[Effect of core: dentin thickness ratio on the flexure strength of IPS Empress II heat-pressed all-ceramic restorative material].

PubMed

Liu, Yi-hong; Feng, Hai-lan; Bao, Yi-wang; Qiu, Yan

2007-02-18

To evaluate the effect of core:dentin thickness ratio on the flexure strength, fracture mode and origin of bilayered IPS Empress II ceramic composite specimens. IPS Empress II core ceramic, dentin porcelain and bilayered composite specimens with core:dentin thickness ratio of 2:1 and 1:1 were tested in three-point flexure strength. Mean strengths and standard deviations were determined. The optical microscopy was employed for identification of the fracture mode and origin. The flexure strength of dentin porcelain was the smallest(62.7 MPa), and the strength of bilayered composite specimens was smaller than single-layered core ceramic(190.2 MPa). The core: dentin ratio did not influence the strength of bilayered composite specimens. The frequency of occurrence of bilayered specimen delaminations was higher in the group of core: dentin thickness ratio of 1:1 than in the group of 2:1. IPS Empress II core ceramic was significantly stronger than veneering dentin porcelain. Core:dentin thickness ratio could significantly influence the fracture mode and origin, and bilayered IPS Empress II ceramic composite specimens showed little influence in the fracture strength.

Mechanical properties of glass fiber-reinforced endodontic posts.

PubMed

Cheleux, Nicolas; Sharrock, Patrick J

2009-10-01

Five types of posts from three different manufacturers (RTD, France, Carbotech, France and Ivoclar-Vivadent, Liechenstein) were subjected to three-point bending tests in order to obtain fatigue results, flexural strength and modulus. Transverse and longitudinal polished sections were examined by scanning electron microscopy and evaluated by computer-assisted image analysis. Physical parameters, including volume % of fibers, their dispersion index and coordination number, were calculated and correlated with mechanical properties. The weaker posts showed more fiber dispersion, higher resin contents, larger numbers of visible defects and reduced fatigue resistance. The flexural strength was inversely correlated with fiber diameter and the flexural modulus was weakly related to coordination number, volume % of fibers and dispersion index. The interfacial adhesion between the silica fibers and the resin matrix was observed to be of paramount importance.

A Comparison of the Flexural and Impact Strengths and Flexural Modulus of CAD/CAM and Conventional Heat-Cured Polymethyl Methacrylate (PMMA).

PubMed

Al-Dwairi, Ziad N; Tahboub, Kawkab Y; Baba, Nadim Z; Goodacre, Charles J

2018-06-13

The introduction of computer-aided design/computer-aided manufacturing (CAD/CAM) technology to the field of removable prosthodontics has recently made it possible to fabricate complete dentures of prepolymerized polymethyl methacrylate (PMMA) blocks, which are claimed to be of better mechanical properties; however, no published reports that have evaluated mechanical properties of CAD/CAM PMMA. The purpose of this study was to compare flexural strength, impact strength, and flexural modulus of two brands of CAD/CAM PMMA and a conventional heat-cured PMMA. 45 rectangular specimens (65 mm × 10 mm × 3 mm) were fabricated (15 CAD/CAM AvaDent PMMA specimens from AvaDent, 15 CAD/CAM Tizian PMMA specimens from Shütz Dental, 15 conventional Meliodent PMMA specimens from Heraeus Kulzer) and stored in distilled water at (37  ± 1°C) for 7 days. Specimens (N = 15) in each group were subjected to the three-point bending test and impact strength test, employing the Charpy configuration on unnotched specimens. The morphology of the fractured specimens was studied under a scanning electron microscope (SEM). Statistical analysis was performed using one-way ANOVA and Tukey pairwise multiple comparisons with 95% confidence interval. The Schütz Dental specimens showed the highest mean flexural strength (130.67 MPa) and impact strength (29.56 kg/m 2 ). The highest mean flexural modulus was recorded in the AvaDent group (2519.6 MPa). The conventional heat-cured group showed the lowest mean flexural strength (93.33 MPa), impact strength (14.756 kg/m 2 ), and flexural modulus (2117.2 MPa). Differences in means of flexural properties between AvaDent and Schütz Dental specimens were not statistically significant (p > 0.05). As CAD/CAM PMMA specimens exhibited improved flexural strength, flexural modulus, and impact strength in comparison to the conventional heat-cured groups, CAD/CAM dentures are expected to be more durable. Different brands of CAD/CAM PMMA may have inherent variations in mechanical properties. © 2018 by the American College of Prosthodontists.

Flexural Strength of Polymethyl Methacrylate Repaired with Fiberglass.

PubMed

Golbidi, Fariba; Pozveh, Maryam Amini

2017-07-01

The purpose of this experimental study was to discover a method to increase the strength of repaired polymethyl methacrylate (PMMA) samples. In this experimental study, 40 specimens with the dimensions of 65×10×2.5mm 3 were fabricated using heat-curing acrylic resin. Sixteen specimens were repaired with fiberglass and self-curing PMMA, while 16 samples were repaired with self-curing PMMA. Eight specimens were left intact as the control group. Afterwards, the flexural strengths of the repaired and intact specimens were measured by three-point bending test in a universal testing machine. Data were analyzed with one-way analysis of variance (ANOVA) and Tukey's HSD and LSD tests. The level of significance was set at P<0.05. The mean flexural strength of the samples repaired with fiberglass was higher than that of the other repaired samples. However, the difference was statistically significant only with respect to the Meliodent group (P=0.008). Impregnated fiberglass could be used in the repair of denture bases to improve the flexural strength. In terms of the fracture site, it can be concluded that the lower flexural strength of the auto-polymerizing acryl compared to that of the heat-curing type was the main reason for the occurrence of fractures, rather than the weak bond between heat-curing and auto-polymerizing acrylic resins.

Effect of different aging methods on the mechanical behavior of multi-layered ceramic structures.

PubMed

Borba, Márcia; de Araújo, Maico D; Fukushima, Karen A; Yoshimura, Humberto N; Griggs, Jason A; Della Bona, Álvaro; Cesar, Paulo F

2016-12-01

To evaluate the effect of two aging methods (mechanical cycling and autoclave) on the mechanical behavior of veneer and framework ceramic specimens with different configurations (monolithic, two and three-layers). Three ceramics used as framework for fixed dental prostheses (YZ-Vita In-Ceram YZ; IZ-Vita In-Ceram Zirconia; AL-Vita In-Ceram AL) and two veneering porcelains (VM7 and VM9) were studied. Bar-shaped specimens were produced in three different designs: monolithic, two layers (porcelain-framework) and three layers (porcelain-framework-porcelain). Specimens were tested for three-point flexural strength at 1MPa/s in 37°C artificial saliva. Three different experimental conditions were evaluated (n=10): control; mechanical cycling (2Hz, 37°C artificial saliva); and autoclave aging (134°C, 2 bars, 5h). Bi-layered specimens were tested in both conditions: with porcelain or framework ceramic under tension. Fracture surfaces were analyzed using stereomicroscope and scanning electron microscopy. Results were statistically analyzed using Kruskal-Wallis and Student-Newman-Keuls tests. Only for AL group, mechanical cycling and autoclave aging significantly decreased the flexural strength values in comparison to the control (p<0.01). YZ, AL, VM7 and VM9 monolithic groups showed no strength degradation. For multi-layered specimens, when the porcelain layer was tested in tension (bi and tri-layers), the aging methods evaluated also had no effect on strength (p≥0.05). Total and partial failure modes were identified. Mechanical cycling and autoclave aging protocols had no effect on the flexural strength values and failure behavior of YZ and IZ ceramic structures. Yet, AL monolithic structures showed a significant decrease in flexural strength with any of the aging methods. Copyright © 2016. Published by Elsevier Ltd.

Flexural toughness of steel fiber reinforced high performance concrete containing nano-SiO2 and fly ash.

PubMed

Zhang, Peng; Zhao, Ya-Nan; Li, Qing-Fu; Wang, Peng; Zhang, Tian-Hang

2014-01-01

This paper aims to clarify the effect of steel fiber on the flexural toughness of the high performance concrete containing fly ash and nano-SiO2. The flexural toughness was evaluated by two methods, which are based on ASTM C1018 and DBV-1998, respectively. By means of three-point bending method, the flexural toughness indices, variation coefficients of bearing capacity, deformation energy, and equivalent flexural strength of the specimen were measured, respectively, and the relational curves between the vertical load and the midspan deflection (P(V)-δ) were obtained. The results indicate that steel fiber has great effect on the flexural toughness parameters and relational curves (P(V)-δ) of the three-point bending beam specimen. When the content of steel fiber increases from 0.5% to 2%, the flexural toughness parameters increase gradually and the curves are becoming plumper and plumper with the increase of steel fiber content, respectively. However these flexural toughness parameters begin to decrease and the curves become thinner and thinner after the steel fiber content exceeds 2%. It seems that the contribution of steel fiber to the improvement of flexural toughness of the high performance concrete containing fly ash and nano-SiO2 is well performed only when the steel fiber content is less than 2%.

Flexural resistance of heat-pressed and CAD-CAM lithium disilicate with different translucencies.

PubMed

Fabian Fonzar, Riccardo; Carrabba, Michele; Sedda, Maurizio; Ferrari, Marco; Goracci, Cecilia; Vichi, Alessandro

2017-01-01

To compare flexural strength of CAD-CAM and heat-pressed lithium disilicate. For Pressed specimens (Group A), acrylate polymer blocks were cut with a saw in bars shape. Sprueing, investing and preheating procedures were carried out following manufacturer's instructions. IPS e.max Press ingots (Ivoclar-Vivadent) were divided into subgroups (n=15) according to translucency: A.1=HT-A3; A.2=MT-A3; A.3=LT-A3; A.4=MO2. Ingots were then pressed following manufacturer's instructions. For CAD-CAM specimens (Group B) blocks of IPS e.max CAD (Ivoclar-Vivadent) were divided into subgroups: B.1=HT-A3; B.2=MT-A3; B.3=LT-A3; B.4=MO2. Specimens (n=15) were obtained by cutting the blocks with a saw. Final crystallization was performed following manufacturer's instructions. Both Press and CAD specimens were polished and finished with silica carbide papers of increasing grit. Final dimensions of the specimens were 4.0±0.2mm, 1.2±0.2mm, and 16.0±0.2mm. Specimens were tested using a three-point bending test. Flexural strength, Weibull modulus, and Weibull characteristic strength were calculated. Flexural strength data were statistically analyzed. The overall means of Press and CAD specimens did not differ significantly. Within the Press group different translucencies were found to have similar flexural strength. Within the CAD group, statistically significant differences emerged among the tested translucencies (p<0.001). Specifically, MT had significantly higher flexural strength than HT and MO. Also, LT exhibited significantly higher flexural strength than MO. The choice between IPS e.max Press and IPS e.max CAD formulations can be based on different criteria than flexural resistance. Within each formulation, for IPS e.max Press translucency does not affect the flexural strength while for IPS e.max CAD it is an influential factor. Copyright © 2016 The Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Variations in Flexural Strength of Heat-polymerized Acrylic Resin after the Usage of Denture Cleansers.

PubMed

Ragher, Mallikarjuna; Vinayakumar, G; Patil, Sanketsopan; Chatterjee, Aishwarya; Mallikarjuna, D M; Dandekeri, Savita; Swetha, V; Pradeep, M R

2016-04-01

The objective of this study was to evaluate and compare changes in the flexural strength of heat-cured denture base resins when treated using denture cleansers. A total of 40 specimens with dimension 65 mm length, 10 mm width, and 3 mm thickness were prepared as per ISO 1567 specification. A total of 10 specimens were immersed in distilled water to be used as control. Of the remaining 30 samples, 10 were treated with Clinsodent, 10 with VI-Clean, and 10 with Clanden denture cleansers. Specimens in each group were subjected to three-point flexural load in universal testing machine at a cross-head speed of 5 mm/min. The peak load (N) was recorded and flexural strength was calculated. The findings were analyzed using Kruskal-Wallis analysis of variance and Mann-Whitney test. Heat-cured denture base resin selected for this study showed significant difference in flexural strength after immersion in denture cleansers Clinsodent, VI-Clean, and Clanden solutions, when compared with the control group. Findings of this study showed that denture cleansers altered the flexural strength of heat polymerized acrylic resins that endured soaking cycles which simulated 180 days of use. Hence, denture cleansers should be used with caution, once a day after brushing the dentures. It is advisable for patients to follow the manufacturer's instructions.

Effect of water temperature on cyclic fatigue properties of glass-fiber-reinforced hybrid composite resin and its fracture pattern after flexural testing.

PubMed

Kuroda, Soichi; Shinya, Akikazu; Vallittu, Pekka K; Nakasone, Yuji; Shinya, Akiyoshi

2013-02-01

To evaluate in vitro the influence of dynamic loading applied to a glass-fiber-reinforced hybrid composite resin on its flexural strength in a moist, simulated oral environment. Three-point flexural strength specimens were subjected to cyclic loading in water at 37°C and 55°C to investigate the influence of immersion temperature on impact fatigue properties. Specimens were subjected to cyclic impact loading at 1 Hz for up to 5 × 105 cycles to obtain the number of cycles to failure, the number of unbroken specimens after 5 × 105 cycles, and the residual flexural strength of unbroken specimens. Maximum loads of 100, 200, and 300 N were chosen for both the non-reinforced and the glass-fiber reinforced hybrid composite resins. The mean residual flexural strength for 100 N impact loading at temperatures of 37°C and 55°C was 634 and 636 MPa, respectively. All specimens fractured at fewer than 5 × 105 cycles for loads of 200 and 300 N. Reduced numbers of cycles to fracture and lower fatigue values were observed as both the maximum load and immersion temperature increased.

The volumetric fraction of inorganic particles and the flexural strength of composites for posterior teeth.

PubMed

Adabo, Gelson Luis; dos Santos Cruz, Carlos Alberto; Fonseca, Renata Garcia; Vaz, Luís Geraldo

2003-07-01

To evaluate the content of inorganic particles and the flexural strength of new condensable composites for posterior teeth in comparison to hybrid conventional composites. The determination of the content of inorganic particles was performed by mass weighing of a polymerized composite before and after the elimination of the organic phase. The volumetric particle content was determined by a practical method based on Archimedes' principle, which calculates the volume of the composite and their particles by differential mass measured in the air and in water. The flexural strength of three points was evaluated according to the norm ISO 4049:1988. The results showed the following filler content: Alert, 67.26%; Z-100, 65.27%; Filtek P 60, 62.34%; Ariston pHc, 64.07%; Tetric Ceram, 57.22%; Definite, 54.42%; Solitaire, 47.76%. In the flexural strength test, the materials presented the following decreasing order of resistance: Filtek P 60 (170.02 MPa)>Z-100 (151.34 MPa)>Tetric Ceram (126.14 MPa)=Alert (124.89 MPa)>Ariston pHc (102.00 MPa)=Definite (93.63 MPa)>Solitaire (56.71 MPa). New condensable composites for posterior teeth present a concentration of inorganic particles similar to those of hybrid composites but do not necessarily present higher flexural strength.

Effect of gas release in hot molding on flexural strength of composite friction brake

NASA Astrophysics Data System (ADS)

Rusdja, Andy Permana; Surojo, Eko; Muhayat, Nurul; Raharjo, Wijang Wisnu

2018-02-01

Composite friction brake is a vital part of braking system which serves to reduce the speed of vehicle. To fulfill the requirement of brake performance, composite friction brake must have friction and mechanical characteristic as required. The characteristics of composite friction brake are affected by brake material formulation and manufacturing parameter. In the beginning of hot molding, intermittent hot pressing was carried out to release the gases that consist of ammonia gas and water vapor. In composite friction brake, phenolic resin containing hexamethylenetetramine (HMTA) is often used as a binder. During hot molding, the reaction of phenolic resin and HMTA forms ammonia gas. Hot molding also generates water vapor because raw materials absorb moisture from environment when they are placed in storage. The gas release in hot molding is supposed affecting mechanical properties because it avoid entrapped gas in composite, so that this research investigated effect of gas release on flexural strength. Manufacturing of composite specimen was carried out as follow: mixing of raw materials, cold molding, and hot molding. In this research, duration of intermittent hot pressing and number of gas release were varied. The flexural strength of specimen was measured using three point bending test. The results showed that flexural strength specimens that were manufactured without gas release, using 4 times gas release with intermittent hot pressing for 5 and 10 seconds were not remarkably different. Conversely, hot molding using 4 times gas release with intermittent hot pressing for 15 seconds decreased flexural strength of composite. Hot molding using 2, 4, and 8 times gas release with intermittent hot pressing for 10 seconds also had no effect on increasing flexural strength. Increasing of flexural strength of composite was obtained only by using 6 times gas release with intermittent hot pressing for 10 seconds.

Transverse flexural tests as a tool for assessing damage to PMR-15 composites from isothermal aging in air at elevated temperatures

NASA Technical Reports Server (NTRS)

Bowles, Kenneth J.

1992-01-01

To date, the effect of thermo-oxidative aging on unidirectional composite mechanical properties has been monitored by the measurement of interlaminar shear strength (ILSS) and either three or four point longitudinal flexural strength (LFS) of the composites being tested. Both results are affected by the fiber-to-matrix bonding, the former being dependent on the shear resistance of the interface and the latter on the degree of load sharing by the fibers through the fiber/matrix interface. Recently, fiber/matrix interfacial bond strengths have been monitored using a transverse flexural strength (TFS) test method. This test method was used to evaluate the effect of fiber surface treatment on the fiber/matrix bond. The interface bonding was varied in these tests using Hercules A-fibers with three-types of surfaces that produce bonds of poor, better, and good quality. The TFS was found not only to be sensitive to the bonding, but also to the aging time of unidirectional A-fiber/PMR-15 composites. This relationship reflects the mechanism by which the PMR-15 degrades during thermal aging.

The effect of clinically relevant thermocycling on the flexural properties of endodontic post materials.

PubMed

Stewardson, Dominic A; Shortall, Adrian C; Marquis, Peter M

2010-05-01

It is suggested that fibre-reinforced composite (FRC) posts have lower elastic moduli than metal posts and this will reduce the incidence of root fracture. However, the mechanical properties may be altered in the oral environment. The aims of this study were to determine the effect on the flexural properties of FRC and metal post materials produced by: (1) a thermocycling regime which was clinically relevant and representative of that which would occur during 1 year in the mouth and (2) storage for 1 year at body temperature. Nine FRC and two metal post material samples were sealed in polythene sleeves and thermocycled between 10 degrees C and 50 degrees C for 10,000 cycles. Additional samples were stored dry at 37 degrees C for 1 year. The flexural strength and moduli were determined by three-point bending and compared with untreated control samples. Thermocycling and storage at 37 degrees C for 1 year decreased the mean flexural modulus of all materials. This was statistically significant for 8 of 11 materials after thermocycling, and 4 of 11 materials after storage at 37 degrees C (p<0.05). Thermocycling and storage at 37 degrees C produced a non-significant increase in yield strength for both metal post materials. Thermocycling significantly increased the flexural strength of Postec while it decreased for the other FRC materials. Storage at 37 degrees C increased the flexural strength of three FRC materials (significantly for Postec) while it was decreased among the other materials. Although some of the changes noticed in flexural properties were statistically significant, it is doubtful that they are of sufficient magnitude to affect clinical performance.

Flexural Strength of Polymethyl Methacrylate Repaired with Fiberglass

PubMed Central

Golbidi, Fariba

2017-01-01

Objectives: The purpose of this experimental study was to discover a method to increase the strength of repaired polymethyl methacrylate (PMMA) samples. Materials and Methods: In this experimental study, 40 specimens with the dimensions of 65×10×2.5mm3 were fabricated using heat-curing acrylic resin. Sixteen specimens were repaired with fiberglass and self-curing PMMA, while 16 samples were repaired with self-curing PMMA. Eight specimens were left intact as the control group. Afterwards, the flexural strengths of the repaired and intact specimens were measured by three-point bending test in a universal testing machine. Data were analyzed with one-way analysis of variance (ANOVA) and Tukey’s HSD and LSD tests. The level of significance was set at P<0.05. Results: The mean flexural strength of the samples repaired with fiberglass was higher than that of the other repaired samples. However, the difference was statistically significant only with respect to the Meliodent group (P=0.008). Conclusions: Impregnated fiberglass could be used in the repair of denture bases to improve the flexural strength. In terms of the fracture site, it can be concluded that the lower flexural strength of the auto-polymerizing acryl compared to that of the heat-curing type was the main reason for the occurrence of fractures, rather than the weak bond between heat-curing and auto-polymerizing acrylic resins. PMID:29285033

Flexural properties of fiber reinforced root canal posts.

PubMed

Lassila, Lippo V J; Tanner, Johanna; Le Bell, Anna-Maria; Narva, Katja; Vallittu, Pekka K

2004-01-01

Fiber-reinforced composite (FRC) root canal posts have been introduced to be used instead of metal alloys and ceramics. The aim of this study was to investigate the flexural properties of different types of FRC posts and compare those values with a novel FRC material for dental applications. Seventeen different FRC posts of various brands (Snowpost, Carbopost, Parapost, C-post, Glassix, Carbonite) and diameters, (1.0-2.1 mm) and a continuous unidirectional E-glass FRC polymerized by light activation to a cylindrical form (everStick, diameter 1.5 mm) as a control material were tested. The posts (n=5) were stored at room's humidity or thermocycled (12.000 x, 5 degrees C/55 degrees C) and stored in water for 2 weeks before testing. A three-point bending test (span=10 mm) was used to measure the flexural strength and modulus of FRC post specimens. Analysis of ANOVA revealed that thermocycling, brand of material and diameter of specimen had a significant effect (p<0.001) on the fracture load and flexural strength. The highest flexural strength was obtained with the control material (everStick, 1144.9+/-99.9 MPa). There was a linear relationship between fracture load and diameter of posts for both glass fiber and carbon fiber posts. Thermocycling decreased the flexural modulus of the tested specimens by approximately 10%. Strength and fracture load decreased approximately 18% as a result of thermocycling. Considerable variation can be found in the calculated strength values of the studied post brands. Commercial prefabricated FRC posts showed lower flexural properties than an individually polymerised FRC material.

Flexural Toughness of Steel Fiber Reinforced High Performance Concrete Containing Nano-SiO2 and Fly Ash

PubMed Central

Zhao, Ya-Nan; Li, Qing-Fu; Wang, Peng; Zhang, Tian-Hang

2014-01-01

This paper aims to clarify the effect of steel fiber on the flexural toughness of the high performance concrete containing fly ash and nano-SiO2. The flexural toughness was evaluated by two methods, which are based on ASTM C1018 and DBV-1998, respectively. By means of three-point bending method, the flexural toughness indices, variation coefficients of bearing capacity, deformation energy, and equivalent flexural strength of the specimen were measured, respectively, and the relational curves between the vertical load and the midspan deflection (P V-δ) were obtained. The results indicate that steel fiber has great effect on the flexural toughness parameters and relational curves (P V-δ) of the three-point bending beam specimen. When the content of steel fiber increases from 0.5% to 2%, the flexural toughness parameters increase gradually and the curves are becoming plumper and plumper with the increase of steel fiber content, respectively. However these flexural toughness parameters begin to decrease and the curves become thinner and thinner after the steel fiber content exceeds 2%. It seems that the contribution of steel fiber to the improvement of flexural toughness of the high performance concrete containing fly ash and nano-SiO2 is well performed only when the steel fiber content is less than 2%. PMID:24883395

Composite resin reinforced with pre-tensioned glass fibers. Influence of prestressing on flexural properties.

PubMed

Schlichting, Luís Henrique; de Andrada, Mauro Amaral Caldeira; Vieira, Luiz Clóvis Cardoso; de Oliveira Barra, Guilherme Mariz; Magne, Pascal

2010-02-01

This investigation evaluated the flexural properties of two composite resins, and the influence of unidirectional glass fiber reinforcements, with and without pre-tensioning. Two composite resins (Q: Quixfil and A: Adoro) were used to fabricate 2 mm x 2 mm x 25 mm beams (N = 10), reinforced with two fiber bundles along the long axis of the beam and pre-tensioned under a load equivalent to 73.5% of its tensile strength (groups QPF and APF). In two other experimental groups, the bundles were similarly positioned but without pre-tension (groups QF and AF). Two more groups were included without fiber reinforcement (control groups Q and A). After 24h storage, specimens were subjected to a three-point flexural bending test to establish the flexural module, the deflection at initial failure and the flexural strength. Data were analyzed using a two-way analysis of variance (composite resin system and fiber reinforcement type) and the Tukey HSD post hoc tests (alpha = .05). The results showed that prestressing increased the flexural module of Adoro specimens (p<.001) but not Quixfil (p = .17). Prestressed beams reached greater deflection at initial failure than those conventionally reinforced (p<.001), namely .85-1.35 mm for Adoro and .66-.90 mm for Quixfil. Prestressing also significantly increased the flexural strength of beams (p<.001) in both Adoro and Quixfil groups, from 443.46 to 569.15 MPa and from 425.47 to 568.00 MPa, respectively. Pre-tensioning of unidirectional glass fibers increased both deflection until initial failure and flexural strength of Quixfil and Adoro composite resins, however, with limited effects on the flexural modulus. Copyright 2009 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Mechanical properties of contemporary composite resins and their interrelations.

PubMed

Thomaidis, Socratis; Kakaboura, Afrodite; Mueller, Wolf Dieter; Zinelis, Spiros

2013-08-01

To characterize a spectrum of mechanical properties of four representative types of modern dental resin composites and to investigate possible interrelations. Four composite resins were used, a microhybrid (Filtek Z-250), a nanofill (Filtek Ultimate), a nanohybrid (Majesty Posterior) and an ormocer (Admira). The mechanical properties investigated were Flexural Modulus and Flexural Strength (three point bending), Brinell Hardness, Impact Strength, mode I and mode II fracture toughness employing SENB and Brazilian tests and Work of Fracture. Fractographic analysis was carried out in an SEM to determine the origin of fracture for specimens subjected to SENB, Brazilian and Impact Strength testing. The results were statistically analyzed employing ANOVA and Tukey post hoc test (a=0.05) while Pearson correlation was applied among the mechanical properties. Significant differences were found between the mechanical properties of materials tested apart from mode I fracture toughness measured by Brazilian test. The latter significantly underestimated the mode I fracture toughness due to analytical limitations and thus its validity is questionable. Fractography revealed that the origin of fracture is located at notches for fracture toughness tests and contact surface with pendulum for Impact Strength testing. Pearson analysis illustrated a strong correlation between modulus of elasticity and hardness (r=0.87) and a weak negative correlation between Work of Fracture and Flexural Modulus (r=-0.46) and Work of Fracture and Hardness (r=-0.44). Weak correlations were also allocated between Flexural Modulus and Flexural Strength (r=0.40), Flexural Strength and Hardness (r=0.39), and Impact Strength and Hardness (r=0.40). Since the four types of dental resin composite tested exhibited large differences among their mechanical properties differences in their clinical performance is also anticipated. Copyright © 2013 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Influence of water immersion on the mechanical properties of fiber posts.

PubMed

Komada, Wataru; Inagaki, Tasuku; Ueda, Yoji; Omori, Satoshi; Hosaka, Keiichi; Tagami, Junji; Miura, Hiroyuki

2017-01-01

The purpose of this study was to evaluate the influence of water immersion on the mechanical properties of three kinds of glass fiber posts and the fracture resistance of structures using resin composites with glass fiber posts. Each post was divided into three groups; a control group and two water immersion groups (30 and 90 days). Flexural strength was determined by three-point bending test. Each structure was divided into two groups; a control group and a water immersion group for 30 days. The fracture strength of structures was determined by a static loading test. In the flexural strength, two kinds of post in water immersion groups showed lower values than control groups. In the fracture strength, two kinds of structures in water immersion group showed lower values than control groups. The prefabricated glass fiber posts and structures using resin composites with glass fiber posts were affected by water immersion. Copyright © 2016 Japan Prosthodontic Society. Published by Elsevier Ltd. All rights reserved.

Effect of Heat Treatment on the Physical Properties of Provisional Crowns during Polymerization: An in Vitro Study

PubMed Central

Mei, May L.; So, Sam Y. C.; Li, Hao; Chu, Chun-Hung

2015-01-01

This study concerned the effect of heat treatment during setting on the physical properties of four resin-based provisional restorative materials: Duralay (polymethyl methacrylate), Trim II (polyethyl methacrylate), Luxatemp (bis-acrylic composite), and Protemp 4 (bis-acrylic composite). Specimens were prepared at 23, 37, or 60 °C for evaluation of flexural strength, surface roughness, color change and marginal discrepancy. Flexural strength was determined by a three-point bending test. Surface profile was studied using atomic force microscopy. Color change was evaluated by comparing the color of the materials before and after placement in coffee. A travelling microscope helped prepare standardized crowns for assessment of marginal discrepancy. Flexural strength of all tested materials cured at 23 °C or 37 °C did not significantly change. The surface roughness and marginal discrepancy of the materials increased at 60 °C curing temperature. Marginal discrepancies, color stability, and other physical properties of materials cured at 23 °C or 37 °C did not significantly change. Flexural strength of certain provisional materials cured at 60 °C increased, but there was also an increase in surface roughness and marginal discrepancy. PMID:28788031

Step-stress analysis for predicting dental ceramic reliability

PubMed Central

Borba, Márcia; Cesar, Paulo F.; Griggs, Jason A.; Bona, Álvaro Della

2013-01-01

Objective To test the hypothesis that step-stress analysis is effective to predict the reliability of an alumina-based dental ceramic (VITA In-Ceram AL blocks) subjected to a mechanical aging test. Methods Bar-shaped ceramic specimens were fabricated, polished to 1µm finish and divided into 3 groups (n=10): (1) step-stress accelerating test; (2) flexural strength- control; (3) flexural strength- mechanical aging. Specimens from group 1 were tested in an electromagnetic actuator (MTS Evolution) using a three-point flexure fixture (frequency: 2Hz; R=0.1) in 37°C water bath. Each specimen was subjected to an individual stress profile, and the number of cycles to failure was recorded. A cumulative damage model with an inverse power law lifetime-stress relation and Weibull lifetime distribution were used to fit the fatigue data. The data were used to predict the stress level and number of cycles for mechanical aging (group 3). Groups 2 and 3 were tested for three-point flexural strength (σ) in a universal testing machine with 1.0 s in 37°C water. Data were statistically analyzed using Mann-Whitney Rank Sum test. Results Step-stress data analysis showed that the profile most likely to weaken the specimens without causing fracture during aging (95% CI: 0–14% failures) was: 80 MPa stress amplitude and 105 cycles. The median σ values (MPa) for groups 2 (493±54) and 3 (423±103) were statistically different (p=0.009). Significance The aging profile determined by step-stress analysis was effective to reduce alumina ceramic strength as predicted by the reliability estimate, confirming the study hypothesis. PMID:23827018

Step-stress analysis for predicting dental ceramic reliability.

PubMed

Borba, Márcia; Cesar, Paulo F; Griggs, Jason A; Della Bona, Alvaro

2013-08-01

To test the hypothesis that step-stress analysis is effective to predict the reliability of an alumina-based dental ceramic (VITA In-Ceram AL blocks) subjected to a mechanical aging test. Bar-shaped ceramic specimens were fabricated, polished to 1μm finish and divided into 3 groups (n=10): (1) step-stress accelerating test; (2) flexural strength-control; (3) flexural strength-mechanical aging. Specimens from group 1 were tested in an electromagnetic actuator (MTS Evolution) using a three-point flexure fixture (frequency: 2Hz; R=0.1) in 37°C water bath. Each specimen was subjected to an individual stress profile, and the number of cycles to failure was recorded. A cumulative damage model with an inverse power law lifetime-stress relation and Weibull lifetime distribution were used to fit the fatigue data. The data were used to predict the stress level and number of cycles for mechanical aging (group 3). Groups 2 and 3 were tested for three-point flexural strength (σ) in a universal testing machine with 1.0MPa/s stress rate, in 37°C water. Data were statistically analyzed using Mann-Whitney Rank Sum test. Step-stress data analysis showed that the profile most likely to weaken the specimens without causing fracture during aging (95% CI: 0-14% failures) was: 80MPa stress amplitude and 10(5) cycles. The median σ values (MPa) for groups 2 (493±54) and 3 (423±103) were statistically different (p=0.009). The aging profile determined by step-stress analysis was effective to reduce alumina ceramic strength as predicted by the reliability estimate, confirming the study hypothesis. Copyright © 2013 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Effect of the application of surface treatments before and after sintering on the flexural strength, phase transformation and surface topography of zirconia.

PubMed

Kurtulmus-Yilmaz, Sevcan; Aktore, Huseyin

2018-05-01

To evaluate the effects of airborne-particle abrasion (APA) and Er,Cr:YSGG laser irradiation on 4-point-flexural strength, phase transformation and morphologic changes of zirconia ceramics treated at pre-sintered or post-sintered stage. Three hundred and forty-two bar shaped zirconia specimens were milled with different sizes according to the flexural strength test (n = 10), X-ray diffraction (XRD) (n = 4) and field emission scanning electron microscope (FE-SEM) (n = 4) analyses. For each test protocol, specimens were divided into 4 main groups whether the surface treatments applied before or after sintering and whether the specimens received heat treatment or not as pre-sintered, post-sintered no-heat and post-sintered heat-treated groups, and a group was served as control. Main groups were further divided into 6 equal subgroups according to surface treatment method applied (2 W-, 3 W-, 4 W-, 5 W-, 6 W-laser irradiations and APA). Surface treatments were applied to pre-sintered groups before sintering and to post-sintered groups after sintering. Post-sintered heat-treated groups were subjected to veneer ceramic firing simulation after surface treatments. Flexural strength and flexural modulus values were statistically analysed and monoclinic phase content was calculated. Weibull analysis was used to evaluate strength reliability and fractographic analysis was conducted. Highest flexural strength values were detected at post-sintered no-heat APA and 4W-laser groups (P < 0.05). Pre-sintered groups showed statistically lower flexural strength values. Heat treatment decreased the strength of the specimens. Monoclinic phase content was only detected at post-sintered no-heat groups and the highest amount was detected at APA group. Rougher surfaces and deeper irregularities were detected at FE-SEM images pre-sintered groups. Application of surface treatments at pre-sintered stage may be detrimental for zirconia ceramics in terms of flexural strength. Treating the surface of zirconia ceramic before sintering process is not recommended due to significant decrease in flexural strength values. 2 W-4 W Er,Cr:YSGG laser irradiations can be regarded as alternative surface treatment methods when zirconia restoration would be subjected to veneer ceramic firing procedures. Copyright © 2018 Elsevier Ltd. All rights reserved.

Effect of plasma welding parameters on the flexural strength of Ti-6Al-4V alloy.

PubMed

Lyra e Silva, João Paulo; Fernandes Neto, Alfredo Júlio; Raposo, Luís Henrique Araújo; Novais, Veridiana Resende; de Araujo, Cleudmar Amaral; Cavalcante, Luisa de Andrade Lima; Simamoto Júnior, Paulo Cezar

2012-01-01

The aim of this study was to assess the effect of different plasma arc welding parameters on the flexural strength of titanium alloy beams (Ti-6Al-4V). Forty Ti-6Al-4V and 10 NiCr alloy beam specimens (40 mm long and 3.18 mm diameter) were prepared and divided into 5 groups (n=10). The titanium alloy beams for the control group were not sectioned or subjected to welding. Groups PL10, PL12, and PL14 contained titanium beams sectioned and welded at current 3 A for 10, 12 or 14 ms, respectively. Group NCB consisted of NiCr alloy beams welded using conventional torch brazing. After, the beams were subjected to a three-point bending test and the values obtained were analyzed to assess the flexural strength (MPa). Statistical analysis was carried out by one-way ANOVA and Tukey's HSD test at 0.05 confidence level. Significant difference was verified among the evaluated groups (p<0.001), with higher flexural strength for the control group (p<0.05). No significant differences was observed among the plasma welded groups (p>0.05). The NCB group showed the lowest flexural strength, although it was statistically similar to the PL 14 group (p>0.05). The weld depth penetration was not significantly different among the plasma welded groups (p=0.05). Three representative specimens were randomly selected to be evaluated under scanning electron microcopy. The composition of the welded regions was analyzed by energy dispersive X-ray spectroscopy. This study provides an initial set of parameters supporting the use of plasma welding during fabrication of titanium alloy dental frameworks.

Acoustic emission analysis of fiber-reinforced composite in flexural testing.

PubMed

Alander, Pasi; Lassila, Lippo V J; Tezvergil, Arzu; Vallittu, Pekka K

2004-05-01

The aim of this study was to examine the emission of acoustic signals from six commercially available fiber-reinforced composites (FRC) used in the frameworks of fixed partial dentures in material bending. FRC test specimens were made of six commercially available fiber products of polyethylene or glass and five light-curing resins. FRC test specimens were polymerized with a hand light-curing unit or with a light-curing oven. The flexural test for determination of ultimate flexural strength of test specimens (n = 6) was based on the ISO 10477 standard after the specimens were stored in air or in water for two weeks. The acoustic emission (AE) signals were monitored during three-point loading test of the test specimens using a test with increasing loading levels until the specimens fractured. Generally, stress level required for the AE activity initiation ranged from 107 MPa (Ribbond) to 579 MPa (everStick). The ultimate flexural strength of FRC specimens were higher, ranging from 132 to 764 MPa, being highest with everStick and Vectris FRC, and lowest with Ribbond FRC. ANOVA showed a statistically significant difference between the initiation of AE activity and the ultimate flexural strength according to the brand (p < 0.001) storing conditions (p < 0.001) and polymerization procedure (p < 0.001). AE activity and ultimate flexural strength correlated significantly (p < 0.010, r = 0.887). The result of this study suggested that AE activity in FRC specimens started at a 19-32% lower stress level than occurred at final fracture.

Effect of thermal cycling on flexural properties of carbon-graphite fiber-reinforced polymers.

PubMed

Segerström, Susanna; Ruyter, I Eystein

2009-07-01

To determine flexural strength and modulus after water storage and thermal cycling of carbon-graphite fiber-reinforced (CGFR) polymers based on poly(methyl methacrylate) and a copolymer matrix, and to examine adhesion between fiber and matrix by scanning electron microscopy (SEM). Solvent cleaned carbon-graphite (CG) braided tubes of fibers were treated with a sizing resin. The resin mixture of the matrix was reinforced with 24, 36, 47 and 58wt% (20, 29, 38 and 47vol.%) CG-fibers. After heat polymerization the specimens were kept for 90 days in water and thereafter hydrothermally cycled (12,000 cycles, 5/55 degrees C). Mechanical properties were evaluated by three-point bend testing. After thermal cycling, the adhesion between fibers and matrix was evaluated by SEM. Hydrothermal cycling did not decrease flexural strength of the CGFR polymers with 24 and 36wt% fiber loadings; flexural strength values after thermocycling were 244.8 (+/-32.33)MPa for 24wt% and 441.3 (+/-68.96)MPa for 36wt%. Flexural strength values after thermal cycling were not further increased after increasing the fiber load to 47 (459.2 (+/-45.32)MPa) and 58wt% (310.4 (+/-52.79)MPa). SEM revealed good adhesion between fibers and matrix for all fiber loadings examined. The combination of the fiber treatment and resin matrix described resulted in good adhesion between CG-fibers and matrix. The flexural values for fiber loadings up to 36wt% appear promising for prosthodontic applications such as implant-retained prostheses.

Effects of cementation surface modifications on fracture resistance of zirconia.

PubMed

Srikanth, Ramanathan; Kosmac, Tomaz; Della Bona, Alvaro; Yin, Ling; Zhang, Yu

2015-04-01

To examine the effects of glass infiltration (GI) and alumina coating (AC) on the indentation flexural load and four-point bending strength of monolithic zirconia. Plate-shaped (12 mm × 12 mm × 1.0 mm or 1.5 or 2.0 mm) and bar-shaped (4 mm × 3 mm × 25 mm) monolithic zirconia specimens were fabricated. In addition to monolithic zirconia (group Z), zirconia monoliths were glass-infiltrated or alumina-coated on their tensile surfaces to form groups ZGI and ZAC, respectively. They were also glass-infiltrated on their upper surfaces, and glass-infiltrated or alumina-coated on their lower (tensile) surfaces to make groups ZGI2 and ZAC2, respectively. For comparison, porcelain-veneered zirconia (group PVZ) and monolithic lithium disilicate glass-ceramic (group LiDi) specimens were also fabricated. The plate-shaped specimens were cemented onto a restorative composite base for Hertzian indentation using a tungsten carbide spherical indenter with a radius of 3.2mm. Critical loads for indentation flexural fracture at the zirconia cementation surface were measured. Strengths of bar-shaped specimens were evaluated in four-point bending. Glass infiltration on zirconia tensile surfaces increased indentation flexural loads by 32% in Hertzian contact and flexural strength by 24% in four-point bending. Alumina coating showed no significant effect on resistance to flexural damage of zirconia. Monolithic zirconia outperformed porcelain-veneered zirconia and monolithic lithium disilicate glass-ceramics in terms of both indentation flexural load and flexural strength. While both alumina coating and glass infiltration can be used to effectively modify the cementation surface of zirconia, glass infiltration can further increase the flexural fracture resistance of zirconia. Copyright © 2015 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Effects of cementation surface modifications on fracture resistance of zirconia

PubMed Central

Srikanth, Ramanathan; Kosmac, Tomaz; Bona, Alvaro Della; Yin, Ling; Zhang, Yu

2015-01-01

Objectives To examine the effects of glass infiltration (GI) and alumina coating (AC) on the indentation flexural load and four-point bending strength of monolithic zirconia. Methods Plate-shaped (12 mm × 12 mm × 1.0 mm or 1.5 mm or 2.0 mm) and bar-shaped (4 mm × 3 mm × 25 mm) monolithic zirconia specimens were fabricated. In addition to monolithic zirconia (group Z), zirconia monoliths were glass-infiltrated or alumina-coated on their tensile surfaces to form groups ZGI and ZAC, respectively. They were also glass-infiltrated on their upper surfaces, and glass-infiltrated or alumina-coated on their lower (tensile) surfaces to make groups ZGI2 and ZAC2, respectively. For comparison, porcelain-veneered zirconia (group PVZ) and monolithic lithium disilicate glass-ceramic (group LiDi) specimens were also fabricated. The plate-shaped specimens were cemented onto a restorative composite base for Hertzian indentation using a tungsten carbide spherical indenter with a radius of 3.2 mm. Critical loads for indentation flexural fracture at the zirconia cementation surface were measured. Strengths of bar-shaped specimens were evaluated in four-point bending. Results Glass infiltration on zirconia tensile surfaces increased indentation flexural loads by 32% in Hertzian contact and flexural strength by 24% in four-point bending. Alumina coating showed no significant effect on resistance to flexural damage of zirconia. Monolithic zirconia outperformed porcelain-veneered zirconia and monolithic lithium disilicate glass-ceramics in terms of both indentation flexural load and flexural strength. Significance While both alumina coating and glass infiltration can be used to effectively modify the cementation surface of zirconia, glass infiltration can further increase the flexural fracture resistance of zirconia. PMID:25687628

Comparison of the wear and flexural characteristics of flowable resin composites for posterior lesions.

PubMed

Sumino, Natsu; Tsubota, Keishi; Takamizawa, Toshiki; Shiratsuchi, Koji; Miyazaki, Masashi; Latta, Mark A

2013-01-01

To determine the localized wear and flexural properties of flowable resin composites for posterior lesions compared with universal resin composites produced by the same manufacturers. Ten specimens of each of three flowable resins, G-ænial Universal Flo, G-ænial Flo and Clearfil Majesty Flow, and the corresponding resin composite materials, Kalore and Clearfil Majesty Esthetics, were prepared in custom fixtures and subjected to 400,000 wear machine cycles to simulate localized wear. The total maximum depth and volume loss of the wear facets was calculated for each specimen using a profilometer. A three-point bending test was performed to determine the flexural strength, modulus of elasticity and resilience. Values were statistically compared using one-way analysis of variance (ANOVA) followed by Tukey's Honestly Significant Difference (HSD) test. The wear depth ranged from 58.3-126.9 m and the volumetric loss ranged from 0.019-0.049 mm(3), with significant differences observed between restorative materials. The wear depth of G-ænial Universal Flo was significantly smaller than those of the other resin composites tested. The flexural strengths and elastic modulus ranged from 90.5-135.1 MPa and from 4.7-7.6 GPa, respectively. A significantly greater flexural strength and higher elastic modulus was found for G-ænial Universal Flo than the other composites. The wear and mechanical properties of the flowable resin composites tested suggested improved performance compared with universal resin composites.

Flexural properties and shock-absorbing capabilities of new face guard materials reinforced with fiberglass cloth.

PubMed

Abe, Keisuke; Takahashi, Hidekazu; Churei, Hiroshi; Iwasaki, Naohiko; Ueno, Toshiaki

2013-02-01

 Experimental materials incorporating fiberglass cloth were used to develop a thin and lightweight face guard (FG). This study aims to evaluate the effect of fiberglass reinforcement on the flexural and shock absorption properties compared with conventional thermoplastic materials.  Four commercial 3.2-mm and 1.6-mm medical splint materials (Aquaplast, Polyform, Co-polymer, and Erkodur) and two experimental materials were examined for use in FGs. The experimental materials were prepared by embedding two or four sheets of a plain woven fiberglass cloth on both surfaces of 1.5-mm Aquaplast. The flexural strength and flexural modulus were determined using a three-point bending test. The shock absorption properties were evaluated for a 5200-N impact load using the first peak intensity with a load cell system and the maximum stress with a film sensor system.  The flexural strength (74.6 MPa) and flexural modulus (6.3 GPa) of the experimental material with four sheets were significantly greater than those of the 3.2-mm commercial specimens, except for the flexural strength of one product. The first peak intensity (515 N) and maximum stress (2.2 MPa) of the experimental material with four sheets were significantly lower than those of the commercial 3.2-mm specimens, except for one product for each property. These results suggest that the thickness and weight of the FG can be reduced using the experimental fiber-reinforced material. © 2012 John Wiley & Sons A/S.

Comparative characterization of a novel cad-cam polymer-infiltrated-ceramic-network

PubMed Central

Pascual, Agustín; Camps, Isabel; Grau-Benitez, María

2015-01-01

Background The field of dental ceramics for CAD-CAM is enriched with a new innovative material composition having a porous three-dimensional structure of feldspathic ceramic infiltrated with acrylic resins.The aim of this study is to determine the mechanical properties of Polymer-Infiltrated-Ceramic-Network (PICN) and compare its performance with other ceramics and a nano-ceramic resin available for CAD-CAM systems. Material and Methods In this study a total of five different materials for CAD-CAM were investigated. A polymer-infiltrated ceramic (Vita Enamic), a nano-ceramic resin (Lava Ultimate), a feldspathic ceramic (Mark II), a lithium disilicate ceramic (IPS-e max CAD) and finally a Leucite based ceramic (Empress - CAD). From CAD-CAM blocks, 120 bars (30 for each material cited above) were cut to measure the flexural strength with a three-point-bending test. Strain at failure, fracture stress and Weibull modulus was calculated. Vickers hardness of each material was also measured. Results IPS-EMAX presents mechanical properties significantly better from the other materials studied. Its strain at failure, flexural strength and hardness exhibited significantly higher values in comparison with the others. VITA ENAMIC and LAVA ULTIMATE stand out as the next most resistant materials. Conclusions The flexural strength, elastic modulus similar to a tooth as well as having less hardness than ceramics make PICN materials an option to consider as a restorative material. Key words:Ceramic infiltrated with resin, CAD-CAM, Weibull modulus, flexural strength, micro hardness. PMID:26535096

Static and cyclic loading of fiber-reinforced dental resin.

PubMed

Drummond, James L; Bapna, Mahendra S

2003-05-01

The aim of this study was to evaluate the flexure strength of unidirectional fiber-reinforced resins under static and cyclic loading with and without thermal cycling. The fiber-reinforced resin materials chosen for this project were commercially available endodontic posts and commercially procured bar samples. For all materials, controls for flexure strength were tested in air and in water using three-point loading. Specimens were thermal cycled between 7 and 63 degrees C for 6000 cycles. A staircase approach was used to determine the flexure fatigue limit and scanning microscopy was used to examine the microstructure. The carbon/graphite fiber-reinforced resin posts and the glass FiberKor posts were significantly stronger than the ceramic (zirconia) and the other glass-reinforced resin materials. Thermal cycling caused a significant lowering (11-24%) of the flexure strength for each resin based post system. The ceramic post system decreased only by 2%. Further, for standard size glass fiber-reinforced resin bars, no significant differences between testing in air and water was observed, but a significant difference between static and cyclic loading was noted. The decreases in the strength property due to thermal cycling and the cyclic loading of these materials indicates that their utilization in the oral environment enhances their degradation, and potentially shortens their clinical life.

Research on graphite reinforced glass matrix composites

NASA Technical Reports Server (NTRS)

Bacon, J. F.; Prewo, K. M.; Thompson, E. R.

1978-01-01

A composite that can be used at temperatures up to 875 K with mechanical properties equal or superior to graphite fiber reinforced epoxy composites is presented. The composite system consist of graphite fiber, uniaxially or biaxially, reinforced borosilicate glass. The mechanical and thermal properties of such a graphite fiber reinforced glass composite are described, and the system is shown to offer promise as a high performance structural material. Specific properties that were measured were: a modified borosilicate glass uniaxially reinforced by Hercules HMS graphite fiber has a three-point flexural strength of 1030 MPa, a four-point flexural strength of 964 MPa, an elastic modulus of 199 GPa and a failure strain of 0.0052. The preparation and properties of similar composites with Hercules HTS, Celanese DG-102, Thornel 300 and Thornel Pitch graphite fibers are also described.

[Comparison of wear resistance and flexural strength of three kinds of bulk-fill composite resins].

PubMed

Zhang, Huan; Zhang, Meng-Long; Qiu, Li-Hong; Yu, Jing-Tao; Zhan, Fu-Liang

2016-06-01

To compare the abrasion resistance and flexure strength of three bulk-fill resin composites with an universal nano-hybrid composite resins. The specimens were prepared with three kinds of bulk fill composites (SDR , sonicfill, Tetric N-Ceram Bulk Fill) and an universal nano-hybrid composite resins(Herculite Precis). 10 mm in diameter × 2mm in height specimens were prepared for abrasion resistance, while 2 mm in width × 2 mm in depth×25 mm in length specimens were prepared for flexure strength. The specimens were mounted in a bal1-on-disc wear testing machine and abraded with the media artificial saliva(50 N loads, 10000 cycles).Flexural test was performed with an Universal Testing Machine at a cross-head speed of 1mm/min. One-way variance analysis was used to determine the statistical differences of volume loss and flexural strength among groups with SPSS 13.0 software package(P<0.05). The volume loss was as follows: SDR (1.2433±0.11) mm30.05). With regard to wear resistance and flexural strength, Tetric N-Ceram Bulk Fill is recommended as an alternative for posterior restorations.

Evaluating the fracture toughness and flexural strength of pressable dental ceramics: an in vitro study.

PubMed

Gurram, Ravi; Krishna, C H Vamsi; Reddy, K Mahendranadh; Reddy, G V K Mohan; Shastry, Y Mahadev

2014-12-01

The study was undertaken to evaluate the biaxial flexural strength, biaxial flexural strength after etching with 9 % HF acid and fracture toughness of three commonly used pressable all ceramic core materials. Ninety glass ceramic specimens were fabricated from three commercially available leucite based core ceramic material (1) Esthetic Empress, (2) Cergo, and (3) Performance Plus. Thirty discs of each material were divided into three groups of 10 discs each. Biaxial flexural strength (30 discs,) Biaxial flexural strength for samples treated with 9 % HF acid (30 discs) and fracture toughness (30 discs) were evaluated. Core material Performance Plus had the lowest biaxial strength of 124.89 MPa, Cergo had strength of 152.22 MPa and the highest value of 163.95 was reported for Esthetic Empress. For samples treated 9 % HF, Performance Plus had the lowest biaxial strength of 98.37 MPa, Cergo had strength of 117.42 MPa and the highest value of 143.74 was reported for Esthetic Empress. Core material Performance Plus had the lowest fracture toughness of 1.063 MPa, Cergo had strength of 1.112 MPa and the highest value of 1.225 was reported for Esthetic Empress. The results shows that Esthetic Empress had better mechanical properties compared to Cergo had Performance Plus in relation to the parameters tested.

Tensile and flexural strength of commercially pure titanium submitted to laser and tungsten inert gas welds.

PubMed

Atoui, Juliana Abdallah; Felipucci, Daniela Nair Borges; Pagnano, Valéria Oliveira; Orsi, Iara Augusta; Nóbilo, Mauro Antônio de Arruda; Bezzon, Osvaldo Luiz

2013-01-01

This study evaluated the tensile and flexural strength of tungsten inert gas (TIG) welds in specimens made of commercially pure titanium (CP Ti) compared with laser welds. Sixty cylindrical specimens (2 mm diameter x 55 mm thick) were randomly assigned to 3 groups for each test (n=10): no welding (control), TIG welding (10 V, 36 A, 8 s) and Nd:YAG laser welding (380 V, 8 ms). The specimens were radiographed and subjected to tensile and flexural strength tests at a crosshead speed of 1.0 mm/min using a load cell of 500 kgf applied on the welded interface or at the middle point of the non-welded specimens. Tensile strength data were analyzed by ANOVA and Tukey's test, and flexural strength data by the Kruskal-Wallis test (α=0.05). Non-welded specimens presented significantly higher tensile strength (control=605.84 ± 19.83) (p=0.015) and flexural strength (control=1908.75) (p=0.000) than TIG- and laser-welded ones. There were no significant differences (p>0.05) between the welding types for neither the tensile strength test (TIG=514.90 ± 37.76; laser=515.85 ± 62.07) nor the flexural strength test (TIG=1559.66; laser=1621.64). As far as tensile and flexural strengths are concerned, TIG was similar to laser and could be suitable to replace laser welding in implant-supported rehabilitations.

Biaxial flexural strength of Turkom-Cera core compared to two other all-ceramic systems.

PubMed

Al-Makramani, Bandar Mohammed Abdullah; Razak, Abdul Aziz Abdul; Abu-Hassan, Mohamed Ibrahim

2010-12-01

Advances in all-ceramic systems have established predictable means of providing metal-free aesthetic and biocompatible materials. These materials must have sufficient strength to be a practical treatment alternative for the fabrication of crowns and fixed partial dentures. The aim of this study was to compare the biaxial flexural strength of three core ceramic materials. Three groups of 10 disc-shaped specimens (16 mm diameter x 1.2 mm thickness - in accordance with ISO-6872, 1995) were made from the following ceramic materials: Turkom-Cera Fused Alumina [(Turkom-Ceramic (M) Sdn Bhd, Puchong, Selangor, Malaysia)], In-Ceram (Vita Zahnfabrik, Bad Säckingen, Baden-Württemberg, Germany) and Vitadur-N (Vita Zahnfabrik, Bad Säckingen, Baden-Württemberg, Germany), which were sintered according to the manufacturer's recommendations. The specimens were subjected to biaxial flexural strength test in an universal testing machine at a crosshead speed of 0.5 mm/min. The definitive fracture load was recorded for each specimen and the biaxial flexural strength was calculated from an equation in accordance with ISO-6872. The mean biaxial flexural strength values were: Turkom-Cera: 506.8 ± 87.01 MPa, In-Ceram: 347.4 ± 28.83 MPa and Vitadur-N: 128.7 ± 12.72 MPa. The results were analyzed by the Levene's test and Dunnett's T3 post-hoc test (SPSS software V11.5.0 for Windows, SPSS, Chicago, IL, USA ) at a preset significance level of 5% because of unequal group variances (P<0.001). There was statistically significant difference between the three core ceramics (P<0.05). Turkom-Cera showed the highest biaxial flexural strength, followed by In-Ceram and Vitadur-N. Turkom-Cera core had significantly higher flexural strength than In-Ceram and Vitadur-N ceramic core materials.

Does artificial aging affect mechanical properties of CAD/CAM composite materials.

PubMed

Egilmez, Ferhan; Ergun, Gulfem; Cekic-Nagas, Isil; Vallittu, Pekka K; Lassila, Lippo V J

2018-01-01

The purpose of this study was to determine the flexural strength and Weibull characteristics of different CAD/CAM materials after different in vitro aging conditions. The specimens were randomly assigned to one of the six in vitro aging conditions: (1) water storage (37°C, 3 weeks), (2) boiling water (24h), (3) hydrochloric acid exposure (pH: 1.2, 24h), (4) autoclave treatment (134°C, 200kPa, 12h), (5) thermal cycling (5000 times, 5-55°C), (6) cyclic loading (100N, 50,000 cycles). No treatment was applied to the specimens in control group. Three-point bending test was used for the calculation of flexural strength. The reliability of the strength was assessed by Weibull distribution. Surface roughness and topography was examined by coherence scanning interferometry. Evaluated parameters were compared using the Kruskall-Wallis or Mann-Whitney U test. Water storage, autoclave treatment and thermal cycling significantly decreased the flexural strength of all materials (p<0.05), whereas HCl exposure or cyclic loading did not affect the properties (p>0.05). Weibull moduli of Cerasmart™ and Lava™ Ultimate were similar with control. Vita Enamic ® exhibited similar Weibull moduli in all aging groups except the HCl treated group (p>0.05). R a values of Cerasmart™ and Lava™ Ultimate were in the range of 0.053-0.088μm in the aged groups. However R a results of Vita Enamic ® were larger than 0.2μm. Flexural strength of newly developed restorative CAD/CAM materials was significantly decreased by artificial aging. Cyclic loading or HCl exposure does not affect to the flexural strength and structural reliability of Cerasmart™ and Lava™ Ultimate. Copyright © 2017 Japan Prosthodontic Society. Published by Elsevier Ltd. All rights reserved.

Evaluation of machinability and flexural strength of a novel dental machinable glass-ceramic.

PubMed

Qin, Feng; Zheng, Shucan; Luo, Zufeng; Li, Yong; Guo, Ling; Zhao, Yunfeng; Fu, Qiang

2009-10-01

To evaluate the machinability and flexural strength of a novel dental machinable glass-ceramic (named PMC), and to compare the machinability property with that of Vita Mark II and human enamel. The raw batch materials were selected and mixed. Four groups of novel glass-ceramics were formed at different nucleation temperatures, and were assigned to Group 1, Group 2, Group 3 and Group 4. The machinability of the four groups of novel glass-ceramics, Vita Mark II ceramic and freshly extracted human premolars were compared by means of drilling depth measurement. A three-point bending test was used to measure the flexural strength of the novel glass-ceramics. The crystalline phases of the group with the best machinability were identified by X-ray diffraction. In terms of the drilling depth, Group 2 of the novel glass-ceramics proves to have the largest drilling depth. There was no statistical difference among Group 1, Group 4 and the natural teeth. The drilling depth of Vita MK II was statistically less than that of Group 1, Group 4 and the natural teeth. Group 3 had the least drilling depth. In respect of the flexural strength, Group 2 exhibited the maximum flexural strength; Group 1 was statistically weaker than Group 2; there was no statistical difference between Group 3 and Group 4, and they were the weakest materials. XRD of Group 2 ceramic showed that a new type of dental machinable glass-ceramic containing calcium-mica had been developed by the present study and was named PMC. PMC is promising for application as a dental machinable ceramic due to its good machinability and relatively high strength.

Fiber-matrix integrity, micromorphology and flexural strength of glass fiber posts: Evaluation of the impact of rotary instruments.

PubMed

Pereira, Gabriel Kalil Rocha; Lançanova, Mateus; Wandscher, Vinicius Felipe; Kaizer, Osvaldo Bazzan; Limberger, Inácio; Özcan, Mutlu; Valandro, Luiz Felipe

2015-08-01

Several rotary instruments have been daily employed on clinic to promote cut aiming to adjust the length of fiber posts to the radicular conduct, but there is no information on the literature about the effects of the different rotary instruments and its impact on the micromorphology of surface and mechanical properties of the glass fiber post. This study aimed the impact of rotary instruments upon fiber-matrix integrity, micromorphology and flexural-strength of glass-fiber posts (GFP). GFP (N=110) were divided into 5 groups: Ctrl: as-received posts, DBc: coarse diamond-bur, DBff: extra-fine diamond-bur, CB: carbide-bur, DD: diamond-disc. Cutting procedures were performed under abundant irrigation. Posts exposed to rotary instruments were then subjected to 2-point inclined loading test (compression 45°) (n=10/group) and 3-point flexural-strength test (n=10/group). Fiber-matrix integrity and micromorphology at the cut surface were analyzed using a SEM (n=2/group). Cutting procedures did not significantly affect the 2-point (51.7±4.3-56.7±5.1 MPa) (p=0.0233) and 3-point flexural-strength (671.5±35.3-709.1±33.1 MPa) (p=0.0968) of the posts (One-way ANOVA and Tukey׳s test). Fiber detachment was observed only at the end point of the cut at the margins of the post. Cut surfaces of the CB group were smoother than those of the other groups. After 3-point flexural strength test, fiber-matrix separation was evident at the tensile side of the post. Rotary instruments tested with simultaneous water-cooling did not affect the resistance of the tested fiber posts but caused disintegration of the fibers from the matrix at the end of the cut, located at the margins. Copyright © 2015 Elsevier Ltd. All rights reserved.

The effect of custom adaptation and span-diameter ratio on the flexural properties of fiber-reinforced composite posts.

PubMed

Grande, Nicola M; Plotino, Gianluca; Ioppolo, Pietro; Bedini, Rossella; Pameijer, Cornelis H; Somma, Francesco

2009-05-01

To evaluate whether custom modification resulting in an anatomically shaped post and whether the span/diameter ratio (L/D) would affect the mechanical properties of fiber-reinforced composite posts. Preformed glass-fiber posts (Group 1) and modified glass-fiber posts (Group 2) and glass-fiber rods (Groups 3 and 4) (n=20) were loaded to failure in a three-point bending test to determine the maximum load (N), flexural strength (MPa) and flexural modulus (GPa). The span distance tested for Group 3 was 10.0mm, while for Group 4 was 22.0mm. Data were subjected to different statistical analysis with significance levels of P<0.05. The maximum load recorded for Groups 1 and 2 was 72.5+/-5.9N and 73.4+/-6.4N respectively, while for Groups 3 and 4 was 215.3+/-7N and 156.6+/-3.6N respectively. The flexural strength for Groups 1 and 2 was 914.6+/-53.1MPa and 1069.2+/-115.6MPa, while for Groups 3 and 4 was 685.4+/-22.2MPa and 899.6+/-46.1MPa. The flexural modulus recorded for Groups 1 and 2 was 32.6+/-3.2GPa and 33.4+/-2.2GPa respectively, while for Groups 3 and 4 was 13.7+/-0.3GPa and 34.4+/-0.3GPa respectively. The flexural properties of an anatomically custom modified fiber post were not affected by the modification procedure and the span-diameter ratio is an important parameter for the interpretation of flexural strength and flexural modulus values.

Cold spraying SiC/Al metal matrix composites: effects of SiC contents and heat treatment on microstructure, thermophysical and flexural properties

NASA Astrophysics Data System (ADS)

Gyansah, L.; Tariq, N. H.; Tang, J. R.; Qiu, X.; Feng, B.; Huang, J.; Du, H.; Wang, J. Q.; Xiong, T. Y.

2018-02-01

In this paper, cold spray was used as an additive manufacturing method to fabricate 5 mm thick SiC/Al metal matrix composites with various SiC contents. The effects of SiC contents and heat treatment on the microstructure, thermophysical and flexural properties were investigated. Additionally, the composites were characterized for retention of SiC particulates, splat size, surface roughness and the progressive understanding of strengthening, toughening and cracking mechanisms. Mechanical properties were investigated via three-point bending test, thermophysical analysis, and hardness test. In the as-sprayed state, flexural strength increased from 95.3 MPa to 133.5 MPa, an appreciation of 40% as the SiC contents increased, and the main toughening and strengthening mechanisms were zigzag crack propagation and high retention of SiC particulates respectively. In the heat treatment conditions, flexural strength appreciated significantly compared to the as-sprayed condition and this was as a result of coarsening of pure Al splat. Crack branching, crack deflection and interface delamination were considered as the main toughening mechanisms at the heat treatment conditions. Experimental results were consistent with the measured CTE, hardness, porosity and flexural modulus.

Evaluation of the flexural strength and microhardness of provisional crown and bridge materials fabricated by different methods

PubMed Central

Digholkar, Shruti; Madhav, V. N. V.; Palaskar, Jayant

2016-01-01

Purpose: The purpose of this study was to evaluate and compare the flexural strength and microhardness of provisional restorative materials fabricated utilizing rapid prototyping (RP), Computer Assisted Designing and Computer Assisted Milling (CAD-CAM) and conventional method. Materials and Methods: Twenty specimens of dimensions 25 mm × 2 mm × 2 mm (ADA-ANSI specification #27) were fabricated each using: (1) Three dimensional (3D) printed light-cured micro-hybrid filled composite by RP resin group, (2) a milled polymethyl methacrylate (CH) using CAD-CAM (CC resin group), and (3) a conventionally fabricated heat activated polymerized CH resin group. Flexural strength and microhardness were measured and values obtained were evaluated. Results: The measured mean flexural strength values (MegaPascals) were 79.54 (RP resin group), 104.20 (CC resin group), and 95.58 (CH resin group). The measured mean microhardness values (Knoop hardness number) were 32.77 (RP resin group), 25.33 (CC resin group), and 27.36 (CH resin group). The analysis of variance (ANOVA) test shows that there is statistically significant difference in the flexural strength values of the three groups (P < 0.05). According to the pairwise comparison of Tukey's honest significant difference (HSD) test, flexural strength values of CC resin group and CH resin group were higher and statistically significant than those of the RP resin group (P < 0.05). However, there was no significant difference between flexural strength values of CC resin and CH resin group (P = 0.64). The difference in microhardness values of the three groups was statistically significant according to ANOVA as well as the intergroup comparison done using the Tukey's HSD (post hoc) test (P < 0.05). Conclusions: CC-based CH had the highest flexural strength whereas RP-based 3D printed and light cured micro-hybrid filled composite had the highest microhardness. PMID:27746595

Effect of the addition of silanated silica on the mechanical properties of microwave heat-cured acrylic resin.

PubMed

da Silva, Lucas H; Feitosa, Sabrina A; Valera, Marcia C; de Araujo, Maria A M; Tango, Rubens N

2012-06-01

The purpose of this study was to evaluate the flexural strength and Vickers hardness of a microwave energy heat-cured acrylic resin by adding different concentrations of silane surface-treated nanoparticle silica. Acrylic resin specimens with dimensions of 65 × 10 × 2.5 mm were formed and divided into five experimental groups (n = 10) according to the silica concentration added to the acrylic resin mass (weight %) prior to polymerisation : G1, without silica; G2, 0.1% silica; G3, 0.5% silica; G4, 1.0% silica; and G5, 5.0% silica. The specimens were submitted to a three-point flexural strength test and to the Vickers hardness test (HVN). The data obtained were statistically analysed by anova and the Tukey test (α = 0.05). Regarding flexural strength, G5 differed from the other experimental groups (G1, G2, G3 and G4) presenting the lowest mean, while G4 presented a significantly higher mean, with the exception of group G3. Regarding Vickers hardness, a decrease in values was observed, in which G1 presented the highest hardness compared with the other experimental groups. Incorporating surface-treated silica resulted in direct benefits in the flexural strength of the acrylic resin activated by microwave energy; however, similar results were not achieved for hardness. © 2012 The Gerodontology Society and John Wiley & Sons A/S.

Influence of translucence/opacity and shade in the flexural strength of lithium disilicate ceramics

PubMed Central

Santos, Mila Oliveira; do Amaral, Flávia Lucisano Botelho; França, Fabiana Mantovani Gomes; Basting, Roberta Tarkany

2015-01-01

Background: Lithium disilicate ceramic system consists of glass ceramic ingots with different grades of translucence which may influence its flexural strength. Aims: To assess the three-point flexural strength of the different lithium disilicate-based ceramic ingots (IPS e.max Press/Ivoclar Vivadent) with different levels of translucence and shade. Materials and Methods: Six groups of ceramic ingots were selected to represent different levels of translucence and shade (HTA1, HTBL2, LTA2, LTB2, MO2, and HO). They measured 25 mm × 5 mm × 2 mm (n = 10), according to ISO 6872 specifications, and tested on a universal test machine (EMIC). Statistical Analysis Used: A one-way analysis of variance (ANOVA) was used (α = 0.05). Results: The results (in MPa) were: HTA1 = 392.98; HTBL2 = 390.74; LTA2 = 390.46; LTB2 = 389.92; MO2 = 390.43; HO = 391.96. ANOVA showed no significant difference among groups (P = 0.1528). Conclusions: Different levels of translucence, opacity and shade of ingots did not affect their mechanical strength, and the use of these ceramics should be guided by the esthetic demands of each clinical situation. PMID:26430304

Damage formation, fatigue behavior and strength properties of ZrO{sub 2}-based ceramics

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kozulin, A. A., E-mail: kozulyn@ftf.tsu.ru; Kulkov, S. S.; Narikovich, A. S.

It is suggested that a non-destructive testing technique using a three-dimensional X-ray tomography be applied to detecting internal structural defects and monitoring damage formation in a ceramic composite structure subjected to a bending load. Three-point bending tests are used to investigate the fatigue behavior and mechanical and physical properties of medical-grade ZrO{sub 2}-based ceramics. The bending strength and flexural modulus are derived under static conditions at a loading rate of 2 mm/min. The fatigue strength and fatigue limit under dynamic loading are investigated at a frequency of 10 Hz in three stress ranges: 0.91–0.98, 0.8–0.83, and 0.73–0.77 MPa of themore » static bending strength. The average values of the bending strength and flexural modulus of sintered specimens are 43 MPa and 22 GPa, respectively. The mechanical properties of the ceramics are found to be similar to those of bone tissues. The testing results lead us to conclude that the fatigue limit obtained from 10{sup 5} stress cycles is in the range 33–34 MPa, i.e. it accounts for about 75% of the static bending strength for the test material.« less

In vitro evaluation of the flexural properties of All-on-Four provisional fixed denture base resin partially reinforced with fibers.

PubMed

Li, Bei Bei; Xu, Jia Bin; Cui, Hong Yan; Lin, Ye; Di, Ping

2016-01-01

The aim of this study was to assess the effects of partial carbon or glass fiber reinforcement on the flexural properties of All-on-Four provisional fixed denture base resin. The carbon or glass fibers were woven (3% by weight) together in three strands and twisted and tightened between the two abutments in a figure-of-"8" pattern. Four types of specimens were fabricated for the three-point loading test. The interface between the denture base resin and fibers was examined using scanning electron microscopy (SEM). Reinforcement with carbon or glass fibers between two abutments significantly increased the flexural strength and flexural modulus. SEM revealed relatively continuous contact between the fibers and acrylic resin. The addition of carbon or glass fibers between two abutments placed on All-on-Four provisional fixed denture base resin may be clinically effective in preventing All-on-Four denture fracture and can provide several advantages for clinical use.

Static flexural properties of hedgehog spines conditioned in coupled temperature and relative humidity environments.

PubMed

Kennedy, Emily B; Hsiung, Bor-Kai; Swift, Nathan B; Tan, Kwek-Tze

2017-11-01

Hedgehogs are agile climbers, scaling trees and plants to heights exceeding 10m while foraging insects. Hedgehog spines (a.k.a. quills) provide fall protection by absorbing shock and could offer insights for the design of lightweight, material-efficient, impact-resistant structures. There has been some study of flexural properties of hedgehog spines, but an understanding of how this keratinous biological material is affected by various temperature and relative humidity treatments, or how spine color (multicolored vs. white) affects mechanics, is lacking. To bridge this gap in the literature, we use three-point bending to analyze the effect of temperature, humidity, spine color, and their interactions on flexural strength and modulus of hedgehog spines. We also compare specific strength and stiffness of hedgehog spines to conventional engineered materials. We find hedgehog spine flexural properties can be finely tuned by modifying environmental conditioning parameters. White spines tend to be stronger and stiffer than multicolored spines. Finally, for most temperature and humidity conditioning parameters, hedgehog spines are ounce for ounce stronger than 201 stainless steel rods of the same diameter but as pliable as styrene rods with a slightly larger diameter. This unique combination of strength and elasticity makes hedgehog spines exemplary shock absorbers, and a suitable reference model for biomimicry. Copyright © 2017 Elsevier Ltd. All rights reserved.

Biaxial flexural strength of Turkom-Cera core compared to two other all-ceramic systems

PubMed Central

AL-MAKRAMANI, Bandar Mohammed Abdullah; RAZAK, Abdul Aziz Abdul; ABU-HASSAN, Mohamed Ibrahim

2010-01-01

Advances in all-ceramic systems have established predictable means of providing metal-free aesthetic and biocompatible materials. These materials must have sufficient strength to be a practical treatment alternative for the fabrication of crowns and fixed partial dentures. Objectives The aim of this study was to compare the biaxial flexural strength of three core ceramic materials. Material and methods Three groups of 10 disc-shaped specimens (16 mm diameter x 1.2 mm thickness - in accordance with ISO-6872, 1995) were made from the following ceramic materials: Turkom-Cera Fused Alumina [(Turkom-Ceramic (M) Sdn Bhd, Puchong, Selangor, Malaysia)], In-Ceram (Vita Zahnfabrik, Bad Säckingen, Baden-Württemberg, Germany) and Vitadur-N (Vita Zahnfabrik, Bad Säckingen, Baden-Württemberg, Germany), which were sintered according to the manufacturer's recommendations. The specimens were subjected to biaxial flexural strength test in a universal testing machine at a crosshead speed of 0.5 mm/min. The definitive fracture load was recorded for each specimen and the biaxial flexural strength was calculated from an equation in accordance with ISO-6872. Results The mean biaxial flexural strength values were: Turkom-Cera: 506.8±87.01 MPa, In-Ceram: 347.4±28.83 MPa and Vitadur-N: 128.7±12.72 MPa. The results were analyzed by the Levene's test and Dunnett's T3 post-hoc test (SPSS software V11.5.0 for Windows, SPSS, Chicago, IL, USA ) at a preset significance level of 5% because of unequal group variances (P<0.001). There was statistically significant difference between the three core ceramics (P<0.05). Turkom-Cera showed the highest biaxial flexural strength, followed by In-Ceram and Vitadur-N. Conclusions Turkom-Cera core had significantly higher flexural strength than In-Ceram and Vitadur-N ceramic core materials. PMID:21308292

Flexural Behavior of HPFRCC Members with Inhomogeneous Material Properties.

PubMed

Shin, Kyung-Joon; Jang, Kyu-Hyeon; Choi, Young-Cheol; Lee, Seong-Cheol

2015-04-21

In this paper, the flexural behavior of High-performance Fiber-Reinforced Cementitious Composite (HPFRCC) has been investigated, especially focusing on the localization of cracks, which significantly governs the flexural behavior of HPFRCC members. From four points bending tests with HPFRCC members, it was observed that almost evenly distributed cracks formed gradually, followed by a localized crack that determined the failure of the members. In order to investigate the effect of a localized crack on the flexural behavior of HPFRCC members, an analytical procedure has been developed with the consideration of intrinsic inhomogeneous material properties of HPFRCC such as cracking and ultimate tensile strengths. From the comparison, while the predictions with homogeneous material properties overestimated flexural strength and ductility of HPFRCC members, it was found that the analysis results considering localization effect with inhomogeneous material properties showed good agreement with the test results, not only the flexural strength and ductility but also the crack widths. The test results and the developed analysis procedure presented in this paper can be usefully applied for the prediction of flexural behaviors of HPFRCC members by considering the effect of localized cracking behavior.

[Properties and infiltration arts of machinable infiltration ceramic(MIC)].

PubMed

Yang, H; Xian, S; Liao, Y; Xue, Y; Chai, F

2000-06-01

The purpose of this study is to explore the infiltration arts of MIC and study the effects of different packing density of Al2O3 matrix on the properties of MIC. alpha-Al2O3 specimens were fabricated by pouring alpha-Al2O3 slip with different powder/liquid ratios(P/L = 3.5, 7.5, 10.5) into a mold, and subsequently pre-fired at 1160 degrees C for 6 hours to form Al2O3 matrix. The packing density of the matrices were measured. Infiltration concepts were introduced into this study by infiltrating molten mica micro-crystalline glass into the porous Al2O3 matrix at 1160 degrees C for 6 hours to form a continuous interpenetrating composite. The composite then underwent micro-crystallization by nucleating at 550 degrees C for 1 hour and crystallizing at 900 degrees C for 1 hour, which resulted in the MIC. Mechanical properties including three point flexural strength, elastic modulus, Vicker's hardness, indentation fracture toughness and Weibull's modulus of flexural strength were determined. Parameters of machinability(H/KIC)2 of MIC were calculated. XRD and SEM were employed to study its microstructure. The resulted matrices reached packing densities of 63%, 76%, 78% with P/L of 3.5, 7.5 and 10.5. The MIC attained high strength and good machinability after infiltration. Three-point flexural strength and indentation fracture toughness were 342, 431, 374 MPa and 4.05, 4.14, 5.02 MPa m1/2 for MIC with packing density of 63%, 76%, 78% separately. And parameters of machinability were 5.41, 6.84 and 7.39 respectively. Packing density of Al2O3 matrix significantly influenced the mechanical properties. Maximum properties were obtained with a matrix packing density of 75%(P/L = 7.5), with a Weibull's modulus of flexural strength of 6.8. Machinability decreased with the increase of P/L ratio. Micro-crystallizing treatment resulted in the formation of evenly distributed mica crystalline in the composite, which contributed to the high strength of this composite material. MIC is a new infiltrated ceramic with favorable strength and machinability which can satisfy the prosthodontic requirements as all ceramic crown and bridge materials, it also shows promising outlook for future developments and clinical usage.

Weibull models of fracture strengths and fatigue behavior of dental resins in flexure and shear.

PubMed

Baran, G R; McCool, J I; Paul, D; Boberick, K; Wunder, S

1998-01-01

In estimating lifetimes of dental restorative materials, it is useful to have available data on the fatigue behavior of these materials. Current efforts at estimation include several untested assumptions related to the equivalence of flaw distributions sampled by shear, tensile, and compressive stresses. Environmental influences on material properties are not accounted for, and it is unclear if fatigue limits exist. In this study, the shear and flexural strengths of three resins used as matrices in dental restorative composite materials were characterized by Weibull parameters. It was found that shear strengths were lower than flexural strengths, liquid sorption had a profound effect on characteristic strengths, and the Weibull shape parameter obtained from shear data differed for some materials from that obtained in flexure. In shear and flexural fatigue, a power law relationship applied for up to 250,000 cycles; no fatigue limits were found, and the data thus imply only one flaw population is responsible for failure. Again, liquid sorption adversely affected strength levels in most materials (decreasing shear strengths and flexural strengths by factors of 2-3) and to a greater extent than did the degree of cure or material chemistry.

Effects of heat and moisture on fiberglass composite materials in the load carrying and non-load carrying conditions

NASA Astrophysics Data System (ADS)

McClurg, Jack Albert

The objective set forth in this study was to thoroughly document the effects of heat, moisture, and loading conditions on a variety of pultruded unidirectional fiberglass reinforced composite materials. This study incorporated the use of two environmental control chambers and two water immersion tanks in order to provide the necessary range of environmental exposure conditions. A set of specially designed stainless steel loading fixtures was produced in order to introduce the factor of external loading of the specimens while exposed to the predetermined environmental condition and how that would affect the mechanical and physical properties in question. The properties of interest were the flexural strength (determined using the three-point flexural bending method), flexural modulus (determined using the three-point flexural bending method), and glass transition temperature of the material (determined using differential scanning calorimetry). Other data that was noted during the conditioning and testing of the specimens was the break type (flexural tension, compression, shear, etc...), the change in dimensions (prior to exposure vs. after exposure), and the change in weight (prior to exposure vs. after exposure). Using all of the information that was obtained from this study, a more detailed understanding of how and why fiberglass reinforced materials react the way they do when exposed to moisture and elevated temperature was drawn. This study is different from most others in that it explores the interactions of three independent variables (heat, moisture, and loading condition) on three different fiberglass reinforced composite systems (epoxy, vinylester, and polyester resin).

Effect of thermal cycling on composites reinforced with two differently sized silica-glass fibers.

PubMed

Meriç, Gökçe; Ruyter, I Eystein

2007-09-01

To evaluate the effects of thermal cycling on the flexural properties of composites reinforced with two differently sized fibers. Acid-washed, woven, fused silica-glass fibers, were heat-treated at 500 degrees C, silanized and sized with one of two sizing resins (linear poly(butyl methacrylate)) (PBMA), cross-linked poly(methyl methacrylate) (PMMA). Subsequently the fibers were incorporated into a polymer matrix. Two test groups with fibers and one control group without fibers were prepared. The flexural properties of the composite reinforced with linear PBMA-sized fibers were evaluated by 3-point bend testing before thermal cycling. The specimens from all three groups were thermally cycled in water (12,000 cycles, 5/55 degrees C, dwell time 30 s), and afterwards tested by 3-point bending. SEM micrographs were taken of the fibers and of the fractured fiber reinforced composites (FRC). The reduction of ultimate flexural strength after thermal cycling was less than 20% of that prior to thermal cycling for composites reinforced with linear PBMA-sized silica-glass fibers. The flexural strength of the composite reinforced with cross-linked PMMA-sized fibers was reduced to less than half of the initial value. This study demonstrated that thermal cycling differently influences the flexural properties of composites reinforced with different sized silica-glass fibers. The interfacial linear PBMA-sizing polymer acts as a stress-bearing component for the high interfacial stresses during thermal cycling due to the flexible structure of the linear PBMA above Tg. The cross-linked PMMA-sizing, however, acts as a rigid component and therefore causes adhesive fracture between the fibers and matrix after the fatigue process of thermal cycling and flexural fracture.

Determination of Temperature- Dependent Mechanical Properties of Carbon Composites Under Tensile and Flexural Loading

NASA Astrophysics Data System (ADS)

Chripunow, Andre; Kubisch, Aline; Ruder, Matthias; Forster, Andreas; Korber, Hannes

2014-06-01

The presented test setup utilises a custom-built furnace realising test temperatures of up to 500°C. In order to ensure always optimal test conditions the temperature cell can be exchanged depending on the mechanical tests and specimen sizes. Cells for tensile and flexural loadings had been developed. With the latter one it is possible to perform three-point-bending tests, interlaminar-shear-strength tests as well as tests to determine the interlaminar fracture toughness. In this work the effect of fibre orientation on the mechanical properties of CFRP prepreg material under tensile and flexural loads at elevated temperatures was studied. Especially the matrix dominated layups showed a rather early decay of the mechanical properties even at temperatures quite lower than Tg. An analytical model has been used to describe the temperature-dependent properties. The model shows good agreement concerning the strength whereas the proper prediction of the moduli was only possible for the matrix dominated layups.

The effect of core material, veneering porcelain, and fabrication technique on the biaxial flexural strength and weibull analysis of selected dental ceramics.

