.

2013-01-01

Absolute doubly differential electron emission yields were measured from thin films of amorphous solid water (ASW) after the transmission of 6 MeV protons and 19 MeV (1 MeV/nucleon) fluorine ions. The ASW films were frozen on thin (1-μm) copper foils cooled to approximately 50 K. Electrons emitted from the films were detected as a function of angle in both the forward and backward direction and as a function of the film thickness. Electron energies were determined by measuring the ejected electron time of flight, a technique that optimizes the accuracy of measuring low-energy electron yields, where the effects of molecular environment on electron transport are expected to be most evident. Relative electron emission yields were normalized to an absolute scale by comparison of the integrated total yields for proton-induced electron emission from the copper substrate to values published previously. The absolute doubly differential yields from ASW are presented along with integrated values, providing single differential and total electron emission yields. These data may provide benchmark tests of Monte Carlo track structure codes commonly used for assessing the effects of radiation quality on biological effectiveness. PMID:20681805

Lenz's Law with Aluminum Foil and a Lengthwise Slit

ERIC Educational Resources Information Center

Berls, Rob; Ruiz, Michael J.

2018-01-01

The classic demonstration illustrating Lenz's law by dropping a magnet through a copper pipe is presented using household aluminum foil right out of the box. Then comes the surprise. The teacher presents an aluminum foil cylinder with a missing lengthwise slice (cut before class). Will the demonstration still work? Students are amazed at the…

Approximating the near-edge mass absorption coefficients for Ni using an ultra-thin bimetal foil

DOE PAGES

Alkire, Randall W.

2016-11-01

In an effort to improve the characteristics of a fluorescing metal-foil-based beam position monitor, a new bimetal ultra-thin (0.98/0.67 µm) Ti–Ni foil was introduced to replace an existing single-element ultra-thin 0.5 µm thick Cr foil. During characterization it was determined that absorption measurements on the bimetal foil could be used to fit the Ni mass absorption coefficients accurately in the vicinity of the NiKedge. Comparison with experimental results from the literature demonstrated that the fitting procedure produced coefficients with uncertainties of the order of ±1%. Once determined, these fit coefficients allowed the thickness of an independently mounted 8 µm thickmore » Ni foil to be computed from absorption measurements instead of relying on a tool-based measurement of the foil thickness. Using the 8 µm thick foil, a continuous map of Ni mass absorption coefficients was produced at 1 eV resolution throughout the near-edge region. Lastly, this high-resolution map marks a significant improvement over the existing NIST XCOM or FFAST database mass absorption coefficients, which have estimated errors of 10–20% for the near-edge region.« less

Controllable poly-crystalline bilayered and multilayered graphene film growth by reciprocal chemical vapor deposition

NASA Astrophysics Data System (ADS)

Wu, Qinke; Jung, Seong Jun; Jang, Sung Kyu; Lee, Joohyun; Jeon, Insu; Suh, Hwansoo; Kim, Yong Ho; Lee, Young Hee; Lee, Sungjoo; Song, Young Jae

2015-06-01

We report the selective growth of large-area bilayered graphene film and multilayered graphene film on copper. This growth was achieved by introducing a reciprocal chemical vapor deposition (CVD) process that took advantage of an intermediate h-BN layer as a sacrificial template for graphene growth. A thin h-BN film, initially grown on the copper substrate using CVD methods, was locally etched away during the subsequent graphene growth under residual H2 and CH4 gas flows. Etching of the h-BN layer formed a channel that permitted the growth of additional graphene adlayers below the existing graphene layer. Bilayered graphene typically covers an entire Cu foil with domain sizes of 10-50 μm, whereas multilayered graphene can be epitaxially grown to form islands a few hundreds of microns in size. This new mechanism, in which graphene growth proceeded simultaneously with h-BN etching, suggests a potential approach to control graphene layers for engineering the band structures of large-area graphene for electronic device applications.We report the selective growth of large-area bilayered graphene film and multilayered graphene film on copper. This growth was achieved by introducing a reciprocal chemical vapor deposition (CVD) process that took advantage of an intermediate h-BN layer as a sacrificial template for graphene growth. A thin h-BN film, initially grown on the copper substrate using CVD methods, was locally etched away during the subsequent graphene growth under residual H2 and CH4 gas flows. Etching of the h-BN layer formed a channel that permitted the growth of additional graphene adlayers below the existing graphene layer. Bilayered graphene typically covers an entire Cu foil with domain sizes of 10-50 μm, whereas multilayered graphene can be epitaxially grown to form islands a few hundreds of microns in size. This new mechanism, in which graphene growth proceeded simultaneously with h-BN etching, suggests a potential approach to control graphene layers for engineering the band structures of large-area graphene for electronic device applications. Electronic supplementary information (ESI) available: The growth conditions, statistical studies of OM images and high-resolution STM/TEM measurements for multi-/bi-layered graphene are discussed in detail. See DOI: 10.1039/c5nr02716k

n-Type Conductivity of Cu2O Thin Film Prepared in Basic Aqueous Solution Under Hydrothermal Conditions

NASA Astrophysics Data System (ADS)

Ursu, Daniel; Miclau, Nicolae; Miclau, Marinela

2018-03-01

We report for the first time in situ hydrothermal synthesis of n-type Cu2O thin film using strong alkaline solution. The use of copper foil as substrate and precursor material, low synthesis temperature and short reaction time represent the arguments of a new, simple, inexpensive and high field synthesis method for the preparation of n-type Cu2O thin film. The donor concentration of n-type Cu2O thin film obtained at 2 h of reaction time has increased two orders of magnitude than previous reported values. We have demonstrated n-type conduction in Cu2O thin film prepared in strong alkaline solution, in the contradiction with the previous works. Based on experimental results, the synthesis mechanism and the origin of n-type photo-responsive behavior of Cu2O thin film were discussed. We have proposed that the unexpected n-type character could be explained by H doping of Cu2O thin film in during of the hydrothermal synthesis that caused the p-to-n conductivity-type conversion. Also, this work raises new questions about the origin of n-type conduction in Cu2O thin film, the influence of the synthesis method on the nature of the intrinsic defects and the electrical conduction behavior.

X-ray optics made from thin plastic foils

NASA Astrophysics Data System (ADS)

Schnopper, Herbert W.; Silver, Eric H.; Ingram, Russell H.; Christensen, Finn E.; Hussain, Ahsen M.; Barbera, Marco; Romaine, Suzanne E.; Collura, Alfonso; Kenter, Almus T.; Bandler, Simon; Murray, Stephen S.

1999-09-01

New design concepts and materials can be used to produce very lightweight, thin foil approximations, to Wolter I and other x-ray optics. Structures are designed around a central hub and spacers that connect one spoked wheels. Figure defining, thin pins span the distance between the wheels. Thin, metal coated or multilayered, plastic foils can be formed into cones, cylinders or spirals for x-ray telescopes or lenses. Imaging and spectroscopic data obtained with x- ray lenses are presented and they indicate that a 60 cm diameter, 4.65 m focal length x-ray telescope can have a half power diameter of < 2 arcmin.

Ultrafast proton radiography of the magnetic fields generated by a laser-driven coil current

DOE Office of Scientific and Technical Information (OSTI.GOV)

Gao, Lan; Ji, Hantao; Princeton Plasma Physics Laboratory, Princeton University, Princeton, New Jersey 08543

2016-04-15

Magnetic fields generated by a current flowing through a U-shaped coil connecting two copper foils were measured using ultrafast proton radiography. Two ∼1.25 kJ, 1-ns laser pulses propagated through laser entrance holes in the front foil and were focused to the back foil with an intensity of ∼3 × 10{sup 16 }W/cm{sup 2}. The intense laser-solid interaction induced a high voltage between the copper foils and generated a large current in the connecting coil. The proton data show ∼40–50 T magnetic fields at the center of the coil ∼3–4 ns after laser irradiation. The experiments provide significant insight for future target designs that aim tomore » develop a powerful source of external magnetic fields for various applications in high-energy-density science.« less

Radiation pressure acceleration of corrugated thin foils by Gaussian and super-Gaussian beams

DOE Office of Scientific and Technical Information (OSTI.GOV)

Adusumilli, K.; Goyal, D.; Tripathi, V. K.

Rayleigh-Taylor instability of radiation pressure accelerated ultrathin foils by laser having Gaussian and super-Gaussian intensity distribution is investigated using a single fluid code. The foil is allowed to have ring shaped surface ripples. The radiation pressure force on such a foil is non-uniform with finite transverse component F{sub r}; F{sub r} varies periodically with r. Subsequently, the ripple grows as the foil moves ahead along z. With a Gaussian beam, the foil acquires an overall curvature due to non-uniformity in radiation pressure and gets thinner. In the process, the ripple perturbation is considerably washed off. With super-Gaussian beam, the ripplemore » is found to be more strongly washed out. In order to avoid transmission of the laser through the thinning foil, a criterion on the foil thickness is obtained.« less

Thin silicon foils produced by epoxy-induced spalling of silicon for high efficiency solar cells

DOE Office of Scientific and Technical Information (OSTI.GOV)

Martini, R., E-mail: roberto.martini@imec.be; imec, Kapeldreef 75, 3001 Leuven; Kepa, J.

2014-10-27

We report on the drastic improvement of the quality of thin silicon foils produced by epoxy-induced spalling. In the past, researchers have proposed to fabricate silicon foils by spalling silicon substrates with different stress-inducing materials to manufacture thin silicon solar cells. However, the reported values of effective minority carrier lifetime of the fabricated foils remained always limited to ∼100 μs or below. In this work, we investigate epoxy-induced exfoliated foils by electron spin resonance to analyze the limiting factors of the minority carrier lifetime. These measurements highlight the presence of disordered dangling bonds and dislocation-like defects generated by the exfoliation process.more » A solution to remove these defects compatible with the process flow to fabricate solar cells is proposed. After etching off less than 1 μm of material, the lifetime of the foil increases by more than a factor of 4.5, reaching a value of 461 μs. This corresponds to a lower limit of the diffusion length of more than 7 times the foil thickness. Regions with different lifetime correlate well with the roughness of the crack surface which suggests that the lifetime is now limited by the quality of the passivation of rough surfaces. The reported values of the minority carrier lifetime show a potential for high efficiency (>22%) thin silicon solar cells.« less

Pu-Zr alloy for high-temperature foil-type fuel

DOEpatents

McCuaig, Franklin D.

1977-01-01

A nuclear reactor fuel alloy consists essentially of from slightly greater than 7 to about 4 w/o zirconium, balance plutonium, and is characterized in that the alloy is castable and is rollable to thin foils. A preferred embodiment of about 7 w/o zirconium, balance plutonium, has a melting point substantially above the melting point of plutonium, is rollable to foils as thin as 0.0005 inch thick, and is compatible with cladding material when repeatedly cycled to temperatures above 650.degree. C. Neutron reflux densities across a reactor core can be determined with a high-temperature activation-measurement foil which consists of a fuel alloy foil core sandwiched and sealed between two cladding material jackets, the fuel alloy foil core being a 7 w/o zirconium, plutonium foil which is from 0.005 to 0.0005 inch thick.

Pu-ZR Alloy high-temperature activation-measurement foil

DOEpatents

McCuaig, Franklin D.

1977-08-02

A nuclear reactor fuel alloy consists essentially of from slightly greater than 7 to about 4 w/o zirconium, balance plutonium, and is characterized in that the alloy is castable and is rollable to thin foils. A preferred embodiment of about 7 w/o zirconium, balance plutonium, has a melting point substantially above the melting point of plutonium, is rollable to foils as thin as 0.0005 inch thick, and is compatible with cladding material when repeatedly cycled to temperatures above 650.degree. C. Neutron flux densities across a reactor core can be determined with a high-temperature activation-measurement foil which consists of a fuel alloy foil core sandwiched and sealed between two cladding material jackets, the fuel alloy foil core being a 7 w/o zirconium, plutonium foil which is from 0.005 to 0.0005 inch thick.

Copper foil provides uniform heat sink path

NASA Technical Reports Server (NTRS)

Phillips, I. E., Jr.; Schreihans, F. A.

1966-01-01

Thermal path prevents voids and discontinuities which make heat sinks in electronic equipment inefficient. The thermal path combines the high thermal conductivity of copper with the resiliency of silicone rubber.

Lenz’s law with aluminum foil and a lengthwise slit

NASA Astrophysics Data System (ADS)

Berls, Rob; Ruiz, Michael J.

2018-07-01

The classic demonstration illustrating Lenz’s law by dropping a magnet through a copper pipe is presented using household aluminum foil right out of the box. Then comes the surprise. The teacher presents an aluminum foil cylinder with a missing lengthwise slice (cut before class). Will the demonstration still work? Students are amazed at the result, described in this paper and included in our accompanying video (Ruiz 2018 Video: Lenz’s law with aluminum foil http://mjtruiz.com/ped/aluminum/).

Advanced foil activation techniques for the measurement of within-pin distributions of the 63Cu(n,γ) 64Cu reaction rate in nuclear fuel

NASA Astrophysics Data System (ADS)

Macku, K.; Jatuff, F.; Murphy, M. F.; Joneja, O. P.; Bischofberger, R.; Chawla, R.

2006-06-01

Different foil activation techniques have been used for measuring spatial distributions of the 63Cu(n,γ) 64Cu reaction within two pins of a SVEA-96 Optima2 boiling water reactor fuel assembly, at the critical facility PROTEUS. This reaction is of interest because its 1/v cross-section gives it a good representation of the 235U fission rate. Initially, radial capture rate profiles were measured with mechanically punched copper foils. More detailed profiles were then determined by using a 0.2 mm copper wire spiral (˜200 μm resolution), as well as 5-, 10-, and 20-ring UV-lithography, electroplating, and molding (UV-LIGA) foils (up to a 100 μm resolution). For azimuthal measurements, apart from manually cut activation foils (into 8 sectors), 8- and 12-sector LIGA foils were used. The highly versatile LIGA foils have the additional advantage of being very easily separated into individual pieces after irradiation without the use of punches or other cutting tools. In order to account for the invasive character of the foil activation techniques, corrections to account for sample perturbations and for self-shielding effects were determined via simplified Monte Carlo (MCNP4C) modeling of the experimental setup. The final results from the various measurements of 63Cu(n,γ) 64Cu within-pin distributions have been compared with MCNP computations employing a detailed model of the full SVEA Optima2 fuel assembly.

Fabrication of copper decorated tungsten oxide-titanium oxide nanotubes by photochemical deposition technique and their photocatalytic application under visible light

NASA Astrophysics Data System (ADS)

Momeni, Mohamad Mohsen

2015-12-01

Copper decorated WO3-TiO2 nanotubes (Cu/WTNs) with a high photocatalytic activity were prepared by anodizing and photochemical deposition. Highly ordered WO3-TiO2 nanotubes (WTNs) on pure titanium foils were successfully fabricated by electrochemical anodizing and copper deposited on these nanotubes (Cu/WTNs) by photoreduction method. The resulting samples were characterized by various methods. Only the anatase phase was detected by X-ray diffraction analysis. The presence of copper in the structure of thin films was confirmed by energy dispersive X-ray spectrometry and X-ray diffraction. The extension of optical absorption into the visible region of as-prepared films was indicated by UV/Vis spectroscopy. The degradation of methylene blue was used as a model reaction to evaluate the photocatalytic activity of the obtained samples. Results showed that the photocatalytic activity of Cu/WTNs samples is higher than bare WTNs sample. Kinetic research showed that the reaction rate constant of Cu/WTNs is approximately 2.5 times higher than the apparent reaction rate constant of bare WTNs. These results not only offer an economical method for constructing Cu/WTNs photocatalysts, but also shed new insight on the rational design of a low cost and high-efficiency photocatalyst for environmental remediation.

Edge-on dislocation loop in anisotropic hcp zirconium thin foil

NASA Astrophysics Data System (ADS)

Wu, Wenwang; Xia, Re; Qian, Guian; Xu, Shucai; Zhang, Jinhuan

2015-10-01

Edge-on dislocation loops with 〈 a 〉 -type and 〈 c 〉 -type of Burgers vectors can be formed on prismatic or basel habit planes of hexagonal close-packed (hcp) zirconium alloys during in-situ ion irradiation and neutron irradiation experiments. In this work, an anisotropic image stress method was employed to analyze the free surface effects of dislocation loops within hcp Zr thin foils. Calculation results demonstrate that image stress has a remarkable effect on the distortion fields of dislocation loops within infinite medium, and the image energy becomes remarkable when dislocation loops are situated close to the free surfaces. Moreover, image forces of the 1 / 2 〈 0001 〉 (0001) dislocation loop within (0001) thin foil is much stronger than that of the 1 / 3 〈 11 2 bar 0 〉 (11 2 bar 0) dislocation loop within (11 2 bar 0) thin foil of identical geometrical configurations. Finally, image stress effect on the physical behaviors of loops during in-situ ion irradiation experiments is discussed.

Role of target material in proton acceleration from thin foils irradiated by ultrashort laser pulses.

PubMed

Tayyab, M; Bagchi, S; Ramakrishna, B; Mandal, T; Upadhyay, A; Ramis, R; Chakera, J A; Naik, P A; Gupta, P D

2014-08-01

We report on the proton acceleration studies from thin metallic foils of varying atomic number (Z) and thicknesses, investigated using a 45 fs, 10 TW Ti:sapphire laser system. An optimum foil thickness was observed for efficient proton acceleration for our laser conditions, dictated by the laser ASE prepulse and hot electron propagation behavior inside the material. The hydrodynamic simulations for ASE prepulse support the experimental observation. The observed maximum proton energy at different thicknesses for a given element is in good agreement with the reported scaling laws. The results with foils of different atomic number Z suggest that a judicious choice of the foil material can enhance the proton acceleration efficiency, resulting into higher proton energy.

Suprathermal electrons in kJ-laser produced plasmas: M- shell resolved high-resolution x-ray spectroscopic study of transient matter evolution

NASA Astrophysics Data System (ADS)

Condamine, F. P.; Šmíd, M.; Renner, O.; Dozières, M.; Thais, F.; Angelo, P.; Bobin, J.-L.; Rosmej, F. B.

2016-05-01

Hot electrons are of key importance to understand many physical processes in plasma physics. They impact strongly on atomic physics as almost all radiative properties are seriously modified. X-ray spectroscopy is of particular interest due to reduced photoabsorption in dense matter. We report on a study of the copper Kα X-ray emission conducted at the ns, kJ laser facility PALS, Prague, Czech Republic. Thin copper foils have been irradiated with 1ω pulses. Two spherically bent quartz Bragg crystal spectrometers with high spectral and spatial resolution have been set up simultaneously to achieve a high level of confidence in the spectral distribution. In particular, an emission on the red wing of the Kα2 transition (λ = 1.5444 Å) could be identified with complex atomic structure calculations. We discuss possible implications for the analysis of non-equilibrium phenomena and present first atomic physics simulations.

Fabrication of free-standing copper foils covered with highly-ordered copper nanowire arrays

NASA Astrophysics Data System (ADS)

Zaraska, Leszek; Sulka, Grzegorz D.; Jaskuła, Marian

2012-07-01

The through-hole nanoporous anodic aluminum oxide (AAO) membranes with relatively large surface area (ca. 2 cm2) were employed for fabrication of free-standing and mechanically stable copper foils covered with close-packed and highly-ordered copper nanowire arrays. The home-made AAO membranes with different pore diameters and interpore distances were fabricated via a two-step self-organized anodization of aluminum performed in sulfuric acid, oxalic acid and phosphoric acid followed by the pore opening/widening procedure. The direct current (DC) electrodeposition of copper was performed efficiently on both sides of AAO templates. The bottom side of the AAO templates was not insulated and consequently Cu nanowire arrays on thick Cu layers were obtained. The proposed template-assisted fabrication of free-standing copper nanowire array electrodes is a promising method for synthesis of nanostructured current collectors. The composition of Cu nanowires was confirmed by energy dispersive X-Ray spectroscopy (EDS) and X-ray diffraction (XRD) analyses. The structural features of nanowires were evaluated from field emission scanning electron microscopy (FE-SEM) images and compared with the characteristic parameters of anodic alumina membranes.

Progress in Chile in the development of the fission {sup 99}Mo production using modified CINTICHEM

DOE Office of Scientific and Technical Information (OSTI.GOV)

Schrader, R.; Klein, J.; Medel, J.

2008-07-15

Fission {sup 99}Mo will be produced in Chile irradiating low-enriched uranium (LEU) foil in a MTR research reactor. For the purpose of developing the capability to fabricate the target, which is done of uranium foil enclosed in swaged concentric aluminum tubes, dummy targets are being fabricated using 130 {mu}m copper foil instead of the uranium foil, wrapped in a 14{mu}m nickel fission-recoil barrier. Dummy targets using several dimensions of copper foil have been assembled; however, the emphasis is being set in targets fabricated using the dimensions of the LEU foil that KAERI will provide, i.e. 50 mm x 100mm xmore » 0.130 mm. The assembling of target using the last dimensions has not been free of difficulties. Neutronic calculations and preliminary thermal and fluid analyses were performed to estimate the fission products activity and the heat removal capability for a 13 grams LEU-foil annular target, which will be irradiated in the RECH-1 research reactor at the level power of 5 MW during 48 hours. In a fume hood, Cintichem processing of natural uranium shavings with the addition of different carriers were performed, obtaining recovery over 90% of the added Mo carrier. Expertise has been gained in (a) foil dissolution process in a dissolver locally designed, (b) in Mo precipitation process, and (c) preparation of the purification columns with AgC, C and HZrO. Additionally, the irradiated target cutting machine with an innovative design was finally assembled. (author)« less

21 CFR 189.301 - Tin-coated lead foil capsules for wine bottles.

Code of Federal Regulations, 2014 CFR

2014-04-01

... 21 Food and Drugs 3 2014-04-01 2014-04-01 false Tin-coated lead foil capsules for wine bottles... Addition to Human Food Through Food-Contact Surfaces § 189.301 Tin-coated lead foil capsules for wine bottles. (a) Tin-coated lead foil is composed of a lead foil coated on one or both sides with a thin layer...

Producing Foils From Direct Cast Titanium Alloy Strip

NASA Technical Reports Server (NTRS)

Stuart, T. A.; Gaspar, T. A.; Sukonnik, I. M.; Semiatan, S. L.; Batawi, E.; Peters, J. A.; Fraser, H. L.

1996-01-01

This research was undertaken to demonstrate the feasibility of producing high-quality, thin-gage, titanium foil from direct cast titanium strip. Melt Overflow Rapid Solidification Technology (MORST) was used to cast several different titanium alloys into 500 microns thick strip, 10 cm wide and up to 3 m long. The strip was then either ground, hot pack rolled or cold rolled, as appropriate, into foil. Gamma titanium aluminide (TiAl) was cast and ground to approximately 100 microns thick foil and alpha-2 titanium aluminide (Ti3AI) was cast and hot pack rolled to approximately 70 microns thick foil. CP Ti, Ti6Al2Sn4Zr2Mo, and Ti22AI23Nb (Orthorhombic), were successfully cast and cold-rolled into good quality foil (less than 125 microns thick). The foils were generally fully dense with smooth surfaces, had fine, uniform microstructures, and demonstrated mechanical properties equivalent to conventionally produced titanium. By eliminating many manufacturing steps, this technology has the potential to produce thin gage, titanium foil with good engineering properties at significantly reduced cost relative to conventional ingot metallurgy processing.

Influence of sulfurization temperature on Cu2ZnSnS4 absorber layer on flexible titanium substrates for thin film solar cells

NASA Astrophysics Data System (ADS)

Gokcen Buldu, Dilara; Cantas, Ayten; Turkoglu, Fulya; Gulsah Akca, Fatime; Meric, Ece; Ozdemir, Mehtap; Tarhan, Enver; Ozyuzer, Lutfi; Aygun, Gulnur

2018-02-01

In this study, the effect of sulfurization temperature on the morphology, composition and structure of Cu2ZnSnS4 (CZTS) thin films grown on titanium (Ti) substrates has been investigated. Since Ti foils are flexible, they were preferred as a substrate. As a result of their flexibility, they allow large area manufacturing and roll-to-roll processes. To understand the effects of sulfurization temperature on the CZTS formation on Ti foils, CZTS films fabricated with various sulfurization temperatures were investigated with several analyses including x-ray diffraction (XRD), scanning electron microscopy (SEM), x-ray photoelectron spectroscopy and Raman scattering. XRD measurements showed a sharp and intense peak coming from the (112) planes of the kesterite type lattice structure (KS), which is strong evidence for good crystallinity. The surface morphologies of our thin films were investigated using SEM. Electron dispersive spectroscopy was also used for the compositional analysis of the thin films. According to these analysis, it is observed that Ti foils were suitable as substrates for the growth of CZTS thin films with desired properties and the sulfurization temperature plays a crucial role for producing good quality CZTS thin films on Ti foil substrates.

An application of computer image-processing and filmy replica technique to the copper electroplating method of stress analysis

NASA Astrophysics Data System (ADS)

Sugiura, M.; Seika, M.

1994-02-01

In this study, a new technique to measure the density of slip-bands automatically is developed, namely, a TV image of the slip-bands observed through a microscope is directly processed by an image-processing system using a personal computer and an accurate value of the density of slip-bands is measured quickly. In the case of measuring the local stresses in machine parts of large size with the copper plating foil, the direct observation of slip-bands through an optical microscope is difficult. In this study, to facilitate a technique close to the direct microscopic observation of slip-bands in the foil attached to a large-sized specimen, the replica method using a platic film of acetyl cellulose is applied to replicate the slip-bands in the attached foil.

Printed silver nanowire antennas with low signal loss at high-frequency radio

NASA Astrophysics Data System (ADS)

Komoda, Natsuki; Nogi, Masaya; Suganuma, Katsuaki; Kohno, Kazuo; Akiyama, Yutaka; Otsuka, Kanji

2012-05-01

Silver nanowires are printable and conductive, and are believed to be promising materials in the field of printed electronics. However, the resistivity of silver nanowire printed lines is higher than that of metallic particles or flakes even when sintered at high temperatures of 100-400 °C. Therefore, their applications have been limited to the replacement of transparent electrodes made from high-resistivity materials, such as doped metallic oxides, conductive polymers, carbon nanotubes, or graphenes. Here we report that using printed silver nanowire lines, signal losses obtained in the high-frequency radio were lower than those obtained using etched copper foil antennas, because their surfaces were much smoother than those of etched copper foil antennas. This was the case even though the resistivity of silver nanowire lines was 43-71 μΩ cm, which is much higher than that of etched copper foil (2 μΩ cm). When printed silver nanowire antennas were heated at 100 °C, they achieved signal losses that were much lower than those of silver paste antennas comprising microparticles, nanoparticles, and flakes. Furthermore, using a low temperature process, we succeeded in remotely controlling a commercialized radio-controlled car by transmitting a 2.45 GHz signal via a silver nanowire antenna printed on a polyethylene terephthalate film.Silver nanowires are printable and conductive, and are believed to be promising materials in the field of printed electronics. However, the resistivity of silver nanowire printed lines is higher than that of metallic particles or flakes even when sintered at high temperatures of 100-400 °C. Therefore, their applications have been limited to the replacement of transparent electrodes made from high-resistivity materials, such as doped metallic oxides, conductive polymers, carbon nanotubes, or graphenes. Here we report that using printed silver nanowire lines, signal losses obtained in the high-frequency radio were lower than those obtained using etched copper foil antennas, because their surfaces were much smoother than those of etched copper foil antennas. This was the case even though the resistivity of silver nanowire lines was 43-71 μΩ cm, which is much higher than that of etched copper foil (2 μΩ cm). When printed silver nanowire antennas were heated at 100 °C, they achieved signal losses that were much lower than those of silver paste antennas comprising microparticles, nanoparticles, and flakes. Furthermore, using a low temperature process, we succeeded in remotely controlling a commercialized radio-controlled car by transmitting a 2.45 GHz signal via a silver nanowire antenna printed on a polyethylene terephthalate film. Electronic supplementary information (ESI) available: Operation of R/C car with a silver nanowire monopole antenna. See DOI: 10.1039/c2nr30485f

Method for fabrication of ceramic dielectric films on copper foils

DOEpatents

Ma, Beihai; Narayanan, Manoj; Dorris, Stephen E.; Balachandran, Uthamalingam

2017-06-14

The present invention provides copper substrate coated with a lead-lanthanum-zirconium-titanium (PLZT) ceramic film, which is prepared by a method comprising applying a layer of a sol-gel composition onto a copper foil. The sol-gel composition comprises a precursor of a ceramic material suspended in 2-methoxyethanol. The layer of sol-gel is then dried at a temperature up to about 250.degree. C. The dried layer is then pyrolyzed at a temperature in the range of about 300 to about 450.degree. C. to form a ceramic film from the ceramic precursor. The ceramic film is then crystallized at a temperature in the range of about 600 to about 750.degree. C. The drying, pyrolyzing and crystallizing are performed under a flowing stream of an inert gas.

High-quality uniform dry transfer of graphene to polymers.

PubMed

Lock, Evgeniya H; Baraket, Mira; Laskoski, Matthew; Mulvaney, Shawn P; Lee, Woo K; Sheehan, Paul E; Hines, Daniel R; Robinson, Jeremy T; Tosado, Jacob; Fuhrer, Michael S; Hernández, Sandra C; Walton, Scott G

2012-01-11

In this paper we demonstrate high-quality, uniform dry transfer of graphene grown by chemical vapor deposition on copper foil to polystyrene. The dry transfer exploits an azide linker molecule to establish a covalent bond to graphene and to generate greater graphene-polymer adhesion compared to that of the graphene-metal foil. Thus, this transfer approach provides a novel alternative route for graphene transfer, which allows for the metal foils to be reused. © 2011 American Chemical Society

Accurate measurements of the 63Cu(d,p)64Cu and natCu(d,x)65Zn cross-sections in the 2.77-5.62 MeV energy range

NASA Astrophysics Data System (ADS)

Weissman, L.; Kreisel, A.; Hirsh, T.; Aviv, O.; Berkovits, D.; Girshevitz, O.; Eisen, Y.

2015-01-01

The cross sections of 63Cu(d,p)64Cu and natCu(d,x)65Zn were determined for deuteron beam energy range of 2.77-5.62 MeV at the SARAF Phase I variable energy LINAC. Thin copper foils were irradiated by a deuteron beam followed up by measurement of the produced activation at the Soreq NRC low-background γ-counting system. The results are consistent with data in the literature, but are of better accuracy. The data are important for assessment of the activation of components of Radio Frequency Quadrupole injectors and Medium Energy Beam Transport beam dumps in modern deuteron LINACs.

Rupture testing for the quality control of electrodeposited copper interconnections in high-speed, high-density circuits

NASA Technical Reports Server (NTRS)

Zakraysek, Louis

1987-01-01

Printed Wiring Multilayer Board (PWMLB) structures for high speed, high density circuits are prone to failure due to the microcracking of electrolytic copper interconnections. The failure can occur in the foil that makes up the inner layer traces or in the plated through holes (PTH) deposit that forms the layer to layer interconnections. It is shown that there are some distinctive differences in the quality of Type E copper and that these differences can be detected before its use in a PWMLB. It is suggested that the strength of some Type E copper can be very low when the material is hot and that it is the use of this poor quality material in a PWMLB that results in PTH and inner layer microcracking. Since the PWMLB failure in question are induced by a thermal stress, and since the poorer grades of Type E materials used in these structures are susceptible to premature failure under thermal stress, the use of elevated temperature rupture and creep rupture testing is proposed as a means for screening copper foil, or its PTH equivalent, in order to eliminate the problem of Type E copper microcracking in advanced PWMLBs.

Temperature measurements at material interfaces with thin-foil gauges

NASA Astrophysics Data System (ADS)

Morley, Mike; Chapman, David; Proud, William

2009-06-01

Measurements of shock heating are important in determining Equations of State that incorporate entropic effects. The use of thin-foil nickel gauges to measure shock heating in material was proposed by Rosenberg et al. in the 1980s. This research investigates the use of such commercial thin-foil gauges at interfaces between materials of different thermal and shock properties. The technique requires analysis of the resistance changes of the gauge which is a function of both temperature and stress. The response of manganin gauges to shock loading is well understood, and was used to calibrate for the piezoresistive effect in nickel. Results are presented for a variety of well-characterised materials and the applicability of the proposed method discussed.

Temperature Measurements at Material Interfaces with Thin-Foil Gauges

NASA Astrophysics Data System (ADS)

Morley, Mike J.; Chapman, David J.; Proud, William G.

2009-12-01

Measurements of shock heating are important in determining Equations of State that incorporate entropic effects. The use of thin-foil nickel gauges to measure shock heating in material was proposed by Rosenberg et al. in the 1980s. This research investigates the use of such commercial thin-foil gauges at interfaces between materials of different thermal and shock properties. The technique requires analysis of the resistance changes of the gauge which is a function of both temperature and stress. The response of manganin gauges to shock loading is well understood, and was used to calibrate for the piezoresistive effect in nickel. Results are presented for a variety of well-characterised materials and the applicability of the proposed method discussed.

A new, simple and precise method for measuring cyclotron proton beam energies using the activity vs. depth profile of zinc-65 in a thick target of stacked copper foils.

PubMed

Asad, A H; Chan, S; Cryer, D; Burrage, J W; Siddiqui, S A; Price, R I

2015-11-01

The proton beam energy of an isochronous 18MeV cyclotron was determined using a novel version of the stacked copper-foils technique. This simple method used stacked foils of natural copper forming 'thick' targets to produce Zn radioisotopes by the well-documented (p,x) monitor-reactions. Primary beam energy was calculated using the (65)Zn activity vs. depth profile in the target, with the results obtained using (62)Zn and (63)Zn (as comparators) in close agreement. Results from separate measurements using foil thicknesses of 100, 75, 50 or 25µm to form the stacks also concurred closely. Energy was determined by iterative least-squares comparison of the normalized measured activity profile in a target-stack with the equivalent calculated normalized profile, using 'energy' as the regression variable. The technique exploits the uniqueness of the shape of the activity vs. depth profile of the monitor isotope in the target stack for a specified incident energy. The energy using (65)Zn activity profiles and 50-μm foils alone was 18.03±0.02 [SD] MeV (95%CI=17.98-18.08), and 18.06±0.12MeV (95%CI=18.02-18.10; NS) when combining results from all isotopes and foil thicknesses. When the beam energy was re-measured using (65)Zn and 50-μm foils only, following a major upgrade of the ion sources and nonmagnetic beam controls the results were 18.11±0.05MeV (95%CI=18.00-18.23; NS compared with 'before'). Since measurement of only one Zn monitor isotope is required to determine the normalized activity profile this indirect yet precise technique does not require a direct beam-current measurement or a gamma-spectroscopy efficiency calibrated with standard sources, though a characteristic photopeak must be identified. It has some advantages over published methods using the ratio of cross sections of monitor reactions, including the ability to determine energies across a broader range and without need for customized beam degraders. Copyright © 2015 Elsevier Ltd. All rights reserved.

Effect of Substrate Compliance on Measuring Delamination Properties of Elastic Thin Foil

DOE Office of Scientific and Technical Information (OSTI.GOV)

Liu, C.

Through the analysis of a model problem, a thin elastic plate bonded to an elastic foundation, we address several issues related to the miniature bulge test for measuring the energy-release rate associated with the interfacial fracture of a bimaterial system, where one of the constituents is a thin foil. These issues include the effect of the substrate compliance on the interpretation of the energy release rate, interfacial strength, and the identification of the boundary of the deforming bulge or the location of the interfacial crack front. The analysis done also suggests a way for measuring the so-called foundation modulus, whichmore » characterizes the property of the substrate. An experimental example, a stainless steel thin foil bonded to an aluminum substrate through hot-isostatic-pressing (HIP), is used to illustrate and highlight some of the conclusions of the model analysis.« less

Effect of Substrate Compliance on Measuring Delamination Properties of Elastic Thin Foil

DOE PAGES

Liu, C.

2018-03-20

Through the analysis of a model problem, a thin elastic plate bonded to an elastic foundation, we address several issues related to the miniature bulge test for measuring the energy-release rate associated with the interfacial fracture of a bimaterial system, where one of the constituents is a thin foil. These issues include the effect of the substrate compliance on the interpretation of the energy release rate, interfacial strength, and the identification of the boundary of the deforming bulge or the location of the interfacial crack front. The analysis done also suggests a way for measuring the so-called foundation modulus, whichmore » characterizes the property of the substrate. An experimental example, a stainless steel thin foil bonded to an aluminum substrate through hot-isostatic-pressing (HIP), is used to illustrate and highlight some of the conclusions of the model analysis.« less

Design of a medium size x-ray mirror module based on thin glass foils

NASA Astrophysics Data System (ADS)

Basso, Stefano; Civitani, Marta; Pareschi, Giovanni

2016-07-01

The hot slumping glass technology for X-ray mirror is under development and in the last years the results have been improved. Nustar is the first X-ray telescope based on slumped glass foils and it benefit is the low cost compared to the direct polishing of glass. With the slumping technique it is possible to maintain the glass mass to low values with respect to the direct polishing, but in general the angular resolution is worst. A further technique based on glass is the cold shaping of foils. The improved capabilities of manufacturing thin glass foils, pushed by the industrial application for screens, open new possibilities for X-ray mirror. The increase in strength of thin tempered glasses, the reduction of thickness errors and the good roughness of flat foils are potentially great advantages. In this paper a design of a mediumsize X-ray mirror module is analysed. It is based on integration of glass foils, stacked directly on a supporting structure that is part of the X-ray telescope using stiffening ribs as spacer between foils. The alignment of each stack is performed directly into the integration machine avoiding the necessity of the alignment of different stacked modules. A typical module (glass optic and metallic structure) provides an effective area of 10 cm2/kg at 1 keV (with a mass of about 50- 100 kg and a focal length of 10 m).

Study of the spatial resolution of low-material GEM tracking detectors

NASA Astrophysics Data System (ADS)

Kudryavtsev, V. N.; Maltsev, T. V.; Shekhtman, L. I.

2018-02-01

The spatial resolution of GEM based tracking detectors has been simulated and measured. The simulation includes the GEANT4 based transport of high energy electrons with careful accounting for atomic relaxation processes including emission of fluorescent photons and Auger electrons and custom post-processing, including accounting for diffusion, gas amplification fluctuations, the distribution of signals on readout electrodes, electronics noise and a particular algorithm of the final coordinate calculation (center of gravity). The simulation demonstrates that a minimum of the spatial resolution of about 10 μm can be achieved with strip pitches from 250 μm to 300 μm. For larger pitches the resolution is quickly degrading reaching 80-100 μm at a pitch of 500 μm. The spatial resolution of low-material triple-GEM detectors for the DEUTRON facility at the VEPP-3 storage ring is measured at the extracted beam facility of the VEPP-4M collider. The amount of material in these detectors is reduced by etching the copper of the GEMs electrodes and using a readout structure on a thin kapton foil rather than on a glass fibre plate. The exact amount of material in one DEUTRON detector is measured by studying multiple scattering of 100 MeV electrons in it. The result of these measurements is X/X0 = 2.4×10-3 corresponding to a thickness of the copper layers of the GEM foils of 3 μm. The spatial resolution of one DEUTRON detector is measured with 500 MeV electrons and the measured value is equal to 35 ± 1 μm for orthogonal tracks.

Collodion-reinforcement and plasma-cleaning of target foils

NASA Astrophysics Data System (ADS)

Stoner, John O.

2002-03-01

The preparation of evaporated target foils can often be facilitated by use of collodion coatings either on the substrate sides or on the exterior surfaces of the foils. Later, such coatings must usually be removed. Cleaning of a foil is necessary if thin layers of adhesives have crept onto the foil. Removal and/or cleaning can often be done satisfactorily with an oxygen plasma. Apparatus and procedures used for this are described. Foils that were cleaned successfully, and some that were incompatible with the cleaning process are listed.

Laser-driven x-ray and neutron source development for industrial applications of plasma accelerators

NASA Astrophysics Data System (ADS)

Brenner, C. M.; Mirfayzi, S. R.; Rusby, D. R.; Armstrong, C.; Alejo, A.; Wilson, L. A.; Clarke, R.; Ahmed, H.; Butler, N. M. H.; Haddock, D.; Higginson, A.; McClymont, A.; Murphy, C.; Notley, M.; Oliver, P.; Allott, R.; Hernandez-Gomez, C.; Kar, S.; McKenna, P.; Neely, D.

2016-01-01

Pulsed beams of energetic x-rays and neutrons from intense laser interactions with solid foils are promising for applications where bright, small emission area sources, capable of multi-modal delivery are ideal. Possible end users of laser-driven multi-modal sources are those requiring advanced non-destructive inspection techniques in industry sectors of high value commerce such as aerospace, nuclear and advanced manufacturing. We report on experimental work that demonstrates multi-modal operation of high power laser-solid interactions for neutron and x-ray beam generation. Measurements and Monte Carlo radiation transport simulations show that neutron yield is increased by a factor ~2 when a 1 mm copper foil is placed behind a 2 mm lithium foil, compared to using a 2 cm block of lithium only. We explore x-ray generation with a 10 picosecond drive pulse in order to tailor the spectral content for radiography with medium density alloy metals. The impact of using  >1 ps pulse duration on laser-accelerated electron beam generation and transport is discussed alongside the optimisation of subsequent bremsstrahlung emission in thin, high atomic number target foils. X-ray spectra are deconvolved from spectrometer measurements and simulation data generated using the GEANT4 Monte Carlo code. We also demonstrate the unique capability of laser-driven x-rays in being able to deliver single pulse high spatial resolution projection imaging of thick metallic objects. Active detector radiographic imaging of industrially relevant sample objects with a 10 ps drive pulse is presented for the first time, demonstrating that features of 200 μm size are resolved when projected at high magnification.

Euromir '95: first results from the Dustwatch-P detectors of the european space exposure facility

NASA Astrophysics Data System (ADS)

Shrine, N. R. G.; McDonnell, J. A. M.; Burchell, M. J.; Gardner, D. J.; Jolly, H. S.; Ratcliff, P. R.; Thomson, R.

A small, passive, retrievable dust detector/collector experiment (Dustwatch-P), based on thin foil and aerogel capture cells has been developed at the University of Kent by the Unit for Space Sciences & Astrophysics (USSA). It was mounted in the European Space Exposure Facility (ESEF) designed by the Institut d'Astrophysique Spatial (Orsay, France) and flown on the joint ESA/Russian Space Agency EuroMir '95 mission. The experiment sampled micrometeoroids and space debris in the immediate vicinity of a large space facility (Mir) and offers the opportunity for detailed particle characterisation by intact capture. Dustwatch-P was housed in 2 ESEF cassettes, each contained: 1849mm^2 of aluminium foil capture cells, 2.4mum and 5mum thick respectively, mounted above a pure copper plate; 8450mm^2 of 12mm thick silica aerogel (density of 0.1 g/cm^3 and pore size of approximately 0.07mum). 8650mm^2 of experiment-holder surfaces (highly polished 6061-T6 aluminium alloy) were also used for detection. The foils and experiment-holder surfaces readily give a flux measurement for comparison to previous data with chemical classification of any impactor residues. The aerogel was intended to capture, with minimal modification, incident hypervelocity particles. Dustwatch-P was exposed to the space environment when the ESEF cassettes were opened during Mir EVA's on the 20/21 October '95. The cassettes were hermetically sealed in space for return to Earth in February '96. We present the first results of post-flight analysis. A hypervelocity perforation has been found in each foil and a region of ejecta impacts indicating a large impact in the vicinity. This impact rate gives a higher flux than expected, possibly due to a debris cloud.

Correlation Between Microstructure and Optical Properties of Cu (In0.7, Ga0.3) Se2 Grown by Electrodeposition Technique

NASA Astrophysics Data System (ADS)

Chihi, Adel; Bessais, Brahim

2017-01-01

Polycrystalline thin films Cu (In0.7, Ga0.3) Se2 (CIGSe) were grown on copper foils at various cathodic potentials by using an electrodeposition technique. Scanning electron microscopy showed that the average diameter of CIGSe grains increase from 0.1 μm to 1 μm when the cathodic potential decreases. The structure and surface morphology were investigated by x-ray diffraction and atomic force microscopy (AFM) techniques. This structure study shows that the thin films were well crystallized in a chalcopyrite structure without unwanted secondary phases with a preferred orientation along (112) plane. Energy-dispersive x-ray analyses confirms the existence of CIGSe single phase on a copper substrate. AFM analysis indicated that the root mean square roughness decreases from 64.28 to 27.42 when the potential deposition increases from -0.95 V to -0.77 V. Using Raman scattering spectroscopy, the A1 optical phonon mode was observed in 173 cm-1 and two other weak peaks were detected at 214 cm-1 and 225 cm-1 associated with the B2 and E modes of the CIGSe phase. Through spectroscopy ellipsometry analysis, a three-layer optical model was exploited to derive the optical properties and layer thickness of the CIGSe film by least-squares fitting the measured variation in polarization light versus the obtained microstructure.

Process for producing molybdenum foil and collapsible tubing

NASA Technical Reports Server (NTRS)

Bretts, G. R.; Gavert, R. B.; Groschke, G. F.

1971-01-01

Manufacturing process produces molybdenum foil 0.002 cm thick and 305 m long, and forms foil into high-strength, thin-walled tubing which can be flattened for storage on a spool. Desirable metal properties include high thermal conductivity stiffness, yield and tensile stress, and low thermal expansion coeffecient.

X-ray opacity measurements in mid-Z dense plasmas with a new target design of indirect heating

NASA Astrophysics Data System (ADS)

Dozières, M.; Thais, F.; Bastiani-Ceccotti, S.; Blenski, T.; Fariaut, J.; Fölsner, W.; Gilleron, F.; Khaghani, D.; Pain, J.-C.; Reverdin, C.; Rosmej, F.; Silvert, V.; Soullié, G.; Villette, B.

2015-12-01

X-ray transmission spectra of copper, nickel and aluminum laser produced plasmas were measured at the LULI2000 laser facility with an improved target design of indirect heating. Measurements were performed in plasmas close to local thermodynamic equilibrium at temperatures around 25 eV and densities between 10-3g/cm3 and 10-2 g/cm3. This improved design provides several advantages, which are discussed in this paper. The sample is a thin foil of mid-Z material inserted between two gold cavities heated by two 300J, 2ω, nanosecond laser beams. A third laser beam irradiates a gold foil to create a spectrally continuous X-ray source (backlight) used to probe the sample. We investigate 2p-3d absorption structures in Ni and Cu plasmas as well as 1s-2p transitions in an additional Al plasma layer to infer the in-situ plasma temperature. Geometric and hydrodynamic calculations indicate that the improved geometry reduces spatial gradients during the transmission measurements. Experimental absorption spectra are in good agreement with calculations from the hybrid atomic physics code SCO-RCG.

Time-resolved K α spectroscopy measurements of hot-electron equilibration dynamics in thin-foil solid targets: collisional and collective effects

NASA Astrophysics Data System (ADS)

Nilson, P. M.; Solodov, A. A.; Davies, J. R.; Theobald, W.; Mileham, C.; Stoeckl, C.; Begishev, I. A.; Zuegel, J. D.; Froula, D. H.; Betti, R.; Meyerhofer, D. D.

2015-11-01

Time-resolved K α spectroscopy measurements from high-intensity laser interactions with thin-foil solid targets are reviewed. Thin Cu foils were irradiated with 1-10 J, 1 ps pulses at focused intensities from 1018 to 1019 W cm-2. The experimental data show K α -emission pulse widths from 3 to 6 ps, increasing with laser intensity. The time-resolved K α -emission data are compared to a hot-electron transport and K α -production model that includes collisional electron-energy coupling, resistive heating, and electromagnetic field effects. The experimental data show good agreement with the model when a reduced ponderomotive scaling is used to describe the initial mean hot-electron energy over the relevant intensity range.

FAST OPENING SWITCH

DOEpatents

Bender, M.; Bennett, F.K.; Kuckes, A.F.

1963-09-17

A fast-acting electric switch is described for rapidly opening a circuit carrying large amounts of electrical power. A thin, conducting foil bridges a gap in this circuit and means are provided for producing a magnetic field and eddy currents in the foil, whereby the foil is rapidly broken to open the circuit across the gap. Advantageously the foil has a hole forming two narrow portions in the foil and the means producing the magnetic field and eddy currents comprises an annular coil having its annulus coaxial with the hole in the foil and turns adjacent the narrow portions of the foil. An electrical current flows through the coil to produce the magnetic field and eddy currents in the foil. (AEC)

Developing NanoFoil-Heated Thin-Film Thermal Battery

DTIC Science & Technology

2013-09-01

buffer discs (in gray) sandwiching the NanoFoil disc (in yellow). Two Microtherm discs (in dark gray) bracketed the sandwich to prevent excessive heat...of the fuse strip with a Microtherm disc. Cathode Electrolyte Anode Microtherm Heat paper NanoFoil Buffer Agilent 34970A 606.5 Nichrome wire Maccor...gray) sandwiching the NanoFoil disc (in yellow). Two Microtherm discs (in dark gray) bracketed the sandwich to prevent excessive heat loss

Development of CIGS2 Thin Films on Ultralightweight Flexible Large Area Foil Sunstrates

NASA Technical Reports Server (NTRS)

Dhere, Neelkanth G.; Gade, Vivek S.; Kadam, Ankur A.; Jahagirdar, Anant H.; Kulkarni, Sachin S.; Bet, Sachin M.

2005-01-01

The development of thin film solar cells is aimed at reducing the costs for photovoltaic systems. Use of thin film technology and thin foil substrate such as 5-mil thick stainless steel foil or 1-mil thick Ti would result in considerable costs savings. Another important aspect is manufacturing cost. Current single crystal technology for space power can cost more than $ 300 per watt at the array level and weigh more than 1 kg/sq m equivalent to specific power of approx. 65 W/kg. Thin film material such as CuIn1-xGaxS2 (CIGS2), CuIn(1-x)Ga(x)Se(2-y)S(y) (CIGSS) or amorphous hydrogenated silicon (a-Si:H) may be able to reduce both the cost and mass per unit area by an order of magnitude. Manufacturing costs for solar arrays are an important consideration for total spacecraft budget. For a medium sized 5kW satellite for example, the array manufacturing cost alone may exceed $ 2 million. Moving to thin film technology could reduce this expense to less than $ 500K. Earlier publications have demonstrated the potential of achieving higher efficiencies from CIGSS thin film solar cells on 5-mil thick stainless steel foil as well as initial stages of facility augmentation for depositing thin film solar cells on larger (6 in x 4 in) substrates. This paper presents the developmental study of achieving stress free Mo coating; uniform coatings of Mo back contact and metallic precursors. The paper also presents the development of sol gel process, refurbishment of selenization/sulfurization furnace, chemical bath deposition (CBD) for n-type CdS and scrubber for detoxification of H2S and H2Se gases.

Interdigitated Eutectic Alloy Foil Anodes for Rechargeable Batteries

DOE PAGES

Kreder, III, Karl J.; Heligman, Brian T.; Manthiram, Arumugam

2017-09-19

An interdigitated eutectic alloy (IdEA) foil is presented as a framework for the development of alloy anodes with a capacity that is significantly higher than that of the traditional graphite/copper assembly. In conclusion, it is a simple, low-cost approach that can be applied to a broad range of alloy systems with various working ions such as Li, Na, or Mg.

Method for fabricating prescribed flaws in the interior of metals

DOEpatents

Hsu, David K.; Thompson, Donald O.

1989-03-07

The method for fabricating a metal body having a flaw of predetermined size and shape located therein comprises placing half of the metal powder required to make the metal body in the die of a press and pressing it to create a flat upper surface thereon. A piece of copper foil is cut to the size and shape of the desired interior crack and placed on the upper surface of the powder and centered in position. The remaining powder is then placed in the die to cover the copper foil. The powder is first cold pressed and removed from the press. The powder metal piece is then sintered in a furnace at a temperature above the melting point of the copper and below the melting point of the metal. It is then removed from the furnace, cooled to room temperature, and placed back in the die and pressed further. This procedure results in an interior flaw or crack. Modified forms of the method involve using a press-sinter-press-sinter cycle with the first sinter being below the melting point of the copper and the second sinter being above the melting point of the copper and below the melting point of the metal.

Eddy current probe with foil sensor mounted on flexible probe tip and method of use

DOEpatents

Viertl, John R. M.; Lee, Martin K.

2001-01-01

A pair of copper coils are embedded in the foil strip. A first coil of the pair generates an electromagnetic field that induces eddy currents on the surface, and the second coil carries a current influenced by the eddy currents on the surface. The currents in the second coil are analyzed to obtain information on the surface eddy currents. An eddy current probe has a metal housing having a tip that is covered by a flexible conductive foil strip. The foil strip is mounted on a deformable nose at the probe tip so that the strip and coils will conform to the surface to which they are applied.

Use of Kelvin probe force microscopy for identification of CVD grown graphene flakes on copper foil

NASA Astrophysics Data System (ADS)

Kumar, Rakesh; Mehta, B. R.; Kanjilal, D.

2017-05-01

Graphene flakes have been grown by chemical vapour deposition (CVD) method on Cu foils. The obtained graphene flakes have been characterized by optical microscopy, field emission scanning electron microscopy, Kelvin probe force microscopy (KPFM) and Raman spectroscopy. The graphene flakes grown on Cu foil comprise mainly single layer graphene and confirm that the nucleation for graphene growth starts very quickly. Moreover, KPFM has been found to be a valuable technique to differentiate between covered and uncovered portion of Cu foil by graphene flakes deposited for shorter duration. The results show that KPFM can be a very useful technique in understanding the mechanism of graphene growth.

Poly-silicon TFT AM-OLED on thin flexible metal substrates

NASA Astrophysics Data System (ADS)

Afentakis, Themis; Hatalis, Miltiadis K.; Voutsas, Apostolos T.; Hartzell, John W.

2003-05-01

Thin metal foils present an excellent alternative to polymers for the fabrication of large area, flexible displays. Their main advantage spurs from their ability to withstand higher temperatures during processing; microelectronic fabrication at elevated temperatures offers the ability to utilize a variety of crystallization processes for the active layer of devices and thermally grown gate dielectrics. This can lead to high performance (high mobility, low threshold voltage) low cost and highly reliable thin film transistors. In some cases, the conductive substrate can also be used to provide power to the active devices, thus reducing layout complexity. This paper discusses the first successful attempt to design and fabricate a variety of active matrix organic light emitting diode displays on thin, flexible stainless steel foils. Different pixel architectures, such as two- and four-transistor implementations, and addressing modes, such as voltage- or current-driven schemese are examined. This work clearly demonstrates the advantages associated with the fabrication of OLED displays on thin metal foils, which - through roll-to-roll processing - can potentially result in revolutionizing today's display processing, leading to a new generation of low cost, high performance versatile display systems.

Time-resolved K α spectroscopy measurements of hot-electron equilibration dynamics in thin-foil solid targets: Collisional and collective effects

DOE PAGES

Nilson, P. M.; Solodov, A. A.; Davies, J. R.; ...

2015-09-25

Time-resolved K α spectroscopy measurements from high-intensity laser interactions with thin-foil solid targets are reviewed. Thin Cu foils were irradiated with 1- to 10-J, 1-ps pulses at focused intensities from 10 18 to 10 19 W/cm 2. The experimental data show K α-emission pulse widths from 3 to 6 ps, increasing with laser intensity. The time-resolved K α-emission data are compared to a hot-electron transport and K α-production model that includes collisional electron-energy coupling, resistive heating, and electromagnetic field effects. The experimental data show good agreement with the model when a reduced ponderomotive scaling is used to describe the initialmore » mean hot-electron energy over the relevant intensity range.« less

Normalization of a collimated 14.7 MeV neutron source in a neutron spectrometry system for benchmark experiments

NASA Astrophysics Data System (ADS)

Ofek, R.; Tsechanski, A.; Shani, G.

1988-05-01

In the present study a method used to normalize a collimated 14.7 MeV neutron beam is introduced. It combined a measurement of the fast neutron scalar flux passing through the collimator, using a copper foil activation, with a neutron transport calculation of the foil activation per unit source neutron, carried out by the discrete-ordinates transport code DOT 4.2. The geometry of the collimated neutron beam is composed of a D-T neutron source positioned 30 cm in front of a 6 cm diameter collimator, through a 120 cm thick paraffin wall. The neutron flux emitted from the D-T source was counted by an NE-213 scintillator, simultaneously with the irradiation of the copper foil. Thus, the determination of the normalization factor of the D-T source is used for an absolute flux calibration of the NE-213 scintillator. The major contributions to the uncertainty in the determination of the normalization factor, and their origins, are discussed.