PubMed

Lin, Wei-Shao; Ercoli, Carlo; Feng, Changyong; Morton, Dean

2012-07-01

The objective of this study was to compare the effect of veneering porcelain (monolithic or bilayer specimens) and core fabrication technique (heat-pressed or CAD/CAM) on the biaxial flexural strength and Weibull modulus of leucite-reinforced and lithium-disilicate glass ceramics. In addition, the effect of veneering technique (heat-pressed or powder/liquid layering) for zirconia ceramics on the biaxial flexural strength and Weibull modulus was studied. Five ceramic core materials (IPS Empress Esthetic, IPS Empress CAD, IPS e.max Press, IPS e.max CAD, IPS e.max ZirCAD) and three corresponding veneering porcelains (IPS Empress Esthetic Veneer, IPS e.max Ceram, IPS e.max ZirPress) were selected for this study. Each core material group contained three subgroups based on the core material thickness and the presence of corresponding veneering porcelain as follows: 1.5 mm core material only (subgroup 1.5C), 0.8 mm core material only (subgroup 0.8C), and 1.5 mm core/veneer group: 0.8 mm core with 0.7 mm corresponding veneering porcelain with a powder/liquid layering technique (subgroup 0.8C-0.7VL). The ZirCAD group had one additional 1.5 mm core/veneer subgroup with 0.7 mm heat-pressed veneering porcelain (subgroup 0.8C-0.7VP). The biaxial flexural strengths were compared for each subgroup (n = 10) according to ISO standard 6872:2008 with ANOVA and Tukey's post hoc multiple comparison test (p≤ 0.05). The reliability of strength was analyzed with the Weibull distribution. For all core materials, the 1.5 mm core/veneer subgroups (0.8C-0.7VL, 0.8C-0.7VP) had significantly lower mean biaxial flexural strengths (p < 0.0001) than the other two subgroups (subgroups 1.5C and 0.8C). For the ZirCAD group, the 0.8C-0.7VL subgroup had significantly lower flexural strength (p= 0.004) than subgroup 0.8C-0.7VP. Nonetheless, both veneered ZirCAD groups showed greater flexural strength than the monolithic Empress and e.max groups, regardless of core thickness and fabrication techniques. Comparing fabrication techniques, Empress Esthetic/CAD, e.max Press/CAD had similar biaxial flexural strength (p= 0.28 for Empress pair; p= 0.87 for e.max pair); however, e.max CAD/Press groups had significantly higher flexural strength (p < 0.0001) than Empress Esthetic/CAD groups. Monolithic core specimens presented with higher Weibull modulus with all selected core materials. For the ZirCAD group, although the bilayer 0.8C-0.7VL subgroup exhibited significantly lower flexural strength, it had highest Weibull modulus than the 0.8C-0.7VP subgroup. The present study suggests that veneering porcelain onto a ceramic core material diminishes the flexural strength and the reliability of the bilayer specimens. Leucite-reinforced glass-ceramic cores have lower flexural strength than lithium-disilicate ones, while fabrication techniques (heat-pressed or CAD/CAM) and specimen thicknesses do not affect the flexural strength of all glass ceramics. Compared with the heat-pressed veneering technique, the powder/liquid veneering technique exhibited lower flexural strength but increased reliability with a higher Weibull modulus for zirconia bilayer specimens. Zirconia-veneered ceramics exhibited greater flexural strength than monolithic leucite-reinforced and lithium-disilicate ceramics regardless of zirconia veneering techniques (heat-pressed or powder/liquid technique). © 2012 by the American College of Prosthodontists.

Effect of adhesive resin flexibility on enamel fracture during metal bracket debonding: an ex vivo study.

PubMed

Kim, Young Kyung; Park, Hyo-Sang; Kim, Kyo-Han; Kwon, Tae-Yub

2015-10-01

To test the null hypothesis that neither the flexural properties of orthodontic adhesive resins nor the enamel pre-treatment methods would affect metal bracket debonding behaviours, including enamel fracture. A dimethacrylate-based resin (Transbond XT, TX) and two methyl methacrylate (MMA)-based resins (Super-Bond C&B, SB; an experimental light-cured resin, EXP) were tested. Flexural strength and flexural modulus for each resin were measured by a three-point-bending test. Metal brackets were bonded to human enamel pretreated with total-etch (TE) or self-etch adhesive using one of the three resins (a total of six groups, n = 15). After 24 hours of storage in water at 37°C, a shear bond strength (SBS) test was performed using the wire loop method. After debonding, remaining resin on the enamel surfaces and occurrence of enamel fracture were assessed. Statistical significance was set at P < 0.05. The two MMA resins exhibited substantially lower flexural strength and modulus values than the TX resin. The mean SBS values of all groups (10.15-11.09MPa) were statistically equivalent to one another (P > 0.05), except for the TE-TX group (13.51MPa, P < 0.05). The two EXP groups showed less resin remnant. Only in the two TX groups were enamel fractures observed (three cases for each group). The results were drawn only from ex vivo experiments. The hypothesis is rejected. This study suggests that a more flexible MMA resin is favourable for avoiding enamel fracture during metal bracket debonding. © The Author 2014. Published by Oxford University Press on behalf of the European Orthodontic Society. All rights reserved. For permissions, please email: journals.permissions@oup.com.

Strength degradation and lifetime prediction of dental zirconia ceramics under cyclic normal loading.

PubMed

Li, Wanzhong; Xu, Yingqiang; He, Huiming; Zhao, Haidan; Sun, Jian; Hou, Yue

2015-01-01

Clinical cases show that zirconia restoration could happen fracture by accident under overloading after using a period of time. The purpose of this study is to research mechanical behavior and predict lifetime of dental zirconia ceramics under cyclic normal contact loading with experiments. Cyclic normal contact loading test and three point bending test are carried on specimens made of two brands of dental zirconia ceramic to obtain flexure strength and damage degree after different number of loading cycles. By means of damage mechanics model, damage degree under different number of contact loading cycles are calculated according to flexure strength, and verified by SEM photographs of cross section morphology of zirconia ceramics specimen phenomenologically. Relation curve of damage degree and number of cycles is fitted by polynomial fitting, then the number of loading cycles can be concluded when the specimen is complete damage. Strength degradation of two brands dental zirconia ceramics are researched in vitro, and prediction method of contact fatigue lifetime is established.

Evaluation of Mechanical Properties of Glass Fiber Posts Subjected to Laser Surface Treatments.

PubMed

Barbosa Siqueira, Carolina; Spadini de Faria, Natália; Raucci-Neto, Walter; Colucci, Vivian; Alves Gomes, Erica

2016-10-01

The aim of this study was to evaluate the influence of laser irradiation on flexural strength, elastic modulus, and surface roughness and morphology of glass fiber posts (GFPs). Laser treatment of GFPs has been introduced to improve its adhesion properties. A total of 40 GFPs were divided into 4 groups according to the irradiation protocol: GC-no irradiation, GYAG-irradiation with erbium:yttrium-aluminum-garnet [Er:YAG], GCR-irradiation with erbium, chromium:yttrium-scandium-gallium-garnet (Er,Cr:YSGG), and GDI-irradiation with diode laser. The GFP roughness and morphology were evaluated through laser confocal microscopy before and after surface treatment. Three-point bending flexural test measured flexural strength and elastic modulus. Data about elastic modulus and flexural strength were subjected to one-way ANOVA and Bonferroni test (p < 0.05). The effect of roughness was evaluated using the linear mixed effects model and Bonferroni test (p < 0.05). Laser treatment changed surface roughness in the groups GCR (p = 0.000) and GDI (p = 0.007). The mean flexural strength in GYAG (995.22 MPa) was similar to that in GC (980.48 MPa) (p = 1.000) but different from that in GCR (746.83 MPa) and that in GDI (691.34 MPa) (p = 0.000). No difference was found between the groups GCR and GDI (p = 0.86). For elastic modulus: GYAG (24.47 GPa) was similar to GC (25.92 GPa) (p = 1.000) but different from GCR (19.88 GPa) (p = 0.002) and GDI (17.20 GPa) (p = 0.000). The different types of lasers, especially Er,Cr:YSGG and 980 ηm diode, influenced the mechanical properties of GFPs.

Effect of Two Polishing Systems on Surface Roughness, Topography, and Flexural Strength of a Monolithic Lithium Disilicate Ceramic.

PubMed

Mohammadibassir, Mahshid; Rezvani, Mohammad Bagher; Golzari, Hossein; Moravej Salehi, Elham; Fahimi, Mohammad Amin; Kharazi Fard, Mohammad Javad

2017-03-08

To evaluate the effect of overglazing and two polishing procedures on flexural strength and quality and quantity of surface roughness of a monolithic lithium disilicate ceramic computer-aided design (CAD) after grinding. This in vitro study was conducted on 52 partially crystalized bar-shaped specimens (16 × 4 × 1.6 mm) of monolithic lithium disilicate ceramic. The specimens were wet polished with 600-, 800-, and 1200-grit silicon carbide papers for 15 seconds using a grinding/polishing machine at a speed of 300 rpm. Then, the specimens were crystalized and glaze-fired in one step simultaneously and randomly divided into four groups of 13: (I) Glazing group (control); (II) Grinding-glazing group, subjected to grinding with red band finishing diamond bur (46 μm) followed by glazing; (III) Grinding-D+Z group, subjected to grinding and then polishing by coarse, medium, and fine diamond rubber points (D+Z); and (IV) Grinding-OptraFine group, subjected to grinding and then polishing with a two-step diamond rubber polishing system followed by a final polishing step with an OptraFine HP brush and diamond polishing paste. The surface roughness (Ra and Rz) values (μm) were measured by a profilometer, and the mean values were compared using one-way ANOVA and Tamhane's test (post hoc comparison). One specimen of each group was evaluated under a scanning electron microscope (SEM) for surface topography. The three-point flexural strength values of the bars were measured using a universal testing machine at a 0.5 mm/min crosshead speed and recorded. The data were analyzed using one-way ANOVA and Tamhane's test (α = 0.05). Statistically significant differences were noted among the experimental groups for Ra, Rz (p < 0.0001), and flexural strength values (p < 0.009). The lowest Ra and Rz values were found in the grinding-OptraFine group (0.465 ± 0.153), which were significantly lower than those in glazing (p < 0.03) and grinding-glazing (p < 0.001) groups. The Ra and Rz values were not significantly different between the two polishing systems (p = 0.23 and p = 0.25, respectively). The highest flexural strength was found in the glazing group (283.350 ± 49.854 MPa) without significant differences compared to grinding-glazing (p = 0.98) and grinding-OptraFine groups (p = 0.86). The lowest flexural strength was found in grinding-D+Z group (225.070 ± 17.299), which was significantly different from the value in glazing (p < 0.03) and grinding-glazing (p < 0.04) groups. SEM analysis of polished surfaces revealed regular morphology with some striations. The OptraFine system created smoother and more uniform surfaces in terms of quantity (p < 0.03 for Ra, p < 0.01 for Rz) and quality of roughness compared to glazing. The flexural strength of lithium disilicate ceramic after polishing with the OptraFine system was similar to that after glazing (p = 0.86). Despite similar surface roughness after polishing with the two systems, the D+Z system reduced the flexural strength of ceramic (p < 0.03). © 2017 by the American College of Prosthodontists.

Effect of a self-adhesive coating on the load-bearing capacity of tooth-coloured restorative materials.

PubMed

Bagheri, R; Palamara, Jea; Mese, A; Manton, D J

2017-03-01

The aim of this study was to compare the flexural strength and Vickers hardness of tooth-coloured restorative materials with and without applying a self-adhesive coating for up to 6 months. Specimens were prepared from three resin composites (RC), two resin-modified glass-ionomer cements (RM-GIC) and two conventional glass-ionomer cements (CGIC). All materials were tested both with and without applying G-Coat Plus (GCP). Specimens were conditioned in 37 °C distilled deionized water for 24 h, and 1, 3 and 6 months. The specimens were strength tested using a four-point bend test jig in a universal testing machine. The broken specimen's halves were used for Vickers hardness testing. Representative specimens were examined under an environmental scanning electron microscope. Data analysis showed that regardless of time and materials, generally the surface coating was associated with a significant increase in the flexural strength of the materials. Applying the GCP decreased the hardness of almost all materials significantly (P < 0.05) and effect of time intervals on hardness was material dependent. The load-bearing capacity of the restorative materials was affected by applying self-adhesive coating and ageing. The CGIC had significantly higher hardness but lower flexural strength than the RM-GIC and RC. © 2016 Australian Dental Association.

Effects of porcelain thickness on the flexural strength and crack propagation in a bilayered zirconia system.

PubMed

Figueiredo, Viviane Maria Gonçalves de; Pereira, Sarina Maciel Braga; Bressiani, Eduardo; Valera, Márcia Carneiro; Bottino, Marco Antônio; Zhang, Yu; Melo, Renata Marques de

2017-01-01

This study evaluated the influence of porcelain (VM9, VITA Zahnfabrik, Germany) thickness on the flexural strength and crack propagation in bilayered zirconia systems (YZ, VITA Zahnfabrik, Germany). Thirty zirconia bars (20.0x4.0x1.0 mm) and six zirconia blocks (12.0x7.5x1.2 mm) were prepared and veneered with porcelain with different thickness: 1 mm, 2 mm, or 3 mm. The bars of each experimental group (n=10) were subjected to four-point flexural strength testing. In each ceramic block, a Vickers indentation was created under a load of 10 kgf for 10 seconds, for the propagation of cracks. The results of flexural strength were evaluated by One-way ANOVA and Tukey's test, with a significance level of 5%. The factor "thickness of the porcelain" was statistically significant (p=0.001) and the l-mm group presented the highest values of flexural strength. The cracks were predominant among the bending specimens with 1 and 2 mm of porcelain, and catastrophic failures were found in 50% of 3-mm-thick porcelain. After the indentation of blocks, the most severe defects were observed in blocks with 3-mm-thick porcelain. The smallest (1 mm) thickness of porcelain on the zirconia infrastructure presented higher values of flexural strength. Better resistance to defect propagation was observed near the porcelain/ zirconia interface for all groups. Higher flexural strength was found for a thinner porcelain layer in a bilayered zirconia system. The damage caused by a Vickers indentation near and far the interface with the zirconia shows that the stress profiles are different.

Effects of porcelain thickness on the flexural strength and crack propagation in a bilayered zirconia system

PubMed Central

de Figueiredo, Viviane Maria Gonçalves; Pereira, Sarina Maciel Braga; Bressiani, Eduardo; Valera, Márcia Carneiro; Bottino, Marco Antônio; Zhang, Yu; de Melo, Renata Marques

2017-01-01

Abstract Objective: This study evaluated the influence of porcelain (VM9, VITA Zahnfabrik, Germany) thickness on the flexural strength and crack propagation in bilayered zirconia systems (YZ, VITA Zahnfabrik, Germany). Material and Methods: Thirty zirconia bars (20.0x4.0x1.0 mm) and six zirconia blocks (12.0x7.5x1.2 mm) were prepared and veneered with porcelain with different thickness: 1 mm, 2 mm, or 3 mm. The bars of each experimental group (n=10) were subjected to four-point flexural strength testing. In each ceramic block, a Vickers indentation was created under a load of 10 kgf for 10 seconds, for the propagation of cracks. Results: The results of flexural strength were evaluated by One-way ANOVA and Tukey's test, with a significance level of 5%. The factor “thickness of the porcelain” was statistically significant (p=0.001) and the l-mm group presented the highest values of flexural strength. The cracks were predominant among the bending specimens with 1 and 2 mm of porcelain, and catastrophic failures were found in 50% of 3-mm-thick porcelain. After the indentation of blocks, the most severe defects were observed in blocks with 3-mm-thick porcelain. Conclusion: The smallest (1 mm) thickness of porcelain on the zirconia infrastructure presented higher values of flexural strength. Better resistance to defect propagation was observed near the porcelain/ zirconia interface for all groups. Higher flexural strength was found for a thinner porcelain layer in a bilayered zirconia system. The damage caused by a Vickers indentation near and far the interface with the zirconia shows that the stress profiles are different. PMID:29069155

Reliability Analysis of Uniaxially Ground Brittle Materials

NASA Technical Reports Server (NTRS)

Salem, Jonathan A.; Nemeth, Noel N.; Powers, Lynn M.; Choi, Sung R.

1995-01-01

The fast fracture strength distribution of uniaxially ground, alpha silicon carbide was investigated as a function of grinding angle relative to the principal stress direction in flexure. Both as-ground and ground/annealed surfaces were investigated. The resulting flexural strength distributions were used to verify reliability models and predict the strength distribution of larger plate specimens tested in biaxial flexure. Complete fractography was done on the specimens. Failures occurred from agglomerates, machining cracks, or hybrid flaws that consisted of a machining crack located at a processing agglomerate. Annealing eliminated failures due to machining damage. Reliability analyses were performed using two and three parameter Weibull and Batdorf methodologies. The Weibull size effect was demonstrated for machining flaws. Mixed mode reliability models reasonably predicted the strength distributions of uniaxial flexure and biaxial plate specimens.

Influence of incorporation of ZrO2 nanoparticles on the repair strength of polymethyl methacrylate denture bases

PubMed Central

Gad, Mohammed M; Rahoma, Ahmed; Al-Thobity, Ahmad M; ArRejaie, Aws S

2016-01-01

Background Repeated fracture of the denture base is a common problem in prosthodontics, and it represents a nuisance and a time sink for the clinician. Therefore, the possibility of increasing repair strength using new reinforcement materials is of great interest to prosthodontists. Aim of the study This study aimed to evaluate the effects of incorporation of zirconia nanoparticles (nano-ZrO2) on the flexural strength and impact strength of repaired polymethyl methacrylate (PMMA) denture bases. Materials and methods One hundred eighty specimens of heat-polymerized acrylic resin were fabricated (90 for each test) and divided into three main groups: one control group (intact specimens) and two groups divided according to surface design (45° bevels and butt joints), in which specimens were prepared in pairs to create 2.5 mm gaps. Nano-ZrO2 was added to repair resin in 2.5 wt%, 5 wt%, and 7.5 wt% concentrations of acrylic powder. A three-point bending test was used to measure flexural strength, and a Charpy-type test was used to measure impact strength. Scanning electron microscopy was used to analyze the fracture surfaces and nano-ZrO2 distribution. The results were analyzed with a paired sample t-test and an unpaired t-test, with a P-value of ≤0.05 being significant. Results Incorporation of nano-ZrO2 into the repair resin significantly increased flexural strength (P<0.05). The highest value was found in the bevel group reinforced with 7.5% nano-ZrO2, whereas the lowest value was found in the butt group reinforced with 2.5% nano-ZrO2. The impact strength values of all repaired groups were significantly lower than those of the control group (P<0.05). Among repaired groups, the higher impact strength value was seen in the butt group reinforced with 2.5% nano-ZrO2. The bevel joint demonstrated mainly cohesive failure, whereas the butt joint demonstrated mainly adhesive failure. Conclusion Incorporation of nano-ZrO2 into the repair resin improved the flexural strength of repaired denture bases, whereas it decreased impact strength, especially with high nano-ZrO2 concentrations. PMID:27822041

Study on Microstructures and Properties of Porous TiC Ceramics Fabricated by Powder Metallurgy

NASA Astrophysics Data System (ADS)

Ma, Yana; Bao, Chonggao; Han, Longhao; Chen, Jie

2017-02-01

Powder metallurgy process was used to fabricate porous titanium carbide (TiC) ceramics, in which TiC powders were taken as the raw materials, nickel was used as the metallic binder and urea was the space-holder. Microstructure, composition and phase of porous TiC ceramics were characterized by scanning electron microscopy (SEM) and x-ray diffraction (XRD). Flexure strength of the porous TiC ceramics was tested by a three-point bending method. The results show that macropores and micropores coexist in the prepared porous TiC ceramics. Moreover, the pore number, size and distribution in porous TiC ceramics can be controlled on demand. Particularly, the factors such as the number or size of space-holder, compacting pressure and Ni content have significant effect on the porosity and flexure strength.

Mechanical properties of kenaf composites using dynamic mechanical analysis

NASA Astrophysics Data System (ADS)

Loveless, Thomas A.

Natural fibers show potential to replace glass fibers in thermoset and thermoplastic composites. Kenaf is a bast-type fiber with high specific strength and great potential to compete with glass fibers. In this research kenaf/epoxy composites were analyzed using Dynamic Mechanical Analysis (DMA). A three-point bend apparatus was used in the DMA testing. The samples were tested at 1 hertz, at a displacement of 10 ?m, and at room temperature. The fiber volume content of the kenaf was varied from 20% - 40% in 5% increments. Ten samples of each fiber volume fraction were manufactured and tested. The flexural storage modulus, the flexural loss modulus, and the loss factor were reported. Generally as the fiber volume fraction of kenaf increased, the flexural storage and flexural loss modulus increased. The loss factor remained relatively constant with increasing fiber volume fraction. Woven and chopped fiberglass/epoxy composites were manufactured and tested to be compared with the kenaf/epoxy composites. Both of the fiberglass/epoxy composites reported higher flexural storage and flexural loss modulus values. The kenaf/epoxy composites reported higher loss factor values. The specific flexural storage and specific flexural loss modulus were calculated for both the fiberglass and kenaf fiber composites. Even though the kenaf composites reported a lower density, the fiberglass composites reported higher specific mechanical properties.

Physical properties of self-, dual-, and light-cured direct core materials.

PubMed

Rüttermann, Stefan; Alberts, Ian; Raab, Wolfgang H M; Janda, Ralf R

2011-08-01

The objective of this study is to evaluate flexural strength, flexural modulus, compressive strength, curing temperature, curing depth, volumetric shrinkage, water sorption, and hygroscopic expansion of two self-, three dual-, and three light-curing resin-based core materials. Flexural strength and water sorption were measured according to ISO 4049, flexural modulus, compressive strength, curing temperature, and curing depth according to well-proven, literature-known methods, and the volumetric behavior was determined by the Archimedes' principle. ANOVA was calculated to find differences between the materials' properties, and correlation of water sorption and hygroscopic expansion was analysed according to Pearson (p < 0.05). Clearfil Photo Core demonstrated the highest flexural strength (125 ± 12 MPa) and curing depth (15.2 ± 0.1 mm) and had the highest flexural modulus (≈12.6 ± 1.2 GPa) concertedly with Multicore HB. The best compressive strength was measured for Voco Rebilda SC and Clearfil DC Core Auto (≈260 ± 10 MPa). Encore SuperCure Contrast had the lowest water sorption (11.8 ± 3.3 µg mm(-3)) and hygroscopic expansion (0.0 ± 0.2 vol.%). Clearfil Photo Core and Encore SuperCure Contrast demonstrated the lowest shrinkage (≈2.1 ± 0.1 vol.%). Water sorption and hygroscopic expansion had a very strong positive correlation. The investigated core materials significantly differed in the tested properties. The performance of the materials depended on their formulation, as well as on the respective curing process.

Laboratory Characterization of Cemented Rock Fill for Underhand Cut and Fill Method of Mining

NASA Astrophysics Data System (ADS)

Kumar, Dinesh; Singh, Upendra Kumar; Singh, Gauri Shankar Prasad

2016-10-01

Backfilling with controlled specifications is employed for improved ground support and pillar recovery in underground metalliferous mine workings. This paper reports the results of a laboratory study to characterise various mechanical properties of cemented rock fill (CRF) formulations for different compaction levels and cement content percentage for use in underhand cut and fill method of mining. Laboratory test set ups and procedures have been described for conducting compressive and bending tests of CRF block samples. A three dimensional numerical modelling study has also been carried out to overcome the limitations arising due to non-standard dimension of test blocks used in flexural loading test and the test setup devised for this purpose. Based on these studies, specific relations have been established between the compressive and the flexural properties of the CRF. The flexural strength of the wire mesh reinforced CRF is also correlated with its residual strength and the Young's modulus of elasticity under flexural loading condition. The test results of flexural strength, residual flexural strength and modulus show almost linear relations with cement content in CRF. The compressive strength of the CRF block samples is estimated as seven times the flexural strength whereas the compressive modulus is four times the flexural modulus. It has been found that the strengths of CRF of low compaction and no compaction are 75 and 60 % respectively to that of the medium compaction CRF. The relation between the strength and the unit weight of CRF as obtained in this study is significantly important for design and quality control of CRF during its large scale application in underhand cut and fill stopes.

Mechanical properties of commercial high strength ceramic core materials.

PubMed

Rizkalla, A S; Jones, D W

2004-02-01

The objective of the present study is to evaluate and compare the flexural strength, dynamic elastic moduli and true hardness (H(o)) values of commercial Vita In-Ceram alumina core and Vita In-Ceram matrix glass with the standard aluminous porcelain (Hi-Ceram and Vitadur), Vitadur N and Dicor glass and glass-ceramic. The flexural strength was evaluated (n=5) using 3-point loading and a servo hydraulic Instron testing machine at a cross head speed of 0.5 mm/min. The density of the specimens (n=3) was measured by means of the water displacement technique. Dynamic Young's shear and bulk moduli and Poisson's ratio (n=3) were measured using a non-destructive ultrasonic technique using 10 MHz lithium niobate crystals. The true hardness (n=3) was measured using a Knoop indenter and the fracture toughness (n=3) was determined using a Vickers indenter and a Tukon hardness tester. Statistical analysis of the data was conducted using ANOVA and a Student-Newman-Keuls (SNK) rank order multiple comparative test. The SNK rank order test analysis of the mean flexural strength was able to separate five commercial core materials into three significant groups at p=0.05. Vita In-Ceram alumina and IPS Empress 2 exhibited significantly higher flexural strength than aluminous porcelains and IPS Empress at p=0.05. The dynamic elastic moduli and true hardness of Vita In-Ceram alumina core were significantly higher than the rest of the commercial ceramic core materials at p=0.05. The ultrasonic test method is a valuable mechanical characterization tool and was able to statistically discriminate between the chemical and structural differences within dental ceramic materials. Significant correlation was obtained between the dynamic Young's modulus and true hardness, p=0.05.

Slow Crack Growth Behavior and Life/Reliability Analysis of 96 wt % Alumina at Ambient Temperature With Various Specimen/Loading Configurations

NASA Technical Reports Server (NTRS)

Choi, Sung R.; Powers, Lynn M.; Nemeth, Noel N.

2000-01-01

Extensive constant stress-rate testing for 96 wt % alumina was conducted in room-temperature distilled water using four different specimen/loading configurations: rectangular beam test specimens under four-point uniaxial flexure, square plate test specimens in ring-on-ring biaxial flexure, square plate test specimens in ball-on-ring biaxial flexure, and dog-boned tensile test specimens in pure tension. The slow crack growth (SCG) parameter n was almost independent of specimen/loading configurations, in either four-point uniaxial flexure, ring-on-ring biaxial flexure, ball-on-ring biaxial flexure, or pure tension, ranging from n = 35 to 47 with an average value of n = 41.1 +/- 4.5. The prediction of fatigue strength/reliability based on the four-point uniaxial flexure data by using the CARES/Life design code as well as a simple PIA model was in good agreement with both the ring-on-ring biaxial and the ball-on-ring biaxial flexure data. A poor prediction using the PIA model was observed for the dog-boned tensile test specimens, presumably due to different flaw population involved in the tensile test specimens.

Analysis of Ninety Degree Flexure Tests for Characterization of Composite Transverse Tensile Strength

NASA Technical Reports Server (NTRS)

OBrien, T. Kevin; Krueger, Ronald

2001-01-01

Finite element (FE) analysis was performed on 3-point and 4-point bending test configurations of ninety degree oriented glass-epoxy and graphite-epoxy composite beams to identify deviations from beam theory predictions. Both linear and geometric non-linear analyses were performed using the ABAQUS finite element code. The 3-point and 4-point bending specimens were first modeled with two-dimensional elements. Three-dimensional finite element models were then performed for selected 4-point bending configurations to study the stress distribution across the width of the specimens and compare the results to the stresses computed from two-dimensional plane strain and plane stress analyses and the stresses from beam theory. Stresses for all configurations were analyzed at load levels corresponding to the measured transverse tensile strength of the material.

Carbon fiber reinforced root canal posts. Mechanical and cytotoxic properties.

PubMed

Torbjörner, A; Karlsson, S; Syverud, M; Hensten-Pettersen, A

1996-01-01

The aim of this study was to compare the mechanical properties of a prefabricated root canal post made of carbon fiber reinforced composites (CFRC) with metal posts and to assess the cytotoxic effects elicited. Flexural modulus and ultimate flexural strength was determined by 3 point loading after CRFC posts had been stored either dry or in water. The bending test was carried out with and without preceding thermocycling of the CFRC posts. The cytotoxicity was evaluated by an agar overlay method after dry and wet storage. The values of flexural modulus and ultimate flexural strength were for dry stored CFRC post 82 +/- 6 GPa and 1154 +/- 65 MPa respectively. The flexural values decreased significantly after water storage and after thermocycling. No cytotoxic effects were observed adjacent to any CFRC post. Although fiber reinforced composites may have the potential to replace metals in many clinical situations, additional research is needed to ensure a satisfying life-span.

The relationship between compressive strength and flexural strength of pavement geopolymer grouting material

NASA Astrophysics Data System (ADS)

Zhang, L.; Han, X. X.; Ge, J.; Wang, C. H.

2018-01-01

To determine the relationship between compressive strength and flexural strength of pavement geopolymer grouting material, 20 groups of geopolymer grouting materials were prepared, the compressive strength and flexural strength were determined by mechanical properties test. On the basis of excluding the abnormal values through boxplot, the results show that, the compressive strength test results were normal, but there were two mild outliers in 7days flexural strength test. The compressive strength and flexural strength were linearly fitted by SPSS, six regression models were obtained by linear fitting of compressive strength and flexural strength. The linear relationship between compressive strength and flexural strength can be better expressed by the cubic curve model, and the correlation coefficient was 0.842.

Effect of stacking angles on mechanical properties and damage propagation of plain woven carbon fiber laminates

NASA Astrophysics Data System (ADS)

Zhuang, Weimin; Ao, Wenhong

2018-03-01

Damage propagation induced failure is a predominant damage mechanism. This study is aimed at assessing the damage state and damage propagation induced failure with different stacking angles, of woven carbon fiber/epoxy laminates subjected to quasi-static tensile and bending load. Different stages of damage processing and damage behavior under the bending load are investigated by Scanning Electron Microscopy (SEM). The woven carbon fiber/epoxy laminates which are stacked at six different angles (0°, 15°, 30°, 45°, 60°, 75°) with eight plies have been analyzed: [0]8, [15]8, [30]8, [45]8, [60]8, [75]8. Three-point bending test and quasi-static tensile test are used in validating the woven carbon fiber/epoxy laminates’ mechanical properties. Furthermore, the damage propagation and failure modes observed under flexural loading is correlated with flexural force and load-displacement behaviour respectively for the laminates. The experimental results have indicated that [45]8 laminate exhibits the best flexural performance in terms of energy absorption duo to its pseudo-ductile behaviour but the tensile strength and flexural strength drastically decreased compared to [0]8 laminate. Finally, SEM micrographs of specimens and fracture surfaces are used to reveal the different types of damage of the laminates with different stacking angles.

Repair of heat damaged reinforced concrete slab with High Strength Fibre Reinforced Concrete materials

NASA Astrophysics Data System (ADS)

Ain Hamiruddin, Nur; Razak, Rafiza Abd; Muhammad, Khairunnisa; Zahid, Muhd Zulham Affendi Mohd

2018-04-01

The purpose of this study is to investigate the flexural behaviour of heat damaged reinforced concrete (RC) slab by using High Strength Fibre Reinforced Concrete (HSFRC) as repair materials. The slab samples consist of twelve one-way columns heated at 200 ° C, 400 ° C and 600 ° C for 120 minutes. The thickness of the HSFRC layer used to heat damaged slab samples is 40 mm thick. Two distinct curing methods were implement during this study: i.e. normal curing (standard room temperature 26°C) and heat curing (temperature of 90°C for 48 hours). The center-point loading flexural strength test based on ASTM C 293 were referred to examine the flexural strength of the slab samples other than evaluated the mechanical properties of repaired samples (i.e. flexural strength, secant stiffness, toughness and ductility). The HSFRC's results showed that compressive strength at 28 days was 88.66 MPa. Whereas the flexural strength of heat damage repaired samples that exposed to 200°C (R200), 400°C (RNC400) and 400°C (RHC400) were gained by about 3.06% (34.93 MPa), 14.47% (38.79 MPa) and 30.95% (44.38 MPa) respectively, contrasted to the control sample (CS) which is 33.89 MPa. However, heat damage for non-repaired samples that exposed to 200 ° C (NR200) and 400°C (NR400) decline by about 0.77% (33.63 MPa) and 8.13% (31.14 MPa) respectively. Therefore, the utilized of HSFRC as repair materials can improve the flexural strength than control sample (CS). This is clearly indicate that HSFRC can enhance the mechanical properties of heat damaged reinforced concrete (RC) slab which can illustrate that the results of flexural behaviour reflected the superiority by using HSFRC as repair materials.

Deformation and flexural properties of denture base polymer reinforced with glass fiber sheet.

PubMed

Kanie, Takahito; Arikawa, Hiroyuki; Fujii, Koichi; Ban, Seiji

2005-09-01

The purpose of this study was to investigate the deformation and flexural properties of acrylic and urethane polymers reinforced with glass fiber sheet. Four types of specimen--self-curing resin plate (R), light-curing oligomer plate containing a reinforcement (GO), and self-curing resin plate containing a reinforcement on one (GR) or both (GRG) sides--were prepared with three thicknesses: 1.5, 2.4, and 3.0 mm. Gaps between polymerized test specimen and a standard metal plate were measured at the corner (C), middle of the long sides (LS), and middle of the short sides (SS). The gaps for R were 0-2.0 microm. GO and GR markedly deformed at Points C, LS, and SS, and the degree of deformation increased as GO became thinner. Flexural strength was significantly increased by the reinforcement (p < 0.05). The flexural moduli of 3.0-mm thick R, GO, and GR were significantly smaller than that of 1.5-mm thick specimens.

Effect of metal chloride solutions on coloration and biaxial flexural strength of yttria-stabilized zirconia

NASA Astrophysics Data System (ADS)

Oh, Gye-Jeong; Lee, Kwangmin; Lee, Doh-Jae; Lim, Hyun-Pil; Yun, Kwi-Dug; Ban, Jae-Sam; Lee, Kyung-Ku; Fisher, John G.; Park, Sang-Won

2012-10-01

The effect of three kinds of transition metal dopants on the color and biaxial flexural strength of zirconia ceramics for dental applications was evaluated. Presintered zirconia discs were colored through immersion in aqueous chromium, molybdenum and vanadium chloride solutions and then sintered at 1450 °C. The color of the doped specimens was measured using a digital spectrophotometer. For biaxial flexural strength measurements, specimens infiltrated with 0.3 wt% of each aqueous chloride solution were used. Uncolored discs were used as a control. Zirconia specimens infiltrated with chromium, molybdenum and vanadium chloride solutions were dark brown, light yellow and dark yellow, respectively. CIE L*, a*, and b* values of all the chromium-doped specimens and the specimens infiltrated with 0.1 wt% molybdenum chloride solution were in the range of values for natural teeth. The biaxial flexural strengths of the three kinds of metal chloride groups were similar to the uncolored group. These results suggest that chromium and molybdenum dopants can be used as colorants to fabricate tooth colored zirconia ceramic restorations.

[Influence on mechanical properties and microstructure of nano-zirconia toughened alumina ceramics with nano-zirconia content].

PubMed

Wang, Guang-Kui; Kang, Hong; Bao, Guang-Jie; Lv, Jin-Jun; Gao, Fei

2006-10-01

To investigate the mechanical properties and microstructure of nano -zirconia toughened alumina ceramics with variety of nano-zirconia content in centrifugal infiltrate casting processing of dental all-ceramic. Composite powder with different ethanol-water ratio, obtained serosity from ball milling and centrifugal infiltrate cast processing of green, then sintered at 1 450 degrees C for 8 h. The physical and mechanical properties of the sintered sample after milling and polishing were tested. Microstructures of the surface and fracture of the sintered sample were investigated by SEM. The experimental results showed that there had statistical significience (P < 0.01) on static three-point flexure strength and Vickers Hardness in three kinds of different nano-zirconia content sintered sample. Fracture toughness of 20% group was different from other two groups, while 10% group had not difference from 30% group (P < 0.05). The mechanical properties of this ceramic with 20% nano-zirconia was the best of the three, the static three-point flexure strength was (433 +/- 19) MPa and fracture toughness was (7.50 +/- 0.56) MPa x min 1/2. The intra/inter structure, fracture of intragranular and intergranular on the surface and fracture of sintered sample in microstrucre was also found. Intra/inter structure has strengthen toughness in ceramics. It has better toughness with 20% nano-zirconia, is suitable dental all-ceramic restoratives.

Improved Strength and Toughness of Carbon Woven Fabric Composites with Functionalized MWCNTs

PubMed Central

Soliman, Eslam; Kandil, Usama; Reda Taha, Mahmoud

2014-01-01

This investigation examines the role of carboxyl functionalized multi-walled carbon nanotubes (COOH-MWCNTs) in the on- and off-axis flexure and the shear responses of thin carbon woven fabric composite plates. The chemically functionalized COOH-MWCNTs were used to fabricate epoxy nanocomposites and, subsequently, carbon woven fabric plates to be tested on flexure and shear. In addition to the neat epoxy, three loadings of COOH-MWCNTs were examined: 0.5 wt%, 1.0 wt% and 1.5 wt% of epoxy. While no significant statistical difference in the flexure response of the on-axis specimens was observed, significant increases in the flexure strength, modulus and toughness of the off-axis specimens were observed. The average increase in flexure strength and flexure modulus with the addition of 1.5 wt% COOH-MWCNTs improved by 28% and 19%, respectively. Finite element modeling is used to demonstrate fiber domination in on-axis flexure behavior and matrix domination in off-axis flexure behavior. Furthermore, the 1.5 wt% COOH-MWCNTs increased the toughness of carbon woven composites tested on shear by 33%. Microstructural investigation using Fourier Transform Infrared Spectroscopy (FTIR) proves the existence of chemical bonds between the COOH-MWCNTs and the epoxy matrix. PMID:28788698

Reinforcing effects of different fibers on denture base resin based on the fiber type, concentration, and combination.

PubMed

Yu, Sang-Hui; Lee, Yoon; Oh, Seunghan; Cho, Hye-Won; Oda, Yutaka; Bae, Ji-Myung

2012-01-01

The aim of this study was to evaluate the reinforcing effects of three types of fibers at various concentrations and in different combinations on flexural properties of denture base resin. Glass (GL), polyaromatic polyamide (PA) and ultra-high molecular weight polyethylene (PE) fibers were added to heat-polymerized denture base resin with volume concentrations of 2.6%, 5.3%, and 7.9%, respectively. In addition, hybrid fiber-reinforced composite (FRC) combined with either two or three types of fibers were fabricated. The flexural strength, modulus and toughness of each group were measured with a universal testing machine at a crosshead speed of 5 mm/min. In the single fiber-reinforced composite groups, the 5.3% GL and 7.9% GL had the highest flexural strength and modulus; 5.3% PE was had the highest toughness. Hybrid FRC such as GL/PE, which showed the highest toughness and the flexural strength, was considered to be useful in preventing denture fractures clinically.

Flexural strength and failure modes of layered ceramic structures.

PubMed

Borba, Márcia; de Araújo, Maico D; de Lima, Erick; Yoshimura, Humberto N; Cesar, Paulo F; Griggs, Jason A; Della Bona, Alvaro

2011-12-01

To evaluate the effect of the specimen design on the flexural strength (σ(f)) and failure mode of ceramic structures, testing the hypothesis that the ceramic material under tension controls the mechanical performance of the structure. Three ceramics used as framework materials for fixed partial dentures (YZ--Vita In-Ceram YZ; IZ--Vita In-Ceram Zirconia; AL--Vita In-Ceram AL) and two veneering porcelains (VM7 and VM9) were studied. Bar-shaped specimens were produced in three different designs (n=10): monolithic, two layers (porcelain-framework) and three layers (TRI) (porcelain-framework-porcelain). Specimens were tested for three-point flexural strength at 1MPa/s in 37°C artificial saliva. For bi-layered design, the specimens were tested in both conditions: with porcelain (PT) or framework ceramic (FT) layer under tension. Fracture surfaces were analyzed using stereomicroscope and scanning electron microscopy (SEM). Young's modulus (E) and Poisson's ratio (ν) were determined using ultrasonic pulse-echo method. Results were statistically analyzed by Kruskal-Wallis and Student-Newman-Keuls tests. Except for VM7 and VM9, significant differences were observed for E values among the materials. YZ showed the highest ν value followed by IZ and AL. YZ presented the highest σ(f). There was no statistical difference in the σ(f) value between IZ and IZ-FT and between AL and AL-FT. σ(f) values for YZ-PT, IZ-PT, IZ-TRI, AL-PT, AL-TRI were similar to the results obtained for VM7 and VM9. Two types of fracture mode were identified: total and partial failure. The mechanical performance of the specimens was determined by the material under tension during testing, confirming the study hypothesis. Copyright © 2011 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Comparative Evaluation of Flexural Strength of Provisional Crown and Bridge Materials-An Invitro Study

PubMed Central

Garg, Sandeep

2016-01-01

Introduction Provisional restorations serve a key role as a functional and esthetic try-in for the design of the final prosthesis. During selection of materials for this restoration, clinicians must consider physical properties, ease of handling, cost and patient satisfaction and approval. Aim To evaluate and compare the flexural strength of provisional crown and bridge materials available commercially. Materials and Methods This in-vitro study was done to compare the flexural strength of six temporary crown and bridge materials available commercially at 24 hours, 8 days and after repair. Three poly methyl methacrylate based materials (DPI, SC10 and Trulon) and three bis-acrylic based composite resins (Protemp, Cooltemp and Luxatemp) were selected. A total of 72 specimens of dimensions 64mm×10mm×2.5mm were prepared from these materials (12 from each material) and divided into two groups (n=36). Specimens were stored in artificial saliva and were fractured after 24 hours and 8 days using Universal Testing Machine. The fractured samples from the 8 days study were then subjected to repair. A uniform space of 2mm and a 450 bevel was maintained for all the repaired samples for better distribution of forces. Flexural strength of these repaired samples was recorded using the same machine. Results were recorded and statistically analysed by one-way Anova and Post hoc tests. Result: Results revealed that there was decrease in flexural strength for all the materials tested from 24 hours to 8 days, though flexural strength between poly methyl methacrylate and bis-acrylic resins was similar at 24 hours and 8 days time interval. A substantial decrease was noticed in the strength of bis-acrylic composite resins after repair. Conclusion From the current study it can be suggested that though there is decrease in flexural strength for all the materials from 24 hours to 8 days, both can be used to fabricate the provisional restorations. However, in the event of a fracture of a bis-acrylic provisional restoration, it may be more advantageous to make a new provisional restoration than to repair the fractured one. PMID:27656568

Fibre reinforcement of two temporary composite bridge materials--effect upon flexural properties.

PubMed

Al Twal, E Q H; Chadwick, R G

2012-12-01

Temporary bridges must survive for their anticipated time in clinical service. Fibre reinforcement offers a potential means of increasing the chances of achieving this. This study sought to investigate this. This in vitro study determined the three point flexural strength and flexural fatigue characteristics of beam specimens (25 mm long × 3 mm wide × 2 mm deep) of a chairside temporary crown and bridge material (Protemp 4, 3M ESPE) and a laboratory resin composite (Ceramage, Shofu Inc.) in unreinforced and reinforced states. Reinforcement was provided by Everstick Crown and Bridge (Stick Tech Ltd.) and Ribbond THM (Ribbond Inc.). All testing was performed using an Instron Universal testing machine following one week of storage in distilled water at 37 °C. Fibre reinforcement with Everstick C&B significantly (P < 0.001) increased the mean flexural strengths of both materials. The flexural fatigue limits of both Protemp 4 and Ceramage were significantly (P < 0.001) increased by fibre incorporation. The observed fibre resin coupling (where Everstick C&B was used) and knitting together of fractured specimen fragments to restore specimen function (specimens where Ribbond THM was used) demonstrated the potential to enhance the durability of temporary bridges made of the materials studied here. The incorporation of fibre reinforcement in temporary bridge materials has the potential to enhance the longevity of temporary bridges and thus reduce the need for emergency treatment. Copyright © 2012 Elsevier Ltd. All rights reserved.

The effect of 8.25% sodium hypochlorite on dental pulp dissolution and dentin flexural strength and modulus.

PubMed

Cullen, James K T; Wealleans, James A; Kirkpatrick, Timothy C; Yaccino, John M

2015-06-01

The purpose of this study was to evaluate the effect of various concentrations of sodium hypochlorite (NaOCl), including 8.25%, on dental pulp dissolution and dentin flexural strength and modulus. Sixty dental pulp samples and 55 plane parallel dentin bars were retrieved from extracted human teeth. Five test groups (n = 10) were formed consisting of a pulp sample and dentin bar immersed in various NaOCl solutions. The negative control group (n = 5) consisted of pulp samples and dentin bars immersed in saline. The positive control group (n = 5) consisted of pulp samples immersed in 8.25% NaOCl without a dentin bar. Every 6 minutes for 1 hour, the solutions were refreshed. The dentin bars were tested for flexural strength and modulus with a 3-point bend test. The time until total pulp dissolution and any changes in dentin bar flexural strength and modulus for the different NaOCl solutions were statistically analyzed. An increase in NaOCl concentration showed a highly significant decrease in pulp dissolution time. The pulp dissolution property of 8.25% NaOCl was significantly faster than any other tested concentration of NaOCl. The presence of dentin did not have a significant effect on the dissolution capacity of NaOCl if the solutions were refreshed. NaOCl concentration did not have a statistically significant effect on dentin flexural strength or modulus. Dilution of NaOCl decreases its pulp dissolution capacity. Refreshing the solution is essential to counteract the effects of dentin. In this study, NaOCl did not have a significant effect on dentin flexural strength or modulus. Published by Elsevier Inc.

Biaxial flexural strength of CAD/CAM ceramics.

PubMed

Buso, L; Oliveira-Júnior, O B; Hiroshi Fujiy, F; Leão Lombardo, G H; Ramalho Sarmento, H; Campos, F; Assunção Souza, R O

2011-06-01

Aim of the study was to evaluate the biaxial flexural strength of ceramics processed using the Cerec inLab system. The hypothesis was that the flexural strength would be influenced by the type of ceramic. Ten samples (ISO 6872) of each ceramic (N.=50/n.=10) were made using Cerec inLab (software Cerec 3D) (Ø:15 mm, thickness: 1.2 mm). Three silica-based ceramics (Vita Mark II [VM], ProCad [PC] and e-max CAD ECAD]) and two yttria-stabilized tetragonal-zirconia-polycrystalline ceramics (Y-TZP) (e-max ZirCad [ZrCAD] and Vita In-Ceram 2000 YZ Cubes [VYZ]) were tested. The samples were finished with wet silicone carbide papers up to 1 200-grit and polished in a polishing machine with diamond paste (3 µm). The samples were then submitted to biaxial flexural strength testing in a universal testing machine (EMIC), 1 mm/min. The data (MPa) were analyzed using the Kruskal-Wallis and Dunn (5%) tests. Scanning electronic microscopy (SEM) was performed on a representative sample from each group. The values (median, mean±sd) obtained for the experimental groups were: VM (101.7, 102.1±13.65 MPa), PC (165.2, 160±34.7 MPa), ECAD (437.2, 416.1±50.1 MPa), ZrCAD (804.2, 800.8±64.47 MPa) and VYZ (792.7, 807±100.7 MPa). The type of ceramic influenced the flexural strength values (P=0.0001). The ceramics ECADa, e-max ZrCADa and VYZa presented similar flexural strength values which were significantly higher than the other groups (PCb and VM IIb), which were similar statistically between them (Dunn's test). The hypothesis was accepted. The polycrystalline ceramics (Y-TZP) should be material chosen for make FPDs because of their higher flexural strength values.

Evaluation of Flexural Strength of Polymethyl Methacrylate modified with Silver Colloidal Nanoparticles subjected to Two Different Curing Cycles: An in vitro Study.

PubMed

Munikamaiah, Ranganath L; Jain, Saket K; Pal, Kapil S; Gaikwad, Ajay

2018-03-01

Silver colloidal nanoparticles have been incorporated into acrylic resins to induce antimicrobial properties. However, as additives, they can influence the mechanical properties of the final product. Mechanical properties are also dependent on different curing cycles. The aim of this study was to evaluate flexural strength of a denture base resin incorporated with different concentrations of silver colloidal nanoparticles subjected to two different curing cycles. Lucitone 199 denture base resin was used into which silver colloidal nanoparticles were incorporated at 0.5 and 5% by polymer mass. Specimens devoid of nanoparticles were used as controls. A total of 60 specimens were fabricated and divided into two groups. Each group was divided into three subgroups consisting of 10 specimens each. The specimens were fabricated according to American Dental Association (ADA) specification No. 12 and tested for flexural strength using universal testing machine. Silver colloidal nanoparticle incorporation at 0.5% concentration increased the mean flexural strength in both curing cycles by 7.5 and 4.4%, respectively, when compared with the control group. The study suggested that the mean flexural strength value of 0.5% silver colloidal nanoparticles in denture base resin was above the value of the control group both in short and long curing cycles, which makes it clinically suitable as a denture base material. However, at 5% concentration, the statistically significant amount of decrease in flexural strength compared with the value of control group both in short and long curing cycles gives it a questionable prognosis. The specimens incorporated with the antimicrobial agent 0.5% silver colloidal nanoparticles and processed by long curing cycles showed significant increase in its flexural strength compared with the control group, which makes it clinically suitable as a denture base material.

Flexural properties of denture base polymers reinforced with a glass cloth-urethane polymer composite.

PubMed

Kanie, Takahito; Arikawa, Hiroyuki; Fujii, Koichi; Ban, Seiji

2004-10-01

A newly designed light-cured reinforcement made from urethanemethacrylate oligomer and woven glass cloth has orthotropic anisotropy. This is produced for incorporation into the outermost position under the greatest tension in denture base resins. In this study, the flexural properties of self-, heat-, and light-curing reinforced resins were determined. The silanized glass cloth was soaked in urethanemethacrylate oligomer containing camphorquinone and 2-(dimethylamino)ethylmethacrylate. It was sandwiched between two pieces of polyethylene film and pressed to form a reinforcement sheet 0.3 mm in thickness, which was light-cured and prepared using four different surface conditions: with or without the polyethylene film and with or without a bonding agent. The reinforcement sheet was fixed in a fluorocarbon resin mold 3 mm in thickness, which was filled with self-, heat-, or light-curing resin and cured. The cured laminated plate was cut for flexural testing (40 x 7 x 3 mm3). A three-point flexural test was carried out at a crosshead speed of 2 mm/min and a span length of 30 mm. In this study, the glass fiber content was measured at percentages by weight because it was not possible to determine accurately the volume of the various polymers. The baseline flexural strengths of the self-, heat-, and light-curing resins were 76.2, 68.6, and 55.6 MPa, respectively, and these values were increased to 271.7, 216.4, and 266.5 MPa by the reinforcement sheet. The baseline flexural moduli of self-, heat-, and light-curing resins were 2.0, 2.4, and 2.1 GPa, respectively. These values were increased to 7.2, 5.1, and 6.6 GPa by the reinforcement sheet. SEM photographs revealed good impregnation of the glass fiber within the polymer matrix. The differences in the flexural strengths and flexural moduli of the control and reinforced specimens were significant (p < 0.01).

Effect of sintering temperature on flexural properties of alumina fiber-reinforced, alumina-based ceramics prepared by tape casting technique.

PubMed

Tanimoto, Yasuhiro; Nemoto, Kimiya

2006-01-01

The purpose of this study was to investigate the effect of sintering temperature on flexural properties of an alumina fiber-reinforced, alumina-based ceramic (alumina-fiber/alumina composite) prepared by a tape casting technique. The alumina-based ceramic used a matrix consisting of 60 wt% Al(2)O(3) powder and 40 wt% SiO(2)-B(2)O(3) glass powder with the following composition in terms of wt%: 33 SiO(2), 32 B(2)O(3), 20 CaO, and 15 MgO. Prepreg sheets of alumina-fiber/alumina composite in which uniaxial aligned alumina fibers were infiltrated with the alumina-based matrix were fabricated continuously using a tape casting technique employing a doctor blade system. Four sintering temperatures were investigated: 900 degrees C, 1000 degrees C, 1100 degrees C, and 1200 degrees C, all for 4 hours under atmospheric pressure in a furnace. The surface of the alumina-fiber/alumina composite after sintering was observed with a field-emission scanning electron microscope (FE-SEM). A three-point bending test was carried out to measure the flexural strength and modulus of alumina-fiber/alumina composite specimens. In addition, sintered alumina fiber was characterized by X-ray diffraction (XRD). FE-SEM observation showed that alumina-fiber/alumina composite was confirmed to be densely sintered for all sintering temperatures. Three-point bending measurement revealed that alumina-fiber/alumina composite produced at sintering temperatures of 1100 degrees C and 1200 degrees C exhibit flexural strengths lower than those of alumina-fiber/alumina composite produced at sintering temperatures of 900 degrees C and 1000 degrees C; alumina-fiber/alumina composite produced at sintering temperatures of 1100 degrees C and 1200 degrees C exhibit flexural moduli lower than that of alumina-fiber/alumina composite produced at a sintering temperature of 1000 degrees C. Additional XRD pattern of alumina fiber indicated that with increasing sintering temperature, the crystallographic structure of gamma-alumina transformed to mullite. There were significant differences in the flexural properties between the alumina-fiber/alumina composite sintered at the four temperatures. This indicates that the choice of optimum sintering temperature is an important factor for successful dental applications of alumina-fiber/alumina composite developed by the tape casting system.

Static and fatigue mechanical behavior of three dental CAD/CAM ceramics.

PubMed

Homaei, Ehsan; Farhangdoost, Khalil; Tsoi, James Kit Hon; Matinlinna, Jukka Pekka; Pow, Edmond Ho Nang

2016-06-01

The aim of this study was to measure the mechanical properties and fatigue behavior of three contemporary used dental ceramics, zirconia Cercon(®) (ZC), lithium disilicate e.max(®) CAD (LD), and polymer-infiltrated ceramic Enamic(®) (PIC). Flexural strength of each CAD/CAM ceramic was measured by three point bending (n=15) followed by Weibull analysis. Elastic modulus was calculated from the load-displacement curve. For cyclic fatigue loading, sinusoidal loading with a frequency of 8Hz with minimum load 3N were applied to these ceramics (n=24) using three point bending from 10(3) to 10(6) cycles. Fatigue limits of these ceramics were predicted with S-N fatigue diagram. Fracture toughness and Vickers hardness of the ceramics were measured respectively by single edge V-notch beam (SEVNB) and microindentation (Hv 0.2) methods. Chemical compositions of the materials׳ surfaces were analyzed by EDS, and microstructural analysis was conducted on the fracture surfaces by SEM. One-way ANOVA was performed and the level of significance was set at 0.05 to analyze the numerical results. The mean flexural strength of ZC, LD, and PIC was respectively 886.9, 356.7, and 135.8MPa. However, the highest Weibull modulus belonged to PIC with 19.7 and the lowest was found in LD with 7.0. The fatigue limit of maximum load for one million cycles of ZC, LD, and PIC was estimated to be 500.1, 168.4, and 73.8GPa. The mean fracture toughness of ZC, LD, and PIC was found to be respectively 6.6, 2.8, and 1.4MPam(1/2), while the mean Vickers hardness was 1641.7, 676.7, and 261.7Hv. Fracture surfaces followed fatigue loading appeared to be smoother than that after monotonic loading. Mechanical properties of ZC were substantially superior to the two other tested ceramics, but the scattering of data was the least in PIC. The fatigue limit was found to be approximately half of the mean flexural strength for all tested ceramics. Copyright © 2016 Elsevier Ltd. All rights reserved.

Dynamic Fracture Behavior of Steel Fiber Reinforced Self-Compacting Concretes (SFRSCCs).

PubMed

Zhang, Xiaoxin; Ruiz, Gonzalo; Tarifa, Manuel; Cendón, David; Gálvez, Francisco; Alhazmi, Waleed H

2017-11-05

Three-point bending tests on notched beams of three types of steel fiber-reinforced self-compacting concrete (SFRSCC) have been performed by using both a servo-hydraulic machine and a drop-weight impact instrument. The lo ading rates had a range of six orders of magnitude from 2.20 × 10 -3 mm/s (quasi-static) to 2.66 × 10³ mm/s. These SFRSCCs had the same matrix, but various types of steel fiber (straight and hooked-end) and contents (volume ratios), 0.51%, 0.77% and 1.23%, respectively. The results demonstrate that the fracture energy and the flexural strength increase as the loading rate increases. Moreover, such tendency is relatively moderate at low rates. However, at high rates it is accentuated. For the 0.51% fiber content, the dynamic increase factors of the flexural strength and the fracture energy are approximately 6 and 3, while for the 1.23% fiber content, they are around 4 and 2, respectively. Thus, the higher the fiber content the less rate sensitivity there is.

Dynamic Fracture Behavior of Steel Fiber Reinforced Self-Compacting Concretes (SFRSCCs)

PubMed Central

Tarifa, Manuel; Cendón, David; Gálvez, Francisco; Alhazmi, Waleed H.

2017-01-01

Three-point bending tests on notched beams of three types of steel fiber-reinforced self-compacting concrete (SFRSCC) have been performed by using both a servo-hydraulic machine and a drop-weight impact instrument. The lo ading rates had a range of six orders of magnitude from 2.20 × 10−3 mm/s (quasi-static) to 2.66 × 103 mm/s. These SFRSCCs had the same matrix, but various types of steel fiber (straight and hooked-end) and contents (volume ratios), 0.51%, 0.77% and 1.23%, respectively. The results demonstrate that the fracture energy and the flexural strength increase as the loading rate increases. Moreover, such tendency is relatively moderate at low rates. However, at high rates it is accentuated. For the 0.51% fiber content, the dynamic increase factors of the flexural strength and the fracture energy are approximately 6 and 3, while for the 1.23% fiber content, they are around 4 and 2, respectively. Thus, the higher the fiber content the less rate sensitivity there is. PMID:29113095

[Effect of vacuum deposition technology on the metal-porcelain bond strength of a new type of CO-CR ceramic and framework dental alloy].

PubMed

Wu, Jun-ling; Chao, Yong-lie; Ji, Ping; Gao, Xu

2007-10-01

To investigate the effect of a new engineering technique of vacuum deposition-plasma magnetron reactive sputter deposition technique on the metal-porcelain bond strength of a new type of Co-Cr ceramic and framework dental alloy. Before porcelain painted on the specimens, the standardized metal strips made from DA9-4 dental alloy were coated with a thin Al2O3 ceramic film by plasma magnetron reactive sputter deposition technique. The conformation, structure and thickness of the ceramic film were analyzed. The specimens for three-point bending test made from DA9-4 alloy and VMK95 porcelain were used for metal-porcelain bond strength measurement, in the same time the interface of metal-porcelain and element distribution were also observed. The flexural bonding strength of metal-porcelain of sputtering group and control group were (180.55+/-16.45) MPa and (143.80+/-24.49) MPa. The flexural bonding strength of metal-porcelain of sputtering group was higher than control group significantly through statistical analysis (P<0.01). The plasma magnetron reactive sputter deposition technique has a positive effect in improving the bonding strength of DA9-4 dental alloy and ceramic.

Porcelain monolayers and porcelain/alumina bilayers reinforced by Al2O3/GdAlO3 fibers.

PubMed

Sgura, Ricardo; Medeiros, Igor Studart; Cesar, Paulo Francisco; Campos, Adeliani Almeida; Hernandes, Antonio Carlos

2012-01-01

This work tested the effect of the addition of Al(2)O(3)/GdAlO(3) longitudinal fibers in different contents to veneering porcelain of two dental all ceramic systems. Fibers (0.5 mm diameter) obtained by the Laser Heated Pedestal Growth (LHPG) method were added to bar-shaped specimens made by veneer porcelain (monolayers) or both the veneer and the core ceramic (bilayers) of two all-ceramic systems: In-Ceram Alumina-glass infiltrated alumina composite (GIA) and In-Ceram 2000 AL Cubes-alumina polycrystal (AP) (VITA Zahnfabrik). The longitudinal fibers were added to veneering porcelain (VM7) in two different proportions: 10 or 17 vol%. The bars were divided into nine experimental conditions (n=10) according to material used: VM7 porcelain monolayers, VM7/GIA, VM7/AP; and according to the amount of fibers within the porcelain layer: no fibers, 10 vol% or 17 vol%. After grinding and polishing the specimens were submitted to a three point bending test (crosshead speed = 0.5 mm/min) with porcelain positioned at tensile side. Data were analyzed by means of one-way ANOVA and a Tukey's test (α=5%). Scanning electronic microscopy (SEM) was conducted for fractographic analysis. Regarding the groups without fiber addition, VM7/AP showed the highest flexural strength (MPa), followed by VM7/GIA and VM7 monolayers. The addition of fibers led to a numerical increase in flexural strength for all groups. For VM7/GIA bilayers the addition of 17 vol% of fibers resulted in a significant 48% increase in the flexural strength compared to the control group. Fractographic analysis revealed that the crack initiation site was in porcelain at the tensile surface. Cracks also propagated between fibers before heading for the alumina core. The addition of 17 vol% of Al(2)O(3)/GdAlO(3) longitudinal fibers to porcelain/glass infiltrated alumina bilayers significantly improved its flexural strength. 10 vol% or 17 vol% of fibers inclusion increased the flexural strength for all groups. Copyright © 2011 Elsevier Ltd. All rights reserved.

Flexural Properties of PLA Components Under Various Test Condition Manufactured by 3D Printer

NASA Astrophysics Data System (ADS)

Jaya Christiyan, K. G.; Chandrasekhar, U.; Venkateswarlu, K.

2018-06-01

Rapid Prototyping (RP) technologies have emerged as a fabrication method to obtain engineering components in the resent past. Desktop 3D printing, also referred as an additive layer manufacturing technology is a powerful method of RP technique that can fabricate 3 dimensional engineering components. In this method, 3D digital data is converted into real product. In the present investigation, Polylactic Acid (PLA) was considered as a starting material. Flexural strength of PLA material was evaluated using 3-point bend test, as per ASTM D790 standard. Specimens with flat (0°) and vertical (90°) orientation were considered. Moreover, layer thicknesses of 0.2, 0.25, and 0.3 mm were considered. To fabricate these specimens, printing speed of 38 and 52 mm/s was maintained. Nozzle diameter of 0.4 mm with 40 % of infill density were used. Based on the experimental results, it was observed that 0° orientation, 38 mm/s printing speed, and 0.2 mm layer thickness resulted maximum flexural strength, as compared to all other specimens. The improved flexural strength was due to the lower layer thickness (0.2 mm) specimens, as compared with other specimens made of 0.25 and 0.30 mm layer thicknesses. It was concluded that flexural strength properties were greatly influenced by lower the layer thickness, printing speed, and orientation.

High-temperature mechanical properties of a solid oxide fuel cell glass sealant in sintered forms

NASA Astrophysics Data System (ADS)

Chang, Hsiu-Tao; Lin, Chih-Kuang; Liu, Chien-Kuo; Wu, Szu-Han

High-temperature mechanical properties of a silicate-based glass sealant (GC-9) for planar solid oxide fuel cell have been studied in sintered forms. Ring-on-ring biaxial flexural tests are carried out at room temperature to 800 °C for the sintered GC-9 glass. The results are also compared with those in cast bulk forms. From the force-displacement curves, the glass transition temperature (T g) of the non-aged, sintered GC-9 glass is estimated to be between 700 °C and 750 °C, while that of the aged one is between 750 °C and 800 °C. Due to a crack healing effect of the residual glass at high temperature, the flexural strength of the sintered GC-9 glass at temperature of 650 °C to T g point is greater than that at room temperature. At temperature above T g, the flexural strength and stiffness are considerably reduced to a level lower than the room-temperature one. The sintered GC-9 glass with pores and crystalline phases has a flexural strength lower than the cast bulk one at temperature of 650 °C and below. Due to a greater extent of crystallization, the flexural strength and stiffness of the sintered GC-9 glass are greater than those of the cast bulk one at 700-800 °C.

Sol-gel derived bioactive coating on zirconia: Effect on flexural strength and cell proliferation.

PubMed

Shahramian, Khalil; Leminen, Heidi; Meretoja, Ville; Linderbäck, Paula; Kangasniemi, Ilkka; Lassila, Lippo; Abdulmajeed, Aous; Närhi, Timo

2017-11-01

The purpose of this study was to evaluate the effect of sol-gel derived bioactive coatings on the biaxial flexural strength and fibroblast proliferation of zirconia, aimed to be used as an implant abutment material. Yttrium stabilized zirconia disc-shaped specimens were cut, ground, sintered, and finally cleansed ultrasonically in each of acetone and ethanol for 5 minutes. Three experimental groups (n = 15) were fabricated, zirconia with sol-gel derived titania (TiO 2 ) coating, zirconia with sol-gel derived zirconia (ZrO 2 ) coating, and non-coated zirconia as a control. The surfaces of the specimens were analyzed through images taken using a scanning electron microscope (SEM), and a non-contact tapping mode atomic force microscope (AFM) was used to record the surface topography and roughness of the coated specimens. Biaxial flexural strength values were determined using the piston-on-three ball technique. Human gingival fibroblast proliferation on the surface of the specimens was evaluated using AlamarBlue assay™. Data were analyzed using a one-way analysis of variance (ANOVA) followed by Tukey's post-hoc test. Additionally, the biaxial flexural strength data was also statistically analyzed with the Weibull distribution. The biaxial flexural strength of zirconia specimens was unaffected (p > 0.05). Weibull modulus of TiO 2 coated and ZrO 2 coated groups (5.7 and 5.4, respectively) were lower than the control (8.0). Specimens coated with ZrO 2 showed significantly lower fibroblast proliferation compared to other groups (p < 0.05). In conclusion, sol-gel derived coatings have no influence on the flexural strength of zirconia. ZrO 2 coated specimens showed significantly lower cell proliferation after 12 days than TiO 2 coated or non-coated control. © 2016 Wiley Periodicals, Inc. J Biomed Mater Res Part B: Appl Biomater, 105B: 2401-2407, 2017. © 2016 Wiley Periodicals, Inc.

Evaluation of thermal conductivity and flexural strength properties of poly(methyl methacrylate) denture base material reinforced with different fillers.

PubMed

Kul, Esra; Aladağ, Lütfü İhsan; Yesildal, Ruhi

2016-11-01

Poly(methyl methacrylate) (PMMA) is widely used in prosthodontics as a denture base material. However, it has several disadvantages, including low strength and low thermal conductivity. The purpose of this in vitro study was to evaluate thermal conductivity and flexural strength after adding powdered Ag, TiO 2 , ZrO 2 , Al 2 O 3 , SiC, SiC-nano, Si 3 N 4 , and HA-nano in ratios of 10 wt% to PMMA. A total of 144 specimens were fabricated and divided into 18 groups. Specimens were left in water for 30 days. Thermal conductivity values were measured using a heat flowmeter, flexural strength was measured with a 3-point bend test, and specimens were investigated with environmental scanning electron microscopy. One-way ANOVA was used to compare means followed by using Duncan multiple range test (α=.05). The thermal conductivity value of PMMA increased significantly after the addition of Si 3 N 4 , SiC, Al 2 O 3 , SiC-nano, TiO 2 , ZrO 2 , HA-nano, and Ag. Progressive increases in thermal conductivity were observed in Si 3 N 4 , SiC, and Al 2 O 3 fillers. Flexural strength values of the control group were not significantly different from those of the SiC, Al 2 O 3 , or Ag group (P>.05). In the other groups, flexural strength values decreased significantly (P<.05). On the basis of electron microscopy, we observed that Si 3 N 4 , SiC, and Al 2 O 3 powders had higher thermal conductivity values that are dissipated more homogeneously in PMMA. Although the addition of 10 wt% SiC, Al 2 O 3, and Ag powder to PMMA significantly increased thermal conductivity, the flexural strength values of PMMA were not significantly changed. Copyright © 2016 Editorial Council for the Journal of Prosthetic Dentistry. Published by Elsevier Inc. All rights reserved.

Effect of etching time and resin bond on the flexural strength of IPS e.max Press glass ceramic.

PubMed

Xiaoping, Luo; Dongfeng, Ren; Silikas, Nick

2014-12-01

To evaluate the effect of hydrofluoric acid (HFA) etching time and resin cement bond on the flexural strength of IPS e.max(®) Press glass ceramic. Two hundred and ten bars, 25mm×3mm×2mm, were made from IPS e.max(®) Press ingots through lost-wax, hot-pressed ceramic fabrication technology and randomly divided into five groups with forty-two per group after polishing. The ceramic surfaces of different groups were etched by 9.5% hydrofluoric acid gel for 0, 20, 40, 60 and 120s respectively. Two specimens of each group were selected randomly to examine the surface roughness and 3-dimensional topography with atomic force microscope (AFM), and microstructure was analyzed by the field emission scanning electron microscope (FE-SEM). Then each group were subdivided into two subgroups (n=20). One subgroup of this material was selected to receive a thin (approximately 0.1mm) layer of resin luting agent (Variolink N) whereas the other subgroup remained unaltered. Half of subgroup's specimens were thermocycled 10,000 times before a 3-point bending test in order to determine the flexural strength. Interface between resin cement and ceramic was examined with field emission scanning electronic microscope. Roughness values increased with increasing etching time. The mean flexural strength values of group 0s, 20s, 40s, 60s and 120s were 384±33, 347±43, 330±53, 327±67 and 317±41MPa respectively. Increasing HF etching times reduced the mean flexural strength (p<0.05). However, the mean flexural strength of each group, except group 0s, increased significantly to 420±31, 435±50, 400±39 and 412±58MPa after the application of dual-curing resin cement. In the present investigation, no significant differences after thermocycling on the flexural strengths were evident. Overtime HF etching could have a wakening effect on IPS e.max(®) Press glass ceramic, but resin cement bonding to appropriately etched surface would strengthen the dental ceramic. Copyright © 2014 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Thermal effects on the mechanical properties of SiC fiber reinforced reaction bonded silicon nitride matrix (SiC/RBSN) composites

NASA Technical Reports Server (NTRS)

Bhatt, R. T.; Phillips, R. E.

1988-01-01

The elevated temperature four-point flexural strength and the room temperature tensile and flexural strength properties after thermal shock were measured for ceramic composites consisting of 30 vol pct uniaxially aligned 142 micron diameter SiC fibers in a reaction bonded Si3N4 matrix. The elevated temperature strengths were measured after 15 min of exposure in air at temperatures to 1400 C. Thermal shock treatment was accomplished by heating the composite in air for 15 min at temperatures to 1200 C and then quenching in water at 25 C. The results indicate no significant loss in strength properties either at temperature or after thermal shock when compared with the strength data for composites in the as-fabricated condition.

The Application of a Novel Ceramic Liner Improves Bonding between Zirconia and Veneering Porcelain

PubMed Central

Lee, Hee-Sung

2017-01-01

The adhesion of porcelain to zirconia is a key factor in the success of bilayered restorations. In this study, the efficacy of a novel experimental liner (EL) containing zirconia for improved bonding between zirconia and veneering porcelain was tested. Four ELs containing various concentrations (0, 3.0, 6.0, and 9.0 wt %) of zirconia were prepared. Testing determined the most effective EL (EL3 containing 3.0 wt % zirconia) in terms of shear bond strength value (n = 15). Three different bar-shaped zirconia/porcelain bilayer specimens were prepared for a three-point flexural strength (TPFS) test (n = 15): no-liner (NL), commercial liner (CL), and EL3. Specimens were tested for TPFS with the porcelain under tension and the maximum load was measured at the first sign of fracture. The strength data were analyzed using one-way ANOVA and Tukey’s test (α = 0.05) as well as Weibull distribution. When compared to NL, the CL application had no effect, while the EL3 application had a significant positive effect (p < 0.001) on the flexural strength. Weibull analysis also revealed the highest shape and scale parameters for group EL3. Within the limitations of this study, the novel ceramic liner containing 3.0 wt % zirconia (EL3) significantly enhanced the zirconia/porcelain interfacial bonding. PMID:28869512

Effects of slag on flexural strength of slurry infiltrated fibrous concrete

NASA Astrophysics Data System (ADS)

Elavarasi, D.; Saravana Raja Mohan, K.; Parthasarathy, P.; Dinesh, T.

2017-07-01

Slurry infiltrated fibrous concrete is one of the new advanced concrete composite which differs from method of fabrication and composition of the matrix. Extensive research is being carried out on alternative binders or supplements to cement aiming to reduce environmental impact. However, little has been published to investigate the structural behaviour of SIFCON incorporating with mineral admixtures, particularly as regards its ultrahigh ductility, which may alter the mode of failure from brittle to the more desirable ductile. An experimental study was carried out to investigate the flexural behavior of SIFCON containing three different percentage of fibre content 6%,8% &10% with incorporation of optimum dosage of blast furnace slag replaced by cement. Strength characteristics such as Compressive strength and splitting tensile strength test were carry out for SIFCON incorporating 10% of fibre content and different percentage of slag (0, 15, 30, 45, 60%&75%) to optimize the replacement level. The test results found that the maximum strengths were attained at 30% of blast furnace slag replaced by cement. To study the flexural behavior of SIFCON beam of size 1.2x0.1x0.2m containing different percentages (6%, 8% & 10%) fibre content incorporating with and without the optimum percentage of slag were cast and tested. Both flexural strength and Load displacement characteristics of the specimens were studied under flexure. The outcomespresentedfromtest resultshave been compared. The test results reveals that the flexural strength, toughness, ductility and stiffness characteristics were significantly improved due to incorporation of optimum dosage of slag enhancing when compared to without mineral admixtures also compared to conventional concrete(RCC). Major conclusions were drawn from the investigations which are presented.

Effect of in vitro aging on the flexural strength and probability to fracture of Y-TZP zirconia ceramics for all-ceramic restorations.

PubMed

Siarampi, Eleni; Kontonasaki, Eleana; Andrikopoulos, Konstantinos S; Kantiranis, Nikolaos; Voyiatzis, George A; Zorba, Triantafillia; Paraskevopoulos, Konstantinos M; Koidis, Petros

2014-12-01

Dental zirconia restorations should present long-term clinical survival and be in service within the oral environment for many years. However, low temperature degradation could affect their mechanical properties and survival. The aim of this study was to investigate the effect of in vitro aging on the flexural strength of yttrium-stabilized (Y-TZP) zirconia ceramics for ceramic restorations. One hundred twenty bar-shaped specimens were prepared from two ceramics (ZENO Zr (WI) and IPS e.max(®) ZirCAD (IV)), and loaded until fracture according to ISO 6872. The specimens from each ceramic (nx=60) were divided in three groups (control, aged for 5h, aged for 10h). One-way ANOVA was used to assess statistically significant differences among flexural strength values (P<0.05). The variability of the flexural strength values was analyzed using the two-parameter Weibull distribution function, which was applied for the estimation of Weibull modulus (m) and characteristic strength (σ0). The crystalline phase polymorphs of the materials (tetragonal, t, and monoclinic, m, zirconia) were investigated by X-ray diffraction (XRD) analysis, Raman spectroscopy and Fourier transform infrared (FTIR) spectroscopy. A slight increase of the flexural strength after 5h, and a decrease after 10h of aging, was recorded for both ceramics, however statistically significant was for the WI group (P<0.05). Both ceramics presented a t→m phase transformation, with the m-phase increasing from 4 to 5% at 5h to around 15% after 10h. The significant reduction of the flexural strength after 10h of in vitro aging, suggests high fracture probability for one of the zirconia ceramics tested. Copyright © 2014 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Comparative Effect of Different Polymerization Techniques on the Flexural and Surface Properties of Acrylic Denture Bases.

PubMed

Gad, Mohammed M; Fouda, Shaimaa M; ArRejaie, Aws S; Al-Thobity, Ahmad M

2017-05-22

Polymerization techniques have been modified to improve physical and mechanical properties of polymethylmethacrylate (PMMA) denture base, as have the laboratory procedures that facilitate denture construction techniques. The purpose of the present study was to investigate the effect of autoclave polymerization on flexural strength, elastic modulus, surface roughness, and the hardness of PMMA denture base resins. Major Base and Vertex Implacryl heat-polymerized acrylic resins were used to fabricate 180 specimens. According to the polymerization technique, tested groups were divided into: group I (water-bath polymerization), group II (short autoclave polymerization cycle, 60°C for 30 minutes, then 130°C for 10 minutes), and group III (long autoclave polymerization cycle, 60°C for 30 minutes, then 130°C for 20 minutes). Each group was divided into two subgroups based on the materials used. Flexural strength and elastic modulus were determined by a three-point bending test. Surface roughness and hardness were evaluated with a profilometer and Vickers hardness (VH) test, respectively. One-way ANOVA and the Tukey-Kramer multiple-comparison test were used for results analysis, which were statistically significant at p ≤ 0.05. Autoclave polymerization showed a significant increase in flexural strength and hardness of the two resins (p < 0.05). The elastic modulus showed a significant increase in the major base resin, while a significant decrease was seen for Vertex Implacryl in all groups (p < 0.05); however, there was no significant difference in surface roughness between autoclave polymerization and water-bath polymerization (p > 0.05). Autoclave polymerization significantly increased the flexural properties and hardness of PMMA denture bases, while the surface roughness was within acceptable clinical limits. For a long autoclave polymerization cycle, it could be used as an alternative to water-bath polymerization. © 2017 by the American College of Prosthodontists.

Effect of fiber content on flexural properties of glass fiber-reinforced polyamide-6 prepared by injection molding.

PubMed

Nagakura, Manamu; Tanimoto, Yasuhiro; Nishiyama, Norihiro

2017-07-26

The use of non-metal clasp denture (NMCD) materials may seriously affect the remaining tissues because of the low rigidity of NMCD materials such as polyamides. The purpose of this study was to develop a high-rigidity glass fiber-reinforced thermoplastic (GFRTP) composed of E-glass fiber and polyamide-6 for NMCDs using an injection molding. The reinforcing effects of fiber on the flexural properties of GFRTPs were investigated using glass fiber content ranging from 0 to 50 mass%. Three-point bending tests indicated that the flexural strength and elastic modulus of a GFRTP with a fiber content of 50 mass% were 5.4 and 4.7 times higher than those of unreinforced polyamide-6, respectively. The result showed that the physical characteristics of GFRTPs were greatly improved by increasing the fiber content, and the beneficial effects of fiber reinforcement were evident. The findings suggest that the injection-molded GFRTPs are adaptable to NMCDs because of their excellent mechanical properties.

Evaluation of polymethyl methacrylate resin mechanical properties with incorporated halloysite nanotubes

PubMed Central

2016-01-01

PURPOSE This study inspects the effect of incorporating halloysite nanotubes (HNTs) into polymethyl methacrylate (PMMA) resin on its flexural strength, hardness, and Young's modulus. MATERIALS AND METHODS Four groups of acrylic resin powder were prepared. One group without HNTs was used as a control group and the other three groups contained 0.3, 0.6 and 0.9 wt% HNTs. For each one, flexural strength, Young's modulus and hardness values were measured. One-way ANOVA and Tukey's test were used for comparison (P<.05). RESULTS At lower concentration (0.3 wt%) of HNT, there was a significant increase of hardness values but no significant increase in both flexural strength and Young's modulus values of PMMA resin. In contrast, at higher concentration (0.6 and 0.9 wt%), there was a significant decrease in hardness values but no significant decrease in flexural strength and Young's modulus values compared to those of the control group. CONCLUSION Addition of lower concentration of halloysite nanotubes to denture base materials could improve some of their mechanical properties. Improving the mechanical properties of acrylic resin base material could increase the patient satisfaction. PMID:27350849

Thio-urethanes improve properties of dual-cured composite cements.

PubMed

Bacchi, A; Dobson, A; Ferracane, J L; Consani, R; Pfeifer, C S

2014-12-01

This study aims at modifying dual-cure composite cements by adding thio-urethane oligomers to improve mechanical properties, especially fracture toughness, and reduce polymerization stress. Thiol-functionalized oligomers were synthesized by combining 1,3-bis(1-isocyanato-1-methylethyl)benzene with trimethylol-tris-3-mercaptopropionate, at 1:2 isocyanate:thiol. Oligomer was added at 0, 10 or 20 wt% to BisGMA-UDMA-TEGDMA (5:3:2, with 25 wt% silanated inorganic fillers) or to one commercial composite cement (Relyx Ultimate, 3M Espe). Near-IR was used to measure methacrylate conversion after photoactivation (700 mW/cm(2) × 60s) and after 72 h. Flexural strength and modulus, toughness, and fracture toughness were evaluated in three-point bending. Polymerization stress was measured with the Bioman. The microtensile bond strength of an indirect composite and a glass ceramic to dentin was also evaluated. Results were analyzed with analysis of variance and Tukey's test (α = 0.05). For BisGMA-UDMA-TEGDMA cements, conversion values were not affected by the addition of thio-urethanes. Flexural strength/modulus increased significantly for both oligomer concentrations, with a 3-fold increase in toughness at 20 wt%. Fracture toughness increased over 2-fold for the thio-urethane modified groups. Contraction stress was reduced by 40% to 50% with the addition of thio-urethanes. The addition of thio-urethane to the commercial cement led to similar flexural strength, toughness, and conversion at 72h compared to the control. Flexural modulus decreased for the 20 wt% group, due to the dilution of the overall filler volume, which also led to decreased stress. However, fracture toughness increased by up to 50%. The microtensile bond strength increased for the experimental composite cement with 20 wt% thio-urethane bonding for both an indirect composite and a glass ceramic. Novel dual-cured composite cements containing thio-urethanes showed increased toughness, fracture toughness and bond strength to dentin while demonstrating reduced contraction stress. All of these benefits are derived without compromising the methacrylate conversion of the resin component. The modification does not require changing the operatory technique. © International & American Associations for Dental Research.

Thio-urethanes Improve Properties of Dual-cured Composite Cements

PubMed Central

Bacchi, A.; Dobson, A.; Ferracane, J.L.; Consani, R.; Pfeifer, C.S.

2014-01-01

This study aims at modifying dual-cure composite cements by adding thio-urethane oligomers to improve mechanical properties, especially fracture toughness, and reduce polymerization stress. Thiol-functionalized oligomers were synthesized by combining 1,3-bis(1-isocyanato-1-methylethyl)benzene with trimethylol-tris-3-mercaptopropionate, at 1:2 isocyanate:thiol. Oligomer was added at 0, 10 or 20 wt% to BisGMA-UDMA-TEGDMA (5:3:2, with 25 wt% silanated inorganic fillers) or to one commercial composite cement (Relyx Ultimate, 3M Espe). Near-IR was used to measure methacrylate conversion after photoactivation (700 mW/cm2 × 60s) and after 72 h. Flexural strength and modulus, toughness, and fracture toughness were evaluated in three-point bending. Polymerization stress was measured with the Bioman. The microtensile bond strength of an indirect composite and a glass ceramic to dentin was also evaluated. Results were analyzed with analysis of variance and Tukey’s test (α = 0.05). For BisGMA-UDMA-TEGDMA cements, conversion values were not affected by the addition of thio-urethanes. Flexural strength/modulus increased significantly for both oligomer concentrations, with a 3-fold increase in toughness at 20 wt%. Fracture toughness increased over 2-fold for the thio-urethane modified groups. Contraction stress was reduced by 40% to 50% with the addition of thio-urethanes. The addition of thio-urethane to the commercial cement led to similar flexural strength, toughness, and conversion at 72h compared to the control. Flexural modulus decreased for the 20 wt% group, due to the dilution of the overall filler volume, which also led to decreased stress. However, fracture toughness increased by up to 50%. The microtensile bond strength increased for the experimental composite cement with 20 wt% thio-urethane bonding for both an indirect composite and a glass ceramic. Novel dual-cured composite cements containing thio-urethanes showed increased toughness, fracture toughness and bond strength to dentin while demonstrating reduced contraction stress. All of these benefits are derived without compromising the methacrylate conversion of the resin component. The modification does not require changing the operatory technique. PMID:25248610

Silicon nitride having a high tensile strength

DOEpatents

Pujari, Vimal K.; Tracey, Dennis M.; Foley, Michael R.; Paille, Norman I.; Pelletier, Paul J.; Sales, Lenny C.; Willkens, Craig A.; Yeckley, Russell L.

1996-01-01

A silicon nitride ceramic comprising: a) inclusions no greater than 25 microns in length, b) agglomerates no greater than 20 microns in diameter, and c) a surface finish of less than about 8 microinches, said ceramic having a four-point flexural strength of at least about 900 MPa.

[Effect of nano-hydroxyapatite to glass ionomer cement].

PubMed

Mu, Ya-Bing; Zang, Guang-Xiang; Sun, Hong-Chen; Wang, Cheng-Kun

2007-12-01

To investigate the mechanical character, microleakage and mineralizing potential of nano-hydroxyapatite (nano-HAP)-added glass ionomer cement(GIC). 8% nano-HAP were incorporated into GIC as composite, and pure GIC as control. Both types of material were used to make 20 cylinders respectively in order to detect three-point flexural strength and compressive strength. Class V cavities were prepared in 120 molars extracted for orthodontic treatment, then were filled by two kinds of material. The microleakage at the composite-dentine interface was observed with confocal laser scanning microscope (CLSM) after stained with 1% rhodamin-B-isothiocyanate for 24 hours. Class V cavities were prepared in the molars of 4 healthy dogs, filled with composite, and the same molars in the other side were filled with GIC as control. The teeth were extracted to observe the mineralizing property with polarimetric microscope in 8 weeks after filling. Three-point flexural strength and compressive of nano-HAP-added GIC were increased compared with pure GIC (P < 0.001, P < 0.05). The nanoleakages and microleakages appeared at the material-dentine interface in the two groups, but there were more microleakages in control group than in experiment group (P = 0.004). New crystals of hydroxyapatite were formed into a new mineralizing zone at the interface of tooth and nano-HAP-added GIC, while there was no hydroxyapatite crystals formed at the interface of tooth and pure GIC. 8% nano-HAP-added GIC can tightly fill tooth and have mineralizing potential, and can be used as liner or filling material for prevention.

Contribution of postpolymerization conditioning and storage environments to the mechanical properties of three interim restorative materials.

PubMed

Thompson, Geoffrey A; Luo, Qing

2014-09-01

Because polymer-based interim restorative materials are weak, even well-made restorations sometimes fail before the definitive restoration is ready for insertion. Therefore, knowing which fabrication procedures and service conditions affect mechanical properties is important, particularly over an extended period. The purpose of this study was to evaluate the effect of thermal treatment, surface sealing, thermocycling, storage media, storage temperature, and age on autopolymerizing poly(methylmethacrylate) and bis-acryl interim restorative materials. Outcome measures were flexural strength, Vickers surface microhardness, and impact strength. Flexural strength and microhardness of poly(methylmethacrylate) (Jet Acrylic) and 2 bis-acryl-composite resin (Protemp 3 Garant and Integrity) interim restorative materials were evaluated as affected by storage media, storage temperature, storage time, thermocycling, postpolymerization thermal treatment, or application of a surface sealer. In total, 2880 beam specimens (25×2×2 mm) were fabricated. Mechanical property analyses were made at 10 days, 30 days, 6 months, and 1 year after specimen preparation. Flexural strength was determined by using a 3-point bending test in a universal testing machine with a 1 kN load cell at a crosshead speed of 5.0 mm min(-1). Fracture specimens were recovered and used for determining Vickers microhardness. Measurements were made with a 0.1 N load and 15 second dwell time. Three microhardness measurements were made for each specimen, and the mean was used for reporting Vickers microhardness. Notched impact specimens (64×12.7×6.35 mm) were fabricated from Jet, Protemp 3 Garant, and Integrity interim restorative materials, yielding 288 impact specimens. Impact strengths were assessed at 10 days, 30 days, 6 months, and 1 year with a 2 J pendulum. The effects of the various experimental treatments were determined and rank ordered with analysis of variance, F ratios, and least square means differences Student t tests (α=.05). All experimental treatments investigated had significant effects on flexural strength, with material (P<.001) and thermocycling (P<.001) being dominant. Moreover, all experimental treatments investigated had a significant overall impact on Vickers microhardness with material (P<.001) and Palaseal glaze (P<.001) showing large effects. Material (P<.001) and age (P=.010) had a significant effect on impact strength. Mechanical properties of some interim polymeric materials can be improved by postpolymerization heat treatments or surface glazing. This procedure may extend the useful lifetime of some bis-acryl interim restorations. Copyright © 2014 Editorial Council for the Journal of Prosthetic Dentistry. Published by Elsevier Inc. All rights reserved.

Effects of incorporation of 2.5 and 5 wt% TiO2 nanotubes on fracture toughness, flexural strength, and microhardness of denture base poly methyl methacrylate (PMMA).

PubMed

Abdulrazzaq Naji, Sahar; Behroozibakhsh, Marjan; Jafarzadeh Kashi, Tahereh Sadat; Eslami, Hossein; Masaeli, Reza; Mahgoli, Hosseinali; Tahriri, Mohammadreza; Ghavvami Lahiji, Mehrsima; Rakhshan, Vahid

2018-04-01

The aim of this preliminary study was to investigate, for the first time, the effects of addition of titania nanotubes (n-TiO 2 ) to poly methyl methacrylate (PMMA) on mechanical properties of PMMA denture base. TiO 2 nanotubes were prepared using alkaline hydrothermal process. Obtained nanotubes were assessed using FESEM-EDX, XRD, and FT-IR. For 3 experiments of this study (fracture toughness, three-point bending flexural strength, and Vickers microhardness), 135 specimens were prepared according to ISO 20795-1:2013 (n of each experiment=45). For each experiment, PMMA was mixed with 0% (control), 2.5 wt%, and 5 wt% nanotubes. From each TiO 2 :PMMA ratio, 15 specimens were fabricated for each experiment. Effects of n-TiO 2 addition on 3 mechanical properties were assessed using Pearson, ANOVA, and Tukey tests. SEM images of n-TiO 2 exhibited the presence of elongated tubular structures. The XRD pattern of synthesized n-TiO 2 represented the anatase crystal phase of TiO 2 . Moderate to very strong significant positive correlations were observed between the concentration of n-TiO 2 and each of the 3 physicomechanical properties of PMMA (Pearson's P value ≤.001, correlation coefficient ranging between 0.5 and 0.9). Flexural strength and hardness values of specimens modified with both 2.5 and 5 wt% n-TiO 2 were significantly higher than those of control ( P ≤.001). Fracture toughness of samples reinforced with 5 wt% n-TiO 2 (but not those of 2.5% n-TiO 2 ) was higher than control ( P =.002). Titania nanotubes were successfully introduced for the first time as a means of enhancing the hardness, flexural strength, and fracture toughness of denture base PMMA.

Silicon nitride having a high tensile strength

DOEpatents

Pujari, V.K.; Tracey, D.M.; Foley, M.R.; Paille, N.I.; Pelletier, P.J.; Sales, L.C.; Willkens, C.A.; Yeckley, R.L.

1996-11-05

A silicon nitride ceramic is disclosed comprising: (a) inclusions no greater than 25 microns in length, (b) agglomerates no greater than 20 microns in diameter, and (c) a surface finish of less than about 8 microinches, said ceramic having a four-point flexural strength of at least about 900 MPa. 4 figs.

Comparative study of the physical properties of core materials.

PubMed

Saygili, Gülbin; Mahmali, Sevil M

2002-08-01

This study was undertaken to measure physical properties of materials used for direct core buildups, including high-copper amalgam, visible light-cured resin composite, autocured titanium-containing composite, polyacid-modified composite, resin-modified glass-ionomer, and silver cermet cement. Compressive strength, diametral tensile strength, and flexural strength of six core materials of various material classes were measured for each material as a function of time up to 3 months at different storage conditions, using a standard specification test designed for the materials. Three different storage conditions (dry, humid, wet) at 37 degrees C were chosen. Materials were manipulated according to manufacturers' instructions for use as cores. Mean compressive, diametral tensile, and flexural strengths with associated standard deviations were calculated for each material. Multiple comparison and Newman-Keuls tests discerned many differences among materials. All materials were found to meet the minimum specification requirements, except in terms of flexural strength for amalgam after 1 hour and the silver cermet at all time intervals.

Artificial Composites for High Temperature Applications; A Review (Composites Artificiels Destines a des Applications a Haute Temperature; Un Expose),

DTIC Science & Technology

1987-01-01

71 6 Propagation of the recrystallization front in W-wire activated by Ni and Fe in the temperature range 1473 to 1923 K...composites. 73 9 Comparitive creep data for W - 1%ThO2 /FeCrAIY and DS eutectics . 73 10 Three point flexural strength in argon versus temperature for...particularly directionally solidified eutectics . In these composites the fibrous reinforcing phase is usually in chemical equilibrium with the

CHARACTERIZATION OF POLED SINGLE-LAYER PZT FOR PIEZO STACK IN FUEL INJECTION SYSTEM

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wang, Hong; Matsunaga, Tadashi; Lin, Hua-Tay

2010-01-01

Poled single-layer PZT has been characterized in as-extracted and as-received states. PZT plate specimens in the former were extracted from a stack. Flexure strength of PZT was evaluated by using ball-on-ring and 4-point bend tests. Fractography showed that intergranular fractures dominated the fracture surface and that volume pores were the primary strength-limiting flaws. The electric field effect was investigated by testing the PZT in open circuit and coercive field levels. An asymmetrical response on the biaxial flexure strength with respect to the electric field direction was observed. These experimental results will assist reliability design of the piezo stack that ismore » being considered in fuel injection system.« less

Flexural strength and behaviour of SFRSCC ribbed slab under four point bending

NASA Astrophysics Data System (ADS)

Ahmad, Hazrina; Hashim, Mohd Hisbany Mohd; Bakar, Afidah Abu; Hamzah, Siti Hawa; Rahman, Fadhillah Abdul

2017-11-01

An experimental investigation was carried out to study the ultimate strength and behaviour of SFRSCC ribbed slab under four point bending. Comparison was been made between ribbed slab that was fully reinforced with steel fibres (SFWS) with conventionally reinforced concrete ribbed slab (CS and CRC). The volume fraction of the 35 mm hooked end steel fibres used in the mix was 1% (80 kg/m3) with the aspect ratio of 65. Three full scale slab samples with the dimension of 2.8 x 1.2 m with 0.2 m thickness was constructed for the purpose of this study. The slab samples was loaded until failure in a four point bending test. As a whole, based on the results, it can be concluded that the performance of the steel fiber reinforced samples (SFWS) was found to be almost equivalent to the conventionally reinforced concrete ribbed slab sample (CRC).

Effect of etching with distinct hydrofluoric acid concentrations on the flexural strength of a lithium disilicate-based glass ceramic.

PubMed

Prochnow, Catina; Venturini, Andressa B; Grasel, Rafaella; Bottino, Marco C; Valandro, Luiz Felipe

2017-05-01

This study examined the effects of distinct hydrofluoric acid concentrations on the mechanical behavior of a lithium disilicate-based glass ceramic. Bar-shaped specimens were produced from ceramic blocks (e.max CAD, Ivoclar Vivadent). The specimens were polished, chamfered, and sonically cleaned in distilled water. The specimens were randomly divided into five groups (n = 23). The HF1, HF3, HF5, and HF10 specimens were etched for 20 s with acid concentrations of 1%, 3%, 5%, and 10%, respectively, while the SC (control) sample was untreated. The etched surfaces were evaluated using a scanning electron microscope and an atomic force microscope. Finally, the roughness was measured, and 3-point bending flexural tests were performed. The data were analyzed using one-way analysis of variance (ANOVA) and Tukey's test (α = 0.05). The Weibull modulus and characteristic strength were also determined. No statistical difference in the roughness and flexural strength was determined among the groups. The structural reliabilities (Weilbull moduli) were similar for the tested groups; however, the characteristic strength of the HF1 specimen was greater than that of the HF10 specimen. Compared with the untreated ceramic, the surface roughness and flexural strength of the ceramic were unaffected upon etching, regardless of the acid concentration. © 2016 Wiley Periodicals, Inc. J Biomed Mater Res Part B: Appl Biomater, 105B: 885-891, 2017. © 2016 Wiley Periodicals, Inc.

Influence of nanoparticles on color stability, microhardness, and flexural strength of acrylic resins specific for ocular prosthesis.

PubMed

Andreotti, Agda Marobo; Goiato, Marcelo Coelho; Moreno, Amália; Nobrega, Adhara Smith; Pesqueira, Aldiéris Alves; dos Santos, Daniela Micheline

2014-01-01

The aim of this study was to assess the effect of adding nanoparticles to N1 acrylic resin intended for artificial sclera, in terms of the color stability, microhardness, and flexural strength of the resin. Three hundred samples of N1 acrylic resin were used: 100 samples for color stability and microhardness tests (each test was performed on the opposite side of each sample), and 200 samples for flexural strength testing (100 samples before and after 1,008 hours of accelerated aging). Samples for each test were separated into ten groups (n=10), ie, without nanoparticles (control group) or with nanoparticles of zinc oxide, titanium dioxide (TiO₂), and barium sulfate at weight concentrations of 1%, 2%, and 2.5% (nanoparticle groups). Data were subjected to statistical analysis with nested analysis of variance and Tukey's test (P<0.05 significance level). Among the nanoparticle groups, the TiO₂ groups showed better color stability at all concentrations. Microhardness values increased after artificial aging, except for the control and zinc oxide groups. After aging, the 1%-2% TiO₂ groups had significantly higher microhardness values compared with the other nanoparticle groups. Before aging, there was a significant difference in flexural strength between the control and nanoparticle groups. After aging, the control and TiO₂ groups, regardless of concentration, showed the lowest flexural strength values. Incorporation of nanoparticles directly influenced the acrylic resin properties, with TiO₂ being the most influential nanoparticle in terms of the evaluated properties.

[The effect of core veneer thickness ratio on the flexural strength of diatomite-based dental ceramic].

PubMed

Jiang, Jie; Zhang, Xin; Gao, Mei-qin; Zhang, Fei-min; Lu, Xiao-li

2015-06-01

To evaluate the effect of different core veneer thickness ratios on the flexural strength and failure mode of bilayered diatomite-based dental ceramics. Diatomite-based dental ceramics blocks (16 mm×5.4 mm×1 mm) were sintered with different thickness of veneer porcelains: 0 mm (group A), 0.6 mm (group B), 0.8 mm (group C) and 1.0 mm (group D). Flexural strength was detected and scanning electron microscope was used to observe the interface microstructure. Statistical analysis was performed using SPSS 17.0 software package. With the increase of the thickness of the veneer porcelain, flexural strength of group C showed highest flexural strength up to (277.24±5.47) MPa. Different core veneer thickness ratios can significantly influence the flexural strength of bilayered diatomite-based dental ceramics. Supported by Science and Technology Projects of Nantong City (HS2013010).

Stem breakage of salt marsh vegetation under wave forcing: A field and model study

NASA Astrophysics Data System (ADS)

Vuik, Vincent; Suh Heo, Hannah Y.; Zhu, Zhenchang; Borsje, Bas W.; Jonkman, Sebastiaan N.

2018-01-01

One of the services provided by coastal ecosystems is wave attenuation by vegetation, and subsequent reduction of wave loads on flood defense structures. Therefore, stability of vegetation under wave forcing is an important factor to consider. This paper presents a model which determines the wave load that plant stems can withstand before they break or fold. This occurs when wave-induced bending stresses exceed the flexural strength of stems. Flexural strength was determined by means of three-point-bending tests, which were carried out for two common salt marsh species: Spartina anglica (common cord-grass) and Scirpus maritimus (sea club-rush), at different stages in the seasonal cycle. Plant stability is expressed in terms of a critical orbital velocity, which combines factors that contribute to stability: high flexural strength, large stem diameter, low vegetation height, high flexibility and a low drag coefficient. In order to include stem breakage in the computation of wave attenuation by vegetation, the stem breakage model was implemented in a wave energy balance. A model parameter was calibrated so that the predicted stem breakage corresponded with the wave-induced loss of biomass that occurred in the field. The stability of Spartina is significantly higher than that of Scirpus, because of its higher strength, shorter stems, and greater flexibility. The model is validated by applying wave flume tests of Elymus athericus (sea couch), which produced reasonable results with regards to the threshold of folding and overall stem breakage percentage, despite the high flexibility of this species. Application of the stem breakage model will lead to a more realistic assessment of the role of vegetation for coastal protection.

Influence of airborne-particle abrasion on mechanical properties and bond strength of carbon/epoxy and glass/bis-GMA fiber-reinforced resin posts.

PubMed

Soares, Carlos Jose; Santana, Fernanda Ribeiro; Pereira, Janaina Carla; Araujo, Tatiana Santos; Menezes, Murilo Souza

2008-06-01

Controversy exists concerning the use of fiber-reinforced posts to improve bond strength to resin cement because some precementation treatments can compromise the mechanical properties of the posts. The purpose of this study was to analyze the influence of airborne-particle abrasion on the mechanical properties and microtensile bond strength (MTBS) of carbon/epoxy and glass/bis-GMA fiber-reinforced resin posts. Flexural strength (delta(f)), flexural modulus (E(f)), and stiffness (S) were assessed using a 3-point bending test for glass fiber-reinforced and carbon fiber-reinforced resin posts submitted to airborne-particle abrasion (AB) with 50-microm Al(2)O(3), and for posts without any surface treatment (controls) (n=10). Forty glass fiber (GF) and 40 carbon fiber (CF) posts were submitted to 1 of 4 surface treatments (n=10) prior to MTBS testing: silane (S); silane and adhesive (SA); airborne-particle abrasion with 50-microm Al(2)O(3) and silane (ABS); airborne-particle abrasion, silane, and adhesive (ABSA). Two composite resin restorations (Filtek Z250) with rounded depressions in the lateral face were bilaterally fixed to the post with resin cement (RelyX ARC). Next, the specimen was sectioned with a precision saw running perpendicular to the bonded surface to obtain 10 bonded beam specimens with a cross-sectional area of 1 mm(2). Each beam specimen was tested in a mechanical testing machine (EMIC 2,000 DL), under stress, at a crosshead speed of 0.5 mm/min until failure. Data were analyzed by 2-way ANOVA followed by Tukey HSD test (alpha=.05). Failure patterns of tested specimens were analyzed using scanning electron microscopy (SEM). The 3-point bending test demonstrated significant differences among groups only for the post type factor for flexural strength, flexural modulus, and stiffness. The carbon fiber posts exhibited significantly higher mean flexural strength (P=.001), flexural modulus (P=.003), and stiffness (P=.001) values when compared with glass fiber posts, irrespective of surface treatment. An alteration in the superficial structure of the posts could be observed by SEM after airborne-particle abrasion. MTBS testing showed no significant effect for the surface treatment type; however, significant effects for post system factor and for interaction between the 2 factors were observed. For the carbon fiber post, the ABSA surface treatment resulted in values significantly lower than the S surface treatment. SEM analysis of MTBS-tested specimens demonstrated adhesive and cohesive failures. Airborne-particle abrasion did not influence the mechanical properties of the post; however, it produced undesirable surface changes, which could reduce the bond strength to resin cement. For the surface treatments studied, if silane is applied, the adhesive system and airborne-particle abrasion are not necessary.

Mechanical performance of encapsulated restorative glass-ionomer cements for use with Atraumatic Restorative Treatment (ART).

PubMed

Molina, Gustavo Fabián; Cabral, Ricardo Juan; Mazzola, Ignacio; Lascano, Laura Brain; Frencken, Jo E

2013-01-01

The Atraumatic Restorative Treatment (ART) approach was suggested to be a suitable method to treat enamel and dentine carious lesions in patients with disabilities. The use of a restorative glass-ionomer with optimal mechanical properties is, therefore, very important. To test the null-hypotheses that no difference in diametral tensile, compressive and flexural strengths exists between: (1) The EQUIA system and (2) The Chemfil Rock (encapsulated glass-ionomers; test materials) and the Fuji 9 Gold Label and the Ketac Molar Easymix (hand-mixed conventional glass-ionomers; control materials); (3) The EQUIA system and Chemfil Rock. Specimens for testing flexural (n = 240) and diametral tensile (n=80) strengths were prepared according to standardized specifications; the compressive strength (n=80) was measured using a tooth-model of a class II ART restoration. ANOVA and Tukey B tests were used to test for significant differences between dependent and independent variables. The EQUIA system and Chemfil Rock had significantly higher mean scores for all the three strength variables than the Fuji 9 Gold Label and Ketac Molar Easymix (α=0.05). The EQUIA system had significant higher mean scores for diametral tensile and flexural strengths than the Chemfil Rock (α=0.05). The two encapsulated high-viscosity glass-ionomers had significantly higher test values for diametral tensile, flexural and compressive strengths than the commonly used hand-mixed high-viscosity glass-ionomers.

Influence of Waste Tyre Crumb Rubber on Compressive Strength, Static Modulus of Elasticity and Flexural Strength of Concrete

NASA Astrophysics Data System (ADS)

Haridharan, M. K.; Bharathi Murugan, R.; Natarajan, C.; Muthukannan, M.

2017-07-01

In this paper, the experimental investigations was carried out to find the compressive strength, static modulus of elasticity and flexural strength of concrete mixtures, in which natural sand was partially replaced with Waste Tyre Crumb Rubber (WTCR). River sand was replaced with five different percentages (5%, 10%, 15%, 20% and 25%) of WTCR by volume. The main objective of the experimental investigation is to find the relationship between static modulus of elasticity and flexural strength with compressive strength of concrete with WTCR. The experimentally obtainedstatic modulus of elasticity and flexural strength results comparing with the theoretical values (various country codes recommendations).

In vitro evaluation of endodontic posts.

PubMed

Drummond, J L

2000-05-01

To compare stainless steel posts and three different fibrous posts with respect to pullout (shear) strength from extracted third molars embedded in denture acrylic. Post space was prepared and the posts cemented with a resin cement according to manufacturer's instructions. Single step and multi-step dentin bonding systems were also evaluated. The testing was in tension at a loading rate of 2 mm/min. The statistical analysis indicated no significant difference in the pullout (shear) strength between any of the post groups tested. Also evaluated was the flexure strength of the fibrous posts before and after thermal cycling. Statistical analysis indicated a significant decrease in flexure strength for the respective fibrous posts following thermal cycling.

Variation in flexural properties of photo-pultruded composite archwires: analyses of round and rectangular profiles.

PubMed

Fallis, D W; Kusy, R P

2000-11-01

Prototype continuous, unidirectional, fiber-reinforced composite archwires were manufactured into round and rectangular profiles utilizing a photo-pultrusion process. Both 0.022 inch (0.56 mm) diameter and 0.021 x 0.028 inch (0.53 x 0.71 mm) rectangular composites were formed utilizing commercially available S2-glass reinforcement within a polymeric matrix. Reinforcement was varied according to the number, denier and twists per inch (TPI) of four S2-glass yarns to volume levels of 32-74% for round and 41-61% for rectangular profiles. Cross-sectional geometry was evaluated via light microscopy to determine loading characteristics; whereas two flexural properties (the elastic moduli and flexural strengths) were determined by 3-point bending tests. Morphological evaluation of samples revealed that as the TPI increased from 1 to 8, the yarns were more separated from one another and distributed more peripherally within a profile. For round and rectangular profiles utilizing 1 TPI fibers, moduli increased with fiber content approaching theoretical values. For round profiles utilizing 1 TPI and 4 TPI fibers, flexural strengths increased until the loading geometry was optimized. In contrast, the flexural strengths of composites that were pultruded with 8 TPI fibers were not improved at any loading level. Doubling the denier of the yarn, without altering the loading, increased both the moduli and flexural strengths in rectangular samples; whereas, the increases observed in round samples were not statistically significant. At optimal loading the maximum mean moduli and strengths equaled 53.6 +/- 2.0 and 1.36 +/- 0.17 GPa for round wire and equaled 45.7 +/- 0.8 and 1.40 +/- 0.05 GPa for rectangular wires, respectively. These moduli were midway between that of martensitic NiTi (33.4 GPa) and beta-titanium (72.4 GPa), and produced about one-quarter the force of a stainless steel wire per unit of activation. Values of strengths placed this composite material in the range of published values for beta-titanium wires (1.3-1.5 GPa). Copyright 2000 Kluwer Academic Publishers

Effect of Impact Damage and Open Hole on Compressive Strength of Hybrid Composite Laminates

NASA Technical Reports Server (NTRS)

Hiel, Clement; Brinson, H. F.

1993-01-01

Impact damage tolerance is a frequently listed design requirement for composites hardware. The effect of impact damage and open hole size on laminate compressive strength was studied on sandwich beam specimens which combine CFRP-GFRP hybrid skins and a syntactic foam core. Three test specimen configurations have been investigated for this study. The first two were sandwich beams which were loaded in pure bending (by four point flexure). One series had a skin damaged by impact, and the second series had a circular hole machined through one of the skins. The reduction of compressive strength with increasing damage (hole) size was compared. Additionally a third series of uniaxially loaded open hole compression coupons were tested to generate baseline data for comparison with both series of sandwich beams.

Experimental investigation on flexure and impact properties of injection molded polypropylene-nylon 6-glass fiber polymer composites

NASA Astrophysics Data System (ADS)

Nuruzzaman, D. M.; Kusaseh, N. M.; Chowdhury, M. A.; Rahman, N. A. N. A.; Oumer, A. N.; Fatchurrohman, N.; Iqbal, A. K. M. A.; Ismail, N. M.

2018-04-01

In this research study, glass fiber (GF) reinforced polypropylene (PP)-nylon 6 (PA6) polymer blend composites were prepared using injection molding process. Specimens of four different compositions such as 80%PP+20%PA6, 80%PP+18%PA6+2%GF, 80%PP+16%PA6+4%GF and 80%PP+14%PA6+6%GF were prepared. In the injection molding process, suitable process parameters were selected depending on the type of composite specimen in producing defects free dog bone shaped specimens. Flexure and impact tests were carried out according to ASTM standard. The important flexure properties such as flexural modulus, flexural yield strength, flexural strength and flexural strain were investigated. The obtained results revealed that flexural modulus of 80%PP+20%PA6 polymer blend is the lowest and the polymer blend composite shows steadily improved modulus as the glass fiber content is increased. Results also showed that flexural strength of pure polymer blend is the lowest but it improves gradually when the glass fiber content is increased. Impact test results revealed that impact strength of 80%PP+20%PA6 polymer blend is the highest whereas all the composites show reduced impact strength or toughness. It is noticed that 80%PP+14%PA6+6%GF composite exhibits the lowest impact strength.

Mechanical behavior of glass/epoxy composite laminate with varying amount of MWCNTs under different loadings

NASA Astrophysics Data System (ADS)

Singh, K. K.; Rawat, Prashant

2018-05-01

This paper investigates the mechanical response of three phased (glass/MWCNTs/epoxy) composite laminate under three different loadings. Flexural strength, short beam strength and low-velocity impact (LVI) testing are performed to find an optimum doping percentage value for maximum enhancement in mechanical properties. In this work, MWCNTs were used as secondary reinforcement for three-phased composite plate. MWCNT doping was done in a range of 0–4 wt% of the thermosetting matrix system. Symmetrical design eight layered glass/epoxy laminate with zero bending extension coupling laminate was fabricated using a hybrid method i.e. hand lay-up technique followed by vacuum bagging method. Ranging analysis of MWCNT mixing highlighted the enhancement in flexural, short beam strength and improvement in damage tolerance under LVI loading. While at higher doping wt%, agglomeration of MWCNTs are observed. Results of mechanical testing proposed an optimized doping value for maximum strength and damage resistance of the laminate.

Evaluation of post-fire strength of concrete flexural members reinforced with glass fiber reinforced polymer (GFRP) bars

NASA Astrophysics Data System (ADS)

Ellis, Devon S.

Owing to their corrosion resistance and superior strength to weight ratio, there has been, over the past two decades, increased interest in the use of fiber-reinforced polymer (FRP) reinforcing bars in reinforced concrete structural members. The mechanical behavior of FRP reinforcement differs from that of steel reinforcement. For example, FRP reinforcement exhibit a linear stress-strain behavior until the bar ruptures and the strength, stiffness and bond properties of FRP reinforcement are affected more adversely by elevated temperatures. All structures are subject to the risk of damage by fire and fires continue to be a significant cause of damage to structures. Many structures do not collapse after being exposed to fire. The safety of the structure for any future use is dependent on the ability to accurately estimate the post-fire load capacity of the structure. Assuming that the changes, due to fire exposure, in the mechanical behavior of the GFRP reinforcing bar and concrete, and the bond between the reinforcing bar and the concrete are understood, an analytical procedure for estimating the post-fire strength of GFRP reinforced concrete flexural elements can be developed. This thesis investigates the changes in: a) tensile properties and bond of GFRP bars; and b) the flexural behavior of GFRP reinforced concrete beams flexural after being exposed to elevated temperatures up to 400°C and cooled to ambient temperature. To this end, twelve tensile tests, twelve pullout bond tests and ten four-point beam tests were performed. The data from the tests were used to formulate analytical procedures for evaluating the post-fire strength of GFRP reinforced concrete beams. The procedure produced conservative results when compared with the experimental data. In general, the residual tensile strength and modulus of elasticity of GFRP bars decrease as the exposure temperature increases. The loss in properties is however, smaller than that observed by other researchers when similar bars were tested while hot. The residual bond strength was also found to decrease with increase in exposure temperature. Residual bond mechanism and flexural behavior were found to be influenced, in complex ways, by the exposure to elevated temperatures. Additionally, an apparent "yielding plateau" and an apparent increase in bar ductility was observed in the post-heat behavior of some of the tensile specimens. This points to a potential for heat treatment of FRP bars to achieve higher ductility.

Effect of surface acid etching on the biaxial flexural strength of two hot-pressed glass ceramics.

PubMed

Hooshmand, Tabassom; Parvizi, Shaghayegh; Keshvad, Alireza

2008-07-01

The purpose of this study was to assess the effect of surface acid etching on the biaxial flexural strength of two hot-pressed glass ceramics reinforced by leucite or lithium disilicate crystals. Forty glass ceramic disks (14-mm diameter, 2-mm thick) consisting of 20 leucite-based ceramic disks (IPS Empress) and 20 lithia disilicate-based ceramic (IPS Empress 2) were produced by hot-pressing technique. All specimens were polished and then cleaned ultrasonically in distilled water. Ten specimens of each ceramic group were then etched with 9% hydrofluoric (HF) acid gel for 2 minutes and cleaned ultrasonically again. The biaxial flexural strength was measured by the piston-on-three-ball test in a universal testing machine. Data based on ten specimens in each group were analyzed by two-way ANOVA (alpha= 0.05). Microstructure of ceramic surfaces before and after acid etching was also examined by a scanning electron microscope. The mean biaxial flexural strength values for each group tested were (in MPa): nonetched IPS Empress = 118.6 +/- 25.5; etched IPS Empress = 102.9 +/- 15.4; nonetched IPS Empress 2 = 283.0 +/- 48.5; and etched IPS Empress 2 = 250.6 +/- 34.6. The results showed that the etching process reduced the biaxial flexural strengths significantly for both ceramic types (p= 0.025). No significant interaction between the ceramic type and etching process was found (p= 0.407). From the results, it was concluded that surface HF acid etching could have a weakening effect on hot-pressed leucite or lithia disilicate-based glass ceramic systems.

An evaluation of the processing conditions, structure, and properties (biaxial flexural strength and antibacterial efficacy) of sintered strontium-zinc-silicate glass ceramics.

PubMed

Looney, Mark; Shea, Helen O'; Gunn, Lynda; Crowley, Dolores; Boyd, Daniel

2013-05-01

The use of artificial bone grafts has increased in order to satisfy a growing demand for bone replacement materials. Initial mechanical stability of synthetic bone grafts is very advantageous for certain clinical applications. Coupled with the advantage of mechanical strength, a material with inherent antibacterial properties would be very beneficial. A series of strontium-doped zinc silicate (Ca-Sr-Na-Zn-Si) glass ceramics have been characterized in terms of their crystalline structure, biaxial flexural strength and antibacterial efficacy based on the identification of optimum sintering conditions. All three glass ceramics, namely, BT110, BT111, and BT112 were found to be fully crystalline, with BT111 and BT112 comprising of biocompatible crystalline phases. The biaxial flexural strengths of the three glass ceramics ranged from 70 to 149 MPa and were shown to be superior to those of clinically established ceramics in dry conditions and following incubation in simulated physiological conditions. The bacteriostatic effect for each glass ceramic was also established, where BT112 showed an inhibitory effect against three of the most common bacteria found at implantation sites, namely, Enterococcus faecalis, methicillin-resistant Staphylococcus aureus (MRSA), and Pseudomonas aeruginosa. The results of the evaluation suggest that the materials studied offer advantages over current clinical materials and indicate the potential suitability of the glass ceramics as therapeutic bone grafts.

Mechanical properties and superficial characterization of a milled CAD-CAM glass fiber post.

PubMed

Ruschel, George Hebert; Gomes, Érica Alves; Silva-Sousa, Yara Terezinha; Pinelli, Rafaela Giedra Pirondi; Sousa-Neto, Manoel Damião; Pereira, Gabriel Kalil Rocha; Spazzin, Aloísio Oro

2018-06-01

Computer-aided design and computer-aided manufacturing (CAD-CAM) technology may be used to produce custom intraradicular posts, but studies are lacking. The purpose of this in vitro study was to evaluate the flexural properties (strength and modulus), failure mode, superficial morphology, and roughness of two CAD-CAM glass fiber posts (milled at different angulations) compared with a commercially available prefabricated glass fiber post. Three groups were tested (n = 10): PF (control group)- prefabricated glass fiber post; C-Cd-diagonally milled post; and C-Cv-vertically milled post. A 3-dimensional virtual image was obtained from a prefabricated post, which guided the posterior milling of posts from a glass fiber disk (Trilor Blanks; Bioloren). Surface roughness and morphology were evaluated using confocal laser microscopy. Flexural strength and modulus were evaluated with the 3-point bend test. Data were submitted to one-way analysis of variance followed by the Student-Newman-Keuls post hoc test (α = 0.05). The fractured surfaces were evaluated with scanning electron microscopy. The superficial roughness was highest for PF and similar for the experimental groups. Morphological analysis shows different sizes and directions of the glass fibers along the post. The flexural strength was highest for PF (900.1 ± 30.4 > C-Cd - 357.2 ± 30.7 > C-Cv 101.8 ± 4.3 MPa) as was the flexural modulus (PF 19.3 ± 2.0 GPa > C-Cv 10.1 ± 1.9 GPa > C-Cd 7.8 ± 1.3 GPa). A CAD-CAM milled post seems a promising development, but processing requires optimizing, as the prefabricated post still shows better mechanical properties and superficial characteristics. Copyright © 2018 Elsevier Ltd. All rights reserved.

Evaluation of recycled timber members

Treesearch

Douglas R. Rammer

1999-01-01

An experimental study was conducted to evaluate the residual shear capacity of large Douglas-fir timbers used in a military facility in Ardeen Hills, MN. A S-point and 4-point bending test was used to determine the effects of checks and splits on the shear strength capacity. Experimental results are compared to past shear and flexural studies.

Effects of thermal and mechanical fatigue on the flexural strength of G40-600/PMR-15 cross-ply laminates

DOE Office of Scientific and Technical Information (OSTI.GOV)

Roberts, G.D.; Ho, B.Ping Hsiao; Wallace, J.F.

1993-02-01

The effects of thermal and mechanical fatigue on the flexural strength of G40-600/PMR-15 cross-ply laminates with ply orientation of (0(2),90(2))2S and (90(2),0(2))2S are examined. The relative importance of shear and tensile stresses is examined by varying the span-to-depth ratios of flexural test specimens from 8 to 45. Acoustic emission signals are measured during the flexural tests in order to monitor the initiation and growth of damage. Optical microscopy is used to examine specimens for resin cracking, delamination, and fiber breaks after testing. Transverse matrix cracks and delaminations occur in all specimens, regardless of ply orientation, span-to-depth ratio, or previous exposuremore » of specimens to thermal and mechanical fatigue. A small amount of fiber tensile fracture occurs in the outer 0 deg ply of specimens with high span-to-depth ratios. Because of the complex failure modes, the flexural test results represent the apparent strengths rather than the true flexural or shear strengths for these cross-ply laminates. Thermal cycling of specimens prior to flexural testing does not reduce the apparent flexural strength or change the mode of failure. However, fewer acoustic events are recorded at all strains during flexural testing of specimens exposed to prior thermal cycling. High temperature thermal cycling (32 to 260 C, 100 cycles) causes a greater reduction in acoustic events than low temperature thermal cycling (-85 to +85 C, 500 cycles). Mechanical cycling (0 to 50 percent of the flexural strength, 100 cycles) has a similar effect, except that acoustic events are reduced only at strains less than the maximum strain applied during flexural fatigue.« less

Effects of thermal and mechanical fatigue on the flexural strength of G40-600/PMR-15 cross-ply laminates

NASA Technical Reports Server (NTRS)

Roberts, Gary D.; Ho, Barry Ping Hsiao; Wallace, John F.

1993-01-01

The effects of thermal and mechanical fatigue on the flexural strength of G40-600/PMR-15 cross-ply laminates with ply orientation of (0(2),90(2))2S and (90(2),0(2))2S are examined. The relative importance of shear and tensile stresses is examined by varying the span-to-depth ratios of flexural test specimens from 8 to 45. Acoustic emission signals are measured during the flexural tests in order to monitor the initiation and growth of damage. Optical microscopy is used to examine specimens for resin cracking, delamination, and fiber breaks after testing. Transverse matrix cracks and delaminations occur in all specimens, regardless of ply orientation, span-to-depth ratio, or previous exposure of specimens to thermal and mechanical fatigue. A small amount of fiber tensile fracture occurs in the outer 0 deg ply of specimens with high span-to-depth ratios. Because of the complex failure modes, the flexural test results represent the 'apparent' strengths rather than the true flexural or shear strengths for these cross-ply laminates. Thermal cycling of specimens prior to flexural testing does not reduce the apparent flexural strength or change the mode of failure. However, fewer acoustic events are recorded at all strains during flexural testing of specimens exposed to prior thermal cycling. High temperature thermal cycling (32 to 260 C, 100 cycles) causes a greater reduction in acoustic events than low temperature thermal cycling (-85 to +85 C, 500 cycles). Mechanical cycling (0 to 50 percent of the flexural strength, 100 cycles) has a similar effect, except that acoustic events are reduced only at strains less than the maximum strain applied during flexural fatigue.

Fatigue Behavior of Crystalline-Reinforced Glass-Ceramics.

PubMed

Vicari, Carolina Barbosa; Magalhães, Bárbara de Oliveira; Griggs, Jason Alan; Borba, Márcia

2018-01-03

To evaluate the fatigue behavior of two crystalline-reinforced ceramics: leucite-reinforced (VL) and lithium disilicate-based (VD) glass-ceramics. Bar-shaped specimens (16 × 4 × 1.2 mm) were produced for each ceramic using prefabricated CAD/CAM blocks. For each group, 30 specimens were subjected to a three-point flexural strength test in a universal testing machine. For VL and VD, 36 and 41 specimens were subjected to a cyclic fatigue test, respectively. The cyclic fatigue test was performed with a pneumatic mechanical cycling machine (1 Hz; 37°C distilled water). Specimens were tested at two stress levels for each preset lifetime (10 3 and 10 4 cycles for VL; 10 4 and 10 5 cycles for VD) following the boundary technique. Fractography was performed with a scanning electron microscope. Data were analyzed with Weibull analysis. There were significant differences among groups for characteristic strength (σ 0 ) and Weibull modulus (m), as the confidence intervals did not overlap. The VD group presented the highest values of σ 0 , but the lowest Weibull modulus. Both groups showed a reduction of approximately 60% of the initial flexural strength (σ f ) after cycling for 10 4 cycles. For VD tested in fatigue, there was no degradation of σ f when the number of cycles was increased from 10 4 to 10 5 . The VL group showed an 18% decrease in σ f when the number of cycles increased from 10 3 to 10 4 . Flexural strength values estimated for a 5% probability of failure were 36 MPa for VL and 55 MPa for VD, after 10 4 cycles. Both glass-ceramics showed similar strength degradation (60%) after a lifetime of 10 4 cycles, despite their distinct mechanical properties. Mechanical cycling in humid conditions proved to be an important factor for the degradation of the mechanical properties of crystalline-reinforced glass-ceramics. © 2018 by the American College of Prosthodontists.

Mechanical performance of encapsulated restorative glass-ionomer cements for use with Atraumatic Restorative Treatment (ART)

PubMed Central

MOLINA, Gustavo Fabián; CABRAL, Ricardo Juan; MAZZOLA, Ignacio; BRAIN LASCANO, Laura; FRENCKEN, Jo. E.

2013-01-01

The Atraumatic Restorative Treatment (ART) approach was suggested to be a suitable method to treat enamel and dentine carious lesions in patients with disabilities. The use of a restorative glass-ionomer with optimal mechanical properties is, therefore, very important. Objective: To test the null-hypotheses that no difference in diametral tensile, compressive and flexural strengths exists between: (1) The EQUIA system and (2) The Chemfil Rock (encapsulated glass-ionomers; test materials) and the Fuji 9 Gold Label and the Ketac Molar Easymix (hand-mixed conventional glass-ionomers; control materials); (3) The EQUIA system and Chemfil Rock. Material and Methods: Specimens for testing flexural (n=240) and diametral tensile (n=80) strengths were prepared according to standardized specifications; the compressive strength (n=80) was measured using a tooth-model of a class II ART restoration. ANOVA and Tukey B tests were used to test for significant differences between dependent and independent variables. Results: The EQUIA system and Chemfil Rock had significantly higher mean scores for all the three strength variables than the Fuji 9 Gold Label and Ketac Molar Easymix (α=0.05). The EQUIA system had significant higher mean scores for diametral tensile and flexural strengths than the Chemfil Rock (α=0.05). Conclusion: The two encapsulated high-viscosity glass-ionomers had significantly higher test values for diametral tensile, flexural and compressive strengths than the commonly used hand-mixed high-viscosity glass-ionomers. PMID:23857657

Effect of repair resin type and surface treatment on the repair strength of polyamide denture base resin.

PubMed

Gundogdu, Mustafa; Yanikoglu, Nuran; Bayindir, Funda; Ciftci, Hilal

2015-01-01

The purpose of the present study was to evaluate the effects of different repair resins and surface treatments on the repair strength of a polyamide denture base material. Polyamide resin specimens were prepared and divided into nine groups according to the surface treatments and repair materials. The flexural strengths were measured with a 3-point bending test. Data were analyzed with a 2-way analysis of variance, and the post-hoc Tukey test (α=0.05). The effects of the surface treatments on the surface of the polyamide resin were examined using scanning electron microscopy. The repair resins and surface treatments significantly affected the repair strength of the polyamide denture base material (p<0.05); however, no significant differences were observed interaction between the factors (p>0.05). The flexural strength of the specimens repaired with the polyamide resin was significantly higher than that of those repaired with the heat-polymerized and autopolymerizing acrylic resins.

Stress analysis of the space telescope focal plane structure joint

NASA Technical Reports Server (NTRS)

Foster, W. A., Jr.; Shoemaker, W. L.

1985-01-01

Two major efforts were begun concerning the Space Telescope focal plane structure joint. The 3-D solid finite element modeling of the bipod flexure plate was carried out. Conceptual models were developed for the load transfer through the three major bolts to the flexure plate. The flexure plate drawings were reconstructed using DADAM for the purpose of developing a file from which the coordinates of any point on the flexure plate could be determined and also to locate the attachment points of the various components which connect with the flexure plate. For modeling convenience the CADAM drawing of the flexure plate has been divided into several regions which will be subdivided into finite elements using MSGMESH, which is a finite element mesh generator available with MSC/NASTRAN. In addition to the CADAM work on the flexure plate, an effort was also begun to develop computer aided drawings of the peripheral beam which will be used to assist in modeling the connection between it and the flexure plate.

Experimental Study On Flexural Behaviour Of Beams Reinforced With GFRP Rebars

NASA Astrophysics Data System (ADS)

Naveen Kumar, G.; Sundaravadivelu, Karthik

2017-07-01

In saline, moisture and cold conditions corrosion of steel is inevitable and the lot of economy is used for rehabilitation works. Corrosion of steel is nothing but oxidation of iron in moisture conditions and this corrosion leads to the spalling of concrete which intern reduces the strength of the structure. To reduce this corrosion effects, new materials with resistance against corrosion have to be introduced. Many experiments are going on using Glass Fiber Reinforced Polymer (GFRP) as alternate material for steel due to its non-corrosive nature, weight of GFRP is nearly one third of steel and ultimate tensile strength is higher than steel. In this paper, six beams are casted in which three beams are casted with steel as main and shear reinforcement and another three beams are casted with GFRP as main reinforcement with steel as shear reinforcing material. All beams casted are of same dimensions with variation in reinforcement percentage. The size of the beams casted is of length 1200 mm, breadth 100 mm and depth 200 mm. The clear cover of 25 mm is provided on top and bottom of the beam. Beams are tested under two-point loading with constant aspect ratio (a/d) and comparing the flexural strength, load deflection curves and types of failures of beams reinforced with GFRP as main reinforcement and beams reinforced with conventional steel. The final experimental results are compared with numerical results. M30 grade concrete with Conplast as a superplasticizer is used for casting beams.

Effect of air-abrasion regimens and fine diamond bur grinding on flexural strength, Weibull modulus and phase transformation of zirconium dioxide.

PubMed

Michida, Silvia Masae de Araújo; Kimpara, Estevão Tomomitsu; dos Santos, Claudinei; Souza, Rodrigo Othavio Assunção; Bottino, Marco Antonio; Özcan, Mutlu

2015-10-16

This study evaluated the effect of air abrasion and polishing regimens on the flexural strength of yttrium stabilized polycrystalline tetragonal zirconia (Y-TZP). From Y-TZP blocks (InCeram 2000 YZ Cubes; Vita Zahnfabrik, Bad Säckingen, Germany) 120 bars (25 mm × 4 mm × 1.2 mm) were obtained according to ISO 6872:2008 and randomly divided into 4 groups: Group C: (control) without surface treatment (n = 30); Group APA: Air abrasion with aluminum oxide (44 µm) (n = 30); Group SC: Silica-coating (CoJet, 30 µm) (n = 30); Group FD: Fine diamond bur (n = 30). Subsequently, all specimens were subjected to 4-point bending test (in distilled water at 37 °C) in a universal testing machine (EMIC DL 1000; São José dos Pinhais, Paraná, Brazil); cross-head speed: 0.5 mm/min). The characteristic strength (σ0) of each specimen was obtained from the flexural strength test and evaluated using Weibull analysis. X-ray diffraction analysis was utilized to quantity the monoclinic phase. The surface topography of specimens was analyzed using 3D optical profilometer and scanning electron microscopy (SEM) after surface conditioning methods. The flexural strength data (σ4p) were statistically analyzed by 1-way ANOVA, Tukey test (α = 0.05) and Weibull (m = modulus, σ0 = characteristic strength) were calculated. The mean ± standard deviations (MPa) of the groups were as follows: C: 1196.2 ± 284.2a; APA: 1369.7 ± 272.3a; SC: 1207.1 ± 229.7a and FD: 874.4 ± 365.4b. The values (m) and (σ0) were as follows: C: 4.5 and 1308.12; APA: 5.9 and 1477.88; SC: 6.0 and 1300.28; and FD: 2.6 and 985.901, respectively. Air particle abrasion with neither silica nor alumina showed significant difference compared to the control group but grinding with fine diamond bur impaired the flexural strength of the zirconia tested.

Effect of coarse grinding, overglazing, and 2 polishing systems on the flexural strength, surface roughness, and phase transformation of yttrium-stabilized tetragonal zirconia.

PubMed

Mohammadi-Bassir, Mahshid; Babasafari, Mansoure; Rezvani, Mohammad Bagher; Jamshidian, Mahdieh

2017-11-01

Limited information is available for the best polishing systems and methods to obtain minimally abrasive monolithic zirconia surfaces after contouring and occlusal adjustment. The purpose of this in vitro study was to evaluate the effect of grinding and polishing procedures on the flexural strength, quality and quantity of surface roughness, topography, and phase transformation of a zirconia-based ceramic system. Fifty bar-shaped yttrium-stabilized zirconium oxide specimens (20×4×2 mm) were cut from presintered zirconia blanks. The specimens were wet-polished and divided into 5 groups (n=10): standard polishing without any surface treatment (group SP); grinding with a diamond rotary instrument (group Gr); grinding with a diamond rotary instrument (DRI) and over-glazing (group Gl); grinding with a DRI and polishing with an intraoral zirconia polishing kit in a 2-step procedure (group BP); and grinding with a DRI and polishing with an intraoral polishing kit (group MP). The Ra and Rz surface roughness values (μm) were measured with a profilometer. One specimen of each group was subjected to x-ray diffraction (XRD) to estimate the monoclinic phase and evaluated using scanning electron microscopy (SEM) for surface topography. The 3-point flexural strength of the bars was measured in a universal testing machine at a crosshead speed of 0.5 mm/min. The mean flexural strength (MPa) and surface roughness values were calculated, and the results were analyzed using 1-way ANOVA and Tukey honest significant difference tests (α=.05). Statistically significant differences were noted among the experimental groups for Ra, Rz (P<.001), and flexural strength values (P<.001). The highest Ra and Rz values were found in group Gr (P<.001) and the lowest in group Gl, which were significantly lower than the values in group Gr (P<.001). The 2 polishing systems (BP and MP) were not significantly different in terms of Ra and Rz values (P=.755 for Ra and P=.319 for Rz). The highest flexural strength was found in group Gr (283.35 ±49.85 MPa) without significant differences from those of MP and BP (P=.958 for BP and P=.404 for MP). The lowest flexural strength was found in Gl, which had no significant differences from those of the control group (P=1.000). In XRD the monoclinic phase was observed in Gr (26%), BP (24%), and MP (23%) groups. However, groups Gl and SP did not have any monoclinic phase. SEM showed deep unidirectional scratches after grinding that were smoothened by glazing and polishing. Roughness increased significantly after grinding, but polishing and glazing similarly diminished it. Glazing after grinding significantly decreased the flexural strength values, but polishing did not. Copyright © 2017 Editorial Council for the Journal of Prosthetic Dentistry. Published by Elsevier Inc. All rights reserved.

Comparison of flexural properties of aramid-reinforced pultrusions having varied matrices, pretreatments and postcures

NASA Technical Reports Server (NTRS)

Wilson, Maywood L.; Johnson, Gary S.; Macconochie, Ian O.

1987-01-01

Aramid-reinforced composite materials of equal fiber volume and varied polymer thermoset matrices were pultruded and flexurally tested to failure. The objective was to improve the flexural properties of aramid-reinforced pultrusions. Pultrusions of both sized and unsized aramid fiber with four different resin systems were compared to determine the effects of sizing compounds and postcuring on flexural strength, fiber wettability, and fiber-to-resin interface bonding. Improvements in flexural strength resulting from pretreatments with the sizing solutions used were marginal. The most significant improvements in flexural properties resulted from postcuring. Flexural strengths ranged from a low of 39,647 psi (273MPa) to a high of 80,390 psi (554 MPa), an overall increase of 103 percent. The fact that postcuring improved the flexural properties of the pultrusions of the four resin systems indicates that a full cure did not occur in any of the resin systems during the pultrusion process. The increased flexural strengths of the polyester and vinyl ester pultrusions were the most surprising. The four resin systems examined were Interplastic Corporation VE 8300 vinyl ester, Ashland Chemical Company Aropol 7430 Polyester, and Shell Chemical Company Epon 9302 and Epon 9310 epoxides.

Effect of surface treatments on the flexural properties and adhesion of glass fiber-reinforced composite post to self-adhesive luting agent and radicular dentin.

PubMed

Elnaghy, Amr M; Elsaka, Shaymaa E

2016-01-01

This study evaluated the effect of different surface treatments on the flexural properties and adhesion of glass fiber post to self-adhesive luting agent and radicular dentin. Seventy-five single-rooted human teeth were prepared to receive a glass fiber post (Reblida). The posts were divided into five groups according to the surface treatment: Gr C (control; no treatment), Gr S (silanization for 60 s), Gr AP (airborne-particle abrasion), Gr HF (etching with 9 % hydrofluoric acid for 1 min), and Gr M10 (etching with CH2Cl2 for 10 min). Dual-cure self-adhesive luting agent (Rely X Unicem) was applied to each group for testing the adhesion using micropush-out test. Failure types were examined with stereomicroscope and surface morphology of the posts was characterized using a scanning electron microscopy (SEM). Flexural properties of posts were assessed using a three-point bending test. Data were analyzed using ANOVA and Tukey's HSD test. Statistical significance was set at the 0.05 probability level. Groups treated with M10 showed significantly higher bond strength than those obtained with other surface treatments (P < 0.05). In general, improvements in bond strength (MPa) were found in the following order: M10 > C > S > AP > HF. Most failure modes were adhesive type of failures between dentin and luting agent (48.2%). SEM analysis revealed that the fiber post surfaces were modified after surface treatments. The surface treatments did not compromise the flexural properties of fiber posts. Application of M10 to the fiber post surfaces enhanced the adhesion to self-adhesive luting agent and radicular dentin.

Kinetics and mechanics of photo-polymerized triazole-containing thermosetting composites via the copper(I)-catalyzed azide-alkyne cycloaddition

PubMed Central

Song, Han Byul; Wang, Xiance; Patton, James R.; Stansbury, Jeffrey W.; Bowman, Christopher N.

2017-01-01

Objectives Several features necessary for polymer composite materials in practical applications such as dental restorative materials were investigated in photo-curable CuAAC (copper(I)-catalyzed azide-alkyne cycloaddition) thermosetting resin-based composites with varying filler loadings and compared to a conventional BisGMA/TEGDMA based composite. Methods Tri-functional alkyne and di-functional azide monomers were synthesized for CuAAC resins and incorporated with alkyne-functionalized silica microfillers for CuAAC composites. Polymerization kinetics, in situ temperature change, and shrinkage stress were monitored simultaneously with a tensometer coupled with FTIR spectroscopy and a data-logging thermocouple. The glass transition temperature was analyzed by dynamic mechanical analysis. Flexural modulus/strength and flexural toughness were characterized in three-point bending on a universal testing machine. Results The photo-CuAAC polymerization of composites containing between 0 and 60 wt% microfiller achieved ~99% conversion with a dramatic reduction in the maximum heat of reaction (~20 °C decrease) for the 60 wt% filled CuAAC composites as compared with the unfilled CuAAC resin. CuAAC composites with 60 wt% microfiller generated more than twice lower shrinkage stress of 0.43±0.01 MPa, equivalent flexural modulus of 6.1±0.7 GPa, equivalent flexural strength of 107±9 MPa, and more than 10 times higher energy absorption of 10±1 MJ m−3 when strained to 11% relative to BisGMA-based composites at equivalent filler loadings. Significance Mechanically robust and highly tough, photo-polymerized CuAAC composites with reduced shrinkage stress and a modest reaction exotherm were generated and resulted in essentially complete conversion. PMID:28363645

Effect of additive particles on mechanical, thermal, and cell functioning properties of poly(methyl methacrylate) cement

PubMed Central

Khandaker, Morshed; Vaughan, Melville B; Morris, Tracy L; White, Jeremiah J; Meng, Zhaotong

2014-01-01

The most common bone cement material used clinically today for orthopedic surgery is poly(methyl methacrylate) (PMMA). Conventional PMMA bone cement has several mechanical, thermal, and biological disadvantages. To overcome these problems, researchers have investigated combinations of PMMA bone cement and several bioactive particles (micrometers to nanometers in size), such as magnesium oxide, hydroxyapatite, chitosan, barium sulfate, and silica. A study comparing the effect of these individual additives on the mechanical, thermal, and cell functional properties of PMMA would be important to enable selection of suitable additives and design improved PMMA cement for orthopedic applications. Therefore, the goal of this study was to determine the effect of inclusion of magnesium oxide, hydroxyapatite, chitosan, barium sulfate, and silica additives in PMMA on the mechanical, thermal, and cell functional performance of PMMA. American Society for Testing and Materials standard three-point bend flexural and fracture tests were conducted to determine the flexural strength, flexural modulus, and fracture toughness of the different PMMA samples. A custom-made temperature measurement system was used to determine maximum curing temperature and the time needed for each PMMA sample to reach its maximum curing temperature. Osteoblast adhesion and proliferation experiments were performed to determine cell viability using the different PMMA cements. We found that flexural strength and fracture toughness were significantly greater for PMMA specimens that incorporated silica than for the other specimens. All additives prolonged the time taken to reach maximum curing temperature and significantly improved cell adhesion of the PMMA samples. The results of this study could be useful for improving the union of implant-PMMA or bone-PMMA interfaces by incorporating nanoparticles into PMMA cement for orthopedic and orthodontic applications. PMID:24920906

Effect of additive particles on mechanical, thermal, and cell functioning properties of poly(methyl methacrylate) cement.

PubMed

Khandaker, Morshed; Vaughan, Melville B; Morris, Tracy L; White, Jeremiah J; Meng, Zhaotong

2014-01-01

The most common bone cement material used clinically today for orthopedic surgery is poly(methyl methacrylate) (PMMA). Conventional PMMA bone cement has several mechanical, thermal, and biological disadvantages. To overcome these problems, researchers have investigated combinations of PMMA bone cement and several bioactive particles (micrometers to nanometers in size), such as magnesium oxide, hydroxyapatite, chitosan, barium sulfate, and silica. A study comparing the effect of these individual additives on the mechanical, thermal, and cell functional properties of PMMA would be important to enable selection of suitable additives and design improved PMMA cement for orthopedic applications. Therefore, the goal of this study was to determine the effect of inclusion of magnesium oxide, hydroxyapatite, chitosan, barium sulfate, and silica additives in PMMA on the mechanical, thermal, and cell functional performance of PMMA. American Society for Testing and Materials standard three-point bend flexural and fracture tests were conducted to determine the flexural strength, flexural modulus, and fracture toughness of the different PMMA samples. A custom-made temperature measurement system was used to determine maximum curing temperature and the time needed for each PMMA sample to reach its maximum curing temperature. Osteoblast adhesion and proliferation experiments were performed to determine cell viability using the different PMMA cements. We found that flexural strength and fracture toughness were significantly greater for PMMA specimens that incorporated silica than for the other specimens. All additives prolonged the time taken to reach maximum curing temperature and significantly improved cell adhesion of the PMMA samples. The results of this study could be useful for improving the union of implant-PMMA or bone-PMMA interfaces by incorporating nanoparticles into PMMA cement for orthopedic and orthodontic applications.

Kinetics and mechanics of photo-polymerized triazole-containing thermosetting composites via the copper(I)-catalyzed azide-alkyne cycloaddition.

PubMed

Song, Han Byul; Wang, Xiance; Patton, James R; Stansbury, Jeffrey W; Bowman, Christopher N

2017-06-01

Several features necessary for polymer composite materials in practical applications such as dental restorative materials were investigated in photo-curable CuAAC (copper(I)-catalyzed azide-alkyne cycloaddition) thermosetting resin-based composites with varying filler loadings and compared to a conventional BisGMA/TEGDMA based composite. Tri-functional alkyne and di-functional azide monomers were synthesized for CuAAC resins and incorporated with alkyne-functionalized glass microfillers for CuAAC composites. Polymerization kinetics, in situ temperature change, and shrinkage stress were monitored simultaneously with a tensometer coupled with FTIR spectroscopy and a data-logging thermocouple. The glass transition temperature was analyzed by dynamic mechanical analysis. Flexural modulus/strength and flexural toughness were characterized in three-point bending on a universal testing machine. The photo-CuAAC polymerization of composites containing between 0 and 60wt% microfiller achieved ∼99% conversion with a dramatic reduction in the maximum heat of reaction (∼20°C decrease) for the 60wt% filled CuAAC composites as compared with the unfilled CuAAC resin. CuAAC composites with 60wt% microfiller generated more than twice lower shrinkage stress of 0.43±0.01MPa, equivalent flexural modulus of 6.1±0.7GPa, equivalent flexural strength of 107±9MPa, and more than 10 times higher energy absorption of 10±1MJm -3 when strained to 11% relative to BisGMA-based composites at equivalent filler loadings. Mechanically robust and highly tough, photo-polymerized CuAAC composites with reduced shrinkage stress and a modest reaction exotherm were generated and resulted in essentially complete conversion. Copyright © 2017 The Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

An evaluation of the effects of handpiece speed, abrasive characteristics, and polishing load on the flexural strength of polished ceramics.

PubMed

Ahmad, Rohana; Morgano, Steven M; Wu, Benjamin M; Giordano, Russell A

2005-11-01

Many studies on the strengthening effects of grinding and polishing, as well as heat treatment on ceramics, are not well standardized or use commercially available industrial polishing systems. The reported effectiveness of these strengthening mechanisms on ceramics may not be applicable to clinical dentistry. The purpose of this study was to evaluate the effects of controlled polishing on the flexural strength of dental ceramics by using a custom-made machine that applied standardized loads and speeds that coincided with the mean loads and speeds used by experienced prosthodontists. A total of 140 aluminous dental ceramic bar-shaped specimens (Vitadur Alpha Enamel) measuring 1.5 x 2.0 x 25 mm were fabricated and divided into 12 groups (for most groups, n=10). Specimens were untreated, polished with different polishing systems, polished at different speeds, ground and autoglazed, polished and autoglazed, autoglazed and polished, polished with loose (paste) and bonded abrasives, or overglazed. Simulated clinical polishing was performed on the ceramic specimens by using a customized polishing apparatus that allowed independent control over the relevant polishing parameters (abrasive hardness, applied load, linear speed, rotational velocity, and wheel stiffness). Flexural strength (MPa) was measured with a 4-point bending test, and subjective surface roughness was assessed with scanning electron microscopy. Autoglazing was performed at various stages of the polishing sequence to determine the effects of polishing on surface stresses. Mean values, standard deviations, independent-sample t tests, 1-way and 2-way analyses of variance, Dunnett t tests and Kruskal-Wallis tests were applied to the data (alpha=.05). Under a clinical load of 0.6 N for a coarse polishing wheel, 1.0 N for a medium polishing wheel, and 1.3 N for a fine polishing wheel, a linear speed of 499 mm/min, and a rotational velocity of 10,000 rpm, the use of clinical polishing instruments did not affect the flexural strength of the aluminous ceramics studied (P=.274). At higher rotational velocity (20,000 rpm), specimens polished with the diamond polishing system produced statistically weaker specimens compared with those that had been polished at 10,000 rpm (P=.019). Autoglazing treatment of the diamond-polished specimens did not reverse the strength degradation (P=.125). Conversely, diamond polishing of the autoglazed specimens resulted in significant flexural strength reduction (P=.029). Fine-diamond-bonded abrasive significantly reduced flexural strength (P=.025). Simulated clinical polishing at 10,000 rpm did not appear to substantially strengthen or weaken the ceramic specimens. Polishing at 20,000 rpm reduced flexural strength of the ceramic bars.

A Novel Model to Simulate Flexural Complements in Compliant Sensor Systems

PubMed Central

Tang, Hongyan; Zhang, Dan; Guo, Sheng; Qu, Haibo

2018-01-01

The main challenge in analyzing compliant sensor systems is how to calculate the large deformation of flexural complements. Our study proposes a new model that is called the spline pseudo-rigid-body model (spline PRBM). It combines dynamic spline and the pseudo-rigid-body model (PRBM) to simulate the flexural complements. The axial deformations of flexural complements are modeled by using dynamic spline. This makes it possible to consider the nonlinear compliance of the system using four control points. Three rigid rods connected by two revolute (R) pins with two torsion springs replace the three lines connecting the four control points. The kinematic behavior of the system is described using Lagrange equations. Both the optimization and the numerical fitting methods are used for resolving the characteristic parameters of the new model. An example is given of a compliant mechanism to modify the accuracy of the model. The spline PRBM is important in expanding the applications of the PRBM to the design and simulation of flexural force sensors. PMID:29596377

Mechanical behavior of carbon-carbon composites

NASA Technical Reports Server (NTRS)

Rozak, G. A.

1984-01-01

A general background, test plan, and some results of preliminary examinations of a carbon-carbon composite material are presented with emphasis on mechanical testing and inspection techniques. Experience with testing and evaluation was gained through tests of a low modulus carbon-carbon material, K-Karb C. The properties examined are the density - 1.55 g/cc; four point flexure strength in the warp - 137 MPa (19,800 psi) and the fill - 95.1 MPa (13,800 psi,) directions; and the warp interlaminar shear strength - 14.5 MPa (2100 psi). Radiographic evaluation revealed thickness variations and the thinner areas of the composite were scrapped. The ultrasonic C-scan showed attenuation variations, but these did not correspond to any of the physical and mechanical properties measured. Based on these initial tests and a survey of the literature, a plan has been devised to examine the effect of stress on the oxidation behavior, and the strength degradation of coated carbon-carbon composites. This plan will focus on static fatigue tests in the four point flexure mode in an elevated temperature, oxidizing environment.

Evaluation of flexural, diametral tensile, and shear bond strength of composite repairs.

PubMed

Imbery, T A; Gray, T; DeLatour, F; Boxx, C; Best, A M; Moon, P C

2014-01-01

Repairing composite restorations may be a more conservative treatment than replacing the entire restoration. The objective of this in vitro study was to determine the best repair method by measuring flexural, diametral tensile, and shear bond strength of repaired composites in which the surfaces were treated with chemical primers (Add & Bond or Silane Bond Enhancer), a bonding agent (Optibond Solo Plus [OBSP]), or mechanical retention with a bonding agent. Filtek Supreme Ultra shade B1B was placed in special molds to fabricate specimens that served to test the flexural, diametral tensile, or shear strength of the inherent resin substrate. The same molds were modified to make specimens for testing repair strength of the resin. Repairs were made immediately or after aging in deionized water at 37°C for seven days. All repair sites were finished with coarse Sof-Lex discs to simulate finishing new restorations or partially removing aged restorations. Repair surfaces were treated with one of the following: 1) phosphoric-acid etching and OBSP; 2) Add & Bond; 3) phosphoric-acid etching, Silane Bond Enhancer, and OBSP; or 4) quarter round bur, phosphoric-acid etching, and OBSP. Specimens were placed back in the original molds to fabricate specimens for diametral tensile or flexural testing or in an Ultradent jig to make specimens for shear bond testing. Composite resin in shade B5B was polymerized against the treated surfaces to make repairs. Two negative control groups for the three testing methods consisted of specimens in which repairs were made immediately or after aging without any surface treatments. Controls and experimental repairs were aged (water 37°C, 24 hours) before flexural, diametral tensile, or shear testing in an Instron Universal testing machine at a crosshead speed of 0.5 mm/min. Experimental flexural repair strengths ranged from 26.4% to 88.6% of the inherent substrate strength. Diametral tensile repair strengths ranged from 40% to 80% of the inherent substrate strength, and shear bond strength repairs ranged from 56% to 102%. Geometric means were statistically analyzed with two-way analysis of variance on their log-transformed values. Significant differences were determined using Tukey honestly significant difference (p<0.05). Depending on the mechanical property being tested, surface treatments produced different results. OBSP produced more consistent results than chemical primers.

Effects of KMnO4 Treatment on the Flexural, Impact, and Thermal Properties of Sugar Palm Fiber-Reinforced Thermoplastic Polyurethane Composites

NASA Astrophysics Data System (ADS)

Mohammed, A. A.; Bachtiar, D.; Rejab, M. R. M.; Jiang, X. X.; Abas, Falak O.; Abass, Raghad U.; Hasany, S. F.; Siregar, Januar P.

2018-05-01

Global warming has had a great impact on environmental changes since the last decade. Eco-friendly industrial products are of great importance to sustain life on earth, including using natural composites. Natural fibers used as fillers are also environmentally valuable because of their biodegradable nature. However, compatibility issues between the fiber and its respective matrix is a major concern. The present work focused on the study of the flexural, impact, and thermal behaviors of environmentally friendly sugar palm fibers (SPF) incorporated into a composite with thermoplastic polyurethane (TPU). Two techniques (extrusion and compression molding) were used to prepare these composites. The fiber size and dosage were kept constant at 250 µm and 30 wt.% SPF, respectively. The effects of potassium permanganate (KMnO4) treatment on the flexural, impact, and thermal behaviors of the treated SPF with 6% NaOH-reinforced TPU composites were investigated. Three different concentrations of KMnO4 (0.033%, 0.066%, and 0.125%) were studied for this purpose. The characterization of the flexural and impact properties of the new TPU/SPF composites was studied as per American Society for Testing Materials ASTM standards. Thermogravimetric analysis was employed for thermal behavior analysis of the TPU/SPF composites. The best flexural strength, impact strength, and modulus properties (8.118 MPa, 55.185 kJ/m2, and 262.102 MPa, respectively) were obtained with a 0.033% KMnO4-treated sample. However, all flexural strength, impact strength, and modulus properties for the KMnO4-treated samples were lower than the sample treated only with 6% NaOH. The highest thermal stability was also shown by the sample treated with 0.033% KMnO4. Therefore, this method enhanced the thermal properties of the TPU/SPF composites with clear deterioration of the flexural and impact properties.

Strength and microstructure of IPS Empress 2 glass-ceramic after different treatments.

PubMed

Oh, S C; Dong, J K; Lüthy, H; Schärer, P

2000-01-01

This investigation was designed to determine whether heat pressing and/or simulated heat treatments affect the flexure strength and microstructure of the lithium disilicate glass-ceramic of the IPS Empress 2 system. Four groups of the lithium disilicate glass-ceramic were prepared as follows: group 1 = as-received material; group 2 = heat-pressed material; group 3 = heat-pressed and stimulated initial heat-treated material; and group 4 = heat-pressed and simulated heat-treated material with full firings for a final restoration. Three-point bending tests and scanning electron microscopy (SEM) analysis were conducted. The flexure strength of group 2 was significantly higher than that of group 1. However, there were no significant differences in strength among groups 2, 3, and 4, or between groups 1 and 4. The SEM micrographs of the lithium disilicate glass-ceramic showed a closely packed, multidirectionally interlocking microstructure of numerous lithium disilicate crystals protruding from the glass matrix. The crystals in the glass matrix of the heat-pressed materials (groups 2, 3, and 4) were a little more homogeneous and about 2 times bigger than those of the as-received material (group 1). These changes of the microstructure were greatest between groups 1 and 2. However, there were no marked differences among groups 2, 3, and 4. Although there were significant increases in the strength and some changes of the microstructure after the heat-pressing operation, the combination of heat pressing and simulated subsequent heat treatments did not produce an increase of strength of IPS Empress 2 glass-ceramic.

Comparison of the flexural strength of six reinforced restorative materials.

PubMed

Cohen, B I; Volovich, Y; Musikant, B L; Deutsch, A S

2001-01-01

This study calculated the flexural strength for six reinforced restorative materials and demonstrated that flexural strength values can be determined simply by using physical parameters (diametral tensile strength and Young's modulus values) that are easily determined experimentally. A one-way ANOVA analysis demonstrated a statistically significant difference between the two reinforced glass ionomers and the four composite resin materials, with the composite resin being stronger than the glass ionomers.

Influence of nano alumina coating on the flexural bond strength between zirconia and resin cement

PubMed Central

Mumcu, Emre; Şen, Murat

2018-01-01

PURPOSE The purpose of this in vitro study is to examine the effects of a nano-structured alumina coating on the adhesion between resin cements and zirconia ceramics using a four-point bending test. MATERIALS AND METHODS 100 pairs of zirconium bar specimens were prepared with dimensions of 25 mm × 2 mm × 5 mm and cementation surfaces of 5 mm × 2 mm. The samples were divided into 5 groups of 20 pairs each. The groups are as follows: Group I (C) – Control with no surface modification, Group II (APA) – airborne-particle-abrasion with 110 µm high-purity aluminum oxide (Al2O3) particles, Group III (ROC) – airborne-particle-abrasion with 110 µm silica modified aluminum oxide (Al2O3 + SiO2) particles, Group IV (TCS) – tribochemical silica coated with Al2O3 particles, and Group V (AlC) – nano alumina coating. The surface modifications were assessed on two samples selected from each group by atomic force microscopy and scanning electron microscopy. The samples were cemented with two different self-adhesive resin cements. The bending bond strength was evaluated by mechanical testing. RESULTS According to the ANOVA results, surface treatments, different cement types, and their interactions were statistically significant (P<.05). The highest flexural bond strengths were obtained in nanostructured alumina coated zirconia surfaces (50.4 MPa) and the lowest values were obtained in the control group (12.00 MPa), both of which were cemented using a self-adhesive resin cement. CONCLUSION The surface modifications tested in the current study affected the surface roughness and flexural bond strength of zirconia. The nano alumina coating method significantly increased the flexural bond strength of zirconia ceramics. PMID:29503713

Precision tip-tilt-piston actuator that provides exact constraint

DOEpatents

Hale, Layton C.

1999-01-01

A precision device which can precisely actuate three degrees of freedom of an optic mount, commonly referred to as tip, tilt, and piston. The device consists of three identical flexure mechanisms, an optic mount to be supported and positioned, a structure that supports the flexure mechanisms, and three commercially available linear actuators. The advantages of the precision device is in the arrangement of the constraints offered by the flexure mechanism and not in the particular design of the flexure mechanisms, as other types of mechanisms could be substituted. Each flexure mechanism constrains two degrees of freedom in the plane of the mechanisms and one direction is actuated. All other degrees of freedom are free to move within the range of flexure mechanisms. Typically, three flexure mechanisms are equally spaced in angle about to optic mount and arranged so that each actuated degree of freedom is perpendicular to the plane formed by the optic mount. This arrangement exactly constrains the optic mount and allows arbitrary actuated movement of the plane within the range of the flexure mechanisms. Each flexure mechanism provides a mechanical advantage, typically on the order of 5:1, between the commercially available actuator and the functional point on the optic mount. This improves resolution by the same ratio and stiffness by the square of the ratio.

Correlation of processing and sintering variables with the strength and radiography of silicon nitride

NASA Technical Reports Server (NTRS)

Sanders, W. A.; Baaklini, G. Y.

1986-01-01

A sintered Si3N4-SiO2-Y2O3 composition, NASA 6Y, was developed that reached four-point flexural average strength/standard deviation values of 857/36, 544/33, and 462/59 MPa at room temperature, 1200 and 1370 C respectively. These strengths represented improvements of 56, 38, and 21 percent over baseline properties at the three test temperatures. At room temperature the standard deviation was reduced by over a factor of three. These accomplishments were realized by the iterative utilization of conventional x-radiography to characterize structural (density) uniformity as affected by systematic changes in powder processing and sintering parameters. Accompanying the improvement in mechanical properties was a change in the type of flaw causing failure from a pore to a large columnar beta- Si3N4 grain typically 40 to 80 microns long, 10 to 30 microns wide, and with an aspect ratio of 5:1.

Prediction on flexural strength of encased composite beam with cold-formed steel section

NASA Astrophysics Data System (ADS)

Khadavi, Tahir, M. M.

2017-11-01

A flexural strength of composite beam designed as boxed shaped section comprised of lipped C-channel of cold-formed steel (CFS) facing each other with reinforcement bars is proposed in this paper. The boxed shaped is kept restrained in position by a profiled metal decking installed on top of the beam to form a slab system. This profiled decking slab is cast by using self-compacting concrete where the concrete is in compression when load is applied to the beam. Reinforcement bars are used as shear connector between slab and CFS as beam. A numerical analysis method proposed by EC4 is used to predict the flexural strength of the proposed composite beam. It was assumed that elasto-plastic behaviour is developed in the cross -sectional of the proposed beam. The calculated predicted flexural strength of the proposed beam shows reasonable flexural strength for cold-formed composite beam.

Effect of Different Concentration of Sodium Hydroxide [NaOH] on Kenaf Sandwich Structures

NASA Astrophysics Data System (ADS)

Aziz, M.; Halim, Z.; Othman, M.

2018-01-01

Sandwich panels are structures that made of three layers, low-density core inserted in between thin skin layers. This structures allow the achievement of excellent mechanical performance with low weight, thus this characteristic fulfil requirement to be use in aircraft application. In recent time, sandwich structures have been studied due to it has multifunction properties and lightweight. The aim of this study is to fabricate a composite sandwich structures with biodegradable material for face sheet [skin] where the fibre being treat with different concentration of sodium hydroxide [NaOH] with 10 and 20 hours of soaking time. Kenaf fibre [treated] reinforced epoxy will be used as skins and Nomex honeycomb is chosen to perform as core for this sandwich composite structure. The mechanical properties that are evaluated such as flexural strength and impact energy of kenaf fibre-reinforced epoxy sandwich structures. For flexural test, the optimum flexural strength is 13.4 MPa and impact strength is 18.3 J.

Effect of thickness and surface modifications on flexural strength of monolithic zirconia.

PubMed

Ozer, Fusun; Naden, Andrew; Turp, Volkan; Mante, Francis; Sen, Deniz; Blatz, Markus B

2017-10-14

A recommended minimum thickness for monolithic zirconia restorations has not been reported. Assessing a proper thickness that has the necessary load-bearing capacity but also conserves dental hard tissues is essential. The purpose of this in vitro study was to evaluate the effect of thickness and surface modifications on monolithic zirconia after simulated masticatory stresses. Monolithic zirconia disks (10 mm in diameter) were fabricated with 1.3 mm and 0.8 mm thicknesses. For each thickness, 21 disks were fabricated. The specimens of each group were further divided into 3 subgroups (n=7) according to the surface treatments applied: untreated (control), airborne-particle abrasion with 50-μm Al 2 O 3 particles at a pressure of 400 kPa at 10 mm, and grinding with a diamond rotary instrument followed by polishing. The biaxial flexure strength was determined by using a piston-on-3-balls technique in a universal testing machine. Flexural loading was applied with a 1.4-mm diameter steel cylinder, centered on the disk, at a crosshead speed of 0.5 mm/min until fracture occurred. X-ray diffraction (XRD) and scanning electron microscopy (SEM) analyses were performed. The data were statistically analyzed with 2-way ANOVA, Tamhane T2, 1-way ANOVA, and Student t tests (α=.05). The 1.3-mm specimens had significantly higher flexural strength than the 0.8-mm specimens (P<.05). Airborne-particle abrasion significantly increased the flexural strength (P<.05). Grinding and polishing did not affect the flexural strength of the specimens (P>.05). The mean flexural strength of 0.8-mm and 1.3-mm thick monolithic zirconia was greater than reported masticatory forces. Airborne-particle abrasion increased the flexural strength of monolithic zirconia. Grinding did not affect flexural strength if subsequently polished. Copyright © 2017 Editorial Council for the Journal of Prosthetic Dentistry. Published by Elsevier Inc. All rights reserved.

Specimen geometry effects on graphite/PMR-15 composites during thermo-oxidative aging

NASA Technical Reports Server (NTRS)

Bowles, K. J.; Meyers, A.

1986-01-01

Studies were conducted to establish the effects of specimen geometry on the thermo-oxidative stability and the mechanical properties retention of unidirectional Celion 12000 graphite fiber reinforced PMR-15 polyimide composites. Weight loss, flexural strength and interlaminar shear strength are measured at isothermal aging times as long as 1639 hr at a temperature of 316 C for three different specimen geometries. It is found that the three different types of specimen surfaces exhibit different values of weight loss/unit area. The mechanical properties retention is also found to be dependent on geometry for these composites. The interlaminar shear strength decreases significantly over the complete range of aging times. The flexural strength retention starts showing geometric dependency after about 1000 hr of aging at 316C. Weight loss fluxes, associated with the three different types of exposed surfaces, are calculated and used to develop an empirical mathematical model for predicting the weight loss behavior of unidirectional composites of arbitrary geometries. Data are presented comparing experimentally determined weight loss with weight loss values predicted using the empirical model.

Specimen geometry effects on graphite/PMR-15 composites during thermo-oxidative aging

NASA Technical Reports Server (NTRS)

Bowles, K. J.; Meyers, A.

1986-01-01

Studies were conducted to establish the effects of specimen geometry on the thermo-oxidative stability and the mechanical properties retention of unidirectional Celion 12000 graphite fiber reinforced PMR-15 polyimide composites. Weight loss, flexural strength and interlaminar shear strength are measured at isothermal aging times as long as 1639 hr at a temperature of 316 C for three different specimen geometries. It is found that the three different types of specimen surfaces exhibit different values of weight loss/unit area. The mechanical properties retention is also found to be dependent on geometry for these composites. The interlaminar shear strength decreases significantly over the complete range of aging times. The flexural strength retention starts showing geometric dependency after about 1000 hr of aging at 316 C. Weight loss fluxes, associated with the three different types of exposed surfaces, are calculated and used to develop an empirical mathematical model for predicting the weight loss behavior of unidirectional composites of arbitrary geometries. Data are presented comparing experimentally determined weight loss with weight loss values predicted using the empirical model.

Accelerated aging characteristics of three yttria-stabilized tetragonal zirconia polycrystalline dental materials.

PubMed

Flinn, Brian D; deGroot, Dirk A; Mancl, Lloyd A; Raigrodski, Ariel J

2012-10-01

Concerns have been expressed about the effect of aging on the mechanical properties of zirconia. The purpose of this study was to assess the accelerated aging characteristics of 3 commercially available yttria-stabilized tetragonal zirconia polycrystalline (Y-TZP) materials by exposing specimens to hydrothermal treatments at 134°C, 0.2 MPa and 180°C, 1.0 MPa in steam. Thin bars of Y-TZP from 3 manufacturers, Lava, Zirkonzahn, and Zirprime, n=30 for each brand (22 × 3 × 0.2 mm), were cut and ground from blocks and sintered according to the manufacturer's specifications. Control specimens (n=10) for each brand were evaluated in the as-received condition. Experimental specimens were artificially aged at standard autoclave sterilization conditions,134°C at 0.2 MPa (n=5 per group at 50, 100, 150, and 200 hours) and standard industrial ceramic aging conditions, 180°C at 1.0 MPa (n=5 per group at 8, 16, 24, 28, and 48 hours). Tetragonal to monoclinic transformation was measured by using X-ray diffraction (XRD) for all groups. Flexural strength was measured in 4-point bending (ASTM1161-B) for all groups. Fracture surfaces were examined by scanning electron microscopy (SEM). Data were analyzed as a function of aging time. The statistical comparisons were based on the log value and 2-way ANOVA with heteroscedasticity-consistent standard errors used to compare mean strength among conditions (α=.05). After 200 hours at 134°C and 0.2 MPa, flexural strength (SD) decreased significantly from 1156 (87.6) MPa to 829.5 (71) MPa for Lava; 1406 (243) MPa to 882.7 (91) MPa for Zirkonzahn; and 1126 (92.4) MPa to 976 (36.4) MPa for Zirprime with P<.001 for all 3 comparisons. After 200 hours at 134°C and 0.2 MPa, some tetragonal crystals transformed to the monoclinic phase. The relative XRD peak intensity of the monoclinic to tetragonal crystal phases increased from 0.07 to 1.82 for Lava, from 0.06 to 2.43 for Zirkonzahn, and from 0.05 to 0.53 for Zirprime. After 28 hours at 180°C and 1.0 MPa, all Lava and Zirkonzahn specimens spontaneously fractured during aging. The Noritake specimens were intact after 48 hours, and the flexural strength showed no significant change, 1156 (87.6) MPa to 1122 (108) MPa. The flexural strength decreased with an increase in the monoclinic phase. SEM micrographs revealed a transformed layer on the fracture surfaces. Hydrothermal aging of Y-TZP can cause significant transformation from tetragonal to monoclinic crystal structure, which results in a statistically significant decrease in the flexural strength of thin bars. Although the strengths of all 3 Y-TZP materials are higher than other materials used for ceramic restorations, there are notable differences among them. Copyright © 2012 The Editorial Council of the Journal of Prosthetic Dentistry. Published by Mosby, Inc. All rights reserved.