Simbol-X Mirror Module Thermal Shields: II-Small Angle X-Ray Scattering Measurements

NASA Astrophysics Data System (ADS)

Barbera, M.; Ayers, T.; Collura, A.; Nasillo, G.; Pareschi, G.; Tagliaferri, G.

2009-05-01

The formation flight configuration of the Simbol-X mission implies that the X-ray mirror module will be open to Space on both ends. In order to reduce the power required to maintain the thermal stability and, therefore, the high angular resolution of the shell optics, a thin foil thermal shield will cover the mirror module. Different options are presently being studied for the foil material of these shields. We report results of an experimental investigation conducted to verify that the scattering of X-rays, by interaction with the thin foil material of the thermal shield, will not significantly affect the performances of the telescope.

Multi-dimensional effects in radiation pressure acceleration of ions

DOE Office of Scientific and Technical Information (OSTI.GOV)

Tripathi, V. K., E-mail: tripathivipin@yahoo.co.in

A laser carries momentum. On reflection from an ultra-thin overdense plasma foil, it deposits recoil momentum on the foil, i.e. exerts radiation pressure on the foil electrons and pushes them to the rear. The space charge field thus created takes the ions along, accelerating the electron-ion double layer as a single unit. When the foil has surface ripple, of wavelength comparable to laser wavelength, the radiation pressure acts non-uniformly on the foil and the perturbation grows as Reyleigh-Taylor (RT) instability as the foil moves. The finite spot size of the laser causes foil to bend. These effects limit the quasi-monomore » energy acceleration of ions. Multi-ion foils, e.g., diamond like carbon foil embedded with protons offer the possibility of suppressing RT instability.« less

Printed silver nanowire antennas with low signal loss at high-frequency radio.

PubMed

Komoda, Natsuki; Nogi, Masaya; Suganuma, Katsuaki; Kohno, Kazuo; Akiyama, Yutaka; Otsuka, Kanji

2012-05-21

Silver nanowires are printable and conductive, and are believed to be promising materials in the field of printed electronics. However, the resistivity of silver nanowire printed lines is higher than that of metallic particles or flakes even when sintered at high temperatures of 100-400 °C. Therefore, their applications have been limited to the replacement of transparent electrodes made from high-resistivity materials, such as doped metallic oxides, conductive polymers, carbon nanotubes, or graphenes. Here we report that using printed silver nanowire lines, signal losses obtained in the high-frequency radio were lower than those obtained using etched copper foil antennas, because their surfaces were much smoother than those of etched copper foil antennas. This was the case even though the resistivity of silver nanowire lines was 43-71 μΩ cm, which is much higher than that of etched copper foil (2 μΩ cm). When printed silver nanowire antennas were heated at 100 °C, they achieved signal losses that were much lower than those of silver paste antennas comprising microparticles, nanoparticles, and flakes. Furthermore, using a low temperature process, we succeeded in remotely controlling a commercialized radio-controlled car by transmitting a 2.45 GHz signal via a silver nanowire antenna printed on a polyethylene terephthalate film.

Birefringence and dichroism of poly(vinyl-alcohol) foils containing phthalazinium ylids

NASA Astrophysics Data System (ADS)

Rogojanu, Alina; Dascalu, Carmen Felicia; Zelinschi, Beatrice Carmen; Caprosu, Maria; Dorohoi, Dana Ortansa

2011-10-01

Pure and colored with phthalazinium ylids poly(vinyl-alcohol) (PVA) foils were stretched under gentile heating. The birefringence of the thin foils was determined with a Babinet compensator standardized for yellow radiation of a Sodium lamp. The determined birefringence of the colored PVA foils is higher than that of the pure PVA foils. This fact indicates that the phthalazinium ylids facilitate the increase in the anisotropy of the stretched foils. The visible absorption electronic band of phthalazinium ylids was used to estimate the dichroic ratio and the degree of order of the ylid molecules in the stretched PVA foils. An increase in dichroism and birefringence with the degree of stretching has been evidenced for uncolored and colored PVA foils.

Investigation of ablation of thin foil aluminum ribbon array at 1.5 MA

DOE Office of Scientific and Technical Information (OSTI.GOV)

Ye, Fan, E-mail: yefan1931@126.com; Li, Zhenghong; Chen, Faxin

We present experimental studies of initiation and ablation of a thin foil aluminum ribbon array at the 1.5 MA current level. In contrast to the previous work, we employ ribbon arrays with different ribbon gap parameters to investigate how this affects plasma initiation and foil ablation. Gated narrowband ultraviolet imaging indicated that the current was disorderly distributed at early period of discharge. But later on, it became axially stable and azimuthally symmetrical even for load with a gap as small as 0.1 mm. Using magnetic field probes installed inside and outside the array, we also observed that precursor current at positionsmore » with a distance of less than 2.7 mm to the central axis for 4-mm-radius arrays decreased when ribbon gap became small. Results of 0.2 mm gap ribbon array showed an evidence that ribbons can be merged. These observations imply that thin foil ribbon arrays may have potential applications in z-pinch experiments on large scale pulsed power facilities.« less

Effects of laser power density and initial grain size in laser shock punching of pure copper foil

NASA Astrophysics Data System (ADS)

Zheng, Chao; Zhang, Xiu; Zhang, Yiliang; Ji, Zhong; Luan, Yiguo; Song, Libin

2018-06-01

The effects of laser power density and initial grain size on forming quality of holes in laser shock punching process were investigated in the present study. Three different initial grain sizes as well as three levels of laser power densities were provided, and then laser shock punching experiments of T2 copper foil were conducted. Based upon the experimental results, the characteristics of shape accuracy, fracture surface morphology and microstructures of punched holes were examined. It is revealed that the initial grain size has a noticeable effect on forming quality of holes punched by laser shock. The shape accuracy of punched holes degrades with the increase of grain size. As the laser power density is enhanced, the shape accuracy can be improved except for the case in which the ratio of foil thickness to initial grain size is approximately equal to 1. Compared with the fracture surface morphology in the quasistatic loading conditions, the fracture surface after laser shock can be divided into three zones including rollover, shearing and burr. The distribution of the above three zones strongly relates with the initial grain size. When the laser power density is enhanced, the shearing depth is not increased, but even diminishes in some cases. There is no obvious change of microstructures with the enhancement of laser power density. However, while the initial grain size is close to the foil thickness, single-crystal shear deformation may occur, suggesting that the ratio of foil thickness to initial grain size has an important impact on deformation behavior of metal foil in laser shock punching process.

Fuel cell with metal screen flow-field

DOEpatents

Wilson, M.S.; Zawodzinski, C.

1998-08-25

A polymer electrolyte membrane (PEM) fuel cell is provided with electrodes supplied with a reactant on each side of a catalyzed membrane assembly (CMA). The fuel cell includes a metal mesh defining a rectangular flow-field pattern having an inlet at a first corner and an outlet at a second corner located on a diagonal from the first corner, wherein all flow paths from the inlet to the outlet through the square flow field pattern are equivalent to uniformly distribute the reactant over the CMA. In a preferred form of metal mesh, a square weave screen forms the flow-field pattern. In a particular characterization of the present invention, a bipolar plate electrically connects adjacent fuel cells, where the bipolar plate includes a thin metal foil having an anode side and a cathode side; a first metal mesh on the anode side of the thin metal foil; and a second metal mesh on the cathode side of the thin metal foil. In another characterization of the present invention, a cooling plate assembly cools adjacent fuel cells, where the cooling plate assembly includes an anode electrode and a cathode electrode formed of thin conducting foils; and a metal mesh flow field there between for distributing cooling water flow over the electrodes to remove heat generated by the fuel cells. 11 figs.

Fuel cell with metal screen flow-field

DOEpatents

Wilson, Mahlon S.; Zawodzinski, Christine

2001-01-01

A polymer electrolyte membrane (PEM) fuel cell is provided with electrodes supplied with a reactant on each side of a catalyzed membrane assembly (CMA). The fuel cell includes a metal mesh defining a rectangular flow-field pattern having an inlet at a first corner and an outlet at a second corner located on a diagonal from the first corner, wherein all flow paths from the inlet to the outlet through the square flow field pattern are equivalent to uniformly distribute the reactant over the CMA. In a preferred form of metal mesh, a square weave screen forms the flow-field pattern. In a particular characterization of the present invention, a bipolar plate electrically connects adjacent fuel cells, where the bipolar plate includes a thin metal foil having an anode side and a cathode side; a first metal mesh on the anode side of the thin metal foil; and a second metal mesh on the cathode side of the thin metal foil. In another characterization of the present invention, a cooling plate assembly cools adjacent fuel cells, where the cooling plate assembly includes an anode electrode and a cathode electrode formed of thin conducting foils; and a metal mesh flow field therebetween for distributing cooling water flow over the electrodes to remove heat generated by the fuel cells.

Fuel cell with metal screen flow-field

DOEpatents

Wilson, Mahlon S.; Zawodzinski, Christine

1998-01-01

A polymer electrolyte membrane (PEM) fuel cell is provided with electrodes supplied with a reactant on each side of a catalyzed membrane assembly (CMA). The fuel cell includes a metal mesh defining a rectangular flow-field pattern having an inlet at a first corner and an outlet at a second corner located on a diagonal from the first corner, wherein all flow paths from the inlet to the outlet through the square flow field pattern are equivalent to uniformly distribute the reactant over the CMA. In a preferred form of metal mesh, a square weave screen forms the flow-field pattern. In a particular characterization of the present invention, a bipolar plate electrically connects adjacent fuel cells, where the bipolar plate includes a thin metal foil having an anode side and a cathode side; a first metal mesh on the anode side of the thin metal foil; and a second metal mesh on the cathode side of the thin metal foil. In another characterization of the present invention, a cooling plate assembly cools adjacent fuel cells, where the cooling plate assembly includes an anode electrode and a cathode electrode formed of thin conducting foils; and a metal mesh flow field therebetween for distributing cooling water flow over the electrodes to remove heat generated by the fuel cells.

Creative Copper Crests

ERIC Educational Resources Information Center

Knab, Thomas

2011-01-01

In this article, the author discusses how to create an art activity that would link the computer-created business cards of fourth-grade students with an upcoming school-wide medieval event. Creating family crests from copper foil would be a great connection, since they, like business cards, are an individual's way to identify themselves to others.…

Solid Lubricants for Oil-Free Turbomachinery

NASA Technical Reports Server (NTRS)

DellaCorte, Christopher

2005-01-01

Recent breakthroughs in gas foil bearing solid lubricants and computer based modeling has enabled the development of revolulionary Oil-Free turbomachinery systems. These innovative new and solid lubricants at low speeds (start-up and shut down). Foil bearings are hydrodynamic, self acting fluid film bearings made from thin, flexible sheet metal foils. These thin foils trap a hydrodynamic lubricating air film between their surfaces and moving shaft surface. For low temperature applications, like ainrafl air cycle machines (ACM's), polymer coatings provide important solid lubrication during start-up and shut down prior to the development of the lubricating fluid film. The successful development of Oil-Free gas turbine engines requires bearings which can operate at much higher temperatures (greater than 300 C). To address this extreme solid lubrication need, NASA has invented a new family of compostie solid lubricant coatings, NASA PS300.

Process for forming a nickel foil with controlled and predetermined permeability to hydrogen

DOEpatents

Engelhaupt, Darell E.

1981-09-22

The present invention provides a novel process for forming a nickel foil having a controlled and predetermined hydrogen permeability. This process includes the steps of passing a nickel plating bath through a suitable cation exchange resin to provide a purified nickel plating bath free of copper and gold cations, immersing a nickel anode and a suitable cathode in the purified nickel plating bath containing a selected concentration of an organic sulfonic acid such as a napthalene-trisulfonic acid, electrodepositing a nickel layer having the thickness of a foil onto the cathode, and separating the nickel layer from the cathode to provide a nickel foil. The anode is a readily-corrodible nickel anode. The present invention also provides a novel nickel foil having a greater hydrogen permeability than palladium at room temperature.

Characterization of laser-cut copper foil X-pinches

NASA Astrophysics Data System (ADS)

Collins, G. W.; Valenzuela, J. C.; Hansen, S. B.; Wei, M. S.; Reed, C. T.; Forsman, A. C.; Beg, F. N.

2016-10-01

Quantitative data analyses of laser-cut Cu foil X-pinch experiments on the 150 ns quarter-period, ˜250 kA GenASIS driver are presented. Three different foil designs are tested to determine the effects of initial structure on pinch outcome. Foil X-pinch data are also presented alongside the results from wire X-pinches with comparable mass. The X-ray flux and temporal profile of the emission from foil X-pinches differed significantly from that of wire X-pinches, with all emission from the foil X-pinches confined to a ˜3 ns period as opposed to the delayed, long-lasting electron beam emission common in wire X-pinches. Spectroscopic data show K-shell as well as significant L-shell emission from both foil and wire X-pinches. Fits to synthetic spectra using the SCRAM code suggest that pinching foil X's produced a ˜1 keV, ne ≥ 1023 cm-3 plasma. The spectral data combined with the improved reliability of the source timing, flux, and location indicate that foil X-pinches generate a reproducible, K-shell point-projection radiography source that can be easily modified and tailored to suit backlighting needs across a variety of applications.

Anomalous transmission of an ultrashort ionizing laser pulse through a thin foil.

PubMed

Ferrante, G; Zarcone, M; Uryupin, S A

2003-08-22

The formation of a highly anisotropic photoelectron velocity distribution as a result of the interaction of a powerful ultrashort laser pulse with a thin foil is found to yield a large skin-layer depth and an anomalous increase of the transmission coefficient. The physical reason for the effect is the influence of the incident wave magnetic field, through the Lorenz force, on the electron kinetics in the skin layer.

Dispersion of Projectile and Target Debris Upon Penetration of Thin Targets

NASA Astrophysics Data System (ADS)

Gwynn, D.; Bernhard, R. P.; See, T. H.; Horz, F.

1996-03-01

We continue to conduct penetration experiments of thin foils to support the development of cosmic-dust flight instruments that utilize thin films for the measurement of particle trajectories, or for the potential soft capture of hypervelocity impactors for subsequent compositional analysis upon retrieval to Earth. Each experiment is equipped with a witness plate, mounted to the rear of the target and fabricated from soft Aluminum-1100, ~30 x 30 cm in size and ranging from 2 to 5 mm thick; these witness plates essentially simulate the rear wall of a capture cell onto which the projectile material will plate out, including material that is being dislodged from the penetrated foil itself. Using compositionally contrasting projectile and foil materials in the laboratory, such as soda-lime glass impactors and aluminum targets, one produces two distinct populations of craters on the witness plates.

Radiation effects measurements on spacecraft electrostatic discharge tapes, thermal blankets and thermooptical coatings

NASA Technical Reports Server (NTRS)

Bouquet, F. L.; Hribar, V. F.; Metzler, E. C.; Russell, D. A.

1984-01-01

Selective results are presented of laboratory radiation tests of metallic foil tapes, thermal blankets, and thermooptical coatings undertaken as part of the development and qualification of materials for the Galileo spacecraft. Of the two metallic foil tapes used for electrical continuity, the adhesive used on the aluminum embossed foil was superior to the copper embossed foil when exposed to simulated Jovian electrons. Proton-irradiation tests performed on a number of thermal blanket samples showed that black polyester on Kapton proved to be a lower weight loss (i.e., outgassing) material than Fluorglas. In addition, preliminary results concerning the response of thermooptical coatings to simulated Jovian electrons show that the ITO-coated polyester over a Kapton surface gave the lowest absorptance.

DYNAMIC PROPERTIES OF SHOCK LOADED THIN URANIUM FOILS

DOE Office of Scientific and Technical Information (OSTI.GOV)

Robbins, D. L.; Kelly, A. M.; Alexander, D. J.

A series of spall experiments has been completed with thin depleted uranium targets, nominally 0.1 mm thick. The first set of uranium spall targets was cut and ground to final thickness from electro-refined, high-purity, cast uranium. The second set was rolled to final thickness from low purity uranium. The impactors for these experiments were laser-launched 0.05-mm thick copper flyers, 3 mm in diameter. Laser energies were varied to yield a range of flyer impact velocities. This resulted in varying degrees of damage to the uranium spall targets, from deformation to complete spall or separation at the higher velocities. Dynamic measurementsmore » of the uranium target free surface velocities were obtained with dual velocity interferometers. Uranium targets were recovered and sectioned after testing. Free surface velocity profiles were similar for the two types of uranium, but spall strengths (estimated from the magnitude of the pull-back signal) are higher for the high-purity cast uranium. Velocity profiles and microstructural evidence of spall from the sectioned uranium targets are presented.« less

Status of flexible CIS research at ISET

NASA Technical Reports Server (NTRS)

Basol, B. M.; Kapur, V. K.; Minnick, A.; Halani, A.; Leidholm, C. R.

1994-01-01

Polycrystalline thin film solar cells fabricated on light-weight, flexible substrates are very attractive for space applications. In this work CulnSe2 (CIS) based thin film devices were processed on metallic foil substrates using the selenization technique. CIS deposition method involved reaction of electron-bean evaporated Cu-In precursor layers with a selenizing atmosphere at around 400 C. Several metallic foils such as Mo, Ti, Al, Ni, and Cu were evaluated as possible substrates for these devices. Solar cells with AM1.5 efficiencies of 9.0-9.34 percent and good mechanical integrity were demonstrated on Mo and Ti foils. Monolithic integration of these devices was also demonstrated up to 4 in x 4 in size.

Metal-assisted exfoliation (MAE): green process for transferring graphene to flexible substrates and templating of sub-nanometer plasmonic gaps (Presentation Recording)

NASA Astrophysics Data System (ADS)

Zaretski, Aliaksandr V.; Marin, Brandon C.; Moetazedi, Herad; Dill, Tyler J.; Jibril, Liban; Kong, Casey; Tao, Andrea R.; Lipomi, Darren J.

2015-09-01

This paper describes a new technique, termed "metal-assisted exfoliation," for the scalable transfer of graphene from catalytic copper foils to flexible polymeric supports. The process is amenable to roll-to-roll manufacturing, and the copper substrate can be recycled. We then demonstrate the use of single-layer graphene as a template for the formation of sub-nanometer plasmonic gaps using a scalable fabrication process called "nanoskiving." These gaps are formed between parallel gold nanowires in a process that first produces three-layer thin films with the architecture gold/single-layer graphene/gold, and then sections the composite films with an ultramicrotome. The structures produced can be treated as two gold nanowires separated along their entire lengths by an atomically thin graphene nanoribbon. Oxygen plasma etches the sandwiched graphene to a finite depth; this action produces a sub-nanometer gap near the top surface of the junction between the wires that is capable of supporting highly confined optical fields. The confinement of light is confirmed by surface-enhanced Raman spectroscopy measurements, which indicate that the enhancement of the electric field arises from the junction between the gold nanowires. These experiments demonstrate nanoskiving as a unique and easy-to-implement fabrication technique that is capable of forming sub-nanometer plasmonic gaps between parallel metallic nanostructures over long, macroscopic distances. These structures could be valuable for fundamental investigations as well as applications in plasmonics and molecular electronics.

Atomic layer deposition of copper thin film and feasibility of deposition on inner walls of waveguides

NASA Astrophysics Data System (ADS)

Yuqing, XIONG; Hengjiao, GAO; Ni, REN; Zhongwei, LIU

2018-03-01

Copper thin films were deposited by plasma-enhanced atomic layer deposition at low temperature, using copper(I)-N,N‧-di-sec-butylacetamidinate as a precursor and hydrogen as a reductive gas. The influence of temperature, plasma power, mode of plasma, and pulse time, on the deposition rate of copper thin film, the purity of the film and the step coverage were studied. The feasibility of copper film deposition on the inner wall of a carbon fibre reinforced plastic waveguide with high aspect ratio was also studied. The morphology and composition of the thin film were studied by atomic force microscopy and x-ray photoelectron spectroscopy, respectively. The square resistance of the thin film was also tested by a four-probe technique. On the basis of on-line diagnosis, a growth mechanism of copper thin film was put forward, and it was considered that surface functional group played an important role in the process of nucleation and in determining the properties of thin films. A high density of plasma and high free-radical content were helpful for the deposition of copper thin films.

Bi-Directional Ion Emission from Massive Gold Cluster Impacts on Nanometric Carbon Foils.

PubMed

Debord, J Daniel; Della-Negra, Serge; Fernandez-Lima, Francisco A; Verkhoturov, Stanislav V; Schweikert, Emile A

2012-04-12

Carbon cluster emission from thin carbon foils (5-40 nm) impacted by individual Au(n) (+q) cluster projectiles (95-125 qkeV, n/q = 3-200) reveals features regarding the energy deposition, projectile range, and projectile fate in matter as a function of the projectile characteristics. For the first time, the secondary ion emission from thin foils has been monitored simultaneously in both forward and backward emission directions. The projectile range and depth of emission were examined as a function of projectile size, energy, and target thickness. A key finding is that the massive cluster impact develops very differently from that of a small polyatomic projectile. The range of the 125 qkeV Au(100q) (+q) (q ≈ 4) projectile is estimated to be 20 nm (well beyond the range of an equal velocity Au(+)) and projectile disintegration occurs at the exit of even a 5 nm thick foil.

Bi-Directional Ion Emission from Massive Gold Cluster Impacts on Nanometric Carbon Foils

PubMed Central

DeBord, J. Daniel; Della-Negra, Serge; Fernandez-Lima, Francisco A.; Verkhoturov, Stanislav V.; Schweikert, Emile A.

2012-01-01

Carbon cluster emission from thin carbon foils (5–40 nm) impacted by individual Aun+q cluster projectiles (95–125 qkeV, n/q = 3–200) reveals features regarding the energy deposition, projectile range, and projectile fate in matter as a function of the projectile characteristics. For the first time, the secondary ion emission from thin foils has been monitored simultaneously in both forward and backward emission directions. The projectile range and depth of emission were examined as a function of projectile size, energy, and target thickness. A key finding is that the massive cluster impact develops very differently from that of a small polyatomic projectile. The range of the 125 qkeV Au100q+q (q ≈ 4) projectile is estimated to be 20 nm (well beyond the range of an equal velocity Au+) and projectile disintegration occurs at the exit of even a 5 nm thick foil. PMID:22888385

Porus electrode comprising a bonded stack of pieces of corrugated metal foil

NASA Technical Reports Server (NTRS)

Mccallum, J. (Inventor)

1973-01-01

An electrode suitable for use in an electrochemical cell is described. The electrode is composed of a porous conductive support with a bonded stack of pieces of thin corrugated nickel foil where the corrugations are oriented approximately perpendicular to the sides of the electrode and form an array of passages through the electrode. Active material such as cadmium hydroxide or nickel hydroxide is uniformly distributed within the passages. The support may comprise also a piece of thin flat nickel foil between adjacent pieces of the corrugated foil, forming a barrier between the passages formed on each side of it. Typically the corrugations in the odd corrugated layers are oriented at a small angle from the perpendicular in one direction and the corrugations in the even corrugated layers are oriented at a small angle from the perpendicular in the opposite direction.

Method for fabricating uranium foils and uranium alloy foils

DOEpatents

Hofman, Gerard L [Downers Grove, IL; Meyer, Mitchell K [Idaho Falls, ID; Knighton, Gaven C [Moore, ID; Clark, Curtis R [Idaho Falls, ID

2006-09-05

A method of producing thin foils of uranium or an alloy. The uranium or alloy is cast as a plate or sheet having a thickness less than about 5 mm and thereafter cold rolled in one or more passes at substantially ambient temperatures until the uranium or alloy thereof is in the shape of a foil having a thickness less than about 1.0 mm. The uranium alloy includes one or more of Zr, Nb, Mo, Cr, Fe, Si, Ni, Cu or Al.

Infrared particle detection for battery electrode foils

NASA Astrophysics Data System (ADS)

Just, P.; Ebert, L.; Echelmeyer, T.; Roscher, M. A.

2013-11-01

Failures of electrochemical cells caused by internal shorts still are an important issue to be faced by the cell manufacturers and their customers. A major cause for internal shorts are contaminated electrode foils. These contaminations have to be detected securely via a non-destructive inspection technique integrated into the electrode manufacturing process. While optical detection already is state of the art, infrared detection of particles finds a new field of application in the battery electrode manufacturing process. This work presents two approaches focusing on electrode inspection by electromagnetic radiation (visible and infrared). Copper foils with a carbon based coating were intentionally contaminated by slivers of aluminum and copper as well as by abraded coating particles. Optical excitation by a flash and a luminescent lamp was applied at different angles in order to detect the reflected visible radiation. A laser impulse was used to heat up the specimen for infrared inspection. Both approaches resulted in setups providing a high contrast between contaminations and the coated electrode foil. It is shown that infrared detection offers a higher security thanks to its reliance on absorbance and emissivity instead of reflectivity as it is used for optical detection. Infrared Detection offers a potential since it is hardly influenced by the particle's shape and orientation and the electrode's waviness.

Braze system and method for reducing strain in a braze joint

DOEpatents

Cadden, Charles H.; Goods, Steven H.; Prantil, Vincent C.

2004-05-11

A system for joining a pair of structural members having widely differing coefficients of thermal expansion is disclosed. A mechanically "thick" foil is made by dispersing a refractory metal powder, such as molybdenum, niobium, tantalum, or tungsten into a quantity of a liquid, high expansion metal such as copper, silver, or gold, casting an ingot of the mixture, and then cutting sections of the ingot about 1 mm thick to provide the foil member. These foil members are shaped, and assembled between surfaces of structural members for joining, together with a layer of a braze alloy on either side of the foil member capable of wetting both the surfaces of the structural members and the foil. The assembled body is then heated to melt the braze alloy and join the assembled structure. The foil member subsequently absorbs the mechanical strain generated by the differential contraction of the cooling members that results from the difference in the coefficients of thermal expansion of the members.

NMR of samples containing metal foils.

PubMed

Xiong, J; Lock, H; Tao, T; Keeler, C; Maciel, G E

1999-07-01

By using spool configurations of a sample containing aluminum foil, in which the axis of the spool is collinear with the RF coil axis, one can obtain high-quality 13C NMR spectra of static samples of organic material attached to the aluminum foil. By combining such a spool configuration (or, alternatively, analogous samples containing equivalent amounts of fine aluminum powder) with the magic-angle hopping (MAH) technique, one can achieve a high degree of isotropic averaging of the 13C spectrum. This opens to NMR techniques the study of a variety of samples containing macroscopic pieces of metal foils, e.g., thin films deposited on metal foils and electrochemical systems with species adsorbed on metal-foil electrodes.

Note: Radial-thrust combo metal mesh foil bearing for microturbomachinery

NASA Astrophysics Data System (ADS)

Park, Cheol Hoon; Choi, Sang Kyu; Hong, Doo Euy; Yoon, Tae Gwang; Lee, Sung Hwi

2013-10-01

This Note proposes a novel radial-thrust combo metal mesh foil bearing (MMFB). Although MMFBs have advantages such as higher stiffness and damping over conventional air foil bearings, studies related to MMFBs have been limited to radial MMFBs. The novel combo MMFB is composed of a radial top foil, thrust top foils, and a ring-shaped metal mesh damper—fabricated by compressing a copper wire mesh—with metal mesh thrust pads for the thrust bearing at both side faces. In this study, the combo MMFB was fabricated in half-split type to support the rotor for a micro gas turbine generator. The manufacture and assembly process for the half-split-type combo MMFB is presented. In addition, to verify the proposed combo MMFB, motoring test results up to 250 000 rpm and axial displacements as a function of rotational speed are presented.

Note: Radial-thrust combo metal mesh foil bearing for microturbomachinery.

PubMed

Park, Cheol Hoon; Choi, Sang Kyu; Hong, Doo Euy; Yoon, Tae Gwang; Lee, Sung Hwi

2013-10-01

This Note proposes a novel radial-thrust combo metal mesh foil bearing (MMFB). Although MMFBs have advantages such as higher stiffness and damping over conventional air foil bearings, studies related to MMFBs have been limited to radial MMFBs. The novel combo MMFB is composed of a radial top foil, thrust top foils, and a ring-shaped metal mesh damper--fabricated by compressing a copper wire mesh--with metal mesh thrust pads for the thrust bearing at both side faces. In this study, the combo MMFB was fabricated in half-split type to support the rotor for a micro gas turbine generator. The manufacture and assembly process for the half-split-type combo MMFB is presented. In addition, to verify the proposed combo MMFB, motoring test results up to 250,000 rpm and axial displacements as a function of rotational speed are presented.

X-ray optics made from thin plastic foils

NASA Astrophysics Data System (ADS)

Schnopper, H. W.; Barbera, M.; Ingram, R.; Silver, E.; Romaine, S.; Bandler, S.; Murray, S.; Christensen, F. E.; Hussain, A.; Collura, A.

2000-10-01

New design concepts and materials can be used to produce lightweight, thin foil approximations, to Wolter I and other X-ray optics. Structures are designed around a central hub and spacers that connect two (or three) spoked wheels. Figure defining, thin pins span the distance between the wheels. Thin, metal coated or multilayered, plastic foils can be formed into full cones, cylinders or spirals for X-ray telescopes or lenses. High resolution X-ray scattering data were obtained for single foils at Cu K (8 KeV). Multi-energy (0.28 - 8 KeV) data were obtained with a multichannel plate imager in a 17 m beam line with a point-to-point focusing, cylindrical X-ray lens with 14 shells. The largest shell has a diameter of 175 mm and a length of 100 mm. Typical images have a FWHM of 20 arcsec. The results indicate that a 60 cm diameter, 4.65 m focal length X-ray telescope can have an HPD of considerably less than 2 arcmin. This research is supported, in part by NASA Grant NAG5-5268, ONR Grant N00014-95-1-1248, and by institutional funding from the Smithsonian Astrophysical Observatory. The SAO multilayer facility receives support from NASA Grant NAG5-5095. This work made use of the MRSEC Shared Experimental Facilities at MIT supported by NSF Grant DMR94-00334.

Microstructure Evolution and Composition Control During the Processing of Thin-Gage Metallic Foil

NASA Astrophysics Data System (ADS)

Semiatin, S. L.; Gross, M. E.; Matson, D. W.; Bennett, W. D.; Bonham, C. C.; Ustinov, A. I.; Ballard, D. L.

2012-12-01

The manufacture of thin-gage superalloy and gamma-titanium-aluminide foil products via near-conventional thermomechanical processing and two different vapor-deposition methods was investigated. Thermomechanical processing was based on hot-pack rolling of plate and sheet. Foils of the superalloy LSHR and the near-gamma titanium aluminide Ti-45.5Al-2Cr-2Nb made by this approach exhibited excellent gage control and fine two-phase microstructures. The vapor-phase techniques used magnetron sputtering (MS) of a target of the desired product composition or electron-beam physical vapor deposition (EBPVD) of separate targets of the specific alloying elements. Thin deposits of LSHR and Ti-48Al-2Cr-2Nb made by MS showed uniform thickness/composition and an ultrafine microstructure. However, systematic deviations from the specific target composition were found. During subsequent heat treatment, the microstructure of the MS samples showed various degrees of grain growth and coarsening. Foils of Ti-43Al and Ti-51Al-1V fabricated by EBPVD were fully dense. The microstructures developed during EBPVD were interpreted in terms of measured phase equilibria and the dependence of evaporant flux on temperature.

A concept for Z-dependent microbunching measurements with coherent X-ray transition radiation in a sase FEL

DOE Office of Scientific and Technical Information (OSTI.GOV)

Lumpkin, A.H.; Fawley, W.M.; Rule, D.W.

We present an adaptation of the measurements performed in the visible-to-VUV regime of the z-dependent microbunching in a self-amplified spontaneous emission (SASE) free-electron laser (FEL). In these experiments a thin metal foil was used to block the more intense SASE radiation and to generate coherent optical transition radiation (COTR) as one source in a two-foil interferometer. However, for the proposed x-ray SASE FELs, the intense SASE emission is either too strongly transmitted at 1.5 Angstrom or the needed foil thickness for blocking scatters the electron beam too much. Since x-ray transition radiation (XTR) is emitted in an annulus with openingmore » angle 1/g = 36 mrad for 14.09-GeV electrons, we propose using a thin foil or foil stack to generate the XTR and coherent XTR (CXTR) and an annular crystal to wavelength sort the radiation. The combined selectivity in angle and wavelength will favor the CXTR over SASE by about eight orders of magnitude. Time-dependent GINGER simulations support the z-dependent gain evaluation plan.« less

Mechanical and electrical properties of laminates for high performance printed wiring boards

NASA Astrophysics Data System (ADS)

Guiles, Chester L.

The physical and electrical properties of laminate boards intended for high-performance applications are reviewed with particular reference to the coefficient of thermal expansion, dielectric constant, and characteristic impedance. It is shown, in particular, that the electrical properties can be tailored to some extent by using various conbinations of basic board materials, such as copper foil, fiberglass fabric, glass fabric, epoxy resin, polyimide resin, aluminum sheet, Kevlar and quartz fabrics, copper-invar-copper, and alumina-ceramic.

Calibrating an optical scanner for quality assurance of large area radiation detectors

NASA Astrophysics Data System (ADS)

Karadzhinova, A.; Hildén, T.; Berdova, M.; Lauhakangas, R.; Heino, J.; Tuominen, E.; Franssila, S.; Hæggström, E.; Kassamakov, I.

2014-11-01

A gas electron multiplier (GEM) is a particle detector used in high-energy physics. Its main component is a thin copper-polymer-copper sandwich that carries Ø =70  ±  5 µm holes. Quality assurance (QA) is needed to guarantee both long operating life and reading fidelity of the GEM. Absence of layer defects and conformity of the holes to specifications is important. Both hole size and shape influence the detector’s gas multiplication factor and hence affect the collected data. For the scanner the required lateral measurement tolerance is ± 5 µm. We calibrated a high aspect ratio optical scanning system (OSS) to allow ensuring the quality of large GEM foils. For the calibration we microfabricated transfer standards, which were imaged with the OSS and which were compared to corresponding scanning electron microscopy (SEM) images. The calibration fulfilled the ISO/IEC 17025 and UKAS M3003 requirements: the calibration factor was 1.01  ±  0.01, determined at 95% confidence level across a 950  ×  950 mm2 area. The proposed large-scale scanning technique can potentially be valuable in other microfabricated products too.

Foil focusing of relativistic electron beams

DOE Office of Scientific and Technical Information (OSTI.GOV)

Ekdahl, Jr., Carl August

2017-10-26

When an intense relativistic electron beams (IREB) passes through a grounded metal foil, the transverse electric field due to the beam space charge is locally shorted out, and the beam is focused by the magnetic field of its current. The effect can be treated as focusing by a thin lens with first order aberration. Expressions for the focal length and aberration coefficient of the equivalent thin lens are developed in this note. These are then applied to practical examples representative of IREB research at Los Alamos National Laboratory.

Effect of mechanical strain on mobility of polycrystalline silicon thin-film transistors fabricated on stainless steel foil

NASA Astrophysics Data System (ADS)

Kuo, Po-Chin; Jamshidi-Roudbari, Abbas; Hatalis, Miltiadis

2007-12-01

The effect of uniaxial tensile strain parallel to the channel on mobility of polycrystalline silicon thin-film transistors (TFTs) on stainless steel foil has been investigated. The electron mobility increases by 20% while the hole mobility decreases by 6% as the strain increases to 0.5%, and both followed by saturation as the strain increases further. The off current decreases for both types of TFTs under strain. All TFTs remained functional at the applied strain of 1.13%.

Lead zirconate titanate (PZT)-based thin film capacitors for embedded passive applications

NASA Astrophysics Data System (ADS)

Kim, Taeyun

Investigations on the key processing parameters and properties relationship for lead zirconate titanate (PZT, 52/48) based thin film capacitors for embedded passive capacitor application were performed using electroless Ni coated Cu foils as substrates. Undoped and Ca-doped PZT (52/48) thin film capacitors were prepared on electroless Ni coated Cu foil by chemical solution deposition. For PZT (52/48) thin film capacitors on electroless Ni coated Cu foil, voltage independent (zero tunability) capacitance behavior was observed. Dielectric constant reduced to more than half of the identical capacitor processed on Pt/SiO2/Si. Dielectric properties of the capacitors were mostly dependent on the crystallization temperature. Capacitance densities of almost 350 nF/cm2 and 0.02˜0.03 of loss tangent were routinely measured for capacitors crystallized at 575˜600°C. Leakage current showed dependence on film thickness and crystallization temperature. From a two-capacitor model, the existence of a low permittivity interface layer (permittivity ˜30) was suggested. For Ca-doped PZT (52/48) thin film capacitors prepared on Pt, typical ferroelectric and dielectric properties were measured up to 5 mol% Ca doping. When Ca-doped PZT (52/48) thin film capacitors were prepared on electroless Ni coated Cu foil, phase stability was influenced by Ca doping and phosphorous content. Dielectric properties showed dependence on the crystallization temperature and phosphorous content. Capacitance density of ˜400 nF/cm2 was achieved, which is an improvement by more than 30% compared to undoped composition. Ca doping also reduced the temperature coefficient of capacitance (TCC) less than 10%, all of them were consistent in satisfying the requirements of embedded passive capacitor. Leakage current density was not affected significantly by doping. To tailor the dielectric and reliability properties, ZrO2 was selected as buffer layer between PZT and electroless Ni. Only RF magnetron sputtering process could yield stable ZrO2 layers on electroless Ni coated Cu foil. Other processes resulted in secondary phase formation, which supports the reaction between PZT capacitor and electroless Ni might be dominated by phosphorous component. (Abstract shortened by UMI.)

Multiple-layer printed-wiring trace connector

NASA Technical Reports Server (NTRS)

Pizzeck, D. E.

1977-01-01

Nickel-plated spring-steel foil connector is hollow pin, with lengthwise slit, that is inserted into improperly plated-through holes. Edges of connector make positive contact with copper pads within hole.

Effect of interfacial interactions on the thermal conductivity and interfacial thermal conductance in tungsten–graphene layered structure

DOE Office of Scientific and Technical Information (OSTI.GOV)

Jagannadham, K., E-mail: jag-kasichainula@ncsu.edu

2014-09-01

Graphene film was deposited by microwave plasma assisted deposition on polished oxygen free high conductivity copper foils. Tungsten–graphene layered film was formed by deposition of tungsten film by magnetron sputtering on the graphene covered copper foils. Tungsten film was also deposited directly on copper foil without graphene as the intermediate film. The tungsten–graphene–copper samples were heated at different temperatures up to 900 °C in argon atmosphere to form an interfacial tungsten carbide film. Tungsten film deposited on thicker graphene platelets dispersed on silicon wafer was also heated at 900 °C to identify the formation of tungsten carbide film by reaction of tungstenmore » with graphene platelets. The films were characterized by scanning electron microscopy, Raman spectroscopy, and x-ray diffraction. It was found that tungsten carbide film formed at the interface upon heating only above 650 °C. Transient thermoreflectance signal from the tungsten film surface on the samples was collected and modeled using one-dimensional heat equation. The experimental and modeled results showed that the presence of graphene at the interface reduced the cross-plane effective thermal conductivity and the interfacial thermal conductance of the layer structure. Heating at 650 and 900 °C in argon further reduced the cross-plane thermal conductivity and interface thermal conductance as a result of formation nanocrystalline tungsten carbide at the interface leading to separation and formation of voids. The present results emphasize that interfacial interactions between graphene and carbide forming bcc and hcp elements will reduce the cross-plane effective thermal conductivity in composites.« less

Simulation of the energy spectra of original versus recombined H{sub 2}{sup +} molecular ions transmitted through thin foils

DOE Office of Scientific and Technical Information (OSTI.GOV)

Barriga-Carrasco, Manuel D.; Garcia-Molina, Rafael

2004-09-01

This work presents the results of computer simulations for the energy spectra of original versus recombined H{sub 2}{sup +} molecular ions transmitted through thin amorphous carbon foils, for a broad range of incident energies. A detailed description of the projectile motion through the target has been done, including nuclear scattering and Coulomb repulsion as well as electronic self-retarding and wake forces; the two latter are calculated in the dielectric formalism framework. Differences in the energy spectra of recombined and original transmitted H{sub 2}{sup +} molecular ions clearly appear in the simulations, in agreement with the available experimental data. Our simulationmore » code also differentiates the contributions due to original and to recombined H{sub 2}{sup +} molecular ions when the energy spectra contain both contributions, a feature that could be used for experimental purposes in estimating the ratio between the number of original and recombined H{sub 2}{sup +} molecular ions transmitted through thin foils.« less

Direct hot slumping and accurate integration process to manufacture prototypal x-ray optical units made of glass

NASA Astrophysics Data System (ADS)

Civitani, M.; Ghigo, M.; Basso, S.; Proserpio, L.; Spiga, D.; Salmaso, B.; Pareschi, G.; Tagliaferri, G.; Burwitz, V.; Hartner, G.; Menz, B.; Bavdaz, M.; Wille, E.

2013-09-01

X-ray telescopes with very large collecting area, like the proposed International X-ray Observatory (IXO, with around 3 m2 at 1 keV), need to be composed of a large number high quality mirror segments, aiming at achieving an angular resolution better than 5 arcsec HEW (Half-Energy-Width). A possible technology to manufacture the modular elements that will compose the entire optical module, named X-ray Optical Units (XOUs), consists of stacking in Wolter-I configuration several layers of thin foils of borosilicate glass, previously formed by hot slumping. The XOUs are subsequently assembled to form complete multi-shell optics with Wolter-I geometry. The achievable global angular resolution of the optic relies on the required surface shape accuracy of slumped foils, on the smoothness of the mirror surfaces and on the correct integration and co-alignment of the mirror segments. The Brera Astronomical Observatory (INAF-OAB) is leading a study, supported by ESA, concerning the implementation of the IXO telescopes based on thin slumped glass foils. In addition to the opto-mechanical design, the study foresees the development of a direct hot slumping thin glass foils production technology. Moreover, an innovative assembly concept making use of Wolter-I counter-form moulds and glass reinforcing ribs is under development. The ribs connect pairs of consecutive foils in an XOU stack, playing a structural and a functional role. In fact, as the ribs constrain the foil profile to the correct shape during the bonding, they damp the low-frequency profile errors still present on the foil after slumping. A dedicated semirobotic Integration MAchine (IMA) has been realized to this scope and used to build a few integrated prototypes made of several layers of slumped plates. In this paper we provide an overview of the project, we report the results achieved so far, including full illumination intra-focus X-ray tests of the last integrated prototype that are compliant with a HEW of around 17''.

Characterization of Magnetron Sputtered Copper-Nickel Thin Film and Alloys

DTIC Science & Technology

2016-09-01

ARL-TR-7783 ● SEP 2016 US Army Research Laboratory Characterization of Magnetron Sputtered Copper-Nickel Thin Films and Alloys...TR-7783 ● SEP 2016 US Army Research Laboratory Characterization of Magnetron Sputtered Copper-Nickel Thin Films and Alloys by Eugene...

Sandwiched Thin-Film Anode of Chemically Bonded Black Phosphorus/Graphene Hybrid for Lithium-Ion Battery.

PubMed

Liu, Hanwen; Zou, Yuqin; Tao, Li; Ma, Zhaoling; Liu, Dongdong; Zhou, Peng; Liu, Hongbo; Wang, Shuangyin

2017-09-01

A facile vacuum filtration method is applied for the first time to construct sandwich-structure anode. Two layers of graphene stacks sandwich a composite of black phosphorus (BP), which not only protect BP from quickly degenerating but also serve as current collector instead of copper foil. The BP composite, reduced graphene oxide coated on BP via chemical bonding, is simply synthesized by solvothermal reaction at 140 °C. The sandwiched film anode used for lithium-ion battery exhibits reversible capacities of 1401 mAh g -1 during the 200th cycle at current density of 100 mA g -1 indicating superior cycle performance. Besides, this facile vacuum filtration method may also be available for other anode material with well dispersion in N-methyl pyrrolidone (NMP). © 2017 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Simulation of thin aluminium-foil in the packaging industry

NASA Astrophysics Data System (ADS)

Eskil, Andreasson; Lindström, Tommy; Käck, Britta; Malmberg, Christoffer; Asp, Ann-Magret

2017-10-01

This work present an approach of how to account for the anisotropic mechanical material behaviour in the simulation models of the thin aluminium foil layer (≈10 µm) used in the Packaging Industry. Furthermore, the experimental results from uniaxial tensile tests are parameterised into an analytical expression and the slope of the hardening subsequently extended way beyond the experimental data points. This in order to accommodate the locally high stresses present in the experiments at the neck formation. An analytical expression, denominated Ramberg-Osgood, is used to describe the non-linear mechanical behaviour. Moreover it is possible with a direct method to translate the experimental uniaxial tensile test results into useful numerical material model parameters in Abaqus™. In addition to this the extended material behaviour including the plastic flow i.e. hardening, valid after onset of localisation, the described procedure can also capture the microscopic events, i.e. geometrical thinning, ongoing in the deformation of the aluminium foil. This method has earlier successfully been applied by Petri Mäkelä for paperboard material [1]. The engineering sound and parameterised description of the mechanical material behaviour facilitates an efficient categorisation of different aluminium foil alloys and aid the identification of the correct anisotropic (RD/TD/45°) mechanical material behaviour derived from the physical testing.

Short protection device for stack of electrolytic cells

DOEpatents

Katz, Murray; Schroll, Craig R.

1985-10-22

Electrical short protection is provided in an electrolytic cell stack by the combination of a thin, nonporous ceramic shield and a noble metal foil disposed on opposite sides of the sealing medium in a gas manifold gasket. The thin ceramic shield, such as alumina, is placed between the porous gasket and the cell stack face at the margins of the negative end plate to the most negative cells to impede ion current flow. The noble metal foil, for instance gold, is electrically coupled to the negative potential of the stack to collect positive ions at a harmless location away from the stack face. Consequently, corrosion products from the stack structure deposit on the foil rather than on the stack face to eliminate electrical shorting of cells at the negative end of the stack.

Small scale mechanical characterization of thin foil materials via pin load microtesting

DOE PAGES

Wheeler, Robert; Pandey, Amit; Shyam, Amit; ...

2015-05-06

In situ scanning electron microscope (SEM) experiments, where small-scale mechanical tests are conducted on micro- and nanosized specimens, allow direct visualization of elastic and plastic responses over the entirety of the volume being deformed. This enables precise spatial and temporal correlation of slip events contributing to the plastic flow evidenced in a stress–strain curve. A new pin-loading methodology has been employed, in situ within the SEM, to conduct microtensile tests on thin polycrystalline metal foils. This approach can be tailored to a specific foil whose particular grain size may range from microns to tens of microns. Manufacture of the specializedmore » pin grip was accomplished via silicon photolithography-based processing followed by subsequent focused ion beam finishing. Microtensile specimen preparation was achieved by combining a stencil mask methodology employing broad ion beam sputtering along with focused ion beam milling in the study of several metallic foil materials. Finite-element analyses were performed to characterize the stress and strain distributions in the pin grip and micro-specimen under load. Furthermore, under appropriately conceived test conditions, uniaxial stress–strain responses measured within these foils by pin-load microtensile testing exhibit properties consistent with larger scale tests.« less

Monitoring transients in low inductance circuits

DOEpatents

Guilford, Richard P.; Rosborough, John R.

1987-01-01

A pair of flat cable transmission lines are monitored for transient current spikes by using a probe connected to a current transformer by a pickup loop and monitoring the output of the current transformer. The approach utilizes a U-shaped pickup probe wherein the pair of flat cable transmission lines are received between the legs of the U-shaped probe. The U-shaped probe is preferably formed of a flat coil conductor adhered to one side of a flexible substrate. On the other side of the flexible substrate there is a copper foil shield. The copper foil shield is connected to one end of the flat conductor coil and connected to one leg of the pickup loop which passes through the current transformer. The other end of the flat conductor coil is connected to the other leg of the pickup loop.

A new approach of the synthesis of SiO 2 nanowires by using bulk copper foils as catalyst

DOE PAGES

Gomez-Martinez, A.; Márquez, F.; Morant, C.

2016-06-22

In this paper, a novel procedure for the growth of SiO 2 nanowires (SiO 2NWs) directly from polycrystalline copper foils is reported. The single-step synthesis procedure consists of a thermal treatment at 900°C without the need for additional catalysts. As a result, nanowires with an average diameter of 100 nm are synthesized. A systematic study undertaken at different stages of the SiO 2NWs growth confirmed the generation of nucleation centers on the Cu surface, as well as revealed the existence of an intermediate gaseous SiO species at the synthesis temperature. Lastly, on the basis of these evidences, the vapor-liquid-solid (VLS)more » route has been proposed as the mechanism responsible for the growth.« less

Experimental Investigation of Material Flows Within FSWs Using 3D Tomography

DOE Office of Scientific and Technical Information (OSTI.GOV)

Charles R. Tolle; Timothy A. White; Karen S. Miller

2008-06-01

There exists significant prior work using tracers or pre-placed hardened markers within friction stir welding (FSWing) to experimentally explore material flow within the FSW process. Our experiments replaced markers with a thin sheet of copper foil placed between the 6061 aluminum lap and butt joints that were then welded. The absorption characteristics of x-rays for copper and aluminum are significantly different allowing for non-destructive evaluation (NDE) methods such as x-ray computed tomography (CT) to be used to demonstrate the material movement within the weldment on a much larger scale than previously shown. 3D CT reconstruction of the copper components ofmore » the weldment allows for a unique view into the final turbulent state of the welding process as process parameters are varied. The x-ray CT data of a section of the weld region was collected using a cone-beam x-ray imaging system developed at the INL. Six-hundred projections were collected over 360-degrees using a 160-kVp Bremsstrahlung x-ray generator (25-micrometer focal spot) and amorphoussilicon x-ray detector. The region of the object that was imaged was about 3cm tall and 1.5cm x 1cm in cross section, and was imaged at a magnification of about 3.6x. The data were reconstructed on a 0.5x0.5x0.5 mm3 voxel grid. After reconstruction, the aluminum and copper could be easily discriminated using a gray level threshold allowing visualization of the copper components. Fractal analysis of the tomographic reconstructed material topology is investigated as a means to quantify macro level material flow based on process parameters. The results of multi-pass FSWs show increased refinement of the copper trace material. Implications of these techniques for quantifying process flow are discussed.« less

Observation of alpha particle loss from JET plasmas during ion cyclotron resonance frequency heating using a thin foil Faraday cup detector array.

PubMed

Darrow, D S; Cecil, F E; Kiptily, V; Fullard, K; Horton, A; Murari, A

2010-10-01

The loss of MeV alpha particles from JET plasmas has been measured with a set of thin foil Faraday cup detectors during third harmonic heating of helium neutral beam ions. Tail temperatures of ∼ 2 MeV have been observed, with radial scrape off lengths of a few centimeters. Operational experience from this system indicates that such detectors are potentially feasible for future large tokamaks, but careful attention to screening rf and MHD induced noise is essential.

Methods of making copper selenium precursor compositions with a targeted copper selenide content and precursor compositions and thin films resulting therefrom

DOEpatents

Curtis, Calvin J [Lakewood, CO; Miedaner, Alexander [Boulder, CO; van Hest, Marinus Franciscus Antonius Maria; Ginley, David S [Evergreen, CO; Leisch, Jennifer [Denver, CO; Taylor, Matthew [West Simsbury, CT; Stanbery, Billy J [Austin, TX

2011-09-20

Precursor compositions containing copper and selenium suitable for deposition on a substrate to form thin films suitable for semi-conductor applications. Methods of forming the precursor compositions using primary amine solvents and methods of forming the thin films wherein the selection of temperature and duration of heating controls the formation of a targeted species of copper selenide.

Large-area thin self-supporting carbon foils with MgO coatings

NASA Astrophysics Data System (ADS)

Stolarz, Anna; Maier-Komor, Peter

2002-03-01

Large area self-supporting carbon foils in the thickness of range of 8-22 μg/cm 2, coated with approximately 4 μg/cm 2 MgO have been prepared by e-gun evaporation. They were mounted on frames with apertures of 130 cm 2. Problems related to the parting agent preparation, floating procedure, and mounting onto frames are discussed. Special precautions necessary to avoid damage during foil drying, storage and transportation are suggested.

Joining of materials using laser heating

DOEpatents

Cockeram, Brian V.; Hicks, Trevor G.; Schmid, Glenn C.

2003-07-01

A method for diffusion bonding ceramic layers such as boron carbide, zirconium carbide, or silicon carbide uses a defocused laser beam to heat and to join ceramics with the use of a thin metal foil insert. The metal foil preferably is rhenium, molybdenum or titanium. The rapid, intense heating of the ceramic/metal/ceramic sandwiches using the defocused laser beam results in diffusive conversion of the refractory metal foil into the ceramic and in turn creates a strong bond therein.

Development of Fractal Ultra-Hydrophobic Coating Films to Prevent Water Vapor Dewing and to Delay Frosting

NASA Astrophysics Data System (ADS)

Quan, Yun-Yun; Jiang, Pei-Guo; Zhang, Li-Zhi

2014-09-01

Superhydrophobic films fabricated on copper and aluminum surfaces have potential applications to solve water condensation and frosting problems on chilled ceiling system. The rough surfaces of copper foils obtained by solution immersion method exhibit the existence of fractal structures. The hydrophobicity of copper surfaces is enhanced with fractal structures. The relationship between contact angles (CAs) and the fractal dimensions (FDs) for surface roughness of Cu samples with different etching time is investigated. Moisture condensation and frosting experiments on the two kinds of surfaces are conducted in natural environment under different chilling temperatures. During condensation, micro water condensate droplets drift down the surface like dust floating in the air. Several larger condensate droplets about 1-2 mm appear on the substrates after 3 h condensation. This continuous jumping motion of the condensate will be beneficial in delaying frosting. The results demonstrate that dense nanostructures on copper surfaces are superior to loose lattice-like microstructures on aluminum surfaces for preventing the formation of large droplets condensate and in delaying the icing. The large water droplets of 2-3 mm in diameter that would form on a common metal foil are sharply decreased to dozens of microns and small droplets are formed on a modified surface, which will then drift down like a fog.

Graphene growth process modeling: a physical-statistical approach

NASA Astrophysics Data System (ADS)

Wu, Jian; Huang, Qiang

2014-09-01

As a zero-band semiconductor, graphene is an attractive material for a wide variety of applications such as optoelectronics. Among various techniques developed for graphene synthesis, chemical vapor deposition on copper foils shows high potential for producing few-layer and large-area graphene. Since fabrication of high-quality graphene sheets requires the understanding of growth mechanisms, and methods of characterization and control of grain size of graphene flakes, analytical modeling of graphene growth process is therefore essential for controlled fabrication. The graphene growth process starts with randomly nucleated islands that gradually develop into complex shapes, grow in size, and eventually connect together to cover the copper foil. To model this complex process, we develop a physical-statistical approach under the assumption of self-similarity during graphene growth. The growth kinetics is uncovered by separating island shapes from area growth rate. We propose to characterize the area growth velocity using a confined exponential model, which not only has clear physical explanation, but also fits the real data well. For the shape modeling, we develop a parametric shape model which can be well explained by the angular-dependent growth rate. This work can provide useful information for the control and optimization of graphene growth process on Cu foil.

Numerical simulations of energy deposition caused by 50 MeV—50 TeV proton beams in copper and graphite targets

NASA Astrophysics Data System (ADS)

Nie, Y.; Schmidt, R.; Chetvertkova, V.; Rosell-Tarragó, G.; Burkart, F.; Wollmann, D.

2017-08-01

The conceptual design of the Future Circular Collider (FCC) is being carried out actively in an international collaboration hosted by CERN, for the post-Large Hadron Collider (LHC) era. The target center-of-mass energy of proton-proton collisions for the FCC is 100 TeV, nearly an order of magnitude higher than for LHC. The existing CERN accelerators will be used to prepare the beams for FCC. Concerning beam-related machine protection of the whole accelerator chain, it is critical to assess the consequences of beam impact on various accelerator components in the cases of controlled and uncontrolled beam losses. In this paper, we study the energy deposition of protons in solid copper and graphite targets, since the two materials are widely used in magnets, beam screens, collimators, and beam absorbers. Nominal injection and extraction energies in the hadron accelerator complex at CERN were selected in the range of 50 MeV-50 TeV. Three beam sizes were studied for each energy, corresponding to typical values of the betatron function. Specifically for thin targets, comparisons between fluka simulations and analytical Bethe equation calculations were carried out, which showed that the damage potential of a few-millimeter-thick graphite target and submillimeter-thick copper foil can be well estimated directly by the Bethe equation. The paper provides a valuable reference for the quick evaluation of potential damage to accelerator elements over a large range of beam parameters when beam loss occurs.