Flexural properties, morphology and bond strength of fiber-reinforced posts: influence of post pretreatment.

PubMed

Braga, Neilor Mateus Antunes; Souza-Gabriel, Aline Evangelista; Messias, Danielle Cristine Furtado; Rached-Junior, Fuad Jacob Abi; Oliveira, Camila Fávero; Silva, Ricardo Gariba; Silva-Sousa, Yara T Corrêa

2012-01-01

The aim of this study was to assess the influence of surface pretreatments of fiber-reinforced posts on flexural strength (FS), modulus of elasticity (ME) and morphology of these posts, as well as the bond strength (BS) between posts and core material. Fifty-two fiber posts (smooth and serrated) were assigned to 4 groups (n=13): no treatment (control), 10% hydrogen peroxide (HP) for 10 min (HP-10), 24% HP for 1 min (HP-24) and airborne-particle abrasion (Al(2)O(3)). To evaluate FS and ME, a 3-point bending test was performed. Three posts of each group were examined by scanning electron microscopy. Composite resin was used as the core build-up and samples were sectioned to obtain microtensile sticks. Data were analyzed by ANOVA and Tukey's test (α=0.05). For FS, significant differences were observed between posts type and surface pretreatment (p<0.05), with the highest means for the smooth posts. Al2O3 provided higher FS than HP-24. Al(2)O(3) promoted higher ME than HP-24 and control. SEM images revealed partial dissolution of the resin matrix in all treated groups. The smooth posts had higher BS and FS than serrated posts (p<0.05). Mechanical properties of the glass fiber posts and the bond strength between posts and composite material were not altered by the surface treatments, except for airborne-particle abrasion that increased the post elastic modulus.

Analytical Modeling for Mechanical Strength Prediction with Raman Spectroscopy and Fractured Surface Morphology of Novel Coconut Shell Powder Reinforced: Epoxy Composites

NASA Astrophysics Data System (ADS)

Singh, Savita; Singh, Alok; Sharma, Sudhir Kumar

2017-06-01

In this paper, an analytical modeling and prediction of tensile and flexural strength of three dimensional micro-scaled novel coconut shell powder (CSP) reinforced epoxy polymer composites have been reported. The novel CSP has a specific mixing ratio of different coconut shell particle size. A comparison is made between obtained experimental strength and modified Guth model. The result shows a strong evidence for non-validation of modified Guth model for strength prediction. Consequently, a constitutive modeled equation named Singh model has been developed to predict the tensile and flexural strength of this novel CSP reinforced epoxy composite. Moreover, high resolution Raman spectrum shows that 40 % CSP reinforced epoxy composite has high dielectric constant to become an alternative material for capacitance whereas fractured surface morphology revealed that a strong bonding between novel CSP and epoxy polymer for the application as light weight composite materials in engineering.

Comparison of mechanical properties of three machinable ceramics with an experimental fluorophlogopite glass ceramic.

PubMed

Leung, Brian T W; Tsoi, James K H; Matinlinna, Jukka P; Pow, Edmond H N

2015-09-01

Fluorophlogopite glass ceramic (FGC) is a biocompatible, etchable, and millable ceramic with fluoride releasing property. However, its mechanical properties and reliability compared with other machinable ceramics remain undetermined. The purpose of this in vitro study was to compare the mechanical properties of 3 commercially available millable ceramic materials, IPS e.max CAD, Vitablocs Mark II, and Vita Enamic, with an experimental FGC. Each type of ceramic block was sectioned into beams (n=15) of standard dimensions of 2×2×15 mm. Before mechanical testing, specimens of the IPS e.max CAD group were further fired for final crystallization. Flexural strength was determined by the 3-point bend test with a universal loading machine at a cross head speed of 1 mm/min. Hardness was determined with a hardness tester with 5 Vickers hardness indentations (n=5) using a 1.96 N load and a dwell time of 15 seconds. Selected surfaces were examined by scanning electron microscopy and energy-dispersive x-ray spectroscopy. Data were analyzed by the 1-way ANOVA test and Weibull analysis (α=.05). Weibull parameters, including the Weibull modulus (m) as well as the characteristic strength at 63.2% (η) and 10.0% (B10), were obtained. A significant difference in flexural strength (P<.001) was found among groups, with IPS e.max CAD (341.88 ±40.25 MPa)>Vita Enamic (145.95 ±12.65 MPa)>Vitablocs Mark II (106.67 ±18.50 MPa), and FGC (117.61 ±7.62 MPa). The Weibull modulus ranged from 6.93 to 18.34, with FGC showing the highest Weibull modulus among the 4 materials. The Weibull plot revealed that IPS e.max CAD>Vita Enamic>FGC>Vitablocs Mark II for the characteristic strength at both 63.2% (η) and 10.0% (B10). Significant difference in Vickers hardness among groups (P<.001) was found with IPS e.max CAD (731.63 ±30.64 H(V))>Vitablocs Mark II (594.74 ±25.22 H(V))>Vita Enamic (372.29 ±51.23 H(V))>FGC (153.74 ±23.62 H(V)). The flexural strength and Vickers hardness of IPS e.max CAD were significantly higher than those of the 3 materials tested. The FGC's flexural strength was comparable with Vitablocs Mark II. The FGC's Weibull modulus was the highest, while its Vickers hardness was the lowest among the materials tested. Copyright © 2015 Editorial Council for the Journal of Prosthetic Dentistry. Published by Elsevier Inc. All rights reserved.

Argon Ion Laser Polymerized Acrylic Resin: A Comparative Analysis of Mechanical Properties of Laser Cured, Light Cured and Heat Cured Denture Base Resins

PubMed Central

Murthy, S Srinivasa; Murthy, Gargi S

2015-01-01

Background: Dentistry in general and prosthodontics in particular is evolving at greater pace, but the denture base resins poly methyl methacrylate. There has been vast development in modifying chemically and the polymerization techniques for better manipulation and enhancement of mechanical properties. One such invention was introduction of visible light cure (VLC) denture base resin. Argon ion lasers have been used extensively in dentistry, studies has shown that it can polymerize restorative composite resins. Since composite resin and VLC resin share the same photo initiator, Argon laser is tested as activator for polymerizing VLC resin. In the Phase 1 study, the VLC resin was evaluated for exposure time for optimum polymerization using argon ion laser and in Phase 2; flexural strength, impact strength, surface hardness and surface characteristics of laser cured resin was compared with light cure and conventional heat cure resin. Materials and Methods: Phase 1; In compliance with American Dental Association (ADA) specification no. 12, 80 samples were prepared with 10 each for different curing time using argon laser and evaluated for flexural strength on three point bend test. Results were compared to established performance requirement specified. Phase 2, 10 specimen for each of the mechanical properties (30 specimen) were polymerized using laser, visible light and heat and compared. Surface and fractured surface of laser, light and heat cured resins were examined under scanning electron microscope (SEM). Results: In Phase 1, the specimen cured for 7, 8, 9 and 10 min fulfilled ADA requirement. 8 min was taken as suitable curing time for laser curing. Phase 2 the values of mechanical properties were computed and subjected to statistical analysis using one-way ANOVA and Tukey post-hoc test. The means of three independent groups showed significant differences between any two groups (P < 0.001). Conclusion: Triad VLC resin can be polymerized by argon ion laser with 1 W/mm2 power and exposure time of 8 min to satisfy ADA specification. Impact strength, surface hardness of laser cure was better than light cure and heat cure resin. Flexural strength of light cure was better than laser cure and heat cure resin. The SEM study showed similar density on surface, the fractured surface of heat cure resin was dense and compact. PMID:26124596

Effect of Heat-Pressing Temperature and Holding Time on the Microstructure and Flexural Strength of Lithium Disilicate Glass-Ceramics

PubMed Central

Gao, Jing; Wang, Hui; Chen, Jihua

2015-01-01

The present study aimed to evaluate the influence of various heat-pressing procedures (different holding time and heat pressing temperature) on the microstructure and flexural strength of lithium disilicate glass ceramic. An experimental lithium silicate glass ceramic (ELDC) was prepared from the SiO2-Li2O-K2O-Al2O3-ZrO2-P2O5 system and heat-pressed following different procedures by varying temperature and holding time. The flexural strength was tested and microstructure was analyzed. The relationships between the microstructure, mechanical properties and heat-pressing procedures were discussed in-depth. Results verified the feasibility of the application of dental heat-pressing technique in processing the experimental lithium disilicate glass ceramic. Different heat-pressing procedures showed significant influence on microstructure and flexural strength. ELDC heat-pressed at 950℃ with holding time of 15 min achieved an almost pore-free microstructure and the highest flexural strength, which was suitable for dental restorative application. PMID:25985206

Effects of Ceramic Density and Sintering Temperature on the Mechanical Properties of a Novel Polymer-Infiltrated Ceramic-Network Zirconia Dental Restorative (Filling) Material.

PubMed

Li, Weiyan; Sun, Jian

2018-05-10

BACKGROUND Polymer-infiltrated ceramic-network (PICN) dental material is a new and practical development in orthodontics. Sintering is the process of forming a stable solid mass from a powder by heating without melting. The aim of this study was to evaluate the effects of sintering temperature on the mechanical properties of a PICN zirconia dental material. MATERIAL AND METHODS A dense zirconia ceramic and four PICN zirconia dental materials, with varying porosities, were sintered at three different temperatures; 12 PICN zirconia dental materials based on these porous ceramics were prepared, as well as a pure polymer. After the specimen preparation, flexural strength and elastic modulus values were measured using the three-point bending test, and fracture toughness were determined by the single-edge notched beam (SENB) method. The Vickers hardness test method was used with an indentation strength (IS) test. Scanning electron microscopy (SEM) was used to examine the microstructure of the ceramic surface and the fracture surface. RESULTS Mechanical properties of the PICN dental materials, including flexural strength, elastic modulus, fracture toughness, and hardness, were more similar to the properties of natural teeth when compared with traditional dental ceramic materials, and were affected by the density and sintering temperature. SEM showed that the porous ceramic network became cohesive and that the length of cracks in the PICN dental material was reduced. CONCLUSIONS PICN zirconia dental materials were characterized by similar mechanical properties to natural dental tissues, but further studies are required continue to improve the similarities with natural human enamel and dentin.

Effects of Ceramic Density and Sintering Temperature on the Mechanical Properties of a Novel Polymer-Infiltrated Ceramic-Network Zirconia Dental Restorative (Filling) Material

PubMed Central

Li, Weiyan

2018-01-01

Background Polymer-infiltrated ceramic-network (PICN) dental material is a new and practical development in orthodontics. Sintering is the process of forming a stable solid mass from a powder by heating without melting. The aim of this study was to evaluate the effects of sintering temperature on the mechanical properties of a PICN zirconia dental material. Material/Methods A dense zirconia ceramic and four PICN zirconia dental materials, with varying porosities, were sintered at three different temperatures; 12 PICN zirconia dental materials based on these porous ceramics were prepared, as well as a pure polymer. After the specimen preparation, flexural strength and elastic modulus values were measured using the three-point bending test, and fracture toughness were determined by the single-edge notched beam (SENB) method. The Vickers hardness test method was used with an indentation strength (IS) test. Scanning electron microscopy (SEM) was used to examine the microstructure of the ceramic surface and the fracture surface. Results Mechanical properties of the PICN dental materials, including flexural strength, elastic modulus, fracture toughness, and hardness, were more similar to the properties of natural teeth when compared with traditional dental ceramic materials, and were affected by the density and sintering temperature. SEM showed that the porous ceramic network became cohesive and that the length of cracks in the PICN dental material was reduced. Conclusions PICN zirconia dental materials were characterized by similar mechanical properties to natural dental tissues, but further studies are required continue to improve the similarities with natural human enamel and dentin. PMID:29746449

Polymerization Behavior and Mechanical Properties of High-Viscosity Bulk Fill and Low Shrinkage Resin Composites.

PubMed

Shibasaki, S; Takamizawa, T; Nojiri, K; Imai, A; Tsujimoto, A; Endo, H; Suzuki, S; Suda, S; Barkmeier, W W; Latta, M A; Miyazaki, M

The present study determined the mechanical properties and volumetric polymerization shrinkage of different categories of resin composite. Three high viscosity bulk fill resin composites were tested: Tetric EvoCeram Bulk Fill (TB, Ivoclar Vivadent), Filtek Bulk Fill posterior restorative (FB, 3M ESPE), and Sonic Fill (SF, Kerr Corp). Two low-shrinkage resin composites, Kalore (KL, GC Corp) and Filtek LS Posterior (LS, 3M ESPE), were used. Three conventional resin composites, Herculite Ultra (HU, Kerr Corp), Estelite ∑ Quick (EQ, Tokuyama Dental), and Filtek Supreme Ultra (SU, 3M ESPE), were used as comparison materials. Following ISO Specification 4049, six specimens for each resin composite were used to determine flexural strength, elastic modulus, and resilience. Volumetric polymerization shrinkage was determined using a water-filled dilatometer. Data were evaluated using analysis of variance followed by Tukey's honestly significant difference test (α=0.05). The flexural strength of the resin composites ranged from 115.4 to 148.1 MPa, the elastic modulus ranged from 5.6 to 13.4 GPa, and the resilience ranged from 0.70 to 1.0 MJ/m 3 . There were significant differences in flexural properties between the materials but no clear outliers. Volumetric changes as a function of time over a duration of 180 seconds depended on the type of resin composite. However, for all the resin composites, apart from LS, volumetric shrinkage began soon after the start of light irradiation, and a rapid decrease in volume during light irradiation followed by a slower decrease was observed. The low shrinkage resin composites KL and LS showed significantly lower volumetric shrinkage than the other tested materials at the measuring point of 180 seconds. In contrast, the three bulk fill resin composites showed higher volumetric change than the other resin composites. The findings from this study provide clinicians with valuable information regarding the mechanical properties and polymerization kinetics of these categories of current resin composite.

The effect of filler loading and morphology on the mechanical properties of contemporary composites.

PubMed

Kim, Kyo-Han; Ong, Joo L; Okuno, Osamu

2002-06-01

Little information exists regarding the filler morphology and loading of composites with respect to their effects on selected mechanical properties and fracture toughness. The objectives of this study were to: (1) classify commercial composites according to filler morphology, (2) evaluate the influence of filler morphology on filler loading, and (3) evaluate the effect of filler morphology and loading on the hardness, flexural strength, flexural modulus, and fracture toughness of contemporary composites. Field emission scanning electron microscopy/energy dispersive spectroscopy was used to classify 3 specimens from each of 14 commercial composites into 4 groups according to filler morphology. The specimens (each 5 x 2.5 x 15 mm) were derived from the fractured remnants after the fracture toughness test. Filler weight content was determined by the standard ash method, and the volume content was calculated using the weight percentage and density of the filler and matrix components. Microhardness was measured with a Vickers hardness tester, and flexural strength and modulus were measured with a universal testing machine. A 3-point bending test (ASTM E-399) was used to determine the fracture toughness of each composite. Data were compared with analysis of variance followed by Duncan's multiple range test, both at the P<.05 level of significance. The composites were classified into 4 categories according to filler morphology: prepolymerized, irregular-shaped, both prepolymerized and irregular-shaped, and round particles. Filler loading was influenced by filler morphology. Composites containing prepolymerized filler particles had the lowest filler content (25% to 51% of filler volume), whereas composites containing round particles had the highest filler content (59% to 60% of filler volume). The mechanical properties of the composites were related to their filler content. Composites with the highest filler by volume exhibited the highest flexural strength (120 to 129 MPa), flexural modulus (12 to 15 GPa), and hardness (101 to 117 VHN). Fracture toughness was also affected by filler volume, but maximum toughness was found at a threshold level of approximately 55% filler volume. Within the limitations of this study, the commercial composites tested could be classified by their filler morphology. This property influenced filler loading. Both filler morphology and filler loading influenced flexural strength, flexural modulus, hardness, and fracture toughness.

Flexural Behavior of Aluminum Honeycomb Core Sandwich Structure

NASA Astrophysics Data System (ADS)

Matta, Vidyasagar; Kumar, J. Suresh; Venkataraviteja, Duddu; Reddy, Guggulla Bharath Kumar

2017-05-01

This project is concerned with the fabrication and flexural testing of aluminium honey comb sandwich structure which is a special case of composite materials that is fabricated by attaching two thin but stiff skins to a light weight but thick core. The core material is normally low density material but its high thickness provide the sandwich composite with high bonding stiffness. Honeycomb core are classified into two types based on the materials and structures. Hexagonal shape has a unique properties i.e has more bonding strength and less formation time based on the cell size and sheet thickness. Sandwich structure exhibit different properties such as high load bearing capacity at low weight and has excellent thermal insulation. By considering the above properties it has tendency to minimize the structural problem. So honey comb sandwich structure is choosed. The core structure has a different applications such as aircraft, ship interiors, construction industries. As there is no proper research on strength characteristics of sandwich structure. So, we use light weight material to desire the strength. There are different parameters involved in this structure i.e cell size, sheet thickness and core height. In this project we considered 3 level of comparison among the 3 different parameters cell size of 4, 6 and 8 mm, sheet thickness of 0.3, 0.5 and 0.7 mm, and core height of 20,25 and 30 mm. In order to reduce the number of experiment we use taguchi design of experiment, and we select the L8 orthogonal array is the best array for this type of situation, which clearly identifies the parameters by independent of material weight to support this we add the minitab software, to identify the main effective plots and regression equation which involves the individual response and corresponding parameters. Aluminium material is used for the fabrication of Honeycomb sandwich structure among the various grades of aluminium we consider the AL6061 which is light weight material and has more strength. By the power press used as forming method we fabricate the honey comb core and stacking the sheets with adhesive as epoxy resin or laser beam welding and sandwich structure will form with two face sheets. Then the specimen is taken to be tested to know the flexural behaviour by the flexural test as 3 point and 4 pont bend test. After testing of two different tests then we get the force vs displacement curve by this we can know the maximum force and by loading configurations and its displacement or deflection then we can calculate flexural stiffness and core shear modulus by the variation of three parameters. Our ultimate aim is to achieve maximum strength by minimum weight.

Comparison of different grinding procedures on the flexural strength of zirconia.

PubMed

Işeri, Ufuk; Ozkurt, Zeynep; Yalnız, Ayşe; Kazazoğlu, Ender

2012-05-01

The surface of zirconia ceramic is damaged during grinding, which may affect the mechanical properties of the material. The purpose of this study was to compare the biaxial flexural strength of zirconia after different grinding procedures and to measure the temperature rise from grinding. Forty disk-shaped zirconia specimens (15 × 1.2 mm) with a smaller disk in the center of each disk (1 × 3 mm) were divided into 4 groups (n=10). The specimens were ground with a high-speed handpiece and micromotor with 2 different grinding protocols, continual grinding and periodic grinding (10 seconds grinding with 10 seconds duration), until the smaller disk was removed. Control specimens without the center disk (n=10) were analyzed without grinding. The biaxial flexural strengths of the disks were determined in a universal testing machine at a crosshead speed of 0.5 mm/min. The fracture strength (MPa) was recorded, and the results were analyzed using a 1-way ANOVA, Tukey HSD test, Student's t test, and Pearson correlation test (α=05). All grinding procedures significantly decreased flexural strength (P<.01). The mean flexural strength of the high-speed handpiece groups was higher (815 MPa) than that of the micromotor groups (718 MPa). The temperature values obtained from micromotor grinding (127°C) were significantly higher than those from high-speed handpiece grinding (63°C) (P<.01). Grinding zirconia decreased flexural strength. Zirconia material ground with a high-speed handpiece run continually caused the least reduction in flexural strength. Copyright © 2012 The Editorial Council of the Journal of Prosthetic Dentistry. Published by Mosby, Inc. All rights reserved.

Preparation and characterisation of poly p-phenylene-2,6-benzobisoxazole fibre-reinforced resin matrix composite for endodontic post material: a preliminary study.

PubMed

Hu, Chen; Wang, Feng; Yang, Huiyong; Ai, Jun; Wang, Linlin; Jing, Dongdong; Shao, Longquan; Zhou, Xingui

2014-12-01

Currently used fibre-reinforced composite (FRC) intracanal posts possess low flexural strength which usually causes post fracture when restoring teeth with extensive loss. To improve the flexural strength of FRC, we aimed to apply a high-performance fibre, poly p-phenylene-2, 6-benzobisoxazole (PBO), to FRCs to develop a new intracanal post material. To improve the interfacial adhesion strength, the PBO fibre was treated with coupling agent (Z-6040), argon plasma, or a combination of above two methods. The effects of the surface modifications on PBO fibre were characterised by determining the single fibre tensile strength and interfacial shear strength (IFSS). The mechanical properties of PBO FRCs were characterised by flexural strength and flexural modulus. The cytotoxicity of PBO FRC was evaluated by the MTT assay. Fibres treated with a combination of Z-6040 and argon plasma possessed a significantly higher IFSS than untreated fibres. Fibre treated with the combination of Z-6040-argon-plasma FRC had the best flexural strength (531.51 ± 26.43MPa) among all treated fibre FRCs and had sufficient flexural strength and appropriate flexural moduli to be used as intracanal post material. Furthermore, an in vitro cytotoxicity assay confirmed that PBO FRCs possessed an acceptable level of cytotoxicity. In summary, our study verified the feasibility of using PBO FRC composites as new intracanal post material. Although the mechanical property of PBO FRC still has room for improvement, our study provides a new avenue for intracanal post material development in the future. To our knowledge, this is the first study to verify the feasibility of using PBO FRC composites as new intracanal post material. Our study provided a new option for intracanal post material development. Copyright © 2014 Elsevier Ltd. All rights reserved.

Finite element modelling of FRC beams containing PVA and Basalt fibres: A comparative study

NASA Astrophysics Data System (ADS)

Ayub, Tehmina; Khan, Sadaqat Ullah

2017-09-01

The endeavour of current study is to compare the flexural behaviour and three dimensional (3D) finite element analysis (FEA) and the results of FEM are compared with the experimental results of 07 HPFRC beams. Out of seven (07), 01 beam of plain concrete without fibres was cast as a control beam. Three (03) beams containing 1, 2 and 3% volume of PVA fibres were prepared by using HPFRC mixes while, the remaining other three (03) beams were prepared using HPFRC mixes containing 1, 2 and 3% volume of Basalt fibres. In order to ensure flexural failure, three-point bending load was applied at the mid span of all beams. The maximum flexural load and corresponding deflection and strains at the mid span attained prior to the failure were obtained as flexural test results. The FEM results were obtained by simulating all beams in ATENA 3D program and verified through flexural test results. Both of the results of FEM and Experiment showed good agreement with each other.

Coatings and surface treatments for enhanced performance suspensions for future gravitational wave detectors

NASA Astrophysics Data System (ADS)

Birney, R.; Cumming, A. V.; Campsie, P.; Gibson, D.; Hammond, G. D.; Hough, J.; Martin, I. W.; Reid, S.; Rowan, S.; Song, S.; Talbot, C.; Vine, D.; Wallace, G.

2017-12-01

Further improvements in the low frequency sensitivity of gravitational wave detectors are important for increasing the observable population of astrophysical sources, such as intermediate mass compact black hole binary systems. Improvements in the lower stage mirror and suspension systems will set challenging targets for the required thermal noise performance of the cantilever blade springs, which provide vertical softness and, thus, isolation to the mirror suspension stack. This is required due to the coupling between the vertical and horizontal axes due to the curvature of the Earth. This can be achieved through use of high mechanical Q materials, which are compatible with cryogenic cooling, such as crystalline silicon. However, such materials are brittle, posing further challenges for assembly/jointing and, more generally, for long-term robustness. Here, we report on experimental studies of the breaking strength of silicon at room temperature, via both tensile and 4-point flexural testing; and on the effects of various surface treatments and coatings on durability and strength. Single- and multi-layer DLC (diamond-like carbon) coatings, together with magnetron-sputtered silica and thermally-grown silica, are investigated, as are the effects of substrate preparation and argon plasma pre-treatment. Application of single- or multi-layer DLC coatings can significantly improve the failure stress of silicon flexures, in addition to improved robustness for handling (assessed through abrasion tests). Improvements of up to 80% in tensile strength, a twofold increase in flexural strength, in addition to a 6.4 times reduction in the vertical thermal noise contribution of the suspension stack at 10 Hz are reported (compared to current Advanced LIGO design). The use of silicon blade springs would also significantly reduce potential ‘crackling noise’ associated with the underlying discrete events associated with plastic deformation in loaded flexures.

Strength and fracture energy of foamed concrete incorporating rice husk ash and polypropylene mega-mesh 55

NASA Astrophysics Data System (ADS)

Jaini, Z. M.; Rum, R. H. M.; Boon, K. H.

2017-10-01

This paper presents the utilization of rice husk ash (RHA) as sand replacement and polypropylene mega-mesh 55 (PMM) as fiber reinforcement in foamed concrete. High pozzolanic reaction and the ability to become filler make RHA as a strategic material to enhance the strength and durability of foamed concrete. Furthermore, the presence of PMM optimizes the toughness of foamed concrete in resisting shrinkage and cracking. In this experimental study, cube and cylinder specimens were prepared for the compression and splitting-tensile tests. Meanwhile, notched beam specimens were cast for the three-point bending test. It was found that 40% RHA and 9kg/m3 PMM contribute to the highest strength and fracture energy. The compressive, tensile and flexural strengths are 32MPa, 2.88MPa and 6.68MPa respectively, while the fracture energy achieves 42.19N/m. The results indicate high potential of RHA and PMM in enhancing the mechanical properties of foamed concrete.

Strengthening Performance of PALF-Epoxy Composite Plate on Reinforced Concrete Beams

NASA Astrophysics Data System (ADS)

Chin, Siew C.; Tong, Foo S.; Doh, Shu I.; Gimbun, Jolius; Ong, Huey R.; Serigar, Januar P.

2018-03-01

This paper presents the effective strengthening potential of pineapple leaves fiber (PALF)-epoxy composite plate on reinforced concrete (RC) beam. At first the PALF is treated with alkali (NaOH) and its morphology is observed via scanning electron microscope (SEM). The composite plates made of PALF and epoxy with fiber loading ranging from 0.1 to 0.4 v/v was tested for its flexural behaviour. The composite was then used for external RC beam strengthening. The structural properties of RC beams were evaluated and all the beams were tested under four-point bending. It was found that the flexural strength increased as the fiber volume ratio increases. The maximum flexural strength (301.94 MPa) was obtained at the fiber volume ratio of 40%. The beam strengthened with PALF-epoxy composite plate has a 7% higher beam capacity compared to the control beam. Cracks formed at the edge of the plate of PALF-strengthened beams resulted in diagonal cracking. Result from this work shows that the PALF-epoxy composite plate has the potential to be used as external strengthening material for RC beam.

Phase I: Evaluation of Low Flexural Strength for Northern Nevada Concrete Paving Mixtures

DOT National Transportation Integrated Search

2017-07-01

Production paving grade concrete in Northern Nevada having acceptable strength is universally acknowledged to be difficult; however understanding why this is true remains elusive. Current practice is to meet flexural strength requirements by using mi...

Feasibility of Reducing the Fiber Content in Ultra-High-Performance Fiber-Reinforced Concrete under Flexure.

PubMed

Park, Jung-Jun; Yoo, Doo-Yeol; Park, Gi-Joon; Kim, Sung-Wook

2017-01-28

In this study, the flexural behavior of ultra-high-performance fiber-reinforced concrete (UHPFRC) is examined as a function of fiber length and volume fraction. Straight steel fiber with three different lengths ( l f ) of 13, 19.5, and 30 mm and four different volume fractions ( v f ) of 0.5%, 1.0%, 1.5%, and 2.0% are considered. Test results show that post-cracking flexural properties of UHPFRC, such as flexural strength, deflection capacity, toughness, and cracking behavior, improve with increasing fiber length and volume fraction, while first-cracking properties are not significantly influenced by fiber length and volume fraction. A 0.5 vol % reduction of steel fiber content relative to commercial UHPFRC can be achieved without deterioration of flexural performance by replacing short fibers ( l f of 13 mm) with longer fibers ( l f of 19.5 mm and 30 mm).

Feasibility of Reducing the Fiber Content in Ultra-High-Performance Fiber-Reinforced Concrete under Flexure

PubMed Central

Park, Jung-Jun; Yoo, Doo-Yeol; Park, Gi-Joon; Kim, Sung-Wook

2017-01-01

In this study, the flexural behavior of ultra-high-performance fiber-reinforced concrete (UHPFRC) is examined as a function of fiber length and volume fraction. Straight steel fiber with three different lengths (lf) of 13, 19.5, and 30 mm and four different volume fractions (vf) of 0.5%, 1.0%, 1.5%, and 2.0% are considered. Test results show that post-cracking flexural properties of UHPFRC, such as flexural strength, deflection capacity, toughness, and cracking behavior, improve with increasing fiber length and volume fraction, while first-cracking properties are not significantly influenced by fiber length and volume fraction. A 0.5 vol % reduction of steel fiber content relative to commercial UHPFRC can be achieved without deterioration of flexural performance by replacing short fibers (lf of 13 mm) with longer fibers (lf of 19.5 mm and 30 mm). PMID:28772477

Effect of tooth whitening strips on fatigue resistance and flexural strength of bovine dentin in vitro

PubMed Central

Kim, Namhee; De Souza, Grace M.

2017-01-01

Objective To determine the effects of whitening strips on bovine dentin fatigue resistance and flexural strength in vitro. Materials and methods A total of eighty bovine dentin specimens (2x2x17mm) were treated with either: control glycerine gel on plastic film wrap or whitening strips containing 9.5% hydrogen peroxide. Treatment was applied for 30 minutes, twice a day, for 1- or 4-weeks. After the last treatment, ten specimens per group were randomly selected to undergo fatigue testing (106 cycles, 3Hz, 20N) while the other ten were subjected to flexural strength testing after ten days of storage in artificial saliva. Kaplan-Meier method with a log rank test, Wilcoxon test and Cox regression were used to assess fatigue test results (p<0.05). One-way ANOVA and Tukey’s tests were used to compare the flexural strength results (p<0.05). Results There were significant differences in survival during the fatigue test among the groups (p<0.001). Treatment (control or bleach) was a significant factor for specimen survival (p<0.001, Exp(B) = 33.45). There were significant differences in mean flexural strength (p<0.001). No significant difference was found between “1-wk control” and “4-wk control”. The mean flexural strength and fatigue resistance of the “4-wk bleach” were significantly lower than all the other groups. Conclusions The use of whitening strips reduced the fatigue resistance and flexural strength of bovine dentin in vitro. Until the effect of whitening strips on mechanical properties of human dentin is fully elucidated, it remains prudent to advise patients to avoid excessive direct use of whitening strips on dentin. PMID:28278191

An in vitro study to compare the transverse strength of thermopressed and conventional compression-molded polymethylmethacrylate polymers.

PubMed

Raut, Anjana; Rao, Polsani Laxman; Vikas, B V J; Ravindranath, T; Paradkar, Archana; Malakondaiah, G

2013-01-01

Acrylic resins have been in the center stage of Prosthodontics for more than half a century. The flexural fatigue failure of denture base materials is the primary mode of clinical failure. Hence there is a need for superior physical and mechanical properties. This in vitro study compared the transverse strength of specimens of thermopressed injection-molded and conventional compression-molded polymethylmethacrylate polymers and examined the morphology and microstructure of fractured acrylic specimens. The following denture base resins were examined: Brecrystal (Thermopressed injection-molded, modified polymethylmethacrylate) and Pyrax (compression molded, control group). Specimens of each material were tested according to the American Society for Testing and Materials standard D790-03 for flexural strength testing of reinforced plastics and subsequently examined under SEM. The data was analyzed with Student unpaired t test. Flexural strength of Brecrystal (82.08 ± 1.27 MPa) was significantly higher than Pyrax (72.76 ± 0.97 MPa). The tested denture base materials fulfilled the requirements regarding flexural strength (>65 MPa). The scanning electron microscopy image of Brecrystal revealed a ductile fracture with crazing. The fracture pattern of control group specimens exhibited poorly defined crystallographic planes with a high degree of disorganization. Flexural strength of Brecrystal was significantly higher than the control group. Brecrystal showed a higher mean transverse strength value of 82.08 ± 1.27 MPa and a more homogenous pattern at microscopic level. Based on flexural strength properties and handling characteristics, Brecrystal may prove to be an useful alternative to conventional denture base resins.

Effect of Loading Rates and Surface Conditions on the Flexural Strength of Borosilicate Glass

DTIC Science & Technology

2009-01-01

strength of etched soda - lime glass rods.32 According to this model, an idealized surface crack is uniformly attacked by acid at every point so that this...R. Lin, ‘‘Effect of Polymer Coatings on the Strength and Fatigue Behavior of Indented Soda - Lime Glass ,’’ Glass Technol., 32 [2] 51–4 (1991). 10J. J...Scott Glaesemann, K. Jakus, and J. E. Ritter Jr., ‘‘Strength Variability of Indented Soda - Lime Glass ,’’ J. Am. Ceram. Soc., 70 [6] 441–4 (1987). 12C

Biaxial flexure strength determination of endodontically accessed ceramic restorations.

PubMed

Kelly, R D; Fleming, G J P; Hooi, P; Palin, W M; Addison, O

2014-08-01

To report analytic solutions capable of identifying failure stresses from the biaxial flexure testing of geometries representative of endodontic access cavities prepared through dental restorative materials. The ring-on-ring biaxial flexure strength of annular discs with a central circular hole supported peripherally by a knife-edge support and loaded evenly at the upper edge of the central hole were solved using general expressions of deformations, moments and shears for flat plates of a constant thickness. To validate the solutions, finite element analyses were performed. A three-dimensional one-quarter model of the test was generated using a linear P-code FEA software and the boundary conditions represented the experimental test configuration whereby symmetry planes defined the full model. To enable comparison of the maximum principal stresses with experimental derived data, three groups of nominally identical feldspathic ceramic disks (n=30) were fabricated. Specimens from Group A received a 4mm diameter representative endodontic access cavity and were tested in ring-on-ring. Group B and C specimens remained intact and were tested in ring-on-ring and ball-on-ring, respectively, to give insight into strength scaling effects. Fractography was used to confirm failure origins, and statistical analysis of fracture strength data was performed using one-way ANOVAs (P<0.05) and a Weibull approach. The developed analytical solutions were demonstrated to deviate <1% from the finite element prediction in the configuration studied. Fractography confirmed the failure origin of tested samples to coincide with the predicted stress maxima and the area where fracture is observed to originate clinically. Specimens from the three experimental groups A-C exhibited different strengths which correlated with the volume scaling effects on measured strength. The solutions provided will enable geometric and materials variables to be systematically studied and remove the need for load-to-failure 'crunch the crown' testing. Copyright © 2014 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Radiographic and ultrasonic characterization of sintered silicon carbide

NASA Technical Reports Server (NTRS)

Baaklini, G. Y.; Abel, P. B.

1988-01-01

The capabilities were investigated of projection microfocus X-radiography, ultrasonic velocity and attenuation, and reflection scanning acoustic microscopy for characterizing silicon carbide specimens. Silicon carbide batches covered a range of densities and different microstructural characteristics. Room temperature, four point flexural strength tests were conducted. Fractography was used to identify types, sizes, and locations of fracture origins. Fracture toughness values were calculated from fracture strength and flaw characterization data. Detection capabilities of radiography and acoustic microscopy for fracture-causing flaws were evaluated. Applicability of ultrasonics for verifying material strength and toughness was examined.

Flaw imaging and ultrasonic techniques for characterizing sintered silicon carbide

NASA Technical Reports Server (NTRS)

Baaklini, George Y.; Abel, Phillip B.

1987-01-01

The capabilities were investigated of projection microfocus x-radiography, ultrasonic velocity and attenuation, and reflection scanning acoustic microscopy for characterizing silicon carbide specimens. Silicon carbide batches covered a range of densities and different microstructural characteristics. Room temperature, four point flexural strength tests were conducted. Fractography was used to identify types, sizes, and locations of fracture origins. Fracture toughness values were calculated from fracture strength and flaw characterization data. Detection capabilities of radiography and acoustic microscopy for fracture-causing flaws were evaluated. Applicability of ultrasonics for verifying material strength and toughness was examined.

Effect of Waterproofing Admixtures on the Flexural Strength and Corrosion Resistance of Concrete

NASA Astrophysics Data System (ADS)

Geetha, A.; Perumal, P.

2012-02-01

This paper deals about the flexural strength and corrosion behaviour of concrete using waterproofing admixtures. The effect of waterproofing admixtures on the corrosion behaviour of RCC specimen has been studied by conducting accelerated corrosion test. To identify the effect of corrosion in pull out strength, corrosion process was induced by means of accelerated corrosion procedure. To accelerate the reinforcement corrosion, direct electric current was impressed on the rebar embedded in the specimen using a DC power supply system that has a facility to adjust voltage. The addition of waterproofing admixtures also shows the improvement in the flexural strength of concrete has been studied by conducting flexural strength tests on the concrete prism specimen of size 100 × 100 × 500 mm with and without admixtures for various dosages and various curing periods of 7 and 28 days. The results showed that the presence of waterproofing admixtures always improves the corrosion resistance and thus increases the strength of concrete due to the hydrophobic action of waterproofing admixtures.

Effects of number of ply, compression temperature, pressure and time on mechanical properties of prepreg kenaf-polypropilene composites

NASA Astrophysics Data System (ADS)

Tomo, H. S. S.; Ujianto, O.; Rizal, R.; Pratama, Y.

2017-07-01

Composite material thermoplastic was prepared from polypropilen granule as matrix, kenaf fiber as reinforcement and grafted polypropylene copolymer maleic anhydride as coupling agent. Composite products were produced as sandwich structures using compression molding. This research aimed to observe the influence of number of ply, temperature, pressure, and compression time using factorial design. Effects of variables on tensile and flexural strength were analyzed. Experimental results showed that tensile and flexural strength were influenced by degradation, fiber compaction, and matrix - fiber interaction mechanisms. Flexural strength was significantly affected by number of ply and its interaction to another process parameters (temperature, pressure, and compression time), but no significant effect of process parameters on tensile strength. The highest tensile strength (62.0 MPa) was produced at 3 ply, 210 °C, 50 Bar, and 3 min compression time (low, high, high, low), while the highest flexural strength (80.3 MPa) was produced at 3 ply, 190 °C, 50 Bar, and 3 min compression time (low, low, high, low).

Fracture Toughness Properties of Gd123 Superconducting Bulks

NASA Astrophysics Data System (ADS)

Fujimoto, H.; Murakami, A.

Fracture toughness properties of melt growth GdBa2Cu3Ox (Gd123) large single domain superconducting bulks with Ag2O of 10 wt% and Pt of 0.5 wt%; 45 mm in diameter and 25 mm in thickness with low void density were evaluated at 77 K through flexural tests of specimens cut from the bulks, and compared to those of a conventional Gd123 with voids. The densified Gd123 bulks were prepared with a seeding and temperature gradient method; first melt processed in oxygen, then crystal growth in air; two-step regulated atmosphere heat treatment. The plane strain fracture toughness, KIC was obtained by the three point flexure test of the specimens with through precrack, referring to the single edge pre-cracked beam (SEPB) method, according to the JIS-R-1607, Testing Methods for Fracture Toughness of High Performance Ceramics. The results show that the fracture toughness of the densified Gd123 bulk with low void density was higher than that of the standard Gd123 bulk with voids, as well as the flexural strength previously reported. We also compared the fracture toughness of as-grown bulks with that of annealed bulks. The relation between the microstructure and the fracture toughness of the Gd123 bulk was clearly shown.

Impact of machining on the flexural fatigue strength of glass and polycrystalline CAD/CAM ceramics.

PubMed

Fraga, Sara; Amaral, Marina; Bottino, Marco Antônio; Valandro, Luiz Felipe; Kleverlaan, Cornelis Johannes; May, Liliana Gressler

2017-11-01

To assess the effect of machining on the flexural fatigue strength and on the surface roughness of different computer-aided design, computer-aided manufacturing (CAD/CAM) ceramics by comparing machined and polished after machining specimens. Disc-shaped specimens of yttria-stabilized polycrystalline tetragonal zirconia (Y-TZP), leucite-, and lithium disilicate-based glass ceramics were prepared by CAD/CAM machining, and divided into two groups: machining (M) and machining followed by polishing (MP). The surface roughness was measured and the flexural fatigue strength was evaluated by the step-test method (n=20). The initial load and the load increment for each ceramic material were based on a monotonic test (n=5). A maximum of 10,000 cycles was applied in each load step, at 1.4Hz. Weibull probability statistics was used for the analysis of the flexural fatigue strength, and Mann-Whitney test (α=5%) to compare roughness between the M and MP conditions. Machining resulted in lower values of characteristic flexural fatigue strength than machining followed by polishing. The greatest reduction in flexural fatigue strength from MP to M was observed for Y-TZP (40%; M=536.48MPa; MP=894.50MPa), followed by lithium disilicate (33%; M=187.71MPa; MP=278.93MPa) and leucite (29%; M=72.61MPa; MP=102.55MPa). Significantly higher values of roughness (Ra) were observed for M compared to MP (leucite: M=1.59μm and MP=0.08μm; lithium disilicate: M=1.84μm and MP=0.13μm; Y-TZP: M=1.79μm and MP=0.18μm). Machining negatively affected the flexural fatigue strength of CAD/CAM ceramics, indicating that machining of partially or fully sintered ceramics is deleterious to fatigue strength. Copyright © 2017 The Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

The influences of accelerated aging on mechanical properties of veneering ceramics used for zirconia restorations.

PubMed

Luo, Huinan; Tang, Xuehua; Dong, Zhen; Tang, Hui; Nakamura, Takashi; Yatani, Hirofumi

2016-01-01

This study evaluated the influences of accelerated aging on the mechanical properties of veneering ceramics used for zirconia frameworks. Five different veneering ceramics for zirconia frameworks were used. Twenty specimens were fabricated for each veneering ceramic. All specimens were divided into two groups. One was subjected to accelerated aging and the other was used as a control. Accelerated aging was performed in distilled water for 5 h at 200ºC and 2 atm. The density, open porosity, surface roughness, three-point flexural strength, and Vickers hardness were measured. The results showed that the density, open porosity, and surface roughness of all examined veneering ceramics were changed by the accelerated aging process. Accelerated aging was also found to have a positive effect on strength and a negative effect on the hardness.

Use of polypropylene fibers coated with nano-silica particles into a cementitious mortar

DOE Office of Scientific and Technical Information (OSTI.GOV)

Coppola, B., E-mail: bcoppola@unisa.it; Di Maio, L.; Scarfato, P.

Fiber reinforced cementitious composite (FRCC) materials have been widely used during last decades in order to overcome some of traditional cementitious materials issues: brittle behaviour, fire resistance, cover spalling, impact strength. For composite materials, fiber/matrix bond plays an important role because by increasing fiber/matrix interactions is possible to increase the behaviour of the entire material. In this study, in order to improve fiber to matrix adhesion, two chemical treatments of polypropylene fibers were investigated: alkaline hydrolysis and nano-silica sol-gel particles deposition. Treatmtents effect on fibers morphology and mechanical properties was investigated by scanning electron microscopy (SEM) and tensile tests. SEMmore » investigations report the presence of spherical nano-silica particles on fiber surface, in the case of sol-gel process, while alkaline hydrolysis leads to an increase of fibers roughness. Both treatments have negligible influence on fibers mechanical properties confirming the possibility of their use in a cementitious mortar. Pullout tests were carried out considering three embedded length of fibers in mortar samples (10, 20 and 30 mm, respectively) showing an increase of pullout energy for treated fibers. The influence on fiber reinforced mortar mechanical properties was investigated by three-point flexural tests on prismatic specimens considering two fibers length (15 and 30 mm) and two fibers volume fractions (0.50 and 1.00 %). A general increase of flexural strength over the reference mix was achieved and an overall better behaviour is recognizable for mortars containing treated fibers.« less

Stereolithography: A new method for processing dental ceramics by additive computer-aided manufacturing.

PubMed

Dehurtevent, Marion; Robberecht, Lieven; Hornez, Jean-Christophe; Thuault, Anthony; Deveaux, Etienne; Béhin, Pascal

2017-05-01

The aim of this study was to compare the physical and mechanical properties of stereolithography (SLA)- manufactured alumina ceramics of different composition to those of subtractive- manufactured ceramics and to produce suitable dental crown frameworks. The physical and mechanical properties of a control and six experimental SLA ceramics prepared from slurries with small (S) and large (L) particles (0.46±0.03 and 1.56±0.04μm, respectively) and three dry matter contents (70%, 75%, 80%) were evaluated by dynamic rheometry, hydrostatic weighing, three3-point flexural strength measurements, and Weibull analyses, and by the micrometrics measurement of shrinkage ratio before and after the heat treatments. S75 was the only small particle slurry with a significantly higher viscosity than L70. The viscosity of the S80 slurry made it impossible to take rheological measurements. The viscosities of the S75 and S80 slurries caused deformations in the printed layers during SLA manufacturing and were excluded from further consideration. SLA samples with low dry matter content had significantly lower and densityflexural strengths. Only SLA samples with a large particle size and high dry matter content (L75 and L80) were similar in density and flexural strength to the subtractive- manufactured samples. The 95% confidence intervals of the Weibull modulus of the L80 ceramic were higher (no overlap fraction) than those of the L75 ceramic and were similar to the control (overlap fraction). The Weibull characteristics of L80 ceramic were higher than those of L75 ceramic and the control. SLA can be used to process suitable crown frameworks but shows results in anisotropic shrinkage. The hH High particle size and dry matter content of the L80 slurry allowed made it possible to produce a reliable ceramic by SLA manufacturing with an anisotropic shrinkage, and a density, and flexural strength similar to those of a subtractive-manufactured ceramic. SLA allowed made it possible to build up a dense 3D alumina crown framework with controlled shape. Further studies on the marginal adaptation and shrinkage model of alumina crown frameworks will be required to optimize the process. Copyright © 2017 The Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Novel nano-particles as fillers for an experimental resin-based restorative material.

PubMed

Rüttermann, S; Wandrey, C; Raab, W H-M; Janda, R

2008-11-01

The purpose of this study is to compare the properties of two experimental materials, nano-material (Nano) and Microhybrid, and two trade products, Clearfil AP-X and Filtek Supreme XT. The flexural strength and modulus after 24h water storage and 5000 thermocycles, water sorption, solubility and X-ray opacity were determined according to ISO 4049. The volumetric behavior (DeltaV) after curing and after water storage was investigated with the Archimedes principle. ANOVA was calculated with p<0.05. Clearfil AP-X showed the highest flexural strength (154+/-14 MPa) and flexural modulus (11,600+/-550 MPa) prior to and after thermocycling (117+/-14 MPa and 13,000+/-300 MPa). The flexural strength of all materials decreased after thermocycling, but the flexural modulus decreased only for Filtek Supreme XT. After thermocycling, there were no significant differences in flexural strength and modulus between Filtek Supreme XT, Microhybrid and Nano. Clearfil AP-X had the lowest water sorption (22+/-1.1 microg mm(-3)) and Nano had the highest water sorption (82+/-2.6 microg mm(-3)) and solubility (27+/-2.9 microg mm(-3)) of all the materials. No significant differences occurred between the solubility of Clearfil AP-X, Filtek Supreme XT and Microhybrid. Microhybrid and Nano provided the highest X-ray opacity. Owing to the lower filler content, Nano showed higher shrinkage than the commercial materials. Nano had the highest expansion after water storage. After thermocycling, Nano performed as well as Filtek Supreme XT for flexural strength, even better for X-ray opacity but significantly worse for flexural modulus, water sorption and solubility. The performances of microhybrids were superior to those of the nano-materials.

Precision tool holder with flexure-adjustable, three degrees of freedom for a four-axis lathe

DOEpatents

Bono, Matthew J [Pleasanton, CA; Hibbard, Robin L [Livermore, CA

2008-03-04

A precision tool holder for precisely positioning a single point cutting tool on 4-axis lathe, such that the center of the radius of the tool nose is aligned with the B-axis of the machine tool, so as to facilitate the machining of precision meso-scale components with complex three-dimensional shapes with sub-.mu.m accuracy on a four-axis lathe. The device is designed to fit on a commercial diamond turning machine and can adjust the cutting tool position in three orthogonal directions with sub-micrometer resolution. In particular, the tool holder adjusts the tool position using three flexure-based mechanisms, with two flexure mechanisms adjusting the lateral position of the tool to align the tool with the B-axis, and a third flexure mechanism adjusting the height of the tool. Preferably, the flexures are driven by manual micrometer adjusters. In this manner, this tool holder simplifies the process of setting a tool with sub-.mu.m accuracy, to substantially reduce the time required to set the tool.

Does Acid Challenge Affect the Properties and Bond Stability of Restorative Materials on Primary Teeth?

PubMed

Tedesco, Tamara K; Calvo, Ana F B; Yoshioka, Laysa; Fukushima, Karen A; Cesar, Paulo F; Raggio, Daniela P

2018-05-31

To evaluate the effect of acidic challenge (AC) on the properties and bond stability of restorative materials to primary enamel and dentin. One hundred twenty primary molars were assigned to 12 groups according to substrate (enamel or dentin), restorative material (composite, high-viscosity glass ionomer cement [HV-GIC] or resin-modified glass-ionomer cement [RM-GIC]), and immersion after restoration (control [saline solution/7 days] or AC [cola-based drink/5 min/3x per day/7 days]). Twenty-four hours after the restorative procedure, specimens were submitted to one of the proposed challenges. Half of the specimens were immediately subjected to the microshear bond strength test, and the other half after 12 months. To determine flexural strength flexural strength and superficial roughness (SR), 30 specimens were built up. After 24 h, the first measurement of SR from 10 specimens was performed. Specimens were then immersed in one of proposed challenges and SR was measured again. Subsequently, flexural strength testing was performed. Bond strength, surface roughness, and flexural strength data were subjected to ANOVA and Tukey's test. Composite showed the highest bond strengths compared to the others materials on both substrates. The storage period negatively influenced the bond strength only for composite groups in dentin. AC after restoration negatively influenced bond strength when the materials were evaluated in eroded dentin. AC affected the second SR measurement, showing increased SR for all restorative materials. AC did not affect flexural strength. The acidic challenge jeopardizes the surface roughness and bond strength of restorations to eroded dentin.

Strength of a Ceramic Sectored Flexure Specimen

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wereszczak, Andrew A; Duffy, Stephen F; Baker, E. H.

2008-01-01

A new test specimen, defined here as the "sectored flexure strength specimen", was developed to measure the strength of ceramic tubes specifically for circumstances when flaws located at the tube's outer diameter are the strength-limiter and subjected to axial tension. The understanding of such strength-limitation is relevant for when ceramic tubes are subjected to bending or when the internal temperature is hotter than the tube's exterior (e.g., heat exchangers). The specimen is both economically and statistically attractive because eight specimens (eight in the case of this project - but the user is not necessarily limited to eight) were extracted outmore » of each length of tube. An analytic expression for maximum or failure stress, and relationships portraying effective area and effective volume as a function of Weibull modulus were developed. Lastly, it was proven from the testing of two ceramics that the sectored flexure specimen was very effective at producing failures caused by strength-limiting flaws located on the tube's original outer diameter. Keywords: ceramics, strength, sectored flexure specimen, effective area, effective volume, finite-element analysis, Weibull distribution, and fractography.« less

Microstructure and Mechanical Properties of Reaction-Formed Joints in Reaction Bonded Silicon Carbide Ceramics

NASA Technical Reports Server (NTRS)

Singh, M.

1998-01-01

A reaction-bonded silicon carbide (RB-SiC) ceramic material (Carborundum's Cerastar RB-SIC) has been joined using a reaction forming approach. Microstructure and mechanical properties of three types of reaction-formed joints (350 micron, 50-55 micron, and 20-25 micron thick) have been evaluated. Thick (approximately 350 micron) joints consist mainly of silicon with a small amount of silicon carbide. The flexural strength of thick joints is about 44 plus or minus 2 MPa, and fracture always occurs at the joints. The microscopic examination of fracture surfaces of specimens with thick joints tested at room temperature revealed the failure mode to be typically brittle. Thin joints (<50-55 micron) consist of silicon carbide and silicon phases. The room and high temperature flexural strengths of thin (<50-55 micron) reaction-formed joints have been found to be at least equal to that of the bulk Cerastar RB-SIC materials because the flexure bars fracture away from the joint regions. In this case, the fracture origins appear to be inhomogeneities inside the parent material. This was always found to be the case for thin joints tested at temperatures up to 1350C in air. This observation suggests that the strength of Cerastar RB-SIC material containing a thin joint is not limited by the joint strength but by the strength of the bulk (parent) materials.

Effects of neutron irradiation on the strength of continuous fiber reinforced SiC/SiC composites

DOE Office of Scientific and Technical Information (OSTI.GOV)

Youngblood, G.E.; Henager, C.H. Jr.; Jones, R.H.

1997-04-01

Flexural strength data as a function of irradiation temperature and dose for a SiC{sub f}/SiC composite made with Nicalon-CG fiber suggest three major degradation mechanisms. Based on an analysis of tensile strength and microstructural data for irradiated Nicalon-CG and Hi-Nicalon fibers, it is anticipated that these degradation mechanisms will be alleviated in Hi-Nicalon reinforced composites.

Fatigue and shear behavior of HPC bulb-tee girders : interim report.

DOT National Transportation Integrated Search

2003-10-01

Three 96-ft (29.3-m) long, 72-in. (1.83-m) deep, precast, pretensioned bulb-tee girders were tested to evaluate behavior under flexural fatigue and static shear loadings. The three girders had a design concrete compressive strength of 10,000 psi (69....

Creation of bioactive glass (13-93) scaffolds for structural bone repair using a combined finite element modeling and rapid prototyping approach.

PubMed

Xiao, Wei; Zaeem, Mohsen Asle; Bal, B Sonny; Rahaman, Mohamed N

2016-11-01

There is a clinical need for synthetic bioactive materials that can reliably repair intercalary skeletal tissue loss in load-bearing bones. Bioactive glasses have been investigated as one such material but their mechanical response has been a concern. Previously, we created bioactive silicate glass (13-93) scaffolds with a uniform grid-like microstructure which showed a compressive strength comparable to human cortical bone but a much lower flexural strength. In the present study, finite element modeling (FEM) was used to re-design the scaffold microstructure to improve its flexural strength without significantly lowering its compressive strength and ability to support bone infiltration in vivo. Then scaffolds with the requisite microstructures were created by a robotic deposition method and tested in four-point bending and compression to validate the FEM simulations. In general, the data validated the predictions of the FEM simulations. Scaffolds with a porosity gradient, composed of a less porous outer region and a more porous inner region, showed a flexural strength (34±5MPa) that was more than twice the value for the uniform grid-like microstructure (15±5MPa) and a higher compressive strength (88±20MPa) than the grid-like microstructure (72±10MPa). Upon implantation of the scaffolds for 12weeks in rat calvarial defects in vivo, the amount of new bone that infiltrated the pore space of the scaffolds with the porosity gradient (37±16%) was similar to that for the grid-like scaffolds (35±6%). These scaffolds with a porosity gradient that better mimics the microstructure of human long bone could provide more reliable implants for structural bone repair. Copyright © 2016 Elsevier B.V. All rights reserved.

Flexural strength of proof-tested and neutron-irradiated silicon carbide

NASA Astrophysics Data System (ADS)

Price, R. J.; Hopkins, G. R.

1982-08-01

Proof testing before service is a valuable method for ensuring the reliability of ceramic structures. Silicon carbide has been proposed as a very low activation first-wall and blanket structural material for fusion devices, where it would experience a high flux of fast neutrons. Strips of three types of silicon carbide were loaded in four-point bending to a stress sufficient to break about a third of the specimens. Groups of 16 survivors were irradiated to 2 × 10 26n/ m2 ( E>0.05 MeV) at 740°C and bend tested to failure. The strength distribution of chemically vapor-deposited silicon carbide (Texas Instruments) was virtually unchanged by irradiation. The mean strength of sintered silicon carbide (Carborundum Alpha) was reduced 34% by irradiation, while the Weibull modulus and the truncated strength distribution characteristic of proof-tested material were retained. Irradiation reduced the mean strength of reaction-bonded silicon carbide (Norton NC-430) by 58%, and the spread in strength values was increased. We conclude that for the chemically vapor-deposited and the sintered silicon carbide the benefits of proof testing to eliminate low strength material are retained after high neutron exposures.

Development and testing of fiber-reinforced composite space maintainers.

PubMed

Kulkarni, Gajanan; Lau, Domenic; Hafezi, Sara

2009-01-01

The purpose of this study was to develop a clinically acceptable, cheaper, and more expedient alternative to standard stainless steel band and loop space maintainers. Loops of fiber-reinforced composites were constructed using polyethylene fiber (Ribbond) and glass fiber (Sticktech). The loops were bonded on extracted third molars and tested for flexural strength before and after thermocycling and following repair of the appliances after initial stress failure. Bacterial colonization on the appliances was also compared. Conventional stainless steel band and loop space maintainers cemented with Ketac were controls. Ribbond samples demonstrated higher flexural strength than Sticktech and the control (P<.05). No differences were noted among the other samples and the control. The repaired Ribbond samples were statistically comparable in flexural strength to the initial samples. Thermocycling resulted in decreased flexural strength of both Ribbond and Sticktech (P<.05). Thermocycled Ribbond samples were comparable to the control, but a lower flexural strength was noted for Sticktech samples (P<.05). While all space maintainers allowed some bacterial adhesion, Sticktech showed higher Streptococcus mutans counts than Ribbond (P=.06). Ribbond space-maintainers are comparable to the stainless steel in terms of physical strength and biofilm formation. The fiber-reinforced composite space maintainers may be a clinically acceptable and expedient alternative to the conventional band-loop appliance.

Enhanced Flexural Strength of Tellurium Nanowires/epoxy Composites with the Reinforcement Effect of Nanowires

NASA Astrophysics Data System (ADS)

Balguri, Praveen Kumar; Harris Samuel, D. G.; Aditya, D. B.; Vijaya Bhaskar, S.; Thumu, Udayabhaskararao

2018-02-01

Investigating the mechanical properties of polymer nanocomposite materials has been greatly increased in the last decade. In particular, flexural strength plays a major role in resisting bending and shear loads of a composite material. Here, one dimensional (1D) tellurium nanowires (TeNWs) reinforced epoxy composites have been prepared and the flexural properties of resulted TeNWs/epoxy nanocomposites are studied. The diameter and length of the TeNWs used to make TeNWs/epoxy nanocomposites are 21±2.5 nm and 697±87 nm, respectively. Plain and TeNWs/epoxy nanocomposites are characterized by X-ray diffraction (XRD), thermogravimetric analysis (TGA), and differential thermal analysis (DTA). Furthermore, significant enhancement in the flexural strength of TeNWs/epoxy nanocomposite is observed in comparison to plain epoxy composite, i.e. flexural strength is increased by 65% with the addition of very little amount of TeNWs content (0.05 wt.%) to epoxy polymer. Structural details of plain and TeNWs/epoxy at micrometer scale were examined by scanning electron microscopy (SEM). We believe that our results provide a new type of semiconductor nanowires based high strength epoxy polymer nanocomposites.

[Effect of pigmentation on the strength of dental Y-TZP/porcelain bilayered structure].

PubMed

Ma, Ting-ting; Yi, Yuan-fu; Shao, Long-quan; Liu, Hong-chen; Tian, Jie-mo; Hou, Kang-lin; Zhang, Wei-wei; Wen, Ning; Deng, Bin

2010-05-01

To investigate the effect of two methods of pigmentation on the flexural strength of dental Y-TZP/porcelain layered structure. KaVo zirconia substructures were pigmented by dipping presintered blocks in the coloring solution VITA LL1 and LL5, and colored TZ-3YS zirconia substructures were fabricated by adding pigments before isostatic pressing. The colors No.1 and No.5 were used for the test. The specimens were made in monolithic or bilayered forms, and the flexural strength was tested. XRD and SEM with EDX were used to analyze the characteristics of the surface structure. In KaVo group, no significant differences were found in the flexural strength between white and LL1 and LL5 colored monoclinic materials, nor in bilayered structures. While in TZ-3YS group, significant differences were noted in the flexural strength between color No.5 white and color No.1 monoclinic materials, but not between the latter two subgroups. The flexural strength was significantly lowered by veneering with porcelain in both zirconia groups, and similar findings were observed with the monoclinic materials. Only the tetragonal phase was detected in both of the zirconia groups. Pigmentation has no apparent effects on the bonding strength between the veneering porcelain and zirconia. Both coloring methods are appropriate when the concentration of the pigments is under deliberate control.

Development and characterization of hybrid thermoplastic composites

NASA Astrophysics Data System (ADS)

Karkhanis, Priyanka Chandrashekhar

This work is aimed at studying the possibility of using interply hybrid woven thermoplastic semi-pregs in secondary structures in aircrafts at TenCate Advanced Composites, Netherlands and Purdue University. Three different interply hybrids were designed from combination of Cetex(c) carbon-PPS semi-preg, Owen corning's woven glass with PPS sheets and discontinuous chopped Cetex(c) carbon-PPS semi-preg to get desired flexural, out of plane and bearing properties. The design calculations are done based on classical laminate theory and the selection of materials to be used with carbon-PPS was done based on cost and availability. The Hybrid laminate performances are analyzed and compared to the conventional Cetex (c) Carbon-PPS semi-preg laminates. Observations are reported on three point bend test (European standard 2562), four point bend test(ASTM D6415-99) and bearing test (Airbus standards AITM 1-0009) for the laminates and it was found that hybrid laminates show a reduction of 5-10% in bending stiffness, 20-40% reduction in out-of-plane strength and 2-5%reduction in bearing with a cost reduction of 20-30%. The research identifies and documents the different factors responsible for failures and reduction in strength in the Hybrids.

Flexural properties of ethyl or methyl methacrylate-UDMA blend polymers.

PubMed

Kanie, Takahito; Kadokawa, Akihiko; Arikawa, Hiroyuki; Fujii, Koichi; Ban, Seiji

2010-10-01

Light-curing polyethyl methacrylate (PEMA)-urethane dimethacrylate (UDMA) resins and polymethyl methacrylate (PMMA)-UDMA resins were prepared by two processes. For first step, PEMA or PMMA powders were fully dissolved in ethyl methacrylate (EMA) or methyl methacrylate (MMA) and then the PEMA-EMA/PMMA-MMA mixtures were mixed with UDMA. The flexural properties of cured PEMA-UDMA and PMMA-UDMA polymers were measured using two PEMA (Mw: 300,000-400,000 and 650,000-1,000,000) and three PMMA (Mw: 30,000-60,000, 350,000 and 650,000-1,000,000) powders with different molecular weight, four mixing ratios of PMMA-MMA, and three mixing ratios of PMMA-MMA mixture and UDMA oligomer. Polymers with PMMA(Mw: 350,000) MMA=25/50, and with PMMA(Mw: 350,000)-MMA/UDMA=1/2 and =1/1, showed no-fracture in a flexural test at 1 mm/min and flexural strength and flexural modulus showed no significant difference compared with those of commercially available heat- and self-curing acrylic resins (p>0.01). Within limitation of this investigation, methyl methacrylate-UDMA blend polymer of this composition is available for denture base resin.

Mechanical behaviour of fibre reinforced concrete using soft - drink can

NASA Astrophysics Data System (ADS)

Ilya, J.; Cheow Chea, C.

2017-11-01

This research was carried out to study the behaviour of concrete, specifically compressive and flexural strength, by incorporating recycled soft drink aluminium can as fibre reinforcement in the concrete. Another aim of the research is to determine the maximum proportion of fibres to be added in the concrete. By following standard mix design, Ordinary Portland Cement (OPC) concrete was made to have a target mean strength of 30 N/mm2 with not more than 30 mm of slump. Having the same workability, OPC concrete with 0%, 1% and 2% of soft drink can aluminium fibre was prepared based on weight of cement. The specimens were tested for compressive strength and flexural strength. Laboratory test results based on short term investigation reveals that the compressive strength and flexural strength of concrete containing fibre are higher than of normal OPC concrete. Among two volume fractions, concrete with 1% of soft drink can fibre have performed better result in compressive strength and flexural strength compared with 2% amount of soft drink can fibre. The optimum proportion of aluminium fibre to be added in the concrete as fibre reinforcement is 1% fibre content by weight of cement which gave all the positive response from all the tests conducted.

Characterization of multiwalled carbon nanotube-polymethyl methacrylate composite resins as denture base materials.

PubMed

Wang, Russell; Tao, Junliang; Yu, Bill; Dai, Liming

2014-04-01

Most fractures of dentures occur during function, primarily because of the flexural fatigue of denture resins. The purpose of this study was to evaluate a polymethyl methacrylate denture base material modified with multiwalled carbon nanotubes in terms of fatigue resistance, flexural strength, and resilience. Denture resin specimens were fabricated: control, 0.5 wt%, 1 wt%, and 2 wt% of multiwalled carbon nanotubes. Multiwalled carbon nanotubes were dispersed by sonication. Thermogravimetric analysis was used to determine quantitative dispersions of multiwalled carbon nanotubes in polymethyl methacrylate. Raman spectroscopic analyses were used to evaluate interfacial reactions between the multiwalled carbon nanotubes and the polymethyl methacrylate matrix. Groups with and without multiwalled carbon nanotubes were subjected to a 3-point-bending test for flexural strength. Resilience was derived from a stress and/or strain curve. Fatigue resistance was conducted by a 4-point bending test. Fractured surfaces were analyzed by scanning electron microscopy. One-way ANOVA and the Duncan tests were used to identify any statistical differences (α=.05). Thermogravimetric analysis verified the accurate amounts of multiwalled carbon nanotubes dispersed in the polymethyl methacrylate resin. Raman spectroscopy showed an interfacial reaction between the multiwalled carbon nanotubes and the polymethyl methacrylate matrix. Statistical analyses revealed significant differences in static and dynamic loadings among the groups. The worst mechanical properties were in the 2 wt% multiwalled carbon nanotubes (P<.05), and 0.5 wt% and 1 wt% multiwalled carbon nanotubes significantly improved flexural strength and resilience. All multiwalled carbon nanotubes-polymethyl methacrylate groups showed poor fatigue resistance. The scanning electron microscopy results indicated more agglomerations in the 2% multiwalled carbon nanotubes. Multiwalled carbon nanotubes-polymethyl methacrylate groups (0.5% and 1%) performed better than the control group during the static flexural test. The results indicated that 2 wt% multiwalled carbon nanotubes were not beneficial because of the inadequate dispersion of multiwalled carbon nanotubes in the polymethyl methacrylate matrix. Scanning electron microscopy analysis showed agglomerations on the fracture surface of 2 wt% multiwalled carbon nanotubes. The interfacial bonding between multiwalled carbon nanotubes and polymethyl methacrylate was weak based on the Raman data and dynamic loading results. Copyright © 2014 Editorial Council for the Journal of Prosthetic Dentistry. Published by Elsevier Inc. All rights reserved.

In vitro study of transverse strength of fiber reinforced composites.

PubMed

Mosharraf, R; Hashemi, Z; Torkan, S

2011-01-01

Reinforcement with fiber is an effective method for considerable improvement in flexural properties of indirect composite resin restorations. The aim of this in-vitro study was to compare the transverse strength of composite resin bars reinforced with pre-impregnated and non-impregnated fibers. Thirty six bar type composite resin specimens (3×2×25 mm) were constructed in three groups. The first group was the control group (C) without any fiber reinforcement. The specimens in the second group (P) were reinforced with pre-impregnated fibers and the third group (N) with non-impregnated fibers. These specimens were tested by the three-point bending method to measure primary transverse strength. Data were statistically analyzed with one way ANOVA and Tukey's tests. There was a significant difference among the mean primary transverse strength in the three groups (P<0.001). The post-hoc (Tukey) test showed that there was a significant difference between the pre-impregnated and control groups in their primary transverse strength (P<0.001). Regarding deflection, there was also a significant difference among the three groups (P=0.001). There were significant differences among the mean deflection of the control group and two other groups (P(C&N)<.001 and P(C&P)=.004), but there was no significant difference between the non-and pre-impregnated groups (P(N&P)=.813). Within the limitations of this study, it was concluded that reinforcement with fiber considerably increased the transverse strength of composite resin specimens, but impregnation of the fiber used implemented no significant difference in the transverse strength of composite resin samples.

Compressive and flexural strength of high strength phase change mortar

NASA Astrophysics Data System (ADS)

Qiao, Qingyao; Fang, Changle

2018-04-01

High-strength cement produces a lot of hydration heat when hydrated, it will usually lead to thermal cracks. Phase change materials (PCM) are very potential thermal storage materials. Utilize PCM can help reduce the hydration heat. Research shows that apply suitable amount of PCM has a significant effect on improving the compressive strength of cement mortar, and can also improve the flexural strength to some extent.

Evaluation of fiber reinforced concrete : final report.

DOT National Transportation Integrated Search

1991-05-01

This study was conducted to evaluate the physical properties of plastic and hardened fiber reinforced concrete using three basic types of fibers: steel, fiberglass and polypropylene. Fibers have been shown to increase flexural and tensile strength, d...

Influence of dimethyl sulfoxide used as a solvent on the physical properties and long-term dentin bonding of hydrophilic resins.

PubMed

Stape, Thiago Henrique Scarabello; Tezvergil-Mutluay, Arzu; Mutluay, Mustafa Murat; Martins, Luís Roberto Marcondes; do Prado, Rosana Leal; Pizi, Eliane Cristina Gava; Tjäderhane, Leo

2016-12-01

To examine the feasibility of dimethyl sulfoxide (DMSO) incorporation into relatively hydrophilic resins as a new potential method to improve the durability of resin-dentin bonds. Six experimental light-curing BisGMA/HEMA resins solvated in ethanol and DMSO with increasing concentrations of DMSO (0, 0.5, 1, 2, 4 and 10wt%) were prepared. The degree of conversion (DC) was evaluated by Fourier Transform Infrared Spectroscopy (n=8); water sorption (Wsp) and water solubility (Wso) were gravimetrically assessed (n=10); and flexural strength (FS) and elastic modulus (E) were determined by a three-point bending flexural test (n=10). Flat dentin surfaces on sound third molars (n=10/group) were bonded with resins containing 0, 2, 4 and 10wt% DMSO used as a two-step etch-and-rinse system. Dentin microtensile bond strength was determined at 24h and after two-year aging in artificial saliva at 37°C. DMSO significantly affected Wsp (p=0.0006), DC, Wso, FS, and E (p<0.0001). In general, the resins' mechanical/physical properties were not affected by 2% or lower DMSO incorporation. Incorporation of 4% or higher DMSO content significantly increased DC, Wsp and Wso, but 2% or higher DMSO concentrations significantly reduced FS and E. No influence on immediate dentin bond strength occurred up to 4% DMSO incorporation. While 4% or higher DMSO concentrations impaired bond strength over time, the resin containing 2% DMSO presented significant higher dentin bond strength compared to the control resin after two year-aging. The use of DMSO as a new solvent in adhesive dentistry improves dentin bonding of relatively hydrophilic resins over time. 2% DMSO incorporation in BisGMA/HEMA resins should be sufficient to reduce bond strength loss without compromising polymer mechanical strength and physical properties. Copyright © 2016 Elsevier Ltd. All rights reserved.

The Thermoelectric Properties and Flexural Strength of Nano-TiN/Co4Sb11.3Te0.58Se0.12 Composites Affected by Annealing Treatment

NASA Astrophysics Data System (ADS)

Pengfei, Wen; Pengcheng, Zhai; Shijie, Ding; Bo, Duan; Yao, Li

2017-05-01

This paper is devoted to investigating the thermoelectric properties and flexural strength of the nano-TiN (1 vol.%) dispersed Co4Sb11.3Te0.58Se0.12 composites affected by different thermal annealing treatments at 773 K in a vacuum. After 200 h of annealing treatment, the density of the sample decreases by 4% compared with that before annealing. Moreover, the electrical conductivity and thermal conductivity decline because of the higher porosity in the annealed sample. However, the Seebeck coefficient changes little after annealing. As a result, the ZT value varies slightly after 200 h of annealing. In addition, it is noteworthy that the flexural strength decreases by 16% after 200 h of annealing treatment. Furthermore, the discrete degree of the flexural strength increases with increasing annealing time.

Mechanical properties of new dental pulp-capping materials.

PubMed

Nielsen, Matthew J; Casey, Jeffery A; VanderWeele, Richard A; Vandewalle, Kraig S

2016-01-01

The mechanical properties of pulp-capping materials may affect their resistance to fracture during placement of a final restorative material or while supporting an overlying restoration over time. The purpose of this study was to compare the compressive strength, flexural strength, and flexural modulus of 2 new pulp-capping materials (TheraCal LC and Biodentine), mineral trioxide aggregate (MTA), and calcium hydroxide over time. Specimens were created in molds and tested to failure in a universal testing machine after 15 minutes, 3 hours, and 24 hours. The MTA specimens did not set at 15 minutes. At all time periods, TheraCal LC had the greatest compressive and flexural strengths. After 3 and 24 hours, Biodentine had the greatest flexural modulus. TheraCal LC had greater early strength to potentially resist fracture during immediate placement of a final restorative material. Biodentine had greater stiffness after 3 hours to potentially provide better support of an overlying restoration under function over time.

Effect of electrospun nanofibers on flexural properties of fiberglass composites

NASA Astrophysics Data System (ADS)

White, Fatima T.

In the present study, sintered electrospun TEOS nanofibers were interleaved in S2 fiberglass woven fabric layers, and composite panels were fabricated using the heated vacuum assisted resin transfer molding (H-VARTM) process. Cured panels were water jet cut to obtain the flexural test coupons. Flexural coupons were then tested using ASTM D7264 standard. The mechanical properties such as flexural strength, ultimate flexural failure strains, flexural modulus, and fiber volume fraction were measured. The S-2 fiberglass composite with the sintered TEOS electrospun nanofibers displayed lower flexural stiffness and strength as compared to the composites that were fabricated using S-2 fiberglass composite without the TEOS electrospun nanofibers. The present study also indicated that the composites fabricated with sintered TEOS electrospun nanofibers have larger failure strains as compared to the ones that were fabricated without the presence of electrospun nanofibers. The study indicates that the nanoengineered composites have better energy absorbing mechanism under flexural loading as compared to conventional fiberglass composites without presence of nanofibers.

Properties of indirect composites reinforced with monomer-impregnated glass fiber.

PubMed

Tanoue, Naomi; Sawase, Takashi; Matsumura, Hideo; McCabe, John F

2012-07-01

Sufficient flexural strength is required for long-term clinical use of fixed partial dentures made with fiber-reinforced composite. The flexural strengths of indirect composite materials reinforced with a monomer-preimpregnated glass fiber material were determined to evaluate the compatibility of the composites to glass fiber material. Four types (microhybrid, nanohybrid, microfilled, and minifilled) of indirect composites and a unidirectional long glass fiber material were selected for investigation. The composites were placed on a fiber plate and polymerized in accordance with the respective manufacturer's instructions. Rectangular bar fiber-composite specimens were machined and the flexural strength was calculated. The flexural strength of each indirect composite was also measured. The microfilled composite with the lowest filler content (70 wt%) exhibited the highest increase ratio using the fiber, although its strength without fiber reinforcement was the lowest (62.1 MPa). The fiber-microhybrid specimen demonstrated the highest mean strength (355.9 MPa), although the filler content of the microhybrid composite was comparatively low (73 wt%). The type of composite material should be considered for the selection of an optimal fiber-composite combination.

Investigation on Flexure Test of Composite Beam of Repair Materials and Substrate Concrete for Durable Repair

NASA Astrophysics Data System (ADS)

Pattnaik, Rashmi R.; Rangaraju, Prasada Rao

2014-12-01

An experimental study was conducted on composite beam of repair materials and substrate concrete to investigate the failures of concrete repair due to differences in strength of repair materials and substrate concrete. In this investigation the flexural strength, load-deflection curves and failure patterns of the composite beam specimens are studied for the durability of the concrete repair. Flexure test was conducted to simulate tensile stress in the concrete repair material. Compressive strength and split tensile strength of the repair materials and substrate concrete are investigated to aid in the analysis of the concrete repair. It was observed that the repair materials of higher compressive strength than the substrate concrete are causing an incompatible failure in the concrete repair.

Effect of joint design and welding type on the flexural strength and weld penetration of Ti-6Al-4V alloy bars.

PubMed

Simamoto Júnior, Paulo Cézar; Resende Novais, Veridiana; Rodrigues Machado, Asbel; Soares, Carlos José; Araújo Raposo, Luís Henrique

2015-05-01

Framework longevity is a key factor for the success of complete-arch prostheses and commonly depends on the welding methods. However, no consensus has been reached on the joint design and welding type for improving framework resistance. The purpose of this study was to assess the effect of different joint designs and welding methods with tungsten inert gas (TIG) or laser to join titanium alloy bars (Ti-6Al-4V). Seventy titanium alloy bar specimens were prepared (3.18 mm in diameter × 40.0 mm in length) and divided into 7 groups (n=10): the C-control group consisting of intact specimens without joints and the remaining 6 groups consisting of specimens sectioned perpendicular to the long-axis and rejoined using an I-, X30-, or X45-shaped joint design with TIG welding (TI, TX30, and TX45) or laser welding (LI, LX30, and LX45). The specimens were tested with 3-point bending. The fracture surfaces were first evaluated with stereomicroscopy to measure the weld penetration area and then analyzed with scanning electron microscopy (SEM). The data were statistically analyzed with 2-way ANOVA and the Tukey post hoc test, 1-way ANOVA and the Dunnett test, and the Pearson correlation test (α=.05). Specimens from the X30 and X45 groups showed higher flexural strength (P<.05) and welded area (P<.05) than specimens from the I groups, regardless of the welding type. TIG welded groups showed significantly higher flexural strength than the laser groups (P<.05), regardless of the joint design. TIG welding also resulted in higher welded areas than laser welding for the I-shaped specimens. No significant differences were found for the weld penetration area in the X45 group, either for laser or TIG welding. SEM analysis showed more pores at the fracture surfaces of the laser specimens. Fracture surfaces indicative of regions of increased ductility were detected for the TIG specimens. TIG welding resulted in higher flexural strength for the joined titanium specimens than laser welding. For both welding methods, X30- and X45-shaped joint designs resulted in higher flexural strength and welding penetration than the I-shaped joint design. Copyright © 2015 Editorial Council for the Journal of Prosthetic Dentistry. Published by Elsevier Inc. All rights reserved.

The Effect of Disinfection Techniques on the Flexural Strength of Thermopolymerisable Acrylic Resins With or Without Pigment Addition.

PubMed

Goiato, Marcelo Coelho; Zuccolotti, Bruna Carolina Rossatti; Haddad, Marcela Filié; Moreno, Amália; Pesqueira, Aldiéris Alves; Gennari, Humberto Filho; Dos Santos, Daniela Micheline

2015-12-01

The aim of this study was to assess the flexural strength of two brands of thermopolymerisable acrylic resins (Onda Cryl, Artigos Odontológicos Clássico Ltda, São Paulo, SP, Brazil; and Lucitone 550, Dentsply, York, PA, USA) with varying concentrations of pigment (Poli-Côr, Artigos Odontológicos Clássico Ltda, São Paulo, SP, Brazil) under the influence of thermocycling, storage and disinfection. A total of 210 samples were manufactured (105 for each acrylic resin brand), with dimensions of 64 x 10 x 3.3 mm. The samples were divided into 30 subgroups (n = 7) according to the proportion of pigment used (without pigment, 3% and 7%), the assessment period (initial or thermocycling for 2000 cycles) and disinfection method (immersion in 1% sodium hypochlorite, (Apothicário, Araçatuba, SP, Brazil), microwave energy or immersion in alkaline peroxide (Efferdent, Pfizer, Morris Plains, NJ, USA). The samples were submitted to the flexural strength test before and after thermocycling, and after storage with disinfection. The disinfection process was performed every 3 days, for 60 days. Data were submitted to analysis of variance (ANOVA) and Tukey test (p < 0.05). The factors that provided statistical alteration in flexural strength values were resin type and assessment period. The Onda Cryl resin and the period after disinfection (126 ± 25 MPa) exhibited the higher values of flexural strength. Following disinfection, Onda-Cryl resin exhibited the highest values of flexural strength. All the samples obtained are considered clinically acceptable.

An in vitro evaluation of diametral tensile strength and flexural strength of nanocomposite vs hybrid and minifill composites cured with different light sources (QTH vs LED).

PubMed

Garapati, Surendra Nath; Priyadarshini; Raturi, Piyush; Shetty, Dinesh; Srikanth, K Venkata

2013-01-01

Composites always remained the target of discussion due to lot of controversies around it. Mechanical properties are one of them. With the introduction of new technology and emergence of various composites which combine superior strength and polish retention, nanocomposites have led to a new spark in the dentistry. A recent curing unit LED with various curing modes claims to produce higher degree of conversion. The aim of this study was to evaluate the diametral tensile strength and flexural strength of nanocomposite, hybrid and minifill composites cured with different light sources (QTH vs LED). Seventy-two samples were prepared using different specially fabricated teflon molds, 24 samples of each composite were prepared for the diametral tensile strength (ADA specification no. 27) and the flexural strength (ISO 4049) of the 12 samples, six were cured with LED (Soft Start curing profile) and other six with QTH curing light and tested on a universal testing machine. The nanocomposite had highest diametral tensile strength and flexural strength which were equivalent to the hybrid composite and superior than the minifill composite. With the combination of superior esthetics and other optimized physical properties, this novel nanocomposite system would be useful for all posterior and anterior applications.

Interface effects on mechanical properties of particle-reinforced composites.

PubMed

Debnath, S; Ranade, R; Wunder, S L; McCool, J; Boberick, K; Baran, G

2004-09-01

Effective bonding between the filler and matrix components typically improves the mechanical properties of polymer composites containing inorganic fillers. The aim of this study was to test the hypothesis that composite flexural modulus, flexure strength, and toughness are directly proportional to filler-matrix interfacial shear strength. The resin matrix component of the experimental composite consisted of a 60:40 blend of BisGMA:TEGDMA. Two levels of photoinitiator components were used: 0.15, and 0.5%. Raman spectroscopy was used to determine degree of cure, and thermogravimetry (TGA) was used to quantify the degree of silane, rubber, or polymer attachment to silica and glass particles. Filler-matrix interfacial shear strengths were measured using a microbond test. Composites containing glass particles with various surface treatments were prepared and the modulus, flexure strength, and fracture toughness of these materials obtained using standard methods. Mechanical properties were measured on dry and soaked specimens. The interfacial strength was greatest for the 5% MPS treated silica, and it increased for polymers prepared with 0.5% initiator compared with 0.15% initiator concentrations. For the mechanical properties measured, the authors found that: (1) the flexural modulus was independent of the type of filler surface treatment, though flexural strength and toughness were highest for the silanated glass; (2) rubber at the interface, whether bonded to the filler and matrix or not, did not improve toughness; (3) less grafting of resin to silanated filler particles was observed when the initiator concentration decreased. These findings suggest that increasing the strength of the bond between filler and matrix will not result in improvements in the mechanical properties of particulate-reinforced composites in contrast to fiber-reinforced composites. Also, contraction stresses in the 0.5 vs 0.15% initiator concentration composites may be responsible for increases in interfacial shear strengths, moduli, and flexural strengths.