Flower-Like CuO/ZnO Hybrid Hierarchical Nanostructures Grown on Copper Substrate: Glycothermal Synthesis, Characterization, Hydrophobic and Anticorrosion Properties

PubMed Central

Beshkar, Farshad; Khojasteh, Hossein; Salavati-Niasari, Masoud

2017-01-01

In this work we have demonstrated a facile formation of CuO nanostructures on copper substrates by the oxidation of copper foil in ethylene glycol (EG) at 80 °C. On immersing a prepared CuO film into a solution containing 0.1 g Zn(acac)2 in 20 mL EG for 8 h, ZnO flower-like microstructures composed of hierarchical three-dimensional (3D) aggregated nanoparticles and spherical architectures were spontaneously formed at 100 °C. The as-synthesized thin films and 3D microstructures were characterized using XRD, SEM, and EDS techniques. The effects of sodium dodecyl sulphate (SDS), cetyltrimethylammonium bromide (CTAB), and polyethylene glycol (PEG) 6000 as surfactants and stabilizers on the morphology of the CuO and ZnO structures were discussed. Possible growth mechanisms for the controlled organization of primary building units into CuO nanostructures and 3D flower-like ZnO architectures were proposed. The hydrophobic property of the products was characterized by means of water contact angle measurement. After simple surface modification with stearic acid and PDMS, the resulting films showed hydrophobic and even superhydrophobic characteristics due to their special surface energy and nano-microstructure morphology. Importantly, stable superhydrophobicity with a contact angle of 153.5° was successfully observed for CuO-ZnO microflowers after modification with PDMS. The electrochemical impedance measurements proved that the anticorrosion efficiency for the CuO/ZnO/PDMS sample was about 99%. PMID:28773056

Flower-Like CuO/ZnO Hybrid Hierarchical Nanostructures Grown on Copper Substrate: Glycothermal Synthesis, Characterization, Hydrophobic and Anticorrosion Properties.

PubMed

Beshkar, Farshad; Khojasteh, Hossein; Salavati-Niasari, Masoud

2017-06-25

In this work we have demonstrated a facile formation of CuO nanostructures on copper substrates by the oxidation of copper foil in ethylene glycol (EG) at 80 °C. On immersing a prepared CuO film into a solution containing 0.1 g Zn(acac)₂ in 20 mL EG for 8 h, ZnO flower-like microstructures composed of hierarchical three-dimensional (3D) aggregated nanoparticles and spherical architectures were spontaneously formed at 100 °C. The as-synthesized thin films and 3D microstructures were characterized using XRD, SEM, and EDS techniques. The effects of sodium dodecyl sulphate (SDS), cetyltrimethylammonium bromide (CTAB), and polyethylene glycol (PEG) 6000 as surfactants and stabilizers on the morphology of the CuO and ZnO structures were discussed. Possible growth mechanisms for the controlled organization of primary building units into CuO nanostructures and 3D flower-like ZnO architectures were proposed. The hydrophobic property of the products was characterized by means of water contact angle measurement. After simple surface modification with stearic acid and PDMS, the resulting films showed hydrophobic and even superhydrophobic characteristics due to their special surface energy and nano-microstructure morphology. Importantly, stable superhydrophobicity with a contact angle of 153.5° was successfully observed for CuO-ZnO microflowers after modification with PDMS. The electrochemical impedance measurements proved that the anticorrosion efficiency for the CuO/ZnO/PDMS sample was about 99%.

Cadmium-free junction fabrication process for CuInSe.sub.2 thin film solar cells

DOEpatents

Ramanathan, Kannan V.; Contreras, Miguel A.; Bhattacharya, Raghu N.; Keane, James; Noufi, Rommel

1999-01-01

The present invention provides an economical, simple, dry and controllable semiconductor layer junction forming process to make cadmium free high efficiency photovoltaic cells having a first layer comprised primarily of copper indium diselenide having a thin doped copper indium diselenide n-type region, generated by thermal diffusion with a group II(b) element such as zinc, and a halide, such as chlorine, and a second layer comprised of a conventional zinc oxide bilayer. A photovoltaic device according the present invention includes a first thin film layer of semiconductor material formed primarily from copper indium diselenide. Doping of the copper indium diselenide with zinc chloride is accomplished using either a zinc chloride solution or a solid zinc chloride material. Thermal diffusion of zinc chloride into the copper indium diselenide upper region creates the thin n-type copper indium diselenide surface. A second thin film layer of semiconductor material comprising zinc oxide is then applied in two layers. The first layer comprises a thin layer of high resistivity zinc oxide. The second relatively thick layer of zinc oxide is doped to exhibit low resistivity.

Influence of UV and Gamma radiations on the induced birefringence of stretched poly(vinyl) alcohol foils

NASA Astrophysics Data System (ADS)

Nechifor, Cristina-Delia; Zelinschi, Carmen Beatrice; Dorohoi, Dana-Ortansa

2014-03-01

The aim of our paper is to evidence the influence of Gamma and UV radiations on the induced birefringence of poly(vinyl alcohol) stretched foils. Thin foils of PVA were prepared and dried without modifying their surfaces. The polymeric foils were irradiated from 15 min to 6 h using UV and Gamma radiations. The induced by stretching under heating birefringence of PVA films was measured at λ = 589.3 nm with a Babinet Compensator. Physico-chemical processes (photo stabilization, photo degradation, oxidation) induced by irradiation of polymer matrix influence both the stretching degree and the anisotropy of etired foils. An increase of birefringence versus the stretching ratio of the PVA foils was evidenced for all studied samples. The dependence of the birefringence on the exposure time, stretching ratio and nature of radiation was also confirmed.

Thin film fabrication and system integration test run for a microactuator for a tuneable lens

NASA Astrophysics Data System (ADS)

Hoheisel, Dominik; Rissing, Lutz

2014-03-01

An electromagnetic microactuator, for controlling of a tuneable lens, with an integrated electrostatic element is fabricated by thin film technology. The actuator consists of two parts: the first part with microcoil and flux guide and the second part with a ring shaped back iron on a polyimide membrane. The back iron is additionally useable as electrode for electrostatic measurement of the air gap and for electrostatic actuation. By attracting the back iron an optical liquid is displaced and forms a liquid lens inside the back iron ring covered by the membrane. For testing the thin film fabrication sequence, up-scaled systems are generated in a test run. To fabricate the flux guide in an easy and quick way, a Ni-Fe foil with a thickness of 50 μm is laminated on the Si-wafer. This foil is also utilized in the following fabrication sequence as seed layer for electroplating. Compared to Ni-Fe structures deposited by electroplating, the foil is featuring better soft magnetic properties. The foil is structured by wet chemical etching and the backside of the wafer is structured by deep reactive ion etching (DRIE). For post fabrication thinning, the polyimide membrane is treated by oxygen plasma etching. To align the back iron to the microcoil and the flux guide, a flip-chip-bonder is used during test run of system integration. To adjust a constant air gap, a water solvable polymer is tested. A two component epoxy and a polyimide based glue are compared for their bonding properties of the actuator parts.

Intense pulsed light annealing of copper zinc tin sulfide nanocrystal coatings

DOE Office of Scientific and Technical Information (OSTI.GOV)

Williams, Bryce A.; Smeaton, Michelle A.; Holgate, Collin S.

2016-09-15

A promising method for forming the absorber layer in copper zinc tin sulfide [Cu{sub 2}ZnSnS{sub 4} (CZTS)] thin film solar cells is thermal annealing of coatings cast from dispersions of CZTS nanocrystals. Intense pulsed light (IPL) annealing utilizing xenon flash lamps is a potential high-throughput, low-cost, roll-to-roll manufacturing compatible alternative to thermal annealing in conventional furnaces. The authors studied the effects of flash energy density (3.9–11.6 J/cm{sup 2}) and number of flashes (1–400) during IPL annealing on the microstructure of CZTS nanocrystal coatings cast on molybdenum-coated soda lime glass substrates (Mo-coated SLG). The annealed coatings exhibited cracks with two distinct linearmore » crack densities, 0.01 and 0.2 μm{sup −1}, depending on the flash intensity and total number of flashes. Low density cracking (0.01 μm{sup −1}, ∼1 crack per 100 μm) is caused by decomposition of CZTS at the Mo-coating interface. Vapor decomposition products at the interface cause blisters as they escape the coating. Residual decomposition products within the blisters were imaged using confocal Raman spectroscopy. In support of this hypothesis, replacing the Mo-coated SLG substrate with quartz eliminated blistering and low-density cracking. High density cracking is caused by rapid thermal expansion and contraction of the coating constricted on the substrate as it is heated and cooled during IPL annealing. Finite element modeling showed that CZTS coatings on low thermal diffusivity materials (i.e., SLG) underwent significant differential heating with respect to the substrate with rapid rises and falls of the coating temperature as the flash is turned on and off, possibly causing a build-up of tensile stress within the coating prompting cracking. Use of a high thermal diffusivity substrate, such as a molybdenum foil (Mo foil), reduces this differential heating and eliminates the high-density cracking. IPL annealing in presence of sulfur vapor prevented both low- and high-density cracking as well as blistering. However, grain growth was limited even after annealing with 400 flashes. This lack of grain growth is attributed to a difficulty of maintaining high sulfur vapor pressure and absence of alkali metal impurities when Mo foil substrates are used.« less

METHOD OF MEASURING THE INTEGRATED ENERGY OUTPUT OF A NEUTRONIC CHAIN REACTOR

DOEpatents

Sturm, W.J.

1958-12-01

A method is presented for measuring the integrated energy output of a reactor conslsting of the steps of successively irradiating calibrated thin foils of an element, such as gold, which is rendered radioactive by exposure to neutron flux for periods of time not greater than one-fifth the mean life of the induced radioactlvity and producing an indication of the radioactivity induced in each foil, each foil belng introduced into the reactor immediately upon removal of its predecessor.

Flexible patch composed of PZT thin-film on stainless steel foil for energy harvesting from low-frequency human motions

NASA Astrophysics Data System (ADS)

Wang, Yin Jie; Chen, Chao Ting; Chen, Jiun Jung; Yeh, Sou Peng; Wu, Wen Jong

2015-03-01

To harvest energy from human motion and generate power for the emerging wearable devices, energy harvesters are required to work at very low frequency. There are several studies based on energy harvesting through human gait, which can generate significant power. However, when wearing these kind of devices, additional effort may be required and the user may feel uncomfortable when moving. The energy harvester developed here is composed of a 10 μm PZT thin-film deposited on 50 μm thick stainless steel foil by the aerosol deposition method. The PZT layer and the stainless steel foil are both very thin, thus the patch is highly flexible. The patch can be attached on the skin to harvester power through human motions such as the expansion of the chest region while breathing. The energy harvester will first be tested with a moving stage for power output measurements. The energy density can be determined for different deformation ranges and frequencies. The fabrication processes and testing results will all be detailed in this paper.

Micrometeoroids and debris on LDEF

NASA Technical Reports Server (NTRS)

Mandeville, Jean-Claude

1992-01-01

Part of the LDEF tray allocated to French Experiments (FRECOPA) was devoted to the study of dust particles. The tray was located on the face of LDEF directly opposed to the velocity vector. Two passive experiments were flown: a set of glass and metallic samples; and multilayer thin foil detectors. Crater size distribution made possible the evaluation of the incident microparticle flux in the near environment. Comparisons are made with measurements obtained on the other faces of LDEF and with results from similar experiments on the MIR. Of interest was the study of impact features on stacked thin foil detectors. The top foil acted as a shield, fragmenting the projectiles and spreading the fragments over the surface of the thick plate located underneath. EDS analysis has provided evidence of impactor fragments. Detectors consisting of a thin shield and thick bottom plate appear to offer a significantly higher return of data concerning chemical analysis of impactor residues than single plate detectors. The samples of various materials offer a unique opportunity for the study of the many processes involved upon hypervelocity impact phenomena.

Laser Radiation Pressure Acceleration of Monoenergetic Protons in an Ultra-Thin Foil

NASA Astrophysics Data System (ADS)

Eliasson, Bengt; Liu, Chuan S.; Shao, Xi; Sagdeev, Roald Z.; Shukla, Padma K.

2009-11-01

We present theoretical and numerical studies of the acceleration of monoenergetic protons in a double layer formed by the laser irradiation of an ultra-thin film. The stability of the foil is investigated by direct Vlasov-Maxwell simulations for different sets of laser-plasma parameters. It is found that the foil is stable, due to the trapping of both electrons and ions in the thin laser-plasma interaction region, where the electrons are trapped in a potential well composed of the ponderomo-tive potential of the laser light and the electrostatic potential due to the ions, and the ions are trapped in a potential well composed of the inertial potential in an accelerated frame and the electrostatic potential due to the electrons. The result is a stable double layer, where the trapped ions are accelerated to monoenergetic energies up to 100 MeV and beyond, which makes them suitable for medical applications cancer treatment. The underlying physics of trapped and untapped ions in a double layer is also investigated theoretically and numerically.

A Manganin Thin Film Ultra-High Pressure Sensor for Microscale Detonation Pressure Measurement

PubMed Central

Zhang, Guodong; Zhao, Yulong; Zhao, Yun; Wang, Xinchen; Ren, Wei; Li, Hui; Zhao, You

2018-01-01

With the development of energetic materials (EMs) and microelectromechanical systems (MEMS) initiating explosive devices, the measurement of detonation pressure generated by EMs in the microscale has become a pressing need. This paper develops a manganin thin film ultra-high pressure sensor based on MEMS technology for measuring the output pressure from micro-detonator. A reliable coefficient is proposed for designing the sensor’s sensitive element better. The sensor employs sandwich structure: the substrate uses a 0.5 mm thick alumina ceramic, the manganin sensitive element with a size of 0.2 mm × 0.1 mm × 2 μm and copper electrodes of 2 μm thick are sputtered sequentially on the substrate, and a 25 μm thick insulating layer of polyimide is wrapped on the sensitive element. The static test shows that the piezoresistive coefficient of manganin thin film is 0.0125 GPa−1. The dynamic experiment indicates that the detonation pressure of micro-detonator is 12.66 GPa, and the response time of the sensor is 37 ns. In a word, the sensor developed in this study is suitable for measuring ultra-high pressure in microscale and has a shorter response time than that of foil-like manganin gauges. Simultaneously, this study could be beneficial to research on ultra-high-pressure sensors with smaller size. PMID:29494519

Tin Can Radiation Detector.

ERIC Educational Resources Information Center

Crull, John L.

1986-01-01

Provides instructions for making tin can radiation detectors from empty aluminum cans, aluminum foil, clear plastic, copper wire, silica gel, and fine, unwaxed dental floss put together with tape or glue. Also provides suggestions for activities using the detectors. (JN)

Method of fabricating a uranium-bearing foil

DOEpatents

Gooch, Jackie G [Seymour, TN; DeMint, Amy L [Kingston, TN

2012-04-24

Methods of fabricating a uranium-bearing foil are described. The foil may be substantially pure uranium, or may be a uranium alloy such as a uranium-molybdenum alloy. The method typically includes a series of hot rolling operations on a cast plate material to form a thin sheet. These hot rolling operations are typically performed using a process where each pass reduces the thickness of the plate by a substantially constant percentage. The sheet is typically then annealed and then cooled. The process typically concludes with a series of cold rolling passes where each pass reduces the thickness of the plate by a substantially constant thickness amount to form the foil.

Synthetic Graphene Grown by Chemical Vapor Deposition on Copper Foils

DTIC Science & Technology

2013-04-11

b) Transparent PMMA /graphene membrane floating on copper etchant. (c) Three layers of stacked CVD graphene on a cover glass made by consecutively...insulating substrate is a critical step for fabricating electronic devices. PMMA -assisted transfer techniques are commonly applied because of their...simplicity and repeatability.13 In a typical transfer, a graphene film on Cu substrate was first coated with PMMA (950PMMA-A4, MicroChem)b by spin

Ion acceleration from thin foil and extended plasma targets by slow electromagnetic wave and related ion-ion beam instability

DOE Office of Scientific and Technical Information (OSTI.GOV)

Bulanov, S. V.; A. M. Prokhorov Institute of General Physics RAS, Moscow, 119991; Esirkepov, T. Zh.

When ions are accelerated by the radiation pressure of a laser pulse, their velocity cannot exceed the pulse group velocity which can be considerably smaller than the speed of light in vacuum. This is demonstrated in two cases corresponding to a thin foil target irradiated by high intensity laser light and to the hole boring produced in an extended plasma by the laser pulse. It is found that the beams of accelerated ions are unstable against Buneman-like and Weibel-like instabilities which results in the broadening of the ion energy spectrum.

Deposition of thin insulation layers from the gas phase

NASA Technical Reports Server (NTRS)

Behn, R.; Hagedorn, H.; Kammermaier, J.; Kobale, M.; Packonik, H.; Ristow, D.; Seebacher, G.

1981-01-01

The continuous deposition of thin organic dielectric films on metallized carrier foils by glow discharge in monomeric gases is described. Depending on the applied monomers, the films had a dissipation factor of .001 to .003 (1 kHz), a relative permittivity of 2.3 to 2.5 and a resistivity of about 10 to the 17th power omega cm. Additionally, they proved to have a high mechanical homogeneity. Self-healing rolled capacitors with a very high capacitance per volume and of consistently high quality were fabricated from the metallized carrier foils covered with the dielectric film.

Proceeding of the 1999 Particle Accelerator Conference. Volume 5

DTIC Science & Technology

1999-04-02

peeled back from the pipe. Sumitomo’s specification gives an Ic of 133A at 4.2K and 12T. This is defined at a critical field of 1 jtV/cm. Our The...copper peeled away from the pipe had a light discoloration where it had been held most tightly in 5.1 Derivation of J, at Higher Temperatures contact with...were bonded between the Invar BB20/1_- T L and the copper. No discoloration of the Invar or of the To copper foil was seen in the areas where we peeled

Modification of surface layers of copper under the action of the volumetric discharge initiated by an avalanche electron beam in nitrogen and CO2 at atmospheric pressure

NASA Astrophysics Data System (ADS)

Shulepov, M. A.; Akhmadeev, Yu. Kh.; Tarasenko, V. F.; Kolubaeva, Yu. A.; Krysina, O. V.; Kostyrya, I. D.

2011-05-01

The results of experimental investigations of the action of the volumetric discharge initiated by an avalanche electron beam on the surface of copper specimens are presented. The volumetric (diffuse) discharge in nitrogen and CO2 at atmospheric pressure was initiated by applying high voltage pulses of nanosecond duration to a tubular foil cathode. It has been found that the treatment of a copper surface by this type of discharge increases the hardness of the surface layer due to oxidation.

Bending fatigue of electron-beam-welded foils. Application to a hydrodynamic air bearing in the Chrysler/DOE upgraded automotive gas tubine engine

NASA Technical Reports Server (NTRS)

Saltsman, J. F.; Halford, G. R.

1984-01-01

A hydrodynamic air bearing with a compliment surface is used in the gas generator of an upgraded automotive gas turbine engine. In the prototype design, the compliant surface is a thin foil spot welded at one end to the bearing cartridge. During operation, the foil failed along the line of spot welds which acted as a series of stress concentrators. Because of its higher degree of geometric uniformity, electron beam welding of the foil was selected as an alternative to spot welding. Room temperature bending fatigue tests were conducted to determine the fatigue resistance of the electron beam welded foils. Equations were determined relating cycles to crack initiation and cycles to failure to nominal total strain range. A scaling procedure is presented for estimating the reduction in cyclic life when the foil is at its normal operating temperature of 260 C (500 F).

Evidence for Coincident Fusion Products Using Silicon Surface-barrier Detectors

NASA Astrophysics Data System (ADS)

Jones, Steven; Scott, Mark; Keeney, Frank

2002-10-01

We report experimental results showing coincident proton and triton production from the reaction: d + d --> t (1.01 MeV) + p (3.02 MeV). Partially-deuterided thin titanium foils were positioned between two silicon surface-barrier detectors which were mounted in a small cylindrical vacuum chamber which also served as a Faraday cage. We performed Monte Carlo studies using the SRIM code to determine the expected energies of arriving particles after they exit the host foil. The dual-coincidence requirement reduces background to very low levels so that low yields from very thin TiD foils can be readily detected. In one sequence of experiments, we observed 74 foreground coincidences in the regions of interest compared with 24 background counts; the statistical significance is approximately ten standard deviations. A striking advance is that the repeatability from the dual-coincidence experiments is currently greater than 70%.

Thin plastic foil X-ray optics with spiral geometry

NASA Astrophysics Data System (ADS)

Barbera, Marco; Mineo, Teresa; Perinati, Emanuele; Schnopper, Herbert W.; Taibi, Angelo

2007-09-01

Winding a plastic foil ribbon into spiral cylinder or spiral cones we can design and build single or multiple reflection X-ray grazing incidence focusing optics with potential applications in Astronomy as well as experimental physics. The use of thin plastic foils from common industrial applications and of a mounting technique which does not require the construction of mandrels make these optics very cost effective. A spiral geometry focusing optic produces an annular image of a point source with the angular size of the annulus depending mainly on the pitch of the winding and the focal length. We use a ray-tracing code to evaluate the performances of cylindrical, and double conical spiral geometry as a function of the design parameters e.g. focal length, diameter, optic length. Some preliminary results are presented on X-ray imaging tests performed on spiral cylindrical optics.

X-ray mirror prototype based on cold shaping of thin glass foils

NASA Astrophysics Data System (ADS)

Basso, Stefano; Civitani, Marta; Ghigo, Mauro; Hołyszko, Joanna; Pareschi, Giovanni; Salmaso, Bianca; Vecchi, Gabriele; Burwitz, Vadim; Pelliciari, Carlo; Hartner, Gisela D.; Breunig, Elias

2017-08-01

The Slumping Glass Optics technology for the fabrication of astronomical X-ray mirrors has been developed in recent years in USA and Europe. The process has been used for making the mirrors of the Nustar, mission. The process starts with very thin glass foils hot formed to copy the profile of replication moulds. At INAF - Osservatorio Astronomico di Brera a process based on cold shaping is being developed, based on an integration method involving the use of interconnecting ribs for making stacks. Each glass foil in the stack is shaped onto a very precise integration mould and the correct shape is frozen by means of glued ribs that act as spacers between one layer and the next one (the first layers being attached to a thick substrate). Therefore, the increasing availability of flexible glass foils with a thickness of a few tens of microns (driven by electronic market for ultra-thin displays) opens new possibilities for the fabrication of X-ray mirrors. This solution appears interesting especially for the fabrication of mirrors for hard X-rays (with energy > 10 keV) based on multilayer coatings, taking advantage from the intrinsic low roughness of the glass foils that should grant a low scattering level. The stress frozen on the glass due to the cold shaping is not negligible, but it is kept into account in the errors of the X-ray optics design. As an exercise, we have considered the requirements and specs of the FORCE hard Xray mission concept (being studied by JAXA) and we have designed the mirror modules assuming the cold slumping as a fabrication method. In the meantime, a prototype (representative of the FORCE mirror modules) is being design and integrated in order to demonstrate the feasibility and the capacity to reach good angular resolution.

Cost-Effective TiAl based Materials

NASA Technical Reports Server (NTRS)

Moxson, V. S.; Sun, Fusheng; Draper, Susan L.; Froes, F. H.; Duz, V.

2003-01-01

Because of their inherent low ductility, TiAl-based materials are difficult to fabricate, especially thin gage titanium gamma aluminide (TiAl) sheet and foil. In this paper, an innovative powder metallurgy approach for producing cost-effective thin gage TiAl sheets (with 356 mm long and 235 mm wide, and a thickness of 0.74, 1.09, 1.55, and 2.34 mm, respectively) is presented. The microstructures and tensile properties at room and elevated temperatures of the thin gage TiAl are studied. Results show that these TiAl sheets have a relatively homogenous chemistry, uniform microstructure, and acceptable mechanical properties. This work demonstrates a cost-effective method for producing both flat products (sheet/foil) and complex chunky parts of TiAl for various advanced applications including aerospace and automotive industries.

INTEGRAL REACTION RATES AND NEUTRON ENERGY SPECTRA IN A WELL MODERATED REACTOR

DOE Office of Scientific and Technical Information (OSTI.GOV)

Connolly, J.W.; Rose, A.; Wall, T.

1963-04-01

Cadmium ratio measurements in the internal reflector of MOATA were made with gold, indium, tungsten, manganese, molybdenum, and copper detectors. These measurements were analyzed on the assumption that the neutron spectrum consists of a Maxwellian distribution to which is smoothly joined a 1/E slowing down spectrum, the cross sections being averaged according to the methods of Westcott. A search through recent literature suggests that the s factors for gold and indium listed by Westcott are in error. If this is accepted, then it appears that the measured epithermal spectrum is closely 1/E in form for neutron energies between 1 andmore » 600 ev. The corrections to be applied when foils of finite thickness are used in cadmium ratio measuremerts are discussed, and the spectrum derived from these measurements was used to calculate reaction rate ratios of copper: indium and copper: gold alloy foils. These ratios were compared with measured values. Values of the effective resonance integral of Pt/sup 198/ wire detectors were measured, and from these values an estimate was made of the infinitely dilute resonance integral of this isotope. (auth)« less

Evaluated activation cross sections of longer-lived radionuclides produced by deuteron-induced reactions on natural copper

NASA Astrophysics Data System (ADS)

Takács, S.; Tárkányi, F.; Király, B.; Hermanne, A.; Sonck, M.

2006-09-01

Activation cross sections for deuteron-induced reactions on natural copper were measured by using a standard stacked foil technique up to 50 MeV deuteron bombarding energy. Reaction products with half-life longer than half an hour were studied. Experimental elemental cross sections were determined and compared with earlier measured data for 62,63,65Zn, 64Cu, 57,65Ni, 57,58,60Co and 59Fe isotopes.

MULPEX: A compact multi-layered polymer foil collector for micrometeoroids and orbital debris

NASA Astrophysics Data System (ADS)

Kearsley, A. T.; Graham, G. A.; Burchell, M. J.; Taylor, E. A.; Drolshagen, G.; Chater, R. J.; McPhail, D.

Detailed studies of preserved hypervelocity impact residues on spacecraft multi-layer insulation foils have yielded important information about the flux of small particles from different sources in low-Earth orbit (LEO). We have extended our earlier research on impacts occurring in LEO to design and testing of a compact capture device. MUlti- Layer Polymer EXperiment (MULPEX) is simple, cheap to build, lightweight, of no power demand, easy to deploy, and optimised for the efficient collection of impact residue for analysis on return to Earth. The capture medium is a stack of very thin (8 and 40 μm) polyimide foils, supported on poly-tetrafluoroethylene sheet frames, surrounded by a protective aluminium casing. The uppermost foil has a very thin metallic coating for thermal protection and resistance to atomic oxygen and ultra-violet exposure. The casing provides a simple detachable interface for deployment on the spacecraft, facing into the desired direction for particle collection. On return to the laboratory, the stacked foils are separated for examination in a variable pressure scanning electron microscope, without need for surface coating. Analysis of impact residue is performed using energy dispersive X-ray spectrometers. Our laboratory experiments, utilising buck-shot firings of analogues to micrometeoroids (35-38 μm olivine) and space debris (4 μm alumina and 1 mm stainless steel) in a light gas gun, have shown that impact residue is abundant within the foil layers, and preserves a record of the impacting particle, whether of micrometer or millimetre dimensions. Penetrations of the top foil are easily recognised, and act as a proxy for dimensions of the penetrating particle. Impact may cause disruption and melting, but some residue retains sufficient crystallographic structure to show clear Raman lines, diagnostic of the original mineral.

MULPEX: a compact multi-layered polymer foil collector for micrometeoroids and orbital debris.

NASA Astrophysics Data System (ADS)

Kearsley, A. T.; Graham, G. A.; Burchell, M. J.; Taylor, E. A.; Drolshagen, G.; Chater, R. J.; McPhail, D.

Detailed studies of preserved hypervelocity impact residues on spacecraft multi-layer insulation foils have yielded important information about the flux of small particles from different sources in low-Earth orbit (LEO). We have extended our earlier research on impacts occurring in LEO to design and testing of a compact capture device. MULPEX (MUlti-Layer Polymer EXperiment) is simple, cheap to build, lightweight, of no power demand, easy to deploy, and optimised for the efficient collection of impact residue for analysis on return to Earth. The capture medium is a stack of very thin (8 micron and 40 micron) polyimide foils, supported on poly-tetrafluoroethylene sheet frames, surrounded by a protective aluminium casing. The uppermost foil has a very thin metallic coating for thermal protection and resistance to atomic oxygen and ultra-violet exposure. The casing provides a simple detachable interface for deployment on the spacecraft, facing into the desired direction for particle collection. On return to the laboratory, the stacked foils are separated for examination in a variable pressure scanning electron microscope, without need for surface coating. Analysis of impact residue is performed using energy dispersive X-ray spectrometers. Our laboratory experiments, utilising buck-shot firings of analogues to micrometeoroids (35-38 micron olivine) and space debris (4 micron alumina and 1mm stainless steel) in a light gas gun, have shown that impact residue is abundant within the foil layers, and preserves a record of the impacting particle, whether of micrometer or millimetre dimensions. Penetrations of the top foil are easily recognised, and act as a proxy for dimensions of the penetrating particle. Impact may cause disruption and melting, but some residue retains sufficient crystallographic structure to show clear Raman lines, diagnostic of the original mineral.

Anisotropic Hydrogen Etching of Chemical Vapor Deposited Graphene

NASA Astrophysics Data System (ADS)

Zhang, Yi; Li, Zhen; Zhang, Luyao; Kim, Pyojae; Zhou, Chongwu

2012-02-01

In terms of the preparation of graphene, chemical vapor deposition (CVD) has raised its popularity as a scalable and cost effective approach for graphene synthesis. While the formation of graphene on copper foil has been intensively studied, the reverse reaction of graphene reacts with hydrogen has not been systematically studied. In this talk we will present a simple, clean, and highly anisotropic hydrogen etching method for CVD graphene catalyzed by the copper substrate. By exposing CVD graphene on copper foil to hydrogen flow around 800 ^oC, we observed that the initially continuous graphene can be etched to have many hexagonal openings. In addition, we found that the etching is temperature dependent and the etching of graphene at 800 oC is most efficient and anisotropic. 80% of the angles of graphene edges after etching are 120^o, indicating the etching is highly anisotropic. No increase of D band along the etched edges indicates that the crystallographic orientation of etching is zigzag direction. Furthermore, we observed that copper played an important role in catalyzing the etching reaction, as no etching was observed for graphene transferred to Si/SiO2 under similar conditions. This highly anisotropic hydrogen etching technology may work as a simple and convenient way to determine graphene crystal orientation and grain size, and may enable the etching of graphene into nanoribbons for electronic applications.

Photon bubbles and ion acceleration in a plasma dominated by the radiation pressure of an electromagnetic pulse.

PubMed

Pegoraro, F; Bulanov, S V

2007-08-10

The stability of a thin plasma foil accelerated by the radiation pressure of a high intensity electromagnetic (e.m.) pulse is investigated analytically and with particle in cell numerical simulations. It is shown that the onset of a Rayleigh-Taylor-like instability can lead to transverse bunching of the foil and to broadening of the energy spectrum of fast ions. The use of a properly tailored e.m. pulse with a sharp intensity rise can stabilize the foil acceleration.

Fabrication of rippled surfaces for diffraction gratings by plastic deformation of platinum foils and metallic glasses

NASA Astrophysics Data System (ADS)

Korsukov, V. E.; Malygin, G. A.; Korsukova, M. M.; Nyapshaev, I. A.; Obidov, B. A.

2015-12-01

Thin platinum foils and metallic glass ribbons with a fractal surface consisting of different-scale unidirectionally oriented ripples have been fabricated using special thermoplastic processing. The general fractal dimension of the rippled surface and dimensions along and across the ripples have been measured. The optical spectra of a PRK-4 lamp using rippled Pt(111) foils as reflective diffraction gratings have been determined. A model describing the mechanism of the formation of surface unidirectional fractal structures during deformation has been proposed.

Electric current heating calibration of a laser holographic nondestructive test system

NASA Technical Reports Server (NTRS)

Liu, H.-K.; Kurtz, R. L.

1975-01-01

Holographic NDT was used to measure small surface displacements controlled by electric heating by detecting the difference of the interference fringe patterns as viewed through the hologram on a real time basis. A perforated aluminum test plate, with the holes used to position thin metal foils, was used in the experiment. One of the foils was connected to an electric power source and small displacements of the foil were caused and controlled by Ohmic heating. An He-Ne laser was used to perform the holography.

Effects of the foil flatness on irradiation performance of U10Mo monolithic mini-plates

DOE PAGES

Ozaltun, Hakan; Medvedev, Pavel G.; Rabin, Barry H.

2015-09-03

Monolithic plate-type fuels comprise of a high density, low enrichment, U10Mo fuel foil encapsulated in a cladding material. This concept generates several fabrication challenges such as flatness, centering or thickness variation. There are concerns, if these parameters have implications on overall performance. To investigate these inquiries, the effects of the foil flatness were studied. For this, a representative plate was simulated for an ideal case. The simulations were repeated for additional cases with various foil curvatures to evaluate the effects on the irradiation performance. The results revealed that the stresses and strains induced by fabrication process are not affected bymore » the flatness of the foil. Furthermore, fabrication stresses in the foil are relieved relatively fast in the reactor. The effects of the foil flatness on peak irradiation stressstrains are minimal. There is a slight increase in temperature for the case with maximum curvature. The major impact is on the displacement characteristics. Furthermore, while the case with a flat foil produces a symmetrical swelling, if the foil is curved, more swelling occurs on the thin-cladding side and the plate bows during irradiation.« less

High temperature autoclave vacuum seals

NASA Technical Reports Server (NTRS)

Hoffman, J. R.; Simpson, W. G.; Walker, H. M.

1971-01-01

Aluminum sheet forms effective sealing film at temperatures up to 728 K. Soft aluminum wire rings provide positive seal between foil and platen. For applications at temperatures above aluminum's service temperature, stainless steel is used as film material and copper wire as sealant.

Fission fragment assisted reactor concept for space propulsion: Foil reactor

NASA Technical Reports Server (NTRS)

Wright, Steven A.

1991-01-01

The concept is to fabricate a reactor using thin films or foils of uranium, uranium oxide and then to coat them on substrates. These coatings would be made so thin as to allow the escaping fission fragments to directly heat a hydrogen propellant. The idea was studied of direct gas heating and direct gas pumping in a nuclear pumped laser program. Fission fragments were used to pump lasers. In this concept two substrates are placed opposite each other. The internal faces are coated with thin foil of uranium oxide. A few of the advantages of this technology are listed. In general, however, it is felt that if one look at all solid core nuclear thermal rockets or nuclear thermal propulsion methods, one is going to find that they all pretty much look the same. It is felt that this reactor has higher potential reliability. It has low structural operating temperatures, very short burn times, with graceful failure modes, and it has reduced potential for energetic accidents. Going to a design like this would take the NTP community part way to some of the very advanced engine designs, such as the gas core reactor, but with reduced risk because of the much lower temperatures.

Influence of barrier absorption properties on laser patterning thin organic films

NASA Astrophysics Data System (ADS)

Naithani, Sanjeev; Mandamparambil, Rajesh; van Assche, Ferdie; Schaubroeck, David; Fledderus, Henri; Prenen, An; Van Steenberge, Geert; Vanfleteren, Jan

2012-06-01

This paper presents a study of selective ablation of thin organic films (LEP- Light Emitting Polymer, PEDOT:PSS- Poly 3,4-ethylenedioxythiophene: polystyrene sulfonate) by using 248 nm Excimer laser, on various kinds of multilayered SiN barrier foils for the development of Organic Light Emitting Diodes (OLED). Different Silicon Nitride (SiN) barrier foils with dedicated absorption spectra are taken into account for this purpose. The drive for looking into different types of SiN originates from the fact that the laser selective removal of a polymer without damage to the barrier layer underneath is challenging in the dynamic laser processing of thin films. The barrier is solely responsible for the proper encapsulation of the OLED stack. The main limitation of current OLED design is its shorter life span, which is directly related to the moisture or water permeation into the stack, leading to black spots. An optimization of laser parameters like fluence and number of shots has been carried out for the various types of SiN barrier foils. We are able to obtain a wider working process window for the selective removal of LEP and PEDOT:PSS from SiN barrier, by variation of the different types of SiN.

Number distribution of emitted electrons by MeV H+ impact on carbon

NASA Astrophysics Data System (ADS)

Ogawa, H.; Koyanagi, Y.; Hongo, N.; Ishii, K.; Kaneko, T.

2017-09-01

The statistical distributions of the number of the forward- and backward-emitted secondary electrons (SE's) from a thin carbon foil have been measured in coincidence with foil-transmitted H+ ions of 0.5-3.0 MeV in every 0.5 MeV step. The measured SE energy spectra were fitted by assuming a Pólya distribution for the simultaneous n-SE emission probabilities. For our previous data with a couple of the carbon foils with different thicknesses, a similar analysis has been carried out. As a result, it was found that the measured spectra could be reproduced as well as by an analysis without placing any restriction on the emission probabilities both for the forward and backward SE emission. The obtained b-parameter of the Pólya distribution, which is a measure of the deviation from a Poisson distribution due to the cascade multiplication by high energy internal SE's, increases monotonically with the incident energy of proton beams. On the other hand, a clear foil-thickness dependence is not observed for the b-parameter. A theoretical model which could reproduced the magnitude of the b-parameter for the SE energy spectra obtained with thick Au, Cu and Al targets is found to overestimates our values for thin carbon foils significantly. Another model calculation is found to reproduce our b-values very well.

Flying-plate detonator using a high-density high explosive

DOEpatents

Stroud, John R.; Ornellas, Donald L.

1988-01-01

A flying-plate detonator containing a high-density high explosive such as benzotrifuroxan (BTF). The detonator involves the electrical explosion of a thin metal foil which punches out a flyer from a layer overlying the foil, and the flyer striking a high-density explosive pellet of BTF, which is more thermally stable than the conventional detonator using pentaerythritol tetranitrate (PETN).

How Thin Is Foil? Applying Density to Find the Thickness of Aluminum Foil

ERIC Educational Resources Information Center

Concannon, James P.

2011-01-01

In this activity, I show how high school students apply their knowledge of density to solve an unknown variable, such as thickness. Students leave this activity with a better understanding of density, the knowledge that density is a characteristic property of a given substance, and the ways density can be measured. (Contains 4 figures and 1 table.)

Creep analysis of solid oxide fuel cell with bonded compliant seal design

NASA Astrophysics Data System (ADS)

Jiang, Wenchun; Zhang, Yucai; Luo, Yun; Gong, J. M.; Tu, S. T.

2013-12-01

Solid oxide fuel cell (SOFC) requires good sealant because it works in harsh conditions (high temperature, thermal cycle, oxidative and reducing gas environments). Bonded compliant seal (BCS) is a new sealing method for planar SOFC. It uses a thin foil metal to bond the window frame and cell, achieving the seal between window frame and cell. At high temperature, a comprehensive evaluation of its creep strength is essential for the adoption of BCS design. In order to characterize the creep behavior, the creep induced by thermal stresses in SOFC with BCS design is simulated by finite element method. The results show that the foil is compressed and large thermal stresses are generated. The initial peak thermal stress is located in the thin foil because the foil acts as a spring stores the thermal stresses by elastic and plastic deformation in itself. Serving at high temperature, initial thermal displacement is partially recovered because of the creep relaxation, which becomes a new discovered advantage for BCS design. It predicts that the failures are likely to happen in the middle of the cell edge and BNi-2 filler metal, because the maximum residual displacement and creep strain are located.

Evaluation of selected thermal control coatings for long-life space structures

NASA Technical Reports Server (NTRS)

Teichman, Louis A.; Slemp, Wayne S.; Witte, William G., Jr.

1992-01-01

Graphite-reinforced resin matrix composites are being considered for spacecraft structural applications because of their light weight, high stiffness, and lower thermal expansion. Thin protective coatings with stable optical properties and the proper ratio of solar absorption (alpha sub s) to thermal emittance (epsilon) minimize orbital thermal extremes and protect these materials against space environment degradation. Sputtered coatings applied directly to graphite/epoxy composite surfaces and anodized coatings applied to thin aluminum foil were studied for use both as an atomic oxygen barrier and as thermal control coatings. Additional effort was made to develop nickel-based coatings which could be applied directly to composites. These coating systems were selected because their inherent tenacity made them potentially more reliable than commercial white paints for long-life space missions. Results indicate that anodized aluminum foil coatings are suitable for tubular and flat composite structures on large platforms in low Earth orbit. Anodized foil provides protection against some elements of the natural space environment (atomic oxygen, ultraviolet, and particulate radiation) and offers a broad range of tailored alpha sub s/epsilon. The foil is readily available and can be produced in large quantities, while the anodizing process is a routine commercial technique.

The BiPo-3 detector for the measurement of ultra low natural radioactivities of thin materials

NASA Astrophysics Data System (ADS)

Barabash, A. S.; Basharina-Freshville, A.; Birdsall, E.; Blondel, S.; Blot, S.; Bongrand, M.; Boursette, D.; Brudanin, V.; Busto, J.; Caffrey, A. J.; Calvez, S.; Cascella, M.; Cebrián, S.; Cerna, C.; Cesar, J. P.; Chauveau, E.; Chopra, A.; Dafní, T.; De Capua, S.; Duchesneau, D.; Durand, D.; Egorov, V.; Eurin, G.; Evans, J. J.; Fajt, L.; Filosofov, D.; Flack, R.; Garrido, X.; Gómez, H.; Guillon, B.; Guzowski, P.; Holý, K.; Hodák, R.; Huber, A.; Hugon, C.; Iguaz, F. J.; Irastorza, I. G.; Jeremie, A.; Jullian, S.; Kauer, M.; Klimenko, A.; Kochetov, O.; Konovalov, S. I.; Kovalenko, V.; Lang, K.; Lemière, Y.; Le Noblet, T.; Liptak, Z.; Liu, X. R.; Loaiza, P.; Lutter, G.; Luzón, G.; Macko, M.; Mamedov, F.; Marquet, C.; Mauger, F.; Morgan, B.; Mott, J.; Nemchenok, I.; Nomachi, M.; Nova, F.; Ohsumi, H.; Oliviéro, G.; Ortiz de Solórzano, A.; Pahlka, R. B.; Pater, J.; Perrot, F.; Piquemal, F.; Povinec, P.; Přidal, P.; Ramachers, Y. A.; Remoto, A.; Richards, B.; Riddle, C. L.; Rukhadze, E.; Saakyan, R.; Salazar, R.; Sarazin, X.; Shitov, Yu.; Simard, L.; Šimkovic, F.; Smetana, A.; Smolek, K.; Smolnikov, A.; Söldner-Rembold, S.; Soulé, B.; Štekl, I.; Thomas, J.; Timkin, V.; Torre, S.; Tretyak, Vl. I.; Tretyak, V. I.; Umatov, V. I.; Vilela, C.; Vorobel, V.; Waters, D.; Žukauskas, A.

2017-06-01

The BiPo-3 detector, running at the Canfranc Underground Laboratory (Laboratorio Subterr&aposaneo de Canfranc, LSC, Spain) since 2013, is a low-radioactivity detector dedicated to measuring ultra low natural radionuclide contaminations of 208Tl (232Th chain) and 214Bi (238U chain) in thin materials. The total sensitive surface area of the detector is 3.6 m2. The detector has been developed to measure the radiopurity of the selenium double β-decay source foils of the SuperNEMO experiment. In this paper the design and performance of the detector, and results of the background measurements in 208Tl and 214Bi, are presented, and the validation of the BiPo-3 measurement with a calibrated aluminium foil is discussed. Results of the 208Tl and 214Bi activity measurements of the first enriched 82Se foils of the double β-decay SuperNEMO experiment are reported. The sensitivity of the BiPo-3 detector for the measurement of the SuperNEMO 82Se foils is Script A(208Tl) <2 μBq/kg (90% C.L.) and Script A(214Bi) <140 μBq/kg (90% C.L.) after 6 months of measurement.

High-performance coaxial EPR cavity for investigations at elevated temperatures and pressures

NASA Astrophysics Data System (ADS)

Goldberg, Ira B.; McKinney, Ted M.

1984-07-01

A microwave cavity suitable for heating a sample to temperatures above 800 °C within 15 s at gas pressures above 17.5 MPa is reported. The cavity is coaxial and operates in the TE011 mode at frequencies between 9 and 10 GHz. The heating element is constructed of nickel-chromium (i.e., Chromel) wire. It consists of two concentric helices wound in opposite senses (directions) and connected in series so as to minimize the magnetic field generated by the heater current. The heater is potted in magnesium oxide-phosphate ceramic and placed inside of a cylinder made from 50-μm copper foil which provides uniform temperature distribution and shields the heater from the microwave field. This assembly then serves as the heating element and the coaxial conductor of the cavity. The diameter of the coaxial heater assembly is approximately 7 mm. The sample is confined by a cylindrical quartz cuvette which surrounds the coaxial conductor. Sample thicknesses of 0.2 to 1.0 mm can be used. Heating from room temperature to 800 °C requires between 15 and 20 s. Operating pressures up to 17 MPa have been used, although the structural design limit of the brass or beryllium copper walls is greater than 22 MPa. Modulation coils are placed in recessed areas of the cavity walls and covered with a thin layer of copper. Cooling water flows through channels cut into the walls to maintain constant microwave parameters. Q factors of 8000 -12 000 can be obtained depending on the sample.

Slumped glass foils as substrate for adjustable x-ray optics

NASA Astrophysics Data System (ADS)

Salmaso, Bianca; Basso, Stefano; Civitani, Marta; Ghigo, Mauro; Hołyszko, Joanna; Pelliciari, Carlo; Spiga, Daniele; Vecchi, Gabriele; Pareschi, Giovanni

2016-09-01

Thin glass modular mirrors are a viable solution to build future X-ray telescopes with high angular resolution and large collecting area. In our laboratories, we shape thin glass foils by hot slumping and we apply pressure to assist the replication of a cylindrical mould figure; this technology is coupled with an integration process able to damp low frequency errors and produces optics in the Wolter I configuration, typical for the X-ray telescopes. From the point of view of the hot slumping process, the efforts were focused in reducing low-, mid- and high- frequency errors of the formed Eagle glass foils. Some of our slumped glass foils were used for the development of active X-ray optics, where piezoelectric actuators are used to correct the slumped glass foil deviations from the ideal shape. In particular, they were used for the Adjustable X-raY optics for astrOnoMy project (AXYOM) developed in Italy, and the X-ray Surveyor mission, as developed at the Smithsonian Astrophysical Observatory / Center for Astrophysics (SAO/CfA) in USA. In this paper we describe the optimisation of the hot slumping process, comparing the results with the requirements of the considered active optics projects. Finally, since the present configuration of the Pennsylvania State University (PSU) coating equipment is limited to 100 x 100 mm2, the slumped glass foils used for the SAO project were cut from 200 x 200 mm2 to 100 x 100 mm2, and a low-frequency change was observed. A characterisation of the profile change upon cutting is presented.

Analytic Modeling of the Hydrodynamic, Thermal, and Structural Behavior of Foil Thrust Bearings

NASA Technical Reports Server (NTRS)

Bruckner, Robert J.; DellaCorte, Christopher; Prahl, Joseph M.

2005-01-01

A simulation and modeling effort is conducted on gas foil thrust bearings. A foil bearing is a self acting hydrodynamic device capable of separating stationary and rotating components of rotating machinery by a film of air or other gaseous lubricant. Although simple in appearance these bearings have proven to be complicated devices in analysis. They are sensitive to fluid structure interaction, use a compressible gas as a lubricant, may not be in the fully continuum range of fluid mechanics, and operate in the range where viscous heat generation is significant. These factors provide a challenge to the simulation and modeling task. The Reynolds equation with the addition of Knudsen number effects due to thin film thicknesses is used to simulate the hydrodynamics. The energy equation is manipulated to simulate the temperature field of the lubricant film and combined with the ideal gas relationship, provides density field input to the Reynolds equation. Heat transfer between the lubricant and the surroundings is also modeled. The structural deformations of the bearing are modeled with a single partial differential equation. The equation models the top foil as a thin, bending dominated membrane whose deflections are governed by the biharmonic equation. A linear superposition of hydrodynamic load and compliant foundation reaction is included. The stiffness of the compliant foundation is modeled as a distributed stiffness that supports the top foil. The system of governing equations is solved numerically by a computer program written in the Mathematica computing environment. Representative calculations and comparisons with experimental results are included for a generation I gas foil thrust bearing.

High efficiency graphene coated copper based thermocells connected in series

NASA Astrophysics Data System (ADS)

Sindhuja, Mani; Indubala, Emayavaramban; Sudha, Venkatachalam; Harinipriya, Seshadri

2018-04-01

Conversion of low-grade waste heat into electricity had been studied employing single thermocell or flowcells so far. Graphene coated copper electrodes based thermocells connected in series displayed relatively high efficiency of thermal energy harvesting. The maximum power output of 49.2W/m2 for normalized cross sectional electrode area is obtained at 60ºC of inter electrode temperature difference. The relative carnot efficiency of 20.2% is obtained from the device. The importance of reducing the mass transfer and ion transfer resistance to improve the efficiency of the device is demonstrated. Degradation studies confirmed mild oxidation of copper foil due to corrosion caused by the electrolyte.

Exploring electronic structure of one-atom thick polycrystalline graphene films: A nano angle resolved photoemission study

PubMed Central

Avila, José; Razado, Ivy; Lorcy, Stéphane; Fleurier, Romain; Pichonat, Emmanuelle; Vignaud, Dominique; Wallart, Xavier; Asensio, María C.

2013-01-01

The ability to produce large, continuous and defect free films of graphene is presently a major challenge for multiple applications. Even though the scalability of graphene films is closely associated to a manifest polycrystalline character, only a few numbers of experiments have explored so far the electronic structure down to single graphene grains. Here we report a high resolution angle and lateral resolved photoelectron spectroscopy (nano-ARPES) study of one-atom thick graphene films on thin copper foils synthesized by chemical vapor deposition. Our results show the robustness of the Dirac relativistic-like electronic spectrum as a function of the size, shape and orientation of the single-crystal pristine grains in the graphene films investigated. Moreover, by mapping grain by grain the electronic dynamics of this unique Dirac system, we show that the single-grain gap-size is 80% smaller than the multi-grain gap recently reported by classical ARPES. PMID:23942471

Building A New Kind of Graded-Z Shield for Swift's Burst Alert Telescope

NASA Technical Reports Server (NTRS)

Robinson, David W.

2002-01-01

The Burst Alert Telescope (BAT) on Swift has a graded-Z Shield that closes out the volume between the coded aperture mask and the Cadmium-Zinc-Telluride (CZT) detector array. The purpose of the 37 kilogram shield is to attenuate gamma rays that have not penetrated the coded aperture mask of the BAT instrument and are therefore a major source of noise on the detector array. Unlike previous shields made from plates and panels, this shield consists of multiple layers of thin metal foils (lead, tantalum, tin, and copper) that are stitched together much like standard multi-layer insulation blankets. The shield sections are fastened around BAT, forming a curtain around the instrument aperture. Strength tests were performed to validate and improve the design, and the shield will be vibration tested along with BAT in late 2002. Practical aspects such as the layup design, methods of manufacture, and testing of this new kind of graded-Z Shield are presented.

Inspection of cup-shaped steel parts from the I.D. side using eddy current

NASA Astrophysics Data System (ADS)

Griffiths, Erick W.; Pearson, Lee H.

2018-04-01

An eddy current method was developed to inspect cup-shaped steel parts from the I.D. side. During the manufacturing process of these parts, a thin Al tape foil is applied to the I.D. side of the part. One of the critical process parameters is that only one foil layer can be applied. An eddy current inspection system was developed to reject parts with more than one foil layer. The Al tape foil is cut to length to fit the inner diameter, however, after application of the foil there is a gap created between the beginning and end of the foil. It was found that this gap interfered with the eddy current inspection causing a false positive indication. To solve this problem a sensor design and data analysis process were developed to overcome the effects of these gaps. The developed system incorporates simultaneous measurements from multiple eddy current sensors and signal processing to achieve a reliable inspection.

The Chevron Foil Thrust Bearing: Improved Performance Through Passive Thermal Management and Effective Lubricant Mixing

NASA Technical Reports Server (NTRS)

Bruckner, Robert

2013-01-01

An improved foil thrust bearing is described that eliminates or reduces the need for forced cooling of the bearing foils while at the same time improves the load capacity of the bearing, enhances damping, provides overload tolerance, and eliminates the high speed load capacity drop-off that plagues the current state of the art. The performance improvement demonstrated by the chevron foil thrust bearing stems from a novel trailing edge shape that splays the hot lubricant in the thin film radially, thus preventing hot lubricant carry-over into the ensuing bearing sector. Additionally, the chevron shaped trailing edge induces vortical mixing of the hot lubricant with the gas that is naturally resident within the inter-pad region of a foil thrust bearing. The elimination of hot gas carry-over in combination with the enhanced mixing has enabled a completely passive thermally managed foil bearing design. Laboratory testing at NASA has confirmed the original analysis and reduced this concept to practice.

Improved composite targets for small scale 64Cu production comparing Au- and Pt-foils as 64Ni backing

NASA Astrophysics Data System (ADS)

Walther, M.; Preusche, S.; Fuechtner, F.; Pietzsch, H. J.; Steinbach, J.

2012-12-01

Advantages of a stacked assembly of target support components for 64Cu production via 64Ni(p,n)64Cu reaction were reported recently. The present work shows the applicability of these composite targets for beam currents up to 22 μA. Gold and platinum foils were evaluated as 64Ni backing. The effective specific activity (ESA) and specific activity (SA) were determined by TETA titration at room temperature and at 80 °C and compared with additional copper quantification results via ICP-MS and stripping voltammetric trace analysis (VA).

Supercapacitors based on pillared graphene nanostructures.

PubMed

Lin, Jian; Zhong, Jiebin; Bao, Duoduo; Reiber-Kyle, Jennifer; Wang, Wei; Vullev, Valentine; Ozkan, Mihrimah; Ozkan, Cengiz S

2012-03-01

We describe the fabrication of highly conductive and large-area three dimensional pillared graphene nanostructure (PGN) films from assembly of vertically aligned CNT pillars on flexible copper foils for applications in electric double layer capacitors (EDLC). The PGN films synthesized via a one-step chemical vapor deposition process on flexible copper foils exhibit high conductivity with sheet resistance as low as 1.6 ohms per square and possessing high mechanical flexibility. Raman spectroscopy indicates the presence of multi walled carbon nanotubes (MWCNT) and their morphology can be controlled by the growth conditions. It was discovered that nitric acid treatment can significantly increase the specific capacitance of the devices. EDLC devices based on PGN electrodes (surface area of 565 m2/g) demonstrate enhanced performance with specific capacitance value as high as 330 F/g extracted from the current density-voltage (CV) measurements and energy density value of 45.8 Wh/kg. The hybrid graphene-CNT nanostructures are attractive for applications including supercapacitors, fuel cells and batteries.

Effects of temperature and holding time on bonding W and W-Cu composites with an amorphous W-Fe coated copper foil as the interlayer by hot-pressing

NASA Astrophysics Data System (ADS)

Zhao, Pei; Wang, Song; Guo, Shibin; Chen, Yixiang; Ling, Yunhan; Li, Jiangtao

2013-07-01

W and W-Cu composites were bonded with an amorphous W-Fe coated copper foil as the interlayer at different temperature and holding time by hot pressing method. Effects of the bonding temperature and holding time on the microstructure and thermal conductivity of the bonded specimens were investigated. The thermal conductivity of the bonded sample increased with the bonding temperature and reached the maximum at 1000 °C, but essentially unchanged with the holding time. Because at 1000 °C more W-Fe compounds would be formed at the interlayer, which were helpful for tight bonding of W and W-Cu composites, and the grain size was larger which could reduce thermal resistance. The W-Cu FGM bonded by this method showed good resistance to thermal load, and performed well when facing to short pulse plasma in experimental advanced superconducting tokamak (the first full superconductive fusion device in the world).