Semi-2-interpenetrating polymer networks of high temperature systems

NASA Technical Reports Server (NTRS)

Hanky, A. O.; St. Clair, T. L.

1985-01-01

A semi-interpenetrating (semi-IPN) polymer system of the semi-2-IPN type is described in which a polymer of acetylene-terminated imidesulfone (ATPISO2) is cross linked in the presence of polyimidesulfone (PISO2). Six different formulations obtained by mixing of either ATPISO2-1n or ATPISO2-3n with PISO2 in three different proportions were characterized in terms of glass transition temperature, thermooxidative stability, inherent viscosity, and dynamic mechanical properties. Adhesive (lap shear) strength was tested at elevated temperatures on aged samples of adhesive scrim cloth prepared from each resin. Woven graphite (Celion 1000)/polyimide composites were tested for flexural strength, flexural modulus, and shear strength. The network polymers have properties intermediate between those of the component polymers alone, have greatly improved processability over either polyimide, and are able to form good adhesive bonds and composites, making the semi-2-IPN systems superior materials for aerospace structures.

Coatings for graphite fibers

NASA Technical Reports Server (NTRS)

Galasso, F. S.; Scola, D. A.; Veltri, R. D.

1980-01-01

Graphite fibers released from composites during burning or an explosion caused shorting of electrical and electronic equipment. Silicon carbide, silica, silicon nitride and boron nitride were coated on graphite fibers to increase their electrical resistances. Resistances as high as three orders of magnitude higher than uncoated fiber were attained without any significant degradation of the substrate fiber. An organo-silicone approach to produce coated fibers with high electrical resistance was also used. Celion 6000 graphite fibers were coated with an organo-silicone compound, followed by hydrolysis and pyrolysis of the coating to a silica-like material. The shear and flexural strengths of composites made from high electrically resistant fibers were considerably lower than the shear and flexural strengths of composites made from the lower electrically resistant fibers. The lower shear strengths of the composites indicated that the coatings on these fibers were weaker than the coating on the fibers which were pyrolyzed at higher temperature.

Effect of mission cycling on the fatigue performance of SiC-coated carbon-carbon composites

NASA Technical Reports Server (NTRS)

Mahfuz, H.; Das, P. S.; Jeelani, S.; Baker, D. M.; Johnson, S. A.

1993-01-01

The effects of thermal and pressure cycling on the fatigue performance of carbon-carbon composites, and the influence of mission cycling on these effects, were investigated by subjecting both virgin and mission-cycled two-dimensional specimens of SiC-coated carbon-carbon composites to fatigue tests, conducted at room temperature in three-point bending, with a stress ratio of 0.2 and a frequency of 1 Hz. It was found that the fatigue strength of C-C composites is high (about 90 percent of the ultimate flexural strength), but decreased with the mission cycling. The lowering of the fatigue strength with mission cycling is attributed to the increase in interfacial bond strength due to thermal and pressure cycling of the material. The already high sensitivity of C-C composites to stress during cyclic loading increases further with the amount of mission cycling. Results of NDE suggest that the damage growth in virgin C-C, in the high-cycle range, is slow at the initial stage of the cyclic life, but propagates rapidly after certain threshold cycles of the fatigue life.

Compressive and flexural strength of expanded perlite aggregate mortar subjected to high temperatures

NASA Astrophysics Data System (ADS)

Zulkifeli, Muhamad Faqrul Hisham bin Mohd; Saman@Hj Mohamed, Hamidah binti Mohd

2017-08-01

Work on thermal resistant of outer structures of buildings is one of the solution to reduce death, damages and properties loss in fire cases. Structures protected with thermal resistant materials can delay or avoid failure and collapse during fire. Hence, establishment of skin cladding with advance materials to protect the structure of buildings is a necessary action. Expanded perlite is a good insulation material which can be used as aggregate replacement in mortar. This study is to study on mortar mechanical properties of flexural and compressive strength subjected to elevated temperatures using expanded perlite aggregate (EPA). This study involved experimental work which was developing mortar with sand replacement by volume of 0%, 10%, 20%, 30% and 40% of EPA and cured for 56 days. The mortars then exposed to 200°C, 400 °C, 700 °C and 1000 °C. Flexural and compressive strength of the mortar were tested. The tests showed that there were increased of flexural and compressive strength at 200°C, and constantly decreased when subjected to 400°C, 700°C and 1000 °C. There were also variation of strengths at different percentages of EPA replacement. Highest compressive strength and flexural strength recorded were both at 200 °C with 65.52 MPa and 21.34 MPa respectively. The study conclude that by using EPA as aggregate replacement was ineffective below elevated temperatures but increased the performance of the mortar at elevated temperatures.

Compressive strength, flexural strength and water absorption of concrete containing palm oil kernel shell

NASA Astrophysics Data System (ADS)

Noor, Nurazuwa Md; Xiang-ONG, Jun; Noh, Hamidun Mohd; Hamid, Noor Azlina Abdul; Kuzaiman, Salsabila; Ali, Adiwijaya

2017-11-01

Effect of inclusion of palm oil kernel shell (PKS) and palm oil fibre (POF) in concrete was investigated on the compressive strength and flexural strength. In addition, investigation of palm oil kernel shell on concrete water absorption was also conducted. Total of 48 concrete cubes and 24 concrete prisms with the size of 100mm × 100mm × 100mm and 100mm × 100mm × 500mm were prepared, respectively. Four (4) series of concrete mix consists of coarse aggregate was replaced by 0%, 25%, 50% and 75% palm kernel shell and each series were divided into two (2) main group. The first group is without POF, while the second group was mixed with the 5cm length of 0.25% of the POF volume fraction. All specimen were tested after 7 and 28 days of water curing for a compression test, and flexural test at 28 days of curing period. Water absorption test was conducted on concrete cube age 28 days. The results showed that the replacement of PKS achieves lower compressive and flexural strength in comparison with conventional concrete. However, the 25% replacement of PKS concrete showed acceptable compressive strength which within the range of requirement for structural concrete. Meanwhile, the POF which should act as matrix reinforcement showed no enhancement in flexural strength due to the balling effect in concrete. As expected, water absorption was increasing with the increasing of PKS in the concrete cause by the porous characteristics of PKS

Investigation on Failures of Composite Beam and Substrate Concrete due to Drying Shrinkage Property of Repair Materials

NASA Astrophysics Data System (ADS)

Pattnaik, Rashmi Ranjan

2017-06-01

A Finite Element Analysis (FEA) and an experimental study was conducted on composite beam of repair material and substrate concrete to investigate the failures of the composite beam due to drying shrinkage property of the repair materials. In FEA, the stress distribution in the composite beam due to two concentrate load and shrinkage of repair materials were investigated in addition to the deflected shape of the composite beam. The stress distributions and load deflection shapes of the finite element model were investigated to aid in analysis of the experimental findings. In the experimental findings, the mechanical properties such as compressive strength, split tensile strength, flexural strength, and load-deflection curves were studied in addition to slant shear bond strength, drying shrinkage and failure patterns of the composite beam specimens. Flexure test was conducted to simulate tensile stress at the interface between the repair material and substrate concrete. The results of FEA were used to analyze the experimental results. It was observed that the repair materials with low drying shrinkage are showing compatible failure in the flexure test of the composite beam and deform adequately in the load deflection curves. Also, the flexural strength of the composite beam with low drying shrinkage repair materials showed higher flexural strength as compared to the composite beams with higher drying shrinkage value of the repair materials even though the strength of those materials were more.

Study on Mechanical Properties of Hybrid Fiber Reinforced Concrete

NASA Astrophysics Data System (ADS)

He, Dongqing; Wu, Min; Jie, Pengyu

2017-12-01

Several common high elastic modulus fibers (steel fibers, basalt fibers, polyvinyl alcohol fibers) and low elastic modulus fibers (polypropylene fiber) are incorporated into the concrete, and its cube compressive strength, splitting tensile strength and flexural strength are studied. The test result and analysis demonstrate that single fiber and hybrid fiber will improve the integrity of the concrete at failure. The mechanical properties of hybrid steel fiber-polypropylene fiber reinforced concrete are excellent, and the cube compressive strength, splitting tensile strength and flexural strength respectively increase than plain concrete by 6.4%, 3.7%, 11.4%. Doped single basalt fiber or polypropylene fiber and basalt fibers hybrid has little effect on the mechanical properties of concrete. Polyvinyl alcohol fiber and polypropylene fiber hybrid exhibit ‘negative confounding effect’ on concrete, its splitting tensile and flexural strength respectively are reduced by 17.8% and 12.9% than the single-doped polyvinyl alcohol fiber concrete.

Deflection and Flexural Strength Effects on the Roughness of Aesthetic-Coated Orthodontic Wires.

PubMed

Albuquerque, Cibele Gonçalves de; Correr, Américo Bortolazzo; Venezian, Giovana Cherubini; Santamaria, Milton; Tubel, Carlos Alberto; Vedovello, Silvia Amélia Scudeler

2017-01-01

The aim was to evaluate the flexural strength and the effects of deflection on the surface roughness of esthetic orthodontic wires. The sample consisted of 70 archwire 0.014-inch: polytetrafluorethylene (PTFE)-coated Nickel-Titanium (Niti) archwires (Titanol Cosmetic-TC, Flexy Super Elastic Esthetic-FSE, esthetic Nickel Titanium Wire-ANT); epoxy resin-coated Niti archwires (Spectra-S, Niticosmetic-TEC); gold and rhodium coated Niti (Sentalloy-STC) and a control group (superelastic Niti (Nitinol-NS). The initial roughness was evaluated with a rugosimeter. After that, the wires were submitted to flexural test in an universal testing machine. Each wire was deflected up to 2 mm at a speed of 1 mm/min. After flexural test, the roughness of the wires was evaluted on the same surface as that used for the initial evaluation. The data of roughness and flexural strength were analyzed by one-way ANOVA and Tukey's test (a=0.05). Student t-test compared roughness before and after deflection (a =0.05). The roughness of S and ANT (epoxy resin and PTFE-coated wires, respectively), before and after deflection, was significantly higher than the other groups (p<0.05). Wire deflection significantly increased the roughness of the wires S and STC (p<0.05). The flexural strength of groups FSE and NS (PTFE and uncoated) was higher compared with that of the other groups (p<0.05). We concluded that the roughness and flexural strength of the orthodontic wires does not depend on the type of the esthetic coating, but it is influenced by the method of application of this coating. The deflection can increase the roughness of the esthetic orthodontic wires.

Viscoelastic analysis of a dental metal-ceramic system

NASA Astrophysics Data System (ADS)

Özüpek, Şebnem; Ünlü, Utku Cemal

2012-11-01

Porcelain-fused-to-metal (PFM) restorations used in prosthetic dentistry contain thermal stresses which develop during the cooling phase after firing. These thermal stresses coupled with the stresses produced by mechanical loads may be the dominant reasons for failures in clinical situations. For an accurate calculation of these stresses, viscoelastic behavior of ceramics at high temperatures should not be ignored. In this study, the finite element technique is used to evaluate the effect of viscoelasticity on stress distributions of a three-point flexure test specimen, which is the current international standard, ISO 9693, to characterize the interfacial bond strength of metal-ceramic restorative systems. Results indicate that the probability of interfacial debonding due to normal tensile stress is higher than that due to shear stress. This conclusion suggests modification of ISO 9693 bond strength definition from one in terms of the shear stress only to that accounting for both normal and shear stresses.

Flexure and impact properties of glass fiber reinforced nylon 6-polypropylene composites

NASA Astrophysics Data System (ADS)

Kusaseh, N. M.; Nuruzzaman, D. M.; Ismail, N. M.; Hamedon, Z.; Azhari, A.; Iqbal, A. K. M. A.

2018-03-01

In recent years, polymer composites are rapidly developing and replacing the metals or alloys in numerous engineering applications. These polymer composites are the topic of interests in industrial applications such as automotive and aerospace industries. In the present research study, glass fiber (GF) reinforced nylon 6 (PA6)-polypropylene (PP) composite specimens were prepared successfully using injection molding process. Test specimens of five different compositions such as, 70%PA6+30%PP, 65%PA6+30%PP+5%GF, 60%PA6+30%PP+10%GF, 55%PA6+30%PP+15%GF and 50%PA6+30%PP+20%GF were prepared. In the experiments, flexure and impact tests were carried out. The obtained results revealed that flexure and impact properties of the polymer composites were significantly influenced by the glass fiber content. Results showed that flexural strength is low for pure polymer blend and flexural strength of GF reinforced composite increases gradually with the increase in glass fiber content. Test results also revealed that the impact strength of 70%PA6+30%PP is the highest and 55%PA6+30%PP+15%GF composite shows moderate impact strength. On the other hand, 50%PA6+30%PP+20%GF composite shows low toughness or reduced impact strength.

Wear, strength, modulus and hardness of CAD/CAM restorative materials.

PubMed

Lawson, Nathaniel C; Bansal, Ritika; Burgess, John O

2016-11-01

To measure the mechanical properties of several CAD/CAM materials, including lithium disilicate (e.max CAD), lithium silicate/zirconia (Celtra Duo), 3 resin composites (Cerasmart, Lava Ultimate, Paradigm MZ100), and a polymer infiltrated ceramic (Enamic). CAD/CAM blocks were sectioned into 2.5mm×2.5mm×16mm bars for flexural strength and elastic modulus testing and 4mm thick blocks for hardness and wear testing. E.max CAD and half the Celtra Duo specimens were treated in a furnace. Flexural strength specimens (n=10) were tested in a three-point bending fixture. Vickers microhardness (n=2, 5 readings per specimen) was measured with a 1kg load and 15s dwell time. The CAD/CAM materials as well as labial surfaces of human incisors were mounted in the UAB wear device. Cusps of human premolars were mounted as antagonists. Specimens were tested for 400,000 cycles at 20N force, 2mm sliding distance, 1Hz frequency, 24°C, and 33% glycerin lubrication. Volumetric wear and opposing enamel wear were measured with non-contact profilometry. Data were analyzed with 1-way ANOVA and Tukey post-hoc analysis (alpha=0.05). Specimens were observed with SEM. Properties were different for each material (p<0.01). E.max CAD and Celtra Duo were generally stronger, stiffer, and harder than the other materials. E.max CAD, Celtra Duo, Enamic, and enamel demonstrated signs of abrasive wear, whereas Cerasmart, Lava Ultimate, Paradigm MZ100 demonstrated signs of fatigue. Resin composite and resin infiltrated ceramic materials have demonstrated adequate wear resistance for load bearing restorations, however, they will require at least similar material thickness as lithium disilicate restorations due to their strength. Copyright © 2016 The Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Flexural performance of steel fiber reinforced concrete (SFRC) ribbed slab with various topping thicknesses

NASA Astrophysics Data System (ADS)

Rahman, Fadhillah Abdul; Bakar, Afidah Abu; Hashim, Mohd Hisbany Mohd; Ahmad, Hazrina

2017-11-01

Ribbed slab provides lighter slab than an equivalent solid slab which helps in reducing the weight with its voids. However, in order to overcome the drawbacks in the construction process, the application of steel fibre reinforcement concrete (SFRC) is seen as an alternative material to be used in the slab. This study is performed to investigate the behaviour of SFRC as the main material in ribbed slab, omitting the conventional reinforcements, under four-point bending test. Three equivalent samples of ribbed slabs were prepared for this study with variations in the topping thickness of 100, 75 and 50 mm. The flexural strength of ribbed slab with 100 mm topping shows similar loading carrying capacity with the 75mm topping while 50 mm gave the lowest ultimate loading. First cracks for all slabs occurred at the topping. The cracks began from the external ribs and propagates toward the internal rib. Incorporation of steel fibres help in giving a longer deflection softening than a sudden brittle failure, thus proves its ability to increase energy absorption capacity and improving cracking behaviour.

Modified glass fibre reinforced polymer composites

NASA Astrophysics Data System (ADS)

Cao, Yumei

A high ratio of strength to density and relatively low-cost are some of the significant features of glass fibre reinforced polymer composites (GFRPCs) that made them one of the most rapidly developed materials in recent years. They are widely used as the material of construction in the areas of aerospace, marine and everyday life, such as airplane, helicopter, boat, canoe, fishing rod, racket, etc. Traditionally, researchers tried to raise the mechanical properties and keep a high strength/weight ratio using all or some of the following methods: increasing the volume fraction of the fibre; using different polymeric matrix material; or changing the curing conditions. In recent years, some new techniques and processing methods were developed to further improve the mechanical properties of glass fibre (GF) reinforced polymer composite. For example, by modifying the surface condition of the GF, both the interface strength between the GF and the polymer matrix and the shear strength of the final composite can be significantly increased. Also, by prestressing the fibre during the curing process of the composite, the tensile, flexural and the impact properties of the composite can be greatly improved. In this research project, a new method of preparing GFRPCs, which combined several traditional and modern techniques together, was developed. This new method includes modification of the surface of the GF with silica particles, application of different levels of prestressing on the GF during the curing process, and the change of the fibre volume fraction and curing conditions in different sets of experiments. The results of the new processing were tested by the three-point bend test, the short beam shear test and the impact test to determine the new set of properties so formed in the composite material. Scanning electronic microscopy (SEM) was used to study the fracture surface of the new materials after the mechanical tests were performed. By taking advantages of the traditional and modern techniques at the same time, the newly developed modified glass fibre reinforced epoxy matrix composites (MGFRECs) have much improved comprehensive properties. The flexural strength, the flexural modulus, the shear modulus and the impact energy (Izod impact test) of the composites were improved up to 87%, 74%, 30% and 89% respectively when modified samples were compared to the samples made by the traditional methods.

Color stability and flexural strength of poly (methyl methacrylate) and bis-acrylic composite based provisional crown and bridge auto-polymerizing resins exposed to beverages and food dye: an in vitro study.

PubMed

Gujjari, Anil K; Bhatnagar, Vishrut M; Basavaraju, Ravi M

2013-01-01

To evaluate the color stability and flexural strength of poly (methyl methacrylate) (PMMA) and bis-acrylic composite based provisional crown and bridge auto-polymerizing resins exposed to tea, coffee, cola, and food dye. Two provisional crown and bridge resins, one DPI self-cure tooth molding powder (PMMA) (Group A), and one Protemp 4 Temporization Material (bis-acrylic composite) (Group B) were used. Disk-shaped specimens for color stability testing (n = 30 for each material) and bar-shaped specimens for flexural strength testing (n = 30 for each material) were fabricated using a metal mold. The specimens were immersed in artificial saliva, artificial saliva + tea, artificial saliva + coffee, artificial saliva + cola, and artificial saliva + food dye solutions and stored in an incubator at 37°C. Color measurements were taken before immersion, and then after 3 and 7 days of immersion. Flexural strength was evaluated after 7 days of immersion. Group A showed significantly higher color stability as compared to Group B, and artificial saliva + coffee solution had the most staining capacity for the resins. Test solutions had no effect on the flexural strength of Group A, but Group B specimens immersed in artificial saliva + cola showed significantly lower flexural strength values as compared to the control group. The findings of the study showed that for materials used in the study, PMMA was more color stable than bis-acrylic composite based resin. Also, material based on PMMA was more resistant to damage from dietary beverages as compared to bis-acrylic composite based provisional crown and bridge resin.

Seismic Response Of Masonry Plane Walls: A Numerical Study On Spandrel Strength

DOE Office of Scientific and Technical Information (OSTI.GOV)

Betti, Michele; Galano, Luciano; Vignoli, Andrea

2008-07-08

The paper reports the results of a numerical investigation on masonry walls subjected to in-plane seismic loads. This research aims to verify the formulae of shear and flexural strength of masonry spandrels which are given in the recent Italian Standards. Seismic pushover analyses have been carried out using finite element models of unreinforced walls and strengthened walls introducing reinforced concrete (RC) beams at the floor levels. Two typologies of walls have been considered distinguished for the height to length ratio h/l of the spandrels: a) short beams (h/l = 1.33) and b) slender beams (h/l = 0.5). Results obtained formore » the unreinforced and the strengthened walls are compared with equations for shear and flexural strength provided in Standards [1]. The numerical analyses show that the reliability of these equations is at least questionable especially for the prediction of the flexural strength. In the cases in which the axial force has not been determined by the structural analysis, Standards seems to overestimate the flexural strength of short spandrels both for the unreinforced and the strengthened wall.« less

Seismic Response Of Masonry Plane Walls: A Numerical Study On Spandrel Strength

NASA Astrophysics Data System (ADS)

Betti, Michele; Galano, Luciano; Vignoli, Andrea

2008-07-01

The paper reports the results of a numerical investigation on masonry walls subjected to in-plane seismic loads. This research aims to verify the formulae of shear and flexural strength of masonry spandrels which are given in the recent Italian Standards [1]. Seismic pushover analyses have been carried out using finite element models of unreinforced walls and strengthened walls introducing reinforced concrete (RC) beams at the floor levels. Two typologies of walls have been considered distinguished for the height to length ratio h/l of the spandrels: a) short beams (h/l = 1.33) and b) slender beams (h/l = 0.5). Results obtained for the unreinforced and the strengthened walls are compared with equations for shear and flexural strength provided in Standards [1]. The numerical analyses show that the reliability of these equations is at least questionable especially for the prediction of the flexural strength. In the cases in which the axial force has not been determined by the structural analysis, Standards [1] seems to overestimate the flexural strength of short spandrels both for the unreinforced and the strengthened wall.

The determination of resistance of marble to thermal and moisture cycles: relevance and limits of the recent European natural stone standard

NASA Astrophysics Data System (ADS)

Bellopede, Rossana; Castelletto, Eleonora; Marini, Paola; Zichella, Lorena

2015-04-01

The recent European standard EN 16306:2013 specifies laboratory methodology on the determination of the resistance to thermal and moisture cycling of marble for cladding of building façades. In particular measurements of bowing and flexural strength should be performed before and at the end of the ageing cycles. Bowing is measured on specimens of dimension 30*100*400mm exposed to moisture from beneath and heating (gradually till 80°C) on the upper face. The flexural strength should be measured both on reference and on exposed specimens in order to assess the variation of mechanical properties. Additional non-destructive tests are foreseen but are not compulsory for the standard. Moreover, the Annex A of the EN 16306, contains a guidance of the limit values that could be useful for the building planner for façade panels dimensioning. Different varieties of marble (two from Italy, one from Greece and three from Portugal) have been tested by means of this laboratory ageing test. Non-destructive tests such as the measurements of Ultrasonic Pulse Velocity (UPV), porosity, and water absorption have been executed together with the conventional flexural strength test. Image analysis on thin sections soaked with methylene blue have been analysed to further investigate the correlation between porosity and tendency to bowing. Base on the results obtained, some consideration on the decrease of mechanical resistance and the bowing in relation to the variety of marble tested and the limit values indicated the Annex A of EN 16306 can be drawn. Besides, from the data analysed a deepened discussion has been made. It is known that bowing and rapid strength loss occur in some varieties of marble when used as exterior cladding but further considerations can be made: bowing and flexural strength are correlate and in which way? Often the bowing is related to the decrease of flexural strength but it happens that there is a decrease in the mechanical resistance of the stone also without the bowing phenomenon. Non-destructive tests are surely useful to evaluate deterioration of mechanical properties but attention should be paid to the analysis of results, correlating the information coming from UPV measures with that from porosity evaluation.

Nose Fairing Modeling and Simulation to Support Trident II D5 Lifecycle Extension

DTIC Science & Technology

2013-09-01

Rupture Flexural Modulus Flexural Yield strength Compressive Yield strength Poissons Ratio Machinabi lily Shear strength Impact Work to...Categories: Ceramic; Glass; Glass Fiber , other Engineeting Material; C<>mposite Rbers Material Notes: Used as a reinforcing agent in fiber glass compos~es...MATWEB AMERICAN SITKA SPRUCE WOOD .......................35 APPENDIX B. MATWEB E–GLASS FIBER , GENERIC ......................................37 APPENDIX

Synthesis of Zinc Oxide Nanoparticles and Their Effect on the Compressive Strength and Setting Time of Self-Compacted Concrete Paste as Cementitious Composites

PubMed Central

Arefi, Mohammad Reza; Rezaei-Zarchi, Saeed

2012-01-01

In the present study, the mechanical properties of self-compacting concrete were investigated after the addition of different amounts of ZnO nanoparticles. The zinc oxide nanoparticles, with an average particle size of about 30 nm, were synthesized and their properties studied with the help of a scanning electron microscope (SEM) and X-ray diffraction. The prepared nanoparticles were partially added to self-compacting concrete at different concentrations (0.05, 0.1, 0.2, 0.5 and 1.0%), and the mechanical (flexural and split tensile) strength of the specimens measured after 7, 14, 21 and 28 days, respectively. The present results have shown that the ZnO nanoparticles were able to improve the flexural strength of self-compacting concrete. The increased ZnO content of more than 0.2% could increase the flexural strength, and the maximum flexural and split tensile strength was observed after the addition of 0.5% nanoparticles. Finally, ZnO nanoparticles could improve the pore structure of the self-compacted concrete and shift the distributed pores to harmless and less-harmful pores, while increasing mechanical strength. PMID:22605981

Synthesis of zinc oxide nanoparticles and their effect on the compressive strength and setting time of self-compacted concrete paste as cementitious composites.

PubMed

Arefi, Mohammad Reza; Rezaei-Zarchi, Saeed

2012-01-01

In the present study, the mechanical properties of self-compacting concrete were investigated after the addition of different amounts of ZnO nanoparticles. The zinc oxide nanoparticles, with an average particle size of about 30 nm, were synthesized and their properties studied with the help of a scanning electron microscope (SEM) and X-ray diffraction. The prepared nanoparticles were partially added to self-compacting concrete at different concentrations (0.05, 0.1, 0.2, 0.5 and 1.0%), and the mechanical (flexural and split tensile) strength of the specimens measured after 7, 14, 21 and 28 days, respectively. The present results have shown that the ZnO nanoparticles were able to improve the flexural strength of self-compacting concrete. The increased ZnO content of more than 0.2% could increase the flexural strength, and the maximum flexural and split tensile strength was observed after the addition of 0.5% nanoparticles. Finally, ZnO nanoparticles could improve the pore structure of the self-compacted concrete and shift the distributed pores to harmless and less-harmful pores, while increasing mechanical strength.

Properties of Experimental Dental Composites Containing Antibacterial Silver-Releasing Filler.

PubMed

Stencel, Robert; Kasperski, Jacek; Pakieła, Wojciech; Mertas, Anna; Bobela, Elżbieta; Barszczewska-Rybarek, Izabela; Chladek, Grzegorz

2018-06-18

Secondary caries is one of the important issues related to using dental composite restorations. Effective prevention of cariogenic bacteria survival may reduce this problem. The aim of this study was to evaluate the antibacterial activity and physical properties of composite materials with silver sodium hydrogen zirconium phosphate (SSHZP). The antibacterial filler was introduced at concentrations of 1%, 4%, 7%, 10%, 13%, and 16% ( w / w ) into model composite material consisting of methacrylate monomers and silanized glass and silica fillers. The in vitro reduction in the number of viable cariogenic bacteria Streptococcus mutans ATCC 33535 colonies, Vickers microhardness, compressive strength, diametral tensile strength, flexural strength, flexural modulus, sorption, solubility, degree of conversion, and color stability were investigated. An increase in antimicrobial filler concentration resulted in a statistically significant reduction in bacteria. There were no statistically significant differences caused by the introduction of the filler in compressive strength, diametral tensile strength, flexural modulus, and solubility. Statistically significant changes in degree of conversion, flexural strength, hardness (decrease), solubility (increase), and in color were registered. A favorable combination of antibacterial properties and other properties was achieved at SSHZP concentrations from 4% to 13%. These composites exhibited properties similar to the control material and enhanced in vitro antimicrobial efficiency.

Experimental investigations of timber beams strengthened by CFRP and Rebars under bending

NASA Astrophysics Data System (ADS)

Nianqiang, Zhou; Weixing, Shi

2017-04-01

Wooden structure houses deteriorate over time due to environmental aging, fatigue, and other reasons. In order to solve this problem, composite timber beams strengthened by extra steel bars (rebar) and carbon fiber-reinforced plastic (CFRP) are studied experimentally in this paper. Specimens with various strenghting, ie., rebars only, CFRP only, and a combination of the two, were considered under four-point flexural tests. Failure, displacement and strain response and ductility capacity were evaluated for the present tested models. Dramatic enhancement of the capacity in addition to improved deflection and ductility were gained for the strengthened beams relative to the plain specimens, indicating the effectiveness of the reinforcement on the flexural strength of such composite beams.

Preparation and Mechanical Behavior of Glass-Ceramics from Feldspathic Frits

NASA Astrophysics Data System (ADS)

da Silva, Fernanda A. N. G.; Barbato, Carla N.; França, Silvia C. A.; Silva, Ana Lúcia N.; de Andrade, Mônica C.

2017-10-01

Glass-ceramics were produced from frits with feldspar (79.09% wt/wt), alumina, sodium carbonate, potassium carbonate, borax and cerium dioxide. Feldspathic frits obtained at 1200 °C were shaped and sintered at various temperatures. Flexural strength results were analyzed by using the Weibull statistical distribution. These materials were also characterized by x-ray diffraction and scanning electron microscopy (SEM). At 600 °C, an initial leucite formation occurred as a crystalline phase, but the amorphous phase still prevailed, with low flexural strength. On the other hand, when the temperature increased to 800 °C, flexural strength also increased to approximately 70 MPa and Weibull modulus, m = 4.4 . This behavior was explained by the formation of leucite crystals dispersed within the glassy matrix, which hinders, in a certain concentration, the propagation of cracks. However, for the sintering temperature of 1000 °C, flexural strength decreased and may be associated with higher levels of this leucite crystal, in spite of the higher reliability m = 6.6.

High strength fused silica flexures manufactured by femtosecond laser

NASA Astrophysics Data System (ADS)

Bellouard, Yves; Said, Ali A.; Dugan, Mark; Bado, Philippe

2009-02-01

Flexures are mechanical elements used in micro- and precision-engineering to precisely guide the motion of micro-parts. They consist of slender bodies that deform elastically upon the application of a force. Although counter-intuitive at first, fused silica is an attractive material for flexure. Pending that the machining process does not introduce surface flaws that would lead to catastrophic failure, the material has a theoretically high ultimate tensile strength of several GPa. We report on high-aspect ratio fused silica flexures manufactured by femtosecond laser combined with chemical etching. Notch-hinges with thickness as small as twenty microns and aspect ratios comparable to aspect ratios obtained by Deep- Reactive-Ion-Etching (DRIE) were fabricated and tested under different loading conditions. Multiple fracture tests were performed for various loading conditions and the cracks morphologies were analyzed using Scanning Electron Microscopy. The manufactured elements show outstanding mechanical properties with flexural strengths largely exceeding those obtained with other technologies and materials. Fused silica flexures offer a mean to combine integrated optics with micro-mechanics in a single monolithic substrate. Waveguides and mechanical elements can be combined in a monolithic devices opening new opportunities for integrated opto-mechatronics devices.

Effects of core-to-dentin thickness ratio on the biaxial flexural strength, reliability, and fracture mode of bilayered materials of zirconia core (Y-TZP) and veneer indirect composite resins.

PubMed

Su, Naichuan; Liao, Yunmao; Zhang, Hai; Yue, Li; Lu, Xiaowen; Shen, Jiefei; Wang, Hang

2017-01-01

Indirect composite resins (ICR) are promising alternatives as veneering materials for zirconia frameworks. The effects of core-to-dentin thickness ratio (C/Dtr) on the mechanical property of bilayered veneer ICR/yttria-tetragonal zirconia polycrystalline (Y-TZP) core disks have not been previously studied. The purpose of this in vitro study was to assess the effects of C/Dtr on the biaxial flexural strength, reliability, and fracture mode of bilayered veneer ICR/ Y-TZP core disks. A total of 180 bilayered 0.6-mm-thick composite resin disks in core material and C/Dtr of 2:1, 1:1, and 1:2 were tested with either core material placed up or placed down for piston-on-3-ball biaxial flexural strength. The mean biaxial flexural strength, Weibull modulus, and fracture mode were measured to evaluate the variation trend of the biaxial flexural strength, reliability, and fracture mode of the bilayered disks with various C/Dtr. One-way analysis of variance (ANOVA) and chi-square tests were used to evaluate the variation tendency of fracture mode with the C/Dtr or material placed down during testing (α=.05). Light microscopy was used to identify the fracture mode. The mean biaxial flexural strength and reliability improved with the increase in C/Dtr when specimens were tested with the core material either up and down, and depended on the materials that were placed down during testing. The rates of delamination, Hertzian cone cracks, subcritical radial cracks, and number of fracture fragments partially depended on the C/Dtr and the materials that were placed down during testing. The biaxial flexural strength, reliability, and fracture mode in bilayered structures of Y-TZP core and veneer ICR depend on both the C/Dtr and the material that was placed down during testing. Copyright © 2016 Editorial Council for the Journal of Prosthetic Dentistry. Published by Elsevier Inc. All rights reserved.

Compressive and flexural strength of concrete containing palm oil biomass clinker and polypropylene fibres

NASA Astrophysics Data System (ADS)

Ibrahim, M. H. Wan; Mangi, Sajjad Ali; Burhanudin, M. K.; Ridzuan, M. B.; Jamaluddin, N.; Shahidan, S.; Wong, YH; Faisal, SK; Fadzil, M. A.; Ramadhansyah, P. J.; Ayop, S. S.; Othman, N. H.

2017-11-01

This paper presents the effects of using palm oil biomass (POB) clinker with polypropylene (PP) fibres in concrete on its compressive and flexural strength performances. Due to infrastructural development works, the use of concrete in the construction industry has been increased. Simultaneously, it raises the demand natural sand, which causes depletion of natural resources. While considering the environmental and economic benefits, the utilization of industrial waste by-products in concrete will be the alternative solution of the problem. Among the waste products, one of such waste by-product is the palm oil biomass clinker, which is a waste product from burning processes of palm oil fibres. Therefore, it is important to utilize palm oil biomass clinker as partial replacement of fine aggregates in concrete. Considering the facts, an experimental study was conducted to find out the potential usage of palm oil fibres in concrete. In this study, total 48 number of specimens were cast to evaluate the compressive and flexural strength performances. Polypropylene fibre was added in concrete at the rate of 0.2%, 0.4% and 0.6%, and sand was replaced at a constant rate of 10% with palm oil biomass clinker. The flexural strength of concrete was noticed in the range of 2.25 MPa and 2.29 MPa, whereas, the higher value of flexural strength was recorded with 0.4% polypropylene fibre addition. Hence, these results show that the strength performances of concrete containing POB clinker could be improved with the addition of polypropylene fibre.

Influence of Grid Reinforcement Placed In Masonry Bed Joints on Its Flexural Strength

NASA Astrophysics Data System (ADS)

Piekarczyk, Adam

2017-10-01

The paper presents the test results of the flexural strength of masonry when plane of failure is perpendicular to the bed joints. Comparison tests of unreinforced specimens and specimens reinforced with steel wire, glass and basalt fibre grids applied in masonry bed joints showed the higher flexural strength and crack resistance of masonry reinforced in this manner and so loaded. Reinforced masonry exposed plastic character after cracking allow for large horizontal displacements and transfer the considerable loads perpendicular to their surface. The strengthening of masonry was observed in most tests of reinforced specimens leading to occurrence of the maximum load in after cracking phase.

Properties of porous magnesium prepared by powder metallurgy.

PubMed

Čapek, Jaroslav; Vojtěch, Dalibor

2013-01-01

Porous magnesium-based materials are biodegradable and promising for use in orthopaedic applications, but their applications are hampered by their difficult fabrication. This work reports the preparation of porous magnesium materials by a powder metallurgy technique using ammonium bicarbonate as spacer particles. The porosity of the materials depended on the amount of ammonium bicarbonate and was found to have strong negative effects on flexural strength and corrosion behaviour. However, the flexural strength of materials with porosities of up to 28 vol.% was higher than the flexural strength of non-metallic biomaterials and comparable with that of natural bone. Copyright © 2012 Elsevier B.V. All rights reserved.

Experimental and simulation study of flexural behaviour of woven Glass/Epoxy laminated composite plate

NASA Astrophysics Data System (ADS)

Sahoo, Sushree S.; Singh, Vijay K.; Panda, Subrata K.

2015-02-01

Flexural behaviour of cross ply laminated woven Glass/Epoxy composite plate has been investigated in this article. Flexural responses are examined by a three point bend test and tensile test carried out on INSTRON 5967 and Universal Testing Machine INSTRON 1195 respectively. The finite element model is developed in ANSYS parametric design language code and discretised using an eight nodded structural shell element. Convergence behaviour of the simulation result has been performed and validated by comparing the results with experimental values. The effects of various parameters such as side-to-thickness ratio, modular ratio on flexural behaviour of woven Glass/Epoxy laminated composite plate are discussed in details.

Mechanical properties of woven glass fiber-reinforced composites.

PubMed

Kanie, Takahito; Arikawa, Hiroyuki; Fujii, Koichi; Ban, Seiji

2006-06-01

The aim of this investigation was to measure the flexural and compressive strengths and the corresponding moduli of cylindrical composite specimens reinforced with woven glass fiber. Test specimens were made by light-curing urethane dimethacrylate oligomer with woven glass fiber of 0.18-mm standard thickness. Tests were conducted using four reinforcement methods and two specimen diameters. Flexural strength and modulus of woven glass fiber-reinforced specimens were significantly greater than those without woven glass fiber (p < 0.01). Likewise, compressive strength of reinforced specimens was significantly greater than those without woven glass fiber (p < 0.01), except for specimens reinforced with woven glass fiber oriented at a tilt direction in the texture (p > 0.05). In terms of comparison between the two specimen diameters, no statistically significant differences in flexural strength and compressive strength (p > 0.05) were observed.

Variations in lithospheric thickness on Venus

NASA Technical Reports Server (NTRS)

Johnson, C. L.; Sandwell, David T.

1992-01-01

Recent analyses of Magellan data have indicated many regions exhibiting topograhic flexure. On Venus, flexure is associated predominantly with coronae and the chasmata with Aphrodite Terra. Modeling of these flexural signatures allows the elastic and mechanical thickness of the lithosphere to be estimated. In areas where the lithosphere is flexed beyond its elastic limit the saturation moment provides information on the strength of the lithosphere. Modeling of 12 flexural features on Venus has indicated lithospheric thicknesses comparable with terrestrial values. This has important implications for the venusian heat budget. Flexure of a thin elastic plate due simultaneously to a line load on a continuous plate and a bending moment applied to the end of a broken plate is considered. The mean radius and regional topographic gradient are also included in the model. Features with a large radius of curvature were selected so that a two-dimensional approximation could be used. Comparisons with an axisymmetric model were made for some features to check the validity of the two-dimensional assumption. The best-fit elastic thickness was found for each profile crossing a given flexural feature. In addition, the surface stress and bending moment at the first zero crossing of each profile were also calculated. Flexural amplitudes and elastic thicknesses obtained for 12 features vary significantly. Three examples of the model fitting procedures are discussed.

Modification of glass fibers to improve reinforcement: a plasma polymerization technique.

PubMed

Cökeliler, Dilek; Erkut, Selim; Zemek, Josef; Biederman, Hynek; Mutlu, Mehmet

2007-03-01

This study evaluates the effect of plasma treated E-glass fiber to improve the mechanical properties of acrylic resin denture base material, polymethylmethacrlyate (PMMA). Plasma surface treatment of fibers is used as reinforcement in composite materials to modify the chemical and physical properties of their surfaces with tailored fiber-matrix bonding strength. Three different types of monomer 2-hydroxyethyl methacrylate (HEMA), triethyleneglycoldimethylether (TEGDME) and ethylenediamine (EDA) were used in the plasma polymerization modification of glass fibers. A radiofrequency generator was used to sustain plasma in a glass vacuum chamber. Glass fibers were modified at the same glow-discharge power of 25 W and exposure time of 30 min for each monomer. Fibers were incorporated into the acrylic with 1% (w/w) loading except control group. Specimens were prepared using a standard mold of 3 cmx0.5 cmx0.8 cm in dimension with eight specimens in each group. Samples were subjected to a flexural strength test set up at a crosshead speed of 5mm/min. Scanning electron microscopy (SEM) was used to examine the microstructure and X-ray photoelectron spectroscopy (XPS) was used for chemical analysis of the surface. Data were analyzed by means of ANOVA and Duncan's tests. Test results revealed that fiber reinforcement had a significant effect on the flexural strength of the specimens (p<0.05). Among the fiber reinforced groups, plasma treatment with EDA monomer resulted in the most significant increase in flexural strength values (p<0.05). XPS results have shown an increasing number of nitrogenous compounds in EDA treated fibers. The chemical structure of the surface, especially with the increase in nitrogenous compounds could give an idea for the amine film deposition and SEM figures showed an increase in surface roughness. The results showed that plasma treatment with EDA monomer was an effective alternative method of increasing the flexural strength of PMMA based denture base polymers through fiber reinforcement.

3D-WOVEN FIBER-REINFORCED COMPOSITE FOR CAD/CAM DENTAL APPLICATION

PubMed Central

Petersen, Richard; Liu, Perng-Ru

2016-01-01

Three-dimensional (3D)-woven noncrimp fiber-reinforced composite (FRC) was tested for mechanical properties in the two principal directions of the main XY plane and compared to different Computer-Aided-Design/Computer-Aided-Machining (CAD/CAM) Dental Materials. The Dental Materials included ceramic with Vitablock Mark II®, ProCAD®, InCeram® Spinel, InCeram® Alumina and InCeram® Zirconia in addition to a resin-based 3M Corp. Paradigm® particulate-filled composite. Alternate material controls included Coors 300 Alumina Ceramic and a tungsten carbide 22% cobalt cermet. The 3D-woven FRC was vacuum assisted resin transfer molding processed as a one-depth-thickness ~19-mm preform with a vinyl-ester resin and cut into blocks similar to the commercial CAD/CAM Dental Materials. Mechanical test samples prepared for a flexural three-point span length of 10.0 mm were sectioned for minimum-depth cuts to compare machinability and fracture resistance between groups. 3D-woven FRC improved mechanical properties with significant statistical differences over all CAD/CAM Dental Materials and Coors Alumina Ceramic for flexural strength (p<0.001), resilience (p<0.05), work of fracture (p<0.001), strain energy release (p<0.05), critical stress intensity factor (p<0.001) and strain (p<0.001). PMID:27642198

3D-WOVEN FIBER-REINFORCED COMPOSITE FOR CAD/CAM DENTAL APPLICATION.

PubMed

Petersen, Richard; Liu, Perng-Ru

2016-05-01

Three-dimensional (3D)-woven noncrimp fiber-reinforced composite (FRC) was tested for mechanical properties in the two principal directions of the main XY plane and compared to different Computer-Aided-Design/Computer-Aided-Machining (CAD/CAM) Dental Materials. The Dental Materials included ceramic with Vitablock Mark II®, ProCAD®, InCeram® Spinel, InCeram® Alumina and InCeram® Zirconia in addition to a resin-based 3M Corp. Paradigm® particulate-filled composite. Alternate material controls included Coors 300 Alumina Ceramic and a tungsten carbide 22% cobalt cermet. The 3D-woven FRC was vacuum assisted resin transfer molding processed as a one-depth-thickness ~19-mm preform with a vinyl-ester resin and cut into blocks similar to the commercial CAD/CAM Dental Materials. Mechanical test samples prepared for a flexural three-point span length of 10.0 mm were sectioned for minimum-depth cuts to compare machinability and fracture resistance between groups. 3D-woven FRC improved mechanical properties with significant statistical differences over all CAD/CAM Dental Materials and Coors Alumina Ceramic for flexural strength (p<0.001), resilience (p<0.05), work of fracture (p<0.001), strain energy release (p<0.05), critical stress intensity factor (p<0.001) and strain (p<0.001).

Mechanical properties and polymerization shrinkage of composite resins light-cured using two different lasers.

PubMed

Kim, Tae-Wan; Lee, Jang-Hoon; Jeong, Seung-Hwa; Ko, Ching-Chang; Kim, Hyung-Il; Kwon, Yong Hoon

2015-04-01

The purpose of the present study was to investigate the usefulness of 457 and 473 nm lasers for the curing of composite resins during the restoration of damaged tooth cavity. Monochromaticity and coherence are attractive features of laser compared with most other light sources. Better polymerization of composite resins can be expected. Eight composite resins were light cured using these two lasers and a light-emitting diode (LED) light-curing unit (LCU). To evaluate the degrees of polymerization achieved, polymerization shrinkage and flexural and compressive properties were measured and compared. Polymerization shrinkage values by 457 and 473 nm laser, and LED ranged from 10.9 to 26.8, from 13.2 to 26.1, and from 11.5 to 26.3 μm, respectively. The values by 457 nm laser was significantly different from those by 473 and LED LCU (p<0.05). However, there was no statistical difference between values by 473 and LED LCU. Before immersion in distilled water, flexural strength (FS) and compressive modulus (CM) of the specimens were inconsistently influenced by LCUs. On the other hand, flexural modulus (FM) and compressive strength (CS) were not significantly different for the three LCUs (p>0.05). For the tested LCUs, no specific LCU could consistently achieve highest strength and modulus from the specimens tested. Two lasers (457 and 473 nm) can polymerize composite resins to the level that LED LCU can achieve despite inconsistent trends of polymerization shrinkage and flexural and compressive properties of the tested specimens.

Mechanical properties and flexure behaviour of lightweight foamed concrete incorporating coir fibre

NASA Astrophysics Data System (ADS)

Mohamad, Noridah; Afif Iman, Muhamad; Othuman Mydin, M. A.; Samad, A. A. A.; Rosli, J. A.; Noorwirdawati, A.

2018-04-01

This paper presents an experimental investigation on the mechanical properties and flexural behaviour of lightweight foamed concrete (LFC) with added coir fibre as filler. The compressive strength (Pt), tensile strength (Ft), modulus of elasticity (E), ultimate load and crack pattern of the foamed concrete were determined. The coir fibre was added to the foamed concrete mixture at 0.1%, 0.2% and 0.3% of the total weight of cement. Effects of various percentage of coir fibre used on foam concrete’s mechanical and properties and flexural behaviour were studied and analysed. It was found that the increase percentage of fibre resulted in increase in compressive strength, tensile strength and modulus of elasticity of LFC mixture. LFC with added coir of 0.3% experienced the smallest crack propagation.

Flexure fatigue testing of 90 deg graphite/epoxy composites

NASA Technical Reports Server (NTRS)

Peck, Ann Nancy W.

1995-01-01

A great deal of research has been performed characterizing the in-plane fiber-dominated properties, under both static and fatigue loading, of advanced composite materials. To the author's knowledge, no study has been performed to date investigating fatigue characteristics in the transverse direction. This information is important in the design of bonded composite airframe structure where repeated, cyclic out-of-plane bending may occur. Recent tests characterizing skin/stringer debond failures in reinforced composite panels where the dominant loading in the skin is flexure along the edge of the frame indicate failure initiated either in the skin or else the flange, near the flange tip. When failure initiated in the skin, transverse matrix cracks formed in the surface skin ply closest to the flange and either initiated delaminations or created matrix cracks in the next lower ply, which in turn initiated delaminations. When failure initiated in the flanges, transverse cracks formed in the flange angle ply closest to the skin and initiated delamination. In no configuration did failure propagate through the adhesive bond layer. For the examined skin/flange configurations, the maximum transverse tension stress at failure correlates very well with the transverse tension strength of the composites. Transverse tension strength (static) data of graphite epoxy composites have been shown to vary with the volume of material stressed. As the volume of material stressed increased, the strength decreased. A volumetric scaling law based on Weibull statistics can be used to predict the transverse strength measurements. The volume dependence reflects the presence of inherent flaws in the microstructure of the lamina. A similar approach may be taken to determine a volume scale effect on the transverse tension fatigue behavior of graphite/epoxy composites. The objective of this work is to generate transverse tension strength and fatigue S-N characteristics for composite materials using 3-point flexure tests of 90 deg graphite/epoxy specimens. Investigations will include the volume scale effect as well as frequency and span-to-thickness ratio effects. Prior to the start of the experimental study, an analytical study using finite element modeling will be performed to investigate the span-to-thickness effect. The ratio of transverse flexure stress to shear stress will be monitored and its values predicted by the FEM analysis compared with the value obtained using a 'strength of materials' based approach.

Reactive Melt Infiltration of Silicon-Niobium Alloys in Microporous Carbons

NASA Technical Reports Server (NTRS)

Singh, M.; Behrendt, D. R.

1994-01-01

Studies of the reactive melt infiltration of silicon-niobium alloys in microporous carbon preforms prepared by the pyrolysis of a polymer precursor have been carried out using modeling, Differential Thermal Analysis (DTA), and melt infiltration. Mercury porosimetry results indicate a very narrow pore size distribution with virtually all the porosity within the carbon preforms open to infiltrants. The morphology and amount of the residual phases (niobium disilicide and silicon) in the infiltrated material can be tailored according to requirements by careful control of the properties (pore size and pore volume) of the porous carbon preforms and alloy composition. The average room temperature four-point flexural strength of a reaction-formed silicon carbide material (made by the infiltration of medium pore size carbon preform with Si - 5 at. % Nb alloy) is 290 +/- 40 MPa (42 +/- 6 ksi) and the fracture toughness is 3.7 +/- 0.3 MPa square root of m. The flexural strength decreases at high temperatures due to relaxation of residual thermal stresses and the presence of free silicon in the material.

Acoustic emission monitoring of recycled aggregate concrete under bending

NASA Astrophysics Data System (ADS)

Tsoumani, A. A.; Barkoula, N.-M.; Matikas, T. E.

2015-03-01

The amount of construction and demolition waste has increased considerably over the last few years, making desirable the reuse of this waste in the concrete industry. In the present study concrete specimens are subjected at the age of 28 days to four-point bending with concurrent monitoring of their acoustic emission (AE) activity. Several concrete mixtures prepared using recycled aggregates at various percentages of the total coarse aggregate and also a reference mix using natural aggregates, were included to investigate their influence of the recycled aggregates on the load bearing capacity, as well as on the fracture mechanisms. The results reveal that for low levels of substitution the influence of using recycled aggregates on the flexural strength is negligible while higher levels of substitution lead into its deterioration. The total AE activity, as well as the AE signals emitted during failure, was related to flexural strength. The results obtained during test processing were found to be in agreement with visual observation.

Laboratory and environmental decay of wood–plastic composite boards: flexural properties

Treesearch

Rebecca Ibach; Marek Gnatowski; Grace Sun; Jessie Glaeser; Mathew Leung; John Haight

2017-01-01

The flexural properties of wood–plastic composite (WPC) deck boards exposed to 9.5 years of environmental decay in Hilo, Hawaii, were compared to samples exposed to moisture and decay fungi for 12 weeks in the laboratory, to establish a correlation between sample flexural properties and calculated void volume. Specimens were tested for flexural strength and modulus,...

Effect of nylon fiber on mechanical properties of cement based mortar

NASA Astrophysics Data System (ADS)

Hanif, I. M.; Syuhaili, M. R. Noor; Hasmori, M. F.; Shahmi, S. M.

2017-11-01

An investigation has been carried out to study the effect of nylon fiber on the mechanical properties of cement based mortar after receiving large quantities of nylon waste. Subsequently, this research was conducted to compare the compressive, tensile and flexural strength of normal cement based mortar with nylon fiber cement based mortar. All samples using constant water-cement ratio of 0.63 and three different percentages of nylon fiber were added in the mixture during the samples preparation period which consists of 0.5%, 1.5% and 2.5% by total weight of cement based mortar. The results obtained with different nylon percentage marked an increases in compressive strength (up to 17%), tensile strength (up to 21%) and flexural strength (up to 13%) when compared with control cement based mortar samples. Therefore, the results obtained from this study shows that by using nylon fiber as additive material can improve the mechanical properties of the cement based mortar and at the same time produce a good sustainable product that can protects and conserve the marine environment.

Study on extrusion process of SiC ceramic matrix

NASA Astrophysics Data System (ADS)

Dai, Xiao-Yuan; Shen, Fan; Ji, Jia-You; Wang, Shu-Ling; Xu, Man

2017-11-01

In this thesis, the extrusion process of SiC ceramic matrix has been systematically studied.The effect of different cellulose content on the flexural strength and pore size distribution of SiC matrix was discussed.Reselts show that with the increase of cellulose content, the flexural strength decreased.The pore size distribution in the sample was 1um-4um, and the 1um-2um concentration was more concentrated. It is found that the cellulose content has little effect on the pore size distribution.When the cellulose content is 7%, the flexural strength of the sample is 40.9Mpa. At this time, the mechanical properties of the sample are the strongest.

Glass fiber-reinforced thermoplastics for use in metal-free removable partial dentures: combined effects of fiber loading and pigmentation on color differences and flexural properties.

PubMed

Tanimoto, Yasuhiro; Nagakura, Manamu; Nishiyama, Norihiro

2018-02-21

The purpose of this study was to investigate the combined effects of fiber loading and pigmentation on the color differences and flexural properties of glass fiber-reinforced thermoplastics (GFRTPs), for use in non-metal clasp dentures (NMCDs). The GFRTPs consisted mainly of E-glass fibers, a polypropylene matrix, and a coloring pigment: the GFRTPs with various fiber loadings (0, 10, and 20mass%) and pigmentations (0, 1, 2, and 4mass%) were fabricated by using an injection molding. The color differences of GFRTPs were measured based on the Commission Internationale de l'Eclairage (CIE) Lab color system, by comparing with a commercially available NMCD. The flexural properties of GFRTPs were evaluated by using a three-point bending test, according to International Standards Organization (ISO) specification number 20795-1. The visible colors of GFRTPs with pigment contents of 2mass% were acceptable for gingival color, and the glass fibers harmonized well with the resins. The ΔE* values of the GFRTPs with pigment contents of 2mass% obtained by using the CIE Lab system were lowest at all fiber loadings. For GFRTPs with fiber contents of 10 and 20mass% at 2mass% pigment content, these GFRTPs surpassed the ISO 20795-1 specification regarding flexural strength (> 60MPa) and modulus (> 1.5GPa). A combination of the results of color difference evaluation and mechanical examination indicates that the GFRTPs with fiber contents of 10 or 20mass%, and with pigment contents of 2mass% have acceptable esthetic appearance and sufficient rigidity for NMCDs. Copyright © 2018 Japan Prosthodontic Society. Published by Elsevier Ltd. All rights reserved.

Compression and flexural strength of bone cement mixed with blood.

PubMed

Tan, J H; Koh, B Th; Ramruttun, A K; Wang, W

2016-08-01

To assess the compression and flexural strength of bone cement mixed with 0 ml, 1 ml, or 2 ml of blood. High viscosity polymethyl methacrylate (PMMA) loaded with or without gentamicin was used. Blood was collected from total knee arthroplasty patients. In the same operating room, one pack of cement each was mixed with 0 ml (control), 1 ml, or 2 ml of blood for 1 minute during the dough phase. The dough was extruded into cylindrical and rectangular moulds for 20 minutes of setting, and then cured in phosphate buffered saline at 37±1ºC for 7 days. The samples were visually inspected for fractures and areas of weakness, and then scanned using microcomputed tomography. 48 gentamicin-loaded and 59 non-gentamicin-loaded samples mixed with 0 ml (control), 1 ml, or 2 ml of blood were randomised for flexural and compression strength testing; each group had at least 6 samples. In samples loaded with or without gentamicin, the flexural and compressive strength was highest in controls, followed by samples mixed with 1 ml or 2 ml of blood. In samples mixed with 2 ml of blood, the flexural strength fell below the standard of 50 MPa. In samples mixed with 2 ml of blood and all gentamicin-loaded samples, the compressive strength fell below the standard of 70 MPa. Microcomputed tomography revealed areas of voids and pores indicating the presence of laminations and partitions within. The biomechanical strength of PMMA contaminated with blood may decrease. Precautions such as saline lavage, pack drying the bone, change of gloves, and prompt insertion of the implant should be taken to prevent blood from contaminating bone cement.

Biaxial flexural strength and microstructure changes of two recycled pressable glass ceramics.

PubMed

Albakry, Mohammad; Guazzato, Massimiliano; Swain, Michael Vincent

2004-09-01

This study evaluated the biaxial flexural strength and identified the crystalline phases and the microstructural features of pressed and repressed materials of the glass ceramics, Empress 1 and Empress 2. Twenty pressed and 20 repressed disc specimens measuring 14 mm x 1 mm per material were prepared following the manufacturers' recommendations. Biaxial flexure (piston on 3-ball method) was used to assess strength. X-ray diffraction was performed to identify the crystalline phases, and a scanning electron microscope was used to disclose microstructural features. Biaxial flexural strength, for the pressed and repressed specimens, respectively, were E1 [148 (SD 18) and 149 (SD 35)] and E2 [340 (SD 40), 325 (SD 60)] MPa. There was no significant difference in strength between the pressed and the repressed groups of either material, Empress 1 and Empress 2 (p > 0.05). Weibull modulus values results were E1: (8, 4.7) and E2: (9, 5.8) for the same groups, respectively. X-ray diffraction revealed that leucite was the main crystalline phase for Empress 1 groups, and lithium disilicate for Empress 2 groups. No further peaks were observed in the X-ray diffraction patterns of either material after repressing. Dispersed leucite crystals and cracks within the leucite crystals and glass matrix were features observed in Empress 1 for pressed and repressed samples. Similar microstructure features--dense lithium disilicate crystals within a glass matrix--were observed in Empress 2 pressed and repressed materials. However, the repressed material showed larger lithium disilicate crystals than the singly pressed material. Second pressing had no significant effect on the biaxial flexural strength of Empress 1 or Empress 2; however, higher strength variations among the repressed samples of the materials may indicate less reliability of these materials after second pressing.

The effect of thermal damage on the mechanical properties of polymer regrinds

NASA Technical Reports Server (NTRS)

Kundu, Nikhil K.

1990-01-01

Reprocessed polymers are subjected to high processing temperatures that result in the breakdown of molecular chains and changes in the molecular structures. These phenomena are reflected in the mechanical properties of materials. Practically every regrind is seen as a new material. These experiments deal with the molding, regrinding, and reprocessing of test specimens for the study of their mechanical properties. The comparative test data from each recycled material would give students an insight of the molecular structures and property degradation. Three important rheological and mechanical properties such as melt flow, impact strength, and flexural strength are to be determined. These properties play key roles in the selection of engineering materials. The material selected for demonstration was Makrolon 3000L, a polycarbonate thermoplastic from Bayer AG. The thermal degradation due to repeated processing is reflected in the decrease in molecular weight and breakdown of molecular chains causing increase in melt flow. The Izod-impact resistance and the flexural strength deteriorate gradually.

Fatigue and shear behavior of HPC bulb-tee girders: final report.

DOT National Transportation Integrated Search

2005-02-01

Five 96-ft. (29.3-m) long, 72-in. (1.83-m) deep, precast, pretensioned bulb-tee girders were tested to evaluate their behavior under flexural fatigue. Three of the girders were also tested to measure their static shear strength. One girder was tested...

Effects of programming and healing temperatures on the healing efficiency of a confined healable polymer composite

NASA Astrophysics Data System (ADS)

Yougoubare, Y. Quentin; Pang, Su-Seng

2014-02-01

In previous work, a biomimetic close-then-heal (CTH) healing mechanism was proposed and validated to repeatedly heal wide-open cracks in load carrying engineering structures by using constrained expansion of compression programmed thermoset shape memory polymers (SMPs). In this study, the effects on healing efficiencies of variation of temperature during both thermomechanical programming and shape recovery (healing) under three-dimensional (3D) confinement are evaluated. The polymer considered is a polystyrene shape memory polymer with 6% by volume of thermoplastic particle additives (copolyester) dispersed in the matrix. In addition to the programming and healing temperatures, some of the parameters investigated include the flexural strength, crack width and elemental composition at the crack interface. It is observed that while increase of the programming temperature is slightly beneficial to strength recovery, most of the strength recovered and damage repair are strongly dependent on the healing temperature. The best healing efficiency (63%) is achieved by a combination of a programming temperature above the glass transition temperature of the polymer and a healing temperature above the bonding point of the copolyester.

Effect of kenaf fiber in reinforced concrete slab

NASA Astrophysics Data System (ADS)

Syed Mohsin, S. M.; Baarimah, A. O.; Jokhio, G. A.

2018-04-01

The effect of kenaf fibers in reinforced concrete slab with different thickness is discusses and presented in this paper. Kenaf fiber is a type of natural fiber and is added in the reinforced concrete slab to improve the structure strength and ductility. For this study, three types of mixtures were prepared with fiber volume fraction of 0%, 1% and 2%, respectively. The design compressive strength considered was 20 MPa. Six cubes were prepared to be tested at 7th and 28th day. A total of six reinforced concrete slab with two variances of thickness were also prepared and tested under four-point bending test. The differences in the thickness is to study the potential of kenaf fiber to serve as part of shear reinforcement in reinforced concrete slab that was design to fail in shear. It was observed that, addition of kenaf fiber in reinforced concrete slab improves the flexural strength and ductility of the reinforced concrete slab. In the slab with reduction in thickness, the mode of failure change from brittle to ductile with the inclusion of kenaf fiber.

Flexural strength and reliability of monolithic and trilayer ceramic structures obtained by the CAD-on technique.

PubMed

Basso, G R; Moraes, R R; Borba, M; Griggs, J A; Della Bona, A

2015-12-01

To evaluate the flexural strength, Weibull modulus, fracture toughness, and failure behavior of ceramic structures obtained by the CAD-on technique, testing the null hypothesis that trilayer structures show similar properties to monolithic structures. Bar-shaped (1.8mm×4mm×16mm) monolithic specimens of zirconia (IPS e.max ZirCAD - Ivoclar Vivadent) and trilayer specimens of zirconia/fusion ceramic/lithium dissilicate (IPS e.max ZirCAD/IPS e.max CAD Crystall./Connect/IPS e.max CAD, Ivoclar Vivadent) were fabricated (n=30). Specimens were tested in flexure in 37°C deionized water using a universal testing machine at a crosshead speed of 0.5mm/min. Failure loads were recorded, and the flexural strength values were calculated. Fractography principles were used to examine the fracture surfaces under optical and scanning electron microscopy. Data were statistically analyzed using Student's t-test and Weibull statistics (α=0.05). Monolithic and trilayer specimens showed similar mean flexural strengths, characteristic strengths, and Weibull moduli. Trilayer structures showed greater mean critical flaw and fracture toughness values than monolithic specimens (p<0.001). Most critical flaws in the trilayer groups were located on the Y-TZP surface subjected to tension and propagated catastrophically. Trilayer structures showed no flaw deflection at the interface. Considering the CAD-on technique, the trilayer structures showed greater fracture toughness than the monolithic zirconia specimens. Copyright © 2015 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Flexural analysis of palm fiber reinforced hybrid polymer matrix composite

NASA Astrophysics Data System (ADS)

Venkatachalam, G.; Gautham Shankar, A.; Raghav, Dasarath; Santhosh Kiran, R.; Mahesh, Bhargav; Kumar, Krishna

2015-07-01

Uncertainty in availability of fossil fuels in the future and global warming increased the need for more environment friendly materials. In this work, an attempt is made to fabricate a hybrid polymer matrix composite. The blend is a mixture of General Purpose Resin and Cashew Nut Shell Liquid, a natural resin extracted from cashew plant. Palm fiber, which has high strength, is used as reinforcement material. The fiber is treated with alkali (NaOH) solution to increase its strength and adhesiveness. Parametric study of flexure strength is carried out by varying alkali concentration, duration of alkali treatment and fiber volume. Taguchi L9 Orthogonal array is followed in the design of experiments procedure for simplification. With the help of ANOVA technique, regression equations are obtained which gives the level of influence of each parameter on the flexure strength of the composite.

Effect of thermal tempering on strength and crack propagation behavior of feldspathic porcelains.

PubMed

Anusavice, K J; Hojjatie, B

1991-06-01

The objective of this study was to test the hypothesis that tempering stress can retard the growth of surface cracks in layered porcelain discs with variable levels of contraction mismatch. Porcelain discs, 16 mm in diameter and 2 mm thick, were prepared with a 0.5-mm-thick layer of opaque porcelain (O) and a 1.5-mm-thick layer of body porcelain (B). The materials were selected to produce contraction coefficient differences, alpha O-alpha B, of +3.2, +0.7, -0.9, and -1.5 ppm/degrees C. Body porcelain discs with a thickness of 2 mm were used as the thermally compatible control specimens (delta alpha = 0). The discs were fired to the maturing temperature of body porcelain (982 degrees C) and were then subjected to three cooling procedures: slow cooling (SC) in a furnace, fast cooling (FC) in air, and tempering (T) by blasting the surface of the body porcelain with compressed and dried air for 90 s. The dimensions of cracks induced by a Vickers microhardness indenter under a load of 4.9 N were measured at baseline and six months after indentation at 80 points along diametral lines within the surface of body porcelain. In addition, biaxial flexure tests were performed to determine the influence of mismatch and tempering on flexure strength. The results of ANOVA indicate that crack dimensions were influenced significantly by the interaction of cooling rate and contraction mismatch (p less than 0.0001).(ABSTRACT TRUNCATED AT 250 WORDS)

Synthesis, characterization and evaluation of a fluorinated resin monomer with low water sorption.

PubMed

Liu, Xue; Wang, Zengyao; Zhao, Chengji; Bu, Wenhuan; Zhang, Yurong; Na, Hui

2018-01-01

A fluorinated acrylate monomer (4-TF-PQEA) without BPA (bisphenol-A) structure was synthesized and mixed with triethylene glycol dimethacrylate (TEGDMA) to used as dental resin system in order to achieve lower water sorption and reduce human exposure to BPA derivatives. Double bond conversion (DC) was measured using Fourier transform infrared spectroscopy (FTIR). Water sorption (WS), water solution (WL) and depth of cure (DOC) were evaluated according to ISO 4049:2009. Water contact angle (CA) was measured using contact angle analyzer. Polymerization shrinkage (PS) was evaluated according to the Archimedes' principle and ISO 17304:2013. Flexural strength (FS) and flexural modulus (FM) were measured by three-point bending test with a universal testing machine according to ISO 4049:2009. Comprehensive strength (CS) and vickers microhardness (VM) were also investigated. Thermal stability test was measure by Thermogravimetric analyzer. Cytotoxicity of three resin systems was tested through MTT (3-(4,5-dimethylthiazol-2-yl)-2,5-diphenyltetrazoliumbromid) cytotoxicity method according to the ISO 10993-5:2009. Bisphenol-A glycidyl dimethacrylate (Bis-GMA)/ TEGDMA resin system was used as a control. The results show that 4-TF-PQEA/TEGDMA resin system had lower PS, lower WS and higher DC values than those of Bis-GMA/TEGDMA resin system except some mechanical properties, such as FS, FM and CS. Moreover, properties of other 4-TF-PQEA-containing resin systems were also comparable with those of Bis-GMA/TEGDMA resin system. In particular, the overall performance of resin system consisted of 4-TF-PQEA/Bis-GMA/TEGDMA is optimized when the mixture ratio is 30/40/30(wt/wt/wt). Therefore, the 4-TF-PQEA has potential to be used as resin monomer for dental resin composites to achieve lower water sorption. Copyright © 2017 Elsevier Ltd. All rights reserved.

Mechanical performance of porous concrete pavement containing nano black rice husk ash

NASA Astrophysics Data System (ADS)

Ibrahim, M. Y. Mohd; Ramadhansyah, P. J.; Rosli, H. Mohd; Ibrahim, M. H. Wan

2018-01-01

This paper presents an experimental research on the performance of nano black rice husk ash on the porous concrete pavement properties. The performance of the porous concrete pavement mixtures was investigated based on their compressive strength, flexural strength, and splitting tensile strength. The results indicated that using nano material from black rice husk ash improved the mechanical properties of porous concrete pavement. In addition, the result of compressive, flexural, and splitting tensile strength was increased with increasing in curing age. Finally, porous concrete pavement with 10% replacement levels exhibited an excellent performance with good strength compared to others.

The effect of air-abrasion and heat treatment on the fracture behavior of Y-TZP.

PubMed

Passos, Sheila P; Linke, Bernie; Major, Paul W; Nychka, John A

2015-09-01

This study evaluated how the flexural strength and fracture behavior of a zirconia-based ceramic (Y-TZP) were affected by pre- and post-sintering mechanical and thermal treatments. Treatments included sandblasting with different particle size and type (30μm SiO2; 50 and 110μm Al2O3) and thermal conditioning. Two hundred bar-shaped specimens of pre-sintered Y-TZP ceramic (Lava Frame, 3M) were prepared (specimen dimensions: 25mm length×4mm width×0.7mm thickness) and divided into three groups (before sintering, after sintering and after sintering with heating treatment). The before sintering group specimens were airborne-particle abraded prior to dense sintering. Specimens from the after sintering group were airborne-particle abraded after sintering. The after sintering with heating treatment group specimens were submitted to a heating procedure after airborne-particle abrasion. The controls were the specimens that were sintered and not treated with any conditioning procedures. The specimens from all experimental conditions were analyzed by SEM, CLSM and XRD. All specimens were tested in four-point bending. Data were statistically analyzed using one-way ANOVA and Post Hoc tests (α=0.05). A Weibull analysis was used to analyze the strength reliability. Sandblasting pre-sintered zirconia before sintering significantly decreased the flexural strength, except when the smallest blasting particles were used (30μm SiO2). Phase transformation (t-m) was observed after sandblasting and reverse transformation (m-t) was observed after heating. Sandblasting with 30μm SiO2 and 50μm Al2O3 allowed lower phase transformation. However, 30mm SiO2 presented better reliability. Copyright © 2015 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

WETTING AND REACTIVE AIR BRAZING OF BSCF FOR OXYGEN SEPARATION DEVICES

DOE Office of Scientific and Technical Information (OSTI.GOV)

LaDouceur, Richard M.; Meier, Alan; Joshi, Vineet V.

Reactive air brazes Ag-CuO and Ag-V2O5 were evaluated for brazing Ba0.5Sr0.5Co0.8Fe0.2O(3-δ) (BSCF). BSCF has been determined in previous work to have the highest potential mixed ionic/electronic conducting (MIEC) ceramic material based on the design and oxygen flux requirements of an oxy-fuel plant such as an integrated gasification combined cycle (IGCC) used to facilitate high-efficiency carbon capture. Apparent contact angles were observed for Ag-CuO and Ag-V2O5 mixtures at 1000 °C for isothermal hold times of 0, 10, 30, and 60 minutes. Wetting apparent contact angles (θ<90°) were obtained for 1%, 2%, and 5% Ag-CuO and Ag-V2O5 mixtures, with the apparent contactmore » angles between 74° and 78° for all compositions and furnace dwell times. Preliminary microstructural analysis indicates that two different interfacial reactions are occurring: Ag-CuO interfacial microstructures revealed the same dissolution of copper oxide into the BSCF matrix to form copper-cobalt-oxygen rich dissolution products along the BSCF grain boundaries and Ag-V2O5 interfacial microstructures revealed the infiltration and replacement of cobalt and iron with vanadium and silver filling pores in the BSCF microstructure. The Ag-V2O5 interfacial reaction product layer was measured to be significantly thinner than the Ag-CuO reaction product layer. Using a fully articulated four point flexural bend test fixture, the flexural fracture strength for BSCF was determined to be 95 ± 33 MPa. The fracture strength will be used to ascertain the success of the reactive air braze alloys. Based on these results, brazes were fabricated and mechanically tested to begin to optimize the brazing parameters for this system. Ag-2.5% CuO braze alloy with a 2.5 minute thermal cycle achieved a hermetic seal with a joint flexural strength of 34 ± 15 MPa and Ag-1% V2O5 with a 30 minute thermal cycle had a joint flexural strength of 20 ± 15 MPa.« less

Effect of fabric structure and polymer matrix on flexural strength, interlaminar shear stress, and energy dissipation of glass fiber-reinforced polymer composites

USDA-ARS?s Scientific Manuscript database

We report the effect of glass fiber structure and the epoxy polymer system on the flexural strength, interlaminar shear stress (ILSS), and energy absorption properties of glass fiber-reinforced polymer (GFRP) composites. Four different GFRP composites were fabricated from two glass fiber textiles of...

Thermal-mechanical properties of a graphitic-nanofibers reinforced epoxy.

PubMed

Salehi-Khojin, Amin; Jana, Soumen; Zhong, Wei-Hong

2007-03-01

We previously developed a series of reactive graphitic nanofibers (r-GNFs) reinforced epoxy (nano-epoxy) as composite matrices, which have shown good wetting and adhesion properties with continuous fiber. In this work, the thermal-mechanical properties of the nano-epoxy system containing EponTM Resin 828 and Epi-cure Curing Agent W were characterized. Results from three-point bending tests showed that the flexural strength and flexural modulus of this system with 0.30 wt% of reactive nanofibers were increased by 16%, and 21% respectively, over pure epoxy. Fracture toughness increased by ca. 40% for specimens with 0.50 wt% of r-GNFs. By dynamic mechanical analysis (DMA) test, specimens with 0.30 wt% of r-GNFs showed a significant increase in storage modulus E' (by ca. 122%) and loss modulus E" (by ca. 111%) with respect to that of pure epoxy. Also thermo-dilatometry analysis (TDA) was used to measure dimensional change of specimens as a function of temperature, and then, coefficients of thermal expansion (CTE) before and after glass transition temperature (Tg) were obtained. Results implied that nano-epoxy materials had good dimensional stability and reduced CTE values when compared to those of pure epoxy.

Rapid repair of severely earthquake-damaged bridge piers with flexural-shear failure mode

NASA Astrophysics Data System (ADS)

Sun, Zhiguo; Wang, Dongsheng; Du, Xiuli; Si, Bingjun

2011-12-01

An experimental study was conducted to investigate the feasibility of a proposed rapid repair technique for severely earthquake-damaged bridge piers with flexural-shear failure mode. Six circular pier specimens were first tested to severe damage in flexural-shear mode and repaired using early-strength concrete with high-fluidity and carbon fiber reinforced polymers (CFRP). After about four days, the repaired specimens were tested to failure again. The seismic behavior of the repaired specimens was evaluated and compared to the original specimens. Test results indicate that the proposed repair technique is highly effective. Both shear strength and lateral displacement of the repaired piers increased when compared to the original specimens, and the failure mechanism of the piers shifted from flexural-shear failure to ductile flexural failure. Finally, a simple design model based on the Seible formulation for post-earthquake repair design was compared to the experimental results. It is concluded that the design equation for bridge pier strengthening before an earthquake could be applicable to seismic repairs after an earthquake if the shear strength contribution of the spiral bars in the repaired piers is disregarded and 1.5 times more FRP sheets is provided.

Correlation between strength properties in standard test specimens and molded phenolic parts

NASA Technical Reports Server (NTRS)

Turner, P S; Thomason, R H

1946-01-01

This report describes an investigation of the tensile, flexural, and impact properties of 10 selected types of phenolic molding materials. The materials were studied to see in what ways and to what extent their properties satisfy some assumptions on which the theory of strength of materials is based: namely, (a) isotropy, (b) linear stress-strain relationship for small strains, and (c) homogeneity. The effect of changing the dimensions of tensile and flexural specimens and the span-depth ratio in flexural tests were studied. The strengths of molded boxes and flexural specimens cut from the boxes were compared with results of tests on standard test specimens molded from the respective materials. The nonuniformity of a material, which is indicated by the coefficient of variation, affects the results of tests made with specimens of different sizes and tests with different methods of loading. The strength values were found to depend on the relationship between size and shape of the molded specimen and size and shape of the fillers. The most significant variations observed within a diversified group of materials were found to depend on the orientation of fibrous fillers. Of secondary importance was the dependence of the variability of test results on the pieces of filler incorporated into the molding powder as well as on the size of the piece. Static breaking strength tests on boxes molded from six representative phenolic materials correlated well with falling-ball impact tests on specimens cut from molded flat sheets. Good correlation was obtained with Izod impact tests on standard test specimens prepared from the molding materials. The static breaking strengths of the boxes do not correlate with the results of tensile or flexural tests on standard specimens.

Strength measurement of optical fibers by bending

NASA Astrophysics Data System (ADS)

Srubshchik, Leonid S.

1999-01-01

A two-point bending technique has been used not only to measure the breaking stress of optical fiber but also to predict its static and dynamic fatigue. The present theory of this test is based on elastica theory of rod. However, within the limits of elastica theory the tensile and shear stresses cannot be determined. In this paper we study dynamic and static problems for optical fiber in the two- point bending test on the base of geometrically exact theory in which rod can suffer flexure, extension, and shear. We obtain the governing partial differential equations taking into account the fact that the lateral motion of the fiber is restrained by the presence of flat parallel plates. We develop the computational methods for solving the initial and equilibrium free-boundary nonlinear planar problems. We derive the formulas for predicting of the tensile strength from strength in the bending and calculate one example.

Antifungal, optical, and mechanical properties of polymethylmethacrylate material incorporated with silanized zinc oxide nanoparticles.

PubMed

Kamonkhantikul, Krid; Arksornnukit, Mansuang; Takahashi, Hidekazu

2017-01-01

Fungal infected denture, which is typically composed of polymethylmethacrylate (PMMA), is a common problem for a denture wearer, especially an elderly patient with limited manual dexterity. Therefore, increasing the antifungal effect of denture by incorporating surface modification nanoparticles into the PMMA, while retaining its mechanical properties, is of interest. This study aimed to evaluate antifungal, optical, and mechanical properties of heat-cured PMMA incorporated with different amounts of zinc oxide nanoparticles (ZnOnps) with or without methacryloxypropyltrimethoxysilane modification. Specimens made from heat-cured PMMA containing 1.25, 2.5, and 5% (w/w) nonsilanized (Nosi) or silanized (Si) ZnOnps were evaluated. Specimens without filler served as control. The fungal assay was performed placing a Candida albicans suspension on the PMMA surface for 2 h, then Sabouraud Dextrose Broth was added, and growth after 24 h was determined by counting colony forming units on agar plates. A spectrophotometer was used to measure the color in L* (brightness), a* (red-green), b* (yellow-blue) and opacity of the experimental groups. Flexural strength and flexural modulus were determined using a three-point bending test on universal testing machine after 37°C water storage for 48 h and 1 month. The antifungal, optical, and mechanical properties of the PMMA incorporated with ZnOnps changed depending on the amount. With the same amount of ZnOnps, the silanized groups demonstrated a greater reduction in C. albicans compared with the Nosi groups. The color difference (ΔE) and opacity of the Nosi groups were greater compared with the Si groups. The flexural strength of the Si groups, except for the 1.25% group, was significantly greater compared with the Nosi groups. PMMA incorporated with Si ZnOnps, particularly with 2.5% Si ZnOnps, had a greater antifungal effect, less color differences, and opacity compared with Nosi ZnOnps, while retaining its mechanical properties.

Comparative study of mechanical properties of direct core build-up materials

PubMed Central

Kumar, Girish; Shivrayan, Amit

2015-01-01

Background and Objectives: The strength greatly influences the selection of core material because core must withstand forces due to mastication and para-function for many years. This study was conducted to evaluate certain mechanical properties of commonly used materials for direct core build-up, including visible light cured composite, polyacid modified composite, resin modified glass ionomer, high copper amalgam, and silver cermet cement. Materials and Methods: All the materials were manipulated according to the manufacturer's recommendations and standard test specimens were prepared. A universal testing machine at different cross-head speed was used to determine all the four mechanical properties. Mean compressive strength, diametral tensile strength, flexural strength, and elastic modulus with standard deviations were calculated. Multiple comparisons of the materials were also done. Results: Considerable differences in compressive strength, diametral tensile strength, and flexural strength were observed. Visible light cured composite showed relatively high compressive strength, diametral tensile strength, and flexural strength compared with the other tested materials. Amalgam showed the highest value for elastic modulus. Silver cermet showed less value for all the properties except for elastic modulus. Conclusions: Strength is one of the most important criteria for selection of a core material. Stronger materials better resist deformation and fracture provide more equitable stress distribution, greater stability, and greater probability of clinical success. PMID:25684905

Compressive, diametral tensile and biaxial flexural strength of cutting-edge calcium phosphate cements.

PubMed

Luo, Jun; Ajaxon, Ingrid; Ginebra, Maria Pau; Engqvist, Håkan; Persson, Cecilia

2016-07-01

Calcium phosphate cements (CPCs) are widely used in bone repair. Currently there are two main types of CPCs, brushite and apatite. The aim of this project was to evaluate the mechanical properties of particularly promising experimental brushite and apatite formulations in comparison to commercially available brushite- and apatite-based cements (chronOS(™) Inject and Norian(®) SRS(®), respectively), and in particular evaluate the diametral tensile strength and biaxial flexural strength of these cements in both wet and dry conditions for the first time. The cements׳ porosity and their compressive, diametral tensile and biaxial flexural strength were tested in wet (or moist) and dry conditions. The surface morphology was characterized by scanning electron microscopy. Phase composition was assessed with X-ray diffraction. It was found that the novel experimental cements showed better mechanical properties than the commercially available cements, in all loading scenarios. The highest compressive strength (57.2±6.5MPa before drying and 69.5±6.0MPa after drying) was found for the experimental brushite cement. This cement also showed the highest wet diametral tensile strength (10.0±0.8MPa) and wet biaxial flexural strength (30.7±1.8MPa). It was also the cement that presented the lowest porosity (approx. 12%). The influence of water content was found to depend on cement type, with some cements showing higher mechanical properties after drying and some no difference after drying. Copyright © 2016 The Authors. Published by Elsevier Ltd.. All rights reserved.

Effect of amorphous silica ash used as a partial replacement for cement on the compressive and flexural strengths cement mortar.

NASA Astrophysics Data System (ADS)

Usman, Aliyu; Ibrahim, Muhammad B.; Bala, Nura

2018-04-01

This research is aimed at investigating the effect of using amorphous silica ash (ASA) obtained from rice husk as a partial replacement of ordinary Portland cement (OPC) on the compressive and flexural strength of mortar. ASA was used in partial replacement of ordinary Portland cement in the following percentages 2.5 percent, 5 percent, 7.5 percent and 10 percent. These partial replacements were used to produce Cement-ASA mortar. ASA was found to contain all major chemical compounds found in cement with the exception of alumina, which are SiO2 (91.5%), CaO (2.84%), Fe2O3 (1.96%), and loss on ignition (LOI) was found to be 9.18%. It also contains other minor oxides found in cement. The test on hardened mortar were destructive in nature which include flexural strength test on prismatic beam (40mm x 40mm x 160mm) and compressive strength test on the cube size (40mm x 40mm, by using the auxiliary steel plates) at 2,7,14 and 28 days curing. The Cement-ASA mortar flexural and compressive strengths were found to be increasing with curing time and decreases with cement replacement by ASA. It was observed that 5 percent replacement of cement with ASA attained the highest strength for all the curing ages and all the percentage replacements attained the targeted compressive strength of 6N/mm2 for 28 days for the cement mortar

Thermal and mechanical behaviour of sub micron sized fly ash reinforced polyester resin composite

NASA Astrophysics Data System (ADS)

Nantha Kumar, P.; Rajadurai, A.; Muthuramalingam, T.