Synthesis and characterization of Copper/Cobalt/Copper/Iron nanostructurated films with magnetoresistive properties

NASA Astrophysics Data System (ADS)

Ciupinǎ, Victor; Prioteasa, Iulian; Ilie, Daniela; Manu, Radu; Petrǎşescu, Lucian; Tutun, Ştefan Gabriel; Dincǎ, Paul; MustaÅ£ǎ, Ion; Lungu, Cristian Petricǎ; Jepu, IonuÅ£; Vasile, Eugeniu; Nicolescu, Virginia; Vladoiu, Rodica

2017-02-01

Copper/Cobalt/Copper/Iron thin films were synthesized in order to obtain nanostructured materials with special magnetoresistive properties. The multilayer films were deposited on silicon substrates. In this respect we used Thermionic Vacuum Arc Discharge Method (TVA). The benefit of this deposition technique is the ability to have a controlled range of thicknesses starting from few nanometers to hundreds of nanometers. The purity of the thin films was insured by a high vacuum pressure and a lack of any kind of buffer gas inside the coating chamber. The morphology and structure of the thin films were analyzed using Scanning Electron Microscopy (SEM) and Transmission Electron Microscopy (TEM) Techniques and Energy Dispersive X-ray Spectroscopy (EDXS). Magnetoresistive measurement results depict that thin films possess Giant Magneto-Resistance Effect (GMR). Magneto-Optic-Kerr Effect (MOKE) studies were performed to characterize the magnetic properties of these thin films.

Polyelectrolyte-mediated assembly of copper-phthalocyanine tetrasulfonate multilayers and the subsequent production of nanoparticulate copper oxide thin films.

PubMed

Chickneyan, Zarui Sara; Briseno, Alejandro L; Shi, Xiangyang; Han, Shubo; Huang, Jiaxing; Zhou, Feimeng

2004-07-01

An approach to producing films of nanometer-sized copper oxide particulates, based on polyelectrolyte-mediated assembly of the precursor, copper(II)phthalocyanine tetrasulfonate (CPTS), is described. Multilayered CPTS and polydiallyldimethylammonium chloride (PDADMAC) were alternately assembled on different planar substrates via the layer-by-layer (LbL) procedure. The growth of CPTS multilayers was monitored by UV-visible spectrometry and quartz crystal microbalance (QCM) measurements. Both the UV-visible spectra and the QCM data showed that a fixed amount of CPTS could be attached to the substrate surface for a given adsorption cycle. Cyclic voltammograms at the CPTS/PDADMAC-covered gold electrode exhibited a decrease in peak currents with the layer number, indicating that the permeability of CPTS multilayers on the electrodes had diminished. When these CPTS multilayered films were calcined at elevated temperatures, uniform thin films composed of nanoparticulate copper oxide could be produced. Ellipsometry showed that the thickness of copper oxide nanoparticulate films could be precisely tailored by varying the thickness of CPTS multilayer films. The morphology and roughness of CPTS multilayer and copper oxide thin films were characterized by atomic force microscopy. X-ray diffraction (XRD) measurements indicated that these thin films contained both CuO and Cu2O nanoparticles. The preparation of such copper oxide thin films with the use of metal complex precursors represents a new route for the synthesis of inorganic oxide films with a controlled thickness.

The possibility of using platinum foils with a rippled surface as diffraction gratings

NASA Astrophysics Data System (ADS)

Korsukov, V. E.; Ankudinov, A. V.; Butenko, P. N.; Knyazev, S. A.; Korsukova, M. M.; Obidov, B. A.; Shcherbakov, I. P.

2014-09-01

The atomic structure and surface relief of thin cold-rolled platinum foils upon recrystallization annealing and loading under ultrahigh vacuum conditions have been studied by low energy electron diffraction (LEED), atomic force microscopy (AFM), and scanning tunneling microscopy (STM). The surface of samples upon high-temperature annealing and subsequent uniaxial extension of recrystallized Pt foils represents a fractal structure of unidirectional ripples on various spatial scales. The total fractal dimension of this surface is D GW = 2.3, while the fractal dimensions along and across ripples are D ‖ ≈ 1 and D ⊥ ≈ 1.3, respectively. The optical spectra of a halogen lamp and a PRK-2 mercury lamp were recorded using these rippled Pt foils as reflection diffraction gratings. It is shown that Pt foils with this surface relief can be used as reflection diffraction gratings for electromagnetic radiation in a broad spectral range.

Development of Accurate Structure for Mounting and Aligning Thin-Foil X-Ray Mirrors

NASA Technical Reports Server (NTRS)

Heilmann, Ralf K.

2001-01-01

The goal of this work was to improve the assembly accuracy for foil x-ray optics as produced by the high-energy astrophysics group at the NASA Goddard Space Flight Center. Two main design choices lead to an alignment concept that was shown to improve accuracy well within the requirements currently pursued by the Constellation-X Spectroscopy X-Ray Telescope (SXT).

Investigation of the 68Zn(p, 2p) 67Cu nuclear reaction: New measurements up to 40 MeV and compilation up to 100 MeV

NASA Astrophysics Data System (ADS)

Szelecsényi, F.; Steyn, G. F.; Dolley, S. G.; Kovács, Z.; Vermeulen, C.; van der Walt, T. N.

2009-06-01

The excitation function was measured for the 68Zn(p, 2p) 67Cu nuclear reaction from its threshold energy up to 40 MeV. Nine pieces of highly enriched 68Zn (>98%) metal foils were irradiated to obtain reliable cross-sections using the usual stacked-foil technique. All foils were subjected to high efficiency radiochemical separation before the activity measurements. A critical compilation of the available experimental cross-section results was also performed. Thick target yields of 67Cu and the longer-lived copper radio-contaminants ( 61Cu and 64Cu) were calculated using the reliable literature results up to 100 MeV. Additionally, EOB (End Of Bombardment) contamination levels as a function of bombarding energy and irradiation time were deduced.

The stopping powers and energy straggling of heavy ions in polymer foils

NASA Astrophysics Data System (ADS)

Mikšová, R.; Macková, A.; Malinský, P.; Hnatowicz, V.; Slepička, P.

2014-07-01

The stopping power and energy straggling of 7Li, 12C and 16O ions in thin poly(etheretherketone) (PEEK), polyethylene terephthalate (PET) and polycarbonate (PC) foils were measured in the incident beam energy range of 9.4-11.8 MeV using an indirect transmission method. Ions scattered from a thin gold target at an angle of 150° were registered by a partially depleted PIPS detector, partly shielded with a polymer foil placed in front of the detector. Therefore, the signals from both direct and slowed down ions were visible in the same energy spectrum, which was evaluated by the ITAP code, developed at our laboratory. The ITAP code was employed to perform a Gaussian-fitting procedure to provide a complete analysis of each measured spectrum. The measured stopping powers were compared with the predictions obtained from the SRIM-2008 and MSTAR codes and with previous experimental data. The energy straggling data were compared with those calculated by using Bohr's, Lindhard-Scharff and Bethe-Livingston theories.

Suppression of copper thin film loss during graphene synthesis.

PubMed

Lee, Alvin L; Tao, Li; Akinwande, Deji

2015-01-28

Thin metal films can be used to catalyze the growth of nanomaterials in place of the bulk metal, while greatly reducing the amount of material used. A big drawback of copper thin films (0.5-1.5 μm thick) is that, under high temperature/vacuum synthesis, the mass loss of films severely reduces the process time due to discontinuities in the metal film, thereby limiting the time scale for controlling metal grain and film growth. In this work, we have developed a facile method, namely "covered growth" to extend the time copper thin films can be exposed to high temperature/vacuum environment for graphene synthesis. The key to preventing severe mass loss of copper film during the high temperature chemical vapor deposition (CVD) process is to have a cover piece on top of the growth substrate. This new "covered growth" method enables the high-temperature annealing of the copper film upward of 4 h with minimal mass loss, while increasing copper film grain and graphene domain size. Graphene was then successfully grown on the capped copper film with subsequent transfer for device fabrication. Device characterization indicated equivalent physical, chemical, and electrical properties to conventional CVD graphene. Our "covered growth" provides a convenient and effective solution to the mass loss issue of thin films that serve as catalysts for a variety of 2D material syntheses.

Process Of Bonding Copper And Tungsten

DOEpatents

Slattery, Kevin T.; Driemeyer, Daniel E.; Davis, John W.

2000-07-18

Process for bonding a copper substrate to a tungsten substrate by providing a thin metallic adhesion promoting film bonded to a tungsten substrate and a functionally graded material (FGM) interlayer bonding the thin metallic adhesion promoting film to the copper substrate. The FGM interlayer is formed by sintering a stack of individual copper and tungsten powder blend layers having progressively higher copper content/tungsten content, by volume, ratio values in successive powder blend layers in a lineal direction extending from the tungsten substrate towards the copper substrate. The resulting copper to tungsten joint well accommodates the difference in the coefficient of thermal expansion of the materials.

Highly periodic laser-induced nanostructures on thin Ti and Cu foils for potential application in laser ion acceleration

DOE Office of Scientific and Technical Information (OSTI.GOV)

Das, Susanta Kumar, E-mail: skdasfpy@kiit.ac.in; Andreev, Alexander; Braenzel, Julia

2016-03-21

The feasibility of femtosecond laser-induced periodic nanostructures on thin Ti and Cu foils (thickness down to 1 μm) is demonstrated. At pulse durations of 120 fs and a wavelength of 400 nm, periods of 61 nm to 320 nm were obtained. Particle-in-cell simulations of laser ion acceleration processes with such nanostructured targets indicate their potential for high energy particle physics applications. In particular, a measurable enhancement of the proton cut-off energy and a significant enhancement of the number of accelerated particles compared to non- or weakly structured targets of same thickness and material are expected.

Adapalene

MedlinePlus

... or cream, use your fingers to spread a thin film of medication over the affected area. If you are using a pledget, remove it from the foil pouch and gently wipe the affected area. If you are using the glass bottle of solution, apply a thin layer to the affected area using the applicator ...

{001} Oriented piezoelectric films prepared by chemical solution deposition on Ni foils

NASA Astrophysics Data System (ADS)

Yeo, Hong Goo; Trolier-McKinstry, Susan

2014-07-01

Flexible metal foil substrates are useful in some microelectromechanical systems applications including wearable piezoelectric sensors or energy harvesters based on Pb(Zr,Ti)O3 (PZT) thin films. Full utilization of the potential of piezoelectrics on metal foils requires control of the film crystallographic texture. In this study, {001} oriented PZT thin films were grown by chemical solution deposition (CSD) on Ni foil and Si substrates. Ni foils were passivated using HfO2 grown by atomic layer deposition in order to suppress substrate oxidation during subsequent thermal treatment. To obtain the desired orientation of PZT film, strongly (100) oriented LaNiO3 films were integrated by CSD on the HfO2 coated substrates. A high level of {001} LaNiO3 and PZT film orientation were confirmed by X-ray diffraction patterns. Before poling, the low field dielectric permittivity and loss tangents of (001) oriented PZT films on Ni are near 780 and 0.04 at 1 kHz; the permittivity drops significantly on poling due to in-plane to out-of-plane domain switching. (001) oriented PZT film on Ni displayed a well-saturated hysteresis loop with a large remanent polarization ˜36 μC/cm2, while (100) oriented PZT on Si showed slanted P-E hysteresis loops with much lower remanent polarizations. The |e31,f| piezoelectric coefficient was around 10.6 C/m2 for hot-poled (001) oriented PZT film on Ni.

Handheld Reflective Foil Emissometer with 0.007 Absolute Accuracy at 0.05

NASA Astrophysics Data System (ADS)

van der Ham, E. W. M.; Ballico, M. J.

2014-07-01

The development and performance of a handheld emissometer for the measurement of the emissivity of highly reflective metallic foils used for the insulation of domestic and commercial buildings are described. Reflective roofing insulation based on a thin coating of metal on a more robust substrate is very widely used in hotter climates to reduce the radiant heat transfer between the ceiling and roof in commercial and residential buildings. The required normal emissivity of these foils is generally below 0.05, so stray reflected ambient infrared radiation (IR) makes traditional reflectance-based measurements of emissivity very difficult to achieve with the required accuracy. Many manufacturers apply additional coatings onto the metallic foil to reduce visible glare during installation on a roof, and to provide protection to the thin reflective layer; however, this layer can also substantially increase the IR emissivity. The system as developed at the National Measurement Institute, Australia (NMIA) is based on the principle of measurement of the modulation in thermal infrared radiation, as the sample is thermally modulated by hot and cold air streams. A commercial infrared to band radiation thermometer with a highly specialized stray and reflected radiation shroud attachment is used as the detector system, allowing for convenient handheld field measurements. The performance and accuracy of the system have been compared with NMIA's reference emissometer systems for a number of typical material samples, demonstrating its capability to measure the absolute thermal emissivity of these very highly reflective foils with an uncertainty of better than.

Polymer gel dosimetry for measuring the dose near thin high-Z materials irradiated with high energy photon beams.

PubMed

Warmington, Leighton L; Gopishankar, N; Broadhurst, John H; Watanabe, Yoichi

2016-12-01

To investigate the feasibility of three-dimensional (3D) dose measurements near thin high-Z materials placed in a water-like medium by using a polymer gel dosimeter (PGD) when the medium was irradiated with high energy photon beams. PGD is potentially a useful tool for this application because it can record the dose around a small object made of a high-Z material in a continuous 3D medium. In this study, the authors manufactured a methacrylic acid-based normoxic PGD, nMAG. Two 0.5 mm thick lead foils (1 × 1 cm) were placed in foil supports with 0.7 cm separation in a 1000 ml polystyrene container filled with nMAG. The authors used two foil configurations, i.e., orthogonal and parallel. In the orthogonal configuration, two foils were placed in the direction orthogonal to the beam axis. The parallel configuration had two foils arranged in parallel to the beam axis. The phantom was irradiated with an 18 MV photon beam of 5 × 5 cm field size. It was imaged with a three-Tesla (3 T) magnetic resonance imaging (MRI) scanned using the Car-Purcell-Meiboom-Gill pulse sequence. The spin-spin relaxation time (R2) to-dose calibration data were obtained by using small vials filled with nMAG and exposing to known doses. The DOSXYZnrc Monte Carlo (MC) code was used to get the expected dose distributions. More than 35 × 10 6 of histories were simulated so that the average error was less than 1%. An in-house matlab-based software was used to obtain the dose distributions from the measured R2 data as well as to compare the measurements and the MC predictions. The dose change due to the presence of the foils was studied by comparing the dose distributions with and without foils (or the reference). For the orthogonal configuration, the measured dose along the beam axis showed an increase in the upstream side of the first foil, between the foils, and on the downstream side of the second foil. The range of increased dose area was 1.1 cm in the upstream of the first foil. However, in the downstream of the second foil, it was 0.2 cm, beyond which the dose fell below the reference dose by 10%. The dose profile between the foils showed a well-like shape with the minimum dose still larger than the reference dose by 1.8%. The minimum dose point was closer to the first foil than to the second foil. For the parallel configuration, the dose between foils was the largest at the center. The increased dose area opposite to the gap between foils extended outward to 1 cm. The spatial dose distributions of PGD and MC showed the same geometrical patterns except for the points inside the foils for both orthogonal and parallel foil arrangements. The authors demonstrated that the nMAG PGD with MRI could be used to measure the 3D dosimetric structures at the mm-scale in the vicinity of the foil. The current study provided more accurate 3D spatial dose distribution than the previous studies. Furthermore, the measurements were validated by the MC simulation.

Investigation of the crater-like microdefects induced by laser shock processing with aluminum foil as absorbent layer

NASA Astrophysics Data System (ADS)

Ye, Y. X.; Xuan, T.; Lian, Z. C.; Feng, Y. Y.; Hua, X. J.

2015-06-01

This paper reports that 3D crater-like microdefects form on the metal surface when laser shock processing (LSP) is applied. LSP was conducted on pure copper block using the aluminum foil as the absorbent material and water as the confining layer. There existed the bonding material to attach the aluminum foil on the metal target closely. The surface morphologies and metallographs of copper surfaces were characterized with 3D profiler, the optical microscopy (OM) or the scanning electron microscopy (SEM). Temperature increases of metal surface due to LSP were evaluated theoretically. It was found that, when aluminum foil was used as the absorbent material, and if there existed air bubbles in the bonding material, the air temperatures within the bubbles rose rapidly because of the adiabatic compression. So at the locations of the air bubbles, the metal materials melted and micromelting pool formed. Then under the subsequent expanding of the air bubbles, a secondary shock wave was launched against the micromelting pool and produced the crater-like microdefects on the metal surface. The temperature increases due to shock heat and high-speed deformation were not enough to melt the metal target. The temperature increase induced by the adiabatic compression of the air bubbles may also cause the gasification of the metal target. This will also help form the crater-like microdefects. The results of this paper can help to improve the surface quality of a metal target during the application of LSP. In addition, the results provide another method to fabricate 3D crater-like dents on metal surface. This has a potential application in mechanical engineering.

Design and evaluation of thin metal surface insulation for hypersonic flight

NASA Technical Reports Server (NTRS)

Miller, R. C.; Petach, A. M.

1976-01-01

An all-metal insulation was studied as a thermal protection system for hypersonic vehicles. Key program goals included fabricating the insulation in thin packages which are optimized for high temperature insulation of an actively cooled aluminum structure, and the use of state-of-the-art alloys. The insulation was fabricated from 300 series stainless steel in thicknesses of 0.8 to 12 mm. The outer, 0.127 mm thick, skin was textured to accommodate thermal expansion and oxidized to increase emittance. The thin insulating package was achieved using an insulation concept consisting of foil radiation shields spaced within the package, and conical foil supports to carry loads from the skin and maintain package dimensions. Samples of the metal-insulation were tested to evaluate thermal insulation capability, rain and sand erosion resistance, high temperature oxidation resistance, applied load capability, and high temperature emittance.

Design and Development of Thin Plastic Foil, Conical Approximation, High Through-out X-Ray Telescope: Light Weight, Thin Plastic Foil, X-Ray Telescopes

NASA Technical Reports Server (NTRS)

Schnopper, Herbert W.; Barbera, Marco; Silver, Eric; Ingram, Russell; Christensen, Finn E.; Romaine, Suzanne; Cohen, Lester; Collura, Alfonso; Murray, Stephen S.; Brinton, John C. (Technical Monitor)

2002-01-01

We present results from a program to develop an X-ray telescope made from thin plastic shells. Our initial results have been obtained from multi-shell cylindrical lenses that are used in a point-to-point configuration to image the small focal spot of a an X-ray tube on a microchannel plate detector. We describe the steps that led up to the present design and present data from the tests that have been used to identify the properties of the plastic material that make it a suitable X-ray reflector. We discuss two applications of our technology to X-ray missions that are designed to address some of the scientific priorities set forth in NASA's long term plans for high energy astrophysics. One mission will observe in the 1 - 10 keV band, the other will extend up to ca. 100 keV.

Microstructure based procedure for process parameter control in rolling of aluminum thin foils

NASA Astrophysics Data System (ADS)

Johannes, Kronsteiner; Kabliman, Evgeniya; Klimek, Philipp-Christoph

2018-05-01

In present work, a microstructure based procedure is used for a numerical prediction of strength properties for Al-Mg-Sc thin foils during a hot rolling process. For this purpose, the following techniques were developed and implemented. At first, a toolkit for a numerical analysis of experimental stress-strain curves obtained during a hot compression testing by a deformation dilatometer was developed. The implemented techniques allow for the correction of a temperature increase in samples due to adiabatic heating and for the determination of a yield strength needed for the separation of the elastic and plastic deformation regimes during numerical simulation of multi-pass hot rolling. At the next step, an asymmetric Hot Rolling Simulator (adjustable table inlet/outlet height as well as separate roll infeed) was developed in order to match the exact processing conditions of a semi-industrial rolling procedure. At each element of a finite element mesh the total strength is calculated by in-house Flow Stress Model based on evolution of mean dislocation density. The strength values obtained by numerical modelling were found in a reasonable agreement with results of tensile tests for thin Al-Mg-Sc foils. Thus, the proposed simulation procedure might allow to optimize the processing parameters with respect to the microstructure development.

Effects of etchants in the transfer of chemical vapor deposited graphene

NASA Astrophysics Data System (ADS)

Wang, M.; Yang, E. H.; Vajtai, R.; Kono, J.; Ajayan, P. M.

2018-05-01

The quality of graphene can be strongly modified during the transfer process following chemical vapor deposition (CVD) growth. Here, we transferred CVD-grown graphene from a copper foil to a SiO2/Si substrate using wet etching with four different etchants: HNO3, FeCl3, (NH4)2S2O8, and a commercial copper etchant. We then compared the quality of graphene after the transfer process in terms of surface modifications, pollutions (residues and contaminations), and electrical properties (mobility and density). Our tests and analyses showed that the commercial copper etchant provides the best structural integrity, the least amount of residues, and the smallest doping carrier concentration.

Decomposition of poly(amide-imide) film enameled on solid copper wire using atmospheric pressure non-equilibrium plasma.

PubMed

Sugiyama, Kazuo; Suzuki, Katsunori; Kuwasima, Shusuke; Aoki, Yosuke; Yajima, Tatsuhiko

2009-01-01

The decomposition of a poly(amide-imide) thin film coated on a solid copper wire was attempted using atmospheric pressure non-equilibrium plasma. The plasma was produced by applying microwave power to an electrically conductive material in a gas mixture of argon, oxygen, and hydrogen. The poly(amide-imide) thin film was easily decomposed by argon-oxygen mixed gas plasma and an oxidized copper surface was obtained. The reduction of the oxidized surface with argon-hydrogen mixed gas plasma rapidly yielded a metallic copper surface. A continuous plasma heat-treatment process using a combination of both the argon-oxygen plasma and argon-hydrogen plasma was found to be suitable for the decomposition of the poly(amide-imide) thin film coated on the solid copper wire.

Spot size dependence of laser accelerated protons in thin multi-ion foils

DOE Office of Scientific and Technical Information (OSTI.GOV)

Liu, Tung-Chang, E-mail: tcliu@umd.edu; Shao, Xi; Liu, Chuan-Sheng

2014-06-15

We present a numerical study of the effect of the laser spot size of a circularly polarized laser beam on the energy of quasi-monoenergetic protons in laser proton acceleration using a thin carbon-hydrogen foil. The used proton acceleration scheme is a combination of laser radiation pressure and shielded Coulomb repulsion due to the carbon ions. We observe that the spot size plays a crucial role in determining the net charge of the electron-shielded carbon ion foil and consequently the efficiency of proton acceleration. Using a laser pulse with fixed input energy and pulse length impinging on a carbon-hydrogen foil, amore » laser beam with smaller spot sizes can generate higher energy but fewer quasi-monoenergetic protons. We studied the scaling of the proton energy with respect to the laser spot size and obtained an optimal spot size for maximum proton energy flux. Using the optimal spot size, we can generate an 80 MeV quasi-monoenergetic proton beam containing more than 10{sup 8} protons using a laser beam with power 250 TW and energy 10 J and a target of thickness 0.15 wavelength and 49 critical density made of 90% carbon and 10% hydrogen.« less

The Gamma-Ray Laser Project

DTIC Science & Technology

1989-10-01

rabbits, P to flat planchettes , F to metallic foils, and B to scintillation bottles. The 18Ta sample consisted of a dusting of oxide on a thin aluminum...slower class consisted either of thin metallic disks or metallic chips or chemical compounds contained within flat polyethylene planchettes . 16 N00014-86

Fast-acting calorimeter measures heat output of plasma gun accelerator

NASA Technical Reports Server (NTRS)

Dethlefson, R.; Larson, A. V.; Liebing, L.

1967-01-01

Calorimeter measures the exhaust energy from a shot of a pulsed plasma gun accelerator. It has a fast response time and requires only one measurement to determine the total energy. It uses a long ribbon of copper foil wound around a glass frame to form a reentrant cavity.

Paper

ERIC Educational Resources Information Center

Kamata, Masahiro; Yajima, Seiko

2013-01-01

An educational experiment illustrates the electrolysis of water and copper chloride to middle school science students. The electrolysis cell is composed of filter paper soaked with Na[subscript 2]SO[subscript 4] or CuCl[subscript 2] aqueous solution sandwiched, along with a sheet of platinum foil, between two coin-type lithium batteries. When the…

Hazardous Waste Cleanup: Square D Company in Bordentown, New Jersey

EPA Pesticide Factsheets

Square D Company is located at 90 US Highway 130 in Bordentown, New Jersey. The site was formerly used for clay mining in the 1930's and then for a municipal landfill. The site was originally used as for a copper-foil manufacturing process under a company

Rapid Growth of Large Single-Crystalline Graphene via Second Passivation and Multistage Carbon Supply.

PubMed

Lin, Li; Sun, Luzhao; Zhang, Jincan; Sun, Jingyu; Koh, Ai Leen; Peng, Hailin; Liu, Zhongfan

2016-06-01

A second passivation and a multistage carbon-source supply (CSS) allow a 50-fold enhancement of the growth rate of large single-crystalline graphene with a record growth rate of 101 μm min(-1) , almost 10 times higher than for pure copper. To this end the CSS is tailored at separate stages of graphene growth on copper foil, combined with an effective suppression of new spontaneous nucleation via second passivation. © 2016 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Auger electron and X-ray photoelectron spectroscopic study of the biocorrosion of copper by alginic acid polysaccharide

NASA Astrophysics Data System (ADS)

Jolley, John G.; Geesey, Gill G.; Hankins, Michael R.; Wright, Randy B.; Wichlacz, Paul L.

1989-08-01

Thin films (3.4 nm) of copper on germanium substrates were exposed to 2% alginic acid polysaccharide aqueous solution. Pre- and post-exposure characterization were done by Auger electron spectroscopy and X-ray photoelectron spectroscopy. Ancillary graphite furnace atomic absorption spectroscopy was used to monitor the removal process of the copper thin film from the germanium substrate. Results indicate that some of the copper was oxidized by the alginic acid solution. Some of the copper was removed from the Cu/Ge interface and incorporated into the polymer matrix. Thus, biocorrosion of copper was exhibited by the alginic acid polysaccharide.

Measurements of Deuteron-Induced Activation Cross Sections for IFMIF Accelerator Structural Materials

NASA Astrophysics Data System (ADS)

Nakao, Makoto; Hori, Jun-ichi; Ochiai, Kentaro; Sato, Satoshi; Yamauchi, Michinori; Ishioka, Noriko S.; Nishitani, Takeo

2005-05-01

Activation cross sections for deuteron-induced reactions on aluminum, copper, and tungsten were measured by using a stacked-foil method. The stacked foils were irradiated with deuteron beam at the AVF cyclotron in the TIARA facility, JAERI. We obtained the activation cross sections for 27Al(d,2p)27Mg, 27Al(d,x)24Na, natCu(d,x)62,63Zn, 61,64Cu, and natW(d,x)181-184,186Re, 187W in the 22-40 MeV region. These cross sections were compared with other experimental ones and the data in the ACSELAM library calculated by the ALICE-F code.

High strain rate metalworking with vaporizing foil actuator: Control of flyer velocity by varying input energy and foil thickness

DOE Office of Scientific and Technical Information (OSTI.GOV)

Vivek, A., E-mail: vivek.4@osu.edu; Hansen, S. R.; Daehn, Glenn S.

2014-07-15

Electrically driven rapid vaporization of thin metallic foils can generate a high pressure which can be used to launch flyers at high velocities. Recently, vaporizing foil actuators have been applied toward a variety of impulse-based metal working operations. In order to exercise control over this useful tool, it is imperative that an understanding of the effect of characteristics of the foil actuator on its ability for mechanical impulse generation is developed. Here, foil actuators made out of 0.0508 mm, 0.0762 mm, and 0.127 mm thick AA1145 were used for launching AA2024-T3 sheets of thickness 0.508 mm toward a photonic Dopplermore » velocimeter probe. Launch velocities ranging between 300 m/s and 1100 m/s were observed. In situ measurement of velocity, current, and voltage assisted in understanding the effect of burst current density and deposited electrical energy on average pressure and velocity with foil actuators of various thicknesses. For the pulse generator, geometry, and flyer used here, the 0.0762 mm thick foil was found to be optimal for launching flyers to high velocities over short distances. Experimenting with annealed foil actuators resulted in no change in the temporal evolution of flyer velocity as compared to foil actuators of full hard temper. A physics-based analytical model was developed and found to have reasonable agreement with experiment.« less

Analytical model for release calculations in solid thin-foils ISOL targets

NASA Astrophysics Data System (ADS)

Egoriti, L.; Boeckx, S.; Ghys, L.; Houngbo, D.; Popescu, L.

2016-10-01

A detailed analytical model has been developed to simulate isotope-release curves from thin-foils ISOL targets. It involves the separate modeling of diffusion and effusion inside the target. The former has been modeled using both first and second Fick's law. The latter, effusion from the surface of the target material to the end of the ionizer, was simulated with the Monte Carlo code MolFlow+. The calculated delay-time distribution for this process was then fitted using a double-exponential function. The release curve obtained from the convolution of diffusion and effusion shows good agreement with experimental data from two different target geometries used at ISOLDE. Moreover, the experimental yields are well reproduced when combining the release fraction with calculated in-target production.

Laser energy transformation to shock waves in multi-layer flyers

NASA Astrophysics Data System (ADS)

Kasperczuk, A.; Pisarczyk, T.; Gus'kov, S. Yu.; Ullschmied, J.; Krouský, E.; Masek, K.; Pfeifer, M.; Rohlena, K.; Skala, J.; Kalal, M.; Tikhonchuk, V.; Pisarczyk, P.

Investigations of powerful laser pulse action on planar flyer targets consisting of the layers of different materials are of importance from the basic as well as the applied physics point of view. One important aspect of this research deals with optimization of inertial fusion targets design. Here, the role of a thin heavy metal layer as a protector against preliminary heating of compressed thermonuclear fuel by thermal X-ray radiation can be mentioned as one particular topic to be properly understood. In this paper, the results of our studies of such a thin layer influence on the laser-produced energy deposition in the flyer foils as well as on the hydrodynamic motion of the foils as a hole will be reported. A 0.4 μ m thick gold layer was located between an aluminum layer of 6 μ m thickness and mylar layer with thickness of 2.5 μ m, used here as an ablator. For comparison, the flyer target without the gold layer but of the same area density was employed. Two different target constructions were used: (1) with a 2 mm gap separating the foil and the massive targets for measuring the foil velocity and (2) with gaps of 50, 100 and 200 μ m for laser energy transfer efficiency measurements. Targets were irradiated by laser beam energies of ˜100 J in the case of the first harmonic, and by laser beam energies ˜120 J in the case of the third one using the Prague Asterix Laser System iodine laser. The interaction spot radius of 200 μ m and the laser pulse duration of ˜250 ps were employed in these experiments. A three-frame interferometric and shadowgraphic system was set-up as to measure velocities of the rear side of the foils and to determine electron density distributions at different stages of plasma evolution. Volumes of craters produced by collisions of accelerated foils with a massive aluminum block were used as an indicator of the laser energy transfer efficiency into the foils of both types. These experiments have shown that the presence of the thin gold layer causes a decrease of the flyer velocity by a factor of ˜1.2 for both the harmonics. However, in the case of the first harmonic, the energy transfer into the flyer with the gold layer is higher (compared with the flyers without the gold layer) only for the targets with smaller gaps. In the case of the third harmonic, about 10% decrease in the amount of energy transferred into the foil with the gold layer was observed.

Multiple-foil microabrasion package (A0023)

NASA Technical Reports Server (NTRS)

Mcdonnell, J. A. M.; Ashworth, D. G.; Carey, W. C.; Flavill, R. P.; Jennison, R. C.

1984-01-01

The specific scientific objectives of this experiment are to measure the spatial distribution, size, velocity, radiance, and composition of microparticles in near-Earth space. The technological objectives are to measure erosion rates resulting from microparticle impacts and to evaluate thin-foil meteor 'bumpers'. The combinations of sensitivity and reliability in this experiment will provide up to 1000 impacts per month for laboratory analysis and will extend current sensitivity limits by 5 orders of magnitude in mass.

Process Of Bonding Copper And Tungsten

DOEpatents

Slattery, Kevin T.; Driemeyer, Daniel E.

1999-11-23

Process for bonding a copper substrate to a tungsten substrate by providing a thin metallic adhesion promoting film bonded to a tungsten substrate and a functionally graded material (FGM) interlayer bonding the thin metallic adhesion promoting film to the copper substrate. The FGM interlayer is formed by thermal plasma spraying mixtures of copper powder and tungsten powder in a varied blending ratio such that the blending ratio of the copper powder and the tungsten powder that is fed to a plasma torch is intermittently adjusted to provide progressively higher copper content/tungsten content, by volume, ratio values in the interlayer in a lineal direction extending from the tungsten substrate towards the copper substrate. The resulting copper to tungsten joint well accommodates the difference in the coefficient of thermal expansion of the materials.

Thin, Light, Flexible Heaters Save Time and Energy

NASA Technical Reports Server (NTRS)

2007-01-01

The Icing Branch at NASA's Glenn Research Center uses the Center's Icing Research Tunnel (IRT) and Icing Research Aircraft to research methods for evaluating and simulating the growth of ice on aircraft, the effects that ice may have on aircraft in flight, and the development and effectiveness of various ice protection and detection systems. EGC Enterprises Inc. (EGC), of Chardon, Ohio, used the IRT to develop thermoelectric thin-film heater technology to address in-flight icing on aircraft wings. Working with researchers at Glenn and the original equipment manufacturers of aircraft parts, the company tested various thin, flexible, durable, lightweight, and efficient heaters. Development yielded a thin-film heater technology that can be used in many applications in addition to being an effective deicer for aircraft. This new thermoelectric heater was dubbed the QoFoil Rapid Response Thin-Film Heater, or QoFoil, for short. The product meets all criteria for in-flight use and promises great advances in thin-film, rapid response heater technology for a broad range of industrial applications. Primary advantages include time savings, increased efficiency, and improved temperature uniformity. In addition to wing deicing, EGC has begun looking at the material's usefulness for applications including cooking griddles, small cabinet heaters, and several laboratory uses.

Automated Composites Processing Technology: Film Module

NASA Technical Reports Server (NTRS)

Hulcher, A. Bruce

2004-01-01

NASA's Marshall Space Flight Center (MSFC) has developed a technology that combines a film/adhesive laydown module with fiber placement technology to enable the processing of composite prepreg tow/tape and films, foils or adhesives on the same placement machine. The development of this technology grew out of NASA's need for lightweight, permeation-resistant cryogenic propellant tanks. Autoclave processing of high performance composites results in thermally-induced stresses due to differences in the coefficients of thermal expansion of the fiber and matrix resin components. These stresses, together with the reduction in temperature due to cryogen storage, tend to initiate microcracking within the composite tank wall. One way in which to mitigate this problem is to introduce a thin, crack-resistant polymer film or foil into the tank wall. Investigation into methods to automate the processing of thin film or foil materials into composites led to the development of this technology. The concept employs an automated film supply and feed module that may be designed to fit existing fiber placement machines, or may be designed as integral equipment to new machines. This patent-pending technology can be designed such that both film and foil materials may be processed simultaneously, leading to a decrease in part build cycle time. The module may be designed having a compaction device independent of the host machine, or may utilize the host machine's compactor. The film module functions are controlled by a dedicated system independent of the fiber placement machine controls. The film, foil, or adhesive is processed via pre-existing placement machine run programs, further reducing operational expense.

The stopping power and energy straggling of the energetic C and O ions in polyimide

NASA Astrophysics Data System (ADS)

Mikšová, R.; Macková, A.; Slepička, P.

2016-03-01

The stopping power and energy straggling of 12Cn+ and 16On+ heavy ions in the energy range 5.3-8.0 MeV in 8 μm thick polyimide (PI) foil were measured by means of an indirect transmission method using a half-covered a PIPS detector. Ions scattered from thin gold layer, under the scattering angle 150° were detected and the spectrum of ions penetrating the PI foil and without foil was recorded. The values of the experimentally determined stopping powers were compared to the calculated data by SRIM-2013 and MSTAR codes. Measured data were in good agreement with data calculated by SRIM-2013, especially for C ions was observed better agreement than for O ions. The energy straggling was determined and compared to those calculated by using Bohr's, Bethe-Livingston and Yang models. The measured energy straggling values in the PI foil was corrected for foil roughness and thickness inhomogeneity determined from AFM. Bethe-Livingston predicting formula has been modified to make it appropriate for thicker targets. The energy straggling determined in our experiment was obtained higher than Bohr's predicted value; the predictions by Yang are in good agreement with our experiment. Bethe-Livingston formulation of the energy straggling shows better agreement with the experimental data after the modified formula implementation which assumes that the thick target was consisted to be composed of n-number of thin layers. Influence of the charge-exchange phenomena to the energy straggling of C and O ions in PI was discussed.

Deposition of Antimicrobial Copper-Rich Coatings on Polymers by Atmospheric Pressure Jet Plasmas

PubMed Central

Kredl, Jana; Kolb, Juergen F.; Schnabel, Uta; Polak, Martin; Weltmann, Klaus-Dieter; Fricke, Katja

2016-01-01

Inanimate surfaces serve as a permanent reservoir for infectious microorganisms, which is a growing problem in areas in everyday life. Coating of surfaces with inorganic antimicrobials, such as copper, can contribute to reduce the adherence and growth of microorganisms. The use of a DC operated air plasma jet for the deposition of copper thin films on acrylonitrile butadiene styrene (ABS) substrates is reported. ABS is a widespread material used in consumer applications, including hospitals. The influence of gas flow rate and input current on thin film characteristics and its bactericidal effect have been studied. Results from X-ray photoelectron spectroscopy (XPS) and atomic force microscopy confirmed the presence of thin copper layers on plasma-exposed ABS and the formation of copper particles with a size in the range from 20 to 100 nm, respectively. The bactericidal properties of the copper-coated surfaces were tested against Staphylococcus aureus. A reduction in growth by 93% compared with the attachment of bacteria on untreated samples was observed for coverage of the surface with 7 at. % copper. PMID:28773396

Flying mirror model for interaction of a super-intense laser pulse with a thin plasma layer: Transparency and shaping of linearly polarized laser pulses

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kulagin, Victor V.; Cherepenin, Vladimir A.; Hur, Min Sup

2007-11-15

A self-consistent one-dimensional (1D) flying mirror model is developed for description of an interaction of an ultra-intense laser pulse with a thin plasma layer (foil). In this model, electrons of the foil can have large longitudinal displacements and relativistic longitudinal momenta. An approximate analytical solution for a transmitted field is derived. Transmittance of the foil shows not only a nonlinear dependence on the amplitude of the incident laser pulse, but also time dependence and shape dependence in the high-transparency regime. The results are compared with particle-in-cell (PIC) simulations and a good agreement is ascertained. Shaping of incident laser pulses usingmore » the flying mirror model is also considered. It can be used either for removing a prepulse or for reducing the length of a short laser pulse. The parameters of the system for effective shaping are specified. Predictions of the flying mirror model for shaping are compared with the 1D PIC simulations, showing good agreement.« less

Treatment of waste printed circuit board by green solvent using ionic liquid.

PubMed

Zhu, P; Chen, Y; Wang, L Y; Zhou, M

2012-10-01

Recycling of waste printed circuit boards (WPCBs) is an important subject not only for the protection of environment but also for the recovery of valuable materials. A feasibility study was conducted to dissolve bromine epoxy resins of WPCBs using ionic liquid (IL) of 1-ethyl-3-methylimizadolium tetrafluoroborate [EMIM(+)][BF(4)(-)] (nonaqueous green solvent) for recovering copper foils and glass fibers. Experimental results indicated that the initial delamination had seen from the cross-section of the WPCBs by mean of metallographic microscope and digital camera when WPCBs were heated in [EMIM(+)][BF(4)(-)] at 240°C for a duration of 30 min. When temperature was increased to 260°C for a duration of 10 min, the bromine epoxy resins of WPCBs were throughout dissolved into [EMIM(+)][BF(4)(-)] and the separations of copper foils and glass fibers from WPCBs were completed. This clean and non-polluting technology offers a new way to recycle valuable materials from WPCBs and prevent the environmental pollution of WPCBs effectively. Crown Copyright © 2012. Published by Elsevier Ltd. All rights reserved.

Ultrarapid Inductive Rewarming of Vitrified Biomaterials with Thin Metal Forms.

PubMed

Manuchehrabadi, Navid; Shi, Meng; Roy, Priyatanu; Han, Zonghu; Qiu, Jinbin; Xu, Feng; Lu, Tian Jian; Bischof, John

2018-06-19

Arteries with 1-mm thick walls can be successfully vitrified by loading cryoprotective agents (CPAs) such as VS55 (8.4 M) or less concentrated DP6 (6 M) and cooling at or beyond their critical cooling rates of 2.5 and 40 °C/min, respectively. Successful warming from this vitrified state, however, can be challenging. For example, convective warming by simple warm-bath immersion achieves 70 °C/min, which is faster than VS55's critical warming rate of 55 °C/min, but remains far below that of DP6 (185 °C/min). Here we present a new method that can dramatically increase the warming rates within either a solution or tissue by inductively warming commercially available metal components placed within solutions or in proximity to tissues with non-invasive radiofrequency fields (360 kHz, 20 kA/m). Directly measured warming rates within solutions exceeded 1000 °C/min with specific absorption rates (W/g) of 100, 450 and 1000 for copper foam, aluminum foil, and nitinol mesh, respectively. As proof of principle, a carotid artery diffusively loaded with VS55 and DP6 CPA was successfully warmed with high viability using aluminum foil, while standard convection failed for the DP6 loaded tissue. Modeling suggests this approach can improve warming in tissues up to 4-mm thick where diffusive loading of CPA may be incomplete. Finally, this technology is not dependent on the size of the system and should therefore scale up where convection cannot.

High areal capacity, micrometer-scale amorphous Si film anode based on nanostructured Cu foil for Li-ion batteries

NASA Astrophysics Data System (ADS)

Si, Wenping; Sun, Xiaolei; Liu, Xianghong; Xi, Lixia; Jia, Yandong; Yan, Chenglin; Schmidt, Oliver G.

2014-12-01

We report a feasible design to fabricate micrometer-scale Si films deposited on nanostructured Cu foil as high areal capacity anodes for Li-ion batteries with excellent cycling performance. Nanostructured copper oxides are prepared by anodic oxidation of Cu foil in alkaline solution. The resultant copper oxide nanofibers function as matrix for thick Si films (1-2 μm) loading. Metallic Cu nanofibers are obtained by in-situ electrochemical reduction at low potentials, which work as electrical highways for fast electron transport and a reliable mechanical matrix to accommodate volume changes during lithium-silicon alloy/dealloy processes. The engineered thick Si film anode exhibit both high areal capacity (0.48 mAh cm-2 for 1 μm Si film and 0.6 mAh cm-2 for 2 μm Si film after 200 cycles at 0.225 mA cm-2) and excellent rate capability (0.52 mAh cm-2 at 1.05 mA cm-2 for 2 μm Si film). The 2 μm silicon film electrode is able to recover to the initial value of 1 mAh cm-2 when the current rate is set back to 0.15 mA cm-2 even after cycling at high current rates. The reported concept can be a general method for high-loading-film electrodes, which is industrial scalable and compatible with current battery manufacturing processes.

Modification of Bushing Test Rig and Research of Variable Inlet Guide Vane Bushings For Further Development of PM304 Bushings

NASA Technical Reports Server (NTRS)

Yanke, Anne

2004-01-01

PS304 is a high temperature solid lubricant coating comprised of a nickel-chrome binder, chrome oxide hardener, barium-calcium fluoride high temperature lubricant, and silver as the low temperature lubricant. This coating is used to lubricate Oil-Free Foil Air Bearings as they experience friction and wear during start up and shut down. The coating deposition process begins with undercutting the shaft. This area is then sandblasted to provide a rough surface for the coating to adhere to. The coating powder is then sent through the plasma spray gun and a reasonably thick layer is applied to the undercut area of the shaft. The coating is then ground down even with the surface of the shaft and gets a nice polished finish. The foil air bearings use the solid lubricant, as mentioned above, during start up and shut down. During normal operating conditions, generally above 2000RPM, the bearings utilize air as their lubricant. Foil air bearings are comprised of a thin top foil and a corrugated bump foil. They have an interference fit with the shaft before operation. As the air gets "trapped" between the top foil and the shaft, it presses the top foil against the bump foil, in turn compressing the bumps. As the bumps compress, it allows for the air to separate the top foil from the shaft, therefore, utilizing the trapped air as its lubricant.

Nonlinear Dynamics of a Foil Bearing Supported Rotor System: Simulation and Analysis

NASA Technical Reports Server (NTRS)

Li, Feng; Flowers, George T.

1996-01-01

Foil bearings provide noncontacting rotor support through a number of thin metal strips attached around the circumference of a stator and separated from the rotor by a fluid film. The resulting support stiffness is dominated by the characteristics of the foils and is a nonlinear function of the rotor deflection. The present study is concerned with characterizing this nonlinear effect and investigating its influence on rotordynamical behavior. A finite element model is developed for an existing bearing, the force versus deflection relation characterized, and the dynamics of a sample rotor system are studied. Some conclusions are discussed with regard to appropriate ranges of operation for such a system.

Role of Friction on the Thermal Development in Ultrasonically Consolidated Aluminum Foils and Composites

DTIC Science & Technology

2011-01-01

amplitude, . The third input parameter, weld speed, s, is inversely proportional to N, the num- ber of cycles as shown in Eq. (3). In summary, F is...though, an extensive body of work on mechanical testing of ultrasonically consolidated thin foils has been performed at Loughborough University. In...comprehensive textbook on tribology presents a preliminary derivation for plastic contact of ductile metals which suggests ≤ 1/5; this is much lower

Growth of Monolayer Graphene on Nanoscale Copper-Nickel Alloy Thin Films

PubMed Central

Cho, Joon Hyong; Gorman, Jason J.; Na, Seung Ryul; Cullinan, Michael

2017-01-01

Growth of high quality and monolayer graphene on copper thin films on silicon wafers is a promising approach to massive and direct graphene device fabrication in spite of the presence of potential dewetting issues in the copper film during graphene growth. Current work demonstrates roles of a nickel adhesion coupled with the copper film resulting in mitigation of dewetting problem as well as uniform monolayer graphene growth over 97 % coverage on films. The feasibility of monolayer graphene growth on Cu-Ni alloy films as thin as 150 nm in total is also demonstrated. During the graphene growth on Cu-Ni films, the nickel adhesion layer uniformly diffuses into the copper thin film resulting in a Cu-Ni alloy, helping to promote graphene nucleation and large area surface coverage. Furthermore, it was found that the use of extremely thin metal catalyst films also constraint the total amount of carbon that can be absorbed into the film during growth, which helps to eliminate adlayer formation and promote monolayer growth regardless of alloying content, thus improving the monolayer fraction of graphene coverage on the thinner films. These results suggest a path forward for the large scale integration of high quality, monolayer graphene into nanoelectronic and nanomechanical devices. PMID:28669999

A Systems Approach to the Solid Lubrication of Foil Air Bearings for Oil-Free Turbomachinery

NASA Technical Reports Server (NTRS)

DellaCorte, Christopher; Zaldana, Antonio R.; Radil, Kevin C.

2002-01-01

Foil air bearings are self-acting hydrodynamic bearings which rely upon solid lubricants to reduce friction and minimize wear during sliding which occurs at start-up and shut-down when surface speeds are too low to allow the formation of a hydrodynamic air film. This solid lubrication is typically accomplished by coating the non-moving foil surface with a thin, soft polymeric film. The following paper introduces a systems approach in which the solid lubrication is provided by a combination of self lubricating shaft coatings coupled with various wear resistant and lubricating foil coatings. The use of multiple materials, each providing different functions is modeled after oil-lubricated hydrodynamic sleeve bearing technology which utilizes various coatings and surface treatments in conjunction with oil lubricants to achieve optimum performance. In this study, room temperature load capacity tests are performed on journal foil air bearings operating at 14,000 rpm. Different shaft and foil coating technologies such as plasma sprayed composites, ceramic, polymer and inorganic lubricant coatings are evaluated as foil bearing lubricants. The results indicate that bearing performance is improved through the individual use of the lubricants and treatments tested. Further, combining several solid lubricants together yielded synergistically better results than any material alone.

Explosion of thin aluminum foils in air

NASA Astrophysics Data System (ADS)

Baksht, R.; Pokryvailo, A.; Yankelevich, Y.; Ziv, I.

2004-12-01

An inductive-based power supply (240μH, 50kA) was used for the investigation of the foil explosion process in the time range of 0.05ms

Thin film photovoltaic cells having increased durability and operating life and method for making same

DOEpatents

Barnett, Allen M.; Masi, James V.; Hall, Robert B.

1980-12-16

A solar cell having a copper-bearing absorber is provided with a composite transparent encapsulating layer specifically designed to prevent oxidation of the copper sulfide. In a preferred embodiment, the absorber is a layer of copper sulfide and the composite layer comprises a thin layer of copper oxide formed on the copper sulfide and a layer of encapsulating glass formed on the oxide. It is anticipated that such devices, when exposed to normal operating conditions of various terrestrial applications, can be maintained at energy conversion efficiencies greater than one-half the original conversion efficiency for periods as long as thirty years.

Preparation Of Copper Indium Gallium Diselenide Films For Solar Cells

DOEpatents

Bhattacharya, Raghu N.; Contreras, Miguel A.; Keane, James; Tennant, Andrew L. , Tuttle, John R.; Ramanathan, Kannan; Noufi, Rommel

1998-08-08

High quality thin films of copper-indium-gallium-diselenide useful in the production of solar cells are prepared by electrodepositing at least one of the constituent metals onto a glass/Mo substrate, followed by physical vapor deposition of copper and selenium or indium and selenium to adjust the final stoichiometry of the thin film to approximately Cu(In,Ga)Se.sub.2. Using an AC voltage of 1-100 KHz in combination with a DC voltage for electrodeposition improves the morphology and growth rate of the deposited thin film. An electrodeposition solution comprising at least in part an organic solvent may be used in conjunction with an increased cathodic potential to increase the gallium content of the electrodeposited thin film.

Cyclotron production of 61Cu using natural Zn & enriched 64Zn targets

NASA Astrophysics Data System (ADS)

Asad, A. H.; Smith, S. V.; Chan, S.; Jeffery, C. M.; Morandeau, L.; Price, R. I.

2012-12-01

Copper-61 (61Cu) shares with 64Cu certain advantages for PET diagnostic imaging, but has a shorter half-life (3.4hr vs. 12.7hr) and a greater probability of positron production per disintegration (61% vs. 17.9%). One important application is for in vivo imaging of hypoxic tissue. In this study 61Cu was produced using the 64Zn(p,α)61Cu reaction on natural Zn or enriched 64Zn targets. The enriched 64Zn (99.82%) was electroplated onto high purity gold or silver foils or onto thin Al discs. A typical target bombardment used 30μA; at 11.7, 14.5 or 17.6MeV over 30-60min. The 61Cu (radiochemical purity of >95%) was separated using a combination of cation and anion exchange columns. The 64Zn target material was recovered after each run, for re-use. In a direct comparison with enriched 64Zn-target results, 61Cu production using the cheaper natZn target proved to be an effective alternative.

Large-scale studies of ion acceleration in laser-generated plasma at intensities from 1010 W/cm2 to 1019 W/cm2

NASA Astrophysics Data System (ADS)

Torrisi, L.

2018-02-01

A large-scale study of ion acceleration in laser-generated plasma, extended to intensities from 1010 W/cm2 up to 1019 W/cm2, is presented. Aluminium thick and thin foils were irradiated in high vacuum using different infrared lasers and pulse durations from ns up to fs scale. Plasma was monitored mainly using SiC detectors employed in time-of-flight configuration. Protons and aluminium ions, at different energies and yields, were measured as a function of the laser intensity. The discontinuity region between particle acceleration from both the backward plasma (BPA) in thick targets and the forward plasma in thin foils in the target normal sheath acceleration (TNSA) regimes were investigated.

Numerical and Experimental Studies on the Explosive Welding of Tungsten Foil to Copper

PubMed Central

Zhou, Qiang; Feng, Jianrui; Chen, Pengwan

2017-01-01

This work verifies that the W foil could be successfully welded on Cu through conventional explosive welding, without any cracks. The microstructure was observed through scanning electron microscopy (SEM), optical microscopy and energy-dispersive X-ray spectrometry (EDS). The W/Cu interface exhibited a wavy morphology, and no intermetallic or transition layer was observed. The wavy interface formation, as well as the distributions of temperature, pressure and plastic strain at the interface were studied through numerical simulation with Smoothed Particle Hydrodynamics (SPH). The welding mechanism of W/Cu was analyzed according to the numerical results and experimental observation, which was in accordance with the indentation mechanism proposed by Bahrani. PMID:28832527

Additional security features for optically variable foils

NASA Astrophysics Data System (ADS)

Marshall, Allan C.; Russo, Frank

1998-04-01

For thousands of years, man has exploited the attraction and radiance of pure gold to adorn articles of great significance. Today, designers decorate packaging with metallic gold foils to maintain the prestige of luxury items such as perfumes, chocolates, wine and whisky, and to add visible appeal and value to wide range of products. However, today's products do not call for the hand beaten gold leaf of the Ancient Egyptians, instead a rapid production technology exists which makes use of accurately coated thin polymer films and vacuum deposited metallic layers. Stamping Foils Technology is highly versatile since several different layers may be combined into one product, each providing a different function. Not only can a foil bring visual appeal to an article, it can provide physical and chemical resistance properties and also protect an article from human forms of interference, such as counterfeiting, copying or tampering. Stamping foils have proved to be a highly effective vehicle for applying optical devices to items requiring this type of protection. Credit cards, bank notes, personal identification documents and more recently high value packaged items such as software and perfumes are protected by optically variable devices applied using stamping foil technology.

Preparation and characterization of copper telluride thin films by modified chemical bath deposition (M-CBD) method

NASA Astrophysics Data System (ADS)

Pathan, H. M.; Lokhande, C. D.; Amalnerkar, D. P.; Seth, T.

2003-09-01

Copper telluride thin films were deposited using modified chemical method using copper(II) sulphate; pentahydrate [CuSO 4·5H 2O] and sodium tellurite [Na 2TeO 3] as cationic and anionic sources, respectively. Modified chemical method is based on the immersion of the substrate into separately placed cationic and anionic precursors. The preparative conditions such as concentration, pH, immersion time, immersion cycles, etc. were optimized to get good quality copper telluride thin films at room temperature. The films have been characterized for structural, compositional, optical and electrical transport properties by means of X-ray diffraction (XRD), scanning electron microscopy (SEM), energy dispersive X-ray analysis (EDAX), Rutherford back scattering (RBS), optical absorption/transmission, electrical resistivity and thermoemf measurement techniques.

Preparation of CIGS-based solar cells using a buffered electrodeposition bath

DOEpatents

Bhattacharya, Raghu Nath

2007-11-20

A photovoltaic cell exhibiting an overall conversion efficiency of at least 9.0% is prepared from a copper-indium-gallium-diselenide thin film. The thin film is prepared by simultaneously electroplating copper, indium, gallium, and selenium onto a substrate using a buffered electro-deposition bath. The electrodeposition is followed by adding indium to adjust the final stoichiometry of the thin film.

A New Electrochemical Approach for the Synthesis of Copper-Graphene Nanocomposite Foils with High Hardness

PubMed Central

Pavithra, Chokkakula L. P.; Sarada, Bulusu V.; Rajulapati, Koteswararao V.; Rao, Tata N.; Sundararajan, G.

2014-01-01

Graphene has proved its significant role as a reinforcement material in improving the strength of polymers as well as metal matrix composites due to its excellent mechanical properties. In addition, graphene is also shown to block dislocation motion in a nanolayered metal-graphene composites resulting in ultra high strength. In the present paper, we demonstrate the synthesis of very hard Cu-Graphene composite foils by a simple, scalable and economical pulse reverse electrodeposition method with a well designed pulse profile. Optimization of pulse parameters and current density resulted in composite foils with well dispersed graphene, exhibiting a high hardness of ~2.5 GPa and an increased elastic modulus of ~137 GPa while exhibiting an electrical conductivity comparable to that of pure Cu. The pulse parameters are designed in such a way to have finer grain size of Cu matrix as well as uniform dispersion of graphene throughout the matrix, contributing to high hardness and modulus. Annealing of these nanocomposite foils at 300°C, neither causes grain growth of the Cu matrix nor deteriorates the mechanical properties, indicating the role of graphene as an excellent reinforcement material as well as a grain growth inhibitor. PMID:24514043

"Light sail" acceleration reexamined.

PubMed

Macchi, Andrea; Veghini, Silvia; Pegoraro, Francesco

2009-08-21

The dynamics of the acceleration of ultrathin foil targets by the radiation pressure of superintense, circularly polarized laser pulses is investigated by analytical modeling and particle-in-cell simulations. By addressing self-induced transparency and charge separation effects, it is shown that for "optimal" values of the foil thickness only a thin layer at the rear side is accelerated by radiation pressure. The simple "light sail" model gives a good estimate of the energy per nucleon, but overestimates the conversion efficiency of laser energy into monoenergetic ions.

Digital Systems Validation Handbook. Volume 2

DTIC Science & Technology

1989-02-01

power. 2. A grid of wires, solid sheet, or foil. 3. A wire from circuit to grounding block or case. 4. A wire from circuit to structure. 5. Shield...RETURN. (11) 1. Structure, for power, fault, and "discrete" circuits. 2. A grid of wires, solid sheet, or foil. 3. A wire from circuit load back to...TV (14) Television TWTD (13) Thin Wire Time Domain TX (5) Transmit U.K. (13,141 United Kingdom U.S. (14) United States UART (15) Universal Asynchronous

Thermal Loading of Thin Metal Foils Used as Electron Beam Windows for a KRF Laser

DTIC Science & Technology

2005-06-01

the Inertial Fusion Energy (IFE) requirements for durability, efficiency, and cost. One of the challenging laser components is the pressure foil that...R. Welch, D. V. Rose, and S. Searles, "Electron beam pumped krypton fluoride lasers for fusion energy ," Proc. IEEE, vol. 92, pp. 1043-1056, July...D. Weidenheimer, and D. V. Rose, "Repetitively pulsed, high energy KrF lasers for inertial fusion energy ," Nucl. Fusion, vol. 44, pp. S247-S253

Vacuum barrier for excimer lasers

DOEpatents

Shurter, Roger P.

1992-01-01

A barrier for separating the vacuum area of a diode from the pressurized gas area of an excimer laser. The barrier is a composite material comprising layers of a metal such as copper, along with layers of polyimide, and a matrix of graphite fiber yarns impregnated with epoxy. The barrier is stronger than conventional foil barriers, and allows greater electron throughput.

Compact, Low-Power, and High-Speed Graphene-Based Integrated Photonic Modulator Technology

DTIC Science & Technology

2017-11-02

which we want to transfer graphene, we cut the graphene-on- Copper foil into appropriate pieces using sharp razor blades or scissors. We then follow a...rinsed under running DI water for 5 minutes. Patterns on HSQ are then transferred to alumina in a Plasma-Therm ICP system using the recipe which was

Conducting-polymer-driven actively shaped propellers and screws

NASA Astrophysics Data System (ADS)

Madden, John D.; Schmid, Bryan; Lafontaine, Serge R.; Madden, Peter G. A.; Hover, Franz S.; McLetchie, Karl; Hunter, Ian W.

2003-07-01

Conducting polymer actuators are employed to create actively shaped hydrodynamic foils. The active foils are designed to allow control over camber, much like the ailerons of an airplane wing. Control of camber promises to enable variable thrust in propellers and screws, increased maneuverability, and improved stealth. The design and fabrication of the active foils are presented, the forces are measured and operation is demonstrated both in still air and water. The foils have a "wing" span of 240 mm, and an average chord length (width) of 70 mm. The trailing 30 mm of the foil is composed of a thin polypyrrole actuator that curls chordwise to achieve variable camber. The actuator consists of two 30 μm thick sheets of hexafluorophosphate doped polypyrrole separated from each other by a gel electrolyte. A polymer layer encapsulates the entire structure. Potentials are applied between the polymer layers to induce reversible bending by approximately 35 degrees, and generating forces of 0.15 N. These forces and displacements are expected to enable operation in water at flow rates of > 1 m/s and ~ 30 m/s in air.

Effect of low-stiffness closeout overwrap on rocket thrust-chamber life

NASA Technical Reports Server (NTRS)

Kasper, H. J.; Nota-Donato, J. J.

1979-01-01

Three rocket thrust chambers with copper liners and a thrust level of 20.9 kN were cyclically test fired to failure. Two of the liners were made from oxygen free, high conductivity (OFHC) copper and from annealed Amzirc. The milled coolant channels were closed out with a thin copper closeout over which a fiberglass composite was wrapped to provide hoop strength only. Experimental data are presented, along with the results of a preliminary analysis that was performed before fabrication to evaluate the life extending potential of a thin copper closeout with a fiberglass overwrap.

Pleated metal bipolar assembly

DOEpatents

Wilson, Mahlon S.; Zawodzinski, Christine

2001-01-01

A thin low-cost bipolar plate for an electrochemical cell is formed from a polymer support plate with first flow channels on a first side of the support plate and second flow channels on a second side of the support plate, where the first flow channels and second flow channels have intersecting locations and have a depth effective to form openings through the support plate at the intersecting locations. A first foil of electrically conductive material is pressed into the first flow channels. A second foil of electrically conductive material pressed into the second flow channels so that electrical contact is made between the first and second foils at the openings through the support plate. A particular application of the bipolar plate is in polymer electrolyte fuel cells.

Enhancement in sensitivity of copper sulfide thin film ammonia gas sensor: Effect of swift heavy ion irradiation

DOE Office of Scientific and Technical Information (OSTI.GOV)

Sagade, Abhay Abhimanyu; Sharma, Ramphal; Department of Chemistry, Hanyang University, Sungdong-Ku, Haengdang-dong 17, Seoul 133-791

2009-02-15

The studies are carried out on the effect of swift heavy ion (SHI) irradiation on surface morphology and electrical properties of copper sulfide (Cu{sub x}S) thin films with three different chemical compositions (x values). The irradiation experiments have been carried out on Cu{sub x}S films with x=1.4, 1.8, and 2 by 100 MeV gold heavy ions at room temperature. These as-deposited and irradiated thin films have been used to detect ammonia gas at room temperature (300 K). The SHI irradiation treatment on x=1.4 and 1.8 copper sulfide films enhances the sensitivity of the gas sensor. The results are discussed consideringmore » high electronic energy deposition by 100 MeV gold heavy ions in a matrix of copper sulfide.« less

Method of making an improved superconducting quantum interference device

DOEpatents

Wu, Cheng-Teh; Falco, Charles M.; Kampwirth, Robert T.

1977-01-01

An improved superconducting quantum interference device is made by sputtering a thin film of an alloy of three parts niobium to one part tin in a pattern comprising a closed loop with a narrow region, depositing a thin film of a radiation shield such as copper over the niobium-tin, scribing a narrow line in the copper over the narrow region, exposing the structure at the scribed line to radiation and removing the deposited copper.

Study of meteoroid impact craters on various materials (AO 138-1). Attempt at dust debris collection with stacked detectors (AO 138-2)

NASA Technical Reports Server (NTRS)

Mandeville, Jean Claude

1991-01-01

Part of the Long Duration Exposure Facility (LDEF) tray allocated to French experiments, known as FRECOPA payload, was devoted to the study of dust particles. Two passive experiments were flown: one composed of a set of glass and metallic samples and one composed of multilayer thin foils detectors. In addition to these experiments, a broad variety of materials were exposed to the bombardment of microparticles and provide more data. Thick target experiment comprises selected metallic (Al, Au, Cu, W, Stainless Steel) 250 microns thick and glass surfaces 1.5 mm thick. Crater size distribution from these thick target experiments enable, with the aid of lab calibrations by solid particle accelerators, the evaluation of the incident microparticle flux in the near earth environment. The aim of the multiple foil penetration and collection experiment is primarily to study the feasibility of multilayer thin film detectors acting as energy sorters in order to collect micrometeoroids, if not in their original shape, at least as 'breakup' fragments suitable for chemical analysis. Foil thicknesses range from 0.75 to 5 microns of Al.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Bharadwaja, S. S. N., E-mail: s.s.n.bharadwaja@gmail.com; Ko, S. W.; Qu, W.

Excimer laser assisted re-oxidation for reduced, crystallized BaTiO{sub 3} thin films on Ni-foils was investigated. It was found that the BaTiO{sub 3} can be re-oxidized at an oxygen partial pressure of ∼50 mTorr and substrate temperature of 350 °C without forming a NiO{sub x} interface layer between the film and base metal foil. The dielectric permittivity of re-oxidized films was >1000 with loss tangent values <2% at 100 Hz, 30 mV{sub rms} excitation signal. Electron Energy Loss Spectroscopy indicated that BaTiO{sub 3} thin films can be re-oxidized to an oxygen stoichiometry close to ∼3 (e.g., stoichiometric). High resolution cross sectional transmission electronmore » microscopy showed no evidence of NiO{sub x} formation between the BaTiO{sub 3} and the Ni foil upon excimer laser re-oxidation. Spectroscopic ellipsometry studies on laser re-oxidized [001]{sub C} and [111]{sub C} BaTiO{sub 3} single crystals indicate that the re-oxidation of BaTiO{sub 3} single crystals is augmented by photo-excitation of the ozone, as well as laser pulse induced temperature and local stress gradients.« less

Heat Transfer in High Temperature Multilayer Insulation

NASA Technical Reports Server (NTRS)

Daryabeigi, Kamran; Miller, Steve D.; Cunnington, George R.

2007-01-01

High temperature multilayer insulations have been investigated as an effective component of thermal-protection systems for atmospheric re-entry of reusable launch vehicles. Heat transfer in multilayer insulations consisting of thin, gold-coated, ceramic reflective foils and Saffil(TradeMark) fibrous insulation spacers was studied both numerically and experimentally. A finite volume numerical thermal model using combined conduction (gaseous and solid) and radiation in porous media was developed. A two-flux model with anisotropic scattering was used for radiation heat transfer in the fibrous insulation spacers between the reflective foils. The thermal model was validated by comparison with effective thermal conductivity measurements in an apparatus based on ASTM standard C201. Measurements were performed at environmental pressures in the range from 1x10(exp -4) to 760 torr over the temperature range from 300 to 1300 K. Four multilayer samples with nominal densities of 48 kg/cu m were tested. The first sample was 13.3 mm thick and had four evenly spaced reflective foils. The other three samples were 26.6 mm thick and utilized either one, two, or four reflective foils, located near the hot boundary with nominal foil spacing of 1.7 mm. The validated thermal model was then used to study relevant design parameters, such as reflective foil spacing and location in the stack-up and coating of one or both sides of foils.

Gold leaf counter electrodes for dye-sensitized solar cells

NASA Astrophysics Data System (ADS)

Shimada, Kazuhiro; Toyoda, Takeshi

2018-03-01

In this study, a gold leaf 100 nm thin film is used as the counter electrode in dye-sensitized solar cells. The traditional method of hammering gold foil to obtain a thin gold leaf, which requires only small amounts of gold, was employed. The gold leaf was then attached to the substrate using an adhesive to produce the gold electrode. The proposed approach for fabricating counter electrodes is demonstrated to be facile and cost-effective, as opposed to existing techniques. Compared with electrodes prepared with gold foil and sputtered gold, the gold leaf counter electrode demonstrates higher catalytic activity with a cobalt-complex electrolyte and higher cell efficiency. The origin of the improved performance was investigated by surface morphology examination (scanning electron microscopy), various electrochemical analyses (cyclic voltammetry, linear sweep voltammetry, and electrochemical impedance spectroscopy), and crystalline analysis (X-ray diffractometry).

Investigation of Structural, Compositional and Anti-Microbial Properties of Copper Thin Film Using Direct Current Magnetron Sputtering for Surgical Instruments

NASA Astrophysics Data System (ADS)

Kalaiselvam, S.; Sandhya, J.; Krishnan, K. V. Hari; Kedharnath, A.; Arulkumar, G.; Roseline, A. Ameelia

Surgical instruments and other bioimplant devices, owing to their importance in the biomedical industry require high biocompatibility to be used in the human body. Nevertheless, issues of compatibility, bacterial infections are quite common in such devices. Hence development of surface coatings on various substrates for implant applications is a promising technique to combat the issues arising in these implant materials. The present investigation aims at coating copper on stainless steel substrate using DC Magnetron sputtering which is used to achieve film of required thickness (0.5-8μm). The deposition pressure, substrate temperature, power supply, distance between the specimen and target are optimized and maintained constant, while the sputtering time (30-110min) is varied. The sputtered copper thin film’s morphology, composition are characterized by SEM and EDAX. X-ray diffraction analysis shows copper oriented on (111) and (002) and copper oxide on (111) planes. The contact angle of copper thin film is 92∘ while AISI 316L shows 73∘. The antimicrobial studies carried in Staphylococcus aureus, Escherichia Coli, Klebsiella pneumonia and Candida albicans show that the maximum reduction was seen upto 35, 26, 54, 39CFU/mL, respectively after 24h. The cell viability is studied by MTT assay test on Vero cell line for 24h, 48h and 72h and average cell viability is 43.85%. The copper release from the thin film to the culture medium is 6691μg/L (maximum) is estimated from AAS studies. The copper coated substrate does not show much reaction with living Vero cells whereas the bacteria and fungi are found to be destroyed.

Laser Embossing of Micro-and Submicrometer Surface Structures in Copper

NASA Astrophysics Data System (ADS)

Ehrhardt, Martin; Lorenz, Pierre; Frost, Frank; Zimmer, Klaus

Micro- and submicrometer structures have been transferred from nickel foils into solid copper surfaces by laser microembossing. The developed arrangement for laser microembossing allows a large-area replication using multi- pulse laser scanning scheme, guaranties a low contamination of the embossed surface and enables the utilization of thick workpieces. In the micrometer range the replicated patterns feature a high accuracy regarding the shape. A significant difference between the master and the replication pattern could be observed for the laser embossing of submicrometer patterns. In conclusion, the results show that the proposed laser embossing process is a promising method with a number of applications in microengineering.

Vacuum barrier for excimer lasers

DOEpatents

Shurter, R.P.

1992-09-15

A barrier for separating the vacuum area of a diode from the pressurized gas area of an excimer laser. The barrier is a composite material comprising layers of a metal such as copper, along with layers of polyimide, and a matrix of graphite fiber yarns impregnated with epoxy. The barrier is stronger than conventional foil barriers, and allows greater electron throughput. 3 figs.

Fabrication and characterization of silver- and copper-coated Nylon 6 forcespun nanofibers by thermal evaporation

DOE Office of Scientific and Technical Information (OSTI.GOV)

Mihut, Dorina M., E-mail: dorinamm@yahoo.com; Lozano, Karen; Foltz, Heinrich

2014-11-01

Silver and copper nanoparticles were deposited as thin films onto substrates consisting of Nylon 6 nanofibers manufactured using forcespinning{sup ®} equipment. Different rotational speeds were used to obtain continuous nanofibers of various diameters arranged as nonwoven mats. The Nylon 6 nanofibers were collected as successive layers on frames, and a high-vacuum thermal evaporation method was used to deposit the silver and copper thin films on the nanofibers. The structures were investigated using scanning electron microscopy–scanning transmission electron microscopy, atomic force microscopy, x-ray diffraction, and electrical resistance measurements. The results indicate that evaporated silver and copper nanoparticles were successfully deposited onmore » Nylon 6 nanofibers as thin films that adhered well to the polymer substrate while the native morphology of the nanofibers were preserved, and electrically conductive nanostructures were achieved.« less

Wireless digital pressure gauge based on nanomaterials

NASA Astrophysics Data System (ADS)

Abay, Dilyara; Otarbay, Zhuldyz; Token, Madengul; Guseinov, Nazim; Muratov, Mukhit; Gabdullin, Maratbek; Ismailov, Daniyar

2018-03-01

In the article studies the efficiency of using nanostructured nickel copper films as thin films for bending sensors. Thin films of nickel-copper alloy were deposited using magnetron sputtering technology followed by the appropriate masks. Scanning electron microscopy (SEM) and energy- dispersive X-ray spectroscopy (EDS) techniques were used to examine structure and surface of the Ni Cu coatings. The results of the bending sensors result indicated that the Ni Cu thin film strain gauge showed an excellent sensitive.

Preparation and investigation of diamond-like carbon stripper foils by filtered cathodic vacuum arc

NASA Astrophysics Data System (ADS)

Fan, Qiwen; Du, Yinghui; Zhang, Rong; Xu, Guoji

2013-04-01

Thin diamond-like carbon (DLC) stripper foils ˜5 μg/cm2 in thickness were produced and evaluated as heavy-ion strippers for the Beijing HI-13 Tandem Accelerator. The DLC layers ˜4 μg/cm2 in thickness were produced by the filtered cathodic vacuum arc technology onto glass slides coated with betaine-saccharose as releasing agent, which were previously covered with evaporated carbon layers ˜1 μg/cm2 in thickness by the controlled ac arc-discharge method. Irradiation lifetimes of the DLC stripper foils were tested using the heavy-ion beams at the terminal of the Beijing HI-13 Tandem Accelerator, and compared with those of the standard carbon stripper foils made by the combined dc and ac arc-discharge method. The measurements indicate that the DLC stripper foils outlast the standard combined dc and ac arc-discharge carbon stripper foils by a factor of at least 13 and 4for the 197Au- (˜9 MeV, ˜1 μA) and 63Cu- (˜9 MeV, ˜1 μA) ion beams, respectively. The structure and properties of the DLC foils deposited onto silicon substrates by the filtered cathodic vacuum arc technology were also evaluated and analyzed by scanning electron microscopy, Raman spectroscopy and X-ray photoelectron spectroscopy. The scanning electron microscopy images show that the DLC foils contain hardly droplets through the double 90° filters. The X-ray photoelectron spectrum indicates that sp3 bonds of the DLC foils exceed 70%. The integral intensity ratio of the D peak to the G peak (ID/IG) measured by the Raman spectroscopy is0.78.

A direct thin-film path towards low-cost large-area III-V photovoltaics

PubMed Central

Kapadia, Rehan; Yu, Zhibin; Wang, Hsin-Hua H.; Zheng, Maxwell; Battaglia, Corsin; Hettick, Mark; Kiriya, Daisuke; Takei, Kuniharu; Lobaccaro, Peter; Beeman, Jeffrey W.; Ager, Joel W.; Maboudian, Roya; Chrzan, Daryl C.; Javey, Ali

2013-01-01

III-V photovoltaics (PVs) have demonstrated the highest power conversion efficiencies for both single- and multi-junction cells. However, expensive epitaxial growth substrates, low precursor utilization rates, long growth times, and large equipment investments restrict applications to concentrated and space photovoltaics (PVs). Here, we demonstrate the first vapor-liquid-solid (VLS) growth of high-quality III-V thin-films on metal foils as a promising platform for large-area terrestrial PVs overcoming the above obstacles. We demonstrate 1–3 μm thick InP thin-films on Mo foils with ultra-large grain size up to 100 μm, which is ~100 times larger than those obtained by conventional growth processes. The films exhibit electron mobilities as high as 500 cm2/V-s and minority carrier lifetimes as long as 2.5 ns. Furthermore, under 1-sun equivalent illumination, photoluminescence efficiency measurements indicate that an open circuit voltage of up to 930 mV can be achieved, only 40 mV lower than measured on a single crystal reference wafer. PMID:23881474

Weldment for austenitic stainless steel and method

DOEpatents

Bagnall, Christopher; McBride, Marvin A.

1985-01-01

For making defect-free welds for joining two austenitic stainless steel mers, using gas tungsten-arc welding, a thin foil-like iron member is placed between the two steel members to be joined, prior to making the weld, with the foil-like iron member having a higher melting point than the stainless steel members. When the weld is formed, there results a weld nugget comprising melted and then solidified portions of the joined members with small portions of the foil-like iron member projecting into the solidified weld nugget. The portions of the weld nugget proximate the small portions of the foil-like iron member which project into the weld nugget are relatively rich in iron. This causes these iron-rich nugget portions to display substantial delta ferrite during solidification of the weld nugget which eliminates weld defects which could otherwise occur. This is especially useful for joining austenitic steel members which, when just below the solidus temperature, include at most only a very minor proportion of delta ferrite.

[Microfabricated X-ray Optics Technology Development for the Constellation X-Mission

NASA Technical Reports Server (NTRS)

Schattenburg, Mark L.

2005-01-01

MIT has previously developed advanced methods for the application of silicon microstructures (so-called microcombs) in the precision assembly of foil x-ray optics in support of the Constellation-X Spectroscopy X-ray Telescope (SXT) technology development at the NASA Goddard Space Flight Center (GSFC). During the first year of the above Cooperative Agreement, MIT has developed a new, mature, potentially high- yield process for the manufacturing of microcombs that can be applied to a range of substrates independent of thickness. MIT also developed techniques to extract microcomb accuracy from an assembly truss metrology test stand and to extend the dynamic range of its Shack-Hartmann foil metrology tool. The placement repeatability of foil optics with microcombs in the assembly truss has been improved by a factor of two to approximately 0.15 micron. This was achieved by electric contact determination in favor of determining contact through force measurements. Development work on a stress-free thin foil holder was also supported by this agreement and successfully continued under a different grant.

Plasma diagnostics for x-ray driven foils at Z

DOE Office of Scientific and Technical Information (OSTI.GOV)

Heeter, R F; Bailey, J E; Cuneo, M E

We report the development of techniques to diagnose plasmas produced by X-ray photoionization of thin foils placed near the Z-pinch on the Sandia Z Machine. The development of 100+ TW X-ray sources enables access to novel plasma regimes, such as the photoionization equilibrium. To diagnose these plasmas one must simultaneously characterize both the foil and the driving pinch. The desired photoionized plasma equilibrium is only reached transiently for a 2-ns window, placing stringent requirements on diagnostic synchronization. We have adapted existing Sandia diagnostics and fielded an additional gated 3-crystal Johann spectrometer with dual lines of sight to meet these requirements.more » We present sample data from experiments in which 1 cm, 180 eV tungsten pinches photoionized foils composed of 200{angstrom} Fe and 300{angstrom} NaF co-mixed and sandwiched between 1000{angstrom} layers of Lexan (CHO), and discuss the application of this work to benchmarking astrophysical models.« less

Plasma diagnostics for x-ray driven foils at Z

DOE Office of Scientific and Technical Information (OSTI.GOV)

Heeter, R. F.; Bailey, J. E.; Cuneo, M. E.

We report the development of techniques to diagnose plasmas produced by x-ray photoionization of thin foils placed near the Z-pinch on the Sandia Z Machine. The development of 100+ TW x-ray sources enables access to novel plasma regimes, such as the photoionization equilibrium. To diagnose these plasmas one must simultaneously characterize both the foil and the driving pinch. The desired photoionized plasma equilibrium is only reached transiently for a 2-ns window, placing stringent requirements on diagnostic synchronization. We have adapted existing Sandia diagnostics and fielded an additional gated three-crystal Johann spectrometer with dual lines of sight to meet these requirements.more » We present sample data from experiments using 1-cm, 180-eV tungsten pinches to photoionize foils made of 200 Aa Fe and 300 Aa NaF co-mixed and sandwiched between 1000 Aa layers of Lexan (C16H14O3), and discuss the application of this work to benchmarking astrophysical models.« less

Analysis of spectra of 3s-3p and 3p-3d transitions of highly-charged copper ions

NASA Astrophysics Data System (ADS)

Su, M. G.; Min, Q.; He, S. Q.; Wu, L.; Sun, R.; Ding, X. B.; Sun, D. X.

2017-08-01

Beam-foil excited spectra in the range of 160-360 Å from highly charged copper ions were identified with the aid of the National Institute of Standards and Technology Atomic Spectra Database and theoretical calculations with Cowan and Flexible Atomic Code (FAC) calculations. Spectra arising from 3s-3p and 3p-3d transitions of Cu13+-Cu22+ ions were considered. The ion fraction at an ion beam energy of 110 MeV was estimated from the equilibrium charge distribution of the fast ion beams after passing through the solid. The corresponding simulated spectra were in good agreement with the experimental result. Our Cowan and FAC calculation results should be useful for further spectral identification and lifetime measurements of highly charged copper ions.

Single-jet gas cooling of in-beam foils or specimens: Prediction of the convective heat-transfer coefficient

NASA Astrophysics Data System (ADS)

Steyn, Gideon; Vermeulen, Christiaan

2018-05-01

An experiment was designed to study the effect of the jet direction on convective heat-transfer coefficients in single-jet gas cooling of a small heated surface, such as typically induced by an accelerated ion beam on a thin foil or specimen. The hot spot was provided using a small electrically heated plate. Heat-transfer calculations were performed using simple empirical methods based on dimensional analysis as well as by means of an advanced computational fluid dynamics (CFD) code. The results provide an explanation for the observed turbulent cooling of a double-foil, Havar beam window with fast-flowing helium, located on a target station for radionuclide production with a 66 MeV proton beam at a cyclotron facility.

Investigation of the aluminium-aluminium oxide reversible transformation as observed by hot stage electron microscopy.

NASA Technical Reports Server (NTRS)

Grove, C. A.; Judd, G.; Ansell, G. S.

1972-01-01

Thin foils of high purity aluminium and an Al-Al2O3 SAP type of alloy were oxidised in a specially designed hot stage specimen chamber in an electron microscope. Below 450 C, amorphous aluminium oxide formed on the foil surface and was first detectable at foil edges, holes, and pits. Islands of aluminium then nucleated in this amorphous oxide. The aluminium islands displayed either a lateral growth with eventual coalescence with other islands, or a reoxidation process which caused the islands to disappear. The aluminium island formation was determined to be related to the presence of the electron beam. A mechanism based upon electron charging due to the electron beam was proposed to explain the nucleation, growth, coalescence, disappearance, and geometry of the aluminium islands.

Novel target design for enhanced laser driven proton acceleration

NASA Astrophysics Data System (ADS)

Dalui, Malay; Kundu, M.; Tata, Sheroy; Lad, Amit D.; Jha, J.; Ray, Krishanu; Krishnamurthy, M.

2017-09-01

We demonstrate a simple method of preparing structured target for enhanced laser-driven proton acceleration under target-normal-sheath-acceleration scheme. A few layers of genetically modified, clinically grown micron sized E. Coli bacteria cell coated on a thin metal foil has resulted in an increase in the maximum proton energy by about 1.5 times and the total proton yield is enhanced by approximately 25 times compared to an unstructured reference foil at a laser intensity of 1019 W/cm2. Particle-in-cell simulations on the system shows that the structures on the target-foil facilitates anharmonic resonance, contributing to enhanced hot electron production which leads to stronger accelerating field. The effect is observed to grow as the number of structures is increased in the focal area of the laser pulse.

Tribological performance of monolithic copper thin films during nanowear

DOE PAGES

Schultz, Bradley M.; Li, Nan; Economy, David R.; ...

2017-10-07

Mathematical models suggest that the strain along the film formed by parallel passes of a nanoindentation probe in contact with the film can be either homogenous or heterogeneous, depending on contact pressure and spacing between passes. Here, in this study, a 1 µm copper thin film was worn with a cono-spherical diamond probe with normal loads ranging from 25 to 800 µN and wear box edge lengths of 40, 60, and 80 µm. The nanoindenter counterface was rastered across the surface to mimic dry sliding wear. To determine potential strain field changes, 10-step quasi-static indents (200–2000 µN) were performed usingmore » nanoindentation inside the wear boxes created at various loads to determine if a strain field alteration could be observed in changes in hardness of the copper thin film. It was shown that there was a softening effect in the hardness for normal loads < 400 µN used during nanowear compared to the as-deposited copper. Normal loads ≥ 400 µN had a similar or higher hardness than the as-deposited copper. This is believed to have occurred due to a relaxation in the residual stresses created during deposition in the copper thin films at lower loads, which caused a decrease in hardness. Conversely, at the higher loads, increased deformation leads to an increase in hardness. Lastly, all of the wear boxes displayed a higher estimated strain hardening exponent than the as-deposited material.« less

Mechanical tearing of graphene on an oxidizing metal surface.

PubMed

George, Lijin; Gupta, Aparna; Shaina, P R; Das Gupta, Nandita; Jaiswal, Manu

2015-12-11

Graphene, the thinnest possible anticorrosion and gas-permeation barrier, is poised to transform the protective coatings industry for a variety of surface applications. In this work, we have studied the structural changes of graphene when the underlying copper surface undergoes oxidation upon heating. Single-layer graphene directly grown on a copper surface by chemical vapour deposition was annealed under ambient atmosphere conditions up to 400 °C. The onset temperature of the surface oxidation of copper is found to be higher for graphene-coated foils. Parallel arrays of graphene nanoripples are a ubiquitous feature of pristine graphene on copper, and we demonstrate that these form crucial sites for the onset of the oxidation of copper, particularly for ∼0.3-0.4 μm ripple widths. In these regions, the oxidation proceeds along the length of the nanoripples, resulting in the formation of parallel stripes of oxidized copper regions. We demonstrate from temperature-dependent Raman spectroscopy that the primary defect formation process in graphene involves boundary-type defects rather than vacancy or sp(3)-type defects. This observation is consistent with a mechanical tearing process that splits graphene into small polycrystalline domains. The size of these is estimated to be sub-50 nm.

GRAPHITE BONDING METHOD

DOEpatents

King, L.D.P.

1964-02-25

A process for bonding or joining graphite members together in which a thin platinum foil is placed between the members, heated in an inert atmosphere to a temperature of 1800 deg C, and then cooled to room temperature is described. (AEC)

Definition of the Spatial Resolution of X-Ray Microanalysis in Thin Foils

NASA Technical Reports Server (NTRS)

Williams, D. B.; Michael, J. R.; Goldstein, J. I.; Romig, A. D., Jr.

1992-01-01

The spatial resolution of X-ray microanalysis in thin foils is defined in terms of the incident electron beam diameter and the average beam broadening. The beam diameter is defined as the full width tenth maximum of a Gaussian intensity distribution. The spatial resolution is calculated by a convolution of the beam diameter and the average beam broadening. This definition of the spatial resolution can be related simply to experimental measurements of composition profiles across interphase interfaces. Monte Carlo calculations using a high-speed parallel supercomputer show good agreement with this definition of the spatial resolution and calculations based on this definition. The agreement is good over a range of specimen thicknesses and atomic number, but is poor when excessive beam tailing distorts the assumed Gaussian electron intensity distributions. Beam tailing occurs in low-Z materials because of fast secondary electrons and in high-Z materials because of plural scattering.

Photo-Induced Room-Temperature Gas Sensing with a-IGZO Based Thin-Film Transistors Fabricated on Flexible Plastic Foil.

PubMed

Knobelspies, Stefan; Bierer, Benedikt; Daus, Alwin; Takabayashi, Alain; Salvatore, Giovanni Antonio; Cantarella, Giuseppe; Ortiz Perez, Alvaro; Wöllenstein, Jürgen; Palzer, Stefan; Tröster, Gerhard

2018-01-26

We present a gas sensitive thin-film transistor (TFT) based on an amorphous Indium-Gallium-Zinc-Oxide (a-IGZO) semiconductor as the sensing layer, which is fabricated on a free-standing flexible polyimide foil. The photo-induced sensor response to NO₂ gas at room temperature and the cross-sensitivity to humidity are investigated. We combine the advantages of a transistor based sensor with flexible electronics technology to demonstrate the first flexible a-IGZO based gas sensitive TFT. Since flexible plastic substrates prohibit the use of high operating temperatures, the charge generation is promoted with the help of UV-light absorption, which ultimately triggers the reversible chemical reaction with the trace gas. Furthermore, the device fabrication process flow can be directly implemented in standard TFT technology, allowing for the parallel integration of the sensor and analog or logical circuits.

Thin Shell, Segmented X-Ray Mirrors

NASA Technical Reports Server (NTRS)

Petre, Robert

2010-01-01

Thin foil mirrors were introduced as a means of achieving high throughput in an X-ray astronomical imaging system in applications for which high angular resolution were not necessary. Since their introduction, their high filling factor, modest mass, relative ease of construction, and modest cost have led to their use in numerous X-ray observatories, including the Broad Band X-ray Telescope, ASCA, and Suzaku. The introduction of key innovations, including epoxy replicated surfaces, multilayer coatings, and glass mirror substrates, has led to performance improvements, and in their becoming widely used for X-ray astronomical imaging at energies above 10 keV. The use of glass substrates has also led to substantial improvement in angular resolution, and thus their incorporation into the NASA concept for the International X-ray Observatory with a planned 3 in diameter aperture. This paper traces the development of foil mirrors from their inception in the 1970's through their current and anticipated future applications.

Strong electromagnetic pulses generated in laser-matter interactions with 10TW-class fs laser

NASA Astrophysics Data System (ADS)

Rączka, Piotr; Rosiński, Marcin; Zaraś-Szydłowska, Agnieszka; Wołowski, Jerzy; Badziak, Jan

2018-01-01

The results of an experiment on the generation of electromagnetic pulses (EMP) in the interaction of 10TW fs pulses with thick (mm scale) and thin foil (μm scale) targets are described. Such pulses, with frequencies in the GHz range, may pose a threat to safe and reliable operation of high-power, high-intensity laser facilities. The main point of the experiment is to investigate the fine temporal structure of such pulses using an oscilloscope capable of measurements at very high sampling rate. It is found that the amazing reproducibility of such pulses is confirmed at this high sampling rate. Furthermore, the differences between the EMP signals generated from thick and thin foil targets are clearly seen, which indicates that besides electric polarization of the target and the target neutralization current there may be other factors essential for the EMP emission.

Photo-Induced Room-Temperature Gas Sensing with a-IGZO Based Thin-Film Transistors Fabricated on Flexible Plastic Foil

PubMed Central

Bierer, Benedikt; Takabayashi, Alain; Ortiz Perez, Alvaro; Wöllenstein, Jürgen

2018-01-01

We present a gas sensitive thin-film transistor (TFT) based on an amorphous Indium–Gallium–Zinc–Oxide (a-IGZO) semiconductor as the sensing layer, which is fabricated on a free-standing flexible polyimide foil. The photo-induced sensor response to NO2 gas at room temperature and the cross-sensitivity to humidity are investigated. We combine the advantages of a transistor based sensor with flexible electronics technology to demonstrate the first flexible a-IGZO based gas sensitive TFT. Since flexible plastic substrates prohibit the use of high operating temperatures, the charge generation is promoted with the help of UV-light absorption, which ultimately triggers the reversible chemical reaction with the trace gas. Furthermore, the device fabrication process flow can be directly implemented in standard TFT technology, allowing for the parallel integration of the sensor and analog or logical circuits. PMID:29373524

Preparation of osmium targets with carbon backing

NASA Astrophysics Data System (ADS)

Fremont, Georges; Ngono-Ravache, Yvette; Schmitt, Christelle; Stodel, Christelle

2018-05-01

For nuclear reaction studies, thin metallic osmium targets, either natural or isotopically enriched (Os-192) of 200-300 µg/cm2 thicknesses deposited on a thin carbon backing are required. A challenging method was successfully performed at GANIL involving firstly the preparation of an aqueous solution of osmium tetrachloride, then its electro-deposition onto a thick copper backing (100 µm); this process was followed by the evaporation of a thin carbon layer (≈40 µg/cm²) and finally the dissolution of the copper material.

Scattering effects in passive foil focusing of ion beams

DOE PAGES

Yuen, Albert; Lund, Steven M.; Barnard, John J.; ...

2015-09-11

A stack of thin, closely spaced conducting foils has been investigated by Lund et al. [ Phys. Rev. ST Accel. Beams 16, 044202 (2013)] as a passive focusing lens for intense ion beams. The foils mitigate space-charge defocusing forces to enable the beam self-magnetic field to focus. In this study, we analyze possible degradation of focusing due to scattering of beam ions resulting from finite foil thickness using an envelope model and numerical simulations with the particle-in-cell code WARP. Ranges of kinetic energy where scattering effects are sufficient to destroy passive focusing are quantified. The scheme may be utilized tomore » focus protons produced in intense laser-solid accelerator schemes. The spot size of an initially collimated 30 MeV proton beam with initial rms radius 200 μm, perveance Q=1.8×10 -2, and initial transverse emittance ϵ x,rms=0.87 mm mrad propagating through a stack of 6.4 μm thick foils, spaced 100 μm apart, gives a 127.5 μm spot with scattering and a 81.0 μm spot without scattering, illustrating the importance of including scattering effects.« less

Fabrication of flower-like micro/nano dual scale structured copper oxide surfaces: Optimization of self-cleaning properties via Taguchi design

NASA Astrophysics Data System (ADS)

Moosavi, Saeideh Sadat; Norouzbeigi, Reza; Velayi, Elmira

2017-11-01

In the present work, copper oxide superhydrophobic surface is fabricated on a copper foil via the chemical bath deposition (CBD) method. The effects of some influential factors such as initial concentrations of Cu (II) ions and the surface energy modifier, solution pH, reaction and modification steps time on the wettability property of copper oxide surface were evaluated using Taguchi L16 experimental design. Results showed that the initial concentration of Cu (II) has the most significant impact on the water contact angle and wettability characteristics. The XRD, SEM, AFM and FTIR analyses were used to characterize the copper oxide surfaces. The Water contact angle (WCA) and contact angle hysteresis (CAH) were also measured. The SEM results indicated the formation of a flower-like micro/nano dual-scale structure of copper oxide on the substrate. This structure composed of numerous nano-petals with a thickness of about 50 nm. As a result, a copper oxide hierarchical surface with WCA of 168.4°± 3.5° and CAH of 2.73° exhibited the best superhydrophobicity under proposed optimum condition. This result has been obtained just by 10 min hydrolysis reaction. Besides, this surface showed a good stability under acidic and saline conditions.

CIGS2 Thin-Film Solar Cells on Flexible Foils for Space Power

NASA Technical Reports Server (NTRS)

Dhere, Neelkanth G.; Ghongadi, Shantinath R.; Pandit, Mandar B.; Jahagirdar, Anant H.; Scheiman, David

2002-01-01

CuIn(1-x)Ga(x)S2 (CIGS2) thin-film solar cells are of interest for space power applications because of the near optimum bandgap for AM0 solar radiation in space. CIGS2 thin film solar cells on flexible stainless steel (SS) may be able to increase the specific power by an order of magnitude from the current level of 65 Wkg(sup -1). CIGS solar cells are superior to the conventional silicon and gallium arsenide solar cells in the space radiation environment. This paper presents research efforts for the development of CIGS2 thin-film solar cells on 127 micrometers and 20 micrometers thick, bright-annealed flexible SS foil for space power. A large-area, dual-chamber, inline thin film deposition system has been fabricated. The system is expected to provide thickness uniformity of plus or minus 2% over the central 5" width and plus or minus 3% over the central 6" width. During the next phase, facilities for processing larger cells will be acquired for selenization and sulfurization of metallic precursors and for heterojunction CdS layer deposition both on large area. Small area CIGS2 thin film solar cells are being prepared routinely. Cu-rich Cu-Ga/In layers were sputter-deposited on unheated Mo-coated SS foils from CuGa (22%) and In targets. Well-adherent, large-grain Cu-rich CIGS2 films were obtained by sulfurization in a Ar: H2S 1:0.04 mixture and argon flow rate of 650 sccm, at the maximum temperature of 475 C for 60 minutes with intermediate 30 minutes annealing step at 120 C. Samples were annealed at 500 C for 10 minutes without H2S gas flow. The intermediate 30 minutes annealing step at 120 C was changed to 135 C. p-type CIGS2 thin films were obtained by etching the Cu-rich layer segregated at the surface using dilute KCN solution. Solar cells were completed by deposition of CdS heterojunction partner layer by chemical bath deposition, transparent-conducting ZnO/ZnO: Al window bilayer by RF sputtering, and vacuum deposition of Ni/Al contact fingers through metal mask. PV parameters of a CIGS2 solar cell on 127 micrometers thick SS flexible foil measured under AM 0 conditions at NASA GRC were: V(sub oc) = 802.9 mV, J(sub sc) = 25.07 mA per square centimeters, FF = 60.06%, and efficiency 0 = 8.84%. For this cell, AM 1.5 PV parameters measured at NREL were: V(sub oc) = 788 mV, J(sub sc) = 19.78 mA per square centimeter, FF = 59.44%, efficiency 0 = 9.26%. Quantum efficiency curve showed a sharp QE cutoff equivalent to CIGS2 bandgap of approximately 1.50 eV, fairly close to the optimum value for efficient AM0 PV conversion in the space.

Instellar Gas Experiment (IGE): Testing interstellar gas particles to provide information on the processes of nucleosynthesis in the big bang stars and supernova

NASA Technical Reports Server (NTRS)

Lind, Don

1985-01-01

The Interstellar Gas Experiment (IGE) is designed to collect particles of the interstellar gas - a wind of interstellar media particles moving in the vicinity of the solar system. These particles will be returned to earth where the isotopic ratios of the noble gases among these particles will be measured. IGE was designed and programmed to expose 7 sets of six copper-beryllium metallic collecting foils to the flux of neutral interstellar gas particles which penetrate the heliosphere to the vicinity of the earth's orbit. These particles are trapped in the collecting foils and will be returned to earth for mass-spectrographic analysis when Long Duration Exposure Facility (LDEF) on which IGE was launched, is recovered.

A heater made from graphite composite material for potential deicing application

NASA Technical Reports Server (NTRS)

Hung, C. C.; Stahl, M.; Stahl, M.; Stahl, M.

1986-01-01

A surface heater was developed using a graphite fiber-epoxy composite as the heating element. This heater can be thin, highly electrically and thermally conductive, and can conform to an irregular surface. Therefore it may be used in an aircraft's thermal deicing system to quickly and uniformly heat the aircraft surface. One-ply of unidirectional graphite fiber-epoxy composite was laminated between two plies of fiber glass-epoxy composite, with nickel foil contacting the end portions of the composite and partly exposed beyond the composites for electrical contact. The model heater used brominated P-100 fibers from Amoco. The fiber's electrical resistivity, thermal conductivity and density were 50 micro ohms per centimeter, 270 W/m-K and 2.30 gm/cubic cm, respectively. The electricity was found to penetrate through the composite in the transverse direction to make an acceptably low foil-composite contact resistance. When conducting current, the heater temperature increase reached 50 percent of the steady state value within 20 sec. There was no overheating at the ends of the heater provided there was no water corrosion. If the foil-composite bonding failed during storage, liquid water exposure was found to oxidize the foil. Such bonding failure may be avoided if perforated nickel foil is used, so that the composite plies can bond to each other through the perforated holes and therefore lock the foil in place.

Cyclotron production of {sup 61}Cu using natural Zn and enriched {sup 64}Zn targets

DOE Office of Scientific and Technical Information (OSTI.GOV)

Asad, A. H.; Smith, S. V.; Chan, S.

2012-12-19

Copper-61 ({sup 61}Cu) shares with {sup 64}Cu certain advantages for PET diagnostic imaging, but has a shorter half-life (3.4hr vs. 12.7hr) and a greater probability of positron production per disintegration (61% vs. 17.9%). One important application is for in vivo imaging of hypoxic tissue. In this study {sup 61}Cu was produced using the {sup 64}Zn(p,{alpha}){sup 61}Cu reaction on natural Zn or enriched {sup 64}Zn targets. The enriched {sup 64}Zn (99.82%) was electroplated onto high purity gold or silver foils or onto thin Al discs. A typical target bombardment used 30{mu}A; at 11.7, 14.5 or 17.6MeV over 30-60min. The {sup 61}Cumore » (radiochemical purity of >95%) was separated using a combination of cation and anion exchange columns. The {sup 64}Zn target material was recovered after each run, for re-use. In a direct comparison with enriched {sup 64}Zn-target results, {sup 61}Cu production using the cheaper {sup nat}Zn target proved to be an effective alternative.« less

Development of the apparatus for measuring magnetic properties of electrical steel sheets in arbitrary directions under compressive stress normal to their surface

NASA Astrophysics Data System (ADS)

Maeda, Yoshitaka; Urata, Shinya; Nakai, Hideo; Takeuchi, Yuuya; Yun, Kyyoul; Yanase, Shunji; Okazaki, Yasuo

2017-05-01

In designing motors, one must grasp the magnetic properties of electrical steel sheets considering actual conditions in motors. Especially important is grasping the stress dependence of magnetic power loss. This paper describes a newly developed apparatus to measure two-dimensional (2-D) magnetic properties (properties under the arbitrary alternating and the rotating flux conditions) of electrical steel sheets under compressive stress normal to the sheet surface. The apparatus has a 2-D magnetic excitation circuit to generate magnetic fields in arbitrary directions in the evaluation area. It also has a pressing unit to apply compressive stress normal to the sheet surface. During measurement, it is important to apply uniform stress throughout the evaluation area. Therefore, we have developed a new flux density sensor using needle probe method. It is composed of thin copper foils sputtered on electrical steel sheets. By using this sensor, the stress can be applied to the surface of the specimen without influence of this sensor. This paper described the details of newly developed apparatus with this sensor, and measurement results of iron loss by using are shown.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Jankowski, A.F.; Hayes, J.P.; Kanna, R.L.

The formation of high energy density, storage devices is achievable using composite material systems. Alternate layering of carbon aerogel wafers and Ni foils with rnicroporous separators is a prospective composite for capacitor applications. An inherent problem exists to form a physical bond between Ni and the porous carbon wafer. The bonding process must be limited to temperatures less than 1000{degrees}C, at which point the aerogel begins to degrade. The advantage of a low temperature eutectic in the Ni-Ti alloy system solves this problem. Ti, a carbide former, is readily adherent as a sputter deposited thin film onto the carbon wafer.more » A vacuum bonding process is then used to join the Ni foil and Ti coating through eutectic phase formation. The parameters required for successfld bonding are described along with a structural characterization of the Ni foil-carbon aerogel wafer interface.« less

Near monochromatic 20 Me V proton acceleration using fs laser irradiating Au foils in target normal sheath acceleration regime

DOE Office of Scientific and Technical Information (OSTI.GOV)

Torrisi, L., E-mail: Lorenzo.Torrisi@unime.it; Ceccio, G.; Cannavò, A.

2016-04-15

A 200 mJ laser pulse energy, 39 fs-pulse duration, 10 μm focal spot, p-polarized radiation has been employed to irradiate thin Au foils to produce proton acceleration in the forward direction. Gold foils were employed to produce high density relativistic electrons emission in the forward direction to generate a high electric field driving the ion acceleration. Measurements were performed by changing the focal position in respect of the target surface. Proton acceleration was monitored using fast SiC detectors in time-of-flight configuration. A high proton energy, up to about 20 Me V, with a narrow energy distribution, was obtained in particular conditions dependingmore » on the laser parameters, the irradiation conditions, and a target optimization.« less

Non-destructive evaluation of nano-sized structure of thin film devices by using small angle neutron scattering.

PubMed

Shin, E J; Seong, B S; Choi, Y; Lee, J K

2011-01-01

Nano-sized multi-layers copper-doped SrZrO3, platinum (Pt) and silicon oxide (SiO2) on silicon substrates were prepared by dense plasma focus (DPF) device with the high purity copper anode tip and analyzed by using small angle neutron scattering (SANS) to establish a reliable method for the non-destructive evaluation of the under-layer structure. Thin film was well formed at the time-to-dip of 5 microsec with stable plasma of DPF. Several smooth intensity peaks were periodically observed when neutron beam penetrates the thin film with multi-layers perpendicularly. The platinum layer is dominant to intensity peaks, where the copper-doped SrZnO3 layer next to the platinum layer causes peak broadening. The silicon oxide layer has less effect on the SANS spectra due to its relative thick thickness. The SANS spectra shows thicknesses of platinum and copper-doped SrZnO3 layers as 53 and 25 nm, respectively, which are well agreement with microstructure observation.

Weld Repair of Thin Aluminum Sheet

NASA Technical Reports Server (NTRS)

Beuyukian, C. S.; Mitchell, M. J.

1986-01-01

Weld repairing of thin aluminum sheets now possible, using niobium shield and copper heat sinks. Refractory niobium shield protects aluminum adjacent to hole, while copper heat sinks help conduct heat away from repair site. Technique limits tungsten/inert-gas (TIG) welding bombardment zone to melt area, leaving surrounding areas around weld unaffected. Used successfully to repair aluminum cold plates on Space Shuttle, Commercial applications, especially in sealing fractures, dents, and holes in thin aluminum face sheets or clad brazing sheet in cold plates, heat exchangers, coolers, and Solar panels. While particularly suited to thin aluminum sheet, this process also used in thicker aluminum material to prevent surface damage near weld area.

Copper-Zinc-Tin-Sulfur Thin Film Using Spin-Coating Technology

PubMed Central

Yeh, Min-Yen; Lei, Po-Hsun; Lin, Shao-Hsein; Yang, Chyi-Da

2016-01-01

Cu2ZnSnS4 (CZTS) thin films were deposited on glass substrates by using spin-coating and an annealing process, which can improve the crystallinity and morphology of the thin films. The grain size, optical gap, and atomic contents of copper (Cu), zinc (Zn), tin (Sn), and sulfur (S) in a CZTS thin film absorber relate to the concentrations of aqueous precursor solutions containing copper chloride (CuCl2), zinc chloride (ZnCl2), tin chloride (SnCl2), and thiourea (SC(NH2)2), whereas the electrical properties of CZTS thin films depend on the annealing temperature and the atomic content ratios of Cu/(Zn + Sn) and Zn/Sn. All of the CZTS films were characterized using X-ray diffraction (XRD), scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy (EDXS), Raman spectroscopy, and Hall measurements. Furthermore, CZTS thin film was deposited on an n-type silicon substrate by using spin-coating to form an Mo/p-CZTS/n-Si/Al heterostructured solar cell. The p-CZTS/n-Si heterostructured solar cell showed a conversion efficiency of 1.13% with Voc = 520 mV, Jsc = 3.28 mA/cm2, and fill-factor (FF) = 66%. PMID:28773647

Large local lattice expansion in graphene adlayers grown on copper

NASA Astrophysics Data System (ADS)

Chen, Chaoyu; Avila, José; Arezki, Hakim; Nguyen, Van Luan; Shen, Jiahong; Mucha-Kruczyński, Marcin; Yao, Fei; Boutchich, Mohamed; Chen, Yue; Lee, Young Hee; Asensio, Maria C.

2018-05-01

Variations of the lattice parameter can significantly change the properties of a material, and, in particular, its electronic behaviour. In the case of graphene, however, variations of the lattice constant with respect to graphite have been limited to less than 2.5% due to its well-established high in-plane stiffness. Here, through systematic electronic and lattice structure studies, we report regions where the lattice constant of graphene monolayers grown on copper by chemical vapour deposition increases up to 7.5% of its relaxed value. Density functional theory calculations confirm that this expanded phase is energetically metastable and driven by the enhanced interaction between the substrate and the graphene adlayer. We also prove that this phase possesses distinctive chemical and electronic properties. The inherent phase complexity of graphene grown on copper foils revealed in this study may inspire the investigation of possible metastable phases in other seemingly simple heterostructure systems.

In situ hydride formation in titanium during focused ion milling.

PubMed

Ding, Rengen; Jones, Ian P

2011-01-01

It is well known that titanium and its alloys are sensitive to electrolytes and thus hydrides are commonly observed in electropolished foils. In this study, focused ion beam (FIB) milling was used to prepare thin foils of titanium and its alloys for transmission electron microscopy. The results show the following: (i) titanium hydrides were observed in pure titanium, (ii) the preparation of a bulk sample in water or acid solution resulted in the formation of more hydrides and (iii) FIB milling aids the precipitation of hydrides, but there were never any hydrides in Ti64 and Ti5553.

Innovative space x-ray telescopes

NASA Astrophysics Data System (ADS)

Hudec, R.; Inneman, A.; Pina, L.; Sveda, L.; Ticha, H.; Brozek, V.

2017-11-01

We report on the progress in innovative X-ray mirror development with focus on requirements of future X-ray astronomy space projects. Various future projects in X-ray astronomy and astrophysics will require large lightweight but highly accurate segments with multiple thin shells or foils. The large Wolter 1 grazing incidence multiple mirror arrays, the Kirkpatrick-Baez modules, as well as the large Lobster-Eye X-ray telescope modules in Schmidt arrangement may serve as examples. All these space projects will require high quality and light segmented shells (shaped, bent or flat foils) with high X-ray reflectivity and excellent mechanical stability.

Electronic and Physical Characterization of Hydrothermally Grown Single Crystal ThO2

DTIC Science & Technology

2013-12-26

35 BNL Brookhaven National Laboratories . . . . . . . . . . . . . . . . . . . . . . . . . . . 39 VBM valence band maximum...Newton’s method. As an example, EXAFS data from Brookhaven National Laboratories ( BNL ) is analyzed. The data is from a thin metal Cu foil. A reasonable

Plasma impact on structural, morphological and optical properties of copper acetylacetonate thin films

NASA Astrophysics Data System (ADS)

Abdel-Khalek, H.; El-Samahi, M. I.; El-Mahalawy, Ahmed M.

2018-06-01

The influence of plasma exposure on structural, morphological and optical properties of copper (II) acetylacetonate thin films deposited by thermal evaporation technique was investigated. Copper (II) acetylacetonate as-grown thin films were exposed to the atmospheric plasma for different times. The exposure of as-grown cu(acac)2 thin film to atmospheric plasma for 5 min modified its structural, morphological and optical properties. The effect of plasma exposure on structure and roughness of cu(acac)2 thin films was evaluated by XRD and AFM techniques, respectively. The XRD results showed an increment in crystallinity due to exposure for 5 min, but, when the exposure time reaches 10 min, the film was transformed to an amorphous state. The AFM results revealed a strong modification of films roughness when the average roughness decreased from 63.35 nm to 1 nm as a result of interaction with plasma. The optical properties of as-grown and plasma exposured cu(acac)2 thin films were studied using spectrophotometric method. The exposure of cu(acac)2 thin films to plasma produced the indirect energy gap decrease from 3.20 eV to 2.67 eV for 10 min exposure time. The dispersion parameters were evaluated in terms of single oscillator model for as-grown and plasma exposured thin films. The influence of plasma exposure on third order optical susceptibility was studied.

Synthesis, Transfer, and Characterization of Nanoscale 2-Dimensional Materials

DTIC Science & Technology

2015-09-01

deposition systems, leading to reduced operating costs. Transfer has been achieved using polymer-assisted methods , and material quality has been...Introduction and Background 1 2. Materials and Methods 1 3. Results and Discussion 2 3.1 Copper Foil Preparation 2 3.2 Graphene Synthesis and...magnification. a) 10 K, b) 18 K, c) 20 K, and d) 40 K. The red arrows indicate wrinkles in the film

Dissolution of brominated epoxy resins by dimethyl sulfoxide to separate waste printed circuit boards.

PubMed

Zhu, Ping; Chen, Yan; Wang, Liangyou; Qian, Guangren; Zhang, Wei Jie; Zhou, Ming; Zhou, Jin

2013-03-19

Improved methods are required for the recycling of waste printed circuit boards (WPCBs). In this study, WPCBs (1-1.5 cm(2)) were separated into their components using dimethyl sulfoxide (DMSO) at 60 °C for 45 min and a metallographic microscope was used to verify their delamination. An increased incubation time of 210 min yielded a complete separation of WPCBs into their components, and copper foils and glass fibers were obtained. The separation time decreased with increasing temperature. When the WPCB size was increased to 2-3 cm(2), the temperature required for complete separation increased to 90 °C. When the temperature was increased to 135 °C, liquid photo solder resists could be removed from the copper foil surfaces. The DMSO was regenerated by rotary decompression evaporation, and residues were obtained. Fourier transform infrared spectroscopy (FT-IR), thermal analysis, nuclear magnetic resonance, scanning electron microscopy, and energy-dispersive X-ray spectroscopy were used to verify that these residues were brominated epoxy resins. From FT-IR analysis after the dissolution of brominated epoxy resins in DMSO it was deduced that hydrogen bonding may play an important role in the dissolution mechanism. This novel technology offers a method for separating valuable materials and preventing environmental pollution from WPCBs.

Generation of metallic plasmon nanostructures in a thin transparent photosensitive copper oxide film by femtosecond thermochemical decomposition

NASA Astrophysics Data System (ADS)

Danilov, P. A.; Zayarny, D. A.; Ionin, A. A.; Kudryashov, S. I.; Litovko, E. P.; Mel'nik, N. N.; Rudenko, A. A.; Saraeva, I. N.; Umanskaya, S. P.; Khmelnitskii, R. A.

2017-09-01

Irradiation of optically transparent copper (I) oxide film covering a glass substrate with a tightly focused femtosecond laser pulses in the pre-ablation regime leads to film reduction to a metallic colloidal state via a single-photon absorption and its subsequent thermochemical decomposition. This effect was demonstrated by the corresponding measurement of the extinction spectrum in visible spectral range. The laser-induced formation of metallic copper nanoparticles in the focal region inside the bulk oxide film allows direct recording of individual thin-film plasmon nanostructures and optical-range metasurfaces.