2018-04-01

The utilization of particles reinforced resin matrix composites is being increased owing to its lower density and high strength to weight ratio. In the present study, an attempt has been made to synthesize fly ash particles reinforced polyester resin composite for engine cowling application. The thermal stability and mechanical behaviours such as hardness and flexural strength of the composite with 2, 3 and 4 weight % of reinforcement is studied and analyzed. The thermo gravimetric analysis indicates that the higher addition of reinforcement increases the decomposition temperature due to its refractory nature. It is also observed that the hardness increases with higher filler addition owing to the resistance of FA particles towards penetration. The flexural strength is found to increase up to the addition of 3% of FA particles, whereas the polyester resin composite prepared with 4% FA particles addition is observed to have low flexural strength owing to agglomeration of particles.

Zirconia changes after grinding and regeneration firing.

PubMed

Hatanaka, Gabriel R; Polli, Gabriela S; Fais, Laiza M G; Reis, José Maurício Dos S N; Pinelli, Lígia A P

2017-07-01

Despite improvements in computer-aided design and computer-aided manufacturing (CAD-CAM) systems, grinding during either laboratory procedures or clinical adjustments is often needed to modify the shape of 3 mol(%) yttria-tetragonal zirconia polycrystal (3Y-TZP) restorations. However, the best way to achieve adjustment is unclear. The purpose of this in vitro study was to evaluate the microstructural and crystallographic phase changes, flexural strength, and Weibull modulus of a 3Y-TZP zirconia after grinding with or without water cooling and regeneration firing. Ninety-six bar-shaped specimens were obtained and divided as follows: as-sintered, control; as-sintered with regeneration firing; grinding without water cooling; grinding and regeneration firing with water cooling; and grinding and regeneration firing. Grinding (0.3 mm) was performed with a 150-μm diamond rotary instrument in a high-speed handpiece. For regeneration firing, the specimens were annealed at 1000°C for 30 minutes. The crystalline phases were evaluated by using x-ray powder diffraction. A 4-point bending test was conducted (10 kN; 0.5 mm/min). The Weibull modulus was used to analyze strength reliability. The microstructure was analyzed by scanning electron microscopy. Data from the flexural strength test were evaluated using the Kruskal-Wallis and Dunn tests (α=.05). Tetragonal-to-monoclinic phase transformation was identified in the ground specimens; R regeneration firing groups showed only the tetragonal phase. The median flexural strength of as-sintered specimens was 642.0; 699.3 MPa for as-sintered specimens with regeneration firing; 770.1 MPa for grinding and water-cooled specimens; 727.3 MPa for specimens produced using water-cooled grinding and regeneration firing; 859.9 MPa for those produced by grinding; and 764.6 for those produced by grinding and regeneration firing; with statistically higher values for the ground groups. The regenerative firing did not affect the flexural strength. Weibull modulus values ranged from 5.3 to 12.4. The SEM images showed semicircular cracks after grinding. Adjustments by grinding in 3Y-TZP frameworks should be performed with water cooling, and regeneration firing should be undertaken to obtain a more reliable material. Copyright © 2016 Editorial Council for the Journal of Prosthetic Dentistry. Published by Elsevier Inc. All rights reserved.

Generalized Reliability Methodology Applied to Brittle Anisotropic Single Crystals. Degree awarded by Washington Univ., 1999

NASA Technical Reports Server (NTRS)

Salem, Jonathan A.

2002-01-01

A generalized reliability model was developed for use in the design of structural components made from brittle, homogeneous anisotropic materials such as single crystals. The model is based on the Weibull distribution and incorporates a variable strength distribution and any equivalent stress failure criteria. In addition to the reliability model, an energy based failure criterion for elastically anisotropic materials was formulated. The model is different from typical Weibull-based models in that it accounts for strength anisotropy arising from fracture toughness anisotropy and thereby allows for strength and reliability predictions of brittle, anisotropic single crystals subjected to multiaxial stresses. The model is also applicable to elastically isotropic materials exhibiting strength anisotropy due to an anisotropic distribution of flaws. In order to develop and experimentally verify the model, the uniaxial and biaxial strengths of a single crystal nickel aluminide were measured. The uniaxial strengths of the <100> and <110> crystal directions were measured in three and four-point flexure. The biaxial strength was measured by subjecting <100> plates to a uniform pressure in a test apparatus that was developed and experimentally verified. The biaxial strengths of the single crystal plates were estimated by extending and verifying the displacement solution for a circular, anisotropic plate to the case of a variable radius and thickness. The best correlation between the experimental strength data and the model predictions occurred when an anisotropic stress analysis was combined with the normal stress criterion and the strength parameters associated with the <110> crystal direction.

Green Composites Based on Blends of Polypropylene with Liquid Wood Reinforced with Hemp Fibers: Thermomechanical Properties and the Effect of Recycling Cycles.

PubMed

Cicala, Gianluca; Tosto, Claudio; Latteri, Alberta; La Rosa, Angela Daniela; Blanco, Ignazio; Elsabbagh, Ahmed; Russo, Pietro; Ziegmann, Gerhard

2017-08-26

Green composites from polypropylene and lignin-based natural material were manufactured using a melt extrusion process. The lignin-based material used was the so called "liquid wood". The PP/"Liquid Wood" blends were extruded with "liquid wood" content varying from 20 wt % to 80 wt %. The blends were thoroughly characterized by flexural, impact, and dynamic mechanical testing. The addition of the Liquid Wood resulted in a great improvement in terms of both the flexural modulus and strength but, on the other hand, a reduction of the impact strength was observed. For one blend composition, the composites reinforced with hemp fibers were also studied. The addition of hemp allowed us to further improve the mechanical properties. The composite with 20 wt % of hemp, subjected to up to three recycling cycles, showed good mechanical property retention and thermal stability after recycling.

Green Composites Based on Blends of Polypropylene with Liquid Wood Reinforced with Hemp Fibers: Thermomechanical Properties and the Effect of Recycling Cycles

PubMed Central

Latteri, Alberta; La Rosa, Angela Daniela; Elsabbagh, Ahmed; Ziegmann, Gerhard

2017-01-01

Green composites from polypropylene and lignin-based natural material were manufactured using a melt extrusion process. The lignin-based material used was the so called “liquid wood”. The PP/“Liquid Wood” blends were extruded with “liquid wood” content varying from 20 wt % to 80 wt %. The blends were thoroughly characterized by flexural, impact, and dynamic mechanical testing. The addition of the Liquid Wood resulted in a great improvement in terms of both the flexural modulus and strength but, on the other hand, a reduction of the impact strength was observed. For one blend composition, the composites reinforced with hemp fibers were also studied. The addition of hemp allowed us to further improve the mechanical properties. The composite with 20 wt % of hemp, subjected to up to three recycling cycles, showed good mechanical property retention and thermal stability after recycling. PMID:28846607

ABA and ABC type thermoplastic elastomer toughening of epoxy matrices and its effect on carbon fiber reinforced composites

NASA Astrophysics Data System (ADS)

Pitchiaya, Gomatheeshwar

Epoxy-matrices have high modulus, strength, excellent creep resistance, but lacks ductility. One approach to improve the mechanical toughness is the addition of thermoplastic elastomers (TPEs). The TPEs investigated here are triblock copolymers of styrene-butadiene-methyl methacrylate (SBM) and methylmethacrylate-butylacrylate-methylmethacrylate (MAM) of the ABC and ABA type, respectively. The effect of concentration (1-12.5 wt %) of these TPEs on a diglycidyl ether of bisphenol-A (DGEBA) epoxy cured with metaphenylenediamine (mPDA), has been investigated. The TPE-DGEBA epoxies were characterized by TGA, DMA, SEM and impact. The flexural modulus, flexural strength and thermal resistance remained unaffected up to 5 wt% loading of TPEs, and exhibited less than 10% decrease at higher weight percent. T g was unaffected for all concentrations. Fracture toughness was improved 250% and up to 375% (when non- stoichiometric amount of curing agent was used) with TPE addition to epoxy/mPDA matrix. A SBM(1phr)EPON system was chosen to be the matrix of choice for a fiber reinforced composite system with a 4wt% aromatic epoxy sizing on a AS4 (UV-treated) carbon fiber. The 0° and 90° flexural modulus and strength of a SBM modified system was compared with the neat and their fracture surfaces were analyzed. A 89% increase in flexural strength was observed in a 90° flexural test for the modified system when compared with the neat. Novel sizing agents were also developed to enhance interfacial shear strength (IFSS) and the fiber-matrix adhesion and their birefringence pattern were analyzed.

Environmentally-Friendly Dense and Porous Geopolymers Using Fly Ash and Rice Husk Ash as Raw Materials

PubMed Central

Ziegler, Daniele; Formia, Alessandra; Tulliani, Jean-Marc; Palmero, Paola

2016-01-01

This paper assesses the feasibility of two industrial wastes, fly ash (FA) and rice husk ash (RHA), as raw materials for the production of geopolymeric pastes. Three typologies of samples were thus produced: (i) halloysite activated with potassium hydroxide and nanosilica, used as the reference sample (HL-S); (ii) halloysite activated with rice husk ash dissolved into KOH solution (HL-R); (iii) FA activated with the alkaline solution realized with the rice husk ash (FA-R). Dense and porous samples were produced and characterized in terms of mechanical properties and environmental impact. The flexural and compressive strength of HL-R reached about 9 and 43 MPa, respectively. On the contrary, the compressive strength of FA-R is significantly lower than the HL-R one, in spite of a comparable flexural strength being reached. However, when porous samples are concerned, FA-R shows comparable or even higher strength than HL-R. Thus, the current results show that RHA is a valuable alternative to silica nanopowder to prepare the activator solution, to be used either with calcined clay and fly ash feedstock materials. Finally, a preliminary evaluation of the global warming potential (GWP) was performed for the three investigated formulations. With the mix containing FA and RHA-based silica solution, a reduction of about 90% of GWP was achieved with respect to the values obtained for the reference formulation. PMID:28773587

Flexural strength of pure Ti, Ni-Cr and Co-Cr alloys submitted to Nd:YAG laser or TIG welding.

PubMed

Rocha, Rick; Pinheiro, Antônio Luiz Barbosa; Villaverde, Antonio Balbin

2006-01-01

Welding of metals and alloys is important to Dentistry for fabrication of dental prostheses. Several methods of soldering metals and alloys are currently used. The purpose of this study was to assess, using the flexural strength testing, the efficacy of two processes Nd:YAG laser and TIG (tungsten inert gas) for welding of pure Ti, Co-Cr and Ni-Cr alloys. Sixty cylindrical specimens were prepared (20 of each material), bisected and welded using different techniques. Four groups were formed (n=15). I: Nd:YAG laser welding; II- Nd:YAG laser welding using a filling material; III- TIG welding and IV (control): no welding (intact specimens). The specimens were tested in flexural strength and the results were analyzed statistically by one-way ANOVA. There was significant differences (p<0.001) among the non-welded materials, the Co-Cr alloy being the most resistant to deflection. Comparing the welding processes, significant differences (p<0.001) where found between TIG and laser welding and also between laser alone and laser plus filling material. In conclusion, TIG welding yielded higher flexural strength means than Nd:YAG laser welding for the tested Ti, Co-Cr and Ni-Cr alloys.

An Experimental Study on Strengthening of Reinforced Concrete Flexural Members using Steel Wire Mesh

NASA Astrophysics Data System (ADS)

Al Saadi, Hamza Salim Mohammed; Mohandas, Hoby P.; Namasivayam, Aravind

2017-01-01

One of the major challenges and contemporary research in the field of structural engineering is strengthening of existing structural elements using readily available materials in the market. Several investigations were conducted on strengthening of various structural components using traditional and advanced materials. Many researchers tried to enhance the reinforced concrete (RC) beams strength using steel plate, Glass and Carbon Fibre Reinforced Polymers (GFRP & CFRP). For the reason that high weight to the strength ratio and compatibility in strength between FRP composites and steel bars, steel plates and GFRP and CFRP composites are not used for strengthening works practically. Hence, in this present work the suitability of using wire mesh for the purpose of strengthening the RC flexural members is studied by conducting experimental works. New technique of strengthening system using wire mesh with a view to improve sectional properties and subsequently flexural strength of RC beams is adopted in this work. The results for experimental and theoretical analysis were compared and found that good correlation exists between them. The experimental results indicate that RC beams strengthened with steel wire mesh are easy technique for strengthening of existing flexural members.

The optimum content of rubber ash in concrete: flexural strength

NASA Astrophysics Data System (ADS)

Senin, M. S.; Shahidan, S.; Shamsuddin, S. M.; Ariffin, S. F. A.; Othman, N. H.; Rahman, R.; Khalid, F. S.; Nazri, F. M.

2017-11-01

Discarded scrap tyres have become one of the major environmental problems nowadays. Several studies have been carried out to reuse waste tires as an additive or sand replacement in concrete with appropriate percentages of tire rubber, called as rubberized concrete to solve this problem. The main objectives of this study are to investigate the flexural strength performance of concrete when adding the rubber ash and also to analyse the optimum content of rubber ash in concrete prisms. The performance total of 30 number of concrete prisms in size of 100mm x 100mm x 500 mm were investigated, by partially replacement of rubber ash with percentage of 0%, 3%, 5%, 7% and 9% from the volume of the sand. The flexural strength is increased when percentage of rubber ash is added 3% from control concrete prism, RA 0 for both concrete prism age, 7 days and 28 days with value 1.21% and 0.976% respectively. However, for RA 5, RA 7 and RA 9, the flexural strength was decreased compared to the control for both age, 7 days and 28 days. In conclusion, 3% is the optimum content of rubber ash in concrete prism for both concrete age

PMR polyimide/graphite fiber composite fan blades

NASA Technical Reports Server (NTRS)

Cavano, P. J.; Winters, W. E.

1976-01-01

Ultrahigh speed fan blades, designed in accordance with the requirements of an ultrahigh tip speed blade axial flow compressor, were fabricated from a high strength graphite fiber tow and a PMR polyimide resin. The PMR matrix was prepared by combining three monomeric reactants in methyl alcohol, and the solution was applied directly to the reinforcing fiber for subsequent in situ polymerization. Some of the molded blades were completely finished by secondary bonding of root pressure pads and an electroformed nickel leading edge sheath prior to final machining. The results of the spin testing of nine PMR fan blades are given. Prior to blade fabrication, heat resin tensile properties of the PMR resin were examined at four formulated molecular weight levels. Additionally, three formulated molecular weight levels were investigated in composite form with both a high modulus and a high strength fiber, both as-molded and postcured, in room temperature and 232 C transverse tensile, flexure and short beam shear. Mixed fiber orientation panels simulating potential blade constructions were also evaluated. Flexure tests, short beam shear tests, and tensile tests were conducted on these angle-plied laminates.

The effect of veneering and heat treatment on the flexural strength of Empress 2 ceramics.

PubMed

Cattell, M J; Palumbo, R P; Knowles, J C; Clarke, R L; Samarawickrama, D Y D

2002-05-01

The aims of the study were to test and compare the biaxial flexural strength and reliability of Empress 2 ceramics after heat treatment and the addition of the veneering material and to characterise their microstructures. Forty disc specimens (2 x 14 mm) and forty disc specimens (1 x 14 mm) were produced by heat pressing in the EP 500 press furnace. Group 1 (2 x 14 mm Empress 2 core) was as heat pressed and group 2 (2 x 14 mm Empress 2 core) was subjected to the recommended firing cycles. Groups 3 and 4 (1 x 14 mm Empress 2 core) were veneered with the dentine material and heat-treated as per group 2. Groups 1, 2 and 3 were lapped to 800 grit silicon carbide paper on the compressive surface only and group 4 on both the compressive and tensile test surfaces. Twenty disc specimens per group were tested using the biaxial flexure test at a crosshead speed of 0.15 mm/min. Specimens were characterised using X-ray diffraction (XRD) and secondary electron imaging (SEM). Mean biaxial flexural strengths (MPa+/-SD) were group 1: 265.5+/-25.7; group 2: 251.3+/-30.2; group 3: 258.6+/-21.4 and group 4: 308.6+/-37.7. There was no statistical difference between groups 1, 2 and 3 (p>0.05), but differences for group 4 (p<0.05). XRD and SEM revealed lithium disilicate and lithium orthophosphate in the Empress 2 core material and an amorphous glass and some evidence of a crystalline phase in the dentine material. CONCLUSIONS; Veneering or heat treatment of Empress 2 ceramics did not significantly affect the mean biaxial flexural strength (p>0.05) or reliability. Surface modification of the Empress 2 core material increased the mean biaxial flexural strength (p<0.05).

Strength, Fracture Toughness, and Slow Crack Growth of Zirconia/alumina Composites at Elevated Temperature

NASA Technical Reports Server (NTRS)

Choi, Sung R.; Bansal, Narottam P.

2003-01-01

Various electrolyte materials for solid oxide fuel cells were fabricated by hot pressing 10 mol% yttria-stabilized zirconia (10-YSZ) reinforced with two different forms of alumina particulates and platelets each containing 0 to 30 mol% alumina. Flexure strength and fracture toughness of platelet composites were determined as a function of alumina content at 1000 C in air and compared with those of particulate composites determined previously. In general, elevated-temperature strength and fracture toughness of both composite systems increased with increasing alumina content. For a given alumina content, flexure strength of particulate composites was greater than that of platelet composites at higher alumina contents (greater than or equal to 20 mol%), whereas, fracture toughness was greater in platelet composites than in particulate composites, regardless of alumina content. The results of slow crack growth (SCG) testing, determined at 1000 C via dynamic fatigue testing for three different composites including 0 mol% (10-YSZ matrix), 30 mol % particulate and 30 mol% platelet composites, showed that susceptibility to SCG was greatest with SCG parameter n = 6 to 8 for both 0 and 30 mol% particulate composites and was least with n = 33 for the 30 mol% platelet composite.

The impact of hydrofluoric acid etching followed by unfilled resin on the biaxial strength of a glass-ceramic.

PubMed

Posritong, Sumana; Borges, Alexandre Luiz Souto; Chu, Tien-Min Gabriel; Eckert, George J; Bottino, Marco A; Bottino, Marco C

2013-11-01

To evaluate the null hypotheses that hydrofluoric (HF) acid etching time would neither decrease the biaxial flexural strength of a glass-based veneering ceramic nor enhance it after silane and unfilled resin (UR) applications. Disc-shaped IPS e.max ZirPress specimens were allocated into 12 groups: G1-control (no-etching), G2-30 s, G3-60 s, G4-90 s, G5-120 s, G6-60 s+60 s. Groups (G7-G12) were treated in the same fashion as G1-G6, but followed by silane and UR applications. Surface morphology and roughness (Ra and Rq) of the ceramics were assessed by means of scanning electron microscopy (SEM) and profilometry, respectively. Flexural strength was determined by biaxial testing. Data were analyzed by two-way ANOVA and the Sidak test (α=0.05). Weibull statistics were estimated and finite element analysis (FEA) was carried out to verify the stress concentration end areas of fracture. The interaction (etching time vs. surface treatment) was significant for Ra (p=0.008) and Rq (0.0075). Resin-treated groups presented significantly lower Ra and Rq than non-treated groups, except for the 60s group (p<0.005). SEM revealed that etching affected the ceramic microstructure and that the UR was able to penetrate into the irregularities. A significant effect of etching time (p=0.029) on flexural strength was seen. G7-G12 presented higher strength than G1-G6 (p<0.0001). None of experimental groups failed to show 95% confidence intervals of σ0 and m overlapped. FEA showed lower stress concentration after resin treatment. HF acid etching time did not show a damaging effect on the ceramic flexural strength. Moreover, the flexural strength could be enhanced after UR treatment. Copyright © 2013 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Surface orientation effects on bending properties of surgical mesh are independent of tensile properties.

PubMed

Simon, David D; Andrews, Sharon M; Robinson-Zeigler, Rebecca; Valdes, Thelma; Woods, Terry O

2018-02-01

Current mechanical testing of surgical mesh focuses primarily on tensile properties even though implanted devices are not subjected to pure tensile loads. Our objective was to determine the flexural (bending) properties of surgical mesh and determine if they correlate with mesh tensile properties. The flexural rigidity values of 11 different surgical mesh designs were determined along three textile directions (machine, cross-machine, and 45° to machine; n = 5 for each) using ASTM D1388-14 while tracking surface orientation. Tensile testing was also performed on the same specimens using ASTM D882-12. Linear regressions were performed to compare mesh flexural rigidity to mesh thickness, areal mass density, filament diameter, ultimate tensile strength, and maximum extension. Of 33 mesh specimen groups, 30 had significant differences in flexural rigidity values when comparing surface orientations (top and bottom). Flexural rigidity and mesh tensile properties also varied with textile direction (machine and cross-machine). There was no strong correlation between the flexural and tensile properties, with mesh thickness having the best overall correlation with flexural rigidity. Currently, surface orientation is not indicated on marketed surgical mesh, and a single mesh may behave differently depending on the direction of loading. The lack of correlation between flexural stiffness and tensile properties indicates the need to examine mesh bending stiffness to provide a more comprehensive understanding of surgical mesh mechanical behaviors. Further investigation is needed to determine if these flexural properties result in the surgical mesh behaving mechanically different depending on implantation direction. © 2017 Wiley Periodicals, Inc. J Biomed Mater Res Part B: Appl Biomater, 106B: 854-862, 2018. © 2017 Wiley Periodicals, Inc.

Depth of cure, flexural properties and volumetric shrinkage of low and high viscosity bulk-fill giomers and resin composites.

PubMed

Tsujimoto, Akimasa; Barkmeier, Wayne W; Takamizawa, Toshiki; Latta, Mark A; Miyazaki, Masashi

2017-03-31

The purpose of this study was to investigate the depth of cure, flexural properties and volumetric shrinkage of low and high viscosity bulk-fill giomers and resin composites. Depth of cure and flexural properties were determined according to ISO 4049, and volumetric shrinkage was measured using a dilatometer. The depths of cure of giomers were significantly lower than those of resin composites, regardless of photo polymerization times. No difference in flexural strength and modulus was found among either high or low viscosity bulk fill materials. Volumetric shrinkage of low and high viscosity bulk-fill resin composites was significantly less than low and high viscosity giomers. Depth of cure of both low and high viscosity bulk-fill materials is time dependent. Flexural strength and modulus of high viscosity or low viscosity bulk-fill giomer or resin composite materials are not different for their respective category. Resin composites exhibited less polymerization shrinkage than giomers.

Concretes and mortars with waste paper industry: Biomass ash and dregs.

PubMed

Martínez-Lage, Isabel; Velay-Lizancos, Miriam; Vázquez-Burgo, Pablo; Rivas-Fernández, Marcos; Vázquez-Herrero, Cristina; Ramírez-Rodríguez, Antonio; Martín-Cano, Miguel

2016-10-01

This article describes a study on the viability of using waste from the paper industry: biomass boiler ash and green liquor dregs to fabricate mortars and concretes. Both types of ash were characterized by obtaining their chemical and mineralogical composition, their organic matter content, granulometry, adsorption and other common tests for construction materials. Seven different mortars were fabricated, one for reference made up of cement, sand, and water, three in which 10, 20, or 30% of the cement was replaced by biomass ash, and three others in which 10, 20, or 30% of the cement was replaced with dregs. Test specimens were fabricated with these mortars to conduct flexural and compression tests. Flexural strength is reduced for all the mortars studied. Compressive strength increases for the mortars fabricated with biomass ash and decreases for the mortar with dregs. Finally, 5 concretes were made, one of them as a reference (neither biomass ash nor dregs added), two of them with replacements of 10 and 20% of biomass ash instead of cement and another two with replacements of 10 and 20% of dregs instead of cement. The compressive and tensile splitting strength increase when a 10% of ash is replaced and decrease in all the other cases. The modulus of elasticity always decreases. Copyright © 2016 Elsevier Ltd. All rights reserved.

Influence of Interleaved Films on the Mechanical Properties of Carbon Fiber Fabric/Polypropylene Thermoplastic Composites

PubMed Central

Kim, Jong Won; Lee, Joon Seok

2016-01-01

A laminated composite was produced using a thermoplastic prepreg by inserting an interleaved film with the same type of matrix as the prepreg during the lay-up process to improve the low interlaminar properties, which is a known weakness of laminated composites. Carbon fiber fabric (CFF) and polypropylene (PP) were used to manufacture the thermoplastic prepregs. Eight prepregs were used to produce the laminated composites. Interleaved films with different thicknesses were inserted into each prepreg. The physical properties of the composite, such as thickness, density, fiber volume fraction (Vf), and void content (Vc), were examined. The tensile strength, flexural strength, interlaminar shear strength (ILSS), impact property, and scanning electron microscopy (SEM) were used to characterize the mechanical properties. Compared to the composite without any inserted interleaved film, as the thickness of the inserted interleaved resin film was increased, Vc decreased by 51.45%. At the same time, however, the tensile strength decreased by 8.75%. Flexural strength increased by 3.79% and flexural modulus decreased by 15.02%. Interlaminar shear strength increased by 11.05% and impact strength increased by 15.38%. Fracture toughness of the laminated composite was improved due to insertion of interleaved film. PMID:28773467

Kenaf/PP and EFB/PP: Effect of fibre loading on the mechanical properties of polypropylene composites

NASA Astrophysics Data System (ADS)

Anuar, N. I. S.; Zakaria, S.; Harun, J.; Wang, C.

2017-07-01

Kenaf and empty fruit bunch (EFB) fibre which are the important natural fibres in Malaysia were studied as nonwoven polymer composites. The effect of fibre loading on kenaf polypropylene and EFB polypropylene nonwoven composite was studied at different mixture ratio. Kenaf polypropylene nonwoven composite (KPNC) and EFB polypropylene nonwoven composite (EPNC) were prepared by carding and needle-punching techniques, followed by a compression moulding at 6 mm thickness. This study was conducted to identify the optimum fibre loading of nonwoven polypropylene composite and their effect on the mechanical strength. The study was designed at 40%, 50%, 60% and 70% of fibre content in nonwoven mat and composite. The tensile strength, flexural strength and compression strength were tested to evaluate the composite mechanical properties. It was found that the mechanical properties for both kenaf and EFB nonwoven composites were influenced by the fibre content. KPNC showed higher mechanical strength than EPNC. The highest flexural strength was obtained at 60% KPNC and the lowest value was showed by 40% EPNC. The tensile and flexural strength for both KPNC and EPNC decreased after the fibre loading of 60%.

Influence of Interleaved Films on the Mechanical Properties of Carbon Fiber Fabric/Polypropylene Thermoplastic Composites.

PubMed

Kim, Jong Won; Lee, Joon Seok

2016-05-06

A laminated composite was produced using a thermoplastic prepreg by inserting an interleaved film with the same type of matrix as the prepreg during the lay-up process to improve the low interlaminar properties, which is a known weakness of laminated composites. Carbon fiber fabric (CFF) and polypropylene (PP) were used to manufacture the thermoplastic prepregs. Eight prepregs were used to produce the laminated composites. Interleaved films with different thicknesses were inserted into each prepreg. The physical properties of the composite, such as thickness, density, fiber volume fraction ( V f ), and void content ( V c ), were examined. The tensile strength, flexural strength, interlaminar shear strength (ILSS), impact property, and scanning electron microscopy (SEM) were used to characterize the mechanical properties. Compared to the composite without any inserted interleaved film, as the thickness of the inserted interleaved resin film was increased, V c decreased by 51.45%. At the same time, however, the tensile strength decreased by 8.75%. Flexural strength increased by 3.79% and flexural modulus decreased by 15.02%. Interlaminar shear strength increased by 11.05% and impact strength increased by 15.38%. Fracture toughness of the laminated composite was improved due to insertion of interleaved film.

Laboratory mechanical parameters of composite resins and their relation to fractures and wear in clinical trials-A systematic review.

PubMed

Heintze, Siegward D; Ilie, Nicoleta; Hickel, Reinhard; Reis, Alessandra; Loguercio, Alessandro; Rousson, Valentin

2017-03-01

To evaluate a range of mechanical parameters of composite resins and compare the data to the frequency of fractures and wear in clinical studies. Based on a search of PubMed and SCOPUS, clinical studies on posterior composite restorations were investigated with regard to bias by two independent reviewers using Cochrane Collaboration's tool for assessing risk of bias in randomized trials. The target variables were chipping and/or fracture, loss of anatomical form (wear) and a combination of both (summary clinical index). These outcomes were modelled by time and material in a linear mixed effect model including random study and experiment effects. The laboratory data from one test institute were used: flexural strength, flexural modulus, compressive strength, and fracture toughness (all after 24-h storage in distilled water). For some materials flexural strength data after aging in water/saliva/ethanol were available. Besides calculating correlations between clinical and laboratory outcomes, we explored whether a model including a laboratory predictor dichotomized at a cut-off value better predicted a clinical outcome than a linear model. A total of 74 clinical experiments from 45 studies were included involving 31 materials for which laboratory data were also available. A weak positive correlation between fracture toughness and clinical fractures was found (Spearman rho=0.34, p=0.11) in addition to a moderate and statistically significant correlation between flexural strength and clinical wear (Spearman rho=0.46, p=0.01). When excluding those studies with "high" risk of bias (n=18), the correlations were generally weaker with no statistically significant correlation. For aging in ethanol, a very strong correlation was found between flexural strength decrease and clinical index, but this finding was based on only 7 materials (Spearman rho=0.96, p=0.0001). Prediction was not consistently improved with cutoff values. Correlations between clinical and laboratory outcomes were moderately positive with few significant results, fracture toughness being correlated with clinical fractures and flexural strength with clinical wear. Whether artificial aging enhances the prognostic value needs further investigations. Copyright © 2016 The Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Reinforcement of Dental Methacrylate with Glass Fiber after Heated Silane Application

PubMed Central

Fonseca, Rodrigo Borges; de Paula, Marcella Silva; Favarão, Isabella Negro; Kasuya, Amanda Vessoni Barbosa; de Almeida, Letícia Nunes; Mendes, Gustavo Adolfo Martins; Carlo, Hugo Lemes

2014-01-01

This study evaluated the influence of silane heat treatment and glass fiber fabrication type, industrially treated (I) or pure (P), on flexural and compressive strength of methacrylate resin bars (BISGMA/TEGDMA, 50/50%). Six groups (n = 10) were created: I-sil: I/silanated; P-sil: P-silanated; I-sil/heat: I/silanated heated to 100°; P-sil/heat: P/silanated heated to 100°; (I: I/not silanated; and P: P/not silanated. Specimens were prepared for flexural strength (10 × 2 × 1 mm) and for compressive strength 9.5 × 5.5 × 3 mm) and tested at 0.5 mm/min. Statistical analysis demonstrated the following for flexural strength (P < 0.05): I-sil: 155.89 ± 45.27BC; P-sil: 155.89 ± 45.27BC; I-sil/heat: 130.20 ± 22.11C; P-sil/heat: 169.86 ± 50.29AB; I: 131.87 ± 15.86C. For compressive strength, the following are demonstrated: I-sil: 1367.25 ± 188.77ab; P-sil: 867.61 ± 102.76d; I-sil/heat: 1162.98 ± 222.07c; P-sil/heat: 1499.35 ± 339.06a; and I: 1245.78 ± 211.16bc. Due to the impossibility of incorporating the stipulated amount of fiber, P group was excluded. Glass fiber treatment with heated silane enhanced flexural and compressive strength of a reinforced dental methacrylate. PMID:24967361

A 3D-Printable Polymer-Metal Soft-Magnetic Functional Composite-Development and Characterization.

PubMed

Khatri, Bilal; Lappe, Karl; Noetzel, Dorit; Pursche, Kilian; Hanemann, Thomas

2018-01-25

In this work, a 3D printed polymer-metal soft-magnetic composite was developed and characterized for its material, structural, and functional properties. The material comprises acrylonitrile butadiene styrene (ABS) as the polymer matrix, with up to 40 vol. % stainless steel micropowder as the filler. The composites were rheologically analyzed and 3D printed into tensile and flexural test specimens using a commercial desktop 3D printer. Mechanical characterization revealed a linearly decreasing trend of the ultimate tensile strength (UTS) and a sharp decrease in Young's modulus with increasing filler content. Four-point bending analysis showed a decrease of up to 70% in the flexural strength of the composite and up to a two-factor increase in the secant modulus of elasticity. Magnetic hysteresis characterization revealed retentivities of up to 15.6 mT and coercive forces of up to 4.31 kA/m at an applied magnetic field of 485 kA/m. The composite shows promise as a material for the additive manufacturing of passive magnetic sensors and/or actuators.

A 3D-Printable Polymer-Metal Soft-Magnetic Functional Composite—Development and Characterization

PubMed Central

Lappe, Karl; Noetzel, Dorit; Pursche, Kilian; Hanemann, Thomas

2018-01-01

In this work, a 3D printed polymer–metal soft-magnetic composite was developed and characterized for its material, structural, and functional properties. The material comprises acrylonitrile butadiene styrene (ABS) as the polymer matrix, with up to 40 vol. % stainless steel micropowder as the filler. The composites were rheologically analyzed and 3D printed into tensile and flexural test specimens using a commercial desktop 3D printer. Mechanical characterization revealed a linearly decreasing trend of the ultimate tensile strength (UTS) and a sharp decrease in Young’s modulus with increasing filler content. Four-point bending analysis showed a decrease of up to 70% in the flexural strength of the composite and up to a two-factor increase in the secant modulus of elasticity. Magnetic hysteresis characterization revealed retentivities of up to 15.6 mT and coercive forces of up to 4.31 kA/m at an applied magnetic field of 485 kA/m. The composite shows promise as a material for the additive manufacturing of passive magnetic sensors and/or actuators. PMID:29370112

Flexural behaviour of RCC beams with externally bonded FRP

NASA Astrophysics Data System (ADS)

Vignesh, S. Arun; Sumathi, A.; Saravana Raja Mohan, K.

2017-07-01

The increasing use of carbon and glass fibre reinforced polymer (FRP) sheets for strengthening existing reinforced concrete beams has generated considerable interest in understanding the behavior of the FRP sheets when subjected to bending. The study on flexure includes various parameters like percentage of increase in strength of the member due to the externally bonded Fiber reinforced polymer, examining the crack patterns, reasons of debonding of the fibre from the structure, scaling, convenience of using the fibres, cost effectiveness etc. The present work aims to study experimentally about the reasons behind the failure due to flexure of an EB-FRP concrete beam by studying the various parameters. Deflection control may become as important as flexural strength for the design of FRPreinforced concrete structures. A numerical model is created using FEM software and the results are compared with that of the experiment.

The influence of architecture on the elasticity and strength of Si(3)N(4)/BN fibrous-monolithic ceramic laminates

NASA Astrophysics Data System (ADS)

King, Bruce H.

Fibrous-monolithic ceramics are a class of material with many similarities to layered ceramic composites. Like layered composites, fibrous monoliths depend on a weak interphase to promote crack deflection and energy absorption, avoiding catastrophic failure. However, in a fibrous monolith, the interphase surrounds fiber-like "cells" of the strong phase, forming a continuous, 2-dimensional honeycomb network. In the most simple architecture, all cells are aligned unidirectionally. More complex architectures are easily produced by varying the orientation of successive layers relative to each other. The Young's modulus of the unidirectional architecture is predicted accurately along principal axes using a "brick" model, while the modulus at angles between 0sp° and 90sp° is predicted using laminate theory. Laminate theory may also be used to accurately predict the Young's modulus of multidirectional architectures such as a cross-ply 0sp°/90sp° and a quasi-isotropic 0sp°/{±}45sp°/90sp°. Unidirectional fibrous monolithic ceramics are linear elastic in flexure until the first major failure event. The flexural strength of the unidirectional architecture tested at orientations between 0sp° and 90sp° is observed to fall into three distinct regions. Between 0sp° and 10sp° the strength is a constant 450 MPa, but between 10sp° and 45sp°, it gradually drops to 80 MPa. Above 45sp° the strength remains essentially constant. Between 0sp° and 30sp°, the strength is accurately predicted using the Maximum Stress theory. Above 30sp°, the strength is predicted using the Tsai-Hill model. The multidirectional architectures exhibit nonlinearity in flexural loading prior to the peak stress. Cyclic loading experiments indicate that this nonlinearity is a result-of microcracking in the boron nitride cell boundaries of the off-axis layers. The cross-ply architecture exhibits a strength of 334 ± 35 MPa, while the quasi-isotropic has a strength of 255 ± 22 MPa. The models developed to describe the unidirectional architecture may be extended to predict upper and lower bounds on the strength of multidirectional architectures.

Evaluation and comparison of transverse and impact strength of different high strength denture base resins.

PubMed

Gupta, Abhinav; Tewari, R K

2016-01-01

The present study was undertaken to evaluate and compare the impact strength and transverse strength of the high-impact denture base materials. A conventional heat polymerized acrylic resin was used as a control. The entire experiment was divided into four main groups with twenty specimens each according to denture base material selected Trevalon, Trevalon Hi, DPI Tuff and Metrocryl Hi. These groups were further subgrouped into the two parameters selected, impact strength and flexural strength with ten specimens each. These specimens were then subjected to transverse bend tests with the help of Lloyds instrument using a three point bend principle. Impact tests were undertaken using an Izod-Charpy digital impact tester. This study was analyzed with one-way analysis of variance using Fisher f-test and Bonferroni t-test. There was a significant improvement in the impact strength of high-impact denture base resins as compared to control (Trevalon). However, in terms of transverse bend tests, only DPI Tuff showed higher transverse strength in comparison to control. Trevalon Hi and Metrocryl Hi showed a decrease in transverse strength. Within the limits of this in vitro study, (1) There is a definite increase in impact strength due to the incorporation of butadiene styrene rubber in this high strength denture base materials as compared to Trevalon used as a control. (2) Further investigations are required to prevent the unduly decrease of transverse strength. (3) It was the limitation of the study that the exact composition of the high-impact resins was not disclosed by the manufacturer that would have helped in better understanding of their behavior.

Measure of microhardness, fracture toughness and flexural strength of N-vinylcaprolactam (NVC)-containing glass-ionomer dental cements.

PubMed

Moshaverinia, Alireza; Brantley, William A; Chee, Winston W L; Rohpour, Nima; Ansari, Sahar; Zheng, Fengyuan; Heshmati, Reza H; Darr, Jawwad A; Schricker, Scott R; Rehman, Ihtesham U

2010-12-01

To investigate the effects of N-vinylcaprolactam (NVC)-containing terpolymers on the fracture toughness, microhardness, and flexural strength of conventional glass-ionomer cements (GIC). The terpolymer of acrylic acid (AA)-itaconic acid (IA)-N-vinylcaprolactam (NVC) with 8:1:1 (AA:IA:NVC) molar ratio was synthesized by free radical polymerization and characterized using (1)H NMR and FTIR. Experimental GIC samples were made from a 50% solution of the synthesized terpolymer with Fuji IX powder in a 3.6:1 P/L ratio. Specimens were mixed and fabricated at room temperature. Plane strain fracture toughness (K(Ic)) was measured in accordance with ASTM Standard 399-05. Vickers hardness was determined using a microhardness tester. Flexural strength was measured using samples with dimensions of 2 mm×2 mm×20 mm. For all mechanical property tests, specimens were first conditioned in distilled water at 37°C for 1 day or 1 week. Fracture toughness and flexural strength tests were conducted on a screw-driven universal testing machine using a crosshead speed of 0.5mm/min. Values of mechanical properties for the experimental GIC were compared with the control group (Fuji IX GIC), using one-way ANOVA and the Tukey multiple range test at α=0.05. The NVC-modified GIC exhibited significantly higher fracture toughness compared to the commercially available Fuji IX GIC, along with higher mean values of flexural strength and Vickers hardness, which were not significantly different. It was concluded that NVC-containing polymers are capable of enhancing clinically relevant properties for GICs. This new modified glass-ionomer is a promising restorative dental material. Copyright © 2010 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Enhancement of mechanical properties of 3D printed hydroxyapatite by combined low and high molecular weight polycaprolactone sequential infiltration.

PubMed

Suwanprateeb, Jintamai; Thammarakcharoen, Faungchat; Hobang, Nattapat

2016-11-01

A new infiltration technique using a combination of low and high molecular weight polycaprolactone (PCL) in sequence was developed as a mean to improve the mechanical properties of three dimensional printed hydroxyapatite (HA). It was observed that using either high (M n ~80,000) or low (M n ~10,000) molecular weight infiltration could only increase the flexural modulus compared to non-infiltrated HA, but did not affect strength, strain at break and energy at break. In contrast, a combination of low and high molecular infiltration in sequence increased the flexural modulus, strength and energy at break compared to those of non-infiltrated HA or infiltrated by high or low molecular weight PCL alone. This overall enhancement was found to be attributed to the densification of low molecular weight PCL and the reinforcement of high molecular PCL concurrently. The combined low and high molecular weight infiltration in sequence also maintained high osteoblast proliferation and differentiation of the composites at the similar level of the HA. Densification was a dominant mechanism for the change in modulus with porosity and density of the infiltrated HA/PCL composites. However, both densification and the reinforcing performance of the infiltration phase were crucial for strength and toughening enhancement of the composites possibly by the defect healing and stress shielding mechanisms. The sequence of using low molecular weight infiltration and followed by high molecular infiltration was seen to provide the greatest flexural properties and highest cells proliferation and differentiation capabilities.

Effect of fiber fibrillation on impact and flexural strength of coir fiber reinforced epoxy hybrid composites

NASA Astrophysics Data System (ADS)

Mawardi, I.; Jufriadi; Hanif

2018-03-01

This study aims to develop fiber-reinforced epoxy resin composites. This study presents the effect of fiber fibrillation on the impact and flextural strength of the epoxy hybrid composite reinforced by coir fiber. Coir is soaked in 5% NaOH solution for 5 hours. Then fiber is rocessed using a blender of 2000 rpm density fibrillation. The length of time the fibrillation varied for 10, 20 and 30 minutes. Volume fraction of 30% fiber and matrix 70% composited. The composite uses a matrix of epoxy by hand lay up method. The implemented tests are impact and flexural tests. The test results show fiber fibrillation treatment can improve the composite mechanical properties. The highest impact and flexural strength, 24.45 kJ/m2 and 87.91 MPa were produced with fiber fibrillation for 10 minutes.

DEGRADATION IN THE FATIGUE STRENGTH OF DENTIN BY DIAMOND BUR PREPARATIONS: IMPORTANCE OF CUTTING DIRECTION

PubMed Central

Majd, B.; Majd, H.; Porter, J.A.; Romberg, E.; Arola, D.

2014-01-01

The objectives of this investigation were to evaluate the degradation in fatigue strength of dentin by diamond bur preparations and to identify the importance of cutting direction. Three groups of coronal dentin specimens were prepared from unrestored 3rd molars, including a flaw free “control”, and two groups that received a diamond bur cutting treatment performed parallel or perpendicular to the specimen length. The specimens were subjected to static or cyclic flexural loading to failure and the results were compared with data for carbide bur cutting. Under static loading diamond bur cutting resulted in significantly flexure lower strength (p≤0.05) than the control for both cutting directions (from 154 MPa to approx. 124 MPa). However, there was no significant difference in the strength between the control and carbide bur treated specimens. Similarly, the fatigue strength of the diamond bur treated specimens was significantly lower (p≤0.0001) than that of the control for both cutting directions. Cutting in the perpendicular direction resulted in nearly 60% reduction to the endurance limit (from 44 MPa to 19 MPa). Based on the results, diamond bur cutting of cavity preparations causes a reduction in the fatigue strength of dentin, regardless of the cutting direction. To maintain the durability of dentin, cavity preparations introduced using diamond burs must be performed with appropriate cutting direction and followed by a finishing pass. PMID:25611951

Degradation in the fatigue strength of dentin by diamond bur preparations: Importance of cutting direction.

PubMed

Majd, B; Majd, H; Porter, J A; Romberg, E; Arola, D

2016-01-01

The objectives of this investigation were to evaluate the degradation in fatigue strength of dentin by diamond bur preparations and to identify the importance of cutting direction. Three groups of coronal dentin specimens were prepared from unrestored third molars, including a flaw free "control," and two groups that received a diamond bur cutting treatment performed parallel or perpendicular to the specimen length. The specimens were subjected to static or cyclic flexural loading to failure and the results were compared with data for carbide bur cutting. Under static loading diamond bur cutting resulted in significantly lower flexure strength (p ≤ 0.05) than the control for both cutting directions (from 154 to ∼124 MPa). However, there was no significant difference in the strength between the control and carbide bur treated specimens. Similarly, the fatigue strength of the diamond bur treated specimens was significantly lower (p ≤ 0.0001) than that of the control for both cutting directions. Cutting in the perpendicular direction resulted in nearly 60% reduction to the endurance limit (from 44 to 19 MPa). Based on the results, diamond bur cutting of cavity preparations causes a reduction in the fatigue strength of dentin, regardless of the cutting direction. To maintain the durability of dentin, cavity preparations introduced using diamond burs must be performed with appropriate cutting direction and followed by a finishing pass. © 2014 Wiley Periodicals, Inc.

Effect of fiber architecture on flexural characteristics and fracture of fiber-reinforced dental composites.

PubMed

Karbhari, Vistasp M; Strassler, Howard

2007-08-01

The aim of this study was to compare and elucidate the differences in damage mechanisms and response of fiber-reinforced dental resin composites based on three different brands under flexural loading. The types of reinforcement consisted of a unidirectional E-glass prepreg (Splint-It from Jeneric/Petron Inc.), an ultrahigh molecular weight polyethylene fiber based biaxial braid (Connect, Kerr) and an ultrahigh molecular weight polyethylene fiber based leno-weave (Ribbond). Three different commercially available fiber reinforcing systems were used to fabricate rectangular bars, with the fiber reinforcement close to the tensile face, which were tested in flexure with an emphasis on studying damage mechanisms and response. Eight specimens (n=8) of each type were tested. Overall energy capacity as well as flexural strength and modulus were determined and results compared in light of the different abilities of the architectures used. Under flexural loading unreinforced and unidirectional prepreg reinforced dental composites failed in a brittle fashion, whereas the braid and leno-weave reinforced materials underwent significant deformation without rupture. The braid reinforced specimens showed the highest peak load. The addition of the unidirectional to the matrix resulted in an average strain of 0.06mm/mm which is 50% greater than the capacity of the unreinforced matrix, whereas the addition of the braid and leno-weave resulted in increases of 119 and 126%, respectively, emphasizing the higher capacity of both the UHM polyethylene fibers and the architectures to hold together without rupture under flexural loading. The addition of the fiber reinforcement substantially increases the level of strain energy in the specimens with the maximum being attained in the braid reinforced specimens with a 433% increase in energy absorption capability above the unreinforced case. The minimum scatter and highest consistency in response is seen in the leno-weave reinforced specimens due to the details of the architecture which restrict fabric shearing and movement during placement. It is crucial that the appropriate selection of fiber architectures be made not just from a perspective of highest strength, but overall damage tolerance and energy absorption. Differences in weaves and architectures can result in substantially different performance and appropriate selection can mitigate premature and catastrophic failure. The study provides details of materials level response characteristics which are useful in selection of the fiber reinforcement based on specifics of application.

Woven Hybrid Composites - Tensile and Flexural Properties of Jute Mat Fibres with Epoxy Composites

NASA Astrophysics Data System (ADS)

Gopal, P.; Bupesh Raja, V. K.; Chandrasekaran, M.; Dhanasekaran, C.

2017-03-01

The jute mat fibers are fabricated with several layers of fiber with opposite orientation in addition with coconut shell powder and resins. In current trends, metallic components are replaced by natural fibers because of the inherent properties such as light in weight, easy to fabricate, less cost and easy availability. This material has high strength and withstands the load. In this investigation the plates are made without stitching the fiber. The result of tensile strength and flexural strength are compared with nano material (coconut shell powder).

Ultra-high modulus organic fiber hybrid composites

NASA Technical Reports Server (NTRS)

Champion, A. R.

1981-01-01

An experimental organic fiber, designated Fiber D, was characterized, and its performance as a reinforcement for composites was investigated. The fiber has a modulus of 172 GPa, tensile strength of 3.14 GPa, and density of 1.46 gm/cu cm. Unidirectional Fiber D/epoxy laminates containing 60 percent fiber by volume were evaluated in flexure, shear, and compression, at room temperature and 121 C in both the as fabricated condition and after humidity aging for 14 days at 95 percent RH and 82 C. A modulus of 94.1 GPa, flexure strength of 700 MPa, shear strength of 54 MPa, and compressive strength of 232 MPa were observed at room temperature. The as-fabricated composites at elevated temperature and humidity aged material at room temperature had properties 1 to 20 percent below these values. Combined humidity aging plus evaluated temperature testing resulted in even lower mechanical properties. Hybrid composite laminates of Fiber D with Fiber FP alumina or Thornel 300 graphite fiber were also evaluated and significant increases in modulus, flexure, and compressive strengths were observed.

Laser Paint Stripping

DTIC Science & Technology

1991-06-01

of this laser system to remove paint from metals, including aluminum, and from carbon fiber reinforced composites cleanly and without damage to the...The tests perpendicular to fiber direction in the unidirectional composite were selected as most sensitive indicators of damage. Flexural tests on the... Composite Flexural Strength Tests 10 2.2.11 Composite Compressive Strength Tests 11 2.2.12 Turbine Blade Cleaning 11 2.2.13 Residual Carbon 11 2.2.14

Characterization of cassava starch based foam blended with plant proteins, kraft fiber, and palm oil.

PubMed

Kaisangsri, Nattapon; Kerdchoechuen, Orapin; Laohakunjit, Natta

2014-09-22

Cassava starch foam (CSF) trays blended with zein, gluten, soy protein, kraft fiber, and palm oil at various concentrations: 0, 5, 10 and 15% by weight of starch, were characterized. The addition of zein and gluten into CSF resulted in consolidated and homogeneous structural foams compared to its controls. Moreover, the flexural and compressive strength increased with increasing kraft, zein and gluten. CSF containing 15% kraft gave the highest flexural and compressive strength. However, the addition of palm oil into CSF gave the lowest flexural strength and compressive strength. The observed water absorption and water solubility index of CSFs blended with 15% zein and 15% gluten protein was lowest. Although kraft, zein and gluten could improve mechanical properties, water absorption and water solubility were greater than the expanded polystyrene foam (EPS). The CSF trays in this study might be an alternative for packing low water content foods. Copyright © 2014 Elsevier Ltd. All rights reserved.

Chemical Vapor Deposited SiC (SCS-0) Fiber-Reinforced Strontium Aluminosilicate Glass-Ceramic Composites

NASA Technical Reports Server (NTRS)

Bansal, Narottam P.

1997-01-01

Unidirectional SrO Al2O3 2SiO2 glass-ceramic matrix composites reinforced with uncoated Chemical Vapor Deposited (CVD) SiC (SCS-0) fibers have been fabricated by hot-pressing under appropriate conditions using the glass-ceramic approach. Almost fully dense composites having a fiber volume fraction of 0.24 have been obtained. Monoclinic celsian, SrAl2Si2O8, was the only crystalline phase observed in the matrix by x-ray diffraction. No chemical reaction was observed between the fiber and the matrix after high temperature processing. In three-point flexure, the composite exhibited a first matrix cracking stress of approx. 231 +/- 20 MPa and an ultimate strength of 265 +/- 17 MPa. Examination of fracture surfaces revealed limited short length fiber pull-out. From fiber push-out, the fiber/matrix interfacial debonding and frictional strengths were evaluated to be approx. 17.5 +/- 2.7 MPa and 11.3 +/- 1.6 MPa, respectively. Some fibers were strongly bonded to the matrix and could not be pushed out. The micromechanical models were not useful in predicting values of the first matrix cracking stress as well as the ultimate strength of the composites.

Improved performance of diatomite-based dental nanocomposite ceramics using layer-by-layer assembly

PubMed Central

Lu, Xiaoli; Xia, Yang; Liu, Mei; Qian, Yunzhu; Zhou, Xuefeng; Gu, Ning; Zhang, Feimin

2012-01-01

To fabricate high-strength diatomite-based ceramics for dental applications, the layer-by-layer technique was used to coat diatomite particles with cationic [poly(allylamine hydrochloride)] and anionic [poly(sodium 4-styrenesulfonate)] polymers to improve the dispersion and adsorption of positively charged nano-ZrO2 (zirconia) as a reinforcing agent. The modified diatomite particles had reduced particle size, narrower size distribution, and were well dispersed, with good adsorption of nano-ZrO2. To determine the optimum addition levels for nano-ZrO2, ceramics containing 0, 20, 25, 30, and 35 wt% nano-ZrO2 were sintered and characterized by the three-point bending test and microhardness test. In addition to scanning electron microscopy, propagation phase-contrast synchrotron X-ray microtomography was used to examine the internal structure of the ceramics. The addition of 30 wt% nano-ZrO2 resulted in the highest flexural strength and fracture toughness with reduced porosity. Shear bond strength between the core and veneer of our diatomite ceramics and the most widely used dental ceramics were compared; the shear bond strength value for the diatomite-based ceramics was found to be significantly higher than for other groups (P < 0.05). Our results show that diatomite-based nanocomposite ceramics are good potential candidates for ceramic-based dental materials. PMID:22619551

Improved performance of diatomite-based dental nanocomposite ceramics using layer-by-layer assembly.

PubMed

Lu, Xiaoli; Xia, Yang; Liu, Mei; Qian, Yunzhu; Zhou, Xuefeng; Gu, Ning; Zhang, Feimin

2012-01-01

To fabricate high-strength diatomite-based ceramics for dental applications, the layer-by-layer technique was used to coat diatomite particles with cationic [poly(allylamine hydrochloride)] and anionic [poly(sodium 4-styrenesulfonate)] polymers to improve the dispersion and adsorption of positively charged nano-ZrO(2) (zirconia) as a reinforcing agent. The modified diatomite particles had reduced particle size, narrower size distribution, and were well dispersed, with good adsorption of nano-ZrO(2). To determine the optimum addition levels for nano-ZrO(2), ceramics containing 0, 20, 25, 30, and 35 wt% nano-ZrO(2) were sintered and characterized by the three-point bending test and microhardness test. In addition to scanning electron microscopy, propagation phase-contrast synchrotron X-ray microtomography was used to examine the internal structure of the ceramics. The addition of 30 wt% nano-ZrO(2) resulted in the highest flexural strength and fracture toughness with reduced porosity. Shear bond strength between the core and veneer of our diatomite ceramics and the most widely used dental ceramics were compared; the shear bond strength value for the diatomite-based ceramics was found to be significantly higher than for other groups (P < 0.05). Our results show that diatomite-based nanocomposite ceramics are good potential candidates for ceramic-based dental materials.

Fatigue Characterization of Fire Resistant Syntactic Foam Core Material

NASA Astrophysics Data System (ADS)

Hossain, Mohammad Mynul

Eco-Core is a fire resistant material for sandwich structural application; it was developed at NC A&T State University. The Eco-Core is made of very small amount of phenolic resin and large volume of flyash by a syntactic process. The process development, static mechanical and fracture, fire and toxicity safety and water absorption properties and the design of sandwich structural panels with Eco-Core material was established and published in the literature. One of the important properties that is needed for application in transportation vehicles is the fatigue performance under different stress states. Fatigue data are not available even for general syntactic foams. The objective of this research is to investigate the fatigue performance of Eco-Core under three types of stress states, namely, cyclic compression, shear and flexure, then document failure modes, and develop empherical equations for predicting fatigue life of Eco-Core under three stress states. Compression-Compression fatigue was performed directly on Eco-Core cylindrical specimen, whereas shear and flexure fatigue tests were performed using sandwich beam made of E glass-Vinyl Ester face sheet and Eco-Core material. Compression-compression fatigue test study was conducted at two values of stress ratios (R=10 and 5), for the maximum compression stress (sigmamin) range of 60% to 90% of compression strength (sigmac = 19.6 +/- 0.25 MPa) for R=10 and 95% to 80% of compression strength for R=5. The failure modes were characterized by the material compliance change: On-set (2% compliance change), propagation (5%) and ultimate failure (7%). The number of load cycles correspond to each of these three damages were characterized as on-set, propagation and total lives. A similar approach was used in shear and flexure fatigue tests with stress ratio of R=0.1. The fatigue stress-number of load cycles data followed the standard power law equation for all three stress states. The constant of the equation were established for the three stress states and three types of the failure modes. This equation was used to estimate endurance limit (106 cycles) of the material. Like metallic materials, the compression fatigue life of Eco-Core was found to be dependent on the stress range instead of maximum or mean cyclic stress. Furthermore shear and flexural ultimate failure of the core material was found to be due to a combination of shear and tensile stress.

Development of novel dental nanocomposites reinforced with polyhedral oligomeric silsesquioxane (POSS).

PubMed

Wu, Xiaorong; Sun, Yi; Xie, Weili; Liu, Yanju; Song, Xueyu

2010-05-01

It has been the focus to develop low shrinkage dental composite resins in recent ten years. A major difficulty in developing low shrinkage dental materials is that their deficiency in mechanical properties cannot satisfy the clinical purpose. The aim of this study is to develop novel dental nanocomposites incorporated with polyhedral oligomeric silsesquioxane (POSS). It is especially interesting to evaluate the volumetric shrinkage and mechanical properties, improve the shrinkage, working performances and service life of dental composite resins. The effect of added POSS on the composites' mechanical properties has been evaluated. The weight percentages of added POSS are 0, 2, 5, 10 and 15wt% respectively. Fourier-transform infra-red spectroscopy and X-ray diffraction were used to characterize their microstructures. Physico-mechanical properties that were investigated included volumetric shrinkage, flexural strength, flexural modulus, compressive strength, compressive modulus, Viker's hardness and fracture energy. Furthermore, the possible reinforced mechanism has been discussed. The shrinkage of novel nanocomposites decreased from 3.53% to 2.18%. The nanocomposites incorporated with POSS showed greatly improved mechanical properties, for example, with only 2wt% POSS added, the nanocompsite's flexural strength increased 15%, compressive strength increased 12%, hardness increased 15% and uncommonly, even the toughness of resins was obviously increased. With 5wt% POSS polymerized, compressive strength increased from 192MPa to 251MPa and compressive modulus increased from 3.93GPa to 6.62GPa, but flexure strength began to decline from 87MPa to 75MPa. This finding indicated that the reinforcing mechanism of flexure state maybe different from that of compressive state. The mechanical properties and volumetric shrinkage of dental composite resins polymerized with POSS can be improved significantly. In current study, the nanocomposite with 2wt% POSS incorporated is observed to achieve the best improved effects. 2010 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Feasibility of Kevlar 49/PMR-15 Polyimide for High Temperature Applications

NASA Technical Reports Server (NTRS)

Hanson, M. P.

1980-01-01

Kevlar 49 aramid organic fiber reinforced PMR-15 polyimide laminates were characterized to determine the applicability of the material to high temperature aerospace structures. Kevlar 49/3501-6 epoxy laminates were fabricated and characterized for comparison with the Kevlar 49/PMR-15 polyimide material. Flexural strengths and moduli and interlaminar shear strengths were determined from 75 F to 600 F for the PMR-15 and from 75 F to 450 F for the Kevlar/3501-6 epoxy material. The effects of hydrothermal and long-term elevated temperature exposures on the flexural strengths and moduli and the interlaminar shear strengths were also studied.

Feasibility of Kevlar 49/PMR-15 polyimide for high temperature applications

NASA Technical Reports Server (NTRS)

Hanson, M. P.

1980-01-01

Kevlar 49 aramid organic fiber reinforced PMR-15 polyimide laminates were characterized to determine the applicability of the material to high temperature aerospace structures. Kevlar 49/3501-6 epoxy laminates were fabricated and characterized for comparison with the Kevlar 49/PMR-15 polyimide material. Flexural strengths and moduli and interlaminar shear strengths were determined from 75 to 600 F for the PMR-15 and from 75 to 450 F for the Kevlar 49/3501-6 epoxy material. The study also included the effects of hydrothermal and long-term elevated temperature exposures on the flexural strengths and moduli and the interlaminar shear strengths.

Reuse of waste iron as a partial replacement of sand in concrete.

PubMed

Ismail, Zainab Z; Al-Hashmi, Enas A

2008-11-01

One of the major environmental issues in Iraq is the large quantity of waste iron resulting from the industrial sector which is deposited in domestic waste and in landfills. A series of 109 experiments and 586 tests were carried out in this study to examine the feasibility of reusing this waste iron in concrete. Overall, 130 kg of waste iron were reused to partially replace sand at 10%, 15%, and 20% in a total of 1703 kg concrete mixtures. The tests performed to evaluate waste-iron concrete quality included slump, fresh density, dry density, compressive strength, and flexural strength tests: 115 cubes of concrete were molded for the compressive strength and dry density tests, and 87 prisms were cast for the flexural strength tests. This work applied 3, 7, 14, and 28 days curing ages for the concrete mixes. The results confirm that reuse of solid waste material offers an approach to solving the pollution problems that arise from an accumulation of waste in a production site; in the meantime modified properties are added to the concrete. The results show that the concrete mixes made with waste iron had higher compressive strengths and flexural strengths than the plain concrete mixes.

INFLUENCE OF DIFFERENT CANTILEVER EXTENSIONS AND GLASS OR POLYARAMID REINFORCEMENT FIBERS ON FRACTURE STRENGTH OF IMPLANT-SUPPORTED TEMPORARY FIXED PROSTHESIS

PubMed Central

Colán Guzmán, Paola; de Freitas, Fernando Furtado Antunes; Ferreira, Paulo Martins; de Freitas, César Antunes; Reis, Kátia Rodrigues

2008-01-01

In long-term oral rehabilitation treatments, resistance of provisional crowns is a very important factor, especially in cases of an extensive edentulous distal space. The aim of this laboratorial study was to evaluate an acrylic resin cantilever-type prosthesis regarding the flexural strength of its in-balance portion as a function of its extension variation and reinforcement by two types of fibers (glass and polyaramid), considering that literature is not conclusive on this subject. Each specimen was composed by 3 total crowns at its mesial portion, each one attached to an implant component (abutment), while the distal portion (cantilever) had two crowns. Each specimen was constructed by injecting acrylic resin into a two-part silicone matrix placed on a metallic base. In each specimen, the crowns were fabricated with either acrylic resin (control group) or acrylic resin reinforced by glass (Fibrante, Angelus) or polyaramide (Kevlar 49, Du Pont) fibers. Compression load was applied on the cantilever, in a point located 7, 14 or 21 mm from the distal surface of the nearest crown with abutment, to simulate different extensions. The specimen was fixed on the metallic base and the force was applied until fracture in a universal test machine. Each one of the 9 sub-groups was composed by 10 specimens. Flexural strength means (in kgf) for the distances of 7, 14 and 21 mm were, respectively, 28.07, 8.27 and 6.39 for control group, 31.89, 9.18 and 5.16 for Kevlar 49 and 30.90, 9.31 and 6.86 for Fibrante. Data analysis ANOVA showed statistically significant difference (p<0.05) only regarding cantilever extension. Tukey's test detected significantly higher flexural strength for the 7 mm-distance, followed by 14 and 21 mm. Fracture was complete only on specimens of non-reinforced groups. PMID:19089201

Influence of different cantilever extensions and glass or polyaramide reinforcement fibers on fracture strength of implant-supported temporary.

PubMed

Colán Guzmán, Paola; Freitas, Fernando Furtado Antunes de; Ferreira, Paulo Martins; Freitas, César Antunes de; Reis, Kátia Rodrigues

2008-01-01

In long-term oral rehabilitation treatments, resistance of provisional crowns is a very important factor, especially in cases of an extensive edentulous distal space. The aim of this laboratorial study was to evaluate an acrylic resin cantilever-type prosthesis regarding the flexural strength of its in-balance portion as a function of its extension variation and reinforcement by two types of fibers (glass and polyaramid), considering that literature is not conclusive on this subject. Each specimen was composed by 3 total crowns at its mesial portion, each one attached to an implant component (abutment), while the distal portion (cantilever) had two crowns. Each specimen was constructed by injecting acrylic resin into a two-part silicone matrix placed on a metallic base. In each specimen, the crowns were fabricated with either acrylic resin (control group) or acrylic resin reinforced by glass (Fibrante, Angelus) or polyaramide (Kevlar 49, Du Pont) fibers. Compression load was applied on the cantilever, in a point located 7, 14 or 21 mm from the distal surface of the nearest crown with abutment, to simulate different extensions. The specimen was fixed on the metallic base and the force was applied until fracture in a universal test machine. Each one of the 9 sub-groups was composed by 10 specimens. Flexural strength means (in kgf) for the distances of 7, 14 and 21 mm were, respectively, 28.07, 8.27 and 6.39 for control group, 31.89, 9.18 and 5.16 for Kevlar 49 and 30.90, 9.31 and 6.86 for Fibrante. Data analysis ANOVA showed statistically significant difference (p<0.05) only regarding cantilever extension. Tukey's test detected significantly higher flexural strength for the 7 mm-distance, followed by 14 and 21 mm. Fracture was complete only on specimens of non-reinforced groups.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Yang, Kang; Wu, Sujun; Guan, Juan

Strong and tough epoxy composites are developed using a less-studied fibre reinforcement, that of natural silk. Two common but structurally distinct silks from the domestic B. mori/Bm and the wild A. pernyi/Ap silkworms are selected in fabric forms. We show that the toughening effects on silk-epoxy composites or SFRPs are dependent on the silk species and the volume fraction of silk. Both silks enhance the room-temperature tensile and flexural mechanical properties of the composite, whereas the more resilient Ap silk shows a more pronounced toughening effect and a lower critical reinforcement volume for the brittle-ductile transition. Specifically, our 60 vol.%more » Ap-SFRP displays a three-fold elevation in tensile and flexural strength, as compared to pure epoxy resin, with an order of magnitude higher breaking energy via a distinct, ductile failure mode. Importantly, the 60 vol.% Ap-SFRP remains ductile with 7% flexural elongation at lower temperatures (-50 °C). Under impact, these SFRPs show significantly improved energy absorption, and the 60 vol.% Ap-SFRP has an impact strength some eight times that of pure epoxy resin. Lastly, the findings demonstrate both marked toughening and strengthening effects for epoxy composites from natural silk reinforcements, which presents opportunities for mechanically superior and "green" structural composites.« less

Enhancing the Mechanical Toughness of Epoxy-Resin Composites Using Natural Silk Reinforcements

DOE PAGES

Yang, Kang; Wu, Sujun; Guan, Juan; ...

2017-09-20

Strong and tough epoxy composites are developed using a less-studied fibre reinforcement, that of natural silk. Two common but structurally distinct silks from the domestic B. mori/Bm and the wild A. pernyi/Ap silkworms are selected in fabric forms. We show that the toughening effects on silk-epoxy composites or SFRPs are dependent on the silk species and the volume fraction of silk. Both silks enhance the room-temperature tensile and flexural mechanical properties of the composite, whereas the more resilient Ap silk shows a more pronounced toughening effect and a lower critical reinforcement volume for the brittle-ductile transition. Specifically, our 60 vol.%more » Ap-SFRP displays a three-fold elevation in tensile and flexural strength, as compared to pure epoxy resin, with an order of magnitude higher breaking energy via a distinct, ductile failure mode. Importantly, the 60 vol.% Ap-SFRP remains ductile with 7% flexural elongation at lower temperatures (-50 °C). Under impact, these SFRPs show significantly improved energy absorption, and the 60 vol.% Ap-SFRP has an impact strength some eight times that of pure epoxy resin. Lastly, the findings demonstrate both marked toughening and strengthening effects for epoxy composites from natural silk reinforcements, which presents opportunities for mechanically superior and "green" structural composites.« less

Behavior of fiber reinforced mortar joints in masonry walls subjected to in-plane shear and out-of-plane bending

NASA Astrophysics Data System (ADS)

Armwood, Catherine K.

In this project, 26 fiber-reinforced mortar (FRM) mixtures are evaluated for their workability and strength characteristics. The specimens tested include two control mixtures and 24 FRMs. The mixtures were made of two types of binders; Type N Portland cement lime (Type N-PCL) and Natural Hydrated Lime 5 (NHL5); and 6 fiber types (5 synthetic fibers and one organic). When tested in flexure, the results indicate that majority of the synthetic fiber mixtures enhanced the performance of the mortar and the nano-nylon and horse hair fibers were the least effective in improving the mortar's modulus of rupture, ductility, and energy absorption. Four FRMs that improved the mortar's mechanical properties most during the flexural strength test were then used to conduct additional experiments. The FRM's compressive strength, as well as flexural and shear bond strength with clay and concrete masonry units were determined. Those four mixtures included Type N-PCL as the binder and 4 synthetic fibers. They were evaluated at a standard laboratory flow rate of 110% +/- 5% and a practical field flow rate of 130% +/- 5%. Results indicate that the use of fibers decreases the compressive strength of the mortar most of the time. However, the bond strength test results were promising: 81% of the FRM mixtures increased the flexural bond strength of the prism. The mixtures at 110 +/- 5% flow rate bonded better with concrete bricks and those ate 130+/-5% flow rate bonded better with clay bricks. The results of the shear bond strength show 50% of the FRM mixtures improved the shear bond strength. The FRM mixtures at 110+/-5% flow rate bonded with clay units provided the most improvement in shear bond strength compared to control specimen results. Along with detailed discussions and derived conclusions of these experiments, this dissertation includes recommendations for the most feasible FRM for different applications.

Investigation of the elastic modulus, tensile and flexural strength of five skull simulant materials for impact testing of a forensic skin/skull/brain model.

PubMed

Falland-Cheung, Lisa; Waddell, J Neil; Chun Li, Kai; Tong, Darryl; Brunton, Paul

2017-04-01

Conducting in vitro research for forensic, impact and injury simulation modelling generally involves the use of a skull simulant with mechanical properties similar to those found in the human skull. For this study epoxy resin, fibre filled epoxy resin, 3D-printing filaments (PETG, PLA) and self-cure acrylic denture base resin were used to fabricate the specimens (n=20 per material group), according to ISO 527-2 IBB and ISO20795-1. Tensile and flexural testing in a universal testing machine was used to measure their tensile/flexural elastic modulus and strength. The results showed that the epoxy resin and fibre filled epoxy resin had similar tensile elastic moduli (no statistical significant difference) with lower values observed for the other materials. The fibre filled epoxy resin had a considerably higher flexural elastic modulus and strength, possibly attributed to the presence of fibres. Of the simulants tested, epoxy resin had an elastic modulus and flexural strength close to that of mean human skull values reported in the literature, and thus can be considered as a suitable skull simulant for a skin/skull/brain model for lower impact forces that do not exceed the fracture stress. For higher impact forces a 3D printing filament (PLA) may be a more suitable skull simulant material, due to its closer match to fracture stresses found in human skull bone. Influencing factors were also anisotropy, heterogeneity and viscoelasticity of human skull bone and simulant specimens. Copyright © 2017 Elsevier Ltd. All rights reserved.

Mechanical characterization and structural analysis of recycled fiber-reinforced-polymer resin-transfer-molded beams

NASA Astrophysics Data System (ADS)

Tan, Eugene Wie Loon

1999-09-01

The present investigation was focussed on the mechanical characterization and structural analysis of resin-transfer-molded beams containing recycled fiber-reinforced polymers. The beams were structurally reinforced with continuous unidirectional glass fibers. The reinforcing filler materials consisted entirely of recycled fiber-reinforced polymer wastes (trim and overspray). The principal resin was a 100-percent dicyclo-pentadiene unsaturated polyester specially formulated with very low viscosity for resin transfer molding. Variations of the resin transfer molding technique were employed to produce specimens for material characterization. The basic materials that constituted the structural beams, continuous-glass-fiber-reinforced, recycled-trim-filled and recycled-overspray-filled unsaturated polyesters, were fully characterized in axial and transverse compression and tension, and inplane and interlaminar shear, to ascertain their strengths, ultimate strains, elastic moduli and Poisson's ratios. Experimentally determined mechanical properties of the recycled-trim-filled and recycled-overspray-filled materials from the present investigation were superior to those of unsaturated polyester polymer concretes and Portland cement concretes. Mechanical testing and finite element analyses of flexure (1 x 1 x 20 in) and beam (2 x 4 x 40 in) specimens were conducted. These structurally-reinforced specimens were tested and analyzed in four-point, third-point flexure to determine their ultimate loads, maximum fiber stresses and mid-span deflections. The experimentally determined load capacities of these specimens were compared to those of equivalent steel-reinforced Portland cement concrete beams computed using reinforced concrete theory. Mechanics of materials beam theory was utilized to predict the ultimate loads and mid-span deflections of the flexure and beam specimens. However, these predictions proved to be severely inadequate. Finite element (fracture propagation) analyses of the flexure and beam specimens were also performed. These progressive failure analyses more closely approximated flexural behavior under actual testing conditions by reducing the elastic moduli of elements that were considered to have partially or totally failed. Individual element failures were predicted using the maximum stress, Tsai-Hill and Tsai-Wu failure criteria. Excellent predictions of flexural behavior were attributed to the progressive failure analyses combined with an appropriate failure criterion, and the reliable input material properties that were generated.

Ageing kinetics and strength of airborne-particle abraded 3Y-TZP ceramics.

PubMed

Cotič, Jasna; Jevnikar, Peter; Kocjan, Andraž

2017-07-01

The combined effects of alumina airborne-particle abrasion and prolonged in vitro ageing on the flexural strength of 3Y-TZP ceramic have been studied. The aim was to identify the different effects on the surface and subsurface regions that govern the performance of this popular bioceramic known for its susceptibility to low-temperature degradation (LTD). As-sintered or airborne-particle abraded 3Y-TZP discs were subjected to ageing at 134°C for up to 480h. Biaxial flexural strength was measured and the relative amount of monoclinic phase determined using X-ray diffraction. The transformed zone depth (TZD) was observed on cross-sections with scanning electron microscopy coupled with a focused ion beam. Segmented linear regression was used to analyze the flexural strength and TZD as functions of the ageing time. A two-step linear ageing kinetics was detected in airborne-particle abraded specimens, reflecting the different microstructures through which the LTD proceeds into the bulk. A 10μm thick altered zone under the abraded surface was involved in both the surface strengthening and the increased ageing resistance. When the zone was annihilated by the LTD, the strength of the ceramic specimens and the speed of LTD returned to the values measured before abrasion. Even at prolonged ageing times, the strength of abraded groups was not lower than that of as-sintered groups. Both the ageing kinetics and the flexural strength were prominently affected by airborne-particle abrasion, which altered the subsurface microstructure and phase composition. Airborne-particle abrasion was not harmful to the 3Y-TZP ceramics' stability. Copyright © 2017 The Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

The effect of surface grinding and sandblasting on flexural strength and reliability of Y-TZP zirconia ceramic.

PubMed

Kosmac, T; Oblak, C; Jevnikar, P; Funduk, N; Marion, L

1999-11-01

This study was conducted to evaluate the effect of grinding and sandblasting on the microstructure, biaxial flexural strength and reliability of two yttria stabilized tetragonal zirconia (Y-TZP) ceramics. Two Y-TZP powders were used to produce fine grained and coarse grained microstructures. Sixty discs from each material were randomly divided into six groups of ten. For each group, a different surface treatment was applied: dry grinding, wet grinding, sandblasting, dry grinding + sandblasting, sandblasting + dry grinding and a control group. Biaxial flexural strength was determined and data were analyzed using one-way ANOVA, followed by Tukey's HSD test (p < 0.05). In addition, Weibull statistics was used to analyze the variability of flexural strength. The relative amount of transformed monoclinic zirconia, corresponding transformed zone depth (TZD) and the mean critical defect size Ccr were calculated. There was no difference in mean strength between the as sintered fine and coarse grained Y-TZP. Significant differences (p < 0.05) were found between the control group and ground fine grained material for both wet and dry grinding. Sandblasting significantly increased the strength in fine and coarse grained materials. All surface treatment procedures reduced the Weibull modulus of Y-TZP. For both materials, the highest amount of the monoclinic phase and the largest TZD was found after sandblasting. Lower amounts of the monoclinic phase were obtained after both grinding procedures, where the highest mean critical defect size Ccr was also calculated. Our results indicate that sandblasting may provide a powerful technique for strengthening Y-TZP in clinical practice. In contrast, grinding may lead to substantial strength degradation and reduced reliability of prefabricated zirconia elements, therefore, sandblasting of ground surfaces is suggested.

Modification of conventional glass-ionomer cements with N-vinylpyrrolidone containing polyacids, nano-hydroxy and fluoroapatite to improve mechanical properties.

PubMed

Moshaverinia, Alireza; Ansari, Sahar; Movasaghi, Zanyar; Billington, Richard W; Darr, Jawwad A; Rehman, Ihtesham U

2008-10-01

The objective of this study was to enhance the mechanical strength of glass-ionomer cements, while preserving their unique clinical properties. Copolymers incorporating several different segments including N-vinylpyrrolidone (NVP) in different molar ratios were synthesized. The synthesized polymers were copolymers of acrylic acid and NVP with side chains containing itaconic acid. In addition, nano-hydroxyapatite and fluoroapatite were synthesized using an ethanol-based sol-gel technique. The synthesized polymers were used in glass-ionomer cement formulations (Fuji II commercial GIC) and the synthesized nanoceramic particles (nano-hydroxy or fluoroapatite) were also incorporated into commercial glass-ionomer powder, respectively. The synthesized materials were characterized using FTIR and Raman spectroscopy and scanning electron microscopy. Compressive, diametral tensile and biaxial flexural strengths of the modified glass-ionomer cements were evaluated. After 24h setting, the NVP modified glass-ionomer cements exhibited higher compressive strength (163-167 MPa), higher diametral tensile strength (DTS) (13-17 MPa) and much higher biaxial flexural strength (23-26 MPa) in comparison to Fuji II GIC (160 MPa in CS, 12MPa in DTS and 15 MPa in biaxial flexural strength). The nano-hydroxyapatite/fluoroapatite added cements also exhibited higher CS (177-179 MPa), higher DTS (19-20 MPa) and much higher biaxial flexural strength (28-30 MPa) as compared to the control group. The highest values for CS, DTS and BFS were found for NVP-nanoceramic powder modified cements (184 MPa for CS, 22 MPa for DTS and 33 MPa for BFS) which were statistically higher than control group. It was concluded that, both NVP modified and nano-HA/FA added glass-ionomer cements are promising restorative dental materials with improved mechanical properties.

Effect of waste banner as fiber on mechanical properties of concrete

NASA Astrophysics Data System (ADS)

Rahmawati, Anis; Saputro, Ida Nugroho

2017-06-01

Banner is broadly used as advertisement media and event backdrop that is usually only used at one moment, resulting to a lot of waste banners. Banner made from nylon fiber is covered by polyvinyl. Nylon is well known as a material with high tensile strength. This research was done as a preliminary investigation on the opportunity of using the waste banner as fiber material of concrete by evaluating its mechanical properties, namely compressive and flexural strength. Research conducted by making cylinder shape specimens of 15 mm in diameter and 300 mm in height for the compressive strength test. While the specimen shape for flexural strength test was a rectangular prism with dimension of 150 mm in height, 150 mm in width, and 600 mm in length. Fiber generated from waste banner was added in concrete mixtures with percentage of 0.00%, 0.20%, 0.40%, 0.60%, 0.80%, and 1.00% by weight of concrete. The concrete strength was tested at 28 days after standard moisture and temperature curing. Experimental results indicated that the addition of 0.20% of waste banner obtained the highest compressive strength that was 21.967 Mpa, while 0.40% of waste banner obtained the highest flexural strength of 4.663 Mpa.

Comprehensive analyses of how tubule occlusion and advanced glycation end-products diminish strength of aged dentin

NASA Astrophysics Data System (ADS)

Shinno, Yuko; Ishimoto, Takuya; Saito, Mitsuru; Uemura, Reo; Arino, Masumi; Marumo, Keishi; Nakano, Takayoshi; Hayashi, Mikako

2016-01-01

In clinical dentistry, since fracture is a major cause of tooth loss, better understanding of mechanical properties of teeth structures is important. Dentin, the major hard tissue of teeth, has similar composition to bone. In this study, we investigated the mechanical properties of human dentin not only in terms of mineral density but also using structural and quality parameters as recently accepted in evaluating bone strength. Aged crown and root dentin (age ≥ 40) exhibited significantly lower flexural strength and toughness than young dentin (age < 40). Aged dentin, in which the dentinal tubules were occluded with calcified material, recorded the highest mineral density; but showed significantly lower flexural strength than young dentin. Dentin with strong alignment of the c-axis in hydroxyapatite exhibited high fracture strength, possibly because the aligned apatite along the collagen fibrils may reinforce the intertubular dentin. Aged dentin, showing a high advanced glycation end-products (AGEs) level in its collagen, recorded low flexural strength. We first comprehensively identified significant factors, which affected the inferior mechanical properties of aged dentin. The low mechanical strength of aged dentin is caused by the high mineral density resulting from occlusion of dentinal tubules and accumulation of AGEs in dentin collagen.

Strength of mortar containing rubber tire particle

NASA Astrophysics Data System (ADS)

Jusoh, M. A.; Abdullah, S. R.; Adnan, S. H.

2018-04-01

The main focus in this investigation is to determine the strength consist compressive and tensile strength of mortar containing rubber tire particle. In fact, from the previous study, the strength of mortar containing waste rubber tire in mortar has a slightly decreases compare to normal mortar. In this study, rubber tire particle was replacing on volume of fine aggregate with 6%. 9% and 12%. The sample were indicated M0 (0%), M6 (6%), M9 (9%) and M12 (12%). In this study, two different size of sample used with cube 100mm x 100mm x 100mm for compressive strength and 40mm x 40mm x 160mm for flexural strength. Morphology test was conducted by using Scanning electron microscopic (SEM) were done after testing compressive strength test. The concrete sample were cured for day 3, 7 and 28 before testing. Results compressive strength and flexural strength of rubber mortar shown improved compare to normal mortar.

Polymer concrete reinforced with recycled-tire fibers: Mechanical properties

NASA Astrophysics Data System (ADS)

Martínez-Cruz, E.; Martínez-Barrera, G.; Martínez-López, M.

2013-06-01

Polymer Concrete was reinforced with recycled-tire fibers in order to improve the compressive and flexural strength. Polymer concrete specimens were prepared with 70% of silicious sand, 30% of polyester resin and various fiber concentrations (0.3, 0.6, 0.9 and 1.2 vol%). The results show increment of 50% in average of the compressive and flexural strength as well as on the deformation when adding 1.2 vol% of recycled-fibers.

Effect of fatigue protocols on flexural strength of lithium disilicate bars with clamped-ends.

PubMed

de Pinho Barcellos, Aline Serrado; Marinho, Caroline Cotes; Miranda, Jean Soares; Amaral, Marina; Shiino, Marcos Yutaka; Kimpara, Estevão Tomomitsu

2018-05-01

The aim of this study was compare the effect of two in vitro ageing protocols to intraoral aging on the flexural strength of a lithium disilicate (LD) ceramic bars with clamped ends. After polishing and crystallization, the both ends of the bars were cemented to a metallic device and subjected to mechanical cycling, thermomechanical cycling, or intraoral ageing. Ten volunteers used an intraoral device - similar to an occlusal splint with a balanced contact condition on the occlusal surface of the ceramic bar - during 8 h night time / 30 days. Both in vitro and intraoral ageing decreased the flexural residual strength of LD, with the lowest values obtained after intraoral ageing. Thus, the in vitro ageing protocols tested in this study revealed to be less deleterious than intraoral ageing of LD. Copyright © 2018. Published by Elsevier Ltd.

Low-temperature mechanical properties of glass/epoxy laminates

DOE Office of Scientific and Technical Information (OSTI.GOV)

Reed, R. P.; Madhukar, M.; Thaicharoenporn, B.