Long pulse Soft X-ray Emission from Laser Generated Irradiated Gold Foils

NASA Astrophysics Data System (ADS)

Davis, Joshua; Frank, Yechiel; Raicher, Erez; Fraenkel, Moshe; Keiter, Paul; Klein, Sallee; Drake, R. P.; Shvarts, Dov

2016-10-01

Long pulse soft x-ray sources (SXS) allow for flexibility in high-energy-density experimental designs by providing a means of driving matter to the high temperatures needed, for example to study radiation waves in different materials. SXSs can be made by using lasers to heat a high-Z thin foil, which then acts as a quasi-blackbody emitter. Previous studies of the x-ray emission characteristics of gold foils have focused on laser pulses of 1ns or less. We performed experiments using a 6.0ns laser pulse with energy of 2kJ on the Omega-60 system to generate and characterize multi-ns laser heated Au foils of thicknesses between 0.5-2.0 μm. We measured the 2D spatial profile of the emission with a soft x-ray camera and the time history of the emission with the Dante photodiode array . Effective temperatures for the emission were then calculated using the Dante measurements. Discussion of experimental results and a comparison with 1-D Rad-Hydro NLTE simulations will be presented.

Apparatus and method for treating a cathode material provided on a thin-film substrate

DOEpatents

Hanson, Eric J.; Kooyer, Richard L.

2001-01-01

An apparatus and method for treating a cathode material provided on a surface of a continuous thin-film substrate and a treated thin-film cathode having increased smoothness are disclosed. A web of untreated cathode material is moved between a feed mechanism and a take-up mechanism, and passed through a treatment station. The web of cathode material typically includes areas having surface defects, such as prominences extending from the surface of the cathode material. The surface of the cathode material is treated with an abrasive material to reduce the height of the prominences so as to increase an 85 degree gloss value of the cathode material surface by at least approximately 10. The web of cathode material may be subjected to a subsequent abrasive treatment at the same or other treatment station. Burnishing or lapping film is employed at a treatment station to process the cathode material. An abrasive roller may alternatively be used to process the web of cathode material. The apparatus and method of the present invention may also be employed to treat the surface of a lithium anode foil so as to cleanse and reduce the roughness of the anode foil surface.

Apparatus and method for treating a cathode material provided on a thin-film substrate

DOEpatents

Hanson, Eric J.; Kooyer, Richard L.

2003-01-01

An apparatus and method for treating a cathode material provided on a surface of a continuous thin-film substrate and a treated thin-film cathode having increased smoothness are disclosed. A web of untreated cathode material is moved between a feed mechanism and a take-up mechanism, and passed through a treatment station. The web of cathode material typically includes areas having surface defects, such as prominences extending from the surface of the cathode material. The surface of the cathode material is treated with an abrasive material to reduce the height of the prominences so as to increase an 85 degree gloss value of the cathode material surface by at least approximately 10. The web of cathode material may be subjected to a subsequent abrasive treatment at the same or other treatment station. Burnishing or lapping film is employed at a treatment station to process the cathode material. An abrasive roller may alternatively be used to process the web of cathode material. The apparatus and method of the present invention may also be employed to treat the surface of a lithium anode foil so as to cleanse and reduce the roughness of the anode foil surface.

Calibration of thin-foil manganin gauge in ALOX material

NASA Astrophysics Data System (ADS)

Benham, R. A.; Weirick, L. J.; Lee, L. M.

1996-05-01

The purpose of this program was to develop a calibration curve (stress as a function of change in gauge resistance/gauge resistance) and to obtain gauge repeatability data for Micro-Measurements stripped manganin thin-foiled gauges up to 6.1 GPa in ALOX (42% by volume alumina in Epon 828 epoxy) material. A light-gas gun was used to drive an ALOX impactor into the ALOX target containing four gauges in a centered diamond arrangement. Tilt and velocity of the impactor were measured along with the gauge outputs. Impact stresses from 0.5 to 6.1 GPa were selected in increments of 0.7 GPa with duplicate tests done at 0.5, 3.3 and 6.1 GPa. A total of twelve tests was conducted using ALOX. Three initial tests were done using polymethyl methacrylate (PMMA) as the impactor and target at an impact pressure of 3.0 GPa for comparison of gauge output with analysis and literature values. The installed gauge, stripped of its backing, has a nominal thickness of 5 μm. The thin gauge and high speed instrumentation allowed higher time resolution measurements than can be obtained with manganin wire.

Auger electron spectroscopy and x-ray photoelectron spectroscopy of the biocorrosion of copper by Gum Arabic, BCS and Pseudomonas atlantica exopolymer

DOE Office of Scientific and Technical Information (OSTI.GOV)

Jolley, J.G.; Geesey, G.G.; Hankins, M.R.

1987-01-01

Thin films (3.4 nm) of copper on germanium substrates were exposed to 10% Gum Arabic aqueous solution, 1% BCS (aqueous and simulated sea water solutions) and 0.5% Pseudomonas atlantica exopolymer (aqueous and simulated sea water solutions). Pre- and post-exposure characterization were done by Auger electron spectroscopy and x-ray photoelectron spectroscopy. Ancillary graphite furnace atomic absorption spectroscopy was used to monitor the removal process of the copper thin film from the germanium substrate. Results indicate that the copper was oxidized by the Gum Arabic and BCS, and some was removed from the Cu/Ge interface by all three polymers and incorporated intomore » the polymer matrix. Thus biocorrosion of copper was exhibited by the Gum Arabic, BCS and Pseudomonas atlantica exopolymer. 14 refs., 4 figs., 3 tabs.« less

Low-Temperature Oxidation-Free Selective Laser Sintering of Cu Nanoparticle Paste on a Polymer Substrate for the Flexible Touch Panel Applications.

PubMed

Kwon, Jinhyeong; Cho, Hyunmin; Eom, Hyeonjin; Lee, Habeom; Suh, Young Duk; Moon, Hyunjin; Shin, Jaeho; Hong, Sukjoon; Ko, Seung Hwan

2016-05-11

Copper nanomaterials suffer from severe oxidation problem despite the huge cost effectiveness. The effect of two different processes for conventional tube furnace heating and selective laser sintering on copper nanoparticle paste is compared in the aspects of chemical, electrical and surface morphology. The thermal behavior of the copper thin films by furnace and laser is compared by SEM, XRD, FT-IR, and XPS analysis. The selective laser sintering process ensures low annealing temperature, fast processing speed with remarkable oxidation suppression even in air environment while conventional tube furnace heating experiences moderate oxidation even in Ar environment. Moreover, the laser-sintered copper nanoparticle thin film shows good electrical property and reduced oxidation than conventional thermal heating process. Consequently, the proposed selective laser sintering process can be compatible with plastic substrate for copper based flexible electronics applications.

Investigating the foil-generated deuteron beam interaction with a DT target in degenerate and classical plasma

NASA Astrophysics Data System (ADS)

Mehrangiz, M.; Ghasemizad, A.

2017-06-01

Deuteron fast ignition of a conically guided pre-compressed DT fuel is investigated. For this purpose, the acceleration of the deuterated thin foil by the intense laser beam is evaluated. The acceleration values and the number of foil-generated deuterons are calculated in terms of the laser pulse duration. Using the created deuterons as the fast ignitors, we investigate the fast ignition scheme by comparing fully degenerate, partial degenerate and classical types of DT plasma. The total energy gain of deuterons "beam fusion" is calculated to show the efficiency of beam reactions in increasing fusion rate. Besides, the stopping time and stopping range of incident deuterons are evaluated. Our numerical results indicate that degeneracy increases the beam-target collisions. Thus, it prepares the ignition situation sooner than the classical plasma. Moreover, the number of generated deuterons and their acceleration depend on the foil thickness and laser parameters. We show that when a 4ps laser with intensity of 10^{19} W/cm^2 focused onto a 20μm foil, 35× 10^{15} deuterons are generated. Moreover, under our analysis, in order to have a practicable fast ignition, 18% of the laser energy is necessary to convert into a deuteron driver.

Shock wave driven microparticles for pharmaceutical applications

NASA Astrophysics Data System (ADS)

Menezes, V.; Takayama, K.; Gojani, A.; Hosseini, S. H. R.

2008-10-01

Ablation created by a Q-switched Nd:Yttrium Aluminum Garnet (Nd:YAG) laser beam focusing on a thin aluminum foil surface spontaneously generates a shock wave that propagates through the foil and deforms it at a high speed. This high-speed foil deformation can project dry micro- particles deposited on the anterior surface of the foil at high speeds such that the particles have sufficient momentum to penetrate soft targets. We used this method of particle acceleration to develop a drug delivery device to deliver DNA/drug coated microparticles into soft human-body targets for pharmaceutical applications. The device physics has been studied by observing the process of particle acceleration using a high-speed video camera in a shadowgraph system. Though the initial rate of foil deformation is over 5 km/s, the observed particle velocities are in the range of 900-400 m/s over a distance of 1.5-10 mm from the launch pad. The device has been tested by delivering microparticles into liver tissues of experimental rats and artificial soft human-body targets, modeled using gelatin. The penetration depths observed in the experimental targets are quite encouraging to develop a future clinical therapeutic device for treatments such as gene therapy, treatment of cancer and tumor cells, epidermal and mucosal immunizations etc.

Spot-Welding Gun With Pivoting Twin-Collet Assembly

NASA Technical Reports Server (NTRS)

Nguyen, Francis; Simpson, Gareth; Hoult, William S.

1996-01-01

Modified spot-welding gun includes pivoting twin-collet assembly that holds two spot-welding electrodes. Designed to weld highly conductive (30 percent gold) brazing-alloy foils to thin nickel alloy workpieces; also suitable for other spot-welding applications compatible with two-electrode configuration.

Dry etching of copper phthalocyanine thin films: effects on morphology and surface stoichiometry.

PubMed

Van Dijken, Jaron G; Brett, Michael J

2012-08-24

We investigate the evolution of copper phthalocyanine thin films as they are etched with argon plasma. Significant morphological changes occur as a result of the ion bombardment; a planar surface quickly becomes an array of nanopillars which are less than 20 nm in diameter. The changes in morphology are independent of plasma power, which controls the etch rate only. Analysis by X-ray photoelectron spectroscopy shows that surface concentrations of copper and oxygen increase with etch time, while carbon and nitrogen are depleted. Despite these changes in surface stoichiometry, we observe no effect on the work function. The absorbance and X-ray diffraction spectra show no changes other than the peaks diminishing with etch time. These findings have important implications for organic photovoltaic devices which seek nanopillar thin films of metal phthalocyanine materials as an optimal structure.

Effect of native oxide layers on copper thin-film tensile properties: A reactive molecular dynamics study

DOE Office of Scientific and Technical Information (OSTI.GOV)

Skarlinski, Michael D., E-mail: michael.skarlinski@rochester.edu; Quesnel, David J.; Department of Mechanical Engineering, University of Rochester, Rochester, New York 14627

2015-12-21

Metal-oxide layers are likely to be present on metallic nano-structures due to either environmental exposure during use, or high temperature processing techniques such as annealing. It is well known that nano-structured metals have vastly different mechanical properties from bulk metals; however, difficulties in modeling the transition between metallic and ionic bonding have prevented the computational investigation of the effects of oxide surface layers. Newly developed charge-optimized many body [Liang et al., Mater. Sci. Eng., R 74, 255 (2013)] potentials are used to perform fully reactive molecular dynamics simulations which elucidate the effects that metal-oxide layers have on the mechanical propertiesmore » of a copper thin-film. Simulated tensile tests are performed on thin-films while using different strain-rates, temperatures, and oxide thicknesses to evaluate changes in yield stress, modulus, and failure mechanisms. Findings indicate that copper-thin film mechanical properties are strongly affected by native oxide layers. The formed oxide layers have an amorphous structure with lower Cu-O bond-densities than bulk CuO, and a mixture of Cu{sub 2}O and CuO charge character. It is found that oxidation will cause modifications to the strain response of the elastic modulii, producing a stiffened modulii at low temperatures (<75 K) and low strain values (<5%), and a softened modulii at higher temperatures. While under strain, structural reorganization within the oxide layers facilitates brittle yielding through nucleation of defects across the oxide/metal interface. The oxide-free copper thin-film yielding mechanism is found to be a tensile-axis reorientation and grain creation. The oxide layers change the observed yielding mechanism, allowing for the inner copper thin-film to sustain an FCC-to-BCC transition during yielding. The mechanical properties are fit to a thermodynamic model based on classical nucleation theory. The fit implies that the oxidation of the films reduces the activation volume for yielding.« less

Dual-Chamber/Dual-Anode Proportional Counter Incorporating an Intervening Thin-Foil Solid Neutron Converter

DOE Office of Scientific and Technical Information (OSTI.GOV)

Boatner, Lynn A; Neal, John S; Blackston, Matthew A

2012-01-01

A dual-chamber/dual-anode gas proportional counter utilizing thin solid 6LiF or 10B neutron converters coated on a 2-micon-thick Mylar film that is positioned between the two counter chambers and anodes has been designed, fabricated, and tested using a variety of fill gases including naturally abundant helium. In this device, neutron conversion products emitted from both sides of the coated converter foil are detected rather than having half of the products absorbed in the wall of a conventional tube type counter where the solid neutron converter is deposited on the tube wall. Geant4-based radiation transport calculations were used to determine the optimummore » neutron converter coating thickness for both isotopes. Solution methods for applying these optimized-thickness coatings on a Mylar film were developed that were carried out at room temperature without any specialized equipment and that can be adapted to standard coating methods such as silk screen or ink jet printing. The performance characteristics of the dual-chamber/dual-anode neutron detector were determined for both types of isotopically enriched converters. The experimental performance of the 6LiF converter-based detector was described well by modeling results from Geant4. Additional modeling studies of multiple-foil/multiple-chamber/anode configurations addressed the basic issue of the relatively longer absorption range of neutrons versus the shorter range of the conversion products for 6LiF and 10B. Combined with the experimental results, these simulations indicate that a high-performance neutron detector can be realized in a single device through the application of these multiple-foil/solid converter, multiple-chamber detector concepts.« less

Hot slumping glass technology for the grazing incidence optics of future missions with particular reference to IXO

NASA Astrophysics Data System (ADS)

Ghigo, M.; Basso, S.; Bavdaz, M.; Conconi, P.; Citterio, O.; Civitani, M.; Friedrich, P.; Gallieni, D.; Guldimann, B.; Martelli, F.; Negri, R.; Pagano, G.; Pareschi, G.; Parodi, G.; Proserpio, L.; Salmaso, B.; Scaglione, F.; Spiga, D.; Tagliaferri, G.; Terzi, L.; Tintori, M.; Vongehr, M.; Wille, E.; Winter, A.; Zambra, A.

2010-07-01

The mirrors of the International X-ray Observatory (IXO) consist of a large number of high quality segments delivering a spatial resolution better than 5 arcsec. A study concerning the slumping of thin glass foils for the IXO mirrors is under development in Europe, funded by ESA and led by the Brera Observatory. We are investigating two approaches, the "Direct" and "Indirect" slumping technologies, being respectively based on the use of convex and concave moulds. In the first case during the thermal cycle the optical surface of the glass is in direct contact with the mould surface, while in the second case it is the rear side of the foil which touches the master. Both approaches present pros and cons and aim of this study is also to make an assessment of both processes and to perform a trade-off between the two. The thin plates are made of D263glass produced by Schott. Each plate is 0.4 mm thick, with a reflecting area of 200 mm x 200 mm; the mould are made of Fused Silica. After the thermal cycle the slumped MPs are characterized to define their optical quality and microroughness. The adopted integration process foresees the bonding of the slumped foils to a rigid backplane by means of reinforcing ribs. During the bonding process the plates are constrained to stay in close contact to the surface of the master (i.e. the same mould used for the hot slumping process) by the application of a vacuum pump suction. In this way spring-back deformations and low frequency errors still present on the foil profile after slumping can be corrected. In this paper we present the preliminary results concerning achieved during the first part of the project.

Characterization of faulted dislocation loops and cavities in ion irradiated alloy 800H

NASA Astrophysics Data System (ADS)

Ulmer, Christopher J.; Motta, Arthur T.

2018-01-01

Alloy 800H is a high nickel austenitic stainless steel with good high temperature mechanical properties which is considered for use in current and advanced nuclear reactor designs. The irradiation response of 800H was examined by characterizing samples that had been bulk ion irradiated at the Michigan Ion Beam Laboratory with 5 MeV Fe2+ ions to 1, 10, and 20 dpa at 440 °C. Transmission electron microscopy was used to measure the size and density of both {111} faulted dislocation loops and cavities as functions of depth from the irradiated surface. The faulted loop density increased with dose from 1 dpa up to 10 dpa where it saturated and remained approximately the same until 20 dpa. The faulted loop average diameter decreased between 1 dpa and 10 dpa and again remained approximately constant from 10 dpa to 20 dpa. Cavities were observed after irradiation doses of 10 and 20 dpa, but not after 1 dpa. The average diameter of cavities increased with dose from 10 to 20 dpa, with a corresponding small decrease in density. Cavity denuded zones were observed near the irradiated surface and near the ion implantation peak. To further understand the microstructural evolution of this alloy, FIB lift-out samples from material irradiated in bulk to 1 and 10 dpa were re-irradiated in-situ in their thin-foil geometry with 1 MeV Kr2+ ions at 440 °C at the Intermediate Voltage Electron Microscope. It was observed that the cavities formed during bulk irradiation shrank under thin-foil irradiation in-situ while dislocation loops were observed to grow and incorporate into the dislocation network. The thin-foil geometry used for in-situ irradiation is believed to cause the cavities to shrink.

QED effects induced harmonics generation in extreme intense laser foil interaction

NASA Astrophysics Data System (ADS)

Yu, J. Y.; Yuan, T.; Liu, W. Y.; Chen, M.; Luo, W.; Weng, S. M.; Sheng, Z. M.

2018-04-01

A new mechanism of harmonics generation (HG) induced by quantum electrodynamics (QED) effects in extreme intense laser foil interaction is found and investigated by particle-in-cell (PIC) simulations. When two laser pulses with identical intensities of 1.6× {10}24 {{W}} {{{cm}}}-2 are counter-incident on a thin foil target, harmonics emission is observed in their reflected electromagnetic waves. Such harmonics radiation is excited due to transversely oscillating electric currents coming from the vibration of QED effect generated {e}-{e}+ pairs. The effects of laser intensity and polarization were studied. By distinguishing the cascade depth of generated photons and pairs, the influence of QED cascades on HG was analyzed. Although the current HG is not an efficient way for radiation source applications, it may provide a unique way to detect the QED processes in the near future ultra-relativistic laser solid interactions.

Metastable alloy materials produced by solid state reaction of compacted, mechanically deformed mixtures

DOEpatents

Atzmon, M.; Johnson, W.L.; Verhoeven, J.D.

1987-02-03

Bulk metastable, amorphous or fine crystalline alloy materials are produced by reacting cold-worked, mechanically deformed filamentary precursors such as metal powder mixtures or intercalated metal foils. Cold-working consolidates the metals, increases the interfacial area, lowers the free energy for reaction, and reduces at least one characteristic dimension of the metals. For example, the grains of powder or the sheets of foil are clad in a container to form a disc. The disc is cold-rolled between the nip of rollers to form a flattened disc. The grains are further elongated by further rolling to form a very thin sheet of a lamellar filamentary structure containing filaments having a thickness of less than 0.01 microns. Thus, diffusion distance and time for reaction are substantially reduced when the flattened foil is thermally treated in oven to form a composite sheet containing metastable material dispersed in unreacted polycrystalline material. 4 figs.

Highly efficient growth of vertically aligned carbon nanotubes on Fe-Ni based metal alloy foils for supercapacitors

NASA Astrophysics Data System (ADS)

Amalina Raja Seman, Raja Noor; Asyadi Azam, Mohd; Ambri Mohamed, Mohd

2016-12-01

Supercapacitors are highly promising energy devices with superior charge storage performance and a long lifecycle. Construction of the supercapacitor cell, especially electrode fabrication, is critical to ensure good performance in applications. This work demonstrates direct growth of vertically aligned carbon nanotubes (CNTs) on Fe-Ni based metal alloy foils, namely SUS 310S, Inconel 600 and YEF 50, and their use in symmetric vertically aligned CNT supercapacitor electrodes. Alumina and cobalt thin film catalysts were deposited onto the foils, and then CNT growth was performed using alcohol catalytic chemical vapour deposition. By this method, vertically aligned CNTs were successfully grown and used directly as a binder-free supercapacitor electrode to deliver excellent electrochemical performance. The device showed relatively good specific capacitance, a superior rate capability and excellent cycle stability, maintaining about 96% capacitance up to 1000 cycles.

A flexible, high-performance magnetoelectric heterostructure of (001) oriented Pb(Zr0.52Ti0.48)O3 film grown on Ni foil

NASA Astrophysics Data System (ADS)

Palneedi, Haribabu; Yeo, Hong Goo; Hwang, Geon-Tae; Annapureddy, Venkateswarlu; Kim, Jong-Woo; Choi, Jong-Jin; Trolier-McKinstry, Susan; Ryu, Jungho

2017-09-01

In this study, a flexible magnetoelectric (ME) heterostructure of PZT/Ni was fabricated by depositing a (001) oriented Pb(Zr0.52Ti0.48)O3 (PZT) film on a thin, flexible Ni foil buffered with LaNiO3/HfO2. Excellent ferroelectric properties and large ME voltage coefficient of 3.2 V/cmṡOe were realized from the PZT/Ni heterostructure. The PZT/Ni composite's high performance was attributed to strong texturing of the PZT film, coupled with the compressive stress in the piezoelectric film. Besides, reduced substrate clamping in the PZT film due to the film on the foil structure and strong interfacial bonding in the PZT/LaNiO3/HfO2/Ni heterostructure could also have contributed to the high ME performance of PZT/Ni.

Preliminary design of a tangentially viewing imaging bolometer for NSTX-U

DOE Office of Scientific and Technical Information (OSTI.GOV)

Peterson, B. J., E-mail: peterson@LHD.nifs.ac.jp; Mukai, K.; SOKENDAI

2016-11-15

The infrared imaging video bolometer (IRVB) measures plasma radiated power images using a thin metal foil. Two different designs with a tangential view of NSTX-U are made assuming a 640 × 480 (1280 × 1024) pixel, 30 (105) fps, 50 (20) mK, IR camera imaging the 9 cm × 9 cm × 2 μm Pt foil. The foil is divided into 40 × 40 (64 × 64) IRVB channels. This gives a spatial resolution of 3.4 (2.2) cm on the machine mid-plane. The noise equivalent power density of the IRVB is given as 113 (46) μW/cm{sup 2} for a timemore » resolution of 33 (20) ms. Synthetic images derived from Scrape Off Layer Plasma Simulation data using the IRVB geometry show peak signal levels ranging from ∼0.8 to ∼80 (∼0.36 to ∼26) mW/cm{sup 2}.« less

Preliminary design of a tangentially viewing imaging bolometer for NSTX-U

DOE PAGES

Peterson, B. J.; Sano, R.; Reinke, M. L.; ...

2016-08-03

The InfraRed imaging Video Bolometer measures plasma radiated power images using a thin metal foil. Two different designs with a tangential view of NSTX-U are made assuming a 640 x 480 (1280 x 1024) pixel, 30 (105) fps, 50 (20) mK, IR camera imaging the 9 cm x 9 cm x 2 μm Pt foil. The foil is divided into 40 x 40 (64 x 64) IRVB channels. This gives a spatial resolution of 3.4 (2.2) cm on the machine mid-plane. The noise equivalent power density of the IRVB is given as 113 (46) μW/cm 2 for a time resolutionmore » of 33 (20) ms. Synthetic images derived from SOLPS data using the IRVB geometry show peak signal levels ranging from ~0.8 - ~80 (~0.36 - ~26) mW/cm 2.« less

Solid-state lithium battery

DOEpatents

Ihlefeld, Jon; Clem, Paul G; Edney, Cynthia; Ingersoll, David; Nagasubramanian, Ganesan; Fenton, Kyle Ross

2014-11-04

The present invention is directed to a higher power, thin film lithium-ion electrolyte on a metallic substrate, enabling mass-produced solid-state lithium batteries. High-temperature thermodynamic equilibrium processing enables co-firing of oxides and base metals, providing a means to integrate the crystalline, lithium-stable, fast lithium-ion conductor lanthanum lithium tantalate (La.sub.1/3-xLi.sub.3xTaO.sub.3) directly with a thin metal foil current collector appropriate for a lithium-free solid-state battery.

Textured carbon surfaces on copper by sputtering

NASA Technical Reports Server (NTRS)

Curren, A. N. (Inventor); Jensen, K. A. (Inventor); Roman, R. F. (Inventor)

1986-01-01

A very thin layer of highly textured carbon is applied to a copper surface by a triode sputtering process. A carbon target and a copper substrate are simultaneously exposed to an argon plasma in a vacuum chamber. The resulting carbon surface is characterized by a dense, random array of needle like spires or peaks which extend perpendicularly from the copper surface. The coated copper is especially useful for electrode plates in multistage depressed collectors.

In situ probing of pulsed laser melting and laser-induced periodic surface structures formation by dynamic reflectivity

NASA Astrophysics Data System (ADS)

Huynh, T. T. D.; Semmar, N.

2017-09-01

The melting process and nanostructure formation induced by nanosecond and picosecond laser pulses on bulk silicon and copper thin film were studied by ex situ analysis and in situ real time reflectivity. Three different probing wavelengths (633, 473 and 326 nm) were used during the pump laser processing and were correlated to the beam parameters (pulse duration, laser fluence and number of laser shots) and copper thin film thickness. On a silicon surface using a KrF laser beam (27 ns, 1 Hz, 248 nm), the melting threshold was determined close to 700 mJ cm-2 and the melting duration increased from 10 to 130 ns as the fluence increased from 700 to 1750 mJ cm-2. Nanostructures with a spatial period close to the laser wavelength were formed on both copper thin film and silicon substrate after nanosecond Nd:YAG laser (10 ns, 266 nm, 1 Hz) irradiation. In the picosecond regime, using an Nd:YAG laser (40 ps, 266 nm, 1 Hz), different nanostructures, from spikes to laser-induced periodic surface structures, were formed on 500 nm copper thin film and were analyzed with respect to the drop in dynamic reflectivity changes versus the number of laser shots.

Contact-metal dependent current injection in pentacene thin-film transistors

NASA Astrophysics Data System (ADS)

Wang, S. D.; Minari, T.; Miyadera, T.; Tsukagoshi, K.; Aoyagi, Y.

2007-11-01

Contact-metal dependent current injection in top-contact pentacene thin-film transistors is analyzed, and the local mobility in the contact region was found to follow the Meyer-Neldel rule. An exponential trap distribution, rather than the metal/organic hole injection barrier, is proposed to be the dominant factor of the contact resistance in pentacene thin-film transistors. The variable temperature measurements revealed a much narrower trap distribution in the copper contact compared with the corresponding gold contact, and this is the origin of the smaller contact resistance for copper despite a lower work function.

Talbot-Lau x-ray deflectometer electron density diagnostic for laser and pulsed power high energy density plasma experiments (invited).

PubMed

Valdivia, M P; Stutman, D; Stoeckl, C; Mileham, C; Begishev, I A; Theobald, W; Bromage, J; Regan, S P; Klein, S R; Muñoz-Cordovez, G; Vescovi, M; Valenzuela-Villaseca, V; Veloso, F

2016-11-01

Talbot-Lau X-ray deflectometry (TXD) has been developed as an electron density diagnostic for High Energy Density (HED) plasmas. The technique can deliver x-ray refraction, attenuation, elemental composition, and scatter information from a single Moiré image. An 8 keV Talbot-Lau interferometer was deployed using laser and x-pinch backlighters. Grating survival and electron density mapping were demonstrated for 25-29 J, 8-30 ps laser pulses using copper foil targets. Moiré pattern formation and grating survival were also observed using a copper x-pinch driven at 400 kA, ∼1 kA/ns. These results demonstrate the potential of TXD as an electron density diagnostic for HED plasmas.

Study of the surface contamination of copper with the improved positron annihilation-induced Auger electron spectrometer at NEPOMUC

NASA Astrophysics Data System (ADS)

Mayer, J.; Hugenschmidt, C.; Schreckenbach, K.

2008-10-01

The high intensity positron source NEPOMUC at the FRM-II in Munich enables measurement times for positron annihilation-induced Auger electron spectroscopy (PAES) of only 2.4 h/spectrum, in contrast to usual lab beams with measurement times up to several days. The high electron background due to surrounding experiments in the experimental hall of the FRM-II has been eliminated and hence background free experiments have become possible. Due to this, the signal to noise ratio has been enhanced to 4.5:1, compared to 1:3 with EAES. In addition, a long-term measurement has been performed in order to observe the contamination of a polycrystalline copper foil at 150 °C.

Talbot-Lau X-ray Deflectometer electron density diagnostic for laser and pulsed power high energy density plasma experiments

DOE PAGES

Valdivia, M. P.; Stutman, D.; Stoeckl, C.; ...

2016-04-21

Talbot-Lau X-ray Deflectometry has been developed as an electron density diagnostic for High Energy Density plasmas. The technique can deliver x-ray refraction, attenuation, elemental composition, and scatter information from a single Moiré image. An 8 keV Talbot-Lau interferometer was deployed using laser and x-pinch backlighters. Grating survival and electron density mapping was demonstrated for 25-29 J, 8-30 ps laser pulses using copper foil targets. Moire pattern formation and grating survival was also observed using a copper x-pinch driven at 400 kA, ~1 kA/ns. Lastly, these results demonstrate the potential of TXD as an electron density diagnostic for HED plasmas.

A simple algorithm for beam profile diagnostics using a thermographic camera

DOE Office of Scientific and Technical Information (OSTI.GOV)

Katagiri, Ken; Hojo, Satoru; Honma, Toshihiro

2014-03-15

A new algorithm for digital image processing apparatuses is developed to evaluate profiles of high-intensity DC beams from temperature images of irradiated thin foils. Numerical analyses are performed to examine the reliability of the algorithm. To simulate the temperature images acquired by a thermographic camera, temperature distributions are numerically calculated for 20 MeV proton beams with different parameters. Noise in the temperature images which is added by the camera sensor is also simulated to account for its effect. Using the algorithm, beam profiles are evaluated from the simulated temperature images and compared with exact solutions. We find that niobium ismore » an appropriate material for the thin foil used in the diagnostic system. We also confirm that the algorithm is adaptable over a wide beam current range of 0.11–214 μA, even when employing a general-purpose thermographic camera with rather high noise (ΔT{sub NETD} ≃ 0.3 K; NETD: noise equivalent temperature difference)« less

Impact of the De-Alloying Kinetics and Alloy Microstructure on the Final Morphology of De-Alloyed Meso-Porous Metal Films

PubMed Central

Lin, Bao; Kong, Lingxue; Hodgson, Peter D.; Dumée, Ludovic F.

2014-01-01

Nano-textured porous metal materials present unique surface properties due to their enhanced surface energy with potential applications in sensing, molecular separation and catalysis. In this paper, commercial alloy foils, including brass (Cu85Zn15 and Cu70Zn30) and white gold (Au50Ag50) foils have been chemically de-alloyed to form nano-porous thin films. The impact of the initial alloy micro-structure and number of phases, as well as chemical de-alloying (DA) parameters, including etchant concentration, time and solution temperature on the final nano-porous thin film morphology and properties were investigated by electron microscopy (EM). Furthermore, the penetration depth of the pores across the alloys were evaluated through the preparation of cross sections by focus ion beam (FIB) milling. It is demonstrated that ordered pores ranging between 100 nm and 600 nm in diameter and 2–5 μm in depth can be successfully formed for the range of materials tested. The microstructure of the foils were obtained by electron back-scattered diffraction (EBSD) and linked to development of pits across the material thickness and surface during DA. The role of selective etching of both noble and sacrificial metal phases of the alloy were discussed in light of the competitive surface etching across the range of microstructures and materials tested. PMID:28344253

Bimorph material/structure designs for high sensitivity flexible surface acoustic wave temperature sensors.

PubMed

Tao, R; Hasan, S A; Wang, H Z; Zhou, J; Luo, J T; McHale, G; Gibson, D; Canyelles-Pericas, P; Cooke, M D; Wood, D; Liu, Y; Wu, Q; Ng, W P; Franke, T; Fu, Y Q

2018-06-13

A fundamental challenge for surface acoustic wave (SAW) temperature sensors is the detection of small temperature changes on non-planar, often curved, surfaces. In this work, we present a new design methodology for SAW devices based on flexible substrate and bimorph material/structures, which can maximize the temperature coefficient of frequency (TCF). We performed finite element analysis simulations and obtained theoretical TCF values for SAW sensors made of ZnO thin films (~5 μm thick) coated aluminum (Al) foil and Al plate substrates with thicknesses varied from 1 to 1600 μm. Based on the simulation results, SAW devices with selected Al foil or plate thicknesses were fabricated. The experimentally measured TCF values were in excellent agreements with the simulation results. A normalized wavelength parameter (e.g., the ratio between wavelength and sample thickness, λ/h) was applied to successfully describe changes in the TCF values, and the TCF readings of the ZnO/Al SAW devices showed dramatic increases when the normalized wavelength λ/h was larger than 1. Using this design approach, we obtained the highest reported TCF value of -760 ppm/K for a SAW device made of ZnO thin film coated on Al foils (50 μm thick), thereby enabling low cost temperature sensor applications to be realized on flexible substrates.

Manufacturing and characterization of magnesium alloy foils for use as anode materials in rechargeable magnesium ion batteries

NASA Astrophysics Data System (ADS)

Schloffer, Daniel; Bozorgi, Salar; Sherstnev, Pavel; Lenardt, Christian; Gollas, Bernhard

2017-11-01

The fabrication of thin foils of magnesium for use as anode material in rechargeable magnesium ion batteries is described. In order to improve its workability, the magnesium was alloyed by melting metallurgy with zinc and/or gadolinium, producing saturated solid solutions. The material was extruded to thin foils and rolled to a thickness of approximately 100 μm. The electrochemical behavior of Mg-1.63 wt% Zn, Mg-1.55 wt% Gd and Mg-1.02 wt% Zn-1.01 wt% Gd was studied in (PhMgCl)2-AlCl3/THF electrolyte by cyclic voltammetry and galvanostatic cycling in symmetrical cells. Analysis of the current-potential curves in the Tafel region and the linear region close to the equilibrium potential show almost no effect of the alloying elements on the exchange current densities (5-45 μA/cm2) and the transfer coefficients. Chemical analyses of the alloy surfaces and the electrolyte demonstrate that the alloying elements not only dissolve with the magnesium during the anodic half-cycles, but also re-deposit during the cathodic half-cycles together with the magnesium and aluminum from the electrolyte. Given the negligible corrosion rate in aprotic electrolytes under such conditions, no adverse effects of alloying elements are expected for the performance of magnesium anodes in secondary batteries.

Probing of high density plasmas using the multi-beam, high power TiSa laser system ARCTURUS

NASA Astrophysics Data System (ADS)

Willi, Oswald; Aktan, Esin; Brauckmann, Stephannie; Aurand, Bastian; Cerchez, Mirela; Prasad, Rajendra; Schroer, Anna Marie

2017-10-01

The understanding of relativistic laser plasma interaction at ultra-high intensities has advanced considerably during the last decade with the availability of multi-beam, high power TiSa laser systems. These laser systems allow pump-probe experiments to be carried out. The ARCTURUS laser at the University of Duesseldorf is ideally suited for various kinds of pump-probe experiments as it consists of two identical, high power beams with energies of 5J in 30 fs and a third beam for optical probing with energy of 30mJ in a 30fs pulse. All three beams are synchronised and have flexible time delays with respect to each other. Several different processes were studied where one of the beams was used as an interaction beam and the second one was incident on a thin solid gold foil to generate a proton beam. For example, thin foil targets were irradiated either with a linear or circular polarized pulse and probed with protons at different times. The expansion of foils for the two cases was clearly different consistent with numerical simulations. In addition, the interaction of gas targets was probed with protons and separately with an optical probe. With both diagnostics the formation of a channel was observed. In the presentation various two beam measurements will be discussed.

Plasma impact on structural, morphological and optical properties of copper acetylacetonate thin films.

PubMed

Abdel-Khalek, H; El-Samahi, M I; El-Mahalawy, Ahmed M

2018-06-15

The influence of plasma exposure on structural, morphological and optical properties of copper (II) acetylacetonate thin films deposited by thermal evaporation technique was investigated. Copper (II) acetylacetonate as-grown thin films were exposed to the atmospheric plasma for different times. The exposure of as-grown cu(acac) 2 thin film to atmospheric plasma for 5min modified its structural, morphological and optical properties. The effect of plasma exposure on structure and roughness of cu(acac) 2 thin films was evaluated by XRD and AFM techniques, respectively. The XRD results showed an increment in crystallinity due to exposure for 5min, but, when the exposure time reaches 10min, the film was transformed to an amorphous state. The AFM results revealed a strong modification of films roughness when the average roughness decreased from 63.35nm to ~1nm as a result of interaction with plasma. The optical properties of as-grown and plasma exposured cu(acac) 2 thin films were studied using spectrophotometric method. The exposure of cu(acac) 2 thin films to plasma produced the indirect energy gap decrease from 3.20eV to 2.67eV for 10min exposure time. The dispersion parameters were evaluated in terms of single oscillator model for as-grown and plasma exposured thin films. The influence of plasma exposure on third order optical susceptibility was studied. Copyright © 2018 Elsevier B.V. All rights reserved.

Deposition of thermal and hot-wire chemical vapor deposition copper thin films on patterned substrates.

PubMed

Papadimitropoulos, G; Davazoglou, D

2011-09-01

In this work we study the hot-wire chemical vapor deposition (HWCVD) of copper films on blanket and patterned substrates at high filament temperatures. A vertical chemical vapor deposition reactor was used in which the chemical reactions were assisted by a tungsten filament heated at 650 degrees C. Hexafluoroacetylacetonate Cu(I) trimethylvinylsilane (CupraSelect) vapors were used, directly injected into the reactor with the aid of a liquid injection system using N2 as carrier gas. Copper thin films grown also by thermal and hot-wire CVD. The substrates used were oxidized silicon wafers on which trenches with dimensions of the order of 500 nm were formed and subsequently covered with LPCVD W. HWCVD copper thin films grown at filament temperature of 650 degrees C showed higher growth rates compared to the thermally ones. They also exhibited higher resistivities than thermal and HWCVD films grown at lower filament temperatures. Thermally grown Cu films have very uniform deposition leading to full coverage of the patterned substrates while the HWCVD films exhibited a tendency to vertical growth, thereby creating gaps and incomplete step coverage.

Terahertz and Microwave Devices Based on the Photo-Excited Low Dimensional Electronic System

DTIC Science & Technology

2015-03-11

Morphology of Thermally Annealed Copper Foils for Graphene Growth, Chemistry of Materials , (05 2013): 1643. doi : 10.1021/cm400032h R. G. Mani, J...connected specimens, IEEE Transactions on Nanotechnology, (01 2011): 179. doi : Jesús Iñarrea, R. Mani, W. Wegscheider. Sublinear radiation power...dependence of photoexcited resistance oscillations in two-dimensional electron systems, Physical Review B, (11 2010): 0. doi : 10.1103/PhysRevB

Superconducting structure

DOEpatents

Kwon, Chuhee; Jia, Quanxi; Foltyn, Stephen R.

2003-04-01

A superconductive structure including a dielectric oxide substrate, a thin buffer layer of a superconducting material thereon; and, a layer of a rare earth-barium-copper oxide superconducting film thereon the thin layer of yttrium-barium-copper oxide, the rare earth selected from the group consisting of samarium, gadolinium, ytterbium, erbium, neodymium, dysprosium, holmium, lutetium, a combination of more than one element from the rare earth group and a combination of one or more elements from the rare earth group with yttrium, the buffer layer of superconducting material characterized as having chemical and structural compatibility with the dielectric oxide substrate and the rare earth-barium-copper oxide superconducting film is provided.

Superconducting Structure

DOEpatents

Kwon, Chuhee; Jia, Quanxi; Foltyn, Stephen R.

2005-09-13

A superconductive structure including a dielectric oxide substrate, a thin buffer layer of a superconducting material thereon; and, a layer of a rare earth-barium-copper oxide superconducting film thereon the thin layer of yttrium-barium-copper oxide, the rare earth selected from the group consisting of samarium, gadolinium, ytterbium, erbium, neodymium, dysprosium, holmium, lutetium, a combination of more than one element from the rare earth group and a combination of one or more elements from the rare earth group with yttrium, the buffer layer of superconducting material characterized as having chemical and structural compatibility with the dielectric oxide substrate and the rare earth-barium-copper oxide superconducting film is provided.

Effect of input perturbation on the performance and wake dynamics of aquatic propulsion in heaving flexible foils

NASA Astrophysics Data System (ADS)

Lehn, Andrea M.; Thornycroft, Patrick J. M.; Lauder, George V.; Leftwich, Megan C.

2017-02-01

In this paper we consider the effects of adding high-frequency, low-amplitude perturbations to a smooth sinusoidal base input signal for a heaving panel in a closed loop flow tank. Specifically, 0.1 cm amplitude sinusoidal perturbation waves with frequency fp ranging from 0.5 to 13.0 Hz are added to 1 cm heave sinusoids with base frequencies, fb, ranging from 0.5 to 3.0 Hz. Two thin foils with different flexural stiffness are heaved with the combined input signals in addition to both the high-heave and low-heave signals independently. In all cases, the foils are heaved in a recirculating water channel with an incoming velocity of Vx=10 cm/s and a Reynolds number based on the chord length of Re=17 300 . Results demonstrate that perturbations increase the net axial force, in the streamwise direction, in most cases tested (with the exception of some poor performing flexible foil cases). Most significantly, for a base frequency of 1 Hz, perturbations at 9 Hz result in a 780.7% increase in net streamwise force production. Generally, the higher the perturbation frequency, fp the more axial force generated. However, for the stiffer foil, a clear peak in net force exists at fp=9 Hz , regardless of the base frequency. For the stiffer foil, swimming efficiency at a 1 Hz flapping frequency is increased dramatically with the addition of a perturbation, with reduced efficiency increases at higher flapping frequencies. Likewise, for the flexible foil, swimming efficiency gains are greatest at the lower flapping frequencies. Perturbations alter the wake structure by increasing the vorticity magnitude and increasing the vortex shedding frequency; i.e., more, stronger vortices are produced in each flapping cycle.

Synthesizing photovoltaic thin films of high quality copper-zinc-tin alloy with at least one chalcogen species

DOEpatents

Teeter, Glenn; Du, Hui; Young, Matthew

2013-08-06

A method for synthesizing a thin film of copper, zinc, tin, and a chalcogen species ("CZTCh" or "CZTSS") with well-controlled properties. The method includes depositing a thin film of precursor materials, e.g., approximately stoichiometric amounts of copper (Cu), zinc (Zn), tin (Sn), and a chalcogen species (Ch). The method then involves re-crystallizing and grain growth at higher temperatures, e.g., between about 725 and 925 degrees K, and annealing the precursor film at relatively lower temperatures, e.g., between 600 and 650 degrees K. The processing of the precursor film takes place in the presence of a quasi-equilibrium vapor, e.g., Sn and chalcogen species. The quasi-equilibrium vapor is used to maintain the precursor film in a quasi-equilibrium condition to reduce and even prevent decomposition of the CZTCh and is provided at a rate to balance desorption fluxes of Sn and chalcogens.

Effect of copper doping sol-gel ZnO thin films: physical properties and sensitivity to ethanol vapor

NASA Astrophysics Data System (ADS)

Boukaous, Chahra; Benhaoua, Boubaker; Telia, Azzedine; Ghanem, Salah

2017-10-01

In the present paper, the effect of copper doping ZnO thin films, deposited using a sol-gel dip-coating technique, on the structural, optical and ethanol vapor-sensing properties, was investigated. The range of the doping content is 0 wt. %-5 wt. % Cu/Zn and the films’ properties were studied using x-ray diffraction, scanning electron microscopy and a UV-vis spectrophotometer. The obtained results indicated that undoped and copper-doped zinc oxide thin films have polycrystalline wurtzite structure with (1 0 1) preferred orientation. All samples have a smooth and dense structure free of pinholes. A decrease in the band gap with Cu concentration in the ZnO network was observed. The influence of the dopant on ethanol vapor-sensing properties shows an increase in the film sensitivity to the ethanol vapor within the Cu concentration.

CHEMICAL SOLUTION DEPOSITION BASED OXIDE BUFFERS AND YBCO COATED CONDUCTORS

DOE Office of Scientific and Technical Information (OSTI.GOV)

Paranthaman, Mariappan Parans

We have reviewed briefly the growth of buffer and high temperature superconducting oxide thin films using a chemical solution deposition (CSD) method. In the Rolling-Assisted Biaxially Textured Substrates (RABiTS) process, developed at Oak Ridge National Laboratory, utilizes the thermo mechanical processing to obtain the flexible, biaxially oriented copper, nickel or nickel-alloy substrates. Buffers and Rare Earth Barium Copper Oxide (REBCO) superconductors have been deposited epitaxially on the textured nickel alloy substrates. The starting substrate serves as a template for the REBCO layer, which has substantially fewer weak links. Buffer layers play a major role in fabricating the second generation REBCOmore » wire technology. The main purpose of the buffer layers is to provide a smooth, continuous and chemically inert surface for the growth of the REBCO film, while transferring the texture from the substrate to the superconductor layer. To achieve this, the buffer layers need to be epitaxial to the substrate, i.e. they have to nucleate and grow in the same bi-axial texture provided by the textured metal foil. The most commonly used RABiTS multi-layer architectures consist of a starting template of biaxially textured Ni-5 at.% W (Ni-W) substrate with a seed (first) layer of Yttrium Oxide (Y2O3), a barrier (second) layer of Yttria Stabilized Zirconia (YSZ), and a Cerium Oxide (CeO2) cap (third) layer. These three buffer layers are generally deposited using physical vapor deposition (PVD) techniques such as reactive sputtering. On top of the PVD template, REBCO film is then grown by a chemical solution deposition. This article reviews in detail about the list of oxide buffers and superconductor REBCO films grown epitaxially on single crystal and/or biaxially textured Ni-W substrates using a CSD method.« less

Influence of post-deposition annealing on structural, morphological and optical properties of copper (II) acetylacetonate thin films.

PubMed

Abdel-Khalek, H; El-Samahi, M I; El-Mahalawy, Ahmed M

2018-05-21

In this study, the effect of thermal annealing under vacuum conditions on structural, morphological and optical properties of thermally evaporated copper (II) acetylacetonate, cu(acac) 2 , thin films were investigated. The copper (II) acetylacetonate thin films were deposited using thermal evaporation technique at vacuum pressure ~1 × 10 -5  mbar. The deposited films were thermally annealed at 323, 373, 423, and 473 K for 2 h in vacuum. The thermogravimetric analysis of cu(acac) 2 powder indicated a thermal stability of cu(acac) 2 up to 423 K. The effects of thermal annealing on the structural properties of cu(acac) 2 were evaluated employing X-ray diffraction method and the analysis showed a polycrystalline nature of the as-deposited and annealed films with a preferred orientation in [1¯01] direction. Fourier transformation infrared (FTIR) technique was used to negate the decomposition of copper (II) acetylacetonate during preparation or/and annealing up to 423 K. The surface morphology of the prepared films was characterized by means of field emission scanning electron microscopy (FESEM). A significant enhancement of the morphological properties of cu(acac) 2 thin films was obtained till the annealing temperature reaches 423 K. The variation of optical constants that estimated from spectrophotometric measurements of the prepared thin films was investigated as a function of annealing temperature. The annealing process presented significantly impacted the nonlinear optical properties such as third-order optical susceptibility χ (3) and nonlinear refractive index n 2 of cu(acac) 2 thin films. Copyright © 2018 Elsevier B.V. All rights reserved.

Investigation of Annealing Temperature on Copper Oxide Thin Films Using Sol-Gel Spin Coating Technique

NASA Astrophysics Data System (ADS)

Hashim, H.; Samat, S. F. A.; Shariffudin, S. S.; Saad, P. S. M.

2018-03-01

Copper (II) Oxide or cupric oxide (CuO) is one of the well-known materials studied for thin films applications. This paper was studied on the effect of annealing temperature to CuO thin films using sol-gel method and spin coating technique. The solution was prepared by sol-gel method and the thin films were synthesized at various temperatures from 500°C to 700°C that deposited onto the quartz substrates. After the annealing process, the thin films were uniform and brownish black in colour. The measurements were performed by atomic force microscopy (AFM), surface profiler (SP), two-point probe and Ultraviolet-visible (UV-Vis-NIR) spectrometer. From the optical measurement, the band gap was estimated to be 1.44eV for sample annealed at 550°C.

Method of making a partial interlaminar separation composite system

NASA Technical Reports Server (NTRS)

Elber, W. (Inventor)

1981-01-01

An interlaminar separation system for composites is disclosed a thin layer of a perforated foil film is interposed between adjacent laminae of a composite formed from prepreg tapes. Laminae adherence takes place through the perforations and a composite structure with improved physical property characteristics is produced.

Partial interlaminar separation system for composites

NASA Technical Reports Server (NTRS)

Elber, W. (Inventor)

1980-01-01

This inventor relates to an interlaminar separation system for composites wherein a thin layer of a perforated foil film is interposed between adjacent laminae of a composite formed from prepreg tapes to thereby permit laminate adherence through the perforations and produce a composite structure having improved physical property characteristics.

P-doped strontium titanate grown using two target pulsed laser deposition for thin film solar cells

NASA Astrophysics Data System (ADS)

Man, Hamdi

Thin-film solar cells made of Mg-doped SrTiO3 p-type absorbers are promising candidates for clean energy generation. This material shows p-type conductivity and also demonstrates reasonable absorption of light. In addition, p-type SrTiO3 can be deposited as thin films so that the cost can be lower than the competing methods. In this work, Mg-doped SrTiO3 (STO) thin-films were synthesized and analyzed in order to observe their potential to be employed as the base semiconductor in photovoltaic applications. Mg-doped STO thin-films were grown by using pulsed laser deposition (PLD) using a frequency quadrupled Yttrium Aluminum Garnet (YAG) laser and with a substrate that was heated by back surface absorption of infrared (IR) laser light. The samples were characterized using X-ray photoelectron spectroscopy (XPS) and it was observed that Mg atoms were doped successfully in the stoichiometry. Reflection high energy electron diffraction (RHEED) spectroscopy proved that the thin films were polycrystalline. Kelvin Probe work function measurements indicated that the work function of the films were 4.167 eV after annealing. UV/Vis Reflection spectroscopy showed that Mg-doped STO thin-films do not reflect significantly except in the ultraviolet region of the spectrum where the reflection percentage increased up to 80%. Self-doped STO thin-films, Indium Tin Oxide (ITO) thin films and stainless steel foil (SSF) were studied in order to observe their characteristics before employing them in Mg-doped STO based solar cells. Self-doped STO thin films were grown using PLD and the results showed that they are capable of serving as the n-type semiconductor in solar cell applications with oxygen vacancies in their structure and low reflectivity. Indium Tin Oxide thin-films grown by PLD system showed low 25-50 ?/square sheet resistance and very low reflection features. Finally, commercially available stainless steel foil substrates were excellent substrates for the inexpensive growth of these novel solar cells.

Quasi-monoenergetic proton beam from a proton-layer embedded metal foil irradiated by an intense laser pulse

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kim, Kyung Nam; Lee, Kitae, E-mail: klee@kaeri.re.kr; Kumar, Manoj

A target structure, ion-layer embedded foil (ILEF) is proposed for producing a quasi-monoenergetic proton beam by utilizing a bulk electrostatic field, which is generated by irradiating the target with an ultra-intense laser pulse, inside the plasma. Compared with the case of a single metal foil in which the proton layer is initially present on the surface, in the ILEF target, the proton layer is initially located inside a metal foil. A two-dimensional particle-in-cell (PIC) simulation shows that the target generates a proton beam with a narrow energy spread. With a laser intensity of 2 × 10{sup 19 }W/cm{sup 2}, a 22-MeV proton beammore » with an energy spread of 8% at the full-width-half-maximum (FWHM) is obtained when the proton layer is located at 0.4 μm inside the rear surface of a 2.4 μm-thick copper foil. When the proton layer moves toward the front side, a proton beam with a flat-top energy distribution ranging from 15 MeV to 35 MeV is obtained. Further, with a higher laser intensity of 10{sup 21 }W/cm{sup 2}, a proton beam with the maximum energy of 345 MeV and FWHM energy spread of 7.2% is obtained. The analysis of the PIC simulation with an aid of a fluid analysis shows that the spectrum is affected by the initial position of the proton layer, its initial spread during the formation of the sheath field, and the space charge effect.« less

Copper Oxide Nanograss for Efficient and Stable Photoelectrochemical Hydrogen Production by Water Splitting

NASA Astrophysics Data System (ADS)

Borkar, Rajnikant; Dahake, Rashmi; Rayalu, Sadhana; Bansiwal, Amit

2018-03-01

A biphasic copper oxide thin film of grass-like appendage morphology is synthesized by two-step electro-deposition method and later investigated for photoelectrochemical (PEC) water splitting for hydrogen production. Further, the thin film was characterized by UV-Visible spectroscopy, x-ray diffraction (XRD), Scanning electron microscopy (SEM) and PEC techniques. The XRD analysis confirms formation of biphasic copper oxide phases, and SEM reveals high surface area grass appendage-like morphology. These grass appendage structures exhibit a high cathodic photocurrent of - 1.44 mAcm-2 at an applied bias of - 0.7 (versus Ag/AgCl) resulting in incident to photon current efficiency (IPCE) of ˜ 10% at 400 nm. The improved light harvesting and charge transport properties of grass appendage structured biphasic copper oxides makes it a potential candidate for PEC water splitting for hydrogen production.

Rayleigh-Taylor instability of two-specie laser-accelerated foils

NASA Astrophysics Data System (ADS)

Ratliff, T. H.; Yi, S. A.; Khudik, V.; Yu, T. P.; Pukhov, A.; Chen, M.; Shvets, G.

2010-11-01

When an ultra intense circularly polarized laser pulse irradiates an ultra thin film, a monoenergetic ion beam is produced with characteristics well suited for applications in science and medicine. Upon laser incidence, the electrons in the foil are pushed via the ponderomotive force to the foil rear; the charge separation field then accelerates ions. In the accelerating frame the ions are trapped in a potential well formed by the electrostatic and inertial forces. However, their energy spectrum can be quickly degraded by the Rayleigh-Taylor (RT) instability. Stabilization in the case of a two-specie foil is the subject of this poster. First, we use a 1D particle-in-cell (PIC) simulation to establish an equilibrium state of the two-specie foil in the accelerating frame. Next we perturb this equilibrium and analytically investigate the 2D RT instability. Analytical results are compared with 2-D simulations. We also investigate parametrically various effects on the RT growth rate. The protons completely separate from the carbons, and although the vacuum-carbon interface remains unstable, the large spatial extent of the carbon layer prevents perturbations from feeding through to the proton layer. The monoenergetic proton beam is shown to persist beyond the conclusion of the laser pulse interaction. [1] T.P. Yu, A. Pukhov, G. Shvets, and M Chen, Phys. Rev. Lett. (in press)

Graphene on silicon dioxide via carbon ion implantation in copper with PMMA-free transfer

NASA Astrophysics Data System (ADS)

Lehnert, Jan; Spemann, Daniel; Hamza Hatahet, M.; Mändl, Stephan; Mensing, Michael; Finzel, Annemarie; Varga, Aron; Rauschenbach, Bernd

2017-06-01

In this work, a synthesis method for the growth of low-defect large-area graphene using carbon ion beam implantation into metallic Cu foils is presented. The Cu foils (1 cm2 in size) were pre-annealed in a vacuum at 950 °C for 2 h, implanted with 35 keV carbon ions at room temperature, and subsequently annealed at 850 °C for 2 h to form graphene layers with the layer number controlled by the implantation fluence. The graphene was then transferred to SiO2/Si substrates by a PMMA-free wet chemical etching process. The obtained regions of monolayer graphene are of ˜900 μm size. Raman spectroscopy, atomic force microscopy, scanning electron microscopy, and optical microscopy performed at room temperature demonstrated a good quality and homogeneity of the graphene layers, especially for monolayer graphene.

Undercuts by Laser Shock Forming

NASA Astrophysics Data System (ADS)

Wielage, Hanna; Vollertsen, Frank

2011-05-01

In laser shock forming TEA-CO2-laser induced shock waves are used to form metal foils, such as aluminum or copper. The process utilizes an initiated plasma shock wave on the target surface, which leads to a forming of the foil. A challenge in forming technologies is the manufacturing of undercuts. By conventional forming methods these special forms are not feasible. In this article, it is presented that undercuts in the micro range can be produced by laser shock deep drawing. Different drawing die diameters, drawing die depths and the material aluminum in the thicknesses 20 and 50 μm were investigated. It will be presented that smaller die diameters facilitate undercuts compared to bigger die diameters. The phenomena can be explained by Barlow's formula. Furthermore, it is shown which maximum undercut depth at different die diameters can be reached. To this end, cross-sections of the different parameter combinations are displayed.

Conversion of Langmuir-Blodgett monolayers and bilayers of poly(amic acid) through polyimide to graphene

NASA Astrophysics Data System (ADS)

Jo, Hye Jin; Lyu, Ji Hong; Ruoff, Rodney S.; Lim, Hyunseob; In Yoon, Seong; Jeong, Hu Young; Shin, Tae Joo; Bielawski, Christopher W.; Shin, Hyeon Suk

2017-03-01

Various solid carbon sources, particularly poly(methyl methacrylate), have been used as precursors to graphene. The corresponding growth process generally involves the decomposition of the solids to hydrocarbon gases followed by their adsorption on metallic substrates (e.g., Cu). We report a different approach that uses a thermally-resistant polyimide (PI) as a carbon precursor. Langmuir-Blodgett films of poly(amic acid) (PAA) were transferred to copper foils and then converted to graphene via a PI intermediate. The Cu foil substrate was also discovered to facilitate the orientation of aromatic moieties upon carbonization process of the PI. As approximately 50% of the initial quantity of the PAA was found to remain at 1000 °C, thermally-stable polymers may reduce the quantity of starting material required to prepare high quality films of graphene. Graphene grown using this method featured a relatively large domain size and an absence of adventitious adlayers.

Electrodeposition of nano-sized bismuth on copper foil as electrocatalyst for reduction of CO2 to formate

NASA Astrophysics Data System (ADS)

Lv, Weixin; Zhou, Jing; Bei, Jingjing; Zhang, Rui; Wang, Lei; Xu, Qi; Wang, Wei

2017-01-01

Electrochemical reduction of carbon dioxide (CO2) to formate is energetically inefficient because high overpotential is required for reduction of CO2 to formate on most traditional catalysts. In this paper, a novel nano-sized Bi-based electrocatalyst deposited on a Cu foil has been synthesized, which can be used as a cathode for electrochemical reduction of CO2 to formate with a low overpotential (0.69 V) and a high selectivity (91.3%). The electrocatalyst can show excellent catalytic performance toward reduction of CO2 which can probably be attributed to the nano-sized structure and the surface oxide layer. The energy efficiency for reduction of CO2 to formate can reach to 50% when an IrxSnyRuzO2/Ti electrode is used as anode, it is one of the highest values found in the literatures and very practicable for sustainable fuel synthesis.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Martz, Joseph Christopher; Spearing, Dane Robert; Labouriau, Andrea

Microclad is a composite material consisting of a thin copper coating applied on a single side over a Kapton substrate. Kapton is the commercial designator for polyimide supplied by DuPont. Microclad is a key material in detonator manufacture and function. Detonators which utilize Microclad function when a large current applied through a thin bridge etched into the copper produces a plasma, accelerating a Kapton flyer into an explosive (PETN) pellet. The geometry and properties of the Microclad are a critical element of this process.

Studies of Surface Charging of Polymers by Indirect Triboelectrification

NASA Astrophysics Data System (ADS)

Mantovani, James; Calle, Carlos; Groop, Ellen; Buehler, Martin

2001-03-01

Charge is known to develop on the surface of an insulating polymer by frictional charging through direct physical contact with another material. We will present results of recent triboelectrification studies of polymer surfaces that utilized an indirect method of frictional charging. This method first involves placing a grounded thin metal foil in stationary contact over the polymer surface. The exposed metal foil is then rubbed with the surface of the material that generates the triboelectric charge. Data is presented for five types of polymers: fiberglass/epoxy, polycarbonate (Lexan), polytetraflouroethylene (Teflon), Rulon J, and polymethylmethacrylate (PMMA, Lucite). The amount of charge that develops on an insulator's surface is measured using the MECA Electrometer, which was developed jointly by NASA Kennedy Space Center and the Jet Propulsion Laboratory to study the electrostatic properties of soil on the surface of Mars. Even though the insulator's surface is electrically shielded from the rubbing material by the grounded metal foil, charge measurements obtained by the MECA Electrometer after the metal foil is separated from the insulator's surface reveal that the insulator's surface does accumulate charge by indirect frictional charging. A possible explanation of the observations will be presented based on a simple contact barrier model.

Chromatic Titanium Photoanode for Dye-Sensitized Solar Cells under Rear Illumination.

PubMed

Huang, Chih-Hsiang; Chen, Yu-Wen; Chen, Chih-Ming

2018-01-24

Titanium (Ti) has high potential in many practical applications such as biomedicine, architecture, aviation, and energy. In this study, we demonstrate an innovative application of dye-sensitized solar cells (DSSCs) based on Ti photoanodes that can be integrated into the roof engineering of large-scale architectures. A chromatic Ti foil produced by anodizing oxidation (coloring) technology is an attractive roof material for large-scale architecture, showing a colorful appearance due to the formation of a reflective TiO 2 thin layer on both surfaces of Ti. The DSSC is fabricated on the backside of the chromatic Ti foil using the Ti foil as the working electrode, and this roof-DSSC hybrid configuration can be designed as an energy harvesting device for indoor artificial lighting. Our results show that the facet-textured TiO 2 layer on the chromatic Ti foil not only improves the optical reflectance for better light utilization but also effectively suppresses the charge recombination for better electron collection. The power conversion efficiency of the roof-DSSC hybrid system is improved by 30-40% with a main contribution from an improvement of short-circuit current density under standard 1 sun and dim-light (600-1000 lx) illumination.

Material Parameters for Creep Rupture of Austenitic Stainless Steel Foils

NASA Astrophysics Data System (ADS)

Osman, H.; Borhana, A.; Tamin, M. N.

2014-08-01

Creep rupture properties of austenitic stainless steel foil, 347SS, used in compact recuperators have been evaluated at 700 °C in the stress range of 54-221 MPa to establish the baseline behavior for its extended use. Creep curves of the foil show that the primary creep stage is brief and creep life is dominated by tertiary creep deformation with rupture lives in the range of 10-2000 h. Results are compared with properties of bulk specimens tested at 98 and 162 MPa. Thin foil 347SS specimens were found to have higher creep rates and higher rupture ductility than their bulk specimen counterparts. Power law relationship was obtained between the minimum creep rate and the applied stress with stress exponent value, n = 5.7. The value of the stress exponent is indicative of the rate-controlling deformation mechanism associated with dislocation creep. Nucleation of voids mainly occurred at second-phase particles (chromium-rich M23C6 carbides) that are present in the metal matrix by decohesion of the particle-matrix interface. The improvement in strength is attributed to the precipitation of fine niobium carbides in the matrix that act as obstacles to the movement of dislocations.

High density plasma gun generates plasmas at 190 kilometers per second

NASA Technical Reports Server (NTRS)

Espy, P. N.

1971-01-01

Gun has thin metal foil disc which positions or localizes gas to be ionized during electrical discharge cycle, overcoming major limiting factor in obtaining such plasmas. Expanding plasma front travels at 190 km/sec, compared to plasmas of 50 to 60 km/sec previously achieved.

Method and system for making integrated solid-state fire-sets and detonators

DOEpatents

O'Brien, Dennis W.; Druce, Robert L.; Johnson, Gary W.; Vogtlin, George E.; Barbee, Jr., Troy W.; Lee, Ronald S.

1998-01-01

A slapper detonator comprises a solid-state high-voltage capacitor, a low-jitter dielectric breakdown switch and trigger circuitry, a detonator transmission line, an exploding foil bridge, and a flier material. All these components are fabricated in a single solid-state device using thin film deposition techniques.

Erosion of mylar and protection by thin metal films

NASA Technical Reports Server (NTRS)

Fraundorf, P.; Lindstrom, D.; Sandford, S.; Swan, P.; Walker, R.; Zinner, E.; Pailer, N.

1983-01-01

Mylar strips, 2.5 microns thick, uncoated and coated with 50A, 100A and 200A of Al, Pd, and Au/Pd were exposed on STS-5 in order to measure the erosion of mylar and to test means of protecting thin plastic foils commonly used for space experiments in low earth orbit. Analysis by optical microscopy, SEM and STEM investigation, EDX measurements, FTIR spectroscopy and weight loss measurements showed that while up to 75 percent of the uncoated mylar was eroded during exposure, thin coatings of the above metals can protect mylar for integrated oxygen-fluxes of at least 10 to the 21st atoms/sq cm.

Preparation of copper-indium-gallium-diselenide precursor films by electrodeposition for fabricating high efficiency solar cells

DOEpatents

Bhattacharya, Raghu N.; Hasoon, Falah S.; Wiesner, Holm; Keane, James; Noufi, Rommel; Ramanathan, Kannan

1999-02-16

A photovoltaic cell exhibiting an overall conversion efficiency of 13.6% is prepared from a copper-indium-gallium-diselenide precursor thin film. The film is fabricated by first simultaneously electrodepositing copper, indium, gallium, and selenium onto a glass/molybdenum substrate (12/14). The electrodeposition voltage is a high frequency AC voltage superimposed upon a DC voltage to improve the morphology and growth rate of the film. The electrodeposition is followed by physical vapor deposition to adjust the final stoichiometry of the thin film to approximately Cu(In.sub.1-n Ga.sub.x)Se.sub.2, with the ratio of Ga/(In+Ga) being approximately 0.39.

The Chemical Vapor Deposition of Thin Metal Oxide Films

NASA Astrophysics Data System (ADS)

Laurie, Angus Buchanan

1990-01-01

Chemical vapor deposition (CVD) is an important method of preparing thin films of materials. Copper (II) oxide is an important p-type semiconductor and a major component of high T_{rm c} superconducting oxides. By using a volatile copper (II) chelate precursor, copper (II) bishexafluoroacetylacetonate, it has been possible to prepare thin films of copper (II) oxide by low temperature normal pressure metalorganic chemical vapor deposition. In the metalorganic CVD (MOCVD) production of oxide thin films, oxygen gas saturated with water vapor has been used mainly to reduce residual carbon and fluorine content. This research has investigated the influence of water-saturated oxygen on the morphology of thin films of CuO produced by low temperature chemical vapor deposition onto quartz, magnesium oxide and cubic zirconia substrates. ZnO is a useful n-type semiconductor material and is commonly prepared by the MOCVD method using organometallic precursors such as dimethyl or diethylzinc. These compounds are difficult to handle under atmospheric conditions. In this research, thin polycrystalline films of zinc oxide were grown on a variety of substrates by normal pressure CVD using a zinc chelate complex with zinc(II) bishexafluoroacetylacetonate dihydrate (Zn(hfa)_2.2H _2O) as the zinc source. Zn(hfa) _2.2H_2O is not moisture - or air-sensitive and is thus more easily handled. By operating under reduced-pressure conditions (20-500 torr) it is possible to substantially reduce deposition times and improve film quality. This research has investigated the reduced-pressure CVD of thin films of CuO and ZnO. Sub-micron films of tin(IV) oxide (SnO _2) have been grown by normal pressure CVD on quartz substrates by using tetraphenyltin (TPT) as the source of tin. All CVD films were characterized by X-ray powder diffraction (XRPD), scanning electron microscopy (SEM) and electron probe microanalysis (EPMA).

SR-XRD and SR-FTIR study of the alteration of silver foils in medieval paintings.

PubMed

Salvadó, Nati; Butí, Salvador; Labrador, Ana; Cinque, Gianfelice; Emerich, Hermann; Pradell, Trinitat

2011-03-01

Altarpieces and polychrome carved wood from the fifteenth century AD usually exhibit golden and silvery areas by the application of a very thin foil of metal. The metal foils were normally protected from the atmosphere by a varnish or resin which maybe either preserved or absent. Moreover, they were glued to the background surface by adhesive substances (egg yolk, drying oil or animal glue). The high proportion of the glueing substances often renders the development of reaction compounds. With time, silver alters blacken or simply disappear completely. In this paper, we study the alterations to metal foils from a selection of fifteenth century artworks showing different glueing agents, organic coatings and several degrees of conservation of the organic coatings and metal leafs. The submillimetric layered structure and the high variability and low amount of most of the compounds present in the different layers, as well as their differing nature (organic and inorganic) make the use of micron-sensitive high-resolution techniques essential for their study. In particular, the high resolution, high brilliance and small footprint renders synchrotron radiation most adequate for their study. SR-XRD was performed to identify the reaction compounds formed in the different layers; μFTIR was used at to identify the silver protecting organic coatings, the metal foil glueing layers and the corresponding reaction compounds. The results obtained suggest that atmospheric corrosion is the dominant mechanism, and therefore that the degree of corrosion of the metal foils is mainly related to the conservation state of the protecting coatings.

OSIRIS Modeling of High Energy Electron Transport in Warm Dense Matter

NASA Astrophysics Data System (ADS)

May, J.; Yabuuchi, T.; McGuffey, C.; Wei, Ms; Beg, F.; Mori, Wb

2016-10-01

In experiments on the Omega EP laser, a high intensity laser beam (eA /me c > 1) is focused onto a gold foil, generating relativistic electrons. Behind the Au foil is a layer of plastic foam through which the electrons are allowed to transport, and on the far side of the CH from the gold is a copper foil; electron fluence is measured by recording the k- α from that foil. The foam layer is either pre-ionized via a shock launched from an ablator irradiated earlier with a beam perpendicular to the high intensity beam; or the foam is in the solid state when the high intensity beam is switched on. In the latter case the foam - which has an initial density of 200mg /cm3 - heats to a temperature of 40eV and rarifies to a density of 30mg /cm3 . Results show an order of magnitude decrease in k- α when the CH layer is pre-ionized compared to cold CH. OSIRIS simulations indicate that the primary explanation for the difference in transport seen in the experiment is the partial resistive collimation of the beam in the higher density material, caused by collisional resistivity. The effect seems to be mostly caused by the higher density itself, with temperature having minimal effect. The authors acknowledge the support of the Department of Energy under contract DE-NA 0001833 and the National Science Foundation under contract ACI 1339893.

Manufacturing and testing a thin glass mirror shell with piezoelectric active control

NASA Astrophysics Data System (ADS)

Spiga, D.; Barbera, M.; Collura, A.; Basso, S.; Candia, R.; Civitani, M.; Di Bella, M.; Di Cicca, G.; Lo Cicero, U.; Lullo, G.; Pelliciari, C.; Riva, M.; Salmaso, B.; Sciortino, L.; Varisco, S.

2015-09-01

Optics for future X-ray telescopes will be characterized by very large aperture and focal length, and will be made of lightweight materials like glass or silicon in order to keep the total mass within acceptable limits. Optical modules based on thin slumped glass foils are being developed at various institutes, aiming at improving the angular resolution to a few arcsec HEW. Thin mirrors are prone to deform, so they require a careful integration to avoid deformations and even correct forming errors. On the other hand, this offers the opportunity to actively correct the residual deformation: a viable possibility to improve the mirror figure is the application of piezoelectric actuators onto the non-optical side of the mirrors, and several groups are already at work on this approach. The concept we are developing consists of actively integrating thin glass foils with piezoelectric patches, fed by voltages driven by the feedback provided by X-rays. The actuators are commercial components, while the tension signals are carried by a printed circuit obtained by photolithography, and the driving electronic is a multi-channel low power consumption voltage supply developed inhouse. Finally, the shape detection and the consequent voltage signal to be provided to the piezoelectric array are determined in X-rays, in intra-focal setup at the XACT facility at INAF/OAPA. In this work, we describe the manufacturing steps to obtain a first active mirror prototype and the very first test performed in X-rays.

Ultrasonic Spray Pyrolysis Deposited Copper Sulphide Thin Films for Solar Cell Applications

PubMed Central

Firat, Y. E.; Yildirim, H.; Erturk, K.

2017-01-01

Polycrystalline copper sulphide (CuxS) thin films were grown by ultrasonic spray pyrolysis method using aqueous solutions of copper chloride and thiourea without any complexing agent at various substrate temperatures of 240, 280, and 320°C. The films were characterized for their structural, optical, and electrical properties by X-ray diffraction (XRD), scanning electron microscopy (SEM), energy dispersive analysis of X-rays (EDAX), atomic force microscopy (AFM), contact angle (CA), optical absorption, and current-voltage (I-V) measurements. The XRD analysis showed that the films had single or mixed phase polycrystalline nature with a hexagonal covellite and cubic digenite structure. The crystalline phase of the films changed depending on the substrate temperature. The optical band gaps (Eg) of thin films were 2.07 eV (CuS), 2.50 eV (Cu1.765S), and 2.28 eV (Cu1.765S–Cu2S). AFM results indicated that the films had spherical nanosized particles well adhered to the substrate. Contact angle measurements showed that the thin films had hydrophobic nature. Hall effect measurements of all the deposited CuxS thin films demonstrated them to be of p-type conductivity, and the current-voltage (I-V) dark curves exhibited linear variation. PMID:29109807

Talbot-Lau x-ray deflectometer electron density diagnostic for laser and pulsed power high energy density plasma experiments (invited)

DOE Office of Scientific and Technical Information (OSTI.GOV)

Valdivia, M. P., E-mail: mpvaldivia@pha.jhu.edu; Stutman, D.; Stoeckl, C.

2016-11-15

Talbot-Lau X-ray deflectometry (TXD) has been developed as an electron density diagnostic for High Energy Density (HED) plasmas. The technique can deliver x-ray refraction, attenuation, elemental composition, and scatter information from a single Moiré image. An 8 keV Talbot-Lau interferometer was deployed using laser and x-pinch backlighters. Grating survival and electron density mapping were demonstrated for 25–29 J, 8–30 ps laser pulses using copper foil targets. Moiré pattern formation and grating survival were also observed using a copper x-pinch driven at 400 kA, ∼1 kA/ns. These results demonstrate the potential of TXD as an electron density diagnostic for HED plasmas.

M-shell resolved high-resolution X-ray spectroscopic study of transient matter evolution driven by hot electrons in kJ-laser produced plasmas

NASA Astrophysics Data System (ADS)

Condamine, F. P.; Šmíd, M.; Renner, O.; Dozières, M.; Thais, F.; Angelo, P.; Rosmej, F. B.

2017-03-01

Hot electrons represent a key subject for high intensity laser produced plasmas and atomic physics. Simulations of the radiative properties indicate a high sensitivity to hot electrons, that in turn provides the possibility for their detailed characterization by high-resolution spectroscopic methods. Of particular interest is X-ray spectroscopy due to reduced photo-absorption in dense matter and their efficient generation by hot electrons (inner-shell ionization/excitation). Here, we report on an experimental campaign conducted at the ns, kJ laser facility PALS at Prague in Czech Republic. Thin copper foils have been irradiated with 1ω pulses. Two spherically bent quartz Bragg crystal spectrometers with high spectral (λ/Δλ > 5000) and spatial resolutions (Δx = 30µm) have been set up simultaneously to achieve a high level of confidence for the complex Kα emission group. In particular, this group, which shows a strong overlap between lines, can be resolved in several substructures. Furthermore, an emission on the red wing of the Kα2 transition (λ = 1.5444A) could be identified with Hartree-Fock atomic structure calculations. We discuss possible implications for the analysis of non-equilibrium phenomena and present first simulations.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Schultz, Bradley M.; Li, Nan; Economy, David R.

Mathematical models suggest that the strain along the film formed by parallel passes of a nanoindentation probe in contact with the film can be either homogenous or heterogeneous, depending on contact pressure and spacing between passes. Here, in this study, a 1 µm copper thin film was worn with a cono-spherical diamond probe with normal loads ranging from 25 to 800 µN and wear box edge lengths of 40, 60, and 80 µm. The nanoindenter counterface was rastered across the surface to mimic dry sliding wear. To determine potential strain field changes, 10-step quasi-static indents (200–2000 µN) were performed usingmore » nanoindentation inside the wear boxes created at various loads to determine if a strain field alteration could be observed in changes in hardness of the copper thin film. It was shown that there was a softening effect in the hardness for normal loads < 400 µN used during nanowear compared to the as-deposited copper. Normal loads ≥ 400 µN had a similar or higher hardness than the as-deposited copper. This is believed to have occurred due to a relaxation in the residual stresses created during deposition in the copper thin films at lower loads, which caused a decrease in hardness. Conversely, at the higher loads, increased deformation leads to an increase in hardness. Lastly, all of the wear boxes displayed a higher estimated strain hardening exponent than the as-deposited material.« less

PEN as self-vetoing structural material

NASA Astrophysics Data System (ADS)

Majorovits, B.; Eck, S.; Fischer, F.; Gooch, C.; Hayward, C.; Kraetzschmar, T.; van der Kolk, N.; Muenstermann, D.; Schulz, O.; Simon, F.

2018-01-01

Polyethylene Naphtalate (PEN) is a mechanically very favorable polymer. Earlier it was found that thin foils made from PEN can have very high radio-purity compared to other commercially available foils. In fact, PEN is already in use for low background signal transmission applications (cables). Recently it has been realized that PEN also has favorable scintillating properties. In combination, this makes PEN a very promising candidate as a self-vetoing structural material in low background experiments. Components instrumented with light detectors could be built from PEN. This includes detector holders, detector containments, signal transmission links, etc. The current R&D towards qualification of PEN as a self-vetoing low background structural material is be presented.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Song, Bo; Yao, Shurong; Nie, Xu

In this paper, a new type of highly stretchable strain sensor was developed to measure large strains. The sensor was based on the piezo-resistive response of carbon nanotube (CNT)/polydimethylsiloxane (PDMS) composite thin films. The piezo-resistive response of CNT composite gives accurate strain measurement with high frequency response, while the ultra-soft PDMS matrix provides high flexibility and ductility for large strain measurement. Experimental results show that the CNT/PDMS sensor measures large strains (up to 8 %) with an excellent linearity and a fast frequency response. The new miniature strain sensor also exhibits much higher sensitivities than the conventional foil strain gages,more » as its gauge factor is 500 times of that of the conventional foil strain gages.« less

A flexible top-emitting organic light-emitting diode on steel foil

NASA Astrophysics Data System (ADS)

Xie, Zhiyuan; Hung, Liang-Sun; Zhu, Furong

2003-11-01

An efficient flexible top-emitting organic light-emitting diode (FTOLED) was developed on a thin steel foil. The FTOLED was constructed on the spin-on-glass (SOG)-coated steel substrate with an organic stack of NPB/Alq 3 sandwiched by a highly reflective Ag anode and a semitransparent Sm cathode. An ultrathin plasma-polymerized hydrocarbon film (CF X) was interposed between the Ag anode and the NPB layer to enhance hole-injection, and an additional Alq 3 layer was overlaid on the Sm cathode to increase light output. The FTOLED showed a peak efficiency of 4.4 cd/A higher than 3.7 cd/A of a convention NPB/Alq 3-based bottom-emitting OLED.

Examinations on Laser Remote Welding of Ultra-thin Metal Foils Under Vacuum Conditions

NASA Astrophysics Data System (ADS)

Petrich, Martin; Stambke, Martin; Bergmann, Jean Pierre

Metal foils are commonly used for catalytic converters, vacuum insulations, in medical and electrical industry as well as for sensor applications and packaging. The investigations in this paper determine the influence of reduced atmospheric pressure during the welding process with a highly brilliant 400 W single-mode fiber laser combined with a 2D-scanning system. The laser beam is transmitted through a highly transparent glass into a vacuum chamber, where AISI 304 stainless steel foils with a thickness of 25 μm, 50 μm and 100 μm are positioned. The effects of reduced atmospheric pressure on the plasma formation are investigated by means of high-speed videography. Furthermore, the geometry of the weld seam is compared to atmospheric conditions as well as means of the process stability and the process efficiency. The welds were also evaluated by means of metallography. The research is a contribution for extending the range of micro welding applications and shows new aspects for future developments.

Metastable alloy materials produced by solid state reaction of compacted, mechanically deformed mixtures

DOEpatents

Atzmon, Michael; Johnson, William L.; Verhoeven, John D.

1987-01-01

Bulk metastable, amorphous or fine crystalline alloy materials are produced by reacting cold-worked, mechanically deformed filamentary precursors such as metal powder mixtures or intercalated metal foils. Cold-working consolidates the metals, increases the interfacial area, lowers the free energy for reaction, and reduces at least one characteristic dimension of the metals. For example, the grains (13) of powder or the sheets of foil are clad in a container (14) to form a disc (10). The disc (10) is cold-rolled between the nip (16) of rollers (18,20) to form a flattened disc (22). The grains (13) are further elongated by further rolling to form a very thin sheet (26) of a lamellar filamentary structure (FIG. 4) containing filaments having a thickness of less than 0.01 microns. Thus, diffusion distance and time for reaction are substantially reduced when the flattened foil (28) is thermally treated in oven (32) to form a composite sheet (33) containing metastable material (34) dispersed in unreacted polycrystalline material (36).

Combined synchrotron X-ray tomography and X-ray powder diffraction using a fluorescing metal foil.

PubMed

Kappen, P; Arhatari, B D; Luu, M B; Balaur, E; Caradoc-Davies, T

2013-06-01

This study realizes the concept of simultaneous micro-X-ray computed tomography and X-ray powder diffraction using a synchrotron beamline. A thin zinc metal foil was placed in the primary, monochromatic synchrotron beam to generate a divergent wave to propagate through the samples of interest onto a CCD detector for tomographic imaging, thus removing the need for large beam illumination and high spatial resolution detection. Both low density materials (kapton tubing and a piece of plant) and higher density materials (Egyptian faience) were investigated, and elemental contrast was explored for the example of Cu and Ni meshes. The viability of parallel powder diffraction using the direct beam transmitted through the foil was demonstrated. The outcomes of this study enable further development of the technique towards in situ tomography∕diffraction studies combining micrometer and crystallographic length scales, and towards elemental contrast imaging and reconstruction methods using well defined fluorescence outputs from combinations of known fluorescence targets (elements).

In-situ grown nanoporous Zn-Cu catalysts on brass foils for enhanced electrochemical reduction of carbon dioxide

NASA Astrophysics Data System (ADS)

Hu, Hanjun; Tang, Yang; Hu, Qing; Wan, Pingyu; Dai, Liming; Yang, Xiao Jin

2018-07-01

In-situ grown nanoporous Zn-Cu catalysts were prepared by simply annealing a commercial brass foil at 500 °C in air, followed by electrochemical reduction. During the annealing process, Zn preferentially melted and migrated out of the framework of the alloy to form a thin layer of ZnO on its surface. Subsequent electroreduction created nanoporous Zn-enriched surface. The Zn concentration increased from 36% to 50% by 10 min, to 81% by 3 h, and to 87% by 12 h annealing treatment while the average pore size decreased from 290 nm to 120 nm as the annealing time increased from 1 h to 12 h. Faradaic efficiency of CO2 reduction to CO and HCOOH was enhanced by nearly 4 and 6 times, respectively, as compared to untreated brass foils. The nanoporous Zn-Cu catalyst presented a stable ratio of CO/H2 and a steady working current density in a continuous electrolysis of 18 h in 0.5 M KHCO3 solution.

Method for providing uranium with a protective copper coating

DOEpatents

Waldrop, Forrest B.; Jones, Edward

1981-01-01

The present invention is directed to a method for providing uranium metal with a protective coating of copper. Uranium metal is subjected to a conventional cleaning operation wherein oxides and other surface contaminants are removed, followed by etching and pickling operations. The copper coating is provided by first electrodepositing a thin and relatively porous flash layer of copper on the uranium in a copper cyanide bath. The resulting copper-layered article is then heated in an air or inert atmosphere to volatilize and drive off the volatile material underlying the copper flash layer. After the heating step an adherent and essentially non-porous layer of copper is electro-deposited on the flash layer of copper to provide an adherent, multi-layer copper coating which is essentially impervious to corrosion by most gases.

Planetary Geomorphology

NASA Technical Reports Server (NTRS)

Malin, Michael C.

1990-01-01

One of the major problems in the series of ice runs was that the subsurface temperature probes did not function. AIC re-evaluated the design and, after testing several suitable sensors, installed 50 type T thermocouples, each 2 m long. In this design, each thermocouple was soldered to a rectangular copper foil spreader 0.3 com wide by 2.8 cm long to ensure an acute reading. The long rectangular shape was used because it had a large area for good thermal connection to the test material.

Highly sensitive antenna using inkjet overprinting with particle-free conductive inks.

PubMed

Komoda, Natsuki; Nogi, Masaya; Suganuma, Katsuaki; Otsuka, Kanji

2012-11-01

Printed antennas with low signal losses and fast response in high-frequency bands have been required. Here we reported on highly sensitive antennas using additive patterning of particle-free metallo-organic decomposition silver inks. Inkjet overprinting of metallo-organic decomposition inks onto copper foil and silver nanowire line produced antenna with mirror surfaces. As a result, the overprinted antennas decreased their return losses at 0.5-4.0 GHz and increased the speed of data communication in WiFi network.

Characterization and Fate of Gun and Rocket Propellant Residues on Testing and Training Ranges

DTIC Science & Technology

2011-08-01

propellant sticks, is tied in three places with polyester and cotton thread ties. The bundle is then wrapped in lead foil (a de-coppering agent...sticks and the tying of the bundle in five places, again using polyester and cotton thread ties. The combustible case is manufactured mainly from...and brought back to DRDC to be weighed and extracted to measure the remaining 2,4-DNT. Most of what was collected was the remains of the cotton

Niobium thin film coating on a 500-MHz copper cavity by plasma deposition

DOE Office of Scientific and Technical Information (OSTI.GOV)

Haipeng Wang; Genfa Wu; H. Phillips

2005-05-16

A system using an Electron Cyclotron Resonance (ECR) plasma source for the deposition of a thin niobium film inside a copper cavity for superconducting accelerator applications has been designed and is being constructed. The system uses a 500-MHz copper cavity as both substrate and vacuum chamber. The ECR plasma will be created to produce direct niobium ion deposition. The central cylindrical grid is DC biased to control the deposition energy. This paper describes the design of several subcomponents including the vacuum chamber, RF supply, biasing grid and magnet coils. Operational parameters are compared between an operating sample deposition system andmore » this system. Engineering work progress toward the first plasma creation will be reported here.« less

Method and system for making integrated solid-state fire-sets and detonators

DOEpatents

O`Brien, D.W.; Druce, R.L.; Johnson, G.W.; Vogtlin, G.E.; Barbee, T.W. Jr.; Lee, R.S.

1998-03-24

A slapper detonator comprises a solid-state high-voltage capacitor, a low-jitter dielectric breakdown switch and trigger circuitry, a detonator transmission line, an exploding foil bridge, and a flier material. All these components are fabricated in a single solid-state device using thin film deposition techniques. 13 figs.

Model and Subcomponent Development for a Pulse-Combustor-Driven Microgenerator

DTIC Science & Technology

2004-08-31

sputtering of thin magnetic and dielectric layers [4]; and mechanical lamination of polymer -coated NiFe foils [5]. Although these approaches have...photomicrograph of the fabricated device is given in Figure 4.2-6. 3d solenoid- like Cu coil EPOXY SU8 NIFE LAMINATE D CORE Figure 4.2-6 Photomicrograph

A microcalorimeter for measuring heat effects of electrochemical reactions with submonolayer conversions

NASA Astrophysics Data System (ADS)

Etzel, Kai D.; Bickel, Katrin R.; Schuster, Rolf

2010-03-01

We present a microcalorimeter for measuring heat effects during electrochemical reactions with conversions down to a few percent of a monolayer, referenced to the electrode's surface atoms. The design uses a thin pyroelectric polymer foil for temperature measurement at the backside of a thin electrode, similar to the concepts pioneered by the groups of D. A. King and Ch. T. Campbell for UHV adsorption microcalorimetry. To establish intimate thermal contact between electrode and sensor and utmost sensitivity, the free standing sensor and electrode foils are pressed together by air pressure, acting on the electrochemical cell. Pyroelectric temperature sensing is combined with pulsed electrochemistry, where the electrochemical heat is released on a time scale of about 10 ms, which is long enough for thermal equalization of the electrode-sensor assembly but short enough to avoid significant heat loss into electrolyte and cell compartment. As examples heat effects upon Ag deposition and dissolution as well as the electron transfer reaction of [Fe(CN)6]4-/[Fe(CN)6]3- are presented. The latter reaction was also employed for the calibration of the calorimeter.

Internal stress-assisted epitaxial lift-off process for flexible thin film (In)GaAs solar cells on metal foil

NASA Astrophysics Data System (ADS)

Kim, Youngjo; Kim, Kangho; Jung, Sang Hyun; Kim, Chang Zoo; Shin, Hyun-Beom; Choi, JeHyuk; Kang, Ho Kwan

2017-12-01

Flexible thin film (In)GaAs solar cells are grown by metalorganic chemical vapor deposition on GaAs substrates and transferred to 30 μm thick Au foil by internal stress-assisted epitaxial lift-off processes. The internal stress is induced by replacing the solar cell epi-layers from GaAs to In0.015Ga0.985As, which has a slightly larger lattice constant. The compressive strained layer thickness was varied from 0 to 4.5 μm to investigate the influence of the internal stress on the epitaxial lift-off time. The etching time in the epitaxial lift-off process was reduced from 36 to 4 h by employing a GaAs/In0.015Ga0.985As heterojunction structure that has a compressive film stress of -59.0 MPa. We found that the partially strained epi-structure contributed to the much faster lateral etching rate with spontaneous bending. Although an efficiency degradation problem occurred in the strained solar cell, it was solved by optimizing the epitaxial growth conditions.

Modelling the effects of the radiation reaction force on the interaction of thin foils with ultra-intense laser fields

NASA Astrophysics Data System (ADS)

Duff, M. J.; Capdessus, R.; Del Sorbo, D.; Ridgers, C. P.; King, M.; McKenna, P.

2018-06-01

The effects of the radiation reaction (RR) force on thin foils undergoing radiation pressure acceleration (RPA) are investigated. Using QED-particle-in-cell simulations, the influence of the RR force on the collective electron dynamics within the target can be examined. The magnitude of the RR force is found to be strongly dependent on the target thickness, leading to effects which can be observed on a macroscopic scale, such as changes to the distribution of the emitted radiation and the target dynamics. This suggests that such parameters may be controlled in experiments at multi-PW laser facilities. In addition, the effects of the RR force are characterized in terms of an average radiation emission angle. We present an analytical model which, for the first time, describes the effect of the RR force on the collective electron dynamics within the ‘light-sail’ regime of RPA. The predictions of this model can be tested in future experiments with ultra-high intensity lasers interacting with solid targets.

Soft X-ray Spectrometer for Characterization of Electron Beam Driven WDM

NASA Astrophysics Data System (ADS)

Ramey, Nicholas; Coleman, Joshua; Perry, John

2017-10-01

A preliminary design study is being performed on a soft X-ray spectrometer to measure K-shell spectra emitted by a warm dense plasma generated by an intense, relativistic electron beam interacting with a thin, low-Z metal foil. A 100-ns-long electron pulse with a beam current of 1.7 kA and energy of 19.8 MeV deposits energy into the thin metal foil heating it to a warm dense plasma. The collisional ionization of the target by the electron beam produces an anisotropic angular distribution of K-shell radiation and a continuum of both scattered electrons and Bremsstrahlung up to the beam energy of 19.8 MeV. A proof-of-principle Bragg-type spectrometer has been built to measure the Ti K- α and K- β lines. The goal of the spectrometer is to measure the temperature and density of this warm dense plasma for the first time with this heating technique. This work was supported by the National Nuclear Security Administration of the U.S. Department of Energy under Contract No. DE-AC52-06NA25396.

Design, Synthesis and Characterization of Novel Graphene-Based Nanoarchitectures for Sustainability

NASA Astrophysics Data System (ADS)

Bay, Hamed Hosseini

The unique structure and properties of graphene initiated broad fundamental and technological research in recent years, and highlighted graphene as an alternative for various applications such as energy storage and nanoelectronics. Chemical vapor deposition (CVD) of graphene on copper is believed to be the most promising method for large-scale synthesis of continuous sheets. The exceptional properties of graphene however, are governed by its microstructure. The size of graphene grains and the grain boundaries affect the carrier mobility. Therefore understanding the formation mechanism of graphene is critical to control the microstructure and physical properties. We implemented Fluorescence Quenching Microscopy (FQM) in conjunction with other methods to understand a trend which is pertinent in large-scale. In order to investigate the nucleation and growth mechanism of graphene on copper and its subsequent microstructure, effect of key parameters such as density of defects in copper foils and growth pressure in the CVD chamber have been altered. Results point out that microstructure of copper regulates the structure and properties of graphene and heat treatment and electropolishing of the foil substrates as well as controlling the saturation pressure of the carbon precursor yield to large graphene domains. Water decontamination and oil/water separation are principal motives in the surge to develop novel means for sustainability. In this prospect, supplying clean water for the ecosystems is as important as the recovery of the oil spills since the supplies are scarce. Inspired to design an engineering material which not only serves this purpose, but can also be altered for other applications to preserve natural resources, a facile template-free process is suggested to fabricate a superporous, superhydrophobic graphene-based sponge. Moreover, the process is designed to be inexpensive and scalable. The fabricated sponge can be used to clean up different types of oil, organic solvents, toxic and corrosive contaminants. This versatile microstructure can retain its functionality even when pulverized. The sponge is applicable for targeted sorption and collection due to its ferromagnetic properties. We hope that such cost-effective process can be embraced and implemented widely.

Sensing of volatile organic compounds by copper phthalocyanine thin films

NASA Astrophysics Data System (ADS)

Ridhi, R.; Saini, G. S. S.; Tripathi, S. K.

2017-02-01

Thin films of copper phthalocyanine have been deposited by thermal evaporation technique. We have subsequently exposed these films to the vapours of methanol, ethanol and propanol. Optical absorption, infrared spectra and electrical conductivities of these films before and after exposure to chemical vapours have been recorded in order to study their sensing mechanisms towards organic vapours. These films exhibit maximum sensing response to methanol while low sensitivities of the films towards ethanol and propanol have been observed. The changes in sensitivities have been correlated with presence of carbon groups in the chemical vapours. The effect of different types of electrodes on response-recovery times of the thin film with organic vapours has been studied and compared. The electrodes gap distance affects the sensitivity as well as response-recovery time values of the thin films.

Investigation on Structural and Optical Properties of Copper Telluride Thin Films with Different Annealing Temperature

NASA Astrophysics Data System (ADS)

Nishanthini, R.; Muthu Menaka, M.; Pandi, P.; Bahavan Palani, P.; Neyvasagam, K.

The copper telluride (Cu2Te) thin film of thickness 240nm was coated on a microscopic glass substrate by thermal evaporation technique. The prepared films were annealed at 150∘C and 250∘C for 1h. The annealing effect on Cu2Te thin films was examined with different characterization methods like X-ray Diffraction Spectroscopy (XRD), Scanning Electron Microscopy (SEM), Ultra Violet-Visible Spectroscopy (UV-VIS) and Photoluminescence (PL) Spectroscopy. The peak intensities of XRD spectra were increased while increasing annealing temperature from 150∘C to 250∘C. The improved crystallinity of the thin films was revealed. However, the prepared films are exposed complex structure with better compatibility. Moreover, the shift in band gap energy towards higher energies (blue shift) with increasing annealing temperature is observed from the optical studies.

Preparation of cuxinygazsen (X=0-2, Y=0-2, Z=0-2, N=0-3) precursor films by electrodeposition for fabricating high efficiency solar cells

DOEpatents

Bhattacharya, Raghu N.; Contreras, Miguel A.; Keane, James; Tennant, Andrew L.; Tuttle, John R.; Ramanathan, Kannan; Noufi, Rommel

1998-03-24

High quality thin films of copper-indium-gallium-diselenide useful in the production of solar cells are prepared by electrodepositing at least one of the constituent metals onto a glass/Mo substrate, followed by physical vapor deposition of copper and selenium or indium and selenium to adjust the final stoichiometry of the thin film to approximately Cu(In,Ga)Se.sub.2. Using an AC voltage of 1-100 KHz in combination with a DC voltage for electrodeposition improves the morphology and growth rate of the deposited thin film. An electrodeposition solution comprising at least in part an organic solvent may be used in conjunction with an increased cathodic potential to increase the gallium content of the electrodeposited thin film.

Fixation of the stressed state of glass plates by coating them with thin films using a plasma focus installation

NASA Astrophysics Data System (ADS)

Kolokoltsev, V. N.; Degtiarev, V. F.; Borovitskaya, I. V.; Nikulin, V. Ya.; Peregudova, E. N.; Silin, P. V.; Eriskin, A. A.

2018-01-01

Elastic deformation in transparent mediums is usually studied by the photoelasticity method. For opaque mediums the method of film coating and strain gauge method are used. After the external load was removed, the interference pattern corresponding to elastic deformation of the material disappears. It is found that the elastic deformation state of the thin glass plate under the action of concentrated load can be fixed during the deposition of a thin metal film. Deposition of thin copper films was carried out by passing of plasma through the copper tube installed inside the Plasma Focus installation. After removing of the load, interference pattern on the glass plates was observed in the form of Newton’s rings and isogers in non-monochromatic light on the CCD scanners which uses uorescent lamps with cold cathode. It is supposed that the copper film fixes the relief of the surface of the glass plate at the time of deformation and saves it when the load is removed. In the case of a concentrated load, this relief has the shape of a thin lens of large radius. For this reason, the interference of coherent light rays in a thin air gap between the glass of the scanners atbed and the lens surface has the shape of Newton's rings. In this case, when scanning the back side of the plate, isogyres are observed. The presented method can be used in the analysis of the mechanical stress in a various optical elements.

Conformable wearable systems comprising organic electronics on foil for well being and healthcare (presentation video)

NASA Astrophysics Data System (ADS)

de Kok, Margreet M.

2014-10-01

Integration of electronics into materials and objects that have not been functionalized with electronics before, open up extensive possibilities to support mankind. By adding intelligence and/or operating power to materials in close skin contact like clothing, furniture or bandages the health of people can be monitored or even improved. Foil based electronics are interesting components to be integrated as they are thin, large area and cost effective available components Our developed technology of printed electronic structures to which components are reliably bonded, fulfills the promise. We have integrated these components into textiles and built wearable encapsulated products with foil based electronics. Foil components with organic and inorganic LEDs are interconnected and laminated onto electronic textiles by using conductive adhesives to bond the contact pads of the component to conductive yarns in the textile. Modelling and reliability testing under dynamic circumstances provided important insights in order to optimise the technology. The design of the interconnection and choice of conductive adhesive / underfill and lamination contributed to the durability of the system. Transition zones from laminated foil to textile are engineered to withstand dynamic use. As an example of a product, we have realized an electronic wristband that is encapsulated in rubber and has a number of sensor functionalities integrated on stretchable electronic circuits based on Cu and Ag. The encapsulation with silicone or polyurethanes was performed such, that charging and sensor/skin contacts are possible while simultaneously protecting the electronics from mechanical and environmental stresses.

Thin-film CdTe detector for microdosimetric study of radiation dose enhancement at gold-tissue interface.

PubMed

Paudel, Nava Raj; Shvydka, Diana; Parsai, E Ishmael

2016-09-08

Presence of interfaces between high and low atomic number (Z) materials, often encountered in diagnostic imaging and radiation therapy, leads to radiation dose perturbation. It is characterized by a very narrow region of sharp dose enhancement at the interface. A rapid falloff of dose enhancement over a very short distance from the interface makes the experimental dosimetry nontrivial. We use an in-house-built inexpensive thin-film Cadmium Telluride (CdTe) photodetector to study this effect at the gold-tissue interface and verify our experimental results with Monte Carlo (MC) modeling. Three-micron thick thin-film CdTe photodetectors were fabricated in our lab. One-, ten- or one hundred-micron thick gold foils placed in a tissue-equivalent-phantom were irradiated with a clinical Ir-192 high-dose-rate (HDR) source and current measured with a CdTe detector in each case was compared with the current measured for all uniform tissue-equivalent phantom. Percentage signal enhancement (PSE) due to each gold foil was then compared against MC modeled percentage dose enhancement (PDE), obtained from the geometry mimicking the experimental setup. The experimental PSEs due to 1, 10, and 100 μm thick gold foils at the closest measured distance of 12.5μm from the interface were 42.6 ± 10.8 , 137.0 ± 11.9, and 203.0 ± 15.4, respectively. The corresponding MC modeled PDEs were 38.1 ± 1, 164 ± 1, and 249 ± 1, respectively. The experimental and MC modeled values showed a closer agreement at the larger distances from the interface. The dose enhancement in the vicinity of gold-tissue interface was successfully measured using an in-house-built, high-resolution CdTe-based photodetector and validated with MC simulations. A close agreement between experimental and the MC modeled results shows that CdTe detector can be utilized for mapping interface dose distribution encountered in the application of ionizing radiation. © 2016 The Authors.

Characteristics of coated copper wire specimens using high frequency ultrasonic complex vibration welding equipments.

PubMed

Tsujino, J; Ihara, S; Harada, Y; Kasahara, K; Sakamaki, N

2004-04-01

Welding characteristic of thin coated copper wires were studied using 40, 60, 100 kHz ultrasonic complex vibration welding equipments with elliptical to circular vibration locus. The complex vibration systems consisted of a longitudinal-torsional vibration converter and a driving longitudinal vibration system. Polyurethane coated copper wires of 0.036 mm outer diameter and copper plates of 0.3 mm thickness and the other dimension wires were used as welding specimens. The copper wire part is completely welded on the copper substrate and the insulated coating material is driven from welded area to outsides of the wire specimens by high frequency complex vibration.

Measurements of the ^89Y(n,n')^89Y^m reaction cross section using the ASP D-T fusion source

NASA Astrophysics Data System (ADS)

Simons, Andrew; Gardner, Matthew; Williams, Ben; Rubery, Michael

2012-10-01

A programme of measurements of the ^89Y(n,n')^89Y^m reaction cross section has commenced at AWE using the ASP accelerator to impinge deuterons onto tritiated titanium layers mounted on copper discs producing fluxes of approximately 10^11 neutrons per second. The neutrons are generated for up to half an hour and are used to excite Yttrium into its first isomeric state at 909.1 keV which then decays with a half life of 15.7 seconds. Two other high purity foils (of ^27Al and ^63,65Cu) are used as a reference to establish consistency between the isotopes energetic and temporal decay signatures. These foils mainly serve to check the reported total neutron fluence, produced by the accelerator, incident on the targets. The activation foils are extracted from the irradiation position by a pneumatic transfer system in ˜ 7 seconds and are transferred to the counting station in 5 to 30 seconds. Data are taken with a BEGe detector and recorded with both a Canberra Genie analogue system and a Xia Pixie-4 digital system. The results from the first campaigns are presented with a discussion of improvements and future plans.

Multiple scattering of 13 and 20 MeV electrons by thin foils: a Monte Carlo study with GEANT, Geant4, and PENELOPE.

PubMed

Vilches, M; García-Pareja, S; Guerrero, R; Anguiano, M; Lallena, A M

2009-09-01

In this work, recent results from experiments and simulations (with EGSnrc) performed by Ross et al. [Med. Phys. 35, 4121-4131 (2008)] on electron scattering by foils of different materials and thicknesses are compared to those obtained using several Monte Carlo codes. Three codes have been used: GEANT (version 3.21), Geant4 (version 9.1, patch03), and PENELOPE (version 2006). In the case of PENELOPE, mixed and fully detailed simulations have been carried out. Transverse dose distributions in air have been obtained in order to compare with measurements. The detailed PENELOPE simulations show excellent agreement with experiment. The calculations performed with GEANT and PENELOPE (mixed) agree with experiment within 3% except for the Be foil. In the case of Geant4, the distributions are 5% narrower compared to the experimental ones, though the agreement is very good for the Be foil. Transverse dose distribution in water obtained with PENELOPE (mixed) is 4% wider than those calculated by Ross et al. using EGSnrc and is 1% narrower than the transverse dose distributions in air, as considered in the experiment. All the codes give a reasonable agreement (within 5%) with the experimental results for all the material and thicknesses studied.

Enhanced pair plasma generation in the relativistic transparency regime

NASA Astrophysics Data System (ADS)

Liu, W. Y.; Luo, W.; Yuan, T.; Yu, J. Y.; Chen, M.; Sheng, Z. M.

2017-10-01

Electron-positron ( e - e + ) pair plasma generation in the relativistic transparency regime in a thin foil with a fixed thickness irradiated by two counter-propagating laser pulses is investigated through multi-dimensional particle-in-cell simulations. It is shown that target transparency can significantly enhance the pair generation due to the formation of a stable standing wave. An optimum foil density of 200-280 n c (with nc being the critical plasma density of the incident laser at the wavelength of 1 μm) is found for enhanced e - e + pair generation for laser intensity around 10 PW. With such foil density, laser energy transformed to pair plasma formation is approximately four times higher than that with a foil density of 710 nc, while the laser energy transformed to γ-photons remains almost the same. Dense e - e + plasma with a density as high as 10 22 cm - 3 ( ≃ 10 n c ) can be produced accordingly. Comparison of pair plasma generation between cases with fundamental and double frequency driver lasers further demonstrates such an enhancement effect. It shows that when the duration of the laser pulse is relatively short, the double frequency driver can generate more pair plasmas due to the earlier excitation of relativistic transparency.

New technique for heterogeneous vapor-phase synthesis of nanostructured metal layers from low-dimensional volatile metal complexes

NASA Astrophysics Data System (ADS)

Badalyan, A. M.; Bakhturova, L. F.; Kaichev, V. V.; Polyakov, O. V.; Pchelyakov, O. P.; Smirnov, G. I.

2011-09-01

A new technique for depositing thin nanostructured layers on semiconductor and insulating substrates that is based on heterogeneous gas-phase synthesis from low-dimensional volatile metal complexes is suggested and tried out. Thin nanostructured copper layers are deposited on silicon and quartz substrates from low-dimensional formate complexes using a combined synthesis-mass transport process. It is found that copper in layers thus deposited is largely in a metal state (Cu0) and has the form of closely packed nanograins with a characteristic structure.

Characterization of defects in copper antimony disulfide

DOE PAGES

Willian de Souza Lucas, Francisco; Peng, Haowei; Johnston, Steve; ...

2017-09-19

Copper antimony disulfide (CuSbS 2) has several excellent bulk optoelectronic properties for photovoltaic absorber applications. Here, we report on the defect properties in CuSbS 2thin film materials and photovoltaic devices studied using several experimental methods supported by theoretical calculations.

Transient line starting analysis of the ultra-high speed PMSM

PubMed Central

Cheng, Wenjie; Li, Wei; Xiao, ling; Li, Ming; Tian, Yongsheng; Sun, Yanhua; Yu, Lie

2017-01-01

Aiming at the ultra high speed permanent magnet synchronous motor (PMSM) supported by gas foil bearings (GFBs), this paper calculates the transient line starting of the motor. Firstly, the start effect of the rotor composed of cylindrical PM and stainless steel sleeve is studied. Then, in order to enhance the start torque, copper ring, nickel ring and copper squirrel-cage are introduced in the rotor and their start effect are analysed, respectively. It can be found that the rotor including nickel ring can be accelerated to set speed, but all the other rotors are failed due to the higher PM and braking torques. It can be concluded that some material owning slight large relative permeability can be applied in the rotor to reduce the PM field and contribute to start by using the line-start method. PMID:28105384

Synthesis of Large-grain, Single-crystalline Monolayer and AB-stacking Bilayer Graphene

NASA Astrophysics Data System (ADS)

Zhang, Luyao; Lin, Yung-Chen; Zhang, Yi; Chang, Han-Wen; Yeh, Wen-Cheng; Zhou, Chongwu; USC Nanotechnology Research Laboratory Team

2013-03-01

We report the growth of large-grain, single-crystalline monolayer and AB-stacking bilayer graphene by the combination of ambient pressure chemical vapor deposition and low pressure chemical vapor deposition. The shape of the monolayer graphene was modified to be either hexagons or flowers under different growth conditions. The size of the bilayer graphene region was enlarged under ambient pressure growth conditions with low methane concentration. Raman spectra and selected area electron diffraction of individual graphene grain indicated that the each graphene grain is single-crystalline. With electron beam lithography patterned PMMA seeds, graphene nucleation can be controlled and graphene monolayer and bilayer arrays were synthesized on copper foil. Electron backscatter diffraction study revealed that the graphene morphology had little correlation with the crystalline orientation of underlying copper substrate. Mork Family Department of Chemical Engineering and Materials Science

Development of a highly reliable composite board for printed circuitry for use in space environment

NASA Technical Reports Server (NTRS)

Bradbury, E. J.; Markle, R. A.; Dunnavant, W. R.; Stickney, P. B.

1971-01-01

Materials, processes and fabrication techniques have been investigated for the development of a high-temperature circuit-board laminate. High quality, void-free copper-clad laminates have been made using 7628/HS-1 style fiberglas reinforcements with filled polyimide matrices. The fabricating characteristics of P13N resin appear suitable for use as a filled matrix in this circuit board development. High-fired, ball-milled alumina appears to be necessary to obtain the desired effects in the circuit board system. Nickel-clad copper foil bonding surfaces appear to be another requirement for retention of good bond strengths after art work and plating sequences. The fabrication cycle for this circuit board system is very dependent on the heating profile. Very rapid heating with quick loading is recommended. A stack approach to lamination was successfully used.

"Silicon millefeuille": From a silicon wafer to multiple thin crystalline films in a single step

NASA Astrophysics Data System (ADS)

Hernández, David; Trifonov, Trifon; Garín, Moisés; Alcubilla, Ramon

2013-04-01

During the last years, many techniques have been developed to obtain thin crystalline films from commercial silicon ingots. Large market applications are foreseen in the photovoltaic field, where important cost reductions are predicted, and also in advanced microelectronics technologies as three-dimensional integration, system on foil, or silicon interposers [Dross et al., Prog. Photovoltaics 20, 770-784 (2012); R. Brendel, Thin Film Crystalline Silicon Solar Cells (Wiley-VCH, Weinheim, Germany 2003); J. N. Burghartz, Ultra-Thin Chip Technology and Applications (Springer Science + Business Media, NY, USA, 2010)]. Existing methods produce "one at a time" silicon layers, once one thin film is obtained, the complete process is repeated to obtain the next layer. Here, we describe a technology that, from a single crystalline silicon wafer, produces a large number of crystalline films with controlled thickness in a single technological step.

Cu-Doped ZnO Thin Films Deposited by a Sol-Gel Process Using Two Copper Precursors: Gas-Sensing Performance in a Propane Atmosphere.

PubMed

Gómez-Pozos, Heberto; Arredondo, Emma Julia Luna; Maldonado Álvarez, Arturo; Biswal, Rajesh; Kudriavtsev, Yuriy; Pérez, Jaime Vega; Casallas-Moreno, Yenny Lucero; Olvera Amador, María de la Luz

2016-01-29

A study on the propane gas-sensing properties of Cu-doped ZnO thin films is presented in this work. The films were deposited on glass substrates by sol-gel and dip coating methods, using zinc acetate as a zinc precursor, copper acetate and copper chloride as precursors for doping. For higher sensitivity values, two film thickness values are controlled by the six and eight dippings, whereas for doping, three dippings were used, irrespective of the Cu precursor. The film structure was analyzed by X-ray diffractometry, and the analysis of the surface morphology and film composition was made through scanning electron microscopy (SEM) and secondary ion mass spectroscopy (SIMS), respectively. The sensing properties of Cu-doped ZnO thin films were then characterized in a propane atmosphere, C₃H₈, at different concentration levels and different operation temperatures of 100, 200 and 300 °C. Cu-doped ZnO films doped with copper chloride presented the highest sensitivity of approximately 6 × 10⁴, confirming a strong dependence on the dopant precursor type. The results obtained in this work show that the use of Cu as a dopant in ZnO films processed by sol-gel produces excellent catalysts for sensing C₃H₈ gas.