2014-01-27

Selected mechanical properties of glass/epoxy laminate candidates for use in the electrical turn and ground insulation of the ITER Central solenoid (CS) modules were measured. Short-beam shear and flexural tests have been conducted on various E-glass cloth weaves/epoxy laminates at 295 and 77 K. Types of glass weave include 1581, 7500, 7781, and 38050, which represent both satin and plain weaves. The epoxy, planned for use for vacuum-pressure impregnation of the CS module, consists of an anhydride-cured bisphenol F resin system. Inter-laminar shear strength, flexural elastic modulus, and flexural strength have been measured. The data indicate that these properties aremore » dependent on the volume percent of glass. Short-beam shear strength was measured as a function of the span-to-thickness ratio for all laminates at 77 K. Comprehensive fractography was conducted to obtain the failure mode of each short-beam shear test sample.« less

Low-temperature mechanical properties of glass/epoxy laminates

NASA Astrophysics Data System (ADS)

Reed, R. P.; Madhukar, M.; Thaicharoenporn, B.; Martovetsky, N. N.

2014-01-01

Selected mechanical properties of glass/epoxy laminate candidates for use in the electrical turn and ground insulation of the ITER Central solenoid (CS) modules were measured. Short-beam shear and flexural tests have been conducted on various E-glass cloth weaves/epoxy laminates at 295 and 77 K. Types of glass weave include 1581, 7500, 7781, and 38050, which represent both satin and plain weaves. The epoxy, planned for use for vacuum-pressure impregnation of the CS module, consists of an anhydride-cured bisphenol F resin system. Inter-laminar shear strength, flexural elastic modulus, and flexural strength have been measured. The data indicate that these properties are dependent on the volume percent of glass. Short-beam shear strength was measured as a function of the span-to-thickness ratio for all laminates at 77 K. Comprehensive fractography was conducted to obtain the failure mode of each short-beam shear test sample.

Characteristics and porcelain bond strength of (Ti,Al)N coating on dental alloys.

PubMed

Chung, Kwok-Hung; Duh, Jeng-Gong; Shin, Daehwan; Cagna, David R; Cronin, Robert J

2002-01-01

The effect of a novel titanium-aluminum nitride film, or (Ti,Al)N film, on the bond strength between a dental porcelain and two nickel-based dental alloy substrates was investigated. A thin layer of (Ti,Al)N film was deposited on flat metal samples using a reactive radio-frequency sputtering method. A uniform thickness of porcelain was applied to the film- coated metal samples. Metal-ceramic specimens were subjected to three-point bending, and failure loads were recorded. Bond strengths between the porcelain and (Ti,Al)N-coated metal alloys ranged from 159.0 +/- 11.7 N to 278.0 +/- 12.3 N. These values were significantly greater (p< 0.05) than bond strengths recorded for control samples that did not incorporate the (Ti,Al)N film. An electron probe microanalyzer with a line profile mode was used to characterize the interface between the (Ti,Al)N film and the porcelain. Results of this investigation suggest that the (Ti,Al)N film (1) increases the flexural bond strength between dental porcelain and nickel-based alloy substrates by permitting elemental diffusion, (2) interferes with the surface oxide formation that characteristically originates from the nickel-based metal alloy substrate, and (3) provides an appropriate oxide layer for porcelain application. Copyright 2002 Wiley Periodicals, Inc. J Biomed Mater Res (Appl Biomater) 63: 516-521, 2002

Fabrication and characterisation of a novel biomimetic anisotropic ceramic/polymer-infiltrated composite material.

PubMed

Al-Jawoosh, Sara; Ireland, Anthony; Su, Bo

2018-04-10

To fabricate and characterise a novel biomimetic composite material consisting of aligned porous ceramic preforms infiltrated with polymer. Freeze-casting was used to fabricate and control the microstructure and porosity of ceramic preforms, which were subsequently infiltrated with 40-50% by volume UDMA-TEGDMA polymer. The composite materials were then subjected to characterisation, namely density, compression, three-point bend, hardness and fracture toughness testing. Samples were also subjected to scanning electron microscopy and computerised tomography (Micro-CT). Three-dimensional aligned honeycomb-like ceramic structures were produced and full interpenetration of the polymer phase was observed using micro-CT. Depending on the volume fraction of the ceramic preform, the density of the final composite ranged from 2.92 to 3.36g/cm 3 , compressive strength ranged from 206.26 to 253.97MPa, flexural strength from 97.73 to 145.65MPa, hardness ranged from 1.46 to 1.62GPa, and fracture toughness from 3.91 to 4.86MPam 1/2 . Freeze-casting provides a novel method to engineer composite materials with a unique aligned honeycomb-like interpenetrating structure, consisting of two continuous phases, inorganic and organic. There was a correlation between the ceramic fraction and the subsequent, density, strength, hardness and fracture toughness of the composite material. Copyright © 2018 The Academy of Dental Materials. Published by Elsevier Inc. All rights reserved.

Effects of thermal cycling on surface roughness, hardness and flexural strength of polymethylmethacrylate and polyamide denture base resins.

PubMed

Ayaz, Elif Aydoğan; Bağış, Bora; Turgut, Sedanur

2015-10-16

The purpose of this study was to evaluate the effects of thermal cycling on the surface roughness, hardness and flexural strength of denture resins. Polyamide (PA; Deflex and Valplast) and polymethylmethacrylate (PMMA; QC-20 and Acron MC) denture materials were selected. A total of 180 specimens were fabricated and then divided into 3 groups. The first group (group 1) acted as a control and was not thermocycled. The second group (group 2) was subjected to thermocycling for 10,000 cycles in artificial saliva and 5,000 cycles in distilled water. The last group (group 3) was thermocycled for 20,000 cycles in artificial saliva and 10,000 cycles in distilled water. The surface roughness were measured with a profilometer. The hardness of the resins were measured with a Vickers Hardness Tester using a 100-gf load. The flexural strength test was performed using the universal test machine with a crosshead speed of 5 mm/min. Data were analyzed using statistical software. The results of the measurements in the 3 different tests were analyzed by Kruskal-Wallis test with Bonferroni correction. Multiple comparisons were made by Conover and Wilcoxon tests. There was a significant difference between the PMMA and PA groups in terms of surface roughness, hardness and transverse strength before and after thermal cycling (p<0.001). Thermal cycling did not change the surface roughness, hardness and flexural strength values of either the PMMA or PA group (p>0.001).

Fracture behavior of glass fiber reinforced polymer composite

DOE Office of Scientific and Technical Information (OSTI.GOV)

Avci, A.; Arikan, H.; Akdemir, A

2004-03-01

Chopped strand glass fiber reinforced particle-filled polymer composite beams with varying notch-to-depth ratios and different volume fractions of glass fibers were investigated in Mode I fracture using three-point bending tests. Effects of polyester resin content and glass fiber content on fracture behavior was also studied. Polyester resin contents were used 13.00%%, 14.75%, 16.50%, 18.00% and 19.50%, and glass fiber contents were 1% and 1.5% of the total weight of the polymer composite system. Flexural strength of the polymer composite increases with increase in polyester and fiber content. The critical stress intensity factor was determined by using several methods such asmore » initial notch depth method, compliance method and J-integral method. The values of K{sub IC} obtained from these methods were compared.« less

Effect of Electrospun Nanofibers on the Short Beam Strength of Laminated Fiberglass Composite

NASA Astrophysics Data System (ADS)

Shinde, Dattaji K.

High specific modulus and strength are the most desirable properties for the material used in structural applications. Composite materials exhibit these properties and over the last decade, their usage has increased significantly, particularly in automotive, defense, and aerospace applications. The major cause of failures in composite laminates is due to delaminations. Delamination in composite laminates can occur due to fatigue, low velocity impact and other loadings modes. Conventional methods like "through-the-thickness stitching" or "Z-Pinning" have limitations for improving flexural and interlaminar properties in woven composites due to the fact that while improving interlaminar properties, the presence of stitches or Z pins affects in-plane properties. This study investigates the flexural behavior of fiberglass composites interleaved with non-woven Tetra Ethyl Orthosilicate (TEOS) electrsopsun nanofibers (ENFs). TEOS ENFs were manufactured using an electrospinning technique and then sintered. Nanoengineered beams were fabricated by interleaving TEOS ENFs between the laminated fiberglass composites to improve the flexural properties. TEOS ENFs, resin film, and failed fiberglass laminated composites with and without nanofibers were characterized using SEM Imaging and ASTM standard testing methods. A hybrid composite was made by interleaving a non-woven sheet of TEOS ENFs between the fiberglass laminates with additional epoxy resin film and fabricated using the out of autoclave vacuum bagging method. Four commonly used stacking sequences of fiberglass laminates with and without nanofibers were used to study the progressive failure and deformation mechanics under flexural loadings. The experimental study has shown significant improvements in short beam strength and strain energy absorption in the nanoengineered laminated fiberglass composites before complete failure. The modes were investigated by performing detailed fractographic examination of failed specimens. Experimental results were validated by developing a detailed three dimensional finite element model. Results of the progressive deformation and damage mechanics from the finite element model agreed well with the experimental results. Overall, nanoengineered beams showed improvement in the short beam strength and 30 % improvement in energy absorption as compared to a fiberglass beam without the presence of nanofibers.

Steel Fibers Reinforced Concrete Pipes - Experimental Tests and Numerical Simulation

NASA Astrophysics Data System (ADS)

Doru, Zdrenghea

2017-10-01

The paper presents in the first part a state of the art review of reinforced concrete pipes used in micro tunnelling realised through pipes jacking method and design methods for steel fibres reinforced concrete. In part two experimental tests are presented on inner pipes with diameters of 1410mm and 2200mm, and specimens (100x100x500mm) of reinforced concrete with metal fibres (35 kg / m3). In part two experimental tests are presented on pipes with inner diameters of 1410mm and 2200mm, and specimens (100x100x500mm) of reinforced concrete with steel fibres (35 kg / m3). The results obtained are analysed and are calculated residual flexural tensile strengths which characterise the post-cracking behaviour of steel fibres reinforced concrete. In the third part are presented numerical simulations of the tests of pipes and specimens. The model adopted for the pipes test was a three-dimensional model and loads considered were those obtained in experimental tests at reaching breaking forces. Tensile stresses determined were compared with mean flexural tensile strength. To validate tensile parameters of steel fibres reinforced concrete, experimental tests of the specimens were modelled with MIDAS program to reproduce the flexural breaking behaviour. To simulate post - cracking behaviour was used the method σ — ε based on the relationship stress - strain, according to RILEM TC 162-TDF. For the specimens tested were plotted F — δ diagrams, which have been superimposed for comparison with the similar diagrams of experimental tests. The comparison of experimental results with those obtained from numerical simulation leads to the following conclusions: - the maximum forces obtained by numerical calculation have higher values than the experimental values for the same tensile stresses; - forces corresponding of residual strengths have very similar values between the experimental and numerical calculations; - generally the numerical model estimates a breaking force greater than that obtained in the experimental tests. Experimental and numerical studies are used to establish the residual characteristic flexural tensile strength minimum guaranteed and limits of applicability of concrete pipes reinforced with steel fibres used in various field and loading situations.

Effect of repair resin type and surface treatment on the repair strength of heat-polymerized denture base resin.

PubMed

Alkurt, Murat; Yeşil Duymuş, Zeynep; Gundogdu, Mustafa

2014-01-01

Acrylic resin denture fracture is common in prosthodontic practice. When fractured denture bases are repaired, recurrent fractures frequently occur at the repair surface interface or adjacent areas. The purpose of this study was to evaluate the effect of different surface treatments on the flexural strength of the acrylic resin denture base repaired with heat-polymerized acrylic resin, autopolymerizing resin, and light-polymerized acrylic resin. Ninety-six specimens of heat-polymerized acrylic resin were prepared according to the American Dental Association Specification No. 12 (65.0 × 10.0 × 2.5 mm) and sectioned into halves to create a repair gap (3.0 × 10 × 2.5 mm). The sectioned specimens were divided into 3 groups according to their repair materials. The specimens from each group were divided into 4 subgroups according to their surface treatments: a control group without any surface treatment; an experimental group treated with methyl methacrylate monomer (MMA group); an experimental group treated with airborne-particle abrasion with aluminum oxide particles of 250-μm particle size (abrasion group); and an experimental group treated with erbium:yttrium-aluminum-garnet laser (laser group). After the surface treatments, the 3 materials were placed into the repair gaps and then polymerized. After all of the specimens had been ground and polished, they were stored in distilled water at 37°C for 1 week and subjected to a 3-point bend test. Data were analyzed with a 2-way analysis of variance, and the Tukey honestly significant difference test was performed to identify significant differences (α=.05). The effects of the surface treatments and repair resins on the surface of the denture base resin were examined with scanning electron microscopy. Significant differences were found among the groups in terms of repair resin type (P<.001). All surface-treated specimens had higher flexural strength than controls, except the surface treated with the methyl methacrylate in the heat-polymerized group. A significant difference between the control and abrasion groups (P=.013) was found. The scanning electron microscopy observations showed that the application of surface treatments modified the surface of the denture base resin. The repair procedure with heat-polymerized resin exhibited significantly higher flexural strength than that of the autopolymerized and light-polymerized resins. In addition, the airborne-particle abrasion with aluminum oxide particles of 250-μm particle size improved the flexural strength of the specimens tested. Copyright © 2014 Editorial Council for the Journal of Prosthetic Dentistry. Published by Mosby, Inc. All rights reserved.

Mechanical properties of steel/kenaf (hybrid) fibers added into concrete mixtures

NASA Astrophysics Data System (ADS)

Baarimah, A. O.; Syed Mohsin, S. M.

2018-04-01

This paper investigates the potential advantages of adding hybrid steel-kenaf fibers to concrete mixtures. Compression and flexural test were conducted on six concrete mixtures at 28 days to investigate the mechanical properties of the concrete. The experimental work consists of six concrete mixtures, in which the first mixture was a control mixture without adding any fiber. The following five concrete mixtures contain a total of 1% of volume fraction for steel, kenaf and a mixture of steel-kenaf (hybrid) fibers. Three ratios were considered for hybrid fibers with the ratios of 0.25/0.75, 0.5/0.5 and 0.75/0.25 for steel and kenaf fibers, respectively. From the investigation, it was observed that fibers have minimal effect on compressive strength of the concrete. However, the findings suggest promising improvement on the flexural strength of the concrete added with hybrid fiber (up to 86%) as well as manages to change the mode of failure of the beam from brittle to a more ductile manner.

Hierarchical flexural strength of enamel: transition from brittle to damage-tolerant behaviour

PubMed Central

Bechtle, Sabine; Özcoban, Hüseyin; Lilleodden, Erica T.; Huber, Norbert; Schreyer, Andreas; Swain, Michael V.; Schneider, Gerold A.

2012-01-01

Hard, biological materials are generally hierarchically structured from the nano- to the macro-scale in a somewhat self-similar manner consisting of mineral units surrounded by a soft protein shell. Considerable efforts are underway to mimic such materials because of their structurally optimized mechanical functionality of being hard and stiff as well as damage-tolerant. However, it is unclear how different hierarchical levels interact to achieve this performance. In this study, we consider dental enamel as a representative, biological hierarchical structure and determine its flexural strength and elastic modulus at three levels of hierarchy using focused ion beam (FIB) prepared cantilevers of micrometre size. The results are compared and analysed using a theoretical model proposed by Jäger and Fratzl and developed by Gao and co-workers. Both properties decrease with increasing hierarchical dimension along with a switch in mechanical behaviour from linear-elastic to elastic-inelastic. We found Gao's model matched the results very well. PMID:22031729

Residual stress in glass: indentation crack and fractography approaches.

PubMed

Anunmana, Chuchai; Anusavice, Kenneth J; Mecholsky, John J

2009-11-01

To test the hypothesis that the indentation crack technique can determine surface residual stresses that are not statistically significantly different from those determined from the analytical procedure using surface cracks, the four-point flexure test, and fracture surface analysis. Soda-lime-silica glass bar specimens (4 mm x 2.3 mm x 28 mm) were prepared and annealed at 650 degrees C for 30 min before testing. The fracture toughness values of the glass bars were determined from 12 specimens based on induced surface cracks, four-point flexure, and fractographic analysis. To determine the residual stress from the indentation technique, 18 specimens were indented under 19.6N load using a Vickers microhardness indenter. Crack lengths were measured within 1 min and 24h after indentation, and the measured crack lengths were compared with the mean crack lengths of annealed specimens. Residual stress was calculated from an equation developed for the indentation technique. All specimens were fractured in a four-point flexure fixture and the residual stress was calculated from the strength and measured crack sizes on the fracture surfaces. The results show that there was no significant difference between the residual stresses calculated from the two techniques. However, the differences in mean residual stresses calculated within 1 min compared with those calculated after 24h were statistically significant (p=0.003). This study compared the indentation technique with the fractographic analysis method for determining the residual stress in the surface of soda-lime-silica glass. The indentation method may be useful for estimating residual stress in glass.

Residual stress in glass: indentation crack and fractography approaches

PubMed Central

Anunmana, Chuchai; Anusavice, Kenneth J.; Mecholsky, John J.

2009-01-01

Objective To test the hypothesis that the indentation crack technique can determine surface residual stresses that are not statistically significantly different from those determined from the analytical procedure using surface cracks, the four-point flexure test, and fracture surface analysis. Methods Soda-lime-silica glass bar specimens (4 mm × 2.3 mm × 28 mm) were prepared and annealed at 650 °C for 30 min before testing. The fracture toughness values of the glass bars were determined from 12 specimens based on induced surface cracks, four-point flexure, and fractographic analysis. To determine the residual stress from the indentation technique, 18 specimens were indented under 19.6 N load using a Vickers microhardness indenter. Crack lengths were measured within 1 min and 24 h after indentation, and the measured crack lengths were compared with the mean crack lengths of annealed specimens. Residual stress was calculated from an equation developed for the indentation technique. All specimens were fractured in a four-point flexure fixture and the residual stress was calculated from the strength and measured crack sizes on the fracture surfaces. Results The results show that there was no significant difference between the residual stresses calculated from the two techniques. However, the differences in mean residual stresses calculated within 1 min compared with those calculated after 24 h were statistically significant (p=0.003). Significance This study compared the indentation technique with the fractographic analysis method for determining the residual stress in the surface of soda-lime silica glass. The indentation method may be useful for estimating residual stress in glass. PMID:19671475

Effect of airborne-particle abrasion and aqueous storage on flexural properties of fiber-reinforced dowels.

PubMed

Petrie, Cynthia S; Walker, Mary P

2012-06-01

A great range of clinical failures have been observed with fiber-reinforced dowels, often attributed to fracture or bending of the dowels. This study investigated flexural properties of fiber-reinforced dowels, with and without airborne-particle abrasion, after storage in aqueous environments over time. Scanning electron microscopy (SEM) was used to analyze the mode of failure of dowels. Two dowel systems (ParaPost Fiber Lux and FibreKor) were evaluated. Ten dowels of each system were randomly assigned to one of six experimental groups: 1--control, dry condition; 2--dowels airborne-particle abraded and then stored dry; 3--dowels stored for 24 hours in aqueous solution at 37°C; 4--dowels airborne-particle abraded followed by 24-hour aqueous storage at 37°C; 5--dowels stored for 30 days in aqueous solution at 37°C; 6--dowels airborne-particle abraded followed by 30-day aqueous storage at 37°C. Flexural strength and flexural modulus were tested for all groups according to American Society of Testing and Materials (ASTM) standard D4476. One failed dowel from each group was randomly selected to be evaluated with SEM equipped with energy dispersive spectroscopy (EDS) to characterize the failure pattern. One intact dowel of each system was also analyzed with SEM and EDS for baseline information. Mean flexural modulus and strength of ParaPost Fiber Lux dowels across all conditions were 29.59 ± 2.89 GPa and 789.11 ± 89.88 MPa, respectively. Mean flexural modulus and strength of FibreKor dowels across all conditions were 25.58 ± 1.48 GPa and 742.68 ± 89.81 MPa, respectively. One-way ANOVA and a post hoc Dunnett's t-test showed a statistically significant decrease in flexural strength as compared to the dry control group for all experimental groups stored in water, for both dowel systems (p < 0.05). Flexural modulus for both dowel systems showed a statistically significant decrease only for dowels stored in aqueous solutions for 30 days (p < 0.05). Airborne-particle abrasion did not have an effect on flexural properties for either dowel system (p > 0.05). SEM and EDS analyses revealed differences in composition and failure mode of the two dowel systems. Failed dowels of each system revealed similar failure patterns, irrespective of the experimental group. Aqueous storage had a negative effect on flexural properties of fiber-reinforced dowels, and this negative effect appeared to increase with longer storage times. The fiber/resin matrix interface was the weak structure for the dowel systems tested. © 2012 by the American College of Prosthodontists.

Numerical Analysis on the High-Strength Concrete Beams Ultimate Behaviour

NASA Astrophysics Data System (ADS)

Smarzewski, Piotr; Stolarski, Adam

2017-10-01

Development of technologies of high-strength concrete (HSC) beams production, with the aim of creating a secure and durable material, is closely linked with the numerical models of real objects. The three-dimensional nonlinear finite element models of reinforced high-strength concrete beams with a complex geometry has been investigated in this study. The numerical analysis is performed using the ANSYS finite element package. The arc-length (A-L) parameters and the adaptive descent (AD) parameters are used with Newton-Raphson method to trace the complete load-deflection curves. Experimental and finite element modelling results are compared graphically and numerically. Comparison of these results indicates the correctness of failure criteria assumed for the high-strength concrete and the steel reinforcement. The results of numerical simulation are sensitive to the modulus of elasticity and the shear transfer coefficient for an open crack assigned to high-strength concrete. The full nonlinear load-deflection curves at mid-span of the beams, the development of strain in compressive concrete and the development of strain in tensile bar are in good agreement with the experimental results. Numerical results for smeared crack patterns are qualitatively agreeable as to the location, direction, and distribution with the test data. The model was capable of predicting the introduction and propagation of flexural and diagonal cracks. It was concluded that the finite element model captured successfully the inelastic flexural behaviour of the beams to failure.

Dynamic Ring-on-Ring Equibiaxial Flexural Strength of Borosilicate Glass

DTIC Science & Technology

2010-01-01

Flexure Strength and Dynamic Fatigue of Soda – Lime – Silica Float Glass ,’’ J. Am. Ceram. Soc., 85 [7] 1777–1782 (2002). 9. A. Borger, R. Danzer, and P...on the Strength and Fatigue Behavior of Indented Soda – Lime Glass ,’’ Glass Technol., 32 [2] 51– 54 (1991). 16. J. J. Jr. Mecholsky, S. W. Freiman, and... Soda – Lime Glass Rods by a Statistical Approach,’’ J. Eur. Ceram. Soc., 11 341–346 (1993). 28. S. R. Choi and J. A. Salem, ‘‘Ultra-fast Fracture

Effect of Curing Period on Properties of Steel and Polypropylene Fibre Reinforced Ultra-High Performance Concrete

NASA Astrophysics Data System (ADS)

Smarzewski, Piotr

2017-10-01

This study has investigated the effect of curing period on the mechanical properties of straight polypropylene and hooked-end steel fibre reinforced ultra-high performance concrete (UHPC). Various physical properties are evaluated, i.e. absorbability, apparent density and open porosity. Compressive strength, tensile splitting strength, flexural strength and modulus of elasticity were determined at 28, 56 and 730 days. Comparative strength development of fibre reinforced mixes at 0.5%, 1%, 1.5% and 2% by volume fractions in relation to the mix without fibres was observed. Good correlations between the compressive strength and the modulus of elasticity are established. Steel and polypropylene fibres significantly increased the compressive strength, tensile splitting strength, flexural strength and modulus of elasticity of UHPC after two years curing period when fibre content volume was at least 1%. It seems that steel fibre reinforced UHPC has better properties than the polypropylene fibre reinforced UHPC.

Ultimate Strength of Ferro-Geopolymer Composite Built-Up I Joist

NASA Astrophysics Data System (ADS)

Vipin, K. T.; Ganesan, N.; Indira, P. V.

2017-07-01

An experimental study was carried out to study the behaviour of ferro-geopolymer built-up I- joist with different types of mesh reinforcements under flexure. Mesh reinforcements considered in this study are square welded meshes, square woven meshes and hexagonal meshes. First crack load as well as ultimate strength of ferro-geopolymer built-up I-joist in flexure was obtained. An attempt was made to predict the first crack load and ultimate moment capacity of the specimen.

Strengthening of oxidation resistant materials for gas turbine applications. [treatment of silicon ceramics for increased flexural strength and impact resistance

NASA Technical Reports Server (NTRS)

Kirchner, H. P.

1974-01-01

Silicon nitride and silicon carbide ceramics were treated to form compressive surface layers. On the silicon carbide, quenching and thermal exposure treatments were used, and on the silicon nitride, quenching, carburizing, and a combination of quenching and carburizing were used. In some cases substantial improvements in impact resistance and/or flexural strength were observed. The presence of compressive surface stresses was demonstrated by slotted rod tests.

Preparation and mechanical properties of carbon fiber reinforced hydroxyapatite/polylactide biocomposites.

PubMed

Shen, Lie; Yang, Hui; Ying, Jia; Qiao, Fei; Peng, Mao

2009-11-01

A novel biocomposite of carbon fiber (CF) reinforced hydroxyapatite (HA)/polylactide (PLA) was prepared by hot pressing a prepreg which consisting of PLA, HA and CF. The prepreg was manufactured by solvent impregnation process. Polymer resin PLA dissolved with chloroform was mixed with HA. After reinforcement CF bundle was impregnated in the mixture, the solvent was dried completely and subsequently hot-pressed uniaxially under a pressure of 40 MPa at 170 degrees C for 20 min. A study was carried out to investigate change in mechanical properties of CF/HA/PLA composites before and after degradation in vitro. The composites have excellent mechanical properties. A peak showed in flexural strength, flexural modulus and shear strength aspects, reaching up 430 MPa, 22 GPa, 212 MPa, respectively, as the HA content increased. Degraded in vitro for 3 months, the flexural strength and flexural modulus of the CF/HA/PLA fell 13.2% and 5.4%, respectively, while the shear strength of the CF/HA/PLA composites remains at the 190 MPa level. The SEM photos showed that there were gaps between the PLA matrix and CF after degradation. Water uptake increased to 5%, but the mass loss rate was only 1.6%. The pH values of the PBS dropped less than 0.1. That's because the alkaline of HA neutralize the acid degrades from PLA, which can prevent the body from the acidity harm.

Stress-Strain Behavior of Cementitious Materials with Different Sizes

PubMed Central

Zhou, Jikai; Qian, Pingping; Chen, Xudong

2014-01-01

The size dependence of flexural properties of cement mortar and concrete beams is investigated. Bazant's size effect law and modified size effect law by Kim and Eo give a very good fit to the flexural strength of both cement mortar and concrete. As observed in the test results, a strong size effect in flexural strength is found in cement mortar than in concrete. A modification has been suggested to Li's equation for describing the stress-strain curve of cement mortar and concrete by incorporating two different correction factors, the factors contained in the modified equation being established empirically as a function of specimen size. A comparison of the predictions of this equation with test data generated in this study shows good agreement. PMID:24744688

Effects of silicon coating on bond strength of two different titanium ceramic to titanium.

PubMed

Ozcan, Isil; Uysal, Hakan

2005-08-01

This study investigated the effect of silicon coating (SiO2) by magnetron sputtering on bond strength of two different titanium ceramics to titanium. Sixty cast titanium specimens were prepared following the protocol ISO 9693. Titanium specimens were divided into two test and control groups with 15 specimens in each. Test groups were silicon coated by the magnetron sputtering technique. Two titanium ceramics (Triceram and Duceratin) were applied on both test (coated) and control (uncoated) metal specimens. The titanium-ceramic specimens were subjected to a three point flexural test. The groups were compared for their bond strength. SEM and SEM/EDS analyses were performed on the delaminated titanium surfaces to ascertain bond failure. The mean bond strength of Ti-Duceratin, Ti-Triceram, Si-coated Ti-Duceratin and Si-coated Ti-Triceram were 17.22+/-2.43, 23.31+/-3.18, 23.21+/-3.81 and 24.91+/-3.70 MPa, respectively. While the improvement in bond strength was 30% for Duceratin, it was statistically insignificant for Triceram. An adhesive mode of failure was observed in the Duceratin control group. In the silicoated Duceratin specimen, the bonded ceramic boundaries were wider but less than in the silicoated Triceram specimen. In the coated Triceram specimen, the ceramic retained areas were frequent and the failure mode was generally cohesive. Silicon coating was significantly effective in both preventing titanium oxide layer formation and in improving bond strength for Duceratin. However, it was of less value for Triceram.

Development of polyphenylquinoxaline graphite composites

NASA Technical Reports Server (NTRS)

Hoggatt, J. T.; Hergenrother, P. M.; Shdo, J. G.

1973-01-01

The potential of polyphenylquinoxaline (PPQ)/graphite composites to serve as structural material at 316 C (600 F)has been demonstrated using a block copolymer, BlCo(13), PPQ derivative. Initially, thirteen polyphenylquinoxalines were evaluated. From this work, four candidate polymers were selected for preliminary evaluation as matrices for HMS graphite fiber reinforced composites. The preliminary composite evaluation enabled selection of one of the four polymers for advanced composite preparation and testing. Using an experimentally established cure schedule for each of the four polymers, preliminary laminates of 50% resin volume content, prepared without postcure, were tested for flexure strength and modulus, interlaminar shear strength (short beam), and tensile strength and modulus at ambient temperature. A block copolymer (Bl Co 13) derived from one mole p-bis (phenylglyoxalyl) benzene, one fourth mole 3,3'-diaminobenzidine and three-fourths mole 3,3', 4,4'-tetraminobenzophenone was selected for extensive study. Tensile, flexural, and interlaminar shear values were obtained after aging and testing postcured BlCo(13) laminates at 316 C (600 F). The potential of PPQ/graphite laminates to serve as short term structural materials at temperatures up to 371 C (700 F) was demonstrated through weight loss experiments.

Solid Oxide Fuel Cell Seal Glass - BN Nanotubes Composites

NASA Technical Reports Server (NTRS)

Bansal, Narottam P.; Choi, Sung R.; Hurst, Janet B.; Garg, Anita

2005-01-01

Solid oxide fuel cell seal glass G18 composites reinforced with approx.4 weight percent of BN nanotubes were fabricated via hot pressing. Room temperature strength and fracture toughness of the composite were determined by four-point flexure and single edge V-notch beam methods, respectively. The strength and fracture toughness of the composite were higher by as much as 90% and 35%, respectively, than those of the glass G18. Microscopic examination of the composite fracture surfaces using SEM and TEM showed pullout of the BN nanotubes, similar in feature to fiber-reinforced ceramic matrix composites with weak interfaces. Other mechanical and physical properties of the composite will also be presented.

Effect of unground oil palm ash as mixing ingredient towards properties of concrete

NASA Astrophysics Data System (ADS)

Sulaiman, M. A.; Muthusamy, K.; Mat Aris, S.; Rasid, M. H. Mohd; Paramasivam, R.; Othman, R.

2018-04-01

Malaysia being one of the world largest palm oil producers generates palm oil fuel ash (POFA), a by-product in increasing quantity. This material which usually disposed as solid waste causes pollution to the environment. Success in converting this waste material into benefitting product would reduce amount of waste disposed and contributes towards cleaner environment. This research explores the potential of unground oil palm ash being used as partial sand replacement in normal concrete production. Experimental work has been conducted to determine the workability, compressive strength and flexural strength of concrete when unground oil palm ash is added as partial sand replacement. A total of five mixes containing various percentage of oil palm ash, which are 0%, 5%, 10%, 15% and 20% have been prepared. All specimens were water cured until the testing date. The slump test, compressive strength test and flexural strength test was conducted. The findings show that mix produced using 10% of palm oil fuel ash exhibit higher compressive strength and flexural strength as compared to control specimen. Utilization of unground oil palm ash as partial sand replacement would be able to reduce dependency of construction industry on natural sand supply and also as one of the solution to reuse palm oil industry waste.

[Effect of sintering temperature on mechanical properties of dental zirconia toughened alumina ceramics].

PubMed

Fan, Jiang-Yuan; Lin, Ting-Ting; Hu, Fang-Xuan; Zheng, Rui-Bin; Fan, Fan; Ma, Jian-Feng

2017-04-01

To investigate the effect of sintering temperature on mechanical properties of dental zirconia toughened alumina (ZTA) ceramics prepared by gel-casting technique. The samples prepared by gel-casting were sintered at 1100, 1200, 1250, 1300 and 1400degrees centigrade for each group. The flexural strength, fracture toughness, Vickers hardness and brittleness index were obtained and microscopic morphology of each group was observed under scanning electron microscope (SEM). The data were statistically analyzed using SPSS 19.0 software package. The flexural strength, fracture toughness and Vickers hardness increased with the increasing sintering temperature during 1100~1400degrees centigrade. The lowest brittleness index (0.74±0.16) μm -1/2 was observed in group sintered at 1200degrees centigrade and the highest (2.76±0.14) μm -1/2 was at 1400degrees centigrade (P<0.05), while the flexural strength of these two groups was (46.89±3.24) MPa and (349.64±54.72) MPa, respectively. The ZTA dental ceramics exhibit good machinability with proper sintering temperature (1200degrees centigrade) and the strength meets the requirement of clinical application.

Coating glass-ionomer cements with a nanofilled resin.

PubMed

Bonifácio, Clarissa Calil; Werner, Arie; Kleverlaan, Cornelis Johanes

2012-12-01

The objective of this study was to investigate the effect of a nanofilled resin coat on the flexural strength (FS) and the early wear (after 50,000 and 200,000 cycles) of the glass-ionomer cements Fuji IX GP Extra (FIXE) and Ketac Molar Aplicap (KM). Specimens were prepared and half of them were coated with G-Coat plus. The uncoated specimens were used as controls. Flexural strength (n = 10) was evaluated after 24 h using a 3-point bending test on a universal testing machine (ISO 9917-2). Wear (n = 20) was evaluated after 50,000 and 200,000 cycles using the ACTA wear machine. One-way, two-way ANOVA and Tukey post-hoc tests were used to analyze differences in FS and wear. For FIXE the coat significantly increased the FS and the wear along the two time spans. KM did not show a significant difference in FS with the coat. Improvements in wear were observed only after 50,000 cycles. Based on these laboratory results, it is concluded that G-coat Plus is indicated in association with GP IX Extra with the aim to improve the mechanical properties of the former. However, this study is limited to a short-term observation.

Ethanol postpolymerization treatment for improving the biocompatibility of acrylic reline resins.

PubMed

Neves, Cristina B; Lopes, Luís P; Ferrão, Helena F; Miranda, Joana P; Castro, Matilde F; Bettencourt, Ana F

2013-01-01

To evaluate the effect of postpolymerization treatment based on ethanol-aqueous solutions on the residual monomer (RM) content, flexural strength, microhardness, and cytotoxicity of hard chairside reline resins (Kooliner, Ufi Gel Hard). After polymerization, specimens were immersed in water, 20%, 50%, or 70% ethanol solutions at 23°C or 55°C for 10 minutes. Controls were left untreated. HPLC was used for the determination of RM content. Specimens were submitted to Vickers microhardness and 3-point loading flexural strength tests. Cytotoxicity of resin eluates was determined on human fibroblasts by assessing cellular mitochondrial function and lactate dehydrogenase release. Higher concentrations of ethanol promoted lower RM content at 55°C in both materials. The mechanical properties were maintained after 50% and 20% ethanol treatments in Kooliner and Ufi Gel Hard, respectively. Specimens submitted to those treatments showed significant reduction on cytotoxicity compared to immersion in hot water, the treatment of choice in the recent literature. Immersion of relined dentures in specific ethanol solutions at 55°C for 10 minutes can be considered an effective postpolymerization treatment contributing to increase materials biocompatibility. The proposed protocol is expeditious and easy to achieve with simple equipment in a dental office.

Flexural strength of self compacting fiber reinforced concrete beams using polypropylene fiber: An experimental study

NASA Astrophysics Data System (ADS)

Lisantono, Ade; Praja, Baskoro Abdi; Hermawan, Billy Nouwen

2017-11-01

One of the methods to increase the tensile strength of concrete is adding a fiber material into the concrete. While to reduce a noise in a construction project, a self compacting concrete was a good choices in the project. This paper presents an experimental study of flexural behavior and strength of self compacting fiber reinforced concrete (RC) beams using polypropylene fiber. The micro monofilament polypropylene fibers with the proportion 0.9 kg/m3 of concrete weight were used in this study. Four beam specimens were cast and tested in this study. Two beams were cast of self compacting reinforced concrete without fiber, and two beams were cast of self compacting fiber reinforced concrete using polypropylene. The beams specimen had the section of (180×260) mm and the length was 2000 mm. The beams had simple supported with the span of 1800 mm. The longitudinal reinforcements were using diameter of 10 mm. Two reinforcements of Ø10 mm were put for compressive reinforcement and three reinforcements of Ø10 mm were put for tensile reinforcement. The shear reinforcement was using diameter of 8 mm. The shear reinforcements with spacing of 100 mm were put in the one fourth near to the support and the spacing of 150 mm were put in the middle span. Two points loading were used in the testing. The result shows that the load-carrying capacity of the self compacting reinforced concrete beam using polypropylene was a little bit higher than the self compacting reinforced concrete beam without polypropylene. The increment of load-carrying capacity of self compacting polypropylene fiber reinforced concrete was not so significant because the increment was only 2.80 % compare to self compacting non fiber reinforced concrete. And from the load-carrying capacity-deflection relationship curves show that both the self compacting polypropylene fiber reinforced concrete beam and the self compacting non fiber reinforced concrete beam were ductile beams.

A comparative study of progressive wear of four dental monolithic, veneered glass-ceramics.

PubMed

Zhang, Zhenzhen; Yi, Yuanping; Wang, Xuesong; Guo, Jiawen; Li, Ding; He, Lin; Zhang, Shaofeng

2017-10-01

This study evaluated the wear performance and wear mechanisms of four dental glass-ceramics, based on the microstructure and mechanical properties in the progressive wear process. Bar (N = 40, n = 10) and disk (N = 32, n = 8) specimens were prepared from (A) lithium disilicate glass-ceramic (LD), (B) leucite reinforced glass-ceramic (LEU), (C) feldspathic glass-ceramic (FEL), and (D) fluorapatite glass-ceramic (FLU). The bar specimens were tested for three-point flexural strength, hardness, fracture toughness and elastic modulus. The disk specimens paired with steatite antagonists were tested in a pin-on-disk tribometer with 10N up to 1000,000 wear cycles. The wear analysis of glass-ceramics was performed using a 3D profilometer after every 200,000 wear cycles. Wear loss of steatite antagonists was calculated by measuring the weight and density using sensitive balance and Archimedes' method. Wear morphologies and microstructures were analyzed by scanning electron microscopy (SEM). The crystalline phase compositions were determined using X-ray diffraction (XRD). One-way analysis of variance (ANOVA) was used to analyze the data. Multiple pair-wise comparison of means was performed by Tukey's post-hoc test. LD showed the highest fracture toughness, flexural strength, elastic modulus and crystallinity, followed by LEU and FEL, and FLU showed the lowest. However, the hardness of LD was lower than all the other three types of ceramics. For steatite antagonists, LD produced the least wear loss of antagonist, followed by LEU and FEL, and FLU had the most wear loss. For glass-ceramic materials, LD exhibited similar wear loss as LEU, but more than FLU and FEL did. Moreover, fracture occurred on the wear surface of FLU. In the progressive wear process, veneering porcelains showed better wear resistance but fluorapatite veneering porcelains appeared fracture surface. Monolithic lithium disilicate glass-ceramics with higher mechanical properties showed more wear loss, however, they did not fracture and produced less wear loss of antagonists. Copyright © 2017 Elsevier Ltd. All rights reserved.

Silicon carbide whisker-zirconia reinforced mullite and alumina ceramics

DOEpatents

Becher, Paul F.; Tiegs, Terry N.

1987-01-01

The flexural strength and/or fracture toughness of SiC whisker-reinforced composites utilizing mullite or alumina as the matrix material for the composite are increased by the addition of zirconia in a monoclinic or tetragonal phase to the matrix. The zirconia addition also provides for a lower hot-pressing temperature and increases the flexural strength and/or fracture toughness of the SiC whisker-reinforced composites over SiC whisker-reinforced composites of the similar matrix materials reinforced with similar concentrations of SiC whiskers.

The Effect of Mechanical Performance on PP Fiber to Polymer Mortar

NASA Astrophysics Data System (ADS)

Xie, Xinying; Kang, Xinnan; Jin, Yujie; Cai, Jingwei

2018-03-01

It introduces the purpose of of adding Polypropylene fiber. The paper The production process and test method of epoxy resin mortar with PP fiber are developed. The influence of PP fiber on mechanical properties of polymer mortar was studied in this paper, including the influence of PP fiber content on flexural strength, the ratio of flexural and compressive strength and so on. The experimental results are compared and analyzed. The reason is found, the conclusion of research is acquired.

Physical properties of a new sonically placed composite resin restorative material.

PubMed

Ibarra, Emily T; Lien, Wen; Casey, Jeffery; Dixon, Sara A; Vandewalle, Kraig S

2015-01-01

A new nanohybrid composite activated by sonic energy has been recently introduced as a single-step, bulk-fill restorative material. The purpose of this study was to compare the physical properties of this new composite to various other composite restorative materials marketed for posterior or bulk-fill placement. The following physical properties were examined: depth of cure, volumetric shrinkage, flexural strength, flexural modulus, fracture toughness, and percent porosity. A mean and standard deviation were determined per group. One-way ANOVA and Tukey's post hoc tests were performed per property (α = 0.05). Percent porosity was evaluated with a Kruskal-Wallis/Mann-Whitney test (α = 0.005). Significant differences were found between groups (P < 0.001) per test type. Compared to the other composite restorative materials, the new nanohybrid composite showed low shrinkage and percent porosity, moderate fracture toughness and flexural modulus, and high flexural strength. However, it also demonstrated a relatively reduced depth of cure compared to the other composites.

An experimental investigation into the behavior of concrete elements rerofitted with NSM composite strips at elevated temperatures

NASA Astrophysics Data System (ADS)

Namrou, Abdul Rahman

Near-surface-mounted (NSM) fiber reinforced polymer (FRP) is another strengthening alternative of externally bonded fiber reinforced polymers. NSM FRP is a promising alternative technology that has emerged for enhancing the strength capacity of concrete structures. Most laboratory researches have focused mainly on the overall member performance and/or the bonding performance of the NSM bars or strips. Limited research has focused on the effect of temperature exposure on NSM FRP performance. The results of an experimental program performed on forty-eight (48) concrete block specimen with NSM carbon-fiber reinforced polymer (CFRP) strengthening systems at elevated temperatures that reaches to 200°C [392°F] to investigate flexural performance. The effect of using two different adhesive systems (epoxy anchoring system) with manufacturer recommendation at ordinary and high temperature exposures is also studied. The adhesive was injected in a NSM groove size (25 mm [1 in] deep x 13 mm [0.5 in] wide) the width and depth of the groove were greater than 3 and 1.5 times the CFRP thickness and width, respectively. Test results show that the interfacial strength of the specimens bonded with the ordinary epoxy is maintained until 75°C [167°F] is reached, while the strength noticeably decreases with an increasing temperature above this limit. The specimens with the high-temperature epoxy preserve interfacial capacity up to 200°C [392°F] despite a trend of strength-decrease being observed. The failure of the test specimens is brittle irrespective of adhesive type. Interfacial damage is localized along the bond-line with the presence of hairline cracks that further develop when interfacial failure is imminent. This thesis also presents an experimental result concerning the bond performance of concrete-adhesive at elevated temperatures that reaches to 200°C [392°F] applied for three hours. Then, the concrete prisms were tested under three point flexural loading. The experimental program is comprised of seventy-two (72) specimens bonded with low viscosity, high viscosity adhesives and high-temperature adhesive and their comparative performance is of interest in the present investigation. Emphasis is placed on the residual capacity of the conditioned bond-concrete interface and corresponding failure mode. For high temperature exposure, it is shown that the high temperature laminated adhesive outperforms the high and low viscosity adhesives by remaining fairly consistent and allowing the strengthening system to remain effective for up to three hours of 200°C [392°F].

Flexural controls on late Neogene basin evolution in southern McMurdo Sound, Antarctica

NASA Astrophysics Data System (ADS)

Aitken, Alan R. A.; Wilson, Gary S.; Jordan, Thomas; Tinto, Kirsty; Blakemore, Hamish

2012-01-01

The basins of southern McMurdo Sound have evolved under the influence of lithospheric flexure induced by the loads of the Erebus Volcanic Province. To characterise these basins, it is important to investigate the lithosphere's flexural properties, and estimate their influence on basin architecture and evolution. Seismic and gravity data are used to constrain 3D forward modelling of the progressive development of accommodation space within the flexural basins. Elastic plate flexure was calculated for a range of effective elastic thicknesses (T e) from 0.5 to 25 km using a spectral method. Models with low, but nonzero, T e values (2 km < T e < 5 km) produce the best fit to the gravity data, although uncertainty is high due to inaccuracies in the Digital Elevation Model. The slopes of flexural horizons revealed in seismic reflection lines are consistent with this, indicating a T e of 2 km to 5 km, although the depths to these horizons are not consistent, perhaps due to a northwards slope, or step, in the pre-flexural surface. These results indicate that the lithospheric strength of southern McMurdo Sound is significantly less than estimates of the regional average (T e ~ 20 km). This low strength may reflect the weakening effects of the Terror Rift, and perhaps also the Discovery Accommodation Zone, a region of major transverse faulting. A low T e model (T e = 3) for southern McMurdo Sound predicts the development of two discrete flexural depressions, each 2-2.5 km deep. The predicted stratigraphy of the northern basin reflects flexure due to Ross Island, predominantly erupted since ca. 1.8 Ma. The predicted stratigraphy of the southern basin reflects more gradual flexure from ca. 10 Ma to ca. 2 Ma, due to the more dispersed volcanoes of the Discovery subprovince. Collectively, these two basins have the potential to preserve a remarkable stratigraphic record of Antarctic climate change through the late Neogene.

Reprint of: Flexural controls on late Neogene basin evolution in southern McMurdo Sound, Antarctica

NASA Astrophysics Data System (ADS)

Aitken, Alan R. A.; Wilson, Gary S.; Jordan, Tom; Tinto, Kirsty; Blakemore, Hamish

2012-10-01

The basins of southern McMurdo Sound have evolved under the influence of lithospheric flexure induced by the loads of the Erebus Volcanic Province. To characterise these basins, it is important to investigate the lithosphere's flexural properties, and estimate their influence on basin architecture and evolution. Seismic and gravity data are used to constrain 3D forward modelling of the progressive development of accommodation space within the flexural basins. Elastic plate flexure was calculated for a range of effective elastic thicknesses (Te) from 0.5 to 25 km using a spectral method. Models with low, but nonzero, Te values (2 km < Te < 5 km) produce the best fit to the gravity data, although uncertainty is high due to inaccuracies in the Digital Elevation Model. The slopes of flexural horizons revealed in seismic reflection lines are consistent with this, indicating a Te of 2 km to 5 km, although the depths to these horizons are not consistent, perhaps due to a northwards slope, or step, in the pre-flexural surface. These results indicate that the lithospheric strength of southern McMurdo Sound is significantly less than estimates of the regional average (Te ~ 20 km). This low strength may reflect the weakening effects of the Terror Rift, and perhaps also the Discovery Accommodation Zone, a region of major transverse faulting. A low Te model (Te = 3) for southern McMurdo Sound predicts the development of two discrete flexural depressions, each 2-2.5 km deep. The predicted stratigraphy of the northern basin reflects flexure due to Ross Island, predominantly erupted since ca. 1.8 Ma. The predicted stratigraphy of the southern basin reflects more gradual flexure from ca. 10 Ma to ca. 2 Ma, due to the more dispersed volcanoes of the Discovery subprovince. Collectively, these two basins have the potential to preserve a remarkable stratigraphic record of Antarctic climate change through the late Neogene.

Polymerisation characteristics of resin composites polymerised with different curing units.

PubMed

Danesh, Gholamreza; Davids, Hendrick; Reinhardt, Klaus-Jürgen; Ott, Klaus; Schäfer, Edgar

2004-08-01

The aim of this study was to compare the plasma arc light source Apollo 95E and the conventional halogen lamp Elipar Visio regarding a number of polymerisation characteristics of different resin composites. Four different resin composites (Arabesk Top, Herculite XRV, Pertac II, Tetric) were irradiated using the Apollo 95E unit for one, two or three cycles of 3 s and using the Elipar Visio unit for 40 s. The investigated polymerisation characteristics were: flexural strength and modulus of elasticity, bond strength to dentine, depth of polymerisation, and quantity of remaining double bonds. The data were treated statistically by analysis of variance and by Scheffé test. The modulus of elasticity and the flexural strength resulting from curing with Apollo 95E for 1 x 3 s were equal to or less than those resulting from curing with Elipar Visio. The bond strength to dentine and the depth of polymerisation with Apollo 95E used for 1 x 3 s were equal to or less than that obtained with the conventional lamp, depending on the resin composite. Irradiation of Herculite XRV resulted in a higher quantity of remaining double bonds than did Elipar Visio. In general, two or three curing cycles of 3 s with Apollo 95E were necessary to produce mechanical properties not significantly worse than with 40 s of conventional curing. The efficiency of plasma arc curing with Apollo 95E strongly depends on the resin composite. For most resin composites tested, plasma arc curing for 3 s resulted in inferior mechanical properties as compared to conventional curing.

Environmental Effects on Graphite-Epoxy Fatigue Properties

NASA Technical Reports Server (NTRS)

Sumsion, H. T.

1976-01-01

Effects of torsional and flexural fatigue on the long-time Integrity of advanced graphite-epoxy structural composites have been investigated. Torsional fatigue tests were run at stress ratios of R = 0 (zero to maximum, repeated) and R = -1 (zero mean stress) on unidirectional, angleply, and woven graphite fiber materials in air and water at room temperature and at 74 C. Flexural fatigue tests (four-point bending) with R = -1 were run in air and water at room temperature, and with R = 0 in air. Results show that, in torsional cycling, both water environment and higher test temperature contribute to significant degradation of torsional stiffness. The degradation of stiffness from torsional stress cycling was observed to be much greater with R = -1 than with simple R = 0 cycling. The effect of environment also is greater in the fully reversed cycling. Flexural fatigue results on +/- 30 deg material show a large fatigue effect, with fatigue limits of less than 50% and 30% of the static failure strength for specimens tested under stress ratios of R = 0 and R = -1, respectively. Compliance measurements indicate that the final failures are preceded by damage initiation and accumulation, which begins at about 1% of the specimen life.

Intrinsic low pass filtering improves signal-to-noise ratio in critical-point flexure biosensors

DOE Office of Scientific and Technical Information (OSTI.GOV)

Jain, Ankit; Alam, Muhammad Ashraful, E-mail: alam@purdue.edu

2014-08-25

A flexure biosensor consists of a suspended beam and a fixed bottom electrode. The adsorption of the target biomolecules on the beam changes its stiffness and results in change of beam's deflection. It is now well established that the sensitivity of sensor is maximized close to the pull-in instability point, where effective stiffness of the beam vanishes. The question: “Do the signal-to-noise ratio (SNR) and the limit-of-detection (LOD) also improve close to the instability point?”, however remains unanswered. In this article, we systematically analyze the noise response to evaluate SNR and establish LOD of critical-point flexure sensors. We find thatmore » a flexure sensor acts like an effective low pass filter close to the instability point due to its relatively small resonance frequency, and rejects high frequency noise, leading to improved SNR and LOD. We believe that our conclusions should establish the uniqueness and the technological relevance of critical-point biosensors.« less

The effect of high fiber fraction on some mechanical properties of unidirectional glass fiber-reinforced composite.

PubMed

Abdulmajeed, Aous A; Närhi, Timo O; Vallittu, Pekka K; Lassila, Lippo V

2011-04-01

This study was designed to evaluate the effect of an increase of fiber-density on some mechanical properties of higher volume fiber-reinforced composite (FRC). Five groups of FRC with increased fiber-density were fabricated and two additional groups were prepared by adding silanated barium-silicate glass fillers (0.7 μm) to the FRC. The unidirectional E-glass fiber rovings were impregnated with light-polymerizable bisGMA-TEGDMA (50-50%) resin. The fibers were pulled through a cylindrical mold with an opening diameter of 4.2mm, light cured for 40s and post-cured at elevated temperature. The cylindrical specimens (n=12) were conditioned at room temperature for 2 days before testing with the three-point bending test (Lloyd Instruments Ltd.) adapted to ISO 10477. Fiber-density was analyzed by combustion and gravimetric analyzes. ANOVA analysis revealed that by increasing the vol.% fraction of E-glass fibers from 51.7% to 61.7% there was a change of 27% (p<0.05) in the modulus of elasticity, 34% (p<0.05) in the toughness, and 15% (p<0.05) in the load bearing capacity, while there was only 8% (p<0.05) increase in the flexural strength although it was statistically insignificant. The addition of particulate fillers did not improve the mechanical properties. This study showed that the properties of FRC could be improved by increasing fibervolume fraction. Modulus of elasticity, toughness, and load bearing capacity seem to follow the law of ratio of quantity of fibers and volume of the polymer matrix more precisely than flexural strength when high fiber-density is used. Copyright © 2010 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Stabilizing sodium hypochlorite at high pH: effects on soft tissue and dentin.

PubMed

Jungbluth, Holger; Marending, Monika; De-Deus, Gustavo; Sener, Beatrice; Zehnder, Matthias

2011-05-01

When sodium hypochlorite solutions react with tissue, their pH drops and tissue sorption decreases. We studied whether stabilizing a NaOCl solution at a high pH would increase its soft-tissue dissolution capacity and effects on the dentin matrix compared with a standard NaOCl solution of the same concentration and similar initial pH. NaOCl solutions were prepared by mixing (1:1) a 10% stock solution with water (standard) or 2 mol/L NaOH (stabilized). Physiological saline and 1 mol/L NaOH served as the controls. Chlorine content and alkaline capacity of NaOCl solutions were determined. Standardized porcine palatal soft-tissue specimens and human root dentin bars were exposed to test and control solutions. Weight loss percentage was assessed in the soft-tissue dissolution assay. Three-point bending tests were performed on the root dentin bars to determine the modulus of elasticity and flexural strength. Values between groups were compared using one-way analysis of variance with the Bonferroni correction for multiple testing (α < .05). Both solutions contained 5% NaOCl. One milliliter of the standard and the stabilized solution consumed 4.0 mL and 13.7 mL of a 0.1-mol/L HCl solution before they reached a pH level of 7.5, respectively. The stabilized NaOCl dissolved significantly more soft tissue than the standard solution, and the pH remained high. It also caused a higher loss in elastic modulus and flexure strength (P < .05) than the control solutions, whereas the standard solution did not. NaOH-stabilized NaOCl solutions have a higher alkaline capacity and are thus more proteolytic than standard counterparts. Copyright © 2011 American Association of Endodontists. Published by Elsevier Inc. All rights reserved.

Thermoplastic composites for veneering posterior teeth-a feasibility study.

PubMed

Gegauff, Anthony G; Garcia, Jose L; Koelling, Kurt W; Seghi, Robert R

2002-09-01

This pilot study was conducted to explore selected commercially-available thermoplastic composites that potentially had physical properties superior to currently available dental systems for restoring esthetic posterior crowns. Polyurethane, polycarbonate, and poly(ethylene/tetrafluoroethylene) (ETFE) composites and unfilled polyurethane specimens were injection molded to produce shapes adaptive to five standardized mechanical tests. The mechanical testing included abrasive wear rate, yield strength, apparent fracture toughness (strength ratio), flexural strength, and compressive strength. Compared to commercially available dental composites, abrasion wear rates were lower for all materials tested, yield strength was greater for the filled polycarbonates and filled polyurethane resins, fracture toughness testing was invalid (strength ratios were calculated for comparison of the pilot test materials), flexural strength was roughly similar except for the filled ETFE which was significantly greater, and compressive strength was lower. Commercially available thermoplastic resin composites, such as polyurethane, demonstrate the potential for development of an artificial crown material which exceeds the mechanical properties of currently available esthetic systems, if compressive strength can be improved.

Mechanical characterization of glass fiber (woven roving/chopped strand mat E-glass fiber) reinforced polyester composites

NASA Astrophysics Data System (ADS)

Bhaskar, V. Vijaya; Srinivas, Kolla

2017-07-01

Polymer reinforced composites have been replacing most of the engineering material and their applications become more and more day by day. Polymer composites have been analyzing from past thirty five years for their betterment for adapting more applications. This paper aims at the mechanical properties of polyester reinforced with glass fiber composites. The glass fiber is reinforced with polyester in two forms viz Woven Rovings (WRG) and Chopped Strand Mat (CSMG) E-glass fibers. The composites are fabricated by hand lay-up technique and the composites are cut as per ASTM Standard sizes for corresponding tests like flexural, compression and impact tests, so that flexural strength, compression strength, impact strength and inter laminar shear stress(ILSS) of polymer matrix composites are analyzed. From the tests and further calculations, the polyester composites reinforced with Chopped Strand Mat glass fiber have shown better performance against flexural load, compression load and impact load than that of Woven Roving glass fiber.

An experimental bioactive dental ceramic for metal-ceramic restorations: Textural characteristics and investigation of the mechanical properties.

PubMed

Goudouri, Ourania-Menti; Kontonasaki, Eleana; Papadopoulou, Lambrini; Manda, Marianthi; Kavouras, Panagiotis; Triantafyllidis, Konstantinos S; Stefanidou, Maria; Koidis, Petros; Paraskevopoulos, Konstantinos M

2017-02-01

The aim of this study was the evaluation of the textural characteristics of an experimental sol-gel derived feldspathic dental ceramic, which has already been proven bioactive and the investigation of its flexural strength through Weibull Statistical Analysis. The null hypothesis was that the flexural strength of the experimental and the commercial dental ceramic would be of the same order, resulting in a dental ceramic with apatite forming ability and adequate mechanical integrity. Although the flexural strength of the experimental ceramics was not statistically significant different compared to the commercial one, the amount of blind pores due to processing was greater. The textural characteristics of the experimental ceramic were in accordance with the standard low porosity levels reported for dental ceramics used for fixed prosthetic restorations. Feldspathic dental ceramics with typical textural characteristics and advanced mechanical properties as well as enhanced apatite forming ability can be synthesized through the sol-gel method. Copyright © 2016 Elsevier Ltd. All rights reserved.

The Effect of Different Shape and Perforated rHDPE in Concrete Structures on Flexural Strength

NASA Astrophysics Data System (ADS)

Yuhazri, MY; Hafiz, KM; Myia, YZA; Jia, CP; Sihombing, H.; Sapuan, SM; Badarulzaman, NA

2017-10-01

This research was carried out to develop a reinforcing structure from recycled HDPE plastic lubricant containers to be embedded in concrete structure. Different forms and shapes of recycled HDPE plastic are designed as reinforcement incorporate with cement. In this study, the reinforcing structure was prepared by washing, cutting, dimensioning and joining of the waste HDPE containers (direct technique without treatment on plastic surface). Then, the rHDPE reinforced concrete was produced by casting based on standard of procedure in civil engineering technique. Eight different shapes of rHDPE in concrete structure were used to determine the concrete’s ability in terms of flexural strength. Embedded round shape in solid and perforated of rHDPE in concrete system drastically improved flexural strength at 17.78 % and 13.79 %. The result would seem that the concrete with reinforcing rHDPE structure exhibits a more gradual or flexible properties than concrete beams without reinforcement that has the properties of fragile.

Effects of various etching protocols on the flexural properties and surface topography of fiber-reinforced composite dental posts.

PubMed

Aksornmuang, Juthatip; Chuenarrom, Chanya; Chittithaworn, Natjira

2017-09-26

The purpose of this study was to evaluate the flexural properties and surface topography of fiber posts surface-treated with various etching protocols. Seventy each of three types of fiber posts: RelyX Fiber Post, Tenax Fiber Trans, and D.T. Light-Post Illusion X-Ro, were randomly divided into 7 groups: no surface treatment, surface treated with hydrofluoric acid (HF) 4.5% for 60 s, HF 4.5% for 120 s, HF 9.6% for 15 s, HF 9.6% for 60 s, HF 9.6% for 120 s, and treated with H 2 O 2 24% for 10 min. The specimens were then subjected to a three-point bending test. Surface topographies of the posts were observed using a SEM. The results indicate that fiber post surface pretreatments had no adverse effects on the flexural properties. However, the fiber posts treated with high HF concentrations or long etching times seemed to have more surface irregularities.

Mechanical properties and internal fit of 4 CAD-CAM block materials.

PubMed

Goujat, Alexis; Abouelleil, Hazem; Colon, Pierre; Jeannin, Christophe; Pradelle, Nelly; Seux, Dominique; Grosgogeat, Brigitte

2018-03-01

Recent polymer-based computer-assisted design and computer-assisted manufacturing (CAD-CAM) materials have been commercialized for inlay restorations, a polymer-infiltrated ceramic-network (PICN) and composite resin nanoceramics. Little independent evidence regarding their mechanical properties exists. Internal adaptation is an important factor for the clinical success and longevity of a restoration, and data concerning this parameter for inlays made with these blocks are scarce. The purpose of this in vitro study was to evaluate and compare the mechanical properties (flexural strength, flexural modulus, Vickers hardness, fracture toughness) and the internal adaptation of these recent polymer-based blocks with a lithium disilicate glass-ceramic block. The materials tested in this study were a PICN material (Vita Enamic), 2 composite resin nanoceramics (Lava Ultimate; 3M ESPE and Cerasmart; GCDental Products), and a lithium disilicate glass-ceramic (IPS e.max CAD). Mechanical properties were evaluated according to ISO norm DIS 6872:2013. Bar-shaped specimens (18×3×3 mm) were prepared and submitted to a 3-point bend test using a universal testing machine at a cross-head speed of 0.5 mm/min. In addition, identical cavities were prepared in 60 human mandibular extracted molars (n=15) and optically scanned to receive mesioocclusodistal inlays milled with the 4 materials tested in a CEREC Inlab milling machine. The replica technique and a stereomicroscope (×20) were used to measure the internal fit of the inlays at 9 preselected locations. All data were statistically analyzed using 1-way ANOVA and the post hoc Tukey multiple comparison or Games-Howell test (α=.05). The mean flexural strength of the tested blocks ranged from 148.7 ±9.5 MPa (Vita Enamic) to 216.5 ±28.3 MPa (Cerasmart). The mean flexural modulus ranged from 23.3 ±6.4 GPa (Vita Enamic) to 52.8 ±10.5 GPa (IPS e.max CAD). The mean Vickers hardness ranged from 0.66 ±0.02 GPa (Cerasmart) to 5.98 ±0.69 GPa (IPS e.max CAD). The mean fracture toughness ranged from 1.2 ±0.17 MPa.m 1/2 (Cerasmart) to 1.8 ±0.29 MPa.m 1/2 (IPS e.max CAD). The values for internal discrepancy ranged from 119 ±55 μm to 234 ±51 μm. The mean internal discrepancy was significantly higher for Lava Ultimate (P<.05) than IPS e.max CAD and Cerasmart but not for Vita Enamic. The factor ''material'' was statistically significant in relation to the mechanical properties evaluated in this study (P<.05). The Pearson correlation was negative between the flexural strength results and the internal discrepancy of the materials tested (R 2 =0.941; P<.05). The mechanical properties of the CAD-CAM block materials tested were within the acceptable range for fabrication of single restorations according to the ISO standard for ceramics (ISO 6872:2008). IPS e.max CAD and Cerasmart were observed to have superior flexural strength and better internal fit. Copyright © 2017 Editorial Council for the Journal of Prosthetic Dentistry. Published by Elsevier Inc. All rights reserved.

[In vitro evaluation of low-temperature aging effects of Y2O3 stabilized tetragonal zirconia polycrystals dental ceramics].

PubMed

Yi, Yuan-fu; Liu, Hong-chen; Wang, Chen; Tian, Jie-mo; Wen, Ning

2008-03-01

To investigate the influence of in vitro low-temperature degradation (LTD) treatment on the structural stability of 5 kinds of Y2O3 stabilized tetragonal zirconia polycrystals (Y-TZP) dental ceramics. TZ-3YS powder was compacted at 200 MPa using cold isostatic pressure and pre-sintered at 1050 degrees C for 2 h forming presintered blocks. Specimens were sectioned into 15 mm x 15 mm x 1.5 mm slices from blocks of TZ-3YS, Vita In-Ceram YZ, Ivoclar, Cercon Smart, and Kavo Y-TZP presintered blocks, 18 slices for each brand, and then densely sintered. Specimens were divided into 6 groups and subjected to an accelerated aging test carried out in an autoclave in steam at 134 degrees C, 0.2 MPa, for 0, 1, 2, 3, 4, and 5 h. X-ray diffraction (XRD) was used to identify crystal phases and relative content of monoclinic phase was calculated. Specimens for three-point bending test were fabricated using TZ-3YS ceramics according to the ISO 6872 standard and bending strength was tested before and after aging. The polished and aging specimens of TZ-3YS and Cercon Smart zirconia ceramics were observed by atomic force microscopy (AFM) to evaluate surface microstructure. Tetragonal-to-monoclinic phase transformation was detected for specimens of TZ-3YS, Vita In-Ceram YZ, Ivoclar, and Kavo zirconia ceramics except for Cercon Smart ceramics after aging, and the relative content of monoclinic phase was increasing with the prolonged aging time. TZ-3YS was the most affected material, Kavo took the second, and Vita and Ivoclar were similar. Aging had no significant negative effects on flexural strength of TZ-3YS with average bending strength being over 1100 MPa. The nucleation and growth of monoclinic phase were detected by AFM in surface of Cercon Smart zirconia in which monoclinic phase was not detected by XRD. The results suggest that LTD of dental Y-TZP is time dependent, but the aging test does not reduce the flexural strength of TZ-3YS. The long-term clinical serviceability of dental Y-TZP needs further observation.

Radial basis function network learns ceramic processing and predicts related strength and density

NASA Technical Reports Server (NTRS)

Cios, Krzysztof J.; Baaklini, George Y.; Vary, Alex; Tjia, Robert E.

1993-01-01

Radial basis function (RBF) neural networks were trained using the data from 273 Si3N4 modulus of rupture (MOR) bars which were tested at room temperature and 135 MOR bars which were tested at 1370 C. Milling time, sintering time, and sintering gas pressure were the processing parameters used as the input features. Flexural strength and density were the outputs by which the RBF networks were assessed. The 'nodes-at-data-points' method was used to set the hidden layer centers and output layer training used the gradient descent method. The RBF network predicted strength with an average error of less than 12 percent and density with an average error of less than 2 percent. Further, the RBF network demonstrated a potential for optimizing and accelerating the development and processing of ceramic materials.

Experimental Investigation on Mechanical and Thermal Properties of Marble Dust Particulate-Filled Needle-Punched Nonwoven Jute Fiber/Epoxy Composite

NASA Astrophysics Data System (ADS)

Sharma, Ankush; Patnaik, Amar

2018-03-01

The present investigation evaluates the effects of waste marble dust, collected from the marble industries of Rajasthan, India, on the mechanical properties of needle-punched nonwoven jute fiber/epoxy composites. The composites with varying filler contents from 0 wt.% to 30 wt.% marble dust were prepared using vacuum-assisted resin-transfer molding. The influences of the filler material on the void content, tensile strength, flexural strength, interlaminar shear strength (ILSS), and thermal conductivity of the hybrid composites have been analyzed experimentally under the desired optimal conditions. The addition of marble dust up to 30 wt.% increases the flexural strength, ILSS, and thermal conductivity, but decreases the tensile strength. Subsequently, the fractured surfaces of the particulate-filled jute/epoxy composites were analyzed microstructurally by field-emission scanning electron microscopy.

Analysis of Adhesively Bonded Ceramics Using an Asymmetric Wedge Test

DTIC Science & Technology

2008-12-01

4 Figure 2. Average crack ...flexure specimen. The flaw, indicated by the white arrow, is a subsurface semi-elliptical crack induced by surface machining damage...strength-limiting orthogonal surface machining crack in an alumina flexure specimen coated with a single layer of film adhesive. The white arrow

Functional gradients in the pericarp of the green coconut inspire asymmetric fibre-composites with improved impact strength, and preserved flexural and tensile properties.

PubMed

Graupner, Nina; Labonte, David; Humburg, Heide; Buzkan, Tayfun; Dörgens, Anna; Kelterer, Wiebke; Müssig, Jörg

2017-02-28

Here we investigate the mechanical properties and structural design of the pericarp of the green coconut (Cocos nucifera L.). The pericarp showed excellent impact characteristics, and mechanical tests of its individual components revealed gradients in stiffness, strength and elongation at break from the outer to the inner layer of the pericarp. In order to understand more about the potential effect of such gradients on 'bulk' material properties, we designed simple, graded, cellulose fibre-reinforced polylactide (PLA) composites by stacking layers reinforced with fibres of different mechanical properties. Tensile properties of the graded composites were largely determined by the 'weakest' fibre, irrespective of the fibre distribution. However, a graded design led to pronounced asymmetric bending and impact properties. Bio-inspired, asymmetrically graded composites showed a flexural strength and modulus comparable to that of the strongest reference samples, but the elongation at maximum load was dependent on the specimen orientation. The impact strength of the graded composites showed a similar orientation-dependence, and peak values exceeded the impact strength of a non-graded reference composite containing identical fibre fractions by up to a factor of three. In combination, our results show that an asymmetric, systematic variation of fibre properties can successfully combine desirable properties of different fibre types, suggesting new routes for the development of high-performance composites, and improving our understanding of the structure-function relationship of the coconut pericarp.

Possibility of using waste tire rubber and fly ash with Portland cement as construction materials.

PubMed

Yilmaz, Arin; Degirmenci, Nurhayat

2009-05-01

The growing amount of waste rubber produced from used tires has resulted in an environmental problem. Recycling waste tires has been widely studied for the last 20 years in applications such as asphalt pavement, waterproofing systems and membrane liners. The aim of this study is to evaluate the feasibility of utilizing fly ash and rubber waste with Portland cement as a composite material for masonry applications. Class C fly ash and waste automobile tires in three different sizes were used with Portland cement. Compressive and flexural strength, dry unit weight and water absorption tests were performed on the composite specimens containing waste tire rubber. The compressive strength decreased by increasing the rubber content while increased by increasing the fly ash content for all curing periods. This trend is slightly influenced by particle size. For flexural strength, the specimens with waste tire rubber showed higher values than the control mix probably due to the effect of rubber fibers. The dry unit weight of all specimens decreased with increasing rubber content, which can be explained by the low specific gravity of rubber particles. Water absorption decreased slightly with the increase in rubber particles size. These composite materials containing 10% Portland cement, 70% and 60% fly ash and 20% and 30% tire rubber particles have sufficient strength for masonry applications.

Fracture strength testing of crowns made of CAD/CAM composite resins.

PubMed

Okada, Ryota; Asakura, Masaki; Ando, Akihiro; Kumano, Hirokazu; Ban, Seiji; Kawai, Tatsushi; Takebe, Jun

2018-03-28

The purpose of this study was to ascertain whether computer aided design/computer aided manufacturing (CAD/CAM) composite resin crowns have sufficient strength to withstand the bite force of the molar teeth. The null hypothesis was that the fracture strength of CAD/CAM composite resin crowns is lower than the average maximum bite force of the molar tooth. The crowns, which shape is the right maxillary first molar, were fabricated using four CAD/CAM blanks made of composite resins (Block HC: HC, KZR-CAD HR: HR, KZR-CAD HR2: HR2, Avencia Block: AVE) and one CAD/CAM blank made of lithium disilicate glass-ceramic (IPS e.max CAD: IPS), which was used as a control. Fracture strength of fabricated crowns bonded to metal abutment and biaxial flexural strength of the materials were evaluated. The results of fracture strength test and biaxial flexural strength test showed different tendencies. The fracture strength of CAD/CAM composite resin crowns except HC ranged from 3.3kN to 3.9kN, and was similar to that of IPS (3.3kN). In contrast, biaxial flexural strength of CAD/CAM composite resins ranged from 175MPa to 247MPa, and was significantly lower than that of IPS (360MPa). All CAD/CAM composite resin crowns studied presented about 3-4 times higher fracture strength than the average maximum bite force of the molar tooth (700-900N), which result leads to the conclusion that CAD/CAM composite resin crowns would have sufficient strength to withstand the bite force of the molar teeth. Copyright © 2017 Japan Prosthodontic Society. Published by Elsevier Ltd. All rights reserved.

The effect of surface treatments on dental zirconia: An analysis of biaxial flexural strength, surface roughness and phase transformation.

PubMed

Botelho, Michael G; Dangay, Sachin; Shih, Kaimin; Lam, Walter Y H

2018-05-26

This study investigates the effect of selected surface finishing techniques on the biaxial flexural strength, surface roughness and phase transformation of a zirconia dental restorative material. Fully-sintered zirconia discs (⌀19.5 mm × 0.85 mm) were treated on one side with a single or a combination of the following treatments: diamond and/or tungsten-carbide burs without water coolant in an air-turbine handpiece, air-particle abrasion, rubber-point polishing in a contra-angle handpiece, or no treatment (control). Biaxial flexural strength (BFS) (eleven groups, n = 10) was determined using a universal testing machine and surface roughness (thirteen groups, n = 6) was assessed using a profilometer. Results were analysed using one-way ANOVA and Student-Newman-Keuls Post-hoc test (α = 0.05) with Bonferroni correction. Specimens were observed under scanning electron microscopy (SEM) and x-ray diffraction (XRD) for their microstructure and crystalline phases respectively. Grinding with diamond burs did not weaken zirconia (p > 0.0045) but produced rougher surfaces than the control group (p < 0.0038). Tungsten-carbide burs smoothened diamond ground specimens (p < 0.0038) for both grits of diamond. Specimens ground by tungsten-carbide burs have significantly reduced mean BFS (p < 0.0045) by up to two-thirds and SEM revealed fine surface cracks. Air-particle abrasion restored the mean BFS of tungsten-carbide ground specimens to control levels (p > 0.0045) and surface cracks were not observed. Phase transformation was not detected by XRD. Dental zirconia ground dry with tungsten-carbide burs has a significantly reduced BFS and a smooth but defective surface. These defects may be removed and BFS restored by air-particle abrasion. The use of tungsten-carbide burs for grinding dental zirconia should be cautioned. Diamond grinding does not weaken zirconia but requires further polishing. Copyright © 2018 Elsevier Ltd. All rights reserved.

Surface modification of quartz fibres for dental composites through a sol-gel process.

PubMed

Wang, Yazi; Wang, Renlin; Habib, Eric; Wang, Ruili; Zhang, Qinghong; Sun, Bin; Zhu, Meifang

2017-05-01

In this study, quartz fibres (QFs) surface modification using a sol-gel method was proposed and dental posts reinforced with modified QFs were produced. A silica sol (SS) was prepared using tetraethoxysilane (TEOS) and 3-methacryloxypropyltrimethoxysilane (γ-MPS) as precursors. The amount of γ-MPS in the sol-gel system was varied from 0 to 24wt.% with a constant molar ratio of TEOS, ethanol, deionized water, and HCl. Thermogravimetric analysis (TGA), Fourier transform infrared spectroscopy (FT-IR), and contact angle (CA) measurements were used to characterize the modified QFs, which confirmed that SS had successfully coated the surface of QFs. SEM images showed good interfacial bonding between the modified QFs and the resin matrix. The results of three-point bending tests of the fibre reinforced composite (FRC) posts showed that the QFs modified by SS with 12wt.% γ-MPS presented the best mechanical properties, demonstrating improvements of 108.3% and 89.6% for the flexural strength and flexural modulus, respectively, compared with untreated QFs. Furthermore, the sorption and solubility of the prepared dental posts were also studied by immersing the posts in artificial saliva (AS) for 4weeks, and yielded favourable results. This sol-gel surface modification method promises to resolve interfacial bonding issues of fibres with the resin matrix, and produce FRC posts with excellent properties. Copyright © 2017. Published by Elsevier B.V.

Prediction of Mean and Design Fatigue Lives of Self Compacting Concrete Beams in Flexure

NASA Astrophysics Data System (ADS)

Goel, S.; Singh, S. P.; Singh, P.; Kaushik, S. K.

2012-02-01

In this paper, result of an investigation conducted to study the flexural fatigue characteristics of self compacting concrete (SCC) beams in flexure are presented. An experimental programme was planned in which approximately 60 SCC beam specimens of size 100 × 100 × 500 mm were tested under flexural fatigue loading. Approximately 45 static flexural tests were also conducted to facilitate fatigue testing. The flexural fatigue and static flexural strength tests were conducted on a 100 kN servo-controlled actuator. The fatigue life data thus obtained have been used to establish the probability distributions of fatigue life of SCC using two-parameter Weibull distribution. The parameters of the Weibull distribution have been obtained by different methods of analysis. Using the distribution parameters, the mean and design fatigue lives of SCC have been estimated and compared with Normally vibrated concrete (NVC), the data for which have been taken from literature. It has been observed that SCC exhibits higher mean and design fatigue lives compared to NVC.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kanna, V.; Olson, R.A.; Jennings, H.M.

The effects of drying on mortars containing Portland cement blended with fly ash or slag on the shrinkage, extent of surface cracking, pore size distribution as measured by mercury intrusion porosimetry, flexural strength, fracture toughness, and Young`s modulus are reported. Specimens were exposed to conditions of 100% relative humidity (RH), 50% RH, and/or oven-drying at 105 C. Drying coarsened the pore structure and increased the density of surface cracks, but surprisingly increased the flexural strength and the fracture toughness, and as anticipated lowered the Young`s modulus. This was regardless of the content of mineral admixture.

PMR-15/Layered Silicate Nanocomposites For Improved Thermal Stability And Mechanical Properties

NASA Technical Reports Server (NTRS)

Campbell, Sandi; Scheiman, Daniel; Faile, Michael; Papadopoulos, Demetrios; Gray, Hugh R. (Technical Monitor)

2002-01-01

Montmorillonite clay was organically modified by co-exchange of an aromatic diamine and a primary alkyl amine. The clay was dispersed into a PMR (Polymerization of Monomer Reactants)-15 matrix and the glass transition temperature and thermal oxidative stability of the resulting nanocomposites were evaluated. PMR-15/ silicate nanocomposites were also investigated as a matrix material for carbon fabric reinforced composites. Dispersion of the organically modified silicate into the PMR-15 matrix enhanced the thermal oxidative stability, the flexural strength, flexural modulus, and interlaminar shear strength of the polymer matrix composite.

Viscoelastic Properties of Advanced Polymer Composites for Ballistic Protective Applications

DTIC Science & Technology

1994-09-01

ofthe Damaged Sample 78 Figure 69: Fracture Surface of Damage Area Near the Point of Penetration 79 Figure 70. Closer View ofthe Damaged Area...LIST OF TABLES Table 1. Basic Mechanical Properties of the Materials 6 Table 2. Initial DMA Test Results 23 Table 3. Flexural Three Point Bend... point bend testing was conducted using an Instron 1127 Universal Tester to verify the DMA test method and specimen clamping configuration. Interfacial

Strength, Fracture Toughness, Fatigue, and Standardization Issues of Free-standing Thermal Barrier Coatings

NASA Technical Reports Server (NTRS)

Choi, Sung R.; Zhu, Dong-Ming; Miller, Robert A.

2003-01-01

Strength, fracture toughness and fatigue behavior of free-standing thick thermal barrier coatings of plasma-sprayed ZrO2-8wt % Y2O3 were determined at ambient and elevated temperatures in an attempt to establish a database for design. Strength, in conjunction with deformation (stress-strain behavior), was evaluated in tension (uniaxial and trans-thickness), compression, and uniaxial and biaxial flexure; fracture toughness was determined in various load conditions including mode I, mode II, and mixed modes I and II; fatigue or slow crack growth behavior was estimated in cyclic tension and dynamic flexure loading. Effect of sintering was quantified through approaches using strength, fracture toughness, and modulus (constitutive relations) measurements. Standardization issues on test methodology also was presented with a special regard to material's unique constitutive relations.

Mechanical properties of direct core build-up materials.

PubMed

Combe, E C; Shaglouf, A M; Watts, D C; Wilson, N H

1999-05-01

This work was undertaken to measure mechanical properties of a diverse group of materials used for direct core build-ups, including a high copper amalgam, a silver cermet cement, a VLC resin composite and two composites specifically developed for this application. Compressive strength, elastic modulus, diametral tensile strength and flexural strength and modulus were measured for each material as a function of time up to 3 months, using standard specification tests designed for the materials. All the materials were found to meet the minimum specification requirements except in terms of flexural strength for the amalgam after 1 h and the silver cermet at all time intervals. There proved to be no obvious superior material in all respects for core build-ups, and the need exists for a specification to be established specifically for this application.

Reinforcing effect of discontinuous microglass fibers on resin-modified glass ionomer cement.

PubMed

Garoushi, Sufyan; Vallittu, Pekka K; Lassila, Lippo

2018-06-08

This study investigated the reinforcing effect of discontinuous-glass fiber fillers with different loading-fractions on selected mechanical properties and wear of resin-modified glass ionomer cement (RMGIC). Experimental fiber-reinforced RMGIC (Exp-RMGIC) was prepared by adding discontinuous-glass fiber of 200-500 µm in length to the powder of RMGIC (GC Fuji II LC) with different weight ratios (15, 20, 25 and 30 wt%). Mechanical properties and wear were determined for each experimental and control material. Scanning electron microscopy was used to evaluate the microstructure of the Exp-RMGICs. Wear pattern was analyzed by a three-dimensional (3D) noncontact optical profilometer. Fiber-reinforced RMGIC (30 wt%) had significantly higher mechanical performance of fracture toughness (1.9 MPa•m 1/2 ), flexural strength (90.3 MPa), and diametral tensile strength (31 MPa) (p<0.05) compared to unreinforced material (0.8 MPa•m 1/2 , 51.9 and 20.7 MPa). The use of discontinuous-glass fiber fillers with RMGIC matrix is novel reinforcement and yielded superior toughening and flexural performance compared to conventional RMGIC.

Light-attenuating effect of dentin on the polymerization of light-activated restorative resins.

PubMed

Arikawa, Hiroyuki; Kanie, Takahito; Fujii, Koichi; Ban, Seiji; Takahashi, Hideo

2004-12-01

The light-attenuating effect of dentin on the mechanical properties of light-activated composite resins was evaluated using a simple experimental filter. The filter was designed to simulate the light transmittance and light diffusion characteristics of 1.0-mm thick dentin. The depth of cure, surface hardness, and flexural strength for 13 shades of three light-activated restorative resins were examined. These resins were cured either using direct irradiation with a light source, or indirect irradiation through the filter. The attenuation of light intensity by 1.0-mm thick dentin reached 85-90% in the 400-550 nm wavelength region. For all materials, the values of depth of cure, surface hardness on the top and bottom surfaces, and flexural strength of specimens irradiated indirectly through the simulated 1.0-mm thick dentin filter decreased by 37-60%, 16-55%, 50-83%, and 44-82% in comparison with those by direct irradiation, respectively. Recovery from mechanical properties' reduction was achieved when materials were irradiated 1.5-4 times longer than the standard irradiation time.

Effect of fiber diameter on flexural properties of fiber-reinforced composites.

PubMed

Rezvani, Mohammad Bagher; Atai, Mohammad; Hamze, Faeze

2013-01-01

Flexural strength (FS) is one of the most important properties of restorative dental materials which could be improved in fiber-reinforced composites (FRCs) by several methods including the incorporation of stronger reinforcing fibers. This study evaluates the influence of the glass fiber diameter on the FS and elastic modulus of FRCs at the same weight percentage. A mixture of 2,2-bis-[4-(methacryloxypropoxy)-phenyl]-propaneand triethyleneglycol dimethacrylate (60/40 by weight) was prepared as the matrix phase in which 0.5 wt. % camphorquinone and 0.5 wt. % N-N'-dimethylaminoethyl methacrylate were dissolved as photoinitiator system. Glass fibers with three different diameters (14, 19, and 26 μm) were impregnated with the matrix resin using a soft brush. The FRCs were inserted into a 2 × 2 × 25 mm3 mold and cured using a light curing unit with an intensity of ca. 600 mW/cm2 . The FS of the FRCs was measured in a three-point bending method. The elastic modulus was determined from the slope of the initial linear part of stress-strain curve. The fracture surface of the composites was observed using scanning electron microscopy to study the fiber-matrix interface. The results were analyzed and compared using one-way ANOVA and Tukey's post-hoc test. Although the FS increased as the diameter of fibers increased up to 19 μm (P < 0.05), no significant difference was observed between the composites containing fibers with diameters of 19 and 26 μm. The diameter of the fibers influences the mechanical properties of the FRCs.

Stress-strain behavior under static loading in Gd123 high-temperature superconductors at 77 K

NASA Astrophysics Data System (ADS)

Fujimoto, Hiroyuki; Murakami, Akira; Teshima, Hidekazu; Morita, Mitsuru

2013-10-01

Mechanical properties of melt-growth GdBa2Cu3Ox (Gd123) superconducting samples with 10 wt.% Ag2O and 0.5 wt.% Pt were evaluated at 77 K through flexural tests for specimens cut from the samples in order to estimate the mechanical properties of the Gd123 material without metal substrates, buffer layers or stabilization layers. We discuss the mechanical properties; the Young's modulus and flexural strength with stress-strain behavior at 77 K. The results show that the flexural strength and fracture strain of Gd123 at 77 K are approximately 100 MPa and 0.1%, respectively, and that the origin of the fracture is defects such as pores, impurities and non-superconducting compounds. We also show that the Young's modulus of Gd123 is estimated to be 160-165 GPa.

Mechanical and morphological properties of polypropylene/nano α-Al2O3 composites.

PubMed

Mirjalili, F; Chuah, L; Salahi, E

2014-01-01

A nanocomposite containing polypropylene (PP) and nano α-Al2O3 particles was prepared using a Haake internal mixer. Mechanical tests, such as tensile and flexural tests, showed that mechanical properties of the composite were enhanced by addition of nano α-Al2O3 particles and dispersant agent to the polymer. Tensile strength was approximately ∼ 16% higher than pure PP by increasing the nano α-Al2O3 loading from 1 to 4 wt% into the PP matrix. The results of flexural analysis indicated that the maximum values of flexural strength and flexural modulus for nanocomposite without dispersant were 50.5 and 1954 MPa and for nanocomposite with dispersant were 55.88 MPa and 2818 MPa, respectively. However, higher concentration of nano α-Al2O3 loading resulted in reduction of those mechanical properties that could be due to agglomeration of nano α-Al2O3 particles. Transmission and scanning electron microscopic observations of the nanocomposites also showed that fracture surface became rougher by increasing the content of filler loading from 1 to 4% wt.

Experimental Study on Semi-Dry Flue Gas Desulfurization Ash Used in Steel Slag Composite Material

NASA Astrophysics Data System (ADS)

Lu, Lijun; Fang, Honghui

This article carried out the experimental study on using desulfurization ash in steel slag composite material. This was done by investigating the desulfurization ash content in formula one and formula two samples on the influence of setting time and strength of mortar. Through this study the following conclusions were reached for formula one: (1) a setting time of more than 10 hours is required, (2) a dosage of desulfurization ash of 1 2% is optimal, where flexural strength is reduced by 10% 23% and compressive strength reduced by 5.7% 16.4%. The conclusions of formula two were: (1) when the dosage of desulfurization ash is within 5%, the setting time is within 10 hours; (2) when the dosage of desulfurization ash is 1 2%, the flexural strength is increased by 5 7% and the compressive strength is reduced by 1 2%. The results show that the formula two is better.

Properties of poly(lactic acid)/hydroxyapatite composite through the use of epoxy functional compatibilizers for biomedical application.

PubMed

Monmaturapoj, Naruporn; Srion, Autcharaporn; Chalermkarnon, Prasert; Buchatip, Suthawan; Petchsuk, Atitsa; Noppakunmongkolchai, Warobon; Mai-Ngam, Katanchalee

2017-08-01

A composite of 70/30 poly(lactic acid)/hydroxyapatite was systematically prepared using various amounts of glycidyl methacrylate as reactive compatibilizer or Joncryl ADR®-4368 containing nine glycidyl methacrylate functions as a chain extension/branching agent to improve the mechanical and biological properties for suitable usage as internal bone fixation devices. The effect of glycidyl methacrylate/Joncryl on mechanical properties of poly(lactic acid)/hydroxyapatite was investigated through flexural strength. Cell proliferation and differentiation of osteoblast-like MC3T3-E1 cells cultured on the composite samples were determined by Alamar Blue assay and alkaline phosphatase expression, respectively. Result shows that flexural strength tends to decrease, as glycidyl methacrylate content increases except for 1 wt.% glycidyl methacrylate. With an addition of dicumyl peroxide, the flexural strength shows an improvement than that of without dicumyl peroxide probably due to the chemical bonding of the hydroxyapatite and poly(lactic acid) as revealed by FTIR and NMR, whereas the composite with 5 wt.% Joncryl shows the best result, as the flexural strength increases getting close to pure poly(lactic acid). The significant morphology change could be seen in composite with Joncryl where the uniform agglomeration of hydroxyapatite particles oriented in poly(lactic acid) matrix. Addition of the epoxy functional compatibilizers at suitable percentages could also have benefits to cellular attachment, proliferation, differentiation and mineralization. So that, this poly(lactic acid)/hydroxyapatite composite could be a promising material to be used as internal bone fixation devices such as screws, pins and plates.

Characterization of sintered SiC by using NDE

NASA Technical Reports Server (NTRS)

Baaklini, George Y.

1988-01-01

Capabilities of projection microfocus X-radiography and of ultrasonic velocity and attenuation for characterizing silicon carbide specimens were assessed. Silicon carbide batches covered a range of densities and different microstructural characteristics. Room-temperature, four-point flexural strength tests were conducted. Fractography was used to identify types, sizes, and locations of fracture origins. Fracture toughness values were calculated from fracture strength and flaw characterization data. Detection capabilities of radiography for fracture-causing flaws were evaluated. Applicability of ultrasonics for verifying material strength and toughness was examined. Radiography proved useful in detecting high-density inclusions and isolated voids, but failed in detecting surface and subsurface agglomerates and large grains as fracture origins. Ultrasonic velocity dependency on density was evident. Attenuation dependency on density and mean pore size was clearly demonstrated. Understanding attenuation as a function of toughness was limited by shortcomings in K sub IC determination.

[Microstructure and mechanical property of a new IPS-Empress 2 dental glass-ceramic].

PubMed

Luo, Xiao-ping; Watts, D C; Wilson, N H F; Silsons, N; Cheng, Ya-qin

2005-03-01

To investigate the microstructure and mechanical properties of a new IPS-Empress 2 dental glass-ceramic. AFM, SEM and XRD were used to analyze the microstructure and crystal phase of IPS-Empress 2 glass-ceramic. The flexural strength and fracture toughness were tested using 3-point bending method and indentation method respectively. IPS-Empress 2 glass-ceramic mainly consisted of lithium disilicate crystal, lithium phosphate and glass matrix, which formed a continuous interlocking structure. The crystal phases were not changed before and after hot-pressed treatment. AFM showed nucleating agent particles of different sizes distributed on the highly polished ceramic surface. The strength and fracture toughness were 300 MPa and 3.1 MPam(1/2). The high strength and fracture toughness of IPS-Empress 2 glass ceramic are attributed to the fine lithium disilicate crystalline, interlocking microstructure and crack deflection.

Mechanical properties and aesthetics of FRP orthodontic wire fabricated by hot drawing.

PubMed

Imai, T; Watari, F; Yamagata, S; Kobayashi, M; Nagayama, K; Toyoizumi, Y; Nakamura, S

1998-12-01

The FRP wires 0.5 mm in diameter with a multiple fiber structure were fabricated by drawing the fiber polymer complex at 250 degrees C for an esthetic, transparent orthodontic wire. Biocompatible CaO-P2O5-SiO2-Al2O3 (CPSA) glass fibers of 8-20 microm in diameter were oriented unidirectionally in the longitudinal direction in PMMA matrix. The mechanical properties were investigated by 3-point flexural test. The FRP wire showed sufficient strength and a very good elastic recovery after deformation. Young's modulus and the flexural load at deflection 1 mm were nearly independent of the fiber diameter and linearly increased with the fiber fraction. The dependence on fiber fraction obeys well the rule of mixture. This FRP wire could cover the range of strength corresponding to the conventional metal orthodontic wires from Ni-Ti used in the initial stage of orthodontic treatments to Co-Cr used in the final stage by changing the volume ratio of glass fibers with the same external diameter. The estheticity in external appearance was excellent. Thus the new FRP wire can satisfy both mechanical properties necessary for an orthodontic wire and enough estheticity, which was not possible for the conventional metal wire.

Ethanol Postpolymerization Treatment for Improving the Biocompatibility of Acrylic Reline Resins

PubMed Central

Neves, Cristina B.; Lopes, Luís P.; Ferrão, Helena F.; Miranda, Joana P.; Castro, Matilde F.; Bettencourt, Ana F.

2013-01-01

Objective. To evaluate the effect of postpolymerization treatment based on ethanol-aqueous solutions on the residual monomer (RM) content, flexural strength, microhardness, and cytotoxicity of hard chairside reline resins (Kooliner, Ufi Gel Hard). Methods. After polymerization, specimens were immersed in water, 20%, 50%, or 70% ethanol solutions at 23°C or 55°C for 10 minutes. Controls were left untreated. HPLC was used for the determination of RM content. Specimens were submitted to Vickers microhardness and 3-point loading flexural strength tests. Cytotoxicity of resin eluates was determined on human fibroblasts by assessing cellular mitochondrial function and lactate dehydrogenase release. Results. Higher concentrations of ethanol promoted lower RM content at 55°C in both materials. The mechanical properties were maintained after 50% and 20% ethanol treatments in Kooliner and Ufi Gel Hard, respectively. Specimens submitted to those treatments showed significant reduction on cytotoxicity compared to immersion in hot water, the treatment of choice in the recent literature. Significance. Immersion of relined dentures in specific ethanol solutions at 55°C for 10 minutes can be considered an effective postpolymerization treatment contributing to increase materials biocompatibility. The proposed protocol is expeditious and easy to achieve with simple equipment in a dental office. PMID:23971038

Crystallization of high-strength nano-scale leucite glass-ceramics.

PubMed

Theocharopoulos, A; Chen, X; Wilson, R M; Hill, R; Cattell, M J

2013-11-01

Fine-grained, high strength, translucent leucite dental glass-ceramics are synthesized via controlled crystallization of finely milled glass powders. The objectives of this study were to utilize high speed planetary milling of an aluminosilicate glass for controlled surface crystallization of nano-scale leucite glass-ceramics and to test the biaxial flexural strength. An aluminosilicate glass was synthesized, attritor or planetary milled and heat-treated. Glasses and glass-ceramics were characterized using particle size analysis, X-ray diffraction and scanning electron microscopy. Experimental (fine and nanoscale) and commercial (Ceramco-3, IPS Empress Esthetic) leucite glass-ceramics were tested using the biaxial flexural strength (BFS) test. Gaussian and Weibull statistics were applied. Experimental planetary milled glass-ceramics showed an increased leucite crystal number and nano-scale median crystal sizes (0.048-0.055 μm(2)) as a result of glass particle size reduction and heat treatments. Experimental materials had significantly (p<0.05) higher mean BFS and characteristic strength values than the commercial materials. Attritor milled and planetary milled (2h) materials showed no significant (p>0.05) strength difference. All other groups' mean BFS and characteristic strengths were found to be significantly different (p<0.05) to each other. The mean (SD) MPa strengths measured were: Attritor milled: 252.4 (38.7), Planetary milled: 225.4 (41.8) [4h milling] 255.0 (35.0) [2h milling], Ceramco-3: 75.7 (6.8) and IPS Empress: 165.5 (30.6). Planetary milling enabled synthesis of nano-scale leucite glass-ceramics with high flexural strength. These materials may help to reduce problems associated with brittle fracture of all-ceramic restorations and give reduced enamel wear. Copyright © 2013 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Formulation and characterization of date palm fibers mortar by addition of silica fume

NASA Astrophysics Data System (ADS)

Mokhtari, A.; Kriker, A.; Ouaggad, H.; Merad, N.

2018-05-01

This paper presents the results of experimental investigations of the formulated and characterization of date palm fibers mortar by addition of silica fume. The use of addition mineral is widely used in the production of cements through the world. The objective of this work is to bring our contribution to the recovery of local resources in the occurrence vegetable fibers of date palm to weak cost and from renewable source and integrate it in the filled of building. Date palm fiber are from Ouargla town in south of Algeria. Different mortar mixtures were prepared in which the cement was substitute by 10% of silica fume. The mechanical characteristics (compressive and flexural strength) of date palm fibers mortar by treatment of the matrix by the adding of silica fume were examined. The results obtained have shown that the mortar workability as well as the compressive and flexural strength decreases with increasing the silica fume replacement. The results showed that the use of silica fume enabled to evaluate the flexural strength. However, another treatment of fibers and matrix will be recommended for Improved the characteristics.

Study on Flexural Behaviour of Ternary Blended Reinforced Self Compacting Concrete Beam with Conventional RCC Beam

NASA Astrophysics Data System (ADS)

Marshaline Seles, M.; Suryanarayanan, R.; Vivek, S. S.; Dhinakaran, G.

2017-07-01

The conventional concrete when used for structures having dense congested reinforcement, the problems such as external compaction and vibration needs special attention. In such case, the self compacting concrete (SCC) which has the properties like flow ability, passing and filling ability would be an obvious answer. All those SCC flow behavior was governed by EFNARC specifications. In present study, the combination type of SCC was prepared by replacing cement with silica fume (SF) and metakaolin (MK) along with optimum dosages of chemical admixtures. From the fresh property test, cube compressive strength and cylinder split tensile strength, optimum ternary mix was obtained. In order to study the flexural behavior, the optimum ternary mix was taken in which beam specimens of size 1200 mm x 100 mm x 200 mm was designed as singly reinforced section according to IS: 456-2000, Limit state method. Finally the comparative experimental analysis was made between conventional RCC and SCC beams of same grade in terms of flexural strength namely yield load & ultimate load, load- deflection curve, crack size and pattern respectively.

The Degradation Behavior of SiCf/SiO2 Composites in High-Temperature Environment

NASA Astrophysics Data System (ADS)

Yang, Xiang; Cao, Feng; Qing, Wang; Peng, Zhi-hang; Wang, Yi

2018-04-01

SiCf/SiO2 composites had been fabricated efficiently by Sol-Gel method. The oxidation behavior, thermal shock property and ablation behavior of SiCf/SiO2 composites was investigated. SiCf/SiO2 composites showed higher oxidation resistance in oxidation atmosphere, the flexural strength retention ratio was larger than 90.00%. After 1300 °C thermal shock, the mass retention ratio was 97.00%, and the flexural strength retention ratio was 92.60%, while after 1500 °C thermal shock, the mass retention ratio was 95.37%, and the flexural strength retention ratio was 83.34%. After 15 s ablation, the mass loss rate was 0.049 g/s and recession loss rate was 0.067 mm/s. The SiO2 matrix was melted in priority and becomes loosen and porous. With the ablation going on, the oxides were washed away by the shearing action of the oxyacetylene flame. The evaporation of SiO2 took away large amount of heat, which is also beneficial to the protection for SiCf/SiO2 composites.

Two-fold sustainability – Adobe with sawdust as partial sand replacement

NASA Astrophysics Data System (ADS)

Jokhio, Gul A.; Syed Mohsin, Sharifah M.; Gul, Yasmeen

2018-04-01

Adobe is a material that is economic, environment friendly, and provides better indoor air quality. The material required for the preparation of adobe include clay, sand, and sometimes straw or other organic materials. These materials do not require industrial processing or transportation, however, sand mining has been recently posing a threat to the environment. Therefore, to enhance the existing sustainability of adobe, sand can be partially or fully replaced by other waste materials. This approach will not only solve the problem of excessive sand mining, it will also address the issue of waste management. Sawdust is one such waste material that can be used to partially replace sand in Adobe. This paper presents the results of compressive and flexural test carried out on Adobe samples with partial sand replacement by sawdust. The results show that about 4% sand replacement by volume produces higher compressive strength, whereas the flexural strength reduces with the use of sawdust. However, since flexural strength is not a critical property for adobe, it is concluded that replacing sand with sawdust by about 4% of volume will be beneficial.

Fiber Reinforced Concrete (FRC) for High Rise Construction: Case Studies

NASA Astrophysics Data System (ADS)

Gharehbaghi, Koorosh; Chenery, Rhea

2017-12-01

Due to its material element, Fiber Reinforced Concrete (FRC) could be stronger than traditional Concrete. This is due to FRC internal material compounds and elements. Furthermore, FRC can also significantly improve flexural strength when compared to traditional Concrete. This improvement in flexural strength can be varied depending on the actual fibers used. Although not new, FRC is gradually gaining popularity in the construction industry, in particular for high rise structures. This is due to its flexural strength, especially for high seismic zones, as it will provide a better solution then reinforced Concrete. The main aim of this paper is to investigate the structural importance of FRC for the high rise construction. Although there has been numerous studies and literature in justifying the FRC for general construction; this paper will consider its use specifically for high rise construction. Moreover, this paper will closely investigate eight case studies from Australian and United States as a part of the FRC validation for high rise construction. In doing so, this paper will examine their Structural Health Monitoring (SHM) to determine their overall structural performance.

Influence of fiber length on flexural and impact properties of Zalacca Midrib fiber/HDPE by compression molding

NASA Astrophysics Data System (ADS)

Pamungkas, Agil Fitri; Ariawan, Dody; Surojo, Eko; Triyono, Joko

2018-02-01

The aim of the research is to investigate the effect of fiber length on the flexural and impact properties of the composite of Zalacca Midrib Fiber (ZMF)/HDPE. The process of making composite was using compression molding method. The variation of fiber length were 1 mm, 3 mm, 5 mm, 7 mm and 9 mm, at 30% fiber volume fraction. The flexural and impact test according to ASTM D790 and ASTM D5941, respectively. Observing fracture surface was examained by using Scanning Electron Microscopy (SEM). The results showed that the flexural and impact strengths would be increase with the increase of fiber length.

Effect of Glass Fiber Incorporation on Flexural Properties of Experimental Composites

PubMed Central

Fonseca, Rodrigo Borges; Marques, Aline Silva; Bernades, Karina de Oliveira; Carlo, Hugo Lemes; Naves, Lucas Zago

2014-01-01

This study evaluated the effect of fiber addiction in flexural properties of 30 wt% silica filled BisGMA resin (FR) or unfilled Bis-GMA (UR). Ten groups were created (N = 10) varying the resin (FR or UR) and quantity of glass fibers (wt%: 0, 10, 15, 20, and 30). Samples (10 × 2 × 1 mm) were submitted to flexural strength test following SEM examination. Data were analyzed by two-way ANOVA, Tukey, and Student t-test (α = 0.05). Results for flexural strength (MPa) were FR-groups: 0% (442.7 ± 140.6)C, 10% (772.8 ± 446.3)ABC, 15% (854.7 ± 297.3)AB, 20% (863.4 ± 418.0)A, 30% (459.5 ± 140.5)BC; UR-groups: 0% (187.7 ± 120.3)B, 10% (795.4 ± 688.1)B, 15% (1999.9 ± 1258.6)A, 20% (1911.5 ± 596.8)A, and 30% (2090.6 ± 656.7)A, and for flexural modulus (GPa) FR-groups: 0% (2065.63 ± 882.15)B, 10% (4479.06 ± 3019.82)AB, 15% (5694.89 ± 2790.3)A, 20% (6042.11 ± 3392.13)A, and 30% (2495.67 ± 1345.86)B; UR-groups: 0% (1090.08 ± 708.81)C, 10% (7032.13 ± 7864.53)BC, 15% (19331.57 ± 16759.12)AB, 20% (15726.03 ± 8035.09)AB, and 30% (29364.37 ± 13928.96)A. Fiber addiction in BisGMA resin increases flexural properties, and the interaction between resin and fibers seems better in the absence of inorganic fillers increasing flexural properties. PMID:25136595

Effect of glass fiber incorporation on flexural properties of experimental composites.

PubMed

Fonseca, Rodrigo Borges; Marques, Aline Silva; Bernades, Karina de Oliveira; Carlo, Hugo Lemes; Naves, Lucas Zago

2014-01-01

This study evaluated the effect of fiber addiction in flexural properties of 30 wt% silica filled BisGMA resin (FR) or unfilled Bis-GMA (UR). Ten groups were created (N = 10) varying the resin (FR or UR) and quantity of glass fibers (wt%: 0, 10, 15, 20, and 30). Samples (10 × 2 × 1 mm) were submitted to flexural strength test following SEM examination. Data were analyzed by two-way ANOVA, Tukey, and Student t-test (α = 0.05). Results for flexural strength (MPa) were FR-groups: 0% (442.7 ± 140.6)(C), 10% (772.8 ± 446.3)(ABC), 15% (854.7 ± 297.3)(AB), 20% (863.4 ± 418.0)(A), 30% (459.5 ± 140.5)(BC); UR-groups: 0% (187.7 ± 120.3)(B), 10% (795.4 ± 688.1)(B), 15% (1999.9 ± 1258.6)(A), 20% (1911.5 ± 596.8)(A), and 30% (2090.6 ± 656.7)(A), and for flexural modulus (GPa) FR-groups: 0% (2065.63 ± 882.15)(B), 10% (4479.06 ± 3019.82)(AB), 15% (5694.89 ± 2790.3)(A), 20% (6042.11 ± 3392.13)(A), and 30% (2495.67 ± 1345.86)(B); UR-groups: 0% (1090.08 ± 708.81)(C), 10% (7032.13 ± 7864.53)(BC), 15% (19331.57 ± 16759.12)(AB), 20% (15726.03 ± 8035.09)(AB), and 30% (29364.37 ± 13928.96)(A). Fiber addiction in BisGMA resin increases flexural properties, and the interaction between resin and fibers seems better in the absence of inorganic fillers increasing flexural properties.

Gravity anomalies and lithospheric flexure around the Longmen Shan deduced from combinations of in situ observations and EGM2008 data

NASA Astrophysics Data System (ADS)

She, Yawen; Fu, Guangyu; Wang, Zhuohua; Liu, Tai; Xu, Changyi; Jin, Honglin

2016-10-01

The current work describes the combined data of three field campaigns, spanning 2009-2013. Their joint gravity and GPS observations thoroughly cover the sites of lithospheric flexure between the Sichuan Basin and the Eastern Tibetan Plateau. The study area's free-air gravity anomalies (FGAs) are updated by using a remove-and-restore algorithm which merges EGM2008 data with in situ observations. These new FGAs show pairs of positive and negative anomalies along the eastern edges of the Tibetan Plateau. The FGAs are used to calculate effective elastic thickness ( T e) and load ratios ( F) of the lithosphere. Admittance analysis indicates the T e of Longmen Shan (LMS) to be 6 km, and profile analysis indicates that the T e of the Sichuan Basin excesses 30 km. The load ratio ( F 1 = 1) confirms that the lithospheric flexure of the LMS area can be attributed solely to the surface load of the crust. [Figure not available: see fulltext. Caption: The current work describes the combined data of three field campaigns, spanning 2009-2013. Their joint gravity and GPS observations thoroughly cover the sites of lithospheric flexure between the Sichuan Basin and the Eastern Tibetan Plateau. The study area's free-air gravity anomalies (FGAs) are updated by using a remove-and-restore algorithm which merges EGM2008 data with in situ observations. With the new FGAs data, the lithospheric strength of the study area is studied by the authors, and they also give a combined model to illustrate the uplift mechanism of this area.

Evaluation of acceptance strength tests for concrete pavements.

DOT National Transportation Integrated Search

2005-06-30

The North Carolina Department of Transportation has used traditionally flexural strength tests for acceptance : testing of Portland cement concrete pavements. This report summarizes a research project implemented to : investigate the feasibility of u...

Pervious concrete mix optimization for sustainable pavement solution

NASA Astrophysics Data System (ADS)

Barišić, Ivana; Galić, Mario; Netinger Grubeša, Ivanka

2017-10-01

In order to fulfill requirements of sustainable road construction, new materials for pavement construction are investigated with the main goal to preserve natural resources and achieve energy savings. One of such sustainable pavement material is pervious concrete as a new solution for low volume pavements. To accommodate required strength and porosity as the measure of appropriate drainage capability, four mixtures of pervious concrete are investigated and results of laboratory tests of compressive and flexural strength and porosity are presented. For defining the optimal pervious concrete mixture in a view of aggregate and financial savings, optimization model is utilized and optimal mixtures defined according to required strength and porosity characteristics. Results of laboratory research showed that comparing single-sized aggregate pervious concrete mixtures, coarse aggregate mixture result in increased porosity but reduced strengths. The optimal share of the coarse aggregate turn to be 40.21%, the share of fine aggregate is 49.79% for achieving required compressive strength of 25 MPa, flexural strength of 4.31 MPa and porosity of 21.66%.

Analysis on Flexural Strength of A36 Mild Steel by Design of Experiment (DOE)

NASA Astrophysics Data System (ADS)

Nurulhuda, A.; Hafizzal, Y.; Izzuddin, MZM; Sulawati, MRN; Rafidah, A.; Suhaila, Y.; Fauziah, AR

2017-08-01

Nowadays demand for high quality and reliable components and materials are increasing so flexural tests have become vital test method in both the research and manufacturing process and development to explain in details about the material’s ability to withstand deformation under load. Recently, there are lack research studies on the effect of thickness, welding type and joint design on the flexural condition by DOE approach method. Therefore, this research will come out with the flexural strength of mild steel since it is not well documented. By using Design of Experiment (DOE), a full factorial design with two replications has been used to study the effects of important parameters which are welding type, thickness and joint design. The measurement of output response is identified as flexural strength value. Randomize experiments was conducted based on table generated via Minitab software. A normal probability test was carried out using Anderson Darling Test and show that the P-value is <0.005. Thus, the data is not normal since there is significance different between the actual data with the ideal data. Referring to the ANOVA, only factor joint design is significant since the P-value is less than 0.05. From the main plot and interaction plot, the recommended setting for each of parameters were suggested as high level for welding type, high level for thickness and low level for joint design. The prediction model was developed thru regression in order to measure effect of output response for any changes on parameters setting. In the future, the experiments can be enhanced using Taguchi methods in order to do verification of result.

The residual monomer content and mechanical properties of CAD\\CAM resins used in the fabrication of complete dentures as compared to heat cured resins

PubMed Central

Ayman, Al-Dharrab

2017-01-01

Background The utilization of computer-assisted designing and computer-assisted milling CAD\\CAM resins in the fabrication of removable prostheses is a modern-day concept that offers many advantages over the use of the traditional polymethylmethacrylate (PMMA). Aim This study instigated some of the mechanical properties of CAD\\CAM denture base resin including the amount of residual monomer. Methods This study was conducted at the Faculty of Dentistry, King Abdulaziz University from October 2016 to February 2017. A total of seventy rectangular specimens were fabricated (group A: 35 heat-cured PMMA and group B: 35 CAD/CAM pre-polymerized acrylic resin blocks). The flexural strength and surface hardness were tested while the residual monomer content at baseline, two-day and seven-day intervals was estimated using gas chromatography (GC). Means and standard deviations were determined for each group as well as independent-samples t-test and ANOVA with repeated measures for comparison between the groups and subgroups of varying time intervals. Results Heat cured PMMA (A), displayed higher flexural strength and low value flexural modulus compared to CAD/CAM acrylic resin denture base material (B). Student t-test indicated highly significant differences (p<0.001) of the flexural strength (t=37.911) and flexural modulus (t=88.559). The surface hardness of group (B) was significantly higher compared to group (A) as indicated by the t-test (t=20.430). Higher release of the monomer content was detected by GC in group (A) at different time intervals with a statistically significant difference (p<0.001) in residual monomer content. Conclusion CAD/CAM resin may be considered suitable for use in the construction of denture bases. PMID:28894533

Biobased Epoxy Resins from Deconstructed Native Softwood Lignin.

PubMed

van de Pas, Daniel J; Torr, Kirk M

2017-08-14

The synthesis of novel epoxy resins from lignin hydrogenolysis products is reported. Native lignin in pine wood was depolymerized by mild hydrogenolysis to give an oil product that was reacted with epichlorohydrin to give epoxy prepolymers. These were blended with bisphenol A diglycidyl ether or glycerol diglycidyl ether and cured with diethylenetriamine or isophorone diamine. The key novelty of this work lies in using the inherent properties of the native lignin in preparing new biobased epoxy resins. The lignin-derived epoxy prepolymers could be used to replace 25-75% of the bisphenol A diglycidyl ether equivalent, leading to increases of up to 52% in the flexural modulus and up to 38% in the flexural strength. Improvements in the flexural strength were attributed to the oligomeric products present in the lignin hydrogenolysis oil. These results indicate lignin hydrogenolysis products have potential as sustainable biobased polyols in the synthesis of high performance epoxy resins.

Processing and Mechanical Properties of Macro Polyamide Fiber Reinforced Concrete

PubMed Central

Jeon, Joong Kyu; Kim, WooSeok; Jeon, Chan Ki; Kim, Jin Cheol

2014-01-01

This study developed a macro-sized polyamide (PA) fiber for concrete reinforcement and investigated the influence of the PA fiber on flexural responses in accordance with ASTM standards. PA fibers are advantageous compared to steel fibers that are corrosive and gravitated. The macro-sized PA fiber significantly improved concrete ductility and toughness. Unlike steel fibers, the PA fibers produced two peak bending strengths. The first-peaks occurred near 0.005 mm of deflection and decreased up to 0.5 mm of deflection. Then the bending strength increased up to second-peaks until the deflections reached between 1.0 and 1.5 mm. The averaged flexural responses revealed that PA fiber content did not significantly influence flexural responses before L/600, but had significant influence thereafter. Toughness performance levels were also determined, and the results indicated more than Level II at L/600 and Level IV at others. PMID:28788265

Processing and Mechanical Properties of Macro Polyamide Fiber Reinforced Concrete.

PubMed

Jeon, Joong Kyu; Kim, WooSeok; Jeon, Chan Ki; Kim, Jin Cheol

2014-11-26

This study developed a macro-sized polyamide (PA) fiber for concrete reinforcement and investigated the influence of the PA fiber on flexural responses in accordance with ASTM standards. PA fibers are advantageous compared to steel fibers that are corrosive and gravitated. The macro-sized PA fiber significantly improved concrete ductility and toughness. Unlike steel fibers, the PA fibers produced two peak bending strengths. The first-peaks occurred near 0.005 mm of deflection and decreased up to 0.5 mm of deflection. Then the bending strength increased up to second-peaks until the deflections reached between 1.0 and 1.5 mm. The averaged flexural responses revealed that PA fiber content did not significantly influence flexural responses before L /600, but had significant influence thereafter. Toughness performance levels were also determined, and the results indicated more than Level II at L /600 and Level IV at others.

Design optimization of continuous partially prestressed concrete beams

NASA Astrophysics Data System (ADS)

Al-Gahtani, A. S.; Al-Saadoun, S. S.; Abul-Feilat, E. A.

1995-04-01

An effective formulation for optimum design of two-span continuous partially prestressed concrete beams is described in this paper. Variable prestressing forces along the tendon profile, which may be jacked from one end or both ends with flexibility in the overlapping range and location, and the induced secondary effects are considered. The imposed constraints are on flexural stresses, ultimate flexural strength, cracking moment, ultimate shear strength, reinforcement limits cross-section dimensions, and cable profile geometries. These constraints are formulated in accordance with ACI (American Concrete Institute) code provisions. The capabilities of the program to solve several engineering problems are presented.

Characterization of the bioactive and mechanical behavior of dental ceramic/sol-gel derived bioactive glass mixtures.

PubMed

Abbasi, Zahra; Bahrololoum, Mohammad E; Bagheri, Rafat; Shariat, Mohammad H

2016-02-01

Dental ceramics can be modified by bioactive glasses in order to develop apatite layer on their surface. One of the benefits of such modification is to prolong the lifetime of the fixed dental prosthesis by preventing the formation of secondary caries. Dental ceramic/sol-gel derived bioactive glass mixture is one of the options for this modification. In the current study, mixtures of dental ceramic/bioactive glass with different compositions were successfully produced. To evaluate their bioactive behavior, prepared samples were immersed in a simulated body fluid at various time intervals. The prepared and soaked specimens were characterized using Fourier transform infrared spectroscopy, X-ray diffractometry and scanning electron microscopy. Since bioactive glasses have deleterious effects on the mechanical properties of dental ceramics, 3-point bending tests were used to evaluate the flexural strength, flexural strain, tangent modulus of elasticity and Weibull modulus of the specimens in order to find the optimal relationship between mechanical and bioactive properties. Copyright © 2015 Elsevier Ltd. All rights reserved.

Design and Fabrication of 3D printed Scaffolds with a Mechanical Strength Comparable to Cortical Bone to Repair Large Bone Defects

PubMed Central

Roohani-Esfahani, Seyed-Iman; Newman, Peter; Zreiqat, Hala

2016-01-01

A challenge in regenerating large bone defects under load is to create scaffolds with large and interconnected pores while providing a compressive strength comparable to cortical bone (100–150 MPa). Here we design a novel hexagonal architecture for a glass-ceramic scaffold to fabricate an anisotropic, highly porous three dimensional scaffolds with a compressive strength of 110 MPa. Scaffolds with hexagonal design demonstrated a high fatigue resistance (1,000,000 cycles at 1–10 MPa compressive cyclic load), failure reliability and flexural strength (30 MPa) compared with those for conventional architecture. The obtained strength is 150 times greater than values reported for polymeric and composite scaffolds and 5 times greater than reported values for ceramic and glass scaffolds at similar porosity. These scaffolds open avenues for treatment of load bearing bone defects in orthopaedic, dental and maxillofacial applications. PMID:26782020

Design and Fabrication of 3D printed Scaffolds with a Mechanical Strength Comparable to Cortical Bone to Repair Large Bone Defects

NASA Astrophysics Data System (ADS)

Roohani-Esfahani, Seyed-Iman; Newman, Peter; Zreiqat, Hala

2016-01-01

A challenge in regenerating large bone defects under load is to create scaffolds with large and interconnected pores while providing a compressive strength comparable to cortical bone (100-150 MPa). Here we design a novel hexagonal architecture for a glass-ceramic scaffold to fabricate an anisotropic, highly porous three dimensional scaffolds with a compressive strength of 110 MPa. Scaffolds with hexagonal design demonstrated a high fatigue resistance (1,000,000 cycles at 1-10 MPa compressive cyclic load), failure reliability and flexural strength (30 MPa) compared with those for conventional architecture. The obtained strength is 150 times greater than values reported for polymeric and composite scaffolds and 5 times greater than reported values for ceramic and glass scaffolds at similar porosity. These scaffolds open avenues for treatment of load bearing bone defects in orthopaedic, dental and maxillofacial applications.

Recycling of Malaysia's electric arc furnace (EAF) slag waste into heavy-duty green ceramic tile.

PubMed

Teo, Pao-Ter; Anasyida, Abu Seman; Basu, Projjal; Nurulakmal, Mohd Sharif

2014-12-01

Recently, various solid wastes from industry such as glass waste, fly ash, sewage sludge and slag have been recycled into various value-added products such as ceramic tile. The conventional solutions of dumping the wastes in landfills or incineration, including in Malaysia are getting obsolete as the annual huge amount of the solid wastes would boost-up disposal cost and may cause permanent damage to the flora and fauna. This recent waste recycling approach is much better and greener as it can resolve problems associated with over-limit storage of industrial wastes and reduce exploration of natural resources for ceramic tile to continuously sustain the nature. Therefore, in this project, an attempt was made to recycle electric arc furnace (EAF) slag waste, obtained from Malaysia's steel making industry, into ceramic tile via conventional powder compaction method. The research work was divided into two stages. The first stage was to evaluate the suitability of EAF slag in ceramic tile by varying weight percentage of EAF slag (40 wt.%, 50 wt.% and 60 wt.%) and ball clay (40 wt.%, 50 wt.% and 60 wt.%), with no addition of silica and potash feldspar. In the second stage, the weight percentage of EAF slag was fixed at 40 wt.% and the percentage of ball clay (30 wt.% and 40 wt.%), feldspar (10 wt.% and 20 wt.%) and silica (10 wt.% and 20 wt.%) added was varied accordingly. Results obtained show that as weight percentage of EAF slag increased up to 60 wt.%, the percentage of apparent porosity and water absorption also rose, with a reduction in tile flexural strength and increased porosity. On the other hand, limiting the weight percentage of EAF slag to 40 wt.% while increasing the weight percentage of ball clay led to a higher total percentage of anorthite and wollastonite minerals, resulting in higher flexural strength. It was found that introduction of silica and feldspar further improved the flexural strength due to optimization of densification process. The highest flexural strength, lowest apparent porosity and water absorption of EAF slag based tile was attained at the composition of 40 wt.% EAF slag--30 wt.% ball clay--10 wt.% feldspar--20 wt.% silica. The properties of ceramic tile made with EAF slag waste (up to 40 wt.%), especially flexural strength are comparable to those of commercial ceramic tile and are, therefore, suitable as high flexural strength and heavy-duty green ceramic floor tile. Continuous development is currently underway to improve the properties of tile so that this recycling approach could be one of the potential effective, efficient and sustainable solutions in sustaining our nature. Copyright © 2014 Elsevier Ltd. All rights reserved.

Influence of fibre reinforcement on selected mechanical properties of dental composites.

PubMed

Niewczas, Agata M; Zamościńska, Jolanta; Krzyżak, Aneta; Pieniak, Daniel; Walczak, Agata; Bartnik, Grzegorz

2017-01-01

For splinting or designing adhesive bridges, reconstructive composite structures with increased mechanical properties owing to embedded reinforcement fibres are used. The aim of this article was to determine the influence of glass and aramid fibres on the mechanical strength of composites reinforced with these fibres. Two polymer-ceramic microhybrid materials: Boston and Herculite were tested. Three types of reinforcement fibres were used: aramid (Podwiązka) with a single layer weave, a single layer weave glass fibre (FSO) and triple layer weave glass fibre (FSO evo). Tests were conducted in accordance with the requirements of ISO 4049:2009. The following material types were chosen for research: Boston, Boston + Podwiązka, Herculite, Herculite + Podwiązka, Herculite + FSO and Herculite + FSO evo. The scope of research included: flexural strength B, bending modulus of elasticity εB and work to failure of the reinforced composite Wfb. Additionally, microscopic observations of fracture occurring in samples were made. In comparison: the Herculite (97.7 MPa) type with the Herculite + FSO evo (177.5 MPa) type was characterized by the highest strength. Fibre reinforcement resulted in decreasing the elasticity modulus: Herculite + reinforcement (6.86 GPa; 6.33 GPa; 6.11 GPa) in comparison with the Herculite (9.84 GPa) and respectively Boston + reinforcement (10.08 GPa) as compared with the Boston (11.81 GPa). Using glass fibres increases flexural strength of the test composites. Using aramid fibres does not change their strength. The elasticity modulus of the reinforced reconstructive structures decreases after application of either type of fibres. However, their resistance to the crack initiation increases.

Development of sugar palm yarn/glass fibre reinforced unsaturated polyester hybrid composites

NASA Astrophysics Data System (ADS)

Nurazzi, N. Mohd; Khalina, A.; Sapuan, S. Mohd; Rahmah, M.

2018-04-01

This study investigates the effect of fibre hybridization for sugar palm yarn fibre with glass fibre reinforced with unsaturated polyester composites. In this work, unsaturated polyester resin are reinforced with fibre at a ratio of 70:30 wt% and 60:40 wt%. The hybrid composites were characterized in terms of physical (density and water absorption), mechanical (tensile, flexural and compression) and thermal properties through thermal gravimetry analysis (TGA). Density determination showed that density increased with higher wt% of glass fibre. The inherently higher density of glass fibre increased the density of hybrid composite. Resistance to water absorption is improved upon the incorporation of glass fibre and the hybrid composites were found to reach equilibrium absorption at days 4 and 5. As for mechanical performance, the highest tensile strength, tensile modulus, flexural strength, flexural modulus and compression strength were obtained from 40 wt% of fibres reinforcement with ratio of 50:50 wt% of sugar palm yarn fibre and glass fibre reinforced unsaturated polyester composites. The increase of glass fibre loading had a synergistic effect on the mechanical properties to the composites structure due to its superior strength and modulus. The thermal stability of hybrid composites was improved by the increase of onset temperature and the reduction of residues upon increase in temperature.

Influence of Curing on the Strength Development of Calcium-Containing Geopolymer Mortar

PubMed Central

Li, Xueying; Wang, Zheng; Jiao, Zhenzhen

2013-01-01

This paper investigated the curing effects on the mechanical properties of calcium-containing geopolymer mortar. Three precursors are used: Class C fly ash, Class F fly ash plus calcium hydroxide and Class F fly ash plus slag. Curing conditions included: (1) standard curing at 20 ± 3 °C and RH 95% (C); (2) steam curing at 60 °C for 24 h (S); (3) steam curing at 60 °C for 6 h (S6); and (4) oven curing at 60 °C for 24 h (O), then the latter three followed by the standard curing. Under the standard conditions, the flexural strength and compressive strength of Class C fly ash geopolymer mortars developed quickly until the age of 7 days, followed by a gradual increase. Specimens with Class F fly ash plus Ca(OH)2 showed slow increase till the age of 28 days. Under these non-standard conditions (2–4), all specimens showed higher 3-day strength, while later strengths were either higher or lower than those in standard conditions, depending on the type of the precursor. PMID:28788377

Influence of Curing on the Strength Development of Calcium-Containing Geopolymer Mortar.

PubMed

Li, Xueying; Wang, Zheng; Jiao, Zhenzhen

2013-11-07

This paper investigated the curing effects on the mechanical properties of calcium-containing geopolymer mortar. Three precursors are used: Class C fly ash, Class F fly ash plus calcium hydroxide and Class F fly ash plus slag. Curing conditions included: (1) standard curing at 20 ± 3 °C and RH 95% (C); (2) steam curing at 60 °C for 24 h (S); (3) steam curing at 60 °C for 6 h (S6); and (4) oven curing at 60 °C for 24 h (O), then the latter three followed by the standard curing. Under the standard conditions, the flexural strength and compressive strength of Class C fly ash geopolymer mortars developed quickly until the age of 7 days, followed by a gradual increase. Specimens with Class F fly ash plus Ca(OH)₂ showed slow increase till the age of 28 days. Under these non-standard conditions (2-4), all specimens showed higher 3-day strength, while later strengths were either higher or lower than those in standard conditions, depending on the type of the precursor.

Investigation of Usability as Aggregate of Different Originated Rocks

NASA Astrophysics Data System (ADS)

Başpinar Tuncay, Ebru; Kilinçarslan, Şemsettin; Yağmurlu, Fuzuli

2016-10-01

The general properties of aggregate can determine the performance and durability of the concrete. In this study, mineralogical, petrographic, mechanical, physical and chemical properties of the rock samples of different origin (limestone, recrystallized limestone, dolomite, sand and gravel, tephra-phonolite, trachybasalt) were determined. Samples were obtained from different origin rocks units and they have been classified in three different sizes of aggregate with crushing and screening method. Grading, classification of particle, loose bulk density, water absorption ratio, flakiness index, coefficient of Los Angeles, resistance to freeze-loosening and alkali-silica reaction of aggregates and organic matter determination has been determined. The rocks have been investigated in compliance with the relevant standards. Trachybasalt and dolomite have higher particle density than other rocks. In addition, strength and flexural strength of these rocks are higher than other rocks. Tephra-phonolite has the lowest water absorption rate. At the same time resistance to freeze loosening of Tephra- phonolite is lower than the other rocks. Resistance to fragmentation and the resistance to wear of all of rocks are quite high. Sand and gravel, tephra-phonolite and trachybasalt are evaluated in terms of alkali-silica reaction. Sand and gravel are more reactive than the other aggregates. Organic matter content of the aggregates is low for the quality of aggregate. Also high correlation between some properties of aggregates was observed. For example, high correlation between compressive strength and flexural strength, water absorption and porosity, resistance to fragmentation and the resistance to ware (Micro-Deval).

Reliability, failure probability, and strength of resin-based materials for CAD/CAM restorations

PubMed Central

Lim, Kiatlin; Yap, Adrian U-Jin; Agarwalla, Shruti Vidhawan; Tan, Keson Beng-Choon; Rosa, Vinicius

2016-01-01

ABSTRACT Objective: This study investigated the Weibull parameters and 5% fracture probability of direct, indirect composites, and CAD/CAM composites. Material and Methods: Discshaped (12 mm diameter x 1 mm thick) specimens were prepared for a direct composite [Z100 (ZO), 3M-ESPE], an indirect laboratory composite [Ceramage (CM), Shofu], and two CAD/CAM composites [Lava Ultimate (LU), 3M ESPE; Vita Enamic (VE), Vita Zahnfabrik] restorations (n=30 for each group). The specimens were polished, stored in distilled water for 24 hours at 37°C. Weibull parameters (m= modulus of Weibull, σ0= characteristic strength) and flexural strength for 5% fracture probability (σ5%) were determined using a piston-on-three-balls device at 1 MPa/s in distilled water. Statistical analysis for biaxial flexural strength analysis were performed either by both one-way ANOVA and Tukey's post hoc (α=0.05) or by Pearson's correlation test. Results: Ranking of m was: VE (19.5), LU (14.5), CM (11.7), and ZO (9.6). Ranking of σ0 (MPa) was: LU (218.1), ZO (210.4), CM (209.0), and VE (126.5). σ5% (MPa) was 177.9 for LU, 163.2 for CM, 154.7 for Z0, and 108.7 for VE. There was no significant difference in the m for ZO, CM, and LU. VE presented the highest m value and significantly higher than ZO. For σ0 and σ5%, ZO, CM, and LU were similar but higher than VE. Conclusion: The strength characteristics of CAD/ CAM composites vary according to their composition and microstructure. VE presented the lowest strength and highest Weibull modulus among the materials. PMID:27812614

Behaviour of concrete beams reinforced withFRP prestressed concrete prisms

NASA Astrophysics Data System (ADS)

Svecova, Dagmar

The use of fibre reinforced plastics (FRP) to reinforce concrete is gaining acceptance. However, due to the relatively low modulus of FRP, in comparison to steel, such structures may, if sufficient amount of reinforcement is not used, suffer from large deformations and wide cracks. FRP is generally more suited for prestressing. Since it is not feasible to prestress all concrete structures to eliminate the large deflections of FRP reinforced concrete flexural members, researchers are focusing on other strategies. A simple method for avoiding excessive deflections is to provide sufficiently high amount of FRP reinforcement to limit its stress (strain) to acceptable levels under service loads. This approach will not be able to take advantage of the high strength of FRP and will be generally uneconomical. The current investigation focuses on the feasibility of an alternative strategy. This thesis deals with the flexural and shear behaviour of concrete beams reinforced with FRP prestressed concrete prisms. FRP prestressed concrete prisms (PCP) are new reinforcing bars, made by pretensioning FRP and embedding it in high strength grout/concrete. The purpose of the research is to investigate the feasibility of using such pretensioned rebars, and their effect on the flexural and shear behaviour of reinforced concrete beams over the entire loading range. Due to the prestress in the prisms, deflection of concrete beams reinforced with this product is substantially reduced, and is comparable to similarly steel reinforced beams. The thesis comprises both theoretical and experimental investigations. In the experimental part, nine beams reinforced with FRP prestressed concrete prisms, and two companion beams, one steel and one FRP reinforced were tested. All the beams were designed to carry the same ultimate moment. Excellent flexural and shear behaviour of beams reinforced with higher prestressed prisms is reported. When comparing deflections of three beams designed to have the same ultimate capacity, but reinforced with either steel, PCP or FRP rebars, the service load deflections of beams reinforced with PCP are comparable to that of a steel reinforced concrete beam, and are four times smaller than the deflection of the companion FRP reinforced beam. Similarly, the crack width of the PCP reinforced beams under service loads is comparable to that of the steel reinforced beam while the FRP reinforced beam developed unacceptably wide cracks. In the analytical part comprehensive analysis of the experimental data in both flexure and shear is performed. It is determined that the existing design expressions for ultimate flexural strength and service load deflection calculation cannot accurately predict the response of PCP reinforced beams. Accordingly, new expressions for calculation of deflection, crack width, tension stiffening, and ultimate capacity of the PCP reinforced beams are proposed. The predictions of the proposed methods of analysis agree very well with the corresponding experimental data. Based on the results of the current study, it is concluded that high strength concrete prisms prestressed with carbon fibre reinforced plastic bars can be used as reinforcement in concrete structures to avoid the problems of large deflections and wide cracks under service loads.

Influence of core thickness and artificial aging on the biaxial flexural strength of different all-ceramic materials: An in-vitro study.

PubMed

Dikicier, Sibel; Ayyildiz, Simel; Ozen, Julide; Sipahi, Cumhur

2017-05-31

The purpose of this study was to investigate the flexural strength of all-ceramics with varying core thicknesses submitted to aging. In-Ceram Alumina (IC), IPS e.max Press (EM) and Katana (K) (n=40), were selected. Each group contained two core groups based on the core thickness as follows: IC/0.5, IC/0.8, EM/0.5, EM/0.8, K/0.5 and K/0.8 mm in thickness (n=20 each). Ten specimens from each group were subjected to aging and all specimens were tested for strength in a testing machine either with or without being subjected aging. The mean strength of the K were higher (873.05 MPa) than that of the IC (548.28 MPa) and EM (374.32 MPa) regardless of core thickness. Strength values increased with increasing core thickness for all IC, EM and K regardless of aging. Results of this study concluded that strength was not significantly affected by aging. Different core thicknesses affected strength of the all-ceramic materials tested (p<0.05).

Properties and uses of concrete, appendix B

NASA Technical Reports Server (NTRS)

Corley, Gene

1992-01-01

Concretes that can now be formed have properties which may make them valuable for lunar or space construction. These properties include high compressive strength, good flexural strength (when reinforced), and favorable responses to temperature extremes (even increased strength at low temperatures). These and other properties of concrete are discussed.

Light-curing reinforcement for denture base resin using a glass fiber cloth pre-impregnated with various urethane oligomers.

PubMed

Kanie, Takahito; Arikawa, Hiroyuki; Fujii, Koichi; Ban, Seiji

2004-09-01

The purpose of this study was to investigate the flexural properties of denture base resin reinforced using glass fiber cloth and a urethane oligomer. The five types of oligomer used in this study were S5, S9, S3, U4, and U6, which have varying functional groups and viscosities. The flexural properties of S9 with glass fiber cloth could not be measured because S9 is elastic. In the heat-cured resin reinforced with S9, the reinforcement peeled away from the resin. In the self- and light-cured resins reinforced with S9, the flexural properties increased significantly. When reinforced with the other four oligomers (S5, S3, U4, and U6), the flexural strength and flexural modulus of the self-, heat-, and light-cured resins increased significantly (p<0.01).

Effects of seawater and deionized water at 0 to 80 deg C on the flexural properties of a glass/epoxy composite

NASA Technical Reports Server (NTRS)

Penn, B. G.; Daniels, J. G.; Ledbetter, F. E., III; Semmel, M. L.; Goldberg, B. G.; White, W. T.; Clemons, J. M.

1986-01-01

The effect on the flexural properties of a glass/epoxy composite of immersion in deionized water or seawater at 0, 25, and 80 C for 451 hr was examined. The percent weight gain at 0 and 25 C was low (0.06 to 0.17 percent) and there was no significant change in the flexural properties for these environmental conditions. At 80 C there was a decrease in the flexural strength of 17 and 20 percent in seawater and deionized water, respectively. This is a comparison to control samples exposed to 80 C heat alone. These decreases were found to be nearly reversible once the samples were dried. Optical microscopy did not reveal cracking of the matrix. The flexural modulus was essentially unaffected by exposure to deionized water and seawater at 80 C.

Investigation of concrete containing condensed silica fume.

DOT National Transportation Integrated Search

1986-01-01

The properties of hydraulic cement concretes containing silica fume were investigated to assess their suitability for use in overlays with s minimum thickness of 1 1/4 in. The properties studied were compressive and flexural strengths, bond strength,...

Properties of concrete containing ground palm oil fuel ash as fine aggregate replacement

NASA Astrophysics Data System (ADS)

Saffuan, W. A.; Muthusamy, K.; Salleh, N. A. Mohd; Nordin, N.

2017-11-01

Environmental degradation resulting from increasing sand mining activities and disposal of palm oil fuel ash (POFA), a solid waste generated from palm oil mill needs to be resolved. Thus, the present research investigates the effect of ground palm oil fuel ash as partial fine aggregate replacement on workability, compressive and flexural strength of concrete. Five mixtures of concrete containing POFA as partial sand replacement designed with 0%, 10%, 20%, 30% and 40% of POFA by the weight of sand were used in this experimental work. The cube and beam specimens were casted and water cured up to 28 days before subjected to compressive strength and flexural strength testing respectively. Finding shows that concrete workability reduces as the amount of POFA added become larger. It is worth to note that 10% of POFA is the best amount to be used as partial fine aggregate replacement to produce concrete with enhanced strength.

Effect of long-term water immersion or thermal shock on mechanical properties of high-impact acrylic denture base resins.

PubMed

Sasaki, Hirono; Hamanaka, Ippei; Takahashi, Yutaka; Kawaguchi, Tomohiro

2016-01-01

The purpose of this study was to investigate the effect of long-term water immersion or thermal shock on the mechanical properties of high-impact acrylic denture base resins. Two high-impact acrylic denture base resins were selected for the study. Specimens of each denture base material tested were fabricated according to the manufacturers' instructions (n=10). The flexural strength at the proportional limit, the elastic modulus and the impact strength of the specimens were evaluated. The flexural strength at the proportional limit of the high-impact acrylic denture base resins did not change after six months' water immersion or thermocycling 50,000 times. The elastic moduli of the high-impact acrylic denture base resins significantly increased after six months' water immersion or thermocycling 50,000 times. The impact strengths of the high-impact acrylic denture base resins significantly decreased after water immersion or thermocycling as described above.

Strength and Durability of Fly Ash-Based Fiber-Reinforced Geopolymer Concrete in a Simulated Marine Environment

NASA Astrophysics Data System (ADS)

Martinez Rivera, Francisco Javier

This research is aimed at investigating the corrosion durability of polyolefin fiberreinforced fly ash-based geopolymer structural concrete (hereafter referred to as GPC, in contradistinction to unreinforced geopolymer concrete referred to as simply geopolymer concrete), where cement is completely replaced by fly ash, that is activated by alkalis, sodium hydroxide and sodium silicate. The durability in a marine environment is tested through an electrochemical method for accelerated corrosion. The GPC achieved compressive strengths in excess of 6,000 psi. Fiber reinforced beams contained polyolefin fibers in the amounts of 0.1%, 0.3%, and 0.5% by volume. After being subjected to corrosion damage, the GPC beams were analyzed through a method of crack scoring, steel mass loss, and residual flexural strength testing. Fiber reinforced GPC beams showed greater resistance to corrosion damage with higher residual flexural strength. This makes GPC an attractive material for use in submerged marine structures.

Mechanical and Morphological Properties of Polypropylene/Nano α-Al2O3 Composites

PubMed Central

Mirjalili, F.; Chuah, L.; Salahi, E.

2014-01-01

A nanocomposite containing polypropylene (PP) and nano α-Al2O3 particles was prepared using a Haake internal mixer. Mechanical tests, such as tensile and flexural tests, showed that mechanical properties of the composite were enhanced by addition of nano α-Al2O3 particles and dispersant agent to the polymer. Tensile strength was approximately ∼16% higher than pure PP by increasing the nano α-Al2O3 loading from 1 to 4 wt% into the PP matrix. The results of flexural analysis indicated that the maximum values of flexural strength and flexural modulus for nanocomposite without dispersant were 50.5 and 1954 MPa and for nanocomposite with dispersant were 55.88 MPa and 2818 MPa, respectively. However, higher concentration of nano α-Al2O3 loading resulted in reduction of those mechanical properties that could be due to agglomeration of nano α-Al2O3 particles. Transmission and scanning electron microscopic observations of the nanocomposites also showed that fracture surface became rougher by increasing the content of filler loading from 1 to 4% wt. PMID:24688421

Edge chipping and flexural resistance of monolithic ceramics☆

PubMed Central

Zhang, Yu; Lee, James J.-W.; Srikanth, Ramanathan; Lawn, Brian R.

2014-01-01

Objective Test the hypothesis that monolithic ceramics can be developed with combined esthetics and superior fracture resistance to circumvent processing and performance drawbacks of traditional all-ceramic crowns and fixed-dental-prostheses consisting of a hard and strong core with an esthetic porcelain veneer. Specifically, to demonstrate that monolithic prostheses can be produced with a much reduced susceptibility to fracture. Methods Protocols were applied for quantifying resistance to chipping as well as resistance to flexural failure in two classes of dental ceramic, microstructurally-modified zirconias and lithium disilicate glass–ceramics. A sharp indenter was used to induce chips near the edges of flat-layer specimens, and the results compared with predictions from a critical load equation. The critical loads required to produce cementation surface failure in monolithic specimens bonded to dentin were computed from established flexural strength relations and the predictions validated with experimental data. Results Monolithic zirconias have superior chipping and flexural fracture resistance relative to their veneered counterparts. While they have superior esthetics, glass–ceramics exhibit lower strength but higher chip fracture resistance relative to porcelain-veneered zirconias. Significance The study suggests a promising future for new and improved monolithic ceramic restorations, with combined durability and acceptable esthetics. PMID:24139756

Preparation and Various Characteristics of Epoxy/Alumina Nanocomposites

NASA Astrophysics Data System (ADS)

Kozako, Masahiro; Ohki, Yoshimichi; Kohtoh, Masanori; Okabe, Shigemitsu; Tanaka, Toshikatsu

Epoxy/ alumina nanocomposites were newly prepared by dispersing 3, 5, 7, and 10 weight (wt) % boehmite alumina nanofillers in a bisphenol-A epoxy resin using a special two-stage direct mixing method. It was confirmed by scanning electron microscopy imaging that the nanofillers were homogeneously dispersed in the epoxy matrix. Dielectric, mechanical, and thermal properties were investigated. It was elucidated that nanofillers affects various characteristics of epoxy resins, when they are nanostructrued. Such nano-effects we obtained are summarized as follows. Partial discharge resistance increases as the filler content increases; e.g. 7 wt% nanofiller content creates a 60 % decrease in depth of PD-caused erosion. Weibull analysis shows that short-time electrical treeing breakdown time is prolonged to 265 % by 5 wt% addition of nanofillers. But there was more data scatter in nanocomposites than in pure epoxy. Permittivity tends to increase from 3.7 to 4.0 by 5 wt% nanofiller addition as opposed to what was newly found in the recent past. Glass transition temperature remains unchanged as 109 °C. Mechanical properties such as flexural strength and flexural modulus increase; e.g. flexural strength and flexural modulus are improved by 5 % and 8 % with 5 wt% content, respectively. Excess addition causes a reverse effect. It is concluded from permittivity and glass transition temperature characteristics that interfacial bonding seems to be more or less weak in the nanocomposite specimens prepared this time, even though mechanical strengths increase. There is a possibility that the nanocomposites specimens will be improved in interfacial quality.

An experimental study of the mechanism of failure of rocks under borehole jack loading

NASA Technical Reports Server (NTRS)

Van, T. K.; Goodman, R. E.

1971-01-01

Laboratory and field tests with an experimental jack and an NX-borehole jack are reported. The following conclusions were made: Under borehole jack loading, a circular opening in a brittle solid fails by tensile fracturing when the bearing plate width is not too small. Two proposed contact stress distributions can explain the mechanism of tensile fracturing. The contact stress distribution factor is a material property which can be determined experimentally. The borehole tensile strength is larger than the rupture flexural strength. Knowing the magnitude and orientation of the in situ stress field, borehole jack test results can be used to determine the borehole tensile strength. Knowing the orientation of the in situ stress field and the flexural strength of the rock substance, the magnitude of the in situ stress components can be calculated. The detection of very small cracks is essential for the accurate determination of the failure loads which are used in the calculation of strengths and stress components.

Development of high temperature resistant graphite fiber coupling agents

NASA Technical Reports Server (NTRS)

Griffin, R. N.

1975-01-01

Surface treatments were investigated as potential coupling agents to improve the elevated temperature shear strength retention of polyimide/graphite and polyphenylquinoxaline/graphite composites. The potential coupling agents were evaluated by fiber strand tensile tests, fiber and composite weight losses at 533 and 588K, and by interlaminar shear strength retention at 533 and 588K. The two surface treatments selected for more extensive evaluation were a coating of Ventromer T-1, a complex organometallic reaction product of titanium tetrachloride and trimethyl borate, and a polyphenylquinoxaline (PPQ) sizing which was pyrolyzed in nitrogen to form a carbonaceous layer on the fiber. Pyrolyzed polyphenylquinoxaline is a satisfactory coupling agent for polyimide/Thornel 300 graphite fiber composites. During 1000 hours aging at 588K such composites lose a little over half their transverse tensile strength, and suffer a slight loss in flexural modulus. No degradation of flexural strength or interlaminar shear strength occured during 1000 hours aging at 588K. None of the coupling agents examined had a markedly beneficial effect with polyphenylquinoxaline composites.

Influences of multiple firings and aging on surface roughness, strength and hardness of veneering ceramics for zirconia frameworks.

PubMed

Tang, Xuehua; Luo, Huinan; Bai, Yang; Tang, Hui; Nakamura, Takashi; Yatani, Hirofumi

2015-09-01

To evaluate the effects of multiple firings and aging on surface roughness, strength, and hardness of veneering ceramics for zirconia frameworks. Five different veneering ceramics for zirconia frameworks were used: Vintage ZR (ZR), Cerabien ZR (CZR), VitaVM9 (VM9), Cercon ceram KISS (KISS), and IPS e.max ceram (e.max). Specimens were fired 2 or 10 times in order to accelerate aging. Surface roughness was evaluated using laser profilometry. Flexural strength and Vickers hardness were also measured. Surface topography was observed using scanning electron microscopy. After accelerated aging, the surface roughness of all specimens fired 10 times was significantly lower than that of the same specimens fired 2 times (P=0.000). Except for VM9, the flexural strength of all specimens fired 10 times was greater than that of the same specimens fired 2 times, and the differences were significant for ZR and CZR (P<0.01). The flexural strength of VM9 fired 10 times was significantly lower than that of VM9 fired 2 times (P=0.034). The Vickers hardness of ZR and VM9 fired 10 times was significantly higher than that of the same specimens fired 2 times (P<0.05), but that of KISS fired 10 times was significantly lower than that of KISS fired 2 times (P=0.000). Multiple firings had a positive effect on the surface roughness of all aged veneering ceramics used for zirconia restorations and on the strength and hardness of many aged veneering ceramics used for zirconia restorations. Copyright © 2015 Elsevier Ltd. All rights reserved.

Improvement of the Shock Absorption Ability of a Face Guard by Incorporating a Glass-Fiber-Reinforced Thermoplastic and Buffering Space

PubMed Central

Churei, Hiroshi; Takayanagi, Haruka; Iwasaki, Naohiko; Takahashi, Hidekazu; Uo, Motohiro

2018-01-01

This study aimed to evaluate the shock absorption ability of trial face guards (FGs) incorporating a glass-fiber-reinforced thermoplastic (GF) and buffering space. The mechanical properties of 3.2 mm and 1.6 mm thick commercial medical splint materials (Aquaplast, AP) and experimental GF prepared from 1.6 mm thick AP and fiberglass cloth were determined by a three-point bending test. Shock absorption tests were conducted on APs with two different thicknesses and two types of experimental materials, both with a bottom material of 1.6 mm thick AP and a buffering space of 30 mm in diameter (APS) and with either (i) 1.6 mm thick AP (AP-APS) or (ii)  1.6 mm thick GF (GF-APS) covering the APS. The GF exhibited significantly higher flexural strength (64.4 MPa) and flexural modulus (7.53 GPa) than the commercial specimens. The maximum load of GF-APS was 75% that of 3.2 mm AP, which is widely used clinically. The maximum stress of the GF-APS only could not be determined as its maximum stress is below the limits of the analysis materials used (<0.5 MPa). Incorporating a GF and buffering space would enhance the shock absorption ability; thus, the shock absorption ability increased while the total thickness and weight decreased. PMID:29854774

Improvement of the Shock Absorption Ability of a Face Guard by Incorporating a Glass-Fiber-Reinforced Thermoplastic and Buffering Space.

PubMed

Wada, Takahiro; Churei, Hiroshi; Takayanagi, Haruka; Iwasaki, Naohiko; Ueno, Toshiaki; Takahashi, Hidekazu; Uo, Motohiro

2018-01-01

This study aimed to evaluate the shock absorption ability of trial face guards (FGs) incorporating a glass-fiber-reinforced thermoplastic (GF) and buffering space. The mechanical properties of 3.2 mm and 1.6 mm thick commercial medical splint materials (Aquaplast, AP) and experimental GF prepared from 1.6 mm thick AP and fiberglass cloth were determined by a three-point bending test. Shock absorption tests were conducted on APs with two different thicknesses and two types of experimental materials, both with a bottom material of 1.6 mm thick AP and a buffering space of 30 mm in diameter (APS) and with either (i) 1.6 mm thick AP (AP-APS) or (ii)  1.6 mm thick GF (GF-APS) covering the APS. The GF exhibited significantly higher flexural strength (64.4 MPa) and flexural modulus (7.53 GPa) than the commercial specimens. The maximum load of GF-APS was 75% that of 3.2 mm AP, which is widely used clinically. The maximum stress of the GF-APS only could not be determined as its maximum stress is below the limits of the analysis materials used (<0.5 MPa). Incorporating a GF and buffering space would enhance the shock absorption ability; thus, the shock absorption ability increased while the total thickness and weight decreased.

Effect of Grinding and Multi-Stimuli Aging on the Fatigue Strength of a Y-TZP Ceramic.

PubMed

Silvestri, Tais; Pereira, Gabriel Kalil Rocha; Guilardi, Luis Felipe; Rippe, Marilia Pivetta; Valandro, Luiz Felipe

2018-01-01

This study aimed to investigate the effect of grinding and multi-stimuli aging on the fatigue strength, surface topography and the phase transformation of Y-TZP ceramic. Discs were manufactured according to ISO-6872:2008 for biaxial flexure testing (diameter: 15 mm; thickness: 1.2 mm) and randomly assigned considering two factors "grinding" and "aging": C- control (as-sintered); CA- control + aging; G- ground; GA- ground + aging. Grinding was carried out with coarse diamond burs under water-cooling. Aging protocols consisted of: autoclave (134°C, 2 bars pressure, 20 hours), followed by storage for 365 days (samples were kept untouched at room temperature), and by mechanical cycling (106 cycles by 20 Hz under a load of 50% from the biaxial flexure monotonic tests). Flexural fatigue strengths (20,000 cycles; 6 Hz) were determined under sinusoidal cyclic loading using staircase approach. Additionally, surface topography analysis by FE-SEM and phase transformation analysis by X-ray Diffractometry were performed. Dixon and Mood methodology was used to analyze the fatigue strength data. Grinding promotes alterations of topographical pattern, while aging apparently did not alter it. Grinding triggered t-m phase transformation without impacting the fatigue strength of the Y-TZP ceramic; and aging promoted an intense t-m transformation that resulted in a toughening mechanism leading to higher fatigue strength for as-sintered condition, and a tendency of increase for ground condition (C < CA; G = GA). It concludes that grinding and aging procedures did not affect deleteriously the fatigue strength of the evaluated Y-TZP ceramic, although, it promotes surface topography alterations, except to aging, and t-m phase transformation.

Processing and damage recovery of intrinsic self-healing glass fiber reinforced composites

NASA Astrophysics Data System (ADS)

Sordo, Federica; Michaud, Véronique

2016-08-01

Glass fiber reinforced composites with a self-healing, supramolecular hybrid network matrix were produced using a modified vacuum assisted resin infusion moulding process adapted to high temperature processing. The quality and fiber volume fraction (50%) of the obtained materials were assessed through microscopy and matrix burn-off methods. The thermo-mechanical properties were quantified by means of dynamic mechanical analysis, revealing very high damping properties compared to traditional epoxy-based glass fiber reinforced composites. Self-healing properties were assessed by three-point bending tests. A high recovery of the flexural properties, around 72% for the elastic modulus and 65% of the maximum flexural stress, was achieved after a resting period of 24 h at room temperature. Recovery after low velocity impact events was also visually observed. Applications for this intrinsic and autonomic self-healing highly reinforced composite material point towards semi-structural applications where high damping and/or integrity recovery after impact are required.

Chairside CAD/CAM materials. Part 2: Flexural strength testing.

PubMed

Wendler, Michael; Belli, Renan; Petschelt, Anselm; Mevec, Daniel; Harrer, Walter; Lube, Tanja; Danzer, Robert; Lohbauer, Ulrich

2017-01-01

Strength is one of the preferred parameters used in dentistry for determining clinical indication of dental restoratives. However, small dimensions of CAD/CAM blocks limit reliable measurements with standardized uniaxial bending tests. The objective of this study was to introduce the ball-on-three-ball (B3B) biaxial strength test for dental for small CAD/CAM block in the context of the size effect on strength predicted by the Weibull theory. Eight representative chairside CAD/CAM materials ranging from polycrystalline zirconia (e.max ZirCAD, Ivoclar-Vivadent), reinforced glasses (Vitablocs Mark II, VITA; Empress CAD, Ivoclar-Vivadent) and glass-ceramics (e.max CAD, Ivoclar-Vivadent; Suprinity, VITA; Celtra Duo, Dentsply) to hybrid materials (Enamic, VITA; Lava Ultimate, 3M ESPE) have been selected. Specimens were prepared with highly polished surfaces in rectangular plate (12×12×1.2mm 3 ) or round disc (Ø=12mm, thickness=1.2mm) geometries. Specimens were tested using the B3B assembly and the biaxial strength was determined using calculations derived from finite element analyses of the respective stress fields. Size effects on strength were determined based on results from 4-point-bending specimens. A good agreement was found between the biaxial strength results for the different geometries (plates vs. discs) using the B3B test. Strength values ranged from 110.9MPa (Vitablocs Mark II) to 1303.21MPa (e.max ZirCAD). The strength dependency on specimen size was demonstrated through the calculated effective volume/surface. The B3B test has shown to be a reliable and simple method for determining the biaxial strength restorative materials supplied as small CAD/CAM blocks. A flexible solution was made available for the B3B test in the rectangular plate geometry. Copyright © 2016 The Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Improved consolidation of silicon carbide

NASA Technical Reports Server (NTRS)

Freedman, M. R.; Millard, M. L.

1986-01-01

Alpha silicon carbide powder was consolidated by both dry and wet methods. Dry pressing in a double acting steel die yielded sintered test bars with an average flexural strength of 235.6 MPa with a critical flaw size of approximately 100 micro m. An aqueous slurry pressing technique produced sintered test bars with an average flexural strength of 440.8 MPa with a critical flaw size of approximately 25 micro m. Image analysis revealed a reduction in both pore area and pore size distribution in the slurry pressed sintered test bars. The improvements in the slurry pressed material properties are discussed in terms of reduced agglomeration and improved particle packing during consolidation.

Internal geometry effect of structured PLA materials manufactured by dropplet-based 3D printer on its mechanical properties

NASA Astrophysics Data System (ADS)

Wicaksono, Sigit T.; Ardhyananta, Hosta; Rasyida, Amaliya; Hidayat, Mas Irfan P.

2018-04-01

Rapid Prototyping (RP) technologies, the manufacturing technology with less time consuming including high precission and complicated structure of products, are now become high demanding technologies. Those technologies can be base on top-down or bottom-up approaches. One of the bottom-up approach of RP technology is 3D printing machine. In this research, we have succeed to apply the droplet-based 3D printer to make the structured PLA (Polylactic Acid) materials with different internal geometry structures. The internal geometry used are triangle and honeycomb structure with different size of each symmetry axis of 4.5 mm and 9 mm and the thickness varied of 1 mm and 2 mm as well. The mechanical properties of those structures including tensile and bending stregth are evaluated by using tensile and flexural test respectively. Test results show that the best performance obtained by measuring its tensile and flexural strength is the sampel with triangle geometry of 9 mm geometrical size and 2 mm of thickness. The tensile strength and flexural strength values of the specimens are 59.2996 MPa and 123 MPa respectively.

Mechanical Characterization of Composites and Foams for Aerospace Applications

NASA Technical Reports Server (NTRS)

Veazie, D. R.; Glinsey, C.; Webb, M. M.; Norman, M.; Meador, Michael A. (Technical Monitor)

2000-01-01

Experimental studies to investigate the mechanical properties of ultra-lightweight polyimide foams for space applications, compression after impact (CAI) properties for low velocity impact of sandwich composites, and aspen fiber/polypropylene composites containing an interface adhesive additive, Maleic Anhydride Grafted Polypropylene (MAPP), were performed at Clark Atlanta University. Tensile, compression, flexural, and shear modulus tests were performed on TEEK foams categorized by their densities and relative cost according to ASTM specifications. Results showed that the mechanical properties of the foams increased as a function of higher price and increasing density. The CAI properties of Nomex/phenolic honeycomb core, fiberglass/epoxy facesheet sandwich composites for two damage arrangements were compared using different levels of impact energy ranging from 0 - 452 Joules. Impact on the thin side showed slightly more retention of CAI strength at low impact levels, whereas higher residual compressive strength was observed from impact on the thick side at higher impact levels. The aspen fiber/polypropylene composites studied are composed of various percentages (by weight) of aspen fiber and polypropylene ranging from 30%-60% and 40%-100%, respectively. Results showed that the MAPP increases tensile and flexural strength, while having no significant influence on tensile and flexural modulus.

Monoclinic phase transformation and mechanical durability of zirconia ceramic after fatigue and autoclave aging.

PubMed

Mota, Yasmine A; Cotes, Caroline; Carvalho, Rodrigo F; Machado, João P B; Leite, Fabíola P P; Souza, Rodrigo O A; Özcan, Mutlu

2017-10-01

This study evaluated the influence of two aging procedures on the biaxial flexural strength of yttria-stabilized tetragonal zirconia ceramics. Disc-shaped zirconia specimens and (ZE: E.max ZirCAD, Ivoclar; ZT: Zirkon Translucent, Zirkonzahn) (N = 80) (∅:12 mm; thickness:1.2 mm, ISO 6872) were prepared and randomly divided into four groups (n = 10 per group) according to the aging procedures: C: Control, no aging; M: mechanical cycling (2 × 10 6 cycles/3.8 Hz/200 N); AUT: Aging in autoclave at 134°C, 2 bar for 24 h; AUT + M: Autoclave aging followed by mechanical cycling. After aging, the transformed monoclinic zirconia (%) were evaluated using X-ray diffraction and surface roughness was measured using atomic force microscopy. The average grain size was measured by scanning electron microscopy and the specimens were submitted to biaxial flexural strength testing (1 mm/min, 1000 kgf in water). Data (MPa) were statistically analyzed using 2-way analysis of variance and Tukey's test (α = 0.05). Aging procedures significantly affected (p = 0.000) the flexural strength data but the effect of zirconia type was not significant (p = 0.657). AUT ZT (936.4 ± 120.9 b ) and AUT + M ZE (867.2 ± 49.3 b ) groups presented significantly higher values (p < 0.05) of flexural strength than those of the control groups (C ZT : 716.5 ± 185.7 a ; C ZE : 779.9 ± 114 a ) (Tukey's test). The monoclinic phase percentage (%) was higher for AUT ZE (71), AUT ZT (66), AUT + M ZE (71), and AUT + M ZM (66) compared to the C groups (ZE:0; ZT:0). Surface roughness (µm) was higher for AUT ZE (0.09), AUT ZT (0.08), AUT + M ZE (0.09 µm), and AUT + M ZT (0.09 µm) than those of other groups. Regardless of the zirconia type, autoclave aging alone or with mechanical aging increased the flexure strength but also induced higher transformation from tetragonal to monoclinic phase in both zirconia materials tested. © 2016 Wiley Periodicals, Inc. J Biomed Mater Res Part B: Appl Biomater, 105B: 1972-1977, 2017. © 2016 Wiley Periodicals, Inc.

Air-particle abrasion on zirconia ceramic using different protocols: effects on biaxial flexural strength after cyclic loading, phase transformation and surface topography.

PubMed

Souza, Rodrigo O A; Valandro, Luiz F; Melo, Renata M; Machado, João P B; Bottino, Marco A; Ozcan, Mutlu

2013-10-01

This study evaluated the effect of different air-particle abrasion protocols on the biaxial flexural strength and structural stability of zirconia ceramics. Zirconia ceramic specimens (ISO 6872) (Lava, 3M ESPE) were obtained (N=336). The specimens (N=118, n=20 per group) were randomly assigned to one of the air-abrasion protocols: Gr1: Control (as-sintered); Gr2: 50 µm Al2O3 (2.5 bar); Gr3: 50 µm Al2O3 (3.5 bar); Gr4: 110 µm Al2O3(2.5 bar); Gr5: 110 µm Al2O3 (3.5 bar); Gr6: 30 µm SiO2 (2.5 bar) (CoJet); Gr7: 30 µm SiO2(3.5 bar); Gr8: 110 µm SiO2 (2.5 bar) (Rocatec Plus); and Gr9: 110 µm SiO2 (3.5 bar) (duration: 20 s, distance: 10 mm). While half of the specimens were tested immediately, the other half was subjected to cyclic loading in water (100,000 cycles; 50 N, 4 Hz, 37 °°C) prior to biaxial flexural strength test (ISO 6872). Phase transformation (t→m), relative amount of transformed monoclinic zirconia (FM), transformed zone depth (TZD) and surface roughness were measured. Particle type (p=0.2746), pressure (p=0.5084) and cyclic loading (p=0.1610) did not influence the flexural strength. Except for the air-abraded group with 110 µm Al2O3 at 3.5 bar, all air-abrasion protocols increased the biaxial flexural strength (MPa) (Controlnon-aged: 1,030 ± 153, Controlaged: 1,138 ± 138; Experimentalnon-aged: 1,307 ± 184-1,554 ± 124; Experimentalaged: 1,308 ± 118-1,451 ± 135) in both non-aged and aged conditions, respectively. Surface roughness (Ra) was the highest with 110 µm Al2O3(0.84 µm. FM values ranged from 0% to 27.21%, higher value for the Rocatec Plus (110 µm SiO2) and 110 µm Al2O3 groups at 3.5 bar pressure. TZD ranged between 0 and 1.43 µm, with the highest values for Rocatec Plus and 110 µm Al2O3 groups at 3.5 bar pressure. Copyright © 2013 Elsevier Ltd. All rights reserved.

[Effect of three kinds of rare earth oxides on chromaticity and mechanical properties of zirconia ceramic].

PubMed

Huang, Hui; Zhang, Fu-qiang; Sun, Jing; Gao, Lian

2006-06-01

To evaluate the colouration of zirconia ceramic by adding three kinds of rare earth oxides. The influence of the pigments concentration on the mechanical properties and the microstructure was also analyzed. Added different concentrations of CeO(2), Er(2)O(3) and Pr(6)O(11) in tetragonal zirconia poly crystals stabilized with 3 mol% yttria (3Y-T2P) powder, compacted at 200 MPa using cold isostatic pressure, and sintered to 1 400 degrees C. The heating rate was 150 degrees C/h and the dwelling time was 2 hours. The chromaticity of sintered bodies was measured with chroma meter. The relative density, hardness, flexure strength and fracture toughness were investigated as well. The phase stability of the colorized and pure zirconia was evaluated by X-ray diffraction (XRD) using an automated diffractometer. The microstructures of the specimens were evaluated by scanning electron microscope (SEM). Several kinds of color achieved by the different pigments praseodym oxide, cerium oxide and erbium oxide were presented in the CIELab system. The a* value increased with the added amount of Er(2)O(3), while b* value rose with the increasing amount of CeO(2) and Pr(6)O(11). However, three pigments failed to decrease L* value and the sintered body appeared too bright. Adding three pigments influenced flexure strength of zirconia ceramic significantly, but had little influence on the hardness and fracture toughness. Microscopy revealed the relationship between the porosity and shapes of grains was correlated to strength of the diphase ceramics. No additional phase could be detected by XRD, except t-ZrO(2) in all colorized samples after sintering at 1 400 degrees C for 120 min. Zirconia ceramic can be colorized by CeO(2), Er(2)O(3), and Pr(6)O(11). Pigments even in a small amount influence the mechanical properties of the colorized zirconia material, which necessitates further investigation.

Effect of High Energy Radiation on Mechanical Properties of Graphite Fiber Reinforced Composites. M.S. Thesis

NASA Technical Reports Server (NTRS)

Naranong, N.

1980-01-01

The flexural strength and average modulus of graphite fiber reinforced composites were tested before and after exposure to 0.5 Mev electron radiation and 1.33 Mev gamma radiation by using a three point bending test (ASTM D-790). The irradiation was conducted on vacuum treated samples. Graphite fiber/epoxy (T300/5208), graphite fiber/polyimide (C6000/PMR 15) and graphite fiber/polysulfone (C6000/P1700) composites after being irradiated with 0.5 Mev electron radiation in vacuum up to 5000 Mrad, show increases in stress and modulus of approximately 12% compared with the controls. Graphite fiber/epoxy (T300/5208 and AS/3501-6), after being irradiated with 1.33 Mev gamma radiation up to 360 Mrads, show increases in stress and modulus of approximately 6% at 167 Mrad compared with the controls. Results suggest that the graphite fiber composites studied should withstand the high energy radiation in a space environment for a considerable time, e.g., over 30 years.

Flexural behavior of the fibrous cementitious composites (FCC) containing hybrid fibres

NASA Astrophysics Data System (ADS)

Ramli, Mahyuddin; Ban, Cheah Chee; Samsudin, Muhamad Fadli

2018-02-01

In this study, the flexural behavior of the fibrous cementitious composites containing hybrid fibers was investigated. Waste materials or by product materials such as pulverized fuel ash (PFA) and ground granulated blast-furnace slag (GGBS) was used as supplementary cement replacement. In addition, barchip and kenaf fiber will be used as additional materials for enhance the flexural behavior of cementitious composites. A seven mix design of fibrous cementitious composites containing hybrid fiber mortar were fabricated with PFA-GGBS as cement replacement at 50% with hybridization of barchip and kenaf fiber between 0.5% and 2.0% by total volume weight. The FCC with hybrid fibers mortar will be fabricated by using 50 × 50 × 50 mm, 40 × 40 × 160 mm and 350 × 125 × 30 mm steel mold for assessment of mechanical performances and flexural behavior characteristics. The flexural behavior and mechanical performance of the PFA-GGBS with hybrid fiber mortar block was assessed in terms of load deflection response, stress-strain response, crack development, compressive and flexural strength after water curing for 28 days. Moreover, the specimen HBK 1 and HBK 2 was observed equivalent or better in mechanical performance and flexural behavior as compared to control mortar.