Studies of Niobium Thin Film Produced by Energetic Vacuum Deposition

DOE Office of Scientific and Technical Information (OSTI.GOV)

Genfa Wu; Anne-Marie Valente; H. Phillips

2004-05-01

An energetic vacuum deposition system has been used to study deposition energy effects on the properties of niobium thin films on copper and sapphire substrates. The absence of working gas avoids the gaseous inclusions commonly seen with sputtering deposition. A biased substrate holder controls the deposition energy. Transition temperature and residual resistivity ratio of the niobium thin films at several deposition energies are obtained together with surface morphology and crystal orientation measurements by AFM inspection, XRD and TEM analysis. The results show that niobium thin films on sapphire substrate exhibit the best cryogenic properties at deposition energy around 123 eV.more » The TEM analysis revealed that epitaxial growth of film was evident when deposition energy reaches 163 eV for sapphire substrate. Similarly, niobium thin film on copper substrate shows that film grows more oriented with higher deposition energy and grain size reaches the scale of the film thickness at the deposition energy around 153 eV.« less

An Innovative Method for Manufacturing Gamma-TiAl Foil

NASA Technical Reports Server (NTRS)

Hales, Stephen J.; Saqib, Mohammad; Alexa, Joel A.

2003-01-01

The manufacture and entrance into service of thin gage gamma-TiAl product has been hampered by the inherent low room temperature ductility of the material. In the present study a new approach was explored for the efficient manufacture of gamma-TiAl foil with improved ductility. The objective was to produce a very clean material (low interstitial content) with a highly refined, homogeneous microstructure placed in a fully lamellar condition. The processing route involved the use of RF plasma spray deposition of pre-alloyed powders, followed by consolidation via vacuum hot pressing and heat treatment. The approach took advantage of a deposition process which included no electrodes, no binders and high cooling rates. Results and discussion of the work performed to date are presented.

Highly stretchable miniature strain sensor for large dynamic strain measurement

DOE PAGES

Song, Bo; Yao, Shurong; Nie, Xu; ...

2016-01-01

In this paper, a new type of highly stretchable strain sensor was developed to measure large strains. The sensor was based on the piezo-resistive response of carbon nanotube (CNT)/polydimethylsiloxane (PDMS) composite thin films. The piezo-resistive response of CNT composite gives accurate strain measurement with high frequency response, while the ultra-soft PDMS matrix provides high flexibility and ductility for large strain measurement. Experimental results show that the CNT/PDMS sensor measures large strains (up to 8 %) with an excellent linearity and a fast frequency response. The new miniature strain sensor also exhibits much higher sensitivities than the conventional foil strain gages,more » as its gauge factor is 500 times of that of the conventional foil strain gages.« less

Work function measurements of copper nanoparticle intercalated polyaniline nanocomposite thin films

NASA Astrophysics Data System (ADS)

Patil, U. V.; Ramgir, Niranjan S.; Bhogale, A.; Debnath, A. K.; Muthe, K. P.; Gadkari, S. C.; Kothari, D. C.

2017-05-01

The nature of contact between the electrode and the sensing material plays a crucial role in governing the sensing mechanism. Thin films of polyaniline (PANI) and copper-polyaniline nanocomposite (NC) have been deposited at room temperatures by in-situ oxidative polymerization of aniline in the presence of Cu nanoparticles. For sensing applications a thin film Au (gold) ˜100 nm is deposited and used as a conducting electrode. To understand the nature of contact (i.e., ohmic or Schottky) the work function of the conducting polyaniline and nanocomposite films were measured using Kelvin Probe method. I-V characteristics of PANI and NC films investigated at room temperatures further corroborates and confirms the formation of Ohmic contact as evident from work function measurements.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Laskowski, Lukasz, E-mail: lukasz.laskowski@kik.pcz.pl; Laskowska, Magdalena, E-mail: magdalena.laskowska@onet.pl; Jelonkiewicz, Jerzy, E-mail: jerzy.jelonkiewicz@kik.pcz.pl

The SBA-15 silica thin films containing copper ions anchored inside channels via propyl phosphonate groups are investigated. Such materials were prepared in the form of thin films, with hexagonally arranged pores, laying rectilinear to the substrate surface. However, in the case of our thin films, their free standing form allowed for additional research possibilities, that are not obtainable for typical thin films on a substrate. The structural properties of the samples were investigated by X-ray reflectometry, atomic force microscopy (AFM) and transmission electron microscopy (TEM). The molecular structure was examined by Raman spectroscopy supported by numerical simulations. Magnetic measurements (SQUIDmore » magnetometry and EPR spectroscopy) showed weak antiferromagnetic interactions between active units inside silica channels. Consequently, the pores arrangement was determined and the process of copper ions anchoring by propyl phosphonate groups was verified in unambiguous way. Moreover, the type of interactions between magnetic atoms was determined. - Highlights: • Functionalized free-standing SBA-15 thin films were synthesized for a first time. • Thin films synthesis procedure was described in details. • Structural properties of the films were thoroughly investigated and presented. • Magnetic properties of the novel material was investigated and presented.« less

An electron-microscope study of alpha to gamma transformation in an iron-nickel alloy

NASA Technical Reports Server (NTRS)

Lobodyuk, V. A.; Khandros, L. G.; Fedas, N. P.

1980-01-01

Procedures used to study the alpha to gamma conversion in thin foils of an iron alloy with 32% nickel concentration and initial martensite conversion temperature of -60 C are described. Photomicrographs show deformation twinning as well as changes in samples after they were heated. Reverse conversion is discussed and results are examined.

IMM Solar Cell Shows Its Versatility - Continuum Magazine | NREL

Science.gov Websites

. Inventing a new type of solar cell is one thing. Setting efficiency records with it and winning major awards add to the achievement. But when one of the world's leading manufacturers of compound semiconductor thin metal foil, and the substrate that the cell was grown on is removed. One advantage of this

Basic Operating Mode | Materials Science | NREL

Science.gov Websites

indium diselenide thin film, showing elemental maps of copper (left) and indium (right). CuInSe2 thin film. Cu and In elemental maps obtained by EDS. In its basic operating mode, scanning electron

Liquid precursor for deposition of copper selenide and method of preparing the same

DOEpatents

Curtis, Calvin J.; Miedaner, Alexander; Franciscus Antonius Maria Van Hest, Marinus; Ginley, David S.; Hersh, Peter A.; Eldada, Louay; Stanbery, Billy J.

2015-09-08

Liquid precursors containing copper and selenium suitable for deposition on a substrate to form thin films suitable for semiconductor applications are disclosed. Methods of preparing such liquid precursors and methods of depositing a precursor on a substrate are also disclosed.

SEM and AFM studies of dip-coated CuO nanofilms.

PubMed

Dhanasekaran, V; Mahalingam, T; Ganesan, V

2013-01-01

Cupric oxide (CuO) semiconducting thin films were prepared at various copper sulfate concentrations by dip coating. The copper sulfate concentration was varied to yield films of thicknesses in the range of 445-685 nm by surface profilometer. X-ray diffraction patterns revealed that the deposited films were polycrystalline in nature with monoclinic structure of (-111) plane. The surface morphology and topography of monoclinic-phase CuO thin films were examined using scanning electron microscopy (SEM) and atomic force microscopy (AFM), respectively. Surface roughness profile was plotted using WSxM software and the estimated surface roughness was about ∼19.4 nm at 30 mM molar concentration. The nanosheets shaped grains were observed by SEM and AFM studies. The stoichiometric compound formation was observed at 30 mM copper sulfate concentration prepared film by EDX. The indirect band gap energy of CuO films was increased from 1.08 to 1.20 eV with the increase of copper sulfate concentrations. Copyright © 2012 Wiley Periodicals, Inc.

Alternative designs for space x-ray telescopes

NASA Astrophysics Data System (ADS)

Hudec, R.; Pína, L.; Maršíková, Veronika; Černá, Daniela; Inneman, A.; Tichý, V.

2017-11-01

The X-ray optics is a key element of space X-ray telescopes, as well as other X-ray imaging instruments. The grazing incidence X-ray lenses represent the important class of X-ray optics. Most of grazing incidence (reflective) X-ray imaging systems used in astronomy but also in other (laboratory) applications are based on the Wolter 1 (or modified) arrangement. But there are also other designs and configurations proposed, used and considered for future applications both in space and in laboratory. The Kirkpatrick-Baez (K-B) lenses as well as various types of Lobster-Eye optics and MCP/Micropore optics serve as an example. Analogously to Wolter lenses, the X-rays are mostly reflected twice in these systems to create focal images. Various future projects in X-ray astronomy and astrophysics will require large segments with multiple thin shells or foils. The large Kirkpatrick-Baez modules, as well as the large Lobster-Eye X-ray telescope modules in Schmidt arrangement may serve as examples. All related space projects will require high quality and light segmented shells (bent or flat foils) with high X-ray reflectivity and excellent mechanical stability. The Multi Foil Optics (MFO) approach represent a promising alternative for both LE and K-B X-ray optical modules. Several types of reflecting substrates may be considered for these applications, with emphasis on thin float glass sheets and, more recently, high quality silicon wafers. This confirms the importance of non-Wolter X-ray optics designs for the future. The alternative designs require novel reflective substrates which are also discussed in the paper.

An integration machine for the assembly of the x-ray optic units based on thin slumped glass foils for the IXO mission

NASA Astrophysics Data System (ADS)

Civitani, M. M.; Basso, S.; Bavdaz, M.; Citterio, O.; Conconi, P.; Gallieni, D.; Ghigo, M.; Martelli, F.; Pareschi, G.; Parodi, G.; Proserpio, L.; Sironi, G.; Spiga, D.; Tagliaferri, G.; Tintori, M.; Wille, E.; Zambra, A.

2011-09-01

The International X-ray Observatory (IXO) is a joint mission concept studied by the ESA, NASA, and JAXA space agencies. The main goal of the mission design is to achieve a large effective area (>2.5m2 at 1 keV) and a good angular resolution (5 arcsec HEW at 1 keV) at the same time. The Brera Astronomical Observatory - INAF, Italy), under the support of ESA, is developing a method for the realization of the X-Ray Optical Units, based on the use of slumped thin glass segments to form densely packed modules in a Wolter type I optical configuration. In order to reach the very challenging integration requirements, it has been developed an innovative assembly approach for aligning and mounting the IXO mirror segments. The method is based on the use of an integration mould for each foil. In particular the glass segment is forced to adhere to the integration mould in order to maintain the optimal figure without deformations until the integration of the foil in the stack is completed. In this way an active correction for major existing figure errors after slumping is also achieved. Moreover reinforcing ribs are used in order to connect the facets to each-other and to realize a robust monolithic stack of plates. In this paper we present the design, the development and the validation status of a special Integration Machine (IMA) that has been specifically developed to allow the integration of the Plate Pairs into prototypal X-Ray Optical Unit stacks.

Design of 95 GHz gyrotron based on continuous operation copper solenoid with water cooling

DOE Office of Scientific and Technical Information (OSTI.GOV)

Borodin, Dmitri; Ben-Moshe, Roey; Einat, Moshe

2014-07-15

The design work for 2nd harmonic 95 GHz, 50 kW gyrotron based on continuous operation copper solenoid is presented. Thermionic magnetron injection gun specifications were calculated according to the linear trade off equation, and simulated with CST program. Numerical code is used for cavity design using the non-uniform string equation as well as particle motion in the “cold” cavity field. The mode TE02 with low Ohmic losses in the cavity walls was chosen as the operating mode. The Solenoid is designed to induce magnetic field of 1.8 T over a length of 40 mm in the interaction region with homogeneitymore » of ±0.34%. The solenoid has six concentric cylindrical segments (and two correction segments) of copper foil windings separated by water channels for cooling. The predicted temperature in continuous operation is below 93 °C. The parameters of the design together with simulation results of the electromagnetic cavity field, magnetic field, electron trajectories, and thermal analyses are presented.« less

SU-C-207-06: In Vivo Quantification of Gold Nanoparticles Using K-Edge Imaging Via Spectrum Shaping by Gold Filter

DOE Office of Scientific and Technical Information (OSTI.GOV)

Chen, H; Cormack, R; Bhagwat, M

Purpose: Gold nanoparticles (AuNP) are multifunctional platforms ideal for drug delivery, targeted imaging and radiosensitization. We have investigated quantitative imaging of AuNPs using on board imager (OBI) cone beam computed tomography (CBCT). To this end, we also present, for the first time, a novel method for k-edge imaging of AuNP by filter-based spectral shaping. Methods: We used a digital 25 cm diameter water phantom, embedded with 3 cm spheres filled with AuNPs of different concentrations (0 mg/ml – 16 mg/ml). A poly-energetic X-ray spectrum of 140 kVp from a conventional X-ray tube is shaped by balanced K-edge filters to createmore » an excess of photons right above the K-edge of gold at 80.7 keV. The filters consist of gold, tin, copper and aluminum foils. The phantom with appropriately assigned attenuation coefficients is forward projected onto a detector for each energy bin and then integrated. FKD reconstruction is performed on the integrated projections. Scatter, detector efficiency and noise are included. Results: We found that subtracting the results of two filter sets (Filter A:127 µm gold foil with 254 µm tin, 330 µm copper and 1 mm aluminum, and Filter B: 635 µm tin with 264 µm copper and 1 mm aluminum), provides substantial image contrast. The resulting filtered spectra match well below 80.7 keV, while maintaining sufficient X-ray quanta just above that. Voxel intensities of AuNP containing spheres increase linearly with AuNP concentration. K-edge imaging provides 18% more sensitivity than the tin filter alone, and 38% more sensitivity than the gold filter alone. Conclusion: We have shown that it is feasible to quantitatively detect AuNP distributions in a patient-sized phantom using clinical CBCT and K-edge spectral shaping.« less

SU-E-T-474: Improvements to Intra-Oral Shield Design for Electron Beam Treatments: Use of Multi-Layered Metal Foils

DOE Office of Scientific and Technical Information (OSTI.GOV)

Butson, M

Purpose: Intraoral electron shields used in radiotherapy are designed to minimize radiation exposure to non-treatment tissue. Sites where shields are used include but are not limited to, the treatment of lips, cheeks and ears whilst shielding the underlying oral cavity, tongue, gingival or temporal region. However their use produces an enhancement in dose on the beam side caused by an increase in electron backscatter radiation. This work designs a new shield incorporating copper, aluminium and wax in a step down filter arrangement to minimise backscatter whilst minimizing overall shield thickness. Methods: For electron beams ranging from 6 MeV to 10more » MeV, shields of varying designs and thicknesses were assessed to determine the thinnest shield design that could be produced whilst minimising backscattered radiation to a clinically acceptable level. This was performed with conventional lead and wax shields as well as varying quantities of aluminium and copper foils. Results: From tested shield designs, a new shield design of 4 mm lead, 0.6 mm copper, 1.0 mm aluminium and 1.5 mm wax (3.1 mm added filtration, 7.1 mm total thickness) provided a clinically acceptable (no greater than 110% dose) backscatter and transmission reduction and matched a standard 4.5 mm lead and 10 mm wax (total thickness 14.5 mm) electron shield. Dose enhancement values of no more than 10 % were measured utilising this shield design with a 50 % reduction in shield thickness. Conclusion: The thinner layered shield reduced backscattered radiation dose to less than 10% enhancement for beam energies on 10 MeV and less and will allow easier patient set up. The thinner shields are tolerated better by patients when mucosal reactions occur as they place less physical pressure on these sites during treatment due to their smaller size and thickness.« less

Femtosecond to nanosecond excited state dynamics of vapor deposited copper phthalocyanine thin films.

PubMed

Caplins, Benjamin W; Mullenbach, Tyler K; Holmes, Russell J; Blank, David A

2016-04-28

Vapor deposited thin films of copper phthalocyanine (CuPc) were investigated using transient absorption spectroscopy. Exciton-exciton annihilation dominated the kinetics at high exciton densities. When annihilation was minimized, the observed lifetime was measured to be 8.6 ± 0.6 ns, which is over an order of magnitude longer than previous reports. In comparison with metal free phthalocyanine (H2Pc), the data show evidence that the presence of copper induces an ultrafast relaxation process taking place on the ca. 500 fs timescale. By comparison to recent time-resolved photoemission studies, this is assigned as ultrafast intersystem crossing. As the intersystem crossing occurs ca. 10(4) times faster than lifetime decay, it is likely that triplets are the dominant excitons in vapor deposited CuPc films. The exciton lifetime of CuPc thin films is ca. 35 times longer than H2Pc thin films, while the diffusion lengths reported in the literature are typically quite similar for the two materials. These findings suggest that despite appearing to be similar materials at first glance, CuPc and H2Pc may transport energy in dramatically different ways. This has important implications on the design and mechanistic understanding of devices where phthalocyanines are used as an excitonic material.

Simulated Thin-Film Growth and Imaging

NASA Astrophysics Data System (ADS)

Schillaci, Michael

2001-06-01

Thin-films have become the cornerstone of the electronics, telecommunications, and broadband markets. A list of potential products includes: computer boards and chips, satellites, cell phones, fuel cells, superconductors, flat panel displays, optical waveguides, building and automotive windows, food and beverage plastic containers, metal foils, pipe plating, vision ware, manufacturing equipment and turbine engines. For all of these reasons a basic understanding of the physical processes involved in both growing and imaging thin-films can provide a wonderful research project for advanced undergraduate and first-year graduate students. After producing rudimentary two- and three-dimensional thin-film models incorporating ballsitic deposition and nearest neighbor Coulomb-type interactions, the QM tunneling equations are used to produce simulated scanning tunneling microscope (SSTM) images of the films. A discussion of computational platforms, languages, and software packages that may be used to accomplish similar results is also given.

Spatially and temporally resolved measurements of a dense copper plasma heated by intense relativistic electrons

NASA Astrophysics Data System (ADS)

Coleman, J. E.; Colgan, J.

2017-08-01

A 100-μm-thick Cu foil is isochorically heated by a ˜100-ns-long electron bunch with an energy of 19.8 MeV and current of 1.7 kA to Te > 1 eV. After 100 ns of heating and 20 ns of expansion, the plasma exhibits a stable, quiescent temperature and density distribution for >200 ns. Several intense Cu-I emission lines are observed after ˜20 J of electron beam energy is deposited. These lines have well known Stark widths providing a direct measurement of ne. The Los Alamos ATOMIC code [Magee et al., AIP Conf. Proc. 2004, 168-179 and Hakel et al., J. Quant. Spectrosc. Radiat. Transfer 99, 265 (2006)] was run in local-thermodynamic-equilibrium mode to estimate Te and ne. Spatially and temporally resolved measurements are presented in both the vertical and horizontal directions adjacent to the foil indicating temperatures >1 eV and densities ranging from 1-3 × 1017 cm-3 after expansion and cooling.

Ultra-Flexible Thermal Bus for Use in the Astro-H Adiabatic Demagnetization Refrigerator

NASA Technical Reports Server (NTRS)

Kimball, Mark O.; Shirron, Peter J.

2015-01-01

The adiabatic demagnetization refrigerator (ADR) developed for the Astro-H Soft-X-ray Spectrometer (SXS) is a multi-stage solid-state cooler. It is capable of holding the SXS detector array at 0.050 K for greater than 24 hours with a recycle time of less than one hour. This quick recycle time relies upon high-conductivity thermal straps to couple the individual stages to a pair of heat switches without imposing a lateral load on the paramagnetic salt pills. To accomplish this we construct thermal straps using a technique of diffusion bonding together the ends of high-purity copper straps leaving the length between as individual foils. A thermal bus created this way has a thermal conductivity comparable to a solid strap of the equivalent thickness but with much-increased flexibility. The technique for selecting the base material, machining, cleaning, forming into final shape, and finally bonding together individual foils will be discussed along with examples of complete straps in various geometries.

Synthesis, Optical and Photoluminescence Properties of Cu-Doped Zno Nano-Fibers Thin Films: Nonlinear Optics

NASA Astrophysics Data System (ADS)

Ganesh, V.; Salem, G. F.; Yahia, I. S.; Yakuphanoglu, F.

2018-03-01

Different concentrations of copper-doped zinc oxide thin films were coated on a glass substrate by sol-gel/spin-coating technique. The structural properties of pure and Cu-doped ZnO films were characterized by different techniques, i.e., atomic force microscopy (AFM), photoluminescence and UV-Vis-NIR spectroscopy. The AFM study revealed that pure and doped ZnO films are formed as nano-fibers with a granular structure. The photoluminescence spectra of these films showed a strong ultraviolet emission peak centered at 392 nm and a strong blue emission peak cantered at 450 nm. The optical band gap of the pure and copper-doped ZnO thin films calculated from optical transmission spectra (3.29-3.23 eV) were found to be increasing with increasing copper doping concentration. The refractive index dispersion curve of pure and Cu-doped ZnO film obeyed the single-oscillator model. The optical dispersion parameters such as E o , E d , and n_{∞}2 were calculated. Further, the nonlinear refractive index and nonlinear optical susceptibility were also calculated and interpreted.

Thin film filter lifetesting results in the extreme ultraviolet

NASA Technical Reports Server (NTRS)

Vedder, P. W.; Vallerga, J. V.; Gibson, J. L.; Stock, J.; Siegmund, O. H. W.

1993-01-01

We present the results of the thin film filter lifetesting program conducted as part of the NASA Extreme Ultraviolet Explorer (EUVE) satellite mission. This lifetesting program is designed to monitor changes in the transmission and mechanical properties of the EUVE filters over the lifetime of the mission (fabrication, assembly, launch and operation). Witness test filters were fabricated from thin film foils identical to those used in the flight filters. The witness filters have been examined and calibrated periodically over the past seven years. The filters have been examined for evidence of pinholing, mechanical degradation, and oxidation. Absolute transmissions of the flight and witness filters have been measured in the extreme ultraviolet (EUV) over six orders of magnitude at numerous wavelengths using the Berkeley EUV Calibration Facility.

Reduction of angular divergence of laser-driven ion beams during their acceleration and transport

NASA Astrophysics Data System (ADS)

Zakova, M.; Pšikal, Jan; Margarone, Daniele; Maggiore, Mario; Korn, G.

2015-05-01

Laser plasma physics is a field of big interest because of its implications in basic science, fast ignition, medicine (i.e. hadrontherapy), astrophysics, material science, particle acceleration etc. 100-MeV class protons accelerated from the interaction of a short laser pulse with a thin target have been demonstrated. With continuing development of laser technology, greater and greater energies are expected, therefore projects focusing on various applications are being formed, e.g. ELIMAIA (ELI Multidisciplinary Applications of laser-Ion Acceleration). One of the main characteristic and crucial disadvantage of ion beams accelerated by ultra-short intense laser pulses is their large divergence, not suitable for the most of applications. In this paper two ways how to decrease beam divergence are proposed. Firstly, impact of different design of targets on beam divergence is studied by using 2D Particlein-cell simulations (PIC). Namely, various types of targets include at foils, curved foil and foils with diverse microstructures. Obtained results show that well-designed microstructures, i.e. a hole in the center of the target, can produce proton beam with the lowest divergence. Moreover, the particle beam accelerated from a curved foil has lower divergence compared to the beam from a flat foil. Secondly, another proposed method for the divergence reduction is using of a magnetic solenoid. The trajectories of the laser accelerated particles passing through the solenoid are modeled in a simple Matlab program. Results from PIC simulations are used as input in the program. The divergence is controlled by optimizing the magnetic field inside the solenoid and installing an aperture in front of the device.

Shock Wave Based Biolistic Device for DNA and Drug Delivery

NASA Astrophysics Data System (ADS)

Nakada, Mutsumi; Menezes, Viren; Kanno, Akira; Hosseini, S. Hamid R.; Takayama, Kazuyoshi

2008-03-01

A shock wave assisted biolistic (biological ballistic) device has been developed to deliver DNA/drug-coated micro-projectiles into soft living targets. The device consists of an Nd:YAG laser, an optical setup to focus the laser beam and, a thin aluminum (Al) foil (typically 100 µm thick) which is a launch pad for the micro-projectiles. The DNA/drug-coated micro-particles to be delivered are deposited on the anterior surface of the foil and the posterior surface of the foil is ablated using the laser beam with an energy density of about 32×109 W/cm2. The ablation launches a shock wave through the foil that imparts an impulse to the foil surface, due to which the deposited particles accelerate and acquire sufficient momentum to penetrate soft targets. The device has been tested for particle delivery by delivering 1 µm size tungsten particles into liver tissues of experimental rats and in vitro test models made of gelatin. The penetration depths of about 90 and 800 µm have been observed in the liver and gelatin targets, respectively. The device has been tested for in vivo DNA [encoding β-glucuronidase (GUS) gene] transfer by delivering plasmid DNA-coated, 1-µm size gold (Au) particles into onion scale, tobacco leaf and soybean seed cells. The GUS activity was detected in the onion, tobacco and soybean cells after the DNA delivery. The present device is totally non-intrusive in nature and has a potential to get miniaturized to suit the existing medical procedures for DNA and/or drug delivery.

Electro deposition of cuprous oxide for thin film solar cell applications

NASA Astrophysics Data System (ADS)

Shahrestani, Seyed Mohammad

p and n type copper oxide semiconductor layers were fabricated by electrochemistry using new approaches for photovoltaic applications. Thin films were electroplated by cathodic polarization on a copper foil or indium tin oxide (ITO) substrates. The optimum deposition conditions (composition, pH and temperature of the electrolyte and applied potential) of the layers as thin films have been identified; in particular the conditions that allow getting the n-type layers have been well identified for the first time. The configuration of a photo - electrochemical cell was used to characterize the spectral response of the layers. It was shown that the p type layers exhibit a photocurrent in the cathode potential region and n layers exhibit photo current in the anode potential region. Measurements of electrical resistivity of electro chemically deposited layers of p and n type Cu2O, showed that the resistivity of p-type Cu2O varies from 3.2 x 105 to 2.0 x 108 Ocm. These values depend the electrodepositing conditions such as the pH of the solution, the deposition potential and temperature. The influence of several plating parameters of the p type layers of Cu2O, such as applied potential, pH and temperature of the bath on the chemical composition, degree of crystallinity, grain size and orientation parameters of the sample was systematically studied using X-ray diffraction and scanning electron microscopy. Depending of the electro-deposition potential, two different surface morphologies with various preferential crystal orientations were obtained for the temperatures of the electro-deposition of 30 °C and pH 9. For the same temperature, the layers of p type Cu2O of highly crystalline p type are obtained at pH 12, indicating that the crystallinity depends on the pH of the bath. Also, it has been shown that the morphology of Cu2O layers was changed by varying the potential and the duration of deposition, as well as the temperature of the solution. The conditions for the electro-deposition of Cu2O n-type were identified consistently for the first time. The electro-deposition electrolyte is based 0.01M acetate copper and 0.1 M sodium acetate: it has a pH between 6.3 and 4, a potential of from 0 to -0.25 V vs. Ag / AgCl and a temperature of 60oC. The optimum annealing temperature of the n-type Cu2O layers is between 120-150oC for the annealing time of 30 to 120 minutes. Resistivity of the n-type films varies between 5 x 103 and 5 x 104 at pH 4 to pH 6.4. We have shown for the first time that bubbling nitrogen gas in the electroplating cell improves significantly the spectral response of the electro-deposited n-type thin film. A two steps electro-deposition process was implemented to make the p-n homojunction cuprous oxide. Indium tin oxide (ITO) was used as a transparent conductive oxide substrate. A p-Cu2O was electrodeposited on ITO. After heat treatment a thin film layer of n-Cu 2O was electrodeposited on top of previous layer. The performance of a p-n homojunction photovoltaic solar cell of Cu2O was determined. The short-circuit current and the open circuit voltage were respectively determined to be as 0.35 volts and 235 muA/cm2. The fill factor (FF) and conversion efficiency of light into electricity were respectively measured to be 0.305 and 0.082%.

SMA Foils for MEMS: From Material Properties to the Engineering of Microdevices

NASA Astrophysics Data System (ADS)

Kohl, Manfred; Ossmer, Hinnerk; Gueltig, Marcel; Megnin, Christof

2018-03-01

In the early nineties, microelectromechanical systems (MEMS) technology has been still in its infancy. As silicon (Si) is not a transducer material, it was clear at the very beginning that mechanically active materials had to be introduced to MEMS in order to enable functional microdevices with actuation capability beyond electrostatics. At that time, shape memory alloys (SMAs) have been available in bulk form, mainly as SMA wires and SMA plates. On the macro scale, these materials show highest work densities compared to other actuation principles in the order of 107 J/m3, which stimulated research on the integration of SMA to MEMS. Subsequently, two approaches for producing planar materials have been initiated (1) magnetron sputtering of SMA thin films and (2) the integration of rolled SMA foils, which both turned out to be very successful creating a paradigm change in microactuation technology. The following review covers important milestones of the research and development of SMA foil-based microactuators including materials characterization, design engineering, technology, and demonstrator development as well as first commercial products.

Measuring Submicron-Sized Fractionated Particulate Matter on Aluminum Impactor Disks

PubMed Central

Buchholz, Bruce A.; Zermeño, Paula; Hwang, Hyun-Min; Young, Thomas M.; Guilderson, Thomas P.

2011-01-01

Sub-micron sized airborne particulate matter (PM) is not collected well on regular quartz or glass fiber filter papers. We used a micro-orifice uniform deposit impactor (MOUDI) to fractionate PM into six size fractions and deposit it on specially designed high purity thin aluminum disks. The MOUDI separated PM into fractions 56–100 nm, 100–180 nm, 180–320 nm, 320–560 nm, 560–1000 nm, and 1000–1800 nm. Since the MOUDI has a low flow rate (30 L/min), it takes several days to collect sufficient carbon on 47 mm foil disks. The small carbon mass (20–200 microgram C) and large aluminum substrate (~25 mg Al) present several challenges to production of graphite targets for accelerator mass spectrometry (AMS) analysis. The Al foil consumes large amounts of oxygen as it is heated and tends to melt into quartz combustion tubes, causing gas leaks. We describe sample processing techniques to reliably produce graphitic targets for 14C-AMS analysis of PM deposited on Al impact foils. PMID:22228915

SMA Foils for MEMS: From Material Properties to the Engineering of Microdevices

NASA Astrophysics Data System (ADS)

Kohl, Manfred; Ossmer, Hinnerk; Gueltig, Marcel; Megnin, Christof

2017-12-01

In the early nineties, microelectromechanical systems (MEMS) technology has been still in its infancy. As silicon (Si) is not a transducer material, it was clear at the very beginning that mechanically active materials had to be introduced to MEMS in order to enable functional microdevices with actuation capability beyond electrostatics. At that time, shape memory alloys (SMAs) have been available in bulk form, mainly as SMA wires and SMA plates. On the macro scale, these materials show highest work densities compared to other actuation principles in the order of 107 J/m3, which stimulated research on the integration of SMA to MEMS. Subsequently, two approaches for producing planar materials have been initiated (1) magnetron sputtering of SMA thin films and (2) the integration of rolled SMA foils, which both turned out to be very successful creating a paradigm change in microactuation technology. The following review covers important milestones of the research and development of SMA foil-based microactuators including materials characterization, design engineering, technology, and demonstrator development as well as first commercial products.

Maintaining stable radiation pressure acceleration of ion beams via cascaded electron replenishment

NASA Astrophysics Data System (ADS)

Shen, X. F.; Qiao, B.; Chang, H. X.; Zhang, W. L.; Zhang, H.; Zhou, C. T.; He, X. T.

2017-03-01

A method to maintain ion stable radiation pressure acceleration (RPA) from laser-irradiated thin foils is proposed, where a series of high-Z nanofilms are placed behind to successively replenish co-moving electrons into the accelerating foil as electron charging stations (ECSs). Such replenishment of co-moving electrons, on the one hand, helps to keep a dynamic balance between the electrostatic pressure in the accelerating slab and the increasing laser radiation pressure with a Gaussian temporal profile at the rising front, i.e. dynamically matching the optimal condition of RPA; on the other hand, it aids in suppressing the foil Coulomb explosion due to loss of electrons induced by transverse instabilities during RPA. Two-dimensional and three-dimensional particle-in-cell simulations show that a monoenergetic Si14+ beam with a peak energy of 3.7 GeV and particle number 4.8× {10}9 (charge 11 nC) can be obtained at an intensity of 7 × 1021 W cm-2 and the conversion efficiency from laser to high energy ions is improved significantly by using the ECSs in our scheme.

Effect of copper doping on the photocatalytic activity of ZnO thin films prepared by sol-gel method

NASA Astrophysics Data System (ADS)

Saidani, T.; Zaabat, M.; Aida, M. S.; Boudine, B.

2015-12-01

In the present work, we prepared undoped and copper doped ZnO thin films by the sol-gel dip coating method on glass substrates from zinc acetate dissolved in a solution of ethanol. The objective of our work is to study the effect of Cu doping with different concentrations on structural, morphological, optical properties and photocatalytic activity of ZnO thin films. For this purpose, we have used XRD to study the structural properties, and AFM to determine the morphology of the surface of the ZnO thin films. The optical properties and the photocatalytic degradation of the films were examined by UV-visibles spectrophotometer. The Tauc method was used to estimate the optical band gap. The XRD spectra indicated that the films have an hexagonal wurtzite structure, which gradually deteriorated with increasing Cu concentration. The results showed that the incorporation of Cu decreases the crystallite size. The AFM study showed that an increase of the concentration of Cu causes the decrease of the surface roughness, which passes from 20.2 for Un-doped ZnO to 12.16 nm for doped ZnO 5 wt% Cu. Optical measurements have shown that all the deposited films show good optical transmittance (77%-92%) in the visible region and increases the optical gap with increasing Cu concentration. The presence of copper from 1% to 5 wt% in the ZnO thin films is found to decelerate the photocatalytic process.

Graphene decorated microelectrodes for simultaneous detection of ascorbic, dopamine, and folic acids by means of chemical vapor deposition

NASA Astrophysics Data System (ADS)

Namdar, N.; Hassanpour Amiri, M.; Dehghan Nayeri, F.; Gholizadeh, A.; Mohajerzadeh, S.

2015-09-01

In this paper, high quality and large area graphene layers were synthesized using thermal chemical vapour deposition on copper foil substrates. We use graphene incorporated electrodes to measure simultaneously ascorbic acid, dopamine and folic acid. Cyclic voltammetry and differential pulse voltammetry methods were used to evaluate electrochemical behaviour of the grown graphene layers. The graphene-modified electrode shows large electrochemical potential difference compared to bare gold electrodes with higher current responses. Also our fabricated electrodes configuration can be used easily for microfluidic analysis.

Flexible Circuits

NASA Technical Reports Server (NTRS)

1986-01-01

Adflex Solutions, Inc.'s flexible circuits may be molded to the shape of a chassis for bulk reduction. Particularly valuable when circuitry must be moved. They are produced by combining a plastic film, a metallic conductor and an adhesive. One adhesive, LARC-TPI, developed by the Langley Research Center, is a thermoplastic polyimide resin used to produce laminates by Rogers Corporation. It can be processed at a lower temperature, has good moisture resistance and excellent adherence. It is used to bond film to copper foil conductor materials in flexible circuits. The circuits have both aerospace and commercial applications.

Low energy sputtering of cobalt by cesium ions

NASA Technical Reports Server (NTRS)

Handoo, A.; Ray, Pradosh K.

1989-01-01

An experimental facility to investigate low energy (less than 500 eV) sputtering of metal surfaces with ions produced by an ion gun is described. Results are reported on the sputtering yield of cobalt by cesium ions in the 100 to 500 eV energy range at a pressure of 1 times 10(exp -6) Torr. The target was electroplated on a copper substrate. The sputtered atoms were collected on a cobalt foil surrounding the target. Co-57 was used as a tracer to determine the sputtering yield.

Soldering Technology (4th) Proceedings of Annual Seminar, 20-21 February 1980.

DTIC Science & Technology

1980-02-01

from the data is the time to reach a certain predefined stage in the wetting process. ’Me test is more general than many in that it allows testing of...trace to cross the zero force axis and this was the endpoint used for all Me.scograph wetting time results reportea in this paper. For copper foil...measured on the Surface Tension Balance as the slope of the crace at the zero force axis, shows a fairly large range for each value but still

Note: Arc discharge plasma source with plane segmented LaB{sub 6} cathode

DOE Office of Scientific and Technical Information (OSTI.GOV)

Akhmetov, T. D., E-mail: t.d.akhmetov@inp.nsk.su; Davydenko, V. I.; Ivanov, A. A.

2016-05-15

A plane cathode composed of close-packed hexagonal LaB{sub 6} (lanthanum hexaboride) segments is described. The 6 cm diameter circular cathode is heated by radiation from a graphite foil flat spiral. The cathode along with a hollow copper anode is used for the arc discharge plasma production in a newly developed linear plasma device. A separately powered coil located around the anode is used to change the magnetic field strength and geometry in the anode region. Different discharge regimes were realized using this coil.

TERS v2.0: An improved version of TERS

NASA Astrophysics Data System (ADS)

Nath, S.

2009-11-01

We present a new version of the semimicroscopic Monte Carlo code "TERS". The procedure for calculating multiple small angle Coulomb scattering of the residues in the target has been modified. Target-backing and residue charge-reset foils, which are often used in heavy ion-induced complete fusion reactions, are included in the code. New version program summaryProgram title: TERS v2.0 Catalogue identifier: AEBD_v2_0 Program summary URL:http://cpc.cs.qub.ac.uk/summaries/AEBD_v2_0.html Program obtainable from: CPC Program Library, Queen's University, Belfast, N. Ireland Licensing provisions: Standard CPC licence, http://cpc.cs.qub.ac.uk/licence/licence.html No. of lines in distributed program, including test data, etc.: 7309 No. of bytes in distributed program, including test data, etc.: 1 219 555 Distribution format: tar.gz Programming language: C Computer: The code has been developed and tested on a PC with Intel Pentium IV processor. Operating system: Linux RAM: About 8 Mbytes Classification: 17.7 External routines: pgplot graphics subroutine library [1] should be installed in the system for generating residue trajectory plots. (The library is included in the CPC distribution file.) Catalogue identifier of previous version: AEBD_v1_0 Journal reference of previous version: Comput. Phys. Comm. 179 (2008) 492 Does the new version supersede the previous version?: Yes Nature of problem: Recoil separators are employed to select and identify nuclei of interest, produced in a nuclear reaction, rejecting unreacted beam and other undesired reaction products. It is important to know what fraction of the selected nuclei, leaving the target, reach the detection system. This information is crucial for determining absolute cross section of the studied reaction. Solution method: Interaction of projectiles with target nuclei is treated event by event, semimicro-scopically. Position and angle (with respect to beam direction), energy and charge state of the reaction products are calculated by Monte Carlo method. Trajectory of each nuclei inside the separator is then calculated by ion optical transfer matrix method. Ratio of the number of trajectories completing their journey up to the detection system to the total number of trajectories is a direct measure of absolute transmission efficiency of the separator. Reasons for new version: The method for calculating mean squared scattering angle (< ϑ > 2), used earlier [2], was found to be inadequate particularly for low energy heavy residues. Energy loss of beam in the target-backing foil and energy loss of residues in the charge-reset foil (wherever used) needed to be taken into account for better matching of simulated residue parameters with measurements. Summary of revisions: A new method [3] for calculating multiple small angle Coulomb scattering of residues in the target has been adopted. The change is incorporated in function Weibull() in the program ters_pti2.c. Isotopically enriched targets are made on a thin backing foil (usually made of carbon) quite often. Energy loss of beam in the backing foil (assuming beam is made to pass through the backing foil first, which is the usual practice) need to be taken into account. This calls for minor changes in the input file ters_pti2.inp. Following is the modified list of input parameters in this file with explanation. Atomic no. and mass no. of projectile and target. Projectile energy [MeV] in laboratory. Dia. [mm] of (circular) beam spot and target thickness [mg/cm2]. Atomic no. and mass no. of the backing material and thickness [mg/cm2] of the backing foil. Q value [MeV] for CN formation and inverse level density parameter. Numbers of evaporated alphas, protons and neutrons. Alpha separation energies [MeV], to be left blank if no alpha evaporation. Proton separation energies [MeV], to be left blank if no proton evaporation. Neutron separation energies [MeV], to be left blank if no neutron evaporation. Number of events i.e. residues to be considered by the program (maximum 5 ×105). The parameters in input line number 4 are new in this version. If the target is backed by a carbon foil of thickness 125 μg/cm2, the input line would look like "6 12 0.125". If the target is self-supporting, i.e. there is no backing, value of the last parameter (thickness) should be zero. However, the first two parameters must not be left blank or have 0 values. The input line would look like "6 12 0.0" in this case. A new function ThinFoil() has been introduced in the program ters_tra2.c. A thin foil can be inserted anywhere along the path of the residues by calling this function using the following syntax: Status = ThinFoil(argument list); if (Status == 0) continue; The function is particularly useful to place a residue charge-reset foil (usually made of carbon) after the target and is described in Table 1.Name of the functionJob of the functionList of argumentsDescription of argumentsThinFoil()To calculate ion energy loss in a thin foilint arg1, int arg2, int arg3arg1 = atomic number of the foil material, arg2 = mass number of the foil material, arg3 = thickness of the foil [mg/cm2] There is a minor change in the input file ters_tra2.inp. Following is the modified list of input parameters in this file with explanation. Residue atomic number and mass number. Energy [MeV], mass no. and charge state of the reference particle. Number of events i.e. trajectories to be calculated. Program/input files which have been modified in this version are suffixed by "2" in their names (before the extension), e.g., ters_pti.c has been renamed ters_pti2.c. The complete list of files included in the distributed code can be viewed in the readme file. Restrictions: The present version of the code is applicable to complete fusion reactions only. Calculation of transmission efficiency has been illustrated with a specific recoil separator, viz. the Heavy Ion Reaction Analyzer (HIRA) [4,5], at IUAC. One has to make necessary changes in the code, while performing calculations for other recoil separators. Also, atomic number of the residual nucleus should not exceed 92, as the method used for calculating stopping power of ions [6] is valid for Z ⩽ 92. The code can perform energy loss calculation only in elemental targets and foils (i.e. compounds or alloys are not supported). Further, number of events (NEVENT) in ters_tra2.inp should not exceed the same in ters_pti2.inp. Running time: From few seconds to several minutes depending on the reaction, number of events and separator layout. References: [1] http://www.astro.caltech.edu/~tjp/pgplot/. [2] G.R. Lynch, O.I. Dahl, Nucl. Instr. Methods B 58 (1991) 6. [3] L. Meyer, Phys. Status Solidi 44 (1971) 253. [4] A.K. Sinha, N. Madhavan, J.J. Das, P. Sugathan, D.O. Kataria, A.P. Patro, G.K. Mehta, Nucl. Instr. Methods A 339 (1994) 543. [5] S. Nath, Nucl. Instr. Methods A 576 (2007) 403. [6] J.F. Ziegler, J.P. Biersack, U. Littmark, The Stopping and Range of Ions in Solids, vol. I, Pergamon Press, Oxford, 1984.

Film/Adhesive Processing Module for Fiber-Placement Processing of Composites

NASA Technical Reports Server (NTRS)

Hulcher, A. Bruce

2007-01-01

An automated apparatus has been designed and constructed that enables the automated lay-up of composite structures incorporating films, foils, and adhesives during the automated fiber-placement process. This apparatus, denoted a film module, could be used to deposit materials in film or thin sheet form either simultaneously when laying down the fiber composite article or in an independent step.

An efficient and cost-effective method for preparing transmission electron microscopy samples from powders

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wen, Haiming; Lin, Yaojun; Seidman, David N.

The preparation of transmission electron microcopy (TEM) samples from powders with particle sizes larger than ~100 nm poses a challenge. The existing methods are complicated and expensive, or have a low probability of success. Herein, we report a modified methodology for preparation of TEM samples from powders, which is efficient, cost-effective, and easy to perform. This method involves mixing powders with an epoxy on a piece of weighing paper, curing the powder–epoxy mixture to form a bulk material, grinding the bulk to obtain a thin foil, punching TEM discs from the foil, dimpling the discs, and ion milling the dimpledmore » discs to electron transparency. Compared with the well established and robust grinding–dimpling–ion-milling method for TEM sample preparation for bulk materials, our modified approach for preparing TEM samples from powders only requires two additional simple steps. In this article, step-by-step procedures for our methodology are described in detail, and important strategies to ensure success are elucidated. Furthermore, our methodology has been applied successfully for preparing TEM samples with large thin areas and high quality for many different mechanically milled metallic powders.« less

Exploring aligned-carbon-nanotubes@polyaniline arrays on household Al as supercapacitors.

PubMed

Huang, Fan; Lou, Fengliu; Chen, De

2012-05-01

Herein, we demonstrate a new approach towards the construction of supercapacitors consisting of carbon nanotubes (CNTs) and conducting polymers (ECPs) with high specific power, high specific energy, and stable cycling performance through a 3D design of a thin film of polyaniline (PANI) on an aligned small carbon nanotube (ACNT) array on household Al foils. The thin-film strategy is used to fully exploit the specific capacitance of PANI, and obtain regular pores, strong interaction between PANI and CNTs, and reduced electrical resistance for the electrodes. A facile process is developed to fabricate a highly flexible supercapacitor using this binder-free composite on household Al foil as the current collector. It exhibits high specific energy of 18.9 Wh kg(-1) , high maximum specific power of 11.3 kW kg(-1) of the active material in an aqueous electrolyte at 1.0 A g(-1) , and excellent rate performance and cycling stability. A high specific energy of 72.4 Wh kg(-1) , a high maximum specific power of 24.9 kW kg(-1) , and a good cycling performance of the active material are obtained in an organic electrolyte. Copyright © 2012 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

A novel method for computing effective diffusivity: Application to helium implanted α-Fe thin films

NASA Astrophysics Data System (ADS)

Dunn, Aaron; Agudo-Merida, Laura; Martin-Bragado, Ignacio; McPhie, Mathieu; Cherkaoui, Mohammed; Capolungo, Laurent

2014-05-01

The effective diffusivity of helium in thin iron films is quantified using spatially resolved stochastic cluster dynamics and object kinetic Monte Carlo simulations. The roles of total displacement dose (in DPA), damage rate, helium to DPA ratio, layer thickness, and damage type (cascade damage vs Frenkel pair implantation) on effective He diffusivity are investigated. Helium diffusivity is found to decrease with increasing total damage and decreasing damage rate. Arrhenius plots show strongly increased helium diffusivity at high temperatures, high total implantation, and low implantation rates due to decreased vacancy and vacancy cluster concentrations. At low temperatures, effective diffusivity is weakly dependent on foil thickness while at high temperatures, narrower foils prevent defect accumulation by releasing all defects at the free surfaces. Helium to DPA ratio is not shown to strongly change helium diffusivity in the range of irradiation conditions simulated. Frenkel pair implantation is shown to cause higher effective diffusivity and more complex diffusion mechanisms than cascade implantation. The results of these simulations indicate that the differences in damage rates between implantation experiments and fission or fusion environments may result in differences in the final microstructure.

An efficient and cost-effective method for preparing transmission electron microscopy samples from powders

DOE PAGES

Wen, Haiming; Lin, Yaojun; Seidman, David N.; ...

2015-09-09

The preparation of transmission electron microcopy (TEM) samples from powders with particle sizes larger than ~100 nm poses a challenge. The existing methods are complicated and expensive, or have a low probability of success. Herein, we report a modified methodology for preparation of TEM samples from powders, which is efficient, cost-effective, and easy to perform. This method involves mixing powders with an epoxy on a piece of weighing paper, curing the powder–epoxy mixture to form a bulk material, grinding the bulk to obtain a thin foil, punching TEM discs from the foil, dimpling the discs, and ion milling the dimpledmore » discs to electron transparency. Compared with the well established and robust grinding–dimpling–ion-milling method for TEM sample preparation for bulk materials, our modified approach for preparing TEM samples from powders only requires two additional simple steps. In this article, step-by-step procedures for our methodology are described in detail, and important strategies to ensure success are elucidated. Furthermore, our methodology has been applied successfully for preparing TEM samples with large thin areas and high quality for many different mechanically milled metallic powders.« less

Cu-Doped ZnO Thin Films Deposited by a Sol-Gel Process Using Two Copper Precursors: Gas-Sensing Performance in a Propane Atmosphere

PubMed Central

Gómez-Pozos, Heberto; Arredondo, Emma Julia Luna; Maldonado Álvarez, Arturo; Biswal, Rajesh; Kudriavtsev, Yuriy; Pérez, Jaime Vega; Casallas-Moreno, Yenny Lucero; Olvera Amador, María de la Luz

2016-01-01

A study on the propane gas-sensing properties of Cu-doped ZnO thin films is presented in this work. The films were deposited on glass substrates by sol-gel and dip coating methods, using zinc acetate as a zinc precursor, copper acetate and copper chloride as precursors for doping. For higher sensitivity values, two film thickness values are controlled by the six and eight dippings, whereas for doping, three dippings were used, irrespective of the Cu precursor. The film structure was analyzed by X-ray diffractometry, and the analysis of the surface morphology and film composition was made through scanning electron microscopy (SEM) and secondary ion mass spectroscopy (SIMS), respectively. The sensing properties of Cu-doped ZnO thin films were then characterized in a propane atmosphere, C3H8, at different concentration levels and different operation temperatures of 100, 200 and 300 °C. Cu-doped ZnO films doped with copper chloride presented the highest sensitivity of approximately 6 × 104, confirming a strong dependence on the dopant precursor type. The results obtained in this work show that the use of Cu as a dopant in ZnO films processed by sol-gel produces excellent catalysts for sensing C3H8 gas. PMID:28787885

Spontaneous interfacial reaction between metallic copper and PBS to form cupric phosphate nanoflower and its enzyme hybrid with enhanced activity.

PubMed

He, Guangli; Hu, Weihua; Li, Chang Ming

2015-11-01

We herein report the spontaneous interfacial reaction between copper foil with 0.01 M phosphate buffered saline (PBS) to form free-standing cupric phosphate (Cu3(PO4)2) nanoflowers at ambient temperature. The underlying chemistry was thoroughly investigated and it is found that the formation of nanoflower is synergistically caused by dissolved oxygen, chlorine ions and phosphate ions. Enzyme-Cu3(PO4)2 hybrid nanoflower was further prepared successfully by using an enzyme-dissolving PBS solution and the enzymes in the hybrid exhibit enhanced biological activity. This work provides a facile route for large-scale synthesis of hierarchical inorganic and functional protein-inorganic hybrid architectures via a simple one-step solution-immersion reaction without using either template or surfactant, thus offering great potential for biosensing application among others. Copyright © 2015 Elsevier B.V. All rights reserved.

New trends in space x-ray optics

NASA Astrophysics Data System (ADS)

Hudec, R.; Maršíková, V.; Pína, L.; Inneman, A.; Skulinová, M.

2017-11-01

The X-ray optics is a key element of various X-ray telescopes, X-ray microscopes, as well as other X-ray imaging instruments. The grazing incidence X-ray lenses represent the important class of X-ray optics. Most of grazing incidence (reflective) X-ray imaging systems used in astronomy but also in other (laboratory) applications are based on the Wolter 1 (or modified) arrangement. But there are also other designs and configurations proposed, used and considered for future applications both in space and in laboratory. The Kirkpatrick-Baez (K-B) lenses as well as various types of Lobster-Eye optics and MCP/Micropore optics serve as an example. Analogously to Wolter lenses, the X-rays are mostly reflected twice in these systems to create focal images. Various future projects in X-ray astronomy and astrophysics will require large segments with multiple thin shells or foils. The large Kirkpatrick-Baez modules, as well as the large Lobster-Eye X-ray telescope modules in Schmidt arrangement may serve as examples. All these space projects will require high quality and light segmented shells (bent or flat foils) with high X-ray reflectivity and excellent mechanical stability. The Multi Foil Optics (MFO) approach represent a promising alternative for both LE and K-B X-ray optical modules. Several types of reflecting substrates may be considered for these applications, with emphasis on thin float glass sheets and, more recently, high quality silicon wafers. This confirms the importance of non- Wolter X-ray optics designs for the future. Future large space X-ray telescopes (such as IXO) require precise and light-weight X-ray optics based on numerous thin reflecting shells. Novel approaches and advanced technologies are to be exploited and developed. In this contribution, we refer on results of tested X-ray mirror shells produced by glass thermal forming (GTF) and by shaping Si wafers. Both glass foils and Si wafers are commercially available, have excellent surface microroughness of a few 0.1 nm, and low weight (the volume density is 2.5 g cm-3 for glass and 2.3 g cm-3 for Si). Technologies are needed to be exploited; how to shape these substrates to achieve the required precise Xray optics geometries without degradations of the fine surface microroughness. Although glass and recently silicon wafers are considered to represent most promising materials for future advanced large aperture space Xray telescopes, there also exist other alternative materials worth further study such as amorphous metals and glassy carbon [1]. In order to achieve sub-arsec angular resolutions, principles of active optics have to be adopted.

Evaluation of glued-diaphragm fibre optic pressure sensors in a shock tube

NASA Astrophysics Data System (ADS)

Sharifian, S. Ahmad; Buttsworth, David R.

2007-02-01

Glued-diaphragm fibre optic pressure sensors that utilize standard telecommunications components which are based on Fabry-Perot interferometry are appealing in a number of respects. Principally, they have high spatial and temporal resolution and are low in cost. These features potentially make them well suited to operation in extreme environments produced in short-duration high-enthalpy wind tunnel facilities where spatial and temporal resolution are essential, but attrition rates for sensors are typically very high. The sensors we consider utilize a zirconia ferrule substrate and a thin copper foil which are bonded together using an adhesive. The sensors show a fast response and can measure fluctuations with a frequency up to 250 kHz. The sensors also have a high spatial resolution on the order of 0.1 mm. However, with the interrogation and calibration processes adopted in this work, apparent errors of up to 30% of the maximum pressure have been observed. Such errors are primarily caused by mechanical hysteresis and adhesive viscoelasticity. If a dynamic calibration is adopted, the maximum measurement error can be limited to about 10% of the maximum pressure. However, a better approach is to eliminate the adhesive from the construction process or design the diaphragm and substrate in a way that does not require the adhesive to carry a significant fraction of the mechanical loading.

Diagnosis of warm dense conditions in foil targets heated by intense femtosecond laser pulses using Kα imaging spectroscopy

DOE PAGES

Bae, L. J.; Zastrau, U.; Chung, H. -K.; ...

2018-03-01

Warm dense conditions in titanium foils irradiated with intense femtosecond laser pulses are diagnosed using an x-ray imaging spectroscopy technique. The line shapes of radially resolved titanium Kα spectra are measured with a toroidally bent GaAs crystal and an x-ray charge-coupled device. Measured spectra are compared with the K-shell emissions modeled using an atomic kinetics – spectroscopy simulation code. Kα line shapes are strongly affected by warm (5-40 eV) bulk electron temperatures and imply multiple temperature distributions in the targets. Finally, the spatial distribution of temperature is dependent on the target thickness, and a thin target shows an advantage tomore » generate uniform warm dense conditions in a large area.« less

High temperature insulation materials for reradiative thermal protection systems

NASA Technical Reports Server (NTRS)

Hughes, T. A.

1972-01-01

Results are presented of a two year program to evaluate packaged thermal insulations for use under a metallic radiative TPS of a shuttle orbiter vehicle. Evaluations demonstrated their survival for up to 100 mission reuse cycles under shuttle acoustic and thermal loads with peak temperatures of 1000 F, 1800 F, 2000 F, 2200 F and 2500 F. The specimens were composed of low density refractory fiber felts, packaged in thin gage metal foils. In addition, studies were conducted on the venting requirements of the packages, salt spray resistance of the metal foils, and the thermal conductivity of many of the insulations as a function of temperature and ambient air pressure. Data is also presented on the radiant energy transport through insulations, and back-scattering coefficients were experimentally determined as a function of source temperature.

Multiple layer insulation cover

DOEpatents

Farrell, James J.; Donohoe, Anthony J.

1981-11-03

A multiple layer insulation cover for preventing heat loss in, for example, a greenhouse, is disclosed. The cover is comprised of spaced layers of thin foil covered fabric separated from each other by air spaces. The spacing is accomplished by the inflation of spaced air bladders which are integrally formed in the cover and to which the layers of the cover are secured. The bladders are inflated after the cover has been deployed in its intended use to separate the layers of the foil material. The sizes of the material layers are selected to compensate for sagging across the width of the cover so that the desired spacing is uniformly maintained when the cover has been deployed. The bladders are deflated as the cover is stored thereby expediting the storage process and reducing the amount of storage space required.